TY - CONF A1 - Simbruner, Kai T1 - Brittle failure analysis of spent fuel zirconium alloy claddings during long-term dry interim storage - Current approach at BAM N2 - Understanding the mechanical behaviour of fuel cladding is decisive for an extended dry interim storage period beyond the currently licensed period of 40 years in Germany and subsequent handling, transport, and disposal considering normal and accidental conditions. Since fuel cladding acts as the first barrier for spent fuel, its integrity should be demonstrated to enable safe and secure discharge and handling options after interim storage and subsequent transportation in preparation of final disposal. An established method for characterizing cladding material is the Ring Compression Test (RCT), where a small, cylindrical sample of the cladding tube is subjected to a compressive load. This test is a laboratory representation of a fuel rod load case and has shown a high susceptibility to failure under the occurrence of radial hydrides. Certain hydride morphologies and low temperature might even lead to brittle fracture at very small loads. The BAM research project BRUZL (Fracture mechanical analysis of spent fuel claddings during long-term dry interim storage) aims to study the results of quasi-static RCTs and to establish numerical models to gain an in-depth understanding of the stress state during the experiments. Using a fracture mechanical approach, cases of sudden failure during the RCT procedure are used to characterize the material behaviour and establish a failure criterion. As an integral part of the project BRUZL, quasi-static Ring Compression Tests have been performed to identify all experimental details, which might be helpful for numerical modelling. Unirradiated samples of the cladding material ZIRLO® have been subjected to hydrogen charging and a thermo-mechanical treatment for radial hydride reorientation. Sample preparation, testing procedures, and analysis results are presented. A numerical model has been established and an elastic-plastic material model was derived from as-received RCT samples by inverse finite element analyses. Cohesive zone modelling has been implemented to reproduce sudden load drops during RCT. The project is funded by the Federal Ministry for Economic Affairs and Energy (BMWi) under contract no. 1501561. T2 - Kolloquium der Abteilung 3 CY - Online meeting DA - 05.11.2020 KW - Ageing Management KW - Cladding Embrittlement KW - Extended Storage KW - Ring Compression Test KW - Spent Nuclear Fuel PY - 2020 AN - OPUS4-51987 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simbruner, Kai T1 - Embrittlement of Spent Fuel Claddings ‒ Results of Ring Compression Tests N2 - An established method for characterizing cladding material is the Ring Compression Test (RCT), where a small, cylindrical sample of the cladding tube is subjected to a compressive load. This test is a laboratory representation of a fuel rod load case and has shown a high susceptibility to failure under the occurrence of radial hydrides. Certain hydride morphologies and low temperature might even lead to brittle fracture at very small loads. The BAM research project BRUZL (Fracture mechanical analysis of spent fuel claddings during long-term dry interim storage) aims to study the results of quasi-static RCTs and to establish numerical models to gain an in-depth understanding of the stress state during such experiments. Using a fracture mechanical approach, cases of sudden failure during the RCT procedure are used to characterize the material behaviour and establish a failure criterion. As an integral part of the project BRUZL, quasi-static Ring Compression Tests have been performed to identify all experimental details, which might be helpful for numerical modelling. Unirradiated samples of the cladding material ZIRLO® have been subjected to hydrogen charging and a thermo-mechanical treatment for radial hydride reorientation. Sample preparation, testing procedures, and analysis results are presented. A numerical model has been established and an elastic-plastic material model was derived from as-received RCT samples by inverse finite element analyses. Cohesive zone modelling has been implemented to reproduce sudden load drops during RCT. The project is funded by the Federal Ministry for Economic Affairs and Energy (BMWi) under contract no. 1501561. T2 - 4th GRS Workshop on Safety of Extended Dry Storage of Spent Nuclear Fuel CY - Online meeting DA - 03.06.2020 KW - Ageing Management KW - Cladding Embrittlement KW - Extended Storage KW - Ring Compression Test KW - Spent Nuclear Fuel PY - 2020 AN - OPUS4-51988 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simbruner, Kai T1 - Embrittlement of Spent Fuel Claddings – Fracture Mechanical Evaluation and Failure Criteria N2 - The BAM research project BRUZL (Fracture mechanical analysis of spent fuel claddings during long-term dry interim storage) evaluates results of quasi-static Ring Compression Tests (RCT). Due to its simple realisation, the RCT is an established method for characterising the mechanical behaviour of fuel cladding, where a small tube sample is subjected to a compressive load and the relation between load and displacement is obtained. During tests at room temperature, unirradiated ZIRLO® samples with a distinct extend of radial hydrides have shown high susceptibility to sudden, brittle failure at relatively small loads. Hydride morphology and radial hydride metrics have been an integral part of the characterisation of degradation mechanisms of cladding. A software tool for the analysation of metallographic micrographs was developed. The program allows the automated calculation of hydride lengths, detection of continuous hydride structures, their statistical evaluation and visualisation. Numerical models have been established to reproduce experimental RCT results featuring an elastic-plastic material model, which was derived from inverse finite element analyses of as-received RCT samples. A cohesive zone model (CZM) is introduced to the model to reproduce load drops in the linear regime of the load vs. displacement curve. Using a traction-separation approach for the CZM, the cohesive parameters are fitted to match numerical and experimental results yielding the fracture mechanical material properties. Combining the three key aspects hydride morphology, fracture mechanics and RCT stress-state a failure criterion can be established as a result of the BRUZL project. The project is funded by the Federal Ministry for Economic Affairs and Energy (BMWi) under contract no. 1501561. T2 - 5th GRS Workshop on Safety of Extended Dry Storage of Spent Nuclear Fuel CY - Online meeting DA - 09.06.2021 KW - Ageing Management KW - Cladding Embrittlement KW - Extended Storage KW - Ring Compression Test KW - Spent Nuclear Fuel PY - 2021 AN - OPUS4-53779 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simbruner, Kai T1 - Embrittlement of Spent Fuel Claddings - Micromechanically Motivated Cohesive Zone Modelling N2 - Since cladding acts as the first barrier for nuclear fuel, it is key to understand the degrading mechanisms leading to cladding embrittlement. Zirconium alloy based cladding samples subjected to simulated pre-storage drying conditions have shown high susceptibility to brittle failure under the occurrence of hoop stress and low temperature as expected after long-term interim storage. The stress state associated with a compressive pinch-load scenario is reproduced by the Ring Compression Test (RCT), which results in sudden failure at relatively small mechanical loads with high sensitivity to the presence of radial hydrides. As part of the BAM research project BRUZL (Fracture mechanics analysis of spent fuel claddings during long-term dry interim storage), static RCTs were conducted on non-irradiated, pre-hydrided ZIRLO® ring-shaped samples that were subjected to a radial hydride treatment. All samples failed in macroscopically brittle fashion with sudden load drops and severe crack propagation through almost the entire wall thickness. In a post-RCT examination of the fracture surfaces using scanning electron microscopy, radial hydrides could be identified as the weakest link of the structure. However, the microscopic failure mechanism is much more complex due to cracks initiating at different axial positions in depth direction of the ring, overlapping cracks, and arresting cracks. A considerable portion of the fracture surfaces appeared to have undergone plastic deformation of the zirconium matrix resulting in void growth and coalescence associated with ductile failure. The geometry of the ductile patches was measured, and the ductile surface fraction was determined. Based on these observations, a statistical model was developed that can reproduce the composition of the fracture surface as a one-dimensional projection. A micromechanically motivated cohesive zone model (CZM) was implemented in existing RCT finite element analysis (FEA) models with different constitutive laws for brittle hydrides and ductile matrix respectively. In this work, FEA results are presented for non-irradiated ZIRLO® and high-burnup M5® claddings. The impact of varying hydride-matrix combinations is discussed. Acknowledgement: The project was funded by the former Federal Ministry for Economic Affairs and Energy (BMWi) under contract no. 1501561. T2 - 6th GRS Workshop on the Safety of Extended Dry Storage of Used Nuclear Fuel CY - Garching, Germany DA - 01.06.2022 KW - Ageing Management KW - Cladding Embrittlement KW - Extended Storage KW - Ring Compression Test KW - Spent Nuclear Fuel PY - 2022 AN - OPUS4-55023 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simbruner, Kai T1 - Brittle Failure Analysis of High-Burnup PWR Fuel Cladding Alloys N2 - The general aim of this research is the development of methods for predicting mechanical behavior and identification of limiting conditions to prevent brittle failure of high-burnup (HBU) pressure water reactor (PWR) fuel cladding alloys. A finite element (FE) model of the ring compression test (RCT) was created to analyze the failure behavior of zirconium-based alloys with radial hydrides during the RCT. An elastic-plastic material model describes the zirconium alloy. The stress-strain curve needed for the elastic-plastic material model was derived by inverse finite element analyses. Cohesive zone modeling is used to reproduce sudden load drops during RCT loading. Based on the failure mechanism in non-irradiated ZIRLO® claddings, a micro-mechanical model was developed that distinguishes between brittle failure along hydrides and ductile failure of the zirconium matrix. Two different cohesive laws representing these types of failure are present in the same cohesive interface. The key differences between these constitutive laws are the cohesive strength, the stress at which damage initiates, and the cohesive energy, which is the damage energy dissipated by the cohesive zone. Statistically generated matrix-hydride distributions were mapped onto the cohesive elements and simulations with focus on the first load drop were performed. Computational results are in good agreement with the RCT results conducted on high-burnup M5® samples. It could be shown that crack initiation and propagation strongly depend on the specific configuration of hydrides and matrix material in the fracture area. T2 - 26th International Conference on Structural Mechanics in Reactor Technology - SMiRT 26 CY - Potsdam, Germany DA - 10.07.2022 KW - Cladding Embrittlement KW - Ring Compression Test KW - Cohesive Zone Modelling KW - Spent Nuclear Fuel PY - 2022 AN - OPUS4-55435 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gaddampally, Mohan Reddy T1 - Failure Analysis on Irradiated Claddings Subjected to Long-Term Dry Interim Storage N2 - Long-term dry interim storage may adversely affect the mechanical properties of spent fuel rods, possibly resulting in a reduced resilience during handling or transport after storage. Since the cladding is the first barrier for the spent fuel pellets, its integrity must be demonstrated until the end of interim storage and subsequent transportation. An established method for characterizing the cladding material is the ring compression test, in which a small, cylindrical sample of the cladding tube is subjected to a compressive load. This test is a laboratory representation of a load case where the fuel rod is crushed. Pre-storage drying and the early stage of interim storage can subject the cladding to higher temperatures and higher pressure induced tensile hoop stresses than those associated with in-reactor operation and pool storage. Under these conditions, radial hydrides may precipitate in zirconium-based alloys (Zircaloy) during slow cooling, which result in embrittlement of the cladding material and eventually a possible sudden failure of cladding integrity under additional mechanical loads. Especially long, continuous radial hydride structures and low temperature can cause severe embrittlement of claddings and finally failure by fracture even at small deformations. Therefore, the study of hydride morphology plays an important role in describing the brittle failure behaviour of the claddings. The focus of the presented research is on the development of appropriate numerical methods for predicting the mechanical behaviour and identification of limiting conditions to prevent brittle fracture of Zircaloy claddings. Typical hydride morphologies are shown. An iterative inverse analysis method is described for deriving the elastic-plastic material properties in the hoop direction of a ring-shaped sample. A modelling approach based on cohesive zones is explained which is able to reproduce the propagation of cracks initiated at radial hydrides in the zirconium matrix. The developed methods are applied to defueled samples of cladding alloy ZIRLO®, which were subjected to a thermo-mechanical treatment to reorient existing circumferential hydrides to radial hydrides. A selected sample showing sudden load drops during a quasi-static ring compression test is analysed by means of fracture mechanics for illustrative purposes. This project as part of the European Joint Programme on Radioactive Waste Management has received funding from the European Union’s Horizon 2020 research and innovation programme under grant agreement no. 847593. T2 - BAM-Kolloquium der Abteilung 3 CY - Berlin, Germany DA - 05.06.2023 KW - Cladding Embrittlement KW - Cohesive Zone Modelling KW - Ring Compression Test KW - Spent Nuclear Fuel PY - 2023 AN - OPUS4-57598 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gaddampally, Mohan Reddy T1 - Cohesive Zone Modelling Approach on Irradiated Claddings Subjected to Long-Term Dry Interim Storage N2 - Long-term dry interim storage may adversely affect the mechanical properties of spent fuel rods, possibly resulting in a reduced resilience during handling or transport after storage. Pre-storage drying and the early stage of interim storage can subject the cladding to higher temperatures and higher pressure induced tensile hoop stresses than those associated with in-reactor operation and pool storage. Under these conditions, radial hydrides may precipitate in zirconium-based alloys (Zircaloy) during slow cooling, which may result in embrittlement of the cladding material and eventually a sudden failure of cladding under additional mechanical loads. Especially long, continuous radial hydride structures and low temperature can cause severe embrittlement of claddings and finally failure by fracture even at small deformations. The focus of the presented research is on the development of appropriate numerical methods for predicting the mechanical behaviour and identification of limiting conditions to prevent brittle fracture of Zircaloy claddings. An iterative inverse analysis method is used for deriving the elastic-plastic material properties in the hoop direction of a ring-shaped sample. A modelling approach based on cohesive zones is explained which can reproduce the propagation of cracks initiated at radial hydrides in the zirconium matrix. The developed methods are applied to defueled samples of cladding alloy ZIRLO®, which were subjected to a thermo-mechanical treatment to reorient existing circumferential hydrides to radial hydrides. A selected sample showing sudden load drops during a quasi-static ring compression test is analysed by means of fracture mechanics for illustrative purposes. T2 - 7th GRS Workshop on the Safety of Extended Dry Storage of Spent Nuclear Fuel CY - Garching, Germany DA - 24.05.2023 KW - Ageing Management KW - Cladding Embrittlement KW - Extended Storage KW - Ring Compression Test KW - Spent Nuclear Fuel PY - 2023 AN - OPUS4-58553 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Zencker, Uwe A1 - Aguado, Carlos A1 - Arkoma, Asko A1 - Bertsch, Johannes A1 - Cristóbal Beneyto, Miguel A1 - Feria Marquez, Francisco A1 - Herranz, Luis Enrique A1 - Ivanov, Ivan A1 - Király, Márton A1 - Nasyrow, Ramil A1 - Papaioannou, Dimitrios A1 - Ruiz-Hervias, Jesus A1 - Vlassopoulos, Efstathios T1 - Thermo-mechanical-chemical properties of unirradiated and irradiated samples of spent nuclear fuel rod segments and cladding N2 - The report addresses the experimental characterisation, thermo-mechanical modelling and performance of unirradiated and irradiated samples of spent nuclear fuel rod segments and cladding. Hydrogen is relocated in nuclear fuel claddings by diffusion along temperature, stress, and concentration gradients, and towards a liner if existent. The precipitation of hydrides during cool-down at the beginning of the storage is influenced by mechanical stress. A strong accumulation of hydrides and a disadvantageous hydride alignment in relation to the stress state can affect the mechanical properties and compromise the fuel cladding integrity. Neutron radiography is used to determine spatially resolved hydrogen and hydride distributions in claddings. A liner in duplex claddings attracts hydrogen, which will then no longer be available to form detrimental hydrides in the bulk part of the cladding. Individual three-point bending and gravitational impact tests on filled pressurised spent nuclear fuel rod segments were conducted in hot-cell facilities. The material behaviour under three-point bending in the presence of hydrides and at different temperatures was systematically investigated in quasi-static laboratory tests on unirradiated rod segments with and without surrogate pellets until rupture. Ring compression tests were carried out on irradiated and unirradiated samples at different temperatures and both with and without radial hydrides. With radial hydrides, brittle failure is possible even at low deformation and simultaneously low temperature. Crack initiation will occur on the radial hydride with the highest fracture mechanics load, which depends on the hydride size in the regions with the highest hoop stresses. Due to the high hydrogen content used in creep tests conducted, precipitation hardening of the hydrides in the zirconium alloy significantly reduces the creep rate, as it strengthens the material and inhibits the dislocation sliding. The use of finite element analyses on mechanical tests to determine the cladding properties using a numerical optimisation method based on a large number of automatically generated sensitivity calculations is demonstrated. The brittle fracture of cladding samples with radial hydrides in the ring compression test can be described with a cohesive zone model if the cohesive parameters are selected appropriately and the hydride morphology is specified. Progress was made in the verification, validation and enhancement of spent fuel performance codes by the compilation of a representative validation database (related to rod internal pressure, fission gas release, rod void volume, and in-clad hydrogen distribution), the enhancement of CIEMAT’s FRAPCON-xt code for rod internal pressure prediction at high burnup, the enhancement of CIEMAT’s in-clad hydrogen performance subroutine HYDCLAD with more phenomenological modelling, the extension of INL’s BISON code with a cladding creep law for dry storage, and a benchmark with FRAPCON-xt and BISON simulating in-reactor and dry storage scenarios. KW - Spent Nuclear Fuel KW - Cladding KW - Experimental Characterisation KW - Modelling KW - Fuel Performance Code PY - 2024 SP - 1 EP - 102 PB - European Joint Programme EURAD AN - OPUS4-61008 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Völzke, Holger T1 - Brittle Failure Limits of Spent Fuel Claddings Subjected to Long-Term Dry Interim Storage Conditions N2 - The mechanical properties of spent fuel claddings can be adversely affected under the conditions of long-term dry interim storage, so that the failure limits may be reached in case of mechanical loads during handling or transport after storage. Pre-storage drying and the early stage of interim storage can expose the cladding to higher temperatures and higher tensile hoop stresses than those associated with in-reactor operation and pool storage. During slow cooling of a cladding tube under internal pressure, radial hydrides may precipitate in zirconium-based cladding alloys. This can lead to embrittlement of the material and sudden failure of the cladding integrity under mechanical stress. In order to prevent brittle failure, numerical methods are being developed to predict the mechanical behaviour and identify limiting conditions. Experimental investigations, numerical analyses and evaluation methods are discussed. An established experimental method for characterising cladding materials is the Ring Compression Test (RCT). Some test results on irradiated cladding tubes after operation in pressure water reactors are publicly available. However, it is helpful to carry out studies on unirradiated surrogate claddings with similar material properties to reduce the effort associated with irradiated samples in hot cells and to perform material tests with a wider range of parameters. On the basis of such experimental data, load-displacement curves have been numerically analysed for a selection of cladding materials. Radial hydrides can cause a sample to break suddenly due to fracture even at low deformation. Noticeable load drops in the RCT are caused by unstable crack propagation through the radial hydride network. The failure mechanism is quasi-cleavage in the hydrides and micro-void nucleation, growth, and coalescence in the zirconium matrix, with ductile tearing patches connecting adjacent hydrides. The cohesive zone approach was used to simulate the failure process taking into account the radial hydride morphology. The developed method can adequately describe both the deformation and failure behaviour of irradiated as well as unirradiated claddings of zirconium-based alloys with radial hydrides under RCT conditions. Limiting conditions can be expressed in terms of fracture energy and cohesive strength. T2 - IAEA International Conference on the Management of Spent Fuel from Nuclear Power Plants - Meeting the Moment CY - Vienna, Austria DA - 10.06.2024 KW - Ageing Management KW - Cladding Embrittlement KW - Extended Storage KW - Ring Compression Test KW - Spent Nuclear Fuel PY - 2024 SP - 1 EP - 10 AN - OPUS4-60323 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe T1 - Brittle Failure Limits of Spent Fuel Claddings Subjected to Long-Term Dry Interim Storage Conditions N2 - The mechanical properties of spent fuel claddings can be adversely affected under the conditions of long-term dry interim storage, so that the failure limits may be reached in case of mechanical loads during handling or transport after storage. Pre-storage drying and the early stage of interim storage can expose the cladding to higher temperatures and higher tensile hoop stresses than those associated with in-reactor operation and pool storage. During slow cooling of a cladding tube under internal pressure, radial hydrides may precipitate in zirconium-based cladding alloys. This can lead to embrittlement of the material and sudden failure of the cladding integrity under mechanical stress. In order to prevent brittle failure, numerical methods are being developed to predict the mechanical behaviour and identify limiting conditions. Experimental investigations, numerical analyses and evaluation methods are discussed. An established experimental method for characterising cladding materials is the Ring Compression Test (RCT). Some test results on irradiated cladding tubes after operation in pressure water reactors are publicly available. However, it is helpful to carry out studies on unirradiated surrogate claddings with similar material properties to reduce the effort associated with irradiated samples in hot cells and to perform material tests with a wider range of parameters. On the basis of such experimental data, load-displacement curves have been numerically analysed for a selection of cladding materials. Radial hydrides can cause a sample to break suddenly due to fracture even at low deformation. Noticeable load drops in the RCT are caused by unstable crack propagation through the radial hydride network. The failure mechanism is quasi-cleavage in the hydrides and micro-void nucleation, growth, and coalescence in the zirconium matrix, with ductile tearing patches connecting adjacent hydrides. The cohesive zone approach was used to simulate the failure process taking into account the radial hydride morphology. The developed method can adequately describe both the deformation and failure behaviour of irradiated as well as unirradiated claddings of zirconium-based alloys with radial hydrides under RCT conditions. Limiting conditions can be expressed in terms of fracture energy and cohesive strength. T2 - IAEA International Conference on the Management of Spent Fuel from Nuclear Power Plants - Meeting the Moment CY - Vienna, Austria DA - 10.06.2024 KW - Ageing Management KW - Cladding Embrittlement KW - Extended Storage KW - Ring Compression Test KW - Spent Nuclear Fuel PY - 2024 AN - OPUS4-60324 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Gaddampally, Mohan Reddy A1 - Völzke, Holger T1 - Failure Analysis on Irradiated Claddings Subjected to Long-Term Dry Interim Storage N2 - Long-term dry interim storage may adversely affect the mechanical properties of spent fuel rods, possibly resulting in a reduced resilience during handling or transport after storage. The cladding is the first barrier for the spent fuel pellets. An established method for characterising the cladding material is the ring compression test (RCT), in which a small, cylindrical sample of the cladding tube is subjected to a compressive load. Radial hydrides may precipitate in zirconium-based alloys (Zircaloy) under pre-storage drying and during slow cooling, which result in embrittlement of the cladding material and eventually a possible sudden failure of cladding integrity under additional mechanical loads. The focus of the presented research is on the development of appropriate nu-merical methods for predicting the mechanical behaviour and identification of limiting conditions to prevent brittle fracture of Zircaloy claddings. A modelling approach based on cohesive zones is ex-plained which is able to reproduce the propagation of cracks initiated at radial hydrides in the zir-conium matrix. The developed methods are applied to defueled samples of cladding alloy ZIRLO®, which were subjected to a thermo-mechanical treatment to reorient existing circumferential hy-drides to radial hydrides. A selected sample showing sudden load drops during a quasi-static ring compression test is analysed by means of fracture mechanics for illustrative purposes. Based on the developed fracture mechanics approach, not only the deformation behaviour but also the fail-ure behaviour of irradiated as well as unirradiated Zircaloy claddings with radial hydrides under RCT loading conditions can be adequately described. T2 - 27th International Conference on Structural Mechanics in Reactor Technology - SMiRT 27 CY - Yokohama, Japan DA - 03.03.2024 KW - Cladding Embrittlement KW - Cohesive Zone Modelling KW - Ring Compression Test KW - Spent Nuclear Fuel PY - 2024 SP - 1 EP - 8 AN - OPUS4-60671 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe T1 - Failure Analysis on Irradiated Claddings Subjected to Long-Term Dry Interim Storage N2 - Long-term dry interim storage may adversely affect the mechanical properties of spent fuel rods, possibly resulting in a reduced resilience during handling or transport after storage. The cladding is the first barrier for the spent fuel pellets. An established method for characterising the cladding material is the ring compression test (RCT), in which a small, cylindrical sample of the cladding tube is subjected to a compressive load. Radial hydrides may precipitate in zirconium-based alloys (Zircaloy) under pre-storage drying and during slow cooling, which result in embrittlement of the cladding material and eventually a possible sudden failure of cladding integrity under additional mechanical loads. The focus of the presented research is on the development of appropriate nu-merical methods for predicting the mechanical behaviour and identification of limiting conditions to prevent brittle fracture of Zircaloy claddings. A modelling approach based on cohesive zones is ex-plained which is able to reproduce the propagation of cracks initiated at radial hydrides in the zir-conium matrix. The developed methods are applied to defueled samples of cladding alloy ZIRLO®, which were subjected to a thermo-mechanical treatment to reorient existing circumferential hy-drides to radial hydrides. A selected sample showing sudden load drops during a quasi-static ring compression test is analysed by means of fracture mechanics for illustrative purposes. Based on the developed fracture mechanics approach, not only the deformation behaviour but also the fail-ure behaviour of irradiated as well as unirradiated Zircaloy claddings with radial hydrides under RCT loading conditions can be adequately described. T2 - 27th International Conference on Structural Mechanics in Reactor Technology - SMiRT 27 CY - Yokohama, Japan DA - 03.03.2024 KW - Cladding Embrittlement KW - Cohesive Zone Modelling KW - Ring Compression Test KW - Spent Nuclear Fuel PY - 2024 AN - OPUS4-60672 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -