TY - CONF A1 - Frei, J. A1 - Biegler, M. A1 - Rethmeier, Michael T1 - Resistance spot welding under external load for evaluation of LME susceptibility of zinc coated advanced high strength steel sheets N2 - Some zinc coated advanced high strength steels (AHSS), under certain manufacturing conditions, are known to be prone to liquid metal embrittlement (LME) during resistance spot welding. LME is an undesired phenomenon, which can cause both surface and internal cracks in a spot weld, potentially influencing its strength. An effort is made to understand influencing factors of LME better, and evaluate geometry-material combinations regarding their LME susceptibility. Manufacturers benefit from such knowledge because it improves the processing security of the materials. The experimental procedure of welding under external load is performed with samples of multiple AHSS classes with strengths up to 1200 MPa, including dual phase, complex phase and TRIP steels. This way, externally applied tensile load values are determined, which cause liquid metal embrittlement in the samples to occur. In the future, finite element simulation of this procedure gives access to in-situ stress and strain values present during LME formation. The visualization improves the process understanding, while a quantification of local stresses and strains allows an assessment of specific welded geometries. T2 - ESDAD 2019 CY - Dusseldorf, Germany DA - 24.06.2019 KW - RSW KW - LME KW - Advanced high strength steel KW - Testing method KW - Zinc coated steel PY - 2019 AN - OPUS4-49079 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Waniek, Tassilo T1 - Water as side effect of reinforcing boehmite filler Local changes in anhydride cured epoxy resin N2 - Nanocomposites offer wide opportunities for lightweight constructions and enable reduction of weight and volume. Beside macroscopic toughening nanoparticle reinforced polymers show a soft interface around boehmite (AlOOH) filler nanoparticles. A related strong interaction between boehmite and the anhydride cured resin system is widely suspected in literature but not determined by structural Analysis. Determination of the molecular structure is important to allow simulations approaching the real system and predict future reinforcing effects. DRIFT (diffuse refletance infrared fourier transformed) spectra of the boehmite reinforced anhydride cured epoxy show significant changes in the molecular structure compared to the neat polymer. Further investigations of the interactions between the single components of the resin system and the boehmite filler pointed out reactions between released water released from the boehmite filler and the anhydride hardener or amine accelerator. This leads to the discussion of competing polymerisation mechanisms that highly influence the polymer properties. Ongoing experiments and literature research approve that this impact of water is able to locally change the stoichiometrie, alter the curing mechanism or support an inhomogeneous crosslink density. T2 - Polydays 2019 CY - Erwin-Schrödinger-Zentrum, Berlin Adlershof, Germany DA - 11.09.2019 KW - Nanocomposites KW - Epoxy KW - FTIR spectroscopy KW - Boehmite alumina PY - 2019 AN - OPUS4-49010 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Babutzka, Martin T1 - Beschreibung der Deckschichtbildung bei Zink und Zinklegierungen mittels minimalinvasiver Korrosionsuntersuchungen und analytischer Methoden (MINIMAL) N2 - Der Vortrag stellt ein neuartiges Korrosionsprüfverfahren für Zinküberzüge auf Basis gelartiger Elektrolyte vor und führt die Vorteile gegenüber konventionellen Prüfverfahren auf. Basierend auf den Ergebnissen wird die Idee für einen IGF-Projektantrag in Kooperation mit dem Fraunhofer IKTS vorgestellt. T2 - Sitzung des GAV-Forschungsbeirates CY - Iserlohn, Germany DA - 18.09.2019 KW - Deckschichtbildung KW - Gelartige Elektrolyte KW - Korrosionsprüfung KW - Zinkdeckschichten KW - Corrosion testing KW - Gel-type electrolytes KW - Layer formation KW - Zinc coatings PY - 2019 AN - OPUS4-49036 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heise, Svenja T1 - Normentwurf für ein Prüfverfahren zur Bestimmung von Deckschichtwiderständen an Zinküberzügen mittels gelartiger Elektrolyte (WIPANO - GELELEK) N2 - Der Vortrag stellt das WIPANO-Vorhaben GELELEK vor. Zu Beginn wird die Problemstellung und Projektidee kurz erläutert. Anschließend wird ein Überblick über die Projektpartner, Projektziele und Arbeitsschritte gegeben, sowie die ausgewählten Probenbleche vorgestellt. Abschließend wurde noch eine Einladung zur Teilnahme am projektbegleitenden Ausschuss ausgesprochen. T2 - Sitzung des GAV-Forschungsbeirates CY - Iserlohn, Germany DA - 18.09.2019 KW - Deckschichtbildung KW - Gelartige Elektrolyte KW - Korrosion KW - Zinküberzüge PY - 2019 AN - OPUS4-49038 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lehmann, Jens T1 - ISER Merkblatt 833 - Edelstahl Rostfrei in Erdböden - Aus Sicht des Korrosionsschutzes N2 - Der Einsatz von Edelstahl Rostfrei in Böden wird nur in wenigen Regelwerken behandelt, somit müssen sich Anwender und mPlaner auf Erfahruzngen und Studien stützen um Hilfestellung zum Beispiel zur Werkstoffauswahl zu erhalten. Der Vortrag stellt das von der BAM und der ISEr überarbeiteet Merkblatt 833 vor, welches den Einsatz von Edelstahl Rostfrei im Erdboden bahandelt. T2 - Informationsstelle Edelstahl Rostfrei - Kursleiter Fortbildung 2019 CY - Kalkar, Germany DA - 23.09.2019 KW - Nichtrostender Stahl KW - Korrosion KW - Erdboden PY - 2019 AN - OPUS4-49108 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe T1 - Schwingfestigkeit und Bruchmechanik N2 - Der Vortrag behandelt in grundsätzlicher weise die Anwendung bruchmechanischer Methoden auf die rechnerische Ermittlung der Wöhlerkurve. Dabei werden die Besonderheiten des Kurzrisswachstums (Notwendigkeit der elastisch-plastischen Beschreibung der zyklischen Rissspitzenbelastung, gradueller Aufbau des Rissschlißphänomens) ebenso diskutiert wie das Problem des Mehrfachrissewachstums und Rissarrest. Die Ausführungen werden an einem Beispiel illustriert. T2 - Sitzung des FKM - Fachkreises "Bauteilfestigkeitä2 CY - Frankfurt/M., Germany DA - 05.09.2019 KW - Schwingfestigkeit KW - Bruchmechanik KW - Rissarrest KW - Kurzrisswachstum PY - 2019 AN - OPUS4-49085 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - von Oertzen, Alexander T1 - New Standardisation Tasks under the European Explosives Directive: Electronic Detonators, On-site Mixed Explosives N2 - Several decades have passed since the initial drafting of the European standards for explosives subject to European Directive 2014/28/EU, and this field as experienced some substantial technical innovations. While at the turn of the millenium the concept of electronic detonators had just been conceived, and it is mentioned in a Technical Specification, today electronic detonators exist in many variants, also regarding communication means between shotfirer and the detonating cap. Questions regarding safe functioning and prevention of inadvertent ignition have to be asked in a quite different way, where delicate electronic circuits are used, and where information is transmitted by radio waves. In addition, the safety of functioning is partly found in software components and the corresponding standards need to be reviewed thoroughly on these grounds. A different but in recent times more and more popular technology, is the on-site production of explosives, being mostly emulsion explosives, ANFO, or combined products. Also here software in the machinery is starting to play an important role. The on-site produced explosive must fulfil safety requirements and has to be, in addition, quality controlled. This cannot solely be left to the hopefully proper design of the software and machinery, but needs to be made accessible to verification. Since this area seems broader in approach, it is not going to be addressed by a new standard. The state of the art technology shall be described in a Technical Specification with a perspective from requirements of the above mentioned European Directive. T2 - EFEE 10th anniversary World Conference on Explosives and Blasting CY - Helsiniki, Finland DA - 15.09.2019 KW - Standardisation KW - Harmonised Standards KW - Technical Specification KW - Electronic Detonators KW - On-site mixed Explosives PY - 2019 AN - OPUS4-49106 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stephan-Scherb, Christiane T1 - Elucidation of Surface Degradation Phenomena By In Situ X-ray techniques N2 - Presentation of in situ and real time approaches to study high temperature oxidation phenomena by adavnced X-ray techniques. Application to the analysis of degradation mechanisms of chemical complex alloys and high entropy alloys was presented. T2 - SPP 2006 Hot Topic Meeting "Large Scale Facility Based Techniques CY - Helmholtz-Zentrum Berlin für Materialien und Energie, Germany DA - 26.09.2019 KW - High entropy alloys KW - Diffraction KW - In situ KW - Oxidation PY - 2019 AN - OPUS4-49134 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Langklotz, U. T1 - FT-IR spectroscopy of corrosion products formed on zinc under atmospheric conditions N2 - Zinc materials are of high importance in the field of corrosion protection. For example, almost half of the annual production of zinc is used as anti-corrosive layer for steel components, particularly under atmospheric conditions. The corrosion protection is frequently ascribed to zinc carbonate species with low solubility which form on the metal surface under atmospheric conditions. Due to the technological importance and wide use of zinc materials, its corrosion behavior and the formation of reaction products has been intensively investigated over decades. Assuming atmospheric corrosion conditions, an initial native passive film of few nanometers thickness forms spontaneously. It consists of zinc oxide and hydroxide, transforming into various species in dependence of the surrounding atmospheric conditions. This study focusses on the investigation of corrosion product layers on massive titanium-zinc sheets, formed during short- and mid-term exposure experiments by Fourier-transformed infrared spectroscopy. This method enables the investigation of extremely thin native passive films which form during the initial hours of exposure. Furthermore, aged surface layers are analyzed which were formed by transformation of initial passive layers over the time of several weeks. The spectroscopic investigations are complemented by scanning electron microscopy (SEM/EDX) in order to obtain information on the chemical composition and morphology of the corrosion products. The combination of both methods offers a comprehensive view on the processes occurring in the early stages of zinc corrosion. T2 - EUROCORR 2019 CY - Sevilla, Spain DA - 09.09.2019 KW - Zinc coatings KW - FT-IR KW - Layer formation PY - 2019 AN - OPUS4-49132 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thünemann, Andreas T1 - A look inside nanoparticles N2 - Small-angle scattering is the method of choice when it comes to obtaining information about the interior of nanoparticles. The aim is to make nanotechnology safer. While the use of small-angle neutron scattering (SANS) is limited to a few instruments in the world, small-angle X-ray scattering (SAXS) is widely accessible, with an upward trend. The example of core-shell particles shows how simple their analysis is with data from an Anton Paar laboratory system. Here, SAXS is a central tool for the development of new reference materials based on poly(methyl) acrylate-PVDF core-shell particles. The dimensions of the cores and shells can be precisely determined. A detailed analysis makes it possible to show that the cores contain fluorinated and nonfluorinated polymers, whereas the shell consist only of PVDF. This core-shell particles with a diameter around 40 nm show a significantly higher PVDF beta phase content than the PVDF homopolymer when using an emulsion polymerization technique. This finding is of importance with respect to applications in electroactive devices. T2 - SAXS excites: International SAXS Symposium 2019 CY - Graz, Austria DA - 24.09.2019 KW - Small-angle X-ray scattering KW - SAXS KW - Nanoplastics PY - 2019 AN - OPUS4-49126 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -