TY - CONF A1 - Nerger, Deborah A1 - Moosavi, Robabeh A1 - Bracklow, F. A1 - Hering, M. A1 - Kühn, T. A1 - Curbach, M. A1 - Hille, Falk A1 - Rogge, Andreas ED - Papadrakakis, M. ED - Fragiadakis, M. ED - Papadimitriou, C. T1 - Impact damage characterization at RC plates with planar tomography and FEM N2 - Prediction of dynamic effects of reinforced concrete structures under impact loading is a technical challenge. This is a consequence of the great variability of the physical properties resulting from the wide adaptability of reinforced concrete and a consequence of the wide range of impact loading. Experiments and numerical investigations are normally used on a small scale to address the problem. In this paper, impact tests on reinforced conrete plates with the lateral dimensions of 1.5 m x 1.5 m and a thickness of 30 cm are presented. In bending reinforcement, besides the velocity two properties are varied, the diameter and the spatial distribution of the rebars. Experiments are performed at the Otto-Mohr-Laboratory of the Institute of Concrete Structures of the Technische Universit¨at Dresden. Due to the accelerated fall of the impactor the velocity ranges between 20 and 70 m/s. In addition to the measured quantities such as bearing forces, accelerations are also measured at 4 different positions on and under the plate, as well as the deflection at several positions. The measured data are used for the analysis of the damage form and the numerical examinations with the program Ansys Autodyn and the material model after Drucker-Prager. Numerical investigations support the tests, with detailed analysis of individual effects. These numerical computations and the planar tomographic investigations were carried out at BAM in Berlin. With the help of planar tomographic evaluation, the damaged structure is made visible and compared with the numerical results. Influences of the bending reinforcement are explained on the basis of damage evaluation in the local area and on selected measured values. In addition to the test evaluation, the tomographic and numerical methods are presented. T2 - XI International Conference on Structural Dynamics (EURODYN 2020) CY - Online meeting DA - 23.11.2020 KW - Post-impact evaluation KW - Damage characterization KW - Planar tomography KW - Drucker-Prager KW - Ansys Autodyn PY - 2020 SN - 978-618-85072-2-7 VL - 1 SP - 2521 EP - 2543 PB - Institute of Structural Analysis and Antiseismic Research, School of Civil Engineering, National Technical University of Athens (NTUA), Greece CY - Athens, Greece AN - OPUS4-51769 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Friedrich, Christian T1 - Eignungsprüfungen geophysikalischer Sensoren zur Rissdetektion an Demonstrationsbauwerken N2 - Bei der Betonage von Abdichtbauwerken können Temperaturen bis 110 °C und hohe Drücke bis 5 MPa erreicht werden. Mittels Technikumsversuchen wurde nachgewiesen, dass Mikroakustik- und Ultraschallsensoren zum Einbau in Demonstrationsbauwerke geeignet sind. Die Untersuchungen wurden bei der BAM (Bundesanstalt für Materialforschung und -prüfung) in Berlin durchgeführt. Es ist vorgesehen, die Sensoren in Morsleben am Demonstrationsbauwerk im Anhydrit einzusetzen. T2 - 84. Jahrestagung der Deutschen Geophysikalischen Gesellschaft CY - Jena, Germany DA - 10.03.2024 KW - Ultraschall KW - Eignungsprüfung KW - Risse KW - Abdichtbauwerk KW - Anhydrit PY - 2024 AN - OPUS4-59772 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nerger, Deborah T1 - Impact damage characterization at RC plates with planar tomography and FEM N2 - Prediction of dynamic effects of reinforced concrete structures under impact loading is a technical challenge. This is a consequence of the great variability of the physical properties resulting from the wide adaptability of reinforced concrete and a consequence of the wide range of impact loading. Experiments and numerical investigations are normally used on a small scale to address the problem. In this paper, impact tests on reinforced conrete plates with the lateral dimensions of 1.5 m x 1.5 m and a thickness of 30 cm are presented. In bending reinforcement, besides the velocity two properties are varied, the diameter and the spatial distribution of the rebars. Experiments are performed at the Otto-Mohr-Laboratory of the Institute of Concrete Structures of the Technische Universit¨at Dresden. Due to the accelerated fall of the impactor the velocity ranges between 20 and 70 m/s. In addition to the measured quantities such as bearing forces, accelerations are also measured at 4 different positions on and under the plate, as well as the deflection at several positions. The measured data are used for the analysis of the damage form and the numerical examinations with the program Ansys Autodyn and the material model after Drucker-Prager. Numerical investigations support the tests, with detailed analysis of individual effects. These numerical computations and the planar tomographic investigations were carried out at BAM in Berlin. With the help of planar tomographic evaluation, the damaged structure is made visible and compared with the numerical results. Influences of the bending reinforcement are explained on the basis of damage evaluation in the local area and on selected measured values. In addition to the test evaluation, the tomographic and numerical methods are presented. T2 - XI International Conference on Structural Dynamics (EURODYN 2020) CY - Online meeting DA - 23.11.2020 KW - Post-impact evaluation KW - Damage characterization KW - Planar tomography KW - Drucker-Prager KW - Ansys Autodyn PY - 2020 AN - OPUS4-51768 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baeßler, Matthias A1 - Herrmann, Ralf A1 - Hille, Falk A1 - Wille, Frank T1 - Dynamisches Verhalten und Überwachung des Großen Fallturms der BAM in Horstwalde N2 - Falltürme sind Bauwerke, die als Versuchsanlagen sehr speziellen, impulsartigen Belastungen ausgesetzt sind. Am Fallturm auf dem Testgelände Technische Sicherheit (TTS) der BAM wurde bei Routineinspektionen eine Abnahme der strukturellen Integrität in Form von Vorspannungsverlusten in den Bolzen der Stahlverbindungen festgestellt. Um ein Verständnis für die zugrundeliegenden Trag- und Schädigungsmechanismen zu erlangen, wurde ein umfassendes Structural Health Monitoring (SHM) System geplant und am Bauwerk installiert unter Nutzung von digitalen Bauwerksmodellen. Für die Auslegung des Überwachungssystems, insbesondere aber zur Unterstützung der Untersuchung des Schädigungsprozesses, wurden Finite-Elemente-Modelle erstellt. Um sicherzustellen, dass die FE-Modelle das reale Tragwerksverhalten mit ausreichender Genauigkeit abbilden, mussten sie jedoch in Bezug auf die gemessenen Antworten des Tragwerks kalibriert werden. Der vorliegende Beitrag beschreibt experimentelle und numerische Untersuchungen zur Identifizierung des strukturellen Systems des Stahlrohrgitterturms in Vorbereitung einer Überwachungskampagne. Die Auswertung von gemessenen Schwingungen unter ambienter Anregung ermöglichte die Identifizierung der Eigenfrequenzen mehrerer globaler Schwingungsmoden des Fallturms. Zur Modellvalidierung wurde zunächst eine Sensitivitätsanalyse durchgeführt, um die Parameter mit dem größten Einfluss zu ermitteln. Anschließend wurde ein evolutionärer Algorithmus (EA) zur Optimierung nach dem Prinzip der Minimierung der Differenzen zwischen gemessenen und simulierten charakteristischen Antworten eingesetzt. Das aktualisierte Modell wurde schließlich an der dynamischen Reaktion der Turmstruktur infolge einer realen Falltest-induzierten Stoßbelastung validiert. Die Ergebnisse zeigten eine gute Übereinstimmung zwischen numerischen und experimentellen Ergebnissen. N2 - Drop test towers are structures subjected to very specific dynamic loadings. At the drop test tower at the Test Site Technical Safety (TTS) of BAM routine inspections revealed a decline of structural integrity in form of loss of pretension in bolts of structural steel connections. To get an understanding about the underlying damage mechanisms as well as to assure the structural safety in operation, a multifaceted Structural Health Monitoring (SHM) system was planned and installed at the structure with the help of digital models. For planning the monitoring system but especially for supporting the investigation of the damaging process finite element models are deployed. Though, to ensure the capability of the FE model to reproduce the real structural behavior in sufficient accuracy, it needs to be calibrated in respect to measured responses of the structure. The present contribution describes experimental and numerical investigations to identify the structural system of the steel tube lattice tower in preparation of the monitoring campaign. An ambient vibration test allowed the identification of the natural frequencies of several global vibrational modes of the drop test tower. For model updating first a sensitivity analysis is applied to identify the most influencing parameter. In succession a genetic algorithm was applied for optimization in the sense of minimization of the difference between measured and simulated characteristic responses. The updated model is finally validated on the dynamic response of the tower structure to a real drop test induced impact loading. The results showed a good agreement between numerical and experimental results though the robustness of the simulation should be improved by more sophisticated numerical modelling. T2 - 7. VDI-Fachtagung Baudynamik CY - Würzburg, Germany DA - 27.04.2022 KW - Großer Fallturm Horstwalde KW - Structural Health Monitoring KW - Belastungsversuch KW - Modalanalyse KW - Schwingungsdynamik KW - Finite Elemente Simulation PY - 2022 SN - 978-3-18-092379-6 SN - 978-3-18-102379-2 DO - https://doi.org/10.51202/9783181023792-265 SN - 0083-5560 VL - 2379 SP - 265 EP - 284 PB - VDI-Verlag CY - Düsseldorf AN - OPUS4-55472 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nerger, Deborah A1 - Moosavi, Robabeh A1 - Bracklow, F. A1 - Hering, M. A1 - Kühn, T. A1 - Curbach, M. A1 - Hille, Falk A1 - Rogge, Andreas T1 - Planar tomography and numerical analysis for damage characterization of impact loaded RC plates N2 - The damage analysis of reinforced concrete (RC) is of high interest for reasons of effective maintenance and structural safe-ty of buildings. The damage structures of RC plates loaded by an impact were investigated, applying X-ray planar tomogra-phy and finite element method (FEM). Planar tomography allows getting three-dimensional information of the RC elements and the damage including crack, spalling and scabbing. The FEM model validated on the tomography data justifies the appli-cation for further predictions of the damage description. In this study, we investigated concrete plates of three different thick-ness subjected to impacts at different low- and medium-velocity, whereby the used impactor had a flat tip, which resulted in small penetrations on the front side and scabbing on the rear side. In order to quantify the damage, the damage volume and its distribution through the plate were computed and the correlations between degree of damage and impact velocity were found out. KW - Impact KW - Damage characterization KW - Planar tomography KW - Numeric simulation KW - Reinforced concrete structure PY - 2020 DO - https://doi.org/10.1002/cend.202000017 VL - 8 SP - 1 EP - 19 PB - Wiley AN - OPUS4-51117 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nerger, Deborah A1 - Hille, Falk A1 - Moosavi, Robabeh A1 - Grunwald, Marcel A1 - Redmer, Bernhard A1 - Kühn, T. A1 - Hering, M. A1 - Bracklow, F. T1 - Post-impact evaluation at RC plates with planar tomography and FEM N2 - Due to the wide range of applications, the easy production and the large field of use, reinforced concrete (RC) is a widespread building material. This variety of applications is reflected in a wide range of physical material properties. Not only therefor it still is a technical challenge to provide all necessary test conditions for experimentally reproducing dynamic effects under impact loading of RC structures. In this paper we present investigations on the thicknesses of RC plates under low and medium high velocity impact loading by a flat-tipped impactor. The planar tomography setup at BAM is used to visualize the impact damage and to characterize the damage features such as cracks, scabbing and spalling. Further, the comparison of tomography results with those of an applied numeric simulation analysis is used to verify the numeric models for future damage prognosis under impact loading. Using the results of both, the tomographic as well as the FE analysis, different damage features were investigated and compared regarding their validity. Crack damage plays a leading part and the significance of summarized crack values as well as their distribution is analyzed. The total damage value but also the determined damage distribution both provide an input for describing damage as a function of the impactor velocity and plate thickness. KW - Reinforced concrete structure KW - Post-impact evaluation KW - Damage characterization KW - Ansys Autodyn KW - Drucker-Prager KW - Planar tomography PY - 2020 DO - https://doi.org/10.1016/j.matpr.2020.05.671 SP - 1 EP - 10 PB - Elsevier AN - OPUS4-51115 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baeßler, Matthias T1 - Dynamisches Verhalten und Überwachung des Großen Fallturms der BAM in Horstwalde N2 - Falltürme sind Bauwerke, die als Versuchsanlagen sehr speziellen, impulsartigen Belastungen ausgesetzt sind. Am Fallturm auf dem Testgelände Technische Sicherheit (TTS) der BAM wurde bei Routineinspektionen eine Abnahme der strukturellen Integrität in Form von Vorspannungsverlusten in den Bolzen der Stahlverbindungen festgestellt. Um ein Verständnis für die zugrundeliegenden Trag- und Schädigungsmechanismen zu erlangen, wurde ein umfassendes Structural Health Monitoring (SHM) System geplant und am Bauwerk installiert unter Nutzung von digitalen Bauwerksmodellen. Für die Auslegung des Überwachungssystems, insbesondere aber zur Unterstützung der Untersuchung des Schädigungsprozesses, wurden Finite-Elemente-Modelle erstellt. Um sicherzustellen, dass die FE-Modelle das reale Tragwerksverhalten mit ausreichender Genauigkeit abbilden, mussten sie jedoch in Bezug auf die gemessenen Antworten des Tragwerks kalibriert werden. Der vorliegende Beitrag beschreibt experimentelle und numerische Untersuchungen zur Identifizierung des strukturellen Systems des Stahlrohrgitterturms in Vorbereitung einer Überwachungskampagne. Die Auswertung von gemessenen Schwingungen unter ambienter Anregung ermöglichte die Identifizierung der Eigenfrequenzen mehrerer globaler Schwingungsmoden des Fallturms. Zur Modellvalidierung wurde zunächst eine Sensitivitätsanalyse durchgeführt, um die Parameter mit dem größten Einfluss zu ermitteln. Anschließend wurde ein evolutionärer Algorithmus (EA) zur Optimierung nach dem Prinzip der Minimierung der Differenzen zwischen gemessenen und simulierten charakteristischen Antworten eingesetzt. Das aktualisierte Modell wurde schließlich an der dynamischen Reaktion der Turmstruktur infolge einer realen Falltest-induzierten Stoßbelastung validiert. Die Ergebnisse zeigten eine gute Übereinstimmung zwischen numerischen und experimentellen Ergebnissen. N2 - Drop test towers are structures subjected to very specific dynamic loadings. At the drop test tower at the Test Site Technical Safety (TTS) of BAM routine inspections revealed a decline of structural integrity in form of loss of pretension in bolts of structural steel connections. To get an understanding about the underlying damage mechanisms as well as to assure the structural safety in operation, a multifaceted Structural Health Monitoring (SHM) system was planned and installed at the structure with the help of digital models. For planning the monitoring system but especially for supporting the investigation of the damaging process finite element models are deployed. Though, to ensure the capability of the FE model to reproduce the real structural behavior in sufficient accuracy, it needs to be calibrated in respect to measured responses of the structure. The present contribution describes experimental and numerical investigations to identify the structural system of the steel tube lattice tower in preparation of the monitoring campaign. An ambient vibration test allowed the identification of the natural frequencies of several global vibrational modes of the drop test tower. For model updating first a sensitivity analysis is applied to identify the most influencing parameter. In succession a genetic algorithm was applied for optimization in the sense of minimization of the difference between measured and simulated characteristic responses. The updated model is finally validated on the dynamic response of the tower structure to a real drop test induced impact loading. The results showed a good agreement between numerical and experimental results though the robustness of the simulation should be improved by more sophisticated numerical modelling. T2 - 7. VDI-Fachtagung Baudynamik CY - Würzburg, Germany DA - 27.04.2022 KW - Großer Fallturm Horstwalde KW - Structural Health Monitoring KW - Belastungsversuch KW - Modalanalyse KW - Schwingungsdynamik KW - Finite Elemente Simulation PY - 2022 AN - OPUS4-55470 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lay, Vera A1 - Baensch, Franziska A1 - Skłodowska, Anna A1 - Fritsch, Tobias A1 - Stamm, Michael A1 - Prabhakara, Prathik A1 - Johann, Sergej A1 - Sturm, Patrick A1 - Kühne, Hans-Carsten A1 - Niederleithinger, Ernst T1 - Multi–sensory Monitoring and Non–destructive Testing of New Materials for Concrete Engineered Barrier Systems N2 - The crucial part of nuclear waste storage is the construction of sealing structures made of reliable, safe and well–understood materials. We present an extended analysis of long-term multi–sensory monitoring and non–destructive testing (NDT) inspection of two laboratory specimens aiming at potential materials for sealing structures for nuclear waste repositories. Specimens with a volume of 340 litres made from newly developed alkali–activated materials (AAM) and established salt concrete (SC) were analysed using embedded acoustic emission and wireless radio-frequency identification (RFID) sensors, ultrasonic echo imaging, active thermography, and X–ray computed tomography. The monitoring analysis showed lower heat of reaction and 50% less acoustic emission events in AAM compared to SC. However, due to the surface effects of the AAM material, the number of acoustic emission events increased significantly after approximately two months of monitoring. Subsequently performed NDT inspections reliably located embedded sensors and confirmed the absence of major cracks or impurities. The presented laboratory results show the feasibility and potential of comprehensive NDT monitoring and inspection to characterise cementitious and alternative materials as well as the need for multi–parameter long–term monitoring. Thus, our study demonstrates that tailored NDT investigations will help to develop safe sealing structures for nuclear waste repositories. KW - Radioactive waste KW - Barrier KW - Concrete KW - AAM KW - Non-destructive testing PY - 2024 DO - https://doi.org/10.3151/jact.22.516 SN - 1347-3913 VL - 22 IS - 9 SP - 516 EP - 529 PB - Japan Concrete Institute AN - OPUS4-61461 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lay, Vera A1 - Mielentz, Frank A1 - Prabhakara, Prathik A1 - Baensch, Franziska A1 - Johann, Sergej A1 - Hofmann, Detlef A1 - Sturm, Patrick A1 - Stamm, Michael A1 - Niederleithinger, Ernst T1 - Multi-sensory monitoring and ultrasound for quality assurance at underground sealing structures N2 - Within the safety concepts of underground disposal sites of nuclear waste, engineered barriers play an important role. As these sealing structures have high demands concerning integrity, we aim at advancing the available construction materials, monitoring, and inspection techniques within the project SealWasteSafe. A specifically developed alkali-activated material is compared to classical salt concrete. A comprehensive multi-sensory monitoring scheme is used at 150-340 l specimens to monitor setting and hardening of both materials. All sensors are demonstrated to resist the highly alkaline environments. Besides cabled and wireless temperature and humidity of the materials, strain variations using fibre optic sensors and acoustic emissions are recorded over periods of at least 28 days, partly for more than eight months. After hardening of the specimens, further nondestructive evaluations using ultrasonic echo and thermographic measurements are conducted. Preliminary results proof the suitability of the tested sensors and clearly highlight differences between the tested materials. Particularly, the newly developed alkali-activated material shows lower acoustic emission activity indicating less cracking activity. Additionally, unique ultrasonic methods will enable better images of potential internal objects and cracks at in-situ sealing structures. A largescale ultrasonic system is optimised to reliably detect objects at a depth exceeding 9 m while still obtaining a good resolution. Modelling studies show the potential of further increasing the distance between individual transducer arrays. Additionally, a new ultrasonic borehole probe using phased arrays allowing for beam focussing is constructed and tested. Laboratory measurements at a halfcylindrical concrete specimen coincide well with the previous modelling. In total, the presented safe materials, detailed monitoring approaches and ultrasonic quality assurance methods will help to obtain safe sealing structures within salt as a host rock. The concepts can partly be transferred to sealing structures in alternative host rocks and will also be valuable for non-nuclear waste repositories. T2 - NDE NucCon CY - Espoo, Finland DA - 25.01.2023 KW - SealWasteSafe KW - Engineered barriers KW - Monitoring KW - Embedded sensors KW - Ultrasonic imaging PY - 2023 SP - 2 EP - 10 AN - OPUS4-56928 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Skłodowska, Anna A1 - Baensch, Franziska A1 - Lay, Vera A1 - Niederleithinger, Ernst A1 - Kühne, Hans-Carsten T1 - Acoustic emission monitoring for engineered barriers in nuclear waste disposal N2 - To safely dispose of nuclear waste in underground facilities, engineered barrier systems are needed to seal shafts and galleries. The material used in these barriers must be adapted to the host rock parameters. Shrinking and cracking must be avoided to provide a barrier with almost zero permeability. For repositories in salt rock environments, several types of salt concrete (SC) are possible construction materials. Within the project SealWasteSafe, we compared the behavior of an innovative alkali-activated material (AAM) with standard SC in their hydration and hardening phase. To monitor the microstructural changes within the two materials SC and AAM, acoustic emission (AE) signals have been recorded for up to ~250 days on 340-litercubic specimens. The phenomenon of AE is defined as the emission of elastic waves in materials due to the release of localized internal energy. Such energy release can be caused by the nucleation of micro-fracture, e.g., in concrete while curing or when exposed to load. The occurrence of AE events gives first rough indications of microstructural changes and potentially occurring cracking and thus, provides insights for structural health monitoring (SHM). The results show, that for the first 28 days after casting, less AE activity was detected in the AAM compared to SC. After 61 days, in the AAM material, the number of AE events exceeded those observed in the SC. However, the majority of the AE detected and located in AAM was related to surface effects, and not to microstructural changes or occurring cracks within the bulk volume. Additionally, the source location analysis indicated, that despite lower activity in SC, we observed some clustering of the events. In contrast, in AAM, the activity inside the specimen is randomly distributed over the whole volume. The monitoring results help to estimate the material’s sealing properties which are crucial to assess their applicability as sealing material for engineered barriers. T2 - 11th European Workshop on Structural Health Monitoring (EWSHM 2024) CY - Potsdam, Germany DA - 11.06.2024 KW - Endlager KW - Barriere KW - AAM KW - Akustische Emission PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-604699 UR - https://www.ndt.net/article/ewshm2024/papers/768_manuscript.pdf DO - https://doi.org/10.58286/29834 SN - 1435-4934 SP - 1 EP - 7 PB - NDT.net AN - OPUS4-60469 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Henning, Ricky A1 - Sturm, Patrick A1 - Keßler, S. A1 - Gluth, Gregor T1 - Corrosion of hybrid alkaline cements in saline solution simulating evaporite rock – effect of the Portland clinker content N2 - Two hybrid alkaline cements (HAC) based on Portland clinker, ground granulated blast furnace slag (GGBFS), fly ash and sodium sulfate, as well as an alkali-activated GGBFS/fly ash blend and a Portland cement paste were exposed to a saturated saline solution for 70 days. The combined chemical attack of chloride, magnesium and sulfate ions and the associated changes of the phase assemblage of the materials were studied by X-ray diffraction, thermal analysis and spatially resolved X-ray fluorescence spectroscopy. The experimental results revealed dissolution of ettringite, C-N-A-S-H and calcite, and the formation of gypsum, Kuzel's salt and Friedel's salt; thermodynamic modeling indicated the formation of M-S-H. The resistance of the HAC against attack by the saline solution increased with Portland clinker fraction. The capacity of portlandite to maintain pH at values above 10 is found to be a major factor controlling the resistance of HAC against corrosion in the saline solution. KW - Hybrid cements KW - Alkali-activated materials KW - Magnesium chloride KW - Corrosion KW - Salt attack PY - 2023 DO - https://doi.org/10.1016/j.cemconres.2023.107215 SN - 0008-8846 SN - 1873-3948 VL - 172 SP - 1 EP - 14 PB - Elsevier Ltd. AN - OPUS4-57638 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gluth, Gregor T1 - Chemical resistance of hybrid cements against aggressive saline solutions N2 - The safe storage of radioactive material in nuclear waste repositories is a major task of our societies. The sealing function of such repositories is depending on the ability of the applied construction materials to form and maintain a geotechnical barrier with the surrounding rock. Corrosion of the construction material can lead to leakage of radioactive compounds and must therefore be avoided or minimized. Since concretes based on conventional Portland cement have not been found suitable in this context, alternative binders must be evaluated. One such class of binders are hybrid cements, which are blends of low fractions of Portland cement or Portland clinker and high fractions of supplementary cementitious materials, such as blast furnace slag and fly ash, activated by an alkali salt. Besides a low heat of hydration and a sufficient early compressive strength [1], chemical similarities with ancient Roman concrete suggest an excellent durability in saline environments [2], which makes these cements potentially suitable for applications in nuclear waste repositories in evaporite rock, such as the Morsleben repository in Germany. In the present study, two previously designed and characterized [3] hybrid cements, an alkali-activated slag/fly ash blend, and an OPC paste were studied regarding their resistance against corrosion in an aggressive saline solution. The saline solution was designed by the Gesellschaft für Anlagen- und Reaktorsicherheit (GRS) [Association for Facility and Reactor Safety] as a reference representing a solution forming as the result of contact of surface water with evaporite rock. The cement pastes were exposed to the saline solution up to 70 days and characterized by X-ray diffraction, thermogravimetric analysis and spatially resolved X-ray fluorescence spectroscopy. In addition, thermodynamic modelling was performed to simulate the alterations of the phase assemblage with increasing exposure to the saline solution and, thus, provide indications on the long-term durability of the cement pastes. The experimental results revealed a correlation between the Portland clinker content of the cements and the resistance of the cement pastes against attack by the saline solution. This outcome was related to the formation of portlandite when sufficient clinker was available, which maintained the pore solution pH at ~12.5, and thus prevented the dissolution of cementitious phases. Once portlandite was consumed, C-N-A-S-H and ettringite dissolved and released calcium, aluminium, and hydroxide ions in the solution, maintaining the pH at ~10. In this pH range, the formation Cl-AFm phases was observed. At lower pH values, i.e., extended exposure durations, gypsum was the major corrosion product. The pH-dependent dissolution and formation of phases lead to pronounced zonation in the exposed cement pastes. Thermodynamic modelling indicated that the dissolved silicon from C-N-A-S-H reacts with magnesium ions in the saline solution to form M-S-H, and that long-term exposure eventually leads to a material rich in amorphous silica and brucite. T2 - Joint 6th International Workshop on Mechanisms and Modelling of Waste / Cement Interactions & EURAD - WP CORI Workshop CY - Prague, Czech Republic DA - 20.11.2023 KW - Hybrid cement KW - Corrosion KW - Salt solution KW - Magnesium chloride KW - Evaporite rock PY - 2023 AN - OPUS4-58885 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gluth, Gregor A1 - Garel, S. ED - Valente, I. B. ED - Ventura Gouveia, A. ED - Dias, S. S. T1 - Calorimetry Study of the Influence of Portland Cement Content, Slag/Fly Ash Ratio, and Activator Type on the Early Hydration of Hybrid Cements N2 - Hybrid cements (cements composed of Portland clinker, supplementary cementitious materials and an alkaline activator) potentially combine advantages of conventional cements with those of alternative binders, such as low heat of hydration and improved durability in some environments. While fly ash-based hybrid cements have been studied in considerable detail, slag-dominated hybrid cements appear to have received less attention. Here, the latter materials have been studied by isothermal calorimetry, X-ray diffraction and strength testing. The heat of hydration of these cements was as low as ~50% of that of an ordinary Portland cement, while their strength after 28-day curing was in the range 31–61 MPa. The phase assemblages after 28-day curing depended on the activator, with Na2SO4 leading to ettringite and Na2CO3 leading to hemicarbonate formation, respectively, besides C–A–S–H, portlandite and hydrotalcite. The U phase was identified when a high Na2SO4 dose and/or fly ash was employed. Na2SO4 accelerated the early reaction of the Portland clinker, while Na2CO3 appeared to decrease the extent of reaction of the clinker and led to a shift of the second hydration peak (likely related to slag reaction) to later hydration times, as did substitution of slag by fly ash. Increasing Na2SO4 dose from 4 to 6% did not lead to further acceleration of hydration or improved strength. T2 - 3rd RILEM Spring Convention and Conference (RSCC 2020) CY - Guimarães, Portugal DA - 10.03.2020 KW - Hybrid cements KW - Alkali-activated materials KW - Calorimetry KW - Early hydration PY - 2021 SN - 978-3-030-76550-7 DO - https://doi.org/10.1007/978-3-030-76551-4_20 SP - 217 EP - 226 PB - Springer CY - Cham AN - OPUS4-53071 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Henning, Ricky A1 - Sturm, Patrick A1 - Kühne, Hans-Carsten A1 - Keßler, S. A1 - Gluth, Gregor T1 - Untersuchungen zur Wärmeentwicklung von hybriden Zementen N2 - Die Hauptfunktion von Verschlussbauwerken für End- und Zwischenlager von radioaktiven Abfällen besteht in der Erhaltung der geologischen Barriere. Vor allem soll ein potenzieller Stofftransport durch eine möglichst geringe Permeabilität des Bauwerks verhindert bzw. auf vernachlässigbare Werte herabgesetzt werden. Die in-situ-Permeabilität des Verschlussbauwerks steht dabei in direktem Zusammenhang mit dessen Poren- und Makrostruktur, welche bei Bauwerken auf Basis von Beton insbesondere durch Schwind-verformungen und durch thermisch induzierte Rissbildung infolge der Reaktionswärmeentwicklung des Bindemittels gestört werden kann. Die Betone müssen daher neben einer hohen chemischen Langzeitstabilität auch eine geringe bzw. langsame Wärmeentwicklung während der Erhärtungsreaktionen aufweisen. Als hybride Zemente werden Mischungen aus Portlandzement, Betonzusatzstoffen und einem alkalischen Aktivator bezeichnet. Dabei können u. a. Alkalisulfate, Alkalicarbonate, Alkalisilicate und Alkalihydroxide als Aktivatoren zum Einsatz kommen. Aufgrund ihrer hohen chemischen Stabilität im salinaren Milieu sind Betone aus solchen Zementen potenziell besonders gut als Verfüllmaterial für End- und Zwischenlager im Steinsalz geeignet. In der vorliegenden Studie wurden daher hybride Zemente hinsichtlich ihrer Wärmeentwicklung in einem isothermen Kalorimeter sowie hinsichtlich Phasenbestand und Festigkeiten untersucht. Hybride Zementleime wurden auf Basis von Portlandklinker, Hüttensandmehl, Flugasche und Natriumsulfat hergestellt und die Zusammensetzungen systematisch variiert, um den Einfluss der Komponenten auf Wärmeentwicklung, Phasenbestand und mechanische Eigenschaften der Leime zu untersuchen; zusätzlich wurden zu Vergleichszwecken ein Zementleim auf Basis der Betonrezeptur M2 sowie eine alkalisch aktivierte Flugasche untersucht. T2 - 2. Tage der Standortauswahl CY - Online meeting DA - 11.02.2021 KW - Hybride Zemente KW - Hydratationswärme KW - Kalorimetrie PY - 2021 SP - 137 EP - 139 AN - OPUS4-52216 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Henning, Ricky A1 - Sturm, Patrick A1 - Keßler, S. A1 - Gluth, Gregor ED - Lothenbach, B. ED - Wieland, E. ED - Altmaier, M. T1 - Influence of salt aggregate on the degradation of hybrid alkaline cement (HAC) concretes in magnesium chloride-rich saline solution simulating evaporite rock N2 - Concretes produced from salt aggregate and hybrid alkaline cements, an alkali-activated slag/fly ash blend, or a Portland cement were exposed to a magnesium chloride-rich saline solution ([Mg2+] = 3.6 m, [Cl−] = 8.3 m), representing a solution formed after contact of surface water with evaporite rock (rock salt) in a nuclear waste repository. The hydration and deterioration of the concretes were studied with X-ray diffraction, thermogravimetric analysis, pH mapping and permeability measurements. The results show that calcium silicate hydrate (C-S-H) or sodium-substituted calcium aluminium silicate hydrate (C-N-A-S-H) and Friedel's salt were the major reaction products in the concretes prior to exposure to the saline solution. During exposure to the saline solution, increasing amounts of C-S-H/C-N-A-S-H dissolved, and gypsum and a secondary AFm phase formed. The durability of the concretes improved with increasing amounts of Portland clinker in the cements, due to the associated differences in permeability and chemical resistance. Nevertheless, a massive increase of permeability occurred for all concretes, likely caused by crack formation due to the formation of gypsum from anhydrite in the salt aggregate. Thus, the behavior of the concretes differed from, and was more complex than, the behavior of plain cement pastes. T2 - Joint 6th International Workshop on Mechanisms and Modelling of Waste/Cement Interactions (JCCW 2023) CY - Prague, Czech Republic DA - 20.11.2023 KW - Nuclear waste repository KW - Evaporite rock KW - Magnesium chloride brine KW - Concrete KW - Hybrid alkaline cement PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-599928 DO - https://doi.org/10.1016/j.apgeochem.2024.106027 SN - 0883-2927 SN - 1872-9134 VL - 168 SP - 1 EP - 14 PB - Elsevier AN - OPUS4-59992 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sturm, Patrick A1 - Moye, J. A1 - Gluth, Gregor A1 - Vogler, Nico A1 - Taffe, A. A1 - Kühne, Hans-Carsten ED - Rossignol, S. ED - Gluth, Gregor T1 - Properties of alkali-activated mortars with salt aggregate for sealing structures in evaporite rock N2 - Concrete structures for sealing of tunnels in the host rock are an essential part of systems for nuclear waste storage. However, concretes based on blended cements or magnesium oxychloride cements, which are commonly considered for this application, can deteriorate severely due to a significant heat of hydration and associated deformation and cracking. Alkali-activated materials (AAMs) offer a potential solution to this problem because of their low heat release during hardening. To explore their suitability for the construction of sealing structures in evaporite rock, various AAMs with salt aggregate were studied regarding fresh properties, heat release, mechanical properties and microstructure. The heat of reaction of the AAMs was up to 55% lower than that of a blended cement designed for sealing structures, indicating significant benefits for the intended application. Other relevant properties such as mechanical strength and permeability depended strongly on the mix-design of the AAMs and curing conditions. KW - Alkali-activated materials KW - Geopolymers KW - Nuclear waste storage KW - Sealing structures KW - Evaporite rock PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-519422 DO - https://doi.org/10.1016/j.oceram.2020.100041 SN - 2666-5395 VL - 5 IS - Special issue: Alkali-activated materials and geopolymers in ceramics and beyond SP - 1 EP - 8 PB - Elsevier CY - Amsterdam AN - OPUS4-51942 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -