TY - CONF A1 - Hüsken, Götz A1 - Shamsuddoha, Md A1 - Thiele, Marc A1 - Baeßler, Matthias A1 - Kühne, Hans-Carsten T1 - Comparison of cracks formed in scaled grouted connection of offshore energy structures under static and cyclic loads N2 - Global energy consumption will increase in the future necessitating both fossil fuels and renewable energy choices - especially wind energy. Such high energy demand requires installation of offshore energy structures, rigs, platforms and towers, which are susceptible to adverse environmental conditions along with maintenances. Due to their large size and remote locations, cylindrical grouted joints are often adopted between substructure and foundation in these offshore platforms and wind structures such as monopiles. However, these connections are composite structures with exterior sleeve, interior pile and infill mortar. Degradation and settlements were reported inside similar connections, which were installed in last three decades. Besides, grouting in the offshore sites were proven difficult to obtain ideal load bearing capacity. In-situ loading conditions were also found to be affecting the failure mechanism inside such connections. This study aims at characterizing the nature of cracks generated in these grouted connections under both static and cyclic loading. Scaled grouted joints were manufactured using a novel reusable mold, and connections were loaded to failure to visualize the main failure patterns. An assessment between failure under these two types of load is drawn along with comparison to previously available literature. T2 - 5th International Conference on Smart Monitoring, Assessment and Rehabilitation of Civil Structures CY - Potsdam, Germany DA - 27.08.2019 KW - Grouted connection KW - Crack formation KW - Crack pattern KW - Static load KW - Cyclic load PY - 2019 AN - OPUS4-48797 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Babski, Veronika A1 - Hüsken, Götz A1 - Pirskawetz, Stephan A1 - Ehlers, N. A1 - Kühne, Hans-Carsten A1 - Brouwers, H.J.H. T1 - Characterisation of Ultra-High Performance Fibre Reinforced Concrete (UHPFC) under Tensile Loading by Acoustic Emission and Optical Deformation Analysis N2 - During the past 20 years, innovative developments in concrete technology have enabled the production of ultra-high performance fibre reinforced concretes (UHPFC) for the protection and preservation of concrete structures. The main characteristics of UHPFC comprise high compressive and flexural strength as well as high ductility compared to normal strength, normal weight concrete (NSC). This paper focuses on the analysis of crack formation and crack propagation in UHPFC under tensile loading under quasistatic conditions by using acoustic emission (AE) and optical deformation analysis (ODA). AE is a non-destructive technique to monitor the development of micro structural damage processes caused by external forces. In this context, AE allows for a continuous monitoring of changes in the microstructure (cracks) over time and the corresponding localisation by appropriate algorithms. The AE measurements were performed along with ODA at the surface of the samples in order to analyse the deformation behaviour of the samples and the crack propagation. For the tests, a UHPFC reference mixture was developed and tested with three different volume percentages of steel fibres (1.0 V.-%, 2.0 V.-%, and 3.0 V.-%). This paper shows that the application of AE is a suitable method to analyse the crack propagation in UHPFC specimens under tensile loading and to localise the crack initiation. Furthermore, insights into the failure mechanism of the fibres are offered by the analysis of the signals of the AE measurements, which allows for a better understanding of UHPFC and its general performance. T2 - 4th International Symposium on Ultra-High Performance Concrete and High Performance Materials (HiPerMat) CY - Kassel, Germany DA - 09.03.2016 KW - Acoustic emission KW - Crack formation KW - Crack propagation KW - Optical deformation analysis KW - Tensile loading KW - UHPFC PY - 2016 AN - OPUS4-36898 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -