TY - CONF A1 - Trappe, Volker A1 - Nielow, Dustin T1 - Fatigue loading of sandwich shell test specimens with simulated production imperfections and in-situ NDT N2 - A shell test bench was developed at BAM 5.3 which allows for static and fatigue testing of curved fiber-reinforced plastic (FRP) structures, during which in-situ the damage state can be non-destructively inspected by thermography and strain-field measurement techniques. Sandwich shell specimens with typical wind turbine blade manufacturing defects were designed and tested. The tested imperfections show a fairly significant reduction (up to 90%) of the shell test specimens‘ lifetime, depending on the type of imperfection. Using the in-situ NDT methods incorporated in the shell test bench, the location and cycle time of the initial defects and the damage evolution was investigated. T2 - 7. International Conference on Fatigue of Composites CY - Vicenza, Italy DA - 04.06.2018 KW - Fatigue of sandwich shell structures KW - Non-destructive testing KW - Wind turbine blades PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-501275 SP - 1 EP - 7 AN - OPUS4-50127 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mirtsch, Mona A1 - Pohlisch, Jakob A1 - Blind, K. T1 - International Diffusion of the Information Security Management System Standard ISO/IEC 27001: Exploring the Role of Culture N2 - In the wake of digitalization, organizations are increasingly exposed to risks associated with security breaches and must take measures to preserve the confidentiality, integrity, and availability of information, and to ensure business continuity. The international standard ISO/IEC 27001 assists organizations in setting up, maintaining and continuously improving their information security management systems. However, despite high growth rates, its international diffusion rates are quite heterogeneous. This paper explores why the diffusion of the international management system standard ISO/IEC 27001 differs across countries. We classify the adoption of ISO/IEC 27001 as a ‘preventive organizational innovation’ and draw from diffusion studies of other management system standards and information security research to develop a set of hypotheses. These relate to the impact of cultural dimensions and national ICT development. We use a negative binomial regression model with panel data covering 57 countries over a 12-year period from 2006 to 2017 to test our hypotheses. We find that the cultural dimensions future orientation, power distance, and institutional collectivism as well as high ICT development are driving factors for the diffusion of ISO/IEC 27001. We derive policy recommendations and avenues for future research. T2 - Twenty-Eighth European Conference on Information Systems (ECIS2020) – A Virtual AIS Conference CY - Online meeting DA - 15.06.2020 KW - Information security KW - International diffusion KW - Standards KW - Management system standards KW - ISO/IEC 27001 KW - Preventive innovations KW - Culture KW - GLOBE KW - ICT development index PY - 2020 SP - RP 88 AN - OPUS4-50919 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Schilling, Markus T1 - Environmental Stress Cracking (ESC) and Slow Crack Growth (SCG) of PE-HD induced by external fluids N2 - High-density polyethylene (PE-HD) is widely used as a packaging material. Typical applications are pipes and containers for storage and transport of dangerous goods. For these applications, the understanding of the craze-crack damage mechanisms slow crack growth (SCG) and environmental stress cracking (ESC) is of importance. Since these mechanisms are considered to be the major causes of failure, their understanding is essential for inspection and release of those materials. A well-established test method for the assessment of these damage mechanisms is the full-notch creep test (FNCT). It is used in this study for a detailed investigation of crack propagation phenomena in PE-HD container materials under the influence of different fluids such as air, water and aqueous detergent solutions (Arkopal N 100) as well as biodiesel and diesel. Based on the results of the FNCT, a classification scheme of different fluids is proposed, which allows for an assignment of the respective damage mechanisms. Hereby, it is differentiated between (i) inert, (ii) purely surface-active and (iii) additionally sorptive, bulk-active fluids with respect to SCG. If the test fluid changes the intrinsic properties (at the surface or in the bulk), the damage mechanism is addressed to ESC behavior. In FNCT investigations, stress, temperature and specimen geometry were varied systematically. In addition to the time to failure as common measure for the resistance of a PE-HD type against crack propagation, specimen elongation was considered in detail. Several imaging techniques were applied for fracture surface analysis of specimens tested in FNCT to gain novel information on SCG and ESC behavior. From height profiles obtained by laser scanning microscopy (LSM) and information on surface structures from scanning electron microscopy (SEM), indicators for the differentiation of the crack propagation mechanisms could be derived. Based on the LSM data, an algorithm for the distinction between ductile shear deformation and brittle crack growth as dominating failure mechanism was developed. Imaging techniques were also used for determination of crack propagation rates, which were related to time-resolved FNCT elongation data. From the time-resolved determination of crack lengths of partly damaged FNCT specimens, an increasing length of craze zone with a progressively propagating crack was revealed for the first time. This relation of crack and craze zones was specified by fracture mechanical considerations. N2 - Polyethylen hoher Dichte (PE-HD) wird als Werkstoff für Rohre und Behälter für den Transport und zur Lagerung von Gefahrgütern verwendet. Für die Beurteilung und technische Freigabe dieser Materialien ist das Verständnis der beiden Schädigungsmechanismen „langsames Risswachstum“ (engl.: „slow crack growth“, SCG) und „umgebungsbedingter Spannungsriss“ (engl.: „environmental stress cracking“, ESC) essentiell. Eine etablierte Prüfmethode zur Bewertung dieser Schädigungsmechanismen ist der Full-Notch Creep Test (FNCT), der in dieser Arbeit zur systematischen Untersuchung des Risswachstums in PE-HD Behältermaterialien unter Einwirkung von Luft, Wasser und wässrigen Netzmittellösungen (Arkopal N 100) sowie Biodiesel und Diesel verwendet wird. Aus den Ergebnissen des FNCT wird ein Klassifikationsschema für Fluide vorgeschlagen, welches ebenfalls eine Zuordnung zu den Schädigungsmechanismen erlaubt. Hierbei wird in (i) inerte, (ii) rein oberflächen-aktive und (iii) zusätzliche sorptive, volumen-aktive Fluide hinsichtlich des langsamen Risswachstums (SCG) unterschieden. Wenn ein Fluid lokal die intrinsischen Materialeigenschaften des Polymers verändert, wird der Schädigungsmechanismus dem umgebungsbedingten Spannungsriss (ESC) zugeordnet. Bei den FNCT-Untersuchungen wurden die mechanische Spannung, die Temperatur und die Prüfkörpergeometrie systematisch variiert. Zusätzlich zur Standzeit wurde die Prüfkörperdehnung zeitabhängig erfasst. Aus einer erweiterten Bruchflächenanalyse konnten neuartige Informationen über SCG und ESC erhalten werden. Hierzu wurden verschiedene Bildgebungsverfahren verwendet. Insbesondere wurden mit Laserscanningmikroskopie (LSM) Höhenprofile und mit Rasterelektronenmikroskopie (REM) Oberflächeninformationen zur Charakterisierung der Rissfortschrittsmechanismen erhalten. Auf Basis der LSM wurde unter Zuhilfenahme von Höhenprofildaten ein Algorithmus zur Unterscheidung zwischen duktiler Scherverformung und sprödem Risswachstum als dominierende Schädigungsmechanismen entwickelt. Die aus den bildgebenden Verfahren ermittelten Rissfortschrittsraten konnten mit den Daten der während des FNCT erfassten Dehnung der Prüfkörper in Beziehung gesetzt werden. Weiterhin wurde mithilfe von zeitaufgelösten Risslängendaten erstmals eine direkte Korrelation der Risslänge zu vorgeschädigten, fibrillierten Bereichen (Crazes) im PE-HD Prüfkörper während des FNCT nachgewiesen. Demnach vergrößert sich die Craze-Länge linear mit zunehmender Risslänge. Dieser Zusammenhang zwischen Riss- und Craze-Längen wurde auf mathematisch, bruchmechanischer Grundlage bestätigt. KW - High-density polyethylene (PE-HD) KW - Full-Notch Creep Test (FNCT) KW - Slow crack growth (SCG) KW - Environmental Stress Cracking (ESC) KW - Biodiesel KW - Diesel KW - Crack propagation analysis KW - Fracture Surface Analysis KW - Test Improvement KW - Imaging PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:tuda-tuprints-115443 DO - https://doi.org/10.25534/tuprints-00011544 SP - 1 EP - 212 CY - Darmstadt AN - OPUS4-50941 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schoknecht, Ute T1 - Gelungene Zusammenarbeit im Projekt "Beregnete Fassaden" N2 - Im Artikel wird dargestellt, mit welchen Zielstellungen die Projektgruppe "Beregnete Fassaden" zur Thematik der Freisetzung von Bioziden aus Fassaden zusammenarbeitet, wie die Arbeit der Gruppe organisiert ist und welche positiven Erfahrungen bzw. Grenzen es dabei gibt. KW - Fassaden KW - Biozide KW - Freisetzung PY - 2020 UR - https://www.wirsindfarbe.de/service-publikationen/wir-sind-farbe-das-magazin/wir-sind-farbe-ausgabe-9 IS - 9 SP - 30 EP - 31 PB - Verband der deutschen Lack- und Druckfarbenindustrie e.V. CY - Frankfurt am Main AN - OPUS4-50992 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koclega, Damian A1 - Radziszewska, A. A1 - Kranzmann, Axel A1 - Marynowski, P. A1 - Wozny, K. T1 - Morphology and chemical composition of inconel 686 after high-temperature corrosion N2 - The work presents the microstructure, chemical composition and mechanical properties of Inconel 686 coatings after high - temperature corrosion in environment of aggressive gases and ashes. To produce the Ni - based coatings the QS Nd:YAG laser cladding process was carried out. As the substrate used 13CrMo4-5 boilers plate steel. Ni - base alloys characterize the excellent high-temperature corrosion resistance, good strength and ability to work in aggressive environments. Formed clad were characterized by high quality of metallurgical bonding with the substrate material and sufficiently low amount of the iron close to the clad layer surface. After corrosion experiment the oxide scale on the substrate and clad created. The scale on 13CrMo4-5 steel had 70 μm thickness while the scale of the clad had less than 10 μm. The microstructure, chemical composition of the obtained clad and scales were investigated by scanning electron microscope (SEM) and electron probe microanalyzer (EPMA) equipped with the EDS detectors. T2 - 27th International conference on metallurgy and materials CY - Brno, Czech Republic DA - 23.05.2018 KW - laser cladding KW - Inconel 686 KW - High - temperature corrosion KW - Aggressive environment KW - Oxide scale PY - 2018 SP - 1010 EP - 1016 AN - OPUS4-49660 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Haller, T. A1 - Völker, Christoph A1 - Hartmann, T. T1 - Machine learning based multi-sensor fusion for the nondestructive testing of corrosion in concrete N2 - Half-cell potential mapping (HP) is the most popular non-destructive testing method (NDT) for locating corrosion damage in concrete. It is generally accepted that HP is susceptible to environmental factors caused by salt-related deterioration, such as different moisture and chloride gradients. Additional NDT methods are able to identify distinctive areas but are not yet used to estimate more accurate test results. We present a Supervised Machine Learning (SML) based approach to data fusion of seven different signal features to obtain higher quality information. SMLs are methods that explore (or learn) relationships between different (sensor) data from predefined data labels. To obtain a representative, labelled data set we conducted a comprehensive experiment simulating the deterioration cycle of a chloride exposed device in the laboratory. Our data set consists of 18 measurement campaigns, each containing HP, Ground Penetrating- Radar, Microwave Moisture and Wenner resistivity data. We compare the performance of different ML approaches. Many outperform the best single method, HP. We describe the intrinsic challenges posed by a data-driven approach in NDT and show how future work can help overcome them. T2 - SMAR2019 - 5th International Conference on Smart Monitoring, Assessment and Rehabilitation of Civil Structures CY - Potsdam, Germany DA - 27.08.2019 KW - Machine Learning KW - NDT KW - Half-Cell Potential Mapping KW - Corrosion KW - Reinforced Concrete KW - Data Fusion PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-498563 UR - http://www.ndt.net/?id=24890 VL - 25 IS - 1 SP - 24890-1 EP - 24890-8 PB - NDT.net CY - Kirchwald AN - OPUS4-49856 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Alfeld, M. A1 - Eckhardt, H.-S. A1 - Kraft, J. A1 - Maiwald, Michael A1 - Meermann, Björn A1 - Merz, K. A1 - Prikler, S. A1 - Richert, J. A1 - Steiner, G. A1 - von Tümpling, W. T1 - Trendbericht Analytische Chemie N2 - Zusätzlich zu Methodenentwicklung, Miniaturisierung und Kopplungsverfahren zeigen sich die Hyperspektroskopie zusammen mit Imaging‐Verfahren, der Einzelmolekülnachweis und der Einsatz von 3‐D‐Druckern als neue Schwerpunkte. Hinzu kommen künstliche Intelligenz bei Sensoren, Bildgebungsverfahren und Prozesssteuerung sowie die Vernetzung von Analyse‐ und Laborgeräten. Trends und Forschungsthemen aus der analytischen Chemie, zusammengestellt von elf Autoren, koordiniert von Günter Gauglitz. KW - Multielementanalytik KW - Multimodale Analytik KW - Kristallolgraphie KW - Prozessanalytik KW - Prozessindustrie KW - Industrielle Analytik KW - Chemometrik KW - Chemometrie PY - 2020 DO - https://doi.org/10.1002/nadc.20204095786 SN - 1868-0054 VL - 68 IS - 4 SP - 52 EP - 60 PB - Wiley CY - Weinheim AN - OPUS4-50609 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bettge, Dirk A1 - Bohraus, Stephan A1 - Schmidt, Rüdiger A1 - Portella, Pedro Dolabella ED - Lohrmann, M. ED - Rettenmayr, P. T1 - Aufbau einer fraktographischen online-Datenbank N2 - Fraktographischen Daten aus Schadensanalysen, Vergleichsversuchen und Vorhaben könnten der Fachöffentlichkeit im Bereich Fraktographie zur Verfügung gestellt werden, sofern das Urheberrecht es zulässt und außerdem ein geeignetes Medium existiert. Ein solches Medium könnte eine offene fraktographische online-Datenbank sein. Eine solche wird im Rahmen der AG Fraktographie im DVM-DGM Gemeinschaftsausschuss "Rasterelektronenmikroskopie in der Materialprüfung" zurzeit erarbeitet. T2 - Metallographietagung 2013 CY - Friedrichshafen, Germany DA - 18.09.2013 KW - Datenbank KW - Fraktographie KW - Schadensanalyse PY - 2013 SN - 978-3-88355-398-6 VL - 45 SP - 19 EP - 24 PB - Inventum CY - Bonn AN - OPUS4-50598 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Millar, Steven A1 - Gottlieb, Cassian A1 - Wilsch, Gerd A1 - Günther, Tobias A1 - Völker, Tobias T1 - Chemische Zustandsanalyse von Stahlbetonbauwerken mit der laserinduzierten Plasmaspektroskopie (LIBS) N2 - Die chemische Analyse von Beton gehört bei der Ermittlung des Ist-Zustandes von Stahl- und Spannbetonbauwerken zu den grundlegenden Untersuchungen bei der Zustandserfassung. Der tiefenabhängige Chloridgehalt sowie der Karbonatisierungsfortschritt müssen bei der Bewertung des Ist-Zustandes, beim Instandsetzungsbedarf und ggf. bei der Planung eines erforderlichen Instandsetzungskonzeptes mit einbezogen werden. Seit Mitte der 1990er Jahre wird an der Bundesanstalt für Materialforschung und -prüfung die laserinduzierte Plasmaspektroskopie (engl. Laser-induced Breakdown Spectroscopy) – kurz LIBS – stetig für die chemische Analyse von Beton weiterentwickelt. In diesem Beitrag wird der aktuelle Stand der Forschung/ Technik und der Normungsarbeit präsentiert, sowie zukünftig mögliche Anwendungen vorgestellt. Mit den aktuellen LIBS-Systemen (mobiles LIBS-System sowie kommerziell erhältliche Laborsysteme) ist es möglich den Chloridgehalt ortsaufgelöst in wenigen Minuten zu quantifizieren, sogenannte Elementlandkarten zu erstellen und somit die Elementverteilung innerhalb des Betons zu visualisieren. Durch das Scannen eines Bohrkernquerschnittes und der simultanen Erfassung von mehreren Elementen mit einer Messung, ist es zudem möglich, die Gesteinskörnung in den Messdaten zu identifizieren und den Chloridgehalt auf die Zementsteinmatrix zu beziehen. Fehlerquellen aus der Umrechnung der betonbezogenen Chloridgehalte können dadurch minimiert werden. Neben den Grundlagen von LIBS werden vor allem aktuelle Praxisbeispiele vorgestellt, die die aktuellen Möglichkeiten des Verfahrens veranschaulichen. T2 - 9. Kolloquium Parkbauten CY - Esslingen, Germany DA - 04.02.2020 KW - LIBS KW - Chemische Analyse KW - Spektroskopie KW - Beton PY - 2020 UR - https://elibrary.narr.digital/article/99.125005/kpb202010305 SN - 2510-7763 VL - 9 IS - 1 SP - 305 EP - 319 AN - OPUS4-50615 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Maiwald, Michael T1 - The internet of things in the lab and in process - The digital transformation challenges for the laboratory 4.0 T1 - Das Internet of Things in Labor und Prozess - Herausforderungen des digitalen Wandels für das Labor 4.0 N2 - It is a fact that much of the time spent on analytical laboratory instrumentation these days goes into system maintenance. Digital transformation could give us more time again for creativity and our actual laboratory work – if we shape it the right way. N2 - Fakt ist: Einen Großteil der Zeit, der an analytischen Laborgeräten verbracht wird, nimmt heute die Systempflege in Anspruch. Der digitale Wandel kann uns endlich wieder mehr Zeit für Kreativität und die eigentliche Laborarbeit geben – wenn wir ihn richtig gestalten. KW - Lab of the Future KW - Digitalisation KW - Automation KW - Data Analysis KW - Instrument Communication KW - Labor der Zukunft KW - Digitale Transformation KW - Automatisierung KW - Gerätekommunikation PY - 2020 IS - 4 SP - 1 EP - 3 PB - Lumitos AG CY - Darmstadt AN - OPUS4-50618 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Schukar, Vivien A1 - Bartholmai, Matthias A1 - Beck, Uwe T1 - Abschlussbericht zum DFG-Projekt „FAMOS²“ FAser-basierter Magneto-Optischer SchichtSensor N2 - Der Mangel an Anwendungsrichtlinien und Validierungsverfahren für struktur-eingebettete faseroptische Dehnungssensoren, insbesondere auf Faser-Bragg-Gitter (FBG)-Basis, führte bislang dazu, dass diese Sensoren trotz ihrer hervorragenden Eigenschaften im Bereich der kommerziellen Material- und Strukturüberwachung nur in geringem Umfange eingesetzt wurden. Fragen zur Degradation der Sensoren unter Beanspruchung, Alterung durch klimatische Einflüsse und Enthaftung infolge Belastung der Struktur konnten bisher nur theoretisch simuliert oder anhand exemplarischer Proben für einzelne einflussnehmende Parameter im Labor untersucht werden. Die Erfassung des Sensorverhaltens im Bauteil unter komplexen Umwelteinflüssen während des Bauteilbetriebes, um damit eine Aussage zur Zuverlässigkeit der Sensormessdaten zu gewinnen, war bisher nicht möglich. Im Forschungsprojekt FAMOS² wurde deshalb von 2014 bis 2018 die Realisierung eines Autodiagnoseverfahrens für faseroptische Dehnungssensoren erarbeitet, um die Funktionszuverlässigkeit und Langzeitstabilität der Sensoren während des Bauteilbetriebes innerhalb einer Bauteilstruktur bewerten zu können. Im Rahmen des Forschungsprojektes wurde gezeigt, dass ein FBG-Sensor mit einer speziell angepassten magnetostriktiven Schicht magnetisch so angeregt werden kann, dass mit einer zugeschnittenen Messmethodik zu jedem Zeitpunkt eine Bewertung der Sensorzuverlässigkeit unter Betriebsbedingungen möglich ist. Die auf den Sensor aufgebrachte magnetostriktive Schicht erzeugt bei Anregung mit einem passenden Magnetfeld eine gepulste, synthetische Dehnung. Diese Dehnung steht in einem definierten Verhältnis zum anregenden Magnetfeld und wird optisch über die Verschiebung der Bragg-Wellenlänge ausgelesen. Die Konstanz dieses Verhältnisses stellt dann ein Maß für die korrekte Funktionsfähigkeit des Sensors dar. Das Beschichtungs-verfahren, das magnetische Anregungs- und optische Ausleseverfahren, wie auch die Validierung des Sensors unter Berücksichtigung faseroptischer Effekte wurden während des Projekts konzeptionell entwickelt, aufgebaut und charakterisiert. Qualitativ kann mit diesem Verfahren zunächst eine Gut-/Schlecht-Beurteilung des Sensors vorgenommen werden. Perspektivisch bietet das Verfahren jedoch auch die Möglichkeit, verschiedene Versagensmechanismen bestimmen und klassifizieren zu können. Es zeichnete sich schon während des Projektverlaufs ab, dass sich aus den erzielten Ergebnissen über das Autodiagnoseverfahren hinaus weitere Anwendungsmöglichkeiten für den Einsatz des kombinierten magnetostriktiv-faseroptischen Sensorprinzips, beispielsweise als reiner Magnetfeldsensor, ergeben. Nach Abschluss dieses Forschungsprojekts besteht nun die Möglichkeit, den Funktionszustand faseroptischer Dehnungssensoren jederzeit unabhängig von Alter, Belastung oder Kenntnis eines Referenzzustands zu einem bestimmten Zeitpunkt bestimmen zu können. Aufbauend auf diesen Ergebnissen können weiterführende Forschungen die Messmethodik vertiefend charakterisieren und weitere Anwendungsfälle erschließen. KW - Faser-Bragg-Gitter (FBG) KW - Sensorvalidierung KW - Magnetostriktive Beschichtung KW - Structural Health Monitoring (SHM) PY - 2018 N1 - Das Dokument unterliegt der Vertraulichkeit und kann nicht zugänglich gemacht werden - Projektlaufzeit: 01.04.2014 - 31.07.2018 The document is subject to confidentiality restrictions and cannot be made accessible - project runtime: 01.04.2014 - 31.07.2018 SP - 1 EP - 28 AN - OPUS4-50418 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Beck, Uwe A1 - Stockmann, Jörg M. T1 - AiF Projekt GmbH, KONTRAST – schnell, sicher, sichtbar N2 - Das Projekt KONTRAST adressiert die Qualitätskontrolle (QC) zur Erfassung nano- und mikroskaliger Belegung/Degradation mittels abbildender Ellipsometrie (IE). Das BAM-Teilvorhaben beinhaltet das Screening von Benchmark-Materialsystemen und die Validierung von Messstrategien. Im Ergebnis erfolgte eine Fokussierung auf das im Vergleich zur off Null Ellipsometrie (ONE) aussichtereichere Verfahren der referenzkompensierten Ellipsometrie(RKE), das marktstrategisch in RSE (referenced spectral ellipsometry) umbenannt wurde. Alle Materialsysteme der BAM-Unterauftragnehmer konnten mit IE visualisiert werden, mit dem RSE-System in wesentlich kürzeren Zeiten, auf größeren Flächen, bei vergleichbarer Empfindlichkeit und Auflösung, Komplementärverfahren waren für den schnellen Nachweis nano- und mikroskaliger Belegung nicht konkurrenzfähig, wobei zusätzliche Materialsysteme mit niedrigem Kontrast (SnO:Ni auf Glas bzw. Cr auf Chromstahl) in der BAM hergestellt wurden. Die öffentliche Präsentation des RSE-Prototyps erfolgte auf der ICSE-7 2016 mit der Publikation 2017 in Applied Surface Science. KW - Abbildende Ellipsometrie (IE) KW - Imaging Null Ellipsometrie (INE) KW - Referenced Spectral Ellipsometry (RSE) KW - Oberflächenverunreinigungen KW - Visualisierung bei geringem Kontrast PY - 2017 N1 - Das Dokument unterliegt der Vertraulichkeit und kann nicht zugänglich gemacht werden Projektlaufzeit: 01.10.2014 bis 28.08.2017 The document is subject to confidentiality restrictions and cannot be made accessible Project runtime: 01.10.2014 to 28.08.2017 SP - 1 EP - 16 AN - OPUS4-50420 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, A. A1 - Simkin, Roman A1 - Kranzmann, Axel T1 - Construction of an adiabatic calorimeter for investigation of high tempertarue salt - based phase change material N2 - The commercial usage of latent thermal energy storages primarily depends on the development of a suitable phase change material (PCM). For industrial high temperature applications above 400 °C multicomponent chloride eutectics are promising and therefore discussed seriously. The profound thermodynamic investigation of such eutectics requires a much greater amount of specimen material than conventional calorimeter can handle. Therefore, a special adiabatic calorimeter was developed and designed. With a specimen mass of > 100 g the typical thermodynamic measurements with a commercial calorimeter can be extended by cycle stability measurements, which are often decisive for practical application of PCM. Furthermore, by implementing corrosion specimens inside the calorimeter high temperature corrosion experiments according to ISO 21608 can be performed inside the calorimeter. Adiabatic measuring conditions can be provided by using two separate heating systems. Therefore, the outer “protective system” follows the temperature curve of the inner “measuring system” minimizing the temperature difference between the heating systems and simultaneously preventing heat losses from the measuring systems. T2 - 10th International Conference on Chemical, Biological and Environmental Engineering ICBEE 2018 CY - Berlin, Germany DA - 27.09.2018 KW - Adiabatic calorimeter KW - Thermal energy storage KW - Phase change material KW - Salt eutectics PY - 2018 DO - https://doi.org/10.7763/IPCBEE.2018.V103.6 VL - 103 SP - 21 EP - 28 AN - OPUS4-50363 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, A. A1 - Wolf, M. A1 - Kranzmann, Axel T1 - In-situ testing of corrosion and corrosion fatigue behavior of stainless steels in geothermal environment N2 - In CCS environment (carbon capture and storage) pipes are loaded statically and/or cyclically and at the same time exposed constantly to the highly corrosive hot thermal water. Experimental procedures such as ambient pressure immersions tests, in-situ corrosion fatigue experiments using a flexibly designed corrosion chamber at ambient pressure and a specially designed corrosion chamber at high pressure. Experimental set-ups for push/pull and rotation bending load are introduced. The corrosion behavior and lifetime reduction of high alloyed steels (X46Cr13, 1.4043), (X5CrNiCuNb16-4, 1.4542) and (X2CrNiMoN22-5-3, 1.4462) is demonstrated (T=60 °C, geothermal brine: Stuttgart Aquifer flow rate: 9 l/h, CO2 ). T2 - 10th International Conference on Chemical, Biological and Environmental Engineering ICBEE 2018 CY - Berlin, Germany DA - 27.09.2018 KW - Adiabatic calorimeter KW - Thermal energy storage KW - Phase change material KW - Salt eutectics PY - 2018 DO - https://doi.org/10.7763/IPCBEE.2018.V103.5 VL - 103 SP - 13 EP - 20 AN - OPUS4-50364 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Helmerich, Rosemarie A1 - Moldenhauer, Laura A1 - Voigt, Gerrit A1 - Köppe, E. T1 - Considerations for identification of moisture in building materials using Bluetooth (R) N2 - The vulnerability of low-quality concrete of some bridges to ageing and deterioration while they are exposed to environmental conditions during their service life, influence of growing population and climate changes, is a well-known effect and requires survey. For survey, the development of a low cost, cost-efficient sensor network to be embedded for continuous or attached to the surface for periodic monitoring is essential. Changing ground water conditions, flood or even leakage in fresh or disposal of waste water can lead to in-creased moisture content in building materials and structural elements as walls or floors. Moisture allows the transport of other adverse chemicals that might reduce the durability of structures. The paper presents a feasibility study about the capability of microwave modules as bluetooth® or ZigBee with frequency range at 2,4 GHz to create advanced Wireless Sensor Networks (WSN) for estimation and visualization of moisture distribution in infrastructure assets. It was found that the value of the received signal strength indication (RSSI) depends on the moisture content and can be the basis for the moisture distribution inside a massive structure. The microwave modules may be used to compose networks outside and inside of building materials or structural elements. The higher the number of connections between BLE modules, the more precise and the more distant information can be obtained from the network. Mesh networking was applied to increase the quantitative information. T2 - 9th International Conference on Bridge Maintenance, Safety and Management (IABMAS) CY - Melbourne, Australia DA - 09.07.2018 KW - Structural Health Monitoring KW - Moisture KW - Bluetooth PY - 2018 SN - 978-1-315-18939-0 SN - 978-1-138-73045-8 SP - 2752 EP - 2759 AN - OPUS4-50340 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Vollert, F. A1 - Thomas, Maximilian A1 - Kromm, Arne A1 - Gibmeier, J. T1 - Hot crack assessment of LTT welds using μCT N2 - Investigations on weldability often deal with hot cracking, as one of the most popular failure during weld fabrication. The modified varestraint transvarestraint hot cracking test (MVT) is well known for the assessment of the hot cracking susceptibility of materials. The shortcoming of this approach is that the information is only from the very near surface region, which inhibits access to the characteristic of the hot crack network in the bulk. Here, we report about a new approach, illustrated in the example of low transformation temperature (LTT) weld filler materials, to monitor the entire 3D hot crack network after welding by means of microfocus X-ray computer tomography (μCT). T2 - 10th Conference on Industrial Computed Tomography (iCT 2020) CY - Wels, Austria DA - 04.02.2020 KW - Varestraint testing KW - LTT weld filler materials KW - Hot cracking KW - Welding KW - μCT-analysis PY - 2020 DO - https://doi.org/https://doi.org/10.58286/25121 SN - 1435-4934 VL - 25 IS - 2 SP - 1 EP - 7 PB - NDT.net CY - Kirchwald AN - OPUS4-50341 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Beck, Uwe T1 - Abschlussbericht zum BMWi / MNPQ – Verbundprojekt Quo Vadis Qualitätssicherung von Verbundwerkstoffen und Validierung des Zentrifugenversuchs – eines neuartigen Prüfverfahrens zur Bestimmung von Verbundfestigkeiten N2 - Quo Vadis – Kurzdarstellung Im Fokus von Quo Vadis stehen die Qualitätssicherung von Verbundwerkstoffen und die Validierung der Zentrifugentechnologie zur quantitativen Bestimmung von Festigkeitswerten in der Beanspruchung auf Zug als Mehr-Proben-Prüfverfahren unter Verwendung einer analytischen Zentrifuge (nachfolgend als „Adhesion Analyser LUMiFrac®“ bezeichnet). Zu den Festigkeiten, die mit Hilfe des LUMiFrac® unter Verwendung aufgeklebter Prüfstempel bestimmt werden, gehören die Fügefestigkeit (FF) von Klebverbindungen, die Haftfestigkeit (HF) von Beschichtungen sowie die Verbundfestigkeit (VF) von Faserverbundwerkstoffen. Aufbauend auf zwei Funktionsmustern der analytischen Zentrifuge sollen für die genannten Anwendungsszenarien (FF, HF, VF) in Anlehnung an die geltenden Normen DIN EN 15870 „Klebstoffe – Zugprüfung zur Bestimmung der Zugfestigkeit von Stumpfklebungen“ und DIN EN ISO 4624 „Beschichtungsstoffe – Abreißversuch zur Beurteilung der Haftfestigkeit“ geeignete Prüfstrategien und -abläufe sowie zum Klebprozess kompatible Aufnahmen für den Prüfkörperverbund in der Zentrifuge entwickelt werden. Im Ergebnis des Vorhabens soll ein automatisiertes und validiertes Mehr-Proben-Prüfverfahren zur Qualitätssicherung von Verbundfestigkeiten zur Verfügung stehen, welches neben der Hardware auch eine Software für die angepassten Prüfstrategien in Form von SOPs (standard operating procedures) bereitstellt. KW - Zentrifugentechnologie KW - Mehr-Proben-Prüfverfahren KW - Fügefestigkeit KW - Klebverbindungen KW - Haftfestigkeit KW - Beschichtungen KW - Verbundfestigkeit KW - Zugfestigkeit PY - 2015 N1 - Das Dokument unterliegt der Vertraulichkeit und kann nicht zugänglich gemacht werden Projektlaufzeit: 01.05.2012 bis 31.08.2015 The document is subject to confidentiality restrictions and cannot be made accessible Project runtime: 01.05.2012 bis 31.08.2015 SP - 1 EP - 12 AN - OPUS4-50390 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Beck, Uwe A1 - Krüger, A. T1 - Abschlussbericht für das Kooperationsprojekt zwischen Unternehmen und Forschungseinrichtungen (KF) - Nanoskalige Haftvermittler zur Erhöhung der Haft- bzw. Klebfestigkeit kritischer Verbundsysteme unter Verwendung von ALD-Hybridprozessen N2 - Aufzählung der wichtigsten wissenschaftlich-technischen und anderer wesentlicher Ergebnisse • ALD Abscheidungen auf Polymeren (PE, PP, PTFE) unter Atmosphärendruck und im Vakuum mit Ozon als Oxidationsmittel wurden durchgeführt: - Mit Variation der Schichtdicke - Mit Variation der Zykluszeit - Mit und ohne Ozon Vorbehandlung der Oberfläche • ALD Abscheidungen auf (PE, PP, PTFE) in Vakuum mit O2- und H2-Plasma Vorbehandlung wurden durchgeführt. - Mit Variation der Schichtdicke - Mit Variation der Zykluszeit - Mit und ohne Plasma Vorbehandlung der Oberfläche • Die ALD Prozesse wurden mit in situ Laserellipsometrie untersucht. • Die ALD Schichten wurden für die Haftfestigkeit bei der BAM ausgewerte KW - ALD-Abscheidungen KW - Plasma Vorbehandlung KW - Laserellipsometrie KW - Haftfestigkeit PY - 2017 N1 - Das Dokument unterliegt der Vertraulichkeit und kann nicht zugänglich gemacht werden - The document is subject to confidentiality restrictions and cannot be made accessible - Projektlaufzeit: 01.07.2015-30.06.2017 - Project runtime: 01.07.2015-30.06.2017 SP - 1 EP - 17 AN - OPUS4-50386 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hampel, U. A1 - Schütze, A. A1 - Rädle, M. A1 - Rück, T. A1 - Krawczyk-Becker, M. A1 - Musch, T. A1 - Maiwald, Michael A1 - Fröhlich, H. J. A1 - Zeck, S. T1 - Positionspapier Sensorik für die Digitalisierung chemischer Produktionsanlagen N2 - Die chemische Industrie steht derzeit, wie viele andere Industriebereiche, vor den Herausforderungen einer Digitalisierung der Produktion. Sie ist der Schlüssel für die Flexibilisierung von Prozessen und Anlagen, für die Verkürzung von Produkteinführungszeiten sowie für den Zuschnitt der Produktion auf wechselnde Nachfrage und kürzere Produktlebenszyklen. Die Messtechnik und Sensorik spielt neben der intelligenten Datenverarbeitung eine Schlüsselrolle für die Digitalisierung. Flexiblere Anlagen benötigen Sensorik zur Überwachung des Anlagenzustandes, zur Früherkennung nicht bestimmungsgemäßer Betriebszustände sowie für eine bedarfsgerechte Wartung. Da die Entwicklung neuer und verbesserter Messtechnik und Sensorik grundlegend aus verschiedenen Richtungen gedacht werden muss, haben sich Akteure aus verschiedenen Branchen zusammengetan und dieses Positionspapier erstellt. Es basiert auf einer grundlegenden Analyse des Ist-Stands sowie des Bedarfs der Industrie, die unter anderem auf einem eigens dafür durchgeführten Workshop mit Sensorentwicklern, Anlagenherstellern sowie Anlagenbetreibern am 18. Juni 2019 bei der DECHEMA in Frankfurt a. M. diskutiert wurden. Diese Aktivitäten wurden maßgeblich von der Initiative Wanted Technologies der ProcessNet sowie dem AMA Verband für Sensorik und Messtechnik e.V. initiiert. KW - Prozessindustrie KW - Smarte Sensoren KW - Prozessanalytik KW - DECHEMA KW - Positionspapier PY - 2020 UR - https://dechema.de/Sensorik SP - 1 EP - 20 PB - DECHEMA CY - Frankfurt am Main AN - OPUS4-50403 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Reiche, I. A1 - Landsberger, B. A1 - Frauendorf, A1 - Plarre, Rüdiger A1 - Adler, C. A1 - Zender, J. T1 - Innovative Untersuchungsmethoden zur nachhaltigen Wirksamkeit modellhafter Anoxia-Behandlung gegen Insektenbefall an national bedeutsamen Kulturgütern der Sammlungen der Stiftung Preußischer Kulturbesitz (DBU AZ 31865-45) N2 - Anoxische Objektbehandlungen gegen Schädlingsbefall stellen eine besonders materialverträgliche und umweltschonende Alternative zu chemischen Bekämpfungsverfahren dar. Die Wirksamkeit hängt jedoch von der Dauer, dem Restsauerstoffgehalt sowie der Temperatur und Feuchtigkeit ab. Unterschiedliche Arten von Schadinsekten sind verschieden tolerant gegenüber sauerstoffarmen Bedingungen. Insbesondere bei Behandlungsbedingungen von unter 24° C und mehr als 0,5 % Restsauerstoffgehalt stößt das Verfahren an die Grenze der Zuverlässigkeit. In Versuchsreihen unter standardisierten Bedingungen erwiesen sich insgesamt 12 von 34 im Projekt untersuchte Insektenarten hierbei als widerstandsfähig. Davon als besonders tolerante Arten sind Hylotrupes bajulus, Lasioderma serricorne, Trogoderma parabile und Mezium affine zu nennen. Mit dem entwickelten UWB-Sensoriksystem können durch elektromagnetische Wellen Bewegungen von Schädlingen innerhalb geschlossener Holzobjekte berührungslos erfasst werden. Voraussetzung für die eindeutige Detektion der Schädlingsaktivität ist neben der digitalen Signalverarbeitung zur Filterung und Extraktion des Nutzsignals, die genügend hohe Eindringtiefe, die ausreichend ist, wenn Schädlingsvorkommen häufig dicht unter der Holzoberfläche gelegen sind. Die Versuchsergebnisse haben gezeigt, dass bereits eine einzelne Trockenholztermite der Art Incisitermes marginipennis hinter einer 5 cm dicken Holzplatte aufgespürt werden kann. Somit erscheint das Messsystem potentiell für die Erfolgskontrolle einer Anoxia-Behandlung an Museumsgütern geeignet. KW - Kulturgut KW - Anoxia KW - Museumsschädlinge PY - 2018 SP - 1 EP - 37 AN - OPUS4-49654 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Puthiyaveettil, N. A1 - Kidangan, R. A1 - Unnikrishnakurup, Sreedhar A1 - Krishnamurthy, C. V. A1 - Ziegler, Mathias A1 - Myrach, Philipp A1 - Balasubramaniam, K. T1 - Numerical study of laser line thermography for crack detection at high temperature N2 - The detection of cracks before the failure is highly significant when it comes to safety-relevant structures. Crack detection in metallic samples at high surface temperature is one of the challenging situation in manufacturing industries. Laser thermography has already proved its detection capability of surface cracks in metallic samples at room temperature. In this work a continuous wave (CW) laser use to generate a laser, which is using to scan the metal surface with notch. The corresponding heat distribution on the surface monitored using infrared thermal (IR) camera. A simplified 3D model for laser thermography is developed and validated with experimental results. A dedicated image processing algorithm developed to improve the detectability of the cracks. To understand the dependency of surface temperature, laser power, laser scanning speed etc. in defect detection, we carried out parametric studies with our validated model. Here we Report the capability of laser thermography in crack detection at elevated temperature. T2 - 14th Quantitative InfraRed Thermography Conference CY - Berlin, Germany DA - 25.06.2018 KW - Thermal contrast KW - Laser Thermography KW - FEM KW - Surface cracks KW - NDT PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-499113 DO - https://doi.org/10.21611/qirt.2018.076 SN - 2371-4085 VL - 2018 SP - 685 EP - 686 AN - OPUS4-49911 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simon, Franz-Georg A1 - Barqawi, Haitham A1 - Chubarenko, B. A1 - Esiukova, E. A1 - Putna-Nimane, I. A1 - Barda, I. A1 - Strode, E. A1 - Purina, I. ED - Köppen, S. ED - Reckermann, M. T1 - EI‐GEO environmental impact of geosynthetics in aquatic systems N2 - EI‐GEO is a multinational research project (Germany, Latvia, Russia) funded under the ERA.Net RUS Plus Call 2017. Aim of the project is the investigation whether geosynthetics in hydraulic engineering applications could be a source of microplastics (MPs) and other contaminants to the aquatic environment causing negative effects to aquatic organisms. Whereas the behavior of geosynthetics in landfill engineering is well studied and documented since decades, little is known on application in applications such as coastal protection or ballast layers for wind energy plants. However, due to the rapid expansion of offshore wind energy, rising water levels and more extreme weather conditions as a result of climate change more and more hydraulic engineering projects will be realized in the future. Applied methods are artificial ageing of geosynthetics in environmental simulation chambers, storage of samples under environmental condition for comparison with laboratory simulation, sample characterization by microscopic methods and ecotoxicological testing of water in contact with geosynthetics. In parallel a case study at the Baltic Sea shore at Kaliningrad Oblast (Russia) will be performed. The aim of study is to estimate the level of pollution of the beaches by geosynthetic debris and identify the possible sources. T2 - 3rd Baltic Earth Conference CY - Online meeting DA - 02.06.2020 KW - Geosynthetics KW - Micro plastic KW - Hydraulic engineering PY - 2020 UR - https://www.baltic-earth.eu/hel2020/material/3rd_BalticEarth_Conference_Proceedings.pdf SN - 2198-4247 SP - 151 EP - 152 PB - International Baltic Earth Secretariat Publications CY - Geesthacht AN - OPUS4-50881 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ahmadi, Samim A1 - Hirsch, Philipp Daniel A1 - Lecompagnon, Julien A1 - Hassenstein, Christian A1 - Jung, P. A1 - Caire, G. A1 - Ziegler, Mathias T1 - New techniques in super resolution photothermal imaging for nondestructive testing N2 - In this work we focus on our most recent studies to super resolution (SR) laser thermography. The goal of SR nondestructive testing methods is to facilitate the separation of closely spaced defects. We explain how to combine laser scanning with SR techniques. It can be shown that stepwise as well as continuous scanning techniques are applicable. Finally, we discuss the effect of experimental parameters and im-age processing techniques to find the optimal SR technique which leads to the highest reconstruction quality within laser thermography. T2 - SMSI 2020 Conference CY - Online meeting DA - 22.06.2020 KW - Super resolution KW - Laser thermography KW - Nondestructive testing KW - Laser scanning KW - Photothermal imaging PY - 2020 DO - https://doi.org/10.5162/SMSI2020/C4.1 SP - 169 EP - 170 AN - OPUS4-50895 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ziegler, Mathias A1 - Ahmadi, Samim A1 - Hirsch, Philipp Daniel A1 - Lecompagnon, Julien A1 - Hassenstein, Christian A1 - Thiel, Erik A1 - Pech May, Nelson Wilbur T1 - Using spatial and temporal shaping of laser-induced diffuse thermal wave fields in thermography N2 - The diffuse nature of thermal waves is a fun-damental limitation in thermographic nonde-structive testing. In our studies we investigated different approaches by shaping the thermal wave fields which result from heating. We have used high-power laser sources to heat metallic samples. Using these spatial and temporal shaping techniques leads to a higher detection sensitivity in our measurements with the infra-red camera. In this contribution we show our implementation of shaping laser-induced diffuse thermal wave fields and the effect on the defect reconstruction quality. T2 - SMSI 2020 Conference CY - Online meeting DA - 22.06.2020 KW - Thermal wave KW - Diffusion KW - High-power laser KW - Thermography KW - Spatiotemporal shaping PY - 2020 DO - https://doi.org/10.5162/SMSI2020/C5.1 SP - 179 EP - 180 AN - OPUS4-50897 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Beck, Uwe A1 - Lange, Thorid T1 - Validierung der Oberflächenbehandlung für hochfeste Klebverbindungen und Beschichtungen als durchgehendes Mehr-Proben-Konzept in den Schritten Reinigung, Vorbehandlung, Klebung und Prüfung der Verbundfestigkeit "OKTETT - Acht auf einen Streich" N2 - Aus der Möglichkeit mittels Zentrifugentechnologie bis zu 8 Proben gleichzeitig einer Zugprüfung unter wirklich identischen Bedingungen, schnell über einfaches Einstecken der Proben und unter Ausschluss jeglicher Querkräfte, zu unterziehen , ergab sich für Klebverbindungen erstmals die Möglichkeit einer statistisch abgesicherten Prüfung identischer bzw. einer vergleichend bewertenden Prüfung unterschiedlicher Verbundsysteme. Es war deshalb naheliegend, auch das Aufkleben der Prüfstempel unter möglichst identischen Bedingungen und ebenfalls frei von Querkräften im OKTETT durchzuführen. Außerdem sind beim durchgehenden Handling im OKTETT die identische Vorbehandlung vor dem Kleben, identische Transferzeiten und -bedingungen zwischen den verschiedenen Prozessschritten, eine weitgehend gleichartige Klebstoffaufbereitung und -applikation sowie die bessere Einhaltung von gleichen Verarbeitungs- und Aushärtezeiten der Klebstoffe vor der Prüfung der Verbundfestigkeit für jeweils 8 Proben sichergestellt. Im Ergebnis dieser Überlegungen stellte sich schnell heraus, dass das Mehr-Proben-Kleben unter identischen Bedingungen für in Grenzen unterschiedliche Verbundsysteme eine ungelöste Aufgabenstellung ist. KW - Zentrifugentechnologie KW - Mehr-Proben-Handling KW - Ranking und Statistik KW - Verbundfestigkeit KW - Klebfestigkeit PY - 2014 N1 - Das Dokument unterliegt der Vertraulichkeit und kann nicht zugänglich gemacht werden Projektlaufzeit: 01.10.2014 bis 30.09.2014 The document is subject to confidentiality restrictions and cannot be made accessible Project runtime: 01.10.2014 to 30.09.2014 SP - 1 EP - 14 AN - OPUS4-50429 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Schulz, Wencke T1 - Abscheidung und Charakterisierung von Sol-Gel-Aluminiumoxidschichten auf kommerziellen Kraftwerksstählen zum Schutz gegen Korrosion bei Oxyfuel-Verbrennung N2 - The objective of the present work was the investigation and demonstration of the potential of sol-gel alumina layers as corrosion protection of commercial power plant steels under oxyfuel conditions. The starting points of this work were modified Yoldas-sols which were developed in the BAM-department 5.6. These sols were suitable for the spin-coating method only. The application of coatings on tubes by spin-coating is impossible. Therefore, the chemical composition of the modified Yoldas-sol had to be adapted to the dip- and spray-coating techniques. Exclusively the sol with the composition s-0.52-6-1.5 with a nitrate/aluminium ratio of 0.52; a solid content of 6 wt.% and a PVP (binder) content of 1.5 wt.% could fulfill the necessary criteria: long-term stability; formation of a dense, crack-free and well adhered layer on polished metal surfaces; as well as high protective abilities against corrosion in H2O-CO2-O2-SO2. The commercial power plant steel X20CrMoV12-1 (X20) and the steel X12Cr13 were successfully coated with the sol s-0.52-6-1.5 by means of the dip-coating method. An at least 400 nm thick alumina layer (δ-Al2O3) is necessary to ensure the corrosion protection of these steels. The corrosion of the coated samples compared to that of the uncoated ones was significantly reduced, even after 1000 h of exposure in a H2O-CO2-O2-SO2 atmosphere at 600°C. Sulfur and carbon were not detected at the substrate surface or beneath the coating. Hence the transport of the flue gas components SO2 and CO2 into as well as through the alumina layer could be hindered. The diffusion of the alloying elements (Cr, Mn, Si) into the alumina layer resulted in the formation of mixed oxides like δ-(Al,Cr)2O3. Formation of such phases considerably contributed to the corrosion protection. The long-term stability of the sol s-0.52-6-1.5 and the high protective abilities of the alumina layer on commercial power plant steels provide a good basis for an industrial application. KW - TEM KW - Alumina KW - Coating KW - Oxyfuel KW - Steel KW - High-Temperature Corrosion PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:188-fudissthesis000000102280-0 DO - https://doi.org/10.17169/refubium-6842 SP - 0 EP - 179 PB - Freie Universität CY - Berlin AN - OPUS4-50310 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe T1 - Application of fracture mechanics to welds with crack origin at the weld toe—a review. Part 2: welding residual stresses. Residual and total life assessment N2 - The two-part paper series provides an overview on the state-of-the-art in the application of engineering fracture mechanics to weldments limited to butt and fillet welds with crack initiation at weld toes. In the present second part, one focus is on welding residual stresses, their characteristics and stability under cyclic loading and their effect on structural integrity. Subsequently, features will be addressed which are essential for applying fracture mechanics to overall fatigue life and fatigue strength considerations of weldments. These comprise fatigue life relevant initial crack sizes and multiple crack initiation and Propagation due to various stress peaks along the weld toe. A concept is briefly introduced which covers all these aspects. KW - Fracture mechanics KW - Welding residual stresses KW - Multiple crack propagation KW - Fatigue strength PY - 2020 DO - https://doi.org/10.1007/s40194-019-00816-y VL - 64 IS - 1 SP - 151 EP - 169 PB - Springer AN - OPUS4-50263 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lauschkin, Maik A1 - Bulling, Jannis A1 - Lugovtsova, Yevgeniya A1 - Wasmer, P. A1 - Prager, Jens T1 - Bestimmung von Materialparametern aus dem dispersiven Verhalten geführter Wellen mittels neuronaler Netze N2 - Damit eine Simulationsrechnung, beispielsweise mit einer FEM-Software, eine ausreichend hohe Genauigkeit erreicht, muss vorausgesetzt werden, dass die Modellparameter eine sehr hohe Güte aufweisen. Die genaue Kenntnis der Materialparameter ist dabei von besonderer Bedeutung. Um diese Parameter bestimmen zu können, müssen die verwendeten Werkstoffe messtechnisch charakterisiert werden. Neben anderen Ansätzen sind dafür akustische Verfahren im Ultraschallbereich geeignet. Für dünnwandige und plattenförmige Materialien können aus den sich ausbreitenden geführten Wellen messtechnisch Dispersionskurven bestimmt und aus diesen die Materialparameter abgeleitet werden. Da für die Signalverarbeitung und für Optimierungsaufgaben aktuell zunehmend Machine Learning Tools zum Einsatz kommen, stellt sich die Frage, ob diese Werkzeuge auch für die Ermittlung der Materialparameter aus den gemessenen Dispersionskurven eingesetzt werden können. In der vorgestellten Untersuchung soll ein Convolutional Neural Network aufgestellt werden, welches aus Dispersionsbildern Muster extrahiert und aus diesen eine Schätzung für die Materialparameter ermittelt. Um die Machbarkeit dieses Ansatzes zu prüfen, werden zunächst nur isotrope Materialien betrachtet. Für das Netz werden mit der Scaled-Boundary-Finite-Element-Methode synthetische Daten für das Trainieren und Validieren generiert. Zusätzlich werden die Hyperparameter des neuronalen Netzes variiert, um ein optimales Model für die Schätzung zu finden. Anschließend kann das Netz mit experimentellen Daten getestet und das Ergebnis hinsichtlich der Genauigkeit bewertet werden. T2 - DAGA 2020 - 46. Jahrestagung für Akustik CY - Meeting was canceled DA - 16.03.2020 KW - Machinelles Lernen KW - Geführte Ultraschallwellen KW - Materialcharakterisierung KW - Elastische Konstanten KW - Isotrope Materialien PY - 2020 SN - 978-3-939296-17-1 SP - 571 EP - 574 PB - Deutsche Gesellschaft für Akustik e.V. CY - Berlin AN - OPUS4-50765 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Adamczyk, Burkart A1 - Neuhold, S. A1 - Drissen, P. A1 - Algermissen, D. A1 - Presoly, P. A1 - Sedlazeck, K. P. A1 - Schenk, J. A1 - Raith, J. G. A1 - Pomberger, R. A1 - Vollprecht, D. T1 - Tailoring the FeO/SiO2 ratio in electric arc furnace slags to minimize the leaching of Vanadium and Chromium N2 - Based on recently published research on leaching control mechanisms in electric arc furnace (EAF) slags, it is assumed that a FeO/SiO2 ratio of around one leads to low leached V and Cr concentrations. This ratio influences the mineral phase composition of the slag toward higher amounts of spinel and a lower solubility of calcium silicate phases by suppressing the formation of magnesiowuestite and highly soluble calcium silicate phases. To evaluate this hypothesis, laboratory and scaled up tests in an EAF pilot plant were performed on slag samples characterized by elevated V and Cr leaching and a high FeO/SiO2 ratio. Prior to the melting experiments, the optimum FeO/SiO2 ratio was calculated via FactSageTM. In the melting experiments, the ratio was adjusted by adding quartz sand, which also decreased the basicity (CaO/SiO2) of the slag. As a reference, remelting experiments without quartz sand addition were conducted and additionally, the influence of the cooling rate of the slag was examined. The remelted (without quartz sand) and the remelted modified slags (with quartz sand) were analyzed chemically and mineralogically and the leaching behavior was investigated. The modification of the slags yielded a minimized release of V and Cr, supporting the hypothesis that the FeO/SiO2 ratio influences the mineralogy and the leaching behavior. KW - Electric arc furnace slags KW - FactSage calculations KW - EAF slags KW - Leaching control mechanisms KW - Melting experiments PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-507748 DO - https://doi.org/10.3390/app10072549 VL - 10 IS - 7 SP - 2549 EP - 2565 AN - OPUS4-50774 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kowarik, Stefan A1 - Hicke, Konstantin A1 - Chruscicki, Sebastian A1 - Schukar, Marcus A1 - Breithaupt, Mathias A1 - Lämmerhirt, A. A1 - Pohl, P. A1 - Schubert, M. ED - Cranch, G. ED - Wang, A. ED - Digonnet, M. ED - Dragic, P. T1 - Train monitoring using distributed fiber optic acoustic sensing N2 - We use distributed acoustic sensing to determine the velocity of trains from train vibration patterns using artificial neural network and conventional algorithms. The velocity uncertainty depends on track conditions, train type and velocity. T2 - 27th International Conference on Optical Fiber Sensors (OFS) CY - Meeting was canceled DA - 08.06.2020 KW - Train monitoring KW - Distributed acoustic sensing KW - DAS KW - Distributed fiber optic sensing PY - 2020 SN - 978-1-55752-307-5 DO - https://doi.org/10.1364/OFS.2020.T3.25 SP - 1 EP - 4 PB - The Optical Society (Optical Society of America) CY - Washington D.C., USA AN - OPUS4-50758 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Plarre, Rüdiger ED - Trematerra, P. ED - Conti, B. T1 - Uninvited and welcomed guests in museums – biological management of clothes moths and woodworms N2 - In museums and historic houses clothes, moths (Tineola bisselliella, Tinea pellionella) and the furniture beetle (Anobium punctatum) are the most economically important pests on textiles or wooden artifacts, respectively. Their management is essential to protect cultural ethnological heritage and natural history collections for future generations. Pest management strategies have changed over time. Today, intensive knowledge on pest biology and overall material science are key cornerstones in IPM concepts - also for the Museum environment. The important first steps for sustainable pest management are risk assessment, early pest detection and identification of pathways of infestation. These steps are followed by physical and biological means of control, which have lately gained more importance than applying biocides. Several potentially effective biological enemies of clothes moths and woodworm have been known for a long time, but their promotion for pest control in Museums and historic houses is just beginning. This short review summarizes current concepts of pest life cycle interruption by applying good quarantine and very specific biological measures. The lessons learned from recent faunistic surveys, life-history studies as well as behavioral observations of parasitoids and predators of clothes moths and woodworm may supplement the pest management tool box. The need for further research in this field is addressed. T2 - Working Group Meeting "Integrated Protection of Stored Products" CY - Pisa, Italy DA - 03.09.2019 KW - Corynetes caeruleus KW - Biological control KW - Museum pests KW - Tineola bisselliella KW - Anobium punctatum KW - Apanteles carpatus KW - Baryscapus tineivorus PY - 2020 SN - 978-92-9067-333-0 VL - 148 SP - 266 EP - 273 AN - OPUS4-50543 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Longobucco, M. A1 - Stajanca, Pavol A1 - Curilla, L. A1 - Buczynski, R. A1 - Bugar, I. T1 - Applicable ultrafast all-optical switching by soliton self-trapping in high index contrast dual-core fibre N2 - The improvement potential of ultrafast all-optical switching by soliton self-trapping, using all-solid dual-core fibres with high index contrast, was analyzed numerically. The study of the femtosecond nonlinear propagation was performed based on coupled generalised nonlinear Schrödinger equations considering three fibre architectures: homogeneous cladding all-solid, photonic crystal air-glass, and photonic crystal all-solid. The structural geometries of all three architectures were optimised in order to support high-contrast switching performance in the C-band, considering pulse widths at the 100 fs level. Comparing the three structural alternatives, the lowest switching energies at common excitation parameters (1700 nm and 70 fs pulses) were predicted for the homogeneous cladding dual-core structure. Further optimization of the excitation wavelength and pulse width resulted in lower switching energies and simultaneous improvement of the switching contrasts at the combination of 1500 nm, 75 fs pulses and a fibre length of 43 mm. The spectral aspect in this optimised case expresses a broadband and uniform switching character with a span of over 200 nm and a contrast exceeding 30 dB at more frequency channels. KW - Ultrafast nonlinear propagation KW - All-optical switching KW - Dispersion tailoring of optical fibres KW - Generalised nonlinear Schrödinger equation KW - Dual-core optical fibres KW - Nonlinear directional coupler KW - Soft-glass optical fibres PY - 2020 DO - https://doi.org/10.1088/1612-202X/ab63d8 VL - 17 IS - 2 SP - 025102 PB - Astro Ltd. AN - OPUS4-51042 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Martin, Tina A1 - Nordsiek, S. A1 - Weller, Andreas T1 - Low-frequency impedance spectroscopy of wood N2 - The method of low-frequency impedance spectroscopy has been successfully applied in Earth sciences to characterize soils and rocks. The method uses the diagnosing power of complex electrical resistivity in a frequency range between 1 mHz and 1 kHz. In our study, the potential of this method has been explored for the investigation of wood. We observed remarkable differences in the resulting spectra of complex resistivity for different European and Tropical tree species. The data processing of the acquired low-frequency impedance spectra yields integrating parameters. The comparison of the integrating parameters with the mean pore diameter that has been separately determined for the tropical tree species indicates clear correlations. An additional investigation has revealed remarkable difference in the complex resistivity spectra between oil bearing and non-oil bearing sandal wood. This result and the relations between electrical parameters and structural parameters of wood indicate the prospective potential of low-frequency impedance spectroscopy. KW - Holz KW - Spektroskopie KW - ZfP KW - SIP KW - Nondestructive KW - Low-frequency impedance spectroscopy KW - Spectral induced polarization PY - 2015 DO - https://doi.org/10.5171/2015.910447 SP - 1 EP - 9 PB - IBIMA Publ. AN - OPUS4-34811 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baier, Jennifa A1 - Beck, Uwe A1 - Hidde, Gundula A1 - Hielscher, Stefan A1 - Lange, Thorid A1 - Mix, Renate T1 - Plasmagestützte Oberflächenfunktionalisierung von Polypropylen (PP) N2 - Polypropylen (PP) ist als Niedrigenergie-Polymer ohne nass- und plasmachemische Vorbehandlung weder haftfest zu beschichten noch verbundfest zu kleben. Typische Haft- bzw. Klebfestigkeiten liegen für die unbehandelte Polymeroberfläche bei maximal 0,5 MPa. Hinzu kommt, dass bei der Bestimmung von Haft- und Klebfestigkeiten der unmodifizierten Oberfläche mit großen Streuungen zu rechnen ist, die bezogen auf die Spannweite durchaus einem Faktor 5 entsprechen können. Generell besteht bei Prüfung der Haftfestigkeit mittels Stirnabzugsversuch und bei der Prüfung der Klebfestigkeit die Notwendigkeit eines statistisch validierten Herangehens. Hierzu sind zeitaufwändige Ein-Proben-Klebungen und -Prüfungen nur eingeschränkt geeignet. Zudem ist, insbesondere für geringe Haft- bzw. Klebfestigkeiten, ein querkraftfreies Prüfen Grundvoraussetzung. Im vorliegenden Beitrag werden verschiedenartige plasmagestützte Oberflächenfunktionalisierungen von PP sowie das Mehr-Proben-Konzept zur Klebung/Prüfung von bis zu acht Proben vorgestellt. Dazu werden ein BAM-Funktionsmuster einer Mehr-Proben-Kleb-Vorrichtung und eine kommerzielle analytische Zentrifuge zum Prüfen verwendet. T2 - 24. Workshop des Anwenderkreises Atmosphärendruckplasma "Haftung durch Oberflächenfunktionalisierung" CY - Erfurt, Germany DA - 11.11.2015 KW - Plasmamodifizierung KW - Polypropylen KW - Haftfestigkeit KW - Klebfestigkeit KW - Mehr-Proben-Kleben/-Prüfen PY - 2015 SP - 1 EP - 6 PB - Anwenderkreis Atmosphärendruckplasma CY - Jena AN - OPUS4-34838 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Schoknecht, Ute A1 - Mathies, Helena A1 - Wegner, R. A1 - Uhlig, S. A1 - Baldauf, H. A1 - Colson, B. T1 - Emissions of material preservatives into the environment - realistic extimation of environmental risks through the improved characterisation of the leaching of biocides from treated materials used outdoors N2 - This report supports the implementation of European regulations on biocidal products for the product types 7, 9 and 10. Emission of active substances from material preservatives into environmental compartments can occur due precipitation. Risk characterisations have to be based on estimations of environmental concentrations of target substances leached from material preservatives. Harmonised test procedures are required to predict environmental impact due to leaching. Seventeen treated articles, mainly paints, but also a textile, sealing tapes and sealing masses were investigated by intermittent contact to water to prove suitability of the proposed laboratory test procedure. Parameters that affect leaching of active substances were examined. Further development of a semi-analytical model to describe laboratory leaching data revealed that the model can be improved if changes of the leachability of substances during the test are supposed and integrated. Six paints and a textile were exposed to weathering to compare results from laboratory and field experiments. Similarities between leaching processes in both test approaches were observed. Generally, emissions of active substances are considerably higher in laboratory tests than from vertically installed test specimens exposed to weathering. Competing processes that cause losses of active substances can occur in both tests, but to a higher degree in field experiments. In addition, the influence of meteorological parameters on leaching processes was investigated. Factors besides the amount of driving rain were identified that effect leaching processes by complex interaction. Relations between laboratory and field data were analysed, and the applicability of the semi-analytical model was tested for field data. Guidance documents for leaching tests under laboratory and field conditions were drafted and discussed with experts on EU Level workshop 3./4. July 2014, BAM, Berlin), and are included in this Report. N2 - Dieser Bericht unterstützt die Umsetzung europäischer Regelungen für Biozidprodukte der Produkttypen 7, 9 und 10. Die Freisetzung von Wirkstoffen aus Materialschutzmitteln in Umweltkompartimente kann bei Niederschlagsereignissen auftreten. Risikocharakterisierungen müssen auf Abschätzungen von Umweltkonzentrationen der betrachteten Stoffe basieren. Harmonisierte Testverfahren sind erforderlich, um eine Beeinflussung der Umwelt durch Auswaschung vorherzusagen. Siebzehn behandelte Waren, vor allem Farben, aber auch ein Textil, Dichtungsbänder und Dichtungsmassen wurden bei periodischem Wasserkontakt untersucht, um die Anwendbarkeit des vorgeschlagenen Laborverfahrens nachzuweisen. Faktoren, die Einfluss auf die Auswaschung von Wirkstoffen haben, wurden untersucht. Die Wieterentwicklung eines semianalytischen Modells zur Beschreibung von Auswaschdaten aus Laborversuchen ergab, dass das Modell verbessert werden kann, wenn eine Änderung der Auswaschbarkeit von Substanzen während des Versuchs angenommen und einbezogen wird. Sechs Farben und ein Textil wurden der Witterung ausgesetzt, um Ergebnisse aus Labor- und Freilandversuchen zu vergleichen. Zwischen Auswaschprozessen in beiden Versuchsansätzen wurden Ähnlichkeiten beobachtet. Im Allgemeinen sind die Emissionen von Wirkstoffen im Laborversuch deutlich höher als bei vertikal installierten bewitterten Prüfkörpern. Konkurrierende Prozesse, die Verluste an Wirkstoffen bewirken, können in beiden Testverfahren auftreten, sind aber im Freilandversuch stärker ausgeprägt. Außerdem wurde der Einfluss von meteorologischen Parametern auf Auswaschprozesse untersucht. Es wurden Faktoren identifiziert, die zusätzlich zur Schlagregenmenge durch komplexe Interaktion auf Auswaschprozesse wirken. Beziehungen zwischen Labor- und Frei-landdaten wurden analysiert und die Anwendbarkeit des semianalytischen Modells für Freilanddaten getestet. Leitfäden für Auswaschversuche unter Labor-bzw. Freilandbedingungen wurden entworfen, mit europäischen Experten diskutiert (Workshop 3./4. Juli 2014, BAM, Berlin) und sind Bestandteil dieses Berichts. KW - EU Biocides Regulation KW - Leaching tests KW - Treated articles KW - Modelling KW - EU-Biozidverordnung KW - Auswaschversuche KW - Behandelte Waren KW - Modellierung PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-355139 SN - 1862-4804 SP - 1 EP - 136 AN - OPUS4-35513 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Raupach, M. A1 - Mietz, Jürgen A1 - Nürnberger, U. A1 - Wolff, L. A1 - Bruns, M. A1 - Burkert, Andreas A1 - Eich, Gerd A1 - Menzel, K. T1 - Entwicklung eines kombinierten Schutzsystems für chloridbelastete Betonflächen aus Spritzverzinkung mit abdichtender Beschichtung (Abschlussbericht, AiF 12 818 N/2) N2 - Die Zielsetzung dieses Projektes war es, ein kombiniertes Schutzsystem aus Spritzverzinkung und abdichtendem Oberflächenschutzsystem für die Instandsetzung chloridbelasteter und korrosionsgeschädigter Stahlbetonbauteile zu entwickeln. Dabei soll die Spritzverzinkung der Betonoberfläche in den ersten Jahren nach der Instandsetzung einen kathodischen Korrosionsschutz der Bewehrung bewirken, bis der Beton infolge des Oberflächenschutzsystems soweit ausgetrocknet ist, dass auch ohne kathodischen Schutz praktisch keine Korrosion der Bewehrung mehr stattfinden kann. Anhand von Untersuchungen zur Haftung zwischen Beton, Zinkschicht und verschiedenen Oberflächenschutzsystemen wurde der Aufbau des kombinierten Schutzsystems entwickelt. Es wurden verschiedene OS-11a-Systeme ein OS-13-System sowie zwei Systeme nach ZTV-ING, Teil 7 vor und nach künstlicher Bewitterung untersucht. Anhand der Ergebnisse wurde für das kombinierte System ein OS-11a-System ausgewählt und im weiteren hinsichtlich der Wirksamkeit des kathodischen Schutzes sowie hinsichtlich der Austrocknung des Betons untersucht. Es zeigte sich sowohl an ausgelagerten Prüfköpfen sowie auf einer angelegten Versuchsfläche auf Freideck eines Parkhauses, dass ein wirksamer galvanischer kathodischer Korrosionsschutz der Bewehrung nur bei sehr hohen Chloridgehalten (4 M.-% bezogen auf den Zementgehalt) erreicht werden kann. Bei geringeren untersuchten Chloridgehalten kam es vermutlich infolge der Austrocknung der Zink/Beton-Kontaktzone nach relativ kurzer Zeit zu einer Inaktivierung des Zinks. Bei Chloridgehalten von 4 M.-% bildeten sich zwischen der Zinkschicht und dem ausgewählten OS-System gasgefüllte Blasen. Diese Problematik, sowie die Tatsache dass die Wirksamkeit des Prinzips W (Austrocknung des Betons) bei derart hohen Chloridgehalten bezweifelt werden muss, grenzt die Anwendbarkeit des Kombinationssystems mit der Zinkschicht als Opferanode deutlich ein. An neun Jahre alten, ausgelagerten Prüfköpfen durchgeführte Untersuchungen zeigten jedoch, dass mittels Fremdstrombeaufschlagung zwischen Zinkschicht und Bewehrung ein wirksamer kathodischer Schutz auch bei geringeren Chloridgehalten erreicht werden kann. Der Einsatz des entwickelten Kombinationssystems mit Fremdstrombeaufschlagung erscheint somit durchaus durchführbar. Dabei sollte der Fremdstrom jedoch vorsichtig dosiert werden, um den Haftverbund zum Zink nicht zu sehr zu schwächen. Das Ziel des Vorhabens wurde somit erreicht. KW - Chlorinduzierte Korrosion KW - Kathodischer Korrosionsschutz KW - Oberflächenschutzsystem KW - Stahlbeton KW - Thermische Spritzverzinkung PY - 2004 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-355176 SP - 1 EP - 122 PB - IBAC Institut für Bauforschung CY - Aachen AN - OPUS4-35517 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Helmecke, E. A1 - Fleßner, M. A1 - Kaufmann, M. A1 - Staude, Andreas A1 - Hausotte, T. T1 - Numerical measurement uncertainty determination for dimensional measurements of microparts with CT N2 - Up to now, the only standardized method to determine the measurement uncertainty for computed tomography (CT) is to use calibrated workpieces as specified in the Guideline VDI/VDE 2630 Part 2.1. This paper discusses a promising numerical method for uncertainty determination with help of a virtual metrological CT (VMCT). It gives an explanation of the adjustments, the input parameters and the execution of the simulation. Furthermore, it discusses the first results of uncertainty determination compared to the method of using calibrated workpieces with the aid of two example cases. T2 - 6th Conference on Industrial Computed Tomography (iCT) CY - Wels, Austria DA - 09.02.2016 KW - simulation KW - Simulation KW - Computertomographie KW - Dimensionelle Metrologie KW - Normung KW - numerische Messunsicherheitsbestimmung KW - computed tomography KW - dimensional metrology KW - standardization KW - numerical uncertainty determination PY - 2016 UR - http://www.ndt.net/article/ctc2016/papers/ICT2016_paper_id17.pdf SP - Paper ID17, 1 EP - 7 AN - OPUS4-35481 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gleis, Markus A1 - Gehrmann, Hans-Joachim A1 - Simon, Franz-Georg T1 - VDI-Richtlinie 3925 – Anwendung auf zwei Fallbeispiele N2 - Die VDI-Richtlinie 3925 entstand aus Diskussionen und Fragestellungen, die sich aus der Anwendung unterschiedlichster Methoden zur Bewertung verschiedener Verfahrenskonzepten aus dem Bereich der Abfallbehandlung ergeben haben. Je nach nachdem, wo der Focus der vorzunehmenden Bewertung liegt, wird sich die Methodik an diese Ziele anpassen oder - falls es die entsprechende Methodik noch nicht geben sollte - sich die Fragestellung anpassen müssen. T2 - ProcessNet Jahrestreffen CY - Frankfurt/Main DA - 23.02.2016 KW - Wirkungsgrad KW - Exergie KW - Abfallbehandlung KW - Ökobilanz PY - 2016 SP - 25 EP - 26 PB - ProcessNet CY - Frankfurt/Main AN - OPUS4-35506 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simon, Franz-Georg A1 - Holm, Olaf T1 - Reduction of natural resource use by improving resource efficiency N2 - Improving resource efficiency at the end-of-life stage is illustrated in this paper by the example of materials recovery from waste, here from residues out of municipal solid waste incineration (MSWI). With mechanical treatment valuable materials like ferrous and non-ferrous metals and secondary construction material can be extracted from MSWI bottom ash. The potential contribution on the resource efficiency will be discussed. T2 - 12th International Conference on Ecomaterials CY - Tainan, Taiwan DA - 08.11.2015 KW - secondary raw material KW - resource efficiency KW - raw material equivaltent KW - bottom ash PY - 2015 SP - 5 EP - 6 AN - OPUS4-35509 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thiel, Erik A1 - Kreutzbruck, M. A1 - Ziegler, Mathias T1 - Spatial and temporal control of thermal waves by using DMDs for interference based crack detection N2 - Active Thermography is a well-established non-destructive testing method and used to detect cracks, voids or material inhomogeneities. It is based on applying thermal energy to a samples’ surface whereas inner defects alter the nonstationary heat flow. Conventional excitation of a sample is hereby done spatially, either planar (e.g. using a lamp) or local (e.g. using a focused laser) and temporally, either pulsed or periodical. In this work we combine a high power laser with a Digital Micromirror Device (DMD) allowing us to merge all degrees of freedom to a spatially and temporally controlled heat source. This enables us to exploit the possibilities of coherent thermal wave shaping. Exciting periodically while controlling at the same time phase and amplitude of the illumination source induces – via Absorption at the sample’s surface - a defined thermal wave propagation through a sample. That means thermal waves can be controlled almost like acoustical or optical waves. However, in contrast to optical or acoustical waves, thermal waves are highly damped due to the diffusive character of the thermal heat flow and therefore limited in penetration depth in relation to the achievable resolution. Nevertheless, the coherence length of thermal waves can be chosen in the mmrange for modulation frequencies below 10 Hz which is perfectly met by DMD technology. This approach gives us the opportunity to transfer known technologies from wave shaping techniques to thermography methods. We will present experiments on spatial and temporal wave shaping, demonstrating interference based crack detection. T2 - Photonics West 2016, OPTO, 9761 CY - San Francisco, CA, USA DA - 15.02.2016 KW - Active thermography KW - Thermal wave KW - Spatial light modulation KW - Crack detection KW - DMD KW - DMD coupled laser PY - 2016 DO - https://doi.org/10.1117/12.2210918 SN - 0277-786X VL - 9761 SP - 97610N-1 EP - 97610N-13 AN - OPUS4-35587 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thöns, S. A1 - Schneider, Ronald A1 - Faber, M.H. ED - Haukaas, T. T1 - Quantification of the value of structural health monitoring information for fatigue deteriorating structural systems N2 - This paper addresses the quantification of the value of structural health monitoring (SHM) before its implementation for structural systems on the basis of its Value of Information (VoI). The value of SHM is calculated utilizing the Bayesian pre-posterior decision analysis modelling the structural life cycle performance, the integrity management and the structural risks. The relevance and precision of SHM information for the reduction of the structural system risks and the expected cost of the structural integrity management throughout the life cycle constitutes the value of SHM and is quantified with this framework. The approach is focused on fatigue deteriorating structural steel systems for which a continuous resistance deterioration formulation is introduced. In a case study, the value of SHM for load monitoring is calculated for a Daniels system subjected to fatigue deterioration. The influence of and the value of SHM in regard to the structural system risks and the integrity management is explicated and explained. The results are pointing to the importance of the consideration of the structural system risks for the quantification of the value of SHM. T2 - ICASP 12 - 12th International conference on applications of statistics and probability in civil engineering CY - Vancouver, Canada DA - 12.07.2015 PY - 2015 DO - https://doi.org/10.14288/1.0076284 SP - Paper 605, 1 EP - 8 AN - OPUS4-34332 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krankenhagen, Rainer A1 - Worzewski, Tamara A1 - Doroshtnasir, Manoucher A1 - Röllig, Mathias A1 - Studemund, Taarna T1 - Inspecting defective rotor blades by thermographic monitoring from greater distances: A review on results of the three-year project IKARUS T2 - DEWEK 2015 - 12th German Wind Energy Conference CY - Bremen, Germany DA - 2015-05-19 KW - Wind turbine KW - Thermography KW - Rotor blade PY - 2015 SP - Session No. 20, 1 EP - 4(?) AN - OPUS4-34348 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Babutzka, Martin A1 - Lehmann, Jens A1 - Burkert, Andreas T1 - The KorroPad - A novel test method for assessing the pitting corrosion susceptibility of stainless steel surfaces N2 - Pitting corrosion is one of the most common mechanisms of local passivity breakdown on stainless steels. Electrochemical methods have preferentially been applied for the evaluation of pitting corrosion resistance of stainless steels in laboratory. Nevertheless, some of them are not reliable enough and in general the application of electrochemical methods in the field becomes difficult because of a required deep understanding of corrosion phenomena and measurement technology. A new approach for the evaluation of the pitting corrosion susceptibility of stainless Steel surfaces in the laboratory as well as in the field is frequently demanded by representatives of the metalworking industry. Therefore, the KorroPad-test was invented and patented as part of a research project at the BAM Federal Institute for Materials Research and Testing in Germany. T2 - EUROCORR 2015 - European corrosion congress CY - Graz, Austria DA - 06.09.2015 KW - KorroPad KW - Pitting corrosion KW - Stainless steel PY - 2015 SP - Paper 5_730, 1 AN - OPUS4-34297 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wu, Cheng-Chieh A1 - Weisbrich, S. A1 - Neitzel, F. T1 - Inverse finite element adjustment of material parameters from integrated analysis of displacement field measurement N2 - The integration of finite element method (FEM) into the least-squares adjustment presented in [1] is further extended for a joint evaluation of an elastostatic model and displacement field measurement. For linear solids which obey the HOOKE's law, the material parameters determination from measurements is being examined. In many literature, see for example [2], parameters are iteratively tuned until the computed FEM results are in accordance with the measurements. In contrast to these debatable approaches, we follow a rigorous and direct method. The “classical” FEM procedure starts with known material constants and ends up with computed fields such as dis-placement or temperature field. We present a method to invert the FEM procedure using the most general least-squares adjustment – the GAUSS-HELMERT Model (GHM). From given fields, the material parameters are directly calculated. T2 - 32nd Danubia-Adria Symposium on Advances in Experimental Mechanics CY - Stary Smokovec, Slovakia DA - 22.09.2015 PY - 2015 AN - OPUS4-34369 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weise, Hans-Peter ED - Henning, K. T1 - Strahlenexposition der Bevölkerung in der Umgebung von Beschleunigeranlagen niedriger Energie T2 - 18. Jahrestagung des Fachverbandes für Strahlenschutz CY - Lübeck-Travemünde, Germany DA - 1985-10-06 PY - 1985 N1 - Serientitel: FS-Berichte aus der Schriftenreihe des Fachverbandes für Strahlenschutz – Series title: FS-Berichte aus der Schriftenreihe des Fachverbandes für Strahlenschutz IS - 85-37 SP - 470 EP - 483 PB - Fachverband für Strahlenschutz CY - Würenlingen AN - OPUS4-34252 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Amon, H. A1 - Florian, Wolfgang T1 - Härtemessungen in der Wärmeeinflusszone von Schweissverbindungen T2 - Tagung Werkstoffprüfung CY - Bad Nauheim, Germany DA - 1984-12-06 PY - 1985 SP - 115 EP - 131 PB - DVM CY - Berlin AN - OPUS4-34254 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Florian, Wolfgang T1 - Stand der Normung, Forschungs- und Entwicklungsaktivitäten im Bereich der Kaltrißbildung PY - 1985 SP - 1 EP - 15 PB - SLV-Duisburg CY - Duisburg AN - OPUS4-34257 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Florian, Wolfgang A1 - Jaenicke, Bernd T1 - Entwicklung von Konstruktions- und Fertigungsrichtlinien zur optimalen Gestaltung und Herstellung geschweißter, einsatzgehärteter Großzahnräder T2 - Informationstagung des Wissenschaftlichen Beirats der Forschungsvereinigung Antriebstechnik CY - Bad Soden, Germany DA - 1985-11-12 PY - 1985 SP - 1 EP - 18 PB - Forschungsvereinigung Antriebstechnik CY - Frankfurt am Main AN - OPUS4-34259 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Krause, Hans-Joachim T1 - Recommended procedure for testing spot-, seam- and projection weldability PY - 1985 IS - III-WG12-36-85 SP - 1 EP - 5 PB - International Institute of Welding CY - Paris AN - OPUS4-34260 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kind, Thomas A1 - Trela, Christiane A1 - Schubert, Marcus A1 - Wöstmann, Jens ED - Lambot, S. ED - Giannopoulos, A. ED - Pajewski, L. ED - André, F. ED - Slob, E. ED - Craeye, C. T1 - Aggregates scattering of GPR waves in concrete N2 - Time slices of very dense GPR measurements carried out at concrete with a real point distance of less than 10 mm in x and y direction show weak reflection patterns besides the strong reflections of reinforcements. A repetition of these measurements with the same local geometrical precision at the same specimen shows the same reflection pattem. We suppose that the heterogeneity of concrete given by aggregates (e.g. gravel, broken granite) causes local weak Scattering of the GPR waves and leads to reflection patterns in the GPR data. These reflection patterns can be explained by a Superposition of multiple scatterings of single aggregates. So far these reflection patterns have been not recognized in Standard time slices due to the large spacing (> 5 cm) between single profiles and because of the interpolation between the profiles. We investigate the characteristics of the volume scattering effects, caused by aggregates, at concrete blocks with two different grading curves. In a more general investigation we study the volume scattering of aggregates by using wooden boxes filled with only typical aggregates and an included defined reflector (metal plate). The thickness of the aggregate layer above the metal plate was varied between 20 cm and 40 cm. With a very dense measuring grid at the surface we are able to calculate the effective volume scattering and to analyze the distribution of the reflection amplitude of the included metal plate for different aggregate set-ups. Results of this study confirm that the weak reflection patterns in concrete can be explained by aggregate scattering and have a direct correlation to the penetration depth of GPR in concrete. T2 - GPR 2014 - 15th International conference on ground penetrating radar CY - Brussels, Belgium DA - 30.06.2014 KW - Aggregates KW - Volume scattering PY - 2014 UR - http://sites.uclouvain.be/GPR2014 SP - 933 EP - 938 AN - OPUS4-34576 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wiggenhauser, Herbert T1 - Advanced NDT methods for quality assurance of concrete structures T2 - National Seminar on NDE 2010 CY - Kolkata, India DA - 2010-12-09 KW - Beton KW - Qualitätssicherung KW - Zerstörungsfreie Prüfung PY - 2010 SP - 1 EP - 8 AN - OPUS4-34610 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Babutzka, Martin A1 - Reinemann, S. T1 - Electrochemical investigations regarding the influence of deformation-induced martensite on the corrosion behaviour of austenitic stainless steels N2 - Contents of deformation-induced martensite in the lattice structure of austenitic stainless steels lead to an either beneficial or detrimental change of mechanical and magnetic properties depending on the prospective application. Whereas these changes are well-known and investigated widely the influence of deformation-induced martensite on the corrosion behaviour is frequently an issue of scientific discussions. There are opposing opinions that depend on the type of corrosion mechanism being investigated for example regarding pitting corrosion resistance in Chloride containing media. In it is stated that pitting resistance is not influenced by deformationinduced martensite while in it is discussed that more pitting occurs on martensitic structure. The same conflictive opinions appear regarding active dissolution in acidic media or intergranular corrosion. In addition, when having deeper insight into literature it can be concluded that even the type of test method, i. e. dynamic or static testing, has a big influence on the obtained results concerning the influence of martensite in austenitic stainless steels. T2 - EUROCORR 2015 - European corrosion congress CY - Graz, Austria DA - 06.09.2015 KW - Deformation-induced martensite KW - Stainless steel KW - Electrochemical investigations PY - 2015 SP - paper 5_776 AN - OPUS4-34617 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fasano, A. A1 - Woyessa, G. A1 - Stajanca, Pavol A1 - Markos, C. A1 - Stefani, A. A1 - Nielsen, K. A1 - Rasmussen, H. K. A1 - Krebber, Katerina A1 - Bang, O. T1 - Production and characterization of polycarbonate microstructured polymer optical fiber bragg grating sensor N2 - We present the fabrication and characterization of a polycarbonate (PC) microstructured polymer optical fiber (mPOF) and the writing of a fiber Bragg grating (FBG) in it to obtain a polymer optical FBG sen-sor. The manufacturing process of the PC mPOF consists of multiple consecutive stages, such as casting of pol-ymer granulates into a solid rod, machining and drilling of a 3-ring hexagonal lattice of holes into it, and finally drawing into fiber. We demonstrate that the obtained PC mPOF is photosensitive and FBGs can be conveniently inscribed into it, thereby enabling FBG-based temperature and strain sensing. The PC optical fibers are for some applications an attractive alternative to conventional materials used in POF fabrication, such as polymethyl methacrylate (PMMA). In general, PC can be used at temperature up to 120 °C and breaks at considerably higher strains than PMMA. T2 - POF 2015 - 24th International conference on plastic optical fibers CY - Nürnberg, Germany DA - 22.09.2015 PY - 2015 SP - 64 EP - 67 AN - OPUS4-34587 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eberle, Arno A1 - Klingbeil, Dietmar A1 - Schicker, Johannes T1 - Die Berechnung dynamischer JR-Kurven aus der FE-Simulation des Kerbschlagbiegeversuchs unter Einbeziehung eines geschwindigkeitsabhängigen Schädigungsmodells T2 - 29. Tagung des DVM-Arbeitskreises Bruchvorgänge CY - Stuttgart, Germany DA - 1997-02-25 PY - 1997 N1 - Serientitel: DVM-Bericht – Series title: DVM-Bericht IS - 229 SP - 325 EP - 334 PB - DVM CY - Berlin AN - OPUS4-34624 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niederleithinger, Ernst T1 - Levee inspection - geophysics between science, standards, reliability and budgets N2 - Numerous case histories show evidence that geophysical methods are valuable tools for levee inspection and monitoring. National and international standards and recommendations recommend the use of geophysics for a variety of tasks. However, in some cases reported have been flaws missed or false indications given. Due to the larger variety in type, size and construction of levees and the even larger variety of potential tasks and targets the success of geophysical surveys still pretty much depends on the available budget and the experience and capabilities of the clients and contractors involved. It is strongly recommended that all relevant parties agree on the detailed objectives of the survey, required accuracy and reliability of the results and any follow up measures. For the most common tasks more research and practical work using techniques as POD (probability of detection), which are well established in other fields of non-destructive testing, would be of benefit. T2 - SAGEEP 2016 CY - Denver, CO, USA DA - 20.03.2016 KW - Levee KW - Geophysics KW - Inspection PY - 2016 SP - paper levees 07, 1 EP - 4 AN - OPUS4-35705 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Merryweather, S. A1 - Zweifel, D. A1 - Woydt, Mathias ED - Franek, F. ED - Bartz, Wilfried J. ED - Pauschitz, A. ED - Vizintin, J. ED - Ciulli, E. ED - Crockett, R. T1 - Fuel economy of engine oils based on polyalkylene glycols N2 - The driver for automotive OEMs to work on alternative engine oils is the need for fuel economy and no adverse effect of the engine oil on the durability of particulate filters and catalysts. The alternative engine oils should for mid-term also comply with a positive environmental Profile. T2 - 3rd European Conference on Tribology and 4th Vienna International Conference on Nano-Technology CY - Vienna, Austria DA - 07.06.2011 KW - Biomotox KW - Head capacity KW - Fuel economy KW - Drain KW - Polyglycol KW - Polypropylene glycol KW - Polyalkylene glycol KW - Polybutylene glycol PY - 2011 SN - 978-3-901657-38-2 SP - 25 EP - 34 PB - MDH Media GesmbH CY - Wien AN - OPUS4-35671 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Kühn, Julius T1 - Composition and chemistry of Pd-Ni-Co thin film alloys for hydrogen related applications N2 - The discovery and design of high performance Pd-alloys is of great interest for the use of hydrogen as a future energy carrier. Therefore hydrogen has to be detected, separated from other gases and stored. In this respect this thesis presents the combinatorial synthesis and characterization of the ternary Pd-Ni-Co alloy System over a wide composition range based on so-called thin film alloy libraries. Those libraries are model systems to characterize a large number of alloy compositions at the same time. The sputter-deposition process is optimized for the gradient of the Pd concentration on the surface of the alloy library by the use of electron-excited Auger electron spectroscopy. The scientific goal of this work is the experimental Investigation of adsorbate-induced surface segregation phenomena on alloy libraries. The surface and bulk compositions of an alloy library are studied after deposition, H2 exposure and H2S poisoning. The co-segregation of Ni and Co to the surface is observed. The segregation process is influenced by the oxidation of Ni and Co due to the contact with ambient air, by H2 and by H2S poisoning. Also at very high Pd concentrations in the range of 87 at.% to 97 at.%, which is interesting for the detection of very low H2-Concentrations in air, the co-segregation of Ni and Co takes place. The poisoning effects were investigated in detail on a pre-selected Pd-Ni-Co alloy by photoelectron spectroscopy (XPS, HAXPES) in addition to AES and EDX. The composition profile of the alloy on the nm scale is acquired and the surface and bulk chemistry is discussed before and after poisoning. The composition of the alloy only changed within the first 3 nm due to H2S exposure. In the ternary Pd-Ni-Co alloy system Pd is present in its metallic state, while Ni and Co show several oxidation states. The presented concepts of ternary alloy development pave the way for the systematic synthesis and characterization of new ternary transition metal alloy systems. KW - Hydrogen sensor KW - Library of ternary Pd-alloys KW - AES KW - (HAX)PES KW - REM/EDX KW - Wasserstoffsensor KW - Bibliothek ternärer Pd-Legierungen PY - 2016 DO - https://doi.org/10.14279/depositonce-5002 SP - 1 EP - 127 PB - Technische Universität CY - Berlin AN - OPUS4-35680 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Cabillic, J. A1 - Fallot, C. A1 - Hein, Sebastian A1 - Lalere, B. A1 - Philipp, Rosemarie T1 - Développement et validation d’une méthode de référence pour l’analyse des HAP dans l’eau totale dans le contexte de la DCE T1 - Development and validation of a reference method for the analysis of PAHs in whole water in accordance to the WFD N2 - Afin de garantir la qualité des eaux en Europe, la Commission Européenne a demandé aux États Membres, de leur fournir des résultats de mesure comparables et traçables pour l’analyse des polluants critiques. Devant ces enjeux considérables pour la protection de l’environnement, l’apport de la métrologie est nécessaire pour améliorer la fiabilité des analyses et permettre la comparabilité des résultats. C’est pourquoi, le projet de recherche européen Euramet/EMRP/ENV08 « Traçabilité des mesures pour la surveillance des polluants critiques de la DCE, Directive Cadre européenne sur l’Eau (2000/60/CE) », financé par l’EMRP, avait pour objectif de fournir des éléments pour la mise en place d’une base métrologique. Des méthodes de référence primaires permettant d’analyser des substances dangereuses prioritaires y sont développées pour répondre aux exigences de la DCE en termes de niveaux de performance (limites de quantification et incertitudes). Les hydrocarbures aromatiques polycycliques (HAP), substances dangereuses prioritaires « orphelines » de méthodes DCE compatibles, font partie des polluants ciblés par le projet. Le développement et la validation de la méthode d’analyse des HAP dans l’eau totale ont été réalisés. La méthode qui satisfait au mieux les exigences de la DCE en termes de concentrations et d’incertitudes accessibles est l’extraction en phase solide (SPE) sur un support disque suivie d’une analyse par dilution isotopique associée à la chromatographie en phase gazeuse couplée à la spectroscopie de masse (DI-CG/SM). N2 - To ensure the water quality in Europe, the European Commission asked the member states to provide comparable and traceable measurement results for the analysis of critical pollutants. Considering the increasing environmental challenges, the contribution of metrology is necessary both for the improvement of analysis reliability and the comparability of results. For this reason the European research project Euramet/EMRP/ENV08 “Traceable measurements for monitoring critical pollutants under the European Water Framework Directive (WFD-2000/60/EC)”, funded by the EMRP, aimed to provide the elements for the development of a metrological basis. The project develops primary reference methods enabling the analysis of priority hazardous substances in order to meet the WFD requirements in terms of performance levels (limit of quantification and uncertainties). Polycyclic aromatic hydrocarbons (PAHs) – priority hazardous substances for which no DCE compatible methods exist – are among the three families of pollutants targeted by the project. This paper tackles the development and validation of the PAH analysis method on whole water samples. The method that best meets the requirements of the WFD in terms of level of concentration and uncertainty is the solid phase extraction (SPE) method with SPE-disks, followed by isotope dilution analysis combined with gas chromatography mass spectrometry (ID-GC/MS). KW - Reference method KW - Referenzmethode KW - Limit of quantification KW - Bestimmungsgrenze KW - Polycyclic aromatic hydrocarbons KW - Polyzyklische aromatische Kohlenwasserstoffe PY - 2015 UR - http://www.metrologie-francaise.fr/publications/revue_francaise_metrologie/2015-04/RFM40-1514.pdf DO - https://doi.org/10.1051/rfm/2015014 SN - 1772-1792 VL - 2015-4 IS - 40 SP - 3 EP - 12 AN - OPUS4-35731 LA - fra AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kronemann, Jens A1 - Hünger, K.-J. T1 - Aggregate reactivity and the efficiency of supplementary cementing materials N2 - The knowledge of dissolution processes of aggregates and supplementary cementing materials (SCMs) in alkaline solutions can help to describe the expansion of concretes caused by alkali-silica reaction (ASR) and the effects to avoid ASR by using SCMs in more details. Therefore, dissolution experiments in alkaline solutions under different pH values and different temperatures were performed using aggregates in the original grain size and SCMs in different ratios. The concentrations of soluble silica and additionally alumina were determined by ICP-OES. The investigations showed that up to now the “best” conditions to explain the damage behavior of concrete structures are a pH value of 13 (e.g. 0.1 M KOH solution) and a temperature of 80 °C. The evaluation bases on the parameter “excess silica” which is calculated from the dissolved silica and alumina of the aggregates and the SCMs. It was demonstrated that SCMs reduce and sometimes stop the dissolution of aggregates. The efficiency of the SCMs depends on their amount and chemical composition. T2 - 13th International conference on recent advances in concrete technology and sustainability issues CY - Ottawa, Canada DA - 14.07.2015 KW - alkali silica reaction KW - aggregate reactivity KW - dissolution of silica and alumina KW - dissolution rate PY - 2015 SN - 978-1-942727-23-1 SP - SP-303-26, 355 EP - 370 AN - OPUS4-35609 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hünger, K.-J. A1 - Kronemann, Jens A1 - Hübert, C. A1 - Scholz, Y. T1 - On the mechanism of ASR inhibition by Si and Al containing SCMs N2 - The use of supplementary cementing materials (SCMs) added to concrete mixtures can avoid the alkali-silica reaction. Such materials have a wide range of composition and therefore the inhibition mechanisms can be very differently. The effectiveness of SCMs which provide silica and alumina into the alkaline solution cannot only be explained by reducing the OH--concentration of the pore solution. From dissolution experiments in potassium hydroxide solutions, an interaction was noted between the aggregate and five SCMs via the alkaline solution. Under specific conditions, no silica is released from the aggregate grains. Mineralogical investigations (XRD, SEM+EDX) of the grain surfaces confirm that quartz is the main source of silica. In the presence of alumina providing SCMs, the quartz dissolution is strongly reduced or even sometimes stopped. On surfaces of grains a very thin layer can be observed which is probably responsible for reduction or stopping of the silica dissolution and therefore for the inhibition of ASR. T2 - 13th International conference on recent advances in concrete technology and sustainability issues CY - Ottawa, Canada DA - 14.07.2015 KW - alkali-silica reaction KW - alkali reactivity KW - solubility KW - supplementary cementing materials KW - surface layer PY - 2015 SP - 437 EP - 451 AN - OPUS4-35612 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Liehr, Sascha A1 - Burgmeier, J. A1 - Krebber, Katerina T1 - Quasi-distributed fiber bend and temperature measurement in femtosecond laser-structured POF N2 - We propose to use focused femtosecond laser pulses to inscribe Scattering damage in the core of polymer optical fibers for interrogation as quasi-distributed sensor points by optical time domain reflectometry. Fiber bend measurement is demonstrated on off-center inscribed sensor points and absolute temperature measurement is presented by evaluation of the constant backscatter intensities from the inscribed structures relative to temperature-dependent Rayleigh Scattering. Application possibilities and limitations of this new approach are discussed. T2 - POF 2013 - 22nd International conference on plastic optical fibers CY - Búzios, Rio de Janeiro, Brazil DA - 11.09.2013 KW - POF KW - Polymer optical fiber KW - Femtosecond laser KW - Optical fiber sensors KW - OTDR KW - Backscatter measurement PY - 2013 SP - 279 EP - 284 CY - Rio de Janeiro, Brazil AN - OPUS4-30082 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bonsiepen, L. A1 - Ferri, D. A1 - de Günther, S. A1 - Kaes, F. A1 - Krug, Sonja A1 - Lauer, R. A1 - Sleczek, E. T1 - LunchTalk Bericht: Sammlungserschließung N2 - Das Basisprojekt »Sammlungserschießung« erforscht exemplarisch einen bisher unerschlossenen Sammlungsbereich der Lipperheideschen Kostümbibliothek, angesiedelt an der Kunstbibliothek der Staatlichen Museen zu Berlin. KW - Restaurierung KW - Konservierungswissenschaft KW - Informatik KW - Interaction Design KW - Kunstgeschichte KW - Modegeschichte KW - Erschließung KW - Museum KW - Sammlung PY - 2013 IS - 44 SP - 3 EP - 6 AN - OPUS4-30292 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krug, Sonja T1 - LunchTalk-Bericht: Restaurierung & Konservierung KW - Restaurierung KW - Konservierung PY - 2013 IS - 27 SP - 3 AN - OPUS4-30293 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auster, Jürgen A1 - Neumeyer, Tino A1 - Müller, Karsten A1 - Droste, Bernhard T1 - Leakage testing during lateral displacement of metallic seals under mechanical accident impact N2 - In context with approval design tests, the IAEA regulations for the safe transport of radioactive material specify tests for demonstrating ability to withstand normal and accident conditions of transport. For 9-m drop test onto an unyielding target the drop orientation of the package must be chosen in a manner so that maximum damage occurs with regard to the safety criteria. With respect to leak tightness after drop test impacts a horizontal or slap-down orientated test model can cause a lateral displacement of the packaging’s lids, affecting the leakage rate of the closure lid system strongly. In Germany dual purpose casks with double lid sealing system composed of primary and secondary lid with bolts, metallic seals as well as cask body sealing surfaces are mainly used. Besides free drop tests with full-scale and half-scale models within licensing approval procedure BAM develops experimental testing methods to simulate defined stresses and deformations by means of components testing. In order to investigate the relation between lateral lid displacement and leakage rate, BAM performs impact tests with small scaled flange-lid systems of transport packages in a drop test machine for guided drop tests. The test setup is realized in a way that the flange part is fixed while a drop weight is impacting onto the lid’s edge. The dynamic displacement of the lid is measured simultaneously. Because of capturing the drop weight after first impact during a short rebound phase by pneumatic arrest mechanism a secondary impact on lid’s edge is excluded. The guided drop tests were accompanied by various measurements such as leakage rate recording during and after impact, identification of lateral shifting by electro-optical displacement transducer as well as decelerations of the lid and the impacting weight. This paper describes the test setup, the test and measurement techniques as well as first results concerning the relation between lateral lid displacement and leaktightness. T2 - PATRAM 2013 - 17th International symposium on the packaging and transportation of radioactive materials CY - San Francisco, CA, USA DA - 18.08.2013 PY - 2013 SP - Paper 168, 1 EP - 6 PB - Omnipress AN - OPUS4-30282 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bachmann, Marcel A1 - Avilov, Vjaceslav A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Magnets improve quality of high-power laser beam welding N2 - Welding is one of the most critical operations for the construction of reliable metal structures in everything from ships to reactor vessels. When welds fail, often the entire structure fails, and expectations on weld quality have never been higher. Any process that uses a localized heat source, such as welding, is likely to result in some distortion. The welding process of very thick metal components is not inherently stable and is barely controllable without external forces. KW - Electromagnetic weld pool control KW - Laser beam weliding KW - Marangoni effect PY - 2014 VL - 2013-2014 SP - 30 EP - 32 AN - OPUS4-30338 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Nery de Araújo Neto, Gilberto T1 - O que é monitoracao na construcao civil? N2 - Quando se constrói uma estrutura, na maioria das vezes, não se sabe ao certo até quando esta será necessária, útil ou ainda, segura. No projeto utilizam-se características conhecidas dos materiais, como resistência à compressão, resistência a ataques químicos e a intempéries, além de expectativas de carregamento e condições de exposição em uso. Porém, as reais interações entre a estrutura e o ambiente no qual ela está inserida são difíceis de prever ou simular. Além do carregamento em uso, que pode variar de forma diferente do previsto (incremento de tráfego sobre uma ponte ou modificação de uso de um edifício, por exemplo), outra questão são as sobrecargas acidentais, como terremotos, inundações, etc. Todas estas incertezas fazem com que a uma previsão precisa da degradação da estrutura ao longo do tempo seja difícil (quase impossível). Para confirmar a segurança e a fidelidade da estrutura em relação ao projeto são feitas inspeções, que avaliam a degradação, a segurança e as condições gerais da estrutura. Podem-se citar como principais usos do monitoramento estrutural na engenharia civil: auxiliar as inspeções provendo ao especialista um histórico de degradação e comportamento que possibilita um melhor entendimento de possíveis problemas e a identificação de causas; certificar uma estrutura em relação à fidelidade ao projeto; avaliar a segurança de uma estrutura antiga ou num dado momento em que condições especiais se apresentem; e otimizar programas de manutenção. T2 - What is monitoring in construction? KW - Structural health monitoring KW - Sensors KW - Maintenance management PY - 2013 N1 - Serientitel: Monitoreo en la Construcción Civil – Series title: Monitoreo en la Construcción Civil VL - 5 SP - 1 EP - 16 AN - OPUS4-30382 LA - spa AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Agirrezabal-Telleria, Iker A1 - Hemmann, Felix A1 - Jäger, Christian A1 - Arias, P. L. A1 - Kemnitz, E. T1 - Functionalized partially hydroxylated MgF2 as catalysts for the dehydration of d-xylose to furfural N2 - Among the furan-based compounds, furfural (FUR) shows interesting properties as building-block or industrial solvent. It is produced from pentosan-rich biomass via xylose cyclodehydration. The current FUR production uses homogeneous catalysts and steam. According to recent studies, the reaction mechanism is different in the presence of Lewis (L) or Brønsted (B) sites. In this work, partially hydroxylated MgF2 catalysts, containing bifunctional Lewis and Brønsted properties, were further functionalized using different fluorosulfonic precursors. Its main objective was to test these solids as catalysts for xylose conversion to furfural. Extensive characterization techniques using TG–MS, 19F-MAS-NMR, or pyridine adsorption confirmed the substitution of surface OH groups by stronger Brønsted sites. The activity data showed a considerable change of the reaction kinetics and a final furfural selectivity of 90% at 160 °C in water/toluene for optimized L/B ratios by the one-step grafting technique. Moreover, the reaction analyses and the change of conversion pathways were studied. KW - Hydroxylated MgF2 KW - Functionalization KW - Fluorosulfonic acid KW - Lewis KW - Brønsted KW - Xylose KW - Furfural PY - 2013 DO - https://doi.org/10.1016/j.jcat.2013.05.005 VL - 305 SP - 81 EP - 91 AN - OPUS4-30444 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Herbst, Tristan A1 - Schneider, S. A1 - Brandstetter, C.P. A1 - Flassenberg, G. T1 - Stoffkreislauf im Mauerwerksbau - Nachhaltigkeitsanalyse für das Mauerwerksrecycling N2 - In Deutschland fallen nach Abschätzungen von jährlich bis zu 10 Millionen Tonnen Mauerwerkbruch an. Im Sinne einer nachhaltigen Kreislaufwirtschaft sind diese Restmassen zukünftig einem möglichst hochwertigen und individuell angepassten Recycling zuzuführen. Vor diesem Hintergrund wurde im IGF-Forschungsvorhaben 17022 N der Forschungsvereinigung Porenbetonindustrie e.V. die Nachhaltigkeit verschiedener Recyclingoptionen für Mauerwerkbruch ganzheitlich untersucht. Unter Einbeziehung der Hauptmauersteinarten Ziegel, Kalksandstein, Porenbeton und Leichtbeton wurden dabei material- und verfahrenstechnische sowie ökologische, ökonomische und soziale Aspekte berücksichtigt. Als Ergebnis wurde ein EDV-gestütztes Analysetool (Web-Tool) zur Nachhaltigkeitsbewertung für das Mauerwerksrecycling entwickelt. Mit dem Web-Tool sollen Anwender (Planer, Architekten, Recycler) die Möglichkeit erhalten, für verschiedene Untersuchungsfälle unter Einbeziehung regional und sachlich bedingter Parameter objektspezifische Aussagen zur Nachhaltigkeit treffen zu können. Auf diesem Wege können im Sinne der aktuellen gesetzlichen Vorgaben nachhaltige Stoffkreisläufe im Mauerwerksbau geschlossen und somit letztlich die Deponierung von Mauerwerksrestmassen reduziert oder gar vermieden werden. T2 - R'13 - Fachtagung Recycling CY - Weimar, Germany DA - 19.09.2013 PY - 2013 SP - 1 EP - 6 PB - Bauhaus-Univ. CY - Weimar AN - OPUS4-30408 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Werner, Jan A1 - Heming, Frank T1 - Compatibility of elastomers with biofuels N2 - Biofuels represent an important renewable fuel alternative to petroleum-derived transport fuels. Materials compatibility is a major concern whenever the fuel composition is changed. The aim of this work is to study the interaction of the elastomers: FKM, EPDM, CR, CSM, NBR, IIR, VMQ and FVMQ and biofuels such as biodiesel (FAME), E85 (fuel with 85% ethanol) and B10 (heating oil with 10% biodiesel). Exposure tests were performed with test specimens at 40°C (104°F) and 70°C (158°F) for 84 days to document the changes in mass, volume and tensile properties according to ISO 1817. The exposure tests in E85 showed that the weight gain caused by swelling was in the range up to 12%. The lowest decrease in the tensile properties was determined for FKM, VMQ and IIR. The weight gain of the elastomers in biodiesel varied between 10% (FKM) and 126% (CSM) and the loss of tensile strength between 16% (FKM) and 100% (CSM) at 70°C (158°F). FKM and FVMQ absorbed much less B10 and swelled less. NBR, EPDM, CR, CSM, IIR and VMQ were not resistant to B10 at all as the decrease in the tensile properties was significantly over 50%. Among all of the elastomers FKM showed high compatibility with these biofuels up to 70°C (158°F). T2 - Corrosion 2014 CY - San Antonio, TX, USA DA - 09.03.2014 KW - Biofuels KW - Elastomers KW - Compatibility KW - Change in tensile properties KW - Change in mass KW - Sealing materials KW - Biodiesel KW - E85 KW - B10 KW - Mass loss KW - Tensile properties PY - 2014 SP - Paper 3745, 1 EP - 9 AN - OPUS4-30411 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Werner, Otto T1 - Verfahren zur quantitativen Spektralanalyse antiker Kupferlegierungen PY - 1970 VL - 250 IS - 1 SP - 17 EP - 23 CY - Wiesbaden AN - OPUS4-30152 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Linnemann, Konrad A1 - Ballheimer, Viktor A1 - Sterthaus, Jens A1 - Wille, Frank T1 - Methodological aspects for numerical analysis of lid systems for SNF and HLW transport packages N2 - The regulatory compliance of the containment system is of essential importance for the design assessment of transport packages for radioactive materials. The requirements of the IAEA transport regulations SSR-6 for accident conditions implies high load on the containment system of Type B(U) packages. The integrity of the containment system has to be ensured under the mechanical and thermal tests. The containment system of German transport packages for spent nuclear fuel (SNF) and high level waste (HLW) usually includes bolted lids with metal gaskets. BAM Federal Institute for Materials Research and Testing as the German competent authority for the mechanical and thermal design assessment of approved transport packages has developed the guideline BAM-GGR 012 for the analysis of bolted lid and trunnion systems. According to this guideline the finite element (FE) method is recommended for the calculations. FE analyses provide more accurate and detailed information about loading and deformation of such kind of structures. The results allow the strength assessment of the lid and bolts as well as the evaluation of relative displacements between the lid and the cask body in the area of the gasket groove. This paper discusses aspects concerning FE simulation of lid systems for SNF and HLW transport packages. The work is based on the experiences of BAM within safety assessment procedures. The issues considered are the assessment methods used in the BAM-GGR 012 for bolted lid systems along with the nominal stress concept which is applied for bolts according to that guideline. Additionally, modeling strategies, analysis techniques and the interpretation of the results are illustrated by the example of a generalized bolted lid systems under selected accident conditions of transport. T2 - PATRAM 2013 - 17th International symposium on the packaging and transportation of radioactive materials CY - San Francisco, CA, USA DA - 18.08.2013 PY - 2013 SP - 1 EP - 10 PB - Omnipress AN - OPUS4-30134 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erhard, Anton A1 - Völzke, Holger A1 - Droste, Bernhard A1 - Wolff, Dietmar A1 - Wille, Frank T1 - Nuclear power plant waste management strategy in Germany N2 - The shut-down of eight nuclear power plants and the phase out of the nuclear energy genera� tion in Germany, due to a decision of the German government after the Fukushima accident, has rapidly forced the need for transportation and storage of spent nuclear fuel (SNF) from shut-down reactors in this country. In accordance with the present strategy in Germany, which is characterized by searching for appropriate final repository areas, only the dry interim stor� age facilities are available for storage nuclear waste of the decommissioned plants as well as the operating plants. Therefore, the transportation and the storage casks must be available for both types of light water reactors. But for the time being this is the bottleneck. Unfortunately the prognoses are neglecting the fact, that such a high number of casks are needed in a very short space of time. This requires the acceleration of formal activeness in relation to the li� censes but also an increase of the production. In the meanwhile to get this process started, the only possibility is the storage in the pools at the plant site. Anyway, for the time being, this is one of the problems for dismantling the eight plants which have been shut down due to the decision of the Government, which is now fixed in the last amended German Atomic Energy Act dated 24th of February 2012. Starting to dismantle in the radioactive regions of the plants requires empty pools. For emptying the pools of damaged SNF special procedures regarding the transportation and storage are necessary. The transportation of damaged SNF requires special casks or at least special procedures and therefore also a special licenses. This paper describes the challenge for the management in transportation and storage of SNF in Germany after the shut-down of the nuclear power plants by reason of the Fukushima acci� dent. T2 - PATRAM 2013 - 17th International symposium on the packaging and transportation of radioactive materials CY - San Francisco, CA, USA DA - 18.08.2013 PY - 2013 SP - 1 EP - 11 PB - Omnipress AN - OPUS4-30135 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Komann, Steffen A1 - Kiyak, Yusuf A1 - Wille, Frank A1 - Zerbst, Uwe A1 - Weber, Mike A1 - Klingbeil, Dietmar T1 - Assessment of ductile cast iron fracture mechanics analysis within licensing of German transport packages N2 - In the design approval of transport packages for radioactive materials, the mechanical and thermal safety assessment is carried out in Germany by competent authority BAM. In recent years BAM was involved in several licensing procedures of new spent fuel and HLW package designs, where the cask body is of Ductile Cast Iron (DCI). According to IAEA regulations package designs have to fulfill requirements for specific conditions of transport. Type B(U) packages must withstand the defined accident conditions of transport. The temperature range from -40°C up to the operational temperature has to be considered. For the cask material DCI, it is necessary to determine safety against brittle fracture. The German guideline BAM-GGR 007 defines requirements for fracture mechanics of packagings made of DCI. Due to complex cask body structure and the dynamic loading a fracture mechanical assessment by analytical approaches is not always possible. Experience of recent design approval procedures show that the application of numerical calculations are applicable to determine the stresses and stress intensity factors in the cask body. At the first step a numerical analysis has to be done to identify the loading state at the whole cask body. Secondly an analysis of a detail of the cask body is made considering the displacement boundary conditions of the global model. An artificial flaw is considered in this detailed model to calculate the fracture mechanical loading state. The finite element mesh was strongly refined in the area of the flaw. The size of the artificial flaw is based on the ultrasonic inspection acceptance criteria applied for cask body manufacture. The applicant (GNS) developed additional analysis tools for calculation of stress intensity factor and/or J-Integral. The assessment approach by BAM led to the decision to develop own tools to the possibility for independent proof of the results. The paper describes the authority assessment approach for DCI fracture mechanics analysis. The validation procedure incl. the development of own tools is explained. BAM developed a postprocessor to determine the fracture mechanical loads. A horizontal 1 m puncture bar drop test is used to give a detailed description of the assessment procedure. T2 - PATRAM 2013 - 17th International symposium on the packaging and transportation of radioactive materials CY - San Francisco, CA, USA DA - 18.08.2013 PY - 2013 SP - 1 EP - 10 PB - Omnipress AN - OPUS4-30175 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völzke, Holger A1 - Wolff, Dietmar A1 - Probst, Ulrich A1 - Nagelschmidt, Sven A1 - Schulz, Sebastian T1 - Long-term performance of metal seals for transport and storage casks N2 - Dual purpose casks for the transportation and storage of spent nuclear fuel and other radioactive materials require very high leak-tightness of lid closure Systems under accident conditions as well as in the long-term to prevent activity release. For that purpose metal seals of specific types with an inner helical spring and outer metal liners are widely used and have shown their excellent performance if certain quality assurance requirements for fabrication and assembling are satisfied. Well defined surface roughness, clean and dry inert conditions are therefore essential. No seal failure in a loaded cask happened under these conditions until today. Nevertheless, the considered and licensed Operation period is limited and all safety assessments have been performed and approved for this period of time which is 40 years in Germany so far. But in the meantime longer storage periods might be necessary for the future and therefore additional material data will be required. BAM is involved in the qualification and evaluation procedures of those seals from the early beginning. Because long-term tests are always time consuming BAM has early decided to perform additional tests with specific test seal configurations to gain a better understanding of the long-term behavior with regard to seal pressure force, leakage rate and useable resilience which is safety relevant mainly in case of accidental mechanical loads inside a storage facility or during a subsequent transport. Main test parameters are the material of the outer seal jacket (silver or aluminum) and the temperature. This paper presents the BAM test program including an innovative test mock-up and most recent test results. Based on these data extrapolation models to extended time periods are discussed, and also future plans to continue tests and to investigate seal behavior for additional test parameters are explained. T2 - PATRAM 2013 - 17th International symposium on the packaging and transportation of radioactive materials CY - San Francisco, CA, USA DA - 18.08.2013 PY - 2013 SP - 1 EP - 13 PB - Omnipress AN - OPUS4-30136 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard T1 - A survey on 35 years of packaging, transport and storage of radioactive material N2 - This will is a report from an expert working in this field since 1978, participating in PATRAM conferences since 1980. Exactly in that year 1978 the development and testing of the CASTOR casks started in Germany, with the intention to use these transport casks for interim storage of spent fuel. After involvement in the first full-scale drop tests of those large spent fuel casks for transport package design approval, the official assessment as storage cask started. At the beginning of that new decommissioning technology a series of storage demonstration programs were conducted; most interesting were cases where a cask was loaded in a NPP with fuel assemblies instrumented with thermocouples, equipped with a first lid penetrated by instrumentation cables, closed by a second lid, transported to a research institute and stored there for 2 years, with verification of maximum cladding temperatures and leak-tight closure. In 1982 the basis BAM expert reports for the licensing of CASTOR casks in away-from-reactor storage sites Gorleben and Ahaus were finished. The first cask loading for interim storage was performed in Switzerland in 1983; that CASTOR Ic-Diorit cask, 30 years of age, is the “grandfather” of all dual purpose casks. In 1984, a remarkable transport accident happened, the sinking of the “Mont-Louis” with 30 48-Y-UF6 containers; BAM shortly before had issued the approval for a tank container that could be used for the recovery of some these UF6 containers. The 90s saw the full-scale drop tests with the POLLUX multi� purpose cask design ( for transport, interim storage, final disposal), drop test series with new transport packages for fresh fuel assemblies including the “French puncture drop”, finally a spectacular BLEVE blast onto a CASTOR cask. 2004 we were proud to host the PATRAM conference, the second time in Berlin. For the Technical Tours BAM performed drop tests with two full scale SNF casks (the largest ones tested world-wide) at our new 200 t drop test facility. In the meantime a lot of other assessment experience, e.g. in ductile iron brittle fracture, numerical calculations, radwaste disposal container testing etc. was stacked. Changes in safety assessment methodology over the last decades will briefly be addressed. T2 - PATRAM 2013 - 17th International symposium on the packaging and transportation of radioactive materials CY - San Francisco, CA, USA DA - 18.08.2013 PY - 2013 SP - 1 EP - 10 PB - Omnipress AN - OPUS4-30137 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard A1 - Wille, Frank T1 - Maintenance of package design safety report effectiveness of SNF and HWL dual purpose casks N2 - For interim storage of spent fuel or HLW in many countries transport casks are used. The design of these “dual purpose casks” has to be assessed and approved to transport regulations (based on IAEA SSR-6), and to be assessed within the storage facility licensing procedure. Although the transport cask design differs from the storage cask design, e.g. by use of impact limiters, the majority of cask components is identical for both. Differences occur also in the acceptance criteria; these are for the transport case defined in IAEA SSR-6, and have to be developed for the storage case based on the storage conditions. Considering transport after several decades of storage requires the implementation of ageing behavior into the transport safety case. Additionally the transport package design safety case has to be maintained in an up-to-date state, considering potential regulatory changes and development of scientific and technical knowledge. The review of a transport package design safety case has to be done periodically, implemented in periodic re-assessment for extension of the package design approval certificate. The review process (as a kind of “intellectual periodic inspection”) should be part of the approved applicant’s management system. From experience we have seen that stability of regulatory requirements for Type B(U) packages was not a major problem, but consideration of ageing and developments regarding the state-of-the-art technology can cause necessary adjustments of specific technical evaluation, with the result of confirmation of package safety, or with the development of appropriate compensatory measures to reach the required level of safety. This paper will draw some examples from the past to explain the problems in periodic transport safety case reviews. T2 - PATRAM 2013 - 17th International symposium on the packaging and transportation of radioactive materials CY - San Francisco, CA, USA DA - 18.08.2013 PY - 2013 SP - 1 EP - 9 PB - Omnipress AN - OPUS4-30138 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kumano, Y. A1 - Droste, Bernhard A1 - Hirose, M. A1 - Harvey, J. A1 - Reiche, I.. A1 - Wolff, Dietmar A1 - McConnell, P. A1 - Varley, K. T1 - Overview of the IAEA's joint working group on integrated safety case for dual purpose casks N2 - Spent nuclear fuel is generated from the operation of nuclear reactors and needs to be safely managed following its removal from reactor cores. Spent nuclear fuels are usually stored in a reactor pool for a short period of time after defueling, and then they are shipped to its next destination for reprocessing, disposal, or further storage. In some countries, a concept of Dual Purpose Cask (DPC) is considered as an attractive option for further storage. This is because of that the concept increases flexibility for storage capacity, as well as its economic efficiency that can reduce the complexity of handling highly radioactive spent fuels. The management of spent fuel using a DPC involves storage of spent fuel as well as on-site and off-site transportation before and after storage. Most countries require package design approval for the DPC to be transported. In addition, it is required in many countries to have a license for storage of the spent fuel in the DPC or a license for a storage facility that contains DPCs. Therefore, demonstration of compliance of the DPC with national and international transport regulations as well as with the storage requirements is necessary. In June 2010, the IAEA organized “International Conference on Management of Spent Fuel from Nuclear Power Reactors”. In this conference, many countries expressed their interest on harmonizing both transport and storage safety cases for DPCs that has a possibility to establish an effective and integrated regulatory framework in a holistic manner. Taking into account the increasing needs among Member States, the IAEA set up a new working group following the conference to discuss how to develop an integrated safety case for both transportation and storage.This activity is planned to be completed in 2013. Currently, a technical report is being prepared as an outcome of this activity. In this paper, the IAEA’s approach to demonstrate the safety of DPCs in a holistic manner is described first, followed by the overview of the draft document. It also presents the difference between the conventional transport cask concept and the DPC concept. T2 - PATRAM 2013 - 17th International symposium on the packaging and transportation of radioactive materials CY - San Francisco, CA, USA DA - 18.08.2013 PY - 2013 SP - 1 EP - 9 PB - Omnipress AN - OPUS4-30140 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Melchior, Paul T1 - Geometrische Größen und Gewichtsgrößen von Textilien und ihre Zusammenhänge PY - 1956 IS - 3 AN - OPUS4-30143 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Wieser, Günter A1 - Qiao, Linan A1 - Protz, Christian T1 - Modeling strategies for dynamic finite element cask analyses N2 - The safety of transport packages may be demonstrated by numerical calculation of load scenarios defined in the IAEA regulations. Possible handling accidents of casks at interim storage sites or in a final repository are typically analyzed by dynamic finite element computations. In each case the investigated load scenario must be transferred into a mathematical model. Secondly the mathematical model must be transferred into a numerical model. Reliable finite element models should be developed by assembling verified sub-models of components. The finite element mesh, material modeling, initial and boundary conditions, contact definitions, and time integration as well as the benefit of pre- and post-calculations are discussed. The paper presents lessons learnt from modeling dynamic test scenarios for finite element analyses over the years. T2 - PATRAM 2013 - 17th International symposium on the packaging and transportation of radioactive materials CY - San Francisco, CA, USA DA - 18.08.2013 KW - Structural analysis KW - Dynamic numerical simulation KW - Modeling strategies KW - Discretization KW - Material modeling KW - Boundary conditions KW - Cask load scenarios PY - 2013 SP - Session A, Paper 280, 1 EP - 10 PB - Omnipress AN - OPUS4-30158 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wille, Frank A1 - Wolff, Dietmar A1 - Droste, Bernhard A1 - Völzke, Holger A1 - Baden, M. T1 - German approach and experience feedback of transport ability of SNF packages after interim storage N2 - In Germany the concept of dry interim storage of spent fuel in dual purpose metal casks is implemented, currently for periods of up to 40 years. The casks being used have an approved package design in accordance with the international transport regulations. The license for dry storage is granted on the German Atomic Energy Act with respect to the recently revised “Guidelines for dry interim storage of irradiated fuel assemblies and heat-generating radioactive waste in casks” by the German Waste management Commission (ESK). For transport on public routes between or after long term interim storage periods, it has to be ensured that the transport and storage casks fulfil the specifications of the transport approval or other sufficient properties which satisfy the proofs for the compliance of the safety objectives at that time. In recent years the validation period of transport approval certificates for manufactured, loaded and stored packages were discussed among authorities and applicants. A case dependant system of 3, 5 and 10 years was established. There are consequences for the safety cases in the Package Design Safety Report including evaluation of long term behavior of components and specific operating procedures of the package. Present research and knowledge concerning the long term behavior of transport and storage cask components have to be consulted as well as experiences from interim cask storage operations. Challenges in the safety assessment are e.g. the behavior of aged metal and elastomeric gaskets under IAEA test conditions to ensure that the results of drop tests can be transferred to the compliance of the safety objectives at the time of transport after the interim storage period. T2 - PATRAM 2013 - 17th International symposium on the packaging and transportation of radioactive materials CY - San Francisco, CA, USA DA - 18.08.2013 KW - Storage KW - Transport KW - Lagerung KW - Verpackung KW - Radioactive material PY - 2013 SP - 1 EP - 9 PB - Omnipress AN - OPUS4-30159 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meinel, Dietmar A1 - Staude, Andreas A1 - Ehrig, Karsten ED - Bernard, D. ED - Buffière, J.-Y. ED - Pollock, T. ED - Poulsen, H.F. ED - Rollett, A. ED - Uchic, M. T1 - Analyzing microstructure and damage in construction materials with 3D micro CT N2 - This poster presentation gives an overview of the great potential of X-ray micro computed tomography (CT) to cast light on the evolution of the microstructure in construction materials. Prevention of damage is of major economic and social importance in the development of suitable construction materials such as concrete and asphalt. Therefore a non-destructive testing method such as CT is an appropriate tool for visualization of the inner structure. Its combination with other test methods allows understanding the damage processes such as crack propagation or corrosion. We show examples of internal structure analyses on a wide range of materials: Automatic 3D crack detection and the visualization of corrosion products inside of steel reinforced concrete, pore and shape analysis of lightweight aggregates and the visualization of deformation of high-pressure loaded aerated concrete specimens, distribution of aggregates inside concrete, and determination of the surface of porous asphalt core samples. Segmented structures serve, e.g., as input data for simulation of transport phenomena or virtual load tests. T2 - 2nd International congress on 3D materials science 2014 CY - Annecy, France DA - 29.06.2014 KW - X-ray computed tomography KW - Concrete KW - Asphalt KW - Corrosion KW - Crack detection KW - 3D visualization PY - 2014 SP - 23 EP - 28 PB - Wiley AN - OPUS4-31069 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wiggenhauser, Herbert A1 - Kind, Thomas A1 - Krause, Martin A1 - Schulze, S. A1 - Taffe, A. A1 - Trela, Christiane A1 - Wöstmann, Jens T1 - Praktische Anwendung zerstörungsfreier Prüfverfahren an Brücken N2 - Die drei Beispiele zerstörungsfreier Prüfungen an Spannbetonbrücken zeigen unterschiedliche Problemstellungen und deren Lösung mit unterschiedlichen Ansätzen. Allen drei Beispielen gemeinsam ist die Verwendung kommerzieller Geräte. Diese werden von verschiedenen Anbietern bereitgestellt. Eine weitere Gemeinsamkeit ist, dass die Grundgeräte durch zusätzliche Maßnahmen ergänzt. Erst dann ist der gewünschte Untersuchungserfolg sicher gestellt. Im ersten Beispiel wurde die vom Auftraggeber geforderte Präzision dadurch erreicht, dass systematische Voruntersuchungen stattfanden. Die Übertragung der Lokalisierung direkt auf die Betonoberfläche stellte sicher, dass keinen Informationsverluste an die nachfolgenden Aufgaben auftraten. Das zweite Beispiel zeigt den Nutzen von Automatisierung und Kombination von Verfahren. Damit können dem Auftraggeber die notwendigen Angaben über Einbauteile mit großer Detaitreue und leicht verständlicher Visualisierung aufbereitet werden. Der abschließende Bericht zeigt, wie vorhandene Auswertungen sinnvoll durch noch in der Forschung befindliche Ansätze bereichert werden. Insgesamt ist die zerstörungsfreie Prüfung in der Lage, an Brücken preisrelevante Fragestellungen zu lösen. Voraussetzung hierfür ist eine sorgfältig geplante Vorgehensweise und ein sicheres Verständnis der Grundlage der eingesetzten Geräte und Auswertungsschritte. T2 - 1. Brückenkolloquium - Beurteilung, Ertüchtigung und Instandsetzung von Brücken CY - Ostfildern/Stuttgart, Germany DA - 24.06.2014 PY - 2014 SP - Paper 00_08, 1 EP - 8 AN - OPUS4-31032 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Keserovic, Amela T1 - Geothermal systems in Indonesia - Influence on the corrosion resistance of stainless steel materials N2 - The growth in a global demand for energy, as well as the awareness of a significant climate change, have evolved a very strong incentive for utilizing and expanding the use of clean and renewable energy resources. Geothermal energy is considered as one of a few alternatives ideal for replacing conventional sources due to its consistency and reliability, and is receiving ever more attention. However, geothermal Systems are found to be the most aggressive natural environments in terms of corrosion. High temperature and pressure conditions, as well as the existence of almost an entire periodic System of elements in form of corrosive salts, present a major threat to the integrity of the construction material. Therefore, in order to achieve a safer and continuous energy production, and increase the competitiveness of geothermal energy on the world scene, a comprehensive assessment of the materials suitability is of high importance for operators and vendors. Finally, thäs would lead to an inoreased lifespan of the power plant, as well as its economic profit, due to the reduced maintenance costs. KW - Geothermal energy KW - Indonesia KW - Carbon steel KW - Stainless steel KW - Corrosion PY - 2014 SP - 1-130, A1-A34 CY - Berlin AN - OPUS4-31033 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bork, Claus-Peter A1 - Wolf, Marcus A1 - Pfennig, A. A1 - Trenner, S. A1 - Wiegand, Reiner T1 - Comparison between X5CrNiCuNb16-4 and X46Cr13 under corrosion fatigue N2 - In geothermal power plants materials e.g. pumps are exposed to extremely corrosive thermal water. This results in corrosion fatigue and so inevitably the reduction of the lifetime of these components. Also in the field of the carbon dioxide storage technology (carbon capture and storage CCS) components are exposed to a corrosive environment and mechanical stress. In order to gain knowledge upon the corrosion fatigue strength of materials a corrosion chamber for "in situ" conditions was designed and successfully applied.Two different steels X46Cr13 and X5CrNiCuNb16-4 have been tested and their corrosion fatigue behavior was compared. To simulate the frequency of operating pumps (30 – 40 Hz) a resonant testing machine was used. In addition technical CO2 was introduced into the closed system at a rate close to 9 L/h to keep stable environmental conditions. The samples have a surface roughness of Rz = 4 to simulate technical machined surfaces. The calculated tensile strength of X46Cr13 with soft annealed microstructure (coagulated cementite in ferrite-perlite matrix) is about 680 MPa and the yield strength is about 345 MPa. The tensile strength of X5CrNiCuNb16-4 is about 1078 MPa and the yield strength about 928 MPa. Testing parameters are: corrosion media: saline aquifer water (Stuttgart Aquifer) temperature of the brine at 60 °C and load ratio of R=-1. For X46Cr13 a stress amplitude between 160 MPa to 270 MPa and for X5CrNiCuNb16-4 a stress amplitude between 150 to 500 was chosen. Cycles until crack initiation differ strongly and were found to start at 5 x 104 up to 12.5 x 106 cycles.X46Cr13 has reached a maximum number of cycles (12.5 x 106) at a stress amplitude of 173 MPa. X5CrNiCuNb16-4 has reached the maximum number of cycles (10 x 106) at a stress amplitude of 150 MPa. The range of scatter for X5CrNiCuNb16-4 is very high (1:34) in comparison the range of scatter for X46Cr13 (1:3.5). T2 - Corrosion 2014 CY - San Antonio, TX, USA DA - 09.03.2014 KW - Steel KW - Corrosion chamber KW - Geothermal power KW - CCS KW - Corrosion fatigue PY - 2014 SP - Paper 3776, 1 EP - 6 PB - NACE AN - OPUS4-31085 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, A. A1 - Bork, Claus-Peter A1 - Wolf, Marcus T1 - Design of a high pressure system for in-situ tests on the corrosion fatigue of metallic materials N2 - In geothermal power plants pumps are exposed to corrosive and oscillating loads. This leads to corrosion fatigue and reduces the lifetime of certain components. Usually underwater power pumps are placed inside the borehole. In this case an installation depth of 600 to 800 meters below ground level is typical. In these depths an additional load due to high pressure and high temperature is introduced which is based on geothermal brine. Therefore the material which is used for the pump is steel.For fatigue testing at loads existing in deep geological layers an appropriate system for fatigue tests under in-situ conditions was set up. The requirements of the design are: temperature of the corrosion medium of 200 °C pressure of 200 bars and the complete immersion of the specimen in flowing corrosion medium containing mixtures of corrosive gasses during the entire test period.The test system has three main components the corrosion chamber the heating module and the reservoir. It is important that the corrosion chamber is only fixed onto the specimen which allows for highest flexibility of the test system operational in many different test machines. The heating module heats the corrosion medium up to 200 °C. The reservoir make sure that the volume of the corrosion medium satisfies requirements of the DIN 50905 Part 1 is conformed providing minimum required corrosive medium of 10 ml/cm² in relation to the sample surface.This innovative fatigue test system aims at performing in- situ fatigue corrosion tests simultaneously at high pressure and high temperature in liquid and gaseous corrosive environment. Results from the tests will allow determining the fatigue life of several materials influenced by pressure and temperature under corrosive conditions. T2 - Corrosion 2014 CY - San Antonio, TX, USA DA - 09.03.2014 KW - High pressure KW - Corrosion fatigue KW - Corrosion chamber PY - 2014 SP - Paper 3775, 1 EP - 6 AN - OPUS4-31086 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Musolff, André A1 - Quercetti, Thomas A1 - Müller, Karsten A1 - Droste, Bernhard A1 - Gründer, Klaus-Peter T1 - Experimental testing of impact limiters for RAM packages under drop test conditions N2 - In context with new cask designs and their approval procedure, the experimental testing of impact limiters under drop test conditions becomes more and more important in order to assess the damage mechanics behaviour and safety margins for validation reasons. In recent years, various designs of impact limiters have been tested by the Federal Institute for Materials Research and Testing within specific component testing and particularly with regard to type B package design approval procedures. The paper focuses on the experimental realisation of impact limiter tests and presents implemented measurement techniques to determine the amount of deformation and to explain the impact behaviour by means of photogrammetric metrology and three-dimensional fringe projection method, high speed motion analysis and adjusted deceleration measurements. T2 - PATRAM 2013 - 17th International symposium on the packaging and transportation of radioactive materials CY - San Francisco, CA, USA DA - 18.08.2013 KW - Drop test KW - Impact limiters KW - RAM packages KW - Measurement methods PY - 2013 SP - 1 EP - 9 PB - Omnipress AN - OPUS4-31040 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schilling, O. A1 - Müller, Lars A1 - Ballheimer, Viktor A1 - Komann, Steffen A1 - Wille, Frank T1 - Analytical approaches within the assessment strategy of numerical analyses of components of RAM packages N2 - Load attachment points, consisting of the lifting component and corresponding bolt connections, and lid systems, consisting of a lid, gaskets and bolt connections, are usually analyzed numerically using the Finite Element Method. Reasons for applying the FEM are complex geometry, specific load distribution and the violation of application criteria for analytical approaches. For example the elementary beam theory is not suitable for the calculation of compact trunnions and the Kirchhoff plate theory is not suitable for the calculation of lids with a large thickness to diameter ratio because the Bernoulli-hypothesis is violated. In addition for structural integrity assessments often local stress and for the evaluation of lid systems tightness local contact opening are needed, which can be obtained only through accurately discretized numerical models. Independent comparative calculations are essential for complex calculations. Simplified but appropriate analytical approaches are an efficient way of examination. Is it possible to provide conservative analytical estimates of such kind of analysis problems? Are analytical calculations an appropriate approach in today's authority assessment business? Using the example of bolted trunnion and lid systems of a heavy package the possibilities and limits of analytical comparative calculations are shown. T2 - PATRAM 2013 - 17th International symposium on the packaging and transportation of radioactive materials CY - San Francisco, CA, USA DA - 18.08.2013 PY - 2013 SP - Paper 217, 1 EP - 9 PB - Omnipress AN - OPUS4-31048 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Becker, Gerhard Wilhelm ED - Erismann, Theodor H. T1 - Technik und Kunst PY - 1982 SP - 7 EP - 22 CY - Dübendorf AN - OPUS4-35983 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Becker, Gerhard Wilhelm A1 - Neider, Rudolf T1 - Scientific and Economic Importance of Reference Materials (RM's) T2 - International Symposium on the Production and Use of Reference Materials CY - Japan DA - 01.01.1982 PY - 1982 SP - 60 EP - 63 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-35987 LA - zho AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schimmelwitz, Peter T1 - Verfahren zur Trockenlegung von Mauerwerk T2 - Sitzung des Arbeitskreises "Naturwissenschaftliche Forschung an Kunstgütern aus Stein" CY - Dortmund-Bövinghausen DA - 30.03.1981 PY - 1981 SP - 5 EP - 19 AN - OPUS4-36084 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Brandes, Klaus T1 - Experimental evaluation of the mechanical behaviour of RC structural members under impact load at Bundesanstalt für Materialprüfung (BAM), Berlin PY - 1982 IS - 20 SP - 5 EP - 7 AN - OPUS4-36091 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Brandes, Klaus T1 - Energieaufnahmevermögen von Stahlbetonbauteilen bei Stoßeinwirkung PY - 1982 VL - GRS-F-114, GRS-F-119 SP - 150460/1 EP - 150460/3 CY - Köln AN - OPUS4-36092 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Brandes, Klaus T1 - Energy absorption capacity of reinforced concrete structural members under impact force T1 - Energieaufnahmevermögen von Stahlbetonbauteilen bei Stoßeinwirkung PY - 1982 VL - GRS-F-115 SP - 150460/1 EP - 150460/3 CY - Köln AN - OPUS4-36093 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Brandes, Klaus T1 - Experimental studies concerning energy absorption of reinforced concrete members subjected to impact load (closed loop testing) T1 - Das Tragverhalten quergestoßener Stahlbetonbauteile bei geregeltem Stoßkraft-Zeit-Verlauf PY - 1982 VL - GRS-F-114, GRS-F-115, GRS-F-119 SP - RS 121/1 EP - RS 121/3 CY - Köln AN - OPUS4-36101 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Österle, Werner A1 - Gesatzke, W. T1 - Dislocation particle interaction during secondary hardening and yielding of HSLA steel T2 - Riso International Symposium on Metallurgy and Material Science CY - Roskilde, Denmark DA - 05.09.1983 PY - 1983 SP - 473 EP - 478 AN - OPUS4-36051 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Isecke, Bernd T1 - The influence of practical conditions on hydrogen embrittlement of high strength steels for prestressed concrete T2 - International Congress on Hydrogen and Materials 3 CY - Paris, France DA - 07.06.1982 PY - 1982 SP - 1043 EP - 1048 CY - Paris AN - OPUS4-36035 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Aurich, Dietmar A1 - Helms, Rolf A1 - Zaminer, Christian T1 - Ductility and Microstructure of Ferritic Cast Iron with Nodular Graphite T2 - European Conference on Fracture 4 CY - Leoben, Austria DA - 22.09.1982 PY - 1982 VL - Vol. 1: Fracture and fracture toughness SP - 288 EP - 295 CY - Warley AN - OPUS4-36004 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brocks, Wolfgang A1 - Brückner, Udo T1 - Untersuchung der Rißöffnung einer CT 100-Probe bei Be- und Entlastung mit Hilfe von elastisch-plastischen 3 D-FE-Rechnungen T2 - 13. Sitzung des Arbeitskreises Bruchvorgänge CY - Hannover, Germany DA - 06.10.1981 PY - 1982 SP - 38 EP - 45 CY - Berlin AN - OPUS4-36012 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stichel, Wolfgang T1 - Innen- und Außenkorrosion an Heizungsinstallationen T2 - 10. Fachtagung Krankenhaustechnik CY - Hannover, Germany DA - 25.03.1982 PY - 1982 SP - 245 EP - 251 CY - Hannover AN - OPUS4-36065 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stichel, Wolfgang T1 - Korrosion in der Trinkwasserinstallation T2 - 10. Fachtagung Krankenhaustechnik CY - Hannover, Germany DA - 25.03.1982 PY - 1982 SP - 109 EP - 117 CY - Hannover AN - OPUS4-36067 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Olschewski, Jürgen T1 - Numerische Untersuchungen zur Frage der Fließbedingung beim gekerbten Biegebalken T2 - 13. Sitzung des Arbeitskreises Bruchvorgänge CY - Hannover, Germany DA - 06.10.1981 PY - 1982 SP - 20 EP - 27 CY - Berlin AN - OPUS4-36014 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schlick-Hasper, Eva A1 - Goedecke, Thomas A1 - Kraume, M. ED - Ziegahn, K.-F. T1 - Dichtheitsprüfung unter Verwendung von Prüfgasen N2 - Ziel einer Dichtheitsprüfung ist es entweder, mit einem quantitativen Prüfverfahren integrale Leckageraten zu messen, oder mittels eines lokalisierenden Verfahrens den genauen Leckageort aufzuspüren. In einigen Fällen kann das Betriebsmedium gleichzeitig das Prüfmedium sein, wenn geeignete Sensorik zu Verfügung steht. In anderen Fällen kann dies aus unterschiedlichen Gründen nicht möglich sein. Daher ersetzt man bei der Verwendung von Prüfgasverfahren das Betriebsmedium durch ein spezifisch nachweisbares Prüfgas. Für die Interpretation eines quantitativen Messergebnisses ist es notwendig, die Ist-Leckagerate mit einer zuvor berechneten Grenzleckagerate (maximal zulässige Leckagerate) zu vergleichen. Entspricht das für die Dichtheitsprüfung verwendete Prüfgas nicht dem Betriebsmedium, so ist hierfür eine Umrechnung von Leckageraten notwendig. Es wird ein Überblick über für die Dichtheitsprüfung gängige Prüfgase, deren Eigenschaften sowie Vor- und Nachteile gegeben. Die grundlegenden Prinzipien bei der Umrechnung von Leckageraten (Druckumrechnung; Temperaturumrechnung; Umrechnung der Gasart bzw. des Mediums) werden vorgestellt. T2 - 45. Jahrestagung der Gesellschaft für Umweltsimulation (GUS) CY - Stutensee-Blankenloch, Germany DA - 16. März 2016 KW - Dichtheit KW - Dichtheitsprüfung KW - Prüfgase KW - Dichtheitsprüfverfahren PY - 2016 SN - 978-3-9816286-7-8 SP - 223 EP - 237 AN - OPUS4-36151 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Forler, D. A1 - Schmidt, J. P. A1 - Staude, Andreas T1 - Ein Becken aus Beckentin! - Fund des Monats Mai 2016 N2 - Bronzezeitlicher Hortfund in Mecklenburg-Vorpommern mit CT-Untersuchung an der BAM KW - Computertomographie KW - Hortfund KW - Bronzezeit KW - Mecklenburg-Vorpommern PY - 2016 UR - http://www.kulturwerte-mv.de/cms2/LAKD1_prod/LAKD1/de/Landesarchaeologie/Fund_des_Monats/index.jsp SP - 1 EP - 3 CY - Schwerin AN - OPUS4-36163 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzlöhner, Ulrich T1 - Setzung von Fundamenten infolge dynamischer Last T2 - Arbeitssitzung "Oberbaudynamik, Untergrund Rad/Schiene und Zusammenwirkung Fahrzeug - Fahrweg CY - Berlin, Germany DA - 17.09.1981 PY - 1982 SP - 1 EP - 11 CY - Frankfurt AN - OPUS4-36126 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzlöhner, Ulrich A1 - Rücker, Werner T1 - Dynamische Rückwirkung des Gleisoberbaus: Erstellung eines diskreten Modells mit Hilfe der analytischen Methode T2 - Arbeitssitzung "Oberbaudynamik, Untergrund Rad/Schiene und Zusammenwirkung Fahrzeug - Fahrweg CY - Berlin, Germany DA - 17.09.1981 PY - 1982 SP - 1 EP - 30 CY - Frankfurt AN - OPUS4-36127 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rücker, Werner T1 - Analysis of dynamic structure-soil-structure interaction problems by a continuum model T2 - 7th European Conference on Earthquake Engineering CY - Athens, Greece DA - 20.09.1982 PY - 1982 SP - 1 EP - 10 CY - Athen AN - OPUS4-36128 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Wegener, Peter A1 - Schulze, W. T1 - Ermittlung der Tragfähigkeit von Klemmkupplungen aus Stahl an Gerüstrohren aus Aluminium PY - 1982 VL - T 756 SP - 1 EP - 75 CY - Stuttgart AN - OPUS4-36117 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dietrich, Th. ED - Vermeer, P. A. ED - Luger, H. J. T1 - Incremental parabolic hardening of psammic material; Application to laterally loaded piles in sand T2 - IUTAM-Conference on Deformation and Failure of Granular Materials CY - Delft, The Netherlands DA - 31.08.1982 PY - 1982 SN - 90-6191-224-5 SP - 13 EP - 22 PB - Balkema CY - Rotterdam AN - OPUS4-36118 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dietrich, T. A1 - Holzlöhner, Ulrich A1 - Lehnert, Jan ED - Verruijt, A. ED - Beringen, F. L. ED - de Leeuw, E. H. T1 - Prediction of settlements and bearing capacities of shallow foundations by self-similar penetration T2 - Second European Symposium on Penetration Testing CY - Amsterdam, The Netherlands DA - 24.05.1982 PY - 1982 SN - 90-6191-250-4 SP - 561 EP - 566 PB - Balkema CY - Rotterdam AN - OPUS4-36119 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dolling, Hans-Joachim A1 - Dietrich, Th. T1 - Sackungen des Gleises - untere Schranken T2 - Arbeitssitzung "Oberbaudynamik, Untergrund Rad/Schiene und Zusammenwirkung Fahrzeug - Fahrweg CY - Berlin, Germany DA - 17.09.1981 PY - 1982 SP - 1 EP - 24 CY - Frankfurt AN - OPUS4-36125 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Madia, Mauro A1 - Zerbst, Uwe A1 - Kiyak, Yusuf A1 - Schork, B. T1 - Ermittlung der Wöhlerkurve von Schweißbindungen mittels bruchmechanischer Methoden N2 - IBESS steht für „Integrale Bruchmechanische Ermittlung der Schwingfestigkeit von Schweißverbindungen“ und ist das Ergebnis eines DFG-AiF-Clusters, an dem acht Partner beteiligt waren. Kernstück ist eine analytische Methode zur bruchmechanischen Beschreibung der Rissausbreitung unter Schwingbelastung, die im IBESS-Teilprojekt A3 entwickelt wurde. Da man es im Bereich der Schwingfes-tigkeit mit kurzen Rissen zu tun hat, auf die die etablierten Methoden der Langriss-bruchmechanik nicht anwendbar sind, wurden Lösungen entwickelt, die es erlauben, sowohl die rissnahen Plastizitätsverhältnisse als auch die mit wachsendem Riss gra-duell zunehmenden Rissschließeffekte quantitativ zu beschreiben. Unter Einbeziehung der sogenannten „zyklischen R-Kurve“, deren experimentelle Methodik ebenfalls im Rahmen des Projekts weiterentwickelt wurde, ist es zudem möglich, Ausgangsrissgrö-ßen vorherzusagen, die auf Dauerfestigkeitsniveau gerade so noch arretieren würden. Dies erlaubt umgekehrt eine Abschätzung der Dauerfestigkeit an den Schweißverbin-dungen sowie die statistisch basierte, analytische Vorhersagen des Zeitfestigkeitsas-tes der Wöhlerkurve. In diesem Aufsatz wird die Methodik vorgestellt und ihre Validie-rung an einem ausgewählten Beispiel diskutiert. T2 - 48. Tagung des Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Freiburg, Germany DA - 16.02.2016 KW - Ermüdungsrissausbreitung KW - Schwingfestigkeit KW - Schweißverbindungen PY - 2016 SN - 2366-4797 VL - Bericht 248 SP - 211 EP - 224 AN - OPUS4-36186 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pastuska, Gerhard A1 - Lützow, Wolfgang A1 - Wissmann, R. T1 - Konstitution und Eigenschaften von Erzeugnissen aus Recyclingmaterial T2 - Recycling von Kunststoffabfällen : 10. Kolloquium CY - Aachen, Germany DA - 03.12.1982 PY - 1982 SN - 0172-7818 VL - 34 SP - 59 EP - 80 CY - Aachen AN - OPUS4-36190 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sickfeld, Jürgen T1 - Progress Report on IUPAC's Supported Polymer Films Group PY - 1982 SN - 0361-8773 VL - 54 IS - 688 SP - 20 EP - 30 CY - Easton AN - OPUS4-36192 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sickfeld, Jürgen A1 - Heinze, B. T1 - Differential thermal analysis of epoxy reins in a temperature range above 200°C T2 - VIIIth International Conference in Organic Coatings Science and Technology CY - Athens, Greece DA - 12.07.1982 PY - 1982 SP - 541 EP - 581 CY - Athen AN - OPUS4-36194 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meckel, Lothar ED - Aurand, K. ED - Seifert, B. ED - Wegner, J. T1 - Teppichbeläge und Luftverunreinigung? T1 - Carpeting and air pollution? T2 - Kolloquium "Luftqualität in Innenräumen" CY - Berlin, Germany DA - 01.10.1981 PY - 1982 SN - 3-437-30376-7 SP - 129 EP - 136 PB - Fischer CY - Stuttgart AN - OPUS4-36198 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Trubiroha, Peter T1 - Die Alterung von Strahlern in Bewitterungsgeräten und ihre Auswirkungen auf Bewitterungsergebnisse T2 - Hanauer Symposium CY - Hanau, Germany DA - 05.05.1981 PY - 1982 SP - 1 EP - 9 PB - Heraeus CY - Hanau AN - OPUS4-36174 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - August, Hans A1 - Tatzky, Renate A1 - Pastuska, Gerhard A1 - Win, Tin T1 - Untersuchung des Permeationsverhaltens von handelsüblichen Kunststoffdichtungsbahnen als Deponiebasisabdichtung gegenüber Sickerwasser, organischen Lösungsmitteln und deren wäßrige Lösungen N2 - Zur Basisabdichtung von Mülldeponien werden zunehmend polymere Abdichtungen mit Foliendecken zwischen 1 und 3 mm eingesetzt, die vielfach als absolut dicht gegenüber Sickerwässer und deren Inhaltsstoffen gelten. Durch Permeationsvorgänge ist jedoch mit Restdurchlässigkeiten zu rechnen, die auch bei technisch einwandfreien, intakten Folien auftreten. Es werden Meßmethoden vorgestellt, derartige Restdurchlässigkeitsraten an handelsüblichen Dichtungsbahnen für Deponiebasisabdichtungen zu messen. Als Permeenten dienen neben Sickerwasser aus einer Hausmülldeponie, konzentrierte, reine organische Lösungsmittel, deren Gemische untereinander und stark verdünnte Lösungen organischer Lösungsmittel in Wasser. Meßergebnisse werden angegeben und diskutiert. KW - Müll KW - Abfall KW - Ablagerung KW - Deponie KW - Sickerwasser KW - Grundwasserschutz KW - Umweltschutz KW - Polymere Deponiebasisabdichtungen KW - organische Lösungsmittel KW - Permeation KW - Experimentelle Ergebnisse PY - 1984 SP - 1 EP - 108 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-35914 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sporea, D. A1 - Mihai, L. A1 - Negut, Daniel A1 - Stajanca, Pavol A1 - Krebber, Katerina ED - Kalli, K. ED - Mendez, A. T1 - On-line monitoring of gamma irradiated perfluorinated polymer optical fiber N2 - In this paper, we present the first results regarding the on-line monitoring of gamma-ray exposure effects on a commercial multi-mode perfluorinated polymer optical fiber (PF-POF), type GigaPOF-50SR from Chromis Fiberoptics. Our focus was to evaluate on-line the radiation induced attenuation (RIA) over a wide spectral range (320 nm – 1700 nm), in order to assess the fiber’s radiation hardness and its possible use in radiation detection. An Ocean Optics QE65000 high sensitivity spectrometer and a StellarNet near-IR spectrometer were used to cover the spectral ranges 200 nm – 1μm and 900 nm – 1.6 μm, respectively. Electron paramagnetic resonance was used to monitor the recovery of the irradiation induced centers at room temperature. The study indicated that the optical fiber can be used as radiation monitor at low dose rates by measuring the attenuation in the UV, while higher dose rates irradiation can be observed by RIA monitoring at specific wavelengths in the visible spectral range. T2 - Photonics Europe 2016, Micro-Structured and Specialty Optical Fibers IV CY - Brussels, Belgium DA - 03.04.2016 KW - electron paramagnetic resonance spectroscopy KW - Perfluorinated polymer optical fiber KW - radiation effects KW - gamma irradiation KW - radiation hardness KW - radiation induced attenuation KW - radiation dosimetry PY - 2016 DO - https://doi.org/10.1117/12.2230688 VL - 9886 SP - 98861Q-1 EP - 98861Q-6 PB - SPIE CY - Bellingham, USA AN - OPUS4-35927 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fasano, A. A1 - Woyessa, G. A1 - Stajanca, Pavol A1 - Markos, C. A1 - Stefani, A. A1 - Nielsen, K. A1 - Rasmussen, H. K. A1 - Krebber, Katerina A1 - Bang, O. ED - Kalli, K. ED - Mendez, A. T1 - Creation of a microstructured polymer optical fiber with UV Bragg grating inscription for the detection of extensions at temperatures up to 125°C N2 - We describe the fabrication of a polycarbonate (PC) micro-structured polymer optical fiber (mPOF) and the writing of fiber Bragg gratings (FBGs) in it to enable strain and temperature measurements. We demonstrate the photosensitivity of a dopant-free PC fiber by grating inscription using a UV laser. We further show that PC Bragg gratings can be extended up to at least 3% without affecting the initial functionality of the micro-structured fiber. The response of PC FBGs to temperature up to 125°C is also investigated. Polycarbonate has good mechanical properties and its high temperatureresistance might extend the range of application of polymeric FBGs. T2 - Photonics Europe 2016, Micro-Structured and Specialty Optical Fibres IV CY - Brussels, Belgium DA - 03.04.2016 KW - fiber Bragg gratings KW - Polycarbonate KW - polymers KW - micro-structured polymer optical fibers KW - UV laser inscription KW - optical fiber sensors PY - 2016 DO - https://doi.org/10.1117/12.2227843 VL - 9886 SP - 988619-1 EP - 988619-6 PB - SPIE AN - OPUS4-35928 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Smailos, E. A1 - Stichel, Wolfgang A1 - Köster, R. T1 - Korrosionsuntersuchungen und mechanische Prüfungen an metallischen Werkstoffen zur Auslegung von Behältern für verglaste, hochradioaktive Abfälle als Barriere im Endlager N2 - Zur Ermittlung geeigneter Materialien für die Auslegung von HAW-Behältern als Barriere im Endlager wurden selektierende Korrosionsuntersuchungen und mechanische Prüfungen an verschiedenen metallischen Werkstoffen durchgeführt. Neben den Cr-Ni-Stählen, die entsprechend dem bisherigen Konzept als Kokillenwerkstoff vorgesehen sind, wurden drei Nickelbasislegierungen und ein Baustahl sowie die Werkstoffe Ti 99,8 – Pd und der Stahl X 1Cr MoTi 182 (ELA-Ferrit) untersucht. Da im Rahmen von Störfallbetrachtungen für ein Endlager im Salinar als potentielles Korrosionsmedium Salzlösungen betrachtet werden, erfolgten die Korrosionsprüfungen unter selektierenden Bedingungen in einer quinären Salzlösung bei 170°C und 1 bar. Die mechanischen Prüfungen zeigten, daß die Nickelbasislegierungen und die meisten Cr-Ni-Stähle durch Schweißen bzw. Wärmebehandlung geringe Änderungen ihrer mechanischen Eigenschaften erfahren. Damit wurde belegt, daß diese Materialien als Kokillenwerkstoff geeignet sind. Eine Barrierenfunktion kann von den Cr-Ni-Stählen wegen ihrer hohen Anfälligkeit gegen lokale Korrosionsangriff, insbesondere gegen Spannungsrißkorrosion (SpRK) nicht übernommen werden. Die Werkstoffe Inconel 625, Incoloy 825, ELA-Ferrit und Ti-Pd waren gegen SpRK beständig, jedoch sind diese Materialien gegen Lochkorrosion anfällig. Eine hohe Beständigkeit gegen lokale Korrosionsangriffe zeigten die Werkstoffe Hastelloy C4 und der Feinkornbaustahl. Der Werkstoff Hastelloy C4 zeigte nach einer Versuchszeit von 432 Tagen einen gleichmäßigen Korrosionsabtrag von weniger als 0,03 mm/a. Die Abtragungsrate bei dem Baustahl 1.0566 betrug weniger als 0,25 mm/a für den Ausgangswerkstoff und weniger als 0,5 mm/a für den wärmebehandelten Werkstoff. Die vorliegenden Ergebnisse der selektierenden Untersuchungen zeigten, daß beispielsweise mit Hastelloy C4 die Auslegung des HAW-Behälters als Barriere realisierbar ist und damit unter Beibehaltung des heutigen Borosilikatglases ein zusätzlicher Schutz gegen eine Mobilisierung von Radionukliden beim potentiellen Angriff von Salzlösungen erreicht werden kann. KW - Behältermaterialien KW - Mechanische Prüfungen KW - Korrosionsuntersuchungen PY - 1981 SN - 0303-4003 IS - KfK 3230 SP - 1 EP - 66 PB - Kernforschungszentrum Karlsruhe CY - Karlsruhe AN - OPUS4-35908 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Münchow, Paul T1 - Entwicklung eines spektralanalytischen Multielementverfahrens zur schnellen sequentiellen Bestimmung umweltrelevanter Metalle in Abwässern N2 - Mit der Plasmaspektrometrie (ICP) wurden in Abwässern aus dem Berliner Abwassersystem simultan 11 Elemente (Al, B, Ba, Cr, Cu, Fe, Mn, Ni, P, Ti, Zn) bestimmt. Der erforderliche Arbeitsaufwand ist erheblich geringer als nach Deutschen Einheitsverfahren zur Abwasseruntersuchung. Bestimmungsgrenzen werden mitgeteilt, auf systematische Fehlermöglichkeiten wird eingegangen. Durch Eindampfen der Proben lassen sich die Nachweisgrenzen in den meisten Fällen um den Faktor 10 weiter senken. Die Hydridtechnik zur Verbesserung der Nachweisempfindlichkeit bei den Elementen Sn, As, Sb, Se erwies sich in der Abwassermatrix als problematisch. KW - Abwasser KW - chemische Analyse KW - Schwermetalle KW - ICP PY - 1984 IS - UBA-FB 84-082 SP - 1 EP - 83 AN - OPUS4-35913 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gaal, Mate A1 - Bartusch, Jürgen A1 - Schadow, Florian A1 - Köppe, Enrico A1 - Dohse, Elmar ED - Chimenti, D. E. ED - Bond, L. J. T1 - Focusing of ferroelectret air-coupled ultrasound transducers N2 - Air-coupled ultrasound has been applied increasingly as a non-destructive testing method for lightweight construction in recent years. It is particularly appropriate for composite materials being used in automotive and aviation industry. Air-coupled ultrasound transducers mostly consist of piezoelectric materials and matching layers. However, their fabrication is challenging and their signal-to-noise ratio often not sufficient for many testing requirements. To enhance the efficiency, air-coupled ultrasound transducers made of cellular polypropylene have been developed. Because of its small density and sound velocity, this piezoelectric ferroelectret matches the small acoustic impedance of air much better than matching layers applied in conventional transducers. In our contribution, we present two different methods of spherical focusing of ferroelectret transducers for the further enhancement of their performance in NDT applications. Measurements on carbon-fiber-reinforced polymer (CFRP) samples and on metal adhesive joints performed with commercially available focused air-coupled ultrasound transducers are compared to measurements executed with self-developed focused ferroelectret transducers. T2 - 42nd Annual Review of Progress in Quantitative Nondestructive Evaluation CY - Minneapolis, Minnesota, USA DA - 26.07.2015 KW - Ferroelectret KW - Transducer KW - Air-coupled KW - Ultrasonic KW - Focusing PY - 2016 SP - 080001 PB - AIP Publishing CY - Melville, NY, USA AN - OPUS4-35955 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Aurich, Dietmar A1 - Brocks, Wolfgang A1 - Noack, Hans-Dieter A1 - Veith, Helmut T1 - Erörterung von Bruchmechanik-Konzepten für Reaktorkomponenten anhand elastisch-plastischer FE-Analysen T2 - Jahrungstagung Kerntechnik '83 CY - Berlin, Germany DA - 14. Juni 1983 PY - 1983 VL - 83 SP - 390 EP - 393 AN - OPUS4-35968 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Aurich, Dietmar A1 - Brocks, Wolfgang A1 - Noack, Hans-Dieter A1 - Veith, Helmut T1 - Bruchmechanik - Analyse eines Druckbehälters mit halbelliptischem Innenriss über eine dreidimensionale elastisch-plastische FE-Rechnung T1 - Fracture Analysis of a Pressure Vessel with a Semi-Elliptical Surface Crack by Three-Dimensional Elastic-Plastic Finite Element Calculations T2 - MPA-Seminar (8) Sicherheit der Druckführenden Umschliessung von LWR CY - Stuttgart, Germany DA - 14.10.1982 PY - 1982 SP - 1 EP - 34 CY - Stuttgart AN - OPUS4-36000 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Aurich, Dietmar A1 - Helms, Rolf A1 - Veith, Helmut A1 - Wobst, Klaus T1 - Abschätzung der Anwendungsgrenzen des Kollapskonzeptes mittels des Kerbschlagversuches T2 - 13. Sitzung des Arbeitskreises Bruchvorgänge CY - Hannover, Germany DA - 06.10.1981 PY - 1982 SP - 173 EP - 186 CY - Berlin AN - OPUS4-36002 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Künecke, Georgia A1 - Olschewski, Jürgen A1 - Zelewski, Mirjana T1 - FEM-Untersuchungen zum Größeneinfluß bei CT-Proben T2 - Sitzung des DVM-Arbeitskreises Bruchvorgänge CY - Karlsruhe DA - 01.01.1984 PY - 1984 VL - 1984 (16) SP - 151 EP - 160 CY - Berlin AN - OPUS4-36269 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brocks, Wolfgang A1 - Künecke, Georgia A1 - Noack, Hans-Dieter T1 - Comparative Elastic-Plastic Analyses of Cracked Structures and Specimens T2 - 3rd Conf. on Numerical Methods in Fracture Mechanics CY - Swansea, UK DA - 26.03.1984 PY - 1984 VL - 3 SP - 363 EP - 375 PB - Pineridge Press CY - Swansea AN - OPUS4-36257 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Isecke, Bernd T1 - Failure Analysis of the Collapse of the Berlin Congress Hall T2 - Meeting on Corrosion of Reinforcement in Concrete Construction CY - London, England DA - 13.06.1983 PY - 1983 SP - 79 EP - 89 AN - OPUS4-36290 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kny, Uwe A1 - Kühne, Helmut T1 - Suitability of different termite species for laboratory testing T2 - Annual Meeting. International Research Group on Wood Preservation - Sub-group 4 Termites attacking wood CY - Cesme, Turkey DA - 24.05.1982 PY - 1982 VL - IRG/WP/1159 SP - 1 EP - 14 CY - Cesme AN - OPUS4-36297 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brocks, Wolfgang A1 - Noack, Hans-Dieter A1 - Veith, Helmut A1 - Erbe, H.-H. T1 - Elastic-Plastic Analysis of a Nozzle Corner Crack by the Finitie-Element Method T2 - Elastic-Plastic Fracture: Second Symposium CY - Philadelphia, PA, USA DA - 01.01.1984 PY - 1984 VL - SPT 803/1 SP - 240 EP - 255 CY - Philadelphia AN - OPUS4-36247 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Engel, Günter A1 - Heinsohn, Günter T1 - Systematische Untersuchungen über die Bildung gefährlicher Mengen explosionsfähiger Gemische in geschlossenen Räumen T2 - 8. Internationales Kolloquium über die Verhütung von Arbeitsunfällen und Berufskrankheiten in der chemischen Industrie CY - Frankfurt am Main, Germany DA - 07.06.1982 PY - 1982 SP - 633 EP - 647 CY - Heidelberg AN - OPUS4-36230 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Brookes, S. A1 - Scholz, A. A1 - Klingelhöffer, Hellmuth A1 - Whittaker, M. A1 - Loveday, M. A1 - Wisby, A. A1 - Ryder, N. A1 - Lohr, R. A1 - Stekovic, S. A1 - Moverare, J. A1 - Holdsworth, S. A1 - Dudzinski, D. T1 - Code of practice for force-controlled thermo-mechanical fatigue testing N2 - Components in the Aerospace, Power and Automotive engineering sectors are frequently subjected to cyclic stresses induced by thermal fluctuations and mechanical loads. For the design of such components, reliable material property data are required which need to be acquired using well accepted and reproducible test procedures for thermo-mechanical fatigue (TMF) loading. Available materials TMF property data are limited so that there is a need for further TMF data generated by TMF testing. The TMF behaviour of materials is often desired to be simulated in models which describe the cyclic stress-strain behaviour, the fatigue life and the cyclic crack growth behaviour. There is a continuous need for the development and amendment of such models. Models can be validated by using materials in industrial applications which are subjected to TMF loading. KW - Force controlled TMF testing PY - 2015 UR - http://www.tmf-workshop.bam.de/en/tmf_media/code_of_practice_for_force_controlled_thermo-mechanical_fatigue_(2).pdf SP - 1 EP - 32 AN - OPUS4-35248 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Geilert, Sonja A1 - Vogl, Jochen A1 - Rosner, M. A1 - Voerkelius, S. A1 - Eichert, T. T1 - Boron isotope fractionation in bell pepper N2 - Various plant compartments of a single bell pepper plant were studied to verify the variability of boron isotope composition in plants and to identify possible intra-plant isotope fractionation. Boron mass fractions varied from 9.8 mg/kg in the fruits to 70.0 mg/kg in the leaves. Boron (B) isotope ratios reported as δ11B ranged from -11.0‰ to +16.0‰ (U ≤ 1.9‰, k=2) and showed a distinct trend to heavier δ11B values the higher the plant compartments were located in the plant. A fractionation of Δ11Bleaf-roots = 27‰ existed in the studied bell pepper plant, which represents about about 1/3 of the overall natural boron isotope variation (ca. 80‰). Two simultaneous operating processes are a possible explanation for the observed systematic intra-plant δ11B variation: 1) B is fixed in cell walls in its tetrahedral form (borate), which preferentially incorporates the light B isotope and the remaining xylem sap gets enriched in the heavy B isotope and 2) certain transporter preferentially transport the trigonal 11B-enriched boric acid molecule and thereby the heavy 11B towards young plant compartments which were situated distal of the roots and typically high in the plant. Consequently, an enrichment of the heavy 11B isotope in the upper young plant parts located at the top of the plant could explain the observed isotope systematic. The identification and understanding of the processes generating systematic intra-plant δ11B variations will potentially enable the use of B isotope for plant metabolism studies. KW - Boron isotopes KW - Bell pepper KW - Boron transport KW - Boron isotope fractionation KW - Intra-plant isotope variability KW - Plants KW - Bell KW - Pepper KW - Isotope fractionation PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-352289 DO - https://doi.org/10.4172/mso.1000101 VL - 1 IS - 1 SP - Article 1000101, 1 EP - 6 AN - OPUS4-35228 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sproesser, Gunther A1 - Chang, Ya-Ju A1 - Pittner, Andreas A1 - Rethmeier, Michael A1 - Finkbeiner, Matthias T1 - Laser-MSG-Hybridschweißen und die Ökobilanz: Sieg nach Punkten N2 - Es ist ein Naturgesetz: Mit der verarbeiteten Blechdicke steigt der Zeit-, Material- und Energiebedarf beim Fügen überproportional. Aber ist das noch umweltverträglich ? Dieser Frage stellte sich Gunther Sproesser mit seinen Kollegen an der Technischen Universität Berlin. KW - MSG-Schweißen KW - Hochleistungsschweißen KW - Ökobilanz KW - Laser-MSG-Hybridschweißen PY - 2015 UR - http://www.laser-community.com/de/schweiss-verfahren-im-oeko-check/ N1 - In Deutsch und Englisch erschienen. Titel in English: "A win on points: LAHW/GMAW welding tops life-cycle analysis study" IS - 21/November 2015 SP - 6 EP - 6 AN - OPUS4-35438 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mull, Birte A1 - Jann, Oliver T1 - Biozidemissionen aus Materialien in die Luft N2 - Die meisten organischen Biozide gehören zu der Gruppe der schwerflüchtigen organischen Verbindungen (SVOC – semi volatile organic compounds). Zu den klassischen Bioziden zählen u.a. Lindan, Pentachlorphenol PCP) und Dichlordiphenyltrichlorethan (DDT) und zu den neueren u.a. Dichlofluanid, Tebuconazol und Permethrin. Biozide kamen in Museen vor allem in den 50er und 60er Jahren zum Schutz der Exponate zum Einsatz,1 wo sie hauptsächlich in Depoträumen zu finden sind, in welchen sie zum akuten und zum präventiven Schutz vor Schadorganismen eingesetzt wurden.2 Im Laufe der Zeit wurde jedoch festgestellt, dass sich der Einsatz von Bioziden negativ auf die menschliche Gesundheit auswirkt und auch zu Schäden an den behandelten Exponaten führen kann. 3 Verschiedene Möglichkeiten der Biozidanalytik und der Einfluss von Senkeneffekten auf die Analytik werden in diesem Beitrag vorgestellt. KW - Biozidanalytik KW - Schwerflüchtige organische Verbindungen KW - Emissionsmesskammer PY - 2015 SP - 12 EP - 14 CY - Berlin AN - OPUS4-35394 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Knorr, Annett T1 - Anwendung der TRAS 410 auf die sicherheitstechnische Beurteilung einer Perestersynthese T1 - Application of the technical rule TRAS 410 to the safety evaluation of a peroxide synthesis N2 - Exotherme Reaktionen verursachten in der Vergangenheit im industriellen Maßstab immer wieder Unfälle. Deshalb ist die Kenntnis des Gefahrenpotentials einer chemischen Reaktion sowohl im Normalbetrieb als auch bei Abweichungen davon eine Voraussetzung für eine sichere Prozessführung. Mit der Veröffentlichung der Technischen Regel für Anlagensicherheit (TRAS) 410 "Erkennen und Beherrschen exothermer Reaktionen" im Jahr 2001 existiert für chemische Stoffumwandlungen im Industriemaßstab eine auf dem Stand der Sicherheitstechnik basierende Anleitung zur systematischen Identifizierung von Gefahren, zu deren Bewertung und zur Erstellung von Maßnahmen, um Störfälle zu verhindern. Betrachtet wird dabei vorrangig die thermische Prozess-Sicherheit. Ein erhöhtes Gefahrenpotential besitzen exotherme Reaktionen an denen wie im vorliegenden Fall organische Peroxide beteiligt sind. Diese Verbindungsgruppe ist für ihre thermische Instabilität bekannt. In dieser Arbeit wird die unter basischen Bedingungen, zweistufig ablaufende Umsetzung von tert.-Butylhydroperoxid (TBHP) mit Pivaloylchlorid zum tert.-Butylperoxypivalat (TBPP) untersucht. TBHP, das auftretende Zwischenprodukt und TBPP gehören zur Stoffgruppe der organischen Peroxide. Bei der Bewertung der thermischen Prozess-Sicherheit der TBPP-Synthese wurde entsprechend der TRAS 410 vorgegangen. Die thermische Stabilität der beteiligten Stoffe wurde mit thermoanalytischen Screening-Methoden untersucht und die Reaktion durch kalorimetrische Untersuchungen charakterisiert. Die formale Anwendung der 100 K-Regel zur Festlegung der Grenztemperatur Texo, bei der alle an der Reaktion beteiligten Stoffe unter Verfahrensbedingungen sicher handhabbar sind, beträgt -36 °C. Bei dieser Temperatur ist der Prozess nicht durchführbar, da einzelne Reaktionskomponenten auskristallisieren und die Reaktion nicht wie gewünscht stattfinden kann. Anhand zusätzlicher Untersuchungsergebnisse zur Zersetzungskinetik des Produktes wird erläutert, dass im vorliegenden Fall von der o. g. Regel abgewichen werden kann. Als minimale Prozesstemperatur wurden 0 °C und als maximale Prozesstemperatur 20 °C festgelegt. Der Normalbetrieb wird im Rahmen der festgelegten Verfahrensparameter als sicher bewertet. Die Reaktion läuft dosierkontrolliert ab, eine Akkumulation tritt nicht auf. Aufgrund der geringen Differenz zwischen maximaler Prozesstemperatur und Onset-Temperatur der Zersetzung, besteht bei geringen Abweichungen vom Normalbetrieb die Gefahr, die unkontrollierte Zersetzung des Produktes einzuleiten. Temperaturanstieg und Gasproduktion führen zum Überschreiten der Auslegungsparameter der Anlage. Um die Reaktion durchführen zu können, müssen unbedingt vorbeugende als auch auswirkungsbegrenzende Maßnahmen getroffen werden. Abschließend wird mit Hilfe dimensionsloser Kenngrößen die Maßstabsübertragung mit dem Ziel vorgenommen, Grenzen für Reaktionsvolumina und Dosierzeiten festzulegen. N2 - In the past exothermic reactions in the industrial scale were repeatedly the cause of accidents. Therefore the knowledge of the potential hazards of an exothermic reaction for normal operations as well as for deviations is a precondition for a safe handling of the industrial process. With the release of the technical guide for identification and control of exothermic chemical reactions (“Technische Regel für Anlagensicherheit 410, Erkennen und Beherrschen exothermer chemischer Reaktionen (TRAS 410)“) in Germany 2001 there is a tool available, which is based on the art of safety engineering helps, to identify and to assess hazards and to derive measures to prevent failures. The main focus is pointed to the thermal process safety. A higher potential hazard possess exothermic reactions, in which, like in the present case, organic peroxides are involved. These type of compounds are well known for their thermal instability. In the thesis a two-phase, semi-batch reaction of tert-Butylhydroperoxide (TBHP) with pivaloyl chloride to tert-Butylperoxypivalate (TBPP) was investigated. Both TBHP, the formed intermediate and TBPP belong to the group of peroxide. The technical guide TRAS 410 was applied to assess the thermal process safety of the TBPP synthesis. The thermal stability of the involved substances was examined with screening methods and the reaction itself was characterised by calorimetric measurements. The technical application of the 100-Kelvin rule led to a limit temperature Texo of -36 °C, where a safe handling of all substances is firmed. Practically the process is not realisable at this temperature. Due to additionally studies and the determination of the activation energy and the Arrhenius factor of the decomposition of TBPP the lowest process temperature was set at 0 °C. As maximum temperature 20 °C was fixed. In line with the defined operating conditions the normal mode is assessed to be safe. The reaction is controlled by the feed velocity. No accumulation appeared. Because of a narrow gap between process temperature and the temperature, were the decomposition of TBPP starts considerably, only small deviations of process conditions are permitted. Otherwise the decomposition will run uncontrolled with temperature raise and gas production, definitely resulting in exceeding design limits of the process. To carry out the process several preventive measures like control engineering techniques have to be installed. Finally scale-up using dimensionless parameter is done to determine minimum and maximum reaction volume and feed time. KW - Maßstabsübertragung KW - Peroxidsynthese KW - Reaktionskalorimetrie KW - Semibatch-Reaktion KW - Sicherheit KW - Peroxide synthesis KW - Reaction calorimetry KW - Safety KW - Scale-up KW - Semibatch reaction PY - 2006 UR - https://nbn-resolving.org/urn:nbn:de:kobv:83-opus-11954 DO - https://doi.org/10.14279/depositonce-1279 SP - 1 EP - 162 PB - Technische Universität CY - Berlin AN - OPUS4-35406 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Dörfel, Ilona A1 - Steinborn, Gabriele A1 - Langner, Jeanette A1 - Krietsch, Arne A1 - Seeger, Stefan A1 - Österle, Werner A1 - Schmidt, Martin A1 - Bresch, Harald T1 - Dossier on titanium dioxide - Part 1/1 - NM 105 N2 - In November 2007, OECD’s Working Party on Manufactured Nanomaterials (WPMN) launched the Sponsorship Programme for the Testing of Manufactured Nanomaterials (hereafter the Testing Programme). The objective was to conduct specific tests, relevant to human health and environmental safety endpoints, on a variety of manufactured nanomaterials (MN). The outcomes of the Testing Programme were intended to assess the applicability of the existing test guidelines1 to nanomaterials, as well as to provide useful information on any intrinsic properties of MNs, which are different from the same bulk material with greater external dimensions. Understanding the properties of NMs is crucial to choose appropriate strategies for hazard identification, risk assessment or risk management measures. The Testing Programme involved delegations from OECD member countries, some non-member economies and other stakeholders. The broad international representation, from a range of delegations enabled the programme to pool expertise and resources without which this programme would not have been possible. KW - Nanomaterial KW - Nanoparticle KW - Sponsorship programme KW - Nano characterization PY - 2015 UR - http://www.oecd.org/env/ehs/nanosafety/dossier-on-silver-nanoparticles-part1-1.htm IS - 54 SP - 27 CY - Paris AN - OPUS4-35430 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Oesch, Tyler T1 - In-situ CT investigation of pull-out failure for reinforcing bars embedded in conventional and high-performance concretes N2 - The use of high-performance concretes holds great promise for many structural applications. This paper investigates the performance of these materials when used in combination with traditional reinforcing bars. An improved understanding of failure during reinforcing bar pull-out from high-performance concretes is needed in order to better predict the embedment length required to develop full reinforcing bar pull-out strength and the required thickness of reinforcing bar cover for adequate corrosion protection. The cracking structures surrounding the reinforcing bars were analyzed using x-ray computed tomography (CT) in order to determine the stress states causing failure. This was accomplished by conducting in-situ reinforcing bar pull-out experiments during CT scanning. A conventional concrete, a high-strength concrete, and a high-strength fiber reinforced concrete were all tested during the experiments. The results of these experiments showed that the levels of brittleness of the different concrete materials had a major impact on the failure mechanisms that they experienced during reinforcing bar pull-out. It was also clear that the specimen geometry and the casting method had a major impact on fiber orientation. The inclusion of fibers within concrete was also found to significantly improve strength and corrosion protection during reinforcing bar pull-out. T2 - 6th Conference on industrial computed tomography (iCT) CY - Wels, Austria DA - 09.02.2016 KW - Fiber KW - Reinforcing bar KW - Computed tomography KW - In-situ KW - High-performance concrete PY - 2016 UR - http://www.ndt.net/article/ctc2016/papers/ICT2016_paper_id83.pdf SN - 1435-4934 VL - 21 IS - 2 SP - ID 18788, 1 EP - 8 AN - OPUS4-35436 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Heyn, Emil T1 - Short reports from the metallurgical and metallographical laboratory of the Royal Mechanical and Technical Testing Institute of Charlottenburg PY - 1903 VL - 5 SP - 39 EP - 64 CY - Boston, MA AN - OPUS4-35317 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eberle, Arno A1 - Sievert, Rainer A1 - Schubert, A. ED - Winkler, T. ED - Schubert, A. T1 - On the influence of two different underfill materials on the inelastic thermo-cyclic response of a flip-chip solder bump N2 - The finite element method was used to simulate the thermo-mechanical behaviour of a solder bump configuration on Al2O3 substrate under thermo-cyclic loading between -55 °C and 125 °C. Chaboche's viscoplastic material model was used to describe the Bauschinger effect and the creep/plasticity interaction for the tin-lead solder material. The influence of two different viscoelastic underfill materials (Epoxy+50 % SiO2, Epoxy+70 % SiO2) on the inelastic deformation of the tin-lead solder was analyzed and compared. It may be shown that the thermally matched 'hard' underfiller (Epoxy+70 % SiO2) significantly reduces the accumulated inelastic strain in the bump compared to 'soft' underfiller or no underfill material. On the other hand, the maximum lateral normal stress will increase slightly. PY - 2015 SP - 471 EP - 480 AN - OPUS4-33859 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gogolin, Bernd A1 - Schrimmer, Peter ED - Nowack, H. T1 - Betriebsverhalten und Lebensdauer von Riemengetrieben; Prüfmethoden und Einflußparameter PY - 1985 N1 - Serientitel: Vorträge der Sitzung des Arbeitskreises Betriebsfestigkeit – Series title: Vorträge der Sitzung des Arbeitskreises Betriebsfestigkeit IS - 11 SP - 169 EP - 182 PB - DVM CY - Berlin AN - OPUS4-33910 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Höpfner, Wolfgang T1 - Sicherung der Umwelt durch Korrosionsprüfung dünnwandiger Meß- und Regeleinrichtungen für Gefahrgut PY - 1985 SP - 2 S. PB - DECHEMA CY - Frankfurt am Main AN - OPUS4-33915 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Isecke, Bernd T1 - Untersuchungen zum Zustand der Werkstoffe anläßlich des Abbruchs einer Spannbetonbrücke PY - 1985 SP - 67 EP - 70 PB - VDI-Gesellschaft Werkstofftechnik CY - Düsseldorf AN - OPUS4-33917 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kasparek, Eva Maria A1 - Völzke, Holger T1 - Further research on cask impact limiter needed? N2 - Transport and storage casks for medium and high level radioactive waste are subjected to extreme heavy loads during the accidental drop scenarios prescribed by IAEA regulations and national storage acceptance criteria. Subsequently, considerable efforts have been made to optimize impact limiting structures aiming to reduce cask stresses and deformations. Though, their benefits can only fully be exploited, if the energy absorbing behavior is reliable simulated by numerical models which play an increasingly important role in safety assessments. BAM has had conducted the 5-years research project ENREA in order to overcome the problems caused by the use of simplified, not sufficiently validated or even defective computational concepts for damping materials. While major results of the just recently completed program will be presented, the focus is laid on the question whether these Outputs provide a solid foundation for approximating impact limiting structures in all relevant configurations. So far, material models have been implemented for spruce, Polyurethane foams and damping concrete based mainly on small and medium scale compression test results. The experimental program performed at BAM comprised likewise guided drop tests and, especially for concrete, penetration tests. Although the resulting numerical simulations showed good agreement with measured values, it turned out to be necessary to consider further effects with regard to e.g. multiaxial stress States, shearfailures of shock absorbing components and their interaction with enclosed or enclosing structures. Thus, the strengths and application constraints of the actual models will be shown as well as details about further research needs, if any. T2 - RAMTRANSPORT 2015 - International conference on the radioactive materials transport and storage CY - Oxford, UK DA - 19.05.2015 KW - Numerical model KW - Shock absorber KW - Damping concrete KW - Polyurethane foam KW - Radioactive waste storage cask PY - 2015 SP - 1 EP - 8 AN - OPUS4-33992 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hundt, Jürgen T1 - Einsatz des Endoskops zum Nachweis von Korrosionsschäden an Spannstählen und deren Verankerung T2 - Grazer Congress CY - Graz, Austria DA - 1983-06-21 PY - 1985 SP - 15 EP - 22 PB - TU Graz CY - Graz AN - OPUS4-33997 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brandes, Klaus A1 - Limberger, Ernst A1 - Herter, Jürgen T1 - Experimental verification of punching shear failure of RC slabs subjected to aircraft impact loads T2 - International Conference on structural mechanics in reactor technology (SMiRT 8) CY - Brüssel, Belgium DA - 1985-08-19 PY - 1985 VL - Paper J 5/6 SP - 197 EP - 201 AN - OPUS4-34005 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Burchhardt, F. A1 - Magiera, Götz A1 - Matthees, Wolfgang A1 - Weber, Michael T1 - Interaction between material nonlinearity and damping for aircraft impact analysis T2 - International Conference on structural mechanics in reactor technology (SMiRT 8) CY - Brüssel, Belgium DA - 1985-08-19 PY - 1985 VL - Paper J 5/5 SP - 191 EP - 196 AN - OPUS4-33934 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Matthees, Wolfgang A1 - Burchhardt, F. A1 - Magiera, Götz T1 - A three-dimensional soil-structure lumped parameter analysis for earthquake events T2 - International Conference on structural mechanics in reactor technology (SMiRT 8) CY - Brüssel, Belgium DA - 1985-08-19 PY - 1985 VL - Paper K 5/5 SP - 177- AN - OPUS4-33935 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Struck, Werner ED - Jacoby, G. T1 - Stoßartige Belastungen von Stahlbetonbauteilen PY - 1981 SP - 101 EP - 113 PB - Werkstofftechn. Verl.-Ges. CY - Karlsruhe AN - OPUS4-33986 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kühne, Helmut T1 - Insekten als Materialschädlinge T2 - DEGESCH-Technikertagung "Vorratsschutz bei Langzeitlagerung von Nahrungs-, Genuß- und Futtermitteln" CY - Frankfurt am Main, Germany DA - 1980-09-21 PY - 1981 SP - 20 EP - 26 PB - DEGESCH CY - Frankfurt am Main AN - OPUS4-33954 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hantsche, Harald T1 - Probleme der quantitativen Analyse mit energiedispersiven Röntgenmikroanalysatoren T2 - Tagung der Materialprüfstelle der Bundeswehr "Schadensuntersuchung an metallischen Bauteilen" CY - Erding, Germany DA - 1979-05-31 PY - 1979 SP - 114 EP - 123 PB - Materialprüfstelle der Bundeswehr CY - München AN - OPUS4-33955 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, D. T1 - LaB6- und W-Kathoden im REM S 180 - ein Vergleich T2 - 5. Sitzung des Arbeitsausschusses Geräteentwicklung im Arbeitskreis Rastermikroskopie CY - Wien DA - 1980-11-06 PY - 1981 SP - 27 EP - 39 PB - DVM CY - Berlin AN - OPUS4-33956 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Goebbels, K. A1 - Crostack, H.-A. A1 - Frielinghaus, R. A1 - Ganglbauer, O. A1 - Neumann, Eberhard T1 - Ultrasonic testing of coarse grained materials - research to new approaches T2 - 1st German Japanese Seminar on NDE in Nuclear Industry CY - Saarbrücken, Germany DA - 1980-07-14 PY - 1981 SP - 1 EP - 36 PB - Fraunhoferinstitut für Zerstörungsfreie Prüfverfahren (IzfP) CY - Saarbrücken AN - OPUS4-33957 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wüstenberg, Hermann A1 - Erhard, Anton T1 - Anwendung spezieller Ultraschall-Prüfköpfe unter besonderer Beachtung von Kriechwellen PY - 1981 SP - 1 EP - 22 PB - Koninklijk Instituut Van Ingenieurs (KIVI) CY - Twente AN - OPUS4-33958 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brandes, Klaus T1 - Versuche zum mechanischen Verhalten von Stahlbetonbauteilen unter Stoßeinwirkung PY - 1980 SP - 75 EP - 101 PB - Universität Dortmund CY - Dortmund AN - OPUS4-33960 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rückward, Werner T1 - Einführung in die Arbeit des Laboratoriums für Schallschutz, Erschütterungsschutz T2 - Tagung Maschinengeräusche und Schwingungen PY - 1981 SP - 213 EP - 226 PB - Gesellschaft für Fertigungstechnik AN - OPUS4-33944 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schickert, Gerald T1 - Influence of moisture on results of combined non-destructive tests on 150 mm-concrete cubes T2 - 4th meeting of the RILEM commission TC43-CND CY - Athens, Greece DA - 1981-04-09 PY - 1981 SP - 1 EP - 10 PB - RILEM commission TC43-CND CY - Athens AN - OPUS4-33945 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schickert, Gerald T1 - Infrarot-Thermographie für den baulichen Wärmeschutz T2 - bautec Fachschau '81 - Altbau, Neubau, Stadtbau CY - Berlin DA - 1981-10-27 PY - 1981 SP - 1 EP - 4 CY - Berlin AN - OPUS4-33946 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Feldkamp, Martin A1 - Nehrig, Marko A1 - Bletzer, Claus Wilhelm A1 - Musolff, André A1 - Wille, Frank T1 - Combustion of wood encapsulated in steel sheets during fire test N2 - Packages for the transport of radioactive material are often equipped with impact limiters consisting of wood, encapsulated by Steel sheets. These impact limiters shall ensure the transport cask meets the IAEA safety requirements. After damage caused by the mechanical tests the package has to withstand a severe fire scenario. According to the regulations during and following the fire test, the specimen shall not be artificially cooled and any combustion of materials of the package shall be permitted to proceed naturally. Due to results of the French institute IRSN it was shown that after the fire test an additional energy supply from a pre-damaged impact limiter should be taken into account. The combustion or smouldering of wood was of interest. BAM started a first test phase to examine the issue of combustion for such kind of package components. The goal was to understand the phenomena under the consideration of relevant regulatory boundary conditions. Several metal buckets were filled with wood and equipped with thermocouples. The test specimens have been prepared with different damage arrangements to take the influence of the mechanical tests into account. This paper shows the experimental Setup and the conduction of the tests. The first test shows that pre-damaged metal encapsulations can lead to smouldering of the wood and with this to a Supplement energy release after the end of the 30 minute fire. The consequence could be, to consider additional thermal loads of wood filled impact limiters to filled the IAEA regulations, if the conditions of the tests are transferable to the safety analysis of the package design. T2 - RAMTRANS 2015 - 10th International conference on radioactive materials transport and storage CY - Oxford, UK DA - 19.05.2015 KW - Typ-B KW - Impact limiter KW - Shock absorber KW - Wood KW - Thermal test KW - Fire test PY - 2015 SP - 1 EP - 9 AN - OPUS4-33407 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wille, Frank A1 - Ballheimer, Viktor A1 - Quercetti, Thomas A1 - Sterthaus, Jens T1 - Consideration of gaps between content and lid within package design assessment N2 - Type B(U) packages for the transport of radioactive material have to withstand accident conditions of transport defined in the regulations of the International Atomic Energy Agency in form of different mechanical (drop) tests with a subsequent thermal test. According to the regulatory requirements the orientation of the package in drop tests shall be such to cause the most damaged state in the components performing the safety functions. For the package Iid system a 9 m drop onto the unyielding target with Iid side downwards is often the most damaging orientation. The impact Ioads acting on the Iid in this orientation result mainly from interaction between Iid and internal content. In case of a movable content its impact onto the inner side of the Iid can cause additional Ioad peaks on the Iid and the Iid bolts. The intensity of the internal collision depends on the position of content relating to Iid at the time of package first contact with target. Due to physical limitations an axial gap, which could be set in "pre-drop" configuration of package or which could spontaneously appear during the drop test, usually does not cover the maximum size possible in specific package design. In this context, the combination of drop tests with post-test analysis can be helpful to better estimate the effect of internal impact. The paper summarizes some aspects of this issue based on the BAM experience in the design assessment of Type B(U) transport packages. Additionally the paper shall support applicants in German approval procedures to reduce rounds of questions and ensure delivery of reliable safety case documents to the authorities. T2 - RAMTRANS 2015 - 10th International conference on radioactive materials transport and storage CY - Oxford, UK DA - 19.05.2015 KW - Transport packages KW - Accident conditions of transport KW - Internal impacts KW - Lid/content interaction KW - Radioactive material PY - 2015 SP - 1 EP - 10 AN - OPUS4-33419 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Krause, Hans-Joachim A1 - Preß, Henning T1 - Measurement of the welding fume quantities and analysis of the fume composition during resistance welding PY - 1985 IS - VIII-1278-85 SP - 1 EP - 12 PB - International Institute of Welding CY - Paris AN - OPUS4-34271 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Wilken, Klaus A1 - Kleistner, Horst T1 - Remarks on the classification and evaluation of hot cracking tests PY - 1985 IS - IX-1379-85 SP - 1 EP - 17 PB - International Institute of Welding CY - Paris AN - OPUS4-34275 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Daum, Werner A1 - Rose, Peter T1 - Automatische Isolierung von Schweissnahtfehlern in Röntgenaufnahmen aus der zerstörungsfreien Materialprüfung T2 - 1. Internationale Fachtagung Automatische Bildverarbeitung CY - Berlin, Germany DA - 1985-10-17 PY - 1985 SP - 1 EP - 4 PB - Kammer der Technik CY - Berlin AN - OPUS4-34202 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Kohl, Anka A1 - Haufe, Manuela T1 - Compatibility of polyethylene grades with biofuels and biodiesel-heating oil blends N2 - 8iofuels including ethanol and biodiesel (fatty acid methyl ester) represent an important renewable fuel alternative to petroleum-derived transport fuels. lncreasing biofuels use would bring some benefits, such as a reduction in oil demands and greenhause gas emissions, and an improvement in air quality. T2 - EUROCORR 2015 - European corrosion congress CY - Graz, Austria DA - 06.09.2015 KW - Compatibility KW - Polyethylene grades KW - Biofuels KW - Change in MFR and tensile properties PY - 2015 SP - Paper 16_1074, 1 EP - 11 AN - OPUS4-34203 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Werner, Jan A1 - Jochems, Frank A1 - Heming, Frank T1 - Change in properties of sealing materials in biofuels, biodiesel-heating oil blends, diesel and premium grade fuel at different temperatures N2 - Materials compatibility is a major concern whenever the fuel composition is changed in a fuel system. Therefore frequently used sealing materials such as FKM (fluorocarbon rubber), FVMQ (methyl-fluoro-silicone rubber), VMQ (methyl-vinyl-silicone rubber), EPDM (ethylene-propylene-diene rubber), CR (chloroprene rubber), CSM (chlorosulfonated polyethylene), IIR (butyl rubber), PA (polyamides), N8R (acrylonitrile-butadiene rubber) and PUR (polyester urethane rubber) were exposed to E1 0, diese I fuel with 5% biodiesel, non-aged and 2 year aged 810 (heating oil with 10% biodiesel), and for comparison to pure diese! fuel, standard heating oil and Super plus without bioethanol at 20 °C, 40 oc and 70 oc for 84 days. Mass, tensile strength and breaking elongation of the test specimens were determined before and after the exposure. The visual examination of some elastomer test specimens clearly showed the great volume increase until break or partial dissolution. Shore hardness A and D (for PA) were determined before and after exposure of the test specimens to the biofuels for 42 days. There is not determined a threshold for the reduction in tensile properties and Shore hardness in the international standards. Therefore a threshold of 15% was determined for the evaluation of the compatibility. The sealing materials FKM, EPDM, N8R, FMVQ, CSM and PA were evaluated on the basis of this threshold as resistant in E1 0 at 20 oc and 40 °C. FKM, FVMQ and PA were resistant at 40 oc , and none of the materials were resistant at 70 °C. FKM and FVMQ absorbed much less 810 and swelled less. CR, CSM, EPDM, IIR, N8R and VMQ were not resistant to 810 at all at 20 oc, 40 oc and 70 oc as the decrease in the tensile properties was significantly over 50%. FVMQ and PA could be evaluated as resistant in non-aged and two year aged 810 at 20 oc and 40 oc, whereas FKM was resistant up to 70 °C. FKM, PA and PUR were evaluated as resistant in standard heating oil and pure diese! fuel at temperatures up to 40°C, only FKM was resistant up to 70°C. FVMQ, FKM, N8R, VMQ, CR and IIR can be evaluated as resistant in premium grade fuel Super plus without ethanol at 20 oc. FKM, FVMQ, VMQ and IIR were still resistant at 40 °C. FKM and FVMQ were evaluated as resistant with restrictions at 70 °C. ln summary, it can be therefore stated that the chemical resistance of the fluoropolymers FKM and FVMQ in fuels and biofuels is the best one. T2 - EUROCORR 2015 - European corrosion congress CY - Graz, Austria DA - 06.09.2015 KW - Compatibility KW - Sealing materials KW - Biofuels KW - Tensile properties KW - Shore hardness PY - 2015 SP - Paper 16_173, 1 EP - 11 AN - OPUS4-34204 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erhard, Anton A1 - Wüstenberg, Hermann A1 - Schulz, Eduard A1 - Möckel, U. T1 - Ultrasonic flaw detection and sizing methods for cracks in the nozzle corner area at boiling water reactor vessels T2 - 7th International Conference on NDE in the nuclear industry CY - Grenoble, France DA - 1985-01-28 PY - 1985 SP - 55 EP - 58 CY - Grenoble AN - OPUS4-34209 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erhard, Anton A1 - Wüstenberg, Hermann A1 - Schenk, Gottfried A1 - Möhrle, Walter T1 - Calculation and construction of phased array-UT probes T2 - 3rd Japanese-German joint seminar on structural strength and NDE problems in nuclear engineering CY - Stuttgart, Germany DA - 1985-08-29 PY - 1985 SP - 1 EP - 22 AN - OPUS4-34210 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Knapp, Jürgen T1 - Optical fiber sensors with intensity modulation for utilisation under extreme environmental conditions T2 - 10th IMEKO World Congress CY - Prague, Czech Republic DA - 1985-04-22 PY - 1985 VL - 10 SP - 64 EP - 71 PB - House of Technology CY - Prag AN - OPUS4-34196 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Markowski, Winfried T1 - Zur Kalibrierung von Prüfeinrichtungen bezüglich der Messgrösse Kraft T2 - Tagung Werkstoffprüfung CY - Bad Nauheim, Germany DA - 1985-12-03 PY - 1985 SP - 175 EP - 181 PB - DVM, Deutscher Verband für Materialforschung und -prüfung CY - Berlin AN - OPUS4-34197 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Oblasser, Jörg T1 - Erfahrungen bei der Untersuchung von Härteprüfgeräten T2 - Tagung Werkstoffprüfung CY - Bad Nauheim, Germany DA - 1985-12-03 PY - 1985 SP - 217 EP - 225 PB - DVM, Deutscher Verband für Materialforschung und -prüfung CY - Berlin AN - OPUS4-34198 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Oppermann, Klaus T1 - Force sensor with metal measuring grid transverse to the lines of force T2 - Tagung Werkstoffprüfung CY - Bad Nauheim, Germany DA - 1985-12-03 PY - 1985 SP - 46 EP - 54 PB - DVM, Deutscher Verband für Materialforschung und -prüfung CY - Berlin AN - OPUS4-34200 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krause, Hans-Joachim T1 - Möglichkeiten der Qualitätssicherung für Schweissverbindungen an dünnen Blechen in der Serienfertigung T2 - Tagung Werkstoffprüfung CY - Bad Nauheim, Germany DA - 1984-12-06 PY - 1985 SP - 99 EP - 112 PB - DVM CY - Berlin AN - OPUS4-34262 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krause, Hans-Joachim T1 - Development of materials for resistance welding PY - 1985 SP - 1 EP - 47 PB - Danish Welding Society CY - Copenhagen AN - OPUS4-34264 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Krause, Hans-Joachim A1 - Lehmkuhl, Bernhard T1 - A comparison of the dynamic mechanical characteristics of spot-welding machines PY - 1985 IS - III-816-85 SP - 1 EP - 7 PB - International Institute of Welding CY - Paris AN - OPUS4-34267 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heidt, Heinrich A1 - Rose, Peter A1 - Raabe, P. A1 - Daum, Werner T1 - Digital image processing for radiography in nuclear power plants T2 - 7th International Conference on NDE in the nuclear industry CY - Grenoble, France DA - 1985-01-28 PY - 1985 SP - 317 EP - 319 CY - Grenoble AN - OPUS4-34215 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kettschau, A. A1 - Reimers, Peter A1 - Goebbels, Jürgen T1 - Computertomographie von radioaktiven Abfallgebinden T2 - Jahrestagung Kerntechnik CY - München, Germany DA - 1985-05-21 PY - 1985 SP - 423 EP - 426 PB - Deutsches Atomforum CY - Bonn AN - OPUS4-34220 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaffrey, D. A1 - Wüstenberg, Hermann A1 - Bertus, Norbert A1 - Ludwig, Bernd A1 - Erhard, Anton T1 - Improved detection of near-surface defects with new ultrasonic probes and signal analysis techniques T2 - Fifth international conference on pressure vessel technology CY - San Francisco, CA, USA DA - 1984-09-09 PY - 1984 VL - 2 SP - 693 EP - 702 PB - ASME CY - New York AN - OPUS4-34231 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wüstenberg, Hermann A1 - Hübschen, G. A1 - Maier, H.-J. T1 - US - Testing from outside in nozzle geometries (computerized scanning patterns) T2 - 3rd Japanese-German joint seminar on structural strength and NDE problems in nuclear engineering CY - Stuttgart, Germany DA - 1985-08-29 PY - 1985 SP - 1 EP - 24 AN - OPUS4-34235 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wüstenberg, Hermann A1 - Wegner, W. A1 - Bertus, Norbert A1 - Möhrle, Walter T1 - Inner wall inspection of stream generator tubes with circumferential welds using ultrasonic crack detection T2 - 7th International Conference on NDE in the nuclear industry CY - Grenoble, France DA - 1985-01-28 PY - 1985 SP - 1 EP - 4 CY - Grenoble AN - OPUS4-34236 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neider, Rudolf ED - Henning, K. T1 - Begrenzung der Strahlenexposition der Bevölkerung bei der Verwertung von Reststoffen aus kerntechnischen Anlagen T2 - 18. Jahrestagung des Fachverbandes für Strahlenschutz CY - Lübeck-Travemünde, Germany DA - 1985-10-06 PY - 1985 N1 - Serientitel: FS-Berichte aus der Schriftenreihe des Fachverbandes für Strahlenschutz – Series title: FS-Berichte aus der Schriftenreihe des Fachverbandes für Strahlenschutz IS - 85-37 SP - 721 EP - 734 PB - Fachverband für Strahlenschutz CY - Würenlingen AN - OPUS4-34246 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kettschau, A. A1 - Reimers, Peter A1 - Goebbels, Jürgen A1 - Heidt, Heinrich T1 - Gamma-ray computed tomography of waste containers and conditioned radioactive waste in nuclear industry T2 - 7th International Conference on NDE in the nuclear industry CY - Grenoble, France DA - 1985-01-28 PY - 1985 SP - 321 EP - 324 CY - Grenoble AN - OPUS4-34221 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kettschau, A. A1 - Goebbels, Jürgen A1 - Reimers, Peter A1 - Weise, Hans-Peter ED - Merz, E. T1 - Possibilities of quality assurance on radioactive waste packages by computertomography and other radiometric techniques T2 - International Seminar on Radioactive Waste Products - Suitability for Final Disposal CY - Jülich, Germany DA - 1985-06-10 PY - 1985 N1 - Serientitel: Berichte der Kernforschungsanlage Jülich – Series title: Berichte der Kernforschungsanlage Jülich IS - 54 SP - 483 EP - 491 PB - Zentralbibliothek der Kernforschungsanlage CY - Jülich AN - OPUS4-34222 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Völzke, Holger A1 - Wolff, Dietmar A1 - Kasparek, Eva Maria T1 - Beitrag zu den Anforderungen an die Beschaffenheit von Endlagerbehältern hinsichtlich ihrer Rückholbarkeit und Bergbarkeit N2 - Die Bundesanstalt für Materialforschung und –prüfung (BAM) wurde von der AG 3 der Kommission Lagerung hoch radioaktiver Abfallstoffe gebeten, Anforderungen an Behälter für die Endlagerung hoch radioaktiver Abfallstoffe im Hinblick auf ih-re Rückholbarkeit während des Endlagerbetriebes und ihre Bergbarkeit nach Ver-schluss des Endlagers über einen Zeitraum von 500 (bis 1.000 ?) Jahren darzu-stellen. Die BAM kommt diesem Wunsch auf der Grundlage ihrer langjährigen Er-fahrungen und Fachkenntnisse auf den Gebieten der Bauartprüfung und der si-cherheitstechnischen Begutachtung von Transport- und Lagerbehältern für radio-aktive Stoffe nach. PY - 2015 UR - https://www.bundestag.de/blob/396206/f0a6276f4e2741c3022afb8ce64c0689/drs_047-data.pdf SP - 1 EP - 12 AN - OPUS4-35104 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krause, Martin A1 - Kurz, J.H. A1 - Lanata, F. A1 - Krstevska, L. A1 - Cavalli, A. T1 - Needs for further developing monitoring- and NDT-methods for timber structures N2 - For the assessmentand for monitoring of timber structures there are numerous promising methods that enable the quantitative description of the current condition of construction elements or parts of a structure. This concerns material properties like modulus of elasticity, moisture content and density as well as structural properties like dynamic characteristics, localization of inhomogeneities, cracks, and biological attack. During the work in COST Action FP 1101, since 2012 the capability of experimental methods are discussed and compared. This covers electrical and electromagnetic wave methods (resistivity, microwave, Radar, X-Ray), elastic waves (ultrasound, pile testing) and mechanical testing (static and dynamic). Describing and collecting the use of the experimental methods for monitoring purposes was the objective of working group 3 "Monitoring of Timber Structures" of the COST Action. Monitoring capabilities will extend the use of timber structures to further applications in civil engineering. So far, no standard exists but collections of application examples and review papers representing the state of the art. From there needs for further developments regarding monitoring and NDT methods for timber structures can be identified and these are described in this paper. T2 - SHATIS 2015 - 3rd International conference on structural health assessment of timber structures CY - Wroclaw, Poland DA - 09.09.2015 KW - Holz Konstruktionen KW - Monitoring KW - Langzeitverhalten KW - Erdbebensicherheit KW - Historische Bauwerke KW - Ultrasonic echo imaging KW - Historical timber structures KW - Seismic investigation KW - Dynamic tests KW - Anisotropic wave propagation KW - Extending service life PY - 2015 VL - 1 SP - 1 EP - 12 AN - OPUS4-35178 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krause, Martin A1 - Mayer, K. A1 - Effner, Ute T1 - Ultrasonic echo methods for structural timber N2 - Ultrasonic echo technique with shear waves in the frequency rang of 50 kHz is one of the promising methods for assessment of structural timber and is already frequently applied for this purpose. The article summarizes the state of the art of applying echo measurement via linear measurements as well as the development and first results for an imaging method for this purpose. The highly anisotropic properties of the ultrasonic velocity have to be considered. 3 D ultrasonic imaging results are described for the example of a pedestrian bridge made from Siberian larch. T2 - COST Workshop - Highly performing timber structures: Reliability, assessment, monitoring and strengthening CY - Biel, Switzerland DA - 23.09.2014 KW - Ultrasonic echo KW - SAFT reconstruction calculation KW - Glued-laminated timber (glulam) KW - Footbridge KW - Ultraschallecho KW - SAFT KW - Brettschichtholz PY - 2014 SN - 978-3-9523787-3-1 SP - 77 EP - 82 PB - Bern University of Applied Sciences CY - Bern AN - OPUS4-35179 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Becker, T. A1 - Weisbrich, S. A1 - Euteneuer, F. A1 - Wu, Cheng-Chieh A1 - Neitzel, F. T1 - Neue Möglichkeiten in der Bauwerksüberwachung durch integrierte Analyse von Sensormessungen und 3D-Bauwerksmodell N2 - Die Verwendung offener Standards bietet eine Vielzahl von Möglichkeiten, gerade im Bereich des Datenaustausches, Datenlagerung, aber auch der Interoperabilität. GML und CityGML sind hervorragende Beispiele für die Beschreibung von Realweltobjekten mittels eines offenen Standards wohingegen SensorML dazu dient, Messungen, Sensoren und Messplattformen zu beschreiben. Die Verwendung solcher Standards eröffnet dem Nutzer nicht nur die Möglichkeiten der Verwendung einer gemeinsamen standardisierten Sprache, sondern auch die Nutzung von offenen Servicestandards, wie Web Feature Service (WFS), Web Map Service (WMS) oder von Sensor Observation Services (SOS). Die Kombination von Geodaten- und Sensorstandards in einer Dienste- und Servicearchitektur geht über bisherige am Markt existierende Lösungen hinaus und schafft eine neuartige Plattform für die Bauwerksüberwachung, die weit mehr als ein simples Datenhaltungsmodell darstellt. Die in diesem Beitrag vorgestellte Plattform ermöglicht eine direkte Integration von Sensordaten sowie deren Bereitstellung durch eine offene Standardsprache. Dabei sind alle Zwischenschritte jederzeit über eine offene Diensteschnittstelle adressierbar und können so verschiedenen Akteuren zur Verfügung gestellt werden. Das große Potential und der Mehrwert eines derartigen Informationssystems liegt vor allem in der permanenten Verfüg-barkeit von Mess- und Objektdaten und einer damit verbundenen integrierten Analyse der Sensormessdaten in Kombination mit einem Finite-Elemente-Modell (FEM), basierend auf den Objektdaten. Die automatische Ableitung eines FE-Modells aus dem 3D-Bauwerks-modell, die Visualisierung der FEM-Simulationsergebnisse anhand des Bauwerksmodells, die Bereitstellung von Messrohdaten und Sensorinformationen zu jedem Messzeitpunkt machen die Plattform zu einem universell einsetzbaren Werkzeug im Bereich der Bauwerksüberwachung. In diesem Beitrag werden die einzelnen Bausteine, die verwendeten Standards und die Interaktion der einzelnen Komponenten zu einem Gesamtsystem vorgestellt. T2 - 34. Wissenschaftlich-technische Jahrestagung der DGPF CY - Hamburg, Germany DA - 26.03.2014 KW - 3D-Geoinformation KW - CityGML KW - Finite-Elemente-Methode PY - 2014 VL - 23 SP - Paper 254, 1 EP - 10 AN - OPUS4-30619 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mermillod-Blondin, A. A1 - Seuthe, T. A1 - Eberstein, M. A1 - Grehn, M. A1 - Bonse, Jörn A1 - Rosenfeld, A. ED - Gorecki, C. ED - Asundi, A. K. ED - Osten, W. T1 - Quantitative estimate of fs-laser induced refractive index changes in the bulk of various transparent materials N2 - Over the past years, many applications based on laser-induced refractive index changes in the volume of transparent materials have been demonstrated. Ultrashort pulse lasers offer the possibility to process bulky transparent materials in three dimensions, suggesting that direct laser writing will play a decisive role in the development of integrated micro-optics. At the present time, applications such as 3D long term data storage or embedded laser marking are already into the phase of industrial development. However, a quantitative estimate of the laser-induced refractive index change is still very challenging to obtain. On another hand, several microscopy techniques have been recently developed to characterize bulk refractive index changes in-situ. They have been mostly applied to biological purposes. Among those, spatial light interference microscopy (SLIM), offers a very good robustness with minimal post acquisition data processing. In this paper, we report on using SLIM to measure fs-laser induced refractive index changes in different common glassy materials, such as fused silica and borofloat glass (B33). The advantages of SLIM over classical phase-contrast microscopy are discussed. T2 - Optical Micro- and Nanometrology V CY - Brussels, Belgium DA - 14.04.2014 KW - Laser material processing KW - Quantitative phase-contrast microscopy KW - Spatial light interference microscopy KW - Nanometrology PY - 2014 DO - https://doi.org/10.1117/12.2051590 VL - 9132 SP - Artikel 91320X, 1 EP - 6 AN - OPUS4-30638 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wäsche, Rolf A1 - Hartelt, Manfred T1 - Wear testing with crossed cylinders - comparison of methods N2 - Three different contact geometries, ball on disk and two different settings with crossed cylinders have been investigated with regard to the agreement of the results of the tribological quantities determined by each method. The material combination was α-alumina as upper specimen and steel 100Cr6 as lower specimen. For each of the contact geometries 5 independent measurements were carried out and evaluated independently. The agreement between the single results of coefficient of friction and the coefficient of system wear as well as between the different groups and conditions are good. Largest scatter of the results were found in the dry air regime where both friction and wear depend strongly on the relative humidity. However, comparison of the absolute values of the coefficient of wear between the ball on disk contact geometry on one side and the 2 crossed cylinder contact geometries on the other side reveals a significant difference in that the ball on disk results are lower by about a factor of two. The results document also a high degree of repeatability of single wear tests. T2 - 16th International colloquium tribology - Lubricants, materials and lubrication engineering CY - Stuttgart/Ostfildern, Germany DA - 2008-01-15 KW - Fretting KW - Contact geometry crossed cylinders KW - Friction KW - Wear PY - 2008 SP - Paper 10_04_Wäsche, 1 EP - 6 AN - OPUS4-31602 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Birk, A. M. A1 - Otremba, Frank A1 - Gonzales, F. A1 - Prabhakaran, A. A1 - Borch, Jörg-Peter A1 - Bradley, I. A1 - Bisby, L. ED - de Rademaeker, E. ED - Schmelzer, P. T1 - Fire testing of total containment pressure vessels N2 - Full engulfment fire tests have been conducted on total containment pressure vessels filled to 50% and 98 % capacity with water. The tests included an unprotected tank and tanks with two different levels of thermal protection. Total containment in this context means there was no pressure relief device. The tests were conducted with 1/3rd linear scale rail tank cars similar to the DOT 111 tank cars used in North America. The 2.4 m3 model tanks were subjected to 100 % engulfing fires fuelled by liquid propane. The fire heat flux was approximately 80 % by radiation and 20 % by convection with a total heat flux to a cool surface of approximately 100 kW/m2. T2 - 15th International Symposium on loss prevention and safety promotion (loss 2016) CY - Freiburg, Germany DA - 05.06.2016 KW - fire testing KW - hazmat tanks KW - integrity PY - 2016 SN - 978-88-95608-39-6 DO - https://doi.org/10.3303/CET1648047 VL - 48 SP - 277 EP - 282 PB - AIDIC CY - Milano, Italy AN - OPUS4-36361 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hantsche, Harald A1 - Schmidt, Dieter A1 - Kempf, Gerhard A1 - Treu, Dieter ED - Vetters, H. T1 - Fortschritte bei der Automatisierung der energiedispersiven Röntgenmikroanalyse T2 - 10. Sitzung d. Arbeitskreises Rastermikroskopie in der Materialprüfung, DVM-Tag CY - Dortmund, Germany DA - 13.10.1981 PY - 1982 SP - 21 EP - 28 CY - Berlin AN - OPUS4-36328 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Eberhard A1 - Römer, Manfred A1 - Matthies, Klaus T1 - Sende-Empfangstechnik für schrägeinfallende Longitudinalwellen - Grundlagen und praktische Erfahrungen T2 - Ultraschallprüfung grobkörniger Werkstoffe unter besonderer Berücksichtigung von Austeniten CY - Berlin, Germany DA - 25.09.1980 PY - 1982 SP - 29 EP - 38 CY - Berlin AN - OPUS4-36411 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Eberhard A1 - Römer, Manfred A1 - Schenk, R. A1 - Matthies, Klaus T1 - On the applicability of ultrasonic testing techniques for coarse grain austenitic welds T2 - CSNI Specialist Meeting on Reliability of Ultrasonic Inspection of Austenitic Stainless Steel Components CY - Brussels, Belgium DA - 29.05.1980 PY - 1980 SP - 93 EP - 118 CY - Paris AN - OPUS4-36412 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Marotzke, Christian A1 - Feldmann, Titus ED - Thomson, Ole T1 - Characterisation of failure processes of composite plies under transverse loading N2 - For the design of laminates the knowledge of the failure behaviour of plies under multiaxial stresses is a necessary precondition. The strength of plies under multiaxial stresses commonly is determined by standard off-axis tests using fixed clamps. By varying the off axis angle the ratio of shear to normal stresses can be prescribed. However, by preventing the rotation a complex stress field develops which strongly varies with the off axis angle as well. While these effects are not crucial when determining the elastic material parameters since the stress state in the center of the specimen is not far from the ideal uniaxial stress state they have a great influence on the failure behaviour. T2 - ICCM20 CY - Copenhagen, Danmark DA - 19. 07. 2015 KW - debonding KW - composites KW - failure process KW - fracture mechanics KW - energy release rate PY - 2015 UR - www.iccm-central.org/Proceedings/ICCM20proceedings/ VL - 2015 SP - Paper No. 3314-4 page 01 EP - Paper No. 3314-4 page 09 AN - OPUS4-36414 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wüstenberg, Hermann A1 - Schenk, E. A1 - Möhrle, Walter T1 - Comparison of the performances of probes with different focusing techniques and experiences T2 - Conference on Periodic Inspection of Pressurized Components CY - London, England DA - 12.10.1982 PY - 1982 SN - 0-85298-499-5 SP - 229 EP - 238 PB - Mechanical Engineering Publications for the Institution of Mechanical Engineers CY - London AN - OPUS4-36417 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wüstenberg, Hermann A1 - Schenk, E. A1 - Möhrle, Walter A1 - Neumann, Eberhard T1 - Comparison of the performances of probes with different focusing techniques and experiences T2 - 10th World Conference on Nondestructive Testing CY - Moscow, Russia DA - 22.08.1982 PY - 1982 VL - 7 SP - 563 EP - 587 AN - OPUS4-36418 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hecht, Andreas A1 - Cherian, P. A1 - Neumann, Eberhard A1 - Mundry, Eberhard T1 - Über die Ausbreitung von gestreutem Ultraschall in polykristallinen Werkstoffen T2 - Ultraschallprüfung grobkörniger Werkstoffe unter besonderer Berücksichtigung von Austeniten CY - Berlin, Germany DA - 25.09.1980 PY - 1982 SP - 19 EP - 22 CY - Berlin AN - OPUS4-36390 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hecht, Andreas A1 - Mundry, Eberhard A1 - Neumann, Eberhard T1 - Einfluß der Bandbreite auf die Prüfbarkeit streuender Werkstoffe T2 - Ultraschallprüfung grobkörniger Werkstoffe unter besonderer Berücksichtigung von Austeniten CY - Berlin, Germany DA - 25.09.1980 PY - 1982 SP - 85 EP - 94 CY - Berlin AN - OPUS4-36391 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard A1 - Hübner, Heinz W. A1 - Probst, Ulrich T1 - Qualification and Certification Criteria of Casks for the Intermediate Dry Storage of Spent Fuel in the Federal Republic of Germany T2 - 7th International symposium Packaging and Transportation of Radioactive Materials CY - New Orleans, La., USA DA - 15.05.1983 PY - 1983 VL - 1 SP - 224 EP - 230 AN - OPUS4-36393 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard A1 - Hübner, Heinz W. A1 - Probst, Ulrich T1 - Selection and certification of materials for casks intended for the transport and intermediate storage of spent fuel T2 - 7th International symposium Packaging and Transportation of Radioactive Materials CY - New Orleans, La., USA DA - 15.05.1983 PY - 1983 VL - 2 SP - 1048 EP - 1054 AN - OPUS4-36395 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hecht, Andreas A1 - Thiel, Ralf A1 - Neumann, Eberhard A1 - Michel, K. H. A1 - Mülders, H. T1 - Zerstörungsfreie Korngrößenmessung in einer Durchlaufglühanlage an austenitischen Bändern mit Hilfe der Ultraschallrückstreuung T2 - 2. Statusseminar 1982 "Eisen- und Stahlforschung" CY - Berlin, Germany DA - 18.10.1982 PY - 1982 N1 - Schriftenreihe: Programm / Eisen- und Stahlforschung und -technologie der Bundesregierung; 2 SP - 1 EP - 12 CY - Jülich AN - OPUS4-36396 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Amberg, Claus A1 - Czaika, Norbert T1 - On long-term behavior of encapsulated, weldable half bridge strain gages with PtW-wires at temperatures up to 550°C T2 - Seventh International Conference on Experimental Stress Analysis CY - Haifa, Israel DA - 23.08.1982 PY - 1982 SP - 237 EP - 255 PB - Technion, Israel Institute of Technology CY - Haifa AN - OPUS4-36385 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neider, Rudolf A1 - Kowalewsky, Helmut T1 - Das unfallbedingte Risiko bei der Beförderung radioaktiver Stoffe T2 - Gemeinsame Strahlenschutztagung über Radiologische Auswirkungen von Kernkraftwerken und anderen Kerntechnischen Anlagen auf den Menschen und seine Umwelt, Jahrestagung der Société Française de Radioprotection, Jahrestagung des Fachverbandes für Strahlenschutz CY - Lausanne, Switzerland DA - 30.09.1981 PY - 1982 SP - 515 EP - 530 CY - Würenlingen AN - OPUS4-36422 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heidt, Heinrich A1 - Schnitger, Dierk T1 - Eigenschaften und Klassifizierung moderner industrieller Röntgenfilme T2 - Nationale Tagung über zerstörungsfreie Prüfung CY - Helsinki, Finland DA - 06.12.1982 PY - 1982 N1 - Sprache: Finnisch SP - 1 EP - 23 CY - Helsinki AN - OPUS4-36398 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Heinz W. A1 - Masslowski, Jörg-Peter T1 - Interactions between crush conditions and fire resistance for type B (U) packages less than 500 kg T2 - 7th International symposium Packaging and Transportation of Radioactive Materials CY - New Orleans, La., USA DA - 15.05.1983 PY - 1983 VL - 1 SP - 277 EP - 282 AN - OPUS4-36400 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maaß, K.-E. A1 - Weber, P.-M. A1 - Geipel, H. A1 - Hübner, Heinz W. A1 - Weymann, J. T1 - Transport Analyses for Determination of Man-Rem Dose Rates with Regard to Different Modes of Transport, Routing and Packaging T2 - 7th International symposium Packaging and Transportation of Radioactive Materials CY - New Orleans, La., USA DA - 15.05.1983 PY - 1983 VL - 1 SP - 343 EP - 349 AN - OPUS4-36401 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heidt, Heinrich A1 - Stade, Jürgen T1 - Möglichkeiten der Neutronenradiographie mit einem Linear-Beschleuniger T2 - Nationale Tagung über zerstörungsfreie Prüfung CY - Helsinki, Finland DA - 06.12.1982 PY - 1982 SP - 1 EP - 9 CY - Helsinki AN - OPUS4-36402 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz-Forberg, Bernd T1 - Transport and storage of RAM - the role of BAM T2 - 7th International symposium Packaging and Transportation of Radioactive Materials CY - New Orleans, La., USA DA - 15.05.1983 PY - 1983 VL - 1 SP - 555 EP - 562 AN - OPUS4-36404 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Just, Tilman A1 - Neumann, Eberhard ED - Behrens, D. ED - Rahmel, A. T1 - Spongiosenachweis mit Ultraschall-Prüfverfahren T2 - 2. Symposion über Ergebnisse des Forschungs- und Entwicklungsprogramms "Korrosion und Korrosionsschutz" CY - Willingen, Germany DA - 21.04.1980 PY - 1980 SP - 1 EP - 9 CY - Frankfurt am Main AN - OPUS4-36405 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfeil, Norbert A1 - Treumann, Hartwig T1 - Explosion tests on pyrotechnic compositions in a drying house T2 - Colloque International de Pyrotechnie Fondamentale et Appliquée CY - Arcachon, France DA - 05.10.1982 PY - 1982 SP - 639 EP - 648 CY - Saint-Medard-en-Jalles AN - OPUS4-36238 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Aurich, Dietmar A1 - Helms, Rolf A1 - Kühn, Hans-Joachim A1 - Wobst, Klaus A1 - Ziebs, Josef T1 - Kerbschlagarbeit-Hochlage und Rißwiderstand T2 - 10. MPA-Seminar CY - Stuttgart, Germany DA - 01.01.1984 PY - 1984 VL - 10(1) SP - 1 EP - 37 CY - Stuttgart AN - OPUS4-36241 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Aurich, Dietmar A1 - Helms, Rolf A1 - Naseband, Klaus A1 - Ulrich, Armin A1 - Ziebs, Josef A1 - Freudenthal, R. T1 - Failure of Tank Waggon for Liquified Carbon Dioxide: Mechanical and Materials Considerations T2 - International symposium on transport and storage of LPG and LNG CY - Bruges, Belgium DA - 07.05.1984 PY - 1984 SP - 283 EP - 294 CY - Brügge AN - OPUS4-36246 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael ED - Bakir, Nasim T1 - Numerical simulation of solidification crack formation during laser beam welding of austenitic stainless steels under external load N2 - Solidification cracking phenomena taking place under Controlled Tensile Weldability (CTW) test conditions have already been investigated both experimentally and numerically via FEA in order to get a better understanding of the mechanisms of hot crack formation during laser beam welding of austenitic steel grades. This paper develops a three dimensional finite element model employing the contact elements technique to simulate the formation and propagation of solidification cracks during laser full penetration welding of fully austenitic stainless steel 1.4376. During the experimental procedure the resulting strain and displacement directed to the laser beam in the Close vicinity of the weld pool was measured at the surface of the workpiece using a Digital Image Correlation (DIC) technique with an external diode laser as an illuminating source. Local strain fields, global loads and crack lengths predicted by the model are in good Agreement with those observed in experiments. T2 - The 3rd IIW South‐East European Welding Congress CY - Timisoara, Romania DA - 03.06.2015 KW - Solidification cracking KW - DIC technique KW - Laser beam welding KW - Contact element KW - FEA PY - 2015 SN - 978-606-554-955-5 SP - 1 EP - 6 CY - Timisoara, Romania AN - OPUS4-36519 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weise, Hans-Peter T1 - Berechnung der Strahlenexposition in der Umgebung von Schwerionen-Beschleunigeranlagen T2 - Gemeinsame Strahlenschutztagung über Radiologische Auswirkungen von Kernkraftwerken und anderen Kerntechnischen Anlagen auf den Menschen und seine Umwelt, Jahrestagung der Société Française de Radioprotection, Jahrestagung des Fachverbandes für Strahlenschutz CY - Lausanne, Switzerland DA - 30.09.1981 PY - 1982 SP - 45 EP - 52 CY - Würenlingen AN - OPUS4-36435 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Florian, Wolfgang A1 - Jaenicke, Bernd T1 - Verformungsmessungen an einem geschweißten Zahnrad infolge Spannungsarmglühen, Aufkohlen und Härten T2 - Informationstagung des Wissenschaftlichen Beirates der FVA CY - Mannheim, Germany DA - 24.11.1982 PY - 1982 SP - 1 EP - 42 CY - Frankfurt am Main AN - OPUS4-36439 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Florian, Wolfgang A1 - Neumann, Volker ED - Interrante, C. G. T1 - Influence of the H2-content in the shielding gas (during tig-welding) on the diffusible hydrogen in the weld metal and the cold cracking sensitivity of implant specimens T2 - First International Conference on Current Solutions to Hydrogen Problems in Steels CY - Washington, DC, USA DA - 01.11.1982 PY - 1982 SN - 0-87170-148-0 SP - 119 EP - 123 CY - Metals Park AN - OPUS4-36440 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz-Forberg, Bernd A1 - Ulrich, A. T1 - Transport of RAM in Tanks - How to fit into the IAEA safety philosophy T2 - 7th International symposium Packaging and Transportation of Radioactive Materials CY - New Orleans, La., USA DA - 15.05.1983 PY - 1983 VL - 1 SP - 54 EP - 58 AN - OPUS4-36464 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Volker A1 - Florian, Wolfgang A1 - Schönherr, Wolfgang ED - Interrante, C. G. T1 - The hydrogen influenced cold cracking tendency of low alloyed high strength steels - evaluated by the implant test T2 - First International Conference on Current Solutions to Hydrogen Problems in Steels CY - Washington, DC, USA DA - 01.11.1982 PY - 1982 SN - 0-87170-148-0 N1 - Schriftenreihe: IIW Document; IX-1244-82 SP - 147 EP - 152 CY - Metals Park, Ohio AN - OPUS4-36465 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Preß, Henning T1 - Entstehung luftverunreinigender Stoffe beim Arbeiten mit Brenngasen und Sauerstoff, beim Widerstandspunktschweißen und beim Lichtbogenhandschweißen mit umhüllten Stabelektroden in Druckluft T2 - German-Norwegian cooperation in research and technology - workshop "Humanization of working life" CY - Stavanger, Norway DA - 03.11.1982 PY - 1982 SP - 1 EP - 27 AN - OPUS4-36468 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wieser, Karol E. A1 - Jais, Manfred A1 - Holzlöhner, Ulrich T1 - Drop from the reactor building crane - an event covered by the 9 m-drop test requirement? T2 - 7th International symposium Packaging and Transportation of Radioactive Materials CY - New Orleans, La., USA DA - 15.05.1983 PY - 1983 VL - 2 SP - 879 EP - 885 AN - OPUS4-36472 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wieser, Karol E. A1 - Rödel, Roland T1 - Guide to quality assurance measures for manufacturing and use of RAM packagings T2 - 7th International symposium Packaging and Transportation of Radioactive Materials CY - New Orleans, La., USA DA - 15.05.1983 PY - 1983 VL - 2 SP - 1337 EP - 1341 AN - OPUS4-36473 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Krause, Hans-Joachim A1 - Simon, Götz T1 - Supplementary models of weld nugget formation taking resistance spot welding of soft non-alloy steels as an example PY - 1982 IS - III-716-82 SP - 1 EP - 14 CY - Paris AN - OPUS4-36488 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Krause, Hans-Joachim A1 - Simon, Götz T1 - Electrode life of spot welding electrodes depending on varied parameters PY - 1982 IS - III-714-82 SP - 1 EP - 27 CY - Paris AN - OPUS4-36490 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Preß, Henning A1 - Florian, Wolfgang T1 - Formation of toxic substances in gas shielded arc welding PY - 1982 IS - VIII-1080-83 SP - 1 EP - 34 CY - Paris AN - OPUS4-36481 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Martin A1 - Erdt, René A1 - Gödde, M. A1 - Salg, St. A1 - Ittemann, L. T1 - Selbstentzündungsverhalten von Feststoffen: Validierung der Extrapolation von Labortests mithilfe halbtechnischer Versuche bis 1 m3 N2 - Vorgestellt wird ein 2018 gestartetes Projekt zur Überprüfung der Extrapolation von im Labormaßstab ermittelten Selbstentzündungstemperaturen auf technisch relevante Volumina. Für die Ermittlung reaktionskinetischer Daten von Feststoffschüttungen stehen eine Reihe von Untersuchungsmethoden zur Verfügung. Dies sind thermische Analysen wie z. B. die differential scanning calorimetry DSC sowie Mikrokalorimetrie zur hochgenauen Messung von Wärmeströmen, bei denen sehr geringe Probenmengen zum Einsatz kommen. In der Regel wird das Selbstentzündungsverhalten jedoch mithilfe von isoperibolen oder adiabaten Warmlagerungsversuchen beurteilt, hier liegen die Probenvolumina üblicherweise im Bereich von ca. 100 cm3 bis zu einigen Litern. Die Extrapolation über mehrere Größenordnungen auf technische Volumina birgt Unsicherheiten, da mit Zunahme des Lagervolumens veränderte Start- und Randbedingungen vorliegen können. Zudem besteht die Möglichkeit, dass bei in technischen Lagern vorherrschenden niedrigen Temperaturen Reaktionen ablaufen, die in Standard- Laborversuchen nicht erfasst werden, aber einen wesentlichen Einfluss auf das Selbstentzündungsverhalten aufweisen können. Hauptziel des Projektes ist es daher, die im Labormaßstab vorhandenen Prüfeinrichtungen durch einen Versuchsstand zur Untersuchung von Probengrößen von bis zu 1000 dm3 zu erweitern, die Eignung (oder Nichteignung) der etablierten Methoden nachzuweisen und im Labormaßstab nicht erfassbare Einflussgrößen zu ermitteln. Zudem sollen anhand der kleinskaligen Tests Entscheidungskriterien abgeleitet werden, ob eine Extrapolation nach den derzeit üblichen Methoden zulässig ist. T2 - 15. BAM-PTB-Kolloquium zur chemischen und physikalischen Sicherheitstechnik CY - Brunswick, Germany DA - 21.05.2019 KW - Selbstentzündung KW - Formalkinetische Daten KW - Halbtechnische Versuche KW - Thermoanalytische Methoden PY - 2020 SN - 0030-834X VL - 130 IS - 1 SP - 9 EP - 18 AN - OPUS4-51285 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pohl, Rainer A1 - Casperson, Ralf A1 - Ehlers, Henrik A1 - Pelkner, Matthias T1 - Elektromagnetische zerstörungsfreie Prüfverfahren N2 - Übersicht über die die im FB 8.4 bearbeiteten elektromagnetischen Prüfverfahren mit den Schwerpunkten bildgebende Wirbelstromprüfung, sensorbasierte Streuflussprüfung, magnetische Materialcharakterisierung und Sondenentwicklung. KW - Wirbelstromprüfung KW - Wirbelstromsenoren KW - GMR-Sensoren KW - Magnetische Materialcharakterisierung PY - 2020 SP - 1 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-51033 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Maiwald, Michael T1 - On the way to the cyber-physical lab T1 - Auf dem Weg zum cyber-physical Lab N2 - Laboratories tend to be central hubs for chemical, biotechnological, pharmaceutical or foodstuff production. They play a key role in research and development, chemical analysis, quality assurance, maintenance and process control. For process development and optimization, process analytical technology (PAT) has proven to be a powerful tool to improve our understanding of processes, increase productivity, reduce waste and costs and shorten processing times. N2 - Im Allgemeinen sind Laboratorien zentrale Drehscheiben für die chemische, biotechnologische, pharmazeutische oder Lebensmittelproduktion. Sie spielen eine Schlüsselrolle in Forschung und Entwicklung, chemischer Analytik, Qualitätssicherung, Instandhaltung und Prozesskontrolle. Für die Prozessentwicklung und -Optimierung hat sich die Prozessanalysentechnik (PAT) als leistungsfähiges Werkzeug erwiesen, um das Prozessverständnis zu verbessern, die Produktivität zu steigern, Abfall und Kosten zu reduzieren und die Prozesszeit zu verkürzen. KW - Lab of the Future KW - Digitalisation KW - Cyber-physical Lab KW - Smart Laboratoy PY - 2020 SP - 1 EP - 3 PB - Lumitos AG CY - Darmstadt AN - OPUS4-51036 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Komann, Steffen A1 - Ballheimer, Viktor A1 - Quercetti, Thomas A1 - Scheidemann, Robert A1 - Wille, Frank T1 - Mechanical and thermal assessment by BAM of a new package design for the transport of SNF from a german research reactor N2 - For disposal of the research reactor of the Technical University Munich FRM II a new transport and storage cask design was under approval assessment by the German authorities on the basis of International Atomic Energy Agency (IAEA) requirements. The cask body is made of ductile cast iron and closed by two bolted lid systems with metal seals. The material of the lids is stainless steel. On each end of the cask the wood-filled impact limiters are installed to reduce impact loads to the cask under drop test conditions. In the cavity of the cask a basket for five spent fuel elements is arranged. This design has been assessed by the Bundesanstalt für Materialforschung und -prüfung (BAM) in view to the mechanical and thermal safety analyses, the activity release approaches, and subjects of quality assurance and surveillance for manufacturing and operation of the package. For the mechanical safety analyses of the package a combination of experimental testing and analytical/numerical calculations were applied. In total, four drop tests were carried out at the BAM large drop test facility. Two tests were carried out as a full IAEA drop test sequence consisting of a 9m drop test onto an unyielding target and a 1m puncture bar drop test. The other two drop tests were performed as single 9m drop tests and completed by additional analyses for considering the effects of an IAEA drop test sequence. The main objectives of the drop tests were the investigation of the integrity of the package and its safety against release of radioactive material as well as the test of the fastening system of the impact limiters. Furthermore, the acceleration and strain signals measured during the tests were used for the verification of finite-element (FE) models applied in the safety analysis of the package design. T2 - Pressure Vessels & Piping Conference 2020 CY - Online meeting DA - 03.08.2020 KW - Mechanik KW - radioaktives Material KW - Transportbehälter KW - Antragsverfahren KW - Zulassungen KW - Typ-B Versandstück KW - Thermik PY - 2020 VL - 2020 SP - 1 EP - 7 PB - ASME CY - New York AN - OPUS4-51103 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ecke, Alexander A1 - Schneider, Rudolf T1 - Immunanalytische Bestimmung von β-Lactam-Antibiotika und deren Hydrolyseprodukten im Trinkwasser N2 - Die speziellen Herausforderungen der immunanalytischen Bestimmung von β-Lactam-Antibiotika in (Trink-)Wasserproben werden anhand eines neu entwickelten ELISA (enzyme-linked immunosorbent assay) für das Breitbandantibiotikum Amoxicillin diskutiert. Es konnte gezeigt werden, dass die Hydrolyse des Analyten einen positiven Einfluss auf die Erkennung durch den Antikörper hat. Das entsprechende Hydrolyseprodukt, zu dem der Antikörper folglich eine höhere Affinität aufweist, wurde identifiziert und ein entsprechendes Verhalten wurde auch für andere β-Lactam-Antibiotika aus der Gruppe der Penicilline beobachtet. Eine Strategie für die Analyse von Wasserproben hinsichtlich Kontamination mit den hier betrachteten β-Lactamen und deren Hydrolyseprodukten wurde ausgearbeitet. T2 - Wasser 2020 - Jahrestagung der Wasserchemischen Gesellschaft CY - Meeting was canceled DA - 18.05.2020 KW - ELISA KW - Immunoassay KW - Antibiotika KW - Hydrolyseprodukte KW - Amoxicillin PY - 2020 UR - https://www.wasserchemische-gesellschaft.de/images/pdf_veranstaltungen/2020/Wasserchemische_Gesellschaft_Tagungsband_Wasser_2020_s.pdf SP - 466 EP - 470 AN - OPUS4-51061 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Beck, Uwe A1 - Fischer, Daniel T1 - MISTRAL-Müller-Matrix-basierte Identifizierung von Inhomogenitäten und strukturellen Anomalien N2 - Mit abbildender Ellipsometrie (imaging ellipsometry: IE) können Nanometer-Beschichtungen/ Degradationen visualisiert und bezüglich Brechungsindex n, Extinktionskoeffizient k und Schichtdicke d charakterisiert werden. Materialseitig werden lokal Homogenität und Isotropie innerhalb eines/mehrerer Bildpunkte (field of analysis: FOA) und messtechnisch global die Ebenheit der Proben bezüglich aller Bildpunkte des Messfeldes vorausgesetzt. Für die Müller-Matrix-basierte abbildende Ellipsometrie (MM-IE), die den optischen Response anisotroper Materialien in jedem Bildpunkt über die bis zu 16 Müller-Matrix-Elemente erfasst, ist dies von besonderer Relevanz. Reale Substrate sind aber oft nicht eben, können lokal Noppen/Mulden (im FOA) aufweisen oder sind global konvex/ konkav im möglichen Messfeld (field of view: FOV) gekrümmt. Diese lokalen/globalen strukturellen Anomalien des Substrats werden schon für die IE messtechnisch/modellseitig oft nicht beherrscht und sind für die MM-IE in der Wirkung auf die MM-Elemente unbekannt. Diese Defizite sollen messtechnisch bzw. modellmäßig behoben und somit die Messung lokal/global gekrümmter Oberflächen ermöglicht werden (MM-CSIE, CS curved surface). KW - Abbildende Ellipsometrie (IE) KW - Müller-Matrix Ellipsometrie (MM-IE) KW - Gekrümmte Oberflächen KW - Schichtdicke KW - Optische Konstanten PY - 2020 SP - 1 EP - 7 AN - OPUS4-51574 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klewe, Tim A1 - Strangfeld, Christoph A1 - Ritzer, Tobias A1 - Kruschwitz, Sabine T1 - Nondestructive determination of moisture damage in layered building floors N2 - In this ongoing research project, we study the influence of moisture damage on Ground Penetrating Radar (GPR) in different floor constructions. For this purpose, a measurement setup with interchangeable layers is developed to vary the screed material (cement or anhydrite) and insulation material (glass wool, perlite, expanded and extruded polystyrene), as well as the respective layer thickness. The evaluation of the 2 GHz common-offset radar measurements is focused on the extraction of distinctive signal features that can be used to classify the underlying case of damage without any further information about the hidden materials or layer thicknesses. In the collected dataset, we analyze the horizontal distribution of A-scan features in corresponding B-scans to detect water in the insulation layer. Furthermore, possible combinations of these features are investigated with the use of multivariate data analysis and machine learning (logistic regression) in order to evaluate the mutual dependencies. In this study, the combination of an amplitude- and frequency-based feature achieved an accuracy of 93.2 % and performed best to detect a damage in floor insulations. T2 - 18th International Conference on Ground Penetrating Radar CY - Meeting was canceled DA - 14.07.2020 KW - Radar KW - Feuchte KW - Moisture KW - Building floors PY - 2020 DO - https://doi.org/10.1190/gpr2020-045.1 SN - 2159-6832 SP - 164 EP - 167 AN - OPUS4-51575 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Oster, Simon A1 - Mann, S. A1 - Sharma, R. A1 - Reisgen, U. T1 - In-situ Identifikation der Schweißnahtgeometrie bei der Anwendung von MSG-Schweißprozessen N2 - Lichtbogenbasierte Schweißverfahren wie das Metallschutzgasschweißen (MSG) zählen zu den Standardverfahren der Fügetechnik und werden in vielen Industriebereichen automatisiert unter Verwendung von Industrierobotern eingesetzt. Dabei können Schweißnahtabweichungen auftreten, die aus Änderungen der Prozessrandbedingungen und der hohen Prozessdynamik resultieren. Hier ist die Kontrolle von Schmelzbad- und Schweißnahtgeometrie für die Sicherung der Nahtqualität bedeutsam. Durch den Einsatz optischer Sensorsysteme können mit hoher zeitlicher Auflösung in-situ Informationen des Prozesszustands ermittelt werden. Dabei stellen die rauen Prozessbedingungen und die hohe Strahlungsintensität des Lichtbogens eine Herausforderung für die optischen Komponenten dar. Forschungsarbeiten am Institut für Schweißtechnik und Fügetechnik der RWTH Aachen haben gezeigt, dass durch den Einsatz einer HDR-Kamera in Kombination mit einer strukturierten Laserbelichtung gezielt geometrische Informationen des Lichtbogens und des Schmelzbads aus den Prozessaufnahmen gewonnen werden können. In dieser Arbeit wird eine parallele Schweißnaht- und Schmelzbadbeobachtung durchgeführt, wobei geometrische Informationen durch die Anwendung von Bildverarbeitungsalgorithmen extrahiert werden. Dabei wird ein nachlaufendes Sensorsystem eingesetzt, welches aus einer HDR-Kamera und einer Laserbeleuchtung besteht. Es werden diffraktive optische Elemente (DOE) zur Erzeugung von verschiedenen Laserprojektionsmustern verwendet, um sowohl eine unidirektionale als auch eine multidirektionale Prozessbeobachtung durchführen zu können. Aus den geometrischen Informationen werden Kenngrößen berechnet, anhand derer der Prozesszustand beurteilt werden kann. Es zeigt sich, dass anhand der Kenngrößenverläufe Abweichungen in der Schweiß- und Schmelzbadgeometrie und Positionierungsfehler des Roboters identifiziert werden können. T2 - Große Schweißtechnische Tagung - DVS CAMPUS CY - Online meeting DA - 14.09.2020 KW - Schweißnahtgeometrie KW - MSG-Schweißen KW - In-situ Monitoring KW - Schmelzbadbeobachtung PY - 2020 SN - 978-3-96144-098-6 VL - 365 SP - 41 EP - 47 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-51576 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Lars A1 - Scheidemann, Robert A1 - Schönfelder, Thorsten A1 - Komann, Steffen A1 - Wille, Frank T1 - Drop tests assessment of internal shock absorbers for packages loaded with encapsulations for damaged spent nuclear fuel N2 - Damaged spent nuclear fuel (DSNF) can be loaded in German dual-purpose casks (DPC) for transport and interim storage. Encapsulations are needed to guarantee a safe handling and a tight closure, separated from the package enclosure. These encapsulations shall be durable and leak-tight for a long storage period, because they are usually not accessible within periodical inspections of the DPC. Due to the general design of DPCs for standard fuel assemblies, specific requirements have to be considered for the design of encapsulations for DSNF to ensure the loading in existing package designs. Especially the primary lid system of a DPC is designed for maximum loads due to the internal impact of the content during drop test conditions. The main difference of encapsulations for damaged spent nuclear fuel is that they have usually a much higher stiffness than standard fuel assemblies. Therefore the design of an internal shock absorber, e.g. at the head of an encapsulation is required to reduce mechanical loads to the primary lid system during impacts. BAM as part of the German competent authority system is responsible for the safety assessment of the mechanical and thermal package design, the release of radioactive material and the quality assurance of package manufacturing and operation. Concerning the mechanical design of the encapsulation BAM was involved in the comprehensive assessment procedure during the package design approval process. An internal shock absorber was developed by the package designer with numerical analyses and experimental drop tests. Experimental drop tests are needed to cover limiting parameters regarding, e.g. temperature and wall thickness of the shock absorbing element to enable a detailed specification of the whole load-deformation behavior of the encapsulation shock absorber. The paper gives an overview of the assessment work by BAM and points out the main findings which are relevant for an acceptable design of internal shock absorbers. The physical drop tests were planned on the basis of pre-investigations of the applicant concerning shape, dimension and material properties. In advance of the final drop tests the possible internal impact behavior had to be analyzed and the setup of the test facility had to be validated. The planning, performance and evaluation of the final drop tests were witnessed and assessed by BAM. In conclusion it could be approved that the German encapsulation system for damaged spent nuclear fuel with shock absorbing components can be handled similar to standard fuel assemblies in existing package designs. T2 - Pressure Vessels & Piping Conference 2020 CY - Online meeting DA - 03.08.2020 KW - Encapsulations for damaged spent nuclear fuel KW - Drop tests KW - Internal shock absorber KW - Design assessment of RAM packages PY - 2020 SP - 1 EP - 9 AN - OPUS4-51546 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Tornaghi, M. L. A1 - Tsionis, G. A1 - Pegon, P. A1 - Molina, J. A1 - Peroni, M. A1 - Korzen, Manfred A1 - Tondini, N. A1 - Covi, P. A1 - Abbiati, G. A1 - Antonelli, M. A1 - Gilardi, B. T1 - Experimental study of braced steel frames subjected to fire after earthquake N2 - The EQUFIRE project aims to study the post-earthquake fire Performance of steel frame structures and is part of the Transnational Access activities of the SERA project (www.sera-eu.org) at the ELSA Reaction Wall of the European Commission - Joint Research Centre. As it has happened in many historical occasions, after an earthquake, earthquakeinduced rupture of gas piping, failure of electrical systems, etc. may trigger fire. The structural fire performance can deteriorate because the fire acts on a previously damaged structure. In addition, the earthquake may have damaged fire protection elements and the fire can spread more rapidly if compartmentation walls have failed. This is particularly relevant for steel structures as the high thermal conductivity of elements with small thickness entails quick temperature rise with consequent fast loss of strength and stiffness. EQUFIRE studied a four-storey three-bay steel frame with concentric bracings in the central bay. The structure was designed for reference peak ground acceleration equal to 0.186g, soil type B and type 1 elastic response spectrum according to Eurocode 8. Tests were performed at the ELSA Reaction Wall and at the furnace of the Federal Institute for Materials Research and Testing (BAM). The experimental activities at the ELSA Reaction Wall comprise pseudo-dynamic tests on a full-scale specimen of the first storey of the building, while the upper three storeys are numerically simulated. The aim is to study the response of the structure and fire protection elements, including their interaction, under the design earthquake and for different configurations: bare frame without fire protection, specimen with three fire protection solutions (conventional and seismic-resistant boards, and vermiculite sprayed coating) applied on the bracing and one column, and with conventional and seismic-resistant fire barrier walls built in the two external bays of the specimen. The testing programme at BAM included fire tests of five columns (two specimens without fire protection elements and three specimens with the types of fire protection mentioned above). Before the fire test, each column was subjected to a horizontal and vertical displacement history resulting from the seismic action. During the fire tests, the effect of the surrounding structure was simulated by limiting the axial thermal expansion. The experimental results will serve to study the response of structural and non-structural components to fire following earthquake scenarios, with a view to improving existing design guidelines and future standards. T2 - The 17th World Conference on Earthquake Engineering - 17WCEE CY - Meeting was canceled DA - 13.09.2020 KW - Fire following earthquake KW - Concentrically braced steel frames KW - Large-scale tests KW - Pseudo-dynamic testing KW - Substructuring PY - 2020 SP - 2i-0104-1 EP - 2i-0104-12 AN - OPUS4-51426 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bröcker, S. A1 - Klaer, R.-H. A1 - Kockmann, N. A1 - Maiwald, Michael T1 - Process Industry United in the Digital World - The current landscape of research for the digitalization of the process industry N2 - The Tutzing Symposium "100 % digital: survival strategies for the process industry" (see 4.1) in April 2018 was characterized by a great momentum which has been taken up and continued until today. The aim was to implement the ideas from the Tutzing Symposium in a coordinated and targeted manner. For this purpose, development needs as well as the numerous currently planned or already started research and development activities in the context of digitalisation were first compiled and analysed. This resulted in the current research landscape for digitalization in the process industry. It now enables to identify open topics and to translate them into research funding programs as well as to define new projects in the dialogue between users, suppliers and research, which are to be meaningfully interlinked and consolidated with existing projects. Due to the strong interest in digitalisation, activities are constantly being added, so that this paper can only provide a snapshot of the situation in the period 2019-2020. KW - Process Industry KW - Digitalisation KW - Tutzing Symposion KW - research landscape KW - Process Control PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-512265 UR - https://processnet.org/en/TAKdigital.html SP - 1 EP - 15 AN - OPUS4-51226 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Droste, Bernhard A1 - Schulz, Ina T1 - Gewässerschutz bei der Beförderung wassergefährdender Stoffe auf Binnenschiffen T1 - Water protection in transportation of dangerous goods by vessels on inland waterways N2 - Die Studie gibt einen Überblick über den Umfang und die Struktur der Gefahrgutbeförderung auf Binnenschiffen und stellt die maßgeblichen sicherheitstechnischen Vorschriften dar. Aus dem Unfallgeschehen läßt sich entnehmen, daß in West-Deutschland jährlich ca. 1200 Binnenschiffsunfälle mit größenordnungsmäßig insgesamt 100 bis 300 m³ Ladungsaustritt verbunden sind, wozu fast ausschließlich Mineralölprodukte gehören, und zumeist ein oder zwei Unfälle den größten Beitrag liefern. Während nach Unfällen häufig mit Erfolg Ölsperren zur Begrenzung von Gewässerverunreinigungen eingesetzt werden können, führen ungeklärte Entsorgungsprobleme zu wesentlich kritischer einzuschätzenden, verdeckten Verunreinigungen der Gewässer. Insbesondere die Entsorgung von Ladungsresten bedarf in technischer, administrativer und wirtschaftlicher Hinsicht einer zufriedenstellenden Klärung wie sie z. B. bei der Bilgenwasserentsorgung existiert. N2 - The study gives a survey on the structure and amount of dangerous goods carriage on inland waterway vessels. The technical safety requirements are presented. The accident statistics of West-Germany show that appr. 1200 incidents per year lead to loss of loading of a total amount of 100 to 300 m³. The lost goods are nearly in every case inflammable liquids, and usually only one or two incidents p. a. cause major losses. After accidents often mobile oil barriers can stop water pollution. Unsolved problems in vessel decommissioning serve much more critical situations with respect to water pollution. Primarily the decommissioning of remaining parts of the hazardous cargo inside vessels needs to be clarified with respect to technical, administrative and commercial reasons. KW - Gefahrgutbeförderung KW - Binnenschiffe KW - Gewässerschutz KW - Tankschiffsunfälle KW - Entsorgungsprobleme von Binnenschiffen PY - 1993 VL - Forschungsbericht 102 03 439 SP - 1 EP - 93 PB - Umweltbundesamt CY - Berlin AN - OPUS4-51134 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz T1 - A mid-frequency component of train-induced ground vibration due to scattered axle impulses and the irregularities of the soil and ballast N2 - The passage of the train is dominated by the impulses of the static axle loads. The response of the regular homogeneous and irregular soils has been calculated by the finite-element method in frequency domain. The superposition of the impulse responses yields the quasi-static component of the ground vibration which is restricted to very low frequencies and to the close near-field of the track. In case of an irregular soil or ballast of which the stiffness varies randomly in space, a mid-frequency ground vibration component is generated by the scattering of the axle impulses. Measurements will be shown which prove the existence of the mid-frequency ground vibration component and the unique explanation by the scattered axle impulses: many international measurements with a raised mid-frequency component, axle-box measurements with a too low mid-frequency dynamic load, amplitude-speed dependencies which are incompatible with irregularity-induced dynamic loads, and ground vibration reductions due to stiff track elements. T2 - International Conference on Noise and Vibration Engineering (ISMA/USD) CY - Online meeting DA - 07.09.2020 KW - Ground vibration KW - Railway KW - Irregular soil KW - Irregular ballast KW - Axle impulses PY - 2020 SP - 2611 EP - 2625 PB - KULeuven CY - Leuven AN - OPUS4-51210 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz A1 - Said, Samir A1 - Rohrmann, R. T1 - Natural frequencies and modes of poles, beams, floors, road and rail bridges N2 - In the last three decades, the vibrations of many floors and bridges have been measured. The contribution shows some evaluation methods, experimental results and some modelling and theoretical results. Simple evaluation methods have been developed for single and coupled floors. Two coupled beams have been measured in good agreement with the theory. A more complex coupling model has been found for a large wooden floor in a castle consisting of six floor bays which correlates well with the measurements. Damaged and intact poles have been tested by their natural frequencies and damping values, and a fair correlation between the degree of damage and the shift of the frequency. Road bridges have been analysed in detail and some examples are presented. Railway bridges and trains are studied for resonant excitation. The risk of resonance can be estimated in frequency domain by using axle-sequence spectra of the train and the natural frequencies of the bridge. A measurement example shows the amplification, but even stronger the cancellation of the subsequent axle responses. Several high-speed trains and freight trains have been analysed for their potential resonance amplification. T2 - International Conference on Noise and Vibration Engineering (ISMA/USD 2020) CY - Online meeting DA - 07.09.2020 KW - Modalanalyse KW - Bauwerke KW - Bauteile KW - Brücken KW - Achsfolgespektren PY - 2020 SP - 1573 EP - 1585 PB - KULeuven CY - Leuven AN - OPUS4-51211 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Enzner, Verena A1 - Holm, Olaf A1 - Abis, Marco A1 - Kuchta, Kerstin T1 - The characterisation of the fine fraction of MSWI bottom ashes for the pollution and resource potential N2 - The fine fraction of bottom ash from municipal solid waste incineration is characterized of both a high pollution and relevant resource potential. Methods for studying the environmental behaviour of solid residues are leaching tests. Various leaching test are adopted all over Europe with liquid to solid ratio of 2 or 10 l/kg. In Germany three different leaching Tests are valid with the commencement of the draft of the ordinance of reuse of mineral waste as alternative building ordinance. Comparing two batch tests, only the concentration for chloride is comparable. To evaluate the metal resource potential in the sand fraction wet chemical Methods have been applied. Methodical problems were caused mainly by the material heterogeneity and especially for precious metals due to their low concentration around 1 mg/kg. Other Methods have been available, but hardly applicable. T2 - 16. International Waste Management and Landfill Symposium CY - Cagliari, Italy DA - 02.10.2017 KW - Bottom ash KW - Resource recovery PY - 2017 SN - 978-88-6265-0113 SP - 1 EP - 9 PB - CISA Publisher CY - Padova, Italy AN - OPUS4-51184 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Feldkamp, Martin A1 - Quercetti, Thomas A1 - Wille, Frank T1 - Outcomes of three large scale fire reference tests conducted in BAM fire test facility N2 - Packages for the transport of high-level radioactive material are designed to withstand severe accidents. Hypothetical severe accident conditions are defined in the IAEA Regulations for the Safe Transport of Radioactive Materials. One of these accident conditions is the thermal test, mainly consisting of a 30 minute fully engulfing 800°C pool fire or an equally severe fire test. The heat fluxes into the package depend substantially on the fire characteristics and the Surface temperature of the package. Fire tests can be performed at BAM on a propane gas fire test facility. In order to investigate the heat fluxes over a wide range of surface temperatures in this test facility a fire reference package was designed for multiple use. The package represented the outer geometry of a specific transport cask for radioactive waste. The fire reference package is a closed steel sheet cylinder with a wall thickness of 10 mm, a length of 1500 mm and a diameter of 1050 mm. The package was instrumented with thermocouples and filled with heat resistant insulation material. Three open-air fire tests were performed in the BAM propane gas fire test facility. The flames exposure time period varied slightly for the fire tests. The wind direction as well as the wind Speed were measured and changed between and during the tests. Test stand parameters such as wind shield location and propane gas volume flow were chosen constant for the three tests. The locally measured fire reference package steel sheet temperatures were used for the calculation of heat fluxes as function of time and surface temperature. The measured temperatures allowed further calculations. In a first approach effective fire characteristics of the propane gas fire, including the flame temperature, the fire convection coefficient and a Radiation exchange coefficient mathematically describing the determined average heat flux over the surface temperature were calculated. T2 - Pressure Vessels & Piping Conference 2020 CY - Online meeting DA - 03.08.2020 KW - Fire KW - Testing KW - Large scale testing KW - Calorimeter KW - Heat flux PY - 2020 SP - 1 EP - 9 PB - ASME CY - New York AN - OPUS4-51192 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lugovtsova, Yevgeniya A1 - Bulletti, A. A1 - Giannelli, P. A1 - Capineri, L. A1 - Prager, Jens T1 - Characterization of a Flexible Piezopolymer-based Interdigital Transducer for Selective Excitation of Ultrasonic Guided Waves N2 - Structural health monitoring (SHM) is a term that groups together techniques adopted to evaluate in a continued fashion the structural integrity and degradation of technical appliances. SHM is particularly attractive for components that are difficult to access or expensive to take off-line. Among many other techniques, SHM can be performed using ultrasonic guided waves (UGW) which have an advantage of traveling over Long distances. Various guided wave modes exist along with many methods for their generation and sensing, e.g by means of interdigital transducers (IDT). This contribution is dedicated to the design and characterization of a flexible piezopolymerbased IDT which allows for the selective excitation of UGW, resulting in more straightforward data analysis. The designed IDT was characterized using a 3D Laser Doppler Vibrometer (3D LDV) in the air to identify and analyze the IDT’s Vibration modes. Then the transducer was mounted on an aluminum plate, and the generated wavefield was measured with the 3D LDV. According to this investigation, we demonstrate that it is possible to selectively excite desired guided wave mode, namely the A0 mode, suppressing the excitation of the S0 mode. Moreover, the measured wavefield allows for analysis of the directivity of the designed IDT. All in all the results show good correlation between theoretical predictions and measured values, thus allowing to use the current design in terms of selective excitation as it is. T2 - I2020 IEEE International Ultrasonics Symposium (IUS) CY - Online meeting DA - 07.09.2020 KW - Lamb waves KW - Non-Destructive Testing KW - Structural Health Monitoring KW - Polyvinylidene Fluoride (PVDF) PY - 2020 SN - 978-1-7281-5448-0 SP - 1261, 45 AN - OPUS4-51441 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Seeger, Stefan A1 - Rasch, Fabian A1 - Erdmann, Kerstin A1 - Brödner, Doris A1 - Wilke, Olaf T1 - Weiterentwicklung des Prüfwertes für Ultrafeinstaubpartikel beim Umweltzeichen Blauer Engel für Drucker N2 - Berichtet wird über ein abgeschlossenes Folgeprojekt zu vorangegangenen Forschungsprojekte zum gleichen Thema. In diesem Projekt wurde das Messverfahren und der Prüfwert für die Partikelemission aus Bürogeräten (siehe Vergabegrundlage DE-UZ 205, Anhang S-M) validiert und weiterentwickelt. Dies geschah erstens durch Auswertung der Qualität der im Zuge der Antragsbearbeitung für das Umweltzeichen beim RAL vorgelegten Prüfberichte der zugelassenen Prüfinstitute und - basierend darauf - durch Erarbeitung von technisch-methodischen Veränderungsvorschlägen für die Prüfung der chemischen Emissionen, inklusive der Partikelemissionen. Zweitens wurde zur Beurteilung der Veränderung der Emissionen aktueller gegenüber älteren Geräte-generationen ein nicht repräsentativer Pool von table-top-Laserdruckern aufgebaut und die chemischen Emissionen wurden gemäß DE-UZ-205, Anhang S-M gemessen. Ergänzend wurde eine quantitative chemische Analyse der anorganischen Feststoffe - insbesondere der Metalle - in den emittierten Aerosolen vorgenommen die Feststoffgehalte um 2 Massen-% ergaben. Diese Ergebnisse wurden gemeinsam mit neueren wissenschaftlichen Untersuchungen zur gesundheitlichen Bewertung der Emissionen aus Laserdruckern ausgewertet, es besteht kein Handlungsbedarf hinsichtlich einer Veränderung von Prüfkriterien und Prüfwerten. Drittens wurde untersucht und bestätigt, dass mit dem Ziel eines zukünftigen Umweltzeichens das Emissionsverhalten Kunststoff verarbeitender 3D-FDM-Drucker und/oder die darin verarbeiteten Verbrauchsmaterialien (Filamente) mit dem für Laserdrucker entwickelten Mess- und Prüfschema charakterisiert und quantifiziert werden können. Untersuchungen an Stereo-lithografie (SLA)-Druckern und Vorrichtungen zur Nach-Aushärtung (Curing Units) ergaben keine nachweisbaren Partikelemissionen. KW - Blauer Engel KW - Bürogeräte mit Druckfunktion KW - Emissionen KW - Aerosole KW - Schadgase PY - 2020 UR - https://www.umweltbundesamt.de/publikationen/weiterentwicklung-des-pruefwertes-fuer SN - 1862-4804 VL - 217 SP - 5 EP - 82 PB - Umweltbundesamt CY - Dessau-Roßlau AN - OPUS4-51745 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gottlieb, Cassian A1 - Bohling, Christian A1 - Wilsch, Gerd T1 - New possibilities for concrete analysis 4.0 with the Laser-Induced Breakdown Spectroscopy (LIBS) N2 - In civil engineering the damage assessment of concrete infrastructures is an important task to monitor and ensure the estimated life-time. The aging of concrete is caused by different damage processes like the chloride induced pitting corrosion of the reinforcement. The penetration depth and the concentration of harmful species are crucial factors in the damage assessment. As a highly cost and time-consuming standard procedure, the analysis of concrete drill cores or drilling by wet-chemistry is widely used. This method provides element concentration to the total mass as aggregates and binder are homogenized. In order to provide a method that is capable to detect the element concentration regarding the cement content only, the laser-induced breakdown spectroscopy (LIBS) will be presented. The LIBS method uses a focused pulsed laser on the sample surface to ablate material. The high-power density and the laser-material interaction causes a laser-induced plasma that emits elemental and molecular line emission due to energy transition of the excited species in the plasma during the cooling phase. As each element provides element-specific line emission, it is in principle possible to detect any element on the periodic table (spectroscopic fingerprint) with one laser shot. In combination with a translation stage the sample under investigation can be spatially resolved using a scan raster with a resolution up to 100 µm (element mapping). Due to the high spatial resolution, the element distribution and the heterogeneity of the concrete can be evaluated. By using chemometrics the non-relevant aggregates can be excluded from the data set and the element concentration can be quantified and referred to a specific solid phase like the binding matrix (cement) only. In order to analyze transport processes like diffusion and migration the twodimensional element distributions can provide deep insight into the transport through the pore space and local enrichments of elements. As LIBS is a multi-elemental method it is also possible to compare the ingress and transport process of different elements like Cl, Na, K, S, C, and Li simultaneously and evaluate cross-correlations between the different ions. Furthermore, the element mapping allows to visualize the transport along cracks. This work will show the state of the art in terms of hardware and software for an automated LIBS system as well as different application for a concrete analysis 4.0. Focus will be the application of LIBS for a fast concrete analysis. T2 - SMAR 2019 CY - Potsdam, Germany DA - 27.08.2019 KW - Damage KW - LIBS KW - Concrete KW - Mapping KW - Chlorine PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-517282 UR - https://www.ndt.net/?id=24963 SN - 1435-4934 VL - 25 IS - 1 SP - 1 EP - 8 PB - NDT.net CY - Kirchwald AN - OPUS4-51728 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nerger, Deborah A1 - Moosavi, Robabeh A1 - Bracklow, F. A1 - Hering, M. A1 - Kühn, T. A1 - Curbach, M. A1 - Hille, Falk A1 - Rogge, Andreas ED - Papadrakakis, M. ED - Fragiadakis, M. ED - Papadimitriou, C. T1 - Impact damage characterization at RC plates with planar tomography and FEM N2 - Prediction of dynamic effects of reinforced concrete structures under impact loading is a technical challenge. This is a consequence of the great variability of the physical properties resulting from the wide adaptability of reinforced concrete and a consequence of the wide range of impact loading. Experiments and numerical investigations are normally used on a small scale to address the problem. In this paper, impact tests on reinforced conrete plates with the lateral dimensions of 1.5 m x 1.5 m and a thickness of 30 cm are presented. In bending reinforcement, besides the velocity two properties are varied, the diameter and the spatial distribution of the rebars. Experiments are performed at the Otto-Mohr-Laboratory of the Institute of Concrete Structures of the Technische Universit¨at Dresden. Due to the accelerated fall of the impactor the velocity ranges between 20 and 70 m/s. In addition to the measured quantities such as bearing forces, accelerations are also measured at 4 different positions on and under the plate, as well as the deflection at several positions. The measured data are used for the analysis of the damage form and the numerical examinations with the program Ansys Autodyn and the material model after Drucker-Prager. Numerical investigations support the tests, with detailed analysis of individual effects. These numerical computations and the planar tomographic investigations were carried out at BAM in Berlin. With the help of planar tomographic evaluation, the damaged structure is made visible and compared with the numerical results. Influences of the bending reinforcement are explained on the basis of damage evaluation in the local area and on selected measured values. In addition to the test evaluation, the tomographic and numerical methods are presented. T2 - XI International Conference on Structural Dynamics (EURODYN 2020) CY - Online meeting DA - 23.11.2020 KW - Post-impact evaluation KW - Damage characterization KW - Planar tomography KW - Drucker-Prager KW - Ansys Autodyn PY - 2020 SN - 978-618-85072-2-7 VL - 1 SP - 2521 EP - 2543 PB - Institute of Structural Analysis and Antiseismic Research, School of Civil Engineering, National Technical University of Athens (NTUA), Greece CY - Athens, Greece AN - OPUS4-51769 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pauw, Brian Richard A1 - Szymoniak, Paulina T1 - Dataset and Jupyter worksheet interpreting the (results from) small- and wide-angle scattering data from a series of boehmite/epoxy nanocomposites. Accompanies the publication "Competition of nanoparticle-induced mobilization and immobilization effects on segmental dynamics of an epoxy-based nanocomposite" N2 - Dataset and Jupyter worksheet interpreting the (results from) small- and wide-angle scattering data from a series of boehmite/epoxy nanocomposites. Accompanies the publication "Competition of nanoparticle-induced mobilization and immobilization effects on segmental dynamics of an epoxy-based nanocomposite", by Paulina Szymoniak, Brian R. Pauw, Xintong Qu, and Andreas Schönhals. Datasets are in three-column ascii (processed and azimuthally averaged data) from a Xenocs NanoInXider SW instrument. Monte-Carlo analyses were performed using McSAS 1.3.1, other analyses are in the Python 3.7 worksheet. Graphics and result tables are output by the worksheet. KW - Small angle scattering KW - X-ray scattering KW - Nanocomposite KW - Polymer nanocomposite KW - Boehmite KW - Analysis KW - SAXS/WAXS PY - 2020 DO - https://doi.org/10.5281/zenodo.4321087 PB - Zenodo CY - Geneva AN - OPUS4-51829 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Dittmann, Daniel T1 - Experimental raw data for "Specific adsorption sites and conditions derived by thermal decomposition of activated carbons and adsorbed carbamazepine" N2 - This is the repository of all experimental raw data used in the Scientific Reports publication "Specific adsorption sites and conditions derived by thermal decomposition of activated carbons and adsorbed carbamazepine" by Daniel Dittmann, Paul Eisentraut, Caroline Goedecke, Yosri Wiesner, Martin Jekel, Aki Sebastian Ruhl, and Ulrike Braun. It includes - overview_measurements.xlsx and overview_measurements.ods containing a list of all TGA experiments (TGA, TGA-FTIR, TED-GC-MS, and ramp-kinetics) - TED-GC-MS.zip containing gas chromatography-mass spectrometry experimtent files for the Chemstation and OpenChrom - TGA.zip containing thermogravimetric analyses raw data on evolved gas analyses experiments (TGA-FTIR and TED-GC-MS) - TGA_kinetics.zip containing thermogravimetric analyses raw data on decomposition kinetic experiments (ramp-kinetics) - TGA-FTIR.zip containing Fourier-transform infrared spectroscopy series files for OMNIC - XRF.zip containing x-ray flourescence data on elemental composition KW - Adsorption KW - Aktivkohle KW - TED-GC/MS KW - Thermoanalytik PY - 2020 DO - https://doi.org/10.5281/zenodo.3716316 PB - Zenodo CY - Geneva AN - OPUS4-51902 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Ahmadi, Samim A1 - Lecompagnon, Julien A1 - Hirsch, Philipp Daniel A1 - Burgholzer, P. A1 - Jung, P. A1 - Caire, G. T1 - Laser excited super resolution thermal imaging for nondestructive inspection of internal defects N2 - A photothermal super resolution technique is proposed for an improved inspection of internal defects. To evaluate the potential of the laser-based thermographic technique, an additively manufactured stainless steel specimen with closely spaced internal cavities is used. Four different experimental configurations in transmission, reflection, stepwise and continuous scanning are investigated. The applied image post-processing method is based on compressed sensing and makes use of the block sparsity from multiple measurement events. This concerted approach of experimental measurement strategy and numerical optimization enables the resolution of internal defects and outperforms conventional thermographic inspection techniques. KW - Super resolution KW - Photothermal KW - Imaging KW - Compressed sensing KW - Internal defects KW - Nondestructive testing PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-518866 DO - https://doi.org/10.48550/arXiv.2007.03341 SN - 2331-8422 SP - 1 EP - 9 PB - Cornell University CY - Ithaca, NY AN - OPUS4-51886 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Léonard, Fabien T1 - Overview of XCT data processing workflow for ammonium nitrate prills quantitative analysis N2 - This video presents the data processing workflow that was developed to perform the quantitative structural and morphological analysis of ammonium nitrate prills by x-ray computed tomography. KW - ANFO KW - Data processing KW - Explosives KW - Porosity KW - Surface area KW - XCT PY - 2020 DO - https://doi.org/10.5281/zenodo.3611339 PB - Zenodo CY - Geneva AN - OPUS4-51897 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gottlieb, C. A1 - Bohling, C. A1 - Millar, S. A1 - Günther, Tobias A1 - Wilsch, Gerd ED - Krieger, J. ED - Isecke, B. T1 - Schnelle ortsaufgelöste Chloridbestimmung mit der laserinduzierten Plasmaspektroskopie (LIBS) N2 - Im Zuge der Ist-Zustandserfassung von Stahl- und Spannbetonbauwerken spielt die chemische Analyse von Beton eine zentrale Rolle. Durch den externen Eintrag von schädigenden Substanzen wie Chlorid oder Alkalien aus Tausalzen oder Meerwasser, kann u.U. der Beton und/oder die Stahlbewehrung angegriffen werden. Bei Überschreitung kritischer korrosionsauslösender Chloridgehalte, z.B. bei Stahlbeton 0,4 M.-% (bzw. 0,5 M.-%) und Spannbeton 0,2 M.-% bezogen auf den Zement, erhöht sich das Risiko für eine Chlorid-induzierte Korrosion. Für die Beurteilung eines Instandsetzungsbedarfs und, sofern notwendig, der Erarbeitung eines Instandsetzungskonzeptes muss nach der Rili-SIB1 ein sachkundiger Planer herangezogen werden. Standardmäßig werden für die chemische Analyse Bohrkerne bzw. Bohrmehlproben aus dem zu untersuchenden Bauwerk entnommen und nach aufwendiger Probenvorbereitung nasschemisch analysiert (nach DAfStb Heft 401 oder DIN 14629). Dabei wird der Gesamtchloridgehalt bezogen auf die Einwaage angegeben. Eine Umrechnung auf den Zementgehalt erfolgt i.d.R. durch Schätzwerte. Der Einsatz der laserinduzierten Plasmaspektroskopie (LIBS) wird seit Mitte der 90er Jahren an der Bundesanstalt für Materialforschung und -prüfung erforscht, um den Chloridgehalt durch eine ortsaufgelöste Elementanalyse an einer Betonprobe möglichst genau zu ermitteln. Die zweidimensionale LIBS-Messung mit einer lateralen Auflösung von 100 µm x 100 µm erlaubt die Berücksichtigung der Heterogenität von Beton. Dabei lassen sich die Bindemittelmatrix und die Gesteinskörnung separat betrachten, wodurch sich die Aussagekraft der Ergebnisse und somit die Sicherheit der chemischen Zustandserfassung erhöht. Durch die stetige Weiterentwicklung von Komponenten wie Laser, Spektrometer und analytischer Auswerteroutinen sind mittlerweile automatisierte Systeme für die schnelle LIBS-Analyse auf dem Markt verfügbar. In diesem Vortrag wird der aktuelle Stand der Technik anhand von Praxisbeispielen präsentiert und entscheidende Vorteile gegenüber dem Standardverfahren herausgestellt. Aufgrund der Möglichkeit für eine simultane Multielementanalyse mit LIBS werden weitere Anwendungen, wie z.B. die Ermittlung der Karbonatisierungstiefe, Untersuchungen von Transportprozessen, Chlorideintrag entlang von Rissen oder Untersuchungen von Elementverteilungen im Kontext einer AKR vorgestellt. T2 - 4. Brückenkolloquium CY - Online meeting DA - 08.09.2020 KW - Chloride KW - Beton KW - LIBS KW - Schädigung PY - 2020 SN - 978-3-8169-3518-6 SP - 465 EP - 471 PB - Narr Francke Attempto Verlag GmbH + Co. KG CY - Tübingen AN - OPUS4-51681 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bayerlein, Bernd T1 - Focused ion beam techniques beyond the ordinary - Methodological developments within ADVENT N2 - This poster presents the focused ion beam preparation methodologies developed within the framework of the EU funded EURAMET project ADVENT (Advanced Energy-Saving Technology). It summarises the key breakthroughs achieved for various in situ investigation techniques, e.g. in situ experiments at the Synchrotron facility BESSY II (IR-SNOM and XRS), TEM and SMM instrumentation. The created experimental devices from diverse thin-film semiconductor materials paved the way to dynamic structural studies bearing the potential to determine nanoscale correlations between strain and electric fields and, moreover, for the fundamental development of new in situ capabilities. N2 - Dieses Poster zeigt die FIB Präparationstechniquen, die im Rahmen des EU-finanzierten EURAMET-Projekts ADVENT (Advanced Energy Saving Technology) entwickelt wurden. Es fasst die wichtigsten Errungenschaften zusammen, die für verschiedene in situ Untersuchungstechniken erzielt wurden, z.B. situ-Experimente in dem Synchrotronring BESSY II (IR-SNOM und XRS), in situ TEM Experimente und für die SMM Technik. Die experimentellen Probenstrukturen, die aus verschiedenen Dünnschicht-Halbleitermaterialien erzeugt wurden, ebneten den Weg für dynamische Strukturstudien, die das Potenzial haben, nanoskalige Korrelationen zwischen Dehnung und elektrischen Feldern zu bestimmen und darüber hinaus neue in situ Messmethoden zu entwickeln. T2 - Final Meeting CY - Online Meeting DA - 30.06.2020 KW - FIB KW - Sample preparation KW - In situ KW - TEM KW - AFM PY - 2020 AN - OPUS4-51606 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Kulow, Anicó T1 - Spatial Resolved Dispersive X-Ray Absorption Spectroscopy and Coded Aperture X-Ray Fluorescence Imaging N2 - One aim of this work was the development of a new setup for time- and laterally resolved XAFS measurements, based on the pronciple of dispersive XAFS. This setup is scanning free, stable, inexpensive, and straightforward to adjust for probing different elements. The second part of this work describes the impelemntation of a method for full-field X-ray fluorescence imaging with coded apertures. Expensive and complicated X-ray otpics, that are usually used for full-field imaging, are replaced with a coded aperture that consists of many pinholes drilled in an X-ray opaque material. Coded apertures are inexpensive to fabricate, energy independent and easy to use. The working principle is the same as with a pinhole camera, but the multiple holes allow a higher photon flux compared to a single pinhole or even a polycalippary optic, thus alowwing the reduction of measurement time. KW - X-ray fluorescence imaging KW - Coded Apertures KW - X-ray absorption spectroscopy KW - Synchrotron PY - 2021 SP - 1 EP - 175 CY - Berlin AN - OPUS4-52054 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Palanti, S. A1 - Cragg, S. A1 - Plarre, Rüdiger T1 - Resistance against marine borers: About the revision of EN 275 and the attempt for a new laboratory standard for Limnoria N2 - Wood protection technology in the marine environment has changed over the last decades and will continue to do so. New active ingredients, newer formulations, and novel wood-based materials including physically- and chemically-modified wood, together with increasing concerns over environmental impacts of wood preservatives, urgently demand a major revision of EN 275 “Wood preservatives – Determination of the Protective Effectiveness against Marine Borers”, dated from 1992. This IRG document reports on the technical work in CEN TC 38 regarding the revision of this standard. A Task Group within WG 24 of CEN TC 38 was formed consisting of experts from different field of competence (e.g. wood preservatives industry, wood scientists, marine biologists, archaeologists and cultural heritage conservators). Starting by e-mail correspondence in 2014, and continuing with four physical meetings (Berlin 2x, Florence, Venice) with experts from Germany, Italy, Sweden, and UK were held so far. Significant items for revision in EN 275 were identified as: number of replicates, duration of the test, dimension of specimens, number of test sites, number of reference species, reference material including reference preservative, re-immersion of specimens after non-destructive periodical evaluation for longer periods of time vs higher number of replicates for successive destructive examinations without re-immersion, utilization of X- ray apparatus and specific software to ease evaluation, etc. Furthermore, the task group is working on a standardized lab test for time-saving evaluation of different wood qualities for their potential to resist attack by limnorids. The suitability of this lab test will be determined by round robin tests as soon as safe face-to-face collaboration permits. The outcome will be published as a CEN TR (Technical Report) document, with a view to eventual adoption within the revised standard. T2 - THE INTERNATIONAL RESEARCH GROUP ON WOOD PROTECTION CY - Online meeting DA - 10.06.2020 KW - Standardization KW - Marine borers KW - Bankia sp KW - Teredo sp KW - Limnoria spp KW - Durability PY - 2020 VL - 2020 SP - IRG/WP 20-20669-1 EP - IRG/WP 20-20669-11 CY - Stockholm AN - OPUS4-52064 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Kalbe, Ute A1 - Schatten, René A1 - Szuppa, Tony T1 - Monitoringprogramm zur Verwertung von Bodenmaterial gemäß §§ 6-8 Novelle BBodSchV N2 - Mit der Novellierung der Bundes-Bodenschutz- und Altlastenverordnung (BBodSchV) (am 6.11.2020 im Bundesratsverfahren beschlossen) werden Regelungen zum Auf- und Einbringen von Bodenmaterial außerhalb der durchwurzelbaren Bodenschicht aufgenommen (sogenannte Verfüllungen). Ziel des Vorhabens war es, durch die Auswertung vorhandener und durchzuführender Untersuchungen eine Einstufung von Bodenmaterialien (jährlich fallen weit über 100 Mio. Tonnen davon an) für bestimmte Verwertungswege vornehmen zu können. Es sollte herausgefunden werden, ob Veränderungen hinsichtlich des Verwertungspotentials nachgewiesen werden können. Basis für die Durchführung und Bewertung waren die neuen Regelungen (hier insbesondere die Untersuchung mit einem Wasser/Feststoffverhältnis von 2:1, neue nationale und europäische Elutions- und Untersuchungsverfahren) der novellierten BBodSchV. Der Fokus lag dabei auf den polyzyklischen aromatischen Kohlenwasserstoffen (PAK) sowie ausgewählte anorganische Stoffe (Schwermetalle und Anionen) unter der Berücksichtigung unterschiedlicher Bodenmaterialien zur Verwertung. Dabei handelte es sich um: - Böden aus urban geprägten Gebieten, - Oberböden aus dem Straßenrandbereich in Form von Bankettschälgut, - Baggergut aus Gewässern mit Verdacht auf eine Kontamination, - Bergematerial (Mischung von Abraum- und Bodenmaterial), - Auenböden mit vermuteten Verunreinigungen aus Industrie und Gewerbe. Anhand der vorgelegten Ergebnisse kann nun eine Versachlichung der Diskussion um Ressorcenschutz vs. Schadlosigkeit der Verwertung erfolgen. Sie zeigen für die untersuchten Stoffe, dass bei einer Einführung der §§ 6-8 Novelle BBodSchV mit einer Erhöhung der Verwertungsquote für Bodenmaterial gerechnet werden kann. Eine Erhöhung des Deponievolumens ist somit nicht zu befürchten. Neben den ermittelten Daten konnten Grundlagen für die Überarbeitung verschiedener DIN-Normen für Bodenuntersuchungen erarbeitet werden. KW - Verwertung Bodenmaterial KW - Schadstofftransfer KW - Elutionsverfahren KW - BBodSchV KW - PAK PY - 2020 UR - https://www.umweltbundesamt.de/publikationen/monitoringprogramm-zur-verwertung-von-bodenmaterial SN - 1862-4804 VL - 127/2020 SP - 1 EP - 248 PB - Umweltbundesamt CY - Dessau AN - OPUS4-52039 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz T1 - Zur Prognose von Erschütterungen aus Bahntunneln N2 - Zur Erschütterungsausbreitung an oberirdischen Bahnlinien gibt es gute Übereinstimmungen zwischen Messungen und der Theorie geschichteter Böden. Bei der Interpretation der Ergebnisse spielt die Rayleigh-Welle eine große Rolle. Je nach Frequenz und Wellenlänge hat die Rayleigh-Welle eine bestimmte Eindringtiefe und erreicht damit mehr oder weniger steife Bodenschichten. Damit bekommt man eine frequenzabhängige Bodensteifigkeit für die Erschütterungsprognose. Für die Wellenausbreitung in der Tiefe statt an der Bodenoberfläche müssen eigene Gesetzmäßigkeiten gefunden werden. Es werden die Punktlastlösungen im Frequenz-Wellenzahlbereich und durch Integration über die Wellenzahlen berechnet. Man erhält die Wellenfelder, die Terzspektren für verschiedene Entfernungen und Frequenzen. Es wird die Tiefenlage und das Bodenmodell (homogen, geschichtet und kontinuierlich zunehmende Steifigkeit) variiert. Die Rayleigh-Welle verliert ihre Bedeutung und stattdessen kann die Vollraumlösung zur Interpretation und Prognose verwendet werden. Es werden die Halbraumlösung mit und ohne Rayleigh-Welle und die Vollraumlösung in der Tiefe diskutiert und verglichen. Neben der Wellenausbreitung (der Transmission) werden auch Effekte der Erschütterungsanregung (der Emission) und der Übertragung in Gebäude (der Immission) mit Hilfe der Finite-Element-Randelement-Methode berechnet. Die Verteilung der dynamischen Achslast durch die Tunnelsohle ergibt eine Minderung gegenüber der Punktlastanregung. Bei der Immission hat man keine Freifeldanregung wie an der Bodenoberfläche. Man muss entweder neben der Wellenamplitude (Verschiebung oder Schwinggeschwindigkeit) in der Tiefe auch die Spannung der ankommenden Welle berücksichtigen, oder man muss die Freifeldamplituden nach Bodenaushub berechnen. Die Rechenergebnisse deuten darauf hin, dass man als Freifeldanregung die zweifache Vollraumlösung ansetzen kann. T2 - Wiener Dynamik Tage 2021 CY - Vienna, Austria DA - 22.7.2021 KW - Erschütterungsausbreitung KW - Tunnel KW - Halbraum KW - Vollraum PY - 2021 SP - 1 EP - 11 PB - Steinhauser Consulting Engineers (STCE) CY - Wien AN - OPUS4-53253 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz ED - Carletti, E. ED - Crocker, M. ED - Pawelczyk, M. ED - Tuma, J. T1 - Dynamic measurements during drop tests on stiff foundations N2 - Measurements at the foundation, the surrounding soil and nearby buildings have been done during several drop tests of different containers on different foundations. The first measurements have been done on a big foundation where it should be guaranteed that the foundation is rigid and the container is tested properly. It was controlled that the foundation does not absorb more than 2 percent of the energy of the container. Most of the drop energy is lost in shock absorbers. Later on, a smaller drop test facility has been built on the ground but inside an existing building. It had to be controlled by prediction and measurements that the drop test will not damage the building. Tests from different heights on soft, medium, and stiff targets have been done to find out rules which allow to identify acceptable and unacceptable drop tests. Later on, the biggest drop test facility has been built for masses up to 200 t. It was necessary for the design of the foundation to estimate the forces which occur during the drop tests. On the other hand, the acceptable tests should be selected and controlled by measurements where the impact duration is important. Different sensors, accelerometers, accelerometers with mechanical filters, geophones (velocity transducers), strain gauges, and pressure cells have been applied for these tasks. The signals have been transformed to displacements which proved to be best suited for the interpretation of the impact mechanism. Modell calculations have been used to check and understand the dynamic measurements. The simplest law is the conservation of the momentum which is a good approximation if the impact is short. If the soil under the foundation has an influence on the deceleration of the container, the maximum foundation velocity is lower than the simple estimation. The amplitudes of the foundation could also be estimated from the ground vibrations and their amplitude-distance law. T2 - 27th International Congress on Sound and Vibration (ICSV27) CY - Online meeting DA - 11.07.2021 KW - Drop test KW - Vibration measurement KW - Container loading KW - Foundation load PY - 2021 SN - 978-83-7880-799-5 SN - 2329-3675 SP - 1 EP - 8 PB - Silesian University Press CY - Gliwice, Poland AN - OPUS4-53255 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bulling, Jannis A1 - Jurgelucks, B. A1 - Prager, Jens A1 - Walther, A. T1 - Ein inverses Verfahren zur Schadensrekonstruktion mittels geführter Wellen N2 - Eine zentrale Aufgabe der zerstörungsfreien Prüfung und der Strukturüberwachung (engl. Structural Health Monitoring - SHM) mit Ultraschallwellen ist die Bewertung von Schäden in Bauteilen. In vielen Bauteilen, wie zum Beispiel platten- und schalenförmigen Strukturen, Rohrleitungen oder Laminaten, breitet sich der Ultraschall in Form geführter Wellen aus. Zwar haben geführte Wellen eine relativ große Reichweite innerhalb des Bauteils und ermöglichen so eine großflächige Prüfung, ihre multimodalen und dispersiven Eigenschaften erschweren jedoch die Analyse der vom Schaden kommenden Reflexionen. Eine Möglichkeit, die Messsignale zu interpretieren und die Schäden zu charakterisieren, ist deren Vergleich mit der Wellenausbreitung in einem digitalen Modell. Hierbei stellt sich die Aufgabe, den Schaden im digitalen Modell anhand der Messdaten zu rekonstruieren. Diese Rekonstruktion beschreibt ein inverses Problem, das mehrere Vorwärtsrechnungen braucht, um das Schadensmodell an die Messdaten anzupassen. Durch die kleine Wellenlänge von Ultraschallwellen sind klassische Vorwärtsmethoden wie die Finte Elemente Methode rechenintensiv, weshalb die Autoren die semi-analytische Scaled Boundary Finite Element Method (SBFEM) benutzen, um den Rechenaufwand zu verringern. Im Beitrag wird ein inverses Verfahren basierend auf dem Automatischen Differenzieren in Kombination mit der SBFEM vorgestellt und an verschiedenen Schadenstypen in 2D-Querschnittmodellen von Wellenleitern getestet. In der präsentierten Vorstudie werden dafür „Messdaten“ aus unabhängigen Simulationen verwendet. T2 - DAGA 2021 - 47. Jahrestagung für Akustik CY - Vienna, Austria DA - 15.08.2021 KW - SBFEM KW - Inverse Probleme KW - SHM KW - NDT KW - AD PY - 2021 SP - 1 EP - 4 PB - Deutsche Gesellschaft für Akustik (DEGA) CY - Berlin AN - OPUS4-53305 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz T1 - Aspekte der Erschütterungsprognose bei Bahnlinien: Quasi-Statik und Achsfolge, unregelmäßiger Schotter und Boden, Wellenausbreitung bei Tunneln und Besonderheiten bei Bürogebäuden N2 - Erschütterungen, die durch Eisenbahnverkehr erzeugt werden, breiten sich durch den Erdboden aus und regen benachbarte Gebäude zu Schwingungen an. Es wurde ein Prognoseverfahren für Bahnerschütterungen ent-wickelt, das mit einfachen Modellen schnell Ergebnisse liefert. Dies sind physikalische Modelle, zum Beispiel 1-dimensionale Modelle mit Übertragungsmatrizen für die Fahrzeug-Fahrweg-Boden-Wechselwirkung und für die Gebäude-Boden Wechselwirkung. Damit werden die komplexen Verhältnisse bei der Emission (dem Zusammen¬wirken von Fahrzeug und Fahrweg), bei der Transmission durch den homogenen oder geschichteten Boden und bei der Immission in Gebäuden näherungsweise erfasst. In (Auersch, 2020) wird gezeigt, dass diese einfachen Prognosemodelle die Ergebnisse von detaillierten Modellen wie der Finite-Element-Randelement-Methode für das Gleis, die Wellenzahlintegrale für den Boden und 3-dimensionale Finite-Element-Modelle für das Gebäude gut wiedergeben können. Dies entspricht auch der Absicht, die Prognosemodelle aus den Ergebnissen der Detailmodelle abzuleiten. Die drei Prognoseteile werden getrennt berechnet, aber es werden physikalisch sinn¬volle Schnittstellen verwendet. Für die Emission und Transmission sind es die auf den Untergrund wirkenden Erregerkräfte von Fahrzeug und Fahrweg, für die Transmission und Immission sind es die Freifeldamplituden des Bodens. T2 - 17. D-A-CH Tagung Erdbebeningenieurwesen und Baudynamik CY - Online meeting DA - 16.09.2021 KW - Erschütterungen KW - Emission KW - Transmission KW - Immission PY - 2021 SP - 17 EP - 18 PB - ETH Zürich CY - Zürich AN - OPUS4-53313 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Wiesner, Anja A1 - Neumann, Patrick P. A1 - Krentel, Daniel A1 - Patzelt, Anne-Katrin T1 - Übersicht IFAFRI Capability Gaps N2 - Die zehn Capability Gaps der IFAFRI (International Forum to Advance First Responder Innovation) werden zusammengefasst und übersichtlich dargestellt. KW - BOS KW - KMU KW - IFAFRI KW - Security KW - Safety PY - 2021 SP - 1 EP - 10 CY - Berlin AN - OPUS4-53624 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Melzer, Michael A1 - Fischer, Michael A1 - Thomas, Marcus A1 - Subaric-Leitis, Andreas A1 - Bartholmai, Matthias T1 - Calibration Service as a Gateway to Sustainable Research and Development N2 - Over decades, the German Federal Institute for Materials Research and Testing (BAM) has established a sophisticated calibration laboratory for force, temperature and electrical quantities. Since more than 15 years it is accredited, currently by the national accreditation body (DAkkS), and offers its service also to external entities on a global scale. As a public provider, we are furthermore committed to research and development activities that demand measurements with highest quality and low level of uncertainties. Two R&D examples are highlighted within this contribution. T2 - SMSI 2020 CY - Meeting was canceled DA - 22.06.2020 KW - Calibration of force KW - Calibration of temperature KW - Calibration of electrical quantities KW - Measurement uncertainty KW - New sensor principles PY - 2020 SN - 978-3-9819376-2-6 DO - https://doi.org/10.5162/SMSI2020/E3.3 SP - 374 EP - 375 AN - OPUS4-51222 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - von Werder, Julia A1 - Fontana, P. A1 - Hoppe, Johannes A1 - Bilgin, S. A1 - Meng, Birgit ED - Serrat, C. ED - Casas, J. R. ED - Gibert, V. T1 - Composite Facade Elements with Self-Cleaning Surface made of Ultra-High-Performance Concrete (UHPC) N2 - In the framework of the European project H-House various concrete façade elements were developed with the aim to ensure a long service life by combining a very durable material with self-cleaning properties. The façade elements presented are made of a shell of UHPC filled with blocks of aerated autoclaved concrete as insulating material. Self-cleaning properties were realized amongst others by imprinting a microstructure into the surface during casting. The paper focuses on selected technological aspects of the manufacturing process of prototypes which had to be performed in two concreting sections. Furthermore the challenges faced when upscaling the self-cleaning properties are addressed and the strategy to assess the self-cleaning properties by measuring the contact and the roll-off angel is presented. The results show that a successfull upscalaing process requires detailed planning and that the best results can often be achieved with a moderate work effort or material use. T2 - XV International Conference on Durability of Building Materials and Components (DBMC 2020) CY - Online meeting DA - 20.10.2020 KW - Ultra-High-Performance Concrete KW - Facade Elements KW - Self-Cleaning Properties KW - Adhesive Pull-Strength KW - Microstructure KW - Architectural Concrete PY - 2020 SN - 978-84-121101-8-0 SP - 1289 EP - 1297 PB - International Center for Numerical Methods in Engineering (CIMNE) CY - Spain AN - OPUS4-51967 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Nisi, A. A1 - Koch, Claudia A1 - Mirtsch, Mona A1 - Blind, K. T1 - Effetti della pandemia COVID-19 sulle attività di valutazione della conformità svolte da organismi e laboratori accreditati in Italia N2 - Die Studie fasst Ergebnisse einer Befragung von Konformitätsbewertungsstellen in Italien zu deren Lage und den Aussichten während der Corona-Pandemie zusammen. Besondere Schwerpunkte wurden auf die wirtschaftlichen Auswirkungen und die Arbeitsfähigkeit, aber auch auf die Resilienz und die Wirkungen auf die Digitalisierung gelegt. N2 - Lo scoppio della pandemia da Covid-19 ha travolto Italia a inizio anno e i suoi effetti sull’economia sono stati particolarmente pesanti. Proprio per analizzare gli effetti della pandemia sul mercato della valutazione della conformità, lo scorso settembre Accredia, in collaborazione con l’Istituto Federale tedesco della Ricerca e del Collaudo dei Materiali (BAM), la Technische Universität di Berlino e l’Istituto Fraunhofer ISI, ha condotto un’indagine presso gli organismi e i laboratori accreditati in Italia. KW - Corona KW - Konformitätsbewertungsstellen KW - Resilienz KW - COVID-19 KW - Qualitätsinfrastruktur KW - Zertifizierung KW - Kalibrierung KW - Digitalisierung KW - Konformitätsbewertung KW - Laboratorium KW - Prüfung PY - 2020 UR - https://www.accredia.it/pubblicazione/corona-monitor-effetti-della-pandemia-da-covid-19-sulle-attivita-accreditate/ SP - 1 EP - 22 CY - Rom, Italien AN - OPUS4-51975 LA - ita AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schoonjans, Tom A1 - Brunetti, A. A1 - Golosio, B. A1 - Sanchez del Rio, M. A1 - Solé, V. A. A1 - Ferrero, C. A1 - Vincze, L. T1 - xraylib 3.1.0 N2 - Quantitative estimate of elemental composition by spectroscopic and imaging techniques using X-ray fluorescence requires the availability of accurate data of X-ray interaction with matter. Although a wide number of computer codes and data sets are reported in literature, none of them is presented in the form of freely available library functions which can be easily included in software applications for X-ray fluorescence. This work presents a compilation of data sets from different published works and an xraylib interface in the form of callable functions. Although the target applications are on X-ray fluorescence, cross sections of interactions like photoionization, coherent scattering and Compton scattering, as well as form factors and anomalous scattering functions, are also available. xraylib provides access to some of the most respected databases of physical data in the field of x-rays. The core of xraylib is a library, written in ANSI C, containing over 40 functions to be used to retrieve data from these databases. This C library can be directly linked with any program written in C, C++ or Objective-C. Furthermore, the xraylib package contains bindings to several popular programming languages: Fortran 2003, Perl, Python, Java, IDL, Lua, Ruby, PHP and .NET, as well as a command-line utility which can be used as a pocket-calculator. Although not officially supported, xraylib has been reported to be useable from within Matlab and LabView. The source code is known to compile and run on the following platforms: Linux, Mac OS X, Solaris, FreeBSD and Windows. Development occurs on Github: http://github.com/tschoonj/xraylib Downloads are hosted by the X-ray Micro-spectroscopy and Imaging research group of Ghent University: http://lvserver.ugent.be/xraylib Version 3.1.0 release notes: - Database of commonly used radionuclides for X-ray sources added (new API: GetRadioNuclideDataByName, GetRadioNuclideDataByIndex, GetRadioNuclideDataList and FreeRadioNuclideData) - numpy Python bindings added, generated with Cython. Performance basically the same as the core C library. (suggested by Matt Newville) - docstring support added to Python bindings (suggested by Matt Newville) - Windows SDKs now have support for Python 3.4. - Windows 64-bit SDK now comes with IDL bindings - Confirmed support for LabView (thanks to Dariush Hampai!) - Universal Intel 32/64 bit Framework built for Mac OS X - Perl support for Debian/Ubuntu - Several bugfixes: thanks to those that reported them! KW - Quantitative estimation KW - Elemental composition KW - Spectroscopic techniques KW - Imaging techniques PY - 2014 DO - https://doi.org/10.5281/zenodo.12378 PB - Zenodo CY - Geneva AN - OPUS4-51924 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schoonjans, Tom A1 - Vincze, L. A1 - Solé, V. A. A1 - Sanchez del Rio, M. A1 - Brondeel, P. A1 - Silversmit, G. A1 - Appel, K. A1 - Ferrero, C. T1 - XMI-MSIM 5.0 N2 - XMI-MSIM is an open source tool designed for predicting the spectral response of energy-dispersive X-ray fluorescence spectrometers using Monte-Carlo simulations. It comes with a fully functional graphical user interface in order to make it as user friendly as possible. Considerable effort has been taken to ensure easy installation on all major platforms. Development of this package was part of my PhD thesis. The algorithms were inspired by the work of my promotor Prof. Laszlo Vincze of Ghent University. Links to his and my own publications can be found in our manual. A manuscript has been published in Spectrochimica Acta Part B that covers the algorithms that power XMI-MSIM. Please include a reference to this publication in your own work if you decide to use XMI-MSIM for academic purposes. A second manuscript was published that covers our XMI-MSIM based quantification plug-in for PyMca. Soon information on using this plug-in will be added to the manual. XMI-MSIM is released under the terms of the GPLv3. Development occurs at Github: http://github.com/tschoonj/xmimsim Downloads are hosted by the X-ray Micro-spectroscopy and Imaging research group of Ghent University: http://lvserver.ugent.be/xmi-msim Version 5.0 release notes: Changes: 1. Custom detector response function: build a own plug-in containing your own detector response function and load it at run-time to override the builtin routines. Instructions can be found in the manual. 2. Escape peak improvements: new algorithm is used to calculate the escape peak ratios based on a combined brute-force and variance-reduction approach. Ensures high accuracy even at high incoming photon energies and thin detector crystals. Downside: it's slower… 3. Removed maximum convolution energy option. Was a bit confusing anyway. 4. Number of channels: moved from simulation controls into input-file 5. Radionuclide support added: Now you can select one or more commonly used radionuclide sources from the X-ray sources widget. 6. Advanced Compton scattering simulation: a new alternative implementation of the Compton scattering has been implemented based on the work of Fernandez and Scot (http://dx.doi.org/10.1016/j.nimb.2007.04.203), which takes into account unpopulated atomic orbitals. Provides an improved simulation of the Compton profile, as well as fluorescence contributions due to Compton effect (extremely low!), but slows the code down considerably. Advanced users only. Default: OFF 7. Plot spectra before convolution in results 8. Windows: new Inno Setup installers. Contains the headers and import libraries 9. Windows: compilers changed to GCC 4.8.1 (TDM-GCC) 10. Windows: rand_s used to generate seeds on 64-bit version (requires Vista or later) 11. Windows: new gtk runtime for the 64-bit version (see also https://github.com/tschoonj/GTK-for-Windows-Runtime-Environment-Installer) 12. Mac OS X: compilers changed to clang 5.1 (Xcode) and gfortran 4.9.1 (MacPorts) 13. Original input-files from our 2012 publication (http://dx.doi.org/10.1016/j.sab.2012.03.011) added to examples 14. Updater performs checksum verification after download 15. X-ray sources last used values stored in preferences.ini 16. xmimsimdata.h5 modified: even bigger now... Bugfixes: 1. Windows: support for usernames with unicode characters. Fixed using customized builds of HDF5. Thanks to Takashi Omori of Techno-X for the report! 2. Spectrum import from file fixes. Was never properly tested apparently Note: For those that compiled XMI-MSIM from source: you will need to regenerate the xmimsimdata.h5 file with xmimsim-db. Old versions of this file will not work with XMI-MSIM 5.0. KW - Spectral response KW - Energy-dispersive X-ray fluorescence spectrometers KW - Monte-Carlo simulations PY - 2014 DO - https://doi.org/10.5281/zenodo.12381 PB - Zenodo CY - Geneva AN - OPUS4-51925 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bulling, Jannis A1 - Franosch, Georg A1 - Lugovtsova, Yevgeniya A1 - Prager, Jens ED - Rizzo, P. ED - Milazzo, A. T1 - Sensitivity of Ultrasonic Guided Waves to Elastic Constants: A Numerical Study N2 - The dispersive properties of Lamb waves can be utilised for material characterisation because the frequency-wavenumber-relationship, as well as the group velocity, depend on material parameters. These dependencies make a non-destructive estimation of an elastic constant possible. This preliminary study investigates the sensitivity of dispersion curves caused by a change in elastic constants. The Scaled Boundary Finite Element Method is used to compute special dispersion curves, which show the sensitivity value of the frequency and group velocity as a colour value. This representation allows for easy identification of patterns and local effects. Two sets of dispersion curves are presented, one set for a steel plate and the other set for a plate made of a carbon fibre reinforced polymer. In general, we notice that the sensitivity often increases with the frequency and that higher-order modes seem to be more suitable for material characterisation. Moreover, specific modes respond to material changes while others are relatively unaffected, which must be taken into consideration for material characterisation. T2 - European Workshop on Structural Health Monitoring (EWSHM 2020) CY - Online meeting DA - 06.07.2020 KW - Scaled Boundary Finite Element Method KW - Lamb waves KW - Dispersion curves KW - Carbon fibre reinforced polymer KW - Transverse isotropy PY - 2021 SN - 978-3-030-64593-9 DO - https://doi.org/10.1007/978-3-030-64594-6_73 VL - 127 SP - 759 EP - 768 PB - Springer CY - Cham AN - OPUS4-51986 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Küttenbaum, Stefan T1 - Zur Validierung von zerstörungsfreien Messverfahren für die probabilistische Beurteilung von Bestandsbauwerken mit gemessenen Daten T1 - Validation of non-destructive measurement procedures for reliability assessments of existing structures using measured data N2 - The aging of existing bridge structures coincides with the progressing degradation and increasing requirements on the bridge stock caused by increasing traffic densities as well as heavy traffic. The resulting demand for structural assessments of existing bridges is of substantial importance, both nationally and internationally. The information available about the considered system provides the basis for reassessments. Both the structural reliability and the validity of the computation results depend primarily on the condition, i.e. the quality and the relevance of this information. The purposeful measurement of quality-evaluated and relevant information can significantly increase the engineer’s power of judgement regarding the structural reliability. It is advisable to keep the destructive structural interventions necessary to obtain such information to a minimum. The purpose of the present thesis is the development and evaluation of a methodology for the probabilistic reassessment of existing structures using non-destructively measured data and for the validation of the suitability of non-destructive measurement procedures for the application in the context of reassessments. For this purpose, the applicability of the rules established within the Guide to the Expression of Uncertainty (GUM)-framework for evaluating the quality of the measured information to be used later in the reassessment is emphasized. The requirements on measured data-based basic variables are derived from the First Order Reliability Method (FORM), a probabilistic approximation procedure. Based on this, the metrology and the reassessment are brought together. The measurement-based basic variables are explicitly appreciated as random variables in reliability analyses. The developed methodology is evaluated by means of two prestressed concrete bridges and four basic variables. Geometrical measurement results gathered by radar and ultrasound measurements are incorporated into reassessments regarding the limit states ULS bending, ULS shear and SLS decompression. The modelling of the measurements is an essential part in order to calculate the measurement results, each consisting of a measured value and the attributed measurement uncertainty. It is shown that the incorporation of the non-destructively collected measurement results reduces the uncertainty to be covered and increases the level of approximation of the considered models. The measurement results are reliable and comparable. Extensive sensitivity analyses provide information about crucial structure parameters to be measured, since they significantly influence the structural reliability. This way, the relevance of the information is derived. Such analyses are suitable for the design and commissioning of investigations meeting the demands as well as for the purposeful refinement of initially insufficient computation models. Furthermore, the appreciation of measured data-based basic variables can increase the robustness of structural analyses. Measurement-based reliability reassessments are particularly useful if required information is missing or doubts have arisen about the available information. In the best case, the incorporation of non-destructively measured data results in the extension of estimated remaining service lives, in the enhancement of infrastructural availabilities and in the optimization of the consumption of resources. N2 - Die Alterung bestehender Brückenbauwerke fällt mit dem sich verschlechternden Zustand und zunehmenden Anforderungen an die Bausubstanz zusammen, die eine Folge von steigenden Verkehrszahlen und der Zulassung des Schwerlastverkehrs sind. Der daraus erwachsende Bedarf an Beurteilungen von bestehenden Brücken ist national und international fortwährend groß. Die Grundlage für Nachrechnungen sind die über das System verfügbaren Informationen. Sowohl die rechnerische Zuverlässigkeit eines Tragwerks als auch die Validität der Ergebnisse hängen im Wesentlichen vom Zustand, also von der Qualität und der Relevanz dieser Informationen ab. Die gezielte Messung von gütebewerteten, relevanten Informationen kann die Urteilsfähigkeit des Beurteilenden über die Zuverlässigkeit eines Tragwerks signifikant steigern. Wünschenswert ist die Erhebung derartiger Informationen ohne signifikante Eingriffe in die Bausubstanz. Das Ziel der vorliegenden Arbeit ist die Entwicklung und Erprobung einer Vorgehensweise für die probabilistische Beurteilung von bestehenden Bauwerken mit zerstörungsfrei gemessenen Daten und einer Methodik zum objektiven Nachweis der Eignung von zerstörungsfreien Messverfahren zur Anwendung im Zuge einer Nachrechnung. Herausgestellt wird die Eignung der im Guide to the Expression of Uncertainty in Measurement (GUM) publizierten Regeln zur Bewertung der Qualität der gemessenen Informationen, die später im statischen Nachweis verwendet werden sollen. Die Anforderungen an die Basisvariablen, d. h. an die Eingangsgrößen im probabilistischen Nachweis, werden aus den Vorschriften zur Zuverlässigkeitsanalyse mit dem probabilistischen Näherungsverfahren FORM, der First Order Reliability Method, abgeleitet. Darauf basiert die Entwicklung der Schnittstelle zwischen der Messtechnik und der Nachrechnung. Im Kern werden die messdatenbasierten Basisvariablen explizit als Zufallsgrößen bei der Zuverlässigkeitsanalyse berücksichtigt. Die entwickelte Vorgehensweise wird am Beispiel von zwei Spannbetonbrücken und vier Basisvariablen erprobt. In die Nachweise der Biege- und der Querkrafttragfähigkeit sowie in einen Nachweis der Dekompression fließen geometrische Messergebnisse ein, die mithilfe von Radar- und Ultraschallmessungen generiert werden. Ein wichtiger Bestandteil ist die Bildung von Modellen zur Auswertung der Messungen und zur Berechnung der Messergebnisse. Es wird gezeigt, dass die Einbeziehung der zerstörungsfrei generierten Messergebnisse die Unsicherheit in den Berechnungsmodellen reduzieren und den Grad der Annäherung der Modelle an die Realität steigern kann. Die Messergebnisse sind zuverlässig und vergleichbar. Umfassende Sensitivitätsanalysen geben Aufschluss über sinnvollerweise zu messende Bauwerksparameter, die einen maßgeblichen Einfluss auf die Tragwerkszuverlässigkeit ausüben. Auf diese Weise wird die Relevanz der Informationen ermittelt. Das Potential derartiger Analysen für die gezielte Planung und Beauftragung von Messungen sowie für die bedarfsgerechte Zuschärfung von initial unzureichenden Berechnungsmodellen erscheint groß. Die messdatenbasierten Modelle können darüber hinaus die Robustheit einer Tragwerksanalyse steigern. Die Berücksichtigung von Messergebnissen ist dann besonders nützlich, wenn zur Beurteilung erforderliche Informationen fehlen oder Zweifel an den verfügbaren Informationen aufgekommen sind. Im besten Fall resultiert daraus die Verlängerung von rechnerischen Restnutzungsdauern, die Steigerung der Verfügbarkeit der Infrastruktur, die Optimierung des Ressourcenverbrauchs und insgesamt eine realitätsnahe Bauwerksbewertung. KW - Zerstörungsfreie Prüfung im Bauwesen KW - Nachrechnung KW - Spannbetonbrücken KW - Zuverlässigkeitsanalyse KW - Messunsicherheit PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:bvb:706-7686 SN - 1431-5122 VL - 21/2 SP - I EP - 314 PB - Universität der Bundeswehr München CY - Neubiberg AN - OPUS4-53851 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - von der Au, Marcus A1 - Meermann, Björn T1 - Dem Leben auf der Spur – Einzelzellanalytik N2 - Zellen, als Grundeinheit für Organismen, bilden einen wesentlichen Eckpfeiler für das Leben. Die Untersuchung von einzelnen Zellen liefert wertvolle Einblicke in fundamentale Prozesse des Lebens. So können Anomalien auf der Zelleebene Indikatoren für Krankheiten sein und durch eine Analyse früh erkannt werden. Weiterhin kann durch ein tiefgreifendes Verständnis von Vorgängen in Zellen auch gezielt Forschung zu z.B. neuen Medikamenten betrieben werden. Damit können die Wirksamkeit erhöht und die Nebenwirkungen reduziert werden. KW - SC-ICP-MS KW - Algen KW - Cispaltin PY - 2021 UR - https://faszinationchemie.de/wissen-und-fakten/news/dem-leben-auf-der-spur-einzelzellanalytik/ SP - 1 EP - 4 AN - OPUS4-53859 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Asbach, C. A1 - Held, A. A1 - Kiendler-Scharr, A. A1 - Scheuch, G. A1 - Schmid, H.-J. A1 - Schmitt, S. A1 - Schumacher, S. A1 - Wehner, B. A1 - Weingartner, E. A1 - Weinzierl, B. A1 - Bresch, Harald A1 - Seeger, Stefan A1 - u.a., T1 - Positionspapier der Gesellschaft für Aerosolforschung zum Verständnis der Rolle von Aerosolpartikeln beim SARS-CoV-2 Infektionsgeschehen N2 - Dass Viren sich über Aerosolpartikel ausbreiten können, wurde bereits in vielen Studien gezeigt. Als Aerosol bezeichnet man ein Gemisch aus Luft mit darin verteilten festen oder flüssigen Partikeln. Ein Aerosol ist dabei immer dynamisch, da Partikel neugebildet, in oder mit der Luft transportiert und aus der Luft entfernt werden oder sich im luftgetragenen Zustand verändern. Zum Verständnis der Rolle von Aerosolpartikeln als Übertragungsweg von SARS-CoV-2 ist daher die Kenntnis der verschiedenen Prozesse in einem Aerosol von besonderer Bedeutung. Mit diesem Papier möchte die GAeF einen Beitrag dazu leisten, den momentan so häufig anzutreffenden Begriff „Aerosol“ sowie die relevanten Aerosolprozesse anschaulich darzustellen und zu erläutern. Dabei wird im Rahmen dieses Papiers nur auf die wesentlichen Grundlagen eingegangen. Für ein tiefergehendes Verständnis der teilweise komplexen Prozesse sei auf die angeführte Sekundärliteratur verwiesen. Das Papier fasst eine Vielzahl von Studien zur Entstehung von virenbeladenen Aerosolpartikeln sowie deren Ausbreitung zusammen. Darauf basierend kann festgestellt werden, dass ausgeatmete Aerosolpartikel auch bei der Corona-Pandemie eine prominente Rolle bei der Verbreitung der Viren spielen. Abschließend geht dieses Papier auf mögliche Maßnahmen zur Verringerung der Ausbreitung von Aerosolpartikeln ein. Die diskutierten Maßnahmen orientieren sich an der derzeitigen öffentlichen Diskussion und beinhalten entsprechend die folgenden Punkte: Lüften, Luftreiniger, Lüftungsanlagen und Masken. Es werden Hinweise zum richtigen und sinnvollen Einsatz dieser Maßnahmen gegeben. Aerosolpartikel haben Größen zwischen ca. 0,001 und mehreren 100 Mikrometern (und nicht wie in vielen Publikationen derzeit definiert < 5μm) und verteilen sich mit Luftströmungen relativ schnell, auch über größere Distanzen. Größere Aerosolpartikel sinken – abhängig von ihrer Größe und Dichte – zu Boden; kleine Aerosolpartikel können hingegen sehr lange in der Luft verbleiben (s. Kapitel 3). Jeder Mensch stößt durch die Atmung sowie beim Sprechen, Husten und Niesen flüssige Aerosolpartikel unterschiedlicher Größen aus (s. Kapitel 4). Ist eine Person mit einem Virus, wie z. B. SARS-CoV-2, infiziert, so können diese Aerosolpartikel Viren enthalten, die in die Luft gelangen und von anderen Personen eingeatmet werden können. SARS-CoV-2 hat eine Größe von 0,06 bis 0,14 Mikrometer, die exhalierten flüssigen Aerosolpartikel sind hingegen größer. Die flüssigen Aerosolpartikel können aber je nach Umgebungsbedingungen durch Verdunstung schrumpfen (s. Kapitel 3.3). Für den Partikeltransport und die Partikelabscheidung ist dabei jeweils die aktuelle Partikelgröße relevant. Das höchste Infektionsrisiko besteht in geschlossenen Innenräumen, da sich hierin Aerosolpartikel anreichern können. Insbesondere hier sind entsprechend Maßnahmen zu treffen, die eine Reduktion der Aerosolpartikelkonzentration ermöglichen. Vor dem Hintergrund der Aerosolwissenschaften ordnet die GAeF die aktuellen Maßnahmen zur Eindämmung der Pandemie wie folgt ein: • Prinzipiell gilt: Keine Maßnahme kann für sich alleine funktionieren! Das Zusammenspiel der verschiedensten Maßnahmen ist nach derzeitigem Wissensstand der beste Weg zur Minimierung des Infektionsrisikos. • Abstand halten ist wichtig, denn mit zunehmendem Abstand werden direkt ausgeatmete Viren verdünnt, und die Wahrscheinlichkeit sich anzustecken sinkt. Der vielfach vorgeschriebene Mindestabstand kann als Anhaltspunkt dienen, sollte aber insbesondere bei längeren Zusammenkünften und auch in Innenräumen mit verringerter Luftbewegung vergrößert und durch weitere Maßnahmen (s.u.) ergänzt werden. • Masken helfen, einen Teil der exhalierten Partikel (und Viren) zu filtern. Dadurch sinkt die Konzentration der exhalierten Partikel (und Viren) in einem Raum und damit das Infektionsrisiko. Hierbei ist zu beachten, dass die ausgeatmeten Aerosolpartikel durch anhaftende Feuchtigkeit relativ groß sind und somit auch von einfachen Masken effizient zurückgehalten werden können. Da diese Partikel aber mit längerer Verweilzeit in der Raumluft schrumpfen, sind einfache Mund-Nasen-Bedeckungen für den Selbstschutz weniger effizient. Hierfür sind Atemschutzmasken erforderlich, die auch für feine Partikel eine hohe Abscheidung zeigen, z. B. der Klassen FFP2, N95 oder KN95. Diese sind sowohl für den Selbst- als auch den Fremdschutz effizient, sofern sie über kein Ausatemventil verfügen. Masken mit Ausatemventil dienen hingegen nur dem Selbstschutz und widersprechen daher dem Solidaritätskonzept, dass Mitmenschen durch kollektives Maskentragen geschützt werden. • Gesichtsvisiere, die ohne zusätzliche Verwendung von Masken eingesetzt werden, sind hinsichtlich Aerosolpartikeln weitgehend nutzlos, da die Luft mit Partikeln (und Viren) ungefiltert um die Visiere herumströmt. Gesichtsvisiere werden im klinischen Alltag zusätzlich zu Masken getragen, um Tröpfcheninfektion über die Schleimhäute der Augen zu verhindern. Ebenfalls weitgehend unwirksam gegen die Aerosolverbreitung in Innenräumen sind mobile oder fest installierte Plexiglasbarrieren. Diese können nur kurzfristig die kleinräumige Ausbreitung eines Aerosols, z. B. im Kassenbereich eines Supermarkts, verhindern, bieten aber längerfristig keinen Schutz. Gesichtsvisiere und Plexiglasscheiben dienen im Wesentlichen als Spuck- und Spritzschutz gegenüber großen Tröpfchen. • Im Freien finden so gut wie keine Infektionen durch Aerosolpartikel statt. Allerdings können Tröpfcheninfektionen auftreten, insbesondere in Menschenansammlungen, wenn Mindestabstände nicht eingehalten und/oder keine Masken getragen werden. In geschlossenen Räumen ist Lüften unerlässlich, um die ausgeatmete Luft in einem Raum durch frische Luft von draußen zu ersetzen. Häufiges Stoß- und Querlüften sind dabei vergleichbar effektiv wie dauernd das Fenster vollständig geöffnet zu lassen. Aus energetischer Sicht ist Stoß- oder Querlüften insbesondere im Winter allerdings effizienter. CO2-Monitore können bei der Überwachung der Luftqualität in Innenräumen helfen. Sie zeigen an, wann gelüftet werden sollte und wann die Luft in einem Raum während des Lüftens ausreichend gewechselt ist. Sie können jedoch nur als Indikator verwendet werden und verhindern selbst bei Einhaltung der vorgeschlagenen CO2-Grenzkonzentrationen keine direkte Infektion durch unmittelbar benachbarte Personen. • Luftreiniger können einen sinnvollen Beitrag leisten, um die Partikel- und Virenkonzentration in einem Raum zu reduzieren. Bei der Beschaffung von Luftreinigern muss darauf geachtet werden, dass diese für den betrachteten Raum und die betrachtete Anwendung ausreichend dimensioniert sind, um die Partikel- und Virenlast signifikant zu verringern. Dem Luftdurchsatz des Gerätes kommt dabei eine größere Bedeutung zu, als der reinen Effizienz des Filters. Aus energetischen und Kostenerwägungen kann die Verwendung hocheffizienter Filter sogar kontraproduktiv sein. Fest verbaute Lüftungsanlagen können ebenso sinnvoll sein, sofern sie die Luft filtern, um die Partikel- und Virenlast in einem Raum zu verringern. Hierbei ist es zur Vermeidung von Infektionen sinnvoll, diese möglichst mit 100 % Frischluft zu betreiben. Aus Sicht der Gesellschaft für Aerosolforschung besteht erheblicher Forschungsbedarf insbesondere an den interdisziplinären Grenzen zu Forschungsfeldern der Epidemiologie, Infektiologie, Virologie, Lüftungstechnik und Strömungsmechanik. Die Durchführung gezielter Studien sollte kurzfristig mit speziellen Förder- und Forschungsprogrammen ermöglicht werden. Dieses Papier wurde von Mitgliedern der Gesellschaft für Aerosolforschung verfasst und wird von einer Vielzahl internationaler Aerosolexperten unterstützt (s. Kapitel 8). Neben der vorliegenden Version existiert auch eine englischsprachige Übersetzung (siehe www.info.gaef.de). Sämtliche Abbildungen in diesem Papier stehen unter folgendem Link zum kostenlosen Download bereit: https://www.info.gaef.de/positionspapier. Bei jeder Verwendung ist „Gesellschaft für Aerosolforschung e. V.“ als Quelle zu nennen. KW - Covid KW - Corona KW - GAeF KW - Aerosole KW - Aerosolforschung PY - 2021 UR - https://www.info.gaef.de/_files/ugd/fab12b_a5f114a183cf4f27ab8ac713e8a5b8ef.pdf SP - 1 EP - 48 PB - Gesellschaft für Aerosolforschung CY - Köln AN - OPUS4-53954 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Asbach, C. A1 - Held, A. A1 - Kiendler-Scharr, A. A1 - Scheuch, G. A1 - Schmid, H.-J. A1 - Schmitt, S. A1 - Schumacher, S. A1 - Wehner, B. A1 - Weingartner, E. A1 - Weinzierl, B. A1 - Bresch, Harald A1 - Seeger, Stefan A1 - u.a., T1 - Position paper of the Gesellschaft für Aerosolforschung on understanding the role of aerosol particles in SARS-CoV-2 infection N2 - Many studies have already shown that viruses can spread via aerosol particles. An aerosol is a mixture of air with solid or liquid particles dispersed in it. To understand the role of aerosol particles as a transmission path of SARS-CoV-2, knowledge of the different processes in an Aerosol is therefore of particular importance. With this paper, GAeF would like to contribute to a better understanding of the term “aerosol” and the relevant aerosol processes. In the context of this paper only the essential basics will be discussed. For a deeper understanding of the partly complex processes, please refer to the literature mentioned at the end of the paper. The paper summarises a large number of studies on the formation of virus-laden aerosol particles and their spread. Based on this, it can be concluded that exhaled aerosol particles may play a prominent role in the spread of viruses in the corona pandemic. Finally, this paper discusses possible measures to reduce the spread of aerosol particles. The measures discussed are based on the current public debate including ventilation, air purifiers, HVAC systems and masks. Advice is given on the correct and sensible use of these measures. An aerosol is always dynamic, as particles are newly formed, transported in or with the air, removed from the air or change in the airborne state. Aerosol particles have sizes between approx. 0.001 and several 100 micrometres (and not < 5 μm as currently defined in many publications) and spread relatively quickly with air currents, even over longer distances. Larger aerosol particles sink to the ground, depending on their size and density, while small aerosol particles can remain in the air for a very long time (see Section 3). Every person emits liquid aerosol particles of various sizes through breathing and when speaking, coughing and sneezing (see Section 4). If a person is infected with a virus, such as SARS-CoV-2, these aerosol particles can contain viruses that can be released into the air and inhaled by other people. SARS-CoV-2 has a size of 0.06 to 0.14 micrometres, but the exhaled liquid aerosol particles are larger. The liquid aerosol particles can shrink by evaporation, depending on the ambient conditions (see Section 3.3). Particle size is relevant for particle transport and particle separation. The highest risk of infection exists in closed indoor spaces, as aerosol particles can accumulate there. Here in particular, appropriate measures must be taken to reduce the concentration of aerosol particles (see Section 5). Against the background of aerosol science, the GAeF classifies the current measures to contain the pandemic as follows: • In principle, no measure can work on its own! According to the current state of knowledge, the interaction of the most varied measures is the best way to minimise the risk of infection. • Keeping distance is important, because with increasing distance, directly exhaled viruses are diluted and the probability of infection decreases. The often prescribed minimum distance can be used as a guide, but it should be increased and supplemented by other measures (see below), especially for longer meetings and also indoors with reduced air movement. • Masks help to filter some of the exhaled particles (and viruses). This reduces the concentration of exhaled particles (and viruses) in a room and thus the risk of infection. It should be noted here that the exhaled aerosol particles are relatively large due to adhering moisture and can therefore also be efficiently retained by simple masks. However, since these particles shrink with longer dwell time in the room air, simple mouth-nose masks are less efficient for self-protection. Respiratory masks are required for this purpose, which show a high degree of separation even for fine particles, e.g. of classes FFP2, N95 or KN95. These are efficient for both self-protection and protection of others unless they have an exhalation valve. Masks with an exhalation valve, on the other hand, are only for self-protection and therefore contradict the solidarity concept that fellow human beings are protected by collective mask wearing. Face shields which are used without additional masks are largely useless with regard t• aerosol particles, as the air with particles (and viruses) flows unfiltered around the shields. In everyday clinical practice, facial shields are worn in addition to masks to prevent droplet infection via the mucous membranes of the eyes. Mobile or permanently installed Plexiglas barriers are also largely ineffective against the spread of aerosols indoors. These can only prevent the smallscale spread of an aerosol in the short term, e.g. in the checkout area of a supermarket, but offer no protection in the longer term. Face shields and Plexiglas panels essentially serve as spit and splash protection against large droplets. • Outdoors, there are practically no infections caused by aerosol transmission. However, droplet infections can still occur, especially in crowds, if minimum distances are not observed and/or masks are not worn. In closed rooms, ventilation is essential to replace the exhaled air in a room with fresh air from outside. Frequent airing and cross-ventilation is just as effective as leaving the window open all the time. From an energy point of view, however, it is more efficient to ventilate the room, especially in winter. CO2 monitors can help to monitor indoor air quality. They indicate when it is necessary to ventilate and when the air in a room has been sufficiently changed during ventilation. However, they can only be used as an indicator and even if the proposed CO2 limit concentrations are met, they do not prevent direct infection by people in the immediate vicinity. • Air purifiers can make a useful contribution to reducing the concentration of particles and viruses in a room. When procuring air purifiers, care must be taken to ensure that they are adequately dimensioned for the room and application in question in order to significantly reduce the particle and virus load. The air throughput of the unit is more important than the pure efficiency of the filter. For energy and cost reasons, the use of highly efficient filters can even be counterproductive. Permanently installed ventilation systems can also be useful, provided they filter the air to reduce the particle and virus load in a room. To avoid infections, it is advisable to operate them with 100 % fresh air if possible. From the point of view of the Gesellschaft für Aerosolforschung, there is a considerable need for research, especially at the interdisciplinary borders to research fields of epidemiology, infectiology, virology, ventilation technology and fluid mechanics. The implementation of targeted studies should be made possible at short notice with special funding and research programmes. This paper was written originally in German by members of the Gesellschaft für Aerosolforschung and is supported by a large number of international aerosol experts. Both the English and German version as well as all images in the paper are available for free download at the following link: https://www.info.gaef.de/positionspapier. The “Gesellschaft für Aerosolforschung e. V.” must be named as the source, whenever an image is used. KW - COVID KW - SARS KW - GAeF KW - Aerosol KW - Corona PY - 2021 UR - https://www.info.gaef.de/_files/ugd/fab12b_d8d88393f90240cdbea63c88c09887ef.pdf DO - https://doi.org/10.5281/zenodo.4350494 SP - 1 EP - 48 PB - Association for Aerosol Research CY - Köln AN - OPUS4-53955 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - von Törne, Jannik Wipert A1 - Piechotta, Christian A1 - Karnstedt, L. T1 - Einblicke in das Transformationsverhalten von Warfarin N2 - Warfarin ist seit den 1950er Jahren einer der bekanntesten Gerinnungshemmer. Beim Menschen wird es bis heute zur Vorbeugung von Thrombose und der Behandlung von Vorhofflimmern und Arrhythmie eingesetzt. Doch schon einige Jahre vor der FDA Zulassung (U. S. Food and Drug Administration) als Medikament wurde es zur Bekämpfung von Nagetieren eingesetzt. Bis heute wurde es nur teilweise durch weitaus wirksamere antikoagulante Rodentizide (ARs) der zweiten Generation, sogenannte Superwarfarine, ersetzt. In der Fachliteratur finden sich zahlreiche Beispiele für sekundäre und tertiäre Vergiftung mit ARs bei Wildtieren und anderen Nichtzieltieren. Bisher ist relativ wenig über die Bioakkumulation, Persistenz und Toxizität von ARs und deren Transformationsprodukten (TPs) in der terrestrischen und aquatischen Umwelt, sowie der Nahrungskette bekannt. Um Einblicke in mögliche Transformations- und Abbauprozesse von Warfarin unter umweltrelevanten Bedingungen zu erhalten und um diese Einflüsse zu simulieren, wurde hierzu eine elektrochemische Reaktorzelle in Kopplung mit einem Massenspektrometer verwendet. So können mögliche Phase-I-Metabolite und sogenannte „oxidation products“ vorausgesagt werden. Hinsichtlich des Verhaltens während der Wasseraufbereitung in Kläranlagen wurden technisch relevante Prozesse wie Chlorung, UV-Bestrahlung und Ozonung in Modellen simuliert, um hier potenzielle Abbauwege und -prozesse aufzuklären. Gebildete Transformationsprodukte wurden daher mittels unterschiedlicher chromatografischer Verfahren getrennt und massenspektrometrisch identifiziert, charakterisiert und verglichen. T2 - 49. Jahrestagung der GUS 2020 CY - Stutensee, Blankenloch DA - 24.03.2021 KW - Warfarin KW - Transformationsprodukte KW - Umweltverhalten PY - 2021 SN - 978-3-9818507-6-5 VL - 49 SP - 265 EP - 272 AN - OPUS4-53963 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heßmann, Jennifer A1 - Hilgenberg, Kai T1 - Prozesssimulation elektromagnetischer Kräfte zum Fügen artungleicher Werkstoffe N2 - Prozesssimulation zur Eingrenzung der elektromagnetischen Kräfte zum gezielten Verdrängen einer laserstrahlinduzierten Schmelze zum Fügen artungleicher Materialien. Berechnung der Lorentzkraftverteilung im Schmelzbad. Abschätzung der Temperaturentwicklung beim Verdrängungsprozess. T2 - Assistentenseminar der WGF 2020 CY - Online meeting DA - 01.09.2020 KW - Stahl und Aluminium KW - Artungleiche Werkstoffe KW - Elektromagnetische Schmelzbadbeeinflussung KW - Fügetechnologie KW - Laserstrahlschweißen PY - 2020 SN - 978-3-96144-141-9 VL - 370 SP - 51 EP - 60 PB - DVS Media GmbH AN - OPUS4-53927 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Patrick P. A1 - Hirschberger, Paul A1 - Bartholmai, Matthias T1 - Flying Ant Robot – Aerial Chemical Trail Detection and Localization N2 - This paper presents first advances in the area of aerial chemical trail following. For that purpose, we equipped a palm-size aerial robot, based on the Crazyflie 2.0 quadrocopter, with a small lightweight metal oxide gas sensor for measuring evaporated ethanol from chemical trails. To detect and localize the chemical trail, a novel detection criterion was developed that uses only relative changes in the transient phase of the sensor response, making it more robust in its application. We tested our setup in first crossing-trail experiments showing that our flying ant robot is able to correlate an odor hit with the chemical trail within 0.14 m. Principally, this could enable aerial chemical trail following in the future. T2 - IEEE Sensors 2021 CY - Online meeting DA - 31.10.2021 KW - Nano aerial robot KW - Trail following KW - Trail detection KW - Localization PY - 2021 DO - https://doi.org/10.1109/sensors47087.2021.9639857 SP - 1 EP - 4 PB - IEEE AN - OPUS4-53933 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völzke, Holger A1 - Wolff, Dietmar A1 - Orellana Pérez, Teresa A1 - Herold, Christian A1 - Bollingerfehr, W. A1 - Wunderlich, A. A1 - Prignitz, S. T1 - Anforderungen an Behälter für die Endlagerung hochradioaktiver Abfälle in Steinsalz, Tonstein und Kristallingestein N2 - Bei der Auswahl eines Standortes für ein Endlager für hochradioaktive Abfälle (Wärme entwickelnde radioaktive Abfälle und ausgediente Brennelemente) in Deutschland werden auf Grundlage des Standortauswahlgesetzes von 2017 die drei potenziellen Wirtsgesteine Steinsalz, Tonstein und Kristallingestein in Betracht gezogen. Die Auswahl eines konkreten Endlagerstandortes steht dabei in engem Zusammenhang mit den für die jeweiligen Wirtsgesteine geeignet erscheinender Endlagersystemen. Zentraler Bestandteil dieser Endlagersysteme sind die Endlagerbehälter, deren Gestaltung und Auslegung maßgeblich die Randbedingungen für die Transport- und Einlagerungstechnik vorgibt und zudem die Nachweise zur Betriebs- und Langzeitsicherheit entscheidend prägt. Daher ist es für die Behälterentwicklung erforderlich, die an Endlagerbehälter zu stellenden Anforderungen systematisch herzuleiten. Auf dieser Grundlage können anforderungsgerechte Endlagerbehälter zielgerichtet für die jeweils zu untersuchenden Endlagerstandorte in unterschiedlichen Wirtsgesteinen entwickelt werden. Dieser Beitrag fasst die wesentlichen Ergebnisse des von BAM und BGE TECHNOLOGY GmbH im Zeitraum 2017 bis 2020 bearbeiteten und vom Bundesministerium für Wirtschaft und Energie (BMWi) geförderten Forschungsvorhabens KoBrA zusammen, die in einem Abschlussbericht und vier zugehörigen Teilberichten umfassend dokumentiert sind. T2 - Tage der Standortauswahl CY - Freiberg, Germany DA - 11.02.2021 KW - Endlager KW - Behälter KW - Sicherheitsanforderungen KW - hochradioaktive Abfälle PY - 2021 SP - 1 EP - 10 AN - OPUS4-53114 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Herold, Christian A1 - Völzke, Holger A1 - Wolff, Dietmar A1 - Orellana Pérez, Teresa A1 - Bollingerfehr, W. A1 - Wunderlich, A. A1 - Prignitz, S. T1 - Herleitung und Zusammenstellung der Anforderungen an Endlagerbehälter für ein HAW-Endlager in den drei potenziellen Wirtsgesteinen Steinsalz, Tonstein und Kristallingestein; Bericht zum Arbeitspaket 3 des FuE Verbundvorhabens KoBrA N2 - Der Bericht zum Arbeitspaket 3 baut auf den Ergebnissen der internationalen Recherche (AP1) sowie der Zusammenstellung der Randbedingungen und Beanspruchungsgrößen für die Endlagerbehälter (AP2) auf. Die Anforderungen an die Behälter – regulatorische, betriebliche sowie solche aus der Standortgeologie und den Einwirkungen und Prozessen, denen die Behälter ausgesetzt sind – werden hergeleitet und systematisch dargestellt. Die für das Endlagersystem zu betrachtenden Nutzungsphasen werden aus den regulatorischen Anforderungen hergeleitet und charakterisiert. Die Einwirkungen auf die Behälter in den drei potenziellen Wirtsgesteinen sowie die sich für die Erfüllung der Sicherheitsfunktionen des Behälters als Teil des Endlagersystems ergebenden Behälterfunktionen werden ebenfalls wirtsgesteins- und zeitphasenabhängig betrachtet. Schließlich werden aus den Einwirkungen auf die Behälter und den Anforderungen an die Behälterfunktionen auch quantifizierbare Behälterfunktionen für alle drei potenziellen Wirtsgesteine abgeleitet. KW - Endlager KW - Behälter KW - Sicherheitsanforderungen KW - Hochradioaktive Abfälle PY - 2020 UR - https://www.bge-technology.de/fileadmin/user_upload/MEDIATHEK/f_e_berichte/KoBrA/2020-KoBrA_Bericht_AP3.pdf N1 - Auftraggeber: Bundesministerium für Wirtschaft und Energie (BMWi), Förderkennzeichen: 02E11527 und 02E11537. SP - 1 EP - 254 PB - BGE Technology CY - Peine AN - OPUS4-53119 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fürst, Richard A1 - Mózer, V. A1 - Pokorný, M. A1 - Vlach, T. T1 - Nosné konstrukce z textilního betonu za zvýšené teploty T1 - Loadbearing structures made from textile reinforced concrete at elevated temperatures N2 - The work aims to assess the textile reinforced concrete at elevated temperatures and applications of additional fire protection as well. T2 - Fire Protection Conference CY - Ostrava, Czechia DA - 01.09.2021 KW - High Performance Concrete KW - Textile reinforcement KW - Fire test PY - 2021 SN - 978-80-7385-247-4 SP - 10 EP - 12 PB - Sdružení požárního a bezpečnostního inženýrství CY - Ostrava AN - OPUS4-53509 LA - ces AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Held, Mathias A1 - Rashwan, Abdalla A1 - Bulling, Jannis A1 - Lugovtsova, Yevgeniya A1 - Lauschkin, Maik A1 - Prager, Jens T1 - Inverse Bestimmung elastischer Materialparameter aus dem Ausbreitungsverhalten geführter Ultraschallwellen mittels eines Convolutional Neuronal Networks N2 - Detailliertes Wissen über die mechanischen Eigenschaften verwendeter Materialien ist Grundvoraussetzung für viele ingenieurtechnische Aufgaben und Dienstleistungen. Zur Bestimmung der elastischen Materialparameter gibt es verschiedene klassische, zerstörende Prüfverfahren. Eine Möglichkeit der zerstörungsfreien Bestimmung liegt in der Auswertung von Messergebnissen, die auf Basis des Ausbreitungsverhaltens geführter Ultraschallwellen gewonnen wurden. Das Ausbreitungsverhalten geführter Ultraschallwellen kann mittels Dispersionsabbildungen dargestellt werden. Um aus messtechnisch ermittelten Dispersionsabbildungen Rückschlüsse auf die Materialparameter zu ziehen, werden in der aktuellen Forschung verschiedene inverse Methoden diskutiert. Maschinelles Lernen und insbesondere Convolutional Neural Networks (CNNs) stellen eine Möglichkeit der automatisierten inversen Modellierung und Evaluierung von Bilddaten dar. In diesem Beitrag wird gezeigt, wie das Ausbreitungsverhalten von geführten Ultraschallwellen unter Verwendung von CNNs genutzt werden kann, um die isotropen elastischen Konstanten einer plattenförmigen Struktur zu bestimmen. Hierfür werden die verwendeten Daten analysiert, das Preprocessing erläutert und eine grundlegende CNN-Architektur gewählt. Zur Auswertung des generierten Modells werden verschiedene Verfahren wie Gradienten-Mapping und die Visualisierung der verschiedenen Schichten vorgestellt. Die Anwendbarkeit der Methode wird anhand synthetischer Daten demonstriert. T2 - DAGA 2021 CY - Vienna, Austria DA - 15.08.2021 KW - Geführte Ultraschallwellen KW - Inverse Probleme KW - Materialcharakterisierung KW - Maschinelles Lernen KW - Dispersion KW - Lamb Wellen PY - 2021 SN - 978-3-939296-18-8 VL - 47 SP - 659 EP - 662 AN - OPUS4-53492 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zeipert, H. A1 - Johannesmann, S. A1 - Nicolai, Marcel A1 - Lugovtsova, Yevgeniya A1 - Prager, Jens A1 - Henning, B. T1 - Quantifying the coupling strength of adhesively bonded materials by investigating mode repulsion regions N2 - In the field of non-destructive testing, Lamb waves are often used for material characterisation. The increasing computational capabilities further enable complex and detailed simulations to predict the material behaviour in reality. Since adhesive bonding of different materials is a widely used method in modern applications, a reliable measurement system to determine the quality of these adhesive bonds is needed. Investigations of the dispersive behaviour of acoustic waves in adhesively bonded multi-layered waveguides show mode repulsions in the dispersion diagrams in regions where the modes of the single materials would otherwise intersect. In previous works, changes of the distance between those modes with respect to the bonding quality are observed. The experimental data for this investigation is generated using pulsed laser radiation to excite broadband acoustic waves in plate like specimens which are detected by a piezoelectric ultrasonic transducer. Numerical data is generated using simulations via a semi-analytical finite element method. Using a combination of experimental and numerical data, the present work introduces an approach to determine a parameter which indicates the bonding quality in relation to an ideal material coupling. T2 - DAGA 2021 CY - Vienna, Austria DA - 15.08.2021 KW - Ultrasonic guided waves KW - Multi-layered structures KW - Laser excited ultrasonic waves PY - 2021 SP - 1532 EP - 1535 AN - OPUS4-53581 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Maiwald, Michael T1 - OPC-UA für Prozessindustrie und Laborwelt - Offener Standard für die störungsfreie Kommuniktaion N2 - Im privaten Umfeld machen wir uns keine Gedanken mehr über die Einbindung von elektronischen Geräten in Netzwerke, sei es bei der Verbindung des Mobiltelephons mit dem W-Lan-Netzwerk des Hotels oder von Freunden oder des drahtlosen Kopfhörers mit dem Notebook: Wir erwarten, dass es auf Anhieb funktioniert. Dahinter stecken offene Standards für die Konnektivität. Dafür braucht man immer zwei Dinge: Einen physischen Kommunikationskanal, auf dem die Datenpakete zwischen den Komponenten und Geräten hin- und herwandern und eine einheitliche Kommunikationssprache, so dass sich die Komponenten und Geräte auch untereinander verstehen, weil sie dieselbe Sprache sprechen und automatisch wissen, was sie miteinander zu besprechen haben. Wenn man eine sichere Konnektivität bevorzugt, werden weitere Informationen benötigt, wie etwa ein Passwort. Auch für die störungsfreie Kommunikation aller Automatisierungskomponenten der Prozessindustrie untereinander oder etwa für die Kommunikation von Geräten in einem analytischen Labor wird ein einheitliches Protokoll (Kommunikationssprache) und ein einheitlicher Feldbus (Kommunikationskanal) benötigt. Mittlerweile gilt der Standard OPC Unified Architecture (OPC-UA) für das Erstere als gesetzt und kann als ein kleiner Triumph von Industrie 4.0 betrachtet werden. OPC-UA kann auf verschiedenen Kommunikationskanälen laufen – am liebsten solchen, die eine angemessene Bandbreite oder Datenrate haben. Was den dazu notwendigen physischen Kommunikationskanal betrifft, findet man aus verschiedenen Gründen einen sehr spezialisierten und historisch über Jahrzehnte gewachsenen Lebensraum vor, der Operational Technology (OT) genannt wird. Zumeist findet man Zwei- und Vierdraht-Techniken mit Strom- und Spannungs-Signalübertragung, zum Beispiel mit 4–20 mA. Kommunikationsstandards wie eingangs erwähnt, wie Ethernet oder W-Lan sind absolut die Seltenheit. Dieses wird für die sogenannte Informationstechnik (Information Technology, IT) eingesetzt und ist aus Sicherheitsgründen heute komplett von der OT getrennt. Auch wenn es der OT nicht gefällt, wachsen die beiden Welten IT und OT aber stetig weiter zusammen, da die IT bereits viele funktionierende und preislich attraktive Lösungen bereithält. Die vermeintliche Sicherheit, Verfügbarkeit und Echtzeitfähigkeit der klassischen OT, aber auch ihre Komplexität müssen im Zuge der Digitalen Transformation nun sorgfältig abgewogen werden. KW - Prozessindustrie KW - Laborkommunikation KW - Konnektivität KW - OPC-UA KW - Digital Transformation KW - Labor-IT PY - 2021 UR - https://analyticalscience.wiley.com/do/10.1002/was.00170277/full/blaetterkatalog_git1021.pdf SN - 0016-3538 VL - 65 IS - 10 SP - 1 EP - 4 PB - Wiley CY - Weinheim AN - OPUS4-53566 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Legall, Herbert A1 - Bonse, Jörn A1 - Krüger, Jörg T1 - Emission of X-rays during ultrashort pulse laser processing N2 - Ultrashort pulse laser materials processing can be accompanied by the production of X-rays. Small doses per laser pulse can accumulate to significant dose rates at high laser pulse repetition rates which may exceed the permitted X-ray limits for human exposure. Consequently, a proper radiation shielding must be considered in laser machining. A brief overview of the current state of the art in the field of undesired generation of X-ray radiation during ultrashort pulse laser material processing in air is presented. T2 - Lasers in Manufacturing Conference 2021 CY - Online meeting DA - 21.06.2021 KW - Ultra-short pulse laser processing KW - Laser-induced X-ray emission KW - Radiation protection PY - 2021 SP - 1 EP - 5 AN - OPUS4-53866 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Aßmann, Norman A1 - Bühling, Benjamin T1 - Impact-echo dataset "Radarplatte" N2 - This dataset contains raw data resulting from Impact-Echo measurements at the reference conrete block "Radarplatte", located at BAM (German Federal Institute for Materials Research and Testing). This specimen has been described in detail by Niederleithinger et al. (2021), who applied muon tomography, ultrasonic echo measurements, radar and X-ray laminography to visualize its internal structure. The Impact-Echo method is based on the excitation of the zero-group-velocity frequency of the first symmetric Lamb mode of a plate-like structure, in order to assess its thickness. Numerous publication elaborate on Impact-Echo theory, examples are (Gibson and Popovics 2005, Schubert and Köhler 2008 , Abraham and Popovics 2010). The measurements have been conducted using a setup that contains only commercially available components. The setup consists of an Olson CTG-2 concrete thickness gauge (Olsen Instruments, USA) for actuation and sensing and an 8-bit NI USB-5132 digital storage oscilloscope (National Instruments, USA) combined with the Echolyst software (Schweizerischer Verein für technische Inspektionen (SVTI), Switzerland) for data acquisition. Measurements were conducted using a grid of 23x23 points with a spacing of 50 mm. At each point 8192 samples were recorded at a sampling rate of 1 MS/s. The dataset contains the (X,Y) location in mm of the individual measurement points as well as the raw measurement data at those points. The data is provided in the formats *.mir/*.mhdr (Echolyst), *.npy (Python) and *.mat (Matlab) and *.csv to ease the import in various post-processing tools. KW - Nondestructive testing KW - Impact-echo KW - S1-ZGV mode KW - Concrete PY - 2021 DO - https://doi.org/10.7910/DVN/UNOH2U PB - Harvard College CY - Cambridge, MA, USA AN - OPUS4-53886 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz T1 - Prediction of building noise and vibration – 3D finite element and 1D wave propagation models N2 - Construction work or traffic excite nearby buildings, and the perceptible or audible vibration can be a nuisance for the inhabitants. The transfer of the vibration from the free field to the building has been calculated by the finite element method for many models in consultancy and research work. The analysis for all storeys of certain building points such as walls, columns and floors unveiled some rules, some typical modes, and some wavetype responses. A simplified building-soil model has been created, which includes well these effects of building-soil resonance, wall/column resonance, floor resonances, and the high-frequency reduction. The model consists of one wall for a wall-type apartment building or a column for each specific part (mid, side or corner) of a column-type office building. The building response in the high-frequency (acoustic) region is calculated as mean values over all storeys and over wider frequency bands, by wave-type asymptotes of an infinitely tall building, and by the soil to wall ratio of impedances. The secondary noise is predicted by Transfer values between the building vibration (center of floors, walls at a room corner) and the sound pressure. T2 - Euronoise 2021 CY - Online meeting DA - 25.10.2021 KW - Building vibration KW - Finite element models KW - Soil-wall-floor model KW - Apartment building KW - Office tower PY - 2021 SN - 978-989-53387-0-2 SP - 1792 EP - 1801 AN - OPUS4-53702 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Holm, Olaf T1 - ATR Aufschluss, Trennung und Rückgewinnung von ressourcenrelevanten Metallen aus Rückständen thermischer Prozesse mit innovativen Verfahren N2 - Ziel des Vorhabens war die Steigerung der Rückgewinnung von Metallen aus Aschen und Schlacken durch Aufschluss aus den mineralischen Verbunden. Durch das innovative Prallzerkleinerungsverfahren (Hochgeschwindigkeits-Rotations-Beschleuniger) des Projektpartners TARTECH, sollten die Verunreinigungen an den metallischen Anteilen praktisch vollständig abgeschlagen werden. Diese Aufbereitungstechnik sollte im Rahmen des Projektes so verfeinert und angepasst werden, dass metallische Partikel von 0,5 bis 5 mm aufgeschlossen werden, damit sie anschließend über Wirbelstromscheider in elementarer Form abgetrennt werden können. KW - Rostasche KW - Prallzerkleinerungsverfahren KW - Aufbereitungstechnik PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-521571 UR - https://edocs.tib.eu/files/e01fb21/1748479865.pdf DO - https://doi.org/10.2314/KXP:1748479865 SP - 1 EP - 516 AN - OPUS4-52157 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Holm, Olaf A1 - Simon, Franz-Georg T1 - Aufschluss, Trennung und Rückgewinnung von ressourcenrelevanten Metallen aus Rückständen thermischer Prozesse mit innovativen Verfahren Teilprojekt A: Projektkoordination und physikalische-chemische Verfahren N2 - Die Bundesanstalt für Materialforschung und –prüfung (BAM) mit ihrem Fachbereich 4.3 Schadstofftransfer und Umwelttechnologien hat für das Verbundvorhaben „ATR - Aufschluss, Trennung und Rückgewinnung von ressourcenrelevanten Metallen aus Rückständen thermischer Prozesse mit innovativen Verfahren“ die Gesamtkoordination übernommen. Bei insgesamt neun Projektpartnern fiel folgerichtig ein nicht unwesentlicher Aufwand für Verwaltungsaufgaben an. Insbesondere die Verzögerungen bei dem Bau der großtechnischen Anlagen im Teilprojekt B (ausführlich erläutert im Bericht für das Gesamtvorhaben) resultierten in einer Vielzahl von Folgeaufgaben. Wissenschaftlich verfahrenstechnisches Ziel des Teilprojektes A bei der BAM war die Rückgewinnung von Metallen und metallischer Verbindungen aus speziellen, bereits teilaufbereiteten Fraktionen von Aschen aus der Hausmüllverbrennung (HMVA). Ausgangsmaterial sollten Fraktionen sein, die im Rahmen des Projektes vom Projektpartner TARTECH eco industries AG bereitgestellt werden sollten. Eigens und im Rahmen des Projektes entwickelte Hochgeschwindigkeits-Rotations- Beschleuniger sollten die mineralischen Oberflächenverkrustungen abschlagen, die einzelnen Bestandteile trennen und so eine effizientere Sortierung mit Anschlussverfahren ermöglichen. Die Verfahren, die bei der BAM dafür zum Einsatz kamen, waren im Wesentlichen Flotation und Dichtesortierung mittels eines Zentrifugalsortierers. Der Fokus der Untersuchungen lag dabei auf der Rückgewinnung bzw. Anreicherung von Kupfer und Kupferverbindungen. KW - Rostasche KW - Flotation KW - Dichtesortierung KW - Zentrifugalsortierer PY - 2021 UR - https://edocs.tib.eu/files/e01fb21/1748479865.pdf SP - 68 EP - 122 AN - OPUS4-52158 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Perk, M. A1 - Großwig, S. A1 - Pfeiffer, T. A1 - Rembe, M. A1 - den Hartogh, M. A1 - Weege, S. A1 - Krebber, Katerina A1 - Dijk, H. L. T1 - Faseroptische Leckage-Ortung zum Nachweis von Undichtheiten in Bohrlochkomplettierungen N2 - Im Rahmen der Integritätsbewertung einer zementierten 13 3/8" Rohrtour einer Sole-Produktionsbohrung wurden erstmals 2018 zeitgleich faseroptische Temperaturmessungen (DTS, Distributed Temperature Sensing) und faseroptische Akustikmessungen (DAS, Distributed Acoustic Sensing) durchgeführt und ausgewertet. Dazu wurde die Bohrung zeitweise mit Stickstoff bespannt und wieder entlastet. Durch die Bespannung der Bohrung mit Stickstoff in Kombination mit dem Herunterdrücken des Stickstoff-Sole-Spiegels unter den Rohrschuh der 13 3/8" Rohrtour, konnte Stickstoff aus der Kavernenbohrung durch eine Leckagestelle in die Zementation übertreten und dort ein Stickstoff-Reservoir bilden. Bei der anschließenden Stickstoffentlastung erfolgte der Wiederanstieg des Stickstoff-Sole-Spiegels deutlich schneller als die Entleerung des in der Zementation angelegten Stickstoff-Reservoirs. Der dadurch entstandene Druckgradient hatte zur Folge, dass an der Leckagestelle der Stickstoff aus der Zementation in die aufsteigende Sole in Form von Bläschen eingetreten und dort aufgestiegen ist. Dieser Übertritt der Stickstoffbläschen war sowohl mit der Entstehung eines akustischen Geräusches als auch mit einer Temperaturänderung verbunden, welche mit der DAS- und DTS-Technik nachgewiesen werden konnten. Um die Ergebnisse bzgl. ihres physikalischen Hintergrundes zu überprüfen und basierend auf einer mathematisch-physikalischen Grundlage eine nachvollziehbare Interpretation der Messergebnisse zu ermöglichen, wurde ein numerisches Simulationsmodell der gekoppelten Festkörper- und Druckakustik für die Bohrung aufgebaut. Das Modell berücksichtigt die Geologie und die Komplettierung der Kavernenbohrung. Nach Identifikation der Schallquelle konnte mit dem Modell die Ausbreitung des Schalldrucks in der Bohrung erfolgreich nachgestellt werden. Um dieses Verfahren einer simultanen DAS-DTS-Messung in eine feldtaugliche Version zu überführen, läuft seit November 2019 ein breit angelegtes und vom BMWi gefördertes ZIM-Kooperationsprojekt zwischen der Bundesanstalt für Materialforschung und -prüfung (BAM), der IAB Weimar gGmbH, der GESO GmbH & Co. Projekt KG, der DEEP.KBB GmbH sowie der Rembe Consulting PartG mbB. Durch die Messdatenkopplung und den Wegfall der bewegungsbedingten Nachteile einer Messsonde werden präzisere Ergebnisse zur Bewertung der Bohrlochintegrität erwartet. Das Ziel ist, mit Hilfe der noch zu entwickelnden einfachen und robusten Technik, quantitative Aussagen über die Zustände im verrohrten Bohrloch direkt am Messplatz treffen zu können, wobei ein Fokus auf Detektierung und Quantifizierung von Kleinstleckagen liegt. Im Rahmen dieses Forschungsprojektes kommt neben numerischen Berechnungen auch ein geplanter Bohrlochsimulator zum Einsatz, mit dem umfangreiche Untersuchungen zur Ermittlung der Grenzparameter und Detektionsschwellen durchgeführt werden sollen. T2 - DGMK/ÖGEW-Frühjahrstagung 2020 CY - Celle, Germany DA - 15.​04.​2020 KW - Kavernenspeicher KW - Verteilte faseroptische akustische Sensorik KW - Wasserstoffspeicher PY - 2020 UR - https://dgmk.egnyte.com/fl/k3KJMqKMSb#folder-link/ SN - 978-3-947716-04-3 SN - 1433-9013 N1 - Die DGMK/ÖGEW Frühjahrstagung 2020 wurde abgesagt, der Tagungsband aber trotzdem veröffentlicht. - The DGMK/ÖGEW Frühjahrstagung 2020 was cancelled, the proceedings were published nevertheless. VL - DGMK-Tagungsbericht 2020-1 SP - 106 EP - 121 PB - DGMK - Deutsche Wissenschaftliche Gesellschaft für Erdöl, Erdgas und Kohle CY - Hamburg AN - OPUS4-52159 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ahmadi, Samim A1 - Lecompagnon, Julien A1 - Hirsch, Philipp Daniel A1 - Burgholzer, Peter A1 - Jung, Peter A1 - Caire, Giuseppe A1 - Ziegler, Mathias T1 - Laser excited super resolution thermal imaging for nondestructive testing N2 - The work to be presented focuses on our most recent studies to laser excited super resolution (SR) thermography. The goal of nondestructive testing with SR is to facilitate the separation of closely spaced defects. Photothermal SR can be realized by performing structured illumination measurements in com-bination with the use of deconvolution algorithms in post-processing. We explain that stepwise as well as continuous scanning techniques are applicable to generate structured illumination measurements. Finally, we discuss the effect of experimental parameters and image processing techniques to find the optimal SR technique which leads to the highest reconstruction quality within laser thermography. T2 - Sensor and Measurement Science International Conference SMSI 2021 CY - Online meeting DA - 03.05.2021 KW - Super resolution KW - Laser thermography KW - Nondestructive testing KW - Laser scanning KW - Photothermal imaging PY - 2021 SP - 181 EP - 182 AN - OPUS4-52780 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schlick-Hasper, Eva A1 - Bruchno, Martin A1 - Goedecke, Thomas T1 - Release of Powdery or Granular Substances from Intact Dangerous Goods Bags During Road Transport - Analysis of the Causes and Development of a Test Concept N2 - Abstract: The leaks of dangerous goods from actually intact bags detected in the years 2018 to 2020 tend to be at an almost constant high level. These releases of powdery or granular dangerous goods represent violations of the sift-proofness required in the dangerous goods regulations. This article first analyzes the causes. The components of the bags that are affected by leaks are micro-perforations, joins and closures, in particular internal sleeve valves. A distinction must be made between bags closed in conformity with or contrary to the manufacturer's instructions. The particle release is determined by a number of influencing factors of the filling substance, the packaging and other boundary conditions. Therefore, a comprehensive test concept is developed in this work, which takes all these factors into account. The application of this test concept facilitates the planning of the test setup and the experiments. On this basis, the complex mechanisms involved in the release of solid substances can be systematically investigated in the test laboratory. To prevent releases of powdery or granular substances from intact bags, it is necessary that the user has access to the closing instructions and the relevant properties of the test substance used for the design type approval. Further experimental investigations are needed to assess whether filling substances change their properties during transport and whether this enables them to escape. T2 - IAPRI Member Conference 2021 CY - Online meeting DA - 15.06.2021 KW - Bags KW - Dangerous goods packagings KW - Sift-proofness KW - Particles KW - Leak PY - 2021 UR - https://whova.io/email/click/d11d7d6cf1c84dfdc8c12349468fe91c/c9af5bcf002312cff80d9b962d1014e4/ SN - 978-1-63821-160-0 SP - 390 EP - 405 PB - IAPRI CY - East Lansing, Michigan, USA AN - OPUS4-52786 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Beck, Uwe A1 - Ermilova, Elena A1 - Schneider, S. A1 - Peters, S. T1 - Gemeinsamer Abschlussbericht WIPANO-Vorhaben „Standardisierung und Normung der Ellipsometrie als universeller Spektroskopie“ N2 - Im Vorhaben SNELLIUS wurden in enger Zusammenarbeit der BAM mit den Firmen Accurion und SENTECH Instruments aufbauend auf der Norm DIN 50989-1 „Ellipsometrie - Teil 1: Grundlagen; Ellipsometry – Part 1: Principles“ insgesamt fünf Normenentwürfe erarbeitet, die fünf Modell-basierten Anwendungsfällen der Ellipsometrie entsprechen. Unter Berücksichtigung des neuartigen Modell-basierten Normungskonzepts wurde in den Normenentwürfen erstmals eine GUM- und DIN EN ISO/IEC 17025:2018 konforme Bestimmung bzw. Abschätzung der Messunsicherheit umgesetzt. Dies erforderte neben der textlichen Erstellung auch umfangreiche experimentelle Arbeiten bei den Firmen, Vergleichsversuche und komplementäre Modell- und Datenevaluierungen, da sowohl die verwendete ellipsometrische Hardware (unterschiedliche ellipsometrische Funktionsprinzipien) als auch die ellipsometrische Software (Modell-Randbedingungen, Fitalgorithmus) firmenspezifisch zum Teil sehr unterschiedlich sind. Hierbei mussten in einem Konsensprozess Lösungen gefunden werden, die die beiden deutschen Ellipsometer-Anbieter Accurion (Imaging-Ellipsometrie) und SENTECH Instruments (Mapping Ellipsometrie) gleichermaßen akzeptieren konnten und die zudem einen Transfer auf die Internationale Ebene (ISO Norm) ermöglichen, also vom Grundsatz her auch auf weitere Ellipsometerhersteller wie (J. A. Woollam Co., USA; SEMILAB, Ungarn; HORIBA, Japan) mit wieder anderen ellipsometrischen Funktionsprinzipien, Hard- und Softwarelösungen anwendbar sind. Die weitgehende Unabhängigkeit von ellipsometrischen Funktionsprinzipien, Hard- und Softwarelösungen wurde dadurch erreicht, dass normativ festgelegt wurde, dass die ellipsometrischen Größen PSI und DELTA im Sinne von DIN ENISO/IEC 17025 als Rohdaten fungieren. KW - Ellipsometrie-Norm KW - Messunsicherheit ellipsometrischer Messungen KW - Validierungskonzepte ellipsometrischer Messungen KW - DIN 50989, Teile 1 bis 6 KW - DIN EN ISO/IEC 17025:2018 und GUM Kompatibilität PY - 2021 SP - 1 EP - 16 AN - OPUS4-52857 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Beck, Uwe A1 - Hielscher-Hofinger, Stefan A1 - Lerche, D. A1 - Reetz, U. T1 - Vorhaben ZENSUS, BAM Vh-Nr. 6768 „Zentrifugentechnologie zur statistischen Untersuchung von Stumpfklebungen“ N2 - Das Vorhaben ZENSUS beschäftigt sich mit der Erstellung eines Normenentwurfs bzw. einer normen-konformen Technischen Spezifikation für die Zentrifugen-basierte Prüfung der Klebfestigkeit von Stumpfklebungen. Das umfasst auch umfangreiche Validierungsversuche, um mögliche Unterschiede zwischen Kraft-gesteuerter (Zentrifuge) und Weg-gesteuerter (Zugprüfmaschine) bzw. ggf. dazu korrelierte Materialabhängigkeiten mit ihren Auswirkungen auf SOPs zu identifizieren. Die Zentri-fugen-basierte Mehr-Proben-Prüfung von bis zu 8 Klebverbunden wird im Weiteren mit CAT-Technologie („Centrifugal Adhesion Testing“) abgekürzt. KW - Klebfestigkeit von Stumpfklebungen KW - EN 15870 KW - Centrifugal Adhesion Testing (CAT) Technologie KW - Zugprüfung mittels Zugprüfmaschine KW - Zugprüfung mittels Zentrifugentechnologie PY - 2021 SP - 1 EP - 28 AN - OPUS4-52858 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wosniok, Aleksander A1 - Jansen, R. A1 - Cheng, L. A1 - Chruscicki, Sebastian T1 - Ortsaufgelöste Zustandsüberwachung von Brückenbauwerken mittels faseroptischer Sensoren N2 - In der vorliegenden Studie wurde der Einfluss der statischen Verkehrsbelastung auf die geringen Durchbiegungseffekte in der Betonkonstruktion einer bestehenden Brücke mittels ortsauflösender faseroptischer Sensoren untersucht. Dabei tragen die Ergebnisse der an der Amsterdamer Brücke 705 durchgeführten Belastungstests wesentlich zum Verständnis des Strukturverhaltens bei. Das Konzept der statischen Belastung basierte auf dem Einsatz von zwei 36-Tonnen-Lastwagen, die an mehreren vorbestimmten Stellen auf der Brücke anhielten. Die auf diese Weise aufgebrachte Last führte zu ortsabhängigen kleinen Durchbiegungseffekten, die als lokale Längsdehnung der an der Unterseite der Brücke integrierten Sensorfaser aufgezeichnet wurden. Die reflektometrischen Messungen beruhten auf dem Prinzip genannt TW-COTDR (Tunable Wavelength Coherent Optical Time Domain Reflectometry). Die Messgenauigkeit lag im Bereich von 0,5 µm/m. T2 - DGZfP-Jahrestagung 2021 CY - Online meeting DA - 10.05.2021 KW - Frequenzbereichsreflektometrie KW - Ortsaufgelöste Fasersensorik KW - Rayleigh-Streuung PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-526752 UR - https://jahrestagung.dgzfp.de/Programm#P73 SP - 1 EP - 8 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-52675 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rabe, Torsten A1 - Eichler, J. A1 - Picht, G. A1 - Rossner, W. A1 - Stelter, M. A1 - Voigt, I. T1 - Digitalisierung der keramischen Fertigung - Herausforderungen und Chancen N2 - Dieses Strategiepapier zielt darauf ab, Akteuren und Entscheidungsträgern den Status der Digitalisierung in der keramischen Fertigung, erfolgreiche Best-Practice-Beispiele aber auch die Herausforderungen nahezubringen, die es nun anzugehen gilt. Es ist die Vision, die Keramikfertigung durchgehend zu digitalisieren und alle Schritte des Produktkreislaufs lückenlos über die gesamte Wertschöpfungs- und Nutzungskette zu vernetzen: also eine Keramikindustrie 4.0 zu etablieren. Das Strategiepapier erfasst zunächst die Spezifität der keramischen Fertigung und nimmt eine Analyse des gegenwärtigen Standes der Digitalisierung in der keramischen Industrie vor, auch anhand einiger ausgewählter Beispiele aus der industriellen Praxis. Auf Basis der wesentlichen Bausteine für eine Fertigungsdigitalisierung werden schließlich die Chancen für Keramikproduzenten sowie der erforderliche Forschungs- und Entwicklungsbedarf aufgezeigt. KW - Datenmanagement KW - Digitalisierung KW - Fertigungsprozess KW - Keramik KW - Sensorik PY - 2021 SP - 1 EP - 39 PB - Deutsche Gesellschaft für Materialkunde (DGM) und Deutsche Keramische Gesellschaft (DKG) CY - Köln ET - 1000 AN - OPUS4-52708 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reuter, T. A1 - Plotzki, David A1 - Borges de Oliveira, F. A1 - Hausotte, T. T1 - Simulative Untersuchung des Einflusses von Bildrauschen auf dimensionelle Messungen mit industriellen Computertomografen N2 - Die industrielle Röntgen-Computertomografie (CT) etabliert sich für die Anwendung in der dimensionellen Messtechnik. Sie bietet als zerstörungsfreies Messverfahren das Potential, sowohl innen- als auch außenliegende Merkmale holistisch zu erfassen. Für die Bestimmung der Güte eines Messwerts muss die dem Messwert zugeordnete Messunsicherheit ermittelt werden. Dabei kann, nach derzeitigem Stand der Technik und Normung, die aufgabenspezifische Messunsicherheit nach VDI/VDE 2630 Blatt 2.1 nur unter hohem Aufwand mit einer Vielzahl an experimentellen Wiederholmessungen ermittelt werden. Ziel diverser Forschungs-projekte zu diesem Thema ist es daher, eine numerische Messunsicherheitsbestimmung zu erreichen. Dafür ist es notwendig, alle signifikanten Einflussgrößen zu erfassen, deren Unsicherheitsbeiträge zu bestimmen und zu bewerten. In diesem Beitrag wird der Einfluss des Bildrauschens auf verschiedene dimensionelle Messgrößen simulativ untersucht. Mithilfe eines prismatischen Prüfkörpers, der eine Vielzahl an Geometrieelementen aufweist, werden verschiedene Messgrößen unterschiedlicher Komplexität betrachtet. Ziel ist es, für diese Messgrößen zu testen, wie diese auf das Bildrauschen reagieren. Dieses wird dabei durch das Signal-Rausch-Verhältnis (SNR) der Projektionsgrauwerte beschrieben und variiert. Es werden Wiederholsimulationen durchgeführt, damit eine statistische Aussage über die Verteilung der Messwerte möglich ist und der Einfluss des Rauschens auf verschiedene Messgrößen individuell beurteilt werden kann. Das Simulationsszenario wird so gestaltet, dass lediglich das Bildrauschen Einfluss auf die Messung hat. Die berechneten Verteilungsbreiten lassen mit sinkendem SNR eine deutliche Zunahme erkennen, insbesondere bei der Bestimmung von Formabweichungen. Simuliert wird mit der Software aRTist 2.10 (BAM). T2 - DGZfP-Jahrestagung 2021 CY - Online meeting DA - 10.05.2021 KW - Rauschen KW - Computertomografie KW - Dimensionelle Messung KW - Simulation PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-527144 SP - 1 EP - 11 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung e.V. (DGZfP) CY - Berlin AN - OPUS4-52714 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ecke, Alexander A1 - Bohm, Konrad A1 - Schneider, Rudolf T1 - Magnetpartikelbasierte Immunoassays als vielseitiges Werkzeug für die Umweltanalytik N2 - Der Bedarf nach schnellen und kostengünstigen Analysemethoden in der (Trink-)Wasseranalytik steigt mit dem zunehmenden Eintrag pharmazeutisch aktiver Substanzen in die Umwelt. Insbesondere die Kontamination mit Antibiotika erscheint neben ökotoxikologischen Effekten vor allem in Hinblick auf die Evolution resistenter Keime im Wasser besorgniserregend. Wir berichten hier über die Entwicklung eines magnetpartikelbasierten Immunoassays (MBBA) zur Detektion des Breitbandantibiotikums Amoxicillin (AMX) in Wasserproben, der im Vergleich zum entsprechenden Enzyme-linked Immunosorbent Assay (ELISA) eine wesentlich kürzere Analysendauer sowie einen breiteren Messbereich mit niedrigerer Nachweisgrenze aufweist. Das angewendete Assayprinzip ist dabei leicht auf weitere Analyten übertragbar und ermöglicht die Implementierung in einen Immunosensor. KW - Magnetpartikel KW - Amoxicillin KW - Immunoassay KW - Wasser KW - Antikörper PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-527366 UR - https://www.gdch.de/netzwerk-strukturen/fachstrukturen/umweltchemie-und-oekotoxikologie/publikationen/mitteilungen/archiv/2021.html SN - 1618-3258 VL - 27 IS - 2 SP - 48 EP - 51 PB - Gesellschaft Deutscher Chemiker (GDCh) CY - Frankfurt/Main AN - OPUS4-52736 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Völzke, Holger A1 - Herold, Christian A1 - Wolff, Dietmar A1 - Orellana Pérez, Teresa A1 - Bollingerfehr, W. A1 - Prignitz, S. A1 - Wunderlich, A. T1 - Abschlussbericht zum FuE-Verbundvorhaben KoBrA: Anforderungen und Konzepte für Behälter zur Endlagerung von Wärme entwickelnden radioaktiven Abfällen und ausgedienten Brennelementen in Steinsalz, Tonstein und Kristallingestein N2 - Im Forschungsvorhaben KoBrA werden Anforderungen an Endlagerbehälter für hochradioaktive Abfälle erstmals systematisch und unter Berücksichtigung des internationalen Standes von Wissenschaft und Technik hergeleitet. Parallel werden die behälterrelevanten Randbedingungen und Beanspruchungsgrößen für Endlagerbehälter in den drei potenziellen Wirtsgesteinen Steinsalz, Tonstein und Kristallingestein ermittelt. Darauf aufbauend werden die zur Erfüllung der Anforderungen unter den gegebenen Einwirkungen und Beanspruchungen notwendigen Behälterfunktionen bestimmt und erste Konzeptideen für zukünftige Endlagerbehälter diskutiert bzw. entwickelt. KW - Endlager KW - Behälter KW - Anforderungen KW - Hochradioaktive Abfälle KW - Wirtsgestein PY - 2020 DO - https://doi.org/10.2314/KXP:1750909669 N1 - Auftraggeber: Bundesministerium für Wirtschaft und Energie (BMWi), Förderkennzeichen: 02E11527 und 02E11537. SP - 1 EP - 110 PB - BGE Technology CY - Peine AN - OPUS4-52289 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Lohrer, Christian A1 - Dudek, Gabriele T1 - Kalte Pyrotechnik - ein heißes Thema N2 - Beschreibung der Eigenschaften von vermeintlich kalter Pyrotechnik und die Gefährdungen bei der Verwendung. Beitrag ist als VS-NfD (Verschlusssache - Nur für den Dienstgebrauch) eingestuft. KW - Aerosole KW - Pyrotechnik KW - Nitrocellulose PY - 2021 SP - 32 EP - 38 PB - Bundeskriminalamt (BKA) CY - Wiesbaden AN - OPUS4-52400 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Auersch, Lutz A1 - Said, Samir T1 - Dynamic track-soil interaction – calculations and measurements about slab and ballast tracks N2 - The dynamic behaviour of slab and ballast tracks has been investigated by measurements and calculations. Hammer impacts and train passages have been analysed. Measurements have been performed by geophones (velocity transducers) which have been time-integrated to displacements. The calculations are done in frequency-wavenumber domain for multi-beam-on-continuous soil models. The characteristics of the different tracks and track elements have been established in theory and experiment. The frequency-dependent compliances (displacement transfer functions) show clear rail-on-rail-pad resonances or highly damped track-soil resonances. Compared to the rail and sleeper, the track plate has much lower amplitudes. The slab track has usually the highest rail amplitudes due to soft rail pads. The train passage yields track displacements which are a superposition of the axle loads from the two neighbouring axles of a bogie and from the two bogies of two neighbouring carriages. This global behaviour is characteristic for the track plate of the slab track whereas the rails of the slab and the ballast track behave more local with only one bogie of influence. The measurements agree very well with the theory of the continuous soil in case of the six measured slab tracks and acceptably well for the six measured ballast tracks. The measurements allow to find appropriate model parameters and to check the models, for example the Winkler model of the soil has been found less appropriate as it reacts more locally. KW - Slab track KW - Ballast track KW - Train passage KW - Hammer impact KW - Track-soil interaction PY - 2021 DO - https://doi.org/10.1631/jzus.A1900651 SN - 1673-565X VL - 22 IS - 1 SP - 21 EP - 36 PB - Zhejiang University Press CY - Hangzhou AN - OPUS4-52107 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Bandow, Nicole T1 - HORECA, Hochwertiges Recycling von Aschen aus der Müllverbrennung mittels eines innovativen Nassaufbereitungsverfahrens für eine ressourcenschonende und umweltverträgliche Verwertung N2 - Hausmüllverbrennungsasche (HMVA) hinsichtlich der Menge und der Qualität generierter Fraktionen optimiert. Die Optimierung wurde vom Projektpartner Evers und Co. GmbH durchgeführt. Neben der für die Wirtschaftlichkeit relevanten Rückgewinnung von Metallen stand die Qualität der mineralischen Fraktionen im Vordergrund. Die Mineralik stellt mengenmäßig den größten Anteil an HMVA dar und sollte weitestgehend für einen möglichen Einsatz als Baustoff nutzbar gemacht werden. Dafür musste insbesondere der Chlorid- und Sulfatgehalt reduziert werden. Gut wasserlösliche Substanzen können durch die nass-mechanische Aufbereitung über das Prozesswasser ausgetragen und unerwünschte Elemente im Filterkuchen angereichert und entsorgt werden. KW - Rostasche KW - Nassaufbereitung PY - 2015 VL - KF2201051MF2 SP - 1 EP - 34 AN - OPUS4-52424 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Kalbe, Ute A1 - Witt, K. J. A1 - Simon, Franz-Georg A1 - Prohaska, S. A1 - Slowik, V. T1 - Bedingungen suffosiver Erosionsphänomene in Böden N2 - Für eine detaillierte Analyse der Gefüge- und Porenstruktur weitgestufter Erdstoffe ist es notwendig, diese dreidimensional (3D) zu visualisieren und ihre Kenngrößen zu ermitteln. Dazu wurde an der BAM eine Präparationsmethode entwickelt, die es ermöglicht die Porenstruktur von Probenkörpern aus suffosiven Erdstoffen und definierten Korngrößenverteilungen über CT-Aufnahmen abzubilden. Über eine eigens dafür, in Zusammenarbeit mit dem Zuse-Institut Berlin (ZIB), entwickelte Bildanalysemethode wurden die Strukturdaten visualisiert. Aus dem Bilddatensatz konnte bereits in der Rückwärtsrechnung eine Kornverteilungslinie zur Validierung generiert und mit experimentell ermittelten Sieblinien verglichen werden. Des Weiteren wurden in Säulenexperimenten Kornumlagerungsprozesse unter der Verwendung von CT-Aufnahmen beobachtet. Als eine weitere Möglichkeit zur Beschreibung von Gefüge- und Porenstrukturen wurden Kugelpackungen modelliert und deren Strukturdaten ermittelt. Mit einem an der HTWK entwickelten stochastisch-heuristischen Algorithmus lassen sich wirklichkeitsnahe 3D-Gefügemodelle aus kugelförmigen Feststoffpartikeln generieren. Die Kornverteilung ist dabei wählbar. Für die erstellten Gefügemodelle kann der vollständige Porengraph einschließlich der Porengrößen und Engstellen ermittelt und ausgelesen werden. Ein an der BAM entwickelter und durch die BUW erweiterter Säulenversuch unter Verwendung systematisch veränderter Korngemische von natürlichen Gesteinskörnungen und Glaskugeln ergab weitere Aufschlüsse über die strukturbildenden Fraktionen des Korngerüstes. Die Perkolationstheorie ist eine moderne wahrscheinlichkeitstheoretische Methode, um Fluss- und Transportvorgänge innerhalb poröser Medien zu simulieren. Über Porennetzwerkmodelle werden die komplexen Fließwege in der Porenstruktur vereinfacht abgebildet. An der BUW wurde ein 3D-Bond-Perkolationsmodell auf einem simplen kubischen Gitter realisiert, in dem die Gitterknoten die Poren und die Gitterstäbe die Porenengstellen repräsentieren. Lokale und globale Strukturveränderungen infolge Partikeltransports werden über die Analyse von Porenräumen beschrieben. Mit diesem Perkolationsmodell können Aussagen zur lokalen und globalen Strukturveränderung durch Partikeltransport in definierten Bodenvolumen abgeleitet werden. Die hergeleiteten Zusammenhänge zu den suffosiven Materialtransportbedingungen mit der Perkolationstheorie sind für homogene, isotrope und selbstähnliche Erdstoffgefüge gültig. KW - Wasserbau KW - Bodenmechanik PY - 2012 VL - SI 1382/1-2 SP - 1 EP - 24 AN - OPUS4-52427 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Martin A1 - Erdt, René A1 - Gödde, M. A1 - Salg, St. T1 - Validierung der Extrapolation von Labortests mit Hilfe halbtechnischer Versuche bis 1 m3 und thermoanalytischer Methoden N2 - Zur Bestimmung der reaktionskinetischen Daten von Schüttgütern und iur Vorhersage des Selbstentzündungsverhaltens großer.Lager kommen verschiedene Analysemethoden zum Einsatz. Dabei handelt es sich .um thermische Verfahren wie die Differential-Scanning- Kalorimetrie OS(. die simultane Thermoanalyse STA sowie die Mikrokalorimetrie zur hochpräzisen Messung von Wärmeströmen. Für die oben genannten Methoden werden sehr kleine Probenmengen verwendet. In der Regel wird das Selbstentzündungsverhalten jedoch mit Hilfe von isoperibolen oder adiabatischen Warmlagerungsversuchen ermittelt: die Probenvolumina liegen hier meist im Bereich von ca. 100 cm3 bis zu mehreren Litern. Die Extrapolation auf technisch relevante Volumina birgt jedoch erhebliche Unsicherheiten. Diese Unsicherheiten zu identifizieren und zu reduzieren ist das Hauptziel eines 2018 gestarteten Forschungsprojekts. Dies soll in erster Linie durch den Aufbau eines Versuchsstandes zur Untersuchung von Probengrößen von bis zu. 1000 dm 3 geschehen. Sowohl Warmlagerungsversucl1e im Labormaßstab als auch thermoanalytische Verfahren. die mit Hilfe verschiedener Methoden ausgewertet werden. lassen, einzeln betrachtet. häufig nur bedingt zuverlässige Aussagen über das Selbstentzündungsverhalten von großen Schüttgütern zu. Es werden komplette Versuchsreihen mit allen genannten Prüfverfahren vorgestellt und Aussagen zur Anwendbarkeit der Extrapolationsmethoden diskutiert. T2 - VDI-Fachtagung "Sichere Handhabung brennbarer Stäube 2020" CY - Online meeting DA - 04.11.2020 KW - Selbstentzündung KW - Kinetische Daten KW - Halbtechnische Versuche KW - Thermoanalytische Methoden PY - 2020 SN - 978-3-18-092376-5 SP - 17 EP - 36 AN - OPUS4-52443 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ewert, Uwe A1 - Zscherpel, Uwe T1 - Aktuelle Entwicklungen in der Normung N2 - Es wird über die neuen Anforderungen ausgewählter Normen bzw. Normrevisionen informiert und insbesondere auch über die veränderten Parameter, die bei der Prüfpraxis, der Qualitätssicherung in der digitalen Radiographie und bei der Klassifizierung zu berücksichtigen sind. Das wichtigste Projekt ist die Revision der DIN EN ISO 17636-1, -2, RT von Schweißverbindungen, in ISO TC 44 SC 5 WG 1. Hauptaktivität bei ASTM ist gegenwärtig die Überarbeitung der CT-Standards und die Berücksichtigung der Anforderungen an das dimensionelle Messen. Der „Standard Guide for Computed Tomography“, ASTM E 1441, zur Bestimmung von MTF, Kontrast-Detail-Funktion (CDF) und Kontrast-Diskrimination-Diagramm (CDD) wurde revidiert und veröffentlicht. Die Mehrzahl der Hersteller von CT-Anlagen bietet entsprechende Software-Tools an. Weiterhin werden neue Festkörperentwürfe zur Charakterisierung von CT-Anlagen vorgestellt. Die folgenden Revisionen sind bei ASTM derzeit in Bearbeitung: ASTM E 2445, „CR Long Term Stability“ nach einem Round Robin-Test und für DDAs der Standard zur System-Charakterisierung, ASTM E2597/E2597M−14, und zur „DDA Long Term Stability“. Das Spider-Net-Diagramm zur Klassifizierung von DDAs wird um die Position „ISO Material Thickness limit“ erweitert. Der Standard EN 12679 zur Messung der Größe von Gammastrahlern wurde nach Revision unter Berücksichtigung von digitalen Messverfahren veröffentlicht. Die Revision der Standardserie EN 12543 zur Messung der Brennfleckgröße ist mit Verzögerung in Überarbeitung, um die digitalen Detektoren und Messmöglichkeiten mit Bildverarbeitungsprogrammen zu berücksichtigen. Die Messprozedur für Lochkameras wurde grundlegend revidiert und ist harmonisiert mit ASTM E 1165-12(2017). Die gemessenen Brennflecke unterscheiden sich und passen besser zu den Unschärfe-Messungen mit Doppeldraht BPKs (ISO 19232-5:2018) bei Vergrößerung. Ein Entwurf zur Messung der Brennfleckgröße von nano-Fokusröhren und Mikro-Fokusröhren (< 5 µm) wird derzeit vom Europäischen Metrologie-Programm EMPIR gefördert. Es wird über erste Ergebnisse informiert. T2 - 19. Seminar Aktuelle Fragen der Durchstrahlungsprüfung und Strahlenschutz CY - Online meeting DA - 23.03.2021 KW - Industrielle Durchstrahlungsprüfung KW - ZfP KW - Normentwicklung RT KW - DIN ISO ASTM International PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-524149 SP - Paper 8, 1 EP - Paper 8, 15 PB - DGZfP AN - OPUS4-52414 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pauw, Brian Richard T1 - Set of technical drawings, associated with manuscript entitled: "Extending Synchrotron SAXS instrument ranges through addition of a portable, inexpensive USAXS module with vertical rotation axes" N2 - This is a set of drawings accompanying the submitted paper entitled "Extending Synchrotron SAXS instrument ranges through addition of a portable, inexpensive USAXS module with vertical rotation axes". The parts described herein will combine with commercial off-the-shelf components to build a high precision pair of rotation stages for accurate measurement of scattering angles with a sub-microradian precision. KW - X-ray scattering KW - USAXS KW - ultra-small-angle X-ray scattering KW - technical drawings KW - module KW - extension PY - 2021 DO - https://doi.org/10.5281/zenodo.4604703 PB - Zenodo CY - Geneva AN - OPUS4-52547 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wilrich, Cordula T1 - Lagerung von Gefahrstoffen N2 - Die neugefasste TRGS 510 "Lagerung von Gefahrstoffen in ortsbeweglichen Behältern" ist veröffentlicht. In diesem Aufsatz werden ihre Kernelemente vorgestellt. KW - Arbeitsschutz KW - Gefahrstoffe KW - Gefahrstofflagerung KW - Gefahrstoffverordnung KW - Lagerung KW - Schutzmaßnahmen KW - TRGS 510 PY - 2021 IS - 2 SP - 10 EP - 11 AN - OPUS4-52558 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Ahmadi, Samim A1 - Hauffen, Jan Christian A1 - Kästner, L. A1 - Jung, P. A1 - Caire, G. A1 - Ziegler, Mathias T1 - Learned block iterative shrinkage thresholding algorithm for photothermal super resolution imaging N2 - Block-sparse regularization is already well-known in active thermal imaging and is used for multiple measurement based inverse problems. The main bottleneck of this method is the choice of regularization parameters which differs for each experiment. To avoid time-consuming manually selected regularization parameters, we propose a learned block-sparse optimization approach using an iterative algorithm unfolded into a deep neural network. More precisely, we show the benefits of using a learned block iterative shrinkage thresholding algorithm that is able to learn the choice of regularization parameters. In addition, this algorithm enables the determination of a suitable weight matrix to solve the underlying inverse problem. Therefore, in this paper we present the algorithm and compare it with state of the art block iterative shrinkage thresholding using synthetically generated test data and experimental test data from active thermography for defect reconstruction. Our results show that the use of the learned block-sparse optimization approach provides smaller normalized mean square errors for a small fixed number of iterations than without learning. Thus, this new approach allows to improve the convergence speed and only needs a few iterations to generate accurate defect reconstruction in photothermal super resolution imaging. KW - Iterative shrinkage thresholding algorithm KW - Neural network KW - Deep learning KW - Active thermography KW - Photothermal super resolution PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-525364 DO - https://doi.org/10.48550/arXiv.2012.03547 SN - 2331-8422 SP - 1 EP - 11 PB - Cornell University CY - Ithaca, NY AN - OPUS4-52536 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Ahmadi, Samim A1 - Kästner, L. A1 - Hauffen, Jan Christian A1 - Jung, P. A1 - Ziegler, Mathias T1 - Photothermal-SR-Net: A customized deep unfolding neural network for photothermal super resolution imaging N2 - This paper presents deep unfolding neural networks to handle inverse problems in photothermal radiometry enabling super resolution (SR) imaging. Photothermal imaging is a well-known technique in active thermography for nondestructive inspection of defects in materials such as metals or composites. A grand challenge of active thermography is to overcome the spatial resolution limitation imposed by heat diffusion in order to accurately resolve each defect. The photothermal SR approach enables to extract high-frequency spatial components based on the deconvolution with the thermal point spread function. However, stable deconvolution can only be achieved by using the sparse structure of defect patterns, which often requires tedious, hand-crafted tuning of hyperparameters and results in computationally intensive algorithms. On this account, Photothermal-SR-Net is proposed in this paper, which performs deconvolution by deep unfolding considering the underlying physics. This enables to super resolve 2D thermal images for nondestructive testing with a substantially improved convergence rate. Since defects appear sparsely in materials, Photothermal-SR-Net applies trained blocksparsity thresholding to the acquired thermal images in each convolutional layer. The performance of the proposed approach is evaluated and discussed using various deep unfolding and thresholding approaches applied to 2D thermal images. Subsequently, studies are conducted on how to increase the reconstruction quality and the computational performance of Photothermal-SR-Net is evaluated. Thereby, it was found that the computing time for creating high-resolution images could be significantly reduced without decreasing the reconstruction quality by using pixel binning as a preprocessing step. KW - Photothermal super resolution KW - Nondestructive testing KW - Deep unfolding KW - Deep learning KW - Deep imaging KW - Physics-based deep learning KW - Laser thermography KW - Elastic net KW - Iterative shrinkage thresholding algorithm PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-525371 DO - https://doi.org/10.48550/arXiv.2104.10563 SN - 2331-8422 SP - 1 EP - 10 PB - Cornell University CY - Ithaca, NY AN - OPUS4-52537 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lecompagnon, Julien A1 - Ahmadi, Samim A1 - Hirsch, Philipp Daniel A1 - Ziegler, Mathias ED - Zalameda, J. N. ED - Mendioroz, A. T1 - Full-frame thermographic super-resolution with 2D-structured laser heating N2 - Thermographic super-resolution techniques allow the resolution of defects/inhomogeneities beyond the classical limit, which is governed by the diffusion properties of thermal wave propagation. Photothermal super-resolution is based on a combination of an experimental scanning strategy and a numerical optimization which has been proven to be superior to standard thermographic methods in the case of 1D linear defects. In this contribution, we report on the extension of this approach towards a full frame 2D photothermal super-resolution technique. The experimental approach is based on a repeated spatially structured heating using high power lasers. In a second post-processing step, several measurements are coherently combined using mathematical optimization and taking advantage of the (joint) sparsity of the defects in the sample. In our work we extend the possibilities of the method to efficiently detect and resolve defect cross sections with a fully 2D-structured blind illumination. T2 - Thermosense: Thermal Infrared Applications XLIII CY - Online meeting DA - 12.04.2021 KW - Thermography KW - super-resolution KW - NDT KW - Inspection KW - Image resolution PY - 2021 DO - https://doi.org/10.1117/12.2586093 VL - 11743 SP - 11743-26, 10 PB - SPIE AN - OPUS4-52524 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lecompagnon, Julien A1 - Ahmadi, Samim A1 - Hirsch, Philipp Daniel A1 - Ziegler, Mathias T1 - 2D-Photothermal Super Resolution with Sparse Matrix Stacking N2 - Thermographic super resolution techniques allow the spatial resolution of defects/inhomogeneities below the classical limit, which is governed by the diffusion properties of thermal wave propagation. In this work, we report on the extension of this approach towards a full frame 2D super resolution technique. The approach is based on a repeated spatially structured heating using high power lasers. In a second post-processing step, several measurements are coherently combined using mathematical optimization and taking advantage of the (joint) sparsity of the defects in the sample T2 - Sensor and Measurement Science International Conference SMSI 2021 CY - Online meeting DA - 03.05.2021 KW - Thermography KW - Super-resolution KW - NDT KW - Inspection KW - Image resolution PY - 2021 SN - 978-3-9819376-4-0 DO - https://doi.org/10.5162/SMSI2021/C2.2 VL - SMSI 2021 - Sensors and Instrumentation SP - 183 EP - 184 AN - OPUS4-52589 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Held, Mathias A1 - Rashwan, Abdalla A1 - Lauschkin, Maik A1 - Bulling, Jannis A1 - Lugovtsova, Yevgeniya A1 - Prager, Jens T1 - Inverse determination of elastic material parameters from ultrasonic guided waves dispersion measurements using Convolutional Neuronal Networks N2 - In the context of Industry 4.0 and especially in the field of Structural Health Monitoring, Condition Monitoring and Digital Twins, simulations are becoming more and more important. The exact determination of material parameters is required for realistic results of numerical simulations of the static and dynamic behavior of technical structures. There are many possibilities to determine elastic material parameters. One possibility of non-destructive testing are ultrasonic guided waves. For the evaluation of the measurement results, mostly inverse methods are applied in order to be able to draw conclusions about the elastic material parameters from analysing the ultrasonic guided wave propagation. For the inverse determination of the elastic material Parameters with ultrasonic guided waves, several investigations were carried out, e.g. the determination of the isotropic material parameters through the point of zero-groupvelocity or anisotropic material parameters with a simplex algorithm. These investigations are based on the evaluation of dispersion images. Machine learning and in particular Convolutional Neural Networks (CNN) are one possibility of the automated evaluation from Image data, e.g. classification or object recognition problems. This article shows how the dispersive behavior of ultrasonic guided waves and CNNs can be used to determine the isotropic elastic constants of plate-like structures. T2 - SMSI 2021 2021-05-03 - 2021-05-06 digital CY - Online meeting DA - 03.05.2021 KW - Convolutional Neuronal Networks KW - Inverse Probleme KW - Materialcharakterisierung KW - guided waves KW - Dispersion PY - 2021 SN - 978-3-9819376-4-0 DO - https://doi.org/10.5162/SMSI2021/A10.2 VL - 2021 SP - 239 EP - 240 AN - OPUS4-52618 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Winkler, Nicolas P. A1 - Neumann, Patrick P. A1 - Kohlhoff, Harald A1 - Erdmann, Jessica A1 - Schaffernicht, Erik A1 - Lilienthal, Achim J. T1 - Development of a Low-Cost Sensing Node with Active Ventilation Fan for Air Pollution Monitoring N2 - A fully designed low-cost sensing node for air pollution monitoring and calibration results for several low-cost gas sensors are presented. As the state of the art is lacking information on the importance of an active ventilation system, the effect of an active fan is compared to the passive ventilation of a lamellar structured casing. Measurements obtained in an urban outdoor environment show that readings of the low-cost dust sensor (Sharp GP2Y1010AU0F) are distorted by the active ventilation system. While this behavior requires further research, a correlation with temperature and humidity inside the node shown. T2 - SMSI 2021 Conference: Sensor and Measurement Science International CY - Online meeting DA - 03.05.2021 KW - Wireless sensing node KW - Air pollution KW - Sensor network KW - Environmental monitoring PY - 2021 DO - https://doi.org/10.5162/SMSI2021/D3.5 VL - 2021 SP - 260 EP - 261 AN - OPUS4-52607 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zeipert, H. A1 - Claes, L. A1 - Johannesmann, S. A1 - Webersen, M. A1 - Lugovtsova, Yevgeniya A1 - Prager, Jens A1 - Henning, B. T1 - Measurement and simulation of Lamb waves in adhesive-bonded multilayer systems N2 - Lamb waves are a common tool in the field of non-destructive testing and are widely used for materialcharacterisation. Further, the increasing computational capability of modern systems enables the Simulation of complex and detailed material models. This work demonstrates the possibility of simulating an adhesive-bonded multilayer system by characterising each layer individually, and introduces an Approach for determining the dispersive behaviour of acoustic waves in a multilayer system via real measurements. T2 - SMSI 2021 Conference – Sensor and Measurement Science International CY - Online meeting DA - 03.05.2021 KW - Adhesive bonds KW - Lamb waves KW - Elastic constants KW - Non-Destructive Testing KW - Ultrasound PY - 2021 DO - https://doi.org/10.5162/SMSI2021/A8.2 SP - 91 EP - 92 AN - OPUS4-52634 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wosniok, Aleksander A1 - Krebber, Katerina T1 - Faseroptische Strahlungssensoren für kerntechnische Anwendungen N2 - Der Anstieg der Vielfalt nuklearer Anwendungen weit über die Bereiche der kerntechnischen Stromerzeugung erhöht die Relevanz der Entwicklung und Anwendung neuer Technologien zur Strahlungsüberwachung. Auch die offenen Sicherheitsfragen bei der Entsorgung radioaktiver Abfälle einschließlich Zwischen- und Endlagerungsproblematik verstärkt die Nachfrage nach effizienten Monitoringsystemen zum Schutz von Mensch und Umwelt vor ionisierender Strahlung. Aufgrund ihrer messtechnisch vorteilhaften Materialeigenschaften stellen die faseroptischen Strahlungssensoren eine vielversprechende Alternative zu traditionellen Dosimetern dar. Bedingt durch ihre kleinen Abmessungen, elektromagnetische Unempfindlichkeit und ihr geringes Gewicht können faseroptische Sensoren in einer harschen Umgebung an schwer zugänglichen Stellen eingesetzt werden. Darüber hinaus bietet diese Art der Sensoren die Möglichkeit der ortsverteilten Messung entlang der gesamten Sensorfaser. Somit kann durch eine einzelne optische Faser eine Vielzahl an punktuell messenden Sensoren ersetzt werden. Dieser Beitrag beschreibt die in der BAM vorangetriebenen Entwicklungen unterschiedlicher Sensorprinzipien, -lösungen und -verfahren zur Detektion ionisierender Strahlung. T2 - 2. Tage der Standortauswahl CY - Online meeting DA - 11.02.2021 KW - Faseroptischer Strahlungssensor KW - Ortsauflösende Fasersensorik KW - Strahlungsinduzierte optische Dämpfung KW - Gammastrahlung KW - Rayleigh-Streuung KW - Brillouin-Streuung PY - 2021 SP - 43 AN - OPUS4-52211 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hicke, Konstantin A1 - Chruscicki, Sebastian A1 - Münzenberger, Sven T1 - Urban traffic monitoring using Distributed Acoustic Sensing along laid fiber optic cables N2 - The feasibility of traffic monitoring along a major urban road using Distributed Acoustic Sensing (DAS) is demonstrated. We present measurement results of conventional intensity-based DAS along a dark fiber in a tubed fiber optic cable buried roadside. With only minimal postprocessing different classes of traffic participants can be distinguished (cars, bikes, pedestrians). Different methods for pre-processing raw data are compared, especially with regard to providing suitable inputs for pattern recognition algorithms. Furthermore, the various challenges for automatized vehicle detection and classification related to varying sensitivity and inhomogeneous signal propagation are discussed. Sensitivity fluctuations and variations are in part inherent to the measurement technology and originate in part in ground conditions. The measurement quality and usefulness for traffic monitoring of intensity-based DAS is compared to that of state-of-the-art phase-resolved DAS, allowing quantitative evaluation of vibration signals. T2 - EAGE GeoTech 2021 Second EAGE Workshop on Distributed Fibre Optic Sensing CY - Online meeting DA - 01.03.2021 KW - Distributed fiber optic sensing KW - Distributed acoustic sensing KW - DAS KW - Traffic monitoring KW - Road condition monitoring PY - 2021 DO - https://doi.org/10.3997/2214-4609.202131008 VL - 2021 SP - Paper 8, 1 PB - European Association of Geoscientists & Engineers CY - Houten, Niederlande AN - OPUS4-52214 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Essig, W. A1 - Bernhardt, Y. A1 - Döring, D. A1 - Solodov, I. A1 - Gautzsch, T. A1 - Gaal, Mate A1 - Hufschläger, Daniel A1 - Sommerhuber, R. A1 - Marhenke, T. A1 - Hasener, J. A1 - Szewieczek, A. A1 - Hillger, W. T1 - Air-coupled ultrasound - emerging NDT method N2 - This paper deals with the state of the art of air-coupled ultrasonic testing. KW - Air-coupled KW - Ultrasonic testing KW - Transducers PY - 2021 SN - 1616-069X VL - 173 SP - 32 EP - 43 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-52231 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heßmann, Jennifer A1 - Bachmann, Marcel A1 - Hilgenberg, Kai T1 - Joining dissimilar materials a new approach based on laser beam welding and melt displacement by electromagnetic forces N2 - In order to reduce weight of vehicles, the interest in multi-material-design has been growing within the last few years. For vehicles the combination of steel and aluminium alloys offers the most promising compromise between weight, strength and formability. Thermal joining of these dissimilar materials is still a challenge to overcome. A possible approach is a new joining technology, whereby a combination of laser beam welding and contactless induced electromagnetic forces are used to displace the generated melt of one joining partner into a notch of the other. This paper presents the working principle and shows numerical analyses to improve the understanding of this joining process. The simulations help to calculate the thermal development of the joining partners, which is important for the formation of intermetallic phases. Furthermore, the calculation of the time required for a complete displacement is possible. The numerical results are validated by experimental results. T2 - LiM 2021 CY - Online meeting DA - 21.06.2021 KW - Joining dissimilar materials KW - Laser beam welding KW - Electromagnetic forces KW - Steel and aluminium PY - 2021 SP - 1 EP - 9 PB - Wissenschaftliche Gesellschaft Lasertechnik e.V. (WLT) AN - OPUS4-52978 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Beck, Uwe A1 - Baier, Jennifa A1 - Dähne, L. A1 - Lerche, K.-H. T1 - Schlussbericht zum BMWi/MNPQ-Verbundprojekt: PLASMA-FIT (PLASMA-kompatible Partikel zur gepulsten in-situ Injektion von ex-situ hergestellten Partikeln für add-on Funktionen und zur Identifizierung in BeschichTungen) N2 - Im Fokus steht die Qualitätssicherung mit Blick auf Herstellung, Modifizierung, Handling und Erprobung von PLASMA-kompatiblen Partikeln zur gepulsten in-situ Injektion von ex-situ hergestellten Partikeln für add-on Funktionen in und zur Identifikationsprüfung von BeschichTungen (PLASMA-FIT). Im Kern war zunächst zu prüfen, welche Klassen ex-situ hergestellter Partikel unterschiedlichster Materialien überhaupt bzw. unter welchen Bedingungen PLASMA-fit sind oder unter welchen Randbedingungen PLASMA-fit gemacht werden können. In den dazugehörenden Projektphasen Screening und Adaption stand dabei das komplexe Beanspruchungsszenario bestehend aus Vakuum-, Temperatur- und wenigstens kurzzeitiger Plasmabeständigkeit der ex-situ bereitgestellten Partikel im Fokus. In der Projektphase Applikation sollte dann unter Verwendung einer modifizierten Plasmaquelle (BAM-Patentanmeldung, beabsichtigte Lizenznahme durch Fa. CemeCon, Optionsvertrag) hinsichtlich der Realisierbarkeit, Prüfung und Qualitätssicherung von Plasmadispersionsschichten ein erster Praxistest zur in-situ Injektion von Partikeln in einen laufenden Beschichtungsprozess, zur Realisierung funktioneller Eigenschaften z.B. zur Identifikation oder Authentifizierung von Originalteilen, vorgenommen werden KW - Plasma-kompatible Partikel KW - Plasma-Injektion KW - add-on Funktionen PY - 2015 N1 - Das Dokument unterliegt der Vertraulichkeit und kann nicht zugänglich gemacht werden - The document is subject to confidentiality restrictions and cannot be made accessible - Projektlaufzeit: 17.11.2010-16.02.2015 - Project runtime: 17.11.2010-16.02.2015 SP - 1 EP - 10 AN - OPUS4-48360 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Mike A1 - Völzke, Holger A1 - Zencker, Uwe A1 - Hauer, Katharina A1 - Herz, A. A1 - Kreienmeyer, M. T1 - Aufbau eines Aufprallfundamentes mit reproduzierbaren Eigenschaften für Baumusterprüfungen von Abfallbehältern für das Endlager Konrad N2 - Abgeleitet aus den in Teil 3 der „Systemanalyse Konrad“ definierten Lastannahmen für den „untertägigen Anlagenbereich“ müssen Verpackungen, die der Abfallbehälterklasse I (ABK I) mit dem zusätzlichen Merkmal der störfallfesten (sf) Verpackung oder der ABK II zugeordnet werden, gemäß den „Endlagerungsbedingungen, Endlager Konrad“, nach einem „…Fall aus 5 m Höhe auf eine unnachgiebige Unterlage…“ bestimmten Anforderungen genügen. Eine nähere Beschreibung der Prüfeinrichtung sowie die Definition detaillierter Anforderungen an das Aufprallfundament erfolgen in der „Produktkontrolle, Endlager Konrad“: „Die Prüfeinrichtung, bestehend aus einer Hebeeinrichtung und einem Fundament ist so zu gestalten, dass der Fall des Prüfmusters in jeder beliebigen Aufprallorientierung aus 5 m Höhe, gemessen von der Unterkante des Prüfmusters zum Fundament, möglich ist. Das Fundament ist aus Beton der Mindestgüte B 35 herzustellen und muss so beschaffen und verankert sein, dass keine Zerstörung in zahlreiche kleinere Bruchstücke erfolgt und keine horizontale Verschiebung des Fundamentes oder seiner Teile auftritt. Maße und Masse des Fundaments müssen so beschaffen sein, dass der Einfluss des Baugrundes unter dem Fundament auf den Aufprallwiderstand vernachlässigbar ist.“ Im Rahmen der Bauartprüfung für Behälter zur Endlagerung radioaktiver Abfälle mit zu vernachlässigender Wärmeentwicklung im Endlager Konrad wird die Bundesanstalt für Materialforschung und -prüfung (BAM) von der Bundesgesellschaft für Endlagerung (BGE) als Sachverständige hinzugezogen und ist in der Regel auch mit der Durchführung der notwendigen Fallprüfungen auf dem Testgelände Technische Sicherheit der BAM (BAM TTS) einschließlich der Bereitstellung der benötigten Prüfeinrichtungen sowie des regelkonformen Aufprallfundamentes beauftragt. Der Prozess, beginnend von der Gewährleistung einer von allen Beteiligten als gültig bewerteten Fallprüfung bis hin zur abschließenden Bewertung und Interpretation der Versuchsergebnisse erfordert dabei u.a. eine sorgfältige Planung und Fertigung der für das Endlager Konrad repräsentativen Fundamentplatte und deren Ankopplung an einen Untergrund im Sinne der „Regulations for the Safe Transport of Radioactive Material“ wie er zum Beispiel auf den beiden Fallversuchsanlagen des BAM Testgelände Technische Sicherheit (BAM TTS) zur Verfügung steht. Um diese Anforderungen zu erfüllen muss zum einen der Erhalt der Integrität der Fundamentplatte beim Fallversuch durch eine geeignete Auswahl und kraftflussgerechte Anordnung der Stabstahl-Bewehrung sowie deren Verankerung garantiert und damit eine unzulässige Energieaufnahme durch Risse sowie eine unzulässige „… Zerstörung (der Fundamentplatte) in zahlreiche kleinere Bruchstücke …“, wie in [3] gefordert, verhindert werden. Außerdem ist zu gewährleisten, dass der Beton die Anforderungen an die vorgeschriebene Mindestgüte bzw. -festigkeit zum Zeitpunkt der Fallprüfung erfüllt, die Betonfestigkeit jedoch zur Vermeidung unnötig verschärfter Prüfrandbedingungen eine zu definierende Obergrenze nicht überschreitet. Ausgehend von dem 2009 im Rahmen der KONTEC veröffentlichten Wissensstand präsentiert die BAM im vorliegenden Beitrag die wesentlichen Ergebnisse der zwischenzeitlich bei der Planung und Durchführung von zahlreichen Fallprüfungen gewonnenen Erfahrungen bzgl. Spezifikation und Fertigung der für die Fallversuche notwendigen Fundamentplatten sowie deren Anbindung an den Untergrund. Neben den immer wieder notwendigen Anstrengungen zur Gewährleistung einer im Rahmen der Definition korrekten Betondruckfestigkeit am Tag der Fallprüfung wird die Anpassung der Bewehrungsführung an verschiedene Fallpositionen diskutiert. Zur Ergänzung des gültigen Regelwerks entsteht parallel zu diesem Dokument eine Fachnotiz, in der BGE und BAM die Vorgaben und Spezifikationen zur regelwerkskonformen Herstellung und Montage von Fundamentplatten für Fallprüfungen im Rahmen der Behälterbauartprüfungsverfahren für das Endlager Konrad zusammenfassen und veröffentlichen werden. Diese Fachnotiz soll detaillierte Vorgaben und Spezifikationen zur Planung, Beauftragung, Herstellung und abschließenden Prüfung eines solchen Fundamentes und dessen Anbindung an den Untergrund enthalten. Damit soll allen beteiligten Organisationen wie Antragstellern, Sachverständigen und BGE ein langfristig verlässlicher Leitfaden im Hinblick auf die Durchführung anforderungsgerechter Fallprüfungen unter definierten und reproduzierbaren Randbedingungen im Rahmen der Bauartprüfungsverfahren für das Endlager Konrad an die Hand gegeben werden. T2 - KONTEC 2021 CY - Dresden, Germany DA - 25.08.2021 KW - Aufprallfundament KW - Endlager Konrad KW - Fallprüfung PY - 2021 SP - 1 EP - 10 CY - Dresden AN - OPUS4-53372 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - VIDEO A1 - Pauw, Brian Richard T1 - The SAXS platform at BAM N2 - Presentation of the Small-Angle X-Ray Scattering intrument at BAM (Berlin - Germany). More information about SAXS is available on Brian Pauw's long-running SAXS blog: https://lookingatnothing.com/ KW - X-ray scattering KW - MOUSE KW - Instrumentation KW - SAXS KW - Laboratory PY - 2021 UR - https://www.youtube.com/watch?v=OjYToZQTsqo PB - YouTube, LLC CY - San Bruno, CA, USA AN - OPUS4-53358 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Shapovalov, Oleg A1 - Shapovalova, M. A1 - Ossenbrink, R. A1 - Heckel, Thomas A1 - Michailov, V. A1 - Weiss, S. A1 - Gaal, Mate T1 - Verbessern der Korrosionsbeständigkeit eines hochtemperaturbeständigen Ultraschalldämpfungskörpers mittels Laserstrahl-Auftragschweißen N2 - Während in einem konventionellen Ultraschallprüfkopf ein Kunststoffdämpfungskörper mit Kleber oder Öl an einen Piezoschwinger angekoppelt ist, werden als Hochtemperaturlösung feinporöse sintermetallische Dämpfungsmaterialien mit einer Flüssigglasankopplung eingesetzt. Um dabei das Sintermetall vor dem korrosiven Angriff der Glasschmelze zu schützten, wird am Dämpfungskörper gegenwärtig Gold- oder Platinfolie zeit- und kostenaufwendig appliziert. In der aktuellen Arbeit wurde eine Methode zum Korrosionsschutz der sintermetallischen Oberfläche aus rostfreiem Stahl mittels Laser-Pulverauftragschweißen entwickelt. Im Laufe einer Schweißparameterstudie auf dem Substratmaterial aus massivem rostfreiem Stahl wurde die Eignung unterschiedlicher Auftragsmaterialien auf Nickel- und Kobaltbasis untersucht. Dabei wurde zunächst der Einfluss verschiedener Schweißparameter wie Laserleistung, Vorschubgeschwindigkeit und Pulvermenge auf die Auftragsqualität (Nahtform, Vermischungsgrad, Porosität) metallografisch bewertet. Anschließend wurden die aufgetragenen Schichten hinsichtlich ihrer Korrosionsbeständigkeit getestet. Der Kontakt mit einer flüssigen Glasmischung bei 500 °C hat bei keiner der beschichteten Proben sichtbare Korrosionswirkung gezeigt. Als Resultat der Schweißparameterstudie haben sich besonders die nickelbasierten Pulver als gut geeignete Materialien für den Prozess gezeigt. Die identifizierten Schweißparameter wurden im nächsten Schritt erfolgreich an das sintermetallische Substrat angepasst. T2 - DVS Congress CY - Online meeting DA - 14.09.2021 KW - Korrosion KW - Hochtemperaturbeständigkeit KW - Ultraschallwandler PY - 2021 SN - 978-3-96144-146-4 SN - 978-3-96144-147-1 VL - 2021 SP - 370 EP - 377 AN - OPUS4-53362 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wu, Cheng-Chieh A1 - Völker, Daniel A1 - Weisbrich, S. A1 - Neitzel, F. ED - Holl, H. T1 - The Finite Volume Method in point of view of Finite Element Method N2 - The best-known discretization methods for solving engineering problems formulated as partial differential equations are finite difference method (FDM), finite element method (FEM) and finite volume method (FVM). While the finite volume method is used in fluid mechanics, the finite element method is predominant in solid state mechanics. At first glance, FVM and FEM are two highly specialized methods. However, both methods can solve problems of both solid mechanics and fluid mechanics well. Since experimental mechanics deals not only with solid state physics but also with fluid mechanics problems, we want to understand FVM in the sense of FEM in this work. In the long term, we want to use the variational calculus to unify many important numerical methods in engineering science into a common framework. In this way, we expect that experiences can be better exchanged between different engineering sciences and thus innovations in the field of experimental mechanics can be advanced. But in this work, we limit ourselves to the understanding of the FVM with the help of the variational calculus already known in FEM. We use a simple 1D Poisson equation to clarify the point. First, we briefly summarize the FVM and FEM. Then we will deal with the actual topic of this paper, as we establish the FEM and the FVM on a common basis by variation formulation. It is shown here that the FVM can be understood in terms of the finite element method with the so-called Galerkin-Petrov approach. T2 - 37th Danubia Adria Symposium on Advances in Experimental Mechanics CY - Linz, Österreich DA - 21.09.2021 KW - Finite element method KW - Finite volume method KW - Variational calculation KW - Simulation KW - Computational physics PY - 2021 SN - 978-3-9504997-0-4 SP - 12 EP - 13 AN - OPUS4-53422 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kröll, Mirco A1 - Grundtner, R. A1 - Pagano, F. A1 - Nyberg, E. A1 - Heino, V. A1 - Spaltmann, Dirk A1 - Gradt, Thomas T1 - Auswirkungen von vereinheitlichten Prozeduren auf tribologische Versuche N2 - Anerkannte Institutionen stellen ihre Kompetenzen auf dem Gebiet tribologischer Charakterisierungen Industrie und Forschung zur Verfügung (https://www.i-tribomat.eu/). Ein Aspekt hierbei ist eine tribologische Datenbank. Um die nötige Qualität der Daten sicherzustellen, sind vereinheitlichte Prozeduren erforderlich, in deren Auswirkungen dieser Vortrag einen Einblick gibt. T2 - 62. Tribologie-Fachtagung der Gesellschaft für Tribologie e. V. CY - Online meeting DA - 27.09.2021 KW - Datenbank KW - Tribologische Daten KW - Europäisches Tribologie-Zentrum PY - 2021 SN - 978-3-9817451-6-0 VL - 15 SP - 15/1 EP - 15/4 AN - OPUS4-53430 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Florian, Camilo A1 - Deziel, J.-L. A1 - Kirner, Sabrina V. A1 - Siegel, J. A1 - Bonse, Jörn T1 - Femtosecond laser-induced oxidation in the formation of periodic surface structures N2 - Micro- and nanostructuring with laser-induced periodic surface structures (LIPSS) has been demonstrated to be feasible in a wide variety of materials including metals, semiconductors and dielectrics. Suitable processing regimes for flat, curved and complex surfaces have been identified for many materials, allowing the generation of diverse applications in fields such as optics, tribology and medicine, to name a few. A common side effect when producing such structures in air environment is the formation of a thin surface oxide layer in the laser irradiated areas. Previous studies have shown that oxidation plays an important role in the tribological performance for which the structures where created, and very recently it has been shown that the laser-induced oxide graded layers may contribute to the formation of a new type of embedded low-spatial frequency LIPSS (LSFL) with annomalous orientation parallel to the laser polarization, in addition to the appearance of the well-known high-spatial frequency LIPSS (HSFL) at the surface. In this contribution, we explore this effect experimentally for chromium nitride (CrN) irradiated with femtosecond laser pulses and compare the findings to finite-difference time-domain (FDTD) simulations of the intensity distributions at different depth positions. T2 - 2021 Conference on Lasers and Electro-Optics/Europe – European Quantum Electronics Virtual Conferences CY - Munich, Germany DA - 21.06.2021 KW - Femtosecond laser ablation KW - Finite-difference time-domain calculations KW - Laser-induced periodic surface structures (LIPSS) KW - Surface oxidation PY - 2021 SN - 978-1-6654-1876-8 DO - https://doi.org/10.1109/CLEO/Europe-EQEC52157.2021.9542774 VL - 2021 SP - 1 PB - Institute of Electrical and Electronics Engineers (IEEE) CY - Piscataway, NJ, USA AN - OPUS4-53457 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baensch, Franziska A1 - Sanabria, S. T1 - Der Verformungswiderstand im Holz und die Rolle der Holzstrahlen N2 - Von den Zellulosefibrillen über die Zellwand und die Anordnung der Früh- und Spätholzzellen in einem Jahrring bis hin zum Balken von Natur aus ist Holz ein optimierter Hochleistungswerkstoff, der Handwerker, Architekten, Ingenieure und Wissenschaftler fasziniert und begeistert. Im digitalen Zeitalter werden neben Standard-Laborexperimenten zunehmend Modelle und Simulationen eingesetzt, um das Verhalten des Materials unter verschiedenen Belastungen besser zu verstehen und vorherzusagen. Dazu werden Zahlenwerte von Verformungen im subzellulären Maßstab benötigt, die nun in Experimenten an der TOMCAT-Beamline (TOmographic Microscopy and Coherent rAdiology ExperimenTs) der SLS (Swiss Light Source) gewonnen werden konnten: Holzproben aus Fichte ( Picea abies Karst.) mit einem Prüfquerschnitt von mindestens 1 mm² auf Zug oder Druck beansprucht. Die strukturellen Veränderungen auf Zellebene wurden mittels Computertomographie erfasst. Für die nachträgliche Analyse der 3D-Mikrostruktur von Holz wurde ein Ansatz entwickelt, der es ermöglicht, einzelne Zellen, die in mehreren Tomogrammen unterschiedlicher Belastungszustände erfasst wurden, zu verfolgen. Dabei wurden die Zellgeometrien und das subzelluläre Deformationsverhalten quantifiziert. Unter Zugbelastung beispielsweise verengt sich die Zellwanddicke um ca. 0,8%, das sind bei der gemessenen mittleren Zellwanddicke von 3,5 µm ca. 28 nm. Diese und andere Erkenntnisse liefern nun einen direkten numerischen Zusammenhang zwischen Verformungen der Holzmikrostruktur und dem daraus resultierenden makroskopischen Verhalten. T2 - 5. Holzanatomisches Kolloquium CY - Dresden, Germany DA - 09.09.2021 KW - Wood materials KW - Holz KW - Individual cell tracking KW - Mikro CT PY - 2021 SP - 92 EP - 101 CY - Dresden AN - OPUS4-53405 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Patrick P. A1 - Hirschberger, Paul A1 - Bartholmai, Matthias ED - Holl, H. T1 - Aerial Chemical-Trail Detection and Localization N2 - This paper presents first advances in the area of aerial chemical trail following. For that purpose, we equipped a palm-size aerial robot, based on the Crazyflie 2.0 quadrocopter, with a small lightweight metal oxide gas sensor for measuring evaporated ethanol from chemical trails. To detect and localize the chemical trail, a novel detection criterion was developed that uses only relative changes in the transient phase of the sensor response, making it more robust in its application. We tested our setup in first crossing-trail experiments showing that our flying ant robot is able to correlate an odor hit with the chemical trail within 0.14 m. Principally, this could enable aerial chemical trail following in the future. T2 - 37th Danubia - Adria Symposium on Advances in Experimental Mechanics CY - Linz, Austria DA - 21.09.2021 KW - Nano aerial robot KW - Trail following KW - Trail detection KW - Localization PY - 2021 SN - 978-3-9504997-0-4 VL - 2021 SP - 39 EP - 40 AN - OPUS4-53409 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beck, Uwe A1 - Baier, Jennifa A1 - Fischer, Daniel A1 - Griepentrog, Michael A1 - Hertwig, Andreas A1 - Hielscher-Hofinger, Stefan A1 - Stockmann, Jörg Manfred A1 - Weise, Matthias T1 - Mapping und Imaging modifizierter Oberflächen: Generische Kenngrößen, Fehlstellen, Reinigungszustand und Haftfestigkeit N2 - Der Vortrag widmet sich dem Mapping und Imaging modifizierter Oberflächen: generische Kenngrößen, Fehlstellen, Reinigungszustand und Haftfestigkeit. Es werden Untersuchungsmethoden zu ihrer Prüfung dargestellt. T2 - 37. ak-adp 2021 CY - Jena, Germany DA - 16.06.2021 KW - Qualitätssicherung KW - Mapping modifizierter Oberflächen KW - Imaging modifizierter Oberflächen KW - Generische Kenngrößen KW - Haftfestigkeit KW - Klebfestigkeit PY - 2021 SP - 1 EP - 10 AN - OPUS4-52893 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Kranzmann, Axel T1 - Effects of saline aquifer water on the corrosion behaviour of martensitic stainless steels during exposure to CO2 environment N2 - Immersion tests of potential injection pipe steels 42CrMo4, X20Cr13, X46Cr13, X35CrMo4 and X5CrNiCuNb16-4 at T=60 °C and ambient pressure and p=100 bar were performed for 700 h - 8000 h in a CO₂-saturated synthetic aquifer environment similar to CCS-sites in the Northern-German-Basin. Main corrosion products are FeCO₃ and FeOOH. Highest surface corrosion rates at ambient pressure are 0.8 mm/year for 42CrMo4 and lowest 0.01 mm/year for X5CrNiCuNb16-4. Corrosion rates at 100 bar (max. 0.01 mm/year for 42CrMo4, X20Cr13, X46Cr13) are generally lower than at ambient pressure (<0.01 mm/year for X35CrMo4, X5CrNiCuNb16-4). Heat treatment to martensitic microstructure offers good corrosion resistance. T2 - 15th International Conference on Greenhouse Gas Control Technologies, GHGT-15 CY - Abu Dhabi, United Arab Emirates DA - 15.03.2021 KW - CCS KW - Corrosion KW - High alloyed steels PY - 2021 DO - https://doi.org/10.2139/ssrn.3812248 SP - 1 EP - 12 PB - SSRN CY - Rochester, NY AN - OPUS4-53140 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Wolf, Marcus A1 - Kranzmann, Axel T1 - Evaluating corrosion and corrosion fatigue behavior via laboratory testing techniques in highly corrosive CCS-environment N2 - In CCS environment (carbon capture and storage) pipes are loaded statically and/or cyclically and at the same time exposed constantly to the highly corrosive hot thermal water. Experimental procedures such as ambient pressure immersions tests, in-situ corrosion fatigue experiments using a flexibly designed corrosion chamber at ambient pressure and a specially designed corrosion chamber at high pressure. Experimental set-ups for push/pull and rotation bending load are introduced. The corrosion behavior and lifetime reduction of high alloyed steels (X46Cr13, 1.4043), (X5CrNiCuNb16-4, 1.4542) and (X2CrNiMoN22-5-3, 1.4462) is demonstrated (T=60 °C, geothermal brine: Stuttgart Aquifer flow rate: 9 l/h, CO₂). T2 - 15th International Conference on Greenhouse Gas Control Technologies, GHGT-15 CY - Abu Dhabi, United Arab Emirates DA - 15.03.2021 KW - Steel KW - Supercritical CO2 KW - Pipeline KW - Corrosion KW - CO2-storage PY - 2021 DO - https://doi.org/10.2139/ssrn.3812193 SP - 1 EP - 11 PB - SSRN CY - Rochester, NY AN - OPUS4-53142 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wiehle, Philipp A1 - Brinkmann, M. T1 - Tragfähigkeit von Lehmmauerwerk - Experimentelle und numerische Analyse T1 - Load-bearing capacity of earth masonry – An experimental and numerical analysis N2 - Die Bemessung von tragendem Lehmmauerwerk erfolgt in Deutschland auf Basis der Lehmbau Regeln. Das dort verankerte Nachweisverfahren beruht auf einem globalen Sicherheitskonzept, welches aus zuverlässigkeitstheoretischer Sicht nicht mehr dem Stand der Technik entspricht. Auf Grund dessen wird das Bemessungskonzept für Lehmmauerwerk vom Deutschen Institut für Bautechnik (DIBt) voraussichtlich 2023 außer Kraft gesetzt. Ein statischer Nachweis von tragenden Lehmbauten wäre in Deutschland dann ausschließlich mit einer Zustimmung im Einzelfall (ZiE) oder vorhabenbezogener Bauartgenehmigung (vBg) möglich. Beides ist mit erheblichem Mehraufwand und höheren Kosten verbunden, was für den Lehmmauerwerksbau einen entscheidenden Nachteil im Vergleich zum konventionellen Mauerwerksbau darstellt. Um eine unkomplizierte Praxisanwendung von Lehmmauerwerk zu ermöglichen, werden innerhalb eines Forschungsvorhabens, welches von der Bundesanstalt für Materialforschung und -prüfung (BAM), dem Institut für Massivbau der Technischen Universität Darmstadt sowie dem Ingenieurbüro ZRS durchgeführt wird, auf Basis der Produktnormen für Lehmsteine und Lehmmauermörtel Grundlagen für ein aktualisiertes Bemessungskonzept entwickelt. Im Rahmen des Projekts wird ebenfalls untersucht, inwiefern die Bemessungsregeln nach den vereinfachten Berechnungsmethoden für unbewehrtes Mauerwerk gemäß DIN EN 1996-3 / NA auf den Lehmmauerwerksbau übertragbar sind. Falls eine Anwendung des normativen Nachweisverfahrens bei Lehmmauerwerk möglich ist, wäre zukünftig eine Aufnahme von Lehmsteinen und Lehmmauermörtel in den nationalen Anhang des Eurocode 6 denkbar, was eine bedeutsame Erweiterung des Anwendungsbereichs von Lehmmauerwerk zur Folge hätte. Diverse wissenschaftliche Untersuchungen konnten zeigen, dass bemessungsrelevante Festigkeits- und Verformungseigenschaften von Lehmmauerwerksbaustoffen stark von der vorherrschenden Materialfeuchte abhängen, welche im hygroskopischen Wassergehaltsbereich im Wesentlichen von der relativen Luftfeuchte (RLF) bestimmt wird. Auch die Zwischenergebnisse des laufenden Forschungsvorhabens zur Entwicklung eines Bemessungskonzepts für Lehmmauerwerk ergaben eine deutlich erkennbare Abhängigkeit zwischen der Materialfeuchte und den relevanten Festigkeits- und Verformungseigenschaften. Eine detaillierte Kenntnis des feuchteabhängigen Materialverhaltens von Lehmsteinen, -mörtel und -mauerwerk ist zwingend erforderlich, um ein konsistentes und zuverlässiges Bemessungskonzept für Lehmmauerwerk zu entwickeln. Im Rahmen des laufenden Forschungsprojektes werden deshalb umfangreiche Versuche zum Drucktragverhalten von Lehmsteinen und -mörtel sowie Lehmmauerwerk nach Konditionierung bei unterschiedlichen RLF durchgeführt und analysiert. Weiterhin werden auf Basis der experimentellen Ergebnisse numerische Modelle kalibriert, welche die detaillierte Analyse der Biegedrucktragfähigkeit von Lehmmauerwerk ermöglichen. In diesem Beitrag werden zunächst die bisherigen Zwischenergebnisse bezüglich der experimentell ermittelten feuchteabhängigen Materialkennwerte von Lehmsteinen, -mörtel und -mauerwerk dargelegt. Darauf aufbauend werden numerische Untersuchungen zur Bestimmung der Systemtragfähigkeit von Lehmmauerwerk unter Feuchteeinflusses durchgeführt und erläutert. N2 - The structural design of load-bearing earthen masonry in Germany is based on the Lehmbau Regeln. The verification procedure outlined in these regulations is based on a global safety concept that no longer corresponds to the state of the art from a reliability theory perspective. As a result, the structural design concept for earthen masonry will most likely be discontinued by the German Institute for Building Technology (DIBt) in 2023. A structural verification of load-bearing earthen buildings would then only be possible in Germany with an approval for individual cases (ZiE) or a project-related permit type (vBg). Both methods are associated with considerable additional work and higher costs, which is a decisive disadvantage for earthen masonry construction compared to conventional masonry construction. In order to enable a straightforward practical application of earthen masonry, the Federal Institute for Materials Research and Testing (BAM), the Institute for Solid Construction of the Technical University of Darmstadt and ZRS Engineers are laying the groundwork for an updated structural design concept based on the product standards for earth blocks and earthen masonry mortar. The project will also investigate the extent to which the design rules based on the simplified calculation methods for unreinforced masonry according to DIN EN 1996-3 / NA can be transferred to earthen masonry construction. If the normative verification procedure can be applied to earthen masonry, it would be conceivable to include earth blocks and earthen masonry mortar in the national appendix of Eurocode 6 in the future, which would result in a significant expansion of the field of application of earthen masonry. Various scientific studies have shown that the strength and deformation properties of earthen masonry building materials relevant to structural design are strongly dependent on the prevailing material moisture level, which is essentially determined by the relative humidity (RH) in the hygroscopic water content range. The interim results of the current research project for the development of a structural design concept for earthen masonry also showed a clearly recognisable dependency between the material moisture level and the relevant strength and deformation properties. Detailed knowledge of the moisture-dependent material behaviour of earth blocks, earthen mortar and masonry is absolutely essential to developing a consistent and reliable structural design concept for earthen masonry. Within the framework of the current research project, extensive tests on the pressure load bearing capacity of earth blocks and earthen mortar as well as earthen masonry after conditioning at different RH levels are therefore being carried out and analysed. Furthermore, numerical models are being calibrated on the basis of the experiment results, which facilitate a detailed analysis of the bending pressure bearing capacity of earthen masonry. This paper presents, firstly, the interim results obtained so far concerning the experimentally determined moisture-dependent material characteristics of earth blocks, earthen mortar and masonry. Based on this material, numerical investigations for determining the system bearing capacity of earthen masonry under the influence of moisture are carried out and explained. T2 - LEHM 2020 CY - Weimar, Germany DA - 30.10.2020 KW - Lehm KW - Earth KW - Tragfähigkeit KW - Mauerwerk KW - Feuchte KW - Load-bearing KW - Moisture KW - Strength PY - 2020 SP - 1 EP - 12 PB - Dachverband Lehm CY - Weimar AN - OPUS4-53231 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wosniok, Aleksander A1 - Krebber, Katerina T1 - Distributed fiber optic radiation sensors N2 - In this work, we present our results achieved in several research activities for development of distributed fiber optic radiation sensors using glass and polymer optical fibers. The findings show that both the measurement of the radiation-induced attenuation (RIA) along the entire sensing fiber and the accompanying change in the refractive index of the fiber core can be used for distributed radiation monitoring. T2 - safeND CY - Online meeting DA - 10.11.2021 KW - Distributed fiber optic radiation sensors KW - Radiation-induced attenuation KW - Optical fiber sensor KW - Incoherent optical frequency domain reflectometry PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-537531 DO - https://doi.org/10.5194/sand-1-15-2021 VL - 1 SP - 15 EP - 16 AN - OPUS4-53753 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lecompagnon, Julien A1 - Ahmadi, Samim A1 - Hirsch, Philipp Daniel A1 - Rupprecht, C. A1 - Ziegler, Mathias ED - Kimata, M. ED - Shaw, J. A. ED - Valenta, C. R. T1 - Investigations on photothermal super resolution reconstruction using 2D-structured illumination patterns N2 - Active thermography as a nondestructive testing modality suffers greatly from the limitations imposed by the diffusive nature of heat conduction in solids. As a rule of thumb, the detection and resolution of internal defects/inhomogeneities is limited to a defect depth to defect size ratio greater than or equal to one. Earlier, we demonstrated that this classical limit can be overcome for 1D and 2D defect geometries by using photothermal laser-scanning super resolution. In this work we report a new experimental approach using 2D spatially structured illumination patterns in conjunction with compressed sensing and computational imaging methods to significantly decrease the experimental complexity and make the method viable for investigating larger regions of interest. T2 - Future Sensing Technologies Conference 2021 CY - Online meeting DA - 15.11.2021 KW - Thermography KW - Super resolution KW - NDT KW - Inspection KW - Image resolution PY - 2021 DO - https://doi.org/10.1117/12.2603838 VL - 11914 SP - 124 EP - 131 PB - International Society for Optics and Photonics. SPIE AN - OPUS4-53745 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lugovtsova, Yevgeniya A1 - Zeipert, H. A1 - Johannesmann, S. A1 - Nicolai, Marcel A1 - Prager, Jens A1 - Henning, B. T1 - К определению прочности клеевого соединения в многослойных материалах путем исследования областей расталкивания бегущих упругих волн T1 - Towards the determination of adhesive bonding strength of multi-layered materials by investigating guided wave mode repulsion N2 - Бегущие упругие волны часто используются в области неразрушающего контроля для определения механических характеристик материалов. Поскольку склеивание различных материалов является широко используемым методом в автомобильной и авиационной промышленности, необходима надежная система измерения для определения качества таких клеевых соединений. Дисперсионные кривые для многослойных волноводов при наличии клеевых прослоек характеризуются появлением эффекта расталкивания нормальных мод в тех областях, где соответствующие моды для отдельных материалов пересекались бы. Таким образом, в зависимости от качества клеевого соединения расстояние между этими модами изменяется. Используя комбинацию экспериментальных и численных данных, в настоящей работе представлен подход к определению параметра, указывающего на качество клеевого соединения. T2 - XXX Всероссийская школа-конференция МАТЕМАТИЧЕСКОЕ МОДЕЛИРОВАНИЕ В ЕСТЕСТВЕННЫХ НАУКАХ CY - Online meeting DA - 06.10.2021 KW - многослойный волновод KW - волны лэмбовского типа KW - контроль качества клеевого соединения PY - 2021 SP - 1 EP - 3 AN - OPUS4-53769 LA - rus AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - von Laar, C. A1 - Baar, C. A1 - Plarre, Rüdiger A1 - McMahon, Dino Peter T1 - Genetic relationships of local infestations by Anobium punctatum, Xestobium rufovillosum and their associated predator Korynetes caeruleus from buildings in North-Eastern Germany N2 - Wood-destroying pests such as Anobium punctatum and Xestobium rufovillosum cause damage to art and cultural objects as well as to buildings. Monitoring population dynamics of pest species as well as of their naturally occurring counterparts are an essential part in the development of biological control measures as alternatives to conventional wood protection. Therefore, both the dispersal and homogeneity of pest and beneficial insect populations across multiple sites and buildings were investigated in the present study using DNA barcoding. Specifically, beetles of Anobium punctatum (de Geer 1774) (Coleoptera, Ptinidae), Xestobium rufovillosum (de Geer, 1974) (Coloeptera, Ptinidae), and Korynetes caeruleus (de Geer 1775) (Coleoptera, Cleridae) were collected from buildings at four different sites in Mecklenburg-Western Pomerania, North-Eastern Germany. DNA analysis was performed using mitochondrial cytochrome c oxidase subunit I (COI). For A. punctatum, low base pair variability was found in the gene segment studied (4-5 SNPs) within one building (Greven) and between four spatially separated sites. Conversely, in X. rufovillosum, the sequences from two sites studied were homogeneous within a site but differed between locations by nine base pair positions (SNPs). The main result of this study is that the pests A. punctatum and X. rufovillosum showed a higher variability in the investigated gene segment than the natural counterpart K. caeruleus. T2 - IRG52 Webinar on Wood Protection CY - Online meeting DA - 01.11.21 KW - Anobium punctatum KW - Xestobium rufovillosum KW - Korynetes caeruleus KW - DNA barcode PY - 2021 SN - 2000-8953 VL - 21 SP - 1 EP - 11 PB - The International Research Group on Wood Protection CY - Stockholm, Sweden AN - OPUS4-54197 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja T1 - Vom Blended Learning zum Full Online – so einfach geht es nicht – Praxiserfahrungen zum Einsatz von Lehrfilmen N2 - Mit Beginn der Covid-19 Pandemie und dem damit verbundenen ausschließlichen Lehren im online-Format war die Hoffnung verbunden ein Blended Learning Lehrformat für die Studieeingangsphase ohne viel konzeptionelle Änderungen übertragen zu können. Der Kurs Werkstofftechnik als Grundlagenfach für den Maschinenbau baut sich auf inverted classroom Lehrszenarien auf, deren Lerngrundlage hierfür eigens produzierte und auf das Lernziel abgestimmte Lehrfilme und Lightboard-Vorlesungen darstellen. Im Kontext der Studieneingangsphase bieten audiovisuell stimulierende Lehrfilme umfassende Lernmedien, wenn sie analog der Lerninhalte einem technischen und didaktischen Qualitätsanspruch genügen. In der Praxis des SS2020 und WS2020/21 hat sich gezeigt, dass die Moderation und Durchführung eines online-Kurses sich deutlich von dem eins blended learning-Kurses unterscheidet. Um denselben Lernerfolg bei Studierenden zu erzielen, müs-sen Anforderungen viel genauer und detaillierter verfasst werden, Studierende enger und persönlicher begleitet werden und Lehrfilme und Lernmedien in einen Gesamtzusammenhang gestellt werden. Im Folgenden werden aus persönlicher Erfahrung heraus niederschwellige, zum Teil ungewöhnliche praktische Erfahrungen zur erfolgreichen Umsetzung von Lehrfilm-basierten inverted classroom Lehrszenarien zusammengefasst und im Hinblick auf die online-Lehre bewertet. T2 - 19. Fachtagung Bildungstechnologien (DELFI) CY - Bonn, Germany DA - 13.09.2021 KW - Inverted classroom KW - Lehrfilm KW - Lehrfilmformate KW - Online KW - Covid-19 PY - 2021 SP - 289 EP - 295 AN - OPUS4-54154 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja T1 - How flipped classroom teaching methods in first year studying succeed N2 - Flipping the classroom is a method to let students study on their own and then take time to discuss their questions and do extended hands-on lectures or exercises in class – or in the case of the covid-19 pandemic during plenary online sessions. First year mechanical engineering students use different teaching materials (mainly lecture videos, lightboard videos and micromodule lectures) to study from a distance and comprehend the principle underlying science in theory. Then the online plenary lectures offer the opportunity to apply their knowledge and transfer different scientific aspects of the course to get the bigger picture. Exercises, worked solutions, selfassessed tests and peer-instruction during present time help students to check on their learning progress. However, the self-study periods and (online) plenary sessions need to be guided carefully. To meet the course learning outcome and overcome the diversity of a first year class various practical leads have to be fulfilled to turn flipped classroom teaching into success. T2 - 7th International Conference on Higher Education Advances (HEAd’21) CY - Valencia, Spain DA - 20.06.2021 KW - Inverted classroom KW - Flipped classroom KW - Online teaching KW - Lecture videos KW - First year students PY - 2021 DO - https://doi.org/10.4995/HEAd21.2021.12792 SP - 1211 EP - 1219 AN - OPUS4-54156 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krietsch, Arne A1 - Reyes Rodriguez, M. A1 - Kristen, A. A1 - Kadoke, D. A1 - Abbas, Z. A1 - Krause, U. T1 - Ignition temperatures and flame velocities of metallic nanomaterials N2 - The production of materials with dimensions in the nanometre range has continued to increase in recent years. In order to ensure safety when handling these products, the hazard potential of such innovative materials must be known. While several studies have already investigated the effects of explosions (such as maximum explosion pressure and maximum pressure rise) of powders with primary particles in the nanometre range, little is known about the ignition temperatures and flame velocities. Therefore, the minimum ignition temperature (MIT) of metallic nano powders (aluminium, iron, copper and zinc) was determined experimentally in a so called Godbert-Greenwald (GG) oven. Furthermore, the flame velocities were determined in a vertical tube. In order to better classify the test results, the tested samples were characterised in detail and the lower explosion limits of the tested dust samples were determined. Values for the burning velocity of aluminium nano powders are higher compared to values of micrometre powders (from literature). While MIT of nanometre aluminium powders is within the range of micrometre samples, MIT of zinc and copper nano powders is lower than values reported in literature for respective micrometre samples. T2 - 13th Symposium International Symposium on Hazards, Prevention and Mitigation of Industrial Explosions (ISHPMIE) CY - Online meeting DA - 27.07.2021 KW - Dust explosions KW - Nanomaterial KW - Flame propagation KW - Minimum ignition temperature PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-540930 DO - https://doi.org/10.7795/810.20200724 SP - 591 EP - 605 PB - Physikalisch-Technische Bundesanstalt AN - OPUS4-54093 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krietsch, Arne A1 - Krause, U. A1 - Gabel, D. A1 - Abbas, Z. A1 - Dufaud, O. T1 - Quasi-static dispersion of dusts for the determination of lower explosion limits of hybrid mixtures N2 - Knowledge of explosion limiting concentration of explosible materials is necessary for the design of explosion protection measures. Currently employed methods of testing MEC of a dust cloud or LEL of a hybrid mixture are based on arbitrary assumptions and possess technical limitations that often lead to values of MEC/LEL, which are unrealistically low or poorly reproducible. This contribution presents an improved method for experimental determination of MEC of a combustible dust cloud or LEL of a flammable gas or hybrid mixture. The new set-up operates under laminar conditions and allows a uniform suspension of dust particles in an open top acrylic glass tube. Dust concentration is measured with the help of infrared sensors installed a few centimeters above and below the ignition source. In order to evaluate the dependence of MEC on flow front velocity, MEC of lycopodium was determined at four flow velocities. The results show that the flow field intensity does not significantly influence the MEC of lycopodium for the flow ranges tested in this work. Moreover, LEL of hybrid mixtures of lycopodium and methane was also tested at flow velocities of 4.7 cm/s, 5.8 cm/s, 7 cm/s and 11 cm/s and compared with the values obtained from other sources. The results suggest that the requirement of high energy pyrotechnical igniter may be relinquished, provided that a truly homogeneous suspension of dust particles could be achieved. Moreover, the effect of relative amount of dust and gas, on the course of ignition and flame propagation in hybrid mixtures at their LEL, was studied by the help of high speed videos. For hybrid mixtures of carbonaceous dusts (like lycopodium) at their LEL, ignition occurs in the gas phase, however, flame propagation is only possible through a two-way interaction of dust and gas during the course of combustion. T2 - 13th Symposium International Symposium on Hazards, Prevention and Mitigation of Industrial Explosions (ISHPMIE) CY - Online meeting DA - 27.07.2020 KW - Dust explosions KW - Gas explosions KW - Lower explosion limit KW - Hybrid mixtures PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-540955 DO - https://doi.org/10.7795/810.20200724 SP - 750 EP - 764 PB - Physikalisch-Technische Bundesanstalt AN - OPUS4-54095 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schnur, C. A1 - Moll, J. A1 - Lugovtsova, Yevgeniya A1 - Schütze, A. A1 - Schneider, T. T1 - Explainable machine learning for damage detection - In carbon fiber composite plates under varying temperature conditions N2 - Understanding on how a machine learning model interprets data is a crucial step to verify its reliability and avoid overfitting. While the focus of the scientific community is nowadays orientated towards deep learning approaches, which are considered as black box approaches, this work presents a toolbox that is based on complementary methods of feature extraction and selection, where the classification decisions of the model are transparent and can be physically interpreted. On the example of guided wave benchmark data from the open guided waves platform, where delamination defects were simulated at multiple positions on a carbon fiber reinforced plastic plate under varying temperature conditions, the authors could identify suitable frequencies for further investigations and experiments. Furthermore, the authors presented a realistic validation scenario which ensures that the machine learning model learns global damage characteristics rather than position specific characteristics. T2 - 48th Annual Review of Progress in Quantitative Nondestructive Evaluation CY - Online meeting DA - 28.07.2021 KW - Explainable machine learning KW - Guided waves KW - Damage detection KW - Structural health monitoring KW - Composite structures PY - 2021 SN - 978-0-7918-8552-9 DO - https://doi.org/10.1115/QNDE2021-75215 SP - 1 EP - 6 PB - American Society of Mechanical Engineers (ASME) CY - New York, NY AN - OPUS4-54219 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wachtendorf, Volker A1 - Schartel, Bernhard A1 - Lin, Xuebao A1 - Tan, Yi A1 - Schoch, R. A1 - Lang, M. A1 - Tröppner, O. A1 - Bosse, M. ED - Ziegahn, K.-F. T1 - Untersuchung der Witterungsbeständigkeit komplexer Funktionalitäten von Polymerwerkstoffen durch künstliche Bewitterung: Flammschutz N2 - In den letzten Jahrzehnten wurde die Degradation der polymeren Matrix von flammgeschützten Polymeren eingehend untersucht. Erst in den letzten Jahren jedoch hat sich die Frage der Lebensdauer der Funktionalität des Flammschutzes selbst als wichtige Fragestellung herauskristallisiert, z.B. bei Kabeln. Deshalb sollte diese Fragestellung durch systematisch-variierte künstliche Klima- und Bewitterungstests an flammgeschützten Polymerwerkstoffen untersucht werden. T2 - 50. Jahrestagung der Gesellschaft für Umweltsimulation (GUS) CY - Online meeting DA - 23.03.2022 KW - Flammschutz, Witterungsbeständigkeit, Langzeitbeständigkeit, UV, E&E PY - 2022 SN - 978-3-9818507-7-2 VL - 50 SP - 143 EP - 148 CY - Pfinztal (Berghausen) AN - OPUS4-54543 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Beckmann, M. A1 - Danz, P. A1 - Deike, R. A1 - Dornack, C. A1 - Gehrmann, H.-J. A1 - Gleis, M. A1 - Hölemann, K. A1 - Karpf, R. A1 - Pieper, C. A1 - Quicker, P. A1 - von Raven, R. A1 - Seifert, H. A1 - Simon, Franz-Georg T1 - Positionspapier - Abfallverbrennung in der Zukunft N2 - Die Autoren zeigen dazu die gesetzlichen und energiepolitischen Rahmenbedingungen und Perspektiven auf, widmen sich in aktuellen Beiträgen zur Verfahrenstechnik der thermischen Abfallbehandlung sowohl den thermischen Hauptverfahren als auch der Abgasreinigung und gehen auf das Thema Wertstoffrückgewinnung ein. Ihr Fazit: Durch Anstrengungen, das stoffliche Recycling weiter zu optimieren, können künftig weitere Kreisläufe von Produkten und Materialien hochwertig geschlossen werden. Für manche Abfallströme wird dies aber aus verschiedenen Gründen nicht möglich sein – hier bleibt die thermische Abfallbehandlung unverzichtbar. KW - Rostasche KW - Abfallverbrennung PY - 2022 UR - https://dechema.de/Medien/Studien+und+Positionspapiere/2022+03+Abfallverbrennung.html SP - 1 EP - 52 PB - DECHEMA CY - Frankfurt/M. AN - OPUS4-54510 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Kudela, P. A1 - Radzienski, M. A1 - Moix-Bonet, M. A1 - Willberg, C. A1 - Lugovtsova, Yevgeniya A1 - Bulling, Jannis A1 - Tschöke, K. A1 - Moll, J. T1 - Dataset on full ultrasonic guided wavefield measurements of a CFRP plate with fully bonded and partially debonded omega stringer N2 - The fourth dataset dedicated to the Open Guided Waves platform presented in this work aims at a carbon fiber composite plate with an additional omega stringer at constant temperature conditions. The dataset provides full ultrasonic guided wavefields. A chirp signal in the frequency range 20-500 kHz and Hann windowed tone-burst signal with 5 cycles and carrier frequencies of 16.5 kHz, 50 kHz, 100 kHz, 200 kHz and 300kHz are used to excite the wave. The piezoceramic actuator used for this purpose is attached to the center of the stringer side surface of the core plate. Three scenarios are provided with this setup: (1) wavefield measurements without damage, (2) wavefield measurements with a local stringer debond and (3) wavefield measurements with a large stringer debond. The defects were caused by impacts performed from the backside of the plate. As result, the stringer feet debonds locally which was verified with conventional ultrasound measurements. The dataset can be used for benchmarking purposes of various signal processing methods for damage imaging. The detailed description of the dataset is published in Data in Brief Journal. KW - Open data KW - Ultrasonic guided waves KW - Experimental data PY - 2021 DO - https://doi.org/10.5281/zenodo.5105861 PB - Zenodo CY - Geneva AN - OPUS4-54504 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Rühl, Karl H. T1 - Möglichkeiten und Grenzen der experimentellen Spannungsanalyse N2 - Der Zweck der Dehnungsmessungen ist es in vielen Fällen, aus der Dehnung die zu erwartende Sicherheit eines Baukörpers zu ermitteln. Dazu müssen aus den Dehnungen über die Spannungen die Lasten bestimmt werden. Die Spannungsdehnungslinie des Werkstoffes ist aber von zahlreichen Parametern, wie Belastungsdauer, Beanspruchungsgeschwindigkeit, Spannungszustand, Eigenspannungen, abhängig. Zur Deutung von Dehnungsmessungen muß die Vielfalt der Spannungsdehnungslinien einschließlich ihrer Endpunkte bekannt sein. Die Dehnungsmessung kann hierfür einen Teil, aber nicht die Gesamtheit der notwendigen Parameter liefern. Die Feststellung der Spannungsdehnungskurve mit ihrer Hilfe ist Sache der Tragfähigkeitsforschung. Die hier zu lösenden Fragen, z.B. Bedeutung der Dehnungen im Atomgitter, Abhängigkeit der Verformungsfähigkeit vom Spannungszustand, Einfluß des Spannungsgefälles, der Beanspruchungsgeschwindigkeit usw., gehören zu den z.Z. wichtigsten Fragen der Werkstoffmechanik und Tragfähigkeitsforschung. Tragfähigkeitsforschung und Dehnungsmeßtechnik sind daher in ihrer Entwicklung gegenseitig voneinander abhängig. PY - 1952 SP - 1 EP - 20 PB - Materialprüfungsamt CY - Berlin AN - OPUS4-54522 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Kuntze, Wilhelm T1 - Weitere praktische Ausbeutung der Ergebnisse der Kerbschlagzugprüfung in der Sicherheitsfrage der Baustähle auf Grund der Sprödbruchtheorie N2 - Wenn man eine Kerbzugprobe im Pendelhammer zerschlägt und eine gleiche Probe in der Zerreißmaschine zu Bruch bringt, dann gibt der Quotient aus beiden gemessenen Brucheinschnürungen vollständigen Aufschluß über die Sprödigkeitsgrenzen des Werkstoffes, als Folge von Temperatur, Belastungsgeschwindigkeit und Spannungszustand. Die Sprödigkeitsgrenze ist dadurch gekennzeichnet, daß die Elastizität vollständig unterbunden ist. Man ermittelt die Sprödigkeitsgrenze, indem man das Plastizitätsgefälle in Abhängigkeit von einem der genannten Einflüsse feststellt. Geschieht dies in Abhängigkeit von der Temperatur, so treten große Versuchsstreuungen auf, die insbesondere bei tiefen Temperaturen und im Abfallgebiet der Zähigkeit sehr groß werden. Wird dagegen bei konstanter Raumtemperatur die Belastungsgeschwindigkeit variiert und das Plastizitätsgefälle durch Brucheinschnürungsmessungen festgestellt, dann sind die Ergebnisse so gut wie fehlerfrei. Daß man hierbei mit nur zwei Einschnürungsmessungen auskommt, hat seine Begründung in der Eindeutigkeit des Sprödigkeitsgesetzes. Es läßt keine vielseitigen Variationen aus der vier Bedingungen: Stoff, Temperatur, Geschwindigkeit und Spannungszustand zu, sondern seine gesetzmäßigen Möglichkeiten sind nur durch einen Punkt des vierdimensionalen Diagramms festgelegt. Diese empirische Entdeckung war die Folge der Versuchsauswertungen im obigen Bericht. Der Spannungszustand ist die für den Baustatiker wichtigste Bedingung. Sein Einfluß auf den Sprödbruch läßt sich auf das einfache Verhältnis der linearen Streckgrenze σ(S) zur Normalspannung σ(NF) im tragenden Querschnitt bei Fließeintritt zurückführen. Dieses Verhältnis ist - wenn es nicht unmittelbar experimentell gemessen werden kann - aus den räumlichen Spannungszuständen und der Spannungsverteilung zu entwickeln. Daß die Reduzierung beliebiger räumlicher Kräfte auf die drei Hauptspannungen und die Reduzierung dieser auf eine in gewünschter haupttragender Richtung schwierig oder auch noch nicht gelöst ist, wenn die primär angreifenden Kräfte mit einer ungleichmäßigen Spannungsverteilung behaftet sind, ist Künstlerpech der Elastostatik. Seitens der Physik, Werkstoffmechanik und Werkstoffprüfung kann das Problem des Sprödbruches als gelöst angesehen werden. Aber selbst, wenn solche präzisen Feststellungen nicht möglich sind, ist eine Einordnung des Spannungsquotienten σ(S)/σ(NF) in die von 0 bis 1 (linearer Zustand) reichende Skala leicht abschätzbar, innerhalb welcher die vorliegende Kerbzugprobe mit 0,33 zu beziffern ist. Dieser umfassende Erfolg der Kerbschlagzugprüfung ist auf die Verbindung zwischen Versuchspraxis und Theorie zurückzuführen, die eine Folge der Kreissymmetrie der Probenform und der Einschnürungsmessung ist. Etwa aus diesen Gründen das Verfahren als umständlich oder schwierig anzusehen, entbehrt der Berechtigung, da sich die praktische Prüfung neben ihrer Exaktheit als einfacher herausstellt als die gealterte Kerbschlagbiegeprobe. Keines der z.Zt. zur Diskussion stehenden Sprödigkeitsprüfverfahren erlaubt so weitgreifende Auswertungen der Versuchsergebnisse. Insbesondere sind die auf Biegung beanspruchten unsymmetrischen Probenformen mit Schlagarbeitsmessung nicht geeignet, eine Theorie so unmittelbar in die Wirklichkeit umzusetzen und man ist mit ihnen aufs Probieren angewiesen. Wenn man heute die Kerbschlagbiegezähigkeit künstlich gealterter Stähle als Maßstab für die Sprödigkeitsneigung einführen möchte, so läßt sich - ohne erst ausprobieren zu müssen - auf Grund theoretischer Erkenntnis sagen, daß sich die Stähle hinsichtlich ihres Alterungseffektes überhaupt nicht differentieren, da alle eine etwa gleich große Schädigung erfahren, die in einer Verschiebung der kritischen Geraden um etwa +70°C besteht. Wenn also die Kerbzähigkeit gealterter Stähle eine Differentierung erfährt, so nur deshalb, weil schon vor der künstlichen Alterung die kritische Gerade eine ungünstige Lage hatte. Das läßt sich aber ohne die Umständlichkeit des künstlichen Alterns mit der Kerbzugprobe ermitteln. Im übrigen werden im obigen Bericht die Unsicherheiten und die starken Streuungen der Kerbschlagbiegezähigkeit im gealterten Zustand erläutert, die darauf zurückzuführen sind, daß dieser Begriff kein so reiner Ausdruck für die Sprödigkeitsgrenzen wie der Brucheinschnürungsquotient ist, sondern Einflüsse enthält, die mit der Sprödigkeitsgrenze nichts zu tun haben. PY - 1953 VL - Bericht 11/53 SP - 1 EP - 26 PB - Materialprüfungsamt CY - Berlin AN - OPUS4-54491 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pfender, Max T1 - Dr.-Ing. Hans Umstätter zum Gedenken N2 - Nachruf auf Dr.-Ing. Hans Umstätter, der seit 1949 bis zu seinem Tode als wissenschaftlicher Mitarbeiter in der Bundesanstalt für Materialprüfung in Berlin-Dahlem tätig war und dort die von ihm begründete Fachgruppe Rheologie leitete. PY - 1957 SN - 0374-0838 IS - Frühjahr 1957 SP - 1 EP - 18 PB - Deutsche Rheologische Gesellschaft CY - Berlin AN - OPUS4-54282 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Muschalla, Rudolf T1 - Menschliche Werte im Zeitalter der Automation PY - 1957 SN - 0009-5788 VL - 46 IS - 5 SP - [1] EP - [8] PB - Katholischer Deutscher Frauenbund CY - Köln AN - OPUS4-54283 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Zehr, Joachim T1 - Die experimentelle Bestimmung der oberen Zündgrenze von Staub/Luft-Gemischen als Beitrag zur Beurteilung der Staubexplosionsgefahren N2 - In der vorliegenden Arbeit ist nach Hinweisen auf die Bedeutung auch der oberen Zündgrenze für Sicherheit und Arbeitsschutz in durch Staubexplosionen gefährdeten Betrieben und auf die bisher relativ geringen Kenntnisse zu diesem Problem eine Apparatur geschildert, mit der serienmäßige Untersuchungen an vielen brennbaren Stäuben durchführbar sind, und das zugehörige Auswerteverfahren angegeben worden. Die Methode beruht im Prinzip darauf, daß das reaktionsfähige System im Bereich der oberen Zündgrenze in komprimiertem Zustand und dadurch mit besserer Handhabungsmöglichkeit untersucht wird. Eine Reihe von Ergebnissen wurde mitgeteilt und an Hand dieser die Anwendbarkeit der Methode diskutiert. Der abschließende Teil behandelte zusammengefaßt Sicherheitsmaßnahmen mit besonderen Hinweisen für einige praktische Fälle. PY - 1959 SP - 1 EP - 24 PB - Technische Universität CY - Berlin AN - OPUS4-54284 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Kuntze, Wilhelm T1 - Beschreibung des Prüfverfahrens zur Ermittlung der Sprödigkeitsneigung von Metallen in Kerbzug- und Kerbschlagversuchen N2 - Die Becker-Orowan-Kockendörfersche Plastizitätstheorie bildet eine anschauliche Grundlage für die Sprödigkeitsbedingungen. Danach sind für den Eintritt des Sprödbruches außer den Materialeigenschaften drei äußere Faktoren maßgebend: Temperatur, Belastungszeit und Spannungszustand (Gestalt). Um den Sprödbruch herbeizuführen, braucht man nur einen dieser drei Faktoren genügend zu verschärfen. Diesen Umstand macht sich die Materialprüfung zu Nutze, indem z.B. bei der Kerbschlagbiegeprobe Schlaggeschwindigkeit und Probenform unveränderlich bleiben und nur die Temperatur soweit erniedrigt wird, bis der Sprödbruch erfolgt. Die so ermittelte "Übergangstemperatur" ist - obgleich sie nur für diese speziellen Zeit- und Gestaltverhältnisse Gültigkeit hat - ein guter Vergleichsmaßstab für verschiedene Werkstoffe. Nun ist aber die Prüfung bei veränderlichen, insbesondere niedrigen Temperaturen sehr umständlich. Deshalb wird bei dem hier beschriebenen Prüfverfahren nicht die Temperatur, sondern die Belastungszeit verändert. Infolge der achsen-symmetrischen Einkerbung und der daraus folgenden Möglichkeit, die Brucheinschnürung sehr einfach zu messen, kommt man mit nur zwei Geschwindigkeitsstufen aus, weil das zwischen beiden liegende meßbare Zähigkeitsgefälle für die Beurteilung der Sprödigkeitsneigung ausreicht, vorausgesetzt, daß man sich nahe der Sprödigkeitsgrenze befindet ohne aber die wirkliche Sprödbruchgrenze erreichen zu müssen. PY - 1953 VL - Bericht 5/53 SP - 1 EP - 13 PB - Materialprüfungsamt CY - Berlin AN - OPUS4-54285 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Tang, Chi-Long A1 - Wilke, Olaf A1 - Seeger, Stefan A1 - Kalus, Sabine A1 - Erdmann, Kerstin T1 - Chemical characterization of ultrafine particles released from 3D printers N2 - Previous studies have shown that desktop 3D printers (Fused Filament Fabrication) emit high numbers of particulate matter, mainly as ultrafine particles (UFP, particle diameter less than 100 nm). However, the chemical composition of emitted particles has been less extensively investigated. In this study, we therefore focused on the chemical composition of particles emitted from 3D printing. The measurements were conducted in a 1 m³ emission test chamber. Emitted particles were sampled by a 13-stage low-pressure cascade impactor onto aluminum foils and then analyzed by TD-GC/MS to identify their organic compounds. Nine commercial filaments made from basic polymers such as Acrylonitrile Butadiene Styrene (ABS), Acrylonitrile Styrene Acrylate (ASA), Polycarbonate (PC), Poly(methyl methacrylate) (PMMA), Nylon, High Performance Polystyrene (HIPS) and a copper-filled Polylactide (PLA) were investigated. The results show that the organic components of the particles are primarily plastic additives such as plasticizer, antioxidant agents, lubricants, UV-absorbers and UV-stabilizers from the filaments. T2 - 17th International Conference Healthy Buildings Europe 2021 CY - Online Meeting DA - 21.06.2021 KW - Chemical characterization KW - FFF-3D-Printer KW - UFP KW - Chamber measurement PY - 2021 SP - 251 EP - 252 AN - OPUS4-54255 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Erenberg, Marina T1 - Analyse des Brandverhaltens von Stoßdämpfern für Behälter zum Transport radioaktiver Stoffe N2 - Stoßdämpfer, die zum Schutz von Behältern zum Transport radioaktiver Stoffe eingesetzt werden und welche häufig aus von Stahlblech ummantelten, geschichtetem Holz bestehen, reduzieren bei einem etwaigen Unfall die auf den Behälterkörper wirkende mechanische Belastung erheblich. In Zulassungsverfahren muss die Sicherheit der jeweiligen Behälterkonstruktion nachgewiesen werden, wobei u. a. der Nachweis erbracht werden muss, dass die Behälter definierten Prüfbedingungen widerstehen. Diese beinhalten Aufprallsequenzen aus verschiedenen Höhen und Positionen sowie ein anschließendes das Versandstück 30 min lang allumhüllendes Feuer bei 800°C. Falls Stoßdämpfer infolge der 30-minütigen Feuerbeanspruchung in Brand geraten, dürfen diese unter den Prüfbedingungen nicht gelöscht werden. Die Auswirkungen auf die Sicherheit des Behälters sind hierbei zu untersuchen. Das ist die Basis für die in dieser Arbeit durchgeführten Untersuchungen zum Brandverhalten von stahlblechumkapselten Holzstrukturen mit dem Ziel der Bewertung der daraus resultierenden zusätzlichen thermischen Belastung auf den Behälter. Ein wesentlicher Bestandteil war die Durchführung eines Großbrandversuchs, bei dem ein originalgroßer Stoßdämpfer auf dem Brandprüfstand während einer 30-minütigen Feuerphase entzündet wurde. Der Stoßdämpfer hatte ein Volumen von 3m³ und war mit aus den Prüfbedingungen resultierenden Vorschädigungen versehen. Es wurde ein Prüfstand zur Messung der variablen Wärmeleistung des brennenden Stoßdämpfers entwickelt. Die Wärme wird dabei in den Energieaufnahmebehälter (EAB) eingetragen. Aufgrund der entwickelten Temperaturregelung konnte die Wärmeleistung mit geringen Messfehlern bestimmt werden. Dabei wurde der EAB um maximal 10 K erwärmt. Im Großbrandversuch wurde gezeigt, dass der vorgeschädigte Stoßdämpfer 72 h lang brannte und dass eine signifikante Wärmeleistung in den EAB eingetragen wurde. Die während des Stoßdämpferbrands erzeugte Energie betrug ein Vielfaches im Vergleich zur Wärmeleistung, die allein durch das IAEA-Feuer eingetragen wird. Temperaturen von bis zu 1100°C wurden erreicht. Im Versuch wurde Flammenschlagen im Stoßdämpferinnern und das Glühen der Stoßdämpferstahlblechummantelung beobachtet. Bewusst dessen, dass ein einzig durchgeführter Brandversuch nur unzulängliche Aussagekraft hat, um das Brandverhalten von Stoßdämpfern zu beschreiben, wurde in weiteren Kleinbrandversuchen die Parameterabhängigkeit beim Brand von stahlblechumkapselten Holzstrukturen untersucht. Dafür wurde das Brandverhalten von 8 zylinderförmigen 0,07m³ großen Probekörpern bei variabler Schadstellengröße getestet. In der Bewertung der Kleinbrandversuche konnte gezeigt werden, dass eine kritische Schadstellengröße existiert und welche Streubreite in den Kleinbrandversuchen vorliegt. Die Kleinbrandversuche können damit Aufschluss darüber geben, welche Abweichungen in weiteren Großbrandversuchen zu erwarten wären. KW - Stoßdämpfer KW - Holz KW - Brand PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:gbv:ma9:1-1981185920-397479 DO - https://doi.org/10.25673/39100 SP - 1 EP - 154 PB - Otto-von-Guericke-Universität Magdeburg CY - Magdeburg AN - OPUS4-54263 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nehrig, Marko A1 - Scheidemann, Robert A1 - Wille, Frank A1 - Ballheimer, Viktor T1 - Investigation of the internal impact during a 9 m drop test of an accident-safe waste package N2 - The safety assessment of packages for the transport of radioactive material follows the IAEA regulations and guidance. The specified regulatory tests cover severe accidents and demonstrate the package containment system integrity. Special attention must be drawn to the behaviour of the content which could move inside the package due to unpreventable gaps caused by the loading procedure and the structure of the content. A possible internal impact of the content which occurs during the drop tests onto the lid system is investigated. The IAEA regulations SSR-6 and the Guidance SSG-26, revised recently, consider input from Germany and France related to the significance of internal gaps. In the context of a waste package design assessment, a model was equipped with a representative content to conduct a drop test with an internal impact. The weight and kinetic impact of this content covered all possible real contents. The objective of the test was to maximize the load onto the lid system and to prove the mechanical integrity by complying with the required leak tightness. The test was conducted conservatively at a package temperature lower than -40 °C at the BAM Test Site Technical Safety. This paper gives an overview of efforts to address internal gaps and their consequences, and the BAM efforts with the implementation of this topic into IAEA regulations and guidance material. The paper then focuses on the conduction of a drop test and investigation of internal component impact. T2 - ASME 2021 Pressure Vessels & Piping Conference (PVP2021) CY - Online meeting DA - 13.07.2021 KW - Internal gaps KW - Drop test KW - IAEA PY - 2021 SN - 978-0-7918-8535-2 DO - https://doi.org/10.1115/PVP2021-60996 SP - 1 EP - 6 PB - American Society of Mechanical Engineers (ASME) CY - New York, NY, USA AN - OPUS4-54742 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Meier, Karl T1 - Kunststoffe im Bauwesen - Ein Verzeichnis von Kunststoff-Erzeugnissen für das Bauwesen N2 - In den letzten Jahren hat die Verwendung von Kunststoffen im Bauwesen einen erheblichen Aufschwung genommen. Hierbei hat nicht nur der Umsatz, sondern auch der Verwendungsumfang von Jahr zu Jahr zugenommen, was nicht zuletzt seine Ursache in den Variationsmöglichkeiten der Eigenschaften von Kunststoffen hat. So befindet sich eine Vielzahl von Kunststoff-Erzeugnissen für das Bauwesen mit unterschiedlichen Eigenschaften auf dem Markt. Um Bauherren, Bauträgern und Architekten eine Übersicht über geeignete Kunststoff-Erzeugnisse und ihre technischen Anwendungsmöglichkeiten im Bauwesen zu geben, ist vom Bundesministerium für Wohnungswesen, Städtebau und Raumordnung die Aufstellung eines Verzeichnisses „Kunststoffe im Bauwesen“ angeregt worden. Dieses Verzeichnis soll die Anwendung von solchen Kunststoff-Erzeugnissen erleichtern, die sich als geeignet und bewährt herausgestellt haben. Dadurch wird indirekt eine Steigerung der Güte, der baulichen Ausführung und Wohnungsausstattung ermöglicht, überdies wird das Kunststoff-Verzeichnis dazu beitragen, Vorurteile gegen die Verwendung von Kunststoffen zu beseitigen. Das Verzeichnis hat keinerlei amtlichen Charakter, wobei jedoch angenommen wird, das sich auch amtliche Stellen des Verzeichnisses bedienen werden. Es enthält keine Preisangaben. PY - 1963 IS - 2/1963 SP - 5 EP - 6 PB - Gesamtverband kunststoffverarbeitende Industrie (GKV) CY - Frankfurt am Main AN - OPUS4-54654 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Müller, Anja T1 - Determination of the actual morphology of core-shell nanoparticles by advanced X-ray analytical techniques: A necessity for targeted and safe nanotechnology N2 - Even though we often do not knowingly recognize them, nanoparticles are present these days in most areas of our daily life, including food and its packaging, medicine, pharmaceuticals, cosmetics, pigments as well as electronic products, such as computer screens. The majority of these particles exhibits a core-shell morphology either intendedly or unintendedly. For the purpose of practicability, this core-shell nanoparticle (CSNP) morphology is often assumed to be ideal, namely a spherical core fully encapsulated by a shell of homogeneous thickness with a sharp interface between core and shell material. It is furthermore widely presumed that all nanoparticles in the sample possess the same shell thickness. As a matter of fact, most real CSNPs deviate in several ways from this ideal model with quite often severe impact on how efficiently they perform in a specific application. The topic of this cumulative PhD thesis is the accurate characterization of the actual morphology of CSNPs by advanced X-ray analytical techniques, namely X-ray photoelectron spectroscopy (XPS) and scanning transmission X-ray microscopy (STXM). A special focus is on CSNPs which deviate from an ideal core-shell morphology. In the paper from 2019 nanoparticle shell thicknesses are extracted from the elastic-peak intensities in an XPS spectrum based on an ideal particle morphology. This happens for a series of CSNP samples comprising a poly(tetrafluoroethylene) (PTFE) core and either a poly(methyl methacrylate) (PMMA) or polystyrene (PS) shell. The same paper as well as the paper from 2020 demonstrate for the first time, that the analysis of the inelastic background in an XPS spectrum of CSNPs can identify and quantify the heterogeneity of the shell and the incomplete encapsulation of the core. The result from an XPS experiment is always an average across a large nanoparticle ensemble. Deviations from an ideal morphology within a single particle of the sample cannot be assessed separately. As opposed to that, a spatial resolution of 35 nm enables STXM to visualize the interior of single CSNPs which exhibit a sufficient X-ray absorption contrast between core and shell material. In the paper from 2018 a STXM analysis is demonstrated based on the example of the PTFE-PS CSNP samples already mentioned in the previous paragraph. In the publication from 2021 (Ca/Sr)F₂ core-shell like nanoparticle ensembles for the practical use in, among others, antireflective coatings are investigated. These nanoparticles do not possess a sharp interface between core and shell material, which is why a shell thickness determination as described in the second paragraph is inappropriate. Instead, in-depth profiles of the chemical composition are obtained by XPS experiments based on synchrotron radiation with variable X-ray photon energy to elucidate the internal morphology of the particles. Additionally, theoretical in-depth profiles of Ca and Sr XPS peak intensities are simulated, in order to facilitate the interpretation of the experiments. Thus, an enrichment of CaF₂ at the particle surface was determined, which could hardly have been assessed by any other analytical technique. Because this kind of non-destructive depth profiling by XPS is very demanding, more than usual effort is spent on gapless documentation of the experiments to ensure full reproducibility. Due to the vast diversity of nanoparticles differing in material, composition and shape, a measurement procedure cannot unalteredly be transferred from one sample to another. Nevertheless, because the papers in this thesis present a greater depth of reporting on the experiments than comparable publications, they constitute an important guidance for other scientists on how to obtain meaningful information about CSNPs from surface analysis. N2 - Obwohl wir sie oft nicht bewusst wahrnehmen, sind Nanopartikel heutzutage in den meisten Bereichen unseres Alltags präsent, unter anderem in Lebensmitteln und ihren Verpackungen, Medizin, Medikamenten, Kosmetik, Pigmenten und in elektronischen Geräten wie Computermonitoren. Ein Großteil dieser Partikel weist, beabsichtigt oder unbeabsichtigt, eine Kern-Schale Morphologie auf. Einfachheitshalber wird diese Morphologie eines Kern-Schale-Nanopartikels (CSNP) oft als ideal angenommen, d.h. als ein sphärischer Kern, der komplett von einer Schale homogener Dicke bedeckt ist, mit einer scharfen Grenzfläche zwischen Kern- und Schalenmaterial. Außerdem wird vielfach auch davon ausgegangen, alle Partikel der Probe hätten gleiche Schalendicken. Tatsächlich weichen die meisten realen CSNPs in verschiedenster Weise von diesem Idealmodell ab, mit oft drastischen Auswirkungen darauf, wie gut sie ihre Aufgabe in einer bestimmten Anwendung erfüllen. Das Thema dieser kumulativen Doktorarbeit ist die exakte Charakterisierung der wirklichen Morphologie von CSNPs mit modernen Röntgen-basierten Methoden, konkret Röntgen-Photoelektronen-Spektroskopie (XPS) und Raster-Transmissions-Röntgen-Mikroskopie (STXM). Der Fokus liegt insbesondere auf CSNPs, die von einer idealen Kern-Schale-Morphologie abweichen. Im Artikel von 2019 werden Schalendicken von Nanopartikeln aus den elastischen Peakintensitäten im XPS-Spektrum unter Annahme einer idealen Partikelmorphologie abgeleitet. Dies geschieht für eine Reihe von CSNP-Proben, welche aus einem Polytetrafluoroethylen- (PTFE) Kern und entweder einer Polymethylmethacrylat- (PMMA) oder Polystyrol- (PS) Schale bestehen. Sowohl dieser Artikel als auch der von 2020 zeigen erstmals, dass die Auswertung des inelastischen Untergrunds eines CSNP-XPS-Spektrums in der Lage ist, die Heterogenität der Schale und die unvollständige Ummantelung des Kerns zu identifizieren und zu quantifizieren. Das Ergebnis eines XPS-Experiments ist immer ein Mittelwert über ein großes Nanopartikelensemble. Inwiefern ein einzelner Partikel innerhalb der Probe von einer idealen Morphologie abweicht, kann nicht gesondert erfasst werden. Im Gegensatz dazu kann STXM mit einer räumlichen Auflösung von 35 nm das Innere einzelner CSNPs visualisieren, sofern sie genügend Röntgenabsorptionskontrast zwischen Kern- und Schalenmaterial aufweisen. Im Artikel von 2018 wird am Beispiel der bereits im vorherigen Abschnitt genannt PTFE-PS-CSNPProben eine solche STXM-Untersuchung demonstriert. In der Veröffentlichung von 2021 werden Kern-Schale-artige (Ca/Sr)F₂-Nanopartikel für den praktischen Einsatz in unter anderem entspiegelnden Beschichtungen untersucht. Da hier keine scharfe Grenzfläche zwischen Kern- und Schalenmaterial vorliegt, ist eine Schalendickenbestimmung, wie sie im zweiten Abschnitt diskutiert wird, nicht sinnvoll. Stattdessen werden mit Hilfe von XPS, angeregt mit Synchrotronstrahlung bei variabler Röntgenphotonenenergie, Tiefenprofile der chemischen Zusammensetzung generiert, um die innere Morphologie der Partikel aufzuklären. Zusätzlich werden theoretische Tiefenprofile der Ca- und Sr-XPS-Peakintensitäten simuliert, um die Interpretation der Experimente zu erleichtern. So wurde eine CaF₂-Anreicherung an der Oberfläche der Partikel festgestellt, die kaum mit einer anderen analytischen Methode hätte entdeckt werden können. Da diese zerstörungsfreie Bestimmung von XPS-Tiefenprofilen sehr anspruchsvoll ist, wird noch mehr als üblich auf die lückenlose Dokumentation des Experiments geachtet, um vollständige Reproduzierbarkeit zu gewährleisten. Aufgrund der enormen Vielfalt an CSNPs, die sich in Material, Zusammensetzung und Form unterscheiden, kann eine Messmethode nicht völlig unverändert von einer Probe auf eine andere übertragen werden. Nichtsdestotrotz, da die als Teil dieser Doktorarbeit präsentierten Artikel eine deutlich ausführlichere Beschreibung der Experimente enthalten als vergleichbare Publikationen, stellen sie eine wichtige Anleitung für andere Wissenschaftler dafür dar, wie aussagekräftige Informationen über CSNPs durch Oberflächenanalytik erhalten werden können. KW - Core-shell nanoparticle (CSNP) KW - X-ray photoelectron spectroscopy (XPS) KW - Scanning transmission X-ray microscopy (STXM) PY - 2022 DO - https://doi.org/10.18452/24312 SP - i EP - 243 PB - Humboldt-Universität CY - Berlin AN - OPUS4-54991 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hufschläger, Daniel A1 - Gaal, Mate A1 - Ahmadzadeh, Majid T1 - Simulation und Vermessung von thermoakustischen Schallquellen N2 - Zur Simulation des Schallfeldes von beliebig geformten konventionellen Schallquellen existieren viele Ansätze (EFIT, GPSS). Sie alle basieren auf der Annahme eines monochromatischen akustischen Signals, was meist eine gültige Annäherung darstellt. Allerdings sind bei thermoakustischen Quellen aufgrund ihrer Funktionsweise und der hohen Bandbreite viele der existierenden Ansätze nicht direkt anwendbar und können Beobachtungen bei der Vermessung von thermoakustischen Wandlern nicht vollständig abbilden und erklären. In diesem Beitrag wurde die bekannte Methode der generalisierten Punktquellensynthese (GPSS) für die Berechnung von Schallfeldern von thermoakustischen Schallquellen angewendet. Dabei gehen zahlreiche Parameter wie die Dicke und Geometrie der leitfähigen Schicht, Krümmung des Substrats, sowie die Signalform der Anregung in die Simulation ein. Neu an dem präsentierten Ansatz ist die Abweichung von der üblichen monochromatischen Annäherung und die Berücksichtigung der großen Bandbreite von thermoakustischen Wandlern. Für die Validierung der Simulationen wurden Schallfelder von Quellen mit bekannter Anregung und Geometrie breitbandig durch ein optisches Mikrofon vermessen. T2 - DGZfP Jahrestagung CY - Kassel, Germany DA - 23.05.2022 KW - Thermoacoustics KW - Sensor characterization KW - Simulation PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-549944 SP - 1 EP - 7 AN - OPUS4-54994 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hufschläger, Daniel A1 - Gaal, Mate A1 - Gohlke, Dirk A1 - Weise, Matthias A1 - Szewieczek, A. A1 - Hillger, W. A1 - Ilse, D. T1 - Array-Prüfköpfe für luftgekoppelte Ultraschallprüfung N2 - Seit Jahren stellt die luftgekoppelte Ultraschallprüfung eine etablierte Alternative zur konventionellen Prüfung von Leichtbaukomponenten aus den Bereichen Luft- und Raumfahrt sowie Automotive dar. Im Gegenteil zur flüssigkeitsgekoppelten Prüfung in Kontakt oder im Tauchbecken ist sie weniger invasiv und bietet daher zeitliche und finanzielle Anreize. Normalerweise wird die luftgekoppelte Prüfung mit Einzelelementschwingern in Durchschallung realisiert, wohingegen die Gruppenstrahlertechnik bereits Industriestandard im Bereich der Kontakttechnik darstellt. Die damit verbundenen Vorteile wie die aktive Fokussierung oder, die gezielte Manipulation des Einschallwinkels zur Anregung von geführten Wellen, finden im Bereich der luftgekoppelten Prüfung dabei noch wenig Anwendung. Im Rahmen dieses Beitrags stellen wir die ersten Zwischenergebnisse des geförderten Projektes „PALUP – Phased- Array-Technik für Luftultraschall-Prüfungen“ vor. Ziel des Projektes ist die Entwicklung von Mehrelementschwingern auf Basis von zellulären Kunststoffen, die Entwicklung einer dedizierten Pulserstufe im Kilovoltbereich, sowie die nötige rauscharme messtechnische Auswertung jedes Einzelelements. T2 - DGZfP Jahrestagung CY - Kassel, Germany DA - 23.05.2022 KW - Phased array KW - Air-coupled ultrasound PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-549954 SP - 1 EP - 7 AN - OPUS4-54995 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Winkler, Nicolas P. A1 - Matsukura, H. A1 - Neumann, Patrick P. A1 - Schaffernicht, E. A1 - Ishida, H. A1 - Lilienthal, A. J. ED - Rudnitskaya, A. T1 - Super-Resolution for Gas Distribution Mapping: Convolutional Encoder-Decoder Network N2 - Gas distribution mapping is important to have an accurate understanding of gas concentration levels in hazardous environments. A major problem is that in-situ gas sensors are only able to measure concentrations at their specific location. The gas distribution in-between the sampling locations must therefore be modeled. In this research, we interpret the task of spatial interpolation between sparsely distributed sensors as a task of enhancing an image's resolution, namely super-resolution. Because autoencoders are proven to perform well for this super-resolution task, we trained a convolutional encoder-decoder neural network to map the gas distribution over a spatially sparse sensor network. Due to the difficulty to collect real-world gas distribution data and missing ground truth, we used synthetic data generated with a gas distribution simulator for training and evaluation of the model. Our results show that the neural network was able to learn the behavior of gas plumes and outperforms simpler interpolation techniques. T2 - 19th International Symposium on Olfaction and Electronic Nose CY - Aveiro, Portugal DA - 29.05.2022 KW - Gas Distribution Mapping KW - Spatial Interpolation KW - Deep Learning KW - Super-Resolution KW - Sensor Network PY - 2022 SN - 978-1-6654-5860-3 DO - https://doi.org/10.1109/isoen54820.2022.9789555 SP - 1 EP - 3 PB - IEEE CY - USA AN - OPUS4-54955 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Burgmayer, R. A1 - Bake, Friedrich A1 - Enghardt, L. T1 - Design and Evaluation of a Zero Mass Flow Liner N2 - In this study, the concept of a Zero Mass Flow Liner is evaluated. The concept enables impedance control by the induction of periodic bias flow through the perforated facing sheet of the liner. The periodic bias flow is generated by a secondary high amplitude acoustic actuation. By means of the periodic bias flow, the liner can be tuned to different operating points in a given range of grazing flow velocities. The equivalent fluid impedance model for perforated plates is modified to account for the effects of periodic bias flow and grazing flow. An optimization routine, based on a genetic algorithm, is implemented. The method is applicable to any liner concept and uses the impedance of the lined surface as boundary condition in a numerical simulation. Thereby, a set of liner parameters is derived in order to obtain the desired damping characteristics. Based on the results of the optimization, a Zero Mass Flow Liner is manufactured and consequently evaluated experimentally. The damping characteristics are evaluated in form of the dissipated energy along the lined surface. Prediction and measurements show agreement. The Zero Mass Flow Liner delivers broad band dissipation of high peak value over a range of grazing flow Mach numbers. Under grazing ow conditions, the effect of periodic bias flow is reduced. This poses high energy requirements in high Mach number flow regimes which might restrict the applicability of the Zero Mass Flow concept to grazing flows of low Mach numbers. T2 - 28th AIAA/CEAS Aeroacoustics 2022 Conference CY - Southampton, Great Britain DA - 14.06.2022 KW - Acoustic damping KW - Liner KW - Zero Massflow Liner (ZML) PY - 2022 DO - https://doi.org/10.2514/6.2022-2820 SP - 1 EP - 16 PB - AIAA / CEAS AN - OPUS4-55042 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hirschberg, L. A1 - Bake, Friedrich A1 - Hulshoff, S. T1 - Sound production due to main-flow oriented vorticity-nozzle interaction in absence of a net swirl N2 - The downstream acoustic response due to the interaction of main-flow oriented vorticity with a choked nozzle in a swirl-free flow was experimentally demonstrated. The response was obtained by means of impulsive radial air injection in the pipe upstream from the nozzle. The resulting downstream acoustic data are shown to obey a scaling rule that differs, from the one for swirl-nozzle interaction, which according to the literature is proportional to the square of the swirl number. In contrast, here evidence is presented that points to the scaling of main-flow oriented vorticity noise with the cross-sectional average of the square of the transversal velocity at the throat divided by the square of the critical sound speed. T2 - 28th AIAA/CEAS Aeroacoustics 2022 Conference CY - Southampton, Great Britain DA - 14.06.2022 KW - Main-flow oriented vorticity-nozzle interaction KW - Indirect noise PY - 2022 DO - https://doi.org/10.2514/6.2022-3055 SP - 1 EP - 8 PB - AIAA / CEAS AN - OPUS4-55043 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lecompagnon, Julien A1 - Hirsch, Philipp Daniel A1 - Rupprecht, C. A1 - Ziegler, Mathias ED - Mendioroz, A. ED - Avdelidis, N. P. T1 - Thermographic testing using 2D pseudo-random illumination and photothermal super resolution reconstruction N2 - Due to the diffusive nature of heat propagation in solids, the detection and resolution of internal defects with active thermography based non-destructive testing is commonly limited to a defect-depth-to-defect-size ratio greater than or equal to one. In the more recent past, we have already demonstrated that this limitation can be overcome by using a spatially modulated illumination source and photothermal super resolution-based reconstruction. Furthermore, by relying on compressed sensing and computational imaging methods we were able to significantly reduce the experimental complexity to make the method viable for investigating larger regions of interest. In this work we share our progress on improving the defect/inhomogeneity characterization using fully 2D spatially structured illumination patterns instead of scanning with a single laser spot. The experimental approach is based on the repeated blind pseudo-random illumination using modern projector technology and a high-power laser. In the subsequent post-processing, several measurements are then combined by taking advantage of the joint sparsity of the defects within the sample applying 2D-photothermal super resolution reconstruction. Here, enhanced nonlinear convex optimization techniques are utilized for solving the underlying ill-determined inverse problem for typical simple defect geometries. As a result, a higher resolution defect/inhomogeneity map can be obtained at a fraction of the measurement time previously needed. T2 - Thermosense: Thermal Infrared Applications XLIV CY - Orlando, Florida, USA DA - 05.04.2022 KW - Thermography KW - Super resolution KW - NDT KW - Material testing KW - Internal defects KW - DMD KW - DLP PY - 2022 DO - https://doi.org/10.1117/12.2618562 SN - 0277-786X VL - 12109 SP - 1 EP - 10 PB - SPIE AN - OPUS4-54909 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Babutzka, Martin A1 - et al., T1 - Exposure Site Catalogue - Catalogue of atmospheric corrosion field exposure sites in Europe N2 - Exposure sites and outdoor exposure have always been a part of atmospheric corrosion research providing the “final answer”, although at the cost of long exposure times. Individual exposure programs such as ISOCORRAG, MICAT and ICP Materials have resulted in collaborative networks of exposure sites. So far, however, there has been no collective effort to put together currently active sites in a comprehensive manner and across programs and nations. The information collected in the catalogue is possible thanks to the work of all individual site managers listed as contact persons, efforts of members of Working Party 25 (WP25) Atmospheric Corrosion of the European Federation of Corrosion (EFC) and financial support of the EFC. With this Catalogue you can both get a general overview of what is available and be guided if you are looking for a particular environment with certain characteristics. KW - Atmospheric Corrosion KW - Atmosphärische Korrosion KW - Corrosion KW - Korrosion KW - Exposure KW - Auslagerungsversuche PY - 2022 UR - https://efcweb.org/Scientific+Groups/WP25_+Atmospheric+Corrosion/Current+Activities/_/Exposure%20site%20catalogue%20EFC%20lores.pdf SP - 1 EP - 56 PB - European Federation of Corrosion, EFC AN - OPUS4-55284 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Liao, Chun-Man A1 - Fontoura Barroso, Daniel T1 - Investigation of temperature effects on ultrasonic velocity in a prestressed concrete bridge model N2 - Ultrasonic measurements have recently been applied in the context of structural health monitoring in civil engineering. The ultrasonic method is very sensitive to environmental conditions and material property changes, which might be caused by prestress losses and loading effects on the bridge. However, it remains a challenge to identify the damage mechanisms causing structural property changes from the above mentioned factors influencing ultrasonics. The focus of this contribution is to investigate the correlation between ultrasonic velocities and temperature by the coda wave interferometry (CWI) analysis. Long-term monitoring of a prestressed concrete bridge model under field conditions was carried out to observe the effect of temperature. The homogeneous change in concrete caused by temperature was revealed by applying the CWI method. The threshold value of the best correlation coefficients for the linear regression of temperature and ultrasonic velocity changes was also studied. Experimental assessment will provide a ratio for temperature correction to evaluate the pre-stressing force decrease and its consequences on crack opening or extension. T2 - Tagung EWSHM2022 CY - Palermo, Italy DA - 04.07.2022 KW - Ultrasonic Velocity KW - Coda Wave Interferometry KW - Temperature Correction KW - Prestressing Force KW - Bridge Monitoring PY - 2022 SN - 978-3-031-07257-4 SN - 978-3-031-07258-1 DO - https://doi.org/10.1007/978-3-031-07258-1_82 VL - 2 SP - 813 EP - 823 PB - Springer Nature AN - OPUS4-55289 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gaal, Mate A1 - Bernhardt, Y. A1 - Csaszar, L. A1 - Dengiz, N. A1 - Fuchs, M. A1 - Gautzsch, T. A1 - Gohlke, Dirk A1 - Hahn-Jose, T. A1 - Heckel, Thomas A1 - Hillger, W. A1 - Hufschläger, Daniel A1 - Ilse, D. A1 - Kiel, M. A1 - Labud, P. A1 - Schubert, F. A1 - Sommerhuber, R. A1 - Szewieczek, A. A1 - Waschkies, T. T1 - Richtlinie zur Charakterisierung von luftgekoppelten Ultraschallwandlern N2 - Zur Charakterisierung von luftgekoppelten Ultraschallwandlern werden mehrere verschiedene Methoden und Verfahren angewendet. Durch die unterschiedlichen Herangehensweisen werden oft unterschiedliche Prüfkopfpara-meter und Schallfeldgrößen ermittelt, was einen direkten Vergleich von Datenblättern erschwert. Für die Charakterisierung von Kontakt- und Tauchtechnikprüfköpfen hat sich ISO 22232-2:2021 bereits etabliert, allerdings ist diese Norm nicht auf die luftgekoppelten Wandlertechnologien direkt übertragbar. Daher erkannten Hersteller, Forschungseinrichtungen und Anwender den Bedarf an einer Richtlinie zur einheitlichen Charakterisierung von luftgekoppelten Wandlern. Gemeinsam arbeiten sie aktuell im Rahmen des Unterausschusses „Luftgekoppelte Ultraschallprüfung“ der DGZfP an der Erstellung einer solcher Richtlinie mit dem Anspruch, die bestehende Normung um die luftgekoppelte Prüfung zu erweitern und somit die Vereinheitlichung der Charakterisierung dieser Wandler zu erleichtern. In diesem Beitrag wird ein Überblick über den geplanten Inhalt der Richtlinie und über die Methoden zur akustischen Charakterisierung von luftgekoppelten Ultraschallwandlern gegeben. Insbesondere werden verschiedene Methoden der Ermittlung von wichtigen Wandlerparametern wie z.B. Empfindlichkeit, Mittenfrequenz, Bandbreite, Fokusgröße und Fokusabstand dargestellt und verglichen. T2 - DGZfP-Jahrestagung CY - Kassel, Germany DA - 23.05.2022 KW - Lutgekoppelte Ultraschallprüfung KW - Prüfkopf KW - Charakterisierung KW - Richtlinie PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-552918 SP - 1 EP - 7 AN - OPUS4-55291 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Olino, M. A1 - Lugovtsova, Yevgeniya A1 - Memmolo, V. A1 - Prager, Jens T1 - Temperature Compensation Strategies for Lamb Wave Inspection using Distributed Sensor Networks N2 - The application of temperature compensation strategies is crucial in structural health monitoring approaches based on guided waves. Actually, the varying temperature influences the performance of the inspection system inducing false alarms or missed detection, with a consequent reduction of reliability. This paper quantitatively describes a method to compensate the temperature effect, namely the optimal baseline selection (OBS), extending its application to the case of distributed sensor networks (DSN). The effect of temperature separation between baseline time-traces in OBS are investigated considering multiple couples of sensors employed in the DSN. A combined strategy that uses both OBS and frequent value warning is considered. Theoretical results are compared, using data from two several experiments, which use different frequency analysis with either predominantly A0 mode or S0 mode data or both. The focus is given on the fact that different paths are available in a sensor network and several possible combination of results are available. Nonetheless, introducing a frequent value warning it is possible to increase the efficiency of the OBS approach making use of fewer signal processing algorithms. These confirm that the performance of OBS quantitatively agrees with predictions and also demonstrate that the use of compensation strategies improve detectability of damage. T2 - IEEE International Workshop on Metrology for AeroSpace CY - Pisa, Italy DA - 27.06.2022 KW - Ultrasound KW - Ultrasonic Guided Waves KW - Structural Health Monitoring PY - 2022 SN - 978-1-6654-1076-2 DO - https://doi.org/10.1109/MetroAeroSpace54187.2022.9856029 SP - 598 EP - 601 AN - OPUS4-55268 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mueller, I. A1 - Freitag, S. A1 - Memmolo, V. A1 - Moix-Bonet, M. A1 - Möllenhoff, K. A1 - Golub, M. A1 - Sridaran Venkat, R. A1 - Lugovtsova, Yevgeniya A1 - Eremin, A. A1 - Moll, J. A1 - Tschöke, K. ED - Rizzo, P. ED - Milazzo, A. T1 - Performance Assessment for Artificial Intelligence-Based Data Analysis in Ultrasonic Guided Wave-Based Inspection: A Comparison to Classic Path-Based Probability of Detection N2 - Performance assessment for GuidedWave (GW)-based Structural Health Monitoring (SHM) systems is of major importance for industrial deployment. With conventional feature extraction methods like damage indices, pathbased probability of detection (POD) analysis can be realized. To achieve reliability quantification enough data needs to be available, which is rarely the case. Alternatives like methods for performance assessment on system level are still in development and in a discussion phase. In this contribution, POD results using an Artificial Intelligence (AI)-based data analysis are compared with those delivered by conventional data analysis. Using an open-access dataset from Open Guided Wave platform, the possibility of performance assessment for GW-based SHM systems using AI-based data analysis is shown in detail. An artificial neural network (ANN) classifier is trained to detect artificial damage in a stiffened CFRP plate. As input for the ANN, classical damage indicators are used. The ANN is tested to detect damage at another position, whose inspection data were not previously used in training. The findings show very high detection capabilities without sorting any specific path but only having a global view of current damage metrics. The systematic evaluation of the ANN predictions with respect to specific damage sizes allows to compute a probability of correct identification versus flaw dimension, somehow equivalent to and compared with the results achieved through classic path-based POD analysis. Also, sensitive paths are detected by ANN predictions allowing for evaluation of maximal distances between path and damage position. Finally, it is shown that the prediction performance of the ANN can be improved significantly by combining different damage indicators as inputs. T2 - 10th European Workshop on Structural Health Monitoring (EWSHM 2022) CY - Palermo, Italy DA - 04.07.2022 KW - Probability of Detection KW - Composites KW - Open Guided Waves Platform KW - Artificial Neural Network PY - 2022 SN - 978-3-031-07257-4 DO - https://doi.org/10.1007/978-3-031-07258-1 SN - 2366-2557 VL - 2 SP - 953 EP - 961 PB - Springer CY - Cham, Switzerland AN - OPUS4-55269 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Tschöke, K. A1 - Mueller, I. A1 - Memmolo, V. A1 - Sridaran Venkat, R. A1 - Golub, M. A1 - Eremin, A. A1 - Moix-Bonet, M. A1 - Möllenhoff, K. A1 - Lugovtsova, Yevgeniya A1 - Moll, J. A1 - Freitag, S. ED - Rizzo, P. ED - Milazzo, A. T1 - A Model-Assisted Case Study Using Data from Open Guided Waves to Evaluate the Performance of Guided Wave-Based Structural Health Monitoring Systems N2 - Reliability assessment of Structural Health Monitoring (SHM) systems poses new challenges pushing the research community to address many questions which are still open. For guided wave-based SHM it is not possible to evaluate the system performance without taking into account the target structure and applied system parameters. This range of variables would result in countless measurements. Factors like environmental conditions, structural dependencies and wave characteristics demand novel solutions for performance analysis of SHM systems compared to those relying on classical non-destructive evaluation. Such novel approaches typically require model-assisted investigations which may not only help to explain and understand performance assessment results but also enable complete studies without costly experiments. Within this contribution, a multi input multi output approach using a sparse transducer array permanently installed on a composite structure to excite and sense guided waves is considered. Firstly, the method and the analysis of path-based performance assessment are presented considering an open-access dataset from the Open Guided Wave platform. Then, a performance analysis of a guided wave-based SHM system using Probability of Detection is presented. To explain some unexpected results, the model-assisted investigations are used to understand the physical phenomena of wave propagation in the test specimen including the interaction with damage. Finally, issues and future steps in SHM systems’ performance assessment and their development are discussed. T2 - 10th European Workshop on Structural Health Monitoring (EWSHM 2022) CY - Palermo, Italy DA - 04.07.2022 KW - Performance assessment KW - Ultrasonic Guided Waves KW - Open Guided Waves Platform PY - 2022 SN - 978-3-031-07257-4 DO - https://doi.org/10.1007/978-3-031-07258-1 SN - 2366-2557 VL - 2 SP - 938 EP - 944 PB - Springer CY - Cham, Switzerland AN - OPUS4-55270 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Grotelüschen, Bjarne A1 - Bühling, Benjamin T1 - Impact-Echo Dataset "IE Platte" N2 - This dataset contains raw data resulting from Impact-Echo measurements at the reference concrete block "IE Platte", located at BAM (German Federal Institute for Materials Research and Testing). The specimen contains three polystyrene slabs and one polyethylene foil to act as reflectors. The specimen was produced in a three-step process. First, the base plate was cast. Second, the reflectors were taped to the base plate. Finally, the upper layer was cast on top of base plate and reflectors. A drawing is contained in the dataset. The Impact-Echo method is based on the excitation of the zero-group-velocity frequency of the first symmetric Lamb mode of a plate-like structure, in order to assess its thickness. Numerous publications elaborate on Impact-Echo theory, examples are (Gibson and Popovics 2005, Schubert and Köhler 2008 , Abraham and Popovics 2010). The measurements have been conducted using a setup that contains only commercially available components. The setup consists of an Olson CTG-2 concrete thickness gauge (Olsen Instruments, USA) for actuation and sensing and an 8-bit NI USB-5132 digital storage oscilloscope (National Instruments, USA) combined with the Echolyst software (Schweizerischer Verein für technische Inspektionen (SVTI), Switzerland) for data acquisition. Measurements were conducted using a grid of 29x29 points with a spacing of 50 mm. At each point 8192 samples were recorded at a sampling rate of 1 MS/s. The dataset contains the (X,Y) location in mm of the individual measurement points as well as the raw measurement data at those points. The data is provided in the formats *.mir/*.mhdr (Echolyst), *.npy (Python) and *.mat (Matlab) and *.csv to ease the import in various post-processing tools. KW - Concrete KW - Impact-Echo KW - Nondestructive testing PY - 2022 DO - https://doi.org/10.7910/DVN/EH4E9G PB - Harvard College CY - Cambridge, MA, USA AN - OPUS4-55279 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hassenstein, Christian A1 - Heckel, Thomas A1 - Prager, Jens A1 - Berendt, T. A1 - Voehringer, D. T1 - Robotergeführte Ultraschallprüfung von Gasturbinenschaufeln mit adaptiver TFM im ZfP 4.0-Umfeld N2 - Leit- und Laufschaufeln stationärer Gasturbinen sind im Betrieb anspruchsvollen Bedingungen ausgesetzt. Die Prüfung, Wartung und Reparatur der hochbelasteten Teile sind notwendig, um Sicherheit und Effizienz über längere Zeiträume zu gewährleisten. Eine der in diesem Prozess angewandten Methoden ist die Ultraschallprüfung. Im Zuge der fortschreitenden Digitalisierung ist es das Ziel des Projektes MRO 2.0, den Aufbereitungsvorgang um digitale Prozesse zu erweitern und somit zu modernisieren. Eine der Aufgaben ist es, dabei anstelle der konventionellen Ultraschallprüfung eine Array-Technik mit rekonstruierenden Verfahren einzusetzen und eine automatisierte, digital eingebundene Methode im Rahmen von ZfP 4.0 zu entwickeln. Um die Ist-Geometrie der Oberfläche und die verbleibende Wanddicke flächendeckend an den Turbinenschaufeln zu bestimmen, wird ein adaptives TFM Verfahren (Total Focusing Method) in Tauchtechnik eingesetzt, welches die Brechung der Schallwellen an der Grenzfläche zum Prüfkörper in der Rekonstruktion berücksichtigt. In der hierfür entwickelten Prüfanlage führt ein Roboterarm einen Array-Prüfkopf und scannt das Bauteil normal zur inspizierten Oberfläche. Somit kann ein 3D-Modell des Ist Zustandes des zu prüfenden Bauteils erstellt werden. Spezielle Herausforderungen an die Aufgabe stellen die komplexe Geometrie des Prüfobjektes sowie dessen geringe und ortsabhängige Wanddicke dar. Ein weiterer Fokus liegt auf der Optimierung der Prüfparameter, Verbesserung der Prüfgeschwindigkeit sowie der Zuverlässigkeit der Methode. In diesem Beitrag werden die während des Projektes entwickelte Methode und die im zweiten Projektjahr erarbeiteten Ergebnisse vorgestellt, mit dem Schwerpunkt auf die entwickelten Rekonstruktionsalgorithmen und den Versuchsaufbau. T2 - DGZfP Jahrestagung 2022 CY - Kassel, Germany DA - 23.05.2022 KW - Ultraschallprüfung KW - Turbinenschaufel KW - Phased Array KW - Total Focusing Method KW - Automatisierung KW - Tauchtechnik PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-551881 UR - https://www.ndt.net/search/docs.php3?id=27055 SP - 1 EP - 11 PB - NDT.net AN - OPUS4-55188 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Kuntze, Wilhelm T1 - Festlegung von Grenzwerten der Sprödigkeitsneigung mittels Kerbzug- und Kerbschlagzugproben für Abnahmezwecke N2 - In Auswertung der Theorie lassen sich die Bedingungen des spröden Bruches für eine bestimmte Probenform (Spannungszustand) im Geschwindigkeits-Temperatur-Schaubild durch eine gerade Linie (kritische Gerade) darstellen, welche im Schaubild das Gebiet des zähen Bruches vom Gebiet des spröden Bruches abgrenzt. Die Größe des Raumes zwischen der kritischen Geraden und den Gebrauchsbedingungen ist ein Maßstab für den Sicherheitsgrad des Werkstoffes gegenüber dem spröden Bruch. Die Formänderungsfähigkeit, die der Werkstoff unterhalb dieser Grenzen, also im Gebiet des zähen Bruches aufbringt, ist gänzlich unabhängig von den Sprödbruchbedingungen. Ein Werkstoffprüfverfahren bei Raumtemperatur muß mit Proben sehr scharfer Einkerbung bei entsprechendem Spannungszustand durchgeführt werden, damit die Ergebnisse in die Nähe der kritischen Geraden fallen; denn nur so lassen sich die Werkstoffe hinsichtlich ihrer Sprödigkeitsneigung differenzieren. Außerdem muß die Formänderungsfähigkeit herausdividierbar sein, damit sich die Sprödbruchbedingungen klar absondern lassen. Mildere Probenformen, z.B. die Kerbschlagbiegeprobe mit flacher, kreissegmentförmiger Kerbe, sind indifferent; sie geben nur die von der Sprödbruchneigung unabhängige Formänderungsfähigkeit wieder und bieten daher nichts Neues. Bei dem vorliegenden Prüfverfahren wird der Sicherheitsgrad durch das Verhältnis der dynamischen zur statischen Brucheinschnürung Ψ(KS)/Ψ(K) bei der Kerbzugprobe wiedergegeben. Die statische Brucheinschnürung Ψ(K) kennzeichnet die Formänderungsfähigkeit, durch welche vor Eintritt der Sprödbruchbedingungen ein, die Sicherheit vermehrender plastischer Abbau von Spannungsspitzen ermöglicht wird. Kaltreckschäden sind nicht so aufzufassen, daß sie nur bei "alterungsanfälligen" Stählen vorkommen; alle Werkstoffe erleiden Kaltreckschäden. Bemerkbar und gefährlich werden diese nur dann, wenn von vornherein der Quotient Ψ(KS)/Ψ(K) und damit der Sicherheitsgrad klein ist. Diese quantitative Erklärung macht es verständlich, daß der Quotient Ψ(KS)/Ψ(K) im ungeschädigtem Zustand so gute Voraussagen erlaubt. PY - 1953 VL - Bericht 6/53 SP - 1 EP - 23 PB - Materialprüfungsamt CY - Berlin AN - OPUS4-54427 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Kuntze, Wilhelm T1 - Vergleich der Ergebnisse von Aufschweißbiegeversuchen mit den Ergebnissen von Kerbzug- und Kerbschlagzugversuchen N2 - Die prüfmäßige Ermittlung der Sprödigkeitsgrenzen von Baustählen im Anlieferungszustand ergibt eine breite Differenzierung, die für die Übergangstemperatur bei statischer Beanspruchung einen Bereich zwischen etwa -90 and -225°C, also von etwa 135°C einnimmt. Bei der Aufschweißbiegeprobe drängt sich dieser Bereich auf etwa 40°C, zwischen etwa +30 und -10°C liegend zusammen. Daraus geht hervor, daß die besseren Stähle durch das Schweißen eine größere Schädigung erfahren als die minderwertigen. Die Ursache sind innere Spannungen, die als Folge räumlich begrenzter Plastizierungen bei Erwärmung und Wiederabkühlung entstehen und die am stärksten bei den Stählen auftreten, welche bei den höchsten Geschwindigkeiten und tiefsten Temperaturen noch plastizieren. Dieselbe Theorie, welche die Qualität der Stähle in Anlieferungszustand bedingt (Becker - Orowan - Kochendörfer), begründet auch die Schädigung der qualifiziertesten Stähle durch das Schweißen. Trotzdem bleiben die qualifizierten Stähle noch überlegen: 1.) sie behalten noch einen, wenn auch kleinen Überschuß an Zähigkeit beim Aufschweißbiegeversuch, 2.) im Sprödigkeitsgebiet (-20°C) ertragen sic höhere elastische Biegewinkel und damit höhere Spannungen, 3.) die inneren Spannungen lassen sich durch Ausglühen umso leichter beseitigen, je besser die Qualität ist; bei Stählen minderer Qualität können schon beim Schweißen Schrumpfrisse entstehen. Die Qualität ist dadurch gekennzeichnet, daß die Sprödigkeitsgrenzen des Stahles weit von den Gebrauchsbedingungen entfernt liegen. Die Ermittlung des Brucheinschnürungsquotienten aus dem Kerbschlagzug- und Kerbzugversuch im Anlieferungszustand und bei Raumtemperatur ist das einfachste Verfahren, welches anstelle der umständlichen Ermittlung der Temperaturkurven einen Maßstab für die Sprödigkeitsgrenzen abgibt. Zwischen diesem Prüfwert und den Ergebnissen des Aufschweißbiegeversuches wurden folgende Zusammenhänge gefunden: 1.) Die Bruchgefahr bei der Aufschweißbiegeprobe ist durch einen kleinen Brucheinschnürungsquotienten gekennzeichnet. 2.) lm Gebiet des spröden Bruches ordnen sich die elastischen Biegewinkel, d.h. die ertragenen Spannungen, nach der Größe des Brucheinschnürungsquotienten ein. 3.) Der Erfolg des Spannungsfreiglühens kann nach der Größe des Brucheinschnürungsquotienten vorausgesagt werden. Die Sprödigkeitsfrage bei geschweißten dicken Profilen läuft also auf die Auswahl des Stahles unter Berücksichtigung seiner Sprödigkeitsgrenzen im Anlieferungszustand hinaus, wofür die Ermittlung des Brucheinschnürungsquotienten das geeignetste Prüfverfahren ist, und auf die Vervollkommnung der Vorrichtungen zum Vorwärmen oder Ausglühen großer Bauteile. Der Erfolg hängt hier von der richtigen Auswahl des Stahles ab. Außer den Schrumpfspannungen treten noch Umwandlungsspannungen unter Martensitbildung auf. Ihre Beziehungen zu den ursprünglichen Sprödigkeitsgrenzen des Stahles, sowie zum Brucheinschnürungsquotienten im Anlieferungszustand sind noch durch Versuche aufzuklären. PY - 1953 VL - Bericht 12/53 SP - 1 EP - 11 PB - Materialprüfungsamt CY - Berlin AN - OPUS4-54443 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gehrenkemper, Lennart A1 - Simon, Fabian A1 - Meermann, Björn T1 - Schnelle und einfache Extraktion von PFAS aus Bodenproben: Optimierte EOF-Bestimmung mittels HR-CS-GFMAS N2 - Per- und polyfluorierte Alkylsubstanzen (PFAS) bilden eine sehr komplexe Schadstoffgruppe mit über 6300 Einzelsubstanzen, die in vielfältiger Form in die Umwelt eingetragen werden. Für ein effektives Monitoring dieser Schadstoffklasse benötigt es ein Zusammenspiel aus Summenparameter-Analytik zur hot-spot-Identifizierung und Klassifizierung von Belastungssituationen sowie einer nachgeschalteten target-Analytik zur Identifizierung von Eintragswegen, die zugleich ein tieferes Verständnis von Transformationsprozessen ermöglicht. In diesem Beitrag präsentieren wir eine optimierte Extraktions-Methode für die PFAS-Summenparameteranalytik. Mit Hilfe dieser können bisher verwendete zeit- und kostenintensive Festphasenextraktionen (SPE) umgangen und PFAS-Extraktionseffizienzen gesteigert werden. Die methodische Bestimmungsgrenze (LOQ) war mit 10,30 μg/kg (Fluor pro Bodenprobe) ausreichend für alle 9 untersuchten Realbodenproben. KW - High resolution-continuum source-graphite furnace molecular absorption spectrometry (HR-CS-GFMAS) KW - PFAS KW - Per- and polyfluorinated alkyl substances (PFASs) KW - Extractable organically bound fluorine (EOF) KW - Solid-liquid extraction KW - Böden PY - 2022 UR - https://www.gdch.de/fileadmin/downloads/Netzwerk_und_Strukturen/Fachgruppen/Umweltchemie_Oekotoxikologie/mblatt/2022/Heft122.pdf SN - 1618-3258 VL - 28 IS - 1 SP - 12 EP - 15 PB - Gesellschaft Deutscher Chemiker AN - OPUS4-54417 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Auersch, Lutz A1 - Krüger, F. T1 - Untersuchung zur Ausbreitung und Minderung von Erschütterungen an Trassen des schienengebundenen Nahverkehrs in Geländeniveau N2 - Prognosen zur Erschütterungsausbreitung und zur Immissionssituation in der Umgebung von Bahntrassen sind wegen der Vielfalt der Einflussfaktoren oft mit erheblichen Unsicherheiten behaftet. Ziel der Arbeit war es, die Bedingungen für die Ausbreitung von Körperschall und Erschütterungen genauer zu erfassen und in ein für Prognosezwecke geeignetes Rechenmodell umzusetzen. Aufbauend auf theoretischen Untersuchungen zum Übertragungsverhalten des Bodens und von Gebäuden wurden Erschütterungsmessungen an Trassen verschiedener Bahnen des Stadtverkehrs Erregerspektren sowie mit besonderen Messverfahren Bodenkennwerte ermittelt. Diese dienen als Grundlage für die Modellrechnungen über die Ausbreitung von Erschütterungen. Durch Kontrollmessungen wurde die Anwendbarkeit des Modells überprüft. Es zeigten sich z.T. gute Übereinstimmungen, jedoch wurde auch die Notwendigkeit einer weiteren Verbesserung deutlich. Die Möglichkeiten der Minderung der Erschütterungen wurden umfassend behandelt. KW - Schienenverkehr KW - Erschütterungen KW - Körperschall KW - Rechenmodell KW - Immissionsminderung KW - Immissionsprognose PY - 1983 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-544190 N1 - BMFT-Vorhaben TV 7954 - AP 09 000 VL - Bericht 9 SP - 1 EP - 525 PB - Studiengesellschaft für unterirdische Verkehrsanlagen (STUVA) CY - Köln AN - OPUS4-54419 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Auersch, Lutz A1 - Hebener, Hans A1 - Rücker, Werner T1 - Erschütterungen infolge Schienennahverkehr - Theoretische und meßtechnische Untersuchungen zur Emission, zur Ausbreitung durch den Boden und zur Übertragung in Gebäude N2 - Das Ziel der Untersuchungen ist ein Prognosemodell für Erschütterungen infolge Schiennahverkehr. Ergänzend zu Bericht 9 wird insbesondere der dreidimensionale, instationäre und zufällige Charakter der Erschütterungsquelle und dessen Auswirkungen auf die Ausbreitung durch den Boden und auf die Schwingungen benachbarter Gebäude untersucht. Es werden jeweils theoretisch/numerisch und experimentell/messtechnisch - Amplituden-Abstands-Gesetze, - Freifeld-Bauwerks-Übertragungsverhältnisse und - Deckenresonanzüberhöhungen ermittelt, die zusammen mit den Ergebnissen des Berichts 9 eine realistische Prognose von Erschütterungen ermöglichen. Die Ergebnisse sind in einem einfachen Prognoseprogramm zusammengefasst, mit dem im konkreten Anwendungsfall der Einfluss einer Reihe von Quell-, Boden- und Bauwerkseigenschaften erfasst wird. KW - Erschütterungen KW - Körperschall KW - Immissionsprognose KW - Schienenverkehr KW - Bauwerksschwingungen KW - Deckenresonanz KW - Wellenausbreitung KW - Bodendynamik PY - 1986 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-544209 N1 - BMFT-Vorhaben TV 8329 VL - Bericht 19 SP - 1 EP - 360 PB - Studiengesellschaft für unterirdische Verkehrsanlagen (STUVA) CY - Köln AN - OPUS4-54420 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zhu, Jiangchao A1 - Schurig, M. A1 - Schlums, H. A1 - Madia, Mauro A1 - Zerbst, Uwe T1 - Bruchmechanische Bewertung der Integrität einer Turbinenscheibe bei Überdrehzahl N2 - Turbinenscheiben sind thermisch und mechanisch hochbeanspruchte, sicherheitsrelevante Komponenten in Gasturbinen. Ihre Integrität wird in Bauteiltests unter Überdrehzahlbedingungen nachgewiesen. Kontext des Aufsatzes ist die Erarbeitung einer zusätzlichen Bewertungsebene auf der Grundlage von Versuchen unter monotoner Beanspruchung, die die Beanspruchung im Bauteil realistisch wiedergeben soll. Betrachtet wird ein halbelliptischer Riss, der bei der weiteren Ausbreitung als Umfangsriss wächst (rim peeling). Die Simulation dieser Stelle im Bauteil schließt die mechanische und thermische Beanspruchung sowie sie Dehnungsbehinderung ein. Letztere wird anhand zweier Parameter, der Spannungsmehrachsigkeit ℎ und des (allerdings modifizierten) Constraint-Parameters nach Newman, der die Spannungen über den plastisch verformten Bereich mittelt, bestimmt. Erwartungsgemäß zeigt sich, dass die höchste Dehnungsbehinderung weder an den Oberflächenpunkten, noch an den tiefsten Punkten, sondern an einer Stelle zwischen beiden auf der Rissfront auftritt. Als Versuchsgeometrie für die monotonen Tests soll eine Kreuzprobe mit wanddurchdringenden Rissen ausgehend von einer Innenbohrung dienen. Durch geeignete Wahl der Risstiefe sowie der in beiden Richtungen angreifenden Kräfte gelingt es, bauteiladäquate Zustände zu erzeugen. T2 - 54. Tagung des DVM-Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Online meeting DA - 22.02.2022 KW - Bruchmechanik KW - Struktur Integrität KW - Turbinenscheibe KW - Constraint PY - 2022 SP - 13 EP - 22 AN - OPUS4-54403 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Blind, K. A1 - Krüger, M. A1 - Kinne, J. A1 - Mirtsch, Mona ED - Jacobs, K. T1 - Organisation Innovation in the Digital Layer: Exploring the Adoption of the Management System Standard ISO/IEC 27001 N2 - Despite the increasing relevance of cybersecurity for companies’ performance, there is limited research on the adoption of ISO/IEC 27001, an international information security management standard. The aim of our study is to expand this limited body of literature. First, we analyse the influence of companies’ networks on the adoption of ISO/IEC 27001 as an organisational innovation based on firm website data and their hyperlinks, using the entire population of ISO/IEC 27001 certified firms identified via web mining. Second, we validate the method of constructing and analysing companies’ “digital layer” following the call for new methodological approaches to study the organisational adoption of innovations. Our findings reveal that companies' decision to adopt ISO/IEC 27001 increases significantly with their number of linkages to other companies and to those having the same certificate. Finally, their cognitive and organisational distances to linked partners have the expected inverted u-shaped influence on their own adoption decision. T2 - 11th International Conference on Standardisation and Innovation in Information Technology (SIIT 2021) CY - Aachen, Germany DA - 06.09.2021 KW - Information Security KW - Hyperlinks KW - Management system standard KW - Digital Layer PY - 2021 SN - 978-3-95886-421-4 SP - 95 PB - Verlagshaus Mainz GmbH Aachen CY - Mainz AN - OPUS4-54411 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erning, Johann Wilhelm ED - Leyens, C. T1 - Hygienische Eigenschaften von additiv gefertigtem 1.4404 in Trinkwasser N2 - Elektrochemische Messungen zur hygienischen Bewertung additiv gefertigter Bauteile werden diskutiert. Die Bewertung und Details des Werkstoffs werden beschrieben, Anwendungsbeispiele werden gezeigt. T2 - 3. Fachtagung Werkstoffe und Additive Fertigung CY - Dresden, Germany DA - 11.05.2022 KW - Korrosion KW - Trinkwasser KW - Hygienische Bewertung KW - Additive Fertigung PY - 2022 SN - 978-3-88355-423-2 SP - 126 EP - 127 PB - Deutsche Gesellschaft für Materialkunde (DGM) CY - Sankt Augustin AN - OPUS4-54933 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stamm, Michael A1 - Krankenhagen, Rainer T1 - Weather-dependent passive thermography of unheated wind turbine blades N2 - Up to now, the inspection of wind turbines with industrial climbers has been considered ”state of the art”. However, ever-larger wind turbines and advancing digitization make modern and automated inspection methods indispensable. Passive thermography can serve as such a digital and atomized method while it is well known for its applications in the inspection of buildings or electrical circuits. However, its application relies on thermal gradients in the inspected object such that a temperature contrast exists between damaged and sound areas. This also holds for unheated structures like rotor blades of wind turbines which show no intrinsic temperature gradient and can hardly be heated. Under certain weather conditions with sufficient solar loading and diurnal temperature variations, passive thermography is suitable for the in-service inspection of rotor blades. However, for a reliable use of passive thermography on ”thermal passive” components, the incorporation of these environmental conditions in the planning and evaluation of thermal inspections is crucial. Additionally, the complex inner structure of wind turbine blades in comparison to other objects and buildings require a specific method referencing the individual rotor blades to each other. This allows the distinction between the thermal response of design-specific structural features and damages or irregularities between the three blades. We show thermal signatures of damage in rotor blades and contrast them with structural characteristics by comparing the three blades. In addition to measurements in industrial environments, laboratory measurements are shown and compared to simulations. The long-term goal is to simulate the influence of different weather parameters and thus gain a better understanding of measurements in the field. The results shown here can be seen as one step towards industrial application. T2 - SPIE Defense + Commercial Sensing CY - Orlando, Florida, USA DA - 03.04.2022 KW - Passive thermography KW - Wind energy KW - FEM simulations PY - 2022 DO - https://doi.org/10.1117/12.2618740 VL - 12109 SP - 1 EP - 8 PB - Society of Photo-Optical Instrumentation Engineers (SPIE) AN - OPUS4-54943 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Königsbauer, Korbinian A1 - Wosniok, Aleksander A1 - Nöther, N. A1 - Schaller, B. T1 - Entwicklung eines praxistauglichen POF-basierten Messsystems mittels digitaler I-OFDR zur Dehnungsdetektion T1 - Development of a practicable POF-based measuring system using digital I-OFDR for strain detection N2 - Es wird ein faseroptisches Messsystem vorgestellt, welches auf Basis der Rayleigh-Rückstreumessung eine ortsauflösende Detektion von signifikant großen Dehnungen bei Bauvorhaben im von Anwendern geforderten Größenordnungsbereich von 3 % bis 10 % ermöglicht. Mit dem Verfahren der digitalen inkohärenten optischen Frequenzbereichsreflektometrie (I-OFDR) werden materialspezifische Vorteile robuster perfluorierter polymeroptischer Fasern (PF-POF) erschlossen. Für den angestrebten industriellen Einsatz für die Zustandsüberwachung im Bereich des Tunnel- und Spezialtiefbaus soll die spezifische Rückstreuzunahme in der PF-POF hochauflösend gemessen werden. Diese Veröffentlichung zeigt in ersten Projektergebnissen die Eignung des digitalen I-OFDR für eine Dehnungsdetektion von bis zu 10%. N2 - A fiber-optic measurement system is presented which, based on Rayleigh backscatter measurement, enables distributed detection of significantly large strains in construction projects in the range of 3 % to 10 % required by end users. The method of digital incoherent optical frequency domain reflectometry (I-OFDR) is used exploiting material-specific advantages of robust perfluorinated polymer optical fibers (PF-POF). For the intended industrial application for structural health monitoring in the field of tunnel construction and specialised civil and underground engineering, the specific backscatter increase in the PF-POF is to be measured with high resolution. This publication shows in first project results the suitability of the digital I-OFDR for strain detection up to 10%. T2 - 21. ITG/GMA-Fachtagung CY - Nuremberg, Germany DA - 10.05.2022 KW - Backscatter measurement KW - Optical fiber sensors KW - POF KW - I-OFDR KW - Strain measurement PY - 2022 SN - 978-3-8007-5835-7 SN - 0932-6022 VL - 303 SP - 139 EP - 143 PB - VDE VERLAG GMBH CY - Berlin · Offenbach AN - OPUS4-54851 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Patrick P. A1 - Hüllmann, Dino A1 - Winkler, Nicolas P. A1 - Schugardt, Jan ED - Rudnitskaya, A. T1 - Remote Drone-to-Drone Gas Sensing: A Feasibility Study N2 - Remote gas sensors mounted on mobile robots enable the mapping of gas distributions in large or poorly accessible areas. A challenging task however, is the generation of three-dimensional distribution maps from these spatially sparse gas measurements. To obtain high-quality reconstructions, the choice of optimal measuring poses is of great importance. Remote gas sensors, that are commonly used in Robot Assisted Gas Tomography (RAGT), require reflecting surfaces within the sensor’s range, limiting the possible sensing geometries, regardless of whether the robots are ground-based or airborne. By combining ground and aerial robots into a heterogeneous swarm whose agents are equipped with reflectors and remote gas sensors, remote inter-robot gas measurements become available, taking RAGT to the next dimension – releasing those constraints. In this paper, we demonstrate the feasibility of drone-to-drone measurements under realistic conditions and highlight the resulting opportunities. T2 - 19th International Symposium on Olfaction and Electronic Nose CY - Aveiro, Portugal DA - 29.05.2022 KW - Aerial robot KW - TDLAS KW - Inter-robot measurements KW - Gas tomography KW - Plume PY - 2022 SN - 978-1-6654-5860-3 DO - https://doi.org/10.1109/isoen54820.2022.9789627 SP - 1 EP - 3 PB - IEEE CY - USA AN - OPUS4-54926 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erning, Johann Wilhelm ED - Stojanovic, I. T1 - Hygienic assessment of SLM-printed stainless steel N2 - Electrochemical measurements for the hygienic assessment of additively manufactured products are discussed. The Assessment and details of the material are described, examples for the application are given. N2 - Elektrochemische Messungen zur hygienischen Bewertung additiv gefertigter Bauteile werden diskutiert. Die Bewertung und Details des Werkstoffs werden beschrieben, Anwendungsbeispiele gezeigt. T2 - Kormat 2022 CY - Online meeting DA - 26.04.2022 KW - Korrosion KW - Trinkwasser KW - Hygienische Bewertung KW - Additive Fertigung PY - 2022 SN - 1848-4255 SP - 21 EP - 25 PB - Proceedings of the Croatian Society for Material Protection CY - Zagreb AN - OPUS4-54932 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fürst, Richard A1 - Häßler, Dustin A1 - Peter, A. A1 - Rohleder, R. A1 - Hothan, Sascha T1 - European test standard intumescent coatings applied to steel tension bars with solid section N2 - Intumescent coatings are used in civil engineering to improve the fire resistance of steel constructions. Due to the thin coating thickness and the profile-following application, the architectural appearance of the steel structure can be preserved. EN 13381-8 provides regulations to determine the contribution to the fire resistance of intumescent coatings applied to steel beams and columns. The scope of this standard excludes tension members and steel members with solid sections. For products that have already been successfully tested and assessed on beams and columns, EN 13381-10 offers the possibility based on unloaded fire tests to extend the scope of application of intumescent coatings to tension bars with solid sections. This approach contradicts the national safety level in Germany, where mechanically loaded testing is mandatory. Therefore, a new part of the test standard series EN 13381 is currently developed to enable the application of intumescent coatings on steel tension bars with solid section based on mechanically loaded fire tests. BAM has already carried out numerous fire tests on loaded steel tension members with intumescent coatings. Currently, in the BAM research project FIRESTEMIC, the influence of the steel bar orientation and the profile type on the thermal performance of intumescent coatings are investigated. Both questions concerning the thermal protection ability of intumescent coatings were analysed based on three different test sets, which were carried out in the tension furnace (Fig. 1a). The fire exposure corresponds to the standard temperature-time curve according to EN 1363-1. This paper summarises the main findings from the fire tests conducted in the FIRESTEMIC project. The results serve as an experimental background for the proposal of the new standard. Regarding the bar orientation, a new test setup was developed and proposed for the new standard. The two tested commercial water-based intumescent coatings with applied dry film thickness from 1.5 mm to 2.5 mm showed only a slight dependence on the bar orientation. In terms of the steel profile type, circular and rectangular solid sections with identical section factor and applied dry film thickness were tested. It was observed that the circular solid bars with diameter 30 mm heat up faster compared to the solid rectangular bars with dimension 30×30 mm (Fig. 1b). Also at larger steel bars, i.e. diameter 40 mm and dimension 40×40 mm, the same trend occurred. Thus, it is recommended for the new test standard to allow a transfer of the test results from circular to rectangular solid sections. In addition, the paper will describe and explain the test and assessment procedure proposed for the newly developed standard. T2 - 8th Symposium Structural Fire Engineering CY - Brunswick, Germany DA - 13.09.2022 KW - Fire test KW - Steel KW - Tension member KW - Intumescent coating KW - Test standard PY - 2022 SP - 1 EP - 14 PB - TU Braunschweig CY - Braunschweig AN - OPUS4-55703 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Patzelt, Anne-Katrin A1 - Krentel, Daniel A1 - Wiesner, Anja T1 - InnoBOSK - Ergebnisse der Bedarfserhebung N2 - Im Projekt InnoBOSK wurden insgesamt vier wissenschaftlich basierte Bedarfserhebungsworkshops durchgeführt. Die Workshops hatten jeweils thematische Schwerpunkte und wurden mit Vertretern unterschiedlicher BOS (Behörden und Organisationen mit Sicherheitsaufgaben) durchgeführt. In der vorliegenden Arbeit werden die erhobenen Bedarfe ausgewertet. KW - BOS KW - InnoBOSK KW - Bedarfserhebung KW - Forschungsbedarf PY - 2022 SP - 1 EP - 23 AN - OPUS4-55831 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Viefhues, Eva T1 - Subspace-based damage detection in engineering structures considering reference uncertainties and temperature effects N2 - Automated vibration-based damage detection is of increasing interest for structural health monitoring of engineering structures. In this context, stochastic subspace-based damage detection (SSDD) compares measurements from a testing state to a data-driven reference model in a statistical framework. In this thesis theoretical developments have been proposed to improve the robustness of SSDD for realistic applications conditions. First, a statistical test has been proposed considering the statistical uncertainties about the model obtained from the reference data. This leads to a precise description of the test’s distribution properties and damage detection thresholds. Second, an approach has been developed to account for environmental effects in SSDD. Based on reference measurements at few different environmental conditions, a test is derived with respect to an adequate interpolated reference. The proposed methods are validated in numerical simulations and applied to experimental data from the laboratory and outdoor structures. KW - Damage detection KW - Subspace methods KW - Vibrations KW - Uncertainty quantification KW - Environmental effects KW - Civil structures PY - 2021 SP - 1 EP - 191 CY - Universite de Rennes AN - OPUS4-55774 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Junge, P. A1 - Stargardt, Patrick A1 - Kober, D. A1 - Greinacher, M. A1 - Rupprecht, C. T1 - Thermally Sprayed Al2O3 Ceramic Coatings for Electrical Insulation Applications N2 - Thermal spraying enables a fast and propelling way to additively deposit various ceramics as electric insulators, which are used in conditions where polymers are not suitable. Alumina (Al2O3) is among the most employed materials in the coating industry since it exhibits good dielectric properties, high hardness, high melting point while still being cost-effective. Various parameters (e.g. feedstock type, plasma gas mixture, plasma power) significantly influence the resulting coating in terms of microstructure, porosity, crystallinity, and degree of un-or molten particles. As a consequence, these parameters need to be investigated to estimate the impact on the electrical insulating properties of thermally sprayed alumina. This study focuses on the development of a novel electric insulation coating from Al2O3 feedstock powders deposited via atmospheric plasma spray (APS). The microstructure, porosity, and corresponding crystallographic phases have been analyzed with optical microscopy, XRD, and SEM images. To achieve an understanding of the parameters influencing the electrical insulation performance of the manufactured coatings, an in-depth analysis of the fundamental dielectric parameters e.g., DC resistance, breakdown strength, dielectric loss tangent, permittivity is presented. T2 - International Thermal Spray Conference and Exposition 2022 CY - Vienna, Austria DA - 04.05.2022 KW - Thermal Spray KW - Alumina KW - Dielectric properties PY - 2022 SP - 1 EP - 8 AN - OPUS4-55821 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brence, Blaž A1 - Lugovtsova, Yevgeniya A1 - Prager, Jens T1 - Interdigital Transducers for Structural Health Monitoring N2 - Interdigital transducers (IDTs) are a well-known tool for excitation of surface acoustic waves. The use of IDTs is versatile, but they are most commonly employed as actuators for excitation of ultrasonic guided waves (UGWs). However, they are still a relatively new technology, which leaves many possibilities for future research, especially in the scope of newly emerging structural health monitoring (SHM) systems. IDTs offer low weight, design flexibility and beam directivity, which make them ideal candidates for employment in such systems. Due to the IDTs’ and waves’ complexity, problems often cannot be described analytically, therefore they require numerical solutions and experimental validations. In this contribution, a novel, simple use of IDTs, in the scope of SHM is described. Firstly, numerical findings acquired with finite element method are presented. To validate those results, experiments in a plate-like waveguide are carried out. A good agreement between them is found. The results show the potential of the IDTs in yet another prospective application, which could be attractive for adoption in the future. T2 - 48. Jahrestagung für Akustik (DAGA) CY - Stuttgart, Germany DA - 21.03.2022 KW - Lamb waves KW - Ultrasonic Guided Waves KW - Selective excitation PY - 2022 SP - 221 EP - 224 AN - OPUS4-55501 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schuberth, J. A1 - Ebert, T. A1 - Schlegel, Moritz-Caspar A1 - Rödig, L. A1 - Jepsen, D. T1 - A Front-Runner Approach for EU product policy - Impulse for raising untapped energy saving potentials N2 - In 2020, the European Commission has announced to propose a Sustainable Product Policy for the EU which shall ensure that the performance of front-runners in sustainability progressively becomes the norm. In addition, the European Commission has re-emphasised the necessity to significantly improve the effectiveness of the current Ecodesign framework for energy-related products. With this paper, we present an initial outline of a policy approach which we call the “EU frontrunner approach”. The approach aims at installing a regulatory framework which enables a semi-automated, progressive adaptation of ecodesign minimum requirements for products. It builds on performance levels of the best products available on the market by aggregating information in a database. The “front-runner approach” could first be applied to progressively adapt product-related minimum energy-efficiency requirements. This way it would serve as a starting point to introduce this conceptto the EU policy arena. While the approach can be applied for energy efficiency, it is neither limited to energy-related products nor to energy-related requirements. It can be applied to the wide range of nonenergy related products within the scope of the upcoming Ecodesign for Sustainable Products Regulation (ESPR) as well as to non-energy-related requirements, such as minimum requirements for durability, reparability, recyclability and recycled content. KW - Ecodesign KW - Energy Labelling KW - Circular Economy KW - Efficiency KW - Policy making PY - 2022 UR - https://www.umweltbundesamt.de/publikationen/a-front-runner-approach-for-eu-product-policy SP - 1 EP - 12 PB - German Environment Agency CY - Dessau-Roßlau AN - OPUS4-55503 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simbruner, Kai A1 - Billone, M. C. A1 - Zencker, Uwe A1 - Liu, Y. Y. A1 - Völzke, Holger T1 - Brittle Failure Analysis of High-Burnup PWR Fuel Cladding Alloys N2 - The general aim of this research is the development of methods for predicting mechanical behavior and identification of limiting conditions to prevent brittle failure of high-burnup (HBU) pressure water reactor (PWR) fuel cladding alloys. A finite element (FE) model of the ring compression test (RCT) was created to analyze the failure behavior of zirconium-based alloys with radial hydrides during the RCT. An elastic-plastic material model describes the zirconium alloy. The stress-strain curve needed for the elastic-plastic material model was derived by inverse finite element analyses. Cohesive zone modeling is used to reproduce sudden load drops during RCT loading. Based on the failure mechanism in non-irradiated ZIRLO® claddings, a micro-mechanical model was developed that distinguishes between brittle failure along hydrides and ductile failure of the zirconium matrix. Two different cohesive laws representing these types of failure are present in the same cohesive interface. The key differences between these constitutive laws are the cohesive strength, the stress at which damage initiates, and the cohesive energy, which is the damage energy dissipated by the cohesive zone. Statistically generated matrix-hydride distributions were mapped onto the cohesive elements and simulations with focus on the first load drop were performed. Computational results are in good agreement with the RCT results conducted on high-burnup M5® samples. It could be shown that crack initiation and propagation strongly depend on the specific configuration of hydrides and matrix material in the fracture area. T2 - 26th International Conference on Structural Mechanics in Reactor Technology - SMiRT 26 CY - Potsdam, Germany DA - 10.07.2022 KW - Cladding Embrittlement KW - Cohesive Zone Modelling KW - Spent Nuclear Fuel KW - Ring Compression Test PY - 2022 SP - 1 EP - 10 AN - OPUS4-55434 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Linnemann, Konrad A1 - Komann, Steffen A1 - Wille, Frank A1 - Reiche, I. A1 - Ramsay, J. T1 - New Sco-III regulations to ship large objects as surface contaminated objects N2 - The decommissioning or refurbishment of nuclear facilities necessitates either the storage or disposal of large radioactive components such as steam generators, pressurizers, reactor pressure vessels and heads, and coolant pumps, to list the major contributors. These components or objects are large in size and mass, measuring up to approximately 6 meters in diameter, up to 20 meters in length, and weighing over 400 000 kg. In many situations, the components are transported off-site to a storage, disposal or recycling/treatment facility. Previously, many large objects had to be transported under special arrangement. The latest 2018 edition of the International Atomic Energy Agency (IAEA) Regulations for the Safe Transport of Radioactive Material, No. SSR-6 [1], incorporates regulations for the shipment of large objects as a new category of surface contaminated object, SCO-III, based on the IAEA “performance package” concept. This paper provides background and practical guidance on these regulations. Additionally, the experiences of BAM with the appoval of two steam converters of the NPP Lingen are presented as the first approval process for SCO-III objects in Germany. The primary additions to SSR-6 include SCO-III classification and requirements, approval and administrative requirements for the new classification, and the addition of SCO-III to the proper shipping name for UN 2913. Advisory material drafted for the new requirements will be included in the next revision of SSG-26, Advisory Material for the IAEA Regulations for the Safe Transport of Radioactive Material, expected to be published soon. Note that at this time the proposed provisions for large objects do not include components such as reactor vessels, due to the more limited experience and greater radioactivity levels. The SCO-III concept lays the groundwork and may be extended to cover other large objects that are classified as low specific activity (LSA) material in the future. T2 - Kerntechnik 2022 CY - Leipzig, Germany DA - 21.06.2022 KW - Transport packages KW - Radioactive materials KW - SCO-III KW - Large objects PY - 2022 SP - 1 EP - 7 AN - OPUS4-55423 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Plarre, Rüdiger A1 - Busweiler, Sabine A1 - Haustein, V. A1 - von Laar, C. A1 - Haustein, T. ED - Bueno-Mari, R. ED - Montalvo, T. ED - Robinson, W. H. T1 - Korynetes caeruleus (coleoptera: cleridae) for biological control of anobium punctatum (coleoptera, ptinidae) N2 - Larvae and adults of Korynetes caeruleus (de Geer 1775) (Coleoptera: Cleridae) were collected from old churches and reared in the laboratory on Anobium punctatum (de Geer 1774) (Coleoptera, Ptinidea, formerly Anobiidae). Breeding success of K. caeruleus was low, but basic parameters of this species’ developmental cycle were identified. At 21 °C and 75 % relative humidity and a four-month cold period at 4 °C, the development of K. caeruleus from egg to adult appearance lasted 2 years. The pupal stage may be reached and completed after one and a half years. Feeding on larvae of A. punctatum by larvae of K. caeruleus was observed and consisted of a combination of sucking haemolymph and consuming body parts. The sickle-like mandibles of larvae of K. caeruleus penetrate the cuticle of prey larvae followed by pumping and sucking body movements. Adult beetles of A. punctatum were not attacked by K. caeruleus larvae. Feeding behavior of adult K. caeruleus was not investigated. T2 - 10th International Conference on Urban Pests CY - Barcelona, Spain DA - 26.06.2022 KW - Cultural heritage KW - Biological pest control KW - Life history data KW - Wood protection PY - 2022 SN - 978-84-09-41424-6 SP - 34 EP - 44 AN - OPUS4-55170 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilke, Olaf A1 - Seeger, Stefan A1 - Brödner, Doris A1 - Erdmann, Kerstin A1 - Rasch, Fabian T1 - Chemical characterization of ultra-fine particles released from laser printers N2 - 11 laser printers from 5 manufacturers were purchased in 2017 and tested for their UFP emissions. Size resolved sampling of the emitted particles was done with a 13 stage (30 nm to 10 µm) low pressure cascade impactor. The sampled particles were analysed for their chemical composition by thermal extraction (vaporization at 290°C) followed by GC-MS analysis. High boiling cyclic siloxanes (D10 to D16) were detected as constituents of UFP from laser printers. In comparison to measurements in 2008, aliphatic long-chain alkanes (C22 to C34) were detected additionally as chemical constituents of UFP from most of the tested printers and their amounts were higher than for cyclic siloxanes. Printers of one manufacturer showed very low UPF emissions compared to the other manufacturers. T2 - Indoor Air Conference 2022 CY - Kuopio, Finland DA - 12.06.2022 KW - UFP KW - Thermal extraction KW - Cascade impactor PY - 2022 SP - 1 EP - 4 AN - OPUS4-55106 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Plarre, Rüdiger A1 - Cabral, U. A1 - Querner, P. ED - Ryder, S. ED - Crossman, A. T1 - Screening of two plant-derived extracts from Sri Lanka for their potential to control the subterranean termite Coptotermes formosanus N2 - The tropical environment of Sri Lanka accelerates bio-deterioration of cultural objects. Termites are one of the most damaging insect pests destroying the cellulose components of historical artifacts. Herbal extracts obtained from resin of Vateria copallifera (Retzius) Alston and seeds of Madhuca longifolia (Konig) Macbride have been used for centuries to preserve e.g. palm leaf manuscripts from insect attack. Herbal extractions of these traditional products for palm leaf manuscript were tested for their effect against the termite species Coptotermes formosanus Shiraki, 1909. Natural and artificial aged herbal extractions were tested to obtain a repellent index. Resin oil of V. copallifera caused slightly higher repellencies than M. longifolia. Artificially aged samples produced lower repellencies than naturally aged samples. The results indicate that the active ingredients are volatile. The potential for barrier treatment was tested only with V. copallifera. Tunnelling-behavior of C. formosanus workers through sand in the presence of V. copallifera resin oil was largely reduced. T2 - Pest Odyssey The Next Generation CY - Online meeting DA - 20.09.2021 KW - IPM in museums KW - Termite control KW - Essential oils KW - Library pests PY - 2022 SN - 978-1-909492-83-7 SP - 56 EP - 62 PB - Archetyp Publication LTD CY - London AN - OPUS4-54736 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hufschläger, Daniel A1 - Gaal, Mate T1 - Sending and receiving acoustic waves using atmospheric pressure plasmas N2 - Atmospheric pressure plasmas interact in various physical ways with their surroundings. They release heat and generate charge carriers, which leads to two effects. The first effect is the generation of acoustic waves due to heat release, known as the thermoacoustic effect, and the second effect is the perturbation of the resting fluid provoked by the release of charge carriers, called “ionic wind”. The direct connection between the charge carrier production of the discharge arrangement and the surroundings also allows the detection of acoustic waves by tracking the electrical current of the arrangement. This contribution introduces a multi-fluid model approach to describe the acoustic interaction of atmospheric plasmas. In addition, we present experimental results on commercially available and in-house fabricated discharge arrangements for either emitting or receiving acoustic waves. T2 - DAGA 2022 - 48. Jahrestagung für Akustik CY - Stuttgart, Germany DA - 21.03.2022 KW - Plasma acoustics KW - Atmospheric pressure discharges KW - Ait-coupled ultrasound PY - 2022 SN - 978-3-939296-20-1 VL - 48 SP - 923 EP - 926 CY - Berlin AN - OPUS4-54681 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bischoff, Tristan T1 - Testing and evaluating norms for hot water storage tank efficiency N2 - A round robin test was performed with different laboratories comparing the results for standing heat losses of hot water storage tanks utilizing the current norms for testing. Evaluating these results provides an empirical basis for further developing testing methods. T2 - Conference of young scientists on energy and natural science issues 2022 CY - Kaunas, Lithuania DA - 24.05.2022 KW - Heat storage KW - Standing Losses KW - EU regulations KW - Statistical Analysis KW - Round Robin Test KW - Energy-Label KW - NAPE Project PY - 2022 SN - 2783-6339 SP - 133 EP - 135 AN - OPUS4-55852 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - George, Janine T1 - JaGeo/Advanced_Jobflow_Tutorial: v.0.1.0 N2 - This tutorial is aimed at developers who would like to develop workflows with Jobflow. This could include contributions to atomate2 and quacc. Jobflow workflows can also be executed with Fireworks on Supercomputers. This tutorial includes information on how to write a job for jobflows, how to connect jobs to a workflow including dynamic features and how to store job results in databases. The structure of the workflow is inspired by workflows that have been developed for atomate2 and quacc. This tutorial is also connected to google collab so that you can execute the code via their services. Please access the tutorial here: https://jageo.github.io/Advanced_Jobflow_Tutorial/intro.html KW - Automation KW - Computational Materials Science PY - 2023 UR - https://jageo.github.io/Advanced_Jobflow_Tutorial/intro.html DO - https://doi.org/10.5281/zenodo.8004401 PB - Zenodo CY - Geneva AN - OPUS4-57588 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lu, Xin A1 - Hicke, Konstantin A1 - Krebber, Katerina T1 - Dual functionality of wavelength scanning coherent optical time domain reflectometer N2 - Wavelength scanning coherent optical time domain reflectometer (WS-COTDR) is a good candidate to spatially resolve the environmental information at comparatively low frequency. This paper reveals it can also work as a traditional optical time domain reflectometer (OTDR) to identify Fresnel reflection by averaging the obtained signal over the wavelength scanning range. Simultaneous distributed vibration sensing and a traditional OTDR measurement are experimentally demonstrated using the WS-COTDR system. T2 - European Workshop on Optical Fibre Sensors (EWOFS 2023) CY - Mons, Belgium DA - 23.05.2023 KW - Structural health monitoring KW - Distributed fiber sensing KW - Acoustic sensing PY - 2023 DO - https://doi.org/10.1117/12.2678098 VL - 12643 SP - 1 EP - 4 PB - SPEI AN - OPUS4-57590 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Königsbauer, Korbinian A1 - Wosniok, Aleksander A1 - Nöther, N. A1 - Schaller, M. B. T1 - POF-based digital I-OFDR for strain detection in road construction N2 - We report on the development of a field-proven distributed fiber optic sensing system for structural health monitoring in road construction and civil engineering. The system is based on a cost-efficient digital incoherent optical frequency domain reflectometry (I-OFDR) for distributed strain detection along a polymer optical fiber. In this method, the strain-induced backscatter increase in a graded-index multimode perfluorinated polymer optical fiber (PF-POF) is determined by measuring the complex transfer function of the sensing fiber using a compact digital data acquisition unit. T2 - European Workshop on Optical Fibre Sensors (EWOFS 2023) CY - Mons, Belgium DA - 23.05.2023 KW - Digital I-OFDR KW - Perfluorinated polymer optical fiber KW - Smart geosynthetics KW - Structural health monitoring KW - Road construction KW - Civil engineering PY - 2023 DO - https://doi.org/10.1117/12.2678436 SP - 1264326-1 PB - SPIE AN - OPUS4-57592 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Naik, Aakash A1 - Ertural, Christina A1 - Dhamrait, Nidal A1 - Benner, Philipp A1 - George, Janine T1 - Quantum-Chemical Bonding Database (Unprocessed data : Part 8) N2 - This data is associated with the manuscript "A Quantum-Chemical Bonding Database for Solid-State Materials." Refer to mpids.txt to see data related to which compounds are available in the tar file. (mp-xxx refer to Materials Project ID) KW - Bonding analysis KW - Automation KW - Materials Informatics KW - Computational Chemistry KW - Database PY - 2023 DO - https://doi.org/10.5281/zenodo.7852823 PB - Zenodo CY - Geneva AN - OPUS4-57448 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Winkler, Nicolas P. A1 - Johann, Sergej A1 - Kohlhoff, Harald A1 - Neumann, Patrick P. T1 - Revisiting Environmental Sensing Nodes: Lessons Learned and Way Forward N2 - Setting up sensors for the purpose of environmental monitoring should be a matter of days, but often drags over weeks or even months, preventing scientists from doing real research. Additionally, the newly developed hardware and software solutions are often reinventing existing wheels. In this short paper, we revisit the design of our environmental sensing node that has been monitoring industrial areas over a span of two years. We share our findings and lessons learned. Based on this, we outline how a new generation of sensing node(s) can look like. T2 - SMSI 2023 Conference Sensor and Measurement Science International CY - Nuremberg, Germany DA - 08.05.2023 KW - Sensing node KW - Sensor network KW - Environmental monitoring KW - Low-cost KW - LoRaWAN PY - 2023 SN - 978-3-9819376-8-8 DO - https://doi.org/10.5162/SMSI2023/C5.1 SP - 173 EP - 174 PB - AMA Service GmbH CY - Wunstorf AN - OPUS4-57454 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gaal, Mate A1 - Hufschläger, Daniel A1 - Gohlke, Dirk A1 - Weise, Matthias A1 - Ilse, D. A1 - Hillger, W. A1 - Szewieczek, A. T1 - Thermoakustische und Ferroelektret-Wandler als Phased-Array-Sender für luftgekoppelte Ultraschallprüfung N2 - Die üblichen Verfahren der zerstörungsfreien Prüfung mit Ultraschall basieren auf der Verwendung von flüssigen Koppelmitteln. Luftgekoppelte Prüfung setzt sich gegen die konventionellen Verfahren durch, wenn die Flüssigkeit nicht erwünscht oder den Prüfling gar beschädigen kann. Zwei Technologien für Erzeugung von Ultraschallsignalen sind vielversprechend: thermoakustische Wandler und Ferroelektret-Wandler. Basierend auf diesen beiden Technologien wurden Array-Sender gebaut und in diesem Beitrag miteinander verglichen. Thermoakustische Wandler basieren auf Dünnschichttechnologie und bieten eine resonanzfreie Erzeugung von Ultraschall. Sie bestehen aus einer dünnen elektrisch leitenden Schicht und werden mit kurzen elektrischen Pulsen angeregt. Die Erhöhung der thermischen Energie führt zur Erzeugung von akustischen Wellen in der umgebenden Luft. Bei Ferroelektret-Wandlern handelt es sich um polarisierte zelluläre Kunststoffe, die für den Bau eines Array-Senders besonders gut geeignet sind. Einige Ferroelektrete weisen eine hervorragende an Luft angepasste akustische Impedanz auf, so dass auf den Einsatz von Anpassschichten verzichtet werden kann. Ein sehr niedriges mechanisches Übersprechen zwischen einzelnen Elementen ermöglicht eine unabhängige Anregung einzelner Elemente, was bei Piezokompositen deutlich schwieriger wäre. Mit der Phased-Array-Technik können elektronische Fokussierung oder Schwenkung des Einschallwinkels für eine luftgekoppelte Prüfung genutzt werden. Die Schallfelder von diesen beiden Technologien wurden berechnet, gemessen und miteinander verglichen. Die Vorteile und Nachteile der beiden Technologien werden dargestellt. T2 - DAGA 2023 Jahrestagung für Akustik CY - Hamburg, Germany DA - 06.03.2023 KW - Luftgekoppelte Ultraschallprüfung KW - Thermoakustik KW - Ferroelektret KW - Phased Array PY - 2023 UR - https://pub.dega-akustik.de/DAGA_2023 SN - 978-3-939296-21-8 SP - 1594 EP - 1597 AN - OPUS4-57554 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gaal, Mate A1 - Hufschläger, Daniel A1 - Gohlke, Dirk A1 - Weise, Matthias A1 - Ilse, D. A1 - Hillger, W. A1 - Szewieczek, A. T1 - Phased-Array-Prüfköpfe für luftgekoppelte Ultraschallprüfung auf Basis von zellulären Kunststoffen N2 - Luftgekoppelte Ultraschallprüfung setzt sich immer häufiger gegen die konventionelle Ultraschallprüfung von Leichtbaukomponenten durch, und zwar in vielen Industriezweigen von der Holzindustrie bis zur Luftfahrt. Während die Phased-Array-Technik mittlerweile zu dem industriellen Standard im Bereich der Prüfung mit Ankopplung gehört, wird luftgekoppelte Ultraschallprüfung meist mit zwei Wandlern in Durchschallung durchgeführt. Deswegen werden Vorteile der Phased-Array-Technik wie beispielsweise elektronische Fokussierung oder Schwenkung des Einschallwinkels für luftgekoppelte Prüfung selten genutzt. In diesem Beitrag werden die laufenden Arbeiten an der Entwicklung eines neuen Phased-Array-Geräts vorgestellt, mit dem Schwerpunkt an der Charakterisierung der Prüfköpfe und ihrer Schallfelder. Das Gerät besteht aus einem linearen Phased-Array-Prüfkopf, einer Sende- und einer Empfangseinheit. Die Hauptinnovation unserer Arbeit ist die Anwendung von zellulären Kunststoffen für den Bau eines Arrays, wobei der Sender mit Hochspannung von ca. 1500 V angeregt wird. Geladene zelluläre Polymere werden auch Ferroelektrete oder Piezoelektrete genannt. Sie weisen ein sehr niedriges Elastizitätsmodul und dadurch eine niedrige akustische Impedanz auf, so dass auf den Einbau von Anpassschichten verzichtet werden kann. Eine sehr niedrige mechanische Kreuzkopplung bei Ferroelektreten ermöglicht eine unabhängige Anregung einzelner Elemente, was bei Piezokompositen deutlich schwieriger wäre. Die Entwicklung der Array-Prüfköpfe wurde durch Berechnungen des Schallfeldes unterstützt, die auf Punktquellensynthese basieren. Die beabsichtigte Anwendung von Phased-Array-Prüfköpfen und des Prüfsystems sind die Durchschallung mit Fokussierung, elektronischer Scan und die Schwenkung des Einschallwinkels zur Anregung von geführten Wellen, angewandt an carbonfaserverstärkten Kunststoffen und ähnlichen Materialien. Die Anwendung von geführten Wellen bietet die Perspektive, Bauteile mit einseitiger Zugänglichkeit zu prüfen. T2 - DACH-Jahrestagung 2023 CY - Friedrichshafen, Germany DA - 15.05.2023 KW - Luftgekoppelte Ultraschallprüfung KW - Ferroelektret KW - Ultraschallwandler KW - Phased Array PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-575564 SP - 1 EP - 6 AN - OPUS4-57556 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hufschläger, Daniel A1 - Gohlke, Dirk A1 - Weise, Matthias A1 - Bente, K. A1 - Gaal, Mate T1 - Thermoakustische Gruppenstrahler: Theorie und Anwendungen N2 - Bei der Prüfung von Werkstücken mit empfindlichen Oberflächen oder auch hydrophilen Werkstoffen sind traditionelle ultraschallbasierte zerstörungsfreie Prüfmethoden wie die Kontakttechnik oder die Tauchtechnik in vielen Anwendungsfällen aufgrund der Flüssigkeitsankopplung nicht anwendbar. Die luft-gekoppelte Ultraschallprüfung umgeht diese Problematik und eröffnet neue Prüfszenarien. Derzeit werden zwei Varianten der Schallerzeugung als vielversprechend angesehen: ferroelektrische Folien und thermoakustische Dünnschichtwandler. Thermoakustische Wandler ermöglichen die resonanzfreie Erzeugung von Ultraschall und somit kurze zeitliche Impulse sowie eine sehr breitbandige Anregung. Durch die Verwendung von gekrümmten Substraten ist sowohl eine Herstellung von planaren als auch fokussierten Wandlern möglich. Dieser Beitrag präsentiert die letzten Forschungsergebnisse im Bezug auf thermoakustischen Wandlern, welche derzeit in einen thermoakustischen Gruppenstrahler münden. Gruppenstrahler erlauben die simultane Änderung des Einschallwinkels, sowie die Verschiebung des Fokuspunktes während der Verwendung. Durch die Verbindung beider Schlüsseltechnologien, der thermoakustischen Anregung und des Gruppenstrahlerprinzips, wird das Spektrum der klassischen ZfP-Anwendungen, sowie moderner Ansätze wie der Anregung von geführten Wellen oder der Strukturüberwachung erheblich erweitert und bereichert. Dabei soll innerhalb dieses Beitrages auf die Modellierung des Schallfeldes, die elementweise Charakterisierung und verschiedene Anwendungsszenarien eingegangen werden. T2 - DACH-Jahrestagung 2023 CY - Friedrichshafen, Germany DA - 15.05.2023 KW - Luftgekoppelte Ultraschallprüfung KW - Thermoakustik KW - Ultraschallwandler KW - Phased Array PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-575599 SP - 1 EP - 6 AN - OPUS4-57559 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmitt, M. A1 - Casperson, Ralf A1 - Baensch, F. T1 - Ein Überblick über die Normung in der zerstörungsfreien Prüfung N2 - Normung und Standardisierung in der zerstörungsfreien Prüfung finden auf nationaler, europäischer und internationaler Ebene statt. Durch die Übernahme von Leitungsfunktionen in diesen Gremien kann ein deutlicher steuernder Einfluss auf Themen und Inhalte der Normen genommen werden. Unabdingbar für den Erfolg ist zusätzlich das persönliche Engagement der Fachexpert*innen in den nationalen Gremien und den europäischen und internationalen Arbeitsgruppen. Denn wer nicht normt wird genormt und muss letztlich Regeln verwenden, die andere entsprechend ihrer eigenen Interessen gestalten. Voraussetzung für die Teilnahme in europäischen und internationalen Normungsgremien ist die Mitwirkung in den entsprechenden nationalen Spiegelgremien der nationalen Normungsinstitute, welche die europäischen und internationalen Aktivitäten spiegeln und die Fachexperten für die Mitarbeit autorisieren. Gezeigt werden die relevante Gremienstruktur auf internationaler Ebene (ISO/TC 135 “Non-destructive testing”, ISO/TC 44/SC 5 “Testing and inspection of welds”), auf europäischer Ebene (CEN/TC 138 “Zerstörungsfreie Prüfverfahren”), die Struktur der nationalen deutschen Spiegelgremien, das Zusammenspiel der Gremien, und die Einflussmöglichkeiten. T2 - DACH-Jahrestagung 2023 CY - Friedrichshafen, Germany DA - 15.05.2023 KW - Normung PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-575759 UR - https://jahrestagung.dgzfp.de/Portals/jt2023/bb/P4.pdf VL - 2023 SP - 1 EP - 6 PB - DGZfP CY - Berlin AN - OPUS4-57575 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Xu, R. A1 - Hicke, Konstantin A1 - Chruscicki, Sebastian A1 - Marx, S. ED - Curbach, M. ED - Marx, S. ED - Scheerer, S. ED - Hampel, T. T1 - Akustisches SpRK-Monitoring mit SEA und verteilten faseroptischen Sensoren N2 - Im vorliegenden Bericht wurde untersucht, Spanndrahtbrüche in einem Brückenträger sowohl mittels Schallemissionsanalyse (SEA) als auch mit (eingebetteter) verteilter faseroptischer akustischer Sensorik (DAS) zu erkennen. Die Ergebnisse zeigen, dass die Bruchsignale anhand beider Messverfahren detektiert werden können. Die jeweils detektierten Drahtbrüche werden miteinander verglichen. Durch eine Gegenüberstellung werden SEA und DAS detailliert dargestellt. T2 - 12. Symposium "Experimentelle Untersuchungen von Baukonstruktionen" (SEUB) CY - Dresden, Germany DA - 01.06.2023 KW - Verteilte faseroptische akustische Sensorik KW - DAS KW - Brückenmonitoring KW - Spanndrahtbruchdetektion KW - Schallemissionsanalyse KW - SEA PY - 2023 SN - 978-3-86780-740-1 SN - 1613-6934 VL - 67 SP - 136 EP - 147 PB - Technische Universität Dresden - Fakultät Bauingenieurwesen CY - Dresden AN - OPUS4-57581 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schilling, Markus T1 - Tensile Test Ontology (TTO) N2 - This is the stable version 2.0.1 of the PMD ontology module of the tensile test (Tensile Test Ontology - TTO) as developed on the basis of the 2019 standard ISO 6892-1: Metallic materials - Tensile Testing - Part 1: Method of test at room temperature. The TTO was developed in the frame of the PMD project. The TTO provides conceptualizations valid for the description of tensile test and corresponding data in accordance with the respective standard. By using TTO for storing tensile test data, all data will be well structured and based on a common vocabulary agreed on by an expert group (generation of FAIR data) which will lead to enhanced data interoperability. This comprises several data categories such as primary data, secondary data and metadata. Data will be human and machine readable. The usage of TTO facilitates data retrieval and downstream usage. Due to a close connection to the mid-level PMD core ontology (PMDco), the interoperability of tensile test data is enhanced and data querying in combination with other aspects and data within the broad field of material science and engineering (MSE) is facilitated. The TTO class structure forms a comprehensible and semantic layer for unified storage of data generated in a tensile test including the possibility to record data from analysis, re-evaluation and re-use. Furthermore, extensive metadata allows to assess data quality and reproduce experiments. Following the open world assumption, object properties are deliberately low restrictive and sparse. KW - Ontology KW - Tensile Test KW - Digitalization KW - Plattform MaterialDigital KW - Structured Data PY - 2023 UR - https://github.com/MarkusSchilling/application-ontologies/blob/479311832819af695a2c64fa8eb772f2da398061/tensile_test_ontology_TTO/pmd_tto.ttl UR - https://github.com/materialdigital/core-ontology/blob/59f5727b0437ceea5e3d9fcb8fcd0ac211e92cc3/pmd_tto.ttl PB - GitHub CY - San Francisco, CA, USA AN - OPUS4-57935 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Plarre, Rüdiger A1 - Busweiler, Sabine A1 - von Laar, C. A1 - Haustein, V. A1 - Haustein, T. T1 - Holzwurm Smoothie - Der Energy-Drink für den Blauen Fellkäfer N2 - Lange kann sich eine Larve des kleinen Holzwurms oder Gemeinen Nagekäfers [Anobium punctatum] nicht wehren, wenn sie vom Blauen Fellkäfer [Korynetes caeruleus] aufgespürt und attackiert wird. Gnadenlos schlagen die kräftigen Zangen am Kopf des Räubers durch die weiche Haut des Schädlings. KW - Holzwurm KW - Holzschutz KW - Biologische Schädlingsbekämpfung PY - 2023 IS - 74 SP - 16 EP - 18 AN - OPUS4-57835 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kröll, Mirco T1 - Benefits of novel tools open to Industry from Open Innovation Testbeds. Effects of harmonised procedures in (digital) Tribology N2 - The work on Tribology, digitalisation, and the harmonised procedures developed in i-TRIBOMAT Open Innovation Testbed was presented. The project develops procedures and shares ideas on how to deal with characterisation techniques and provide services to end users in different places and locations, which is realised by adopting a common and widely agreed procedures. i-TRIBOMAT is active also via YouTube platform to enhance communication and spread the word amongst the interested parties and society. T2 - Workshop of NanoMECommons project: "Materials characterisation challenges to support the industry transition in the digital era" CY - Online meeting DA - 13.12.2021 KW - Tribology KW - i-TRIBOMAT KW - Characterisation KW - Digitalisation KW - Interoperability KW - Harmonisation KW - Green Deal PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-548909 DO - https://doi.org/10.5281/zenodo.6339985 SP - 14 EP - 17 AN - OPUS4-54890 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lecompagnon, Julien A1 - Hirsch, Philipp Daniel A1 - Rupprecht, C. A1 - Ziegler, Mathias T1 - Hochaufgelöste thermografische Detektion eingeschlossener Defekte mit Hilfe von 2Dstrukturierten Beleuchtungsmustern N2 - Für die aktive Thermografie als zerstörungsfreie Prüfmethode galt lange Zeit die Faustformel, dass die Auflösung interner Defekte/Inhomogenitäten auf ein Verhältnis von Defekttiefe/Defektgröße ≤ 1 beschränkt ist. Die Ursache hierfür liegt in der diffusiven Natur der Wärmeleitung in Festkörpern. Sogenannte Super-Resolution-Ansätze erlauben seit Kurzem die Überwindung dieser physikalischen Grenze um ein Vielfaches. Damit ergibt sich die attraktive Möglichkeit die Thermografie von einem rein oberflächensensitiven Prüfverfahren hin zu einem Verfahren mit verbesserter Tiefenreichweite zu entwickeln. Wie weit diese Entwicklung getrieben werden kann, ist Gegenstand aktueller Forschung. Wir konnten bereits zeigen, dass diese klassische Grenze für 1D- und 2D Defektgeometrien mit Hilfe des Abscannens des Prüfkörpers mittels einzelner Laserspots und der anschließenden Anwendung von photothermischer Super-Resolution-Rekonstruktion überwunden werden kann. Bei dieser Methode wird eine Kombination aus sequenzieller räumlich strukturierter Beleuchtung und numerischen Optimierungsmethoden eingesetzt. Dies geschieht allerdings auf Kosten der experimentellen Komplexität, die zu einer langen Messdauer, großen Datensätzen und langwieriger numerischer Auswertung führt. In dieser Arbeit berichten wir über einen neuen experimentellen Ansatz, bei dem räumlich strukturierte 2D-Beleuchtungsmuster in Verbindung mit Compressed-Sensing und Computational-Imaging-Methoden verwendet werden, um die experimentelle Komplexität deutlich zu verringern und die Methode für die Untersuchung größerer Prüfflächen nutzbar zu machen. Der experimentelle Ansatz basiert dabei auf der wiederholten (blinden) photothermischen Anregung mit räumlich strukturierten 2D-Mustern unter Verwendung moderner Projektortechnik und eines Hochleistungslasers. In der anschließenden numerischen Rekonstruktion werden mehrere Messungen unter Ausnutzung der Joint-Sparsity der Defekte innerhalb des Prüfkörpers mittels nichtlinearer konvexer Optimierungsmethoden kombiniert. Als Ergebnis kann eine 2D-sparse Defekt-/Inhomogenitätskarte erstellt werden. T2 - DGZfP-Jahrestagung 2022 CY - Kassel, Germany DA - 23.05.2022 KW - Thermografie KW - Super resolution KW - NDT KW - ZfP KW - Eingeschlossene Defekte KW - Projektor PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-548945 SN - 978-3-947971-25-1 VL - 177 SP - 1 EP - 16 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung AN - OPUS4-54894 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heßmann, Jennifer A1 - Hilgenberg, Kai ED - Hausmann, J. M. T1 - Meeting the challenge of thermal joining of steel and aluminum using a new approach based on melt displacement by electromagnetic forces N2 - Environmental protection, resource conservation and CO2 reduction require new joining concepts for effective multi-material design in automotive lightweight construction. The thermal joining of dissimilar materials, especially the combination of aluminum alloys and steel, is associated with difficulties. Different material properties, such as melting point and coefficient of thermal expansion, complicate joining processes. Furthermore, the insolubility between these materials results in the formation of intermetallic phases. These brittle phases reduce the load-bearing capacity and quality of the joints. The thickness of the intermetallic phases should not reach the critical value of 10 μm to ensure good mechanical properties of the joint. It is known that a two-phase reaction layer consisting of Al5Fe2 and Al3Fe (also known as Al13Fe4) forms at the interface between solid steel and liquid aluminum. Due to high cooling rates, as it is the case in laser beam welding, metastable intermetallic compounds can form different from the equilibrium state. The formation of the intermetallic reaction layer is a diffusion-controlled process. So, it is only possible to control the growth of these phases. This problem has led to use joining methods that do not require the melting of both joining partners. A promising joining method is laser beam welding-brazing, whereby only one joining partner is melted and wets the solid joining partner. Conventional laser beam welding-brazing only results in material-fit joints and often requires the use of expensive filler materials. An additional form-fit could optimize the mechanical performance of the joint. For this reason, a new joining method for overlap configurations of dissimilar materials was developed. A laser beam melts the lower joining partner through a cavity of the upper joining partner. The created melt pool is moved upwards into the cavity of the upper joining partner due to contactless induced Lorentz forces of an AC-magnetic system. The displaced melt creates a form- and material-fit joint after solidification. The advantage of this joining technology is the absence of filler materials, flux agents and expensive auxiliary joining elements. T2 - 5th International Conference Hybrid 2022 - Materials and Structures CY - Leoben, Austria DA - 20.07.2022 KW - Joining dissimilar materials KW - Laser beam welding KW - Electromagnetic forces KW - Steel and aluminium PY - 2022 SN - 978-3-88355-426-6 SP - 6 EP - 8 PB - Deutsche Gesellschaft für Materialkunde (DGM) CY - Sankt Augustin AN - OPUS4-55536 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rückschloss, J. A1 - Schischke, K. A1 - Berwald, A. A1 - Schlegel, Moritz-Caspar T1 - Pandemic-related behavioural changes – does EU Ecodesign policy making need to react? N2 - The global COVID-19 pandemic has brought far-reaching changes for our society. Suddenly, millions of people spent the majority of their time at home - either due to a lock down or by switching from office to working remotely. This paper offers a literature review regarding pandemic-related behavioural changes and a first mapping of likely consequences for EU Ecodesign regulations. These impacts are considered for product groups that are already regulated by EU Ecodesign or are under discussion for future regulation. Furthermore, potential for smart home applications are analysed exemplarily. We identified which behavioural changes have the potential to become established in the long-term. This might need to result in adaptions for regulations under the Ecodesign Directive and EU-Energy Labelling regulations to better reflect the recently appeared usage profiles. It might require different priority settings regarding the product groups to be regulated and communicated to users, due to online shopping proliferation, to be updated. Changed behaviour can be observed in product groups such as ICT, consumer electronics and household appliances. Examples include the increased use of laptops and tablets for digital teaching, use of gaming devices and office equipment in private households (IT, printing and network devices) and changed cooking behaviour. This resulted in increased sales of some product types. Online sales became even more important than in-store sales, which also means that consumers are increasingly informed online about energy efficiency. More do-it-yourself (DIY) home projects result in more frequent - not yet regulated - DIY power tool use and over the long run might stimulate the need for (semi-)professional tools. The changes in behaviour patterns also offer the opportunity to optimize consumption by means of smart homes and smart products. However, the control of networked household appliances requires additional energy for standby states and data exchange. As an illustrative example, we discuss the conflict between higher energy consumption for smart system components and the possible optimization of consumption in private households. T2 - ECEEE 2022 SUMMER STUDY CY - Hyères, France DA - 06.06.2022 KW - Ecodesign KW - Energy Labelling KW - Circular Economy KW - Pandemic KW - Behavioural change PY - 2022 UR - https://www.eceee.org/static/media/uploads/site-2/summerstudy2022/pdfs_docs/panel8-papers.zip SP - 1237 EP - 1244 AN - OPUS4-55509 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klewe, Tim A1 - Völker, Tobias A1 - Götz, J. A1 - Landmann, M. A1 - Wilsch, Gerd A1 - Kruschwitz, Sabine T1 - Sorting of construction and demolition waste by combining LIBS with NIR spectroscopy N2 - In a joint project of partners from industry and research, the automated recycling of construction and demolition waste (CDW) is investigated and tested by combing laser-induced breakdown spectroscopy (LIBS) and near-infrared (NIR) spectroscopy. Joint processing of information (data fusion) is expected to significantly improve the sorting quality of various materials like concrete, main masonry building materials, organic components, etc., and may enable the detection and separation of impurities such as SO3-cotaining building materials (gypsum, aerated concrete, etc.). The project focuses primarily on the Berlin site to analyze the entire value chain, minimize economic/technological barriers and obstacles at the cluster level, and sustainably increase recovery and recycling rates. First measurements with LIBS and NIR spectroscopy show promising results in distinguishing various material types and indicate the potential for a successful combination. In addition, X-ray fluorescence (XRF) spectroscopy is being performed to obtain more information about the quantitative elemental composition of the different building materials. Future work will apply the developed sorting methodology in a fully automated measurement setup with CDW on a conveyor belt. T2 - NDT-CE 2022 CY - Zurich, Switzerland DA - 16.08.2022 KW - LIBS KW - NDT KW - Circular economy KW - Recycling KW - Material classification PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-555531 UR - http://www.ndt.net/?id=27220 VL - 2022/09 SP - 1 EP - 9 PB - NDT.net CY - Bad Breisig AN - OPUS4-55553 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klewe, Tim A1 - Völker, Tobias A1 - Landmann, Mirko A1 - Wilsch, Gerd A1 - Kruschwitz, Sabine T1 - Laser-based sorting of construction and demolition waste for the circular economy N2 - Closed material cycles and unmixed material fractions are required to achieve high recovery and recycling rates in the building industry. The growing diversity of construction and demolition waste is leading to increasing difficulties in separating the individual materials. Manual sorting involves many risks and dangers for the executing staff and is merely based on obvious, visually detectable differences for separation. An automated, sensor-based sorting of these building materials could complement or replace this practice to improve processing speed, recycling rates, sorting quality, and prevailing health conditions. A joint project of partners from industry and research institutions approaches this task by investigating and testing the combination of laser-induced breakdown spectroscopy (LIBS) and visual (VIS)/ near-infrared (NIR) spectroscopy. Joint processing of information (data fusion) is expected to significantly improve the sorting quality of various materials like concrete, main masonry building materials, organic components, etc., and may enable the detection and separation of impurities such as SO3-containing building materials (gypsum, aerated concrete, etc.). Focusing on Berlin as an example, the entire value chain will be analyzed to minimize economic/technological barriers and obstacles at the cluster level and to sustainably increase recovery and recycling rates. First LIBS measurements show promising results in distinguishing various material types. A meaningful validation shall be achieved with further practical samples. Future works will investigate the combination of LIBS and VIS/NIR spectroscopy in a fully automated measurement setup with conveyor belt speeds of 3 m/s. T2 - 6th fib Congress 2022 CY - Oslo, Norway DA - 12.06.2022 KW - LIBS KW - Data fusion KW - Circular economy KW - Recycling KW - Material classification PY - 2022 SP - 1 EP - 7 AN - OPUS4-55555 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schumacher, David A1 - Waske, Anja T1 - XCT data of metallic feedstock powder with pore size analysis N2 - X-Ray computed tomography (XCT) scan of 11 individual metallic powder particles, made of (Mn,Fe)2(P,Si) alloy. The data set consists of 4 single XCT scans which have been stitched together [3] after reconstruction. The powder material is an (Mn,Fe)2(P,Si) alloy with an average density of 6.4 g/cm³. The particle size range is about 100 - 150 µm with equivalent pore diameters up to 75 µm. The powder and the metallic alloy are described in detail in [1, 2]. KW - Additive Manufacturing KW - Feedstock powder KW - Powder Characterization KW - X-Ray Computed Tomography PY - 2022 DO - https://doi.org/10.5281/zenodo.5796487 PB - Zenodo CY - Geneva AN - OPUS4-55556 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Muth, Thilo T1 - MassIVE MSV000089620 - Critical Assessment of MetaProteome Investigation (CAMPI): A multi-lab comparison of established workflows N2 - Metaproteomics, the study of the collective proteome within a microbial ecosystem, has substantially grown over the past few years. This growth comes from the increased awareness that it can powerfully supplement metagenomics and metatranscriptomics analyses. Although metaproteomics is more challenging than single-species proteomics, its added value has already been demonstrated in various biosystems, such as gut microbiomes or biogas plants. Because of the many challenges, a variety of metaproteomics workflows have been developed, yet it remains unclear what the impact of the choice of workflow is on the obtained results. Therefore, we set out to compare several well-established workflows in the first community-driven, multi-lab comparison in metaproteomics: the critical assessment of metaproteome investigation (CAMPI) study. In this benchmarking study, we evaluated the influence of different workflows on sample preparation, mass spectrometry acquisition, and bioinformatic analysis on two samples: a simplified, lab-assembled human intestinal sample and a complex human fecal sample. We find that the same overall biological meaning can be inferred from the metaproteome data, regardless of the chosen workflow. Indeed, taxonomic and functional annotations were very similar across all sample-specific data sets. Moreover, this outcome was consistent regardless of whether protein groups or peptides, or differences at the spectrum or peptide level were used to infer these annotations. Where differences were observed, those originated primarily from different wet-lab methods rather than from different bioinformatic pipelines. The CAMPI study thus provides a solid foundation for benchmarking metaproteomics workflows, and will therefore be a key reference for future method improvement. [doi:10.25345/C5SX64D9M] [dataset license: CC0 1.0 Universal (CC0 1.0)] KW - Benchmarking KW - Data set PY - 2021 DO - https://doi.org/10.25345/c5sx64d9m PB - University of California CY - San Diego AN - OPUS4-58087 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schischke, K. A1 - Rückschloss, J. A1 - Schlegel, Moritz-Caspar A1 - Zöllinger, J. A1 - Nisse, N. F. A1 - Schneider-Ramelow, M. T1 - The European Union’s Energy Label for Smartphones: Does it guide consumers to make environmentally sustainable choices? N2 - The European Commission adopted an EU Energy Label for smartphones and tablets in June 2023. For the first time, the EU Energy Label will depict, among energy efficiency, also a reparability score, battery endurance, battery lifetime, drop resistance and dust and water ingress protection. However, does the multitude of parameters bear the risk to confuse consumers instead of triggering environmentally sustainable purchase decisions? In a survey in Germany, consumers were asked to make a choice when the label does not clearly identify the environmentally better product. Instead, energy efficiency has to be valued against reparability, reliability against energy efficiency, and reparability against reliability. The sustainability lever of the different aspects is not the same, as e.g. lifetime extension has a much more positive environmental impact than energy efficiency in case of mobile devices. Therefore, the question remains, whether consumers intuitively make the right choice. Results of the survey indicate that consumers interpret the complex label in the desired manner and value those aspects higher, which indeed have a more positive effect on the environment. T2 - 2023 IEEE 13th International Conference on Consumer Electronics CY - Berlin, Germany DA - 03.09.2023 KW - Circular Economy KW - Kreislaufwirtschaft KW - policy making KW - EU Energy Labelling KW - Smartphone PY - 2023 SP - 1 EP - 6 AN - OPUS4-58177 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Jaut, Valerie T1 - Investigation of the engineering of Leishmania RNA Virus 1 capsid protein N2 - Virus-like particles are of great interest. Due to the lack of functional amino acids, they are non-infectious and are widely investigated for their usage in the biomedical field, such as nanomaterials, vaccines, drug delivery. This thesis is about the engineering of virus-like particles, which are formed by self-assembly of LRV1 capsid proteins. Basis was a publication by Procházková et al. (2021), where the structure of virus-like particles, derived from recombinant LRV1 capsid proteins, was determined using cryo-electron microscopy. Goal of my work was to investigate, whether it is possible to modify the surface of LRV1 virus-like particles by protein engineering. Next to an LRV1 capsid protein with a C-termini polyhistidine-tag like in the publication, a genetically modified LRV1 capsid protein with an internal polyhistidine-tag was supposed to be expressed. It was supposed to be analyzed, whether it still comes to a self-assembly of the capsid proteins. The genetical constructs were generated by PCR based on a complementary LRV1 DNA, cloned into an expression vector, and using Sanger sequencing it was shown that the amino acid sequences were like expected. For the recombinant expression different E. coli (BL21 STAR (DE3), BL21 (DE3) pLysS, BL21 STAR (DE3) pRARE3 and T7 express lysY/Iq) strains were used, as well as different expression conditions tested by varying temperature, medium, isopropyl-ß-D-thiogalactoside oncentration, and induction duration. Best results were obtained expressing in T7 express lysY/Iq for 5 hours in Terrific Broth medium at 16 °C and 3 mM Isopropyl ß-D-1thiogalactopyranoside. After that, the recombinant proteins were purified under native conditions by their polyhistidine-tags using nickel affinity chromatography. Overall, a higher yield was obtained for the capsid protein with the C-termini polyhistidine-tag during expression, which was also visible in all following experiments. The expression of both constructs in E. coli was comparably low. Still, it was possible to validate for virus-like particles for both proteins using transmission electron microscopy. Thus, it was demonstrated for the first time that surface-modified LRV1 capsid proteins are able to assemble into virus-like particles. For further experiments and higher yield of soluble LRV1 capsid proteins for virus-like particle production, a different expression system should be used: Therefore, the LEXSY expression system should be optimal, it bases on Leishmania tarenolae, a natural LRV1 host system. KW - Protein engineering KW - Recombinant protein expression PY - 2023 SP - 1 EP - 98 PB - Technische Hochschule Wildau CY - Wildau AN - OPUS4-57723 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bayram, Rabia T1 - Rekombinante Herstellung einer Amin-Oxidase aus Aspergillus niger und deren Einsatz in der Biosensorik N2 - Das Ziel der vorliegenden Arbeit war die rekombinante Herstellung der AnFAO in E. coli, welche ursprünglich von A. niger produziert wird, und deren anschließende Anwendung in der Entwick-lung eines Fumonisin- Biosensors für die Lebensmittelanalytik. In Bezug auf die aktuell steigen-den Lebensmittel- und Rohstoffpreise ist die Entwicklung eines Schnelltestsystems zur Detektion von Kontaminationen mit Mykotoxinen besonders gefragt, da zusätzliche Verluste und Kosten verhindert werden können. Für die Herstellung der AnFAO als MBP-Fusionsprotein und Biotin-Fusionsprotein mit zusätzlichem 6x His-Tag wurden die pET-MBP-AnFAO und pRSET-BH6-An-FAO Expressionsvektoren erfolgreich konstruiert. Die lösliche Expression im Cytoplasma wurde von MBP-AnFAO erreicht, wobei die Expression von BH6-AnFAO in inclusion bodies erfolgte und keine Aktivität des Enzyms nachgewiesen wurde. Die Enzymaktivität von MBP-AnFAO wurde im optischen Assay und amperometrisch durch die Detektion von H2O2 ermittelt. Im optischen Assay wurde die maximale spezifische Aktivität von 2,45 U/mg bei 45 °C, einer Enzymkonzentration von 3 μM und 50 μM FB1 erreicht. Generell wurden mit FB1 als Enzymsubstrat höhere Fluoreszenzsig-nale und dementsprechend höhere Enzymaktivitäten als für FB2 beobachtet. Es wurde ein linearer Zusammenhang der Enzymaktivitäten mit der Substratkonzentration beobachtet. Außerdem wurde ein Anstieg der H2O2-Konzentration mit zunehmender Inkubationszeit (bis zu 60 Minuten) erkannt. Des Weiteren wurde der Einfluss des MBP-Fusionsproteins auf die Enzymaktivität des AnFAO untersucht. Dabei wurde anhand von wesentlich geringeren Aktivitäten für AnFAO allein ein eventueller Einfluss des MBP auf dessen Aktivität festgestellt. Ein elektrochemischer Aufbau wurde zur Entwicklung eines Fumonisin- Sensors genutzt. Dazu wurde nachgewiesen, dass FB1 von rekombinant hergestelltem MBP-AnFAO unter Bildung von NH3 und H2O2 zu weniger toxi-schem FB1, dem FPy1, oxidiert werden kann. An der PB/Kohlenstoff-Elektrode, welche sensitiver gegenüber H2O2 und stabiler als die CoPC/Kohlenstoff Elektrode war, wurde die Reduktion des enzymatisch gebildeten H2O2 gemessen. Die Erstellung einer FB1- Kalibriergerade mit FB1- Lösun-gen verschiedener Konzentrationen zeigte, dass das Enzym auch in immobilisierter Form in der Lage ist unterschiedliche Konzentrationen an FB1 zu desaminieren. Dazu gehört auch der Kon-zentrationsbereich unterhalb des festgelegten Grenzwertes von 2,7 μmol/kg für Fumonisin. Die amperometrischen Kurven hierfür wurden an der PB/Kohlenstoff-Elektrode erfolgreich aufge-nommen. Störungen des H2O2- Redoxstroms durch das Enzym, der Enzymsubstrate und der Ne-benprodukte während der amperometrischen Messung wurden ausgeschlossen. Sowohl im opti-schen als auch im amperometrischen Assay wurde ausschließlich das enzymatisch gebildete H2O2 bestimmt. KW - Fumonisin KW - Mykotoxin KW - rekombinante Protein Expression KW - Amperometrie PY - 2022 SP - 1 EP - 104 PB - Berliner Hochschule für Technik CY - Berlin AN - OPUS4-57724 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ferreira Camoes Liestmann, Zoe T1 - Development of an electrochemiluminescence immunoassay for selected pathogens in wastewater N2 - The outbreak of SARS-CoV-2 in December of 2019, led to a worldwide still on-going pandemic. Since then, several so-called waves of SARS-CoV-2 infections, a time period with a high and fast rising number of new infections, have occurred all over the world. Classic surveillance approaches are hardly applicable, and further, non-detected cases cannot be covered by them. Wastewater-based Epidemiology (WBE) was proven to be a reliable tool for the prediction of new SARS-CoV-2 infection waves, due to the discharge of virus particles in fecal shedding of infectious people. Until now, for the monitoring of SARS-CoV-2 in wastewater, Polymerase Chain Reaction (PCR) is used as analytical tool. Even though PCR is a highly sensitive analytical tool, is presents several disadvantages, such as the need for trained personnel, specific technical equipment, as well as a difficult performance. An analytical tool, to which these disadvantaged do not apply, are immunoassays. In this work, a sandwich Enzyme-Linked Immunosorbent Assay (ELISA), with the immobilization of the capture antibodies on the surface of a Microtiter Plate (MTP), as well as a sandwich Magnetic Bead-Based Assay (MBBA), with immobilization of the capture antibodies on the surface of Magnetic Beads (MBs), targeting the SARS-CoV-2 N-protein, were developed and optimized. Both assay formats were performed with a colorimetric and chemiluminescent detection. The developed assay is composed of the two monoclonal antibodies (mAb) AH2 and DE6 - which was biotinylated in the course of the work - which bind to two different epitops of the antigen N-protein. As tracer, Neutravidin-HRP was used, which binds, through interaction of the Neutravidin with the biotin, to the mAb DE6-Biotin. The assay development and optimization procedure included the investigation of the surface saturation with the mAb AH2, the concentration and dilution of the mAb DE6-Biotin and Neutravidin-HRP, the ideal MBs, the ideal coating as well as dilution buffers, and the colorimetric and chemiluminescent substrates. For the developed and fully optimized colorimetric ELISA, a test midpoint x0 of 388 μg/L, for the chemiluminsecent ELISA of 371 μg/L, for the colorimetric MBBA of 251 μg/L and for the chemiluminescent MBBA of 243 μg/L was obtained. Validation of the colorimetric MBBA was done by measurement of three wastewater samples collected at the Wastewater Treatment Plant (WWTP) Potsdam. Whilst no N-protein could be detected in the samples, by spiking of the wastewater samples with certain concentrations of the N-protein, 10- to 18-times lower concentrations could be back-calculated, which can be attributed to matrix-effects of the wastewater sample. Next to the matrix-effects, also several other reason exist, why no N-protein could be determined in the samples. Because of that, further investigation of the handling, and the measurement of the wastewater samples, as well as the improvement of the assay sensitivity through further optimization steps or exchange of the antibodies, is still necessary. KW - SARS-CoV-2 KW - ELISA KW - Antibody KW - N-capsid PY - 2022 SP - 1 EP - 102 PB - Technischen Universität München CY - München AN - OPUS4-57744 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Komann, Steffen A1 - Linnemann, Konrad A1 - Wille, Frank A1 - Reiche, Ingo A1 - Ramsay, J. T1 - New SCO-iii regulations to ship large comonents as surface contaminated objects N2 - The decommissioning or refurbishment of nuclear facilities necessitates either the storage or disposal of large radioactive components such as steam generators, pressurizers, reactor pressure vessels and heads, and coolant pumps, to list the major contributors. These components or objects are large in size and mass, measuring up to approximately 6 meters in diameter, up to 20 meters in length, and weighing over 400 000 kg. In many situations, the components are transported off-site to a storage, disposal or recycling/treatment facility. Previously, many large objects had to be transported under special arrangement. T2 - PATRAM22 CY - Juan les Pins, France DA - 11.06.2023 KW - Gefahrgut KW - Radioaktive Stoffe KW - Rückbau kerntechnischer Anlagen KW - Transport PY - 2023 SP - 1 EP - 8 AN - OPUS4-57750 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Kazlagić, Anera A1 - Rosner, M. A1 - Cipriani, A. A1 - Frick, D. A. A1 - Glodny, J. A1 - Hoffmann, E. J. A1 - Hora, J. M. A1 - Irrgeher, J. A1 - Lugli, F. A1 - Magna, T. A1 - Meisel, T. C. A1 - Meixner, A. A1 - Possolo, A. A1 - Pramann, A. A1 - Pribil, M. J. A1 - Prohaska, T. A1 - Retzmann, A. A1 - Rienitz, O. A1 - Rutherford, D. A1 - Paula-Santos, G. M. A1 - Tatzel, M. A1 - Widhalm, S. A1 - Willbold, M. A1 - Zuliani, T. A1 - Vogl, Jochen T1 - Data of the characterisation of conventional 87Sr/86Sr isotope ratios in cement, limestone and slate reference materials based on an interlaboratory comparison study N2 - This dataset represents the electronic supplementary material (ESM) of the publication entitled "Characterisation of conventional 87Sr/86Sr isotope ratios in cement, limestone and slate reference materials based on an interlaboratory comparison study", which is published in Geostandards and Geoanalytical Research under the DOI: 10.1111/GGR.12517. It consists of four files. 'ESM_Data.xlsx' contains all reported data of the participants, a description of the applied analytical procedures, basic calculations, the consensus values, and part of the uncertainty assessment. 'ESM_Figure-S1' displays a schematic on how measurements, sequences and replicates are treated for the uncertainty calculation carried out by PTB. 'ESM_Technical-protocol.pdf' is the technical protocol of the interlaboratory comparison, which has been provided to all participants together with the samples and which contains bedside others the definition of the measurand and guidelines for data assessment and calculations. 'ESM_Reporting-template.xlsx' is the Excel template which has been submitted to all participants for reporting their results within the interlaboratory comparison. Excel files with names of the the structure 'GeoReM_Material_Sr8786_Date.xlsx' represent the Rcon(87Sr/86Sr) data for a specific reference material downloaded from GeoReM at the specified date, e.g. 'GeoReM_IAPSO_Sr8786_20221115.xlsx' contains all Rcon(87Sr/86Sr) data for the IAPSO seawater standard listed in GeoReM until 15 November 2022. KW - Reference data KW - Strontium isotope ratio KW - Interlaboratory comparison KW - Reference material KW - Cement KW - Geological material KW - Value assignment KW - Measurement uncertainty KW - Conventional method PY - 2023 UR - https://doi.org/10.5281/zenodo.7804445 DO - https://doi.org/10.5281/zenodo.7804444 PB - Zenodo CY - Geneva AN - OPUS4-57809 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lecompagnon, Julien A1 - Hirsch, Philipp Daniel A1 - Rupprecht, C. A1 - Ziegler, Mathias ED - Maldague, X. T1 - Detection of internal defects applying photothermal super resolution reconstruction utilizing two-dimensional high-power random pixel patterns N2 - In this work, we report on our progress for investigating a new experimental approach for thermographic detection of internal defects by performing 2D photothermal super resolution reconstruction. We use modern high-power laser projector technology to repeatedly excite the sample surface photothermally with varying spatially structured 2D pixel patterns. In the subsequent (blind) numerical reconstruction, multiple measurements are combined by exploiting the joint-sparse nature of the defects within the specimen using nonlinear convex optimization methods. As a result, a 2D-sparse defect/inhomogeneity map can be obtained. Using such spatially structured heating combined with compressed sensing and computational imaging methods allows to significantly reduce the experimental complexity and to study larger test surfaces as compared to the one-dimensional approach reported earlier. T2 - Quantitative Infrared Thermography 2022 CY - Paris, France DA - 04.07.2022 KW - Thermography KW - Super resolution KW - NDT KW - inspection KW - Internal defects KW - DMD KW - DLP PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-577795 DO - https://doi.org/10.21611/qirt.2022.1005 SN - 2371-4085 SP - 1 EP - 7 PB - QIRT Council AN - OPUS4-57779 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rolle, Annette A1 - Komann, Steffen A1 - Wille, Frank T1 - Ageing aspect in design approval of special form radioactive material N2 - In accordance with the IAEA transport regulations, the design of special form radioactive material (SFRM) shall resist a severe transport accident without undue loss or dispersal of radioactive material. The safety assessment for design approval includes besides the program for physical tests (impact, percussion, bending and heat test) also the evaluation of the management system for design, manufacture, testing, documentation, use, maintenance, and inspection. SFRM source design plus management system shall ensure, that every specimen of the approved design is able to survive the severe mechanical and thermal tests at any time of its SFRM-working life. Due to the long-term use of SFRM designs in most cases, the assessment of the source ageing behavior is an important aspect in the approval procedure. Different fields of application imply a wide range of environmental conditions, from clean room atmosphere to highly aggressive industrial conditions. Besides of radioactive content, corrosion is a main factor for possible SFRM design degradation. Although the IAEA Advisory Material SSG-26 already implies an indication of the need for considering ageing mechanisms, suitable amendments in the regulatory requirements of SSR-6 should be introduced to make the approval procedure more transparent and help to reduce rounds of questions by the authority. A supplementary requirement for considering of ageing mechanisms could be a helpful contribution to an international harmonization of the approval procedure. This paper will describe major influencing factors to be considered to assess the ageing behavior of a SFRM design and will identify the need for a regulatory specification of a SFRM-working life as basis for the assessment of the SFRM design regarding time-dependent weakening. A proposal for an explicit requirement for consideration of ageing mechanisms in safety assessment of SFRM, which should be considered in the ongoing SSR-6 revision cycle, will be explained. T2 - PATRAM22 Conference CY - Juan-Les-Pins, Antibes, France DA - 11.06.2023 KW - Ttransport KW - Radioactive material KW - Sealed sources KW - Ageing PY - 2023 SP - 1 EP - 6 AN - OPUS4-57786 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bertovic, Marija A1 - Given, Joseph A1 - Lehleitner, Johannes T1 - First insights into the human-related risks of tunnel inspection N2 - Whereas human factors (HF) in the non-destructive testing (NDT) of metallic components are a poorly investigated topic (in comparison to other industrial fields such as aviation), HF in the inspection of concrete components are even less known. Studies have shown that there is always some variability between individuals in their inspection results and that HF affect the reliability of NDT inspections. The aim of the ongoing WIPANO project is to draft a standard for a holistic reliability assessment, with concrete inspection as one case study. This includes also the HF. A human-oriented Failure Modes and Effects Analysis (FMEA) was carried out to do the following: a) identify possible human-related risks in tunnel inspection processes using a laser scan method (including data collection,evaluation, and assessment of tunnel damage) and b) evaluate these human-related risks as regards their possible causes, consequences and probability of occurrence – in addition with respect to existing and possible preventive measures. The results show that the causes for possible failures can lie within people, the physical environment, technology, organisation, and extra-organisational environment. Whereas current preventive measures rely mostly on the individual and quality management practices, there is potential for even larger improvement at the organisational and extra-organisational level. The FMEA results were also used to develop a quantification method to further understand the HF in tunnel inspection, which could possibly be included in the information into the overall reliability assessment. The usage of qualitative and quantitative data collected through the human-FMEA within the proposed quantification method shows promise that HF can be quantified and could offer broader understanding of HF influences on inspection in various industries. T2 - NDT-CE 2022 CY - Zurich, Switzerland DA - 16.08.2022 KW - Human Factors KW - Failure Modes and Effects Analysis KW - FMEA KW - Tunnel Inspection KW - NDT Reliability KW - Quantification PY - 2022 AN - OPUS4-56015 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gradt, Thomas A1 - Martin, Martin A1 - Gleim, Tobias T1 - Reibungszahlen von Holz-Holz- und Holz-Stahl-Kontakten für Stoßdämpfer von CASTOR-Behältern N2 - Holz wird vielfach in Stoßdämpfern von Transportbehältern für radioaktives Material eingesetzt. Dafür wird oftmals Fichtenholz verwendet, das in mehreren Lagen und senkrecht zueinander liegender Faserrichtung zwischen einer inneren und einer äußeren Stahlhülle eingebaut wird. Die Reibung zwischen den dabei entstehenden Grenzflächen ist von entscheidender Bedeutung für die Stoß- und Energieabsorption, z. B. bei einem Aufprall des Behälters auf eine harte Unterlage. Um detaillierte Informationen für entsprechende numerische Simulationen zu bekommen, wurden in dieser Arbeit die Reibungszahlen von Holz-Holz- und Holz-Stahl-Paarungen bei für derartige Behälter relevanten Beanspruchungsbedingungen im Temperaturbereich zwischen -40°C und 90°C gemessen. Die Ergebnisse zeigen eine gleichmäßige, mit steigender Temperatur abfallende Reibung, wobei die Werte für Holz-Stahl-Paarungen zwischen 0,43 bei -40°C und 0,22 bei 90°C sowie für Holz-Holz-Kontakte zwischen 0,3 bei -40°C und 0,24 bei 90°C liegen. T2 - 63. Tribologie-Fachtagung 2022 CY - Göttingen, Germany DA - 26.09.2022 KW - Reibung KW - Holz-Holz-Kontakte KW - Holz-Stahl-Kontakte KW - CASTOR-Behälter KW - Stoßdämpfer PY - 2022 SN - 978-3-9817451-7-7 SP - 23/1 EP - 23/4 AN - OPUS4-56021 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bertovic, Marija A1 - Given, Joseph A1 - Rentala, V. K. A1 - Lehleitner, Johannes A1 - Kanzler, D. A1 - Heckel, Thomas A1 - Tkachenko, Viktoriya T1 - Human Factors in der POD - ist das möglich? N2 - Menschliche Faktoren sind ein häufig genanntes Thema, wenn wir über die Zuverlässigkeit der zerstörungsfreien Prüfung (ZfP) sprechen. Die Probability of Detection (POD), das üblicherweise verwendete Maß für die Zuverlässigkeit der ZfP, betrachtet jedoch nur die technische Fähigkeit eines ZfP-Systems, einen Fehler zu entdecken. Nach mehreren Jahrzehnten der Erforschung des Einflusses der menschlichen Faktoren auf die Zuverlässigkeit der ZfP gibt es immer noch keinen allgemein akzeptierten Ansatz, um menschliche Faktoren in der Zuverlässigkeitsbewertung sichtbar zu machen. Dieser Beitrag gibt einen Überblick über verschiedene verfügbare Methoden zur Einbeziehung menschlicher Faktoren in die Zuverlässigkeitsbewertung. Das Thema ist ein essenzieller Bestandteil des laufenden WIPANO-Projekts "normPOD", das sich als Ziel gesetzt hat, die Standardisierung der Zuverlässigkeitsbewertung in Deutschland voranzutreiben und im Vergleich zu den schon bekannten internationalen Normen einen Fokus auf den Umgang mit den menschlichen Faktoren zu legen. T2 - DGZfP Jahrestagung 2022 CY - Kassel, Germany DA - 23.05.2022 KW - Human factors KW - Zuverlässigkeit KW - POD KW - Probability of detection KW - Reliability PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-559942 SP - 1 EP - 15 AN - OPUS4-55994 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jüngert, A. A1 - Heckel, Thomas A1 - Tkachenko, Viktoriya A1 - Bertovic, Marija A1 - Vrana, J. A1 - Kanzler, D. T1 - POD, aber wie? Konzeption und Herstellung von Testkörpersätzen und Prüfvorschriften für die experimentelle Zuverlässigkeitsbestimmung von ZfP-Prüfansätzen N2 - Im Rahmen des WIPANO Vorhabens „normPOD“ wird eine Richtlinie zur experimentellen und simulationsgestützten Zuverlässigkeitsbewertung erstellt. In der Richtlinie wird die Zuverlässigkeitsbewertung beispielhaft für zwei praktische Anwendungsfälle vorgestellt. Ein Anwendungsfall beschäftigt sich mit konventionellen Ultraschallprüfungen an ferritischen Stählen und deren Schweißnähten. Zur Berechnung von Probability-Of-Detection (POD)-Kurven ist es notwendig, dass ein geeigneter Testkörpersatz zur Verfügung steht, der sowohl leicht zu findende Fehlstellen als auch Fehlstellen, die an der Grenze der Detektierbarkeit liegen, enthält. Im Vorhaben kommen verschiedene Testkörper zum Einsatz, die entweder Ersatzfehler wie Nuten und Bohrungen oder künstlich eingebrachte realistische Fehlstellen wie Risse und Schweißfehler enthalten. Zur Erstellung eines möglichst allgemeinen Leitfadens zur Testkörperherstellung für die Zuverlässigkeitsbewertung werden verschiedene Möglichkeiten betrachtet. Es wird ein Testkörpersatz mit Ersatzfehlern hergestellt und durch Testkörper mit realistischen Fehlstellen ergänzt. Mit Hilfe von Simulationen mit CIVA sollen die optimalen Konfigurationen und Anordnung von realistischen Fehlstellen und Ersatzfehlern identifiziert, und anschließend mithilfe geeigneter Fertigungsverfahren eingebracht und validiert werden. Neben den Testkörpern, die gezielt für das Vorhaben hergestellt werden, kommen außerdem kommerziell erhältliche Testkörpersätze mit realistischen Fehlstellen zum Einsatz. Die Prüfaussage einer Ultraschallprüfung hängt weiterhin wesentlich von den Informationen ab, die dem Prüfpersonal vor Ort zur Verfügung steht. Es muss ein ausgewogenes Maß zwischen zu wenig und zu viel Informationen gefunden werden. Im letzten Schritt wird deshalb eine geeignete Vorlage für eine Prüfanweisung erstellt, die so formuliert ist, dass die Wahrscheinlichkeit menschlicher Fehler (z. B. Missverständnis, Fehlinterpretation, Überspringen von Schritten usw.) möglichst gering ist. T2 - DGZfP Jahrestagung 2022 CY - Kassel, Germany DA - 23.05.2022 KW - Zuverlässigkeit KW - POD KW - Testkörper KW - Ultraschallprüfung PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-560103 SP - 1 EP - 9 AN - OPUS4-56010 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kanzler, D. A1 - Rentala, V. K. A1 - Bertovic, Marija A1 - Heckel, Thomas A1 - Tkachenko, Viktoriya A1 - Given, Joseph A1 - Keßler, S. A1 - Dethof, F. A1 - Jüngert, A. A1 - Vrana, J. T1 - Lasst uns mal POD standardisieren! N2 - Seit beinahe 50 Jahren werden Zuverlässigkeitsbewertungen zerstörungsfreier Prüfverfahren erfolgreich in unterschiedlichen Industriebranchen eingesetzt. Dennoch gibt es weiterhin viele Vorbehalte, da die Bewertungsgrundlage nicht standardisiert ist und konkrete Handlungsanweisungen fehlen. Dem gegenüber steht die Anerkennung in der ZfP-Community. Es ist bisher nur Wenigen bekannt, dass dem Wissen über die Zuverlässigkeit eines zerstörungsfreien Prüfverfahren eineSchlüsselfunktion für die ZfP 4.0 zukommt. Im Vortrag wird die Notwendigkeit für eine Norm oder eine Richtlinie zum Thema Zuverlässigkeitsbewertungen aufgezeigt. Es wird darauf eingegangen, warum es bisher (in Deutschland) noch keine Richtlinie gab und gibt und was der:die Anwender:innen aus einer Richtlinie zur Zuverlässigkeitsbewertung von ZfP-Prüfverfahren erwarten kann. Es werden konkrete Schritte und Vorgehensweisen zur Bewertung der Zuverlässigkeit eines Verfahrens aufgezeigt; von der Definition eines Anwendungsfalls, über die Herstellung geeigneter Testkörper bis hin zur Durchführung und Bewertung von Prüfungen unter Einbeziehung von menschlichen Einflüssen. Die Beispiele umfassen sowohl Anwendungen aus dem Bauwesen als auch aus dem Maschinen- und Anlagenbau. Der Vortrag fasst die bisherigen und geplanten Arbeiten in dem WIPANO Projekt „Normung für die probabilistische Bewertung der Zuverlässigkeit für zerstörungsfreie Prüfverfahren“ zusammen. T2 - DGZfP Jahrestagung 2022 CY - Kassel, Germany DA - 23.05.2022 KW - Zuverlässigkeit KW - POD KW - Probability of detection KW - Reliability KW - Human Factors KW - Simulation PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-560113 SP - 1 EP - 10 AN - OPUS4-56011 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bertovic, Marija A1 - Given, Joseph A1 - Lehleitner, Johannes T1 - First insights into the human-related risks of tunnel inspection N2 - Whereas human factors (HF) in the non-destructive testing (NDT) of metallic components are a poorly investigated topic (in comparison to other industrial fields such as aviation), HF in the inspection of concrete components are even less known. Studies have shown that there is always some variability between individuals in their inspection results and that HF affect the reliability of NDT inspections. The aim of the ongoing WIPANO project is to draft a standard for a holistic reliability assessment, with concrete inspection as one case study. This includes also the HF. A human-oriented Failure Modes and Effects Analysis (FMEA) was carried out to do the following: a) identify possible human-related risks in tunnel inspection processes using a laser scan method (including data collection,evaluation, and assessment of tunnel damage) and b) evaluate these human-related risks as regards their possible causes, consequences and probability of occurrence – in addition with respect to existing and possible preventive measures. The results show that the causes for possible failures can lie within people, the physical environment, technology, organisation, and extra-organisational environment. Whereas current preventive measures rely mostly on the individual and quality management practices, there is potential for even larger improvement at the organisational and extra-organisational level. The FMEA results were also used to develop a quantification method to further understand the HF in tunnel inspection, which could possibly be included in the information into the overall reliability assessment. The usage of qualitative and quantitative data collected through the human-FMEA within the proposed quantification method shows promise that HF can be quantified and could offer broader understanding of HF influences on inspection in various industries T2 - The International Symposium on Nondestructive Testing in Civil Engineering CY - Zurich, Switzerland DA - 16.08.2022 KW - Human Factors KW - Failure Modes and Effects Analysis KW - FMEA KW - Tunnel Inspection KW - NDT Reliability KW - Quantification PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-560138 SP - 1 EP - 5 AN - OPUS4-56013 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Königsbauer, Korbinian A1 - Nöther, N. A1 - Schaller, M. B. A1 - Wosniok, Aleksander A1 - Krebber, Katerina T1 - Distributed POF sensors for structural health monitoring in civil construction applications N2 - In this paper, a cost-efficient distributed fiber optic measurement system based on Rayleigh scattering is presented. The distributed digital incoherent optical frequency domain reflectometry (I-OFDR) method is developed for detection of significantly large strain in the range from 3 % up to 10 % as required by end users. For this purpose, a vector network analyzer used in the I-OFDR is replaced by a compact and cost-effective digital data acquisition system. This digital emitting/receiving unit enables the recording of the complex transfer function carrying information about the local deformations along the entire sensing fiber. T2 - POF 2022 The 30th International Conference on Plastic Optical Fibers CY - Bilbao, Spain DA - 26.09.2022 KW - I-OFDR KW - PF-POF KW - Structural health monitoring KW - Rayleigh backscatter measurement KW - Strain detection PY - 2022 VL - 2022 SP - 152 EP - 155 AN - OPUS4-56060 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilsch, Gerd A1 - Völker, Tobias A1 - Klewe, Tim A1 - Kruschwitz, Sabine T1 - Laser Induced Breakdown Spectroscopy – A Tool for Imaging the Chemical Composition of Concrete N2 - One of the most common causes of damage is the ingress of harmful ions into the concrete, which can lead to deterioration processes and affect structural performance. Therefore, the increasingly aging infrastructure is regularly inspected to assess durability. Regular chemical analysis can be useful to determine the extent and evolution of ion ingress and to intervene in a timely manner. This could prove more economical than extensive repairs for major damage, particularly for critical infrastructure. In addition to already established elemental analysis techniques in civil engineering such as potentiometric titration or X-ray fluorescence analysis, laser-induced breakdown spectroscopy (LIBS) can provide further important complementary information and benefits. The possibilities of LIBS are demonstrated using the example of a drill core taken from a parking garage. T2 - 6th International Conference on Concrete Repair, Rehabilitation and Retrofitting CY - Kapstadt, South Africa DA - 03.10.2022 KW - LIBS KW - Concrete KW - Chlorine PY - 2022 UR - https://iccrrr2022.org/downloads SP - 126 EP - 127 AN - OPUS4-56062 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kröll, Mirco A1 - Grundtner, R. A1 - Newrkla, K. A1 - Pagano, F. A1 - Nyberg, E. A1 - Heino, V. A1 - Spaltmann, Dirk T1 - On the quality of wear volume data of laboratory model tests N2 - European tribological research organisations unify their capabilities for the European Tribology Centre (https://www.i-tribomat.eu/). At its core is a database, which data are made comparable and trusted via harmonised procedures for their generation. This contribution will focus on wear volume data. T2 - 63. Tribologie-Fachtagung 2022 CY - Göttingen, Germany DA - 26.09.2022 KW - Tribology KW - i-TRIBOMAT KW - Characterisation KW - Digitalisation KW - Harmonisation KW - Round robin tests KW - Interlaboratory tests KW - Wear volume PY - 2022 SN - 978-3-9817451-7-7 SP - 192 EP - 194 PB - Gesellschaft für Tribologie e.V. AN - OPUS4-55881 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Winkler, Nicolas P. A1 - Neumann, Patrick P. A1 - Schaffernicht, E. A1 - Lilienthal, A. J. A1 - Poikkimäki, M. A1 - Kangas, A. A1 - Säämänen, A. ED - Kourkoulis, S. K. T1 - Gather Dust and Get Dusted: Long-Term Drift and Cleaning of Sharp GP2Y1010AU0F Dust Sensor in a Steel Factory N2 - The Sharp GP2Y1010AU0F is a widely used low-cost dust sensor, but despite its popularity, the manufacturer provides little information on the sensor. We installed 16 sensing nodes with Sharp dust sensors in a hot rolling mill of a steel factory. Our analysis shows a clear correlation between sensor drift and accumulated production of the steel factory. An eye should be kept on the long-term drift of the sensors to prevent early saturation. Two of 16 sensors experienced full saturation, each after around eight and ten months of operation. T2 - 38th Danubia-Adria Symposium on Advances in Experimental Mechanics CY - Poros, Greece DA - 20.09.2022 KW - Low-cost KW - Dust sensor KW - Sensor network KW - Sensor drift PY - 2022 SP - 1 EP - 2 CY - Athens, Greece AN - OPUS4-55909 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Patrick P. A1 - Kohlhoff, Harald A1 - Johann, Sergej A1 - Erdmann, Jessica A1 - Winkler, Nicolas P. ED - Kourkoulis, S. K. T1 - The RASEM System: A Technical Overview N2 - Occupational health is an important topic, especially in industry, where workers are exposed to airborne by-products (e.g., dust particles and gases). Therefore, continuous monitoring of the air quality in industrial environments is crucial to meet safety standards. For practical and economic reasons, high-quality, costly measurements are currently only carried out sparsely, both in time and space, i.e., measurement data are collected in single day campaigns at selected locations only. The project “Robot-assisted Environmental Monitoring for Air Quality Assessment in Industrial Scenarios” (RASEM) addresses this issue by bringing together the benefits of both – low- and high-cost – measuring technologies enabling costefficient long-term air quality monitoring in realtime: A stationary network of low-cost sensors that is augmented by mobile units carrying high-quality sensors. By mapping the distribution of gases and particles in industrial environments with the proposed RASEM system, measures can be identified to improve on-site working conditions much faster than using traditional methods. In this paper, we detail the technical aspects of RASEM and introduce the mobile platforms used. T2 - 38th Danubia-Adria Symposium on Advances in Experimental Mechanics CY - Poros, Greece DA - 20.09.2022 KW - RASEM KW - Dust sensor KW - Low-cost KW - Sensor network KW - Ground Robot KW - Aerial Robot PY - 2022 SP - 1 EP - 2 CY - Athens, Greece AN - OPUS4-55915 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pauw, Brian Richard T1 - The SPONGE v.1.0.0: Modeling scattering of shapes by STL input, with absolute intensities and size distribution. N2 - Simulates X-ray and Neutron scattering patterns from arbitrary shapes defined by STL files. Features: - Uses multithreading to compute a number of independent solutions, then uses the variance of the results to estimate an uncertainty on the output. - Can be launched from the command line using an excel sheet to define settings, or from a jupyter notebook. - Outputs scattering patterns in absolute units if the contrast is set. - A Gaussian size distribution is available, where the relative scaling of objects for each repetion can be varied. Recommended to be used with limited width (max. 10%) to avoid artefacts. - Writes results with settings to an archival HDF5 file. Application examples: This software has been used in several studies to date. For example, it has been used here to simulate a model scattering pattern for a cuboid shape, which was then fed forward into the McSAS3 analysis program for analyzing scattering patterns of polydisperse cuboids. A second use is here, where it was used for the modeling of flattened helices. In this paper, scattering pattern features could be matched with particular morphological changes in the structure. Lastly, this paper has an example where it was used to validate the analytical analysis model, and explore the realistic limits of application of the analytical model. KW - Software KW - Scattering pattern analysis KW - Scattering pattern simulation KW - X-ray KW - Neutron KW - Command-line interface KW - Scattering pattern KW - STL file input KW - Python KW - Arbitrary shapes PY - 2023 DO - https://doi.org/10.6084/m9.figshare.21857130.v1 PB - Digital Science CY - Cambridge, MA, USA AN - OPUS4-56815 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilsch, Gerd A1 - Völker, Tobias A1 - Klewe, Tim A1 - Kruschwitz, Sabine T1 - Laser-induced breakdown spectroscopy to investigate the chemical composition of concrete N2 - Laser-induced breakdown spectroscopy (LIBS) is a spectroscopic method for the analysis of the chemical composition of sample materials. Generally, the measurement of all elements of the periodic table is possible. In particular, light elements such as H, Li, Be, S, C, O, N and halogens can be measured. Calibration with matrix-matching standards allows the quantification of element concentrations. In combination with scanner systems, the two-dimensional element distribution can be determined. Even rough surfaces can be measured by online adjustment of the laser focus. LIBS can also be used on-site with mobile systems. Hand-held systems are available for point measurements. Common applications include the investigation of material deterioration due to the ingress of harmful ions and their interaction in porous building materials. Due to the high spatial resolution of LIBS and the consideration of the heterogeneity of concrete, the determination of precise input parameters for simulation and modelling of the remaining lifetime of a structure is possible. In addition to the identification of materials, it is also possible to assess the composition for example of hardened concrete, which involves the cement or aggregate type used. Other important fields of application are the detection of environmentally hazardous elements or the material classification for sorting heterogeneous material waste streams during dismantling. Non-contact NDT for “difficult to assess” structures as an example application through safety glass or in combination with robotics and automation are also possible. In this work, an overview of LIBS investigations on concrete is given based on exemplary laboratory and on-site applications. T2 - NDE NucCon 2023 CY - Espoo, Finland DA - 25.01.2023 KW - LIBS KW - Concrete KW - Chemical analysis PY - 2023 UR - https://www.aalto.fi/en/nde-nuccon-2023 SP - 351 EP - 359 AN - OPUS4-57303 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Prager, Jens A1 - Lugovtsova, Yevgeniya A1 - Bulling, Jannis A1 - Held, Mathias A1 - Klärner, M. A1 - Winkler, T. A1 - Kroll, L. T1 - Akustische Bestimmung der Werkstoffparameter faserverstärkter Kunststoffe durch Auswertung der Dispersionseigenschaften geführter Wellen N2 - Akustische Verfahren eignen sich hervorragend zur Bestimmung der Werkstoffeigenschaften. Die Verfügbarkeit derartiger Verfahren ist vor allem für Kunststoffe wichtig, da deren Eigenschaften stark abhängig vom jeweiligen Herstellungsprozess und vom Alterungszustand sind. Exakte und vollständige Werte sind daher in Datenbanken oder von Herstellern nur begrenzt zu finden. Insbesondere die Entwicklung von Methoden zur Charakterisierung faserverstärkter Kunststoffe (FKV) ist nach wie vor Gegenstand der Forschung. Hier müssen anisotropiebedingt mehrere Kennwerte bestimmt werden. Da FKV zumeist als dünnwandige Bauteile zum Einsatz kommen, können die Werkstoffparameter aus den Dispersionseigenschaften der Lamb-Wellen, die sich in diesen Strukturen ausbreiten, abgeleitet werden. Dazu ist eine räumliche Abtastung des sich ausbreitenden Schallfelds erforderlich. In der vorliegenden Untersuchung wird dieser Ansatz für die relativ neue Werkstoffklasse der faserverstärkten Thermoplaste angewendet. Diese zeichnet ein ausgeprägtes Dämpfungsverhalten und eine Anisotropie der Materialparameter aus. Dazu wurde das Schallfeld im Ultraschallbereich mit einem Laser-Doppler-Vibrometers vermessen. Rechnerisch bestimmte Dispersionskurven wurden dann an die gemessenen Werte angepasst, womit die richtungsabhängigen Materialparameter bestimmt werden konnten. Im Vortrag wird das Messverfahren vorgestellt und auf spezielle Probleme, die sich z.B. aus dem Dämpfungsverhalten des Werkstoffs ergeben, eingegangen. Ausgewählte gemessene Werte werden mit den Ergebnissen von Referenzverfahren verglichen. T2 - DAGA 2021 - 47. Jahrestagung für Akustik CY - Vienna, Austria DA - 15.08.2021 KW - Ultraschall KW - Composites KW - Thermoplastische Kunststoffe PY - 2021 SP - 52 EP - 55 PB - Deutsche Gesellschaft für Akustik (DEGA) CY - Berlin AN - OPUS4-57340 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nicolai, Marcel A1 - Zeipert, H. A1 - Lugovtsova, Yevgeniya A1 - Bulling, Jannis A1 - Johannesmann, S. A1 - Prager, Jens A1 - Henning, B. ED - Nicolai, Marcel T1 - Characterization of adhesion strength using guided ultrasonic waves N2 - Klebeverbindungen sind aus vielen Anwendungen wie dem Leichtbau nicht mehr wegzudenken. Durch die Verklebung gleicher oder ungleicher Materialien entstehen viele Vorteile gegenüber konservativen Fügeverfahren. Jedoch stellen schwache Haftfestigkeiten eine sehr unbeliebte Fehlerart dar, die schlecht zu detektieren sind und zu einem frühzeitigen Versagen der Verklebung bei vergleichsweise geringen Belastungen führen können. Aufgrund hoher Sicherheits- und Qualitätsansprüche wird die Haftfestigkeit dieser Verbindungen jedoch noch immer zerstörend geprüft. Zufriedenstellende zerstörungsfreie Verfahren, um Haftfestigkeiten zu prüfen, sind nicht vorhanden und Thema gegenwärtiger Forschung. Ein Ansatz, der in diesem Projekt verfolgt wird, liegt in der Verwendung geführter Ultraschallwellen. Hierzu wird anhand von Simulationen mittels der Scaled Boundary Finite Element Methode gezeigt, dass die gezielte Auswertung bestimmter Bereiche des Dispersionsdiagrams, den sogenannten vermiedenen Kreuzungen (engl. mode repulsion regions), eine Charakterisierung der Haftfestigkeiten zulassen könnten. Dies liegt darin begründet, dass die mittleren mechanischen Belastungen der Kleberschicht in diesen Bereichen ein lokales Maximum aufweisen und daher eine erhöhte Sensitivität auf Materialänderungen haben. Es wird gezeigt, wie sensitiv diese Bereiche auf Materialänderungen in der Klebergrenzschicht sind und welche potenziellen Fehlergrößen existieren. T2 - DAGA 2023 CY - Hamburg, Germany DA - 06.03.2023 KW - SBFEM KW - Adhesive Bonding KW - Kissing Bonds KW - NDT KW - Ultrasonic Guided Waves PY - 2023 UR - https://pub.dega-akustik.de/DAGA_2023 SN - 978-3-939296-21-8 SP - 823 EP - 826 PB - Deutsche Gesellschaft für Akustik e.V. CY - Berlin AN - OPUS4-57378 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bayoumi, A. A1 - Lozano, Daniel A1 - Bulling, Jannis A1 - Mueller, I. A1 - Prager, Jens T1 - Comparative Study Between Simulation and Experimental Guided Ultrasonic Wave Propagation on a Plate Like Structure N2 - In plate-like structures, ultrasonic waves propagate as Lamb waves. Their use is important for many applications from non-destructive testing to structural health monitoring. Efficient simulation tools contribute to a significant value add e.g. in designing systems for these applications. Under which conditions an acceptable accuracy of these models with affordable computational costs can be achieved is an open question. Many of these applications include the usage of a plane wavefront, simulated in 2D crossesctional models to reduce complexity. In this contribution, a comparative case study between simulations and experiments is presented. The aim is to verify and compare a 2D cross-sectional model with experimental data. The experimental setup for this case study consists of an aluminum plate. A rectangular piezoelectric transducer is mounted for guided wave excitation. A laser Doppler vibrometer (LDV) measures out-of-plane velocities on the plate. A 2D cross-sectional model based on the Scaled Boundary Finite Element Method (SBFEM) is used to simulate the wave propagation of the experimental setup. The first data points near the transducer are used to fit the excitation tractions of the model, while additional points further away from the source are used to validate the model. The comparison between the recorded measurements and the simulated velocities shows a high degree of compatibility. T2 - DAGA 2023 - 49. Jahrestagung für Akustik CY - Hamburg, Germany DA - 06.03.2023 KW - Scaled Boundary Finite Element Method KW - Guided Ultrasonic Wave KW - Laser Doppler Vibrometer PY - 2023 SN - 978-3-939296-21-8 SP - 88 EP - 91 AN - OPUS4-57354 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heimann, Jan A1 - Mustapha, S. A1 - Yilmaz, Bengisu A1 - Charmi, Amir A1 - Brence, Blaž A1 - Prager, Jens T1 - Untersuchung der Ausbreitung von geführten Ultraschallwellen in Wasserstoffdruckbehältern zur Zustandsüberwachung N2 - Die zunehmende Bedeutung von Wasserstoff als emissionsfreier Energieträger der Zukunft lässt die Anforderungen an eine technisch einwandfreie und sichere Wasserstoffspeicherung steigen. Im Mobilitätssektor kommen dabei vorwiegend Kohlefaserverbundbehälter zur Speicherung von gasförmigem Wasserstoff im Hochdruckbereich zum Einsatz, die sich durch ihre Leichtbauweise bei gleichzeitig hoher Speicherkapazität auszeichnen. Materialfehler oder -ermüdung können jedoch zum Ausfall bis hin zum kritischen Versagensfall führen. Ein sicherer Betrieb der Behälter erfordert daher ein innovatives und zuverlässiges Konzept, um deren Integrität zu gewährleisten und folgenschwere Zwischenfälle zu vermeiden. Die Strukturüberwachung mittels geführter Ultraschallwellen ist dafür einer der prominentesten Ansätze, da sich die Wellen über große Entfernungen in der Struktur ausbreiten können und zudem sehr empfindlich auf kleinste Materialdefekte reagieren. In diesem Beitrag wird der Aufbau eines Sensornetzwerks zur Schadenserkennung und -lokalisierung vorgestellt, das auf den Prinzipien der Ausbreitung geführter Ultraschallwellen in Druckbehältern aus Verbundwerkstoffen basiert. Dazu werden in einem ersten Schritt das dispersive und multimodale Ausbreitungsverhalten analysiert und dominante Wellenmoden identifiziert. Basierend auf der Analyse werden Dämpfungsverhalten und Empfindlichkeit gegenüber künstlichen Defekten bestimmt. Unter Verwendung der ermittelten Informationen wird ein Sensornetzwerk bestehend aus piezoelektrischen Flächenwandlern entworfen, welches den zu untersuchenden Bereich vollständig abdecken soll. Das Ergebnis wird anschließend durch Aufbringen künstlicher Defekte experimentell evaluiert und präsentiert. T2 - DAGA 2023 CY - Hamburg, Germany DA - 06.03.2023 KW - Geführte Ultraschallwellen KW - Zustandsüberwachung KW - Wasserstoffdruckbehälter KW - Sensornetzwerk KW - Structural Health Monitoring PY - 2023 UR - https://pub.dega-akustik.de/DAGA_2023 SN - 978-3-939296-21-8 SP - 1598 EP - 1601 CY - Berlin AN - OPUS4-58022 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Melzer, Michael T1 - Flexible Magnetic Sensors Enabling Novel Measuring Capabilities N2 - Since several years, magnetic sensor elements are available in fully flexible architectures that often reveal identical sensing properties, compared to their rigid counterparts, while being bent severely and repeatedly. Nowadays, a variety of magnetic senor principles, including well known Hall, AMR and GMR but also more exotic PHE and AHE sensors were demonstrated on such flexible platforms. The novel properties of being thin, lightweight, shapeable, and wearable enable magnetic sensory systems to be utilized in vicinities and conditions that are inaccessible for rigid and microchip-based sensors. T2 - SMSI 2023 - Sensor and Measurement Science International CY - Nuremberg, Germany DA - 08.05.2023 KW - Flexible electronics KW - Flexible sensors KW - Magnetic sensors KW - Novel applications KW - In-situ sensing PY - 2023 UR - https://www.ama-science.org/proceedings/details/4402 SN - 978-3-9819376-8-8 DO - https://doi.org/10.5162/SMSI2023/C5.2 SP - 175 EP - 176 PB - AMA Service GmbH CY - Wunstorf AN - OPUS4-58039 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wille, Frank A1 - Quercetti, Thomas A1 - Scheidemann, Robert T1 - Test Facilities for Radioactive Materials Transport and Storage Packagings at BAM N2 - BAM acts as authority and for service in safety assessment of packages for transport and storage of radioactive materials. We offer extensive test capabilities and application of analytical methods for design verification and simulation for all types of packages for the transport and storage of radioactive materials according with the international IAEA Regulations for the safe transport and for national storage acceptance criteria. BAM operates several test facilities for drop and stacking testing, leak testing and thermal testing. The large drop test tower allows dropping full-scale specimens up to 200,000 kg in any drop orientation as requested. The comprehensive test facilities combined with long-term experience, newest equipment and measurement devices according to the latest state-of-the-art technology ensures realisation of complex test campaigns for package safety evaluation. Beyond that, non-destructive and destructive material test devices and experts are available. Equipment and application of all kinds of typical measurement categories can be offered for testing campaigns. In recent years we performed testing of full-scale type B package models with complex handling and preparation procedures. The results were contributed for different package design approval procedures. Type A packages mainly designed for medical related transport purposes, were continuously tested according to the transport regulations over recent years as well. Moreover, we work on research topics with relevance to package safety. The mechanical behaviour of lid closure systems under transport and storage conditions and the thermal behaviour of impact limiters were recently of special importance for the assessment competencies of BAM and were investigated under use of our test facilities. The paper describes the test facilities and capabilities for package design safety evaluation at BAM and shows examples from our recent work. T2 - PATRAM 2022, 20th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Juan-les-Pins, France DA - 11.06.2023 KW - IAEA KW - Fire test KW - Drop testing KW - Transport KW - Package PY - 2023 SP - 1 EP - 12 AN - OPUS4-57967 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klein, Luise A1 - Wilke, Olaf T1 - Chamber comparison for the determination of initial VOC emissions from consumer products N2 - Volatile organic compound (VOC) emissions from consumer products contribute to human inhalation exposure and may cause adverse health effects. Existing methods to determine long-term VOC emissions from e.g. building products need to be verified for their suitability to reliably detect initial VOC emissions from consumer products within the first hours and days of use, which would facilitate realistic inhalation exposure assessments. To investigate this issue, VOCs emitted from a test sample were determined in a large-scale emission test chamber and in two micro-chambers of different volumes, and the results were compared. T2 - Healthy Buildings 2023 Europe CY - Aachen, Germany DA - 11.06.2023 KW - Micro-chamber KW - Emission test chamber KW - Volatile organic compounds KW - Inhalation exposure KW - Consumer products PY - 2023 SP - 6 EP - 8 AN - OPUS4-58055 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Epple, Niklas A1 - Sanchez Trujillo, Camila Andrea A1 - Niederleitinger, Ernst T1 - Ultrasonic monitoring of large-scale structures – input to engineering assessment N2 - Ultrasonic coda wave interferometry can detect small changes in scattering materials like concrete. We embedded ultrasonic transducers in the Gänstorbrücke Ulm, a monitored road bridge in Germany, to test the methodology. Since fall 2020, we've been monitoring parts of the bridge and comparing the results to commercial monitoring systems. We calculate signal and volumetric velocity changes using coda waves, and long-term measurements show that the influence of temperature on strains and ultrasound velocity changes can be monitored. Velocity change maps indicate that different parts of the bridge react differently to environmental temperature changes, revealing local material property differences. A load experiment with trucks allows calibration to improve detectability of possibly damaging events. Our work focuses on measurement reliability, potential use of and distinction from temperature effects, combination with complementary sensing systems, and converting measured values to information for damage and life cycle assessment. T2 - IALCCE 2023 CY - Milano, Italy DA - 02.07.2023 KW - Ultrasonic KW - Monitoring KW - Bridge KW - NDT KW - coda PY - 2023 SP - 1 EP - 8 PB - IALCCE CY - Milan AN - OPUS4-58047 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lu, Xin A1 - Krebber, Katerina T1 - Novel fading suppression method for distributed optical fiber acoustic sensing N2 - A universal method based on alternating pulse widths is proposed to suppress the signal fading for all distributed acoustic sensors (DASs) and experimentally demonstrated by one DAS system based on a Mach-Zehnder interferometer. T2 - Optica Sensing Congress CY - Munich, Germany DA - 30.07.2023 KW - Distributed fiber sensing KW - Acoustic sensing KW - Fading suppression KW - Structural health monitoring PY - 2023 SP - 1 EP - 2 AN - OPUS4-58048 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Feldkamp, Martin A1 - Quercetti, Thomas A1 - Gleim, Tobias A1 - Nehrig, Marko A1 - Musolff, André A1 - Wille, Frank T1 - R&D Activities by BAM Related to Transport Package Fire Testing N2 - Packages for the transport of radioactive material shall meet the mechanical and thermal test requirements of the International Atomic Energy Agency (IAEA) regulations for package design approval. Besides mechanical testing, the Federal Institute for Materials Research and Testing (BAM) performs thermal tests in accordance with the IAEA regulations. The thermal test includes a 30-minute 800°C fully engulfing fire. BAM continuously performs various thermal experiments for the investigation of the thermal response of packages with respect to the IAEA fire. The purpose of this paper is to give an overview of the already performed, ongoing and future physical tests and experiments of BAM in the field of thermal investigations. These research and development works shall support our competencies for the authority package design assessment. BAM operates a propane gas fire test facility. To be able to carry out comparative investigations and validity between the propane fire and the in detail prescribed pool fire test in the regulations, BAM carries out various calorimetric tests and investigates the boundary conditions of the fire with the help of fire reference packages. At the same time, we are conducting various fire scenarios with wood-filled impact limiters. Large-scale fire tests of impact limiters are carried out on a full scale as well as on a small scale. Influencing variables are investigated in particular by means of geometric changes and the consideration of artificial damages, in particular holes. In addition to propane fire as a heat source, thermal scenarios are also investigated with hydrogen as heat source and an infrared radiator system to ignite test specimens. For these numerous test arrangements, the transferability to existing and newly developed transport package designs is essential and fruitful within the review of design approvals, especially for Dual Purpose casks with a long-lasting operation time. T2 - 20th International Symposium on the Packaging and Transportation of Radioactive Materials (PATRAM 22) CY - Juan-Les-Pins, France DA - 11.06.2023 KW - Fire KW - Testing KW - Hydrogen KW - Wood KW - Propane KW - Heat Flux KW - Fire Reference Package KW - Radioactive Material PY - 2023 SP - 1 EP - 10 AN - OPUS4-57721 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schilling, Markus T1 - Full-Notch Creep Test Ontology (ontoFNCT) N2 - This is the stable version of the full-notch creep test ontology (OntoFNCT) that ontologically represents the full-notch creep test. OntoFNCT has been developed in accordance with the corresponding test standard ISO 16770:2019-09 Plastics - Determination of environmental stress cracking (ESC) of polyethylene - Full-notch creep test (FNCT). The OntoFNCT provides conceptualizations that are supposed to be valid for the description of full-notch creep tests and associated data in accordance with the corresponding test standard. By using OntoFNCT for storing full-notch creep test data, all data will be well structured and based on a common vocabulary agreed on by an expert group (generation of FAIR data) which is meant to lead to enhanced data interoperability. This comprises several data categories such as primary data, secondary data and metadata. Data will be human and machine readable. The usage of OntoFNCT facilitates data retrieval and downstream usage. Due to a close connection to the mid-level PMD core ontology (PMDco), the interoperability of full-notch creep test data is enhanced and querying in combination with other aspects and data within the broad field of materials science and engineering (MSE) is facilitated. The class structure of OntoFNCT forms a comprehensible and semantic layer for unified storage of data generated in a full-notch creep test including the possibility to record data from analysis and re-evaluation. Furthermore, extensive metadata allows to assess data quality and reliability. Following the open world assumption, object properties are deliberately low restrictive and sparse. KW - Ontology KW - Full-Notch Creep Test KW - FNCT KW - Knowledge Representation KW - Semantic Web Technologies KW - Data Structures KW - Data Management PY - 2024 UR - https://github.com/MarkusSchilling/ontoFNCT/blob/4abce82852190a5e444d302da077aa7404f433f0/ontoFNCT.ttl UR - https://raw.githubusercontent.com/MarkusSchilling/ontoFNCT/main/ontoFNCT.ttl PB - GitHub CY - San Francisco, CA, USA AN - OPUS4-59815 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Wernicke, Pascal T1 - Codierte Anregung von thermoakustischen Ultraschallwandlern und Wandlern aus zellulärem Polypropylen unter der Anwendung von signalangepassten Filtern N2 - Die Pulskompression wird in der Radartechnik eingesetzt, um den Signal-Rausch-Abstand zu erhöhen. Das Ziel ist es die Entdeckungswahrscheinlichkeit eines Nutzsignals bei gleichbleibender Auflösung zu erhöhen. Durch den Einsatz von Barker Codes oder komplementären Golay Codes werden Sendesignale von Luftultraschallanwendungen pulscodiert. Dies ermöglicht in der zerstörungsfreien Prüfung die Inspektion von dickeren Bauteilen, da die Signalenergie durch zeitlich gestreckte Sendesignale bei gleicher Auflösung vergrößert wird. In dieser Arbeit wird die Pulskompression durch die Einführung von unipolaren Sequenzen zur Pulscodierung für thermoakustische Ultraschallwandler ermöglicht. Der Signal-Rausch-Abstand wird in der Anwendung der Pulscodierung und anschließenden Filterung mit einem signalangepassten Filter in Luftultraschallmessungen mit dem thermoakustischen Wandler und Wandlern aus zellulärem Polypropylen erhöht. KW - Ultraschall KW - Pulskompression KW - Materialprüfung PY - 2023 SP - 1 EP - 85 AN - OPUS4-59795 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lozano, Daniel A1 - Bulling, Jannis A1 - Prager, Jens T1 - Modeling guided waves interacting with arbitrarily shaped inhomogeneities using SBFEM in combination with an extruded quadtree decomposition for 3D plates N2 - For structural health monitoring systems or non-destructive testing, it is crucial to study the interactions of ultrasonic-guided waves with inhomogeneities or damage in structural components. Simulation of these interactions poses a challenge. After the wave-damage interaction, the numerical model must reproduce features like mode conversion or wave scattering. Mathematically, damages are discontinuities in a computational domain, and each wave interacts differently because of the geometrical features. We propose a quadtree-based meshing in the current contribution to capture these geometrical characteristics. This kind of discretisation approach requires special techniques to couple cells of different sizes since, after a quadtree decomposition, the problem of so-called hanging nodes may arise. Transition elements based on high-order transfinite shape functions are used to solve this issue. The advantage is that these elements allow the correct coupling of the cells while retaining a high-order interpolation. Moreover, the reuse of the dynamic stiffness matrices can be exploited based on the similarity of the cells. This procedure makes the approach very efficient. Examples show the scattering characteristics of different guided wave modes after interacting with inhomogeneities and discontinuities in a plate. T2 - DAGA 2023 CY - Hamburg, Germany DA - 06.03.2023 KW - SBFEM KW - Quadtree KW - Ultrasound PY - 2023 SP - 1035 EP - 1038 CY - Hamburg AN - OPUS4-59776 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Küttenbaum, Stefan A1 - Kainz, C. A1 - Braml, T. T1 - Reliability assessment of existing concrete bridges with geometrical NDT results - Case studies N2 - The results of and the validity in reliability assessment of existing bridges essentially depend on the information available about the considered system. Information about the actual condition as well as structural and material characteristics can be observed on-site to refine the computation models used in assessment. Non-destructive testing (NDT) methods for concrete structures are capable of reconstructing missing, questioned, or inconsistent as-built plans. This contribution summarizes recent developments within the scope of the national pre-standardization project “ZfPStatik”, which aims to prepare a guideline about NDT-supported structural analyses. The focus is on the purposeful and explicit utilization of geometrical tendon and reinforcement bar positions (measured on-site using the ultrasound echo and ground penetrating radar (GPR) techniques) in probabilistic reliability analyses — shown by means of real case studies. The well-established first order reliability method is applied to different concrete bridges, which are typical for the German road bridge stock, to demonstrate the utility of incorporating quality-evaluated NDT-results in terms of changes in structural reliability. T2 - 13th German-Japanese Bridge Symposium CY - Osaka, Japan DA - 28.08.2023 KW - Non-destructive testing KW - Prestressed concrete KW - Data-informed reliability analysis PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-582727 SP - 29 EP - 40 PB - Osaka Metropolitan University CY - Osaka AN - OPUS4-58272 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Friedrich, Alexander T1 - Simulation of Eddy Current Rail Testing Data for Neural Networks N2 - The present work is part of the AIFRI project (Artificial Intelligence For Rail Inspection), where we and our project partners train a neural network for defect detection and classification. Our goal at BAM is to generate artificial ultrasound and eddy current training data for the A.I. This paper has an exploratory nature, where we focus on the simulation of eddy current signals for head check cracks, one of the most important rail surface defects. The goal of this paper is twofold. On the one hand, we present our general simulation setup. This includes geometric models for head check cracks with features like branching and direction change, a model for the HC10 rail testing probe, and the configuration of the Faraday simulation software. On the other hand, we use the Faraday software to simulate eddy current testing signals with a strong focus on the influence of the damage depth on the signal, while differentiating between different crack geometries. Here, we observe an early saturation effect of the test signal at a damage depth of 2 mm (at a crack angle of 25◦ to the surface). That is about 2 mm earlier than we would expect from measurements at a crack angle of 90◦. This behavior will be investigated further in a future paper. Finally, we interpolate the simulated signals in a two-step curve fitting process. With these interpolations we may generate eddy current test signals for any damage depth within the simulated range. T2 - 13th European Conference on Non-Destructive Testing 2023 CY - Lisbon, Portugal KW - Artificial Intelligence KW - Simulation KW - Eddy Current PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-581918 DO - https://doi.org/10.58286/28179 SN - 1435-4934 VL - 28 IS - 8 SP - 1 EP - 6 PB - NDT.net CY - Kirchwald AN - OPUS4-58191 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Riedel, Soraya T1 - Development of electrochemical antibody-based and enzymatic assays for mycotoxin analysis in food N2 - Electrochemical methods are promising to meet the demand for easy-to-use devices monitoring key parameters in the food industry. Many companies run own lab procedures for mycotoxin analysis, but it is a major goal to simplify the analysis. The enzyme-linked immunosorbent assay using horseradish peroxidase as enzymatic label, together with 3,3',5,5' tetramethylbenzidine (TMB)/H2O2 as substrates allows sensitive mycotoxin detection with optical detection methods. For the miniaturization of the detection step, an electrochemical system for mycotoxin analysis was developed. To this end, the electrochemical detection of TMB was studied by cyclic voltammetry on different screen-printed electrodes (carbon and gold) and at different pH values (pH 1 and pH 4). A stable electrode reaction, which is the basis for the further construction of the electrochemical detection system, could be achieved at pH 1 on gold electrodes. An amperometric detection method for oxidized TMB, using a custom-made flow cell for screen-printed electrodes, was established and applied for a competitive magnetic bead-based immunoassay for the mycotoxin ochratoxin A. A limit of detection of 150 pM (60 ng/L) could be obtained and the results were verified with optical detection. The applicability of the magnetic bead-based immunoassay was tested in spiked beer using a handheld potentiostat connected via Bluetooth to a smartphone for amperometric detection allowing to quantify ochratoxin A down to 1.2 nM (0.5 µg/L). Based on the developed electrochemical detection system for TMB, the applicability of the approach was demonstrated with a magnetic bead-based immunoassay for the ergot alkaloid, ergometrine. Under optimized assay conditions a limit of detection of 3 nM (1 µg/L) was achieved and in spiked rye flour samples ergometrine levels in a range from 25 to 250 µg/kg could be quantified. All results were verified with optical detection. The developed electrochemical detection method for TMB gives great promise for the detection of TMB in many other HRP-based assays. A new sensing approach, based on an enzymatic electrochemical detection system for the mycotoxin fumonisin B1 was established using an Aspergillus niger fumonisin amine oxidase (AnFAO). AnFAO was produced recombinantly in E. coli as maltose-binding protein fusion protein and catalyzes the oxidative deamination of fumonisins, producing hydrogen peroxide. It was found that AnFAO has a high storage and temperature stability. The enzyme was coupled covalently to magnetic particles, and the enzymatically produced H2O2 in the reaction with fumonisin B1 was detected amperometrically in a flow injection system using Prussian blue/carbon electrodes and the custom-made wall-jet flow cell. Fumonisin B1 could be quantified down to 1.5 µM (≈ 1 mg/L). The developed system represents a new approach to detect mycotoxins using enzymes and electrochemical methods. N2 - Zur Entwicklung von einfach zu bedienenden Vor-Ort-Geräten, welche für die Analytik von wichtigen Parametern in der Lebensmittelindustrie eingesetzt werden können, sind elektrochemische Methoden besonders vielversprechend. Viele Unternehmen führen bereits Mykotoxinanalytik in eigenen Laboren am Produktionsstandort durch, dennoch gibt es große Bestrebungen Analysenmethoden weiter zu vereinfachen. Der Enzyme-linked Immunosorbent Assay (ELISA), welcher häufig mit der Meerrettichperoxidase als enzymatischem Label und 3,3',5,5'-Tetramethylbenzidine (TMB)/H2O2 als Enzymsubstraten arbeitet, ermöglicht den sensitiven Mykotoxinnachweis mithilfe optischer Detektionsmethoden. Zur Miniaturisierung des Detektionsschrittes wurde in dieser Arbeit der Aufbau von elektrochemischen Detektionssystemen für die Mykotoxinanalytik untersucht. Dazu wurde zunächst die elektrochemische Reaktion von TMB an verschiedenen Materialien siebgedruckter Elektroden (Kohlenstoff und Gold) sowie bei verschiedenen pH-Werten (pH 1 und pH 4) untersucht. Eine stabile Elektrodenreaktion, welche die Grundlage für den weiteren Aufbau des elektrochemischen Detektionssystems darstellt, konnte bei pH 1 an Goldelektroden erzielt werden. Basierend darauf wurde eine amperometrische Detektionsmethode für oxidiertes TMB entwickelt, wofür eine maßgefertigte Durchflusszelle verwendet wurde. Die amperometrische TMB-Detektion wurde für einen kompetitiven Magnetpartikel-basierten Immunoassay für Ochratoxin A eingesetzt. Mit diesem Assay wurde eine Nachweisgrenze von 150 pM (60 ng L-1) erreicht und die Ergebnisse konnten durch optische Detektion verifiziert werden. Die Anwendbarkeit des Assays konnte in Ochratoxin A dotiertem Bier demonstriert werden, wobei für die Detektion ein tragbarer Potentiostat verwendet wurde, welcher über Bluetooth mit einem Smartphone verbunden war. Hiermit konnten niedrige Ochratoxin A Konzentration von bis zu 1.2 nM (0.5 µg L-1) bestimmt werden. Aufbauend auf dem entwickelten elektrochemischen Detektionssystem für TMB wurde die Anwendbarkeit des Ansatzes auf einen Magnetpartikel-basierten Immunoassay für das Ergotalkaloid Ergometrine, evaluiert. Unter optimierten Bedingungen konnte mit dem Assay eine Nachweisgrenze von 3 nM (1 µg L-1) erreicht werden. In mit Ergometrin versetztem Roggenmehl konnten Konzentrationen von 25 bis 250 µg kg-1 nachgewiesen werden. Die entwickelte elektrochemische Nachweismethode für TMB bietet einen vielversprechenden Ansatz für den Einsatz in vielen anderen Meerrettichperoxidase-basierten Assays. Für das Mykotoxin Fumonisin B1, wurde ein neues sensorisches System entwickelt, welches auf einem enzymatischen elektrochemischen Nachweis basiert. Hierfür wurde eine Aspergillus niger Fumonisin Aminoxidase (AnFAO) rekombinant als Fusionsprotein mit dem Maltose-bindenden Protein exprimiert. AnFAO katalysiert die oxidative Deaminierung von Fumonisinen, wobei H2O2 gebildet wird. Es konnte gezeigt werden, dass AnFAO eine hohe Lagerungs- und Temperaturstabilität hat. Für den Nachweis von Fumonisin B1 wurde das Enzym kovalent an Magnetpartikel gekoppelt. Das enzymatisch produzierte H2O2 konnte anschließend amperometrisch mithilfe von Preußisch Blau/Kohlenstoff-Elektroden in der maßgefertigten Durchflusszelle detektiert werden. Fumonisin B1 konnte bis zu einer Konzentration von 1,5 µM (≈ 1 mg L-1) quantifiziert werden. Das entwickelte System stellt einen neuen Ansatz dar, um Mykotoxine unter Nutzung von Enzymen und elektrochemischen Methoden zu detektieren. KW - Mycotoxins KW - Biosensor KW - Antibodies KW - Electrochemical detection PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:517-opus4-607477 DO - https://doi.org/10.25932/publishup-60747 SP - 1 EP - 96 PB - Universität Potsdam CY - Potsdam AN - OPUS4-59189 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Gaddampally, Mohan Reddy A1 - Völzke, Holger T1 - Fracture Mechanics Analysis of Spent Fuel Claddings during Long-Term Dry Interim Storage N2 - The prevention of brittle fracture of spent fuel claddings during long-term dry interim storage is based on experimental investigations, numerical analyses and assessment methods for predicting the mechanical behavior and determining limiting conditions. The ring compression test (RCT) is an established experimental method for characterizing cladding material. Test results for various high-burnup pressure water reactor zirconium-based fuel cladding alloys (e.g., ZIRLO®, M5®) are publicly available. To reduce the effort associated with irradiated samples in hot cells, it is helpful to perform studies on unirradiated surrogate cladding material. Based on such experimental data, load-displacement curves were numerically analyzed for selected cladding materials. In the presence of radial hydrides, a sample may suddenly fail by fracture even at small deformations. Noticeable load drops in the RCT occur associated to unstable crack propagation through the radial hydride network. The failure mechanism is quasi-cleavage in the hydrides and micro-void nucleation, growth, and coalescence in the zirconium matrix, with ductile tearing patches connecting neighboring hydrides. The failure process was simulated by cohesive zones controlled by the fracture energy and the cohesive strength. A modeling approach is presented in which the radial hydride morphology is taken into account. Based on the developed fracture mechanics approach with cohesive zone modeling, not only the deformation behavior but also the failure behavior of irradiated as well as unirradiated claddings with radial hydrides under RCT loading conditions can be adequately described. T2 - 20th International Symposium on the Packaging and Transportation of Radioactive Materials (PATRAM 2022) CY - Juan-les-Pins, France DA - 11.06.2023 KW - Extended Interim Storage KW - Nuclear Fuel Cladding KW - Numerical Failure Analysis KW - Ring Compression Test KW - Spent Fuel Characterization PY - 2023 SP - 1 EP - 8 AN - OPUS4-59146 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Caruso, Stefano A1 - Vlassopoulos, Efstathios A1 - Dagan, Ron A1 - Fiorito, Luca A1 - Herm, Michel A1 - Jansson, Peter A1 - Kromar, Marjan A1 - Király, Márton A1 - Leppanen, Jaakko A1 - Feria Marquez, Francisco A1 - Metz, Volker A1 - Papaioannou, Dimitrios A1 - Herranz, Luis Enrique A1 - Rochman, Dimitri A1 - Schillebeeckx, Peter A1 - Seidl, Marcus A1 - Hernandez Solis, Augusto A1 - Stankovskiy, Alexey A1 - Alvarez Velarde, Francisco A1 - Verwerft, Marc A1 - Rodriguez Villagra, Nieves A1 - Zencker, Uwe A1 - Žerovnik, Gasper T1 - EURAD - Work Package 8 - Deliverable 8.1 - State-of-the-art report N2 - A state-of-the-art (SOTA) review on characterisation of spent nuclear fuel (SNF) properties in terms of source term and inventory assessment (neutron, gamma-ray emission, decay heat, radionuclide inventory, elemental content) and in terms of out-of-core fuel performance (cladding performance and fuel integrity in view of the safety criteria for SNF interim storage, transport and canister packaging) using several numerical and experimental approaches and methodologies is presented. This SOTA report is a result of the spent fuel characterisation (SFC) work package as part of the European Joint Programme on Radioactive Waste Management (EURAD), which offers an overview of the status of knowledge in the field of SNF characterisation and assessment during the pre-disposal phase. The document aims to focus on the current safety-significant gaps and related challenges, providing a direct link to the goals of the mandated actors of EURAD. The report is expected to be used by all EURAD colleagues in their national programmes as a key resource for knowledge management programmes and to contribute to demonstrating and documenting the state-of-the-art. KW - Radioactive waste management KW - Spent fuel characterisation KW - Extended interim storage KW - Predisposal PY - 2022 UR - https://www.ejp-eurad.eu/publications/eurad-d81-state-art-report SP - 1 EP - 112 PB - Agence Nationale pour la Gestion des Déchets Radioactifs (ANDRA) CY - Châtenay-Malabry AN - OPUS4-59154 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Vergin, Chantal Celine T1 - Entwicklung eines Extraktionsverfahrens für Mykotoxine aus Lebensmitteln für die Messung in immunanalytischen Assays und Sensoren N2 - Mykotoxine sind sekundäre Stoffwechselprodukte, die von Schimmelpilzen gebildet werden. Sie sind unvermeidliche Lebensmittelkontaminanten und stellen daher ein ernstes Gesundheitsrisiko für Mensch und Tier dar. Aus diesem Grund hat die Europäische Kommission Vorschriften erlassen, die Höchstwerte für Mykotoxine in bestimmten Lebensmitteln vorsehen. Um die gesetzlichen Grenzwerte einzuhalten, müssen in der Lebensmittelindustrie Mykotoxinanalysen der eingehenden Waren durchgeführt werden. Gegenwärtig umfasst die Analyse zeitaufwändige Probenvorbereitungsschritte, denen in der Regel eine chromatographische Analyse folgt. Immunoassays ermöglichen eine Vor-Ort-Analyse, aber in der Regel sind für feste Lebensmittelproben lösungsmittelbasierte Extraktionsschritte erforderlich. Da Immunoassays in der Regel nicht mit den hohen Lösungsmittelkonzentrationen kompatibel sind, die üblicherweise für die Mykotoxinextraktion verwendet werden (z.B. Acetonitril oder Methanol), war es das Ziel dieser Arbeit, ein Extraktionsverfahren für die Mykotoxine Deoxynivalenol und Ochratoxin A aus Weizenmehl und Getreide zu entwickeln, das für Immunoassays und -sensoren verwendet werden kann. Vier verschiedene Lösungsmittel, Methanol (10 %), Ethanol (5 %) und Acetonitril (10 %) sowie Milli-Q-Wasser wurden für die Extraktion des Analyten Deoxynivalenol getestet. Um negative Umweltaspekte zu vermeiden und aufgrund der vergleichbaren Extraktionseffizienz von Milli-Q-Wasser gegenüber den anderen Lösungsmitteln, wurde Milli-Q-Wasser als Extraktionslösung im optimierten Extraktionsprotokoll für Deoxynivalenol verwendet. Es wurden verschiedene Extraktionsbedingungen, wie die Extraktionszeit, das Lösungsmittel-Feststoff-Verhältnis, der Filtrationsschritt, der Zentrifugationsschritt sowie die Zusammensetzung des Wassers untersucht. Auf der Grundlage der Ergebnisse wurde ein Extraktionsprotokoll festgelegt, mit dem Wiederfindungsraten in einem Bereich von x bis x erzielt wurden. Das Extraktionsprotokoll umfasste die Extraktion von 2 g Weizenmehl mit 40 ml Milli-Q-Wasser für 30 Minuten, die anschließende Zentrifugation bei 3000 U/min für 15 Minuten bei 4 °C und die Filtration des Überstands. KW - Mykotoxine KW - ELISA KW - Probenvorbereitung PY - 2023 SP - 1 EP - 81 CY - Berlin AN - OPUS4-59199 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sunder, S. A1 - Jauregui Rozo, Maria A1 - Schartel, Bernhard A1 - Ruckdäschel, H. T1 - Adapting intumescent/low-melting glass flame-retardant formulations for transfer to glass-fiber-reinforced composites and post-fire mechanical analysis N2 - The residual post-fire mechanical properties of fiber-reinforced epoxy composites are influenced by their fire residues after burning. This study uses intumescent/low-melting glass flame retardants to tailor fire residues in epoxy resin. Processibility of prepregs and their quality are analysed for transfer of the flame-retardant epoxy resins to layered glass-fiber reinforced composites. Minimal effects were found on the pre-fire flexural strengths of the composites due to low loading of the flame retardants. However, when transferred to glass-fiber reinforced composites, the fire residues diminish significantly. Further studies are required to improve theoretical and experimental estimations of the post-fire mechanics of the composites. T2 - SAMPE Europe Conference 2023 CY - Madrid, Spain DA - 03.10.2023 KW - Fire residue KW - Prepregs KW - Mechanics KW - Lightweight materials KW - Composites KW - Flame retardancy PY - 2023 SP - 1 EP - 7 AN - OPUS4-59138 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bintz, Thilo A1 - Kruschwitz, Sabine T1 - Investigation of Capillary Water Absorption of Clinker-Reduced Binders by NMR Relaxometry N2 - To evaluate the durability of new alternative cement compositions, it is important to examine the internal transport of moisture through these materials. For this purpose, mortars were prepared from different types of cement and capillary suction experiments were carried out. The moisture transport was studied with an NMR tomograph and compared with weight measurements. With the tomograph, the total moisture input could be determined, as well as the moisture content within the samples non-destructively and spatially resolved. This allows precise observation of the moisture fronts. The tomograph was also used to determine the capillary transport coefficient. T2 - International Conference on Electromagnetic Wave Interaction with Water and Moist Substances of the International Society for Electromagnetic Aquametry (ISEMA) 2023 CY - Brisbane, Ausralia DA - 25.09.2023 KW - NMR relaxometry KW - Capillary suction KW - Capillary transport coefficient PY - 2023 SP - 1 EP - 3 AN - OPUS4-59217 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gleim, Tobias A1 - Neumann, Martin A1 - Linnemann, Konrad A1 - Wille, Frank T1 - Welding Seam Safety Evaluation in a Thick-Walled Type B Transport Package N2 - The safety demonstration of heavy weight type B transport packages used for storing spent nuclear fuel (SNF) or radioactive waste is ensured by a combination of physical testing and numerical calculations. While experiments are performed in accordance with the IAEA regulations for selected drop scenarios, Finite-Element-Method (FEM) simulations are used to predict the most damaging case and to investigate additional drop positions. BAM as competent authority in Germany has performed different investigations of a welding seam for a typical large transport package made of A508 forged steel, where the bottom plate is welded to the cylindrical shell. The package has a mass of approx. 120 t. Results of physical drop tests with a full-scale model and accompanying preliminary FEM simulations are presented to determine the decisive stresses in the welding seam. A drop test only represents one set of a package and test parameters. A further parameter analysis is considered to account for allowable variations of packaging properties (e.g. resulting from the manufacturing process) and, based on IAEA requirements, the temperature dependence of the material behaviour. The results of the stress analyses from the drop test and the simulation form the basis and provide the input parameters for a fracture mechanics analysis. In addition to the IAEA specifications, further standards are taken into account for an in-depth investigation, see R6 [1], BS 7910 [2] and API 579-1/ASME FFS1 [3]. All the above-mentioned standards require a manufacturer-specific defect analysis with respect to size and position. Both result from the welding process and the following heat treatment regime. The maximum defect sizes are ensured with non-destructive test methods (such as ultrasonic or particle methods) as integral part of the manufacturing process of the welding seam. Another important parameter in the welding process is the residual stress (secondary stress). The combination of the primary and secondary stress determines the total stress in the welding seam. The most damaging case of the welding seam is determined and evaluated with help of the abovementioned standards and taking into account the IAEA requirements with respect to defect sizes, material properties, primary and residual stress, yield strength etc. T2 - PATRAM 22 - The International Symposium on the Packaging and Transportation of Radioactive Materials CY - Juan-Les-Pins, Antibes DA - 11.06.2023 KW - Welding KW - Transport Package KW - Fracture Mechanics PY - 2023 SP - 1 EP - 11 AN - OPUS4-59421 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Häusler, F. A1 - Stührenberg, J. A1 - Neumann, Patrick P. ED - Sigalov, K. ED - Hagedorn, P. ED - Schönfelder, P. ED - Faltin, B. ED - Zentgraf, S. ED - Block, M. T1 - Gasquellenlokalisierung mit Drohnenschwärmen N2 - Gasquellenlokalisierungen (Gas Source Localization, GSL) tragen dazu bei, die Folgen von Industrieunfällen und Naturkatastrophen zu mildern. Während die GSL, wenn von Menschen durchgeführt, gefährlich und zeitaufwändig ist, können Schwärme von wendigen und kostengünstigen Nanodrohnen die Effizienz und Sicherheit der Suche erhöhen. Da die geringe Nutzlast von Nanodrohnen die Sensor- und Rechenressourcen einschränkt, werden Strategien zur Koordination des Roboterschwarms verwendet, die von biologischen Schwärmen, wie Kolonien sozialer Insekten, inspiriert sind. Die meisten Schwarm-GSL-Strategien verwenden das Maximum der Gaskonzentrationsverteilung zur Schätzung der Gasquellenposition. Experimente legen jedoch nahe, dass die Intermittenz der Gasverteilung vielversprechender ist. In diesem Beitrag wird eine neuartige GSL-Strategie für Schwärme vorgestellt, die auf Pheromonkommunikation und Intermittenz der Gasverteilung basiert. Die Agenten, d.h. die Nanodrohnen, emittieren Pheromonmarker in einer virtuellen Umgebung, wenn sie eine neue Gaswolke feststellen. Die Agenten werden durch virtuelle Kräfte gesteuert und nutzen abwechselnd das Wissen des Schwarms, indem sie dem Pheromongradienten folgen, oder erkunden den Suchraum, indem sie einen Zufallspunkt ansteuern. Zur Kollisionsvermeidung werden die Agenten durchgehend von anderen Agenten und Wänden abgestoßen. Die Strategie wurde auf drei Nanodrohnen implementiert und durch ein Experiment in einem Innenraum mit einer statischen Gasquelle validiert. Die Ergebnisse zeigen eine Verbesserung gegenüber maximabasierten Verfahren und geringe Lokalisierungsfehler in Windrichtung. T2 - 34. Forum Bauinformatik 2023 CY - Bochum, Germany DA - 06.08.2023 KW - Mobile Robotic Olfaction KW - Bouts KW - Mobile Sensorik KW - Nanodrohnen KW - Pheromonkommunikation KW - Schwarmrobotik PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-594320 DO - https://doi.org/10.13154/294-10088 SP - 168 EP - 175 AN - OPUS4-59432 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Suárez Ocano, Patricia T1 - Thermodynamic and microstructural stabilities at high temperatures and their effects on mechanical properties in an AlMo0.5NbTa0.5TiZr refractory high entropy superalloy N2 - Today’s industrial demands challenge the research and development sector to make advances in the design and properties of materials that can withstand harsh environments. The AlMo0.5NbTa0.5TiZr refractory high-entropy superalloy (RSA), with a remarkable morphological similarity to the γ/γ' microstructure of Ni-based superalloys and promising high-temperature compressive properties, has been considered as a candidate for structural applications. However, additional properties need to be investigated in order to assess the suitability of this alloy for high temperature applications. Therefore, this work investigates the thermodynamic and microstructural stabilities of the RSA at room temperature and between 900 and 1100 °C, and their influence on the mechanical properties. Although it is possible to improve the mechanical properties at 20 °C by tuning the cooling rate, long-term high temperature exposures lead to phase instabilities that negatively influence the creep behavior. N2 - Die heutigen industriellen Anforderungen erfordern Fortschritte bei Werkstoffdesign und -entwicklung, insbesondere für raue Umgebungen. Die hochentropische Refraktärsuperlegierung (RSA) AlMo0.5NbTa0.5TiZr, die eine bemerkenswerte morphologische Ähnlichkeit mit der γ/γ'-Mikrostruktur von Ni-Basis-Superlegierungen und vielversprechende Hochtemperatur-Druckeigenschaften aufweist, wurde als Kandidat für strukturelle Anwendungen erwägt. Weitere Eigenschaften müssen untersucht werden, um die Eignung dieser Legierung für Hochtemperaturanwendungen zu beurteilen. In dieser Arbeit werden die thermodynamischen und mikrostrukturellen Stabilitäten von RSA bei Raumtemperatur und zwischen 900 und 1100°C sowie deren Einfluss auf die mechanischen Eigenschaften untersucht. Obwohl es möglich ist, die mechanischen Eigenschaften bei 20 °C durch Abstimmung der Abkühlrate zu verbessern, führen langfristige Hochtemperaturexpositionen zu Phaseninstabilitäten, die das Kriechverhalten negativ beeinflussen. KW - Hochentropielegierung KW - Gefüge (Werkstoffkunde) KW - Mikrostruktur KW - Kriechen KW - Thermodynamische Stabilität KW - High entropy alloys KW - Microstructure KW - Creep KW - Thermodynamic stability PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:hbz:294-108415 DO - https://doi.org/10.13154/294-10841 SP - 1 EP - 170 CY - Bochum AN - OPUS4-59929 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pech May, Nelson Wilbur A1 - Lecompagnon, Julien A1 - Hirsch, Philipp Daniel A1 - Ziegler, Mathias T1 - Robot-assisted infrared thermography for surface breaking crack detection on complex shaped components N2 - Infrared thermography using a focused (spot or line) beam has proved to be effective for detection of surface breaking cracks on planar samples. In this work, we use the same principle, but applied to complex shaped components, like a rail section, a gear, and a gas turbine blade. We use a six-axis robot arm to move the sample in front of our thermographic setup. Several scanning paths and thermographic parameters are explored: scanning speed, density of points in each scanning slice, laser power and camera frame-rate. Additionally, we explore semi-automatic evaluation algorithms for crack detection, as well as 2D-to-3D registration of the found indications. T2 - SPIE Future Sensing Technologies, 2023 CY - Yokohama, Japan DA - 18.04.2023 KW - Complex shaped component testing KW - Flying line thermography KW - Robot-assisted thermography KW - Crack detection KW - Robot path planning KW - 2D/3D thermographic registration PY - 2023 DO - https://doi.org/10.1117/12.2666757 VL - 12327 SP - 1 EP - 3 PB - SPIE Future Sensing Technologies AN - OPUS4-59867 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Heidenreich, Sebastian A1 - Bär, Markus A1 - Klauenberg, Katy A1 - Elster, Clemens A1 - Harris, Peter A1 - Lines, Keith A1 - Hippolyte, Jean-Laurent A1 - George, Indhu A1 - Wright, Louise A1 - Cox, Maurice A1 - Rhodes, Susan A1 - Zilberti, Luca A1 - Manzin, Alessandra A1 - Pennecchi, Francesca A1 - Kok, Gertjan A1 - van der Veen, Adriaan A1 - Fischer, Nicolas A1 - Sousa, Joao Alves A1 - Vogel, Kristin A1 - Bosnjakovic, Alen A1 - Ellison, Stephen T1 - Strategic Agenda, European Metrology Network for Mathematics and Statistics N2 - This document constitutes the Strategic Research Agenda (SRA) for the European Metrology Network for Mathematics and Statistics in Metrology (EMN Mathmet). The EMN Mathmet is an alliance of European National Metrology Institutes (NMIs), Designated Institutes (DIs) and an EMN Partner that aims to strengthen research and cooperation in the field. The SRA has been developed within a European project (EMPIR 18NET05 MATHMET) to promote and support the network. The SRA was developed based on a consultation process with stakeholders and the strategies of individual NMIs and DIs, and in alignment with the EURAMET 2030 strategy. As a key result, the SRA defines a long-term research goal: the EMN Mathmet will coordinate research to strengthen the trust in algorithms, software tools and data to underpin digital transformation. For this purpose, new emerging research topics where algorithms, software tools and data play a significant role were identified: (i) Artificial Intelligence and Machine Learning, and (ii) Computational Modelling and Virtual Metrology. The foundation for the development of these new topics is given by the traditional focus on (iii) Data Analysis and Uncertainty Evaluation. The SRA characterises the future needs and challenges in the field of mathematics and statistics in metrology and provides an outline of how the EMN Mathmet can meet these new emerging requirements. KW - Research Agenda KW - Metrology KW - Mathematics and Statistics PY - 2023 UR - https://www.euramet.org/european-metrology-networks/mathmet/strategy/strategic-research-agenda SN - 978-3-942992-78-7 SP - 1 EP - 68 PB - EURAMET e.V. CY - Braunschweig AN - OPUS4-59526 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF ED - Kulla, D. ED - Saadat, A. ED - Spalek, A. ED - Bettge, Dirk ED - Hesshaus, A. T1 - GeoHyBe - Geothermische Anlagen unter hydrogeochemischen Aspekten der Betriebssicherheit N2 - Mit GeoHyBe wurde ein neues Forum für die etwa 150 Vertreter der verschiedensten Berufszweige geschaffen, die eng mit dem Thema "Geothermische Anlagen unter hydrogeochemischen Aspekten der Betriebssicherheit" in Berührung stehen. Insgesamt besteht der Beitrag zu Zielen des Forschungsschwerpunkts Geothermie somit in zwei Hauptergebnissen: in der Schaffung der oben genannten Plattform sowie im fachlichen Austausch über hydrogeochemische Probleme mit tiefen geothermischen Anlagen. Ferner wurden vor allem im Laufe der Podiumsdiskussion wünschenswerte Entwicklungen geäußert (Datenfreigabe bzw. Erleichterung des Zugangs zu relevanten Daten, Bedarf an weiterführenden oder vertiefenden Veranstaltungen etc.). Die erreichten Ergebnisse haben das Potenzial, zu einer vereinfachten, besser angepassten Anlagenplanung und einer Verbesserung tiefengeothermischer Technologien und Materialien beizutragen. Dies führt zu einer erhöhten Betriebssicherheit und Energieausbeute geothermischer Anlagen, welche das klimapolitische Ziel der Erhöhung des Anteils regenerativer Energien am Gesamtenergieverbrauch und den Rückgang des CO₂-Ausstoßes unterstützen. Als bedeutendstes wissenschaftlich-technisches Ergebnis des Workshops ist - neben dem Austausch von relevantem Fachwissen - sicherlich die Formulierung des gemeinsamen Verbesserungs- und Forschungsbedarfs hervorzuheben. Vor allem die Schwierigkeiten in der Beschaffung und im Austausch geothermisch relevanter Daten wurden betont. Daneben besteht bezüglich hydrogeochemischer und mikrobieller Prozesse unter den anspruchsvollen Bedingungen in der tiefen Geothermie offensichtlich noch ein großer Bedarf an Forschung und Entwicklung, um den Einsatz geeigneter Materialien und angepasster Technologien gewährleisten zu können. Wesentliche Erfahrungen wurden vor allem bezüglich der Aktualität und des Diskussionsbedarfs zum Thema gemacht. GeoHyBe kann im Rückblick eher als Auftaktveranstaltung denn als abgeschlossenes Projekt betrachtet werden, da von vielen Seiten der Bedarf nach weiterführenden und/oder vertiefenden Veranstaltungen geäußert wurde. T2 - GeoHyBe - Geothermische Anlagen unter hydrogeochemischen Aspekten der Betriebssicherheit CY - Berlin, Germany DA - 23.03.2009 KW - Alternative Energieformen KW - Geochemie KW - Grundwasser KW - Regenerative Energieformen PY - 2009 UR - https://edocs.tib.eu/files/e01fb10/617262454.pdf N1 - Abschlussbericht zum Vorhaben 0325085 "GeoHyBe - Geothermische Anlagen unter hydrogeochemischen Aspekten der Betriebssicherheit", gefördert durch das Bundesministerium für Umwelt, Naturschutz und Reaktorsicherheit vom 01.07.2008 bis 30.06.2009. SP - 1 EP - 33 PB - Bundesanstalt für Geowissenschaften und Rohstoffe (BGR) CY - Hannover AN - OPUS4-59555 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Martin T1 - Selbstentzündung von Biokohlen – Lager- und Transportsicherheit N2 - Mit der Abkehr von der Nutzung fossiler Rohstoffe rücken regenerative Energieträger immer weiter in den Focus. Neben klassischen Holzkohlen werden verstärkt so genannte Biokohlen produziert. Dieser Begriff findet Verwendung für mit Hilfe verschiedener Verfahren karbonisierte pflanzliche, tierische oder mikrobielle Ausgangsstoffe. Diese Kohlen werden zum Teil über weite Strecken zum Bestimmungsort transportiert (Überseetransporte) oder vor Verwendung für längere Zeit gelagert. Häufig zeigen diese Kohlen ein kritisches Selbstentzündungsverhalten, wobei Einstufungstests (UN N.4 Test) versagen können. Ein negatives Testergebnis des UN N.4 Tests führte dabei in der Vergangenheit zur Nichteinstufung als selbsterhitzungsfähiger Stoff; in der Praxis entzündeten sich aber bereits vergleichsweise kleine Schüttungen (einige m³), z. B. beim Seetransport in Containern. Der Artikel geht auf dieses Problem ein und stellt Prüfverfahren vor. Aus den Ergebnissen durchgeführter Untersuchungen werden Empfehlungen für sicheren Transport und Lagerung abgeleitet. T2 - Magdeburg-Köthener Brandschutz- und Sicherheitstagung CY - Magdeburg, Germany DA - 14.03.2024 KW - Biokohlen KW - Selbstentzündung KW - Gefahrguteinstufung PY - 2024 SN - 978-3-948749-41-5 SP - 68 EP - 77 PB - Otto-von-Guericke-Universität Magdeburg CY - Magdeburg AN - OPUS4-59717 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Feldkamp, Martin A1 - Quercetti, Thomas A1 - Gleim, Tobias A1 - Wille, Frank T1 - Evaluation of Heat Fluxes in Fire Reference Test Conducted in BAM Propane Gas Fire Test Facility N2 - Packages for the transport of intermediate- and high-level radioactive waste are designed to withstand severe accidents. The International Atomic Energy Agency (IAEA) has established specific mechanical and thermal tests. Packages for the transport of radioactive material must withstand these tests to comply with the Regulations for the Safe Transport of Radioactive Materials IAEA [IAEA (2018)]. A fire reference package was developed with the primary objective to demonstrate that the fire meets the regulatory requirements. Another aim is to characterise the boundary conditions of the actual fire as input parameters for thermo-mechanical simulations. A simple method to characterise the boundary conditions of a real steady state fire with a fire reference package is presented. The thermal test mainly consists of a 30 minute fully engulfing 800°C pool fire or an equally severe fire, such as a propane gas fire. The fire reference tests are performed prior to the actual fire test with the real package. The heat fluxes into the package depend substantially on the fire characteristics and the surface temperature of the package. To investigate local and overall heat fluxes over a wide range of surface temperatures in this test facility a fire reference package was designed for repeated use. The fire reference package presented in this paper represents the outer geometry of a small transport container for radioactive material and is used as a device in civil engineering. It is designed as a closed steel sheet cylinder with a wall thickness of 10 mm, a length of 182 mm and a diameter of 102 mm. The package was instrumented with thermocouples and filled with heat resistant insulation material. Open-air fire tests were performed in a BAM propane gas fire test facility with the fire reference package. The measured temperatures are used to determine the changes of heat fluxes into the fire reference package in relation to the package surface temperature. The calculated heat fluxes allow its fitting to express the thermal exposure as simple mathematical boundary condition. Therefore, in a first approach, fire properties such as adiabatic surface temperature (AST) as proposed by Wickström et al. (2007), convection coefficient and emissivity are determined mathematically fitting the heat flux development presented in this paper. The evaluated results provide an initial picture of local fire characteristics of the conducted propane gas fire and are a further development of previous works from Feldkamp et al. (2020). The results can be used in thermal and thermo-mechanical models to simulate the load on the real transport package in fire. The test shows that the examined propane gas fire covers the IAEA-fire over a wide range of surface temperatures with the chosen test stand parameters. T2 - SMiRT 27 (27th conference on Structural Mechanics in Reactor Technology) CY - Yokohama, Japan DA - 03.03.2024 KW - Fire KW - Propane KW - Heat Flux KW - Fire Reference PY - 2024 SP - 1 EP - 10 PB - IASMiRT AN - OPUS4-59679 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pauw, Brian Richard T1 - Trinamic TMCL IOC for exposing Trinamics motor controllers to EPICS CA N2 - Trinamic TMCL IOC is a Python package designed for controlling stepper motors connected to a Trinamic board using the TMCL language (all boards supported by PyTrinamic should now work, has been tested on the TMCM 6110 and the TMCM 6214). Since it is implementing the TMCL protocol, it should be easy to adapt to other Trinamic motor controller boards. This package assumes the motor controller is connected over a machine network via a network-to-serial converter, but the underlying PyTrinamic package allows for other connections too. This allows the control of attached motors via the EPICS Channel-Access virtual communications bus. If EPICS is not desired, plain Pythonic control via motion_control should also be possible. An example for this will be provided in the example.ipynb Jupyter notebook. This package leverages Caproto for EPICS IOCs and a modified PyTrinamic library for the motor board control, and interfaces between the two via an internal set of dataclasses. Configuration for the motors and boards are loaded from YAML files (see tests/testdata/example_config.yaml). The modifications to PyTrinamic involved extending their library with a socket interface. This was a minor modification that should eventually find its way into the official package (a pull request has been submitted). KW - Instrumentation KW - Motor controller KW - EPICS KW - Channel access KW - Instrument control KW - Laboratory automation PY - 2024 DO - https://doi.org/10.5281/zenodo.10792593 PB - Zenodo CY - Geneva AN - OPUS4-59624 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schischke, Karsten A1 - Rückschloss, Jana A1 - Schlegel, Moritz-C. A1 - Zöllinger, Jonathan A1 - Nissen, Nils F. A1 - Schneider-Ramelow, Martin T1 - The European Union’s Energy Label for Smartphones: Does it guide consumers to make environmentally sustainable choices? N2 - The European Commission adopted an EU Energy Label for smartphones and tablets in June 2023. For the first time, the EU Energy Label will depict, among energy efficiency, also a reparability score, battery endurance, battery lifetime, drop resistance and dust and water ingress protection. However, does the multitude of parameters bear the risk to confuse consumers instead of triggering environmentally sustainable purchase decisions? In a survey in Germany, consumers were asked to make a choice when the label does not clearly identify the environmentally better product. Instead, energy efficiency has to be valued against reparability, reliability against energy efficiency, and reparability against reliability. The sustainability lever of the different aspects is not the same, as e.g. lifetime extension has a much more positive environmental impact than energy efficiency in case of mobile devices. Therefore, the question remains, whether consumers intuitively make the right choice. Results of the survey indicate that consumers interpret the complex label in the desired manner and value those aspects higher, which indeed have a more positive effect on the environment. T2 - 13th International Conference on Consumer Electronics CY - Berlin, Germany DA - 03.09.2023 KW - Energy efficiency KW - EU Energy Labelling KW - Reparability KW - Reliability KW - ESPR PY - 2023 UR - https://ieeexplore.ieee.org/document/10375619 DO - https://doi.org/10.1109/ICCE-Berlin58801.2023.10375619 SP - 1 EP - 6 PB - IEEE AN - OPUS4-59318 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Linnemann, Konrad A1 - Quercetti, Thomas A1 - Sterthaus, Jens A1 - Ballheimer, Viktor T1 - Experimental and numerical investigation of prestressed bolt connections under lateral displacements N2 - The containment system of transport packages for spent nuclear fuel and high-level waste usually includes bolted lids with metal gaskets. The packages are assessed to specific transport conditions which are specified in the IAEA safety standards SSR-6 (IAEA 2018). These transport conditions, especially the so-called accident conditions of transport, imply high dynamic loading on the lids and the bolt connections of the package. The response of the lid systems on the mechanical accident conditions is generally investigated by experimental drop tests or numerically, e.g., by finite element analyses. The interpretation of the drop test results for the verification of the numerical models is often not obvious due to the complex superposition of different effects in the real tests. BAM has started a research project to get a better understanding about the behavior of prestressed bolt connections under loadings typical for these drop tests. In this context an experimental test set-up was developed to investigate the response of a single bolt connection under a prescribed lateral displacement of clamped parts. The bolt is instrumented by strain gauges to get the pretensional, the torsional and the bending stress in the bolt shank. Furthermore, the lateral movement and the tilt of the bolt head is measured during the test. A finite element model of the test set-up has been created in Abaqus FEA (Simulia 2021). The very detailed instrumentation of the test set-up shall give the opportunity to investigate and validate the numerical model. The aim of this paper is to give an overview about the proposed research project and to present first results. T2 - SMIRT 26 (26th conference on Structural Mechanics in Reactor Technology) CY - Potsdam, Germany DA - 10.07.2022 KW - Bolt connections KW - Finite element anaylsis KW - Experimental testing KW - Transport package for radioactive materials PY - 2022 UR - https://www.lib.ncsu.edu/resolver/1840.20/40614 SP - 1 EP - 7 PB - IASMiRT AN - OPUS4-59378 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krankenhagen, Rainer A1 - Dell'Avvocato, Giuseppe A1 - Gohlke, Dirk A1 - Palumbo, Davide A1 - Galietti, Umberto T1 - Quantitative evaluation of the welded area in Resistance Projection Welded (RPW) thin joints by pulsed laser thermography N2 - A semi-automatic thermographic procedure for the assessment of the welded area of resistance projection welded joints has been developed. Currently, to assess the quality of RPW joints destructive tests are used and the more commonly used non-destructive technique is the ultrasonic one. The possibility for a quantitative evaluation of the welded area by thermographic technique has been proved by means of an innovative procedure applied on steel RPW joints with ‘as it’ surface conditions. Measurements obtained by thermography and ultrasound have been compared, to verify the developed procedure. T2 - Thermosense: Thermal Infrared Applications XLIV, CY - Orlando, USA DA - 03.04.2022 KW - Nondestructive evaluation KW - Ultrasonics KW - Contact area PY - 2022 DO - https://doi.org/10.1117/12.2618806 VL - 12109 SP - 1 EP - 14 PB - SPIE AN - OPUS4-59380 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grundmann, Jana A1 - Ermilova, Elena A1 - Hertwig, Andreas A1 - Klapetek, Petr A1 - Pereira, Silvania F. A1 - Rafighdoost, Jila A1 - Bodermann, Bernd T1 - Optical and Tactile Measurements on SiC Sample Defects N2 - The different defect types on SiC samples are measured with various measurement methods including optical and tactile methods. The defect types investigated include particles, carrots and triangles and they are analyzed with imaging ellipsometry, coherent Fourier scatterometry and atomic force microscopy. Each of these methods measures different properties of the defects and they all together contribute to a complete analysis. T2 - SMSI 2023 - Sensor and Measurement Science International CY - Nuremberg, Germany DA - 08.05.2023 KW - Defects KW - Silicon carbide KW - Imaging ellipsometry KW - Atomic force microscopy KW - Coherent Fourier scatterometry PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-593397 SN - 978-3-9819376-8-8 DO - https://doi.org/10.5162/SMSI2023/D5.2 VL - 2023/D5 SP - 233 EP - 234 PB - AMA Service CY - Wunstorf AN - OPUS4-59339 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schilling, Markus A1 - Bayerlein, Bernd A1 - Birkholz, H. A1 - Fliegener, S. A1 - Grundmann, J. A1 - Hanke, T. A1 - von Hartrott, P. A1 - Waitelonis, J. T1 - PMD Core Ontology (PMDco) N2 - The PMD Core Ontology (PMDco) is a comprehensive framework for representing knowledge that encompasses fundamental concepts from the domains of materials science and engineering (MSE). The PMDco has been designed as a mid-level ontology to establish a connection between specific MSE application ontologies and the domain neutral concepts found in established top-level ontologies. The primary goal of the PMDco is to promote interoperability between diverse domains. PMDco's class structure is both understandable and extensible, making it an efficient tool for organizing MSE knowledge. It serves as a semantic intermediate layer that unifies MSE knowledge representations, enabling data and metadata to be systematically integrated on key terms within the MSE domain. With PMDco, it is possible to seamlessly trace data generation. The design of PMDco is based on the W3C Provenance Ontology (PROV-O), which provides a standard framework for capturing the generation, derivation, and attribution of resources. By building on this foundation, PMDco facilitates the integration of data from various sources and the creation of complex workflows. In summary, PMDco is a valuable tool for researchers and practitioners in the MSE domains. It provides a common language for representing and sharing knowledge, allowing for efficient collaboration and promoting interoperability between diverse domains. Its design allows for the systematic integration of data and metadata, enabling seamless traceability of data generation. Overall, PMDco is a crucial step towards a unified and comprehensive understanding of the MSE domain. PMDco at GitHub: https://github.com/materialdigital/core-ontology KW - Ontology KW - Semantic Web technologies KW - Digitalization KW - Data Interoperability KW - PMD Core Ontology PY - 2023 UR - https://github.com/materialdigital/core-ontology/blob/f2bd420348b276583fad6fa0fb4225f17b893c78/pmd_core.ttl PB - GitHub CY - San Francisco, CA, USA AN - OPUS4-59352 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Seeber, Henrik ED - Krentel, Daniel ED - Grasse, Dennis ED - Gerbeit, Marco ED - Grobert, Steffen ED - Hauer, Thorsten T1 - Experimental Setup for the Reproducible Generation of Pressure Waves in Free Field Conditions N2 - The injuries caused by the primary blast are still poorly understood, especially in the torso region. To generate sufficiently large data sets, shock tubes are often used. However, these have some limitations, such as blockage, use of the exit jet, widening cross-sections, and scaling problems with respect to compressive strength and test objects. Therefore, it is appropriate to conduct experiments under free-field conditions, but tests with real explosives are often associated with long preparation and setup times as well as high safety requirements. Therefore, this paper presents an experimental setup for the reproducible generation of blast waves under free-field conditions. This experimental setup aims to provide a test environment for a sufficiently large specimen to investigate the behaviour of the shock wave within the specimen, especially at the media interfaces. As an example of application, the influence of the primary explosive effect on protective equipment or on tissue simulants for the investigation of blast injuries can be mentioned. An autoclave is used as a shock wave generator. It has a volume of 0.065 m3 and is filled with a stoichiometric acetylene-oxygen gas mixture. The setup and turnaround time is approximately 30 minutes. The following factors have been selected as target variables for the optimization of the shock wave generator: reproducibility of the pressure wave, use-case-relevant positive phase duration and peak overpressure, a pressure curve characteristic corresponding to that of a military explosive under undisturbed free field conditions, and short setup times of the experimental setup. For this purpose, the experimental setup is presented in this paper. Several series of measurements are presented, showing the characteristics of the generated pressure wave. For the generated pressure wave, the classical pressure curve characteristics can be clearly recognized. A peak pressure of 92 kPa is reached at a distance of 1 m from the opening, and the first positive pressure phase lasts 1.17 ms. Furthermore, the pressure wave propagates in a hemispherical shape. The typical characteristics of the blast wave generated by the SWG have been demonstrated using the military explosive PETN. It is shown that the actual load case corresponds to about 70 g of PETN. T2 - 26th International Symposium on Military Aspects of Blast and Shock CY - Wolongong, Australia DA - 03.12.2023 KW - Shock wave generator KW - Blast injury KW - Pressure wave KW - Experimental setup PY - 2023 SP - 1 EP - 13 AN - OPUS4-59357 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Gornushkin, Igor B. A1 - Kornev, R. A. A1 - Shabarova, L. V. A1 - Ermakov, A. A. A1 - Mochalov, G. M. A1 - Rekunov, N. V. A1 - Medov, V. A. A1 - Chaschina, A. D. A1 - Kalinina, A. A. T1 - Features of Plasma-Chemical Hydrogen Reduction of Volatile Silicon and Germanium Chlorides in RF-arc Discharge N2 - The processes of hydrogen reduction of silicon and germanium chlorides under the conditions of radio-frequency (40.68 MHz) counteracted arc discharge stabilized between two rod electrodes were investigated. The main gas-phase and solid products of plasma-chemical transformations were determined. Thermodynamic analysis of SiCl4 + H2 and GeCl4 + H2 systems was carried out. It is shown that under the implemented experimental conditions, equilibrium components of the products are established. The detected spectra of chemical activity were studied, which gave reason to assume that the molecular mechanism of the hydrogen reduction process is the main one. The impurity composition of gas-phase and solid reaction products was investigated. The possibility of single-stage production of high-purity Si and Ge mainly in the form of compact ingots, as well as high-purity chlorosilanes and trichlorogermane, was shown. KW - RF-arc discharge KW - Hydrogen reduction KW - Silicon chloride KW - Germanium chloride KW - Thermodynamic KW - Silicon KW - Germanium PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-588909 DO - https://doi.org/10.20944/preprints202311.1412.v1 SP - 1 EP - 14 PB - MDPI CY - Basel AN - OPUS4-58890 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Srinivasan, Krishnanand A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Laser Metal Deposition of Rene 80 – Microstructure and Solidification Behaviour Modelling N2 - New developments in nickel-based superalloys and production methods, such as the use of additive manufacturing (AM), can result in innovative designs for turbines. It is crucial to understand how the material behaves during the AM process to advance industrial use of these techniques. An analytical model based on reaction-diffusion formalism is developed to better explain the solidification behavior of the material during laser metal deposition (LMD). The well-known Scheil-Gulliver theory has some drawbacks, such as the assumption of equilibrium at the solid-liquid interface, which is addressed by this method. The solidified fractions under the Scheil model and the pure equilibrium model are calculated using CALPHAD simulations. Differential scanning calorimeter is used to measure the heat flow during the solid-liquid phase transformation, the result of which is further converted to solidified fractions. The analytical model is compared with all the other models for validation. T2 - Lasers in Manufacturing Conference 2023 CY - Munich, Germany DA - 26.06.2023 KW - Additive manufacturing KW - Laser metal deposition KW - Solidification behaviour KW - Analytical model KW - Nickel-based superalloy PY - 2023 SP - 1 EP - 10 AN - OPUS4-58612 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Charmi, Amir A1 - Mustapha, Samir A1 - Yilmaz, Bengisu A1 - Heimann, Jan A1 - Prager, Jens T1 - A Machine Learning Based-Guided Wave Approach for Damage Detection and Assessment in Composite Overwrapped Pressure Vessels N2 - The applications of composite overwrapped pressure vessels (COPVs) in extreme conditions, such as storing hydrogen gases at very high pressure, impose new requirements related to the system's integrity and safety. The development of a structural health monitoring (SHM) system that allows for continuous monitoring of the COPVs provides rich information about the structural integrity of the component. Furthermore, the collected data can be used for different purposes such as increasing the periodic inspection intervals, providing a remaining lifetime prognosis, and also ensuring optimal operating conditions. Ultimately this information can be complementary to the development of the envisioned digital twin of the monitored COPVs. Guided waves (GWs) are preferred to be used in continuous SHM given their ability to travel in complex structures for long distances. However, obtained GW signals are complex and require advanced processing techniques. Machine learning (ML) is increasingly utilized as the main part of the processing pipeline to automatically detect anomalies in the system's integrity. Hence, in this study, we are scrutinizing the potential of using ML to provide continuous monitoring of COPVs based on ultrasonic GW data. Data is collected from a network of sensors consisting of fifteen Piezoelectric (PZT) wafers that were surface mounted on the COPV. Two ML algorithms are used in the automated evaluation procedure (i) a long short-term memory (LSTM) autoencoder for anomaly detection (defects/impact), and (ii) a convolutional neural network (CNN) model for feature extraction and classification of the artificial damage sizes and locations. Additional data augmentation steps are introduced such as modification and addition of random noise to original signals to enhance the model's robustness to uncertainties. Overall, it was shown that the ML algorithms used were able to detect and classify the simulated damage with high accuracy. T2 - 13th European Conference on Non-Destructive Testing (ECNDT) 2023 CY - Lisbon, Portugal DA - 03.07.2023 KW - Machine learning KW - Structural health monitoring KW - COPV KW - Guided waves KW - Damage localization PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-590789 DO - https://doi.org/10.58286/28079 SN - 2941-4989 VL - 1 IS - 1 SP - 1 EP - 6 PB - NDT.net CY - Mayen AN - OPUS4-59078 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mustapha, S. A1 - Yilmaz, Bengisu A1 - Heimann, Jan A1 - Brence, Blaz A1 - Prager, Jens T1 - Guided Waves Propagation in Composite Overwrapped Pressure Vessel N2 - The application of composite overwrapped pressure vessels (COPV) to store hydrogen and other compressed gases, especially when operating at high pressures, imposed the need for an innovative and reliable approach to ensure the safe operation of the system. Continuous structural health monitoring (SHM) based on ultrasonic guided waves (GWs) is a promising approach due to the ability of the wave to propagate for long distances and go around complex structures, moreover the high sensitivity to various failure modes such as delamination, matrix cracking and debonding. In this study, we scrutinize the behavior of (GWs) within the COPV using a network of PZT elements that are used for excitation and sensing. A laser doppler vibrometer (LDV) was also used to scan the surface of the vessel in various directions. L(0,1) and L(0,2) were observed in the captured signal. The L(0, 2) appeared to be a dominant mode in the COPV and was capable of propagating along the entire length and maintaining a good signal-to-noise ratio. The L(0,2) mode maintained the same phase velocity when it is captured at various excitation angles (0, 45, and 90 degrees). The reduced effect of the orthotropy of the materials on the propagating waves is an important result as it will reduce the complexity in data processing when performing damage identification. T2 - 13th. European Conference on Non-Destructive Testing (ECNDT) CY - Lisbon, Portugal DA - 03.07.2023 KW - Composite Overwrapped Pressure Vessels KW - Guided Waves KW - Laser Doppler Vibrometer KW - Structural Health Monitoring KW - Sensors Placement PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-591081 DO - https://doi.org/10.58286/28068 SN - 2941-4989 VL - 1 IS - 1 SP - 1 EP - 6 PB - NDT.net CY - Mayen AN - OPUS4-59108 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yilmaz, Bengisu A1 - Heimann, Jan A1 - Mustapha, S. A1 - Charmi, Amir A1 - Prager, Jens T1 - Guided wave ultrasonic feature determination in Type IV composite overwrapped pressure vessels towards the digital twin N2 - The digitalization of quality control processes and the underlying data infrastructures for safety relevant components, such as hydrogen pressure vessels, plays a significant role in the transition towards Industry 4.0. In the current safety regulations for hydrogen pressure vessels, there is no established concept for structural health monitoring. The development of a reliable structural health monitoring methodology for monitoring the structural integrity of pressure vessels enables a fast-forward transition from personnel- and costintensive recurring inspections, a.k.a. periodic maintenance, to predictive maintenance. In the work presented; we investigated the application of ultrasonic guided wave propagation to monitor and assess the condition of Type IV composite overwrapped pressure vessel (COPV). A sensor network of fifteen piezo-electric wafers is placed on the carbon fibre reinforced composite cylinder. Five different artificial damage configurations are created by gluing two different weight blocks on three different locations. The database containing measured guided wave data sets is enriched by two different boundary conditions. We utilized an open-source software, openBIS labnotebook, to store and analyse experimental datasets. The guided wave ultrasonic signals were investigated and analysed by using commonly used ultrasonic features (e.g., amplitude, frequency, time of flight) as well as non-traditional time-series features (kurtosis, skewness, variance). The features were used to calculate damage index and the detection performance for the results has been evaluated. The results suggest that both traditional and non-traditional features assume significant importance in artificial damage detection. The future works will additionally involve the impacts of operational conditions, such as periodic pressure variations temperature loadings as well as material degradations. T2 - 13th European Conference on Non-Destructive Testing (ECNDT) CY - Lisbon, Portugal DA - 03.07.2023 KW - Industry 4.0 KW - Composite overwrapped pressure vessels KW - Structural health monitoring KW - Ultrasonic guided waves KW - Predictive maintenance PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-591094 DO - https://doi.org/10.58286/28072 SN - 2941-4989 VL - 1 IS - 1 SP - 1 EP - 6 PB - NDT.net CY - Mayen AN - OPUS4-59109 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Lecompagnon, Julien T1 - Nondestructive defect characterization using full-frame spatially structured super resolution laser thermography N2 - Laser-based active thermography is a contactless non-destructive testing method to detect material defects by heating the object and measuring its temperature increase with an infrared camera. Systematic deviations from predicted behavior provide insight into the inner structure of the object. However, its resolution in resolving internal structures is limited due to the diffusive nature of heat diffusion. Thermographic super resolution (SR) methods aim to overcome this limitation by combining multiple thermographic measurements and mathematical optimization algorithms to improve the defect reconstruction. Thermographic SR reconstruction methods involve measuring the temperature change in an object under test (OuT) heated with multiple different spatially structured illuminations. Subsequently, these measurements are inputted into a severely ill-posed and heavily regularized inverse problem, producing a sparse map of the OuT’s internal defect structure. Solving this inverse problem relies on limited priors, such as defect-sparsity, and iterative numerical minimization techniques. Previously mostly experimentally limited to one-dimensional regions of interest (ROIs), this thesis aims to extend the method to the reconstruction of two-dimensionalROIs with arbitrary defect distributions while maintaining reasonable experimental complexity. Ultimately, the goal of this thesis is to make the method suitable for a technology transfer to industrial applications by advancing its technology readiness level (TRL). In order to achieve the aforementioned goal, this thesis discusses the numerical expansion of a thermographic SR reconstruction method and introduces two novel algorithms to invert the underlying inverse problem. Furthermore, a forward solution to the inverse problem in terms of the applied SR reconstruction model is set up. In conjunction with an additionally proposed algorithm for the automated determination of a set of (optimal) regularization parameters, both create the possibility to conduct analytical simulations to characterize the influence of the experimental parameters on the achievable reconstruction quality. On the experimental side, the method is upgraded to deal with two-dimensional ROIs, and multiple measurement campaigns are performed to validate the proposed inversion algorithms, forward solution and two exemplary analytical studies. For the experimental implementation of the method, the use of a laser-coupled DLP-projector is introduced, which allows projecting binary pixel patterns that cover the whole ROI, reducing the number of necessary measurements per ROI significantly (up to 20x). Finally, the achieved reconstruction of the internal defect structure of a purpose-made OuT is qualitatively and qualitatively benchmarked against well-established thermographic testing methods based on homogeneous illumination of the ROI. Here, the background-noise-free two-dimensional photothermal SR reconstruction results show to outclass all defect reconstructions by the considered reference methods. N2 - Die laserbasierte aktive thermografische Prüfung als berührungslose Methode der zerstörungsfreien Werkstoffprüfung (NDT) basiert auf der aktiven Erwärmung des Testobjekts (OuT) und Messung des resultierenden Temperaturanstiegs mit einer Infrarotkamera. Dadurch bedingt können systematische Abweichungen vom vorhergesagten Erwärmungsverhalten Aufschluss über dessen innere Struktur geben. Jedoch ist das Auflösungsvermögen für innenliegende Defekte durch die diffusive Natur der Wärmeleitung in Festkörpern begrenzt. Thermografische Super-Resolution (SR)-Methoden zielen darauf ab, diese Limitation durch die Kombination mehrerer Messungen mit jeweils unterschiedlicher strukturierter Erwärmung und mathematischer Optimierungsmethoden zu überwinden. Zur Rekonstruktion innerer Defekte mithilfe thermografischer SR-Rekonstruktionsmethodik wird für die Gesamtheit mehrerer Messungen ein schlecht gestelltes und stark regularisiertes inverses mathematisches Problem gelöst, was in einer dünnbesetzten Karte der internen Defektstruktur des OuTs resultiert. Die Inversion mittels iterativer numerischer Minimierungsverfahren profitiert dabei von einzelnen Annahmen wie der vergleichsweisen Seltenheit von Materialdefekten. Nachdem die Methode bisher experimentell fast ausschließlich auf eindimensionale Messbereiche (ROIs) beschränkt war, zielt diese Arbeit auf eine Erweiterung zur Prüfung zweidimensionaler ROIs mit arbiträren Defektverteilungen bei erträglicher experimenteller Komplexität ab. Ziel ist es, durch die Weiterentwicklung des Technologie-Reifegrades (TRL) den Technologietransfer zur industriellen Anwendung zu ermöglichen. Hierzu werden erst die numerische Erweiterung der SR-Rekonstruktionsmethodik für zweidimensionale ROIs erörtert und zwei neue Algorithmen zur Invertierung des zugrunde liegenden inversen Problems vorgestellt, sowie eine Vorwärtslösung des inversen Problems entwickelt. In Verbindung mit einem neuartigen Algorithmus zur automatisierten Bestimmung der (optimalen) Regularisierungsparameter wird erstmals die Möglichkeit geschaffen, analytische Simulationen zum Einfluss einzelner Parameter auf die erreichbare Rekonstruktionsqualität durchzuführen. Weiterhin wird der experimentelle Ansatz zur Prüfung zweidimensionaler ROIs erweitert. Mehrere Messkampagnen validieren die eingeführten Inversionsalgorithmen, die Vorwärtslösung und zwei exemplarische analytische Studien. Für die experimentelle Umsetzung wird erstmals die Verwendung lasergekoppelter DLP-Technologie für die makroskopische thermografische Prüfung nutzbar gemacht, welche die Projektion großflächiger binärer Pixelmuster ermöglicht. Dadurch kann die Anzahl der erforderlichen Messungen pro ROI ohne Qualitätseinbußen erheblich reduziert werden (bis zu 20x). Abschließend werden die erzielten Rekonstruktionsergebnisse der internen Defektstruktur eines speziell angefertigten OuTs qualitativ und quantitativ mit auf homogener Erwärmung basierenden etablierten Methoden der thermografischen Prüfung verglichen. Hier zeigt sich, dass die weitgehend rauschfreien SR-Rekonstruktionsergebnisse alle Defektrekonstruktionen der betrachteten Referenzmethoden deutlich übertreffen. KW - Nondestructive testing KW - Zerstörungsfreie Prüfung KW - Thermography KW - Thermografie KW - Super resolution KW - Structured illumination KW - Strukturierte Beleuchtung KW - Defect characterization KW - Defektcharakterisierung KW - DMD KW - DLP PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-588296 DO - https://doi.org/10.14279/depositonce-19271 SP - 1 EP - 154 PB - Technische Universität Berlin CY - Berlin AN - OPUS4-58829 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Tschirschwitz, Rico A1 - Hahn, Sarah-K. A1 - Krause, Ulrich T1 - BEV Accidents - Consequences in Case of a Battery Thermal Runaway N2 - The number of cars which use a battery for propulsion, like BEV (battery electric vehicle) or PHEV (plug-in hybrid electric vehicle), is increasing. Following, the probability of these car types being involved in car accidents will increase. In a worst-case accident scenario, the installed batteries could go under thermal runaway (TR). A TR could be initiated by various causes, e.g., high temperatures from outside, mechanical damage of the cells/modules/batteries or internal and external short circuits. During such an event, large amounts of heat and toxic and/or flammable gases are released. This poses a great hazard to people and property in the immediate vicinity. The paper describes a large-scale test series on the lithium-ion battery TR consequences of automobile cells and modules up to E = 6.85 kWh. Near field temperatures of ΔT > 800°C in a distance of l = 2 m were measured. During an overcharge test, fragment throwing distances of l > 30 m were detected. Subsequent gas explosions of the released gases were documented. Hydrogen fluoride (HF) was measured in all tests, from cell to module. The highestmeasured concentration was cHF = 76 ppm, which is significantly higher than the 30-min-level for AEGL 2 (acute exposure guideline level 2). Based on the experimentally determined consequences, concrete measures for the accident analysis are subsequently drawn. T2 - 31st Annual Congress of the European Association for Accident Research and Analysis (EVU) CY - Limassol, Cyprus DA - 05.10.2023 KW - Gas release KW - Consequences KW - Lithium-ion battery KW - Electrical Energy Storage KW - BEV PY - 2023 SP - 1 EP - 18 AN - OPUS4-58552 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lohrke, Heiko A1 - Neumann, Patrick P. ED - Kossa, A. ED - Kiss, R. T1 - Robotic Measurement System Concept for Greenhouse Gas Tomography in Wastewater Treatment Plants N2 - This paper introduces a conceptual framework for a robotic greenhouse gas (GHG) measurement system designed for wastewater treatment plants (WWTPs). The emphasis is on accurate gas tomography measurement of emissions, crucial for national emission assessments. The proposed system is movable, semi-autonomous, and employs a combination of ground and air robots equipped with integral remote gas sensors and in-situ sensors. Employing a two/two configuration ensures comprehensive coverage of WWTPs, overcoming obstacles. The system concept lays the foundation for future implementation and evaluation, addressing the need for enhanced understanding of GHG emissions from WWTPs. T2 - 39th Danubia-Adria Symposium on Advances in Experimental Mechanics CY - Siófok, Hungary DA - 26.09.2023 KW - Remote Gas Sensing KW - Greenhouse Gas Emissions KW - Robot-based Emission Measurements KW - Semi-autonomous Sensor Networks KW - Gas Tomography PY - 2023 SN - 978-963-421-927-9 SP - 160 EP - 161 PB - Hungarian Scientific Society of Mechanical Engineering (GTE) CY - Siófok, Hungary AN - OPUS4-58880 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Häusler, F. A1 - Stührenberg, J. A1 - Smarsly, K. A1 - Neumann, Patrick P. T1 - Bout-based Gas Source Localization using Aerial Robot Swarms N2 - Gas source localization (GSL) helps mitigate the impact of industrial accidents and natural disasters. While GSL may be dangerous and time-consuming when performed by humans, swarms of agile and inexpensive nano aerial robots may increase the safety and efficiency of gas source localizations. Since the small payloads of nano aerial robots limit the sensing and computing resources, strategies adapted from biological swarms, such as colonies of social insects, are used to coordinate robot swarms. Most swarm GSL strategies are based on the assumption that the maxima of gas concentrations are sufficiently close to the gas sources. However, prior studies have indicated that the occurrence of “bouts”, a metric for the intermittency of gas distributions, may advantageously be used as a more accurate gas source proximity indicator. This paper presents a swarm GSL strategy employing bouts as source proximity indicators and a bio-inspired pheromone system for communication. Nano aerial robots, deployed in this study, act as agents and emit pheromone markers in an artificial environment upon detecting bouts. Leveraging the concept of artificial potential fields, the agents switch between exploiting the knowledge of the swarm by following pheromone gradients and exploring the search space by targeting a random point. The agents are repelled by each other and by walls to avoid collisions. The swarm GSL strategy is implemented into three nano aerial robots and validated in a real-world experiment in an indoor environment with a single gas source. The results indicate that the the swarm GSL strategy presented in this paper is capable of GSL in indoor environments and that the intermittency of gas distributions is a better source proximity indicator than the mean concentration. T2 - IEEE Sensors 2023 CY - Vienna, Austria DA - 29.10.2023 KW - Mobile robotic olfaction KW - Nano aerial robot KW - Gas source localization KW - Bouts KW - Distributed robotics PY - 2023 SN - 979-8-3503-0387-2 DO - https://doi.org/10.1109/sensors56945.2023.10325109 SP - 1 EP - 4 PB - IEEE AN - OPUS4-58778 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfender, Max T1 - Über Seilschwingungen an Freileitungen - Zusammenfassender Überblick T2 - 22. Tagung der Studiengesellschaft für Höchstspannungsanlagen CY - Berlin, Germany DA - 20.06.1950 KW - Freileitung KW - Höchstspannungsanlage KW - Seilschwingung PY - 1950 SP - 13 EP - 41 PB - Studiengesellschaft für Höchstspannungsanlagen CY - Berlin AN - OPUS4-58713 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ayerdi Gomez, A. A1 - Slachciak, Nadine A1 - Zubia Aranburu, J. A1 - Zabala, A. A1 - Aginagalde, A. A1 - Bonse, Jörn A1 - Spaltmann, Dirk T1 - Improvement of the tribological performance of titanium alloy using FS-laser-induced periodic surface structures in combination with ZDDP and ionic liquid lubricant additives N2 - The performance of titanium alloy (Ti6Al4V) surfaces was investigated in lubricated reciprocating sliding tribological tests (RSTT). Special emphasis was laid on the effect of surface nanostructures in area of contact on the respective friction and wear behaviour. These so-called laser-induced periodic surface structures (LIPSS, ripples) were produced on the titanium alloy surface upon scan processing in air by an ultrashort pulsed femtosecond (fs) laser. As lubricant served two types of base oils, a pure polyalcylene-glycol, and an SAE 0W30 oil containing only antioxidants and temperature stabilizers. Tribological tests were carried out on polished as well as LIPSS covered areas using both types of base oil. A test metrics was established, combining the additive 2-ethylhexyl-zincdithiophosphate (ZDDP) or the ionic liquid [P6,6,6,14] [DEHP] (98% purity) with the respective base oils. The test metrics also considered the orientation of motion with respect to the orientation of the structures formed on the surface. Results are presented which show that the interplay between LIPSS and the local chemistry formed by the respective additives is beneficial for the tribological behaviour of the titanium alloy. Certain combinations of base oil, additive and LIPSS reduced friction and wear significantly in the tribological contact. T2 - 64. Tribologie-Fachtagung CY - Göttingen, Germany DA - 25.09.2023 KW - TiAl64V KW - 100Cr6 KW - Friction KW - Wear KW - LIPSS KW - Lubrication KW - PAG KW - Ionic liquid PY - 2023 SP - 1 EP - 5 AN - OPUS4-58642 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simon, Franz-Georg A1 - Frieling, Sophie T1 - Sorptionsverhalten von Antimon an Eisenoxidverbindungen N2 - Aschen und Schlacken aus der thermischen Abfallbehandlung enthalten eine Vielzahl von Schwermetallverbindungen. Für Antimon, Chrom, Kupfer, Molybdän und Vanadium werden in der neuen Ersatzbaustoffverordnung (Bundesregierung, 2021) Eluatgrenzwerte für die Verwertung festgelegt. Aschen und Schlacken werden aus der Abfallverbrennungsanlage nass ausgetragen und vor einer Verwertung in der Regel mehrere Wochen gelagert. Dabei finden hydraulische Reaktionen statt und enthaltenes CaO wird zu einem Großteil in Calciumcarbonat umgewandelt. Während wässrige Eluate von frischen Aschen pH-Werte von 12 und höher aufweisen, sind die Eluate nach einigen Wochen weniger stark alkalisch. Die gemessenen Schwermetallkonzentrationen sind daher dann auch deutlich niedriger, mit Ausnahme von Antimon (Sb) und Vanadium (V). Hier steigen die Konzentration mit der Lagerungsdauer. Grund sind sinkende Konzentrationen von Ca-Ionen, die sonst zu einer Ausfällung von Antimonaten und Vanadaten führen. Zu hohe Eluatwerte von Sb und V können jedoch durch Sorption an Eisenoxidverbindungen gemindert werden. Dazu wurden Sorptionsexperimente mit verschiedenen Eisenoxidverbindungen durchgeführt. T2 - 5. Internationales Bergbausymposium WISSYM 2023 CY - Dresden, Germany DA - 25.09.2023 KW - Rostasche KW - Sorption KW - Ersatzbaustoff PY - 2023 UR - https://www.wismut.de/de/download.php?download=Wi_WISSYM2023_Abstracts_END_klein.pdf SP - 247 EP - 250 AN - OPUS4-58701 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meng, Xiangmeng A1 - Putra, Stephen Nugraha A1 - Bachmann, Marcel A1 - Rethmier, Michael T1 - Influence of the spatial laser energy absorption on the molten pool dynamics in high-power laser beam welding N2 - The spatial laser energy absorption inside the keyhole is decisive for the dynamic molten pool behaviors and the resultant weld properties in high-power laser beam welding (LBW). In this paper, a numerical simulation of the LBW process, considering the 3D transient heat transfer, fluid flow, and keyhole dynamics, is implemented, in which the free surface is tracked by the volume-of-fluid algorithm. The underlying laser-material interactions i.e., the multiple reflections and Fresnel absorption, are considered by an advanced ray-tracing method based on a localized Level-Set strategy and a temperature-dependent absorption coefficient. The laser energy absorption is analyzed from a time-averaged point of view for a better statistical representation. It is found for the first time that a noticeable drop of the time-averaged laser energy absorption occurs at the focus position of the laser beam, and the rest region of the keyhole has relatively homogenous absorbed energy. This unique absorption pattern may lead to a certain keyhole instability and have a strong correlation with the detrimental bulging and narrowing phenomena in the molten pool. The influence of the different focus positions of the laser beam on the keyhole dynamics and molten pool profile is also analyzed and compared. The obtained numerical results are compared with experimental measurements to assure the validity of the proposed model. T2 - International Congress of Applications of Lasers & Electro-Optics 2023 CY - Chicago, USA DA - 16.10.2023 KW - Laser beam welding KW - laser energy absorption KW - molten pool KW - keyhole dynamics KW - numerical modeling PY - 2023 SP - 1 EP - 8 AN - OPUS4-58754 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Epperlein, Martin A1 - Hilgenberg, Kai A1 - Hellfritz, Benjamin A1 - Löffler, Frank T1 - Digitisation of the quality infrastructure - using the example of additive manufacturing N2 - Rapidly advancing technologies and progressive digitisation are posing challenges to the established quality infrastructure (QI). In response, the key stakeholders of the German QI established the initiative QI-Digital aimed at developing new solutions for modern quality assurance. One of the central use cases herein is quality assurance for additive manufacturing, in which a fully interlinked additive manufacturing process chain is established. The intention is to collect and process data from each production step, allowing for a comprehensive digital view of the physical material flow. Within this process chain, prototypes of digital QI tools like machine readable standards and digital quality certificates are being demonstrated, tested, and evolved. This is complemented by research on the process level, comprising the evaluation and refinement of methods for in-situ and ex-situ quality assurance, as well as algorithms for registration, reduction, and analysis of process data. This paper presents the status, goals, and vision for the QI-Digital use case additive manufacturing. T2 - Metal Additive Manufacturing Conference 2023 CY - Wien, Austria DA - 17.10.2023 KW - Additive Manufacturing KW - Digitalisation KW - Quality Assurance PY - 2023 SP - 96 EP - 104 CY - Wien AN - OPUS4-58628 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tschirschwitz, Rico A1 - Hahn, Sarah-K. A1 - Saupe, Alexander A1 - Janßen, Marvin A1 - Krause, Ulrich T1 - Sicherheitsrisiko Batterien – Demonstrator aus dem Projekt SEE-2L bereits im Einsatz N2 - Der Beitrag beschreibt das BMBF-Verbundvorhaben SEE-2L. Im Artikel werden die wesentlichen Meilensteine des Projektes vorgestellt. Ebenso werden die wichtigsten im Projekt erzielten Ergebnisse aufgeführt und verlinkt. KW - Stationäre Energiespeicher KW - Batterie KW - Auswirkungsbetrachtungen KW - EES KW - Elektrische Energiespeicher PY - 2023 UR - https://info.sifo.de/public/a_25436_GZ5jd/file/data/669_Informationsbrief_zur_zivilen_Sicherheitsforschung_07-2023.pdf#page=7 IS - 7 SP - 7 EP - 9 PB - Bundesministerium für Bildung und Forschung (BMBF) CY - Bonn AN - OPUS4-58347 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erning, Johann Wilhelm T1 - “Grabenkorrosion": How scientific debate leads to an solution. and modern failures due to neglection of well described facts N2 - In the late 1980s, a new type of corrosion appeared in drinking water installations where galvanized steel pipes failed forming a deep groove with no corrosion at the other surfaces. The reason was discussed quite fiercely between failure analysts and material suppliers. In the end the discussion lead to the solution: inductive welded pipes of a certain sulphur content were prone to selective corrosion. The history of the arguments is discussed using old communications between Wilhelm Schwenk and Wolfgang Stichel, who later published the results in a paper unfortunately only I german. Thus the knowledge got lost and new cases based on the same material problems are observed in application of so-called C-Steel piping systems. Failure cases are shown. T2 - MTech 2023 CY - Cavtat, Croatia DA - 02.10.2023 KW - Corrosion KW - Grabenkorrosion PY - 2023 SN - 2806-8769 SP - 1 EP - 6 PB - Croatian Society for Heat Treatment and Sufrace Engineering CY - Zagreb AN - OPUS4-58521 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Mike A1 - Völzke, Holger A1 - Zencker, Uwe A1 - Herz, A. A1 - Kreienmeyer, M. T1 - Design of a Drop Test Target with Reproducible Properties for Konrad Prototype Testing N2 - Beginning in 1976 the former iron ore mine Konrad was geologically investigated concerning its suitability as a location for a German final repository for low and intermediate level waste. After a comprehensive licensing procedure it was approved and is now being prepared and equipped for the planned start of storage in 2027. At the end of the 1980s, the requirements for waste containers for storage in this repository were defined for the first time on the basis of an incident analysis of the on-site handling procedures, beginning with the unloading of the packages after the arrival at the site up to the final positioning in the underground storage galleries. A 5-meter drop onto the rock ground of the mine was identified as the covering case for high mechanical requirements (ABK II container class). In contrast to the 9-meter drop according to the IAEA Regulations for the Safe Transport of Radioactive Material, the 5-meter drop is performed onto a hard but not essentially unyielding target. The container is typically not protected by an impact limiter. The requirements for a potential test facility are described in the regulations for the Konrad repository. The mechanical strength of the target is defined as a concrete strength equivalent to the identified properties of the rock ground of the mine. Since 1991 BAM has consistently used precast reinforced concrete slabs as target for drop tests in the framework of licensing procedures as well as in research projects. While the original design fulfilled the requirement for the integrity of the concrete slab in most cases, it failed when drop tests onto an edge of a container were performed. A redesigned concrete slab developed in a research project and suggested as a reference target in 2009 has been successfully used in Konrad licensing procedures since then. The paper gives a brief overview of the historical development and it describes BAM’s efforts and approaches to continuously guarantee a concrete slab of defined quality and to provide a test setup for valid drop tests from the applicants and the authorities view. T2 - PATRAM 2022, 20th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Juan-les-Pins, France DA - 11.06.2023 KW - Target KW - Drop test KW - Final repository Konrad PY - 2023 SP - 1 EP - 11 AN - OPUS4-58563 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Brierley, N. A1 - Casperson, Ralf A1 - Engert, D. A1 - Heilmann, S. A1 - Herold, F. A1 - Hofmann, D. A1 - Küchler, H. A1 - Leinenbach, F. A1 - Lorenz, S. A1 - Martin, J. A1 - Rehbein, J. A1 - Sprau, B. A1 - Suppes, A. A1 - Vrana, J. A1 - Wild, E. T1 - DICONDE in industrial inspection N2 - DICONDE (Digital Imaging and Communication in Non-Destructive Testing) is an open international standard for storing and exchanging industrial test data and process-related information. The DICONDE standard defines both the semantics for structured storage of data and the network-based communication between two endpoints. This allows many test processes to be mapped digitally and securely, while at the same time meeting normative requirements such as traceability to the tester and test object and reproducibility of test results. KW - DICONDE KW - NDT KW - Interoperability KW - Data storage KW - Communication PY - 2023 SN - 978-3-947971-32-9 N1 - Es gibt eine parallele Sprachausgabe (deutsch), ein Link befindet sich im Feld zugehöriger Identifikator - There is a parallel language edition (German), a link is in the field related identifier VL - Specification ZfP 4.0-01E SP - 1 EP - 13 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin ET - Edition August 2023 AN - OPUS4-58576 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Casperson, Ralf A1 - Engert, D. A1 - Heilmann, S. A1 - Herold, F. A1 - Hofmann, D. A1 - Küchler, H. A1 - Leinenbach, F. A1 - Lorenz, S. A1 - Martin, J. A1 - Rehbein, J. A1 - Sprau, B. A1 - Suppes, A. A1 - Vrana, J. A1 - Wild, E. T1 - DICONDE in der ZfP N2 - DICONDE (Digital Imaging and Communication in Non-Destructive Evaluation) ist ein offener internationaler Standard zur Speicherung und zum Austausch industrieller Prüfdaten und prozessbezogener Informationen. Der DICONDE-Standard definiert sowohl die Semantik für eine strukturierte Speicherung von Daten als auch die netzwerkbasierte Kommunikation zwischen zwei Endpunkten. Damit lassen sich viele Vorgänge von Prüfprozessen digital und sicher abbilden und gleichzeitig normative Anforderungen wie eine Rückführbarkeit zum Prüfer und Prüfobjekt sowie eine Reproduzierbarkeit von Prüfergebnissen erfüllen. KW - DICONDE KW - ZfP KW - Interoperabilität KW - Datenspeicherung KW - Kommunikation PY - 2023 SN - 978-3-947971-30-5 N1 - Es gibt eine parallele Sprachausgabe (englisch), ein Link befindet sich im Feld zugehöriger Identifikator - There is a parallel language edition (English), a link is in the field related identifier VL - Merkblatt ZfP 4.0-01 SP - 1 EP - 13 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin ET - Ausgabe Juni 2023 AN - OPUS4-58578 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scheuschner, Nils A1 - Heinrichsdorff, F. A1 - Oster, Simon A1 - Uhlmann, E. A1 - Polte, J. A1 - Gordei, A. A1 - Hilgenberg, Kai T1 - In-situ monitoring of the laser powder bed fusion process by thermography, optical tomography and melt pool monitoring for defect detection N2 - For the wide acceptance of the use of additive manufacturing (AM), it is required to provide reliable testing methods to ensure the safety of the additively manufactured parts. A possible solution could be the deployment of in-situ monitoring during the build process. However, for laser powder bed fusion using metal powders (PBF-LB/M) only a few in-situ monitoring techniques are commercially available (optical tomography, melt pool monitoring), which have not been researched to an extent that allows to guarantee the adherence to strict quality and safety standards. In this contribution, we present results of a study of PBF-LB/M printed parts made of the nickel-based superalloy Haynes 282. The formation of defects was provoked by local variations of the process parameters and monitored by thermography, optical tomography and melt pool monitoring. Afterwards, the defects were characterized by computed tomography (CT) to identify the detection limits of the used in-situ techniques. T2 - Lasers in Manufacturing Conference 2023 CY - Munich, Germany DA - 26.06.2023 KW - Thermography KW - Optical tomography KW - Melt-pool-monitoring KW - Laser powder bed fusion KW - Haynes 282 KW - Additive Manufacturing PY - 2023 UR - https://www.wlt.de/lim2023-proceedings/system-engineering-and-process-control SP - 1 EP - 10 AN - OPUS4-58466 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ghafafian, Carineh A1 - Trappe, Volker ED - Vassilopoulos, A. P. ED - Michaud, V. T1 - Fully-reversed fatigue behavior of scarf joint repairs for wind turbine blade shell applications N2 - To enable a quick and cost-effective return to service for wind turbine blades, localized repairs can be executed by technicians in the field. Scarf repairs, shown to be highly efficient with a smooth load transition across angled joint walls and a restored aerodynamic profile, are the focus of this work. The failure mechanisms of these structures were examined under quasi-static tensile and fully-reversed cyclic loading. While the scarf ratio was held constant at 1:50, the repair layup was varied between large-to-small and small-to-large. The effect of the presence of resin pockets and the fiber orientation mismatch between parent and repair material on the restored strength of BIAX ±45° glass fiber reinforced polymer scarf joint structures was studied. T2 - 20th European Conference on Composite Materials CY - Lausanne, Switzerland DA - 26.06.2022 KW - Fatigue KW - Scarf repairs KW - Glass fiber reinforced polymers PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-569646 UR - https://infoscience.epfl.ch/record/298799 SN - 978-2-9701614-0-0 VL - Vol. 5 - Applications and structures SP - 195 EP - 201 PB - Composite Construction Laboratory (CCLab) CY - Lausanne AN - OPUS4-56964 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Schaumann, P. A1 - Hothan, Sascha A1 - Mund, M. A1 - Häßler, Dustin A1 - Schartel, Bernhard A1 - Daus, Lars-Hendrik T1 - Bewertung des Feuerwiderstandes von Stahlkonstruktionen mit reaktiven Brandschutzsystemen unter Berücksichtigung des Alterungsverhaltens N2 - Im Rahmen des Forschungsprojektes IGF 20470N wurden Untersuchungen zum Alterungsverhalten von reaktiven Brandschutzsystemen (RBS) auf Stahlbauteilen durchgeführt. Mithilfe der Ergebnisse einer umfangreichen Literaturrecherche sowie experimentellen und numerischen Untersuchungen sollte ein Vorschlag für ein Prüfkonzept zum Nachweis einer Nutzungsdauer von RBS von mehr als 10 Jahren auf Basis von Kurzzeitversuchen abgeleitet werden. Dabei setzt die Bewertung des Alterungsverhaltens von RBS voraus, dass die Mechanismen der Alterung hinreichend bekannt sind. Dafür wurden zunächst systematisch Daten von Kurz- und Langzeitversuchen von nationalen Zulassungsprüfungen der letzten Jahrzehnte ausgewertet. Anschließend wurden umfangreiche experimentelle Untersuchungen an einer wasserbasierten sowie einer epoxidharzbasierten Richtrezeptur durchgeführt. Da aus der Literatur bekannt ist, dass die Einflüsse der Bewitterung zu einer Veränderung der Konzentration der Bestandteile innerhalb der Beschichtung führen können, wurden Untersuchungen mit Mangelrezepturen durchgeführt, wobei systematisch einzelne Bestandteile reduziert wurden. Neben optischen Untersuchungen wurden thermoanalytische Verfahren (DSC-TG-, ATR-FTIR-, Elementar-, Farbanalyse) angewandt sowie Brandversuche an beschichteten Stahlplatten durchgeführt. Des Weiteren wurden die Richtrezepturen den beschleunigten Kurzzeitversuchen gemäß EAD 350402-00-1106 (2017) unterzogen, welche die Zulassung von Produkten auf europäischer Ebene regelt. Für die wasserbasierte Richtrezeptur wurden die Bewitterung für den feuchten Innenraum (Typ Z1) mehrfach wiederholt (1x, 3x, 6x). Für die epoxidharzbasierte Richtrezeptur entsprach die Bewitterung dem Zyklus für die Außenanwendung (Typ X). In Brandversuchen sowie thermoanalytischen und optischen Untersuchungen wurde das Alterungsverhalten sowie die thermische Schutzwirkung analysiert. Anschließend wurden numerische Simulationen von Stahlbauteilen mit gealterten RBS durchgeführt und anhand der experimentellen Untersuchungen validiert. Mithilfe der numerischen Modelle kann eine Bewertung der thermischen Schutzwirkung von Stahlbauteilen mit gealterten RBS vorgenommen werden. Mithilfe der gesammelten Erkenntnisse wurde ein Vorschlag für ein Prüfkonzept für den Nachweis einer Nutzungsdauer von mehr als 10 Jahren abgeleitet. Das Prüfkonzept besteht dabei aus einem Katalog von Möglichkeiten, die aktuellen Zulassungsprüfungen auf europäischer Ebene für eine Nutzungsdauer von 10 Jahren auf einen längeren Zeitraum zu erweitern. N2 - Within the scope of the research project IGF 20470N, investigations were carried out on the assessment of the aging behavior of intumescent coatings (ICs) for the fire protection of steel members. With the help of the results of an extensive literature research as well as experimental and numerical investigations, a proposal for a test concept for the proof of a service life of ICs of more than 10 years was to be derived on the basis of short-term tests. The evaluation of the aging behavior of ICs presupposes that the aging mechanisms are sufficiently known. For this purpose, data from short- and long-term tests of national approval tests of the last decades were first systematically evaluated. Subsequently, extensive experimental investigations were carried out on a water-based and epoxy resin-based model formulation. Since it is known from the literature that the effects of weathering may lead to a change in the concentrations of the constituents within the coating, investigations were carried out with formulations of the ICs in which individual constituents were systematically reduced. In addition to optical investigations, thermoanalytical methods (DSC-TG-, ATR-FTIR-, elemental-, color analysis) were used and fire tests were carried out on coated steel plates. Furthermore, the model formulations were subjected to the accelerated short-term tests of EAD 350402-00-1106 (2017), which regulates the approval of products at the European level. For the water-based model formulation, the weathering for the interior application with a high moisture content (type Z1) was repeated several times (1x, 3x, 6x). For the epoxy resin-based model formulation, the weathering corresponded to the cycle for exterior application (type X). Fire tests as well as thermoanalytical and optical investigations were carried out to analyze the aging behavior and the thermal protection performance. Subsequently, numerical simulations of steel members with aged ICs were carried out and validated on the basis of the experimental investigations. With the help of the numerical models, an evaluation of the thermal protection performance of steel members with aged ICs can be carried out. Bases on the findings, a proposal for a test concept for the verification of a service life of more than 10 years was derived. The test concept consists of a catalogue of possibilities for extending the current approval tests at European level for a service life of 10 years to a longer period. KW - Brandschutz KW - Dauerhaftigkeit KW - Alterung KW - Reaktive Brandschutzsysteme KW - Brandversuche PY - 2022 UR - https://dast.deutscherstahlbau.de/veroeffentlichungen/forschungsberichte SP - 1 EP - 367 PB - Stahlbau Verlags- und Service GmbH CY - Düsseldorf AN - OPUS4-57257 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schnur, C. A1 - Moll, J. A1 - Lugovtsova, Yevgeniya A1 - Schütze, A. A1 - Schneider, T. ED - Kundu, T. ED - Reis, H. ED - Ihn, J.-B. ED - Dzenis, Y. T1 - Explainable Machine Learning for Damage Detection: in Carbon Fiber Composite Plates Under Varying Temperature Conditions N2 - Understanding on how a machine learning model interprets data is a crucial step to verify its reliability and avoid overfitting. While the focus of the scientific community is nowadays orientated towards deep learning approaches, which are considered as black box approaches, this work presents a toolbox that is based on complementary methods of feature extraction and selection, where the classification decisions of the model are transparent and can be physically interpreted. On the example of guided wave benchmark data from the open guided waves platform, where delamination defects were simulated at multiple positions on a carbon fiber reinforced plastic plate under varying temperature conditions, the authors could identify suitable frequencies for further investigations and experiments. Furthermore, the authors presented a realistic validation scenario which ensures that the machine learning model learns global damage characteristics rather than position specific characteristics. T2 - 2021 48th Annual Review of Progress in Quantitative Nondestructive Evaluation CY - Online meeting DA - 28.07.2021 KW - Explainable machine learning KW - Guided waves KW - Damage detection KW - Structural health monitoring KW - Composite structures PY - 2021 SN - 978-0-7918-8552-9 DO - https://doi.org/10.1115/QNDE2021-75215 VL - QNDE2021-75215 SP - 1 EP - 6 PB - The American Society of Mechanical Engineers (ASME) CY - New York, USA AN - OPUS4-56723 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Melzer, Michael T1 - Taxonomie magnetischer Maßverkörperungen N2 - Darstellung der Taxonomie magnetischer Maßverkörperungen im Zusammenhang mit der DIN SPEC 91411 "Anforderungen an die technische Darstellung von magnetischen Maßverkörperungen in Konstruktionszeichnungen" KW - Magnetische Maßverkörperungen KW - Magnetische Messysteme KW - Taxonomie PY - 2022 UR - https://innomag.org/wp-content/uploads/2021/10/DIN-SPEC-Poster_final.pdf SP - 1 EP - 1 PB - Innovationsplattform Magnetische Mikrosysteme INNOMAG CY - Kaiserslautern AN - OPUS4-56633 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Völker, Christoph A1 - Moreno Torres, Benjami T1 - SLAMD-FIB-Case-Study N2 - With 8% of man-made CO2 emissions, cement production is an important driver of the climate crisis. By using alkali-activated binders part of the energy-intensive clinker production process can be dispensed with. However, because numerous chemicals are involved in the manufacturing process here, the complexity of the materials increases by orders of magnitude. Finding a properly balanced cement formulation is like looking for a needle in a haystack. We have shown for the first time that artificial intelligence (AI)-based optimization of cement formulations can significantly accelerate research. The „Sequential Learning App for Materials Discovery“ (SLAMD) aims to accelerate practice transfer. With SLAMD, materials scientists have low-threshold access to AI through interactive and intuitive user interfaces. The value added by AI can be determined directly. For example, the CO2 emissions saved per ton of cement can be determined for each development cycle: the more efficient the AI optimization, the greater the savings. Our material database already includes more than 120,000 data points of alternative cements and is constantly being expanded with new parameters. We are currently driving the enrichment of the data with a life cycle analysis of the building materials. Based on a case study we show how intuitive access to AI can drive the adoption of techniques that make a real contribution to the development of resource-efficient and sustainable building materials of the future and make it easy to identify when classical experiments are more efficient. KW - Alkali activated concrete KW - Concrete PY - 2022 UR - https://github.com/BAMcvoelker/SLAMD-FIB-Case-Study#slamd-fib-case-study PB - GitHub CY - San Francisco, CA, USA AN - OPUS4-56637 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Trappe, Volker A1 - Sachs, Patrick ED - Vassilopoulos, A. P. ED - Michaud, V. T1 - Dynamic mechanical analysis of epoxy-matrix cross linking measured in-situ using an elastomer container N2 - A new patented dynamic mechanical analysis (DMA) is presented, where the tensile, bending- or torsional stiffness of a media can be characterized in-situ during the phase transition from liquid to solid. An epoxy system, e.g. Hexion L285/H287, is filled into an elastomer container, such as a silicone tube. This can be mounted into a conventional OMA and, based on a linear viscoelastic approach, the storage modulus (E';G'), the loss modulus (E'';G'') and the loss angle tan(δ) can be measured at constant temperature as a function of time in order to investigate the liquid to sol-gel to solid transition. With this new method, the stiffness increase as a result of the cure process can be directly measured more precisely than with a rheometer in a shear plate set-up, because using an elastomer container gives a defined cross section for calculating the Young's modulus. T2 - 20th European Conference on Composite Materials CY - Lausanne, Switzerland DA - 26.06.2022 KW - Cross linking KW - Dynamic mechanical analysis (DMA) KW - Thermoset polymers KW - Cure process PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-569651 UR - https://infoscience.epfl.ch/record/298799 SN - 978-2-9701614-0-0 VL - Vol. 5 - Applications and structures SP - 181 EP - 186 PB - Composite Construction Laboratory (CCLab) CY - Lausanne AN - OPUS4-56965 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Johann, Sergej A1 - Winkler, Nicolas P. A1 - Bartholmai, Matthias ED - Kourkoulis, S. K. T1 - Multi-sensor system for long-term monitoring with WiFi and LoRaWAN technology N2 - In many cases, science falls back on self-developed prototype systems, which are used and developed for the measurement and execution of the tasks. About 80 % of the development is based on the same hardware design, which is used in only one application scenario and then discarded. For the most part, there are also uncalibrated sensors, since it is costly to calibrate a complicated sensor measurement system or the entire measurement chain since access to the sensor systems is not always available. This paper describes a conceptual design to implement a versatile sensor system with the motivation to fuse the data recording and data reception, which can cover large areas with the help of LoRaWAN (Long Range Wide Area Network) technology. To overcome disadvantages of LoRaWAN, namely the slow data rates, the proposed sensor system can also cover smaller areas with the widespread WiFi technology. An enormous advantage over individual complete systems in the form of a prototype, is the rapid expansion, uncomplicated calibration of the individual sensors and the ecological relief. A modular design is used, where individual stacks with sensors and peripherals can be added separately. The stacks are standalone low-power systems and can be calibrated, maintained, and replaced separately and do not require the entire measurement chain. The measured and sent values are stored locally on the main stack and sent to the data collector (gateway) and evaluated by means of the automated selection between WiFi and LoRaWAN. T2 - 38th Danubia-Adria Symposium on Advances in Experimental Mechanics CY - Athens, Greece DA - 20.09.2022 KW - Multisensor system KW - LoRaWAN KW - WiFi KW - Long term monitoring PY - 2022 SP - 1 EP - 2 AN - OPUS4-56462 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bachmann, Marcel A1 - Meng, Xiangmeng A1 - Artinov, Antoni A1 - Rethmeier, Michael T1 - Evaluation of narrowed weld pool shapes and their effect on resulting potential defects during deep penetration laser beam welding N2 - This study presents mechanisms of the evolution of a narrowed region in the weld pool center during deep penetration laser beam welding. In numerous numerical studies presented in this study, it was also found that the local reduction of the weld pool size can cause detrimental effects on the melt flow behavior and the resulting properties of the welds. A particularly large influence of this effect was identified in three aspects. Firstly, the local variation of the solidification sequence of the weld pool causes an increase in the hot-cracking susceptibility due to a locally delayed solidification. Secondly, it was proven that a change in the local length and width of the weld pool is associated with an adverse impact on the potential flow routes of the molten material that induces stronger local variations of its solidification. Thus, the element mixing, e.g. during the welding with filler materials, is blocked. This leads to a non-homogeneous chemical composition of the final weld and can cause undesired effects on the final material properties. Finally, another observed effect is related to the reduced ability of process pores to reach the top surface. As this type of porosity is usually produced around the keyhole tip, the change of the fluid flow regime above this area plays a significant role in determining the final path of the pores until the premature solidification in the middle of the weld pool captures them. This study summarizes mainly numerical results which were supported by selected experimental validation results. T2 - International Congress of Applications of Lasers & Electro-Optics 2022 CY - Orlando, FL, USA DA - 17.10.2022 KW - Weld pool shape KW - Laser beam welding KW - Solidification KW - Porosity KW - Numerical process simulation PY - 2022 SP - 1 AN - OPUS4-56532 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bulling, Jannis A1 - Jurgelucks, B. A1 - Prager, Jens A1 - Walther, A. T1 - Defect Characterization in Plate Models Facilitated by Algorithmic Differentiation N2 - In non-destructive testing and structural health monitoring with ultrasonic waves, the quantification of damage in components is one of the main tasks. In many shell-like structures, such as plates, pipes, or laminate components, ultrasonic waves propagate as guided waves. Although guided waves enable the testing of large areas, their multimodal and dispersive properties make it challenging to analyze signals. So, there is a need for more advanced algorithms to handle these properties, especially when reconstructing damage position and geometry. The reconstruction can be formulated as an inverse problem where the measured signals are fitted with a simulative forward model. Due to the small wavelength of ultrasonic waves, classic forward models based on, e.g., the Finite Element Method are computationally intensive. In contrast, the authors use the semi-analytical Scaled Boundary Finite Element Method (SBFEM) to reduce the computational effort. The SBFEM approximates arbitrary long, undamaged parts of the structure with only a few degrees of freedom. This contribution summarizes a general inverse procedure based on algorithmic differentiation in combination with the SBFEM. Results are presented for damaged 2D cross-sectional models of waveguides. These results include an analysis of the robustness of the proposed algorithms against noise. T2 - DAGA 22 CY - Stuttgart, Germany DA - 21.03.2022 KW - Structural health monitoring KW - Inverse Methods KW - SBFEM KW - Algorithmic Differentiation KW - Non-destructive testing PY - 2022 VL - 2022 SP - 871 EP - 874 AN - OPUS4-56547 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Memmolo, V. A1 - Lugovtsova, Yevgeniya A1 - Olino, M. A1 - Prager, Jens ED - Kundu, T. ED - Reis, H. ED - Ihn, J.-B. T1 - Application of Temperature Compensation Strategies for Ultrasonic Guided Waves to Distributed Sensor Networks N2 - Temperature compensation strategies play a key role in the implementation of guided wave based structural health monitoring approaches. The varying temperature influences the performance of the inspection system inducing false alarms or missed detection, with a consequent reduction of reliability. This paper quantitatively assesses two temperature compensation methods, namely the optimal baseline selection (OBS) and the baseline signal stretch (BSS), with the aim to extend their use to the case of distributed sensor networks (DSN). The effect of temperature separation between baseline time-traces in OBS and BSS are investigated considering multiple couples of sensors employed in the DSN. A decision strategy that uses frequent value warning to define the optimal baseline or stretching parameter is found to be effective analyzing data from two several experiments, which use different frequency analysis with either predominantly A0 mode or S0 mode data or both. The focus is given on the fact that different paths are available in a sensor network and several possible combinations of results are available. Nonetheless, introducing a frequent value warning it is possible to increase the efficiency of the OBS and BSS approach making use of fewer signal processing algorithms. In addition, the effectiveness of those approach is quantified using damage indicators as metric, which confirms that the performance of OBS and BSS quantitatively agree with predictions and also demonstrate that the use of compensation strategies improve detectability of damage with a higher reliability of the system. T2 - 2022 49th Annual Review of Progress in Quantitative Nondestructive Evaluation (QNDE 2022) CY - San Diego, CA, USA DA - 25.07.2022 KW - Ultrasound KW - Elastic waves KW - Structural Health Monitoring KW - Environmental Effects KW - Damage Detection PY - 2022 SN - 978-0-7918-8659-5 DO - https://doi.org/10.1115/QNDE2022-98534 SP - 1 PB - The American Society of Mechanical Engineers (ASME) CY - 2 Park Avenue, New York, NY 10016, USA AN - OPUS4-57074 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kühne, Hans-Carsten A1 - Hüsken, Götz A1 - Mundra, Shishir A1 - Sander, C. A1 - Obermann, S. T1 - Die Betondickglasfenster des Glockenturms am Eiermannbau der Kaiser-Wilhelm-Gedächtniskirche N2 - Die Kaiser-Wilhelm-Gedächtniskirche (KWG) gilt als eine der wichtigsten Sehenswürdigkeiten Berlins in der City West und als ein herausragendes Beispiel für die „Dalle de Verre“ Verglasungen in sakralen Gebäuden. Der vorliegende Beitrag widmet sich der Fassade und den Glasfenstern des neuen Glockenturms, wobei die beschriebenen Szenarien aufgrund der annähernd gleichen Bauweise der restlichen neuen Baukörper in weiten Teilen starke Analogien aufweisen und insofern übertragbar sind. T2 - Workshop Kulturguterhaltung - Vom Dampfkessel zu Nanomaterialien CY - Berlin, Germany DA - 17.11.2021 KW - Kaiser-Wilhelm-Gedächtniskirche KW - Betondickglasfenster KW - Instandsetzung KW - Elektrochemische Realkalisierung PY - 2021 VL - 3 SP - 125 EP - 140 PB - Druckerei G. Bohm CY - Berlin AN - OPUS4-57092 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lozano, Daniel A1 - Bulling, Jannis A1 - Prager, Jens T1 - Quadtree decomposition as a meshing strategy for guided waves simulations using the scaled boundary finite element method N2 - Structural health monitoring techniques associate strongly with damage detection and characterization. Ultrasonic guided waves (UGW), for such scope, arise as one of the most promising methods for many reasons i.e. UGW are able to travel long distances and they have high sensitivity to damage. In this context, the necessity to model realistic wave-defect interaction occurs to be critical. Realistic damage scenarios can be modeled through the usage of image-based quadtree meshes. Images, such as the outcome from X-ray scans, C-scans, etc., can be converted into meshes for further integration in a computational domain. Quadtree meshes are created by converting the intensity of the pixels to quadrilateral cells. Homogeneous regions inside one image result in one quad, whereas fine features such as discontinuities can be described with smaller quads. This contribution proposes an efficient methodology to model wave defect interaction, using as a framework the scaled boundary finite element method (SBFEM) and quadtree meshes. Problems as non-conforming regions in the mesh due to the space tree decomposition can be easily avoided using SBFEM’s polygonal elements. Moreover, the semi-analytical nature of the SBFEM allows the modeling of arbitrarily long prismatic/undamaged regions of the waveguides without an increase in the computational burden. T2 - DAGA 2022 CY - Stuttgart, Germany DA - 21.03.2022 KW - Wave defect interaction KW - Scaled Boundary Finite Element Method KW - Quadtree meshes KW - Image-based models KW - Transient analysis PY - 2022 SP - 887 EP - 890 CY - Stuttgart AN - OPUS4-57153 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Wulfes, Birte S. T1 - Rekombinante Herstellung und explorative Anwendung immobilisierter, thermostabiler Trypsin-Varianten für die Bottom-Up-Proteomik N2 - Die Erforschung des Proteoms, der Gesamtheit der Proteine eines Lebewesens, ist von großer Bedeutung für das Verständnis biologischer Systeme. Aufgrund dessen ist die Proteomik ist eines der bedeutendsten aktuellen Forschungsfelder der Biowissenschaften. In der Bottom-Up-Proteomik werden die Proteine einer Probe vor ihrer Analyse einem enzymatischen Verdau mit Proteasen unterzogen, was eine erleichterte Analyse mit hohem Durchsatz ermöglicht. Aufgrund seiner hohen Aktivität und Effektivität hat sich die Serinprotease Trypsin als Standard-Enzym der Proteomik etabliert. Die weitere Verbesserung ihrer Enzymcharakteristika, wie Thermostabilität und Aktivität, ist unter anderem durch Immobilisierung an ein Trägermaterial oder genetische Modifikation möglich. In der vorliegenden Arbeit wurde eine von Xiao et al. 2023 entwickelte thermostabile Trypsin-Variante mit erhöhter Oberflächen-Hydrophobizität rekombinant in E. coli hergestellt und sowohl immobilisiert als auch in Lösung hinsichtlich ihrer Enzymaktivität und Thermostabilität im Vergleich zum Wildtyp charakterisiert. Die vorliegende Arbeit stellt dabei eine Erstbeschreibung der Immobilisierung einer thermostabilen Trypsin-Spezies an ein Trägermaterial dar und untersucht somit erstmalig das Zusammenspiel der beiden Optimierungsstrategien Immobilisierung und genetische Modifikation. Das thermostabile Trypsin und sein Wildtyp wurden rekombinant als Zymogene hergestellt, wobei trotz verschiedener Strategien zum Erhalt der nativen Konformation, wie der Fusion mit dem Chaperon-ähnlichen Maltose-bindenden Protein (MBP), eine starke Aggregation in Einschlusskörperchen (inclusion bodies, IB) erfolgte. Im Zuge der Rückfaltung der fehlgefalteten Proteine wurden verschiedene Rückfaltungsbedingungen untersucht, wobei die Vorteile einer langsamen Absenkung des Gehalts der Denaturierungsreagenz in Kombination mit einem Cystein-Cystine- Redoxsystem dargelegt werden konnten. Es konnte keine Verbesserung der Aktivität und Thermostabilität des genetisch modifizierten Enzyms in freier Form festgestellt werden, jedoch eine erhöhte Substrataffinität. Durch Immobilisierung an Magnetbeads mit tosylfunktionalisierter Oberfläche konnte die Enzymaktivität der genetisch modifizierten Trypsin-Variante bei 80 °C vollständig erhalten werden, während die Aktivität des Wildtyps verringert wurde. Dies legt nahe, dass die erhöhte Oberflächen-Hydrophobizität der modifizierten Trypsin-Variante zu einer erhöhten Bindung an das Trägermaterial beiträgt, was eine Verbesserung der Stabilität bei thermischer Erhitzung bewirkt. KW - Rekombinante Proteine KW - Proteomik KW - Thermostabile Enzyme KW - Immobilisierung PY - 2024 SP - 1 EP - 149 PB - Technische Universität Berlin CY - Berlin AN - OPUS4-60885 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hashemi, Seyedreza A1 - Heimann, Jan A1 - Charmi, Amir A1 - Prager, Jens T1 - Guided Wave Behavior in Type IV Composite Overwrapped Pressure Vessels Under Fatigue Loading N2 - The digitalization of quality control processes and the use of digital data infrastructures is a novel idea that can be applied for ensuring the operational safety and reliability of pressure vessels, particularly in the context of hydrogen storage at high pressure. Despite the critical role these pressure vessels play, current safety regulations lack an established concept for Structural Health Monitoring (SHM). This research addresses this gap by presenting a study on the application of ultrasonic guided waves (GWs) for SHM of Type IV Composite Overwrapped Pressure Vessels (COPVs). The study focuses on the development of a reliable measurement system to transition from conventional periodic inspections to SHM and predictive maintenance, prolonging the remaining lifetime of the vessels. A sensor network is employed, consisting of fifteen piezoelectric wafers arranged in three rings, which are mounted on the outer surface of the COPV. Deploying GWs, known for their long-distance propagation and ability to cover complex structures, the study explores GW behavior under different environmental and operational conditions, including periodic pressure fluctuations and temperature loadings. Meticulous analysis of GW signals by utilizing various features and damage indices, underscores their suitability for an effective SHM under realistic working conditions. The project aims to localize defects by considering temperature, and internal pressure. Mimicking the continuous monitoring of Type IV COPVs in H2 refueling gas stations under authentic operational conditions, the COPV underwent thousands of pressure load cycles in our special test facility. The implemented methodology facilitates early damage detection, showcasing the efficacy of the designed method in effective safety assurance. T2 - 11th European Workshop on Structural Health Monitoring CY - Potsdam, Germany DA - 10.06.2024 KW - Predictive Maintenance KW - Industry 4.0 KW - Structural Health Monitoring KW - Ultrasonic Guided Waves KW - Hydrogen Storage KW - Type IV Composite Overwrapped Pressure Vessels PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-608600 DO - https://doi.org/10.58286/29780 SN - 1435-4934 SP - 1 EP - 8 PB - NDT.net CY - Potsdam, Germany AN - OPUS4-60860 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Shaheen, Sabahat T1 - Distributed acoustic sensing using geometric phase and its application to seismology N2 - This thesis deals with the development of a novel optical fiber sensing scheme based on geometric phase for sensing strain and its application to seismology. Interference of two coherent frequency offset electromagnetic waves gives rise to a geometric phase in the resulting beat signal. The existence of this phase was recently reported along with requisite conditions for its existence. This thesis proposes to detect and use this geometric phase in the context of distributed and dynamic fiber optic strain sensing, also known as distributed acoustic sensing (DAS). In the first part, I devise a novel DAS hardware setup capable of detecting the geometric phase considering that its measurement methods require the measurement of beam intensities and the beat signal’s envelope. The geometric phase is a function of relative intensity and polarisation state of two interfering beams. Therefore, its measurement is verified by determining its relation on these quantities using a polarisation scrambler and a piezoelectric transducer, inline an optical fiber. It is a fundamental study that has implications in coherent optical communication and novel sensing mechanisms. The second part involves using the geometric phase in DAS for measurement of strain. I attempt to replace the traditionally measured dynamic phase in a DAS setup with the geometric phase. This is made possible by the fact that the geometric and dynamic phases are reportedly coupled over every beat period such that their sum remains constant. However, the spatial resolution for geometric phase is lower as it is measured per beat period. I determine an equivalence for the two phases empirically as well as optimum test parameters such as the required frequency offset between the interfering beams. The advantages offered by the use of geometric phase are demonstrated; geometric phase can be measured even when the two interfering beams have non-identical polarisation states, unlike the traditionally measured dynamic phase. Moreover, it does not require phase unwrapping and is therefore free from unwrapping errors. In the third and final part, the setup, after optimisation, is tested in the field to detect seismic waves travelling on the surface of the Earth in response to a set of blasts carried out at a test-site. The surface waves are used for the characterisation of the structure and material properties of the first tens of meters of the Earth with applications in earthquake monitoring, resource exploration and infrastructure planning. In short, this study is the first of its kind to measure geometric phase in beat signal of light using optical fiber medium and to measure strain with it, for which a novel hardware setup and a novel sensing mechanism is designed and tested in addition to its application in real-world seismology measurements. KW - C-OTDR KW - Distributed fiber optic sensing KW - Distributed vibration sensing KW - Geometric phase measurement PY - 2024 SP - 1 EP - 89 PB - Technische Universität Carolo-Wilhelmina CY - Braunschweig AN - OPUS4-60956 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schalau, Bernd T1 - Ausbläser – Berechnung von Ex-Bereichen N2 - Die Gefährdungen durch die Freisetzung von Gasen und Dämpfen infolge der Ableitung über Ausbläser aus Sicherheitsventilen, Prozess-Berstscheiben, Entlüftungs- und Entspannungsleitungen sind in einer Gefährdungsbeurteilung zu bewerten. Freisetzungen aus Druckanlagen können nach TRBS 2141 beurteilt werden. In der Fachbereich AKTUELL werden verschiedene Methoden mit ihren benötigten Eingangsdaten und Anwendungsgrenzen zur Beurteilung der Gefahren an Ausbläsern für brennbare Gase vorgestellt, um den Anwendern und Prüfern von solchen Anlagen eine Hilfestellung bei der Bewertung und Beurteilung möglicher Gefahren an den prozessbedingten Stoffauslässen ins Freie zu geben. KW - Ex-Schutz bei Ausbläsern PY - 2024 IS - FBRCI-028 SP - 1 EP - 12 PB - DGUV Fachbereich Rohstoffe und chemische Industrie CY - Deutschland AN - OPUS4-60961 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmitt, M. A1 - Casperson, Ralf A1 - Baensch, F. A1 - Müller, D. T1 - Nationale, europäische und internationale Normung in der zerstörungsfreien Prüfung N2 - Normung und Standardisierung in der zerstörungsfreien Prüfung finden auf nationaler, europäischer und internationaler Ebene statt. Die Übernahme von Leitungsfunktionen in diesen Gremien erzeugt die Möglichkeit der Steuerung von Themen und Inhalten der relevanten Normen. Das persönliche Engagement der Fachexpert*innen in den nationalen Gremien und den europäischen und internationalen Arbeitsgruppen ist ein zusätzlicher Faktor für die inhaltliche Korrektheit und die inhaltliche Ausrichtung der Norm. Denn wer nicht normt, wird genormt und muss letztlich Normen anwenden, die andere entsprechend ihrer eigenen Interessen gestaltet haben. Voraussetzung für die Teilnahme in europäischen und internationalen Normungsgremien ist die Mitwirkung in den entsprechenden DINSpiegelgremien, welche die europäischen (CEN) und internationalen (ISO) Aktivitäten spiegeln und die Fachexpert*innen für die Mitarbeit autorisieren. Auf internationaler Ebene findet die Normungsarbeit in den technischen Komitees ISO/TC 135 “Non-destructive testing” und ISO/TC 44/SC 5 “Testing and inspection of welds” und ihren Arbeitsgruppen statt. Das europäische Pendant ist das CEN/TC 138 “Zerstörungsfreie Prüfverfahren” mit seinen Arbeitsgremien. Die DINSpiegelgremien sind für die deutsche Mitarbeit in diesen Gremien und die inhaltliche Bewertung der Norm-Entwürfe zuständig. T2 - DGZfP Jahrestagung 2024 CY - Osnabrück, Germany DA - 05.05.2024 KW - Normung KW - Zerstörungsfreie Prüfung KW - Qualifizierung KW - Qualitätssicherung PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-600726 DO - https://doi.org/10.58286/29496 IS - 5 SP - 1 EP - 6 AN - OPUS4-60072 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Chaudhuri, Somsubhro A1 - Stamm, Michael T1 - Infrared thermography of turbulence patterns of operational wind turbine rotor blades supported with high-resolution photography: KI-VISIR Dataset N2 - With increasing wind energy capacity and installation of wind turbines, new inspection techniques are being explored to examine wind turbine rotor blades, especially during operation. A common result of surface damage phenomena (such as leading-edge erosion) is the premature transition of laminar to turbulent flow on the surface of rotor blades. In the KI-VISIR (Künstliche Intelligenz Visuell und Infrarot Thermografie – Artificial Intelligence-Visual and Infrared Thermography) project, infrared thermography is used as an inspection tool to capture so-called thermal turbulence patterns (TTP) that result from such surface contamination or damage. To compliment the thermographic inspections, high-resolution photography is performed to visualise, in detail, the sites where these turbulence patterns initiate. A convolutional neural network (CNN) was developed and used to detect and localise the turbulence patterns. A unique dataset combining the thermograms and visual images of operational wind turbine rotor blades has been provided, along with the simplified annotations for the turbulence patterns. Additional tools are available to allow users to use the data requiring only basic Python programming skills. KW - Reference Data KW - Infrared Thermography KW - Wind energy KW - Dataset PY - 2024 DO - https://doi.org/10.5281/zenodo.13771899 PB - Zenodo CY - Geneva AN - OPUS4-61102 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Zencker, Uwe A1 - Aguado, Carlos A1 - Arkoma, Asko A1 - Bertsch, Johannes A1 - Cristóbal Beneyto, Miguel A1 - Feria Marquez, Francisco A1 - Herranz, Luis Enrique A1 - Ivanov, Ivan A1 - Király, Márton A1 - Nasyrow, Ramil A1 - Papaioannou, Dimitrios A1 - Ruiz-Hervias, Jesus A1 - Vlassopoulos, Efstathios T1 - Thermo-mechanical-chemical properties of unirradiated and irradiated samples of spent nuclear fuel rod segments and cladding N2 - The report addresses the experimental characterisation, thermo-mechanical modelling and performance of unirradiated and irradiated samples of spent nuclear fuel rod segments and cladding. Hydrogen is relocated in nuclear fuel claddings by diffusion along temperature, stress, and concentration gradients, and towards a liner if existent. The precipitation of hydrides during cool-down at the beginning of the storage is influenced by mechanical stress. A strong accumulation of hydrides and a disadvantageous hydride alignment in relation to the stress state can affect the mechanical properties and compromise the fuel cladding integrity. Neutron radiography is used to determine spatially resolved hydrogen and hydride distributions in claddings. A liner in duplex claddings attracts hydrogen, which will then no longer be available to form detrimental hydrides in the bulk part of the cladding. Individual three-point bending and gravitational impact tests on filled pressurised spent nuclear fuel rod segments were conducted in hot-cell facilities. The material behaviour under three-point bending in the presence of hydrides and at different temperatures was systematically investigated in quasi-static laboratory tests on unirradiated rod segments with and without surrogate pellets until rupture. Ring compression tests were carried out on irradiated and unirradiated samples at different temperatures and both with and without radial hydrides. With radial hydrides, brittle failure is possible even at low deformation and simultaneously low temperature. Crack initiation will occur on the radial hydride with the highest fracture mechanics load, which depends on the hydride size in the regions with the highest hoop stresses. Due to the high hydrogen content used in creep tests conducted, precipitation hardening of the hydrides in the zirconium alloy significantly reduces the creep rate, as it strengthens the material and inhibits the dislocation sliding. The use of finite element analyses on mechanical tests to determine the cladding properties using a numerical optimisation method based on a large number of automatically generated sensitivity calculations is demonstrated. The brittle fracture of cladding samples with radial hydrides in the ring compression test can be described with a cohesive zone model if the cohesive parameters are selected appropriately and the hydride morphology is specified. Progress was made in the verification, validation and enhancement of spent fuel performance codes by the compilation of a representative validation database (related to rod internal pressure, fission gas release, rod void volume, and in-clad hydrogen distribution), the enhancement of CIEMAT’s FRAPCON-xt code for rod internal pressure prediction at high burnup, the enhancement of CIEMAT’s in-clad hydrogen performance subroutine HYDCLAD with more phenomenological modelling, the extension of INL’s BISON code with a cladding creep law for dry storage, and a benchmark with FRAPCON-xt and BISON simulating in-reactor and dry storage scenarios. KW - Spent Nuclear Fuel KW - Cladding KW - Experimental Characterisation KW - Modelling KW - Fuel Performance Code PY - 2024 SP - 1 EP - 102 PB - European Joint Programme EURAD AN - OPUS4-61008 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ali, Syrine T1 - Antibiotics in wastewater: Optimisation of an ELISA Assay for the Detection of Clarithromycin in Wastewater N2 - Since they were first discovered, antibiotics have been used extensively to treat diseases caused by bacteria. This increasing and uncontrollable use is causing a number of environmental problems. Unfortunately, traces of various antibiotics can be found in drinking water also in wastewater. In this study was focused on the detection of clarithromycin (CLA) in wastewater using the immunofluorescence ELISA assay which is a highly selective and sensitive technique. ELISA is a multi-type of technique and the one used in this study was the indirect competitive ELISA. For the detection of CLA, a checkerboard was performed to obtain a dilution factor until 1:1,000,000 for the antigen (CLA-BSA) with a concentration of 5 ng/mL and a dilution factor until 1:5,120,00 for the primary antibody (anti-CLA mAb) with a concentration of 1. 035 ng/mL. Standardization was performed to obtain a better profile of the 4-parameter curve A, B, C and D which determines the maximum, minimum and inflection concentration. In addition, a pure synthetic water experiment was used to determine the stability of the assay and the matrix effect due to some interactions from chemicals or components used during the assays. The detection of CLA in pure water in Germany showed that the concentration of CLA differs from province to province and differs from time of year, however, the commonly detected concentration of CLA in pure water was ng/L. KW - Immunoassay KW - Clarithromycin KW - Abwasser KW - Anthropogener Marker KW - Antibiotikum PY - 2024 SP - 1 EP - 51 PB - Berliner Hochschule für Technik CY - Berlin AN - OPUS4-61027 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lu, Xin A1 - Krebber, Katerina T1 - Configuration simplification and data reduction in a DAS system for monitoring large infrastructures N2 - The distributed acoustic sensor based on an imbalanced Mach-Zehnder interferometer with a 3×3 coupler is simplified by using a balanced detector instead of three identical photodetectors. The obtained data is reduced by two third accordingly. T2 - Optica Sensing Congress 2024 CY - Toulouse, France DA - 15.07.2024 KW - Data reduction KW - Distributed fiber optic sensing KW - System simplification PY - 2024 SP - 1 EP - 2 PB - Optica CY - Washington D.C., USA AN - OPUS4-60840 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sunder, Sruthi A1 - Jauregui Rozo, Maria A1 - Ruckdäschel, Holger A1 - Schartel, Bernhard T1 - Investigating the trade-off effects of inorganic phosphate/silicate flame retardant content on the fire performance and post-fire flexural mechanics of epoxy/glass fiber composites N2 - Considering the existing challenges involved in the transfer of flame retardant (FR) formulations from epoxy (EP) resins to glass fiber reinforced composites (GFRCs), obtaining data on the post-fire flexural properties of such composites is even more challenging as this involves balancing test parameters with potential composite delamination. In this study, solvent-free FR additives: ammonium polyphosphate (APP), and inorganic silicate (InSi) were added at 10, 30% and 50% w/w loading to a Bisphenol A diglycidyl ether (DGEBA)-dicyandiamide (DICY)-Urone resin matrix. These resin formulations were transferred to bidirectional (BD) glass fiber composites via prepregs. A novel, but facile approach was developed to prepare the composite samples for furnace tests at 400 oC. The composites were also subjected to fire exposure at different heat fluxes and times via a bench-scale test and subsequently tested via three-point bending. At approximately 3.5% P content, the FRs significantly improve the fire performance of both the resins and composites. However, they also degrade the systems’ pre- and postfire flexural modulus and strength. Therefore, improving the flame-retardant mode of action of the FRs in the composites, contrastingly reduces their structural integrity post-fire leading to a trade-off effect. T2 - ECCM21 – 21st European Conference on Composite Materials CY - Nantes, France DA - 02.07.2024 KW - Flame retardants KW - Post-fire KW - Epoxy KW - Glass fiber composites KW - Prepregs PY - 2024 SP - 1 EP - 7 AN - OPUS4-60788 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - El Moutaouakil, H. A1 - Fuchs, C. A1 - Savli, E. A1 - Heimann, Jan A1 - Prager, Jens A1 - Moll, J. A1 - Tschöke, K. A1 - Márquez Reyes, O. A1 - Schackmann, O. A1 - Memmolo, V. A1 - Schneider, T. T1 - Acquiring a Machine Learning Data Set for Structural Health Monitoring of Hydrogen Pressure Vessels at Operating Conditions using Guided Ultrasonic Waves N2 - Hydrogen is an energy source of increasing importance. As hydrogen is very reactive to air and needs to be stored under high pressure, it is crucial to provide safe transportation and storage. Therefore, structural health monitoring, based on guided ultrasonic waves and machine learning methods, is used for Composite Overwrapped Pressure Vessels (COPVs) containing hydrogen. To acquire data that allows robust detection of COPV defects, there are two main process parameters to consider. These are the pressurization of the vessel and the temperature conditions at the vessel. This paper will focus on the derivation of a design of experiment (DoE) from the needs of various validation scenarios (e.g. concerning pressure, temperature or excitation frequency). Practical limitations must be considered as well. We designed experiments with multiple reversible damages at different positions. A network of 25 transducers, structured as five rings with five sensors in one line, is installed on a vessel. Guided ultrasonic waves are used via the pitch-catch procedure, which means that the transducers act pairwise as transmitter and receiver in order to measure all transmitterreceiver combinations. This leads to 600 signal paths, recorded by a Verasonics Vantage 64 LF data acquisition system. Finally, the influences of temperature and pressure within the acquired data set are going to be visualized. T2 - 11th European Workshop on Structural Health Monitoring CY - Potsdam, Germany DA - 10.06.2024 KW - Composite Overwrapped Pressure Vessel KW - Hydrogen KW - Guided Ultrasonic Waves KW - Data Acquisition KW - Pressurization KW - Machine Learning PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-607472 DO - https://doi.org/10.58286/29754 SN - 1435-4934 SP - 1 EP - 8 AN - OPUS4-60747 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hicke, Konstantin A1 - Lu, Xin A1 - Chruscicki, Sebastian A1 - Krebber, Katerina T1 - Measurement of Slowly Changing and Quasi-Static Strain Signals for Ground Motion Monitoring Applications using Distributed Acoustic Sensing N2 - The suitability of wavelength-scanning COTDR for distributed dynamic strain sensing (DAS) along buried fiber cables for long-term geotechnical monitoring applications is demonstrated by experiments showing the method’s capability to demodulate slowly varying and quasi-static signals. T2 - Optica Sensing Congress 2024 CY - Toulouse, France DA - 15.07.2024 KW - Ground motion KW - Ground movement monitoring KW - Distributed fiber optic sensing KW - Quasi-static signals KW - Geomonitoring PY - 2024 SP - 1 EP - 2 PB - Optica CY - Washington D.C., USA AN - OPUS4-60816 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Vlassopoulos, Efstathios A1 - Dagan, Ron A1 - Fiorito, Luca A1 - Herm, Michel A1 - Jansson, Peter A1 - Kromar, Marjan A1 - Király, Márton A1 - Leppanen, Jaakko A1 - Feria Marquez, Francisco A1 - Metz, Volker A1 - Papaioannou, Dimitrios A1 - Herranz, Luis Enrique A1 - Rochman, Dimitri A1 - Schillebeeckx, Peter A1 - Seidl, Marcus A1 - Hernandez Solis, Augusto A1 - Stankovskiy, Alexey A1 - Alvarez Velarde, Francisco A1 - Verwerft, Marc A1 - Rodriguez Villagra, Nieves A1 - Wiss, Thierry A1 - Zencker, Uwe A1 - Žerovnik, Gasper T1 - EURAD Work Package 8 Deliverable 8.2 Updated State-of-the-Art Report N2 - The state-of-the-art (SOTA) report offers an overview of the status of knowledge in the area of spent nuclear fuel (SNF) characterisation and assessment during the pre-disposal phase using several numerical and experimental approaches and methodologies. A review on characterisation of SNF properties in terms of source term and inventory assessment (neutron, gamma-ray emission, decay heat, radionuclide inventory, and elemental content) and in terms of out-of-core fuel performance (cladding performance and fuel integrity in view of the safety criteria for SNF interim storage, transport and canister packaging) is presented. This updated SOTA report provides the progress made in the spent fuel characterisation (SFC) work package as part of the European Joint Programme on Radioactive Waste Management (EURAD), documents the identified technical gaps, and provides recommendations for future work. The report is expected to be used by all EURAD colleagues in their national programmes as a key resource for knowledge management programmes and to contribute to demonstrating and documenting the state-of-the-art. KW - Radioactive waste management KW - Spent fuel characterisation KW - Extended interim storage KW - Predisposal PY - 2024 UR - https://www.ejp-eurad.eu/publications/d82-updated-state-art-report SP - 1 EP - 182 AN - OPUS4-61218 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Singh, R. A1 - Vigelahn, L. A1 - Vogel, Christian A1 - Roesch, Philipp A1 - Simon, Franz-Georg A1 - Egloffstein, T. A1 - Birke, V. T1 - Rapid and Virtually Complete Mechanochemical Reductive Defluorination of Per- and Polyfluoro Alkyl Substances (PFAS) In Contaminated Soil Using Sodium and Amines as Co-milling Agents: A Promising First Approach for the Development of Novel Non-Combustion PFAS Remediation Processes for Soils N2 - PFAS contamination poses significant challenges due to their persistence, bioaccumulation, and potential adverse effects on ecosystems and human health. In recent years, conventional treatment methods, such as incineration, photolysis, and chemical oxidation, have been applied for PFAS treatment. However, these technologies have limitations in terms of their efficacy and cost-effectiveness for efficient PFAS degradation. Consequently, researchers have explored alternative approaches such as photocatalysis, sonochemical degradation, oxidation, electrochemical degradation, and mechanochemical degradation also known as DMCR (Dehalogenation by Mechanochemical Reaction) to address the remediation challenge posed by PFAS contaminated environments. Lab scale experiments were conducted using a planetary ball mill, procured from Retsch GmbH Germany, equipped with 50 mL steel grinding jars under controlled conditions to investigate the degradation of perfluorooctanoic sulfonic acid (PFOS) and perfluorooctanoic acid (PFOA) in contaminated model sand. The experiments were carried out in two stages: initially, with sand alone (15 g), and subsequently, with the addition of co-milling agents, that is, sodium metal (Na), Na with butylamine (BA), and Na with ethylenediamine (EDA) in different proportions. T2 - International CleanUp conference CY - Adelaide, Australia DA - 15.09.2024 KW - Mechanochemical treatment KW - Per- und Polyfluoroierte Alkylsubstanzen (PFAS) KW - Remediation PY - 2024 SP - 177 AN - OPUS4-61119 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Glauer, M. A1 - Schilling, Markus A1 - Stappel, M. T1 - A practical ontology development guide N2 - Knowledge representation is becoming increasingly important in view of the large amounts of data that are handled in the modern scientific landscape. Many of the domains that have most readily realised this problem and worked on potential solutions have been the domain of biochemistry. And although the developments sought here were not accompanied by philosophers, this process organically led to the development of formal and structured representations of certain domains. While the resulting structures were not the first formal ontologies, they are ones that are still in wide use to this day. These approaches have led to major advances in the organisation, structuring and communication of scientific results. Since then, a variety of other domains have tried to adapt a similar process and develop their own ontologies. However, the development of ontologies from the domain of biochemistry was the result of a years-long process that also involved a large number of errors and course corrections. One of the greatest challenges is also one of the greatest strengths of ontologies: Interoperability with other ontologies. To ensure this interoperability, ontologies must follow certain principles. In the field of biochemistry, the OBO Foundry has established itself, which offers functionalities for a rich network of ontologies from the domain, but at the same time also defines rules. The purpose of this document is to define a similar set of rules for open ontology development, but which addresses a broader domain and at the same time lowers the barrier of entry for new ontology developers. To this end, we will outline a workflow that can be used to build new ontologies more efficiently. This workflow is based not only on our own years of experience in ontology development, but also on the rules of external experts such as the OBO Foundry. KW - Ontology KW - Data integration KW - Ontologie KW - Data interoperability PY - 2024 UR - https://scientific-ontology-network.github.io/ UR - https://github.com/scientific-ontology-network/ontology-development-guide/releases/download/v0.1.0/ontology-guide.pdf SP - 1 EP - 27 PB - GitHub CY - San Francisco ET - Version 0.1 AN - OPUS4-61140 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zhu, Jiangchao A1 - Madia, Mauro A1 - Schurig, M. A1 - Schlums, H. A1 - Zerbst, Uwe T1 - Fracture mechanics-based structural integrity assessment of aeroengine turbine disks under overspeed conditions N2 - Aero-engine turbine disks are safety-relevant components which are operated under high thermal and mechanical stress conditions. The actual part qualification and certification procedures make use of spin-tests conducted on productionsimilar disks. While these tests provide, on the one hand, a reliable definition of the critical conditions for real components, on the other hand they represent a relevant cost item for engine manufacturers. The aim of this work is to present part of a fracture mechanics-based procedure under development which aims at replacing the tests on production-similar disks with lab tests on fracture mechanics specimens. In particular, the rimpeeling failure mode is considered as case study. A semi-circular surface crack is modelled at the most stressed region at the diaphragm of a turbine disk, with the crack plane perpendicular to the radial direction. The crack is therefore subjected to a biaxial stress state and grows under increasing rotational speed until it triggers the rim-peeling failure. The finite element simulation of the cracked disk considers the real thermal and mechanical loading conditions. In order to design a lab representative specimen, beside the crack driving force, expressed in terms of � -integral, also the constraint to plastic deformation e.g., stress triaxiality, at the crack-tip must be similar for the same crack in the specimen and in the disk. This has been achieved and as expected, both the highest � -integral and constraint factor are calculated at the same location along the crack front for both disk and specimen. The results of the structural integrity assessment in the form of a Failure Assessment Diagram (FAD) show good agreement between designed specimen and disk both in terms of expected failure mode and value of the critical speed. Probabilistic aspects are also considered in the calculations. T2 - ASME Turbo Expo 2022: Turbomachinery Technical Conference and Exposition (GT2022) CY - Rotterdam, The Netherlands DA - 13.06.2022 KW - Fracture mechanics KW - Burst KW - Turbine disk PY - 2022 SP - 1 EP - 7 PB - ASME AN - OPUS4-55903 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simon, Franz-Georg T1 - Aschen und Schlacken und aus der Abfallverbrennung, chemische und mineralogische Zusammensetzung N2 - Aschen und Schlacken sind mengenmäßig der wichtigste Reststoffstrom in der thermischen Abfallbehandlung. Die enthaltenen elementaren Metalle werden mit gängigen Verfahren abgetrennt und einer Verwertung als Sekundärrohstoff zugeführt. Durch die chemische und mineralogische Zusammensetzung der mineralischen Fraktion wird das Umweltverhalten sowie die abfallrechtliche Einstufung bestimmt. Methoden zur Ermittlung der Einstufung werden vorgestellt. Das Löslichkeitsverhalten von Schwermetallen in gealterten Aschen hängt meist vom pH-Wert in den standardisierten Auslaugtests ab. Das davon abweichende Verhalten von Antimon wird detailliert beschrieben. T2 - VDI-/ITAD-Spezialtag Aufbereitung und Verwertung von MVA-Rückständen CY - Würzburg, Germany DA - 20.09.2022 KW - Rostasche KW - Aquatische Toxizität KW - Ersatzbaustoffverordnung PY - 2022 SP - 1 EP - 8 AN - OPUS4-56068 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ermilova, Elena A1 - Weise, Matthias A1 - Hertwig, Andreas T1 - Hybrid optical measurement technique for detection of defects in epitaxially grown 4H-SiC layers N2 - Recent developments in power electronics require the use of new wide bandgap compound semiconductor. We demonstrate the use of the ellipsometry and white light interference microscopy to detect defects in epitaxially grown SiC layers on SiC substrates. Such hybrid optical metrology methods can be used to better understand the mechanism of the development of the defects as well as their effects on the material´s optoelectronic properties. T2 - EOS Annual Meeting (EOSAM 2022) CY - Porto, Portugal DA - 12.09.2022 KW - Imaging ellipsometry KW - White light interference microscopy KW - Wide bandgap compound semiconductor KW - Epitaxially grown 4H-SiC layers PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-561113 DO - https://doi.org/10.1051/epjconf/202226610001 VL - 266 SP - 1 EP - 2 AN - OPUS4-56111 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schlegel, Moritz-Caspar A1 - Rockland, Ulrike A1 - Harrer, Andrea T1 - Informationsmaterial zu Wartung und Betrieb von Getränkekühlern N2 - „Getränkekühler optimal einsetzen“: So sparen Sie die Energiekosten und schonen das Klima. Wussten Sie, dass Sie durch den Einsatz eines effizienten Getränkekühlers (Energieeffizienzklasse B) ca. 114 € pro Jahr sparen im Vergleich zu einem weniger effizienten Gerät (Energieeffizienzklasse D)? Aber nicht immer gibt es die Möglichkeit ein Neugerät anzuschaffen. Oft werden die Kühlgeräte von Getränkeherstellern zur Präsentation ihrer Waren zur Verfügung gestellt. Trotzdem tragen am Ende die Betreiber:innen die Betriebskosten der Geräte. Aber auch beim Einsatz Ihres weniger effizienten Getränkekühler gibt es verschiedene Möglichkeiten, die Energiekosten zu senken. Beispielsweise kann schon der Einsatz einer Zeitschaltuhr zu einer Stromreduzierung von bis zu 50 Prozent oder auch die richtige Platzierung der Geräte an kühlen Orten ohne Zugluft zu einem geringeren Strombedarf von bis zu 30% führen. In unserer Checkliste für die Aufstellung und das Betreiben von Getränkekühlgeräten zeigen wir Ihnen einfache Schritte, um den Energieverbrauch schnell zu senken. KW - Getränkekühler PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-561581 SP - 1 EP - 2 CY - Berlin AN - OPUS4-56158 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ewert, U. A1 - Jaenisch, Gerd-Rüdiger A1 - Schumacher, David A1 - Bircher, B. A1 - Meli, F. A1 - Deresch, A. T1 - EMPIR-Projekt NanoXSpot: Neue Normentwürfe für die Brennfleckmessung an Röntgenröhren im Makro-, Mikro- und Nanometerbereich für Hersteller und Anwender N2 - Im Rahmen des EMPIR-Projektes NanoXSpot (Nanometre X-ray Focal Spot Measurement) werden rückführbare Messverfahren zur Bestimmung der Brennfleckgröße und -form von Röntgenröhren im Bereich von 100 nm bis 10 mm entwickelt, welche die Grundlage für die Erarbeitung mehrerer Normentwürfe bilden. Diese werden 2022 parallel bei ISO TC 135 (NDT) SC 5 (RT) und CEN TC 138 (NDT) WG 1 (RT) eingereicht. Entsprechende Normen werden auch bei ASTM vorgestellt. Die Norm EN 12543-4 (Kantenmethode) wird umgeschrieben für die Messung von Brennflecken von 1 μm – 10 mm durch Auswertung von Loch- oder Scheibenaufnahmen. Der im Rahmen des NanoXSpot-Projektes neu entwickelte NxS-Testkörper ist geeignet für den Bereich von 1 μm – 100 μm. Von 100 μm bis 10 mm können ASTM-Lochtestkörper verwendet werden, die bereits bei ASTM E 1165 beschrieben sind. Neu ist die Anwendung eines CT-Algorithmus zur Rekonstruktion der Brennflecke, um Lochblenden-basierte Brennfleckkameras, insbesondere im Bereich unter 100 μm, zu ersetzen. Ein neuer Normteil, EN 12543-6, wurde entworfen, um die Brennfleckmessung im Bereich 100 nm – 20 μm mit hoher Genauigkeit zu ermöglichen. Verschiedene Strichgruppen-Testkörper kommen hier zum Einsatz. Das sind die JIMAPrüfkörper, ein neuer Hochkontrast-Strichgruppentestkörper von YXLON (HiCo) und der neu entwickelte Testkörper NxS. Diese werden vorgestellt. Die Messprozedur für Röhrenhersteller wird auf einer numerischen Fit-Prozedur basieren, die über einen Ringversuch im Projekt validiert wurde. Beide Normen benötigen numerische Auswertealgorithmen zur korrekten Anwendung, die als kommerzielle Software und Public Domain – Software verfügbar gemacht werden. Es wird über die zu erwartenden Standardprozeduren und die erforderliche Hardware zur Anwendung der Normen informiert. T2 - DGZfP-Jahrestagung CY - Kassel, Germany DA - 23.05.2022 KW - Röntgenröhre KW - Brennfleckmessung KW - Normung PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-561029 SP - 1 EP - 10 AN - OPUS4-56102 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schumacher, David A1 - Jaenisch, Gerd-Rüdiger A1 - Ewert, U. A1 - Bircher, B. A1 - Meli, F. A1 - Sofiienko, A. A1 - Steffen, J. P. A1 - Deresch, A. T1 - EMPIR-Projekt NanoXSpot: Ringversuch zur Untersuchung der neu entwickelten Methoden für die Brennfleckmessung an Röntgenröhren im Mikro- und Nanometerbereich N2 - Im Rahmen des EMPIR-Projektes NanoXSpot (Nanometre X-Ray Focal Spot Measurement) werden rückführbare Messverfahren zur Bestimmung der Brennfleckgröße und -form von Röntgenröhren mit Submikrometerauflösung (100 nm – 20 μm) entwickelt, die die Grundlage für die Erarbeitung eines Standardentwurfes bilden. Der Standardentwurf wird bei CEN TC 138 (Non-destructive testing) WG 1 (Radiographic testing) eingereicht und mit ISO und ASTM harmonisiert. Zur Untersuchung der entwickelten Methoden (Brennfleck-CT, Fit-Prozedur für Strichgruppenkörper) und des im Projekt NanoXSpot neu entworfenen Testkörpers, NxS, wurde ein Ringversuch durchgeführt. Dabei wurde sowohl der angestrebte Überlappungsbereich mit EN 12543 Teil 5 (Messung der effektiven Brennfleckgröße von Mini- und Mikrofokus-Röntgenröhren) und ASTM E 2903 (Standard Test Method for Measurement of the Effective Focal Spot Size of Mini and Micro Focus X-ray Tubes) für Brennflecke >5 μm als auch Brennflecke <5 μm untersucht. Im Mittelpunkt standen dabei Stabilität und Wiederholbarkeit der entwickelten Methoden zur Bestimmung der Brennfleckgröße. In diesem Beitrag werden die Ergebnisse des durchgeführten Ringversuches vorgestellt und diskutiert, um Schlussfolgerungen und Empfehlungen für die Vorbereitung eines erweiterten Ringversuchs mit Partnern und Stakeholdern abzuleiten. T2 - DGZfP-Jahrestagung CY - Kassel, Germany DA - 23.05.2022 KW - Brennfleckmessung KW - Computer-Tomografie KW - EMPIR KW - Normung PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-561037 SP - 1 EP - 2 AN - OPUS4-56103 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rolle, Annette A1 - Wille, Frank ED - Czarwinski, R. T1 - Radioaktive Stoffe in besonderer Form-wichtige Aspekte im Zulassungsverfahren N2 - Für die Beförderung von umschlossenen radioaktiven Stoffen (Strahler) können Transporterleichterungen gelten, wenn das Strahlerdesign nachweislich unfallsicher ausgelegt ist und eine Zulassung als radioaktiver Stoff in besonderer Form vorliegt. Die in Deutschland zuständige Behörde für die Prüfung und Zulassung radioaktiver Stoffe in besonderer Form ist die Bundesanstalt für Materialforschung und –prüfung (BAM). Eine oft langfristige Nutzung der Strahler kann eine alterungsbedingte Schwächung der Umschließung des radioaktiven Stoffes zur Folge haben. Jeder Strahler einer zugelassenen Bauart muss jedoch im Beförderungsfall zu jeder Zeit, auch nach längerer Nutzung, den vorgeschriebenen Prüfanforderungen genügen. Die Alterungsbewertung auf der Grundlage einer vom Antragsteller zu spezifizierenden Nutzungsdauer des radioaktiven Stoffes in besonderer Form ist seit langer Zeit Bestandteil des Zulassungsverfahrens in Deutschland. Ein von Deutschland eingebrachter Vorschlag im Rahmen der anstehenden Revision der IAEA Empfehlungen für die sichere Beförderung von radioaktiven Stoffen (SSR-6) soll die Lesbarkeit des Regelwerkes bezüglich der Alterungsbewertung verbessern, Klarheit über die damit verbundenen Anforderungen erzeugen und damit zu einer Harmonisierung der Zulassungsverfahren auf internationaler Ebene beitragen. In diesem Beitrag sollen wichtige Einflussfaktoren auf das Alterungsverhalten von radioaktiven Stoffen in besonderer Form aufgezeigt und die Notwendigkeit für die Spezifikation einer Nutzungsdauer als Grundlage für die Alterungsbewertung begründet werden. Der deutsche Vorschlag für die Revision des IAEA Regelwerks zum sicheren Transport radioaktiver Stoffe (SSR-6) wird vorgestellt und erläutert. T2 - Jahrestagung des FS 2022 CY - Konstanz, Germany DA - 26.09.2022 KW - Strahlenschutz KW - Radioaktive Stoffe KW - Beförderung KW - Zulassung PY - 2022 SN - 1013-4506 SP - 15 EP - 20 PB - Fachverband für Strahlenschutz e.V. CY - Berlin AN - OPUS4-56134 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ewert, U. A1 - Jaenisch, Gerd-Rüdiger A1 - Schumacher, David A1 - Zscherpel, U. A1 - Deresch, A. A1 - Bircher, B. A1 - Meli, F. T1 - Schnelle Messung und tomographische Rekonstruktion von Brennflecken < 5 μm durch Aufnahmen strukturierter Prüfkörper N2 - Im Europäischen EMPIR-Projekt „NanoXSpot“ (Measurement of the focal spot size of Xray tubes with spot sizes down to 100 nm) werden neue Messmethoden für Brennflecke von Röntgenröhren entwickelt. Teil des Projektes ist die Entwicklung eines zur Lochkameramethode äquivalenten Messverfahrens für kleine Brennflecke. ASTM E 1165-20, Annex A, beschreibt die Bestimmung von Brennfleckgrößen aus Kantenprofilen von Lochaufnahmen für Röntgenröhren mit Brennflecken > 50 μm. Es wurde bereits vorgeschlagen über die Analyse der richtungsabhängigen Kantenunschärfe einer Lochblende und anschließender CT-Rekonstruktion die Intensitätsverteilung des Brennflecks äquivalent zur Lochkameraaufnahme zu berechnen. Die Lochkameramethode, wie in EN 12543-2 und ASTM E 1165-20 beschrieben, ist im unteren Größenbereich für Mikrofokusröhren nicht geeignet, da Pinholes < 10 μm schwer zu fertigen sind und lange Belichtungszeiten erwartet werden. Mit Hilfe exakt gefertigter Lochblenden sowie strukturierter Targets mit konvergierenden Strukturen wird der Bereich mit der Single-Shot-CT-Methode auf die Messung von Mikrofokusröhren, alternativ zur Vermessung von Kanten oder Strichgruppenkörpern, erweitert. Die rekonstruierten Brennfleckformen werden mit Kantenund Lochkameraaufnahmen quantitativ verglichen, um die Messgenauigkeit zu bewerten. Außerdem werden CNR und Messzeit bestimmt, um die Wirtschaftlichkeit der Verfahren zu bewerten. T2 - DGZfP-Jahrestagung CY - Online meeting DA - 10.05.2021 KW - Röntgenröhre KW - Brennfleckmessung KW - Prüfkörper KW - Rekonstruktion PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-561846 SP - 1 EP - 2 AN - OPUS4-56184 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Haratsu, T. A1 - Sakaue, M. A1 - Matsukura, H. A1 - Neumann, Patrick P. A1 - Ishida, H. ED - Tardioli, D. ED - Matellán, V. ED - Heredia, G. ED - Silva, M. F. ED - Marques, L. T1 - Simulating a Gas Source Localization Algorithm with Gas Dispersion Produced by Recorded Outdoor Wind N2 - This paper reports the use of the first gas dispersion simulator capable of introducing large wind fluctuations into simulations. The proposed simulator enables testing of a modification made to a gas source localization algorithm in a realistic scenario in order to study how the change affects it. Gas source localization in an outdoor environment is a challenging task mainly due to the complexity of the gas spread caused by the unpredictable nature of constantly changing wind. Therefore, a novel use of outdoor wind in developing a gas source localization system by simulation is presented in this paper. To consider the characteristic of sudden but large and unpredictable changes in wind direction, we propose to use recorded outdoor wind to simulate a realistic outdoor gas dispersion which has been done for the first time to the best of our knowledge. With the use of this simulator, we have tested a modification to a mobile robot-based gas source localization algorithm. Multiple simulations of the modified and the original particle filter-based algorithm have been done to study the effect of the tested modification. The results showed that a small difference in the algorithm can greatly impact the results. From this study, we show that the use of simulation consisting of the necessary traits to evaluate outdoor gas source localization, has the potential to accelerate the development of a reliable localization system. T2 - ROBOT2022: Fifth Iberian Robotics Conference CY - Zaragoza, Spain DA - 23.11.2022 KW - Gas Dispersion Simulator KW - Gas Source Localization KW - Mobile Robot Olfaction KW - Particle Filter PY - 2023 SN - 978-3-031-21061-7 DO - https://doi.org/10.1007/978-3-031-21062-4_9 SP - 105 EP - 116 PB - Springer AN - OPUS4-56416 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Üstündag, Ömer A1 - Bakir, Nasim A1 - Pittner, Andreas A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Einlagiges MSG-Hochleistungsschweißen von dickwandigen Baustählen mit kontaktloser elektromagnetischer Schmelzbadsicherung N2 - Diese Arbeit zeigt erstmals die Anwendung einer elektromagnetischen Schmelzbadsicherung beim einlagigen MSG-Schweißen von dickwandigen Stählen. Die innovativen Entwicklungen im Bereich des Lichtbogenschweißverfahrens ermöglichen eine Erhöhung der Abschmelzleistung, um die Einschweißtiefe zu steigern. Somit kann die Lagenanzahl reduziert und die Produktivität gesteigert werden. Allerdings besteht insbesondere beim einlagigen Schweißen von dickwandigen Bauteilen in PA-Position ein erhöhtes Risiko für das gravitationsbedingte Austropfen der Schmelze an der Wurzel. Zur Verhinderung werden Badsicherungen eingesetzt, die mechanisch angebracht und nach dem Schweißen entfernt werden müssen, was zeit- und kostenintensiv ist. Die im Rahmen dieser Studie eingesetzte elektromagnetische Schmelzbadsicherung wirkt dem gravitationsbedingten Austropfen der Schmelze entgegen und kompensiert den hydrostatischen Druck. Sie wirkt kontaktlos, was im Gegensatz zu herkömmlichen Badsicherungen vorteilhaft ist, so dass auf eine zeit- und kostenintensive Nachbearbeitung der Schweißnahtwurzel verzichtet werden kann. Das auf extern angelegten oszillierenden Magnetfeldern beruhende Verfahren wird dabei unterhalb des zu schweißenden Bauteils positioniert. Die Magnetfeldlinien sind quer zur Schweißrichtung ausgerichtet, sodass längs zur Schweißrichtung Wirbelströme im Werkstück und eine stets nach oben gerichtete Lorentzkraft generiert werden. Mit Hilfe der elektromagnetischen Badsicherung konnten beim einlagigen MSG-Schweißen von bis zu 10 mm dicken Blechen die Tropfenbildung vermieden werden. Die innovative Technologie ermöglicht es, dickwandige Bauteile einlagig zu schweißen und reduziert die Nachbearbeitungszeiten und -kosten deutlich. T2 - DVS Congress 2022 - Große Schweißtechnische Tagung CY - Koblenz, Germany DA - 19.09.2022 KW - Elektromagnetische Schmelzbadsicherung KW - Hochleistungsschweißen KW - MSG-Schweißen PY - 2022 SN - 978-3-96144-189-1 VL - 382 SP - 640 EP - 645 PB - DVS Media GmbH AN - OPUS4-56371 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pauw, Brian Richard T1 - dataMerge V0.1 - A statistics-aware binning and merging backend N2 - A tool for merging and/or rebinning single or multiple datasets to achieve a lower point density with best possible statistics. highly scriptable, CLI, no GUI Version 0.1: works but could do with a cleanup. Weighting by uncertainty currently always on, but should be optional for use as an azimuthal or radial averager KW - X-ray science KW - Image averaging KW - Dataset merging KW - Photon counting detectors KW - SAXS KW - SANS KW - X-ray scattering KW - X-ray diffraction PY - 2022 DO - https://doi.org/10.6084/m9.figshare.21591360 PB - Digital Science CY - Cambridge, MA, USA AN - OPUS4-56340 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Üstündag, Ömer A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Elektromagnetische Schmelzbadbeeinflussung beim Laserhybridschweißen von Dickblechen N2 - Die technischen Entwicklungen in der Lasertechnologie in den letzten Jahrzehnten haben eine neue Generation von Hochleistungslasersystemen im Leistungsbereich bis zu 100 kW auf den Markt gebracht. Dennoch ist die industrielle Anwendung des Hochleistungslaserstrahlschweißens auf bis zu 15 mm dicke Bleche beschränkt. Mögliche Ursachen der Einschränkungen des Verfahrens sind z.B. die Sensibilität des Verfahrens auf Fertigungstoleranzen wie Spalt und Kantenversatz, die erhöhte Tropfenbildung bei höheren Blechdicken und eine inhomogene Verteilung des Zusatzwerkstoffes beim Laserhybridschweißen. In dieser Studie wird ein auf extern angelegte Magnetfelder basierte elektromagnetische Schmelzbadstütze eingesetzt, um die Grenzen des Verfahrens zu erweitern und die Herausforderungen zu minimieren. Der wesentliche Vorteil der elektromagnetischen Schmelzbadstütze ist, dass sie berührungslos arbeitet. Mit Hilfe der elektromagnetischen Schmelzbadstütze konnten bei 20 mm dicken Proben aus S355J2 die Tropfenbildung an der Wurzel vermieden werden. Zudem wurde der Einfluss der Kantenqualität auf die Schweißnahtqualität untersucht, wobei verschiedene Schneidverfahren zur Kantenvorbereitung eingesetzt wurden, wie z.B. Plasma-, Brenn- oder Laserschneiden. Es konnte gezeigt werden, dass auch bei schlechteren Kantenvorbereitung im Gegensatz zu gefrästen Bauteilen die Werkstoffe einlagig mittels Laserhybridschweißen bei einer hohen Schweißnahtqualität gefügt werden konnten. Bei plasmageschnittenen Proben wurden zudem eine Spaltüberbrückbarkeit bzw. Kantenversatz von bis zu 2 mm sicher überbrückt. Des Weiteren war es mit Hilfe der externen Magnetfelder möglich, die Durchmischung des Zusatzwerkstoffes über die gesamte Schweißnahttiefe deutlich zu homogenisieren. T2 - 42. Assistentenseminar der Wissenschaftlichen Gesellschaft Fügetechnik e.V. CY - Blankenau, Germany DA - 06.10.2021 KW - Elektromagnetische Schmelzbadstütze KW - Laserhybridschweißen KW - Dickblech PY - 2022 VL - 385 SP - 1 EP - 7 PB - DVS Media GmbH AN - OPUS4-56375 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Manninger, Tanja T1 - Eco friendly stabilization of loam with calcined clay and potassium hydroxide – calorimetric background study N2 - The low calcination temperature for clays (600° C) and a low CO2 footprint compared to cement make them an interesting material. To find a stabilization method for loam using calcined clays, activation by alkalis was necessary. Therefore (and to keep the mixture environmentally friendly) KOH was used as alkali activator. It could be proven that the alkali activated polymer enhances water resistance of the loam mixture. T2 - First International RILEM Conference on Earthen Construction Fundamentals and Applications for a Circular Economy CY - Paris, France DA - 18.03.2022 KW - Loam KW - Alkali activation PY - 2022 SP - 44 EP - 47 CY - Paris AN - OPUS4-56393 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Baloh, P. A1 - Bauer, L. A1 - Bendová, A. A1 - Čermák, P. A1 - Fellner, K. A1 - Ghanathe, M. A1 - Hernández Alvarez, O. E. A1 - Hricov, Š. A1 - Jochum, J. K. A1 - Kotvytska, L. A1 - Kumar, S. A1 - Labh, A. A1 - Machovec, P. A1 - Pauw, Brian Richard A1 - Ramszová, K. A1 - Walz, E. A1 - Wild, P. T1 - An exercise in open data: Triple axis data on Si single crystal N2 - Efforts are rising in opening up science by making data more transparent and more easily available, including the data reduction and evaluation procedures and code. A strong foundation for this is the F.A.I.R. principle, building on Findability, Accessibility, Interoperability, and Reuse of digital assets, complemented by the letter T for trustworthyness of the data. Here, we have used data, which was made available by the Institute Laue-Langevin and can be identified using a DOI, to follow the F.A.I.R.+T. principle in extracting, evaluating and publishing triple axis data, recorded at IN3. KW - Open data KW - Neutron diffraction KW - Analysis KW - Open science PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-562257 DO - https://doi.org/10.48550/arXiv.2010.12086 SN - 2331-8422 SP - 1 EP - 4 PB - Cornell University CY - Ithaca, NY AN - OPUS4-56225 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bernhardt, Y. A1 - Császár, L. A1 - Dengiz, N. A1 - Fuchs, M. A1 - Gaal, Mate A1 - Gautzsch, T. A1 - Gohlke, Dirk A1 - Hahn-Jose, T. A1 - Heckel, Thomas A1 - Hillger, W. A1 - Hufschläger, Daniel A1 - Ilse, D. A1 - Kiel, M. A1 - Kornely, M. A1 - Labud, P. A. A1 - Marhenke, T. A1 - Schubert, F. A1 - Sommerhuber, R. A1 - Steinhausen, R. A1 - Szewieczek, A. A1 - Wachter, L. A1 - Waschkies, T. T1 - Characterization and verification of air-coupled ultrasonic probes N2 - This guideline was drafted following and complementing the norm ISO 22232-2:2020(E) to include air-coupled ultrasonic transducers. This document specifies the characteristics of probes used for non-destructive air-coupled ultrasonic testing with center frequencies above 20 kHz, with focusing or without focusing means. KW - Air-coupled ultrasound KW - Ultrasonic testing KW - Guideline KW - Probe KW - Characterization PY - 2022 SN - 978-3-947971-26-8 VL - Guideline US 08 SP - 1 EP - 23 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin ET - Edition September 2022 AN - OPUS4-56228 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Vogel, Christian A1 - Simon, Franz-Georg A1 - Scholz, Philipp T1 - The chemical state of antimony and vanadium species in municipal solid waste incineration bottom ash N2 - Due to the large quantity as residual mineral waste, municipal solid waste incineration - bottom ash (MSWI-BA) is an interesting secondary raw material that can be utilized for road construction. However, leaching of chloride, sulfate and potentially hazardous heavy metals from MSWSI-BA into the environment may cause problems in utilization of it in civil engineering. In a previous study, we performed a long-term leaching test of MSWI-BA in a lysimeter for almost six years to investigate the efficiency of the treatment process on the release of hazardous substances. While concentrations of chloride, sulfate and the majority of the heavy metals started to decrease rapidly with progressive liquid-to-solid ratio (L/S), the ecotoxic hazardous elements antimony (Sb) and vanadium (V) behaved differently. To unravel these unusual release behaviors and the oxyanion-formation of Sb and V we will apply HERFD-XANES spectroscopy to analyze their chemical state. KW - Bottom ash KW - Antimony KW - Vanadium KW - XANES PY - 2023 DO - https://doi.org/10.15151/ESRF-ES-1020936484 PB - European synchroton Radiation Facility ESRF CY - Grenoble AN - OPUS4-56875 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Schrimmer, Peter T1 - Profilverformung und Betriebsverhalten von Keilriemen N2 - Ziel der vorliegenden Arbeit war es, die Profilverformung von Keilriemen bei verschiedenen Beanspruchungen zu untersuchen und die Auswirkungen dieser Profilverformung auf das Betriebsverhalten der Riemen zu erforschen. Die Untersuchungen wurden an Normal- und Schmalkeilriemen handelsüblicher Ausführung, vorwiegend Profil 17 und SPB, durchgeführt. Nur in Ausnahmefällen wurde für Vergleichszwecke zur Charakterisierung eventueller besonderer Verhaltensweisen auf Sonderanfertigungen entsprechender Profilgrößen zurückgegriffen. Sowohl auf theoretischem als auch auf experimentellem Wege wurden zunächst Untersuchungen zur Kennzeichnung des Verformungsverhaltens von Keilriemen bei verschiedenen Beanspruchungszuständen durchgeführt und der Einfluß der Profilverformung auf die Lage des Riemens in der Rille sowie daraus folgend eine Normalspannungsverteilung ermittelt. Als Ergebnis zeigte sich, daß jeder Riemen unabhängig von seinem Aufbau eine lediglich in ihrer Lage vom Riemenaufbau abhängige Breite besitzt, die bei allen Beanspruchungszuständen unverändert bleibt. Diese sog. Wirkbreite ist gewissermaßen die Drehebene bei der im Wesentlichen von der Biegung (Krümmung) abhängigen Profilverformung. Eine rein rechnerische Bestimmung der Lage der Wirkebene ist unter bestimmten Voraussetzungen mit ausreichender Genauigkeit möglich. Gegenstand weiterer intensiver Untersuchungen war das Elastizitätsverhalten der Proben bei allen praktisch vorkommenden Beanspruchungszuständen. Mit Rücksicht auf den inhomogenen Aufbau des Keilriemens aus verschiedenen Werkstoffen wurde u.a. die Querelastizität des Profils durch schichtweises Vermessen bestimmt und diese Ergebnisse mit solchen aus Versuchen am Querschnitt verglichen. Für die Berechnungen wurden z.T. entsprechend abgewandelte Modellvorstellungen aus der Theorie der Berechnung von glasfaserverstärkten Kunststoffen herangezogen. Die Elastizitätsmodulwerte bei Zugbeanspruchung wurden mit Hilfe geeigneter Proben ebenfalls für die einzelnen Aufbauelemente getrennt und auch für den Gesamtriemen berechnet. Damit wurden Angaben über die Anteile der von den Aufbauelementen übernommenen Spannungen an der Gesamtspannung und über das relative Dehnungsverhalten der Werkstoffe möglich. Angaben zur Biegeelastizität wurden im Hinblick auf diesbezügliche Elastizitätsmodulwerte nur auf eine Literaturrecherche beschränkt, jedoch wurden die durch Biegung auf die Scheibenflanken wirkenden Zusatzkräfte mit Hilfe einer eigens hierfür geschaffenen Vorrichtung ermittelt. Umfangreiche Untersuchungen sowohl theoretischer als auch experimenteller Art waren dem Verhalten des elastischen Umschlingungsmittels in der Keilrille gewidmet. Dabei wurde auf der linearen Zugkraft-Einwanderungstheorie nach 0. LUTZ und den Erweiterungen von K.D. SCHLUMS aufbauend eine modifizierte, nichtlineare Einwanderungstheorie gefunden. Die Nichtlinearität zwischen Zugkraft und Einwanderung wurde auch in der inzwischen erschienenen Habilitation von SCHLUMS bestätigt. Beide nichtlinearen Ansätze unterscheiden sich prinzipiell voneinander. In einer Diskussion wird dargelegt, daß beide Ansätze jedoch ähnliche Aussagen ermöglichen. Ferner werden die von der Theorie nicht oder nur unvollständig erfaßten Einflußgrößen, wie Längsdehnung und Winkelverformung, erörtert. Die Ermittlung der Keilriemenlänge wurde lediglich im Hinblick auf ihre Bedeutung beim Zusammenstellen von Riemensätzen für Mehrstrangantriebe behandelt. Schließlich mußten Leistungs- und Lebensdauerversuche zeigen, welche Auswirkungen Profilverformungen auf diese beiden, das Betriebsverhalten kennzeichnenden, Größen haben werden. Dabei ergaben sich infolge unterschiedlicher Keilwinkel von Riemen und Rille eindeutige Einbußen in der übertragbaren Leistung. Die wegen der gleichen Ursachen vermutete Verminderung der Lebensdauer trat nicht in dem erwarteten Umfang auf. Die Abweichungen in den geometrischen Maßen bewirkten vornehmlich eine Vergrößerung des Streubereiches und verschlechterten damit die Aussagesicherheit. In Bezug auf das Verhalten von Mehrstrangantrieben wurde versucht, eine Abschätzung der Auswirkung geometrischer Riemen- und Scheibenfehler sowie elastischer Unvollkommenheiten der Riemen auf Leistungsübertragung und Lebensdauer vorzunehmen. Im Gegensatz zu den sehr umfangreichen Versuchen mit Einstrangantrieben mußten Versuche hier mit Rücksicht auf die mengen- und leistungsmäßig begrenzte Maschinenkapazität auf Stichproben beschränkt bleiben. KW - Profilverformung KW - Betriebsverhalten KW - Keilriemen PY - 1971 SP - 1 EP - 225 PB - Technische Universität Carolo Wilhelmina CY - Braunschweig AN - OPUS4-56937 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Zencker, Uwe A1 - Simbruner, Kai A1 - Völzke, Holger T1 - Entwicklung eines bruchmechanischen Berechnungsansatzes zur Beschreibung des Festigkeitsverhaltens von Brennstabhüllrohren bei längerfristiger Zwischenlagerung (BRUZL) N2 - Es werden Methoden zur sicherheitstechnischen Bewertung des mechanischen Verhaltens von Brennstabhüllrohren entwickelt, um sprödes Versagen in Belastungsszenarien nach längerfristiger trockener Zwischenlagerung zu verhindern. Unbestrahlte Brennstabhüllrohrsegmente aus der Zirkoniumlegierung ZIRLO® wurden hydriert und thermomechanischen Behandlungen unterzogen, um Hüllrohrmaterial durch Ausscheidung radialer Hydride zu verspröden. Die Proben mit radialen Hydriden wurden im Ring Compression Test (RCT) bei Raumtemperatur untersucht. Bereits bei kleinen Probenverformungen wurden abrupte Kraftabfälle mit instabiler Rissausbreitung durch das Netzwerk radialer Hydride beobachtet. Die Risslängen erreichten in einigen Fällen bis zu 90 % der Wanddicke. Der mikromechanische Versagensmechanismus ist Quasi-Spaltbruch in den Hydriden und Porenbildung, -wachstum und -vereinigung in der Zirkoniummatrix an den duktilen Brücken zwischen benachbarten Hydriden. Es wurde ein Finite-Elemente-Modell des Ring Compression Tests erstellt, um das Versagensverhalten zirkoniumbasierter Legierungen mit radialen Hydriden im RCT zu analysieren. Die Fließkurve für das elastisch-plastische Materialmodell des Matrixmaterials wurde durch eine inverse Finite-Elemente-Analyse ermittelt. Kohäsivzonenmodelle wurden benutzt, um die plötzlichen Kraftabfälle zu reproduzieren. Es wurde ein mikromechanisches Modell mit statistisch generierten Matrix-Hydrid-Verteilungen entwickelt, das zwischen sprödem Versagen entlang der Hydride und duktilem Versagen der Zirkoniummatrix in der Kohäsivzone unterscheidet. Für das jeweilige Materialverhalten wird ein lokales zweiparametriges Versagenskriterium auf Grundlage der Kohäsionsfestigkeit und der Separationsenergie bei einer festgelegten Form des Kohäsivgesetzes vorgeschlagen. Geeignete Kohäsivparameter lassen sich mit einer inversen Finite-Elemente-Analyse des Versagensverhaltens von hydrierten Proben im Ring Compression Test bestimmen. In den Simulationen lag der Schwerpunkt auf dem ersten Kraftabfall. Die Berechnungsergebnisse stimmen gut mit den RCT-Ergebnissen überein. Es konnte gezeigt werden, dass die Rissinitiierung und -ausbreitung stark von der speziellen Anordnung der radialen Hydride und Matrixbrücken in der Bruchzone abhängt. Die numerische Modellbildung wurde an Versuchen mit bestrahlten Proben aus der Zirkoniumlegierung M5® validiert. KW - Zwischenlagerung KW - Brennstabhüllrohr KW - Versagensmechanismus KW - Kohäsivzonenmodell KW - Ring Compression Test PY - 2022 SP - 1 EP - 106 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-56853 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Friedrich, Alexander T1 - Simulation data for eddy current rail testing - simulation accuracy and evaluation uncertainty quantification N2 - This dataset serve to quantify the simulation error and the evaluation uncertainties in the context of eddy current rail testing. It was obtained during the AIFRI project (Artificial Intelligence for Rail Inspection) with the Faraday software by INTEGRATED Engineering Software, using its BEM Solver. KW - Non-destructive testing KW - Eddy current testing KW - Eddy current simulstion PY - 2024 DO - https://doi.org/10.5281/zenodo.13970374 PB - Zenodo CY - Geneva AN - OPUS4-61470 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Langer, Carlotta A1 - Georgie, Yasmin Kim A1 - Porohovoj, Ilja A1 - Hafner, Verena Vanessa A1 - Ay, Nihat T1 - Analyzing Multimodal Integration in the Variational Autoencoder from an Information-Theoretic Perspective N2 - Human perception is inherently multimodal. We integrate, for instance, visual, proprioceptive and tactile information into one experience. Hence, multimodal learning is of importance for building robotic systems that aim at robustly interacting with the real world. One potential model that has been proposed for multimodal integration is the multimodal variational autoencoder. A variational autoencoder (VAE) consists of two networks, an encoder that maps the data to a stochastic latent space and a decoder that reconstruct this data from an element of this latent space. The multimodal VAE integrates inputs from different modalities at two points in time in the latent space and can thereby be used as a controller for a robotic agent. Here we use this architecture and introduce information-theoretic measures in order to analyze how important the integration of the different modalities are for the reconstruction of the input data. Therefore we calculate two different types of measures, the first type is called single modality error and assesses how important the information from a single modality is for the reconstruction of this modality or all modalities. Secondly, the measures named loss of precision calculate the impact that missing information from only one modality has on the reconstruction of this modality or the whole vector. The VAE is trained via the evidence lower bound, which can be written as a sum of two different terms, namely the reconstruction and the latent loss. The impact of the latent loss can be weighted via an additional variable, which has been introduced to combat posterior collapse. Here we train networks with four different weighting schedules and analyze them with respect to their capabilities for multimodal integration. KW - Multimodal Integration KW - Variational Autoencoder KW - Information Theory KW - Posterior Collapse PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-616420 DO - https://doi.org/10.48550/arXiv.2411.00522 SP - 1 EP - 17 PB - Cornell University CY - Ithaca, NY AN - OPUS4-61642 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schultheiß, Annika L. A1 - Kruschwitz, Sabine A1 - Wilsch, Gerd A1 - Bogner, Andreas A1 - Patel, Ravi T1 - Lessons learnt on quantiative spatial chloride analysis using libs and µXRF N2 - Understanding chloride ingress is crucial in the context of the durability of concrete structures against corrosion. Techniques such as Laser-Induced Breakdown Spectroscopy (LIBS) and Micro X‑ray Fluorescence (µXRF) can provide a 2D representation of chloride ingress. However, obtaining quantitative data from such techniques is not a trivial task. In this study, we focus on factors such as sample preparation, measurement settings, calibration strategy, and post-processing of results which directly affect the outcome of the experiments but are rarely discussed in the literature. T2 - Rilem Annual Week 2024 CY - Toulouse, Frankreich DA - 25.08.2024 KW - Durability KW - Chloride ingress KW - LIBS KW - µXRF KW - Nondestructive testing KW - Imaging PY - 2024 SP - 1 EP - 9 AN - OPUS4-61664 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hahn, Sarah-K. A1 - Tschirschwitz, Rico A1 - Amano, Kofi Owusu Ansah A1 - Gimadieva, Elena A1 - Krause, Ulrich T1 - A Study on Thermal Runaway Propagation in Battery Modules Assembled from Pouch Cells N2 - Thermal runaway reactions were studied in arrangements from single battery cells with energy capacities of 2.5 Ah (9.25 Wh) to battery modules up to 6.85 kWh. All cells were pouch cells of the Li-ion NMC type and the modules were composed of such. Abuse was triggered either by overcharging or thermally by attaching a heat source (heating plate or glow plug) to the cells. Experiments with single cells or assemblies of two to four cells were undertaken in closed autoclaves. Samples of the gas released from the cells during the runaway were extracted and analysed using a Fourier-transformed infrared spectrometer (FTIR). In some experiments pressure peaks up to 7 bar (g) were observed which could not be explained by the gas release alone. Obviously, secondary explosions took place. Thermal runaway propagation was studied with and without an insulation layer between the battery cells. Several materials and combinations of them were tested as insulations: hollow glass spheres (Pyrobubbles®), phase change materials (PCM) and intumescent materials. Experiments showed that already layers of 10 to 20 mm of insulation effectively prevented the propagation of a thermal runaway. In addition to the experiments, a mathematical model was developed for studying numerically the heat transfer through arrangements of multiple battery cells and also the effect of insulation layers. This model was implemented into the commercial finite-element software package COMSOL Multiphysics®. The simulations confirmed the experimental findings that already quite thin insulation layers between cells or modules effectively delay or even suppress the propagation of the thermal runaway. T2 - EUSAS conference "Addressing the Fire Risks of Electromobility" CY - Frankfurt am Main, Germany DA - 10.05.2023 KW - Thermal Runaway KW - Consequences KW - Electrical Energy Storage KW - Gas release KW - Lithium-ion battery PY - 2024 UR - https://eusas.eu/publications/eusas-journals VL - 15 SP - 43 EP - 50 PB - EUSAS e.V. (European Society for Automatic Alarm Systems e.V.), Universität Duisburg-Essen, Dept. Nachrichtentechnische Systeme CY - Duisburg AN - OPUS4-61598 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weichert, Dorina A1 - Kister, Alexander A1 - Houben, Sebastian A1 - Link, Patrick A1 - Ernis, Gunar ED - Kiyavash, Negar ED - Mooij, Joris M. T1 - Robust Entropy Search for Safe Efficient Bayesian Optimization N2 - The practical use of Bayesian Optimization (BO) in engineering applications imposes special requirements: high sampling efficiency on the one hand and finding a robust solution on the other hand. We address the case of adversarial robustness, where all parameters are controllable during the optimization process, but a subset of them is uncontrollable or even adversely perturbed at the time of application. To this end, we develop an efficient information-based acquisition function that we call Robust Entropy Search (RES). We empirically demonstrate its benefits in experiments on synthetic and real-life data. The results show that RES reliably finds robust optima, outperforming state-of-the-art algorithms. T2 - UAI 2024 CY - Barcelona, Spain DA - 15.07.2024 KW - Bayesian Optimization KW - Gaussian process KW - Active learning PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-613523 UR - https://proceedings.mlr.press/v244/weichert24a.html SN - 2640-3498 VL - 244 SP - 3711 EP - 3729 PB - Proceedings of Machine Learning Research AN - OPUS4-61352 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Melzer, Michael ED - Deschermeier, Regina ED - Bünger, Lars ED - Schüür, Jens T1 - Good practice für digitale Kalibrierscheine von Temperatur- und Feuchtemessgrößen N2 - Der digitale Kalibrierschein (DCC) enthält alle Informationen eines herkömmlichen Kalibrierscheins in maschinenlesbarer und möglichst auch -interpretierbarer Form, um eine Automatisierung des Qualitätsmanagements und der metrologischen Rückführbarkeit in den Laboren und im industriellen Messwesen zu ermöglichen. Neben den allgemeinen Anforderungen, z.B. aus ISO/IEC 17025, gibt es spezifische Anforderungen bezüglich der Messgrößen und der Kalibrierverfahren, die auch in digitalen Ergebnisberichten erfüllt sein müssen. Innerhalb des DKD Fachausschusses für Temperatur und Feuchte werden derzeit good practice Empfehlungen erarbeitet, um zu definieren, wie genau diese Anforderungen im Rahmen des DCC erfüllt werden sollten. Anhand der Temperaturskala und des Kalibriermediums werden zwei dieser good practices hier beispielhaft erläutert. Außerdem wird eine Übersicht über die bereits definierten spezifischen refType-Attribute für Temperatur- und Feuchtemessgrößen gegeben. T2 - TEMPERATUR 2024 CY - Berlin, Germany DA - 05.06.2024 KW - Digital Calibration Certificate KW - Digital certificates KW - Digital Metrology KW - QI-Digital KW - Calibration PY - 2024 UR - https://www.temperatur.ptb.de/startseite SP - 145 EP - 151 AN - OPUS4-61923 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Proll, Günther A1 - Seidel, Michael A1 - Schneider, Rudolf T1 - Moderne bioanalytische Methoden für die schnelle Quantifizierung von Mikroschadstoffen und Pathogenen in Wasser N2 - Analytische Methoden für die Quantifizierung von Mikroschadstoffen (Synonym für Spurenstoffe) und Pathogenen im Wasser sind eine Grundvoraussetzung für die Umsetzung des Ziels Nr. 6 für Nachhaltige Entwicklung der UN, weltweit sauberes Wasser zur Verfügung zu stellen. Dafür sind schnelle, einfach zu bedienende und kostengünstige Überwachungssysteme notwendig. Antikörperbasierte Biosensoren haben das Potential, z.B. die Eliminationsleistung bezüglich kleiner organischer Moleküle durch die vierte Reinigungsstufe von Kläranlagen vor Ort zu überwachen. Darüber hinaus kommt modernen bioanalytischen Verfahren bei der Quantifizierung von Pathogenen eine immer wichtigere Rolle zu. Neben einer Bestandsaufnahme zu diesen Themen ist es das Ziel dieses Beitrags, die Anwendungsbarrieren von Biosensoren für die Wasseranalytik von Mikroschadstoffen abbauen zu helfen und die Vorzüge moderner bioanalytischer Methoden für die Quantifizierung von Pathogenen aufzuzeigen. KW - Biosensoren KW - Antikörper KW - Abwasser PY - 2024 SN - 1618-3258 VL - 30 IS - 2 SP - 66 EP - 70 PB - GDCh CY - Weinheim AN - OPUS4-60233 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Tschirschwitz, Rico A1 - Bernardy, Christopher T1 - Aufbau eines Großversuchsstandes sowie Realisierung von Brandversuchen mit elektrischen Energiespeichern im Bereich bis 500 kWh - Schlussbericht zum Teilvorhaben BAM, Teil I: Kurzbericht N2 - Der Abschlussbericht stellt die wesentlichen Arbeitsschritte und Ergebnisse des Teilvorhabens der BAM im BMBF-Vorhaben SEE-2L vor. Im Rahmen dieses Vorhabens wurde auf dem Testgelände Technische Sicherheit (BAM TTS) ein Großversuchsstand für das thermische Durchgehen von Lithium-Batterien auf Modul- und Batterieebene entwickelt und aufgebaut. Im Zuge des Projektes konnte eine erste Versuchsserie zu den Auswirkungen des thermischen Durchgehens von Batteriemodulen durchgeführt werden. Der Abschlussbericht umfasst zwei Teile, im Teil I den Kurzbricht und im Teil II die eingehende Darstellung. KW - Thermisches Durchgehen KW - Auswirkungsbetrachtungen KW - Elektrische Energiespeicher KW - Stationäre Energiespeicher KW - Lithium-Ionen-Batterie PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-600676 DO - https://doi.org/10.2314/KXP:1887873864 N1 - Das Projekt SEE-2L ist ein drittmittelfinanziertes Verbundvorhaben des BMBF, Förderkennzeichen 13N15493, Projektlaufzeit 01.02.2021 - 30.04.2023. SP - 1 EP - 20 PB - Technische Informationsbibliothek (TIB) CY - Hannover AN - OPUS4-60067 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hahn, Sarah-K. A1 - Saupe, Alexander A1 - Tschirschwitz, Rico A1 - Bernardy, Christopher A1 - Janßen, Marvin A1 - Amano, Kofi Owusu Ansah A1 - Krause, Ulrich T1 - Sicherheit elektrochemischer Energiespeicher – Ergebnisse aus dem Projekt SEE-2L N2 - Die Transformation der Energienutzung von konventionellen zu erneuerbaren Quellen führt dazu, dass zukünftig mehr Energie effizient zwischengespeichert werden muss. Eine Möglichkeit der elektrochemischen Zwischenspeicherung bieten Lithium-Ionen-Batterien. Hierfür können ausgemusterte Automobilantriebsbatterien verwendet werden. Erfüllen sie die hohen Anforderungen des mobilen Bereichs nicht mehr, haben sie oftmals noch eine ausreichende Kapazität und Leistungsfähigkeit für die stationäre Zwischenspeicherung. Neben der Verwendung der Batterien im größeren Maßstab, z.B. bei Energieversorgern, werden durch den vermehrten Einsatz von Photovoltaik-Anlagen in Ein- und Mehrfamilienhäusern verstärkt Zwischenspeicher für Privathaushalte nachgefragt. Dies birgt auch für Einsatzkräfte neue Herausforderungen in der Gefahrenabwehr. Im vom Bundesministerium für Bildung und Forschung (BMBF) geförderten Verbundprojekt „SEE-2L – Sicherheit elektrochemischer Energiespeicher in Second Life Anwendungen“ wurden Versuche mit Second Life Modulen durchgeführt. Verbundpartner im Projekt waren neben der vfdb die Otto-von-Guericke-Universität Magdeburg und die Bundesanstalt für Materialforschung und -prüfung. Zudem war das Institut der Feuerwehr Nordrhein-Westfalen eingebunden. Die durchgeführten Versuche bilden eine Grundlage für die Einordnung der Batteriespeicher, z.B. aus Sicht des baulichen Brandschutzes, zur Methodik der Brandbekämpfung oder zur Risikobewertung hinsichtlich der Prozess- und Anlagensicherheit. Im Beitrag werden die Versuchsergebnisse vorgestellt und Ansätze für deren Anwendung gezeigt. Um die gewonnenen Erkenntnisse zu vermitteln, wurde im Projekt zudem ein Schulungskonzept für Einsätze mit Lithium-Ionen-Technologien erarbeitet, das im Beitrag präsentiert wird. Es besteht aus theoretischen und praktischen Anteilen, sodass bei den Feuerwehren praxisnah aus- bzw. fortgebildet werden kann. T2 - 70. Jahresfachtagung der vfdb CY - Magdeburg, Deutschland DA - 06.05.2024 KW - Auswirkungsbetrachtungen KW - Elektrische Energiespeicher KW - Lithium-Ionen-Batterie KW - Stationäre Energiespeicher KW - Thermisches Durchgehen PY - 2024 SN - 978-3-9360-5038-7 SP - 645 EP - 657 PB - vfdb, Vereinigung zur Förderung des Deutschen Brandschutzes e.V. CY - Münster AN - OPUS4-60068 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gaal, Mate A1 - Wernicke, Pascal A1 - Hufschläger, Daniel T1 - Pulskompression für luftgekoppelte Ultraschallprüfung mit Ferroelektret- und thermoakustischen Wandlern N2 - Die größten Vorteile der luftgekoppelten Ultraschallprüfung sind: die berührungslose Prüfung und der Verzicht auf ein flüssiges Koppelmittel. Allerdings weisen die meisten luftgekoppelten Prüfszenarien ein sehr geringes Signal-zu-Rausch-Verhältnis (SNR) auf und die Pegel, die von luftgekoppelten Ultraschallwandlern realisiert werden, sind um mehrere Größenordnungen kleiner. Da diese Herausforderung auch in anderen Disziplinen wie bspw. der Radartechnik existiert und dort ebenfalls eine entscheidende Rolle spielt, wurde die dort eingesetzte Pulskompression auf die physikalischen Gegebenheiten der luftgekoppelten Ultraschallprüfung angepasst und angewandt. Dieser Beitrag präsentiert die Ergebnisse von zwei Versuchsaufbauten: 1) ein thermoakustischer Sender und ein optisches Mikrofon und 2) ein Paar Ferroelektret-Wandler als Sender und Empfänger. Aufgrund der physikalischen Randbedingungen wurden unipolare Kodierungen verwendet. Die Verwendung von unipolaren Kodes zur Modulation der Anregungssignale stellt dabei eine neue Methode dar, die so die Pulskompression für Ferroelektret- und thermoakustische Wandler ermöglichen soll. Die Anwendung der Pulskompression auf die Kombination aus thermoakustischem Sender und optischem Mikrofon konnte das Signal-zu-Rausch-Verhältnis um bis zu 15 dB und für die Ferroelektret-Wandler um bis zu 23 dB erhöhen. T2 - DAGA CY - Hannover, Germany DA - 19.3.2024 KW - Pulskompression KW - Luftgekoppelter Ultraschall KW - Ferroelektrete KW - Thermoakustik PY - 2024 UR - https://pub.dega-akustik.de/DAGA_2024/ SP - 1580 EP - 1583 AN - OPUS4-60169 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kowalski, Kurt A1 - Hulshoff, S.J. A1 - Ströer, P. A1 - Withag, J. A1 - Genot, A. A1 - Morgans, A.S. A1 - Bake, Friedrich A1 - Venner, K. A1 - Sanders, M.P.J. A1 - Hirschberg, Lionel T1 - Entropy-patch choked-nozzle interaction: quasi-steady-modeling-regime limits probed N2 - Indirect combustion noise due to the interaction of flow inhomogeneities with a choked combustion-chamber exit is an important cause of combustion instability in solid rocket motors. Moreover, it is believed to be an issue in electrical-power generation turbines and aero-engines. If these flow inhomogeneities are essentially characterized by the fluid having a locally appreciablydifferent thermodynamic state, the acoustic response engendered by its interaction with the combustion-chamber exit is commonly referred to as entropy noise. In this paper, dedicated numerical-simulation results of entropy-patch choked-nozzle interactions are presented. Two types of entropy patches were considered: rectangular slugs and circular spots. Moreover, analytical-model-based analysis, of said simulation results, is presented. Based on said analysis, the authors posit the existence of three modeling regimes: the quasi-steady-modeling regime, the blended-physical-effects regime, and the inertial-modeling regime. T2 - 30th AIAA/CEAS Aeroacoustics Conference (2024) CY - Rome, Italy DA - 04.06.2024 KW - Entropy-Nozzle Interaction KW - Indirect Combustion Noise KW - Entropy Noise PY - 2024 SN - 978-1-62410-720-7 DO - https://doi.org/10.2514/6.2024-3113 SP - 1 EP - 23 AN - OPUS4-60174 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quercetti, Thomas A1 - Feldkamp, Martin A1 - Gleim, Tobias A1 - Musolff, Andre A1 - Werner, Jan A1 - Wille, Frank T1 - Enhancement of the BAM Fire Test Stand for Testing a Large Transport Package for Radioactive Materials N2 - Packages for the transport of spent nuclear fuel are designed to endure severe accidents. To obtain approval, these transport packages must adhere to the specification-based criteria of the international transport regulations SSR-6 of the International Atomic Energy Agency (IAEA). To ensure compliance with these requirements, specific mechanical and thermal tests need to be addressed with respect to the package type. Typically, SSR-6 prescribes a mechanical test followed by a thermal fire test as part of different testing scenarios. To approve the latter test of the sequence, BAM performs calorimeter tests in advance with so-called fire reference packages for characterizing the actual fire and its impact on the package to be tested. Packages are designed with different geometry sizes depending on their purpose. For previous tests, the implemented test setups in the fire test stand were sufficiently dimensioned and could cover all requirements in this respect. However, to cover additional testing needs in the future, BAM is expanding the test setup for the purpose of testing significantly larger packages. In previous test setups one ring burner for propane surrounding the test specimen was sufficient. The limiting size in this configuration was the design height of the transport package to be tested. According to the thermal test of the IAEA-Regulations [1], a 30-minute fully engulfing 800°C pool fire or an equally severe fire, e.g., propane gas fire, must be applied to the transport package. Possible adjustments such as nozzle cross-section and propane mass flow can be adjusted to a certain extent. Further modifications, to cover significantly higher and larger packages all-around with a fully engulfing fire, must be accomplished with an additional, second burner ring. Both burner rings had the same dimensions and were mounted on top of each other at different heights to create a significantly larger volume of fire that completely engulfs the package including its impact limiter. To meet the IAEA regulatory boundary conditions, the enhanced fire test stand with the second burner ring is tested with a large fire reference package and will then be used for real-size transport packages after all parameters are successfully met. This fire reference package represents the external geometry of a generic transport cask for radioactive material and is equipped with numerous temperature sensors to record temperature curves at the interior wall surfaces. T2 - RAMTrans 2024 CY - London, United Kingdom DA - 14.05.2024 KW - Fire testing KW - Full-scale KW - Transport package PY - 2024 SP - 1 EP - 7 AN - OPUS4-60253 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lu, Xin A1 - Hicke, Konstantin A1 - Krebber, Katerina T1 - Distributed fiber optic sensing for monitoring of underground facilities N2 - Distributed fiber optic sensing (DFOS) technique is a promising and robust non-destructive testing tool that can seamlessly acquire environmental conditions over large scales. Therefore, it has found extensive applications in structural health monitoring. Its appeal for monitoring underground facilities lies in the intrinsic properties of the optical fiber, such as immunity to magnetic interference, small size, chemical inertia, etc. This paper provides a concise overview of DFOS applications in underground facility monitoring. Following a brief introduction to the workingbnprinciple of the DFOS technique, various examples are provided to demonstrate how distributed fiber sensors contribute to monitoring underground facilities. The paper presents unpublished field test results with an emphasis in the energy sector, including monitoring gas storage facilities, geothermal reservoir exploration, and ground movement detection. Furthermore, the paper identifies several directions for enhancing the DFOS system. T2 - SPIE Photonics Europe CY - Strasbourg, France DA - 07.04.2024 KW - Structure health monitoring KW - Geothermal borehole KW - Distributed fiber optic sensing KW - Ground movement KW - Leakage detection PY - 2024 DO - https://doi.org/10.1117/12.3023571 SN - 0277-786X VL - 13001 SP - 1 EP - 10 PB - SPIE AN - OPUS4-60384 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hirsch, Philipp Daniel A1 - Kunji Purayil, Sruthi Krishna A1 - Lecompagnon, Julien A1 - Hassenstein, Christian A1 - Ziegler, Mathias T1 - Robotergestützte 3D-Scans und Laserthermografie zur Prüfung an komplexen Bauteilen auf Risse N2 - Die Integration von Automation und Robotik in die Prüfprozesse ermöglicht die Untersuchung komplexer Bauteile. Diese Studie präsentiert die robotergestützte Laserthermografie, um Risse in solchen Bauteilen zu identifizieren und analysieren. Diese Technik ermöglicht die automatisierte Rissprüfung welche im Vergleich zur Farbeindringprüfung auf viele, meist manuelle, Arbeitsschritte sowie die notwendigen Chemikalien verzichtet. Zusätzlich wird ein automatisiertes Einscannen der Bauteile mithilfe eines Linienscanners vorgestellt. Dieser Schritt ermöglicht eine detaillierte 3D-Rekonstruktion der Bauteilgeometrie und ermöglicht eine einfache Korrektur von Abweichungen in der Bauteilaufnahme und eröffnet Möglichkeiten zur adaptiven Bahnplanung bei Bauteilverformungen. Die Rückprojektion der gefundenen Risse auf die Oberfläche des Bauteils kann automatisiert erfolgen. Dieser Schritt erlaubt nicht nur die Identifikation der Risse, sondern auch eine genauere Analyse ihrer Geometrie und Lage am Bauteil. Die Kombination von robotergestützter Laserthermografie, automatisiertem 3DScanning und Rückprojektion der Risse auf die Bauteiloberfläche eröffnet neue Möglichkeiten in der zerstörungsfreien Prüfung von komplexen Bauteilen und erweitert damit mögliche Anwendungsfelder. T2 - Jahrestagung der Deutschen Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) 2024 CY - Osnabrück, Germany DA - 06.05.2024 KW - ZFP4.0 KW - Automatisierung KW - Thermografie KW - Laser KW - Roboter PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-604811 UR - https://www.ndt.net/?id=29520 VL - 182 SP - 1 EP - 8 PB - NDT.net AN - OPUS4-60481 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schlegel, Moritz-Caspar A1 - McAlister, Catriona A1 - Rama, Mathieu T1 - Pioneering durability in electronics - The role of standardisation in policymaking and vice versa N2 - This paper highlights the role of standardisation in enabling greener electronics in the EU. It presents an analysis of the evolving landscape of material efficiency standardization, the majority of which has been undertaken in the framework of the European Ecodesign Directive, soon to be repealed by the Ecodesign for Sustainable Products Regulation. The impending policy shift will include a very broad extension of product scope, a strengthening of the way in which material efficiency aspects are addressed, and wider potential for product labelling. During the stakeholder consultation process, the European Commission announced that the durability of products would be one of the major topics in the new regulatory approach - hence the specific focus of this paper on durability scoring. The paper first examines the policy and standardization context, and then provides an overview of material efficiency indexes and scoring systems currently in place or being developed. It highlights where standardization is following policymaking, and where standardization is paving the way for more circular products. Scoring systems and indexes could potentially be used for both (i) setting minimum requirements for products entering the EU market, and (ii) consumer labels on material efficiency aspects such as product durability that could trigger environmentally sustainable purchase decisions. Subsequently, a methodological framework for a comprehensive durability scoring system that could be developed in standards is proposed, and the potential for these to be used as a basis for product legislation is explored. Potential durability criteria are listed, divided into technical, servicerelated and further aspects. Technical aspects include external factors that influence the durability of products such as drop/shock resistance. Service-related aspects include, for example, pre-purchase information provision on battery replaceability or availability of software updates. Other aspects include for example pro. T2 - EGG+ Electronics Goes Green 2024+ CY - Berlin, Germany DA - 18.06.2024 KW - Circular Economy KW - Durability KW - Material efficiency KW - Ecodesign KW - ESPR KW - Labelling KW - Consumer PY - 2024 SN - 979-8-3503-8822-0 SP - 56 EP - 62 AN - OPUS4-60399 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Tochtrop, Christoph A1 - von Geibler, Justus A1 - Rückschloss, Jana A1 - Schlegel, Moritz-Caspar T1 - Product features: Upgraded Functionality or Sustainability Problem? An environmental assessment approach for additional product functions and its application in the case of fridge-freezers N2 - Next to primary functions, energy-related products have an increasing number of additional functions. This affects the overall environmental footprint, but the question is how? A number of European policy strategies, initiatives and measures, such as the Green Deal, the Circular Economy Action Plan,the Ecodesign Directive and the EU Energy Labelling, aim to ensure that the environmental impact of the overall product is better determined, communicated and finally reduced. A core element of these efforts is the DIN EN 4555x series of standards. However, there is currently no comprehensive and systematic classification of the additional product functions or an approach to assess the associated positive and negative environmental impacts. Therefore, we present in this study an environmental assessment approach for additional product functions and illustrate its application in the case of fridge-freezers. A key element of the life-cycle-oriented methodology is an assessment matrix to categorize and evaluate the direct, indirect and systemic impacts of products’ functions. Based on semiquantitative assessments of experts, the matrix provides an indication of how the additional function affects the overall environmental product impact as well as specific product aspects such as durability or reparability. Based on the results experts can discuss and better understand how specific functions can influence various stages of the product life cycle and how intended systemic changes or rebound effects could occur. As part of the approach, a representative survey was conducted to analyze consumers’ knowledge and information needs. Based on the results, recommendations for purchasing decisions and the consumer information were developed. This paper presents the results from the assessment of the additional functions of fridge-freezers. T2 - EGG+ Electronics Goes Green 2024+ CY - Berlin, Germany DA - 18.06.2024 KW - Circular Economy KW - ESPR KW - Material efficiency KW - Ecodesign KW - Policy making KW - Standardization KW - Consumer PY - 2024 SN - 978-3-00-079329-5 DO - https://doi.org/10.23919/EGG62010.2024.10631252 SP - 87 EP - 97 AN - OPUS4-60400 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Casperson, Ralf A1 - Friedrich, Alexander A1 - Heckel, Thomas A1 - Zhang, Tianyun T1 - Verwendung von DICONDE bei der Eisenbahn-Schienenprüfung N2 - Bei der zerstörungsfreien Prüfung verlegter Eisenbahnschienen werden die Rohdaten derzeit in proprietären Datenformaten gespeichert und auf Datenträgern zwischen den Prüfzügen und den auswertenden Stellen versendet. Die proprietären Datenformate sind in der Regel nur den Herstellern der Prüfsysteme bekannt und deren Dokumentation nicht allgemein zugänglich. Die „Standard Practice for Digital Imaging and Communication in Nondestructive Evaluation“ (DICONDE), basierend auf dem medizinischen Standard „Digital Imaging and Communication in Medicine“ (DICOM), ermöglicht es, sowohl Prüfdaten als auch Prüfergebnisse und Streckeninformationen in einem standardisierten Format zu speichern und zwischen verschiedenen Endpunkten zu übertragen. Das Poster gibt zunächst einen kurzen Überblick über die hierarchische Struktur von DICONDE und zeigt dann, wie DICONDE bei der Prüfung verlegter Eisenbahnschienen verwendet werden kann. Die geometrischen Besonderheiten (mehrere Kilometer Länge pro Prüffahrt, kurviger Streckenverlauf) stellen dabei eine besondere Herausforderung dar. Im Rahmen des mFUND-geförderten Projektes „Arteficial Intelligence for Railway Inspection (AIFRI)“, Förderkennzeichen 19FS2014C, wurde ein Vorschlag für eine Erweiterung des DICONDE-Standards für die Schienenprüfung erarbeitet und bei der ASTM eingereicht. T2 - DGZfP Jahrestagung 2024 CY - Osnabrück, Germany DA - 05.05.2024 KW - DICONDE KW - Eisenbahn KW - Schienenprüfung PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-600204 DO - https://doi.org/10.58286/29500 SP - 1 EP - 5 PB - NDT.net AN - OPUS4-60020 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baar, C A1 - Laar von, C A1 - Plarre, Rüdiger A1 - McMahon, Dino Peter T1 - Insektenmonitoring und genetisches Barcoding N2 - Die aus der Kirche in Greven entnommenen A. punctatum wiesen größere genetische Unterschiede auf als die aus der isolierten Zucht der BAM. Dies lässt vermuten, dass ein Austausch von zufliegenden oder eingeschleppten Individuen zu einer erhöhten genetischen Variabilität beiträgt. Die Ergebnisse der Sequenzanalysen vom Standort Greven zeigten, dass vier Variationen vorhanden waren. Die DNA-Barcodes aus der Datenbank NCBI (Frankreich, Finnland und Deutschland) besaßen nur SNPs, die bereits aus den Insekten der Kirche in Greven bekannt waren. Nach aktueller Datenlage für den betrachteten Genabschnitt sind diese Varianten (V2 bis V22) als repräsentativ für den mitteleuropäischen Raum anzunehmen. Potenzielle weitere Varianten lassen sich nur über eine größere Stichprobenanzahl entdecken/finden. Die Ergebnisse der Käferproben aus der isolierten Zucht der BAM sind deutlich homogener und entsprachen der Variante 1 aus Greven. Die Variante 1 wurde ebenfalls in vier französischen und einer deutschen Probe aus der NCBI-Datenbank nachgewiesen. Die Ergebnisse deuten auf zwei Hauptvariationen (Vx und V20) hin, wobei die eine (VJ homogener als die andere (V20) zu sein scheint. Da für den Räuber K. caeruleus keine Unterschiede in der COI gefunden wurden, gilt zu prüfen, ob der gewählte Genabschnitt für die Untersuchung repräsentativ ist. Dies ist mit einer höheren Probenzahl zu validieren. T2 - 32. Deutsche Holzschutztagung CY - Dresden, Germany DA - 25.04.2024 KW - Korynaetes caeruleus KW - Insektenmonitoring KW - Genetisches Barcoding KW - Anobium punctatum PY - 2024 SP - 244 EP - 252 AN - OPUS4-60027 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Barretto, T. A1 - Gentes, S. A1 - Braun, J. A1 - Averin, Anton A1 - Lecompagnon, Julien A1 - Stroncik, N. T1 - Automated non-destructive internal corrosion detection on radioactive drums (ZIKA) N2 - The aim of the ZIKA research project, funded by the BMBF funding program FORKA (FKZ:15S9446 A-C), is the automated detection of internal corrosion of radioactive drums using non-destructive testing (NDT). The newly gained findings will be combined with research results from the previous project EMOS (FKZ:15S9420), which dealt with the external damage of drums. Using NDT, internal corrosion and possible internal sources of damage can be identified before they become a safety-relevant issue. However, if internally sourced damages can be seen externally, the integrity of the damaged drum is no longer guaranteed, which has significant consequences. Therefore, early detection before integrity failure is of particular importance for interim storage facilities with low- and medium-level radioactive waste drums. T2 - Kerntechnik 2024 CY - Leipzig, Germany DA - 11.06.2024 KW - Corrosion detection KW - Non-destructive testing KW - Automated inspection system PY - 2024 SP - 1 EP - 5 AN - OPUS4-60322 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Völzke, Holger T1 - Brittle Failure Limits of Spent Fuel Claddings Subjected to Long-Term Dry Interim Storage Conditions N2 - The mechanical properties of spent fuel claddings can be adversely affected under the conditions of long-term dry interim storage, so that the failure limits may be reached in case of mechanical loads during handling or transport after storage. Pre-storage drying and the early stage of interim storage can expose the cladding to higher temperatures and higher tensile hoop stresses than those associated with in-reactor operation and pool storage. During slow cooling of a cladding tube under internal pressure, radial hydrides may precipitate in zirconium-based cladding alloys. This can lead to embrittlement of the material and sudden failure of the cladding integrity under mechanical stress. In order to prevent brittle failure, numerical methods are being developed to predict the mechanical behaviour and identify limiting conditions. Experimental investigations, numerical analyses and evaluation methods are discussed. An established experimental method for characterising cladding materials is the Ring Compression Test (RCT). Some test results on irradiated cladding tubes after operation in pressure water reactors are publicly available. However, it is helpful to carry out studies on unirradiated surrogate claddings with similar material properties to reduce the effort associated with irradiated samples in hot cells and to perform material tests with a wider range of parameters. On the basis of such experimental data, load-displacement curves have been numerically analysed for a selection of cladding materials. Radial hydrides can cause a sample to break suddenly due to fracture even at low deformation. Noticeable load drops in the RCT are caused by unstable crack propagation through the radial hydride network. The failure mechanism is quasi-cleavage in the hydrides and micro-void nucleation, growth, and coalescence in the zirconium matrix, with ductile tearing patches connecting adjacent hydrides. The cohesive zone approach was used to simulate the failure process taking into account the radial hydride morphology. The developed method can adequately describe both the deformation and failure behaviour of irradiated as well as unirradiated claddings of zirconium-based alloys with radial hydrides under RCT conditions. Limiting conditions can be expressed in terms of fracture energy and cohesive strength. T2 - IAEA International Conference on the Management of Spent Fuel from Nuclear Power Plants - Meeting the Moment CY - Vienna, Austria DA - 10.06.2024 KW - Ageing Management KW - Cladding Embrittlement KW - Extended Storage KW - Ring Compression Test KW - Spent Nuclear Fuel PY - 2024 SP - 1 EP - 10 AN - OPUS4-60323 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ronen, A. A1 - Vogel, Christian A1 - Leube, Peter A1 - Ben Efraim, R. A1 - Nir, O. A1 - Chaudhary, M. A1 - Futterlieb, M. A1 - Panglisch, S. T1 - DEFEAT-PFAS: Detection, Quantification, and Treatment of Per- and Polyfluoroalkyl Substances (PFAS) in Groundwater N2 - The research project focuses on tackling the detection, measurement, and elimination of per- and polyfluoroalkyl substances (PFAS) from polluted groundwater, with a particular emphasis on addressing short (C4-C7) and ultrashort (C1-C3) chain PFAS. Given the widespread use of PFAS in various products, they are commonly found in groundwater near industrial and military sites in Germany and Israel. Moreover, recent regulations limiting the use of long chain PFAS have led industries to shift towards shorter chain alternatives. Hence, our efforts are geared towards refining detection, quantification, and removal methods for short and ultrashort chain PFAS. In terms of detection, ww are developing passive sampling devices capable of collecting and tracking the temporal distribution of PFAS species in groundwater. This will enable us to analyze contaminations in German and Israeli groundwater using cutting-edge analytical techniques. Additionally, contaminated groundwater will undergo a two-stage treatment process aimed at concentrating the relatively low PFAS concentrations using innovative membrane technologies such as closed-circuit reverse osmosis and mixed matrix composite nanofiltration membrane adsorbers. Subsequently, the streams containing higher PFAS concentrations will be treated through coagulation, with the remaining PFAS being adsorbed onto carbonaceous nanomaterials. The outcome of this research will include the creation of advanced tools for detecting, measuring, and eliminating PFAS from polluted groundwater, while also enhancing our understanding of the scope of these contaminations. T2 - German Israeli Water Technology Status Seminar CY - Koblenz, Germany DA - 18.06.2024 KW - Ground water KW - Per- and Polyfluoroalkyl substances (PFAS) KW - Remediation PY - 2024 UR - https://indico.scc.kit.edu/event/4029/attachments/7552/12045/Proceedings_Ger-Isr-Coop_Status-Seminar-2024.pdf SP - 33 EP - 36 AN - OPUS4-60331 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simon, Franz-Georg A1 - Scholz, Philipp ED - Thiel, Stephanie ED - Thome-Kozminesky, Elisabeth ED - Antrekowitsch, Helmut ED - Pomberger, Roland ED - Firsbach, Felix T1 - Einstufung von Aschen und Schlacken aus der Abfallverbrennung im Hinblick auf die weitere Verwertung – Handlungsempfehlungen N2 - Die Einstufung von Hausmüllverbrennungsasche (IBA) als gefährlich oder nicht gefährlich nach der Gefahreneigenschaft HP14 (ökotoxisch) ist nach wie vor umstritten, da es noch keine keine allgemein anerkannten Methoden zur Bewertung gibt. Wenn die Berechnungsregeln angewendet werden sollen angewendet werden sollen, sind Kenntnisse über die chemische Zusammensetzung von IBA erforderlich. Informationen über über die chemische Zusammensetzung von IBA können mit einem Ansatz gewonnen werden, der auf der Gruppierung von Substanzen. Für IBA können vier Stoffgruppen definiert werden: 1. elementare und legierte Metalle, 2. leicht wasserlösliche Stoffe, 3. schwer lösliche Stoffe und 4. Stoffe mit starken chemischen Bindungen. Elementares und legiertes Cu und Zn sind in der IBA vorhanden und werden in der Regel als Nichteisenmetallfraktion zurückgewonnen, zumindest die größeren Partikel. Zn-Partikel, die kleiner als 1 mm sind, werden als H410 eingestuft, feine Partikel von Cu nur als H411. Die wasserlösliche Fraktion kann mit Standardauslaugungsmethoden quantifiziert werden Auslaugungsmethoden quantifiziert werden, z. B. bei einem Flüssigkeits-Feststoff-Verhältnis (L/S) von 2 oder 10 l/kg. Sowohl die Sulfate von Zn als auch von Cu gehören zu dieser Gruppe. In einer neueren Veröffentlichung wurde gezeigt, dass bei den oben genannten Metalle die ausgelaugte Menge weit unter dem Grenzwert von 1.000 mg/kg liegt, selbst wenn stöchiometrische Faktoren angewendet werden. Stoffgruppe 3 sind potenzielle H410-Stoffe. Dabei handelt es sich um Carbonate, Hydroxide und Oxide der betreffenden Elemente, die löslich sind in schwachen organischen Säuren wie Essigsäure löslich sind. Die Worst-Case-Stoffe der Gruppe 3, d. h. die Verbindungen mit den höchsten stöchiometrischen Faktoren, sind CuCO3xCu(OH)2 und ZnO. Stoffe mit starken chemischen Bindungen wie Silikate oder Sulfide sind nur löslich in starken Säuren (z.B. Königswasser) löslich und haben keinen Ökotoxizitäts-Gefahrencode. Das Mobilisierungsverhalten der relevanten Schwermetalle und damit der Gruppe der schwer schwerlöslichen Verbindungen kann mit der 4-stufigen sequentiellen Extraktion untersucht werden. Für die HP14 Einstufung könnte auch eine einstufige Extraktion ausreichend sein. Nur die Elemente Zn und Cu sind für die HP14-Einstufung der IBA von Bedeutung, da die Feststoffgehalte aller anderen Schwermetalle unterhalb des Feststoffgehalte aller anderen Schwermetalle unter der Cut-Off-Grenze von 0,1 % liegen, selbst wenn man sie in chemischen Verbindungen mit stöchiometrischen Faktoren. Im Ergebnis wurde gezeigt, dass IBA in der Regel als nicht gefährlich einzustufen ist. T2 - Berliner Konferenz Mineralische Nebenprodukte und Abfälle CY - Berlin, Germany DA - 12.06.2024 KW - Rostasche KW - Ökotoxizität KW - Sequenzielle Extraktion PY - 2024 SN - 978-3-911006-80-4 VL - 11 SP - 176 EP - 190 PB - TK-Verlag CY - Neuruppin AN - OPUS4-60281 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wosniok, Aleksander A1 - Königsbauer, Korbinian A1 - Nöther, Nils A1 - Färber, Jan A1 - Schaller, M.-Barbara A1 - Krebber, Katerina T1 - Distributed polymer optical fiber sensors using digital I-OFDR for geotechnical infrastructure health monitoring N2 - We present a distributed polymer optical fiber sensor system for deformation monitoring of geotechnical infrastructure. The sensor system is based on the digital incoherent optical frequency domain reflectometry (I-OFDR) for the detection of local strain events along a perfluorinated polymer optical fiber (PF-POF) used as a sensing fiber. For the best possible load transfer, the PF-POFs were integrated onto geosynthetics which pose a sensor carrier for the sensing fiber. By using elastic PF-POF instead of a standard glass fiber as a sensing fiber the strain range of geosynthetics-integrated fiber optic sensors could be extended up to 10 % in accordance with the end-user requirements. T2 - 11th European Workshop on Structural Health Monitoring CY - Potsdam, Germany DA - 10.06.2024 KW - Digital I-OFDR KW - Distributed polymer optical fiber sensor KW - Ddistributed strain sensing KW - Smart geosynthetics KW - Structural health monitoring PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-603096 SP - 1 EP - 7 PB - NDT.net AN - OPUS4-60309 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Charmi, Amir A1 - Heimann, Jan A1 - Duffner, Eric A1 - Hashemi, Seyedreza A1 - Prager, Jens T1 - Application of deep learning for structural health monitoring of a composite overwrapped pressure vessel undergoing cyclic loading N2 - Structural health monitoring (SHM) using ultrasonic-guided waves (UGWs) enables continuous monitoring of components with complex geometries and provides extensive information about their structural integrity and their overall condition. Composite overwrapped pressure vessels (COPVs) used for storing hydrogen gases at very high pressures are an example of a critical infrastructure that could benefit significantly from SHM. This can be used to increase the periodic inspection intervals, ensure safe operating conditions by early detection of anomalies, and ultimately estimate the remaining lifetime of COPVs. Therefore, in the digital quality infrastructure initiative (QI-Digital) in Germany, an SHM system is being developed for COPVs used in a hydrogen refueling station. In this study, the results of a lifetime fatigue test on a Type IV COPV subjected to many thousands of load cycles under different temperatures and pressures are presented to demonstrate the strengths and challenges associated with such an SHM system. During the cyclic testing up to the final material failure of the COPV, a sensor network of fifteen surface-mounted piezoelectric (PZT) wafers was used to collect the UGW data. However, the pressure variations, the aging process of the COPV, the environmental parameters, and possible damages simultaneously have an impact on the recorded signals. This issue and the lack of labeled data make signal processing and analysis even more demanding. Thus, in this study, semi-supervised, and unsupervised deep learning approaches are utilized to separate the influence of different variables on the UGW data with the final aim of detecting and localizing the damage before critical failure. T2 - 11th European Workshop on Structural Health Monitoring CY - Potsdam, Germany DA - 10.06.2024 KW - Structural health monitoring KW - Deep learning KW - Ultrasonic-guided waves KW - Anomaly detection KW - Damage localization PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-607396 DO - https://doi.org/10.58286/29751 SP - 1 EP - 8 AN - OPUS4-60739 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Gaddampally, Mohan Reddy A1 - Völzke, Holger T1 - Failure Analysis on Irradiated Claddings Subjected to Long-Term Dry Interim Storage N2 - Long-term dry interim storage may adversely affect the mechanical properties of spent fuel rods, possibly resulting in a reduced resilience during handling or transport after storage. The cladding is the first barrier for the spent fuel pellets. An established method for characterising the cladding material is the ring compression test (RCT), in which a small, cylindrical sample of the cladding tube is subjected to a compressive load. Radial hydrides may precipitate in zirconium-based alloys (Zircaloy) under pre-storage drying and during slow cooling, which result in embrittlement of the cladding material and eventually a possible sudden failure of cladding integrity under additional mechanical loads. The focus of the presented research is on the development of appropriate nu-merical methods for predicting the mechanical behaviour and identification of limiting conditions to prevent brittle fracture of Zircaloy claddings. A modelling approach based on cohesive zones is ex-plained which is able to reproduce the propagation of cracks initiated at radial hydrides in the zir-conium matrix. The developed methods are applied to defueled samples of cladding alloy ZIRLO®, which were subjected to a thermo-mechanical treatment to reorient existing circumferential hy-drides to radial hydrides. A selected sample showing sudden load drops during a quasi-static ring compression test is analysed by means of fracture mechanics for illustrative purposes. Based on the developed fracture mechanics approach, not only the deformation behaviour but also the fail-ure behaviour of irradiated as well as unirradiated Zircaloy claddings with radial hydrides under RCT loading conditions can be adequately described. T2 - 27th International Conference on Structural Mechanics in Reactor Technology - SMiRT 27 CY - Yokohama, Japan DA - 03.03.2024 KW - Cladding Embrittlement KW - Cohesive Zone Modelling KW - Ring Compression Test KW - Spent Nuclear Fuel PY - 2024 SP - 1 EP - 8 AN - OPUS4-60671 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Johann, Sergej A1 - Stürenberg, Jan A1 - Tandon, Aditya T1 - Robotergestütztes Bauwerksmonitoring basierend auf eingebetteter Sensorik N2 - In den letzten Jahrzehnten hat sich das Bauwerksmonitoring (engl. „Structural Health Monitoring“, SHM) zu einer nützlichen Ergänzung routinemäßiger Inspektionen entwickelt. SHM ermöglicht die frühzeitige Erkennung von Schäden an Bauwerken und dadurch die frühe, und somit kostengünstige, Durchführung von Reparatur- und Wartungsarbeiten. Mit dem Aufkommen drahtloser Technologien und Fortschritten in der Informations- und Kommunikationstechnologie werden Bauwerke zunehmend mit drahtlosen Sensorknoten ausgestattet, um für SHM relevante Bauwerksdaten zu erfassen, zu analysieren und zu übertragen. Eine vielversprechende Methode für SHM ist die direkte Einbettung von Sensoren in den Beton. In diesem Beitrag wird ein Sensorsystem zur Einbettung in Beton vorgestellt, das in der Lage ist, die im Beton aufgenommenen Bauwerksdaten auszuwerten. Die Sensoren werden bei Bedarf von vierbeinigen Robotern mittels Radio Frequency Identification (RFID) ausgelesen und mit Energie versorgt, was einen automatisierten und effizienten Prozess ermöglicht. Der prototypische Prozess zur automatischen Erfassung von Bauwerksdaten mit eingebetteter Sensorik und vierbeinigen Robotern wird durch Tests in einer Büroumgebung validiert. Die Ergebnisse der Tests bestätigen die automatische und effiziente Erfassung von Bauwerksdaten, die eine frühzeitige Erkennung von Bauwerksschäden, auch von nicht sichtbaren Schäden, ermöglicht, und eine folgerichtige Weiterentwicklung des modernen Bauwerksmonitorings repräsentiert. T2 - 35. Forum Bauinformatik CY - Hamburg, Germany DA - 18.09.2024 KW - Radio Frequency Identification (RFID) KW - Bauwerksmonitoring (SHM) KW - Eingebettete Sensorik KW - Vierbeinige Roboter KW - Autonome Navigation PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-621890 DO - https://doi.org/10.15480/882.13502 SP - 139 EP - 146 AN - OPUS4-62189 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz A1 - Said, Samir T1 - Vibration measurements for the control of damaged and repaired railway tracks N2 - The damage detection and repair control have become important tasks for ballast and slab tracks. Measurements which compare the damaged and the repaired status of the same track section at different times, or which compare a damaged and an intact track section at the same time, have been successfully performed at some sites in Germany with slab tracks and ballast tracks and compared with the theoretical behaviour of intact and damaged tracks. The loss of contact between the sleeper and the plate, between the plate and the base layer, and some problems with soft or weakened soil have been analysed. The observed results, changes in the time histories of displacements and velocities due to train passages and in the transfer functions (compliances) due to hammer impacts, are encouraging that these measurements can be used to detect track damage. In addition, calculations with the combined finite-element boundary-element method have been used to confirm the conclusions about intact or damaged railway tracks. T2 - 7th International Symposium on Environmental Vibration and Transportation Geodynmaics CY - Hangzhou, China DA - 28.10.2016 KW - Railway track KW - Slab track KW - Ballast track KW - Track-soil interaction KW - Field tests KW - Track damage monitoring KW - Finite element method KW - Boundary element method PY - 2016 SP - 3 EP - 19 AN - OPUS4-38261 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Maiwald, Michael T1 - Die Technologie-Roadmap „Prozess-Sensoren 4.0“ – Chancen für neue Automatisierungskonzepte und neue Geschäftsmodelle N2 - Die auf der NAMUR HS 2015 vorgestellte Technologie-Roadmap „Prozess-Sensoren 4.0“ zeigt die nötigen Anforderungen an Prozess-Sensoren sowie an deren Kommunikations-fähigkeiten auf. Eine Topologie für smarte Sensoren, das Zusammenwirken mit daten- und modellbasierte Steuerungen bis hin zur Softsensorik sowie weitere Anforderungen an Sensoren sind heute noch nicht angemessen beschrieben. Wir müssen jetzt schnell die Weichen für eine smarte und sichere Kommunikationsarchitektur stellen, um zu einer störungsfreien Kommunikation aller Sensoren auf Basis eines einheitlichen Protokolls zu kommen, welches alle Sensoren ausgeben und verstehen. KW - Prozess-Sensoren KW - Prozess-Sensoren 4.0 KW - Industrie 4.0 KW - OPC UA KW - Prozessanalytik KW - Prozessindustrie KW - Automatisierung PY - 2016 UR - https://www.di-verlag.de/de/atp-plus-Smart-Sensors SN - 2510-3911 VL - 01 IS - 1 SP - 12 EP - 21 PB - DIV Deutscher Industrieverlag GmbH CY - München AN - OPUS4-38229 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klinger, Christian T1 - Schwingbruch einer Kraftstoffleitung durch Biodiesel? N2 - Schadensteil: PME-Kraftstoffleitung Schadensmechanismus: Reibverschleiß und Schwingbruch Schadensursachen: Nichtbeständigkeit der Elastomereinlage in Befestigungsschelle gegen unplanmäßig ausgetretenen Biodiesel (PME); Schwingungen der Kraftstoffleitungen Schadensablauf: Elastomer versprödet, Schwingungen der Kraftstoffanlage, Reibverschleiß an der Befestigungsschelle, äußerliche oberflächliche Korrosion der Leitung; Schwingbruch der Kraftstoffleitung; Brand am Motor eines BHKWs T2 - 42. VDI-Jahrestagung CY - Würzburg, Germany DA - 29.09.2016 KW - Schwingbruch PY - 2016 VL - 42. VDI-Jahrestagung SP - 109 EP - 119 PB - VDI-Wissensforum GmbH AN - OPUS4-38284 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völker, Christoph A1 - Kruschwitz, Sabine A1 - Boller, C. A1 - Wiggenhauser, Herbert T1 - Feasibility study on adapting a machine learning based multi-sensor data fusion approach for honeycomb detection in concrete N2 - We present the results of a machine learning (ML)- inspired data fusion approach, applied to multi-sensory nondestructive testing (NDT) data. Our dataset consists of Impact-Echo (IE), Ultrasonic Pulse Echo (US) and Ground Penetrating Radar (GPR) measurements collected on large-scale concrete specimens with built–in simulated honeycombing defects. In a previous study we were able to improve the detectability of honeycombs by fusing the information from the three different sensors with the density based clustering algorithm DBSCAN. We demonstrated the advantage of data fusion in reducing the false positives up to 10% compared to the best single sensor, thus, improving the detectability of the defects. The main objective of this contribution is to investigate the generality, i.e. whether the conclusions from one specimen can be adapted to the other. The effectiveness of the proposed approach on a separate full-scale concrete specimen was evaluated. T2 - NDE/NDT for Highway and Bridges: Structural Materials Technology 2016 CY - Portland, Oregon, USA DA - 29.08.2016 KW - Data fusion KW - Concrete evaluation KW - Honeycombing KW - Machine learning KW - Clustering PY - 2016 SN - 978-1-57117-392-8 SP - 144 EP - 148 PB - The American Society for Nondestructive Testing, Inc CY - Portland, Oregon, USA AN - OPUS4-38288 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Patrick P. A1 - Lazik, D. A1 - Bartholmai, Matthias T1 - Leak detection with linear soil gas sensors under field conditions - First experiences running a new measurement technique N2 - A 400 m² soil test field with gas injection system was built up, which enables an experimental validation of linear gas sensors for specific applications and gases in an application-relevant scale. Several injection and soil watering experiments with carbon dioxide (CO2) at different days with varying boundary conditions were performed indicating the potential of the method for, e.g., rapid leakage detection with respect to Carbon Capture and Storage (CCS) issues. T2 - IEEE Sensors 2016 CY - Orlando, FL, USA DA - 30.10.2016 KW - Soil test field KW - Membrane-based linear gas sensor KW - Leak detection KW - Field conditions PY - 2016 SN - 978-1-4799-8287-5 SN - 1930-0395 SP - B-3-65, 757 EP - 759 PB - IEEE AN - OPUS4-38244 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Apel, Andreas A1 - Wille, Frank A1 - Moutarde, M. A1 - Sert, G. A1 - Caillard-Lizot, M.-T. A1 - Eckert, B. A1 - Konnai, A. A1 - Pstrak, D. A1 - Harvey, J. A1 - Desnoyers, B. A1 - Purcell, P. A1 - Fiaccabrino, V. T1 - Stowage during transport: a proposal for harmonization N2 - For stowage and retention during transport, the International Atomic EnergyAgency (IAEA) Transport regulations (SSR-6) only require that the package shall be securely stowed. Additional information is given in the IAEA guidance material (SSG-26), that includes specific load factors that should be considered in the safety demonstrations. Nevertheless, applicants commonly use other load factors to justify the design of the packaging attachment points. In particular, acceleration values vary between different countries and this may lead to difficulties during the validation of foreign approval certificates. Discussions with applicants identified that the load factors presented in the IAEA guidance material are not necessarily relevant for the different transport modes. For some modes, the load factors are representative of situations occurring in routine conditions of transport. For other modes, the load factors are more representative of situations occurring in normal or accident conditions of transport. Furthermore, the origins of the specified values are not clear. In this context, some IAEA TRANSSC members decided to review the stowage guidance. An international working group was constituted in 2013, including representatives of competent authorities, technical support organizations, and transport stakeholders. Several topics were discussed and many questions were raised during the two year review. For example, some discussions focused on Paper No.1031 2 the conditions which have to be considered for stowage design, both as relevant to the load factors used for strength and fatigue analysis, as well as the criteria which have to be considered for the package attachment points. In addition, related questions on operational aspects were also discussed. Overall, the working group concluded that new guidance material was warranted as input into SSG-26. As a result of those discussions, the international working group produced new guidance material for stowage in transport, addressing each of these topics. The proposal to modify the IAEA guidance material (SSG-26, Appendix IV), presented by France to the TRANSSC in the 2015 initiated Review cycle of the Regulations, was unanimously accepted and will be implemented in the next edition of the guidance material. T2 - PATRAM 2016 CY - Kobe, Japan DA - 18.09.2016 KW - Packages for radioactive material KW - IAEA regulations (SSR-6, SSG-26) KW - Tie-down and stowage KW - Load cases for transport KW - Design of the packaging attachment points PY - 2016 SP - Paper 1031, 1 EP - 8 AN - OPUS4-38644 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schukar, Vivien A1 - Gong, Xin A1 - Hofmann, Detlef A1 - Basedau, Frank A1 - Köppe, Enrico A1 - Bartholmai, Matthias A1 - Westphal, Anja A1 - Sahre, Mario A1 - Beck, Uwe ED - Berghmans, F. ED - Mignani, A. G. T1 - Modelling and simulation of a fibre Bragg grating strain sensor based on a magnetostrictive actuator principle N2 - A new concept for the self-diagnosis of embedded fiber Bragg grating (FBG) strain sensors was developed, simulated and experimentally tested. This concept is based on a magnetostrictive metallic layer directly coated on the fibre cladding over the grating segment of the FBG sensor, so that an on-demand external magnetic field in a millitesla scale can produce a controllable artificial strain as an indication signal for the remote optical interrogator. The relationship between the pre-defined magnetic field and its induced Bragg wavelength shift characterizes this validation concept. Any deviation of the local bonding state of the interfaces from the initial or/and any change of shear strain transferring mechanism from composite matrix to the optical fibre core will result in alterations in this sensitive relationship, and thus triggers an immediate alert for a further inspection. The finite element method is used to simulate the strain of this configuration as result of different values of the magnetic field in order to optimize the geometrical sensor parameters. The simulations are verified by experiments results. © (2016) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only. T2 - Optical Sensing and Detection IV CY - Brüssel, Belgium DA - 03.04.2016 KW - Fiber Bragg gratings KW - Actuators KW - Modeling and simulation KW - Finite element methods PY - 2016 SN - 9781510601444 DO - https://doi.org/10.1117/12.2224728 SN - 0277-786X SN - 1996-756X VL - 9899 SP - 9899-39 PB - SPIE Digital Library AN - OPUS4-38634 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koegler, M. A1 - Paul, Andrea A1 - Alborch, K. P. A1 - Birkholz, M. A1 - Junne, S. A1 - Neubauer, P. T1 - Raman on-line monitoring approach for bioprocess and bio-pharmaceutical manufacturing N2 - There is a high demand of monitoring in the era of QbD in industrial scale require new approaches to gain data rapidly and of sufficient quality in real time. Raman spectroscopy technology has great potential but not yet shown it fully in process on-line monitoring due to limitations such as i) uncomplete separation between cells and growth media alone, ii) general weak Raman signals of analytes in complex solutions and iii) strong background signals such as the auto-fluorescence, cosmic rays and surrounding lights overlapping the weak Raman signals. Here we demonstrate a Proof-of-Concept on an the example lactic acid bacteria process using a Streptococcus thermophiles fermentation. Results from three different Raman approaches are presented: 1) Time-Gated Raman Spectroscopy (TG-Raman), 2) Surface Enhanced Raman Spectroscopy (SERS) and 3) Raman process spectroscopy with NIR excitation combined with multivariate data analysis (MVDA) using Principal Component Analysis (PCA) and Partial Least Squares Regression (PLSR). T2 - 12. Kolloquium Arbeitskreis Prozessanalytik CY - Berlin, Germany DA - 28.11.2016 KW - Raman KW - Chemometrics KW - SERS KW - TimeGate PY - 2016 SP - 91 EP - 93 CY - Berlin AN - OPUS4-38673 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Grunewald, Thomas A1 - Grätz, Rainer A1 - Holländer, Lars T1 - Entwicklung normativer Anforderungen an explosionsgeschützte nichtelektrische Geräte resultierend aus der Zündfähigkeit mechanisch erzeugter Schlagfunken (NAMES) N2 - Die Ergebnisse des Forschungsprojektes zeigen, dass Schlagvorgänge mit Edelstählen eine erhebliche Zündgefahr von explosionsfähigen Brenngasgemischen darstellen können. Dabei bestehen jedoch mitunter deutliche Unterschiede zwischen den verschiedenen Brenngasgemischen. Besonders hohe Zündwahrscheinlichkeiten konnten bei Brenngasgemischen mit Brenngasen der IEC-Explosionsgruppe IIC beobachtet werden, die Acetylen bzw. Wasserstoff als Brenngas enthielten. Schläge im Wasserstoff/Luft-Gemisch waren dabei jedoch bedeutend zündwirksamer. In diesem Gasgemisch konnte bei nied-rigen maximalen Schlagenergien bis 60 J sogar eine mitunter höhere relative Zündhäufigkeit beobachtet werden als bei Versuchen mit unlegiertem Baustahl. KW - Funken KW - Mechanisch erzeugte Funken KW - Schlagfunken KW - Reibfunken KW - Mechanische Funken KW - Mechanische Geräte KW - Explosionsschutz KW - ATEX KW - Nichtelektrische Geräte PY - 2015 UR - https://www.tib.eu/de/suchen/id/TIBKAT%3A877987866/Entwicklung-normativer-Anforderungen-an-explosionsgesch%C3%BCtzte/?tx_tibsearch_search%5Bsearchspace%5D=tn SP - 1 EP - 38 AN - OPUS4-38581 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jann, Oliver T1 - Emissionen flüchtiger Verbindungen aus Bauprodukten N2 - Vielzahl unterschiedlicher VOC kann aus Bauprodukten freigesetzt werden. In den meisten Bauproduktgruppen gibt es sowohl emissionsarme als auch emissionsreiche Produkte. Manche VOC produktgruppenspezifisch: Siloxane/Silikon, andere VOC unspezifisch wie Formaldehyd, Essigsäure VOC-Analytik und Gerüche zeigen im Allgemeinen keinen Zusammenhang. Schwerflüchter zeigen Langzeitemission und ausgeprägte Senken-/Memoryeffekte. Radon kann aus manchen Bauprodukten abgegeben werden und bei luftdichten Gebäuden in radonarmen Gebieten Haupt-Radonquelle sein. Radonexhalation kann grundsätzlich (statisch/dynamisch) mit VOC-Kammern - ergänzt mit geeigneten Messgeräten - bestimmt werden. T2 - VDI-Wissensforum: Bauprodukte und gesunde Innenraumluft CY - Düsseldorf, Germany DA - 22.11.2016 KW - VOC KW - Bauprodukte KW - Emissionen KW - Luft KW - Radon PY - 2016 SP - 3 EP - 23 PB - VDI CY - Düsseldorf AN - OPUS4-38589 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bettge, Dirk A1 - Klinger, Christian T1 - Aufbau einer Wissensbasis zu Bruchflächen und Gefüge in der fraktographischen online-Datenbank N2 - In einer fraktographischen online-Datenbank werden Informationen zum Bruchverhalten von technischen Werkstoffen zusammengetragen. Primäres Ziel ist die kontrollierte Erzeugung von Brüchen und deren anschließende Analyse, aber auch Beispiele aus Schadensfällen werden eingestellt. Die makroskopischen und mikroskopischen Merkmale von Bruchflächen, die Art der Beanspruchung und die dazugehörigen Werkstoffgefüge werden in Datensätzen zusammengefasst, die der interessierten Fachöffentlichkeit zu Verfügung stehen. T2 - Metallographietagung 2016 CY - Berlin, Germany DA - 21.9.2016 KW - Fraktografie KW - Datenbank KW - Bruchverhalten KW - Schadensanalyse PY - 2016 SN - 978-3-88355-412-9 VL - 50 SP - 3 EP - 12 PB - DGM AN - OPUS4-38189 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Linnemann, Konrad A1 - Ballheimer, Viktor A1 - Müller, Lars A1 - Rolle, Annette A1 - Wille, Frank A1 - Droste, Bernhard T1 - Aspects of spent fuel behavior assessment for transport packages N2 - Transport packages for spent nuclear fuel have to be assessed with respect to specific transport conditions which are defined in the safety regulations of the International Atomic Energy Agency. In general, gastight fuel rods constitute the first barrier of the containment system. The physical state of the spent fuel and the fuel rod cladding as well as the geometric configuration of the fuel assemblies are important inputs for the evaluation of the package safety under transport conditions. The objective of this paper is to discuss the methodologies accepted by BAM for the authority assessment of spent fuel behavior within the package design approval procedure of German package designs. In particular, cracks or failures in the fuel rod cladding can occur under regulatory transport conditions. These defects can cause the release of gas, volatiles, fuel particles or fragments into the package cavity and have to be considered properly in the safety analysis. Another issue is the transport of defective fuel rods. One concept is to use special canisters which can be handled like fuel assemblies. This concept requires additional assessment concerning drying, sealing and the mechanical and thermal design of such canisters. The package as a mechanical system is characterized by a complex set of interactions, e.g. between the fuel rods within the assembly as well as between the fuel assemblies, the basket, and the cask containment. This complexity together with the limited knowledge about the material properties and the variation of the fuel assemblies regarding cladding material, burn-up and the operation history makes an exact mechanical analysis of the fuel rods nearly impossible. The simplified approaches to consider conservatively spent fuel behavior currently accepted by BAM are presented here. T2 - International Conference on Management of Spent Fuel from Nuclear Power Reactors - An Integrated Approach to the Back-End of the Fuel Cycle CY - Wien, Austria DA - 15.06.2015 KW - Transport packages KW - Spent fuel assessment PY - 2015 SP - 1 AN - OPUS4-38102 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Harsha, A. P. A1 - Wäsche, Rolf T1 - Tribological studies on polyetherimide composites sliding against steel under reciprocating conditions N2 - The friction and wear properties of polyetherimide composites under dry oscillating sliding condition at room temperature (RT) as well as at elevated temperature (120 °C) was investigated. The polymer specimens were made to oscillate against steel cylinder as a counterpart. The friction and wear properties of PEI and composites were strongly influenced by the temperature. In case of carbon fiber composite abrasive action of carbon fibers has severely damaged the counterpart and resulted in accelerated wear of the composite at RT. Solid lubricants filled (PTFE, MoS2, graphite) along with glass fiber is beneficial in improving the friction and wear performance of the PEI composite at RT, whereas at elevated temperature wear performance was deteriorated. T2 - 2nd International Conference on Polymer Tribology CY - Ljubljana, Slovenia DA - 15.09.2016 KW - Polyetherimide KW - Composites KW - Friction KW - Wear KW - Temperature KW - Oscillating sliding KW - Solid lubricant KW - Fibers PY - 2016 AN - OPUS4-38135 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bienge, J.-E. A1 - Illerhaus, Bernhard A1 - Epperlein, J. ED - Szallies, agrathaer GmbH, Isabell T1 - Blick in den Boden N2 - Computertomographische Untersuchungen in einer Studie zum vergleichenden Wurzelwachstum von Raps unter verschiedenen Bedingungen der Bodenbearbeitung. T2 - 20 Jahre Praxisversuch Lietzen Ackerbau und Forschung auf dem Weg in die Zukunft Feldtag in der Komturei Lietzen CY - Komturei Lietzen, Germany DA - 19.5.2016 KW - Computer Tomographie PY - 2016 SP - 28 EP - 29 AN - OPUS4-38144 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Gartiser, S. A1 - Heisterkamp, I. A1 - Schoknecht, Ute A1 - Burkhardt, M. A1 - Ratte, M. T1 - Empfehlungen für eine Testbatterie zur ökotoxikologischen Bewertung der Umweltverträglichkeit von Bauprodukten N2 - Die Europäische Bauprodukteverordnung (EU) Nr. 305/2011 ermöglicht den Mitgliedstaaten Vorschriften zur Bewertung der Umweltauswirkungen ihrer Bauwerke zu erlassen. Ziel des Pro-jektes war es, Empfehlungen für eine Testbatterie zur ökotoxikologischen Bewertung der Um-weltverträglichkeit von Bauprodukten für die Außenanwendung zu erarbeiten, die zur Europä-ischen Harmonisierung von Prüfmethoden beitragen. Aus einer Auswahlliste von 39 Produkten wurden 20 Produkte in das ökotoxikologische Untersuchungsprogramm einbezogen. Monoli-thische und flächige Bauprodukte wurden in der horizontalen dynamischen Oberflächenaus-laugprüfung (DSL-Test) nach CEN/TS 16637-2, granulare Produkte im Schütteltest nach DIN EN 12457-1 eluiert. Die Eluate wurden in vier aquatischen Toxizitätstests (Algen, Daphnien, Leuchtbakterien, Fischeier), einem Gentoxizitätstest (umu-Test) und im Respirometertest (OECD 301 F) untersucht. Hierbei wurden niedrige bis sehr hohe Ökotoxizitäten (bis Verdün-nungsstufe 1536) bestimmt. Zudem wurde ein Europäischer Ringversuch mit 17 Teilnehmern und zwei Bauprodukten konzeptionell vorbereitet, durchgeführt und gemäß DIN ISO 5725 ausgewertet. Nach Ausschluss der nicht validen bzw. als Ausreißer identifizierten Biotests war die laborübergreifende Streuung des Gesamtverfahrens zur ökotoxikologischen Charakterisie-rung von Bauprodukten akzeptabel. Der Variationskoeffizient für die Konzentration, die einen 50%igen Effekt induziert (EC50) lag für die verschiedenen Tests und Bauprodukte zwischen 9 und 110% und beschreibt die Variabilität des gesamten, komplexen Verfahrensablaufs vom Elutionsprozess über Probenlagerung bis hin zur eigentlichen Biotestdurchführung. Es wurden Empfehlungen zur Planung und Durchführung von Ökotoxizitätstests zur Bewertung von Bau-produkten erarbeitet und bei der für die europäische Harmonisierung von Auslaugtests für Bauprodukte zuständigen CEN-Arbeitsgruppe eingereicht. KW - Freisetzung KW - Schadstoffe KW - Umweltbewertung KW - Ökotoxikologische Testverfahren KW - Bauprodukte PY - 2016 UR - http://www.umweltbundesamt.de/publikationen/empfehlungen-fur-eine-testbatterie-zur SN - 1862-4804 VL - 74/2016 SP - 1 EP - 161 CY - Dessau-Roßlau AN - OPUS4-38559 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bleeker, E. A1 - Visser, M. A1 - Groenewold, M. A1 - Blab, G. A1 - Brouwer, D. A1 - Sultan, Y. A1 - Gagnon, C. A1 - Wilkinson, K. A1 - Doa, M. A1 - Boyes, W. A1 - Kiyota, Y. A1 - Yanase, K. A1 - Holmqvist, J. A1 - Rasmussen, K. A1 - Sumrein, A. A1 - Clancy, S. A1 - Brown, S. A1 - Carlander, D. A1 - Murphy, L. A1 - Bresch, Harald A1 - Hund-Rinke, K. A1 - Igarashi, T. A1 - Riego-Sintes, J. A1 - Tentschert, J. T1 - Physical-chemical properties of nanomaterials: Evaluation of methods applied in the OECD-WPMN Testing Programme N2 - The Sponsorship Programme for the Testing of Manufactured Nanomaterials (further referred to as “the Testing Programme”) was concluded in March 2013, and the publication of the dossiers via the OECD website (www.oecd.org/science/nanosafety) started in June 2015. As indicated in the “Guidance manual for the testing of manufactured nanomaterials: OECD’s sponsorship programme”, after conclusion of the Testing Programme a next step is to consider “the status, need for, and coordination of further test development”. Parallel to concluding the final stages of the Testing Programme, a series of workshops have taken place, in which for different topics the applicability of existing OECD test guidelines for nanomaterials was discussed and the need for new ones analysed. One workshop focussed on physico-chemical methods, addressing in detail the relevance of each physico-chemical endpoint proposed in the Testing Programme for the regulation of nanomaterials. The methods were discussed in more general terms. However, as most of the proposed endpoints are new to the OECD Test Guidelines Programme, a much more detailed evaluation of the applied methods would be highly relevant. To this extent,the Netherlands volunteered to lead an initial detailed evaluation of the applicability of the test methods applied to determine the physico-chemical properties of different types of nanomaterials in the Testing Programme. This initial focus on physico-chemical properties was prompted by the essential need for an adequate and complete characterisation of nanomaterials to enable a further evaluation of their (toxicological) properties. A number of experts from several delegations volunteered to review and evaluate the methods applied to determine the physico-chemical properties of the nanomaterials in the Testing Programme. KW - Nanomaterialien KW - Nano KW - Nanopartikel KW - Charakterisierung KW - OECD KW - Nanomaterials PY - 2016 UR - http://www.oecd.org/env/ehs/nanosafety/publications-series-safety-manufactured-nanomaterials.htm IS - 65 SP - 1 EP - 43 CY - Paris AN - OPUS4-38495 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simon, Franz-Georg A1 - Bandow, Nicole T1 - Significance of cadmium from artists‘ paints to agricultural soil and the food chain N2 - An Annex XV restriction dossier for cadmium in artists’ paints was submitted by an EU member state to the European Chemicals Agency ECHA. By cleaning used brushes under the tap cadmium can enter the food chain via waste water treatment and subsequent agricultural application of the sewage sludge. It was estimated that 110 kg Cd per year is spread on agricultural land via this exposure route. Other sources of Cd amount to almost 120 tons per year. The mobility of Cd from pigments was studied in a field-like scenario by leaching experiments using soil samples amended with sewage sludge and spiked with Cd pigments in percolation columns. The redox conditions were confirmed to be the decisive factor for the release of Cd. The release of Cd from artists’ paints was in most cases 1% or lower in the experiments performed. Cd from artists’ paints in sewage sludge applied in agriculture will be mobilized for intake by crops or to leaching either by oxidation of sulfide to sulfate or by dissolution at lower pH values. The quantity of Cd from artists’ paints calculated in the restriction dossier is however negligible compared to other sources of Cd to agricultural soil. Therefore ECHA did not consider the proposed restriction to be the most appropriate EU wide measure to address the negligible level of risk. In the presentation sources of Cd on agricultural land will be discussed together with possible policy instruments to mitigate such emissions. T2 - 9th International Cadmium Conference CY - Lisbon, Portugal DA - 26.10.2016 KW - Cadmium KW - REACH KW - leaching PY - 2016 UR - http://www.conference.cadmium.org/ SP - 9 EP - 10 AN - OPUS4-38473 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dong, Xian-Quan T1 - Analysis and attenuation of disturbance vibrations in notched bar impact testing T2 - 2nd Internat. Symp. on Modal Analysis CY - Florida, USA DA - 01.02.1984 PY - 1984 SP - 275 EP - 279 AN - OPUS4-36740 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klamrowski, Günter A1 - Neustupny, Paul A1 - Zajc, A. ED - Sneck, T. T1 - Degree of moisture saturation and mechanical properties of concrete T2 - Third International Conference on the Durability of Building Materials and Components CY - Espoo, Finland DA - 12.08.1984 PY - 1984 SP - 500 EP - 509 CY - Espoo AN - OPUS4-36800 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Richter, Harry A1 - Böttcher, Bernhard T1 - Zerstörungsfreier Feuchtigkeitsnachweis im Mauerwerk mit Hilfe der Infrarotkamera T2 - Internationaler Thermografiekongreß CY - Lucerne, Switzerland DA - 07.05.1984 PY - 1984 SP - 1 EP - 10 CY - Luzern AN - OPUS4-36806 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Winkler, Helmut T1 - Fundamental investigations on the influence of test equipment on multiaxial test results of concrete T1 - L'influence de la technique employee lors de l'essai a l'ecrasement pluriaxial de beton T2 - International Conference on Concrete under Multiaxial Conditions CY - Toulouse, France DA - 22.05.1984 PY - 1984 VL - 1 SP - 9 EP - 19 PB - Sabatier CY - Toulouse AN - OPUS4-36807 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmidt, Stephan ED - Schmidt, Stephan T1 - Entwicklung monoklonaler Antikörper gegen Diclofenac N2 - Diclofenac (DCF) wird als nicht-steroidales-antientzündliches Arzneimittel gegen Fieber, Entzündungen, rheumatische Erkrankungen und Schmerzen eingesetzt. 70 % werden nach Einnahme wieder ausgeschieden. Aufgrund unvollständiger Elimination in den Kläranlagen lassen sich Rückstände im Trinkwasser und im Oberflächengewässer nachweisen. Diclofenac wird in der Umweltanalytik v.a. mittels GC-MS oder LC-MS nachgewiesen. Bioanalytische Methoden machen sich die spezifische Antigen-Antikörper-Wechselwirkung zunutze, so z.B. Immunoassays. Die hierfür erforderlichen Antikörper werden durch Immunisierung mit einem Konjugat aus dem Analyten und einem Trägerprotein gewonnen. Die Kopplung kann direkt über die Carboxylfunktion von Diclofenac erfolgen. Um Abschirmungseffekte zu vermeiden, kann zwischen Protein und Analyt ein Spacer sinnvoll sein. T2 - 2. Forum Junger Umweltwissenschaftler CY - Blomberg, Germany DA - 22.06.2015 KW - Haptene KW - Diclofanc KW - Antikörper KW - Proteinkonjugate KW - ELISA PY - 2015 SN - 1618-3258 VL - 21 IS - 4/2015 SP - 107 EP - 109 PB - Fachgruppe Umweltchemie und Ökotoxikologie der Gesellchaft Deutscher Chemiker CY - Trier AN - OPUS4-36810 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wieser, Karol E. A1 - Masslowski, Jörg-Peter A1 - Sieber, R. T1 - Investigations on shock absorbers for tye B packagings T2 - 7th International symposium Packaging and Transportation of Radioactive Materials CY - New Orleans, La., USA DA - 15.05.1983 PY - 1983 VL - 1 SP - 1569 EP - 1575 AN - OPUS4-36580 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stengel, Dominik A1 - Clobes, M. A1 - Thiele, K. T1 - Investigation on the dynamic behavior of an OHL conductor bundle with light and heavy ice accretion N2 - Under a variety of possible cable vibrations which overhead line conductors can suffer, galloping identifies by large amplitudes at rather low frequencies. Changes of the cross-section as by ice-accretion provide the basis for such vibrations through an aerodynamic instability of drag and lift responses under wind excitation. Two different types of light and heavy ice bodies attached to a quad bundle conductor are analysed in wind tunnel tests. The results of aerodynamic drag and lift coefficients are investigated by means of a finite element model under turbulent wind excitation. It was found that instability can be well simulated for the heavy ice accretion but not for the case of lightly iced conductors. T2 - 8th International Colloquium on Bluff Body Aerodynamics and Applications CY - Boston, MA, USA DA - 07.06.2016 KW - wind turbulence KW - overhead transmission line KW - bundle conductors KW - ice accretion KW - dynamic behaviour PY - 2016 SP - Paper 116, 1 EP - Paper 116, 8 AN - OPUS4-36554 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hebener, H. A1 - Rücker, Werner ED - Natke, H. G. T1 - Entstehung und Ausbreitung von Rammerschütterungen T2 - Tagung "Dynamische Probleme -Modellierung und Wirkleichkeit -" CY - Hanover, Germany DA - 04.10.1984 PY - 1984 SP - 195 EP - 214 CY - Hannover AN - OPUS4-36839 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brandes, Klaus T1 - Design of reinforced concrete structures against impact and impulsive loading T1 - Entwurf von Stahlbetonkonstruktionen unter Stossbelastung T2 - 12th Congress of the International Association for Bridge and Structural Engineering CY - Vancouver, BC, Canada DA - 03.09.1984 PY - 1984 SN - 3-85748-044-0 SP - 927 EP - 932 PB - ETH-Hönggerberg CY - Zürich AN - OPUS4-36830 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Plauk, Günther A1 - Herter, Jürgen T1 - Reinforced concrete structures under impact and impulsive loading: recent developments, problems and trends T2 - Conference on structural analysis and design of nuclear power plants CY - Porto Alegre, Brazil DA - 03.10.1984 PY - 1984 SP - 1 EP - 17 CY - Porto Alegre AN - OPUS4-36836 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ledworuski, Siegmar T1 - Über eine leistungsfähige rechnergestützte Instrumentierung des Kerbschlagbiegeversuches PY - 1984 VL - 12 IS - 4 SP - 113 EP - 118 CY - Dübendorf AN - OPUS4-36777 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Packeiser, R. A1 - Olschewski, J. A1 - Ziebs, Josef A1 - Aurich, Dietmar T1 - Zur Anwendung des Näherungsverfahrens von Kumar, German und Shih auf Stähle T2 - 16. Sitzung des DVM-Arbeitskreises Burchvorgänge CY - Karlsruhe DA - 01.01.1984 PY - 1984 VL - 16 SP - 141 EP - 150 AN - OPUS4-36779 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Buchhardt, Frank A1 - Magiera, Götz A1 - Matthees, Wolfgang A1 - Weber, Michael T1 - Sensitivity of nuclear power plant structural response to aircraft impact T2 - Conference on structural analysis and design of nuclear power plants CY - Porto Alegre, Brazil DA - 03.10.1984 PY - 1984 SP - 111 EP - 114 CY - Porto Alegre AN - OPUS4-36780 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike A1 - Dümichen, Erik A1 - Barthel, Anne-Kathrin A1 - Bannick, Claus Gerhard T1 - Charakterisierung von Mikroplastik Partikeln aus Umweltproben N2 - Durch den stetig steigenden Einsatz von Plastikprodukten sind unerwünschte Kunststofffunde in verschiedenen Umweltmatrices mittlerweile allgegenwärtig. Besonderes Interesse erfahren die Kunststoffpartikel von einer Größe kleiner 5 mm, sogenannte Mikroplastik (MP) Partikel. Es werden aktuell Risiken für Mensch und Umwelt diskutiert, die von diesen Partikeln ausgehen. T2 - Wasser 2016 - Jahrestagung der Wasserchemischen Gesellschaft CY - Bamberg, Deutschland DA - 02.05.2016 KW - Mikroplastik KW - Polymere KW - Polyethylen (PE) KW - Polystyrol (PS) KW - Poly(ethylenterephthalat) (PET) PY - 2016 SN - 978-3-936028-94-2 SP - 74 EP - 76 PB - Wasserchemische Gesellschaft CY - Mülheim an der Ruhr, Germany AN - OPUS4-36782 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Buchhardt, Frank A1 - Weber, Michael A1 - Yazdi, F. T1 - On decisive factors of liner anchorage behaviour T2 - Conference on structural analysis and design of nuclear power plants CY - Porto Alegre, Brazil DA - 03.10.1984 PY - 1984 SP - 87 EP - 100 CY - Porto Alegre AN - OPUS4-36783 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brandes, Klaus T1 - Strain rate effects appearing in the mechanical behaviour of reinforced concrete structures under impact load T2 - Mechanics of inelastic media and structures, International Symposium CY - Warszawa, Poland DA - 08.09.1978 PY - 1982 VL - 8 SP - 73 EP - 86 AN - OPUS4-36769 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Stichel, Wolfgang T1 - Korrosion in Heizkörpern PY - 1983 N1 - Kolloquium: Fragen der Fernheizwasseraufbereitung und Korrosionen in Fernwärmesystemen SP - 1 EP - 16 CY - Frankfurt am Main AN - OPUS4-36770 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz-Forberg, Bernd T1 - Untersuchungen an Transportbehältern für radioaktive Stoffe T2 - Informationstagung "Strahlenschutzforschung" des BMI CY - Bonn DA - 30.05.1984 PY - 1984 N1 - Schriftenreihe: Reaktorsicherheit und Strahlenschutz; 48 SP - 121 EP - 140 CY - Eggenstein-Leopoldshafen AN - OPUS4-36771 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilsch, Gerd A1 - Gottlieb, Cassian A1 - Millar, Steven A1 - Wiggenhauser, Herbert T1 - Laser induced breakdown spectroscopy (LIBS) – automated 2D chemical analysis of concrete N2 - Laser-induced breakdown spectroscopy (LIBS) is a combination of laser ablation and optical emission spectroscopy. Due to the possibility of direct measurements on the sample surface with a minimum of sample preparation investigations of building materials can be conducted quite fast. In combination with a scanning technique (translation stage or scanning mirrors head) 2D element distributions of harmful species like chlorides and alkalis are evaluated with a sub-mm resolution. By scanning a surface of typically 100 mm x 100 mm the heterogeneity of the material may be considered. LIBS is capable to identify hot spots in element concentration with a resolution of 0.1 mm or even smaller. A LIBS-system for the on-site application on building materials is, in cooperation with system developers and companies which will use this technique for investigation on real structures, under test at BAM. We present an example. Further work will focus on providing guidelines to establish LIBS as a standard procedure for chemical investigations of building materials. T2 - NDE / NDT for Highway and Bridges: Structural Materials Technology CY - Portland, Oregon, USA DA - 29.08.2016 KW - LIBS KW - Concrete KW - Chloride KW - Chemical analysis PY - 2016 SN - 978-1-57117-392-8 SP - 155 EP - 160 PB - The American Society for Nondestructive Testing, Inc. CY - Columbus, OH 43228-0518, USA AN - OPUS4-37679 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zscherpel, Uwe A1 - Ewert, Uwe T1 - Electronic reference images for flaw indications in welds and castings N2 - Since decades the evaluation of flaw indications on radiographs from welds or castings are based on well accepted reference film catalogues from organizations like IIW (weldments), ASTM (castings) or DGZfP (D5 recommendation on heavy steel castings). Today, the transformation of classical film radiography to the digital world is in full progress. Some ASTM standards do not permit the evaluation of digital radiographs in reference to film catalogues. Therefore, these reference film catalogues have to be converted into the digital age too. BAM is supporting this transition by high definition film scanning. The result is a corresponding reference image catalogue. The different standard organizations selected different ways to distribute the digital data. ASTM used high definition film scanning at 10 μm pixel size and distribution of a huge amount of high-res data via DVD. The user sub-samples these high-res data during catalogue import to the resolution of his system. The comparison is done by synchronized image viewing on the computer work station. IIW recently decided to distribute their ISO 5817 reference images installed on tablets, which are used for image viewing too. The tablet image has to be compared with the digital image on the system monitor. DGZfP transformed their D5 reference radiographs into a PDF for monitor viewing. This is the simplest and cheapest solution, but still allows the full usage of the catalogue in the digital era. The status of ongoing work in progress will be discussed. T2 - WCNDT 2016 CY - Munich, Germany DA - 13.06.2016 KW - Castings KW - NDT KW - RT KW - Radiography KW - Discontinuities KW - Catalogues KW - Welds PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-377306 UR - http://ndt.net/?id=19310 SN - 1435-4934 VL - 21 IS - 7 SP - 1 EP - 8 PB - NDT.net CY - Kirchwald AN - OPUS4-37730 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rietz, U. A1 - Lange, Thorid A1 - Hielscher, Stefan A1 - Beck, Uwe A1 - Kavianpour, D. A1 - Lerche, D. T1 - Quantitative determination of adhesive tape properties by CAT-technology (centrifugal adhesion testing) N2 - The future commercial prospects for adhesive tapes are very good and its application range is very broad. From every-day-use in office, packaging, maintenance, and quick repair in workshops, it ranges from handicraft work, medical purposes and cosmetics up to workmanship. The study describes a new multi-sample approach in adhesive tape testing from theoretical background, preparation of test specimen for tensile as well as shear testing, detailed measurement procedures up to analysis and result interpretation. Various types of single and double-sided pressure sensitive adhesive tapes supplied by different manufacturers were investigated and compared T2 - EURADH 2016 Adhesion ´16 CY - Glasgow, UK DA - 21.09.2016 KW - Tensile KW - Shear KW - Peel KW - Strength KW - Analytical centrifugation KW - Adhesive tapes PY - 2016 SP - 352 EP - 355 AN - OPUS4-37664 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Komann, Steffen A1 - Wille, Frank A1 - Droste, Bernhard T1 - Gap analysis by periodical reviews of transport package design safety reports of German SNF/HLW dual purpose casks N2 - Storage of spent nuclear fuel and high-level waste in dual purpose casks (DPC) is related with the challenge of maintaining safety for transportation over several decades of storage. Beside consideration of aging mechanisms by appropriate design, material selection and operational controls to assure technical reliability by aging management measures, an essential issue is the continuous control and update of the DPC safety case. Not only the technical objects are subject of aging but also the safety demonstration basis is subject of “aging” due to possible changes of regulations, standards and scientific/technical knowledge. The basic document, defining the transport safety conditions, is the package design safety report (PDSR) for the transport version of the DPC. To ensure a safe transport in future to a destination which is not known yet (because of not yet existing repository sites) periodical reviews of the PDSR, in connection with periodic renewals of package design approval certificates, have to be carried out. The main reviewing tool is a gap analysis. A gap analysis for a PDSR is the assessment of the state of technical knowledge, standards and regulations regarding safety functions of structures, systems and components. T2 - 18th International Symposium on the Packaging and Transportation of Radioactive Materials PATRAM2016 CY - Kobe, Japan DA - 18.09.2016 KW - Radioactive material KW - Gap analysis KW - Periodical review KW - Approved packages PY - 2016 SP - Paper 5004, 1 EP - 9 AN - OPUS4-37641 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Patrick P. A1 - Lazik, D. A1 - Bartholmai, Matthias ED - Aulova, Alexandra ED - Rogelj Ritonja, A. ED - Emri, I. T1 - Validation of membrane-based linear soil gas sensors – results from repetitive CO2 injection experiments performed in the field N2 - This work presents first results from repetitive CO2 injection experiments performed on a recently built-up 400 m² soil test field with gas injection system. The test field contains 48 membrane-based linear gas sensors that were installed in several depths of the test field. Sensors for measuring meteorological parameters (e.g., wind / rain) and the parameters soil temperature, soil moisture, and groundwater level were installed additionally. T2 - 33rd Danubia- Adria Symposium on Advances in Experimental Mechanics CY - Portorož, Slovenia DA - 20.09.2016 KW - Distributed linear sensor KW - Gas distribution mapping and gas source localization KW - Gas storage areas KW - Membrane-based gas sensing KW - Subsurface monitoring PY - 2016 SN - 978-961-94081-0-0 SP - 174 EP - 175 CY - Ljubljana AN - OPUS4-37644 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schukar, Vivien A1 - Köppe, Enrico A1 - Hofmann, Detlef A1 - Westphal, Anja A1 - Sahre, Mario A1 - Beck, Uwe A1 - Gong, Xing A1 - Bartholmai, Matthias ED - Aulova, Alexandra ED - Rogelj Ritonja, A. ED - Emri, I. T1 - A contribution to intelligent automatic validation of structure-integrated fibre optic strain sensors N2 - Sensors integrated into devices and structures provide essential data to control, optimize or manage machines and structural components. In the last years, processes, applications and machine parts became more and more intelligent. Consequently, the need for sensor validation increased significantly in order to rely on sensor data and measurement results. Structure-integrated fibre optic strain sensors, such as fiber Bragg gratings (FBG), are of special interest in the composite manufacturing industry. This type of sensor makes it possible to gain information and to collect measurement data about entire production processes and whole life-time cycles of composite-made machine parts and structures. However, validation concepts and approaches for this type of sensors are barely reported in literature. Furthermore, all the reported activities have the drawback that the sensor diagnosis strategy is implemented as limited mathematical models and/or complex time-consuming spectral analysis tools which are applied in data post-processing loops. However, to automate sensor validation and to apply real-time and in-field sensor fault detection, it is necessary to acquire measurement data and information about the measurement reliability at the same time. T2 - 33rd Danubia- Adria Symposium on Advances in Experimental Mechanics CY - Portorož, Slovenia DA - 20.09.2016 KW - Fiber bragg grating KW - Magnetic field KW - Magnetostrictive metal coating KW - Self-diagnostic fiber optical sensor PY - 2016 SN - 978-961-94081-0-0 SP - 180 EP - 181 CY - Ljubljana AN - OPUS4-37645 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bartholmai, Matthias A1 - Werner, Klaus-Dieter A1 - Kohlhoff, Harald A1 - Helmerich, Rosemarie A1 - Daum, Werner ED - Aulova, Alexandra ED - Rogelj Ritonja, A. ED - Emri, I. T1 - Long-Term measurement of vertical displacements at the outer concrete bridges of the Berlin Main Station N2 - Berlin Main Station is the largest multi-level station in Europe. Its daily passenger number amounts to over 300.000. Structures built for such a large number of people require a high-level safety standard. The station was built on the inner city site of the historic Lehrter Bahnhof. The conditions for building and start of operation were challenging by several reasons. The typical sandy ground with a high level of groundwater makes the permanent static stability of such a complex structure difficult. Several completed, ongoing, and planned construction activities in the immediate vicinity of the station influence the ground settlement of the whole area. On basis of the structural design an impact prediction was calculated, which expected certain vertical displacements particularly between the single columns of the outer concrete bridges of the building. These columns support the glass roof construction, which only allows a defined limit of displacement. In order to avoid damage, a concept for monitoring and adjusting potentially occurring displacements was developed for installation at the outer bridges of the station. T2 - 33rd Danubia- Adria Symposium on Advances in Experimental Mechanics CY - Portorož, Slovenia DA - 20.09.2016 KW - Berlin Main Station KW - Differential displacements KW - Hydraulic levelling system KW - Laser-based displacement measuring system KW - Monitoring KW - Strain measurements PY - 2016 SN - 978-961-94081-0-0 SP - 166 EP - 167 CY - Ljubljana AN - OPUS4-37646 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Matthees, Wolfgang T1 - Tangent modulus method versus initial strain method T2 - 7th International Semiar on the Computational Aspects of the Finite Element Method CY - Chicago, Ill., USA DA - 29.08.1983 PY - 1983 SP - 289 EP - 328 AN - OPUS4-36658 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fuhrmann, Günter A1 - Kühne, Helmut T1 - Europäische Zusamenarbeit auf dem Gebiet des Holzschutzes PY - 1983 IS - 9 SP - 1 EP - 3 CY - Paris AN - OPUS4-36660 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wieser, Karol E. A1 - Tobisch, Karl A1 - Probst, Ulrich T1 - The elastomere gasket - a black sheep for quality assurance measures? T2 - 7th International symposium Packaging and Transportation of Radioactive Materials CY - New Orleans, La., USA DA - 15.05.1983 PY - 1983 VL - 2 SP - 1366 EP - 1369 AN - OPUS4-36579 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Niesel, Konrad T1 - Analyses aux rayons X sur microscope électronique à balayage PY - 1983 VL - 4 IS - 3 SP - 34 EP - 35 CY - Chartes, France AN - OPUS4-36690 LA - fra AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Buchhardt, Frank T1 - Review of Contributions to Session 6 - Applications T2 - Concrete Structures under impact and impulsive loading CY - Berlin, Germany DA - 02.04.1982 PY - 1983 AN - OPUS4-36646 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Buchhardt, Frank A1 - Magiera, Götz A1 - Matthees, Wolfgang T1 - A nonlinear 3D containment analysis for airplane impact T2 - 7th International Conference on Structural Mechanics in Reactor Technology CY - Chicago, Ill., USA DA - 29.08.1983 PY - 1983 SP - 439 EP - 446 AN - OPUS4-36649 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Buchhardt, Frank A1 - Yazdi, F. T1 - Analysis of optimum economic liner design T2 - 7th International Conference on Structural Mechanics in Reactor Technology CY - Chicago, Ill., USA DA - 29.08.1983 PY - 1983 SN - 0167-899x VL - H 1/7 SP - 37 EP - 44 AN - OPUS4-36652 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Magiera, Götz A1 - Czaika, Norbert T1 - On the theoretical assumption for stress measurement in concrete T2 - 7th International Conference on Structural Mechanics in Reactor Technology CY - Chicago, Ill., USA DA - 29.08.1983 PY - 1983 VL - H 1/10 SP - 61 EP - 68 AN - OPUS4-36654 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Niesel, Konrad T1 - The weathering behaviour of natural building stone PY - 1983 VL - 18 IS - 8 SP - 30 EP - 31 CY - London AN - OPUS4-36692 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Paatsch, Wolfgang A1 - Kiesner, A. T1 - Formation of highly corrosion resistant conversion layers by zinc anodizing T2 - 11th World Congress on Metal Finishing CY - Jerusalem, Israel DA - 21.10.1984 PY - 1984 SP - 389 EP - 391 PB - International Ltd. CY - Tel Aviv AN - OPUS4-36711 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grätz, Rainer T1 - Konformitätsbewertung mechanischer Ex-Betriebsmittel N2 - Ausgehend von den entsprechenden Artikeln des Vertrages über die Arbeitsweise der Europäischen Union /1/ lassen sich die Europäischen Richtlinien entsprechend der Zielrichtung der zugrundeliegenden Artikel folgendermaßen gliedern: - Richtlinien zur Harmonisierung des Handels (Beschaffenheitsrichtlinien) nach Artikel 114 (früher Artikel 95 EG-Vertrag) - Richtlinien über Mindeststandards zum Schutz der Arbeitnehmer (Arbeitsschutzrichtlinien) nach Artikel 153 (früher Artikel 137 EG-Vertrag) Diese Richtlinien sind von den Mitgliedsstaaten in ihre jeweiligen nationalen Rechtssysteme umzusetzen. Die Art und Weise der Umsetzung ist abhängig davon, zu welcher der beiden Gruppen die Richtlinie gehört. Richtlinien nach Artikel 114 sind in die entsprechenden Gesetze und Verordnungen so umzusetzen, dass die wesentlichen Forderungen unverändert übernommen werden. Beschaffenheitsanforderungen an Produkte, die Explosionsschutzanforderungen zu erfüllen haben, werden in Deutschland durch die 9. Verordnung zum Produktsicherheitsgesetz (9. ProdSV, Maschinenverordnung) /2/ und speziell für atmosphärische Bedingungen in der 11. Verordnung zum Produktsicherheitsgesetz (11. ProdSV, Explosionsschutzverordnung /3/ bis 19.4.2016 bzw. Explosionsschutzprodukteverordnung /4/ ab 20.04.2016) geregelt. Durch die 11. ProdSV wurde die Richtlinie 94/9/EG /5/ bzw. wird die Richtlinie 2014/34/EU /6/ in deutsches Recht überführt. Die Richtlinie 2014/34/EU gibt es seit dem 26. Februar 2014. Sie ersetzt die Richtlinie 94/9/EG. Die Frist für den Übergang von der Richtlinie 94/9/EG zur Richtlinie 2014/34/EU endet am 20. April 2016. Die Richtlinie 2014/34/EU ist eine Neufassung der Richtlinie 94/9/EG, wobei die Inhalte des sogenannten Neuen Rechtsrahmens einbezogen wurden. Die materiellen Anforderungen der Richtlinie 2014/34/EU unterscheiden sich nicht von denen der Richtlinie 94/9/EG. Wesentlicher Inhalt dieser Verordnungen und der Europäischen Richtlinie 2014/34/EU sind die Begriffsdefinitionen für Geräte, Schutzsysteme und Komponenten, das System der Konformitätsbewertung und die Konformitätserklärung, sowie die grundlegenden Sicherheits- und Gesundheitsanforderungen. Es gilt dabei das Prinzip der Herstellerverantwortung. Der Hersteller eines Produktes dokumentiert die Erfüllung der Richtlinienanforderungen mit seiner Konformitätserklärung und der Kennzeichnung des Produktes mit dem CE-Zeichen. T2 - 41. Heilbronner Ex-Schutz-Seminare "Planen, Errichten und Betreiben von Anlagen in explosionsgefährdeten Betriebsstätten" CY - Heilbronn, Germany DA - 02.03.2016 KW - Mechanische Ex-Betriebsmittel KW - Nichtelektrische Geräte KW - ATEX Richtlinie 2014/34/EU KW - Konformitätsbewertung KW - Kombinierte Geräte PY - 2016 SP - Paper 1 5, 10 AN - OPUS4-37476 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hofmann, Michael ED - Thinová, L. T1 - Proficiency test of commercial radon monitors for low level radon exhalation measurements in chambers with air exchange N2 - Compared to the designated European upper reference level of 300 Bq/m³ for indoor radon concentrations, the contribution of building materials appears to be low. Taking into account the recommended limit of 100 Bq/m³ by WHO as well as the increased dose conversion factor, the contribution of building products is quite relevant, especially at low air change rates. Therefore in Germany a maximum contribution of building materials to the indoor radon concentration of 20 Bq/m³ is discussed. Because measurements of low concentrations are associated with high uncertainties, radon exhalation rates are often determined in chambers without air exchange and indoor conditions are extrapolated. This study investigated the suitability of direct low level radon measurement under simulated indoor conditions with commercially available instruments, based on the preliminary EU standard for the determination of the emission of volatile organic compounds (VOC) from building materials in test chambers. Measurements are possible with a relative uncertainty ranging from 7 to 18%. Four major problems were identified: 1. Detector sensitivity: Two of four instruments were identified to determine low radon concentrations in a sufficiently short measuring time. 2. Thoron discrimination: Thoron was discriminated by aging the sampled air in a hose before the detector. 3. Sampling setup: An external chamber measurement was feasible as long as all main system parts were under slight overpressure. 4. Blank value: For VOC-emission testing ambient air, conditioned by filtration and sorption, is used to generate an air exchange. Regarding radon, this treatment is non-effective. If all instrument background levels have been characterized, the blank value must be measured with a second detector in parallel. T2 - 8th International Conference on Protection against Radon at Home and at Work CY - Prague, Czechia DA - 12.09.2016 KW - Radon exhalation KW - Building materials KW - Radon measurement KW - VOC emission test chamber PY - 2016 UR - http://www.radon2016.cz/download/radon2016-el.pdf?attredirects=0&d=1 SN - 978-80-01-05993-7 SP - 21 EP - 21 PB - České vysoké učení technické v Praze CY - Prague AN - OPUS4-37439 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grätz, Rainer T1 - Effects of the "new" ATEX Directive 2014/34/EU - consequences for manufacturers - claims by users N2 - Directive 94/9/EC of the European Parliament and of the Council of 23 March 1994 on the approx-imation of the laws of the Member States concerning equipment and protective systems intended for use in potentially explosive atmospheres has been substantially amended. The new ATEX Di-rective 2014/34/EU on equipment and protective systems intended for use in potentially explosive atmospheres replaces Directive 94/9/EC. The new Directive was published on March 29, 2014, became enacted on April 19, 2014 and will become effective starting April 20, 2016. It was the aim of the revision to harmonize the requirements with the New Legal Framework (New Legislative Framework - NLF). The NLF consists of the following two documents: the Regulation (EC) No 765/2008 of the European Parliament and of the Council of 9 July 2008, which sets out the re-quirements for accreditation and market surveillance relating to the marketing of products, and the Decision No 768/2008/EC of the European Parliament and of the Council of 9 July 2008, which sets on a common framework for the marketing of products. The harmonization with the NLF especially results in a lot of new definitions and a new structure compared with the “old” ATEX. Some content which was in the annexes of the “old” ATEX is now turned into distinct chapters or articles in the main part. New content was included which comprises things like presumption of conformity, principles of CE marking, notification of conformity as-sessment bodies, Union market surveillance, and Union safeguard procedure. What is more, the definitions of the economic operators like manufacturer, distributor and importer and the description of their duties are now in separate chapters. Thus, the “new” ATEX is much bigger than the “old” one. With the publication of the Directive 2014/34/EU a lot of questions were raised especially from manufacturers. These questions include: - Did everything change now? - Does the new Directive affect essential safety and health requirements (ESHR) for equipment and protective systems intended for use in hazardous areas? - Is the module system for conformity assessment changed? - What happens with existing certificates? - What happens with products which were already produced before April 20, 2016 but will be placed on the market later? The presentation will deal with some of these questions. But it has to be stated that the essential health and safety requirements for equipment and protective systems intended for use in potentially explosive atmospheres have not changed. That means: A product which was safe under the Directive 94/9/EC is still a safe product in the sense of the Directive 2014/34/EU. T2 - 3rd International Rotating Equipment Conference - Pump Users International Forum 2016 CY - Frankfurt/Main DA - 14.09.2016 KW - Directive 2014/34/EU KW - ATEX KW - New Legislative Framework KW - Explosion protection KW - Conformity assessment PY - 2016 SN - 978-3-8163-0697-9 SP - 9 EP - 17 PB - VDMA Pumps + Systems Association CY - Frankfurt/Main AN - OPUS4-37468 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Babutzka, Martin A1 - Burkert, Andreas A1 - Heyn, A. T1 - Corrosion investigations on zinc coatings by using gel-type electrolytes N2 - In the presentation different zinc coatings are presented and investigated. Their naturally formed protective layers are electrochemically characterized and corrosion relevant values are determined by using a gel pad based on polysaccharide. The corrosion relevant values allow the differentiation of various zinc coating systems and can describe the current protective effect provided by the coating. It is shown that gel-type electrolytes influence protective layers and coatings considerably less than corresponding bulk electrolytes. From the results it is evident that gel-type electrolytes represent a viable and promising field in corrosion research. T2 - 7th Kurt-Schwabe-Symposium CY - Mittweida, Germany DA - 04.09.2016 KW - zinc coatings KW - gel-type electrolytes KW - corrosion invetsigations PY - 2016 SP - 19 AN - OPUS4-37411 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schickert, Gerald T1 - Review of Contributions to Session 2 - Mechanical Properties of Materials T2 - RILEM-CEB-IABSE-IASS-Interassociation Symposium, Concrete Structures under impact and impulsive loading CY - Berlin, Germany DA - 02.06.1982 PY - 1983 SP - 36 EP - 38 AN - OPUS4-37488 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fuhrmann, Günter A1 - Plank, Arno T1 - Derzeitige und künftige Möglichkeiten zum Abbau von Handelshemmnissen technischer Art im Bauwesen T2 - Kolloquium am 4. und 5. Juni 1984 in Straßburg mit Förderung der Friedrich Ebert-Stiftung CY - Strasbourg, France DA - 04.06.1984 PY - 1984 N1 - Bulletin Sonderausgabe Nr. 10 SP - 71 EP - 78 CY - Straßburg AN - OPUS4-36795 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gierloff, Michael ED - Schulz, H. T1 - Die Wirkung von Zusatzstoffen auf der Basis von Polyacrylsäureester auf die Betoneigenschaften T2 - 4. Internationaler Kongreß Polymere und Beton CY - Darmstadt, Germany DA - 19.09.1984 PY - 1984 SP - 73 EP - 78 CY - Darmstadt AN - OPUS4-36796 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gierloff, Michael T1 - Studies on the mode of action of admixtures on the basis of polyacrylic-acid-esters in concrete T1 - Recherches sur l'efficacite de dispersions polymerisees a base d'esters polyacryliques dans le beton T2 - International Symposium CY - Lìege, Belgium DA - 04.06.1984 PY - 1984 SP - 1B.16.1 EP - 1B.16.3 CY - Lüttich AN - OPUS4-36797 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stichel, Wolfgang ED - Kruse, C. L. T1 - Elementkorrosion in Warmwasserheizungsanlagen T2 - Korrosion in Kalt- und Warmwassersystemen der Hausinstallation CY - Bad Nauheim, Germany DA - 08.09.1983 PY - 1984 SN - 3-88355-077-9 SP - 93 EP - 108 CY - Oberursel AN - OPUS4-36723 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Isecke, Bernd T1 - Einfluss einer Wasserstoffaufnahme bei Spannstählen auf die mechanischen Kennwerte im Zugversuch T2 - Tagung Werkstoffprüfung 1983 CY - Bad Nauheim, Germany DA - 08.12.1983 PY - 1984 VL - 1983 SP - 215 EP - 230 AN - OPUS4-36970 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Isecke, Bernd T1 - Korrosionsverhalten von schlaffer und vorgespannter Bewehrung in Betonbauteilen T2 - Korrosionum CY - Mannhein, Germany DA - 29.11.1984 PY - 1984 VL - 1984/4 SP - 29 EP - 38 AN - OPUS4-36973 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Martin A1 - Wille, Frank A1 - Droste, Bernhard T1 - Introduction of BAM safety assessment experience feedback list N2 - BAM as competent authority regarding assessment of mechanical and thermal design, activity release and quality assurance aspects of SNF and HLW transport packages developed a thesaurus of experience feedback topics from recent approval procedures. The list is structured according to the European PDSR guide. It involves issues, which from BAM point of view, needed clarification during last package design assessment procedures. The list contains issues from operation (e.g. deactivation of handling lugs not intended for package handling), maintenance (e.g. leak tightness of impact limiting devices) to technical assessment (e.g. formation of hydrogen by radiolysis and its impact on pressure and ignitability, consideration of ageing mechanisms, thermo-mechanical assessment, impact of gaps between content and flask, spent fuel behaviour) as well as to general and specific safety analysis report requirements (e.g. report structure and required data). T2 - PATRAM 2016 CY - Kobe, Japan DA - 18.09.2016 KW - Experience feedback list KW - Radioactive material KW - Transport PY - 2016 UR - http://www.patram2016.org/ SP - Paper 4002, 1 AN - OPUS4-37850 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Feldkamp, Martin A1 - Nehrig, Marko A1 - Bletzer, Claus A1 - Musolff, André A1 - Erenberg, Marina A1 - Wille, Frank T1 - Behaviour of Wood Filled Impact Limiters during Fire Test N2 - Packages for the transport of radioactive material are often equipped with impact limiters consisting of wood, encapsulated by steel sheets. These impact limiters shall ensure the transport cask meets the mechanical and thermal IAEA regulatory test requirements. After damage caused by the mechanical tests the package has to withstand a severe fire scenario. According to the regulations during and following the thermal test, the specimen shall not be artificially cooled and any combustion of materials of the package shall be permitted to proceed naturally. Corresponding to results of the French institute IRSN combustion and smouldering of wood inside the impact limiter occurred during and after the fire test. An additional energy supply from a pre-damaged impact limiter to the cask could be the consequence for the safety assessment of the containment. BAM started a first test phase to examine the issue of combustion for such kind of package components. The goal was to understand the phenomena under the consideration of relevant regulatory boundary conditions. Several metal buckets were filled with wood and equipped with thermocouples. The test specimens have been prepared with different damage arrangements to take the influence of the mechanical tests into account. This paper shows the experimental setup and the conduction of the tests. The first test shows that pre-damaged metal encapsulations can lead to smouldering of the wood and with this to a supplement energy release after the end of the 30 minute fire. BAM is in the preparation process for a second test phase. A thermal test will take place with a wood filled test specimen weighing about 2Mg. T2 - The 18th International Symposium on the Packaging and Transportation of Radioactive Materials (PATRAM 2016) CY - Kobe, Japan DA - 18.09.2016 KW - Large scale testing KW - Fire test KW - Impact limiter KW - Shock absorber KW - Thermal test KW - Typ-B KW - Wood KW - Smouldering PY - 2016 SP - paper no. 1011 AN - OPUS4-37854 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Mohrbacher, H. A1 - Vleugels, J. A1 - Huang, S. T1 - Substitution of tungsten carbide by niobium carbide as cutting materials and for wear protection N2 - Im binären System NbC-C existieren verschiedene Phasen im Homogenitätsbereich NbCₓ, mit 0,75 ≤ x ≤ 1,0, wie NbC, Nb₆C₅ und Nb₄ C₃ , die ein breites Prozessfenster beim Sintern und in der Werkstoffentwicklung ermöglichen. Die Mikrohärte, die Warmhärte, der Verschleißwiderstand, das Elastizitätsmodul und die Zähigkeit von Hartmetallen hängen vom C/Nb-Verhältnis ab, wie auch von der Zugabe von Sekundärcarbiden. N2 - Several phases, like Nb₄ C₃ , Nb₆C₅ and other short and long range ordered phases occur in the region of homogeneity of NbCₓ (0.75 ≤ x ≤ 1.0) in the binary phase diagram. Properties, like micro-hardness, hot hardness, sliding wear resistance, elastic modulus and toughness can be tailored by the C/Nb ratio, the addition of secondary carbides and the type of binder. Supporting results from different grades with varying C/Nb ratio or binder types were illuminated. Thus, the NbC system offers to producers a wider process window, than WC. The impact of these tailored properties on sliding wear and cutting performance was illuminated by tribological and machining results. Niobium is today largely available. NbC can be synthesized by carbothermal conversion of Nb₂O₅ or be metallurgically grown and leached out, provides comparably low friction in many relevant tribo-contacts and displays low wear. NbC and Nb₂O₅ have so far no REACH classification related to human toxicology and are not listed as substances of very high concern contrary to WO₃ and Co₃ O₄ . T2 - 57. Tribologie-Fachtagung CY - Göttingen, Germany DA - 26.09.2016 KW - cutting materials KW - niobium carbide KW - wear protection PY - 2016 SN - 978-3-9817451-1-5 SP - 65/1 EP - 65/14 AN - OPUS4-37833 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wolter, Christian A1 - Österle, Werner A1 - Gradt, Thomas T1 - Metal sulphides as friction stabilisers under variable humidity N2 - Neben Kohlenstoff werden Metallsulfide in jeder Standardrezeptur für Bremsbeläge als Reibungsstabilisatoren verwendet. Um deren Wirkung zu untersuchen, wurden verschiedene Pulvermischungen in einer Stift-Scheibe-Anordnung tribologisch beansprucht, um künstliche dritte Körper zu erzeugen und zu testen, deren definierte Zusammensetzungen aus drei wichtigen Bestandteilen einer realen Reibschicht bestehen: Magnetit, Graphit und div. Metallsulfide. N2 - Besides carbon, metal sulphides are used in every standard brake pad formulation as friction stabilisers. In order to investigate their impact, various powder mixtures were tribologically stressed in a pin-on-disc device in order to produce and test artificial third bodies. containing the three main components of a real friction film, namely magnetite, graphite and a metal sulphide of interest. Since the sliding behaviour is influenced by the relative humidity the powder mixtures are tested at low, medium and high moisture levels. The tests revealed that the presence of graphite dominates the friction behaviour as well as the humidity sensitivity. The powders were prepared by either manual mixing or high energy ball-milling. Interestingly, all ball-milled blends provided coefficients of friction within the desired range for braking, which was attributed to the effect of zirconia particles from wear debris of the milling balls. The zirconia particles prevent the formation of solid lubricant films on the surfaces and support a homogeneous mixture of all constituents of the powder. Optimum brake performance is gained by an optimum combination of solid lubricants and abrasives. T2 - 57. Tribologie-Fachtagung CY - Göttingen, Germany DA - 26.09.2016 KW - Friction KW - Metal sulphides KW - Brake pad formulation PY - 2016 SN - 978-3-9817451-1-5 SP - 1.5/1 EP - 1.5/6 AN - OPUS4-37838 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hüllmann, Dino A1 - Kohlhoff, Harald A1 - Erdmann, Jessica A1 - Neumann, Patrick P. ED - Aulova, Alexandra ED - Rogelj Ritonja, A. ED - Emri, I. T1 - Current-independent torque control of PMSM servo drives N2 - A permanent-magnet synchronous motor (PMSM) is controlled using measurements from a digital, optical incremental encoder. The motor speed is estimated from these measurement. Basic performance results are presented. T2 - 33rd Danubia Adria Symposium on Advances in Experimental Mechanics CY - Portorož, Slovenia DA - 20.09.2016 KW - BLDC KW - PMSM KW - Motor control KW - Servo drive PY - 2016 SN - 978-961-94081-0-0 SP - 172 EP - 173 PB - Narodna in univerzitetna knjižnica CY - Ljubljana, Slovenia AN - OPUS4-37813 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sickfeld, Jürgen T1 - Progress report on IUPAC's supported polymer films group T2 - IUPAC-Macromolecular division (MMD)-working party Supported polymer films Group's meeting CY - Duebendorf, Switzerland DA - 28.04.1983 PY - 1983 VL - 55 SP - 61 EP - 62 AN - OPUS4-37780 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Petrat, Torsten A1 - Graf, B. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Build-up strategies for generating components of cylindrical shape with laser metal deposition N2 - Laser Metal Deposition LMD) as additive manufacturing process offers the potential to produce near net shape components. This reduces the amount of material and post-processing. The components are composed of individual layers. Already mall irregularities within a layer can add up over multiple layers and lead to error propagation. This paper deals with the issue of build-up strategies to minimize irregularities and prevent error propagation. Different travel paths and the influence of a changing starting point regarding to error propagation are discussed. Different deposition rates between core and peripheral area are detected and successfully compensated by adjusting the build-up sequence. Stainless steel and titanium alloy Ti-6Al-4V are used in the experiments. The results are intended to illustrate the potential of an adjusted build-up strategy and provide basic information on the way to an automated deposition process. This paper is of interest for engineers in industry or science using LMD as additive manufacturing process. T2 - Lasers in Manufacturing Conference 2015 CY - Munich, Germany DA - 22.06.2015 KW - Ti - 6Al - 4V KW - Additive Manufacturing KW - Build - up Strategy KW - Laser Metal Deposition KW - Stainless Steel PY - 2015 UR - http://www.wlt.de/lim/Proceedings/Stick/sessions.html SP - 1 EP - 6 AN - OPUS4-37829 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz T1 - Die Bedeutung von Eisenbahn-Achsüberfahrten für die Bodenerschütterungen und Brückenschwingungen - Auswertung von Messungen verschiedener Länder N2 - Messungen bei Fern- und Hochgeschwindigkeitsbahnen aus verschiedenen Ländern (Portugal, Spanien, Belgien, Großbritannien, Deutschland, Schweiz, China, Japan u.a.) sollen die besondere Wichtigkeit eines mittelfrequenten Erschütterungsanteils zeigen. Relativ einheitlich werden dabei drei zusammenhängende Terzen mit angehobenen Amplituden beobachtet. Dieser Erschütterungsanteil dominiert mit zunehmender Entfernung vom Gleis das Frequenzspektrum der Erschütterungen. Die hochfrequenteren Anteile nehmen aufgrund der Materialdämpfung des Bodens stärker ab, die tieffrequenteren Anteile aus der sogenannten Quasistatik, der Vorbeifahrt der statischen Achslasten, verschwinden innerhalb der ersten zehn Meter vom Gleis fast vollständig. Die Frequenzcharakteristik des mittelfrequenten Erschütterungsanteils wird durch die Achsfolge des Zuges bestimmt. Im Terzmaßstab ist die Achsfolge im Drehgestell maßgeblich für die Ausprägung von zwei Amplitudenminima, die den Frequenzbereich eingrenzen. Diese Achsfolgespektren sind auch bei Brückenschwingungen von Bedeutung. Sie können die schwächere oder stärkere Anregung einzelner Brückeneigenschwingungen regeln. Die Ursachen der Boden- oder Brückenschwingungen sind mit den Achsfolgespektren noch nicht geklärt. Bei der Brücke und beim Boden können kurzwelligere Gleislagefehler (auch Radunrundheiten 1. Ordnung) Fahrzeugbeschleunigungen und damit dynamische Kräfte auf das Gleis erzeugen. Bei der Brücke ist die diskontinuierliche Auf- und Abfahrt der Achsen ebenfalls eine relevante Anregung, während die Kraftimpulse auf das Gleis, die durch die Achsüberfahrten entstehen, für die Wellenausbreitung im Boden von Bedeutung sind. Heterogene Böden oder Gleise ergeben einen Zerstreuanteil der Achsüberfahrtimpulse. Fallbeispiele mit verschiedenen Böden und verschiedenen Fahrgeschwindigkeiten werden ausgewertet, um die Ursachen und Gesetzmäßigkeiten des mittelfrequenten Erschütterungsanteils zu erkennen. T2 - Dynamik Tage Wien 2016 CY - Vienna, Austria DA - 06.10.2016 KW - Bodeneigenschaften KW - Bahnerschütterungen KW - Frequenzbereiche KW - Erschütterungsursachen PY - 2016 AN - OPUS4-37945 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Beck, Uwe T1 - Multidimensional Methods for Industrial Quality Assurance N2 - The paper addresses the „Multidimensional Methods for Industrial Quality Assurance“ and the following points are discussed in more detail: thin film analysis, major trends regarding optical measuring methods. KW - optische Konstanten KW - Ellipsometrie KW - Klassifizierungssystem KW - Optical konstantyss KW - Ellipsometry KW - Classification stem PY - 2015 SP - 35 EP - 35 AN - OPUS4-37949 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Molnarne, M. A1 - Schröder, Volkmar T1 - Flammability of Gases in Focus of European and US Standards N2 - The presentation will discuss the difference between EU and US standards for the determination of explosion (flammability) limits and limiting oxygen concentration. Small differences observed in measured values can be traced back to the different test apparatuses and criteria. The discrepancies can be much greater in the case of limiting oxygen concentration because of the high amount of inert gases and the corresponding low laminar burning velocities. The paper describes some examples and the influence of the chosen criteria on the results. The European and US standards use the criteria of flame propagation in open test vessels and of pressure rise in closed ones. The examples discussed show that flame propagation is still possible at very small pressure rise values, as observed much below the pressure rise criterion of usual standards. However, flame propagation in a process plant can cause an accident or explosion and must be avoided. Therefore, the flame propagation criterion is recommended to be used in chemical safety engineering. The European safety database CHEMSAFE contains expert-evaluated safety data for cases where the determination method and criteria are known. Flammability characteristics based on the pressure rise criterion may suffice in certain cases, e.g. for explosion protection in closed vessels without any connecting pipes. T2 - 2016 International Symposium on Safety Science and Technology CY - Kunming, China DA - 17.10.2016 KW - Flammability KW - Limiting oxygen concentration KW - Standardization KW - Explosion protection KW - Test methods PY - 2016 VL - Vol. XI SP - 400 EP - 409 AN - OPUS4-37951 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Salge, T. A1 - Nolze, Gert T1 - Innovations in EDS and EBSD Microanalysis: Hyperspectral Imaging for Planetological Applications Using Silicon Drift Detectors (SDD) and EBSD N2 - Within the last decade, silicon drift detectors (SDD) systems have become more and more popular in the field of energy-dispersive spectroscopy (EDS). The main characteristic of the SDDs is their extremely high pulse load capacity of up to 750,000 counts per second at good or reasonable energy resolution (<123eV Mn-Kα, <46eV C-Kα at 100.000 cps). These properties in conjunction with electron backscatter diffraction (EBSD) techniques and modern data processing make a range of innovative analysis options possible, not only high speed mapping but also hyperspectral imaging techniques. T2 - 72nd Annual Meeting of the Meteoritical Society CY - Nancy, France DA - 13.07.2009 KW - Electron backscatter diffraction KW - Energy dispersive x-ray spectroscopy KW - Method combination PY - 2009 VL - Suppl. SP - 5270 AN - OPUS4-38002 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Kranzmann, Axel T1 - Borehole integrity of austenitized and annealed pipe steels suitable for carbon capture and storage (CCS) N2 - Properties of pipe steels for CCS (carbon capture and storage) technology require resistance against the corrosive environment of a potential CCS-site (heat, pressure, salinity of the aquifer, CO2-partial pressure). The influence of austenitzing in heat treatment routines of two different injection pipe Steels (1.4034, X46Cr13 and 1.4021, X20Cr13) was evaluated. Steel coupons were austenitized at different temperatures (900- 1050 °C) for different lengths of time (30-90 min) before quenching and annealing prior to long term corrosion experiments (60°C, 100 bar, artificial brine close to a CCS-site in the Northern German Basin, Germany). In general, fewer pits are found on X46Cr13. Comparing steels with 13% chromium each the higher carbon content of X46Cr13 (0.46% C) results in a lower number of pits compared to X20Cr13 (0.20% C). It is found that neither the carbon content of the steels nor austenitizing temperature has much influence, but local corrosion behaviour is most susceptible towards austenitzing time. T2 - 2016 APCBEES Pattaya Conference CY - Pattaya, Thailand DA - 23.01.2016 KW - Heat Treatment KW - CCS KW - CO2 KW - Corrosion KW - Steel PY - 2016 AN - OPUS4-38444 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Daschewski, Maxim T1 - Thermophony in real gases - Theory and applications N2 - A thermophone is an electrical device for sound generation. The advantages of thermophones over conventional sound transducers such as electromagnetic, electrostatic or piezoelectric transducers are their operational principle which does not require any moving parts, their resonance-free behavior, their simple construction and their low production costs. In this PhD thesis, a novel theoretical model of thermophonic sound generation in real gases has been developed. The model is experimentally validated in a frequency range from 2 kHz to 1 MHz by testing more than fifty thermophones of different materials, including Carbon nano-wires, Titanium, Indium-Tin-Oxide, different sizes and shapes for sound generation in gases such as air, argon, helium, oxygen, nitrogen and sulfur hexafluoride. Unlike previous approaches, the presented model can be applied to different kinds of thermophones and various gases, taking into account the thermodynamic properties of thermophone materials and of adjacent gases, degrees of freedom and the volume occupied by the gas atoms and molecules, as well as sound attenuation effects, the shape and size of the thermophone surface and the reduction of the generated acoustic power due to photonic emission. As a result, the model features better prediction accuracy than the existing models by a factor up to 100. Moreover, the new model explains previous experimental findings on thermophones which cannot be explained with the existing models. The acoustic properties of the thermophones have been tested in several gases using unique, highly precise experimental setups comprising a Laser-Doppler-Vibrometer combined with a thin polyethylene film which acts as a broadband and resonance-free sound-pressure detector. Several outstanding properties of the thermophones have been demonstrated for the first time, including the ability to generate arbitrarily shaped acoustic signals, a greater acoustic efficiency compared to conventional piezoelectric and electrostatic airborne ultrasound transducers, and applicability as powerful and tunable sound sources with a bandwidth up to the megahertz range and beyond. Additionally, new applications of thermophones such as the study of physical properties of gases, the thermo-acoustic gas spectroscopy, broad-band characterization of transfer functions of sound and ultrasound detection systems, and applications in non-destructive materials testing are discussed and experimentally demonstrated. N2 - Ein Thermophon ist ein elektrisches Gerät zur Schallerzeugung. Aufgrund der fehlenden beweglichen Teile verfügen Thermophone über mehrere Vorteile gegenüber den herkömmlichen elektromagnetischen, elektrostatischen oder piezoelektrischen Schallwandlern. Besonders bemerkenswert sind das resonanz- und nachschwingungsfreie Verhalten, die einfache Konstruktion und die niedrigen Herstellungskosten. Im Rahmen dieser Doktorarbeit wurde ein neuartiges theoretisches Modell der thermophonischen Schallerzeugung in Gasen entwickelt und experimentell verifiziert. Zur Validierung des Modells wurden mehr als fünfzig Thermophone unterschiedlicher Größen, Formen und Materialien, darunter Kohlenstoff-Nanodrähte, Titan und Indium-Zinnoxid zur Erzeugung von Schall in Gasen wie Luft, Argon, Helium, Sauerstoff, Stickstoff und Schwefelhexafluorid in einem Frequenzbereich von 2 kHz bis 1 MHz eingesetzt. Das präsentierte Modell unterscheidet sich von den bisherigen Ansätzen durch seine hohe Flexibilität, wobei die thermodynamischen Eigenschaften des Thermophons und des umgebenden Gases, die Freiheitsgrade und das Eigenvolumen der Gasatome und Moleküle, die Schallschwächungseffekte, die Form und Größe des Thermophons, sowie die Verringerung der erzeugten akustischen Leistung aufgrund der Photonenemission berücksichtigt werden. Infolgedessen zeigt das entwickelte Modell eine um bis zu einem Faktor 100 höhere Vorhersagegenauigkeit als die bisher veröffentlichten Modelle. Das präsentierte Modell liefert darüber hinaus eine Erklärung zu den Ergebnissen aus den Vorarbeiten, die von den bisherigen Modellen nicht abschließend geklärt werden konnten. Die akustische Eigenschaften der Thermophone wurden unter Verwendung von einzigartigen hochpräzisen Versuchsaufbauten getestet. Dafür wurde ein Laser-Doppler-Vibrometer in Kombination mit einer dünnen Polyethylenfolie verwendet, welche als breitbrandiger und resonanzfreier Schalldruckdetektor fungiert. Somit konnten mehrere herausragende akustische Eigenschaften der Thermophone zum ersten Mal demonstriert werden, einschließlich der Möglichkeit, beliebig geformte akustische Signale zu erzeugen, eine größere akustische Wirksamkeit im Vergleich zu herkömmlichen Luftultraschallwandlern und die Anwendbarkeit als leistungsfähige beliebig abstimmbare Schallquellen mit einer Bandbreite bis in den Megahertz-Bereich. Zusätzlich werden neue Anwendungen von Thermophonen wie die Untersuchung der physikalischen Eigenschaften von Gasen, die thermoakustische Gasspektroskopie, eine breitbandige Charakterisierung der Übertragungsfunktionen von Schall- und Ultraschallmesssystemen und Anwendungen in der zerstörungsfreien Materialprüfung demonstriert. KW - Acoustic actuator KW - Thermoacoustics KW - Sound source PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:517-opus4-98866 SP - 1 EP - 85 PB - Universität Potsdam CY - Potsdam AN - OPUS4-38344 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rohwetter, Philipp A1 - Eisermann, René A1 - Großwig, S. A1 - Krebber, Katerina T1 - Fibre-optic distributed acoustic and vibration sensing for monitoring of industrial plants and installations N2 - We propose the application of Distributed Acoustic Sensing (DAS) based on Rayleigh Coherent Optical Time-Domain Reflectometry (C-OTDR) to unconventional sensing tasks in industrial condition monitoring. As examples we present results on the way to fibre-optic remote sensing of dielectric damage processes in high voltage cable joints as well as to condition monitoring of passive rollers in large industrial belt conveyor systems. T2 - International Conference on Smart Infrastructure and Construction CY - Cambridge, UK DA - 27.06.2016 KW - Distributed sensing KW - C-OTDR KW - Strain measurement KW - Structural health monitoring PY - 2016 UR - http://www.icevirtuallibrary.com/doi/abs/10.1680/tfitsi.61279.063 SN - 978-0-7277-6127-9 DO - https://doi.org/10.1680/tfitsi.61279.063 SP - 63 EP - 68 PB - ICE Publishing CY - London, UK AN - OPUS4-38411 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe T1 - Schadensentwicklung und Schadenstoleranz von SLM-gefertigten Werkstoffen N2 - Unterschiedliche Werkstoffeigenschaften reagieren auf jeweils spezifische Weise auf Gittertyp, Gefüge und Defekte. Für die schadenstolerante Betrachtung von Werkstoff und Bauteil ist das Verständnis dieser Zusammenhange essentiell. Der Beitrag gibt mit Hinblick auf additiv gefertigte metallische Bauteile (Selective Laser Melting) einen kurzen, keineswegs vollständigen Überblick über Faktoren, die die Steifigkeit, Festigkeit, Duktilität, Zähigkeit, Ermüdungsrissausbreitung und Schwingfestigkeit beeinflussen. Es wird aufgezeigt, wie die bruchmechanische Betrachtung zur Quantifizierung der zusammenhänge beitragen kann. T2 - 1. Tagung des Arbeitskreises Additiv gefertigte Bauteile und Strukturen CY - Berlin, Germany DA - 02.11.2016 KW - Selective Laser Melting (SLM) KW - Werkstoffeigenschaften KW - Schadenstoleranz KW - Bruchmechanik PY - 2016 SN - 2509-8772 VL - Bericht 401 SP - 187 EP - 212 AN - OPUS4-38420 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brosig, Laura A1 - Horn, Wolfgang A1 - Jann, Oliver T1 - Method-verification and optimisation of the standardised assessment of odour intensity regarding ISO 16000-28 N2 - Besides measurement of VOC emissions also the evaluation of odour emissions and the perceived intensity of odours gains in importance. Due to difficulties detected in the measurement method of the perceived intensity described in (ISO 16000-28, 2012) the introduction of “reference” odours will be recommended for the training of panellists and as basis for interlaboratory comparisons. In order to generate the “reference” odours standard liquid substances were directly injected into the main gas flow provided to the panellists. One of the substances tested was ethyl acetate. A pre-evaluation was conducted with six untrained panellists and has shown that ethyl acetate is potentially suitable as reference odour. For further validation of those “reference” odours they additionally will be provided to and evaluated by trained panellists of well established-measurement institutes. T2 - Indoor Air 2016 The 14th international conference of Indoor Air Quality and Climate CY - Ghent, Belgium DA - 03.07.2016 KW - Odour assessment KW - Perceived odour intensity KW - Reference odour KW - Emission testing KW - Building products PY - 2016 SN - 978-0-9846855-5-4 SP - Paper 568, 1 EP - 6 AN - OPUS4-38373 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Karrasch, S. A1 - Jörres, R. A1 - Ehret, M. A1 - Herbig, B. A1 - Schierl, R. A1 - Seeger, Stefan A1 - Langner, J. A1 - Nowak, D. ED - Hildenbrandt, Sibylle ED - Rieger, Monika A. T1 - Untersuchung möglicher gesundheitlicher Gefährdungen durch Drucker- und Kopierer-Emissionen Teil 1 und 2 N2 - Teil 1: In der Öffentlichkeit werden immer wieder mögliche gesundheitliche Auswirkungen von Laserdruckeremissionen diskutiert. Um diese möglichen Auswirkungen genauer zu analysieren, wurden die Effekte 75-minütiger Expositionen von sogenannten Low-Emittern (LE, Untergrund 2000-4000 UFP/cm3) gegenüber High-Emittern (HE, 100.000 UFP/cm3) untersucht. Teil 2: Mögliche gesundheitliche Auswirkungen von Laserdruckeremissionen sind immer wieder Gegenstand öffentlicher Aufmerksamkeit. Die dabei auftretenden potenziellen psychologischen Aspekte, wurden in einem standardisierten Szenario mittels 75-minütiger Expositionen gegenüber Low-Emittern (LE, Untergrund 2000-4000 UFP/cm3) und High-Emittern (HE, 100.000 UFP/cm3) untersucht. T2 - 55. Jahrestagung der DGAUM 2015 CY - Munich, Germany DA - 18.03.2015 KW - Gesundheitsgefährdung KW - Laserdrucker KW - Bürogeräte KW - Partikel KW - Emissionen PY - 2015 SN - 978-3-9817007-1-8 SP - 357 EP - 489 PB - Geschäftsstelle der Deutschen Gesellschaft für Arbeitsmedizin und Umweltmedizin e. V. CY - München AN - OPUS4-38751 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Niederleithinger, Ernst T1 - State-of-the-art of Ultrasonic Monitoring of Concrete N2 - Ultrasonic methods are well established in various aspects of concrete testing. They are used for imaging the interior geometry of constructions, estimation of concrete strength or monitoring lab investigations. However, so far the detection of distributed damages, especially in an early stage, has been almost impossible. The arrival of new technologies as deep penetration ultrasonic echo devices, new imaging techniques, embedded transducers for permanent monitoring and sensitive data processing techniques adopted from seismology have opened new fields of work. Recent research has been focused to detect changes in concrete elements induced by stress, temperature, moisture or chemical attacks. KW - Ultrasound KW - Concrete KW - Monitoring KW - Imaging PY - 2016 IS - 10 SP - 15 EP - 18 AN - OPUS4-38728 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Wäsche, Rolf A1 - Brandt, Guido A1 - Ehrke, Roman A1 - Yano, S. A1 - Sasaki, S. T1 - Tribology in hot steam for energy recovery N2 - The wear rates of self-mated alumina couples show that friction as well as wear is largely determined by the above-mentioned hydro-thermal conditions. The presence of water and its amount available in the surrounding system either in liquid or in gaseous form plays a key role for friction and wear behavior and can be beneficial for the tribological profile of steam degradation resistant materials. Hot steam enhances the tribo-chemical formations of oxides and hydroxides on MgO-ZrO2 alumina and antimony impregnated carbon. T2 - 21th International Colloquium Tribology CY - Stuttgart/Ostfildern, Germany DA - 09.01.2018 KW - Tribology KW - Friction KW - Alumina KW - Hot steam PY - 2018 SP - 1 EP - 2 AN - OPUS4-43896 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Babutzka, Martin A1 - Burkert, Andreas T1 - Untersuchungen zur Versalzung von Metalloberflächen im maritimen Bereich N2 - Die Versalzung und Verunreinigung von Metalloberflächen durch chloridhaltige Aerosole hat eine große Bedeutung für das Korrosionsverhalten von beschichteten Metalloberflächen im maritimen Bereich und bei Offshore-Anwendungen. So ist z. B. zu klären, ob und in welchem Maße eine Versalzung der Oberfläche Einfluss auf die Haftung und Dauerhaftigkeit von Beschichtungen hat. Dafür sind Detailfragen zu klären, etwa mit welcher Versalzung nach welchem Zeitraum zu rechnen ist oder wie für systematische Untersuchungen eine definierte und reproduzierbare Versalzung im Labor nachgestellt werden kann. Der Beitrag widmet sich diesen Fragestellungen. Es werden Ergebnisse eines Feldversuches auf Helgoland gezeigt und ein einfaches Verfahren zur definierten Beladung von Metalloberflächen mit Chloriden im Labormaßstab vorgestellt. T2 - 17. Tagung "Korrosionsschutz in der maritimen Technik" CY - Hamburg, Germany DA - 24.01.2018 KW - Maritime Atmosphäre KW - Maritime atmosphere KW - Versalzung KW - Salinization PY - 2018 SN - 978-3-935406-65-9 VL - 17 SP - 87 EP - 102 AN - OPUS4-43937 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Patrick P. A1 - Bennetts, V. H. A1 - Lilienthal, A.J. A1 - Bartholmai, Matthias T1 - From Insects to Micro Air Vehicles - A Comparison of Reactive Plume Tracking Strategies N2 - Insect behavior is a common source of inspiration for roboticists and computer scientists when designing gas-sensitive mobile robots. More specifically, tracking airborne odor plumes and localization of distant gas sources are abilities that suit practical applications such as leak localization and emission monitoring. Gas sensing with mobile robots has been mostly addressed with ground-based platforms and under simplified conditions and thus, there exist a significant gap between the outstanding insect abilities and state of the art robotics systems. As a step towards practical applications, we evaluated the performance of three biologically inspired plume tracking algorithms. The evaluation is carried out not only with computer simulations, but also with real-world experiments in which, a quadrocopter-based micro Unmanned Aerial Vehicle autonomously follows a methane trail towards the emitting source. Compared to ground robots, micro UAVs bring several advantages such as their superior steering capabilities and fewer mobility restrictions in complex terrains. The experimental evaluation shows that, under certain environmental conditions, insect like behavior in gas-sensitive UAVs is feasible in real world environments. T2 - 13th International Conference on Intelligent Autonomous Systems (IAS) CY - Padova, Italy DA - 15.07.2014 KW - Autonomous micro UAV KW - Mobile robot olfaction KW - Gas source localization KW - Reactive plume tracking KW - Biologically inspired robots PY - 2014 SP - 1 EP - 12 AN - OPUS4-43920 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schlegel, Moritz-Caspar A1 - Simo, Anne A1 - Palkowski, Carsten A1 - Kniechewski, Arno A1 - Akkerman, Floris T1 - Following the evidence – How quality of appliance components can hint at non-compliance with efficiency requirements N2 - Improving the energy efficiency of products was identified as the most important short-term opportunity to decrease energy consumption and therefore CO2-emission worldwide. More efficient products are created due to technical innovation. Restricting market access to efficient products only and making the most efficient products stand out by energy labelling are legislative approaches to encourage this development. Market surveillance authorities’ checks are fundamental to protect the consumer from wrongly declared goods on the market and ensure fair competition between manufacturers. However, the activities of market surveillance authorities are limited by their financial resources. Testing all product efficiency parameters in an accredited laboratory is very time consuming and cost intensive. In this article, a theoretical concept is presented which can be used to develop screening tests enabling market surveillance authorities to perform product tests with less financial resources. The concept identifies components which lead to non-compliance or make a product less energy efficient with minimum effort. The principle is based on a combination of random product tests, disassembling specific products and comparing components. This represents a new approach in product testing procedures beyond the current market surveillance activities. The concept is being tested within a research project funded by the German government. T2 - EEDAL'17 CY - Irvine, CA, USA DA - 13.09.2017 KW - Methodology KW - Market surveillance KW - Ecodesign PY - 2018 UR - http://publications.jrc.ec.europa.eu/repository/handle/JRC109209 SN - 978-92-79-77173-6 DO - https://doi.org/10.2760/68449 SN - 1018-5593 VL - 3 SP - 1113 EP - 1116 PB - Publications Office of the European Union CY - Luxembourg AN - OPUS4-43925 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Moldenhauer, Laura A1 - Helmerich, Rosemarie A1 - Köppe, E. A1 - Wittmann, J. ED - Cosmi, F. T1 - Experimental modeling approach for determining the moisture damping exponent of a Bluetooth Low Energy signal in moist building material N2 - The presented development of a damping model is a research component of an experimental feasibility study about moisture in building materials measured with Bluetooth® Low Energy (BLE) signals. This study may be part of a structural health monitoring aiming on early damage detection in the built infrastructure and is increasingly focusing on wireless sensor Network technology. It is investigated, how the Received Signal Strength Indicator (RSSI) of a BLE signal, transmitted from the BLE-module embedded in building materials with changing moisture content is damped. The BLE-module communicates with a mobile Smart Device as tablet or mobile phone via 2.45 GHz-ISMfrequency band where water dipoles start to oscillate. If the BLE-signal transfers through a moist material, the moisture Content influences the RSS-Indicator. The damping model demonstrates this damping effect on RSSI by the abstraction of the reality observed in a real system. T2 - 34th Danube Adria Symposium CY - Trieste, Italy DA - 19.09.2017 KW - Moisture damping coefficient, KW - Buliding materials KW - Bluetooth Low Energy KW - RSSI KW - Experimental approach PY - 2017 SN - 978-88-8303-863-1 DO - https://doi.org/https://www.openstarts.units.it/handle/10077/14834 SP - 141 EP - 142 CY - Trieste, Italy AN - OPUS4-44528 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hielscher, Stefan A1 - Beck, Uwe A1 - Lange, Thorid A1 - Grunwald, Daniel A1 - Stockmann, Jörg M. A1 - Lerche, D. A1 - Rietz, U. T1 - Die Zentrifuge als universelles Prüfsystem für Beanspruchungen auf Zug und Druck N2 - Mit der Zentrifugentechnologie ist seit einigen Jahren ein neuartiges Mehr-Proben-Prüf-verfahren auf dem Markt etabliert, welches die klassische Zugprüfung in den Trommelrotor einer Tischzentrifuge überträgt. In der Beanspruchung auf Zug ist die Prüfung der Verbundfestigkeit seit 2017 nach DIN EN ISO/IEC 17025 akkreditiert, wobei die Verbundfestigkeit von Klebungen direkt bestimmt wird und in Abhängigkeit von den Versagensformen Rückschlüsse auf die Klebfestigkeit von Klebstoffen/Klebebändern oder die Haftfestigkeit von Beschichtungen gezogen werden können. Bei der zerstörenden Beanspruchung auf Zug ist zu beachten, dass es sich bei der Verbundfestigkeit um eine Systemeigenschaft handelt, d.h. nicht nur die chemischen und topografischen Oberflächeneigenschaften, sondern auch die plasto-elastischen Volumeneigenschaften des Klebstoffes und der Fügeteile haben Einfluss auf die ermittelten Kennwerte. Dabei ist eine qualitative Bestimmung der Versagensformen und Bruchbilder nach DIN EN ISO 10365 zwingend erforderlich, um eine Aussage über die Art des Versagens treffen zu können. Mit der Erweiterung der Zentrifugentechnologie um Beanspruchungen auf Druck wurde dann der Nachweis erbracht, dass auch die klassische Härteprüfung in einer Zentrifuge als Mehr-Proben-Prüfung durchgeführt werden kann. Im Verbundvorhaben QUO VADIS PLUS werden derzeit invasive Beanspruchungen auf Druck zur Bestimmung der Härte von Materialien, der Kompressibilität von Metallschäumen sowie der Kompaktierbarkeit von Pulvern untersucht, was das Anwendungspotential der Zentrifugentechnologie nochmals erweitert. Dazu gehören auch kombinierte Beanspruchungen wie Zug-Scher- und Druck-Scher-Prüfungen. Die Verbundfestigkeit von CFK-Platten in Abhängigkeit der Beanspruchungsart (Zug vs. Zug-Scher) bzw. der Faserorientierung (0°, 45°, 90°), die Klebfestigkeit von Klebstoffen bzw. Klebebändern auf unterschiedlichen Fügeteilwerkstoffen in Abhängigkeit von der Vorbehandlung, die Haftfestigkeit optischer Schichten auf Kunststoffen, die Bestimmung der Vickers-, Brinell- bzw. Kugeldruck-Härte sowie die Kompressibilität von metallischen Schäumen und Federn werden als ausgewählte Beispiele diskutiert. T2 - 13. ThGOT Thementage Grenz- und Oberflächentechnik und 11. Thüringer Biomaterial-Kolloquium CY - Zeulenroda, Germany DA - 13.03.2018 KW - Zentrifugentechnologie KW - Haftfestigkeit KW - Härteprüfung KW - Mehr-Proben-Prüfung KW - Beanspruchung auf Zug und Druck PY - 2018 SN - 978-3-00-058187-8 SP - 1 EP - 5 CY - Jena AN - OPUS4-44572 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stajanca, Pavol A1 - Krebber, Katerina T1 - Polymer optical fibers for sensing applications: Ionizing radiation monitoring N2 - In the last decades, considerable attention has been paid to the development of polymer optical fibers (POFs) that may in certain cases represent more suitable or cost-effective alternative to their glass-based counterparts. Among other applications, special attention was paid to the utilization of optical fiber sensors in radiation environments. A concept of attenuation-based radiation sensing with perfluorinated POFs is here presented as a potential candidate for low-cost easy-to-use on-line radiation monitoring system. T2 - The Fiber Society 2017 Spring Conference: Next Generation Fibers for Smart Products CY - Aachen, Germany DA - 17.05.2017 KW - Polymer optical fibers KW - Radiation monitoring KW - Cytop PY - 2017 SP - 50 AN - OPUS4-43026 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Otremba, Frank A1 - Romero-Navarrete, José A. T1 - Modelling a partly filled road tanker during an emergency braking N2 - A simplified model, based upon physical principles, is proposed the simulate the effect of sloshing on the pressure developed in the tanker chambers. The model has been validated in good extent, with experimental data from full scale testing. The characteristic that mostly affects the pressure developed with the chambers of the tanker is the length of the chamber. While a reduction in this property could decrease the pressure developed within a given chamber, the analysis should take into account an overall approach, as a shortening of the individual chambers would influence the number of chambers necessary to carry a certain amount of product. Consequently, the resulting model could be used to study different effects of the sloshing cargo on the carrying vehicles, including the length and position of the chambers along the tanker body. T2 - WCECS 2017 CY - San Francisco, CA, USA DA - 25.10.2017 KW - Braking KW - Emergency KW - Tanker PY - 2017 UR - http://www.iaeng.org/publication/WCECS2017/ SN - 978-988-14048-4-8 SN - 2078-0958 VL - II SP - 610 EP - 614 AN - OPUS4-42957 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Mohrbacher, H. T1 - The tribological property profile of hard metals and metal matrix composites based on niobium carbide N2 - This work is focused on the tribological profile of NbC-based material, as well as their potential applications and environmental implications. T2 - International Symposium on Wear Resistant Alloys for the Mining and Processing Industry CY - Sao Paulo, Brazil DA - 04.05.2015 KW - Niobium carbide KW - Metal KW - Binder KW - Metal matrix composite KW - Friction KW - Wear KW - Hardness KW - Solubility KW - Toughness KW - Abrasion PY - 2018 SN - 978-0-692-05382-9 SP - 427 EP - 461 AN - OPUS4-44201 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Huang, S. G. A1 - Vleugels, J. A1 - Mohrbacher, H. A1 - Woydt, Mathias T1 - NbC-based cermets: influence of secondary carbide addition and metal binder N2 - Full densification of Fe, Co and Ni bonded NbC based cermet’s was achieved by pressure less liquid phase sintering in vacuum for one hour at 1420°C. The hardness and toughness of the NbC matrix cermet’s can be mainly tailored by the binder composition and secondary carbide additions. Ni binder based NbC cermet’s allow the combination of high hardness and improved toughness. The addition of lesser amounts of VC/Cr3C2 in a NbC partially substituted WC-Co cemented carbide increased significantly the hardness in combination with a moderate fracture toughness. T2 - International Symposium on Wear Resistant Alloys for the Mining and Processing Industry CY - Sao Paulo, Brazil DA - 04.05.2015 KW - Niobium carbide KW - Hardmetal KW - Cemented carbide KW - Sintering KW - Grain growth KW - Microstructure KW - Hardness KW - Fracture toughness PY - 2018 SN - 978-0-692-05382-9 SP - 521 EP - 534 AN - OPUS4-44206 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Le Quilliec, G. A1 - Leroy, R. A1 - Richard, C. A1 - Woydt, Mathias A1 - Morandeau, A. T1 - Comparison of the life-span of NbC-Co and WC-Co inserts during different machining operations on 100Cr6 (SAE 52100) bearing steel N2 - The aim of the study presented in this paper is to highlight the potential of niobium carbide cutting tool inserts for machining and to compare their performance to commercially available tungsten carbide inserts. In this work, a comparison between a conventional Wc-Co insert and NbC-Co inserts was carried out under hard machining conditions on specimens made of 100Cr6 bearing steel grade (SAE 52100). T2 - International Symposium on Wear Resistant Alloys for the Mining and Processing Industry CY - Sao Paulo, Brazil DA - 04.05.2015 KW - Niobium carbide KW - Cobalt KW - Fe3Al KW - Inserts KW - Cutting tools KW - Wear KW - Turning PY - 2018 SN - 978-0-692-05382-9 SP - 535 EP - 545 AN - OPUS4-44207 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Genga, R. M. A1 - Cornish, L. A. A1 - Woydt, Mathias A1 - Sobiyi, K. A1 - Polese, C. T1 - Wear and Mechanical properties of spark plasma and liquid phase sintered WC and NbC based cemented carbide inserts N2 - The effects on the mechanical properties, thermal behavior, response to cutting forces and wear mechanisms have been investigated for different manufacturing processes and materials for cemented carbide inserts. T2 - International Symposium on Wear Resistant Alloys for the Mining and Processing Industry CY - Sao Paulo, Brazil DA - 04.05.2015 KW - WC KW - NbC KW - SPS KW - Co KW - Fe3Al KW - Hard-turning KW - Interrupted milling KW - Flank KW - Wear KW - Coolant-free KW - Crater wear KW - Machinability PY - 2018 SN - 978-0-692-05382-9 SP - 547 EP - 567 AN - OPUS4-44208 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Komann, Steffen A1 - Gröke, Carsten A1 - Wille, Frank T1 - Assessment of quality management for transport packages not requiring authority design approval N2 - The majority of transports of radioactive materials are carried out in packages which don’t need a package design approval of a competent authority. Low active radioactive materials are transported in such kind of packages e.g. in the medical and pharmaceutical industry and in the nuclear industry as well. In Germany the decision to phase out nuclear energy leads to a strong demand for packages to transport low and middle active radioactive waste due to the dismantling and decommissioning of nuclear power plants. According to IAEA regulations the “non-competent authority approved package types” are the excepted packages and the industrial packages of Type IP-1, IP-2 and IP-3 and of Type A. For the packages of Type IP-2, IP-3 and Type A an assessment by the German competent authority is required for the quality management for the design, manufacture, testing, documentation, use, maintenance and inspection. In general a compliance audit of the manufacturer of the packaging is required during this assessment procedure. T2 - Waste Management Conference 2018 CY - Phoenix, USA DA - 18.3.2018 KW - Radioactive material KW - Quality management system KW - Transport packages PY - 2018 SP - Article 18194, 1 EP - 7 AN - OPUS4-44170 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Knieschewski, Arno A1 - Schlegel, Moritz-Caspar A1 - Akkerman, Floris A1 - Simo, Anne T1 - Evaluation of performance tests of range hoods used for the European energy efficiency label N2 - Several models of range hoods were tested by independent and accredited testing institutes. The results have been compared to the information declared by the manufacturer on the energy efficiency label and the product fiche. The measured electric power input of the lighting System and the measured grease absorption factor often differed significantly from the declared values. The reasons for these observations and the necessary steps to ensure accurate measurements and a meaningful EU energy efficiency label are elucidated. It is suggested that the ranges of the lighting efficiency classes are readjusted to fit the nowadays prevalent LED technology. Furthermore the tolerance in the regulation for the nominal electric power input of the lighting could be extended by a minimum absolute tolerance. The grease absorption test method may need a rework to achieve a satisfying accuracy. T2 - EEDAL 2017 CY - Irvine, California, USA DA - 13.09.2017 KW - Energy label KW - Range hood KW - Cooking fume extractor PY - 2018 SN - 978-92-79-77173-6 DO - https://doi.org/10.2760/68449 SN - 1018-5593 IS - Part III SP - 1065 EP - 1072 AN - OPUS4-43831 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scheidemann, Robert A1 - Qiao, Linan A1 - Müller, Karsten T1 - Comparison of experimental results and numerical simulations of penetration tests with damping concrete N2 - The shock absorbing material damping concrete is for the foundation in dry interim storage facilities for radioactive waste in Germany. In case of a potential cask drop damping concrete minimizes the mechanical loads to the cask. In course of safety analyzes this accident scenario is considered by numerical simulations using the finite element method. To get reliable results of numerical simulations a suitable material model is needed to take the characteristics of damping concrete into account. Due to the lack of sufficient material knowledge a research project was started to characterize the material’s behavior under different load conditions. This paper presents the test program to analyze the material behavior of damping concrete which is characterized by large volume change and strain rate hardening dependence. The determined Parameters were used to adapt an existing material model of the FE-code ABAQUS®. This model has to handle the mechanical damage behavior of damping concrete which occurs under compression and shear loads during a potential cask drop. To verify the material model numerical simulations are compared with dynamic penetration tests, which were conducted with specimens assembled similar to the real application of the damping concrete footings. The transferability of the material model to a real accident scenario was verified by a drop test with a full-scale cask on a damping concrete footing. T2 - ASME 2017 Pressure Vessels & Piping Conference (PVP2017) CY - Waikoloa, Hawaii, USA DA - 16.07.2017 KW - Drop test KW - Damping concrete KW - Cask KW - Material model PY - 2017 SN - 978-0-7918-5802-8 VL - 7 SP - Article UNSP V007T07A034, 1 EP - 6 PB - The American Society of Mechanical Engineers CY - New York AN - OPUS4-44042 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Quercetti, Thomas A1 - Müller, Karsten A1 - Johnson, Mark A1 - Tait, Trevor A1 - Tso, Chi-Fung A1 - Izatt, Conrad ED - ASME, T1 - Drop testing of a container for the storage. transport and disposal of intermediate level waste N2 - Impact tests were performed, as part of a corresponding container’s substantiation, during design development of a shielded container. The container will be used for storage, transport, and disposal of intermediate level waste in the UK. The mechanical test program comprised a 9m free drop test onto an unyielding target in a container long lid edge down orientation at ambient conditions. Further, a 0,5m free drop test onto a punch target was performed. Here, the container was orientated with the lid downwards in a way that the punch, a mild steel bar, impacts a filter lid. The test specimen was instrumented with strain gauges and accelerometers for the drop tests. Transient strains at selected points of the inner and outer container walls, at the shielding lid, as well as at the lid bolts were measured during the container’s impact. Furthermore, decelerations of the container body, container lid, and the skip were measured. The complex geometrical changes of the container due to impact were determined by optical 3d- deformation measures using the projected fringes method in combination with multi-image photogrammetry. This paper summarizes the performance of the drop tests and various drop test results in context with the design development as well as aspects regarding the associated Finite Element (FE) analyses and post-test evaluation. KW - Drop testing KW - Container KW - Intermediate level waste PY - 2017 SN - 978-0-7918-5802-8 VL - 7 SP - Article UNSP V007T07A036, 1 EP - 7 CY - New York AN - OPUS4-44047 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Plarre, Rüdiger T1 - Eine kleine kleine Natur- und Kulturgeschichte der Kleidermotte (Tineola bisselliella) N2 - A short natural and cultural history of the webbing clothes moth (Tineola bisselliella). It is generally accepted that the natural habitats of most pest insects can be found outside the synanthropic environment in layers of leaf litter, under bark, as well as in rodent or bird nests. Indeed, most of the common fabric pests have been reported as being facultative nidicolous. Therefore, infestation of commodities by pest insects out of these reservoirs is one possibility to be considered. However, the likelihood of a pest´s occurrence and survival outside of the synanthropic habitat largely depends on its ecological potential and competitiveness against other species of the same ecological guild. Some pest species are rarely found in wild habitats, especially in those regions where they are not native and where they have been introduced by man. The fabric pest Tineola bisselliella serves as a good example. Most likely originating from Central or Southern Africa, this insect was introduced into Europe probably not earlier than the late 18th century. Being more tolerant to dry environments than other fabric pests, its economical importance increased during the 20th century when the indoor climate changed because of central heating systems. Its occurrence in outdoor natural habitats must be regarded as accidental. Reported finds of webbing clothes moth larvae in bird nests e. g. have been largely overstated in the literature. Tineola bisselliella should be regarded as an invasive and eusynanthropic species in most parts of the world. KW - Textilschädling KW - Museumsschädling KW - Anpassung KW - Evolution PY - 2018 SN - 0037-5942 VL - Neue Folge 53 SP - 43 EP - 57 PB - Gesellschaft Naturforschender Freunde zu Berlin CY - Berlin AN - OPUS4-44048 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Plarre, Rüdiger A1 - Busweiler, Sabine T1 - Erneute Antennen-Anomalie beim Hausbockkäfer Hylotrupes bajulus (Coleoptera: Cerambycidae) in der F3-Generation N2 - Second occurrence of aberrant antenna in house longhorn beetle Hylotrupes bajulus (Coleoptera: Cerambycidae) in the F3 generation. In 2016, the house longhorn beetle (Hylotrupes bajulus) breeding culture of the Federal Institute for Materials Research and Testing (BAM) in Berlin produced a second female beetle with a unique malformed right antenna similar to the one previously reported. As in the first case the flagellum following the pedical was bifurcated. This time, however, both branches were of similar length with 7 and 8 flagellomeres, respectively. The left antenna was normally developed with 11 antennal segments (scape, pedicel and 9 flagellomeres). This second female stands as F3-generation in direct maternal line to the previous one. A heritable cause for the malformation is likely. KW - Hausbockkäfer KW - Entwicklung KW - Vererbung PY - 2018 SN - 0037-5942 VL - Neue Folge 53 SP - 101 EP - 105 PB - Gesellschaft Naturforschender Freunde zu Berlin CY - Berlin AN - OPUS4-44052 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Plarre, Rüdiger T1 - Termiten in Deutschland - wo gibt es denn so was? N2 - Rare occurrences of termites in Germany. Termites are typical elements of the tropical and subtropical insect fauna. In Europe, their most northern natural range is southern France, Italy and the South-Balkan region. Only occasionally are termites found in Germany. Their occurrence is always very closely associated with the synanthropic environment. Drywood termites like Cryptotermes brevis or Kalotermis flavicollis were accidentally imported with furniture, wooden artefacts or plant material into homes or indoor arboretums. Similar pathways of termite introduction are described for Coptotermes gestroi and Reticulitermes sp. into tropical botanical gardens and tropical theme parks. Although termites were introduced to Germany several times, successful spreading or long term establishment never occurred due to climatic barriers, namely cold winter temperatures. Only Reticulitermes flavipes formed sustainable colonies in the city of Hamburg for several decades. Originating from the eastern United States of America, this species was introduced in the 1930s with infested wood through the sea port. Small subterranean colonies could survive the winter in areas where pipes of the central heating system kept the ground from freezing. Control efforts of this potentially invasive species of economic importance started early on but failed until modern bait techniques were applied in the year 2000. Currently, termites have not been detected in Hamburg for the last five years. KW - Holzschutz KW - Termiten KW - Neozoon PY - 2018 SN - 0037-5942 VL - Neue Folge 53 SP - 83 EP - 90 PB - Gesellschaft Naturforschender Freunde zu Berlin CY - Berlin AN - OPUS4-44055 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grätz, Rainer T1 - Grundlagen für die Konformitätsbewertung nichtelektrischer Produkte N2 - Beschaffenheitsanforderungen an Produkte, die Explosionsschutzanforderungen zu erfüllen haben, werden in Deutschland durch die 9. Verordnung zum Produktsicherheitsgesetz (9. ProdSV, Maschinenverordnung) und speziell für atmosphärische Bedingungen in der 11. Verordnung zum Produktsicherheitsgesetz (11. ProdSV, Explosionsschutzverordnung bis 19.4.2016 bzw. Explosionsschutzprodukteverordnung ab 20.04.2016) geregelt. Wesentlicher Inhalt dieser Verordnungen und der Europäischen Richtlinie 2014/34/EU sind die Begriffsdefinitionen für Geräte, Schutzsysteme und Komponenten, das System der Konformitätsbewertung und die Konformitätserklärung, sowie die grundlegenden Sicherheits- und Gesundheitsanforderungen. Es gilt dabei das Prinzip der Herstellerverantwortung. Der Hersteller eines Produktes dokumentiert die Erfüllung der Richtlinienanforderungen mit seiner Konformitätserklärung und der Kennzeichnung des Produktes mit dem CE-Zeichen. T2 - 43. Heilbronner Ex-Schutz-Seminare Planen, Errichten und Betreiben elektrischer Anlagen in explosionsgefährdeten Betriebsstätten CY - Heilbronn, Germany DA - 20.02.2018 KW - Explosionsschutz KW - Konformitätsbewertung KW - ATEX KW - Richtlinie 2014/34/EU KW - Zündgefahrenbewertung PY - 2018 SP - Paper M05, 1 EP - 58 AN - OPUS4-44287 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Paul, Niels A1 - Hüllmann, Dino A1 - Kohlhoff, Harald A1 - Neumann, Patrick P. ED - Cosmi, F. T1 - A concept for an aerial-based landfill monitoring system N2 - Aerial based robots constitute a safe and suitable approach to remote gas-sensing. This paper describes a new concept , incorporating existing UAVs and newly developed gas sensors. The presented autonomous system is able to perform gas source localization and gas distribution mapping. T2 - 34th Danubia-Adria Symposium on Advances in Experimental Mechanics CY - Trieste, Italy DA - 19.09.2017 KW - Gassensor KW - Multicopter KW - UAV KW - Olfaction PY - 2017 SN - 978-88-8303-863-1 SP - 179 EP - 181 PB - University of Trieste, Italy CY - Trieste, Italy AN - OPUS4-42122 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kraus, David A1 - Trappe, Volker T1 - Impact of thermal loads on the damage onset of fiber reinforced plastics N2 - In this study, quasi-static material tests on unidirectional and multi-angle glass fiber reinforced epoxy laminates at ambient temperatures from -213 K to 353 K (-60 °C to +80 °C) are performed. In addition, neat resin is investigated under tension and compression loads at different temperatures. The coefficient of thermal expansion is determined for neat resin and unidirectional reinforced specimens. The dependence of the resin’s thermomechanical properties on the ambient temperature is shown. The point of damage onset at which first cracks appear within the matrix under quasi-static loading is investigated by means of optical grey scale analysis. The correlation between damage onset and effective matrix stress at different ambient temperatures is identified. An approach for the calculation of thermomechanical loads and the prediction of the damage onset by means of inverse calculations is presented. The impact of the strain blocking effect of the matrix is considered as well as residual thermal stresses due to curing and resin shrinkage. T2 - ICCM21 - 21th International conference on composite materials CY - Xi'an, China DA - 20.08.2017 KW - Fatigue KW - Composite KW - Thermomechanics KW - Fiber reinforced plastics KW - Damage onset PY - 2017 SP - 1 EP - 12 AN - OPUS4-42075 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gollwitzer, Christian A1 - Cabeza, Sandra A1 - Garces, G. ED - Petzow, G. T1 - Synchrotron-Absorptionskantentomographie zur dreidimensionalen Gefügeuntersuchung von Mg-Y-Zn Legierungen N2 - Absorptionskantentomographie, auch bekannt als differentielle Tomographie an Kanten, ist ein Verfahren, bei dem ausgenutzt wird, dass sich die Schwächung von Röntgenstrahlen beim Übergang der Photonenenergie über die Absorptionskanten sprunghaft ändert. Die Verwendung von Synchrotronstrahlung ermöglicht die Anwendung der Absorptionskantentomographie für nahezu jedes Element, da sie eine intensive, durchstimmbare Strahlenquelle mit kleiner Bandbreite darstellt. Der Mikrotomographieaufbau der BAM am Elektronenspeicherring BESSY II eignet sich mit einem Energiebereich von 5 keV bis über 60 keV und einer Ortsauflösung besser als 0.5 µm zur differentiellen Tomographie an den K-Kanten der Elemente von Chrom bis zu den Lanthaniden, bei Einbeziehung der L-Kante bis zu Uran. In dieser Arbeit wird die Absorptionskantentomographie ausgenutzt, um das Gefüge von Legierungen dreidimensional und nichtdestruktiv zu vermessen. Als Beispiel wird eine Legierung zwischen Magnesium, Yttrium und Zink analysiert, die sich gegenüber unlegiertem Magnesium durch größere Festigkeit und geringere Korrosionsanfälligkeit auszeichnet. Der Grund dafür liegt in der Bildung einer kristallographisch hochgeordneten Phase (long period stacking ordered - LPSO) der Legierungsbestandteile, die die Matrix in Form von Fasern durchzieht. Anhand ihres Yttriumgehaltes wird die dreidimensionale Verteilung der LPSO-Phase in der Matrix für verschiedene Proben bestimmt und mit Schnittbildern und Korrosionstests verglichen. Die Absorptionskantentomographie erweist sich als eine geeignete Methode, um die dreidimensionale Mikrostruktur von Legierungen zu charakterisieren. T2 - 51. Metallographie-Tagung Materialographie CY - Aalen, Germany DA - 13.09.2017 KW - Tomographie KW - Absorptionskante KW - Synchrotron KW - Legierung PY - 2017 SN - 978-3-88355-415-0 SP - 177 EP - 178 PB - Deutsche Gesellschaft für Materialkunde eV AN - OPUS4-42218 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grätz, Rainer T1 - Rechtliche Anforderungen des Explosionsschutzes: Einordnung des Explosionsschutzes im System der gesetzlichen Regelungen N2 - Ausgehend von den entsprechenden Artikeln des Vertrages über die Arbeitsweise der Europäischen Union lassen sich die Europäischen Richtlinien entsprechend der Zielrichtung der zugrundeliegenden Artikel folgendermaßen gliedern: - Richtlinien zur Harmonisierung des Handels (Beschaffenheitsrichtlinien) nach Artikel 114 (früher Artikel 95 EG-Vertrag) - Richtlinien über Mindeststandards zum Schutz der Arbeitnehmer (Arbeitsschutzrichtlinien) nach Artikel 153 (früher Artikel 137 EG-Vertrag) Diese Richtlinien sind von den Mitgliedsstaaten in ihre jeweiligen nationalen Rechtssysteme umzusetzen. Die Art und Weise der Umsetzung ist abhängig davon, zu welcher der beiden Gruppen die Richtlinie gehört. Richtlinien nach Artikel 114 sind in die entsprechenden Gesetze und Verordnungen so umzusetzen, dass die wesentlichen Forderungen unverändert übernommen werden. Im Gegensatz dazu können bei der Umsetzung von Richtlinien nach Artikel 153 über die Forderungen dieser Richtlinien hinaus eigene weitergehende Forderungen beibehalten oder neu eingeführt werden. T2 - DECHEMA-Weiterbildungskurs "Grundlagen und rechtliche Anforderungen des Explosiosschutzes" CY - Frankfurt am Main, Germany DA - 22.11.2017 KW - Explosionsschutz KW - ATEX KW - Konformitätsbewertung KW - Zündgefahrenbewertung PY - 2017 SP - Paper 3, 1 EP - 74 PB - DECHEMA-Forschungsinstitut CY - Frankfurt am Main, Germany AN - OPUS4-43224 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grätz, Rainer T1 - Normung im Bereich des Explosionsschutzes - nicht-elektrisch - N2 - Geräte zur Verwendung in explosionsgefährdeten Bereichen fallen unter die europäische Richtlinie 2014/34/EU /1/. Diese ist eine Richtlinie zur Harmonisierung des Handels (Beschaffenheitsrichtlinien) nach Artikel 114 des Vertrages über die Arbeitsweise der Europäischen Union /2/ (früher Artikel 95 EG-Vertrag) und regelt grundlegende Anforderungen an die Sicherheit der entsprechenden Geräte. Die Forderungen der Richtlinien nach Artikel 114 werden durch harmonisierte europäische Normen konkretisiert. Hinsichtlich der grundlegenden Struktur der Normen im nicht-elektrischen Bereich unterscheidet man dabei: A-Normen • Normen zu Grundprinzipien des Explosionsschutzes, wie Gefährdungsbeurteilung und Zündgefahrenbewertung B-Normen • Normen zur Bestimmung sicherheitstechnischer Kenngrößen • Normen für nicht-elektrische Geräte in explosionsgefährdeten Bereichen • Normen zu konstruktiven Explosionsschutzmaßnahmen C-Normen • Normen für spezielle Geräte oder Schutzsysteme, wie Flammendurchschlagsicherungen oder Ventilatoren Von besonderer Bedeutung für nicht-elektrische Geräte sind die Normenreihe DIN EN 13463ff/3/ und die DIN EN ISO 80079-36 /4/ und DIN EN ISO 80079-37 /5/. T2 - DECHEMA-Weiterbildungskurs "Grundlagen und rechtliche Anforderungen des Explosiosschutzes" CY - Frankfurt am Main, Germany DA - 22.11.2017 KW - Normen KW - Explosionsschutz KW - ATEX KW - Konformitätsbewertung KW - Zündgefahrenbewertung PY - 2017 SP - Paper 6, 1 PB - DECHEMA-Forschungsinstitut CY - Frankfurt am Main AN - OPUS4-43226 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Häßler, Dustin A1 - Hothan, Sascha T1 - Reaktive Brandschutzsysteme für Stahlbauteile N2 - Die Feuerwiderstandsdauer von ungeschützten Stahlbauteilen lässt sich durch den Einsatz reaktiver Brandschutzsysteme (RBS) signifikant erhöhen. Durch den profilfolgenden Auftrag der Brandschutzbeschichtung und die hierfür erforderlichen geringen Trockenschichtdicken, welche in der Regel nur wenige Millimeter betragen, können neben den brandschutz¬technischen Anforderungen auch die an die Stahl-konstruktion gestellten gestalterischen Ansprüche erfüllt werden. Kommt es zu einem Brandereignis schäumt das reaktive Brandschutzsystem auf und bildet eine thermische Schutzschicht um das Stahlbauteil aus. Dadurch wird die Erwärmung des Stahls verlangsamt und der Festigkeitsverlust infolge Temperatur wird verzögert. Die Anwendung von reaktiven Brandschutzsystemen auf Stahlbauteilen wird im Allgemeinen durch Zulassungen geregelt. In Bezug auf die durch die Zulassung abgedeckte Verwendung von reaktiven Brandschutzsystemen auf zug¬beanspruchten Stahlbauteilen haben sich in den letzten Jahren verschiedene Änderungen ergeben. Der nachfolgende Beitrag gibt hierzu einen aktuellen Überblick und beschreibt die Hintergründe, welche zu den neuen Regelungen geführt haben. Ferner erfolgt in diesem Zusammenhang ein Ausblick auf noch zu untersuchende Fragestellungen, welche bisher noch nicht durch die Regelungen in den Zulassungen abgedeckt werden. Darüber hinaus wird in dem Beitrag die derzeit aktuelle Problematik bezüglich der Alterungsbeständigkeit von reaktiven Brandschutz¬systemen thematisiert. T2 - 18. EIPOS-Sachverständigentage Brandschutz CY - Dresden, Germany DA - 20.11.2017 KW - Brandschutz KW - Stahlbau KW - Reaktive Brandschutzsysteme KW - Zugglieder KW - Dauerhaftigkeit KW - Alterung PY - 2017 SN - 978-3-9814551-6-8 SP - 26 EP - 43 PB - EIPOS GmbH CY - Dresden AN - OPUS4-43161 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maiwald, Michael A1 - Gräßer, Patrick A1 - Wander, Lukas A1 - Guhl, Svetlana A1 - Meyer, Klas A1 - Kern, Simon T1 - Innen hui und außen pfui – Smarte Prozess-Sensoren in der gegenwärtigen Automatisierungslandschaft der Prozessindustrie N2 - Der Wandel von der aktuellen Automation zum smarten Sensor ist im vollen Gange. Automatisierungstechnik, sowie die Informations- und Kommunikationstechnik (IKT) verschmelzen zunehmend. Eine Topologie für smarte Sensoren, die das Zusammenwirken mit daten- und modellbasierten Steuerungen bis hin zur Softsensorik beschreibt gibt es bis heute jedoch noch nicht. Um zu einer störungsfreien Kommunikation aller Komponenten auf Basis eines einheitlichen Protokolls zu kommen sollte die Prozessindustrie die Weichen für eine smarte und sichere Kommunikationsarchitektur stellen. Sie verwehrt stattdessen die Entwicklungen ihrer Zulieferer und wartet lieber ab. Der Beitrag greift die Anforderungen der Technologie-Roadmap „Prozess-Sensoren 4.0“ auf und zeigt Möglichkeiten zu ihrer Realisierung am Beispiel eines Online-NMR-Analysators, der im Rahmen eines EU-Projekts entwickelt wurde. T2 - 13. Dresdner Sensor Symposium CY - Dresden, Germany DA - 04.12.2017 KW - Smarte Feldgeräte KW - Process Control KW - Modulare Produktion KW - Online-NMR-Spektroskopie KW - Indirect Hard Modeling KW - Industrie 4.0 PY - 2017 UR - https://www.ama-science.org/proceedings/details/2717 SN - 978-3-9816876-5-1 DO - https://doi.org/10.5162/13dss2017/2.1 SP - 61 EP - 66 PB - AMA Service GmbH CY - Berlin AN - OPUS4-43252 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kern, Simon A1 - Guhl, Svetlana A1 - Meyer, Klas A1 - Wander, Lukas A1 - Paul, Andrea A1 - Maiwald, Michael T1 - Mathematical and statistical tools for online NMR spectroscopy in chemical processes N2 - Monitoring chemical reactions is the key to chemical process control. Today, mainly optical online methods are applied, which require excessive calibration effort. NMR spectroscopy has a high potential for direct loop process control while exhibiting short set-up times. Compact NMR instruments make NMR spectroscopy accessible in industrial and harsh environments for advanced process Monitoring and control, as demonstrated within the European Union’s Horizon 2020 project CONSENS. We present a range of approaches for the automated spectra analysis moving from conventional multivariate statistical approach, (i.e., Partial Least Squares Regression) to physically motivated spectral models (i.e., Indirect Hard Modelling and Quantum Mechanical calculations). By using the benefits of traditional qNMR experiments data analysis models can meet the demands of the PAT community (Process Analytical Technology) regarding low calibration effort/calibration free methods, fast adaptions for new reactants or derivatives and robust automation schemes. T2 - 13. Dresdner Sensor Symposium CY - Dresden, Germany DA - 04.12.2017 KW - Online NMR spectroscopy KW - Process control KW - Partial least squares regression KW - Indirect hard modeling KW - Quantum mechanics KW - First principles PY - 2017 UR - https://www.ama-science.org/proceedings/details/2748 SN - 978-3-9816876-5-1 DO - https://doi.org/10.5162/13dss2017/P2.07 SP - P2, 209 EP - 212 PB - AMA Service GmbH CY - Berlin AN - OPUS4-43254 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simon, Franz-Georg A1 - Holm, Olaf T1 - Resources from recycling and urban mining, limits and prospects N2 - In Germany, the direct material input (DMI) was 1727 million tons in the year 2014. This figure would be even higher by more than 14 % if no secondary materials were already used in industrial production. For example, production of secondary Cu is advantageous due to lower energy consumption and conservation of scarce natural resources. The presentation will discuss pathways to increase the use of secondary raw materials to foster a circular economy with a focus on waste treatment processes. T2 - The 13th International Conference on Ecomaterials CY - Bangkok, Thailand DA - 10.11.2017 KW - Waste treatment KW - Secondary raw materials KW - Direct material input PY - 2017 SP - 9 EP - 9 PB - King Mongkut's University of Technnology Thonburi CY - Bangkok, Thailand AN - OPUS4-43186 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Graf, B. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - 3D laser metal deposition in an additive manufacturing process chain N2 - Laser metal deposition is described with its applications for additive manufacturing. The necessary process chain is discussed, with regard to weld bead dimensions and 3D build-up strategy. Metallurgical cross sections, x-ray and tensile tests are conducted. As demonstrative components, a gas turbine burner and a turbine blade are shown. T2 - 1st International Congress on Welding, Additive Manufacturing and Associated Non- CY - Metz, France DA - 17.05.2017 KW - Laser metal deposition KW - Additive manufacturing KW - Ti-6Al-4V KW - Turbine industry KW - Process chain PY - 2017 UR - https://icwam.com/sites/default/files/Abstract%20book.pdf SP - AM 34-2 EP - 3 AN - OPUS4-43190 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Bartholmai, Matthias A1 - Neumann, Patrick P. T1 - Multifunktionaler Sensor zur Überwachung von Untergrundspeichern durch flächendeckendes ortsaufgelöstes Monitoring von Gasen, Temperatur und Gefügebewegungen im Boden N2 - Untergrundspeicher für Roh- und Abfallstoffe gewinnen zunehmend an Bedeutung. Verwendet werden sie vor allem für Stoffe wie Erdgas, Wasserstoff, Erdöl und neuerdings auch für Kohlen-stoffdioxid (CO2). Diese Stoffe werden meist unter Druck in Kavernen- oder Porenspeichern einge-lagert. Die Speicher dienen einerseits zum Ausgleich von Ungleichgewichten zwischen Ange-bot/Förderung und Nachfrage/Verbrauch und zur Erhöhung der Versorgungssicherheit. Anderer-seits bestehen Konzepte Abfallstoffe oder Gefahrstoffe für die Umwelt (aktuell CO2-Speicherung) dort für lange Zeiträume einzulagern. Mit den Einlagerungsstoffen verbunden ist ein signifikantes Gefahrenpotential für Mensch und Umwelt, falls es trotz aller Sicherheitsmaßnahmen zu einem unkontrollierten Austritt dieser Stoffe kommen sollte. Daher kommt dem Monitoring derartiger Untergrundspeicher und den darüber befindlichen Bodenstrukturen eine extrem hohe Bedeutung zu. Ein hochaktuelles Beispiel, das die Überwachung entsprechender Bodenflächen fordert, ist die unterirdische CO2-Speicherung im Rahmen der CO2-Abscheidung und -Speicherung (Carbon Dioxide Capture and Storage, CCS). CCS gilt als wichtige Brückentechnologie der Energiewirtschaft und wird weltweit vorangetrieben, während die Sicherheit von Bevölkerung und Biosphäre noch kont-rovers diskutiert wird. Auch die EU setzt auf CCS und gibt in der EU-Richtlinie 2009/31 als Ziel-setzung bis 2015 vor, 15 Pilotanlagen zu bauen und in Betrieb zu nehmen. Als Bedingung für die Genehmigung der CO2-Speicherung ist explizit die Überwachung der Speicheranlagen durch Monito-ring vorgeschrieben, wobei die technisch besten Lösungen zum Einsatz kommen sollen. Das zu entwickelnde Messsystem adressiert neben den o.g. Anwendungsfeldern weitere, bei denen insbesondere die Emission von Gasen ein Risiko für Mensch und Umwelt darstellt oder wirt-schaftlichen Schaden verursachen kann. Hierzu zählen die Überwachung von Abfalldeponien, Ge-fahrgutlagerstätten, kontaminierten Altlastengebieten, Moor-, Torf-, Kohleflözen (präventive Branderkennung) und geodynamisch aktiven Regionen. Auch moderne Fördertechnologien, wie das Hot-Dry-Rock-Verfahren (HDR) zur Energiegewinnung durch Einpressen von überkritischem CO2 in den Erdkörper, das die Beweglichkeit eines Gases mit der Dichte einer Flüssigkeit kombiniert und Wärmeaustausch im Erdinneren bewirkt, bergen das Risiko unkontrollierter Gasemissionen und bedürfen der umfassenden Überwachung. KW - Verteilte Sensorik KW - Gassensor KW - CCS KW - Gasspeicher PY - 2015 DO - https://doi.org/10.2314/GBV:867138327 SP - 1 EP - 13 AN - OPUS4-43195 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Feldkamp, Martin A1 - Erenberg, Marina A1 - Nehrig, Marko A1 - Bletzer, Claus A1 - Musolff, André A1 - Schönfelder, Thorsten A1 - Wille, Frank T1 - Behavior of wood filled impact limiters during the IAEA thermal test N2 - Packages for the transport of radioactive material are often equipped with impact limiters consisting of wood, encapsulated by steel sheets. These impact limiters shall ensure that transport casks meet the IAEA safety requirements. After damage caused by the mechanical tests the package has to withstand a severe fire scenario. It is required that the mechanical tests have to produce maximum damage, taking into account the thermal test. Furthermore, any damage, which would give rise to increased radiation or loss of containment or affect the confinement system after the thermal test, should be considered. Concerning the thermal test, the IAEA safety requirements state that during and following the fire test, the specimen shall not be artificially cooled and any combustion of materials of the package shall be permitted to proceed naturally. Different works from the French Institute for Radiological Protection and Nuclear Safety (IRSN) and BAM show that additional energy supply from a pre-damaged impact limiter to the cask could occur caused by smoldering of the wood. This effect should be considered within the safety assessment of the package. A heat wave from the fire could overlap with the additional energy from the impact limiter in the sealing system. In 2015 BAM conducted small scale fire tests with wood filled metal drums showing continuing combustion processes during the cooling down phase. As not much is known about smoldering processes in wood filled impact limiters, it is highly complex to define pre-damage of impact limiters, which are conservative, regarding the most damaging energy flow from the impact limiter to the containment system in dependence of time. More research has to be done to develop models to examine the effects of smoldering impact limiters on the containment of packages for the assessment. The process of smoldering is described with regard to the requirements in the thermal safety assessment. Parameters influencing the smoldering process are identified. BAM operates test facilities to examine the issue of mechanical damage, combustion and heat transfer of packages for transport of radioactive material. A thermal test will take place with a wood filled test specimen with a diameter of about 2.3 meters. The aim is to understand the phenomena of smoldering under the consideration of relevant regulatory boundary conditions. T2 - ASME 2017 Pressure Vessels and Piping Conference (PVP2017) CY - Waikoloa, Hawaii, USA DA - 16.07.2017 KW - Fire test KW - Wood KW - IAEA KW - Smoldering KW - Smouldering KW - Shock absorber KW - Thermal test KW - Combustion KW - Impact limiter PY - 2017 SN - 978-0-7918-5802-8 VL - 7 SP - Article UNSP V007T07A038, 1 EP - 9 AN - OPUS4-43172 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pistol, Klaus ED - Zehfuß, Jochen T1 - Betontechnologie und Brandschutz: Hochtemperatureigenschaften innovativer Betone als Grundlage für die Heißbemessung N2 - Die Bemessungsnorm für Stahlbeton- und Spannbetontragwerke DIN EN 1992 (EC 2) erlaubt die Anwendung von vereinfachten und allgemeinen Rechenverfahren für den Tragfähigkeitsnachweis im Brandfall (Heißbemessung). Als Grundlage für die Heißbemessung werden für Normalbeton und für Hochfesten Beton temperaturabhängige Spannungs-Dehnungs-Beziehungen angegeben, mit denen der Festigkeits- und Steifigkeitsverlust von Beton bei zunehmender Temperatur berücksichtigt wird. Im vorliegenden Aufsatz wird herausgearbeitet, dass die aktuelle betontechnologische Entwicklung und die damit einhergehende Diversifizierung in der stofflichen Zusammensetzung innovativer Betone bei der Heißbemessung berücksichtigt werden muss. Zum einen muss bei Verwendung von innovativen Betonen untersucht werden, ob bei Feuereinwirkung zerstörende Abplatzungen auftreten, die sich auf die Tragfähigkeit der untersuchten Tragstruktur auswirken. Zum anderen müssen die temperaturabhängigen Festigkeits- und Verformungseigenschaften innovativer Betone experimentell untersucht werden, da das Hochtemperaturverhalten von Beton vor allem von der stofflichen Zusammensetzung und weniger von der Kaltdruckfestigkeit abhängt. T2 - 4th Symposium Structural Fire Engineering – TU Braunschweig 2017 CY - TU Braunschweig, Germany DA - 12.09.2017 KW - Heißbemessung KW - Betontechnologie KW - Brandschutz PY - 2017 SP - 1 EP - 19 AN - OPUS4-42177 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scharff, Erik T1 - Verflüssigtes Erdgas (LNG) als Antriebsquelle im Schwerlastverkehr: Eine Sicherheitsbetrachtung am Referenzfall „Verkehrstunnel“ N2 - Die BAM plant Untersuchungen zur unfallbedingten Freisetzung brennbarer Gase in Umschließungen. Anlass ist die prognostizierte Zunahme verflüssigter Gase als Antriebsquelle im Lkw-Schwerlastverkehr aufgrund der strenger werdenden Abgasnormen. Im Hinblick auf die Bewertung von Gefahren zukünftiger Kraftstoffe für die Sicherheit von Infrastrukturen soll als Versuchsszenario verflüssigtes Erdgas (LNG) in einer verkehrstunnelartigen Einhausung auf dem Testgelände Technische Sicherheit der BAM freigesetzt werden. In diesem Beitrag werden die sicherheitstechnischen Vorbetrachtungen geschildert, die den Anlass zur Festlegung auf dieses Szenario gaben sowie die Relevanz einer notwendigen vertieften Betrachtung illustrieren. Dabei wird auf die allgemeinen Entwicklungen im Güterverkehr, die sicherheitstechnischen Eigenschaften von LNG sowie den baulichen Anforderungen an und für die Gefährdungsbetrachtung relevanten Bedingungen in Verkehrstunneln eingegangen. Vereinfacht soll die prinzipielle Herangehensweise bei der Gefährdungsbeurteilung dargestellt werden sowie im Zuge dessen anhand einer überschlägigen Berechnung der Dimension der explosionsfähigen Wolke im Tunnel die Gefährdung für Verkehrsteilnehmer und die Bauwerksstruktur abgeschätzt werden. Hilfsmittel, die zum Einsatz kommen, sind physikalische Modellvorstellungen, empirische sowie CFD-Methoden. T2 - 5. Magdeburger Brand- und Explosionsschutztage CY - Magdeburg, Germany DA - 23.03.2017 KW - Erdgas - LNG KW - Tunnel KW - Freisetzung KW - Schwerlastverkehr PY - 2017 SN - 978-3-00-056201-3 DO - https://doi.org/10.978.300/0562013 SP - 1 EP - 13 AN - OPUS4-42179 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kovalev, A. A1 - Spaltmann, Dirk A1 - Woydt, Mathias A1 - Meng, Y. T1 - Characterization of low wear on top aperities N2 - The aim of this research is to characterize a surface that has experienced low wear on asperities. The procedure used is similar to an Abbott-Firestone approach and based on functional bearing of projected area, surface area and material volume. Surface features extracted from surface height maps provide more comprehensive information about topography changes due to wear. Thus, they were used to detect low wear volumes on the top of asperities. T2 - The 6th World Tribology Congress CY - Beijing, China DA - 17.09.2017 KW - Simulation KW - Wear KW - Asperities KW - Abbott KW - Firestone PY - 2017 SP - 1 EP - 4 AN - OPUS4-42465 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Spaltmann, Dirk ED - Burbank, J.-T. ED - Woydt, Mathias T1 - Kaltverfestigung und reaktive Grenzschichten in metallischen Wälzkontakten N2 - Aus Schmierstoffen gebildete Tribofilme bestimmen das Reibungs- und Verschleißverhalten von Tribosystemen neben der Fresslasttragefähgikeit. Die Kaltverfestigung stellt einen weiteren Mechanismus insbesondere zum Verschleißschutz dar. Unter Wälzreibung wird das funktionale Profil organischer und metallorganischer Tribofilme sowie von Kaltverfestigung verglichen, die auf verschiedenen Stahlmetallurgien innerhalb von 10.000 Überrollungen in einem 2Disk-Prüfstand erzeugt wurden. Dabei wurden Hertzsche Kontaktspannungen ober von P0max=2,14 GPa (FZG14) eingesetzt. T2 - 58. Tribologie-Fachtagung 2017 CY - Göttingen, Germany DA - 25.09.2017 KW - Kaltverfestigung KW - Wälzreibung KW - Tribofilme PY - 2017 SN - 978-3-9817451-1-5 SP - 229 EP - 242 AN - OPUS4-42470 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias ED - Wäsche, Rolf ED - Brandt, Guido ED - Ehrke, Roman ED - Yano, S. ED - Sasaki, S. T1 - Tribology in hot steam N2 - The wear rates of self-mated alumina couples show that friction as well as wear is largely determined by the above mentioned hydro-thermal conditions. The presence of water and its amount available in the surrounding system either in liquid or in gaseous form plays a key role for friction and wear behavior and can be beneficial for the tribological profile of steam degradation resistant materials. Hot steam enhances the tribo-chemical formations of oxides and hydroxides on MgO-ZrO2, alumina and antimony impregnated carbon. T2 - The 6th World Tribology Congress CY - Beijing, China DA - 17.09.2017 KW - Hot steam KW - Friction KW - Wear behaviour PY - 2017 SP - 1 EP - 3 AN - OPUS4-42472 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias ED - Huang, S. ED - Vleugels, J. ED - Mohrbacher, H. T1 - Cutting tools and wear protection through nickel bonded niobium carbide (NbC) as a subtitute for cobalt bonded tungsten carbide (WC) N2 - The research and developments on niobium carbide-based hard materials generated grades, which meet the application line for tungsten carbide and showed already a very high potential for many technical applications, especially for wear protection and machining. T2 - The 6th World Tribology Congress - WTC 2017 CY - Beijing, China DA - 17.09.2017 KW - Cutting tools KW - Niobium carbide KW - NbC PY - 2017 SP - 1 EP - 4 AN - OPUS4-42474 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hothan, Sascha A1 - Pistol, Klaus A1 - Häßler, Dustin A1 - Klemmstein, Frank ED - Zehfuß, Jochen T1 - Einfluss der Querdehnungsbehinderung auf das Trag- und Verformungsverhalten von Spannbeton-Hohlplatten N2 - Spannbeton-Hohlplatten (engl.: hollow core slabs, HC-Platten) werden insbesondere aus wirtschaftlichen Gründen als Deckensysteme im Hochbau eingesetzt. Bei einem 2007 aufgetretenen Brandereignis in einem Parkhaus in Rotterdam kam es zu einer teilweisen Ablösung des unteren Plattenspiegels. Dies hatte eine europaweite Diskussion zur brandschutztechnischen Bewertung dieser Bauart zur Folge. Mittlerweile liegen eine Vielzahl von gutachterlichen Stellungnahmen, Literaturauswertungen und auch jüngeren Forschungsarbeiten zum Brandverhalten von Konstruktionen aus Spannbeton-Hohlplatten vor. In den Untersuchungen wurde unter anderem das Tragverhalten von HC-Platten bei starrer Auflagerung, insbesondere hinsichtlich der Querkrafttragfähigkeit, untersucht. Ein weiterer bei der Prüfung und Bewertung von Spannbeton-Hohlplatten bisher kaum beachteter Aspekt ist die im Brandfall auftretende Behinderung der Querdehnung. Um zu untersuchen inwieweit die Tragfähigkeit der HC-Platten von der Querdehnungsbehinderung beeinflusst wird, wurden an der BAM entsprechende experimentelle und numerische Untersuchungen an Deckenfeldern aus Spannbeton-Hohlplatten mit variierender seitlicher Zwängung durchgeführt. In der Praxis kann für HC-Platten eine Querdehnungsbehinderung im Brandfall auftreten, wenn beispielsweise eine sehr steife Begrenzung des brandbeanspruchten Deckenbereiches vorliegt, z.B. durch Treppenhauskerne oder auch durch umgebende Deckenfelder bei lokaler Brandbeanspruchung. Im Beitrag werden die im Realmaßstab durchgeführten Brandversuche ausführlich beschrieben und deren Ergebnisse und daraus abgeleiteten Erkenntnisse vorgestellt. Anhand der an der BAM durchgeführten Untersuchungen konnte gezeigt werden, dass bei einer Zunahme der seitlichen Zwängung die Horizontalrissbildung in den Plattenstegen zu und die Längsrissbildung abnimmt. Die unterschiedlich starke, thermisch bedingte horizontale Verformung der Plattenober- und -unterseite bewirkte aufgrund der Dehnungsbehinderung am Übergang zur seitlichen Zwängungskonstruktion eine Schubbeanspruchung in Plattenquerrichtung. Die Schubspannung wurde durch Horizontalrissbildung in den Plattenstegen abgebaut. Trotz der ausgeprägten Horizontalrissbildung kam es in den Brandversuchen nicht zu einer Ablösung des unteren Plattenspiegels. Ebenso zeigte sich kein negativer Einfluss der Horizontalrisse auf das Trag- und Verformungsverhalten der brandbeanspruchten Deckenkonstruktion. Die in den Brandversuchen erfassten thermischen und mechanischen Messwerte sowie die Ergebnisse aus Materialuntersuchungen stehen zukünftig als umfangreiche Datenbasis für die Validierung numerischer Modelle zur Verfügung. T2 - 4th Symposium Structural Fire Engineering – TU Braunschweig 2017 CY - Braunschweig, Germany DA - 12.09.2017 KW - Spannbetonhohldecken KW - Feuerwiderstand KW - Brandschutz KW - Querdehnungsbehinderung PY - 2017 VL - 4 SP - Artikel 8, 1 EP - 15 PB - TU Braunschweig CY - Braunschweig AN - OPUS4-42419 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hüllmann, Dino A1 - Paul, Niels A1 - Neumann, Patrick P. ED - Cosmi, F. T1 - Motor Speed Transfer Function for Wind Vector Estimation on Multirotor Aircraft N2 - A set of equations is derived to estimate the 3D wind vector with a multirotor aircraft using the aircraft itself as a flying anemometer. Since the thrust component is required to compute the wind vector, the PWM signal controlling the motors of the aircraft is measured and a transfer function describing the relation between the PWM signal and the rotational speed of the motors is derived. T2 - 34th Danubia-Adria Symposium on Advances in Experimental Mechanics CY - Trieste, Italy DA - 19.09.2017 KW - Anemometer KW - Multicopter KW - UAV KW - Wind KW - PWM PY - 2017 UR - https://www.openstarts.units.it/handle/10077/14834 SN - 978-88-8303-863-1 SP - 75 EP - 77 PB - University of Trieste, Italy CY - Trieste, Italy AN - OPUS4-42426 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Spaltmann, Dirk A1 - Woydt, Mathias T1 - Alternative approach to simulate an entire particle erosion experiment N2 - The cause and type of solid particle erosion varies across different industries and locations in plants, for instance the particles could be volcanic ash in aero-engines, fly ash in boilers, exfoliated scale in steam turbines or mineral matter in oil excavation. In all cases the durability of materials can be improved through better surface engineering and coatings, but the development of these is restricted also due to lack of generic models. In this respect, the simulation of a single impact with finite element methods using 100.000 knots would take about 15 minutes. In order to simulate an entire particle erosion experiment, up to one billion of such impacts would have to be considered. In order to simulate an entire particle erosion experiment, the current work presents an alternative approach capable of calculating about half a billion impacts on a substrate in less than six hours on a standard PC. The predictions of the simulation will be compared to a steel sample at 600°C eroded by aluminum oxide particles with a velocity around 210 m/s. T2 - The 6th World Tribology Congress CY - Beijing, China DA - 17.09.2017 KW - Particle erosion KW - Simulation KW - Wear PY - 2017 SP - 1 EP - 3 AN - OPUS4-42449 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wolter, Christian T1 - A bottom-up approach to study metal sulphides in brake friction materials at higher temperatures N2 - The impact of metal sulphides in brake friction materials on the friction behaviour of disc brakes was studied at two different temperatures and in two different atmospheres using a pin-on-disc device with powder supply. Powder mixtures were prepared by using a bottom-up approach, where magnetite is the main component, in which different metal sulphides are mixed in. At 400 °C, the resulting coefficients of friction are higher in air than in nitrogen atmosphere, which can be attributed to the generation of metal oxides and were confirmed by doing thermal analysis. T2 - The 6th World Tribology Congress CY - Beijing, China DA - 17.09.2017 KW - Brake friction materials KW - Artificial third body KW - Metal sulphies PY - 2017 SP - 1 EP - 3 AN - OPUS4-42452 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lüth, Peter A1 - Brandes, E. A1 - Frost, K. A1 - Kurth, Lutz A1 - Schmidt, Martin A1 - Michael-Schulz, Heike A1 - Uhlig, S. T1 - CEQAT-DGHS Ringversuchsprogramm für die Chemikaliensicherheit – Methodenvalidierung N2 - Bei der Bewertung der Verlässlichkeit der im Labor gewonnenen Prüfergebnisse spielen Ringversuche eine entscheidende Rolle. Die Bundesanstalt für Materialforschung und –prüfung (BAM) unterstützt deshalb den weiteren Ausbau des Ringversuchsprogramms des im Jahr 2007 gegründeten Kompetenzzentrums zur Qualitätssicherung für Prüfungen von Gefahrgütern und Gefahrstoffen auf physikalische Gefahren (Centre for quality assurance for testing of dangerous goods and hazardous substances, CEQAT-DGHS). Bei allen bisher untersuchten Prüfmethoden besteht ein Verbesserungsbedarf. Die RV müssen daher zunächst auf die Methodenentwicklung, -verbesserung und -validierung und auf die Bestimmung der Messunsicherheit der jeweiligen Prüfmethode abzielen und nicht auf Leistungstests. T2 - 13. Fachtagung Anlagen-, Arbeits- und Umweltsicherheit CY - Köthen, Germany DA - 16.11.2017 KW - Gefahrgut KW - Gefahrstoff KW - Ringversuch KW - Prüfmethode KW - Validierung KW - Qualitätssicherung PY - 2017 SN - 978-3-96057-032-5 SP - 1 EP - 13 CY - Köthen AN - OPUS4-43299 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Plarre, Rüdiger T1 - Termiten - Biologie, Vorkommen und Bekämpfung N2 - Der globale Handel mit Holz, als Rohware, Verpackungsholz, Mobiliar oder Kulturgut haben dazu beigetragen, dass einige Termitenarten eine weltweite Verbreitung erfahren haben. Ob sich eine Art in einem neuen Habitat erfolgreich etabliert, hängt dabei von vielen Faktoren ab. Für Termiten ist die Temperatur ein entscheidender Faktor. In Deutschland ist die Gefahr, dass Termiten ein regelmäßiger Bestandteil der Fauna werden, in naher Zukunft und trotz Klimawandels nicht zu erwarten. Es sind nicht die Jahresmitteltemperaturen, sondern die für Termiten extremen Minusgrade mit Bodenfrost im Winter – und sei es nur über ein paar Tage –, die ihr nachhaltiges Vorkommen verhindern. Nur unter bestimmten synanthropen Bedingungen treten Termiten gelegentlich in Deutschland in Erscheinung, wie die wenigen Beispiele zeigen T2 - 28. Weiterbildungstag des Deutschen Holzschutzfachverbandes Berlin Brandenburg CY - Berlin, Germany DA - 02.12.2017 KW - Klimawandel KW - Holzschutz KW - Materialschutz PY - 2017 SP - 1 AN - OPUS4-43257 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schalau, Bernd A1 - Schalau, Sebastian T1 - AUSTAL, ein Lagrange´sches Partikelmodell für Störfallauswirkungsbetrachtungen N2 - Zur Bestimmung von Gefährdungsbereichen wird für Gasausbreitungsberechnungen zurzeit vorwiegend die VDI Richtlinie 3783 herangezogen. Bei der Berechnung der Ausbreitung dichteneutraler oder leichter Gase nach Blatt 1 der Richtlinie kann die Bebauung nicht berücksichtigt werden. Dies und die Frage der Anwendbarkeit im Nahbereich der Quelle waren Gründe die VDI-RL zu überarbeiten. Grundlage hierfür ist ein Lagrange´sches Partikelmodell nach VDI 3945 Blatt 3 in Verbindung mit dem Windfeldmodell in der VDI-RL 3783 Blatt 8. Vergleichsberechnungen zeigen, dass das Lagrange´sches Partikelmodell im Vergleich zu experimentellen Untersuchungen einer ebenen, ungestörten Grenzschichtströmung eine bessere Übereinstimmung in der Konzentrationsverteilung ergibt, als die VDI-RL 3783 Blatt 1. Die Qualität einer Berechnung mit dem Lagrange´schen Partikelmodell ist wesentlich von der Güte der Windfeldberechnung abhängig. Für drei Gebäudekonfigurationen sind die Windfelder mit dem etablierten diagnostischen Windfeldmodell TALdia und mit dem prognostischen CFD-Tool OpenFOAM berechnet und mit Messwerten verglichen worden. Mit OpenFOAM können nach den bisherigen Untersuchungen qualitativ gleichwertige, eher bessere Windfelder berechnet werden. T2 - 13. Fachtagung Anlagen-, Arbeits-und Umweltsicherheit 16./17.11.2017 CY - Köthen, Germany DA - 16.11.2017 KW - Gasausbreitung KW - Störfallauswirkungsbetrachtungen PY - 2017 SN - 978-3-96057-032-5 SP - N-01, 1 EP - 14 AN - OPUS4-43260 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Deußing, G. A1 - Dümichen, Erik A1 - Braun, Ulrike T1 - Polymeranalytik Intelligent kombiniert N2 - Durch die intelligente Anbindung an die Stir Bar Sorptive Extraction (SBSE) lassen sich Zersetzungsprodukte der thermogravimetrischen Analyse (TGA) von Polymeren auf effiziente Weise anreichern, auftrennen und mittels GC/MS identifizieren. KW - Thermische Degradation KW - Mikroplastik PY - 2016 UR - http://www.gerstel.cn/de/GA51_Polymeranalytik.htm IS - 51 SP - 9 EP - 11 PB - Gerstel AN - OPUS4-42146 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Deußing, G. A1 - Dümichen, Erik A1 - Braun, Ulrike T1 - Der Fänger im Spülgas N2 - Durch die intelligente Anbindung an eine in der GC/MS gängige Extraktionstechnik (SBSE) lassen sich Zersetzungsprodukte der thermogravimetrischen Analyse (TGA) von Polymeren auf effiziente Weise anreichern, anschließend trennen und sicher identifizieren. KW - Polymeranalytik KW - Thermische Extraktion PY - 2015 UR - http://www.laborpraxis.vogel.de/so-erweitern-sie-die-moeglichkeiten-der-tga-a-490995/index2.html UR - https://files.vogel.de/vogelonline/vogelonline/issues/6773.pdf SN - 0344-1733 VL - 39 IS - 6 SP - 24 EP - 27 PB - Vogel Business Media AN - OPUS4-42149 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dümichen, Erik A1 - Eisentraut, Paul A1 - Braun, Ulrike T1 - Polymere und Mikroplastik in der Umwelt N2 - Es wird ein neues und voll automatisiertes Verfahren vorgestellt für die Analyse von Mikroplastik in der Umwelt. KW - Mikroplastik KW - TED PY - 2017 SN - 0016-3538 VL - 61 IS - 9 SP - 24 EP - 27 PB - Wiley AN - OPUS4-42170 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Patrick P. A1 - Detlefsen, Malte A1 - Hüllmann, Dino A1 - Kohlhoff, Harald ED - Cosmi, Francesca T1 - A low-cost cable-suspended parallel manipulator for testing 3D olfaction algorithms N2 - Cable-suspended parallel manipulators have been a topic of research for multiple decades and called special attention in the fields of simulations. However, they are also well-suited for the simple evaluation of aerial-based mobile robot olfaction (MRO) algorithms, such as gas source localization and gas distribution mapping. Based on an open source framework for 3D printers, we designed a low-cost underconstrained, cable-suspended parallel manipulator. Computations are carried out purely on an Atmel ATmega2560 microcontroller. T2 - 34rd Danubia - Adria Symposium on Advances in Experimental Mechanics CY - Trieste, Italy DA - 19.09.2017 KW - Cable-suspended parallel manipulator KW - 3D KW - Mobile Robot Olfaction PY - 2017 SN - 978-88-8303-863-1 SP - 171 EP - 172 CY - Trieste AN - OPUS4-42316 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Horn, Wolfgang A1 - Wilke, Olaf A1 - Mull, B. A1 - Richter, Matthias A1 - Brödner, Doris A1 - Mölders, N. A1 - Renner, M. T1 - Reproducibly emitting reference material for quality assurance/quality control of emission test chamber measurements N2 - Volatile Organic Compounds (VOC) are ubiquitous in the indoor air, since they emit from materials used indoors. Investigations of these materials are mostly carried out in test chambers under controlled climatic conditions. Quality control of these test chamber measurements is important but there is a lack of commercially available homogenous reference materials as required for round robin tests or quality assurance of laboratories. The approach of the present study is the impregnation of a supporting material with VOC, which are reproducibly released in measurable chamber air concentrations under standardised test conditions. A polymer made of Thermoplastic Polyurethane (TPU) was chosen as carrier material. It was impregnated with the VOC trimethyl pentanediol isobutyrat (texanol). T2 - Healthy Buildings 2017 Europe CY - Lublin, Poland DA - 02.07.2017 KW - Emissions testing KW - Volatile organic compounds KW - Polymeric material KW - CO2 assisted impregnation PY - 2017 SN - 978-83-7947-232-1 SP - Paper 0172, 1 EP - 2 AN - OPUS4-42348 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Dittrich, Matthias T1 - Endlagerbehälter und deren Qualifizierung N2 - Vorlesung zum Thema Qualifizierung von Endlagerbehältern für das Endlager Konrad. Grundlagen der Bauartprüfung. T2 - Modul 6 – Konditionierung, Entsorgung und Endlagerung radioaktiver Abfälle KW - Endlager Konrad KW - Bauartprüfung KW - Endlagerbehälter PY - 2017 SP - Kap. 18, 1 EP - 60 PB - AiNT CY - Aachen AN - OPUS4-42350 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Petrat, T. A1 - Marko, A. A1 - Graf, B. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael ED - Mayr, P. ED - Berger, M. T1 - Baustrategien zur Beeinflussung von Materialauftrag und Temperaturentwicklung bei der additiven Fertigung mittels Laser-Pulver-Auftragschweißen N2 - Die Weiterentwicklung des Laser-Pulver-Auftragschweißens im Bereich der additiven Fertigung stellt dieses Verfahren vor neue Herausforderungen. Bauteile können schnell und endformnah hergestellt werden, was diese Technik für den Prototypenbau sowie Kleinserienfertigung interessant macht. Die Vielzahl an Varianten, um ein Volumen aus einzelnen Schichten aufzubauen, erhöhen die Möglichkeiten die Eigenschaften des entstehenden Bauteils zu beeinflussen. Hierfür müssen Strategien entwickelt werden, welche einen gleiclunäßigen Materialauftrag bei gleichzeitig optimalen Materialeigenschaften gewährleisten. Die durchgeführten Untersuchungen behandeln den Einfluss von Pendelstrategien sowie Spiralstrategien auf die Temperaturentwicklung und stellen diese vergleichend gegenüber. Um den unterschiedlichen Bedingungen bei der Bauteilfertigung Rechnung zu tragen, wurden Versuche in Randbereichen sowie im zentralen Bereich des Testobjekts untersucht. Die Ergebnisse verdeutlichen die Notwendigkeit angepasste Baustrategien zu entwickeln, um durch einen stabilen Fertigungsprozess Qualität und Eigenschaften eines Bauteils gewährleisten zu können. T2 - FüMoTec 2017 CY - Chemnitz, Germany DA - 14.11.2017 KW - Laser-Pulver-Auftragschweißen KW - Additiv KW - Pendelstrategie KW - Spiralstrategie KW - Temperaturentwicklung PY - 2017 SN - 978-3-96100-034-0 SN - 2365-8096 SN - 2365-810X VL - 2017/2 SP - 27 EP - 36 PB - readbox unipress CY - Münster AN - OPUS4-43104 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Blankenhagel, Paul T1 - Brandszenarien organischer Peroxide in Stahlbehältern N2 - Für organische Peroxide (OP) ergeben sich im Falle eines Brandes im Vergleich zu herkömmlichen entzündbaren/brennbaren Stoffen höhere Massenabbrandraten, größere Flammenhöhen und erhöhte Strahlungsbelastungen für Objekte und Personen in der Umgebung. Eine besondere Gefahr kann von OP in Stahlgefäßen ausgehen, sofern sie für die Lagerung oder Beförderung zugelassen sind. Brandversuche an 200-Liter-Stahlfässern zeigen z. B. eine explosionsartige Ausbildung von Feuerbällen hochkonzentrierter flüssiger OP nach einem zuvor schon heftigen Abbrandverhalten. In diesem Beitrag wird auf den Brand verschiedener OP in Stahlfässern eingegangen und die Schadenswirkung auf die Umgebung bewertet. Die zu beobachtenden Phänomene Pool- und Jetfeuer, Boil-Over sowie Feuerball werden mittels der Versuchsergebnisse beschrieben. Messtechnisch erfasst und gegenübergestellt werden die Massenabbrandraten, diverse Flammeneigenschaften sowie die thermische Strahlungsbelastung auf die Umgebung. Durch eine Vielzahl von Versuchen zeigen sich Feuerbälle unterschiedlicher Größe, die durch bekannte semi-empirische Korrelationen für flüssige Kohlenwasserstoffe nicht beschrieben werden können. T2 - 13. Fachtagung für Anlagen-, Arbeits- und Umweltsicherheit CY - Köthen, Germany DA - 16.11.2017 KW - Organische Peroxide KW - Feuerball KW - Thermische Strahlung KW - Sicherheitsabstände PY - 2017 SN - 978-3-96057-032-5 SP - 1 EP - 9 CY - Köthen AN - OPUS4-43047 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulte, Petra T1 - Kritische Bewertung der Prüfergebnisse in chemikalienrechtlichen Verfahren: Wie agiert die Behörde? Welche Folgen haben die Ergebnisse für die Rechtsetzung? N2 - Mit nicht-konformen oder schlecht dokumentierten Prüfergebnissen können weder Behörden noch Unternehmen etwas anfangen. Belastbare und eindeutige Informationen aus den Registrierungsdossiers sind entscheidend, damit industrielle und gewerbliche Verwender der Stoffe das Gefahrenpotenzial einschätzen und ggf. Maßnahmen zum Schutz von Menschen und Umwelt treffen können. Darüber hinaus benötigen die Behörden verlässliche Daten aus den Registrierungen, um ihrer Verantwortung bei der Identifizierung regulierungsbedürftiger Stoffe nachkommen zu können. T2 - 13. Fachtagung "Anlagen-, Arbeits- und Umweltsicherheit" CY - Köthen, Germany DA - 16.11.2017 KW - Prüfmethoden KW - Einstufung KW - REACH KW - CLP KW - Registrierungsdossiers KW - SIEF KW - Qulitätssicherung KW - IUCLID KW - ECHA KW - OECD PY - 2017 SN - 978-3-96057-032-5 SP - 1 EP - 6 CY - Köthen AN - OPUS4-43078 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Halisch, Matthias A1 - Kruschwitz, Sabine A1 - Weller, Andreas A1 - Mensching, Bernadette A1 - Gürlich, Lucinda T1 - Maximizing the core value – joint investigations with special emphasis on complex electrical conductivity give new insights into Fontainebleau Sandstone N2 - Within this study we have shown, that spectral induced polarization is a reliable method for the enhanced characterization of the Fontainebleau sandstone in general, and for its related stratigraphical units in particular. Due to its high sensitivity towards pore network and pore surface changes, different stratigraphical units can be clearly differentiated and probably even classified. We have observed a good correlation between the maximum of the SIP phase shift and the dominant pore throat radius for this rock type, as it has been reported for others sandstones before [20]. T2 - Annual Symposium of the Society of Core Analysts CY - Vienna, Austria DA - 27.08.2017 KW - Spectral induced polarization KW - µ-CT KW - ESEM KW - Fontainebleau Sandstone PY - 2017 SP - 035, 1 EP - 035, 9 AN - OPUS4-43079 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nützmann, Kathrin A1 - Kranzmann, Axel A1 - Stephan-Scherb, Christiane T1 - Real time investigation of high temperature corrosion of ferritic alloys in SO2-gas N2 - The ageing of Fe-Cr model alloys in 0.5 % SO2 and 99.5 % Ar atmosphere was investigated to aim in a fundamental and systematic analysis of the combined oxidation and sulfidation mechanism. The crystallization and reaction paths for oxide and sulfide formation were followed in-situ by energy dispersive X-ray diffraction (EDXRD) in an early stage of corrosion (30 s – 24 h). For this technique, high energetic white synchrotron X-ray radiation (10-100 keV) was used as radiation source. Diffraction pattern were collected continuously in an early stage of corrosion up to 24 h during the complete ageing experiment. The crystalline phases, growing on top of the coupons, were identified directly via their specific dhkl values. The evolution of the extracted integral intensities of specific reflections of the corrosion products as a function of time access direct information about the kinetics of the nucleation and growth. The results presented here show for iron with 2 wt% Cr wuestite formation first. Wuestite vanishes after 10 min of reaction only and magnetite and hematite appear. Magnetite formation proceeds simultaneously with sulfide formation. Sulfides growth proceeds after an incubation time, which differs for low alloyed (2 wt% Cr) and high alloyed (9 wt% Cr) material. T2 - EUROCORR CY - Prague, Czech Republic DA - 03.09.2017 KW - In situ KW - Diffraction KW - Corrosion PY - 2017 SP - 79746 AN - OPUS4-44708 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gulikers, J. A1 - Millar, Steven A1 - Wilsch, Gerd T1 - Practical application of Laser Induced Breakdown Spectroscopy for determinafion of the chioride content in concrete structures N2 - This paper will address the relevance of chloride measurements in practice for durability condition assessment and a description of the working principle of LIBS will be given. Examples of chloride profiles obtained by the common wet chemical analysis will be shown and compared with results from LIBS measurements as to demonstrate the accuracy of the LIBS-technique. The latter will be supported by clear graphs. In addition examples on the extra information resulting from measurements performed with LIBS for improvement of condition assessment and prediction will be shown. T2 - CONFERENCE IN HONOR OF Centennial of LABORATORY OF CONSTRUCTION MATERIALS CY - Lausanne, Switzerland DA - 19.08.2018 KW - LIBS KW - Concrete KW - Chloride KW - Condition assesment PY - 2018 SP - 80 EP - 83 CY - Lausanne AN - OPUS4-47108 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krafka, Helmut ED - Richard, H. A. T1 - Risse in Schweißverbindungen - Heißrissarten, Heißrissentstehung und Heißrissprüfung N2 - Es wird ein Überblick über Heißrisse in heißrissanfälligen Schweißungen gegeben. Die Ursachen der Rissbildung der unterschiedlichen Heißrisstypen werden beschrieben und mit Fotos dokumentiert. Einige ausgewählte Heißrissuntersuchungsverfahren mit Fremdbeanspruchung der Proben werden erläutert und ihre Bewertungskriterien angegeben. N2 - A survey is given about hot cracks in hot crack susceptible welds. The reasons of the formation of different hot crack types are described and documented by photograhs. Some selected hot cracking testing procedures using externally loaded specimens are described and their evaluation criteria indicated. T2 - 32. Tagung des DVM-Arbeitskreises Bruchvorgänge CY - Berlin, Germany DA - 22.02.2000 KW - heißrissanfällige Schweißungen KW - Heißrisstypen PY - 2000 VL - 232 SP - 161 EP - 171 PB - DVM - Deutscher Verband für Materialforschung und -prüfung CY - Berlin AN - OPUS4-47023 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wack, Yannick A1 - Heckel, Thomas A1 - Boehm, Rainer A1 - Brackrock, Daniel T1 - Simulation der Schallausbreitung in Eisenbahnschienen mit FEM und SAM N2 - Die Simulation von Ultraschallausbreitung ist ein wesentliches Hilfsmittel zur Optimierung von Prüfanordnungen und wird zunehmend in der Prüfvorbereitung eingesetzt. Eisenbahnschienen sind Bauteile mit komplexer Geometrie und im eingebauten Zustand eingeschränkter Zugänglichkeit. Bei der Prüfung im Feld entstehen aus der Schienengeometrie komplexe Echosignale mit Formanzeigen, die schwer zu interpretieren sind. Für das bessere Verständnis der Schallausbreitung in der Eisenbahnschiene wird diese in einem ersten Schritt mit Hilfe verschiedener Ansätze modelliert. Hierbei werden Finite Elemente Methoden und semi-analytischen Modelle verwendet. In einem zweiten Schritt werden die Ergebnisse der Simulationsmodelle einander gegenübergestellt und mit Messungen an realen Schienen verglichen. Ziel dieser Untersuchungen ist die Validierung von Simulationsverfahren mit Hilfe von Messdatensätzen und Überprüfung der Anwendbarkeit bei der Bewertung von Ergebnissen der Schienenprüfung. T2 - DGZfP-Jahrestagung 2018 CY - Leibzig, Gemany DA - 07.05.2018 KW - Ultraschall KW - FEM KW - Eisenbahn KW - Simulation KW - SAM PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-474585 SP - Poster 4 - 1 EP - 5 PB - Deutsche Gesellschaft für zerstörungsfreie Prüfung e.V. (DGZfP) AN - OPUS4-47458 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völker, Christoph T1 - Visualization of automated multi‐sensor NDT assessment of concrete structures (NDT Data Fusion) N2 - Nondestructive testing(NDT) of concrete buildings allows efficient repair measures. Multi-sensor platforms collect large data sets but the data analysis is typically performed manually. Data Fusion uses the full potential of a multi-sensory data set in order to: - improve information quality (reliability, robustness, accuracy, clarity, completeness) - enable automated algorithm based data analysis. This poster summarizes results of the IGSTC-project entitled "NDT-Data Fusion" (short title) and demonstrates a significant improvement in the testing performance for the example of corrosion detection. T2 - IGSTC-Partners Meeting 2017 CY - Jodhpur, India DA - 22.10.2017 KW - NDT KW - Data Fusion KW - Concrete KW - Corrosion KW - Data analytics PY - 2017 AN - OPUS4-42716 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sankat, Nina A1 - Wilsch, Gerd A1 - Gottlieb, Cassian A1 - Millar, Steven T1 - Analysis of concrete structures using Laser-Induced Breakdown Spectroscopy N2 - The Laser-Induced Breakdown Spectroscopy (LIBS) is a laser spectroscopic method which allows a time efficient, minor-destructive, chemical analysis of materials. In principle all elements on the periodic table can be simultaneously analysed by using LIBS, regardless of the state of aggregation. LIBS offers numerous applications in the field of civil engineering; most importantly the analysis of building materials. This work will focus on the evaluation of concrete structures and harmful substances which can penetrate the concrete. A variety of information can be collected through LIBS. Determining the concentration of harmful substances like chloride, sodium or sulphur, the examination of the carbonation depth and the distinction between varying layers of materials (e.g. aggregates, cement paste, metals, etc.) are possible applications. All this information can be provided through one LIBS measurement in the form of a high resolution 2D element map, with resolutions up to 0.1 mm x 0.1 mm. To scan a concrete surface only an optical access is needed. To create a depth profile of an intruding substance the extraction of a drill core is necessary. Onsite measurements via LIBS can be conducted by using a mobile version of the LIBS system. Through using calibration curves LIBS allows not only the qualitative but also quantitative analysis of element concentrations. All those prospects make LIBS a trendsetting method to secure the integrity of infrastructures in a sustainable manner. A variety of examples which show the performance and results of LIBS analysis will be presented. T2 - CoMS 2017 CY - Zadar, Croatia DA - 19.04.2017 KW - Testing method KW - Concrete KW - LIBS KW - Harmful substances PY - 2017 SN - 978-953-8168-04-8 VL - 1 SP - 334 EP - 340 AN - OPUS4-42630 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Souza, Roberto A1 - Knaust, Christian A1 - Andreini, M. A1 - La Mendola, S. T1 - Probability Distribution Sensitivity on the Thermo-Mechanical FEM of a Concrete Tunnel Exposed to Fire N2 - A probabilistic approach for finite element analysis (FEA) for tunnel linings exposed to the nominal fire is presented. The probabilistic FEA accounted for the uncertainties distributions tied to the conductivity and specific heat as well as of the compressive strength, tensile strength, Young’s modulus, and ultimate strain in compression. To get an understanding on the influence of different probability density functions on the distribution of maximum displacements of the tunnel lining, a sensitivity analysis was performed. Four sets of FEAs were carried out with different probability distributions of the conductivity, the specific heat, and the compressive strength of the concrete, respectively. An experimental design based on a Latin Hypercube Sampling algorithm was performed to define the input parameters which describe each analysis case. A reliability analysis was executed considering a limit state function based on the temperature-dependent ultimate strain. The results show that, depending on the distribution adopted, the standard deviation of the maximum displacements can vary up to 47,4% of the minimum standard deviation. The large standard deviation is associated with the possibility of a greater displacement and, hence, to a structure more vulnerable to fire. T2 - 4th Symposium Structural Fire Engineering Braunschweig CY - Brunswick, Germany DA - 12.09.2017 KW - Probabilistic analysis KW - Fire KW - Concrete KW - Finite elements analysis PY - 2017 SP - 1 EP - 13 AN - OPUS4-42681 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rohn, H. A1 - Simon, Franz-Georg A1 - Schmidt, M. A1 - Giegrich, J. A1 - Oberender, C. A1 - Denz, W. A1 - Niebaum, A. ED - Ludwig, C. ED - Matasci, C. T1 - The Guideline Series VDI 4800 Resource Efficiency: An Approach for Increasing Resource Efficiency with Aim of Conservation of Natural Resources in the Industrial Sector N2 - In 2011, the Association of German Engineers (VDI) started working on a set of guidelines towards increased resource efficiency. These guidelines represent a framework that defines resource efficiency and outlines considerations for the producing industry. A special guideline for SMEs is included as well as guidelines on methodologies for evaluating resource use indicators, such as the cumulative raw material demand of products and production systems. Resource efficiency, defined here as the relationship between a specific benefit or use and the natural resources that need to be spent or consumed to attain this benefit or use. It can be evaluated by defining a function which expresses the specific benefit and quantifies the resource requirements through a set of indicators (use of raw materials, energy, water, land and ecosystem services including sinks). The results from this also depend on the system boundary parameters and the allocation rules for by-products and waste treatment options. Optimising resource use is possible at all stages of a product’s or production system’s life cycle chain (raw material extraction, production and manufacturing, use and consumption, and the end-of-life stage). VDI guidelines are widely accepted across Germany’s industrial sector and therefore represent an important means of mainstreaming resource efficiency in this target area. As well as providing a methodological framework, the guidelines describe strategies and measures towards increasing resource efficiency, and they enable industrial producers and service providers to identify potential areas of improvement. The full article presents an overview of the methodology and contents of these guidelines and discusses their impact in achieving absolute reductions in the industrial use of natural resources. KW - Resource efficiency KW - Life cycle thinking KW - Products and production systems KW - Standardization PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-426443 UR - https://www.wrforum.org/wrfpublicationspdf/boosting-resource-productivity/ SN - 978-3-9521409-7-0 SP - 125 EP - 132 PB - Paul Scherrer Institute CY - Villigen PSI, Switzerland ET - 1 AN - OPUS4-42644 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Wilsch, Gerd T1 - Fast Quantitative Chemical Analysis of Cencrete using LIBS N2 - Non-destructive testing of concrete based on laser induced breakdown spectroscopy in civil engineering. KW - LIBS KW - Concrete KW - Chloride PY - 2017 SP - 289 EP - 325 CY - Berlin, Germany AN - OPUS4-42648 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Winterkorn, R. A1 - Petrat, T. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Temperature generation of different travel path strategies to build layers using laser metal deposition N2 - Laser Metal Deposition offers the chance to build near net shape parts. The temperature evolution within the process has an influence on track and layer geometries. There are special travel path strategies required to produce near net shape components and reduce shape deviation resulting of error propagation. This paper deals with the temperature progression of individual layers and the maximum heating of deeper substrate regions. Spiral and zig-zag strategies are examined. The investigations are carried out using S235JR as substrate and 316L as powder material. The influence of different strategies on temperature evolution is discussed. The results from the experiments show that various production strategies are associated with different temperature fields. Furthermore, the extent of the temperature variations of layer strategies and layer position are strongly dependent on the production direction. These results demonstrate the importance of developing suitable build-up strategies for parts of complex shape to ensure a stable process with constant temperature as well as even layers. T2 - Lasers in Manufacturing Conference 2017 CY - Munich, Germany DA - 26.06.2017 KW - 316L KW - Additive Manufacturing KW - Temperature behavior KW - Laser Metal Deposition KW - Stainless Steel KW - Edge effects PY - 2017 SP - 1 EP - 5 AN - OPUS4-42878 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Fischer, Daniel T1 - Charakterisierung von dotierten Zinnoxidschichten für die Detektion von Gasen durch ellipsometrische Messung der Oberflächenplasmonenresonanz N2 - In der vorliegenden Dissertation wird die Verbesserung von Gassensoren durch Beschichtung mit dotierten Zinnoxidschichten untersucht, wobei zur Messung der Gase die Methode der oberflächenplasmonenresonanzverstärkten Ellipsometrie (SPREE) angewendet wurde. Die vorgestellten Ergebnisse unterteilen sich dabei in drei Schritte: Herstellung der Schichtsysteme, Analyse der chemischen, strukturellen und optischen Eigenschaften, sowie die Anwendung in der SPREE Gasmessung. Die dotierten Zinnoxidschichten wurden erfolgreich mittels Hochfrequenz-Magnetronsputtern hergestellt, indem das Zinnoxidtarget mit dem metallischen Dotierungsmaterial (Eisen bzw. Nickel) modifiziert wurde. Die chemische Analyse der Schichten wurde mit energiedispersiver Röntgenspektroskopie (EDX), Flugzeit-Sekundärionenmassenspektrometrie (TOF-SIMS) und Röntgenfluoreszenz unter streifendem Einfall (GI-XRF) durchgeführt. Die EDX Untersuchungen zeigten qualitativ, dass das Dotierungsmaterial in die Schicht eingebaut wurde. Mithilfe der TOF-SIMS Experimente konnte nachgewiesen werden, dass die Dotierungskonzentration innerhalb der Schicht heterogen verteilt ist und mithilfe der GI-XRF Messung konnte der Dotierungsgrad quantitativ mit ca. 10% bestimmt werden. Für die strukturelle Untersuchung wurden die Methoden der Rasterkraftmikroskopie (AFM) und Transmissionselektronenmikroskopie (TEM) ausgewählt. Die AFM Messungen zeigten, dass die Schichten eine mittlere quadratische Rauheit kleiner als 1 nm aufweisen und die Rauheit damit nicht als Faktor in der Gasmessung berücksichtigt werden muss. In den TEM Messungen wurde der Schichtaufbau bestätigt und gezeigt, dass in den dotierten Schichten nanokristalline Strukturen vorliegen. Die optische Charakterisierung der Schichten wurde mit spektraler Ellipsometrie (SE) durchgeführt, um die dielektrische Funktion in Abhängigkeit der Dotierung zu untersuchen. Dafür wurden Modelle für die dielektrische Funktion auf der Basis von mehreren Gauss-Funktionen entwickelt. Es zeigte sich, dass die undotierten Schichten sich wie typische Dielektrika mit Bandkanten >4 eV verhält und mit drei Gauss-Funktionen simuliert werden kann. Für die dotierten Schichten verschiebt sich die Bandkante, in Abhängigkeit vom Grad der Dotierung und dem Oxidationsgrad, zu bis zu 2.1 eV. Außerdem muss das Modell um eine zusätzliche Gauss-Funktion im nahen Infrarot erweitert werden, die auf die Anwesenheit von metallischen Nanopartikeln zurückzuführen ist. Weiterhin zeigte sich, dass die dielektrischen Eigenschaften von der Dicke der Schicht abhängen. Die Benutzung der Zusatzschichten in der SPREE Gasmessung zeigte, dass diese Schichten die Sensoroberfläche effektiv vor Degradation schützt. Weiterhin wurde nachgewiesen, dass die Sensitivität der jeweiligen Sensorschicht für bestimmte Gase von der Dotierung der Schicht abhängt. Es wurde gezeigt, dass eine Eisendotierung zu einer erhöhten Sensitivität für Kohlenmonoxid führt, während undotierte Schichten vor allem unpolare Alkane bevorzugen. Die Nickel-dotierten Schichten zeigten im Vergleich zur Eisendotierung deutlich schlechtere Ergebnisse für alle Gase. Diese Effekte wurden auf die unterschiedliche Bindungsstärke der Gase an die metallischen Nanopartikel und das Vorhandensein einer unterschiedlichen Zahl an Adsorptionsplätzen zurückgeführt. Für Wasserstoff wurden für alle Proben vergleichbare Ergebnisse gefunden, was darauf zurückzuführen ist, dass diese Moleküle aufgrund der geringen Größe und Masse in die Schicht diffundieren. Zusätzlich wurde das SPREE Verfahren signifikant verbessert, indem die Druckabhängigkeit Sensoren erstmals erfasst wurde. Weiterhin wurde die Auswertung weiterentwickelt, indem nur einzelne Parameter des Stokes-Vektors für die Gasmessung benutzt wurden. KW - Oberflächenplasmonen KW - Ellipsometrie KW - Transparente Halbleiter KW - Dotiertes Zinnoxid KW - Gasmessung PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-435039 DO - https://doi.org/10.14279/depositonce-5969 SP - 1 EP - 154 PB - Technische Universität CY - Berlin AN - OPUS4-43503 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Kern, Simon A1 - Guhl, Svetlana A1 - Meyer, Klas A1 - Maiwald, Michael ED - Maiwald, Michael T1 - Validation report on NMR N2 - The departure from the current automation landscape to next generation automation concepts for the process industry has already begun. Smart functions of sensors simplify their use and enable plug and play integration, even though they may appear to be more complex at first sight. Smart sensors enable concepts like self-diagnostics, self-calibration, and self-configuration/ parameterization whenever our current automation landscape allows it. Here we summarize the currently discussed general requirements for process sensors 4.0 and introduce a smart online NMR sensor module as example, which was developed for an intensified industrial process funded by the EU’s Horizon 2020 research and innovation programme (www.consensspire.eu). KW - Process Monitoring KW - Online NMR Spectroscopy KW - Indirect Hard Modeling KW - Process Control KW - Process Analytical Technology KW - CONSENS PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-435521 SP - 1 EP - 31 AN - OPUS4-43552 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erenberg, Marina A1 - Bletzer, Claus A1 - Feldkamp, Martin A1 - Musolff, André A1 - Nehrig, Marko A1 - Wille, Frank T1 - Experimental investigations of the burning behaviour of transport package impact limiters and of fire spread impact onto the cask N2 - Accident safe packages for the transport of spent nuclear fuel and high-level waste shall fulfil international IAEA safety requirements. Compliance is shown by consecutive mechanical and thermal testing. Additional numerical analysis are usually part of the safety evaluation. For damage protection some package designs are equipped with wood filled impact limiters encapsulated by steel sheets. The safety of these packages is established in compliance with IAEA regulations. Cumulative mechanical and fire tests are conducted to achieve safety standards and to prevent loss of containment. Mechanical reliability is proven by drop tests. Drop testing might cause significant damage of the impact limiter steel sheets and might enable sufficient oxygen supply to the impact limiter during the fire test to ignite the wood filling. The boundary conditions of the fire test are precisely described in the IAEA regulatory. During the test the impact limiter will be subjected to a 30 minute enduring fire phase. Subsequent to the fire phase any burning of the specimen has to extinguish naturally and no artificial cooling is allowed. At BAM a large-scale fire test with a real size impact limiter and a wood volume of about 3m3 was conducted to investigate the burning behaviour of wood filled impact limiters in steel sheet encapsulation. The impact limiter was equipped with extensive temperature monitoring equipment. Until today burning of such impact limiters is not sufficiently considered in transport package design and more investigation is necessary to explore the consequences of the impacting fire. The objective of the large scale test was to find out whether a self-sustaining smouldering or even a flaming fire inside the impact limiter was initiated and what impact on the cask is resulting. The amount of energy, transferred from the impact limiter into the cask is of particular importance for the safety of heavy weight packages. With the intention of heat flux quantification a new approach was made and a test bench was designed. T2 - ASME 2018 Pressure Vessels and Piping Conference CY - Prague, Czech Republic DA - 15.07.2018 KW - Shock absorber KW - Impact limiter KW - Wood KW - Thermal testing KW - Fire KW - Smoldering KW - IAEA KW - Fire test PY - 2018 SN - 978-0-7918-5170-8 VL - PVP2018 SP - 84714-1 EP - 84714-10 AN - OPUS4-46984 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schwaar, Timm A1 - Remmler, Dario A1 - Börner, Hans G. T1 - Spec2Seq N2 - Spe2Seq automatically translates mass spectrometry fragment spectra of precision polymers into their corresponding sequence. This software is especially useful for combinatorial approaches. KW - Java GUI KW - Polymers KW - Mass spectroscopy (MS) PY - 2018 SP - 1 EP - 8 PB - Humboldt-Universität CY - Berlin AN - OPUS4-46987 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilsch, Gerd A1 - Gottlieb, Cassian A1 - Günther, Tobias A1 - Millar, Steven ED - Forde, Mike T1 - Application of laser induced breakdown spectroscopy N2 - A big part of the infrastructure is made of concrete, which is a multiphase system made of cement, aggregates, water and pores. Concrete is often used in combination with steel as reinforced concrete. Environmental influences, especially the ingress of harmful ions in combination with the ingress of water, trigger different damage processes which reduce the designed lifetime of a structure. The ingress of chlorides from de-icing salt or sea water leads to corrosion of the reinforcement. In addition, the carbonation of the concrete may trigger the corrosion of the reinforcement. The ingress of alkalis from deicing salts may cause the expansion of the amorphous silica aggregates (alkali-silica reaction) through formation of a swelling gel of calcium silicate hydrate if water is present. The ingress of sulphates may cause spalling of the concrete surface due to ettringite formation. For the standard procedure in civil engineering cores are taken, cut in slices, grinded and the obtained homogenized powder is solved in acid and investigated by standard procedures. BAM has developed the LIBS technique for the 2D evaluation of the chemical composition of concrete. The technique is established for automated laboratory use with high numbers of samples to investigate transport processes of harmful species (Cl-, CO2 , SO4 2-and alkalis) in concrete. Information about ingress depth and the quantitative values are important to estimate the remaining lifetime of the infrastructure. LIBS is a surface technique. To get information about the ingress depth, a drill core has to be taken and cut in the middle. The measurements are carried out at the cross section. The main advantages of LIBS are the direct measurement on the surface of the concrete, fast analysis (sample rate 100 Hz) with a spatial resolution of up to 100 µm, the consideration of the heterogeneity of the concrete and the possibility of automated measurements which save a lot of manpower and time. As an example the investigation of ingress profiles for standard diffusion and migration tests in civil engineering takes hours in comparison to just a few minutes using LIBS. At the same time a 2D-evaluation provides information about hot spots of elemental concentration which may not be found by standard methods. The state of the art of LIBS technique for applications in civil engineering will be presented, including typical results of 2D investigation of concrete in laboratory. The performance is also demonstrated by examples for onsite applications using a mobile LIBS system. The road map to standardization is presented as well. T2 - Structural Faults + Repair-2018 CY - Edinburgh, UK DA - 15.05.2018 KW - Sulphate KW - Chloride KW - Concrete KW - LIBS PY - 2018 SN - 0-947644-86-5 DO - https://doi.org/10.25084/sfr.2018.0030 SP - 1 EP - 7 PB - University of Edinburgh CY - Edinburgh AN - OPUS4-46947 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe T1 - Die zyklische R-Kurve als Kenngröße des Kurzrisswachstums N2 - Unter der zyklischen R-Kurve versteht man die Abhängigkeit des Schwellenwertes gegen Ermüdungsrissausbreitung von der Risstiefe im Kurzrissbereich. Bei Spannungsverhältnissen R = omin/omax < ca. 0,7 erhöht sich der Schwellenwert AKltl ausgehend von einer intrinsischen, werkstoffspezifischen Untergrenze mit zunehmender Risstiefe, bis er einen risslängenunabhängigen Wert erreicht. Ursache ist der graduelle Aufbau unterschiedlicher Rissschließeffekte. Die besondere Bedeutung des Kurzrisswachtums allgemein und der zyklischen R-Kurve speziell besteht darin, dass sie ein physikalisches Bindeglied zwischen der konventionellen Schwingfestigkeit (Wöhlerkurve) und der Bruchmechanik repräsentieren. Der Beitrag befasst sich sowohl mit der experimentellen Ermittlung der zyklischen R-Kurve als auch mit ihrer Anwendung auf Rissarrest im Zusammenhang mit Schwingfestigkeitsbetrachtungen. Die experimentelle Ermittlung der zyklischen R-Kurve erfordert einen experimentellen Aufwand, der deutlich über den der Langrissbruchmechanik hinausgeht. Insbesondere im Anfangsbereich ist eine sehr genaue Messung der Risstiefe erforderlich, was eine Verbesserung etwa der konventionellen Potentialmethode erforderlich macht. Von wesentlicher Bedeutung ist auch, dass der Ausgangsriss vor Beginn des eigentlichen Versuchs keine Rissschließeffekte gesehen haben darf. Realisiert wird das durch eine vorgeschaltete Phase von sog. „Compression Pre-cracking“, d.h. durch Anschwingen komplett im Druckbereich. T2 - DVM Tagung der Werkstoffprüfung 2018 CY - Bad Neuenahr, Germany DA - 06.12.2018 KW - Kurzrissbruchmechanik KW - Zyklische R-Kurve KW - Rissschließphenomen KW - Rissarrest PY - 2018 AN - OPUS4-46874 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kutz, Philipp A1 - Otremba, Frank A1 - Werner, Jan A1 - Sklorz, Christian T1 - Development of a Single Walled Tank under Cryogenic Conditions made of Composite N2 - The use of glass-fiber reinforced plastic (GRP) can reduce the weight of tanks significantly. By replacing steel with GRP in tanks for gases (propane, etc.) a weight reduction of up to 50 % was reached. In this project not only the material should be optimized, but also the design. Previous tanks consist of a double-walled structure with an insulation layer between the two shells (e.g. vacuum). Goal of this project is to realize a single-walled construction of GRP with an insulation layer on the outside. To determine the temperature dependent material values, two different experiments are performed: In the first experiment, temperature dependent material properties of liquid nitrogen found in literature research are validated in a simple setup. The level of liquid nitrogen in a small jar is measured over the experiment time. Numerical simulation shows the change of nitrogen level with sufficient precision. In the second experiment, a liquid nitrogen is applied on one side of a GRP plate. Temperature is measured with thermocouples on top and bottom of the GRP plate, as well as in the middle of the plate. By use of numerical simulation, temperature dependent thermal conductivity is determined. In the third experiment, a test stand is designed to examine different insulation materials. In this test stand, the insulation material can easily be changed. A numerical simulation, in which the determined material data is used, is performed as well for this test stand. The experiments show, that GRP can be used in cryogenic environments. Multiphase simulations are a suitable tool to describe the energy absorption of thermal energy due to thermal phase change. Results on different insulation materials will follow. T2 - IMECE 2018 CY - Pittsburgh, PA, USA DA - 09.11.2018 KW - Lightweight design KW - Thermal properties of GRP KW - Liquid nitrogen KW - LNG PY - 2018 UR - http://proceedings.asmedigitalcollection.asme.org/proceeding.aspx?articleID=2722335 SN - 978-0-7918-5214-9 DO - https://doi.org/10.1115/IMECE2018-86365 VL - 9 SP - V009T12A019 PB - ASME AN - OPUS4-47321 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ewert, Uwe A1 - Zscherpel, Uwe A1 - Vogel, Justus A1 - Zhang, F. A1 - Long, N.X. A1 - Nguyen, T.P. T1 - Visibility of Image Quality Indicators (IQI) by Human Observers in Digital Radiography in Dependence on Measured MTFs and Noise Power Spectra N2 - Digital radiographic images were analysed to predict the visibility of image quality indicators (IQI), based on normalized noise power spectra (NNPP) and modulation transfer function (MTF) measurements. The fixed pattern noise of some digital detectors result in different noise spectra, which influence the visibility of different IQIs, depending on the hole diameter. Studies, based on measurement of basic spatial resolution and contrast to noise ratio were performed together with presampled MTF measurements and the NNPS in dependence on the spatial frequency. Plate hole IQIs, step hole IQIs, and equivalent penetrameter sensitivity (EPS) IQIs based on ASTM E 746 were measured to verify the influence of the different parameters. Modelling of digital images was used to verify the applied numeric tools. A study has been performed for imaging plates and digital detector arrays to analyse differences. Formulas for the prediction of the visibility functions for hole type IQIs are derived. In consequence the standards for characterization and classification of computed radiography (ASTM E 2446) and radiography with DDAs (ASTM E 2597) need to be revised. T2 - 12th ECNDT 2018 CY - Gothenburg, Sweden DA - 11.06.2018 KW - Image evaluation KW - Computed radiography (CR) KW - Digital Detector Array (DDA) KW - Detail detection PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-473486 UR - www.ndt.net/?id=22967 SN - 1435-4934 VL - 23 IS - 8 SP - 1 EP - 7 PB - NDT.net CY - Kirchwald AN - OPUS4-47348 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ewert, Uwe A1 - Zscherpel, Uwe A1 - Zhang, F. A1 - Long, N.X. A1 - Phong, N. T1 - Essentielle Parameter zur numerischen Abschätzung der Sichtbarkeit von Bildgüteprüfkörpern in der digitalen Radiographie N2 - Die Voraussetzungen für die Vorhersage der Sichtbarkeit von Bildgüteprüfkörpern (BPK) wurden seit Beginn der kommerziellen Anwendung der technischen Radiographie diskutiert und in diversen nationalen und internationalen Standards festgeschrieben. Diese Fragen werden nach Einführung der digitalen Radiographie und der CT wieder neu diskutiert. Draht BPKs wurden in Deutschland seit 1935 (DIN 1915: 1935) und später in den meisten europäischen Ländern benutzt. In den USA und Frankreich wurden vorzugsweise BPKs mit Löchern verwendet (ASTM E 1025 seit 1984 oder E 1742 seit 1992 bzw. die Vorgängernorm MIL STD-543 seit 1962). Jetzt werden auch die Umrechnungsnormen zur Erkennbarkeit von Draht zu Loch-BPKs in Frage gestellt. ISO 19232-3, der französische RCCM-Kode einerseits und ASTM E 747 und ASME BPVC Section V Tab. T-276 andererseits unterscheiden sich erheblich bei den Anforderungen im Bereich hoher Wandstärken (Hochenergieradiographie). Untersuchungen dazu werden vorgestellt. Mit Einführung der digitalen Detektoren ändern sich auch die Rauschspektren. Durch die Herstellung werden insbesondere bei Speicherfolien "Rauschmuster" eingeprägt, die bei hohen Belichtungsdosen sichtbar werden. Diese veränderten Rauschspektren ergeben auch veränderte Erkennungsparameter für menschliche Bildauswerter. Hierzu wurden an ausgewählten Detektoren MTFs (presampled) und normierte Rauschspektren gemessen. Erweiterte Erkennbarkeits-Formeln zur Vorhersage der Sichtbarkeit von BPKs für Bildauswerter und erste Ergebnisse werden vorgestellt. T2 - DGZfP-Jahrestagung 2018 CY - Leipzig, Germany DA - 07.05.2018 KW - Image quality KW - Computed radiography (CR) KW - Digital Detector Array (DDA), KW - Sichtbarkeit von Anzeigen PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-473496 UR - www.ndt.net/?id=23069 VL - 2018 SP - 1 EP - 14 PB - Deutsche Gesellschaft für zerstörungsfreie Prüfung e.V. (DGZfP) AN - OPUS4-47349 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Heideklang, René T1 - Data fusion for multi-sensor nondestructive detection of surface cracks in ferromagnetic materials N2 - Fatigue cracking is a dangerous and cost-intensive phenomenon that requires early detection. But at high test sensitivity, the abundance of false indications limits the reliability of conventional materials testing. This thesis exploits the diversity of physical principles that different nondestructive surface inspection methods offer, by applying data fusion techniques to increase the reliability of defect detection. The first main contribution are novel approaches for the fusion of NDT images. These surface scans are obtained from state-of-the-art inspection procedures in Eddy Current Testing, Thermal Testing and Magnetic Flux Leakage Testing. The implemented image fusion strategy demonstrates that simple algebraic fusion rules are sufficient for high performance, given adequate signal normalization. Data fusion reduces the rate of false positives is reduced by a factor of six over the best individual sensor at a 10 μm deep groove. Moreover, the utility of state-of-the-art image representations, like the Shearlet domain, are explored. However, the theoretical advantages of such directional transforms are not attained in practice with the given data. Nevertheless, the benefit of fusion over single-sensor inspection is confirmed a second time. Furthermore, this work proposes novel techniques for fusion at a high level of signal abstraction. A kernel-based approach is introduced to integrate spatially scattered detection hypotheses. This method explicitly deals with registration errors that are unavoidable in practice. Surface discontinuities as shallow as 30 μm are reliably found by fusion, whereas the best individual sensor requires depths of 40–50 μm for successful detection. The experiment is replicated on a similar second test specimen. Practical guidelines are given at the end of the thesis, and the need for a data sharing initiative is stressed to promote future research on this topic. KW - Data fusion KW - Non destructive testing KW - Multi-sensor KW - Surface cracks PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-471339 DO - https://doi.org/10.18452/19586 SP - 1 EP - 157 CY - Berlin AN - OPUS4-47133 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Even, Morgane A1 - Hutler, C. A1 - Wilke, Olaf A1 - Vieth, B. A1 - Luch, A. T1 - Investigations on emission properties of VOCs from consumer products made of polymers N2 - There is a need for an assessment of the emission properties of volatile organic compounds (VOCs) from consumer products. A method comparison was carried out to evaluate adapted and cost-effective procedures for such items. Smaller and automated emission chambers depicted similar kinetics compared to a 203 L standard chamber. Toy samples made of PVC (Polyvinyl chloride) emitted more VOCs compared to other tested polymeric products. The emissions from 2 selected samples were studied to allow an evaluation of the resulting room concentration and external exposure of a child. Obtained concentrations were not of concern. T2 - Indoor Air Conference 2018 CY - Philadelphia, USA DA - 22.07.2018 KW - Emission chamber KW - VOC KW - Consumer article PY - 2018 SP - Paper 381, 1 EP - 2 AN - OPUS4-45654 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koclęga, Damian A1 - Dymek, S. A1 - Radziszewska, A. A1 - Huebner, J. T1 - Laser cladding of Inconel 686 overlay weld on low carbon steel N2 - The work presents the effects of the change of the laser cladding parameters on microstructure, chemical composition and mechanical properties of Inconel 686 overlays (coatings). To obtain the best quality of These coatings the various parameters of laser cladding such as the power density of the laser beam, the laser beam velocity and overlapping ratio of the weld tracks were applied. The substrates were boilers plate made of the 13CrMo4-5 steel. Ni - base alloys characterize by the excellent high-temperature corrosion resistance, good strength and good ability to work in aggressive environments. This could be achieved by the reduction of the substrate melting and its dissolution into the overlays. The microstructure, chemical composition of the obtained overlays were investigated by means of a light microscope, a scanning electron microscope (SEM) equipped with the EDS detector. The overlays had cellular-dendritic structure. The variations of the chemical composition (especially Mo, Ni and W ) in the interdendritic and dendritic regions were observed. The interdendritic regions were enriched during solidifications in Mo and W and had lower content of Ni. T2 - 26TH INTERNATIONAL CONFERENCE ON METALLURGY AND MATERIALS CY - Brno, Czech Republic DA - 24.05.2017 KW - Laser cladding KW - Overlay KW - Chemical composition KW - Inconel 686 KW - Process optimization PY - 2017 SP - 1327 EP - 1333 AN - OPUS4-45629 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Liehr, Sascha A1 - Muanenda, Y. A1 - Münzenberger, Sven A1 - Krebber, Katerina T1 - Wavelength-modulated C-OTDR techniques for distributed dynamic measurement N2 - We present two wavelength-modulated coherent optical time domain reflectometry techniques for dynamic, quantitative and distributed measurement. The robust and simple techniques are based on backscattering correlations along the time axis and along the pulse wavelength shift axis. T2 - 26th International Conference on Optical Fibre Sensors OFS-26 CY - Lausanne, Switzerland DA - 24.09.2018 KW - Fiber optics sensors KW - Optical time domain reflectometry KW - OTDR KW - DAS KW - Distributed strain sensor KW - Rayleigh scattering PY - 2018 DO - https://doi.org/10.1364/OFS.2018.TuE15 SP - 1 EP - 4 AN - OPUS4-46414 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hothan, Sascha A1 - Häßler, Dustin ED - Zehfuß, Jochen T1 - Reaktive Branschutzsysteme für Stahlbauteile – Zulassung, Instandhaltung und Dauerhaftigkeit N2 - Die Erkenntnisse zu reaktiven Brandschutzsystemen (RBS) werden kontinuierlich erweitert, was sich in der Entwicklung neuer Produkte und der Ausweitung des durch technische Regelungen abgedeckten Anwendungsbereichs äußert. Der hier vorliegende Beitrag konzentriert sich auf die Verwendung von RBS auf Stahlkonstruktionen. In den vergangenen zehn Jahren wurden, abgesichert durch neue Erkenntnisse aus der Forschung, die Anwendung auf Stahlzuggliedern mit offenem Profil präzisiert und im Rahmen allgemeiner bauaufsichtlicher Zulassungen (abZ) neu geregelt. Ferner wurde die Grundlage geschaffen, die Anwendung von RBS auf Zuggliedern mit kreisrundem Vollprofil zu bewerten und auf Basis der abZ zu ermöglichen. Neben einer umfassenden Darstellung der aktuellen nationalen und europäischen Regelungen zu RBS, werden technologische Besonderheiten und deren Einfluss auf den Regelungsinhalt im Beitrag thematisiert. In der jüngsten Vergangenheit stellt sich mit zunehmender Dringlichkeit die Frage nach der Bewertung der Dauerhaftigkeit von RBS für lange Zeiträume, wobei damit Nutzungsdauern weit jenseits der in den nationalen und europäischen Regelungen bereits etablierten 10 Jahre gemeint sind. In diesem Zusammenhang ist zu klären, wie der Feuerwiderstand von Konstruktionen zu bewerten ist, die bereits über lange Zeiträume mit RBS versehen sind. Nicht zuletzt stellt sich die Frage nach der Dauerhaftigkeit der Systeme selbst und adäquaten Prüfverfahren zu deren Beantwortung. Neue und bereits etablierte Ansätze werden vorgestellt und diskutiert. Der Beitrag schließt mit einer Darstellung der aktuellen Forschung. Neben den Forschungsaktivitäten zur Dauerhaftigkeit sind hier insbesondere Untersuchungen zur Anwendung und Bewertung von RBS auf Grundlage von Naturbränden und extremen Brandereignissen genannt. Neuste Untersuchungen befassen sich auch mit der Anwendung von RBS auf komplexen Geometrien wie auch auf anderen Substraten wie Beton, Aluminium und faserverstärkten Kunststoffen sowie hybriden Werkstoffen. Die hybriden Werkstoffe aus der Kombination von Metallen und Verbundwerkstoffen sind derzeit vorwiegend im Behälter-, Fahrzeug- und Flugzeugbau anzutreffen. Auch die bereits vor Jahrzehnten begonnenen Aktivitäten zur Entwicklung rechnerischer Verfahren zur Beurteilung der Wirkungsweise von RBS werden in der aktuellen Forschung fortgeführt und weiterentwickelt. T2 - Braunschweiger Brandschutz-Tage 2018 CY - Brunswick, Germany DA - 19.09.2018 KW - Reaktive Brandschutzsysteme KW - Feuerwiderstand KW - Dauerhafigkeit KW - Stahlbauteile KW - Zulassung KW - Instandhaltung PY - 2018 SN - 978-3-89288-219-0 SN - 1439-3875 SN - 0934-2419 VL - 234 SP - 41 EP - 70 PB - Institut für Baustoffe, Massivbau und Brandschutz (iBMB) CY - Braunschweig AN - OPUS4-46415 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bertovic, Marija T1 - Assessing and Treating Risks in Mechanised NDT: A Human Factors Study N2 - Reliability of NDT is affected by human factors, which have thus far received the least amount of attention in the reliability assessments. With increased use of automation, in terms of mechanised testing (automation-assisted inspection and the corresponding evaluation of data), higher reliability standards are believed to have been achieved. However, human inspectors, and thus human factors, still play an important role throughout this process and the risks involved in this application are unknown. The aim of this study was to explore for the first time the risks associated with mechanised NDT and find ways of mitigating their effects on the inspection performance. Hence, the objectives were to identify and Analyse potential risks in mechanised NDT and devise measures against them. To address those objectives, a risk assessment in form of a Failure Modes and Effects Analysis (FMEA) was conducted. This analysis revealed potential for failure during both the acquisition and evaluation of NDT data that could be assigned to human, technology, and organisation. Since the existing preventive measures were judged to be insufficient to defend the system from identified failures, new preventive measures were suggested. KW - NDT KW - Human factors KW - Risk assessment KW - FMEA KW - Reliability KW - Human error PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-463325 SN - 1616-069X IS - 161 SP - 52 EP - 62 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-46332 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Otremba, Frank A1 - Romero-Navarrete, José A. A1 - Lozano Guzmán, A. A. T1 - Cargo securement standards and braking maneuvers N2 - There was a need to validate the longitudinal performance required for the cargo securement, as current standards exhibit differences. A model has been proposed in this paper, to simulate the effect of a shifting cargo on the braking efficiency of the vehicle. Results suggest that the braking efficiency can be greater in the case of a shifting cargo, as a result of the uncoupling of the cargo-vehicle systems, implying that similar braking forces are exerted on a reduced mass. The shifting of the cargo can occur as a result of the vibration of the vehicle, that leads to having a diminished friction force to prevent the shifting of the cargo. T2 - International Research Conference CY - Paris, France DA - 29.10.2018 KW - Cargo KW - Securement KW - Maneuvers PY - 2018 SP - 2105 EP - 2108 AN - OPUS4-46423 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Romero-Navarrete, José A. A1 - Otremba, Frank A1 - Lozano Guzmán, A. A. T1 - Energy saving potentials of railways instead of roadways: Mexico case N2 - For the last 100 years, Mexico has not invested in new freight railway infrastructure. Consequently, the values of indicators about the use of such Transport mode are poorly compared with those of developed countries such as Germany. T2 - Railways 2018 CY - Sitges, Barcelona, Spain DA - 03.09.2018 KW - Energy saving KW - Potentials KW - Railways KW - Roadways PY - 2018 UR - http://www.railwaysconference.com/ SP - Paper E5.05, 1 EP - 4 PB - Civil-Comp Limited CY - Dun Eaglais, UK AN - OPUS4-45909 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bente, Klaas T1 - The thermoacoustic effect and its application in air-coupled testing of composite structures N2 - Airborne ultrasonic testing of lightweight, structured composite materials enables fast and contact-free non-destructive testing in aerospace and avoids material degradation due to contact with a coupling liquid. Established resonant air-coupled transducers consist of piezocomposite materials and several matching layers or more advanced materials like charged cellular polypropylene. The relaxation time and the specific frequency of such mechanical ultrasound emitters limit the spectrum of applications for each device. A short pulse length is key for reliable defect detection and each component at test can be best characterized at material- and geometry-specific frequencies. Here we show that focused thermoacoustic transducers are suited for testing lightweight, structured composite plates. Since the ultrasound is generated in air, these transducers show no resonance behavior and emit a broadband acoustic spectrum between 1.2 kHz and 1 MHz. Composite specimens of 3 mm to 9 mm thickness made of polylactide with a honeycomb structure were tested. Flat bottom holes were introduced to quantify the spatial resolution of the imaging method inside the strongly anisotropic specimen. As no broadband receivers are available yet, cellular polypropylene transducers were used as receivers, which limits the bandwidth of the method towards the bandwidth of the receiver. Nevertheless, we demonstrate the competitiveness of the thermoacoustic transducer compared to mechanical emitters at their respective resonance frequencies. Because a thermoacoustic transmitter features a nearly ideal pulse width, a single transmitter can be coupled with receivers with different resonance frequencies. With the development of broadband ultrasound receivers, air-coupled ultrasound spectroscopy will likely be possible in the near future. The analysed transducer holds the potential to speed up testing during production and maintenance in aerospace and automotives. Its combination with a broadband receiver could also expand the application field of air-coupled ultrasonic testing from a qualitative error detection towards a quantitative, spatially resolved analysis of mechanical material properties. T2 - 10th International Symposium on NDT in Aerospace CY - Dresden, Germany DA - 24.10.2018 KW - Thermoacoustics KW - Ultrasonic Testing KW - Broadband KW - Ultrasound Emission PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-464677 SN - 978-3-940283-96-2 SP - 1 EP - 8 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-46467 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Bandow, Nicole A1 - Jürgens, Frederike A1 - Schoknecht, Ute T1 - Beregnete Bauteile und Bauprodukte: Entwicklung von Vergabekriterien für den Blauen Engel mit Hilfe von Auslaugtests N2 - Auslaugversuche wurden mit verschiedenen Bauprodukten durchgeführt, die unter Anwendungsbe-dingungen mit Niederschlägen in Kontakt kommen können. In das Testprogramm wurden Lacke für Außenanwendungen, Wärmedämmverbundsysteme, Dachziegel und polymere Dachfolien einbezogen. Mit diesen Produkten wurden der von CEN TC 351 entwickelte dynamische Oberflächenauslaugtest (DSLT) und Immersionstests nach EN 16105 durchgeführt. Emissionsverläufe wurden sowohl für an-organische Komponenten als auch für organische Substanzen in den Eluaten ermittelt. Auslaugbare organische Substanzen wurden zuvor in Screeningtests identifiziert. Um die mögliche Freisetzung von Stoffen aus Bauprodukten beurteilen zu können, ist es erforderlich, Emissionsverläufe zu beschreiben. Dazu sind die verwendeten Testverfahren geeignet. Um Baupro-dukte mit einem Blauen Engel als „Produkte mit geringer Auslaugung“ auszuloben, müssen die aus-laugbaren Substanzen komplett bekannt sein. Für organische Verbindungen ist das noch eine Heraus-forderung. Außerdem erfordert die Bewertung der Testergebnisse sowohl Übertragungsmodelle, die Vorhersagen über freisetzbare Stoffmengen unter Anwendungsbedingungen ermöglichen, als auch Vorgaben zu tolerierbaren Umweltkonzentrationen. Hier besteht noch Handlungsbedarf. N2 - Leaching tests were performed on different construction products that can be exposed to precipitation during service life. Varnishes for outdoor application, exterior thermal insulation systems, roof tiles and polymeric roof membranes were included in the test program. Leaching tests according to the dynamic surface leaching test (DSLT) as developed by CEN TC 351 and the immersion test according to EN 16105 were performed using these products. Emission curves were determined for inorganic as well as organic substances in the eluates. Leachable organic sub-stances in the eluates were identified by screening tests prior to the leaching tests. It is necessary to describe emission curves to be able to evaluate possible release of substances from construction products. The applied leaching tests are suitable to describe leaching processes. All leach-able substances need to be known in order to award the ecolabel ‘Blue Angel’. This is still challenging in case of organic substances. In addition, evaluation of the test results requires transfer models to predict leachable amounts under service conditions as well as requirements on concentrations that can be tolerated in environmental compartments. There is still need for action to solve these topics. KW - Bauprodukte KW - Auslaugtests KW - Blauer Engel KW - Construction Products KW - Leaching PY - 2018 SN - 1862-4359 VL - 67/2018 SP - 1 EP - 89 CY - Dessau-Rosslau AN - OPUS4-45799 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias T1 - Dry turning with niobium carbide based tools N2 - Niobium carbide (NbC) has attracted recently some attention as a substitute for tungsten carbide in machining. In the present work it was shown that the metallurgical and mechanical aspects favoring long tool lifes of NbC. T2 - POWDERMET 2018 CY - San Antonio, TX, USA DA - 17.06.2018 KW - Niobium carbide KW - NbC KW - Cutting tool KW - Machining PY - 2018 SN - 978-1-943694-18-1 VL - 2 SP - 538 EP - 545 AN - OPUS4-45802 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kiewitt, W. A1 - Bardl, Richard A1 - Kühnel, C. A1 - Loudon, D. A1 - Stengel, D. A1 - Wunkte, M. T1 - Comparative study of the long-term reliability of HTLS conductor systems N2 - In recent years, several high temperature low sag conductors (HTLS) have been developed and are now commercially available. Very few utilities have long-term experience with all the technologies. Moreover, most of the operational experience is at low temperatures. An independent testing program at maximum operational temperatures comparing most of the available technologies would provide useful guidance to utilities considering using such conductors. This paper describes the approach and results of an international research project assessing the long-term reliability of a wide range of commercially available high temperature conductor systems. Each system was exposed to 4,400 hours of simultaneous mechanical and electrical stresses. A set of standard mechanical and electrical tests were carried out to determine any changes. A conventional ACSR conductor was also tested and provided a validation that the testing program was realistic. The majority of the conductor systems performed satisfactorily. However the ACSS system joint resistance and the grease on the TACSR performed poorly. T2 - CIGRE Sesstion 2018 CY - Paris, France DA - 26.08.2018 KW - HTLS KW - Conductor KW - Freileitung PY - 2018 SP - B2-204,1 EP - 10 AN - OPUS4-46028 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wägner, Yannick A1 - Binkowski, Sigrid A1 - Woydt, Mathias T1 - Charakterisierung von Hartstoffphasen in Gefüge N2 - Der Beitrag handelt von der Verbesserung der Verschleißbeständigkeit von Hartstoffphasen in Metal Matrix Composites (MMC), Hartgusslegierungen, Hadfield-Stählen oder Werkzeugstählen. T2 - 15. International Metallographie-Tagung CY - Leoben, Asutria DA - 19.09.2018 KW - Verschleißbeständigkeit KW - Hartstoffphasen KW - NbC PY - 2018 SN - 978-3-88355-416-7 VL - 52 SP - 133 EP - 138 PB - DGM - INVENTUM GmbH CY - Sankt Augustin AN - OPUS4-46056 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wäsche, Rolf A1 - Ehrke, R. A1 - Kramer, R. A1 - Jayachandran, A. R. A1 - Brandt, G. T1 - Influence of temperature on tribological behaviour of DLC coatings under lubricated conditions up to 250°C N2 - In the present work it was shown that there is an influence of temperature and counter body material on the tribological properties of a-C:H coatings deposited on Cronidur 30 steel in a lubricated ball on disk contact situation. T2 - ASIATRIB 2018 CY - Kuching, Sarawak, Malaysia DA - 17.09.2018 KW - DLC KW - Temperature KW - Lubricated sliding PY - 2018 SP - 253 EP - 254 AN - OPUS4-46213 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zakel, S. A1 - Brandes, E. A1 - Schröder, Volkmar T1 - Safety characteristics of flammable gases and liquids – a review N2 - The safety characteristics of flammable gases and liquids are required when identifying potentially explosive mixtures and taking appropriate actions concerning explosion protection. Examples are given in this review of the safe handling and evaluation of hazards during the processing, storage, transport, and disposal of flammable liquids and gases. The CHEMSAFE database is presented as a reliable source of safety characteristic data, and ist new open-access version is introduced. CHEMSAFE currently contains assessed properties for about 3000 flammable liquids, gases and mixtures. The lack of a broad experimental foundation in the extensive field of non-atmospheric conditions shows the need for further investigation and standardization. This review summarizes experimental evidence and estimation methods for safety characteristic data under non-atmospheric conditions pointing out current limitations. Suggestions for pre-normative research on safety data under nonatmospheric conditions are given. T2 - 12th International Symposium on Hazards, Prevention and Mitigation of Industrial Explosions CY - Kansas City, USA DA - 12.08.2018 KW - Explosion protection KW - Safety characteristic KW - Classification KW - Flammable gas KW - Flammable liquid PY - 2018 SP - 1 EP - 15 AN - OPUS4-46295 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schönhals, Andreas A1 - Zorn, R. T1 - Quasi-elastic scattering of high free volume polymers by neutron time-of-flight spectroscopy N2 - Experimental report to proposal 13562 Quasi-elastic scattering of the polymer with intrinsic microporoasity PIM-1 is measured by neutron time-of-flight spectroscopy and discussed. KW - Neutron scattering KW - PIM-1 PY - 2018 SP - 1 EP - 2 CY - Garching AN - OPUS4-46693 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gaal, Mate A1 - Schadow, Florian A1 - Nielow, Dustin A1 - Trappe, Volker T1 - Air-coupled ultrasonic ferroelectret transducers with additional bias voltage for testing of composite structures N2 - Common air-coupled transducers for non-destructive testing consist of a piezocomposite material and several matching layers. Better acoustical matching to air is achieved by transducers based on charged cellular polypropylene (PP). This material has about hundred times lower acoustic impedance than any piezocomposite, having about the same piezoelectric coefficient. The piezoelectric properties of cellular PP are caused by the polarization of air cells. Alternatively, a ferroelectret receiver can be understood as a capacitive microphone with internal polarization creating permanent internal voltage. The sensitivity of the receiver can be increased by applying additional bias voltage. We present an ultrasonic receiver based on cellular PP including a high-voltage module providing bias voltage up to 2 kV. The application of bias voltage increased the signal by 12 to 15 dB with only 1 dB increase of the noise. This receiver was combined with a cellular PP transmitter in through transmission to inspect several test specimens consisting of glass-fiber-reinforced polymer face sheets and a porous closed-cell PVC core. These test specimens were inspected before and after load. Fatigue cracks in the porous PVC core and some fatigue damage in the face sheets were detected. These test specimens were originally developed to emulate a rotor blade segment of a wind power plant. Similar composite materials are used in lightweight aircrafts for the general aviation. The other inspected test specimen was a composite consisted of glass-fiber-reinforced polymer face sheets and a wooden core. The structure of the wooden core could be detected only with cellular PP transducers, while commercial air-coupled transducers lacked the necessary sensitivity. Measured on a 4-mm thick carbon-fiber-reinforced polymer plate, cellular PP transducers with additional bias voltage achieved a 32 dB higher signal-to-noise ratio than commercial air-coupled transducers. T2 - 10th International Symposium on NDT in Aerospace CY - Dresden, Germany DA - 26.10.2018 KW - Airborne ultrasonic testing KW - Air-coupled ultrasonic testing KW - Ferroelectret KW - Composites KW - Transducers PY - 2018 SP - 1 EP - 6 AN - OPUS4-46657 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Hothan, Sascha A1 - Mahler-de Silva, Tina A1 - Pistol, Klaus A1 - Häßler, Dustin T1 - Einfluss der Lagerungs- und Randbedingungen auf die Versagensmechanismen von Spannbeton-Hohlplatten im Brandfall N2 - Das Forschungsprojekt fokussiert sich auf die Untersuchung des Einflusses der Querdehnungs-behinderung auf das Trag- und Verformungsverhalten von Spannbeton-Hohlplatten (HC-Platten) im Brandfall. Das Vorhaben wird vom Deutschen Institut für Bautechnik (DIBt) finanziell gefördert und von der Bundesanstalt für Materialforschung und -prüfung (BAM) durchgeführt. Der Forschungs¬bericht beinhaltet eine Literaturrecherche, numerische Simulationsberechnungen, realmaßstäbliche Brandversuche an Deckenfeldern aus HC-Platten sowie Materialuntersuchungen für den verwendeten Beton. In numerischen Simulationen wurden sowohl einzelne HC-Platten als auch ganze Deckenfelder unter mechanischer Belastung und Brandbeanspruchung analysiert. Realmaßstäbliche Brandversuche mit Beanspruchung nach Einheits-Temperaturzeitkurve und auflagernaher Einleitung der mechanischen Prüflast (Querkraftbeanspruchung) wurden an insgesamt drei Deckenfeldern durchgeführt. Die Deckenfelder wurden aus 5 m langen HC-Platten zusammengesetzt. In zwei Brandversuchen wurden einachsig gespannte Deckenfelder untersucht. In dem einen Versuch waren die Längsränder frei, in dem anderen an der Querdehnung gehindert. In einem dritten Brandversuch wurde ein zweiachsig gespanntes Deckenfeld mit seitlicher Dehnungsbehinderung untersucht. Um das Verhalten der HC-Platten im Brandversuch quantitativ beschreiben zu können, wurde eine umfangreiche Sensorik zur Erfassung thermischer und mechanischer Kenngrößen eingesetzt. Die Brandversuche haben gezeigt, dass bei einer Zunahme des Grades der seitlichen Dehnungsbehinderung die Horizontalrissbildung in den Plattenstegen zu und die Längsrissbildung abnimmt. Die unterschiedlich starke thermisch bedingte horizontale Verformung der Plattenober- und -unterseite bewirkte am Übergang zur seitlichen Zwängungskonstruktion eine Schub-beanspruchung in Plattenquerrichtung. Die Schubspannung wurde durch Horizontalrissbildung in den Plattenstegen abgebaut. Trotz der ausgeprägten Rissbildung kam es in den Brandversuchen nicht zu einer Ablösung des unteren Plattenspiegels. Ebenso zeigte sich kein negativer Einfluss der Horizontalrisse auf das Trag- und Verformungsverhalten der brandbeanspruchten Decken-konstruktion. Die in den Brandversuchen erfassten thermischen und mechanischen Messwerte sowie die Ergebnisse aus Materialuntersuchungen stehen zukünftig als umfangreiche Datenbasis für die Validierung numerischer Modelle zur Verfügung. KW - Brandversuch KW - Beton KW - Spanbbetonhohlplatten KW - Zwängung PY - 2017 SP - 1 EP - 119 CY - Berlin AN - OPUS4-46703 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - El-Batahgy, A. A1 - Gook, S. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Effect of laser-beam and hybrid-laser-arc welding parameters and filler metal on microstructure and mechanical properties of thick heat-treated steel X8ni9+Qt640 for cryogenic service N2 - The present research work encloses results of experimental investigations of the interaction between welding process parameters for laser-beam and hybrid-laser-arc as well as type of the filler metal and the achievable mechanical properties of the weld joints on steel grade X8Ni9+QT640 for cryogenic service containing 9% nickel. The results obtained contribute to the development and conversion in the industrial practice a new laser beam-based welding technology for the automated manufacturing of facilities for the liquefaction, storage and the transport of natural gases (LNG facilities). The results show, that the martensitic microstructure of the laser weld metal including low amount of retained austenite not exceeding 3.5% leads to the relatively low V-notch impact energy. The remarkable heterogeneity in the chemical composition of the weld metal through the weld thickness could be recognized in the case of hybrid-laser-arc welding with ERNiCrMo-3 austenitic filler metal, what also led to insufficient impact toughness of the weld metall. The most promising results could be achieved by using 11%Ni filler wire, which is similar to the base metal and provides a homogeneous microstructure with uniform distribution of Ni through the weld seam. It is remarkable, that a correlation between Charpy impact toughness and wire feeding speed and respectively process heat input exists. The highest toughness values were 134±58 J at -196C. The both laser as well as laser-hybrid welds passed the tensile test. The failure stress of 720±3 MPa with a fracture location in the base material was achieved for all samples tested. T2 - 4th International Conference on Welding and Failure Analysis of Engineering Materials CY - Aswan, Egypt DA - 19.11.2018 KW - Hybrid-laser-arc welding KW - Laser-beam welding, KW - Cryogenic steel KW - Microstructure KW - Tensile strength PY - 2018 SP - W-29, 1 EP - 10 AN - OPUS4-46738 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Romero-Navarrete, José A. A1 - Otremba, Frank A1 - Lozano -Guzmán, A. A. T1 - Commidities and rail damage N2 - A roll-plane simplified model, representing the suspended body-cargo of a railway car, was developed to simulate thedynamic response of a railway car while subjectedto lateral acceleration derived from its traveling along curved tracks. The model provides the means to calculate the suspension forces, which are supposed to be transmitted to the bogie´s wheelset. For the analysis of the potential effect of such forces on the railway fatigue life, different performance measures were considered, under different concepts. A family of curves were produced to analyze the effect of the height of the center of gravity of the body-cargo system, on the different performance measures. The resultingdiagramswereused to assess the rail damage potentials offour different railway cars. Results suggest that the height of the center of gravity, associated to the different types of railway cars, nonlinearly and strongly affects the fatigue lifeof the rail, with the double stack car being the moreinfrastructure-aggressive. In this respect, experimental evidence should be provided about such remarkable effects, so as to supportsome operational recommendationsthat shouldbe taken to mitigate these effects, including, for example, the regulation of the traveling speed of some vehicles. T2 - IMECE 2018 International Mechanical Engineering Congress and Exposition CY - Pittsburgh, PA, USA DA - 09.11.2018 KW - Commidities KW - Rail KW - Damage PY - 2018 SP - 86008-1 EP - 86008-6 PB - ASME AN - OPUS4-46650 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Vogl, Jochen T1 - Roadmap for the purity determination of pure metallic elements – Basic rinciples and helpful advice N2 - High purity materials can serve as a realisation of the Système International d’Unitès (SI) unit amount of substance for the specific element. Solutions prepared from such high purity materials using gravimetric preparation and the concept of molar mass are used as calibration solutions in many fields of analytical chemistry. Calibration solutions prepared this way provide the traceability to the SI and are the metrological basis in elemental analysis. The preparation and characterization of such primary pure substances, representing the realisation of the SI unit amount of substance, is undertaken only by a small number of National Metrology Institutes (NMI) and Designated Institutes (DI). Many other NMIs and DIs, however, prepare elemental calibration solutions as calibrants for their measurement services, such as the certification of matrix Reference Materials or the provision of reference values for Proficiency Testing schemes. The elemental calibration solutions used for this purpose are not a direct service to customers, such as preparing secondary calibration solutions, but provide the source of traceability for the other services. Hence, it is necessary for the NMI or DI to obtain data on the purity of the pure metals or other materials used to prepare the solutions with measurement uncertainties meeting the needs of the above described services. This is commonly undertaken as a “fit for purpose” assessment, appropriate for the uncertainty requirement of the service provided to customers. As a consequence, total purity measurements are a long-term strategy of CCQM-IAWG. Several studies were conducted (CCQM-P107, CCQM-K72 and CCQM-P149) on the measurement of the purity of zinc. From these studies, several conclusions can be drawn for the purity assessment of a pure (metallic) element. These conclusions will be put together in this document in order to assist all NMIs/DIs in performing a purity assessment, whenever needed. KW - Purity assessment KW - Metal assay approach KW - Impurity assessment approach KW - Traceability PY - 2018 UR - https://www.bipm.org/wg/CCQM/IAWG/Allowed/April_2017/CCQM-IAWG17-28.pdf.pdf SP - 1 EP - 9 CY - Sevre AN - OPUS4-46834 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilsch, Gerd A1 - Gottlieb, Cassian A1 - Günther, Tobias A1 - Völker, Tobias ED - Ludwig, H.-M. T1 - Schnelle quantitative Untersuchung von Elementverteilungen in Beton mittels LIBS N2 - Die Laserinduzierte Plasmaspektroskopie (engl.: Laser-induced Breakdown Spectroscopy, kurz: LIBS) ist eine Kombination aus Laserablation mittels eines energiereichen Laser-Pulses, der Erzeugung eines Plasmas auf der zu untersuchenden Oberfläche und dem quantitativen Nachweis der Elementzusammensetzung durch spektroskopische Untersuchung der vom Plasma emittierten Strahlung. Ein LIBS-Gerät liefert dem sachkundigen Planer Daten für die Bewertung des Ist-Zustandes von Bauwerken unserer Infrastruktur durch die zweidimensionale Erfassung von Elementverteilungen. Typische Anwendungen sind die Erfassung von Chlor, Schwefel, Kohlenstoff, Natrium, Kalium und Lithium in Beton oder als – Qualitätssicherung – der Nachweis der mit einem Marker versehenen Tiefenhydrophobierung. In Zusammenarbeit zwischen Industriepartnern und der BAM wurden ein Labor und ein mobiles LIBS-System für die Vor-Ort-Messungen entwickelt. Die Analyse erfolgt vollautomatisch. Die Ortsauflösung beträgt bis zu 0,1 mm x 0,1 mm. Es können Messflächen von 140 mm x 170 mm gescannt werden. Die Erstellung von 2D-Elementverteilungen im Beispiel unten benötigt weniger als 10 Minuten. T2 - ibausil - 20. Internationale Baustofftagung CY - Weimar, Germany DA - 12.09.2018 KW - LIPS KW - LIBS KW - Beton KW - Chlorid PY - 2018 SN - 978-3-00-059950-7 VL - 2 SP - 2380 EP - 2387 PB - F.A. Finger-Institut für Baustoffkunde, CY - Weimar AN - OPUS4-46779 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Molkenthin, André A1 - Wilsch, Gerd A1 - Millar, Steven T1 - Sofortige Chloridbestimmung am Bauwerk mit LIBS N2 - Alle bislang angewendeten Verfahren zur Chloridbestimmung in Beton- und Stahlbetonbauwerken arbeiten über die Entnahme von Probenmaterial und dessen Analyse unter Laborbedingungen. Diese Methodik erfordert Zeit und generiert erhöhte Aufwendungen. Prüfverfahren, die direkt und zuverlässig solche Untersuchungen am Bauteil oder Bauwerk vornehmen können, standen bislang nicht zur Verfügung. Eine bereits in früheren Kolloquien vorgestellte Methode der Laser-induzierten Breakdown Spektroskopie wurde innerhalb eines aktuellen Forschungsvorhabens so weiter entwickelt, dass mit Hilfe eines neuartigen mobilen und kompakten Analysegerätes die Chloridwerte nun direkt und unmittelbar auf den Betonflächen bestimmt werden können. T2 - 8. Kolloquium Parkbauten CY - Ostfildern/Stuttgart, Germany DA - 23.01.2018 KW - Parkbauten KW - Chlorid KW - Mobiles LIBS PY - 2018 SP - 231 EP - 236 AN - OPUS4-46811 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thiel, Erik A1 - Kreutzbruck, M. A1 - Studemund, T. A1 - Ziegler, Mathias T1 - Thermal wave interference with high-power VCSEL arrays for locating vertically oriented subsurface defects N2 - Among the photothermal methods, full-field thermal imaging is used to characterize materials, to determine thicknesses of layers, or to find inhomogeneities such as voids or cracks. The use of classical light sources such as flash lamps (impulse heating) or halogen lamps (modulated heating) led to a variety of nondestructive testing methods, in particular, lock-in and flash-thermography. In vertical-cavity surface-emitting lasers (VCSELs), laser light is emitted perpendicularly to the surface with a symmetrical beam profile. Due to the vertical structure, they can be arranged in large arrays of many thousands of individual lasers, which allows power scaling into the kilowatt range. Recently, a high-power yet very compact version of such a VCSEL-array became available that offers both the fast timing behavior of a laser as well as the large illumination area of a lamp. Moreover, it allows a spatial and temporal control of the heating because individual parts of the array can be controlled arbitrarily in frequency, amplitude, and phase. In conjunction with a fast infrared camera, such structured heating opens up a field of novel thermal imaging and testing methods. As a first demonstration of this approach, we chose a testing problem very challenging to conventional thermal infrared testing: The detection of very thin subsurface defects perpendicularly oriented to the surface of metallic samples. First, we generate destructively interfering thermal wave fields, which are then affected by the presence of defects within their reach. It turned out that this technique allows highly sensitive detection of subsurface defects down to depths in excess of the usual thermographic rule of thumb, with no need for a reference or surface preparation. T2 - 44TH ANNUAL REVIEW OF PROGRESS IN QUANTITATIVE NONDESTRUCTIVE EVALUATION CY - Provo, Utah DA - 16.07.2017 KW - Laser applications KW - Thermography KW - VCSEL KW - Subsurface defects PY - 2018 SN - 978-0-7354-1644-4 DO - https://doi.org/10.1063/1.5031547 SN - 0094-243X VL - 1949 SP - UNSP 060001, 1 EP - 8 AN - OPUS4-45171 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wasmer, Paul A1 - Krome, Fabian A1 - Bulling, Jannis A1 - Prager, Jens T1 - Entwicklung eines Ultraschallsensors zur Flüssigkeitsanalyse in Rohrleitungen N2 - Zur Messung von Konzentrationen in Flüssigkeiten können akustische Sensoren genutzt werden. Ziel der vorliegend Arbeit ist es einen Sensor zu entwerfen der sehr hohe Messgenauigkeiten erzielen kann. Der Sensor besteht aus einem rechteckigen Rohr, welches auf einem Halbraum angebracht ist. Die Konzentrationsbestimmung erfolgt anhand des Resonanzverhaltens der Struktur, wodurch eine hohe Messgenauigkeit erreicht werden kann. Um den Sensors zu verwirklichen, muss eine Optimierung der Geometrie mit vielen Iterationsschritten durchlaufen werden. Da keine analytische Beschreibung des akustischen Verhaltens vorliegt, wird eine effiziente Simulationsmethode benötigt. Die Scaled Boundary Finite Element Method (SBFEM) für prismatische Strukturen erscheint für die Simulation geeignet, da Teile der Geometrie ohne neue Vernetzung geändert werden können. Für die Berechnung des Sensors wird ein Modell der akustischen Fluid-Struktur Interaktion benötigt, das bisher nicht vorhanden ist. Die Präsentation behandelt die Implementierung des Fluidmodells in die SBFEM und deren Validierung. Für die Validierung werden die Ergebnisse mit analytischen Beispielen ohne Fluid-Struktur Kopplung und mit Comsol-Ergebnissen der Dispersionskurven mit Wasser gefüllter Rohre verglichen. Schließlich wird das neuartige Verfahren für die Modellierung der Sensorgeometrie angewendet. An einer einfachen Geometrie wird das Sensorprinzip zur Bestimmung der Salzkonzentration demonstriert. T2 - DAGA 2018 - 44. Jahrestagung für Akustik CY - Munich, Germany DA - 19.03.2018 KW - Scaled Boundary Finite Element Method KW - Penalty Parameter KW - Sensorentwicklung PY - 2018 SN - 978-3-939296-13-3 VL - 2018 SP - 1023 EP - 1026 AN - OPUS4-45262 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Babutzka, Martin A1 - Burkert, Andreas A1 - Heyn, A. T1 - Corrosion investigations on zinc coatings by using gel-type electrolytes N2 - A new approach to the assessment of the corrosion behaviour of zinc coatings under atmospheric conditions can be achieved using gel-type electrolytes as an alternative to standard aqueous test electrolytes. Gel-type electrolytes allow minimally invasive corrosion investigations on zinc coatings. They also provide the possibility to carry out corrosion investigations onsite. By using gel-type electrolytes corrosion-relevant characteristic values such as corrosion currents and polarization resistances can be determined. These allow to describe the formation and the stability of the formed corrosion product layers under various climatic conditions. With this knowledge, a prediction of the zinc coating life cycle is possible. In this contribution, the value of gel-type electrolytes for corrosion research on zinc coatings is presented. T2 - Intergalva 2018 CY - Berlin, Germany DA - 17.06.2018 KW - Deckschichtbildung KW - Layer formation KW - Gelartige Elektrolyte KW - Gel-type electrolytes KW - Korrosionsprüfung KW - Corrosion testing KW - Zinkdeckschichten KW - Zinc coatings PY - 2018 SP - 385 EP - 392 AN - OPUS4-45245 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Lars A1 - Schönfelder, Thorsten A1 - Komann, Steffen A1 - Ballheimer, Viktor A1 - Wille, Frank ED - Müller, Lars T1 - Assessment experience on packages loaded with damaged spent nuclear fuel for transport after storage N2 - In 2017 the first German package approval certificate was issued for a dual purpose cask (DPC) design with encapsulated damaged spent nuclear fuel. At the Bundesanstalt für Materialforschung und -prüfung (BAM) a comprehensive assessment procedure was carried out with respect to the mechanical and thermal design, the containment design and quality assurance for manufacturing and operation. Main objective of this procedure was to verify the Package Design Safety Report (PDSR) fulfils the requirements according to the IAEA regulations SSR-6. Until now only standard spent nuclear fuel assemblies were designated for interim storage and transports. Due to nuclear phase out in Germany all other kinds of SNF in particular damaged fuel has to be packed. Therefore specific requirements have to be considered in accordance with international experiences written in IAEA technical reports. In Germany damaged spent nuclear fuel (DSNF) needs a tight encapsulation with special encapsulations and clearly defined properties. Due to the limited amount of DSNF these encapsulations are designed for storage and transport in existing packages. From the assessment experience it has been seen, corresponding PDSR need an extensively expansion to cover the design of these encapsulations and their influences on the package. Then such well-defined encapsulations can be handled like standard fuel assemblies. The main difference to standard package components is, encapsulations with permanent closure achieve their specified condition not after manufacturing but only during operation after loading and closing. Thus specific handling instruction and test procedures are necessary especially for welding, where BAM is able to survey the quality of this first part of operation. T2 - 11th International Conference on the Transport, Storage and Disposal of Radioactive Materials CY - London, UK DA - 15.05.2018 KW - Assessment KW - Dual purpose cask KW - Spent nuclear fuel PY - 2018 SP - Paper 18524, 1 EP - 8 AN - OPUS4-45258 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lugovtsova, Yevgeniya A1 - Prager, Jens T1 - Analysis of Guided Wave Propagation in an Aluminium-CFRP Plate N2 - Guided waves cover comparably long distances and thus allow for online structural health monitoring of safety relevant components, e.g. lightweight composite overwrapped pressure vessels (COPV) as used for the transportation of pressurised gases. Reliable non-destructive assessment of COPVs’ condition is not available yet due to their complex composite structure comprising a thin metal liner and a fibre reinforced plastics (FRP) overwrap. The conventional overload hydrostatic pressure testing used for the metal vessels is not suitable for the composite vessels, because it may damage the FRP overwrap reducing the service life of the COPV. Therefore, ISO and CEN defined a maximum service life of composite pressure vessels as of 15 to 20 years. To extend the COPVs’ service life and to ensure a safer usage a structural health monitoring system based on guided ultrasonic waves is to be developed. In this contribution first results of guided waves propagation in a flat composite plate consisting of an aluminium layer firmly bonded to a carbon fibre reinforced plastic laminate are presented. Based on experimental results material properties of FRP are reconstructed by means of the Scaled Boundary Finite Element Method (SBFEM). T2 - ECNDT 2018 CY - Gothenburg, Sweden DA - 11.06.2018 KW - Structural Health Monitoring KW - Pressure tanks KW - Hydrogen storage KW - Natural gas KW - Composites PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-452084 SP - 1 EP - 6 AN - OPUS4-45208 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gaal, Mate A1 - Kotschate, Daniel T1 - New technologies for air-coupled ultrasonic transducers N2 - Air-coupled ultrasonic testing (ACUT) has experienced rapid growth within the last years. It is especially well suited to inspection of lightweight structures consisting of composite materials and adhesive joints. Uniform coupling and easy maintenance are its advantages compared to contact technique. However, the impedance mismatch between the transducer and air poses a major challenge to the development of ACUT transducers. Commercially available air-coupled transducers consist of a piezocomposite material and matching layers. Their fabrication is difficult in handling and their signal-to-noise ratio sometimes not sufficient for various testing requirements. However, there are several innovative approaches using other materials and other physical principles to transmit and receive an ultrasonic pulse. We present a review of the latest advances in research on air-coupled transducers for non-destructive testing, including previously unpublished results. We recognize two major directions as most promising: ferroelectrets and thermoacoustic transducers. Ferroelectrets are charged cellular polymers exhibiting piezoelectric properties. Their small acoustic impedance is matched to air better than matching layers applied in conventional air-coupled transducers. Applying bias voltage to a ferroelectret receiver is the latest development in this field, which increased the received signal by 12 to 15 dB. Thermoacoustic transducers use heat to initiate an ultrasonic wave, acting as transmitters. The working principle is known from nature as thunder and lightning: thermal energy of an electrically heated material, which can also be air, is converted into acoustic energy. Some thermoacoustic transmitters consist of a conductive layer with a thickness in the nanometer range deposited on a solid substrate. Another possibility is to use an electric spark. For the first time, measurements of the sound field of an electric spark up to 500 kHz were performed. Thermoacoustic transducers enable excitation of extremely broadband pulses while producing high pressure levels, which opens new possibilities for advanced signal processing. T2 - 12th European conference on Non-Destructive Testing CY - Gothenburg, Sweden DA - 11.06.2018 KW - Air-coupled ultrasonic testing KW - Atmospheric pressure plasma KW - Cellular polypropylene KW - Ferroelectret KW - Transducer PY - 2018 SP - ECNDT-0608-2018, 1 EP - 9 AN - OPUS4-45209 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grager, J.-C. A1 - Kotschate, Daniel A1 - Gamper, J. A1 - Gaal, Mate A1 - Pinkert, K. A1 - Mooshofer, H. A1 - Goldammer, M. A1 - Grosse, C. U. T1 - Advances in air-coupled ultrasonic testing combining an optical microphone with novel transmitter concepts N2 - Air-coupled ultrasound (ACU) is increasingly used for automated and contactless inspection of large-scale composite structures as well as for non-destructive testing (NDT) of water-sensitive or porous materials. The major challenge to overcome using ACU in NDT is the enormous loss of ultrasonic energy at each solid-air interface caused by the high acoustic impedance mismatch. Resonant low-frequency piezoceramic transducers are specially designed to achieve high sound pressure levels. For an expanded use of this technique, however, the spatial resolution needs to be increased. Recent studies of our collaborative research group demonstrated the successful application of a resonance-free, highly sensitive receiver that uses a Fabry-Pérot etalon instead of piezoceramic materials or membranes. However, to reach the full potential of this broadband small-aperture optical microphone, novel transmitter concepts have to be developed and evaluated for advanced NDT applications. Different types of transmitter were tested in combination with the optical microphone acting as receiver and they were compared to conventional piezoceramic transducers in through-transmission mode. Monolithic carbon fiber-reinforced plastics (CFRP) and CFRP sandwich structures containing different defect types were inspected. Presented results are processed as C-scan images and further evaluated for spatial resolution, signal-to-noise ratio and sensitivity of each measurement setup. Novel transmitter concepts, such as ferroelectret and thermoacoustic emitters, show promising findings with a considerably improved time and spatial resolution for ACU-NDT. T2 - 12th European conference on Non-Destructive Testing CY - Gothenburg, Sweden DA - 11.06.2018 KW - Air-coupled ultrasonic testing KW - Optical microphone KW - Thermoacoustic KW - Cellular polypropylene KW - Ferroelectret KW - Transducer PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-452114 SP - ECNDT-0166-2018, 1 EP - 10 AN - OPUS4-45211 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Seneschal-Merz, Karine A1 - Bücker, Michael T1 - Entwicklung von transparenten farbigen keramischen Schmelzfarben für den Einsatz auf digitalen Druckmaschinen N2 - Ziel des Projektes war es, schwermetallfreie Schmelzfarben für den Einsatz auf einem Digitaldrucker zu entwickeln. Dafür sollten die Glasfarben, bei Temperaturen unter 630°C verarbeitbar und deren Eigenschaften kompatibel mit denen von Floatgläsern sein. Zudem sollte die aufgeschmolzene Farbe transparent und im Außenbereich eingesetzt beständig sein. Weiterhin mussten die Farben eine Partikelkorngröße kleiner als 20µm besitzen, um die Druckköpfe des Digitaldruckers nicht zu verstopfen. Gute Dispergierbarkeit, thixotropes Verhalten und eine schnelle Trocknung waren weitere Voraussetzungen. Die Ersetzung von PbO durch ZnO und Bi2O3 wurde getestet und zeigte positive Ergebnisse. Ein geeigneter Mahl-und Dispergierprozess wurde entwickelt. Bei der Firma „glas&räume“ wurden die Musterfarben getestet und zeigten ein gutes Druckverhalten. Bedingt durch das Tintenstrahlverfahren erreicht der Farbauftrag keine 100%ige Transparenz. Trotzdem erscheint die transparente keramische Schmelzfarbe im Vergleich zur Verwendung von opaker Schmelzfarbe tatsächlich völlig transparent. Der Unterschied ist signifikant und öffnet so ein neues Kapitel im keramischen Digitaldruck. KW - Glass KW - Low melting KW - Chemical durability KW - Dispersion of glass particle KW - Printing KW - Architecture KW - Weathering KW - Architektur KW - Chemische Beständigkeit KW - Dispergierung von Glaspartikeln KW - Glas KW - Niedrig schmelzend KW - Druck KW - Bewitterung PY - 2018 SP - 1 EP - 61 AN - OPUS4-44650 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yalçin, M. A1 - Taşçioğlu, C. A1 - Plarre, Rüdiger A1 - Akçay, Ç. A1 - Busweiler, Sabine T1 - Investigation of natural durability of some native and exotic wood species against Hylotrupes bajulus (Cerambycidae) and Anobium punctatum (Anobiidae) N2 - Aim of study: In this study, natural durability of some domestic and foreign wood species against Hylotrupes bajulus and Anobium punctatum larvae were tested on laboratory scale Area of study: This study was conducted at Department of Forest Products Engineering in Duzce University, Turkey and Federal Institute for Materials Research and Testing (BAM), Germany. Material and Methods: Scotch pine (Pinus sylvestris), fir (Abies nordmanniana), spruce (Picea orientalis), cedar (Cedrus libani), poplar (Populus tremula) and beech (Fagus orientalis) woods were used to test H. bajulus larvae (EN 46-1). Alder (Alnus glutinosa), oak (Quercus cerris), poplar (Populus tremula), beech (Fagus orientalis), maple (Acer carpinifolium), ash (Fraxinus angustifolia), teak (Tectona grandis), ayous (Triplochiton scleroxylon), movingui (Distemonanthus benthamianus), dahoma (Piptadeniastrum africanum), iroko (Chlorophora excelsa), bubinga (Guibourtia tessmannii) and sapele (Entandrophragma cylindiricum) woods were used for A. punctatum larvae (EN 49-1). At the end of the experiment, the mortality rates of the larvae were determined and the size and weights of the surviving larvae were measured. Main results: F. orientalis and C. libani were found to be the most resistant wood species against H. bajulus larvae while A. nordmanniana was the least resistant. All tropical wood species and oak and maple from domestic wood species showed 100% mortality rate therefore found to be the most resistant against A. punctatum larvae. The most vulnerable wood species was found to be alder with a 35% mortality. Research highlights: while F. orientalis, C. libani, and P. tremula were found the most resistance wood species against H. bajulus, P. sylvestris and A. nordmanniana were determined as most vulnerable. All tropical wood species and two domestic species (Q. cerris and A. carpinifolium) showed the highest mortality rate as 100%. The least durable domestic wood was determined as alder. KW - Hylotrupes bajulus, Anobium punctatum, natural durability, tropical wood, native wood. PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-446572 DO - https://doi.org/10.17475/kastorman.311971 SN - 1303-2399 SN - 1309-4181 VL - 18 IS - 1 SP - 83 EP - 91 PB - Kastamonu University CY - Kastamonu AN - OPUS4-44657 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Vlassopoulos, E. A1 - Caruso, S. A1 - Linnemann, Konrad A1 - Nasyrow, R. A1 - Gretter, R. A1 - Fongaro, L. A1 - Papaioannou, D. T1 - Mechanical integrity of spent nuclear fuel rods N2 - The properties of spent nuclear fuel (SNF) rods change significantly during their operation life in the reactor core. Further changes occur after their discharge mainly due to the heating-cooling processes and possible ageing associated with the cumulative effects of radioactive decay induce damage in the fuel. Such changes may affect the response of the SNF rods to mechanical solicitations corresponding to normal and accidental conditions. Research activities at JRC-KARLSRUHE aim at assessing the integrity of SNF rods and processes which might affect their mechanical properties during their interim storage, transport or other handling operations. JRC Hot Cell facilities have been fully adapted to fulfil the experimental goals. The number of experiments that can be performed, however, is limited and there is an acute need to model them, using this process to validate codes, to deeper understand and to extend the results gained at the JRC beyond the conditions that have been tested. For the experimental campaigns two devices for gravitational impact and 3-point bending tests were developed and installed in a hot cell. Segments of real SNF rods pressurized at their original pressures after discharge have been investigated. The setup is fully operational and new results are reported continuously. T2 - ANS Annual 2018 CY - Philadelphia, PA, USA DA - 17.06.2018 KW - Spent nuclear fuel KW - Mechanical testing KW - Hot cell testing PY - 2018 SP - 170 EP - 172 AN - OPUS4-44862 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Musolff, Andre A1 - Quercetti, Thomas A1 - Müller, Karsten A1 - Bartholmai, Matthias T1 - Kinematic aspects of RAM packages drop tests N2 - BAM is the German Federal Institute for Materials Research and Testing and the competent authority for mechanical and thermal safety assessment of transport packages for spent fuel and high level waste. In context with safety assessment of RAM packages BAM performed numerous drop tests in the last decades. The tests were mostly accompanied by extensive and various measurement techniques especially by instrumented measurements with strain gages and accelerometers. The procedure of drop testing and the resulting measurement analysis are the main methods to evaluate the safety against mechanical test conditions. Measurement techniques are dedicated to answer questions in regard to the structural integrity of a RAM package, the mechanical behavior of the prototype as well as of its content under impact conditions. Test results like deceleration-time functions constitute a main basis for the validation of assumptions in the safety analysis and for the evaluation of numerical calculations. In this context the adequate selection of accelerometers and measurement systems for the performance of drop tests is important. Therefore it is not only necessary to find suitable positions for the accelerometers at the test specimens, but also to consider technical boundary conditions as e.g. temperature. T2 - 2018 WM Symposia CY - Phoenix, AZ, USA DA - 18.03.2018 KW - Drop KW - Test KW - Measurement KW - Analysis KW - Prototyp PY - 2018 SP - Paper 18149, 1 EP - 12 AN - OPUS4-44872 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Franz, Philipp A1 - Metz, Christain A1 - Brackrock, Daniel A1 - Fischer, C. A1 - Wachtendorf, Volker A1 - Maierhofer, Christiane T1 - Zerstörungsfreie Charakterisierung und Qualitätssicherung der Materialeigenschaften und Beständigkeit additiv gefertigter Kunststoffteile N2 - Mit additiven Fertigungsverfahren hergestellte Bauteile und Produkte aus Kunststoffen werden zunehmend nicht mehr nur als Prototypen, sondern als voll funktionsfähige Bauteile und Produkte gefertigt. Bedingt durch die Fertigungsprozesse und den schichtweisen Aufbau resultieren physikalische Materialeigenschaften, die stark von den Fertigungsparametern abhängen und zudem anisotrop sind. Von den Fertigungsparametern werden auch die Oberflächeneigenschaften beeinflusst, sodass zu erwarten ist, dass sich die Beständigkeit gegenüber äußeren Umwelteinflüssen bei additiv gefertigten Bauteilen von der konventionell gefertigter unterscheiden kann. Nachfolgend wird daher die Entwicklung eines Qualitätssicherungskonzeptes basierend auf spektroskopischen und zerstörungsfreien Prüfverfahren vorgestellt, in dem der Alterungsprozess von mittels Fused Deposition Modelling (FDM) und mittels Lasersintering (LS) hergestellten Probekörpern untersucht wird. T2 - DGZfP-Jahrestagung 2018 CY - Leipzig, Germany DA - 07.05.2018 KW - Additive Fertigung KW - Kunststoffe KW - Zerstörungsfreie Prüfung PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-449016 SN - 978-3-940283-92-4 VL - DGZfP BB 166 SP - Mo.2.A.1, 1 EP - 9 AN - OPUS4-44901 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krankenhagen, Rainer A1 - Maierhofer, Christiane A1 - Röllig, Mathias A1 - Heckel, Thomas A1 - Brackrock, Daniel A1 - Gaal, Mate T1 - Charakterisierung von Impactschäden während und nach der Belastung mit thermografischen Verfahren und mit Ultraschall N2 - Der Umfang der durch Impacts in Faserverbundmaterialien erzeugten Schäden ist abhängig von der Energie des Impacts, von der Zusammensetzung und dem Aufbau der Faserverbundwerkstoffe und von der Geometrie der Bauteile und hier im Wesentlichen von der Dicke des Bauteils. Der zerstörungsfreie Nachweis dieser Schädigungen kann sowohl mit Ultraschallverfahren als auch mit Verfahren der aktiven Thermografie erfolgen. Ein Vergleich der Nachweisempfindlichkeiten dieser Verfahren für die unterschiedlichen Schädigungen wird in diesem Beitrag in Abhängigkeit vom verwendeten Faserverbundwerkstoff (CFK und GFK), der Dicke des Materials und von der Impactenergie durchgeführt. Ergänzt werden die im Anschluss an die Schädigung eingesetzten ZfP-Verfahren mit zeitlich hochaufgelösten Thermografiemessungen, die bereits während des Impacts aufgenommen wurden. T2 - DGZfP Jahrestagung 2018 CY - Leipzig, Germany DA - 07.05.2018 KW - Thermografie KW - Ultraschall KW - Faserverbundwerkstoffe KW - Impactschäden PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-448773 SN - 978-3-940283-92-4 VL - 166 SP - 1 EP - 8 PB - Deutsche Gesellschaft für zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-44877 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Illerhaus, Bernhard A1 - Kunisch, E. A1 - Kinne, R. W. T1 - μCT begleitete in-situ Druckversuche an spongiösem Knochen - Vergleich(ende Bestimmung) des experimentellen und simulierten Verschiebungsfeldes mit der simulierten internen Spannung N2 - Untersuchungen haben gezeigt, dass sich ältere Schafe gut als Modell für die mi-nimalinvasive Behandlung von Osteoporose eignen [1]. Um einen Behandlungs-effekt nachzuweisen, wird dabei unter anderem die Belastungsfähigkeit des Kno-chens durch Druckversuche an kleinen Zylindern aus den behandelten und unbe-handelten Knochen bestimmt. Diese hatten hier einen Durchmesser von 10 mm und eine Höhe von 13 mm. Für den in-situ Druckversuch wurde eine Deben CT5000 verwendet. In einer Serie von Druckerhöhungen wurden die Proben je-weils tomographiert. Dabei ergab sich zunächst, dass mit der µCT innerhalb der Knochen im oberen und unteren Bereich schon Brüche nachgewiesen werden können, obwohl die gemessene Kraftaufnahmekurve keine Unstetigkeit zeigt. Deswegen wurden die starren Probenaufnehmer der Deben Anordnung durch bewegliche Aufnehmer ergänzt, die eine leichte Verkippung der belasteten Ober-flächen ausgleichen können. Ein Vergleich der gemessenen und der aus den µCT-Daten berechneten Verschiebungsfelder ergab trotz der komplexen Struktur der Knochen gute Übereinstimmungen. Diese Verschiebungen wurden dann mit den aus den µCT Daten simulierten mechanischen Druckversuchen, Von-Mise-Spannungen und daraus berechneten Verschiebungen verglichen. (VGStudioMax Simulation). T2 - DGZfP-Jahrestagung CY - Leipzig, Germany DA - 07.05.2018 KW - Computer Tomographie KW - In-situ Druckversuch KW - Simulation PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-448827 UR - https://www.ndt.net/?id=23080 SN - 978-3-940283-92-4 VL - DGZfP BB 166 SP - 1 EP - 7 PB - DGZfP CY - Berlin AN - OPUS4-44882 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Linnemann, Konrad A1 - Nehrig, Marko A1 - Musolff, André A1 - Wille, Frank T1 - Experience by BAM in the transport package safety assessment of German waste containers N2 - Transport and storage containers for low and midlevel radioactive waste are getting more and more of relevance due to the nuclear phase out decision in 2011. For higher activities Type B(U) approved waste containers will be needed for the shut down and dismantling phases of NPPs. It is expected that large quantities are required in the near future. German waste containers are generally approved for transport and interim storage and are also intended for the final disposal in the Konrad repository. BAM is involved in the authority licensing of transport package designs in Germany. In this context, BAM is responsible for the assessment of safe containment, mechanical, thermal and quality management issues. BAM also operates test facilities and performs drop as well as thermal tests during package licensing procedures. This paper summarizes our experience in the transport package design assessment of Type B(U) waste containers. A general overview of the approval process, the requirements and approaches BAM applies are described. Some examples are used to illustrate different aspects and technical issues we are addressing during the package assessment. In the first part of the paper the specific design aspects of German waste containers are described. Here, a general overview is given e.g. about closure systems, impact limiter designs, and the handling concepts. Furthermore, the wide range of radioactive content and their physical behavior including the impact on the packages assessment are described. The second part is focused on questions about the licensing and assessment process of German waste containers from the BAM authority point of view. The general approaches for the strategy of demonstration are outlined on the basis of the test conditions according to IAEA Regulations SSR-6. Furthermore, particular issues of the mechanical and thermal assessment with respect to the specific test conditions are discussed. For accident conditions of transport, aspects to be mentioned are e.g. the assessment of the lid bolts, the axial gap applied between content and lid, and the thermal behavior of the wood filled impact limiter after the fire test. However, issues of the assessment for routine and normal conditions of transport are addressed in this paper, too. The intention of this paper is introduce recent approval procedure experience in Germany, describing technical evaluation issues and so reduce rounds of questions during applications. T2 - 2018 WM Symposia CY - Phoenix, AZ, USA DA - 18.03.2018 KW - Transport packages KW - Safety assessment KW - Lowlevel and midlevel radioactive waste PY - 2018 SP - Paper 18469, 1 EP - 10 AN - OPUS4-44861 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kraus, David A1 - Trappe, Volker T1 - Cyclic fatigue behavior of glass fiber reinforced epoxy resin at ambient and elevated temperatures N2 - The fatigue behavior of ±45° glass fiber reinforced epoxy resin under cyclic mechanical and constant thermal loading is investigated in this study. Tests at three different temperature levels in the range 296 K to 343 K have been performed in order to create S-N curves for each temperature level. The specimen damage is measured in-situ using optical grayscale analysis. The characteristic damage state (CDS) is evaluated for each specimen. It is shown that the point of CDS is suitable as a failure criterion to compare the resulting S-N curves. With micromechanical formulations, the temperature-dependent matrix effort is calculated for each stress-temperature level. In terms of matrix effort, the longest fatigue life is reached at high temperatures, while, in terms of stress, the lowest fatigue life is reached at the highest temperatures. T2 - ECCM18 - 18th European conference on composite materials CY - Athens, Greece DA - 24.06.2018 KW - Composite KW - Fatigue KW - Thermomechanics KW - Residual stresses KW - Temperature PY - 2018 SP - 1 EP - 7 PB - European society for composite materials AN - OPUS4-45338 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Metz, Christian A1 - Franz, Philipp A1 - Fischer, C. A1 - Wachtendorf, Volker A1 - Maierhofer, Christiane T1 - Active thermography for quality assurance of 3D-printed polymer structures N2 - Additively manufactured test specimens made of polyamide 12 (PA 12) by Laser Sintering (LS) as well as of acrylnitril-butadien-styrol (ABS) by Fused Layer Modeling (FLM), were tested with active thermography. For this, two different excitation methods (flash and impulse excitation) were used and compared, regarding the suitability for the detection of constructed and imprinted defects. To increase the quality of the thermograms, data processing methods like thermal signal reconstruction (TSR) and Fourier-Transformation were applied. Furthermore, the long-term stability of the probes towards environmental stress, like UV-radiation, heat, water contact and frost is being investigated in the presented project with artificial weathering tests. T2 - 14th Quantitative InfraRed Thermography Conference CY - Berlin, Germany DA - 25.06.2018 KW - Additive manufacturing KW - Active thermography KW - Artificial weathering PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-453919 SP - Tu.3.A.2, 1 EP - 9 AN - OPUS4-45391 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Illerhaus, Bernhard A1 - Kunisch, E. A1 - Kinne, R. W. T1 - Serial in situ compression of spongiosa cylinder observed by μCT, compared to simulated stress, strain, and movement N2 - Minimally invasive injection of calcium phosphate cement into bone defects in aged sheep vertebrae has been used as a model for the treatment of osteoporotic vertebral fractures. One of the therapeutic criteria is a compression test of non-treated or treated vertebral bodies. In the present study, an in situ compression test with a stepwise load increase was performed with small spongiosa cylinders from the vertebrae under continuous monitoring by μCT. This allows localization of bone cracks and the visualization of correct placement and form of the bone cylinder. In addition, the effects of an uneven load distribution on the sample due to an irregular shape and a subsequent underperformance of the test sample can be excluded by controlling its shape under increasing load. There was a good agreement between the measured data and those obtained by simulated load-dependent transformation on the basis of a digital volume correlation between consecutive compression tests on the bone surface under the assumption of homogeneous bone material. Mechanic simulation was executed by directly using structural voxel data, resulting in maps of Von Mise stresses and predicted displacements. T2 - 12th ECNDT CY - Gothenburg, Sweden DA - 11.6.2018 KW - Computed tomography KW - In-situ compression KW - Simulation PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-453317 SN - 978-91-639-6217-2 SP - 0162, 1 EP - 7 AN - OPUS4-45331 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Linnemann, Konrad A1 - Ballheimer, Viktor A1 - Sterthaus, Jens A1 - Rolle, Annette A1 - Wille, Frank A1 - Nasyrow, R. A1 - Papaioannou, D. A1 - Rondinella, V. A1 - Vlassopoulos, E. A1 - Pautz, A. T1 - Finite element modeling of spent fuel rod segments under bending loads N2 - Transport packages for spent nuclear fuel have to be assessed with respect to specific transport conditions which are defined in the regulations of the International Atomic Energy Agency. The physical state of the spent fuel and the fuel rod cladding as well as the geometric configuration of the fuel assemblies are important Inputs for the evaluation of the package capabilities under These conditions. Cracks or failures in the fuel rod cladding can cause the release of gas, volatiles or fuel particles into the cavity. The amount of substances in the cavity has to be considered in the assessment of the activity release and criticality safety. The mechanical analysis of the compound system formed by the fuel rod cladding and the spent fuel pellets is very difficult due to the limited knowledge of the material properties and the insufficient understanding of the interaction between pellets and cladding and between adjacent pellets. The variation of fuel assembly properties regarding cladding material, burn-up and the history of usage makes reliable predictions of the fuel rod behavior even harder. For a better understanding about the behavior of spent fuel rods, JRC and BAM have started a joint research project. In this context, JRC has developed a test device which allows quasi-static 3-point-bending test on fuel rod segments in the hot cell. The loads are applied with respect to the boundary conditions of the activity release assessment. This paper deals with the numerical calculation of a single fuel rod segment under bending load. The aim is to identify the governing mechanical parameters by the variation of constitutive assumptions, contact conditions, inner constraints, etc. This knowledge helps for the interpretation of the experimental results. Furthermore, the improved understanding about the behavior of the cladding-pellets system will be beneficial for the assessment of spent fuel transport conditions. T2 - SMIRT24 - 24th Conference on Structural Mechanics in Reactor Technology CY - Busan, Korea DA - 20.08.2017 KW - Finite element methods KW - Spent fuel assessment KW - Transport packages PY - 2017 SP - 1 EP - 8 AN - OPUS4-45316 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gaal, Mate A1 - Schadow, Florian A1 - Nielow, Dustin A1 - Trappe, Volker T1 - Prüfung von Rotorblattschalen mit Luftultraschall N2 - Um den sicheren Betrieb von Windkraftanlagen zu gewährleisten, werden Rotorblätter nach der Fertigung und nach Reparatur mit verschiedenen zerstörungsfreien Verfahren auf Schaden untersucht. Bei der Fertigung von Blattschalen, die in einer Sandwich-Schalenbauweise gefertigt werden, entstehen Imperfektionen, die unter Belastung zu großen Rissen führen können. Zur Prüfung von Blattschalen wird unter anderem Ultraschallprüfung in Kontakttechnik eingesetzt. Um den Wartungsaufwand von Ultraschallanlagen zu reduzieren und um manche Kompositstrukturen vor Koppelmittel zu schützen, wird die Anwendung von Luftultraschall erforscht. Insbesondere große Fortschritte gibt es im Bereich der Entwicklung neuer Wandler. In diesem Beitrag berichten wir über die Luftultraschallprüfung von Schalen für Rotorblätter. Es wurden typische Sandwichschalenstrukturen hergestellt und mit einem eigenentwickelten Schalenprüfstand unter simulierter Betriebsbeanspruchung belastet. Die in den Schalenprüfkörpern entstandenen Schäden wurden außerhalb des Prüfstandes mit Luftultraschall in Durchschallung untersucht. Es wurden fokussierende Wandler auf Basis von Ferroelektreten entwickelt und für diese Prüfungen eingesetzt. Mit zusätzlicher elektrischer Vorspannung konnte die Empfindlichkeit der Empfänger deutlich erhöht werden. Die nach dem Lastwechsel entstandenen Schäden in den Rotorblattschalen waren eindeutig zu detektieren. T2 - DGZfP-Jahrestagung CY - Leipzig, Germany DA - 07.05.2018 KW - Wandler KW - Rotorblattschalen KW - Luftultraschall KW - Ferroelektret PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-453066 SP - 7 PB - Deutsche Gesellschaft für zerstörungsfreie Prüfung e.V. (DGZfP) AN - OPUS4-45306 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nehrig, Marko A1 - Erenberg, Marina A1 - Feldkamp, Martin A1 - Bletzer, Claus A1 - Musolff, André A1 - Wille, Frank T1 - Large Scale IAEA Thermal Test with Wood filled Impact Limiters N2 - Packages for the transport of radioactive material are often equipped with impact limiters consisting of wood. Mostly this wood is encapsulated by steel sheets. The impact limiters are needed to ensure that the transport casks meet the IAEA safety requirements. According to the IAEA safety requirements a package has to withstand consecutively severe mechanical tests followed by a thermal test. The mechanical tests have to produce maximum damage concerning the thermal test. Following this, the impact limiters may have serious pre-damage when the thermal tests begins. The IAEA safety requirements state that during and following the fire test, the specimen shall not be artificially cooled and any combustion of materials of the package shall be permitted to proceed naturally. Small scale fire tests with wood filled metal drums by BAM and works of the French Institute for Radiological Protection and Nuclear Safety (IRSN) showed that pre-damaged steel encapsulated wooden structures could start smoldering initiated by the thermal test. These processes supply additional energy to the cask which should be considered within the safety assessment of the package. As not much is known about smoldering processes in encapsulated wooden structures with a reduced oxygen supply the need for a test was identified. To investigate the influence of a smoldering impact limiter concerning the amount of energy supplied to the cask in dependence of the time BAM conducted a large scale impact limiter thermal test. For that, a pre-damaged impact limiter with a diameter of 2,3 m was mounted on a water tank simulating a cask. A complex system of a regulated pump, a heater, a cooler, a slide valve, a flow meter and numerous thermocouples were installed and connected to a control unit to ensure all needed operating conditions. After a pre-heating compared to typical SNF decay-heat, the 30 min lasting fire phase of the thermal test was started. After that, the expected and initiated smoldering began. The results of the large scale test are presented in this poster. Systematic small scale tests will follow to identify the influence of different parameters, e.g. moisture content and scale effects. The tests took place at BAM Test Site for Technical Safety (TTS) with its various possibilities for mechanical and thermal tests. The results of these tests will have direct influence in the safety assessment of transport cask for the transport of radioactive material T2 - 2018 WM Symposia CY - Phoenix, AZ, USA DA - 18.03.2018 KW - Type-B Package KW - Thermal Test PY - 2018 SP - Paper 18257, 1 EP - 11 AN - OPUS4-45311 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krankenhagen, Rainer A1 - Maierhofer, Christiane A1 - Heckel, Thomas A1 - Brackrock, Daniel A1 - Gower, M. A1 - Lodeiro, M. A1 - Baker, G. T1 - Quantitative comparison of different non-destructive techniques for the detection of artificial defects in GFRP N2 - In order to test their suitability different non-destructive methods were performed to inspect a GFRP plate with artificial defects. These defects were manufactured by means of thin PTFE sheets inserted between two plies in three different depth. The inspection methods were microwave reflection, flash thermography and phased array ultrasonics, all applied to the same specimen. Selected results are shown for all methods demonstrating opportunities and limits of the particular inspection methods. The achieved detection limits and further application aspects are compared directly to provide a useful information for the planning of inspection tasks. T2 - ECNDT CY - Gothenburg, Sweden DA - 11.06.2018 KW - Fiber resisted polymers KW - Non-destructive testing KW - Thermographic testing KW - Ultrasonic testing PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-453728 SP - ECNDT-0247-2018 AN - OPUS4-45372 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krankenhagen, Rainer A1 - Ziegler, Mathias A1 - Maierhofer, Christiane ED - Maldague, X. T1 - Systematic errors in the evaluation of uncorrected data from thermographic lock-in measurements N2 - Lock-in thermography (LT) is based on the correct evaluation of phase differences between the temperature oscillations at different surface regions of the object under test during periodic heating. Since the usual heating procedures contain a DC component, the actual heating pattern achieved is not harmonic. This causes systematic deviations when phase differences are determined by means of harmonic analysis, e.g. with FFT analysis. The resulting errors depend clearly on the ratio between DC and AC amplitude, which is demonstrated at simulated and experimentally recorded temperature transients. Further experimental LT data obtained by different oscillating energy inputs showed a variety of possible shapes of transients with different DC components. T2 - 14th QIRT Conference CY - Berlin, Germany DA - 26.06.2018 KW - NDT KW - Lock-in Thermography KW - FFT PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-453768 SP - 539 EP - 547 PB - QIRT Council AN - OPUS4-45376 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wille, Frank A1 - Moutarde, M. A1 - Apel, Andreas A1 - Ballheimer, Viktor A1 - Sterthaus, Jens T1 - Recent developments in standards and IAEA guidance material for package load attachment points N2 - For transport package design and operation according to IAEA regulations, the package shall be securely stowed and its retention system shall be capable to withstand load conditions of routine transport. The supporting IAEA Advisory Material SSG-26 provides information how to do that. Up to now package designers in different countries use other load factors for the design of attachment points than those specified in the IAEA guidance material. In particular the acceleration values vary between different countries and lead to difficulties during the validation of foreign approval certificates. Therefore the IAEA started a discussion process to review the existing guidance text. An international working group was constituted in 2013. Representatives came from different stakeholders, e.g. transport operators, competent authorities and modal organizations. The discussions concluded especially on the transport conditions which has to be considered for stowage design, including on the one hand the relevance of the load factors used for strength and fatigue analysis and on the other hand the criteria which have to be considered for the attachment points. Another standard with relevance to the load attachment of packages is ISO 10276. This standard deals with trunnion design, manufacturing and operational aspects. The regular standard revision phase started in 2017. An expert group discussed new state-of-the-art technology and proposed revised text for the ISO standard for international discussion. The paper describes relevant tie-down aspects, gives background argumentation, and tries to support harmonized application of the revised IAEA guidance material and future ISO 10276 standard. T2 - 11th International Conference on the Transport, Storage and Disposal of Radioactive Materials CY - London, UK DA - 15.05.2018 KW - Verzögerungswerte KW - Lastanschlag KW - Trunnion design KW - ISO KW - Retention PY - 2018 SP - 18511, 1 EP - 8 AN - OPUS4-45294 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Debruyne, M. A1 - Eckert, B. A1 - Wille, Frank A1 - Gauthier, F. A1 - Le Bars, I. A1 - Cordier, N. A1 - Jouve, A.-C. T1 - Assessment of safety demonstrations relative to packages containing UF6 N2 - Specific attention should be paid on safety demonstrations transmitted by applicants in the case of approval request for the package designs containing enriched UF6. Concerning the shipment of enriched UF6, the package designs consist in general of a filled 30B cylinder surrounded by an overpack. The description of the content, considering the UF6 origin, i.e. natural or reprocessed, shall be clearly justified especially when the UF6 isotopic composition exceeds the limits specified in ASTM standards. Concerning the containment of the UF6, the applicant shall demonstrate in all conditions of Transport the leak-tightness of the valve and plug of the cylinders filled with enriched UF6. In this regard, when justifications are based on numerical calculations, the absence of contact between These components of the cylinder and the internal surfaces of the overpack after the regulatory drop tests shall be shown. In particular, absence of contact between the valve and any other component of the packaging shall be confirmed to respect the current IAEA regulations [3]. If complementary calculations show a contact between the plug and the internal surfaces of the overpack, additional tests are required to confirm that the strength resulting from this contact will not affect the plug leak-tightness. It can be noticed that the future revision of the IAEA regulations will include additional provision in case of contact of the plug with any other component of the packaging. In addition, the applicant shall demonstrate that the melting temperature of the valve, including the tinned joint, will not be exceeded during the regulatory fire test. Furthermore, the representativeness of the ballast used to simulate the behaviour of the UF6 loaded within the cylinder shall be justified if drop tests are performed. Finally, specific provisions relative to the use of plugs and the maintenance of cylinders should be included in the safety analysis reports. T2 - 11th International Conference on the Transport, Storage and Disposal of Radioactive Materials CY - London, UK DA - 15.05.2018 KW - Uranhexaflourid KW - Package safety KW - Valve KW - Drop testing KW - Radioactive material PY - 2018 SP - 18523, 1 EP - 8 AN - OPUS4-45295 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lüth, Peter A1 - Brandes, E. A1 - Frost, K. A1 - Kurth, Lutz A1 - Schmidt, Martin A1 - Michael-Schulz, Heike A1 - Uhlig, S. T1 - CEQAT-DGHS Ringversuchsprogramm für die Chemikaliensicherheit -Methodenvalidierung N2 - Bei der Bewertung der Verlässlichkeit der im Labor gewonnenen Prüfergebnisse spielen Ringversuche eine entscheidende Rolle. Die Bundesanstalt für Materialforschung und –prüfung (BAM) unterstützt deshalb den weiteren Ausbau des Ringversuchsprogramms des im Jahr 2007 gegründeten Kompetenzzentrums zur Qualitätssicherung für Prüfungen von Gefahrgütern und Gefahrstoffen auf physikalische Gefahren (Centre for quality assurance for testing of dangerous goods and hazardous substances, CEQAT-DGHS). Bei allen bisher untersuchten Prüfmethoden besteht ein Verbesserungsbedarf. Die RV müssen daher zunächst auf die Methodenentwicklung, -verbesserung und -validierung und auf die Bestimmung der Messunsicherheit der jeweiligen Prüfmethode abzielen und nicht auf Leistungstests. T2 - Behörden-Erfahungsaustausch CY - Berlin, Germany DA - 4. Juni 2018 KW - Prüfmethode KW - Methodenvalidierung KW - Gefahrgut KW - Gefahrstoff KW - Qualitätssicherung PY - 2018 AN - OPUS4-45297 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Griesche, Axel A1 - Pfretzschner, Beate A1 - Schaupp, Thomas A1 - Schulz, M. A1 - Kardjilov, N. ED - Duprez, Lode T1 - Hydrogen in steel visualized by neutron imaging N2 - Neutron cameras allow visualizing hydrogen distributions with radiographic or tomographic imaging methods in iron and steel. The necessary contrast between hydrogen and iron stems from the high difference in the total neutron cross section of both elements. This allows e.g. the in situ measurement of hydrogen mass flow inside cm thick steel samples with a temporal resolution of 20 s using neutron radiography as well as the quantitative measurement of hydrogen accumulations at the crack’s inner surfaces in hydrogen embrittled iron samples with neutron tomography. We could detect directly gaseous hydrogen in the crack cavities and we measured the gas pressure. This new quality of the information on a micrometer scale allows new insights for the analysis of hydrogen-induced damage mechanisms. Further, this method is non-destructive and provides local information in situ and in three dimensions with a spatial resolution of 20-30 µm. In this contribution, we show examples that demonstrate the spatial and temporal resolution of the neutron radiography and tomography methods in order to visualize and quantify hydrogen accumulations at cracks. The measurements were performed at the research reactor BER II of the HZB in Berlin and at the FRM II reactor of the neutron source Heinz Maier-Leibnitz in Garching. T2 - Third International Conference on Metals & Hydrogen CY - Ghent, Belgium DA - 29.05.2018 KW - Hydrogen KW - Steel KW - Neutron imaging PY - 2018 SN - 978-9-08179-422-0 SP - J01 AN - OPUS4-45359 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Dai, X. A1 - Zhang, W. A1 - Li, H. A1 - Huang, T. A1 - Li, M. A1 - Quan, C. A1 - Zhang, Q. A1 - Davies, S. R A1 - Warren, J. A1 - Lo, M.-F. A1 - Kakoulides, E. A1 - Ceyhan Gören, A. A1 - Marbumrung, S. A1 - Pfeifer, Dietmar A1 - Ün, I. A1 - Gündüz, S. A1 - Yilmaz, H. A1 - Kankaew, P. A1 - Sudsiri, N. A1 - Shearman, K. A1 - Pookrod, P. A1 - Polzer, J. A1 - Radeck, W. T1 - CCQM-K104 Key Comparison on the characterization of organic substances for chemical purity - Avermectin B1a N2 - Anwendungen von qNMR KW - qNMR PY - 2017 SP - 1 EP - 32 AN - OPUS4-45035 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dittmann, Daniel A1 - Braun, Ulrike A1 - Jekel, M. A1 - Ruhl, A. S. T1 - Thermoanalytische Verfahren in der Umweltanalytik: Neue Methoden für die weitergehende Abwasserbehandlung mit Aktivkohle N2 - In diesem Beitrag werden zwei Möglichkeiten zur Quantifizierung von PAK in Belebtschlamm durch thermogravimetrische Methoden beschrieben sowie der Einfluss von PAK auf die Biomasse mittels Zersetzungsgasanalyse nachgewiesen. T2 - Wasser 2018 CY - Papenburg, Germany DA - 07.05.2018 KW - Thermogravimetrie KW - Belebtschlamm KW - Infrarotspektroskopie KW - Thermoanalyse KW - Pulveraktivkohle PY - 2018 SN - 978-3-947197-05-7 SP - 301 EP - 305 AN - OPUS4-44972 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lugovtsova, Yevgeniya A1 - Bulling, Jannis A1 - Krome, Fabian A1 - Prager, Jens T1 - Effiziente Modellierung von geführten Wellen mit der Scaled Boundary Finite Elemente Methode und deren Anwendung für Composite-Druckbehälter N2 - Die Scaled Boundary Finite Elemente Methode (SBFEM) ist eine semi-analytische Methode, die speziell für Modellierung von geführten Wellen weiterentwickelt und optimiert wurde. Da nur den Rand der Rechendomäne diskretisiert wird, hat die SBFEM einen geringen Rechenaufwand. In diesem Beitrag wird die SBFEM benutzt, um die Ausbreitung geführter Wellen in einer Metall-Faserverbund-Werkstoffstruktur zu analysieren. Mittels der SBFEM ist es möglich, verschiede Fehlertypen, z.B. Ermüdungsrisse, Poren, Delaminationen, Korrosion, in das numerische Modell zu integrieren und damit Defekt-Mode-Wechselwirkung zu analysieren. Die Ergebnisse wurden für die Entwicklung einer Methode zur Zustandsüberwachung von Composite-Druckbehältern verwendet. T2 - DGZfP-Jahrestagung 2018 CY - Leipzig, Germany DA - 07.05.2018 KW - Wasserstoffspeicher KW - Automobilindustrie KW - Kohlenstofffaserverstärkter Kunststoff KW - Hybrid Materialien PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-449797 SP - 1 EP - 4 AN - OPUS4-44979 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grätz, Rainer T1 - Absichern von Anlagen - Auswirkungsbegrenzung N2 - Nach dem Prinzip der integrierten Explosionssicherheit sind bei der Planung von Anlagen folgende Maßnahmen in Betracht zu ziehen: a) Vermeidung der Bildung von explosionsfähiger Atmosphäre b) Vermeidung der Entzündung von explosionsfähiger Atmosphäre und c) Vorrichtungen, die anlaufende Explosionen umgehend stoppen und/oder den von einer Explosion betroffenen Bereich begrenzen. Im Folgenden werden einige Aspekte der konstruktiven Maßnahmen zur Auswirkungsbegrenzung von Explosionen nach c) erläutert. Die vier wesentlichen, eingeführten und erprobten derartigen Schutzmaßnahmen sind Explosionsdruckentlastung, explosionsfestes Gerät, Explosionsunterdrückung und Explosionsentkopplung. T2 - VDI-Wissensforum "Explosionsschutz entzündbarer Flüssigkeiten und Gase" CY - Düsseldorf, Germany DA - 15.05.2018 KW - Explosionsschutz KW - Schutzsysteme KW - ATEX KW - Richtlinie 2014/34/EU KW - Explosionsdruckentlastung KW - Flammendurchschlagsicherungen KW - Explosionsfeste Bauweise PY - 2018 SP - Paper 8, 1 EP - 24 PB - VDI-Wissensforum GmbH CY - Düsseldorf AN - OPUS4-45013 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grätz, Rainer T1 - Europäische Richtlinien und Normen auf dem Gebiet des Explosionsschutzes für nichtelektrische Geräte N2 - Beschaffenheitsanforderungen an Produkte, die Explosionsschutzanforderungen zu erfüllen haben, werden durch die Europäische Richtlinie 2014/34/EU /8/ geregelt. Diese Europäische Richtlinie erfasst sowohl elektrische als auch nicht-elektrische Geräte. Durch die 11. Verordnung zum Produktsicherheitsgesetz (11. ProdSV) /9/ wurde die Richtlinie 2014/34/EU, in deutsches Recht überführt.Wesentlicher Inhalt der Richtlinie 2014/34/EU sind neben den Definitionen aus dem sogenannten Neuen Rechtsrahmen die Begriffsdefinitionen für Geräte, Schutzsysteme und Komponenten, das System der Konformitätsbewertung und die Konformitätserklärung, sowie die grundlegenden Sicherheits- und Gesundheitsanforderungen. Es gilt dabei das Prinzip der Herstellerverantwortung. Der Hersteller eines Produktes dokumentiert die Erfüllung der Richtlinienanforderungen mit seiner Konformitätserklärung und der Kennzeichnung des Produktes mit dem CE-Zeichen. T2 - VDI-Wissensforum "Explosionsschutz entzündbarer Flüssigkeiten und Gase" CY - Düsseldorf, Germany DA - 15.05.2018 KW - Explosionsschutz KW - ATEX KW - Richtlinie 2014/34/EU KW - Nichtelektrische Geräte KW - Konformitätsbewertung PY - 2018 SP - Paper 3, 1 EP - 48 PB - VDI-Wissensforum GmbH CY - Düsseldorf AN - OPUS4-45014 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Tietje, O. A1 - Burkhardt, M. A1 - Rohr, M. A1 - Borho, N. A1 - Schoknecht, Ute T1 - Emissions- und Übertragungsfunktionen für die Modellierung der Auslaugung von Bauprodukten N2 - Auslaugung von Stoffen aus Bauteilen kann zu einer Belastung von Boden und Gewässern führen. Das Simulationsmodell COMLEAM (COnstruction Material LEAching Model) wurde eingesetzt, um die Stoffauswaschung besser zu verstehen und das damit verbundene Umweltrisiko besser einschätzen zu können. Emissionsfunktionen sind Bestandteil dieses Modells. Hier werden fünf verschiedenen Funktionen beschrieben, getestet und hinsichtlich ihrer Eignung für Prognosemodelle bewertet. KW - Emissionsfunktionen KW - Auswaschverlauf KW - Bauprodukt KW - Biozid KW - Modellierung PY - 2018 SN - 1862-4359 VL - 28 SP - 1 EP - 57 CY - Dessau-Roßlau AN - OPUS4-44735 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Orellana Pérez, Teresa A1 - Völzke, Holger A1 - Wolff, Dietmar A1 - Zencker, Uwe T1 - Relevance of cladding failure mechanisms due to zirconium hydride precipitation under extended dry storage conditions in Germany N2 - The German nuclear waste management strategy consists of dry interim storage of spent fuel inside dual purpose casks and its subsequent direct final disposal in a deep geological repository. Interim storage is limited to 40 years so far, but will have to be extended until repository site selection and operation is concluded, potentially up to 100 years. In this context, research on the long term performance of safety relevant cask components and fuel rod integrity during such extended periods of time is of outmost importance. The barrier function of the fuel cladding depends on its integrity under operational and accidental conditions along with storage and subsequent transportation and is mainly affected over time by altering of the cladding microstructure and by thermo-mechanical conditions during reactor operation and subsequent wet and dry storage. This paper focuses on failure mechanisms regarding cladding embrittlement caused by physical phenomena concerning hydrogen dissolution and precipitation of hydrides in the zirconium matrix. Within this context, potential cladding integrity issues under extended interim storage conditions followed by transportation are emphasized. Delayed hydride cracking (DHC) is a well-known time-dependent temperature-activated phenomenon failure mechanism of the fuel cladding during reactor operation. The phenomenon consists of hydrogen diffusion and hydride precipitation at the tip of an initial crack and the propagation of the crack to an approximate distance equal to the length of the hydride. This failure mechanism is temperature-activated phenomenon and enhances along with thermal cycling of the fuel cladding, e. g. during reactor shutdowns. DHC shows limited relevance under quasi static storage conditions with continuously lowering temperatures. However, the literature points that DHC may occur when the temperature during storage decreases to a certain level after some decades and in combination with stress concentrations in the cladding material. When spent fuel is transferred to dry storage by vacuum drying, the cladding temperature raises up to peak temperatures of ~370°C. Under these conditions, hydrides dissolute into the zirconium matrix up to the solubility limit defined by the peak temperature and this amount of hydrogen can precipitate in a radial re-oriented fashion due to the temperature decrease during storage. Cladding materials with radially precipitated hydrides show significant embrittlement. Radially oriented hydrides are perpendicularly oriented to hoop stresses representing the most critical configuration. Brittle failure of the cladding then occurs by crack propagation through radially oriented hydrides and finally through the zirconium matrix. The susceptibility to radial hydride precipitation depends on cladding material type and microstructure, hydrogen content, pre-drying hydride distribution, irradiation conditions, and temperature and stress histories during drying and storage operations. This paper addresses major considerations concerning spent fuel cladding embrittlement due to hydride precipitation with regard to the boundary conditions of dry spent fuel storage in Germany. Analytical, numerical, and experimental approaches are to be discussed by BAM in order to identify the specific needs for future R&D work in that area with the purpose to provide the necessary data base for proper safety demonstration and evaluation along with future extended storage licensing procedures. T2 - 2017 Water Reactor Fuel Performance Meeting CY - Jeju, Korea DA - 10.09.2017 KW - Cladding KW - Hydride precipitation KW - Spent fuel PY - 2017 SP - 1 EP - 8 AN - OPUS4-44749 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bonse, Jörn A1 - Kirner, Sabrina V. A1 - Epperlein, Nadja A1 - Spaltmann, Dirk A1 - Krüger, Jörg T1 - Surface functionalization by laser-induced periodic surface structures (LIPSS) N2 - In this contribution the mechanisms of formation and current applications of LIPSS are reviewed, including the colorization of technical surfaces, the control of surface wetting properties, the mimicry of the natural texture of animal integuments, the tailoring of surface colonization by bacterial biofilms, and the improvement of the tribological performance of nanostructured metal surfaces. T2 - 10th Stuttgart Laser Technology Forum 2018 CY - Stuttgart, Germany DA - 05.06.2018 KW - Laser-induced periodic surface structures (LIPSS) KW - Femtosecond laser ablation KW - Surface functionalization KW - Wetting KW - Tribology KW - Biofilms PY - 2018 SP - 35 AN - OPUS4-45128 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Häßler, Mai A1 - Häßler, Dustin A1 - Hothan, Sascha A1 - Krüger, Simone T1 - Performance of intumescent fire protection coatings on steel tension rod systems N2 - Steel tension rod systems consist of tension rods, fork connectors and associated intersection or connecting plates. They are used for truss systems, bracings or suspensions owing to slender design and increased economic efficiency. In case of fire, beside the tension rods themselves, the connection parts require appropriate fire protection. The use of intumescent fire protection coatings prevents a rapid heating of the steel and helps to ensure the load-carrying capacity of the structures. Because the connection components of the tension rod systems feature surface curvature as well as a complex geometry, high demand is placed on the intumescence and thermal protection effectiveness of the reactive fire protection coatings. Experimental studies were carried out to investigate the performance of intumescent coatings applied to the components of tension rod systems. The examined aspects include the foaming and cracking behaviour of the intumescent coatings, the influence of different dry film thicknesses (DFT), the heating rate of the steel connecting parts in comparison to the tension rods, as well as the mounting orientation of the tension rods together with their associated fork connectors. The results show that a decrease in the surface curvature and/or an increase in the mass concentration of the steel components lead to a lower heating rate of the steel. Moreover, the performance of the intumescent coating on tension rod systems is influenced by the mounting orientation of the steel components. T2 - 10th International Conference on Structures in Fire CY - Belfast, UK DA - 06.06.2018 KW - Steel KW - Tension rod system KW - Intumescent fire protection coating KW - Reactive fire protection system KW - Real-scale fire test PY - 2018 SN - 978-1-85923-274-3 SP - 649 EP - 654 PB - Ulster University CY - Belfast AN - OPUS4-45152 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beck, Uwe A1 - Mitzkus, Anja A1 - Sahre, Mario A1 - Weise, Matthias A1 - Köppe, Enrico A1 - Bartholmai, Matthias A1 - Basedau, Frank A1 - Hofmann, Detlef A1 - Schukar, Vivien T1 - Faser-basierter magneto-optischer Schicht-Sensor zum Monitoring von Bauteilen N2 - In Glasfasern eingeschriebene Bragg-Gitter (FBG: fibre-based Bragg gratings) sind über die Verschiebung der Bragg-Wellenlänge in der Lage, Stauchungen und Dehnungen von Glasfasern hochgenau zu erfassen. In Kompositwerkstoffe eingebettete faseroptische Sensoren können Bauteile bezüglich ihrer mechanischen Integrität überwachen und früh-zeitig Informationen über Materialveränderungen gewinnen. Um die Zuverlässigkeit eines solchen Sensors zu gewährleisten, ist es wichtig, die korrekte Funktion des Sensors im Verbund mit der Werkstoff-Matrix on-line und in-situ sicherzu-stellen. Im Rahmen des DFG-Projekts FAMOS² (FAser-basierter Magneto-Optischer SchichtSensor) wurde ein selbstdiagnosefähiger Schichtsensor entwickelt, der mit Hilfe von magnetostriktiven Aktorschichten aus Nickel bzw. Eisen-Nickel validiert werden kann. Der FAMOS²-Schichtsensor wird durch ein PVD (physical vapour deposition)/ECD (electro-chemical deposition) Hybridschichtsystem realisiert, das auf dem Fasermantel im Bereich des FBG haftfest, homogen und langzeitfunktional abzuscheiden ist. Dabei wird in einem ersten Schritt ein etwa 100 Nanometer dünnes PVD-Schichtsystem aus Chrom und Kupfer als Haftvermittler auf der Glasfaser bzw. als leitfähige Startschicht für den nachfolgenden ECD-Prozess abgeschieden. Um eine rotationssymmetrische Schich-tabscheidung zu gewährleisten, erfolgt während der PVD-Beschichtung eine Rotation der Glasfasern. In einem zweiten Schritt wird dann unter Verwendung eines klassischen Watts-Elektrolyten in einer speziell entwickelten ebenfalls rotationssymmetrisch aufgebau-ten ECD-Durchströmungszelle dann die etwa 30 Mikrometer dicke, magnetostriktive Ak-torschicht auf dem PVD-Schichtsystem abgeschieden, im Vergleich sowohl reine Nickel-Schichten als auch Nickel-Eisen-Schichten. Ein äußeres Magnetfeld dehnt die magnetostriktive Aktorschicht und damit auch die Faser reversibel. Diese Dehnung führt zu einer Verschiebung der Bragg-Wellenlänge, welche direkt mit der Stärke eines zu messenden oder zu Validierungszwecken vorgegebenen Magnetfeldes korreliert. Die Anpassung der Beschichtungsverfahren an die Fasergeome-trie und die mechanischen Eigenschaften der Hybridschichten werden hinsichtlich der me-chanischen Integrität des faseroptischen Sensors diskutiert und der Nachweis der Selbst-diagnosefähigkeit erbracht. T2 - 13. ThGOT Thementage Grenz- und Oberflächentechnik und 11. Thüringer Biomaterial-Kolloquium CY - Zeulenroda, Germany DA - 13.03.2018 KW - Magneto-optischer Sensor KW - Faser-Bragg Gitter KW - Magnetostriktive Beschichtung KW - Selbstkalibrierung KW - Bauteilmonitoring PY - 2018 SN - 978-3-00-058187-8 SP - 1 EP - 5 CY - Jena AN - OPUS4-44599 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kotschate, Daniel A1 - Gaal, Mate A1 - Kersten, H. T1 - Untersuchung der akustischen Eigenschaften von Plasmalautsprechern auf Basis einer dielektrischen gehemmten Oberflächenentladung (SDBD) N2 - Analog zu Blitz und Donner können elektrische Entladungen innerhalb eines Gasvolumens als akustische Quellen agieren und haben daher eine starke Verbreitung als diagnostische Methode (bspw. in der Raumakustik und bei der Ortung von Teilentladungen). Diese auf dem Prinzip der Thermoakustik beruhende Möglichkeit der Schallerzeugung und die damit verbundenen physikalischen Wechselwirkungen machen die Notwendigkeit einer mechanisch ausgelenkten Membran überflüssig. Dabei wird dem hochfrequenten Träger das Nutzsignal aufgeprägt, welches eine Volumenänderung des umliegenden Gases um seinen Ruhezustand verursacht. Durch die somit hervorgerufene zyklische thermische Wechselwirkung mit dem umliegenden Gasgemisch bedarf es daher ebenfalls keiner akustischen Anpassung. In den vorgestellten Ergebnissen wurde das Übertragungsverhalten eines Oberflächenplasmas (SDBD, surface dielectric barrier discharge) untersucht. Als Maß für den Wirkungsgrad und das Übertragungsverhalten des Aktuators wurden Klirrfaktor- und THD- Messungen und unter Variation der Eingangsleistungen durchgeführt. Durch die positiven akustischen Eigenschaften eröffnen sich neue Applikationen für den Einsatz von Plasmahochtönern wie bspw. zerstörungsfreie Werkstoffprüfung von Verbundsystemen und Klebeverbindungen im Automobilsektor oder im Bauwesen. T2 - 44. Jahrestagung für Akustik (DAGA 2018) CY - Munich, Germany DA - 19.03.2018 KW - Gas discharges KW - Atmospheric pressure plasma KW - Surface dielectric barrier discharge KW - Plasma speaker PY - 2018 SN - 978-3-939296-13-3 SP - 555 EP - 558 AN - OPUS4-44812 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Metz, Christian A1 - Franz, Philipp A1 - Wachtendorf, Volker A1 - Maierhofer, Christiane A1 - Fischer, C. ED - Ziegahn, K.-F. T1 - Additiv gefertigte Polymerbauteile: Untersuchung der Beständigkeit durch künstliche Bewitterung und zerstörungsfreie Charakterisierung N2 - Es wird ein Verfahren zur Charakterisierung der Beständigkeit und Langzeitstabilität von additiv gefertigten Kunststoff-Bauteilen vorgestellt. Dabei sollen die Prüfkörper über 2000 Stunden künstlich bewittert und währenddessen die Änderungen der Eigenschaften der Bauteile zerstörungsfrei untersucht werden. T2 - 47. Jahrestagung der Gesellschaft für Umweltsimulation e.V. CY - Stutensee, Germany DA - 21.03.2018 KW - Additive Fertigung KW - Künstliche Bewitterung KW - Thermografie KW - Additive manufacturing PY - 2018 VL - 47. SP - 99 EP - 105 PB - Gesellschaft für Umweltsimulatin e.V. AN - OPUS4-44638 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Otremba, Frank A1 - Romero-Navarrete, José A. T1 - A testing rig to study vehicle-track interaction during turning N2 - A testing rig for the measurement of the dynamic loads on the rails due to cargo sloshing,has been proposedin this paper. The system represents a scale-down approach that simulates astraightening maneuver of the railway car after negotiating a turn. As part of the experimental effort, a mathematical model was developed that, oncevalidated, will provide more insights about the potential effect of many other cardesign factors, on the level of stress developed in the raildue to the sloshing cargo.A fundamental output from the testing, will be the objective comparison between the railloads due toa sloshing and a non-sloshing cargo, together with a validated model that wouldallow parametric studies in relation withthe potential effect,of several track and carproperties,on the magnitude of the sloshing forces on the rail. T2 - IEEE/ASME Joint Rail Conference CY - Pittsburgh, PA, USA DA - 18.04.2018 KW - Testing KW - Rig KW - Vehicle-Track KW - Interaction PY - 2018 SP - 1 EP - 6 PB - ASME AN - OPUS4-44816 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Becker, Günther T1 - Protection of Wood Particle Board against Termites N2 - Particle boards are of increasing economic importance. Without special treatment they are destroyed by termites. Deterioration of unprotected material as well as possibilities and present knowledge of preservation against termite attack are briefly described. Recent laboratory experiments with particle board treated to make it resistant to humidity and basidiomycete fungi showed that only one organic preservative out of four protected the boards also against termite attack; one of two water-soluble preservatives gave promising results. Heterotermes indicola (Wasmann) from India proved to be more aggressive and resistant to the preservatives than Coptotermes amanii (Sjöstedt) from Kenya and Nasutitermes nigriceps (Haldemann) from Guatemala. Kalotermes flavicollis (Fabr.) from Italy was also very tolerant to the fungicidal preservatives. Further development of treatments of particle board against termites is required. T2 - The World Consultation on the Use of Wood in Housing CY - Vancouver, B. C., Canada DA - 05.07.1971 KW - Material Processing KW - India KW - Laboratory Experiment KW - Promising Result KW - Special Treatment PY - 1972 VL - 6 IS - 3 SP - 239 EP - 248 PB - Springer AN - OPUS4-45428 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schade, U. A1 - Ritter, E. A1 - Aziz, E. F. A1 - Puskar, L. A1 - Beckmann, Jörg T1 - Spectroscopic ellipsometry on liquids in the far infrared N2 - The far infrared refractive indices and the extinction coefficients of liquids can be obtained by means of spectroscopic ellipsometry in attenuated total reflection configuration. Such optical constants will contribute to a spectroscopic data base in the far infrared and terahertz spectral regions. The experimental implementation and the calibration procedure of the method are described in detail. The temperature dependency of the optical constants for water over a broad spectral range is exemplarily presented. T2 - 42nd International Conference on Infrared, Millimeter and THz Waves CY - Cancun, Mexico DA - 27.08.2017 KW - Ellipsometry KW - Far Infrared KW - ATR KW - Attenuated total reflection KW - Calibration KW - Extinction coefficients KW - Refractive index measurement KW - Spectroscopic ellipsometry KW - Far infrared refractive index KW - Terahertz spectral region KW - Optical constant KW - Attenuated total reflection configuration KW - Liquid extinction coefficient KW - Optical refraction KW - Optical variables control KW - Optical reflection KW - Liquids KW - Optical films KW - Optical polarization KW - Optical variables measurement PY - 2017 UR - http://ieeexplore.ieee.org/stamp/stamp.jsp?tp=&arnumber=8066931&isnumber=8066832 DO - https://doi.org/10.1109/IRMMW-THz.2017.8066931 SN - 2162-2035 SP - MD.1.5-1 EP - MD.1.5-2 PB - IEEE CY - Danvers AN - OPUS4-42028 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beckmann, Jörg A1 - Spranger, Holger T1 - THz-TDS-SAFT for the detection of inherent discontinuities in dielectric materials N2 - Today X-ray tomography and Ultrasound Synthetic Aperture Focusing Techniques are representative examples for defect imaging in the field of nondestructive testing. THz time domain spectroscopy (TDS) operates with short electromagnetic pulses. The sensitivity of the pulses to optical material property changes makes THz-TDS attractive for the detection of flaws in dielectric materials. Unfortunately, the X-ray computed tomography (CT) model holds only for THz-TDS reconstruction if minor refraction index differences between the inhomogeneities and the surrounding material matrix exist. A Time Domain SAFT algorithm has been developed to overcome the restrictions. THz time domain measurement on representative sample sets with inherent artefacts were performed to use them for the Image reconstructions. The results will be presented and compared with optical surface images of the used test objects to evaluate the SAFT algorithm in relation to the econstruction quality. T2 - 42nd International Conference on Infrared, Millimeter and Terahertz Waves CY - Cancun, Mexico DA - 27.08.2017 KW - THz-TDS-Saft KW - Tomography KW - Dielectric materials KW - Image reconstruction KW - Terahertz spectroscopy KW - Terahertz wave imaging KW - Time-domain analysis KW - X-ray tomography KW - Ultrasound synthetic aperture focusing techniques KW - Terahertz time domain spectroscopy KW - Time domain SAFT algorithm KW - Image reconstructions KW - Optical surface images KW - Computed tomography KW - Dielectrics KW - Time measurement KW - Reflection PY - 2017 UR - http://ieeexplore.ieee.org/stamp/stamp.jsp?tp=&arnumber=8067159&isnumber=8066832 SN - 978-1-5090-6048-1 DO - https://doi.org/10.1109/IRMMW-THz.2017.8067159 SP - TD.19-1 EP - TD.19-2 PB - IEEE CY - Danvers, USA AN - OPUS4-42030 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bartholmai, Matthias A1 - Werner, Klaus-Dieter A1 - Johann, Sergej A1 - Daum, Werner ED - Cosmi, F. T1 - Characterization of the temperature behavior of a piezoresistive accelerometer N2 - Piezoresistive accelerometers use a strain-sensing element, generally made of semiconductor material, e.g., silicon to convert the mechanical motion into an electrical signal. This element is usually designed in form of a cantilever beam loaded with a mass. Acceleration causes bending of the beam, which produces a change of electrical resistance proportional to the applied acceleration. Main advantages of piezoresistive accelerometers in comparison to other types, e.g., piezoelectric and capacitive, is their robust and highly dynamic behavior, which qualifies them for application in high impact shock applications. Mechanical damping is typically implemented with silicon oil in a way that the output signal is undistorted over a wide frequency range. These characteristics principally qualify them for the application in drop tests carried out at BAM, for which they are calibrated over the frequency range from 1 to 4 kHz. However, using silicon oil for damping, has the drawback of temperature dependent change of its viscosity, leading to temperature dependent deviation of the accelerometer’s sensitivity. This study presents experimental results of the temperature behavior of a piezoresistive accelerometer with a dynamic range up to ±5000 g. This type of accelerometer is applied for drop tests which are partially performed at temperatures of -40 or +100 °C. T2 - 34th Danubia-Adria Symposium on Advances in Experimental Mechanics CY - Trieste, Italy DA - 19.09.2017 KW - Accelerometer KW - Temperature behavior KW - Drop test PY - 2017 UR - https://www.openstarts.units.it/handle/10077/14921 SN - 978-88-8303-863-1 SP - 93 EP - 95 CY - Trieste AN - OPUS4-42109 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dietrich, Matthes A1 - Knaust, Christian A1 - Arnold, L. A1 - Brüne, M. A1 - Festag, S. T1 - Buoyancy driven flow in an underground metro station for different climate conditions – experimental and numerical investigation N2 - In urban areas the demand for public transportation is constantly growing. Underground railway systems overcome the problem of limited space on the ground and are therefore one of the most powerful systems in urban public transportation. These facilities can be very complex and are used by a large amount of passengers. Therefore, it is important to maintain the safety for people and buildings. Especially in the case of fire or arson attack. This paper focusses on a fire scenario in a complex subway station for different weather conditions. The purpose is to identify the influences of different weather conditions on the smoke spread and the ability of self-rescue in case of a burning luggage. The evaluation of the fire simulations will focus on toxicity and visibility taking into account the FED concept. T2 - AUBE '17 & SUPDET 2017 CY - Washington D.C., USA DA - 12.09.2017 KW - Fire simulations KW - Weather conditions KW - FED PY - 2017 SN - 978-3-940402-11-0 VL - 2 SP - II-121 EP - II-128 AN - OPUS4-42253 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Barnefske, Lena A1 - Wachtendorf, Volker T1 - Self-healing silicone rubber for fluorescent partial discharge POF sensors in high-voltage cable accessories N2 - To avoid a catastrophic failure of insulation in high-voltage (HV) applications, a monitoring of partial discharges (PDs) is necessary. Fluorescently labelled polymer optical fibers (F-POF) offer an electrically passive method for PD detection in HV facilities. F-POFs could be embedded in HV cable accessories, which are usually made of silicone rubber. Herein they detect the light emitted by the PD and convert it into an electrical signal that can be monitored. Due to the difficult accessibility of HV cable accessories, a self-healing silicone rubber with prolonged service life after PD detection represents an attractive material design for HV accessories. With this contribution, we would like to present and discuss the possibilities of combining self-healing materials with POF-based sensors for PD detection in HV applications. T2 - 26th International Conference on Plastic Optical Fibres CY - Aveiro, Portugal DA - 13.09.2017 KW - Fluorescent polymer optical fibres KW - Partial discharge detection KW - High voltage cable accessories KW - Self-healing KW - Silicone rubber PY - 2017 SN - 978-989-97345-2-4 SP - paper 16, 1 EP - 5 AN - OPUS4-42510 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wosniok, Aleksander A1 - Krebber, Katerina T1 - Smart geosynthetics for structural health monitoring applications N2 - Responding to a growing need for intelligent monitoring of critical geotechnical and civil infrastructures, new multifunctional geotextiles and geogrids with integrated optical fibers were developed and investigated within several research projects. Such smart two-dimensional geosynthetics intercorporating optical fibers as distributed sensors provide solutions both for soil reinforcement, erosion control, drainage or environmental protection and for cost-effective monitoring of critical mechanical deformations and temperature distribution in geotechnical and masonry structures at the same time. The integrated fiber optic sensors provide online information about the condition of the monitored structure and about the occurrence and localization of any damage or degradation for the purpose of preventing a total collapse. T2 - The Fiber Society's Spring 2017 Conference CY - Institut für Textiltechnik der RWTH Aachen, Germany DA - 17.05.2017 KW - Smart geosynthetics KW - Sensor-based geotextiles KW - Fiber optic sensor KW - POF sensor KW - Distributed sensing PY - 2017 SP - 43 AN - OPUS4-42560 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krütt, Enno ED - Breit, W. ED - Kurz, W. ED - Pahn, M. ED - Sadegh-Azar, H. ED - Schnell, J. ED - Thiele, C. T1 - Ermüdungsbedingte Degradation von Fahrbahnbeton - Einfluss auf den Stofftransport N2 - In den letzten 15 Jahren hat im deutschen Autobahnnetz die Anzahl von Schäden an Betonfahrbahnen, die vor 2005 er-richtet wurden zugenommen. Dies führt oft zu einer Vermin-derung der Lebensdauer von 30 auf 10 bis 15 Jahre. Trotz umfassender Untersuchungen wurde die Ursache bis jetzt nicht eindeutig geklärt, jedoch scheint die Alkali-Kieselsäure-Reaktion (AKR) hierbei eine Rolle zu spielen. Vor diesem Hintergrund wurden AKR-Performance-Tests entwickelt, die jedoch die mechanischen Einwirkungen aus Klima und Ver-kehr nicht berücksichtigen. Aus diesem Grund wurde eine AKR-Forschergruppe von der Deutschen Forschungsgemein-schaft ins Leben gerufen, welche sich experimentell und auf Simulationsebene mit diesem Thema befasst. Inhalt dieses Beitrages sind ausgewählte Ergebnisse des an der BAM bear-beiteten experimentellen Projektteils, welche in eine auf die Auswirkung einer mechanischen Degradation fokussierte Promotionsarbeit einfließen. Ziel der ausgewählten Untersuchung ist es, den Einfluss einer mechanisch induzierten Betondegradation auf den Stofftrans-port herauszuarbeiten. Hierzu wird ein großformatiger Balken einem zyklischen Vier-Punkt Biegezugversuch mit einer Anzahl von 5 Mio. Lastwechseln unterzogen. Während des Versuches findet ein Schadensmonitoring mit verschiedenen zerstörungsfreien Prüftechniken statt. Hierzu zählen Deh-nungsmessungen, Schallemissionsanalyse und Ultraschall-messungen (vgl. Bild 1). Nach dem zyklischen Belastungs-versuch werden kleinformatige Probekörper aus dem belasteten Balken entnommen. Als Referenz dienen unbelas-tete Probekörper aus der gleichen Herstellungscharge. Die Oberflächen der entnommenen Probekörper werden in einem kapillaren Saugversuch zum einen mit deionisiertem Wasser und zum anderen mit einer 3,6 %igen NaCl-Lösung beauf-schlagt. Während der Saugversuche dienen verschiedene zerstörungsfreie bzw. -arme Messmethoden dazu, die Feuch-teaufnahme bzw. -verteilung in den Probekörpern zu messen. Hierzu gehören neben der Gravimetrie die Messung mit NMR (Nuclear-Magnetic-Resonance) sowie TDR (Time-Domain-Reflectometry). Nach den Saugversuchen wird die Na- und Cl-Verteilung an den mit NaCl-Lösung beaufschlagten Pro-bekörpern zerstörend mittels LIBS (Laser-Induced-Breakdown-Spectroscopy) ermittelt. Erste Ergebnisse zeigen, dass die zyklische Ermüdungsdegradation den Stofftransport tendenziell verstärkt (vgl. Bild 2). T2 - 5. DAfStb-Jahrestagung mit 58. Forschungskolloquium CY - Kaiserslautern, Germany DA - 20.09.2017 KW - Baustoffe KW - Ermüdung KW - AKR PY - 2017 SN - 978-3-00-057267-8 VL - Band 1 SP - 56 EP - 67 AN - OPUS4-42567 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Mohrbacher, H. A1 - Vleugels, J. A1 - Huang, S. T1 - Potentials of niobium carbide (NBC) as cutting tools and for wear protection N2 - Niobium is today largely available. NbC displayed lower dry sliding friction over WC grades. The softer Ni- and NiMo-bonded NbC1.0-grades have a higer abrasive wear resistance (ASTM G65), even with lower toughnesses, than the tougher WC-Co grades and harder NbC-Co grades. T2 - 41st International Conference and Exposition on Advanced Ceramics and Composites CY - Daytona Beach, FL, USA DA - 22.01.2017 KW - Niobium Carbide (NbC) KW - Cutting tool KW - Hardness KW - Friction PY - 2017 VL - 38 SP - 1 EP - 13 AN - OPUS4-43430 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rietz, U. A1 - Lerche, D. A1 - Hielscher, Stefan A1 - Grunwald, Daniel A1 - Beck, Uwe ED - Frenz, H. ED - Langer, J. B. T1 - CAT-Technologie als neues Multiprobenverfahren N2 - Das Fügeverfahren Kleben bietet viele Vorteile, wie das Verbinden verschiedener Materialklassen und eine Lastverteilung über den gesamten Fügebereich, und erfordert schnelle Prüfverfahren zur Ermittlung von Verbundeigenschaften. Das Messprinzip CAT-Technologie® (Centrifugal Adhesion Testing) verwendet die radial gerichtete Zentrifugalkraft als Belastungsgröße, die durch programmierbare Variation der Drehzahl statisch oder dynamisch vorgegeben wird. Bei Erreichen der kritischen Beanspruchung trennt sich der Prüfstempel vom Substrat, zeitgleich wird ein positionsbezogenes Signal aus dem drehenden Rotor gesendet und zusammen mit der Drehzahl an die PC-Software übertragen. Für jede Probe wird die Bruchkraft berechnet und in Echtzeit angezeigt. Der Adhesion Analyser LUMiFrac® untersucht simultan bis zu acht Prüfkörper unter identischen Bedingungen. Das neue Messprinzip erfüllt die Anforderungen von DIN EN 15870, DIN EN 14869-2 und ISO 4624. Neben der Festigkeitsbestimmung von Klebverbindungen ist die Haftung von Schichtsystemen ein weiterer wichtiger Anwendungsbereich. Ergebnisse für Zug- und Scherbeanspruchung, realisiert mit unterschiedlichen Prüfkörper-Layouts, werden vorgestellt und Festigkeit beeinflussende Faktoren, wie Prüfgeschwindigkeit oder Substratverformung bei Beanspruchung, werden aufgezeigt. Die Charakterisierung von Klebebandeigenschaften über die Möglichkeiten der Schälprüfung hinaus wird gezeigt. Des Weiteren werden experimentelle Ergebnisse durch zyklische Belastung (Ermüdung) im Vergleich zu Stan-dard-Tests diskutiert. T2 - Tagung „Werkstoffprüfung" 2017 CY - Berlin, Germany DA - 30.11.2017 KW - Adhäsion KW - Festigkeit KW - Scherbelastung KW - Zugbelastung KW - analytische Zentrifuge PY - 2017 SN - 978-3-9814516-7-2 SN - 1861-8154 SP - 277 EP - 282 PB - DVM Deutscher Verband für Materialforschung und -prüfung CY - Berlin AN - OPUS4-43414 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krome, Fabian A1 - Gravenkamp, Hauke T1 - 3-D Waveguide modeling and simulation using SBFEM N2 - The modeling of waveguides by means of the Scaled Boundary Finite Element Method (SBFEM) has recently been addressed and is considered an effective procedure for the simulation of ultrasonic guided waves in plates and uniform structures, as well as their interaction with defects. This work presents the extension of the known applications like uniform concrete foundation cylinders to structures with more complex shapes and defects. The main focus is the required modeling of 3-D structures in SBFEM to solve these efficiently. Furthermore the coupling of different models is discussed. This involves models like a mainly uniform foundation cylinder with varying material behavior or geometry in certain areas which has to be modeled in 3-D SBFEM. With the presentation of numerical examples the accuracy and performance of the modeling is discussed and the advantages in improving numerical stability are shown. T2 - ICSV22 CY - Florence, Italy DA - 12.07.2015 KW - Scaled boundary finite element method PY - 2015 SP - 2805 EP - 2810 AN - OPUS4-43416 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Romero-Navarrete, José A. A1 - Lozano Guzmán, A. A. A1 - Otremba, Frank T1 - An active acceleration system to mitigate/avoid underride rear-end crashes N2 - Rear-end crashes involving heavy trucks as the leading vehicle, and cars as the impact vehicle, cause many deaths and permanent injuries to car´s occupants. Measures have been thus taken in the trucks to prevent underride crashes, including the mounting of stiffer underride guards, set at car´s bumper height. In this respect, an active acceleration system(AAS), installed in the truck, could also contribute to mitigate the effects of These crashes, through the decrease of the relative Speed of the vehicles at the instant of the crash. In this paper, an AAS system is proposed, under the principles of ultrasonic sensors and an actuator for the truck´s accelerator mechanism. Simulation results of the operation of this AAS system, suggest that such a system could decrease the relative impact speed around 8% for an initial relative speed of 10 m/s. T2 - 2017 International Conference on Advanced Mechatronic Systems CY - Xiamen, China DA - 06.12.2017 KW - Mitigate KW - Avoid KW - Rear-end crashes PY - 2017 SN - 978-1-5386-2601-6 SP - 329 EP - 334 AN - OPUS4-43400 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stajanca, Pavol A1 - Krebber, Katerina ED - Nogueira, R. ED - Rocha, A. M. T1 - Polymer optical fibers as radiation sensors? N2 - Application importance of ionizing radiation has been growing steadily over the last decades. Extensive utilization of ionizing radiation generates demand for development of suitable monitoring techniques. Radiation monitoring systems based on optical fibers offer several key advantages such as small footprint, possibility of remote and real-time measurement as well as electromagnetic immunity. In this contribution, we investigate radiation-induced attenuation (RIA)-based sensing with perfluorinated polymer optical fibers (PF-POFs). The RIA response of two commercial PF-POFs is assessed in a low dose region and performance and limitations of the system are discussed. The concept represents a potential high-sensitivity, low-cost and easy-to-use on-line radiation monitoring system with distributed detection capability T2 - 26thth International Conference on Plastic Optical Fibres (POF 2017) CY - Aveiro, Portugal DA - 13.09.2017 KW - Perfluorinated polymer optical fibers KW - Gamma radiation KW - Radiation monitoring KW - Optical fiber sensor PY - 2017 SN - 978-989-97345-2-4 SP - Paper 5, 1 EP - 4 AN - OPUS4-42318 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stajanca, Pavol A1 - Krebber, Katerina ED - Nogueira, R. ED - Rocha, A. M. T1 - Post-fabrication cladding doping of commercial PMMA polymer optical fiber N2 - Possibility of post-fabrication doping of commercial PMMA fibers using well-known solution doping technique is presented. The cladding of 1 mm PMMA fiber is doped with Rhodamine B with the help of methanol-mediated diffusion of the dye molecules into the fiber material. Doping of the fiber core was not possible even at extended doping times. The proposed method represents rather simple and cheap way for preparing custom cladding-doped POFs with high flexibility of dopant choice and fiber length. Produced cladding-doped fibers have potential for various sensing or lighting applications. T2 - 26th International Conference on Plastic Optical Fibres (POF 2017) CY - Aveiro, Portugal DA - 13.09.2017 KW - Polymer optical fibers KW - Fluorescent dyes KW - Solution doping KW - Polymethyl methacrylate PY - 2017 SN - 978-989-97345-2-4 SP - Paper 14, 1 EP - 4 AN - OPUS4-42319 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Wilke, Olaf A1 - Richter, Matthias A1 - Brödner, Doris T1 - Weiterentwicklung des Umweltzeichens Blauer Engel RAL-UZ 38 „Emissionsarme Produkte aus Holz und Holzwerkstoffen“ (UFOPLAN 3710 95 305 1) N2 - In diesem Projekt wurde das Prüfverfahren für die chemischen Emissionen zum RAL-UZ 38 überarbeitet. Dabei stand die Bewertung der Prüfkammermessungen mit Hilfe des AgBB-Schemas im Vordergrund. Dafür wurden die Prüfkammerbedingungen angepasst. Mit Hilfe einer Emissionsdatenbasis wurden Anforderungen an die Emissionen der Umweltzeichenprodukte abgeleitet. Die Datenbasis bildeten vorhandene Emissionsdaten der Umweltzeichenprodukte und Messungen aktueller Produkte. Dazu wurden 10 Prüfkammermessungen an unterschiedlichen Möbelplatten durchgeführt. In Zusammenarbeit mit den Lizenznehmern, dem RAL und dem Umweltbundesamt wurde ein neues Verfahren für die Auswahl der Prüfmuster für die Emissionsmessung erarbeitet. Dieses vereinigt eine repräsentative Auswahl mit einer regelmäßigen Nachprüfung einzelner Möbel und/oder Bauteile. Zudem wurden Kriterien für die Überprüfung der Anforderungen an die Herkunft des Holzes aufgestellt. Für Bodenbeläge, Paneele und Türen aus Holz und Holzwerkstoffen für Innenräume wurde eine neue Vergabegrundlage erschaffen (RAL-UZ 176). KW - Blauer Engel KW - Emissionsarme Materialien KW - Prüfverfahren KW - VOC-Emission PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-427472 SN - 1862-4359 VL - 2017/31 SP - 1 EP - 46 PB - Umweltbundesamt (UBA) AN - OPUS4-42747 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stamenkovic, V. A1 - Felsheim, F. T. A1 - Plath, R. A1 - Kapa, Thomas ED - Diaz, Ricardo Rubén ED - Assaf, Leonardo Octavio ED - Silva, José ED - Rizzotti, Bruno T1 - Lab testing of external gas pressure cables and determination of different ageing states N2 - In the last century external gas pressure cable systems with 64/110 kV operating voltage have proven to form a reliable way for the transportation of electrical energy in larger cities all over the world. The beginning of their development reaches back to the 1930s. The dielectric used in these thermally stable cables consists of a mass impregnated cable paper insulation that requires the absence of partial discharges as a prerequisite for continuous operation. In this contribution two test set-ups for advanced lab testing of external gas pressure cable specimens were established. Two specimens of different aging state were subjected to various electrical voltage levels and frequencies as well as different temperatures. Simultaneously dissipation factor measurement and partial discharge detection were applied. Finally the specimens’ relationships between dissipation factor, partial discharge level, temperature, impregnation mass to paper ratio, water content and external gas pressure were discussed. T2 - The 20th International Symposium on High Voltage Engineering CY - Buenos Aires, Argentina DA - 27.08.2017 KW - High voltage cable KW - Fibre optic sensors KW - Gas pressure cable PY - 2017 SN - 978-987-45745-6-5 VL - 2017 SP - 1 EP - 6 PB - Asociación Coorperadora de la Facultad de Ciencias Exactas y Tecnologia de la UNT AN - OPUS4-42766 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hothan, Sascha A1 - Häßler, Dustin A1 - Pistol, Klaus A1 - Klemmstein, Frank ED - Zehfuß, Jochen T1 - Einfluss der Querdehnungsbehinderung auf das Trag- und Verformungsverhalten von Spannbeton-Hohlplatten N2 - Ziel der Forschung ist die experimentelle und numerische Untersuchung des Brandverhaltens von HC-Platten unter besonderer Berücksichtigung des Einflusses der Querdehnungsbehinderung (seitliche Zwängung). Eine starke Querdehnungsbehinderung der HC-Platten kann in der Praxis aus der Konstruktionsart resultieren, z.B. durch an das Deckenfeld angrenzende steife Treppenhauskerne. Eine teilweise Querdehnungsbehinderung tritt auf, wenn die thermische Ausdehnung lokal brandbeanspruchter HC-Platten durch angrenzende nicht beflammte Deckenbereiche behindert wird. Da bisher keine Untersuchungen zu dieser Fragestellung vorlagen, wurden Großbrandversuche mit Deckenfeldern aus HC-Platten bei unterschiedlichem Grad der Querdehnungsbehinderung durchgeführt. T2 - Symposium "Heißbemessung - Structural Fire Engineering" CY - TU Braunschweig, Germany DA - 22.09.2017 KW - Spannbeton-Hohlplatten KW - Feuerwiderstand KW - Querdehnungsbehinderung KW - Versagensmechanismen PY - 2017 VL - 4 SP - 1 EP - 15 PB - Eigenverlag TU Braunschweig CY - Braunschweig AN - OPUS4-43593 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Adão, Filipe Jorge Santos Ferreira A1 - Rosemarie, Helmerich A1 - Gerrit, Voigt A1 - Laura, Moldenhauer A1 - Neumann, Patrick P. ED - Motavalli, M. ED - Ilki, A. T1 - Humidity monitoring in concrete using Bluetooth Low Energy sensors N2 - The vulnerability of low quality concrete to changing weather conditions is well known. The constant exposure to temperature changes, biological activity, and humidity ends up in damage to buildings and structures which contain this material. It is therefore necessary to take preventive measures to control the extent of the damage done by weathering and possible penetration of adverse chemicals into structures which need public safety. The Federal Institute for Materials Research and Testing (BAM), in cooperation with the small enterprise LinTech GmbH, is working on a project to monitor humidity changes in concrete by analyzing the changes in signal strength (RSSI) from Bluetooth Low Energy sensors. In this paper, we show results which demonstrate the influence of changing water content in concrete on the received RSSI. We observed that as water content in concrete decreases, the received RSSI improves. However, the damping effect is not linearly proportional to water content, rather exponentially proportional. This suggests that changes in the received signal strength are more easily observed when water content in concrete is higher. Finally, we reconstructed a RSSI distribution map using computed tomography. T2 - SMAR 2017 CY - Zurich, Switzerland DA - 13.09.2017 KW - Bluetooth Low Energy Computed Tomography KW - RSSI KW - Concrete KW - Water KW - Monitoring KW - Computed Tomography PY - 2017 UR - http://www.smar-conferences.org/smar/SMAR_2017_Proceedings/papers/153.pdf VL - 2017 SP - 1 EP - 8 CY - Zurich, Switzerland AN - OPUS4-43597 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Qiao, Linan A1 - Völzke, Holger T1 - Influence of impact angle and real target properties on drop test results of cubic containers N2 - Drop test scenarios with cubic containers without impact limiters at interim storage sites or in a final repository have been investigated by numerical simulations. An ideally flat drop is impossible to conduct as a free fall of a container even under laboratory conditions. Dynamic stresses and strains inside the container structure are sensitive to the impact angle. Even very small impact angles cause remarkable changes in the experimental or numerical results when a flat bottom or wall of a container hits a flat target. For drop tests with transport packages the International Atomic Energy Agency (IAEA) regulations define an essentially unyielding target. In contrast, potential accident scenarios for storage containers are derived from site-specific safety analyses or acceptance criteria in Germany. Each interim storage site or repository has a yielding or so-called real target with individual structural and material properties. The real target acts as a kind of impact limiter. A more conservative container design is required if the impact limiting effect of the target is not considered. T2 - ASME 2017 Pressure Vessels and Piping Conference CY - Waikoloa, Hawaii, USA DA - 16.07.2017 KW - Finite element method KW - Simulation KW - Drop test KW - Impact angle KW - Real target KW - Yielding target PY - 2017 SN - 978-0-7918-5802-8 DO - https://doi.org/10.1115/PVP2017-65731 VL - 7 SP - Article UNSP V007T07A039, 1 EP - 9 AN - OPUS4-43631 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Krankenhagen, Rainer T1 - Abschlussbericht des Projektes: IKARUS Infrarot-Kameratechnologie zur berührungslosen Analyse von Rotorblättern unter Hoch-See- (Offshore)-Bedingungen (IKARUS) N2 - Derzeitiger Stand von Wissenschaft und Technik: Die Inspektion der Rotorblätter von Windenergieanlagen (WEA) erfolgt derzeit durch Sichtinspektion von außen und wenn möglich auch von innen. Das die Wartung ausführende Personal muss sich hierfür von der Gondel aus abseilen oder die Inspektion von einer speziellen Plattform aus durchführen. Dazu muss die WEA für die Dauer der Inspektion außer Betrieb gesetzt werden. Kleinere Schäden am Rotorblatt können sofort ausgebessert werden. In Deutschland ist ein zweijähriges Wartungsintervall vorgeschrieben. Begründung/Zielsetzung der Untersuchung: Das bisher angewandte Verfahren der individuellen Nahinspektion aller Rotorblätter lässt nicht ohne weiteres auf den Offshore-Bereich übertragen. Allein der notwendige Umstieg von einem Boot auf eine fest stehende Plattform bei geringem Wellengang von 1 m Wellenhöhe veranschaulicht die Schwierigkeiten. Weitere typische Probleme sind eingeschränkte Zugänglichkeit bei Schlechtwetterlagen, lange Anfahrtswege und das schlecht kalkulierbare Risiko der Seekrankheit. Es besteht daher Bedarf an neuen Inspektionsmethoden, bei denen die WEA nicht direkt begangen werden muss. Ein entsprechendes Verfahren könnte auch im onshore-Bereich eingesetzt werden, um Wartungsintervalle zu optimieren und Stillstandszeiten zu minimieren. Methode: Thermografische Verfahren sind berührungslos und werden bereits zur Rotorblattinspektion eingesetzt, allerdings nur während der Fertigung und dicht am Rotorblatt. Weiterhin ist bekannt, dass Thermografiekameras auch auf Hubschraubern eingesetzt werden, z.B. zur Personensuche. Im Rahmen des Projektes soll untersucht und evaluiert werden, ob Thermografie auf größere Entfernungen zur Untersuchung von Rotorblättern geeignet ist. Gemäß Projektplan sind vor allem Laboruntersuchungen an geeigneten Probekörpern sowie Außenmessungen an WEA geplant. Damit soll das Potenzial der thermografischen Ferninspektion von Rotorblättern evaluiert werden. Ergebnis: 1. Die Untersuchungen an Rotorblattausschnitten mit verschiedenartigen Fehlern im Labormaßstab belegten die Eignung der Thermografie als zerstörungsfreie Prüfmethode für Rotorblätter. 2. Langzeituntersuchungen an einem Teilbereich eines Rotorblatts in einer Freiluftanordnung zeigten, dass messbare thermische Kontraste an inneren Strukturen oder an inneren Fehlern unter verschiedenartigen Wetterbedingungen entstehen können. 3. Bei Messungen an Rotorblättern im montierten Zustand, d.h. an einer intakten WEA, treten entsprechende thermische Kontraste ebenfalls auf. Allerdings ist die Nachweisbarkeit erschwert durch Reflexionen aus der Umwelt sowie durch Wind, der zu charakteristischen thermischen Streifenmustern auf den Rotorblättern führt. Bei Messungen an ruhenden Rotorblättern dominiert der erste Effekt, während der Wind kaum stört. Bei sich drehenden Rotorblättern ist die Situation umgekehrt, störende Reflexionen können korrigiert werden, aber der Wind beeinflusst die thermischen Kontraste beträchtlich, vor allem in nabenfernen Bereichen der Rotorblätter. Schlussfolgerung/Anwendungsmöglichkeit: Eine abschließende Evaluierung der Eignung der Thermografie als Ferninspektionsmethode für WEA-Rotorblätter konnte nicht vorgenommen werden. Ursache hierfür sind sowohl die vielfältigen Störfaktoren bei einer Freiluftmessung als auch das Fehlen einer geeigneten Referenzanlage, an der typische Rotorblattfehler und –defekte während des Betriebs systematisch beobachtet werden können. Die Schlussfolgerung ist daher, dass weitere Forschungsarbeit notwendig ist, um Möglichkeiten und Einsatzgrenzen einer thermografischen Ferninspektion angeben zu können. Eine thermografische Rotorblattinspektion ist unter günstigen Witterungsbedingungen anwendbar und kann wahrscheinlich innere Defekte aufdecken, auch wenn der direkte Nachweis innerhalb des Projektes nicht geführt werden konnte. Wenn ein Rotorblatt-Thermogramm Auffälligkeiten aufweist, vor allem im Vergleich zu den beiden anderen Rotorblättern der gleichen Anlage, ist eine nähere Untersuchung der entsprechenden Stelle zu empfehlen. Das Auftreten solcher Kontraste, deren räumliche Ausdehnung und Ausprägung hängen jedoch von vielfältigen Faktoren ab und sind gemäß jetzigem Kenntnisstand noch nicht voll verstanden. KW - Rotorblattinspektion KW - Ferndiagnose KW - Thermografie KW - meteorologischer Einfluss KW - Zerstörungsfreie Prüfung PY - 2016 UR - https://www.tib.eu/de/suchen/id/TIBKAT%3A870669729/Abschlussbericht-des-Projektes-IKARUS-Infrarot/ DO - https://doi.org/10.2314/GBV:870669729 SP - 1 EP - 121 AN - OPUS4-45833 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mirtsch, Mona ED - Jakobs, K. ED - O'Connor, R.V. T1 - The Role of Conformity Assessment in the Digital Transformation: Focusing on Cybersecurity N2 - Digital transformation and especially the dramatic rise of products and services connected to the Internet of Things raise the questions on how to deal with the increasing risks related to Privacy and Cybersecurity. Presumably, these risks seem to be insufficiently reflected in the European Union’s current regulative system – by being neither part of the traditional definition of a safe product nor part of product-specific vertical or horizontal directives. Certification based on standards as underlying requirements has been identified by policymakers as an instrument to address this issue. The latest European draft regulation aims at increasing security and trust in ICT products and services, and reducing current European market fragmentation with a new Cybersecurity Certification Framework. Based on the results of a qualitative analysis of stakeholder statements on the current proposal on the Cybersecurity Act, this paper discusses elements of the proposed Cybersecurity Certification Framework. As a theoretical background, this paper provides definitions of the terms Safety, IT-security, and Cybersecurity, presents selected Cybersecurity-related standards and provides an outlook on future challenges to Conformity Assessment in the digital transformation. T2 - 23rd EURAS Annual Standardisation Conference "Standards for a Smarter Future" CY - Dublin, Irland DA - 13.06.2018 KW - Conformity Assessment KW - Cybersecurity KW - Certification KW - IT-Security PY - 2018 SN - 978-3-95886-229-6 VL - 2018 SP - 183 EP - 202 PB - Verlagshaus Mainz GmbH Aachen CY - Aachen AN - OPUS4-45686 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Korzen, Manfred ED - Pavese, Alberto T1 - Hybrid fire testing via the substructuring method N2 - Originally introduced in the field of earthquake engineering hybrid testing, i.e. the simultaneous combined application of numerical simulation techniques and execution of experiments, is nowadays used in different areas of experimental analysis. The focus of this paper is on the presentation of the so-called substructuring method as a hybrid method in fire engineering. Motivation are EU standards for fire resistance tests of columns or beams. According to these codes building elements are considered as stand-alone elements whereas in real fires each building element interacts with its adjacent elements. Therefore, to conduct a fire test in a more realistic fashion, the concept of hybrid substructuring as a special experimental technique has been adopted to fire engineering. Due to this concept the entire building, which is exposed to a real fire, is decomposed into two parts. One part is represented by the building element under test in a special furnace, whereas the remaining building environment is simulated by a model, based on the equations of thermomechanics. The paper addresses the historical development of the substructuring method in fire engineering supplemented by presentation of the results of realized fire resistance tests in substructuring mode on different types of specimens. T2 - 7th International Conference on Advances in Experimental Structural Engineering CY - Pavia, Italy DA - 6 September 2017 KW - Hybrid testing PY - 2017 SN - 978-88-85701-01-4 SP - 945 EP - 947 PB - EUCENTRE Foundation CY - Pavia, Italy AN - OPUS4-45760 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Talebi, Elnaz A1 - Korzen, Manfred A1 - Espinós, A. A1 - Hothan, Sascha ED - Albero, Vicente T1 - The effect of damage location on the performance of seismically damaged concrete filled steel tube columns at fire N2 - In this paper, a nonlinear three-dimensional finite element (FE) model was developed and validated to study the effect of seismic damage location on the response of concrete filled tube (CFT) columns at fire after earthquakes. Three analyses were conducted consecutively in the modelling, namely, cyclic, thermal and structural. Results of the cyclic loading analysis comprising residual deformations were applied as the Initial condition to the thermal-stress model, replicating the seismic performance of column. Following, a nonlinear sequentially coupled-thermal stress Analysis was carried out to investigate the fire response of CFT columns after the seismic event. Three damage scenarios were contemplated, considering any possible potential damages that could be generated by the earthquake loading on CFT columns. The accuracy of the proposed FE model was examined by comparing the numerical results with that of available tests on fire and cyclic loading. By means of the validated model, the performance of damaged CFT columns was then investigated under fire after earthquakes. The level of damage was assumed as a high damage level, presuming that the column reached 50% of ist lateral resistance while still maintaining its overall stability after the earthquake. The results were presented broadly, including the axial deformation history as well as the fire resistance time for CFT columns. To have a comprehensive insight on the influence of damage location in columns, the fire response of damaged specimens was compared with that of an intact one. T2 - 12th International Conference on Advances in Steel-Concrete Composite Structures (ASCCS 2018) CY - Valencia, Spain DA - 27.06. 2018 KW - Fire after earthquake KW - Concrete filled tube (CFT) column KW - Finite element model KW - Seismically damaged column KW - Damage location KW - Fire performance PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-457694 SN - 978-84-9048-601-6 DO - https://doi.org/10.4995/ASCCS2018.2018.8534 SP - 835 EP - 842 PB - Editorial Universitat Politècnica de València CY - València AN - OPUS4-45769 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Romero-Navarrete, José A. A1 - Otremba, Frank A1 - Lozano Guzmán, A. A. T1 - Simulation of liquid cargo – vehicle interaction under lateral and longitudinal accelerations N2 - Amongst the vehicle parameters influencing road safety, the carried cargo plays a critical role in the case of a liquid cargo, posing rollover risk and affecting the available friction forces for braking. While the lateral sloshing of the cargo within the vehicle´s compartments, can be excited when the vehicle negotiates a turn, the longitudinal motion of the cargo derives from changes of speed. The combination of both types of perturbations occurs when the vehicle brakes while negotiating a turn. In this paper, a two-pendulum formulation is used to simulate the lateral and longitudinal behavior of a vehicle when negotiating a braking in a turn maneuver. The suspension forces are thus calculated as the linear superposition of both models. Results suggest that the vehicle roll stability is affected by the cargo sloshing, with increments on the order of 100% in the lateral load transfer, for a 50% filled tank. On the other hand, the dispersion of the travelling speed also affects the lateral stability of such type of vehicles, as a function of the dispersion of the vehicle´s travelling speed. T2 - The 9th International Conference on Computational Methods (ICCM2018) CY - Rome, Italy DA - 06.08.2018 KW - Sloshing cargo KW - Road tankers KW - Pendulum analogy KW - Braking in a turn KW - Lateral load transfer ratio PY - 2018 SP - 88 EP - 102 PB - Scientech Publisher LLC AN - OPUS4-45821 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Maiwald, Michael A1 - Klaer, R.-H. A1 - Wagner, A. T1 - 100 % Digital in der Prozessindustrie - Tutzing-Symposion Teil 3: Intelligente Nutzung von Daten und Bausteinen der Digitalisierung N2 - Digitalisierung und Industrie 4.0 verändern komplette Geschäftsmodelle, heben neue Effizienzpotenziale und stärken die Wettbewerbsfähigkeit. Auf dem 57. Tutzing-Symposion vom 15.–18.04.2018 wurde mit Vorträgen und Kreativworkshops erkundet, welche speziellen Anforderungen die Prozessindustrie hat, welche digitalen Innovationen bereits umgesetzt wurden und wo noch Handlungsbedarf besteht. Ein Workshop befasste sich mit den Themenfeldern Datenkonzepte, Datenanalyse, Big Data und künstliche Intelligenz. Es geht nicht um die Digitalisierung von heute. Im Angesicht der wachsenden Digitalisierung unserer Prozesse stellt sich die Frage, ob wir den Prozess wirklich gut kennen. Ob alle Verfahrensschritte detailliert hinterlegt wurden. Nur mit einem heuristischen Ansatz kann das vorhandene Wissen nicht digitalisiert werden. Sehr schnell werden die Mechanismen eines Massenmarktes mit denen einer Nische verwechselt. Nicht jeder Mechanismus, den wir von großen Suchmaschinen oder Einkaufsportalen kennen, gibt uns einen Hinweis auf Nutzen und Verfügbarkeit für die Prozess- oder pharmazeutische Industrie. Eine gute Analyse der Anforderungen in der Zukunft mit einem Abgleich der derzeitigen technischen Möglichkeiten ist Voraussetzung für eine Verbesserung der derzeitigen digitalen Umsetzung. Dabei ist es sinnvoll unkonventionelle Methoden einzusetzen. KW - Digitalisierung KW - Prozessindustrie KW - Tutzing-Symposion KW - Datenkonzepte KW - Datenanalyse KW - Big Data KW - Künstlicher Intelligenz PY - 2018 UR - https://www.chemanager-online.com/themen/produktion/100-digital-der-prozessindustrie SN - 1436-2597 VL - 21 IS - 9 SP - 6 EP - 9 PB - Wiley-VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-45861 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schönhals, Andreas A1 - Zorn, R. T1 - Elastic scans on highly permeable glassy polynorbornenes N2 - Experimantal Report to proposal 13603: Elastic Scans on Highly Permeable Glassy Polynorbornenes are measured by neutron backscatering and discuused KW - Neutron backscattering KW - Glassy polynorbornenes PY - 2018 SP - 1 EP - 2 CY - Garching (MLZ) AN - OPUS4-45436 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ziegler, Mathias A1 - Thiel, Erik A1 - Ahmadi, Samim T1 - Lock-in Thermography using High-Power Laser Sources N2 - Optical lock-in thermography is a completely contactless and very sensitive NDT technique. As an optical source of energy, incandescent lamps are most commonly used because they are relatively inexpensive and offer high irradiances at the test specimen. However, they are strongly restricted by their low modulation bandwidth with a maximum modulation frequency of only about 1 Hz. The use of high-power kilowattclass laser sources, e.g. diode laser arrays, pushes this constraint beyond 100 Hz. This allows for the exploration of the near-surface region of metals and layer systems with better and more accurate penetration depth and depth resolution. Moreover, these lasers are virtually free of any additional thermal radiation that could interfere with the “true” thermal response emitted from the heated sample. In turn, they can be easily used in a one-sided test configuration. We present current activities with kilowatt-class highpower laser sources for advanced lock-in thermography and focus on the application of laser arrays that offer a very high irradiation strength over a large sample area beyond the mentioned advantages. T2 - 12th European Conference on Non-destructive Testing CY - Gothenburg, Sweden DA - 11.06.2018 KW - Thermography KW - Laser Thermography KW - Lock-in Thermography PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-454466 UR - http://cdn.ecndt2018.com/wp-content/uploads/2018/05/ecndt-0139-2018.pdf SN - 978-91-639-6217-2 SP - ECNDT-0139-2018,1 EP - 7 AN - OPUS4-45446 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Burgholzer, P. A1 - Berer, T. A1 - Ziegler, Mathias A1 - Thiel, Erik A1 - Ahmadi, Samim A1 - Gruber, J. A1 - Mayr, G. A1 - Hendorfer, G. T1 - Blind structured illumination as excitation for super-resolution photothermal radiometry N2 - Using an infrared camera for radiometric imaging allows the contactless temperature measurement of multiple surface pixels simultaneously. From the measured surface data, a sub-surface structure, embedded inside a sample or tissue, can be reconstructed and imaged when heated by an excitation light pulse. The main drawback in radiometric imaging is the degradation of the spatial resolution with increasing depth, which results in blurred images for deeper lying structures. We circumvent this degradation with blind structured illumination, combined with a non-linear joint sparsity reconstruction algorithm. The ground-breaking concept of super-resolution can be transferred from optics to thermographic imaging. T2 - Conference QIRT 2018 CY - Berlin, Germany DA - 25.06.2018 KW - Thermography KW - Laser thermography KW - Super resolution PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-454506 SN - 978-3-940283-94-8 DO - https://doi.org/10.1080/17686733.2019.1655247 SP - We.3.A.2, 1 EP - 7 AN - OPUS4-45450 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lugovtsova, Yevgeniya A1 - Bulling, Jannis A1 - Prager, Jens A1 - Boller, C. T1 - Efficient modelling of guided ultrasonic waves using the Scaled Boundary FEM towards SHM of composite pressure vessels N2 - The Scaled Boundary Finite Element Method (SBFEM) is a semi-analytical method that shows promising results in modelling of guided ultrasonic waves. Efficiency and low computational cost of the method are achieved by a discretisation of the boundary of a computational domain only, whereas for the domain itself the analytical solution is used. By means of the SBFEM different types of defects, e.g. cracks, pores, delamination, corrosion, integrated into a structure consisting of anisotropic and isotropic materials can be modelled. In this contribution, the SBFEM is used to analyse the propagation of guided waves in a structure consisting of an isotropic metal bonded to anisotropic carbon fibre reinforced material. The method allows appropriate wave types (modes) to be identified and to analyse their interaction with different defects. Results obtained are used to develop a structural health monitoring system for composite pressure vessels used in automotive and aerospace industries. T2 - 9th European Workshop on Structural Health Monitoring (EWSHM) CY - Manchester, UK DA - 10.07.2018 KW - Structural Health Monitoring KW - Pressure tanks KW - Hydrogen storage KW - Finite Element Modelling KW - Composites PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-454859 SP - 1 EP - 7 AN - OPUS4-45485 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maierhofer, Christiane A1 - Krankenhagen, Rainer A1 - Röllig, Mathias A1 - Heckel, Thomas A1 - Brackrock, Daniel A1 - Gaal, Mate T1 - Quantification of impact damages in CFRP and GFRP structures with thermography and ultrasonics N2 - The extent of damage caused by impacts in fibre reinforced composites depends on the energy of the impacts, on the velocity and the shape of the impacting body, on the material and structure of the composite and on the geometry of the structure. Here, mainly the thickness of the component is essential. The non-destructive evaluation of these damages can be carried out using both ultrasound and active thermography methods. A comparison of the detection sensitivity of these methods for the different damages is carried out in this paper depending on the fibre composite material used (CFRP and GFRP), the thickness of the material and the impact energy. The NDT methods used after the damage are supplemented by thermographic measurements with high temporal resolution, which were already recorded during the impact. T2 - 14th Quantitative InfraRed Thermography Conference CY - Berlin, Germany DA - 25.06.2018 KW - Active thermography KW - Passive thermography KW - Ultrasonics KW - CFRP KW - GFRP KW - Impact PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-454952 UR - http://www.qirt.org/archives/qirt2018/papers/126.pdf DO - https://doi.org/10.21611/qirt.2018.126 SP - 933 EP - 940 PB - DGZfP e. V. AN - OPUS4-45495 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN T1 - Improvement of effectiveness of in-service inspection in nuclear power plants (IAEA-TECDOC-1853) N2 - This publication represents a consensus among experts drawn from the IAEA and global practitioners to compile a set of common or good individual practices for use at nuclear power plants to improve ISI effectiveness. It sets forth a number of strategies and practices for improving the effectiveness of ISI and investigates the role of ISI in maintaining or improving safety at plants and the relationship of ISI improvement to cost. Strategies for improving ISI effectiveness are discussed, with consideration given to the entire framework of ISI, including effective selection of the proper inspection scope, inspection interval and NDE efficiency. This publication is an update of the publication IAEA-TECDOC-1400, Improvement of In-service Inspection in Nuclear Power Plants, which was published in 2004. It takes into account new techniques and technologies for qualification processes for methodologies, equipment, procedures and personnel as well human factors in NDE inspections. KW - NDT KW - Nuclear power KW - Human factors KW - In-service inspection KW - ISI effectiveness KW - Non-destructive testing PY - 2018 UR - https://www-pub.iaea.org/MTCD/Publications/PDF/TE-1853web.pdf SN - 978-92-0-106618-3 SN - 1011-4289 VL - 1853 SP - 1 EP - 85 PB - International Atomic Energy Agency CY - Vienna AN - OPUS4-46163 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias T1 - Machining with niobium carbide based tools N2 - The present work deals with Niobcarbid (NbC). Strategic reflections on tungsten carbide and more and more stringent toxicological restrictions for cobalt associated for both with spiraling stock market prices have attracted recently some attention for Niobium carbide as a substitute for tungsten carbide in machining. T2 - 59. Tribologie-Fachtagung CY - Goettingen, Germany DA - 24.09.2018 KW - Hard tungsten KW - Semi-finishing KW - Niobium carbide KW - Friction KW - Wear KW - NbC KW - Hard metal KW - Cobalt KW - Nickel KW - Fe3Al PY - 2018 SN - 978-3-9817451-3-9 SP - 48/1 EP - 48/11 AN - OPUS4-46170 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Huang, S. A1 - Vleugels, J. A1 - Cannizza, E. A1 - Woydt, Mathias A1 - Liu, Z. A1 - Mohrbacher, H. T1 - Niobium carbide based cermets with secondary carbide and carbonitride addition N2 - In this study, the influence of Ni binder content and carbide/carbonitride additions on the microstructure and mechanical properties of NbC-Ni matrix cermets were investigated. T2 - WORLDPM2018 CY - Beijing, China DA - 16.09.2018 KW - Cermet KW - Niobium carbide KW - Carbonitride KW - Sintering KW - Mechanical properties PY - 2018 SP - Part 5, 801 EP - 809 AN - OPUS4-46201 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Uhlmann, E. A1 - Meier, P. A1 - Hinzmann, D. A1 - Kropidlowski, K. A1 - Prasol, L. A1 - Woydt, Mathias T1 - Dry turning with niobium carbide based tools N2 - In the present work it was shown that Niobium carbide (NbC) offers a competitive profile compared to tungsten carbide (WC) as cutting material regarding ist wear resistance preferably in metal cutting processes. T2 - WORLDPM 2018 CY - Beijing, China DA - 16.09.2018 KW - Turning KW - Semi-finishing KW - Niobium carbide KW - Tungsten carbide KW - Iron-based alloys KW - Aluminum PY - 2018 SP - Part 5, 775 EP - 784 AN - OPUS4-46203 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Huang, S. A1 - Vleugels, J. A1 - Mohrbacher, H. A1 - Cannizza, E. T1 - Tailoring the functional profile of niobium carbide (NbC) as cutting tool materials and for wear protection N2 - In the present work it was shown that the properties of NbCx, like micro-hardness, hot-hardness, sliding wear resistance, elastic modulus and toughness can be tailored by the C/Nb ratio, the addition of secondary carbides and the type of binder. T2 - WORLDPM2018 CY - Beijing, China DA - 16.09.2018 KW - Niobium carbide KW - Properties KW - Wear KW - Machining PY - 2018 SP - Part 5, 785 EP - 795 AN - OPUS4-46204 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wu, Cheng-Chieh A1 - Kadoke, Daniel A1 - Fischer, Michael A1 - Kohlhoff, Harald A1 - Weisbrich, S. A1 - Neitzel, F. ED - Pastramă, Ştefan Dan ED - Constantinescu, Dan Mihai T1 - A small-scale test bridge for measurement- and model-based structural analysis N2 - To examine the capability to detect and localise damage using the Measurement- and Model-based Structural Analysis (MeMoS), a small-scale truss bridge (1520 mm × 720 mm × 720 mm) made of aluminium profiles is built as a test specimen for this purpose. The truss frame of the test bridge is made of aluminium profiles with a sophisticated design of the cross-sectional area. In comparison, with solid profiles, only a fraction of the material is needed to produce the profiles, while their bending resistance decreases slightly. The profiles are built into a truss frame by connecting them by means of fastening sets made of steel. The bridge model is mounted on four steel bearings which each of them consist of a cylinder arranged between two plates. Fixed bearings are made by holding onto one end of the bridge. The bridge is subjected by an external load by placing a heavy object beneath it. At the same time, measurements can be conducted below the bridge. Therefore, the bridge specimen is elevated by attaching it on a pedestal with four columns. Damages can be induced by loosening the fastening pieces. T2 - 35th Danubia-Adria Symposium on Advances in Experimental Mechanics CY - Sinaia, Romania DA - 25.09.2018 KW - Adjustment calculation KW - Finite element method KW - Damage detection and localisation KW - Structural analysis KW - Photogrammetry PY - 2018 SN - 978-606-23-0874-2 SP - 23 EP - 24 PB - PRINTECH CY - Bukarest AN - OPUS4-46116 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Patrick P. A1 - Hüllmann, Dino A1 - Bartholmai, Matthias ED - Pastramă, D. Ş ED - Constantinescu, D. M. T1 - Concept of a gas-sensitive nano aerial robot swarm for indoor air quality monitoring N2 - In industrial environments, airborne by-products such as dust and (toxic) gases, constitute a major risk for the worker’s health. Major changes in automated processes in the industry lead to an increasing demand for solutions in air quality management. Thus, occupational health experts are highly interested in precise dust and gas distribution models for working environments. For practical and economic reasons, high-quality, costly measurements are often available for short time-intervals only. Therefore, current monitoring procedures are carried out sparsely, both in time and space, i.e., measurement data are collected in single day campaigns at selected locations only. Real-time knowledge of contaminant distributions inside the working environment would also provide means for better and more economic control of air impurities. For example, the possibility to regulate the workspace’s ventilation exhaust locations can reduce the concentration of airborne contaminants by 50%. To improve the occupational health and safety of (industrial) workplaces, this work aims for developing a swarm of gas-sensitive aerial nano robots for monitoring indoor air quality and for localizing potential emission sources. T2 - 35th Danubia-Adria Symposium on Advances in Experimental Mechanics CY - Sinaia, Romania DA - 25.09.2018 KW - Mobile Robot Olfaction KW - Swarm KW - Nano aerial robot KW - Gas sensing PY - 2018 SN - 978-606-23-0874-2 SP - 139 EP - 140 PB - PRINTECH CY - Bukarest AN - OPUS4-46137 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hüllmann, Dino A1 - Kohlhoff, Harald A1 - Erdmann, Jessica A1 - Neumann, Patrick P. ED - Pastramă, D. Ş. ED - Constantinescu, D. M. T1 - Control of a spherical parallel manipulator with three degrees of freedom N2 - In robotic applications, it is often necessary to orient a sensor quickly. Spherical parallel manipulators (SPM) are well suited for this purpose since they offer superior dynamics and structural stiffness as compared to serial manipulators. To control them, however, the kinematic equations have to be known. In this paper, a SPM with three degrees of freedom and the kinematic equations describing its mechanical properties are presented. T2 - 35th Danubia-Adria Symposium on Advances in Experimental Mechanics CY - Sinaia, Romania DA - 25.09.2018 KW - Spherical parallel manipulator KW - Control KW - 3 DoF PY - 2018 SN - 978-606-23-0874-2 SP - 159 EP - 160 PB - PRINTECH CY - Bukarest AN - OPUS4-46141 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erning, Johann Wilhelm A1 - Kamaraj, Abinaya T1 - Influence of electrochemically active fluids on the corrosion risk of stainless steel N2 - The influence of electrochemically produced disinfectants on the corrosion behaviour of stainless steel is investigated. Special attention is given to crevice corrosion. T2 - Eurocorr 2018 CY - Krakau, Poland DA - 10.09.2018 KW - Disinfection KW - Crevice corrosion KW - Stainless steel PY - 2018 SP - 1 EP - 5 AN - OPUS4-46126 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koclega, Damian A1 - Radziszewska, A. A1 - Kranzmann, Axel T1 - The influence of the aggressive environments on the Inconel 686 coating in high-temperature corrosion experiments N2 - This work presents the microstructure and chemical composition of oxide scales created on Ni – base coating after corrosion experiments in aggressive gases and ashes. The Inconel 686 coating applied on the low carbon steel 13CrMo4-5 was performed by a CO2 laser cladding process. The experiments were carried out in oxidizing gas atmospheres containing O2, COx, SOx. The second Variation of corrosion experiments were performed in a reducing atmosphere with ashes containing elements such as: Na, Cl, Ca, Si, C, Fe, Al etc. After 240 h and 1.000 h corrosion experiments the oxide scales on the substrate and overlay were created in both cases. The sulfur compounds were found on the top of the coating surface (EPMA) and also higher contents of silica compounds were revealed on specimens covered by ashes during the experiments. The microstructure and chemical composition of the clad and scales were investigated by means of a light microscope and an electron microscope (SEM)equipped with an EDS detector. T2 - 50. Kraftwerkstechnisches Kolloquium CY - Dresden, Germany DA - 23.10.2018 KW - Nickel based coatings KW - Inconel 686 KW - High temperature corrosion PY - 2018 SP - 599 AN - OPUS4-46590 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kapa, Thomas A1 - Gmiha, Wajdi A1 - Heidmann, G. A1 - Vaterrodt, K. A1 - Hicke, Konstantin T1 - Verteilte faseroptische Zustandsüberwachung von Mittel- und Hochspannungskabeln N2 - Verteilte faseroptische Sensorik eignet sich sehr gut für eine Zustands- und Gefährdungsüberwachung von ausgedehnten Hochspannungskabelinstallationen. Basierend auf der Messung von verschiedenen faseroptischen Rückstreueffekten in der Sensorfaser lassen sich ortsaufgelöste Profile von Messgrößen wie Temperatur, Dehnung oder Vibrationen erzielen. Hier demonstrieren wir die Leistungsfähigkeit verschiedener faseroptischer Sensorikansätze bezüglich dieser Größen anhand von Experimenten u.a. an einem Mittelspannungskabel. Des Weiteren zeigen wir, wie die Verwendung von verschiedenen Sensorkabeltypen mit unterschiedlicher Applikation auf der Kabeloberfläche die Messergebnisse bei einem Biegeversuch beeinflussen und schlussfolgern damit auf die für die Einbettung in Kabeln geeigneten Sensoren. T2 - VDE Fachtagung Hochspannungstechnik CY - Berlin, Germany DA - 12.11.2018 KW - Verteilte Fasersensorik KW - Hochspannung KW - Monitoring PY - 2018 SN - 978-3-8007-4807-5 SN - 0341-3934 VL - 2018 SP - 1 EP - 6 PB - VDE Verlag GmbH CY - Berlin AN - OPUS4-46620 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kotschate, Daniel A1 - Wendland, Saskia A1 - Gaal, Mate T1 - Airborne testing of molded polymer compounds N2 - Modern and energy-efficient materials are essential for innovative designs for aerospace and automotive industries. Current technologies for rapid manufacturing such as additive manufacturing and liquid composite moulding by polymer Extrusion allow innovative ways of creating robust and lightweight constructions. Commercially available printing devices often use polylactide (PLA) or acrylonitrile butadiene styrene (ABS) as raw material. Therefore, parameters like the infill ratio, influencing the ability to resist mechanical stress, may have a beneficial impact on the lifetime of components. These manufacturing technologies require a good knowledge about materials and even adapted non-destructive testing technologies and methods. Airborne ultrasonic testing has beneficial advantages for testing those lightweight constructions. It is a contact-free testing method, which does not require a liquid couplant. Therefore, it allows fast test cycles without any unwanted alternations of the material properties due to interactions with any coupling liquid. This contribution deals with the characterisation of printed specimens based on PLA by using airborne ultrasound and presents the current edge of non-destructive testing and evaluation using airborne ultrasonic transducers. The specimens, manufactured by polymer extrusion, are printed as thin plates. The infill ratio, as well as the material thickness, were varied to model density imperfections with different geometric shapes and properties. For better understanding of the limits of airborne ultrasonic testing in transmission, we compared own-developed transducers based on different physical principles: on ferroelectrets, on the thermoacoustic effect, as well as a new type of transducers based on gas discharges. T2 - 10th International Symposium on NDT in Aerospace CY - Dresden, Germany DA - 24.10.2018 KW - Air-coupled ultrasonic testing KW - Polymer KW - Plasma acoustics KW - Gas discharges KW - Atmospheric pressure plasma PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-465609 VL - 168 SP - Th.6.C.1, 1 EP - 7 AN - OPUS4-46560 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Falkenberg, Rainer A1 - Charmi, Amir T1 - Virtual-lab-based determination of a macroscopic yield function for additively manufactured parts N2 - Diese Arbeit beschreibt eine Methode für die Ermittlung einer Fließfunktion für additiv gefertigte Bauteile des Werkstoffs S316L. Ein Kristallplastizitätsmodell wird zunächst mit experimentellen Daten kalibriert. Anschließend werden mit diesem Modell sogenannte virtuelle Experimente durchgeführt, die die prozeßspezifische Mikrostruktur in Form von kristallographischen und morphologischen Texturen miteinbeziehen. Diese Simulationen werden mit einem representativen Volumenelement (RVE) durchgeführt, das aus EBSD/CT-Scans an additiv gefertigten Proben generiert wurde und daher die Kornstruktur und Kristallorientierungen enthält. Die virtuellen Experimente werden durchgeführt, um anhand der damit erhaltenen Fließpunkte eine anisotrope Barlat-Fließfunktion zu bestimmen. Dieser skalenübergreifende Ansatz ermöglicht die Simulation großer Strukturen, für die die Anwendung eines Kristallplastizitätsmodells numerisch zu teuer wäre. N2 - This work presents a method for the yield function determination of additively manufactured parts of S316L steel. A crystal plasticity model is calibrated with test results and used afterwards to perform so-called virtual experiments, that account for the specific process-related microstructure including crystallographic and morphological textures. These simulations are undertaken on a representative volume element (RVE), that is generated from EBSD/CT-Scans on in-house additively manufactured specimen, considering grain structure and crystal orientations. The results of the virtual experiments are used to determine an anisotropic Barlat yield function, that can be used in a macroscopical continuum-sense afterwards. This scale-bridging approach enables the calculation of large-scale parts, that would be numerically too expensive to be simulated by a crystal plasticity model. T2 - 3. Tagung des DVM-Arbeitskreises Additiv gefertigte Bauteile und Strukturen CY - Berlin, Germany DA - 07.11.2018 KW - Additive manufacturing KW - Scale-bridging KW - Crystal plasticity KW - Virtual experiments KW - Anisotropy PY - 2018 SN - 2509-8772 SP - 153 EP - 158 PB - DVM CY - Berlin AN - OPUS4-46570 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stamenkovic, V. A1 - Kapa, Thomas A1 - Felsheim, F. A1 - Plath, R. T1 - Dielektrische Diagnose von 110kV-Gasaußendruckkabelprüflingen unter Betriebsbedingungen mit faseroptischer Temperaturerfassung N2 - Es wurde ein Messaufbau realisiert, der die Betriebsedingungen von hydraulisch- pneumatischen Gasdruckkabelsystemen nachbildet und in dieser Veröffentlichung vorgestellt. Mit seiner Hilfe können im Labor diagnostische Messungen und beschleunigte Alterung der Isolierung bei variablen Temperaturen, Druckstufen, Spannungen und Frequenzen durchgeführt werden. Zur Temperatureinstellung wurde im Messaufbau eine Kurzschlussschleife verwendet, die stabile Heizströme über 700 A bei 50 Hz ermöglicht. Der Prüfspannungsbereich während der Verlustfaktor- und Teilentladungsmessungen lag zwischen 1 kV bis 25 kV mit einem Frequenzbereich zwischen 0,1 Hz bis 60 Hz. Um die örtliche und zeitlich lastabhängige Temperatur entlang des Messbelags bestimmen zu können, wurde eine optische Faser (Loose tube) um den Prüfling gewickelt, so dass eine ortsaufgelöste Temperaturermittlung über den Prüflingsmantel erreicht wurde. Aus den erhaltenen Temperaturmessdaten wurde ein einphasiges, planares thermisches Modell erzeugt, das das thermische Verhalten des Prüflings in Abhängigkeit von Laststrom, Raumtemperatur und Materialdaten nachbildet. Dieses wurde mit den aufgenommenen Messdaten verglichen. Aus den Erkenntnissen des einphasigen thermischen Modells soll ein dreiphasiges Modell entstehen, mit dessen Hilfe die Diagnosetemperatur und das Abkühlverhalten von erdverlegten Gasdruckkabeln abgeschätzt werden können. Dadurch kann zukünftig der Temperatureinflusses bei der Interpretation von Vor-Ort-Messungen hinzugezogen werden. T2 - VDE Fachtagung Hochspannungstechnik CY - Berlin, Germany DA - 12.11.2018 KW - Temperatur KW - Fasersensorik KW - Hochspannung PY - 2018 SN - 978-3-8007-4807-5 VL - 2018 SP - 1 PB - VDE Verlag GmbH CY - Berlin AN - OPUS4-46617 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Pérez Alonso, M. A1 - Albarrán Sanz, J. A1 - Dinkel, M. A1 - Heckel, Thomas A1 - Kotschate, Daniel A1 - Cabeza, Sandra A1 - Senaneuch, J. A1 - Heikkila, I. A1 - Toscanelli, O. T1 - A novel approach for rating fatigue-initiating inclusions in highly demanding steel (INCAFAT) N2 - INCAFAT project aimed to improve existing fatigue damage models by establishing the most suitable combination of measurement techniques to characterise harmful inclusion populations in highly demanding steels. The different inclusion assessments carried out confirm that, chemical composition, secondary metallurgy and manufacturing route affect content, nature, size and shape of inclusions. According to the FEM model, inclusions produce an alteration of the stress field in their surrounding region, which can promote a fatigue failure. Experimental work on fatigue testing has demonstrated that depending on the stressed direction fatigue failures in highly demanding steels could be produced by different types of inclusions. Fractography analyses confirmed that meso-inclusions harmful in fatigue cannot be rated by standard methods, nor 10 MHz ultrasonic testing (macro) or micro-cleanness assessments. The necessity of rating these meso-inclusions has led to critical evaluation of Extreme Value Analysis according to ASTM E2283-08 and the development of high frequency immersion ultrasonic testing. EVA methodology based on inclusion width can be applied reliably when principal stress is parallel to the rolling direction. On the contrary, if inclusions are testing in the elongated directions its fails. On the other hand, the guidelines and recommendations for high frequency ultrasonic testing have been compiled in a new European standard draft. This method based on focal beam probes and high-resolution devices is able to provide information on meso-inclusion distribution. KW - Material characterisation KW - Non-destructive testing KW - Ultrasonic testing KW - Cleanliness PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-479219 UR - https://publications.europa.eu/en/publication-detail/-/publication/6bd25206-316a-11e8-b5fe-01aa75ed71a1/language-en/format-PDF/source-68610160 SN - 978-92-79-76985-6 DO - https://doi.org/10.2777/473350 SN - 1831-9424 SN - 1018-5593 SP - 1 EP - 154 AN - OPUS4-47921 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Vogl, Jochen A1 - Yim, Y.-H. A1 - Lee, K.-S. A1 - Goenaga-Infante, H. A1 - Malinovskiy, D. A1 - Vocke, R. D. A1 - Murphy, K. A1 - Nonose, N. A1 - Rienitz, O. A1 - Noordmann, J. A1 - Näykki, T. A1 - Sara-Aho, T. A1 - Ari, B. A1 - Cankur, O. T1 - CCQM-P134 Pb isotope amount ratios and delta-values in bronze N2 - Isotope amount ratios (hereafter referred to as simply isotope ratios) are proving useful in an ever increasing array of applications that range from studies unravelling transport processes, to pinpointing the provenance of specific samples as well as trace element quantification by using isotope dilution mass spectrometry (IDMS). These expanding applications encompass fields as diverse as archaeology, food chemistry, forensic science, geochemistry, medicine and metrology. However, to be effective tools, the isotope ratio data must be reliable and traceable to enable the comparability of measurement. The importance of traceability and comparability in isotope ratio analysis has already been recognized by the Inorganic Analysis Working Group (IAWG) within the CCQM. Three pilot studies have focused on the quality of isotope ratio determinations (P48 “U isotope ratios in urine”, P75 “stable isotopes in Methionine”, P105 “87Sr/86Sr in wine”). Moreover, isotope ratio measurements are fundamental to IDMS amount of substance determinations. For example, when Pb quantification using IDMS is undertaken, this requires the measurements of Pb isotope ratios. While the requirements for isotope ratio accuracy and precision in the case of of IDMS are generally quite modest, “absolute” Pb isotope ratio measurements for geochemical age dating and source rock characterization as well as forensic provenance and fingerprinting studies require Pb isotope ratio measurements of the highest quality. To support present and future CMCs on isotope ratio determinations, a Key Comparison was urgently needed. Therefore, it was decided at the IAWG meeting in Paris in April 2011 that a Key Comparison on the determination of Pb isotope ratios in a pure Pb solution and in a bronze sample should be organized and accompanied by a pilot study. Measuring Pb isotope amount ratios in a pure Pb solution, while seemingly straight forward, rigorously tests the ability of analyst to correct for any instrumental effects (such as mass discrimination and blank correction) on the measured ratios. Pb, present in trace amounts in a metal matrix sample (e.g. Pb in bronze), provides a real world test of the whole chemical and instrumental procedure, from chemical separation and sample purification to analysis and subsequent correction of appropriate instrumental effects on the separated samples. A suitable bronze material with a Pb mass fraction between 10 and 100 mg·kg-1 was available at BAM. A high purity solution of Pb with a mass fraction of approximately 100 mg·kg-1 was also available. By comparing the Pb isotope ratio results obtained for the bronze sample with the Pb isotope ratio results from the Pb solution, potential biases arising from the processing of the bronze sample could be effectively identified and separated from the instrumental effects arising from the measurement and data processing protocol. KW - Isotope ratio KW - Delta value KW - Molar mass KW - Measurement uncertainty KW - Traceability PY - 2017 UR - https://www.bipm.org/wg/CCQM/IAWG/Allowed/IAWG_Pilot_Studies/CCQM-P134.pdf SP - 1 EP - 42 PB - BIPM (Bureau International des Poids et Mesures) CY - Paris AN - OPUS4-47709 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Kern, Simon A1 - Wander, Lukas A1 - Meyer, Klas A1 - Guhl, Svetlana A1 - Gottu Mukkula, A. R. A1 - Holtkamp, M. A1 - Salge, M. A1 - Fleischer, C. A1 - Weber, N. A1 - Engell, S. A1 - Paul, Andrea A1 - King, R. A1 - Maiwald, Michael T1 - Raw data of pilot plant runs for CONSENS project (Case study 1) N2 - In case study one of the CONSENS project, two aromatic substances were coupled by a lithiation reaction, which is a prominent example in pharmaceutical industry. The two aromatic reactants (Aniline and o-FNB) were mixed with Lithium-base (LiHMDS) in a continuous modular plant to produce the desired product (Li-NDPA) and a salt (LiF). The salt precipitates which leads to the formation of particles. The feed streams were subject to variation to drive the plant to its optimum. The uploaded data comprises the results from four days during continuous plant operation time. Each day is denoted from day 1-4 and represents the dates 2017-09-26, 2017-09-28, 2017-10-10, 2017-10-17. In the following the contents of the files are explained. KW - Process Analytical Technology KW - Multivariate Data Analysis KW - Nuclear Magnetic Resonance KW - Near Infrared Spectroscopy KW - Continuous Manufacturing KW - CONSENS PY - 2018 DO - https://doi.org/10.5281/zenodo.1438233 PB - Zenodo CY - Geneva AN - OPUS4-48063 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krüger, Simone A1 - Friedrich, Jörg A1 - Hidde, Gundula A1 - Farag, Zeinab R. A1 - Moustapha, Moustapha E. A1 - Azzam, Maged M. T1 - Promotion of adhesion of green flame retardant coatings onto polyolefins by depositing ultra-thin plasma polymer films: A critical review N2 - Various methods have been used for introducing fire retardant additives into polymers. Deposition of thick fire retardant coatings directly onto polymer substrates is an alternative technique. An important Advantage of the coating technique is the preservation of the physical and chemical integrity of the polymer material. Moreover, the fire retardancy of the polymer materials can be achieved following their production. Suitable coating materials are inorganics, intumescent, char-forming, oxygendiluting, and cooling or radical quenching layers. The most important problem is to achieve sufficient coating thickness to withstand the direct attack of flame and to protect the polymer bulk from pyrolysis, otherwise blistering of coating, caused by emitted pyrolysis gases, is often observed. To avoid blistering of coating, the adhesion between polyolefin Substrate and fire retardant coating has to be extraordinarily high. In order to achieve such a high level of adhesion, the polymer surface has to be modified with adhesion-promoting functional groups. The deposition of thin plasma polymers as adhesion-promoting layers with NH2, OH or COOH groups has been the most suited method. These functional groups are able to form covalent bonds and other interactions between the fire-resistant coating and the plasma-modified polyolefin substrate. Additionally, the plasma polymer counteracts the strong mechanical stresses in the laminate on exposure to high temperatures by its flexibility. The thick fire retardant coatings were chosen based on “green” ecological aspects to avoid flame-initiated emission of toxic or corrosive gases and remains of toxic char. KW - Flame retardant KW - Adhesion KW - Coating PY - 2016 DO - https://doi.org/10.7569/RAA.2016.097314 SN - 2168-0965 SN - 2168-0973 VL - 4 IS - 4 SP - 417 EP - 447 PB - Scrivener Publishing LLC AN - OPUS4-48164 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eisermann, R. A1 - Esterl, F. A1 - Schuchardt, M. A1 - Breithaupt, Mathias A1 - Plath, R. T1 - Distributed acoustic/vibration sensing: Towards advanced transformer condition monitoring N2 - A novel method for transformer vibration monitoring using intensity-based distributed acoustic/vibration sensing (DAS/DVS) is presented. Fibre optic sensors were fully integrated into an oil-filled medium voltage distribution transformer. Opencircuit in-situ measurements were carried out using a single and three-phase supply with an electrical power of up to 30 kVA. Spectral analysis of the mechanical vibrations were performed by measuring the frequency response of the transformer using plain fibre- and transducer-based DVS approaches. The results were compared with the spectra of a microphone mounted on the outside of the transformer housing and the electrical measurements on the high voltage side. Using the fibre optic DVS based monitoring we were able to detect changes in operating power and frequency. Further it could be shown, that it is possible to identify anomalous behaviour such as electrical/mechanical noise sources using the determined vibration spectra. T2 - 2024 IEEE International Conference on High Voltage Engineering and Applications (ICHVE) CY - Berlin, Germany DA - 18.08.2024 KW - Distributed acoustic sensing KW - DAS KW - Transformer monitoring PY - 2024 DO - https://doi.org/10.1109/ICHVE61955.2024.10676084 SP - 1 EP - 4 PB - IEEE CY - New York City, New York, USA AN - OPUS4-61798 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - VIDEO A1 - Engemann, T. T1 - Explosionen in Super Slow-Mo - Druckwellen und ihre Folgen N2 - Wissenschaftler der Bundeswehr und der Bundesanstalt für Materialforschung und -prüfung, kurz BAM, erforschen die Auswirkungen von Druckwellen auf den menschlichen Körper. Um Druckwellen untersuchen zu können, kommt ein Stoßwellengenerator zum Einsatz. Dabei handelt es sich um einen Metallzylinder, in welchem ein explosives Gasgemisch zur Detonation gebracht wird. Wir geben einen Einblick in die Versuchsreihe. KW - Blast KW - Low-level blast KW - Explosionswirkung KW - Explosionstrauma KW - Bundeswehr PY - 2024 UR - https://www.youtube.com/watch?v=j1PCPTYdUMc PB - YouTube, LLC CY - San Bruno, CA, USA AN - OPUS4-62581 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krankenhagen, Rainer A1 - Chaudhuri, Somsubhro A1 - Pittner, Andreas A1 - Winterkorn, Rene A1 - de Finis, Rosa A1 - Palumbo, Davide A1 - Galietti, Umbero T1 - Thermographic investigation of the anisotropic behaviour of additively manufactured AISI316 steel using DED-Arc N2 - Additive manufacturing is one of the most promising techniques for industrial production and maintenance, but the specifics of the layered structure must be considered. The Direct Energy Deposition-Arc process enables relatively high deposition rates, which is favourable for larger components. For this study, specimens with different orientations were prepared from one AISI316 steel block – parallel and orthogonal to the deposition plane. Quasistatic tensile loading tests were carried out, monitored by an infrared camera. The obtained surface temperature maps revealed structural differences between both orientations. The consideration of surface temperature transients yields more details about the behaviour of the material under tensile loading than the conventional stress-strain-curve. These preliminary investigations were supplemented by thermographic fatigue trials. Although the anisotropy was also observed during fatigue loading the fatigue behaviour in general was the same, at least for both inspected specimens. The presented results demonstrate the abilities and the potential of thermographic techniques for tensile tests. T2 - 17th Quantitative Infrared Thermography Conference CY - Zagreb, Croatia DA - 01.07.2024 KW - WAAM PY - 2024 SP - 1 EP - 8 AN - OPUS4-62548 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Massimo, Carraturo A1 - Breese, Philipp P. A1 - Oster, Simon ED - Rank, E. ED - Kollmannsberger, S. T1 - Thermal model for laser-based powder bed fusion of metal process: modelling, calibration, and experimental validation N2 - In the present contribution, we propose an effective numerical thermal modeling solution for melt pool simulations in Laser-based Powder Bed Fusion of Metals processes. The proposed model employs an anisotropic conductivity to represent melt pool dynamics effects in a homogeneous material model. The numerical implementation of the proposed physical model is first experimentally calibrated and then validated with respect to a series of melt pool measurements as acquired by using a short-wave infrared (SWIR) camera monitoring system. T2 - IVth International Conference on Simulation for Additive Manufacturing (Sim-AM 2023) CY - Munich, Germany DA - 26.07.2023 KW - Laser powder bed fusion of metals KW - Melt pool measurements KW - Experimental validation KW - Thermal analysis KW - SS 316L PY - 2023 DO - https://doi.org/10.23967/c.simam.2023.015 SP - 1 EP - 9 AN - OPUS4-62525 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Krankenhagen, Rainer A1 - Chaudhuri, Somsubhro A1 - Stamm, Michael A1 - Lapšanská, Ivana A1 - Aderhold, J. A1 - Schlüter, F. T1 - EvalTherm – Evaluierung der passiven Thermografie für die Zustandsbewertung von Rotorblättern an Windenergieanlagen N2 - Der Bericht gibt einen Überblick über im Rahmen des Projektes durchgeführte Forschungsarbeiten sowie ausgewählte Ergebnisse. Er wurde zusammen mit dem FhI für Holzforschung (WKI) erstellt. KW - Rotorblattinspektion KW - Passive Thermografie KW - Feldmessungen KW - Windturbine PY - 2025 N1 - Schlussbericht des Projektes N1 - Laufzeit: 1.9.2020 – 31.8.2024 N1 - Das Verbundprojekt wurde im Rahmen des 7. Energieforschungsprogramms "Innovationen für die Energiewende" gefördert N1 - Das Vorhaben wurde mit Mitteln des Bundesministeriums für Wirtschaft und Klima unter dem Förderkennzeichen 03EE3035A/B gefördert SP - 1 EP - 67 PB - Technische Informationsbibliothek (TIB) CY - Hannover AN - OPUS4-62647 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Kozachynskyi, Volodymyr A1 - Staubach, Dario T1 - Monte Carlo analysis of esterification reaction model with disappearing second liquid phase N2 - This research item is associated with the publication: Parameter estimation in dynamic multiphase liquid-liquid equilibrium systems (submitted after 2025-02-15) The software used to generate and analyze the experimental data is stored with the research data. KW - Parameter Estimation KW - NRTL KW - LLE KW - Phase Detection PY - 2025 DO - https://doi.org/10.14279/depositonce-21232 PB - Technische Universität Berlin CY - Berlin AN - OPUS4-62670 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baier, Johanna A1 - Ziegert, Christof T1 - DIN 18940 für tragendes Lehmsteinmauerwerk – Potenzial und erste Anwendungserfahrungen N2 - Mit der Veröffentlichung der DIN 18940 Juni 2023 steht in Deutschland eine zeitgemäße Bemessungsgrundlage für tragendes Lehmmauerwerk zur Verfügung, die derzeit europaweit einmalig ist. Während nach bisherigen Vorschriften lediglich zweigeschossige Gebäude mit tragendem Lehmsteinmauerwerk realisierbar waren, ermöglicht die DIN 18940 nun den Einsatz von Lehmsteinmauerwerk in fünfgeschossigen, bis zu 13 m hohen Gebäuden. Das Bemessungskonzept der DIN 18940 lehnt sich an die Grundprinzipien der vereinfachten Berechnungsmethoden für unbewehrte Mauerwerksbauten nach DIN EN 1996-3/NA an und berücksichtigt dabei die materialspezifischen Eigenschaften von Lehmsteinmauerwerk. Anpassungen waren aufgrund der feuchteabhängigen Festigkeits- und Verformungskenngrößen sowie der im Vergleich zu herkömmlichem Mauerwerk geringen Steifigkeit erforderlich. Ein Vergleich mit konventionellem Mauerwerk aus Ziegeln, Porenbeton und Kalksandsteinen zeigt, dass Lehm hinsichtlich Tragfähigkeit und bauphysikalischen Eigenschaften im Bereich der Gebäudeklasse 1-4 konkurrenzfähig ist. Besonders die geringen CO2-Emissionen und die vollständige Rezyklierbarkeit machen Lehmsteinmauerwerk zu einer klimagerechten Alternative. Weiterhin werden erste Projekte vorgestellt, die nach DIN 18940 geplant wurden. Aus den Anwendungserfahrungen werden materialgerechte Entwurfsgrundsätze für Gebäude aus Lehmsteinmauerwerk formuliert. Abschließend zeigen Einblicke in laufende Forschung und zukünftige Entwicklung, wie das Potenzial von Lehmsteinmauerwerk weiter gesteigert werden kann. T2 - LEHM 2024 - 9. Internationale Fachtagung für Lehmbau CY - Weimar, Germany DA - 27.09.2024 KW - Lehmmauerwerk KW - Ökobilanzierung KW - Normung PY - 2024 SP - 1 EP - 8 AN - OPUS4-62030 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - VIDEO A1 - Melzer, Michael T1 - Der DCC-Demonstrator erklärt N2 - In diesem Video erklärt Dr. Michael Melzer (Leiter des BAM-Kalibrierlabors) die notwendigen Entwicklungsschritte hin zu einer Praxistauglichkeit des DCCs und wie die „Metrologische Rückführung auf Knopfdruck“ funktioniert. Der digitale Kalibrierschein macht den Kalibrierprozess effizienter, sicherer und digital nachverfolgbar. Anhand eines Demonstrators zeigt er die Vorteile der metrologischen Digitalisierung und Automatisierung in der Anwendung – von der Reduzierung von Fehlerquellen bis hin zum wirtschaftlichen Nutzen im industriellen Messwesen. KW - Digital calibration certificate KW - QI-digital KW - Digital metrology KW - Calibration KW - Automation PY - 2024 UR - https://www.youtube.com/watch?v=0lfYypvTl9E&t=8s PB - YouTube, LLC CY - San Bruno, CA, USA AN - OPUS4-62076 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Völker, Tobias A1 - Mensing, Friedrich A1 - Kruschwitz, Sabine T1 - Estimation of cement content in concrete by spatially resolved laser induced breakdown spectroscopy – Dataset N2 - This dataset includes both simulated and raw measurement data as detailed in the journal paper [1]. File names follow the format SampleNo_Type, where SampleNo corresponds to the sample identifier listed in Table 1, and Type specifies the data type: either syn (synthetic) or exp (experimental). For experimental data, a slice index is appended to the file name in the format SampleNo_Type_Slice, identifying the specific subsample. [1] https://doi.org/10.1016/j.cemconres.2024.107714 KW - LIBS KW - Spectroscopy KW - Cement content KW - Elemental mapping PY - 2024 DO - https://doi.org/10.5281/zenodo.14246581 PB - Zenodo CY - Geneva AN - OPUS4-62394 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wüstenberg, Hermann A1 - Erhard, Anton A1 - Ludwig, Bernd T1 - Grundlagen der Ultraschallprüfung an plattierten Reaktorkomponenten N2 - Die Ultraschallprüfung an plattierten Reaktorkomponenten erfährt bestimmte Einschränkungen insbesondere durch Schwankungen der Empfindlichkeit, durch Verschlechterung des Signal-Rausch-Verhältnisses und durch Störanzeigen unterschiedlicher Herkunft. Die Entwicklungen der vergangenen Jahre haben Möglichkeiten aufgezeigt, durch die die Ultraschallprüfung an Reaktorkomponenten mit der bei nicht plattierten Komponenten üblichen Nachweisempfindlichkeit möglich geworden ist. Diese Empfindlichkeit wird aber bei plattierten Komponenten erkauft mit einer spürbaren Erhöhung der Zahl von Anzeigen, die zu registrieren sind. Daher muß bei der Prüfung plattierter Komponenten insbesondere auf eine bessere Klassierung der aufgefundenen Anzeigen geachtet werden. In diesem Zusammenhang muß das Instrumentarium für eine Klassierung der Anzeigen verbessert werden, z. B. durch verbesserte Signalauswertung sowie durch Benutzung des Laufzeitverhaltens einer Echoanzeige. Für eine verbesserte Befundanalyse müssen entsprechende Hilfsmittel wie fokussierende Prüfköpfe oder die akustische Holographie zur Verfügung stehen. Die vorliegenden Erfahrungen beim Einsatz der Ultraschallprüfung an plattierten Komponenten auch während der Fertigung zeigen, daß der an sich notwendige, erhöhte Aufwand nur selten zum Tragen kommt, weil die heute verfügbare Basisqualität der Komponenten erheblich verbessert werden konnte und damit die Zahl von registrierpflichtigen Anzeigen ohnehin zurückgegangen ist. T2 - Deusch-Schweizerisches Seminar "Ausgewählte Aspekte der zerstörungsfreien Prüfung von Reaktorkomponenten" CY - Stuttgart, Germany DA - 28.03.1983 KW - Zerstörungsfreie Prüfung KW - Ultraschall-Impulsechoverfahren KW - Plattierung KW - Reaktordruckgefäß PY - 1983 SP - 1 EP - 23 PB - Materialprüfungsanstalt (MPA) CY - Stuttgart AN - OPUS4-62811 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Braymer, Joseph J. A1 - Knauer, L. A1 - Crack, J. C. A1 - Oltmanns, J. A1 - Heghmanns, M. A1 - Soares, J. C. A1 - Le Brun, N. E. A1 - Schünemann, V. A1 - Kasanmascheff, M. T1 - Yeast [FeFe]-hydrogenase-like protein Nar1 can bind not only two [4Fe-4S] clusters but also a [2Fe-2S] cluster N2 - Nar1 is an essential eukaryotic protein proposed to function as an iron-sulfur (Fe/S) cluster trafficking factor in the cytosolic iron-sulfur assembly (CIA) machinery. However, such a role has remained unclear due to difficulties in purifying adequate amounts of cofactor-bound protein. The [FeFe]-hydrogenase-like protein has two conserved binding sites for [4Fe-4S] clusters, one of which is predicted to be a labile site for cluster transfer to downstream targets. Here, we report a new preparation procedure for Nar1 that facilitated studies by UV-Vis, EPR, and Mössbauer spectroscopies, along with native mass spectrometry. Nar1 recombinantly produced in E. coli contained a [4Fe-4S] cluster, bound presumably at site 1, along with an unexpected [2Fe-2S] cluster bound at an unknown site. Fe/S reconstitution reactions installed a second [4Fe-4S] cluster at site 2, leading to protein with three Fe/S cofactors. Strikingly, one [4Fe-4S] cluster was rapidly destroyed by molecular oxygen, potentially linking Nar1 oxygen sensitivity to phenotypes observed previously in vivo. These advances now allow for the pursuit of in vitro Fe/S cluster transfer assays, which will shed light on Fe/S trafficking by CIA components and how they may facilitate the insertion of [4Fe-4S] and potentially [2Fe-2S] clusters into target proteins in the cytosol. KW - Iron sulfur cluster KW - Hydrogenase-like proteins KW - Metalloprotein PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-628217 DO - https://doi.org/10.1101/2025.03.25.644927 SP - 1 EP - 14 AN - OPUS4-62821 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Chaves Spoglianti de Souza, Roberto T1 - Sensitivity Analyses of Probabilistic Thermo-Mechanical Fire Safety Assessment of Tunnel Linings N2 - Fire safety structural analyses contain uncertainties related to the mechanical aspects, such as compressive strength and tensile strength, and the thermal aspects, such as conductivity, specific heat and fire loads. The uncertainties related to the mechanical aspects are explicitly considered by the applicable standards. However, the uncertainties related to the conductivity and specific heat are implicitly considered by the standards, while the uncertainties related to the fire loads are only considered in the German National Annex of the Eurocode 1991-1-2. Nevertheless, considering the severe nature of tunnel fires, these uncertainties must be incorporated into the design. The complexity of the stresses in a tunnel lining in fire can be determined by a probabilistic thermo-mechanical analysis as proposed in the methodology presented in this work. The methodology presented here to investigate the influence of thermal parameters on the fire safety of concrete structures in tunnels is based on the thermo-mechanical finite element analysis. The methodology includes the design of experiments executed by a Correlation Latin Hypercube Sampling. This work includes three case studies to illustrate the use of the proposed methodology. The second and the third studies contain reliability analyses to evaluate the probabilities of failure. The first case study uses an analytical thermo-mechanical analysis based on the 500 °C isotherm method. It considers the uncertainties related to the thermal and mechanical properties of the concrete, the soil load, and the temperatures described by the standard temperature-time curve. The results demonstrate the importance of incorporating the characteristic values of conductivity and specific heat in the semi-probabilistic structural fire design. The probability of failure is Pf = 3.1 × 10−3. The second case study is a probabilistic thermo-mechanical analysis of tunnels using the standard temperature-time curve. It considers the uncertainties related to the thermal and mechanical properties of the concrete, the soil load, and temperature. The probability of failure is Pf = 0.06. The third case study is a probabilistic thermo-mechanical analysis of the tunnel using natural fire calculated with CFast. It considers the uncertainties related to the thermal and mechanical properties of the concrete, the soil load, and the fire load. The probability of failure is Pf = 0.08. Although the natural fire in the third study results in higher temperatures than the standard fire in the second study, the difference between the failure probabilities of both case studies is smaller than expected. The reason for the small difference is probably that the effects due to the higher temperatures are compensated by the decay phase of the natural fire. The reliability assessments of both the second and the third case study show that the investigated structures do not meet the reliability requirements derived from the EN 1990 standard. Therefore, the structures would either need to be redesigned or more protective methods would need to be provided, such as the thermal boards or sprinklers. The conductivity, specific heat, and fire load are the parameters that correlate to the results the most. For the tunnel structural fire design, the following safety factors are recommended based on this work: γfi = 1.76 for the conductivity, γfi = 0.31 for the specific heat, and γfi = 1.8 for the fire load. Given the range of results of the fire safety analyses, the inclusion of the uncertainties is demonstrated to be necessary. The choice of failure criterion has a significant influence on the probability of failure and is, therefore, a critical step in the safety analysis. For the tunnel fire, the model must be improved to accurately account for the fast heating rate and the cooling phase of tunnel fires. KW - Tunnel Fires KW - Uncertainties of Structural Fire Safety KW - Tunnel Linings KW - Fire Safety Assessment PY - 2021 SP - 1 EP - 186 PB - Fakultät Architektur, Bauingenieurwesen und Umweltwissenschaften der Technischen Universität Carolo-Wilhelmina zu Braunschweig CY - Braunschweig AN - OPUS4-62967 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Siefke, Lennart A1 - Linden, Anna T1 - Towards a robust automated surface inspection method for CT-scanned cannulas N2 - For certain cardiovascular diseases, cannulas are implanted into the blood circuit. To match the patients individual anatomy of the heart, there is research for cannulas to be custom-designed and manufactured aided by 3D printing. However, cannulas have to hold very high standards with regard to the smoothness of their surfaces, as rough patches can lead to formation of blood clots. Therefore, this work uses computer vision to detect such patches as part of quality assurance. First, the produced cannula is scanned using a precise CT scanner and transformed into a 3D mesh object. Rough patches in an otherwise smooth but curved surface are detected by using cosine similarity between neighboring faces and a statistical evaluation. In the end, this method is able to raise a warning when curved surfaces are not smooth enough and visualizes the problematic patches. However, there is just limited access to test data currently and the scanner used needs to be upgraded. T2 - 3D in Science & Applications (3D-iSA) 2024 CY - Berlin, Germany DA - 26.11.2024 KW - Algorithm KW - Additive manufacturing KW - Surface evaluation PY - 2025 UR - https://www.gfai.de SN - 978-3-942709-34-7 SP - 66 EP - 70 AN - OPUS4-63057 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baier, Jennifa A1 - Beck, Uwe A1 - Sahre, Mario T1 - Validierung der Plasmabeständigkeit von monodispersen und funktionalisierten Partikeln N2 - Mit mikroskopischer) und spektroskopischen Untersuchungsmethoden wird die Beständigkeit von monodispersen und fluoreszenzmarkierten Partikeln gegenüber Temperatur-, Vakuum- und Plasmaeinfluss geprüft. Im Fokus steht die Erprobung von plasma-kompatiblen Partikeln für Plasmadispersionsschichten zur Realisierung funktioneller add-on Eigenschaften im Rahmen des BMWi-geförderten Projektes Plasma-Fit. T2 - 9. ThGOT - Thementage Grenz- und Oberflächentechnik CY - Zeulenroda, Germany DA - 03.09.2013 KW - Partikel KW - Plasmabeständigkeit PY - 2013 SP - 242 EP - 243 AN - OPUS4-29086 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schragen, Christian A1 - Lohrer, Christian T1 - A brief journey through the world of standardization of fireworks of the last decade and into the future N2 - This paper aims at giving an overview about this entire standardization process, explaining the main differences of the EN versions from 2015 and 2022, outlining the practical implications for the stakeholders applying these ENs and giving a cautious look into the future requirements for fireworks in Europe. T2 - 19th International Symposium on Fireworks CY - Liling, P.R. China DA - 21.04.2025 KW - Fireworks KW - Standardization PY - 2025 SP - 1 EP - 17 AN - OPUS4-63077 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zia, Ghezal Ahmad Jan A1 - Valdestilhas, Andre A1 - Moreno Torres, Benjami A1 - Kruschwitz, Sabine T1 - Leveraging large language models for automated knowledge graphs generation in non-destructive testing N2 - This paper presents an innovative approach for the automatic generation of Knowledge Graphs (KGs) from heterogeneous scientific articles in the domain of Non-Destructive Testing (NDT) applied to building materials. Our methodology leverages large language models (LLMs) to extract and semantically relate concepts from diverse sources. We developed material-specific agents for concrete, wood, steel, and bricks, each equipped with a curated glossary of terms to ensure domain accuracy. These agents process PDF documents, extracting relevant information on deterioration mechanisms, physical changes, and applicable NDT methods. The extracted data is then normalized, validated, and structured into a Neo4j graph database, forming a comprehensive KG. Our results demonstrate the system’s ability to automatically discover and represent intricate relationships between materials, deterioration mechanisms, physical changes, and NDT techniques. The generated KG successfully captures complex interactions, such as the applicability of specific NDT methods to various materials under different deterioration conditions. This work not only highlights the potential of KGs in enhancing knowledge discovery and representation in NDT research but also provides a scalable framework for extending this approach to other scientific domains. T2 - SeMatS 2024 - The 1st International Workshop on Semantic Materials Science CY - Amsterdam, The Netherlands DA - 17.09.2024 KW - Materials science and engineering KW - Large language model KW - Linked open data KW - Data interoperability KW - RDF KW - Semantic web PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-624597 DO - https://doi.org/10.5281/zenodo.13834164 SN - 1613-0073 N1 - Serientitel: CEUR workshop proceedings – Series title: CEUR workshop proceedings VL - 3760 SP - 101 EP - 110 PB - RWTH Aachen CY - Aachen AN - OPUS4-62459 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dalichow, Dirk A1 - Wilsch, Gerd A1 - Völker, Tobias T1 - Laser Induced Breakdown Spectroscopy for the Chemical Investigation of Concrete—Status of Practical Application N2 - The assessment and maintenance of reinforced concrete structures depends largely on knowledge of the chloride content and chloride ingress. Common methods are the wet chemical analysis of drill dust or powder from ground drill core segments. However, due to the homogenization process, this approach often fails to detect locally elevated chloride levels. A state-of-the-art alternative method is laser-induced breakdown spectroscopy (LIBS), which offers rapid analysis and the possibility of detecting several chemical elements simultaneously. This method is particularly characterized by its ability to measure light elements such as hydrogen, carbon or sodium. The spatial resolution of LIBS is usually 0.25 mm but can be increased to 0.1 mm or less if required. BARG, is the first commercial building materials laboratory in Germany to use LIBS in practice. The current LIBS setup enables rapid, spatial quantification of the chlorine content and at the same time the creation of element maps that visually represent the distribution of essential elements in the concrete. This method can be used to localize areas of elevated chlorine content, particularly in cracks or near reinforcing bars. With the ability to analyze several elements simultaneously, LIBS can determine measurement points associated with the cement phase and, taking into account the water content, relate the measured contents directly to the cement mass. The detailed ingress profiles determined by LIBS provide essential data for the estimation of accurate chlorine diffusion coefficients, which are crucial for probabilistic lifetime predictions. The estimation of the carbon distribution enables the localization of carbonated regions and their effect on the chloride distribution. The possibility of quantitatively determining the sulfur distribution also indicates areas that are affected by a possible sulfate attack. The presentation uses practical examples to demonstrate the possibilities and advantages of the LIBS method. In addition, the newly published leaflet B14 of the German Society for Non-Destructive Testing (DGZfP) will be presented, which describes the use of LIBS for the quantitative determination of chloride content in concrete. T2 - ICCRRR 2024 CY - Cape Town, South Africa DA - 04.11.2024 KW - Concrete KW - Chloride KW - Corrosion KW - Repair KW - Maintenance PY - 2024 DO - https://doi.org/10.1007/978-3-031-75507-1_40 VL - 59 SP - 411 EP - 420 AN - OPUS4-62480 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bernhardt, Yannick A1 - Császár, Lukas A1 - Dengiz, Nizamettin A1 - Fuchs, Martin A1 - Gaal, Mate A1 - Gautzsch, Tobias A1 - Gohlke, Dirk A1 - Hahn-Jose, Thomas A1 - Heckel, Thomas A1 - Hillger, Wolfgang A1 - Hufschläger, Daniel A1 - Ilse, Detlef A1 - Kiel, Mario A1 - Kornely, Mike A1 - Labud, Patrick Alexander A1 - Marhenke, Torben A1 - Schubert, Frank A1 - Sommerhuber, Ryan A1 - Steinhausen, Ralf A1 - Szewieczek, Artur A1 - Wachter, Luis A1 - Waschkies, Thomas T1 - Charakterisierung und Verifizierung der luftgekoppelten Ultraschallprüfköpfe N2 - Dieses Dokument beschreibt die Eigenschaft en von fokussierten und unfokussierten Prüfköpfen, die für die zerstörungsfreie luftgekoppelte Ultraschallprüfung mit Mittenfrequenzen von über 20 kHz verwendet werden. Dieses Dokument bezieht sich auf Prüfköpfe, die auf dem piezoelektrischen Effekt basieren. KW - Luftgekoppelter Ultraschall KW - Ultraschallprüfung KW - Prüfköpfe KW - Charakterisierung PY - 2024 SN - 978-3-947971-36-7 VL - Richtlinie US 08 SP - 1 EP - 24 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin ET - Ausgabe Mai 2024 AN - OPUS4-62489 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Dengiz, Nizametin A1 - Fuchs, Martin A1 - Gaal, Mate A1 - Gautzsch, Tobias A1 - Herzog, Thomas A1 - Kornely, Mike A1 - Littner, Linus A1 - Marhenke, Torben A1 - Schmid, Simon A1 - Sommerhuber, Ryan A1 - Steinhausen, Ralf A1 - Szewieczek, Artur A1 - Wachter, Luis A1 - Waschkies, Thomas A1 - Wunderl, Stefan T1 - Leitfaden zur Durchführung von luftgekoppelter Ultraschallprüfung N2 - Die Anwendungsgebiete der luftgekoppelten Ultraschallprüfung (ACUT) können sehr vielfältig sein und weichen häufig stark von den Einsatzgebieten der klassischen Ultraschallprüfung ab. Vielmehr ist die ACUT eine eigenständige Methode, welche sich häufig eher mit Röntgen oder Thermografie überschneidet oder Prüfungen ermöglicht, die bis heute gar nicht verlässlich zerstörungsfrei durchgeführt werden können. Obwohl die luftgekoppelte Ultraschallprüfung mittlerweile keine neue Technologie ist, bleibt sie im Vergleich zu anderen Verfahren der ZfP ein Randgebiet unter den Methoden. Dies kommt nicht zuletzt dadurch zustande, dass es an Normen, Fachbüchern und Ausbildungsmöglichkeiten für interessierte Prüfer und Prüfaufsichten mangelt. Dies schafft für viele Anwendungsgebiete eine Einstiegshürde, welche die häufigere Anwendung verhindert. Aus diesen Gründen haben sich Experten aus Forschungseinrichtungen und aus der Industrie entschieden, einen Unterausschuss „Luftgekoppelte Ultraschallprüfung“ (ACUT) als Teil des Fachausschusses Ultraschallprüfung der DGZfP einzurichten und dort diese Themen zu bearbeiten. Es wurde beschlossen, einen Leitfaden zu erarbeiten, der interessierten Anwendern den Einstieg in ACUT erleichtert und eine Hilfestellung bei der Spezifikation und Umsetzung von solchen Prüfungen gibt. Das vorliegende Dokument ist das Ergebnis dieser Zusammenarbeit. KW - Luftgekoppelter Ultraschall KW - Ultraschallprüfung KW - Leitfaden PY - 2025 UR - https://publikationen.dgzfp.de/shop/leitfaden-zur-durchfuehrung-von-luftgekoppelter-ultraschallpruefung/ SN - 978-3-947971-45-9 VL - Richtlinie ACUT SP - 1 EP - 28 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin ET - Ausgabe Januar 2025 AN - OPUS4-62491 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF ED - Valdestilhas, Andre ED - Li, H. ED - Lambrix, P. ED - Sack, H. T1 - SeMatS 2024 - Proceedings of the first international workshop on semantic materials science: Harnessing the power of semantic web technologies in materials science N2 - Advanced technological solutions play a vital role in leveraging the potential of data and driving innovative research. However, the compatibility issues arising from different formats and structures of scientific data hinder progress in data generation, organization, storage, and sharing. To address these challenges, interoperability and efficient data access and analysis automation are crucial. The Semantic Web emerges as a powerful solution to overcome these obstacles. Expanding and adapting Semantic Web technologies to the Materials Science domain can significantly enhance research outcomes by enabling the uniform consideration, integration, and analysis of heterogeneous data from diverse sources and formats. Implementing these technologies can improve the traceability and reproducibility of scientific procedures, experiments, and simulations. It also facilitates automatable data management solutions and empowers researchers to answer scientific inquiries using semantic queries. Moreover, machine learning methods can benefit from enhanced data completeness and coherence. The primary objective of this workshop was to gather professionals in Semantic Web and in Materials Science and Engineering to show the recent advances in the use of Semantic Web technologies for Materials Science and Engineering, as well as provide a platform for discussing issues, finding collaboration opportunities and developing a community for this interdisciplinary field. We thank all authors for their submissions and all members of the SeMatS program committee for their useful reviews and comments. We are also grateful to Daniel Garijo and Andrea Mannocci, the workshop chairs of SEMANTICS 2024, for their continuous support during the workshop organization. T2 - SeMatS 2024 - The 1st International Workshop on Semantic Materials Science CY - Amsterdam, The Netherlands DA - 17.09.2024 KW - Materials science and engineering KW - Semantic web PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:0074-3760-0 SN - 1613-0073 VL - 3760 SP - 1 EP - 127 PB - RWTH Aachen CY - Aachen AN - OPUS4-62497 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Rübner, Katrin A1 - Schneider, S. A1 - Beck, T. A1 - Flassenberg, G. A1 - Herbst, Tristan T1 - Stoffkreislauf im Mauerwerksbau - Nachhaltigkeitsanalyse für das Mauerwerksrecycling / Schlussbericht zum IGF-Vorhaben 17022 N N2 - In Deutschland fallen mittelfristig erhebliche Mengen von Mauerwerkbruch an. Aus dem jährlichen Bauschuttanfall und den Produktionszahlen von Wandbausteinen lassen sich die Mengen an Mauerwerksrestmassen ableiten, die als Rückbaumaterial bei Abriss-, Umbau und Sanierungsarbeiten in Deutschland anfallen werden. Hiernach ist pro Jahr mit bis zu 10 Millionen Tonnen heute vornehmlich heterogen anfallendem Mauerwerkbruch zu rechnen [1a]. Im Sinne einer nachhaltigen Kreislaufwirtschaft sind diese Restmassen zukünftig einem möglichst hochwertigen Recycling zuzuführen. In diesem Spannungsfeld führt die deutsche Mauersteinindustrie das breit aufgestellte gemeinschaftliche Forschungsprojekt "SIM Stoffkreislauf im Mauerwerksbau" durch. In insgesamt acht mauersteinübergreifenden IGFForschungsvorhaben wurden und werden technisch orientierte Lösungsmöglichkeiten für das Recycling von Mauerwerk erarbeitet und Anwendungsbereiche für Mauerwerksrestmassen aufgezeigt. Eine grundsätzliche Entscheidung über die Eignung von Mauerwerksrestmassen für bestimmte Recyclingwege kann es letztlich nicht geben. Es wird immer eine Einzelfallentscheidung bleiben, die wesentlich durch komplexe technische sowie ökologische und ökonomische Randbedingungen geprägt wird. Vor diesem Hintergrund wurde im Rahmen des IGF-Forschungsvorhabens 17022 N der Forschungsvereinigung Porenbetonindustrie e.V., Berlin die Nachhaltigkeit verschiedener Recyclingoptionen für Mauerwerkbruch ganzheitlich untersucht und bewertet. Unter Einbeziehung der Hauptwandbausteinarten Ziegel, Kalksandstein, Porenbeton und Leichtbeton wurden dabei material- und verfahrenstechnische sowie ökologische, ökonomische und soziale Aspekte berücksichtigt. Auf Grundlage der gewonnenen Erkenntnisse wurde ein EDV-gestütztes Analysetool (Web-Tool) zur Nachhaltigkeitsbewertung für das Mauerwerksrecycling entwickelt. Mit dem Web-Tool sollen Anwender (Planer, Architekten, Recycler) die Möglichkeit erhalten, für verschiedene Untersuchungsfälle unter Einbeziehung regional und sachlich bedingter Parameter, wie Materialqualität, Stoffmengen, Logistik, Aufbereitungstechnik, Anwendungsbereiche, Kosten und Erlöse, objektspezifische Aussagen zur Nachhaltigkeit treffen zu können. Auf diesem Wege können im Sinne der aktuellen gesetzlichen Vorgaben nachhaltige Stoffkreisläufe im Mauerwerksbau geschlossen und somit letztlich die Deponierung von Mauerwerksrestmassen vermieden werden. Alle vier Wandbaustoffarten haben sich im Rahmen des Forschungsvorhabens als recyclingfähig und hinsichtlich der Nachhaltigkeit als gleichwertig erwiesen. Das Ziel des Vorhabens wurde damit erreicht. KW - Nachhaltigkeit KW - Mauerwerkbruch KW - Ganzheitlichkeit PY - 2013 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-288572 SP - 1 EP - 182 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-28857 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Strangfeld, Christoph A1 - Stolpe, Heiko A1 - Wiehle, Philipp T1 - Moisture diffusion affected by the Knudsen effect in temporal changing pore networks N2 - Almost all building materials in civil engineering have an open porosity and interact with or are affected by the environmental conditions. Structures might suffer from effects such as moisture adsorption, carbonation, corrosion, penetration of salt ions and chemical substances, etc. In the hygroscopic range, these processes are mostly driven by diffusion. Due to the confinement of small pores (< 1 µm), the Knudsen effect reduces the molecular diffusion. This reduction can become more significant in case of temporal changing pore systems because of physisorption of water vapor, carbonation, or chemisorption. In this study, unstabilised earth blocks and earth masonry are investigated. In a first step, the pore size distribution of the blocks is measured and sorption isotherms are recorded in experiments. Besides the ordinary physisorption, the involved clay minerals undergo swelling or shrinking due to chemisorption. The following two effects must be considered: first, the reduction of the available pore space by the adsorbed water layer. For this, the Hillerborg sorption theory is used, which is a combination of the well-known Brunauer-Emmett-Teller sorption theory and the Kelvin equation. This allows the computation of adsorbed water layers even in curved pore geometries. Second, the variation of the initial pore size distribution due to chemisorption needs to be modelled. Based on these two models, the effective diffusion coefficient can be predicted. For validation, arrays of relative humidity sensors were embedded into a free-standing earth masonry wall. This monitoring was carried out over more than a year to have a broad variety of environmental conditions and was located in Berlin, Germany. The prediction of the effective diffusion coefficient can also be transferred to other processes and allows the investigation of materials having temporarily changing pore systems. Examples are the carbonation of cementitious materials, alkali silica reaction, calcium leaching of long-lasting structures, etc. This effect becomes most prominent in the meso-pore range and might alter the effective diffusion coefficient by more than 100 %. T2 - 4th International Congress on Materials & Structural Stability CY - Rabat, Morocco DA - 08.03.2023 KW - Earth masonry KW - Material moisture KW - Molecular diffusion KW - Chemisoprtion KW - Knudsen effect KW - Physisorption PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-571391 SP - 1 EP - 8 PB - RILEM CY - Champs-sur-Marne AN - OPUS4-57139 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Johann, Sergej A1 - Strangfeld, Christoph A1 - Zimmek, David A1 - Bartholmai, Matthias T1 - Smart electronic helper for long-term monitoring of bridges and building structures N2 - Increasing traffic volume on the one hand and ageing infrastructure on the other hand have created many new challenges for maintenance and structural health monitoring of roads and bridges. In the past, many bridges and road structures have been neglected, often resulting in traffic congestion, road closure, and increased repair costs. This research is concerned with the development of a system to improve the challenge of maintenance and early detection of damage, particularly moisture penetration and corrosion of steel reinforced concrete components. The objective is to develop a method that will also work after 30 years and longer. Many new IoT solutions are equipped with internal energy storage elements (accumulators or batteries) which are inappropriate here, since most relevant signs of concrete degradation occur after decades, where the functioning of such elements are more than questionable. The presented technology approach uses radio-frequency identification (RFID) and enables connectivity to sensors. It offers the advantage of an passive, completely independent energy supply without any energy storage components. Since the system should be permanently embedded in concrete, it is crucial to develop a long-term stable device which is adapted to the environmental influences of the structure, e.g., long-term resistance in very alkaline environment of pH 13. In numerous experiments, the robustness of the system was tested and evaluated. Various tests with encapsulations to protect the electronics were performed, and for long-term validation different concrete specimens were instrumented with RFID-sensor-systems. Their operating time is now around two years and investigations for signs of fatigue and damage to the encapsulation and the electronics are ongoing. T2 - SMAR 2019 CY - Potsdam, Germany DA - 27.08.2019 KW - Sensors KW - Passive RFID KW - Smart structures KW - SHT KW - Long term monitoring PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-501931 UR - https://www.ndt.net/?id=25011 SN - 1435-4934 VL - 25 IS - 1 SP - 1 EP - 6 PB - NDT.net CY - Kirchwald AN - OPUS4-50193 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Klewe, Tim T1 - Non-destructive classification of moisture deterioration in layered building floors using ground penetrating radar N2 - In the event of moisture deterioration, rapid detection and localization is particularly important to prevent further deterioration and costs. For building floors, the layered structure poses a challenging obstacle for most moisture measurement methods. But especially here, layer-specific information on the depth of the water is crucial for efficient and effective repairs. Ground Penetrating Radar (GPR) shows the potential to generate such depth information. Therefore, the present work investigates the suitability of GPR in combination with machine learning methods for the automated classification of the typical deterioration cases (i) dry, (ii) wet insulation, and (iii) wet screed. First, a literature review was conducted to identify the most common methods for detecting moisture in building materials using GPR. Here, it especially became clear that all publications only investigated individual time-, amplitude- or frequency features separately, without combining them. This was seen as a potential aspect for innovation, as the multivariate application of several signal features can help to overcome individual weaknesses and limitations. Preliminary investigations carried out on drying screed samples confirmed the profitable use of multivariate evaluations. In addition to the general suitability and dependencies of various features, first limitations due to possible interference between the direct wave and the reflection wave could be identified. This is particularly evident with thin or dry materials, for which the two-way travel times of the reflected radar signals become shorter. An extensive laboratory experiment was carried out, for which a modular test specimen was designed to enable the variation of the material type and thickness of screed and insulation, as well as the simulation of moisture deteriorations. The data collected revealed clear differences between dry and deteriored structures within measured B-scans. These deviations were to be detected with the newly introduced B-scan features, which evaluate the statistical deviation of A-scan features within a survey line. In this way, deteriorations to unknown floor structures are recognized, regardless of the material parameters present. In a subsequent training and cross-validation process of different classifiers, accuracies of over 88 \% of the 504 recorded measurements (252 different experimental setups) were achieved. For that, the combination of amplitude and frequency features, which covered all relevant reflections of the radar signals, was particularly beneficial. Furthermore, the data set showed only small differences between dry floors and deteriored screeds for the B-scan features, which could be attributed to a homogeneous distribution of the added water in the screeds. The successfully separation of these similar feature distributions raised the suspicion of overfitting, which was examined in more detail by means of a validation with on-site data. For this purpose, investigations were carried out at five different locations in Germany, using the identical measurement method like in the laboratory. By extracting drilling cores, it was possible to determine the deterioration case for each measurement point and thus generate a corresponding reference. However, numerous data had to be sorted out before classification, since disturbances due to underfloor heating, screed reinforcements, steel beams or missing insulation prevented comparability with the laboratory experiments. Validation of the remaining data (72 B-scans) achieved only low accuracy with 53 \% correctly classified deterioration cases. Here, the previously suspected overfitting of the small decision boundary between dry setups and deteriored screeds within the laboratory proved to be a problem. The generally larger deviations within (also dry) on-site B-scans were thus frequently misclassified as screed deterioration. In addition, there were sometimes strongly varying layer thicknesses or changing cases of deterioration within a survey line, which caused additional errors due to the local limitation of the drilling core reference. Nevertheless, individual on-site examples also showed the promising potential of the applied signal features and the GPR method in general, which partly allowed a profound interpretation of the measurements. However, this interpretation still requires the experience of trained personnel and could not be automated using machine learning with the available database. Nevertheless, such experience and knowledge can be enriched by the findings of this work, which provide the basis for further research. Future work should aim at building an open GPR data base of on-site moisture measurements on floors to provide a meaningful basis for applying machine learning. Here, referencing is a crucial point, whose limitations with respect to the moisture present and its distribution can easily reduce the potential of such efforts. The combination of several reference methods might help to overcome such limitations. Similarly, a focus on monitoring approaches can also help to reduce numerous unknown variables in moisture measurements and increase confidence in the detection of different deterioration cases. KW - NDT KW - Moisture measurement KW - Ground penetrating radar KW - Building floor PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-591044 DO - https://doi.org/10.14279/depositonce-19306 SP - 1 EP - 146 PB - Technische Universität Berlin CY - Berlin AN - OPUS4-59104 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bühling, Benjamin A1 - Maack, Stefan A1 - Strangfeld, Christoph T1 - OsciCheck - A Novel Fluidic Transducer for Air-Coupled Ultrasonic Measurements N2 - Ultrasonic measurement technology has become indispensable in NDT-CE. Air-coupled ultrasonic (ACU) measurement techniques promise to reduce measurement time. However, the signal quality suffers from large specific impedance mismatch at the transducer-air and air-specimen interface. Additionally, large pressure amplitudes are necessary for the penetration depth required in NDT-CE applications. To address the specific requirements of ultrasonic testing in NDT-CE, a robust ACU transducer was developed, that generates ultrasound by quickly switching a pressurized air flow. The simple design of the fluidic transducer makes the device maintenance free and resilient against harsh environmental conditions. Since the signal is generated by aeroacoustics, there is no specific impedance mismatch between the transducer and the surrounding air. The ultrasonic signal exhibits frequencies in the 30-60 kHz range and is therefore well suited to penetrate heterogenous materials such as concrete. This contribution gives an introduction in the working principle and signal characteristics of the fluidic transducer. Its applicability to measurements in concrete is verified. A detailed outlook is given to discuss the future potential of fluidic ultrasonic actuators. T2 - NDT-CE 2022 CY - Zurich, Switzerland DA - 16.08.2022 KW - Air-coupled ultrasound KW - Nondestructive testing KW - Fluidics KW - Bistable amplifier KW - Aeroacoustics PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-555271 UR - https://www.ndt.net/search/docs.php3?id=27319 VL - 2022/09 SP - 1 EP - 9 PB - NDT.net CY - Bad Breisig AN - OPUS4-55527 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hille, Falk A1 - Herrmann, Ralf A1 - Schneider, Ronald A1 - Pitters, S. A1 - Wedel, F. A1 - Hindersmann, I. T1 - Developing a guideline for structural health monitoring of road bridges in Germany N2 - In recent years, Structural Health Monitoring (SHM) has become a useful and increasingly widely used tool for supporting lifetime extensions of existing bridges with known structural deficiencies or indications of potentially critical damages or damage processes. At the same time, methods and tools are emerging, which enable monitoring-informed predictive maintenance of new and existing bridges based on digital twins. The monitoring process – starting from the definition of monitoring actions and ending with decisions based on monitoring outcomes – is complex and requires expertise in structural engineering, operation and maintenance of bridges, metrology, and data analytics. To support German road authorities, engineering consultancies, building contractors and other stakeholders of the bridge management, the Federal Highway Research Institute (BASt) has initiated the development of a new guideline for applying SHM as part of the management of road bridges. The guideline will present various use cases and for each identified use case, it will propose a proven monitoring scheme. In addition, the guideline will provide guidance on assessing the benefits of SHM as well as a common approach to managing monitoring data as a systematic basis for integrating monitoring data in the bridge management. This contribution discusses the motivation, objectives, and scope of the guideline, describes its use case centric structure and outlines the proposed data management. T2 - IABMAS 2024 CY - Kopenhagen, Danmark DA - 24.06.2024 KW - Guideline KW - Structural health monitoring KW - Road bridges KW - Infrastructure PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-613947 SN - 978-1-032-77040-6 DO - https://doi.org/10.1201/9781003483755-236 SP - 2009 EP - 2017 PB - CRC Press AN - OPUS4-61394 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Deresse, N. E. A1 - Thiele, Marc A1 - Pirskawetz, Stephan A1 - Sarem, M. A1 - Francois, St. A1 - Verstrynge, E. T1 - Evaluation of Concrete Fatigue Damage with Elastic Wave-based Measurement Techniques N2 - The fatigue damage evolution and the fatigue life of quasi-brittle materials such as concrete are not yet completely understood. Accordingly to get better insights, researchers have recently been incorporating advanced measuring techniques in their fatigue experiments. In this research, acoustic emission techniques (AET), active ultrasonic, and deformation measurements are used to track the damage evolution of concrete samples subjected to fatigue loading. The samples are subjected to constant amplitude and stepwise fatigue loading in Brazilian splitting test set-ups. Initially, a good agreement is observed between the deformation and the ultrasonic measurements in capturing the crack propagation during Brazilian splitting tests. The three fatigue damage phases could be identified with all of the three techniques. The Phase II damage rates quantified by deformation measurements and AET in stepwise fatigue tests were used to predict the number of cycles to failure at various stress levels. The predictions were validated using the number of cycles to failure of the constant amplitude fatigue tests. T2 - 36th Conference of the European Working Group on Acoustic Emission CY - Potsdam, Germany DA - 18.09.2024 KW - Concrete KW - Acoustic emission KW - Ultrasonic testing KW - Fatigue PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-615677 DO - https://doi.org/10.58286/30228 SN - 1435-4934 VL - 29 IS - 10 SP - 1 EP - 10 PB - NDT.net AN - OPUS4-61567 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Villani, P. A1 - Unger, Jörg F. A1 - Weiser, M. T1 - Adaptive Gaussian process regression for Bayesian inverse problems N2 - We introduce a novel adaptive Gaussian Process Regression (GPR) methodology for efficient construction of surrogate models for Bayesian inverse problems with expensive forward model evaluations. An adaptive design strategy focuses on optimizing both the positioning and simulation accuracy of training data in order to reduce the computational cost of simulating training data without compromising the fidelity of the posterior distributions of parameters. The method interleaves a goal-oriented active learning algorithm selecting evaluation points and tolerances based on the expected impact on the Kullback-Leibler divergence of surrogated and true posterior with a Markov Chain Monte Carlo sampling of the posterior. The performance benefit of the adaptive approach is demonstrated for two simple test problems. T2 - Algoritmy 2024 - Central-European Conference on Scientific Computing CY - Vysoké Tatry, Slovakia DA - 15.03.2024 KW - Active learning KW - Bayesian inverse problems KW - Gaussian Process Regression (GPR) KW - Parameter identification KW - Surrogate models PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-600408 DO - https://doi.org/10.48550/arXiv.2404.19459 SN - 2331-8422 SP - 1 EP - 12 PB - Cornell University CY - Ithaca, NY AN - OPUS4-60040 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schönsee, Eric A1 - Jeyifous, Olubunmi Anthony A1 - Strangfeld, Christoph A1 - Hüsken, Götz T1 - Investigations on multi-sensor data for monitoring volume flow during the printing process N2 - Extrusion based 3D concrete printing (3DCP) is a growing technology because of its high potential for automating construction and the new possibilities of design. In conventional construction methods, a sample is taken to be representative for one material batch. However, in 3DCP continuous mixing is used which results in variations during the mixing process. Therefore, one sample is not representative for the entire structure. This leads to the necessity of continuous and real-time process monitoring. This study focuses on the variations of pressure and temperature which are caused by changes in the material due to the ongoing mixing process. Changes in material, which is transported downstream, are influencing sensor signals in different positions with a time delay. In the following, the data is analysed to investigate if the changing material and the so caused change in pressure can be used to calculate volume flow. T2 - Digital Concrete 2024 CY - Munich, Germany DA - 04.09.2024 KW - Additive manufacturing KW - In-line Monitoring KW - Volume Flow KW - Process Control PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:gbv:084-2024081513042 DO - https://doi.org/10.24355/dbbs.084-202408151304-0 SP - 1 EP - 3 AN - OPUS4-61001 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Viefhues, Eva A1 - Döhler, M. A1 - Hille, Falk A1 - Mevel, L. T1 - Fault detection for linear parameter varying systems under changes in the process noise covariance N2 - Detecting changes in the eigenstructure of linear systems is a comprehensively investigated subject. In particular, change detection methods based on hypothesis testing using Gaussian residuals have been developed previously. In such residuals, a reference model is confronted to data from the current system. In this paper, linear output-only systems depending on a varying external physical parameter are considered. These systems are driven by process noise, whose covariance may also vary between measurements. To deal with the varying parameter, an interpolation approach is pursued, where a limited number of reference models – each estimated from data measured in a reference state – are interpolated to approximate an adequate reference model for the current parameter. The problem becomes more complex when the different points of interpolation correspond to different noise conditions. Then conflicts may arise between the detection of changes in the eigenstructure due to a fault and the detection of changes due to different noise conditions. For this case, a new change detection approach is developed based on the interpolation of the eigenstructure at the reference points. The resulting approach is capable of change detection when both the external physical parameter and the process noise conditions are varying. This approach is validated on a numerical simulation of a mechanical system. T2 - 21st IFAC World Congress CY - Online meeting DA - 13.07.2020 KW - Linear parameter varying systems KW - Fault detectionchanging KW - Process noise KW - Subspace-based residual KW - Model interpolation PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-524652 DO - https://doi.org/10.1016/j.ifacol.2020.12.868 SN - 2405-8963 VL - 53 IS - 2 SP - 13668 EP - 13673 PB - Elsevier AN - OPUS4-52465 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kanzler, D. A1 - Schmitt, M. A1 - Maack, Stefan A1 - Baensch, F. T1 - Erarbeitung einer Norm für einen standardisierten Prozess zur probabilistischen Bewertung von Prüfverfahren N2 - Im DIN-Normenausschuss Materialprüfung (NMP) wurde das Normungsgremium NA 062-08-28 AA „Qualifizierung von zerstörungsfreien Prüfungen“ reaktiviert. Das Ziel der Reaktivierung ist die Erarbeitung einer Norm für einen standardisierten Prozess zur probabilistischen Bewertung von Prüfverfahren. In der zerstörungsfreien Prüfung (ZfP) führt die Ermittlung von Mess- / Prüfunsicherheiten von Prüfverfahren, in normativer Hinsicht in Deutschland und Europa, noch ein Schattendasein. Die Norm ISO IEC 17025 und auch der VDA-Band 5 wurden weiter in Richtung Messunsicherheit entwickelt, allerdings führt ihre Anwendung in der ZfP zu Problemen. Der Arbeitsausschuss NA 062-08-28 AA soll hier den Brückenschlag zwischen Messunsicherheit, objektiver statistischer Bewertung für ZfP-Verfahren und eine weitere Stärkung der probabilistischen Bruchmechanik erreichen. Geplant ist daher die Erarbeitung einer DIN-Norm, welche die Kriterien für eine korrekte Versuchsplanung, ein praktikables Vorgehen zur Bewertung der Prüfergebnisse und die mathematische Überführung in eine Zuverlässigkeitsaussage enthält. Es soll ein Leitfaden erstellt werden, der für ein möglichst breites Branchenspektrum eingesetzt werden kann, unabhängig von den Besonderheiten verschiedener Industriezweige. Dargestellt werden das relevante Normungsgremium sowie der Hintergrund des zu erstellenden Dokuments. T2 - DGZfP Jahrestagung 2023 CY - Friedrichshafen, Germany DA - 15.05.2023 KW - Validation KW - Probabilistischen Bewertung KW - Zerstörungsfreie Prüfverfahren KW - POD PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-584176 UR - https://www.ndt.net/search/docs.php3?id=28574 SN - 978-3-947971-29-9 SP - 1 EP - 8 PB - NDT.net AN - OPUS4-58417 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Küttenbaum, Stefan A1 - Braml, T. A1 - Taffe, A. A1 - Maack, Stefan ED - Li, J. ED - Spanos, D. ED - Chen, J. B. ED - Peng, Y. B. T1 - Towards NDT-supported decisions on the reliability of existing bridges N2 - A major advantage in the reassessment of existing structures is the possibility of including measured data that describe the actual properties and the current condition of the structure to be reassessed. Currently, the incorporation of such measured information is mostly unregulated. However, the use of measurement results is vitally important, since a measured data-based improvement of the computation models level of approximation can lead at least to more meaningful results, possibly to extended remaining life times of the structure and in the best case to a saving of resources. Conversely, not appreciating well measurable and relevant information can be equated with a waste of resources. In this paper, a concept for the comparable use of non-destructively measured data as basic variables in probabilistic reliability assessments is outlined and examined using a typical prestressed concrete road bridge as a case-study. An essential requirement is the calculation of measurement uncertainties in order to evaluate the quality of the measurement results comparably. In conclusion, the example of ultrasonic and radar measurement data is used to demonstrate the effects that the incorporation of the measured information has on the reliability of the structure. T2 - 13th International Conference on Structural Safety and Reliability (ICOSSAR 2021-2022) CY - Online meeting DA - 13.09.2022 KW - Measurement uncertainty KW - Reliability assessment KW - Existing structures KW - Concrete Bridge KW - Non-Destructive Testing (NDT) PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-583013 SP - 1 EP - 10 AN - OPUS4-58301 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Andrés Arcones, Daniel A1 - Weiser, M. A1 - Koutsourelakis, F. A1 - Unger, Jörg F. T1 - A Bayesian Framework for Simulation-based Digital Twins of Bridges N2 - Simulation-based digital twins have emerged as a powerful tool for evaluating the mechanical response of bridges. As virtual representations of physical systems, digital twins can provide a wealth of information that complements traditional inspection and monitoring data. By incorporating virtual sensors and predictive maintenance strategies, they have the potential to improve our understanding of the behavior and performance of bridges over time. However, as bridges age and undergo regular loading and extreme events, their tructural characteristics change, often differing from the predictions of their initial design. Digital twins must be continuously adapted to reflect these changes. In this article, we present a Bayesian framework for updating simulation-based digital twins in the context of bridges. Our approach integrates information from measurements to account for inaccuracies in the simulation model and quantify uncertainties. Through its implementation and assessment, this work demonstrates the potential for digital twins to provide a reliable and up-to-date representation of bridge behavior, helping to inform decision-making for maintenance and management. T2 - Eurostruct 2023 CY - Vienna, Austria DA - 25.09.2023 KW - Digital Twins KW - Bayesian Inference KW - Bridge Monitoring KW - Uncertainty Quantification PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-586803 UR - https://eurostruct.org/eurostruct-2023/ DO - https://doi.org/10.1002/cepa.2177 SN - 2509-7075 VL - 6 IS - 5 SP - 734 EP - 740 PB - Ernst & Sohn CY - Berlin AN - OPUS4-58680 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Munsch, Sarah Mandy A1 - Bintz, Thilo A1 - Heyn, R. A1 - Hirsch, H. A1 - Grunewald, J. A1 - Kruschwitz, Sabine T1 - Detailed investigation of capillary active insulation materials by 1H nuclear magnetic resonance (NMR) and thermogravimetric drying N2 - Capillary active interior insulation materials are an important approach to minimize energy losses of historical buildings. A key factor for their performance is a high liquid conductivity, which enables redistribution of liquid moisture within the material. We set up an experiment to investigate the development of moisture profiles within two different interior insulation materials, calcium-silicate (CaSi) and expanded perlite (EP), under constant boundary conditions. The moisture profiles were determined by two different methods: simple destructive sample slicing with subsequent thermogravimetric drying as well as non-destructive NMR measurements with high spatial resolution. The moisture profiles obtained from both methods show good agreement, when compared at the low spatial resolution of sample slicing, which demonstrates the reliability of this method. Moreover, the measured T2-relaxation-time distributions across the sample depth were measured, which may give further insight into the saturation degree of the different pore sizes. In order to explain differences in the moisture profiles between CaSi and EP, we determined their pore-size distribution with different methods: conversion of the NMR T2 relaxationtime distribution at full saturation, mercury intrusion porosimetry and indirect determination from pressure plate measurements. CaSi shows a unimodal distribution at small pore diameters, while in EP, a bi-modal or wider distribution was found. We assume that the smaller pore diameters of CaSi lead to a higher capillary conductivity, which causes a more distributed moisture profile in comparison with that of EP. T2 - NDT-CE CY - Zurich, Switzerland DA - 16.08.2022 KW - Insulation material KW - Nuclear magnetic resonance KW - Capillary conductivity KW - Pore-size distribution PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-579172 DO - https://doi.org/10.58286/27205 SN - 1435-4934 VL - 27 IS - 9 SP - 1 EP - 11 AN - OPUS4-57917 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Taffe, A. A1 - Küttenbaum, Stefan A1 - Maack, Stefan T1 - ZfPStatik - Messergebnisse rechenbar machen N2 - ZfPStatik bezeichnet die Verwendung von statistisch bewerteten Messergebnissen, die mit zerstörungsfreien Prüfverfahren im Bauwesen (ZfPBau) gewonnen werden und in statischen Berechnungen zum Nachweis der Tragfähigkeit verwendet werden. Dazu ist die Ermittlung der Messunsicherheit der Versuchsdaten auf der Basis des GUM (Guide to the Expression of Uncertainty in Measurement) der erste Schritt. Der statische Nachweis erfolgt durch Grenzzustandsgleichungen, die im Bauwesen angewandt werden. Diese müssen modifiziert werden, so dass jede Messgröße als Zufallsvariable in der Grenzzustandsgleichung vorhanden ist. Der statische Nachweis erfolgt mit probabilistischen Berechnungsmethoden aus der Zuverlässigkeitstheorie. Diese Vorgehensweise wird exemplarisch für den Standsicherheitsnachweis eines Plattenbalkenquerschnitts einer Stahlbetonbrücke auf Biegung angewandt. Auf die möglichen Schlussfolgerungen aus den probabilistischen Berechnungen wird abschließend kurz eingegangen. T2 - DGZfP-Fachtagung Bauwerksdiagnose 2018 CY - Berlin, Germany DA - 15.02.2018 KW - ZfP KW - ZfPBau KW - ZfPStatik KW - Zuverlässigkeitstheorie PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-442266 UR - https://www.bauwerksdiagnose2018.de/Portals/bauwerksdiagnose2018/BB/20.pdf UR - https://www.bauwerksdiagnose2018.de SN - 978-3-940283-90-0 VL - BB 165 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-44226 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Hille, Falk T1 - Unterraumbasierte Detektion von Strukturschäden an Jacket-Gründungen von Offshore-Windenergieanlagen N2 - Die vorliegende Arbeit beschreibt die Adaption eines globalen, schwingungsbasierten Verfahrens zur frühzeitigen Erkennung von Strukturschäden an Gründungsstrukturen offshore installierter Windenergieanlagen (OWEA). Damit soll es, Betreibern von Offshore-Windparks ermöglicht werden, im Rahmen periodisch durchgeführter messtechnischer Überwachungsmaßnahmen mit einem gegenüber wiederkehrender Inspektionen wesentlich geringen Aufwand auftretende Schäden an der Struktur zuverlässig zu delektieren. Das untersuchte und implementierte Verfahren basiert auf der Methode der stochastischen unterraumbasierten Schadensdetektion. Dabei erfolgt eine statistische Analyse des wiederkehrend messtechnisch aufgenommenen dynamischen Antwortverhaltens des mechanischen Systems. Mittels statistischem Test werden signifikante Änderungen in dessen Eigenstruktur und damit Schäden delektiert. Im Rahmen der vorliegenden Arbeit wurden umfangreiche experimentelle als auch numerische Untersuchungen zur Sensitivität und Robustheit des beschriebenen Schadensindikators durchgeführt. Dazu sind zunächst an einem Labormodell mittels künstlich und reversibel eingebrachter Schäden grundlegende Analysen zu den Einflüssen signal- und verfahrensinhärenter Kenngrößen durchgeführt worden. Auf der Basis dieser Ergebnisse wurde im Anschluss mittels numerischer Analysen das Antwortverhalten von OWEA simuliert und der entwickelte Algorithmus zur Schadensdetektion an den so realisierten Datensätzen angewendet. Anhand der Ergebnisse der Arbeit wird aufgezeigt, dass, vorausgesetzt die Windenergieanlage befindet sich in Parkposition, eine Detektion von schon geringen Schäden an Gründungs-strukturen mit dem beschriebenen Verfahren, auch unter Einsatz weniger Messaufnehmer, zuverlässig möglich ist. N2 - The present work describes the adaptation of a global, vibration-based procedure for an early detection of structural damage to foundation-structures of offshore wind turbines (OWT). It is intended to enable operators of offshore wind farms to reliably detect structural damage by periodic measurement with a once installed monitoring System. The analyzed and implemented procedure is based on the method of stochastic subspace- based damage detection. This involves a Statistical analysis of the of the periodically measured dynamic response behavior of the mechanical System. By means of a Statistical test, significant change in its eigenstructure and thus damage is detected. Within the present work extensive experimental as well as numerical investigations on the sensitivity and robustness of the described damage indicator were conducted. For this purpose, fundamental analyzes of the effects of signal- and process-inherent Parameters on the detection results has been performed at a laboratory model structure by means of artificially and reversibly applied damage. Based on these results, the response behavior of OWT structures was then simulated numerically and the developed algorithm for damage detection was finally applied to the thus achieved data sets. Based on the results of the work it is shown that, assuming the wind turbine Stands in parking position, a detection of already small damage at foundation structures is reliably possible with the described method, even using only a limited number of sensors. KW - Offshore-Windenergieanlagen KW - Structural Health Monitoring KW - Schwingungsbasierte Verfahren KW - Schadensdetektion KW - Unterraummethoden PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-470040 DO - https://doi.org/10.14279/depositonce-7567 SP - 1 EP - 219 PB - Technische Universität CY - Berlin AN - OPUS4-47004 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wiehle, Philipp A1 - Härder, M. A1 - Strangfeld, Christoph T1 - Moisture behaviour of earth block masonry under natural climate conditions – experimental and numerical studies N2 - The compressive stength of unstabilised earth masonry depends on the moisture content. Knowledge of the moisture content is necessary in order to be able to account for the impact of moisture on the structural design of earth block masonry. For conventional building materials it is possible to precisely forecast the component moisture according to the layered structure on the basis of hygrothermal simulations. However , it is still not clear to what degree these numerical calculations can offer valid results for earth building materials. Earth building materials have a number of special properties related to moisture storage and moisture transport that differ significantly from the physical simplifications that are a component of existing material models. The swelling and shrinking of earth materials and their organic components results in changes to the pore space, the sorption behaviour exhibits a clear hysteresis, and the experimental determination of hygrothermal parameters in continuous contact with liquid water is almost impossible. To adequately forecast the moisture content of earth block masonry under natural climate conditions, extensive investigations of the moisture behaviour of load-bearing earth block masonry have been carried out within the framework of this project. These efforts began with the performance of magnetic resonance spectroscopic tests on two load-bearing earth blocks, in order to quantify the adsorption and desorption processes at relative humidities of between 50 % and 90 % under controlled, isothermal laboratory conditions. Once this had been done, a modified test setup was used to determine the water absorption coefficient , from which the liquid transport coefficients were derived. Based on the hygrothermal parameters values that were thus determined, the model was calibrated using the WUFI software program [7]. Finally, long-term moisture measurements were conducted on an earth block masonry wall that was ex-Increasing shortages of raw materials and rising energy prices are resulting in continuous growth in the demand for earth construction. In comparison to conventional building materials, earth building materials offer three significant advantages that have become even more important in light of the energy crisis in 2021 and the associated increase in the price of building supplies by approx. 40 percent [1]. Firstly, water solubility makes it possible to fully separate and recover all of the material components, and in particular the sand component. Secondly, energy-intensive firing processes, such as those required for cement production or brick manufacture, are eliminated. And thirdly, earth is a local raw material that is available in large quantities [1]. However, the load-bearing capacity of earth building materials is very much dependent on the moisture content. An increase in the relative humidity results in a reduction in the clay mineral cohesion , and this in turn results in a decline in both the compressive strength and the modulus of elasticity. In this regard, the mechanical properties of earth block masonry change in inverse proportion to the relative humidity. In other words, with every percentage point increase in relative humidity, both the compressive strength and the modulus of elasticity decline by one percent [2] [4]. The internal walls of heated living areas are generally only subject to relatively small fluctuations in relative humidity (between 40 % and 60 %) [5], and short periods in excess of these levels (such as in bathrooms or kitchens) only lead to a significant increase in the moisture content of the uppermost layers [6]. Exterior walls, on the other hand, are subject to large seasonal fluctuations in temperate climates, with a relative humidity in excess of 90 % in winter months. However, the exterior walls of heated living areas must be insulated in accordance with the German Buildings Energy Act (GEG), and with masonry this is generally done us T2 - LEHM 2024 – 9. Internationale Fachtagung für Lehmbau CY - Weimar, Germany DA - 27.09.2024 KW - Earth stone KW - Masonry KW - Material moisture KW - Moisture monitoring KW - Hygrothermal simulations PY - 2024 SP - 1 EP - 10 AN - OPUS4-61220 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pirskawetz, Stephan T1 - Richtlinie „Detektion von Spanndrahtbrüchen mit Schallemission“ N2 - Ein großer Teil unserer Brücken wurden in den 1950er bis 1970er Jahren als Spannbetonbrücken gebaut. Mit der damals noch relativ jungen Technologie entstanden elegante, teilweise gewagte Bauwerke mit großen Spannweiten, welche die Vorteile der Materialien Stahl und Beton geschickt kombinieren. Die Standsicherheit einiger dieser Brücken ist heute gefährdet. Die Ursachen liegen in der enorm gewachsenen Belastung durch Schwerverkehr, teilweise ungenügender Wartung und in konstruktiven und Materialschwächen, die der mangelnden Erfahrung mit der Technologie in der Bauzeit geschuldet sind. Ein neuralgischer Punkt der Bauwerke sind die in den Beton integrierten Spannglieder. Infolge von Korrosion und Ermüdung können Elemente der Spannglieder reißen, wodurch die für das Tragwerk notwendige Spannung und somit die Tragfähigkeit reduziert werden. Nicht bei allen Brücken kündigen sichtbare Risse im Beton oder auffällige Verformungen den Tragfähigkeitsverlust bzw. das finale Versagen rechtzeitig an. Die Schallemissionsanalyse ist die derzeit einzige Methode, das Reißen einzelner Spannstähle zuverlässig und mit wirtschaftlich vertretbarem Aufwand zu detektieren. Trotzdem es schon einige Spannbetonbauwerke gibt, die mit Schallemissionsanalyse überwacht werden, ist das Verfahren noch wenig bekannt. Außerdem fehlen technische Richtlinien, was die Ausschreibung und Vergabe von entsprechenden Aufträgen und die Bewertung der Angebote sehr erschwert. Um sowohl Baulastträger als auch Dienstleistungsanbieter in den Vergabeverfahren und im Betrieb der Monitoringsysteme zu unterstützen, hat sich eine Gruppe von Experten aus den Bereichen Bauingenieurwesen und Schallemission zum Entwurf einer Richtlinie „Detektion von Spanndrahtbrüchen mit Schallemission“ zusammengefunden. Mit diesem Beitrag wird die Richtlinie vorgestellt, deren Bearbeitung bis zur SCHALL 23 abgeschlossen sein soll. T2 - SCHALL 23 Entwicklung und Anwendung der Schallemissionsanalyse und Zustandsüberwachung mit geführten Wellen CY - Wetzlar, Germany DA - 21.03.2023 KW - Schallemission KW - Spannbeton KW - Brücke KW - Spannstahlbruch PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-573904 SP - 1 EP - 4 PB - DGZfP CY - Berlin AN - OPUS4-57390 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schubert, T. A1 - Bracklow, F. A1 - Unger, N. A1 - Hering, Marcus A1 - Beckmann, B. T1 - Impact Tests on Reinforced Concrete Slabs – Variation in Results and Residual Load Bearing Capacity due to Hard Impact N2 - Structures such as concrete slabs and concrete barriers of critical infrastructure facilities must be able to withstand impact events or severe accidents. In particular, the structural safety of the confinements of nuclear power plants against a possible aircraft impact is essential to ensure the safety of inhabitants and environment. This article presents research results of hard impact on reinforced concrete slabs, which have been carried out at the Institute of Concrete Structures (IMB) at TUD Dresden University of Technology Technische Universität (TU Dresden). A specially designed drop tower is available for this purpose on the premises of the Otto Mohr Laboratory of TU Dresden. In the framework of a research project many reinforced concrete slabs of dimension 1.5 x 1.5 x 0.2 m³ were tested by hard impact. The investigation on some already carried out impact tests on reinforced concrete slabs intend to show the range of deviation of impact tests. In particular, the possible standard deviations that should be regarded in impact tests are estimated for the applied test setup. Furthermore, the residual structural capacity of an undamaged and damaged reinforced concrete slab has been investigated. T2 - Conference: 27th International Conference on Structural Mechanics in Reactor Technology (SMiRT) CY - Yokohama, Japan DA - 04.03.2024 KW - Reinforced Concrete KW - Drop Tower KW - Hard Impact PY - 2024 SP - 1 EP - 10 PB - IASMiRT CY - Yokohama, Japan AN - OPUS4-61915 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hüsken, Götz A1 - Jeyifous, Olubunmi Anthony A1 - Schönsee, Eric A1 - Strangfeld, Christoph T1 - An assessment of the repeatability of 3D printed concrete structures N2 - Additive manufacturing of concrete structures, also known as 3D concrete printing, is a technology that received a lot of attention over the past decade due to its financial an ecological advantage as sustainable construction technology. Although several techniques and approaches demonstrate these advantages, quality control during printing is highly challenging and rarely applied and harmonized standards are not existing. Due to the continuous mixing process used in 3D concrete printing, it is impossible to exclude variations in the dry mixture or water content, and a single test sample is insufficient to be representative for the whole structure. A defect in one layer during the printing can affect the entire integrity of the whole structure. This study shows the results of an arch designed as framework structure that was printed multiple times under the same boundary conditions using an extrusion-based 3D concrete printer. Each arch was tested for its mechanical strength and load bearing behavior. The results of the mechanical testing of the printed arches are compared with material data obtained by classical tests and discussed regarding their statistical significance. T2 - Digital Concrete 2024 CY - Munich, Germany DA - 04.09.2024 KW - 3D concrete printing KW - Repeatability KW - Monitoring KW - Process control KW - Quality control PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-611012 DO - https://doi.org/10.24355/dbbs.084-202408150641-0 SP - 1 EP - 9 PB - TU Braunschweig AN - OPUS4-61101 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Algernon, A. A1 - Walther, A. A1 - Denzel, W. A1 - Ebsen, B. A1 - Feistkorn, S. A1 - Friese, M. A1 - Grosse, C. A1 - Kathage, S. A1 - Kessler, S. A1 - Köpp, Christian A1 - Krause, M. A1 - Maack, Stefan A1 - Schickert, M. A1 - Taffe, A. A1 - Timofeev, Juri A1 - Wilcke, M. A1 - Wolf, J. T1 - Qualitätssicherung und Validierung der Anwendung zerstörungsfreier Prüfungen von Stahlbetonbauteilen im Bauwesen N2 - Stahlbetontragwerke sind eine wichtige Konstruktionsweise im Bauwesen und ein wachsendes Anwendungsfeld für die Zerstörungsfreie Prüfung (ZfP). Zur Sicherung der Tragsicherheit, strukturellen Integrität, Bestimmung von Geometrien und zur Detektion konstruktiver Elemente wie z.B. Bewehrung, Verankerungen und Spannkanälen besitzen zerstörungsfreie Prüfverfahren in diesem Bereich inzwischen große Relevanz. Durch den bislang erreichten Fortschritt in der Forschung und Entwicklung haben moderne akustische und elektromagnetische Verfahren eine beachtliche Leistungsfähigkeit erreicht. Von Geräteherstellern sind diese in kommerziellen Produktserien umgesetzt worden und finden eine zunehmend breite Anwendung in der Praxis. In einigen anderen Anwendungsgebieten, in denen die ZfP bereits fester Bestandteil von Überwachungen ist, wie z.B. im Maschinenbau und insbesondere in der Kerntechnik und der Luftfahrt, existieren umfangreiche Qualitätssicherungssysteme für die konforme Anwendung und zuverlässige Einbeziehung der ZfP. Dem relativ jungen Entwicklungsstadium moderner ZfP für Stahlbetonbauteile entsprechend müssen solche Konzepte im Bauwesen erst noch entwickelt bzw. implementiert werden. Dementsprechend hat sich der Unterausschuss Qualitätssicherung (UA- S) des Fachausschusses ZfP im Bauwesen (ZfPBau) die Definition und Verbesserung der Qualität von ZfP-Anwendungen sowie insbesondere die verfahrensunabhängige Standardisierung von Prüfprozeduren und statistische Absicherung der Prüfergebnisse zum Ziel gemacht. Die aktuellen Arbeitsfelder beinhalten die Entwicklung praxisgerechter Konzepte für Prüfprozeduren und deren Erprobung in einem Ringversuch sowie die Konzeption von Testkörpern hinsichtlich unterschiedlicher Aspekte wie Parameterstudien, Validierung, Kalibrierung und Simulation. Dabei werden Ansätze anderer Branchen durchaus einbezogen, die Anpassung an die spezifischen Bedürfnisse und Gegebenheiten des Bauwesens wird jedoch als wesentlich angesehen und stellt somit eine wichtige Vorgabe dar. Da die Tätigkeiten nicht auf einzelne Verfahren begrenzt sind, müssen generelle Vorgehensweisen entwickelt werden, die sich auf die jeweiligen Verfahren konkretisieren lassen. Der Vortrag gibt hierzu erste Einblicke in die Arbeit des Ausschusses. T2 - DGZfP-Jahrestagung 2018 CY - Leipzig, Germany DA - 07.05.2018 KW - Zerstörungsfreie Prüfung KW - Beton KW - Qualitätssicherung KW - Validierung PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-472417 SP - 1 EP - 9 AN - OPUS4-47241 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Strangfeld, Christoph A1 - Johann, Sergej A1 - Müller, Maximilian A1 - Bartholmai, Matthias T1 - Moisture Measurements with RFID based Sensors in Screed and Concrete N2 - To quantify the moisture in concrete, RFID based humidity sensors are embedded. Passive high frequency, ultra-high frequency RFID tags as well as active Bluetooth sensors are tested. After concreting, all sensors measure the corresponding relative humidity to monitor the concrete moisture. Two case studies are performed, embedding in an existing construction, i.e. the duraBASt test bridge, and embedding in cement based mortar in the laboratory. As basis for robust and long-life sensors in alkaline concrete, different casing materials are tested. Furthermore, signal strength measurements and their sensitivity to different moisture levels are performed. T2 - 8th European Workshop On Structural Health Monitoring CY - Bilbao, Spain DA - 05.07.2016 KW - Humidity sensors KW - Moisture measurements KW - RFID based sensors KW - DuraBASt PY - 2016 SP - 1 EP - 10 AN - OPUS4-36817 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Unger, Jörg F. T1 - Mechanics group at Federal Institute for Materials Research and Testing N2 - The poster presents the work of the mechanics group in BAM, department 7. The current projects deal with the simulation of concrete on different spatial and temporal scales - ranging from the creation of mesoscale geometries up to fatigue and high strain rate impact phenomena. T2 - COST Meeting 1404 CY - Ljubljana, Slovenia DA - 16.05.2015 KW - Mechanics KW - Contact KW - Multiscale KW - Concrete KW - Constitutive modelling PY - 2015 AN - OPUS4-38647 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zorn, Sebastian A1 - Unger, Jörg F. A1 - Schneider, Ronald ED - Silva Gomes, J. F. ED - Meguid, S. A. T1 - A probabilistic method for identification of vehicle loads and system parameters for reinforced concrete bridges N2 - Growth of vehicle traffic density can be observed in many countries all over the world. This accretion is caused by world-wide population growth on the one hand, but also by increasing freight volumes and, thus, freight transports on the streets on the other hand. This increased exposure becomes more and more of a problem for the civil infrastructure such as bridges. Many of these bridges are nowadays stressed to their limits by higher loads than they were originally designed for and/or operating times beyond the initially predicted life span. This raises questions about structural safety and lifetime prediction, of course, and therefore illustrates the need for accurate structural monitoring. Since the lifetime of bridge structures is primarily influenced by their traffic loading, an accurate identification of load configurations over the whole length of a structure is most desirable. In this paper, a method for vehicle load identification is proposed. It involves Bayesian Analysis and (quasi-)static importance functions in order to estimate vehicle positions, velocities and weights. The structure is modeled with finite elements in order to generate model predictions for different load configurations. The model predictions are compared to the actual measured data to identify the most probable loading configuration for that measurement. This involves the use of enhanced Monte Carlo simulations such as MCMC to reduce the computational effort. The measured data from different kinds of sensors can (and should) be combined for accuracy gain – in this case a combination of measured displacements and inclinations. Since the measurements take place over some time during the passage of the vehicle, these estimations are carried out for several time instants for which the estimation is carried out. The advantage of using Bayesian Updating Method is the embodied learning effect leading to an improvement of the estimation when adding new information in a new calculation step. Using the estimates for the loading conditions of a bridge structure as well as measurements of the structural responses, Bayesian analysis is again used in order to estimate localized structural parameters such as Young's modulus or Moments of Inertia in form of probability density functions yielding most probable values for the parameters. Considering the difficulties for load identification close to the support poles of the bridge and therefore for the proposed structural parameter identification procedure, it is clear that this problem is ill posed. Bayesian regularization methods also have proven to be very effective when handling ill posed problems. T2 - IRF2016 - Integrity Reliability Failure CY - Porto, Portugal DA - 24.07.2016 KW - Vehicle load identification KW - Structural health monitoring KW - Bayesian updating method PY - 2016 SN - 978-989-98832-4-6 VL - 2016 SP - PAPER REF: 6294-575 EP - 576 PB - INEGI-Instituto de Ciencia e Inovacao em Engenharia Mecanica e Gestao Industrial CY - Porto - Portugal AN - OPUS4-39833 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mendler, A. A1 - Döhler, M. A1 - Hille, Falk T1 - Detecting changes in boundary conditions based on sensitivity-based statistical tests N2 - Structural health monitoring is a promising technology to automatically detect structural changes based on permanently installed sensors. Vibration-based methods that evaluate the global system response to ambient excitation are suited to diagnose changes in boundary conditions, i.e., changes in member prestress or imposed displacements. In this paper, these changes are evaluated based on sensitivity-based statistical tests, which are capable of detecting and localizing parametric structural changes. The main contribution is the analytical calculation of sensitivity vectors for changes in boundary conditions (i.e., changes in prestress or support conditions) based on stress stiffening, and the combination with a numerically efficient algorithm, i.e., Nelson’s method. One of the main advantages of the employed damage diagnosis algorithm is that, although it uses physical models for damage detection, it considers the uncertainty in the data-driven features, which enables a reliabilitybased approach to determine the probability of detection. Moreover, the algorithm can be trained and the probability of detecting future damages can be predicted based on data and a model from the undamaged structure, in an unsupervised learning mode, making it particularly relevant for unique structures, where no data from the damaged state is available. For proof of concept, a numerical case study is presented. The study assesses the loss of prestress in a two-span reinforced concrete beam and showcases suitable validation approaches for the sensitivity calculation. T2 - International Symposium on Non-Destructive Testing in Civil Engineering (NDT-CE 2022) CY - Zurich, Switzerland DA - 16.08.2022 KW - Nelson’s method KW - Global ambient vibrations KW - Asymptotic local approach KW - Sensitivity vectors KW - Probability of detection KW - Stress stiffening PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-566632 DO - https://doi.org/10.58286/27311 SN - 1435-4934 VL - 27 IS - 9 SP - 1 EP - 13 PB - NDT.net CY - Kirchwald AN - OPUS4-56663 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Maack, Stefan A1 - Küttenbaum, Stefan A1 - Bühling, Benjamin T1 - Low-frequency ultrasound data (pulse-echo technique) with shear horizontal and longitudinal waves on the step-shaped concrete specimen “Pk050” N2 - This dataset contains raw data acquired in ultrasound measurements on a reference specimen made of concrete at Bundesanstalt für Materialforschung und -prüfung (BAM), Berlin (Germany). The internal specimen identifier is “Pk050”. The measurements were conducted using the pulse-echo method. The upper surface of the specimen was defined as measuring area. The aim of the measurements is to determine the geometrical dimensions (thickness) of the specimen “Pk050”. In addition to this, a dataset of a second specimen with identifier “Pk266” has been acquired. Pk266 has the same geometrical dimensions and concrete recipe as Pk050, but contains tendons [Reference: https://doi.org/10.7910/DVN/NUU0WZ]. KW - Ultrasound KW - Pulse echo method KW - Synthetic Aperture Focusing Technique KW - Validation KW - Elastic wave PY - 2023 DO - https://doi.org/10.7910/DVN/9EID5D PB - Harvard College CY - Cambridge, MA, USA AN - OPUS4-57231 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stelzner, Ludwig A1 - Eiz Eddin, Ahmad A1 - Häßler, Dustin A1 - Hothan, Sascha T1 - Zum Feuerwiderstand vorgespannter Carbonbetondecken N2 - Der Einsatz von hoch zugbeanspruchbarem und korrosionsbeständigem Carbongelege anstelle herkömmlichen Spannstahls ermöglicht es Beton vorzuspannen und gleichzeitig die Betondeckung auf ein für den Verbund nötiges Minimum zu reduzieren. Der Wechsel von massiven zu filigranen Bauteilen führt in der Regel aufgrund der geringeren thermischen Masse zu einer Abnahme des Feuerwiderstandes. Der Beitrag stellt Versuchsergebnisse zum Abplatz- und Hochtemperaturverhalten von Carbonbeton vor, die im Rahmen des Verbundvorhabens „Vorgespannte Carbonbetondecken mit reduzierten Querschnitten“ (CaPreFloor) erzielt wurden. Für die Untersuchung der Tragfähigkeit bei hohen Temperaturen wurden 4-Punktbiegeversuche mit instationärer Temperaturbeanspruchung an vorgespannten Carbonbetonplatten bei Variation des Carbongeleges und des Vorspanngrades durchgeführt. Ferner erfolgte die Analyse der Abplatzneigung an bewehrten und unbewehrten Bauteilen mittels Brandversuchen unter Einheits-Temperaturzeitkurve. T2 - 16. Carbonbetontage 2024 CY - Dresden, Germany DA - 24.09.2024 KW - Carbonbeton KW - Feuerwiderstand KW - Abplatzverhalten PY - 2024 SP - 56 EP - 57 AN - OPUS4-62430 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lozano, Daniel A1 - Bulling, Jannis T1 - The SBFEM to simulate the scattering of ultrasonic guided waves interacting with defects in 3D plate structures N2 - In the field of guided waves for non-destructive testing, the interaction of these waves with damages or other discontinuities in a structure is critical. When a guided wave mode travels and hits a defect, it scatters in all directions, converting to other modes and reflecting the existing one. These interactions are captured in scattered far field complex amplitudes and characterise the elastodynamic behaviour of a defect completely. Simulating these interactions is challenging, and analytical solutions only exist for simple geometries. Still, using general tools like the finite element method results in large, usually costly models. We employ a method based on a numerical implementation of the Kirchhoff–Helmholtz integral that allows the computation of the scattering matrices using a model containing only the damaged region. However, classical techniques to resolve the far field and low-order elements are commonly used, leading to large models yet more efficient than using other strategies.We propose using the SBFEM as an alternative to enhance the computation of the far field scattering. The damaged region is discretised using high-order polyhedral elements, while the far field is constructed using a modified version of the SBFEM. Examples compared to the literature demonstrate the validity of the approach. T2 - DAGA 2024 - 50. Jahrestagung für Akustik CY - Hannover, Germany DA - 18.03.2024 KW - Simulations KW - Guided waves KW - SBFEM PY - 2024 SP - 636 EP - 639 CY - Hannover AN - OPUS4-62713 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Alphonse, Amal A1 - Hintermüller, Michael A1 - Kister, Alexander A1 - Lun, Chin Hang A1 - Sirotenko, Clemens T1 - A neural network approach to learning solutions of a class of elliptic variational inequalities N2 - We develop a weak adversarial approach to solving obstacle problems using neural networks. By employing (generalised) regularised gap functions and their properties we rewrite the obstacle problem (which is an elliptic variational inequality) as a minmax problem, providing a natural formulation amenable to learning. Our approach, in contrast to much of the literature, does not require the elliptic operator to be symmetric. We provide an error analysis for suitable discretisations of the continuous problem, estimating in particular the approximation and statistical errors. Parametrising the solution and test function as neural networks, we apply a modified gradient descent ascent algorithm to treat the problem and conclude the paper with various examples and experiments. Our solution algorithm is in particular able to easily handle obstacle problems that feature biactivity (or lack of strict complementarity), a situation that poses difficulty for traditional numerical methods. KW - Obstacle Problems KW - Numerical Analysis KW - Optimization and Control KW - Simulation PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-622160 DO - https://doi.org/10.48550/arXiv.2411.18565 SP - 1 EP - 38 AN - OPUS4-62216 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bulling, Jannis A1 - Gravenkamp, H. A1 - Birk, C. T1 - On the efficient simulation of ultrasonic waves on polygonal meshes N2 - At many stages of technology development in ultrasonic Non-Destructive Testing (NDT) and Structural Health Monitoring (SHM), simulation tools are essential. Many modern approaches to ultrasonic testing, such as Model Assisted Probability of Detection, inverse problems with iterative optimization, or the generation of data for AI training, benefit from highly efficient simulation tools in terms of simulation time. In this talk, we investigate explicit time stepping with the Scaled Boundary Finite Element Method (SBFEM) for approximating the linear elastic wave equation on 2D polygonal meshes, enhanced with a mass lumping technique for faster simulation times. We present the proposed changes to the formulation to successfully use mass lumping. Examples are used to demonstrate that there is no loss of quality due to the approximated mass matrix. Furthermore, mass lumping reduces the simulation time and makes the simulation more efficient. In addition, the proposed simulation method has the advantages of SBFEM meshing techniques. These advantages include fast meshing using an image-based quadtree algorithm or polygonal meshing by transforming triangular meshes based on a CAD model. The latter meshing method can include special crack tip elements that efficiently handle the crack tip singularity. T2 - DAS | DAGA 2025 CY - Copenhagen, Denmark DA - 17.03.2025 KW - Non-Destructive Testing (NDT) KW - Scaled Boundary Finite Element Method (SBFEM) KW - Structural Health Monitoring (SHM) KW - Numerical simulation PY - 2025 UR - https://pub.dega-akustik.de/DAS-DAGA_2025/imprint.html SN - 978-3-939296-23-2 SP - 1592 EP - 1595 AN - OPUS4-63017 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bintz, Thilo A1 - Kruschwitz, Sabine T1 - Non-destructive Testing for the Determination of Durability-Relevant Material Properties of Clinker-Reduced Building Materials N2 - In the quest to combat climate change, the construction industry, heavily reliant on cement-based materials, faces scrutiny due to significant CO2 emissions, mainly from clinker production. To address this, there’s a need to strategically reduce clinker content in cement. However, these new formulations must meet the same requirements as the original ones, so their durability must be investigated. In this study, we determined material parameters that enable an assessment of moisture and ion transport. These methods offer advantages over conventional approaches, including non-destructiveness, reduced measurement time, simplified setup, enhanced resolution, and improvement of detection limits. Our investigation utilizes NDT techniques, using 1H NMR relaxometry for moisture transport and LIBS for ion transport in various clinker-reduced materials. The NMR tomograph provides spatial insights into internal moisture transport, correlated with weight change assessments for the capillary transport coefficient. Additionally, based on NMR relaxometry data the chloride diffusion coefficient is estimated. Chloride migration tests are performed, and results are evaluated using LIBS and indicator tests for the chloride migration coefficient. Our findings highlight NMR relaxometry and LIBS advantages over conventional methods, showcasing superior spatial resolution, non-destructiveness, and, in some cases, expedited results with independence from the formulation of the cement matrix. Thus, these new methods can be used to test the durability of new, more heterogeneous cementbased building. T2 - Rilem Spring Convention 2024 CY - Milano, Italy DA - 10.04.2024 KW - NMR relaxometry KW - LIBS KW - Clinker reduced cement KW - Durability parameters PY - 2025 SN - 978-3-031-70281-5 DO - https://doi.org/10.1007/978-3-031-70281-5_48 VL - 56 SP - 426 EP - 434 AN - OPUS4-61824 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pittrich, Tim A1 - Stelzner, Ludwig A1 - Weise, Frank T1 - Fire-induced spalling of normal strength concrete with different types of blended Portland cement N2 - The cement industry is looking to reduce its overall CO2 footprint. Greener manufacturing can be achieved by the introduction of more clinker-reduced cements. Concrete exposed to fire tends to show explosive spalling caused by thermomechanical and thermohydraulic processes. It is therefore essential to determine how concretes with clinker-reduced cements behave under fire exposure, especially for concretes containing calcined clays, as these are expected to be the supplementary cementitious material of the future. In this paper, normal strength concretes with four different cements (CEM I, CEM II/A-LL, CEM III/A and CEM II/B-Q) were examined for their fire-induced spalling behaviour. In addition, a mix with PP fibres was investigated for each concrete. The experiments were conducted on ring-restrained cylindrical specimens exposed to the hydrocarbon fire curve. The results showed that the cement type influences spalling behaviour. Samples with CEM I spalled the least, followed by CEM II/A-LL and CEM III/A. Finally, samples with CEM II/B-Q showed the most severe damage. It was found that the spalling behaviour of different concretes correlates with the moisture content before exposure to fire, meaning that higher moisture content leads to higher spalling susceptibility. The use of 2 kg/m³ PP fibres completely inhibited spalling regardless of the cement type used and therefore remains a successful avoidance strategy. T2 - Structures in Fire 2024 CY - Coimbra, Portugal DA - 19.06.2024 KW - Fire-induced concrete spalling KW - Concrete KW - Blended Portland cement KW - SCM KW - PP-fibres PY - 2024 SN - 978-989-35292-2-5 DO - https://doi.org/10.30779/cmm_SIF24 VL - 1st Edition SP - 461 EP - 471 AN - OPUS4-60809 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dombrowski, M. A1 - Hückler, A. A1 - Stelzner, Ludwig A1 - Häßler, Dustin A1 - Heidemann, L. A1 - Reinhold, S. A1 - Zeitler, B. A1 - Früke, J. A1 - Lenz, T. A1 - Theuerkauf, H. A1 - Söll, S. A1 - Reyher, B. A1 - Schlaich, M. T1 - Innovative lightweight floors made of prestressed CFRP-reinforced concrete – from research to construction practice N2 - The presented joint research project “CaPreFloor”, which started in 2023, aims to employ prestressed textile-reinforced concrete using carbonfibre-reinforced polymer (CFRP) to design lightweight floor elements. This allows the reduction of common steel-reinforced concrete floors of 30 cm thickness to a maximum of 6 cm for office, residential, and hotel buildings. Lower material consumption significantly contributes to the conservation of resources and minimises the carbon footprint. In addition, the prefabrication of these floor elements results in high and consistent quality, short construction times and enhanced reusability of the components. A team of experts from various research and practice fields works on this project to achieve the set goal. Currently, open questions include the anchorage and load transfer of the prestressed CFRP reinforcement, structural failure indication, the behaviour of CFRP reinforcement and high-performance concrete at elevated temperatures, as well as fire resistance and sound insulation. As a result, an extensive test programme on different size scales will be conducted. Practical aspects, such as design, field of application and life cycle, as well as the development of an automated production plant, are also considered. The paper will present considerations related to the geometry and design, material selection, manufacturing, ecological footprint, and intended experimental test programme. Four different geometries and two different CFRP reinforcements are being examined. As a result, the developed floor must fulfil all practical requirements in building construction. T2 - XI International Symposium on Fiber Reinforced Concrete (Befib 2024) CY - Dresden, Germany DA - 15.09.2024 KW - Lightweight floor system KW - Prestressed CFRP concrete KW - Fire resistance KW - Sound insulation PY - 2024 SP - 246 EP - 256 AN - OPUS4-62431 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Diercks, Philipp A1 - Robens-Radermacher, Annika A1 - Rosenbusch, Sjard Mathis A1 - Unger, Jörg F. A1 - Saif-Ur-Rehman, Saif-Ur-Rehman T1 - fenics-constitutive N2 - This software enables the use of nonlinear constitutive models with FEniCSx. KW - Constitutive models KW - FEniCSx KW - Fenics-constitutive PY - 2024 DO - https://doi.org/10.5281/zenodo.13364955 PB - Zenodo CY - Geneva AN - OPUS4-62114 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Robens-Radermacher, Annika A1 - Strobl, Dominic T1 - PGDrome N2 - A FEniCS based python module of the Proper Generalized Decomposition (PGD) method. KW - Reduced Order Model KW - Proper Generalized Decomposition KW - Fenics PY - 2023 DO - https://doi.org/10.5281/zenodo.10075334 PB - Zenodo CY - Geneva AN - OPUS4-59134 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Zimmek, David T1 - Experimentelle Validierung eingebetteter Sensorik zur pH-Wert Bestimmung basierend auf Fluoreszenzspektroskopie N2 - Die vorliegende Arbeit beschäftigt sich mit der experimentellen Validierung eingebetteter Sensorik zur pH-Wert Bestimmung basierend auf Fluoreszenspektroskopie. Bisherige Karbonatisierungsmessungen basieren auf zerstörenden Methoden. Durch das Einbetonieren von immer erreichbaren pH-Sonden wird die Überprüfung zerstörungsfrei. Um ein fehlerfreies, reproduzierbares Ergebnis zu gewährleisten, mussten diese pH-Sonden zunächst getestet und eine ausreichend präzise Methode zur Messung entwickelt werden. Durch das Vorgeben unterschiedlicher pH-Milieus und dem Testen verschiedener Messmethoden und Versuchsaufbauten werden Situationen im Beton simuliert. Hierzu werden die pH-Sonden mit unterschiedlich starken basischen und neutralen Lösungen in Kontakt gebracht, wodurch der in den Sonden befindliche Indikator je nach pH-Wert eine blaue oder orange Färbung annimmt. In den Sonden befindliche Quantenpunkte werden durch einen Laser angeregt. Diese Quantenpunkte fluoreszieren aufgrund der Anregung im blauen und orangen Spektrum. Mithilfe der Fluoreszenzspektroskopie wird die durch den Indikator gefilterte Fluoreszenz in Reflexion und Transmission gemessen. Die Ergebnisse werden genutzt, um ein Verhältnis zwischen den zwei Wellenlängen zu berechnen, anhand dessen zu erkennen ist, welche Farbe der Indikator in den Sonden angenommen hat. Die experimentelle Validierung dient der Optimierung der Methodik, des Versuchsaufbaus und der Zusammensetzung der Sonden. Nach eine Reihe unterschiedlicher Versuche, werden Bedingungen geschaffen, welche zu den gewünschten Ergebnissen führen. Das in Reflexion gemessene Licht kann Aussage darüber geben, welche Farbe der Indikator annimmt und das Verhältnis zwischen dem blauen und dem orangen Spektrum gibt die erwarteten Werte zurück. Die Ergebnisse dieser Arbeit sollen in Betonprobekörpern angewandt werden, um die hier erprüfte Methode in Realbedingungen zu testen. KW - pH Wert in Baustoffen KW - Fluoreszenzspektroskopie KW - Eingebettete Sensorik PY - 2018 SP - 1 EP - 68 CY - Berlin AN - OPUS4-46326 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Johann, Sergej A1 - Strangfeld, Christoph A1 - Chahardehinejad, Omid A1 - Bartholmai, Matthias ED - Pastrama, S. D. ED - Constantinescu, D. M. T1 - Passive RFID Transponder – Low-Power Multi-Sensor Interface for Structural Health Monitoring in Concrete N2 - Structural Health Monitoring (SHM) has become very important in today's rapidly developing time. High buildings, large bridges and complex technical structures need to be monitored continuously and this over long periods. Visual monitoring cannot evaluate the internal condition of building structures. Thus, material embedded sensors are needed. Cable connection of these sensors pose the disadvantage of weak spots and water intrusion. For concrete embedded sensors the use of batteries is not convenient, because of limited lifetime, difficult charging, and generation of electrical waste.. Hence, monitoring should be implemented preferentially with firmly embedded passive RFID sensor modules. However, since the concrete structure forms an electromagnetically reflective and absorbing barrier, only limited energy can be transmitted to the module. This project requires a highly energy-saving system, which can record different sensor parameters at critical points. T2 - 35th Danubia - Adria Symposium on Advances in Experimental Mechanics CY - Sinaia, Romania DA - 25.09.2018 KW - RFID KW - Structural Health Monitoring KW - Passive sensor interface KW - Concrete PY - 2018 SN - 978-606-23-0874-2 SP - 141 EP - 142 AN - OPUS4-46097 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rosenbusch, Sjard Mathis A1 - Diercks, Philipp A1 - Kindrachuk, Vitaliy A1 - Unger, Jörg F. T1 - Integrating custom constitutive models into FEniCSx: A versatile approach and case studies N2 - The development and integration of user-defined constitutive relationships into finite element (FE) tools using standardized interfaces play a pivotal role in advancing the capabilities of FE solvers for structural mechanics applications. While commercial FE solvers like Abaqus and Ansys have designed their interfaces to provide custom stresses, tangents, and updated history variables, the open-source solver FEniCSx remains efficient only when the constitutive update has an analytical representation. This restricts the application of FEniCSx for non-linear structural mechanics. Since FEniCSx has become a powerful and popular open-source tool for solving partial differential equations, particularly due to its automatic computation of Hessians, we aim to develop a generalized interface to enhance its capability for constitutive modeling. This approach will address complex constitutive equations that require iterative solutions at the quadrature point level. Specific implementation challenges, such as using return-mapping procedures, can then be managed commonly. The provided interface for custom constitutive models offers a versatile way to implement them in various languages, including C++, Python, Rust, and Fortran. Finally, using the example of UMATs for viscoplastic models, we demonstrate how available user subroutines can be incorporated into the interface while maintaining computational performance of FEniCSx comparable to that of Abaqus. KW - Finite element method KW - Constitutive models KW - FEniCSx KW - UMAT KW - Rust KW - Python KW - C++ PY - 2024 DO - https://doi.org/10.5281/zenodo.13980988 PB - Zenodo CY - Geneva AN - OPUS4-62112 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rücker, Werner A1 - Said, Samir A1 - Rohrmann, Rolf A1 - Schmid, Wolfgang A1 - Hille, Falk A1 - Mehdianpour, Milad T1 - Aufgaben der Dauerüberwachung und baulichen Bewertung am Beispiel von Betonbrücken und Windenergieanlagen T2 - Fachtagung 2005 des Deutschen Ausschusses für Stahlbeton "Zerstörungsfreie Prüfverfahren und Bauwerksdiagnose im Betonbau" CY - Berlin, Deutschland DA - 2005-03-10 KW - Monitoring KW - Zustandsüberwachung KW - Verkehrslasten KW - Dynamik KW - Brücken KW - Windenergieanlagen KW - Bauliche Bewertung PY - 2005 SP - A39 EP - A46 PB - BAM CY - Berlin AN - OPUS4-7334 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pirskawetz, Stephan A1 - Schmidt, S. A1 - Steinbock, O. T1 - Rückbau der Brücke Altstädter Bahnhof, Brandenburg/Havel - Detektion von Spanndrahtbrüchen mit Schallemissionsanalyse N2 - Bei einer turnusmäßigen Inspektion der B1 Brücke am Altstädter Bahnhof in Brandenburg an der Havel wurden im Dezember 2019 Risse und Hohlstellen entlang der Längsträger festgestellt. Als Ursache wurde das Versagen eines signifikanten Anteils der Spanndrähte der konzentrierten Spannglieder vermutet. Die Brücke wurde umgehend für den Verkehr gesperrt und nach weiteren, umfassenden Untersuchungen im Mai 2021 abgebrochen. Um die Sicherheit des unter der Brücke geführten Verkehrs zu gewährleisten, wurde die Brücke unter anderem mit einem Schallemissionsmesssystem überwacht. Mit diesem Verfahren ist es möglich, Spanndrahtbrüche zuverlässig zu detektieren und zu lokalisieren. In dem gut einjährigen Überwachungszeitraum wurden mehr als einhundert Spanndrahtbrüche detektiert, die in einigen Bereichen der Brücke besonders konzentriert auftraten. Vor dem Abbruch der Brücke war es möglich, den Nachweis der Detektion von Spanndrahtbrüchen mit der Schallemissionsanalyse und ihre Ortungsgenauigkeit anhand von künstlich erzeugten Drahtbrüchen zu validieren. Weiterhin konnte das sichtbare Schadensbild, Längsrisse und Hohlstellen über den Spannkanälen, auf die lokale Schädigung der Spanndrähte zurückgeführt werden. Derzeit wird ein Merkblatt erarbeitet, in dem die Erfahrungen in der bisherigen Anwendung der Schallemissionsanalyse zum Monitoring von Spanndrahtbrüchen zusammengefasst werden. In diesem Beitrag werden die Grundlagen der Schallemissionsanalyse und die Ergebnisse der Validierungsversuche an der Brücke in Brandenburg dargestellt. Weiterhin werden die Vorteile und Grenzen der Brückenüberwachung mittels Schallemissionsanalyse sowie Maßnahmen zur Sicherstellung der Qualität und der Zuverlässigkeit diskutiert. T2 - 5. Brückenkolloquium CY - Esslingen, Germany DA - 05.09.2022 KW - Spannbeton KW - Spannstahlbruch KW - Schallemission KW - Brücke PY - 2022 SN - 978-3-8169-3549-0 SN - 978-3-8169-0125-9 SP - 549 EP - 553 PB - expert verlag - Narr Francke Attempto Verlag GmbH + Co. KG AN - OPUS4-55685 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bos, Freek A1 - Robens-Radermacher, Annika A1 - Muthukrishnan, S. A1 - Versteegen, J. A1 - Wolfs, R. A1 - Santhanam, M. A1 - Menna, C. A1 - Mechtcherine, V. T1 - Database of the RILEM TC 304-ADC interlaboratory study on mechanical properties of 3D printed concrete (ILS-mech) N2 - The RILEM TC 304-ADC has set up a large interlaboratory study on the mechanical properties of 3D printed concrete (ILS-mech). The study was prepared in 2022 by a preparation group leading to a Study Plan which the TC approved on 29 November 2022 (https://doi.org/10.14459/2023mp1705940). The ILS-mech was performed in 2023. The data was collected using a pre-prepared spreadsheet template. For data management, a database was derived and set-up in openBIS. The underlying Postgres database of openBIS was exported to the here-published SQLite database for sharing without maintaining a server. The structure of the database is described in (doi). The results are discussed in three associated papers focusing on the overall outcomes and evaluation of the procedures (doi), the compressive test results (doi), and the tensile test results (doi). KW - Additive manufacturing of concrete KW - 3d concrete printing KW - 3dcp KW - Test protocol KW - Compression KW - Flexure KW - Tension KW - E-modulus KW - Bending KW - Splitting PY - 2023 PB - Zenodo CY - Geneva AN - OPUS4-61022 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neugum, Tim A1 - Stelzner, Ludwig A1 - Häßler, Dustin A1 - Hothan, Sascha A1 - Zehfuß, J. T1 - Feuerwiderstand gezwängter Stahlbetonstützen N2 - Bei realen Brandereignissen stellen sich in der Regel mechanische und thermische Randbedingungen ein, die deutlich von denen in präskriptiven, bauteilorientierten Brandprüfungen abweichen. Beispielsweise werden Interaktionen der brandbeanspruchten Bauteile mit dem umgebenden Tragwerk und daraus resultierende Zwangsbeanspruchungen bei konventionellen Brandprüfungen nicht berücksichtigt. Mit Hilfe der Substrukturtechnik kann das Verhalten einer Stütze im Brandfall unter Berücksichtigung der Interaktion mit dem umgebenden Tragwerk untersucht werden. T2 - 11. Jahrestagung des DAfStb mit 63. Forschungskolloquium der BAM CY - Berlin, Germany DA - 16.10.2024 KW - Substrukturtechnik KW - Stahlbeton KW - Stützen KW - Zwang KW - Brandschutz PY - 2024 SN - 978-3-9818564-7-7 SP - 270 EP - 277 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-61401 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neugum, Tim A1 - Stelzner, Ludwig A1 - Häßler, Dustin A1 - Hothan, Sascha A1 - Zehfuß, J. T1 - Anwendung der Substrukturtechnik zur Untersuchung des Feuerwiderstands von Stützen unter Zwang N2 - Bei realen Brandereignissen stellen sich in der Regel mechanische und thermische Randbedingungen ein, die deutlich von denen in präskriptiven, bauteilorientierten Brandprüfungen abweichen. Beispielsweise werden Interaktionen der brandbeanspruchten Bauteile mit dem umgebenden Tragwerk und daraus resultierende Zwangsbeanspruchungen bei konventionellen Brandprüfungen nicht berücksichtigt. Mit Hilfe der Substrukturtechnik kann das Verhalten einer Stütze im Brandfall unter Berücksichtigung der Interaktion mit dem umgebenden Tragwerk untersucht werden. T2 - Symposium Heißbemessung 2024 CY - Braunschweig, Germany DA - 24.09.2024 KW - Substrukturtechnik KW - Stahlbeton KW - Stützen KW - Zwang KW - Brandschutz PY - 2024 SP - 40 EP - 60 PB - TU Braunschweig CY - Braunschweig AN - OPUS4-61234 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Gebauer, D. A1 - Beltrán Gutierrez, R. A1 - Marx, S. A1 - Maack, Stefan A1 - Küttenbaum, Stefan A1 - Pirskawetz, Stephan A1 - Breit, W. A1 - Mechtcherine, V. A1 - Grahl, K. A1 - Thiel, T. A1 - Schickert, M. A1 - Krüger, M. T1 - Interrelated Data Set from Nondestructive and Destructive Material Testing of Concrete Compressive Strength Specimens N2 - "This data set contains three different data types obtained from concrete specimens. For each specimen, the rebound numbers, ultrasonic data (ultrasonic velocity, time of flight), and destructive concrete strength are given. Two kind of specimen geometries were tested: cubes and drilled cores. The files are labeled according to the specimen geometry as "cube" or "core" and the type of measurement data as "compressive_strength", "rn_R" and "rn_Q" for rebound numbers as well as "us" for ultrasonic data. The ultrasonic data were generated by six independent laboratories, the rebound numbers by five independent laboratories and the destructive tests by one laboratory. The designation of each specimen establishes the relationship between the different data types." KW - Compressive Concrete Strength KW - Rebound Hammer KW - Ultrasonic Pulse Velocity PY - 2023 DO - https://doi.org/10.7910/DVN/AFCITK PB - Harvard College CY - Cambridge, MA, USA AN - OPUS4-57223 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thiele, Marc A1 - Makris, Ralf ED - Aign, J. T1 - Reinforcement bar and reinforcement bar splicing systems under impact loading – Experimental tests and test specification N2 - Reinforced concrete is a widely used material for power generation structures, where load scenarios like impact loadings need to be considered. In this context mechanical splicing systems for the connection of reinforcement bars are of specific interest and impact resistance for the splicing systems has to be verified. High speed tensile tests need to be performed on splicing systems for reinforcement bars to confirm the capability of the coupler to resist impact loading. Furthermore, the ability of the reinforcement steel to dissipate energy by ductile behaviour with pronounced plastic strains should be confirmed by these tests. During the last decades comprehensive experiences were developed at BAM performing high speed tensile tests on reinforcement bars as well as on several splicing systems. For the lack of available standards defining these tests in detail an appropriate test procedure was developed and continuously optimized during this period at BAM. The test procedure is partially based on testing principles adapted from available standards. The main intention behind this test procedure is to perform high-speed tensile tests with a specific constant strain rate generated at the specimen. Furthermore, main objective was to establish a procedure to guarantee the comparability of test results for different diameter of reinforcement as well as for different types of couplers. Besides the pure execution of the high-speed tensile tests, the test specification also declares how to evaluate the measurements and the test results. Finally, some typical results will be presented in this contribution. T2 - SMIRT 26 CY - Potsdam, Germany DA - 10.07.2022 KW - Impact KW - Coupler systems KW - High-speed KW - Reinforcement PY - 2022 SP - 1 EP - 10 AN - OPUS4-55422 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Wallau, Wilma A1 - Pirskawetz, Stephan A1 - Greim, M. A1 - Teubert, O. T1 - AKR-Schadensmonitoring im 60 °C-Betonversuch: Abschlussbericht zum MNPQ-Projekt N2 - Zur Vermeidung der schädigenden Alkali-Kieselsäure-Reaktion (AKR) in Betonbauwerken wird die Alkalireaktivität von Gesteinskörnungen getestet. Der 60°C-Betonversuch ermöglicht eine vergleichsweise schnelle Einschätzung nach fünf-monatiger Testdauer. Dazu wird die Dehnung von Betonprüfkörpern, die mit der zu testenden Gesteinskörnung hergestellt wurden, manuell alle 28 Tage gemessen. Ein alternatives, an der BAM in den vergangen Jahren entwickeltes Verfahren setzt Dehnungssensoren ein, um kontinuierlich und online zu messen. Ziel dieses MNPQ-Projektes war es ein Messmodul zu entwickeln, welches eine kontinuierliche Dehnungsmessung leicht handhabbar umsetzt. Das von der Firma Schleibinger Geräte Teubert und Greim GmbH und der BAM in Kooperation entwickelte Messmodul lässt sich entweder in die herkömmliche AKR-Prüftruhe, in einen Wärmeschrank oder einen eigens entwickelten Minireaktor einlagern. Die kontinuierliche berührungslose Dehnungsmessung mittels Wirbelstromsensoren hat sich als robust und leicht handhabbar herausgestellt. Im Rahmen des Projektes ausgeführte Messungen untersuchen Einflüsse von gegenüber dem konventionellen Test variierten Testparametern, wie u.a. der Prüfkörperzahl je Behälter und dem ausbleibenden Drehen der Prüfkörper während des Tests. Die kontinuierliche Erfassung von Schallemissionen und Ultraschallgeschwindigkeit erweist sich als interessante Option um ein umfassendes Bild der Schädigungs-, Expansions-, und Hydratationsvorgänge zu gewinnen. Der eingefügte Erfolgskontrollbericht stellt den Projektverlauf dar und zeigt Chancen des entwickelten Gerätes auf. KW - Alkali-Kieselsäure-Reaktion KW - 60 °C-Betonversuch KW - Automatisierte Dehnungsmessung KW - Kontinuierliche Lagerung KW - Geräteentwicklung PY - 2017 DO - https://doi.org/10.2314/GBV:106750463X SP - 1 EP - 17 AN - OPUS4-47782 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Recknagel, Christoph A1 - Pirskawetz, Stephan A1 - Huth, Christian T1 - Alterungsverhalten von Fugenfüllsystemen in Verkehrsflächen - Teilbericht zur Bearbeitungsphase 2: Stoff- und Systemuntersuchungen an heiß verarbeitbaren Fugenmassen KW - Fugen KW - Fahrbahnbeläge KW - Funktionsfähigkeit KW - Dauerhaftigkeit KW - Unikaler Prüfstand KW - Plastische Fugenvergussmassen KW - Performance-orientierte Stoff- und Systemkennzeichnung PY - 2005 SP - 1 EP - 148 CY - Berlin AN - OPUS4-11966 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Büyüksahin, Kaan T1 - Weiterentwicklung und Automatisierung einer Ultraschallbohrlochsonde zur zerstörungsfreien Prüfung untertägiger Verschlussbauwerke N2 - Im Jahre 2011 wurde in Deutschland nach 50 Jahren der Ausstieg aus der kommerziellen Kernenergie beschlossen. Fünf Jahre später war Deutschland mit 80.000 GWh immer noch unter den zehn größten Atomstromproduzenten. Im darauffolgenden Jahr wurden weltweit 2.500.000 GWh Atomstrom produziert. Durch die Atomstromproduktion fallen große Mengen an radioaktiven Reststoffen an, die bis zu mehrere tausend Jahre für einen vollständigen Abbau benötigen. Aus dieser Problematik geht die Debatte über den Verbleib der Reststoffe hervor. Die Endlagerung in tiefen Gesteinsschichten ist eine Lösung für das Problem. Voraussetzung ist hierbei allerdings die Gewährleistung eines dauerhaften Schutzes vor ionisierender Strahlung, die durch Verschlüsse der tiefen Gesteinsschichten in Form von Verschlussbauwerken erzielt werden sollen. Es gilt die bauliche Integrität sowie die Dichtwirkung der Verschlussbauwerke dauerhaft zu überwachen und zu prüfen, um eine langfristige Verzögerung der Radionuklidfreisetzung zu gewährleisten. KW - Bohrlochsonde KW - Beton KW - ZfP im Bauwesen KW - Abschlussbauwerke KW - Ultraschall PY - 2022 SP - 1 EP - 77 CY - Berlin AN - OPUS4-54942 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pirskawetz, Stephan A1 - Bösche, Thomas A1 - Carstens, Ole A1 - Hille, Falk A1 - Holst, Ralph A1 - Käding, Max A1 - Kaplan, Felix A1 - Löhr, Manuel A1 - Richter, Walter A1 - Saloga, Katrin A1 - Schmidt, Sebastian A1 - Sodeikat, Christian A1 - Thenikl, Thomas T1 - Detektion von Spanndrahtbrüchen mit Schallemissionsanalyse N2 - Dieses Dokument beschreibt das Verfahren Schallemissionsanalyse zur Detektion von Spanndrahtbrüchen in Spannbetonbrücken im Rahmen einer kontinuierlichen Überwachung. Die Überwachung mit Schallemission liefert eine Aussage über die Anzahl von Spanndrahtbrüchen innerhalb des Überwachungszeitraumes und innerhalb der Reichweite der installierten Sensoren. Mit dem Verfahren können die Spanndrahtbrüche lokalisiert werden. Auf Basis einer weitgehend automatisierten Datenanalyse stehen Informationen über Drahtbrüche kurzfristig nach dem Ereignis zur Verfügung. Der Anwendungsbereich des Dokuments umfasst Brücken- und Ingenieurbauwerke mit Spanndrähten mit sofortigem oder nachträglichem Verbund. Spannsysteme ohne Verbund fallen nicht in den Anwendungsbereich. Die beschriebenen Verfahren können auf Spannsysteme ohne Verbund übertragen werden. Mit dem Verfahren Schallemissionsanalyse ist es nicht möglich, Spanndrahtbrüche zu finden, die vor dem Beginn der Überwachung entstanden sind. Das Dokument richtet sich an Baulastträger, Anbieter und Betreiber von Monitoringsystemen auf Basis der Schallemissionsanalyse sowie Ingenieurbüros, welche die Ergebnisse der Überwachung bewerten und Maßnahmen daraus ableiten. Es gibt Hinweise zur Planung, Ausschreibung, Installation und zum Betrieb von Monitoringsystemen zur Detektion von Spanndrahtbrüchen mit Schallemission sowie zur Überprüfung der Funktion installierter Systeme. Zur Funktionskontrolle werden Signale mit der Referenzquelle am Bauwerk ausgelöst. Diese Signale sind zu detektieren, innerhalb der vorgegebenen Genauigkeit zu lokalisieren und die vorgegebene Alarmkette muss angestoßen werden. KW - Schallemission KW - Brücke KW - Spannbeton KW - Spannstahlbruch PY - 2024 SN - 978-3-947971-34-3 VL - Richtlinie SE 05 SP - 1 EP - 33 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin ET - Ausgabe Mai 2024 AN - OPUS4-60679 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gleim, Tobias A1 - Feldkamp, Martin A1 - Quercetti, Thomas A1 - Wille, Frank T1 - Experimental and Numerical Analyses for the Evaluation of Heat Fluxes of a Fire Reference Test N2 - Packages for the transport of high-level radioactive material are designed to endure severe accidents. To obtain approval, these transport packages must adhere to the specification-based criteria of the IAEA SSR-6. To ensure compliance with these requirements, specific mechanical and thermal tests need to be appointed with respect to the package type. Typically, IAEA SSR-6 prescribes mechanical tests followed by a thermal fire test as part of a cumulative test sequence. To approve the fire test, BAM uses a reference package representing the original package in its outer geometry for characterizing the actual fire and its impact on the package. This serves a dual purpose: it allows the precise adjustment of experimental parameters for the package design to be approved, and it provides input parameters for thermomechanical simulations, cf. With the help of this methodology for characterizing boundary conditions of the package, temperature evolutions within the reference package can be studied in a Finite-Element Analyses (FEA). This helps to compare the experiments with the numerical simulations on the case of the reference package, but also serves at the same time for preliminary simulations with the package design to be approved. The thermal test consists of a 30-minute fully engulfing 800°C pool fire or an equally severe fire, e.g. a propane gas fire. The fire reference test is performed prior to the regulatory fire test with the package design to be approved. The fire reference package in the described case is a closed sheet 316L steel cylinder with a wall thickness of 10 mm, a length of 182 mm, and a diameter of 102 mm. The package was instrumented with thermocouples and filled with heat resistant insulating material. T2 - ASME PVP 2024 CY - Bellevue, WA, USA DA - 28.07.2024 KW - Reference Test KW - Experimental KW - Numerical KW - Heat Flux PY - 2024 SN - 978-0-7918-8851-3 SP - 1 EP - 8 AN - OPUS4-60848 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Naster, Maximilian A1 - Gleim, Tobias A1 - Wille, Frank T1 - Experimental and Numerical Analyses for the Evaluation of Hydrogen as an Energy Source for Thermal Testing of Transport Packages of Radioactive Material N2 - In this paper we present a new hydrogen-based test rig for an ongoing feasibility study of using hydrogen as an energy source for the thermal testing of transport packages containing radioactive materials. The test rig will be capable of combusting hydrogen for a wide range of different burner geometries, mass flows and if necessary hydrogen blends. As this type of fire test according to the IAEA boundary conditions does not yet exist, a large number of preliminary investigations, safety assessments and calculations must be carried out in order to develop a viable concept for hydrogen fires. In the first step of the feasibility study, the temperature, structure, and radiation of various hydrogen flames are surveyed. In future works, the results will make it possible to design burner frames that are suitable for fire reference tests in order to make comparisons with pool and propane fires used in assessment procedures today. In parallel comparative numerical simulations are conducted to model the thermal behaviour of hydrogen flames using the software package Ansys®. On the one hand, the numerical simulations support the experiments by providing an overview of numerous parameters and the measuring range; on the other hand, they will help with the design of the burner frame in future work. This paper gives an overview in the design and capabilities of the test rig. Furthermore, the results of the parameter studies show that burner geometry and mass flow provide a significant design margin for the thermal shape of the hydrogen flames. In addition, the results of the initial numerical calculations will be used to determine the necessary sensors, the positions, and their operating range. Only the optimal interaction allows a controlled system that permits user-defined hydrogen fires. T2 - PVP2024, Pressure Vessels & Piping Conference CY - Bellevue, Washington USA DA - 29.07.2024 KW - Hydrogen KW - Fire KW - Computational Fluid Dynamics (CFD) KW - IAEA fire test KW - Burner PY - 2024 SN - 978-0-7918-8851-3 SP - 1 EP - 9 AN - OPUS4-60852 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Lars A1 - Scheidemann, Robert A1 - Neumeyer, Tino A1 - Komann, Steffen A1 - Wille, Frank T1 - Tightness Verification Procedures of Welded Lids for Encapsulations for Damaged Spent Nuclear Fuel in the Design Approval Process of Dual-Purpose Cask (DPC) N2 - Damaged spent nuclear fuel (DSNF) can be loaded in Germany in dual-purpose casks (DPC) for transport and interim storage. Therefore, special encapsulations are needed to guarantee a safe handling and a reliable tight closure. These encapsulations must be durable and leak-tight for a possible long interim storage term and the transport thereafter. Because components inside the package containment like these special encapsulations are not accessible within periodical inspections of the DPC. Due to the general design of DPCs for standard fuel assemblies, specific requirements needed to be considered for the design of the special encapsulations for DSNF to ensure the loading in existing package designs. Especially the content of the encapsulations with damaged spent nuclear fuel must be avoided to enter in the inner space of the DPC, due to the possible higher amount of corrosive and radioactive material as well as greater quantities of water, which can be trapped in defect fuel rods. The main difference of the encapsulations for damaged spent nuclear fuel is that they have no replaceable sealing as tightness barrier. They have a specific welded lid. Therefor the tightness needs to be shown in the design approval process for all transport conditions especially for accident conditions, where high internal impact loads can occur. As German competent authority, BAM is responsible for the safety assessment of the mechanical and thermal design, the release of radioactive material and the quality assurance aspects of manufacturing and operation. Concerning the mechanical package design BAM carried out a comprehensive safety assessment for the specific encapsulations during the package design approval process of the commonly used DPC. For the proof of tightness of the welded lid no representative standards are available. For minor loads the German KTA standards can verify the tightness of a weld seam but only for low stresses. For higher impact loads physical tests are required. These tests were performed with representative drop tests and highly sensitive leak tests. The present paper gives an overview of the applied assessments by BAM and points out the main findings of the mechanical design for the welded sealing. Both verification procedures are described, on one hand with German standards for lower loads and on the other hand with physical tests for higher impact loads. The drop tests based on complex numerical pre-calculations by the applicant which result in optimized dimensions and properties of the test specimens and representative drop heights for the drop tests. The horizontal drop orientation with a plane-parallel impact on the unyielding basement was most challenging and led to specific adaptations during preparation and conduction of the drop tests performed by BAM. With leak tests and the corresponding test evaluation, it could be finally approved that the specific welded sealing of an encapsulations for DSNF is tight for all transport conditions. T2 - ASME PVP 2024 CY - Bellevue, WA, USA DA - 28.07.2024 KW - Tightness verification KW - Weld seams KW - Drop tests KW - Encapsulations for damaged spent nuclear fuel KW - Helium leak tests PY - 2024 SN - 978-0-7918-8851-3 SP - 1 EP - 10 CY - New York AN - OPUS4-61351 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Komann, Steffen A1 - Wille, Frank A1 - Linnemann, Konrad A1 - Ramsay, Jeff A1 - Reiche, Ingo T1 - Transport of large nuclear power plant components – new SCO-III regulations and mechanical design assessment N2 - The decommissioning or refurbishment of nuclear facilities necessitates either the storage or disposal of large radioactive components such as steam generators, pressurizers, reactor pressure vessels and heads, and coolant pumps, to list the major contributors. These components or objects are large in size and mass, measuring up to approximately 6 meters in diameter, up to 20 meters in length, and weighing over 400 000 kg. In many situations, the components are transported off-site to a storage, disposal or recycling/treatment facility. Previously, many large objects had to be transported under special arrangement. The latest 2018 edition of the International Atomic Energy Agency (IAEA) Regulations for the Safe Transport of Radioactive Material, No. SSR-6, incorporates regulations for the shipment of contaminated, but not activated large objects as a new category of surface contaminated object, SCO-III, based on the IAEA “performance package” concept. This paper provides background and practical guidance on these regulations. Additionally, first experiences with SCO-III in the approval process are presented. For SCO-III components a mechanical assessment regarding the tests specified in the transport regulations SSR-6 for demonstrating ability to withstand normal conditions of transport is required - a free drop of the package onto an unyielding target and a penetration test have to be investigated. Large components are unique objects; therefore, it is not possible to choose experimental testing as assessment method. The application of a complex numerical analysis for mechanical proof is necessary. The assessment of the loads takes place based on local stress distributions. The large nuclear components have typically been transported in an unpackaged manner, so that the external shell of the component provides the containment wall. The paper will represent the methods, which are used for the evaluation of the mechanical integrity of the object for transport approval. T2 - PVP2024, Pressure Vessels & Piping Conference CY - Bellevue, Washington USA DA - 29.07.2024 KW - Transport KW - Radioaktive Stoffe KW - Rückbau kerntechnischer Anlagen KW - Gefahrgut PY - 2024 SN - 978-0-7918-8851-3 SP - 1 EP - 4 AN - OPUS4-60829 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fürst, Richard A1 - Häßler, Dustin A1 - Stelzner, Ludwig A1 - Hothan, Sascha T1 - Development of an in situ test method to assess the fire resistance of steel members with applied intumes-cent coating N2 - Intumescent coatings are commonly used in civil engineering to improve the fire resistance of steel constructions. Exposed to fire, the intumescent coating reacts and forms a thermal protective char around the steel member. Thus, the heating of the steel is delayed, and a higher fire resistance can be achieved. Generally, the scope of application and the durability of intumescent coatings are described in national approvals or European Technical Assessment (ETA) documents. Due to environmental conditions, intumescent coatings are subjected to ageing effects, which can reduce their durability and thermal protection performance. Available in situ methods to investigate the performance of applied intumescent coatings, such as visual inspection, flame exposure testing, adhesive tensile tests or chemical analysis, are not fully conclusive. Therefore, in the civil engineering practice, there is an increasing demand to verify the fire resistance of existing steel structures with applied intumescent coatings necessary in several cases, e.g., the working life is exceeded, the visual appearance of the intumescent coating changed or the information about the applied product is missing. The research presented in the paper shows the progress of the ongoing research project "INSIST" at BAM [1], where a new in situ method is being developed to assess the actual fire resistance of existing steel structures with applied intumescent coating. The investigation is based on a development of the in situ test procedure and a mobile prototype furnace. T2 - 10th Symposium Structural Fire Engineering CY - Braunschweig, Germany DA - 24.09.2024 KW - In situ KW - Intumescent coating KW - Steel structures KW - Test procedure PY - 2024 SP - 1 EP - 15 AN - OPUS4-61275 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fiedler, Georg A1 - Hering, Marcus A1 - Schubert, T. A1 - Bracklow, F. A1 - Nerger, Deborah A1 - Hille, Falk A1 - Beckmann, B. ED - Wuttke, F. ED - Aji, H. ED - Özarmut, A. T1 - Schädigung von Stahlbetonplatten infolge eines harten Anpralls - Vergleich von halb-empirischen Methoden und experimentellen Ergebnissen N2 - Schutzbauwerke von systemkritischen Infrastruktureinrichtungen wie Betonwände und Betonbarrieren müssen Anprallereignissen oder schweren Unfällen in einem vertretbaren Maße widerstehen können. Anprallereignisse können verschiedenster Natur sein. Hierzu zählen Steinschlag, Fahrzeug- oder Flugzeuganprall oder auch Geschosseinschlag. Geschosseinschläge bzw. Bei den Anprall- oder Impaktereignissen wird zwischen hartem und weichem Anprall unterschieden, bei hartem Anprall verformt sich der Anprallkörper nicht oder nur geringfügig, bei weichem Anprall stark. In diesem Artikel werden Forschungsergebnisse zum harten Anprall auf bewehrte Stahlbetonplatten vorgestellt, welche über die letzten Jahre im Rahmen eines Kooperationsprojekts zwischen dem Institut für Massivbau (IMB) der Technischen Universität Dresden (TUD) und der Bundesanstalt für Materialforschung und -prüfung (BAM) durchgeführt wurden. Auf dem Gelände des Otto-Mohr-Labors (OML) der TUD steht hierfür ein speziell konzipierter Fallturm zur Verfügung. Der Aufbau im Fallturm lässt aktuell druckluftbeschleunigte Impaktversuche mit mittleren Anprallgeschwindigkeiten zu. Die durch Anprall geschädigten Stahlbetonplatten wurden anschließend bei der BAM mit Strahlung tomographisch untersucht. Diese Untersuchungen ermöglichen einen Blick auf die Schädigung und Rissstruktur im Inneren der Stahlbetonplatten. Ein Schwerpunkt der durchgeführten Untersuchung ist der Vergleich von Testergebnissen mit den häufig angewendeten halbempirischen Berechnungsmethoden zu den erforderlichen Wandstärken und den sich daraus ergebenden zulässigen Anprallgeschwindigkeiten. Bei diesem Vorgehen wird auch die mit analytischen Methoden abschätzbare Durchdringungsgeschwindigkeit bzw. Austrittgeschwindigkeit eines Projektils ermittelt und mit den realen Testergebnissen verglichen. Außerdem wird der Einfluss von sowohl externen als auch internen Strukturparametern auf Risse betrachtet und ein Fazit abgeleitet. Weiterhin werden laufende und zukünftige wissenschaftliche Untersuchungen zum Anprall auf Betonstrukturen am IMB und der BAM genannt. T2 - 18. D-A-CH-Tagung CY - Kiel, Germany DA - 13.09.2023 KW - Impakt KW - Harter Anprall an Stahlbetonstrukturen KW - Fallturm PY - 2023 SN - 978-3-930108-15-1 SP - 471 EP - 479 PB - Deutsche Gesellschaft für Erdbebeningenieurwesen und Baudynamik (DGEB) e.V. AN - OPUS4-58341 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Johann, Sergej A1 - Stührenberg, Jan A1 - Tandon, Aditya A1 - Dragos, Kosmas A1 - Bartholmai, Matthias A1 - Strangfeld, Christoph A1 - Smarsly, Kay T1 - Investigation of long-term embedded RFID sensors for structural health monitoring N2 - Ensuring the health of civil engineering structures is crucial for the safety and longevity of the built environment. In this direction, structural health monitoring (SHM) has been increasingly employed, providing insight into the structural behavior, based on sensor data representing structural responses. This paper investigates the plausibility of embedding sensors into concrete structures for SHM, leveraging radio frequency identification (RFID) technology, in an attempt to enable the passive operation of sensors without continuous power supply and to reduce potential sources of interference. In contrast to conventional SHM sensors, the uninterrupted operation of embedded sensors must be ensured because post-installation interventions are either impractical or impossible. RFID technology enables wireless data acquisition and energy transmission without mechanical impact on civil engineering structures, although it may be challenging when RFID sensors are embedded in concrete. This study presents a durable passive embedded RFID sensor system (i.e., a system without batteries), including the selection of components, such as housing and cable materials, suitable for withstanding the aggressive environment of concrete without damaging the sensitive electronics or contaminating the data recorded by the sensors. The proposed sensor system is validated in laboratory tests, the results of which provide insights into the influence of each component and are intended to advance the implementation of embedded sensor systems. T2 - IEEE Sensors 2024 CY - Kobe, Japan DA - 20.10.2024 KW - Structural health monitoring KW - RFID-based sensors KW - Smart sensors KW - Embedded sensors PY - 2024 SN - 979-8-3503-6351-7 DO - https://doi.org/10.1109/SENSORS60989.2024.10785220 SP - 1 EP - 4 AN - OPUS4-62162 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - de Vries, H. A1 - Jacobs, K. A1 - Egyedi, T. A1 - Eto, M. A1 - Fertig, S. A1 - Kanevskaia, O. A1 - Klintner, L. A1 - Koch, Claudia A1 - Mijatovic, I. A1 - Mirtsch, Mona A1 - Morone, P. A1 - Orviska, M. A1 - Riillo, C. A1 - Scaramuzzino, G. ED - Jacobs, K. T1 - Standardization: Towards an agenda for research N2 - Standardization research is a fairly new and is a still-evolving field of research, with possibly major practical ramifications. This article presents a summary of the authors’ subjective views of the most pressing research topics in the field. These include, among others, standards (e.g. incorporation of ethical issues), the potential impact of standards, the corporate management of standardization and legal issues like Intellectual Property Rights (IPR). In addition, gaps have been identified with a respect to a basic understanding of standardization, suggesting a need for better education in the field. KW - EURAS KW - Impact of standards KW - Intellectual property rights (IPR) KW - Research agenda KW - Standardization research PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-467873 DO - https://doi.org/10.4018/IJSR.2018010104 SN - 2470-8542 VL - 16 IS - 1 SP - 52 EP - 59 PB - IGI Global AN - OPUS4-46787 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Reichelt, Manuel T1 - Untersuchungen zu ungeschmiertem Schwingungsverschleiß an 100Cr6-Kugeln gegen 100Cr6-Ebenen N2 - Die vorliegende Doktorarbeit handelt von der Bestimmung und der Untersuchung vom Verschleißvolumen und vom Verschleißkoeffizienten bei ungeschmierten Modellversuchen an 100Cr6-Ebenen und -Kugeln unter Schwingungsbeanspruchung. Die experimentelle Arbeit wurde mittels statistischer Auswertung einer großen Menge von eigenen und früheren Versuchsdaten an fünf Tribometern bei umfangreicher Variation der Beanspruchungsparameter durchgeführt. Ziel war es, die Wiederholbarkeit und Reproduzierbarkeit der experimentellen Ergebnisse zu überprüfen sowie das Archard-Gesetz zu verifizieren. Des Weiteren wurde der Einfluss der Luftfeuchtigkeit auf den Verschleiß untersucht. KW - Verschleißkoeffizient KW - 100Cr6-Stahl KW - Gesetz von Archard KW - Verschleiß-Map KW - relative Luftfeuchtigkeit PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-522664 DO - https://doi.org/10.14279/depositonce-10423 SP - 1 EP - 118 PB - Technische Universität Berlin CY - Berlin AN - OPUS4-52266 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Niemz, P. A1 - Baensch, Franziska A1 - Brunner, A. J. ED - Pavalache-Ilie, M. ED - Curtu, A. L. T1 - Acoustic Emission Analysis And Synchrotron-based Microtomography of glued shear strength samples from spruce wood N2 - To better understanding the failure of adhesive joints tensile tests were carried out on miniature test specimens from Norway spruce in the synchrotron. Urea-formaldehyde resin was used as adhesive. e. For comparison purposes, tensile tests were carried out on solid wood and on bonded miniature tensile shear samples with acoustic emission. The acoustic emission signals of all the experiments occurred with classified pattern recognition. This resulted in two classes of signals for each two frequency peaks. One class consisted of the low-frequency and the other of the higher-frequency peak of higher intensity, but this was essentially independent from the structure (solid wood or plywood) and size scale of the test specimens. The influence of the adhesive layers was determined on wood test specimens on laboratory scale and on miniature test specimens with an adhesive layer and selected fiber orientations. This gave evidence that the sound emission signals from the failure of the adhesive layer presumably of the class with low frequency signals peak in the range of services can be assigned. KW - Wood KW - Bondline KW - In-situ test KW - Acoustic emission KW - Synchrotron tomography PY - 2020 DO - https://doi.org/10.31926/but.fwiafe.2020.13.62.1.7 VL - 13 IS - 62 Part 1 SP - 81 EP - 88 PB - Transilvania University Press, Brasov, Romania CY - Brasov AN - OPUS4-51010 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Maack, Stefan A1 - Benner, Philipp A1 - Kröll, Mirco A1 - Prager, Jens A1 - Daum, Werner A1 - Casperson, Ralf A1 - Heckel, Thomas A1 - Spaltmann, Dirk A1 - et al., ED - Wahlster, W. ED - Winterhalter, C. T1 - Deutsche Normungsroadmap künstliche Intelligenz T1 - German standardization roadmap on artificial intelligence N2 - Im Auftrag des Bundesministeriums für Wirtschaft und Klimaschutz haben DIN und DKE im Januar 2022 die Arbeiten an der zweiten Ausgabe der Deutschen Normungsroadmap Künstliche Intelligenz gestartet. In einem breiten Beteiligungsprozess und unter Mitwirkung von mehr als 570 Fachleuten aus Wirtschaft, Wissenschaft, öffentlicher Hand und Zivilgesellschaft wurde damit der strategische Fahrplan für die KI-Normung weiterentwickelt. Koordiniert und begleitet wurden diese Arbeiten von einer hochrangigen Koordinierungsgruppe für KI-Normung und -Konformität. Mit der Normungsroadmap wird eine Maßnahme der KI-Strategie der Bundesregierung umgesetzt und damit ein wesentlicher Beitrag zur „KI – Made in Germany“ geleistet. Die Normung ist Teil der KI-Strategie und ein strategisches Instrument zur Stärkung der Innovations- und Wettbewerbsfähigkeit der deutschen und europäischen Wirtschaft. Nicht zuletzt deshalb spielt sie im geplanten europäischen Rechtsrahmen für KI, dem Artificial Intelligence Act, eine besondere Rolle. N2 - On behalf of the German Federal Ministry of Economic Affairs and Climate Action, DIN and DKE started work on the second edition of the German Standardization Roadmap Artificial Intelligence in January 2022. With the broad participation and involvement of more than 570 experts from industry, science, the public sector and civil society, the strategic Roadmap for AI standardization was thus further developed. This work was coordinated and accompanied by a high-level coordination group for AI standardization and conformity. The standardization roadmap implements a measure of the German government’s AI Strategy and thus makes a significant contribution to “AI – Made in Germany”. Standardization is part of the AI Strategy and is a strategic instrument for strengthening the innovation and competitiveness of the German and European economies. Not least for this reason, standardization plays a special role in the planned European legal framework for AI, the Artificial Intelligence Act. KW - Digitalisierung KW - Künstliche Intelligenz KW - Datenwissenschaft KW - Normung Roadmap KW - Data science KW - Artificial intelligence KW - Standardization roadmap KW - Digitization PY - 2022 UR - https://www.din.de/resource/blob/1072988/20bf33d405710a703aa26f81362493bb/ausgabe-2-nrm-ki-data.pdf UR - https://www.dke.de/de/arbeitsfelder/core-safety/normungsroadmap-ki SP - 1 EP - 448 PB - Deutsches Institut für Normung (DIN) CY - Berlin ET - 2. AN - OPUS4-56576 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Recknagel, Christoph A1 - Pirskawetz, Stephan T1 - Entwicklung eines Prüfverfahrens zum Alterungsverhalten von Fugenfüllsystemen in Verkehrsflächen (BASt-Projekt "Alterungsverhalten von Fugenfüllsystemen" FE 08.169/2001/FRB) KW - Fugen KW - Fahrbahnbeläge KW - Funktionsfähigkeit KW - Dauerhaftigkeit KW - Unikaler Prüfstand PY - 2005 SP - 1 EP - 95 PB - Bundesanstalt für Materialforschung und -prüfung CY - Berlin AN - OPUS4-11965 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simon, Sebastian A1 - Selleng, C. A1 - von Werder, Julia A1 - Meng, Birgit T1 - Einfluss der thermischen Behandlung auf die Phasenentwicklung und die Eigenschaften von UHPC N2 - UHPC (engl. ultra-high-performance concrete) bietet außergewöhnliche Eigenschaften, die sich durch eine optimierte Wärmebehandlung weiter verbessern lassen. Wie bei normalen Beton beschleunigt eine Wärmebehandlung den Aushärteprozess und reduziert das Schrumpfen. Durch Ausbildung eines dichteren Gefüges wird weiterhin die Druckfestigkeit und die Resistenz gegenüber Umwelteinflüssen erhöht. Die Art der Wärmebehandlung wird durch die Parameter: Temperatur, Druck, Wasserdampfsättigung und Dauer definiert und hat einen entscheiden Einfluss auf die Phasenentwicklung und damit auf die makro- und mikroskopischen Eigenschaften des UHPCs. Auch die Dauer und Art der Vorlagerung des UHPCs vor der thermischen Behandlung sind von Bedeutung. Ziel der vorgestellten Untersuchung war der Vergleich und die Optimierung verschiedener Wärmebehandlungsarten mit Blick auf die Druckfestigkeits- und Phasenentwicklung. Dafür wurden UHPC-Zylinder und Prismen hergestellt und ungeschützt bzw. in Folie eingeschweißt bei 90 °C im Ofen, im Heißwasserbad, sowie alternativ bei 185 °C und 1.1 MPa im Autoklaven wärmebehandelt. Zusätzlich wurde die Vorlagerungs- und die Behandlungszeit systematisch variiert. Die Ergebnisse zeigen, dass eine praxisnahe Wärmebehandlung im Ofen (kurze Vorlagerungs- und Behandlungszeit, Verdunstungsschutz durch Einschweißen in Folie) zwar zu einer stark erhöhten Frühfestigkeit führt, aber die Langzeitfestigkeit wird nicht signifikant erhöht. Erst längere Behandlungszeiten verbunden mit intensiviertem Schutz gegen das Austrocknen führen darüber hinaus zu deutlich erhöhten Langzeitfestigkeiten. Nach der Autoklavierung dagegen wurden Festigkeitszuwächse von bis zu 30 % gemessen. Die röntgenographisch nachgewiesene Phasenentwicklung wird in beiden Behandlungsarten durch die Limitierung des zur Verfügung stehenden Wassers bestimmt. Bei der Wärmebehandlung im Ofen wird das durch den Ettringitzerfall freigesetzte Wasser für die puzzolanische Reaktion der Mikrosilika verbraucht, reicht aber für eine weitere Reaktion der Klinkerphasen nicht aus. Bei der hydrothermalen Behandlung dagegen zeigen die Veränderungen im Phasenbestand sowohl eine Intensivierung der puzzolanischen als auch der hydraulischen Reaktion. Der für autoklavierte Baustoffe charakteristische Tobermorit konnte jedoch nicht im Probeninneren, sondern nur als Belag auf der Probenoberfläche nachgewiesen werden. Ursächlich hierfür ist vermutlich wiederum das zu geringe Wasserangebot im Gefüge des UHPC. T2 - 20. Internationale Baustofftagung ibausil CY - Weimar, Germany DA - 12.09.2018 KW - UHPC KW - Wärmebehandlung KW - Hydrothermale Behandlung KW - XRD KW - Kristalline CSH-Phase KW - Tobermorit KW - Ettringit KW - Hydroxyellestadit KW - Hydrogranat PY - 2018 SN - 978-3-00-059950-7 SP - 1 EP - 10 AN - OPUS4-46176 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Klewe, Tim A1 - Strangfeld, Christoph A1 - Ritzer, Tobias A1 - Kruschwitz, Sabine T1 - GPR Dataset of Moisture Measurements on Building Floors in Laboratory and On-Site N2 - Related work Laboratory Study: Combining Signal Features of Ground-Penetrating Radar to Classify Moisture Damage in Layered Building Floors https://doi.org/10.3390/app11198820 On-Site Study: TBA Doctoral Thesis: Non-destructive classification of moisture deterioration in layered building floors using ground penetrating radar https://doi.org/10.14279/depositonce-19306 Measurement Parameters The GPR measurements were carried out with the SIR 20 from GSSI and a 2 GHz antenna pair (bandwidth 1 GHz to 3 GHz) in common-offset configuration. Each B-Scan consists of N A-Scans, each including 512 samples of a 11 ns time window. Survey lines were recorded with 250 A-Scans/ meter, which equals a 4 mm spacing between each A-Scan No Gains were applied. Folder Description: Lab_dry, Lab_insulDamage, Lab_screedDamage - each contain 168 Measurements (B-Scans) in .csv on 84 dry floors, floors with insulation damage and screed damage. - each floor setup was measured twice on two orthogonal survey lines, indicated by _Line1_ and _Line2_ in the file name. - the file names encode the building floor setup e.g. CT50XP100 describes a 50 mm cement screed with 100 mm extruded polystyrene below - the material codes are CT: cement screed, CA: anhydrite screed, EP: expanded polystyrene, XP: extruded polystyrene, GW: glass wool, PS: perlites further information can be found in the publication https://doi.org/10.3390/app11198820 OnSite_ - 5 folders containing B-Scans on 5 different practical moisture damages - the building floor setup is encoded according to the lab with an additional measurement point numbering at the start and a damage case annotation at the end of the file name with _dry, _insulationDamage and_screedDamage File Description: B-Scans, Measurement files - no header - dimension: 512 x N data point with N beeing the number of A-Scans including 512 samples of a 11 ns time window. - survey lines were recorded with 250 A-Scans/ meter, which equals a 4 mm spacing between each A-Scan Moisture References - Moist_Reference of On-Site Locations include the columns MeasPoint: Measurement point, wt%Screed: moisture content of screed layer in mass percent; wt%Insul: moisture content of insulation layer in mass percent. References were obtained by drilling cores with 68 mm diameter in the center of each survey line. - Moist_Reference_Screed of Lab data include the columns Screed: Screed material and thickness in mm, wt%Screed moisture content of screed layer in mass percent - Moist Reference_Insul of Lab data include the columns Insulation: Insulation material and thickness in mm, water addition in l: water added to the insulation layer in liters, V%Insulation: water added to the insulation layer in volume percent, RH%: resulting relative humidy in the insulation layer during measurement. These References are only avaible for Lab measurements on insulation damages. KW - GPR KW - Material Moisture KW - Building Floors KW - Laboratory KW - On-Site PY - 2024 DO - https://doi.org/10.5281/zenodo.10776684 PB - Zenodo CY - Geneva AN - OPUS4-59609 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klimek, Andre A1 - Hothan, Sascha A1 - Rogge, Andreas T1 - Das Abplatzverhalten von Beton im Zusammenhang mit dem Maßstabseffekt N2 - Beton, als aktuell am meisten verwendeter Baustoff ist nicht brennbar und weist zudem eine sehr geringe Temperaturleitfähigkeit auf. Er eignet sich somit gut für den baulichen Brandschutz. Jedoch neigt Beton im Brandfall zu explosionsartigen Abplatzungen, die zu einer Reduzierung des tragfähigen Querschnitts und sogar zum Versagen des Bauteils führen können. Derzeit werden thermomechanische und thermohydraulische Schädigungsprozesse als die zwei maßgeblichen Ursachen für explosionsartige Abplatzungen angesehen. Diese Schädigungsprozesse sind unter anderem abhängig von der Prüfkörpergröße, dem Wasser-Zement-Wert, der Porosität, der Permeabilität und dem Bewehrungsgrad des Bauteils. Im Rahmen des Vortrags werden die Forschungsarbeiten zum Maßstabseffekt des Abplatzverhaltens von Betonen bei Brandbeanspruchung präsentiert. Zu diesem Zweck wurden Betonprüfkörper aus sechs verschiedenen Betonmischungen in jeweils drei Prüfkörpergrößen einseitig, ohne Behinderung der thermischen Ausdehnung und ohne externe Last im Tunnelbrandprüfstand der BAM untersucht. Dieser unikale Prüfstand ermöglicht die Brandprüfung unterschiedlicher Prüfkörpergrößen unter vergleichbaren Brandbedingungen sowie die simultane Prüfung mehrerer kleinformatiger Betonprüfkörper. Das präsentierte, laufende Promotionsvorhaben basiert auf einem von der DFG geförderten Forschungsvorhaben und darauf aufbauenden Folgeuntersuchungen. Die Ergebnisse des DFG-Vorhabens zeigen einen deutlichen Maßstabseffekt mit einer starken Verringerung der Abplatztiefen bei einer Reduzierung der Prüfkörpergröße. Des Weiteren ist das Abplatzverhalten stark von der Betonmischung abhängig. Vor dem Hintergrund der Ressourcenschonung und Kostenreduzierung verfolgen die auf dem DFG-Vorhaben aufbauenden Untersuchungen das Ziel, das Abplatzverhalten großformatiger Betonprüfkörper durch kleinformatige Betonprüfkörper mit angepassten Randbedingungen nachzustellen. Hierfür wurden zwei Betonmischungen des DFG-Vorhabens verwendet. Die Ergebnisse zeigen, dass durch eine Anpassung der Versuchsrandbedingungen dem Maßstabseffekt entgegengewirkt werden kann. T2 - 7. Symposium 'Heißbemessung - Structural Fire Engineering' CY - Online meeting DA - 14.09.2021 KW - Maßstabseffekt KW - Beton KW - Abplatzen KW - Brand PY - 2021 SP - 1 EP - 12 PB - Technische Universität Braunschweig AN - OPUS4-53528 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Karapanagiotis, Christos T1 - Evaluation of the generalization performance of a CNN-assisted BOFDA system N2 - Brillouin Optical Frequency Domain Analysis (BOFDA) is a powerful and well-established method for static distributed sensing of temperature and strain. Recently, we demonstrated a BOFDA system based on convolutional neural network which shortens the measurement time considerably. In this paper, we apply leave-one-out cross validation to evaluate the generalization performance and provide an unbiased and reliable machine learning model for a time-efficient BOFDA system. T2 - 21. ITG/GMA Fachtagung Sensoren und Messsysteme 2022 CY - Nuremberg, Germany DA - 10.05.2022 KW - Fiber optics sensors KW - BOFDA KW - Brillouin distributed sensing KW - Machine learning PY - 2022 UR - https://www.ama-science.org/direct/tagungsband-sensoren-und-messsysteme-2022 SN - 978-3-8007-5835-7 SP - 289 EP - 292 PB - VDE VERLAG GMBH AN - OPUS4-55183 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Beckenbauer, T. A1 - Root, V. A1 - Radenberg, M. A1 - Nytus, N. A1 - Drewes, B. A1 - Hübner, R. A1 - Recknagel, Christoph A1 - Stöckert, U. A1 - Gottaut, C. T1 - Teilvorhaben VI-II - Optimierung der lärmtechnischen und bautechnischen Wirksamkeit und Nutzungsdauer dichter Asphaltdeckschichten N2 - Straßenverkehr stellt in Deutschland die stärkste Quelle für Lärmbelastungen dar. In 2014 wurde durch den Forschungsverbund Leiser Verkehr ein Bericht zur Situation der Lärmwirkungsforschung in Deutschland veröffentlicht, der den aktuellen Wissensstand zum Einfluss des Verkehrslärms auf die Lebensqualität und die Gesundheit der Bevölkerung dokumentiert. Verschiedene Studien belegen, dass Dauerbelastungen über 65 dB(A) die Betroffenen stark beeinträchtigen. So mindern die hohen Lärmbelastungen nicht nur die Lebensqualität, sondern sie können auch Herz-Kreislauf-Erkrankungen, Schlafstörungen, kognitive Leistungseinschränkungen und Tinnitus verursachen. Gerade wegen des stetig wachsenden Verkehrsaufkommens sind deshalb Strategien zu entwickeln, die die Bevölkerung noch wirksamer vor Straßenverkehrslärm schützen. Aus dem Verkehrsforschungsprogramm der Bundesregierung wurden seit 2001 die Verbundprojekte Leiser Straßenverkehr gefördert. In 2014 wurde das dritte und letzte Verbundprojekt erfolgreich abgeschlossen. Das Verbundprojekt Leiser Straßenverkehr 3 (LeiStra3) hatte sich als zentrales Ziel gesetzt, Maßnahmen zur Minderung des Straßenverkehrslärms in Ballungsräumen zu entwickeln, die dort aufgrund der hohen Bevölkerungsdichte besonders wirkungsvoll sind. Es wurden verschiedene Forschungsansätze verfolgt, die die Geräuschemission an der Lärmquelle nachhaltig reduzieren. Da die Geräuschemission des fließenden Verkehrs maßgeblich durch Wechselwirkungen an der Kontaktstelle von rollendem Reifen und Fahrbahn bestimmt wird, standen die Reifen-Fahrbahn-Geräusche im Fokus der Untersuchungen. Ein Schlüsselelement in LeiStra3 war die Erweiterung des Simulationsmodells SPERoN zur quantitativen Analyse und Vorhersage der Reifen-Fahrbahn-Geräusche. Systematische Analysen von experimentell aufgenommenen Geräuschspektren mit dem Modell zeigten in LeiStra3, dass neben der Anregung von Reifenschwingungen aerodynamische Effekte im Reifen-Fahrbahn-Kontakt maßgeblich an der Geräuschentstehung beteiligt sein müssen. Um diese aerodynamischen Effekte eingehend charakterisieren und kritische Größen identifizieren zu können, mussten auf einem angemieteten Testgelände Modelloberflächen mit speziellen Texturmustern hergestellt werden, die die Entstehungsmechanismen des Rollgeräusches weitgehend getrennt und unabhängig voneinander anregen. Diese Projektstudien bildeten die Grundlage für die Entwicklung eines tragfähigen physikalischen Modells zur Beschreibung der aerodynamischen Effekte. Im Ergebnis von LeiStra3 lassen sich mit SPERoN 2020 nun reale Fahrbahnoberflächen hinsichtlich ihres Einflusses auf die Reifen-Fahrbahn-Geräusche quantitativ analysieren und Designs für neuartige geräuschmindernde Fahrbahnbeläge zuverlässig synthetisieren. Darüber hinaus stellt das Modell ein leistungsfähiges Modul zur Reifenoptimierung zur Verfügung, mit dem der Einfluss der Profilierung und des Reifenaufbaus auf die Schallabstrahlung und den Rollwiderstand untersucht werden kann. Im Fokus stand dabei die Auswahl und Anwendung geeigneter numerischer Verfahren zur Verkürzung der Rechenzeiten, um ein praxistaugliches Optimierungstool bereit zu stellen. Dies ermöglicht eine effiziente Bestimmung von Schallabstrahlung und Rollwiderstand ohne aufwendigen Prototypenbau. Im Regionalverkehr treten vielfach Beschleunigungs- und Abbremsvorgänge auf, zudem werden häufig enge Kurven durchfahren. Um die nötige Traktion zu gewährleisten, müssen die Antriebsachsreifen Profile mit einem hohen Anteil an Querrillen aufweisen. Diese Blockprofile neigen zu einer starken Schwingungsanregung auf der Fahrbahn und damit zu einer höheren Geräuschemission. In LeiStra3 wurden technologische Ansätze erarbeitet, um Rollgeräusche blockprofilierter Lkw-Reifen über die gesetzlichen Grenzwerte hinaus zu reduzieren. Im Straßenversuch hat eine Entwicklungsvariante einen Schalldruckpegel von 74,4 dB(A) erreicht. Gegenüber den aktuellen Produkten wurde damit eine Geräuschreduzierung von etwa 4 bis 5 dB(A) erzielt. Diese Variante wurde etwa ein Jahr nach Projektabschluss auf dem Markt eingeführt. Darüber hinaus wurden in LeiStra3 schallabsorbierende Unterbodenverkleidungen realisiert, die das Rollgeräusch effizient absorbieren und damit den Vorbeifahrtpegel um bis zu 3 dB(A) mindern können. Mit Blick auf Elektrofahrzeuge wurden grundlegende Untersuchungen zur Reifen-Fahrbahn-Wechselwirkung unter Antriebsmoment und zur psychoakustischen Charakterisierung durchgeführt. Einen weiteren Schwerpunkt in LeiStra3 stellte die Entwicklung leiserer Fahrbahnoberflächen dar. Modellrechnungen belegen, dass die Oberflächengestalt einen starken Einfluss auf die Schwingungsanregung des Reifens und die aerodynamischen Vorgänge in der Kontaktfläche zwischen Reifen und Fahrbahn hat. Aus akustischer Sicht ist es günstig, wenn alle Profilspitzen auf einer Ebene liegen und sich plateauartige Texturen mit schluchtenförmigen Vertiefungen ausbilden. Die lärmtechnisch optimierte Asphaltdeckschicht AC D LOA stellte zu Projektbeginn eine neue Entwicklung in der Straßenbautechnik dar und greift diesen Ansatz auf. Die Deckschicht wurde auf Basis einer dichten Asphaltzusammensetzung konzipiert und zeichnet sich durch eine Korngrößenverteilung aus, die auf eine lärmtechnisch wirksame Oberflächentextur abgestimmt ist. Der erste Einbau von AC D LOA erfolgte 2007 in Düsseldorf im Bereich der kommunalen Straßen. In LeiStra3 wurde daran gearbeitet, die Verdichtungswilligkeit des Asphaltmischgutes zu verbessern. Auf diese Weise lassen sich die Dauerhaftigkeit der Deckschicht und damit ihr lärmtechnischer Nutzen erhöhen. Die Erkenntnisse flossen in die neuen „Empfehlungen für die Planung und Ausführung von lärmtechnisch optimierten Asphaltdeckschichten“ ein, die in 2015 von der Forschungsgesellschaft für Straßen- und Verkehrswesen herausgegeben wurden. Der Gussasphalt mit offenporiger Oberfläche (engl.: Porous Mastic Asphalt, PMA) zeigt ebenfalls lärmmindernde Effekte. Im Vergleich zum herkömmlichen Gussasphalt enthält der PMA einen wesentlich höheren Anteil grober Gesteinskörnung. Es entsteht eine Deckschicht, die im unteren Bereich dicht und im oberen Bereich offenporig strukturiert ist. Die akustische Wirksamkeit ergibt sich aus der günstigen Oberflächentextur und einem hohen Hohlraumgehalt. In 2009 wurden erste Erprobungsstrecken gebaut, bei denen Schallpegelmessungen nach der Statistischen Vorbeifahrtmethode eine Lärmminderungen von bis zu 3 dB(A) gegenüber dem Referenzwert zeigten. Auf Grundlage dieser Erkenntnisse wurden in LeiStra3 weiterführende Untersuchungen durchgeführt, um die Ausführungssicherheit des PMA zu erhöhen. Zu diesem Zweck wurde die Mischgutzusammensetzung optimiert und Laborverfahren zur Herstellung von praxisnahen Probekörpern für die Mischgutkonzeption entwickelt. Auf den Bundesautobahnen A 553 bei Brühl, A 3 bei Lohmar und A 5 bei Friedberg konnten Erprobungsstrecken mit verschiedenen PMA-Varianten hergestellt werden. Diese wurden hinsichtlich der Mischgut- und Einbauparameter untersucht. Außerdem wurde in LeiStra3 untersucht, inwieweit der Herstellungsprozess von Elektroofenschlacke (EOS) verbessert werden kann, um bestimmte Kornformen und Korngrößen gezielt zu erzeugen und damit einen hochwertigen Ausgangswerkstoff für den Asphaltstraßenbau zu gewinnen. Im ersten Schritt wurden dazu EOS-Körnungen hinsichtlich ihrer bautechnischen Eignung geprüft und darauf aufbauend das Potenzial verschiedener Prozessrouten bewertet. Mit einer ausgewählten EOSKörnung (EloMinit®) konnten zwei Asphaltdeckschichtvarianten konzipiert und im Mai 2014 auf einem Testfeld eingebaut werden. Die Nachgiebigkeit bestimmt neben der Oberflächentextur und der Offenporigkeit die akustischen Eigenschaften eines Fahrbahnbelags. Ein Ziel in LeiStra3 war es, Asphaltkonstruktionen durch die Nutzung der schwingungsdämpfenden Eigenschaften des Straßenoberbaus geräuschmindernd zu gestalten. Dabei wurden verschiedene Ansätze wie die Integration einer elastischen Dämpfungsschicht oder die Konzeption eines Asphaltmischgutes mit schwingungsdämpfenden Eigenschaften verfolgt. Im Bereich Betonbauweisen stand die Herstellung einer Betondecke mit offenporiger Oberfläche (COPS) im Vordergrund. Die Grundidee des Systems COPS greift die im Asphaltstraßenbau bereits erfolgreich eingesetzte Mischgutkonzipierung mit hohem Grobkornanteil und einer feinkörnigen standfesten Bindemittel-/Mörtelphase auf. Während des Einbauvorganges sinkt der feinkörnige Mörtel nach unten ab, so dass innerhalb der oberen 10 mm der Deckschicht eine offenporige Oberfläche entsteht. In Laborversuchen wurde die Betonrezeptur so eingestellt, dass ein kontrolliertes Absetzverhalten des Zementleimes erreicht wird. Die Betonrezeptur muss möglichst stabil gegenüber Einflüssen von Witterung und Einbau sein, um die vorteilhaften akustischen Eigenschaften der fertigen Betondeckschicht sicherzustellen. Im Verbundprojekt LeiStra3 haben Partner aus Wirtschaft und Wissenschaft in einer interdisziplinär angelegten Forschungsarbeit gemeinsam Lösungen erarbeitet, mit denen das Lärmminderungspotenzial von Reifen, Fahrzeug und Fahrbahn weiter ausgeschöpft werden kann. In allen Arbeitspaketen wurden zahlreiche Ergebnisse und Erkenntnisse gewonnen, die dazu beigetragen haben, die bestehende Technik zu verbessern, die Impulse zur Entwicklung neuer Technologien gesetzt haben und auf deren Basis das Technische Regelwerk fortgeschrieben wurde. KW - Innovation KW - Lärmminderung KW - Straßenbeläge PY - 2017 UR - https://bast.opus.hbz-nrw.de/frontdoor/index/index/docId/2056 N1 - Das Verbundprojekt "Leiser Straßenverkehr 3" wurde durch das Bundesministerium für Wirtschaft und Technologie unter dem Förderkennzeichen 19U10016 A-M gefördert. SP - 312 EP - 381 PB - Bundesanstalt für Straßenwesen (BASt) CY - Bergisch Gladbach AN - OPUS4-54612 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hase, Felix T1 - Design und Aufbau verschiedener Messysteme zur Ermittlung des Feuchtigkeitsprofiles von Estrich N2 - Zur Bestimmung des Feuchtigkeitsgehalts von Fußbodenstrich werden bis zu diesem Zeitpunkt hauptsächlich die Calcium-Carbid Methode (CM) oder das thermogravimetrische Darr-Verfahren angewendet. Für die Anwendung beider Methoden muss der Estrich zerstört werden. Die aus der Messung gewonnenen Messdaten sind jedoch nur einmalig und punktuell. Damit sind diese Verfahren nur bedingt aussagefähig. Des Weiteren variieren die Messdaten von Estrichtyp zu Estrichtyp. Zusammen mit Partnern aus der Forschung und Industrie wird an der Bundesanstalt für Materialforschung und -prüfung (BAM) eine Messkampagne durchgeführt, mit dem Ziel, verschiedene Prüfverfahren zur Bestimmung des Feuchtigkeitsgehalts hinsichtlich ihrer Genauigkeit und Sensitivität zu untersuchen. Hierfür sind zwei neue Messsysteme entwickelt worden, welche auf der zerstörungsfreien Messung basieren. Dafür werden in den Estrich zum einen Sensoren, welche die relative Luftfeuchte messen und zum anderen eine Multiringelektrode, eingebettet. Die Messungen finden in verschiedenen Estricharten und Materialdicken statt, welche bei Normklima mit einer Temperatur von 23 °C und einer relativen Luftfeuchtigkeit von 50 % trocknen. Aus den erhaltenen Messdaten kann ein zeitliches und tiefenabhängiges Feuchtigkeitsprofil des Estrichs erstellt werden. KW - Korrespondierende relative Luftfeuchte KW - Ausgleichsfeuchte KW - Estrichfeuchte KW - Feuchtemesstechnik PY - 2016 SP - 1 CY - Berlin AN - OPUS4-37698 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Gebauer, D. A1 - Gutierrez, B. A1 - Marx, S. A1 - Maack, Stefan A1 - Küttenbaum, Stefan A1 - Pirskawetz, Stephan A1 - Breit, W. A1 - Mechtcherine, V. A1 - Grahl, K. A1 - Thiel, T. A1 - Schickert, M. A1 - Krüger, M. T1 - Interrelated data set from nondestructive and destructive material testing of concrete compressive strength specimens N2 - This data set contains three different data types obtained from concrete specimens. For each specimen, the rebound numbers, ultrasonic data (ultrasonic velocity, time of flight), and destructive concrete strength are given. Two kind of specimen geometries were tested: cubes and drilled cores. The files are labeled according to the specimen geometry as "cube" or "core" and the type of measurement data as "compressive_strength", "rn_R" and "rn_Q" for rebound numbers as well as "us" for ultrasonic data. The ultrasonic data were generated by six independent laboratories, the rebound numbers by five independent laboratories and the destructive tests by one laboratory. The designation of each specimen establishes the relationship between the different data types. KW - Non-destructive testing KW - Rebound number KW - Ultrasonic pulse velocity KW - Compressive concrete strength KW - Interlaboratory comparison PY - 2023 DO - https://doi.org/10.7910/DVN/AFCITK PB - Harvard College CY - Cambridge, MA, USA AN - OPUS4-57499 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Mike A1 - Völzke, Holger A1 - Nieslony, Gregor T1 - Consequences of an imperfectly mounted reinforcement cage in a generical cylindrical concrete container during mechanical specimen tests N2 - By highest court decision in 2007 the issued license for the Konrad repository (a former iron ore mine) for low and intermediate level radioactive waste was finally confirmed. Since then, the site is improved, prepared and equipped for the currently planned start of waste package emplacement by 2029. The Bundesanstalt fuer Materialforschung und -pruefung (BAM, Federal Institute for Materials Research and Testing) is regularly contracted by the Bundesgesellschaft für Endlagerung (BGE, Federal Company for Radioactive Waste Disposal) as the responsible authority for waste product control, waste container design testing, and waste package acceptance. In this context BAM is mainly responsible for design testing of various container types including the evaluation quality assurance measures for container manufacturing. In the written Konrad disposal requirements all acceptance criteria for potential final disposal containers are defined. In addition to general requirements concerning container design, materials, dimensions and others, specific mechanical load scenarios the casks have to withstand are derived from an analysis of the on-site handling and emplacement procedures. Drop tests from different heights under consideration of the most damaging drop orientation and a stacking test are two examples for safety demonstrations that have to be performed during the container design testing procedure to qualify the respective container type. The containers, whether cubic or cylindrical containers, can be made from different materials like ductile cast iron, reinforced concrete or as welded construction from steel plates and profiles. In case of concrete containers the reinforcement has the function to absorb tensile forces the concrete is not able to withstand by its own. Because of manufacturing imperfections of cylindrical concrete waste containers manufactured already decades ago, the reinforcement cages are not always exactly, axisymmetrically positioned when they were poured. This inspired BAM to perform various ABAQUS finite-element (FE) simulations by using the example of a simplified cylindrical container design with generic dimensions and pure elastic material properties. As outcome the stress conditions in the container during the drop test impact under different drop positions and during the stacking test were investigated and are explained and illustrated in this contribution. Different reinforcement cage positions were calculated and compared. On the basis of the calculated tensile and compressive stress distributions suggestions are derived on how a cylindrical concrete container with an imperfectly placed reinforcement cage has to be oriented for a drop or stacking test to ensure the most damaging test scenario. T2 - ASME 2024 Pressure Vessels & Piping Conference CY - Bellevue, Washington, USA DA - 28.07.2024 KW - Container design testing procedure KW - Reinforced concrete containers KW - Drop test KW - Stacking test KW - Imperfectly mounted reinforcement cage KW - Finite-element-analysis PY - 2024 SN - 978-0-7918-8851-3 DO - https://doi.org/10.1115/PVP2024-123797 VL - 5 SP - 1 EP - 8 PB - ASME CY - New York City, USA AN - OPUS4-62558 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Munsch, Sarah Mandy A1 - Strangfeld, Christoph A1 - Kruschwitz, Sabine T1 - Interpretation of NMR signals from partly saturated sandstones N2 - The development of prevention methods and the detection of moisture related damages in buildings and transport infrastructure at an early stage are current issues in the field of non-destructive testing in civil engineering. Especially the subject of partial saturation requires further research since it is more likely to occur than full saturation of the material. In fact, partial saturation in porous media is even more complicated because both fully and partly saturated pores (i.e. pores in which the surfaces are covered with thin water layers) are present. As the non-destructive method nuclear magnetic resonance (NMR) enables the measurement and quantification of relative low moisture contents, it is suitable for the investigation of partly saturated porous building materials. Nevertheless, the differentiation between partly and fully saturated pores is still a challenge. Therefore, in this study, we investigate two sandstones types (Bozanov and Schönbrunner sandstone) at various defined saturation states by using NMR. Furthermore, we measure the relative humidities within the samples and compute the water layer thicknesses (WLT) along the pore walls of all pore sizes to calculate the corresponding degree of pore saturation. To finally assign the NMR signals to pore sizes and to differentiate between partly and fully saturated pores, the water content distribution obtained from the WLT calculation is used for calibration of the relaxation-time distribution. In this extended abstract, selected results only for Schönbrunner sandstone are presented. T2 - ISEMA 2021 CY - Online meeting DA - 26.07.2021 KW - NMR KW - Relative humidity KW - Water layer thickness KW - Partial pore saturation KW - Pore-size distribution PY - 2021 SN - 978-1-7281-8736-5 VL - 2021 SP - 111 EP - 115 PB - IEEE AN - OPUS4-53045 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weise, Frank A1 - Müller, Urs T1 - Baustoffliche Untersuchungen am Tuffstein des Charlottenburger Tors T2 - ARKUS-Tagung "Denkmalgestein Tuff" CY - Koblenz, Deutschland DA - 2006-05-10 KW - Denkmalpflege KW - Tuff KW - Schadensanalyse KW - Innovative Prüftechnik PY - 2006 IS - IFS-Bericht Nr. 22 SP - 59 EP - 64 PB - IFS CY - Mainz AN - OPUS4-14400 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Simon, Franz-Georg A1 - Scholz, Philipp A1 - Barqawi, Haitham T1 - Einfluss von Geokunststoffen auf die aquatische Umwelt N2 - Im Rahmen des Projekts konnte gezeigt werden, dass Geokunststoffe bei ausreichender Stabilisierung Einsatzdauern von über 100 Jahren besitzen. Es werden keine Stoffe freigesetzt, die für Wasserorganismen schädlich sind. An den Ostseestränden im Gebiet Kaliningrad werden nennenswerte Mengen von Kunststoffresten gefunden, die zum Teil aus Küstenschutzbauwerken stammen. Ursache ist hier jedoch eine verfehlte Materialauswahl. Hauptsächlich stammen die Kunststoffreste am Strand jedoch aus unsachgemäße Abfallbehandlung. KW - Geokunststoffe KW - Mikroplastik KW - Autoklaventest KW - Ökotoxtests PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-556431 DO - https://doi.org/10.2314/KXP:1813230285 SP - 1 EP - 15 AN - OPUS4-55643 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Duarte, Larissa A1 - Madia, Mauro A1 - Zerbst, Uwe T1 - The effect of the environmental conditions on the threshold against fatigue crack propagation N2 - The threshold against fatigue crack propagation (ΔKth) is a crucial parameter for the damage tolerance assessment of engineering components subjected to cyclic loading and it is composed by two distinct components, one intrinsic, dependent on the elastic material properties and the lattice type, and one extrinsic, related to the occurrence of crack closure effects. An important issue is that several factors can influence ΔKth and, in general, the fatigue crack propagation behavior. In this work, the influence of the experimental procedure, air humidity, stress ratio and test frequency on da/dN-ΔK data has been investigated. Results are discussed with their potential causes and consequences on the calculations of the residual lifetime. KW - Fatigue crack propagation threshold KW - Crack closure effect KW - Experimental procedure KW - Environmental conditions PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-544905 DO - https://doi.org/10.1016/j.prostr.2022.03.030 VL - 38 SP - 292 EP - 299 PB - Elsevier B.V. AN - OPUS4-54490 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erning, Johann Wilhelm T1 - Sprechen wir über Korrosion - aber richtig! N2 - Die Korrosion in ihren zahlreichen Erscheinungsformen beschäftigt Fachleute und Laien. Um-so wichtiger ist es, die einzelnen Phänomene korrekt und eindeutig zu benennen. Nur so kann man eine saubere Beschreibung der Korrosionsvorgänge erreichen und damit in der wörtlichen und schriftlichen Kommunikation richtig verstanden werden. An zahlreichen Beispielen wird der richtige und normgemäße Sprachgebrauch beschrieben. T2 - Korrosionsschutz in der maritimen Technik CY - Hamburg, Germany DA - 29.01.2020 KW - Korrosion KW - Nomenklatur PY - 2020 SN - 978-3-935406-72-7 SP - 7 EP - 11 AN - OPUS4-50327 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kempf, A. A1 - Hilgenberg, Kai T1 - Einfluss der Porosität auf die Duktilitätseigenschaften von additiv gefertigtem AlSi10Mg N2 - Die Werkstoffeigenschaften im selektiven Laserstrahlschmelz-Verfahren hergestellter Bauteile werden von einer Vielzahl technologischer Parameter beeinflusst, sodass sich die Fertigungsgüte verschiedener Anlagen voneinander unterscheiden kann. Vor diesem Hintergrund wurde in der vorliegenden Arbeit untersucht, inwiefern sich durch verschiedene nachgelagerte Wärmebehandlungen die Mikrostruktur und die quasistatischen Festigkeitseigenschaften von Proben aus der Aluminiumlegierung AlSi10Mg, die mit verschiedenen Anlagen, Pulvern, Belichtungsstrategien und Prozessparametern gefertigt wurden, harmonisieren lassen. Die Versuche zeigten u.a., dass die erheblichen Festigkeitsunterschiede im Ausgangszustand unabhängig von der angewendeten Wärmebehandlungsroute aufgehoben wurden. Dennoch wurden signifikante Unterschiede in der Duktilität ermittelt. Anhand umfangreicher Bruchflächenanalysen konnte nachgewiesen werden, dass die in der Bruchfläche ermittelte Porosität eine lineare Korrelation zu der Bruchdehnung aufwies. T2 - 5. Tagung des Arbeitskreises Additiv gefertigte Bauteile und Strukturen CY - Online Meeting DA - 04.11.2020 KW - Wärmebehandlung KW - Additive Fertigung KW - Laser powder bed fusion KW - AlSi10Mg KW - Ringversuch PY - 2020 SN - 2509-8772 VL - 405 SP - 93 EP - 104 AN - OPUS4-51657 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hofmann, Detlef A1 - Basedau, Frank A1 - Heidenreich, F. A1 - Herten, M. T1 - Verwendung faseroptischer Messtechnik im Zuge wiederholter Eignungsprüfungen an Verpressankern N2 - Im Rahmen des Ausbaus des Dortmund-Ems-Kanals wurden an der Schleuse Gleesen Forschungsanker installiert, die Rückschlüsse auf das Tragverhalten in Folge des chemischen Angriffs kalklösender Kohlensäure geben sollen. Die Forschungsanker werden seit der Erstellung im Jahr 2017 mit verteilter faseroptischer Sensorik während der jährlichen Eignungsprüfungen untersucht. Die Ergebnisse der Jahre 2017 bis 2019 werden im Folgenden dargestellt. T2 - Messen in der Geotechnik 2020 CY - Braunschweig, Germany DA - 20.02.2020 KW - Faseroptische Sensorik KW - Rayleigh Rückstreuung KW - Verpressanker KW - Chemischer Angriff KW - Rissbildung PY - 2020 SN - 978-3-948141-02-8 DO - https://doi.org/10.24355/dbbs.084-201912181435-0 IS - 110 SP - 297 EP - 323 AN - OPUS4-51687 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Duarte, Larissa A1 - Zerbst, Uwe A1 - Madia, Mauro T1 - Vergleichende Untersuchungen zum intrinsischen Schwellenwert der da/dN-ΔK-Kurve N2 - Für die Bestimmung der Restlebensdauer zyklisch beanspruchter Bauteile kommt dem Schwellenwert für Ermüdungsrissausbreitung, Δ𝐾𝑡ℎ, und dem sich anschließenden Schwellenwertbereich der 𝑑𝑎𝑑𝑁⁄−Δ𝐾-Kurve große Bedeutung zu. Dem stehen Unsicherheiten bei der Bestimmung und Analyse gegenüber. Der Aufsatz befasst sich mit der Ermittlung des sogenannten intrinsischen Schwellenwerts, der als robuster Eingangsparameter für eine „rissschließfreie“ Analyse der Restlebensdauer von entscheidender Bedeutung ist. T2 - 53. Tagung des DVM-Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Online meeting DA - 18.02.2021 KW - Schadenstolerante Bauteilauslegung, Restlebensdauer, intrinsischer Schwellenwert gegen Ermüdungsrissausbreitung PY - 2021 SN - 2366-4797 SP - 211 EP - 220 PB - Deutscher Verband für Materialforschung und -prüfung e.V. (DVM) CY - Berlin AN - OPUS4-52704 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Duarte, Larissa A1 - Zerbst, Uwe A1 - Madia, Mauro T1 - Der Schwellenwert der da/dN-∆K-Kurve als Auslegungskriterium für die Bauteilbewertung N2 - Für die Bestimmung der Restlebensdauer zyklisch beanspruchter Bauteile kommt dem Schwellenwert für Ermüdungsrissausbreitung ∆Kth und dem sich anschließenden Schwellenwertbereich der da/dN-∆K-Kurve große Bedeutung zu. Dem stehen Unsicherheiten bei der Bestimmung und Analyse gegenüber. Der Aufsatz befasst sich mit der Ermittlung des sogenannten intrinsischen Schwellenwerts, der als robuster Eingangsparameter für eine „rissschließfreie“ Analyse der Restlebensdauer von entscheidender Bedeutung ist. T2 - Tagung Werkstoffprüfung 2020 CY - Online meeting DA - 03.12.2020 KW - Schadenstolerante Bauteilauslegung, KW - Intrinsischer Schwellenwert gegen Ermüdungsrissausbreitung KW - Restlebensdauer PY - 2020 DO - https://doi.org/10.48447/WP-2020-025 SP - 1 EP - 8 AN - OPUS4-52788 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Kalady, Mohammed Fayis A1 - Schultz, Johannes A1 - Weinel, Kristina A1 - Wolf, Daniel A1 - Lubk, Axel T1 - Localization of Hybridized Surface Plasmon Modes on Random Gold Nanoparticle Assemblies N2 - Assemblies of plasmonic nanoparticles (NPs) support hybridized modes of localized surface plasmons (LSPs), which delocalize in geometrically well-ordered arrangements. Here, the hybridization behavior of LSPs in geometrically completely disordered arrangements of Au NPs fabricated by an e-beam synthesis method is studied. Employing electron energy loss spectroscopy in a scanning transmission electron microscope in combination with numerical simulations, the disorder-driven spatial and spectral localization of the coupled LSP modes that depend on the NP thickness is revealed. Below 0.4nm sample thickness (flat NPs), localization increases towards higher hybridized LSP mode energies. In comparison, above 10nm thickness, a decrease of localization (an increase of delocalization) with higher mode energies is observed. In the intermediate thickness regime, a transition of the energy dependence of the localization between the two limiting cases, exhibiting a transition mode energy with minimal localization, is observed. This behavior is mainly driven by the energy and thickness dependence of the polarizability of the individual NPs. KW - Plasmonics KW - Electron-Energy Loss Spectroscopy KW - Discrete Dipole Approximation KW - Nanoparticles PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-618323 DO - https://doi.org/10.48550/arXiv.2410.10514 SP - 1 EP - 8 PB - Cornell University CY - Ithaca, NY AN - OPUS4-61832 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Yang, Fan A1 - Meng, Xiangmeng A1 - Bachmann, Marcel A1 - Artinov, Antoni A1 - Putra, Stephen Nugraha A1 - Rethmeier, Michael T1 - Numerical analysis of the influence of an auxiliary oscillating magnetic field on suppressing the porosity formation in deep penetration laser beam alloys of aluminum alloys N2 - The contactless magnetohydrodynamic technology has been considered as a potential and promising method to improve the weld qualities of deep penetration laser beam welding. In this paper, numerical investigations are conducted to study the influence of the auxiliary oscillating magnetic field on the porosity suppression in laser beam welding of 5754 aluminum alloy. To obtain a deeper insight into the suppression mechanism, a three-dimensional transient multi-physical model is developed to calculate the heat transfer, fluid flow, keyhole dynamic, and magnetohydrodynamics. A ray tracing algorithm is employed to calculate the laser energy distribution on the keyhole wall. A time-averaged downward Lorentz force is produced by an oscillating magnetic field. This force acts in the molten pool, leading to a dominant downward flow motion in the longitudinal section, which blocks the bubble migration from the keyhole tip to the rear part of the molten pool. Therefore, the possibility for the bubbles to be captured by the solidification front is reduced. The electromagnetic expulsive force provides an additional upward escaping speed for the bubbles of 1 m/s ~ 5 m/s in the lower and middle region of the molten pool. The simulation results are in a good agreement with experimental measurements. Based on the results obtained in this study, a better understanding of the underlying physics in laser beam welding enhanced by an auxiliary oscillating magnetic field can be provided and thus the welding process can be further optimized reducing the porosity formation. T2 - 13th International Seminar Numerical Analysis of Weldability CY - Seggau, Austria DA - 04.09.2022 KW - Deep penetration laser beam welding KW - Oscillating magnetic field KW - Numerical simulation KW - Porosity KW - Molten pool behaviour PY - 2023 SN - 2410-0544 VL - 13 SP - 237 EP - 254 PB - Verlag der Technischen Universität Graz AN - OPUS4-58804 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Fliehe, Marc A1 - Steinke, Ingo A1 - Koch, Claudia A1 - Elert, Anna Maria A1 - Meyer, Lena T1 - Konformität digital nachweisen: Maschinenlesbare Zertifikate für mehr Vertrauen und Effizienz N2 - Die fortschreitende Digitalisierung und die Komplexität globaler Lieferketten erfordern ein Umdenken in der Qualitätsinfrastruktur (QI). Papierbasierte Prozesse werden den Anforderungen der digitalen Wirtschaft nicht mehr gerecht. Um wettbewerbsfähig zu bleiben und Handelshemmnisse abzubauen, müssen diese Strukturen modernisiert werden. Digitale, maschinenlesbare Zertifikate ermöglichen eine Neugestaltung der Qualitätssicherung entlang globaler Wertschöpfungsketten. Sie bieten Verbraucher*innen, Wirtschaft und Behörden erhebliche Vorteile, erleichtern die Automatisierung von Konformitätsprüfungen und unterstützen die Einhaltung komplexer regulatorischer Anforderungen. KW - Digitale Zertifikate KW - Maschinenlesbare Zertifikate KW - Digitale Transformation KW - Digitalisierung KW - Qualitätsinfrastruktur KW - Konformitätsbewertung PY - 2024 SP - 1 EP - 16 CY - Berlin AN - OPUS4-62043 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weise, Frank T1 - Verfahren der Feuchtemessung T2 - DAfStb-Fachtagung "Frostwiderstand von Beton in Labor und Praxis" CY - Düsseldorf, Deutschland DA - 2005-09-29 KW - Baustoffe KW - Feuchtemessung KW - Zerstörungsarme und zerstörungsfreie Prüfverfahren PY - 2005 SP - 69 EP - 82 PB - Verein Deutscher Zementwerke CY - Düsseldorf AN - OPUS4-11594 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Jansen, D. A1 - Bald, S. A1 - Birbaum, J. A1 - Küttenbaum, Stefan A1 - Krause, J. A1 - Maack, Stefan A1 - Pichottka, S. A1 - Scherkenbach, M. A1 - Strangfeld, Christoph A1 - Villaret, K. A1 - Wöllenstein, J. T1 - Sensors for the structural assessment of roads N2 - This working paper summarises the current state of knowledge and research on the application of sensors in road pavements, designed to record input quantities and characteristics for structural assessment. In this working paper, sensors generally refer to technical equipment that can used to record the values of physical quantities and display them for interpretation. The working paper deals with every type of sensor that is permanently connected to the road, i.e. sensors that are installed – in the bound and unbound courses of the superstructure as well as in the sub-base/sub-structure, – next to or above the road (for example on masts) and can contribute to structural recording and its subsequent assessment. This can also include sensors that are primarily used for a different purpose (e.g. traffic control). However, this working paper only describes the application of sensors that are installed primarily for other purposes for the sake of completeness; special publications (e.g. Notes on detection technologies in road traffic) are available for the respective installation situations. KW - Asphalt KW - Concrete KW - Measurement chain KW - Sensor technology KW - Condition assessment PY - 2024 SP - 1 EP - 36 PB - Forschungsgemeinschaft für Straßen- und Verkehrswesen e.V. CY - Köln AN - OPUS4-60084 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Duwe, C. A1 - Schnell, A. A1 - Rübner, Katrin T1 - Recycling-Baustoffe aus Shredder-Sanden N2 - Bei der Aufbereitung von Rückständen aus der Zerkleinerung von Altfahrzeugen, weißer Ware und Mischschrotten, wie zum Beispiel durch das patentierte VWSiCon-Verfahren, fallen sogenannte Shredder-Sande an. Es handelt sich dabei um heterogene Gemische mit Korngrößen unter 5 mm. Bislang werden diese Shredder-Sande als inerter Reststoff im Bergeversatz verfüllt. Durch die Novellierungen im Kreislauf-Wirtschaftsgesetz ist fraglich, ob dieser Verwertungsweg in Zukunft noch als Recycling gewertet werden wird. So müssen sich Produkthersteller und Verwerter nun auch mit diesem Stoffstrom auseinandersetzen, um die für die Eingangsstoffe definierten Recyclingquoten erfüllen zu können. Dazu müssen neue Strategien zur Aufbereitung und Verwertung entwickelt werden, um aus dem heterogenen Stoffgemisch aus mineralischen, metallischen und organischen Bestandteilen wieder nutzbare Fraktionen zu erzeugen. T2 - R’13 - Fachtagung Recycling CY - Weimar, Germany DA - 2013-09-19 KW - Shreddersande KW - VW-SiCon-Verfahren KW - Recyclingbaustoffe KW - Leichte Gesteinskörnungen KW - Recycling KW - Nachhaltigkeit PY - 2013 UR - http://www.abw-recycling.de/r13/Duwe_TUC_Shredder-Sande_R13.pdf IS - Paper 14 SP - 1 EP - 11 PB - Bauhaus-Univ. CY - Weimar AN - OPUS4-30083 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schwettmann, K. A1 - Stephan, D. A1 - Nytus, N. A1 - Radenberg, M. A1 - Weigel, Sandra T1 - Post carbon road - The endless cycle of bitumen reuse N2 - In Germany, the reuse of asphalt has a long tradition. Since the 1980s, the reclaimed asphalt has been recycled achieving a reuse rate of around 90% and thus a very high value in the last years. In the future, instead of the amount, the quality of the reclaimed asphalt will be more important because the recycled asphalt will be reused again and again. Thus, these asphalt mixes are in the second or even third cycle of reuse. Concerning this situation, the question arises if asphalt can be reused several times without any loss in quality. An important factor affecting the asphalt quality is the binder bitumen. During the production, construction and service life, the ageing of this binder occurs causing a hardening of the bitumen. To compensate this hardening, additives for the reclaimed asphalt in terms of rejuvenation agents (rejuvenators) gain in importance. With these rejuvenators, the physical properties of bitumen can be modified e.g. the hardness and the stiffness reduced. However, the mechanism of the rejuvenation agents and the effects of the bitumen chemistry are largely unknown because the composition of the products varies very strongly. But with growing knowledge about these mechanisms and effects of the rejuvenation agents, the chemical composition and thus the physical and ageing behavior of bitumen can be targeted modified by the use of suitable rejuvenators. In this work, the actual results of the project Postcarbone road should be presented including investigations about the chemical and physical mechanisms as well as the efficiency of different rejuvenators. Further, a model for the cyclic reuse of bitumen should be developed. Based on this model, the choice of a suitable rejuvenation agent for the considered bitumen or rather asphalt should be possible. The project Postcarbone road (392670763) is funded by the German Research Foundation (DFG). T2 - 7th Eurasphalt and Eurobitume Comgress CY - Online meeting DA - 15.06.2021 KW - Bitumen KW - Multiple ageing and rejuvenation KW - Conventional testing KW - DSR KW - BBR KW - FTIR KW - Asphaltene content KW - Column chromatography PY - 2021 SP - 1 EP - 14 AN - OPUS4-53490 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braml, T. A1 - Wimmer, J. A1 - Maack, Stefan A1 - Küttenbaum, Stefan A1 - Kuhn, T. A1 - Reingruber, M. A1 - Gordt, A. A1 - Hamm, J. ED - Krieger, J. T1 - Datenablage als Grundlage für den digitalen Zwilling eines Bauwerks – Verwaltungsschale BBox N2 - Der Weg zur digitalen Brücke ist eingeschlagen. Im Bereich der Planung, Bauüberwachung und -ausführung wird aktuell das Building Information Modelling (BIM) eingeführt. Ist eine Brücke in der Baulast von Bund und Ländern errichtet, wird ihr Zustand im Zuge von wiederkehrenden Bauwerksprüfungen nach DIN 1076 lückenlos überwacht. Abgespeichert werden die Informationen der Überwachung in einer Datenbank (ASB-ING Teilsystem Bauwerksdaten). Aus dieser Datenbank können anschließend relevante Informationen in ein objektspezifisches Bauwerksbuch überführt werden. In dieser Datenbank werden im Vorfeld definierte Daten abgespeichert. Reine Messdaten oder aber auch die verwendeten ingenieurtechnisch-physikalischen Modelle verbleiben in der Regel bei den beauftragen Dienstleistern. Zusammengefasst existieren verschiedene parallele Insellösungen der Informationsablage. Gegenstand verschiedener Forschungsanstrengungen ist es nun Lösungen zu finden, die einen ganzheitlichen Ansatz für den Informationsfluss von der Errichtung über den Betrieb bis hin zum Abbruch eines Bauwerkes sicherstellen. Im Rahmen einer prototypischen Entwicklung wird auf Grundlage, des für die Industrie 4.0 entwickelten open source Software Framework Eclipse BaSyx, ein möglicher Lösungsansatz – die Verwaltungsschale BBox (Bridge Box) - präsentiert. Dieser Lösungsansatz stellt das physikalisch-ingenieurtechnische Modell zur Zustandsbewertung der Brücke gedanklich in den Mittelpunkt. Unter der Voraussetzung einer durchgängigen Digitalisierung der gesamten Prozessschritte innerhalb der Lebensdauer der Brücke, kann jeder Planungs- und Fertigungsschritt, die Instandhaltung einschließlich des Rückbaus erfasst werden. Das Besondere hierbei ist, dass auch die Grundlagen der Bewertung, wie Messdaten, mit abgespeichert werden. Die Modellstruktur der Verwaltungsschale erlaubt hierbei eine bedarfsgerechte Granularität hinsichtlich der Messdaten auf allen virtuellen Ebenen, um das physikalisch-ingenieurtechnisch Modell mit Daten zu versorgen. Die gewählte Form der Datenablage bildet den Grundstein für zukünftige KI-Auswertungen z.B. mit den Methoden des Maschinellen Lernens (ML). Der Zugriff auf die dafür jeweils benötigten Daten wird durch die Ablage der Daten einschließlich Metadaten und den Einsatz einer Standard S3 Schnittstelle stark vereinfacht. Der Beitrag stellt die Entwicklung und die Systemarchitektur der BBox am Beispiel von 2 Projekten dar. T2 - 1. Fachkongress Digitale Transformation im Lebenszyklus der Verkehrsinfrastruktur CY - Esslingen, Germany DA - 29.05.2021 KW - Brücke KW - Digitalisierung KW - Digitaler Zwilling KW - Datenablage PY - 2021 UR - https://elibrary.narr.digital/article/99.125005/dtv202110075 SN - 2748-9221 IS - 1 SP - 75 EP - 84 PB - expert verlag AN - OPUS4-56159 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weise, Frank A1 - Krütt, Enno A1 - Meng, Birgit T1 - AKR unter kombinierten Einwirkungen - Rissbildungs- und Transportmechanismen N2 - Die vorstehend dargestellten Untersuchungen lassen sich wie folgt zusammenfassen: • Mit dem für die mechanische Vorschädigung entwickelten Versuchsstand und gewählten Prüfregime können die für die ermüdungsinduzierte Schadensevolution typische stabilisierende und stabile Phase in der auf Zug beanspruchten Betonrandzone gut abgebildet werden. So wurde dort zum Beispiel, ausgehend von dem hier gewählten praxisnahen Belastungsregime, mit Ultraschall in der Ruhephase durch das Trockenschwingen ein maximaler Abfall des relativen dynamischen E-Moduls von ca. 8 - 10 % ermittelt. • Mit aufbauenden kapillaren Aufsaugversuchen wurde gezeigt, dass die erzeugte Betondegradation zu einer moderaten Erhöhung der Aufnahme des Prüfmediums führt. • Zur Bewertung der Auswirkungen einer alleinigen Vorschädigung (Trockenschwingen) auf die schädigende AKR mittels Performance-Prüfung ist die Klimawechsellagerung aufgrund der einseitigen Tausalzbeaufschlagung am besten geeignet. Die hier ermittelten Dehnungsverläufe lassen auf einen moderaten Einfluss der mechanischen Vorschädigung auf die AKR schließen. • Die zusätzlich im Kontext der Nasschwingversuche durchgeführten 60°C Betonversuche zeigen, dass die zyklische Beanspruchung vor und nach dem Aufbringen der Tausalzlösung die schädigende AKR gleichfalls moderat erhöht. In derzeit laufenden ergänzenden Untersuchungen wird der separate Einfluss der ermüdungsinduzierten Rissbildung auf die schädigende AKR an homogen, stärker geschädigten Prüfkörpern mit einem hohen inneren AKR-Schädigungspotenzial im 60°C Betonversuch grundhaft analysiert. Zusätzlich wird gegenwärtig der Einfluss der degradierten Betonrandzone auf die Dehnungsverteilung an großformatigen Prüfkörpern über die Höhe im 40°C Betonversuch vertiefend für die makroskopische Modellierung untersucht. T2 - 20. Internationale Baustofftagung ibausil CY - Weimar, Germany DA - 12.09.2018 KW - Betonfahrbahndecke KW - Alkali-Kieselsäure-Reaktion KW - Tausalz KW - LIBS KW - MRFA KW - Nasschemie KW - ZfP PY - 2018 SN - 978-3-00-059950-7 SP - 1 EP - 13 AN - OPUS4-46174 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gaal, Mate A1 - Ahmadzadeh, Majid A1 - Weise, Matthias T1 - Focussed sound field of thermoacoustic transmitters N2 - The thermoacoustic effect offers a method for selectively exciting broadband and focused ultrasonic waves, which can be utilized in air-coupled ultrasonic testing of lightweight components that might otherwise sustain damage from liquid couplants. Thermoacoustic transmitters are composed of an electrically conductive layer deposited on an insulating substrate. When electrical pulses are applied, the conductive layer heats, briefly warming the adjacent air and inducing thermal expansion, which generates an acoustic wave. In testing applications, the thermoacoustic transmitter is positioned at the focal distance to the structure under examination, where the resolution of the resulting ultrasonic image is influenced by the focus diameter. To optimize imaging resolution, understanding the focusing characteristics of thermoacoustic transmitters is essential. In this study, thermoacoustic transmitters with an indium tin oxide (ITO) layer on a quartz glass substrate were developed. Geometrical parameters, including substrate curvature and conductive layer thickness, along with electrical excitation parameters, were systematically varied to investigate their impact on the sound field up to approximately 1 MHz. The results indicate that, among the parameters studied, substrate curvature exerts the most significant influence on the sound field. T2 - DAS-DAGA Tagung CY - Kopenhagen, Danmark DA - 17.03.2025 KW - Air-coupled ultrasound KW - Thermoacoustic transmitter KW - Focussed transducer PY - 2025 SP - 1 EP - 4 AN - OPUS4-63092 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heimann, Jan A1 - Charmi, Amir A1 - Karapanagiotis, Christos A1 - Hashemi, Seyedreza A1 - Prager, Jens T1 - How structural health monitoring can be embedded in a digital quality infrastructure: an example. N2 - The digital Quality Infrastructure (QI) initiative “QI-Digital” in Germany is focusing on implementing new technologies and approaches to ensure that the task of quality assurance is more efficient and ready for the digital and green transformation of the economy. The implementation of quality control key elements, such as Smart Standards, Digital Certificates and QI-cloud solutions shall contribute to solving the socio-economic, ecological, and technological challenges of our time. Hydrogen is a key energy carrier and has the potential to play a significant role in the energy transition, especially in mobility. An essential factor for the broad acceptance of hydrogen-based mobility is the availability of refueling stations that operate reliably and safely. Using the example of a Hydrogen Refueling Station (HRS) built within the QI-Digital initiative, the Federal Institute for Material Research and Testing (BAM) aims to establish a real laboratory where modern measurement techniques and new digital methods are implemented to enhance operational safety, availability, and economic efficiency and render the technology more attractive for the industry. In this work, we present an approach to establish a Structural Health Monitoring (SHM) system on a high-pressure buffer inside HRS and show how it could be embedded into a digital QI. The high-pressure buffers are essential components of the plant which are currently inspected periodically without regard to their operating history. Focusing on the transition to a continuous and digitally supported monitoring of the component’s integrity during operation the novel inspection scheme will be linked to a completely digitalized component-related documentation and tested using digital certificates. This allows the operational safety and, if necessary, the remaining useful lifetime to be assessed on an ongoing basis and to be a valuable contribution to increasing sustainability. T2 - 11th European Workshop on Structural Health Monitoring CY - Potsdam, Germany DA - 10.06.2024 KW - Structural health monitoring KW - Quality infrastructure KW - Digital transformation KW - Reliability KW - Quality control KW - Industry 4.0 PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-607109 DO - https://doi.org/10.58286/29769 SN - 1435-4934 SP - 1 EP - 7 PB - NDT.net AN - OPUS4-60710 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wiehle, Philipp A1 - Härder, M. A1 - Strangfeld, Christoph T1 - Feuchteverhalten von Lehmsteinmauerwerk unter natürlichen Klimabedingungen – Experimentelle und numerische Untersuchungen N2 - Druckfestigkeit und Elastizitätsmodul von Lehmsteinmauerwerk nehmen mit steigendem Feuchtegehalt ab, weswegen die Mauerwerksdruckfestigkeit bei der Bemessung gemäß DIN 18940 in Abhängigkeit der maximal zu erwartenden Ausgleichsfeuchte abgemindert wird. Da bisher allerdings keine Messdaten zum Feuchtegehalt von Lehmsteinmauerwerk unter natürlichen Klimabedingungen vorliegen, stellen die normativen Grenzwerte lediglich eine konservative Abschätzung dar. Um die Feuchtegehalte von Lehmsteinmauerwerk und somit die Tragfähigkeit realitätsnah einschätzen zu können, wurden im Rahmen der vorliegenden Arbeit sowohl experimentelle als auch numerische Untersuchungen zum feuchtetechnischen Verhalten durchgeführt. Dabei wurden erstmalig magnetresonanzspektroskopische Untersuchungen an tragenden Lehmsteinen unterschiedlicher Herstellungsmethoden angewandt Weiterhin wurden Luftfeuchtesensoren in Lehmsteinmauerwerk eingebettet, um hygrische Langzeitfeuchtemessungen unter natürlichen Klimabedingungen durchzuführen. Auf Basis dieser Erkenntnisse wurde schließlich ein numerisches Modell kalibriert und Parameterstudien durchgeführt, um den unter realen Klimabedingungen tatsächlich auftretenden Feuchtegehalt im Lehmmauerwerk sowie dessen Verteilung über den Querschnitt einschätzen zu können und die normativen Grenzwerte zu überprüfen. Gezeigt wurde, dass die realitätsnahe instationäre Berechnung des Feuchtetransports mit üblichen hygrothermischen Simulationsprogrammen auf Basis einfacher feuchtetechnischer Kennwerte auch bei Lehmbaustoffen möglich ist. Der Einfluss des Quellens und Schwindens der enthaltenen Tonminerale und organischen Bestandteile wurde durch eine Modifikation bei der Ermittlung des Wasseraufnahmekoeffizienten explizit berücksichtigt und ist somit auch in den daraus abgeleiteten Transportkoeffizienten enthalten. Darüber hinaus wurde die Feuchtespeicherfunktion im überhygroskopischen Bereich auf Grundlage der Porenvolumenverteilung abgeschätzt. Die Approximation der Transportkoeffizienten und der Feuchtespeicherfunktion stellt dabei eine wesentliche Vereinfachung für Lehmbaustoffe dar, da ihre experimentelle Bestimmung aufgrund des Kontaktes mit Flüssigwasser kaum möglich ist. In Bezug auf das Feuchteverhalten üblicher Außenwandaufbauten von Wohnräumen konnte festgestellt werden, dass die Ausgleichsfeuchte im Lehmsteinmauerwerk stets unterhalb des in Nutzungsklasse 1 gemäß DIN 18940 zulässigen Grenzwertes von 65 % liegt. Je nach Putzsystem und Dämmstoff reduziert sich die Ausgleichsfeuchte auf Werte unter 60 %, wobei sich eine annähernd gleichmäßige Verteilung der Feuchte über den Mauerwerksquerschnitt hinweg einstellt. Bei Außenwänden von unbeheizten Räumen ergab sich eine maximale Ausgleichsfeuchte, die über weite Teile des Querschnitts unterhalb von 80 % lag. Der Ansatz einer maximalen Ausgleichsfeuchte von 90 % in Nutzungsklasse 2 ist folglich zu hoch angesetzt. Die zulässige Ausgleichsfeuchte bzw. der Umgebungsfeuchtefaktor in Nutzungsklasse 2 sollte dementsprechend angepasst werden T2 - LEHM 2024 – 9. Internationale Fachtagung für Lehmbau CY - Weimar, Germany DA - 27.09.2024 KW - Lehmstein KW - Mauerwerk KW - Materialfeuchte KW - Feuchtemonitoring KW - hygrothermische Simulation PY - 2024 SP - 1 EP - 10 AN - OPUS4-61217 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schmidt, S. A1 - Pirskawetz, Stephan T1 - Monitoring mit Schallemissionsmessung N2 - Die Brücke am Altstädter Bahnhof in Brandenburg an der Havel stand bei ihrer Eröffnung im Jahr 1969 für die höchste Ingenieurskunst der damaligen Zeit und für einen in die Zukunft gerichteten Blick. Sie trug den Namen "Brücke des 20. Jahrestag", denn am 20. Jahrestag der DDR wurde die Brücke für den Verkehr freigegeben. Sie verbindet die westlichen Stadtbezirke mit dem Zentrum der Stadt Brandenburg an der Havel und wurde so von vielen Einwohner:innen genutzt. Zu Fuß, mit dem Rad, dem Auto oder mit der Straßenbahn. 50 Jahre später, im Dezember 2019, wurde bei einer Bauwerksprüfung eine starke Schadenszunahme festgestellt. Eine sofortige Sperrung für den Verkehr war unumgänglich. Das hatte es im Land Brandenburg bislang nicht gegeben und stellt einen einzigartigen Sonderfall bei der Bewertung von Bauwerken dar. Die Sperrung führte zu starken Einschränkungen für den Verkehr, für den Landesbetrieb Straßenwesen aber hatte die Sicherheit oberste Priorität. Um die Belastung für die Stadt so gering wie möglich zu halten, hat der Landesbetrieb Straßenwesen sofort mit der Planung für Abriss und Neubau der Brücke begonnen. So gelang es innerhalb von kurzer Zeit den Rückbau umzusetzen und die Pläne für den Ersatzneubau vorzustellen. Gleichzeitig bot sich die einmalige Gelegenheit, kurz vor dem Rückbau noch umfangreiche Untersuchungen zur Verifizierung des Schadensbilds durchzuführen und verschiedene Monitoringverfahren zum Einsatz zu bringen. Damit wurden wertvolle Erfahrungen gesammelt, die der Landesbetrieb Straßenwesen anderen Baulastträgern zur Verfügung stellen möchte. Sie ermöglichen es, bei baugleichen Bauwerken zielgerichteter handeln zu können. Die Fülle der untersuchten Aspekte ist in diesem Bericht dokumentiert. Diese umfangreichen Untersuchungen wurden vom Bundesministerium für Verkehr und digitale Infrastruktur finanziert. Dafür möchten wir uns herzlich bedanken. Mit großem Engagement digitabeteiligt haben sich auch die Bundesanstalt für Materialforschung und -prüfung, die Technische Universität Dresden, die Hochschule für Wirtschaft und Technik Dresden sowie das Unternehmen Bilfinger Noell und die Ingenieursozietät Zech, Ruth, Blasius. Auch bei Ihnen bedankt sich der Landesbetrieb Straßenwesen. KW - Baustoffe KW - Korrosion KW - Beton KW - Spannbeton KW - Brücke KW - Spannstahl KW - Spannungsrisskorrosion KW - Zerstörungsfreie Prüfung KW - Schallemissionsanlayse KW - Spanndrahtbruch PY - 2021 SP - 65 EP - 71 PB - Landesbetrieb Straßenwesen Brandenburg CY - Hoppegarten AN - OPUS4-54600 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kühne, Hans-Carsten T1 - Die Kandelaber des Ensembles am Charlottenburger Tor N2 - Auf der Charlottenburger Brücke entstand mit dem Charlottenburger Tor und den beiden Kandelabern von 1905 bis 1908 ein repräsentatives Ensemble von Einzelbauwerken. Für die architektonische Wirkung des Charlottenburger Tores waren die beiden ca. 22 Meter hohen Kandelaber auf der Charlottenburg zugewandten Seite des Tores bedeutsam. Die Stiftung Denkmal ließ die Kandelaber seit Mai 2007 mit dem Ziel rekonstruieren, dem Tor, seiner Umgebung und der Straße des 17 Juni den historischen Gesamteindruck wiederzugeben. Im Rahmen der Rekonstruktion wurde die Grundsatzentscheidung getroffen, dass die Wiederherstellung der komplett zerstörten und auch nicht mehr in Fragmenten vorhandenen Kandelaber nicht unter Anwendung der Bautechnik von 1900 durchgeführt werden sollte. Die Zielsetzung war viel mehr, mit moderner Bautechnik die Anmutung der Kandelaber von 1903 wiederherzustellen, die in Verbindung mit anderen baulichen Elementen, wie der Charlottenburger Brücke und des Charlottenburger Tores, den historischen Gesamtkomplex bilden. T2 - Workshop Kulturguterhaltung - Vom Dampfkessel zu Nanomaterialien CY - Berlin, Germany DA - 17.11.2021 KW - Charlottenburger Tor KW - Kunststein KW - Hydrophobierung KW - Bildhauerbeton PY - 2021 VL - 3 SP - 97 EP - 105 PB - Druckerei G. Bohm CY - Berlin AN - OPUS4-57091 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Breitenbücher, R. A1 - Przondziono, R. A1 - Meng, Birgit A1 - Krütt, Enno A1 - Weise, Frank T1 - Alkali-Silica Reaction in concrete pavements considering traffic and de-icing agents N2 - In concrete pavements, damages occurred which are related to an Alkali-Silica-Reaction (ASR). Although the background for such an ASR has been studied extensively, special conditions in pavements increase this reaction significantly. These are especially the superposition of microstructural degradation caused by cyclic loading with an external alkali supply. Previous investigations of ASR focused mainly on the material itself (aggregates, cements, assessment of the concrete) while these special circumstances have not been considered. Concrete pavements are subjected to cyclic loadings by traffic and climate changes. Within cooperative research projects the different interdependent influencing factors for a damaging ASR in concrete pavements are studied by experiments as well as by numeric modelling. On the micro-level the ASR-related processes within the aggregate, such as gel-formation or ion-transport, are investigated. On the meso-level, the project focuses on the characterization of degradation effects in the concrete microstructure due to cyclic loading. Further, special attention is paid to the transport behavior of fluids in such pre-damaged concrete structures with and without the effect of overrunning tires as well as the impact on the ASR itself. Finally, on the macro-level the risk of an ASR-damage is assessed. T2 - 13th International Symposium on Concrete Roads CY - Berlin, Germany DA - 19.06.2018 KW - Alkali-Silica Reaction KW - Degradation KW - Cyclic loading KW - Fluid transport KW - Traffic PY - 2018 SP - 1 EP - 15 AN - OPUS4-46354 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Strobl, Domninic T1 - PGD in thermal transient problems with a moving heat source – a sensitivity study on factors affecting accuracy and efficiency N2 - Thermal transient problems, essential in applications like welding and additive metal manufacturing, are characterized by a dynamic evolution of temperature. Accurately simulating these phenomena is often computationally expensive, thus limiting the application, e. g. for model parameter estimation or online process control. Model order reduction, a solution to preserve accuracy while reducing complexity, is explored. This paper addresses challenges in developing a reduced model using the Proper Generalized Decomposition (PGD) for transient thermal problems with a specific treatment of the moving heat source within the reduced model. Factors affecting accuracy, convergence, and computational cost, such as discretization methods (finite element and finite difference), a dimensionless formulation, the size of the heat source, and the inclusion of material parameters as additional PGD variables are examined across progressively complex examples. The results demonstrate the influence of these factors on the PGD model's performance and emphasize the importance of their consideration when implementing such models. For thermal examples it is demonstrated that a PGD model with a finite difference discretization in time, a dimensionless representation, a mapping for a moving heat source, and a spatial domain non-separation yields the best approximation to the full order model. KW - Additive manufacturing KW - Mapping for unseparable load KW - Model order reduction KW - Proper generalized decomposition KW - Sensitivity analysis KW - Thermal transient problem PY - 2024 DO - https://doi.org/10.5281/zenodo.10102489 PB - Zenodo CY - Geneva AN - OPUS4-62235 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Werner, Tiago A1 - Teske, Tanita A1 - Hilgenberg, Kai A1 - Mauro, Madia A1 - Nielsen, S. A1 - Gärtner, F. A1 - Klassen, T. T1 - Untersuchung des Potenzials von Kaltgasspritzen für die Reparatur zyklisch belasteter Bauteile T1 - Investigation on the capability of cold-spray for repair of cyclically loaded components N2 - Die Reparatur mittels Kaltgasspritzen ist eine vielversprechende Alternative zum teuren Austausch fehlerbehafteter Bauteile in der Luft- und Raumfahrt. Im Rahmen dieser Arbeit wurde das Potential des Verfahrens an der hochfesten Aluminiumlegierungen Al6061-T6 unter Anwendung von Stickstoff als kostengünstiges Prozessgas untersucht. Es wurden quasi-statische Zugversuche und einachsige Zeitfestigkeitsversuche mit besonderem Fokus auf das in-situ Kugelstrahlen zur Verbesserung der mechanischen Eigenschaften durchgeführt. Im Ergebnis wurde die Verbesserung der Adhäsion zwischen Substrat und aufgebautem Werkstoff als entscheidendes Kriterium für eine Anwendbarkeit ermittelt. Die Laserstrukturierung von Substratoberflächen ist hierfür vielversprechend und wurde im Rahmen der Arbeit mittels Adhäsionsversuchen untersucht. N2 - Repair by cold-spray is a promising alternative to the costly replacement of flawed components in aerospace applications. In the present work this process was investigated on the high-strength aluminum alloy Al6061-T6. For the cold-spray process, inexpensive Nitrogen was used as process-gas. Quasi-static tensile and highcycle- fatigue tests (HCF) were performed, focusing on in-situ shot peening to improve the mechanical properties of the repaired part. An improved adhesion between substrate and built-up material was identified as a key-factor for the applicability of the process. Under this respect laser-structuring of the substrate surface was applied and its effect on the mechanical performance of the restored samples were examined by adhesion tests. T2 - 9. Tagung des DVM-Arbeitskreises Additiv gefertigte Bauteile und Strukturen CY - Stuttgart, Germany DA - 06.11.2024 KW - Kaltgasspritzen KW - cold-spray KW - Reparatur KW - Repair KW - Ermüdungsfestigkeit KW - Fatigue KW - Luft- und Raumfahrt KW - Aerospace KW - Substratvorbehandlung KW - Substrate pre-treatment PY - 2024 DO - https://doi.org/10.48447/ADD-2024-BB VL - 409 SP - 67 EP - 79 AN - OPUS4-63182 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ratkovac, Mirjana A1 - Gerards-Wünsche, Paul A1 - Thiele, Marc A1 - Brackrock, Daniel A1 - Stamm, Michael T1 - Detection and monitoring of the fatigue crack growth on welds – Application-oriented use of NDT methods N2 - Early detection of fatigue cracks and accurate measurements of the crack growth play an important role in the maintenance and repair strategies of steel structures exposed to cyclic loads during their service life. Observation of welded connections is especially of high relevance due to their higher susceptibility to fatigue damage. The aim of this contribution was to monitor fatigue crack growth in thick welded specimens during fatigue tests as holistically as possible, by implementing multiple NDT methods simultaneously in order to record the crack initiation and propagation until the final fracture. In addition to well-known methods such as strain gauges, thermography, and ultrasound, the crack luminescence method developed at the Bundesanstalt für Materialforschung und -prüfung (BAM), which makes cracks on the surface particularly visible, was also used. For data acquisition, a first data fusion concept was developed and applied in order to synchronize the data of the different methods and to evaluate them to a large extent automatically. The resulting database can ultimately also be used to access, view, and analyze the experimental data for various NDT methods. During the conducted fatigue tests, the simultaneous measurements of the same cracking process enabled a comprehensive comparison of the methods, highlighting their individual strengths and limitations. More importantly, they showed how a synergetic combination of different NDT methods can be beneficial for implementation in large-scale fatigue testing but also in monitoring and inspection programs of in-service structures - such as the support structures of offshore wind turbines. T2 - Fatigue Design 2023 (FatDes 2023) CY - Senlis, France DA - 29.11.2023 KW - Fatigue KW - Welded KW - NDT KW - Crack growth PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-600238 DO - https://doi.org/10.1016/j.prostr.2024.03.062 VL - 57 SP - 560 EP - 568 PB - Elsevier B.V. AN - OPUS4-60023 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Nagelschmidt, Sven T1 - Ein Beitrag zur Zusammenführung von Zeit-Temperatur-Äquivalenz-Methoden: Entwicklung und Anwendung am Beispiel ausgewählter Materialverhalten für Zeit-Temperatur-Parameter und Zeit-Temperatur-Superpositionsprinzip N2 - In der Wissenschaft und Technik gibt es verschiedene Gründe, um auf Basis geeigneter Modelle in die Zukunft schauen zu wollen, beispielsweise um zu bewerten, ob ein Bauteil auch noch deutlich länger verwendet werden kann als eigentlich einmal vorgesehen. Eine Methode dieses zu tun, basiert auf dem Zeit-Temperatur-Äquivalenz-Prinzip, welches besagt, dass ein Zustand oder eine Materialeigenschaft gleichwertig bei verschiedenen Zeit-Temperatur-Kombinationen auftritt oder erreicht werden kann. Höhere Temperaturen verkürzen in der Regel die Dauer und umgekehrt. In den letzten Jahrzehnten hat sich ein umfangreiches Methodenspektrum für unterschiedliche Werkstoffe und Anwendungsgebiete entwickelt, sodass die Identifikation einer geeigneten Methode für einen konkreten Anwendungsfall oder neue Materialien eine Herausforderung darstellt. These: „Fortschrittlich wäre, existierende Methoden zusammenzuführen, methodenspezifische Vorteile zu kombinieren, um mit geringerem Aufwand ein geeignetes Prognosemodell zu entwickeln.“ Für metallische Werkstoffe und Polymere verläuft die Entwicklung von Prognosemodellen mit Zeit-Temperatur-Korrelation seit ca. 1940 parallel und unabhängig voneinander. In diesem Zusammenhang bekannte Methoden sind das Zeit-Temperatur-Superpositionsprinzip und Zeit-Temperatur-Parameter, wie der LARSON-MILLER-Parameter. Die jeweiligen methodischen Ansätze sind in der Regel anwendungs- und materialspezifisch und nur einzelnen Fachartikeln zu entnehmen. Eine zusammenführende thematische Übersicht und Untersuchung existierender Methoden wurden bislang nicht publiziert. Diese Forschungsarbeit verfolgt dahingehend einen neuartigen methodischen Ansatz und zeigt untersuchte Gemeinsamkeiten und Unterschiede als auch Analogien für das Zeit-Temperatur-Superpositionsprinzip und Zeit-Temperatur-Parameter anhand bestimmter Merkmale auf. Dafür wurden verschiedene analytische und grafische Ansätze verwendet. Ferner wird eine zusammenführende Untersuchung anhand eines rheologischen Materialmodells sowie anhand eines praktischen Anwendungsbeispiels gezeigt. Hergeleitet wurde u. a., dass das Prinzip der Zeit-Temperatur-Superposition für sogenanntes thermorheologisch einfaches und komplexes Verhalten konkreten Zeit-Temperatur-Parametern zugeordnet werden können. Und dadurch Verschiebefunktionen nicht nur in Abhängigkeit der Temperatur, sondern auch abhängig vom Zustand untersucht und definiert werden können. Ferner ermöglicht eine Skalierung der Zeit-Temperatur-Parameter auf eine Referenztemperatur physikalisch anschaulichere Auswertungen analog zum Zeit-Temperatur-Superpositionsprinzip. Untersuchungen zeigen, dass sich für einen konkreten Anwendungsfall die geeignetste Zeit-Temperatur-Äquivalenz-Methode aus einer gegenseitigen Abhängigkeit bzw. Kompatibilität einzelner Elemente, wie zugrunde gelegte Daten, Koordinatenachsenskalierung, ermittelte Zeit-Temperatur-Äquivalenz, Masterfunktionsansatz und der geforderten Interpolationsgüte herleitet. Der gewählte Forschungsansatz und die erzielten Ergebnisse bieten eine Plattform für die weitere Entwicklung von Prognosemodellen auf Basis des Zeit-Temperatur-Äquivalenz-Prinzips, insbesondere im Hinblick auf eine Zusammenführung und Kombination existierender Methoden. KW - Zeit-Temperatur-Äquivalenz KW - Zeit-Temperatur-Korrelation KW - Zeit-Temperatur-Superposition KW - Extrapolation PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-601530 DO - https://doi.org/10.14279/depositonce-20439 SP - 1 EP - 145 CY - TU Bibliothek online AN - OPUS4-60153 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hashemi, Seyedreza A1 - Zscherpel, Uwe T1 - Measurement of Focal Spots of X-ray Tubes Using a CT Reconstruction Approach on Edge Images of Large Holes and Comparison to Pinhole Imaging N2 - The first Non-destructive testing (NDT) method which evolved in the industrial age was radiographic testing (RT). Among all NDT methods, RT is no exception, so there are still many issues for optimizations even today. One of them is the measurement of the focal spot of X-ray tubes. The size of the focal spot is critical for imaging, because it determines the spatial resolution in the X-ray image. The classical way to evaluate focal spots of X-ray tubes is by pinhole imaging using a camera obscura. But this method has a natural lower limit, which is defined by the diameter of the pinhole used (today min. 10 µm). Therefore, focal spot sizes lower than 50 µm diameter cannot be imaged and measured correctly. An alternative approach, which permits this, was investigated here using the edge unsharpness of holes much larger than the focal spot size. The results of both methods were compared using 3 different X-ray tubes. KW - Reconstruction method KW - Radiographic testing (RT) using X-rays KW - Focal spot measurement KW - Edge unsharpness KW - X-ray tubes KW - Pinhole imaging KW - Computed Tomography (CT) KW - Focal Spot (FS) PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-608646 DO - https://doi.org/10.58286/29556 SN - 2941-4989 SP - 1 EP - 9 PB - NDT.net CY - Berlin, Germany AN - OPUS4-60864 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lothongkam, Chaiyaporn A1 - Rohwetter, Philipp A1 - Habel, Wolfgang A1 - Gockenbach, E. T1 - Dielectric strength behavior and mechanical properties of transparent silicone rubbers for HV cable accessories N2 - Modern optical partial discharge (PD) detection system based on fiber-optic sensors for PD on-line health monitoring in high-voltage (HV) cable terminations necessarily requires optically transparent or translucent insulation materials. The optically compatible silicone rubbers are the key to facilitate such innovative technology. In this work, AC 50 Hz dielectric strength Eb and mechanical properties of three types of commercially available silicone rubbers have been investigated. The investigations revealed that the translucent silicone rubber has a good mechanical performance but its Eb value is considered too low. However it is sufficiently good for use as base material for rubber stress cones. Unfortunately, its optical transmittance is poor compared to optically clear transparent silicones. On the other hand, the mechanical properties of transparent silicone rubbers do not comply with those demanded from push-on stress cones. In particular, their elongation at break is considered too low for that application. However they provide the Eb values of about 28 kV/mm to 29 kV/mm at 0.5 mm thickness, which are higher than those of the translucent type. Moreover, it was found that the post-curing process does not provide a positive impact on the ultimate elongation of silicone rubbers. T2 - ISEIM 2014 - 7th International symposium on electrical insulating materials CY - Niigata City, Japan DA - 01.06.2014 KW - Silicone rubbers KW - Dielectric strength KW - Tensile strength KW - Elongation at break KW - Rubber stress cone PY - 2014 DO - https://doi.org/10.1109/ISEIM.2014.6870829 SP - 503 EP - 506 PB - IEEE AN - OPUS4-32649 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Kohl, Anka A1 - Haufe, Manuela A1 - Heyer, Martina T1 - Compatibility of polyehtylene grades with biofuels and biodiesel-heating oil blends N2 - The aim of this work was to study the interaction between high density polyethylene (HDPE) grades as material for dangeraus goods packagings and biofuels such as E10 (fuel with 10% ethanol), E85 (fuel with 85% ethanol), biodiesei and 810 (heating oil with 10% biodiesel). Jerricans made of two polyethylene grades were filled with these fuels and exposed to temperatures of 20 oc and 40 oc for more than one year. Tensile properlies (tensile strength, breaking elongation and elasticity modulus) and Melt Flow Rate (MFR) were determined, and Fourier Transform Infrared Spectroscopy (FTIR) was used to evaluate changes in the chemical structure. Measurements of the MFR and tensile properlies of the polyethylene grades after exposure to E1 0, E85 and 810 showed only a slightly damaging influence. A n increase in the peak of 1585 cm·1 for the (C=C) stretching vibrations was visible in the FTIR spectra after immersion tests with E85. A n increase in the MFR with the immersion time of the grades in biodiesei was measured - in parlicular, after one year of exposure. The elasticity modulus of the polyethylene grades was reduced with the immersion time too. The FTIR spectra showed a broadening of the C=O peak of 1740 cm·1 and the appearance of the hydroxyl group at 3500 cm·1. T2 - Corrosion 2015 CY - Dallas, TX, USA DA - 15.03.2015 KW - Polyethylene grades KW - Biodiesel KW - E10 KW - E85 KW - B10 KW - Tensile properties KW - FTIR analysis KW - Compatibility KW - Biofuels KW - Change in MFR and tensile properties PY - 2015 SP - Paper No. 5536, 1 EP - 12 AN - OPUS4-32968 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Heming, Frank A1 - Haufe, Manuela A1 - Heyer, Martina T1 - Compatibility of sealing materials with biofuels and biodiesel-heating oil blends N2 - Changes in fuel composition and the introduction of alternative fuels often create problems of degradation in materials. The objective of this research is to study the interaction of the sealing materials FKM, EPDM, CR, CSM, N8R, IIR, VMQ, FVMQ and PA and biofuels such as non-aged and 2 year aged biodiesel (FAME), E1 0 (fuel with 10% ethanol, E85 (fuel with 85% ethanol} and non-aged and 1 year aged 810 (heating oil with 10% biodiesel) in comparison with premium grade fuel without ethanol. Exposure tests were performed with test specimens at 20 °C, 40 oc and 70 oc for 84 days to document the changes in mass, volume and tensile properties. The sealing materials FKM, FVMQ and PA were evaluated as resistant in E10, and FVMQ, VMQ and PA as resistant in E85 at 20 oc and 40 oc. S welling resulted from the high absorption by the elastemers CR, CSM, EPDM, IIR and N8R in comparison to their dissolution in non-aged biodiesei at 40 °C. FKM was still resistant in aged biodiesei at 40 oc but only to a limited degree at 70 °C. The sealing materials CR, CSM, EPDM, IIR and N8R were damaged to a high extent in non-aged and aged 810. Of all the sealing materials, FKM and FVMQ showed high compatibility with these biofuels up to 70 °C. T2 - Corrosion 2015 CY - Dallas, TX, USA DA - 15.03.2015 KW - Biofuels KW - Sealing materials KW - Compatibility KW - Change in tensile properties KW - Change in mass PY - 2015 SP - Paper No. 5535, 1 EP - 13 AN - OPUS4-32969 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hu, Wei-Hua A1 - Caetano, E. A1 - Cunha, A. A1 - Rücker, Werner ED - Carrera, E. ED - Miglioretti, F. ED - Petrolo, M. T1 - Comparison of different statistical approaches for removal of environmental/operational effects on modal properties and damage detection N2 - The implementation of a continuous dynamic monitoring System in Pedro e Ines footbridge at Coimbra, Portugal, operating since June 2007, enabled to detect different environmental/operational effects on the modal properties, based on appropriate processing of monitoring data collected by a set of accelerometers and thermal sensors. In order to remove or mitigate such environmental/operational effects with the purpose of damage detection, two different Statistical methods have been adopted, One of them consists in the multiple linear regression (MLR) by performing correlation analysis between measured modal properties and environmental/operational variables. Another is based on the identification of the linear subspace within the modal properties by applying principal component regression (PCR) without using measured values of environmental and operational variables. This paper presents a comparison ofthe performance of these two alternative approaches on the basis of continuous monitoring data acquired front the instrumented Pedro e Ines footbridge. T2 - SMART2013 - 6th ECCOMAS conference on smart structures and materials CY - Turin, Italy DA - 24.06.2013 KW - Structural health monitoring KW - Environmental/operational effects KW - Principal component regression KW - Multiple linear regression KW - Damage detection PY - 2013 SP - 1 EP - 13 AN - OPUS4-32972 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gonzalez III, F. A1 - Prabhakaran, A. A1 - Robitaille, A. A1 - Booth, G. A1 - Birk, A.M. A1 - Otremba, Frank T1 - Rail tank car total containment fire testing: planning & test development N2 - Given the frequent incidences of Non-Accident Releases (NARs) of hazardous materials from tank cars, there in an increasing interest in transporting hazardous materials in total containment conditions (i.e., no pressure relief devices). However, the ability of tank cars to meet thermal protection requirements provided in the Code of Federal Regulations under conditions of total containment has not been established. Also, the modeling tool commonly used by industry to evaluate thermal protection, AFFTAC, has not been validated under these conditions. The intent of this effort was to evaluate through a series of third-scale fire tests, the ability of tank cars to meet the thermal protection requirements under total containment conditions, and also, to validate AFFTAC for such conditions. This paper describes the test design and planning effort associated with this research, including the design and evaluation of a fire test setup to simulate a credible, fully engulfing, pool fire that is consistent and repeatable, and the design and hydro-static testing of a third-scale tank specimen. The fire design includes controls on the spatial distribution and temperature variation of the flame temperature, the heat flux, and the radiative balance, to best reflect large liquid hydrocarbon pool fire conditions that may be experienced during derailment scenarios. T2 - JRC2015 - Joint rail conference CY - San Jose, CA, USA DA - 23.03.2015 PY - 2015 SP - 5764, 1 EP - 6 AN - OPUS4-32985 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krug, Sonja A1 - Hohendorf, Stefan A1 - Redmer, Bernhard T1 - Radiographien in der Kunstbibliothek N2 - Im Rahmen des Basisprojektes »Sammlungserschließung« wurden im Oktober 2014 Radiographien von 14 Gemälden und zwei Schmuckrahmen aus der Sammlung Modebild – Lipperheidesche Kostümbibliothek (Kunstbibliothek, Staatliche Museen zu Berlin) erzeugt. Die Aufnahmen wurden von Anja Schönstedt, Bernhard Redmer und Stefan Hohendorf von der Bundesanstalt für Materialforschung und -prüfung (BAM, Fachbereich 8.3 Radiologische Verfahren) angefertigt und uns zur weiteren Bearbeitung bereitgestellt. PY - 2015 VL - 100 SP - 5 EP - 7 AN - OPUS4-33113 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schurig, Michael A1 - Joschko, M. A1 - Kuka, K. A1 - Illerhaus, Bernhard A1 - Fritsch, G. T1 - Wenn Wissenschaftler "spielen" gehen... N2 - Eine Bodenprobenahme selbst hat schon Einfluss auf die Eigenschaften der Probe und kann sie verfälschen. Deshalb haben Forschen einmal einen Blick unter die Bodenoberfläche gewagt. KW - Computertomographie KW - Zerstörungsfreie Bodenproben PY - 2015 IS - 16. Woche SP - 30 EP - 31 PB - Deutscher Bauernverlag GmbH CY - Berlin AN - OPUS4-33117 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mehdianpour, Milad T1 - Risslumineszenz - Ein neues Verfahren zur Detektion und Überwachung von Ermüdungsrissen N2 - Risslumineszenz ist eine neue Erfindung, mit der Ermüdungsrisse unter laufendem Betrieb ohne weiteres Zutun leicht detektiert werden können, indem sie leuchten. Die Bedeutung liegt in der allgemeinen Problematik ermüdungsbeanspruchter Konstruktionen. Risse begrenzen ihre Lebensdauer. Das betrifft zum Beispiel Verkehrsinfrastrukturbauwerke oder allgemein Tragwerke unter nicht ruhender Beanspruchung, auch Maschinen, Baufahrzeuge, Kräne, Zentrifugen und Schiffe. Bei dem Risslumineszenzverfahren leuchten die Risse unter UVLicht. T2 - VSVI-Seminar Brücken- und Ingenieurbau CY - Braunschweig, Germany DA - 24.03.2015 KW - Ermüdung KW - Rissdetektion KW - Rissüberwachung PY - 2015 SP - 1 EP - 5 AN - OPUS4-33120 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grätz, Rainer T1 - Konformitätsbewertung mechanischer Ex-Betriebsmittel N2 - Explosionsschutz ist für viele Bereiche der Industrie und des Transport- und Lagerwesens von großer Bedeutung. Arbeitssicherheit, Anlagenschutz, Umweltschutz und öffentliche Sicherheit sind dabei gleichermaßen sicherzustellen. Die Ex-Schutz-Seminare der Technischen Akademie Heilbronn richten sich an Planer, Errichter, Betreiber und deren befähigte Personen sowie das gesamte Umfeld (Hersteller, Behörden, Prüfstellen, Berater). Sie sind unter ein einheitliches Thema gestellt: Wie sind Anlagen in explosionsgefährdeten Bereichen sicher zu planen, zu errichten und zu betreiben. Zu Beginn jeden Seminars werden die physikalischen und technischen Grundlagen behandelt und anhand der einschlägigen Richtlinien und Normen (VDE, EN, IEC usw.) gezeigt, wie der Explosionsschutz grundsätzlich verwirklicht werden kann (integrierter Explosionsschutz). Die rechtlichen Grundlagen, Zusammenhänge und ihre Bedeutung werden dargestellt, einschließlich der Prüfung und Zertifizierung. T2 - 40. Heilbronner Ex-Schutz-Seminar "Planen, Errichten und Betreiben von Anlagen in explosionsgefährdeten Betriebsstätten Ex-Schutz mechanischer Geräte" CY - Heilbronn, Germany DA - 04.03.2015 KW - Explosionsschutz KW - ATEX KW - Nichtelektrische Geräte KW - Konformitätsbewertung PY - 2015 SP - Kap. 6, 1 EP - 10 AN - OPUS4-33159 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Kanzler, Daniel A1 - Müller, Christina A1 - Pitkänen, J. T1 - Probability of defect detection of Posiva's electron beam weld N2 - The report 'Probability of Defect Detection of Posiva's electron beam weld' describes POD curves of four NDT methods radiographic testing, ultrasonic testing, eddy current testing and visual testing. POD-curves are based on the artificial defects in reference blocks. The results are devoted to the demonstration of suitability of the methods for EB weld testing. Report describes methodology and procedure applied by BAM. Report creates a link from the assessment of the reliability and inspection performance to the risk assessment process of the canister final disposal project. Report ensures the confirmation of the basic quality of the NDT methods and their capability to describe the quality of the EB-weld. The probability of detection curves are determined based on the MIL-1823 standard and it's reliability guidelines. The MIL-1823 standard was developed for the determination of integrity of gas turbine engines for the US military. In the POD-process there are determined as a key parameter for the defect detectability the a90/95 magnitudes, i.e. the size measure a of the defect, for which the lower 95 % confidence band crosses the 90 % POD level. By this way can be confirmed that defects with a size of a90/95 will be detected with 90 % probability. In case the experiment will be repeated 5 % might fall outside this confidence limit. KW - Probability of detection curves KW - POD-curves KW - NDT-methods KW - EB-welding KW - Ultrasonic inspection KW - Radiographic inspection KW - Eddy current inspection KW - Visual inspection PY - 2013 UR - http://www.posiva.fi/en/databank/working_reports/probability_of_defect_detection_of_posiva_s_electron_beam_weld.1874.xhtml?xm_col_report_year=2013&xm_col_language=3&xm_col_type=5&cd_order=col_report_number&cd_offset=0#.VJAIY3uj_mc UR - http://www.posiva.fi/files/3527/WR_2013-70.pdf SP - 1 EP - 86 AN - OPUS4-32512 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Bertovic, Marija T1 - Identifying and managing risks in mechanised NDT: A human factors study N2 - The variety of risks present during the application of mechanised non-destructive testing (NDT) methods for the final disposal of spent nuclear fuel has not been investigated. Therefore, a need exists to identify these risks and find ways to prevent them. The Failure Modes and Effects Analysis (FMEA), a widely used risk assessment technique, was used to achieve this goal. PY - 2014 SP - ID 1427252, 1 EP - 44 AN - OPUS4-32514 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard A1 - Komann, Steffen A1 - Wille, Frank A1 - Rolle, Annette A1 - Probst, Ulrich A1 - Schubert, Sven T1 - Considerations of aging mechanisms influence on transport safety and reliability of dual purpose casks for spent nuclear fuel or HLW N2 - When storage of spent nuclear fuel (SNF) or high-level waste (HLW) is done in dual purpose casks (DPC), the effects of aging on safety relevant DPC functions and properties have to be managed in a way that a safe transport after the storage period of several decades is capable, and can be justified and certified permanently throughout that period. The effects of aging mechanisms (like e.g. radiation, different corrosion mechanisms, stress relaxation, creep, structural changes and degradation) on the transport package design safety assessment features have to be evaluated. The consideration of these issues in the DPC transport safety case will be addressed. Special attention is given to all cask components which cannot be directly inspected or changed without opening the cask cavity, what are the inner parts of the closure system and the cask internals, like baskets or spent fuel assemblies. The design criteria of that transport safety case have to consider the operational impacts during storage. Aging is not subject of technical aspects only, but also of 'intellectual' aspects, like changing standards, scientific/ technical knowledge development and personal as well as institutional alterations. Those aspects are to be considered in the management system of the license holders and in appropriate design approval update processes. The paper addresses issues which are subject of an actual IAEA TECDOC draft 'Preparation of a safety case for a dual purpose cask containing spent nuclear fuel'. T2 - PSAM 12 - Probabilistic safety assessment and management CY - Honolulu, Hawaii, USA DA - 22.06.2014 KW - Transport and storage casks for spent nuclear fuel or high level waste KW - Aging mechanisms KW - Corrosion KW - Safety assessment KW - Metal seals KW - Closure system KW - Spent fuel/high-level waste KW - Dual purpose casks KW - Metal seals reliability KW - Cesium corrosion PY - 2014 UR - http://psam12.org/proceedings/paper/paper_180_1.pdf SP - 1 EP - 10 AN - OPUS4-32518 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Siebler, Daniel A1 - Rohwetter, Philipp A1 - Brusenbach, R. A1 - Lothongkam, Chaiyaporn A1 - Heidmann, G. A1 - Leistner, A. A1 - Plath, R. T1 - Sensitivity-enhanced detection of partial discharge in cable accessories using fluorescent polymer optical fibre-sensor N2 - A new fluorescent polymer optical fibre sensor (F-POF) has been tested in combination with different single photon counting modules in real-scale model of a translucent high voltage (HV) stress cone for the detection of inner partial discharges (PDs). In experiments with different artificial PD sources these sensors were capable to detect discharges with an apparent Charge down to the limit of a few hundred femto Coulombs even with an unfavorable sensor location. By combining the datasets of the electrical and optical PD measurement (coincidence window ±100 ns) it is possible to suppress background noise and to undoubtedly assign signals to real inner PD events. First results of an optical/optical coincident PD measurement (coincidence interval ±100 ns) including an AC phase-correlated filtering show several coincident photon counts in the ränge of 1-2 pC over the whole Observation interval, indicating the potential ofthis new alternative PD measurement and evaluation method. T2 - POF 2014 - 23nd International conference on plastic optical fibers CY - Hiyoshi, Yokohama, Japan DA - 08.10.2014 KW - Polymer optical fibre KW - Partial discharge sensor KW - Fkuorescence KW - High voltage facility PY - 2014 SP - 1 EP - 5 AN - OPUS4-32531 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lothongkam, Chaiyaporn A1 - Siebler, Daniel A1 - Heidmann, G. A1 - Plath, R. A1 - Gockenbach, E. T1 - The influence of thermal aging on AC dielectric strength of transparent silicone rubbers for HV insulation N2 - Optical methods and monitoring systems for the PD detection in GIS, GIL and oil-immersed type transformers have been demonstrated. Very recently these methods have been extended to the detection of PDs in solid insulation materials of cable accessories. This novel application in high-voltage (HV) cable terminations consists of integrated fiber-optic sensor which requires transparent insulation materials. Therefore, transparent silicone rubbers are considered as replacement material for currently used opaque elastomeric insulation material in stress cones of HV cable accessories. For this purpose a preliminary study on the long-term stability of two commercially available fully transparent silicone rubbers was performed. Accelerated thermal aging tests were carried out for 4 hours up to 100 hours at 200 °C under a normal air atmosphere and normal atmospheric pressure. The impact of thermal aging on the AC dielectric strength of the silicone samples was investigated and additionally the optical transmittance was determined using UV-Vis spectrophotometer. The investigation indicated that the dielectric strength value of the silicone samples was seriously reduced for long-term exposures to elevated temperatures. In addition, the UV-visible transmittance of thermally aged silicone samples was also decreased. The influence of these phenomena must be taken into account for the design of HV insulation materials, particularly under extremely high temperature operating conditions. T2 - ISEIM 2014 - 7th International symposium on electrical insulating materials CY - Niigata City, Japan DA - 01.06.2014 KW - AC dielectric strength KW - Thermal aging KW - Silicone elastomer KW - HV insulation KW - Silicone rubbers KW - Optical transmittance KW - Rubber stress cone PY - 2014 DO - https://doi.org/10.1109/ISEIM.2014.6870790 SP - 346 EP - 349 PB - IEEE AN - OPUS4-32533 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Miccoli, Lorenzo A1 - Fontana, Patrick ED - Pena, F. ED - Chávez, M. T1 - Bond strength performances of anchor pins for earthen buildings. A comparison between earth block masonry, rammed earth and cob N2 - Connections improvement plays a key role in seismic upgrade of historical buildings. Their global response is related to the behavior of the single structural elements as well as to their mutual connections. Up to now only few data are available about the performance of grouted anchor pins in earthen materials where the critical point is the bond between the grout and the earthen substrate. In this paper, results of the experimental testing performed on earth block masonry, rammed earth and cob are presented. Pull-out tests were carried out to investigate the bond strength and failure modes of stainless steel rods with a lime based hydraulic grout and their compatibility with earthen materials. Rods with nuts were investigated to improve the pull-out capacity of the anchors. They showed higher pull-out capacity than rods without nuts. The performances of rods with nuts in cob were influenced by the rough surface at/of the earthen substrate. It is assumed that the non homogeneous surface caused an interlocking mechanism, which allowed to reach a pull-out capacity of about 54% higher than in earth block masonry. T2 - SAHC 2014 - 9th International conference on structural analysis of historical constructions CY - Mexiko City, Mexico DA - 14.10.2014 KW - Earthen materials KW - Pull-out tests KW - Anchor pins KW - Lime based hydraulic gout PY - 2014 SP - Paper-ID 07/011, 1-13 AN - OPUS4-32537 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Silva, R.A. A1 - Oliveira, D.V. A1 - Miccoli, Lorenzo A1 - Schueremans, L. ED - Pena, F. ED - Chávez, M. T1 - Modelling of rammed earth under shear loading N2 - The intensive use of earth as a building material since ancient times resulted in an important and significant earthen built heritage currently existing worldwide spread. The rammed earth technique has a significant presence in this heritage, where it served to build from simple dwell-ings to fortresses. However, the high vulnerability of rammed earth constructions to decay agents and to seismic events puts in risk their further existence and the lives of millions of peo-ple. With respect to the seismic behaviour of rammed earth walls, the understanding and mod-elling of their shear behaviour are topics underdeveloped in the bibliography. Nevertheless, these topics are of extreme importance in the preservation and strengthening of rammed earth constructions. Therefore, this paper presents a numerical work aiming at modelling the non-linear behaviour of unstabilised rammed earth under shear loading, resorting to the finite ele-ments method (FEM). The models were used to simulate the behaviour of a set of rammed earth wallets tested under diagonal compression. Both macro- and micro-modelling approach-es were considered, where the objective of this last approach was to evaluate the influence of apparent weakness of the interfaces between layers on the shear behaviour. The total strain ro-tating crack model (TSCRM) was used to simulate the behaviour of the rammed earth material, while the Mohr-Coulomb failure criterion was used to simulate the behaviour of interfaces be-tween layers. Furthermore, uncertainties related to the definition of the input parameters re-quired performing a sensitivity analysis. The numerical models achieved good agreement with the experimental results and the compressive strength, the Poisson’s ratio, the tensile strength and the tensile fracture energy revealed to be the most important parameters in the analyses. T2 - SAHC 2014 - 9th International conference on structural analysis of historical constructions CY - Mexiko City, Mexico DA - 14.10.2014 KW - Rammed earth KW - Diagonal-compression KW - Shear behaviour KW - FEM modelling PY - 2014 SP - Paper-ID 08/015, 1-12 AN - OPUS4-32538 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Mietz, Jürgen A1 - Fischer, Joachim T1 - Spannungsrisskorrosion an Spannstahl - Ringversuch zur Prüfung der Spannungsrisskorrosion an Spannstählen N2 - Für Spannstähle muss im Rahmen der Überwachung die Beständigkeit gegenüber Spannungsrisskorrosion nach DIN EN ISO 15630-3 nachgewiesen werden. Die Stähle werden hierbei entweder einer konzentrierten Ammoniumthiocyanatlösung oder einer verdünnten Lösung, die eher die Verhältnisse in der Baupraxis wiedergibt, ausgesetzt. In den vergangenen Jahren gab es an Spannstäben der Festigkeitsklasse St 950/1050 immer wieder Probleme mit dem Erreichen der erforderlichen Standzeiten in der konzentrierten Lösung. Der Ringversuch sollte nun klären, inwieweit Unsicherheiten hinsichtlich der Zuverlässigkeit und Aussagekraft der Ergebnisse von Spannungsrisskorrosionsprüfungen bestehen. Außerdem sollten die Prüfanweisungen, die Prüfeinrichtungen sowie die Vor-Ort-Inspektion der Prüfstände kritisch beurteilt werden, um eventuell vorhandene versuchstechnische Probleme zu identifizieren und ggf. zu beheben. PY - 2015 SP - T 3306, 1 EP - 29 PB - Fraunhofer IRB Verl. AN - OPUS4-32461 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Müller, Christina A1 - Heckel, Thomas A1 - Brömel, Philip A1 - Pavlovic, Mato A1 - Ronneteg, U. T1 - Attenuation dependent detectability at ultrasonic inspection of copper N2 - This report describes the progress in understanding and describing the detectability of the ultrasonic inspection technique developed by SKB for the inspection of copper tubes used for the final disposal of the Swedish spent nuclear fuel. In former research activities dedicated to the different parts of the canister, the probability of detection (POD) evaluation technique, as developed for thin aircraft components, was further developed for the application on complex hick-walled components. The result of this development was the introduction of a “multi-parameter” POD framework. In contrast to taking only the defect size into consideration (as for aircraft components) additional influencing factors, relevant for thick components, such as depth position, orientation and part geometry, were included. Furthermore, the variation of ultrasonic attenuation due to various material properties was included. PY - 2014 SP - ID 1411328, 1 EP - 54 AN - OPUS4-32522 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN ED - Beck, Uwe ED - Pfuch, A. ED - Rietz, U. ED - Lerche, D. T1 - Klebfestigkeit - Validierung der Prozesskette Vorbehandeln - Kleben - Prüfung im Rahmen eines AiF-Projektes OKTETT N2 - Mit einer neuartigen analytischen Zentrifuge können Klebverbindungen, Beschichtungen und Kompositwerkstoffe untersucht werden. Die Idee der Wissenschaftler an der BAM Bundesanstalt für Materialforschung und -prüfung: Die Proben müssen nicht mehr eingespannt, sondern nur noch eingesteckt werden. Durch das einfache Einstecken der Prüfkörper ist eine sehr schnelle Beladung möglich. Zudem können bis zu acht Proben gleichzeitig unter identischen Bedingungen geprüft werden. Konventionelle Zugprüfmaschinen waren und sind nur in der Lage, einen (eingespannten) Probekörper zu testen. Das von BAM-Forschern bereits 2004 zum Patent angemeldete Funktionsprinzip wurde seitdem von der Berliner LUM GmbH als Lizenznehmer zum marktreifen Produkt weiterentwickelt. KW - Klebfestigkeit KW - Haftfestigkeit KW - Mehr-Proben-Vorbehandeln/Kleben/Prüfen PY - 2015 UR - http://idw-online.de/de/news623384 SP - 1 AN - OPUS4-32523 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Masslowski, Jörg-Peter A1 - Trapp, R. T1 - Type B casks for the intermediate storage of spent fuel elements in the Federal Republic of Germany T2 - PATRAM ´80 - 6th International symposium on the packaging and transportation of radioactive materials CY - Berlin, Germany DA - 1980-11-10 PY - 1981 VL - 2 SP - 961 EP - 965 PB - Bundesanstalt für Materialprüfung CY - Springfield, Va. AN - OPUS4-31933 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz-Forberg, Bernd T1 - The transportation of radioactive materials in the Federal Republic of Germany T2 - PATRAM ´80 - 6th International symposium on the packaging and transportation of radioactive materials CY - Berlin, Germany DA - 1980-11-10 PY - 1981 VL - 2 SP - 1438 EP - 1454 PB - Bundesanstalt für Materialprüfung CY - Springfield, Va. AN - OPUS4-31935 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Yoshimura, H. R. A1 - Pope, R. B. A1 - Leisher, W. B. A1 - Joseph, B. J. A1 - Schulz-Forberg, Bernd A1 - Hubner, H. W. T1 - Extended testing of a modified 18B plutonium nitrate shipping container T2 - PATRAM ´80 - 6th International symposium on the packaging and transportation of radioactive materials CY - Berlin, Germany DA - 1980-11-10 PY - 1981 VL - 2 SP - 1230 EP - 1237 PB - Bundesanstalt für Materialprüfung CY - Springfield, Va. AN - OPUS4-31937 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz-Forberg, Bernd A1 - Hübner, Heinz W. T1 - Classification and safety margins of RAM packagings - results of a research programme T2 - PATRAM ´80 - 6th International symposium on the packaging and transportation of radioactive materials CY - Berlin, Germany DA - 1980-11-10 PY - 1981 VL - 2 SP - 1254 EP - 1258 PB - Bundesanstalt für Materialprüfung CY - Springfield, Va. AN - OPUS4-31938 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simon, Franz-Georg A1 - Holm, Olaf T1 - Recovery of metals from waste, an example for the resource cycle N2 - Bottom ash from municipal solid waste incineration (MSWI) consists of elemental metals in considerable amounts. The fine fraction < 4 mm additionally contains chemically bound metals (oxides, carbonates, silicates). Separation prospects with techniques as in ore processing (flotation, density separation, bioleaching, hydrothermal solution) are discussed. During alteration after wet extraction mineral material with hydraulic properties form coatings on almost all particles of the bottom ash and complicate separation procedures. In addition bottom ash from MSWI is a heterogeneous material. For sufficient enrichment different concerted treatment steps seemed to be essential associated with an uncertainty of economic viability. The utilisation of metal compounds present in bottom ash as secondary raw material depends on the energy- and resource-efficiency of the enrichment processes. Therefore energy and material flow considerations are presented. T2 - WRF 2013 - World Resources Forum conference CY - Davos, Switzerland DA - 06.10.2013 KW - Recyclable material KW - Recycling technology KW - Environmental technology KW - Waste management PY - 2013 UR - http://www.atr.bam.de/de/medien/2013_simon_wrf.pdf SP - 1 EP - 6 AN - OPUS4-32011 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - White, J. A1 - Wolf, Julia A1 - Shokouhi, Parisa A1 - Hurlebaus, S. A1 - Wimsatt, Andrew T1 - Concrete tunnel lining evaluation using nondestructive techniques: a multi-method case study at Eisenhower tunnel N2 - An in-depth investigation of tunnel linings is performed at Eisenhower Tunnel, 60 miles west of Denver, Colorado, using a combination of four nondestructive testing methods: air- and ground-coupled ground penetrating radar (GPR), ultrasonic echo (US echo), ultrasonic tomography (UST), and impact echo (IE). A robotic frame with pneumatically operated vacuum plates is used to automate GPR, US echo, and IE. UST was performed manually. These techniques are used to identify and locate the reinforcement mesh and structural steel ribs. Local changes in ultrasonic phase are calculated by phase analysis processing techniques and apparent relationships between positive and negative phase shifts and steel and air interfaces are observed. According to previous laboratory research, these relationships indicate the bonded state between the concrete and the embedded steel, but without ground truth verification this can only be suggested. It is shown that this combination of methods can be used synergistically to provide tunnel owners with the layout and possible condition of tunnel lining reinforcement and structural components. T2 - TRB 92nd Annual meeting CY - Washington, D.C., USA DA - 13.01.2013 KW - Nondestructive evaluation KW - Concrete KW - Ultrasonic KW - GPR KW - Impact echo PY - 2013 UR - http://trid.trb.org/view.aspx?id=1242002 SP - 1 EP - 16 AN - OPUS4-32025 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - White, J. A1 - Wolf, Julia A1 - Shokouhi, Parisa A1 - Hurlebaus, S. A1 - Wimsatt, Andrew T1 - Nondestructive evaluation of concrete linings at Hanging Lake tunnel N2 - Tunnel lining evaluation is performed in the Hanging Lake Tunnel near Glenwood Springs, Colorado, using variations of four nondestructive evaluation (NDE) methods: air- and ground-coupled ground penetrating radar (GPR), ultrasonic echo (US echo), ultrasonic tomography (UST), and impact echo (IE). Potential regions of interest are identified using high-speed air-coupled GPR and visual inspection. A robotic frame with pneumatically-operated vacuum plates was used to automate the ground-coupled GPR, US echo, and IE tests, while the UST technique was used manually. This study shows that a particular combination of NDE techniques is a powerful tool for assessing the condition of tunnel linings and can detect potential anomalies such as delamination, depth of surface cracks, reinforcement depth and layout, and lining thickness. By mapping the phase shift of the ultrasonic pulses at detected interface, the potential bonding of layer interfaces and reinforcement is assessed. T2 - TRB 92nd Annual meeting CY - Washington, D.C., USA DA - 13.01.2013 KW - Nondestructive evaluation KW - Concrete KW - Ultrasonic KW - GPR KW - Impact echo PY - 2013 UR - http://trid.trb.org/view.aspx?id=1241994 SP - 1 EP - 16 AN - OPUS4-32027 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brosig, Laura A1 - Horn, Wolfgang A1 - Jann, Oliver T1 - Ringversuche zur Einführung von Geruchsmessungen in die Bewertung von Bauprodukten entsprechend der DIN ISO 16000-28 und VDI 4302-1 N2 - The DIN ISO 16000-28 and VDI 4302-1 describe a method for the assessment of the perceived intensity of odours. It is based on a trained assessment panel using a referencing scale that provides defined acetone concentrations. Due to the AgBB-scheme including a place holder for odour assessment it is currently checked whether the method is applicable. To check the applicability a pilot phase regarding the „Implementation of Odour Measurements into the Assessment of Building Products“ was started by AgBB1 in 2012. Düring this phase amongst others two interlaboratory tests were conducted. The first one in 2012 served to test the applicability and to identify need and potential for improvement. Based on those findings an additional Standard Operation procedure was developed for the second interlaboratory test in 2014. The second interlaboratory test confirmed the findings of the first one and the need for improvement of the measurement method as well. Nonetheless both tests showed Standard deviations of reproducibility between 20 and 40%. Standard deviations of reproducibility of well-established interlaboratory tests for VOCs show comparable results. T2 - 17. Workshop - Geruch und Emissionen bei Kunststoffen CY - Kassel, Germany DA - 16.03.2015 PY - 2015 SP - 8-1 EP - 8-9 AN - OPUS4-33075 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dittrich, Matthias A1 - Kasparek, Eva Maria A1 - Völzke, Holger T1 - Präzisierung der Prüfanforderungen an Stahlblechcontainer für das Endlager Konrad N2 - Abfallgebinde, die im Endlager Konrad eingelagert werden sollen, müssen die Anforderungen und Kriterien erfüllen, die in den Endlagerungsbedingungen (SE-IB-29/08-Rev-1 [1]) und in der Produktkontrolle (SE-IB-30/08-Rev-1) festgelegt sind. Die Qualifizierung der Abfallbehälter erfolgt auf dieser Grundlage in Form von Bauartprüfungen, die von der Bundesanstalt für Materialforschung und -prüfung (BAM) im Auftrag des Bundesamtes für Strahlenschutz (BfS) durchgeführt werden. Darüber hinaus sind die im Hinblick auf Behälterbauartprüfungen relevanten Nebenbestimmungen aus dem Planfeststellungsbeschluss für das Endlager Konrad zu berücksichtigen. Zur besseren Anwendbarkeit werden diese Nebenbestimmungen in die Endlagerungsbedingungen und die Produktkontrolle eingearbeitet. Begleitend ist als Hilfestellung für die Abfallablieferer und Behälterhersteller ein Leitfaden geplant, der praktikable Nachweisstrategien aufzeigt und, soweit erforderlich, Hintergrundinformationen zu den Spezifikationen der Regelwerke liefert. Die BAM ist vom BfS beauftragt, hierfür Vorschläge zu entwickeln und Empfehlungen abzugeben. T2 - KONTEC 2015 - 12. Internationales Symposium "Konditionierung radioaktiver Betriebs- und Stilllegungsabfälle" CY - Dresden, Germany DA - 25.03.2015 PY - 2015 SP - Paper 090, 786 EP - 794 AN - OPUS4-33020 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nolze, Gert A1 - Winkelmann, Aimo T1 - The challenge of band detection T2 - RMS Electron backscatter diffraction meeting CY - Glasgow, UK DA - 2015-03-30 KW - EBSD KW - Electron diffraction KW - Band detection KW - Simulation PY - 2015 SP - 1 EP - 2(?) AN - OPUS4-33029 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Winkelmann, Aimo A1 - Nolze, Gert T1 - Orientation mapping of non-centrosymmetric crystals T2 - RMS Electron backscatter diffraction meeting CY - Glasgow, UK DA - 30.03.2015 KW - EBSD KW - Cross-correlation KW - Non-centrosymmetry KW - Simulation PY - 2015 SP - 1 AN - OPUS4-33030 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Maierhofer, Christiane A1 - Krankenhagen, Rainer A1 - Myrach, Philipp A1 - Röllig, Mathias A1 - Mecke, R. A1 - Schiller, M. A1 - Seidl, T. A1 - Kalisch, U. A1 - Hennen, C. A1 - Meinhardt, J. A1 - Kersten, H. A1 - Groll, E.T. T1 - 3D-Kartierung von oberflächennahen Schäden an Bauwerken und Bauteilen N2 - Die messtechnische Erfassung von Bauwerkschäden ist eine wichtige Voraussetzung für die dreidimensionale und zeitaufgelöste Darstellung von möglicherweise sicherheitsrelevanten Veränderungen an Bauwerken, wie z. B. Verformungen, Verwindungen und Risswachstum. Ziel des vorgestellten Projektes war die Entwicklung eines Verfahrens zur effizienten und wiederholbaren 3D-Schadenkartierung an zum Teil empfindlichen Bauteiloberflächen. KW - 3D-Kartierung KW - Aktive Thermografie KW - Photogrammetrie KW - Trackingsystem KW - Risse PY - 2015 IS - März SP - 35 EP - 39 PB - Ernst & Sohn CY - Berlin AN - OPUS4-33084 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rolle, Annette A1 - Droste, Bernhard A1 - Schubert, Sven A1 - Probst, Ulrich A1 - Wille, Frank T1 - Verification of activity release compliance with regulatory limits within spent fuel transport casks T2 - PATRAM 2010 - 16th International symposium on the packaging and transport of radioactive materials CY - London, UK DA - 2010-10-03 KW - Radioactive material KW - Safety assessment KW - Leakage mechanism KW - Leakage rate KW - Sealing behavior PY - 2010 SP - 1 EP - 8(?) AN - OPUS4-32193 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rolle, Annette A1 - Winkler, H. P. A1 - Probst, Ulrich A1 - Ballheimer, Viktor A1 - Neumeyer, Tino T1 - Verification of design leakage rates for activity release calculation N2 - The mechanical and thermal loadings associated with the routine, normal and accident conditions of transport can have a significant effect on the leak tightness of the sealing system of transport casks for spent fuel and high radioactive waste. Applicants are requested by BAM to provide test programmes for verification of design leakage rates of the sealing system under the possible loads. Two test series initiated to clarify the dependency of the standard leakage rate on dynamic lid displacement as well as the dependency of the useful elastic recovery ru of a metallic seal on temperature and time, are outlined in this paper as examples of present investigations: Sliding tests simulating a lid displacement possible by a horizontal drop of the cask are carried out at the controlled drop test facility of BAM with test flange pairs equipped with metallic Helicoflex seals. For specification of covering values for the useful elastic recovery ru GNS has started a very comprehensive test programme with overall 70 metallic seals installed in test flanges which are stored for a period of one year at three different temperatures up to 150°C. This paper gives an overview about the current approach of BAM in the assessment of cask tightness and informs about the status of the running test series. T2 - PATRAM 2013 - 17th International symposium on the packaging and transportation of radioactive materials CY - San Francisco, CA, USA DA - 2013-08-18 KW - Radioactive material KW - Safety assessment KW - Leakage rate KW - Leak tightness KW - Sealing behavior PY - 2013 SP - 1 EP - 7 PB - Omnipress AN - OPUS4-32194 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völzke, Holger T1 - The German aging management approach for dry spent fuel storage in dual purpose casks N2 - Since the decision by the German government to face out nuclear electricity generation the total amount of spent nuclear fuel and high level wastes from reprocessing is limited and well determined. In addition the siting and licensing procedure to establish a final repository has been ruled by a new law in the mid of 2013 and further delays are very likely until a deep geological repository may start its operation. In the meantime dry interim storage in dual purpose casks being permanently certified for interim storage as well as transportation is the established technical solution. Several on-site as well former centralized facilities are operated successfully for many years but storage licenses are generally limited to 40 years and future lifetime extensions are predictable. Permanent aging management for storage facilities and casks is necessary to demonstrate compliance with safety requirements and furthermore to gain relevant data and information about the technical conditions of the facilities and their components for future lifetime extensions. For that reason procedures and measures are currently improved and the approach is explained in this paper. In addition, the current status and latest experiences concerning periodic safety inspections and aging management measures are discussed. T2 - PSAM 12 - Probabilistic safety assessment and management CY - Honolulu, Hawaii, USA DA - 22.06.2014 KW - Interim storage KW - Dual purpose casks KW - Spent nuclear fuel KW - Aging management PY - 2014 SP - T06 - Doc.183, 1-7 AN - OPUS4-32250 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gründer, Klaus-Peter A1 - Goedecke, Thomas A1 - Kadoke, Daniel A1 - Müller, Karsten A1 - Münzenberger, Sven A1 - Protz, Christian T1 - Prüfung von Gefahrgutumschließungen mit optischen 3D-Messverfahren N2 - Der Beitrag konzentriert sich auf bildgebende Messverfahren, die der dreidimensionalen Bestimmung mechanischer, geometrischer und kinematischer Parameter von Materialien und Bauteilen dienen. Das sind hier insbesondere die Mehrbildfotogrammetrie sowie die Stereomessverfahren, die auf folgenden physikalisch-optischen Grundlagen beruhen: die zeit- und raumveränderliche Projektion von Lichtstreifensystemen, die Bildkorrelation mittels Grauwertmustern und die Verfolgung kontrastreich applizierter Punkttargets. Letztendlich werden aus den gemessenen Punktkoordinaten unterschiedlicher Dichte und Belastungszustände die gewünschten 3D-Parameter abgeleitet. Hierzu gehören z. B. die Oberflächengestalt und deren Verformung, approximierte 3D-Geometrielemente, veränderliche 6DoF-Starrkörperorientierungen, Vektorverschiebungsfelder, Oberflächendehnung, Koordinaten-Zeit-Funktionen, Geschwindigkeit und Beschleunigung. Diese Kenngrößen sind beispielsweise für die Ermittlung mechanischer Werkstoffeigenschaften und -kennwerte bis hin zur Form- und Verformungsmessung von Bauteilen in gezielt quasi-statisch oder dynamisch beanspruchenden Prüfeinrichtungen wichtig. Vorteilhaft für die praktische Anwendung dieser Verfahren ist insbesondere, dass sie berührungslos arbeiten, kombiniert werden können und skalierbar sind z. B. hinsichtlich Messvolumen, Auflösung, Genauigkeit und Koordinatensystemen der zu bestimmenden 3D-Punktkoordinaten an Materialoberflächen bzw. Komponenten. Ausgehend von der Beschreibung der messtechnischen Prinzipien dieser Verfahren sollen zwei Anwendungsbeispiele aus dem Bereich der Gefahrgutbehäl-terprüfung im Rahmen von Bauartzulassungen und der normungsbegleitenden Mate-rialforschung den Stand in der Anwendungspraxis aufzeigen und einen Eindruck hinsichtlich der flexiblen Einsatzmöglichkeiten dieser optischen 3D-Verfahren verdeutlichen. T2 - 4. Fachseminar Optische Prüf- und Messverfahren CY - Hamburg, Germany DA - 17.03.2015 KW - 3D-Messverfahren KW - Verformung KW - Dehnung KW - Bremsbeschleunigung PY - 2015 SP - Vortrag 9, 1 EP - 10 AN - OPUS4-32808 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hantsche, Harald T1 - Gesichtspunkte bei der Beschaffung eines Oberflächenanalysengerätes für AES/SAM, ESCA, SIMS und ISS T2 - 5. Sitzung des Arbeitsausschusses Geräteentwicklung im Arbeitskreis Rastermikroskopie CY - Wien DA - 1980-11-06 PY - 1981 SP - 47 EP - 81 PB - DVM CY - Berlin AN - OPUS4-33266 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Strauß, B. T1 - Einige einfache Tests für Rasterelektronenmikroskope, durchgeführt am Stereoscan 180 T2 - 5. Sitzung des Arbeitsausschusses Geräteentwicklung im Arbeitskreis Rastermikroskopie CY - Wien DA - 1980-11-06 PY - 1981 SP - 13 EP - 26 PB - DVM CY - Berlin AN - OPUS4-33267 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krankenhagen, Rainer A1 - Worzewski, Tamara A1 - Doroshtnasir, Manoucher A1 - Röllig, Mathias A1 - Studemund, Taarna T1 - Inspecting rotor blades by thermographic monitoring from greater distances N2 - The paper presents some of the results obtained within a project concerning the validation of the thermographic inspection method applied to rotor blades of wind turbines. Thermographic testing (TT) is a well established nondestructive testing method under laboratory conditions. It is suited to detect typical structural features and also faults and damages within the blade structure. However, the onsite application for wind turbines during Operation is not straightforward. Some resuits of non-rotating blades as well as of rotating blades are presented. The simultaneous recording of all blades in the rotating state allows the application of a reference method suppressing disturbing influences and leading to enhanced thermal contrasts. T2 - DEWEK 2015 CY - Bremen, Deutschland DA - 19.05.2015 PY - 2015 AN - OPUS4-33272 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Becker, Gerhard Wilhelm T1 - O que pensa a Alemanha da normalizacao (Wie funktioniert die deutsche Normierung) PY - 1981 IS - 9 SP - 21,22,24 PB - Aranda CY - Sao Paulo, Brazil AN - OPUS4-33240 LA - por AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Plarre, Rüdiger ED - Fänger, H. T1 - Die Kleidermotte - Eine kleine Natur- und Kulturgeschichte N2 - Zu den unerwünschten Gästen im Museum oder im Haushalt gehört zweifelsohne die Kleidermotte (Abb. 1). Umherfliegende kleine Falter mit lanzettförmigen rostgelben Flügeln oder aber Lochfraß in der Kleidung sind oftmals die ersten Anzeichen ihrer Anwesenheit. Tineola bisselliella, so der wissenschaftliche Name der Kleidermotte, ist weltweit der wirtschaftlich bedeutendste Schädling an allen Materialien, die aus Körperbedeckungen tierischer Herkunft wie Wolle, Federn, Felle, Haare, etc. hergestellt werden. Sie befällt z. B. ausgestopfte Tiere in naturkundlichen Sammlungen oder den Indianer-Federschmuck im Ethnologischen Museum. Im Haushalt findet man Löcher im Pullover oder kahle Stellen am Wollteppich. PY - 2014 VL - 58 IS - Oktober SP - 23 EP - 25 PB - Pest Control News Ldt. AN - OPUS4-32074 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Daum, Werner T1 - Sensing with optical fibres N2 - Starting from the first patent of a fibre optic sensor in 1967, fibre optic sensing has become a success story throughout the world. Today, fibre optic point sensors and continuous distributed fibre optics sensor systems allow the measurement of nearly all physical quantities and contribute to higher safety levels in many industrial sectors. Monitoring of pipelines, power cables, lightweight and civil engineering structures, and of ground movements are heading the hit list of applications. Standardization in this field is of paramount relevance and brings to light some of the challenges now faced by IEC SC (Subcommittee) 86C/WG (Working Group) 2: Fibre optic sensors. KW - Sensing KW - Optical Fibres PY - 2014 UR - http://www.iec.ch/etech/2014/etech_1114/ind-1.htm IS - November SP - 1 EP - 3 CY - Genova AN - OPUS4-32149 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Peuckert, J. A1 - De Souza, T.L. A1 - Mangelsdorf, Axel ED - Goncalves, J. ED - Göthner, K.-C. ED - Rovira, S. T1 - Infraestructura de la calidad e innovación N2 - El sólido vínculo entre las instituciones sociales de control de la calidad y la innovación no siempre resulta obvio. En los párrafos que siguen se sostiene que los servicios de normalización, metrología, evaluación del cumplimiento de las normas y acreditación prestados por la Infraestructura Nacional de la Calidad (INC) son grandes propulsores de nuevos avances sociales y tecnológicos. Todos los elementos de la infraestructura de la calidad ayudan a la sociedad a hacer frente a distintos desafíos en un entorno cambiante, mediante la creación y difusión de nuevas tecnologías. PY - 2014 UR - http://repositorio.cepal.org/bitstream/handle/11362/36634/S2014154_es.pdf?sequence=1 N1 - Serientitel: Colección Documentos de proyectos – Series title: Colección Documentos de proyectos IS - LC/W.588 SP - 25 EP - 32 AN - OPUS4-32727 LA - spa AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Habel, Wolfgang A1 - Schukar, Vivien A1 - Hofmann, Detlef T1 - Requirements to establish fibre-optic sensors for monitoring of structures N2 - Fibre-optic sensors need to be more established in the sensor market. Their advantages have unquestionably been verified by numerous demonstrations. However, there are some open questions leading now and then to restraints in the user's community. The paper dicusses examples where fibre-optic sensors provide outstanding knowledge about the structure's behaviour, but application is often challenging. Requirements are listed and open questions to be solved are discussed. Short outlook to standards useful for better design, characterization and application is given. Standards are the basis for establiching SHM systems, especially for safety-critical structural diagnostics. T2 - EWSHM 2014 - 7th European workshop on structural health monitoring CY - Nantes, France DA - 08.07.2014 KW - Monitoring KW - Fibre-optic sensor KW - Reliability KW - Application PY - 2014 SP - 2330 EP - 2337 AN - OPUS4-32662 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Habel, Wolfgang A1 - Hofmann, Detlef A1 - Döring, H. A1 - Jentsch, H. A1 - Senze, A. A1 - Kowalle, G. ED - Shi, B. T1 - Detection of a slipping soil area in an open coal pit by embedded fibre-optic sensing rods N2 - Movements in geological areas are mostly concentrated on faults or slipping zones. Detection of movements reaching critical values is of crucial importance to avoid losses and harms. The paper presents a new technology of detecting deformations and movements in soil or rock massifs. The core part of the sensing system is a tiny rod with embedded optical sensor fibres. This deformation measurement system was developed and the sensing rod can be installed in a borehole and enables the detection of beginning soil movements. The amount of deformation in soil or rock formations can then be estimated. The sensing rod has an outer diameter of 3 mm to 6 mm and contains several optical fibres. One fibre is used as online measurement system and provides integral strain information along the whole length of the rod. In case of a safety-relevant deformation (warning signal), the second sensing system based on fibre Bragg grating sensors positioned close to the expected shear zone will be activated and records then resulting deformations in detail. T2 - OSMG-2014 - 5th International forum on opto-electronic sensor-based monitoring in geo-engineering CY - Nanjing, China DA - 12.10.2014 KW - Fibre-optic strain sensor KW - Structural health monitoring KW - Soil stability monitoring KW - Early warning PY - 2014 SP - 1 EP - 7 AN - OPUS4-32664 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nolze, Gert T1 - Inverse pole-figure colouring: traps and possible solutions N2 - The visualization of spatially resolved single Orientation data, e.g. collected by electron backscatter diffraction (EBSD) in the scanning electron microscope (SEM), is still a challenge since some Orientation coloring schemes have low color sensitivity, and/or specific color discontinuities. The latter appear even for crystal Orientations which are practically identical and characterized only by a tiny misorientation. Euler angle coloring schemes suffer from their lack of intuitiveness. The inverse pole figure (IPF) coloring that has been widely accepted does not display the real Orientation Information for each measurement point, but only the crystallographic description of a single reference direction. For the representation of the complete Orientation information at least a second IPF Orientation map must be shown which displays the crystallographic description for another reference direction. In this context it must be pointed out that the IPF coloring is also not immune to color discontinuities, which are visible as speckled grains (and usually misinterpreted as erroneous Orientation determinations by EBSD). However, a general analysis of the commonly used color keys shows that color discontinuities are a consequence of the crystal symmetry for 6 of the 11 centrosymmetric Laue groups. This means that the Orientation description is correct, but the representation tool is inappropriate for properly displaying the orientation information. T2 - EMAS 2013 - 13th European workshop on modern developments and applications in microbeam analysis CY - Porto, Portugal DA - 12.05.2013 KW - BSE contrast KW - Intensity extraction KW - Background PY - 2013 SP - 386 AN - OPUS4-32669 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Löschau, Gerhard T1 - Modellmäßige Darstellung von Säulenstapeln zur vereinfachten Bestimmung der kritischen Lagerhöhe PY - 1981 VL - 32 IS - 4 SP - 25 EP - 32 PB - Keppler CY - Heusenstamm AN - OPUS4-31833 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Löschau, Gerhard T1 - Untersuchung von Einflußgrößen bei der Bestimmung der zulässigen Säulen-Stapelhöhe im Vorratslager PY - 1981 VL - 32 IS - 10 SP - 73 EP - 82 PB - Keppler CY - Heusenstamm AN - OPUS4-31834 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mishra, Kirti Bhushan A1 - Wehrstedt, Klaus-Dieter T1 - Rheinland refinery accident 2014: CFD prediction of atmospheric dispersion of smoke N2 - Industrial fire and explosion hazards are most often also associated with the dispersion of toxic substances. These substances can be gases, liquids, solids or in form of aerosols. The critical toxic exposure limits to People and enviroment from such substances are regulated by the concerned authorities of the countries. In order to comply with the defined regulation estimation of such critical limits must be carried out by different semi-empirical and phenomenological models/methods for risk assessment. Many of such methods provide a qualitative estimation of time and space dependent extrimities of toxicity. The overwhelm development of computational capacity has made it possible to perform Computational Fluid Dynamics (CFD) simulation by solving the three-dimensional transport equations for mass momentum and species in lower and upper atmosphere, respectively. CFD simulation not only provides a detailed 3D distribution of toxic particulates/gases in the neighbourhood of the plant but also helps to study the worst-case sceanrios. In the past several small- and large-scale accidents occured in oil and gas plants in different parts of the world including the recent one in Rheinland refinery near Cologne in Germany. This work deals with this accident and provides a methodology to predict the critical exposure limits of smoke emitted by a toluene tank fire by means of CFD simulation. T2 - COMBURA 2014 - Combustion research and application symposium CY - Soesterberg, The Netherlands DA - 08.10.2014 KW - CFD KW - Retinery incident KW - Smoke dispersion PY - 2014 SP - 56 EP - 57 AN - OPUS4-31721 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Ziegler, Kurt T1 - Über die Beeinflussung des Detonationsmechanismus von schlammförmigen und pulverförmigen Sprengstoffen durch die Verwendung von Sprengschnüren als Zündmittel PY - 1981 SP - 1 EP - 188 PB - Technische Universität CY - Berlin AN - OPUS4-31950 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Nohr, Michael T1 - Development of a material with reproducible emission of selected volatile organic compounds PY - 2014 SP - 1 EP - 133 AN - OPUS4-31954 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Komann, Steffen A1 - Wille, Frank A1 - Droste, Bernhard T1 - Gap analysis examples from periodical reviews of transport package design safety reports of SNF/HLW dual purpose casks N2 - Storage of spent nuclear fuel and high-level waste in dual purpose casks (DPC) is related with the challenge of maintaining safety for transportation over several decades of storage. Beside consideration of aging mechanisms by appropriate design, material selection and operational controls to assure technical reliability by aging management measures, an essential issue is the continuous control and update of the DPC safety case. Not only the technical objects are subject of aging but also the safety demonstration basis is subject of "aging" due to possible changes of regulations, standards and scientific/technical knowledge. The basic document, defining the transport safety conditions, is the package design safety report (PDSR) for the transport version of the DPC. To ensure a safe transport in future to a destination which is not known yet (because of not yet existing repository sites) periodical reviews of the PDSR, in connection with periodic renewals of package design approval certificates, have to be carried out. The main reviewing tool is a gap analysis. A gap analysis for a PDSR is the assessment of the state of technical knowledge, standards and regulations regarding safety functions of structures, systems and components. T2 - PSAM 12 - Probabilistic safety assessment and management CY - Honolulu, Hawaii, USA DA - 22.06.2014 KW - Dual Purpose Casks KW - Aging KW - Transportation KW - Periodical Review PY - 2014 UR - http://psam12.org/proceedings/paper/paper_259_1.pdf SP - Paper 259, 1 EP - 9 AN - OPUS4-32574 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zur, Malte A1 - Otremba, Frank T1 - Numerical simulation and experimental study of cabin-airflow and mass transport of dangerous goods in aircraft cargo compartments N2 - Using plastic jerrycans or plastic containers, dangerous goods are transported as air freight in commercial aircrafts. Liquids or gases can escape by leakage or permeation effects from these plastic containers. The German Federal Institute for Materials Research and Testing (BAM) conducted prior research which showed that the lower explosion limit can be reached when transporting dangerous goods in sea-freight containers under normal transportation situations. The presented study is motivated based on these findings. The research objective of this study is to analyze the transportation situation of dangerous goods in cargo compartments of commercial airplanes. The scope of this paper is to present the experimental method used for validating a numerical model for CFD (Computational Fluid Dynamics) simulations and to present some simulation results of the mass transport of dangerous goods in the cargo compartment. The velocity profiles and the mass transport is calculated using numerical simulations and measured by Laser-Doppler-Anemometry (LDA) experiments. The mock-up is a generic model of a wide-body aircraft lower deck cargo compartment in a 1: 10 scale. Geometry, air exchange rates and inlet as well as outlet flow conditions in the cargo compartment are modeled using realistic boundary conditions. The commercial CFD (Computational Fluid Dynamics) code ANSYS CFX 14 is used for numerical flow simulations applying RANS (Reynolds-Averaged-Navier-Stokes) equations and turbulence models. The turbulence models studied are the renormalization group k-e-model (RNG), the BSL-Reynolds-Stress model (BSL) and the SST-k-co-model by Menter (SST). The flow measurement with LDA in the mock-up of a cargo compartment proves to be a feasible method for producing data to validate CFD simulations. Qualitative evaluation of the results shows a good overall agreement between numerical and experimental results. The experimental validation indicates that the implemented CFD model is capable of reproducing the flow situation in the model mock-up T2 - ICCEE 2015 - International conference on civil engineering and environmental engineering CY - Tokyo, Japan DA - 03.02.2015 PY - 2015 SP - 1 EP - 8 AN - OPUS4-32585 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Mohrbacher, H. ED - Gyekenyesi, A. ED - Halbig, M. T1 - Tribological background for the use of niobium carbide (NBC) as cutting tools and for wear resistant tribosystems N2 - The tribological profile of rotating disks made of binder-less niobium carbide (hot-pressed NbC) and cobalt-bonded NbC (NbC-8Co) mated against alumina (99.7%) were determined under unidirectional sliding tests (0.1 m/s to 8.0 m/s; 22°C and 400°C) as well as in oscillation tests (f= 20 Hz, Δx= 0.2 mm, 2/50/98% rel. humidity, n= 105/106 cycles) under un-lubricated (dry) conditions. In addition, the microstructure and mechanical properties of NbC and NbC bonded with 8% cobalt were determined as well. The tribological data obtained were benchmarked with different ceramics, cermets, hard metals and thermally sprayed coatings, where the NbC-8Co presented above 7 m/s the lowest wear rates so far in such a bench mark. NbC and NbC-8Co exhibited low wear rates under dry sliding associated with P·V high load carrying capacity. The tribological profile established revealed a strong position of NbC bearing materials under tribological considerations and for closed tribo-systems against traditional references. T2 - 38th International conference on advanced ceramics and composites CY - Daytona Beach, FL, USA DA - 26.01.2014 KW - Sliding friction KW - Wear KW - Ceramic KW - Oscillation KW - Coating KW - NbC KW - Niobium carbide KW - Cobalt KW - Hard metal PY - 2014 SP - Paper 1 EP - Paper 21 AN - OPUS4-32561 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Häßler, Dustin A1 - Hothan, Sascha T1 - Prüfmethodik für reaktive Brandschutzsysteme auf Stahlzuggliedern mit kreisrundem Vollquerschnitt N2 - An der BAM Bundesanstalt für Materialforschung und -prüfung werden Brandversuche an axial belasteten und unbelasteten Zuggliedern mit reaktiver Brandschutzbeschichtung durchgeführt. Neben den für Zugglieder typischen Kreisvollprofilen ist auch ein Kreishohlprofi! untersucht worden. In dieser Veröffentlichung werden Versuchsaufbau und -durchführung sowie die Ergebnisse der bisher durchgeführten Brandversuche vorgestellt. Die bisherigen Brandprüfungen zeigen, dass grundsätzlich eine Anwendung eines herkömmlichen reaktiven Brandschutzsystems auf kreisrunden Stahlprofilen möglich ist. Jedoch ergeben sich aufgrund des gekrümmten Querschnittes Besonderheiten, welche bei der Prüfung dieser Systeme und deren späteren Anwendung zu berücksichtigen sind. Unter anderem ist besonders bei kleinen Trockenschichtdicken mit einer ausgeprägten Längsrissbildung im aufgeschäumten Brandschutzsystem zu rechnen, welche die thermische Schutzwirkung des Systems erheblich beeinträchtigt. Neben Rissen in Längsrichtung treten auch Querrisse im Brandschutzsystem auf. Anhand der Versuche zeigt sich, dass die aufgebrachte mechanische Zugbelastung die Rissbildung begünstigt. Das Versagen der belasteten Zugglieder ereignet sich meist in der Nähe der gemessen maximalen Stahltemperatur und kündigt sich durch eine Zunahme und Vergrößerung der Querrisse an. Im Allgemeinen führt eine Erhöhung der Trockenschichtdicke bzw. eine Reduzierung des Lastausnutzungsgrades zu einer Verbesserung des Feuerwiderstandes. Ein Unterschied in den Temperaturverläufen von belasteten und unbelasteten Versuchskörpern ist besonders bei geringen Schichtdicken zu beobachten. T2 - 19. DASt-Forschungskolloquium CY - Hannover, Germany DA - 27.10.2014 KW - Stahlbau KW - Reaktive Brandschutzsysteme KW - Brandschutz KW - Zugglieder PY - 2014 SP - 1 EP - 6 AN - OPUS4-31885 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mellmann, Günter T1 - Erfahrungen mit Ultraschall-Laufzeitmessungen am Bauwerk aus Beton T2 - 2. Europäische Tagung für Zerstörungsfreie Prüfung CY - Wien DA - 1981-09-14 PY - 1981 SP - J-17/375-J-17/377 CY - Wien AN - OPUS4-31783 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Niesel, Konrad T1 - Critères pour le comportement à l'altération de pierres en oeuvre, compte tenu d'une sélection de valeurs caractéristiques PY - 1981 IS - 2 SP - 6 EP - 14 AN - OPUS4-31785 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niesel, Konrad ED - Rossi-Manaresi, R. T1 - Durability of porous building stone - importance of judgement criteria related to its structure T2 - International Symposium on Conservation of Stone II CY - Bologna DA - 1981-10-27 PY - 1981 N1 - Serientitel: Rapporti della Soprintendenza per i Beni Artistici e Storici per le Province di Bologna, Ferrara, Forli e Ravenna – Series title: Rapporti della Soprintendenza per i Beni Artistici e Storici per le Province di Bologna, Ferrara, Forli e Ravenna IS - 31 SP - 47 EP - 57 CY - Bologna AN - OPUS4-31797 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gierloff, M. T1 - Resin Dispersion modified Concretes under Traffic Simulation in the Federal Institute for Testing Materials, Berlin T2 - 3rd International Congress on Polymers in Concrete CY - Koriyama DA - 1981-05-13 PY - 1981 VL - 1 SP - 288 EP - 308 CY - Koriyama AN - OPUS4-31777 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaenicke, B. T1 - Gestaltfestigkeit als Bauteileigenschaft T2 - DVM Kolloquium "Werkstoffermüdung und Bauteilfestigkeit" CY - Berlin, Germany DA - 1981-09-25 PY - 1981 SP - 145 EP - 191 CY - Berlin AN - OPUS4-31695 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Isecke, Bernd T1 - The influence of constructional and manufacturing conditions of prestressed steels before mortar injection T2 - Symposium on Stress Corrosion of Prestressing Steel CY - Madrid, Spain DA - 1981-09-22 PY - 1981 SP - 80 EP - 94 CY - Madrid AN - OPUS4-31701 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Isecke, Bernd T1 - Failure analysis of the collapse of the Berlin congress hall T2 - Symposium on Stress Corrosion of Prestressing Steel CY - Madrid, Spain DA - 1981-09-22 PY - 1981 SP - 6 EP - 16 CY - Madrid AN - OPUS4-31702 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krafka, H. A1 - Wobst, Klaus A1 - Ziebs, Josef A1 - Aurich, Dietmar T1 - The influence of specimen geometry on fracture of unwelded and welded steel specimens - comparison of experimental results with FEM-Calculation T2 - 5th international conference on fracture CY - Cannes, France DA - 1981-03-29 PY - 1981 N1 - Serientitel: Advances in fracture research – Series title: Advances in fracture research IS - 5 PB - Pergamon CY - Oxford AN - OPUS4-31679 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rücker, Werner T1 - Auswirkung einzelner Parameter auf die Ausbreitung von U-Bahnerschütterungen T2 - Baugrundtagung CY - Mainz, Germany DA - 1981-01-01 PY - 1981 SP - 79 EP - 103 AN - OPUS4-31800 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niesel, Konrad T1 - Verwitterungsverhalten von Bauwerken und Skulpturen in städtischer Atmosphäre T2 - bautec Fachschau '81 - Altbau, Neubau, Stadtbau CY - Berlin DA - 1981-10-27 PY - 1981 VL - 81 SP - 1 EP - 4 CY - Berlin AN - OPUS4-31801 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Dietrich T1 - Untersuchung von Stützwänden und Überführungsbauwerken der Bundesautobahn Berlin T2 - bautec Fachschau '81 - Altbau, Neubau, Stadtbau CY - Berlin DA - 1981-10-27 PY - 1981 SP - 1 EP - 4 CY - Berlin AN - OPUS4-31806 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böttcher, Bernhard T1 - Infrarotthermographie im Bauwesen T2 - 2. Europäische Tagung für Zerstörungsfreie Prüfung CY - Wien DA - 1981-09-14 PY - 1981 SP - 104-105 Beitrag C-10 CY - Wien AN - OPUS4-31814 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schickert, Gerald T1 - Schallemission von Betonprobekörpern T2 - 2. Europäische Tagung für Zerstörungsfreie Prüfung CY - Wien DA - 1981-09-14 PY - 1981 SP - 218-220 Beitrag F-0 CY - Wien AN - OPUS4-31818 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schickert, Gerald T1 - Results of test concerning combined non-destructive testing of concrete T2 - 2. Europäische Tagung für Zerstörungsfreie Prüfung CY - Wien DA - 1981-09-14 PY - 1981 SP - 378 EP - 380 CY - Wien AN - OPUS4-31819 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Becker, Gerhard Wilhelm T1 - Technischer Fortschritt - An allem schuld PY - 1981 SP - 20 EP - 21 PB - Dt. Inst.-Verl. CY - Köln AN - OPUS4-31650 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Becker, Gerhard Wilhelm T1 - Einführungsreferat T2 - Konferenz Normenpraxis CY - Berlin, Germany DA - 1981-07-02 PY - 1981 SP - 3 EP - 5 PB - Beuth CY - Berlin AN - OPUS4-31659 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Trubiroha, Peter T1 - Künstliche und natürliche Bewitterung von Kunststoffen T2 - Wehrtechnisches Symposium AT 2 CY - Erding, Germany DA - 1981-05-25 PY - 1981 SP - 09.01 EP - 09.13 PB - Akad. Verl. CY - Mannheim AN - OPUS4-31821 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Aurich, Dietmar A1 - Brocks, Wolfgang A1 - Noack, Hans-Dieter A1 - Veith, Helmut T1 - Elastisch-plastische FEM-Analyse eines Innenkantenrisses und Erörtung der Ergebnisse mit einigen Bruchmechanik-Konzepten T2 - MPA Seminar CY - Stuttgart, Germany DA - 1981-10-08 PY - 1981 IS - 7 SP - 1 EP - 28 CY - Stuttgart AN - OPUS4-31662 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilke, Olaf A1 - Pech, Anja A1 - Mull, Birte A1 - Horn, Wolfgang A1 - Jann, Oliver T1 - Determination of methanol and ethanol in test chamber air by using TDS-GC-FID N2 - A method for the determination of very volatile organic compounds (VVOC) in air was developed and successfully tested for methanol and ethanol. Carbotrap 300 (R) (a multi-bed tube using Carbopack C (R), Carbopack B (R) and Carbosive SIII (R)) was selected as sorption material for thermal desorption and tested for its suitability for emission test chamber measurements. The adsorption behaviour and the chromatographic results are influenced negatively by spiking aqueous solutions on the adsorption medium for calibration purposes. The latter effect can be reduced by blowing dry air across the adsorbent to remove the adsorbed water. Detection and quantification limits were determined for a GC-FID system and compared to GC-MS. The applicability of the method was tested with a methanol eliminating silane modified polymeric adhesive (SMP-adhesive for parquet) in an emission test chamber. T2 - Indoor Air 2014 - 13th International conference on indoor air quality and climate CY - Hong Kong, People's Republic of China DA - 07.07.2014 KW - Methanol KW - Ethanol KW - VVOC KW - Thermal desorption KW - Carbotrap 300 PY - 2014 SP - B6-HP0620, 1-2 AN - OPUS4-32323 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hinchliffe, Daniel A1 - Akkerman, Floris A1 - Nitsche, Michael T1 - Are preparatory studies flexible enough for the ecodesign directive? Regulation challenges in complex product groups N2 - In this study the processes driving the EU Ecodesign Directive's preparatory studies forward are summarised and issues occurring in recent product groups are reviewed. As product groups move away from standard mass-produced products, finding ways to bring them under the scope of the Ecodesign Directive becomes more controversial and complex. Through literature review, challenges facing study consultants are outlined and their specific impacts are demonstrated through outline case studies of the fans, industrial ovens, machine tools and thermal insulation product groups. Inconsistencies in the process are found where possible and matched up to the historical process to determine whether preparatory studies could be made more effective or should be more flexible, given the limited resources available at the European Commission and amongst Member States. A number of recommendations for improving the regulation process and the structure of the preparatory study are presented, based upon literature review and the presented analysis. PY - 2014 SP - 1 EP - 39 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-32167 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ewert, Uwe A1 - Zscherpel, Uwe T1 - Minimum requirements for digital radiography equipment and measurement procedures by different industries and standard organizations N2 - The digital photography has almost completely substituted the film photography. The film replacement is also fast progressing in medical X-ray radiography. This process is slower in NDT and especially in Europe. Reasons for the hesitating change to digital radiography (RT-D) in NDT are the necessary time for adoption of standards and the conservative request for film RT by auditors and NDT managers for applications in large plants and at construction areas. The fast serial inspection for small castings is already almost completely dominated by RT-D due to the cost effective short exposure and interpretation times. Standards were developed in parallel at CEN, ISO, ASTM and ASME. Unfortunately, the standard practices are different and the requirements on image quality and useable hardware are different too. The first standard series on Computed Radiography were developed and published by CEN and ASTM in 2005. Harmonized classification and qualification standards are available but the published practices are different. ASTM has developed the first standards for application of Digital Detector Arrays (DDA) in 2010. The first digital RT ISO standard practice is ISO 17636-2 (2013), which describes the practice for application of DDAs and Imaging Plates for weld inspection. At the first time this standard provides requirements for the selection of suitable hardware. Minimum image quality requirements are specified in analogy to film radiography and 3 Compensation Principles are defined to enable the application of a wider range of digital detectors. A comparison of the different international digital RT standards is given and first experiences with ISO 17636-2 are discussed. New standards on RT wall thickness and corrosion measurements (EN 16407, film and digital) have been developed recently. T2 - ECNDT 2014 - 11th European conference on non-destructive testing CY - Prague, Czech Republic DA - 06.10.2014 KW - NDT KW - X-Ray KW - Digital detectors KW - Standards KW - Radiographic procedures KW - Unsharpness KW - Basic spatial resolution KW - Requirements KW - Digital industrial radiology PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-323081 UR - https://www.ndt.net/?id=16708 SN - 1435-4934 VL - 19 IS - 12 SP - 1 EP - 18 PB - NDT.net CY - Kirchwald AN - OPUS4-32308 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sklorz, Christian A1 - Otremba, Frank A1 - Reich, Franziska T1 - Limit load analysis of pressurized containers N2 - Limit load analysis is a well known method to calculate the allowable design pressure of container components. A limit load of a pressurized container is achieved, when the stress of a wall and the flow stress are equal. In the following paper the transferability of limit load analysis from small scale tank containers up to large scale containers (railway tank) are investigated. Finite element calculations are carried out and compared with experimental results. It can be concluded that the limit load analysis works very well. Furthermore, the yield strength of the material should be used as flow stress. T2 - IMECE 2014 - ASME International mechanical engineering congress and exposition CY - Montreal, Quebec, Canada DA - 14.11.2014 PY - 2014 SN - 978-0-7918-4958-3 SP - Paper 36334, 1 EP - 5 AN - OPUS4-32316 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Iancu, O.T. A1 - Otremba, Frank A1 - Sklorz, Christian T1 - Comparison between analytical and finite element calculation for pressurized container N2 - The prediction of the plastic collapse load of cylindrical pressure vessels is very often made by using expensive Finite Element Computations. The calculation of the collapse load requires an elastic-plastic material model and the consideration of non-linear geometry effects. The plastic collapse load causes overalls structural instability and cannot be determined directly from a finite element analysis. The ASME (2007) code recommends that the collapse load should be the load for which the numerical solution does not converge. This load can be only determined approximately if a expensive nonlinear analysis consisting of a very large number of sub steps is done. The last load sub step leading to a convergent solution will be taken as the critical load for the structure. In the instability regime no standard finite element solution can be found because of the lack of convergence of the numerical procedure. Other methods for the calculation of the allowable pressure proposed by the ASME code are the elastic stress analysis and the limit load analysis. In the present paper the plastic collapse load for a cylindrical pressure vessel is determined by an analytical method based on a linear elastic perfectly plastic material model. When plasticity occurs the material is considered as incompressible and the tensor of plastic strains is parallel to the stress deviator tensor. In that case the finite stress-strain relationships of Henkel can be used for calculating the pressure for which plastic flow occurs at the inside of the vessel wall or in the case of full plasticity in the wall. The analytical results are fully confirmed by finite element predictions both for axisymmetric and high costs three dimensional models. The analytical model can be used for fast predictions of the allowable load for the design of a large variety of pressure vessels under safety considerations. The accuracy of the predicted collapse load largely depends on the quality of the temperature dependent wall material data used both in the analytical and numerical calculations. T2 - IMECE 2014 - ASME International mechanical engineering congress and exposition CY - Montreal, Quebec, Canada DA - 14.11.2014 PY - 2014 SN - 978-0-7918-4958-3 SP - Paper 36106, 1 EP - 5 PB - Amer soc mechanical engineers CY - New York, NY, USA AN - OPUS4-32317 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Czepluch, Wolf T1 - Experimentelle Abspaltung des binokularen Glanzes T2 - 4th congress of the International Colour Association CY - Berlin, Germany DA - 1981-09-21 PY - 1981 SP - 1 EP - 3 CY - Berlin AN - OPUS4-32292 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Döring, Günter T1 - Die Farbsysteme DIN 6164, ACC (Acoat Color Codification) und NCS (Natural Color System) PY - 1981 IS - 19 SP - 40 EP - 48 PB - Verl. Farbe + Design CY - Gaildorf AN - OPUS4-32294 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gundlach, Dietrich T1 - Farbmessung an metallischen Oberflächen T2 - 4th congress of the International Colour Association CY - Berlin, Germany DA - 1981-09-21 PY - 1981 SP - 1 EP - 4 CY - Berlin AN - OPUS4-32295 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heinrich, Hans-Joachim T1 - Farbmetrische Festlegung von Druckfarbenreihen T2 - 4th congress of the International Colour Association CY - Berlin, Germany DA - 1981-09-21 PY - 1981 SP - 1 EP - 3 CY - Berlin AN - OPUS4-32296 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rahammer, M. A1 - Myrach, Philipp A1 - Maierhofer, Christiane A1 - Busse, G. A1 - Kreutzbruck, M. T1 - Auflösungsgrenzen der Lockin-Thermografie zur Prüfung von Faserkunststoffverbunden N2 - Aktive Thermografie mit Lockin-Anregung ist ein zerstörungsfreies Prüfverfahren, das insbesondere auch die Prüfung von kohlenstofffaserverstärkten Kunststoffen ermöglicht. Um eine Standardisierung dieses Verfahrens voranzubringen, wurden im Rahmen eines Forschungsprojektes umfangreiche Untersuchungen zur Validierung des Verfahrens durchgeführt. Für die Anregungsmethoden optisch und Ultraschall wurden die wichtigsten Parameter systematisch untersucht. Auf der Auswertungsseite ist dies z.B. der Einfluss der spektralen Empfindlichkeit verschiedener Kamerasysteme. Für die Anregungen sind unter anderem die Einflüsse von Anregungsenergie und Ultraschallfrequenz untersucht worden. Auch Materialparameter, wie der Lagenaufbau bei CFK-Probekörpern, beeinflussen die Ergebnisse stark. T2 - 24. Stuttgarter Kunststoffkolloquium CY - Stuttgart, Germany DA - 25.02.2015 KW - Zerstörungsfreie Prüfung KW - Lockin-Thermografie KW - Faserkunststoffverbunde KW - Non-destructive testing KW - Lockin-Thermography KW - Fibre-reinforced plastics PY - 2015 SP - 1 EP - 7 AN - OPUS4-32876 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Heinrich, Hans-Joachim T1 - Farbmetrische Festlegung von Farbreihen im Mehrfarbendruck und Druck eines Farbspektrums PY - 1981 IS - 19 SP - 32 EP - 39 PB - Verl. Farbe + Design CY - Gaildorf AN - OPUS4-33288 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Richter, Klaus T1 - Bewertung und Kennzeichnung der Farbwiedergabe von Farbfilmmaterialien bei Variation von Aufnahmelichtart, Belichtung, Projektionsleuchtdichte und Bezugslichtart T2 - 4th congress of the International Colour Association CY - Berlin, Germany DA - 1981-09-21 PY - 1981 SP - 1 EP - 4 CY - Berlin AN - OPUS4-33289 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Terstiege, Heinz T1 - Rationalisierung der Farbgebung durch Anwendung der DIN-Farbenkette PY - 1980 N1 - Serientitel: Schriftenreihe Landes- und Stadtentwicklungsforschung des Landes Nordrhein-Westfalen – Series title: Schriftenreihe Landes- und Stadtentwicklungsforschung des Landes Nordrhein-Westfalen IS - 3/28 SP - 104 EP - 109 CY - Dortmund AN - OPUS4-33290 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Terstiege, Heinz T1 - Farbmessung T2 - 4th congress of the International Colour Association CY - Berlin, Germany DA - 1981-09-21 PY - 1981 SP - ? (9 S.) CY - Berlin AN - OPUS4-33291 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Witt, Klaus T1 - Das OSA/UCS-Farbsystem aus der Sicht von DIN 6164 PY - 2015 IS - 19 SP - 49 EP - 52 PB - Verl. Farbe + Design CY - Gaildorf AN - OPUS4-33292 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wüstenberg, Hermann A1 - Erhard, Anton A1 - Möller, G. T1 - Erläuterungen zum Einsatz der akustischen Holographie in der zerstörungsfreien Werkstoffprüfung mit Ultraschall T2 - 4. Internationale Konferenz über Zerstörungsfreie Prüfung in der Kerntechnik CY - Lindau, Germany DA - 1981-05-25 PY - 1981 N1 - Serientitel: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. – Series title: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. IS - 8 SP - 1 EP - 13 PB - DGZfP CY - Berlin AN - OPUS4-33334 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Mike A1 - Zencker, Uwe A1 - Wolff, Dietmar A1 - Völzke, Holger A1 - Herbrich, Uwe A1 - Nagelschmidt, Sven T1 - Numerical analysis of cask accident scenarios in storage facilities N2 - Existing spent nuclear fuel (SF) and high active waste (HAW) management policies and practices worldwide are the result of past presumptions that sufficient reprocessing and/or disposal capacity would be available in the near term. Consequently, in the past many countries have developed specific solutions for different periods of time due to their individual national nuclear policies. In Germany the concept of dry interim storage in dual purpose metal casks before disposal is being pursued for SF and HAW management and transport and storage licenses have been issued accordingly. The current operation licenses for existing storage facilities have been granted for a storage period of up to 40 years. This concept has demonstrated its suitability for over 20 years so far. Relevant safety requirements have been assessed for the short-term as well as for the long-term for site-specific operational and accidental storage conditions. But in the meantime significant delays in the national repository siting procedure occurred which will make extended storage periods necessary in the future. T2 - PATRAM 2013 - 17th International symposium on the packaging and transportation of radioactive materials CY - San Francisco, CA, USA DA - 18.08.2013 KW - Numerical analysis KW - Interim storage KW - Cask accident scenario PY - 2013 SP - Session H, Paper 202, 1 EP - 9 PB - Omnipress AN - OPUS4-30227 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Walter, Astrid T1 - Herstellung und Charakterisierung von Antikörpern gegen Triacetontriperoxid (TATP) N2 - Die vorliegende Arbeit beschreibt die Herstellung und Charakterisierung der ers-ten Antikörper gegen Triacetontriperoxid (TATP), einem hoch empfindlichen und unkonventionellen (nicht-kommerziellen) Initialsprengstoff. Entscheidend dafür war die Synthese eines TATP-imitierenden Haptens, welches die typische nona-gonale Struktur des TATP mit seinen drei Peroxid- und sechs Methylgruppen nahezu perfekt nachbildet, aber den Vorzug einer zusätzlichen Carboxygruppe zur kovalenten Kopplung an Proteine aufweist. Dadurch konnte das TATP-Hapten an Rinderserumalbumin (BSA) gebunden werden, um ein immunogenes Konjugat zu erzeugen, welches die erfolgreiche Immunisierung zweier Säuge-tierarten, Maus und Kaninchen, ermöglichte. Der Verlauf der In-vivo-Immunisierungen wurde durch die Analyse der Tier-seren in regelmäßigen Abständen mittels enzymgekoppeltem Immunoassay (ELISA) verfolgt. Die polyklonalen Antikörper beider Spezies waren ungewöhnlich selektiv gegenüber TATP. Jedoch unterschied sich die Affinität der Antikörper der zwei Spezies um das 5 000-fache, wobei die Kaninchenseren den Mausseren überlegen waren. Entsprechend war auch die mit Kaninchenserum erreichbare TATP-Nachweisgrenze von 0.01 μg L-1 deutlich besser im Vergleich zu 50 μg L-1, die mit Mausserum erzielt wurden. Der Messbereich des TATP-ELISA mit Kanin-chenserum deckte zudem mehr als vier Zehnerpotenzen ab, wie mittels Präzisi-onsprofil bestimmt wurde. Die erhaltenen TATP-Antikörper aus Kaninchen stehen damit Anwendungen in Nachweissystemen für die sehr empfindliche Detektion von TATP zur Verfügung, die u. a. in sicherheitsrelevanten Bereichen zum Einsatz kommen könnten. Als erste Anwendung wurde ein TATP-ELISA realisiert, der im Rahmen dieser Arbeit ausführlich optimiert wurde. Außerdem wurden erste Schritte zur Entwicklung eines TATP-Schnelltests (LFA) unternommen. Weitere Biosensoren auf Grundla-ge der neu entwickelten TATP-Antikörper sind denkbar. KW - Terrorismus KW - ELISA KW - Immunisierung KW - Immunoassay KW - Hapten-Immunoassay KW - Maus-Immunisierung KW - Kaninchen-Immunisierung KW - Hapten-Design KW - TATP KW - Triacetontriperoxid KW - Acetonperoxid KW - APEX KW - Peroxid-basierte Explosivstoffe KW - Organische Peroxide KW - HME KW - Biosensorentwicklung KW - Terrorism KW - Antibody KW - Immunization KW - Mouse immunization KW - Rabbit immunization KW - Hapten design KW - Hapten immunoassay KW - Triacetone triperoxide KW - Acetone peroxide KW - Peroxide based explosives KW - Organic peroxides KW - Biosensor development PY - 2014 SP - 1 EP - 181 CY - Berlin AN - OPUS4-30230 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scheidemann, Robert A1 - Kasparek, Eva Maria A1 - Müller, Karsten A1 - Droste, Bernhard A1 - Völzke, Holger T1 - Model-sized and full-scale dynamic penetration tests on damping concrete N2 - Mechanical loading conditions of transport and storage casks for radioactive materials in accidental scenarios are highly affected by the behavior of both: the impact limiters and the footing materials. To minimize potential damages during the handling of casks, a so called damping concrete is frequently used for the footings in interim nuclear facilities. It obtains its shock absorbing properties through admixing of polymer cells. For a comprehensive mechanical evaluation of casks, advanced material models are also needed for damping concrete. In order to characterize the mechanical properties and to develop numerical material models, penetration tests were carried out at different test facilities of BAM. The tests contain static and dynamic penetration tests on cubic specimen with an edge length of 100 mm as well as mortared specimen with a size of 240 x 240 x 50 cm³. Indenters with different geometries and diameters were used for these model-sized penetration tests. Subsequently a full-scale cylindrical cast-iron indenter with a diameter of 110 cm was dropped of 5 m height on a realistic damping concrete footing. T2 - PATRAM 2013 - 17th International symposium on the packaging and transportation of radioactive materials CY - San Francisco, CA, USA DA - 18.08.2013 KW - Drop test KW - Dynamic KW - Penetration KW - Damping concrete PY - 2013 SP - 1 EP - 10 PB - Omnipress AN - OPUS4-30233 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Botsch, W. A1 - Smalian, S. A1 - Hinterding, P. A1 - Völzke, Holger A1 - Wolff, Dietmar A1 - Kasparek, Eva Maria T1 - Dual purpose cask safety evaluation - Expertise in dry storage N2 - In Germany dual purpose casks for spent nuclear fuel (SF) or high level radioactive waste (HLW) are used for safe transportation and interim storage. Key safety issues in both fields are the safe enclosure of the radioactive material, the safe removal of decay heat, securing nuclear criticality safety, limitation of radiation exposure to acceptable levels and keeping it as low as reasonable achievable (ALARA principle). Whereas these safety requirements during transportation are ensured by the Type-B(U)-design testing and approval procedure on basis of internationally agreed IAEA (International Atomic Energy Agency) requirements storage licenses are issued on national and site specific safety analyses. This paper presents experiences from recent interim storage safety evaluation and licensing procedures in Germany on basis of a Type-B(U) certified cask designs concerning specific differences from Operation and accident conditions inside the storage facility. The focus is laid on the interaction of cask and building structures with regard to shielding, heat removal and accident analyses including aircraft crash. Basic safety is assured by thick-walled metal casks with monitored double lid Systems. They also reduce radiation to levels where workers can safely operate and maintain the casks inside the storage facility. The storage building e. g. provides additional shielding and protection against extemal hazards depending on the building construction. In addition, the storage building helps to reduce radiation levels at the boundary of the storage site well below regulatory limits given by the German Radiation Protection Ordinance (StrSchV). T2 - PATRAM 2013 - 17th International symposium on the packaging and transportation of radioactive materials CY - San Francisco, CA, USA DA - 18.08.2013 KW - Dual purpose cask KW - Long-term storage PY - 2013 SP - 1 EP - 8 PB - Omnipress AN - OPUS4-30235 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lazik, D. A1 - Ebert, Sebastian A1 - Neumann, Patrick P. A1 - Bartholmai, Matthias T1 - Pipeline monitoring with linear gas sensors N2 - Comprehensive monitoring of pipelines over their full length is technically difficult and expensive. Considering a cost-benefit ratio it is reasonable to implement monitoring solutions in pipeline segments, which bear a high risk potential, like residential areas, construction sites, slopes, street or river crossings. Still such segments can measure up to several hundred meters in length, demanding for monitoring solutions that extend along such distances and enable fast response. Point wise sensing and periodical surveillance have clear drawbacks, particularly regarding early damage detection. Fibre optic sensors enable distributed sensing of temperature and strain, but they offer very limited possibilities for measuring gas concentrations. Linear membrane-based gas sensors enable the monitoring of gas concentrations alongside a pipeline. Such line-sensors are implemented in form of flexible tubes and can be arranged inside or outside the pipeline (also underwater or within the subsurface), corresponding to the technical requirements. The measuring method combines the gas specific diffusion rates through a membrane with Dalton’s law of partial pressures and enables the calculation of gas concentrations or the detection of a change of the gas composition. The objective is to detect gas leakages fast and with high reliability. Furthermore, the calibrated system enables to estimate the spatial extent of a leakage. So far the gas concentration measurement is tested for oxygen, carbon dioxide, methane; further gases should follow, e.g. hydrogen, carbon monoxide or mixtures like natural gas. The paper introduces in the different operating modes of line-sensors. A near real-time approach will be demonstrated to quantify the impact of a gas leak on the near environment. This approach is based on a critical length describing the expansion of the leaking gas. T2 - 9th Pipeline technology conference 2014 CY - Berlin, Germany DA - 12.05.2014 KW - Multi-sensor system KW - Condition monitoring KW - Safety management KW - Hazardous scenarios KW - Data fusion PY - 2014 SP - 1 EP - 9 AN - OPUS4-30727 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pospiech, D. A1 - Fischer, O. A1 - Korwitz, A. A1 - Hoffmann, T. A1 - Köppl, T. A1 - Altstädt, V. A1 - Ciesielski, M. A1 - Döring, M. A1 - Brehme, Sven A1 - Schartel, Bernhard A1 - Vollmerhausen, D. T1 - Designed flame retardancy with phosphorus polymers N2 - Polymeric flame retardants offer the possibility to match effective flame retardancy with the requirements of new regulations. Synthesis, properties and efficiency in polymer matrices are discussed for two systems, epoxy resins as well as poly(butylene terephthalate). T2 - 25th Annual conference: Recent advances in flame retardancy of polymeric materials CY - Stamford, Connecticut, USA DA - 18.05.2014 KW - Flame retardancy KW - Phosphorus polymer KW - Poly(butylene terephthalate) KW - Epoxy resin PY - 2014 SP - 1 EP - 5 AN - OPUS4-30951 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Seeger, Stefan A1 - Langner, Jeanette A1 - Nowak, D. A1 - Jörres, R.A. A1 - Karrasch, S. A1 - Ehret, M. A1 - Herbig, B. A1 - Schierl, R. T1 - Untersuchung möglicher gesundheitlicher Gefährdungen durch Drucker- und Kopierer-Emissionen KW - Bürogeräte KW - Laserdrucker KW - Partikelemission KW - Aerosol KW - Gesundheitliche Gefährdung KW - In-vivo-Studie PY - 2014 UR - http://www.dguv.de/Projektdatenbank/0294A/3228509v1.pdf SP - 1 EP - 238 CY - Berlin ET - Abschlussbericht der Projektpartner zum DGUV-Projekt (Kennziffer FP 294) AN - OPUS4-31335 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baier, Jennifa A1 - Hidde, Gundula A1 - Beck, Uwe T1 - Oberflächenaktivierung von Polymeren mittels O2-Plasma N2 - Zur Verbesserung der Verbundfestigkeit kann beim Kleben [1] oder Beschichten von Polymeren die Oberfläche mittels 02-Plasma gereinigt (Feinstreinigung) und aktiviert werden. Bei der Plasmaaktivierung werden sauerstoffhaltige funktionelle Gruppen auf der Oberfläche gebildet. Die Polymersubstrate wurden mit 02-Plasma behandelt, zum einen mit einem Plasmajet bei 200 W (PP, PA) und zum anderen mit einem Mikrowellenplasma bei 100 W (Folie: PE, PP, PS, PC, PET), mittels FTIR-Spektroskopie (p-ATR) charakterisiert sowie die Änderung der Oberflächenenergie mittels Kontaktwinkelmessung bestimmt. T2 - 10. ThGOT Thementage Grenz- und Oberflächentechnik mit 4. Optik-Kolloquium CY - Leipzig, Germany DA - 02.09.2014 KW - Plasma KW - Oberflächenaktivierung PY - 2014 SP - 1 EP - 2 AN - OPUS4-31337 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe ED - Baumgartner, J. ED - Melz, T. T1 - Assessment of welded joints by fracture mechanics IBESS - the development of a procedure N2 - The idea to determine the fatigue strength of weldments by means fracture mechanics was originally based on the empirical observation that the major portion of the fatigue life in weldments is frequently spent in crack propagation. The present paper gives a brief overview on the basic principles of fracture mechanics-based determination of fatigue strength and on special features which have to be considered for weldments. Based on this information, the ongoing research project IBESS is introduced and briefly reviewed. T2 - SoSDiD - 4th Symposium on structural durability in Darmstadt CY - Darmstadt, Germany DA - 2014-05-14 KW - Fracture mechanics KW - Fatigue strength KW - (Residual) lifetime KW - Weldments PY - 2014 SP - 49 EP - 66 PB - Fraunhofer Verlag AN - OPUS4-31321 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rühl, Karl H. T1 - Blechkonstruktionen - Beispiele und Gesichtspunkte PY - 1952 IS - 3 SP - 21 EP - 26 PB - Forschungsgesellschaft Blechverarbeitung CY - Düsseldorf AN - OPUS4-31328 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lange, Thorid A1 - Beck, Uwe A1 - Hielscher, Stefan A1 - Tsoviaki, Anna A1 - Lindner, E. T1 - OKTETT – Acht auf einen Streich: Verbundfestigkeit vs. Schälwiderstand von Klebebändern N2 - Zur Bewertung der Klebkraft von Klebebändern werden üblicherweise die Prüfungen zur Bestimmung des Schälwiderstandes (in N/25 mm) mit 90° bzw. 180° Abzugswinkel unter Verwendung einer Zugprüfmaschine (ZP) herangezogen, Für die hier gezeigten Beispiele wurde dabei eine V2A-Prüfplatte (Ra = 0,15 pm), ein Abzugswinkel von 90° und eine Abzugsgeschwindigkeit von 300 mm/min verwendet. Alternativ wurde der Versuch unternommen, die Klebkraft von Klebebändern durch die Prüfung der Verbundfestigkeit (in N/mm2) mittels Zentrifugen-Technologie (ZT) zu bestimmen. Dazu wurden beidseitig klebende Klebeband-Pads einer Abmessung von (10x10) mm2 zunächst auf V2A-Stahlsubstrate aufgebracht und anschließend dann auf diese modulare Prüfstempel (Klebfläche aus V2A, 0=10 mm; Massekörper aus Cu) aufgesetzt. In Abb. 1 sind Beispiele von Versagensformen, wie sie nach der Prüfung der Verbundfestigkeit mittels ZT auftreten können, dargestellt. T2 - 10. ThGOT Thementage Grenz- und Oberflächentechnik mit 4. Optik-Kolloquium CY - Leipzig, Germany DA - 02.09.2014 KW - Mehr-Proben-Kleb-Vorrichtung KW - Zentrifugen-Technologie KW - Schälwiderstand KW - Verbundfestigkeit PY - 2014 SP - P05, 1 EP - 2 AN - OPUS4-31312 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beck, Uwe A1 - Hielscher, Stefan A1 - Lange, Thorid A1 - Weise, Matthias A1 - Kittler-Packmor, Kai A1 - Rietz, U. A1 - Lerche, D. A1 - Pfuch, A. T1 - Mehr-Proben-Konzept zum Kleben und Prüfen: Validierung von Klebverbunden im OKTETT T2 - 10. ThGOT Thementage Grenz- und Oberflächentechnik mit 4. Optik-Kolloquium CY - Leipzig, Germany DA - 2014-09-02 KW - Zentrifugentechnologie KW - Klebfestigkeit KW - Haftfestigkeit KW - Mehr-Proben-Prüfen/Kleben PY - 2014 SP - BA04, 1 EP - 2 AN - OPUS4-31313 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Berchtold, Florian A1 - Forell, B. A1 - Krause, U. T1 - Probabilistic set of filter criteria in the frame of Fire PSA N2 - Filter criteria in the Frame of Fire PSA identify compartments in a first qualitative analysis for which the contribution to the overall core damage frequency of the NPP is negligible. The aim of the filter criteria is to reduce the number of compartments to be analysed precisely in Fire PSA. One example for filter criteria is the 'fire load criterion'. By the fire load criterion compartments with a fire load density of less than 90 MJ/m² are 'screened out' which means to exclude them from a precise analysis in Fire PSA. Neither the justification of the particular value of 90 MJ/m² is well documented nor does this criterion take into account varying compartment configurations such as ventilation conditions, physical and chemical properties of the fire load as well as compartment characteristics. A probabilistic set of filter criteria was developed to overcome the restrictions of the fire load criterion. In line with the 'fire load criterion', the probabilistic set of filter criteria assumes that a compartment can be screened out if a fire is not able to cause any damage to other components within the compartment. Therefore, the electrical failure of an electrical cable conservatively represents the damages of all components. It is assumed that the electrical cable failure occurs when the maximum cable temperature exceeds an experimentally determined failure temperature. The maximum cable temperature that can occur in a compartment fire is mainly influenced by the four significant factors: 1. inlet air stream of the mechanical ventilation, 2. the fire growth rate, 3. the compartment floor area and 4. the compartment height. A parameter study revealed how the significant factors affect the maximum cable temperature in fictitious compartment fires. The results of the parameter study are transferred on true Nuclear Power Plant compartments. However, it is not possible to determine precisely the occurrence of an electrical cable failure because of uncertainties in the maximum cable temperature and the failure temperature. The probabilistic set of filter criteria considers these uncertainties and determines the probability of cable failure for true compartments to be screened in Fire PSA. Finally, a compartment can be screened out in Fire PSA if the failure probability exceeds a predefined accepted threshold value for the failure probability. The theoretical application of the methodology is shown at the end of the paper. T2 - International workshop on fire PRA CY - Garching, Germany DA - 28.04.2014 PY - 2014 SP - Paper 1-3 EP - 1-15 AN - OPUS4-31316 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mull, Birte A1 - Wilke, Olaf T1 - Photocatalytical degradation of selected volatile organic compounds in emission test chambers N2 - This work focuses on the photocatalytical degradation of selected volatile organic compounds (toluene, butyl acetate, phenol and limonene) under UV-light and blue LED-light (λ = 444 nm) at different relative humidities. Ceramic tiles coated with titanium dioxide were used as photocatalytical active material. The experiments were performed in 20 l emission test chambers with two different kinds of pollutant supply. Toluene was the compound with the highest degradation rate in all performed experiments. A degradation rate of 24 % was obtained under blue LED-light and a relative humidity of (50 ± 5)% and a degradation rate up to 80 % was obtained under UV-light in dry air. T2 - Indoor Air 2014 - 13th International conference on indoor air quality and climate CY - Hongkong, China DA - 07.07.2014 KW - Photocatalysis KW - Titanium dioxide KW - Volatile organic compounds KW - Emission test chamber KW - UV-light PY - 2014 SP - HP0549, 1 EP - 5 AN - OPUS4-31364 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Damm, David A1 - Pinnow, C.J. A1 - Schulz-Forberg, Bernd T1 - Telematik und Gefahrgutsicherheit - Regeln, Gefahrgut - Telematik und Datensicherheit N2 - In einer arbeitsteiligen Wirtschaft erfüllt der Transport eine herausragende Scharnierfunktion. Von der Wirtschaftlichkeit, Zuverlässigkeit und Sicherheit des Transportes hängen vielfältige Arbeitsergebnisse in den unterschiedlichen Prozessen ab. Aus den Bedürfnissen der Wirtschaft ergibt sich i.d.R. ein sogenannter Modal-Split, der die Aufteilung der Wirtschaftsgüter auf die verschiedenen Verkehrsträger Straße, Schiene, Binnenschiff, See und Luft beschreibt. Zuverlässigkeitsangaben und auch Angaben zur Sicherheitslage lassen sich aus den Statistiken herleiten, wie sie z.B. für Deutschland (Statistisches Bundesamt) und Europa (Eurostat) vorliegen. Die Unfallzahlen sind relativ gering, insbesondere aber ist die Tendenz einer stetigen Verringerung der Ereignisse pro Transport zu erkennen. Der Transport gefährlicher Güter ist integrativer Teil des allgemeinen Gütertransportes und demzufolge erfolgen die Transporte mit Gefahrgut auf den gleichen Verkehrswegen ohne nennenswerte Sonderstellungen, abgesehen von Spezialfällen, wie Transporte für die Bundeswehr. Für die Transporte gefährlicher Güter gibt es spezielle Regelungen, die für die verkehrsträgerunabhängigen Bereiche einheitlich von den Vereinten Nationen ausgearbeitet und als sogenannte Modellvorschriften veröffentlicht werden. In einem Rhythmus von zwei Jahren werden diese Modellvorschriften der Vereinten Nationen dem Stand der Technik angepasst, sodass quasi kontinuierlich die Optimierung der Regelsetzung erfolgt. Man kann heute davon ausgehen, dass der materielle Inhalt der Regeln der Vereinten Nationen in den wichtigsten Wirtschaftsregionen der Welt in entsprechenden bindenden Regeln seinen Niederschlag gefunden hat, sodass von einem nahezu einheitlichen Regelwerk für den Transport gefährlicher Güter auf der ganzen Welt ausgegangen werden kann. KW - Gefahrgut KW - Sicherheit KW - Telematik KW - RFID KW - SIGRID PY - 2014 N1 - Serientitel: Gefahrgut für die Praxis – Series title: Gefahrgut für die Praxis SP - Sonderausgabe, 25 EP - 28 PB - Deutscher Bundes-Verlag AN - OPUS4-31536 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hothan, Sascha A1 - Häßler, Dustin T1 - Über die Entwicklung von Anwendungsregeln für reaktive Brandschutzsysteme auf Stahlzuggliedern N2 - Der vorliegende Beitrag stellt den Entwicklungsstand von Anwendungsregeln für reaktive Brandschutzsysteme auf Stahlzuggliedern zusammenfassend dar. Dabei wird insbesondere auf die jüngsten Veränderungen in den normativen Grundlagen und bauaufsichtlichen Regelungen eingegangen und im Hinblick auf Sicherheitsaspekte bewertet. Die Verringerung der Teilsicherheit für den Bauteilwiderstand nicht stabilitätsgefährdeter Bauteile im Regelwerk für die Kaltbemessung von Stahltragwerken ist hier als besonders kritisch anzusehen, da hierdurch ein systematisches Sicherheitsdefizit für den Brandfall verursacht wird. Weiterhin werden neuste Forschungsergebnisse bei der Entwicklung von Bewertungsregeln von reaktiven Brandschutzsystemen auf Vollkreisprofilen unter Zugbeanspruchung vorgestellt und diskutiert. Die Untersuchungen behandeln die Fragestellung, inwieweit Prüfungen mit Zugbeanspruchungen an Kreisvollprofilen erforderlich sein werden. KW - Stahlkonstruktion KW - Brandschutz KW - Reaktive Brandschutzsysteme KW - Zugglieder PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-307949 DO - https://doi.org/10.2314/GBV:77999762X SP - 141 EP - 148 PB - Institut für Stahlbau / Leibniz Universität Hannover CY - Hannover AN - OPUS4-30794 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Trela, Christiane A1 - Kind, Thomas A1 - Schubert, Marcus A1 - Klee, Martin ED - Lambot, S. ED - Giannopoulos, A. ED - Pajewski, L. ED - André, F. ED - Slob, E. ED - Craeye, C. T1 - Detection of weak scatterers in reinforced concrete structures N2 - GPR surveys on concrete structures like bridges, dccks and buildings are succcssfully applied to detect and localize construction elements mostly madc of metal. Dcfects like air voids behind rebars in incompletely compacted concrete still represent major challenges due to thcir weak reflcction amplitudes. In a systcmatic study at a concrete test specimen with vcrtical rebars and simulated air voids of different size and depth, the effects of different GPR data acquisition Parameters like antenna frcqucncies (1.2 up to 2.6 GHz) and antenna orientation on the quality of imaging of thcsc air voids wcre investigated. Vcry dense measurements with high Position accuracy were carried out using an automated scanning System. Despite the strong shadowing and disturbing interference effccts of the reinforccmcnt and the associated strong rcflections, the weak scatterers can still be identified to a ccrtain depth using appropriate antenna configurations. Measurements with the antenna orientation perpendicular to the rebars of 1.2 to 2.0 GHz give the best results. Pre- and postprocessing steps like filtering, gain, 3D SAFT (Synthetic Apcrture Focusing Technique) rcconstruction and somc adapted visualization options were properly applied to improve the imaging results of thcsc weak scatterers. T2 - GPR 2014 - 15th International conference on ground penetrating radar CY - Brussels, Belgium DA - 30.06.2014 KW - Radarmessungen KW - Automatisierung KW - Strukturerkennung KW - Stahlbeton KW - Reflection profiling KW - Data processing KW - SAFT reconstruction and visualisation of NDT-datasets PY - 2014 N1 - Geburtsname von Klee, Martin: Günther, M. - Birth name of Klee, Martin: Günther, M. SP - 904 EP - 910 AN - OPUS4-31168 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Trappe, Volker A1 - Ortwein, Hans-Peter A1 - Hickmann, Stefan T1 - Infinite life of CFRP evaluated nondestructively with X-ray-refraction topography N2 - CFRP are more and more used in modern civil aircrafts hence the whole fuselage is made of this material (B787; A350). Due to strict certification Standards finally the normal in-service loading gives a low stress level compared to the static and even the fatigue strength of the material. Hence CFRP are assumed to have an infinite life. To evaluate this assumption, fatigue tests on CFRP-specimens were performed up to 108 load cycles. The first inter-fiber failure was evaluated non-destructively by the fatigue tests accompanying X-ray-refraction topography altemately and in-situ mechanical loading. The basic idea of the investigation is represented in fig. 1. At low load levels it could not be assumed the total failure of the samples. Hence accompanying non-destructive testing (NDT) is mandatory to get information about the damage state of the material. T2 - ICCM19 - 19th International conference on composite materials CY - Montreal, Canada DA - 28.07.2013 KW - Carbon fibre reinforced plastics (CFRP) KW - Very high cycle fatigue (VHCF) KW - Non-destructive testing (NDT) KW - X-ray refraction KW - Damage mechanics PY - 2013 SP - 1 EP - 8 AN - OPUS4-31169 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kruschwitz, Sabine T1 - SIP responses of building materials, investigation of correlations with specific surface and dominant pore throat size N2 - Many damage processes in building stones are driven by moisture ingress and subsequent decay due to solving, blistering or different types of corrosion. Hence, measuring moisture and/or any material property that is connected to the absorption/desorption behaviour of a porous medium is helpful for building engineers concemed with Conservation or restoration. Since the SEP method is sensitive to both the amount and chemistry of a pore fluid and pore space properties ist applicability and practical use as a non-destructive testing tool for moisture damages is studied at BAM. T2 - 3rd International workshop on induced polarization CY - Ile d'Oléron, France DA - 06.04.2014 KW - Spectral induced polarization KW - Sandstone KW - Building material KW - Pore throat sizes PY - 2014 SP - 136 EP - 137 AN - OPUS4-31175 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Protz, Christian A1 - Zencker, Uwe A1 - Liebich, R. ED - Onate, E. ED - Oliver, J. ED - Huerta, A. T1 - Drop tests and dynamic finite element analyses of steel sheet containers for final disposal of radioactive waste N2 - Within a safety assessment, Containers for radioactive waste have to withstand drop tests at defined conditions. Alternatively to prototype drop tests, numerical methods can be applied, if they are suitable and sufficiently verified. This paper describes the development of a finite element (FE) model of a thin-walled Steel sheet Container used to investigate dynamic load scenarios due to impact events. Experimental and numerical analyses were performed for different drop Orientations. The results are compared to prove the suitability of the FE model. T2 - WCCM XI - 11th World congress on computational mechanics CY - Barcelona, Spain DA - 20.07.2014 KW - Explicit dynamic FEM KW - Impact KW - Drop test KW - Steel sheet container PY - 2014 SP - 1 EP - 12 AN - OPUS4-31137 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schneider, Thomas A1 - Gradt, Thomas A1 - Vierneusel, B. A1 - Tremmel, S. A1 - Wartzack, S. T1 - Tribological behavior of MoS2 in hydrogen environment N2 - The solid lubricant molybdenum disulfide is a well known material for extreme conditions where conventional oil or grease lubrication is not feasible (vacuum, high pressures). However, under reactive environments e.g. high humidity or hydrogen MoS2 is prone to premature failure. By using a PVD process, deposition parameters can be optimized to gain coatings with a more textured structure orienting the basal planes parallel to the Substrate surface, A similar concept has been used by Koch et al. for coatings developed to withstand the extreme operational conditions of the WENDELSTEIN W7-X fusion experiment. Therefore, an improved tribological behavior even under adverse conditions can be achieved. T2 - WTC 2013 - 5th World tribology congress CY - Torino, Italy DA - 08.09.2013 KW - Tribologie KW - Festschmierstoffe KW - MoS2 KW - Wasserstofftechnologie PY - 2013 SP - 1 EP - 3 AN - OPUS4-31156 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Bader, Mark Andreas A1 - Hübert, Thomas T1 - Hydrogen sensors for the safe and reliable use of hydrogen N2 - The use of hydrogen sensors can be categorized into three types of application: - Safety monitoring - Leak detection - Process control When applied in one of these areas hydrogen sensors fulfill the following tasks: - Indicate a hazardous condition - Provide warnings or alarms for out-of-limits conditions - Monitor and control System Operation - Provide performance data KW - Hydrogen sensor KW - Hydrogen safety PY - 2014 SP - 1 EP - 19 PB - BAM Federal Institute for Materials Research and Testing AN - OPUS4-31387 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Neumann, Patrick P. A1 - Bartholmai, Matthias T1 - Mikrodrohne zur Gasmessung in Gefahrenszenarien KW - Mikrodrohne KW - UAV KW - Gefahrenszenarien KW - Gasmessung KW - Windvektorbestimmung KW - Sensortechnik PY - 2014 SP - 1 EP - 21 PB - BAM Bundesanstalt für Materialforschung und -prüfung CY - Berlin ET - Abschlussbericht / BAM Vh 8144 AN - OPUS4-31425 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Köppe, Enrico A1 - Bartholmai, Matthias T1 - Funkbasiertes Sensornetzwerk zur Schadensfrüherkennung und Langzeit-Strukturüberwachung von Bauwerken und Infrastrukturen KW - Bauwerk KW - Technische Infrastruktur KW - Technische Überwachung KW - Schadenfrüherkennung KW - Sensortechnik PY - 2014 SP - 1 EP - 35 PB - BAM Bundesanstalt für Materialforschung und -prüfung CY - Berlin ET - Abschlussbericht / BAM Vh 8142 AN - OPUS4-31426 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Siebler, Daniel A1 - Lothongkam, Chaiyaporn A1 - Rohwetter, Philipp A1 - Habel, Wolfgang A1 - Heidmann, G. T1 - Fluorescent fiber optical partial discharge sensor in high-voltage cable facilities N2 - New sensors for the detection of partial discharges (PDs) in high-voltage (HV) cable accessories are being de-veloped consisting of a fluorescent polymer optical fiber (F-POF) as sensing element. Depending on the fiber material F-POFs can be attached to and even integrated into the translucent silicone rubber insulation of HV cable terminations. As the embedment into the insulation material plays an important role, the sensor should not weaken the dielectric strength of the insulation material and should not be the origin of PD incidents. A sensor consisting of a commercial F-POF has been tested in the high-voltage lab regarding its PD detection ability un-der AC in comparison to a conventional electrical sensor. New silicone rubber F-POF (Si-F-POF) fiber models functionalized with coumarin dyes have been produced. The optical properties of these dye functionalized silox-anes are presented. These potential sensor fibers are highly flexible and might be embeddable at medium to high-voltage level. An additional way to further improve the level of PD light detection is to modify the translucent type of silicone rubber used in HV cable accessories in terms of optical transparency. In this context we present our first results of the optical and mechanical properties of new elastomeric transparent silicone materials specif-ically designed for the application as HV insulation materials in stress cones. T2 - POF 2013 - 22nd International conference on plastic optical fibers CY - Búzios, Rio de Janeiro, Brazil DA - 11.09.2013 KW - Polymer optical fiber KW - Fluorescence sensor KW - Partial discharge monitoring KW - High-voltage power cable KW - Silicone rubber KW - Fluorescence dye KW - Nanoparticles PY - 2013 SP - 322 EP - 327 CY - Rio de Janeiro, Brazil AN - OPUS4-30266 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wolff, Dietmar A1 - Völzke, Holger A1 - Wille, Frank A1 - Droste, Bernhard T1 - Extended storage after long-term storage N2 - Existing spent nuclear fuel (SF) and high active waste (HAW) management policies and practices worldwide are the result of past presumptions that sufficient reprocessing and/or disposal capacity would be available in the near term. Consequently, in the past many countries have developed specific solutions for different periods of time due to their individual national nuclear policies. In Germany the concept of dry interim storage in dual purpose metal casks before disposal is being pursued for SF and HAW management and transport and storage licenses have been issued accordingly. The current operation licenses for existing storage facilities have been granted for a storage period of up to 40 years. This concept has demonstrated its suitability for over 20 years so far. Relevant safety requirements haven been assessed for the short-term as well as for the long-term for site-specific operational and accidental storage conditions. But in the meantime significant delays in the national repository siting procedure occured which will make extended storage periods necessary in the future. This paper describes the current situation in Germany with regard to dry cask storage and focuses on current perspectives considering regulatory, technical, and scientific aspects for storage license renewal. Since there is one case of a storage license limitation to only 20 years due to administrative reasons, first experience is currently gathered in case of an expiring storage license. Subsequent license options have been pursued intensively including the extension of the initial storage license as well as shipping all casks to another storage facility considering an extended storage period at that storage facility as well. All safety relevant aspects have to be reviewed on basis of the current state-of-the-art which might be different from the initial safety demonstrations. That includes new safety assessment standards as well as improved knowledge base. Major issues are e.g. improved accident scenario analyses, assessment methods, and consideration of aging effects from previous operation periods. Inspection programs with respect, e.g. to bolts and seals to verify leak-tightness and lid screw pre-stress have been initiated to demonstrate proper cask conditions for extended storage as well as transportation to another storage facility. T2 - PATRAM 2013 - 17th International symposium on the packaging and transportation of radioactive materials CY - San Francisco, CA, USA DA - 18.08.2013 KW - Extended storage KW - Long-term storage KW - Dual purpose cask PY - 2013 SP - Paper 184, 1 EP - 12 PB - Omnipress AN - OPUS4-30242 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nehrig, Marko A1 - Feldkamp, Martin A1 - Bletzer, Claus Wilhelm A1 - Wille, Frank T1 - Thermal test driven pressure build-up inside type-B packages containing wet radioactive waste N2 - In recent years several German approval procedures for ductile cast iron transport containers containing wet intermediate level waste were conducted. BAM, as one of the German competent authorities, was involved in the complex design assessment work with this specific issue. Thermal analysis is one part of the authority assessment work done by BAM in Germany. The radioactive contents of package designs which were not dried, only drained, consist of saturated ion exchange resin and a small amount of free water. Compared to the safety assessment of packages with dry content, attention must be paid to some more specific points. The most interesting point, however, is the pressure build-up inside the package due to vaporization. This could be caused by radiolysis of the liquid and must be taken into account for the storage period. The inner pressure of the package leads to mechanical loads to the package body, the lid and the lid bolts. Thus, the pressure is the driving force on the gasket system regarding the activity release and a possible loss of tightness. The paper deals primarily with the pressure build-up inside the package caused by the transport regulatory thermal test (30 min at 800 °C) as part of the cumulative test scenario under accident conditions of transport. The pressure build-up is estimated by calculation in a very conservative way regarding conduction and heat radiation. Furthermore the paper discusses a conservative approach for the estimation of the resulting pressure depending on the percentage of water inside the cask. To get trustworthy results without an exact specification of the content, experimental fire tests should be conducted. However, this paper shows the difficulties of assessing casks containing wet content. From the authority assessment point of view, drying of the content could be an effective way to avoid the above described pressure build-up and the associated difficulties for the safety assessment. T2 - PATRAM 2013 - 17th International symposium on the packaging and transportation of radioactive materials CY - San Francisco, CA, USA DA - 18.08.2013 KW - Type-B KW - Wet content KW - Pressure build-up KW - Radioactive waste KW - Thermal test PY - 2013 SP - Paper 108, 1 EP - 10 PB - Omnipress AN - OPUS4-30197 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stengel, Dominik A1 - Clobes, M. A1 - Mehdianpour, Milad ED - Schlünzen, K.H. T1 - Overhead transmission line cables under wind gust loading - measurements and numerical simulations N2 - Overhead transmission lines with conductor cables spanning over a few hundred meters are highly sensitive to the action of wind. Particularly wind acting on the cables signifies a major load on the suspension towers. In order to identify critical loading parameters and the load-response mechanism of those structures, measurements are carried out along a high voltage overhead transmission line capturing the acting wind field as well as the structural response of the cables. A finite element model of the structure is built and used to simulate the system's response. A method is presented which allows generating a complete wind field for all the model’s nodes incorporating measured wind velocities and estimated parameters of the acting wind. The full scale measurements of both action and reaction will be compared to the numerical results. T2 - CWE 2014 - 6th International symposium on computational wind engineering CY - Hamburg, Germany DA - 08.06.2014 PY - 2014 SP - Article 0158_0016, 1 EP - 8 AN - OPUS4-30860 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erhard, Anton A1 - Otremba, Frank T1 - Nondestructive testing and fracture mechanics N2 - Nondestructive Testing (NDT) and fracture mechanics are two different disciplines in applied engineering science. Both areas are very important for the evaluation of the component integrity. Unfortunately the technical understanding in both disciplines is not identically, what lead to misunderstandings. In the present paper, the basic ideas about fracture mechanics and the input parameters coming from the NDT side are explained, concerning the integrity evaluation of the components. The widely used NDT methods are magnetic particle, dye penetrant, electrical eddy currents, radiography and ultrasonics. But not all of these common NDT methods can deliver parameters satisfy the fracture mechanics requirements. The first two can detect only surface-breaking or immediately sub-surface defects. Eddy current can also find defects in deeper sub-surface layers, while radiography and ultrasonics can also find embedded, remote defects. These three methods have furthermore a high potential for defect sizing and are therefore predestined to provide fracture mechanics input parameters. At the example of steam generator tube inspection the interplay of eddy current and fracture mechanics as related to tube integrity will be explained. T2 - 5th International CANDU In-Service inspection workshop and NDT in Canada 2014 conference CY - Toronto, Ontario, Canada DA - 16.06.2014 KW - Eddy current KW - Steam generator tube inspection KW - Component integrity KW - Fracture mechanics PY - 2014 SP - 1 EP - 12 AN - OPUS4-30907 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weisbrich, S. A1 - Wu, Cheng-Chieh A1 - Neitzel, F. ED - Harte, R. T1 - On optimal measurement set-ups for parameter identification from an integrated structural analysis of hybrid measurements and finite element model N2 - One major ambition in Structural Health Monitoring (SHM) is to develop the ability to detect, identify and localize damage as well as to predict the lifespan of civil structures (Worden et al. 2007). This would allow well-informed decision on whether to repair or to demolish these structures. The word monitoring in SHM brings up several frequently ignored questions: What type of sensors and accuracies are needed to monitor a given structure? Where are the optimal sensor placements? How many sensors are necessary? How to analyse spatially distributed hybrid measurements? Or, in short: What is the sensor configuration best suited for structural health monitoring? If these questions are not explicitly addressed, the usefulness of the measurement data for an evaluation is left to coincidence. T2 - XIVth Bilateral Czech/German Symposium 'Experimental methods and numerical simulation in engineering science' CY - Wuppertal, Germany DA - 04.06.2014 PY - 2014 SP - 46 EP - 47 AN - OPUS4-30913 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maierhofer, Christiane A1 - Myrach, Philipp A1 - Steinfurth, Henrik A1 - Reischel, Mercedes A1 - Röllig, Mathias T1 - Development of standards for flash thermography and lock-in thermography N2 - Standards for the application of flash thermography as well as of lock-in thermography are urgently required. Both methods are applied more and more often in research and industry, but still extensive validation procedures are required for each individual application. In this paper, the results of two research projects concerning the validation and standardisation of both methods are presented. This includes results of a detailed study of the influence of measurements parameters on flash thermography, of the comparison of the lateral resolution obtained with flash and lock-in thermography and the description of a draft standard for flash thermography. T2 - QIRT 2014 - 12th International conference on quantitative infrared thermography CY - Bordeaux, France DA - 07.07.2014 KW - Active thermography KW - Flash KW - Lockin KW - CFRP KW - Metal KW - Standardization PY - 2014 UR - http://qirt.gel.ulaval.ca/archives/qirt2014/QIRT%202014%20Papers/QIRT-2014-032.pdf DO - https://doi.org/10.21611/qirt.2014.032 SP - 1 EP - 9 AN - OPUS4-31187 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heideklang, René A1 - Shokouhi, Parisa T1 - Quantitative multi-modal NDT data analysis N2 - A single NDT technique is often not adequate to provide assessments about the integrity of test objects with the required coverage or accuracy. In such situations, it is often resorted to multi-modal testing, where complementary and overlapping information from different NDT techniques are combined for a more comprehensive evaluation. Multimodal material and defect characterization is an interesting task which involves several diverse fields of research, including signal and image processing, statistics and data mining. The fusion of different modalities may improve quantitative nondestructive evaluation by effectively exploiting the augmented set of multi-sensor information about the material. It is the redundant information in particular, whose quantification is expected to lead to increased reliability and robustness of the inspection results. There are different systematic approaches to data fusion, each with its specific advantages and drawbacks. In our contribution, these will be discussed in the context of nondestructive materials testing. A practical study adopting a high-level scheme for the fusion of Eddy Current, GMR and Thermography measurements on a reference metallic specimen with built-in grooves will be presented. Results show that fusion is able to outperform the best single sensor regarding detection specificity, while retaining the same level of sensitivity. T2 - Quantitative nondestructive Evaluation conference 2013 (QNDE) CY - Baltimore, MD, USA DA - 2013-07-21 KW - Data fusion KW - Multi-sensor KW - Reliability PY - 2013 SP - 1 EP - 5(?) AN - OPUS4-30058 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Karsten A1 - Quercetti, Thomas A1 - Musolff, André A1 - Droste, Bernhard T1 - Quality assurance requirements for mechanical test campaigns of packagings N2 - A management system based on international, national or other standards acceptable to the competent authority shall be established and implemented for all activities including design, manufacture, testing, documentation, use, maintenance, inspection in accordance with IAEA SSR-6. Hereby, quality assured testing and documentation can substantially contribute to the demonstration of package design compliance with the regulations. Nowadays, a drop test campaign within the approval process of packages for radioactive materials can be a very complex and extensive project including various test and measurement techniques. On this basis of procedures and documents the experimental tests of packages and containers are performed with quality proofed results and a high reliability. A complete traceability and direct transferability of package design test results can give particular importance to the type approval procedure. T2 - PATRAM 2013 - 17th International symposium on the packaging and transportation of radioactive materials CY - San Francisco, CA, USA DA - 18.08.2013 KW - Quality assurance KW - Packaging KW - Drop test PY - 2013 SP - Paper 181, 1 EP - 7 PB - Omnipress AN - OPUS4-30493 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dorgerloh, Ute A1 - Theißen, H. A1 - Becker, Roland A1 - Nehls, Irene T1 - Das Problem löst sich von selbst: Stabilisierung von Grundwasserproben zur Bestimmung organischer Inhaltsstoffe N2 - Als Folge der industriellen Produktion und der vielfältigen industriellen Nutzung von organischen Lösungsmitteln sind eine Vielzahl von Edukten, Zwischen- und Endprodukten in die Umwelt eingetragen worden und führen zu massiven Verunreinigungen des Bodens und des Grundwassers. Die Untersuchung und Sanierung des Grundwassers stellt einen aktuellen Schwerpunkt in der Altlastenbearbeitung dar. Vielfach werden klassische pump & treat-Verfahren zur Grundwassersanierung verwendet. Diese aktiven Sicherungs- und Sanierungsmaßnahmen werden jedoch unter dem Gesichtspunkt der Verhältnismäßigkeit häufig als ineffizient eingeschätzt. Als Alternative sollen die natürlichen Abbauprozesse im Grundwasserleiter genutzt oder gezielt verstärkt werden, um auf diesem Weg eine in-situ-Sanierung des Grundwasserleiters zu erreichen. In den letzten Jahren haben sich verschiedene Sanierungsverfahren etabliert, bei denen durch die Zugabe von Hilfsstoffen die mikrobiologische Aktivität des Aquifers erhöht wird bzw. Stoffe zugeführt werden, die mit den Schadstoffen reagieren (in-situ chemische Oxidation bzw. Reduktion, ISCO). An ausgewählten Standorten ist auch die aktive Sanierung (pump & treat, on-site- Sanierung) mit biologischem Schadstoffabbau (Bio-Filter) kombiniert worden. Um den Sanierungsverlauf zu verfolgen und zu optimieren, ist die Beprobung von Grundwasser aus dem Grundwasserleiter oder aus laufenden Anlagen erforderlich. In Fällen der gesteigerten mikrobiologischen Aktivität des Grundwassers treten gehäuft Probleme bei der Stabilisierung der Wasserproben auf. Die forcierten Abbauprozesse der Schadstoffe gehen nach der Probenahme in der Probenflasche weiter, bis die Energiebasis der Mikrobiologie aufgebraucht ist. Durch eine geringe Temperaturerhöhung beschleunigen sich diese Prozesse zusätzlich. In der Folge können die Schadstoffgehalte teilweise innerhalb weniger Stunden stark reduziert werden. Im Analysenlabor wird dann ein Schadstoffgehalt nachgewiesen, der nicht mehr die Verhältnisse im Aquifer bzw. im Ablauf der Reinigungsstufen widerspiegelt. Eine Einschätzung des Sanierungsfortschritts oder der Reinigungsleistung ist unter diesen Bedingungen stark fehlerbehaftet und kann zu groben Fehlinterpretationen führen. Grundwasserproben, die einem Aquifer mit hoher natürlicher oder initiierter mikrobiologischer Abbauaktivität entstammen, müssen daher zusätzlich stabilisiert werden, um den Ist-Zustand zum Zeitpunkt der Probenahme zu erfassen. Die Konservierung von Wasserproben bei der Probenahme von Grundwasser ist in der Normung umfangreich beschrieben: Die EN ISO 5667-3 von 2004 ist im Normausschuss (NA 119-01-03-01-01) überarbeitet und 2012 als Norm verabschiedet worden (EN ISO 5667-3, 03.12, deutsche Fassung DIN EN ISO 5667-3, 03-2013) [1], In Einzelfällen hat sie sich nicht als ausreichend erwiesen, um die Stabilität der organischen Schadstoffe in den oben beschriebenen Wasserproben zu gewährleisten. T2 - Altlastensymposium 2014 CY - Fulda, Germany DA - 20.03.2014 KW - Grundwasser KW - In-situ-Sanierung KW - Probenahme KW - Stabilisierung PY - 2014 SP - 76 EP - 85 AN - OPUS4-30480 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kemper, Hugo A1 - Pomaska, W. T1 - Der Einfluß des Flammstrahlens auf die Eigenschaften von Stählen PY - 1953 IS - 9 SP - 1 EP - 20 PB - Beratungsstelle für Autogentechnik CY - Hürth AN - OPUS4-30014 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rietz, U. A1 - Hielscher, Stefan A1 - Kern, Janine A1 - Beck, Uwe A1 - Lerche, D. T1 - Centrifuge technology revolutionises adhesion testing N2 - Composite materials fulfil a great variety of functions in a wide field of applications. Testing the composite properties under environmental conditions is a must for development and quality control. Common tensile strength test instruments have limitations, like single sample handling only. Present test methods for multi-layers, e.g. peel test, permit semi-quantitative ,or qualitative evaluation only. A new instrument based on analytical centrifugation is introduced, using centrifugal force as test load, permitting to determine bonding and adhesive strength of up to 8 samples simultaneously. KW - Adhesion KW - Testing KW - Composites KW - Coatings KW - Tensile strength KW - Analytical centrifugation KW - Zentrifugentechnologie KW - Klebfestigkeit KW - Haftfestigkeit KW - Verbundfestigkeit PY - 2013 SN - 978-3-944261-28-7 VL - 4 SP - 1 EP - 4 PB - LUM GmbH CY - Berlin AN - OPUS4-30047 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Torge, Manfred A1 - Kruschke, Detlef T1 - Investigations into 20th century commercial glass paints and enamels T2 - Corpus vitrearum forum for the conservation of stained glass CY - Lisbon, Portugal DA - 2011-09-26 PY - 2013 UR - http://moodle.fct.unl.pt/mod/resource/view.php?id=197618 IS - Tópico 11 SP - 1 EP - 6 AN - OPUS4-30055 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Konschak, Martin A1 - Scheruhn, Willi T1 - Gasrücktrittsicherungen, ihr Wert bei Schweiß- u. Schneidarbeiten PY - 1953 VL - 5 IS - 9 SP - 1 EP - 4 PB - Beratungsstelle für Autogentechnik CY - Hürth AN - OPUS4-30021 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias T1 - The functional profile of polyglycols in engine applications T2 - 17th International colloquium tribology CY - Esslingen, Germany DA - 2010-01-19 KW - Bionotox KW - Heat capacity KW - Fuel economy KW - Drain Polyglycol KW - Polypropylene glycol KW - Polyalkylene glycol KW - Polybutylene glycol KW - BAM test KW - AlSi liner wear KW - DLC KW - Slip-rolling KW - Lubricants KW - Engine oil KW - Additives KW - Ester KW - Thin film coatings KW - Dilution KW - FAME KW - Jatropha KW - Rape seed KW - Stem valve KW - Piston ring PY - 2010 SP - 17_Woydt_Polyglycols, 1 EP - 11 AN - OPUS4-31736 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias T1 - Triboactive materials for 'zero wear' under dry sliding up to 800°C and mixed lubrication, dry oscillation and thin film coatings under slip-rolling T2 - 16th International colloquium tribology - Lubricants, materials and lubrication engineering CY - Stuttgart/Ostfildern, Germany DA - 2008-01-15 KW - Wear KW - Fretting KW - Contact geometry crossed cylinders KW - Friction KW - Thermal spraying KW - BAM test KW - SRV KW - Oscillation KW - Triboactive KW - Coatings KW - APS KW - HVOF KW - (Ti,Mo)(C,N) KW - Tin-2Cr2O2n-1 KW - Magnéli phases KW - DLC KW - THC KW - ta.C KW - High temperature KW - Foil bearings KW - Dry friction KW - Air KW - Mixed and boundary lubrication KW - Slip-rolling PY - 2008 SP - Paper 00_06_Woydt_Plenar, 1 EP - 15 AN - OPUS4-31737 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Schönbucher, A. A1 - Wehrstedt, Klaus-Dieter A1 - Bockhorn, H. A1 - Schälike, Stefan A1 - Sebbar, N. T1 - Abschätzung des Gefahrenpotentials von wechselwirkenden Bränden beim Umgang mit entzündbaren und selbst zersetzlichen Flüssigkeiten in verfahrenstechnischen Anlagen - Schlussbericht zu dem IGF-Vorhaben Nr. 396 N2 - Mechanical drop test scenarios for Type B (U) packages according to the IAEA regulations have to be carried out onto the so-called “unyielding target” (usually with cask impact limiters) and onto the puncture bar respectively. They are predefined and do not require any further investigation of scenarios that really could happen on transportation routes. Cask accident scenarios in the framework of approval procedures for interim storage sites are derived from a detailed analysis of the handling procedures necessary from arrival of cask at the site to its storing position. In that case, casks are usually handled without impact limiters. Dependent on possible drop heights, drop positions and floor properties, conservative cask accident scenarios are derived for further safety proofs. According to the mechanical assessment concept of the considered approval procedure numerical calculations have to be provided by the applicant to demonstrate mechanical cask safety. Stresses and strains in the cask body as well as in the lid System have to be identified and assessed. Using the example of a 3-mvertical-drop of a transport and storage cask for spent fuel elements onto the floor construction made of damping concrete covered by screed, BAM developed a finite element model. The finite element code ABAQUS/Explicit™ was used. Results of experimental investigations are not available. Therefore parameter studies are necessary to identify the sensitivity of the finite element model to significant Parameters and to verify the finite element models according to the requirements of the Guidelines for the Numerical Safety Analyses for the Approval of Transport and Storage Casks for Radioactive Materials (BAM GGR-008). The paper describes the modeling of the material behavior and attachment of bottom side cask components. Questions concerning the modeling of a crack length limiting reinforcement in the screed layer are discussed. The influence of the mesh density of the screed layer and its strength is considered as well. Finally, the developed finite element model can be used for a numerical safety assessment. It can help to understand the complex mechanisms of the interaction between the cask components and floor construction. PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-317195 DO - https://doi.org/10.13140/2.1.4328.1928 SP - 1 EP - 47 PB - DECHEMA CY - Frankfurt am Main AN - OPUS4-31719 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Siebler, Daniel A1 - Rohwetter, Philipp A1 - Heidmann, G. A1 - Nierhaus, T. A1 - Simunek, J. A1 - Leistner, A. A1 - Leistner, A. A1 - Plath, R. T1 - Kabelgarnituren mit integrierter faseroptischer Teilentladungssensorik T1 - Cable accessories with integrated fibre-optic partial discharge sensors N2 - Wir demonstrieren die Machbarkeit rückwirkungsfrei integrierter optischer Teilentladungssensorik für Aufschiebeelemente aus Silikonelastomer zur Verwendung in Kabelgarnituren. Zu diesem Zweck wurden sowohl ein Funktionsmodell eines optisch transparenten Silikon-Kabelendverschlusses mit integriertem Silikon-Lichtwellenleitersensor als auch ein rein optisches TE-Messsystem auf Basis von zwei Einzelphotonendetektoren und einer Koinzidenzschaltung (PD-COP) entwickelt, die hier vorgestellt werden. Die Leistungsfähigkeit und Stärken der optischen TE-Messtechnik zeigen sich sowohl in Kombination mit der elektrischen Messtechnik, als auch bei alleinigem Einsatz. T2 - VDE Fachtagung Hochspannungstechnik CY - Berlin, Germany DA - 14.11.2016 KW - Faseroptik KW - Teilentladungssensorik KW - Fibre-optic KW - Partial discharge sensors PY - 2016 SN - 978-3-8007-4310-0 SP - 608 EP - 613 PB - VDE Verlag GmbH CY - Berlin AN - OPUS4-38976 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Kranzmann, Axel T1 - Borehole integrity of austenitized and annealed pipe steels suitable for carbon capture and storage (CCS) N2 - Properties of pipe steels for CCS (carbon capture and storage) technology require resistance against the corrosive environment of a potential CCS-site (heat, pressure, salinity of the aquifer, CO2-partial pressure). The influence of austenitzing in heat treatment routines of two different injection pipe steels (1.4034, X46Cr13 and 1.4021, X20Cr13) was evaluated. Steel coupons were austenitized at different temperatures (900-1050 °C) for different lengths of time (30-90 min) before quenching and annealing prior to long term corrosion experiments (60°C, 100 bar, artificial brine close to a CCS-site in the Northern German Basin, Germany). In general, fewer pits are found on X46Cr13. Comparing steels with 13% chromium each the higher carbon content of X46Cr13 (0.46% C) results in a lower number of pits compared to X20Cr13 (0.20% C). It is found that neither the carbon content of the steels nor austenitizing temperature has much influence, but local corrosion behaviour is most susceptible towards austenitzing time. T2 - 6th International Conference on Future Environment and Energy (ICFEE 2016) CY - Pattaya, Thailand DA - 23.01.2016 KW - CCS KW - CO2 KW - Corrosion KW - Steel KW - Heat treatment PY - 2016 SP - 9 EP - 14 AN - OPUS4-38980 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nikonov, A. Y.. A1 - Dmitriev, A. I. A1 - Österle, Werner T1 - Molecular dynamics study of slip mechanisms of nickel with amorphous-like Ni-P coating N2 - In the paper by using molecular dynamics method we investigate behavior of nickel-phosphorus compound in amorphous-like state under conditions of shear loading at the constant velocity. Samples with an amorphous layer of pure nickel and nickel-phosphorus compound were considered. The analysis showed that forces of shear resistance in the sample with an amorphous layer containing phosphorus in about 3 times less than the sample with a layer of pure nickel. Thus, it was shown that nickel-phosphorous coating in amorphous-like state may exhibit low friction properties, and, therefore, serve as the solid lubricant material. T2 - International Conference on Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures CY - Tomsk, Russia DA - 19.09.2016 KW - Local structural transformations KW - Lattice PY - 2016 DO - https://doi.org/10.1063/1.4966457 VL - 1783 SP - 020164-1 EP - 020164-4 AN - OPUS4-38932 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dmitriev, A. I. A1 - Österle, Werner T1 - Sliding simulation of automotive brake primary contact with variable amounts of copper and graphite nanoparticles N2 - Copper is one of the most important components in brake pads and its amount can reach up to 14%. In spite of a number of positive features copper usage in brake pad formulations has recently become the subject of considerable discussions, primarily due to concerns about potential risks related to environmental impacts of copper particles. So, for developing new pad formulations with possible replacements of copper content, it is very important to understand the functionality of copper additions to brake friction materials. In the paper theoretical investigation of the role of copper as a pad ingredient was carried out on the basis of modelling by the method of movable cellular automata (MCA). In the study the concentration of copper particles in a Fe3O4-matrix was varied. The sliding simulations were performed while assuming material properties at 500 degrees C in order to assess the beneficial role of copper during severe braking conditions corresponding to fading cycles during dynamometer testing. T2 - International Conference on Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures CY - Tomsk, Russia DA - 19.09.2016 KW - Polymer matrix composite KW - Silica nanoparticles KW - Friction KW - Wear PY - 2016 DO - https://doi.org/10.1063/1.4966337 VL - 1783 SP - 020044-1 EP - 020044-4 AN - OPUS4-38933 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hilgenberg, Kai A1 - Rethmeier, Michael A1 - Steinhoff, K. T1 - Surface structuring by pulsed laser implantation N2 - Micrometric surface topologies are required for a wide range of technical applications. While lowered surface features have been used for many years to improve the tribological behavior of contacting surfaces, there are also other fields of application, where the potential of elevated surface features is known, e. g. for metal forming tools. However, the demand for a high wear resistance of these structures often inhibits an industrial application. A solution is offered by structuring techniques that use additional material. A promising approach is the localized dispersing of hard ceramic particles by pulsed laser radiation, the so-called laser implantation. This paper describes the potential to adjust the geometry as well as the mechanical properties of laser implanted surfaces by means of microstructural and topological investigations. Afterwards, results of a wear test are given and different applications for this structuring technique are discussed. It can be shown that dome-shaped or ring-shaped structures on a micrometric scale can be produced with high hardness and wear resistance. T2 - THERMEC 2016: 9th International Conference on Processing & Manufacturing of Advanced Materials CY - Graz, Austria DA - 29.05.2016 KW - Surface structuring KW - Metal forming tools KW - Laser implantation KW - Laser dispersing PY - 2017 DO - https://doi.org/10.4028/www.scientific.net/MSF.879.750 SN - 1662-9752 VL - 879 SP - 750 EP - 755 PB - Trans Tech Publications CY - Schweiz AN - OPUS4-38927 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Musolff, André A1 - Quercetti, Thomas A1 - Müller, Karsten A1 - Bartholmai, Matthias T1 - Impact Analysis of RAM Packages under Kinematic Aspects N2 - BAM is the German Federal Institute for Materials Research and Testing and the competent authority for mechanical and thermal safety assessment of transport packages for spent fuel and high level waste. In context with safety assessment of RAM packages BAM performed numerous drop tests in the last decades. The tests were mostly accompanied by extensive and various measurement techniques especially by instrumented measurements with strain gages and accelerometers. The procedure of drop testing and the resulting measurement analysis are the main methods to evaluate the safety against mechanical test conditions. Measurement techniques are dedicated to answer questions in regard to the structural integrity of a RAM package, the mechanical behavior of the prototype as well as of its content under impact conditions. Test results like deceleration-time functions constitute a main basis for the validation of assumptions in the safety analysis and for the evaluation of numerical calculations. In this context the adequate selection of accelerometers and measurement systems for the performance of drop tests is important. Therefore it is not only necessary to find suitable positions for the accelerometers at the test specimens, but also to consider technical boundary conditions as e.g. temperature. T2 - PATRAM 2016 CY - Kobe, Japan DA - 18.09.2016 KW - RAM packages KW - Drop test KW - Impact KW - Radioactive PY - 2016 UR - http://www.patram2016.org/ SP - Paper 1030, 1 AN - OPUS4-38859 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Unger, Wolfgang T1 - Non-destructive surface measurements N2 - Materials and chemical producers require detailed knowledge of surface chemistry for research into new products. One way to understand a surface without damaging it is to bombard it with an electron beam, causing its atoms to emit characteristic X-rays enabling identification. The measurement of these must be precise as many elements emissions are close in energy – traceable reference materials will ensure instruments using this technique are stable and accurate. KW - Metrology KW - EDS KW - EDX PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-388647 UR - http://www.euramet.org/metrology-for-societys-challenges/metrology-for-industry/impact-case-studies-emrp-industry-theme/ SP - 1 EP - 2 CY - Teddington AN - OPUS4-38864 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Unger, Wolfgang T1 - Measuring organic layers N2 - Many innovative products - from touchscreens to solar panels to pharmaceuticals – utilise multiple organic layers to create complex functionality. New techniques have been developed to remove and measure layers individually enabling improved product development and assisting with quality assurance. However, manufacturers cannot be certain of the depth of layer being removed and new reference materials for these techniques are needed to increase uptake, and remove a major barrier to innovation. KW - Organic layers KW - XPS KW - SIMS PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-388656 UR - http://www.euramet.org/metrology-for-societys-challenges/metrology-for-industry/impact-case-studies-emrp-industry-theme/ SP - 1 EP - 2 CY - Teddington AN - OPUS4-38865 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Unger, Wolfgang T1 - Surface analysis for Alzheimer’s N2 - Modifying or controlling surface chemistry is important in new product development, quality control and research. This is particularly true where functionality of surfaces, thin films and interfaces are key to the application, such as organic solar cells and devices for medical diagnostics. Surface chemical analysis aims to provide quantitative elemental, chemical state and functional group information from the surface of materials, but requires comparable test data and improved measurement traceability. KW - Liposomes KW - Proteins KW - ToF-SIMS KW - Peptides KW - Mapping PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-388663 UR - http://www.euramet.org/metrology-for-societys-challenges/metrology-for-industry/impact-case-studies-emrp-industry-theme/ SP - 1 EP - 2 CY - Teddington AN - OPUS4-38866 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Babutzka, Martin A1 - Burkert, Andreas A1 - Heyn, A. T1 - Korrosionsuntersuchungen mit gelartigen Elektrolyten zur Beschreibung der Korrosionsschutzwirkung von Zinküberzügen N2 - Ein neuer Ansatz bei elektrochemischen Korrosionsuntersuchungen kann durch den Einsatz von gelartigen Elektrolyten als Alternative zu wässrigen Prüfelektrolyten beschritten werden. Gelartige Elektrolyte ermöglichen minimalinvasive Untersuchungen an natürlich gebildeten Zinkdeckschichten. Dadurch können korrosionsrelevante Kennwerte ermittelt werden, die Aussagen zur Deckschichtbildung und zur Stabilität der gebildeten Deckschichten unter verschiedenen klimatischen Bedingungen erlauben. In diesem Beitrag wird anhand verschiedener Deckschichtzustände an Zink der Mehrwert von Untersuchungen mit gelartigen Elektrolyten für die Korrosionsforschung verdeutlicht. T2 - 16. Tagung "Korrosionsschutz in der maritimen Technik" CY - Hamburg, Germany DA - 25.01.2017 KW - Deckschichtbildung KW - Layer formation KW - Gelartige Elektrolyte KW - Gel-type electrolytes KW - Korrosionsprüfung KW - Corrosion testing KW - Zinkdeckschichten KW - Zinc coatings PY - 2017 SN - 978-3-935406-64-2 VL - 16 SP - 35 EP - 44 AN - OPUS4-39041 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Unnikrishnakurup, Sreedhar A1 - Kidangan, R. T. A1 - P. Vengara, N. A1 - Balasubramaniam, Krishnan A1 - Rajagopal, P. A1 - Phani Prabhakar, K. V. A1 - Padmanabham, G. T1 - Application of infrared thermography technique for the monitoring of cold metal transfer (CMT) joining of aluminium to galvanized steel N2 - In this study, the feasibility of using non-contact Infrared thermography as a potential tool to monitor the CMT welding process is explored. The presence of internal defects such as porosity, lack of filler material deposition and formation of improper weld bead produce perturbations in the surface temperature which can be identified using an Infrared thermography technique. We present recent results obtained from online monitoring of the the dissimilar joining using CMT weld brazing of Aluminum and Steel using a transmission mode measurement approach. The effect of loss of zinc coating on the weldability of the cold metal transfer joining of aluminum to galvanised steel was investigated. A correlation between measured online thermal indications with the weld anomalies is successfully attempted and the results are compared with the conventional post-weld NDT inspection methods. T2 - 19th World Conference on Non-Destructive Testing (WCNDT 2016) CY - Munich, Germany DA - 13 June 2016 KW - Infrared thermography KW - CMT welding KW - Weld defects KW - Online monitoring PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-389155 UR - http://ndt.net/?id=19475 SN - 1435-4934 VL - 21 IS - 7 SP - 1 EP - 8 PB - NDT.net CY - Kirchwald AN - OPUS4-38915 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Heinrich, Thomas T1 - Switchable Surfaces: Mono- and Multilayers of Stimuli-Responsive Supramolecules on Solid Supports N2 - Rotaxanes are mechanically interlocked molecules (MIMs) that are considered to be excellent prototypes for the development of molecular machines. They comprise a discrete number of molecules that are bound to each other via non-covalent interactions. Mechanically interlocked means that a covalent bond must be broken in order to separate the molecules from another. If the rotaxanes are furthermore provided with different binding sites, they can perform a con-formational change and thus a nanoscopic movement by the application of an external stimu-lus. However, this movement is not directed in solution and a macroscopic effect is therefore, if at all, very difficult to realize. The integration of rotaxanes into a reference system by, for example, the immobilization on a surface is regarded as a promising approach to convert the generated nanoscopic motion into a macroscopic effect. The present work describes the immobilization of chloride-switchable rotaxanes onto surfaces using a variety of methods. In detail, the applied methods are the metal-mediated layer-by-layer (LbL) self-assembly and the covalent deposition using click chemistry, which can be con-sidered as separate approaches. Before the rotaxanes were immobilized, the deposition meth-ods were first established and gradually improved on the basis of earlier results by using dif-ferent macrocycle and guest molecules. Various template layers – so-called self-assembled monolayers (SAMs) – were used. These are terminated with pyridine or terpyridine for the metal-induced LbL deposition. Azide-terminated SAMs are used for the covalent deposition. In the course of that, the following objectives were achieved: The deposition of diterpyridin functionalized macrocycles in multilayers with a preferential orientation was investigated and verified by transmission-UV/Vis, X-ray photoelectron spectroscopy (XPS) as well as near edge X-ray absorption fine structure (NEXAFS). In order to produce the multilayer, metal-ions and macrocycles were alternately deposited onto various SAMs. To enable further process control for the LbL deposition, Time-of-Flight Secondary Ion Mass Spectrometry (ToF-SIMS) has been extended by use of Principal Component Analysis (PCA) which is capable of analyzing even very small changes in the deposition procedure. By using two different macrocycles and four metals, a mixed multilayer was fabricated that can be programmed by its deposition sequence. The treatment of the multilayers with appropriate guest molecules showed that they are on one hand addressable to the lowest layer by an external stimulus and that they are on the other hand able to incorporate a relatively large amount of the guest. Additionally, the covalently deposited supramolecules are also able to bind guests and to adapt to their structures. In both cases, the reversibility could be shown by appropriate experiments. Finally, the introduction of pyridine-functionalized nanoparticles into the multilayers led to a higher guest uptake, which can be explained by the reduction of the macrocycle-order due to the uneven surface of the nanoparticles. KW - Layer-by-layer deposition KW - XPS KW - NEXAFS KW - ToF SIMS KW - Switchable rotaxane PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:188-fudissthesis000000103658-0 SP - 1 EP - 139 PB - Freie Unversität CY - Berlin AN - OPUS4-39614 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Traulsen, Christoph T1 - Programmierbare supramolekulare (Komposit-)Multischichten auf Gold- und Siliziumoberflächen N2 - The present doctoral thesis focuses on the deposition of programmable supramolecular multilayers and composite-multilayers on gold and silicon substrates using a layer-by-layer selfassembly approach which is based on coordination chemistry. For this purpose, a variety of pyridine- and terpyridine-terminated self-assembled monolayers has been developed and deposited on gold and silicon substrates. Multitechnique analysis was carried out using X-ray photoelectron spectroscopy (XPS), (angle-dependent) near-edge Xray-absorption fine-structure spectroscopy (NEXAFS spectroscopy), time-of-flight secondaryion mass spectrometry (ToF-SIMS), transmissions UV/Vis spectroscopy as well as atomic force microscopy (AFM). By optimization of the deposition procedure, highly-ordered monomolecular and binary monolayers were deposited. As a proof of principle, transition metal-ions and appropriately labeled test-ligands were deposited on top of the functional monolayers. Furthermore, monolayers of terpyridine-terminated tetralactam macrocycles and the corresponding ether rotaxanes have been immobilized using coordination chemistry. In order to enhance the macrocycle surface coverage, the deposition procedure has been optimized as well. Multilayers consisting of diterpyridine-terminated tetralactam macrocycles have been deposited using either Fe(II) or alternatingly Fe(II) and Ni(II) metal-ions. The surface analysis proved a regular layer growth and a remarkable orientation of the macrocycles within the layer stacks. The applicability of the deposition procedure was expanded to a programmable layer stack by implementing pyridine-terminated macrocycles. The monodentate ligands led to an additional coordination sphere and thus to the application of a different transition metal-ion. The macrocycles and metal-ions were programmed according to the deposition sequence applied. The corresponding layer stack exhibited a linear dichroism of the π*-resonance corresponding to a preferential orientation of the macrocycles. Furthermore, the concept was extended to the deposition of composite multilayers consisting of pyridine-functionalized macrocycles and gold-nanoparticles which were synthesized during this thesis as well. Finally, reversible on-surface host-guest complex formation N2 - Die vorliegende Dissertation befasst sich mit der Herstellung von programmierbaren, supramolekularen Multischichten und Komposit-Multischichten auf Gold- und Siliziumoberflächen durch Anwendung eines koordinationschemischen Schicht-auf-Schicht-Selbstorganisationsverfahrens und den damit verbundenen Synthesen, Beschichtungen und Analysen. Um dieses Ziel zu erreichen, wurde zunächst eine Vielzahl von pyridin- und terpyridinterminierten selbstorganisierten Monoschichten (SAM) hergestellt und auf Gold- und Siliziumoberflächen abgeschieden. Die Abscheideprozedur wurde optimiert wobei zur Analytik der Oberflächen Röntgenphotoelektronenspektroskopie (XPS), winkelabhängiger kantennaher Röntgenabsorptionsfeinstrukturspektroskopie (NEXAFS-Spektroskopie), Flugzeit-Sekundärionen-Massenspektrometrie (ToF-SIMS), Transmissions-UV/Vis-Spektroskopie sowie Rasterkraftmikroskopie (AFM) eingesetzt wurde. Es konnte gezeigt werden, dass sich hochgeordnete monomolekulare und gemischte Monoschichten erzeugen lassen. Die terminalen funktionellen Gruppen dieser SAMs konnten als Ligand zur Komplexbildung mit Übergangsmetallionen verwendet werden. Diese koordinative Haftschicht wurde zur Verknüpfung zunächst von Testliganden und später von terpyridin-terminierten Tetralactam-Makrozyklen (TLM) und darauf basierenden Etherrotaxanen verwendet. Hierbei wurden ebenfalls die Beschichtungsbedingungen optimiert, um einen vollständigen Bedeckungsgrad zu erreichen. Unter Verwendung dieser Bedingungen wurden anschließend Multischichten aus TLMs und Fe(II)-Ionen sowie alternierend Fe(II) und Ni(II) abgeschieden. Die Analyse der hergestellten Multischichten zeigte reproduzierbar ein regelmäßiges, kontrollierbares Wachstum und eine Vorzugsorientierung. Durch den Einsatz von pyridin- und terpyridin-terminierten TLMs mit variierenden Metallionen konnte gezeigt werden, dass es möglich ist, die Abfolge verschiedener Schichten der Multischicht gezielt festzulegen. Im weiteren Verlauf der Arbeit wurden pyridin-terminierte Goldnanopartikel hergestellt und in die Multischichten integriert, um so Komposit-Multischichten herzustellen. Letztlich konnte gezeigt werden, dass die erzeugten Multischichten genutzt werden können, um über nicht-kovalente Wechselwirkungen reversibel Gastmoleküle zu binden und freizusetzten. KW - Layer-by-layer deposition KW - XPS KW - NEXAFS KW - ToF SIMS KW - Progammable rotaxane stacks PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:188-fudissthesis000000096664-6 SP - 1 EP - 141 PB - Freie Universität CY - Berlin AN - OPUS4-39615 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pelkner, Matthias A1 - Stegemann, Robert T1 - GMR Sensor Arrays for High-Spatial Resolution Measurements in NDT-Applications N2 - Magneto resistive (MR) sensors are suited for a wide range of different applications. Especially due to their small sizes and their frequency-independent behaviour, they are eligible candidates for non-destructive testing methods where high spatial resolution is required. The use of specialized magnetic field probes enables not only a defect evaluation, but also a localized characterization of ferromagnetic materials. This paper presents some NDT (non-destructive testing) examples concerning magnetic flux leakage applications (MFL) and eddy current testing (ET). For MFL-testing we used an NDT-adapted GMR (Giant MR) sensor array for the detection of small inclusions in thin steel sheets. We also investigated the effects of microstructure on magnetic properties using GMR sensors. The ET-example describes an MR array probe consisting of 32 MR-elements, an ASIC, subsequent readout components and a one-wire excitation to generate eddy currents inside the material (developed in the EU-funded IMAGIC-project, 2011-2014, 7th Framework Programme). Using this MR-probe we achieved results with a better spatial resolved defect detection of neighbouring boreholes compared to “conventional” ET-probes. T2 - 14th Symposium Magnetoresistive Sensors and Magnetic Systems CY - Wetzlar, Germany DA - 21.03.2017 KW - GMR KW - Eddy current testing KW - Magnetic flux leakage PY - 2017 SP - 146 EP - 153 AN - OPUS4-39557 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Ehlert, Christopher T1 - Simulationen von Röntgenabsorptionsprozessen zur Charakterisierung von Systemen in kondensierter Phase N2 - Diese Doktorarbeit ist das Resultat einer intensiven und fruchtbaren Zusammenarbeit zwischen dem Fachbereich 6.1 (Oberflächenanalytik und Grenzflächenchemie) der Bundesanstalt für Materialforschung und -prüfung (BAM) sowie der Arbeitsgruppe Theoretische Chemie von Professor Saalfrank an der Universität Potsdam. Zusammen haben wir die Strukturaufklärung von Systemen in kondensierter Phase unter Verwendung der Röntgenabsorptionsspektroskopie betrieben. Von Seiten der BAM wurden experimentelle Röntgenabsorptionsspektren hoher Auflösung an modernen Synchrotroneinrichtungen (BESSY II, Berlin) aufgenommen. Die Theoretische Chemie liefert, unter Verwendung quantenchemischer Methoden, die Möglichkeit die Spektren zu simulieren. Bei der Röntgenabsorption wird ein Photon hoher Energie von einem molekularen System absorbiert und in einen angeregten Zustand versetzt. Die Intensität der Absorption ist stark abhängig von der eingestrahlten Photonenenergie. Das resultierende Absorptionsspektrum enthält eine Vielzahl von Informationen. Meine Aufgabe bestand darin, die untersuchten Systeme am Computer zu modellieren. KW - XPS KW - NEXAFS KW - Spektrensimulation PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:517-opus4-104844 SP - 1 EP - 142 PB - Universität Potsdam CY - Potsdam AN - OPUS4-39562 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Deppe, Hans-Joachim T1 - Preservation of Wood-Based Panels N2 - Universal application of wood-based panels (coreboard, plywood, hardboard, MDF, particle board, moulded products of particles and fibres) for inferior and exterior use is increasing. Compared with solid wood products they have several advantages (large size, homogeneity, controllable properties etc). As a result the consumption ratio of solid wood: woodbased panels decreased from 20:1 in 1950 to 2:1 today. This trend can be observed in industrialised as well as in developing countries. T2 - FAO/UNPD Technical consultation on wood based panels CY - New Delhi, India DA - 13.01.1983 PY - 1983 SP - 57 EP - 73 AN - OPUS4-39598 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kind, Thomas T1 - Gleisbettschotteruntersuchung mit der Impulsradar Array - Technik N2 - Das ZfP Verfahren Impulsradar wird bei der Untersuchung des Schotterunterbaus von Schienen wegen unterstützend eingesetzt, um deren Struktur und Materialeigenschaften zu bestimmen. Eingesetzt werden kann dieses Verfahren sowohl für die Qualitätskontrolle beim Neubau von Schienenwegen als auch für die Bedarfsermittelung von Instandsetzungsarbeiten aufgrund von Schotterverunreinigungen. Kosten können eingespart werden durch eine Verlängerung der Reinigungszyklen und der Lebensdauer des Schotters. Ein Antennenarray für die Ermittlung der Ausbreitungsgeschwindigkeit wurde entwickelt und aufgebaut. Ergebnisse von Schottermessungen im Labor werden vorgestellt. T2 - Fachtagung Bauwerksdiagnose - Praktische Anwendungen Zerstörungsfreier Prüfungen und Zukunftsaufgaben CY - Berlin, Germany DA - 21.02.2008 KW - Radar KW - Zerstörungsfreie Prüfung PY - 2008 SN - 978-3-940283-08-5 VL - 112 SP - 1 EP - 8 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung CY - Berlin AN - OPUS4-39823 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kind, Thomas T1 - Entwicklung eines Radarantennenarrays zur Untersuchung des Untergrundes im Schottergleisbett N2 - Die Erarbeitung der Grundlagen für effiziente und bedarfsgerechte Instandsetzungsmaßnahmen an Schottergleisbetten ist das Ziel des Projektes „SafeRail“. Das Impulsradarverfahren wird als zerstörungsfreie Methode für die Zustandsbestimmung des Schotters verwendet, um entsprechend den hohen Anforderungen der Netzbetreiber Unterbrechungen des Schienenverkehrs weitgehend zu vermeiden. Für eine automatisierte Bewertung der Vermischung des Schotters mit dem Untergrund sowie des Abnutzungszustandes des Schotters wird ein Antennenarray entwickelt, das bezüglich seiner Messgeometrie optimiert wird. T2 - Fachtagung Bauwerksdiagnose 2006 - Praktische Anwendungen zerstörungsfreier Prüfungen und Zukunftsaufgaben CY - Berlin, Germany DA - 23.02.2006 KW - Radar KW - Zerstörungsfreie Prüfung PY - 2006 SN - 3-931381-71-4 VL - 100 SP - 1 EP - 6 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-39824 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kind, Thomas A1 - Maierhofer, Christiane T1 - Railway Ballast Fouling Inspection by Monitoring the GPR Propagation Velocity with a Multi-Offset Antenna Array N2 - In this paper, a new method for the investigation of the degradation of ballast railway track beds is proposed. An array of antennas is used for simultaneous acquisition of reflected radar impulses, which have been transmitted from different sending positions. This array setup allows an automated CMP-measurement, which enables a direct calibration of the ballast thickness. These multiple offset measurements using the array setup are well suited for fast railway inspections. The method offers the possibility to visualize the state of degradation of the ballast in a velocity spectrum. T2 - 11th International Conference on Ground Penetrating Radar, the Ohio State University CY - Columbus, Ohio, USA DA - 19.06.2006 KW - Radar KW - Non-destructive testing KW - Railroad PY - 2006 SP - 1 EP - 4 CY - Columbus, Ohio AN - OPUS4-39825 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kind, Thomas T1 - Multi-offset impulse radar for the inspection of railway ballast N2 - A multi-offset radar system will be presented that features the possibility to get quantitative information about the wave propagation velocity as a measure of the ballast quality. This goes beyond the regular application of conventional radar systems offering only qualitative structural information. The new approach provides a fast NDT method for the classification of ballast fouling. A main advantage of the multi-offset radar is that regular ballast digging for velocity evaluation can be avoided and travel time can be directly transformed into an equivalent depth by using the automatically evaluated velocity. The maintenance cost and interruption time can be significantly decreased by this method. The application of velocity evaluation method is common in geophysical applications but it is used for ballast inspection for the first time. T2 - 9th International Congress Railway Engineering CY - University of Westminster, London, UK DA - 20.06.2007 KW - Radar KW - Non-destructive testing KW - Railroad PY - 2007 SN - 0-947644-61-10 VL - 2007 SP - 1 EP - 7 AN - OPUS4-39826 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kusche, Christian A1 - Knaust, Christian A1 - Krause, U. T1 - Ermittlung von Verbrennungseffizienzen für Feststoffe N2 - Brandlasten stellen eine Gefahr für den Menschen sowie für das industrielle Gebäude dar, in dem sie gelagert sind. Das Brandverhalten der Brandlasten bestimmt dabei maßgeblich die Schwere der Gefahr. Brandschutzmaßnahmen dienen dazu, im Brandfall das Schadensausmaß zu minimieren. Um geeignete Brandschutzmaßnahmen ableiten zu können, ist es erforderlich, das Brandverhalten der Materialien zu bewerten. Eine international angewandte Möglichkeit zur Bewertung des Brandverhaltens von Feststoffen und Flüssigkeiten ist die Verbrennungseffizienz χ. Sie ist das Verhältnis der während einer Verbrennung effektiv freigesetzten Wärme (effektive Verbrennungswärme) zu der maximal möglichen Wärmemenge (Heizwert). Die Grundlage zur Bestimmung von Verbrennungseffizienzen stellen die Wärmefreisetzungsrate (HRR) und die Massenverlustrate (MLR) dar. Ein standardisiertes Bestimmungsverfahren existiert nicht. So liegt es in dem Ermessen des Anwenders, in welcher Prüfapparatur die Experimente durchgeführt werden und welcher Zeitbereich der HRR und der MLR zur Berechnung der Verbrennungseffizienz verwendet wird. Im Rahmen dieser Arbeit wurden Versuche im Cone Calorimeter und im Single Burning Item test anhand von hölzernen Materialien durchgeführt. Die Ergebnisse zeigen auf, dass sich in Abhängigkeit von der verwendeten Prüfapparatur und in Abhängigkeit des für die Berechnung betrachten Versuchszeitraumes verschiedene Werte der Verbrennungseffizienz ergeben. Auf Grundlage dieser Erkenntnisse wurde eine Methode entwickelt, mit der reproduzierbare Werte berechnet werden können. Dabei erfolgt die Berechnung lediglich für die Vollbrandphase. Diese Brandphase stellt die Hauptbrandphase dar und ist durch eine gleichmäßige Verbrennung mit wenigen Änderungen in der Branddynamik gekennzeichnet. T2 - 5. Magdeburger Brand- und Explosionsschutztage 2017 CY - Magdeburg, Germany DA - 23.03.2017 KW - Verbrennungseffizienzen KW - Rechenmodelle KW - Cone Calorimeter KW - Single Burning Item test KW - Brandverhalten KW - Modellierung von Bränden KW - Rauchausbreitung KW - Validierung KW - Brandlastberechnung PY - 2017 SN - 978-3-00-056201-3 DO - https://doi.org/10.978.300/0562013 SP - 1 EP - 13 PB - Otto-von-Guericke-Universität Magdeburg CY - Magdeburg AN - OPUS4-40047 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Herrmann, Bianca T1 - Autökologische und molekularbiologische Untersuchungen zur Charakterisierung der Kleidermotte Tineola bisselliella (Lepidoptera) als Referenzorganismus N2 - Die Kleidermotte Tineola bisselliella, ursprünglich vermutlich aus Afrika stammend (Zeller, 1852), ist als weltweit verbreiteter Materialschädling in Wohnungen, Lagern und Museen bekannt (Key & Common, 1959; Querner, 2014). Um in Form des Integrated Pest Management (IPM) Methoden zur Erkennung, Prävention und Bekämpfung von Vorrats- und Materialschädlingen zu organisieren und zu entwickeln, ist eine genaue Kenntnis der Biologie, Ökologie und des Verhaltens des Schädlings entscheidend. In dieser Arbeit wird aufbauend auf den Studien zur Entwicklung von T. bisselliella unter verschiedenen Temperaturen und Luftfeuchten von Titschak (1925) das Falterschlupfverhalten quantifiziert und mit dem unter der Konkurrenzsituation mit dem aus der gleichen Nahrungsgilde stammenden Polsterwarenkäfers (Anthrenus flavipes) verglichen. Die Konkurrenzfähigkeit der Kleidermotte über das gesamte betrachtete Spektrum an Temperatur und Luftfeuchtigkeiten machen sie als Materialschädling so erfolgreich. Darüber hinaus wird das Vorkommen in natürlichen Reservoiren durch die Untersuchung von Freilandfängen an verschiedenen Standorten in Berlin und Umgebung als unwahrscheinlich angesehen. Molekularbiologische Betrachtungen des Genflusses anhand von mitochondrialen Sequenzabschnitten sowie BOX-PCR Mustern zeigen zwar keine Fragmentierung der Populationen in die einzelnen Fangstandorte, jedoch kann auch ein Netzwerk aus passiver Verbreitung durch den Menschen für einen kontinuierlichen Genfluss sorgen. KW - BOX PCR KW - Kleidermotte KW - Evolution KW - Freilandvorkommen PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:188-fudissthesis000000104477-0 UR - http://www.diss.fu-berlin.de/diss/receive/FUDISS_thesis_000000104477 SP - 1 EP - 150 PB - Freie Universität CY - Berlin AN - OPUS4-40120 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gräning, Dirk A1 - Gradt, Thomas T1 - Sliding wear of martensitic steels in hydrogen – X30CrMoN15-1 and 100Cr6 – the role of water traces N2 - Die Untersuchung befasste sich ursprünglich mit dem Einfluss von gasförmigem Wasserstoff bei Normaldruck auf den Verschleiß von martensitischen Stählen. Dabei wurde als Gegenkörper eine Al2O3-Kugel verwendet, da dieser Werkstoff inert und zugleich hart ist und somit immer einen geringen Abtrag aufweisen sollte. Um 1 ppm Wasserstoff ohne thermomechanische Unterstützung in reines α-Eisen zu drücken, wird nämlich ein Druck von 15·105 MPa(~15 Mbar) benötigt. In der Versuchsreihe wiesen die Al2O3-Kugel in N2- und H2-Atmosphäre einen hohen Verschleiß auf, während bei Luft-Versuchen die Spur klein und der Verschleiß an der Scheibe groß war. Durch Streuungen und daraus folgenden Untersuchungen zeigte sich, dass Wasserstoff keinen merkbaren Einfluss hatte, Wasserspuren im Gas aber dafür umso deutlicher den Verschleiß beeinflussten. N2 - Initially the primary objective of the project has been the investigation of the influence of gaseous hydrogen on the wear of martensitic steels under heavy tribological stress. As a counter body an Al2O3 ball has been used because the material is inert and hard so that a low amount of wear was expected. If only the gas pressure is responsible for the absorption of hydrogen from the gas to pure α-iron it would require 15·105 MPa (~15 Mbar) to press 1 ppm into the material. In the test series the Al2O3 balls showed in N2 and H2 atmosphere a higher wear compared to aerial experiments which showed a smaller wear track and a severer wear for the disc. Because of scattering and thereof following investigations it was shown that hydrogen has no noticeable influence but water traces in the gas are manipulating the outcome of the tests distinctly. T2 - 57. Tribologie-Fachtagung CY - Göttingen, Germany DA - 26.09.2016 KW - Tribology KW - Hydrogen environment KW - Alumina KW - Martensitic steel KW - Adsorbed water film PY - 2016 SN - 978-3-9817451-1-5 VL - 2016 SP - 1.3/1 EP - 1.3/6 AN - OPUS4-40105 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völzke, Holger A1 - Wolff, Dietmar T1 - Update on the German approach of storing spent nuclear fuel in dual purpose casks until final disposal N2 - The German approach of storing spent nuclear fuel in dual purpose casks until final disposal is based on individually licensed storage sites concerning specific nuclear inventories and dual purpose cask types. The currently approved license period is maximum 40 years. With nuclear policy changes including the phase-out decision of 2011 and a new approach for the HLW repository siting process set up 2013 by law also the spent fuel and HLW management strategy has to be adapted. This includes the timely development of disposal container concepts as part of the overall repository siting process and the need for longer interim storage periods until final disposal. Other aspects affect new regulations about the financing of the nuclear waste management by the industry and the public sector, the restructuring of responsible authorities in 2016/2017 and the adaption of R&D funding programs addressing also pre-disposal (or extended interim storage) issues. BAM as a Federal Research Institute has been responsible for or in charge of container safety Evaluation for transport and storage casks for radioactive waste for several decades and started addressing potential Extended interim storage issues already several years ago. This included participation in international projects at the IAEA or in the U.S. Extended Storage Collaboration Program (ESCP) as well as long term laboratory tests with metal seals, elastomeric seals and polymers for neutron shielding purposes. Test results of BAM are published regularly and gained data provide valuable information about thermo-mechanical and radiological degradation effects as well as the long term Performance of respective cask components. Regarding the reliable extrapolation and prediction of the long term Performance of cask materials and components for time periods of up to 80 or even 100 years the continuation and extension of laboratory tests and the development of analytical and numerical simulation models and tools is essential and under way. T2 - 16th International High -Level Radioactive Waste Management Conference (IHLRWM 2017) CY - Charlotte, NC, USA DA - 09.04.2017 KW - Spent fuel KW - Storage KW - Cask KW - Safety KW - Disposal PY - 2017 SP - 189 EP - 194 AN - OPUS4-40411 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Orellana Pérez, Teresa A1 - Völzke, Holger A1 - Wolff, Dietmar A1 - Zencker, Uwe T1 - Cladding considerations at BAM regarding extended storage spent fuel N2 - With the clear expectation of the need for extending spent fuel storage in Germany beyond the initial license period of maximum 40 years additional material data and knowledge about the long term performance and integrity of casks and internals like fuel rods will be required to meet major safety goals and regulatory requirements. Based on a broad knowledge base about fuel cladding behavior, degradation mechanisms and related potential failure mechanisms, e. g. induced by reoriented Hydride precipitation, as illustrated in this paper, a specific gap analyses for the German situation regarding fuel conditions and cladding materials should identify the specific knowledge gaps to be addressed and closed in the near future. This is of specific interest as all spent fuel assemblies are going to be transferred to dry cask storage with the next decade and as a consequence of the German nuclear phase-out decision. Within several decades, BAM as a Federal materials research institute gathered a broad range of expertise in the safety evaluation of materials, components and casks under operational and accidental thermal and mechanical conditions. This paper elucidates selected Basic considerations regarding technical and scientific knowledge about the long term aging performance and potential failure mechanisms of fuel cladding materials. Under consideration of the national R&D funding policy which has been adapted to the extended interim storage or pre-disposal needs and the competences of BAM, its future R&D strategy is explained and some R&D objectives have already been identified. BAM will continue and expand ist engagement in the area of investigating fuel cladding material behavior in the long term and developing validated simulation and analyses tools in collaboration with national and international partners. R&D outcomes shall improve the knowledge-base to close identified knowledge gaps in the area of demonstrating fuel cladding integrity and to provide crucial information with regard to future safety assessments for the extended interim spent fuel storage. T2 - 16th International High -Level Radioactive Waste Management Conference (IHLRWM 2017) CY - Charlotte, NC, USA DA - 09.04.2017 KW - Spent fuel KW - Storage KW - Fuel cladding PY - 2017 SP - 718 EP - 725 AN - OPUS4-40412 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Jan P. A1 - Götschel, S. A1 - Weiser, M. A1 - Maierhofer, Christiane T1 - Thermografie mit optimierter Anregung für die quantitative Untersuchung von Delaminationen in kohlenstofffaserverstärkten Kunststoffen N2 - Da kohlenstofffaserverstärkte Kunststoffe (CFK) in anspruchsvollen sicherheitsrelevanten Einsatzgebieten wie im Automobilbau und in der Luftfahrt eingesetzt werden, besteht ein zunehmender Bedarf an zerstörungsfreien Prüfmethoden. Ziel ist die Gewährleistung der Sicherheit und Zuverlässigkeit der eingesetzten Bauteile. Aktive Thermografieverfahren ermöglichen die effiziente Prüfung großer Flächen mit hoher Auflösung in wenigen Arbeitsschritten. Ein wichtiges Teilgebiet der Prüfungen ist die Ortung und Charakterisierung von Delaminationen, die sowohl bereits in der Fertigung als auch während der Nutzung eines Bauteils auftreten können, und dessen strukturelle Integrität schwächen. In diesem Beitrag werden CFK-Strukturen mit künstlichen und natürlichen Delaminationen mit Hilfe unterschiedlich zeitlich modulierter Strahlungsquellen experimentell untersucht. Verwendet werden dabei Anregungen mit Blitzlampen und mit frequenzmodulierten Halogenlampen. Mittels Filterfunktionen im Zeit- und Frequenzbereich wird das Kontrast-zu-Rausch-Verhältnis (CNR) der detektierten Fehlstellen optimiert. Verglichen werden anschließend die Nachweisempfindlichkeit, das CNR und die Ortsauflösung der zu charakterisierenden Delaminationen für die unterschiedlichen Anregungs- und Auswertungstechniken. Ergänzt werden die Experimente durch numerische Simulationen des dreidimensionalen Wärmetransportes. T2 - DGZfP Jahrestagung 2017 CY - Koblenz, Germany DA - 22.05.2017 KW - CFK KW - Contrast Noise Ratio KW - Lock-in Thermografie KW - Gepulste Thermografie KW - Kurzzeit-Fouriertransformation PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-404276 SN - 978-3-940283-85-6 VL - DGZfP BB 162 SP - Mi.1.A.4, 1 EP - 11 AN - OPUS4-40427 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Axel A1 - Becker, Roland A1 - Braun, Ulrike A1 - Dorgerloh, Ute T1 - Einfluss der Alterung auf das Sorptionsverhalten von Mikroplastik, eine Laborstudie mit BTEX und Etherverbindungen N2 - Die Präsenz von Mikroplastik in aquatischen Ökosystemen ist ein globales Problem und steht zunehmend im Fokus der Öffentlichkeit. In mehreren Studien konnten Anreicherungen hydrophober, organischer Schadstoffe an MP nachgewiesen werden. Der Einfluss des Alterungszustandes der MP-Partikel auf das Sorptionsverhalten von hydrophoben organischen Substanzen ist nicht hinreichend geklärt. Ziel der vorliegenden Arbeit war die Untersuchung des Sorptionsverhaltens von Schadstoffen mit Bedeutung für limnische Gewässer an künstlich gealterten Partikeln relevanter Polymere. Das Modell verwendete die Aromaten Benzol, Toluol, Ethylbenzol und Xylol (BTEX) sowie Etherverbindungen. Diese Substanzen sind oder waren Bestandteile in unterschiedlichen Kraftstoffen und finden sich daher in vielen aquatischen Ökosystemen weltweit. Als Sorbentien kamen teilkristallines Polypropylen (PP) und amorphes Polystyrol (PS) in Form von Industriepellets zum Einsatz. Die Pellets wurden jeweils sowohl unbehandelt als auch mittels UV-Bestrahlung künstlich gealtert verwendet und mikroskopisch sowie mittels XPS, FTIR und DSC charakterisiert. Die Alterung führte bei PS zu einer verringerten Sorptionskapazität, während bei PP keine Veränderung im Sorptionsverhalten beobachtet wurde. T2 - Wasser 2017 - Jahrestagung der Wasserchemischen Gesellschaft CY - Donaueschingen, Germany DA - 22.05.2017 KW - Mikroplastik KW - Organische Schadstoffe KW - Sorption KW - Polypropylen Polystyrol PY - 2017 SN - 978-3-947197-01-9 SP - 1 EP - 606 PB - Gesellschaft Dt. Chemiker AN - OPUS4-40447 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - John, Sebastian A1 - Schadow, Florian T1 - Sensitivitätsanalyse des Eigenspannungszustandes in Composite-Druckgefäßen mittels Modalanalyse N2 - Auf Grund ihrer hohen spezifischen Festigkeit sowie des damit einhergehenden Gewichtsvorteils kommt es bei der Auslegung von Druckgefäßen vermehrt zum Einsatz von faserverstärkten Kunststoffverbunden. Im Rahmen eines Forschungsprojektes an der Bundesanstalt für Materialforschung und –prüfung (BAM) wird das Alterungsverhalten von Atemluftflaschen in Verbundbauweise untersucht, um künftig genauere Aussagen zur Abschätzung der Lebensdauer geben zu können. Gegenstand der hier aufgezeigten Untersuchungen bilden dabei Typ-III Druckgefäße mit metallischen Liner und einer kohlefaserverstärkten Armierung. Als wichtiger, der Betriebsfestigkeit zugrunde legender Parameter wurden Druckeigenspannungen im Aluminium-Liner ausgemacht, welche fertigungsseitig zur Steigerung der Lastwechselfestigkeit in die Druckgefäße induziert werden. Ziel ist es, mit Hilfe einer Modalanalyse die aufgezeigten inneren Spannungsverhältnisse durch eine genaue Betrachtung der modalen Parameter zu identifizieren und zu bewerten. Durch den Aufbau eines Finite-Elemente Modells und einer anschließenden Sensitivitätsanalyse der Fertigungsparameter werden zunächst Potential und Aussagekraft des Analyseverfahrens geprüft und bewertet. Anschließend erfolgt eine Eingrenzung relevanter Schwingformen sowie eine Abschätzung zu erwartender spannungsabhängiger Änderungen entsprechender modaler Kennwerte. Durch die Entwicklung und den Aufbau eines geeigneten Prüfstandes werden, darauf aufbauend, im Rahmen einer Betriebsschwingungsanalyse erste Messungen an Atemluftflaschen unterschiedlicher Alterungs- und Schädigungsstufen durchgeführt. Durch einen Vergleich mit Simulationsergebnissen und Erkenntnissen aus alternativ durchgeführten Eigenspannungsmessungen erfolgt abschließend eine kritische Bewertung der experimentell gewonnenen Ergebnisse. T2 - 43. Jahrestagung für Akustik (DAGA 2017) CY - Kiel, Germany DA - 06.03.2017 KW - Modalanalyse KW - Composite-Druckgefäße KW - Eigenspannungen PY - 2017 SN - 978-3-939296-12-6 SP - 1277 EP - 1281 AN - OPUS4-39896 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wille, Frank A1 - Linnemann, Konrad A1 - Ballheimer, Viktor A1 - Rolle, Annette T1 - Assessment approaches of mechanical behavior of SNF under transport package test conditions N2 - German packages for the transport of spent nuclear fuel are assessed with respect to specific transport conditions which are defined in the safety regulations of the International Atomic Energy Agency. In general, gastight fuel rods constitute the first barrier of the containment system. The physical state of the spent fuel and the fuel rod cladding as well as the geometric configuration of the fuel assemblies are important inputs for the evaluation of the package safety under transport conditions. The objective of this paper is to discuss the methodologies accepted by German authority BAM for the evaluation of spent fuel behavior within the package design approval procedure. Specific test conditions will be analyzed with regard to assumptions to be used in the activity release and criticality safety analysis. In particular the different failure modes of the fuel rods, which can cause release of gas, volatiles, fuel particles or fragments, have to be properly considered in these assumptions. The package as a mechanical system is characterized by a complex set of interactions, e.g. between the fuel rods within the assembly as well as between the fuel assemblies, the basket, and the cask containment. This complexity together with the limited knowledge about the material properties and the variation of the fuel assemblies regarding cladding material, burn-up and the operation history makes an exact mechanical analysis of the fuel rods nearly impossible. The application of sophisticated numerical models requires extensive experimental data for model verification, which are in general not available. The gaps in information concerning the material properties of cladding and pellets, especially for the high burn-up fuel, make the analysis more complicated additionally, and require a conservative approach. In this context some practical approaches based on experiences by BAM within safety assessment of packages for transport of spent fuel will be discussed. Ongoing research activities to investigate SNF mechanical behavior in view of gas and fissile material release under transport loads are presented. T2 - International High-Level Radioactive Waste Management Conference, IHLRWM 2017 CY - Charlotte, NC, USA DA - 09.04.2017 KW - Brennelementverhalten KW - Spent fuel behavior KW - Hüllrohr KW - Kritikalität KW - Aktivitätsfreisetzung KW - Mechanisches Verhalten KW - Cladding KW - Criticality PY - 2017 SP - 472 EP - 475 AN - OPUS4-39898 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Habig, Karl-Heinz T1 - Verschleiß-Schutzschichten auf Stählen N2 - Zu Beginn werden die wichtigsten Verfahren zur Herstellung von Verschleiß-Schutzschichten vorgestellt, wobei die Verfahrenstemperatur als Ordnungskriterium dient. Es folgt eine Zusammenstellung der für das funktionelle Verhalten wichtigen Eigenschaften wie chemische Zusammensetzung, Phasenzusammensetzung, Gefüge, Härte, Härteverlauf u.a. Anschließend werden die Möglichkeiten von Verschleiß-Schutzschichten zur Verminderung des adhäsiven und abrasiven Verschleißes aufgezeigt. Unter Einschluß der Beeinflussung der Festigkeitseigenschaften und des Korrosionsverhaltens wird eine Zusammenstellung der wesentlichen Auswahlkriterien für die Anwendung von Stählen mit Verschleiß-Schutzschichten gegeben. T2 - 2. SURTEC-Kongress : International Congress for Surface Technology CY - Berlin PY - 1983 SN - 3800713284 SP - 301 EP - 308 PB - VDE-Verlag GmbH CY - Berlin AN - OPUS4-39676 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rolle, Annette A1 - Neumeyer, Tino A1 - Droste, Bernhard T1 - Design Approval of Special Form Radioactive Material- Important Aspects N2 - The design of a special form radioactive material has to resist a severe transport accident without undue loss or dispersal of radioactive material. Safety assessment by authorities competent for design approval has to include besides the required test program (impact, percussion, bending and heat test) also the evaluation of the quality management system for design, manufacture, testing, documentation, use, maintenance and inspection. These quality assurance measures have to assure that every specimen of the approved design is produced in the same verified quality and every specimen must be able to survive the severe mechanical and thermal tests without undue loss or dispersal of radioactive material at any time of its working life. All important aspects in the design approval procedure by BAM as the competent authority for approvals of special form radioactive material in Germany are summarized in a guideline published in 2014. This paper will give additional explanations to some aspects in safety assessment, e.g.: the applicability of leak test methods and the need to consider ageing aspects. T2 - PATRAM 2016 CY - Kobe, Japan DA - 18.09.2016 KW - Transport KW - Radioactive material KW - Safety PY - 2016 SP - Paper 4004-22 AN - OPUS4-39912 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Komann, Steffen A1 - Wille, Frank A1 - Schönfelder, Thorsten T1 - German concept to ensure transportability of SNF packages after interim storage N2 - In Germany the concept of dry interim storage of spent fuel in dual purpose metal casks is implemented, currently for periods of up to 40 years. The casks being used have an approved transport package design in accordance with the international IAEA transport regulations as well. The storage of spent nuclear fuel and high-level waste in dual purpose casks (DPC) is related with the challenge of maintaining safety for transportation over several decades of storage. Besides consideration of aging mechanisms by appropriate design, material selection and operational controls to assure technical reliability by aging management measures, an essential issue is the continuous control and update of the DPC safety case. Not only the technical objects are subject of aging but also the safety demonstration basis is subject of “aging” due to possible changes of regulations, standards and scientific/technical knowledge. To ensure a safe transport in future to a destination which is not known yet (because of not yet existing repository sites) periodical reviews of the Package Design Safety Report (PDSR), in connection with periodic renewals of package design approval certificates, have to be carried out. T2 - International High-Level Radioactive Waste Management Conference, IHLRWM 2017 CY - Charlotte, NC, USA DA - 09.04.2017 KW - Dual purpose casks KW - Interim storage KW - Transportability PY - 2017 SP - 476 EP - 481 AN - OPUS4-39919 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Malow, Marcus A1 - Michael-Schulz, Heike A1 - Salg, S. A1 - Schomäcker, R. T1 - Der Einfluss hohen Umgebungsdrucks auf Deflagrationen N2 - Das Deflagrationsverhalten von Feststoffen unter atmosphärischen Bedingungen wurde in der Vergangenheit eingehend untersucht. Standardmäßig wird die Deflagrationsprüfung in einem offenen System durchgeführt. Aber auch in geschlossenen Systemen ist die Deflagrationsprüfung durchführbar und sie liefert Ergebnisse, die mit den Standardmethoden vergleichbar sind. Darüber hinaus bietet die Prüfung in einem geschlossenen System den Vorteil, nicht nur die Temperatur, sondern auch den Druck messen und für die Beschreibung des Deflagrationsverlaufs heranziehen zu können. Auch für die Prüfung in geschlossenen Systemen liegt eine Reihe an experimentellen Ergebnissen vor. Von Klais wurde veröffentlicht, dass die Deflagrationsgeschwindigkeit, beschrieben anhand der Druckanstiegsrate, mit steigendem Druck ansteigt. Vor dem Hintergrund dieser experimentellen Beobachtung wurde interpretiert, dass die Steigerung der Geschwindigkeit ihre Ursache im steigenden Umgebungsdruck findet. Es wurde weiter versucht, einen funktionalen Zusammenhang zwischen Umgebungsdruck und Deflagrationsgeschwindigkeit, ausgedrückt durch die Druckanstiegsrate, herzustellen. Dabei wurde nicht beachtet, dass neben dem Umgebungsdruck noch andere Einflussfaktoren auf die Deflagrationsgeschwindigkeit gegeben sind. Wesentlich ist hierbei die für die Reaktion zur Verfügung stehende Oberfläche, die sich bei einer lokalen, punktförmigen Anzündung mit fortschreitender Reaktionszeit vergrößert. In diesem Beitrag wird der Einfluss des Umgebungsdrucks auf die Deflagrationsgeschwindigkeit systematisch untersucht. Zu diesem Zweck wurden Experimente bei verschiedenen Ausgangsdrücken bis zu 50 bar (abs) durchgeführt. Der Anfangsdruck, also der Druck der vor Beginn eines Experiments im Reaktionsraum herrscht, wurde schrittweise von einem Experiment zum nächsten erhöht. Für die Versuchsreihen wurden zwei Substanzen verwendet: Azodicarbonamid und ein Imidazolderivat. Diese unterscheiden sich in ihrem Deflagrationsverhalten und hinsichtlich der Gasmengenentwicklung. Die durchgeführten Experimente haben gezeigt, dass die Deflagrationsgeschwindigkeit mit steigendem Druck zunimmt. Sowohl die Druckanstiegsrate, als auch die lineare Ausbreitungsrate sind ein gutes Maß dafür. Zwischen den beiden Kenngrößen besteht ein linearer Zusammenhang. Für eine gegebene Geometrie lässt sich die eine Kenngröße aus der anderen berechnen. T2 - 5. Brand- und Explosionsschutztage 2017 CY - Magdeburg, Germany DA - 23.03.2017 KW - Deflagrationen KW - Geschlossenes System KW - Azodicarbonamid KW - Druckanstiegsrate KW - Deflagrationsgeschwindigkeit PY - 2017 SN - 978-3-00-056201-3 SP - 1 EP - 11 AN - OPUS4-39920 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Simone A1 - Rappsilber, Tim A1 - Raspe, Tina T1 - Quantitative Rauchgasanalyse mittels FTIR-Spektroskopie - Anforderungen, Kalibrierung, Reproduzierbarkeit N2 - Die Fourier-Transformations-Infrarot-(FTIR)-Spektroskopie ist eine universell einsetzbare Methode zur Rauchgasanalyse. Um verlässliche quantitative Aussagen zu Rauchgaskonzentrationen treffen zu können, müssen die Anforderungen an die FTIR-Spektrometer, die Probenahme sowie die Kalibrierung entsprechend der ISO 19702:2015 eingehalten werden. Im Rahmen dieses Vortrages werden diese Anforderungen sowie die Kalibrierung näher beschrieben und die Reproduzierbarkeit quantitativer Rauchgasmessungen an drei Beispielen beschrieben. T2 - 5. Brand- und Explosionsschutztage 2017 CY - Magdeburg, Germany DA - 23.03.2017 KW - Rauchgase KW - FTIR-Spektroskopie KW - Brandversuche PY - 2017 SN - 978-3-00-056201-3 DO - https://doi.org/10.978.300/0562013 VL - 2017 SP - 1 EP - 7 PB - Otto-von-Guericke-Universität Magdeburg CY - Magdeburg AN - OPUS4-39931 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rappsilber, Tim A1 - Krüger, Simone T1 - Mischbrandkrippen als Bemessungsbrände zur Unterstützung der Löschwirkung von Druckluftschäumen N2 - Dieser Bericht befasst sich mit Bemessungsbränden zur Untersuchung der Effektivität von Druckluftschäumen. Als normative Brandlast wurden dazu neuentwickelte Mischbrandkrippen verwendet. Diese Krippen sollen den steigenden Anteil synthetischer Materialien im Alltag wiederspiegeln und somit hohe Anforderungen an das Löschmittel stellen. Dieses Paper behandelt die Vorbereitung, Durchführung und Auswertung von zwei Versuchsreihen sowohl im Outdoor- als auch im Indoor-Bereich. Das Paper befasst sich mit der Untersuchung der Effektivität des Löschmittels Druckluftschaum im Vergleich zu Wasser und Netzwasser anhand von acht Outdoor- und vier Indoor-Mischkrippenbränden. Aus den In-door-Brandversuchen gehen zudem Aussagen über die Rauchgaszusammensetzung während des Brandverlaufes hervor. Die Ergebnisse der Bemessungsbrände zeigen, dass Druckluftschäume aufgrund ihrer zeitgleich wirkenden Löscheffekte, unter den getesteten Bedingungen eine bessere Brandunterdrückung erzielen, als herkömmliche Löschmittel. T2 - Brand- und Explosionsschutztage 2017 CY - Magdeburg, Germany DA - 23.03.2017 KW - Mischbrandkrippen KW - Löschwirkung KW - Brandversuche PY - 2017 SN - 978-3-00-056201-3 DO - https://doi.org/10.978.300/0562013 SP - 1 EP - 12 PB - Otto-von-Guericke-Universität Magdeburg CY - Magdeburg AN - OPUS4-39933 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF ED - Maiwald, Michael T1 - Proceedings of 4th European Conference on Process Analytics and Control Technology (EuroPACT 2017) N2 - EuroPACT 2017 is the fourth European Conference on Process Analytics and Control Technology. The conference covered new technologies in process analytics, the implementation of these technologies in various fields and the transformation of data into knowledge. The conference was supported by an exhibition of instrumentation, applications and data evaluation tools. EUROPACT 2017 provided a meeting and a discussion forum for scientists and users of process analytics from academia and industry. The conference programme includes plenary lectures and discussion during poster sessions. The conference took place 10-12 May 2017 in Potsdam (nearby Berlin), Germany. T2 - 4th European Conference on Process Analytics and Control Technology (EuroPACT 2017) CY - Potsdam, Germany DA - 10.05.2017 KW - EuroPACT KW - EuroPACT 2017 KW - Prozessanalytik KW - Process Analytical Technology KW - Process control KW - Control Technology KW - Chemometrics PY - 2017 UR - http://dechema.de/europact17.html SP - 1 EP - 176 CY - Frankfurt a. M. AN - OPUS4-40227 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meyer, Klas A1 - Paul, Andrea A1 - Ruiken, J.-P. A1 - Westad, Frank A1 - Illner, M. A1 - Müller, D. A1 - Esche, E. A1 - Repke, J.-U. A1 - Maiwald, Michael T1 - Online Spectroscopy in Microemulsions – A Process Analytical Approach for a Hydroformylation Mini-plant N2 - Within the Collaborative Research Center InPROMPT a novel process concept for the hydroformylation of long-chained olefins is studied in a mini-plant, using a rhodium complex as catalyst in the presence of syngas. Recently, the hydroformylation in micro¬emulsions, which allows for the efficient recycling of the expensive rhodium catalyst, was found to be feasible. However, the high sensitivity of this multi-phase system with regard to changes in temperature and composition demands a continuous observation of the reaction to achieve a reliable and economic plant operation. For that purpose, we tested the potential of both online NMR and Raman spectroscopy for process control. The lab-scale experiments were supported by off-line GC-analysis as a reference method. A fiber optic coupled probe of a process Raman spectrometer was directly integrated into the reactor. 25 mixtures with varying concentrations of olefin (1-dodecene), product (n-tridecanal), water, n-dodecane, and technical surfactant (Marlipal 24/70) were prepared according to a D-optimal design. Online NMR spectroscopy was implemented by using a flow probe equipped with 1/16” PFA tubing serving as a flow cell. This was hyphenated to the reactor within a thermostated bypass to maintain process conditions in the transfer lines. Partial least squares regression (PLSR) models were established based on the initial spectra after activation of the reaction with syngas for the prediction of unknown concentrations of 1-dodecene and n-tridecanal over the course of the reaction in the lab-scale system. The obtained Raman spectra do not only contain information on the chemical composition but are further affected by the emulsion properties of the mixtures, which depend on the phase state and the type of micelles. Based on the spectral signature of both Raman and NMR spectra, it could be deduced that especially in reaction mixtures with high 1-dodecene content the formation of isomers as a competitive reaction was dominating. Similar trends were also observed during some of the process runs in the mini-plant. The multivariate calibration allowed for the estimation of reactants and products of the hydroformylation reaction in both laboratory setup and mini-plant. T2 - 4th European Conference on Process Analytics and Control Technology (EuroPACT 2017) CY - Potsdam, Germany DA - 10.05.2017 KW - Microemulsions KW - Process Analytical Technology KW - Reaction Monitoring KW - Online NMR Spectroscopy KW - Online Raman Spectroscopy PY - 2017 SP - 64 EP - 64 CY - Frankfurt a. M. AN - OPUS4-40228 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kern, Simon A1 - Guhl, Svetlana A1 - Meyer, Klas A1 - Paul, Andrea A1 - Wander, Lukas A1 - Gräßer, Patrick A1 - Maiwald, Michael T1 - Design and Validation of a Compact NMR Analyser N2 - Monitoring chemical reactions is the key to chemical process control. Today, mainly optical online methods are applied. NMR spectroscopy has a high potential for direct loop process control. Compact NMR instruments based on permanent magnets are robust and relatively inexpensive analysers, which feature advantages like low cost, low maintenance, ease of use, and cryogen-free operation. Instruments for online NMR measurements equipped with a flow-through cell, possessing a good signal-to-noise-ratio, sufficient robustness, and meeting the requirements for integration into industrial plants (i.e., explosion safety and fully automated data analysis) are currently not available off the rack. Intensified continuous processes are in focus of current research. Flexible (modular) chemical plants can produce different products using the same equipment with short down-times between campaigns and quick introduction of new products to the market. In continuous flow processes online sensor data and tight closed-loop control of the product quality are mandatory. If these are not available, there is a huge risk of producing large amounts of out-of-spec (OOS) products. This is addressed in the European Unionʼs Research Project CONSENS (Integrated Control and Sensing) by development and integration of smart sensor modules for process monitoring and control within such modular plant setups. The presented NMR module is provided in an explosion proof housing of 57 x 57 x 85 cm module size and involves a compact 43.5 MHz NMR spectrometer together with an acquisition unit and a programmable logic controller for automated data preparation (phasing, baseline correction) and evaluation. Indirect Hard Modeling (IHM) was selected for data analysis of the low-field NMR spectra. A set-up for monitoring continuous reactions in a thermostated 1/8” tubular reactor using automated syringe pumps was used to validate the IHM models by using high-field NMR spectroscopy as analytical reference method. T2 - 4th European Conference on Process Analytics and Control Technology (EuroPACT 2017) CY - Potsdam, Germany DA - 10.05.2017 KW - Prozessanalytik KW - Reaction Monitoring KW - Online NMR Spectrsocopy KW - Process Analytical Technology KW - Industrie 4.0 KW - EuroPACT PY - 2017 SP - 72 EP - 73 CY - Frankfurt a. M. AN - OPUS4-40229 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Illner, M. A1 - Meyer, Klas A1 - Paul, Andrea A1 - Esche, E. A1 - Maiwald, Michael A1 - Repke, J.-U. T1 - Operation and Optimal Control of Multiphase Systems – Hydroformylation in Microemulsions on the Mini-plant Scale N2 - Hydroformylation of short-chained olefins has been established as a standard industrial process for the production of C2 to C6 aldehydes. Using aqueous solutions of transition metal complexes these processes are carried out homogeneously catalyzed. A biphasic approach allows for highly efficient catalyst recovery. Regarding renewable feedstocks, the hydroformylation of long-chained alkenes (> C10) in a biphasic system, using highly selective rhodium catalysts has yet not been shown. Therefore, the Collaborative Research Center SFB/TR 63 InPROMPT develops new process concepts, involving innovative tuneable solvent systems to enable rather difficult or so far nonviable synthesis paths. One possible concept is the hydroformylation of long-chained alkenes in microemulsions. For this, a modular mixer-settler concept was proposed, combining high reaction rates and efficient catalyst recycling via the application of technical grade surfactants. The feasibility of such a concept is evaluated in a fully automated, modular mini-plant system within which the characteristics of such a multiphase system pose several obstacles for the operation. Maintaining a stable phase separation for efficient product separation and catalyst recycling is complicated by small and highly dynamic operation windows as well as poor measurability of component concentrations in the liquid phases. In this contribution, a model-based strategy is presented to enable concentration tracking and phase state control within dynamic mini-plant experiments. Raman spectroscopy is used as an advanced process analytical tool, which allows for online in-situ tracking of concentrations. Combined with optical and conductivity analysis optimal plant trajectories can be calculated via the solution of dynamic optimization problem under uncertainty. Applying these, a stable reaction yield of 40 % was achieved, combined with an oil phase purity of 99,8 % (total amount of oily components in the oil phase) and catalyst leaching below 0.1 ppm. T2 - 4th European Conference on Process Analytics and Control Technology (EuroPACT 2017) CY - Potsdam, Germany DA - 10.05.2017 KW - Hydroformylation KW - Micoemulsion KW - Dispersion KW - Process Analytical Technology KW - Mini-plant KW - EuroPACT PY - 2017 SP - 92 EP - 92 CY - Frankfurt a. M. AN - OPUS4-40230 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Müller, C. A1 - Baumann, O. A1 - Modersohn, W. A1 - Halle, T. T1 - Influence of the post-weld surface treatment on the corrosion resistance of the duplex stainless steel 1.4062 N2 - The duplex stainless steel 1.4062 (X2CrNiN22-2) is used as alternative material to austenitic stainless steels in the construction industry. The corrosion resistance of welded seams is influenced by the base material, the weld filler material, the welding process and also by the final surface treatment. The scale layer next to the weld seam can be removed by grinding, pickling, electro-polished or blasting depending on the application and the requested corrosion resistance. Blasted surfaces are often used in industrial practice due to the easier and cheaper manufacturing process compared to pickled or electro-polished surfaces. Furthermore blasting with corundum-grain is more effective than blasting with glass-beads which also lower the process costs. In recent years, stainless steel surfaces showed an unusually high susceptibility to pitting corrosion after grinding with corundum. For this reason, it is now also questioned critically whether the corrosion resistance is influenced by the applied blasting agent. This question was specifically investigated by comparing grinded, pickled, corundum-grain- and glass-bead-blasted welding seams. Results of the SEM analyses of the blasting agents and the blasted surfaces will be presented and correlated with the different performed corrosion tests (potential measurement, KorroPad-test and pitting potential) on welding seams with different surface treatments. T2 - 19. Werkstofftechnisches Kolloquium Chemnitz CY - Chemnitz, Germany DA - 16.03.2017 KW - Corrosion resistance KW - Duplex stainless steel KW - Influence PY - 2017 SN - 978-3-00-055705-7 SN - 1439-1597 VL - 61 SP - 172 EP - 180 PB - Schriftreihe Werkstoffe und werkstofftechnische Anwendungen CY - Chemnitz AN - OPUS4-40168 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Dieck, S. A1 - Kromm, Arne A1 - Halle, T. T1 - Reversed austenite for enhancing ductility of martensitic stainless steel N2 - The novel heat treatment concept, “quenching and partitioning” (Q&P) has been developed for high strength steels with enhanced formability. This heat treatment involves quenching of austenite to a temperature between martensite start and finish, to receive a several amount of retained austenite. During the subsequent annealing treatment, the so called partitioning, the retained austenite is stabilized due to carbon diffusion, which results in enhanced formability and strength regarding strain induced austenite to martensite transformation. In this study a Q&P heat treatment was applied to a Fe-0.45C-0.65Mn-0.34Si-13.95Cr stainless martensite. Thereby the initial quench end temperature and the partitioning time were varied to characterize their influence on microstructural evolution. The microstructural changes were analysed by dilatometer measurements, X-ray diffraction and scanning electron microscopy, including electron back-scatter diffraction. Compression testing was made to examine the mechanical behaviour. It was found that an increasing partitioning time up to 30 min leads to an enhanced formability without loss in strength due to a higher amount of stabilized retained and reversed austenite as well as precipitation hardening. T2 - 19. Werkstofftechnisches Kolloquium Chemnitz CY - Chemnitz, Germany DA - 16.03.2017 KW - Martensitic stainless steel KW - Reversed austenite PY - 2017 SN - 978-3-00-055705-7 SN - 1439-1597 VL - 61 SP - 308 EP - 315 PB - Schriftreihe Werkstoffe und werkstofftechnische Anwendungen CY - Chemnitz AN - OPUS4-40169 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Guhl, Svetlana A1 - Kern, Simon A1 - Meyer, Klas A1 - Gräßer, Patrick A1 - Wander, Lukas A1 - Maiwald, Michael T1 - Online NMR Spectroscopy for Process Monitoring in Intensified Continuous Production Plants N2 - Process analytical techniques are extremely useful tools for chemical production and manufacture and are of particular interest to the pharmaceutical, food and (petro-) chemical industries. Today, mainly optical online methods are applied. NMR spectroscopy has a high potential for direct loop process control. Compact NMR instruments based on permanent magnets are robust and relatively inexpensive analysers, which feature advantages like low cost, low maintenance, ease of use, and cryogen-free operation. Instruments for online NMR measurements equipped with a flow-through cell, possessing a good signal-to-noise-ratio, sufficient robustness, and meeting the requirements for integration into industrial plants (i.e., explosion safety and fully automated data analysis) are currently not available off the rack. A major advantage of NMR spectroscopy is that the method features a high linearity between absolute signal area and sample concentration, which makes it an absolute analytical comparison method which is independent of the matrix. This is an important prerequisite for robust data evaluation strategies within a control concept and reduces the need for extensive maintenance of the evaluation model over the time of operation. Additionally, NMR spectroscopy provides orthogonal, but complimentary physical information to conventional, e.g., optical spectroscopy. It increases the accessible information for technical processes, where aromatic-toaliphatic conversions or isomerizations occur and conventional methods fail due to only minor changes in functional groups. As a technically relevant example, the catalytic hydrogenation of 2-butyne-1,4-diol and further pharmaceutical reactions were studied using an online NMR sensor based on a commercially available low-field NMR spectrometer within the framework of the EU project CONSENS (Integrated Control and Sensing). T2 - 4th European Conference on Process Analytics and Control Technology (EuroPACT 2017) CY - Potsdam, Germany DA - 10.05.2017 KW - Process Monitoring KW - CONSENS KW - Online NMR Spectroscopy KW - Process Analytical Technology KW - Process control KW - Hydration KW - EuroPACT PY - 2017 SP - 103 EP - 103 CY - Frankfurt a. M. AN - OPUS4-40231 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mishra, K. B. A1 - Wehrstedt, Klaus-Dieter A1 - Krebs, Holger T1 - Prediction of overpressure in buried gas pipeline explosions N2 - The explosion and fire incidents with buried gas pipelines are increasing globally e.g. San Bruno (USA, 2010), East Godavari (India, 2014) and Ludwigshafen (Germany, 2014) are only a few to quote. There are a number of parameters involved behind the occurrence of these incidents such as human mistake, intended efforts leading to major or minor leak, explosion due to depressurization, crater formation, spill of gaseous fuel in the nearby regions and pool/jet/crater fires. In continuation to [3] these parameters are investigated for Ludwigshafen incident in the present work. The semi-empirical and advanced CFD (Computational Fluid Dynamics) based models are utilized to assess the damages caused by the explosion overpressures. Recommendations are also provided on minimum safety distance to be considered for such pipelines to avoid/foresee/mitigate similar hazards in future. T2 - 5. Brand- und Explosionsschutztage 2017 CY - Magdeburg, Germany DA - 23.03.2017 KW - Buried gas pipeline KW - Explosion KW - Overpressure KW - CFD-Model KW - Safety distance PY - 2017 SN - 978-3-00-056201-3 DO - https://doi.org/10.978.300/0562013 SP - 1 EP - 8 AN - OPUS4-40193 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Feldkamp, Martin A1 - Erenberg, Marina A1 - Nehrig, Marko A1 - Bletzer, Claus A1 - Musolff, André A1 - Wille, Frank A1 - Schönfelder, Thorsten T1 - Aspects of assessment of packages with wood filled impact limiters during fire tests N2 - Packages for the transport of radioactive material are often equipped with impact limiters consisting of wood, encapsulated by steel sheets. These impact limiters shall ensure that the transport casks meet the mechanical and thermal IAEA regulatory test requirements. According to the accident conditions of transport it is mandatory to expose the specimens to a cumulative effect by mechanical and thermal impacts. The mechanical tests consist of a free drop from 9 m onto a flat unyielding target and a 1 m drop onto a puncture bar. After damage caused by mechanical test sequences the package has to withstand a severe fire scenario. Corresponding to the IAEA advisory material it is required that the impact attitudes for the 9 m drop test and for the puncture test have to be such as to produce maximum damage, taking into account the thermal test. Moreover, any damage, which would give rise to increased radiation or loss of containment or affect the confinement system after the thermal test, should be considered. During and following the thermal test, the specimen shall not be artificially cooled and any combustion of materials of the package shall be permitted to proceed naturally. Different works from the French Institute for Radiological Protection and Nuclear Safety (IRSN) and BAM show that additional energy supply from a pre-damaged impact limiter to the cask could occur. This effect should be considered within the safety assessment of the containment. Thermal effects at the closure system of the cask, which might result in an elevated activity release, have to be excluded. BAM conducted small scale tests with wood filled metal buckets showing continuing combustion processes during the cooling down phase. These test results are presented. As not much is known about smouldering processes in wood filled impact limiters, it is highly complex to define pre-damage of impact limiters, which are conservative, regarding the maximum damaging energy flow from the impact limiter to the containment system. More research has to be done to develop models to examine the effects of smouldering impact limiters on the containment of packages for the transport of radioactive material. Aspects of assessment and its difficulties are shown. BAM as a competent authority for the approval of transport casks for radioactive material in Germany operates the test facilities to examine the issue of mechanical damage, combustion and heat transfer for such kind of package systems. For this purpose the knowledge from real drop tests with casks of a mass partly over 100 tons was transferred to a test application. A thermal test will take place with a wood filled test specimen with a diameter of about 2.3 meters. The aim is to understand the phenomena of smouldering under the consideration of relevant regulatory boundary conditions. The process of smouldering is described with regard to the requirements in the thermal assessment of safety of packages for the transport of radioactive material. Requirements concerning the pre-damage of packages for the maximum damage of impact limiters are discussed. Parameters influencing the smouldering process are identified. T2 - WM 2017 Conference CY - Phoenix, AZ, USA DA - 05.03.2017 KW - Fire test KW - Wood KW - Combustion KW - Smouldering KW - Smoldering KW - Impact limiter KW - Shock absorber KW - Thermal test KW - IAEA PY - 2017 SN - 978-0-9828171-6-2 SP - 1 AN - OPUS4-40157 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kind, Thomas T1 - Amplitudes variation of GPR rebar reflection due to the influence of concrete aggregate scattering N2 - Dense GPR measurements of rebar reflection amplitudes Show relative variations, which can be in the order of more than 10% - 20%. Former investigations demonstrated that these variations are caused by the heterogeneity of concrete, i.e. due to the inclusion of aggregates in concrete. These amplitude variations make it difficult to analyse single reflection amplitudes in order to determine the rebar diameter or to estimate the concrete deterioration state. In a systematic study we have quantified the statistical variation of the rebar reflection amplitude for concrete covers of 6 cm, 9 cm, 12 cm, 15 cm and 18 cm, for two different grading curves and for the rebar diameters 12 mm and 28 mm. Also the influence of the wavelength has been investigated by using antennas with different centre frequencies in relation to the aggregate size. The results are discussed with regard to a quantitative amplitude evaluation of GPR measurements and also the potential of using these variations for a characterization of concrete material properties. T2 - NDT-CE 2015 - International symposium non-destructive testing in civil engineering CY - Berlin, Germany DA - 15.09.2015 KW - Ground penetrating radar KW - Concrete KW - Rebar KW - Aggregate scattering PY - 2015 UR - http://www.ndt.net/?id=18402 SN - 1435-4934 VL - 20 IS - 11 SP - 412 EP - 420 PB - NDT.net CY - Kirchwald AN - OPUS4-40007 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Linnemann, Konrad A1 - Ballheimer, Viktor A1 - Sterthaus, Jens A1 - Rolle, Annette A1 - Wille, Frank A1 - Nasyrow, R. A1 - Papaioannou, D. A1 - Vlassopoulos, E. A1 - Rondinella, V. T1 - Analysis of parameters affecting the bending behavior of spent fuel rods N2 - Transport packages for spent nuclear fuel have to be assessed with respect to specific transport conditions which are defined in the regulations of the International Atomic Energy Agency. The physical state of the spent fuel and the fuel rod cladding as well as the geometric configuration of the fuel assemblies are important inputs for the evaluation of the package capabilities under these conditions. Cracks or failures in the fuel rod cladding can cause the release of gas, volatiles or fuel particles into the cavity. The amount of substances in the cavity has to be considered in the assessment of the activity release and criticality safety. The mechanical analysis of the compound system formed by the fuel rod cladding and the spent fuel pellets is very difficult due to the limited knowledge of the material properties and the insufficient understanding of the interaction between pellets and cladding and between adjacent pellets. The variation of fuel assembly properties regarding cladding material, burn-up and the history of usage makes reliable predictions of the fuel rod behavior even harder. For a better understanding about the behavior of spent fuel rods, JRC-ITU and BAM have started a joint research project. In this context, JRC-ITU has developed a test device which allows quasi-static 3-point-bending test on fuel rod segments in the hot cell. The loads are applied with respect to the boundary conditions of the activity release assessment. This paper deals with the numerical calculation of a single fuel rod segment under bending load. The aim is to identify the governing mechanical parameters by the variation of constitutive assumptions, contact conditions, inner constraints, etc. This knowledge helps for the interpretation of the experimental results. Furthermore, the improved understanding about the behavior of the cladding-pellets system will be beneficial for the assessment of spent fuel transport conditions. T2 - PATRAM 2016 - 18th International symposium on the packaging and transportation of radioactive materials CY - Kobe, Japan DA - 18.09.2016 KW - Transport packages KW - Finite element methods KW - Spent fuel assessment PY - 2016 SP - Paper 2012, 1 AN - OPUS4-40000 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nasyrow, R. A1 - Papaioannou, D. A1 - Rondinella, V. A1 - Vlassopoulos, E. A1 - Linnemann, Konrad A1 - Ballheimer, Viktor A1 - Sterthaus, Jens A1 - Rolle, Annette A1 - Wille, Frank A1 - Caruso, St. T1 - Bending test device for mechanical integrity studies of spent nuclear fuel rods N2 - This paper presents data obtained from experiments performed using a bending test set-up developed at the Joint Research Centre (JRC) – Karlsruhe, for spent fuel segment testing. Adjustable sample holders, loading modes and other experimental conditions can be im- plemented in the experiments to study the effects of different deformation ranges up to cladding failure. The experimental set-up has been adapted to hot cell remote controlling and has a modular configuration, which allows manual and motor-driven loading option. The device has been calibrated on hydrogenated, unirradiated cladding tube segments filled with alumina pellets. The final application of present set-up is to test non-defueled spent fuel rod segments, pressurized to the original spent fuel rod pressure level. The range of applicability of this device, the scope of the experimental program and the first results from actual bending tests will be discussed. T2 - PATRAM 2016 - 18th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Kobe, Japan DA - 18.09.2016 KW - Hot cell testing KW - Spent fuel assessment KW - Transport packages PY - 2016 SP - Paper 6023, 1 AN - OPUS4-40002 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Trela, C. A1 - Kind, Thomas A1 - Günther, Martin T1 - Ground penetrating radar in reflection vs transmission mode for void detection in concrete structures N2 - The concreting of prefabricated concrete structures can lead to insufficient bonding or even to remaining cavities. Honeycombs (aggregate clusters without cement) represent potential weakening of the structure and need to be detected non-destructively. In our study we tested the capability of ground penetrating radar (GPR)techniques for this purpose. We applied GPR in reflection mode and zero-offset profiling (ZOP) Transmission mode on a precast concrete twin wall with built-in honeycombs. GPR measurements were performed as twochannel measurement with ground coupled antennas with centre frequencies of 1.5 GHz and 2.6 GHz mounted to an automated scanner system. Our findings show that ZOP transmission measurements are a more efficient method to detect voids in reinforced concrete structures compared to reflection mode measurements. This holds for both the effort needed for the measurement and the evaluation as well as the validity of the data. Honeycombs (basically representing voids) are usually characterized by strongly reduced amplitudes and earlier arrivals of the transmitted wave. T2 - NDT-CE 2015 - International symposium non-destructive testing in civil engineering CY - Berlin, Germany DA - 15.09.2015 KW - Ground penetrating radar KW - Reflection KW - Transmission KW - Reinforced concrete KW - Prefabricated wall KW - Void detection PY - 2015 SN - 1435-4934 SP - 324 EP - 344 PB - Technische Universität Berlin / Bundesanstalt für Materialforschung und -prüfung CY - Berlin, Germany AN - OPUS4-40006 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Blankenhagel, Paul A1 - Wehrstedt, Klaus-Dieter A1 - Mishra, K. B. A1 - Steinbach, J. T1 - Prediction of organic peroxide fireball characteristics using CFD simulation N2 - Single and multiple fireballs of di-tert-butyl peroxide are numerically investigated using ANSYS CFX. Calculations contain varying inlet conditions, scale-adaptive shear stress turbulence modeling and one-step combustion reaction on a three-dimensional hexahedral mesh. Time-resolved flame temperatures, sizes and thermal radiation are compared to experimental results. There, fireballs were generated by fire engulfment of steel drums containing 200 l substance. After a vigorous burning, the remaining peroxide forms single and multiple fireballs involving 10 % to 20 % of the initial amount. The comparison of all simulations and two selected experiments show the special numerical treatment required for organic peroxides. Finally, the numerical predictions of irradiance in 30 m distance to the fire show a good agreement for both experiments. This proves the use of CFD as an appropriate method for thermal hazard assessment and the prediction of safety distances for organic peroxide fireballs. T2 - 8th European Combustion Meeting 2017 CY - Dubrovnik, Croatia DA - 18.04.2017 KW - Organic peroxide KW - DTBP KW - Fireball KW - Steel drum KW - Simulation PY - 2017 SN - 978-953-59504-1-7 AN - OPUS4-39992 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Blankenhagel, Paul A1 - Wehrstedt, Klaus-Dieter A1 - Mishra, K. B. A1 - Steinbach, J. T1 - Fireballs as a possible hazard scenario of organic peroxides in steel drums N2 - To simulate a full fire engulfment during transportation or storage a closed removable head steel drum filled with 200 l Di-tert-butyl peroxide (DTBP) is subjected to a wood fire. Due to the enormous heat flux and the exothermic self-decomposition large flames arise and finally multiple fireballs occur. The fireballs consume up to 20 % of the total mass (20 % equals to 31 kg). They are characterized by high surface emissive power and large flames associated with high thermal radiation causing spontaneous ignition of objects in the surrounding. The measured sizes of the DTBP fireballs are smaller compared to the results of the general equations for hydrocarbon fireballs. Because these equations are recommended by the Health and Safety Executive (UK) to be applicable for organic peroxides explicit comparisons of DTBP with LPG, diesel and gasoline concerning the characteristics of fireballs are carried out. Also the burning time is compared and confirms a faster combustion of the peroxide. Moreover, the development of size and emissive power for DTBP and diesel fireballs are compared in a normalized graph. The results provide the assumption that new empirical models are required to be developed for hazard assessment of organic peroxide fireballs. T2 - 5. Brand- und Explosionsschutztage 2017 CY - Magdeburg, Germany DA - 23.03.2017 KW - Organic peroxide KW - DTBP KW - Fireball KW - Steel drum KW - Simulation PY - 2017 SN - 978-3-00-056201-3 DO - https://doi.org/10.978.300/0562013 VL - 2017 SP - 1 EP - 9 PB - Otto-von-Guericke-Universität CY - Magdeburg AN - OPUS4-39994 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gundlach, Dietrich T1 - Consequences of adjustment errors on the quality of colorimeter heads for colour difference meters N2 - Tristimulus Colorimeters have to comply the condition of Luther. That means that the spectral responsivities of the Instrument must correspond exactly with the colour matching functions of the CIE Standard Observer. In Praxis adjustment errors in simulating the CIE Colour matching functions are unavoidable. These systematic errors determine whether a tristimulus Colorimeter can be taken as an absolute measuring device or only as a relative measuring colour difference meter. A method is proposed to characterize the guality of an Adjustment by means of an expected error of colour measurement. PY - 1983 SP - D201/1 EP - D201/3 AN - OPUS4-39971 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stajanca, Pavol A1 - Krebber, Katerina ED - Webb, D. J. ED - Scully, P. ED - Sugden, K. T1 - Radiation induced attenuation in perfluorinated polymer optical fibres for dosimetry applications N2 - Real-time measurement of radiation-induced attenuation (RIA) in a commercial perfluorinated polymer optical fibre (PF-POF) is performed with regard to on-line Radiation monitoring purposes. Spectral character and dose dependence of fibre’s RIA is measured in 450-900 nm spectral region. Fibre exhibited high radiation sensitivity in the visible region with strong increase towards the UV wavelengths. Good linearity and high sensitivity reaching up to 130 dBm-1/kGy was demonstrated in the VIS region for a low-dose range. This of-the-shelf PF-POF could be therefore interesting for on-line remote dosimetry applications. T2 - POF 2016: 25th International Conference on Plastic Optical Fibres CY - Birmingham, UK DA - 13.09.2016 KW - Perfluorinated polymer optical fibers KW - Gamma radiation monitoring KW - Radiation induced attenuation PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-403221 SN - 978-1-85449-408-5 SP - 167 EP - 170 CY - Birmingham AN - OPUS4-40322 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dittrich, Matthias A1 - Kasparek, Eva-Maria A1 - Völzke, Holger T1 - Legacy waste containers for low and intermediate level radioactive waste in Germany - Actual situation and challenges –17070 N2 - Low and intermediate level radio active waste has been produced in Germany for several decades. While a part of the waste had been deposited in the Morleben repository and the Asse mine which have been operated for just a limited period of time, the major amount is conditioned and packaged in temporarily stored waste containers. Those containers are designated for final disposal in the KONRAD repository being currently under construction and expected to start operation in 2022. As a consequence, an assessment of the waste container documentation and safety is strongly needed to receive an approval for the KONRAD repository. This requalification is challenging because those old containers have to meet the same safety requirements as new containers. T2 - WasteManagement Symposia 2017 CY - Phoenix, USA DA - 05.03.2017 KW - Radioactive waste container KW - Konrad KW - Repository PY - 2017 UR - https://www.xcdsystem.com/wmsym/2017/028.html#17070 SP - Paper 17070, 1 EP - 14 AN - OPUS4-40326 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hoffmann, Mathias ED - Kasparek, Eva-Maria ED - Völzke, Holger T1 - Schmiedestahl als neuer Behälterwerkstoff zur Endlagerung von schwach- und mittelradioaktiven Abfällen für das Endlager Konrad T1 - Forged steel as a new container material to the final storage of low- and medium-level radioactive waste for the Konrad repository N2 - Mit diesem Beitrag berichtet die BAM über den Stand der Technik und die bereits existierenden Behälterbauarten für die Lagerung von mittelradioaktiven Abfällen mit Ausblick auf die Vorteile und Anwendungszwecke von Schmiedestahl als bevorzugter Behälterwerkstoff. Aus Sicht der Bundesanstalt für Materialforschung und -prüfung (BAM) wird dargestellt, welche Herausforderungen im Allgemeinen bei der Qualifizierung von Schmiedestahlbehältern existieren und warum diese im Vergleich zu den bislang verwendeten Konstruktionen bevorzugt zur Erfüllung der erhöhten Anforderungen an die Barriereeigenschaften eines Behälters der Abfallbehälterklasse II (ABK II) ausgewählt werden. T2 - Kontec 2017 - 13. Internationales Symposium "Konditionierung radioaktiver Betriebs- und Stilllegungsabfälle" einschließlich 13. Statusbericht des BMBF "Stilllegung und Rückbau kerntechnischer Anlagen" CY - Dresden, Germany DA - 22.03.2017 KW - Schmiedestahl KW - Behälterwerkstoff KW - Endlagerung KW - Abfälle KW - Konrad PY - 2017 SP - Tagungsband, 673 AN - OPUS4-40344 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Casperson, Ralf A1 - Munzke, Dorit A1 - Pohl, Rainer T1 - Wirbelstromprüfung an Composite-Druckgefäßen N2 - Composite-Druckgefäße für den Gefahrguttransport sowie für Wasserstoff- und Erdgasfahrzeuge bestehen aus einem lasttragenden Composite und einer gasdichten, metallischen oder polymeren Barriereschicht (Liner). Zur Untersuchung des Alterungsverhaltens solcher Composite-Druckgefäße wird in der BAM das interdisziplinäre Themenfeldprojekt COD-AGE durchgeführt. Ziel des Projektes ist die Entwicklung von Methoden und Modellen zur Beschreibung und Bestimmung des Alterungsverhaltens von Carbonfaser-Compositen (CFK) am Beispiel von Druckgefäßen, um eine bessere Vorhersage der Alterung und der sicheren Gebrauchsdauer zu ermöglichen. Ein Schwerpunkt in diesem Projekt ist die Bereitstellung geeigneter ZfP-Methoden. Dabei geht es sowohl um versuchsbegleitende Prüfungen, als auch um die mögliche Entwicklung von Prüfeinrichtungen für den späteren praktischen Gebrauch. In diesem Vortrag werden Prüfsysteme und Prüfergebnisse der „konventionellen“ Wirbelstromprüfung vorgestellt. In einem ersten Schritt wurden Versuche an bereits geschädigten Druckgefäßen durchgeführt. Dabei wurden Druckgefäße mit den Materialpaarungen Stahl-CFK, Aluminium-CFK und Kunststoff-CFK untersucht. Die Dicken der CFK-Schichten reichten hierbei von ca. 4 mm bis ca. 8 mm. Anfangs wurden die Gefäße mit verschiedenen Sensoren von außen geprüft. Es konnten sowohl Beschädigungen des metallischen Liners, als auch Strukturen des CFK-Geflechts nachgewiesen werden. In einem zweiten Schritt wurden die Gefäße von innen geprüft. Hierbei bestand die besondere Herausforderung in der Prüfung eines Zylinders von 150 mm Durchmesser durch einen Zugang von nur 15 mm Durchmesser. Mit den bei diesen Vorversuchen optimierten Prüfsystemen wurden dann begleitende Prüfungen bei Alterungsversuchen durchgeführt. In den Alterungsversuchen wurden Druckbehälter mit einem ca. 4 mm dicken Aluminiumliner und ca. 3,5 mm dicker CFK-Ummantelung untersucht. Typisches Einsatzgebiet solcher Flaschen sind Atemschutzgeräte bei der Feuerwehr. Die verschiedenen Prüfsysteme und die mit ihnen erzielten Ergebnisse werden vorgestellt. T2 - DGZfP-Jahrestagung 2017 CY - Koblenz, Germany DA - 22.05.2017 KW - Composite-Druckgefäß KW - Wirbelstromprüfung KW - CFK PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-403577 SN - 978-3-940283-85-6 VL - 162 SP - 1 EP - 9 PB - DGZfP e.V. AN - OPUS4-40357 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bennetts, V.H. A1 - Kucner, T.P. A1 - Schaffernicht, E. A1 - Neumann, Patrick P. A1 - Fan, H. A1 - Lilienthal, A.J. T1 - Probabilistic Air Flow Modelling Using Turbulent and Laminar Characteristics for Ground and Aerial Robots N2 - For mobile robots that operate in complex, uncontrolled environments, estimating air flow models can be of great importance. Aerial robots use air flow models to plan optimal navigation paths and to avoid turbulence-ridden areas. Search and rescue platforms use air flow models to infer the location of gas leaks. Environmental monitoring robots enrich pollution distribution maps by integrating the information conveyed by an air flow model. In this paper, we present an air flow modelling algorithm that uses wind data collected at a sparse number of locations to estimate joint probability distributions over wind speed and direction at given query locations. The algorithm uses a novel extrapolation approach that models the air flow as a linear combination of laminar and turbulent components. We evaluated the prediction capabilities of our algorithm with data collected with an aerial robot during several exploration runs. The results show that our algorithm has a high degree of stability with respect to parameter selection while outperforming conventional extrapolation approaches. In addition, we applied our proposed approach in an industrial application, where the characterization of a ventilation system is supported by a ground mobile robot. We compared multiple air flow maps recorded over several months by estimating stability maps using the Kullback-Leibler divergence between the distributions. The results show that, despite local differences, similar air flow patterns prevail over time. Moreover, we corroborated the validity of our results with knowledge from human experts. T2 - IEEE International Conference on Robotics and Automation (ICRA) CY - Singapore DA - 29.05.2017 KW - Mapping KW - Field Robots KW - Environment Monitoring and Management KW - Aerial Systems KW - Perception and Autonomy PY - 2017 SN - 978-1-5090-4632-4 SP - 1 EP - 7 PB - IEEE AN - OPUS4-40544 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Tschirschwitz, Rico T1 - Entwicklung von Bestimmungsverfahren für Explosionskenngrößen von Gasen und Dämpfen für nichtatmosphärische Bedingungen N2 - Explosionskenngrößen bilden die Grundlage für die Bewertung von Explosionsrisiken und für die Auslegung von Explosionsschutzmaßnahmen. Typische Kenngrößen für Gase und Dämpfe sind Explosionsgrenzen, Sauerstoffgrenzkonzentration (SGK), maximaler Explosionsdruck und maximaler zeitlicher Explosionsdruckanstieg sowie die Zündtemperatur. Explosionskenngrößen sind von der Bestimmungsmethode (z. B. Zündgefäß, Zündquelle, Kriterium für die Entzündung), den Umgebungsbedingungen (z. B. Druck, Temperatur) und dem Oxidator abhängig. Für sicherheitstechnische Betrachtungen im Explosionsschutz müssen die Kenngrößen zuverlässig und vergleichbar sein. Um die Abhängigkeit vom Bestimmungsverfahren zu minimieren, sind diese genormt. Derzeit sind die bestehenden Normen fast ausschließlich für atmosphärische Bedingungen ausgelegt. Viele Prozesse in der chemischen Industrie werden jedoch unter nichtatmosphärischen Bedingungen (erhöhte Drücke, erhöhte Temperaturen, von Luft abweichende Oxidatoren) durchgeführt. Dadurch ergibt sich das Erfordernis, Explosionskenngrößen auch unter nichtatmosphärischen Bedingungen zu bestimmen. Vielfach werden bereits Explosionskenngrößen unter nichtatmosphärischen Bedingungen gemessen. Aufgrund der unterschiedlichen Bestimmungsverfahren sind die Ergebnisse nur bedingt vergleichbar. Im Rahmen der vorliegenden Arbeit wurden apparative Einflussparameter unter nichtatmosphärischen Bedingungen untersucht, mit dem Ziel, normungsreife Bestimmungsverfahren für Explosionskenngrößen unter nichtatmosphärischen Bedingungen zu entwickeln. Für Verfahren zur Bestimmung der Grenzen des Explosionsbereiches (Explosionsgrenzen, SGK) wurden Untersuchungen hinsichtlich der Mindestgröße des Zündgefäßes, geeigneter Zündkriterien und geeigneter Zündquellen durchgeführt. Aus Sicherheitsgründen sollten gerade bei hohen Anfangsdrücken möglichst kleine geschlossene Zündgefäße verwendet werden. Daher wurde das druckabhängige Mindestvolumen bis zu einem Anfangsdruck von p0 = 50 bar bestimmt. Die Ergebnisse zeigen, dass bei atmosphärischen Bedingungen Gefäße mit einem Volumen V ≥ 11 dm³ verwendet werden müssen, um den Einfluss auf die ermittelten Werte zu minimieren. Bei einem Anstieg des Anfangsdrucks verringert sich das notwendige Gefäßvolumen. Beispielsweise kann bei p0 ≥ 50 bar ein Gefäß mit einem Volumen V = 1 dm³ verwendet werden. Als Kriterium für eine Entzündung werden häufig visuelle Zündkriterien oder Druckschwellenkriterien verwendet. In detaillierten Untersuchungen wurden visuelle Kriterien, Druckkriterien und Temperaturkriterien für sieben Brenngase bis zu einem Ausgangsdruck von p0 = 20 bar miteinander verglichen. Das zuverlässigste Kriterium für eine Entzündung unter nichtatmosphärischen Bedingungen ist eine Kombination aus einem Druckschwellenkriterium von pex/p0 ≥ 1,02 oder einem Temperaturschwellenkriterium von ΔT ≥ 100 K. In den bisher genormten Bestimmungsverfahren für atmosphärische Bedingungen sind verschiedene Zünder beschrieben. Auch unter nichtatmosphärischen Bedingungen muss der Eintrag der Zündenergie zuverlässig, definiert und reproduzierbar erfolgen. Es wurde der Einfluss von Druck, Gemischzusammensetzung und konstruktiven Parametern (z. B. Elektrodenabstand) auf den Zündvorgang der Zündquellen explodierender Draht, Funkenzünder und Gleitfunkenzünder untersucht. Für die Analyse des Zündvorganges wurde ein optisches Verfahren entwickelt. Weiterhin wurden die Zünder kalorimetrisch hinsichtlich ihres realen Energieeintrages verglichen. Unter nichtatmosphärischen Bedingungen eignet sich ein explodierender Draht mit einem Drahthalbwellenzündgerät (bis p = 100 bar) oder ein Gleitfunkenzünder (bis p = 10 bar). Neben Druck und Temperatur werden Explosionskenngrößen vor allem durch den verwendeten Oxidator beeinflusst. Bisher sind kaum Werte für die Explosionsbereiche von Brenngas/Inertgas/Sauerstoff-Gemischen bei hohen Anfangsdrücken vorhanden. Daher wurden die Explosionsbereiche für die ternären Gemische CH4/N2/O2 und C2H4/N2/O2 bis zu einem Anfangsdruck von p0 = 50 bar bestimmt. Gerade in sauerstoffreichen Gemischen können Reaktionen derart schnell ablaufen, dass die Bestimmung der Explosionskenngrößen maximaler Explosionsdruck und maximaler zeitlicher Explosionsdruckanstieg nicht möglich ist. Daher wurden Untersuchungen in binären Brenngas/Sauerstoff-Gemischen bei erhöhten Ausgangsdrücken mit verschiedenen Druckmesssystemen durchgeführt. In Gemischen mit langsameren Reaktionen sind für die Druck-Zeit-Messung piezoresistive Druckaufnehmer besser geeignet. Für die Messungen bei schnelleren Reaktionen, weiter im Explosionsbereich, eignen sich eher piezoelektrische Druckaufnehmer. Damit die Druck-Zeit-Signale dieser sehr schnellen Reaktionen ausgewertet werden können, kann eine Glättung erforderlich sein. Die Messsignale wurden mit unterschiedlichen Verfahren geglättet. Die besten Ergebnisse, hinsichtlich der Genauigkeit und der Größe des Auswertebereiches, wurden mit einem Programm zu Berechnung der Verbrennungsgeschwindigkeit mittels physikalischer Modelle erzielt. Mit der Glättungsmethode dieses Verfahrens ist es möglich auch sehr schnelle Druckanstiege in sauerstoffreichen Gemischen auszuwerten. Resultierend aus den Ergebnissen der Untersuchungen sind Empfehlungen für zwei Bestimmungsverfahren zur Messung der Explosionsgrenzen und SGK sowie des maximalen Explosionsdrucks und des maximalen zeitlichen Explosionsdruckanstieges unter nichtatmosphärischen Bedingungen erarbeitet worden. KW - Sicherheitstechnische Kenngrößen KW - Explosionsgrenzen KW - Zündkriterium KW - Nichtatmosphärische Bedingungen KW - Bestimmungsverfahren PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:gbv:ma9:1-6908 SP - 1 EP - 183 PB - Otto-von-Guericke-Universität CY - Magdeburg AN - OPUS4-39131 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Unger, Wolfgang T1 - IND15 JRP SurfChem: Traceable quantitative surface chemical analysis for industrial applications N2 - The SurfChem project has made a significant contribution to traceable quantitative surface chemical analysis for industrial applications by delivering new certified reference materials and test samples for specific technical applications. Regular performance tests of instruments, metrological methodology for the detection of (bio)organic surface species, ambient and non-destructive surface chemical analysis for in-line process control and new in situ characterisation techniques of catalytically active surfaces have been achieved. KW - Surface analysis KW - Metrology KW - Euramet EMRP PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-388673 UR - http://www.euramet.org/research-innovation/search-research-projects/details/?eurametCtcp_project_show%5Bproject%5D=1115&eurametCtcp_project%5Bback%5D=893&cHash=5fd23fc7f759db18176584b5d8a5fe89 SP - 1 EP - 39 CY - Teddington AN - OPUS4-38867 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hu, W. A1 - Said, Samir A1 - Rohrmann, R. A1 - Teng, J. A1 - Li, Z. A1 - Lu, W. A1 - Cunha, A. T1 - Operational modal analysis and continuous dynamic monitoring of structures N2 - This paper addresses operational modal analysis (OMA) and continuous dynamic monitoring (CDM) of two bridges. One of them is installed with Tuned Mass Dampers (TMDs) while another one is a normal bridge. Two ambient vibration tests were performed on these two bridges respectively. It is observed that not only installation of TMDs but also environmental factors influence the variations of structural frequencies, which may mask the subtle change induced by small structural changes. As a result, continuous dynamic monitoring systems were implemented on these two bridges, in order to evaluate efficiency of the TMD system, remove the environmental effects and build reliable damage indices that are only sensitive to structural changes. The results of CDM of these two bridges during several years are presented. Software systems developed for OMA and CDM are also introduced. T2 - 14th International Symposium on Structural Engineering (ISSE-14) CY - Beijing, Peoples Republic of China DA - 12.10.2016 KW - Structure KW - Operational modal analysis KW - Continuous dynamic monitoring PY - 2016 SN - 978-7-03-050125-7 VL - 2016 SP - 366 EP - 372 PB - Science Press Beijing AN - OPUS4-38876 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wäsche, Rolf A1 - Woydt, Mathias T1 - Tribological characterization of niobium carbide with different binder materials N2 - Wear of Niobium carbide with nickel binder has been experimentally characterized under dry, oscillating sliding conditions against steel and a-alumina up to 600°C. T2 - National Tribology Conference/NTC-2016 CY - Varanasi, India DA - 08.12.2016 KW - Niobium carbide KW - Wear resistance KW - Binder PY - 2016 SP - 1 EP - 2 AN - OPUS4-38879 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fischer, Franziska A1 - Emmerling, Franziska T1 - Synthesen in der Kugelmühle N2 - Wärme, Licht und Elektrizität sind die typischen Energiequellen chemischer Synthesen. In den letzten Jahren haben sich aber auch mechanische Kräfte etabliert: Mechanochemie braucht kein Lösungsmittel und funktioniert bei Raumtemperatur. Über die zugrundeliegenden Prozesse ist bislang wenig bekannt. KW - Mechanochemie PY - 2016 DO - https://doi.org/10.1002/nadc.20164046717 SN - 1439-9598 SN - 1868-0054 VL - 64 IS - 5 SP - 509 EP - 513 AN - OPUS4-39282 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grätz, Rainer T1 - Grundlagen für die Konformitätsbewertung nichtelektrischer Produkte N2 - Beschaffenheitsanforderungen an Produkte, die Explosionsschutzanforderungen zu erfüllen haben, werden in Deutschland durch die 9. Verordnung zum Produktsicherheitsgesetz (9. ProdSV, Maschinenverordnung) /2/ und speziell für atmosphärische Bedingungen in der 11. Verordnung zum Produktsicherheitsgesetz (11. ProdSV, Explosionsschutzverordnung /3/ bis 19.4.2016 bzw. Explosionsschutzprodukteverordnung /4/ ab 20.04.2016) geregelt.Wesentlicher Inhalt dieser Verordnungen und der Europäischen Richtlinie 2014/34/EU sind die Begriffsdefinitionen für Geräte, Schutzsysteme und Komponenten, das System der Konformitätsbewertung und die Konformitätserklärung, sowie die grundlegenden Sicherheits- und Gesundheitsanforderungen. Es gilt dabei das Prinzip der Herstellerverantwortung. Der Hersteller eines Produktes dokumentiert die Erfüllung der Richtlinienanforderungen mit seiner Konformitätserklärung und der Kennzeichnung des Produktes mit dem CE-Zeichen. T2 - 42. Heilbronner Ex-Schutz-Seminar Planen, Errichten und Betreiben von Anlagen in explosionsgefährdeten Betriebsstätten Ex-Schutz mechanischer Geräte CY - Heilbronn, Germany DA - 22.02.2017 KW - Explosionsschutz KW - Konformitätsbewertung KW - ATEX KW - Richtlinie 2014/34/EU KW - Zündgefahrenbewertung PY - 2017 SP - 5-1 EP - 5-63 PB - Technische Akademie Heilbronn e.V. CY - Heilbronn AN - OPUS4-39262 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ertel, Jens-Peter A1 - Niederleithinger, Ernst A1 - Grohmann, Maria ED - Stahlmann, J. T1 - Das PileInspect-Projekt: Pfahlintegritätsprüfung durch Schwinganregung mittels eines elektrodynamischen Shakers N2 - Pfahlintegritätsprüfung von Bohrpfählen durch Messung der Impulsantwort mittels Schwinganregung und regularisierter Dekonvolution. T2 - Pfahlsymposium 2017 CY - Braunschweig, Germany DA - 23.02.2017 KW - Pfahlintegritätsprüfung KW - Tikhonov KW - Dekonvolution KW - PileInspect KW - Shaker PY - 2017 VL - 2017 IS - 102 SP - 217 EP - 235 PB - Eigenverlag Institut für Grundbau und Bodenmechanik - Technische Universität Braunschweig CY - Braunschweig AN - OPUS4-39272 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maack, Stefan A1 - Knackmuß, J. A1 - Creutzburg, R. T1 - Comparative visualization of the geometry of a hollow box girder using 3D-LiDAR – Part 2: Reconstruction of 3D Geometric Model N2 - With the mandatory introduction of the May 2011 directive for reassessment of bridges in Germany, the administrations of the federal and state governments have the duty to prove the stability of their bridge stock. Verification of bridge stability will be realized with consideration of the newly increased traffic loads. Particularly in older bridges, the verification can only be achieved if calculative surplus load capacity of the original structural design is taken into account in the recalculation. One option for considering these reserves is the exact determination of the dead weight of the bridge. Within this case study, it will be demonstrated how the problem can be practically solved. In order to determine the dead weight of a concrete bridge, its volume has to be calculated. as a first step, a 3D laser scanner is used to record the internal geometry of a hollow box bridge girder. For the determination of the thickness of the concrete member, the non-destructive technique ultrasonic echo is applied. The construction must be segmented in approximately equidistant parts in order to be able to carry out an economic and efficient investigation. The description of the segmentation of the point cloud, carried out in a 2D model, was presented in the first part of the publication. The subject of this presentation is the merging of 2D cross sections into a 3D model, from which the weight of the bridge can be calculated. T2 - IS&T International Symposium on Electronic Imaging 2017 CY - San Francisco, CA, USA DA - 29.01.2017 KW - LiDAR KW - Zerstörungsfreie Prüfung KW - Brücken KW - NDT KW - Bridge inspection PY - 2017 DO - https://doi.org/10.2352/ISSN.2470-1173.2017.6.MOBMU-308 SP - 255 EP - 264 PB - Society for Imaging Science and Technology AN - OPUS4-39242 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Vormwald, M. T1 - Schwingfestigkeit und Bruchmechanik N2 - Um bruchmechanisch Schwingfestigkeiten ermitteln zu können, sind einige Voraussetzungen erforderlich: (a) Das Wachstum sowohl langer als auch mechanisch und physikalisch kurzer Risse muss adäquat beschrieben werden. Das erfordert die Anwendung elastisch plastischer Konzepte zur Beschreibung der zyklischen Rissspitzenbeanspruchung sowie die Modellierung des graduellen Aufbaus der Rissschließeffekte im Kurzrissbereich. (b) Es müssen physikalisch sinnvolle Ausgangsrissgrößen für die bruchmechanische Analyse bestimmt werden. (c) Bei Spannungen oberhalb der Dauerfestigkeit respektive der Versagensspannung bei 107 Lastwechseln muss gegebenenfalls Mehrfachrisswachstum berücksichtigt werden. Der Vortrag diskutiert diese Punkte und zeigt Lösungswege auf. T2 - 49. Tagung des Arbeitskreises "Bruchmechanik und Bauteilsicherheit" CY - Mittweida, Germany DA - 14.02.2017 KW - Schwingfestigkeit KW - Bruchmechanik KW - Ausgangsriss KW - Mehrfachriss PY - 2017 VL - 249 SP - 77 EP - 92 PB - DVM (Deutscher Verband für Materialforschung und -prüfung) CY - Berlin AN - OPUS4-39227 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pulikowski, D. A1 - Lackner, F. A1 - Scheuerlein, C. A1 - Meinel, Dietmar A1 - Savary, F. A1 - Tommasini, D. A1 - Pajor, M. T1 - Testing mechanical behavior of Nb3Sn Rutherford cable during coil winding N2 - In the framework of the development of high field magnets made of Nb3Sn superconductor for projects like HL-LHC and FCC studies, it is needed to refine the understanding of the coil winding process and its impact on the overall mechanical behavior of the conductor. For this purpose, a new cable winding setup has been developed in order to compare the windability of different Nb3Sn Rutherford cables. In addition, various geometrical cable inspection methods were tested and compared. First experimental results obtained with the new set-up for winding tests are summarized. T2 - 2016 Applied Superconductivity Conference (ASC’16) CY - Denver, Colorado, USA DA - 04.09.2016 KW - Coil winding KW - Rutherford cable KW - X-ray absorption tomography PY - 2017 DO - https://doi.org/10.1109/TASC.2017.2656179 SN - 1051-8223 SN - 1558-2515 VL - 27 IS - 4 SP - 1 EP - 4 PB - IEEE AN - OPUS4-39357 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bonse, Jörn A1 - Kirner, Sabrina V. A1 - Höhm, S. A1 - Epperlein, Nadja A1 - Spaltmann, Dirk A1 - Rosenfeld, A. A1 - Krüger, Jörg T1 - Applications of laser-induced periodic surface structures (LIPSS) N2 - Laser-induced periodic surface structures (LIPSS, ripples) are a universal phenomenon that can be observed on almost any material after the irradiation by linearly polarized laser beams, particularly when using ultrashort laser pulses with durations in the picosecond to femtosecond range. During the past few years significantly increasing research activities have been reported in the field of LIPSS, since their generation in a single-step process provides a simple way of nanostructuring and surface functionalization towards the control of optical, mechanical or chemical properties. In this contribution current applications of LIPSS are reviewed, including the colorization of technical surfaces, the control of surface wetting, the tailoring of surface colonization by bacterial biofilms, and the improvement of the tribological performance of nanostructured metal surfaces. T2 - SPIE Photonics West Conference, Laser-based Micro- and Nanoprocessing XI CY - San Francisco, USA DA - 27.01.2017 KW - Laser-induced periodic surface structures (LIPSS) KW - Laser processing KW - Surface functionalization KW - Application PY - 2017 SN - 978-1-5106-0625-8 SN - 978-1-5106-0626-5 DO - https://doi.org/10.1117/12.2250919 SN - 0277-786X SN - 1996-756X VL - 10092 SP - Article UNSP 100920N, 100920N-1 EP - 100920N-9 PB - SPIE CY - Bellingham, USA AN - OPUS4-39305 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Genga, R. M. A1 - Cornish, L. A. A1 - Polese, C. A1 - Woydt, Mathias A1 - Janse van Vuuren, A. T1 - Wear investigation of NbC inserts during face-milling of grey cast iron N2 - Tungsten carbide (WC) based cemented carbides have a good combination of hardness, strength and toughness, making them key materials for cutting tool industry. T2 - The 54th Annual Conference CY - Port Elizabeth, South Africa DA - 05.12.2016 KW - Tungsten carbide (WC) KW - Niobium carbide (NbC) KW - Wear KW - Machining PY - 2016 SN - 978-0-620-73767-8 SN - 0250-0418 SP - 1 AN - OPUS4-39388 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klinge, A. A1 - Roswag-Klinge, E. A1 - Fontana, Patrick A1 - Hoppe, Johannes A1 - Richter, Matthias A1 - Sjöström, C. T1 - Reduktion von Lüftungstechnik durch den Einsatz klimasteuernder Naturbaustoffe - Ergebnisse aus dem EU Forschungsvorhaben H-House und der Baupraxis T1 - Reducing the need for mechanical ventilation through the use of climate-responsive natural building materials - Results from the EU research project H-House and building practice N2 - Die größten Ressourcenverbraucher unserer Zeit sind die Gebäude oder Behausungen des Menschen sowohl in der Phase der Errichtung als auch im Betrieb. Der Gebäudesektor und damit auch die Architektur verbrauchen in Deutschland ca. 50 % der fossilen Energieressourcen und verursachen ca. 60 % des gesamten Müllaufkommens mit dem zugehörigen Bedarf an Ressourcen in der Errichtung. Öl, Stahl und Beton haben uns Glauben gemacht die natürlichen Begebenheiten bei der Gestaltung von Gebäuden wenig beachten zu müssen. Immer neue Techniken zum Betrieb und zur Klimatisierung von Gebäuden waren die Zukunft. Der Klimawandel und die Ressourcenknappheit sind Aufforderungen zur Veränderung. Das Voranschreiten der Reform des Bauwesens hat somit zentrale Bedeutung zur Erreichung der Nachhaltigkeitsziele und um unsere Gesellschaft zukunftsfähig zu machen. Klimaangepasste Architekturkonzepte und die Verwendung von klimaaktiven Naturbaustoffen werden einen wesentlichen Beitrag zum Ressourcenschutz erbringen. N2 - More resources are consumed for the construction and use of buildings and dwellings than in any other industry. The building sector, and by extension architecture, is responsible for consuming around 50 % of fossil fuels in Germany and produces around 60 % of the entire volume of waste together with the resources used for the construction of buildings. Oil, steel and concrete has led us to believe that we can overcome the laws of nature in the design of our buildings, and for years we have devised ever new technologies for controlling building climate and operating our buildings. But the onset of climate change and the continuing depletion of resources signals a need for Change. To achieve our declared sustainability goals, and to better equip society for the future, it is vital that we effect reforms in the building sector. Climate-adaptive architectural concepts and the use of climateresponsive natural building materials can potentially make a major contribution to conserving resources. T2 - Lehm 2016 - 7. Internationale Fachtagung für Lehmbau - 7th International Conference on Building with Earth CY - Weimar, Germany DA - 12.11.2016 KW - Baustoffe KW - Hygroskopische Lehm- und Holzbaustoffe KW - Natürliche Belüftung KW - Luftdichte Gebäudehülle KW - Schadstoffemission von Baustoffen KW - Building materials KW - Hygroscopic earthen and wooden building materials KW - Natural ventilation KW - Air-tight building envelope KW - Emission of pollutants from building materials PY - 2016 N1 - Volltext (PDF) in deutsch und englisch - Full text (PDF) in German and English SP - 1 EP - 15 PB - Eigenverlag Dachverband Lehm e. V. CY - Weimar AN - OPUS4-38997 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Unnikrishnakurup, Sreedhar A1 - Thomas, R. A1 - Balasubramaniam, Krishnan A1 - Narayanan, L. A1 - Phanikumar, G. T1 - Dissimilar metal joint quality measurement using infrared thermography: Experimental and numerical approach for the application to CMT welding N2 - Joining of dissimilar material has become highly popular research subject in the automobile industry due to the reduced weight and thereby increasing the fuel efficiency. Infrared thermography can be used as a natural tool to measure the temperature near the welding region and correlate the distribution of temperature to the weld quality. In the present work the quality of the dissimilar welded sample is identified using the temperature distribution in the vicinity of the weld pool region. A numerical model for CMT continues welding process has been modeled and simulated for the first time and compared with the experimental measurement. T2 - The 13th International Conference on Quantitative Infrared Thermography - QIRT 2016 CY - Gdansk, Poland DA - 04.07.2016 KW - Online monitoring KW - CMT welding KW - Dissimilar joint KW - FEM PY - 2016 UR - https://www.ndt.net/?id=20704 DO - https://doi.org/10.21611/qirt.2016.056 SP - 389 EP - 390 PB - Gdansk University of Technology CY - Gdansk AN - OPUS4-39078 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Puthiyaveettil, N. A1 - Krishna, S. A1 - Kidangan, R. A1 - Unnikrishnakurup, Sreedhar A1 - Krishnamurthy, C. V. A1 - Ziegler, Mathias A1 - Myrach, Philipp A1 - Balasubramaniam, Krishnan T1 - In-line laser thermography for crack detection at elevated temperature: A Numerical modeling study N2 - The detection and characterization of cracks prior to damage is a technologically and economically highly significant task and is of very importance when it comes to safety-relevant structures. The evaluation of a components life is closely related to the presence of cracks in it. Laser thermography has already high capability for the detection of surface cracks and for the characterization of the geometry of artificial surface flaws in metallic samples. Crack detection in metallic samples at high temperature is highly significant in present manufacturing scenario. During the casting process of billets, surface cracks form, due to the suboptimal cooling rates. These cracks reduce value of the billet and must be removed using machining process after cooling. This secondary process increases cost of manufacturing. In this work we developed a heat transfer model for laser thermography to study the thermal contrast variation with increase in surface temperature using finite element method (FEM). Here we are mainly concentrating the capability of the scanning laser thermography in crack detection which are in elevated temperature and numerical modeling study of thermal contrast variation of crack with respect increase in metal surface temperature. This study is important to prove the capability of laser thermography for crack detection in elevated temperature. Since we are using High power CW Laser to local heating of the metal surface which can give relatively high thermal contrast even at elevated temperature compare to other heating source. Here we are modeled and simulated 2D laser scanning across a surface breaking crack and developed an algorithm to produce the vicinity of crack. The algorithm we developed applied for various surface temperature data. And validated the credibility of the algorithm with experimental data. T2 - 13th Quantitative Infrared Thermography Conference 2016 CY - Gdansk, Poland DA - 04.07.2016 KW - Thermal contrast KW - Laser thermography KW - Thermography KW - Surface cracks KW - Elevated temperatures KW - FEM PY - 2016 UR - http://www.ndt.net/article/qirt2016/papers/092.pdf DO - https://doi.org/10.21611/qirt.2016.092 VL - 2016 SP - 588 EP - 596 PB - QIRT 2016 Proceedings AN - OPUS4-39105 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Steckenmesser, D. A1 - Vogel, Christian A1 - Steffens, D. T1 - P-Verfügbarkeit von Recyclingprodukten N2 - Die Pflanzenversuche der vorliegenden Arbeit zeigen sehr gut, dass das Pyrolyse Produkt der Firma Pyreg zwar in der kurzfristigen P-Verfügbarkeit nur mäßig abschnitt, dafür aber eine gute P-Nachlieferung aufweist. Dies kann maßgeblich auf die im Produkt vorliegenden P-Verbindungen zurückgeführt werden.Es zeigt sich weiterhin, dass durch eine Na2CO3-Gabe die kurzfristige Verfügbarkeit von eisengefällten Klärschlämmen verbessert werden kann, es aber keinen Einfluss auf die langfristige P-Nachlieferung hat. Das BAM-Verfahren mit Na2SO4 liefert ein Produkt, welches sowohl eine gute kurzfristige P-Verfügbarkeit, als auch eine gute langfristige P-Nachlieferung hat. Dies kann auf die dabei entstehende P-Form, CaNaPO4, zurückgeführt werden. Ferner zeigen die Experimente, dass auch schwerlösliche Phosphate mit N2-fixierendem Rotklee mobilisiert werden können. T2 - 128. VDLUFA-Kongress CY - Rostock, Germany DA - 13.09.2016 KW - Phosphor KW - Recycling KW - Düngemittel PY - 2016 SN - 978-3-941273-23-8 SP - 57 EP - 73 PB - VDLUFA-Verlag CY - Darmstadt AN - OPUS4-38906 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Maiwald, Michael A1 - Guthausen, G. T1 - Abschlussbericht „Prozesskontrolle mittels Niederfeld-NMR-Spektroskopie“ N2 - Die Online-medium-resolution-NMR-Spektroskopie wurde als neue Technik zur Überwachung verfahrenstechnischer Prozesse weiterentwickelt. Entlang der Prozesskette wurden an den verschiedenen Elementen der Online-Spektroskopie gearbeitet. Ein temperierbarer und druckfester Bypass erlaubt, die reagierende Mischung bei Reaktionsbedingungen über eine Pumpe in die NMR-Messzelle zu fördern, für die verschiedene Versionen von temperatur-isolierten NMR-Durchflusszellen berechnet, realisiert und mittels MRI hinsichtlich ihrer strömungsdynamischen und NMR-Eigenschaften charakterisiert wurden. Austauschbare Polymerleitungen für robuste, industrielle Anwendungen kamen ebenso zum Einsatz wie maßgeschneiderte Flusszellen zur Reduktion der Verweilzeitverteilung und des Stoffdurchsatzes. Bewertungsverfahren für MR-NMR-Spektrometer und Durchflusszellen auf Basis leicht verfügbarer Flüssigkeiten (wie z. B. Aceton, Ethanol, Wasser) wurden abgeleitet, Mindestspezifikationen für die Anwendbarkeit der MR-NMR im Prozessmonitoring wurden erarbeitet. Auf der Basis des Bypasssystems konnten einige verschiedene chemische Reaktionen im Bereich einiger 10 s zeitaufgelöst gemessen und ihre Kinetik auch im Fall von Nichtgleichgewichtsmagnetisierung und schneller Strömung analysiert werden. Voraussetzung ist eine stabile und automatisierte Datenbearbeitung, die sich nahtlos in den Workflow von der Datenakquisition bis zur Datenanalyse einbindet. Daher war ein weiteres Augenmerk auf die Datenvorbehandlung gelegt. Bekannte Algorithmen wie die automatisierte Phasenkorrektur entlang der „Minimum Entropy“ Methode und der Maximierung des Realteilspektrums wurden zusammen mit neuen Methoden wie dem Softewarelock implementiert und angewandt. Zur Bestimmung der Konzentrationen wurden verschiedene Verfahren wie die direkte Integration, die Spektrenmodellierung mit und ohne Vorkenntnisse sowie statistische Methoden der Chemometrie angewandt und verglichen. Ebenso ließen sich erstmalig quasiparallel akquirierte 1H- und 19F-MR-NMR-Spektren für die Prozesskontrolle mit gutem Ergebnis analysieren. Die erarbeiteten Konzepte und Verfahren sind unabhängig von der Hard- und -Software des MR-NMR Geräts und damit allgemein einsetzbar. Während des Projektverlaufs kamen Benchtop-Laborgeräte von einer wachsenden Zahl an Herstellern auf den Markt, die immer besser den Anforderungen der Spektroskopie gerecht werden. Online-MR-NMR-Spektroskopie erweitert die Prozessanalytik um eine bislang nur im Labor bekannte chemische Sensitivität gegenwärtig mit der Fähigkeit zur Unterscheidung von beispielsweise Aliphaten, Olefinen oder Aromaten (z. B. Hydrierung) oder Strukturänderungen (z. B. Isomerisierung), bei denen klassische Techniken an ihre Grenzen stoßen. Sie stellt nun eine Alternative für die Prozessanalyse dar, insbesondere wenn schnelle, zerstörungsfreie und integral arbeitende Methoden erforderlich sind. KW - Prozess-Sensoren KW - DFG KW - NMR-Spektroskopie PY - 2015 SP - 1 EP - 15 AN - OPUS4-38852 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kern, Simon A1 - Gräßer, Patrick A1 - Zientek, Nicolai A1 - Maiwald, Michael T1 - First steps towards field integration of benchtop NMR spectroscopy for online monitoring and process control N2 - Online monitoring and process control requires fast and noninvasive analytical methods, which are able to monitor the concentration of reactants in multicomponent mixtures with parts-per-million resolution. Online NMR spectros-copy can meet these demands when flow probes are directly coupled to reactors, since this method features a high linearity between absolute signal area and sample concentration, which makes it an absolute analytical com-parison method being independent on the matrix. Due to improved magnet design and field shimming strategies portable and robust instruments have been introduced to the market by several manufacturers during the last few years. First studies with this technology showed promising results to monitor chemical reaction in the laboratory. T2 - 11. Kolloquium Arbeitskreis Prozessanalytik CY - Wien, Austria DA - 30.11.2015 KW - Online NMR Spectroscopy KW - Smart Sensors KW - Prozess-Spektroskopie KW - Process Analytical Technology KW - Process control PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-388411 SP - 43 EP - 44 AN - OPUS4-38841 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scheidemann, Robert A1 - Weber, Mike A1 - Völzke, Holger A1 - Kasparek, Eva Maria ED - Gomes, J.F.Silva ED - Meguid, S.A. T1 - Temperature dependendency of dynamically loaded polyurethane foam N2 - Polyurethane foam used as impact limiter material undergoes high plastic deformations, whereat the resulting stress-strain relations strongly depend on loading speed and temperature. This paper discusses the efforts necessary to develop a reliable numerical foam simulation model focussing on generation and implementation of temperature- dependent yield curves T2 - 6th International Conference on Mechanics and Materials in Design CY - Ponta Delgada, Azores, Portugal DA - 26.07.2015 KW - Impact limiter KW - Polyurethane foam KW - Finite element model KW - Strain rate KW - Temperature dependency PY - 2015 SN - 978-989-98832-3-9 SP - 1043 EP - 1046 PB - INEGI-FEUP AN - OPUS4-38889 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kasparek, Eva A1 - Völzke, Holger T1 - Non-Heat Generating Legacy Waste - New Strategies for Older Vessels N2 - The German repository “Konrad” is approved for the final storage of approximately 300.000 m³ of non-heat generating radioactive waste considering also the expected residues from operation and decommissioning of current power plants. According to the latest survey as constituted end of 2014, a large proportion of this volume already exists, of which 100.288 m³ are fully loaded packages. As prerequisite for their “Konrad” acceptance, the vessels have to be designed against operational and accidental conditions of the site and be manufactured according to adequate quality assurance programs. The respective safety assessment performed by BAM on behalf of the Federal Office for Radiation Protection is a major challenge especially for those casks that had been produced and loaded already some decades ago. Typically, they were manufactured in big numbers over a longer period of time involving a lot of constructional and management changes. This fact in combination with the previously rather low documentation standards often causes relevant uncertainties about the specific physical and geometrical characteristics of the cask materials and components as well as about details concerning their whole assemblage. This paper highlights current assessment strategies for such older vessels including cubic steel sheet containers as well as cylindrical thick-walled casks. As compliance with each “Konrad”-requirement can hardly be shown independently, only integrated approaches promises success: First, a broader concept of data collection has to be implemented that allows closing documentation gaps by linking dispersed and diverse data, e.g. delivery slips and handwritten fabrication records, by including plausibility considerations as well as random inspection programs. Thereby, the relevant properties of all applied casks have to be identified and their potential range should be quantified as accurately as possible. This knowledge is necessary to define one or more representative configurations of the cask as the base for design testing. The actual investigation program must enable to track the influence of deviations and determine safety margins especially in the likely case that not the most conservative setting of all cask features can be tested. The paper evaluates the respective ongoing efforts of industrial applicants and summarizes BAM experiences and associated research projects. T2 - 18th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Kobe, Japan DA - 18.09.2016 KW - Requalification KW - Low and medium level radioactive waste KW - Final disposal container KW - Legacy waste KW - Konrad repository PY - 2016 SP - Paper 1014, 1 EP - 9 AN - OPUS4-38892 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Trappe, Volker A1 - Günzel, Stephan A1 - Metzkes, Karoline ED - Renard, Jacques T1 - Degradation mechanism of short-fibre reinforced PA due to uniaxial fatigue loading evaluated by NDT and fractography N2 - The damage process of short glass fibre (30% weight) reinforced polyamide caused by mechanical loading was investigated from the beginning on micro cracking level to the incipient crack of mm-dimension. Based on high resolution computer tomography and the X-ray-refraction technique the inner surface due to micro-cracking at the short fibre ends and the fibre matrix debonding of the skin surface of the filament was determined quantitatively. With the knowledge of the fatigue crack propagation rate and fracture toughness of the material from former research projects, it was derived that the total inner surface due to micro cracks measured by X-ray refraction is much higher than the specimen could have withstand the load, supposed the surface is in a localized crack. Hence, the damage process could be described from micro to macro level. Accompanying fractographic investigations endorse the modelling based on the NDT-techniques. T2 - 6th International Conference on Fatigue of Composites - ICFC 6 CY - Paris, France DA - 25.03.2015 KW - Damage evolution KW - Fracture mechanics KW - Crack propagation KW - Short-Fibre-Reinforced Polymadide KW - X-ray-refraction KW - Fractography PY - 2015 SP - 1 EP - 9 PB - ASTech CY - Paris AN - OPUS4-38779 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Trappe, Volker A1 - Basan, Ricardo T1 - Fatigue life evaluation of spar cap materials by four point bending test on width-tapered specimensa N2 - The presented research project focuses on an effective method to evaluate the fatigue strength of thick unidirectional laminates to be applied in spar caps. Therefore, a width-tapered bending specimen was developed for a four point loading set up. Static and fatigue loading was performed with the load ratio of R=-1. The complex stress state was investigated numerically with a finite element analysis. Finally, the concept was proven experimentally on specimens made of pultruded fibre rods. The fatigue behaviour of continuous tapered width by water jet cutting was compared to discrete tapering by rod-drop. T2 - 20th International Conference on Composite Materials CY - Copenhagen, Denmark DA - 19.07.2015 KW - Fatigue KW - Pultruded fibre rods KW - CFRP KW - Four point bending test KW - Spar cap design PY - 2015 UR - http://iccm20.org/fullpapers/file?f=WM39KAy5ME VL - 2015 SP - Paper 150701-2549 PB - ICCM20 CY - Copenhagen AN - OPUS4-38783 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Barth, Enrico A1 - Homann, Tobias A1 - Prager, Jens T1 - Einpunkt-Laser-Doppler-Vibrometer für die mehrdimensionale Analyse des Schwingungsverhaltens auf Festkörperoberflächen im MHz-Bereich N2 - Zur messtechnischen Analyse des Schwingungsverhaltens von Festkörpern kann die Bewegung der Oberfläche mit einem Laservibrometer vermessen werden. Für bestimmte Anwendungen, beispielsweise bei der Charakterisierung von anisotropen Werkstoffeigenschaften, ist eine mehrdimensionale Bestimmung der Schwingungskomponenten notwendig. Zur Umsetzung des Messprinzips wird ein Ansatz mit einem Einpunkt-Vibrometer verfolgt, welcher sequenziell die Messpunkte aus mehreren Winkeln analysiert und unter Verwendung der Winkelbeziehungen die Normal- und In-Plane-Komponenten der Schwingung berechnet. Die exakte Positionierung des Lasers aus verschiedenen Winkeln stellt durch die hohen Frequenzen und die damit verbundenen Wellenlängen im mm-Bereich die wesentliche Herausforderung bei der Umsetzung des Messverfahrens dar. Bereits kleine Abweichungen führen zu einem hohen Phasenversatz und somit zu nicht tolerierbaren Messfehlern. Unter Berücksichtigung schwer zu ermittelnder Geometrieinformationen wurde ein Verfahren entwickelt, mit dem eine ausreichende Positionierungsgenauigkeit gewährleistet werden kann. Im Vortrag werden zunächst die Fehlereinflüsse analysiert und die Umsetzung des Messverfahrens detailliert vorgestellt. Es wird gezeigt, dass die Schwingungskomponenten bis zu einer Frequenz von 1 MHz mit ausreichender Genauigkeit bestimmt werden können. Zusätzlich wird der Einfluss verschiedener Möglichkeiten zur Erhöhung der Reflektivität der Oberfläche auf die Ergebnisse untersucht. T2 - 43. Jahrestagung für Akustik (DAGA) CY - Kiel, Germany DA - 06.03.2017 KW - ZFP Schweißnaht Ultraschall PY - 2017 SN - 978-3-939296-12-6 SP - 448 EP - 451 AN - OPUS4-39421 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Matzen, Melissa A1 - Marti, J. M. A1 - Onate, E. A1 - Idelsohn, S. A1 - Schartel, Bernhard T1 - Particle finite element modelling and advanced experiments on dripping V-0 polypropylene N2 - Melt flow and dripping of polymeric materials can be both beneficial and detrimental during fire. It reduces flame spread and result in extinction, as mass and heat are removed from the actual pyrolysis zone. In contrast, melt flow and dripping can provide an additional ignition source, additional process of flame spread and has the potential to start a pool fire. In the vertical UL 94 test, a well adjusted dripping behaviour of flame retarded polypropylene (PP-FR) resulted in a non-flaming dripping V-0 classification. For the polymer samples and their drops collected in UL 94, the decomposition and viscosity was investigated. Particle finite element method (PFEM) was successfully used to simulate the material behaviour in the UL 94 test and increased the understanding of the complex behaviour of polymeric materials during fire. T2 - Fire and Materials, 15th International Conference CY - San Francisco, CA, USA DA - 06.02.2017 KW - V0 dripping KW - Melt flow KW - Flammability KW - Flame retardant KW - Radical generator KW - Dripping agent KW - Polypropylene KW - Particle Finite Element Modelling PY - 2017 SP - 57 EP - 62 PB - Interscience Communication CY - Bromley, UK AN - OPUS4-39443 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Dietrich, P. A1 - Thissen, A. A1 - Kulak, N. A1 - Kjaervik, Marit A1 - Unger, Wolfgang T1 - XPS surface chemical analysis of aqueous solutions with EnviroESCA N2 - Water and aqueous reagents are essential in any biological process or system. But apart from a few special low vapor-pressure cases, liquids have not been accessible to any technique requiring UHV conditions. EnviroESCA opens up this exciting field of applications. In this paper first results from water based samples are presented as a proof of concept to demonstrate the special capabilities of EnviroESCA analyzing liquid samples. The following solutions were investigated under near ambient pressure conditions: i.) water, ii.) brine, iii.) an oil in water dispersion, iv.) aqueous iron(II) sulfate heptahydrate, and v.) a suspension of nano silver particles in water. KW - Surface Analysis KW - Near Ambient Pressure XPS KW - Aqueous Solutions PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-394603 UR - http://www.enviro.specs.de/cms/upload/bilder/EnviroESCA/Applications/Liquids/Application-Note_EnviroESCA_Aqueous_Solutions.pdf N1 - BAM Mitarbeiter Beitrag im Acknowledgement definiert. IS - #000394 SP - 1 PB - SPECS CY - Berlin AN - OPUS4-39460 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, C. T1 - Einfluss der Abkühlgeschwindigkeit auf die Korrosionsbeständigkeit martensitischer nichtrostender Stähle N2 - Martensitische nichtrostende Stähle werden in verschiedenen technischen Bereichen eingesetzt, bei denen eine optimale Kombination aus hoher mechanischer Festigkeit und guter korrosiver Beständigkeit gefordert wird. Beide Eigenschaften werden in der Industrie primär durch die Wärmebehandlung gesteuert. Die Korrosionseigenschaften sind dabei stark von der diffusionsbedingten Bildung und Auflösung von Chromkarbiden abhängig. In vergangenen wissenschaftlichen Arbeiten konnte nachgewiesen werden, dass die Abkühlgeschwindigkeit nach dem Austenitisieren einen großen Einfluss auf die Bildung solcher Karbide hat. Der Einfluss der Abkühlgeschwindigkeit auf die Lochkorrosionsbeständigkeit wurde an den Stählen 1.4108 und 1.4116 systematisch untersucht. Mit Hilfe des Stirnabschreckversuches wurde dabei die Abkühlgeschwindigkeiten variiert und anschließend die Veränderung von Gefüge, Lochkorrosionsbeständigkeit und Härte untersucht. Als Ergebnis konnten kritische Abkühlgeschwindigkeiten ermittelt werden, bei denen eine kritische Verringerung der Korrosionsbeständigkeit einsetzt. T2 - GfKORR-Jahrestagung 'Duplex-Stähle – Nische oder Zukunft ?' CY - Frankfurt/M., Germany DA - 15.11.2016 KW - Korrosionsbeständigkeit KW - Martensitische nichtrostende Stähle KW - Abkühlgeschwindigkeit PY - 2016 AN - OPUS4-39473 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ziegler, Kurt A1 - Dankwa, J. T1 - Probleme der Sprengtechnik in Ghana, dargestellt am Beispiel einer Gold- und einer Manganmine T2 - Fels- und Gesteinssprengtechnik übertage CY - Essen DA - 03.02.1983 PY - 1983 SP - 1 EP - 14 AN - OPUS4-39484 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Knaust, Christian A1 - Festag, S. A1 - Brüne, M. A1 - Dietrich, Matthes A1 - Amecke-Mönninghoff, Stephan A1 - Konrath, B. A1 - Arnold, L. T1 - Modellierung eines Brandes in einer U-Bahn-Station: Validierung von Rechenmodellen auf der Grundlage von Feldversuchen N2 - Mittels Propan-Brennern mit einer Brennerleistung 750 kW wurden in einer U-Bahn-Station Heißgasversuche durchgeführt und die zeitlichen und örtlichen Verteilungen der physikalischen Größen (Stoffkonzentration, Temperatur und Rauchgasdichte) erfasst. Laborversuche sowie die Feldversuche sind Validierungsgrundlage für ANSYS CFX und FDS und die später im Rechenmodell der U-Bahn-Station zur Untersuchung der Grundströmung und Rauchausbreitung verwendeten mathematisch-physikalischen Modelle. Der Aufsatz stellt das Projekt ORPHEUS vor und diskutiert die ersten Ergebnisse. T2 - Magdeburger Brand- und Explosionsschutztage 2017 CY - Magdeburg, Germany DA - 23.03.2017 KW - Rechenmodelle KW - Ansys CFX KW - FDS KW - Computational fluid dynamics KW - CFD KW - Rauchausbreitung KW - Validierung KW - U-Bahn KW - Brandszenarien KW - Modellierung von Bränden PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-396694 SN - 978-3-00-056201-3 DO - https://doi.org/10.978.300/0562013 SP - 1 EP - 12 PB - Otto-von-Guericke-Universität Magdeburg CY - Magdeburg AN - OPUS4-39669 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beck, Uwe A1 - Lange, Thorid A1 - Hielscher, Stefan A1 - Rietz, Uwe A1 - Lerche, D. A1 - Pfuch, A. T1 - Multiple-sample approach for bonding and testing: validation of bonding strength of adhesive-bonded joints and adhesive tapes N2 - The multiple-sample approach by means of centrifugal adhesion testing (CAT-technology) allows the determination of bonding strength of adhesive-bonded joints on a statistical basis of up to eight samples. Therefore, it is obvious to ensure the continuous handling and identical processing of an octet of samples within the entire process chain of wet-chemical cleaning, plasma-chemical pre-treatment, bonding of samples, and testing of bonding strength. Within the multiple-sample bonding set-up (MPKV-technology) a defined bonding pressure can be adjusted regardless the actual number of samples. A comparison of single- and multiple-sample approach is made for bonding strength of selected adhesives, double-sided adhesive tapes and different material combinations [stainless steel (V2A) vs. stainless steel, polyamide (PA), or polypropylene (PP)]. It is shown that both technologies improve reliability of results T2 - EURADH 2016 Adhesion ´16 CY - Glasgow, UK DA - 21.09.2016 KW - Multiple-sample bonding KW - Multiple-sample testing KW - Bonding strength KW - Adhesives and adhesive tapes PY - 2016 SP - 162 EP - 166 AN - OPUS4-37588 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bertovic, Marija T1 - Automation in non-destructive testing: new risks and risk sources N2 - Over the past couple of decades Non-Destructive Testing (NDT) has seen a significant increase in the use of automation. In addition to increased reliability, objectivity, consistency, repeatability, productivity, and so on, automating parts of the process is expected to decrease the potential for human error. However, the literature on human-automation interaction suggests that automation is not only associated with benefits, but also with new risks and risk sources. First, this paper will present the methodology used to identify—for the first time—possible risks associated with mechanised data acquisition and corresponding data evaluation. Moreover, it will highlight possible risks, their causes, consequences, and ways of preventing them. Second, those preventive measures will be further analysed by examining new risks that can arise from their implementation, i.e. potential for failure that can arise from (a) working with automated defect-detection and sizing aids, (b) implementing human redundancy, and (c) improvement of the inspection procedures without due consideration of the procedure users. And third, some optimisations strategies will be provided. The purpose of this work is to show that mechanised testing is associated with potential for failure and that the sources of those risks go beyond single inspectors and need to be looked at in the interaction of people with other systems, i.e. the technology, the team and, most importantly, the organisation. T2 - 55th annual Conference of the British Institute for Non-Destructive Testing CY - Nottingham, UK DA - 12.09.2016 KW - NDT KW - Automation KW - Reliability PY - 2016 SP - 1 EP - 11 AN - OPUS4-37591 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wu, Cheng-Chieh A1 - Weisbrich, S. A1 - Neitzel, F. ED - Aulova, Alexandra ED - Rogelj Ritonja, Alenka ED - Emri, Igor T1 - Approximate model for geometrical complex structures N2 - Many engineering structures are made of composite materials or metal foam. To simulate the deformational behaviour of these structures often requires a high number of discretisation elements. This in turn yields a very large system of linear equations that are extremely time and memory consuming or practically impossible to solve. It is therefore desirable to find an approach to overcome this obstacle. T2 - 33rd Danubia- Adria Symposium on Advances in Experimental Mechanics CY - Portorož, Slovenia DA - 20.09.2016 KW - Inverse analysis KW - Finite element method KW - Least-squares adjustment PY - 2016 SN - 978-961-94081-0-0 SP - 52 EP - 53 CY - Ljubljana AN - OPUS4-37529 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Babutzka, Martin A1 - Heyn, A. T1 - Corrosion investigations by using gel-type electrolytes N2 - This contribution will show that gel-type electrolytes influence protective layers on zinc coatings considerably less than typical bulk electrolytes. Different zinc coatings are investigated, their naturally formed protective layers are electrochemically characterized and corrosion relevant values are determined by using a gel pad based on polysaccharide. From the results it is evident that gel-type electrolytes represent a viable and promising field in corrosion research. T2 - EUROCORR European Corrosion Congress 2016 CY - Montpellier, France DA - 11.09.2016 KW - Corrosion investigations KW - Gel-type electrolytes KW - Zinc coatings PY - 2016 SP - Paper P-56097 AN - OPUS4-37546 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wille, Frank A1 - Ballheimer, Viktor A1 - Quercetti, Thomas A1 - Sterthaus, Jens T1 - Package design assessment aspects of gaps between content and lid N2 - Type B(U) packages for the transport of radioactive material have to withstand accident conditions of transport defined in the regulations of the IAEA International Atomic Energy Agency in form of different mechanical (drop) tests with a subsequent thermal test. According to the regulatory requirements the orientation of the package in drop tests shall be such to cause the most damaged state in the components performing the safety functions. For the package lid system a 9-m drop onto the unyielding target with lid side downwards is often the most damaging orientation. The impact loads acting on the lid in this orientation result mainly from interaction between lid and internal content. In case of a movable content its impact onto the inner side of the lid can cause additional load peaks on the lid and the lid bolts. The intensity of the internal collision depends on the position of content relating to lid at the time of package first contact with target. Due to physical limitations an axial gap, which could be set in “pre-drop” configuration of package or which could spontaneously appear during the drop test, usually does not cover the maximum size possible in specific package design. In this context, the combination of drop tests with post-test analysis can be helpful to better estimate the effect of internal impact. The paper summarized some aspects of this issue based on the BAM experience in the design assessment of Type B(U) transport packages. Additionally the paper shall support applicants in German approval procedures to reduce rounds of questions and ensure delivery of reliable safety case documents to the authorities. International discussions of this issue at the IAEA and a joint proposal by France and Germany to improve Advisory Material text will be introduced. T2 - 18th International Symposium on the Packaging and Transportation of Radioactive Materials PATRAM 2016 CY - Kobe, Japan DA - 18.09.2016 KW - Lid behavior KW - Transport package KW - Secondary impact KW - Inventaraufprall KW - Fallprüfung PY - 2016 SP - 1 EP - 10 AN - OPUS4-37548 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Trappe, Volker A1 - Basan, Ricardo A1 - Grasse, Fabian ED - Paris, Federico T1 - Stiffness and fracture of shear loaded laminates with unidirectional and biaxial fibre orientation investigated with a picture frame test N2 - Fibre Reinforced Plastics (e.g. CFRP, GFRP) characteristically show nonlinear stress-strain behaviour due to intralaminar shear loading. The determination of the in-plane shear stiffness and strength for this class of material is difficult and common test standards and methods of analysis are partially inaccurate. The identification of the in-plane shear properties was made with an especial designed “picture frame test device” which enables shear loading up to 950N/mm. Therefore the strength limit can be reached at specimens with adequate thickness and a high safety factor against buckling. Due to the chosen design the maximum of the shear loading and the final failure occur in the centre of the specimen. The experiments match with the numerical analysis. T2 - ECCM16 - 16TH EUROPEAN CONFERENCE ON COMPOSITE MATERIALS CY - Seville, Spain DA - 22.06.2014 KW - Picture frame test KW - Fibre reinforced plastics (FRP) KW - Shear strength and stiffness KW - In-situ effect PY - 2014 SN - 978-84-616-9798-4 VL - 2014 SP - ID0263 - 1 EP - 8 PB - ECCM CY - Sevilla AN - OPUS4-37617 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gaal, Mate A1 - Bartusch, Jürgen A1 - Schadow, Florian A1 - Beck, Uwe A1 - Daschewski, M. A1 - Kreutzbruck, M. T1 - Airborne ultrasonic systems for one-sided inspection using thermoacoustic transmitters N2 - Airborne ultrasonic inspection is performed in through transmission, where the test piece (e.g. adhesive joint or polymer-based composite plate) is placed between the transmitter and the receiver. However, many structures with difficult shapes allow only one-sided inspection. The strong reflection of the signal from the surface overshadows the signals from the inside, so that broadband pulses are required. Thermoacoustic transmission, where the thermal energy of an electrically heated electrode is transformed into the acoustic energy of an ultrasonic wave, opens the possibility to excite broadband pulses and thus to inspect objects with one-sided access. We present various thermoacoustic transducers consisting of an electrically conductive film on a solid substrate. The first type of transducer is a transmitter with an indium-tin-oxide electrode on a glass substrate combined with a laser Doppler vibrometer as a receiver. The second type of transducer combines thermoacoustic transmission and piezoelectric reception, having a titanium electrode as a transmitter deposited onto charged cellular polypropylene serving as a piezoelectric receiver. Using a focusing thermoacoustic transmitter and a separate cellular polypropylene receiver, a through-transmission inspection of a 4 mm thick CFRP test piece with inserts as small as 1 mm was performed. The same emitter and a laser vibrometer as a receiver were used for a one-sided inspection of a Plexiglas block with a cross hole at 15 mm depth. A twin probe consisting of a thermoacoustic transmitter on a cellular polypropylene receiver was applied to a profile measurement on a step wedge with flat bottom holes. The smallest detected diameter of a flat bottom hole was 1 mm. Sound pressure level above 140dB was achieved with each of these transmitters. Thermoacoustic transmitters enable a step towards one-sided air-coupled ultrasonic inspection. T2 - IEEE International Ultrasonics Symposium CY - Tours, France DA - 18.09.2016 KW - Airborne KW - Air-coupled KW - Ultrasonic transducer KW - Thermoacoustic KW - Ferroelectret PY - 2016 SN - 978-1-4673-9897-8 SN - 1948-5719 SP - (online publication) 1 EP - 4 AN - OPUS4-37620 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maierhofer, Christiane A1 - Röllig, Mathias A1 - Steinfurth, Henrik A1 - Krankenhagen, Rainer A1 - Myrach, Philipp A1 - Mecke, R. A1 - Schiller, M. A1 - Seidl, T. A1 - Kernchen, A. A1 - Kalisch, U. A1 - Meinhardt, J. A1 - Hennen, C. A1 - Arnold, T. A1 - Groll, T. T1 - 3D-Kartierung von Bauwerksoberflächen mit optischen und thermografischen Verfahren N2 - In diesem Beitrag werden Verfahren und Strategien basierend auf optischen und thermografischen Methoden zur Lokalisierung, Erfassung und Bewertung von Putzablösungen, Ablösungen von Fassadenelementen und Rissen vorgestellt. Abgelöste Fassadenbereiche und Risse zeigen dabei sowohl geometrische als auch thermische Auffälligkeiten, die im Rahmen eines Monitoring auch über größere Zeiträume verfolgt werden können. Als optische Verfahren werden die trackingbasierte taktile 3D‐Erfassung von Oberflächenmerkmalen und die Stereophotogrammetrie eingesetzt. Zur Charakterisierung verdeckter Ablösungen und Bauteile wird die aktive Thermografie mit natürlicher und künstlicher Erwärmung der Bauteiloberfläche verwendet. Systematische Untersuchungen an Probekörpern und Fallstudien (Magdeburger Dom, Wandbild in Cobbelsdorf, Giebichensteinbrücke) zeigen, wie u. a. mit der Verfahrenskombination die Schäden charakterisiert werden können. T2 - Interdisziplinäre Forschung in der Denkmalpflege - 20 Jahre IDK - CY - Dresden, Germany DA - 31.05.2016 KW - Monitoring KW - Risse KW - Ablösungen KW - Aktive Thermografie KW - Optische 3D-Erfassung PY - 2016 SN - 978‐3‐9811706‐2‐7 SP - 141 EP - 156 CY - Dresden AN - OPUS4-37508 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schiller, M. A1 - Mecke, R. A1 - Trostmann, E. A1 - Maierhofer, Christiane A1 - Kalisch, U. A1 - Groll, T. A1 - Hennen, C. A1 - Meinhardt, J. T1 - Optische dreidimsionale Erfassung und Datenverarbeitung von Bauwerksoberflächen in der Denkmalpflege N2 - Im Beitrag werden Verfahren und Strategien für die dreidimensionale und zeitaufgelöste Erfassung und Darstellung von Veränderungen an Bauwerken und Skulpturen vorgestellt. Ablösungen und Verformungen können im Rahmen eines Monitoring über größere Zeiträume verfolgt werden. Anhand systematischer Untersuchungen an einer Fallstudie im Magdeburger Dom werden in diesem Beitrag die Vorgehensweise und Ergebnisse vorgestellt. Zudem kann mit diesen Verfahren auch der Zustand einer Skulptur nach einer Restaurierung dokumentiert werden. Eine dreidimensionale Erfassung kann weiterhin dazu verwendet werden, eine Kopie einer Skulptur mit einem 3D‐Druck‐Verfahren herzustellen. Dieses Verfahren wird in Bezug auf die Genauigkeit mit einem herkömmlich erstellten Gipsabdruck verglichen. T2 - Interdisziplinäre Forschung in der Denkmalpflege - 20 Jahre IDK - CY - Dresden DA - 31.05.2016 KW - Monitoring KW - Bauwerksoberflächen KW - optische 3D-Erfassung PY - 2016 SN - 978‐3‐9811706‐2‐7 SP - 157 EP - 164 CY - Dresden AN - OPUS4-37509 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maierhofer, Christiane A1 - Rothbart, Nick A1 - Goldammer, M. A1 - Hohlstein, F. A1 - Koch, J. A1 - Kryukov, I. A1 - Mahler, G. A1 - Stotter, B. A1 - Walle, G. A1 - Oswald-Tranta, B. A1 - Sengebusch, M. T1 - A round robin test of flash thermography – detectability and quantification of artificial and natural defects in CFRP and metal structures N2 - Within the scope of a DIN INS project, a flash thermography round robin test that evaluates reliability, comparability, and efficiency of different testing situations was organized. The results give information about the detectability of defects, e.g. depending on their size and depth, the evaluation methods and the materials used. Besides, the influences of equipment and parameters used by the participants on the results were analysed. All of the quantitative results as well as the feedback given by the participants will be presented in a DIN committee in order to contribute to a flash thermography standard. T2 - Conference QIRT 2016 CY - Gdansk, Poland DA - 04.07.2016 KW - Active thermography KW - Flash excitation KW - Round robin test KW - CFRP KW - Metal PY - 2016 UR - http://qirt.gel.ulaval.ca/archives/qirt2016/papers/075.pdf DO - https://doi.org/10.21611/qirt.2016.075 SN - 2371-4085 SP - Paper 075, 517 EP - 526 CY - Quebec, Canada AN - OPUS4-37510 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Karsten A1 - Favre, A. A1 - Hilbert, F. A1 - Quercetti, Thomas A1 - Neumeyer, Tino A1 - Weingart, Barbara T1 - Prototype testing of a protective structural packaging for 30B cylinder N2 - Three drop test campaigns have been performed with DN 30 Protective Structural Packaging (PSP) developed by DAHER NUCLEAR TECHNOLOGIES GmbH for the transport of natural, enriched and reprocessed uranium hexafluoride (up to 5 wt%) in 30B cylinders. The mechanical prototype testing is intended to demonstrate that the package DN30 complies with regulatory requirements under normal and hypothetical accident conditions of transport (NCT, ACT) relevant to IF, AF and B(U)F packages, respectively. The paper includes the results of the latest test campaign carried out in 2015-2016 at the drop test facility of BAM, Germany with new full scale prototypes of the DN30 PSP and 30B cylinders. Repetition of drop test sequences became necessary after changing to Polyisocyanurate foam as shock absorbing material with variable foam densities. Furthermore, the mechanical behavior of the UF6 content of the 30B cylinder is now simulated by a mixture of cement and steel grid as modified surrogate material; instead of small steel balls. The behavior of this new content simulation is assumed to be more realistic with respect to the properties of real UF6. T2 - PATRAM 2016, 18th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Kobe, Japan DA - 18.09.2016 KW - Drop test KW - Packaging KW - Radioactive material KW - Uranium hexafluoride PY - 2016 SP - Paper 1018, 1 EP - 11 PB - INMM CY - Deerfield, Illinois, USA AN - OPUS4-37568 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holstein, R. A1 - Müller, Christina T1 - Analyzing the reliability of non-destructive tests using the modular modell - a practical approach N2 - Non-destructive testing is an important tool to guarantee the safety of railway traffic. The infrastructure with tracks, switches and sleepers is regularly tested, the locomotives and wagons with their wheels, bogies and axles as well. Many years of experience and some events lead in Germany to a good practice in testing the railway components. Now, European authorities are drafting a system of common requirements and standards for the European Railway Market. The German practice combines an intensive training of the NDT-personnel including sufficient time for practical exercises with organizational measures of the companies, responsible for rolling stock and infrastructure. Through the example of UT-testing of railway axles it will be shown, how training and organizational measures influence the reliability of such testing. T2 - 19th World Conference on Non-Destructive Testing CY - München, Germany DA - 13.06.2016 KW - NDT KW - Reliability KW - Modular model KW - Railway KW - Human factors PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-375712 UR - http://www.ndt.net/article/wcndt2016/papers/mo1d4.pdf SP - id 19519, 1 EP - 6 AN - OPUS4-37571 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kanzler, D. A1 - Müller, Christina T1 - Evaluating RT systems with a new POD approach N2 - The usefulness and purpose of evaluating nondestructive testing (NDT) systems and their capabilities has changed in the last decade. The conventional method of simply applying a familiar statistical algorithm to say whether the system is usable for the tasks is history. Nowadays, multiple parameter methods which describe the probabilities of detection (POD) of different systems or real defects need new characteristics and a broader variety of statistical models to describe the true system behaviour. The appraisal of the NDT system involves diverse departments within a company (engineering, NDT-operators, and statisticians), but is, at the same time, more needed and requested than in the past. In this article, an approach is discussed in which professionals from different fields worked well together, accomplishing cost-intensive metallographic studies in correlation with well-understood physical behaviour of NDT-methods as well as deep-discussed mathematical methods to create a holistic evaluation of the technical reliability for a specific radiographic testing (RT) equipment. The first part of the publication will show the comparison between metallographic grinding and the RT indications. An essential innovation over past evaluation methods was the use of a multi-scale smoothing algorithm, which describes physical parameters, which were not used in evaluation like the POD in this way in the past. In the second part the statistical requirements for the POD take the focus. It can often be hard to make significant statements; especially in the case where only a small amount of data is available. The combination of data and the use of knowledge from simulations are essential. One possible solution will be shown for the RT evaluation. The methodology is used for evaluating the digital RT system for the inspection of electron-beam welds, which was method considered to seal the Finnish copper canisters for the final deposit of spent nuclear fuel. T2 - 19th World Conference on Non-Destructive Testing CY - München, Germany DA - 13.06.2016 KW - NDT KW - Reliability KW - POD KW - RT PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-375732 UR - http://www.ndt.net/article/wcndt2016/papers/we1d4.pdf SP - id 19535, 1 EP - 8 AN - OPUS4-37573 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Quercetti, Thomas A1 - Müller, Karsten A1 - Musolff, Andre A1 - Nakagami, M. A1 - Komatsuki, S. A1 - Tamaki, H. A1 - Kishimoto, J. A1 - Fujisawa, K. A1 - Nishio, T. ED - Quercetti, Thomas T1 - Experimental testing of RAM packages within Japanese German projects N2 - In context with Japanese disposal and transport container safety assessment the German Federal Institute for Materials Research and Testing (Bundesanstalt für Materialforschung und -prüfung) per-formed extensive drop test series with prototypes of RAM packages in recent years. The paper presents two cooperative projects focused on project management, testing performance and experimental results. In the first project, a full-scale prototype of a package for transport and storage of spent fuel elements with a total mass of 127,000 kg and its reduced-scale model which was similar to the prototype in both geometry and design were drop tested in 9 m and 1 m puncture tests at various drop orientations under regulatory conditions. In context with a corresponding research project the test data was used in combination with numerical methods to investigate the phenomenon of internal cask- content collisions during drop tests. Here, technological gaps between basket or radioactive content and cask body or primary lid can be a reason for significant high dynamic loadings of cask components and its internals due to additional impact interactions in the cask cavity caused by inner relative movement between content and cask. Further investigations were carried out in the field of similarity mechanics comparing experimental drop test data of the full-scale prototype and reduced-scale model in regard to the transferability of package impact response from reduced-scale models to full-scale packages. In the second project, drop tests with a waste container for intermediate depth disposal were per-formed being contracted by Kobe Steel, Ltd. and a consortium of Japanese electric power plant com-panies. The drop test program comprised three single 8-m drop tests in a specimen’s corner edge orientation. For drop tests according to legal regulations for interim storage or final disposal it is often necessary to use a target which represents the real ground of the storage facility. In such cases the container hits directly onto a well-defined concrete slab on top of the IAEA target. Here, the directly impact target for the drop tests were concrete slabs manufactured in Japan and connected by mortar to the impact pad of the unyielding IAEA target. KW - Drop testing KW - Package PY - 2016 SP - Paper 1043, 1 EP - 13 CY - Kobe, Japan AN - OPUS4-37557 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - August, Hans A1 - Salewski, Dieter A1 - Walentowski, Heinz-Ulrich T1 - Untersuchungen zur Erkennung von Regeneratzusätzen in Formteilen aus typisierten und überwachten Formmassen T2 - Kolloquium "Duroplaste" CY - Bad Mergentheim, Germany DA - 16.03.1983 PY - 1983 SP - 41 EP - 56 AN - OPUS4-37559 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wehrstedt, Klaus-Dieter T1 - Self-Accelerating Decomposition Temperature (SADT) von Azobisisobutyronitril (AIBN) N2 - Im Vortrag wird über Untersuchungen zur thermischen Stabilität (Bestimmung der SADT = Self-Accelerating Decomposition Temperature) von 2,2‘-Azobisisobutyronitril (AIBN) in realen Packstücken unterschiedlicher Größe sowie in Dewar-Gefäßen berichtet. Die Packstücke mit 5 kg, 20 kg bzw. 50 kg AIBN wurden nach der UN-Methode H.4 untersucht, die Versuche mit den Dewar-Gefäßen nach UN-Methode H.4. Zusätzlich wurden experimentelle Daten mittels DSC (Differential Scanning Calorimetry) unter Verwendung druckfester Gefäße bestimmt. Die experimentellen Daten wurden für weitergehende Untersuchungen/Simulationen unter Verwendung realer kinetischer Modelle bereitgestellt. Letztendlich konnte nachgewiesen werden, dass mittels Simulation die SADT von AIBN in Abhängigkeit von der Packstückgröße sehr genau, d. h. in guter Übereinstimmung mit den Packstückversuchen, bestimmt werden kann. T2 - ProcessNet-Arbeitsausschusses Reaktionstechnik sicherheitstechnisch schwieriger Prozesse CY - Darmstadt, Germany DA - 03.05.2016 KW - thermische Stabilität KW - SADT KW - 2,2‘-Azobisisobutyronitril (AIBN) KW - UN-Methode H.4 PY - 2016 AN - OPUS4-37190 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mann, Guido A1 - Krüger, Jörg ED - Jitsuno, T. ED - Shao, J. ED - Rudolph, W. T1 - Nanosecond laser damage of optical multimode fibers N2 - For pulse laser materials processing often optical step index and gradient index multimode fibers with core diameters ranging from 100 to 600 μm are used. The design of a high power fiber transmission system must take into account limitations resulting from both surface and volume damage effects. Especially, breakdown at the fiber end faces and self-focusing in the fiber volume critically influence the fiber performance. At least operation charts are desirable to select the appropriate fiber type for given laser parameters. In industry-relevant studies the influence of fiber core diameter and end face preparation on laser-induced (surface) damage thresholds (LIDT) was investigated for frequently used all-silica fiber types (manufacturer LEONI). Experiments on preform material (initial fiber material) and compact specimens (models of the cladding and coating material) accompanied the tests performed in accordance with the relevant LIDT standards ISO 21254-1 and ISO 21254 2 for 1-on-1 and S-on-1 irradiation conditions, respectively. The relation beam diameter vs. LIDT was investigated for fused silica fibers. Additionally, laser-induced (bulk) damage thresholds of fused silica preform material F300 (manufacturer Heraeus) in dependence on external mechanical stress simulating fiber bending were measured. All experiments were performed with 10-ns laser pulses at 1064 and 532 nm wavelength with a Gaussian beam profile. T2 - Pacific Rim Laser Damage 2016 CY - Yokohama, Japan DA - 18.05.2016 KW - laser damage KW - optical fiber KW - nanosecond laser KW - fused silica PY - 2016 DO - https://doi.org/10.1117/12.2238515 VL - 9983 SP - 99830T AN - OPUS4-37140 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weise, Frank A1 - Meng, Birgit A1 - Pirskawetz, Stephan A1 - Voland, K. T1 - Influence of simultaneous cyclic loading and external alkali supply on the alkali-silica reaction in concrete pavements N2 - In recent years the German motorway network has seen an increase in the occurrence of damage to concrete road surfaces which can be attributed to the alkali-silica reaction (ASR). In view of the often drastically reduced life expectancy of road surfaces due to ASR, research activity in this field has notably increased. Alongside preventative measures in concrete technology, the main research focus up to now has been the development of performance-oriented testing procedures for ASR prevention. This included more specifically the accelerated simulation of climatic effects and external alkali penetration on road surfaces. The effects of mechanical pre-damage resulting from cyclic traffic loading and climatic impact had previously not been taken into consideration. Since 2011, the five-partner research group 1498 sponsored by the German Research Foundation (DFG) has been pursuing research on how simultaneous cyclic loading and external alkali penetration impacts destructive ASR in road surface concretes. The depiction of the myriad degradation and transport processes necessary for an understanding of these effects requires close interaction between experiments and their multi-scale modelling. This paper aims to focus on the aforementioned experiments by means of innovative testing techniques. The research is founded on a series of cyclic fatigue tests performed on large-format beams, both with and without previous application of a sodium chloride (NaCl) solution, with simultaneous tracking of crack development. Subsequently, smaller test specimens were extracted from the pre-damaged beams for further experiments. These included the spatial visualization and quantification of fatigue-induced cracks using micro X-ray 3D-computed tomography (3D-CT). Additionally, the effects of fatigue-induced cracks on alkali transport were investigated using Laser-Induced Breakdown Spectroscopy (LIBS). Subsequent storage of the small-format test specimens, with and without cyclic pre-damage, in an ASR-conducive environment then provided initial findings on the influence of fatigue-induced predamage on the ASR. T2 - 15th International Conference on Alkali-Aggregate reaction (ICAAR 2016) CY - Sao Paulo, Brazil DA - 03.07.2016 KW - concrete pavements KW - alkali-silica-reaction KW - fatigue KW - damage monitoring PY - 2016 SP - Paper 191 AN - OPUS4-37142 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Werner, Daniel A1 - Meng, Birgit A1 - Weise, Frank T1 - Influence of aggregate size on the damage potential of alkali-silica reaction N2 - The susceptibility of different aggregate types used in concrete to ASR is strongly associated with their petrography. The aim of this study is to assess the influence of the aggregate size on the ASR potential, in particular applied to the sand fractions in the size range of 0.125-4 mm. The investigation concept is based on the hypothesis that at a specific particle size reactive aggregates could change their characteristic influence in mitigating ASR instead of promoting it. For the study of the size dependent behaviour mortars are prepared, considering aggregates of different reactivity, including very reactive, slow-late and quasi non-reactive types. The analysis is based on a stepwise substitution concept, in which mortars with a constant overall grain size distribution are compared, while only one size fraction of the non-reactive base aggregate is substituted by a reactive aggregate type of this specific size fraction. For the expansion experiments an accelerated mortar bar test (80°C, immersed in NaOH solution) was applied. The results show that the slow-late reactive greywacke yielded a strong reduction of the expansion below an aggregate size in the range of 0.5-1 mm. On the other side with the very reactive borosilicate glass, the expansions increased steadily with decreasing size. To validate if the acquired expansions were caused by ASR, thin sections were analysed. Mainly, higher expansion values were consistent with extensively more amounts of ASR indicators. T2 - 15th International Conference on Alkali-Aggregate Reaction (ICAAR 2016) CY - Sao Paulo, Brazil DA - 03.07.2016 KW - alkali-silica-reaction KW - building materials KW - concrete KW - durability PY - 2016 SP - Paper 194 AN - OPUS4-37143 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Na, S.-J. A1 - Han, S.-W. A1 - Muhammad, S. A1 - Zhang, L. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael A1 - Karhu, M. A1 - Kujanpa, V. T1 - Flow and Bead Formation Characteristics in High Power Laser Welding at Different Welding Positions (Invited Talk) N2 - The numerical simulations of high power laser keyhole welding at different welding positions are performed by using Volume-Of-Fluid (VOF) method. The main material is SS400. The multi-physics phenomenon is considered using several models, such as the heat flux of Gaussian heat source, the recoil pressure with Clausisus-Clapeyron equation, the Marangoni flow considering temperature gradient, the buoyancy force with Boussinesq approximation, the additional shear stress and heat source due to metallic vapor ejected through keyhole entrance, the bubble formation assumed as adiabatic bubble, and the multiple-reflection by solving proper discriminant, are used. To analyze the fluid flow pattern, the concept of streamline formed by reconstructing the value of the velocity vector is applied. Partial and full penetration cases at different welding positions are considered. The welding position seems to have only a minor influence on bead formation characteristics in both cases. This is probably due to the fact that the recoil pressure has a major influence when compared to other driving forces. The flow characteristics and fluid velocity in weld pool are analyzed to compare the gravity direction effect at different welding positions. It is observed that the clockwise flow pattern is mainly formed by the recoil pressure on the keyhole surface in the case of partial penetration. The laser energy can't maintain the whole weld pool when the weld pool size becomes too large. And then the solidification starts from the middle part of weld pool and a necked weld pool shape is formed. In the full penetration welding, the weld pool flow patterns are affected by the leakage of laser power through the full penetration keyhole and also by surface tension. Furthermore, the numerical simulation of full penetration welding with AISI316L is also performed to analyze the effect of material properties. The weld bead shapes obtained by simulations were compared with the corresponding experimental results to confirm the validity of the process models adopted and the CFD simulation tool. T2 - Lasers in Manufacturing Conference 2015 CY - München, Germany DA - 22.06.2015 KW - Macro Processing (Joining, Welding) KW - Weld pool KW - Flow pattern KW - Different welding position KW - Numerical simulation KW - High power laser keyhole welding PY - 2015 SP - 1 EP - 6 AN - OPUS4-37163 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Altenburg, Simon A1 - Krankenhagen, Rainer A1 - Weber, H. T1 - Thickness determination of semitransparent isolated solids using the flash method and an analytical model N2 - As groundwork for thickness determination of polymeric surface protection systems for concrete, we present a method for measuring the thickness of isolated semitransparent solids using pulse thermography both in Transmission and reflection geometry. Since standard models do not capture semitransparency, an advanced analytical model by Salazar et al. is applied. Physical material parameters are deduced by fitting experimental data from samples of well-known thickness. Using those, the thickness of samples of the material can be obtained by fitting, as demonstrated for different semitransparent polymer materials. T2 - QIRT 2016 CY - Gdańsk, Poland DA - 04.07.2016 KW - Analytical model KW - Concrete KW - Flash thermography KW - Semitransparency KW - Surface protection KW - Thermography KW - Thickness PY - 2016 DO - https://doi.org/10.21611/qirt.2016.001 SN - 2371-4085 VL - 2016 SP - 71 EP - 78 AN - OPUS4-37200 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wosniok, Aleksander A1 - Sporea, D. A1 - Neguţ, D. A1 - Krebber, Katerina T1 - Gamma radiation influence on silica optical fibers measured by optical backscatter reflectometry and Brillouin sensing technique N2 - We have studied the influence of gamma rays on physical properties of different commercially available silica optical fibers stepwise irradiated up to a total dose of 100 kGy. The detection of radiation-induced changes in silica glass offers the possibility of using selected optical fibers as distributed radiation sensors. The measurements performed by us were based on optical backscatter reflectometry and Brillouin distributed sensing. The measurement methods enable an analysis of radiation-induced modification of the group refractive index and density of the optical fibers. The most distinct physical effect observed by us concerns the increase of the optical attenuation with rising total radiation doses. Quantitative measurement results indicate a crucial impact of fiber dopants on radiation-induced physical and sensory characteristics of silica optical fibers affected by differences in fiber fabrication techniques. Based on the obtained results, the suitability of distributed Brillouin sensing for dosimetry applications seems to be improved by modifying the refractive index profile of the fiber core. T2 - Sixth European Workshop on Optical Fibre Sensors CY - Limerick, IRL DA - 31.05.2016 KW - Brillouin frequency shift KW - Lonizing radiation KW - Gamma radiation KW - Radiation dosimetry KW - Optical fiber sensor KW - Brillouin scattering KW - Distributed measurement KW - Backscatter reflectometry PY - 2016 SN - 978-1-5106-0219-9 DO - https://doi.org/10.1117/12.2236678 SN - 0277-786X VL - 9916 SP - Article Number: 99162J PB - Spie-Int Soc Optical Engineering CY - Bellingham, WA, USA AN - OPUS4-37083 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz ED - Pombo, Joao T1 - Vehicle-track-soil interaction for track damage, ground vibration and mitigation N2 - A combined finite element boundary element method has been developed to calculate the dynamic interaction of the railway track and the underlying soil. The track-soil results are coupled with a simple vehicle model to establish the force transfer function of the vehicle-track-soil system. Mitigation measures at the track, namely three different tracks with under-sleeper pads, are analysed. The un-sprung vehicle and heavy track masses on soft track elements yield a lower vehicle-tracksoil resonant frequency and a better reduction of the excitation forces at higher frequencies. If the effectiveness of the mitigation is measured as a vibration ratio between the isolated and an un-isolated reference track, the vehicle-track-soil resonance of the reference track has an important influence on the mitigation effectiveness. Therefore, different un-isolated reference tracks are analysed. It is shown how the frequency and amplitude of the vehicle-track resonance are influenced by the stiffness of the rail pads (strongest), the ballast (medium) and the soil (weakest). The reference track models have been compared with shaker tests on two railway tracks with strong resonances. The damage detection and repair control have become important tasks for ballast and slab tracks. Measurements which compare the damaged and the repaired status of the same track section at different times, or which compare a damaged and an intact track section at the same time, have been successfully performed at some sites in Germany and compared with the theoretical behaviour of intact and damaged tracks. T2 - 3. International Conference on Railway Technology CY - Cagliari, Italy DA - 05.04.2016 KW - undersleeper KW - railway track KW - track-soil interaction KW - ground vibration KW - mitigation PY - 2016 SN - 978-1-905088-65-2 SN - 1759-3433 SP - Paper 273 EP - 19 PB - Civil-Comp Press CY - Stirlingshire, Scotland AN - OPUS4-37084 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz ED - Vogiatzis, Konstantinos T1 - Modes and waves of coupled roof or floor structures in historical and modern buildings N2 - Long wooden floor beams above a ball room in an old historical palace have been analysed experimentally. The eleven beams are weakly coupled by three layers of floor boards. It has been investigated if the state (the stiffness) of the wooden beams can be determined by vibration measurements of global or preferably local modes. Hammer, heel-drop and ambient excitations have been used. The vibration modes of the structure show dominating local deformations if an impact excitation is applied. This is understood as the positive superposition of several modes which yield the maximum at the excitation point but a cancellation at more distant points. Natural modes have been estimated from these vibration modes by standard and special methods which were necessary for the high damping of the wooden floor. It has been found that all floor beams contribute to each natural mode even for a weak coupling of the beams. In addition to the modal discussion, the impact tests have also been analysed for the wave propagation and amplitude attenuation with distance. The coupling of floor beams has been studied theoretically by an analytic multiple-beam model where the coupling by translational or rotational springs and by a common support motion has been assumed. T2 - 23. International Congress on Sound and Vibration CY - Athen, Greece DA - 10.07.2016 KW - modal analysis KW - floor vibration KW - wave analysis PY - 2016 SN - 978-960-99226-2-3 SN - 2329-3675 SP - Paper 318, 1 EP - 8 AN - OPUS4-37090 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maierhofer, Christiane A1 - Krankenhagen, Rainer A1 - Röllig, Mathias A1 - Riemer, Stefanie A1 - Gower, M. A1 - Baker, G. A1 - Lodeiro, M. A1 - Knazovicka, L. A1 - Blahut, A. A1 - Monte, C. A1 - Adibekyan, A. ED - Gutschwager, B. T1 - Characterisation of artificial and natural defects in fibre reinforced plastics designed for energy applications using active thermography N2 - Amongst various other NDT methods, within the EMRP-project ‘VITCEA’ active thermography is validated for testing of CFRP and GFRP structures constructed for energy application. In this contribution, the optical and thermal properties of CFRP and GFRP reference defect artefact (RDA) and natural defects artefact (NDA) test specimens are characterized. Different excitation techniques and techniques for data analysis are compared for optimizing the number of detected defects. T2 - 19th World Conference on Non-destructive Testing (WCNDT) CY - Munich, Germany DA - 13.06.2016 KW - Active thermography KW - CFRP KW - GFRP KW - Artificial and natural defects PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-370207 UR - http://www.ndt.net/article/wcndt2016/papers/we2i4.pdf SN - 978-3-940283-78-8 VL - BB 158 SP - Paper we2i4, 1 EP - 9 PB - DGZfP CY - Berlin AN - OPUS4-37020 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Götschel, S. A1 - Höhne, Christian A1 - Kolkoori, Sanjeevareddy A1 - Mitzscherling, Steffen A1 - Prager, Jens A1 - Weiser, M. T1 - Ray tracing boundary value problems: simulation and SAFT reconstruction for ultrasonic testing N2 - The application of advanced imaging techniques for the ultrasonic inspection of inhomogeneous anisotropic materials like austenitic and dissimilar welds requires information about acoustic wave Propagation through the material, in particular travel times between two Points in the material. Forward ray tracing is a popular approach to determine traveling paths and arrival times but is ill suited for inverse problems since a large number of rays have to be computed in order to arrive at prescribed end points. In this contribution we discuss boundary value problems for acoustic rays, where the ray path between two given points is determined by solving the Eikonal equation. The implementation of such a two Point boundary value ray tracer for sound field simulations through an austenitic weld is described and its efficiency as well as the obtained results are compared to those of a forward ray tracer. The results are validated by comparison with experimental results and commercially available UT simulation tools. As an application, we discuss an implementation of the method for SAFT (Synthetic Aperture Focusing Technique) reconstruction. The ray tracer calculates the required travel time through the anisotropic columnar grain structure of the austenitic weld. There, the formulation of ray tracing as a boundary value Problem allows a straightforward derivation of the ray path from a given transducer Position to any pixel in the reconstruction area and reduces the computational cost considerably. T2 - 19th World Conference on Non-Destructive Testing 2016 CY - München, Germany DA - 13.06.2016 KW - Ultrasonic testing KW - SAFT KW - Ray tracing KW - Simulation PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-370494 UR - www.ndt.net/?id=19437 SP - ID 19437, 1 EP - 8 AN - OPUS4-37049 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilke, Olaf A1 - Jann, Oliver T1 - Emissions of very volitale organic compounds (VVOC) from particle boards N2 - The latest version of the German AgBB evaluation scheme (2015) for construction products includes some VVOC, e.g. formaldehyde, acetaldehyde and acetone. For these VVOC so-called LCI values (lowest concentration of interest) were derived which are used for the calculation of the so-called R-value (risk index, see reference 1 for the calculation). Test chamber measurements of particle boards show that the emissions of VVOC might have significant impact on the R-value and therefore for the health evaluation. T2 - The 14th international conference of Indoor Air Quality and Climate, Indoor Air 2016 CY - Gent, Belgium DA - 03.07.2016 KW - Formaldehyde KW - AgBB evaluation scheme KW - Particle board KW - OSB KW - VVOC KW - Emission test chamber PY - 2016 SP - Paper 965, 1 AN - OPUS4-37030 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Preissel, Marcel A1 - Vrana, J. T1 - Ermittlung der Auffindwahrscheinlichkeit von Reflektoren in Abhängigkeit der Rastergröße bei der Ultraschallprüfung großer Schmiedestücke N2 - Die Auswirkung des Prüfrasters nach der DGZfP Richtlinie US 07:2014 auf die Auffindwahrscheinlichkeit von Reflektoren wird untersucht. Hierzu werden Simulationsrechnungen durchgeführt, mit dem Ziel, die Abhängigkeit der Unterbewertung von Größe und Tiefenlage von Reflektoren in Bezug auf das Prüfraster zu ermitteln und experimentell zu überprüfen. In zwei Simulationsreihen wird der Einfluss des Prüfrasters auf die Suche von Anzeigen und auf die Bewertung von Anzeigen ermittelt und bewertet. Auf Basis der Simulationsrechnungen wird eine POD-Analyse mit dem Ziel durchgeführt, die Auffindwahrscheinlichkeit von Reflektoren in Bezug zur Rastergüte Rn zu setzten und die Nachweisgrenze zu ermitteln. KW - Schmiedeteile KW - Ultraschall KW - Probability of detection KW - Prüfraster PY - 2016 UR - http://www.dgzfp.de/Dienste/ZfP-Zeitung IS - 150 SP - 52 EP - 57 AN - OPUS4-37032 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pech, Anja A1 - Wilke, Olaf A1 - Horn, Wolfgang A1 - Jann, Oliver T1 - Analysis of very volatile organic compounds (VVOC) with thermal desorption GC-MS N2 - Most VVOC were rarely considered in the evaluation of construction products. (Salthammer, 2014) In Germany this will change because the latest version of the German AgBB scheme for health evaluation (2015) now include VVOC, e.g. ethyl acetate and ethanol. In this study selected compounds were tested with the procedure described in ISO 16017 and a method for measuring VVOC with thermal desorption was developed. Three different adsorbents Tenax TA, Carbograph 5TD and Carbopack X were tested to analyse VVOC according to ISO 16017. For the tested VVOC, Carbograph 5TD showed the best results under the chosen analytical conditions. T2 - Indoor Air 2016, The 14th international conference of Indoor Air Quality and Climate CY - Gent, Belgium DA - 03.07.2016 KW - Thermal desorption KW - VVOC KW - Carbograph 5TD KW - Carbopack X PY - 2016 SP - Paper 889, 1 EP - 2 AN - OPUS4-37035 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Liehr, Sascha A1 - Krebber, Katerina T1 - Applications and prospects for distributed sensing using polymer optical fibres N2 - One of the unique advantages of polymer optical fibres (POF) is that they can be used to measure very high strain values up to 100 % and beyond exceeding the strain limits of silica fibre-based sensor principles. In this paper the distributed strain measurement capabilities of POF based on backscatter change evaluation are summarized and distributed backscatter measurement technologies are intro-duced. Application examples in the structural health monitoring (SHM) field are presented: a promising approach is the integration into technical textiles for high-strain measurement in earthwork structures and crack detection in buildings. The potential of POF for future applications in SHM such as distributed relative humidity sensing is discussed. T2 - International Conference on Smart Infrastructure and Construction CY - Cambridge, UK DA - 27.06.2016 KW - Strain measurement KW - Structural health monitoring KW - OTDR KW - Polymer Optical Fibre KW - Distributed sensing PY - 2016 UR - http://www.icevirtuallibrary.com/doi/abs/10.1680/tfitsi.61279.093 SN - 978-0-7277-6127-9 DO - https://doi.org/10.1680/tfi tsi.61279.093 SP - 93 EP - 98 PB - ICE Publishing CY - London, UK AN - OPUS4-37230 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzlöhner, Ulrich T1 - Modellversuchstechnik T2 - Meßtechnik im Erd- und Grundbau CY - Munich, Germany DA - 23.11.1983 PY - 1983 SP - 119 EP - 126 CY - Essen AN - OPUS4-37373 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Müller, C. A1 - Meyer, A. A1 - Halle, T. ED - Lampke, T. ED - Wagner, G. ED - Wagner, M. F.-X. T1 - Einfluss von Stickstoff auf Mikrostruktur und Korrosionsverhalten martensitischer nichtrostender Stähle N2 - Die Korrosionsbeständigkeit martensitischer nichtrostender Stähle (MNS) wird wesentlich von der chemischen Zusammensetzung und dem Wärmebehandlungszustand beeinflusst. Beides bestimmt die Verteilung der Legierungselemente im Gefüge und die daraus resultierenden Werkstoffeigenschaften. Das Legieren mit Stickstoff bewirkt im Allgemeinen eine Verbesserung der Lochkorrosionsbeständigkeit von nichtrostenden Stählen. Bei martensitischen nichtrostenden Stählen ist dieser Effekt nicht nur auf den Stickstoffgehalt selbst zurückzuführen, sondern auch auf den gleichzeitig verringerten Kohlenstoffgehalt, der ebenfalls das Ergebnis der Wärmebehandlung beeinflusst. In dieser Arbeit wird der Einfluss von Stickstoff auf die Korrosionsbeständigkeit in Bezug zum Härtungsprozess von MNS dargestellt. Dazu wird vergleichend der Effekt von Austenitisierungsdauer, -temperatur und Abkühlgeschwindigkeit auf Gefüge, Härte und Korrosionsbeständigkeit der MNS X50CrMoV15 und X30CrMoN15 1 untersucht. Die Abkühlgeschwindigkeit wurde mit dem Stirnabschreckversuch gezielt variiert, um den Einfluss von Abkühlgeschwindigkeiten von > 100 K/s bis 1 K/s zu charakterisieren. Die Veränderungen der Korrosionsbeständigkeit werden durch die elektrochemisch potentiodynamische Reaktivierung (EPR) und durch die Bestimmung kritischer Lochkorrosionspotentiale dokumentiert. Neben diesem experimentellen Ansatz werden auch die Ergebnisse von thermodynamischen Berechnungen mit der Software Thermocalc vorgestellt und abschließend auch zur Interpretation des Einflusses von Stickstoff auf die Korrosionsbeständigkeit martensitischer nichtrostender Stähle genutzt. T2 - 18. Werkstofftechnisches Kolloquium der TU Chemnitz CY - Chemnitz, Germany DA - 10.03.2016 KW - Korrosionsbeständigkeit KW - Corrosion resistance KW - Wärmebehandlung KW - Heat treatment KW - Nichtrostende Stähle KW - Stainless steels KW - Thermocalc KW - Thermocalc PY - 2016 SN - 978-3-00-052212-3 SN - 1439-1597 VL - 59 SP - 325 EP - 336 PB - TU Chemnitz, Fakultät für Maschinenbau, Institut für Werkstoffwissenschaft und Werkstofftechnik CY - Chemnitz AN - OPUS4-37263 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beck, Uwe ED - Baier, Jennifa ED - Sahre, Mario ED - Weise, Matthias ED - Dähne, L. ED - Lerche, K.-H. T1 - Plasma Compatibility of Particles for Functional PVD-coatings by ex-situ Injection - Stability of Particles under Plasma Conditions N2 - The validation of the plasma compatibility of particles is a prerequisite for their application in plasma dispersion layers. The goal is the realization of functional add-on features on surfaces, in films and coatings. Although intended applications primarily address nanoparticles, the compatibility tests were carried out at first with particles in the lower micrometer range in order to investigate material-, fluorescent marker- or surface-based degradation effects in a simple manner. Plasma compatibility implies at least the short-term acceptance of charged species, plasma-UV radiation, vacuum and elevated temperatures. Otherwise, effects on geometrical dimensions, chemical bonds, fluorescence efficiency and plastic-elastic properties are expected. The plasma compatibility of monodisperse fluorescent-labeled particles to microwave excitation was evaluated by means of microscopic and spectroscopic investigation methods (light, fluorescence, confocal, atomic force microscopy and FTIR). This study comprises particles of different materials (SiO2, PMMA, PS, MF) and sizes (from 50 nm to 10 μm). A special preparation technique ensures that smallest geometry changes of particles can be measured by atomic force microscopy. For the selected plasma conditions (P = 600 W, f = 2.46 GHz, d = 10 cm) and an exposure time of 10 minutes, the geometry of SiO2 particles (approx. 1.7 μm) remains nearly unchanged, whereas PS particles shrink in diameter by 6% and PMMA particles by 11%. For selected core-particles (SiO2, MF) with fluorescencemarked (rhodamine) shell-polyelectrolytes no remarkable plasma degradation of the fluorescence intensity was observed for the above mentioned plasma conditions, however a doubling of exposure time already results in a significant decrease in intensity. Two different injection systems have been studied for the particle injection into the plasma deposition process. One of the selected systems also proves process compatibility regarding the expected pressure differences upon injection. T2 - PARTEC 2016, International Congress on Particle Technology CY - Nürnberg, Germany DA - 19.04.2016 KW - plasma dispersion layers KW - functional PVD coatings KW - particle injection PY - 2016 SN - 978-3-18-092283-6 SN - 0083-5560 SP - 6. Applications of Particle Technology/6.11_Beck_Uwe PB - VDI Wissensforum GmbH CY - Düsseldorf AN - OPUS4-37265 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Genga, R. M. A1 - Cornish, L. A. A1 - Woydt, Mathias A1 - van Vuuren, J. A1 - Polese, C. T1 - NbC: A machining alternative for dry and MQL face-milling of grey cast rion (GCI) N2 - NbC was studied as the major carbide phase with Ni and Co binders, produced by both spark plasma sintering (SPS) and liquid phase sintering (LPS), and tested as cutting inserts during dry and MQL (Minimum quantity lubrication) face-milling of grey cast iron (GCI) (BS 1452, Grade 17). T2 - World PM2016 CY - Hamburg, Germany DA - 09.10.2016 KW - Niobium carbide KW - NbC KW - Machining KW - Spark plasma sintering (SPS) KW - Liquid phase sintering (LPS) PY - 2016 SN - ISBN 978-1-899072-47-7 SP - 1 EP - 6 AN - OPUS4-37889 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Huang, S. G. A1 - Vleugels, J. A1 - Mohrbacher, H. A1 - Woydt, Mathias T1 - Influence of VC and Mo2C on the microstructure and mechanical properties of Ni bonded NbC-cermets N2 - The current study reports on the effect of VC and Mo2C carbides on the microstructure and mechanical properties of Ni bonded NbC cermets. T2 - World PM2016 CY - Hamburg, Germany DA - 09.10.2016 KW - Niobium carbide KW - NbC KW - Liquid phase sintering (LPS) KW - Hard materials PY - 2016 SN - ISBN 978-1-899072-47-7 SP - 1 EP - 7 AN - OPUS4-37891 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dmitriev, A.I. A1 - Österle, Werner T1 - Sliding simulations with variable amounts of copper and graphite mixed with magnetite N2 - Copper is one of the most important components in brake pads and its amount can reach up to 14%. In spite of a number of positive features copper usage in brake pad formulations has recently become the subject of considerable discussions, primarily due to concerns about potential risks related to environmental impacts of copper particles. So, for developing new pad formulations with possible replacements of copper content, it is very important to understand the functionality of copper additions to brake friction materials. In the paper theoretical investigation of the role of copper as a pad ingredient was carried out on the basis of modelling by the method of movable cellular automata (MCA). Our previous studies show that copper as a constituent of the tribofilm formed during braking provides smooth sliding by forming a granular layer of mechanically mixed materials from the friction layers. In the present study the concentration of copper particles in a Fe3O4-matrix was varied systematically in the range 5.5-28 vol. % and compared to mixtures with the same amount of graphite nanoparticles. The sliding simulations were performed while assuming material properties at 500°C in order to assess the beneficial role of copper during severe braking conditions corresponding to fading cycles during dynamometer testing. T2 - EuroBrake 2016 CY - Milano, Italy DA - 13.06.2016 KW - Movable cellular automata KW - Copper KW - Sliding simulation KW - Third body KW - Tribofilm PY - 2016 UR - www.eurobrake.net VL - EB2016-SVM-054 SP - 1 EP - 7 PB - FISITA AN - OPUS4-37938 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Siddapureddy, S. A1 - Wehrstedt, Klaus-Dieter A1 - Prabhu, S. V. T1 - Heat transfer to bodies engulfed in di-tert-butyl peroxide pool fires - Numerical simulations N2 - The thermal response of bodies engulfed in di-tert-butyl peroxide (DTBP) pool fires is studied numerically. High heat release rates, high velocities and high emissive powers portray the combustion of DTBP. This makes exceptionally hazard for bodies engulfed in DTBP fire accidents. The concept of adiabatic surface temperature (AST) is applied for DTBP pool fires to circumvent the difficulty of defining the fire exposure boundary condition at the solid surface. Adiabatic surface temperatures (AST) are computed for pool diameters 1.13 m and 3.4 m using the fire dynamics simulator. The thermal response of cask in a 1.13 m DTBP pool fire is studied to verify the concept of AST. It is found that a cask encounters twofold the heat fluxes in DTBP fires than in diesel pool fires. More than 30% of the net heat flux to the cask is a direct result of the convective heat exchange between the fire and the cask. This implies that the regular safety guidelines formulated for hydrocarbon pool fires are not adequate for the safety of the bodies engulfed in DTBP pool fires. KW - Di-tert-butyl peroxide (DTBP) pool fire KW - CFD simulation KW - Adiabatic surface temperature (AST) KW - Cask in fire PY - 2016 DO - https://doi.org/10.1016/j.jlp.2016.09.008 SN - 0950-4230 SN - 1873-3352 VL - 44 SP - 204 EP - 211 PB - Elsevier Ltd. AN - OPUS4-37883 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Marotzke, Christian A1 - Feldmann, Titus T1 - The influence of local defects and nonlinear matrix behaviour on the failure process of fiber reinforced composites N2 - The premise for the development of improved failure criteria for fiber reinforced composites is the understanding of the failure processes on microscale. On microscale the local behaviour of the matrix polymer is crucial. It significantly differs from that found in macroscopic measurements. The present study is focused on the plastic material behaviour of a standard epoxy resin. Local plastic strains are measured in tensile test by using digital image correlation. A multilinear plastic law is implemented by the experimental data. The stress field arising in an idealised representative volume element of a unidirectional ply is analysed by finite element calculations. The change of the stress and strain field due to plastic deformation according to the multilinear plastic law is shown. The change leads to a shift of the critical locations where failure is likely to initiate. In addition, the failure type changes from stress based to strain based failure. The dominant role of the shear strains is shown. T2 - ECCM17 CY - Munich, Germany DA - 27.06.2016 KW - failure mechanisms KW - plasticity KW - micromechanics KW - interfacial stresses KW - local deformation PY - 2016 SN - ISBN 978-3-00-053387-7 SP - 1 EP - 8 CY - München AN - OPUS4-37863 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Marotzke, Christian A1 - Feldmann, Titus T1 - Failure of fiber reinforced composites under multiaxial stresses on microscale N2 - The failure of composites is initiated by imperfections on microscale. The interface between fiber and matrix is a key parameter concerning failure initiation. In order to get an improved understanding of local failure processes a fracture mechanical analysis of interfacial failure in a composite ply under transverse stresses is performed. The mixed mode energy release rate is calculated. In addition the failure of interfaces under cyclic loading is studied on a single fiber model. The quasistatic debonding process is compared with the interfacial failure under fatigue loading. It is shown that the tan delta can be used as an indicator for the damage propagation. T2 - ICMFF11 CY - Sevilla, Spain DA - 01.06.2016 KW - failure mechanics KW - failure mechanisms KW - multiaxial loading KW - micromechanics PY - 2016 SP - 1 EP - 8 AN - OPUS4-37864 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kiyak, Yusuf A1 - Madia, Mauro A1 - Zerbst, Uwe A1 - Schork, B. T1 - Ermittlung der Wöhlerkurve von Schweißverbindungen mittels bruchmechanischer Methoden N2 - In diesem Aufsatz wird eine analytische Prozedur zur bruchmechanischen Beschreibung des Schwingverhaltens von Schweißverbindungen beschrieben, die im Rahmen des DFG-AiF-Clusters IBESS entwickelt wurde. Es wurden drei Verbindungen untersucht (Stumpfstöße, Kreuzstöße und Längssteifen), die aus warmgewalzten Stahlplatten produziert wurden. Die analytische Modellierung basierte auf drei wichtigen Aspekten: Quantitative Beschreibung der Rissausbreitung mechanisch-kurzer Risse; Statistische Effekte infolge der Variabilität der lokalen Schweißnahtgeometrie; Modellierung der Mehrfachrissinitiierung und des Mehrfachrisswachstums. Im Folgenden wird die Methodik vorgestellt und ihre Validierung an einem ausgewählten Beispiel diskutiert. T2 - 43. Tagung des DVM-Arbeitskreises Betriebsfestigkeit CY - Steyr, Austria DA - 12.10.2016 KW - Schwingfestigkeit KW - Wöhlerkurve KW - Bruchmechanik KW - Schweißverbindung PY - 2016 SN - 0944-522 SP - 197 EP - 208 AN - OPUS4-37866 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Genga, R. A1 - Cornish, L. A1 - Woydt, Mathias A1 - van Vuuren, A. J. A1 - Polese, C. T1 - Face-milling of grey cast iron (BS 1452) using WC-based and NbC-based cutting tools N2 - NbC was studied as the major carbide phase with Ni and Co binders, produced by both spark plasma sintering (SPS) and liquid phase sintering (LPS), and tested as cutting inserts during dry and MQL (Minimum quantity lubrication) face-milling of gey cast iron (GCI) (BS 1452, Grade 17). T2 - 10th Tool Conference 2016 - TOOL 2016 CY - Bratislava, Slovakia DA - 04.10.2016 KW - NbC KW - Spark plasma sintering KW - Ni KW - Mechanical properties KW - Flank wear KW - Chemical stability PY - 2016 SN - ISBN 978-3-200-04786-0 SP - 336 EP - 342 AN - OPUS4-37869 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Uhlmann, E. A1 - Kropidlowski, K. A1 - Sammler, F. A1 - Richarz, S. A1 - Woydt, Mathias T1 - Niobium carbide as an alternative cutting tool material N2 - Niobium carbide (NbC) is an alternative cutting material. The Federal Institute for Materials Research and Testing (BAM) and the Institute for Machine Tools and Factory Management (IWF) of the TU Berlin assessed the cutting suitability of NbC with cobalt (Co)-binder compared to WC with Co-binder in the machining of a wide range of materials. T2 - 10th Tool Conference 2016 - TOOL 2016 CY - Bratislava, Slovakia DA - 04.10.2016 KW - Niobium carbide (NbC) KW - Tungsten carbide (WC) KW - Cutting material KW - Tool wear KW - Turning trials KW - Wear mechanisms PY - 2016 SN - ISBN 978-3-200-04786-0 SP - 365 EP - 373 AN - OPUS4-37870 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kucharczyk, K. A1 - Banaszak, S. A1 - Gawrylczyk, K. A1 - Leistner, A. A1 - Siebler, Daniel A1 - Heidmann, G. T1 - Characterization of transparent fluorescent silicones for optical monitoring of high-voltage cable accessories N2 - The mechanical and electrical properties of new transparent silicone materials modified with two fluorescent dyes were investigated by measuring stress-strain behaviour, electrical breakdown strength, capacity and dissipation factor, before and after thermal ageing, as well as electrical and optical partial discharges. Mechanical properties of the new materials are comparable to the reference and the addition of dyes stabilises them against thermal ageing. All materials are equivalent in terms of breakdown strength and capacity. The added value of transparency and fluorescence make them suitable materials for novel diagnostic applications in HV cable accessories and insulators. T2 - Jicable 2015 - 9th International conference on insulated power cables CY - Paris, Versailles, France DA - 21.06.2015 KW - Silicones KW - Fluorescent dyes KW - Partial discharge KW - Electrical treeing KW - Breakdown strength KW - Tensile strength KW - Elongation at break KW - Thermal ageing PY - 2015 SP - 1 EP - 6 AN - OPUS4-33811 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nehrig, Marko A1 - Wille, Frank A1 - Feldkamp, Martin A1 - Rolle, Annette T1 - Aspects of gas generation caused by residual water inside ILW packages N2 - Packages for intermediate level waste (ILW) often contain residual water besides the actual waste. The water either exists as obvious free water or it may be bound physically or chemically, e.g. as pore water. Water driven gas generation could occur by vaporisation and by radiolysis. Steam as the result of vaporisation causes an increasing pressure inside a package and can affect corrosion. Vaporisation and condensation processes itself change the thermal behaviour of the content especially during strongly unsteady thermal situations like accident fire situations. Radiolysis changes the chemical composition of the content which could cause an unexpected interaction, e.g. hydrogen embrittlement. Besides the pressure build-up the radiolysis of water generates hydrogen and oxygen, which can be highly flammable respectively explosive. The gas generation caused by vaporisation and radiolysis must be taken into account during the design and the safety assessment of a package. Pressure build-up, a changed thermal behaviour and content chemistry, and especially the risk of accumulation of combustible gases exceeding the limiting concentration for inflammability has to be considered in the safety assessment. Approaches to ensure the transportability of stored packages due to radiolysis will be discussed. T2 - RAMTRANS 2015 - 10th International conference on radioactive materials transport and storage CY - Oxford, UK DA - 19.05.2015 KW - Typ-B KW - ILW package KW - Gas generation KW - Radiolysis KW - Wet content PY - 2015 SP - 1 EP - 7 AN - OPUS4-33429 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Protz, Christian A1 - Zencker, Uwe A1 - Liebich, R. T1 - Explicit finite element analyses of drop tests with thin-walles steel sheet containers for the Konrad repository N2 - Alternatively to experimental drop tests, the mechanical safety analyses of containers for final disposal of radioactive waste with negligible heat generation in the German Konrad repository may be carried out by numerical simulations within the safety assessment procedure. In the past, safety assessments for thin-walled steel sheet containers have been done exclusively by prototype tests and unfavorable drop scenarios were determined by engineering judgment. So far, reliable numerical simulations do not exist. Therefore, a research project was started to develop numerical simulation approaches for drop test analyses and to determine existing safety margins. Comparisons of experimental and numerical results confirm that the Finite Element (FE) model represents the general mechanical behavior of the steel sheet container sufficiently. Simulations have been used to determine an unfavorable drop scenario resulting in large deformation and damage. This paper presents the investigations carried out as well as the further development of the FE model in terms of damage mechanics. T2 - ASME 2015 Pressure vessels & piping conference - PVP2015 CY - Boston, Massachusetts, USA DA - 19.07.2015 KW - Explicit dynamic FEM KW - Impact KW - Drop test KW - Steel sheet container KW - Ductile damage KW - Damage mechanics PY - 2015 SN - 978-0-7918-5702-1 SP - PVP2015-45522, 1-10 AN - OPUS4-33805 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Habel, Wolfgang ED - De Stefano, A. T1 - The role of standardization in establishing new monitoring technologies - example fibre-optic sensors N2 - Sensors for assessment of the structure’s behaviour must work durably and reliably. Even if the performance of produced and delivered sensor is well specified, the sensor's strain characteristics and the performance of an applied sensor can significantly differ from the virgin sensor’s performance. The quality and appropriateness of installation decides over the long-term operability and getting reliable measurement results. The paper shows how important a clear terminology is, which problems might occur when sensor are not well characterized according to Standards or guidelines. Short outlook to experimental methods providing clear knowledge and appropriate Validation of the sensor’s performance for a defined measurement task is given. Finally, the state of-the-art in fibre-optic sensor Standardization is given. T2 - SHMII-7 - 7th International conference on structural health monitoring of intelligent infrastructure CY - Torino, Italy DA - 01.07.2015 KW - SHM KW - Standardization KW - Reliability KW - Fibre-optic sensor KW - Embedded sensor KW - Surface-applied sensor KW - Application KW - Validation KW - Calibration PY - 2015 SP - 1 EP - 10 AN - OPUS4-33779 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Blazek, M. A1 - Deilmann, M. A1 - Gasch, A. A1 - Gerlach, M. A1 - Grümbel, F. A1 - Kaiser, U. A1 - Kloska, M. A1 - Löbbecke, S. A1 - Maiwald, Michael A1 - Pötter, T. A1 - Rebner, K. A1 - Roos, E. A1 - Stieler, S. A1 - Stolz, D. A1 - Theuer, M. A1 - Berthold, J. A1 - Engelhard, H. T1 - Technologie-Roadmap "Prozesssensoren 4.0" N2 - Mit den Technologie-Roadmaps „Prozesssensoren 2005–2015“ [1] (2006) und „Prozesssensoren 2015+“ [2] und [3] (2009) wurden Grundlagen für alle Unternehmen der Prozessindustrie geschaffen, um zielgerichtet auf Kundenbedürfnisse der Prozessindustrie zugeschnittene Produktentwicklungen, technologische Weiterentwicklungen und Forschungsprojekte zum Erfolg zu bringen. Die Roadmap „Prozesssensoren 2015+“ fand große Akzeptanz aufgrund der soliden Betrachtung der Prozesse und der daraus abgeleiteten Thesen. Diese Aussagen haben in vollem Umfang weiterhin Gültigkeit. Im Rückblick auf die damals formulierten Entwicklungsziele wurden viele dieser Ziele im prognostizierten Zeithorizont auf den Weg gebracht und teilweise bereits umgesetzt. In dieser Technologie-Roadmap werden einige Beispiele dazu aufgezeigt. KW - Roadmap KW - Industrie 4.0 KW - Prozess-Sensoren KW - Prozessanalytik KW - Sensoren PY - 2015 UR - http://www.namur.net/fileadmin/media_www/Roadmap_Dateien/Roadmap_Prozesssensoren_4.0.pdf SP - 1 EP - 36 AN - OPUS4-34947 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas T1 - Influence of the weld thermal cycle on residual stress evolution and cold cracking ressistance in welded high-strength steel constructions N2 - The application of high-strength fine-grained structural steels with yield stress ≥ 690 MPa permits significant weight reductions and cost savings. Since welding is the major joining technology, e.g. in mobile crane industry, the sustainable and economical application of these grades depends on the load-bearing capacity and safety of the welds. An economical processing of high-strength steels is determined above all by the avoidance of cold cracking, apart from achieving demand-oriented mechanical properlies in the weid area. High tensile residual stresses are disadvantageaus regarding the cold cracking resistance and strength of welded components. Furthermore, high restraints commonly appearing in component welds increase residual stresses. Hence, in this research the influences of heat control on residual stresses and the overall structural Ioad of welded structures were quantified. The relationship between the weid thermal cycle and the resulting residual stress under additional shrinkage restraint was analysed by a successive augmentation of the restraint intensity. This was achieved by systematic low Ioad and component weid tests. lt was observed that the heat control significantly affects the local residual stresses and the overall structural Ioad of welded structures. A high interpass temperature increases the global and local welding stresses in particular. Moreover, the transferability of experimental welding results obtained from small specimens according to applicable codes to real component geometries was investigated. With the help of these findings it is possible to improve existing heat control concepts for high-strength steel welding. T2 - 2nd METEC & ESTAD 2015 - European steel technology and application days conference CY - Düsseldorf, Germany DA - 15.06.2015 KW - Residual stresses KW - Welding KW - HEat control KW - GMAW KW - Restraint KW - High-strength steels KW - Cold cracking KW - MAG welding KW - Process parameters PY - 2015 SP - P668, 1 EP - 7 AN - OPUS4-34988 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bachmann, Marcel T1 - Wie Magnete Schweissnähte verbessern / How magnets can improve welds N2 - Aluminiumlegierungen gehören neben Stahl zu den im Maschinenbau am häufigsten verwendeten Werkstoffen. Für innovative Baustrukturen in vielfältiger Formensprache aber auch in den klassischen Bereichen wie im Schiffsbau oder bei der Fertigung von Reaktorbehältern vom Kraftwerksbau bis zur Lebensmittelindustrie verwenden Ingenieure Aluminiumwerkstoffe. KW - Schweißen KW - FEM KW - Elektromagnetische Schmelzbadbeeinflussung KW - Hartmann-Effekt KW - Aluminium PY - 2014 N1 - Sprachen: Deutsch/Englisch - Languages: German/English SP - 106 EP - 109 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-34995 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rosenthal, Martina A1 - Müller, Christina A1 - Kanzler, Daniel T1 - Webseiten zum 6th European-American workshop on reliability of NDE N2 - Website for 6th European-American Workshop on Reliability of NDE in Munich, 26-29 July 2015 T2 - 6th European-American Workshop on Reliability of NDE CY - Minneapolis, MN, USA DA - 26.07.2015 PY - 2015 UR - http://www.nde-reliability.com UR - http://www.pod-tutorial.nde-reliability.com SP - 1 EP - 12 AN - OPUS4-34919 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Qiao, Linan A1 - Völzke, Holger T1 - Dynamic finite element analysis of cask handling accidents at storage sites N2 - The safety assessment of casks for radioactive material at interim storage facilities or in final repositories includes the investigation of possible handling accidents if clearly defined test conditions are not available from the regulations. Specific handling accidents usually are the drop of a cask onto the transport vehicle or the floor as well as the collision with the wall of the storage building or another cask. For such load cases an experimental demonstration of cask safety would be difficult. Therefore, numerical analyses of the entire load scenario are preferred. The lessons learnt from dynamic finite element analyses of accident scenarios with thick-walled cubical containers or cylindrical casks are presented. The dependency of calculation results on initial and boundary conditions, material models, and contact conditions is discussed. Parameter sets used should be verified by numerical simulation of experimentally investigated similar test scenarios. On the other hand, decisions have to be made whether a parameter or property is modeled in a realistic or conservative manner. For example, a very small variation of the initial impact angle of a container can cause significantly different stresses and strains. In sophisticated cases an investigation of simpler limit load scenarios could be advantageous instead of analyzing a very complicated load scenario. T2 - ASME 2015 Pressure vessels & piping conference - PVP2015 CY - Boston, Massachusetts, USA DA - 19.07.2015 KW - Finite element method KW - Simulation KW - Cask handling accident KW - Interim storage PY - 2015 SN - 978-0-7918-5702-1 SP - Paper 45606, 1 EP - 10 AN - OPUS4-34937 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Qiao, Linan A1 - Völzke, Holger T1 - Strategies for numerical modelling of metal gaskets in transport and storage casks N2 - Metal gaskets in the lid system of transport and storage casks for radioactive material have to guarantee leak-tightness and safe enclosure of the radioactive inventory under normal and accident conditions during transport, in case of accidents and for the longterm interim storage. For safety assessments by nurnerical simulation of the thermomechanical behaviour of a lid system with metal gaskets, the finite element method offers three options to use: i) special gasket elements, ii) complex three-dimensional modeHing with solid elements, and iii) a simplified axisymmetric approach. Gasket elements can be adjusted by many parameters, but they give only a global representation of the experimentally observed gasket behaviour. For calculations of the entire cask including the lid system with gaskets, nonetheless this approach is recommended. To investigate the hardly measurable impact behaviour in detail or to extrapolate the long-term behaviour, a local modeHing of all parts of a gasket and their interactions with effects like elastic-plastic deformation, creep, relaxation, and friction is necessary. The three-dimensional model can describe the change of contact area between outer jacket of the gasket and flange dependent on the load conditions, what overcomes an essential limitation of special gasket elements. To simplify the problern of investigating the underlying physical effects, an axisymmetric lid system can be modelled with axisymmetric finite elements. Usually an approximation is only necessary for the helical spring of a metal gasket. This paper explains basic ideas for an adequate finite element simulation of cask lid systems with metal gaskets and their thermo-mechanical behaviour under specific load scenarios. T2 - RAMTRANSPORT 2015 - International conference on the radioactive materials transport and storage CY - Oxford, UK DA - 19.05.2015 KW - Metal gasket KW - Finite element method KW - Simulation PY - 2015 SP - Paper RAM15-27, 1-9 AN - OPUS4-34938 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilke, Olaf A1 - Seeger, Stefan T1 - New VOC compounds in the indoor environment from thermoplastic filaments for 3D printing N2 - A screening test for potential emissions of volatile organic compounds (VOC) was run on different thermoplastic filaments used for 3D printing. The method of direct thermal desorption was used to simulate the high temperatures during the 3D printing process and to identify the main compounds emitted from the filaments. A )arge number of unexpected compounds were detected that might affect the user's health and have an impact on indoor air chemistry. T2 - HB 2015 - 1st North American regional conference Healthy Buildings 2015 America CY - Boulder, Colorado, USA DA - 17.09.2015 KW - VOC KW - Emission KW - 3D printer PY - 2015 SP - 281 EP - 282 AN - OPUS4-34941 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz ED - Papadrakakis, M. ED - Papadopoulos, V. ED - Plevris, V. T1 - Fast computation of train-induced vibrations in homogeneous and layered soils N2 - The computation of the wave propagation in homogeneous and layered soils can be performed by a numerical integration in wavenumber domain. The numerical difficulties of an infinite integral and an integrand with poles can be solved. But if this computation must be repeated for many distances, many frequencies, many loads, or many soil models, it becomes a time consuming task which is not acceptable for a user-friendly prediction tool for railway induced ground vibration. Therefore, an approximate method for the computation of the wave field has been developed. The computation consists of several steps. At first, an approximate dispersion profile is calculated according to rules which have been derived from exact solutions. Secondly, the dispersion is used to achieve the amplitude for a certain frequency and a certain distance by calculating the approximate solution of a corresponding homogeneous half-space. Thirdly, three layer corrections are added which include lowfrequency near-field effects, high-frequency far-field effects, and a resonance amplification around the layer frequency. This procedure yields the wave field due to a point load. For a train load, many of these point-load responses have to be summed up, and a frequencydependant reduction factor has to be multiplied to incorporate the effect of the load distribution along and across the track. - The prediction method is applied to real sites, and the appropriate soil models are identified by approximating the measured transfer functions (frequency-dependant amplitudes) which is presented as an alternative to the approximation of the dispersion (frequency-dependant wave velocities). These examples demonstrate the general behavior of layered soils: the low amplitudes of the stiff half-space at low frequencies, the high amplitudes of the softer layer at high frequencies, the strong increase of amplitudes and a possible resonance amplification at mid frequencies. The material damping of the layer yields a strong attenuation of the amplitudes with the distance for high frequencies. The response depends strongly on the resonance or layer frequency which is shown for different layer depths and velocities always in good agreement with measurements. The layer frequency can be of immense influence if train-speed effects are analysed in a layered soil. The good agreement with many measurements in this contribution as well as in the references validates the prediction of ground vibration based on the theory of a layered half-space. T2 - COMPDYN 2015 - 5th International conference on computational methods in structural dynamics and earthquake engineering CY - Crete Island, Greece DA - 25.05.2015 PY - 2015 DO - https://doi.org/10.7712/120115.3381.959 SP - 66 EP - 82 AN - OPUS4-33683 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bradley, I. A1 - Birk, A.M. A1 - Otremba, Frank A1 - Gonzalez III, F. A1 - Prabhakaran, A. A1 - Bisby, L. T1 - Development and characterisation of an engulfing hydrocarbon pool fire test for hazardous materials pressure vessels N2 - The US Department of Transportation, Federal Railroad Administration (FRA) current regulations for rail tank cars in the United States stipulate that, for certain hazardous materials, tank cars shall have a thermal protection system capable of preventing rupture of the tank for 100 minutes when exposed to an engulfing fire with a blackbody equivalent flame temperature of 871 °C (+/- 56°C), and that tanks shall have a pressure relief device set at an appropriate level (depending on the type of tank car and contents). Pressure relief devices are a source of non-accident releases, and hence may cause serious incidents when tanks are transporting hazardous materials. Industry in North America would therefore benefit from removal of pressure relief devices on tanks transporting certain hazardous materials. Such an approach is known as full Containment, and is standard practice in Europe. In 2014 the FRA commissioned an experimental study to investigate the ability of a specific design of rail tank to resist rupture without incorporating a pressure release valve. As a precursor to tests on tanks there was a need to develop and characterise a simulated pool fire capable of reliably exposing large-scale tanks to repeatable, uniform conditions. This paper describes such a fire test setup, developed using a burner array system fuelled by liquid propane and designed to produce luminous, low velocity flames representative of those found in large hydrocarbon pool fires. The experimental set-up is described, along with the Instrumentation (directional flame thermometers, infra-red camera, and thermally massive calorimeter) and methodology used to characterise the fire. Comparisons are made against previous fire tests on vessels to assess the suitability of the experimental set-up for future vessel testing. T2 - CONFAB 2015 - 1st International conference on structural safety under fire & blast CY - Glasgow, UK DA - 02.09.2015 PY - 2015 SP - 485 EP - 494 AN - OPUS4-34545 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Siebler, Daniel A1 - Hohberg, Michaela A1 - Rohwetter, Philipp T1 - A new generation of all-elastomeric fluorescent POF for sensor applications N2 - We present fundamentals for the selection of fluorescent dyes and show the challenges of the implementation of fluorescent dyes in silicone rubber materials for the production of fluorescent all-silicone rubber POF. T2 - POF 2015 - 24th International conference on plastic optical fibers CY - Nürnberg, Germany DA - 2015-09-22 KW - Elastomeric polymer optical fiber KW - Covalently bonded fluorescent dye KW - Silicone rubber KW - Sensor application KW - Reabsorption KW - All-elastomeric POF KW - High temperature stable POF KW - Fluorescent POF PY - 2015 SP - 290 EP - 294 AN - OPUS4-34478 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hohberg, Michaela A1 - Siebler, Daniel A1 - Rohwetter, Philipp T1 - Production process and characterization of sensitized all elastomeric POF N2 - We present the production process and characterization of a fluorescent functionalized elastomeric polymer optical fiber (E-POF) consisting of a covalently linked interface between fiber core and fiber cladding. This all silicone rubber E-POF shows increased temperature stability and can be used for sensing applications. Due to the sophisticated production process surface roughness of the interface of fiber core - fiber cladding are even lower than of the thermoplastic tubing template. Total fiber lengths can be extended by a "chemical splicing" technique, allowing individual tailoring of fibers while maintaining sufficient elasticity under applied mechanical stress. T2 - POF 2015 - 24th International conference on plastic optical fibers CY - Nuremberg, Germany DA - 22.09.2015 KW - Polymer optical fiber KW - Elastomer KW - Silicone rubber KW - Fluorescence KW - Thermally stable POF KW - Sensitized POF KW - Chemical splicing PY - 2015 SP - 91 EP - 94 AN - OPUS4-34532 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wiggenhauser, Herbert A1 - Samokrutov, A.A. A1 - Mayer, K. A1 - Krause, Martin A1 - Alekhin, S. G. A1 - Elkin, V. T1 - LAUS - Large aperture ultrasonic system - for testing thick concrete structures N2 - A Large Aperture UltraSonic (LAUS) system has been designed and built for testing thick concrete structures. The scalable system consists of twelve ultrasonic units, each hosting 32 individual shear wave transducers with mechanical dry point contact (DPC) to the concrete surface. The twelve units are attached to the concrete surface using a vacuum case which holds them in place during operation. Each LAUS unit can be placed individually depending on the surface condition and optimal ultrasonic condition, e.g. rebar position. Air pressure is supplied to each unit through an air hose. The following extended abstract is a short version of an article to be published in the special edition of ASCE JIS that will describe the outline of the system, the principle of functioning, the data processing and adapted reconstruction calculation based on SAFT as well as the system performance during first applications. T2 - NDT-CE 2015 - International symposium non-destructive testing in civil engineering CY - Berlin, Germany DA - 15.09.2015 KW - Ultrasonic imaging KW - Linear array KW - Reconstruction calculation (SAFT) PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-345383 UR - http://www.ndt.net/?id=18313 SN - 1435-4934 VL - 20 IS - 11 SP - 1 EP - 4 PB - NDT.net CY - Kirchwald AN - OPUS4-34538 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Behrends, Malte A1 - Bürger, Christoph A1 - Klieboldt, Ulrich A1 - Näther, Dietmar A1 - Nolde, Moana A1 - Eckhardt, Dietrich T1 - The effects of explosive substances onto vending machines in public areas N2 - The German Federal Police approached the Federal Institute for Materials Research and Testing (Bundesanstalt für Materialforschung und -prüfung, BAM) with the question whether different machines, which are available in public areas, provide a certain amount of protection against the effects of explosions/detonation. The devices of interest were ticket vending machines, found on train Station platforms, as well as x-ray Scanners used for examining luggage or mail at airports and Offices, respectively. A series of experiments was carried out using a number of different explosives, e.g. plastic explosives, improvised explosive devices (IEDs) and pyrotechnic articles. Documentation was done applying video and highspeed video recordings, pressure measurements etc. The results of these experiments are currently under discussion among the different authorities. The final report shall then be used as a basis for further discussions about possible changes in guidelines and legislation in order to further increase the level of public safety. T2 - 16th International symposium on interaction of the effects of munitions with structures, ISIEMS 16 CY - Destin, FL, USA DA - 09.11.2015 KW - IED KW - Pyrotechnic articles KW - Experimental KW - Public safety PY - 2015 SP - 1 EP - 4 AN - OPUS4-35083 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scheidemann, Robert A1 - Qiao, Linan A1 - Müller, Karsten A1 - Droste, Bernhard T1 - Determination of material parameters of damping concrete under dynamic loading N2 - The safety and integrity of casks for radioactive waste in accidental scenarios is analysed by BAM Federal institute tor Materials Research and Testing. An accidental scenario in German interim storage facilities is the drop from a crane during the handling operation. To reduce the mechanical loads to the cask a shock absorbing footing with high energy absorption capability is used in these areas. In order to analyse and evaluate such impact scenarios of casks, numerical simulations are performed. For a comprehensive simulation of an accidental scenario the behaviour of the damping concrete footing has to be taken into account as well and therefor a material model is needed. Material parameters under different loading conditions are the basis for a numerical model. For that reason a government funded research project (Kasparek, 2012) was conducted to characterise damping concrete under quasi-static as well as highly dynamic impact loading conditions. The performed tests include compression tests with and without lateral constraint small-scale and midscale penetration tests with different indenters, and finally a full-scale drop test onto a damping concrete footing. T2 - RAMTRANS 2015 - 10th International conference on radioactive materials transport and storage CY - Oxford, UK DA - 19.05.2015 KW - Drop test KW - Damping concrete KW - Material characterisation PY - 2015 SP - 1 EP - 9 AN - OPUS4-33492 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wüstenberg, Hermann A1 - Schenk, G. A1 - Haufe, U. T1 - Dynamische Fokussierung in Schrägeinschallung bei der Ultraschallprüfung T2 - 4. Internationale Konferenz über Zerstörungsfreie Prüfung in der Kerntechnik CY - Lindau, Germany DA - 1981-05-25 PY - 1981 N1 - Serientitel: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. – Series title: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. IS - 8 SP - 1 EP - 15 PB - DGZfP CY - Berlin AN - OPUS4-33345 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wüstenberg, Hermann A1 - Schenk, E. A1 - Möhrle, W. T1 - Vergleich der Leistungen von fokussierenden Prüfköpfen mit Linsen oder elektronisch gesteuerten Ringstrahlern T2 - 2. Europäische Tagung für Zerstörungsfreie Prüfung CY - Wien DA - 1981-09-14 PY - 1981 SP - 1 EP - 13 CY - Wien AN - OPUS4-33346 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neider, Rudolf T1 - Radiation Protection during the transportation of radioactive materials T2 - PATRAM ´80 - 6th International symposium on the packaging and transportation of radioactive materials CY - Berlin, Germany DA - 1980-11-10 PY - 1981 SP - 1423 EP - 1437 PB - Bundesanstalt für Materialprüfung CY - Springfield, Va. AN - OPUS4-33349 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Witt, Klaus A1 - Döring, Günter T1 - Schwellenwertellipsoid für CIE-Farbbereich Grün an Lackmustern T2 - 4th congress of the International Colour Association CY - Berlin, Germany DA - 1981-09-21 PY - 1981 SP - 1 EP - 5 CY - Berlin AN - OPUS4-33294 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmitt, B. A1 - Segebade, C. A1 - Fusban, H.-U. T1 - Multielement Analysis of Soil of a Sewage-Farm by Photon and Neutron Activation Analysis using Waste Incineration Ash as Reference Material T2 - 4th International Conference on Nuclear methods in environmental and energy research CY - Columbia, MO, USA DA - 1980-04-14 PY - 1981 SP - 159 EP - 168 CY - Oak Ridge AN - OPUS4-33357 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Barthelmeß, Helmut T1 - Datenbanken beantworten Fragen der Fachleute PY - 1981 IS - 5 SP - 1 PB - Dt. Verl. für Schweißtechnik CY - Düsseldorf AN - OPUS4-33363 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz, Eduard A1 - Wegner, W. T1 - Automatisierung der Wanddickenmessung mit US an Rohren bei der Prüfung von der Innenseite T2 - 2. Europäische Tagung für Zerstörungsfreie Prüfung CY - Wien DA - 1981-09-14 PY - 1981 SP - 1 EP - 7 CY - Wien AN - OPUS4-33324 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stade, Jürgen A1 - Heidt, Heinrich T1 - Detailerkennbarkeit auf mit einem 35 MeV-Elektronen-Linearbeschleuniger erzeugten Neutronenradiographen T2 - 2. Europäische Tagung für Zerstörungsfreie Prüfung CY - Wien DA - 1981-09-14 PY - 1981 SP - 193 EP - 194 CY - Wien AN - OPUS4-33325 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stadthaus, Meinhard T1 - Möglichkeiten der Festlegung von Nachweisgrenzen beim Magnetpulververfahren T2 - 2. Europäische Tagung für Zerstörungsfreie Prüfung CY - Wien DA - 1981-09-14 PY - 1981 SP - 301 EP - 303 CY - Wien AN - OPUS4-33326 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wittig, Günther A1 - Beller, M. A1 - Leider, A. A1 - Stumm, W. A1 - Weber, H. P. T1 - Application of Reference Standards for Control of Eddy-Current Test Equipment T2 - Symposium on Eddy-Current Characterization of Materials and Structures CY - Gaithersburg, MD, USA DA - 1979-09-05 PY - 1981 N1 - Serientitel: ASTM special technical publication – Series title: ASTM special technical publication IS - 722 SP - 79 EP - 85 PB - ASTM CY - Philadelphia, PA, USA AN - OPUS4-33329 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wittig, Günther A1 - Thomas, Hans-Martin T1 - Design of a Pulsed Eddy-Current Test Equipment with Digital Signal Analysis T2 - Symposium on Eddy-Current Characterization of Materials and Structures CY - Gaithersburg, MD, USA DA - 1979-09-05 PY - 1981 N1 - Serientitel: ASTM special technical publication – Series title: ASTM special technical publication IS - 722 SP - 387 EP - 397 PB - ASTM CY - Philadelphia, PA, USA AN - OPUS4-33330 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wittig, Günther A1 - Thomas, Hans-Martin T1 - Voruntersuchungen an Dampferzeugerrohr-Testkörpern mit dem Impuls-Wirbelstromverfahren T2 - 4. Internationale Konferenz über Zerstörungsfreie Prüfung in der Kerntechnik CY - Lindau, Germany DA - 1981-05-25 PY - 1981 N1 - Serientitel: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. – Series title: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. IS - 8 SP - 571 EP - 579 PB - DGZfP CY - Berlin AN - OPUS4-33331 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wittig, Günther A1 - Thomas, Hans-Martin T1 - Untersuchungen an Komponenten aus Aluminiumlegierungen mit dem Impuls-Wirbelstromverfahren T2 - 2. Europäische Tagung für Zerstörungsfreie Prüfung CY - Wien DA - 1981-09-14 PY - 1981 SP - ? (8 S.) CY - Wien AN - OPUS4-33332 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wittig, Günther A1 - Thomas, Hans-Martin T1 - Rißnachweis und Rißtiefenbestimmung an Stutzenkanten des HDR mittels Impuls-Wirbelstrom- und Ultraschallverfahren T2 - Sitzung des Projektes HDR-Sicherheitsprogramm des Kernforschungszentrums Karlsruhe CY - Karlsruhe, Germany DA - 1981-12-10 PY - 1981 N1 - Serientitel: PHDR-Arbeitsbericht – Series title: PHDR-Arbeitsbericht IS - 81,5.8 SP - 1 EP - 42 PB - Kernforschungszentrum Karlsruhe CY - Karlsruhe AN - OPUS4-33333 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilken, K. T1 - Hot cracking testing during welding with the "MVT-Test" and their relationship to service conditions T2 - International Colloquium on Hard-Facing Materials in Nuclear Power Plants CY - Avignon, France DA - 1980-09-25 PY - 1980 SP - 227 EP - 234 CY - Paris AN - OPUS4-33389 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Findeisen, Dietmar T1 - Maschinen-Antriebssysteme für Schwingfestigkeits-Prüfungen T2 - DVM Kolloquium "Werkstoffermüdung und Bauteilfestigkeit" CY - Berlin, Germany DA - 1981-09-25 PY - 1981 SP - 253 EP - 281 CY - Berlin AN - OPUS4-33393 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heidt, Heinrich A1 - Oelmayer, P. A1 - Filbert, D. T1 - Lagebestimmung von Innenfehlern durch Bildverarbeitung radiografischer Aufnahmen T2 - 4. Internationale Konferenz über Zerstörungsfreie Prüfung in der Kerntechnik CY - Lindau, Germany DA - 1981-05-25 PY - 1981 N1 - Serientitel: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. – Series title: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. IS - 8 SP - 165 EP - 172 PB - DGZfP CY - Berlin AN - OPUS4-33317 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Oelmayer, P. A1 - Filbert, D. A1 - Heidt, Heinrich T1 - Lagebestimmung von Innenfehlern durch Bildverarbeitung radiografischer Aufnahmen T2 - Kolloquium des DFG-Schwerpunktprogramms Digitale Signalverarbeitung CY - Göttingen, Germany DA - 1981-03-04 PY - 1981 SP - 1 EP - 6 CY - Göttingen AN - OPUS4-33319 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Römer, M. A1 - Matthies, K. A1 - Schmid, R. A1 - Mundry, Eberhard A1 - Neumann, Eberhard T1 - Schallfeldfokussierung mit Zonenplatten-Prüfköpfen - eine einfache Methode zur Fehlergrößenabschätzung T2 - 2. Europäische Tagung für Zerstörungsfreie Prüfung CY - Wien DA - 1981-09-14 PY - 1981 SP - 1 EP - 10 CY - Wien AN - OPUS4-33320 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rose, Peter A1 - Heidt, Heinrich T1 - Verfahren der digitalen Bildverarbeitung zur Aufbereitung von Röntgenfilmen aus der Materialprüfung T2 - 4. Internationale Konferenz über Zerstörungsfreie Prüfung in der Kerntechnik CY - Lindau, Germany DA - 1981-05-25 PY - 1981 N1 - Serientitel: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. – Series title: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. IS - 8 SP - 173 EP - 181 PB - DGZfP CY - Berlin AN - OPUS4-33321 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erhard, Anton A1 - Wüstenberg, Hermann T1 - Der Einsatz der akustischen Holographie an plattierten Bauteilen zur Fehlergrößenbestimmung T2 - 2. Europäische Tagung für Zerstörungsfreie Prüfung CY - Wien DA - 1981-09-14 PY - 1981 SP - 117 EP - 119 CY - Wien AN - OPUS4-33308 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hecht, A. A1 - Thiel, R. A1 - Funck, B. A1 - Neumann, Eberhard A1 - Mundry, Eberhard T1 - Konzeption, Aufbau und Arbeitsweise eines rechnergesteuerten Ultraschallmeßplatzes, dargestellt am Beispiel der Gefügeuntersuchung an austenitischen Rohren T2 - 2. Europäische Tagung für Zerstörungsfreie Prüfung CY - Wien DA - 1981-09-14 PY - 1981 SP - 280 EP - 281 CY - Wien AN - OPUS4-33310 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heidt, Heinrich T1 - Automatische Bestimmung der Tiefenlage von Fehlern mittels Radiometrie T2 - 2. Europäische Tagung für Zerstörungsfreie Prüfung CY - Wien DA - 1981-09-14 PY - 1981 SP - 79 EP - 80 CY - Wien AN - OPUS4-33312 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heidt, Heinrich A1 - Basler, G. T1 - Belichtungsrechner für technische Radiographie T2 - 2. Europäische Tagung für Zerstörungsfreie Prüfung CY - Wien DA - 1981-09-14 PY - 1981 SP - 163 EP - 164 CY - Wien AN - OPUS4-33313 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Florian, W. A1 - Jaenicke, B. T1 - Das geschweißte, einsatzgehärtete Zahnrad T2 - Informationstagung des Wissenschaftlichen Beirats der FVA CY - Wiesbaden, Germany DA - 1981-11-25 PY - 1981 VL - 2 SP - ? (60 S.) PB - Forschungsvereinigung Antriebstechnik CY - Frankfurt am Main AN - OPUS4-33366 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krause, Hans-Joachim T1 - Some comments on the torsion test and the importance of its results PY - 1981 SP - 1 EP - 20 PB - Inst. AN - OPUS4-33370 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Naumann, V. A1 - Florian, W. T1 - Untersuchungen zur wasserstoffbeeinflußten Kaltrißneigung höherfester niedriglegierter Feinkornbaustähle PY - 1980 SP - 54 EP - 62 PB - Technische Vereinigung der Grosskraftwerksbetreiber CY - Essen AN - OPUS4-33374 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schönherr, Wolfgang T1 - Ideas on economic and energy growth and on the goal of the economy in industrialized countries T2 - 3. International Conference on Energy Use Management CY - Berlin DA - 1981-10-26 PY - 1981 IS - 1 SP - 133 EP - 139 PB - Pergamon Pr. CY - Oxford AN - OPUS4-33442 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Terstiege, Heinz T1 - Colours of traffic signs PY - 1981 SP - 254 EP - 259 AN - OPUS4-33443 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erhard, Anton A1 - Wüstenberg, Hermann T1 - Fehlergrößenbestimmung oberflächennaher Fehler mit Hilfe der akustischen Holographie T2 - 4. Internationale Konferenz über Zerstörungsfreie Prüfung in der Kerntechnik CY - Lindau, Germany DA - 1981-05-25 PY - 1981 N1 - Serientitel: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. – Series title: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. IS - 8 SP - 101 EP - 108 PB - DGZfP CY - Berlin AN - OPUS4-33444 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mundry, Eberhard T1 - New Developments and Special Methods of NDT PY - 1979 VL - 1 IS - 4 SP - 25 EP - 32 AN - OPUS4-33463 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mundry, Eberhard A1 - Wittig, Günther A1 - Stadthaus, Meinhard T1 - status and tendency of electromagnetic inspection technique PY - 1980 VL - 2 IS - 4 SP - 46 EP - 49 AN - OPUS4-33464 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfeil, Norbert A1 - Andre, Hilmar ED - Volk, F. ED - Tulis, A. J. T1 - Die Deflagration von Schwarzpulver unter Eigenverdämmung T2 - 16. Internationale ICT-Jahrestagung 1985 combined with 10th international Pyrotechnics Seminar CY - Karlsruhe, Germany DA - 1985-07-02 PY - 1985 SP - 53-1 - 53-16 PB - Fraunhofer-Institut für Treib- und Explosivstoffe CY - Karlsruhe AN - OPUS4-34091 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Treumann, Hartwig A1 - Andre, Hilmar A1 - Pfeil, Norbert T1 - Behältnisse zur Aufbewahrung von explosionsgefährlichen Stoffen in kleinen Mengen PY - 1985 SP - 1 EP - 38 PB - Bayerisches Staatsministerium für Arbeit und Sozialordnung CY - München AN - OPUS4-34092 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Treumann, Hartwig ED - Volk, F. ED - Tulis, A. J. T1 - Systematische Untersuchung der explosiven Eigenschaften von Mischungen aus oxidierenden und verbrennlichen Substanzen T2 - 16. Internationale ICT-Jahrestagung 1985 combined with 10th international Pyrotechnics Seminar CY - Karlsruhe, Germany DA - 1985-07-02 PY - 1985 SP - 47-1 - 47-15 PB - Fraunhofer-Institut für Treib- und Explosivstoffe CY - Karlsruhe AN - OPUS4-34093 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzlöhner, Ulrich T1 - Sand properties governing foundation settlement T2 - 11th international conference on soil mechanics and foundation engineering CY - San Francisco, CA, USA DA - 1985-08-12 PY - 1985 SP - 507 EP - 510 PB - Balkema CY - Rotterdam AN - OPUS4-34024 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Burmester, Arno T1 - Dimensational stabilisation of wood T2 - 12th Annual Meeting of the International Research Group on Wood Preservation - Working Group III (Preservatives and Methods of Treatment) CY - Sarajevo, Bosnia and Herzegovina DA - 1981-05-11 PY - 1981 SP - Document No. IRG/WP/3171, 1 EP - 8 PB - International Research Group on Wood Preservation CY - Stockholm AN - OPUS4-34034 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kühne, Helmut T1 - Remedial treatment of wood attacked by insects T2 - 12th Annual Meeting of the International Research Group on Wood Preservation - Working Group III (Preservatives and Methods of Treatment) CY - Sarajevo, Bosnia and Herzegovina DA - 1981-05-11 PY - 1981 SP - Document No. IRG/WP/3175, 1 EP - 12 PB - International Research Group on Wood Preservation CY - Stockholm AN - OPUS4-34035 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Limberger, Ernst A1 - Brandes, Klaus A1 - Herter, Jürgen T1 - Etude expérimentale des poutres et dalles en béton armé soumises aux charges dynamiques appliquées par un système hydraulique T2 - Effets cycliques et transitoires dans les structures - Séminaire CY - Saint-Rémy-les-Chevreuse, France DA - 1979-10-23 PY - 1980 SP - 151 EP - 164 PB - Ed. du Bâtiment et des Travaux Publics CY - Paris AN - OPUS4-34041 LA - fra AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schickert, Gerald T1 - Methodes d'essais - testing methods PY - 1984 VL - 2 SP - 10 EP - 19 PB - Sabatier CY - Toulouse AN - OPUS4-34044 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schickert, Gerald A1 - Danßmann, Jürgen T1 - Behaviour of concrete stressed by high hydrostatic compression PY - 1984 VL - 2 SP - 69 EP - 84 PB - Sabatier CY - Toulouse AN - OPUS4-34045 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schickert, Gerald A1 - Winkler, Helmut T1 - Considerations on international comparative investigations on concrete subjected to multiaxial compressive stresses PY - 1984 VL - 2 SP - 85 EP - 96 PB - Sabatier CY - Toulouse AN - OPUS4-34046 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - August, Hans T1 - Untersuchungen zum Permeationsverhalten kombinierter Abdichtungssysteme T2 - Fachseminar des Instituts für Grundbau und Bodenmechanik CY - Braunschweig, Germany DA - 1985-02-06 PY - 1985 N1 - Serientitel: Mitteilung des Instituts für Grundbau und Bodenmechanik - Technische Universität Braunschweig – Series title: Mitteilung des Instituts für Grundbau und Bodenmechanik - Technische Universität Braunschweig IS - 17 SP - 205 EP - 219 PB - Institut für Grundbau und Bodenmechanik CY - Braunschweig AN - OPUS4-34054 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Hartmut A1 - Schnabel, Edmund T1 - Prüfung der mechanischen Eigenschaften von Geotextilien T2 - 23. Internationale Chemiefasertagung CY - Dornbirn, Austria DA - 1984-09-26 PY - 1984 SP - 162 EP - 195 PB - Österreichisches Chemiefaser-Institut CY - Wien AN - OPUS4-34080 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stajanca, Pavol A1 - Cetinkaya, O. A1 - Schukar, Marcus A1 - Mergo, P. A1 - Krebber, Katerina T1 - Climatic stability of polymer optical fibers for sensing applications N2 - Systematic investigation of annealing behavior of drawn PMMA fibers was performed. Dynamics of annealing process were measured under different environmental conditions by fiber longitudinal shrinkage monitoring. Process was found to follow stretched exponential decay function indicating heterogeneous nature of underlying molecular dynamics. Consequences of fiber annealing for climatic stability of polymer optical fiber-based sensors are discussed, emphasizing importance of fiber controlled post-fabrication annealing. Dependence of induced fiber shrinkage on annealing time, temperature and fiber drawing conditions is investigated and interpreted. In addition, strong influence of humidity on annealing process was observed, which was not recognized in previous studies. This further highlights role of fiber post-fabrication thermal treatment with respect to intended operating conditions. T2 - POF 2015 - 24th International conference on plastic optical fibers CY - Nuremberg, Germany DA - 22.09.2015 KW - Polymer optical fibers KW - Polymethyl methacrylate KW - Climatic stability KW - Fiber annealing PY - 2015 SP - 209 EP - 212 AN - OPUS4-34422 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Witt, Klaus T1 - Die DIN-Farbenkarte als anschauliche Ordnungshilfe in der Farbtechnik PY - 1985 VL - 33/34 SP - 9 EP - 12 PB - Verl. Farbe + Design CY - Gaildorf AN - OPUS4-34150 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Löschau, Gerhard T1 - Performance testing and certification of packagings for dangerous goods PY - 1985 SP - 1 EP - 16 PB - IAPRI - International Association of Packaging Research Institutes CY - Lansing, MI, USA AN - OPUS4-34153 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Löschau, Gerhard T1 - Possibilities to investigate the stability of column stacks PY - 1985 SP - 1 EP - 17 PB - IAPRI - International Association of Packaging Research Institutes CY - Lansing, MI, USA AN - OPUS4-34154 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz-Forberg, Bernd T1 - Tankcontainer - Verbund der nationalen und internationalen Gefahrgut-Vorschriften für See, Schiene und Strasse T2 - Gefahrgut-Tage Hamburg CY - Hamburg, Germany DA - 1985-02-28 PY - 1985 SP - 40 EP - 55 PB - Storck CY - Hamburg AN - OPUS4-34155 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gierloff, Michael A1 - Schimmelwitz, Peter T1 - Change of mechanical properties of PCC due to long time exposure conditions PY - 1987 N1 - Serientitel: American Concrete Institute special Publications – Series title: American Concrete Institute special Publications IS - 99 SP - 73 EP - 90 PB - ACI CY - Detroit, Mich. AN - OPUS4-34156 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Plank, Arno A1 - Struck, Werner T1 - The vertical large space 25 MN testing machine at BAM, Berlin (Federal Institute for Materials Testing) T2 - International Conference on Destructive Testing Equipment (DTE) CY - Dübendorf, Switzerland DA - 1985-04-18 PY - 1985 SP - 35 EP - 36 PB - RILEM Publ. CY - Cachan AN - OPUS4-34181 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Liehr, Sascha A1 - Krebber, Katerina A1 - Steffen, Milan A1 - Wosniok, Aleksander T1 - Fördermaßnahme KMU-innovativ: Informations- und Kommunikationstechnologie (IKT), EMS-261-003 (Digital OFDR - Entwicklung der digitalen Frequenzbereichsanalyse zur verteilten Rückstreumessung in optischen Fasern-Teilvorhaben: Sensorverfahren und Systembetrachtung / Schlussbericht zum Teilvorhaben KW - Digital OFDR KW - Verteilte Rückstreumessung KW - Frequenzbereichsanalyse PY - 2015 IS - BAM Vh 8158 SP - 1 EP - 45 CY - Berlin AN - OPUS4-34170 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Witt, Klaus T1 - Treshold ellipsoids in the CIE-colour-ranges - variability of observers T2 - 5th Congress of the International Color Association CY - Monte Carlo, France DA - 1985-06-16 PY - 1985 SP - 1 EP - 5 PB - Centre Francais de la Couleur CY - Paris AN - OPUS4-34175 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Amberg, Claus A1 - Czaika, Norbert T1 - On long term strain measurement in prestressed concrete structures at temperatures up to 120 °C with encapsulated weldable strain gages T2 - 10th IMEKO World Congress CY - Prague, Czech Republic DA - 1985-04-22 PY - 1985 VL - 3 SP - 78 EP - 85 PB - House of Technology CY - Prag AN - OPUS4-34178 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Klaffke, Dieter A1 - Kuntze, Gerd T1 - Wechselbiegmaschine für Ermüdungsuntersuchungen ohne und mit Reibbeanspruchung PY - 1985 SP - 18 EP - 19 PB - GIT-Verl. CY - Darmstadt AN - OPUS4-34130 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Habig, Karl-Heinz A1 - Hantsche, Harald T1 - Kennzeichnung von Verschleisserscheinungsformen durch Rasterelektronenmikroskopie und Augerelektronenspektroskopie T2 - 11. Sitzung des Arbeitskreises Rastermikroskopie in der Materialprüfung CY - Mülheim an der Ruhr, Germany DA - 1984-06-07 PY - 1985 SP - 13 EP - 44 PB - DVM CY - Berlin AN - OPUS4-34127 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Czepluch, Wolf T1 - Influence of luminance structures on binocular gloss T2 - 5th Congress of the International Color Association CY - Monte Carlo, France DA - 1985-06-16 PY - 1985 SP - 1 EP - 6 PB - Centre Francais de la Couleur CY - Paris AN - OPUS4-34139 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Döring, Günter T1 - Simplified match formulation for fluorescent colour specimens T2 - 5th Congress of the International Color Association CY - Monte Carlo, France DA - 1985-06-16 PY - 1985 SP - 1 EP - 6 PB - Centre Francais de la Couleur CY - Paris AN - OPUS4-34142 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gundlach, Dietrich T1 - Möglichkeiten der Sonnensimulation T2 - 60. PTB-Seminar CY - Braunschweig, Germany DA - 1984-10-10 PY - 1984 N1 - Serientitel: PTB-Bericht – Series title: PTB-Bericht IS - 17 SP - 1 EP - 10 PB - PTB CY - Braunschweig AN - OPUS4-34144 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Terstiege, Heinz T1 - Normung farbmetrischer Eigenschaften von Uni-Lacken T2 - 7. Fachtagung der Deutschen Forschungsgesellschaft Oberflächenbehandlung CY - Düsseldorf, Germany DA - 1985-12-09 PY - 1985 N1 - Serientitel: Vorträge und Diskussionen der Fachtagung/DFO e. V. – Series title: Vorträge und Diskussionen der Fachtagung/DFO e. V. IS - 7 SP - 125 EP - 136 PB - DFO CY - Düsseldorf AN - OPUS4-34147 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Terstiege, Heinz T1 - Onderzoek naar de levensduur van Verkeersborden [Forschung über die Lebensspanne von Verkehrsschildern] PY - 1985 SP - 14 EP - 16 PB - 3M Nederland BV CY - Leiden AN - OPUS4-34148 LA - nld AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Deppe, Hans-Joachim ED - Maloney, T. M. T1 - The utilization of wastepaper and refuse fiber material T2 - Nineteenth Washington State University International Particleboard/Composite Materials Symposium CY - Pullman, WA, USA DA - 1985-03-26 PY - 1985 SP - 1 EP - 16 PB - Washington State University CY - Pullman, Wash. AN - OPUS4-34115 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilsch, Gerd A1 - Eichler, T. A1 - Millar, Steven A1 - Gottlieb, Cassian T1 - Quantitative determination of chloride-to-cement content of concrete by laser-induced breakdown spectroscopy (LIBS) N2 - Laser-induced breakdown spectroscopy (LIBS) is a combination of plasma generation on the sample surface by a high power laser pulse and optical emission spectroscopy (OES). It is a direct measurement method without an extensive sample preparation. Concrete is a multi phase system. With LIBS it is possible to distinguish the different phases and based on that to correlate the chloride content to the cement mass. This is done by scanning the surface with a resolution of up to 0.1 mm. The high measurement frequency of 100 Hz or even higher allows the in-situ visualization of the chloride content over the measured area. With a calibration a quantification of chloride concentration is possible. As an example the LIBS measurement on a 50 mm by 70 mm area with a resolution of 0.5 mm and the visualization of the chloride distribution takes only 10 minutes. Additionally it is possible to evaluate the carbonation depth from the same measurement. Examples of practical application to determine the chloride-to-cement-content on concrete samples are presented. The possibilities and the limitations of LIBS are discussed. T2 - CONCREEP 10 - Mechanics and physics of creep, shrinkage, and durability of concrete and concrete structures CY - Vienna, Austria DA - 21.09.2015 KW - LIBS KW - Chlorides KW - Carbonation KW - Heterogeneity KW - Quantitative concentration KW - 2D-map PY - 2015 SP - 815 EP - 822 AN - OPUS4-34677 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Otremba, Frank A1 - Prabhakaran, A. A1 - Robitaille, A. A1 - Birk, A. M. A1 - Gonzalez III, F. T1 - Rail tank car total containment fire testing: results and observations N2 - The frequent incidences of Non-Accident Releases (NARs) of lading from tank cars have resulted in an increasing interest in transporting hazardous materials in total Containment conditions (i.e., no pressure relief devices). T2 - Proceedings of the 2016 joint rail conference CY - Columbia, SC, USA DA - 12.04.2016 KW - Rail tank containment fire PY - 2016 SN - 978-0-7918-4967-5 SP - 1 EP - 8 AN - OPUS4-35772 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erning, Wilhelm A1 - Dimper, Matthias A1 - Ahrens, A. A1 - Reimann, S. ED - Stojanovic, I. ED - Alar, V. ED - Simunovic, V. T1 - Corrosion behaviour of stainless steel in contact with ECA-generated disinfectant fluids N2 - The generation of active disinfectants by electrochemical processes gains market share due to the lack of need for transportation and storage of dangerous goods as well as the ease of operation. Usually the process involves the use of specific electrodes for electrolysis of water to produce active chlorine species, sometimes supported by addition of chlorides to the process water. The resulting ECA (ElectroChemically Activated) solutions can cause corrosion due to the content of free active chlorine (FAC) or due to the chloride content of the process solution. These fluids are widely used because they show a good chemical and microbiological stability, are well suited for the standard cleaning procedures and allow reducing germ concentrations to meet hygienic standards. The influence of the respective agents to alloy 1.4301 is investigated by storage experiments and by electrochemical investigations. The results show, that the influence of chlorides is higher for short-term experiments. ECA-Fluids with low chloride concentrations are preferable. The goal of the investigations is to creat evaluation guidelines for the application parameters to provide a sufficient cleansing effect without causing corrosion of the surfaces. T2 - 22. Savjetovanje o zaštiti materijala i industrijskom finišu Kormat 2016 CY - Zagreb, Croatia DA - 20.04.2016 KW - Disinfection pitting corrosion stainless steel PY - 2016 SN - 1848-4255 SP - 43 EP - 49 PB - HRVATSKO DRUŠTVO ZA ZAŠTITU MATERIJALA CY - Zagreb, Croatia AN - OPUS4-35807 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Maiwald, Michael T1 - Die neuen Prozess-Sensoren 4.0 - Selbstdiagnose, Selbstkalibrierung und Selbstkonfiguration stehen im Fokus N2 - Heute wie morgen müssen Prozess-Sensoren zuerst die Aufgabe des Messens und der Generierung von Prozessinformationen erfüllen. Die Mess-Signale gehen in der Regel auf physikalische oder chemische Größen zurück, werden durch eine Kennlinie repräsentiert und lassen sich kalibrieren. Heute muss man dazu einen großen Aufwand betreiben, denn die physikalischen oder chemischen Informationen werden in vielen Fällen nicht direkt gemessen, sondern verbergen sich in Rohdaten, z. B. in einem optischen Spektrum. Diese Kalibrierungen können für komplexe Sensoren teilweise mehr Kostenaufwand bedeuten, als das Messgerät selbst. KW - Prozess-Sensoren KW - Prozess-Sensoren 4.0 KW - Industrie 4.0 KW - Kommunikationsstandards KW - Technologie-Roadmap PY - 2016 SN - 0947-4188 IS - 7-8 SP - 16 EP - 16 PB - Wiley-VCH Verlag GmbH & Co. KGaA AN - OPUS4-35812 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Höhne, Christian T1 - Multimodal approach for the numerical simulation of ultrasonic guided waves in cylindrical structures of non-constant thickness N2 - Guided waves hold great potential for applications in the field of ultrasonic nondestructive testing. Examples of possible applications are the ultrasonic testing and structural health monitoring of wheelset-axles as used in trains. Depending on the particular type, these axles can be described as either thick cylindrical rods or thick walled hollow cylinders with varying thickness. Wheelset-axles are safety relevant components that have to be inspected on a regular basis. The use of guided waves would allow a full inspection while accessing only the front faces of the axle, thus potentially speeding up the inspection procedure. In order to develop such an inspection technique, however, detailed knowledge of wave propagation through the axle is required. Established mesh-based procedures, like the finite element method, could be used to simulate guided wave propagation in such structures. However, due to the size of the axle itself and the comparatively fine mesh that is dictated by the wavelengths usually applied in ultrasonic testing, these mesh-based procedures would be very expensive in terms of computation times. The multimodal approach seems to be a very promising alternative that can be expected to provide results significantly faster. The multimodal method uses the guided wave modes of a corresponding waveguide with a constant cross-section as basis in which the local sound field at any given position in a waveguide with varying thickness can be expressed. Thereby the numerical effort is reduced to solving the one dimensional differential equations that govern the evolution of the coefficients in the mode spectrum along the waveguide. Once the sound field has been calculated, a time dependence can easily be included, which allows the simulation of pulse propagation through the waveguide. In this thesis, the multimodal approach, as described for the calculation of Lamb-waves in plates with non-constant thickness, is extended to other types of elastic waveguides such as cylindrical rods and thick walled hollow cylinders. For the sake of simplicity, investigations are restricted to axially symmetric wave modes. The results obtained with the multimodal approach are validated against FEM-simulations. It is shown that the multimodal method potentially holds a great advantage in terms of computation time over commercially available software based on the finite element method. Finally, the multimodal method is evaluated with respect to possible future applications on wheelset-axles. KW - Guided waves KW - Wave propagation PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:co1-opus4-41255 SP - 1 EP - 123 PB - Brandenburgische Technische Universität CY - Cottbus AN - OPUS4-40884 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klingelhöffer, Hellmuth T1 - Demands for improvement of temperature stability of extensometers N2 - Thermal fluctuations do exist at extensometers but they remain quite often unknown because the temperature of the extensometer is not measured, recorded and assessed in strain controlled tests. The temperature fluctuation leads to thermal expansion of the gauge length of the extensometer resulting in force fluctuations as a materials response of the material tested in a strain controlled test. The thermal expansion leads to an error of the strain range applied. A case study was conducted to calculate the strain range error when the strain range was varied as well as the thermal fluctuation of the extensometer. The most important outcome of the study is that the strain range error can exceed the allowed limits if the thermal fluctuation of the extensometer is too high. Sources of thermal fluctuation of the extensometer were analyzed and identified. Suggestions are given to reduce the thermal fluctuation of the extensometer. T2 - LCF8 CY - Dresden, Germany DA - 27.06.2017 KW - Accuracy KW - Strain error KW - Temperature fluctuation KW - Extensometer PY - 2017 SN - 978-3-9814516-5-8 SP - 227 EP - 232 PB - DVM CY - Berlin AN - OPUS4-40888 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Huang, S. G. A1 - Vleugels, J. A1 - Mohrbacher, H. A1 - Woydt, Mathias T1 - NbC grain growth control and mechanical properties of Ni bonded NbC cermets prepared by vacuum liquid phase sintering N2 - The current study reports on the effect of the sintering temperature and secondary carbide (VC, Mo2C and TiC) additions on the microstructure and concommitant Vickers hardness (HV30) and fracture toughness of Ni-bonded NbC cermets. All cermets were prepared by pressureless sintering in vacuum. Detailed microstructural investigation was performed by electron probe microanalysis (EPMA) and X-ray diffraction (XRD) analysis. Sintering results indicated that both the sintering temperature and secondary carbide additions had a significant effect on the properties of NbC-Ni cermets. Nickel pools and residual pores were observed in the cermets sintered at temperatures ≤ 1340 °C. Increasing of the sintering temperature up to 1420 or 1480 °C resulted in fully densified NbC-Ni based cermets composed of homogeneous contrast cubic NbC grains for the single carbide (VC or Mo2C) modyfied system, whereas core-rim structured NbC grains were observed with the additon of TiC + VC or TiC+Mo2C. The secondary carbide doped cermets with 5–10 vol.% VC/Mo2C and 10 vol.% TiC showed a significantly improved hardness and fracture toughness, as compared to the plain NbC-Ni cermets. T2 - 19. Plansee Seminar CY - Reutte, Austria DA - 29.05.2017 KW - Cermet KW - Hard materials KW - Sintering KW - Microstructure KW - Core-rim KW - Mechanical properties PY - 2017 SP - HM 13/1 EP - HM 13/11 AN - OPUS4-40592 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Mohrbacher, H. A1 - Vleugels, J. A1 - Huang, S. T1 - Potentials of niobium carbide (NbC) as cutting tools and for wear protection N2 - The tool lifes of uncoated NiMo and NiMo2C-bonded stoichiometric NbC1.0 grades under dry turning 42CrMo4 and C45E were between +30 % to + 100 % higher and up compared to WC-6Co (fine grain). Niobium is today largely available. NbC grades displayed lower dry sliding friction over WC grades. T2 - 19. Plansee Seminar CY - Reutte, Austria DA - 29.05.2017 KW - Niobium carbide KW - Friction KW - Wear KW - NbC KW - Hard metal KW - Machining KW - Nickel PY - 2017 SP - HM 102/1 EP - HM 102/16 AN - OPUS4-40593 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Uhlmann, E. A1 - Kropidlowski, K. A1 - Woydt, Mathias A1 - Sammler, F. T1 - Cutting tools made from niobium carbide N2 - Niobium carbide (NbC) presented recently excellent Performance as cutting material for processing iron-based materials. Ist high hot hardness and low solubility in alloys make it a promising tool material for the future. T2 - 19. Plansee Seminar CY - Reutte, Austria DA - 29.05.2017 KW - Niobium carbide (NbC) KW - Tungsten carbide (WC) KW - Cutting material KW - Tool wear KW - Turning trials KW - Wear mechanisms PY - 2017 SP - HM 105/1 EP - HM 105/11 AN - OPUS4-40594 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Huang, S. G. A1 - Vleugels, J. A1 - Mohrbacher, H. A1 - Woydt, Mathias T1 - Effect of carbon content on the microstructure and mechanical properties of NbC-Ni based cermets N2 - The aim of this work was to correlate the carbon content in NbC-Ni starting powders with the resulting microstructure, hardness and fracture toughness of Ni-bonded NbC cermets. T2 - 19. Plansee Seminar CY - Reutte, Austria DA - 29.05.2017 KW - Cermet KW - Liquid phase sintering KW - Microstructure KW - Hardness KW - Carbon PY - 2017 SP - HM 109/1 EP - HM 109/11 AN - OPUS4-40595 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wäsche, Rolf A1 - Steinborn, Gabriele A1 - Woydt, Mathias T1 - Colloidal processing of metal bonded niobium carbide N2 - Manufacturing of Niobium carbide cermets with nickel binder and different additions of titanium carbide has been realized by colloidal processing in aqueous environment. T2 - 19. Plansee Seminar CY - Reutte, Austria DA - 29.05.2017 KW - NbC KW - TiC KW - Ni KW - Colloidal processing KW - Gas pressure sintering KW - Hardness PY - 2017 SP - HM 135/1 EP - HM 135/11 AN - OPUS4-40596 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosignuolo, F. ED - Chaves Spoglianti de Souza, Roberto ED - Andreini, M. ED - La Mendola, S. ED - Knaust, Christian T1 - A comparison between empirical models and FDS simulation to predict the ceiling gas temperature distribution in a tunnel fire N2 - A comparison between the results obtained from a Computational Fluid Dynamic (CFD) simulation and from the application of an empirical formula for determining the temperature distribution inside a tunnel in case of fire is presented. The temperature is measured and calculated at different distances from the location of the fire and at different time intervals. The fire considered varies with time following a time-heat release rate curve which has a parabolic growing phase, a constant period and a linear decay. The comparison reveals differences in the results. The temperatures calculated with the empirical formula resulted higher than the temperatures obtained by means of the CFD simulation. A list of possible reasons for this limited correspondence is also presented and commented. A proposal for further studies to better define the limitations of both the procedures and to define the influence of each parameter involved is finally presented. T2 - World Tunnel Congress 2017 – Surface challenges – Underground solutions CY - Bergen, Norway DA - 09.06.2017 KW - CFD KW - Fire KW - Tunnel KW - Design Fire PY - 2017 SP - 1 EP - 8 AN - OPUS4-40657 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Keller, Christian A1 - Herbrich, Uwe T1 - Plastic Instability of Rate-Dependent Materials - A Theoretical Approach in Comparison to FE-Analyses - N2 - The condition for plastic instability is a material characteristic and defines the onset of necking in tensile tests. In large deformation problems of ductile materials it is fundamental to determine the strain at which necking starts as well as the post-necking behaviour in the instability region properly. For verification purposes of material models, usually results of numerical analyses are compared to experimental outcomes. For tensile tests with ductile materials under dynamic loading, it is challenging to obtain comparable experimental and numerical results in terms of the onset of necking and the post-critical deformation behaviour. This paper focuses on the derivation of a theoretical criterion describing the plastic instability in rate-dependent materials based on the time variation of the strain gradient in a tensile specimen under isothermal conditions. We examine the influence of various constitutive equations on the theoretical stability condition predicted by different multiplicative as well as additive approaches. For multiplicative relations, the results indicate that the onset of necking is, in principle, independent of the strain rate, whereas for the considered additive relation, the dynamic necking strain must decrease with increasing strain rate. In conclusion, the theoretical stability condition is related to results from finite element simulations of dynamic tensile tests with various loading rates. It is shown that the simulated and the theoretical predicted onset of plastic instability agree reasonably. T2 - 11th European LS-DYNA Conference CY - Salzburg, Austria DA - 09.05.2017 KW - FEM KW - Plastic Instability KW - Dynamic Tensile Test PY - 2017 UR - http://www.dynalook.com/11th-european-ls-dyna-conference/crash-metal-failure/plastic-instability-of-rate-dependent-materials-a-theoretical-approach-in-comparison-to-fe-analyses SP - 1 EP - 10 AN - OPUS4-40660 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bradley, I. A1 - Scarponi, G. E. A1 - Otremba, Frank A1 - Cozzani, V. A1 - Birk, A. M. T1 - Experimental Analysis of a Pressurized Vessel Exposed to Fires: an Innovative Representative Scale Apparatus N2 - A novel deign of test equipment has been commissioned to investigate thermal stratification and boiling during fire exposure of pressure vessels. Extensive temperature measurements and video of the internal conditions during fire exposure are possible, and the equipment has been designed for future compatibility with laser-based velocity measurement techniques. It is expected to generate data large quantities of data that will be of use in validation of two- and three-dimensional CFD models for the prediction of pressure vessel behaviour in fire. Future work will seek to characterize the boundary layer conditions in detail for a range of test fluids, fill levels and fire-induced thermal boundary conditions. Initial tests undertaken during commissioning may indicate that fire exposure of the vessel wall just above the liquid level can have a notable influence on the pressurization rate, by increasing the degree of superheat. Further experimental and modelling work is required to confirm and quantify this effect, or to rebut this conclusion. T2 - ICH 13th International Conference on Chemical and Process Engineering CY - Milan, Italy DA - 28.05.2017 KW - Representative Scale Apparatus KW - Pressurized Vessel, KW - Fire PY - 2017 VL - 57 SP - 1 EP - 6 AN - OPUS4-40663 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Romero-Navarrete, José A. A1 - Otremba, Frank T1 - A massive vehicle-flexible pavement dynamic interaction simulator N2 - The interaction of the vehicles with the pavements imply damaging effects on both systems, as a function of the operating conditions and design characteristics of both systems. These effects influence the road pricing as well as the maintenance costs of the vehicles. In this paper, a simulation scheme has been proposed to analyze such interaction in massive way, involving a multivehicle models was the uncoupling of the roll and pitch responses. Results suggest that the damaging effects on the pavement and the vehicle, depends on the position along the road profile. However, the vertical design of the road would mainly affect the pavement damage, while the turning maneuvers would strongly influence the damage of the vehicle. Many uses can be identified for the proposed simulation scheme, involving different design and operating conditions for both systems. T2 - NAFEMS World Congress 2017 CY - Stockholm, Sweden DA - 11.06.2017 KW - Vehicle KW - Interaction simulator PY - 2017 SP - 1 EP - 11 AN - OPUS4-40667 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Romero-Navarrete, José A. A1 - Otremba, Frank T1 - Modelling of the lateral stability of river tankers N2 - A model of the cargo – ship interaction has been presented, for a navigation environment in which there is no waves, in which the ship lateral stability depends only on the manoeuver performed and the characteristics of the ship and cargo. Several simplifications have been introduced in the model, including the circular bottom of the ship, which facilitates the location of the buoyancy force on the ship, and the analogy of the sloshing cargo motion to a simple pendulum. Two forms of damping were introduced (river waters with the ship´s hull and the friction of the liquid inside the tanker walls), while the sliding motion of the ship when turning has been assumed as negligible. The results suggest that the sloshing cargo influences the lateral stability of the river tanker, with increases in the maximum roll angle from 15% to 40%, as a function of the speed and the fill level. The maximum roll angle has been found to occur at a 75% fill level, regardless of the ship speed. T2 - NAFEMS World Congress 2017 CY - Stockholm, Sweden DA - 11.06.2017 KW - Lateral stability KW - River tankers PY - 2017 SP - 1 EP - 11 AN - OPUS4-40669 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Mohrbacher, H. A1 - Vleugels, J. A1 - Huang, S. T1 - Status of nickel bonded niobium carbide (NbC) as a substitute for cobalt-bonded tungsten carbide (WC) as cutting tools and for wear protection N2 - Niobium is today largely available. The initial NbC grade was substoichiometric, SPS sintered and cobalt bonded (NbC0.88-12Co SPS). The NiMo-bonded stoichiometric NbC1.0 grades enable the subtituion of cobalt by nickel, SPS by conventional sintering and NbC0.88 by NbC1.0 in view of functional properties. Nickel bonded NbC grades have improved toughnesses versus cobalt bonded NbC grades, but lose hardness. NiMo and NiMo2C bonded NbC1.0 grades compensated the loss in hardness while keeping the toughness. T2 - POWDERMET 2017 CY - Las Vegas, USA DA - 13.06.2017 KW - Niobium carbide (NbC) KW - Cutting tools KW - Wear PY - 2017 SP - 721 EP - 734 PB - Metal Powder Industries Federation AN - OPUS4-40671 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eisermann, René T1 - C-OTDR Based Quasi-distributed Vibration Sensing Using High Scattering Fiber Segments - Performance for Subhertz Dynamic Strain Events N2 - Distributed vibration sensing (DVS) based on Rayleigh single pulse optical time-domain reflectometry (C-OTDR) is an attractive and robust method for a variety of sensing applications including geosensing. A key issue for the usability of DVS systems is the signal-to-noise ratio (SNR) and thus the feasibility to demodulate a measured signal, especially in the case of small dynamic strain amplitudes. We present a simple method to locally boost the sensitivity of DVS using pairs of fs-laser-written strongly scattering fiber segments. T2 - EAGE/DGG Workshop on Fibre Optic Technology in Geophysics CY - Potsdam, Germany DA - 31.03.2017 KW - C-OTDR KW - Distributed acoustic sensing KW - Quasi-distributed vibration sensing PY - 2017 UR - http://www.earthdoc.org/publication/publicationdetails/?publication=87755 DO - https://doi.org/10.3997/2214-4609.201700170 SP - SR P10 AN - OPUS4-40632 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kühnel, C. A1 - Bardl, Richard A1 - Stengel, Dominik A1 - Kiewitt, W. A1 - Grossmann, S. T1 - Investigations on the mechanical and electrical behaviour of HTLS conductors by accelerated ageing tests N2 - To cope with future requirements, the transfer capacities of distribution systems as well as of transmission systems in Europe need to be increased. Therefore repowering of existing overhead lines with high temperature low sag con-ductors (HTLS) can be one interesting possibility. Because of limited experiences with that technology, current re-search of TU Dresden, the Federal Institute for Materials Research and Testing (BAM) and 50Hertz Transmission GmbH investigates the ageing behaviour of several differ-ent HTLS technologies in a consortium with other Euro-pean partners. In this context, accelerated ageing tests of conductors and its corresponding fittings with combined mechanical and electrical loads are done. To evaluate the changes due to ageing, several mechanical tests of the con-ductors are carried out and the contact behaviour of the fittings is analysed. T2 - CIRED Conference CY - Glasgow, Scotland, UK DA - 12.06.2017 KW - HTLS KW - High temperature low sag KW - Resistance KW - Self-damping PY - 2017 SP - Paper 0200, 1 EP - 5 AN - OPUS4-40869 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weise, Hans-Peter A1 - Jost, Peter T1 - Shielding against scattered radiation at electron accelerator installations N2 - Shielding data for high energy X-rays scattered from common shielding materials at electron accelerators were determined. The required thickness of secondary protective barriers can be calculated if the intensity and the quality of scattered radiation are known. Therefore the differential exposure albedo of various important materials was measured for primary X-rays in the energy ränge from 10 MeV to 35 MeV using an electron linear accelerator. The quality of secondary X-rays was investigated by measuring the spectra of scattered photons with a Nal-detector. From these spectra the attenuation of scattered X-rays in common shielding materials was computed using transmission factors for monoenergetic photons taken from the literature. The calculations were performed for the limiting cases of broad beam and narrow beam geometry. The results are compared with directly measured attenuation curves and with recommendations given in the literature. PY - 1983 IS - 45 SP - 3 EP - 7 AN - OPUS4-40798 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wüstenberg, Hermann A1 - Erhard, Anton T1 - Matching of Ultrasonic Flaw Sizing Methods to the Defect Type and Location N2 - During the last ten years many specialized ultrasonic flaw sizing methods have been reported in the literature and used in practical applications . Most of the proposed approaches are restricted to the special types of defects investigated by the respective authors. Some are specifically for throughsurface cracks, others are able to analyze the size of planar, internal defects with smooth surfaces, and other methods can only be applied if the expected defect sizes are smaller than or significantly larger than the wave length. It is obvious that defect sizing with ultrasound can nowadays be based on a lot of different Instruments, which currently must be selected for a given problem. T2 - Deutsch-Japanisches Seminar CY - Tokyo, Japan DA - 21.08.1983 PY - 1983 VL - 2 AN - OPUS4-40854 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kuschke, Christian A1 - Wille, Frank A1 - Ballheimer, Viktor A1 - Sterhaus, Jens A1 - Apel, Andreas T1 - Standards and guidelines for design of trunnions of RAM transport packages N2 - Trunnion systems of packages for the transport of radioactive materials have to guarantee the safe handling of package during crane operations (lifting, tilting) and to secure package tie down to the transport vehicle, if the trunnions are used as attachment points during transport. The design of trunnions is based on IAEA Regulations SSR-6, the supporting Advisory Material SSG-26 and further appropriate technical standards and/or guidelines. For package approval procedures in Germany the guideline BAM-GGR 012 has to be applied. If a package is handled inside a german nuclear power plant, the standard KTA 3905 has to be fulfilled additionally. In this paper the requirements of KTA 3905 concerning the trunnion systems as load attaching points (LAP) are discussed in connection with the recommendations in the guideline BAM-GGR 012. This guideline is prepared at BAM Federal Institute for Materials Research and Testing for analysis and assessment of bolted lid and trunnion systems of Type B(U) transport packages. The Quality assurance questions concerning trunnion systems are discussed as well. T2 - WM 2017 conference CY - Phoenix, USA DA - 05.03.2017 KW - RAM transport package KW - Trunnions PY - 2017 SP - Paper 17365, 1 EP - 12 AN - OPUS4-40815 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neider, Rudolf A1 - Schmitt, B. F. A1 - Segebade, Christian A1 - Kühl, M. T1 - Photonenaktivierungsanalyse mit Hilfe von Elektronenbeschleunigern N2 - Die Photonenaktivierungsanalyse beruht auf folgendem Prinzip; In einem Elektronenlinearbeschleuniger werden die von einer Glühkathode erzeugten Elektronen in einem Hohlwellenleiter auf eine hohe Energie gebracht. Sie erzeugen beim Auftreffen auf ein Schwer metalltarget ein Bremsstrahlungskontinuum (Abb. 1 und 2). Dessen Maximalenergie ist gleich der der Elektronen. Die Photonen dieser Bremsstrahlung erzeugen in den zu analysierenden Proben Kernreaktionen (Kernphotoeffekt), wobei im allgemeinen durch die (y,n)- Reaktion neutronenärmere Radioisotope der jeweiligen Elemente gebildet werden. Durch y-Spektroskopie läßt sich anschließend der Gehalt von vielen Elementen in diesen Proben bestimmen. T2 - Elementanalyse von Schwebstäuben : (erste Ergebnisse d. AFR-Luftstaub-Verbundprogramms LVPr) ; Kolloquium am 29. Juni 1982 im Kernforschungszentrum Karlsruhe CY - Karlsruhe, Germany DA - 29.06.1982 PY - 1983 VL - Reportnummer: KfK-AFR 006 SP - 234 EP - 254 AN - OPUS4-40841 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Omar, Mohamed A1 - Wilken, Klaus T1 - Schweißeigenspannungs- und Schrumpfungsmessungen an großen Platten N2 - Für Schweißverbindungen des Stahls St E 460 ist die Verteilung der Schweißeigenspannungen in einer stumpfgeschweißten größeren Platte bisher nicht hinreichend untersucht worden. Zwei Gründe könnten für eine gegenüber dem "klassischen Schweißeigenspannungszustand" der Einlagenschweißung an normalem Baustahl deutlich abweichende Verteilung angeführt werden: 1. die Viellagentechnik, bei der die jeweils nachfolgende Schweißraupe eine Änderung des vorher entstandenen Schweißeigenspannungszustandes bewirkt. 2. Die Neigung des St E 460, an Schweißverbindungen von der Abkühlungsgeschwindigkeit abhängige Abschreck- und Gefügeeigenspannungen aufzubauen, wie sie beim normalen Baustahl kaum beobachtet werden. T2 - Symposium der Deutschen Gesellschaft für Metallkunde PY - 1983 VL - 1 SP - 391 EP - 408 AN - OPUS4-40846 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Tamberg, Tomas T1 - Fortschritte der nationalen und internationalen Normung auf den Gebieten Messung von Kontamination, Dekontaminierbarkeit von Oberflächen und Wirkung von Dekontaminationsmitteln N2 - Es wird der Stand der Arbeiten in den Normausschüssen NKe AA2.6 (Oberflächendekontaminationsverfahren), IS0/TC85/SC2/WG9 (Evaluation of contamination) und IS0/TC85/SC2/WG10 (Ease of Decontamination) beschrieben. Der NKe-Ausschuß bemüht sich um die Normung eines Prüfverfahrens, das die Bestimmung der Wirksamkeit von Dekontaminationsmitteln (incl. entsprechender Waschmittel) ermöglichen soll. Daneben betreibt dieser Ausschuß die Verbesserung der Dekontaminierbarkeitsnorm DIN 25415, Teil 1 in Zusammenarbeit mit IS0/TC85/SC2/WG10. Dieser ISO-Ausschuß wiederum hat seine Arbeit auf die Prüfung einer Kompromißvorschrift mit deutschen und britischen Anteilen konzentriert und macht auf der Basis von internationalen Ringexperimenten Fortschritte. ISO/TC85/SC2/WG9 hat bisher ein fast abstimmungsreifes Papier "Messung von Kontamination" erarbeitet, das sich auf ß-Strahler mit Maximalenergien >. 0,15 MeV und a-Strahler bezieht. Ein entsprechender Entwurf zur Messung von Tritium-Oberflächenkontaminationen berücksichtigt bereits eine Gruppe erster Einsprüche aus den Kreisen der SC-2-Mitglieder. Der Beitrag beschreibt wichtige Teilaspekte, die sich aus diesen Normungsbemühungen ergeben haben und macht Angaben über die zu erwartenden Entwicklungen auf den betreffenden Gebieten. T2 - Jahrestagung des Fachverbandes für Strahlenschutz e.V. : in Zsarb. mit der Gesellschaft für Strahlen- und Umweltforschung mbH, Institut für Strahlenschutz CY - Neuherberg DA - 08.06.1983 PY - 1983 VL - 17 SP - 47 EP - 52 CY - Neuherberg AN - OPUS4-40826 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dümmel, Martin A1 - Lohrer, Christian A1 - Mücke, Olaf T1 - Tumbling effects of cylindrical shells N2 - In the future new types of lift charges for display Shells will enter the market. These types may not be based on black powder and therefore will show different Performance behaviors. The European standard series EN 16261 deals with the testing and assessment of display fireworks in order to satisfy the essential safety requirements which have to be met before placing these items on the EU market. The aim of the study is to investigate how certain types of lift charges (NC based) influence the lift, tumbling and drift of cylindrical shells. In consequence, if the performance characteristics deviate strongly from those of typical black powder, safety related regulations in the EU and Germany might be affected, as well. For these investigations, over 50 cylindrical shells were specifically manufactured at BAM to guarantee full influence on all relevant constructional aspects. The shells were constructed to be “blind”, i. e. without break and effect charges, to investigate drift effect on ground in relation to the shooting location. The only reactive substances were the lift charges and a tracer star at the bottom of the shells to guarantee visibility for the post processing using the video grammetric system. The cylindrical shells were of a nominal caliber of 100 mm and manufactured in three different length configurations (single, double and triple length). Their gross weights were designed to correspond to typical effect shells of the same kind. In addition, the impact of different weight distributions inside the shells, leading to altered balance points, on the performance parameters of the shells were also part of this study. Three different types of NC based lift charges were used to show a variety in pressure build ups. T2 - 16th International Symposium on Fireworks CY - Omagari, Japan DA - 24.04.2017 KW - Fireworks KW - Shells KW - Tumbling PY - 2017 SP - 305 EP - 322 AN - OPUS4-40608 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Preß, Henning A1 - von Nieding, G. A1 - John, S. A1 - Wagnitz, K. T1 - Untersuchung über die Entstehung und Wirkung gesundheitsgefärdender Stoffe beim Lichtbogenhandschweißen in Druckluft T2 - Internationales Symposium Unterwasserschweißen CY - Geesthacht DA - 23.06.1983 PY - 1983 SP - 111 EP - 117 AN - OPUS4-40764 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Casperson, Ralf A1 - Heckel, Thomas T1 - New evaluation methods for non-destructive rail inspection using eddy current and ultrasound N2 - Since 1999 there has been a continuous development of non-destructive head check inspection. Especially in case of modern rail inspection systems, high demands on a fast, detailed detection and classification of defects called for improved testing methods. Due to the large amount of different rail types and profiles, the adaptation and optimization of algorithms is still in progress. Additional data analysis is under devel-opment for combined eddy current and ultrasonic inspection methods. This presentation gives an over-view of further enhancement and linking of testing systems as well as data processing. Main foci of the development are an improved sensitivity and an increased reliability of the testing results. Also, addi-tional information can be obtained like determination of local hardness and roughness of the rail as well as an enhanced resolution for locating of defects which will be part of the presented work. T2 - Railway Engineering-2017 CY - Edinburgh, UK DA - 21.06.2017 KW - Eddy current testing KW - Ultrasonic testing KW - Rail inspection KW - Data evaluation KW - Classification PY - 2017 SN - 0-947644-83-0 DO - https://doi.org/10.25084/raileng.2017.0078 SP - 1 EP - 10 AN - OPUS4-40767 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krause, Hans-Joachim T1 - How to do the process control data for spot welding depend on the nugget growth? N2 - Physieal magnitudes, for example voltage drop between the electrodes, measured during welding, are used to make Statements on the nugget size. These physieal magnitudes are used as process control data in the process control of spot welding /1/. A multitude of studies has been concentrating upon the question of which kind of correlation is existing between the quality of the completed weid and the process control data measured during thecurrent time. However, the question of which kind of correlation is existing between the instantaneous values of the process control data and the respective nugget size during the individual current periods was largely neglected. The knowledge of this correlations is necessary to estimate the Signal behaviour influenced by ^isturbance Parameters and to compare different process control data. In a first contribution to this subject 0.8 mm thick specimens of St 1305 to be used for macrosections were welded. The current time was to be extended by 1 period for each specimen with the other conditions remaining constant. During welding the voltage drop between the electrodes and the electrode speed was measured. PY - 1983 AN - OPUS4-40721 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krause, Hans-Joachim T1 - Test methods for torsing testing of spot welds and scatter of the test results N2 - i\t the annual meeting 1982 working group III-WG-7 "Testing of overlap welds" decided the following actions: a) a document with additional informations on the kind of test rnethod and the Instrumentation of the Equipment b) a document containing more Information about the Statistical behaviour of the test results given by the shear and the t o r s i o n test. The present document is concerned with both subjects. A historical overlook of the development, use and assessment of the torsion test for resistance spot welds was given in Doc. III-WG7-22-82 / 1/. Few .Information of the test procedure was given in /2/. The main aim of document III-WG7~18-81 /2/ is to give informations and interpretations of test results. This document took specially into eonsideration results of the Torsion test (torsional moment, torsional angle, spot diameter) and the results of other mechanioal tests on spot welds. PY - 1983 AN - OPUS4-40722 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lugovtsova, Yevgeniya A1 - Prager, Jens T1 - Structural health monitoring of composite pressure vessels using guided ultrasonic waves N2 - Composite pressure vessels are important components for storing gases under high pressure. Beside others, a common type of pressure vessel is made of a metal liner overwrapped with a fibre reinforced plastic material. Conventional hydrostatic tests, used to assess the integrity of pressure vessels, may overstress the material, and thus, may reduce the remaining life-time of the tested component. Therefore, a truly nondestructive structural health monitoring (SHM) system would not only allow to ensure a safer usage and extended life-time, but also to exclude the necessity of the periodic inspection and testing of pressure vessels. We propose to use guided ultrasonic waves which have a potential to detect the main damage types such as cracking in the metal liner, fibre breaks and composite Matrix delamination. For designing such a SHM system, the multimodal ultrasonic wave propagation and the defect-mode interaction must be fully understood. In this contribution, we present simulation results obtained by means of finite element modelling. Based on the findings, suggestions about appropriate wave modes, their interaction with different flaw types as well as the necessary excitation and suitable sensor configuration are made. Finally, we suggest a first approach of a reliable SHM system for composite pressure vessels. T2 - First World Congress on Condition Monitoring (WCCM) CY - London, UK DA - 13.06.2017 KW - Composite materials KW - Simulations KW - Ultrasonic testing PY - 2017 SP - 1 EP - 12 AN - OPUS4-40678 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jost, Peter A1 - Weise, Hans-Peter T1 - Messung der Luftaktivierung beim Betrieb von Elektronenbeschleunigern und Vergleich mit theoretischen Rechnungen T2 - Jahrestagung des Fachverbandes für Strahlenschutz in Zusammenarbeit mit der Gesellschaft für Strahlenschutz- und Umweltforschung, Institut für Strahlenschutz CY - Neuherberg ; (München) DA - 19.10.1982 PY - 1983 SP - 239 EP - 242 AN - OPUS4-40686 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Milster, Helga A1 - Sommer, Ulrich A1 - Meckel, Lothar T1 - Prüfung und Beurteilung von Waschmitteln T2 - 5. Vortragstagung Fortschritte der Waschmittelchemie CY - Konstanz, Germany DA - 25.04.1983 PY - 1983 SP - 262 EP - 281 AN - OPUS4-40924 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klingelhoeffer, Hellmuth T1 - Actual developments in fatigue standardisation N2 - Standardization of fatigue testing procedures takes place mainly on the international scale. The International Organization for Standardization (ISO) and ASTM International (formerly American Society for Testing and Materials) are the most important global players in fatigue standardization. The actual developments in fatigue standardization on ISO scale are shown. Several ISO fatigue testing standards are currently under revision. These are the strain controlled low cycle fatigue testing standard ISO 12106, the strain controlled thermo-mechanical fatigue standard ISO 12111, the force controlled axial fatigue test ISO 1099, the rotating bar bending fatigue test ISO 1134, the cyclic fatigue test DIN 50100, the statistical planning and analysis standard ISO 12107, the fatigue crack growth test ISO 12108 and the Multi-axis fatigue test ISO / TR 12112. Additionally, suggestions for measurement uncertainty annexes of ISO standards are given. Problems regarding the temperature stability of extensometers are reported. In this presentation, an overview over the actual developments in the progress of fatigue testing standards will be given. T2 - LCF8 CY - Dresden, Germany DA - 27.06.2017 KW - Fatigue standardisation KW - ISO 12106 KW - ISO 12111 KW - DIN 50100 PY - 2017 SN - 978-3-9814516-5-8 SP - 239 EP - 244 PB - DVM CY - Berlin AN - OPUS4-40889 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröder, Hertmut A1 - Grabe, W. T1 - Mechanische Eigenschaften PY - 1983 SP - 1 EP - 11 AN - OPUS4-40901 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maierhofer, Christiane A1 - Krankenhagen, Rainer A1 - Röllig, Mathias A1 - Unnikrishnakurup, Sreedhar A1 - Monte, C. A1 - Adibekyan, A. A1 - Gutschwager, B. A1 - Knazowicka, L. A1 - Blahut, A. A1 - Gower, M. A1 - Lodeiro, M. A1 - Baker, G. A1 - Aktas, A. T1 - Einfluss thermischer und optischer Materialeigenschaften auf die Charakterisierung von Fehlstellen in Faserverbundwerkstoffen mit aktiven Thermografieverfahren N2 - In diesem Beitrag werden zerstörungsfreie Untersuchungen mittels aktiver Thermografie an Probekörpern aus CFK und GFK mit unterschiedlichen künstlichen Fehlstellen vorgestellt. Dabei wird die zeitliche und örtliche Temperaturverteilung nach Erwärmung mit Blitzlampen oder mit einem Infrarot-Strahler mit einer Infrarot-Kamera erfasst. Zur Rekonstruktion der Messdaten wurde ein numerisches Modell entwickelt. Dazu war die Bestimmung der thermischen und optischen Materialeigenschaften erforderlich. N2 - This paper presents results of the non-destructive evaluation of CFRP and GFRP test specimens with various artificial defects using active thermography. After heating the samples with flash lamps or with an infrared radiator, the temporal and spatial resolved temperature distribution is recorded with an infrared camera. For the reconstruction of the experimental data, a numerical model was developed. For the numerical simulations, the thermal and optical material parameters had to be determined. T2 - Temperatur 2017 CY - Berlin, Germany DA - 17.05.2017 KW - CFK KW - GFK KW - aktive Thermografie KW - numerische Simulation KW - Emissivität PY - 2017 SN - 978-3-944659-04-6 SP - 15 EP - 20 AN - OPUS4-41088 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Schlichting, S. A1 - Hönig, Gerald A1 - Müßener, J. A1 - Hille, P. A1 - Grieb, T. A1 - Teubert, J. A1 - Schörmann, J. A1 - Wagner, M. R. A1 - Rosenauer, A. A1 - Eickhoff, M. A1 - Hoffmann, A. A1 - Callsen, G. T1 - Tuning of the Quantum-Confined Stark Effect in wurtzite [000-1] group-III-nitride nanostructures by the Internal-Field-Guarded-Active-Region Design N2 - Recently, we suggested an unconventional approach [the so-called Internal-Field-Guarded-Active-Region Design (IFGARD)] for the elimination of the crystal polarization field induced quantum confined Stark effect (QCSE) in polar semiconductor heterostructures. And in this work, we demonstrate by means of micro-photoluminescence techniques the successful tuning as well as the elimination of the QCSE in strongly polar [000-1] wurtzite GaN/AlN nanodiscs while reducing the exciton life times by more than two orders of magnitude. The IFGARD based elimination of the QCSE is independent of any specific crystal growth procedures. Furthermore, the cone-shaped geometry of the utilized nanowires (which embeds the investigated IFGARD nanodiscs) facilitates the experimental differentiation between quantum confinement- and QCSE-induced emission energy shifts. Due to the IFGARD, both effects become independently adaptable. KW - Piezoelectricity KW - Quantum Confined Stark Effect (QCSE) KW - Nanophotonics KW - Semiconductor nanostructures KW - Spontaneous polarization KW - Internal-Field-Guarded-Active-Region Design (IFGARD) PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-411013 DO - https://doi.org/10.48550/arXiv.1707.06882 SN - 2331-8422 SP - 1 EP - 9 PB - Cornell University CY - Ithaca, NY AN - OPUS4-41101 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hering, Henrik A1 - Matzke, Martina ED - Davies, M. P. ED - Pfeiffer, C. ED - Robinson, W. H. T1 - Parasitoids for classical biological control of Tineola Bisselliella (Lepidoptera: Tineidae) N2 - Two species of parasitoid wasps, Apanteles carpatus (Hymenoptera: Braconidae) and Baryscapus tineivorus (Hymenoptera: Eulophidae), are known to successfully parasitize larvae of tineid moths. We have evaluated each species potential impact on suppressing the pest Tineola bisselliella (Lepidoptera: Tineidae). Both parasitoids have shown high potential for biological control of webbing clothes moth larvae when tested on different host instars in the laboratory and field. Preferences for parasitizing older and larger host larval instars for egg largely overlap in both species. Apanteles carpatus is a solitary koinobiont and parthenogen, while B. tineivorus is a gregarious koinobiont, with a sex ratio of approximately 1:5 (male:female). Solitary reproduction in A. carpatus markedly suppressed the pest population early on but lagged large numbers of progeny in the F(-generation. Gregarious reproduction resulted in a faster build-up of the F1generation but lagged the immediate control effect. Combining the release of both parasitoid species for pest control seemed to be the logical conclusion. We tested the reproductive success of both species when experimentally forced into intensive intraguild competition. For this, parasitoids had either to compete simultaneously or slightly time shifted on the same preferred host resource. Reproductive success of A. carpatus was not significantly influenced by the presence of B. tineivorus. B. tineivorus reproductive output was significantly reduced in the presence of A. carpatus. Overall Suppression of host development was not significantly enhanced with both parasitoid species co-occurring when compared to their exclusive access to hosts. B. tineivorus does not significantly improve the control of webbing clothes moth hosts when occurring together with and having to compete against A. carpatus, at least in restricted laboratory conditions. Results show that B. tineivorus should be released with a temporal advantage of at least several days. For inundative release, reproduction strategies and even competition between parasitoids is negligible, and a deferred release strategy would not be required. T2 - Ninth International Conference on Urban Pests CY - Birmingham, UK DA - 09.07.2017 KW - Intraguild predation KW - Apanteles carpatus KW - Baryscapus tineivorus KW - Biological control KW - Inoculative release PY - 2017 SN - 978-1-5272-0738-7 VL - 9 SP - 335 EP - 345 AN - OPUS4-41017 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lange, Thorid T1 - Mehr-Proben-Kleb-Technologie zur Validierung der Klebfestigkeit N2 - Mit der Verfügbarkeit der Mehr-Proben-Prüfung von bis zu 8 Klebverbunden mittels CAT-Technologie (CAT: centrifugal adhesion testing) wurde im Forschungsvorhaben OKTETT ein durchgehendes Mehr-Proben-Konzept zur Validierung der Klebfestigkeit angewendet. Dazu gehört ein universeller Probenteller zur Mehr-Proben-Handhabung bei Vorbehandlung, Lagerung, Transport und Klebung. Für das Mehr-Proben-Kleben wurde die MSB-Technologie (MSB: multiple sample bonding) unter Verwendung einer instrumentierten hydraulischen Mehr-Proben-Klebvorrichtung entwickelt. Damit kann der Klebandruck für bis zu 8 Prüfkörper über einen Drucksensor definiert eingestellt und die gesamte Vorrichtung beim Kleben Temperatu-ren von bis zu 180°C ausgesetzt werden. T2 - 12. ThGOT Thementage Grenz- und Oberflächentechnik und 5. Kolloquium Dünne Schichten in der Optik CY - Zeulenroda, Germany DA - 14.03.2017 KW - Zentrifugentechnologie KW - Mehr-Proben-Kleben (MSB) KW - Mehr-Proben-Prüfen (CAT) KW - Haftfestigkeit KW - Verbundfestigkeit PY - 2017 SN - 978-3-00-055614-2 SP - 1 EP - 2 AN - OPUS4-41467 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Richter, Janine A1 - Jann, Oliver A1 - Wilke, Olaf T1 - Emissions of formaldehyde from acoustic tiles N2 - Acoustics is an important aspect for large rooms especially in schools, kindergartens and offices. Foam tiles made from melamine resins are often used for acoustic insulation because they show good fire resistance and good thermal insulation properties. But they can emit formaldehyde. In Germany there are cases with a resulting indoor air concentration of higher than 100 µg/m³. In this study samples from two schools and one office were investigated. Additionally, new tiles were purchased and tested to evaluate the general potential as formaldehyde source. T2 - Healthy Buildings 2017 Europe CY - Lublin, Poland DA - 02.07.2014 KW - Building product KW - Emission test chamber KW - Formaldehyde KW - Foam tiles PY - 2017 SN - 978-83-7947-232-1 SP - Paper 0176, 1-2 AN - OPUS4-41574 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Martin A1 - Eisenacher, Germar A1 - Schönfelder, Thorsten A1 - Wille, Frank T1 - Development of a material model for the crush of spruce wood N2 - Typical transport packages used in Germany are equipped with wooden impact limiting devices. In this paper we give an overview of the latest status regarding the development of a finite element material model for the crush of spruce wood. Although the crush of wood – mainly in longitudinal direction – is a phenomenon governed by macroscopic fracture and failure of wood fibres we smear fracture and failure mechanisms over the continuous voume. In first step we altered an existing LS-DYNA material model for foams, which considers an ellipse shaped yield surface written in terms of the first two stress invariants. The evolution of the yield surface in the existing model depends on the volumetric strain only. For the use with spruce wood, we modified the existing material model to consider the deviatoric strain for the evolution of the yield surface as well. This is in accordance with the results of crush tests with spruce wood specimens, where the crushing deformation was rather deviatoric for uniaxial stress states and rather volumetric for multiaxial stress states We rate the basic idea of this approach to be reasonable, though other problems exist regarding the shape of the yield surface and the assumption of isotropic material properties. Therefore we developed a new transversal isotropic material model with two main directions, which considers different yield curves according to the multiaxiality of the stress state via a multi-surface yield criterion and a non-associated flow rule. The results show the ability to reproduce the basic strength characteristics of spruce wood. Nevertheless, problems with regularization etc. show that additional investigations are necessary. T2 - ASME PVP 2017 CY - Waikaloa, HY, USA DA - 16.07.2017 KW - Chrush KW - Spruce KW - Wood KW - FEM PY - 2017 SN - 978-0-7918-5802-8 VL - 7 SP - Article UNSP V007T07A037, 1 EP - 9 AN - OPUS4-41613 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wüstenberg, Hermann A1 - Schulz, Eduard A1 - Erhard, Anton A1 - Sonnenberg, G. A1 - Loening, P. T1 - Ultrasonic inservice inspection of shrinkage cracks at turbine rotor discs N2 - During the revision of turbines in power plants,shrinkage cracks in the rotor discs have been detected, whieh are generated sometimes in a keyway area if present or generally in some specially loaded areas of the shrinkage /l, 2/. The crack generation produces ultrasonically reflecting surfaces oriented parallel to the turbine shaft axes and parallel to the turbine diameter. For the detection of such cracks during an inservice inspection a manual or in most cases a mechanical scanning seems to be necessary. Some development and results are reported in /l, 2/. In this contribution we will describe some Solutions we started to develop together with the KWU-Berlin for a special geometric Situation. We will restrict the report on the ultrasonic Problems to solve. T2 - 5. International Conference on NDE in the Nuclear Industry CY - San Diego, CA, USA DA - 10.05.1982 PY - 1983 SP - 373 EP - 378 PB - American Society for Metals CY - Metals Park, Ohio AN - OPUS4-41794 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bulling, Jannis A1 - Prager, Jens A1 - Krome, Fabian T1 - Application of the scaled boundary finite element method (SBFEM) for a numerical simulation of ultrasonic guided waves N2 - This paper addresses the computation of dispersion curves, mode shapes and propagation of elastic guided waves. It summarizes the approaches based on the Scaled Boundary Finite Element Method. Descriptions for plates, rods, pipelines and waveguides with an arbitrary cross section are included. The important steps for the approximation of the displacement in bounded and unbounded domains are stated. The grid generation process is explained. It is highlighted that the Scaled Boundary Finite Element Method is very efficient, if large portions of the domain are either straight or with a constant curvature. The computation of dispersion curves for layered structures is presented. T2 - Sensor + Test CY - Nürnberg, Germany DA - 30.05.2017 KW - Ultrasonic guided waves KW - Non-destructive testing KW - Scaled boundary finite element method (SBFEM) PY - 2017 SN - 978-3-9816876-4-4 VL - 2017 SP - C5.4, 376 EP - 381 AN - OPUS4-41876 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Müller, C. A1 - Halle, T. T1 - Einfluss der Schweißnaht-Nachbehandlung auf die Korrosionsbeständigkeit vom Duplexstahl 1.4062 N2 - Der Duplexstahl 1.4062 (X2CrNi22-2) hat sich im Bauwesen als Werkstoffalternative zu den nichtrostenden Austeniten etabliert. Die Korrosionsbeständigkeit von Schweißverbindungen wird, neben dem Grundwerkstoff, dem Schweißzusatzwerkstoff und dem Schweißverfahren, auch sehr stark von der Schweißnaht-Nachbehandlung beeinflusst. Je nach zukünftigem Anwendungsbereich, geforderter Optik und Korrosionsbeständigkeit wird die Schweißnaht geschliffen, gebeizt, elektropoliert oder gestrahlt, um die beim Schweißen entstehenden An-lauffarben zu entfernen. Gestrahlte Oberflächen sind in der industriellen Praxis häufig anzutreffen, da sie deutlich schneller und kostengünstiger herzustellen sind als geschliffene, gebeizte oder polierte Oberflächen. Das Strahlen mit Korund ist außerdem effektiver als das Strahlen mit Glasperlen. In den letzten Jahren wurden korrosionsanfällige Oberflächen bei nichtrostenden Stählen beobachtet, wenn diese mit Korund geschliffen wurden. Daher wird nun auch beim Strahlen kritisch hinterfragt, ob die eingesetzten Strahlmittel die Korrosionsbeständigkeit beeinflussen. Diese Fragestellung wird beantwortet, indem geschliffene, gebeizte, polierte und mit verschiedenen Strahlmitteln gestrahlte Schweißverbindungen vom Duplexstahl 1.4062 im Vergleich zu gleichartig behandeltem Walzmaterial untersucht werden. Die Ergebnisse der Korrosionsuntersuchungen werden vorgestellt und mit den rasterelektronenmikroskopischen Untersuchungen der gestrahlten Oberflächen korreliert. T2 - 16. Sommerkurs Werkstoffe und Fügen CY - Magdeburg, Germany DA - 08.09.2017 KW - Duplexstahl KW - Nichtrostender Stahl KW - Schweißen KW - Oberflächenbearbeitung KW - Strahlen KW - Korrosion PY - 2017 SN - 978-3-944722-58-0 DO - https://doi.org/10.24352/UB.OVGU-2017-75 SP - 63 EP - 70 AN - OPUS4-41888 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Kauss, N. A1 - Müller, C. A1 - Halle, T. T1 - Einfluss der Abkühlgeschwindigkeit auf die Neigung zur Chromverarmung martensitischer nichtrostender Stähle N2 - Die Legierungselemente (Chrom und Kohlenstoff) und die Wärmebehandlung bestimmen Korrosionsbeständigkeit und Härte martensitischer nichtrostender Stähle. Verschiedene wissenschaftliche Arbeiten haben bereits gezeigt, dass die Korrosionsbeständigkeit sehr stark vom Anteil an Chromkarbiden im Gefüge bestimmt wird. Der kombinierte Einfluss von Kohlenstoffgehalt und der Abkühlgeschwindigkeit beim Härten wurde mit Fokus auf die Korrosionsbeständigkeit bisher nur unzureichend untersucht. Die Literatur liefert außerdem gegensätzliche Aussagen über den Einfluss der Abkühlgeschwindigkeit, was möglicherweise auf unterschiedliche Kohlenstoffgehalte zurückgeführt werden kann. In dieser Arbeit wird daher systematisch untersucht, ab welcher Abkühlgeschwindigkeit es bei den Werkstoffen X20Cr13 und X46Cr13 zu Karbidbildung und Chromverarmung kommt. Die Variation der Abkühlgeschwindigkeit erfolgte für die industriell relevante Härtetemperatur von 1050 °C mit dem Stirnabschreckversuch. In Abhängigkeit von der Abkühlgeschwindigkeit wurden an den Stirnabschreckproben Gefüge, Härte und Korrosionsbeständigkeit (EPR, kritische Lochkorrosionspotentiale) untersucht und die Ergebnisse mit thermodynamischen Berechnungen (ThermoCalc) korreliert. Aus den Ergebnissen wird abgeleitet, unter welchen Bedingungen die Abkühlgeschwindigkeit die Korrosionsbeständigkeit beeinflusst. T2 - 16. Sommerkurs Werkstoffe und Fügen CY - Magdeburg, Germany DA - 08.09.2017 KW - Wärmebehandlung KW - Korrosion KW - Chromverarmung KW - EPR KW - Martensitischer nichtrostender Stahl KW - ThermoCalc KW - Lochkorrosion PY - 2017 SN - 978-3-944722-58-0 DO - https://doi.org/10.24352/UB.OVGU-2017-75 SP - 71 EP - 78 AN - OPUS4-41889 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Müller, C. A1 - Halle, T. T1 - Sensibilisierungsverhalten vom stickstofflegierten, austenitischen, nichtrostenden Stahl 1.4456 N2 - Austenitische nichtrostende Stähle kommen seit vielen Jahren in den verschiedensten industriellen Zweigen zum Einsatz (Pharma-, Medizin- und Lebensmittelindustrie, Bauwesen, Energie- und Antriebstechnik). Druckaufgestickte nichtrostende Austenite mit ca. 19 Gew.-% Mangan und 0,8 Gew.-% Stickstoff, sind als nickelfreie Variante seit einigen Jahren großtechnisch auf dem Markt verfügbar. In diesen Stählen wird die austenitische Matrix ohne die Legierungszugabe von Nickel sichergestellt, während gleichzeitig die korrosive Beständigkeit und die mechanischen Eigenschaften verbessert werden. Wie bei allen nichtrostenden Stählen beeinflussen die chemische Zusammensetzung und die Wärmebehandlung entscheidend das Gefüge und die Eigenschaften. Durch Lösungsglühen, Abschrecken und gezieltes Kaltverfestigen können bei diesen Stählen hervorragende mechanische Kennwerte erreicht werden (Rm von 900 MPa bis 2.000 MPa, A5 > 50 %, Av > 350 J). In der Regel dient das Lösungsglühen der Beseitigung unerwünschter Ausscheidungsphasen (Cr2N, M23C6 und Sigma-Phase) und der homogenen Verteilung der Legierungselemente im Austenit, was auch die Voraussetzung für eine hohe Korrosionsbeständigkeit darstellt. Wird die homogene Verteilung der Legierungselemente (Cr, Mo und N) durch suboptimale Wärmebehandlungs-, Verarbeitungs- oder Einsatzbedingungen beeinträchtigt, kann die korrosive Beständigkeit nicht auf Dauer gewährleistet werden. Daher ist die genaue Kenntnis vom Sensibilisierungsverhalten dieser hochstickstofflegierten Stähle unerlässlich. Am stickstofflegierten Werkstoff 1.4456 (X8CrMnMoN18-18-2) wird das Sensibilisierungsverhalten am lösungsgeglühten Zustand durch die gezielte Variation der Warmauslagerungsparameter untersucht. Dabei wird im Temperaturbereich von 500 °C bis 900 °C die Glühdauer systematisch variiert, um zu ermitteln, wann Ausscheidungen im Gefüge auftreten und ob diese die Korrosionsbeständigkeit beeinträchtigen. Die verschiedenen Sensibilisierungszustände werden mit dem EPR Verfahren, der KorroPad-Prüfung und dem REM vergleichend untersucht. Zur besseren Interpretation der experimentellen Ergebnisse werden auch thermodynamische Berechnungen genutzt, welche die Existenzbereiche der verschiedenen Ausscheidungsphasen vorhersagen. Damit kann die Veränderung der Korrosionsbeständigkeit mit dem Auftreten der verschiedenen Phasen korreliert und die Anwendbarkeit der experimentellen Methoden für stickstofflegierte Stähle nachgewiesen werden. T2 - 16. Sommerkurs Werkstoffe und Fügen CY - Magdeburg, Germany DA - 08.09.2017 KW - Nichtrostender Stahl KW - Wärmebehandlung KW - Korrosion KW - Stickstoff KW - EPR KW - KorroPad KW - ThermoCalc PY - 2017 SN - 978-3-944722-58-0 DO - https://doi.org/10.24352/UB.OVGU-2017-75 SP - 79 EP - 86 AN - OPUS4-41890 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kauss, N. A1 - Halle, T. A1 - Rosemann, Paul T1 - Alterungsverhalten vom kupferaushärtenden martensitisch nichtrostenden Stahl 1.4542 N2 - Der nichtrostende, aushärtbare Stahl 1.4542 (X5CrNiCuNb16-4) wird aufgrund der guten mechanischen Eigenschaften und der hohen Korrosionsbeständigkeit in einer Vielzahl von technischen Anwendungen eingesetzt. Das Verhältnis zwischen den mechanischen Eigenschaften und der Korrosionsbeständigkeit wird durch eine gezielte Wärmebehandlung eingestellt. Härte und Festigkeit werden durch die Bildung von fein verteilten Kupferausscheidungen bei der Warmauslagerung erreicht. Werden dabei auch Chromkarbide gebildet, reduziert sich gleichzeitig die Korrosionsbeständigkeit. Um den Einfluss der Warmauslagerung auf die Eigenschaften zu charakterisieren, wurden verschiedene Alterungszustände erzeugt und vergleichend untersucht. Dabei wurde außerdem der Einfluss einer starken Kaltumformung auf das Alterungsverhalten und die Korrosionsbeständigkeit untersucht. Zur Charakterisierung der Veränderungen wurden die Gefüge im REM untersucht und der magnetisierbare Anteil sowie die Vickershärte ermittelt. Zum Nachweis korrosionsanfälliger Zustände wurde die elektrochemisch potentiodynamische Reaktivierung (EPR) genutzt. Die Ergebnisse zeigen, dass die Kaltverfestigung die Ausscheidungskinetik beschleunigt und die Korrosionsbeständigkeit durch die Warmauslagerung bei 600 °C deutlich reduziert wird. T2 - 16. Sommerkurs Werkstoffe und Fügen CY - Magdeburg, Germany DA - 08.09.2017 KW - Nichtrostender Stahl KW - Wärmebehandlung KW - Korrosion KW - EPR KW - Kaltverfestigung PY - 2017 SN - 978-3-944722-58-0 DO - https://doi.org/10.24352/UB.OVGU-2017-75 SP - 87 EP - 94 AN - OPUS4-41891 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dieck, S. A1 - Ecke, M. A1 - Rosemann, Paul A1 - Halle, T. T1 - Verbesserung der Eigenschaften vom martensitischen, nichtrostenden Stahl X46Cr13 durch Q&P-Wärmebehandlung N2 - Das innovative Wärmebehandlungskonzept des „Quenching and Partitioning“ (Q&P) ermöglicht die Herstellung hochfester, martensitischer Stähle mit hoher Verformbarkeit und Duktilität. Dabei wird Restaustenit im Prozessabschnitt des Partitionierens durch Kohlenstoffdiffusion stabilisiert. Dies ermöglicht die dehnungsinduzierte Phasenumwandlung von Austenit in Martensit und erhöht die Verformbarkeit, ohne dabei die Festigkeit zu reduzieren. Bisher wenig erforscht ist die Anwendung des Q&P-Prozesses bei korrosionsbeständigen Stählen. Die vorliegende Arbeit ergänzt erste Untersuchungen von YUANG und RAABE um wichtige werkstofftechnische Kennwerte sowie um die erreichbare Korrosionsbeständigkeit. Es konnte gezeigt werden, dass im Vergleich zur standardmäßig angewandten Wärmebehandlung die mechanischen und korrosiven Eigenschaften enorm durch den Q&P-Prozess gesteigert werden. T2 - Sommerkurs Werkstoffe und Fügen am Institut für Werkstoff- und Fügetechnik CY - Magdeburg, Germany DA - 08.09.2017 KW - Martensitischer nichtrostender Stahl KW - Wärmebehandlung KW - Q+P KW - Korrosion KW - KorroPad PY - 2017 SN - 978-3-944722-58-0 DO - https://doi.org/10.24352/UB.OVGU-2017-75 SP - 95 EP - 104 AN - OPUS4-41892 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heyn, A. A1 - Rosemann, Paul A1 - Babutzka, Martin A1 - Bender, S. T1 - Elektrochemisches Rauschen von unlegiertem Stahl in wasserbasierten Bindemittel-Pigment-Gemischen N2 - Die Entwicklung von Beschichtungen für den Korrosionsschutz ist ein aufwändiger Prozess mit einer Vielzahl von oftmals langwierigen Untersuchungen und Prüfungen der Schutzeigenschaften. Elektrochemische Methoden unterstützen die Entwicklungsprozesse in hohem Maße und helfen beim Verstehen von Wirk- und Schadensmechanismen. Sie werden meistens an fertig formulierten und applizierten Beschichtungssystemen vorgenommen. Es wird eine Untersuchungsmöglichkeit vorgestellt, bei der sich wasserbasierte Beschichtungsstoffe in unterschiedlichen Formulierungsvarianten bereits im flüssigen Zustand mit Hilfe des elektrochemischen Rauschens charakterisieren lassen. Damit ist es möglich, bereits in einer sehr frühen Phase der Formulierungsentwicklung die Auswahl von Bindemitteln, Pigmenten und weiteren Zusatzstoffen entscheidend zu unterstützen und effizienter zu gestalten. Am Beispiel der Entwicklung von zinkfreien Korrosionsschutzpigmenten für wasserbasierte Beschichtungen wird gezeigt, dass ein einzigartiger Einblick in die dynamischen Prozesse bei Kontakt eines Metalls mit der wässrigen Beschichtungsdispersion möglich ist und wie dies mit der Performance der Beschichtungen korreliert. T2 - 16. Sommerkurs Werkstoffe und Fügen CY - Magdeburg, Germany DA - 08.09.2017 KW - Beschichtung KW - Korrosion KW - Elektrochemisches Rauschen KW - Korrosionsschutzpigmente KW - Korrosionsschutz PY - 2017 SN - 978-3-944722-58-0 DO - https://doi.org/10.24352/UB.OVGU-2017-75 SP - 139 EP - 148 AN - OPUS4-41893 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Babutzka, Martin A1 - Burkert, Andreas A1 - Heyn, A. T1 - Korrosionsuntersuchungen mit gelartigen Elektrolyten zur Beschreibung der Korrosionsschutzwirkung von Zinküberzügen N2 - Ein neuer Ansatz bei elektrochemischen Korrosionsuntersuchungen kann durch den Einsatz von gelartigen Elektrolyten als Alternative zu wässrigen Prüfelektrolyten beschritten werden. Gelartige Elektrolyte ermöglichen minimalinvasive Untersuchungen an natürlich gebildeten Zinkdeckschichten. Dadurch können korrosionsrelevante Kennwerte ermittelt werden, die Aussagen zur Deckschichtbildung und zur Stabilität der gebildeten Deckschichten erlauben. In diesem Beitrag wird anhand verschiedener Deckschichtzustände an Zink der Mehrwert von gelartigen Elektrolyten für die Korrosionsforschung verdeutlicht. T2 - 16. Sommerkurs Werkstoffe und Fügen am Institut für Werkstoff- und Fügetechnik CY - Magdeburg, Germany DA - 08.09.2017 KW - Deckschichtbildung KW - Gelartige Elektrolyte KW - Korrosionsprüfung KW - Zinkdeckschichten KW - Corrosion testing KW - Gel-type electrolytes KW - Layer formation KW - Zinc coatings PY - 2017 SN - 978-3-944722-58-0 DO - https://doi.org/10.24352/UB.OVGU-2017-75 SP - 119 EP - 127 AN - OPUS4-41898 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Le, Quynh Hoa A1 - Bäßler, Ralph A1 - Yevtushenko, Oleksandra A1 - Kratzig, Andreas A1 - Bettge, Dirk T1 - Synergistic effects of impurities in the condensate on the corrosion of CO2 transport pipeline N2 - For the reliability of transport pipelines the corrosion resistance of the materials used needs to be determined in conditions, which are possible during the transport process. In some situations condensation of components out of the CO2 stream can occur. To study the effect of condensate on transport pipeline steel, a “worst-case scenario” gas mixture, containing 2.5 % H2O, 1.8 % O2, 1000 ppmv NO2, and 220 ppmv SO2, was proposed, fed (1.5 L/min) into a glass reactor containing coupon-shaped specimens for 120 600 h at 278 K (to simulate the underground pipeline transport), and resulted in the condensate containing 0.114 M H2SO4 and 0.0184 M HNO3 (pH 2.13). Basing on this “original” condensate, exposure tests and electrochemical characterization together with pH and conductivity in CO2 saturated condition at the same temperature were carried out. The role of each gas impurity and the combination of them, when the condensate is formed, was studied by investigating the role of individual and varying combination of acidic components in the condensate on the corrosion behaviors of the commercial pipeline-steel (L360NB). It can be concluded that although the condensation of NOx in form of HNO3 causes faster corrosion rate, it is the condensation of SOx or the combination of SOx and NOx that may cause much more severe problems in form of localized and pitting corrosions. Different to the corrosion products formed in CO2 atmosphere without impurities (mainly iron carbonate) the corrosion products resulted from these acidic condensation have no protectability, indicating the need of controlling gas quality during the transportation within the pipeline network. T2 - EUROCORR 2017 - PRAG CY - Prague, Czech Republic DA - 03.09.2017 KW - CCUS KW - CO2 corrosion KW - Carbon steels KW - Condensate PY - 2017 SP - Paper 75636,.1 EP - 4 AN - OPUS4-41874 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Kranzmann, Axel T1 - Borehole integrity of austenitized and annealed pipe steels suitable for carbon capture and storage (CCS) N2 - Properties of pipe steels for CCS (carbon capture and storage) technology require resistance against the corrosive environment of a potential CCS-site (heat, pressure, salinity of the aquifer, CO2-partial pressure). The influence of austenitzing in heat treatment routines of two different injection pipe steels (1.4034, X46Cr13 and 1.4021, X20Cr13) was evaluated. Steel coupons were austenitized at different temperatures (900- 1050 °C) for different lengths of time (30-90 min) before quenching and annealing prior to long term corrosion experiments (60°C, 100 bar, artificial brine close to a CCS-site in the Northern German Basin, Germany). In general, fewer pits are found on X46Cr13. Comparing steels with 13% chromium each the higher carbon content of X46Cr13 (0.46% C) results in a lower number of pits compared to X20Cr13 (0.20% C). It is found that neither the carbon content of the steels nor austenitizing temperature has much influence, but local corrosion behaviour is most susceptible towards austenitzing time. T2 - International Conference on Future Environment and Energy CY - Pattaya, Thailand DA - 23.01.2016 KW - Corrosion KW - CCS KW - Carbon storage KW - Aquifer KW - Austenitizing PY - 2017 SP - Article A0005, 213 EP - 219 AN - OPUS4-41854 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wäsche, Rolf A1 - Ehrke, Roman A1 - Woydt, Mathias T1 - Wear of alpha-alumina in hot steam up to 300°C N2 - Selfmated alpha-alumina sliding couples have been investigated under oscillating sliding at 100 N load in different humidity conditions in air as in hot steam up to temperatures of 300°C and ambient pressures up to 4 bar. T2 - 7th International Conference on Mechanics and Materials in Design CY - Albufeira, Portugal DA - 11.06.2017 KW - Apha-alumina KW - Wear KW - Steam KW - Temperature KW - Abrasion PY - 2017 SN - 978-989-98832-6-0 SP - 265 EP - 266 PB - LusoImpress S.A. CY - Avintes, Portugal AN - OPUS4-41128 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koegler, M. T1 - Time-gated Raman spectroscopy and SERS as advanced technologies in bioprocess monitoring N2 - Raman spectroscopy is becoming a powerful process analytical technology (PAT) tool. Until now Raman technology has not shown its full potential in bioprocess on-line monitoring due to several technical challenges. Because of only small? interference from water molecules, Raman-spectroscopy is in contrast to IR spectroscopy able to follow changes of metabolite concentrations in dilute aqueous solutions. Results from common CCD-based process Raman-spectrometers reveal only barely identifiable peaks with a dominating (fluorescence) background. To solve this, Raman spectroscopy needs: (A) an enhancement to increase the limit of detection (LOD), and (B) a reliable method to distinguish the Raman signal from the sample-related auto-fluorescence. SERS (surface enhanced Raman spectroscopy) acts as an optical "nano-antenna"-effect. It causes a dipolar localized surface Plasmon resonance effect due to noble metallic nanoparticles or roughened metal and improves the limit of detection (LOD) significantly. Another new process-monitoring technique, which removes the fluorescence background in Raman-measurements is called time-gated Raman spectroscopy. It uses a picosecond pulsed Nd:YVO4-laser as emission source (exc= 532 nm) and a gated SPAD-array (Single Photon Avalanche Detector) detector instead of commonly used CCD (Charged Coupled Device)-detectors and CW (Continues Wave) laser emission. Time-Gate can measure the Raman-signal before the stronger fluorescence signal reaches the detector. In this study we utilized both SERS (Surface Enhanced Raman Spectroscopy) and time-gated Raman spectroscopy (TG-Raman) in combination on cell-free supernatant samples of an Escherichia coli cultivation with mineral salt media and a lactic acid bacteria fermentation with complex media. As a reference method for the estimation of amino acids and other metabolites, HPLC-RID and HPLC-FLD were used to evaluate the Raman-based detection. The quantitative evaluation of Raman data was performed by multivariate data analysis such as principal component analysis (PCA) and partial least squares regression (PLSR). For the first time, we can show that both qualitative and quantitative measurements are conducted successfully with both, SERS and time-gated Raman methods in industrially relevant media, so that a fast and reliable in situ or bypassed concentration measurement becomes feasible. T2 - 2. Photonics Finland, Optics and Photonics Days 2017 CY - Oulu, Finland DA - 29.05.2017 KW - Time-gate Raman KW - PAT KW - Chemometrics PY - 2017 UR - http://www.photonics.fi/event/opd17-optics-photonics-days-2017/ AN - OPUS4-41182 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF ED - Voigt, Gerrit T1 - Determining moisture in materials and IoT N2 - Knowing the state of the setting process of concrete in buildings or the moisture level of old walls can be crucial in determining further steps in the construction or restoration process. Small 2.4 GHz modules can be either embedded or applied on the surface to determine the moisture distribution in material. Common modules, that are based on the highly available Bluetooth Low Energy standard, emit electromagnetic waves, whose signal strength gets dampened by water molecules. This effect serves as the basis on determining the moisture level in material. We will show how to apply this method in a meshed sensor network for online monitoring. T2 - SMAR2017 CY - Zurich, Switzerland DA - 13.09.2017 KW - Moisture KW - Concrete KW - Radio signals KW - Bluetooth PY - 2017 SP - Paper 152, 1 EP - 6 CY - Zürich, Switzerland AN - OPUS4-41997 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schreier, Andy A1 - Jeschke, T. A1 - Petermann, K. A1 - Wosniok, Aleksander A1 - Krebber, Katerina T1 - Analytical model for mode-based insertion loss in ball-lensed coupling of graded-index silica and polymer fibres N2 - Analytical model for ball-lensed couplers to calculate the insertion loss for each optical mode. The basis for the calculation are commercial perfluorinated polymer optical (PFGI-POFs) and silica based fibres (SOFs). The modal power distribution for given misalignments are presented as well as the reflection-based losses at all optical interfaces. Additionally, the ball-lensed interconnection between PFGI-POF and SOF was theoretically demonstrated. T2 - POF 2017: 26th International Conference on Plastic Optical Fibres CY - Aveiro, Portugal DA - 13.09.2017 KW - Polymer optical fibre KW - Optical connector PY - 2017 VL - 2017 SP - 1 EP - 4 AN - OPUS4-41979 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübert, Thomas T1 - Gas Sensors for Hydrogen Safety N2 - Sensors are of increasing importance in connection with the development and expanded use of hydrogen gas as a source of energy and as a chemical reactant. The detecting principles of the main commercial available used seven sensor principles were presented. The characteristic parameters of the sensors, like detectable concentration range, sensitivity, selectivity and time response were compared. Testing and validation of sensor performance in relation to standards and application in explosive atmospheres are described. T2 - 3rd European Summer School on Hydrogen Safety CY - Belfast, UK DA - 2008-07-21 PY - 2008 SP - 1 EP - 32 AN - OPUS4-18577 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stark, Wolfgang T1 - Characterizing the flow-cure behaviour of thermoset plastics using thermoanalytical and ultrasonic methods N2 - The prospects of modern thermoanalytical methods for characterisation of flow, curing and final mechanical behaviour of moulding compounds were demonstrated. Using urea resin moulding compounds from different manufacturers the possibilities of the various techniques could be shown. With comparatively low effort, fundamental information can be gained before production process had been started. On this basis it is possible to make appropriate material selection at an early point in the process chain. On the basis of thermoanalytical data an incoming goods inspection can be established. Also it is easy to control the compliance with the conditions of delivery. In some cases it could also be helpful to have stored analysis data especially when problems appear in manufacturing process or unexpected part damages occur With the ultrasound measuring system it is possible to transfer the findings from the analytical methods directly to the processes in the mould. The application of ultrasound provides Dynamic Mechanical Analysis in the mould. Beside quality assurance ultrasound can also be used for process optimisation, especially for reduction of cycle time. In an advanced form ultrasound information can be used as a basis for improved machine control based on material state. The ultrasound measuring system developed by ISK Iserlohn and BAM can be obtained from the ISK. T2 - 5. Internationale Duroplasttagung / International Thermoset Conference CY - Iserlohn, Germany DA - 2008-11-20 KW - Differential Scanning Calorimetry KW - Dynamic Mechanical Analysis KW - Ultrasound KW - Urea rsin KW - Moulding compound KW - Incoming goods inspection KW - Process optimization PY - 2008 IS - Duro08_GB_08 SP - 1 EP - 8 AN - OPUS4-18586 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rücker, Werner A1 - Auersch, Lutz T1 - A user-friendly prediction tool for railway induced ground vibrations: Emission - transmission - immission T2 - 9th IWRN - International Workshop on Railway Noise CY - Munich, Germany DA - 2007-09-04 PY - 2007 SP - S.4.2, 1 EP - 6 PB - International Workshop on Railway Noise CY - München AN - OPUS4-18592 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Beck, Uwe A1 - Hertwig, Andreas A1 - Männ, Marion T1 - Ellipsometry and Standardization: Validation of Models - Key Issue for Reference Coatings and Non-ideal Samples N2 - Standardisation of ellipsometry is mainly based on three documents: pioneering work at NIST [1] on film standards, a publicly available specification and stan-dard testing procedure [2] for real-world samples by BAM and a standard specification for integrated metrology by SEMI [3]. Other activities refer to inter-laboratory comparisons for selected layer/substrate systems and analytical methods including ellipsometry [4] and the development of combined standards for thickness d and step height h [5]. Generally, precision of ellipsmetry in terms of raw data Ψ and Δ meets the major demands for all ellipsometric principles (RPE, RAE, PME, RCE, NE). As a result, fingerprint capabilty is al-most perfect for various layer/substrate systems. However, this is not true for accuracy in terms of physical quantities such as thickness d, optical (n, k) and dielectric constans (ε1, ε2,) as modelling is required. Hence, the layer/substrate and material dependent validation of models is nowadays a key issue. In contrast to the sub-nanometer sensi-tivity in vertical direction, the effective lateral resolution of almost all ellipso-metric principles except for imaging null ellipsometry is rather poor, usually be-yond 100 µm. Hence, nanometer-scaled homogeneity testing and the measurement of micro- and nanopatterned structures is not feasible by standard configurations. KW - Ellipsometry KW - Standardisation KW - Reference Coatings KW - Non-ideal samples KW - Validation of models PY - 2008 IS - 2 SP - 6 EP - 7 AN - OPUS4-18673 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Vollertsen, F. A1 - Grünenwald, S. A1 - Rethmeier, Michael A1 - Gumenyuk, Andrey A1 - Reisgen, U. A1 - Olschock, S. T1 - Welding thick steel plates with fibre lasers and GMAW N2 - The results of a collaborative research project on laser beam weldability of carbon steels of high sheet thickness are presented. That includes single and multiple pass welding of 16 mm and 20 mm thick plates, as well as the investigation of acceptable tolerances i.e. gap bridgeability and edge misalignment. For the welding experiments fibre lasers with 8 kW, 20 kW laser power and different MAG-techniques were used in various applications. With the 20 kW fibre laser 16 mm plates could be welded with a single pass, 20 mm required a seam preparation or alternatively preheating of the material. For multi pass welding with 8 kW laser power a joint preparation with a single V-butt joint with a broad root face (Ygroove) was applied. The root pass was always welded with a hybrid process, the filler passes with a hybrid process as well as a MAG process which produced the best results. T2 - 61th IIW Annual Assembly CY - Graz, Austria DA - 2008-07-06 KW - Hybrid Welding KW - Carbon Steels KW - Single pass welding KW - Multi pass welding PY - 2008 IS - IV-965-08 SP - 1 EP - 14 PB - International Institute of Welding CY - Paris AN - OPUS4-18678 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Helmerich, Rosemarie A1 - Wiggenhauser, Herbert T1 - Non-destructive testing of concrete structures T2 - 4th International Conference on Advances in Mechanical Engineering and Mechanics (ICAMEM2008) CY - Sousse, Tunisia DA - 2008-12-16 KW - Non-destructive testing KW - Civil engineering KW - Inspection KW - Knowledge transfer KW - Case study PY - 2008 SP - 1 EP - 10 AN - OPUS4-18655 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rett, S.R. A1 - Santana, D.M.V. A1 - Yanaguizawa, J. A. A1 - Shinohara, A.H. A1 - Tarpani, J.R. A1 - Zscherpel, Uwe A1 - Goebbels, Jürgen T1 - Computed radiography and microtomography of riveted lap joints of Glare™ subjected to constant amplitude loading (CAL) fatigue T2 - 17th World Conference on Non-Destructive Testing CY - Shanghai, China DA - 2008-10-25 KW - Computed Radiography KW - Computed Microtomography KW - Fiber-Metal Laminate KW - Fatigue Crack Propagation KW - Riveted Lap Joints PY - 2008 SP - 1 EP - 8 PB - International Committee for Non-Destructive Testing CY - Shanghai AN - OPUS4-18663 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mishra, Kirti Bhushan A1 - Wehrstedt, Klaus-Dieter A1 - Schönbucher, A. ED - K.N. Seetharamu, ED - T.R. Seetharam, ED - Pradeep G. Hedge, ED - H.M. Mallikarjuna, T1 - On the dynamics of organic peroxide pool flames T2 - 35th National Conference on Fluid Mechanics and Fluid Power CY - Bangalore, India DA - 2008-12-11 KW - Peroxide and kerosene pool flames KW - Froude number KW - CFD (Computational Fluid Dynamics) PY - 2008 IS - FMFP 08 - 076 SP - 643 EP - 650 CY - Bangalore, India AN - OPUS4-18690 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gründer, Klaus-Peter A1 - Kadoke, Daniel A1 - Müller, Karsten A1 - Musolff, André T1 - Characterization of shock absorber deformation by optical surface digitization N2 - The performance of shock absorbers has been tested in specific regulatory drop tests onto an un-yielding target at the BAM drop test facility. Optical surface digitization methods have been used to measure, analyze and evaluate permanent deformations of shock absorbers more systemati-cally. The measurement principle of the fringe projection technique used and its technical appli-cation to shock absorber research is explained in detail in this paper. Furthermore, examples of shock absorber testing results as well as final data visualization are presented. T2 - PATRAM 2007, 15th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Miami, Florida, USA DA - 2007-10-21 KW - 3D Verformung KW - Optische Digitalisierung KW - Behälterzulassung KW - Streifenprojektion KW - Fotogrammetrie PY - 2007 IS - Paper 84 SP - 1 EP - 6 PB - Institute of Nuclear Materials Management AN - OPUS4-18692 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Österle, Werner A1 - Müller, Urs A1 - Desplanques, Y. A1 - Bulthé, A.-L. A1 - Degallaix, G. A1 - Dmitriev, A.I. T1 - 3rd Body formation of two different brake pad materials designed for railway application T2 - 5th European Conference on Braking (JEF 2006) CY - Lille, France DA - 2006-11-08 PY - 2006 SP - 107 EP - 115 AN - OPUS4-18699 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hilbert, F. A1 - Kuschke, Christian A1 - Goedecke, Thomas A1 - Neumeyer, Tino T1 - Drop testing of the NCS 45 T2 - PATRAM 2007, 15th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Miami, Florida, USA DA - 2007-10-21 KW - Drop tests KW - Scale model PY - 2007 SP - 1 EP - 8 PB - Institute of Nuclear Materials Management AN - OPUS4-18644 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mix, Renate A1 - Friedrich, Jörg Florian T1 - Adhesion promotion in metal-polymer composites by introduction of functional groups arranged in a well-defined distance to the polymer surface by spacer incorporation T2 - 10th International Conference on the Science and Technology of Adhesion and Adhesives, Euradh 2008 - Adhesion `08 CY - Oxford, UK DA - 2008-09-03 KW - Adhesion KW - Aluminium KW - Polypropylene KW - Plasma polymers KW - Spacer-bonded functional groups PY - 2008 SP - 447 EP - 451 PB - IOM Communications CY - London AN - OPUS4-18616 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quercetti, Thomas A1 - Müller, Karsten A1 - Schubert, Sven T1 - Comparison of experimental results from drop testing of a spent fuel package design using a full-scale prototype model and a reduced-scale model T2 - PATRAM 2007, 15th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Miami, Florida, USA DA - 2007-10-21 KW - Drop KW - Testing KW - Experiment KW - Prototype KW - Reduced-scale KW - Full-scale PY - 2007 SP - 1 EP - 8 PB - Institute of Nuclear Materials Management AN - OPUS4-18624 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rolle, Annette A1 - Droste, Bernhard T1 - Safety during whole life time - An important aspect in safety assessment of sealed radioactive sources T2 - PATRAM 2007, 15th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Miami, Florida, USA DA - 2007-10-21 PY - 2007 IS - (Abstract # 53) SP - 1 EP - 7 PB - Institute of Nuclear Materials Management AN - OPUS4-18742 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard A1 - Müller, Karsten T1 - Test installations for the examination of CASTOR casks at the BAM test centre technical safety N2 - BAM as competent German government institute for the mechanical and thermal testing of radioactive material transport and storage containers, operates unique drop and fire test facilities for experimental investigations on an open-air Test Centre Technical Safety. To be able to perform even drop tests with full-scale spent fuel or HAW casks (i. e. the German CASTOR cask designs; “CASTOR” in the meantime in synonym for all other spent fuel cask designs) BAM constructed in 2004 a large drop test facility capable to handle 200 tons test objects, and to drop them onto a steel plate covered unyielding target with a mass of nearly 2600 tons. Drop testing of the 181 ton CONSTOR V/TC, the 127 ton MHI-MSF 69BG, a 1:2 scale model (CASTOR HAW TB2) and of cubic containers for radioactive waste disposal will briefly be presented. The experimental BAM drop testing activities can be supported also by drop testing of smaller packages (up to 2 tons) in an in-house test facility, and by dynamic, guided impact testing inside a new drop test machine. In May 2008 a new modern fire test facility was put into operation. The facility provides two test stands fired with liquid Propane. Testing in every case has to be completed by calculational investigations where BAM operates appropriate computer codes, e. g. ABAQUS, LS-Dyna, ANSYS and other analytical tools. T2 - 5th International Seminar on Radioactive Waste Products (RADWAP 2008) CY - Würzburg, Germany DA - 2008-10-27 KW - Drop tests KW - Fire tests KW - Finite element calculations KW - Radioactive waste packages KW - CASTOR casks KW - BAM test centre technical safety PY - 2008 SP - 1 EP - 8 AN - OPUS4-18781 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Österle, Werner A1 - Dmitriev, A.I. A1 - Urban, Ingrid ED - Jayashree Bijwe, T1 - Characterization of up to date brake friction materials T2 - IWAAFC-1, International Workshop on Advances in Asbestos free Friction Composites CY - Delhi, India DA - 2006-01-05 PY - 2006 SP - 21 EP - 35 CY - Delhi, India AN - OPUS4-18700 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Österle, Werner A1 - Dmitriev, A.I. A1 - Kloß, Heinz ED - Jayashree Bijwe, T1 - Basic considerations for the development of friction materials T2 - IWAAFC-2, International Workshop on Advances in Asbestos-free Friction Composites CY - Delhi, India DA - 2008-02-07 PY - 2008 SP - 24 EP - 51 PB - Indian Academy of Sciences CY - Delhi, India AN - OPUS4-18701 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Ostermann, Markus T1 - Wie viel Acrylamid ist in Knäckebrot und wie viel Schwefel in Benzin? N2 - Vier neue Referenzmaterialien zum chemischen Nachweis von Acrylamid in Knäckebrot, Schwefel in Benzin, von polyzyklischen aromatischen Kohlenwasserstoffen und von Legierungen in Akkus stellt die BAM vor. Diese Referenzmaterialien sind durch die BAM zertifiziert und durch das Europäische Referenzmaterialien Programm ERM auf den Markt gebracht. KW - ERM KW - Schwefel KW - Acrylamid KW - Europäische Referenzmaterialien PY - 2008 UR - http://www.chemie.de/news/80032 SP - 1 PB - CHEMIE.DE Information Service CY - Berlin AN - OPUS4-17391 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eberstein, Markus A1 - Glitzky, Carsten A1 - Gemeinert, Marion A1 - Rabe, Torsten A1 - Schiller, Wolfgang Arno A1 - Modes, C. T1 - Design of LTCC with high thermal expansion T2 - IMAPS/ACERS 4th International Conference and Exhibition on Ceramic Interconnect and Ceramic Microsystems Technologies (CICMT 2008) CY - Munich, Germany DA - 2008-04-21 KW - LTCC KW - Glass ceramic composites KW - Coefficient of thermal expansion CTE KW - Design PY - 2008 SP - 000120 EP - 000126 PB - IMAPS, International Microelectronics and Packaging Society CY - Washington, DC AN - OPUS4-17436 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wille, Frank A1 - Droste, Bernhard A1 - Koch, Frank A1 - Komann, Steffen T1 - Design assessment of spent fuel and HLW Transport Casks T2 - 49th INMM Annual Meeting, July 13-17, 2008 CY - Nashville, USA DA - 2008-07-13 KW - Safety Analysis KW - Transport Packages KW - Drop tests KW - Finite Element Analysis KW - Thermal Design KW - Containment KW - Quality Management PY - 2008 SP - 1 EP - 8 AN - OPUS4-17780 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schartel, Bernhard A1 - Braun, Ulrike T1 - Understanding Fire Retardancy Mechanisms in Composites: A Key for Future Development T2 - 5th International Conference on Composites In Fire (CIF5) CY - Newcastle upon Tyne, United Kingdom DA - 2008-07-10 KW - Fire retardancy KW - Composites KW - Flame Retardants KW - Phosphinate PY - 2008 SP - 01-1 - 01-10 CY - Newcastle upon Tyne, UK AN - OPUS4-17716 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fomin, P.A. A1 - chen, J.-R. A1 - Hieronymus, Hartmut T1 - Shock induced explosion of oxygen containing bubble in a flammable liquid: safety aspects of fuel condensation and evaporation T2 - 7th International Symposium on Hazards, Prevention, and Mitigation of Industrial Explosions (ISHPMIE) CY - St. Petersburg, Russia DA - 2008-07-07 KW - Detonation KW - Bubbles KW - Shock wave KW - Condensation PY - 2008 VL - III SP - 141 EP - 150 AN - OPUS4-18035 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Palymsky, I.B. A1 - Fomin, P.A. A1 - Hieronymus, Hartmut T1 - Rayleigh-Benard convection in gas with chemical reactions T2 - 7th International Symposium on Hazards, Prevention, and Mitigation of Industrial Explosions (ISHPMIE) CY - St. Petersburg, Russia DA - 2008-07-07 KW - Detonation KW - Surface detonation KW - Convection PY - 2008 VL - I SP - 131 EP - 138 AN - OPUS4-18036 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, B. A1 - Dahms, A. A1 - Bitter, F. A1 - Wargocki, P. A1 - Olesen, B. A1 - Knudsen, H.N. A1 - Afshari, A. A1 - Jann, Oliver A1 - Horn, Wolfgang A1 - Müller, D. A1 - Airaksinen, M. A1 - Järnström, H. A1 - Tirkkonen, T. A1 - Witterseh, T. T1 - Material labelling: Combined material emission tests and sensory evaluations T2 - Indoor Air 2008, 11th International Conference on Indoor Air Quality and Climate CY - Copenhagen, Denmark DA - 2008-08-17 KW - Material labelling KW - Emission test KW - Sensory evaluation KW - Odour intensity KW - Acceptability PY - 2008 IS - Paper 1066 SP - 1 EP - 8 AN - OPUS4-18047 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völzke, Holger A1 - Nieslony, Gregor A1 - Hagenow, Peter T1 - Approval of Existent Waste Packages and New Package Designs in Preparation for the KONRAD Repository - 8092 T2 - 34th Annual Waste Management Conference & Exhibition (WM2008) CY - Phoenix, Arizona, USA DA - 2008-02-24 KW - Behälter KW - Behälterprüfung KW - Endlager KW - Radioaktive Stoffe KW - Qualitätssicherung KW - Sicherheit PY - 2008 SP - 1 EP - 9 AN - OPUS4-17990 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Sturm, Christine T1 - Correlation between material parameters of high density polyethylene grades and the test performance behaviour of packagings T2 - EUROCORR 2008 CY - Edinburgh, Scotland, UK DA - 2008-09-07 KW - Dangerous goods packagings KW - HDPE grades KW - Material parameters KW - Design type tests PY - 2008 N1 - Serientitel: EFC-Event – Series title: EFC-Event IS - 299 SP - 1 EP - 12 PB - DECHEMA CY - Frankfurt am Main AN - OPUS4-17993 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Molnarne, Maria A1 - Schröder, Volkmar T1 - Chemical safety database - application for flammability limits of biogases N2 - The article addresses safety characteristics of hazardous substances, particularly biogas plants that require specific safety measures. KW - Explosion limit KW - Biogas KW - CHEMSAFE KW - Flammability limit KW - Explosion protection KW - Renewable energy PY - 2009 IS - Spring 2009 SP - 20 EP - 26 PB - Fire & safety group CY - Cedar Grove, NJ, USA AN - OPUS4-19614 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ballheimer, Viktor A1 - Koch, Frank A1 - Kuschke, Christian A1 - Droste, Bernhard T1 - Similarity aspects for closure systems in small scale package drop testing T2 - PATRAM 2007, 15th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Miami, Florida, USA DA - 2007-10-21 KW - Scale model KW - Closure system KW - Drop tests PY - 2007 SP - 1 EP - 8 PB - Institute of Nuclear Materials Management AN - OPUS4-19654 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Pittner, Andreas A1 - Weiss, D. A1 - Schwenk, Christopher A1 - Rethmeier, Michael T1 - Fast temperature field generation for welding simulation and reduction of experimental effort N2 - The quality of welding processes is governed by the occurring induced distortions yielding an increase in production costs due to necessary reworking. Especially for more complex specimens it is difficult to evaluate the optimal configuration of welding sequences in order to minimise the distortion. Even experienced welding operators can solve this task only by trial and error which is time and cost consuming. In modern engineering the application of welding simulation is already known to be able to analyse the heat effects of welding virtually. However, the welding process is governed by complex physical interactions. Thus, recent weld thermal models are based on many simplifications. The state of the art is to apply numerical methods in order to solve the transient heat conduction equation. Therefore, it is not possible to use the real process parameters as input for the mathematical model. The model parameters which allow calculating a temperature field that is in best agreement with the experiments cannot be defined directly but inversely by multiple simulations runs. In case of numerical simulation software based on finite discretisation schemes this approach is very time consuming and requires expert users. The weld thermal model contains an initial weakness which has to be adapted by finding an optimal set of model parameters. This process of calibration is often done against few experiments. The range of model validity is limited. An extension can be obtained by performing a calibration against multiple experiments. The focus of the paper is to show a combined modelling technique which provides an efficient solution of the inverse heat conduction problem mentioned above. On the one hand the inverse problem is solved by application of fast weld thermal models which are closed form solutions of the heat conduction equation. In addition, a global optimisation algorithm allows an automated calibration of the weld thermal model. This technique is able to provide a temperature field automatically that fits the experimental one with high accuracy within minutes on ordinary office computers. This fast paradigm permits confirming the application of welding simulation in an industrial environment as automotive industry. On the other hand, the initial model weakness is compensated by calibrating the model against multiple experiments. The unknown relationship between model and process parameters is approximated by a neural network. The validity of the model is increased successively and enables to decrease experimental effort. For a test case it is shown, that this approach yields accurate temperature fields within very short amount of time for unknown process parameters as input data to the model contributing to the requirement to construct a substitute system of the real welding process. KW - Welding simulation KW - Temperature field generation KW - Short calculation time KW - Multiple experiments KW - Inverse heat conduction problem KW - Neural networks PY - 2009 IS - SC-Auto-32-09 SP - 1 EP - 11 PB - International Institute of Welding CY - Paris AN - OPUS4-19744 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Liebner, Christian A1 - Silakova, M.A. A1 - Pasman, H.J. T1 - Towards a better control of hydrocarbon oxidation: A study of self-ignition phenomena at low temperature and at ambient and elevated pressure N2 - Enhancement of process safety and efficiency are the drivers in EU project SAFEKINEX investigating the mechanisms of hydrocarbon oxidation and explosion safety indices of the associated mixtures. The project produces a wealth of data on explosive behavior at elevated pressures and temperatures. This paper describes some of the self-ignition aspects. T2 - CHISA 2006 - 17th international congress of chemical and process engineering CY - Prague, Czech Republic DA - 2006-08-27 KW - Auto ignition KW - Safety characteristics KW - Hydrocarbon oxidation PY - 2009 SP - 1 EP - 5(?) AN - OPUS4-19746 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bartholmai, Matthias A1 - Köppe, Enrico ED - Urs Meier, ED - Bernadette Havranek, ED - Masoud Motavalli, T1 - Wireless sensor network for long-term structural health monitoring of buildings and infrastructures N2 - Damage commonly occurs in buildings when a component fails suddenly with a partial or total collapse as a consequence. This type of event leads to serious damage to property and if it is a bridge or a large hall, then people in particular are at risk. The often great age of bridges and the increasing volume of traffic (particularly heavy traffic) which they are expected to carry are in clear contradiction to each other. Thus the probability increases that the loadbearing capacity of a bridge decreases rapidly and often unnoticed with sometimes dire consequences. In order to prevent such accidents, the Federal Institute for Materials Research and Testing is currently developing a special radio-based, self-configuring measuring system in cooperation with the Berlin-based ScatterWeb Company. This measuring system consists of a number of identically designed sensor nodes which are self-sustaining, need no wiring, can act as both transmitters and receivers and are equipped with a special sensor technology making long-term monitoring of buildings or engineering facilities possible. The sensor unit uses strain gauges for stress analysis and contains interfaces for additional sensors. The system in particular applies to buildings and structures for transport and traffic and large-scale industrial facilities, where a subsequent wiring installation is difficult or impossible. T2 - 4th International conference on structural health monitoring of intelligent infrastructure CY - Zurich, Switzerland DA - 2009-07-22 KW - Funksensorik KW - Sensornetzwerk KW - Schadensfrüherkennung KW - Strukturüberwachung PY - 2009 IS - Paper 365 SP - 1 EP - 5 AN - OPUS4-19748 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard T1 - Zur Wirksamkeit von Wasserberieselungsvorrichtungen T2 - Zum Stand der Sicherheitstechnik bei der Flüssiggaslagerung CY - Wolfsburg, Deutschland DA - 1988-04-19 PY - 1988 SP - 1 EP - 4 PB - CongressPark CY - Wolfsburg AN - OPUS4-19753 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard T1 - Bleve in kunststoffverarbeitendem Betrieb T2 - Zum Stand der Sicherheitstechnik bei der Flüssiggaslagerung CY - Wolfsburg, Deutschland DA - 1988-04-19 PY - 1988 SP - 1 EP - 2 PB - CongressPark CY - Wolfsburg AN - OPUS4-19754 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard T1 - Safety evaluation of dry spent fuel storage casks T2 - Soviet-West German Seminar on Experience and Prospective Methods of Spent Fuel Storage and Transport CY - Leningrad, Soviet Union DA - 1988-06-27 PY - 1988 SP - 1 EP - 30 PB - All Union Scientific Research and Design Institute for Complex Energy Technologies - VNIPIET CY - Leningrad AN - OPUS4-19755 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard T1 - Die Wasserberieselung als Brandschutzmaßnahme für Flüssiggaslagertanks T2 - Fortbildungsprogramm "Immissionsschutz", Kurs 841 "Flüssiggaslagerung", Landesanstalt für Immissionsschutz des Landes Nordrhein-Westfalen CY - Essen, Deutschland DA - 1988-11-10 PY - 1988 SP - 1 EP - 5 PB - Landesanstalt für Immissionsschutz des Landes Nordrhein-Westfalen CY - Essen AN - OPUS4-19778 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard T1 - Die Wasserberieselung als Brandschutzmaßnahme für Flüssiggaslagertanks T2 - Fortbildungsprogramm "Immissionsschutz", Kurs 941 "Flüssiggaslagerung" CY - Essen, Deutschland DA - 1989-03-09 PY - 1989 SP - 1 EP - 5 PB - Landesanstalt für Immissionsschutz des Landes Nordrhein-Westfalen CY - Essen AN - OPUS4-19779 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard ED - Riede, R. ED - Wefers, H. T1 - Zur Wirksamkeit von Wasserberieselungsvorrichtungen T2 - Seminar Nr. S-70-401-091-9 "Flüssiggaslagerung" CY - Essen, Deutschland DA - 1989-04-05 PY - 1989 SP - 1 EP - 6 PB - Haus d. Technik CY - Essen AN - OPUS4-19780 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pretsch, Thorsten T1 - About the effects of hydrolytic aging on the mechanical and thermo-mechanical properties of a non-stabilized and a Stabaxol-stabilized shape memory polymer T2 - 28th Polymer degradation discussion group meeting CY - Sestri Levante, Italy DA - 2009-09-06 KW - Shape memory polymer KW - Thermo-mechanical properties KW - Active polymer KW - Stimuli-sensitive polymer KW - Poly(ester urethane) KW - Stabilizer KW - Ageing behaviour KW - Stabaxol PY - 2009 SP - 32 EP - 34 PB - Elsevier AN - OPUS4-19864 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - May, U. A1 - Lütkepohl, K. A1 - Bork, Claus-Peter T1 - Örtlich ertragbare Beanspruchungen bei Spannungskonzentrationen in Karosseriebauteilen aus hoch- und höherfesten Stählen KW - Höherfestes Stahlblech KW - Schwingfestigkeit KW - Karosserie KW - Spannungskonzentration KW - Ertragbare Beanspruchung KW - Örtliches Konzept PY - 2009 VL - 215 SP - 1 EP - 23, 72 Abb. CY - Frankfurt/M. AN - OPUS4-19785 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sterthaus, Jens A1 - Ballheimer, Viktor A1 - Droste, Bernhard A1 - Koch, Frank A1 - Probst, Ulrich A1 - Völzke, Holger A1 - Wille, Frank T1 - Analysis of bolted flange joints for lids of packages for radioactive materials T2 - ASME 2009 Pressure vessels and piping conference CY - Prague, Czech Republic DA - 2009-07-26 KW - Bolted flange joints KW - FEA KW - Modelling of gaskets KW - Assessment of leak tightness KW - Results from experiments PY - 2009 SP - PVP2009-77284, 1-8 PB - American Society of Mechanical Engineers CY - New York AN - OPUS4-19786 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krebber, Katerina A1 - Liehr, Sascha A1 - Lenke, Peter A1 - Wendt, Mario T1 - Distributed POF sensors for structural health monitoring - First practical applications and field tests results N2 - Distributed POF sensors based on OTDR have been developed for SHM purposes of geotechnical and masonry structures. The first field tests conducted at a creeping slope and a brick building have proved the functionality of the sensors. T2 - POF 2009 - 18th International conference on plastic optical fibers CY - Sydney, Australia DA - 2009-09-07 PY - 2009 IS - Session 1 (S1_25) SP - 1 EP - 6 CY - Sydney, Australia AN - OPUS4-19914 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schukar, Marcus A1 - Grzemba, Birthe A1 - Krebber, Katerina A1 - Luber, M. T1 - Integration technology of POF sensors into composites for structural health monitoring N2 - We have investigated the application technology of polymer optical fibers (POF) as sensors integrated into respectively applied onto composites for structural health monitoring by using different manufacturing methods and several types of POF. T2 - POF 2009 - 18th International conference on plastic optical fibers CY - Sydney, Australia DA - 2009-09-07 KW - Optische Polymerfasern (POF) KW - Fasersensorik KW - Structural Health Monitoring KW - Faserverbundwerkstoffe KW - OTDR KW - Faser-Integration PY - 2009 IS - Session 1 (S1_25) SP - 1 EP - 4 CY - Sydney, Australia AN - OPUS4-19915 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Poisel, H. A1 - Luber, M. A1 - Ziemann, O. A1 - Diez, J. A1 - Bloos, M. A1 - Bachmann, A. A1 - Schukar, Marcus T1 - Applications of a POF elongation sensor N2 - The principle of a low-cost but nevertheless powerful POF elongation sensor has already been described in the recent years [1, 2, 3]. The measurement of the phase shift of a signal of a modulated light source which is coupled into two different POF, one being stretched, yields information of the elongation with a resolution of up to 10-5. Analyzing the temporal or frequency behaviour of the signal gives additional information. Since the phase measurement can allow for frequencies up to 2 GHz, the vibrational analysis of macroscopic structures can be extended to several kHz very easily, limited mainly by the signal processing electronics. Thus we processed data of a sensing system applied to a 39 m rotor blade of a wind power generator and could resolve the various frequencies related to different exciting conditions, e.g. the appearance of a beat signal when the blade was externally excited by a mechanical system with a frequency close but not identical to the Eigen frequency of the blade. T2 - POF 2009 - 18th International conference on plastic optical fibers CY - Sydney, Australia DA - 2009-09-07 KW - Optische Polymerfasern (POF) KW - Fasersensorik KW - Structural health monitoring KW - Faserverbundwerkstoffe KW - Phasenmesstechnik KW - Faser-Integration PY - 2009 IS - Session 1 (S1_25) SP - 1 EP - 5 CY - Sydney, Australia AN - OPUS4-19917 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schön, W. A1 - Probst, Ulrich A1 - Droste, Bernhard T1 - Experimental investigations of fire protection measures for LPG storage tanks T2 - 6th international symposium on loss prevention and safety promotion in the process industries CY - Oslo, Norway DA - 1989-06-19 PY - 1989 VL - 4 SP - 51/1 EP - 51/17 PB - European Federation of Chemical Engineering CY - Oslo AN - OPUS4-19876 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard A1 - Mallon, Michael T1 - A statistical review of the reasons leading to LPG accidents T2 - 6th international symposium on loss prevention and safety promotion in the process industries CY - Oslo, Norway DA - 1989-06-19 PY - 1989 VL - 2 SP - 79/1 EP - 79/25 PB - European Federation of Chemical Engineering CY - Oslo AN - OPUS4-19879 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hertel, Horst T1 - Anfälligkeit von Holz nach unterschiedlicher Vorbehandlung gegenüber dem Hausbockkäfer T2 - 26. Holzschutztagung 2010 CY - Göttingen, Deutschland DA - 2010-04-22 KW - Verhalten KW - Holzwahl KW - Holzqualität KW - Laborverfahren PY - 2010 SP - 1 EP - 11(?) CY - Göttingen AN - OPUS4-21369 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hertel, Horst T1 - DIN 68800-3, Vorbeugender Schutz von Holz mit Holzschutzmitteln T2 - 26. Holzschutztagung 2010 CY - Göttingen, Deutschland DA - 2010-04-22 KW - DIN KW - Holzschutz KW - Biozide KW - Holzschutzmittel PY - 2010 SP - 1 EP - 5(?) CY - Göttingen AN - OPUS4-21370 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burkert, Andreas A1 - Fischer, Joachim A1 - Zietelmann, Christina A1 - Lehmann, Jens T1 - Erhaltung des Korrosionsschutzes - Wie viel Pflege braucht der Stahl? KW - Nichtrostender Stahl KW - Reinigung KW - Pflege KW - Desinfektion KW - Korrosionsbeständigkeit PY - 2010 VL - 3 SP - 14 EP - 19 PB - Schweizerischer Verein für Schweisstechnik CY - Basel AN - OPUS4-21353 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Griesche, Axel A1 - Engelhardt, M. A1 - Kargl, F. A1 - Meyer, A. A1 - Weis, H. A1 - Yang, F. T1 - Diffusion measurements with neutron radiography KW - Diffusion KW - Metal KW - Semiconductor KW - Melt KW - In-situ KW - Radiography KW - Darken KW - Capillary PY - 2009 IS - Chapter 4.1.5 SP - 214 EP - 215 AN - OPUS4-21449 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niederleithinger, Ernst A1 - Shokouhi, Parisa A1 - Stähler, S. A1 - Nowak, Thomas Rudolf T1 - Detection of subtle changes in materials by Coda Wave interferometry T2 - 10th European conference on non-destructive testing CY - Moscow, Russia DA - 2010-06-07 KW - Cold wave interferometry KW - Beton KW - Concrete KW - Stress PY - 2010 IS - Paper 4.02.18 SP - 1 EP - 9 AN - OPUS4-21468 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sokolowski-Tinten, K. A1 - Barty, A. A1 - Boutet, S. A1 - Shymanovich, U. A1 - Bogan, M. A1 - Marchesini, S. A1 - Hau-Riege, S. A1 - Stojanovic, N. A1 - Bonse, Jörn A1 - Tobey, R. A1 - Ehrke, H. A1 - Cavalleri, A. A1 - Duesterer, S. A1 - Frank, M. A1 - Bajt, S. A1 - Schulz, J. A1 - Seibert, M. A1 - Hajdu, J. A1 - Treusch, R. A1 - Chapman, H. T1 - Short-pulse laser induced transient structure formation and ablation studied with time-resolved coherent XUV-scattering N2 - XUV- and X-ray free-electron-lasers (FEL) combine short wavelength, ultrashort pulse duration, spatial coherence and high intensity. This unique combination of properties opens up new possibilities to study the dynamics of non-reversible phenomena with ultrafast temporal and nano- to atomic-scale spatial resolution. In this contribution we wish to present results of time-resolved experiments performed at the XUV-FEL FLASH (HASYLAB/Hamburg) aimed to investigate the nano-scale structural dynamics of laser-irradiated materials. Thin films and fabricated nano-structures, deposited on Si3N4-membranes, have been excited with ultrashort optical laser pulses. The dynamics of the non-reversible structural evolution of the irradiated samples during laser-induced melting and ablation has been studied in an optical pump - XUV-probe configuration by means of single-shot coherent scattering techniques (i.e. diffraction imaging [1]). In a first set of experiments we investigated the formation of laser induced periodic surface structures (LIPSS) on the surface of thin Si-films (thickness 100 nm). In a simplified view LIPPS are generated as a result of interference between the incident laser pulse and surface scattered waves which leads to a periodically modulated energy deposition. Time-resolved scattering using femtosecond XUV-pulses (with a wavelength of 13.5 nm and 7 nm) allowed us to directly follow LIPSS evolution on an ultrafast time-scale and with better than 40 nm spatial resolution. The observed scattering patterns show almost quantitative agreement with theoretical predictions [2] and reveal that the LIPSS start to form already during the 12 ps pump pulse. In the second set of measurements we studied picosecond and femtosecond laser induced ablation and disintegration of fabricated nano-structures. Correlations of coherent diffraction patterns measured at various time delays to the pattern of the undisturbed object show that order in the structure is progressively lost starting from short length scales. This structural rearrangement progresses at close to the speed of sound in the material. Under certain circumstances (e.g. adequate sampling) it became also possible to reconstruct real-space images of the object as it evolves over time [3]. The possibility of femtosecond single-shot imaging of ultrafast dynamic processes with nanoscale resolution provides yet more details of the physical processes involved. [1] H. N. Chapman et al. Nature Phys. 2, 839 (2006). [2] J. F. Young et al., Phys. Rev. B 27, 1155 (1983). [3] A. Barty et al. Nature Phot. 2, 415 (2008). T2 - Fall meeting of the materials research society 2009 CY - Boston, MA, USA DA - 2009-11-30 KW - Femtosecond laser ablation KW - Laser-induced periodic surface structures KW - Time-resolved coherent XUV scattering KW - Semiconductor KW - Silicon PY - 2010 DO - https://doi.org/10.1557/PROC-1230-MM05-03 N1 - Serientitel: Materials Research Society symposium proceedings – Series title: Materials Research Society symposium proceedings VL - 1230E IS - Paper 1230-MM05-03 SP - 1 EP - 6 AN - OPUS4-21438 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bücker, Michael T1 - Kombinierte Behandlung von Holz mit Nanopartikeln T2 - 26. Holzschutz-Tagung CY - Göttingen, Deutschland DA - 2010-04-22 KW - Holzmodifikation KW - Kieselsol KW - Silane KW - Tränkung und Beschichtung KW - Holzfenster PY - 2010 SP - 137 EP - 144 AN - OPUS4-21453 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard A1 - Völzke, Holger T1 - Prüfungen an Zwischenlagerbehältern zur Belastbarkeit bei Einwirkungen von innen und aussen T2 - Zwischenlager-Workshop CY - Jülich, Deutschland DA - 2001-01-23 PY - 2001 SP - 177 EP - 221 CY - Jülich AN - OPUS4-21569 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schlichting, Joachim A1 - Kervalishvili, Guram N. A1 - Maierhofer, Christiane A1 - Kreutzbruck, Marc T1 - Charakterisierung von Rissen mittels Laser angeregter aktiver Thermografie T2 - Thermographie-Kolloquium 2009 CY - Stuttgart, Germany DA - 2009-10-08 PY - 2009 IS - Vortrag 19 SP - 1 EP - 7 CY - Berlin AN - OPUS4-21571 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Quercetti, Thomas A1 - Wieser, Günter A1 - Völzke, Holger A1 - Droste, Bernhard ED - Droste, B. ED - Kowalewsky, H. T1 - Mechanical impact assessment of cubic waste containers depending on target construction T2 - PATRAM 98 - 12th International conference on the packaging and transportation of radioactive materials CY - Paris, France DA - 1998-05-10 PY - 1998 VL - 3 SP - 1152 EP - 1159 PB - Nuclear Technology Publishing CY - Paris, France AN - OPUS4-21556 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wieser, Günter A1 - Droste, Bernhard A1 - Martens, B.-R. A1 - Probst, Ulrich A1 - Schreiber, D. A1 - Völzke, Holger ED - Droste, B. ED - Kowalewsky, H. T1 - Thermal test of a cubic ductile cast iron container filled with an ion exchanger resin T2 - PATRAM 98 - 12th International conference on the packaging and transportation of radioactive materials CY - Paris, France DA - 1998-05-10 PY - 1998 VL - 1 SP - 429 EP - 435 PB - Nuclear Technology Publishing CY - Paris, France AN - OPUS4-21560 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kowalewsky, Helmut A1 - Droste, Bernhard A1 - Neumeyer, Tino A1 - Burnay, S.G. A1 - Ball, M. H. A1 - Morton, D.A.V. A1 - Smith, P.N. A1 - Tuson, A.T. ED - Droste, B. ED - Kowalewsky, H. T1 - Safety assessment of leaktightness criteria for radioactive materials transport packages T2 - PATRAM 98 - 12th International conference on the packaging and transportation of radioactive materials CY - Paris, France DA - 1998-05-10 PY - 1998 VL - 2 SP - 543 EP - 550 PB - Nuclear Technology Publishing CY - Paris, France AN - OPUS4-21599 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gogolin, B. A1 - Droste, Bernhard ED - Droste, B. ED - Kowalewsky, H. T1 - Casks for transportation and storage of radioactive materials as multi mass systems - additional stresses caused by kinematic effects T2 - PATRAM 98 - 12th International conference on the packaging and transportation of radioactive materials CY - Paris, France DA - 1998-05-10 PY - 1998 VL - 3 SP - 1137 EP - 1143 PB - Nuclear Technology Publishing CY - Paris, France AN - OPUS4-21601 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Liehr, Sascha A1 - Krebber, Katerina T1 - A novel technique for quasi-distributed and dynamic length change measurement in optical fibers N2 - We present a novel technique to measure length changes between multiple reflection points in optical fibers. The technique allows for dynamic measurement up to 1kHz and a resolution better than 1µm. T2 - International conference "Optical sensors" CY - Karlsruhe, Germany DA - 2010-06-21 PY - 2010 DO - https://doi.org/10.1364/SENSORS.2010.STuB5 IS - STuB5 SP - 1 EP - 2 AN - OPUS4-21626 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völzke, Holger A1 - Wieser, Günter A1 - Zencker, Uwe A1 - Droste, Bernhard T1 - Mechanical and thermal safety analyses and demonstrations for cubic DCI - multi-purpose containers T2 - 4th International conference on transportation for the nuclear industry CY - Bournemouth, Dorset, UK DA - 1997-05-13 PY - 1997 IS - Session 2, Paper 5 SP - 1 EP - 13 AN - OPUS4-21665 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Völzke, Holger A1 - Droste, Bernhard T1 - Entwicklung von Beurteilungsmethoden für Transport- und Lagerbehälter mit erhöhten metallischen Reststoffanteilen - Weiterführende Untersuchungen (EBER II) T2 - VI. Stilllegungskolloquium Hannover und 5. Statusbericht "Stilllegung und Rückbau kerntechnischer Anlagen" CY - Hannover, Deutschland DA - 2000-04-13 PY - 2000 SP - 315 EP - 326 AN - OPUS4-21591 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard T1 - Prüfungen im verkehrsrechtlichen Zulassungsverfahren von Transportbehältern T2 - 1. Symposium - Beförderung radioaktiver Stoffe CY - Hannover, Deutschland DA - 1999-11-18 PY - 1999 SP - 1 EP - 16(?) CY - Hannover AN - OPUS4-21592 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard A1 - Ballheimer, Viktor A1 - Zeisler, Peter A1 - Tso, C.F. A1 - Donelan, P. A1 - Hüggenberg, R. ED - Droste, B. ED - Kowalewsky, H. T1 - Evaluation of safety of casks impacting different types of targets T2 - PATRAM 98 - 12th International conference on the packaging and transportation of radioactive materials CY - Paris, France DA - 1998-05-10 PY - 1998 VL - 3 SP - 1343 EP - 1351 PB - Nuclear Technology Publishing CY - Paris, France AN - OPUS4-21658 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Völzke, Holger A1 - Droste, Bernhard T1 - Entwicklung von Beurteilungsmethoden für Transport- und Lagerbehälter mit erhöhten metallischen Reststoffanteilen (EBER) - FEM-Berechnungen zum Aufprall kubischer Gußcontainer T2 - V. Stilllegungskolloquium Hannover und 4. Statusbericht "Stilllegung und Rückbau kerntechnischer Anlagen" CY - Hannover, Deutschland DA - 1997-06-24 PY - 1997 SP - 264 EP - 275 AN - OPUS4-21659 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard A1 - Völzke, Holger T1 - EBER - Entwicklung von Beurteilungsmethoden für Transport- und Lagerbehälter mit erhöhten metallischen Reststoffanteilen T2 - IV. Stilllegungskolloquium Hannover und 3. Statusbericht "Stilllegung und Rückbau kerntechnischer Anlagen" CY - Bad Dürkheim, Deutschland DA - 1995-11-08 PY - 1995 SP - 425 EP - 435 AN - OPUS4-21640 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Völzke, Holger A1 - Zencker, Uwe A1 - Wieser, Günter A1 - Droste, Bernhard T1 - Testing and licensing of radioactive waste containers for disposal in Germany T2 - DisTec `98 - International conference on radioactive waste disposal CY - Hamburg, Germany DA - 1998-09-09 PY - 1998 VL - 2 SP - 431 EP - 436 PB - KONTEC CY - Hamburg AN - OPUS4-21608 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT ED - Droste, Bernhard ED - Gebauer, K.-P. ED - Mallon, Michael ED - Schön, W. ED - Schrödter, W. T1 - Zusammenfassender Abschlussbericht PY - 1988 VL - Fachband 1 IS - Bericht 01501 SP - 1 EP - 75 CY - Berlin AN - OPUS4-21737 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Probst, Ulrich A1 - Droste, Bernhard T1 - Untersuchung von Brandschutzmassnahmen - Instrumentierte Brandversuche an 4850 l-Flüssiggas-Lagertanks mit Wärmeschutz-Isolierung und zwei Sicherheitsventilen im Heizölfeuer PY - 1988 VL - Fachband 5.2 IS - Bericht 01501 SP - 1 EP - 92 CY - Berlin AN - OPUS4-21738 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dreisvogt, H. A1 - Droste, Bernhard A1 - Völzke, Holger A1 - Probst, Ulrich T1 - Dry interim spent fuel storage casks - Licensing, evaluation and operational experience T2 - International symposium on safety and engineering aspects of spent fuel storage CY - Vienna, Austria DA - 1994-10-10 PY - 1995 IS - IAEA-SM-335/35 SP - 355 EP - 368 CY - Vienna, Austria AN - OPUS4-21728 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Schrödter, Wolfgang A1 - Droste, Bernhard A1 - Behrend, Eberhard A1 - Wilde, Hans T1 - Mustersicherheitsanalyse eines Flüssiggastanklagers bei einer Gross-Kfz-Tankstelle (UBA-FB 86-007) PY - 1986 IS - 22 SP - 1 EP - 104 PB - Umweltbundesamt CY - Dessau-Roßlau AN - OPUS4-21703 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Aurich, Dietmar A1 - Droste, Bernhard A1 - Helms, Rolf A1 - Ziebs, Josef T1 - Mechanical requirements for materials of accident proof packagings of radioactive materials T2 - PATRAM ´83 - 7th International Symposium on packaging and transportation of radioactive materials CY - New Orleans, Lousiana, USA DA - 1983-05-15 PY - 1983 VL - I IS - Paper 087 SP - 110 EP - 115 AN - OPUS4-21704 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard A1 - Feller, H.G. ED - Frankenthal, R.P. ED - Kruger, J. T1 - The passivity of nickel and nickel alloys T2 - 4th International Symposium on Passivity - Passivity of Metals CY - Princeton, NJ, USA PY - 1978 SP - 802 EP - 826 CY - Princeton, New Jersey, USA AN - OPUS4-21705 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard ED - Feller, ED - Frohberg, ED - Osterwald, ED - Thomas, T1 - Abscheidungsbedingungen und Eigenschaften galvanisch abgeschiedener Metalle T2 - Fachseminar "Verhalten und Eigenschaften von metallischen Oberflächen" CY - Berlin, Deutschland PY - 1976 SP - 122 EP - 138 CY - Berlin AN - OPUS4-21708 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - von Chrzanowski, Lars A1 - Beckmann, Jörg A1 - Marchetti, Barbara A1 - Ewert, Uwe A1 - Schade, U. T1 - Capability of terahertz-wave instrumentation for non destructive testing of liquids T2 - 10th European conference on non-destructive testing CY - Moscow, Russia DA - 2010-06-07 KW - Terahertz PY - 2010 UR - http://www.ndt.net/article/ecndt2010/reports/1_05_16.pdf IS - Paper 4.02.18 SP - 1 EP - 8 AN - OPUS4-21685 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Droste, Bernhard T1 - Die Verträglichkeit von metallischen Behälterwerkstoffen und wassergefährdenden Flüssigkeiten PY - 1991 IS - Kurs SW 27 / Kap. 8.2 SP - 1 EP - 36 AN - OPUS4-21690 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard T1 - Brandschutz von Flüssiggaslagerbehältern T2 - Internationales Seminar "Gefährliche Stoffe beim Feuerwehreinsatz" CY - Neuherberg, Deutschland DA - 1991-03-19 PY - 1991 VL - I SP - 1 EP - 16 AN - OPUS4-21692 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard T1 - Gutachterliche Stellungnahmen zu Fragen des Brand- und Explosionsschutzes bei Flüssiggasanlagen T2 - BPU-Seminar "Anwendung der Störfall-Verordnung (12. BImSchV)" CY - Berlin, Deutschland DA - 1991-07-01 PY - 1991 SP - 1 EP - 12(?) CY - Berlin AN - OPUS4-21693 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard T1 - Die Beurteilung der Sicherheit von Behältern für die trockene Zwischenlagerung abgebrannter Brennelemente T2 - Deutsch-Sowjetisches Seminar zum thema "Erfahrung auf dem Gebiet der Lagerung und des Transportes von abgebrannten Kernbrennstoffen; zukunftsträchtige Verfahren auf diesem Gebiet" CY - Berlin/Gorleben/Essen, Deutschland DA - 1990-12-13 PY - 1990 SP - 58 EP - 90 AN - OPUS4-21696 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Droste, Bernhard T1 - Über den Einfluss organischer Badzusätze auf die elektrolytische Nickelabscheidung PY - 1981 SP - 1 EP - 146 CY - Berlin AN - OPUS4-21697 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard A1 - Wieser, Günter A1 - Probst, Ulrich T1 - Thermal test requirements and their verification by different test methods N2 - This paper describes a new propane - fired test facility and the results of tests with a big vessel calorimeter to demonstrate compliance with the IAEA thermal test requirements. T2 - PATRAM ´92 - 10th International symposium on the packaging and transportation of radioactive materials CY - Yokohama, Japan DA - 1992-09-13 PY - 1992 VL - 3 SP - 1263 EP - 1272 AN - OPUS4-21822 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard T1 - Passive containment, monitoring and heat removal of spent fuel and HLW in multi-purpose metal casks T2 - Post-SMiRT 14 - International Seminar 18 - Passive safety features in nuclear installations CY - Pisa, Italy DA - 1997-08-25 PY - 1997 SP - C 2.25 EP - C 2.31 CY - Pisa, Italy AN - OPUS4-21803 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard A1 - Gogolin, Bernd A1 - Quercetti, Thomas A1 - Rittscher, D. T1 - Drop test of a cubic DCI container for radioactive wastes T2 - PATRAM ´92 - 10th International symposium on the packaging and transportation of radioactive materials CY - Yokohama, Japan DA - 1992-09-13 PY - 1992 VL - 3 SP - 1435 EP - 1442 AN - OPUS4-21823 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz-Forberg, Bernd A1 - Zeisler, Peter A1 - Droste, Bernhard A1 - Kondratiev, A. A1 - Kozlov, J. A1 - Tichinov, N. T1 - Soviet-German cooperation in safety improvements of spent fuel transport casks N2 - The paper gives a survey of the Soviet (Russian) -German activities which started in 1988 with the objective of creating a long-term scientific-technical cooperation in the field of transport and storage casks for spent nuclear fuel. The first step, i.e., the step of informing each other about the state of development is done. The more complicated second phase with concerted common activities of both the Russian and German competent authorities and industrial enterprises is intended to start in the near future. T2 - PATRAM ´92 - 10th International symposium on the packaging and transportation of radioactive materials CY - Yokohama, Japan DA - 1992-09-13 PY - 1992 VL - 1 SP - 343 EP - 350 AN - OPUS4-21824 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wieser, Günter A1 - Droste, Bernhard T1 - Full-scale versus small-scale fire testing of fire protection materials for LPG storage vessels N2 - This paper presents test results of different fire test series with full-scale fire engulfment (4.85m³ propane vessels protected with an intumescent coating, rock wool or two cementitious fire protection materials based on vermiculite and Portland cement). Furthermore, the correlation of these tests with furnace plate tests and/or numerical calculations are discussed. It is our aim to present a method or way for the usefulness of small-scale fire tests. This method has to be quantified and statistically proved. The paper is a revision and amplification of /13/. T2 - 7th International symposium on loss prevention and safety promotion in the process industries CY - Taormina, Italy DA - 1992-05-04 PY - 1992 IS - Paper 75 SP - 1 EP - 20 AN - OPUS4-21825 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wieser, Günter A1 - Droste, Bernhard T1 - Full-scale and small-scale fire protection matials for vessels containing pressurised inflammable gases N2 - This paper will present test results of different fire test series with full-scale fire engulfment tests (4.85 m³ propane tanks protected with an intumescent coating, rock wool or a heat insulator based on vermiculite and Portland cement). Furthermore, the correlation of these tests with furnace plate tests and/or numerical calculations will be discussed. T2 - IMEKO/GESA Symposium - Risk minimization by experimental mechanics PY - 1992 SP - 345 EP - 356 PB - VDI-Verl. AN - OPUS4-21826 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Swimm, K. A1 - Scherdel, C. A1 - Reichenauer, G. A1 - Klobes, Peter T1 - Characterization of organic aerogels as model materials for thermal conductivity measurements KW - Aerogels KW - SEM KW - SAXS KW - N2 sorption KW - Hg porosimetry KW - Thermal conductivity KW - Porosity PY - 2008 UR - http://hasylab.desy.de/annual_report/files/2008/200838.pdf SP - 1 EP - 2 PB - DESY CY - Hamburg AN - OPUS4-21828 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dietrich, Paul A1 - Unger, Wolfgang T1 - Charakterisierung von Microarrays durch Anwendung physikalischer Methoden der chemischen Oberflächenanalytik KW - Oberflächenmodifizierungen KW - Self-assemblierende Monolagen KW - Thiole KW - Aminierte Oberflächen KW - Microarrays KW - XPS KW - ToF-SIMS PY - 2010 UR - http://www.analytik-news.de/Fachartikel/Volltext/BAM1.pdf SP - 1 EP - 11 PB - Dr. Beyer Internet-Beratung CY - Ober-Ramstadt AN - OPUS4-21834 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard T1 - Versuche mit unterschiedlichen Brandschutzmaterialien für die Erstellung von Prüfungszeugnissen T2 - Brandschutzarten in Lägern für druckverflüssigte, brennbare Gase (Seminar S-72-303-096-2) CY - Essen, Deutschland DA - 1992-03-25 PY - 1992 SP - 1 EP - 8(?) CY - Essen AN - OPUS4-21797 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard T1 - Sicherheitsabstände und Möglichkeiten zu deren Verringerung T2 - Seminar "Flüssiggaslagerung: Neueste technische und rechtliche Vorschriften-Anwendung" CY - Berlin, Deutschland DA - 1992-03-12 PY - 1992 SP - 1 EP - 18(?) CY - Berlin AN - OPUS4-21798 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard T1 - Package testing T2 - Joint IAEA/EC course on the safe transport of radioactive material CY - Mol, Belgium DA - 1996-10-07 PY - 1996 IS - Chapter 15 SP - 197 EP - 209 CY - Vienna, Austria AN - OPUS4-21800 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quercetti, Thomas A1 - Gogolin, Bernd A1 - Droste, Bernhard T1 - Nachweis der mechanischen Integrität eines "POLLUX" Transport- und Endlagerbehälters: Instrumentierte Freifallprüfungen T2 - GESA-Symposium - Experimentelle Beanspruchungsanalyse, Neue Entwicklungen und Anwendungen CY - Schliersee, Deutschland DA - 1996-10-10 PY - 1996 SP - 1 EP - 3(?) CY - Düsseldorf AN - OPUS4-21801 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard T1 - Zulassungen und Prüfungen von Transport- und Lagerbehältern T2 - GRS Workshop "Genehmigung der Zwischenlagerung bestrahlter Brennelemente und Abfälle in Behältern" CY - Berlin, Deutschland DA - 1996-05-06 PY - 1996 N1 - Sprachen: Deutsch/Russisch - Languages: German/Russian IS - Kap. 2.4 SP - 1 EP - 23 CY - Berlin AN - OPUS4-21802 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Dietrich, Paul A1 - Graf, Nora A1 - Gross, Thomas A1 - Lippitz, Andreas A1 - Schüpbach, B. A1 - Terfort, A. A1 - Unger, Wolfgang T1 - Characterization of self-assembled monolayers of terphenylthiols with amine head groups KW - Terphenylthiolate SAMs KW - Gold KW - Microarray KW - NEXAFS PY - 2008 SP - 195 EP - 197 AN - OPUS4-22909 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Enzmann, F. A1 - Kersten, M. A1 - Goebbels, Jürgen A1 - Meinel, Dietmar T1 - High-resolution X-ray tomography imaging of ivory KW - Ivory KW - High-resolution X-ray tomography KW - Elfenbein KW - Hochauflösende Röntgen-Computer-Tomographie PY - 2008 VL - 228 SP - 81 EP - 86 PB - BfN CY - Bonn AN - OPUS4-22889 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Goebbels, Jürgen T1 - Structural index of metal matrix composites evaluated with computed tomography T2 - 17th World Conference on Non-Destructive Testing CY - Shanghai, China DA - 2008-10-25 KW - Computed tomography KW - Titanium metal matrix composites KW - Dimensional control PY - 2008 SP - 1 EP - 6 PB - International Committee for Non-Destructive Testing CY - Shanghai AN - OPUS4-22890 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Gula, Michal T1 - Explosionstechnische Charakterisierung chemisch instabiler Gase N2 - Es wurde das Reaktionsverhalten von drei chemisch instabilen Gasen nach dem Wirksamwerden einer Zündquelle untersucht: Distickstoffmonoxid (N2O), Stickstoffmonoxid (NO) und 1,2-Butadien (C4H6). Dabei wurden die resultierenden Explosionsdrücke, die zeitlichen Druckanstiege sowie die Stabilitätsgrenzen bei Anfangstemperaturen bis 220 °C und Anfangsdrücken bis 30 bara in fünf Autoklaven unterschiedlicher Form und Größe bestimmt. Die chemisch instabilen Gase wurden sowohl als reine Stoffe als auch als binäre Gasgemische untersucht. Bei den binären Gemischen wurden die Einflüsse der Brenngasanteile in CH4/N2O- bzw. C3H8/N2O-Gemischen auf die Reaktionsdynamik und die Einflüsse der Inertgasanteile in N2/N2O- bzw. CO2/N2O-Gemischen auf die Stabilitätsgrenzen untersucht. Für die Auswertung der Zündversuche wurden die zeitlichen Druckverläufe gemessen und bei Versuchen in einem Fensterautoklav teilweise mit Hochgeschwindigkeitsaufnahmen synchronisiert. Die Zerfallsreaktionen wurden jeweils durch eine Fremdzündung in Form eines explodierenden Drahtes initiiert. Da die Flammenausbreitung bei einer Zerfallsreaktion in hohem Maße konvektionsbeeinflusst und sehr anfällig für Wärmeverluste ist, wurde für ausgewählte Gase der Einfluss des Zündortes bzw. die Autoklavenausrichtung auf den Zerfall untersucht. Dadurch wurde auch bei Zündversuchen in gleichen Autoklaven eine Variation der freien Weglänge erreicht, in der sich eine Flamme ungehindert ausbreiten kann. Wärmeverluste werden dabei reduziert. Die Ergebnisse der Versuche zeigten, dass nicht nur das Volumen sondern vor allem die Ausrichtung des Autoklavs bzw. der Zündort einen großen Einfluss auf die Reaktionsdynamik und die Stabilitätsgrenzen haben. Da die Untersuchungen in Volumina bis 100 l möglich waren, konnten auch wichtige Rückschlüsse auf ein mögliches Scale-Up gezogen werden. Zur Abschätzung einer Explosionsauswirkung beim Zerfall chemisch instabiler Gase wurde das Simulationsmodell "FireBall" modifiziert. Das Modell wurde ursprünglich für die Simulation einer Explosion von binären Brenngas/Luft-Gemischen entwickelt, die sich im Bereich der stöchiometrischen Zusammensetzung befinden. Im Rahmen dieser Dissertationsarbeit wurde eine Erweiterung des bestehenden Berechnungsmodells auf reine Zerfallsreaktionen vorgenommen. Die Ausbreitung einer Flamme basiert auf der Berechnung einer laminaren und einer turbulenten Flammengeschwindigkeit, die maßgeblich für die Reaktionsdynamik sind. Das Explosionsausbreitungsmodell beinhaltet verschiedene Sub-Modelle, die zum Beispiel die Wärmeübertragung zu den Wänden oder die freie Konvektion berücksichtigen. Einige Sub-Modelle benötigen empirische Koeffizienten, welche experimentell ermittelt werden müssen. Mit dem Modell werden letztlich zeitliche Druckverläufe eines durch Fremdzündung initiierten deflagrativen Zerfalls in einem geschlossenen System simuliert. Aus den Druck-Zeit-Kurven werden die zeitlichen Druckanstiege bzw. KG-Werte und die Explosionsdrücke ermittelt. Diese Simulationen wurden für N2O und NO unter Variation der Anfangstemperatur, des Anfangsdrucks und des Zündortes für unterschiedliche Behältergeometrien und -volumina durchgeführt. Das erweiterte Berechnungsmodell "FireBall" liefert für beide instabile Gase gute Übereinstimmungen zwischen den experimentellen Ergebnissen und der Simulation. KW - Reaktionsausbreitung KW - Butadien KW - Distickstoffmonoxid KW - Stickstoffmonoxid KW - Inertisierung KW - Modellierung KW - FireBall PY - 2009 SP - 1 EP - 163 CY - Berlin AN - OPUS4-22876 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Drame, Christian T1 - Ausbreitung von Deflagrationen in geschlossenen langen Rohrleitungen KW - Explosionsschutz KW - Deflagration KW - Rohrleitungen PY - 2010 SP - 1 EP - 114 AN - OPUS4-22877 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bartusch, Jürgen A1 - Döring, Joachim A1 - Sickert, Roland A1 - Wüstenberg, Hermann A1 - Albayrak, C. A1 - Rößling, G. T1 - Eine neue Methode zur Bestimmung des Rückstreuverhaltens disperser Systeme T2 - DGZfP-Jahrestagung 1994 CY - Timmendorfer Strand, Deutschland DA - 1994-05-09 PY - 1994 IS - DGZfP-BB 43 SP - 341 EP - 346 AN - OPUS4-22932 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mishra, Kirti Bhushan A1 - Wehrstedt, Klaus-Dieter A1 - Schönbucher, A. T1 - Pool and tank fires - Are we really prepared? N2 - The industrial fire accidents e.g. Buncefield (2005) and Jaipur (2009) have come up with several issues concerning safe storage and transportation of flammable liquids. The pre and post fire consequences are therefore important to be analyzed prior to the handling of flammable fuels. Pool or/and tank fire is the most often seen scenario after the leak/spill of liquid fuel. An overview of the typical scenarios from large hydrocarbon and organic peroxide pool fires and their respective safety distances for the people and the infrastructure are the important subjects of this paper. T2 - 8th Asia-Pacific conference on combustion CY - Hyderabad, India DA - 2010-12-10 KW - Flammable liquids KW - Pool fire KW - Safety distance KW - Organic peroxides PY - 2010 SP - 697 EP - 702 AN - OPUS4-23004 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schwenk, D. A1 - Subaric-Leitis, Andreas T1 - Characteristic quality parameters of measurement - verification and calibration of material testing machines T2 - IMEKO 2010 TC3, TC5 and TC22 Conferences - Metrology in modern context CY - Pattaya, Chonburi, Thailand DA - 2010-11-22 KW - Span KW - Standard deviation KW - Material testing machines PY - 2010 SP - 129 EP - 132 AN - OPUS4-22954 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Krause, Ulrich T1 - Conduction-diffusion problems - „exotics“ in fire simulations? N2 - Fire simulation is mostly understood as simulation of room fires, i.e. where the free volume is large compared to the volume occupied by the combustible matter. In such a case, the fire propagation is predominantly a fluid dynamics problem. Fire propagation through bulk materials, insulation layers or wooden construction elements is, however, determined by conduction and diffusion. For these cases modified modelling principles and different software solutions have to be applied. Computational results are presented for temperature evolution and charring progress in a timber beam exposed to ISO standard temperature curve, for self-ignition and fire propagation in a waste deposit with consideration to conduction/diffusion and convection inside the porous medium and for a fire in an underground coal seam where conduction/diffusion is the prevailing mechanism. T2 - 11th International symposium on fire protection CY - Leipzig, Germany DA - 2010-06-08 KW - Self-ignition KW - Porous media KW - Fire simulation KW - Smouldering PY - 2010 SP - 1 EP - 13 AN - OPUS4-22958 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - de Oliveira, Rui A1 - Schukar, Marcus A1 - Krebber, Katerina A1 - Michaud, V. T1 - Development of adaptive composites with embedded plastic optic fibres N2 - This study discusses the development of advanced composite materials with sensing capabilities obtained from the embedment of long period gratings in microstructured plastic optical fibres (mPOF-LPG). The mPOF-LPG was embedded in a carbon fibre reinforced polymer (CFRP) unidirectional laminate manufactured in autoclave. Processing steps were established in order to insure that mPOF does not suffer significant optical and structural degradation. The strain and temperature responses of the embedded mPOF-LPG were investigated. T2 - ICRACM 2010 - 3rd International conference on recent advances in composite materials CY - Limoges, France DA - 2010-12-13 KW - Polymer composites KW - Optical fibre sensors KW - mPOF-LPG KW - SHM PY - 2010 IS - Polymer composite session / FP-Oliveira SP - 1 EP - 6 AN - OPUS4-23040 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krebber, Katerina A1 - Lenke, Peter A1 - Liehr, Sascha A1 - Nöther, Nils A1 - Wendt, Mario A1 - Wosniok, Aleksander A1 - Schneider-Gloetzl, J. A1 - Gloetzl, R. T1 - Distributed fibre optic sensors embedded in technical textiles for monitoring of geotechnical and masonry structures T2 - Monitoring technologies workshop - MoDeRn (Proceedings) CY - Troyes, France DA - 2010-06-07 PY - 2010 IS - OP.7 SP - 71 EP - 72 AN - OPUS4-23041 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Boas, W. A1 - Rupp, E. T1 - Über die Elektronenbeugung an reinem und an passivem Eisen PY - 1933 IS - 21 SP - 79 EP - 83 PB - Springer CY - Berlin AN - OPUS4-16820 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmid, Erich A1 - Wassermann, G. T1 - Röntgenographische Untersuchungen an elektrolytisch-oxidiertem Aluminium PY - 1933 IS - 21 SP - 83 EP - 87 PB - Springer CY - Berlin AN - OPUS4-16821 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Blumenthal, B. A1 - Hansen, Max T1 - Über den Einfluß von Kadmium und Blei auf die Eigenschaften des Aluminiums PY - 1933 IS - 21 SP - 87 EP - 93 PB - Springer CY - Berlin AN - OPUS4-16822 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Zunker, P. T1 - Einfluß von Temperatur und Fremdmetallen auf die Walzbarkeit von Zink PY - 1933 IS - 21 SP - 93 EP - 102 PB - Springer CY - Berlin AN - OPUS4-16823 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hummel, Alfred T1 - Vom Kriechen oder Fließen des erhärteten Betons und seiner praktischen Bedeutung PY - 1937 IS - 32 SP - 55 EP - 61 PB - Springer CY - Berlin AN - OPUS4-17240 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Wilhelm T1 - Einfluß ungleichförmig verteilter Spannungen auf die Festigkeit von Werkstoffen PY - 1937 IS - 32 SP - 63 EP - 71 PB - Springer CY - Berlin AN - OPUS4-17241 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Wilhelm A1 - Lubimoff, W. T1 - Gesetzmäßige Abhängigkeit der Biegewechselfestigkeit von Probengröße und Kerbform PY - 1937 IS - 32 SP - 73 EP - 77 PB - Springer CY - Berlin AN - OPUS4-17242 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Wilhelm T1 - Einfluß des durch die Gestalt erzeugten Spannungszustandes auf die Biegewechselfestigkeit PY - 1937 IS - 32 SP - 79 EP - 83 PB - Springer CY - Berlin AN - OPUS4-17243 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Wilhelm T1 - Gestaltliche Gefügebeschreibung als aussichtsreiche Grundlage der mechanischen Werkstoffbeurteilung PY - 1937 IS - 32 SP - 85 EP - 88 PB - Springer CY - Berlin AN - OPUS4-17244 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Seidl, Erich T1 - Die theoretischen Grundlagen einer neuzeitlichen Werkstoff-Forschung - Systematik bleibender Formänderungen; als Arbeits-Grundlage für Werkstoff-Forschung und -Prüfung PY - 1937 IS - 33 SP - 5 EP - 20 PB - Springer CY - Berlin AN - OPUS4-17230 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Wilhelm T1 - Neuzeitliche Werkstoff-Mechanik als theoretische Grundlage der Werkstoff-Formgebung und -Prüfung PY - 1937 IS - 33 SP - 21 EP - 28 PB - Springer CY - Berlin AN - OPUS4-17231 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lambertz, A. T1 - Einordnung der wichtigsten Werkstoff-Gruppen in die Systematik Bleibender Formänderungen PY - 1937 IS - 33 SP - 29 EP - 58 PB - Springer CY - Berlin AN - OPUS4-17232 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lehr, Ernst T1 - Elastische Formänderungen als Normalfall, Bleibende Formänderungen als Grenzfall; erläutert am Beispiel des Maschinenbaus PY - 1937 IS - 33 SP - 59 EP - 65 PB - Springer CY - Berlin AN - OPUS4-17233 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kindscher, Erich T1 - Grenzflächenfragen und ihre Bedeutung für die Technik PY - 1937 IS - 32 SP - 2 EP - 17 PB - Springer CY - Berlin AN - OPUS4-17234 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Haase, W. A1 - Richter, G. T1 - Knochenbrüche, beurteilt nach den Grundsätzen und Erkenntnissen der technischen Mechanik PY - 1937 IS - 32 SP - 19 EP - 34 PB - Springer CY - Berlin AN - OPUS4-17235 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald T1 - Gedanken über die Konstitutionsforschung der Metalle und Legierungen PY - 1937 IS - 32 SP - 35 EP - 37 PB - Springer CY - Berlin AN - OPUS4-17236 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lambertz, A. T1 - Werkstoff-Forschung und Physik PY - 1937 IS - 33 SP - 39 EP - 40 PB - Springer CY - Berlin AN - OPUS4-17237 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Werner, Otto T1 - Entwicklung der chemischen, physikalisch-chemischen und physikalischen Prüfverfahren in ihrer Anwendung auf die Metallkunde PY - 1937 IS - 32 SP - 41 EP - 42c PB - Springer CY - Berlin AN - OPUS4-17238 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kreutzbruck, Marc A1 - Brekow, Gerhard A1 - Böhm, R. A1 - Montag, Hans-Joachim A1 - Allweins, K. A1 - Strackbein, C. A1 - Bernau, H. T1 - Visualization of material defects - modern approaches in acoustical and electrical NDE-methods N2 - Increasing demands in materials quality and cost effectiveness have led to advanced standards in manufacturing technology. Especially when dealing with high quality standards in conjunction with high throughput quantitative NDE techniques are vital to provide reliable and fast quality control systems. Fast NDE-systems using a high degree of automatisation can be used for both determining the degree of integrity of the components under test and indicating a change of production parameters as well. However, independently of the applied NDE method and the underlying physical principle a reliable visualisation of hidden defects within the component under test is based on a sufficient high signal to noise ratio (SNR) and a high spatial resolution. In this talk we illuminate two standard NDT methods such as Ultrasonic Testing and Eddy Current Testing and show their physical principles also discussing the interaction between sound waves or induced eddy currents with different kinds of material defects. This introduction substantiates the attainable SNR and spatial resolution of both methods with respect to defect sizing and defect classification. As a first future prospect we report on the SAFT-algorithm to improve SNR and spatial resolution paving the way for a flaw sizing approach in ultrasonic inspection. As a second modern NDE approach we represent the use of small magnetoresistance sensor arrays for EC testing of Al-laser welds or for testing superconducting wires. The high sensitivity and small extent of GMR sensors results in a remarkably SNR and spatial resolution offering new visualisation techniques for defect localisation, defect characterization and tomography-like mapping techniques. T2 - ICAMT 2008 - International Conference on Advances in Manufacturing Technology for Young Engineers CY - Madras, Chennai, India DA - 2008-02-06 PY - 2008 IS - CD-ROM (A.4 / I-1) SP - 1 PB - Indian National Academy of Engineering (INAE) CY - Madras, Chennai, India AN - OPUS4-17622 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völzke, Holger T1 - Erfahrungen und Perspektiven bei der Bauartprüfung von Behältern zur Verpackung radioaktiver Abfälle T2 - TÜV Nord Seminar "Endlagerung radioaktiver Abfälle - Herausforderungen und Lösungen bei der Produktkontrolle radioaktiver Abfälle" CY - Hannover, Deutschland DA - 2008-06-11 KW - Endlager KW - Behälter KW - Bauartprüfung PY - 2008 SP - 11/1 EP - 11/7 AN - OPUS4-17679 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bonnand, V. A1 - Klingelhöffer, Hellmuth ED - Portella, Pedro Dolabella ED - T. Beck, ED - M. Okazaki, T1 - SC16 at 950°C under LCF loading on smooth cylindrical specimen: influence of secondary orientation T2 - 6th International Conference on Low Cycle Fatigue (LCF 6) CY - Berlin, Germany DA - 2008-09-08 KW - Ni-base superalloy KW - Single crystal KW - Fractography KW - LCF KW - Secondary direction KW - Precipitates KW - Damage PY - 2008 SP - 397 EP - 402 AN - OPUS4-17913 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klingelhöffer, Hellmuth A1 - Epishin, A. A1 - Link, T. A1 - Portella, Pedro Dolabella ED - Portella, Pedro Dolabella ED - T. Beck, ED - M. Okazaki, T1 - Low cycle fatigue of the single crystal nickel-base superalloy CMSX-4: anisotropy and effect of creep damage T2 - 6th International Conference on Low Cycle Fatigue (LCF 6) CY - Berlin, Germany DA - 2008-09-08 KW - Anisotropy of mechanical properties KW - Effect of creep damage on LCF KW - Single-crystal nickel-base superalloys PY - 2008 SP - 403 EP - 408 AN - OPUS4-17914 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Huismann, Sven T1 - Damage of a high performance concrete at high temperatures due to thermo-mechanical stresses T2 - 7th International PhD Symposium in Civil Engineering CY - Stuttgart, Germany DA - 2008-09-11 KW - High performance concrete KW - Fire KW - High temperatures KW - Cracking KW - Thermo-mechanical stresses PY - 2008 IS - Kap. 16.3 SP - 23 EP - 29 AN - OPUS4-17950 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bahlmann, Stefanie T1 - Investigation on the use of industrial residues as substitutes for primary resources in mortar and concrete T2 - 7th International PhD Symposium in Civil Engineering CY - Stuttgart, Germany DA - 2008-09-11 KW - Industrial residues KW - Cement substitute KW - Utilization potential PY - 2008 IS - Kap. 2.1 SP - 3 EP - 10 AN - OPUS4-17949 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Kranzmann, Axel T1 - Oxidation of a single crystal nickel-base superalloy at 950 °C - a kinetic and microstructure study N2 - The nickel-base single crystal alloy investigated is a widely used material for first and second row blades in stationary gas turbines. Nickel-base superalloys are especially designed to resist high temperature oxidation by process gases. To determine this high temperature behaviour oxidation testing was carried out using samples cut perpendicular to (001)-direction. Microstructures were characterized by X-ray diffraction XRD, Light Microscopy LM, Scanning Electron Microscopy SEM, and X-ray energy dispersive spectroscopy (EDS), after a series of heat treatments (950 °C, 0 h - 1000 h). Mass gain and the respective thicknesses of the different oxide layers were measured to determine oxidation kinetics. In general, the isothermal oxidation behaviour at 950 °C, as defined by weight gain, follows a parabolic law with a parabolic rate constant around 1.4 · 10-2 mg2/(cm4 · h). A short incubation time is followed by the constitution of a multi-layered oxide scale. The oxide scale consists of a three layer structure. An outer scale contains a Ti-bearing thin film associated as TiO2 and NiTiO3 but mostly Cr attributed to Cr2O3, (Ni/Co)Cr2O4 beside NiTaO4. This outer scale is connected to a discontinuous layer of inner oxidation consisting mainly of Al2O3, which is followed by an area of γ´-depletion within the base material. PY - 2008 SP - 1 EP - 9 AN - OPUS4-17263 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Probst, Ulrich A1 - Hagenow, Peter A1 - Völzke, Holger A1 - Wolff, Dietmar A1 - Wossidlo, Peter A1 - Abbasi, Behboud A1 - Achelpöhler-Schulte, Andreas A1 - Schulz, Sebastian T1 - Investigation of seal effects according to axial compression variation of metal seals for transport and storage casks T2 - PATRAM 2007, 15th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Miami, Florida, USA DA - 2007-10-21 KW - Metal Seals KW - Axial Compression KW - Cycling Tests KW - Helium Leakage Rate PY - 2007 SP - 1 EP - 8 PB - Institute of Nuclear Materials Management AN - OPUS4-17542 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Torge, Manfred A1 - Wilke, Olaf A1 - Brödner, Doris T1 - Effects of emissions of materials for wrapping, transportation and storage on stained glass windows and on glass objects in show cases in museums N2 - The emission of volatile organic compounds (VOC) of materials for wrapping, transportation and storage of stained glass windows were investigated by direct thermal desorption. The analysis was performed with thermal desorption in combination with gas chromatography and mass spectrometry. Emissions of organic acids were determined. The damage risk of volatile organic compounds, e.g. organic acids as acetic acid, propanoic acid, hexanoic acid and octanoic acid was investigated on model glasses in climate chambers. After exposure the surface of the most sensitive samples was damaged. Based on emission measurements in exhibit cases of the former museum "Grünes Gewölbe in the Albertinum" in Dresden, Germany, the atmospheric conditions inside the show cases were determined. It can be shown that the atmospheric conditions inside the cases endanger the glass and enamel objects of art especially in show cases with low air exchange rates. Materials with high emission rates of organic acids should not be in direct contact with medieval glass for a long time and should not be used in exhibit cases. Acid emissions, especially acetic acid plays an important role during investigation of different materials for show cases and can be determined by direct thermal desorption. T2 - Art 2008, 9th International Conference CY - Jerusalem, Israel DA - 2008-05-25 KW - Emissionen KW - Volatile Organic Compounds KW - Glas KW - Medieval staind glass PY - 2008 UR - http://www.ndt.net/article/art2008/papers/059Torge.pdf IS - CD-ROM SP - 1 EP - 9 PB - ISAS International Seminars CY - Jerusalem, Israel AN - OPUS4-17600 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Böttcher, Bernhard ED - Müller, E. A. W. T1 - Wärmeflußverfahren - Technische Hilfsmittel und Einrichtungen PY - 1975 IS - Abschnitt C.4 SP - 1 EP - 28 PB - Oldenbourg CY - München AN - OPUS4-17607 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Böttcher, Bernhard ED - Müller, E. A. W. T1 - Wärmeflußverfahren - Erscheinungsform der Prüfwerte, Genauigkeit und Empfindlichkeit der Prüfverfahren PY - 1975 IS - Abschnitt E.4 SP - 1 EP - 16 PB - Oldenbourg CY - München AN - OPUS4-17608 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Burkert, Andreas A1 - Fischer, Joachim A1 - Isecke, Bernd T1 - Kontaktkorrosion - Grundlagen berücksichtigen und richtig einschätzen N2 - In vielen Konstruktionen erfordern unterschiedliche Eigenschaftsanforderungen an Komponenten und Bauteile häufig die Kombination verschiedener metallischer Werkstoffe. In der Praxis sind aber auch sogenannte Zufallskombinationen häufig anzutreffen, bei denen die Kombination allein durch die momentane Verfügbarkeit z.B. eines Befestigungsmittels oder eines Zwischenstückes zustande kommt. Unter bestimmten Einsatzbedingungen kann eine solche Kombination, die auch unter dem Begriff Mischbauweise bekannt ist, zu Korrosionsproblemen an einem der beiden Partner führen. Die Grundlagen und Einflussgrößen auf die Bimetallkorrosion werden dargestellt und deren praktische Bedeutung anhand von Beispielen verdeutlicht. T2 - 8. Tagung "Korrosionsschutz in der maritimen Technik" CY - Hamburg, Deutschland DA - 2009-01-28 KW - Korrosionsschutz KW - Maritime Technik KW - 8. Tagung PY - 2009 SP - 13 EP - 25 CY - Hamburg AN - OPUS4-18945 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Döring, Joachim A1 - Bovtun, Viktor Petrovic A1 - Bartusch, Jürgen A1 - Erhard, Anton T1 - Eigenschaften von Polypropylen- und PVDF-Folien für Luftschall-Anwendungen N2 - An Methoden zur luftgekoppelten Ultraschallprüfung wird seit einigen Jahren mit großer Intensität gearbeitet. Probleme bei der praktischen Realisierung entstehen vor allem durch die großen Unterschiede in der akustischen Impedanz von Wandlermaterial und Luft. Sie führen zu erheblichen Signaldämpfungen. Durch die Verwendung von Kunststoff-Folien z.B. aus porösem Polypropylen kann dieser Unterschied stark reduziert werden. Im Beitrag werden die akustischen Eigenschaften dieser Folien untersucht und im Hinblick auf ihre Eignung für die Luftultraschall-Technik analysiert. T2 - DACH-Jahrestagung 2004 - ZfP in Forschung, Entwicklung und Anwendung CY - Salzburg, Österreich DA - 2004-05-17 KW - Luftschall-ZfP KW - Ultraschall-Wandler PY - 2004 UR - http://www.ndt.net/article/dgzfp04/papers/p11/p11.htm SP - 1 EP - 4 CY - Salzburg, Österreich AN - OPUS4-19059 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard A1 - Hübner, Heinz W. A1 - Wieser, Karol E. T1 - Quality assurance measures for RAM-Packagings in the Federal Republic of Germany T2 - PATRAM ´80 - 6th International symposium on the packaging and transportation of radioactive materials CY - Berlin, Germany DA - 1980-11-10 PY - 1981 VL - 1 SP - 708 EP - 713 PB - Bundesanstalt für Materialprüfung CY - Springfield, Va. AN - OPUS4-19032 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rücker, Werner A1 - Auersch, Lutz ED - Müller, G. T1 - Praxisgerechtes Prognosemodell für Erschütterungen PY - 2008 SP - 37 EP - 47 AN - OPUS4-19042 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Huismann, Sven A1 - Korzen, Manfred T1 - Experimental and numerical study of high performance concrete columns subjected to fire loading T2 - International Conference "Applications of structural fire engineering" CY - Prague, Czech Republic DA - 2009-02-19 KW - High performance concrete KW - Fire KW - High temperatures KW - Columns PY - 2009 SP - 246 EP - 251 CY - Prague, Czech Republic AN - OPUS4-19048 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz-Forberg, Bernd A1 - Droste, Bernhard A1 - Charlett, H. T1 - Failure mechanisms of propane-tanks under thermal stresses including fire engulfment T2 - Transport and storage of LPG and LNG CY - Bruges, Belgium DA - 07.05.1984 PY - 1984 IS - 1 SP - 295 EP - 305 PB - Koninklijke Vlaamse Ingenieursvereniging CY - Antwerpen AN - OPUS4-19022 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard T1 - Licensing approach used in the F. R. G. to qualify dual purpose casks T2 - Third international spent fuel storage technology symposium/workshop CY - Seattle, WA, USA DA - 1986-04-08 PY - 1986 SP - 341 EP - 344 AN - OPUS4-19122 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard T1 - Experiences in the safety evaluation of dry spent fuel storage casks in the Federal Republic of Germany T2 - Technical committee meeting on methods used in design of wet and dry spent fuel storage facilities CY - Otaniemi, Espoo, Finland DA - 1985-09-30 PY - 1985 SP - 1 EP - 12 PB - Internat. Atomic Energy Agency AN - OPUS4-19108 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schumm, A. A1 - Zscherpel, Uwe ED - Michel Bièth, ED - John Whittle, T1 - The EN584 standard for the classification of industrial radiography films and its use in radiographic modelling T2 - 6th International Conference on NDE in Relation to Structural Integrity for Nuclear and Pressurised Components CY - Budapest, Hungary DA - 2007-10-08 KW - Radiographie KW - Filmsysteme für ZfP KW - Grenzen der Bildqualität KW - Modellierung PY - 2007 N1 - Serientitel: JRC Scientific and Technical Reports / EUR - Scientific and Technical Research series – Series title: JRC Scientific and Technical Reports / EUR - Scientific and Technical Research series IS - EUR 23356 EN- 2008 SP - 347 EP - 352 AN - OPUS4-19097 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard T1 - Experiences and perspectives of package testing under hypothetical accident conditions T2 - PATRAM 2007, 15th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Miami, Florida, USA DA - 2007-10-21 PY - 2007 SP - 1 EP - 8(?) PB - Institute of Nuclear Materials Management AN - OPUS4-19091 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Steiger, Thomas A1 - Pradel, Rita T1 - Improvement of COMAR database N2 - COMAR, the international database for certified reference materials (CRM) has been improved by BAM for the benefit of CRM users and producers worldwide. The usefulness of reference materials (RM) is beyond question. RM provide "measurement benchmarks" for materials testing and chemical analysis and ensure reliability and worldwide comparability of measurements in these fields. The use of RM is a basic requirement for quality assurance. In addition CRM are very important for establishing traceability, especially in chemical analysis. Even in the age of web based technologies and services finding a proper reference material is a demanding task especially for newcomers or for new kind of materials. The best choice ist to use reference material databases that collect data from several RM producers and provide information in a uniform way. COMAR has been established to help laboratories to find the proper CRM needed. The database gives information on the worldwide availibility of certified reference materials. BAM has recently improved COMAR in order to make searching in COMAR more simple and target-orientated and to make the process of updating data more efficient. KW - COMAR KW - Reference materials KW - Certified reference materials KW - RM KW - CRM KW - Metrology in chemistry PY - 2009 IS - February SP - 19 EP - 21 CY - Jerusalem, Israel AN - OPUS4-19074 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Röder, R. A1 - Droste, Bernhard T1 - Qualitätssichernde Maßnahmen für Brennelement-Transport- und Lagerbehälter T2 - Seminar der Bundesanstalt für Materialforschung und -prüfung CY - Berlin, Deutschland DA - 1987-06-09 PY - 1987 VL - 13 SP - 107 EP - 120 PB - Bundesanstalt für Materialforschung und -prüfung CY - Berlin AN - OPUS4-19123 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard T1 - Technische Maßnahmen des vorbeugenden Brandschutzes oberirdischer Flüssiggas-Behälter PY - 1987 SP - 1 EP - 14 PB - Engler-Bunte-Institut CY - Karlsruhe AN - OPUS4-19128 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schön, W. A1 - Droste, Bernhard T1 - Brandschutzausrüstung von Flüssiggaslagertanks PY - 1987 SP - 1 EP - 16 AN - OPUS4-19142 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Senoner, Mathias A1 - Unger, Wolfgang A1 - Powell, C. T1 - Surface chemical analysis - General procedures - Determination of lateral resolution KW - AES KW - Contrast transfer function KW - Imaging KW - ISO TC 201 KW - Lateral resolution KW - Performance of imaging instruments KW - Quality management systems KW - Simulation KW - SIMS KW - XPS PY - 2009 SP - 1 EP - 65 AN - OPUS4-19158 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard A1 - Günther, B. A1 - Kowalewsky, Helmut T1 - The lid closure system of casks for the interim storage of spent fuel T2 - International seminar on spent fuel storage - safety, engineering and environmental aspects CY - Vienna, Austria DA - 1990-10-08 PY - 1990 SP - 1 EP - 19 PB - International Atomic Energy Agency CY - Wien AN - OPUS4-19232 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz, Michael A1 - Gregor, Christian T1 - Assessment of state of residual stress of hybrid pressure vessels N2 - For fully carbon fibre wrapped pressure vessels with load sharing metallic liner (Type III), it was recognized that the state of residual stress given after the autofrettage process can change even if the vessel is stored without pressure. This change is influenced by temperature and time and has a direct effect on the residual lifetime of the vessel. To study the influence of the temperature on the state of residual stress an analytical model was applied which is based on the Classical Laminate Theory (CLT). According to the model, the critical conditions leading to a decrease in lifetime were identified. To confirm the results of the model temperature cycle tests were carried out. The results of the tests are compared with the analytical model and a finite element model. To investigate the influence of time on the state of residual stress, tests on vessels were performed. The tested vessels were aged without any pressure for a longer period of time after the autofrettage process. During these tests, the strain of the vessels was monitored. T2 - ASME 2009 Pressure vessels and piping conference CY - Prague, Czech Republic DA - 2009-07-26 KW - Pressure vessel KW - Residual stress KW - Composite material PY - 2009 SP - PVP2009-77993, 1-9 PB - American Society of Mechanical Engineers CY - New York AN - OPUS4-20052 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Taffe, Alexander T1 - Neue leistungsfähige Systeme zur zerstörungsfreien Prüfung von Brücken im Zuge der objektbezogenen Schadensanalyse (OSA) T2 - VFIB: Erfahrungsaustausch Brückenprüfung 2009 CY - München, Deutschland DA - 2009-09-23 KW - Brückenprüfung nach DIN 1076 KW - Objektbezogene Schadensanalyse (OSA) KW - OSSCAR KW - Bauwerkscanner KW - Remanenzmagnetismus PY - 2009 IS - Kap. IX SP - 1 EP - 9 AN - OPUS4-20089 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beck, Matthias A1 - Goebbels, Jürgen A1 - Isecke, Bernd A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Investigations of corrosion on small cathodes in reinforced concrete - observations and suggestions N2 - Corrosion of steel reinforcement in concrete exposed to chloride containing environments is a serious problem in civil engineering practice. The standards and guidelines contain only minimum requirements regarding concrete quality and concrete cover. In very critical cases, for example the ingress of chlorides, the application of different coatings is currently the only possibility to protect the reinforced concrete structures. In this case the modelling of reinforcement corrosion would be more practical. One sub-project of a DFG-research project (FOR 537) is currently performed at the Federal Institute for Materials Research and Testing (BAM). Aim of the sub-project is the description of corrosion propagation and the characterization of the corrosion on specimens with small cathodes by electrochemical parameters. The electrochemical parameters are determined by suitable electrochemical measurements, considering concrete parameters as well as different environmental conditions. T2 - EUROCORR 2009 CY - Nice, France DA - 2009-09-06 KW - Self-corrosion KW - Steel reinforcement KW - Concrete parameters KW - X-ray tomography PY - 2009 IS - Paper 7976 SP - 1 EP - 13 AN - OPUS4-20063 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bender, S. A1 - Heyn, Andreas T1 - Evaluation and Screening of the pre-treatment states of Mg-alloys using Electrochemical Noise N2 - A successful application of magnesium alloys as light structural materials and for special applications, such as in the medical sector, depends significantly on their corrosion properties. Since the use of well-chosen surface coating systems can optimize these properties, many efforts are going in this direction. In general, any coating process must be seen in a close connection to the pre-treatment of the alloy surface, particularly for magnesium alloys. The pre-treatment is required to prepare the optimal surface for a coating system, in which adhesion and dissolution behaviour are the central properties. In the case of magnesium alloys this means a well-controlled removal of the casting or rolling skin, which would be prone to corrosion and poor adhesion. Additionally, in most cases the surface morphology should be smooth. An investigation of different pickling solutions and pickling parameters showed a wide range of effectiveness (i.e., the resulting mass loss and surface morphology). Another important and often underestimated fact is the comparatively strong tendency of magnesium to react with the atmosphere. For that reason, after a completed pickling and cleaning treatment the condition of the surrounding atmosphere and the time prior to coating of the surface should be taken into account because of the formation of different reaction layers. These layers have an effect on adhesion and the corrosion properties of the coating system as a whole. For a documentation of the influence of different atmospheres and the timedependence of the surface activity the measurement of the electrochemical noise is the preferred technique. This is because it shows instantaneously the actual activity, even in the absence of external excitation. The influence of different pre-treatments as well as exposure conditions and duration was investigated using electrochemical noise measurements as a screening method. As a result the pretreatment which is an important part of the coating process could be considerably improved. T2 - EUROCORR 2009 CY - Nice, France DA - 2009-09-06 KW - Magnesium KW - Pre-treatment KW - Pickling KW - Electrochemical noise PY - 2009 IS - Paper 8080 SP - 1 EP - 8 AN - OPUS4-20064 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kervalishvili, Guram N. A1 - Schlichting, Joachim A1 - Maierhofer, Christiane A1 - Kreutzbruck, Marc T1 - FEM modelling of heat transfer in the vicinity of vertical surface cracks using local thermal excitation T2 - Thermographie-Kolloquium 2009 CY - Stuttgart, Germany DA - 2009-10-08 KW - FEM modelling KW - Active thermography KW - Laser excitation KW - Cracks KW - Steel PY - 2009 IS - DGZfP-BB 119-CD (Poster 02) SP - 1 EP - 8 CY - Berlin AN - OPUS4-20096 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eichler, Thorsten A1 - Isecke, Bernd A1 - Klein, H.-H. T1 - Application of thermal sprayed zinc anode for CP of a multi-storey-car-park T2 - EUROCORR 2009 CY - Nice, France DA - 2009-09-06 KW - Cathodic protection KW - Thermal sprayed zinc KW - Multi-storey-car-park KW - Service life PY - 2009 IS - Paper 7862 SP - 1 EP - 14 AN - OPUS4-20237 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dombrowski, Felix A1 - Ploska, Ute A1 - Berger, Georg A1 - Gildenhaar, Renate A1 - Stiller, M. A1 - Knabe, C. ED - Kim, Sukyoung T1 - Rheological investigations on degradable and figuline calcium alkaline phosphate cements T2 - 22nd International symposium on ceramics in medicine (Bioceramics 22) CY - Daegu, Korea DA - 2009-10-26 KW - Rheology KW - Calcium alkaline phosphate cement KW - Gelatine KW - Composite PY - 2009 SP - 863 EP - 866 AN - OPUS4-20287 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gildenhaar, Renate A1 - Berger, Georg A1 - Lehmann, Erhard A1 - Spitzer, Andrea ED - Kim, Sukyoung T1 - Preparation of calcium alkali phosphate implants by 3D-printing T2 - 22nd International symposium on ceramics in medicine (Bioceramics 22) CY - Daegu, Korea DA - 2009-10-26 KW - Bone substitute material KW - Calcium alkali phosphate KW - Resorbable bioceramics KW - 3D-printing process KW - Bending strength PY - 2009 SP - 71 EP - 74 AN - OPUS4-20288 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ewert, Uwe A1 - Zscherpel, Uwe A1 - Beckmann, Jörg A1 - Bavendiek, K. T1 - Digital radiography - Films and digital detectors in comparison T2 - MINDTCE `09 - Malaysia international NDT conference and exhibiton `09 - NDT Driving industry safety, growth and performance CY - Kuala Lumpur, Malaysia DA - 2009-07-20 KW - Radiography KW - Film replacement KW - Computed radiography KW - Imaging plates KW - Digital detector arrays KW - Contrast sensitivity KW - SNR KW - standards PY - 2009 SP - 181 EP - 189 AN - OPUS4-20253 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reinecke, E.-A. A1 - Hübert, Thomas A1 - Tkatschenko, I. A1 - Kessler, A. A1 - Kuznetsov, M. A1 - Wilkins, B. A. A1 - Hedley, D. A1 - Azkarate, I. A1 - Proust, C. A1 - Acosta-Iborra, B. A1 - Gavrikov, A. A1 - De Bruijn, P.C.J. A1 - Marangon, A. A1 - Teodorczyk, A. A1 - Grafwallner, F. T1 - Integration of experimental facilities: a joint effort for establishing a common knowledge base in experimental work on hydrogen safety T2 - 3rd International conference on hydrogen safety CY - Ajaccio, Corsica, France DA - 2009-09-16 PY - 2009 IS - ID 204 SP - 1 EP - 16 AN - OPUS4-20254 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stoppel, Markus A1 - Kurz, J.H. A1 - Reichling, K. T1 - Selbstfahrendes Scannersystem für Betonflächendiagnosen "BetoScan" KW - BetoScan KW - Betonflächendiagnose KW - Scanner KW - ZfP im Bauwesen PY - 2009 VL - Special 1 SP - 50 EP - 52 PB - Ernst & Sohn CY - Berlin AN - OPUS4-20262 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfeil, Norbert T1 - Kernkompetenzen für die Sicherheit: Wissenschaftlich-technische Kompetenz braucht Lehre und Forschung - ein Beispiel PY - 2009 N1 - Serientitel: acatech diskutiert – Series title: acatech diskutiert SP - 1 EP - 10(?) PB - Springer CY - München AN - OPUS4-20280 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfeil, Norbert A1 - Risch, W. T1 - Kompetenzen für die Sicherheit PY - 2009 N1 - Serientitel: acatech diskutiert – Series title: acatech diskutiert SP - 1 EP - 4(?) PB - Springer CY - München AN - OPUS4-20281 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Beck, Uwe A1 - Reiners, Georg A1 - Sahre, Mario A1 - Weise, Matthias A1 - Gamer, Nadja A1 - Wegwerth, Tillmann T1 - Charakterisierung realer, modifizierter und beschichteter Oberflächen für den sterilen Behälter- und Anlagenbau KW - Steriltechnik KW - Oberflächentechnik KW - Oberflächenmesstechnik KW - Plasmabeschichtung KW - Partikel-Haftung PY - 2009 VL - 18 IS - 4 SP - 10 EP - 15 CY - Magdeburg AN - OPUS4-20307 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Martin, Tina ED - Zhang, Houjiang ED - Wang, Xiping T1 - Complex resistivity (CR) of wood and standing trees T2 - 16th International symposium on nondestructive testing and evaluation of wood CY - Beijing, China DA - 2009-10-12 PY - 2009 SP - 10 EP - 15 AN - OPUS4-20313 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosner, Martin A1 - Pritzkow, Wolfgang A1 - Vogl, Jochen A1 - Voerkelius, S. T1 - Boron isotope compositions of crop plants: A new tracer for the origin and authenticity of food T2 - TRACE 5th Annual Meeting and Conference CY - Freising, Germany DA - 2009-04-01 KW - Boron isotopes in food KW - Provenance studies KW - Reference materials KW - Analytical uncertainty PY - 2009 IS - Session A / Part I SP - 1 EP - 2 AN - OPUS4-20293 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heckel, Thomas A1 - Thomas, Hans-Martin A1 - Kreutzbruck, Marc A1 - Rühe, S. T1 - High speed non-destructive rail testing with advanced ultrasound and eddy-current testing techniques N2 - Today the rails face increased exposure to heavy loads, higher speeds and a very dense overall traffic. A continued development of testing methods for the rail inspection trains became necessary to match the modern needs for a fast detection and detailed classification of defects. To guarantee the safe operation of rail traffic non-destructive inspection techniques with combined ultrasound and eddy current testing methods are used to detect damages on rails. One of the main actual challenges of automated rail testing is the high inspection speed which is very close to the physical limits. To overcome these limits digital signal processing algorithms have to be used which maintain resolution and detection quality independent of operation speed. This paper presents a recently developed state of the art rail inspection system which uses advanced ultrasonic and eddy current testing techniques. Testing results are shown in a newly developed so called Glassy-Rail-Diagram which is capable to present data with a fixed resolution independent of inspection speed. T2 - NDE 2009 CY - Tiruchirappalli, India DA - 2009-12-10 KW - Non-destructive testing (NDT) KW - Rail inspection KW - Ultrasound KW - Eddy current KW - Signal processing PY - 2009 SP - 261 EP - 265 AN - OPUS4-20883 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Shokouhi, Parisa A1 - Zoëga, Andreas A1 - Wiggenhauser, Herbert A1 - Fischer, G. T1 - Macro-effect of microcracks on sonic surface wave velocity in concrete under compression T2 - 89th TRB Annual Meeting CY - Washington, D.C., USA DA - 2010-01-10 KW - NDT KW - Microcracking KW - Sonic wave velocity KW - Concrete KW - Load KW - Stress PY - 2010 SP - 1 EP - 17 AN - OPUS4-20942 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Joschko, M. A1 - Reinhold, J. A1 - Barkusky, D. A1 - Wiemer, M. A1 - Remus, R. A1 - Busse, J. A1 - Müller, H.-J. A1 - Kiesel, J. A1 - Gleixner, G. A1 - Illerhaus, Bernhard A1 - Kirchner, M. A1 - Oehley, J. A1 - Gerlach, F. T1 - Wirkung einer organischen Düngung mit Seeschlamm auf sandigem Boden im nordostdeutschen Trockengebiet PY - 2009 SP - 1 EP - 162 CY - Frankfurt/Main AN - OPUS4-20928 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Burkert, Andreas A1 - Burkert, Annette A1 - Fischer, Joachim T1 - Legierungsgehalt oder Oberfläche - Was bestimmt die Beständigkeit nichtrostender Stähle? T2 - 9. Tagung Korrosionsschutz in der maritimen Technik CY - Hamburg, Deutschland DA - 2010-01-27 KW - Nichtrostender Stahl KW - Werkstoffauswahl KW - Dauerhaftigkeit KW - Korrosion PY - 2010 SP - 7 EP - 18 CY - Hamburg AN - OPUS4-20875 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pittner, Andreas A1 - Schwenk, Christopher A1 - Weiß, D. A1 - Rethmeier, Michael T1 - Application of a combined modelling technique to reduce experimental effort - a case study for laser-GMA-hybrid welding T2 - VI. International conference "Beam technologies & laser application" CY - Saint Petersburg, Russia DA - 2009-09-23 PY - 2009 SP - 97 EP - 102 CY - Saint Petersburg, Russia AN - OPUS4-20882 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kreutzbruck, Marc A1 - Thomas, Hans-Martin A1 - Casperson, Ralf A1 - Reimund, Verena A1 - Blome, Mark A1 - Allweins, K. A1 - Lembke, G. T1 - Magnetic response field of spherical defects on non-destructive evaluation T2 - NDE 2009 CY - Tiruchirappalli, India DA - 2009-12-10 KW - Electromagnetic testing KW - Spherical defects KW - Finite element method PY - 2009 SP - 271 EP - 275 AN - OPUS4-20831 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Boehm, Rainer A1 - Brackrock, Daniel A1 - Kitze, Jessica A1 - Brekow, Gerhard A1 - Kreutzbruck, Marc T1 - The SAFT approach for advanced crack analysis T2 - NDE 2009 CY - Tiruchirappalli, India DA - 2009-12-10 PY - 2009 SP - 315 EP - 318 AN - OPUS4-20832 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Taffe, Alexander A1 - Stoppel, Markus A1 - Wiggenhauser, Herbert T1 - Zerstörungsfreie Prüfverfahren im Bauwesen (ZfPBau) T2 - Betoninstandsetzung im Ingenieur- und Wohnungsbau CY - Filderstadt/Stuttgart, Deutschland DA - 2010-03-04 KW - Zerstörungsfreie Prüfung im Bauwesen KW - ZfPBau KW - Radar KW - Ultraschallecho KW - Automatisierung KW - Radiographie KW - OSSCAR KW - BetoScan PY - 2010 SP - 35 EP - 58 AN - OPUS4-20984 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalbe, Ute A1 - Berger, Wolfgang A1 - Sauer, Andreas A1 - Helm, Renate T1 - Validierung von Elutionsverfahren zur Charakterisierung der Quellstärke von Boden- und Abfallmaterialien N2 - Mit der Novellierung der Bundes-Bodenschutzverordnung und der Einführung einer Ersatzbaustoffverordnung soll die ordnungsgemäße und schadlose Verwertung von mineralischen Abfällen im Boden bundeseinheitlich geregelt werden. Dabei sind die Erfordernisse des Boden- und Grundwasserschutzes zu beachten. In einer Reihe von F&E-Vorhaben der letzten Jahre wurden Vorschläge zur Verbesserung und Harmonisierung von Verfahren zur Bewertung des Eintrages von Schadstoffen in Boden und Grundwasser unterbreitet. Im Blickpunkt standen u.a. Elutionsmethoden zur Ermittlung der Quellstärke von schadstoffbelasteten Matrices. Vom DIN-Normenausschuss Wasserwesen, Unterausschuss "Eluierungsverfahren" wurden auf dieser Grundlage zwei Verfahren zur Elution von Bodenmaterialien und mineralischen Abfällen mit einer Korngröße bis 32 mm erarbeitet. Dabei handelt es sich um ein Säulenperkolationsverfahren zur gemeinsamen Untersuchung des Elutionsverhaltens von organischen und anorganischen Stoffen (DIN 19528) und ein Schüttelverfahren mit einem Wasser-/Feststoff-Verhältnis (W/F) von 2 l/kg zur Untersuchung der Elution von anorganischen Stoffen (DIN 19529). Um die Normen in den gesetzlichen Verordnungen zitieren zu können, war deren Validierung erforderlich, womit die BAM durch das UBA/BMU beauftragt wurde (FKZ 370733307). Auf der Grundlage von vier Referenzmaterialien mit anorganischen Schadstoffen und PAK wurden Ringversuchen durchgeführt. Es wurden die Kenndaten insbesondere zu Wiederholbarkeit und Reproduzierbarkeit der beiden Verfahren ermittelt. T2 - Jahrestagung der DBG "Böden - eine endliche Ressource" CY - Bonn, Deutschland DA - 2009-09-05 KW - Elutionsverfahren KW - Boden KW - Ringversuche KW - Validierung PY - 2009 UR - http://eprints.dbges.de/225/ N1 - Geburtsname von Sauer, Andreas: Buchholz, A. - Birth name of Sauer, Andreas: Buchholz, A. N1 - Serientitel: Berichte der DBG – Series title: Berichte der DBG SP - 1 EP - 4 CY - Bonn AN - OPUS4-20977 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, M. A1 - Durmaz, V. A1 - Becker, Roland A1 - Esslinger, Susanne T1 - Predictive identification of Pentabromocyclododecene (PBCD) isomers with high binding affinity to hTTR N2 - The binding affinities of the six main hexabromocyclododecane (HBCD) stereoisomers and all of their possible 48 allylic pentabromocyclododecene (PBCD) metabolites to the endocrinous human transthyretin receptor (hTTR) were investigated and compared to the natural binder thyroxine, and the two brominated diphenyl ethers BDE-47 and 3-hydroxy-BDE-47. The endocrine disrupting potency was approximated by a combination of two methods: a surface matching with the natural binder thyroxine (T4) followed by approximation of free binding energies for various binding modes within hTTR. The results indicate slightly higher binding affinities for both BDE structures than for T4 itself and similarly high affinities for two trans-configurated PBCD isomers. For many other PBCD isomers, intermediate values were computed, whereas all HBCD diastereomers yielded significantly lower binding affinities. T2 - Dioxin 2009 - 29th International symposium on halogenated persistent organic pollutants / Organohalogen compounds CY - Beijing, China DA - 2009-08-23 KW - Flammschutzmittel KW - Thyroxin KW - Molecular modeling PY - 2009 UR - http://www.dioxin20xx.org/pdfs/2009/09-54.pdf VL - 71 SP - 000247 EP - 000252 CY - Beijing, China AN - OPUS4-20980 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völzke, Holger T1 - Qualifikation von Behältern für das Endlager KONRAD T2 - 7. Expertentreffen Strahlenschutz CY - Lindau/Bodensee, Deutschland DA - 2010-03-03 KW - Behälter KW - Sicherheit KW - Endlager KW - Bauartprüfung KW - Radioaktive Abfälle PY - 2010 IS - Register 12 SP - 1 EP - 8 AN - OPUS4-21001 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Beck, Matthias T1 - Zur Entwicklung der Eigenkorrosion von Stahl in Beton N2 - Sicherheit und Dauerhaftigkeit von Stahlbetonbauwerken sind einer der wichtigsten Ansprüche bei der Bemessung von Gebäuden. Normen und Vorschriften beinhalten nur allgemeine Anforderungen an Betonqualität und Betondeckung. In besonders kritischen Fällen, beispielsweise dem Eindringen von Chloriden ist die Applikation von Beschichtungen häufig die einzige Möglichkeit die Bewehrung effektiv vor der Initiierung der Korrosion zu schützen. Im Fall der Depassivierung der Bewehrung ist die Modellierung der Korrosion eine geeignete Methode um eine Lebensdauerbemessung zu gewährleisten. In der Praxis wird die Bewehrung lokal durch in den Beton eingedrungene Chloride depassiviert und es bilden sich an dieser Stelle eng begrenzte, loch und muldenartige anodische Bereiche aus, die kathodischen Bereichen gegenüber stehen. Nach einer Zeit tritt an der Anode ein signifikanter Massenverlust auf, der aufgrund einer anodischen Eisenauflösung infolge eines Stromflusses zwischen anodischen und kathodischen Bereichen verursacht wird. Dabei kann das Flächenverhältnis zwischen anodischen und kathodischen Bereichen in einer Größenordnung von mehreren Dekaden schwanken und wird als Makroelementkorrosion bezeichnet. Die realen Massenverluste, die in der Praxis vorgefunden werden, liegen allerdings of bedeutend höher. Dieser zusätzliche Anteil an Korrosionsabtrag, der nicht auf Makroelementkorrosion zurückzuführen ist, wird als Eigenkorrosion bezeichnet. Dabei handelt es sich um eine zusätzliche Eisenauflösung auf der Anode, die durch die Hydrolyse in den Löchern verursacht wird. Dieser Eigenkorrosionsanteil muss daher bei der Lebensdauerbemessung eines Bauwerkes berücksichtigt werden. Ziel der vorliegenden Arbeit ist daher die Entwicklung der Eigenkorrosion, sowie die Entwicklung der anodischen Bereiche mit Hilfe elektrochemischer Parameter, Massenverluste und der Computertomografie zu beschreiben. Die elektrochemischen Parameter wurden dabei mit üblichen elektrochemischen Methoden aufgezeichnet und in Abhängigkeit von verschiedenen Betonparametern und Klimaten aufgetragen. Abschließend wird die Entwicklung der Eigenkorrosion in Abhängigkeit der verschiedenen Parameter in dieser Arbeit gezeigt und diskutiert. KW - Korrosionsfortschritt KW - Eigenkorrosion KW - Elektrochemische Messungen KW - Freies Korrosionspotential KW - Polarisationswiderstand KW - Abtragsraten KW - Massenverlust KW - Computertomografie PY - 2010 UR - http://darwin.bth.rwth-aachen.de/opus3/volltexte/2010/3148/ SP - 1 EP - 140 AN - OPUS4-21044 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz T1 - Vehicle dynamics and dynamic excitation forces of railway induced ground vibration T2 - 21th International symposium on dynamics of vehicles on roads and tracks CY - Stockholm, Sweden DA - 2009-08-17 PY - 2009 SP - 1 EP - 12 CY - Stockholm, Sweden AN - OPUS4-21088 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Deuerler, F. T1 - Comparison of the resistance to oxidative degradation of polyethylene grades with the test performance behavior of packagings for the transport of dangerous goods T2 - NACE International Corrosion Conference 2010 CY - San Antonio, Texas, USA DA - 2010-03-14 KW - Dangerous goods packagings KW - Polyethylene grades KW - Resistance to oxidative degradation KW - Design type tests KW - FTIR spectroscopy PY - 2010 SP - 10044-1 - 10044-13 AN - OPUS4-21089 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wille, Frank A1 - Droste, Bernhard A1 - Müller, Karsten A1 - Zencker, Uwe T1 - Recent experiences in mechanical design assessment of spent fuel and HLW casks by competent authority in Germany - 10093 T2 - WM2010 Conference CY - Phoenix, Arizona, USA DA - 2010-03-07 KW - Design testing KW - Transport packages KW - Numerical analysis PY - 2010 SP - 1 EP - 10 AN - OPUS4-21106 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Takahashi, K. A1 - Gaal, Mate A1 - Gülle, D. T1 - Data analysis and performance evaluation of japanese dual-sensor systems tested in Croatia KW - Test KW - Dual sensor KW - Landmine detection PY - 2009 UR - http://maic.jmu.edu/JOURNAL/13.3/randd/takahashi_etal/takahashi_etal.htm IS - 13.3 SP - 1 EP - 6 PB - Mine action info center/JMU AN - OPUS4-21110 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Esslinger, Susanne A1 - Becker, Roland A1 - Müller-Belecke, A. A1 - Jung, Christian A1 - Nehls, Irene T1 - Bioisomerization of HBCD: Results of feeding experiments with pure Gamma-HBCD enantiomers N2 - 1,2,5,6,9,10-hexabromocyclododecane (HBCD), a widely used flame retardant, is an ubiquitous contaminant in the environment. Still, only little is known about the distribution and behavior in the environment such as bioaccumulation or biotransformation of HBCD stereoisomers. In order to investigate enrichment and possible bioisomerization of HBCD stereoisomers, Mirror Carps were exposed to pure (+)- and (-)-γ-HBCD, randomly sampled after a predefined specific period and subjected to enantiomer-specific determination of α-, β-, and γ- HBCD. No evidence for the isomerization of HBCD stereoisomers was observed in Mirror Carp fillets. T2 - Dioxin 2009 - 29th International symposium on halogenated persistent organic pollutants / Organohalogen compounds CY - Beijing, China DA - 2009-08-23 PY - 2009 UR - http://www.dioxin20xx.org/pdfs/2009/09-103.pdf VL - 71 SP - 000487 EP - 000492 CY - Beijing, China AN - OPUS4-21187 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kasinathan, Murugesan A1 - Rao, C.B. A1 - Murali, N. A1 - Jayakumar, T. A1 - Raj, B. A1 - Wosniok, Aleksander A1 - Krebber, Katerina T1 - Analysis of stimulated Brillouin scattering characteristics in frequency domain T2 - ICOP 2009 - International conference on optics & photonics CY - Chandigarh, India DA - 2009-10-30 KW - BOFDA KW - Fibre optic sensors KW - Distributed Brillouin sensors KW - Stimulated Brillouin scattering KW - Nonlinear optics PY - 2009 SP - 1 EP - 5(?) AN - OPUS4-21150 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kasinathan, Murugesan A1 - Rao, C.B. A1 - Murali, N. A1 - Jayakumar, T. A1 - Raj, B. A1 - Wosniok, Aleksander A1 - Krebber, Katerina T1 - Use of Brillouin optical time domain analyser in testing of adhesive bonding T2 - SENNET`09 - International conference on sensors and related networks CY - Vellore, India DA - 2009-12-08 KW - Brillouin KW - Frequency domain analysis KW - Time domain analysis KW - Adhesive KW - Bond evaluation KW - Temperature KW - Strain KW - Distributed sensor PY - 2009 SP - 190 EP - 192 CY - Vellore, India AN - OPUS4-21151 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Komann, Steffen A1 - Droste, Bernhard A1 - Wille, Frank T1 - Transport von Großkomponenten aus der Stilllegung kerntechnischer Anlagen - Erfahrungen bei der mechanischen Bewertung T2 - Jahrestagung Kerntechnik 2010 CY - Berlin, Deutschland DA - 2010-05-04 KW - Kerntechnische Anlagen KW - Rückbau KW - Mechanische Bewertung KW - Großkomponenten KW - Numerische Analyse PY - 2010 IS - Sektion 7 / 706 SP - 1 EP - 5 CY - Berlin AN - OPUS4-21239 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wille, Frank A1 - Droste, Bernhard A1 - Zencker, Uwe A1 - Komann, Steffen T1 - Reflektion der verkehrsrechtlichen Bauartprüfung des CASTOR HAW 28M aus Sicht der zuständigen Behörde BAM T2 - Jahrestagung Kerntechnik 2010 CY - Berlin, Deutschland DA - 2010-05-04 KW - Bauartprüfung KW - Fallprüfungen KW - Transportbehälter KW - FEM PY - 2010 SP - 1 EP - 5 CY - Berlin AN - OPUS4-21241 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Mike A1 - Wille, Frank A1 - Ballheimer, Viktor A1 - Musolff, André T1 - Numerische Analyse der 1-m-Fallprüfung auf einen Stahldorn T2 - Jahrestagung Kerntechnik 2010 CY - Berlin, Deutschland DA - 2010-05-04 KW - IAEO KW - 1-m-Fallprüfung KW - Stahldorn KW - Numerische Analyse KW - Verifizierung PY - 2010 IS - Sektion 5 / 505 SP - 1 EP - 5 CY - Berlin AN - OPUS4-21292 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Marotzke, Christian T1 - Influence of the interface on the strength of fiber reinforced polymers N2 - The debonding of fibers under mixed-mode loading is studied on model composites containing fibers with different orientations with respect to the loading direction. The spacing of the fibers is large, accordingly no significant fiber interaction takes place. For any fiber orientation, interfacial debonding occurs, even though at different load levels. Only for the low off-axis angle, additional fiber fracture is found. Using a rectangular specimen, the interface crack starts at the edges propagating into the center at low speed. In the first phase, only the central part of the interface debonds. After the whole fiber is debonded, the crack propagates in circumferential direction. The superimposition of fiber breakage and debonding shows that the restriction of two potential failure planes - perpendicular or parallel to the fibers - has to be put in question. T2 - 14th European conference on composite materials CY - Budapest, Hungary DA - 2010-06-07 KW - Strength KW - Composites KW - Crack propagation PY - 2010 IS - Paper 708-ECCM14 SP - 1 EP - 10 AN - OPUS4-21278 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Marotzke, Christian A1 - Kalinka, Gerhard T1 - Local failure processes in fiber reinforced polymers N2 - The breakage of a fiber and its effect on the strain energy is studied in a model composite, this is, a single fiber embedded in a dogbone specimen. The fracture process is recorded by an acoustic emission device, the crack patterns are monitored under a microscope. A finite element analysis is performed in order to estimate the energy released by different failure scenarios. The abilities and limitations of the acoustic emission analysis in characterizing different failure types in fiber reinforced composites are evaluated. T2 - ICCM17 - 17th International conference on composite materials CY - Edinburgh, UK DA - 2009-07-27 KW - Fiber KW - Interface KW - Composite material KW - Failure KW - Acoustic emission KW - Fracture mechanics KW - Energy release rate KW - Finite element analysis PY - 2009 IS - D7:8 SP - 1 EP - 10 CY - Edinburgh, UK AN - OPUS4-21295 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - de Oliveira, Rui A1 - Schukar, Marcus A1 - Krebber, Katerina A1 - Michaud, V. T1 - Advanced composite materials with embedded POF sensors for structural health monitoring N2 - A long period grating (LPG) mechanically imprinted in a microstructured polymer optical fibre (mPOF) is embedded in a carbon fibre reinforced polymer (CFRP) unidirectional laminate. Processing steps were established in order to ensure that mPOF does not suffer significant degradation. The strain and temperature responses of the embedded mPOF-LPG were then investigated. T2 - POF 2010 - 19th International conference on plastic optical fibers CY - Yokohama, Japan DA - 2010-10-19 PY - 2010 IS - P-25 SP - 1 EP - 4 AN - OPUS4-22381 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Liehr, Sascha A1 - Krebber, Katerina T1 - Quasi-distributed and dynamic length change measurement in polymer optical fibers N2 - We present a novel technique based on the incoherent optical frequency domain reflectometry (l-OFDR) technique for dynamic (2 kHz) and quasi-distributed length change measurement in polymer optical fibers (POF). The extreme strain sensing capabilities (> 125 %) and cyclic load behaviour of perfluorinated POF are investigated using this technique. T2 - POF 2010 - 19th International conference on plastic optical fibers CY - Yokohama, Japan DA - 2010-10-19 PY - 2010 IS - Sensors-2 SP - 1 EP - 4 AN - OPUS4-22382 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kranzmann, Axel A1 - Hünert, Daniela A1 - Rooch, Heidemarie A1 - Urban, Ingrid A1 - Schulz, Wencke A1 - Österle, Werner T1 - Reactions at the interface between steel and oxide scale in wet CO2 containing atmospheres N2 - The resistance of structural steels against corrosion in CO2-H2O and CO2-H2O-O2 atmospheres at temperatures above 550°C was observed with high magnification methods. The test atmosphere is the basic composition of an oxyfuel coal combustion atmosphere. The analytical information base was applied to develop reaction schemes for the oxidation of steels. It was demonstrated that the formation of phases and the kinetics of oxidation reactions in this atmospheres is affected by the formation of intermediate iron hydroxide and a high carbon activity. In the temperature regime above 550°C the thermal equilibrium between H2O, CO2 and Fe reacted and formed CO. CO triggers the formation of FeO and carbides and increases the reaction kinetics. Porosity at the interface is established by gaseous phases such as Fe(OH)2 or H2O. H2 formation is not limited to the steel - oxide interface but can occur in the whole oxide scale. Examples of the experimental results were compared with a thermodynamic approach. The objective of the work was to derive qualitative rules of the basic corrosion reactions. T2 - NACE International corrosion conference 2009 CY - Atlanta, Georgia, USA DA - 2009-03-22 KW - High temperature corrosion KW - Corrosion gases KW - Mild steels KW - 9-12% Cr-steels KW - Hydrogen transport KW - Oxyfuel combustion PY - 2009 SP - 1 EP - 10 (Paper 09265) AN - OPUS4-22334 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Liehr, Sascha A1 - Wendt, Mario A1 - Krebber, Katerina T1 - Distributed strain and length change measurement in POF using optical frequency domain reflectometry N2 - We show that the incoherent optical frequency domain (l-OFDR) technique provides superior performance compared to standard OTDR techniques in terms of spatial resolution and measurement time. The distributed strain measurement capabilities of perfluorinated POF up 100 % strain are shown and distributed length change measurement using correlation techniques and OFDR are presented. T2 - POF 2010 - 19th International conference on plastic optical fibers CY - Yokohama, Japan DA - 2010-10-19 PY - 2010 IS - Sensors-2 SP - 1 EP - 4 AN - OPUS4-22383 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bredow, Andrea A1 - Berger, Wolfgang A1 - Erdmann, Kerstin T1 - Nassmechanische Aufbereitung von Photovoltaik-Dünnschichtmodulen mittels Flotation T2 - Jahrestagung Aufbereitung und Recycling CY - Freiberg/Sa., Deutschland DA - 2010-11-10 PY - 2010 N1 - Geburtsname von Erdmann, Kerstin: Meißner, K. - Birth name of Erdmann, Kerstin: Meißner, K. SP - 13 EP - 14 AN - OPUS4-22389 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krebber, Katerina A1 - Lenke, Philipp A1 - Liehr, Sascha A1 - Schukar, Marcus A1 - Wendt, Mario A1 - Witt, Jens T1 - Distributed POF sensors - recent progress and new challenges N2 - The potential of the use of POF as distributed sensors in several application fields has been successfully demonstrated. The distributed POF sensors have moved from the laboratory to the field. The paper presents the recent progress in the development of distributed POF sensors and addresses the main challenges to this innovative technology. T2 - POF 2010 - 19th International conference on plastic optical fibers CY - Yokohama, Japan DA - 2010-10-19 PY - 2010 IS - Sensors-2 SP - 1 EP - 4 AN - OPUS4-22305 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Voland, Katja T1 - Neueste Technik für bessere Autobahnen - Innovative Prüftechnik zur Verfolgung von Schädigungsprozessen infolge AKR T2 - 51. DAfStb-Forschungskolloquium CY - Kaiserslautern, Deutschland DA - 2010-11-11 KW - Alkali-Kieselsäure-Reaktion KW - Nebelkammer KW - 60 °C-Betonversuch KW - Schallemissionsanalyse KW - Ultraschallgeschwindigkeit KW - µ-3D-CT PY - 2010 VL - 2 IS - Kap. C2 SP - 637 EP - 648 AN - OPUS4-22437 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mishra, Kirti Bhushan A1 - Wehrstedt, Klaus-Dieter A1 - Schönbucher, A. T1 - Safety aspects of organic peroxide pool fires T2 - COMBURA 2010 - Combustion research and application CY - Maastricht, The Netherlands DA - 2010-10-12 KW - Pool fire KW - Organic peroxides KW - TBPB KW - TBPEH KW - CFD KW - Safety distances PY - 2010 SP - 11 EP - 12 AN - OPUS4-22484 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beckmann, Jörg A1 - Zscherpel, Uwe A1 - Ewert, Uwe A1 - Skerik, M. T1 - Image Quality Assessment of CR Systems N2 - Computed Radiography exposure experiments on welded plate sections were performed to demonstrate that the requirements for pressure vessels weld inspection according to EN1435 or EN14784-2 class B can be achieved. The representative comparative studies of the image qualities were performed with standardized image quality indicators and image evaluation procedures on both film and digital radiographs. Recommendations for weld inspections with CR systems are drawn from the results. It is demonstrated that present CR systems can be used for weld inspection and produce images with testing class B if the selected X-ray tube voltage is reduced compared with the max. voltage of EN 14784-2 and set equivalent to maximum X-ray voltage values for steel as defined in the radioscopic standard EN 13068-3. The work was part of the European 'Filmfree' Project promoted during the 6’th framework. T2 - 10th European conference on non-destructive testing CY - Moscow, Russia DA - 2010-06-07 KW - Film KW - Digital radiography KW - Computed radiography KW - Image quality PY - 2010 UR - http://www.ndt.net/article/ecndt2010/reports/1_04_07.pdf IS - Paper 4.02.18 SP - 1 EP - 10 AN - OPUS4-22536 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe A1 - Ainsworth, R. A. A1 - Madia, Mauro T1 - Grenzlast oder Referenzlast? - Vorschlag für eine hybride Vorgehensweise bei der elastisch-plastischen Bauteilbewertung T2 - 42. Tagung des DVM-Arbeitskreises Bruchvorgänge - Bruchmechanische Werkstoff- und Bauteilbewertung: Beanspruchungsanalyse, Prüfmethoden und Anwendungen CY - Paderborn, Deutschland DA - 2010-02-23 KW - Bruchmechanische Bauteilbewertung KW - EPRI-Methode KW - Referenzspannungsmethode KW - R6-Routine KW - SINTAP KW - FITNET KW - FKM-Richtlinie KW - Grenzlast KW - Referenzlast PY - 2010 SP - 183 EP - 194 AN - OPUS4-22493 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hünert, Daniela A1 - Schulz, Wencke A1 - Kranzmann, Axel T1 - Simultaneous oxidation and carburization under oxyfuel conditions N2 - The combustion of coal in CO2-reduced Oxyfuel power plants requires creep resistant and corrosion resistant materials, which can withstand high temperatures up to 600°C and CO2 rich atmospheres. Among the heat resistant materials, the 9-12% chromium steels are proven to resist high wall temperatures in conventional power plants and are suitable as membrane wall, superheaters and steam piping. During Oxyfuel combustion a flue gas is generated, which consists mainly of H2O (30 mol %) and CO2 (70 mol %). The present paper is focused on the corrosion of 9-12% chromium steels under oxyfuel conditions in a temperature range between 550 and 625°C. Depending on Chromium content of the 9-12%chromium steels, carburization of the base material, perlite formation and carbide formation were observed. Alloys with lower chromium content form a non protective oxide scale with perlite at the scale-alloy interface. Steels with 12% chromium have a small growing oxide scale with enlarged M23C6-particles at the scale-alloy interface. The carburization of the base material is found to be increased for the 9% Cr-steel. Higher pressure of the flue gas results in the formation of less resistant scales and cause accelerated carburization of the base materials. However, the carburization has an impact on the mechanical properties at the surface and leads to an embrittlement, which is deleterious during thermal cycling. Oxidation kinetics, phase analysis of the scale (transmission electron microscope) and carburization depths (microprobe) of the base materials are presented. T2 - EUROCORR 2009 CY - Nice, France DA - 2009-09-06 KW - High-temperature corrosion KW - Carburization KW - 9-12 % Cr-steel KW - M23C6-particles KW - Power plant steels PY - 2010 IS - Paper 7805 SP - 1 EP - 11 AN - OPUS4-22500 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Oliveira, D.F. A1 - Moreira, E.V. A1 - Silva, A.S.S. A1 - Rabello, J.M.B. A1 - Lopes, R.T. A1 - Pereira, M.S. A1 - Zscherpel, Uwe T1 - Application of the digital radiography in weld inspection of gas and oil pipelines N2 - The aim of this work is to evaluate the feasibility of the direct radiography on weld inspection in oil pipelines and gas pipeline during the manufacturing process. To that, 6 specimens with 6 different thickness and varied height of reinforced weld with 5 different kinds of defects were made. All samples were radiographied using Class I films and flat panel. For all specimens the inspection length was 8''. Thus, with the flat panel the detector-to-object distance varied so that it may adequate to several diameters of the tubes. The detector-to-object distance was calculated based on the physical size of the detector taking into consideration a safe distance between the tube curvature and the flat panel extremities, keeping the lowest possible magnification factor so that it could be obtained the length of the inspection. Images with 6 integration time for each experimental arrangement were obtained. The images obtained with the Flat Panel/YXLON system were analyzed according to their quality by using the Contrast parameters (essential wire) (DNV 2007/ IS0 12096 – with reinforcement and ISO 10893-7 – basis material), Basic Spatial Resolution – BSR (ISO 10893-7) and normalized signal-to-noise ratio - SNRN (ISO 10893-7) and by detectability using as reference the conventional radiography. The results showed that for all thickness, the exposure time used to meet the image quality requirements were below with direct radiography. However the BSR were not reached for thickness of 4.85, 6.40 and 9.67 mm, therefore the compensation principle established by ISO 10893-7 was considered, that is, one more contrast wire for a less wire pair. The digital technique proved to be more sensitive to real defects found on welds than the conventional technique. Then it can be conclude that the digital radiography utilizing the flat panel can be applicable to the oil and gas segment with advantages over conventional technique as to quality aspects, productivity, environment, safety and health. T2 - 10th European conference on non-destructive testing CY - Moscow, Russia DA - 2010-06-07 KW - Zerstörungsfreie Prüfung KW - Durchstrahlungsprüfung KW - Digitale Radiologie PY - 2010 UR - http://www.ndt.net/article/ecndt2010/reports/1_04_01.pdf IS - Paper 4.02.18 SP - 1 EP - 11(?) AN - OPUS4-22502 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bletzer, Claus W. A1 - Zencker, Uwe A1 - Völzke, Holger A1 - Nehrig, Marko T1 - Strategien zur Bestimmung von Temperaturen von Transport- und Lagerbehältern für radioaktive Stoffe T2 - Jahrestagung Kerntechnik 2010 CY - Berlin, Deutschland DA - 2010-05-04 KW - Temperaturprofil KW - Transportbehälter KW - Radioaktive Stoffe PY - 2010 IS - Section 5 / Paper 514 SP - 1 EP - 6 CY - Berlin AN - OPUS4-22604 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Österle, Werner A1 - Bresch, Harald A1 - Dörfel, Ilona A1 - Fink, C. A1 - Giese, A. A1 - Prietzel, Claudia A1 - Seeger, Stefan A1 - Walter, J. T1 - Examination of airborne brake dust T2 - JEF 2010 - 6th European conference on braking CY - Lille, France DA - 2010-11-24 KW - Brake dust KW - Nanoparticles KW - Size-distribution PY - 2010 SP - 1 EP - 6(?) AN - OPUS4-22655 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dmitriev, A.I. A1 - Österle, Werner A1 - Kloß, Heinz T1 - Nano-scale modeling of pad-disc interface. The influence of copper as a pad ingredient. T2 - JEF 2010 - 6th European conference on braking CY - Lille, France DA - 2010-11-24 KW - Friction layer KW - Copper particles KW - MCA-modelling PY - 2010 SP - 1 EP - 6(?) AN - OPUS4-22656 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schwenk, D. A1 - Subaric-Leitis, Andreas ED - Pohl, M. T1 - Qualitätskennzahlen bei der Prüfung und Kalibrierung von Werkstoffprüfmaschinen T2 - DGM-Tagung Werkstoffprüfung 2010 CY - Neu-Ulm, Deutschland DA - 2010-12-02 KW - Spannweite KW - Standardabweichung KW - Materialprüfmaschine PY - 2010 SP - 275 EP - 280 AN - OPUS4-22700 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hauswaldt, Sebastian A1 - Korzen, Manfred T1 - A constitutive model for use in finite element simulations in structural fire design T2 - 11th International symposium on fire protection CY - Leipzig, Germany DA - 2010-06-08 KW - Steel KW - Fire KW - Constitutive model KW - Eurocode KW - Creep KW - Finite element simulation KW - ABAQUS KW - UMAT KW - Deformation theory of plasticity PY - 2010 SP - 1 EP - 9(?) AN - OPUS4-22683 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lenke, Philipp A1 - Wendt, Mario A1 - Liehr, Sascha A1 - Krebber, Katerina T1 - The impact of temperature and humidity on the backscatter profile of PMMA POF N2 - In this paper the influence of combined temperature and strain changes as well as changes of moisture content on polymer optical fibers made of polymethyl methacrylat (PMMA) is investigated. The increase of the scattering coefficient with increasing temperature for various strain levels is observed and quantified. The measurement results of influence of humidity on scattering intensity of PMMA-POF encourage to porpose these as a distributed humidity sensor. T2 - POF 2010 - 19th International conference on plastic optical fibers CY - Yokohama, Japan DA - 2010-10-19 KW - POF distributed sensing Rayleigh KW - Humiditiy KW - OTDR KW - Strain PY - 2010 SP - 1 EP - 7(?) AN - OPUS4-22685 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz, Michael T1 - On the creep rupture prediction of composite pressure vessels N2 - This article illustrates a concept of predicting the time dependent deformation and creep rupture strength of carbon fibre reinforced plastics (CFRP). In the presented concept the viscoelastic behaviour of the resin is determined by creep rupture tests at different temperature and load levels. Out of the experiments the relaxation spectrum of the resin is modelled including the spread. With the help of the classical rule of mixture and a modified classical laminate theory the minimum strain rate for the composite will be determined. The results will be compared to experimental data. Furthermore the Monkman-Grant approach is used to determine the time-to-failure strain-rate relation. Therefore an elastic solution of the classical laminate theory is used including Puck´s failure criteria to compute the Monkman-Grant relation. A Monte Carlo Simulation will be done to include the spread of the Monkman-Grant relation. The results will be compared to experimental results of unidirectional specimens. Finally it will be explained how the lifetime of a pressure vessel can be computed using the explained concept. T2 - ASME 2010 Pressure vessels & piping conference CY - Bellevue, Washington, USA DA - 2010-07-18 PY - 2010 IS - PVP2010-26034 SP - 1 EP - 11 PB - American Society of Mechanical Engineers CY - New York AN - OPUS4-22725 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Cristol, A.L. A1 - Desplanques, Y. A1 - Österle, Werner A1 - Degallaix, G. T1 - Coupling between thermal localisation and friction mechanisms: heat accumulation effect N2 - Heat accumulation induced by a succession of railway brakings leads to changes of the friction conditions occurring in pad-disc contact. Infrared thermography observations show a progressive increase of surface temperature over the succession, as well as a modification of the hot band migration phenomenon. From a tribological point of view, the heat accumulation, accompanied by a wear increase, progressively modifies the friction behaviour from one braking to the next. Post-mortem observations of pads are performed on surface by scanning electron microscopy and in depth after Focus Ion Beam cut by scanning ion microscopy. Observations show that, with heat accumulation, the third body quantity rises inside the contact, in accordance with wear increase. It is concluded that source flows of third body, which increase with temperature, feed aplenty the contact and modify its load-bearing capacity. T2 - JEF 2010 - 6th European conference on braking CY - Lille, France DA - 2010-11-24 KW - Successive braking KW - Heat accumulation KW - Thermal localisation KW - Wear KW - SEM KW - FIB PY - 2010 SP - 61 EP - 69 AN - OPUS4-22729 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Plarre, Rüdiger T1 - Material- und Vorratsschädlinge, ihre Anpassungen an den synanthropen Lebensraum sowie ihre wirtschaftliche Relevanz einschließlich ihrer Bekämpfung KW - Materialschutz KW - Insekten KW - Anpassung KW - Evolution KW - Bekämpfungsstrategien PY - 2009 N1 - Sprachen: Deutsch/Englisch - Languages: German/English SP - 1 EP - 62, Anhang CY - Berlin AN - OPUS4-22836 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Madia, Mauro A1 - Riesch-Oppermann, H. A1 - Zerbst, Uwe A1 - Beretta, S. T1 - Ein Konzept für die probabilistische bruchmechanische Bauteilbewertung T2 - 42. Tagung des DVM-Arbeitskreises Bruchvorgänge - Bruchmechanische Werkstoff- und Bauteilbewertung: Beanspruchungsanalyse, Prüfmethoden und Anwendungen CY - Paderborn, Deutschland DA - 2010-02-23 KW - Bruchmechanische Bauteilbewertung KW - SINTAP KW - FITNET KW - Zuverlässigkeit KW - FORM/SORM PY - 2010 SP - 51 EP - 60 AN - OPUS4-22837 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krietsch, Arne A1 - Scheid, Marc T1 - Tests on suitability of a new pyrotechnical igniter for the determination of explosion characteristics of dust clouds in 20-L-sphere and 1-m³-vessel T2 - 8th ISHPMIE - International symposium on hazards, prevention, and mitigation of industrial explosions CY - Yokohama, Japan DA - 2010-09-05 KW - Explosion characteristics of dusts KW - 20-L-sphere KW - 1-m³-vessel KW - Pyrotechnical igniter KW - Dust explosion testing PY - 2010 IS - ISH021 SP - 1 EP - 9 AN - OPUS4-22760 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaenisch, Gerd-Rüdiger A1 - Ewert, Uwe A1 - Jechow, Mirko T1 - Scatter radiation in radiography T2 - 10th European conference on non-destructive testing CY - Moscow, Russia DA - 2010-06-07 KW - Simulation KW - Streustrahlung KW - Abbildungskontrast KW - Bildqualität PY - 2010 IS - Paper 4.02.18 SP - 1 EP - 9 AN - OPUS4-22765 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Musolff, André A1 - Droste, Bernhard A1 - Quercetti, Thomas A1 - Müller, Karsten T1 - Durchführung experimenteller Fallprüfungen im Rahmen der mechanischen Bauartprüfung von Transportbehältern für radioaktive Stoffe T2 - Jahrestagung Kerntechnik 2010 CY - Berlin, Deutschland DA - 2010-05-04 PY - 2010 SP - 1 EP - 7 CY - Berlin AN - OPUS4-22770 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Musolff, André A1 - Quercetti, Thomas A1 - Müller, Karsten A1 - Droste, Bernhard A1 - Komann, Steffen T1 - Drop test program with the half-scale model CASTOR HAW/TB2 T2 - PATRAM 2010 - 16th International symposium on the packaging and transport of radioactive materials CY - London, UK DA - 2010-10-03 KW - Spent fuel transport cask KW - Drop test KW - Impact limiter KW - Measurement procedure PY - 2010 SP - 1 EP - 8 AN - OPUS4-22771 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nehrig, Marko A1 - Wille, Frank A1 - Quercetti, Thomas A1 - Masslowski, Jörg-Peter A1 - Droste, Bernhard A1 - Pope, R. T1 - Historical view and experiences with the crush test for light weight packages T2 - PATRAM 2010 - 16th International symposium on the packaging and transport of radioactive materials CY - London, UK DA - 2010-10-03 KW - Crush test KW - IAEA regulations KW - Type-B PY - 2010 SP - 1 EP - 8(?) AN - OPUS4-23303 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, A. A1 - Linke, B. A1 - Schulz, Sabrina A1 - Kranzmann, Axel T1 - CO2-corrosion of steels exposed to saline water environment N2 - With CO2 being one reason for climate change carbon capture and storage (CCS) is discussed to mitigate climate change. When emission gases are compressed into deep geological layers CO2-corrosion can easily cause failure of injection pipes. Different steels 42CrMo4, X46Cr13 and X20Cr13 were tested as well as X35CrMo17 and X5CrNiCuNb16-4 in a laboratory Environment similar to the conditions of the CCS engineering site at the Northern German Bassin. Samples were exposed to synthetic aquifer water saturated with technical CO2 at a flow rate of 3 NL/h. Corrosion rates obtained via mass loss vary in a wide range (0,005 to 2.5 mm/year). The precipitations within the corrosion scale revealed a complicated multiphase layer containing siderite FeCO3, goethite α-FeOOH, lepidocrocite γ-FeOOH, mackinawite FeS and akaganeite Fe8O8(OH)8Cl1,34 and spinelphases of various compositions. T2 - TMS 2011 - 140th Annual Meeting & Exhibition CY - San Diego, CA, USA DA - 27.02.2011 KW - CCS KW - Steel KW - Corrosion KW - Carbon Capture and Storage PY - 2011 DO - https://doi.org/10.1002/9781118062173.ch102 VL - 3 IS - 0807 SP - 807 EP - 814 AN - OPUS4-23472 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sarmiento Klapper, Helmuth A1 - Heyn, Andreas A1 - Goellner, J. T1 - La técnica de ruido electroquímico para la investigación de la corrosión localizada: del fenómeno a la aplicación N2 - En los últimos anos el registro y análisis del ruido electroquímico ha posibilitado importantes avances en la investigación de fenómenos de corrosión localizada tales como el picado y la corrosión en rendijas. Así mismo, esta técnica a abierto enormes posibilidades para el monitoreo in situ de tales procesos corrosivos en la industria. Sin ninguna duda, la posibilidad de registrar en tiempo real y con extrema sensibilidad los procesos de nucleación de la corrosión localizada, hace de la técnica de ruido electroquímico una invaluable herramienta para alcanzar una mejor comprensión de su origen y propagación. A continuación se discutirán las fuentes de ruido electroquímico relacionadas con la corrosión localizada así como los avances alcanzados para una confiable adquisición y análisis de la información electroquímica suministrada por las senales de ruido electroquímico y se ilustrarán con ejemplos prácticos las ventajas de la técnica de ruido electroquímico para la evaluación de la corrosión localizada. KW - Ruido electroquímico KW - Corrosión localizada KW - Acero inoxidable KW - Aluminio KW - Elektrochemisches Rauschen KW - Korrosion KW - Passivität KW - Lochkorrosion PY - 2010 IS - November SP - 28 EP - 30 CY - Houston, TX, USA AN - OPUS4-23398 LA - spa AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Günther, U. A1 - Baden, M. A1 - Komann, Steffen A1 - Nitz, Thilo T1 - Performance and restrictions of non-destructive testing (NDT) within the quality surveillance during manufacturing of type B-packages T2 - PATRAM 2010 - 16th International symposium on the packaging and transport of radioactive materials CY - London, UK DA - 2010-10-03 KW - Mechanische Bewertung KW - Radioaktives Material KW - Numerische Analyse KW - Qualitätsüberwachung PY - 2010 SP - 1 EP - 8 AN - OPUS4-23675 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wloka, Monika T1 - Neue Norm für Produktzertifizierungsstellen N2 - Die öffentliche Kommentierung des Entwurfs der ISO/IEC 17065 steht bevor. Die neue Norm wird die DIN EN 45011 und den ISO/IEC Guide 65 ersetzen. KW - DAkkS KW - Norm KW - ISO KW - DIN KW - Akkreditierung KW - Zertifizierungsstellen KW - Produkte PY - 2011 VL - 1 SP - 5 AN - OPUS4-23670 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Qiao, Linan A1 - Zencker, Uwe A1 - Wille, Frank A1 - Musolff, André T1 - Numerical simulation of 9 meter drop of a transport and storage cask with aluminium impact limiter N2 - For the purpose of numerical simulation of 9 meter drop of a transport and storage cask with aluminium impact limiter, an elastic-incremental plastic material model with strain rate hardening acc. to Cowper-Symonds is used for the development of isothermal as well as adiabatic stress-strain relations of aluminium from the compression test at constant ambient temperature. After that, two different simulation strategies are compared. At first, the drop test is calculated fully coupled, i.e. with isothermal stress-strain relations and possible heat generation in the material. Then the drop test is recalculated in a very simplified manner with adiabatic stress-strain relations from the compression test in an isothermal simulation. Both calculation strategies show similar results in the investigated load scenario. T2 - PATRAM 2010 - 16th International symposium on the packaging and transport of radioactive materials CY - London, UK DA - 2010-10-03 KW - Drop test KW - Spent fuel transport cask KW - Finite element calculation KW - Dynamic simulation KW - Impact limiter KW - Aluminium PY - 2010 SP - 1-8 (Monday-T16-117) AN - OPUS4-23707 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kasparek, Eva Maria A1 - Scheidemann, Robert A1 - Zencker, Uwe A1 - Wolff, Dietmar A1 - Völzke, Holger T1 - Effect of dynamic loading on compressional behavior of damping concrete N2 - In drop test scenarios related to assessing and licensing the storage procedure of spent fuel and high active waste, the casks under examination are generally not equipped with impact limiters. Hence, the extent of mechanical stresses in case of an assumed handling accident is largely affected by the ground properties of the reception hall floor in the specific storage facility. Unlike conventional brittle foundation materials, damping concrete performs quite well in such applications as it features high stiffness as well as high energy absorption due to the filler pore volume. However, its damping ability is not sufficiently exploited in current finite element (FE) calculations due to a lack of advanced material models for simulating its impact response. An implementation of qualified concepts that account for plastic, strain rate dependent behavior requires additional information that has to be provided by systematic test series. BAM recently started a research project to generate such data, subsequently to develop and to improve numerical methods for the analysis of impact limiters and damping foundation material and thus to optimize safety assessment tools for the design of transport and storage casks. A major part of this research concerns dynamic compression tests of variably shaped specimens conducted at a servo hydraulic 1MN impact testing machine as well as at a BAM facility for guided drop tests. This presentation focuses 100mm damping concrete cubes deformed vertically at constant rates under different constraint conditions. For example, a special fitting jig was constructed to subject the specimens to multi-axial loading. Thereby a deformation of 60% could be applied. Simulation was conducted by FE code ABAQUS™ based on material models “Concrete damaged plasticity” and “Crushable foam” which both allow defining rate sensitive nonlinear stress-strain relations in compression beyond the classic metal plasticity approach. T2 - PATRAM 2010 - 16th International symposium on the packaging and transport of radioactive materials CY - London, UK DA - 2010-10-03 KW - Damping concrete KW - Strain rate sensitivity KW - Numerical simulation KW - Material model PY - 2010 SP - 1-8 (Thursday-T40-114) AN - OPUS4-23708 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kasparek, Eva Maria A1 - Völzke, Holger A1 - Scheidemann, Robert A1 - Zencker, Uwe A1 - Wolff, Dietmar T1 - Experimentelle und numerische Untersuchungen von stoßdämpfenden Werkstoffen für Behälter zur Entsorgung radioaktiver Stoffe N2 - Die mechanische Beanspruchung von Transport- und Lagerbehältern für radioaktive Stoffe gemäß den durch die IAEA vorgegebenen Prüfszenarien oder bei Unfällen, die während der Handhabung in einer kerntechnischen Anlage auftreten können, wird maßgeblich durch das Design der Stoßdämpfer und die Eigenschaften des jeweiligen Untergrundes beeinflusst. Da der Nachweis der Behälterintegrität und -dichtheit häufig an numerische Simulationen gekoppelt ist, sind für die sicherheitstechnische Auslegung der Konstruktion zuverlässige Informationen über das Energieabsorptionsvermögen der Werkstoffe und eine geeignete Umsetzung dieser Daten in FEM - Programme erforderlich. Die im Rahmen von Falluntersuchungen bei der BAM festgestellten, teilweise erheblichen Abweichungen zwischen experimentellen und berechneten Größen sind entsprechend darauf zurückzuführen, dass die zur Verfügung stehenden numerischen Verfahren das komplexe Verhalten der stoßdämpfenden Strukturen nicht ausreichend präzise wiedergeben. Hiervon besonders betroffen sind Bauteile aus Holz und Polyurethan-Schaum (PU-Schaum), die zur Konstruktion von Behälterstoßdämpfern für die Transportkonfiguration eingesetzt werden, sowie Dämpferbeton, der in ausgewählten Bereichen im Fundament von Standort-Zwischenlagern eingebaut wird. Um die zugehörigen Materialmodelle weiter zu entwickeln und die dafür erforderliche Datenbasis zu schaffen, hat die BAM vor knapp zwei Jahren das vom BMBF geförderte Forschungsvorhaben ENREA (Entwicklung rechnerischer Analysemethoden für stoßdämpfende Strukturen beim Anprall oder Absturz von Abfallgebinden) gestartet. Wesentlicher Bestandteil ist ein systematisches Versuchsprogramm, bei dem die drei genannten Werkstoffe statisch und dynamisch hohen Druckbelastungen ausgesetzt werden. Relevante Versuchsparameter sind, neben der Dehnrate, die Temperatur und Lagerungsbedingungen sowie die Orientierung des Werkstoffes hinsichtlich der Belastungsrichtung. Dieser Beitrag präsentiert die wichtigsten Ergebnisse aus der ersten Versuchsphase, die durch weggesteuerte Versuche mit konstanten Prüfgeschwindigkeiten von 0,02 mm/s und 3000 mm/s gekennzeichnet ist. Darüber hinaus wird die Verwertung dieser Daten zur Anpassung von Materialmodellen auf der Grundlage von Nachrechnungen gezeigt, wobei die Möglichkeiten und Grenzen der verwendeten Konzepte Umrissen werden. Aufgrund des Umfangs, den die Versuche mit Holzwerkstoffen einnehmen, und des erforderlichen Aufwandes für die numerische Modellierung werden die entsprechenden Maßnahmen und Ergebnisse in einem eigenständigen Beitrag auf der KONTEC vorgestellt. T2 - KONTEC 2011 - 10. Internationales Symposium "Konditionierung radioaktiver Betriebs- und Stilllegungsabfälle" CY - Dresden, Germany DA - 06.04.2011 KW - Stoßdämpfende Werkstoffe KW - Materialmodellierung KW - Versuchsprogramm KW - Stoßbelastung KW - Dehnratenabhängigkeit KW - Temperaturabhängigkeit KW - Polyurethan Schaum KW - Dämpferbeton PY - 2011 SP - 453 EP - 458 AN - OPUS4-23709 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rücker, Werner A1 - Rohrmann, Rolf A1 - Fritzen, C.-P. A1 - Trappe, Volker A1 - Habel, Wolfgang T1 - Results and experiences from the research project IMO-WIND N2 - Following a modular concept an integrated monitoring system has been developed that includes all components of offshore wind turbines (OWEC). Using commercially available measurement equipments of the involved partners this system was tested at the wind turbine Multibrid M5000_2 in Bremerhaven. Additional results of the research project are findings on the use of embedded FBG sensors in rotor blades that allow condition assessments based on local information. Newly developed algorithms for the identification of external loads and damage characteristics of the structural components have been tested in operation. Developed methods for monitoring based structural assessment were used, which will be suitable to optimize structural maintenance works. T2 - DEWEK 2010 - 10th German wind energy conference CY - Bremen, Germany DA - 2010-11-17 KW - Offshore wind turbines KW - Integrated monitoring system KW - Data management KW - Design verification KW - Structural assessment KW - Limit values KW - Load identification KW - Data analysis KW - Damage identification KW - Rotor blades KW - Embedded sensors PY - 2010 IS - P11.8 SP - 1 EP - 4 PB - DEWI GmbH AN - OPUS4-23714 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Häcker, Ralf A1 - Knothe, Esther A1 - Andrieux, F. A1 - Memhard, D. T1 - Entwicklung und Verifikation von Materialmodellen und numerischen Methoden zur Vorhersage der Containment Sicherheit beim Bersten von Laufrädern in Abgasturboladern (ATL) T2 - Informationstagung Turbomaschinen 2009 CY - Dresden, Deutschland DA - 2009-10-22 KW - Abgasturbolader KW - Containmentsicherheit PY - 2009 IS - R548 SP - 133 EP - 157 AN - OPUS4-23164 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Esslinger, Susanne A1 - Becker, Roland A1 - Jung, Christian A1 - Schröter-Kermani, C. A1 - Nehls, Irene T1 - Time courses of HBCD levels and enantiomeric signatures in herring gull eggs from the German coast T2 - Dioxin 2010 - 30th International symposium on halogenated persistent organic pollutants CY - San Antonio, TX, USA DA - 2010-09-12 PY - 2010 UR - http://www.dioxin20xx.org/pdfs/2010/10-1112.pdf N1 - Serientitel: Organohalogen Compounds – Series title: Organohalogen Compounds VL - 72 SP - 255 EP - 258 AN - OPUS4-23167 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Esslinger, Susanne A1 - Becker, Roland A1 - Nehls, Irene T1 - HBCD isomers: degradation rates and hydroxylated products from microsome incubation experiments T2 - Dioxin 2010 - 30th International symposium on halogenated persistent organic pollutants CY - San Antonio, TX, USA DA - 2010-09-12 PY - 2010 UR - http://www.dioxin20xx.org/pdfs/2010/10-1113.pdf N1 - Serientitel: Organohalogen Compounds – Series title: Organohalogen Compounds VL - 72 SP - 259 EP - 262 AN - OPUS4-23168 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hönig, D. A1 - Schneider, S. A1 - Domnick, R. A1 - Belzner, M. A1 - Beck, Uwe A1 - Hertwig, Andreas A1 - Stephanowitz, Ralph A1 - Weise, Matthias ED - Uhlmann, E. T1 - Ellipsometrische Codierung & Fabry-Perot Schichtsysteme mit offenen, versteckten und forensischen Merkmalen zur Produkt-Authentifizierung T2 - 3. Internationaler Kongress - Sichere Identität CY - Berlin, Deutschland DA - 2011-04-05 KW - Ellipsometric encoding KW - Fabry-Perot layer stacks KW - Product authentification PY - 2011 SP - 1 EP - 4(?) CY - Berlin AN - OPUS4-23306 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mehdianpour, Milad A1 - Schmid, Wolfgang A1 - Clobes, M. T1 - MOSYTRAF - Monitoringsystem zur Tragverhaltensstudie von Freileitungen unter Böenbeanspruchung N2 - MOSYTRAF steht für ein Monitoringsystem zur Tragverhaltensstudie von Freileitungen unter Böenbeanspruchung. Die Tragverhaltensstudie dient der Entwicklung eines realitätsnahen Berechnungsmodells zur Abschätzung der Mastbeanspruchung infolge Starkwindeinwirkung auf die Leiter. T2 - Messen im Bauwesen 2011 CY - Berlin, Germany DA - 01.03.2011 KW - Monitoring KW - Freileitungen KW - Wind KW - Naturmessung PY - 2011 SP - 89 EP - 100 AN - OPUS4-23331 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mermillod-Blondin, A. A1 - Mauclair, C. A1 - Rosenfeld, A. A1 - Bonse, Jörn A1 - Stoian, R. A1 - Audouard, E. T1 - Time-resolved imaging of bulk a-SiO2 upon various ultrashort excitation sequences N2 - Ultrashort pulses lasers are tools of choice for functionalizing the bulk of transparent materials. In particular, direct photoinscription of simple photonic functions have been demonstrated. Those elementary functions rely on the local refractive index change induced when focusing an ultrashort pulse in the volume of a transparent material. The range of possibilities offered by direct photoinscription is still under investigation. To help understanding, optimizing and assessing the full potential of this method, we developed a time-resolved phase contrast microscopy setup. The imaginary part (absorption) and the real part of the laser-induced complex refractive index can be visualized in the irradiated region. The setup is based on a commercially available phase contrast microscope extended into a pump-probe scheme. The originality of our approach is that the illumination is performed by using a pulsed laser source (i.e. a probe beam). Speckle-related issues are solved by employing adequate sets of diffusers. This laser-microscopy technique has a spatial resolution of 650 nm, and the impulse response is about 300 fs. The laser-induced refractive index changes can be tracked up to milliseconds after the energy deposition. The excitation beam (the pump) is focused with a microscope objective (numerical aperture of 0.45) into the bulk of an a-SiO2 sample. The pump beam can be temporally shaped with a SLM-based pulse shaping unit. This additional degree of flexibility allows for observing different interaction regimes. For instance, bulk material processing with femtosecond and picosecond duration pulses will be studied. T2 - Photonics West 2011 CY - San Francisco, CA, USA DA - 22.01.2011 PY - 2011 DO - https://doi.org/10.1117/12.876687 VL - 7925 IS - 79250R SP - 1 EP - 7 AN - OPUS4-23332 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Deuerler, F. T1 - Comparison of the notched impact strength at -30°C of polyethylene grades with the test performance behavior of packagings for the transport of dangerous goods N2 - The notched impact strength at -30 °C is one of the selected properties, together with the corresponding test method and tolerances, for a comparison of polyethylene grades of one design type in the procedural rule on suitability proof for alternative plastic resins used for packagings and intermediate bulk containers (IBCs) for the transport of dangerous goods. The marginal drop heights determined with the drop test at -18 °C after pre-storage of the test samples with 55 % nitric acid at 40 °C only partly related to the notched impact strength at -30 °C. The Charpy method is only suitable for classifying the grade in relation to toughness behavior and using this classification for comparison with other grades. Notched impact strength can provide a qualitative indication if the test samples fail under shock forces. Conditioning the design types with 55 % nitric acid for 21 days at 40 °C causes an increase in the marginal drop heights of the design types in drop tests at -18 °C when compared with design types without pre-storage. Post-crosslinking of the grades increases stiffness because of the acidic influence. T2 - NACE International Corrosion Conference 2011 CY - Houston, TX, USA DA - 13.03.2011 KW - Dangerous goods packagings KW - Polyethylene grades KW - Notched impact strength at -30°C KW - Design type tests KW - Pre-storage with nitric acid PY - 2011 SP - 1 EP - 11 (Paper 11373) AN - OPUS4-23386 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Häcker, Ralf A1 - Knothe, Esther A1 - Andrieux, F. A1 - Memhard, D. T1 - Entwicklung und Verifikation von Materialmodellen und numerischen Methoden zur Vorhersage der Containment Sicherheit beim Bersten von Laufrädern in Abgasturboladern (ATL) N2 - For predicting the Containment safety of turbochargers against failure of rotors at elevated temperatures and dynamic loading the complex deformation and damage behaviour of the respective materials has to be determined by appropriate experiments and on the other Hand the temperature and strain rate dependent data have to be implemented into material models that are able to describe the material behaviour underthese complex loading conditions. In this research project three different casting materials have been investigated. Since most experimental data were determined for the ductile cast iron alloy EN-GJS-400 with nodular graphite, this material was in the focus of numerical calcuiations. Its mechanical behaviour under uniaxial and multiaxial tension as well as under pressure and shear loading has been investigated for a variety of loading rates and temperatures. Since the material behaviour investigated in this project only concerns the Containment but not the rotor of the turbocharger the loading of the whole device was approached by impact loading of a plate with a projectile made of the same material. For the numerical modelling of the Containment safety of turbochargers a material model has been developed with the capability to describe the specific deformation behaviour of casting materials, e.g. different properties under tension and compression as a function of stress triaxiality, temperature and strain rate dependence under large plastic deformations. The material parameters for the model have been determined by numerical modelling of small scale tests under different loading conditions. The modei has been implemented in a commercial finite element code with explicit integration. In the actual Version of the user subroutine the application is limited to solid elements. In this project the material model has been applied to numerical simulations of tests on notched specimens under bending load and above all to the Simulation of penetration Tests under highly dynamic impact loading conditions as well as the Containment fest of a turbocharger. The loading conditions in these tests are comparable to the impact of a broken turbine blade on the Containment of a turbocharger. The main purpose of these tests hence was to prove the prediction capability of the material model. Numerical stability of the user routine could be achieved and the results agreed quite well with the experimental data. N2 - Für die Vorhersage der Containment Sicherheit beim Bersten von Laufrädern in Abgasturboladern müssen zum einen komplexe Verformungs- und Schädigungsvorgänge bei dynamischer Belastung einschließlich ihrer Temperaturabhängigkeit mit geeigneten Versuchen erfasst und gemessen werden, zum anderen müssen diese temperatur- und dehnratenabhängigen Kennwerte in weiterentwickelten Materialmodellen für das Verformungs- und Schädigungsverhalten abgebildet werden. Im Rahmen dieses Vorhabens wurden drei Gusswerkstoffe untersucht. Für den Gusswerkstoff mit Kugelgrafit EN-GJS-400 wurden die weitestgehenden experimentellen Untersuchungen zur Charakterisierung des Materialverhaltens unter ein- und mehrachsigem Zug sowie unter Druck- und Scherbeanspruchung für ein breites Spektrum von Beanspruchungsgeschwindigkeiten und Temperaturen durchgeführt. Die Untersuchungen an den beiden weiteren Werkstoffen erfolgten mit auf der Basis der gewonnen Erkenntnisse optimiertem Aufwand. Der Schwerpunkt der Arbeiten lag dabei im Bereich hoher Beanspruchungsgeschwindigkeiten und höherer Temperaturen sowie deren Kombination. Für die numerische Modellierung der Containment Sicherheit von ATLs wurde ein vorhandenes Materialmodell weiterentwickelt, so dass es in der Lage ist, das Verformungs- und Versagensverhalten von Gusswerkstoffen, wie z.B. den Zug-Druck-Unterschied, in Abhängigkeit von Spannungsmehrachsigkeit, Temperatur und Dehnrate auch für große plastische Deformationen zu beschreiben. Die Modellparameter wurden durch numerische Simulation von Experimenten an Proben bestimmt. Das Modell wurde in ein kommerzielles Finite-Elemente-Programm mit expliziter Integration implementiert und ist in der jetzigen Version auf FE-Modelle mit Volumenelementen beschränkt. Das Materialmodell wurde im Rahmen dieses Vorhabens zunächst zur numerischen Simulation von Experimenten an gekerbten Proben unter Biegebelastung angewendet. In einem zweiten Schritt erfolgte die Verifikation des Bauteilverhaltens durch numerische Simulation der hochdynamischen Beschussversuche. Da in diesem Vorhaben das Materialverhalten jedoch nur für das Containment und nicht auch für den Rotor des ATLs untersucht wurde, hat man für das Projektil und das Bauteil den gleichen Werkstoff verwendet. Die Belastung in diesen Beschussversuchen ist vergleichbar mit dem Aufprall eines Rotorfragments auf das Containment des Abgasturboladers. Abschließend wurde die numerische Simulation eines Containment Tests an einem Abgasturbolader durchgeführt. Die Nachrechnung dieser Experimente ist somit als ein Nachweis der Prognosefähigkeit des Materialmodells anzusehen. Numerische Stabilität der Userroutine konnte erreicht und eine gute Übereinstimmung mit den experimentellen Ergebnissen erzielt werden. T2 - Informationstagung Turbomaschinen, Frühjahrstagung 2011 CY - Bad Neuenahr, Germany DA - 17.03.2011 KW - Abgasturbolader KW - Containmentsicherheit PY - 2011 IS - R554 SP - 65 EP - 94 CY - Bad Neuenahr AN - OPUS4-23388 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Komann, Steffen A1 - Droste, Bernhard A1 - Wille, Frank T1 - Transport of large nuclear power plant components - experiences in mechanical design assessment T2 - PATRAM 2010 - 16th International symposium on the packaging and transport of radioactive materials CY - London, UK DA - 2010-10-03 KW - Mechanische Bewertung KW - Radioaktives Material KW - Numerische Analyse PY - 2010 SP - 1 EP - 8(?) AN - OPUS4-23383 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schälike, Stefan A1 - Vela-Wallenschus, Iris A1 - Wehrstedt, Klaus-Dieter A1 - Schönbucher, A. T1 - Vorhersage der thermischen Strahlung von KW-Poolfeuern mit CFD-Simulation T2 - Workshop Brandschutzforschung CY - Magdeburg, Deutschland DA - 2010-10-04 KW - Pool fire KW - Organic peroxides KW - TBPB KW - TBPEH KW - CFD KW - Safety distances PY - 2011 UR - http://www.vfdb.de/download/MagdeburgWorkshop2010/Schaelike_vfdb2010.pdf N1 - Geburtsname von Vela-Wallenschus, Iris: Vela, I. - Birth name of Vela-Wallenschus, Iris: Vela, I. SP - 1 EP - 25 AN - OPUS4-23352 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Dloczik, L. A1 - Dittrich, T. A1 - Guminskaya, T. A1 - Grigorieva, N. A1 - Lux-Steiner, M. C. A1 - Tomm, Y. A1 - Urban, Ingrid T1 - CuAlO2 prepared from LiAlO2 by ion exchange reaction PY - 2004 UR - http://www.helmholtz-berlin.de/media/media/oea/web/pr_webseite/druckschriften/berichte/2003/hmi03_web.pdf#page=100 SP - 98 PB - Hahn-Meitner-Institut CY - Berlin AN - OPUS4-23343 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Maierhofer, Christiane A1 - Krankenhagen, Rainer A1 - Röllig, Mathias A1 - Mecke, R. A1 - Schiller, M. A1 - Seidl, T. A1 - Kalisch, U. A1 - Hennen, C. A1 - Meinhardt, J. T1 - Bewertung von Schäden an historischen Bauteilen mit aktiver Thermografie und 3D-Laserscanner N2 - Sowohl in der Denkmalpflege als auch in anderen Anwendungsbereichen der zerstörungsfreien Prüfung können größere kostenintensive Erhaltungs- und Instandsetzungsmaßnahmen durch das frühzeitige Erkennen und Einschätzen von Schäden vermieden werden. Eine derartige vorbeugende Instandsetzung ist jedoch nur möglich, wenn häufige Inspektionen kostengünstig und schnell durchgeführt werden können. Systematische Methoden zur Beobachtung und Erfassung von Prozessen über einen längeren Zeitraum sowie deren Überwachung werden unter dem Begriff "Monitoring" zusammengefasst. KW - Aktive Thermografie KW - 3D-Laserscanner KW - Monitoring KW - Historische Bauteile KW - Datenfusion PY - 2011 IS - Februar SP - 51 EP - 56 PB - Ernst & Sohn CY - Berlin AN - OPUS4-23516 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schwenk, Christopher A1 - Tikhomirov, D. A1 - Eßer, G. A1 - Rethmeier, Michael T1 - General standard for welding simulation N2 - For differentiating the applicability of various numerical welding Simulation methods as well as unifying the prerequisites and the Steps to be taken in Simulation, normative codes are required for the user. Since any standard-like documents are currently still lacking in this field, DIN German Institute for Standardization has set up the Standards Committee NA 092-00-29-AA "Welding Simulation" dealing with the preparation of respective documents. This committee was initiated in partnership with the joint committee FA 12 "Weld Simulation on Application" of the Research Association of DVS German Welding Society. The objective of this Standardization work in the field of numerical welding Simulation is to prepare a DIN SPEC with a view to standardizing the approaches to the Simulation of various welding phenomena and processes over the long run. In a draft version of DIN SPEC 32534 that has already been prepared by the above mentioned Committee, the structure of the primary document was stated. The primary document specifies the application fields and the key terms of welding Simulation. In addition, the generally valid Simulation structure has been established which is intended to serve as a recommendation for customers and suppliers in formulating and handling a Service order as well as for persons who Start doing welding Simulation for the first time. This article focuses on the presentation of the new DIN SPEC 32534-1 explaining the major Simulation Steps. It additionally addresses the Classification of the secondary documents depending on the welding process and on the desired Simulation result. Finally, it gives an overview of the other subject areas dealt with in the Standards Committee NA 092-00-29-AA "Welding Simulation" as well as of the international activities in this field. T2 - IIW SC-Auto Intermediate Meeting CY - Ijmuiden, The Netherlands DA - 11.04.2011 KW - Welding simulation KW - Standardization KW - Applicability KW - Execution KW - Result display PY - 2011 IS - SC-Auto-44-11 SP - 1 EP - 10 AN - OPUS4-23519 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Kranzmann, Axel T1 - Integrity of casing and injection pipe steels during carbon capture and storage CCS N2 - During carbon capture and storage (CCS) CO2-corrosion of pipe steels is a relevant safety issue when emission gasses are compressed in deep geological layers. The reliability of the steels 42CrMo4, X20Cr13, X46Cr13 and X35CrMo17 is demonstrated in long term laboratory experiments up to 2 years of exposure time. Testings were carried out at ambient pressure under an equivalent corrosive environment as found at the geological onshore CCS-site at Ketzin, Germany (T=60 °C, aquifer water). T2 - i-SUP 2010 (Innovation for Sustainable Production) CY - Bruges, Belgium DA - 2010-04-18 KW - CCS KW - Corrosion rate KW - Corrosion layer KW - Steel KW - Pipeline PY - 2010 SP - 1 EP - 5(?) AN - OPUS4-23620 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völzke, Holger A1 - Wolff, Dietmar T1 - Safety aspects of long dry interim cask storage of spent fuel in Germany N2 - Dry cask storage of spent fuel and high active waste front reprocessing is licensed and established in Germany for up to 40years so far. About 10years ago, the strategy has been shifted from centralized storage using facilities in Ahaus and Gorleben to cit-site storage facilities in Order to avoid immediate cask shipping from nuclear power plants. At present, several hundred casks are stored safeiy and without any major problem. BAM is highly involved in cask specific safety evaluations within the scope of licensing procedures as well as of quality assurance procedures during cask fabrication, loading and storage. A major prerequisite for any cask storage license is a valid transport Type B license. Subsequently, cask transportability has to be ensured at any point during the entire storage period. So far, this requirement is met by continuous maintenance of the Type B license. Anyhow, IAEA Type B regulations do not consider permanently loaded storage casks that have the sole purpose of being finally shipped öfter decades of storage inducing ageing effects. No transport safety demonstration has to be performed on aged cask components. T2 - International high-level radioactive waste management conference (IHLRWMC 2011) CY - Albuquerque, NM, USA DA - 10.04.2011 KW - Safety KW - Cask KW - Interim storage KW - Spent fuel PY - 2011 SP - 712 EP - 719 AN - OPUS4-23651 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völzke, Holger A1 - Noack, Volker A1 - Nieslony, Gregor A1 - Hagenow, Peter A1 - Kovacs, Oliver T1 - Aktuelle Entwicklungen auf dem Gebiet der Behälter-Bauartprüfungen für das Endlager KONRAD N2 - Das Endlager Konrad wurde bereits im Jahr 2002 als Endlager für nicht Wärme entwickelnde radioaktive Abfälle genehmigt. Jedoch wurde diese Genehmigung anschließend beklagt und konnte erst 2007 in letzter Instanz bestätigt werden. Nachfolgend hat das Bundesamt für Strahlenschutz (BfS) mit der Planung und Realisierung zum Umbau des ehemaligen Eisenerzbergwerkes zum Endlager begonnen. Das genehmigte Endlagervolumen beträgt 303.000 m3 und basiert auf Abschätzungen für die zu erwartende Abfallmenge. Das Bergwerk selbst böte ein deutlich größeres Volumen. Mit der Einlagerung von Behältern kann allerdings erst nach Fertigstellung des Endlagers und nach derzeitigem Stand voraussichtlich nicht vor Ende dieses Jahrzehnts gerechnet werden. Gleichwohl besteht bereits heute ein hohes Interesse an der endlagergerechten Konditionierung und Verpackung der für Konrad vorgesehenen radioaktiven Abfälle, wofür nicht zuletzt von der BAM bauartgeprüfte und vom BfS zugelassene Behälter erforderlich sind. Kernpunkte der Endlagergenehmigung sind umfassende Anforderungen an Abfallprodukte und Behälter. Einzelheiten sind in den vom BfS der Genehmigung zu Grunde liegenden Berichten und Endlageranforderungen definiert. Diese enthalten vor allem Anforderungen an die Abfallprodukte und an die zu deren Verpackung erforderlichen Behälter. Mit der Genehmigungserteilung wurde auch eine Überarbeitung dieser Endlageranforderungen und hinsichtlich der Berücksichtigung Wasser gefährdender Stoffe gefordert. Diese Arbeiten werden derzeit vom BfS in Zusammenarbeit mit dem Niedersächsischen Landesbetrieb für Wasserwirtschaft, Küsten- und Naturschutz (NLWKN) und dem Institut für Sicherheitstechnik (ISTec) vorgenommen. Hinsichtlich der Anforderungen an die Endlagerbehälter wird allerdings davon ausgegangen, dass die für die Behälterbauartprüfung wesentlichen abfallprodukt- und behälterspezifischen Anforderungen davon nicht oder nur unwesentlich berührt sein werden. T2 - KONTEC 2011 - 10. Internationales Symposium "Konditionierung radioaktiver Betriebs- und Stilllegungsabfälle" CY - Dresden, Deutschland DA - 06.04.2011 KW - Behälter KW - Sicherheit KW - Endlager KW - Bauartprüfung KW - Radioaktive Abfälle PY - 2011 SP - 683 EP - 695 AN - OPUS4-23652 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wille, Frank A1 - Droste, Bernhard A1 - Müller, Karsten A1 - Zencker, Uwe T1 - Mechanical design assessment approaches of actual spent fuel and HLW transport package designs T2 - PATRAM 2010 - 16th International symposium on the packaging and transport of radioactive materials CY - London, UK DA - 2010-10-03 KW - Design testing KW - Transport packages KW - Numerical analysis PY - 2010 SP - 1 EP - 8(?) AN - OPUS4-23590 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Maskos, Michael A1 - Berger, Georg A1 - Braun, Ulrike A1 - Heyn, Andreas A1 - Klinger, Christian A1 - Wachtendorf, Volker T1 - Schadensanalyse und Beständigkeit von Materialien in biomedizinischen Einsatzgebieten N2 - Der Anteil von Polymeren als Funktions- und Konstruktionswerkstoffe in dauerhaften medizinischen Anwendungen steigt beständig. Derartige Materialien müssen den mechanischen, biologischen und chemischen Bedingungen im Körper widerstehen (u.a. Abrieb, Hydrolyse, Degradation) und gleichzeitig gut verträglich sein. Der sichere Einsatz von polymeren Materialien erfordert die Kenntnisse über ihre Langzeitstabilität unter verschiedenen äußeren Bedingungen. Diese sind nicht nur beeinflusst durch die unmittelbare Umgebung in vivo, sondern auch durch die Historie der verwendeten Materialien. Dazu zählen u. a. erhöhte Temperaturen unter sauerstoffhaltiger Atmosphäre während der Verarbeitung oder die Exposition von ionisierender Strahlung oder reaktiven Radikalen während der Sterilisation. PY - 2011 SP - 83 EP - 85 CY - Berlin AN - OPUS4-23592 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Deiß, Eugen A1 - Leysaht, H. T1 - Zur Bestimmung von Tellur im Stahl PY - 1936 IS - 28 SP - 113 EP - 115 PB - Springer CY - Berlin AN - OPUS4-16890 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tonn, W. A1 - Günther, Heinrich T1 - Beitrag zur Gebrauchsprüfung von Zinn-Bleiloten PY - 1936 IS - 28 SP - 117 EP - 119 PB - Springer CY - Berlin AN - OPUS4-16891 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Wilhelm T1 - Richtlinien für einheitliche Härteprüfung PY - 1936 IS - 28 SP - 121 EP - 124 PB - Springer CY - Berlin AN - OPUS4-16892 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Büll, R. T1 - Versuche über die Wasserbindung anorganischer Stoffe I PY - 1936 IS - 29 SP - 1 EP - 18 PB - Springer CY - Berlin AN - OPUS4-16893 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schob, Alfred A1 - Nitsche, Rudolf A1 - Salewski, E. T1 - Die Prüfung von Fertigstücken aus Isolierpreßstoffen auf Werkstoff-Eigenschaften PY - 1936 IS - 29 SP - 19 EP - 28 PB - Springer CY - Berlin AN - OPUS4-16894 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hummel, Alfred T1 - Beeinflussung der Beton-Elastizität PY - 1936 IS - 29 SP - 29 EP - 40 PB - Springer CY - Berlin AN - OPUS4-16895 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Herrmann, M. T1 - Über die Nutzbreite bei Steineisendecken mit Einzellast PY - 1936 IS - 29 SP - 41 EP - 50 PB - Springer CY - Berlin AN - OPUS4-16896 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schulze, Bruno T1 - Schwamm-Schäden - Der echte Hausschwamm und die übrigen holzzerstörenden Pilze des Hauses im Lichtbild PY - 1936 IS - 30 SP - 1 EP - 35 PB - Springer CY - Berlin AN - OPUS4-16897 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fahrenhorst, W. A1 - Sachs, Georg T1 - Über das Aufreißen von kaltgezogenem Rundeisen PY - 1932 IS - 19 SP - 87 EP - 92 PB - Springer CY - Berlin AN - OPUS4-16800 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald T1 - Über die Ursachen von Dampfkesselschäden PY - 1932 IS - 19 SP - 92 EP - 104 PB - Springer CY - Berlin AN - OPUS4-16801 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Wilhelm T1 - Kohäsionsfestigkeit PY - 1932 IS - 20 SP - 1 EP - 62 PB - Springer CY - Berlin AN - OPUS4-16803 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Hansen, Max T1 - Der Einfluß von dritten Metallen auf die Konstitution der Messinglegierungen. IV. Der Einfluß von Aluminium. Ein Beitrag zur Kenntnis des Dreistoff-Systems Kupfer-Zink-Aluminium PY - 1933 IS - 21 SP - 3 EP - 18 PB - Springer CY - Berlin AN - OPUS4-16804 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hansen, Max A1 - Blumenthal, B. T1 - Zur Kenntnis der Zweistoffsysteme des Aluminiums mit Kadmium, Blei und Wismut PY - 1933 IS - 21 SP - 19 EP - 20 PB - Springer CY - Berlin AN - OPUS4-16805 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmid, Erich A1 - Siebel, G. T1 - Röntgenographische Bestimmung der Löslichkeit von Mangan und Magnesium PY - 1933 IS - 21 SP - 21 EP - 23 PB - Springer CY - Berlin AN - OPUS4-16806 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wassermann, G. T1 - Über die Umwandlung des Kobalts PY - 1933 IS - 21 SP - 33 EP - 38 PB - Springer CY - Berlin AN - OPUS4-16807 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Boas, W. A1 - Schmid, Erich T1 - Über die Struktur der Oberfläche geschliffener Metallkristalle PY - 1933 IS - 21 SP - 39 EP - 42 PB - Springer CY - Berlin AN - OPUS4-16808 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Caglioti, V. A1 - Sachs, Georg T1 - Die Walztextur von Zink und Magnesium PY - 1933 IS - 21 SP - 42 EP - 46 PB - Springer CY - Berlin AN - OPUS4-16809 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Albrecht, E. T1 - Festigkeitsprüfung von Flachglas PY - 1936 IS - 27 SP - 58 EP - 60 PB - Springer CY - Berlin AN - OPUS4-16850 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Albrecht, E. T1 - Die Prüfung von Mehrschichten-Sicherheitsglas auf Wetterbeständigkeit nach DIN DVM 2302 PY - 1936 IS - 27 SP - 61 EP - 63 PB - Springer CY - Berlin AN - OPUS4-16851 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stöcke, K. T1 - Grundsätzliches und Organisatorisches zur Prüfung natürlicher mineralischer Straßenbaustoffe PY - 1936 IS - 27 SP - 65 EP - 69 PB - Springer CY - Berlin AN - OPUS4-16852 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stöcke, K. T1 - Die Bedeutung der Materialprüfung für die Steinindustrie PY - 1936 IS - 27 SP - 71 EP - 76 PB - Springer CY - Berlin AN - OPUS4-16853 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kristen, Theodor T1 - Erhöhung der Widerstandsfähigkeit von Mauerwerk gegenüber Feuereinwirkung durch geeignete Mörtelzusammensetzung des Putzes PY - 1936 IS - 27 SP - 77 EP - 86 PB - Springer CY - Berlin AN - OPUS4-16854 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kristen, Theodor T1 - Steigerung der Tragfähigkeit von Mauerwerkskörpern durch Verbesserung des Mörtels PY - 1936 IS - 27 SP - 87 EP - 92 PB - Springer CY - Berlin AN - OPUS4-16855 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Deiß, Eugen T1 - Über Beschädigungen an Zinkrinnen und Vorstoßblechen von Bitumenpappdächern PY - 1936 IS - 27 SP - 93 EP - 105 PB - Springer CY - Berlin AN - OPUS4-16856 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kristen, Theodor T1 - Wie lange kann die Einwirkung von Feuer auf Stahlfachwerke durch leichte Zwischendecken hinausgeschoben werden? PY - 1936 IS - 27 SP - 107 EP - 114 PB - Springer CY - Berlin AN - OPUS4-16857 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krüger, Lothar T1 - Prüfung der natürlichen Gesteine auf Wetterbeständigkeit PY - 1936 IS - 27 SP - 115 EP - 119 PB - Springer CY - Berlin AN - OPUS4-16858 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bierett, Georg T1 - Die Lehren der Spannungs- und Festigkeitsforschung für die Ausbildng und Ausführung geschweißter Konstruktionen PY - 1936 IS - 28 SP - 1 EP - 10 PB - Springer CY - Berlin AN - OPUS4-16859 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Sieglerschmidt, H. T1 - Einfluß der Versuchsbedingungen auf das Schwindmaß PY - 1936 IS - 28 SP - 49 EP - 53 PB - Springer CY - Berlin AN - OPUS4-16881 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald T1 - Ist der Korrosionsversuch reif für die Normung? PY - 1936 IS - 28 SP - 55 EP - 59 PB - Springer CY - Berlin AN - OPUS4-16882 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Tonn, W. T1 - Die Arsen-Bleilegierungen PY - 1936 IS - 28 SP - 61 EP - 65 PB - Springer CY - Berlin AN - OPUS4-16883 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Schikorr, Gerhard T1 - Über das Verhalten von Blei in destilliertem Wasser PY - 1936 IS - 28 SP - 67 EP - 70 PB - Springer CY - Berlin AN - OPUS4-16884 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bierett, Georg T1 - Welche Wege weisen die Erkenntnisse über Schrumpfwirkungen den Arbeitsverfahren für die Herstellung von Stumpfnähten im Großstahlbau PY - 1936 IS - 28 SP - 71 EP - 78 PB - Springer CY - Berlin AN - OPUS4-16885 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Wilhelm T1 - Umrechnung der im Zugversuch ermittelten Bruchdehnung auf andere Probenmeßlängen PY - 1936 IS - 28 SP - 79 EP - 93 PB - Springer CY - Berlin AN - OPUS4-16886 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Sipp, K. T1 - Über Gußspannungen und die Mittel zu ihrer Beseitigung PY - 1936 IS - 28 SP - 95 EP - 98 PB - Springer CY - Berlin AN - OPUS4-16887 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Sieglerschmidt, H. T1 - Einfluß der Versuchsbedingungen auf das Schwindmaß - II. Mitteilung PY - 1936 IS - 28 SP - 99 EP - 104 PB - Springer CY - Berlin AN - OPUS4-16888 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Wilhelm T1 - Kerbgestalt und elastische Dehnungsverteilung (beim ebenen Spannungszustand) PY - 1936 IS - 28 SP - 105 EP - 112 PB - Springer CY - Berlin AN - OPUS4-16889 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stamer, J. T1 - Untersuchungen an zugfesten Anschlüssen im Holzbau - Einleitende Versuche mit glatten Dornen PY - 1931 IS - 15 SP - 70 EP - 73 PB - Springer CY - Berlin AN - OPUS4-16747 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sachs, Georg T1 - Zur Einführung in die Technologie der spanlosen Formung PY - 1931 IS - 16 SP - 5 EP - 10 PB - Springer CY - Berlin AN - OPUS4-16749 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lehr, Ernst A1 - Mailänder, R. T1 - Einfluß von Hohlkehlen an abgesetzten Wellen auf die Biegewechselfestigkeit PY - 1936 IS - 28 SP - 11 EP - 17 PB - Springer CY - Berlin AN - OPUS4-16860 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Berthold, Rudolf T1 - Zerstörungsfreie Werkstoffprüfung mit dem Magnetpulver-Verfahren PY - 1936 IS - 28 SP - 19 EP - 26 PB - Springer CY - Berlin AN - OPUS4-16861 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schikorr, Gerhard T1 - Über das atmosphärische Rosten des Eisens PY - 1936 IS - 28 SP - 27 EP - 33 PB - Springer CY - Berlin AN - OPUS4-16862 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Grüning, G. A1 - Hoffmann, W. T1 - Spannungsverteilung und Formziffer des rundgekerbten Zugstabes für die Schweißgutprüfung gemäß DIN 1913 PY - 1936 IS - 28 SP - 35 EP - 36 PB - Springer CY - Berlin AN - OPUS4-16863 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Grüning, G. T1 - Knickversuche mit außermittig gedrückten Stahlstützen. Eine Einordnung von Versuchsergebnissen in die in letzter Zeit aufgestellten Berechnungen PY - 1936 IS - 28 SP - 37 EP - 48 PB - Springer CY - Berlin AN - OPUS4-16864 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gonell, Hans-Wolfgang T1 - Messung des Staubniederschlages im Freien PY - 1936 IS - 27 SP - 15 EP - 20 PB - Springer CY - Berlin AN - OPUS4-16844 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burchartz, Heinrich A1 - Deiß, Eugen T1 - Das Verhalten der Sulfide der Hochofenschlacke in Zementmörtel und Beton PY - 1936 IS - 27 SP - 21 EP - 26 PB - Springer CY - Berlin AN - OPUS4-16845 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kindscher, Erich T1 - Bitumen im Spiegel der Länderberichte zum internationalen Straßenkongreß München PY - 1936 IS - 27 SP - 27 EP - 35 PB - Springer CY - Berlin AN - OPUS4-16846 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weißwange, W. T1 - Prüfung von Dachpappen auf Verhalten gegenüber Witterungseinflüssen PY - 1936 IS - 27 SP - 37 EP - 48 PB - Springer CY - Berlin AN - OPUS4-16847 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Saenger, Georg A1 - Weißwange, W. T1 - Blasen im Gußasphalt PY - 1936 IS - 27 SP - 49 EP - 53 PB - Springer CY - Berlin AN - OPUS4-16848 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Albrecht, E. T1 - Abkühlungs- und Erwärmungsgeschwindigkeit von Mehrschichtensicherheitsglas PY - 1936 IS - 27 SP - 55 EP - 57 PB - Springer CY - Berlin AN - OPUS4-16849 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Seidl, Erich T1 - Die Bedeutung der Struktur für die bleibende Formänderung von Kristallen PY - 1933 IS - 21 SP - 46 EP - 49 PB - Springer CY - Berlin AN - OPUS4-16810 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Caglioti, V. A1 - Sachs, Georg T1 - Die Entwicklung von Eigenspannungen durch Dehnen PY - 1933 IS - 21 SP - 49 EP - 52 PB - Springer CY - Berlin AN - OPUS4-16811 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fahrenhorst, W. A1 - Matthaes, K. A1 - Schmid, Erich T1 - Über die Abhängigkeit der Dauerfestigkeit von Kristallorientierung PY - 1933 IS - 21 SP - 58 EP - 60 PB - Springer CY - Berlin AN - OPUS4-16812 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmid, Erich A1 - Valouch, M.A. T1 - Über sprunghafte Translation von Zinkkristallen PY - 1933 IS - 21 SP - 60 EP - 64 PB - Springer CY - Berlin AN - OPUS4-16813 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Valouch, M.A. T1 - Bemerkungen zur Walztextur von Zink PY - 1933 IS - 21 SP - 64 EP - 65 PB - Springer CY - Berlin AN - OPUS4-16814 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Boas, W. A1 - Schmid, Erich T1 - Laue-Diagramme mit großen Ablenkungswinkeln PY - 1933 IS - 21 SP - 66 EP - 68 PB - Springer CY - Berlin AN - OPUS4-16815 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wassermann, G. T1 - Über eine Heizvorrichtung für Röntgenpräparate PY - 1933 IS - 21 SP - 69 PB - Springer CY - Berlin AN - OPUS4-16816 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmid, Erich T1 - Über die Bedeutung der Röntgenstrahlinterferenzen für die Metallkunde PY - 1933 IS - 21 SP - 70 EP - 74 PB - Springer CY - Berlin AN - OPUS4-16817 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weerts, J. T1 - Präzisions-Röntgenverfahren in der Legierungsforschung PY - 1933 IS - 21 SP - 75 EP - 79 PB - Springer CY - Berlin AN - OPUS4-16819 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Beck, P. A1 - Polanyi, M. T1 - Rückbildung des Rekristallisationsvermögens durch Rückformung PY - 1932 IS - 19 SP - 30 EP - 32 PB - Springer CY - Berlin AN - OPUS4-16790 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmid, Erich A1 - Wassermann, G. T1 - Zur Rekristallisation von Aluminiumblech PY - 1932 IS - 19 SP - 32 EP - 33 PB - Springer CY - Berlin AN - OPUS4-16791 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmid, Erich A1 - Wassermann, G. T1 - Einfluß von Kaltreckung auf die Plastizität bei erhöhten Temperaturen PY - 1932 IS - 19 SP - 33 EP - 35 PB - Springer CY - Berlin AN - OPUS4-16792 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmid, Erich A1 - Wassermann, G. T1 - Über die Walztextur von Cadmium PY - 1932 IS - 19 SP - 35 EP - 36 PB - Springer CY - Berlin AN - OPUS4-16793 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fahrenhorst, W. A1 - Schmid, Erich T1 - Wechseltorsionsversuche an Zinkkristallen PY - 1932 IS - 19 SP - 36 EP - 44 PB - Springer CY - Berlin AN - OPUS4-16794 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmid, Erich A1 - Siebel, G. T1 - Röntgenographische Bestimmung der Löslichkeit von Magnesium in Aluminium PY - 1932 IS - 19 SP - 44 EP - 47 PB - Springer CY - Berlin AN - OPUS4-16795 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stenzel, W. A1 - Weerts, J. T1 - Die Gitterkonstanten der Silber-Palladium- und Gold-Palladium-Legierungen PY - 1932 IS - 19 SP - 47 EP - 51 PB - Springer CY - Berlin AN - OPUS4-16796 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stenzel, W. A1 - Weerts, J. T1 - Röntgenuntersuchungen im System Gold-Platin PY - 1932 IS - 19 SP - 51 EP - 54 PB - Springer CY - Berlin AN - OPUS4-16797 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weißenberg, K. T1 - Mechanik deformierbarer Körper PY - 1932 IS - 19 SP - 54 EP - 84 PB - Springer CY - Berlin AN - OPUS4-16798 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Goens, E. A1 - Schmid, Erich T1 - Über die elastische Anisotropie des Eisens PY - 1932 IS - 19 SP - 84 EP - 87 PB - Springer CY - Berlin AN - OPUS4-16799 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sachs, Georg A1 - Stenzel, W. T1 - Versuche über das Altern von Stahl PY - 1931 IS - 17 SP - 38 EP - 45 PB - Springer CY - Berlin AN - OPUS4-16760 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sachs, Georg A1 - Weerts, J. T1 - Atomordnung und Eigenschaften - Untersuchungen an der Legierung AuCu³ PY - 1931 IS - 17 SP - 45 EP - 48 PB - Springer CY - Berlin AN - OPUS4-16761 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Wilhelm T1 - Struktur, Festigkeit, Stetigkeit PY - 1931 IS - 17 SP - 48 EP - 52 PB - Springer CY - Berlin AN - OPUS4-16762 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Boas, W. A1 - Schmid, Erich T1 - Zur Deutung der Deformationstexturen von Metallen PY - 1931 IS - 17 SP - 53 EP - 56 PB - Springer CY - Berlin AN - OPUS4-16764 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmid, Erich A1 - Wassermann, G. T1 - Über die Walztexturen hexagonaler Metalle PY - 1931 IS - 17 SP - 56 EP - 60 PB - Springer CY - Berlin AN - OPUS4-16766 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schiebold, Ernst A1 - Sachs, Georg T1 - Studien an Magnesium und Magnesiumlegierungen I. PY - 1931 IS - 17 SP - 61 EP - 70 PB - Springer CY - Berlin AN - OPUS4-16768 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sander, B. A1 - Sachs, Georg T1 - Zur röntgenoptischen Gefügeanalyse von Gesteinen PY - 1931 IS - 17 SP - 70 EP - 79 PB - Springer CY - Berlin AN - OPUS4-16769 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Koch, J. A1 - Wilrich, Cordula A1 - Gebel, T. T1 - New GHS-Regulation - Implementation of the GHS (Globally Harmonized System) in the EU - What are the changes? KW - GHS KW - Dangerous chemicals KW - Classification PY - 2008 VL - 1 SP - 10 EP - 11 PB - Vogel CY - Würzburg AN - OPUS4-17123 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Berger, Anka A1 - Krause, Ulrich T1 - Zünd- und Brandverhalten von Massenschüttgütern, Deponiestoffen und Recyclingmaterialien T2 - 57. Jahresfachtagung der Vereinigung zur Förderung des Deutschen Brandschutzes e.V. CY - Bochum DA - 2008-04-27 KW - Selbstentzündung KW - Haldenbrand KW - Brandsimulation PY - 2008 SP - 549 EP - 560 CY - Altenberge AN - OPUS4-17497 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Torge, Manfred A1 - Berkei, I. T1 - Aus der Abstellkammer ins Labor - Wissenschaftler unterstützen die Restaurierung von Glasfenstern KW - Bleiverglasung KW - Restaurierung PY - 2008 SP - 85 EP - 87 PB - Förderkreis Alte Kirchen Berlin-Brandenburg CY - Berlin AN - OPUS4-17503 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thiele, E. A1 - Erth, H. A1 - Helbig, R. A1 - Werth, K. A1 - Glötzl, R. A1 - Schneider, J. A1 - Nöther, Nils A1 - Wosniok, Aleksander A1 - Krebber, Katerina A1 - Schlurmann, T. A1 - Saathoff, F. T1 - Sensitive Textilstrukturen zur Deichüberwachung T2 - BAUTEX 2008, 8. Sächsisches Bautextilien-Symposium "Bauen mit Geokunststoffen" CY - Chemnitz, Deutschland DA - 2008-01-24 PY - 2008 SP - 1 EP - 5 CY - Chemnitz AN - OPUS4-17448 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Köppen, Robert A1 - Becker, Roland A1 - Weber, M. A1 - Durmaz, V. A1 - Nehls, Irene T1 - HBCD stereoisomers: Thermal interconversion and enantiospecific trace analysis in biota T2 - DIOXIN 2008, 28th International Symposium on Halogenated Persistent Organic Pollutants (POPs) CY - Birmingham, UK DA - 2008-08-17 KW - HBCD KW - Stereoisomerie KW - Persistent Organic Pollutant KW - HPLC-MS PY - 2008 UR - http://www.dioxin20xx.org/pdfs/2008/08-819.pdf IS - Paper #154 SP - 1 EP - 4 AN - OPUS4-17842 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilke, Olaf A1 - Seeger, Stefan A1 - Bresch, Harald A1 - Brödner, Doris A1 - Juritsch, Elevtheria A1 - Jann, Oliver T1 - Sampling and characterisation of ultra fine particles released from laser printers T2 - Indoor Air 2008, August 17-22, 2008 CY - Copenhagen, Denmark DA - 2008-08-17 KW - Aerosol KW - Ultra fine particle KW - Laser printer KW - Cyclosiloxanes PY - 2008 IS - Paper ID: 239 SP - 1 AN - OPUS4-17865 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lenke, Philipp A1 - Liehr, Sascha A1 - Krebber, Katerina T1 - Improvements of the distributed strain sensor based on optical time domain reflectometry measurement in polymer optical fibers N2 - Sensing characteristics of standard polymer optical fibers (POF) are further studied using the optical time domain reflectometry (OTDR) technique. The level of the backscattering inside POF, which highly increases at locations where strain is applied to the fiber, is further investigated with respect to spectral behavior, strain rate and span of time from the stretching event. An algorithem to overcome the problem of the decrease of spatial resolution as a result of pulse broadening due to modal disperion, is proposed. The research is carried out on the background of the development of a new strain sensor that is integrated in technical textiles. T2 - 17th International Conference on Plastic Optical Fibers (POF 2008) CY - Santa Clara, California, USA DA - 2008-08-25 KW - Distributed strain sensor KW - Optical fiber sensor KW - POF KW - Scatter KW - PMMA KW - Spatial resolution PY - 2008 IS - Paper 1 SP - 1 EP - 5 AN - OPUS4-18210 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Aris, Stephan A1 - Szypkowski, Marko A1 - Ciscato, W. A1 - Nadeschdin, C. T1 - Nitroxnormen - was gilt nun? N2 - Die seit 2003 gültige Nitroxnorm EN13949 ist in Taucherkreisen ein viel diskutiertes Thema. Vor allem das für Nitrox und Sauerstoff normierte Ventil nach EN144-3 mit dem M26x2 Anschluss sorgt in den letzten Monaten für rote Köpfe. Auch weil die 5jährige Übergangsfrist dafür Ende Juni 2008 in Deutschland abgelaufen ist. Mehrere Autoren aus dem In- und Ausland, welche auf EU-Niveau Experten in Tauchernormen sind, konnte DiveInside für diesen Beitrag gewinnen. Die Autoren Ciscato, Szypkowski und Aris, gehören dem CEN/TC 79/SC 7 (diving apparatus Normenkomitee) an und sind aktiv an der Erstellung und Revision von Tauchgerätenormen und Ventilnormen beteiligt. KW - Nitrox KW - Ventilanschlüsse KW - Normung PY - 2008 UR - http://www.diveinside.de/DI_Nitroxnormen_15_159.pdf IS - 8 SP - 51 EP - 55 AN - OPUS4-18200 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Volkmar A1 - Molnarne, Maria T1 - Explosion protection for biogas plants T2 - International Symposium on Process and Explosion Protection CY - Nürnberg, Germany DA - 2008-09-30 PY - 2008 IS - USB-Stick SP - 1 EP - 11 AN - OPUS4-18207 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Liehr, Sascha A1 - Lenke, Philipp A1 - Wendt, Mario A1 - Krebber, Katerina T1 - Perfluorinated graded-index polymer optical fibers for distributed measurement of strain N2 - Recently, we have proposed, to our knowledge for the first time, to use perfluorinated graded-index polymer optical fiber (POF) for distributed measurement of strain. Thanks to their low attenuation and low modal dispersion compared to standard-POF, this fiber type allows to extend the measurement length to more than 500 meters at increased spatial resolution. In this paper, two mechanisms for strain sensing are introduced. As in standard PMMA POF, strain in the fiber can be detected by evaluating the local backscatter increase occurring at strained fiber sections. Further, we propose, to our knowledge for the first time, a true distributed length change measurement in POF using cross-correlation analysis of the fiber’s characteristic backscatter signature. Using this technique, it is possible to measure relative displacement between different fiber sections avoiding signal fading failures that are inherent in other measurement principles. Cross-sensitivities to the sensor signal, as fiber bends and temperature, are investigated and quantified. T2 - 17th International Conference on Plastic Optical Fibers (POF 2008) CY - Santa Clara, California, USA DA - 2008-08-25 KW - Distributed strain sensor KW - Optical fiber sensor KW - Perfluorinated POF KW - POF sensors PY - 2008 IS - Paper 64 SP - 1 EP - 5 AN - OPUS4-18209 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Huismann, Sven A1 - Rodrigues, J.P.C. A1 - Korzen, Manfred ED - Joao Paulo Correia Rodrigues, ED - Gabriel Alexander Khoury, ED - Niel Peter Hoj, T1 - Damage and strength reduction of a high performance concrete due to thermomechanical stresses T2 - International Workshop "Fire Design of Condrete Structures - from materials modelling to structural performance" CY - Coimbra, Portugal DA - 2007-11-08 KW - High-performance concrete (HPC) KW - Compressive strength KW - Thermal cracking KW - Thermo mechanical stresses KW - Ultrasonic testing PY - 2008 SP - 141 EP - 148 AN - OPUS4-18174 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Qiao, Linan A1 - Zencker, Uwe A1 - Wieser, Günter A1 - Völzke, Holger T1 - Numerische Analyse eines ungedämpften Behälterabsturzes aus 0,3 m Höhe T2 - Jahrestagung Kerntechnik CY - Hamburg, Germany DA - 2008-05-27 KW - Duktiles Gusseisen KW - Behälterdesign KW - Sicherheitsanalyse KW - Dynamische Beanspruchungsbedingungen KW - Finite-Element-Berechnung PY - 2008 SP - 380 EP - 383 PB - INFORUM-Verl. u. Verwaltungsges. CY - Berlin AN - OPUS4-18314 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niebergall, Ute A1 - Mertlová, O. A1 - Nezbedová, E. T1 - Full Notch Creep Test - ISO Round Robin test T2 - The Polymer Processing Society 24th Annual Meeting (PPS-24) CY - Salerno, Italy DA - 2008-06-15 KW - Full Notch Creep Test (FNCT) KW - Spannungsrissempfindlichkeit KW - Zeitstandzugversuch KW - Medium KW - Netzmittellösung PY - 2008 SP - 1 EP - 6 AN - OPUS4-18257 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meyer-Plath, Asmus A1 - Mach, Reinhard A1 - Maneck, Heinz-Eberhard A1 - Oleszak, Franz A1 - Friedrich, Jörg Florian T1 - Plasma-chemical functionalization of expanded graphite T2 - International Conference on Carbon (Carbon 2008) CY - Nagano, Japan DA - 2008-06-13 KW - Gas Discharge Plasma KW - Expanded Graphite KW - Functionalization KW - Surface Chemistry PY - 2008 SP - 1 EP - 5 AN - OPUS4-18339 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lüddecke, Falk T1 - Load bearing behaviour of cast steel components in offshore wind turbines structures under fatigue and static loads T2 - 1st International Workshop for Young Scientists (WMRIF 2008) CY - Tsukuba, Japan DA - 2008-07-22 KW - Offshore KW - Stahlgussbauteile KW - Ermüdung KW - Traglasttests PY - 2008 SP - XXIV-1 - XXIV-9 AN - OPUS4-18341 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lüddecke, Falk A1 - Mehdianpour, Milad T1 - Ertüchtigungsmaßnahmen an bestehenden Stahltragwerken unter Berücksichtigung der Schweißtechnik T2 - Große Schweißtechnische Tagung CY - Basel, Switzerland DA - 2007-09-16 KW - Ertüchtigung KW - Baustahl KW - Schweißtechnik KW - Werkstoffermüdung KW - Betriebsfestigkeit KW - Metallurgie PY - 2007 SP - 1 EP - 5 AN - OPUS4-18343 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Retzlaff, J. A1 - Bronstein, Z. A1 - Müller-Rochholz, J. A1 - Böhning, Martin A1 - Robertson, Daniela A1 - Schröder, Hartmut T1 - Oxidative resistance of geosynthetics: practical aspects and developments of testing at elevated temperature and oxygen pressure N2 - Service life of geosynthetics made of polyolefin materials is mainly limited by oxidative degradation. Durability of polyolefin products depend on formulation, morphology resulting from manufacturing, design and particularly on the antioxidants used. Although the fundamental oxidative reactions are known, the complex effect of geosynthetic characteristics and external influences mean that durability assessments require practical tests. The assessment of oxidative durability involves exposure to accelerating conditions as well as the material characterisation with respect to the state of stabilisation and/or degradation (e.g. by tensile testing and/or oxidation induction time). The autoclave test developed by BAM for durability assessments of polyolefin geosynthetics is based on the simultaneous application of moderately elevated temperatures (up to 80 degrees Celsius) and elevated oxygen pressures (up to 5.0 MPa) in combination with a surrounding aqueous medium. Thus this test method provides several advantages in comparison to conventional oven testing, especially with respect to test duration, impact of surrounding environment and the potential to differentiate and rank oxidative resistance between products of very different dimensions (surface/volume) and stabilisation. In view of the increasing demand for durability assessments of geosynthetic products with lifetimes significantly exceeding 25 years, the contribution is focused on practical aspects concerning implementation and optimisation of test procedures, conditions and evaluation of results. Furthermore, advanced approaches based on multiple exposure conditions will also be included and corresponding calculations of expected service life in typical applications will be evaluated with respect to significance and repeatability. Thereby involved standards and recommendations - such as EN ISO 13438, Part C or EAG-EDT - are considered. T2 - EuroGeo4, 4th European Geosynthetics Conference CY - Edinburgh, UK DA - 2008-09-07 KW - Ageing KW - Degradation KW - HDPE KW - Laboratory test KW - Oxidation KW - Polypropylene PY - 2008 IS - Paper 178 SP - 1 EP - 4 AN - OPUS4-18423 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Retzlaff, J. A1 - Müller-Rochholz, J. A1 - Klapperich, H. A1 - Böhning, Martin T1 - The behaviour of geosynthetics under cyclic load N2 - Whenever geosynthetics are used to reinforce or stabilise infrastructural elements such as road- and railways, bridge abutments, run- and taxiways on airports or to protect coastlines of canals and other steep slopes they may be exposed to cyclic loads. Therefore, a reduction factor for dynamic effects on the geosynthetic tensile strength has been included into the calculation of the Long Term Design Strength (LTDS). An approach to assess the behaviour of geosynthetics is to adopt Woehler- or Smith graphs and Haigh-diagrams for polymers. This is because an endurance limit for polymers, which defines an infinite life under a defined cyclic load, has not been seen so far. A huge amount of mechanical testing is needed to predict the behaviour of geosynthetics against this particular background. To reduce these efforts while getting an indication of the cyclic effect on geosynthetics, a combined method of mechanical and chemical analysis has been developed. The pure tensile strength tests to determine the residual strength after cyclic stress has been amended by IR-spectroscopy and Differential Scanning Calorimetry (DSC). In this context the chain change model of PET has been proven as valid for cyclic loads as well, which helps to define the endurance limit of materials made out of PET. For polyolefins such as PP and PE, a limit for the maximum alternating load has been identified at the point of the stress strain graph where the actual and the numerical stress of a material diverge from each other. Cyclic tensile strength tests have been carried out in a hydraulic test frame. The test parameters have been set to simulate the service life of a railway bed trafficked by high speed trains (ICE). T2 - EuroGeo4, 4th European Geosynthetics Conference CY - Edinburgh, UK DA - 2008-09-07 KW - Cyclic load KW - Dynamic loads KW - Laboratory test KW - Reduction factor KW - Reinforcement KW - Stiffness PY - 2008 IS - Paper 179 SP - 1 EP - 7 AN - OPUS4-18425 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Medhurst, T. A1 - Masendorf, R. A1 - Bork, Claus-Peter A1 - May, U. A1 - Oppermann, H. A1 - Steinbeck, G. A1 - Wagener, R. ED - Portella, Pedro Dolabella ED - T. Beck, ED - M. Okazaki, T1 - Influence of ambient temperature on steel sheet in LCF Tests T2 - 6th International Conference on Low Cycle Fatigue (LCF 6) CY - Berlin, Germany DA - 2008-09-08 KW - Steel sheet KW - Cyclic material characteristics KW - Influence of temperature PY - 2008 SP - 377 EP - 382 AN - OPUS4-18360 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kreutzbruck, Marc A1 - Allweins, K. A1 - Bernau, H. ED - Peter Scharff, T1 - Inverse Algorithm for Electromagnetic Wire Inspection based on GMR-Sensor Arrays T2 - 10th Workshop on optimization and inverse problems in electromagnetism (OIPE 2008) CY - Ilmenau, Germany DA - 2008-09-14 KW - Nondestructive Testing KW - Reconstruction KW - GMR-sensor array KW - Superconducting wires PY - 2008 IS - O6_1 SP - 137 EP - 138 CY - Ilmenau AN - OPUS4-18367 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beckmann, Jörg A1 - Rachny, S. A1 - Zscherpel, Uwe A1 - Ewert, Uwe T1 - Improved Procedure for Computed Radiography - A Comparative Study on Welded Tube Sections by Film Radiography and Computed Radiography N2 - Different girth welds of tube sections have been inspected by elliptical projection technique according to the EN 1435. The radiographic images were taken by using both film radiography and computed radiography. The purpose of this study was to compare a C3 (AGFA D4) film system and a Duerr HDCR 35 NDT / HR IP imaging plate system with respect to the exposure time, image quality and the detection of fine weld imperfections. The results indicate to a dominant influence of the lead screens on the image contrast sensitivity if doing the inspection according to the EN 14748 -2 for imaging plate exposures. New screen combinations had been applied to make a computed radiograph of a testing class B quality possible. T2 - 17th World Conference on Non-Destructive Testing CY - Shanghai, China DA - 2008-10-25 KW - Film KW - Digital radiography KW - Computed radiography KW - Image quality PY - 2008 IS - Paper 69 SP - 1 EP - 7 PB - International Committee for Non-Destructive Testing CY - Shanghai AN - OPUS4-18412 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Köpp, Christian A1 - Kruschwitz, Sabine T1 - Cultural Heritage Protection Against Flood (CHEF) - A European FP6 Research Project T2 - 8th EC Conference on Sustaining Europe´s Cultural Heritage (CHRESP) CY - Ljubljana, Slovenia DA - 2008-11-11 KW - Cultural heritage KW - Flood KW - Damage KW - Non-destructive testing PY - 2008 SP - 24 EP - 25 AN - OPUS4-18382 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Qiao, Linan A1 - Wieser, Günter A1 - Zencker, Uwe A1 - Droste, Bernhard T1 - Dynamic finite element analyses of a HLW transport cask with polyurethane impact limiters in 9m drop tests T2 - PATRAM 2007, 15th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Miami, Florida, USA DA - 2007-10-21 KW - Ductile iron KW - Cask design KW - Safety assessment KW - Impact limiter KW - Dynamic loading conditions PY - 2007 IS - Session E, Paper #60 SP - 1 EP - 7 PB - Institute of Nuclear Materials Management AN - OPUS4-18400 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Horn, Wolfgang A1 - Jann, Oliver A1 - Brödner, Doris A1 - Kalus, Sabine A1 - Juritsch, Elevtheria A1 - Müller, B. A1 - Müller, D. A1 - Kasche, J. T1 - Chemische analytische Bewertung von Baustoffemissionen T2 - Deutsche Kälte-Klima-Tagung 2008 CY - Ulm, Deutschland DA - 2008-11-20 KW - AgBB-Schema KW - VOC KW - Emissionen KW - Bauprodukte KW - Bewertung Emissionen PY - 2008 IS - AA.IV.15 SP - 1 EP - 8 AN - OPUS4-18406 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wehr, A. A1 - Thomas, M. A1 - Hemmleb, M. A1 - Maierhofer, Christiane ED - Gruen, A. ED - H. Kahmen, T1 - Moisture detection on building surfaces by multi-spectral laser scanning T2 - 8th Conference on Optical 3-D Measurement Techniques CY - Zurich, Switzerland DA - 2007-07-09 KW - Multi-Spectral KW - Laser Scanning KW - Three Dimensional KW - Moisture Detection KW - Vegetation Index KW - Multi-Spectral Classification PY - 2007 SP - 1 EP - 8 AN - OPUS4-18407 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Said, Samir A1 - Auersch, Lutz T1 - Environmental vibration due to normal and extreme excitation: railway traffic, explosions and heavy mass drop tests T2 - ISEV 2007, 3rd International Symposium on Environmental Vibrations: Prediction, Monitoring, Mitigation and Evaluation CY - Taipei, Taiwan DA - 2007-11-28 PY - 2007 SP - 1 EP - 6 AN - OPUS4-18408 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eichler, Thorsten A1 - Isecke, Bernd A1 - Wilsch, Gerd A1 - Goldschmidt, Sebastian A1 - Bruns, M. T1 - Investigations on alterations of electrochemical parameters of steel in chloride containing concrete in consequence of cathodic polarization T2 - EUROCORR 2008 CY - Edinburgh, Scotland, UK DA - 2008-09-07 KW - LIBS KW - Cathodic Protection KW - Steel in concrete KW - Chloride Migration PY - 2008 N1 - Serientitel: EFC-Event – Series title: EFC-Event IS - 299 SP - 1 EP - 15 PB - DECHEMA CY - Frankfurt am Main AN - OPUS4-18370 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Qiao, Linan A1 - Weber, Mike A1 - Kovacs, Oliver A1 - Droste, Bernhard T1 - Application limits of low-ductile cast iron for radioactive waste containers T2 - PATRAM 2007, 15th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Miami, Florida, USA DA - 2007-10-21 KW - Ductile iron KW - Container design KW - Safety assessment KW - Fracture mechanics KW - Dynamic loading conditions PY - 2007 IS - Session B, Paper #97 SP - 1 EP - 8 PB - Institute of Nuclear Materials Management AN - OPUS4-18399 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Komann, Steffen A1 - Droste, Bernhard A1 - Wille, Frank A1 - Rittscher, D. T1 - Mechanical assessment of large nuclear power plant components in transport licensing T2 - 49th INMM Annual Meeting CY - Nashville, TN, USA DA - 2008-07-13 KW - Rückbau KW - Kerntechnische Anlagen KW - Großkomponenten KW - Transport KW - Mechanik PY - 2008 SP - 1 EP - 8 AN - OPUS4-18440 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Goedecke, Thomas A1 - Balke, Christian A1 - Probst, Ulrich T1 - Test Facilities on the Open-Air Test Site of the Federal Institute for Materials Research and Testing (BAM) T2 - Dimensions. 06, The International Forum on Transport Packaging CY - San Antonio, Texas, USA DA - 2006-04-18 KW - Test Facilities KW - Fire Tests PY - 2006 SP - 1 EP - 7 AN - OPUS4-18430 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dey, Anika A1 - Thomas, Hans-Martin A1 - Pohl, Rainer T1 - The important role of eddy current testing in railway track maintenance T2 - 17th World Conference on Non-Destructive Testing CY - Shanghai, China DA - 2008-10-25 KW - Eddy current testing KW - Rolling contact fatigue KW - Head checking KW - Rail maintenance KW - Grinding train PY - 2008 IS - Paper 393 SP - 1 EP - 4 PB - International Committee for Non-Destructive Testing CY - Shanghai AN - OPUS4-18433 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kreutzbruck, Marc A1 - Allweins, K. A1 - Strackbein, C. A1 - Bernau, H. T1 - High Resolution Eddy Current Testing of Superconducting Wires using GMR-Sensors T2 - 17th World Conference on Non-Destructive Testing CY - Shanghai, China DA - 2008-10-25 KW - GMR-sensor KW - Eddy Current Testing KW - Reconstruction KW - Superconducting wires PY - 2008 IS - Paper 389 SP - 1 EP - 6 PB - International Committee for Non-Destructive Testing CY - Shanghai AN - OPUS4-18434 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Döring, Joachim A1 - Bovtun, V. A1 - Bartusch, Jürgen A1 - Beck, Uwe A1 - Kreutzbruck, Marc T1 - Cellular polypropylene ferroelectret film: piezoelectric material for non-contact ultrasonic transducers T2 - 17th World Conference on Non-Destructive Testing CY - Shanghai, China DA - 2008-10-25 KW - Air-coupled ultrasound KW - Ultrasonic transducers KW - Electromechanical properties KW - Piezoelectric materials KW - Impedance spectroscopy PY - 2008 IS - Paper 123 SP - 1 EP - 6 PB - International Committee for Non-Destructive Testing CY - Shanghai AN - OPUS4-18435 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brekow, Gerhard A1 - Boehm, Rainer A1 - Brackrock, Daniel A1 - Kreutzbruck, Marc T1 - Quantitative Defect Sizing on Components with Different Wall Thickness using UT-SAFT T2 - 17th World Conference on Non-Destructive Testing CY - Shanghai, China DA - 2008-10-25 KW - UT-SAFT KW - Reconstruction PY - 2008 IS - Paper 122 SP - 1 EP - 6 PB - International Committee for Non-Destructive Testing CY - Shanghai AN - OPUS4-18436 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Correlation between material parameters of high density polyethylene grades and the test performance behavior of packagings T2 - NACE International corrosion conference 2009 CY - Atlanta, Georgia, USA DA - 2009-03-22 KW - Dangerous goods packagings KW - HDPE grades KW - Material parameters KW - Design type tests PY - 2009 SP - 1 EP - 13 (Paper 09328) AN - OPUS4-19257 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Thiele, Joachim A1 - Behrens, Frauke ED - Davies, P. T1 - The future of the German accreditation system PY - 2009 IS - 35 SP - 23 EP - 26 PB - ILAC Secretariat AN - OPUS4-19357 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Weber, Mike A1 - Qiao, Linan A1 - Menzel, Martin A1 - Droste, Bernhard T1 - Beurteilungsmethoden für Transport- und Lagerbehälter mit erhöhten metallischen Reststoffanteilen - Behälterbruchsicherheitsuntersuchungen und Entwicklung eines KONRAD-Referenzprüfstandfundamentes T2 - 9. Internationales Symposium "Konditionierung radioaktiver Betriebs- und Stilllegungsabfälle" (KONTEC 2009) CY - Dresden DA - 2009-04-15 KW - Duktiles Gusseisen KW - Behälterdesign KW - Sicherheitstechnische Bewertung KW - Bruchmechanik KW - Dynamische Belastungsbedingungen KW - KONRAD KW - Referenzprüfstandfundament PY - 2009 SP - 646 EP - 652 PB - KONTEC CY - Hamburg AN - OPUS4-19396 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Töpfer, J. A1 - Mürbe, J. A1 - Kracunovska, S. A1 - Barth, S. A1 - Pawlowski, B. A1 - Bartnizek, T. A1 - Glitzky, Carsten A1 - Rabe, Torsten T1 - LTCC-compatible multilayer ferrites for integrated inductors T2 - 10th International Conference on Ferrites CY - Chengdu, China DA - 2008-10-10 KW - Hexagonal ferrites KW - Multilayer inductors KW - Ni-Cu-Zn ferrites KW - LTCC KW - Integrated inductors PY - 2008 SP - 147 EP - 150 CY - Chengdu, China AN - OPUS4-19426 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bletzer, Claus Wilhelm A1 - Zencker, Uwe A1 - Völzke, Holger A1 - Koch, Frank T1 - Asymmetrische Temperaturprofile in Transport- und Lagerbehältern für radioaktive Stoffe T2 - Jahrestagung Kerntechnik CY - Dresden, Deutschland DA - 2009-05-12 KW - Temperaturprofil KW - CFD-Berechnung KW - Transportbehälter KW - Radioaktive Stoffe PY - 2009 SP - 1 EP - 5(?) CY - Dresden AN - OPUS4-19431 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Magallanes, J.M. A1 - Martinez, R. A1 - Neser, A. A1 - Schreiber, D. A1 - Zencker, Uwe T1 - A comprehensive material testing program for characterizing concrete behaviors under dynamic loads T2 - 13th International symposium on interaction of the effects of munitions with structures, ISIEMS 13 CY - Brühl, Germany DA - 2009-05-11 KW - Concrete properties KW - Dynamic testing KW - Dynamic load KW - Triaxial compression test KW - Storage cask KW - Modified split-Hopkinson pressure bar (SHPB) KW - Moisture PY - 2009 IS - Paper # 46 SP - 1 EP - 13(?) CY - Brühl, Deutschland AN - OPUS4-19452 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schulz-Forberg, Bernd A1 - Balke, Christian T1 - Ereignisauswertung bei der Störfallkommission (SFK) PY - 2005 VL - 6 SP - 53 EP - 55 PB - Vds Schadenverhütung Verl. CY - Köln AN - OPUS4-19434 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Helmerich, Rosemarie T1 - Opportunities and limitation of non-destructive testing in condition assessment of bridge structures T2 - Munich bridge assessment conference (MBAC 2009) CY - Munich, Germany DA - 2009-05-27 KW - Non-destructive testing KW - Condition assessment KW - Data fusion KW - Concrete bridges PY - 2009 SP - 1 EP - 13 AN - OPUS4-19597 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zunkel, Astrid A1 - Erning, Johann Wilhelm T1 - Kugelhähne und typische Schadensursachen PY - 2009 VL - 2009 SP - 60 EP - 62 PB - Strobel CY - Arnsberg AN - OPUS4-19520 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niebergall, Ute A1 - Mertlova, O. A1 - Nezbedova, E. T1 - Full notch creep test for evaluation of PE-HD materials for container and pipes T2 - EUROCORR 2009 CY - Nice, France DA - 2009-09-06 KW - FNCT KW - Container KW - Pipes KW - PE-HD materials KW - Round robin test PY - 2009 IS - SS 9-O-7965 SP - 1 EP - 6 AN - OPUS4-20497 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ludwig, Jörg T1 - Explosionsdruckstoßfestigkeit von Transporttanks T2 - 3. Jahrestagung der VDI-Gesellschaft Werkstofftechnik CY - Technische Universität München, Deutschland DA - 1987-03-19 PY - 1987 SP - 199 EP - 208 CY - Düsseldorf AN - OPUS4-20471 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ludwig, Jörg A1 - Konersmann, Rainer A1 - Peinelt, I. T1 - Safety considerations for the transport and storage of dangerous goods, based on the example of pipelines PY - 2002 SP - 143 EP - 185 PB - NATO CY - Ankara AN - OPUS4-20440 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Prager, Jens A1 - Petersson, B.A.T. ED - Mace, Brian R. ED - Ferguson, Neil S. ED - Rustighi, Emiliano T1 - Improvements on the statistical sound field description using waterhouse correction N2 - The diffuse field assumption employed in Statistical Energy Analysis (SEA) and in statistical room acoustics is violated for source and receiver positions close to boundaries or discontinuities. An approach is suggested to include the correction made by Waterhouse based on spherical Bessel functions in SEA predictions. With this modification the SEA results will be augmented by a position dependence and an additional frequency dependence. The approach is extended and demonstrated for plate-like structures with different boundary conditions. The validity of the approach is confirmed by means of comparisons with modal analysis and finite element calculations. T2 - NOVEM 2009 - Noise and Vibration: Emerging Methods CY - Oxford, UK DA - 2009-04-05 KW - SEA PY - 2009 IS - Contributed Papers / Chapt. 5 SP - 042-1 - 042-8 AN - OPUS4-20586 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ludwig, Jörg A1 - Ulrich, Armin T1 - Safety valves in full scale fire testing T2 - Tenth International Symposium on the Transport of Dangerous Goods by Sea and Inland Waterways CY - Hamburg, Germany DA - 1989-09-25 PY - 1989 SP - 85 EP - 96 PB - Storck CY - Hamburg AN - OPUS4-20520 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ludwig, Jörg A1 - Günther, Burkhard T1 - Flameproof-design of portable tanks T2 - Eleventh International Symposium on the Transport of Dangerous Goods by Sea and Inland Waterways CY - Tokyo, Japan DA - 1992-11-09 PY - 1992 SP - 181 EP - 194 CY - Tokyo AN - OPUS4-20521 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ludwig, Jörg T1 - Compatibility-related tank container approvals T2 - MariChem97 CY - Congress Centrum Ost, KölnMesse, Germany DA - 1997-12-02 PY - 1997 CY - Uxbridge, England AN - OPUS4-20503 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - BOOK A1 - Fuhrmann, G. A1 - Jablonski, H. A1 - Lehnecke, H.-H. A1 - Thiele, Joachim A1 - Wagenführ, L.-P. T1 - Material- und Warenprüfung in der DDR - Anspruch und Wirklichkeit PY - 2010 SP - 1 EP - 233 PB - Beuth CY - Berlin AN - OPUS4-20504 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Komann, Steffen A1 - Droste, Bernhard A1 - Wille, Frank T1 - Transport of large nuclear power plant components - experiences in mechanical design assessment T2 - Ramtransport 09 - 8th International Conference on radioactive materials transport 2009 CY - Manchester, Great Britain DA - 2009-05-12 KW - Rückbau KW - Kerntechnische Anlagen KW - Großkomponenten KW - Transport KW - Mechanik PY - 2009 IS - Session 5 / PAP 12 SP - 1 EP - 8 AN - OPUS4-20557 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Diel, W. A1 - Waßmer, M. A1 - Krüger, K. A1 - Naghib Zadeh, Hamid A1 - Rabe, Torsten T1 - Einfluss unterschiedlicher Dielektrika bei der Realisierung von Dickschichtkondensatoren im Tintenstrahldruck T2 - Deutsche IMAPS-Konferenz 2009 CY - München, Deutschland DA - 2009-10-27 KW - Tintenstrahldruck KW - Inkjet KW - High-K Keramik KW - Kondensator KW - Dickschicht KW - Bariumtitanat PY - 2009 SP - 1 EP - 8 AN - OPUS4-20613 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krahl, Thoralf A1 - Gildenhaar, Renate A1 - Kenning, Hilke A1 - Berger, Georg A1 - Jäger, Christian ED - Kim, Sukyoung T1 - Predicting phase compositions of samples in the ternary system Ca2KNa(PO4)2-Ca3(PO4)2-Ca2P2O7 using 31P MAS NMR T2 - 22nd International symposium on ceramics in medicine (Bioceramics 22) CY - Daegu, Korea DA - 2009-10-26 KW - NMR KW - Bone substitute materials KW - Alkali calcium phosphates KW - TCP KW - Ca10(K,NA)(PO4)7 PY - 2009 SP - 11 EP - 14 AN - OPUS4-20656 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Taffe, Alexander T1 - Validierung zerstörungsfreier Prüfverfahren im Bauwesen - Wie sicher sind die Resultate? T2 - Zielorientierte Bauwerksuntersuchungen mit neueren zerstörungsfreien Prüfverfahren (ZfP) - Fachveranstaltung 894631/32 CY - Wildegg, Schweiz DA - 2009-11-26 KW - Zerstörungsfreie Prüfung im Bauwesen KW - Validierung KW - Messunsicherheit KW - GUM PY - 2009 IS - Kap. 2 SP - 1 EP - 10 CY - Wildegg, Schweiz AN - OPUS4-20606 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Taffe, Alexander T1 - Stand der Forschung und Anwendung von zerstörungsfreien Prüfverfahren (US, IE, Radar) und neuere Entwicklungen in Deutschland T2 - Zielorientierte Bauwerksuntersuchungen mit neueren zerstörungsfreien Prüfverfahren (ZfP) - Fachveranstaltung 894631/32 CY - Wildegg, Schweiz DA - 2009-11-26 KW - Zerstörungsfreie Prüfung im Bauwesen KW - LIBS KW - Remanenzmagnetismus KW - Automatisierung KW - Baustellenscanner KW - OSSCAR KW - SAFT PY - 2009 IS - Kap. 1 SP - 1 EP - 15 CY - Wildegg, Schweiz AN - OPUS4-20607 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Osterloh, Kurt A1 - Ewert, Uwe T1 - Visual perception of spatial subjects T2 - DIR 2007 - International Symposium on Digital industrial Radiology and Computed Tomography CY - Lyon, France DA - 2007-06-25 KW - Image (data) processing KW - Image interpretation KW - Physiological capabilities and constraints KW - Visibility of certain features KW - Perception of a subject PY - 2007 SP - 1 EP - 8 CY - Lyon, France AN - OPUS4-20713 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rethmeier, Michael A1 - Gook, Sergej A1 - Gumenyuk, Andrey T1 - Perspectives of application of laser-GMA-hybrid girth welding for pipeline construction T2 - VI. International conference "Beam technologies & laser application" CY - Saint Petersburg, Russia DA - 2009-09-23 KW - Fibre laser KW - Laser-hybrid welding PY - 2009 SP - 1 EP - 15(?) CY - Saint Petersburg, Russia AN - OPUS4-20766 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mishra, Kirti Bhushan A1 - Wehrstedt, Klaus-Dieter A1 - Schönbucher, A. T1 - Measurement and CFD prediction of gas velocities and temperatures in large pool fires of organic peroxides T2 - 36th National conference on fluid mechanics and fluid power - NCFMFP-2009 CY - Pune, India DA - 2009-12-17 KW - Pool fire KW - TBPB KW - TBPEH KW - Froude number KW - CFD (Computational fluid dynamics) PY - 2009 IS - Paper 58-CFD-5 SP - 1 EP - 11 AN - OPUS4-20769 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völzke, Holger A1 - Wolff, Dietmar A1 - Probst, Ulrich T1 - Advanced investigations to evaluate spent fuel cask safety for extended storage periods T2 - 50th Annual Meeting of the Institute of Nuclear Materials Management (INMM) CY - Tucson, Arizona, USA DA - 2009-07-12 KW - Behälter KW - Beständigkeit KW - Sicherheit KW - Dichtungen KW - Polymere KW - Lagerung KW - Radioaktive Stoffe PY - 2009 SP - 1 EP - 10 AN - OPUS4-20707 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Osterloh, Kurt A1 - Zscherpel, Uwe A1 - Ewert, Uwe T1 - Visualisation of radioactive materials and backscatter radiography with a novel collimation based camera system T2 - 4th Security research conference Karlsruhe CY - Karlsruhe, Germany DA - 2009-09-29 KW - Kamera für hochenergetische Strahlung KW - Bildliche Wiedergabe der Formen von Strahlenquellen KW - Röntgenrückstreustrahlung KW - Anwendung für die öffentliche Sicherheit (Security) PY - 2009 IS - #052 SP - 1 EP - 8 AN - OPUS4-20712 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Maiwald, Michael A1 - Gasch, A. A1 - Gerlach, M. A1 - Kaiser, U. A1 - Kloska, M. A1 - Matalla, N. A1 - Morr, W. A1 - Panzke, R. A1 - Stieler, S. A1 - Westerkamp, D. T1 - Prozess-Sensoren 2015+ - Technologie-Roadmap für Prozess-Sensoren in der chemisch-pharmazeutischen Industrie PY - 2009 SP - 1 EP - 71 AN - OPUS4-20699 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Illerhaus, Bernhard A1 - Staude, Andreas A1 - Meinel, Dietmar T1 - Nondestructive insights into composition of the sculpture of Egyptian Queen Nefertiti with CT and the dependence of object surface from image processing N2 - Precautions in the generation of surfaces from CT images should be the rule. Two different data sets of the bust of Nefertiti and additional data from an industrial CT scanner will show the conflicts that arise when defining a surface. The recent trend in CT is to extract surfaces from CT measurements which can compete with the accuracy of tactile measurements. As CT is complicated by artefacts, a lot of precautions need to be taken in order to get exact results. More errors are introduced, if the surface of an object made from different dense materials is calculated. A publication in April 2009 of "Radiology" dealt with the surface of the stone behind the stucco layer of the famous bust of the Egyptian Queen Nefertiti in the Ägytische Museum Berlin. Using this data, we will show the different problems that arise from inadequate image processing. Furthermore, a detailed comparison of the two CT measurements made 14 years apart is given. Conclusions: Respect the traps in virtual imaging. KW - Image processing (computer-assisted) KW - Computed X ray tomography KW - Artifacts KW - Implants KW - Computertomographie KW - Oberfläche KW - Oberflächenbestimmung PY - 2009 UR - https://www.ndt.net/search/docs.php3?id=8043 SN - 1435-4934 VL - 14 IS - 9 SP - 1 EP - 11 PB - NDT.net CY - Kirchwald AN - OPUS4-20840 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kind, Thomas T1 - Study of the behaviour of a multi-offset antenna array on railway ballast T2 - 12th International conference on ground penetrating radar (GPR08) CY - Birmingham, UK DA - 2008-06-15 KW - Railway KW - Ballast KW - Track bed investigation PY - 2008 SP - 1 EP - 5 AN - OPUS4-20841 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosner, Martin A1 - Peucker-Ehrenbrink, B. A1 - Bach, W. T1 - Osmium isotope and PGE variations in oceanic core complexes: Atlantis Massif, a typical crustal section formed at a MAR T2 - Jahrestagung Deutsche Mineralogische Gesellschaft 2008 CY - Berlin, Deutschland DA - 2008-09-14 KW - Oceanic core complexes KW - Atlantis Massif KW - Osmium isotopes PY - 2008 SP - 1 CY - Berlin AN - OPUS4-20784 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosner, Martin A1 - Pritzkow, Wolfgang A1 - Vogl, Jochen T1 - Boron isotope compositions of food: A potential tool for food authentication T2 - Jahrestagung Deutsche Mineralogische Gesellschaft 2008 CY - Berlin, Deutschland DA - 2008-09-14 KW - Boron isotopes KW - Food KW - Provenance studies PY - 2008 SP - 1 CY - Berlin AN - OPUS4-20785 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosner, Martin A1 - Wiedenbeck, M. A1 - Ludwig, T. T1 - Determination of true boron isotope compositions of silicate glasses by SIMS: NIST SRM glasses and composition-induced variations in SIMS instrumental mass fractionation T2 - Jahrestagung Deutsche Mineralogische Gesellschaft 2008 CY - Berlin, Deutschland DA - 2008-09-14 KW - SIMS KW - Boron isotopes KW - Instrumental mass bias PY - 2008 SP - 1 CY - Berlin AN - OPUS4-20786 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wiggenhauser, Herbert A1 - Streicher, Doreen T1 - Non-destructive testing of bridges T2 - 4th International conference on construction materials (ConMat'09) CY - Nagoya, Japan DA - 2009-08-24 KW - Bridge investigations KW - Radar KW - Impact-echo KW - Ultrasonic echo KW - Data fusion KW - Scanning system PY - 2009 IS - Invited Lecture 1 SP - 1 EP - 7 AN - OPUS4-20794 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schneider-Gloetzl, J. A1 - Gloetzl, R. A1 - Krebber, Katerina A1 - Liehr, Sascha A1 - Wendt, Mario A1 - Wosniok, Aleksander T1 - Geotechnical monitoring of construction activities by distributed fiber optic sensors embedded in geotextiles T2 - 5th European workshop on structural-health-monitoring 2010 CY - Sorrento, Italy DA - 2010-06-29 KW - Foundation engineering KW - Geotechnical monitoring KW - Smart textiles KW - Distributed fiber optic sensors KW - POF sensors KW - Brillouin sensors PY - 2010 IS - SS4-07 SP - 1 EP - 6 AN - OPUS4-21872 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Srinivasan, P. A1 - Wiggenhauser, Herbert A1 - Murthy, S.G.N. A1 - Bhaskar, S. A1 - Ravisankar, K. A1 - Iyer, N.R. T1 - Advanced non-destructive testing methods for application to reinforced concrete structures - Collaborative research between SERC and BAM N2 - Nondestructive testing (NDT) of concrete structures plays an important role in civil engineering. CSIR-SERC, India, for the past three decades involved in the conditon assessment of civil infrastructures based on the expertise and the methodology developed in the area of NDT. Prof., Wiggenhauser, BAM, Berlin visited SERC, under the CSIR- Humboldt Reciprocity Research Award for 2006. During his visit, scientists of SERC have gained knowledge in the area of advanced NDT methods. A unique large scale two storied reinforced concrete specimen was cast at SERC, with columns and beams of different sizes, cross section having different percentages of reinforcement. The defects suc has honeycombs, cracks, delamination, presence od conduits, ducts, etc. were also incorporated. Facilities were created at SERC in the area of advanced NDT methods. BAM, Germany, has offered assistance to three scientists of SERC to work at BAM and to have further exposure in the area of advanced NDT methods. One of the scientists is pursuing Ph.D., in the application of advanced NDT methods for identification of damage in concrete structures. Activities have been carried out on the NDT-CE (Non-Destructive Testing in Civil Engineering) Compendium which is a compilation of the descriptions of 115 methods. It is freely accessible on the Internet. This paper highlights the collaborative research work carried out by SERC and BAM in the area of advanced NDT methods for the evaluation of defects/ damage in reinforced concrete structures and also as a quality assurance tool. The future programme of work is also discussed. T2 - 5th World conference on structural control and monitoring (5WCSCM) CY - Tokyo, Japan DA - 2010-07-12 PY - 2010 IS - A-7 / 044 SP - 1 EP - 11 CY - Tokyo, Japan AN - OPUS4-21925 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard T1 - Wie sicher sind CASTOR-Behälter? T2 - Praxisseminar "Radioaktive Stoffe - Recht, Umgang und Beförderung von Gütern der Klasse 7" CY - München, Deutschland DA - 2001-12-10 PY - 2001 IS - 069.01 SP - 1 EP - 15 PB - Moderne Industrie AG & Co. KG CY - Landsberg AN - OPUS4-21861 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Niebergall, Ute T1 - Comparison of the stress crack resistance of polyethylene grades with the test performance behaviour of packagings for the transport of dangerous goods N2 - Resistance to stress cracking by wetting solution is one of the selected properties together with the corresponding test method FNCT and tolerances for a comparison of polyethylene grades of one design type in the procedural rule on suitability proof for alternative plastic resins used for packagings and intermediate bulk containers (IBCs) for the transport of dangerous goods. The environmental stress crack resistance determined by Full Notch Creep Test (FNCT) represents the impacts from the stacking tests at 40 °C performed with standard liquid wetting solution (without pre-storage) and with normal butyl acetate saturated wetting solution (pre-storage with normal butyl acetate). Environmental stress crack resistance determined with FNCT for the polyethylene grades was related to the times to failure of different jerrican samples made of these grades in stacking tests with 5% wetting solution and a n-butyl acetate saturated wetting solution (pre-storage with n-butyl acetate) at 40 °C. The FNCT is suitable for comparison of polyethylene grades in relation to environmental stress crack resistance independent of their use as drum, IBC or jerrican material. The stiffness of polyethylene grades should be taken into account to the comparison as jerricans are not only chemically but also mechanically stressed. T2 - EUROCORR 2010 CY - Moscow, Russia DA - 2010-09-13 KW - Polyethylenformstoffe KW - Gefahrgutverpackungen KW - Spannungsrissbeständigkeit KW - Stapeldruckprüfungen PY - 2010 N1 - Serientitel: EFC-Event – Series title: EFC-Event IS - 324 SP - 1 EP - 6 PB - DECHEMA CY - Moscow AN - OPUS4-21974 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Müller, Urs A1 - Ziegert, Christof A1 - Röhlen, U. A1 - Schroeder, H. T1 - Standardization of a sustainable and eco-efficient building material: Earth - a german perspective T2 - CESB '10 - Central Europe Towards Sustainable Building CY - Prague, Czech Republic DA - 2010-06-30 KW - Earthen materials KW - Standardization KW - Sustainability KW - Quality control KW - Normierung KW - Lehmbaustoffe KW - Prüfverfahren KW - Qualitätskontrolle KW - Nachhaltigkeit KW - Stoffkreislauf PY - 2010 SN - 978-80-247-3624-2 SP - 711 EP - 714 PB - Czech Technical University CY - Prague AN - OPUS4-21980 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Patrick P. A1 - Wiggerich, B. A1 - Bartholmai, Matthias T1 - Micro-drone for the characterization and self-optimizing search of hazardous gaseous substance sources T2 - IMAV 2010 - International micro air vehicle conference and flight competition CY - Braunschweig, Germany DA - 2010-07-06 KW - Mikrodrohne KW - Quadrokopter KW - Robotik KW - Suche und Lokalisierung von gasförmigen Gefahrstoffquellen PY - 2010 SP - 1 EP - 5 AN - OPUS4-22051 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lang, Cindy A1 - Hübert, Thomas ED - Kupfer, K. ED - Wagner, N. ED - Wagner, R. ED - Bonitz, F. ED - Müller, B. ED - Hübner, C. T1 - "Künstliche Früchte" - Online-Monitoring des Feuchtigkeitsverlustes bei pflanzlichen Frischeprodukten T2 - Aquametry 2010 - 1st European conference on moisture measurement CY - Weimar, Deutschland DA - 2010-10-05 KW - Ausgleichsfeuchte KW - Wasseraktivität KW - Transpiration KW - Nachernteverhalten PY - 2010 SP - 333 EP - 339 AN - OPUS4-22167 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schön, Wolfgang A1 - Droste, Bernhard T1 - Wasserberieselung im Brandversuch T2 - Seminar Nr. S-70-001-096-8 Wasserberieselung CY - Essen, Deutschland DA - 1988-12-05 PY - 1988 SP - 1 EP - 12 PB - Haus d. Technik CY - Essen AN - OPUS4-22130 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Protz, Christian A1 - Völzke, Holger A1 - Zencker, Uwe A1 - Hagenow, Peter A1 - Grünewald, Heike T1 - Entwicklung neuer Prüfmethoden zur numerischen Beanspruchungsanalyse für die Fallprüfung an Stahlblechcontainern für das Endlager Konrad N2 - Die Bundesanstalt für Materialforschung und -prüfung (BAM) führt im Rahmen einer Verwaltungsvereinbarung mit dem Bundesamt für Strahlenschutz (BfS) Bauartprüfungen für Behältertypen durch, die für die Endlagerung von nicht wärmeentwickelnden radioaktiven Abfällen in das Endlager Konrad vorgesehen sind. Zur Erlangung einer Eignungsbestätigung einer Behälterbauart für das Endlager Konrad müssen die Antragssteller die Einhaltung der vom BfS festgelegten behälterspezifischen Anforderungen nachweisen. Zentrale Bestandteile der Bauartprüfung sind die Sicherheitsnachweise zur Behälterauslegung gegen mechanische Betriebs- und Störfallbelastungen sowie gegen thermische Störfallszenarien. Die Prüfanforderungen umfassen hierbei Stapeldruckprüfung, Hebeprüfung, Fallprüfung, thermische Prüfung (Brand), ggf. einschließlich Dichtheitsprüfung zum Nachweis der Einhaltung von Dichtheitsanforderungen. Neben der Nachweisführung mittels sogenannter Baumusterprüfungen oder Obertragbarkeitsbetrachtungen können die Nachweise alternativ mittels numerischer Sicherheitsnachweise erbracht werden, sofern deren hinreichende Verifikation nachgewiesen wird, Dies kann u. a. durch den Vergleich mit hinreichend gesicherten experimentellen Ergebnissen geschehen, Die hier vorgestellten Untersuchungen sind Teil des internen Forschungsprojektes ConDrop der BAM, das zum Ziel hat, erweiterte Prüfmethoden zur Fallprüfung an Stahlblechcontainern für das Endlager Konrad mittels numerischer Beanspruchungsanalyse zu entwickeln. Dazu soll ein Finite-Elemente-(FE)-Modell entwickelt und mit experimentellen Daten, die in Fallversuchen ermittelt werden, verifiziert werden. T2 - Jahrestagung Kerntechnik 2011 CY - Berlin, Deutschland DA - 17.05.2011 KW - Falltest KW - Stahlblechcontainer KW - Endlager Konrad KW - Numerische Beanspruchungsanalyse PY - 2011 IS - Session TS-19 / Paper 161 SP - 1 EP - 3 AN - OPUS4-23755 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ballheimer, Viktor A1 - Wille, Frank A1 - Droste, Bernhard T1 - Mechanical safety analysis for high burn-up spent fuel assemblies under accident transport conditions T2 - PATRAM 2010 - 16th International symposium on the packaging and transport of radioactive materials CY - London, UK DA - 2010-10-03 KW - Accident transport conditions KW - Fuel rods KW - High burn-up KW - Failure PY - 2010 SP - 1 EP - 8(?) AN - OPUS4-23760 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Recknagel, Sebastian A1 - Kipphardt, Heinrich A1 - Lange, Britta A1 - Hoppe, Marion T1 - Traceable analysis of impurities in metallic reference materials using GD-MS N2 - The traceabiiity requirements for certification analyses of reference materials are much more stringent than for routine analysis, where certified matrix reference materials (CRM) can be used for calibration and to establish traceabiiity. Although the ISO-Guides related to CRM production and certification are not fully clear concerning calibration, many established CRM-producers do not accept matrix-CRMs for calibration in case of certification analyses, e.g. to avoid circular reasoning. These requirements limit the methods used for certification to those that can be calibrated using Standards of known high purity and stoichiometry or mixtures of such Standards. Powerful solid sampling techniques such as glow discharge mass spectrometry (GD-MS) or spark-optical emission spectrometry (SOES), where usually compact CRMs are used for calibration, seem not be applicable for certification analyses. Especially GD-MS is a powerful tool for trace element determination of solid samples. Beside metallic impurities the use of specific gas mixtures enables also the determination of interesting nonmetallic impurities such as sulfur and phosphorus. Within BAM a calibration approach, was developed which enables to use mixtures of Standards of known high purity and stoichiometry also for GD-MS. Analogue to matrix adaption in solution based techniques, the calibration approach is based on doped pressed powder pellets. Approach and application on the certification analyses of copper and Steel CRMs are presented. T2 - CETAS 2011 - 8th International workshop on progress in analytical chemistry & materials characterisation in the steel and metal industries CY - Luxembourg, Luxembourg DA - 17.05.2011 PY - 2011 IS - OC53 SP - 361 EP - 365 AN - OPUS4-23762 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kasparek, Eva Maria A1 - Scheidemann, Robert A1 - Wolff, Dietmar A1 - Zencker, Uwe A1 - Völzke, Holger T1 - Untersuchungen zum Verhalten von Dämpferbeton unter Stossbelastung N2 - Während des Transportes sind Behälter für hoch radioaktive Abfälle durch stoßdämpfende Bauteile vor Einwirkungen, die aus Unfallszenarien gemäß den IAEA Regularien resultieren können, weitestgehend geschützt. Nach dem Entfernen dieser Komponenten im Rahmen der Einlagerung ins Zwischenlager müssen Vorkehrungen getroffen sein, um Beanspruchungen der Behälter aus möglichen Handhabungsunfällen im Empfangsbereich zu reduzieren. Die Maßnahmen müssen vor allem darauf abzielen, die stoßdämpfenden Eigenschaften der potentiellen Aufprallflächen zu optimieren. Da Standardmaterialien für Fundamente nur ein geringes Energieabsorptionsvermögen aufweisen, wurde durch die Firma HOCHTIEF eine neuartige Betonmixtur entwickelt, bei der ein spezieller Leichtzuschlag zum Einsatz kommen. Zur Charakterisierung dieses sogenannten Dämpferbetons liegen Standardkennwerte vor sowie Messwerte aus Eindringversuchen, die zur Qualitätssicherung für jede Produktcharge durchgeführt werden. Das stoßdämpfende Potential des neuen Werkstoffs kann jedoch nur dann vollkommen ausgeschöpft werden, wenn die Energieabsorption in numerischen Simulationen der Behälterabstürze über die gesamte Belastungsdauer zuverlässig wiedergegeben wird. Für die Implementierung und Anpassung eines entsprechenden Materialmodelis in einem Finite Elemente (FE) Programm sind Daten aus systematischen Druckversuchen mit Variation der relevanten Einflussgrößen erforderlich. An der BAM werden daher im Rahmen eines werkstoffübergreifenden Forschungsvorhabens zur Untersuchung von stoßdämpfenden Strukturen auch die Eigenschaften von Dämpferbeton experimentell untersucht und zugehörige numerische Methoden entwickelt. Der aktuelle Beitrag behandelt die Ergebnisse der ersten Projektphase, in der kubische Probekörper mit der Kantenlänge 100mm bei unterschiedlichen Lagerungsbedingungen statisch und dynamisch gestaucht wurden. In nachfolgenden Versuchen wird der Einfluß der Probengröße ermittelt sowie die Eignung der verwendeten Materialmodelle anhand realistischer Belastungssituationen validiert. Versuchsprogramm. T2 - Jahrestagung Kerntechnik 2011 CY - Berlin, Germany DA - 17.05.2011 KW - Stoßdämpfende Werkstoffe KW - Materialmodellierung KW - Versuchsprogramm KW - Stoßbelastung KW - Dehnratenabhängigkeit KW - Temperaturabhängigkeit KW - Polyurethan Schaum KW - Dämpferbeton PY - 2011 IS - Session TS-17 / Paper 171 SP - 1 EP - 5 AN - OPUS4-23836 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Weber, Mike A1 - Wille, Frank T1 - Finite element mesh design of a cylindrical cask under puncture drop test conditions N2 - Transport casks for radioactive materials have to withstand the 9 m drop test, 1 m puncture drop test and dynamic crush test with regard to the mechanical requirements according to the IAEA regulations. The safety assessment of the package can be carried out on the basis of experimental investigations with prototypes or models of appropriate scale, calculations, by reference to previous satisfactory safety demonstrations of a sufficiently similar nature or a combination of these methods. Computational methods are increasingly used for the assessment of mechanical test scenarios. However, it must be guaranteed that the calculation methods provide reliable results. Important quality assurance measures at BAM are given concerning the preparation, run and evaluation of a numerical analysis with reference to the appropriate guidelines. Hence, a successful application of the finite element method requires a suitable mesh. An analysis of the 1 m puncture drop test using successively refined finite element meshes was performed to find an acceptable mesh size and to study the mesh convergence using explicit dynamic finite element codes. The finite element model of the cask structure and the puncture bar is described. At the beginning a coarse mesh was created. Then this mesh was refined in two steps. In each step the size of the elements was bisected. The deformation of the mesh and the stresses were evaluated dependent on the mesh size. Finally, the results were extrapolated to an infinite fine mesh or the continuous body, respectively. The uncertainty of the numerical solution due to the discretization of the continuous problem is given. A safety factor is discussed to account for the uncertainty. The calculation results are compared with experimental data from a puncture drop test with a half-scale model of a cylindrical cask. This paper supports the convergence studies of the Task Group on Computational Modeling for Explicit Dynamics reporting to the ASME BPV Code Working Group on Design Methodology. T2 - PATRAM 2010 - 16th International symposium on the packaging and transport of radioactive materials CY - London, UK DA - 2010-10-03 KW - IAEA puncture drop test KW - Numerical analysis KW - Verification KW - Explicit dynamics PY - 2010 SP - 1 EP - 8 (Session T45 / Paper 219) AN - OPUS4-23843 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Weber, Mike A1 - Qiao, Linan A1 - Droste, Bernhard A1 - Völzke, Holger T1 - Mechanical safety analyses of cast iron containers for the KONRAD repository N2 - Within the last years BAM has carried out numerous drop tests with prototype casks made of ductile cast iron onto targets according to the requirements for final disposal of non-heat generating waste in the German KONRAD repository. The results have shown that the target specifications in the acceptance criteria have to be defined more accurately to get reproducible test results with high precision. Hence, a suitable test stand foundation was developed with much effort. The integrity of the upper concrete layer of this target must be preserved during a test. Recently the geometrical properties of a tested cubic cast iron container led to a concentration of the impact forces beneath the container walls. The target was damaged strongly with the consequence of inadmissible reduction of cask stresses. For that reason the target construction was modified. However, the basic design was not changed. A prefabricated concrete slab was still joined by a mortar layer to the IAEA target of the BAM drop test facility. In the course of the optimization of the test stand foundation the concrete slab dimensions and the reinforcement were enlarged. During the drop test repetition the target kept intact. Additionally, the mechanical behavior of the cast iron container and the target was analyzed by finite element calculations. This improved target construction is suggested as a reference target for drop tests with casks whose mass and base area are covered by the container types VI or VII respectively according to the KONRAD repository acceptance criteria. The measurements during the drop tests with cast iron casks have provided the strains on the cask surface at selected positions. This allows the verification of finite element simulations of drop tests which show the stress distribution also inside the component. In September 2008 a drop test was carried out with a cylindrical cast iron cask containing an artificial material defect which was designed under consideration of critical stress states in the cask body. This drop test could demonstrate the safety against failure by fracture of a cask made of a special cast iron with reduced fracture toughness. T2 - PATRAM 2010 - 16th International symposium on the packaging and transport of radioactive materials CY - London, UK DA - 2010-10-03 KW - Ductile iron KW - Container design KW - Safety assessment KW - Fracture mechanics KW - Dynamic loading conditions PY - 2010 SP - 1 EP - 8 (Session T28 / Paper 220) AN - OPUS4-23844 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niebergall, Ute A1 - Weltschev, Margit T1 - Comparison of the stress crack resistance of polyethylene grades with the test performance behaviour of packagings for the transport of dangerous goods N2 - Resistance to stress cracking by wetting solution is one of the selected properties together with the corresponding test method FNCT and tolerances for a comparison of polyethylene grades of one design type in the procedural rule on suitability proof for alternative plastic resins used for packagings and intermediate bulk Containers (IBCs) for the transport of dangerous goods. The environmental stress crack resistance determined by Full Notch Creep Test (FNCT) represents the impacts from the stacking tests at 40 °C performed with Standard liquid wetting solution (without pre-storage) and with normal butyl acetate saturated wetting solution (pre-storage with normal butyl acetate). Environmental stress crack resistance determined with FNCT for the polyethylene grades was related to the times to failure of different jerrican samples made of these grades in stacking tests with 5 % wetting solution and a n-butyl acetate saturated wetting solution (pre-storage with n-butyl acetate) at 40 °C. The FNCT is suitable for comparison of polyethylene grades in relation to environmental stress crack resistance independent of their use as drum, IBC or jerrican material. The stiffness of polyethylene grades should be taken into account to the comparison as jerricans are not only chemically but also mechanically stressed. T2 - PPS-27 - 27th World congress of the polymer processing society CY - Marrakech, Morocco DA - 10.05.2011 KW - Gefahrgutverpackungen KW - Polyethylenformstoffe KW - Full notch creep test KW - Stapeldruckprüfung PY - 2011 SP - 1 EP - 4 AN - OPUS4-23834 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scharf, Holger T1 - Aspekte der Qualitätssicherung bei der Herstellung und Anwendung von Referenzmaterialien für die Analytik von Sedimenten und Böden T2 - 7. Chemisches Kolloquium "Qualitätssicherung bei der Untersuchung von Sedimenten und Baggergut" CY - Berlin, Deutschland DA - 1996-11-04 KW - Anorganische Umweltanalytik KW - Böden KW - Qualitätssicherung KW - Referenzmaterialien KW - Sedimente PY - 1999 N1 - Serientitel: Veranstaltungen / Bundesanstalt für Gewässerkunde, Koblenz, Berlin – Series title: Veranstaltungen / Bundesanstalt für Gewässerkunde, Koblenz, Berlin IS - 1 SP - 49 EP - 54 PB - BfG CY - Koblenz AN - OPUS4-2359 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scharf, Holger T1 - Entwicklung und Herstellung von Boden-Referenzmaterialien für die anorganische Umweltanalytik T2 - Analytica Conference 2000 CY - München, Deutschland DA - 2000-04-11 KW - Anorganische Umweltanalytik KW - Böden KW - Qualitätssicherung KW - Referenzmaterialien PY - 2000 CY - München AN - OPUS4-2360 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scharf, Holger A1 - Becker, Roland A1 - Buge, Hans-Gerhard T1 - Soil Analysis - The BAM Proficiency Testing Scheme "Contaminated Sites" T2 - International ILAC/IAF Conference on Accreditation in Global Trade CY - Berlin, Germany DA - 2002-09-23 KW - Böden KW - Eignungsprüfung KW - Qualitätssicherung KW - Ringversuche KW - Umweltanalytik PY - 2002 AN - OPUS4-2361 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wieser, Karol E. T1 - Bauartgeprüfte GFK-Tanks zur Lagerung von Heizöl und Dieselkraftstoff T2 - 12. öffentliche Jahrestagung der Arbeitsgemeinschaft Verstärkte Kunststoffe CY - Freudenstadt, Deutschland DA - 1974-10-01 PY - 1974 SP - 19-1-19-6 PB - AVK CY - Frankfurt, Main AN - OPUS4-2312 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Österle, Werner T1 - Textur- und Gefügeentwicklung beim Walzen von polykristallinem alpha-Eisen PY - 1981 SP - 1 EP - 179 CY - Berlin AN - OPUS4-2388 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Österle, Werner ED - Brakman, C. T1 - Influence of temperature and impurity content on the development of texture and microstructure of cold-rolled iron T2 - 7th International Conference on Textures of Materials (ICOTOM) CY - Noordwijkerhout, Netherlands DA - 1984-09-17 PY - 1984 VL - 7 SP - 123 EP - 128 PB - Netherlands Society for Materials CY - Zwijndrecht AN - OPUS4-2393 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wieser, Karol E. A1 - Tobisch, Karl A1 - Probst, Ulrich T1 - The Elastomer Gasket - A Black Sheep for Quality Assurance Measures? T2 - 7th International Symposium on Packaging and Transportation of Radioactive Materials CY - New Orleans, LA, USA DA - 1983-05-15 PY - 1983 VL - 2 IS - 4 SP - 1366 EP - 1369 CY - Springfield, Va. AN - OPUS4-2325 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wieser, Karol E. A1 - Masslowski, Jörg-Peter A1 - Sieber, R. T1 - Investigations on Shock Absorbers for Type B Packagings T2 - 7th International Symposium on Packaging and Transportation of Radioactive Materials CY - New Orleans, LA, USA DA - 1983-05-15 PY - 1983 VL - 2 IS - 4 SP - 1569 EP - 1575 CY - Springfield, Va. AN - OPUS4-2326 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Wieser, Karol E. A1 - Hübner, Heinz W. T1 - Development of European Community Guidelines - Quality Assurance for Type B Packagings and Packages for Fissible Materials used for the Transport of Radioactive Materials - A Cataloque of Essentials (Abschlußbericht des von der EG geförderten Vorhabens XVII-AV-83-665) PY - 1984 SP - 1(?) EP - 25(?) CY - Berlin AN - OPUS4-2327 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wieser, Karol E. A1 - Droste, Bernhard T1 - Die Prüfung und Begutachtung von Behältern aus Sphäroguß T2 - Seminar der Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin, Deutschland DA - 1987-06-09 PY - 1987 VL - 13 SP - 55 EP - 66 PB - Bundesanstalt für Materialforschung und -prüfung CY - Berlin AN - OPUS4-2333 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wieser, Karol E. A1 - Tietze, A. T1 - The Legal Status of UF6-Cylinder Testing and Licensing in Germany (and Europe) T2 - 2nd International Conference CY - Oak Ridge, TN, USA DA - 1991-01-01 PY - 1991 SP - 149 EP - 157 PB - Oak Ridge National Laboratory CY - Oak Ridge AN - OPUS4-2345 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wieser, Karol E. T1 - CEN/BTI/WG83 and RID/ADR ? The coordination of Standards on the Transport of Dangerous Goods T2 - Dangerous Goods Update CY - London, England, UK DA - 1994-06-09 PY - 1994 IS - PIRA Ref. TS/TC/17/0694 PB - Pira International CY - Leatherhead AN - OPUS4-2347 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wieser, Karol E. T1 - Die Rolle der Gefahrgutnormung und der BAM bei der Umsetzung der Rechtsvorschriften T2 - 5. Fachtagung der HOLFELDER PACKAGING Wellpappe Wiesloch CY - St. Leon DA - 1995-10-16 PY - 1995 CY - St. Leon AN - OPUS4-2348 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wieser, Karol E. T1 - Gefahrgutverpackungsvorschriften im Überblick T2 - Tagung "Verpackung gefährlicher Güter" CY - Berlin, Deutschland DA - 1997-11-17 PY - 1997 PB - Verl. Moderne Industrie, ecomed Kongreß-Service CY - Landsberg/Lech AN - OPUS4-2351 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Wieser, Karol E. A1 - Elter, R. T1 - Establishment of a Catalogue of Quality Assurance/Control Measures for Industrial and Type A-packagings (Abschlußbericht des EG-Vorhabens 88B-7020-11-5-17) PY - 1990 CY - Berlin AN - OPUS4-2337 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wieser, Karol E. T1 - Qualitätssicherung und Qualitätsüberwachung beim Transport von radioaktiven Stoffen T2 - Tagungsunterlagen zum HSK-Transportseminar CY - Würenlingen, Schweiz DA - 1990-01-01 PY - 1990 CY - Würenlingen AN - OPUS4-2340 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wieser, Karol E. T1 - Verpackungen radioaktiver Stoffe T2 - Tagungsunterlagen zum HSK-Transportseminar CY - Würenlingen, Schweiz DA - 1990-01-01 PY - 1990 CY - Würenlingen AN - OPUS4-2341 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wieser, Karol E. T1 - Die Beförderung radioaktiver Stoffe der Klasse 7 T2 - Tagungsunterlagen CY - Esslingen, Deutschland DA - 1991-01-01 PY - 1991 IS - 13948-16-083 AN - OPUS4-2343 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wieser, Karol E. T1 - Anforderungen an die Beförderung radioaktiver Stoffe in Containern PY - 1991 PB - Ecomed CY - Landsberg am Lech AN - OPUS4-2344 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Wieser, Karol E. T1 - Forschungs- und Entwicklungsarbeiten auf dem Gebiet des Transportes radioaktiver Stoffe (Abschlußbericht Teil 2, Band 2 des vom BMFT geförderten Vorhabens ATT 3035) PY - 1980 VL - 2 SP - 1 EP - 100 CY - Berlin AN - OPUS4-2318 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wieser, Karol E. A1 - Schulz-Forberg, Bernd A1 - Jais, Manfred T1 - Acceleration and Strain Measurements Performed on Casks for Radioactive Materials under Impact Conditions T2 - 6th International Symposium on Packaging and Transportation of Radioactive Materials CY - Berlin, Germany DA - 1980-11-10 PY - 1981 VL - 2 IS - 4 SP - 1183 EP - 1191 CY - Springfield, Va. AN - OPUS4-2319 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Budäus, A. A1 - Wieser, Karol E. T1 - Abschlußbericht des vom BMFT geförderten Vorhabens KWA 19196 - Prüfung von Transportbehältern für radioaktive Stoffe in Übereinstimmung mit gesetzlichen Anforderungen PY - 1982 SP - 1 EP - 43 CY - Berlin AN - OPUS4-2320 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eberstein, Markus A1 - Banach, Ulrich T1 - Zum Einfluss der Glasstruktur auf die dielektrischen Verluste oxidischer Gläser im Mikrowellenbereich T2 - 77. Glastechnische Tagung CY - Leipzig, Deutschland DA - 2003-05-26 PY - 2003 VL - 77 SP - 8 EP - 11 PB - DGG CY - Offenbach AN - OPUS4-2753 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Friedrich, Jörg Florian A1 - Unger, Wolfgang A1 - Lippitz, Andreas A1 - Koprinarov, Ivaylo A1 - Ghode, Archana A1 - Geng, Sh. A1 - Kühn, Gerhard T1 - Plasma-based introduction of monosort functional groups of different type and density onto polymer surfaces. Part 1: Behaviour of polymers exposed to oxygen plasma N2 - Several approaches were investigated to produce monosort functionalized polymer surfaces with a high density and homogeneity of functional groups: (i) Plasma oxidation followed by wet-chemical reduction, (ii) formation of radicals and grafting on of functional group carrying molecules, (iii) plasma bromination followed by (iv) Williamson or Gabriel-like synthesis of spacer molecules, and (v) a pulsed plasma polymerization of functional groups bearing monomers or (vi) their copolymerisation with other comonomers. The formation of hydroxyl (OH), primary amino (NH2), and carboxyl (COOH) groups was studied in detail. The oxygen plasma treatment (i) in a low-pressure non-isothermal glow discharge results in the formation of a wide variety of O functional groups, polymer degradation and crosslinking. Low power densities and short exposure times (0.1 to 2 s) are required to functionalize a surface while preserving the original polymer structure. Carbonate, ester, and aromatic groups are rapidly degraded by an oxygen plasma treatment leading to scissions of polymer backbones and loss in molecular weight. Also the formation of macrocycles and C=C bonds was observed in a region of around 4 nm in depth. The investigated polymers could be classified by their degradation behaviour on exposure to the oxygen plasma.___TAGSTART___BR___TAGEND___ In order to maximize the process selectivity for OH groups, the variety of oxygen functionalities formed by the oxygen plasma was wet-chemically reduced by diborane, vitridetrade (Na complex), and LiAlH4. Typical yields were 9 to 14 OH groups per 100 carbon atoms.___TAGSTART___BR___TAGEND___ Plasma bromination (iii) (40 Br per 100 C atoms) of polymers, followed by grafting of spacer molecules (iv), has been proved to be a highly selective reaction.___TAGSTART___BR___TAGEND___ Another way to produce high densities of monosort functionalities was the pulsed plasma polymerization of functional group bearing monomers such as allylamine, allylalcohol or acrylic acid (v). The retention of chemical structure and functional groups during plasma polymerization was achieved by using low power densities and the pulsed plasma technique. The maximum yields were 30 OH, 18 NH2, and 24 COOH groups per 100 C atoms. To vary the density of functional groups a chemical copolymerization with ''chain-extending'' comonomers such as butadiene and ethylene was initiated in the pulsed plasma (vi). Additionally, the often-observed post-plasma oxidations of such layers initiated by reaction of trapped radicals with oxygen from the air were successfully suppressed by using NO gas as radical quencher. PY - 2003 DO - https://doi.org/10.1163/156855403765826865 VL - 10 IS - 2-3 SP - 139 EP - 171 PB - North-Holland CY - New York, NY AN - OPUS4-2705 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Friedrich, Jörg Florian A1 - Mix, Renate A1 - Kühn, Gerhard A1 - Retzko, Iris A1 - Schönhals, Andreas A1 - Unger, Wolfgang T1 - Plasma-based introduction of monosort functional groups of different type and density onto polymer surfaces. Part 2: Pulsed plasma polymerization N2 - This new functionalization method consists of the deposition of very thin plasma polymer layers (20 to 100 nm) of functional group bearing monomers in pulsed plasma. With allylalcohol, a maximum of 30 OH groups per 100 C atoms was measured with a selectivity of about 90% and a significant stability at long-time exposure to air. Allylamine was used to produce primary amino groups, with a maximum of 18 NH2 groups per 100 C atoms. Side reactions were observed during the storage in air, such as oxidation of the amino groups. Carboxylic groups could be produced using acrylic acid with a maximum concentration of 24 COOH groups per 100 C atoms. The most prominent side reaction was the decarbonylation/ decarboxylation of the acid group during plasma deposition.___TAGSTART___BR___TAGEND___ The variation of the density of functional groups using the pulsed-plasma polymerization of functional-group-bearing monomers was possible by the chemically-initiated radical copolymerization with either a chain-extending monomer, such as ethylene, or a cross linker, such as butadiene, in plasma. The density of functional groups could be adjusted continuously (0 to 30 OH, 0 to 18 NH2 and 0 to 24 COOH groups per 100 C atoms).___TAGSTART___BR___TAGEND___ The successful application of these densely functionalized polymer surfaces for producing biocompatible surfaces and for use in metal–polymer composites is proposed. KW - Pulsed plasma polymerization KW - Plasma-initiated copolymerization KW - Charcterization of homo- and copolymers PY - 2003 DO - https://doi.org/10.1163/156855403765826874 VL - 10 IS - 2-3 SP - 173 EP - 223 PB - North-Holland CY - New York, NY AN - OPUS4-2706 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulze, Rolf-Dieter A1 - Mix, Renate A1 - Kühn, Gerhard A1 - Friedrich, Jörg Florian ED - d'Agostino, R. T1 - Pulsed plasma initiated homo and copolymerisation - deposition rates and plasma diagnostics in dependence on the pulse length and frequency T2 - 16th International Symposium on Plasma Chemistry (ISPC-16) CY - Taormina, Italy DA - 2003-06-22 PY - 2003 IS - CD-ROM PB - Dep. of Chemistry, Univ. CY - Bari AN - OPUS4-2708 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Friedrich, Jörg Florian A1 - Meyer-Plath, Asmus A1 - Retzko, Iris A1 - Kühn, Gerhard A1 - Mix, Renate ED - d'Agostino, R. T1 - Comparison of different plasmachemical processes for the formation of monotype functionalized polymer surfaces T2 - 16th International Symposium on Plasma Chemistry (ISPC-16) CY - Taormina, Italy DA - 2003-06-22 PY - 2003 IS - CD-ROM PB - Dep. of Chemistry, Univ. CY - Bari AN - OPUS4-2709 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Friedrich, Jörg Florian A1 - Schönhals, Andreas A1 - Fritz, Andreas A1 - Mix, Renate A1 - Kühn, Gerhard ED - d'Agostino, R. T1 - Pulsed plasma initiated homo and copolymerisation - characterization of thin plasma polymer layers by dielectric relaxation spectroscopy T2 - 16th International Symposium on Plasma Chemistry (ISPC-16) CY - Taormina, Italy DA - 2003-06-22 PY - 2003 IS - CD-ROM PB - Dep. of Chemistry, Univ. CY - Bari AN - OPUS4-2711 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Friedrich, Jörg Florian A1 - Kühn, Gerhard A1 - Mix, Renate ED - d'Agostino, R. T1 - Polymer surface modification with monofunctional groups of different type and density T2 - 16th International Symposium on Plasma Chemistry (ISPC-16) CY - Taormina, Italy DA - 2003-06-22 PY - 2003 IS - CD-ROM PB - Dep. of Chemistry, Univ. CY - Bari AN - OPUS4-2712 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Steckert, Carsten A1 - Günzel, K.-P. T1 - Digital colour image analysis for quality evaluation of car washing stations and affiliated cleaning agents T2 - International Conference on Materials Testing ; TEST Kongress ; TEST Conference CY - Nuremberg, Germany DA - 2003-05-13 PY - 2003 IS - A 6.5 SP - 141 EP - 146 PB - AMA Service GmbH CY - Wunstorf AN - OPUS4-2717 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jankowski, Lukasz T1 - Calibration procedure for low-end CCD cameras T2 - International Conference on Materials Testing ; TEST Kongress ; TEST Conference CY - Nuremberg, Germany DA - 2003-05-13 PY - 2003 IS - P 12 SP - 255 EP - 260 PB - AMA Service GmbH CY - Wunstorf AN - OPUS4-2720 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Daum, Werner A1 - Czepluch, Wolf T1 - Reliability of Step-Index and Multi-Core POF for Automotive Applications T2 - POF 2003 ; 12th International Conference on Polymer Optical Fiber CY - Seattle, WA, USA DA - 2003-09-14 PY - 2003 SP - 6 EP - 9 CY - Seattle, Wash. AN - OPUS4-2724 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mitropetros, Constantinos A1 - Steinbach, J. A1 - Plewinsky, B. A1 - Hieronymus, Hartmut T1 - Safety behaviour of a chemically active organic bubbly medium induced by gas explosion above it T2 - European Combustion Meeting 2003 ; ECM 2003 CY - Orléans, France DA - 2003-10-25 PY - 2003 SP - 1 EP - 6 CY - Orléans AN - OPUS4-2725 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Appajaiah, Anilkumar A1 - Wachtendorf, Volker A1 - Jankowski, Lukasz T1 - Chemiluminescence investigation of high temperature and humidity aging of PMMA based polymer optical fibres (POF) T2 - POF 2003 ; 12th International Conference on Polymer Optical Fiber CY - Seattle, WA, USA DA - 2003-09-14 PY - 2003 SP - 152 EP - 155 CY - Seattle, Wash. AN - OPUS4-2665 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jankowski, Lukasz A1 - Bunge, Ch.-A. A1 - Zubia, J. A1 - Appajaiah, Anilkumar T1 - Modelling of light propagation through aged and non-aged POFs T2 - POF 2003 ; 12th International Conference on Polymer Optical Fiber CY - Seattle, WA, USA DA - 2003-09-14 PY - 2003 SP - 148 EP - 151 CY - Seattle, Wash. AN - OPUS4-2666 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reinsch, Stefan A1 - Dreßler, Martin A1 - Nofz, Marianne A1 - Pauli, Jutta A1 - Jäger, Christian A1 - Scholz, G. ED - Krämer, V. T1 - Phasentransformationen von anorganisch modifizierten Alumo-Xerogelen T2 - Jahrestagung der Gesellschaft für Thermische Analyse e.V. CY - Augsburg, Deutschland DA - 2003-09-15 PY - 2003 SP - 1 EP - 2 AN - OPUS4-2668 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Wolfgang A1 - Gradt, Thomas A1 - Ostrovskaya, Y. T1 - Tribologische Eigenschaften von Festschmierstoffen in tiefkalten Medien T2 - BAM-Sonderheft 2003 "Polymere Verbundwerkstoffe zwischen Raumtemperatur und 4,2 K" ; 2. Symposium im DFG-Projekt: Eigenschaften von PTFE- und PEEK-Matrix-Werkstoffen bei tribologischer Beanspruchung CY - Berlin, Deutschland DA - 2003-02-27 PY - 2003 SP - 28 EP - 32 AN - OPUS4-2671 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bohse, Jürgen T1 - Schallemission von verstärkten Polymeren T2 - BAM-Sonderheft 2003 "Polymere Verbundwerkstoffe zwischen Raumtemperatur und 4,2 K" ; 2. Symposium im DFG-Projekt: Eigenschaften von PTFE- und PEEK-Matrix-Werkstoffen bei tribologischer Beanspruchung CY - Berlin, Deutschland DA - 2003-02-27 PY - 2003 SP - 46 EP - 57 AN - OPUS4-2672 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Malz, Frank A1 - Jancke, Harald A1 - Radeglia, Reiner T1 - Gehaltsbestimmung von Ethanol in wässriger Matrix (forensische Chemie) mittels quantitativer 1H-Wasserunterdrückungs-NMR T2 - GDCh-NMR-Diskussionstagung "Praktische Probleme der Kernresonanzspektroskopie" CY - Erlangen, Deutschland DA - 2004-01-12 KW - Quantitative NMR KW - Wasserunterdrückung KW - Gehaltsbestimmung KW - Ethanol PY - 2004 SP - 10 PB - GDCh CY - Erlangen AN - OPUS4-3061 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bomas, H. A1 - Hünecke, Joachim A1 - Laue, S. A1 - Schöne, Dieter T1 - Anrisslebensdauervorhersage am Beispiel glatter und gekerbter Proben des Werkstoffes Cm15 T2 - Abschlusskolloquium "Mechanismenorientierte Lebensdauervorhersage für zyklisch beanspruchte metallische Werkstoffe" CY - Bremen, Deutschland DA - 2004-02-11 KW - Kurze Risse KW - Simulation KW - Kerben KW - Korngröße KW - Ermüdung PY - 2004 N1 - Serientitel: DVM-Bericht – Series title: DVM-Bericht IS - 685 SP - 53 EP - 68 PB - Deutscher Verband für Materialforschung und -prüfung CY - Berlin AN - OPUS4-3067 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stark, Wolfgang A1 - Döring, Joachim A1 - Goering, Harald A1 - Knappe, S. A1 - Mc Hugh, Jarlath A1 - Opfermann, J. T1 - Der RTM-Prozess und die Probleme von Gelierung, Verglasung und Aushärtegrad T2 - 6. Internationale AVK-TV Tagung für Verstärkte Kunststoffe und Duroplastische Formmassen ; 6th International AVK-TV Conference for Reinforced Plastics and Thermoset Moulding Compounds CY - Baden-Baden, Deutschland DA - 2003-10-07 KW - Epxidharz KW - Compositbauteil KW - Vernetzungsreaktion PY - 2003 VL - 6 SP - C14-1-C14-16 PB - AVK-TV CY - Frankfurt am Main AN - OPUS4-3034 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilrich, Cordula A1 - Aris, Stephan T1 - Safety of Acetylene Cylinders T2 - 14th EIGA Symposium "Packaged Gases: Past, Present and Future" CY - Strasbourg, France DA - 2004-01-21 KW - Acetylenflaschen KW - Acetylene cylinders PY - 2004 SP - 3.5/1 EP - 3.5/10 PB - European Industrial Gases Association (EIGA) CY - Brüssel AN - OPUS4-3163 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Molnarne, Maria T1 - Curve Fitting Problems at the Evaluation of Explosion Diagrams T2 - 9th International Workshop on Chemical Engineering Mathematics CY - Bad Honnef, Germany DA - 2003-07-14 PY - 2003 UR - http://knight.kit.bme.hu/Bea/alma_Fried/BH2003_proc.doc VL - 9 SP - 7 AN - OPUS4-3169 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Blümel, Peter T1 - New standards for compatibility testing of filling substances and the revised Assimilation list T2 - Plastics packaging - compatability testing for dangerous goods - new developments CY - Brussels, Belgium DA - 2003-09-30 PY - 2003 IS - 2 SP - 1(?) EP - 32(?) AN - OPUS4-3125 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Altantsog, Pagvajav A1 - Ojunbileg, L. A1 - Palam, B. A1 - Tserenshimed, M. A1 - Chadraabal, Shgdariin A1 - Müller, Ralf A1 - Nofz, Marianne A1 - Gaber, Martin T1 - Some experimental results of glass melting by using sands from Buir nuur N2 - We have carried out some laboratory experiments to establish possibilities to melt 16Na2O*10CaO*74SiO2 glasses from consisting of mainly quarz sands of Buir nuur lake. When the sands used directly, the formed glasses had slight blue colour, the origin of which may be connected with aluminium and iron impurities in the sands. Presence of these impurities is confirmed by chemical analyse and ESR study data. Allso have been studied liquid gas extraction phenomena in the sands and melted glass samples and determined some physical properties of them. PY - 2002 VL - 17 SP - 107 EP - 115 AN - OPUS4-3118 LA - mon AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gottschling, Peter A1 - Gaber, Martin A1 - Müller, Ralf T1 - Numerische Simulation von Gasabgabeprozessen aus Glaspulvern T2 - 77. Glastechnische Tagung CY - Leipzig, Deutschland DA - 2003-05-26 PY - 2003 VL - 77 SP - 140 EP - 143 PB - DGG CY - Offenbach AN - OPUS4-3122 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Blümel, Peter T1 - Compatibility testing of co-extruded polyethylene for pesticide containers T2 - Plastics packaging - compatability testing for dangerous goods - new developments CY - Brussels, Belgium DA - 2003-09-30 KW - Verträglichkeitsnachweis KW - Koextrudiertes PE PY - 2003 IS - 9 SP - 1(?) EP - 22(?) AN - OPUS4-3123 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niederleithinger, Ernst A1 - Gardei, André A1 - Behrens, Matthias T1 - Non Destructive Testing of Concrete Railway Tracks by Impulse Response and Impact Echo Techniques T2 - International Conference on Materials Testing ; TEST Kongress ; TEST Conference CY - Nuremberg, Germany DA - 2003-05-13 KW - Impakt-Echo KW - Impulse-Response KW - Beton KW - Feste Fahrbahn KW - Qualitätskontrolle KW - Schwellen KW - Verbund KW - Zerstörungsfreie Prüfung PY - 2003 IS - A 7.2 SP - 153 EP - 156 PB - AMA Service GmbH CY - Wunstorf AN - OPUS4-3229 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hentschel, Manfred P. A1 - Lange, Axel A1 - Harbich, Karl-Wolfram T1 - X-Ray Diffraction Scanning Microscopy - A new method of nondestructive Characterization of inhomogeneous materials T2 - ESA Symposium on Space Applications of Advanced Structural Materials (ESTEC) CY - Noordwijk, Netherlands DA - 1990-03-21 PY - 1990 IS - MBB-Z--0301-90-PUB SP - 447 EP - 450 PB - Zentrale Berichtsstelle, Technisch-wissenschaftliche Information, Messerschmitt-Bölkow-Blohm GmbH CY - München AN - OPUS4-3269 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Harbich, Karl-Wolfram A1 - Hentschel, Manfred P. T1 - Röntgen-Refraktionsanalyse als neues ZfP-Verfahren zur Bestimmung innerer Oberflächen in monolithischer Keramik T2 - DGZfP-Jahrestagung 1992 Zerstörungsfreie Materialprüfung CY - Fulda, Deutschland DA - 1992-04-27 PY - 1992 N1 - Serientitel: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. – Series title: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. IS - 33-1 SP - 786 EP - 792 PB - DGZfP CY - Berlin AN - OPUS4-3270 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilke, Olaf T1 - VOC-Emissionen aus Verlegewerkstoffen, Bodenbelägen und Fußbodenaufbauten T2 - 18. TKB-Fachtagung CY - Frankfurt am Main, Deutschland DA - 2002-03-06 PY - 2002 PB - SN-Verl. CY - Hamburg AN - OPUS4-3274 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Torge, Manfred A1 - Müller, Wolfgang A1 - Adam, Karin A1 - Kruschke, Detlef A1 - Köcher, Christa T1 - Dürfen Glasmalereien des 19. Jahrhunderts bei der Restaurierung einem Neubrand unterzogen werden? T2 - 4. Internationales Forum zur Restaurierung und Technologie historischer Glasmalereien CY - Troyes, Frankreich DA - 2001-05-17 KW - Kulturguterhaltung PY - 2001 VL - 48 SP - 49 EP - 52 CY - Romont AN - OPUS4-3244 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Werner ED - Knipschild, F. T1 - Eignungsnachweis für Kunststoff-Dränelemente in Oberflächenabdichtungen T2 - 20. Fachtagung "Die sichere Deponie" CY - Würzburg, Deutschland DA - 2004-02-26 KW - Kunststoff-Dränelemente KW - Eignungsnachweis KW - Langzeitverhalten KW - Oberflächenabdichtungen PY - 2004 SP - G1 EP - G12 PB - SKZ CY - Würzburg AN - OPUS4-3221 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Torge, Manfred A1 - Müller, Wolfgang A1 - Adam, Karin T1 - Naturwissenschaftliche Untersuchungen an historischen Glasmalereien N2 - Im diesem Artikel soll ein Überblick zur Zusammensetzung von historischen Gläsern, den sich daraus ergebenden Problemen bei der Restaurierung von mittelalterlichen Kirchenfenstern und naturwissenschaftlichen Untersuchungen an den Glasoberflächen zur Auswahl von Reinigungsmethoden gegeben werden. KW - Kulturguterhaltung KW - Airbrasive KW - Rasterelektronenmikroskopie PY - 2001 UR - http://www.struers.com/resources/elements/12/2443/38art6_de.pdf IS - 38 SP - 25 EP - 29 PB - Struers CY - Willich AN - OPUS4-3246 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Göllner, J. A1 - Heyn, Andreas A1 - Burkert, Andreas T1 - Qualitätssicherung und Früherkennung der Korrosionsneigung bei mechanisch gefügten Blechen N2 - Auf dem Gebiet des mechanischen Fügens ist eine rege Entwicklung zu verzeichnen. Der Einsatz neuer Materialien, neuer Nietformen, neuer Schutzschichten, veränderter Fertigungstechnologien, die Notwendigkeit zur Mischbauweise, veränderte mediale Belastungen, geforderte Langzeitgarantien usw. lassen vielfältige alte und neue Fragen hinsichtlich der Korrosionsbeständigkeit auftreten. Herkömmliche Korrosionsprüfverfahren geben oft nur unzureichende Antworten auf diese Fragen. Mit einer neuen Methode (Rauschdiagnostik) ist es möglich, in kurzer Zeit aussagekräftige Ergebnisse über Material- und Bauteileigenschaften zu erhalten. Hierbei macht man sich die Tatsache zu Nutze, dass eine Oberfläche, gleichgültig ob man misst oder nicht misst, ständig kleinste Strom- und Spannungsimpulse generiert, die bei richtiger Messung und Interpretation wertvolle Aussagen liefern. Neben der Möglichkeit, die Korrosionsneigung zu bestimmen, lassen sich über diese Messungen auch bestimmte Verarbeitungsfehler und Oberflächendefekte nachweisen. Die Anwendung dieser Methode bietet somit Möglichkeiten zur Prozessoptimierung und Qualitätssicherung mechanisch gefügter Bauteile, oder auch zur Einschätzung des Zustandes von Fügeverbindungen in der Praxis. KW - Stanznieten KW - Korrosion KW - Elektrochemische Messungen PY - 2003 IS - 3 SP - 1 EP - 7 PB - Meisenbach CY - Bamberg AN - OPUS4-3370 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fengler, Petra A1 - Stark, Wolfgang A1 - Döring, Joachim A1 - Mc Hugh, Jarlath T1 - Coupling of hidden ultrasound sensors to a moulding tool N2 - Ultrasound on-line NDT methods have been demonstrated as a useful tool for monitoring the curing reaction of thermosets. In order to achieve this ultrasound sensors are incorporated into compression, injection and RTM (resin transfer) mould. For many commercial products imprints or any surface markings upon the moulded product are undesirable. Due to its physical properties ultrasound has a large advantage over other techniques for similar applications. The sound wave can pass through the wall of the mould and direct contact with the moulded part is not required. In this particular case one fundamental problem is a good coupling of the sensors to the mould wall. Several mediums came into question but because of the high technical (e. g. temperature and long time stability) and practical demands, it was decided that dry (non-fluid) coupling would be the most promising candidate. A handful of coupling foils suitable also at high temperatures and for long time application under industrial conditions were tested and are presented in this paper. KW - Sensors KW - Ultrasound KW - Mould wall coupling KW - Thermoset manufacturing PY - 2004 UR - http://www.ndt.net/article/v09n03/stark/stark.htm SN - 1435-4934 VL - 9 IS - 3 SP - 1 EP - 10 PB - NDT.net CY - Kirchwald AN - OPUS4-3316 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Wolfgang A1 - Gradt, Thomas A1 - Aßmus, Kristin A1 - Pyzalla, A. A1 - Pinto, H. A1 - Stuke, S. T1 - Hydrogen absorption by steels during friction T2 - Hydrogen and Fuel Cells Conference and Trade Show ; Hydrogène et Piles à Combustible Conférence et Foire Commerciale CY - Vancouver, Canada DA - 2003-06-08 PY - 2003 SP - 1 EP - 11(?) PB - CHA CY - Toronto AN - OPUS4-3319 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bremser, Wolfram A1 - Zschunke, Adolf T1 - Zuverlässige chemische Analytik bringt Sicherheit PY - 2002 SP - 25 EP - 26 PB - IGAFA CY - Berlin AN - OPUS4-3324 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weh, Lothar A1 - Gemeinert, Marion ED - Pratsinis, S. E. T1 - Dispersibility optimization of ceramic particles for ML-LTCC production T2 - PARTEC 2004 ; International Congress for Particle Technology CY - Nuremberg, Germany DA - 2004-03-16 PY - 2004 SP - 1 EP - 4(?) PB - Nürnberg Messe GmbH CY - Nürnberg AN - OPUS4-3404 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Arndt, Ralf A1 - Maierhofer, Christiane A1 - Röllig, Mathias A1 - Weritz, Friederike A1 - Wiggenhauser, Herbert T1 - Structural investigation of concrete and masonry structures behind plaster by means of pulse phase thermography T2 - 7th International Conference on Quantitative Infrared Thermography (QIRT 2004) CY - Rhode-St-Genese, Belgien DA - 2004-06-05 KW - Pulse phase thermography KW - Nondestructive testing in civil engineering KW - Plaster KW - Concrete KW - Masonry KW - Delaminations KW - Voids PY - 2004 SP - I.3.1 EP - I.3.6 PB - Karman Institute for Fluid Dynamics CY - Rhode-St-Genese AN - OPUS4-4397 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Taffe, Alexander A1 - Schaurich, Dieter A1 - Weritz, Friederike A1 - Wiggenhauser, Herbert A1 - Wilsch, Gerd T1 - Ermittlung des Chloridgehaltes von Betonproben mit Laser-Induzierter Breakdown Spektroskopie (LIBS) T2 - 1. Kolloquium "Verkehrsbauten - Schwerpunkt Parkhäuser" CY - Esslingen, Deutschland DA - 2004-01-27 PY - 2004 SP - 651 EP - 657 PB - Techn. Akad. Esslingen CY - Esslingen AN - OPUS4-4402 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grätz, Rainer T1 - Explosionsschutz - Normen und gesetzliche Grundlagen, Nichtelektrischer Explosionsschutz T2 - Seminar "Sicherheit beim Umgang mit Wasserstoff" CY - Hamburg, Deutschland DA - 2003-06-30 PY - 2003 SP - 2 EP - 4 AN - OPUS4-4393 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Habel, Wolfgang T1 - Faseroptische Messverfahren für die Überwachung von Bauwerken - überblickt der potenzielle Anwender die Vielfalt der Angebote? T2 - 61. DVW-Fortbildungsseminar "Interdisziplinäre Messaufgaben im Bauwesen - Weimar 2004" CY - Weimar, Deutschland DA - 2004-09-27 PY - 2004 VL - 46 SP - 57 EP - 73 PB - DVW CY - Weimar AN - OPUS4-4384 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bücker, Michael A1 - Böcker, Wolfgang D. G. A1 - Reinsch, Stefan A1 - Unger, Brita T1 - Holzmodifikation durch Tränkung mit Nanopartikeln T2 - Tagung "Rosenheimer Fenstertage 2004" CY - Rosenheim, Deutschland DA - 2004-01-01 KW - Holzmodifikation KW - Sol-Gel KW - Tränkverfahren KW - Holzschutz PY - 2004 SP - 23 EP - 26 PB - Institut für Fenstertechnik CY - Rosenheim AN - OPUS4-4487 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maultzsch, Matthias T1 - Dünnschichtige Spritzmörtel - Materialien für geringer feste Untergründe N2 - Ein nicht unerheblicher Teil der instand zu setzenden Wasserbauwerke muss den neu definierten Altbetonklassen A2 oder A3 mit Betondruckfestigkeiten zwischen 10 und 30 N/mm² zugeordnet werden. Über Produktentwicklungen, Anforderungen und Nachweis der Eigenschaften geeigneter Spritzmörtel wird berichtet. T2 - BAW-Kolloquium "Instandsetzung von Wasserbauwerken" CY - Hannover, Deutschland DA - 2004-10-20 KW - Building research KW - Research institutes KW - Networks PY - 2004 SP - 41 EP - 45 AN - OPUS4-4571 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Artemiev, Valentin M. A1 - Naumov, Alexandre A1 - Tillack, G.-R. T1 - Dynamic image reconstruction for process tomography KW - Prozesstomographie KW - Rekonstruktionsalgorithmen KW - Dynamische Prozesse KW - Kalman-Filter PY - 2004 VL - 2003 SP - 27 EP - 45 PB - Belaruskaya Navuka Publishing House CY - Minsk AN - OPUS4-4590 LA - rus AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Vengrinovich, Valery A1 - Zolotarev, Serguei A1 - Ewert, Uwe A1 - Redmer, Bernhard A1 - Tillack, G.-R. T1 - Tomographic visualization, inspection and control of thick pipe walls by restricted X-ray data KW - Computertomographie KW - Rekonstruktionsalgorithmen KW - Wanddickenbestimmung KW - Schweißnahtscanner PY - 2004 VL - 2003 SP - 269 EP - 279 PB - Belaruskaya Navuka Publishing House CY - Minsk AN - OPUS4-4591 LA - rus AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz ED - Thompson, D. ED - Jones, C. T1 - Ground vibration due to railway traffic - the calculation of the effects of moving static loads and their experimental verification T2 - 8th International Workshop on Railway Noise CY - Buxton, England, UK DA - 2004-09-08 PY - 2004 VL - 1 SP - 119 EP - 129 CY - Buxton AN - OPUS4-4632 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maultzsch, Matthias A1 - Möller Sörensen, L. T1 - Joint research - A need for construction innovation T2 - Building for a European Future (B4E) CY - Maastricht, The Netherlands DA - 2004-10-14 KW - Building research KW - Research institutes KW - Networks PY - 2004 VL - 2 SP - 101 EP - 114 AN - OPUS4-4558 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Redmer, Bernhard A1 - Ewert, Uwe A1 - Rädel, Christoph A1 - Zscherpel, Uwe A1 - Likhatchov, A.V. A1 - Pickalov, V.V. A1 - Neundorf, B. T1 - Mobile 3D-X-Ray Tomography for Analysis of Planar Defects in Welds by "Tomocar" N2 - Tomographical Computer Aided Radiology (TomoCAR) is based on the mechanical position control of an X-ray tube in front of a welding seam and the application of a planar array detector behind it. Several hundred radiometric projections in small angle steps are acquired. The tomographical reconstruction allows the three-dimensional (3D) representation of the defects. A new radiometric array detector system with a small internal unsharpness and high image contrast is used for the 2- and 3-dimensional visualization and sizing of planar defects with a defect opening of less than 100 µm. This detector is based on a CMOS-flat panel with a direct converting CdTe-single crystal layer. The small design allows the application of the mobile testing equipment for mechanized X-ray inspection in industrial plants. The physical pixel size of the detector amounts to 0,1x0,1 mm². Nevertheless, this system yields a better spatial resolution than indirect converting detectors (e.g. cameras with fluorescence layers of Gd2O2S). It allows the reliable detection of planar defects with openings far below the detector pixel size by subpixel resolution. 'TomoCAR' is qualified at present in the context with a German pilot study following to the ENIQ guidelines for the employment within the nuclear power industry. T2 - 16th World Conference on Nondestructive Testing CY - Montreal, Canada DA - 2004-08-30 KW - Digitale Radiologie KW - Radiometrie KW - Laminografie KW - Mobile Anwendungen PY - 2004 SP - 8 pages PB - International Committee for Non-Destructive Testing CY - Montreal AN - OPUS4-4717 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Gert A1 - Göklü, Sinasi A1 - Tischlinger, Wolfgang A1 - Momeni, Kaveh A1 - Xu, Ping T1 - Widerstandspunktschweißen hoch fester Mehrphasenstähle für den Karosserie-Leichtbau: Schweißbereiche - Prozesssicherheit - Aufhärtung - Festigkeit T2 - Sondertagung Widerstandsschweißen "Treffpunkt Widerstandsschweißen" CY - Duisburg, Deutschland DA - 2004-05-26 KW - Widerstandspunktschweißen KW - Mehrphasenstähle KW - Leichtbau PY - 2004 SP - 113 EP - 137 PB - DVS-Verl. CY - Duisburg AN - OPUS4-4720 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Gert A1 - Göklü, S. T1 - Schweißeignung und Prozesssicherheit beim Widerstandspunktschweißen hoch fester Mehrphasenstähle im Rohkarosserie-Leichtbau T2 - EUROJOIN 5 ; 5th European Conference on Welding, Joining and Cutting CY - Wien, Österreich DA - 2004-05-13 KW - Hoch feste Mehrphasenstähle KW - Widerstandspunktschweißen PY - 2004 VL - 5 SP - V9-1-V9-30 CY - Wien AN - OPUS4-4721 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Gert A1 - Göklü, S. T1 - Resistance Spot Welding of High-Strength Multi-Phase Steels T2 - 3rd International Seminar on Advances in Resistance Welding CY - Berlin, Germany DA - 2004-11-17 KW - Resistance spot welding KW - Multi-phase steels KW - Advanced high-strength steels KW - AHSS PY - 2004 SP - 18 EP - 35 PB - SWANTEC Software and Engineering CY - Hoersholm, Denmark AN - OPUS4-4722 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rücker, Werner A1 - Rohrmann, Rolf A1 - Said, Samir T1 - IMO-WIND: Ein integrales Monitoring-System für Offshore-Windenergieanlagen T2 - Workshop "Windkraftanlagen - Sicherheit und Zuverlässigkeit" CY - Darmstadt, Deutschland DA - 2004-11-04 KW - Wind Energy KW - Offshore Structures KW - Damage Detection KW - Health Monitoring KW - Modal analysis KW - Design Improvement KW - Embedded Sensors KW - Offshore KW - Windenergieanlagen KW - Dynamische Untersuchungen KW - Dauerüberwachung KW - Schadensfrüherkennung KW - Sensorik PY - 2004 SP - 13 Seiten PB - VDI-Verl. CY - Düsseldorf AN - OPUS4-4713 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Unger, Wolfgang ED - Blasek, G. T1 - Plasmapolymerschichten: Zu den Möglichkeiten einer chemischen Charakterisierung mit den Methoden ESCA, ToF-SIMS und Röntgen-absorptions-Spektroskopie (XAS) T2 - 12. Neues Dresdener Vakuumtechnisches Kolloquium (NDVaK) CY - Dresden, Deutschland DA - 2004-10-14 KW - ESCA KW - ToF-SIMS KW - XAS KW - Plasma-Polymerisation PY - 2004 SP - 133 EP - 140 PB - Dresdner Transferstelle für Vakuumtechnik CY - Dresden AN - OPUS4-4699 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Retzko, Iris A1 - Unger, Wolfgang A1 - Gesatzke, Wolfgang A1 - Scholl, A. A1 - Kilcoyne, A. D. A1 - Koprinarov, I. A1 - Ade, H. A1 - Hitchcock, A. P. A1 - Schulz, H. A1 - Scheibe, H.-J. ED - Tamura, L. S. T1 - Spectromicroscopy with inhomogeneous ta - C samples PY - 2003 UR - http://repositories.cdlib.org/lbnl/LBNL-52519/ SP - 1 EP - 3(?) AN - OPUS4-4694 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Friedrich, Jörg Florian A1 - Mix, Renate A1 - Kühn, Gerhard T1 - Contribution of chemical interactions to the adhesion between aluminium and functional groups of different (mono-) type and density at polymer surfaces T2 - 7th European Adhesion Conference (EURADH 2004) CY - Freiburg im Breisgau, Germany DA - 2004-09-07 PY - 2004 VL - 1 SP - 138 EP - 143 PB - DECHEMA CY - Frankfurt am Main AN - OPUS4-4680 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ludwig, Jörg T1 - Perspektiven beim Tankbau - größer, dünner, sicherer? T2 - 7. Gefahrgut-Technik-Tage (GTT) CY - Berlin, Deutschland DA - 2004-11-25 KW - Beförderung gefährlicher Güter KW - Gefahrguttanks KW - Risikoeinflussbereiche KW - Unfall-/Notfallmanagement PY - 2004 VL - 7 SP - 1(?) EP - 7(?) PB - Storck CY - Hamburg AN - OPUS4-5485 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schoknecht, Ute A1 - Wegner, R. A1 - Melcher, E. T1 - Experiences with the OECD guideline proposals for the estimation of emissions from preservative treated wood in the environment T2 - 35th Annual Meeting of the International Research Group on Wood Preservation CY - Ljubljana, Slovenia DA - 2004-06-06 PY - 2004 SP - 13 pages PB - International Research Group on Wood Preservation CY - Stockholm AN - OPUS4-5490 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schoknecht, Ute T1 - Characterization and differentiation of wood rotting fungi by protein and enzyme patterns N2 - Standardized tests for wood preservatives are performed with defined fungal strains to ensure comparability between laboratories. However, changes of virulence and variation of results are well known events. Suitable and reliable measures to control the stability of the test organisms are necessary.Comparison of protein patterns produced by SDS-electrophoresis was already described by several authors as a possible way to identify and to characterize fungal species and strains, i.e. for Serpula, Coniophora and Poria. We compared protein patterns of several strains of Antrodia vaillantii, Poria placenta, Gloeophyllum trabeum, Lentinus lepideus, and Coniophora puteana. Isoelectric focussing and detection of esterase isoenzymes proved to be an alternative method. The investigations resulted in species-specific protein and enzyme patterns. By comparing the strains of single species it was possible to form groups with similar patterns. Possible misidentifications could be detected. The described methods will be further developed and used to follow possible changes in our test strains. T2 - 30th Annual meeting of the International Research Group on Wood Preservation (IRG) CY - Rosenheim, Germany DA - 1999-06-06 KW - Basidiomycetes KW - Strains KW - Standardization KW - SDS Polyacrylamide Gel Electrophoresis KW - Isoelectric focussing KW - Proteins KW - Enzymes PY - 1999 IS - IRG-WP 99-20177, Section 2 SP - 1 EP - 9(?) PB - IRG Secretariat CY - Stockholm AN - OPUS4-5491 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Habel, Wolfgang A1 - Krebber, Katerina A1 - Gutmann, Toivo A1 - Schram, C. A1 - Meyer, D. T1 - Fibre Bragg Grating Sensors to Monitor the Rotor Blades of Wind Turbines - Criteria and Method to put them to the Best Possible Use T2 - 7th German Wind Energy Conference (DEWEK 2004) "Where Industry meets Science" CY - Wilhelmshaven, Germany DA - 2004-10-20 KW - Windkraftanlagen PY - 2004 PB - Deutsches Windenergie-Institut CY - Wilhelmshaven AN - OPUS4-5784 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Karl, Winfried T1 - Neue Gefahrgutbeförderungsvorschriften in Europa - Die Revision der Klasse 2 PY - 1996 IS - 55-95-D SP - 11-1-11-15 AN - OPUS4-5889 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Friedrich, Jörg Florian A1 - Mix, Renate A1 - Kühn, Gerhard A1 - Unger, Wolfgang T1 - Functional groups bearing plasma homo and copolymer layers as adhesion promoters in metal-polymer composites T2 - 10. Neues Dresdner Vakuumtechnisches Kolloquium (NDVaK) CY - Dresden, Germany DA - 2002-10-17 PY - 2002 SP - 6 EP - 15 PB - DTVa CY - Dresden AN - OPUS4-6970 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Retzko, Iris A1 - Friedrich, Jörg Florian A1 - Kühn, Gerhard A1 - Lippitz, Andreas A1 - Unger, Wolfgang T1 - Eine neue Generation von alterungsbeständigen Plasmapolymeren mit definierter chemischer Struktur T2 - 8. Neues Dresdner Vakuumtechnisches Kolloquium (NDVaK) CY - Dresden, Deutschland DA - 2000-10-19 PY - 2000 VL - 8 SP - 110 EP - 114 CY - Dresden AN - OPUS4-6974 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Maultzsch, Matthias T1 - Zur Bildung der ferritischen Klinkerphase aus der Schmelze PY - 1972 SP - 1 EP - 73 CY - Berlin AN - OPUS4-6911 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Unger, Wolfgang A1 - Lippitz, Andreas A1 - Koprinarov, Ivaylo A1 - Friedrich, Jörg Florian A1 - Wöll, Ch. T1 - K-Edge Soft X-ray Absorption (NEXAFS) Spectroscopy In Surface Chemical Analysis of Polymers T2 - International Discussion Meeting Advanced Methods of Polymer Characterization: New Developments and Applications in Industry CY - Mainz, Germany DA - 1999-03-15 PY - 1999 SP - P3.53 CY - Mainz AN - OPUS4-6925 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Matsubayashi, N. A1 - Imamura, M. A1 - Tanaka, T. A1 - Shimada, H. A1 - Retzko, Iris A1 - Unger, Wolfgang T1 - Surface Analysis by XPS and XAS Using a High-Rsolution and High-Flux Soft X-ray from Synchrotron T2 - AIST-BAM Symposium on Materials Surface Technology in Twin Institute Programme CY - Tsukuba, Japan DA - 2003-02-18 KW - XPS KW - XAS KW - DLC KW - Synchrotron Radiation PY - 2003 SP - 67 EP - 69 AN - OPUS4-6927 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Retzko, Iris A1 - Treu, Dieter A1 - Matsubayashi, N. A1 - Imamura, M. A1 - Tanaka, T. A1 - Schulz, H. A1 - Lippitz, Andreas A1 - Unger, Wolfgang T1 - Analysis of carbon materials and plasma polymers by X-ray photoelectron spectroscopy and X-ray absorption spectroscopy (XPS, XAS) T2 - AIST-BAM Symposium on Materials Surface Technology in Twin Institute Programme CY - Tsukuba, Japan DA - 2003-02-18 PY - 2003 SP - 59 EP - 65 AN - OPUS4-6928 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Unger, Wolfgang T1 - The application of X-ray Photoelectron Spectroscopy (ESCA) and X-Ray Absorption Spectroscopy (NEXAFS) in Interface Analysis of Metallized Polymers T2 - AIST-BAM Symposium on Materials Surface Technology in Twin Institute Programme CY - Tsukuba, Japan DA - 2003-02-18 PY - 2003 SP - 53 EP - 58 AN - OPUS4-6929 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ullner, Christian T1 - Critical points in ISO 14577 part 2 and 3 considering the uncertainty in measurement T2 - HARDMEKO 2004 CY - Washington, DC, USA DA - 2004-11-11 KW - Indentation KW - Standard KW - Uncertainty PY - 2004 SP - 1 EP - 5(?) CY - Washington, DC AN - OPUS4-6946 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sojref, Regine ED - Pratsinis, S. E. T1 - "Donut like flow pattern" attrition milling of submicron corundum powder T2 - PARTEC 2004 ; International Congress for Particle Technology CY - Nuremberg, Germany DA - 2004-03-16 PY - 2004 SP - 1 EP - 4(?) PB - Nürnberg Messe GmbH CY - Nürnberg AN - OPUS4-6950 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wondraczek, L. A1 - Reinsch, Stefan A1 - Gaber, Martin A1 - Deubener, J. A1 - Müller, Ralf A1 - Komatsu, T. T1 - Nano-crystalline germanate glass-ceramics T2 - 78. Glastechnische Tagung CY - Nürnberg, Deutschland DA - 2004-06-07 PY - 2004 SP - 37 EP - 40 PB - Deutsche Glastechnische Gesellschaft CY - Offenbach AN - OPUS4-6953 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, P. A1 - Friedrich, Jörg Florian A1 - Meyer-Plath, Asmus T1 - Gezielte chemische Funktionalisierung von porösen Materialien und Bauteilen aus der Mikrosystemtechnik T2 - Workshop Funktionalisierung von Oberflächen für die Biotechnologie CY - Dresden, Deutschland DA - 2003-03-11 PY - 2003 SP - 1(?) EP - 8(?) PB - EFDS CY - Dresden AN - OPUS4-6962 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, P. A1 - Friedrich, Jörg Florian A1 - Meyer-Plath, Asmus T1 - Selective chemical modification of porous materials and films for bio-medical applications T2 - CIP 2003 ; 14th International Colloquium on Plasma Processes CY - Antibes, France DA - 2003-06-30 PY - 2003 SP - 1(?) EP - 4(?) PB - sfv, Sociéte Française du Vide CY - Paris AN - OPUS4-6963 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Maultzsch, Matthias A1 - Meinhold, Uwe T1 - Ansteifen von Beton: Möglichkeiten der Prüfung PY - 1979 VL - 13 SP - 1 EP - 3 PB - Verband Deutscher Betoningenieure CY - Duisburg AN - OPUS4-6916 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maultzsch, Matthias A1 - Gierloff, M. A1 - Schimmelwitz, Peter T1 - Aging of cement through long term storage T2 - 7th International Congress on the Chemistry of Cement ; 7ère Congrès International de la Chimie des Ciments CY - Paris, France DA - 1980-01-01 PY - 1980 VL - 2 SP - I-128-I-133 PB - Ed. Septima CY - Paris AN - OPUS4-6917 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maultzsch, Matthias A1 - Meinhold, Uwe T1 - Testing methods for the set of pastes and mortars T2 - 7th International Congress on the Chemistry of Cement ; 7e Congrès International de la Chimie des Ciments CY - Paris, France DA - 1980-01-01 PY - 1980 VL - 3 SP - VI-158-VI-163 PB - Ed. Septima CY - Paris AN - OPUS4-6918 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Güttler, B. A1 - Schiel, D. A1 - Danzebrink, H. A1 - Unger, Wolfgang A1 - Gross, Thomas A1 - Lippitz, Andreas A1 - Müller, J.-P. T1 - Physical and Chemical Characterization of Thermal and Native Siliconoxide layers on Silicon T2 - Symposium "Reference Materials for Technologies in the New Millenium" CY - Berlin, BAM, Germany DA - 2000-05-22 PY - 2000 SP - 1(?) EP - 7(?) AN - OPUS4-6924 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Werner ED - Jost, D. T1 - Eignungsgutachten für Kunststoff-Dränelemente durch die BAM T2 - 21. Fachtagung "Die sichere Deponie" CY - Würzburg, Deutschland DA - 2005-02-09 KW - Scherfestigkeit KW - Beständigkeit KW - Geokunststoffe KW - Prüftechnik PY - 2005 SP - C1 EP - C18 PB - SKZ CY - Würzburg AN - OPUS4-7027 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schoknecht, Ute T1 - Comparison of laboratory tests and field experiments for the estimation of emissions from treated wood T2 - 6th International Symposium "Environment and wood preservation" CY - Cannes-Mandelieu, France DA - 2005-02-07 KW - Leaching KW - Emission KW - Copper KW - Triazoles KW - Test procedures PY - 2005 SP - 2 EP - 14 PB - IRG Secretariat CY - Stockholm AN - OPUS4-7028 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mosel, Günter A1 - Nofz, Marianne A1 - Hübert, Thomas A1 - Brenneis, Rudolf A1 - Köcher, Peter A1 - Kley, Gerd T1 - Zn-K EXAFS investigations on ZnO/ZnS-containing vitrified incinerator ashes PY - 1998 SP - 833 EP - 834 PB - Hamburger Synchrotonstrahlungslabor CY - Hamburg AN - OPUS4-7033 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mosel, Günter A1 - Nofz, Marianne A1 - Lange, Dörte A1 - Hübert, Thomas T1 - The local environment of vanadium ions in glasses of the system ZnO-B2O3-V2O5 investigated by V-K EXAFS spectroscopy PY - 1996 SP - 749 EP - 750 PB - Hamburger Synchrotonstrahlungslabor CY - Hamburg AN - OPUS4-7034 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mosel, Günter A1 - Nofz, Marianne A1 - Hübert, Thomas T1 - An EXAFS investigation of the local order of Fe2+ and Fe3+ ions in a silicate glass at low Fe concentrations PY - 1997 SP - 743 EP - 744 PB - Hamburger Synchrotonstrahlungslabor CY - Hamburg AN - OPUS4-7035 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Behrendt, Bodo A1 - Hübert, Thomas T1 - Zerstörungsfreie Materialprüfung an Flachglas mit Ultraschall T2 - 71. Glastechnische Tagung CY - Bayreuth, Deutschland DA - 1997-05-26 PY - 1997 SP - 19 EP - 22 CY - Frankfurt/Main AN - OPUS4-7036 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maultzsch, Matthias A1 - Isecke, Bernd ED - Gregor, H. T1 - Korrosion von Stahl und Beton durch Auftaumittel T2 - 68. FGU-Seminar "Fortbildungszentrum Gesundheits- und Umweltschutz" CY - Berlin, Deutschland DA - 1982-06-15 PY - 1982 N1 - Serientitel: FGU-Seminar – Series title: FGU-Seminar IS - 68 SP - 1(?) EP - 10(?) CY - Berlin AN - OPUS4-7037 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, P. A1 - Wigant, L. A1 - Friedrich, Jörg Florian ED - Nowack, H. T1 - Permeabilitätsverminderung von Polyolefinfilmen durch Plasmapolymerbeschichtungen T2 - 5. Internationale Fachtagung - ND-Plasma-Technologie CY - Duisburg, Deutschland DA - 1997-09-22 PY - 1997 VL - 5 SP - 1(?) EP - 16(?) PB - Print-Service CY - Mülheim AN - OPUS4-6996 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Friedrich, Jörg Florian ED - Scheyrer, P. T1 - Vergleich der Wirksamkeit verschiedener Normal- und Niederdruckplasmen bei der Vorbehandlung von Kunststoffen T2 - Seminar Beschriften und vollflächiges Dekorieren von Kunststoffoberflächen CY - Würzburg, Deutschland DA - 1999-03-30 PY - 1995 SP - 14 Seiten PB - Süddeutsches Kunststoffzentrum CY - Würzburg AN - OPUS4-7002 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maultzsch, Matthias A1 - Kwasny, R. T1 - Technische Lieferbedingungen und Prüfvorschriften für Zementmörtel/Beton mit Kunststoffzusatz TL/TP BE-PCC als Bestandteil der ZTV-SIB T2 - Lehrgang CY - Ostfildern, Deutschland DA - 1988-02-23 PY - 1988 IS - 10147-83-064 SP - 1(?) EP - 24(?) PB - Techn. Akad. Esslingen CY - Ostfildern AN - OPUS4-7068 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kwasny, R. A1 - Maultzsch, Matthias T1 - Technische Lieferbedingungen und Prüfvorschriften für Reaktionsharzmörtel/-beton TL/TP BE-PC und Oberflächenschutzsysteme TL/TP OS als Bestandteile der ZTV-SIB T2 - Lehrgang CY - Ostfildern, Deutschland DA - 1988-02-23 PY - 1988 IS - 10147-83-064 SP - 1(?) EP - 16(?) PB - Techn. Akad. Esslingen CY - Ostfildern AN - OPUS4-7069 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maultzsch, Matthias T1 - Technische Lieferbedingungen und Prüfvorschriften für Zementmörtel/Beton mit Kunststoffzusatz TL/TP BE-PCC und Reaktionsharzmörtel/-beton TL/TP BE-PC als Bestandteile der ZTV-SIB T2 - Lehrgang CY - Ostfildern, Deutschland DA - 1989-11-07 PY - 1989 IS - 11963-83-089 PB - Techn. Akad. Esslingen CY - Ostfildern AN - OPUS4-7072 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maultzsch, Matthias T1 - Technische Lieferbedingungen und Prüfvorschriften für Oberflächenschutzsysteme TL/TP OS als Bestandteile der ZTV-SIB T2 - Lehrgang CY - Ostfildern, Deutschland DA - 1989-11-07 PY - 1989 IS - 11963-83-089 PB - Techn. Akad. Esslingen CY - Ostfildern AN - OPUS4-7073 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Steiger, Thomas A1 - Pradel, Rita T1 - COMAR - status and user possibilities KW - COMAR database KW - Certified reference materials KW - CRM KW - Reference materials KW - RM KW - CITAC PY - 2005 SP - 9 EP - 11 CY - Jerusalem, Israel AN - OPUS4-7064 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maultzsch, Matthias T1 - Tests on polymer modified cement mortars for the repair of concrete structures T1 - L'essai pour des mortiers au ciment modifies par des polymers afin d'assainir des batiments en beton T2 - International Symposium CY - Liège, Belgium DA - 04.06.1984 PY - 1984 VL - 2 SP - 4.2.1 EP - 4.2.5 CY - Lüttich AN - OPUS4-7046 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maultzsch, Matthias T1 - Kunststoffmodifizierte Zementmörtel PY - 1987 SP - 1(?) EP - 7(?) CY - Berlin AN - OPUS4-7052 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mellmann, Günter A1 - Krupke, Hans-Joachim A1 - Maultzsch, Matthias T1 - Biegefestigkeit von Flachglas T2 - Gemeinsame Jahrestagung der Deutschen Keramischen Gesellschaft (DKG) und der Deutschen Glastechnischen Gesellschaft (DGG) CY - Berlin, Deutschland DA - 1987-09-21 PY - 1987 SP - 172 EP - 175 AN - OPUS4-7054 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Friedrich, Jörg Florian A1 - Kühn, Gerhard A1 - Mix, Renate T1 - Tailoring of Polymer Surfaces with Different Monotype Functional Groups of Variable Density Using Chemical and Plasma Chemical Processes T2 - 10th Dresden Polymer Discussion: Characterization of Polymer Surfaces and Thin Films CY - Meißen, Germany DA - 2005-04-10 KW - Plasma modification KW - Introduction of functional groups KW - Reactions at polymer surfaces PY - 2005 SP - 34 EP - 49 PB - Leibniz-Institut für Polymerforschung Dresden CY - Meißen AN - OPUS4-7332 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Friedrich, Jörg Florian A1 - Kühn, Gerhard T1 - Kontrolle der Plasmamodifizierung von Polymeroberflächen mittels ESCA PY - 1998 VL - 70 SP - 5 CY - Darmstadt AN - OPUS4-7285 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mitropetros, Constantinos A1 - Fomine, Pavel A1 - Steinbach, J. A1 - Hieronymus, Hartmut T1 - Bubble ignition induced by nearby bubble explosion inside a multi-dispersed bubbly medium N2 - The present work discusses the role of the distance between single explosive bubbles on their explosion behavior after the passage of an incident shock wave. The investigated system was liquid cyclohexane containing oxidizer bubbles. High speed optical and pressure measurements were applied. It was found that if the distance is short enough, then the shock wave caused by a bubble explosion can ignite a nearby compressed bubble. The experimental finding that bubbles can be ignited by shock waves emitted during nearby bubble explosions, indicates that a process of synchronization of bubble explosions can occur. This synchronization process offers a better understanding of the propagation mechanism of self-sustaining bubble detonation waves inside bubbly media. T2 - European Combustion Meeting (ECM 2005) CY - Louvain-la-Neuve, Belgium DA - 2005-04-03 KW - Bubble explosion PY - 2005 SP - 1 EP - 6 PB - Université Catholique de Louvain CY - Louvain AN - OPUS4-7320 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Görner, Wolf A1 - Reinholz, Uwe T1 - Wasserstoffanalytik mit hochenergetischen Ionen KW - Wasserstoff KW - Ionenstrahlanalytik KW - Kernreaktionsanalyse PY - 2005 UR - http://archiv.aktuelle-wochenschau.de/2005/woche15/woche15.html IS - 15 SP - 1 EP - 11 PB - Gesellschaft Deutscher Chemiker CY - Frankfurt am Main AN - OPUS4-7324 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fomine, Pavel A1 - Mitropetros, Constantinos A1 - Hieronymus, Hartmut T1 - Theoretical analysis of shock induced bubble explosion with long ignition delay T2 - European Combustion Meeting (ECM 2005) CY - Louvain-la-Neuve, Belgium DA - 2005-04-03 KW - Bubble explosion PY - 2005 SP - 6 pages PB - Université Catholique de Louvain CY - Louvain AN - OPUS4-7338 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schoknecht, Ute T1 - Testverfahren zur Bestimmung von Biozidemissionen aus behandeltem Holz T2 - 24. Holzschutztagung "Sicherung von Produktqualität und -leistung" CY - Leipzig, Deutschland DA - 2005-04-12 KW - EU-Biozidrichtlinie KW - OECD guideline KW - Biozide KW - Emissionen KW - Testverfahren KW - Holzschutzmittel PY - 2005 SP - 49 EP - 56 PB - Deutsche Gesellschaft für Holzforschung CY - Leipzig AN - OPUS4-7340 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, P. A1 - Friedrich, Jörg Florian T1 - Gezielte chemische Funktionalisierung von Polymermaterialien T2 - 4. Wörlitzer Workshop "Funktionelle Schichten" CY - Wörlitz, Deutschland DA - 2003-05-27 PY - 2003 VL - 4 SP - 1(?) EP - 7(?) PB - EFDS CY - Dresden AN - OPUS4-7289 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hasenstab, Andreas T1 - Zerstörungsfreie Materialprüfung von Holz mit Ultraschallecho- und mobiler Röntgentechnik T2 - 15. Weiterbildungstag - Holzschutz CY - Berlin, Deutschland DA - 2004-12-04 PY - 2004 SP - 59 Seiten PB - TFH-Wedding, Berlin CY - Berlin AN - OPUS4-6863 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rücker, Werner A1 - Karstedt, J. T1 - Schwingungsmessungen beim Rammen von Stahlspundwänden T2 - Symposium Messtechnik im Erd- und Grundbau CY - Munich, Germany DA - 23.11.1983 PY - 1983 SP - 49 EP - 55 PB - Deutsche Gesellschaft für Erd- und Grundbau e.V. CY - Essen AN - OPUS4-6647 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Senoner, Mathias A1 - Wirth, Thomas A1 - Unger, Wolfgang T1 - A reference material for calibration and testing of instruments with nanometric lateral resolution T2 - SIMS Europe 2002 ; 3rd European Workshop on Secondary Ion Mass Spectrometry CY - Münster, Germany DA - 2002-09-15 PY - 2002 SP - 58 AN - OPUS4-6841 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Almagro, J.-F. A1 - Busch, P. A1 - Gohil, D. D. A1 - Saunders, S. R. J. A1 - Sloof, W. G. A1 - Thiot, J.-F. A1 - Schneider, H. A1 - Whitwood, M. A1 - Wirth, Thomas T1 - Electron-Probe MICROanalysis of LighT Elements - Measurement Methods and Certified Reference Materials (MICROLITE) PY - 2000 IS - 266 SP - 1 EP - 35 PB - National Physical Laboratory CY - Teddington, Middlesex AN - OPUS4-6843 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koch, Frank A1 - Rieg, F. A1 - Hackenschmidt, R. T1 - Improve Testing by Simultaneous Simulation during the Development of Pumps T2 - Virtual Product Development Conference 2004 CY - Munich, Germany DA - 2004-11-22 KW - Testing KW - Pumps KW - Strain Gauge KW - CAD KW - MSC KW - Marc PY - 2004 SP - 1 EP - 26 AN - OPUS4-6876 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Senoner, Mathias T1 - Ringversuch - Bestimmung von Stufenhöhen im Nanometerbereich mit dem Rasterkraftmikroskop - Abschlussbericht (Projekt "Qualitätssicherung in der Nanoanalytik") KW - AFM KW - Nanotechnologie KW - Rasterkraftmikroskopie KW - Ringversuch KW - Stufenhöhenbestimmung KW - Verfahrensvalidierung PY - 2001 SP - 1 EP - 41 CY - Berlin AN - OPUS4-6880 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Procop, Mathias T1 - Röntgenspektroskopie am Rasterelektronenmikroskop PY - 2001 SP - 1 EP - 26 AN - OPUS4-6834 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Marotzke, Christian A1 - Qiao, Linan T1 - Analysis of fiber, matrix and interface fracture in composites and fragmentation tests T2 - 9th ECCM ; 9th [European Conference on Composite Materials] CY - Brighton, England, UK DA - 2000-06-04 KW - Interface crack KW - Energy release rate KW - Fracture mechanics KW - Debonding KW - Thermal stresses KW - Friction KW - Finite element method KW - FEM PY - 2000 N1 - Serientitel: CF / IOM Communications Ltd – Series title: CF / IOM Communications Ltd IS - 11 SP - 1 EP - 10(?) PB - IOM Communications CY - London AN - OPUS4-6808 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Marotzke, Christian ED - Jono, M. ED - Inoue, T. T1 - Micromechanical investigation of fibre reinforced polymers PY - 1991 VL - 3 SP - 67 EP - 72 PB - Pergamon Press CY - Oxford AN - OPUS4-6815 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Marotzke, Christian T1 - Influence of the Fiber Length on the Stress from Glass and Carbon Fibers into a Thermo-plastic Matrix PY - 1993 VL - 1 IS - 2 SP - 153 EP - 166 PB - North-Holland CY - New York, NY AN - OPUS4-6818 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hampe, Andreas A1 - Marotzke, Christian T1 - The fracture toughness of the glass fibre/polymer matrix interface: measurement and theoretical analysis T2 - The fracture toughness of the glass fibre/polymer matrix interface: measurement and theoretical analysis CY - Guildford, England, UK DA - 1995-03-27 PY - 1995 CY - Guildfort AN - OPUS4-6823 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hampe, Andreas A1 - Marotzke, Christian T1 - The energy release rate of the fiber/polymer matrix interface: measurement and theoretical analysis PY - 1995 SP - 326 EP - 335 PB - Technomic Publ. CY - Lancaster AN - OPUS4-6824 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heyn, Andreas A1 - Göllner, J. A1 - Bierwirth, M. A1 - Burkert, Andreas T1 - Application of electrochemical noise measurements for salt-spray testing T2 - Corrosion 2005 CY - Houston, TX, USA DA - 2005-04-03 KW - Salt-spray testing KW - Electrochemical noise KW - Corrosion testing KW - Corrosion monitoring KW - Video monitoring PY - 2005 SP - 05364\1 EP - 05364\12 PB - NACE International CY - Houston AN - OPUS4-7154 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maultzsch, Matthias ED - Zajc, A. T1 - Prüfung der Beständigkeit von Beton - Preskusanje obstojnosti betonov T2 - 7. Slowenisches Beton-Kolloquium CY - Ljubljana, Slovenia DA - 2000-05-18 PY - 2000 SP - 51 EP - 55 AN - OPUS4-7160 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maultzsch, Matthias A1 - Raupach, M. A1 - Rößler, G. T1 - Seawater resistance of polymer-modified cement mortars T2 - 10th International Congress on Polymers in Concrete ; ICPIC/ICRI International Concrete Repair Workshop CY - Honolulu, HI, USA DA - 2001-05-21 PY - 2001 SP - 1(?) EP - 15(?) AN - OPUS4-7163 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maultzsch, Matthias T1 - Effect of curing conditions on properties of polymer modified repair mortars T2 - European Colloquium "Construction - Renovation. Contribution of Organic Polymers" CY - Lyon, France DA - 1992-09-08 PY - 1992 SP - 219 EP - 225 CY - Lyon AN - OPUS4-7100 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Maultzsch, Matthias ED - Paturoev, V. ED - Serych, R. T1 - Early shrinkage of polymer modified cement mortar (PCC) T2 - 7th International Congress on Polymers in Concrete (ICPIC) CY - Moscow, Russia DA - 1992-09-22 PY - 1992 VL - 7 SP - 730 EP - 737 PB - Science Business Contact International CY - Moscow AN - OPUS4-7101 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maultzsch, Matthias T1 - Technische Lieferbedingungen und Prüfvorschriften für Zementmörtel/Beton mit Kunststoffzusatz TL/TP BE-PCC, TL/TP BE-SPCC und Reaktionsharzmörtel/-beton TL/TP BE-PC als Bestandteile der ZTV-SIB T2 - Tagung CY - Dresden-Langebrück, Deutschland DA - 1992-12-03 PY - 1992 SP - 1(?) EP - 21(?) PB - Techn. Akad. Esslingen CY - Ostfildern AN - OPUS4-7102 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maultzsch, Matthias T1 - Technische Lieferbedingungen und Prüfvorschriften für Oberflächenschutzsysteme TL/TP OS als Bestandteile der ZTV-SIB T2 - Tagung CY - Dresden-Langebrück, Deutschland DA - 1992-11-03 PY - 1992 SP - 1(?) EP - 14(?) PB - Techn. Akad. Esslingen CY - Ostfildern AN - OPUS4-7103 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maultzsch, Matthias T1 - Technische Lieferbedingungen und Prüfvorschriften für Zementmörtel/Beton mit Kunststoffzusatz TL/TP BE-PCC, TL/TP BE-SPCC und Reaktionsharzmörtel/-beton TL/TP BE-PC als Bestandteile der ZTV-SIB T2 - Tagung CY - Sarnen, Schweiz DA - 1993-03-23 PY - 1993 SP - 1(?) EP - 21(?) PB - Techn. Akad. Esslingen CY - Ostfildern AN - OPUS4-7104 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maultzsch, Matthias T1 - Technische Lieferbedingungen und Prüfvorschriften für Oberflächenschutzsysteme TL/TP OS als Bestandteile der ZTV-SIB T2 - Tagung CY - Sarnen, Schweiz DA - 1993-03-23 PY - 1993 SP - 1(?) EP - 14(?) PB - Techn. Akad. Esslingen CY - Ostfildern AN - OPUS4-7105 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maultzsch, Matthias T1 - Comprehensive tests on concrete repair materials according to ZTV-SIB Specifications, recent experiences and results T2 - CSTB-CEFRACOR Symposium Corrosion Deterioration in Building CY - Paris, France DA - 1990-11-13 PY - 1990 SP - 1(?) EP - 7(?) AN - OPUS4-7081 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maultzsch, Matthias T1 - Technische Lieferbedingungen und Prüfvorschriften für Zementmörtel/Beton mit Kunststoffzusatz TL/TP BE-PCC, TL/TP BE-SPCC und Reaktionsharzmörtel/-beton TL/TP BE-PC als Bestandteile der ZTV-SIB T2 - Lehrgang CY - Ostfildern, Deutschland DA - 1991-11-27 PY - 1991 PB - Techn. Akad. Esslingen CY - Ostfildern AN - OPUS4-7082 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maultzsch, Matthias T1 - Technische Lieferbedingungen und Prüfvorschriften für Oberflächenschutzsysteme TL/TP OS als Bestandteile der ZTV-SIB T2 - Lehrgang CY - Ostfildern, Deutschland DA - 1991-11-27 PY - 1991 PB - Techn. Akad. Esslingen CY - Ostfildern AN - OPUS4-7083 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maultzsch, Matthias ED - Schorn, H. ED - Middel, M. T1 - Effects of moisture content and water migration on PCC properties T2 - International Symposium CY - Bochum, Germany DA - 1991-03-12 PY - 1991 SP - 169 EP - 173 PB - Univ., Inst. für Konstruktiven Ingenieurbau CY - Bochum AN - OPUS4-7084 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maultzsch, Matthias T1 - Betonersatz nach ZTV-SIB 90 - Möglichkeiten - Probleme - Grenzen T2 - Fachtagung "Sonderkapitel aus dem Brücken- und Ingenieurbau" CY - Berlin, Deutschland DA - 1993-04-27 PY - 1993 SP - 1(?) EP - 5(?) AN - OPUS4-7106 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maultzsch, Matthias T1 - Thermische Kompatibilität von Mörteln für die Betoninstandsetzung T2 - 12. Internationale Baustofftagung "ibausil" CY - Weimar, Deutschland DA - 1994-09-22 PY - 1994 IS - Bd. 2 SP - 48 EP - 57 CY - Weimar AN - OPUS4-7108 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maultzsch, Matthias T1 - Effects of cyclic wetting and drying on polymer modified cement mortars T2 - International ICPIC Workshop on Polymers in Concrete CY - Bled, Slovenia DA - 1996-09-10 PY - 1996 SP - 14 EP - 15 PB - ICPIC CY - Bled, Slovenia AN - OPUS4-7113 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Maultzsch, Matthias T1 - Forschung auf dem Gebiet der Baustoffe in der BAM T2 - Beiträge zum 33. Forschungskolloquium CY - Berlin, BAM, Deutschland DA - 1996-10-10 PY - 1996 VL - 33 SP - 11 EP - 14 PB - Dt. Ausschuss für Stahlbeton im DIN CY - Berlin AN - OPUS4-7114 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Maultzsch, Matthias T1 - Eignung von Recyclingmaterial für hochwertigen Beton T2 - Beiträge zum 33. Forschungskolloquium CY - Berlin, BAM, Deutschland DA - 1996-10-10 PY - 1996 VL - 33 SP - 33 EP - 38 PB - Dt. Ausschuss für Stahlbeton im DIN CY - Berlin AN - OPUS4-7115 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Klingbeil, Patrick T1 - Methodenentwicklung für die Präzisionsanalytik von Spurenelementen mittels Multikollektor-ICP-MS unter Anwendung der Isotopenverdünnungstechnik N2 - Methodenentwicklung für die Präzisionsanalytik von Spurenelementen mittels Multikollektor-ICP-MS unter Anwendung der Isotopenverdünnungstechnik Mit der Multikollektor-ICP-MS (ICP-MC-MS) und in Verbindung mit der Isotopenverdünnungstechnik wurden Methoden entwickelt, um die Quantifizierung von Spurenelementen in verschiedensten Matrices mit höchstmöglicher Präzision zu ermöglichen. Bei Bestimmungen mittels konventioneller ICP-MS auftretende polyatomare Interferenzen, wie ArO, ArN oder ArC, konnten durch die Entwicklung optimierter Verfahrensparameter unter Einsatz der Kollisionszellentechnik eliminiert werden. Der Nachweis der vollständigen Eliminierung konnte durch die Aufnahme von hochaufgelösten Massenspektren erbracht werden. Die Praxistauglichkeit der hier entwickelten Methoden wurde anhand der Zertifizierung von Schwermetallgehalten in verschiedenen Matrices nachgewiesen. Bei der Zertifizierung des Quecksilber-Gehalts in Polyethylen konnte demonstriert werden, daß ein Analytelement, bei dessen Bestimmung mit ICP-MS regelmäßig Unterbefunde auftreten, durch die Isotopenverdünnungstechnik in Verbindung mit ICP-MC-MS zuverlässig bestimmt werden kann. Vergleichende Bestimmungen zur Zertifzierung von Cadmium- und Thallium-Gehalten in einer metallischen Matrix, die simultan auch mit Multikollektor-TIMS und Quadrupol-ICP-MS durchgeführt wurden, zeigten eine erhöhte Robustheit gegenüber der untersuchten Zink-Matrix. Für die ICP-MC-MS wurde ein Untergrundkorrekturverfahren neu entwickelt. Mit diesem Verfahren konnten bei Zink-Proben bis zu einer Matrixlast von 1 g/kg Lösung Präzisionen der Isotopenverhältnismessung erreicht werden, die bisher nur mit der Multikollektor-TIMS zu verwirklichen waren. So konnten beispielsweise Thallium-Isotopenverhältnisse mit einer Wiederholpräzision von besser als 0,01 % bestimmt werden. Anhand der hochpräzisen Zertifizierung einer 26Magnesium-Spike-Lösung wurde eine Möglichkeit aufgezeigt, zukünftig die Isotopenverdünnungstechnik einem breiteren Kreis von Anwendern konventioneller ICP-MS zugänglich zu machen. In dieser Arbeit wurden Urin und Blutproben von Probanden untersucht, denen in einer Studie an der ETH Zürich 25Magnesium oral und 26Magnesium intravenös zugeführt wurden. Die Ergebnisse zeigen die prinzipielle Anwendbarkeit der Methode für Studien von Stoffwechselvorgängen. Aussagen über biologische Zusammenhänge waren wegen der geringen Probenzahl nicht möglich. Die Präzision der Messung der Magnesium-Isotopenverhältnisse mit der entwickelten Technik war so hoch, daß sogar Variationen in der Isotopenzusammensetzung von Magnesium-Proben unterschiedlicher Herkunft nachgewiesen werden konnten. Eine Weiterentwicklung der Isotopenverdünnungsanalyse stellt das Online-Isotopenverdünnungssystem dar. In der vorliegenden Arbeit wurde ein Pumpensystem eingesetzt, das eine Erhöhung des Automatisierungsgrades und somit auch einen höheren Probendurchsatz ermöglicht. Weiterhin konnte in Verbindung mit der ICP-MS die Quantifizierung von transienten Signalen durchgeführt werden. Die universelle Einsatzfähigkeit eines solchen Systems wurde durch die Kopplung mit einem chromatographischen Trennsystem und einer anschließenden Metallothionein-Quantifizierung in einer tierischen Gewebeprobe demonstriert. KW - Quantitative Analyse KW - ICP-Massenspektrometrie KW - Isotopenverdünnungsanalyse KW - Spurenelement PY - 2002 UR - http://webdoc.sub.gwdg.de/ebook/diss/2003/tu-berlin/diss/2001/klingbeil_patrick.pdf SP - 1 EP - 171 PB - Technische Universität CY - Berlin AN - OPUS4-7225 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maierhofer, Christiane A1 - Kohl, Christoph A1 - Mayer, K. T1 - Radar in der DFG-Forschergruppe FOR384 T2 - DAfStb-Fachtagung 2005 "Zerstörungsfreie Prüfverfahren und Bauwerksdiagnose im Betonbau" CY - Berlin, Deutschland DA - 2005-03-10 KW - Zerstörungsfreie Prüfung im Bauwesen KW - Radar KW - Datenfusion KW - Bewehrung KW - Spannkanal KW - Hohlkastenbrücke PY - 2005 SP - A19 EP - A24 PB - BAM CY - Berlin AN - OPUS4-7208 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jann, Oliver A1 - Wilke, Olaf T1 - Comparison of FLEC with other climate chambers, Gemeran experiences T2 - 2nd International FLEC Symposium CY - Copenhagen, Denmark DA - 2001-09-06 PY - 2001 SP - 18 EP - 27 AN - OPUS4-7204 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ewert, Uwe A1 - Zscherpel, Uwe T1 - New detectors and perspectives in industrial radiography KW - Radiographie KW - Detectors KW - ZfP KW - Corrosion PY - 2005 VL - 12 IS - 1 SP - 59 EP - 71 PB - National Association for Applications of Radioisotopes and Radiation in Industry CY - Mumbai AN - OPUS4-7229 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilke, Olaf T1 - Emissionsmessungen an strahlenhärtenden Lacksystemen T2 - 8. UCB Radcure-Symposium CY - Dresden, Deutschland DA - 1997-09-11 PY - 1997 AN - OPUS4-7238 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Liebner, Christian T1 - Self-ignition of hydrocarbon-oxidiser mixtures at pressures up to 30 bar T2 - 2nd International Conference "Fire Bridge - Advances and future of accidental combustion research" CY - Ulster, Northern Ireland DA - 2005-05-09 KW - Autoignition KW - Ignition Temperature KW - Cool Flame KW - Slow Combustion PY - 2005 SP - 18 pages PB - University of Ulster CY - Ulster AN - OPUS4-7410 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mc Hugh, Jarlath A1 - Döring, Joachim A1 - Bartusch, Jürgen A1 - Stark, Wolfgang T1 - Making Cure Visible T2 - Aerospace Testing Expo 2005 - Europe, April 5-7, 2005, Hamburg CY - Hamburg, Deutschland DA - 2005-04-05 PY - 2005 SP - 4 pages PB - UKIP Media & Events CY - Dorking AN - OPUS4-7379 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Schoknecht, Ute A1 - Mathies, Helena A1 - Morsing, N. A1 - Lindegaard, B. A1 - van der Sloot, H. A1 - van Zomeren, A. A1 - Deroubaix, G. A1 - Legay, S. A1 - Tadeo, J. L. A1 - García-Valcárcel, A. I. A1 - Gigliotti, G. A1 - Zadra, C. A1 - Hajslová, J. A1 - Tomaniová, M. A1 - Wegner, R. A1 - Bornkessel, C. A1 - Fürhapper, C. T1 - Inter-laboratory evaluation of laboratory test methods to estimate the leaching from treated wood - Agreement No. 04/375757/C4 KW - Emission KW - Leaching KW - Wood preservatives KW - Inter-laboratory evaluation KW - Test methods KW - OECD guideline proposals PY - 2005 SP - 1 EP - 211 CY - Berlin AN - OPUS4-7365 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krebber, Katerina A1 - Habel, Wolfgang A1 - Gutmann, Toivo A1 - Schramm, Ch. T1 - Monitoring of the rotor blades of wind turbines by fibre optic sensors N2 - In order to monitor the mechanical behaviour of the rotor blades of wind turbines, fibre optic sensors are increasingly attached to or embedded in the blades. Usually, fibre Bragg grating sensors arrays are then used. In order to investigate how stable and reliably work such sensors, fibre Bragg grating arrays were embedded into textile-reinforced composite. Long-term temperature and tensile (fatigue) tests have been carried out with composite structure specimens. This paper reports on selected results of the tests and discusses important reliability aspects with regard to the fibre design and the fibre material. T2 - 3rd International Conference on Materials Testing "TEST 2005" CY - Nuremberg, Germany DA - 2005-05-10 KW - Faseroptische Sensorik PY - 2005 SP - B.5-55-B.5-60 PB - AMA Service GmbH CY - Nürnberg AN - OPUS4-7440 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maierhofer, Christiane A1 - Wendrich, Astrid A1 - Köpp, Christian T1 - ONSITEFORMASONRY - A European Research Project: On-site investigation techniques for the structural evaluation of historic masonry T2 - Itecom European Conference : Innovative Technologies and Materials for the Protection of Cultural Heritage. Industry, Research, Education: European Acts and Perspectives CY - Athens, Greece DA - 2003-12-16 KW - Non-destructive testing in civil engineering KW - Historic masonry KW - Structural modelling PY - 2003 SP - 1(?) EP - 10(?) AN - OPUS4-7446 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Simone A1 - Goering, Harald A1 - Stark, Wolfgang A1 - Bayerl, H. A1 - Brinkmann, P. T1 - Thermoanalytische Untersuchungen zur Phenolharzhärtung unter hohem Druck - Ein Weg zur Optimierung der Nachtemperung T2 - 3rd International Thermoset Conference CY - Iserlohn, Deutschland DA - 2005-04-21 KW - Post curing KW - High pressure DSC KW - DMA KW - Reaction kinetic KW - Phenolic resin PY - 2005 SP - 107 EP - 114 PB - Fachhochschule Südwestfalen - Hochschule für Technik und Wirtschaft CY - Iserlohn AN - OPUS4-7452 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Simone A1 - Goering, Harald A1 - Stark, Wolfgang A1 - Bayerl, H. A1 - Brinkmann, P. T1 - Thermo Analytical Investigations of Phenol Moulding Compound Curing - Potential for Post-Cure Optimisation T2 - 3rd International Thermoset Conference CY - Iserlohn, Germany DA - 2005-04-21 KW - Post curing KW - High pressure DSC KW - DMA KW - Reaction kinetic KW - Phenolic resin PY - 2005 SP - 219 EP - 225 PB - Fachhochschule Südwestfalen - Hochschule für Technik und Wirtschaft CY - Iserlohn AN - OPUS4-7453 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wehrstedt, Klaus-Dieter T1 - Testing and classification of new energetic substances and mixtures according to the UN Recommendations on the Transport of Dangerous Goods T2 - Third NRIFD Symposium - International Symposium on Safety in the Manufacture, Storage, Use, Transport and Disposal of Hazardous Materials CY - Tokyo, Japan DA - 2004-03-10 PY - 2004 SP - 201 EP - 217 PB - National Research Institute of Fire and Disaster (NRIFD) CY - Tokio AN - OPUS4-7454 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard A1 - Müller, Karsten A1 - Quercetti, Thomas T1 - Full-scale Drop Testing of Spent Fuel Transport and Storage Casks: experiences of BAM and new Developments T2 - 46th Annual Meeting of the Institute for Nuclear Materials Management CY - Phoenix, AZ, USA DA - 2005-07-10 KW - Drop tests KW - Spent fuel transport packages PY - 2005 SP - 6 pages PB - Institute for Nuclear Materials Management CY - Phoenix AN - OPUS4-7614 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard T1 - Fallversuche im Verfahren zur Zulassung neuer Behälterbauarten - Neuer Fallversuchsstand der BAM T2 - 4. Symposium "Lagerung und Transport radioaktiver Stoffe - Stand der BE-Entsorgung CY - Hannover, Deutschland DA - 2005-05-14 KW - Mechanische Prüfung KW - Transportbehälter für radioaktive Stoffe KW - Fallversuche PY - 2005 SP - 18 Seiten PB - TÜV CY - Hannover AN - OPUS4-7615 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Seeger, Stefan T1 - Zulassung von Schutzlagen T2 - 11. Fachtagung "Die sichere Deponie" CY - Würzburg, Deutschland DA - 1995-02-16 PY - 1995 IS - 11 SP - 1(?) EP - 11(?) CY - Würzburg AN - OPUS4-7587 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Seeger, Stefan T1 - Dichtungskontrollsysteme für Oberflächenabdichtungen T2 - 16. Fachtagung "Die Sichere Deponie" CY - Würzburg, Deutschland DA - 2000-02-10 PY - 2000 IS - 16 SP - H2 EP - H22 PB - SKZ CY - Würzburg AN - OPUS4-7576 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Seeger, Stefan T1 - Anforderungen an Dichtungskontrollsysteme in Oberflächenabdichtungen von Deponien - Überblick der Empfehlungen des Arbeitskreises Dichtungskontrollsysteme T2 - 17. Fachtagung "Die Sichere Deponie" CY - Würzburg, Deutschland DA - 2001-02-15 PY - 2001 IS - 17 SP - 1 EP - 11(?) PB - SKZ CY - Würzburg AN - OPUS4-7580 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Seeger, Stefan T1 - Long term waste containment - A challenge to geotextiles and geomembranes made of plastic materials T2 - International Symposium On Advanced Materials For Functional Manifestation of Frontier And Environmental Consciousness CY - Tokyo, Japan DA - 1997-09-01 PY - 1997 SP - 1(?) EP - 8(?) AN - OPUS4-7581 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Seeger, Stefan T1 - Granta CES Web Software Helps Promote Natural Fibre Eco-Materials N2 - Dr. Stefan Seeger of the German Federal Institute for Materials Research and Testing (Bundesanstalt für Materialforschung und -prüfung - BAM) tells of his successful experience using Granta's CES software to make an eco-materials knowledge resource for automotive, construction, and other industries in the Berlin region. T2 - Abfallwirtschaft für Wien CY - Wien, Österreich DA - 2004-06-24 PY - 2005 SP - 1 EP - 2 PB - Granta CY - Cambridge AN - OPUS4-7582 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maultzsch, Matthias T1 - ENBRI - The Basis of European Cooperation in Building Research T2 - Sympozjum Instytuty Badawcze Budownictwa W Unii Europejskiej CY - Warszawa, Poland DA - 2005-05-24 KW - Building research KW - Research institutes KW - Networks PY - 2005 SP - 33 EP - 41 PB - Instytut Techniki Budowlanej CY - Warschau AN - OPUS4-7570 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Banach, Ulrich A1 - Hübert, Thomas A1 - Krüger, U. T1 - Practical Applications of Electronic Noses T2 - 12th International Conference "Sensor 2005", CY - Nuremberg, Germany DA - 2005-05-10 KW - Electronic Noses KW - Sensor-Array KW - Application KW - Surveillance KW - Environment PY - 2005 VL - II SP - P5.5-211-P5.5-215 PB - AMA Service GmbH CY - Wunstorf AN - OPUS4-7574 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beck, Uwe A1 - Hertwig, Andreas A1 - Reiners, Georg T1 - Qualitätssicherung in der Oberflächen- und Schichttechnik mit optischen Verfahren T2 - Congress Industrielle Oberflächentechnik (CIO 2005) "Schichten auf Glas und Polymeren - Neue Anwendungen für Optik, Elektronik und Umwelt CY - Braunschweig, Deutschland DA - 2005-02-22 KW - Qualitätssicherung KW - Oberflächentechnik KW - Optische Verfahren PY - 2005 SP - 7-1-7-9 PB - Neue Materialien Niedersachsen CY - Göttingen AN - OPUS4-7694 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ritter, C. A1 - Heyde, M. A1 - Stegemann, Bert A1 - Rademann, K. A1 - Schwarz, U.D. T1 - Moving adsorbed particles by scanning force microscopy: A new gateway to the study of nanoscale frictional properties T2 - 3rd ESF Nanotribology Workshop CY - Sesimbra, Portugal DA - 2004-09-18 KW - Friction KW - Nanoparticle KW - Manipulation KW - Dissipation PY - 2004 SP - 34 PB - ESF CY - Sesimbra AN - OPUS4-7680 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Binder, Christian T1 - Transporteigenschaften von Thoriumnitrat in verschiedenen praxisrelevanten Lösungen und Diffusionskoeffizienten von Plutonium(IV)-Nitrat in salpetersauerer Lösung - Ein Beitrag zur Optimierung der Wiederaufarbeitung von Kernbrennstoffen KW - Kernbrennstoffe KW - Wiederaufarbeitung KW - Thoriumnitrat KW - Plutoniumnitrat KW - Diffusionskoeffizienten PY - 1984 SP - 1 EP - 152 AN - OPUS4-7631 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lüth, Peter T1 - Evaluation of the Round Robin Solid Oxidizer Test (UN O.1) 2004 / 05 T2 - OECD IGUS Meeting CY - Buxton, England, UK DA - 2005-07-15 PY - 2005 SP - 6 pages CY - Buxton AN - OPUS4-7674 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Döring, Joachim T1 - Grundlagen zur Charakterisierung von Harzsystemen und deren Verarbeitungsprozessen mittels Ultraschall T2 - IKV-Seminar "Innovative Prozessentwicklungen in der Produktion endlosfaserverstärkter Kunststoffe CY - Aachen, Deutschland DA - 2005-06-28 PY - 2005 SP - 17 Seiten PB - RWTH Aachen CY - Aachen AN - OPUS4-7624 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pfender, Max T1 - Von der Verantwortung der Wissenschaftler und Ingenieure für die Zukunft - Festvortrag auf dem 103. Schinkelfest des Architekten- und Ingenieur-Vereins zu Berlin am 13. März 1958 in der Kongreßhalle PY - 1958 VL - 10 SP - 5 EP - 20 CY - [Berlin] AN - OPUS4-7719 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Wuppermann, A. Th. A1 - Pfender, Max A1 - Amedick, Egon T1 - Untersuchung des Einflusses von Oberflächenfehlern auf die Dauerhaltbarkeit von Kurbelwellen PY - 1958 SP - 1 EP - 48 PB - Verl. Stahleisen CY - Düsseldorf AN - OPUS4-7725 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Teske, Karl T1 - Auch "schweißbare" Stähle können reißen! PY - 1958 VL - 60 IS - 3 SP - 79 EP - 80 PB - Coleman CY - Lübeck AN - OPUS4-7792 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Caemmerer, Winfrid T1 - Wärmeschutz aber richtig PY - 1958 SP - 1 EP - 40 PB - Deutsches Bauzentrum CY - Köln AN - OPUS4-7750 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Becker, Günther T1 - On some organic solvent types of timber preservatives in Germany T2 - 8th Annual Convention of the British Wood Preserving and Damp-Proofing Association CY - Cambridge, England, UK DA - 1958-07-08 PY - 1958 N1 - Serientitel: BWPA – Series title: BWPA IS - 8 SP - 123 EP - 142 CY - London AN - OPUS4-7751 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Strese, Günther T1 - Gasspürgeräte PY - 1961 N1 - Serientitel: Schriftenreihe Arbeitssicherheit – Series title: Schriftenreihe Arbeitssicherheit IS - 3 SP - 7 EP - 24 PB - Verein Deutscher Sicherheitsingenieure CY - Siegen i. W. AN - OPUS4-10140 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Becker, Günther T1 - Status of Biology and Control of Marine Borers T2 - 5th World Forestry Congress Proceedings CY - Seattle, WA, USA DA - 1960-01-01 PY - 1962 VL - 5 SP - 1(?) EP - 9(?) AN - OPUS4-10188 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Milster, Helga A1 - Meckel, Lothar T1 - Über den Nachweis von Kunstharzappreturen - 2. Mitteilung PY - 1962 VL - 17 IS - 9 SP - 485 EP - 489 PB - Zollikofer CY - St. Gallen AN - OPUS4-10209 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dittmar, Paul T1 - Raumexplosionen durch Gase, Dämpfe und Staub T2 - 14. Arbeitstagung des Bundeskriminalamtes über Brandermittlung und Brandverhütung CY - Wiesbaden, Deutschland DA - 1962-04-09 PY - 1962 N1 - Serientitel: Arbeitstagung des Bundeskriminalamtes – Series title: Arbeitstagung des Bundeskriminalamtes IS - 14 SP - 121 EP - 130 PB - Bundeskriminalamt CY - Wiesbaden AN - OPUS4-10215 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Peter, Hans A1 - Emschermann, Hans-Heinrich T1 - Bewertungsvorgänge bei Exzenterpressen und ihre Bedeutung für die Leistung von Schnittwerkzeugen PY - 1961 IS - 15 PB - Forschungsgesellschaft Blechverarbeitung CY - Düsseldorf AN - OPUS4-10157 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Peters, Hans-Jürgen T1 - Flachen-Zerknall durch Tiefkühlung PY - 1961 IS - 2 PB - Berufsgenossenschaft der Chemischen Industrie CY - Heidelberg AN - OPUS4-10151 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Petrowitz, Hans-Joachim T1 - Zur Dünnschichtchromatographie mehrkerniger aromatischer Kohlenwasserstoffe PY - 1964 SP - 132 EP - 137 PB - Elsevier CY - Amsterdam AN - OPUS4-10349 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Meckel, Lothar T1 - Bundesanstalt für Materialprüfung (BAM) - Fachgruppe 3.2 Textilien und Leder - Laboratorium 3.23 Wäschereichemische und -technische Prüfung PY - 1964 VL - 17 IS - 9 SP - 612 EP - 614 PB - Verl. Neuer Merkur CY - München AN - OPUS4-10355 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Becker, Günther T1 - Problèmes de l'emploi et de la protection du bois et des fibres sous les tropiques - Problems of use and protection of wood and fibres in the tropics T2 - Colloque International ; International Symposium CY - Abidjan, Côte d'Ivoire DA - 1963-11-24 PY - 1964 N1 - Sprachen: Englisch/Französisch - Languages: English/French IS - 24-25 SP - 4 EP - 6 AN - OPUS4-10329 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Becker, Günther T1 - Testing results on termite resistance of plastics T2 - Colloque International ; International Symposium CY - Abidjan, Côte d'Ivoire DA - 1963-11-24 PY - 1964 IS - 24-25 SP - 93 EP - 97 AN - OPUS4-10330 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Scheruhn, Willi ED - Stauch, A. ED - Rögnitz, H. T1 - Geräte zur Gasbeschaffung PY - 1964 VL - 2 SP - 524 EP - 529 PB - Ernst CY - Berlin ET - 6 AN - OPUS4-10360 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bub, Heinrich A1 - Becker, Wolfram T1 - Widerstandsfähigkeit von Baustoffen und Bauteilen gegen Feuer und Wärme - DIN 4102 (Ausgabe November 1940) und ihre Ergänzungserlasse PY - 1964 IS - 25 SP - 642 EP - 648 PB - Fachverband Bau Württemberg CY - Stuttgart AN - OPUS4-10322 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bub, Heinrich A1 - Becker, Wolfram T1 - Widerstandsfähigkeit von Baustoffen und Bauteilen gegen Feuer und Wärme - DIN 4102 (Ausgabe November 1940) und ihre Ergänzungserlasse- Fortsetzung PY - 1964 IS - 26 SP - 676 EP - 679 PB - Fachverband Bau Württemberg CY - Stuttgart AN - OPUS4-10323 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Seekamp, Horst A1 - Becker, Wolfram T1 - Erläuterung der Ergänzung zu DIN 4102 (2. Aufsatz) PY - 1964 VL - 18 IS - 40 SP - 1049 EP - 1059 PB - Fachverband Bau Württemberg CY - Stuttgart AN - OPUS4-10324 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Seekamp, Horst A1 - Becker, Wolfram A1 - Struck, Werner T1 - Brandversuche an Stahlbetonfertigsäulen PY - 1964 IS - 162 SP - 1 EP - 46 PB - Ernst CY - Berlin AN - OPUS4-10325 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfender, Max ED - Fueter, E. T1 - Aktuelle Probleme der Materialprüfung PY - 1965 SP - 723 EP - 740 PB - Verlagsaktienges. CY - Thun (Schweiz) AN - OPUS4-10396 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schönherr, Wolfgang T1 - Über die Kerbzähigkeit dünner Bleche PY - 1965 IS - 19-20 SP - 324 EP - 330 PB - Forschungsgesellschaft Blechverarbeitung CY - Düsseldorf AN - OPUS4-10458 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kirschke, Kurt T1 - Experimentelle Ergebnisse zum Normalspannungseffekt T2 - 4th International Congress on Rheology CY - Providence, RI, USA DA - 1963-08-26 PY - 1965 VL - 4 IS - Part 3 SP - 401 EP - 415 CY - London AN - OPUS4-10461 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Strese, Günther ED - Stauch, A. ED - Rögnitz, H. T1 - Gasversorgung PY - 1965 VL - 3 SP - 105 EP - 114 PB - Ernst CY - Berlin ET - 6 AN - OPUS4-10443 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Caemmerer, Winfrid T1 - Erhöhung der Wärme-Isolation verbessert die Rentabilität bei Wohn- und Bürohäusern PY - 1959 IS - 11-12 SP - 1 EP - 20 CY - Zürich AN - OPUS4-10018 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Caemmerer, Winfrid T1 - Baulischer Wärmeschutz in England, Frankreich und Holland PY - 1959 SP - 821 EP - 824 PB - Fachverband Bau Württemberg CY - Stuttgart AN - OPUS4-10019 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Buro, Andreas T1 - Wasserlösliche Holzschutzmittel - Versuche zur Steigerung der Eindringtiefe durch künstliche Erhöhung der Luftfeuchtigkeit PY - 1959 VL - 61 SP - 146 EP - 149 PB - Bruder-Verl. CY - Karlsruhe AN - OPUS4-10032 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wapler, D. T1 - Prüfungsmethoden für Anstriche und ihre praktische Bedeutung PY - 1959 IS - 9 SP - 89 EP - 96 PB - Forschungsgesellschaft Blechverarbeitung CY - Düsseldorf AN - OPUS4-10035 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Elze, Johannes T1 - Schäden an oberflächenbehandelten Blechteilen und ihre Verhütung PY - 1959 SP - 2 EP - 7 PB - Forschungsgesellschaft Blechverarbeitung CY - Düsseldorf AN - OPUS4-10007 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Melchior, Paul T1 - Masse und Kraft - Kilogramm und Kilopond PY - 1956 VL - 2-4 SP - 133-135, 140-141, 148-150 CY - Bad Godesberg AN - OPUS4-9962 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Seekamp, Horst T1 - Feuerschutz von Holz und Holzkonstruktionen PY - 1957 VL - 27 SP - 95 EP - 100 PB - Franckh CY - Stuttgart AN - OPUS4-9918 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Seekamp, Horst A1 - Möhler, Karl T1 - Feuersicherheit von Hausschornsteinen PY - 1957 VL - 27 SP - 81 EP - 89 PB - Franckh CY - Stuttgart AN - OPUS4-9922 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Seekamp, Horst T1 - Die Normung von ein- und zweiflügligen Türen für Fahrschachtzugänge von Aufzügen PY - 1957 IS - 11 SP - 89 EP - 93 PB - Fachverband Bau Württemberg CY - Stuttgart AN - OPUS4-9924 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schneider, Patrick ED - Cremer, L. T1 - Ein Beitrag zur Frage der Installationsgeräusche T2 - 3rd International Congress on Acoustics CY - Stuttgart, Deutschland DA - 1959-01-01 PY - 1961 VL - 2 SP - 1045 EP - 1049 PB - Elsevier Pub. Co CY - Amsterdam AN - OPUS4-10096 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Damaschke, Kurt T1 - Vitamin-C-Schnell-Bestimmung in Konserven PY - 1959 VL - 10 IS - 11 SP - 3427 EP - 3428 PB - Ohler CY - Coburg AN - OPUS4-10068 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Becker, Günther ED - Ray, D. L. T1 - Biological investigations on marine borers in Berlin-Dahlem T2 - 1st Friday Harbor Symposium CY - Seattle, WA, USA DA - 1957-09-01 PY - 1959 SP - 62 EP - 76 PB - Univ. of Wash. Press CY - Seattle, Wash. AN - OPUS4-10071 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Wiederholt, Wilhelm ED - Steudel, H. T1 - Korrosion und Korrosionsschutz PY - 1960 IS - II B8 SP - 1 EP - 10 PB - VDI-Verl. CY - Düsseldorf AN - OPUS4-10078 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kaesche, Helmut T1 - Untersuchungen über die Korrosionshemmung durch Adsorptionsinhibitoren T2 - [1.] Symposium Européen sur les Inhibiteurs de Corrosion : Xème Manifestation de la Fédération Européenne de la Corrosion CY - Ferrara, Italien DA - 1960-09-28 PY - 1961 N1 - Serientitel: Manifestation de la Fédération Européenne de la Corrosion – Series title: Manifestation de la Fédération Européenne de la Corrosion IS - 10 SP - 137 EP - 160 PB - Università CY - Ferrara AN - OPUS4-10082 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mendrzyk, Hildegard T1 - Die Bestimmung des Trockengehaltes von Kammgarnen durch Austrocknen im Heißluftstrom PY - 1961 VL - 10 CY - Aachen ET - 10. AN - OPUS4-10125 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Meckel, Lothar A1 - Milster, Helga T1 - Über den Nachweis von Kunstharz-Appreturen PY - 1961 VL - 16 IS - 9 SP - 593 EP - 603 PB - Zollikofer CY - St. Gallen AN - OPUS4-10129 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfender, Max T1 - Zur Problematik der Wissenschaftsförderung PY - 1964 IS - 18 SP - 1 EP - 27 PB - Stahlbau-Verl. CY - Köln AN - OPUS4-10299 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Gert A1 - Göklü, S. T1 - Resistance Spot Welding of Advanced High Strength Steels - Influence of Welding Parameters and Electrode Cap Type T2 - International Conference of IIW CY - Prague, Czech Republic DA - 2005-07-14 KW - Resistance spot welding KW - Advanced high-strength steels (AHSS) PY - 2005 SP - 22 pages PB - IIW CY - Prag AN - OPUS4-10302 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Feuerberg, Hubert T1 - Neuere Ergebnisse der Pyrolysen-Gaschromatographie organischer Polymere T2 - 36. Congrès international de chimie industrielle CY - Liege, Belgien DA - 1966-09-10 PY - 1966 VL - 1 SP - 140 CY - Bruxelles AN - OPUS4-10580 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Urs A1 - Kanan, M.I.C. ED - Cincotto. M., ED - Da Silva, D. ED - de Oliveira, J. T1 - The Micro Structure of Traditional Brazilian Lime Plasters - The Custom House of Florianopolis T2 - VI Simpósio Brasileiro de Tecnologia de Argamassas / I International Symposium on Mortars Technology CY - Florianopolis, Brazil DA - 2005-05-23 KW - Shell lime KW - Micro structure KW - Custom House KW - Plaster PY - 2005 SP - 736 EP - 745 PB - UFSC-Universidade Federal de Santa Catarina CY - Santa Catarina AN - OPUS4-10560 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Terstiege, Heinz ED - Richter, M. T1 - Der Einfluß von Sehstoff-Konzentrationsänderungen auf Farbgleichungen T2 - Internationale Farbtagung CY - Luzern, Schweiz DA - 1965-06-01 PY - 1965 VL - 1 SP - 141 EP - 153 PB - Musterschmidt CY - Göttingen AN - OPUS4-10554 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Caemmerer, Winfrid ED - Hopkinson, R. ED - Longmore, J. T1 - Testing of sunbreaks in Germany T2 - Proceedings of the C.I.E. (Commission Internationale de l'Éclairage) Intersessional Conference CY - Newcastle-upon-Tyne, England, UK DA - 1965-04-05 PY - 1967 IS - Paper 16 SP - 211 EP - 216 PB - Bouwcentrum International CY - Rotterdam AN - OPUS4-10568 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Meckel, Lothar A1 - Milster, Helga A1 - Grünewald, G. T1 - Aufhellung synthetischer Chemiefasergewebe durch Haushaltswaschmittel PY - 1967 VL - 20 IS - 10 SP - 568,570,572 PB - Verl. Neuer Merkur CY - München AN - OPUS4-10576 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfender, Max T1 - Prüfmaschinen und Geräte aus der Sicht der Stoffprüfung N2 - Eine auf den Werkstoff und seine Umwelteinflüsse bezogene Festigkeitsforschung muß auf Vorgänge im elastischen und im überelastischen Beanspruchungsbereich in gleicher Weise bezogen sein. Merkformeln für mechanische Untersuchungen, Parameterwahl und mögliche Zusammenhänge erleichtern die jeweilige Problemstellung, die Kombination entsprechender Untersuchungsverfahren und die Auswahl oder die Entwicklung geeigneter Prüf-, Registrier- und Auswertgeräte. Beispiele aus der mechanischen Werkstoffprüfung lassen Vorstellungen ableiten über die Vielfalt und die unterschiedlichen Leistungen solcher Untersuchungseinrichtungen. Vor allem interessieren dabei die Beziehungen zwischen der Formänderung und dem Formänderungswiderstand von Proben aus Stoffen und Gemengen und von Konstruktionen bei ein- und mehrachsiger, elastischer und überelastischer, bei zügiger, ruhender, schwingender und stoßförmiger Beanspruchung bis zum Versagen durch unzulässig große Gestaltänderungen, durch Erschöpfen des Formänderungsvermögens, durch Zerrütten der Werkstoffestigkeit oder durch spröden Bruch. Daraus folgt, daß umfangreiche Stoff- und Materialdaten als Grundlage für die zuverlässige und erfolgreiche Prüfung von Werkstoffen und daraus meist im Verbund hergestellten Konstruktionen verfügbar sein sollten. Dafür wiederum ist erforderlich die Beschreibung der Werkstoffe selbst, der für ihr Festigkeitsverhalten typischen Beanspruchungen von zusätzlich einwirkenden Variablen und von Parametern einschließlich der Besonderheiten langer Einwirkungsdauer. Mit dem Denken in solchen Zusammenhängen können grundsätzliche Folgerungen für die Beurteilung und für die Entwicklung von Prüfmaschinen und Geräten gewonnen werden. T2 - RILEM-Kolloquium "Die Entwicklung der Prüfmaschinen für die mechanische Werkstoffprüfung im Bauwesen" CY - Stuttgart, Germany DA - 25.03.1968 PY - 1968 IS - Thema 4 SP - 1 EP - 19 PB - RILEM, International Union of Testing and Research Laboratories for Materials and Structures CY - Paris AN - OPUS4-10622 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schickert, Gerald T1 - Beeinflussung der Prüfergebnisse von Betonprüfungen durch Belastungsgeschwindigkeit und Ebenflächigkeit der Druckflächen T2 - RILEM-Symposium CY - Stuttgart, Deutschland DA - 1968-03-25 PY - 1968 IS - Topic 4 SP - D1 EP - D18 CY - Stuttgart AN - OPUS4-10633 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Struck, Werner T1 - Aufbauten für Prüfanlagen im Baukastensystem zur Untersuchung von Bauteilen unter zügiger Belastung T2 - RILEM-Symposium CY - Stuttgart, Deutschland DA - 1968-03-25 PY - 1968 IS - Topic 3 SP - C1 EP - C24 CY - Stuttgart AN - OPUS4-10634 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Meckel, Lothar A1 - Milster, Helga T1 - Einfluß der Wasch- und Chemischreinigungsbehandlung auf verschiedenartige Webdecken PY - 1968 VL - 21 IS - 4 SP - 149 EP - 155 PB - Verl. Neuer Merkur CY - München AN - OPUS4-10641 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pastuska, Gerhard A1 - Krüger, Renate T1 - Neue Entwicklungen bei der Dünnschicht-Elektrophorese T2 - 4th International Symposium CY - Brussels, Belgium DA - 1966-09-12 PY - 1968 SP - 180 EP - 186 PB - Presses Académiques Européennes CY - Bruxelles AN - OPUS4-10643 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Treumann, Hartwig T1 - Ermittlung der Wirkung thermisch gezündeter pyrotechnischer Sätze und Gegenstände auf Herstellungs- und Lagergebäude einer pyrotechnischen Fabrik T2 - Journées d'Études sur les Substances Instables CY - Brüssel, Belgien DA - 1967-05-08 PY - 1967 SP - 1 EP - 4 CY - Bruxelles AN - OPUS4-10587 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Strese, Günther T1 - Zündmöglichkeit von brennbaren Gasen und Dämpfen durch glimmenden Tabak PY - 1968 IS - 10 SP - 1 EP - 22 PB - Arbeitsgemeinschaft für Feuerschutz (AGF) CY - Berlin AN - OPUS4-10661 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfender, Max T1 - Warum Wissenschaft? T2 - Die technisch-wissenschaftlichen Vorträge CY - Berlin, Deutschland DA - 1968-01-01 PY - 1968 SP - 1 EP - 6 PB - Dt. Industrieausstellung CY - Berlin AN - OPUS4-10712 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Groß, Dieter T1 - Quantitative infrarotspektroskopische Analyse von Styrol-Acrylnitrit-Copolymeren nach pyrolytischer Zersetzung PY - 1969 VL - 248 SP - 40 EP - 41 CY - Wiesbaden AN - OPUS4-10752 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Strogies, Wolfgang A1 - Tengicki, H. A1 - Vogel, L. A1 - Waldschmidt, H. A1 - Wittke, K. T1 - Auswertung von Massenspektren mit Hilfe des Elektronenrechners ZUSE Z 23 V. PY - 1969 VL - 245 SP - 76 EP - 80 CY - Wiesbaden AN - OPUS4-10720 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ladeburg, H. ED - Korogiannakis, P. T1 - Korrosionsverhalten von ungeschütztem Stahl in Hafenwässern des deutschen Küstengebietes T2 - 2. Internationaler Kongress für Meerwasserkorrosion und Bewuchs CY - Athen, Griechenland DA - 1968-09-20 PY - 1969 SP - 1 EP - 7 PB - Chambre Technique de Grèce CY - Athènes AN - OPUS4-10734 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ladeburg, H. ED - Abel, H. T1 - Untersuchung und Konservierung der Eisenteile der Bremer Kogge PY - 1969 IS - 8 SP - 157 EP - 168 PB - Röver CY - Bremen AN - OPUS4-10735 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Caemmerer, Winfrid T1 - Die Energiedurchlässigkeit von Fenstern und ihr Einfluß auf das Klima von Innenräumen T2 - 19. Kongreß für Heizung, Lüftung und Klimatechnik CY - Frankfurt am Main, Deutschland DA - 1969-03-26 PY - 1969 SP - 2 EP - 16 CY - Frankfurt am Main AN - OPUS4-10736 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Petrowitz, Hans-Joachim T1 - Der Einfluss von Alkyl- und Halogen-Substituenten bei der Dünnschichtchromatographie T2 - 4th International Symposium CY - Brussels, Belgium DA - 1966-09-12 PY - 1968 SP - 187 EP - 193 PB - Presses Académiques Européennes CY - Bruxelles AN - OPUS4-10677 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burmester, Arno T1 - Aussichten der Produktion und Verwendung von Polymerholz in Europa PY - 1968 VL - 10 IS - 2 SP - 79 EP - 82 PB - Thiemig CY - München AN - OPUS4-10684 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Deppe, Hans-Joachim T1 - Einsatz von Holzspanplatten im Fußbodenbau PY - 1968 VL - 17 IS - 8 SP - 161 EP - 164 PB - Bauverl. CY - Wiesbaden AN - OPUS4-10689 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Deppe, Hans-Joachim T1 - Flachsschäbenplatten im Bauwesen PY - 1968 VL - 22 IS - 45 SP - 1179 EP - 1181 PB - Fachverband Bau Württemberg CY - Stuttgart AN - OPUS4-10690 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nehls, Irene A1 - Becker, Roland A1 - Buge, Hans-Gerhard T1 - Pentachlorphenol - Eine Altlast im Holz PY - 2005 UR - http://archiv.aktuelle-wochenschau.de/2005/woche19/woche19.html IS - 19 SP - 1 EP - 2 PB - Gesellschaft Deutscher Chemiker CY - Frankfurt am Main AN - OPUS4-10845 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmitt, B. F. T1 - Prüfung der Dekontaminierbarkeit von Anstrichen - Testing the ease of decontamination of coatings PY - 1969 VL - 11 IS - 7 SP - 397 EP - 402 PB - Thiemig CY - München AN - OPUS4-10810 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kirschke, Kurt A1 - Rösener, W. T1 - Documentation in the Field of Rheology T2 - 5th International Congress on Rheology CY - Kyoto, Japan DA - 1968-10-07 PY - 1969 VL - 5 IS - 1 SP - 391 EP - 396 CY - London AN - OPUS4-10792 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Becker, Günther T1 - Termites as Laboratory Insects T2 - 19th Annual Convention of the British Wood Preserving and Damp-Proofing Association CY - Cambridge, England, UK DA - 1969-06-24 PY - 1969 N1 - Serientitel: BWPA – Series title: BWPA IS - 19 SP - 1 EP - 14 CY - London AN - OPUS4-10768 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Becker, Günther ED - Walters, A. ED - Elphick, J. T1 - Protection of timber - an introduction into some problems T2 - 1st International Biodeterioration Symposium CY - Southampton, England, UK DA - 1968-09-09 PY - 1968 SP - 205 EP - 222 PB - Elsevier CY - Amsterdam AN - OPUS4-10771 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübert, Thomas A1 - Banach, Ulrich T1 - Testing and Calibration of Hydrogen Sensors T2 - 1st IEF Workshop - H2 concentration measurements Techniques, areas of application, limitations CY - Pfinztal, Germany DA - 2005-06-05 KW - Sensors KW - Hydrogen KW - Calibration KW - Testing PY - 2005 SP - 32 pages PB - Forschungszentrum Jülich CY - Jülich AN - OPUS4-10896 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Friedrich, Jörg Florian T1 - Kunststoffkorrosion durch Polymerabbau - Früherkennung und zeitraffende Prognose T2 - 1. Thüringer Grenz- und Oberflächentage CY - Jena, Deutschland DA - 2005-09-15 PY - 2005 SP - 33 EP - 50 PB - Innovent CY - Jena AN - OPUS4-10899 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Döring, Joachim A1 - Stark, Wolfgang A1 - Bartusch, Jürgen A1 - Mc Hugh, Jarlath T1 - Contribution to ultrasound cure control for composite manufacturing N2 - The curing conditions play an important role in the quality assurance of composite products. Especially as composite materials are widely used in high tech areas so that they are required to fulfil high quality Standards. Some problems which occur during curing, for instance undercuring, can hardly be detected using Standard NDT investigations, mainly because they are manifested only at high temperatures, particularly close to glass-rubber-transition. On-line eure monitoring has the outstanding advantage that it can monitor the material parameters even at the highest temperatures possible. In recent years eure monitoring with ultrasonic methods has become more populär. In comparison to dielectric methods mechanical parameters are measured directly. The quantities to be measured are the velocity and the attenuation of the sound wave. On this basis the storage and loss modulus can be calculated. Depending on the form of excitation with longitudinal or transversal waves these moduli are referred to as long wave or shear modulus. Well developed Computer based technology and sensor materials are available in the non-destructive testing (NDT) market. The measuring equipment employed a commercial NDT System, which worked computer-aided. With a special Software the demands of automatic Operation under industrial conditions was accomplished. This measurement equipment was tested on composites. Its structure, performance and some practical results will be presented in the following paper. T2 - 15th World Conference on Non-Destructive Testing (WCNDT) CY - Roma, Italy DA - 15.10.2000 PY - 2000 UR - http://www.ndt.net/article/wcndt00/papers/idn482/idn482.htm SN - 1435-4934 VL - 5 IS - 11 PB - NDT.net CY - Kirchwald AN - OPUS4-2136 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Ralph-Peter A1 - Much, Helmut A1 - Schulz, Günter T1 - New Results of Determination of Polymer Heterogeneity by Two-Dimensional Orthogonal Liquid Chromatography T2 - International GPC Symposium CY - Lake Buena Vista, FL, USA DA - 1994-06-05 PY - 1994 SP - 273 EP - 275 PB - Gordon and Breach CY - St. Helier, Jersey AN - OPUS4-2140 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Daum, Werner T1 - Standardised and Particular Methods for Reliability Testing of Polymer Optical Fibres T2 - 2nd Asia-Pacific Polymer Fibre Optics Workshop CY - Hong Kong, China DA - 2003-01-03 PY - 2003 SP - 15 EP - 20 CY - Hong Kong AN - OPUS4-2141 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Döring, Joachim A1 - Bartusch, Jürgen A1 - Mc Hugh, Jarlath A1 - Stark, Wolfgang A1 - Kürten, C. T1 - Mit Ultraschall sieht man mehr - Kontrolle von Werkzeugfüllung und Vernetzungsreaktion beim Harzinjektionsverfahren RTM T2 - Poster-Ausstellung "Sensorik in der BAM" CY - Berlin, BAM, Deutschland DA - 2002-10-01 PY - 2002 SP - 1(?) AN - OPUS4-2114 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Grunewald, Thomas T1 - Die Zündquelle "mechanisch erzeugte Funken" PY - 2003 VL - 3 SP - 102 EP - 122 PB - Schäfer CY - Detmold AN - OPUS4-2119 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Unger, Wolfgang A1 - Gross, Thomas T1 - XPS/ESCA - Ringversuchsergebnisse T2 - Seminar Oberflächenanalytik "Technische Aspekte der Akkreditierung nach ISO/IEC 17025" CY - Berlin, Deutschland DA - 2003-01-24 PY - 2003 SP - 1 EP - 3 AN - OPUS4-2120 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Martin A1 - Krause, Ulrich A1 - Lohrer, Christian T1 - Der Einfluss des Sauerstoffgehaltes auf das Selbstzündungsverhalten von Staubschüttungen T2 - 6. Fachtagung Anlagen-, Arbeits- und Umweltsicherheit CY - Köthen, Deutschland DA - 2002-11-07 PY - 2002 VL - 6 IS - Abschnitt P04 SP - 1(?) EP - 5(?) PB - GVC CY - Düsseldorf AN - OPUS4-2121 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Janiak, Ch. A1 - Lange, K.C.H. A1 - Marquardt, P. A1 - Krüger, Ralph-Peter A1 - Hanselmann, R. ED - Sun, J. ED - Janiak, C. T1 - Propene and 1-hexene oligomerization with unbridged alkyl-substituted cyclopentadienyl- and phospholyl-zirconium/MAO catalysts - mechanistic implications from oligomer analyses by NMR, SEC, and MALDI-TOF MS PY - 2001 SP - 117 EP - 142 PB - Chemical Industry Press CY - Bejing AN - OPUS4-2193 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Ralph-Peter A1 - Much, Helmut A1 - Schulz, Günter ED - Günther, W. T1 - Strukturaufklärung von heterogenen Polymeren durch zweidimensionale Flüssigchromatographie und MALDI-TOF-Massenspektrometrie T2 - InCom '94 - International Symposium on Instrumentalized Analytical Chemistry and Computer Technology CY - Düsseldorf, Deutschland DA - 1994-03-14 PY - 1994 VL - 94 PB - InCom-Bureau CY - Düsseldorf AN - OPUS4-2195 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Ralph-Peter A1 - Much, Helmut A1 - Schulz, Günter T1 - Polymer Characterization by Two-Dimensional HPLC and MALDI-TOF-MS T2 - 7th International Symposium on Polymer Analysis and Characterization (ISPAC) CY - Les Diablerets, Switzerland DA - 1994-05-24 PY - 1994 PB - Gordon and Breach CY - St. Helier, Jersey AN - OPUS4-2196 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sonnenschein, Helmut A1 - Kreher, Th. A1 - Krüger, Ralph-Peter A1 - Ahlers, B. T1 - Synthesis of brigded indolizines-starting materials for molecular tweezers T2 - XVI th European Colloquium on Heterocyclic Chemistry CY - Bled, Slovenia DA - 1994-09-25 PY - 1994 CY - Bled, Slovenia AN - OPUS4-2198 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reinhardt, M. A1 - Krüger, Ralph-Peter A1 - v. Lampe, I. A1 - Lorkowski, H.-J. T1 - Über Lösekinetik und Acidität einiger phenolischer Polymere T2 - 5. Berliner Polymertage 1994 CY - Potsdam DA - 1994-10-05 PY - 1994 CY - Potsdam AN - OPUS4-2199 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz, Günter A1 - Krüger, Ralph-Peter A1 - Much, Helmut ED - Günther, W. T1 - Polymercharakterisierung durch MALDI-TOF-MS und Kopplung mit der HPLC T2 - InCom '95 - International Symposium on Instrumentalized Analytical Chemistry and Computer Technology CY - Düsseldorf, Germany DA - 1995-03-20 PY - 1995 CY - Moers AN - OPUS4-2201 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wachsen, O. A1 - Krüger, Ralph-Peter A1 - Much, Helmut A1 - Schulz, Günter A1 - Reichert, K.H. T1 - Untersuchungen zur Charakterisierung des Abbaus von Polylactiden mittels 2D-HPLC und MALDI-TOF-MS T2 - Sitznung des Berliner Verband für Polymerforschung e.V. CY - Berlin DA - 1995-05-18 PY - 1995 CY - Berlin AN - OPUS4-2202 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Much, Helmut A1 - Krüger, Ralph-Peter A1 - Schulz, Günter T1 - Investigation of Macromer Heterogeneity by Two-Dimensional HPLC and MALDI-TOF-MS T2 - 19th International Symposium on Column Liquid Chromatography CY - Innsbruck, Austria DA - 1995-05-28 PY - 1995 CY - Innsbruck AN - OPUS4-2204 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maier, B. A1 - Trathnigg, B. A1 - Much, Helmut A1 - Krüger, Ralph-Peter A1 - Berek, D. T1 - Characterization of polyethers using different chromatographic techniques and MALDI-TOF-MS PY - 1995 CY - Innsbruck AN - OPUS4-2205 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Ralph-Peter A1 - Much, Helmut A1 - Reichert, K.H. A1 - Schulz, Günter A1 - Wachsen, O. T1 - Untersuchungen zur Charakterisierung des Polylactidabbaus mittels HPLC und MALDI-TOF-MS T2 - Präsentationsveranstaltung des Instituts für Angewandte Chemie Berlin-Adlershof e.V. CY - Berlin, Germany DA - 1995-09-26 PY - 1995 CY - Berlin AN - OPUS4-2206 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Ralph-Peter A1 - Much, Helmut A1 - Schulz, Günter T1 - Investigation of Macromer Heterogeneity by 2D-HPLC and MALDI-TOF-MS T2 - Präsentationsveranstaltung des Instituts für Angewandte Chemie Berlin-Adlershof e.V. CY - Berlin, Germany DA - 1995-09-26 PY - 1995 CY - Berlin AN - OPUS4-2207 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Flatau, S. A1 - Much, Helmut A1 - Schulz, Günter T1 - Hochleistungsflüssigchromatographie T2 - Statusseminar des ACA CY - Berlin, Deutschland DA - 1996-11-05 PY - 1996 AN - OPUS4-2210 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Goering, Harald A1 - Krüger, Ralph-Peter A1 - Joel, D. T1 - Erfassung und Charakterisierung von Hartsegmenten in Polyurethanen mittels MALDI-TOF-MS T2 - Gesellschaft Deutscher Chemiker, "Klassische Polymere im Aufwind, Polymerchemie aktuell" CY - Dresden, Deutschland DA - 1996-03-25 PY - 1996 CY - Dresden AN - OPUS4-2211 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kautek, Wolfgang T1 - Fs-laser interaction with hard and soft materials - fundamentals and applications T2 - 1st European Conference on Applications of Femtosecond Lasers in Materials Science ; FemtoMat 2002 CY - Visegrád, Hungary DA - 2002-10-24 PY - 2002 AN - OPUS4-2647 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Müller, Karsten T1 - Modern Safety Assessment of Cubic Cast Iron Containers Under Mechanical Impact N2 - In the present study, ductile cast iron from an original DCI container with a wide variety of microstructure was investigated in order to determine the materials fracture toughness under impact loading conditions. Three-point bending specimens with thickness of 140 mm from a cubic DCI container were investigated at elevated loading rates to provide reliable fracture toughness parameters for the assessment procedures. In contrast to static fracture behaviour, the fracture toughness values of thick-walled DCI at higher loading rates show a remarkable reduction with decreasing temperature up to –50 °C and a significant shift of the transition range. The lower bound fracture toughness value used in the BAM DCI safety concept was confirmed for impact loading conditions by these fracture mechanics tests using large specimens. These measurements are relevant to the licensing tests for storage containers without shock absorbers, especially to the assessment of the dynamic behaviour of crack-like defects inside a cask structure under drop test conditions. Using extensive dynamic numerical analyses it could be shown, that for special crack configurations the dynamic crack tip parameter (KI, or J) may be estimated by static formulae even under mechanical impact. These results of the safety assessment were verified according to the German Konrad repository acceptance criteria by a drop test with a cubic waste container with artificial crack-like defects from 5 m height onto a representative storage facility foundation. T2 - 17th International Conference on Structural Mechanics in Reactor Technology ; SMiRT 17 CY - Prague, Czech Republic DA - 2003-08-17 KW - Ductile cast iron KW - Mechanical impact KW - Dynamic fracture KW - Safety assessment KW - Storage containers PY - 2003 IS - G04-4 SP - 1(?) EP - 8(?) CY - Prague AN - OPUS4-2650 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bremser, Wolfram A1 - Hässelbarth, Werner A1 - Hirlehei, U. A1 - Hotze, H.-J. A1 - Mickan, B. A1 - Kramer, R. A1 - Dopheide, D. T1 - Uncertainty Analysis and Long-Term Stability Investigation of the German Primary High Pressure Natural Gas Test Facility pigsar T2 - 11th FLOMEKO CY - Groningen, The Netherlands DA - 2003-05-12 PY - 2003 CY - [Groningen] AN - OPUS4-2653 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erning, Johann Wilhelm A1 - Klein, Ulrich T1 - Korrosion von kupfergelöteten Plattenwärmeübertragern - die Folgen T2 - 29. VDI-Jahrestagung "Schadensanalyse, Korrosionsschäden in der Industrie" CY - Würzburg, Deutschland DA - 2003-10-16 KW - Plattenwärmeübertrager KW - Schadensuntersuchung KW - Kupfer PY - 2003 SP - 1(?) EP - 11(?) AN - OPUS4-2642 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bremser, Wolfram A1 - Hässelbarth, Werner T1 - Calibration issues re-visited T2 - Joint BIPM-NPL Workshop on the Impact of Information Technology in Metrology CY - Teddington, England, UK DA - 2002-09-16 PY - 2003 SP - 1 EP - 7(?) AN - OPUS4-2625 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ecker, Klaus A1 - Dudzus, Thomas A1 - Merchel, Silke A1 - Kipphardt, Heinrich ED - Vízkelethy, G. T1 - Oxygen determination in BaF2 and CaF2 by Charged Particle Activation Analysis T2 - 16th International Conference on Ion Beam Analysis (IBA-16) CY - Albuquerque, NM, USA DA - 2003-06-29 PY - 2004 VL - 219-220 SP - P2 EP - 113 PB - Elsevier CY - Amsterdam AN - OPUS4-2627 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - von Oertzen, Alexander A1 - Myatt, S. A1 - Chapman, D. A1 - Webb, R. A1 - v. Rooijen, M. P. A1 - Colpa, W. A1 - de Jong, E.G. A1 - de Ruiter, J. T1 - CHAF Workpackage 4 Report - Literature review of fireworks compositions, propagation mechanisms, storage legislation and environmental effects N2 - This report is a literature review of the current state of knowledge of fireworks and fireworks hazards. It presents work to meet Deliverables D4-1 (types and compositions of fireworks Articles), D4-2 (Functioning mechanism of and between fireworks articles), D4-3 (Storage and transport regulations in EU countries) and D4-4 (The effect of fireworks on health and the environment) of the CHAF work program. Firework compositions are discussed in the first section. This leads to an understanding of the variability in performance of various types of fireworks. Compositions used in report effects are highlighted as being the most energetic while other compositions are seen as providing a much lesser hazard in mass storage of fireworks. Individual types of firework are examined. Large devices such as report shells are identified as posing the largest hazard in bulk storage. Lesser, but still significant, hazards are predicted for similar compositions in Roman candles and rockets. Gradations in hazard are identified corresponding to UN hazard divisions 1.1, 1.3 and 1.4. The second section reports the literature relating to the functioning mechanism of and between fireworks articles. In this the major propagation mechanisms for fireworks compositions are examined. The main stimuli identified are: fragment impact, heat and shock wave, each of which can lead to the functioning of pyrotechnic composition in the article or in an adjacent article leading to large-scale initiation. Consideration of the pyrotechnic compositions leads to a different ranking for the three mechanisms with different fireworks types. Thus with a report composition containing a metal/perchlorate mixture shock initiation is seen to be the main propagation mechanism. Such a mechanism is likely to afford a mass explosion. At a lesser hazard, blackpowder-based compositions are reported to be more likely to propagate via a flame mechanism. This is less likely to produce a mass explosion. National legislation concerning the storage of fireworks for many European countries is considered in the third section. Many of the national regulations are based on a cube root of explosives content to determine "safety distances", often written as Q1/3. Different multiplying factors are then applied depending on the type of adjacent site (production buildings, residential housing, roads etc.). Commonly 22Q1/3 is used for residential dwellings. Special provisions are enacted in many countries either to allow lesser distances or in some cases to increase the safety distances depending on the perceived hazard or extenuating circumstances. The final section deals with the environmental hazards posed by the use of fireworks. Toxic effects of the materials used in the manufacture and the likely reaction products from functioning fireworks are highlighted. These range from heavy metal poisoning from metals present for their colour effect to respiratory problems due to pyrotechnic fume (both particulate and gaseous). Finally, noise pollution is considered. While there is a short term problem from pyrotechnic fume at times of high usage (national celebrations) there is no literature evidence, as yet, of long term detriment to the environment. PY - 2003 UR - http://www.pyrobin.com/files/european%20firework%20testing%20reports,%20bam%20etc.pdf IS - EVG1-CT-2002-00074 CHAF SP - 1 EP - 104 PB - HSE - Health and Safety Executive CY - Sheffield, UK AN - OPUS4-2594 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Levkovitch, Vladislav A1 - Sievert, Rainer A1 - Svendsen, B. T1 - Life Analysis of a fcc Single Crystal and Simulation of Crack Propagation by Blunting and Re-Sharpening T2 - International Conference on Computational and Experimental Engineering and Science 2003 (ICCES '03) CY - Corfu, Greece DA - 2003-07-25 PY - 2003 CY - Tokyo AN - OPUS4-2619 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kurschat, T. A1 - Brandt, O. A1 - Bremser, Wolfram A1 - Hässelbarth, Werner T1 - Analysis of the traceability chain and calculation of uncertainty of a high-pressure test facility for flow rate measurements T2 - 4th International Symposium on Fluid Flow Measurement CY - Denver, CO, USA DA - 1999-06-27 PY - 1999 SP - 1 EP - 12 CY - Denver, Colo. AN - OPUS4-2575 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kley, Gerd A1 - Köcher, Peter A1 - Brenneis, Rudolf T1 - Phosphordüngemittel aus Klärschlammasche PY - 2003 VL - 2 SP - 8 CY - Zürich AN - OPUS4-2578 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - von Oertzen, Alexander A1 - Myatt, S. A1 - de Jong, E. T1 - CHAF Workpackage 6 Report - Instrumented benchmarking - Containing Deliverable D6-1, Selection and purchase of fireworks articles N2 - This is the first part (Deliverable 6-1) of workpackage 6 (WP6) in the framework of a research project funded by the European Community on the "Quantification and control of the hazards associated with the transport and bulk storage of fireworks" which was given the acronym CHAF. The work in this package aims to characterize selected packaged fireworks in standard UN classification tests by measuring the physical conditions (temperature, pressure, radiation, etc.), acting during testing and to use the results to provide benchmark data for the rest of the CHAF project. The objective of Deliverable 6-1 was to identify the types of fireworks that should be used for the benchmarking tests. This was achieved by developing the information generated in the literature review for the project (WP4). A critical element of the work was to attempt to identify fireworks close to the boundaries between different UN Hazard Divisions so that the accuracy of the UN classification assignments, as applied to fireworks, could be tested. This document outlines the types of fireworks selected for benchmark testing and the rationale behind the selection. Having identified the fireworks required a way forward to identify suitable suppliers is given. PY - 2003 UR - http://www.docstoc.com/docs/2923791/CHAF-Workpackage-report-CHAF-Workpackage-Report-Workpackage-leader-A-von IS - EVG1-CT-2002-00074 CHAF SP - 1 EP - 9 PB - HSE - Health and Safety Executive CY - Sheffield, UK AN - OPUS4-2584 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meyer-Plath, Asmus A1 - Mix, Renate A1 - Kühn, Gerhard A1 - Friedrich, Jörg Florian ED - d'Agostino, R. T1 - The Potential of Surface Radicals for Polymer Functionalization T2 - 16th International Symposium on Plasma Chemistry (ISPC-16) CY - Taormina, Italy DA - 2003-06-22 PY - 2003 IS - CD-ROM PB - Dep. of Chemistry, Univ. CY - Bari AN - OPUS4-2612 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Finke, B. A1 - Meyer-Plath, Asmus A1 - Schröder, K. A1 - Ohl, A. ED - d'Agostino, R. T1 - Analysis of plasma-generated radicals on polymer surfaces N2 - Plasma functionalisation in gas phase like ammonia allows to equip polymer surfaces with amino functional groups. An important question of this functionalisation consists in the limited knowledge about heterogeneous interface reactions, especially radical formation and subsequent reaction processes. Useful analytical methods comparable to those avilable for gas phase reactions are scarce. Here we report on investigations on plasma generated C-radicals by NO-labelling, showing similatr effects for different plasmas. T2 - 16th International Symposium on Plasma Chemistry (ISPC-16) CY - Taormina, Italy DA - 2003-06-22 PY - 2003 IS - CD-ROM SP - 1 EP - 6(?) PB - Dep. of Chemistry, Univ. CY - Bari AN - OPUS4-2613 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, K. A1 - Ihrke, R. A1 - Meyer-Plath, Asmus A1 - Finke, B. A1 - Diener, A. A1 - Nebe, B. A1 - Ohl, A. ED - d'Agostino, R. T1 - Surface functionalization in ammonia microwave plasmas for biomedical applications T2 - 16th International Symposium on Plasma Chemistry (ISPC-16) CY - Taormina, Italy DA - 2003-06-22 PY - 2003 IS - CD-ROM PB - Dep. of Chemistry, Univ. CY - Bari AN - OPUS4-2614 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wachtendorf, Volker A1 - Schulz, Ulrich T1 - Shortening of Weathering Tests for Automotive Coatings by Chemiluminescence Detection T2 - 27th FATIPEC Congress CY - Aix-en-Provence, France DA - 2004-04-19 KW - Chemiluminescence KW - Artificial weathering KW - ADF KW - Automotive coatings KW - Chemilumineszenz KW - Künstliche Bewitterung KW - Automobillacke PY - 2004 VL - 3 SP - 931 EP - 940 PB - Association Francaise des Techniciens des Peintures, Vernis,Encres CY - Aix en Provence AN - OPUS4-3561 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kley, Gerd A1 - Köcher, Peter A1 - Brenneis, Rudolf A1 - Peplinski, Burkhard T1 - Möglichkeiten der Nutzbarmachung von Phosphat aus Klärschlammaschen durch thermochemische Behandlung - Ergebnisse experimenteller Untersuchungen T2 - VDI-Seminar 43-36-25, Klärschlamm / Tiermehl / Altholz / Biogene Abfälle CY - München, Deutschland DA - 2004-02-12 KW - Klärschlammaschen KW - Verwertung KW - Schadstoffabtrennung KW - Schwermetalle KW - Thermochemische Behandlung KW - Drehrohrofen KW - Phosphat-Düngemittel PY - 2004 SP - 1 EP - 22 PB - VDI-Verl. CY - Düsseldorf AN - OPUS4-3564 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Steckert, Carsten T1 - Digital Image Analysis for Colorimetric Surface Inspection of Paint Coatings Stressed by Materials Testing T2 - Second European Conference on Color in Graphics, Imaging and Vision and Sixth International Symposium on Multispectral Color Science (CGIV 2004) CY - Aachen, Deutschland DA - 2004-04-05 PY - 2004 SP - 484 EP - 488 CY - Aachen AN - OPUS4-3488 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gross, U. A1 - Müller-Mai, C. A1 - Knabe, C. A1 - Berger, Georg A1 - Ploska, Ute A1 - Gildenhaar, Renate ED - Vincenzini, P. T1 - Animal experiments with biomaterials for direct bone contact displaying higher or lower solubility in comparison to TCP and HA products T2 - 10th International Ceramics Congress ; 3rd Forum on New Materials ; 10th CIMTEC 2002 CY - Florence, Italy DA - 2002-07-14 PY - 2004 SP - 369 EP - 376 PB - Techna CY - Faenza AN - OPUS4-3500 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Erhard, Anton A1 - Munikoti, Vijayendra K. A1 - Brekow, Gerhard A1 - Tessaro, Ute A1 - Tscharntke, Dirk T1 - Modelling for the improvement of dissimilar weld inspection T2 - 16th World Conference on Nondestructive Testing CY - Montreal, Canada DA - 2004-08-30 PY - 2004 SP - 1 EP - 8(?) PB - International Committee for Non-Destructive Testing CY - Montreal AN - OPUS4-3518 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Burkert, Andreas A1 - Isecke, Bernd T1 - Edelstahl Rostfrei in Kontakt mit anderen Werkstoffen N2 - Einleitung; Grundlagen der Bimetallkorrosion (Kontaktkorrosion); Einflussgrößen und Beispiele: Elektrolytwiderstand, Befeuchtungsdauer/Umgebung, Kinetik der Elektrodenreaktionen, Flächenverhältnis Kathode/Anode; Praktische Erfharungen in verschiedenen Anwendungsbereichen: Wasser- und Abwassertechnik, Bauteile an der Atmosphäre, Bauwesen, Fahrzeugbau; Häufige gestellte Fragen; Vermeidung von Bimetallkorrosion; Literatur T2 - Fachtagung "Verbindungstechnik am Bau - Aktuelle Entwicklungen mit Edelstahl Rostfrei" CY - Würzburg, Deutschland DA - 2004-04-27 KW - Bimetallkorrosion KW - Edelstahl Rostfrei KW - Mischverbindungen KW - Verbindungstechnische Lösungen PY - 2004 VL - D884 SP - 49 EP - 64 AN - OPUS4-3522 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hässelbarth, Werner T1 - BERM9 - Ninth International Symposium on Biological and Environmental Reference Materials PY - 2004 IS - Feb. SP - 8 EP - 9 CY - Jerusalem, Israel AN - OPUS4-3523 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Lange, Axel A1 - Harbich, Karl-Wolfram A1 - Hentschel, Manfred P. T1 - Röntgenrefraktometrie ermittelt die Faserenthaftung in Kompositen T2 - DGZfP-Jubiläumstagung 1993 Zerstörungsfreie Materialprüfung CY - Garmisch-Partenkirchen, Deutschland DA - 1993-05-17 PY - 1993 VL - 37-2 SP - 778 EP - 785 PB - DGZfP CY - Berlin AN - OPUS4-3646 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hentschel, Manfred P. A1 - Harbich, Karl-Wolfram A1 - Lange, Axel T1 - New X-ray refractometry of paper and pigments T2 - 4. Internale Konferenz "Zerstörungsfreie Untersuchung an Kunst- und Kulturgütern" CY - Berlin DA - 1994-10-03 PY - 1994 SP - 291 EP - 295 CY - Berlin AN - OPUS4-3650 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hentschel, Manfred P. A1 - Ekenhorst, Derk A1 - Harbich, Karl-Wolfram A1 - Lange, Axel T1 - New X.ray refractography for nondestructive investigations T2 - International Symposium on Advanced Materials for Lightweight Structures CY - Noordwijk, Netherlands DA - 1994-03-22 PY - 1994 N1 - Serientitel: ESA WPP – Series title: ESA WPP IS - 70 SP - 661 EP - 664 PB - ESTEC Conference Bureau CY - Noordwijk AN - OPUS4-3652 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mücke, Udo A1 - Harbich, Karl-Wolfram A1 - Rabe, Torsten T1 - Porengrößenbestimmung an keramischen Sinterwerkstoffen mittels Bildauswertung und Röntgenrefraktionsanalyse T2 - DKG Jahrestagung CY - Aachen, Deutschland DA - 1995-10-08 PY - 1995 SP - 248 EP - 249 CY - Aachen AN - OPUS4-3657 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rabe, Torsten A1 - Mücke, Udo A1 - Röhl-Kuhn, Barbara A1 - Harbich, Karl-Wolfram T1 - Characterization of pores during the densification of SiC T2 - 4th European Ceramic Conference CY - Riccione, Italy DA - 1995-10-02 PY - 1995 SP - 185 EP - 190 CY - Riccione AN - OPUS4-3658 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rabe, Torsten A1 - Mücke, Udo A1 - Harbich, Karl-Wolfram A1 - Goebbels, Jürgen T1 - Nachweis von Porositätsunterschieden in Grün- und Sinterkörpern aus Siliciumcarbid T2 - DKG-Jahrestagung CY - Aachen, Deutschland DA - 1995-10-08 PY - 1995 SP - 41 EP - 43 CY - Aachen AN - OPUS4-3659 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübert, Thomas A1 - Mosel, Günter T1 - Untersuchung der Nahordnung der V5+Ionen in Gläsern des Systems ZnO-B2O3-V2O5 durch Analyse des Vorkantenpeaks im V-K-XANES-Spektrum T2 - 73. Glastechnische Tagung CY - Halle (Saale), Deutschland DA - 1999-05-31 PY - 1999 SP - 22 EP - 25 CY - Frankfurt/Main AN - OPUS4-3772 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübert, Thomas A1 - Mosel, Günter A1 - Nofz, Marianne T1 - Anwendung der Röntgenabsorptionsspektroskopie (XAFS) in der Glasstrukturforschung T2 - 71. Glastechnische Tagung CY - Bayreuth, Deutschland DA - 1997-05-26 PY - 1997 SP - 77 EP - 80 CY - Frankfurt/Main AN - OPUS4-3773 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Qiao, Linan A1 - Droste, Bernhard T1 - Assessment of dynamically loaded cracks in fillets N2 - Practical methods for the safety assessment of postulated crack-like material defects of cubic containers made of ductile cast iron are presented. A formula for the stress intensity factor of a crack in a fillet with a radius from 20 to 200 mm under static load conditions is given. From that, an assessment diagram is derived for the critical depth of a crack in a fillet. The formula may be used to estimate the stress intensity factor of a dynamically loaded crack for special cases. As an application the results of the estimation procedure are compared with the results of a dynamic finite element calculation. T2 - 15th European Conference of Fracture CY - Stockholm, Sweden DA - 2004-08-11 KW - Ductile cast iron KW - Container design KW - Safety assessment KW - Fracture mechanics KW - Dynamic load conditions PY - 2004 UR - http://www.structuralintegrity.eu/pdf/esis/Documents/Conference/ECF/15/Zencker%20U%20et%20al.pdf SP - 1 EP - 8(?) CY - Stockholm AN - OPUS4-3763 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Levkovitch, Vladislav A1 - Sievert, Rainer A1 - Svendsen, B. ED - Portella, Pedro Dolabella T1 - Simulation of Low Cycle Fatigue Failure of FCC Single Crystals T2 - 5th International Conference on Low Cycle Fatigue (LCF-5) CY - Berlin, Germany DA - 2003-09-09 KW - Single crystal KW - Viscoplasticity KW - Simulation KW - Fatigue KW - Lifetime KW - Crack propagation KW - Blunting and resharpening KW - Laird KW - Striations KW - Re-meshing PY - 2003 VL - 5 SP - 415 EP - 420 PB - DVM, Deutscher Verband für Materialforschung und -prüfung CY - Berlin AN - OPUS4-3819 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Cappella, Brunero T1 - Atomic force microscope as a tool for the modification and analysis of surfaces KW - AFM KW - Lithography KW - Surface forces PY - 2004 VL - 1 SP - 1 EP - 30 PB - Transworld Research Network CY - Trivandrum AN - OPUS4-4745 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weise, Frank A1 - Patitz, G. A1 - Redmer, Bernhard A1 - Hübner, M. T1 - Kombination zerstörungsfreier Prüfverfahren zur Strukturaufklärung beim Markttor von Milet KW - Baudenkmäler KW - Strukturaufklärung KW - Zerstörungsfreie Prüfung KW - Radar KW - Radiografie PY - 2004 VL - 2 SP - 117 EP - 128 PB - Wissenschaftlich-Technische Arbeitsgemeinschaft für Bauwerkserhaltung und Denkmalpflege CY - München AN - OPUS4-4820 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, Urs T1 - The Micro-XRF - A New Technique for the Analysis of Building Materials PY - 2004 IS - 26 SP - 3 EP - 4 PB - BRE CY - Garston AN - OPUS4-4738 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bobe, U. A1 - Sommer, K. A1 - Beck, Uwe A1 - Reiners, Georg A1 - Schmidt, R. T1 - Influence on the Adhesion of Biological Particles T2 - 7th European Adhesion Conference - EURADH 2004 CY - Freiburg im Breisgau, Germany DA - 2004-09-07 KW - Haftung KW - Reinigung KW - Mikroorganismen PY - 2004 SP - 6 pages PB - DECHEMA CY - Frankfurt am Main AN - OPUS4-4836 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Innovative korrosionsbeständige höherlegierte Tankwerkstoffe T2 - 7. Gefahrgut-Technik-Tage (GTT) CY - Berlin, Deutschland DA - 2004-11-25 PY - 2004 VL - 7 SP - 52 EP - 60 PB - Storck CY - Hamburg AN - OPUS4-4844 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lohrer, Christian A1 - Schmidt, Martin A1 - Krause, Ulrich T1 - Berechnung des Wärme- und Stofftransportes bei Schüttgutbränden T2 - 7. Fachtagung Arbeits-, Anlagen- und Umweltsicherheit CY - Köthen, Deutschland DA - 2004-11-04 PY - 2004 PB - VDI-Verl. CY - Halle AN - OPUS4-4906 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maierhofer, Christiane A1 - Krause, Martin A1 - Mielentz, Frank A1 - Streicher, Doreen A1 - Milmann, Boris A1 - Gardei, André A1 - Kohl, Christoph A1 - Wiggenhauser, Herbert T1 - Complementary application of radar, impact-echo and ultrasonics for testing concrete structures and metallic tendon ducts T2 - 83rd Annual Meeting Transportation Research Board of the National Academies CY - Washington, D. C., USA DA - 2004-01-11 KW - Non-destructive testing KW - Tendon duct KW - Concrete bridge KW - Radar KW - Ultrasonic KW - Impact-echo PY - 2004 SP - 18 pages CY - Washington AN - OPUS4-4909 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Goedecke, Thomas T1 - Performance and frequency of leakproofness tests for dangerous goods packagings T2 - 14th IAPRI World Conference on Packaging CY - Lidingo, Sweden DA - 2004-06-13 KW - Leakproofness KW - Dangerous goods KW - Packagings PY - 2004 SP - 1(?) EP - 6(?) AN - OPUS4-4911 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Goedecke, Thomas T1 - Baumusterprüfungen von Verpackungen KW - Verpackungen KW - Prüfung KW - Gefahrgut KW - Anerkennung von Prüfstellen PY - 2004 SP - 96 und 117 CY - Hamburg AN - OPUS4-4912 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Mellmann, Günter A1 - Meinhold, Uwe A1 - Oppat, Klaus A1 - Maultzsch, Matthias T1 - Betoninstandsetzung mit Spritzbeton - Anforderungen an den Untergrund - Forschungsbericht FE 15.361/2001/DRB PY - 2004 SP - 1 EP - 70 CY - Berlin AN - OPUS4-4978 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maierhofer, Christiane A1 - Wendrich, Astrid A1 - Köpp, Christian A1 - Falci, M. T1 - Onsiteformasonry - Tecniche die indagine in situ per la valutazione strutturale degli edifici sorici in muratura T2 - Catalogue Restauro CY - Ferrara, Italy DA - 2004-03-25 KW - Non-destructive testing KW - Historic masonry KW - Case studies KW - Structural modelling PY - 2004 SP - 218 EP - 223 AN - OPUS4-4982 LA - ita AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schönhals, Andreas A1 - Goering, Harald A1 - Schick, C. T1 - Segmental Dynamics of Polymeric Liquids Confined to Nanoporous Glasses T2 - ACS 2002 Biennial Symposium "Polymeric Nanomaterials" CY - Rohnert Park, CA, USA DA - 2002-11-17 PY - 2002 AN - OPUS4-2055 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Turky, Gamal A1 - Schönhals, Andreas T1 - Influence of azobenzene concentration on the dielectric behavior of amorphous comb-like copolymers with photochromic azobenzene side groups T2 - 2nd International Conference on Broadband Dielectric Spectroscopy and Its Applications CY - Leipzig, Germany DA - 2002-09-02 PY - 2002 AN - OPUS4-2056 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Goering, Harald A1 - Maneck, Heinz-Eberhard A1 - Mach, Reinhard A1 - Knoll, Uta A1 - Oleszak, Franz A1 - Gajewski, Sven A1 - Brzezinka, Klaus-Werner T1 - Synthese von Nano-Materialien - Fullerene, Kohlenstoff-Nanoröhren, Nanopulver und Schichten T2 - Materialica 2002 ; 5. Internationale Fachmesse für Werkstoffanwendungen, Oberflächen und Product Engineering CY - München, Deutschland DA - 2002-09-30 PY - 2002 SP - 1 EP - 2 AN - OPUS4-2059 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kautek, Wolfgang T1 - Elektrochemische Abscheidung und Konversion für die Mikro- und Nanotechnik - Potential-Pulse und Template T2 - 2. ECHEM Galvaniktag CY - Wiener Neustadt, Österreich DA - 2002-11-25 PY - 2003 AN - OPUS4-2063 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Christina T1 - Proposals for Statistical Methods for Evaluating Performance T2 - CEN Workshop 7 “Humanitarian Mine Action - Test and Evaluation - Metal Detectors” (CW07) CY - Ispra, Italy DA - 2002-04-08 PY - 2002 VL - 7 SP - 1 EP - 7 AN - OPUS4-2067 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Turky, Gamal T1 - Dielectric behavior of some associated liquids T2 - Workshop "Glasübergang" CY - Rostock, Germany DA - 2002-12-16 PY - 2002 AN - OPUS4-2043 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Steckert, Carsten T1 - Farbmetrisch gestützte Farbbildanalyse zur vergleichenden Bewertung geschädigter Lackoberflächen N2 - Für das Qualitätsmanagement der Lackhersteller wurde ein Verfahren entwickelt, das eine objektive Beschreibung des dekorativen Effektes freibewitterter Beschichtungen mit relevanten Messgrößen ermöglicht. Die Maßzahlen über den Farbkontrast bzw. Farbkontrastgradienten der Ungleichmäßigkeiten sowie über die Geometrie erkennbarer Strukturen werden mit Methoden digitaler Farbbildbearbeitung bzw. -analyse ermittelt. Der Einsatz dieser Technik erforderte die systematische Untersuchung und analytische Beschreibung der gerätespezifischen Farbtransformationseigenschaften ausgewählter konventioneller digitaler Ein- und Ausgabemedien (Farbmonitore und Flachbettscanner). In eine kommerzielle Farbbildanalysesoftware wurde ein Farbmanagementsystem implementiert, das auf den bereits ermittelten mathematischen Modellen basiert. Die Bilddaten 150 ausgewählter Probenbleche mit verschieden stark ausgeprägten Beschichtungsschäden wurden mit Methoden der Farbbildanalyse untersucht. Es ließen sich signifikante Merkmale ermitteln, die eine objektive Beschreibung der Farbkontraste der Beschichtungsschäden sowie der Geometrie erkennbarer Mikrostrukturen mit Maßzahlen ermöglichen. Zur Bewertung der fleckartigen Beschichtungsschäden wurden geeignete Klassifikatoren bestimmt, die Korrelationen mit entsprechenden visuellen (subjektiven) Bewertungsergebnissen von geschultem Fachpersonal aufweisen. T2 - Farb-Info 2002 CY - Berlin, BAM, Deutschland DA - 2002-11-21 PY - 2002 UR - http://www.colour-europe.de/StartSeiteInstitutionen-dfz-farbinfo02.htm SP - 1(?) AN - OPUS4-2081 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Senoner, Mathias T1 - Qualitätssicherung in der Nanoanalytik T2 - Abschlussworkshop zum Projektverbund "Nanoskalige Kalibriermethoden- und Normale" CY - Braunschweig, Deutschland DA - 2002-11-19 PY - 2002 AN - OPUS4-2124 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hofmann, Martin A1 - Bender, Josef A1 - Plewinsky, Bodo A1 - Hieronymus, Hartmut A1 - Steinbach, J. T1 - Influence of Obstacles on Surface Detonations T2 - 2nd Internet Conference on Process Safety CY - --- DA - 2000-03-20 PY - 2000 AN - OPUS4-2125 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jäger, Christian A1 - Hartmann, P. A1 - Barth, S. A1 - Vogel, J. A1 - Pauli, Jutta A1 - Schmauder, H.-P. T1 - NMR und Biomaterialien - Was kann man über plasmagespritzte Apatitschichten und Cellulose lernen? T2 - Kolloquium des SFB 428 CY - Freiburg, Deutschland DA - 2002-12-10 PY - 2002 AN - OPUS4-2127 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bertram, R. A1 - Reck, Günter A1 - Alex, V. A1 - Uecker, R. T1 - Growth and domain structure of PZN-PT crystals T2 - 2nd French-German Crystal Growth Meeting (FGCGM - 2003) CY - Nancy, France DA - 2003-03-10 PY - 2003 AN - OPUS4-2129 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schönhals, Andreas T1 - Molecular dynamics and structure of molecules in confining geometries - A comparison of relaxation and scattering techniques T2 - 2nd International Conference on Broadband Dielectric Spectroscopy and Its Applications CY - Leipzig, Germany DA - 2002-09-02 PY - 2002 AN - OPUS4-2039 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schönhals, Andreas T1 - Polar Molecules in Nanoporous Confinements T2 - Workshop "Glasübergang" CY - Rostock, Germany DA - 2002-12-16 PY - 2002 AN - OPUS4-2042 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gogolin, Bernd A1 - Droste, Bernhard A1 - Millan, P. T1 - Results of the Drop Tests with the "RA-3D"Shipping Container for the Transport of Fresh BWR-Fuel Elements T2 - PATRAM 2001 ; Annual International Symposium on Packaging and Transportation of Radioactive Materials CY - Chicago, IL, USA DA - 2001-09-03 PY - 2001 IS - CD-ROM PB - PATRAM CY - Chicago, Ill. AN - OPUS4-1943 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dietlen, Siegmund A1 - Funke, Stefan A1 - Molnarne, Maria A1 - Schröder, Volkmar T1 - Beurteilung der Brennbarkeit von Gasgemischen anhand von Dreistoffdiagrammen - Vergleich mit der Methode der Gefahrstoffverordnung T2 - Dechema-Jahrestagung 1996 CY - Wiesbaden, Deutschland DA - 1996-05-21 PY - 1996 VL - 2 SP - 76 PB - DECHEMA CY - Frankfurt am Main AN - OPUS4-1946 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Molnarne, Maria ED - Nishiumi, H. T1 - Estimation of the Flammability Limits of Combustible Gases and Vapors in Air by a Group Contribution Method T2 - MTMS '97 CY - Tokyo, Japan DA - 1997-01-12 PY - 1997 VL - 144 IS - 1-2 PB - Elsevier CY - Amsterdam AN - OPUS4-1947 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Möller, W. A1 - Molnarne, Maria A1 - Sturm, R. T1 - Limiting oxygen concentration - recent results and their presentation in CHEMSAFE N2 - Summary Substances like alcohols, ethers and esters have recently gained in importance as solvents for paints and varnishes, for surface degreasing and cleaning. Furthermore, fluorinated hydrocarbons are used as refrigerants, replacing chlorofluorocarbons. Because reliable data were not available for most of these substances, measurements of explosion limits and limiting oxygen concentration (MOC) have been carried out by PTB (flammable liquids) and BAM (flammable gases). The poster presents the results of the most recent measurements of MOC for ethanol, i-propanol, ethyl acetate, propyl formate, hexane and for gases as e.g. difluoroethane and methane. Explosion limits and limiting oxygen concentrations have been measured in mixtures with air under ambient conditions and at elevated temperatures according to the German standard DIN 51649. T2 - 9th International Symposium on Loss prevention and safety promotion in the process industries CY - Barcelona, Spain DA - 1998-05-04 PY - 1998 UR - http://www.ptb.de/de/org/3/34/341/moeller.htm AN - OPUS4-1948 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Molnarne, Maria A1 - Möller, W. T1 - New Features of the Databank CHEMSAFE T2 - 1999 AIChE Annual meeting CY - Dallas, TX, USA DA - 1999-10-31 PY - 1999 UR - http://www.aiche.org/conferences PB - American Institute of Chemical Engineers CY - New York AN - OPUS4-1949 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Molnarne, Maria T1 - Estimation of flammability and limiting oxygen concentration of gas mixtures using the database CHEMSAFE T2 - ACHEMA 2000 CY - Frankfurt am Main, Germany DA - 2000-05-01 PY - 2000 PB - DECHEMA CY - Frankfurt, Main AN - OPUS4-1950 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Schendler, Thomas A1 - Fuß, Oliver A1 - Grätz, Rainer A1 - Klank, Wilhelm A1 - Molnarne, Maria A1 - Pfeil, Norbert A1 - Rockland, Ulrike T1 - Studie über Möglichkeiten der Umsetzung des Anhangs I der Seveso-II-Richtlinie unter Berücksichtigung der Anhänge II, III und IV der Störfall-Verordnung PY - 1998 AN - OPUS4-1951 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Molnarne, Maria T1 - Gefahrstoffdaten und ihre Bewertung T2 - Aktualisiertes Fachwissen für Störfallbeauftragte CY - Berlin, Deutschland DA - 1994-04-21 PY - 1994 CY - Berlin AN - OPUS4-1952 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Osterloh, Kurt A1 - Ewert, Uwe T1 - Strahlenprüfung für innere Sicherheit T2 - 2. Internationale Fachmesse für Polizei- und Spezialausrüstung CY - Münster, Deutschland DA - 2002-06-04 PY - 2002 SP - 1 EP - 5 AN - OPUS4-1984 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Osterloh, Kurt T1 - Bildbearbeitung T2 - Pre-Workshop zum 4. BAM-Workshop "Durchstrahlungsprüfung für die öffentliche Sicherheit" CY - Berlin, Deutschland DA - 2002-06-12 PY - 2002 SP - 1 EP - 6 AN - OPUS4-1985 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Osterloh, Kurt A1 - Ewert, Uwe T1 - Auswirkung der Röntgenenergie auf das Bildergebnis T2 - 4. BAM-Workshop "Durchstrahlungsprüfung für die öffentliche Sicherheit" CY - Berlin, BAM, Deutschland DA - 2002-06-12 PY - 2002 SP - 1 EP - 3 AN - OPUS4-1986 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Osterloh, Kurt A1 - Ewert, Uwe T1 - Technologies and Recent Developments to Inspect Suspicious Objects (update and details) T2 - EFNDT Working Group 5 - for Antipersonnel Mines Detection CY - Zagreb, Croatia DA - 2002-09-07 PY - 2002 VL - 7 SP - 1 EP - 9 AN - OPUS4-1988 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Osterloh, Kurt A1 - Ewert, Uwe A1 - Moherndl, A1 - Papenfuß, A1 - Schulz, J. A1 - Rinnebach, A1 - Kempgen, A1 - Becker, A1 - Michel, S. T1 - Podiumsdiskussion - Pro und Contra: Filmersatz durch digitale Medien, Empfehlung für die Zukunft T2 - 4. BAM-Workshop "Durchstrahlungsprüfung für die öffentliche Sicherheit" CY - Berlin, BAM, Deutschland DA - 2002-06-12 PY - 2002 VL - 4 SP - 1 EP - 8 AN - OPUS4-1989 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Molnarne, Maria T1 - Informationssysteme der chemischen Sicherheitstechnik - Datenbanken CHEMSAFE und Gasatlas T2 - EIGA - Symposium CY - Berlin, Deutschland DA - 1998-01-23 PY - 1998 CY - Berlin AN - OPUS4-1965 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Molnarne, Maria T1 - Verfahren zur Darstellung von Explosionsbereichen von Dreistoffsystemen bestehend aus Brenngas/Inertgas/Oxidator T2 - DIN-Normenausschuss "Explosionsgrenzen" CY - Braunschweig, Deutschland DA - 1998-03-23 PY - 1998 CY - Braunschweig AN - OPUS4-1967 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Molnarne, Maria T1 - Erfassung und rechnergestützte Darstellung des Explosionsbereiches von Brenngas/Oxidationsmittel/Inertgas-Systemen T2 - 32. Sitzung "Sicherheitstechnische Kenngrößen" CY - Frankfurt am Main, Deutschland DA - 1999-11-18 PY - 1999 CY - Frankfurt am Main AN - OPUS4-1970 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dióspatonyi, Ildikó A1 - Molnarne, Maria T1 - Kémiai Adatbázisok T2 - Müszaki Kémiai Napok CY - Veszprém, Hungary DA - 2000-04-01 PY - 2000 AN - OPUS4-1972 LA - hun AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Molnarne, Maria T1 - Computer-Vorführung der Datenbank CHEMSAFE T2 - ACHEMA '94 CY - Frankfurt am Main, Deutschland DA - 1994-06-07 PY - 1994 PB - DECHEMA CY - Frankfurt, Main AN - OPUS4-1954 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Molnarne, Maria T1 - Aufbau einer Datenbank für Flüssiggas T2 - GVC/DECHEMA Arbeitsausschuss-Sitzung CY - Frankfurt am Main, Deutschland DA - 1994-11-10 PY - 1994 CY - Frankfurt am Main AN - OPUS4-1955 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Molnarne, Maria T1 - Gefahrstoffe und ihre Bewertung T2 - Tieftemperatur-Technik-Kolloquium der TU Berlin CY - Serfaus, Österreich DA - 1995-02-22 PY - 1995 CY - Serfaus AN - OPUS4-1956 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Molnarne, Maria T1 - Sicherheitstechnische Kenngrößen brennbarer Gase und Gasgemische T2 - DECHEMA-Weiterbildungskurs "Anwendung von bewerteten sicherheitstechnischen Kenngrößen in der Chemischen Technik - Einführung in die Benutzung der CHEMSAFE-Datenbank" CY - Frankfurt am Main, Deutschland DA - 1995-05-16 PY - 1995 CY - Frankfurt am Main AN - OPUS4-1958 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Molnarne, Maria T1 - Sicherheitstechnische Kenngrößen brennbarer Stäube T2 - DECHEMA-Weiterbildungskurs "Anwendung von bewerteten sicherheitstechnischen Kenngrößen in der Chemischen Technik - Einführung in die Benutzung der CHEMSAFE- Datenbank" CY - Frankfurt am Main, Deutschland DA - 1995-05-16 PY - 1995 CY - Frankfurt am Main AN - OPUS4-1959 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Molnarne, Maria T1 - Estimation of flammability of gas mixtures in air containing flammable and inert gases - Testing of the calculation method proposed by ISO 10156 using data from CHEMSAFE T2 - 12th International Congress of Chemical and Process Engineering (CHISA '96) CY - Prague, Czech Republic DA - 1996-08-25 PY - 1996 N1 - Serientitel: Event / European Federation of Chemical Engineering – Series title: Event / European Federation of Chemical Engineering IS - 556 CY - Praha AN - OPUS4-1960 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Molnarne, Maria T1 - Schätz- und Berechnungsverfahren für sicherheitstechnische Kenngrößen und das Programmpaket DDBSP T2 - Benutzertreffen der DDBSP GmbH CY - Oldenburg, Deutschland DA - 1996-09-09 PY - 1996 AN - OPUS4-1961 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Molnarne, Maria T1 - Sicherheitstechnische Probleme bei einem Schiffsunfall T2 - 25. Tieftemperatur-Technik-Kolloquium CY - Serfaus, Österreich DA - 1997-02-19 PY - 1997 CY - Serfaus AN - OPUS4-1962 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schartel, Bernhard A1 - Wachtendorf, Volker A1 - Krüger, Simone A1 - Hennecke, Manfred T1 - Chemiluminescence - An advanced method for small extent, early stages and accelerated testing of the thermooxidative degradation in polymers T2 - Makromolekulares Kolloquium Freiburg CY - Freiburg im Breisgau, Germany DA - 2000-02-24 PY - 2000 SP - 45 CY - Freiburg im Breisgau AN - OPUS4-2435 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schartel, Bernhard A1 - Kunze, Ralf A1 - Neubert, Dietmar T1 - ZnS as Fire Retardant in PVC-P T2 - 2nd International Conference on Polymer Modification, Degradation and Stabilisation (MoDeSt) CY - Budapest, Hungary DA - 2002-06-30 PY - 2002 VL - 82 IS - 2 PB - Elsevier CY - Orlando, Fla. AN - OPUS4-2437 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Habig, Karl-Heinz T1 - Influence of Temperature and Sliding Speed on Friction and Wear of SiSiC and MgO-ZrO2 T2 - 12th Annual Conference on Advanced and Comp. Ceramics CY - Cocoa Beach, FL, USA DA - 1988-01-17 PY - 1988 IS - 9-10 SP - 1419 EP - 1430 AN - OPUS4-2441 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grell, M. A1 - Long, X. A1 - Bradley, D. A1 - Bernius, M. A1 - Chamberlin, T. A1 - Inbasekaran, M. A1 - Woo, E. P. A1 - Hennecke, Manfred A1 - Schartel, Bernhard A1 - Wachtendorf, Volker T1 - A liquid crystalline mainchain conjugated polymer for polarized electroluminescence applications T2 - 4th European Conference on Molecular Electronics (ECME 97) CY - Cambridge, England, UK DA - 1997-09-07 PY - 1997 CY - Stuttgart AN - OPUS4-2432 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schartel, Bernhard A1 - Wachtendorf, Volker A1 - Grell, M. A1 - Bradley, D. A1 - Hennecke, Manfred ED - Gerhard-Multhaupt, R. T1 - Polarized fluorescence and orientational order parameters of a liquid crystalline conjugated polymer T2 - European Conference on Macromolecular Physics: Molecular Orientation in Polymers, Generation, Characterisation, Application CY - Potsdam, Germany DA - 1999-09-30 PY - 1999 N1 - Serientitel: Europhysics conference abstracts – Series title: Europhysics conference abstracts IS - 23H SP - 46 CY - Potsdam AN - OPUS4-2434 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Aurich, Dietmar A1 - Österle, Werner A1 - Portella, Pedro Dolabella A1 - Ziebs, Josef T1 - Werkstoffprüfung einkristalliner Superlegierungen für Turbinenschaufeln T2 - Symposium Materialforschung CY - Bonn, Deutschland PY - 1988 IS - 8 SP - 358 EP - 367 CY - Bonn AN - OPUS4-2455 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Urban, Klaus T1 - Das Versuchsgelände der BAM in Horstwalde PY - 2003 UR - http://html.fkvv.de/artikel/BAM_Howa.pdf SP - 1 EP - 8 PB - Förderverein der Verkehrs-Versuchsanlage Horstwalde CY - Baruth/Mark AN - OPUS4-2466 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Österle, Werner A1 - Li, Pengxi T1 - Development of nanocrystalline microstructures in nickel-base superalloys by grinding and mechanical alloying T2 - 10th European Congress on Electron Microscopy (EUREM) CY - Granada, Spain DA - 1992-09-07 PY - 1992 SP - 313 EP - 314 CY - Stockholm AN - OPUS4-2472 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Österle, Werner A1 - Urban, Ingrid A1 - Nebauer, E. T1 - Alloying reactions of Au-Ni-Ge ohmic contacts to n-GaAs PY - 1994 SP - 781 EP - 782 CY - Les Ulis AN - OPUS4-2479 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Christina A1 - Rosenthal, Martina A1 - Gaal, Mate A1 - Guelle, D. A1 - Lewis, A. A1 - Sieber, A. T1 - Proposals for Performance Demonstration and Modular Reliability Assessment for Humanitarian Demining N2 - For safe and reliable demining it is necessary to determine the actual true performance of mine searching equipment in detecting mines. The subject to detect a hidden subject by penetrating physical interaction with the target is similar to that of non-destructive testing where it is looked for hidden cracks etc. in material via waves and rays. The non destructive testing profession is now about 100 years old and developed some procedures to check reliability of testing. Those principles like the performance demonstration where the successful detections are statistically evaluated against false calls rates and their implementation in an industrial standard (ASME section XI appendix VIII) are analysed. A first adoption to demining was accomplished in the prescription for blind trials in the CEN workshop agreement CEN BT 126 CWA07 for test and evaluation of metal detectors. A number of blind trials were accomplished within an ITEP project to learn about the necessary statistical layout of those trials to achieve true, reproducible and repeatable results to give guidance to selection and improvement of metal detectors. The special focus in these investigations was on the influence of the human factor due to the degree of experience of the operators and the infulence of uncooperative soil. The correlation of the results of the physical parameter measurement and the statistical results is analysed in a first attempt. T2 - EUDEM2-SCOT conference on requirements and technologies for the detection, removal and neutralization of landmines and UXO CY - Brussels, Belgium DA - 2003-09-15 PY - 2003 UR - http://www.itep.ws/pdf/Mueller_Eudem2003_1.pdf N1 - Geburtsname von Rosenthal, Martina: Scharmach, M. - Birth name of Rosenthal, Martina: Scharmach, M. VL - 1 SP - 233 EP - 241 AN - OPUS4-2785 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Osterloh, Kurt T1 - Erste Fachtagung Kampfmittelbeseitigung T2 - 1. Fachtagung Kampfmittelbeseitigung CY - Bad Kissingen, Deutschland DA - 2003-10-22 KW - Definition Kampfmittel KW - Fundmunition KW - Minen KW - Sprengstofffunde PY - 2003 SP - 1(?) EP - 4(?) AN - OPUS4-2788 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heyn, Andreas A1 - Göllner, J. A1 - Burkert, Andreas T1 - Determination of critical pitting temperatures by electrochemical noise T2 - Corrosion 2004 ; 59th NACExpo 2004 ; 59th Annual conference & exposition. NACE International - The Corrosion Society CY - New Orleans, LA, USA DA - 2004-03-28 KW - Critical pitting temperature KW - Electrochemical noise KW - Stainless steel PY - 2004 IS - 04462 SP - 1 EP - 15(?) PB - NACE International CY - New Orleans, La. AN - OPUS4-2775 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fücsök, F. A1 - Müller, Christina A1 - Rosenthal, Martina T1 - Some Results of the RRT of the Radiographic Film Evaluation T2 - MATEST 2003 NDT Achievements and Challenges CY - Brijuni-Pula, Croatia DA - 2003-09-28 KW - Reliability KW - Human factor KW - Radiographic film evaluation PY - 2003 N1 - Geburtsname von Rosenthal, Martina: Scharmach, M. - Birth name of Rosenthal, Martina: Scharmach, M. SP - 1(?) EP - 11(?) AN - OPUS4-2783 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gaal, Mate A1 - Müller, Christina A1 - Osterloh, Kurt A1 - Rosenthal, Martina A1 - Ewert, Uwe A1 - Guelle, D. A1 - Lewis, A. T1 - Metal Detector Test Trials in Germany and Croatia - ITEP Project 2.1.1.2 T2 - MATEST 2003 NDT Achievements and Challenges CY - Brijuni-Pula, Croatia DA - 2003-09-28 KW - Demining KW - Metal detectors KW - Reliability tests KW - ROC diagrams KW - Test and evaluation KW - CWA07 PY - 2003 N1 - Geburtsname von Rosenthal, Martina: Scharmach, M. - Birth name of Rosenthal, Martina: Scharmach, M. SP - 1(?) EP - 15(?) AN - OPUS4-2784 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quercetti, Thomas A1 - Ballheimer, Viktor A1 - Zeisler, Peter A1 - Müller, Karsten T1 - Interactions between Cask Components and Content of Packaging for the Transport of Radioactive Material During Drop Tests N2 - This paper describes the analytical, numerical and experimental investigations on the phenomenon of interactions between cask components and content of packages for the transport of radioactive material during drop tests required according to the IAEA Regulations for the Safe Transport of Radioactive Material. Radial and axial gaps between cask components and content are usually necessary for thermal reasons but larger gaps can exist because of the geometrical dimensions of the specified content. Consequently interactions between content and cask components (lid system, cask body, etc.) are possible and can not be excluded during drop tests. Interactions in this context are relative movements between cask and content which are mainly due to elastic spring effects after releasing the cask for the free drop. These relative movements can cause interior collisions between content and cask during the main impact of the package onto the unyielding target. Drop tests with various types of Type A and Type B packages fully instrumented with strain gauges and accelerometers showed that these interactions respectively interior collisions can be considerable relating to high forces acting on cask lids, lid bolts and the content. Of course the real quantitative consequences of the interactions depend upon different conditions, among others the drop orientation, the design characteristics of the impact limiters, the dimensions of the gaps, the material characteristics of the contents, etc. . In order to investigate more precisely the phenomenon of interactions BAM carried out finite element calculations for the named casks using the ABAQUS/ Standard and ABAQUS/ Explicit computer code comparing them with results obtained from experiments. Additionally, tests with a simplified model instrumented with accelerometers were carried out accompanied by finite element calculations and analytical calculations using MATHEMATICA. The investigations on the mentioned phenomena of interaction show that they should be considered in approval design tests and/ or calculations. T2 - 17th International Conference on Structural Mechanics in Reactor Technology ; SMiRT 17 CY - Prague, Czech Republic DA - 2003-08-17 PY - 2003 UR - http://www.iaea.org/inis/collection/NCLCollectionStore/_Public/36/071/36071659.pdf IS - G04-4 SP - 1(?) EP - 8(?) CY - Prague AN - OPUS4-2825 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grinda, Manfred T1 - Schwierigkeiten der Bewertung von Prüfergebnissen biologischer Prüfungen T2 - 23. Holzschutz-Tagung CY - Augsburg, Deutschland DA - 2003-03-26 PY - 2003 SP - 141 EP - 156 PB - DGfH CY - München AN - OPUS4-2838 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Goedecke, Thomas T1 - Dichtheitsprüfung bei Bauartprüfung und Fertigung T2 - 6. Gefahrgut-Technik-Tage CY - Berlin, Deutschland DA - 2003-01-01 KW - Dichtheitsprüfung KW - Verpackungen KW - Gefahrgut KW - RID/ADR PY - 2003 VL - 6 SP - 1(?) EP - 5(?) PB - Storck CY - Hamburg AN - OPUS4-2839 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fomine, Pavel A1 - Mitropetros, Constantinos A1 - Hieronymus, Hartmut ED - Noskov, A. S. T1 - Some Safety Aspects of a Bubbly Medium Inside Chemical Reactor T2 - 16th International Conference on Chemical Reactors ; 16th CHEMREACTOR CY - Berlin, Germany DA - 2003-12-01 PY - 2003 VL - 107 IS - 1-3 SP - 188 EP - 191 PB - Elsevier CY - Amsterdam AN - OPUS4-2816 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grimm, B. A1 - Krüger, Ralph-Peter A1 - Schrader, S. A1 - Prescher, D. T1 - Molecular structure investigations on fluorine-containing polyazomethines by means of MALDI-TOF-MS technique T2 - Berliner Polymerentage 2000 CY - Berlin, Germany DA - 2000-10-09 PY - 2000 CY - Berlin AN - OPUS4-2253 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beck, Uwe A1 - Baudach, Steffen A1 - Männ, Marion T1 - Spektroskopische Ellipsometrie - Referenzverfahren für die Qualitätssicherung T2 - 2. Workshop Ellipsometrie CY - Berlin, Deutschland DA - 2002-02-18 PY - 2002 AN - OPUS4-2280 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Cobet, C. A1 - Wollschläger, Nicole A1 - Esser, N. A1 - Richter, W. A1 - Baudach, Steffen A1 - Beck, Uwe A1 - Männ, Marion A1 - Brunn, S. A1 - Gruska, B. A1 - Richter, U. T1 - VUV-XUV-Ellipsometrie mit Synchrotronstrahlung T2 - 2. Workshop Ellipsometrie CY - Berlin, Deutschland DA - 2002-02-18 PY - 2002 AN - OPUS4-2282 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Popovics, J. S. A1 - Wiggenhauser, Herbert ED - Smyth, A. W. T1 - Non-Contact Laser Vibrometer Wave Sensing on Concrete N2 - Rapid and accurate non-destructive evaluation (NDE) techniques are needed to assess the in-place condition of concrete structures. However the time and effort required to perform NDE tests using conventional surface-mounted contact sensors hinder rapid evaluation of full-scale structures. The authors are cooperating in research to develop rapid and robust methods that collect mechanical wave signals from concrete structures and to characterize defects in concrete using that signal data. The suitability of surface waves and laser-based, non-contact wave detection techniques for this purpose are examined here. After a brief introduction to non-contact sensing, an experimental set-up is described and results from experimental tests are presented. Mechanical surface waves in a concrete slab specimen are generated with several different conventional sources. The ability of a laser vibrometer to detect wave propagation from concrete that does not have any reflective treatment (normal concrete surface) is demonstrated, allowing the generation of ultrasonic images. Test results from a concrete specimen containing a subsurface defect are then presented. The obtained ultrasonic images illustrate some limitations of using surface waves to detect subsurface defects in concrete, although approaches to improve the results are proposed. T2 - 15th ASCE Engineering Mechanics Conference ; 15th EM 2002 CY - New York, NY, USA DA - 2002-06-02 KW - Concrete KW - Imaging KW - Laser KW - Surface Waves KW - Ultrasound KW - Vibrometer PY - 2002 SP - 1(?) EP - 7(?) AN - OPUS4-2215 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schlaad, H. A1 - Müller, A. A1 - Spickermann, J. A1 - Räder, H. A1 - Krüger, Ralph-Peter T1 - Quantitative Analysis of Molecular Weight Distribution Obtained by Matrix-Assisted Laser Desorption/Ionization Time-of-Flight Mass Spectrometry (MALDI-TOF-MS) T2 - 2nd International Conference on Molecular Mass Characterization of Synthetic and Natural Polymers CY - Bradford, England, UK DA - 1996-04-01 PY - 1996 CY - Bradford AN - OPUS4-2218 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Ralph-Peter A1 - Much, Helmut A1 - Schulz, Günter A1 - Heß, H. A1 - Hübner, H. A1 - Sobisch, T. T1 - Umfassende analytische Charakterisierung handelsüblicher nichtionischer Tenside durch Kopplung von HPLC und MALDI-TOF-MS T2 - Dechema-Jahrestagung 1996 CY - Wiesbaden, Deutschland DA - 1996-05-21 PY - 1996 PB - DECHEMA CY - Frankfurt am Main AN - OPUS4-2220 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Ralph-Peter A1 - Much, Helmut A1 - Schulz, Günter A1 - Frey, H. T1 - Characterization of unusual Silsesquioxane-Based Polymer Architectures Based on the Coupling of Liquid Chromatography and MALDI-TOF-MS T2 - 11th International Symposium on Organosilicon Chemistry CY - Montpellier, France DA - 1996-09-01 PY - 1996 CY - Montpellier AN - OPUS4-2222 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hasche, K. A1 - Herrmann, K. A1 - Thomsen-Schmidt, P. A1 - Krumrey, M. A1 - Ulm, G. A1 - Ade, G. A1 - Pohlenz, F. A1 - Stümpel, J. A1 - Busch, I. A1 - Schädlich, S. A1 - Frank, W. A1 - Hirsch, D. A1 - Schindler, A. A1 - Procop, Mathias A1 - Beck, Uwe T1 - Ein Beitrag zu kalibrierten Nanometerschichten für unterschiedliche Anwendungsbereiche N2 - Nanotechnologien werden gegenwärtig als leistungsfähige Oberflächentechniken in erheblichem Umfange industriell genutzt. Dabei spielen dünne Schichten und deren Kenndaten eine wesentliche Rolle, z.B. als Röntgenspiegel oder optische und magnetooptische Datenträger. Die Schichtdicke zählt hierbei zu den technologisch wichtigen Parametern. Abgeleitet von Anwenderinteressen, werden für die Röntgenreflektometrie (XRR bzw. GIXR), Elektronenstrahl-Mikroanalyse (EPMA) und Röntgenfluoreszenzanalyse (XRF) einerseits und die Ellipsometrie andererseits zugeschnittene Schichtdickenmaßverkörperungen (SDM) entwickelt, gefertigt und untersucht. Das Ziel ist die Bereitstellung praxistauglicher, kalibrierter SDM, im weiteren Schichtdickennormale (SDN) genannt. SDN sind Maßverkörperungen, für die der Schichtdickenwert mit einer definierten Messunsicherheit bekannt und auf ein metrologisch anerkanntes Längennormal zurückgeführt ist. Berichtet wird über die Herstellung und messtechnische Charakterisierung der beiden spezifischen Varianten von Maßverkörperungen. T2 - 47. Internationales Wissenschaftliches Kolloquium. Technische Universität Ilmenau ; Herbstkonferenz der Gesellschaft für Arbeitswissenschaft ; 6. Workshop Multimedia für Bildung und Wirtschaft CY - Ilmenau, Deutschland DA - 2002-09-23 PY - 2002 UR - http://publica.fraunhofer.de/documents/N-14872.html VL - 47 SP - 568 EP - 569 PB - Techn. Univ. CY - Ilmenau AN - OPUS4-2284 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koenders, L. A1 - Hasche, K. A1 - Ulm, G. A1 - Krumrey, M. A1 - Ade, G. A1 - Stümpel, J. A1 - Busch, I. A1 - Thomsen-Schmidt, P. A1 - Schädlich, S. A1 - Schindler, A. A1 - Frank, W. A1 - Beck, Uwe A1 - Procop, Mathias T1 - Über die metrologische Charakterisierung von Schichtdicken Standards im Nanometerbereich T2 - 12th Applied Surface Analysis Workshop ; AOFA 12 CY - --- DA - 2002-09-15 PY - 2002 AN - OPUS4-2285 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reiners, Georg T1 - Bewertung von Dünnschichtsystemen für den Einsatz (Assessment of Thin Film Systems in Practical Operation) T2 - CIO 2003 CY - Braunschweig, Deutschland DA - 2003-02-11 PY - 2003 N1 - Sprachen: Deutsch/Englisch - Languages: German/English SP - 1 EP - 8 CY - Braunschweig AN - OPUS4-2288 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schönhals, Andreas A1 - Frunza, Ligia A1 - Kosslick, H. A1 - Pitsch, I. A1 - Frunza, Stefan T1 - Molecular dynamics of 4n-octylcyanobiphenyl confined to nanoporous molecular sieves of SBA-type T2 - International Conference of Dielectric Spectroscopy CY - Leipzig, Germany DA - 2002-09-01 PY - 2002 SP - 1(?) AN - OPUS4-2264 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schönhals, Andreas A1 - Frunza, Ligia A1 - Frunza, Stefan A1 - Kosslick, H. T1 - Unusual relaxation behavior of water inside the sodalite cages of faujasite-type molecular sieves T2 - International Conference of Dielectric Spectroscopy CY - Leipzig, Germany DA - 2002-09-01 PY - 2002 SP - 1(?) AN - OPUS4-2265 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schönhals, Andreas A1 - Frunza, Stefan A1 - Frunza, Ligia T1 - Dinamica compozitelor aerosil - 8CB prin spectroscopie dielectrica; On the dynamics of aerosil - 8CB composites by dielectric spectroscopy T2 - Romanian Annual Conference 2002 CY - Târgu Mure¸s, Romania DA - 2002-09-01 PY - 2002 SP - 1(?) AN - OPUS4-2266 LA - ron AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schönhals, Andreas A1 - Frunza, Stefan A1 - Kosslick, H. A1 - Frunza, Ligia A1 - Enache, I. A1 - Beica, T. T1 - Studiul stratului de suprafata pe compozite aerosil - 8CB prin analiza termica / Study of surface layer in 8CB-aerosil composites by TG/DTA/TG measurements T2 - Annual Session of Romanian Research Program CERES CY - Bucharest, Romania DA - 2002-11-28 PY - 2002 AN - OPUS4-2267 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schönhals, Andreas A1 - Frunza, Ligia A1 - Kosslick, H. A1 - Pitsch, I. A1 - Fricke, R. A1 - Bentrup, U. A1 - Frunza, Stefan T1 - Nanoporous materials as hosts for liquid crystals T2 - DFG-Workshop on Key Program "Nanoporous Crystals" CY - Berlin, Germany DA - 2002-10-21 PY - 2002 SP - 1(?) AN - OPUS4-2268 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Paatsch, Wolfgang T1 - What is the Alternative to the Salt Spray Test T2 - 5th World Congress on Aluminum CY - Roma, Italy DA - 2003-03-18 PY - 2003 VL - 3 SP - 555 EP - 566 PB - Interall Publications CY - Modena AN - OPUS4-2300 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Prescher, D. A1 - Grimm, B. A1 - Krüger, Ralph-Peter A1 - Schrader, S. T1 - To the formation of F-containing polyazomethines - investigation of the reaction products by MALDI TOF mass spectrometry T2 - 16th International Symposium Fluorine Chemistry CY - Durham, England, UK DA - 2000-07-16 PY - 2000 AN - OPUS4-2246 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, A. A1 - Krüger, Ralph-Peter T1 - Quantitative analysis of molecular weight distribution obtained by matrix-assisted laser desorption/ionization time-of-flight mass spectrometry T2 - DECHEMA-Diskussionstagung "Neue Methoden der Polymeranalytik" CY - Mainz, Germany DA - 1996-10-07 PY - 1996 CY - Mainz AN - OPUS4-2224 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Ralph-Peter A1 - Much, Helmut A1 - Pickard, M. A1 - Schulz, Günter A1 - Wachsen, O. T1 - Characterization of thermal and hydrolytic degradation of polylactides by Liquid Chromatography and MALDI-TOF mass spectrometry T2 - International Symposium on "Biodegradable Materials" and Hamburger Makromolekulares Symposium CY - Hamburg, Germany DA - 1996-10-07 PY - 1996 CY - Hamburg AN - OPUS4-2225 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Malz, Frank A1 - Jancke, Harald A1 - Radeglia, Reiner A1 - Hässelbarth, Werner T1 - Messunsicherheit der quantitativen hochauflösenden NMR-Spektroskopie T2 - GDCh-NMR-Diskussionstagung "Praktische Probleme der Kernresonanzspektroskopie" CY - Bochum, Deutschland DA - 2003-01-13 PY - 2003 SP - 1(?) PB - GDCh CY - Erlangen AN - OPUS4-2226 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rikowski, E. A1 - Krüger, Ralph-Peter A1 - Much, Helmut A1 - Schulz, Günter T1 - Synthesis of Polyhedral Hexa-, Octa-, Deca- and Dodeca Silsesquioxanes, Separation by NP-HPLC, SEC and LACCC, Characterization by MALDI-TOF-MS T2 - 4. Münchener Silikontage CY - München, Germany DA - 1998-04-07 PY - 1998 VL - 4 AN - OPUS4-2234 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simon, Franz-Georg T1 - Benchmarking - An Approach to Characterize Ecomaterials T2 - 2nd International Workshop on Ecomaterials CY - Ibaraki, Japan DA - 2002-11-05 PY - 2002 AN - OPUS4-2499 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völzke, Holger A1 - Schmidt, A. J. T1 - Koordinierungsstelle für Informationen zur Behälterabfertigung (KOBAF / BIBO) T2 - 3. Symposium "Beförderung und Lagerung radioaktiver Stoffe - Stand der BE-Entsorgung" CY - Hannover, Deutschland DA - 2003-05-08 PY - 2003 AN - OPUS4-2500 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike A1 - Schartel, Bernhard T1 - Fire Retardancy Mechanisms of Red Phosphorus in Thermoplastics N2 - The thermal decomposition and the fire behavior of glass fiber reinforced polyamide 66 (PA-66) and high impact polystyrene (HIPS) containing red phosphorus (P4) were investigated. For glass fiber reinforced PA-66, P4 promotes char formation in the condensed phase. Barrier effects and the reduction of combustible volatiles were identified as fire retardancy mechanisms. For HIPS, P4 acts in the gas phase, mainly trapping radicals. The heat release per mass loss polymer is reduced due to an incomplete combustion. T2 - 12th International Conference Additives 2003 CY - San Francisco, CA, USA DA - 2003-04-06 PY - 2003 UR - http://www.executive-conference.com/conferences/archives/abstracts2003/add03_abs5b.html SP - 1(?) EP - 10(?) PB - ECM CY - Plymouth, Mich. AN - OPUS4-2502 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Klaffke, Dieter A1 - Yarim, Rasim A1 - Wäsche, Rolf T1 - Effect of Pre-oxidation on Friction and Wear Behaviour of a SiC-TiC-TiB2 composite PY - 2003 VL - 22 SP - 12 EP - 20 PB - Metallilaboratorio CY - Espoo AN - OPUS4-2517 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Klaffke, Dieter T1 - Test Concept for Tribological Characterisation of Implant Materials Prone to Fretting PY - 2003 VL - 22 SP - 3 EP - 11 PB - Metallilaboratorio CY - Espoo AN - OPUS4-2518 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krull, R. A1 - Hintze, H. A1 - Thomas, Hans-Martin A1 - Heckel, Thomas T1 - ZfP an Schienen heute und in der Zukunft T2 - DVM-Tag 2003 CY - Berlin, Deutschland DA - 2003-05-07 KW - Schienenprüfung KW - Wirbelstromprüfung KW - Ultraschall KW - Head Checks KW - Gruppenstrahlertechnik PY - 2003 N1 - Serientitel: DVM-Bericht – Series title: DVM-Bericht IS - 670 SP - 141 EP - 151 PB - DVM CY - Berlin AN - OPUS4-2522 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Assessment of the corrosion resistance of metallic tank materials in the BAM-list - Requirements for tanks for the transport of dangerous goods T2 - 27th International Exhibition-Congress on Chemical Engineering, Environmental Protection and Biotechnology ; 27th ACHEMA 2003 CY - Frankfurt am Main, Germany DA - 2003-05-19 PY - 2003 SP - 183 PB - DECHEMA, Ges. für Chemische Technik und Biotechnologie CY - Frankfurt am Main AN - OPUS4-2535 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sievert, Rainer A1 - Österle, Werner A1 - Olschewski, Jürgen A1 - Ziebs, Josef T1 - Physical interpretation of a viscoplastic model applied to high temperature performance of a nickel-base superalloy T2 - 7th International Conference on Mechanical Behaviour of Materials CY - The Hague, Netherlands DA - 1995-01-01 PY - 1995 SP - 557 EP - 558 CY - Den Haag AN - OPUS4-2507 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Zunkel, Astrid T1 - Untersuchungen an gütegesicherten Messing-Hahnverlängerungen - BAM-Vorhaben Nr.: VH 7327 PY - 2003 SP - 1 EP - 20 PB - Bundesanstalt für Materialforschung und -prüfung CY - Berlin AN - OPUS4-2529 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Isecke, Bernd T1 - Korrosionsbedingte Schadensfälle an nichtrostenden Stählen - Gründe und Vermeidungsstrategien T2 - VDI-Tagung "Innovative Rostfreistähle für die Verfahrenstechnik, den Anlagen- und Maschinenbau" CY - Düsseldorf, Deutschland DA - 2003-06-25 PY - 2003 AN - OPUS4-2531 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Isecke, Bernd T1 - Prüfverfahren zum Nachweis der Korrosionsbeständigkeit nichtrostender Stähle T2 - VDI-Tagung "Innovative Rostfreistähle für die Verfahrenstechnik, den Anlagen- und Maschinenbau" CY - Düsseldorf, Deutschland DA - 2003-06-25 PY - 2003 AN - OPUS4-2532 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weltschev, Margit T1 - Stichwort "Korrosion": Die Bewertungskriterien für die Beständigkeit von metallischen Tankwerkstoffen PY - 2003 IS - März SP - 4 PB - HOYER GmbH CY - Hamburg AN - OPUS4-2548 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - von Vangerow, Christine T1 - Erfahrungsbericht über integrierte Workflowsysteme in der Verwaltung T2 - Veranstaltung "Effizienter Staat" CY - Berlin, Deutschland DA - 2003-06-02 PY - 2003 AN - OPUS4-2551 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bremser, Wolfram A1 - Hässelbarth, Werner A1 - Kurschat, T. A1 - Wendt, G. T1 - Traceability Chain Analysis and Uncertainty Budget Calculation for the German National Flow Rate Measurement Standard pigsar T2 - International Conference on Metrology - trends and applications in calibration and testing laboratories CY - Jerusalem, Israel DA - 2000-05-16 PY - 2000 PB - NCSL CY - Jerusalem AN - OPUS4-2553 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bremser, Wolfram T1 - Uncertainty Propagation in Analytical Traceability Networks T2 - Analytica Conference 2000 CY - Munich, Germany DA - 2000-04-11 PY - 2000 CY - München AN - OPUS4-2554 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bremser, Wolfram T1 - Nuevos desafíos y dificultades para los laboratorios europeos de ensayo bajo la directiva del "Nuevo Enfoque" T2 - International Qualimetry School "Los laboratorios de análisis bajo el 'Nuevo Enfoque'" CY - Granada, Spain DA - 1999-09-06 PY - 1999 SP - 365 EP - 393 AN - OPUS4-2556 LA - spa AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bremser, Wolfram T1 - Calibration under the new approach T2 - International Gas Analysis Symposium CY - Eindhoven, The Netherlands DA - 1999-11-07 PY - 1999 AN - OPUS4-2559 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hässelbarth, Werner T1 - Traceability in the analysis of natural gas T2 - International Gas Analysis Symposium CY - Eindhoven, The Netherlands DA - 1999-11-07 PY - 1999 AN - OPUS4-2568 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hässelbarth, Werner T1 - Uncertainty based calibration - The approach of the revised ISO 6143 T2 - CCQM Workshop on Measurement Uncertainty CY - Sevres, France DA - 1999-12-01 PY - 1999 AN - OPUS4-2569 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klich, Harry T1 - The Activities of ISO/REMCO in Guidance of Producers and Users of Certified Reference Materials T2 - PITTCON '99 ; Pittsburgh Conference on Analytical Chemistry and Applied Spectroscopy CY - Orlando, FL, USA DA - 1999-03-07 PY - 1999 CY - Orlando, Fla. AN - OPUS4-2571 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klich, Harry T1 - COMAR - The international database for certified reference materials T2 - DUREM-2 CY - New Delhi, India DA - 1999-02-10 PY - 1999 CY - New Delhi AN - OPUS4-2574 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Goering, Harald A1 - Pötschke, P. A1 - Bhattacharyya, A.R. A1 - Janke, A. T1 - Melt mixing of polycarbonate / multi-wall carbon nanotube composites KW - Multi-wall carbon nanotubes KW - Melt mixing KW - Electrical resistivity KW - Rheology PY - 2003 DO - https://doi.org/10.1163/156855403771953650 VL - 10 IS - 4-5 SP - 389 EP - 404 PB - North-Holland CY - New York, NY AN - OPUS4-2869 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klingbeil, Dietmar A1 - Reusch, F. A1 - Svendsen, B. T1 - Fortschritte bei der Zuverlässigkeit rechnerischer Methoden der Schädigungsmechanik zur Auslegung sicherheitsrelevanter Bauteile T2 - 29. MPA-Seminar Sicherheit und Verfügbarkeit in der Energietechnik ; RIMAP Power Workshop ; ECOPRESS Seminar CY - Stuttgart, Deutschland DA - 2003-10-09 PY - 2003 VL - 1 SP - 1.1 EP - 1.20 PB - MPA CY - Stuttgart AN - OPUS4-2855 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erhard, Anton A1 - Boehm, Rainer A1 - Tessaro, Ute A1 - Wüstenberg, Hermann T1 - Characterization and sizing of defects in the cladded area using ultrasonic methods N2 - With the increasing of the storage capability of digitised data and the development of advanced ultrasonic equipment a characterisation of detected defects is possible without new measurements. If the A-scan is stored in a video form (rectified A-scan) or in a high frequency form evaluation techniques like SAFT or echotomography are applicable with advantage. Therefore in some of the cases an estimation of the defect size is reached by the evaluation of the ultrasonic data collected with conventional detection techniques. This is an advantage in relation to the past, because the application of a separate analysis technique is mostly not necessary, therefore time and money is saved. In the present contribution experimental results received in the laboratory are presented. The application of the TOFD approach for defect detection and sizing of crack like defect in heavy components is demonstrated whereas the probes are coupled on the carbon steel surface as well as on the cladded surface. An important point would be the influences of the anisotropic cladding material in relation to the defect sizing using the TOFD technique. These results will be compared with those received with TR longitudinal wave probes and with shear wave probes. T2 - 3rd International Conference on NDE in Relation to Structural Integrity for Nuclear and Pressurized Components CY - Seville, Spain DA - 2001-11-14 PY - 2001 UR - http://www.ndt.net/abstract/ndesi01/data/98.htm SP - 543 EP - 550 CY - Seville AN - OPUS4-2885 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Senoner, Mathias ED - Jäckel, R. T1 - Ein neues zertifiziertes Referenzmaterial für die Analyse von Oberflächenstrukturen im Nanometerbereich KW - zertifiziertes Referenzmaterial KW - Nanotechnologie KW - Oberflächenanalytik KW - Halbleiter-Schichtstrukturen KW - SIMS PY - 2003 UR - http://www.nanotechnology.de/ger/s19/broschuere.pdf SP - 22 EP - 23 PB - Fraunhofer-Institut für Werkstoff- und Strahltechnik CY - Dresden AN - OPUS4-2886 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lebid, Solomija A1 - Gutmann, Toivo A1 - Habel, Wolfgang T1 - Characterisation of high-perfomance composites by using structure-integrated FBG sensors T2 - International Conference on Materials Testing ; TEST Kongress ; TEST Conference CY - Nuremberg, Germany DA - 2003-05-13 PY - 2003 IS - A 3.1 SP - 59 EP - 64 PB - AMA Service GmbH CY - Wunstorf AN - OPUS4-2888 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübert, Thomas A1 - Lorek, Andreas A1 - Banach, Ulrich A1 - Zinal, S. A1 - Boeck, G. T1 - Precision Measurement of Complex Permittivity of Solid Dielectric Materials T2 - International Conference on Materials Testing ; TEST Kongress ; TEST Conference CY - Nuremberg, Germany DA - 2003-05-13 PY - 2003 SP - 89 EP - 94 PB - AMA Service GmbH CY - Wunstorf AN - OPUS4-2878 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jansen, Kirsten A1 - Schulz, Ulrich A1 - Wachtendorf, Volker T1 - Efficiency of UV-Stabilisers in PE-Films under the Influence of Acid Precipitation T2 - 12th International Conference Additives 2003 CY - San Francisco, CA, USA DA - 2003-04-06 PY - 2003 UR - http://www.executive-conference.com/conferences/archives/add03.php SP - 1 EP - 10 PB - ECM CY - Plymouth, Mich. AN - OPUS4-2881 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Beck, Uwe T1 - Referenzverfahren zur Bestimmung von optischen und dielektrischen Materialeigenschaften sowie der Schichtdicke dünner Schichten mittels Ellipsometrie / Reference procedure for the determination of optical and dielectric material properties and the layer thickness of thin films by ellipsometry KW - Ellipsometrie PY - 2004 N1 - Sprachen: Deutsch/Englisch - Languages: German/English IS - DIN PAS 1022 SP - 1 EP - 17 PB - Beuth CY - Berlin AN - OPUS4-3000 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klingbeil, Dietmar A1 - Svendsen, B. A1 - Reusch, F. T1 - Advances in the application of non-local damage models in the simulation of ductile crack-extension N2 - Local damage models usually have the disadvantage that results are strongly mesh dependent. The reason is that the type of the underlying partial differential equations changes under quasi-static conditions from elliptic to hyperbolic. Non-local damage models do not exhibit such behaviour under certain conditions. The usage of such non-local damage models in finite element analyses opens the possibility for preserving the ellipticity of the partial differential equations and thus avoiding mesh dependence of numerically obtained results. The loss of ellipticity for local models and its preservation for non-local models are demonstrated for a wide variety of examples enclosing ductile damage. In the present investigation, the non-local damage model is applied to the simulation of ductile crack extension in fracture mechanics specimens. The type of the underlying differential equations is permanently analysed and controlled. T2 - 15th European Conference on Fracture (ECF-15) CY - Stockholm, Sweden DA - 2004-08-11 KW - Duktile Schädigung KW - Bruchmechanik KW - Nicht-lokal PY - 2004 SP - 1 EP - 8(?) CY - Stockholm AN - OPUS4-4066 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brademann-Jock, Kerstin A1 - Krüger, Simone A1 - Wachtendorf, Volker A1 - Goering, Harald T1 - Degradation effects of automotive coatings after weathering as detected by thermoluminescence T2 - 27th FATIPEC Congress CY - Aix-en-Provence, France DA - 2004-04-19 KW - Automobillacke KW - Bewitterung KW - Thermolumineszenz KW - Automotive coatings KW - Weathering KW - Thermoluminescence PY - 2004 VL - 3 SP - 1045 EP - 1050 PB - Association Francaise des Techniciens des Peintures, Vernis,Encres CY - Aix en Provence AN - OPUS4-4054 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erning, Johann Wilhelm T1 - Sanierung von korrosionsgeschädigten Trinkwasseranlagen T2 - VdS-Fachtagung - Verhütung von Leitungswasserschäden CY - Köln, Deutschland DA - 2004-09-15 KW - Wasserqualität KW - Leckage KW - Korrosion KW - Unterschied Sanierung und Neuinstallation KW - Sanierungsverfahren KW - Ablauf von Sanierungen KW - Trinkwasser PY - 2004 SP - 8 Seiten PB - VdS Schadenverhütung CY - Köln AN - OPUS4-4128 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Paatsch, Wolfgang A1 - Beck, Uwe A1 - Senoner, Mathias T1 - Development of reference materials for surface technology in the micrometer and nanometer range T2 - AESF SUR/FIN 2004 ; Interfinish 2004 World Congress CY - Chicago, IL, USA DA - 2004-06-28 KW - Reference materials KW - Zerstörungsfreie Prüfung KW - Referenzmaterialien PY - 2004 SP - 369 EP - 385 PB - American Electroplaters and Surface Finishers Society (AESF) CY - Orlando AN - OPUS4-4130 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scheid, Marc A1 - Geißler, Andreas A1 - Krause, Ulrich T1 - Zum Einfluss der Turbulenz auf die Druckentlastung von Gas- und Staubexplosionen N2 - Der maßgebliche Einfluss turbulenter Strömungsbewegungen auf den Ablauf von Explosionen ist bereits seit längerem bekannt. Wegen der Schwierigkeit, Betrag und Richtung der turbulenten Schwankungsgeschwindigkeit in-situ zu messen, existieren jedoch nur wenige diesbezügliche experimentelle Daten. Es wurde deshalb eine aus drei Glassegmenten bestehende Versuchsapparatur mit etwa 100 l Volumen und einem Länge/Durchmesser-Verhältnis von 4,7 errichtet, die die gleichzeitige Messung der Strömungsgeschwindigkeit und deren turbulenter Fluktuation, der Ausbreitungsgeschwindigkeit der Flamme, der zeitlichen Entwicklung des Explosionsdruckes sowie im Falle von Staubexplosionen der Staubkonzentration erlaubte. Die Glassegmente wurden durch Metallflansche verbunden, an welche insgesamt sechzehn gleichmäßig über Umfang und Höhe verteilte Ventilatoren zur kontrollierten Erzeugung eines Turbulenzfeldes montiert waren. Die Explosionsversuche wurden mit einem Propan-Stickstoff-Sauerstoff-Gemisch sowie mit einem Maisstärke-Luft-Gemisch durchgeführt. Die Zündung der explosionsfähigen Gemische erfolgte durch einen Hochspannungsfunken. Als Berstfolien wurden zwei Polyethylenfolien (Dicke 10 und 15 µm) und drei Aluminiumfolien (Dicke 15, 20 und 22 µm) verwendet. Die Versuche zeigten sowohl bei Gas- als auch bei Staubexplosionen eine Zunahme des reduzierten Explosionsdruckes für wachsende turbulente Schwankungs-geschwindigkeiten im Bereich von 0 m/s bis 0,45 m/s. Diese Zunahme war besonders ausgeprägt für verhältnismäßig kleine Entlastungsflächen (Durchmesser < 70 mm) bei geringen Ansprechdrücken (Polyethylenfolie), während für höhere Ansprechdrücke (Aluminiumfolie) der Einfluss der Turbulenz zurückging. Zur Ergänzung der Experimente wurden Simulationsrechnungen mit dem Computational Fluid Dynamics-Programm Fluent6 unternommen. Diese Rechnungen dienten der Validierung der den Programmen zugrunde liegenden Modelle im Hinblick auf ihre Anwendbarkeit zur Berechnung von Explosionsabläufen in technischen Anlagen. Es konnte eine realistische Wiedergabe der Druck-Zeit-Verläufe durch die Rechnungen erreicht werden. T2 - 7. Fachtagung Arbeits-, Anlagen- und Umweltsicherheit CY - Köthen, Deutschland DA - 2004-11-04 PY - 2004 SP - 15 Seiten (A 04) PB - VDI-Verl. CY - Halle AN - OPUS4-5069 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scheid, Marc A1 - Krause, Ulrich A1 - Schmidt, Martin T1 - Einflussparameter auf den Ablauf von druckentlasteten Gasexplosionen T2 - 6. Fachtagung Anlagen-, Arbeits- und Umweltsicherheit CY - Köthen, Deutschland DA - 2002-11-07 PY - 2002 IS - Abschnitt P04 SP - C01-1-C01-11 PB - GVC CY - Düsseldorf AN - OPUS4-5071 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scheid, Marc A1 - Geißler, Andreas A1 - Krause, Ulrich T1 - Experiments on the Influence of Turbulence on Vented Gas and Dust Explosions T2 - 5th International Symposium on Hazards, Prevention and Mitigation of Industrial Explosions (ISHPMIE) CY - Cracow, Poland DA - 2004-10-10 KW - Gas explosion KW - Dust explosion KW - Turbulence KW - Venting PY - 2004 SP - 176 EP - 187 PB - Central Mining Institute CY - Kattowitz AN - OPUS4-5074 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias T1 - Lifetime lubricated engines using triboreactive materials N2 - By means of an analysis of future trends in engine oil specifications with the associated consequences for the functional properties performed by base oils and individual additives, the need and potential application of alternative fluids and triboactive materials or lubricious oxides will be displayed. Oxidation resistance and low volatility represent key elements to assure long drains or lifetime lubrication in order to minimize or avoid manual or automatic top-ups. The intrinsic properties of base oils and the additive package define the oxidation resistance and related oxidative volatility. The overall engine oil consumption is also related to design (clearances, thermal stability of geometries, seals,...) and bore surface finishing and are not regarded here. Lubricious oxides or triboactive materials and/or polar base oils substitute the EP and AW properties realized by the additives, thus enabling long drains and responding to "eco-tox" or "bio-no-tox" requirements as well as restrictions from the "chemical box". T2 - RTO Applied Vehicle Technology Panel (AVT) specialists' meeting CY - Williamsburg, VA, USA DA - 2004-06-07 PY - 2004 N1 - Serientitel: RTO meeting proceedings : AVT – Series title: RTO meeting proceedings : AVT IS - 109 PB - NATO Research & Technology Organisation CY - Neuilly-sur-Seine AN - OPUS4-5150 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias A1 - Ketting, M. A1 - Halama, H. A1 - Tomaszewski, J. T1 - Solid bonded films or monolithic ceramics in tracked chains of construction equipments for wear management N2 - Unlubricated tracked chains were realized using soft solid bonded films for the inner wear of the tribosystem of bushing/pin and monolithic ceramic bushings for the outer wear of the tribosystem bushing/sprocket. Both novel approaches were tested on D6 22-to. dozers. Selected solid bonded films and specific monolithic ceramics, offer a potential for simplifying the design, reducing weight and designing a dry-running longlife chain. These results can be further transferred to high-speed running gears or belt drives. T2 - RTO Applied Vehicle Technology Panel (AVT) specialists' meeting CY - Williamsburg, VA, USA DA - 2004-06-07 PY - 2004 UR - http://www.stormingmedia.us/93/9342/A934244.html N1 - Serientitel: RTO meeting proceedings : AVT – Series title: RTO meeting proceedings : AVT IS - 109 PB - NATO Research & Technology Organisation CY - Neuilly-sur-Seine AN - OPUS4-5151 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grinda, Manfred A1 - Carey, J. ED - Bravery, A.F. ED - Peek, R.-D. T1 - The Cost Euro Index for Fungal Decay - Five Years Results T2 - Final Conference 2004 CY - Estoril, Portugal DA - 2004-03-22 KW - Fungal decay KW - EHC 3 KW - Decay index KW - COST E22 PY - 2004 IS - 22597 SP - 1(?) EP - 22(?) AN - OPUS4-5105 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mc Hugh, Jarlath A1 - Döring, Joachim A1 - Stark, Wolfgang A1 - Erhard, Anton T1 - Characterisation of epoxy materials used in the development of ultrasound arrays T2 - 16th World Conference on Nondestructive Testing CY - Montreal, Canada DA - 2004-08-30 PY - 2004 UR - http://www.ndt.net/article/wcndt2004/pdf/materials_characterization/616_mchugh.pdf SP - 8 pages PB - International Committee for Non-Destructive Testing CY - Montreal AN - OPUS4-5215 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schartel, Bernhard ED - Troitzsch, J. T1 - Untersuchungen von Wirkmechanismen - ein Beitrag zur gezielten Optimierung von Polymer-Flammschutzmittel-Systemen T2 - 7. Fachtagung Kunststoffe, Brandschutz und Flammschutzmittel, Neue Entwicklungen und Anwendungen CY - Würzburg, Deutschland DA - 2004-12-01 KW - Fire retardancy KW - Nanocomposites KW - Cone Calorimeter KW - Red Phosphorus KW - Intumescence PY - 2004 SP - D1 EP - D11 PB - SKZ CY - Würzburg AN - OPUS4-5286 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Richter, Klaus T1 - Natural colour connection space (NCCS) between input and output for office systems T2 - International Seminar on Information Office Equipment Standardization CY - Seoul, Korea DA - 2004-11-10 KW - Informationstechnik KW - Farbgeräte KW - Farbordnung KW - Normen PY - 2004 UR - http://www.ps.bam.de/XY91DE.HTM SP - 71 EP - 92 AN - OPUS4-5288 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübert, Thomas T1 - Qualitätssicherung in der Feuchtemesstechnik T2 - Seminar "Feuchtebestimmung bei Trocknungsprozessen" CY - Düsseldorf, Deutschland DA - 2004-11-15 PY - 2004 SP - 34 Seiten PB - VDI-Verl. CY - Düsseldorf AN - OPUS4-5299 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Banach, Ulrich T1 - Referenzverfahren zur Prüfung und Kalibrierung von Gas- und Feuchtesensoren T2 - Symposium "Vor-Ort-Analytik" - Feldmesstechnik für die Erkundung von Altstandorten CY - Stuttgart, Deutschland DA - 2004-01-01 PY - 2004 SP - 1 EP - 10 PB - VEGAS CY - Stuttgart AN - OPUS4-5307 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Kretzschmar, Hans-Jürgen T1 - Ermittlung der Reaktionsprodukte von Vulkanisationsbeschleunigern und deren Entstehung bei der Vulkanisation - Schlußbericht zum Forschungsvorhaben ERP 2558 PY - 1989 SP - 2 EP - 42 PB - Bundesanstalt für Materialforschung und -prüfung CY - Berlin AN - OPUS4-5446 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Burmester, Arno T1 - The economics of possible production in Venezuela T2 - Plastification of wood by irradiation CY - Venezuela DA - 1974-07-12 PY - 1974 IS - VEN/8/03-B SP - 1 EP - 12 PB - International Atomic Energy Agency CY - Vienna AN - OPUS4-8055 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Czichos, Horst T1 - Die tribophysikalischen Abnutzungsmechanismen von Bewegungssystemen T2 - 7. Wissenschaftliche Konferenz der Gesellschaft Deutscher Naturforscher und Ärzte "Biopolymere und Biomechanik von Bindegewebssystemen" CY - --- PY - 1974 SP - 339 EP - 346 PB - Springer CY - Berlin AN - OPUS4-8074 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Czichos, Horst A1 - Mittmann, Hans-Ulrich ED - Glaser, G. T1 - Die mikrostrukturellen Gleitmechanismen von Metall-Metall- und Kunststoff-Metall-Gleitpaarungen mit niedriger Reibung T2 - 9. Internationaler Congress für Chronometrie ; 9e Congrès International de Chronometrie ; 9th International Congress of Chronometry ; 9th CIC CY - Stuttgart, Deutschland DA - 1974-09-16 PY - 1974 VL - D IS - DGC - D9 SP - 1 EP - 15 CY - Stuttgart AN - OPUS4-8078 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmitt, B. F. ED - Schmitt, B. F. T1 - Discussions du Panel PY - 1974 SP - 674 EP - 695 CY - Bruxelles AN - OPUS4-8119 LA - fra AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Richter, Kerstin T1 - Systematische Farbänderungen bei Farbumstimmung und bei verschiedener Beleuchtung PY - 1974 VL - 9 SP - 18 EP - 19 PB - Farbenzentrum e.V CY - Ludwigsburg AN - OPUS4-8097 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Terstiege, Heinz T1 - Spektralphotometrische Untersuchungen an Weißstandards PY - 1974 VL - 26 IS - 6 SP - 277 EP - 282 PB - Elektrotechnischer Verein CY - Wien AN - OPUS4-8098 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Czaika, Norbert A1 - Amberg, N. A1 - Magiera, Götz A1 - Mayer, C. ED - Rossi, B. E. T1 - Instrumentation for Use in Prestressed-concrete Reactor Pressure Vessels T2 - 3rd International Congress on Experimental Mechanics CY - Los Angeles, CA, USA DA - 1973-05-13 PY - 1974 SP - 82 EP - 88 PB - Soc. for Experimental Stress Analysis CY - Westport, Conn. AN - OPUS4-8102 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mayer, Norbert A1 - Amberg, Claus T1 - Ein fluidisches Vielstellen-Meßsystem für den Einsatz unter schwierigen Umgebungsbedingungen T2 - 3. Industrielle Fluidik Tagung CY - Zürich, Schweiz DA - 1974-10-29 PY - 1974 SP - H1 EP - H12 CY - Zürich AN - OPUS4-8103 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mayer, Norbert T1 - Eine neue fluidische Methode zur Messung mechanischer Größen T2 - 5th International Conference on Experimental Stress Analysis and its Influence on Design CY - Udine, Italien DA - 1974-05-27 PY - 1974 IS - Subject 4., Section 4.a., Paper 41 SP - 4.33 EP - 4.38 CY - London AN - OPUS4-8104 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mundry, Eberhard T1 - Erkennung und Beschreibung von Schweißnahtfehlern mit Durchstrahlungs- und Ultraschallprüfung T2 - Schweißtechnisches Seminar CY - --- DA - 1974-01-28 PY - 1974 SP - 93 EP - 104 AN - OPUS4-8105 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mundry, Eberhard T1 - "Klassische" Methoden der zerstörungsfreien Materialprüfung T2 - Laser in der Meßtechnik 1975 CY - Ostfildern, Deutschland DA - 1974-06-19 PY - 1974 IS - 8 (gekürzte Fassung) SP - 1 EP - 4 PB - Techn. Akad. Esslingen CY - Ostfildern AN - OPUS4-8106 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nabel, Eberhard A1 - Mundry, Eberhard A1 - Wüstenberg, Hermann A1 - Neumann, Eberhard T1 - Analysis of ultrasonic echoes by means of pulse spectroscopy T2 - VI. Kongreß für Materialprüfung CY - Budapest, Hungary DA - 1974-10-28 PY - 1974 SP - I-422-I-433 PB - Akademiai Kiado CY - Budapest AN - OPUS4-8107 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Eberhard A1 - Nabel, Eberhard A1 - Leisner, W. A1 - Wüstenberg, Hermann T1 - The ultrasonic testing of welds austenitic steels T2 - International Conference on Quality Control and Non-Destructive Testing in Welding CY - Abington, Cambridge, UK DA - 1974-11-19 PY - 1974 IS - Paper 21 SP - 115 EP - 120 PB - Welding Institute CY - Abington, Cambridge AN - OPUS4-8109 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gerisch, Wolfgang T1 - Grundsätzliche Betrachtungen über Sicherheit und Automatisierung T2 - Symposium Sicherheit und Automatisierung CY - Berlin, Deutschland DA - 1975-10-23 PY - 1975 SP - 9 EP - 28 CY - Berlin AN - OPUS4-8150 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Findeisen, Dietmar T1 - Experimentelle Identifikation von Schwingungsparametern an Viskodämpfern T2 - VDI-Kolloquium - Dämpfungsverhalten von Werkstoffen und Bauteilen CY - Berlin, Deutschland DA - 1975-10-13 PY - 1975 SP - 283 EP - 304 PB - TU Berlin CY - Berlin AN - OPUS4-8153 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Czepluch, Wolf T1 - Rückstrahlmessungen nach DIN 67520 mit verringertem Probenabstand PY - 1974 VL - 26 IS - 1 SP - 17 EP - 20 PB - Elektrotechnischer Verein CY - Wien AN - OPUS4-8092 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mallwitz, E. T1 - Einblick in die Farbenlehre PY - 1974 IS - 10 SP - 13 EP - 14 CY - Berlin AN - OPUS4-8093 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nicolaisen, A. A1 - Richter, Kerstin ED - Hilger, A. T1 - Zum Problem der Farbumstimmung in der Farbmetrik T2 - Colour 73 CY - London, England, UK DA - 1973-01-01 PY - 1974 SP - 539 EP - 542 CY - London AN - OPUS4-8094 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Klingenfuß, Heino T1 - Mischen, Dosieren und Auftragen von Klebstoffen PY - 1974 IS - 11/12 SP - 77 EP - 79 PB - Ingenieur Digest Verl. CY - Frankfurt, M. AN - OPUS4-8127 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krause, Hans-Joachim T1 - Der Gestalteinfluß auf das Tragverhalten punktgeschweißter Bauteile PY - 1974 IS - 11/12 SP - 67 EP - 71 PB - Ingenieur Digest Verl. CY - Frankfurt, M. AN - OPUS4-8132 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Krause, Hans-Joachim T1 - Investigations carried out on the geometry of projections, weld settings and the scatter of shear tensile forces with specimens of USt 1203 PY - 1974 IS - III-507-74 SP - 1 EP - 20 PB - International Institute of Welding CY - Paris AN - OPUS4-8133 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Krause, Hans-Joachim T1 - Proposal for dimensions of spot welded test specimens for measuring shear tensile forces PY - 1974 IS - III-508-74 SP - 1 EP - 13 PB - International Institute of Welding CY - Paris AN - OPUS4-8134 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Preß, Henning T1 - Umweltschutz beim Schweißen - Untersuchungen der Stickoxidbildung bei einer Brenngas-Sauerstoff-Flamme PY - 1974 IS - 11/12 SP - 61 EP - 64 PB - Ingenieur Digest Verl. CY - Frankfurt, M. AN - OPUS4-8136 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schönherr, Wolfgang T1 - Schadensfälle beim Fügen durch Stoffverbinden PY - 1974 IS - 11/12 SP - 49 EP - 53 PB - Ingenieur Digest Verl. CY - Frankfurt, M. AN - OPUS4-8139 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Schönherr, Wolfgang A1 - Wilken, Klaus T1 - Description of 4 not self restraint Hot Cracking Tests PY - 1974 IS - IX-883-74 SP - 1 EP - 16 PB - International Institute of Welding CY - Paris AN - OPUS4-8140 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wilken, Klaus T1 - Das Übertragen der an Proben gewonnenen Versuchsergebnisse auf geschweißte Bauteile PY - 1974 IS - 11/12 SP - 73 EP - 75 PB - Ingenieur Digest Verl. CY - Frankfurt, M. AN - OPUS4-8142 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kirschke, Kurt T1 - Mineral Oils with Polymer Additives - Contributions to Viscometry at High Rates of Shear, Behaviour in Plain Bearings and Normal Stress Effect in Lubrication T2 - Polymères et lubrification CY - Brest, France DA - 1974-05-20 PY - 1975 N1 - Serientitel: Colloques internationaux du Centre national de la recherche scientifique – Series title: Colloques internationaux du Centre national de la recherche scientifique IS - 233 SP - 137 EP - 144 PB - Centre national de la recherche scientifique CY - Paris AN - OPUS4-8298 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kirschke, Kurt T1 - La Documentazione nel Campo dell'Usura, deli' Attrito et della Lubrificazione deli BAM PY - 1974 VL - 9 SP - 122 EP - 123 CY - Milano AN - OPUS4-8300 LA - ita AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neider, Rudolf T1 - National RN Programs in Germany - Standard Reference Materials and Meaningful Measurements PY - 1975 SP - 167 EP - 188 PB - Institute for Materials Research CY - Washington D.C. AN - OPUS4-8333 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reimers, Peter A1 - Lutz, G. A1 - Segebade, Christian T1 - Photonenaktivierungsanalyse von Münzen und kunsthistorischen Objekten T2 - Festkolloquium zum 65. Geburtstag von Dr. K. Giese CY - Bonn, Deutschland DA - 1975-01-01 PY - 1975 SP - 52 EP - 54 AN - OPUS4-8335 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Czaika, Norbert A1 - Amberg, Claus A1 - Magiera, Götz A1 - Mayer, Norbert T1 - Über die Instrumentierung von Spannbeton-Reaktordruckbehältern T2 - Berichterstattung über das vom Bundesminister für Forschung und Technologie geförderte Projekt - Forschung und Entwicklung für Spannbeton-Reaktordruckbehälter CY - Berlin, Deutschland DA - 1975-10-13 PY - 1975 VL - 4-2 SP - 1 EP - 23 CY - Berlin AN - OPUS4-8315 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mundry, Eberhard T1 - "Klassische" Methoden der zerstörungsfreien Materialprüfung T2 - Laser in der Meßtechnik 1975 CY - Ostfildern, Deutschland DA - 1975-10-22 PY - 1975 IS - 2669-02.67 SP - 192 EP - 208 PB - Techn. Akad. Esslingen CY - Ostfildern AN - OPUS4-8320 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schnitger, Dierk A1 - Mundry, Eberhard T1 - Über die Abstufung von Prüfparametern in der Radiographie T2 - 6. Internationales Symposium über zerstörungsfreie Materialprüfung CY - Antwerpen, Belgien DA - 1974-09-18 PY - 1975 SP - SM1 EP - SM7 CY - Mortsel AN - OPUS4-8323 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Becker, Günther T1 - Sur les Termites Xylophages d' Afrique T2 - IUFRO, Division 5, Groupe Protection du Bois, Reunion d'Abidjan CY - Nogent-sur-Marne DA - 1975-02-17 PY - 1975 SP - 75 EP - 83 PB - Centre technique forestier tropical CY - Norgent-sur-Marne AN - OPUS4-8269 LA - fra AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Becker, Günther T1 - Laboratory tests on the natural resistance of wood species against different termite species T2 - IUFRO, Division 5, Groupe Protection du Bois, Reunion d'Abidjan CY - Nogent-sur-Marne DA - 1975-02-17 PY - 1975 SP - 95 EP - 108 PB - Centre technique forestier tropical CY - Norgent-sur-Marne AN - OPUS4-8270 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Becker, Günther A1 - Gersonde, Martin T1 - Preservation of Wood-Based Panels against Fungi and Insects and Testing its Efficiency T2 - World Consultation on Wood Based Panels (background paper) CY - New Delhi, India DA - 1975-02-06 PY - 1975 IS - 114 SP - i-iii, 1-11 CY - New Delhi, India AN - OPUS4-8271 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Deppe, Hans-Joachim T1 - Technological advance in the manufacture and application of wood-based products T2 - World Consultation on Wood-Based Panels (background paper) CY - New Delhi, India DA - 1975-02-06 PY - 1975 IS - 47 SP - i-iii, 1-10 CY - New Delhi, India AN - OPUS4-8279 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Becker, Günther T1 - Bericht über die Tätigkeit des Fachausschusses 3 "Holzschutz" der Deutschen Gesellschaft für Holzforschung 1961-1963 PY - 1963 IS - 3 SP - 2 EP - 4 PB - Deutsche Gesellschaft für Holzforschung CY - München AN - OPUS4-7925 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dittmar, Paul A1 - Voigtsberger, Paul A1 - Schulz, Fabian T1 - Funktionssicheres Werkzeug PY - 1960 IS - 8 SP - 180 EP - 186 PB - Nomos Verl.-Ges. CY - Baden-Baden AN - OPUS4-7877 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Teske, Karl T1 - Auswahl von Stählen nach DIN 17100 für Schweißteile PY - 1960 VL - 62 IS - 2 PB - Coleman CY - Lübeck AN - OPUS4-7891 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rohrbach, Christof T1 - Dynamische Dehnungsmessungen an Beton mit Dehnungsmess-Streifen - insbesondere zur Ermittlung seiner mechanischen Eigenschaften bei schlagartiger Belastung PY - 1960 VL - 13 SP - 1 EP - 43 PB - Verl. Ziviler Luftschutz Ebeling CY - Koblenz AN - OPUS4-7896 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Emschermann, Hans-Heinrich A1 - Flossmann, R. A1 - Rühl, Karl H. T1 - Quantitative Ermittlung der dynamischen Spannungszustände an quergestossenen Biegeträgern mit Hilfe von Funkenkinematographie und Spannungsoptik T2 - 4. Internationaler Kongreß für Kurzzeitphotographie und Hochfrequenzkinematographie CY - Köln, Deutschland DA - 1958-09-22 PY - 1959 SP - 308 EP - 313 PB - Verlag Dr. Othmar Helwich CY - Darmstadt AN - OPUS4-7901 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz-Forberg, Bernd T1 - A severe railway - Accident with UF6 Packagings T2 - 4th International Symposium on Packaging and Transportation of Radioactive Materials CY - Miami Beach, FL, USA DA - 1974-09-22 PY - 1974 IS - 4 SP - 1041 EP - 1050 CY - Springfield, Va. AN - OPUS4-7958 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz-Forberg, Bernd T1 - A furnace test by the standard fire curve as an alternate method to meet the thermal test requirements T2 - 4th International Symposium on Packaging and Transportation of Radioactive Materials CY - Miami Beach, FL, USA DA - 1974-09-22 PY - 1974 IS - 4 SP - 659 EP - 667 CY - Springfield, Va. AN - OPUS4-7959 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz-Forberg, Bernd A1 - Christ, R. T1 - Development and Testing of Overpack-Constructions Based on Phenolic Foam Walls T2 - 4th International Symposium on Packaging and Transportation of Radioactive Materials CY - Miami Beach, FL, USA DA - 1974-09-22 PY - 1974 IS - 4 SP - 207 EP - 216 CY - Springfield, Va. AN - OPUS4-7960 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wieser, Karol E. T1 - Bauartzugelassene GFK-Tanks zur Lagerung von Heizöl und Dieselkraftstoff T2 - 12. öffentliche Jahrestagung der Arbeitsgemeinschaft Verstärkte Kunststoffe CY - Freudenstadt, Deutschland DA - 1974-10-01 PY - 1974 SP - 19-1-19-6 PB - AVK CY - Frankfurt, Main AN - OPUS4-7961 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Becker, Gerhard Wilhelm A1 - Cox, I. A1 - Kelly, A. T1 - Certified reference materials T2 - Western European Metrology Conference CY - Teddington, UK DA - 1973-04-02 PY - 1974 SP - 247 EP - 263 CY - London AN - OPUS4-7940 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Becker, Günther T1 - Wood Preservation in Tropical Countries PY - 1963 VL - 8 IS - 35 SP - 42 EP - 45 PB - SportBusiness Group CY - London AN - OPUS4-7926 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Pohl, Heinz ED - Zimmermann, M. T1 - Mangan in Aluminium, Magnesium und Zink sowie ihren Legierungen PY - 1974 IS - Kap. C-12 SP - 1 EP - 3 PB - Wiss. Verl.-Ges. CY - Stuttgart AN - OPUS4-7969 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Pohl, Heinz ED - Zimmermann, M. T1 - Nickel in Aluminium, Blei und Zink sowie ihren Legierungen PY - 1974 IS - Kap. C-14 SP - 1 EP - 3 PB - Wiss. Verl.-Ges. CY - Stuttgart AN - OPUS4-7970 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pohl, Heinz ED - Zimmermann, M. T1 - Nickel in Elektrolyt- und Hüttenkupfer sowie in Kupferlegierungen PY - 1974 IS - C-14d SP - 1 EP - 3 PB - Wiss. Verl.-Ges. CY - Stuttgart AN - OPUS4-7971 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pohl, Heinz ED - Zimmermann, M. T1 - Nickel in Reinst-Kobalt und Hütten-Kobalt PY - 1974 IS - C-14e SP - 1 EP - 3 PB - Wiss. Verl.-Ges. CY - Stuttgart AN - OPUS4-7972 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Pohl, Heinz ED - Zimmermann, M. T1 - Mangan in unlegierten bis hochlegierten Stählen, Guß- und Roheisen PY - 1974 IS - Kap. D-2c SP - 1 EP - 3 PB - Wiss. Verl.-Ges. CY - Stuttgart AN - OPUS4-7973 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pohl, Heinz ED - Zimmermann, M. T1 - Nickel in unlegierten bis hochlegierten Stählen, Guß- und Roheisen PY - 1974 IS - D-5 SP - 1 EP - 3 PB - Wiss. Verl.-Ges. CY - Stuttgart AN - OPUS4-7974 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rühl, Karl H. T1 - Sprödbruchprüfung und Sprödbruchsicherheit geschweißter Konstruktionen - Tests for Brittle Fracture and Susceptibility to Brittle Fracture of Welded Structures - Etude de la rupture par fragilité et de la sécurité corrélative dans les constructions souldées T2 - Internationale Vereinigung für Brückenbau und Hochbau - Sechster Kongreß CY - Stockholm, Schweden DA - 1960-06-27 PY - 1960 SP - 255 EP - 265 PB - Leemann CY - Zürich AN - OPUS4-7850 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Caemmerer, Winfrid T1 - Risse unterhalb von massiven Dachdecken - Ihre Ursachen und ihre Bekämpfung PY - 1960 VL - 6 SP - 34 EP - 39 PB - Commerzia Verl. CY - Berlin AN - OPUS4-7855 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wiederholt, Wilhelm T1 - Das Verhalten von Metall- und Kunststoffüberzügen und von Rostschutzanstrichen in Hafen-, Meer-, Fluß- und Kanalwasser - Ergebnisse der Laboratoriumsversuche T2 - Fachtagung "Korrosion und Korrosionsschutz am Schiff und im Hafen" CY - Hamburg, Deutschland DA - 1960-06-22 PY - 1960 SP - 105 EP - 117 PB - Blumenfeld CY - Hamburg AN - OPUS4-7841 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Caemmerer, Winfrid T1 - Bauakustik im gegenwärtigen Baugeschehen PY - 1960 VL - 6 SP - 40 EP - 54 PB - Commerzia Verl. CY - Berlin AN - OPUS4-7856 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schneider, Patrick T1 - Zusammenhänge zwischen dem Luftschalldämmaß und dem Luftschallschutz bei verschiedenen Bedingungen im Hochbau PY - 1960 VL - 20 IS - 39-40 SP - 14 EP - 27 PB - Zorn CY - Eichenberg AN - OPUS4-7857 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Becker, Günther T1 - Forschungsaufgaben auf dem Gebiete des Holzschutzes im Hochbau PY - 1960 SP - 46 EP - 47 PB - Bundesministerium für Wohnungsbau AN - OPUS4-7859 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Becker, Günther ED - Ray, D. L. T1 - Testing in the field of timber preservation against marine borers in germany PY - 1959 SP - 443 EP - 450 PB - Univ. of Wash. Press CY - Seattle, Wash. AN - OPUS4-7864 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfender, Max T1 - Politik als moralische Aufgabe - Festvortrag auf dem Bismarck-Kommers der Altakademikerverbände Bremens am 1.4.1960 PY - 1960 AN - OPUS4-7822 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfender, Max T1 - Einweihungsfeier der Gewerbeförderungsanstalt Aachen am 12. März 1959 PY - 1960 SP - 1 EP - 8 AN - OPUS4-7824 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Meckel, Lothar T1 - Papierchromatographische Trennungen direktziehender Cellulose- und Wolldfarbenstoffe PY - 1960 VL - 15 IS - 7 SP - 353 EP - 374 PB - Zollikofer CY - St. Gallen AN - OPUS4-7873 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rühl, Karl H. T1 - Stahlbau und Sprödbruchfragen PY - 1958 SP - 61 EP - 63 PB - Stahlbau-Verl. CY - Köln AN - OPUS4-7742 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Amedick, Egon T1 - Einfluß der Form auf die Dauerhaltbarkeit von Schmiedestücken, insbesondere Kurbelwellen PY - 1958 IS - 3 SP - 55 Seiten PB - Theodor-Wuppermann-Gesellschaft CY - Leverkusen-Schlebusch AN - OPUS4-7726 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Becker, Günther T1 - Protection of plywood against termites PY - 1974 CY - South-Africa AN - OPUS4-8042 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Becker, Günther T1 - Themen und Ergebnisse der von der Arbeitsgemeinschaft Industrieller Forschungsvereinigungen (AIF) geförderten Holzforschung PY - 1974 SP - 92 EP - 101 PB - Dt. Wirtschaftsdienst CY - Köln AN - OPUS4-8045 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Böttcher, Bernhard ED - Müller, E. A. W. T1 - Wärmeflußverfahren - Physikalische Grundlagen PY - 1975 IS - Abschnitt B.4 SP - 1 EP - 10 PB - Oldenbourg CY - München AN - OPUS4-7977 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schickert, Gerald T1 - Acoustic emission technique applied to tests with concrete cubes T2 - 2nd International symposium. RILEM CY - Constanta, Romania DA - 1974-09-04 PY - 1974 VL - 2 SP - 5 EP - 11 PB - Inst. de Recherche du Bâtiment CY - Bucuresti AN - OPUS4-7980 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schickert, Gerald T1 - New approach to calibrating rebound hammers used on concrete T2 - 2nd International symposium. RILEM CY - Constanta, Romania DA - 1974-09-04 PY - 1974 VL - 3 SP - 54 EP - 60 PB - Inst. de Recherche du Bâtiment CY - Bucuresti AN - OPUS4-7981 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brandes, Klaus ED - Schlutheiß, G. F. T1 - Mechanische Probleme der Reaktordynamik T2 - Fachtagung der Fachgruppen Thermo- und Fluiddynamik und Reaktorphysik der Kerntechnischen Gesellschaft im Deutschen Atomforum e. V. über Stand und Erfordernisse der Vorhersage Physikalischer Kenngrössen für Thermische und Schnelle Leistungsreaktoren CY - Karlsruhe, Deutschland DA - 1974-01-29 PY - 1974 N1 - Serientitel: KfK – Series title: KfK IS - 1931 PB - Gesellschaft für Kernforschung mbH CY - Karlsruhe AN - OPUS4-7984 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brandes, Klaus T1 - Der Einfluss der verschiedenen Materialkenngrößen und deren Streuung auf die Abstände von Dehnungsfugen in Flachdächern T2 - 1st International Symposium on Roofs and Roofing CY - Brighton, England, UK DA - 1974-09-09 PY - 1974 IS - 7 SP - 7-1-7-15 CY - London AN - OPUS4-7985 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Deppe, Hans-Joachim T1 - On the Production and Application of Cement-Bonded Wood Chipboards T2 - 8th Washington State University International Particleboard/Composite Materials Symposium CY - Pullman, WA, USA DA - 1974-01-01 PY - 1974 VL - 8 SP - 267 EP - 286 CY - Pullman, Wash. AN - OPUS4-8062 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Voigtsberger, Paul ED - Hagenkötter, Manfred ED - Brenken, W. T1 - Evaluation of Explosion Protection Measurement Methods T2 - Working Place Safety CY - Bad Grund, Germany DA - 1974-07-22 PY - 1974 IS - 7 SP - 7-1-7-5 PB - Federal Institute for Occupational Safety and Accident Research CY - Bad Grund AN - OPUS4-8027 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wiechmann, Wolfgang ED - Hagenkötter, M. ED - Brenken, W. T1 - Appliances for the surveillance of areas endangered by gas explosions T2 - Working Place Safety CY - Bad Grund, Germany DA - 1974-07-22 PY - 1974 IS - 8 SP - 1 EP - 11 PB - Federal Institute for Occupational Safety and Accident Research CY - Bad Grund AN - OPUS4-8028 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Treumann, Hartwig A1 - Lück, H. T1 - Transport und Lagerung von ANC-Sprengstoffen in loser Schüttung T2 - Jahrestagung 1973 CY - Karlsruhe, Deutschland DA - 1973-01-01 PY - 1974 VL - 1973 SP - 87 EP - 104 CY - Karlsruhe AN - OPUS4-8031 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zahn, Edward von A1 - Owen, A. J. T1 - The Activities of the International Group of Experts of the Explosions Risks of Unstable Substances (IGUS) PY - 1974 SP - 235 EP - 237 PB - Elsevier CY - Den Haag AN - OPUS4-8033 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Behrend, Eberhard T1 - Prüfungen im Bauartzulassungsverfahren PY - 1974 SP - 35 EP - 40 AN - OPUS4-8035 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Meckel, Lothar T1 - Textilkennzeichnungsgesetz und Verbraucherschutz PY - 1974 VL - 19 IS - 10 SP - 232 EP - 236 PB - AID CY - Bonn AN - OPUS4-8004 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Knublauch, Erwin T1 - Gipskartonplatten im Entstehungsfeuer PY - 1974 IS - 5 SP - 163 EP - 168 PB - Fachverband Bau Württemberg CY - Stuttgart AN - OPUS4-7990 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hundt, Jürgen T1 - Wärme- und Feuchtigkeitstransport in Beton unter Einwirkung erhöhter Temperatur in Zusammenhang mit den gefügebedingten Eigenschaften T2 - Berichterstattung über das vom Bundesminister für Forschung und Technologie geförderte Projekt - Forschung und Entwicklung für Spannbeton-Reaktordruckbehälter CY - Berlin, Deutschland DA - 1975-10-13 PY - 1975 VL - 4-3 SP - 1 EP - 23 CY - Berlin AN - OPUS4-8186 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mellmann, Günter A1 - Weber, Dietrich T1 - Erfahrungen über die Wirkung äußerer Einflüsse auf die Betoneigenschaften von Spannbeton-Brücken T2 - Die Lebensdauer von Tragkonstruktionen von Betonbauten und Großplattenhäusern CY - Brno, Tschechische Republik DA - 1975-10-13 PY - 1975 SP - 1 EP - 9 CY - Brno AN - OPUS4-8187 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schickert, Gerald T1 - Schwellastprüfungen an Bohrproben aus einer durch äussere Einflüsse stark beanspruchten Spannbeton-Autobahnbrücke T2 - Die Lebensdauer von Tragkonstruktionen von Betonbauten und Großplattenhäusern CY - Brno, Tschechische Republik DA - 1975-10-13 PY - 1975 SP - 1 EP - 8 CY - Brno AN - OPUS4-8188 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schickert, Gerald A1 - Winkler, Helmut T1 - Untersuchungsergebnisse zum mehraxialen Bruch- und Verformungsverhalten von Betonwürfeln T2 - Berichterstattung über das vom Bundesminister für Forschung und Technologie geförderte Projekt: Forschung und Entwicklung für Spannbeton-Reaktordruckbehälter CY - Berlin, Deutschland DA - 1975-10-13 PY - 1975 VL - 3 CY - Berlin AN - OPUS4-8189 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schimmelwitz, Peter A1 - Maultzsch, Matthias T1 - Zum Verhalten von Zementmörtel in ruhenden und bewegten angreifenden Wässern T2 - Die Lebensdauer von Tragkonstruktionen von Betonbauten und Großplattenhäusern CY - Brno, Tschechische Republik DA - 1975-10-13 PY - 1975 SP - 93 EP - 96 CY - Brno AN - OPUS4-8190 LA - ces AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Dietrich A1 - Schimmelwitz, Peter T1 - Škody na predpjatém betonu jednoho dálnicního mostu vyvolané predevším vlivem poypových solí (deutsch: Schäden am Spannbeton einer Autobahnbrücke hervorgerufen insbesondere durch die Einwirkung von Streusalzen) T2 - Die Lebensdauer von Tragkonstruktionen von Betonbauten und Großplattenhäusern CY - Brno, Czech Republic DA - 1975-10-13 PY - 1975 SP - 240 EP - 243 CY - Brno AN - OPUS4-8191 LA - ces AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Winkler, Helmut A1 - Schickert, Gerald T1 - Durchführung von mehraxialen Festigkeitsuntersuchungen an Beton-Probekörpern T2 - Berichterstattung über das vom Bundesminister für Forschung und Technologie geförderte Projekt - Forschung und Entwicklung für Spannbeton-Reaktordruckbehälter CY - Berlin, Deutschland DA - 1975-10-13 PY - 1975 VL - 3-3 SP - 1 EP - 18 CY - Berlin AN - OPUS4-8192 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brandes, Klaus T1 - Abstände von Dehnungsfugen in Flachdächern - Simulation des Verhaltens von Flachdachkonstruktionen mit der Monte-Carlo-Methode T2 - Die Lebensdauer von Tragkonstruktionen von Betonbauten und Großplattenhäusern CY - Brno, Tschechische Republik DA - 1975-10-13 PY - 1975 SP - 1 EP - 8 CY - Brno AN - OPUS4-8193 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Matthees, Wolfgang T1 - Dynamic Analysis of Structural Systems with Internal Gaps under Axialimpact Loading T2 - 3rd International Conference on Structural Mechanics in Reactor Technology CY - London, England, UK DA - 1975-09-01 PY - 1975 IS - E4-11 SP - 1(?) PB - North-Holland CY - Amsterdam AN - OPUS4-8183 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Matthees, Wolfgang T1 - One-dimensional (longitudinal) dynamic analysis of an axisymmetric burst protection vessel: elastic behaviour of prestressed system with varying boundary conditions due to repetitive impact loading T2 - International Seminar on Extreme Load Conditions and Limit Analysis Procedures for Structural Reactor Safeguards and Containment Structures CY - Berlin DA - 1975-09-08 PY - 1975 CY - Berlin AN - OPUS4-8184 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fuhrmann, Gerhard T1 - Das viskoelastische Verhalten von thermoplastischen Kunststoffen bei andauernder Wechselverformung T2 - VDI-Kolloquium - Dämpfungsverhalten von Werkstoffen und Bauteilen CY - Berlin, Deutschland DA - 1975-10-13 PY - 1975 SP - 130 EP - 147 PB - TU Berlin CY - Berlin AN - OPUS4-8232 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Vater, Ernst-Joachim T1 - Viscoelastic Behaviour of Asphalts Used for Highway Construction T2 - 2nd International RILEM Symposium on Mechanical Tests for Bituminous Materials (MTBM) CY - Budapest, Hungary DA - 1975-09-09 PY - 1975 SP - 307 EP - 319 AN - OPUS4-8199 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mielke, Werner T1 - Viskoelastisches Verhalten von Polymeren - Beschreibung durch molekulare Modelle T2 - VDI-Kolloquium - Dämpfungsverhalten von Werkstoffen und Bauteilen CY - Berlin, Deutschland DA - 1975-10-13 PY - 1975 SP - 107 EP - 129 PB - TU Berlin CY - Berlin AN - OPUS4-8238 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Schönherr, Wolfgang T1 - yth-Value as Criterion for Judging the Lamellar Tearing Tendency of Steel Structures PY - 1975 IS - IX-948-76 SP - 1 EP - 14 PB - International Institute of Welding CY - Paris AN - OPUS4-8351 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilken, Klaus ED - Salter, G. T1 - The Measurement of Residual Stresses in Welded Ship Structures and their Effect on the Strenght of the Structure PY - 1975 SP - 169 EP - 178 PB - Welding Institute CY - Abington AN - OPUS4-8352 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ruske, Walter T1 - Wirtschaftspolitik, Unternehmertum und Wissenschaft am Beispiel der chemischen Industrie Berlins im 19. Jahrhundert PY - 1976 N1 - Serientitel: Studien zu Naturwissenschaft, Technik und Wirtschaft im Neunzehnten Jahrhundert – Series title: Studien zu Naturwissenschaft, Technik und Wirtschaft im Neunzehnten Jahrhundert IS - 3 SP - 694 EP - 715 PB - Vandenhoeck und Ruprecht CY - Göttingen AN - OPUS4-8354 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böttcher, Bernhard A1 - Caemmerer, Winfrid A1 - Rudolphi, Reinald T1 - Wärmebrücken im Hochbau PY - 1976 SP - 107 EP - 120 PB - DGZfP CY - Berlin AN - OPUS4-8396 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böttcher, Bernhard A1 - Mundry, Eberhard T1 - Zur Fehlererkennbarkeit bei Anwendung von Wärmeflußverfahren an verschiedenen Werkstoffen T2 - Infrarot-Sondertagung Material- und Bauteilprüfung durch Infrarot-Strahlungsmessungen PY - 1976 SP - 15 EP - 33 PB - DGZfP CY - Berlin AN - OPUS4-8397 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lehnen, A. J. A1 - Meckel, Lothar T1 - Textile Fußbodenbeläge und Brandrisiko PY - 1976 SP - 267 EP - 276 PB - Vereinigung zur Förderung des Deutschen Brandschutzes CY - Karlsruhe AN - OPUS4-8405 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Plank, Arno T1 - Bauforschung und Bauwirtschaft PY - 1976 IS - 8 SP - 368-370, 379-380 PB - Fachverband Bau Württemberg CY - Stuttgart AN - OPUS4-8391 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dietrich, T. T1 - Über die kritische Penetrationsgeschwindigkeit von Pfählen in rolligem Boden T2 - 6th European Conference on Soil Mechanics and Foundation Engineering CY - Wien, Österreich DA - 1976-03-22 PY - 1976 VL - 3 IS - 1-13 SP - 399 EP - 406 CY - Wien AN - OPUS4-8394 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzlöhner, Ulrich T1 - Earthquake induced residual settlements of foundations T2 - 6th World Conference on Earthquake Engineering (WCEE) CY - New Delhi, India DA - 1977-01-10 PY - 1977 VL - 6 SP - 1 EP - 6 CY - San Francisco AN - OPUS4-8395 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schrimmer, Peter T1 - Kette oder Riemen - Weiterhin Zugmittel bei Getrieben? PY - 1976 SP - 283 EP - 285 PB - Ingenieur Digest Verl.-Ges. CY - Frankfurt, M. AN - OPUS4-8366 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wieser, Karol E. ED - Hertsch, H. T1 - GFK-Tanks zur Beförderung gefährlicher Güter T2 - Internationale Tagung über Verstärkte Kunststoffe CY - Freudenstadt, Deutschland DA - 1976-10-05 PY - 1976 SP - 19-1-19-6 PB - AVK, Arbeitsgemeinschaft Verstärkte Kunststoffe CY - Frankfurt, Main AN - OPUS4-8371 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Trapper, Joachim T1 - European Cylinder Regulations PY - 1976 VL - May-June SP - 10 EP - 14 CY - Washington, DC AN - OPUS4-8458 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Becker, Günther T1 - New Results on Nutrition, Orientation and Activity of Termites T2 - Annual Convention of the British Wood Preserving and Damp-Proofing Association CY - Cambridge, England, UK DA - 1976-06-29 PY - 1976 N1 - Serientitel: BWPA – Series title: BWPA IS - 1976 SP - 1(?) EP - 10(?) CY - London AN - OPUS4-8465 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hattwig, Martin T1 - Verfahren zur Bestimmung der Explosionskennzahlen T2 - Kolloquium Druckentlastung von Staubexplosionen CY - Düsseldorf, Deutschland DA - 1975-06-05 PY - 1975 SP - 91 EP - 101 AN - OPUS4-8428 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heinrich, Hans-Jürgen T1 - Explosionsablauf in Behältern und Rohrleitungen sowie Behältern, die durch Rohrleitungen miteinander verbunden sind T2 - Kolloquium Druckentlastung von Staubexplosionen CY - Düsseldorf, Deutschland DA - 1975-06-05 PY - 1975 SP - 23 EP - 31 AN - OPUS4-8429 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Leuschke, Günter T1 - Einführung in die Richtlinie VDI 3673 T2 - Kolloquium Druckentlastung von Staubexplosionen CY - Düsseldorf, Deutschland DA - 1975-06-05 PY - 1975 SP - 4 EP - 9 AN - OPUS4-8431 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Leuschke, Günter T1 - Selbstentzündung von staubförmigen Materialien PY - 1976 SP - 145 EP - 159 PB - Vereinigung zur Förderung des Deutschen Brandschutzes CY - Karlsruhe AN - OPUS4-8432 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klaffke, Dieter ED - Feller, ED - Frohberg, ED - Osterwald, ED - Thomas, T1 - Electron Chanelling Patterns im Rasterelektronenmikroskop T2 - Fachseminar "Verhalten und Eigenschaften von metallischen Oberflächen" CY - Berlin, Deutschland PY - 1976 SP - 189 EP - 211 CY - Berlin AN - OPUS4-8510 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dunger, Birgitt A1 - Hunger, Johanna ED - Effertz, P.H. T1 - Zum Nachweis von Schwingungsbrüchen in Lamellengraphitguß mit Hilfe des Raster- und Durchstrahlungselektronenmikroskops PY - 1976 SP - 23 EP - 27 PB - Allianz Versicherungs-AG CY - München AN - OPUS4-8513 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Günther, Achim T1 - Die Prüfung neuartiger Kunststoffverpackungen für Feuerwerkspielwaren und Kleinfeuerwerk T2 - Jahrestagung / Institut für Chemie der Treib- und Explosivstoffe der Fraunhofer-Gesellschaft CY - Karlsruhe, Deutschland DA - 1975-06-11 PY - 1975 SP - 471 EP - 479 CY - Karlsruhe AN - OPUS4-8444 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lemke, Dieter T1 - Wärmestauverfahren und adiabatische Lagerung zur sicherheitlichen Beurteilung thermisch instabiler Stoffe T2 - 3. Internationales Kolloquium für die Verhütung von Arbeitsunfällen und Berufskrankheiten in der Chemischen Industrie ; 3ère Colloque International sur la Prévention des Risques Professionnels dans l'Industrie Chimique ; 3rd International Symposium on the Prevention of Occupational Risks in the Chemical Industry CY - Frankfurt am Main, Deutschland DA - 1976-06-21 PY - 1976 SP - 103 EP - 115 PB - Sekretariat Berufsgenossenschaft d. Chem. Industrie CY - Heidelberg AN - OPUS4-8445 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Czichos, Horst ED - Feller, ED - Frohberg, ED - Osterwald, ED - Thomas, T1 - Tribophysikalische Grenzflächenvorgänge bei der Festkörperreibung Metall/Metall und Kunststoff/Metall T2 - Fachseminar "Verhalten und Eigenschaften von metallischen Oberflächen" CY - Berlin, Deutschland PY - 1976 SP - 212 EP - 243 CY - Berlin AN - OPUS4-8505 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Treumann, Hartwig T1 - Ein Ordnungs- und Dokumentationssystem für die Pyrotechnik T2 - Jahrestagung / Institut für Chemie der Treib- und Explosivstoffe der Fraunhofer-Gesellschaft CY - Karlsruhe, Deutschland DA - 1975-06-11 PY - 1975 SP - 407 EP - 422 CY - Karlsruhe AN - OPUS4-8447 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zahn, Edward von T1 - Gefahren und Schutzmassnahmen beim Vertrieb pyrotechnischer Gegenstände in Grossverkaufsstätten T2 - Jahrestagung / Institut für Chemie der Treib- und Explosivstoffe der Fraunhofer-Gesellschaft CY - Karlsruhe, Deutschland DA - 1975-06-11 PY - 1975 SP - 455 EP - 470 CY - Karlsruhe AN - OPUS4-8448 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lenz, Matthias ED - Lüscher, M. T1 - The Dependence of Hormone Effects in Termite Caste Determination on External Factors PY - 1976 SP - 73 EP - 89 PB - Pergamon Press CY - Oxford AN - OPUS4-8492 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Deppe, Hans-Joachim T1 - Holzwerkstoffe in ihrer geschichtlichen Entwicklung PY - 1976 SP - 16 EP - 21 CY - Horn-Bad Meinberg AN - OPUS4-8478 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meckel, Lothar A1 - Beyer, Horst T1 - Zur Beurteilung der elektrostatischen Aufladbarkeit textiler Fußbodenbeläge PY - 1976 N1 - Serientitel: Schriftenreihe des Deutschen Wollforschungsinstitut an der Technischen Hochschule Aachen – Series title: Schriftenreihe des Deutschen Wollforschungsinstitut an der Technischen Hochschule Aachen IS - 5 SP - 433 EP - 444 PB - RWTH Aachen CY - Aachen AN - OPUS4-8408 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reimers, Peter A1 - Lutz, G. A1 - Segebade, Christian T1 - Photon Activation Analysis of Coins and Objects of Art T2 - 5th International Conference : Modern trends in activation analysis CY - München, Germany DA - 1976-09-13 PY - 1976 VL - 2 SP - 1171 EP - 1176 CY - College Station, Tex. AN - OPUS4-8556 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reimers, Peter A1 - Bodenstedt, F. T1 - Zerstörungsfreie Bestimmung der Legierungsbestandteile von altgriechischen Goldmünzen PY - 1976 SP - 69 EP - 75 PB - Accademia Nazionale dei Lincei CY - Rom AN - OPUS4-8557 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Segebade, Christian A1 - Lutz, G. A1 - Weise, Hans-Peter T1 - Quantitative Evaluation of Interference Reactions in Photon Activation Analysis T2 - 5th International Conference : Modern trends in activation analysis CY - München, Germany DA - 1976-09-13 PY - 1976 VL - 2 SP - 1239 EP - 1244 CY - College Station, Tex. AN - OPUS4-8560 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weise, Hans-Peter A1 - Segebade, Christian T1 - Application of X-ray spectroscopy in nondestructive photon activation analysis T2 - 5th International Conference : Modern trends in activation analysis CY - München, Germany DA - 1976-09-13 PY - 1976 VL - 1 SP - 146 EP - 153 CY - College Station, Tex. AN - OPUS4-8564 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wüstenberg, Hermann A1 - Kutzner, Jürgen A1 - Engl, G. T1 - Dependence of Echo Amplitude on Defect Orientation in Ultrasonic Examinations T2 - 8th World Conference on Nondestructive Testing CY - Cannes, France DA - 1976-09-06 PY - 1976 IS - 3H4 SP - 1 EP - 8 CY - Cannes AN - OPUS4-8546 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wüstenberg, Hermann A1 - Kutzner, Jürgen A1 - Kaps, U. T1 - Détermination Dimensionelle des Défauts lors de Contrôles par Ultrasons au Moyen d'une Methode d'Interpretation de la Dynamique des Echos T2 - 8th World Conference on Nondestructive Testing CY - Cannes, France DA - 1976-09-06 PY - 1976 IS - 3H2 SP - 1 EP - 8 CY - Cannes AN - OPUS4-8547 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neider, Rudolf A1 - Wandelburg, Klaus A1 - Weise, Hans-Peter A1 - Dudzus, Thomas A1 - Fusban, H. A1 - Jost, Peter A1 - Reimers, Peter A1 - Schmitt, B. A1 - Segebade, Christian T1 - Comparison of photon activation analysis with other modern analytical methods as tools for the solution of actual analytical problems T2 - 5th International Conference : Modern trends in activation analysis CY - München, Germany DA - 1976-09-13 PY - 1976 VL - 2 SP - 1396 EP - 1405 CY - College Station, Tex. AN - OPUS4-8555 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mennigen, Michael T1 - Bundesanstalt für Materialprüfung (BAM) PY - 1977 SP - 96 EP - 97 PB - Kluge CY - Berlin AN - OPUS4-8586 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Aurich, Dietmar A1 - Helms, Rolf A1 - Schmidt, P. A1 - Veith, Helmut A1 - Ziebs, Josef T1 - The Influence of the Stress State on KIc T2 - 4th International Conference on Structural Mechanics in Reactor Technology (SMiRT) CY - San Francisco, CA, USA DA - 1977-08-15 PY - 1977 IS - G5-2 SP - 1 EP - 9 PB - North-Holland CY - Amsterdam AN - OPUS4-8590 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wobst, Klaus A1 - Aurich, Dietmar T1 - Assessment of flaws in structural components on the basis of a hypothesis of cleavage fracture T2 - 4th International Conference on Fracture (ICF4) CY - Waterloo, Canada DA - 1977-06-19 PY - 1977 VL - 2 IS - MS186 SP - 183 EP - 193 CY - [Wechselnde Verlagsorte] AN - OPUS4-8595 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kutzner, Jürgen A1 - Wüstenberg, Hermann A1 - Kaps, U. T1 - Acoustical Holography with Numerical Reconstruction as a Tool for the Analysis of Ultrasonic Indication T2 - 8th World Conference on Nondestructive Testing CY - Cannes, France DA - 1976-09-06 PY - 1976 IS - 3G4 SP - 1 EP - 8 CY - Cannes AN - OPUS4-8533 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gundlach, Dietrich A1 - Hammer, Wilfried T1 - Spectral Adjustment of a Photomultiplier by the Spectral Mask Method T2 - 7th International Symposium of the Technical Committee on Photon Detectors (IMEKO) CY - Budapest, Hungary DA - 1976-01-01 PY - 1976 VL - 7 SP - 90 EP - 106 CY - Budapest AN - OPUS4-8517 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Terstiege, Heinz T1 - Color measurement for non-standard conditions PY - 1976 VL - 3 IS - 1 SP - 1 EP - 9 PB - Color Science Association of Japan CY - Tokyo AN - OPUS4-8518 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Witt, Karin T1 - Nachstellung von Farbvorlagen mit Hilfe der Farbmetrik PY - 1976 VL - 10 SP - 15 EP - 18 PB - Farbenzentrum e.V CY - Ludwigsburg AN - OPUS4-8521 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rohrbach, Christof A1 - Knapp, Jürgen ED - Striker, G. T1 - Novel magnetic-mechanical time-multiplexer for multichannel measurement on rotating parts T2 - 7th IMEKO Congress of the International Measurement Confederation CY - London, England DA - 1976-05-10 PY - 1976 N1 - Serientitel: Acta IMEKO – Series title: Acta IMEKO VL - 3 IS - 7 PB - North-Holland Publ. Co. CY - Amsterdam AN - OPUS4-8522 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mundry, Eberhard T1 - Klassische Methoden der zerstörungsfreien Materialprüfung T2 - Laser in der Meßtechnik 1976 CY - --- DA - 1976-10-27 PY - 1976 IS - 3003-02.84 SP - 209 EP - 226 PB - Techn. Akad. Esslingen AN - OPUS4-8538 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mundry, Eberhard A1 - Kutzner, Jürgen A1 - Wüstenberg, Hermann T1 - Zum Reflexionsverhalten verschiedener Reflektoren bei der Ultraschallprüfung T2 - Symposium - Zerstörungsfreie Analyse von Werkstoff-Gefügen und Werkstoff-Fehlern CY - Saarbrücken, Deutschland DA - 1975-12-03 PY - 1976 SP - 105 EP - 129 AN - OPUS4-8539 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nabel, Eberhard A1 - Neumann, Eberhard T1 - Evaluation of Flaw Indications by Ultrasonic Pulse Amplitude and Phase Spectroscopy T2 - 8th World Conference on Nondestructive Testing CY - Cannes, France DA - 1976-09-06 PY - 1976 IS - 3H6 SP - 1 EP - 8 CY - Cannes AN - OPUS4-8540 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stadthaus, Meinhard A1 - Kern, W. A1 - Michalski, F. A1 - Becker, E. A. A1 - Dickhaut, E. T1 - Properties of inspection media for the magnetic-particle-method T2 - World conference on nondestructive testing ; 8 CY - Cannes, France DA - 1976-09-06 PY - 1976 CY - Cannes AN - OPUS4-8543 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stadthaus, Meinhard A1 - Michalski, F. A1 - Kaiser, Danny T1 - The human eye - an instrument for nondestructive testing T2 - World conference on nondestructive testing ; 8 CY - Cannes, France DA - 1976-09-06 PY - 1976 CY - Cannes AN - OPUS4-8544 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wittig, Günther T1 - About Antenna Problems in the Application of Microwaves in Nondestructive Testing T2 - 8th World Conference on Nondestructive Testing CY - Cannes, France DA - 1976-09-06 PY - 1976 SP - 1 EP - 8 CY - Cannes AN - OPUS4-8545 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Helms, Rolf A1 - Naseband, Klaus T1 - A ductile fracture criterion for metals T2 - 4th International Conference on Fracture CY - Waterloo, Canada DA - 1977-06-19 PY - 1977 VL - 2 IS - MS45 SP - 503 EP - 512 CY - [Wechselnde Verlagsorte] AN - OPUS4-8598 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Klingenfuß, Heino T1 - Entwicklungstendenzen der Klebtechnik in der automatisierten Fertigung PY - 1976 SP - 240 EP - 241 PB - Ingenieur Digest Verl.-Ges. CY - Frankfurt, M. AN - OPUS4-8566 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hattwig, Martin T1 - Selected aspects of explosion venting T2 - 2nd International Symposium on Loss and Safety Promotion in the Process Industries CY - Heidelberg, Germany DA - 1977-09-06 PY - 1977 AN - OPUS4-8689 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heinsohn, G. T1 - Eignungsprüfung von Gaswarngeräten T2 - 27. Sitzung des NAMUR-Ausschusses "Analysenmesstechnik" CY - Karlsruhe, Deutschland DA - 1977-05-12 PY - 1977 SP - 58 EP - 66 CY - Karlsruhe AN - OPUS4-8693 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meckel, Lothar T1 - Tekstil Maddelerinin Taninma Isaretleri Icin Federal Almanyada Kullanian Yöntemlerin Kritik Degerlendirmesi. - Kritische Beurteilung der in der Bundesrepublik Deutschland verwendeten Methoden zur Kennzeichnung von Textilien PY - 1977 AN - OPUS4-8664 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dietrich, T. T1 - On some Extremum Property of Load-Settlement Curves of Axially Loaded Piles T2 - 6th European Conference on Soil Mechanics and Foundation Engineering CY - Vienna, Austria DA - 1976-03-22 PY - 1977 VL - 2.2 IS - 1-13 SP - 181 EP - 182 CY - Wien AN - OPUS4-8645 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Matthees, Wolfgang T1 - Longitudinal Dynamic Analysis of Preloaded Systems due to Repetitive Impact-Loading T2 - 4th International Conference on Structural Mechanics in Reactor Technology (SMiRT) CY - San Francisco, CA, USA DA - 1977-08-15 PY - 1977 IS - J9-7 SP - 1(?) PB - North-Holland CY - Amsterdam AN - OPUS4-8626 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hoffmann, Dirk A1 - Schimmelwitz, Peter A1 - Rooß, Helmut T1 - Interactions of Sulfur Dioxide with Lime Plasters T2 - 2nd International Symposium on the Deterioration of Building Stones CY - Athens, Greece DA - 1976-09-27 PY - 1977 SP - 37 EP - 42 CY - Chambéry AN - OPUS4-8628 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niesel, Konrad A1 - Schimmelwitz, Peter T1 - Deux méthodes pour caractériser des processus lors de I'altération de pierres de construction T2 - 2nd International Symposium on the Deterioration of Building Stones CY - Athens, Greece DA - 1976-09-27 PY - 1977 SP - 127 EP - 131 CY - Chambéry AN - OPUS4-8634 LA - fra AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Plank, Arno T1 - Leichtmauermörtel mit niedriger Wärmeleitfähigkeit für belastetes Mauerwerk - Arten, Eigenschaften, Grenzen der Anwendung T2 - Lehrgang CY - Düsseldorf DA - 1977-03-28 PY - 1977 N1 - Serientitel: VDI-Bildungswerk – Series title: VDI-Bildungswerk SP - 1 EP - 11 CY - Düsseldorf AN - OPUS4-8623 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Buchhardt, Frank T1 - A storage minimizing method for the application of three-dimensional finite elements T2 - 4th International Seminar on the Computational Aspects of the Finite Element Method (CAFEM) CY - Long Beach, CA, USA PY - 1977 SP - 1 EP - 35(?) AN - OPUS4-8625 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dietrich, T. ED - Moh, Z. T1 - A comprehensive mechanical model of sand at low stress level T2 - 9th International Conference on Soil Mechanics and Foundation Engineering CY - Tokyo, Japan DA - 1977-07-01 PY - 1977 SP - 33 EP - 43 CY - Tokyo AN - OPUS4-8646 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzlöhner, Ulrich ED - Borm, G. ED - Meissner, H. T1 - Plane Deformation of Sand T2 - International Symposium on Numerical Methods in Soil Mechanics and Rock Mechanics ; Internationales Symposium über Numerische Methoden der Bodenmechanik und Felsmechanik CY - Karlsruhe, Germany DA - 1975-09-14 PY - 1977 SP - 47 EP - 53 PB - Inst. für Bodenmechanik und Felsmechanik der Univ. Karlsruhe CY - Karlsruhe AN - OPUS4-8650 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wüstenberg, Hermann A1 - Kutzner, Jürgen T1 - Anzeigenregistrierung und Fehlerrandabtastung mit fokussierenden Prüfköpfen T2 - Sitzung Neuere Verfahren zur Analyse von Ultraschall-Befunden CY - Berlin, Deutschland DA - 1977-02-24 PY - 1977 SP - 147 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung CY - Berlin AN - OPUS4-8777 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heidemeyer, Jürgen T1 - Einfluß der mechanischen Verformung von Metallen bei Mischreibung auf die chemische Reaktivität der Reibpartner T2 - 2. Europäischer Tribologie-Kongreß, EUROTRIB CY - Düsseldorf, Deutschland DA - 1977-10-03 PY - 1977 VL - 2-3 SP - 32-1-32-4 AN - OPUS4-8736 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mølgaard, J. A1 - Czichos, Horst ED - Glaeser, W. T1 - The Application of Systems Techniques to the Study of Wear T2 - 1st International Conference on Wear of Materials CY - St. Louis, MO, USA DA - 1977-04-25 PY - 1977 SP - 30 EP - 35 PB - The American Society of Mechanical Engineers CY - New York, NY AN - OPUS4-8738 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Knapp, Jürgen A1 - Rohrbach, Christof T1 - Anwendung der Strombalance-Schaltung für Vielstellenmessungen mit Dehnungsmesstreifen T2 - 5th International Conference on Experimental Stress Analysis and its Influence on Design CY - Udine, Italien DA - 1974-05-27 PY - 1974 IS - Subject 4., Section 4.a., Paper 40 SP - 4.26 EP - 4.32 CY - London AN - OPUS4-8756 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kutzner, Jürgen A1 - Zimpfer, Joachim T1 - Fehleranalyse mit akustischer Linienholographie und numerischer Rekonstruktion T2 - Sitzung Neuere Verfahren zur Analyse von Ultraschall-Befunden CY - Berlin, Deutschland DA - 1977-02-24 PY - 1977 SP - 2 EP - 10 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung CY - Berlin AN - OPUS4-8763 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Habig, Karl-Heinz A1 - Chatterjee-Fischer, R. A1 - Hoffmann, F. T1 - Zum tribologischen Verhalten von Oberflächenschichten, die durch Eindiffusion von Stickstoff, Bor oder Vanadin in Eisenwerkstoffe gebildet werden T2 - 2. Europäischer Tribologie-Kongreß, EUROTRIB CY - Düsseldorf, Deutschland DA - 1977-10-03 PY - 1977 VL - 1 SP - 28-1-28-4 AN - OPUS4-8735 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nabel, Eberhard T1 - Analyse von Ultraschallanzeigen durch Entfaltung T2 - Sitzung Neuere Verfahren zur Analyse von Ultraschall-Befunden CY - Berlin, Deutschland DA - 1977-02-24 PY - 1977 SP - 149 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung CY - Berlin AN - OPUS4-8767 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nabel, Eberhard A1 - Just, Tilman T1 - Diskussionsbeitrag zur Verbesserung des Signal-Rausch-Verhältnisses bei der US-Prüfung grobkörniger Werkstoffe T2 - Sitzung Neuere Verfahren zur Analyse von Ultraschall-Befunden CY - Berlin, Deutschland DA - 1977-02-24 PY - 1977 SP - 119 EP - 126 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung CY - Berlin AN - OPUS4-8768 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Paatsch, Wolfgang T1 - Surface Reactions Investigated by Modulation Spectroscopy and Photopotential Measurements T2 - 7th International Vacuum Congress (IVC) ; 3rd International Conference on Solid Surfaces CY - Vienna, Austria DA - 1977-09-12 PY - 1977 VL - 7 SP - 911 EP - 913 CY - Oxford AN - OPUS4-8613 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Czepluch, Wolf T1 - Der Glanz - ein wichtiger Faktor zur Oberflächenbeurteilung PY - 1977 VL - 6 SP - 22 EP - 23 PB - Verl. Farbe + Design CY - Gaildorf AN - OPUS4-8746 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gundlach, Dietrich T1 - Annäherung von Normlichtart D65 für Zwecke der Farbmessung PY - 1977 SP - 218 EP - 222 PB - Adam Hilger CY - London AN - OPUS4-8747 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Richter, Kerstin T1 - Licht, Material, Farbreiz und Auge PY - 1977 VL - 6 SP - 43 EP - 45 PB - Verl. Farbe + Design CY - Gaildorf AN - OPUS4-8748 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Richter, Kerstin T1 - Gegenfarbsystem (GS) und Farbsehgleichungen für beliebige Farbstimmung PY - 1977 SP - 350 EP - 355 PB - Adam Hilger CY - London AN - OPUS4-8749 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Terstiege, Heinz T1 - Normung in der Farbmetrik PY - 1977 VL - 6 SP - 51 EP - 52 PB - Verl. Farbe + Design CY - Gaildorf AN - OPUS4-8751 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Terstiege, Heinz T1 - Farbmessungen an gekrümmten Oberflächen PY - 1977 SP - 213 EP - 215 PB - Adam Hilger CY - London AN - OPUS4-8752 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Witt, Karin T1 - Möglichkeiten zur Festlegung des Farbsystems DIN 6164 für NL D65 PY - 1977 SP - 401 EP - 404 PB - Adam Hilger CY - London AN - OPUS4-8753 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nagel, Dieter T1 - Influence of Defects in the Brazed Seam on the Mechanical Properties of High-Temperature Brazed Joints T2 - Annual assembly of the International Institute of Welding CY - Copenhagen, Denmark DA - 1977-07-05 PY - 1977 SP - 1 EP - 10 CY - Lausanne AN - OPUS4-8800 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Brandes, Klaus A1 - Struck, Werner T1 - Das Trageverhalten quergestoßener Stahlbetonbauteile bei geregeltem Stoßkraft-Zeit-Verlauf - Stoß auf Stahlbetonbauteile PY - 1978 AN - OPUS4-8856 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dietrich, Th. ED - Heinz, M. T1 - Experimental Study of flexible Piles in Sand Cyclically Displaced at Low Frequency T2 - International symposium on testing in situ of concrete structures ; RILEM international symposium on in-situ tests of concrete structures ; Colloque international de la RILEM sur "L'essai in situ des structures en béton" CY - Budapest, Hungary DA - 1977-09-12 PY - 1978 VL - 1 SP - 233 EP - 244 CY - Budapest AN - OPUS4-8862 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Trubiroha, Peter T1 - Irradiance, Temperature and Humidity in Artificial Weathering Devices T2 - The weathering of plastics and rubber CY - London, England, UK DA - 1976-06-08 PY - 1978 SP - B2.1 EP - B2.11 PB - Inst. of Electrical Engineers CY - London AN - OPUS4-8873 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pastuska, Gerhard A1 - Just, Ulrich A1 - August, Hans T1 - The Influence of Processing on the Molecular Weight Distribution of Polyamides T2 - 5ème Conférence Européenne des Plastiques et des Caoutchoucs ; 5th European Plastics and Rubbers Conference CY - Paris, France DA - 1978-06-12 PY - 1978 IS - C-3 SP - 1 EP - 5 CY - Paris AN - OPUS4-8874 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ruske, Walter T1 - Chemie in Berlin Lehre und Forschung im Wandel der Jahrhunderte T2 - Chemiedozententagung der Chemischen Gesellschaft der DDR 1978 CY - Mühlhausen, Deutschland DA - 1978-04-11 PY - 1978 SP - 1 EP - 24 PB - Chemische Gesellschaft der DDR CY - Berlin AN - OPUS4-8808 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Helms, Rolf A1 - Aurich, Dietmar T1 - Diskussionsbeitrag zum Bericht "Zweiachsiger Nennspannungszustand an der Rißfront" v. H. Dietmann und K. Kußmaul T2 - 4. MPA-Seminar Bruchverhalten und Brucherscheinungen - Primärsystem und Sicherheitsbehälter ; 4. MPA-Seminar CY - Stuttgart, Deutschland DA - 1978-10-04 PY - 1978 N1 - Serientitel: MPA-Seminar – Series title: MPA-Seminar IS - 4 SP - 1 EP - 13(?) PB - MPA CY - Stuttgart AN - OPUS4-8817 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Heinz W. T1 - Extended Testing of Plutonium Shipping Containers T2 - 5th International Symposium on Packaging and Transportation of Radioactive Materials CY - Las Vegas, NV, Vereinigte Staaten von Amerika DA - 1978-05-07 PY - 1978 VL - 5 IS - 4 SP - 235 EP - 250 CY - Springfield, Va. AN - OPUS4-8818 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Heinz W. A1 - Schulz-Forberg, Bernd T1 - Considerations to improve Quality Assurance Criteria - Experience in the Federal Republic of Germany T2 - 5th International Symposium on Packaging and Transportation of Radioactive Materials CY - Las Vegas, NV, Vereinigte Staaten von Amerika DA - 1978-05-07 PY - 1978 VL - 5 IS - 4 SP - 882 EP - 886 CY - Springfield, Va. AN - OPUS4-8819 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz-Forberg, Bernd T1 - Testing and Approval of portable Tanks in the Federal Republic of Germany T2 - 5th International Symposium on the Transport of Dangerous Goods by Sea and Inland Waterways CY - Hamburg, Germany DA - 1978-04-24 PY - 1978 VL - 5-1 SP - 1 EP - 18 CY - Hamburg AN - OPUS4-8821 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz-Forberg, Bernd A1 - Hübner, Heinz W. A1 - Wieser, Karol E. T1 - Model Testing of Heavy Spent Full Casks and Waste Packagings T2 - 5th International Symposium on Packaging and Transportation of Radioactive Materials CY - Las Vegas, NV, Vereinigte Staaten von Amerika DA - 1978-05-07 PY - 1978 VL - 5 IS - 4 SP - 424 EP - 436 CY - Springfield, Va. AN - OPUS4-8822 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz-Forberg, Bernd A1 - Neider, Rudolf T1 - Improvement of the IAEA Safety System - What is necessary? T2 - 5th International Symposium on Packaging and Transportation of Radioactive Materials CY - Las Vegas, NV, Vereinigte Staaten von Amerika DA - 1978-05-07 PY - 1978 VL - 5 IS - 4 SP - 825 EP - 830 CY - Springfield, Va. AN - OPUS4-8823 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rooß, Helmut T1 - Verfahren zur Bekämpfung von aufsteigender Feuchtigkeit im Mauerwerk - Allgemeiner Teil (Informationsschrift) PY - 1978 SP - 1(?) EP - 4(?) CY - Berlin AN - OPUS4-8847 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schickert, Gerald A1 - Gerstle, K. H. A1 - Linse, D. A1 - Bertacchi, P. A1 - Kotosovos, M. A1 - Ko, H.-Y. A1 - Newman, J. A1 - Rossi, P. A1 - Taylor, M. A1 - Traina, L. A1 - Zimmerman, R. A1 - Bellotti, R. T1 - Strength of Concrete under Multiaxial Stress States T2 - Douglas McHenry Symposium ; International Symposium on Concrete and Concrete Structures CY - Mexico City, Mexico DA - 1976-10-29 PY - 1978 N1 - Serientitel: American Concrete Institute special Publications – Series title: American Concrete Institute special Publications IS - 55 SP - 103 EP - 131 PB - American Concrete Institute CY - Detroit, Mich. AN - OPUS4-8848 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Brandes, Klaus T1 - Analyse des statischen und dynamischen Verhaltens von Konstruktionen auf der Grundlage der Methode der finiten Elemente - Anwender-Programmsysteme SAP IV / NONSAP PY - 1978 IS - 1 SP - 9 EP - 13 CY - Berlin AN - OPUS4-8853 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Barthelmeß, Helmut A1 - Zentner, F. T1 - Auf der Messe: Normung und Literaturdokumentation PY - 1977 IS - 3 SP - 1 PB - Dt. Verl. für Schweißtechnik CY - Düsseldorf AN - OPUS4-8791 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Barthelmeß, Helmut T1 - Rules and Principles of Thesaurus Work in the Study Group "Thesaurus and Exchange of Abstracts" (SG-TEA) PY - 1977 IS - SG-TEA-18-77 SP - 1(?) EP - 3(?) CY - London AN - OPUS4-8792 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hoffmann, Dirk T1 - Verfahren zur Bekämpfung von aufsteigender Feuchtigkeit im Mauerwerk - Elektrophysikalische (elektrokinetische) Verfahren (Informationsschrift) PY - 1978 SP - 1(?) EP - 4(?) CY - Berlin AN - OPUS4-8838 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niesel, Konrad T1 - L'evolution de la diminution de la masse comme base pour l'evaluation de l'essai de cristallisation T2 - International Symposium on Deterioration and Protection of Stone Monuments CY - Paris, France DA - 1978-06-05 PY - 1978 IS - Report 3.5 SP - 1 EP - 13 CY - Paris AN - OPUS4-8843 LA - fra AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niesel, Konrad T1 - Untersuchungen an Uranvorkommen in Sandsteinen des Saarlandes PY - 1978 N1 - Serientitel: Geowiss. Ser. – Series title: Geowiss. Ser. IS - 15 SP - 147 EP - 210 PB - Müller CY - Scheidt AN - OPUS4-8844 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Richter, Harry T1 - Verfahren zur Bekämpfung von aufsteigender Feuchtigkeit im Mauerwerk - Mechanische und chemische Verfahren (Informationsschrift) PY - 1978 SP - 1(?) EP - 4(?) CY - Berlin AN - OPUS4-8845 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Treumann, Hartwig T1 - The classification of pyrotechnic compositions and articles according to their safety hazard T2 - 6th International Pyrotechnics Seminar CY - Denver, CO, USA DA - 1978-01-01 PY - 1978 VL - 6 SP - 599 EP - 614 CY - Denver, Colo. AN - OPUS4-8908 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Arndt, Jürgen A1 - Hantsche, Harald T1 - Selbstbau einer Füllstandskontroll- und Sicherheitseinrichtung für die N2-fl.-Kühlung von Halbleiterdetektorsystemen T2 - 2. Sitzung des Arbeitsausschusses Geräteentwicklung CY - Berlin, Deutschland DA - 1977-10-14 PY - 1978 SP - 65 EP - 70 CY - Berlin AN - OPUS4-8940 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Arndt, Jürgen A1 - Hantsche, Harald A1 - Schmidt, Daniel T1 - Eine einfache Strahlstrom-Stabilisierungseinrichtung für das Stereoscan Mark II A T2 - 2. Sitzung des Arbeitsausschusses Geräteentwicklung CY - Berlin, Deutschland DA - 1977-10-14 PY - 1978 SP - 57 EP - 64 CY - Berlin AN - OPUS4-8941 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hantsche, Harald T1 - Einige Auswahlkriterien für die Beschaffung eines Rechners zur Auswertung von energiedispersiven Röntgenspektren T2 - 2. Sitzung des Arbeitsausschusses Geräteentwicklung CY - Berlin, Deutschland DA - 1977-10-14 PY - 1978 SP - 95 EP - 103 CY - Berlin AN - OPUS4-8944 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Deppe, Hans-Joachim T1 - Holzbaustoffe und Holzschutz T2 - Kongreß "Stadtsanierung" (AMK-Messeband) CY - Berlin, Deutschland DA - 1978-01-01 PY - 1978 SP - 2 EP - 12 CY - Berlin AN - OPUS4-8927 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kühne, Helmut T1 - Sanierungsmaßnahmen gegen Holzschädlinge PY - 1978 VL - 16 SP - 25 EP - 27 PB - Bauinformation-GmbH CY - Frankfurt, M. AN - OPUS4-8930 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mundry, Eberhard T1 - Neuere Entwicklungen und besondere Verfahren der zerstörungsfreien Prüfung T2 - Europäische Tagung für Zerstörungsfreie Materialprüfung CY - Mainz, Deutschland DA - 1978-04-24 PY - 1978 SP - 2/21 EP - 2/42 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung CY - Berlin AN - OPUS4-8960 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Trapper, Joachim T1 - Erscheinungsformen des Acetylenzerfalls T2 - Schulungstagung der Beratungsingenieure CY - Bad Godesberg, Deutschland DA - 1978-04-18 PY - 1978 SP - 63 EP - 83 AN - OPUS4-8918 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heinsohn, G. T1 - Prüfung ortsfester Gaswarngeräte T2 - Beitrag zum Lehrgang Gaswarnanlagen CY - Esslingen, Deutschland DA - 1978-05-01 PY - 1978 IS - 3614-07.42 SP - 1 EP - 16 AN - OPUS4-8898 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heinsohn, G. T1 - Safety aspects in transporting motor vehicles and camping trailers via roll-on/roll-off-vessels T2 - 5th International Symposium on the Transport of Dangerous Goods by Sea and Inland Waterways CY - Hamburg, Germany DA - 1978-04-24 PY - 1978 VL - 2-3 IS - F5 SP - 1-18, 23-24 CY - Hamburg AN - OPUS4-8899 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schwarz, Wolfram T1 - Gesichtspunkte bei der Wahl eines Rasterelektronenmikroskopes unter Berücksichtigung der neuesten Entwicklungstendenzen T2 - 2. Sitzung des Arbeitsausschusses Geräteentwicklung CY - Berlin, Deutschland DA - 1977-10-14 PY - 1978 SP - 85 EP - 94 CY - Berlin AN - OPUS4-8948 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Miescher, K. A1 - Richter, Klaus A1 - Valberg, A. T1 - Farbe und Farbsehen, Beschreibung von Experimenten für die Farbenlehre PY - 1978 IS - 8 SP - 15 EP - 29 PB - Verl. Farbe + Design CY - Gaildorf AN - OPUS4-8951 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Richter, Klaus T1 - Modell für einheitliche farbmetrische und lichttechnische Hellempfindungsgrößen T2 - Lichttechnische Gemeinschaftstagung CY - Amsterdam, Niederlande DA - 1978-06-13 PY - 1978 VL - 2 SP - 461 EP - 473 CY - Amsterdam AN - OPUS4-8952 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Terstiege, Heinz T1 - Über die Gründe für die Neuausgabe von DIN 6171 PY - 1978 IS - 1, Beilage SP - 1 EP - 4 PB - 3M Deutschland CY - Neuss AN - OPUS4-8953 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Terstiege, Heinz T1 - Farben und Farbtoleranzen bei innenbeleuchteten Verkehrszeichen T2 - Lichttechnische Gemeinschaftstagung CY - Amsterdam, Niederlande DA - 1978-06-13 PY - 1978 VL - 2 SP - 474 EP - 482 CY - Amsterdam AN - OPUS4-8954 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wutzke, Günter ED - Kreitlow, H. T1 - Moire-Topographie T2 - Herbstschule '77 CY - Hannover, Deutschland DA - 1977-09-28 PY - 1978 SP - 11 EP - 42 CY - Hannover AN - OPUS4-8980 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Engl, G. A1 - Rathgeb, Werner A1 - Wüstenberg, Hermann A1 - Walte, F. T1 - Auslegung von Prüfköpfen und Prüfkopfsystemen für die automatisierte Ultraschallprüfung unter Benutzung beugungstheoretischer Modelle T2 - Europäische Tagung für Zerstörungsfreie Materialprüfung CY - Mainz, Deutschland DA - 1978-04-24 PY - 1978 SP - 115 EP - 121 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung CY - Berlin AN - OPUS4-8981 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erhard, Anton A1 - Wüstenberg, Hermann A1 - Mundry, Eberhard T1 - 90°-Longitudinalwellen-Winkelprüfkopf zum Nachweis oberflächennaher Risse T2 - Europäische Tagung für Zerstörungsfreie Materialprüfung CY - Mainz, Deutschland DA - 1978-04-24 PY - 1978 VL - 1 SP - 107 EP - 114 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung CY - Berlin AN - OPUS4-8982 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hecht, A. A1 - Mundry, Eberhard A1 - Nabel, Eberhard A1 - Neumann, Eberhard T1 - Korngrößenbestimmung in austenitischen Feinblechen mit Ultraschall T2 - Europäische Tagung für Zerstörungsfreie Materialprüfung CY - Mainz, Deutschland DA - 1978-04-24 PY - 1978 VL - 2 SP - 395 EP - 402 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung CY - Berlin AN - OPUS4-8983 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Just, Tilman A1 - Römer, Manfred A1 - Neumann, Eberhard A1 - Mundry, Eberhard T1 - Vergleich der Leistungsfähigkeit verschiedener Ultraschallprüftechniken für grobkristalline Werkstoffe mittels statistischer Methoden T2 - Europäische Tagung für Zerstörungsfreie Materialprüfung CY - Mainz, Deutschland DA - 1978-04-24 PY - 1978 VL - 2 SP - 323 EP - 330 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung CY - Berlin AN - OPUS4-8985 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wüstenberg, Hermann T1 - Erfahrungen beim praktischen Einsatz von fokussierenden Prüfköpfen T2 - Ultraschallprüfung Seminar CY - Saarbrücken, Deutschland DA - 1978-03-09 PY - 1978 SP - 1 EP - 25 AN - OPUS4-8997 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wüstenberg, Hermann A1 - Kutzner, Jürgen A1 - Schulz, Eckhard A1 - Erhard, Anton T1 - Ultraschallanzeigen von Rißkanten T2 - Europäische Tagung für Zerstörungsfreie Materialprüfung CY - Mainz, Deutschland DA - 1978-04-24 PY - 1978 VL - 1 SP - 99 EP - 106 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung CY - Berlin AN - OPUS4-8998 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wüstenberg, Hermann A1 - Neumann, Eberhard T1 - Improved probe techniques at the ultrasonic inspection of coarse grained materials T2 - 6th Water Reactor Safety Research Information Meeting CY - Gaithersburg, MD, USA DA - 1978-11-06 PY - 1978 SP - 1(?) EP - 16(?) CY - Washington, DC AN - OPUS4-9000 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wüstenberg, Hermann A1 - Erhard, Anton A1 - Kutzner, Jürgen T1 - Detection and Analysis of Near Surface-Cracks by Ultrasound T2 - 1st International Symposium on Nondestructive Characterization of Materials CY - Gaithersburg, MD, USA DA - 1978-06-07 PY - 1978 SP - 1(?) EP - 16(?) PB - Plenum Press CY - New York AN - OPUS4-9001 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neider, Rudolf A1 - Becker, K. T1 - The Role of Nuclear Standards in Nuclear Technology Transfer T2 - Conference on Transfer of Nuclear Technology CY - Persepolis, Iran DA - 1977-04-10 PY - 1978 VL - 1 SP - 379 EP - 399 CY - Hinsdale, Ill. AN - OPUS4-9003 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kutzner, Jürgen A1 - Zimpfer, Joachim A1 - Wüstenberg, Hermann T1 - Parameterwahl bei der numerischen Ultraschall-Holographie T2 - Europäische Tagung für Zerstörungsfreie Materialprüfung CY - Mainz, Deutschland DA - 1978-04-24 PY - 1978 VL - 2 SP - 517 EP - 522 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung CY - Berlin AN - OPUS4-8987 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nabel, Eberhard A1 - Mundry, Eberhard T1 - Versuche zur Deutung von Ultraschallechos durch Entfaltung T2 - Europäische Tagung für Zerstörungsfreie Materialprüfung CY - Mainz, Deutschland DA - 1978-04-24 PY - 1978 VL - 1 SP - 123 EP - 129 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung CY - Berlin AN - OPUS4-8990 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Römer, Manfred A1 - Just, Tilman A1 - Matthies, Klaus A1 - Kuhlow, Berndt A1 - Neumann, Eberhard T1 - Erfahrungen bei der Ultraschallprüfung ebener und gekrümmter austenitischer Bauteile T2 - Europäische Tagung für Zerstörungsfreie Materialprüfung CY - Mainz, Deutschland DA - 1978-04-24 PY - 1978 VL - 2 SP - 361 EP - 370 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung CY - Berlin AN - OPUS4-8993 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Winter, R. A1 - Engl, G. A1 - Wüstenberg, Hermann T1 - Vom Auffinden zum Bewerten von Ultraschallanzeigen bei automatischen, wiederkehrenden Prüfungen an nuklearen Komponenten T2 - Europäische Tagung für Zerstörungsfreie Materialprüfung CY - Mainz, Deutschland DA - 1978-04-24 PY - 1978 VL - 3 SP - 739 EP - 746 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung CY - Berlin AN - OPUS4-8994 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wittig, Günther A1 - Grigulewitsch, Wolfgang T1 - Untersuchungen zur Anwendung des Impuls-Wirbelstrom-Verfahrens an Prüfobjekten mit größeren Dicken T2 - Europäische Tagung für Zerstörungsfreie Materialprüfung CY - Mainz, Deutschland DA - 1978-04-24 PY - 1978 VL - 1 SP - 165 EP - 172 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung CY - Berlin AN - OPUS4-8995 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Veith, Helmut T1 - On the Influence of Temperature and Frequency on Fatigue Softening of Structural Steels T2 - 5th International Conference on the Strength of Metals and Alloys CY - Aachen, Germany DA - 1979-08-27 PY - 1979 VL - 5 SP - 1151 EP - 1156 CY - Metals Park, Ohio AN - OPUS4-9047 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaenicke, Bernd A1 - Helms, Rolf A1 - Florian, Wolfgang A1 - Lipp, H. A1 - Seidl, W. A1 - Kaiser, B. T1 - Untersuchungen zur Zeit- und Kurzzeitschwingfestigkeit von St E 47 und St E 70 im geschweißten und ungeschweißten Zustand T2 - 5. Sitzung des Arbeitskreises "Betriebsfestigkeit" CY - Stuttgart, Deutschland DA - 1979-10-08 PY - 1979 VL - 5 SP - 597 EP - 619 PB - DVM CY - Stuttgart AN - OPUS4-9050 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weise, Hans-Peter A1 - Jost, Peter A1 - Freundt, Wolfgang T1 - Absolute Photonenausbeuten technischer Röntgenanlagen - Vergleich zwischen Theorie und Messung T2 - Europäische Tagung für Zerstörungsfreie Materialprüfung CY - Mainz, Deutschland DA - 1978-04-24 PY - 1978 VL - 3 SP - 63/553 EP - 63/564 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung CY - Berlin AN - OPUS4-9012 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klingenfuß, Heino T1 - Vermeidbare Fehler bei Klebverbindungen PY - 1978 SP - 45 EP - 56 PB - Ingenieur Digest Verl. CY - Wiesbaden AN - OPUS4-9014 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Klingenfuß, Heino T1 - Vermeidung von Fehlern beim Kleben von Metallen PY - 1978 VL - 17 IS - 12 SP - 49 EP - 51 PB - KDT-Verl. CY - Berlin AN - OPUS4-9015 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Becker, Gerhard Wilhelm T1 - Technischer Fortschritt durch Materialprüfung PY - 1979 SP - 131 EP - 137 CY - Berlin AN - OPUS4-9038 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Aurich, Dietmar A1 - Erbe, H. H. A1 - Helms, Rolf A1 - Veith, Helmut A1 - Ziebs, Josef T1 - The Influence of the Stress State on Fracture Toughness - Further Results T2 - 5th International Conference on Structural Mechanics in Reactor Technology (SMiRT) CY - Berlin, Germany DA - 1979-08-13 PY - 1979 IS - G2-3 SP - 1 EP - 8 PB - North-Holland CY - Amsterdam AN - OPUS4-9045 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krause, Hans-Joachim T1 - Einfluß von veränderten Einstellbedingungen, Düsen, Düsenstellungen auf die Schnittgüte bei simulierten Brennschneidmaschineneigenschaften und verschiedenen Brenngasen T2 - Bericht über die Schulungstagung der Beratungsingenieure der BEFA CY - Bad Godesberg, Deutschland DA - 1978-04-18 PY - 1978 VL - 29 SP - 121 EP - 134 PB - Beratungsstelle für Autogentechnik CY - Hürth AN - OPUS4-9027 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schönherr, Wolfgang A1 - Wilken, Klaus T1 - Review of Service Failures T2 - 3rd International Symposium of the Japan Welding Society CY - Tokyo, Japan DA - 1978-09-26 PY - 1978 VL - 1 IS - 3JWS-III SP - 35 EP - 53 CY - Tokyo, Japan AN - OPUS4-9033 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Richter, Harry A1 - Schimmelwitz, Peter T1 - An efficiency test on methods for water proofing of masonry T2 - Atti del Convegno presso la Fondazione Cini CY - Venice, Italy DA - 1979-10-22 PY - 1979 SP - 355 EP - 361 PB - Tipo-lit. Armena CY - Venezia AN - OPUS4-9076 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schickert, Gerald T1 - Mehraxiale Betonfestigkeit T2 - Mehraxiale Werkstoffbeanspruchung in Theorie und Praxis CY - Düsseldorf, Deutschland DA - 1979-03-22 PY - 1979 SP - 1 EP - 16 CY - Düsseldorf AN - OPUS4-9077 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brandes, Klaus T1 - A boundary method to solve mixed boundary value problems by consistent weighting to the different boundary conditions T2 - 5th International Conference on Structural Mechanics in Reactor Technology (SMiRT) CY - Berlin, Germany DA - 1979-08-13 PY - 1979 IS - M6-2 SP - 1 EP - 8 PB - North-Holland CY - Amsterdam AN - OPUS4-9078 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brandes, Klaus A1 - Limberger, Ernst A1 - Herter, Jürgen T1 - Experimental Investigation of Reinforced Concrete Behaviour due to Impact Load T2 - 5th International Conference on Structural Mechanics in Reactor Technology (SMiRT) CY - Berlin, Germany DA - 1979-08-13 PY - 1979 IS - J7-3 SP - 1 EP - 8 PB - North-Holland CY - Amsterdam AN - OPUS4-9079 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzlöhner, Ulrich T1 - Anwendung der Methode der finiten Elemente auf Sand PY - 1979 SP - 55 EP - 76 PB - Deutsche Gesellschaft für Erd- und Grundbau e.V. CY - Essen AN - OPUS4-9082 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzlöhner, Ulrich T1 - The Use of an Equivalent Homogeneous Half-Space in Soil-Structure Interaction Analyses T2 - 5th International Conference on Structural Mechanics in Reactor Technology (SMiRT) CY - Berlin, Germany DA - 1979-08-13 PY - 1979 IS - M10-3 SP - 1 EP - 8 PB - North-Holland CY - Amsterdam AN - OPUS4-9083 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzlöhner, Ulrich T1 - Einfluß der Gleisbettung auf das dynamische Verhalten des Fahrwegs - Theoretische Methoden und Versuche T2 - Fachseminar "Spurgeführter Fernverkehr" CY - Augsburg, Deutschland DA - 1979-05-01 PY - 1979 SP - 263 EP - 278 AN - OPUS4-9084 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzlöhner, Ulrich T1 - Verifizierung/Identifizierung im Bereich Untergrund Rad/Schiene T2 - Fachseminar "Spurgeführter Fernverkehr" CY - Augsburg, Deutschland DA - 1979-05-01 PY - 1979 SP - 176 EP - 185 AN - OPUS4-9085 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Deppe, Hans-Joachim T1 - Brett und Platte - Zur Substitution von Massivholz durch Holzspanwerkstoffe (OSB-Technik) PY - 1979 IS - 12 SP - 20 EP - 24 AN - OPUS4-9139 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Buchhardt, Frank A1 - Brandl, P. T1 - A realistic structural analysis of the integrity of the liner of reinforced and prestressed concrete containments T2 - 5th International Conference on Structural Mechanics in Reactor Technology (SMiRT) CY - Berlin, Germany DA - 1979-08-13 PY - 1979 IS - J6-3 SP - 1 EP - 8 PB - North-Holland CY - Amsterdam AN - OPUS4-9065 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ziegler, Kurt T1 - Ispitivanje eksploziva i inicirajucih sredstava u saveznom zavOdu za ispitivanie materijala (SAM) u saveznoj republici njemackoj PY - 1979 VL - 2 SP - 19 EP - 27 AN - OPUS4-9126 LA - srp AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Trubiroha, Peter A1 - Pastuska, Gerhard T1 - Der Einfluß der Lufttemperatur und Luftfeuchte auf Bewitterungsergebnisse T2 - 11. Donauländergespräch über die Natürliche und Künstliche Alterung von Kunststoffen CY - Dubrovnik, Kroatien DA - 1978-10-02 PY - 1979 SP - 10 EP - 12 CY - Wien AN - OPUS4-9094 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Matthees, Wolfgang T1 - Some Considerations on the Dynamic Structure-Soil-Structure Interaction Analysis T2 - 5th International Conference on Structural Mechanics in Reactor Technology (SMiRT) CY - Berlin, Germany DA - 1979-08-13 PY - 1979 IS - M10-3a SP - 1(?) EP - 7(?) PB - North-Holland CY - Amsterdam AN - OPUS4-9067 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gierloff, M. T1 - Kunststoff-Dispersionen auf der Basis von Acrylsäureestern als Betonzusatzstoff PY - 1979 VL - 84 SP - 3 EP - 4 PB - Schück CY - Rüschlikon AN - OPUS4-9070 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hundt, Jürgen T1 - Heat and Moisture Transfer in Concrete under the Influence of Temperature (als deutsche Fassung: Wärme- und Feuchtigkeitstransport in Beton unter Temperatureinwirkung) T2 - 5th International Conference on Structural Mechanics in Reactor Technology (SMiRT) CY - Berlin, Deutschland DA - 1979-08-13 PY - 1979 IS - H1-3 SP - 1 EP - 8 PB - North-Holland CY - Amsterdam AN - OPUS4-9072 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heidt, Heinrich T1 - Auswertung von Durchstrahlungsaufnahmen T2 - "Zerstörungsfreie Werkstoffprüfung" CY - Saarbrücken, Deutschland DA - 1979-11-29 PY - 1979 VL - 54-2 SP - 1 EP - 19(?) AN - OPUS4-9180 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heidt, Heinrich A1 - Mundry, Eberhard T1 - "Klassische" Methoden der zerstörungsfreien Materialprüfung T2 - Laser-Meßtechnik 1979 CY - Ostfildern, Deutschland DA - 1979-10-29 PY - 1979 SP - 1 EP - 16 PB - Techn. Akad. Esslingen CY - Ostfildern AN - OPUS4-9181 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heidt, Heinrich A1 - Mundry, Eberhard A1 - Schnitger, Dierk T1 - Einige neuere Entwicklungen in der Radiographie T2 - 1. Najnovejsi dosezki na podrocju preiskav materiala brez porusitve CY - Krsko, Jugoslawien DA - 1979-09-05 PY - 1979 SP - 2 EP - 16 CY - Krsko AN - OPUS4-9182 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heidt, Heinrich A1 - Weise, Hans-Peter A1 - Schnitger, Dierk T1 - Determination of instrument properties of X-ray installations as a contribution to the radiography objectification T2 - 9th World Conference on Nondestructive Testing CY - Melbourne, Australia DA - 1979-11-19 PY - 1979 IS - 4C.1 SP - 1 EP - 7(?) CY - Cannes AN - OPUS4-9184 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Eberhard A1 - Hecht, A. A1 - Thiel, R. A1 - Nabel, Eberhard A1 - Mundry, Eberhard T1 - Determination of the grain size of austenitic sheet by ultrasonic backscattering during the rolling process T2 - 9th World Conference on Nondestructive Testing CY - Melbourne, Australia DA - 1979-11-19 PY - 1979 SP - 1 EP - 7(?) CY - Cannes AN - OPUS4-9185 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wüstenberg, Hermann A1 - Erhard, Anton A1 - Mundry, Eberhard A1 - Schulz, Eckhard T1 - Improved Techniques for the Ultrasonic Inspection of Welds T2 - 9th World Conference on Nondestructive Testing CY - Melbourne, Australia DA - 1979-11-19 PY - 1979 SP - 1(?) EP - 10(?) CY - Cannes AN - OPUS4-9196 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weise, Hans-Peter A1 - Jost, Peter A1 - Santer, E. A1 - Wieters, C. U. T1 - High Energy Bremsstrahlung Albedo for Ordinary Concrete and Brick PY - 1979 VL - 29 SP - 3 EP - 5 PB - European Shielding Information Service CY - Ispra AN - OPUS4-9204 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bathke, Werner A1 - Schlecker, H. T1 - Löten unter Schwerelosigkeit im Spacelab-Nutzungsprogramm und im Vorprogramm TEXUS II PY - 1979 SP - 287 EP - 294 CY - Köln AN - OPUS4-9206 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bathke, Werner A1 - Philippovich, N. A1 - Stickler, R. A1 - Frieler, K. ED - Faust, D. T1 - Brazing of capillary gaps under microgravity - sounding rocket project TEXUS II PY - 1979 SP - 1 EP - 38 PB - Deutsche Forschungs- u. Versuchsanstalt für Luft- und Raumfahrt e.V. CY - Köln AN - OPUS4-9208 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Barthelmeß, Helmut T1 - Rules and Principles of Thesaurus Work in the Study Group - "Thesaurus and Exchange of Abstracts" PY - 1979 IS - S6-TEA-TG-19-75 SP - 1 EP - 4 CY - London AN - OPUS4-9210 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schönherr, Wolfgang T1 - Judging the Brittle Fracture Tendency of Welded Structures with a Temperature Difference Method Corroborated by Analyses of Cases of Failure T2 - Practical Applications of fracture mechanics to the prevention of failure of welded structures CY - Bratislava, Slovakia DA - 1979-07-10 PY - 1979 SP - 305 EP - 312 CY - Lausanne AN - OPUS4-9224 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mundry, Eberhard T1 - Status and Trends of Non-Destructive Testing (NDT) in the Federal Republic of Germany T2 - Modern Technology in Non-Destructive Testing CY - Singapore DA - 1979-11-27 PY - 1979 SP - 1 EP - 32 CY - Singapore AN - OPUS4-9170 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mundry, Eberhard A1 - Wittig, Günther A1 - Stadthaus, Meinhard T1 - Electric and Magnetic Methods on NDT T2 - Modern Technology in Non-Destructive Testing CY - Singapore DA - 1979-11-27 PY - 1979 SP - 1 EP - 14 CY - Singapore AN - OPUS4-9171 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Eberhard A1 - Römer, Manfred A1 - Schenk, R. A1 - Nabel, Eberhard T1 - Status of Ultrasonic Testing Techniques for Austenitic Coarse Grained Weld Joints T2 - 9th World Conference on Nondestructive Testing CY - Melbourne, Australia DA - 1979-11-19 PY - 1979 SP - 1(?) EP - 13(?) CY - Cannes AN - OPUS4-9186 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schnitger, Dierk A1 - Heidt, Heinrich T1 - Actual situation of standardization in the field of radiation methods and radiation protection in the Federal Republic of Germany T2 - 9th World Conference on Nondestructive Testing CY - Melbourne, Australia DA - 1979-11-19 PY - 1979 IS - 6.4 SP - 1 EP - 7(?) CY - Cannes AN - OPUS4-9188 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schnitger, Dierk A1 - Mundry, Eberhard T1 - Electron Radiography of Watermarks T2 - 9th World Conference on Nondestructive Testing CY - Melbourne, Australia DA - 1979-11-19 PY - 1979 IS - 4A.26 SP - 1(?) EP - 8(?) CY - Cannes AN - OPUS4-9189 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wüstenberg, Hermann A1 - Mundry, Eberhard A1 - Möhrle, Walter A1 - Wegner, W. T1 - Experiences with the Use of Electrodynamic Microphones for the Probe Characterization T2 - 9th World Conference on Nondestructive Testing CY - Melbourne, Australia DA - 1979-11-19 PY - 1979 SP - 1(?) EP - 13(?) CY - Cannes AN - OPUS4-9195 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Döring, Günter T1 - Technische Arbeiten zur Herstellung der DIN-Farbenkarte mit glänzenden Mustern PY - 1979 IS - 12 SP - 10 EP - 15 PB - Verl. Farbe + Design CY - Gaildorf AN - OPUS4-9163 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schönherr, Wolfgang T1 - Hochfeste Feinkornbaustähle für den Stahlbau, DASt-Richtlinie 011 - Verarbeitung durch Schweißen PY - 1979 VL - 11 IS - 7 SP - 29 EP - 36 CY - Köln AN - OPUS4-9226 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Schönherr, Wolfgang T1 - Metallurgical and Constructional Measures for the Prevention of Lamellar Tearing in Welded Structures PY - 1979 IS - IX-1142-79 SP - 1 EP - 11 PB - International Institute of Welding CY - Paris AN - OPUS4-9227 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Findeisen, Dietmar T1 - Berechnung transienter Schwingungen bei stoßartiger Einwirkung unter Anwendung linearer Integraloperatoren PY - 1979 VL - 45 IS - 5 SP - 137 EP - 152 PB - VDI-Verl. CY - Düsseldorf AN - OPUS4-9234 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tengicki, Hanns T1 - Multiplot Macros PY - 1980 VL - 2 IS - 2 SP - 7 PB - Nicolet Instrument Corp. CY - Madison, WI, USA AN - OPUS4-9320 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Helms, Rolf T1 - Mechanisches Verhalten und Bruch technischer Werkstoffe; eine allgemeine Einführung unter Berücksichtigung von Implantatbrüchen PY - 1980 IS - 47-71 SP - 23 EP - 46 CY - Berlin AN - OPUS4-9251 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Naseband, Klaus A1 - Ziebs, Josef T1 - Schadensanalyse an Implantaten; Bedeutung, Methodik, Beispiele aus der Praxis PY - 1980 IS - 47-71 CY - Berlin AN - OPUS4-9255 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Aurich, Dietmar A1 - Wobst, Klaus A1 - Ziebs, Josef A1 - Schönherr, Wolfgang A1 - Florian, Wolfgang A1 - Wilken, Klaus A1 - Soete, W. A1 - Vinkier, A. A1 - Denys, R. A1 - Hagedorn, K. E. T1 - Untersuchungen zum Problem der Spannungsarmglühgrenze PY - 1980 SP - 69 EP - 76 PB - Technische Vereinigung der Grosskraftwerksbetreiber CY - Essen AN - OPUS4-9245 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fuhrmann, Günter A1 - Meyer, H. T1 - Agrément und Zulassung PY - 1980 VL - 2 SP - 1 EP - 2 CY - Paris AN - OPUS4-9278 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niesel, Konrad T1 - Kriterien für das Verwitterungsverhalten von Werkstein unter Berücksichtigung von Materialkennwerten - Derzeitiger Stand der Untersuchungen T2 - Sitzung des Arbeitskreises Naturwissenschaftliche Forschung an Kunstgütern aus Stein CY - München, Deutschland DA - 1980-03-06 PY - 1980 SP - 13 EP - 34 CY - Erlangen AN - OPUS4-9281 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schickert, Gerald T1 - Results of combined non-destructive tests on concrete cubes with particular analysis of the influence of some basic parameters T2 - Meeting of Rilem CY - Sinaia, Romania DA - 1980-05-01 PY - 1980 VL - 3 SP - 1(?) EP - 18(?) AN - OPUS4-9283 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rückward, Werner T1 - Luftschalldämmung offenporiger Materialien T2 - 10th International Congress on Accoustics CY - Sydney, Australien DA - 1980-07-09 PY - 1980 VL - 3 IS - Section E-13.7 SP - 1 PB - Adept CY - Bankstown AN - OPUS4-9296 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rückward, Werner T1 - Einführung in die Arbeit des Laboratoriums für Schallschutz, Erschütterungsschutz T2 - Tagung Maschinengeräusche und Schwingungen PY - 1980 SP - 1(?) EP - 16(?) PB - Gesellschaft für Fertigungstechnik AN - OPUS4-9297 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sickfeld, Jürgen T1 - Innenbeschichtungen für Behälter zur Lagerung brennbarer Flüssigkeiten - Aktuelle Anforderungen und Entwicklungstendenzen T2 - 15. FATIPEC-Kongress CY - Amsterdam, Niederlande DA - 1980-06-08 PY - 1980 VL - 2 SP - 28 EP - 44 CY - [Amsterdam] AN - OPUS4-9304 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz-Forberg, Bernd T1 - Tankcontainer in a Fire Accident T2 - 6th International Symposium on the Transport of Dangerous Goods by Sea and Inland Waterways CY - Tokyo, Japan DA - 1980-10-13 PY - 1980 VL - 6 IS - Paper A 3 SP - 47 EP - 61 CY - Hamburg AN - OPUS4-9256 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz-Forberg, Bernd T1 - Reciprocal Acceptance of Tank Containers T2 - 3rd International Conference and Exhibition on the Marine Transportation, Handling and Storage of Bulk Chemicals (MariChem 80) CY - London, England, UK DA - 1980-10-21 PY - 1980 VL - 80 IS - Paper 3.1 SP - 3 EP - 7 CY - Rickmansworth, Herts., England AN - OPUS4-9257 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Löschau, G. A1 - Reise, W. T1 - Meßverfahren für Standfestigkeitsuntersuchungen am realen Lagerstapel PY - 1980 VL - 31 IS - 9 SP - 61 EP - 65 PB - Keppler CY - Heusenstamm AN - OPUS4-9315 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Paatsch, Wolfgang T1 - Inhibition of localized corrosion by phosphoric acid derivatives T2 - 5th European Symposium on Corrosion Inhibitors CY - Ferrara, Italy DA - 1980-09-15 PY - 1980 N1 - Serientitel: Manifestation of the European Federation of Corrosion – Series title: Manifestation of the European Federation of Corrosion IS - 107 SP - 109 EP - 121 CY - Ferrara AN - OPUS4-9268 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Plieth, W. A1 - Höpfner, Wolfgang T1 - Spectroscopic Studies of Electrochemically Grown Oxide Films T2 - 8th International Vacuum Congress (IVC) CY - Cannes, France DA - 1980-09-22 PY - 1980 VL - 8 SP - 453 EP - 456 CY - Oxford AN - OPUS4-9271 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Voigtsberger, Paul T1 - Maßnahmen des primären Explosionsschutzes T2 - Seminar "Raumexplosionen" CY - Wuppertal DA - 1980-09-10 PY - 1980 SP - 1 EP - 25 AN - OPUS4-9336 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Andre, Hilmar A1 - Pfeil, Norbert T1 - Influence of the venting area on the pressure development following explosions of black powder T2 - Tagung der Arbeitsgruppe "Sensitivity and Propagation" der OECD-IGUS CY - Pittsburgh, PA, USA DA - 1980-01-01 PY - 1980 SP - 2 EP - 12 AN - OPUS4-9338 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Treumann, Hartwig T1 - Quantification of the Degree of Hazard of pyrotechnic Compositions T2 - 7th International Pyrotechnics Seminar CY - Vail, CO, USA DA - 1980-07-14 PY - 1980 VL - 7 SP - 878 EP - 897 CY - Denver, Colo. AN - OPUS4-9343 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Treumann, Hartwig A1 - Krüger, Gunhild A1 - Müller, W. A1 - Niems, P. T1 - The explosive properties of binary systems consisting of NaClO3-resp. NaNO3-lactose monohydrate mixtures T2 - Tagung der Arbeitsgruppe "Sensitivity and Propagation" der OECD-IGUS CY - Pittsburgh, PA, USA DA - 1980-01-01 PY - 1980 SP - 2(?) EP - 8(?) AN - OPUS4-9344 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ziegler, Kurt T1 - Über die Beeinflussung des Umsetzungsmechanismus von Slurry-Ladungen durch Sprengschnüre T2 - Gewinnungstechnik in Steinbruch und Tagebau CY - Essen, Deutschland DA - 1980-02-28 PY - 1980 SP - 1 EP - 11 CY - Essen AN - OPUS4-9345 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erhard, Anton A1 - Wüstenberg, Hermann A1 - Mundry, Eberhard T1 - Nachweis von oberflächennahen Rissen mit Kriechwellen T2 - 2nd FASE CY - Warszawa, Poland DA - 1978-09-18 PY - 1978 SP - 1 EP - 5 CY - Beograd AN - OPUS4-9411 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erhard, Anton A1 - Kutzner, Jürgen A1 - Wüstenberg, Hermann T1 - Verallgemeinerte Punktrichtwirkungen - Übergang Nahfeld-Fernfeld T2 - Internationales Symposium ; International symposium CY - Saarbrücken, Deutschland DA - 1979-09-17 PY - 1980 SP - 75 EP - 88 CY - Berlin AN - OPUS4-9412 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hecht, A. A1 - Neumann, Eberhard A1 - Mundry, Eberhard A1 - Thiel, R. T1 - Probleme der Korngrößenbestimmung an austenitischen Bändern mit Hilfe der Ultraschallrückstreuung T2 - Internationales Symposium ; International symposium CY - Saarbrücken, Deutschland DA - 1979-09-17 PY - 1980 SP - 221 EP - 228 CY - Berlin AN - OPUS4-9413 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heidt, Heinrich T1 - Neue Entwicklungen in der Durchstrahlungsprüfung T2 - Aktuelle Fragen der Durchstrahlungsprüfung und des StrahlenschutzesVorträge des Seminars CY - Remscheid, Deutschland DA - 1980-10-31 PY - 1980 SP - 41 EP - 48 CY - Berlin AN - OPUS4-9414 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hattwig, Martin T1 - Investigations on the recoil of vented vessels T2 - 3rd International Symposium on Loss Prevention and Safety Promotion in the Process Industrie CY - Basel, Switzerland DA - 1980-09-15 PY - 1980 N1 - Serientitel: Event / European Federation of Chemical Engineering – Series title: Event / European Federation of Chemical Engineering IS - 228 SP - 968 EP - 978 CY - Basel AN - OPUS4-9326 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Leuschke, Günter T1 - Induction Times of Dust Deposits stored at and above Self-Ignition Temperatures T2 - 3rd International Symposium on Loss Prevention and Safety Promotion in the Process Industrie CY - Basel, Switzerland DA - 1980-09-15 PY - 1980 N1 - Serientitel: Event / European Federation of Chemical Engineering – Series title: Event / European Federation of Chemical Engineering IS - 228 SP - 647 EP - 656 CY - Basel AN - OPUS4-9329 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kirschke, Kurt T1 - Flow Behaviour of Lubricants in Service Conditions T2 - 8th International Congress on Rheology (ICR) CY - Naples, Italy DA - 1980-09-01 PY - 1980 VL - 8 SP - 601 EP - 606 CY - London AN - OPUS4-9387 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Döring, Günter T1 - Vergleich von Farbensammlungen mit Farbenkarten aus Farbsystemen PY - 1980 VL - 15-16 SP - 2 EP - 12 PB - Verl. Farbe + Design CY - Gaildorf AN - OPUS4-9394 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gundlach, Dietrich ED - Krochmann, J. T1 - Standardization of Daylight and it's Application for Colorimetry T2 - Symposium on Daylight CY - Berlin, Germany DA - 1980-07-09 PY - 1980 SP - 59 EP - 68 CY - Berlin (West) AN - OPUS4-9395 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krochmann, J. A1 - Terstiege, Heinz T1 - Retroreflektierende Verkehrszeichen PY - 1980 IS - 1 SP - 7 EP - 10 PB - 3M Deutschland CY - Neuss AN - OPUS4-9397 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Richter, Kerstin T1 - CIE 1976 color spaces and proposals for modification PY - 1980 VL - 3 IS - 5 SP - 214 EP - 217 PB - Color Science Association of Japan CY - Tokyo AN - OPUS4-9401 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Richter, Kerstin T1 - Farben und ihre Wiedergabe in der Fotografie PY - 1980 VL - 15-16 SP - 42 EP - 49 PB - Verl. Farbe + Design CY - Gaildorf AN - OPUS4-9402 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Czichos, Horst T1 - Importance of Properties of Solids to Friction and Wear Behaviour T2 - International Conference in Tribology in the 80's CY - Cleveland, OH, USA DA - 1983-04-18 PY - 1984 N1 - Serientitel: NASA Conference Publication – Series title: NASA Conference Publication VL - 2300 IS - 2300,1 SP - 71 EP - 106 CY - Washington AN - OPUS4-9505 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heumos, K. A1 - Kowalewsky, Helmut A1 - Weise, Hans-Peter T1 - Investigation of Gas Leakage from Sealing Constructions at Containments for Radioactive Materials T2 - 6th International Symposium on Packaging and Transportation of Radioactive Materials CY - Berlin, Germany DA - 1980-11-10 PY - 1980 VL - 6 IS - 4 SP - 210 EP - 213 CY - Springfield, Va. AN - OPUS4-9429 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kowalewsky, Helmut T1 - Leak Testing and Activity Leakage Rate Evaluation - Practical Experiences, First Approaches to some Systemization and Outstanding Problems T2 - 6th International Symposium on Packaging and Transportation of Radioactive Materials CY - Berlin, Germany DA - 1980-11-10 PY - 1980 VL - 6 IS - 4 SP - 196 EP - 201 CY - Springfield, Va. AN - OPUS4-9430 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thomas, M. A1 - Wittig, Günther A1 - Grigulewitsch, Wolfgang A1 - Maser, Dieter T1 - Signalauswertung beim Impulswirbelstromverfahren T2 - Internationales Symposium ; International symposium CY - Saarbrücken, Deutschland DA - 1979-09-17 PY - 1980 SP - 119 EP - 128 CY - Berlin AN - OPUS4-9421 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wüstenberg, Hermann A1 - Erhard, Anton A1 - Zimpfer, Joachim A1 - Kutzner, Jürgen T1 - Quasi-Flächenholographie, ein Hilfsmittel zur Fehlergrößenbestimmung T2 - Internationales Symposium ; International symposium CY - Saarbrücken, Deutschland DA - 1979-09-17 PY - 1980 SP - 293 EP - 306 CY - Berlin AN - OPUS4-9423 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wüstenberg, Hermann A1 - Erhard, Anton A1 - Kutzner, Jürgen ED - Berger, H. T1 - Detection and analysis for near surface-cracks by ultrasound T2 - 1st International Symposium on Ultrasonic Materials Characterization CY - Gaithersburg, MD, USA DA - 1978-06-07 PY - 1980 N1 - Serientitel: National Bureau of Standards. Special Publication – Series title: National Bureau of Standards. Special Publication IS - 596 SP - 1 EP - 16(?) CY - Washington AN - OPUS4-9425 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weise, Hans-Peter A1 - Jost, Peter A1 - Freundt, Wolfgang T1 - Spectra, Differential Albedo and Shielding Data for Bremsstrahlung Scattered from Common Shielding Materials T2 - 5th International Radiation Protection Association = Association internationale de radioprotection CY - Jerusalem, Israel DA - 1980-03-09 PY - 1980 VL - 5 SP - 327 EP - 330 CY - Oxford AN - OPUS4-9440 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Krause, Hans-Joachim T1 - Assessment of BAM feed back system PY - 1980 IS - III-642-80 SP - 1 EP - 15 PB - International Institute of Welding CY - Paris AN - OPUS4-9445 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Czichos, Horst T1 - Trockenreibung Metall-Metal - Stand der wissenschaftlichen Forschung PY - 1971 SP - 153 EP - 184 CY - Lausanne AN - OPUS4-9471 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Preß, Henning T1 - Neue Erkenntnisse über die Schadstoffbildung beim Schweißen und Schneiden T2 - Kongreß "Verbindungstechnik" CY - Köln, Deutschland DA - 1980-09-08 PY - 1980 SP - 33 EP - 44 PB - Ingenieur Digest Verl.-Ges. CY - Frankfurt am Main AN - OPUS4-9450 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Preß, Henning A1 - Florian, Wolfgang T1 - Contribution on the Formation of Toxic substances in gas shielded arc welding and determination of Requiered Exhaustion Capacity T2 - Colloque sur Soudage et Santé CY - Estoril, Portugal DA - 1980-07-08 PY - 1980 SP - 1 EP - 8 PB - Instituto de Soldadura CY - Lisboa AN - OPUS4-9451 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wilken, Klaus T1 - Maßnahmen zum Vermeiden von Heißrissen in höherlegierten Stählen und Sonderwerkstoffen PY - 1980 SP - 63 EP - 69 PB - Technische Vereinigung der Grosskraftwerksbetreiber CY - Essen AN - OPUS4-9454 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Czichos, Horst T1 - Systems Approach to Wear Problems PY - 1980 SP - 17 EP - 34 PB - American Soc. of Mechanical Engineers CY - New York AN - OPUS4-9485 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Czichos, Horst ED - Kozma, M. T1 - Tribology and New Materials T2 - 6th International Congress on Tribology (EUROTRIB) CY - Budapest, Hungary DA - 1993-08-30 PY - 1993 SP - 135 EP - 157 CY - Budapest AN - OPUS4-9557 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lexow, Jürgen A1 - Czichos, Horst T1 - Advanced material technologies - status and development trends PY - 1994 IS - E-ESCWA-NR-1994-8 SP - 5 EP - 48 PB - United Nations CY - New York AN - OPUS4-9558 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Czichos, Horst A1 - Meyer, Katharina A1 - Zschunke, Adolf T1 - Reference materials at BAM - past, present and future developments T2 - Symposium "Reference Materials for Technologies in the New Millenium" CY - Berlin, BAM, Germany DA - 2000-05-22 PY - 2000 SP - 1(?) EP - 7(?) AN - OPUS4-9547 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Czichos, Horst T1 - Advanced materials in tribology T2 - 5th Nordic Symposium on Tribology (NORDTRIB) CY - Helsinki, Finland DA - 1992-06-08 PY - 1992 SP - 5 EP - 35 CY - Lyngby AN - OPUS4-9553 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Czichos, Horst ED - Bartz, Wilfried J. T1 - Grundlagen der Tribologie PY - 1988 VL - 1 SP - 1.1-1-1.1-7 PB - Techn. Akad. Esslingen AN - OPUS4-9528 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Czichos, Horst T1 - Future Developments and Applications of Materials T2 - Conférence à l'occasion de TEC 88 (Technologies et compétitivité) CY - Grenoble, France DA - 1988-10-11 PY - 1988 SP - 1 EP - 27 CY - Grenoble AN - OPUS4-9530 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Czichos, Horst T1 - Materialprüfung - Aufgaben und Tendenzen PY - 1988 IS - 5 SP - 2 PB - GIT-Verl. CY - Darmstadt AN - OPUS4-9531 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Czichos, Horst T1 - Die Bundesanstalt in den Jahren 1992 bis 1996 PY - 1996 SP - 549 EP - 615 PB - Wirtschaftsverlag NW CY - Bremerhaven AN - OPUS4-9539 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Czichos, Horst T1 - Materialien - stoffliche Basis von Technik, Industrie und Wirtschaft PY - 1998 VL - 34 IS - 5 SP - 10 EP - 11 PB - Bayer. Monatsspiegel Adler CY - München AN - OPUS4-9543 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Czichos, Horst ED - Hansen, J. T1 - Systematik tribologischer Prüfungen PY - 1984 SP - 9 EP - 94 PB - DFVLR CY - Köln-Porz AN - OPUS4-9506 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Czichos, Horst T1 - In-situ Investigations of Tribological Processes on Sliding Polymer Interfaces T2 - 3rd International Conference on Solid Lubrication CY - Denver, CO, USA DA - 1984-08-07 PY - 1984 SP - 177 EP - 186 CY - Park Ridge, Ill. AN - OPUS4-9507 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Czichos, Horst ED - Booser, R. T1 - Systems Analysis PY - 1984 SP - p. 645 EP - 661 PB - CRC Press CY - Boca Raton AN - OPUS4-9509 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Czichos, Horst ED - Hansen, J. T1 - Internationale Situation der Tribologie-Forschung PY - 1985 SP - 47 EP - 56 PB - DFVLR CY - Köln-Porz AN - OPUS4-9514 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Czichos, Horst A1 - Habig, Karl-Heinz T1 - Systemtechnik tribologischer Vorgänge T2 - Tribologie in Theorie und Praxis CY - --- DA - 1986-11-06 PY - 1986 SP - 1 EP - 15 CY - Stuttgart AN - OPUS4-9521 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Czichos, Horst ED - Grantze, E. T1 - Materialforschung und Materialprüfung - Bedeutung, Tendenzen, Aufgaben T2 - Materialforschung und Materialprüfung - Bedeutung, Tendenzen, Aufgaben CY - Berlin DA - 1987-08-13 PY - 1987 SP - 3 EP - 24 PB - BAM CY - Berlin AN - OPUS4-9525 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfender, Max T1 - Normung, Dokumentation, Ausbildung, Erfahrungsaustausch, Arbeitsschutz, Organisationen T2 - Zerstörungsfreie Prüfverfahren - Internationale Tagung CY - Brüssel, Belgien DA - 1955-05-23 PY - 1955 VL - 1 IS - Hauptbericht V SP - 1 EP - 11 CY - Berlin AN - OPUS4-9753 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pohl, Heinz T1 - Eine kolorimetrische Eisen-Bestimmung in Hartchrom-Bädern PY - 1954 VL - 6 IS - 9 SP - 129 EP - 130 PB - Hanser CY - München AN - OPUS4-9709 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Elze, Johannes T1 - Über die Wirkung organischer Inhibitoren auf die Auflösung des Eisens in Säuren PY - 1954 VL - 8 IS - 12 SP - 177 EP - 179 PB - Hanser CY - München AN - OPUS4-9711 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rühl, Karl H. A1 - Schwaigerer, S. T1 - Einführung, Grundbegriffe der Festigkeitslehre PY - 1955 VL - 1 IS - Abschnitt 6/I SP - 836 EP - 837 PB - Ernst CY - Berlin ET - 28., neubearb. AN - OPUS4-9768 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Seekamp, Horst A1 - Saenger, T1 - Das Verhalten von Abschlüsstüren zu Aufzugsschächten im Brande PY - 1955 IS - 3 SP - 895 EP - 903 PB - Statistisches Landesamt CY - Stuttgart AN - OPUS4-9769 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Caemmerer, Winfrid T1 - Schallschutz und Wärmeschutz, eine vergleichende Betrachtung PY - 1955 VL - 15 IS - 1 SP - 9 EP - 14 PB - Zorn CY - Eichenberg AN - OPUS4-9771 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Caemmerer, Winfrid T1 - Wirtschaftlicher baulicher Wärmeschutz PY - 1955 VL - 4 SP - 204-206; 208-210; 212, 214 PB - Schroll CY - Wien AN - OPUS4-9772 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Becker, Günther T1 - Erfahrungen und Entwicklungen auf dem Gebiet des Holzschutzes im Hochbau PY - 1954 VL - 56 IS - 18 SP - 1 EP - 8 PB - Bruder-Verl. CY - Karlsruhe AN - OPUS4-9717 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Becker, Günther T1 - Räuber und Parasiten holzzerstörender Insekten in Gebäuden PY - 1954 SP - 76 EP - 86 PB - Parey CY - Berlin AN - OPUS4-9719 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mendrzyk, Hildegard A1 - Riepe, Wilhelm T1 - Beiträge zur Bestimmung der Reinigungswirkung von Waschmitteln PY - 1954 IS - 4 SP - 257 EP - 260 PB - Verl. Neuer Merkur CY - München AN - OPUS4-9725 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Caemmerer, Winfrid T1 - Die hygienische, heizungstechnische und wirtschaftlische Bedeutung des Wärmeschutzes von Wohnhäusern PY - 1956 IS - 7-9 SP - 1 EP - 15 CY - Zürich AN - OPUS4-9849 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Caemmerer, Winfrid T1 - Die Ausbildung des Wärmeschutztes bei massiven Flachdächern PY - 1956 SP - 145 EP - 148 PB - Schmidt CY - Berlin AN - OPUS4-9851 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Caemmerer, Winfrid T1 - Maßnahmen zur Senkung der Heizungskosten von Wohnhäusern PY - 1956 VL - 7 IS - 10 SP - 1(?) EP - 2(?) PB - GG CY - Berlin AN - OPUS4-9852 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Toeldte, W. T1 - Gilbungsskala für weisse Anstriche T2 - Congrés. F.A.T.I.P.E.C. III CY - Spa, Belgien DA - 1955-05-22 PY - 1955 SP - 83 EP - 86 CY - Bruxelles AN - OPUS4-9782 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mendrzyk, Hildegard T1 - Das Wäschereilaboratorium der Bundesanstalt für Materialprüfung PY - 1955 SP - 51 EP - 54 PB - Verl. Neuer Merkur CY - München AN - OPUS4-9784 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schlosser, Franz T1 - Güteanforderungen und Untersuchungsbefunde bei Bitumen-Dach- und Abdichtungspappen PY - 1955 SP - 182 EP - 184 PB - Plaum CY - Halle, S. AN - OPUS4-9785 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfender, Max ED - Pohl, E. T1 - Über das Festigkeitsverhalten metallischer Werkstoffe und Konstruktionsteile PY - 1956 VL - 1-2 SP - 3 EP - 30 PB - Allianz Versicherungs-AG CY - München AN - OPUS4-9832 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Richter, Manfred T1 - Das DIN-Farbsystem als Grundlage für die Festlegung von Farbgrenzen und Farbtoleranzen T2 - Congrés. F.A.T.I.P.E.C. III CY - Spa, Belgien DA - 1955-05-22 PY - 1955 SP - 311 EP - 315 CY - Bruxelles AN - OPUS4-9819 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rühl, Karl H. T1 - Zeit- und Zukunftsfragen der Festigkeitsforschung PY - 1956 IS - 11 SP - 32 EP - 60 PB - Stahlbau-Verl. CY - Köln AN - OPUS4-9842 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rühl, Karl H. A1 - Pagel, H.-J. T1 - Neue Untersuchungen über die Beanspruchungen eines Biegeträgers bei schlagartiger Querbelastung PY - 1956 VL - 2 SP - 202 EP - 209 PB - Extrabuch-Verl CY - Frankfurt, M. AN - OPUS4-9843 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Damaschke, Kurt T1 - Die Bedeutung der Photosynthese für alles Leben auf unserer Erde PY - 1957 PB - Hanseat. Verl. Anst. CY - Hamburg AN - OPUS4-9892 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mendrzyk, Hildegard T1 - Beobachtungen über Aschegehalte nach häufigem Waschen PY - 1957 VL - 10 IS - 8 SP - 546 EP - 550 PB - Verl. Neuer Merkur CY - München AN - OPUS4-9938 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Scheruhn, Willi ED - Stauch, A. ED - Rögnitz, H. T1 - Geräte zur Gasbeschaffung PY - 1957 VL - 1 IS - Abschnitt 7/IV/A SP - 692 EP - 696 PB - Ernst CY - Berlin ET - 5., neu bearb. und erw. AN - OPUS4-9943 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Katz, Walter T1 - Geschwindigkeiten der Korrosionsvorgänge PY - 1957 VL - 11 IS - 5 SP - 145 EP - 155 PB - Hanser CY - München AN - OPUS4-9911 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Charisius, Kurt T1 - Deckenputz an Massivedecken PY - 1957 SP - 97 EP - 102 PB - Schmidt CY - Berlin AN - OPUS4-9915 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Habel, Wolfgang T1 - Selected Examples of Use of Fibre Optic Sensors in Civil Engineering and Geotechnics T2 - International Symposium on Innovation & Sustainability of Structures in Civil Engineering (ISISS´2005) CY - Nanjing, PR China DA - 2005-11-20 KW - Fibre optic sensor KW - Pressure sensor KW - pH value KW - Corrosion KW - Civil engineering KW - Mortar deformation KW - Concrete shrinkage KW - Long-term stability KW - Reliability KW - Data evaluation PY - 2005 VL - 1 SP - 186 EP - 202 CY - Nanjing AN - OPUS4-11772 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hertel, Horst A1 - Plarre, Rüdiger T1 - Incorporating insect behaviour in standard tests of wood preservatives - a possible way to reduce pesticide loadings T2 - 31th Annual Meeting of the International Research Group on Wood Preservation CY - Kona, HI, USA DA - 2000-05-14 KW - Standard test methods KW - Behavior KW - Wood preservatives KW - Hylotrupes bajulus PY - 2000 SP - Paper 20190, 1 EP - 10 PB - International Research Group on Wood Preservation CY - Stockholm AN - OPUS4-11822 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kunze, Ralf A1 - Mielke, Werner A1 - Niebergall, Ute ED - Hodgkinson, J. T1 - Thermoluminescence of PEHD/PP Blends T2 - Polymat '94 CY - London, England, UK DA - 1994-09-19 PY - 1994 SP - 463 EP - 466 PB - Institute of Materials CY - London AN - OPUS4-11799 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stelling, Karen A1 - Lammers, Marco A1 - Schobbert, Helmut T1 - Nd:YAG-Laser-Plasma-Hybridschweißen mit Zusatzwerkstoffen T2 - Innovationsforum Hybridtechnologien - Fügetechnik für die Fertigung der Zukunft CY - Halle (Saale), Deutschland DA - 2004-11-23 KW - Laser KW - Plasma KW - Pulver KW - Hybridschweißen KW - Austenitischer Stahl PY - 2004 SP - 61 EP - 68 CY - Haale, Saale AN - OPUS4-11932 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Osterloh, Kurt T1 - Human perception of images T2 - 5th BAM-DIN-Workshop on Image Technology CY - Berlin, Deutschland DA - 2005-04-18 PY - 2005 UR - http://www.ps.bam.de/info05/OST05.PDF SP - 16 pages PB - BAM CY - Berlin AN - OPUS4-11864 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nitsche, F. A1 - Rödel, Roland T1 - Revised Guideline for the Approval Procedure of Package Designs in Germany T2 - 14th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Berlin, Germany DA - 2004-09-20 KW - Transport Packaging KW - Procedure for Design Approval KW - Procedure for Validation PY - 2004 IS - 235 SP - 1(?) EP - 5(?) PB - BAM CY - Berlin AN - OPUS4-11902 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mellmann, Günter A1 - Meinhold, Uwe A1 - Maultzsch, Matthias T1 - Verbundeigenschaften von Instandsetzungssystemen auf Baukonstruktionen T2 - 15. DGM-Symposium "Verbundwerkstoffe und Werkstoffverbunde" CY - Kassel, Deutschland DA - 2005-04-06 PY - 2005 UR - http://www.dgm.de/download/tg/706/706_116.pdf SP - 577 EP - 582 PB - DGM CY - Kassel AN - OPUS4-11903 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ballheimer, Viktor A1 - Droste, Bernhard A1 - Wieser, Günter A1 - Qiao, Linan T1 - Spent fuel transport associated with other dangerous goods in regular train units - assessment of hypothetical explosion impacts T2 - 14th International Symposium on the Packaging and Transportation of Radioactive Materials, September 20-24, 2004, Berlin CY - Berlin, Germany DA - 2004-09-20 KW - Transport spent fuel cask KW - Accident KW - Blast wave KW - Finite element analysis PY - 2004 IS - 235 SP - 1 EP - 7(?) PB - BAM CY - Berlin AN - OPUS4-11906 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rücker, Werner A1 - Rohrmann, Rolf A1 - Said, Samir T1 - Monitoring and assessment of structures under changed loading conditions T2 - SAMCO Summer Academy 2005 on Structural Assessment, Monitoring and control CY - Zell am See, Austria DA - 2005-09-05 KW - Monitoring KW - Assessment KW - Vibration PY - 2005 SP - 10 pages PB - Samco Network CY - Zell am See AN - OPUS4-11869 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rücker, Werner A1 - Rohrmann, Rolf A1 - Said, Samir T1 - Monitoring, Schadensfrüherkennung und Sensorik für Offshore-Windenergieanlagen T2 - 4. Symposium Offshore-Windenergie Bau- und umwelttechnische Aspekte CY - Hannover, Deutschland DA - 2005-09-27 KW - Monitoring KW - Zustandüberwachung KW - Schadensanalyse KW - Windlasten KW - Dynamik KW - Windenergieanlagen KW - Offshore KW - Bauliche Bewertung PY - 2005 VL - 4 IS - Beitrag 5 SP - 1(?) EP - 12(?) CY - Hannover AN - OPUS4-11871 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Kühn, W. A1 - Korzen, Manfred A1 - Paetsch, O. T1 - Fast data assimilation in fire tests of steel members N2 - This report presents a fast data assimilation method to produce an interpolating time and space temperature distribution for steel members subject to fire testing. The method assimilates collected temperature data into the numerical integration of the heat equation. This physically based method also allows the computation of lateral and axial heat flux into and inside the member. PY - 1998 UR - https://nbn-resolving.org/urn:nbn:de:0297-zib-3766 SN - 0933-7911 IS - SC-98-33 SP - 1 EP - 14 PB - Konrad-Zuse-Zentrum für Informationstechnik Berlin (ZIB) CY - Berlin AN - OPUS4-12019 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Paetsch, O. A1 - Stalling, D. A1 - Korzen, Manfred T1 - Online-Visualisierung von Brandversuchen an Bauteilen N2 - For the evaluation of the fire resistance time of structural elements thermal and mechanical loadings are applied to the specimen. Up to now the monitored data is represented in tabular form and simple plots. In the following a visualization system to show the data in its geometrical context is discussed. T2 - VisEng'97 - Visualisierung im Ingenieurbereich "Pre- und Postprocessing in Strömungs- und Strukturmechanik" CY - Stuttgart, Deutschland DA - 1997-05-06 PY - 1997 UR - http://www.zib.de/visual-publications/sources/src-1997/brandvis.pdf SP - 1 EP - 13 CY - Stuttgart AN - OPUS4-12021 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bock, Hans Michael A1 - Korzen, Manfred T1 - Brandschutztechnische Ertüchtigung von Stahlverbundhohlprofilstützen - Bericht über die "Proving Trials" an einem europäischen Prüfverfahren T2 - Beiträge zum 33. Forschungskolloquium CY - Berlin, BAM, Deutschland DA - 1996-10-10 PY - 1996 VL - 33 SP - 62 EP - 71 PB - Dt. Ausschuss für Stahlbeton im DIN CY - Berlin AN - OPUS4-12023 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Korzen, Manfred A1 - Schriever, Robert A1 - Ziener, Kai-Uwe A1 - Paetsch, O. A1 - Zumbusch, G. W. ED - Ziebst, J. ED - Bessers, J. ED - Frenz, H. T1 - Real-time 3-D visualization of surface temperature fields measured by thermocouples on steel structures in fire engineering T2 - Local strain and temperature measurments in non-uniform fields at elevated temperatures CY - Berlin, Germany DA - 1996-03-14 PY - 1996 SP - 253 EP - 262 PB - Woodhead Publishing Ltd CY - Berlin AN - OPUS4-12024 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pastuska, Gerhard A1 - Just, Ulrich A1 - Trubiroha, Peter T1 - Change of molecular weight distribution (MWD) of PVC by natural and artificial weathering T2 - 26th IUPAC International Symposium on Macromolecules (MACRO) CY - Mainz, Germany DA - 1979-09-17 PY - 1979 SP - 600 EP - 602 CY - Toronto AN - OPUS4-11948 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mielke, Werner ED - Dulog, L. ED - Moeller, E. T1 - Die Anwendung der Schallemissionsanalyse zur Beurteilung der Haftung von Beschichtungen T2 - 19. FATIPEC Kongress CY - Aachen, Deutschland DA - 1988-01-01 PY - 1988 N1 - Serientitel: Congrès. Fédération d'Associations de Techniciens des Industries de Peintures ... – Series title: Congrès. Fédération d'Associations de Techniciens des Industries de Peintures ... VL - 2 IS - 19 SP - 471 EP - 486 CY - Aachen AN - OPUS4-11949 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Friedrich, Jörg Florian A1 - Kühn, Gerhard A1 - Mix, Renate T1 - Tayloring of polymer surfaces with different monotype functional groups of variable density using chemical and plasma chemical processes T2 - 10th Dresden Polymer Discussion: Characterization of Polymer Surfaces and Thin Films CY - Meißen, Germany DA - 2005-04-10 KW - Plasma modification KW - Introduction of functional groups KW - Reactions at polymer surfaces PY - 2005 SP - 34 EP - 49 PB - Leibniz-Institut für Polymerforschung Dresden CY - Meißen AN - OPUS4-11941 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mach, Reinhard A1 - Maneck, Heinz-Eberhard A1 - Röhl-Kuhn, Barbara A1 - Peplinski, Burkhard A1 - Benemann, Sigrid A1 - Strauß, Birgid A1 - Schütz, W. A1 - Kühn, Gerhard A1 - Friedrich, Jörg Florian ED - Pershin, L. T1 - Modification of graphite powders in a thermal RF induction plasma T2 - 17th International Symposium on Plasma Chemistry (ISPC-17) CY - Toronto, Canada DA - 2005-08-07 PY - 2005 SP - 1(?) EP - 6(?) CY - Toronto AN - OPUS4-11942 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Simone A1 - Schulze, Rolf-Dieter A1 - Brademann-Jock, Kerstin A1 - Friedrich, Jörg Florian ED - Pershin, L. T1 - Introduction of irregularities into plasma polymers by radiative and auto-oxidative processes T2 - 17th International Symposium on Plasma Chemistry (ISPC-17) CY - Toronto, Canada DA - 2005-08-07 PY - 2005 SP - 1(?) EP - 6(?) CY - Toronto AN - OPUS4-11943 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Friedrich, Jörg Florian A1 - Kühn, Gerhard A1 - Mix, Renate ED - Pershin, L. T1 - Chemical synthesis at plasma modified polymer surfaces T2 - 17th International Symposium on Plasma Chemistry (ISPC-17) CY - Toronto, Canada DA - 2005-12-07 PY - 2005 SP - 1(?) EP - 6(?) CY - Toronto AN - OPUS4-11944 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - von Woedtke, T. A1 - Abel, P. A1 - Schröder, K. A1 - Schwock, A. A1 - Krüger, Jörg A1 - Kautek, Wolfgang T1 - Biosensor-Membranen mit "Analyt-Fenster" T2 - 8. Internationale Messe mit Kongreß für Sensoren, Meßaufnehmer & Systeme ; 8th International Fair with Congress for Sensors, Transducers & Systems CY - Nürnberg, Deutschland DA - 1997-05-13 PY - 1997 VL - 2 SP - 101 EP - 106 PB - ACS Organisations GmbH CY - Wunstorf AN - OPUS4-11959 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ludwig, Jörg T1 - Rechtliche Rahmenbedingungen-RID, ADR und EG-Richtlinien T2 - BAM/DIN-Gemeinschaftstagung CY - Berlin, Deutschland DA - 2005-01-14 PY - 2005 SP - ohne Seitenzahlen PB - Beuth CY - Berlin AN - OPUS4-11963 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ulrich, Armin T1 - DIN EN 13094 - Tanks für die Beförderung gefährlicher Güter - Metalltanks mit einem Betriebsdruck von höchstens 0,5 bar - Auslegung und Bau T2 - BAM/DIN-Gemeinschaftstagung CY - Berlin, Deutschland DA - 2005-01-14 PY - 2005 SP - ohne Seitenzahlen PB - Beuth CY - Berlin AN - OPUS4-11964 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hinrichs, V. A1 - Leistner, A. A1 - Kalinka, Gerhard A1 - Schulz, Eckhard A1 - Hinrichsen, G. T1 - Viscoelastic properties of the interphase in fibre reinforced polymers - measurement and simulation KW - Polymer KW - Glass fibre KW - Interphase KW - Coating KW - Glass transition KW - Dynamic KW - Viscoelastic PY - 1999 VL - 6 IS - 2 SP - 93 EP - 101 PB - North-Holland CY - New York, NY AN - OPUS4-12003 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wäsche, Rolf A1 - Klaffke, Dieter A1 - Woydt, Mathias A1 - Dörfel, Ilona T1 - Interface formation by tribo-oxidation in SiC based ceramics T2 - AIST-BAM Symposium on Materials Surface Technology in Twin Institute Programme CY - Tsukuba, Japan DA - 2003-02-18 PY - 2003 SP - 1 EP - 4 AN - OPUS4-12051 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Böcker, Wolfgang D. G. A1 - Bücker, Michael A1 - Reinsch, Stefan A1 - Unger, Brita T1 - Abschlussbericht zum Vorhaben Verbundwerkstoff - Mineralisiertes Holz - FKZ: 033 9829 - Förderschwerpunkt "Integrierter Umweltschutz im Bereich der Holzwirtschaft" des Bundesministeriums für Bildung, Wissenschaft, Forschung und Technologie, BMBF - Projektlaufzeit: 1.10.2000-30.9.2003 KW - Mineralisiertes Holz KW - Sol-Gel KW - Holz KW - Vakuumtränkung KW - Holzschutz KW - Biozide PY - 2004 SP - 1 EP - 94 CY - Berlin AN - OPUS4-12055 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Yarim, Rasim A1 - Wäsche, Rolf A1 - Woydt, Mathias A1 - Dörfel, Ilona T1 - Analysis of wear protecting oxide layers in the system SiC-TiC-TiB2 formed in-situ at high temperatures T2 - AIST-BAM Symposium on Materials Surface Technology in Twin Institute Programme CY - Tsukuba, Japan DA - 2003-02-18 PY - 2003 SP - 5 EP - 8 AN - OPUS4-12057 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Boeck, T. A1 - Schmidt, K. A1 - Lorenz, M. A1 - Rosenfeld, A. A1 - Rudolph, Pascale A1 - Krüger, Jörg A1 - Kautek, Wolfgang ED - Gobrecht, J. T1 - Ultra-short pulse laser seeding techniques for silicon crystallite growth on amorphous substrates T2 - QUANTSOL 99 CY - Wildhaus, Switzerland DA - 1999-03-14 PY - 1999 SP - 1(?) EP - 3(?) AN - OPUS4-12041 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard A1 - Müller, Karsten A1 - Minack, Mathias T1 - The New BAM 200 Ton Drop Test Facility - Construction and Operation Experiences T2 - 7th International Conference on Radioactive Materials Transport - 2005 CY - Cambridge, England, UK DA - 2005-09-27 KW - Drop test KW - Drop tower KW - Radioactive material transport packages PY - 2005 SP - 6 pages PB - The Institution of Nuclear Engineers (INucE) CY - Cambridge AN - OPUS4-12044 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Korzen, Manfred A1 - Haupt, P. ED - Cailletaud, G. ED - Delobelle, P. T1 - A new constitutive model for the phenomenological representation of rate-dependent and rate-independent material behavior T2 - International Seminar on the Inelastic Behaviour of Solids CY - Besançon, France DA - 1988-08-30 PY - 1988 N1 - Serientitel: Proceedings of the International MECAMAT Seminar – Series title: Proceedings of the International MECAMAT Seminar IS - 3 SP - I-41-I-52 PB - MECAMAT CY - Besançon AN - OPUS4-12080 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schönhals, Andreas A1 - Goering, Harald A1 - Schick, C. T1 - Poly(methyl phenyl siloxane) in Random Nanoporous Glasses - Comparison of coated and uncoated confining surfaces T2 - Poly(methyl phenyl siloxane) in Random Nanoporous Glasses: Comparison of coated and uncoated confining surfaces CY - Boston, MA, USA DA - 2006-11-28 PY - 2006 VL - 899E SP - 0899-N09-05.1-0899-N09-05.6 CY - Boston AN - OPUS4-12214 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rücker, Werner A1 - Rohrmann, Rolf A1 - Said, Samir T1 - Offshore wind energy plants- a challenge for integrated structural health monitoring systems T2 - International Workshop on Lifetime Engineering of Civil Infrastructure CY - Ube Yamaguchi, Japan DA - 2005-11-09 KW - Offshore wind energy turbines KW - Structural health monitoring KW - Early damage detection KW - Control of dynamic behavior KW - Structural assessment PY - 2005 SP - 219 EP - 229 PB - Yamaguchi University CY - Ube Yamaguchi AN - OPUS4-12257 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Streicher, Doreen A1 - Kohl, Christoph A1 - Wiggenhauser, Herbert A1 - Petz, J. T1 - Assessment of post tensioned box girder bridges applying automated non-destructive testing methods T2 - 85th TRB Annual Meeting CY - Washington D.C., USA DA - 2006-01-22 KW - Automatisierte ZfPBau-Verfahren KW - Radar KW - Ultraschallecho KW - Impact-Echo KW - Spannbetonbrücken PY - 2006 SP - 1 EP - 13(?) PB - TRB CY - Washington, D.C. AN - OPUS4-12238 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hasenstab, Andreas A1 - Krause, Martin A1 - Scheer, C. T1 - Zerstörungsfreie Integritätsprüfung von Holz mit dem Ultraschallecho-Verfahren T2 - Forschungskolloquium "Holzbau Forschung + Praxis" CY - Stuttgart, Deutschland DA - 2006-02-23 PY - 2006 SP - 33 EP - 40 PB - Technische Universität Stuttgart CY - Stuttgart AN - OPUS4-12242 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - van de Kreeke, Johannes T1 - EPTIS und COEPT - European Initiatives with Worldwide Relevance PY - 2006 IS - February SP - 7 EP - 8 CY - Jerusalem, Israel AN - OPUS4-12260 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Römich, H. A1 - Jägers, E. A1 - Torge, Manfred A1 - Müller, Wolfgang A1 - Adam, Karin T1 - Cleaning - A balancing act N2 - This text originally appeared as chapter 5, 'Reinigung - Eine Gratwanderung' (pp. 101-28) in A. Wolff (ed.), Restaurierung und Konservierung historischer Glasmalereien, Mainz, 2000. Within the context of this research programme, scientists and conservators collaborated to assess various cleaning methods for historical stained glass. For cleaning glass surfaces there are the mechanical methods already being applied in most workshops, as well as the new chemical cleaning possibilities. Laboratory experiments were conducted initially on model glass in order to test the effectiveness and damage potential of these various methods; the model glass was examined both before and after cleaning by means of light microscopy and infra-red spectroscopy. In addition to this, cleaning tests were carried out on samples of original glass; electron-ray micro-analysis was also used to evaluate the results of these tests. The model-glass samples were corroded in advance by accelerated weathering in an attempt to simulate the damage seen on medieval glass. Enough model glass was prepared to allow any number of series of experiments to be carried out, in order to compare the effectiveness and suitability of the various chemical and mechanical methods and techniques. For the mechanical cleaning tests, a wide range of selected tools was tested by different conservators on pre-corroded model glass. This showed clearly that the success (or lack of it) of a cleaning episode was determined not just the choice of tool, but by the skill with which conservator wielded it. This observation was later confirmed by research on samples of original glass. Insensitive handling of tools or unsuitable tools could damage or completely destroy the gel layer. The gel layer should not be damaged, as this leads to increased levels of corrosion subsequently, though the encrustations should be reduced, as their hygroscopic qualities accelerate the corrosion processes. At the next stage, chemical cleaning methods were tested, and the results of cleaning with organic solvents (toluene, ethanol, acetone, etc.) and water-based solutions (oxalic acids, EDTA, ammoniac, etc.) compared with one another and evaluated. It became clear that strongly acidic and alkaline solutions, depending on the condition of the surface, could cause damage or have uncontrollable consequences. In the specific case of the glass from Erfurt Cathedral, for whose firmly fixed, very hard, opaque encrustations mechanical methods proved to be either ineffective or damaging to the glass, new chemical cleaning possibilities had to be found. Following comprehensive preliminary tests on model glass, various types of ion-exchanger and ammonium-carbonate solution were chosen. Both methods were successful in improving the transparency of some (but not all) of the samples. The experiments with the original material from Erfurt Cathedral clearly showed that successful cleaning was dependent on the particular composition of the encrustation. Really gentle cleaning can be achieved by chemical means, though only when the chemical agents are tailored to individual damage situations; this can only be achieved when scientific analysis is undertaken in tandem with the cleaning processes. The assessment of these mechanical and chemical cleaning methods was oriented towards treating corrosion on sensitive medieval glass. Nineteenth-century glass is generally less sensitive, though cleaning of this material must also be careful and very gentle. Scientific analysis alone is not enough to determine the choice of cleaning method, but can act as an aid to the conservator in selecting the right cleaning agent and method. KW - Historische Glasmalereien KW - Restaurierung PY - 2006 UR - http://www.cvma.ac.uk/conserv/cleaning.html SP - 1 EP - 33 PB - Kings's College CY - London AN - OPUS4-12308 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Liebner, Christian A1 - Silakova, M.A. A1 - Pasman, H.J. A1 - Fernández Giua, C. T1 - Report on experiments needed for kinetic model development (high pressure) KW - Explosion indices KW - Dependence of pressure KW - Temperature KW - Ignition energy and fuel content PY - 2006 UR - http://www.morechemistry.com/SAFEKINEX/deliverables/43.Del.%20No.33_fin.pdf IS - EVG1-CT-2002-00072 SP - 18 pages, Add.A 40p., Add.B 37p. AN - OPUS4-12463 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Krüger, Simone A1 - Brademann-Jock, Kerstin A1 - Wachtendorf, Volker A1 - Rauth, W. A1 - Klimmasch, T. A1 - Krüger, P. T1 - Analysis of weathering effects in automotive coatings by thermoluminescence T2 - 28th FATIPEC Congress CY - Budapest, Hungary DA - 2006-06-12 KW - Automotive coatings KW - Weathering KW - Thermoluminescence PY - 2006 SP - 1 EP - 9 CY - Budapest AN - OPUS4-12558 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völzke, Holger A1 - Wille, Frank A1 - Wieser, Günter A1 - Quercetti, Thomas T1 - Transport and Storage Cask Safety Assessment - Drop Tests and Numerical Calculations T2 - Waste Management Symposium 2006 CY - Tucson, Az. USA DA - 2006-02-26 KW - Transportbehälter KW - Lagerbehälter KW - Radioaktive Stoffe KW - Fallversuch KW - FEM KW - Sicherheit PY - 2006 SP - 12 pages CY - Tucson AN - OPUS4-12536 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schartel, Bernhard T1 - Wirkmechanismen von phosphorhaltigen Flammschutzmitteln T2 - 8. SKZ-Fachtagung "Kunststoffe, Brandschutz und Flammschutzmittel" CY - Würzburg, Deutschland DA - 2006-06-21 PY - 2006 SP - D1-D6, 1-16 PB - SKZ CY - Würzburg AN - OPUS4-12537 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Krüger, Simone A1 - Wachtendorf, Volker A1 - Rauth, W. A1 - Klimmasch, T. A1 - Krüger, P. T1 - Screening the weathering stability of automotive coatings by chemiluminescence T2 - XXVIIIth FATIPEC Congress CY - Budapest, Hungary DA - 2006-06-12 KW - Automotive coatings KW - Weathering KW - Chemiluminescence PY - 2006 SP - 8 pages CY - Budapest AN - OPUS4-12557 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Peplinski, Burkhard A1 - Wenzel, J. A1 - Schultze, Dietrich T1 - Certification of the phase composition of a BAM reference material by an interlaboratory comparison applying X-ray and neutron diffraction T2 - Symposium "Reference Materials for Technologies in the New Millenium" CY - Berlin, BAM, Germany DA - 2000-05-22 PY - 2000 SP - 1(?) EP - 13(?) AN - OPUS4-12600 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilrich, Cordula A1 - Aris, Stephan T1 - Type Approval of Cylinders and Valves T2 - EIGA Workshop 2006 "Acetylene, our Heritage and Future" CY - Brussels, Belgium DA - 2006-06-22 KW - Acetylen KW - Acetylenflasche KW - Gasflaschenventil KW - Poröses Material PY - 2006 PB - European Industrial Gases Association (EIGA) CY - Brüssel AN - OPUS4-12678 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rolle, Annette A1 - Droste, Bernhard A1 - Dombrowski, H. T1 - Type testing of devices with inserted radioactive sources T2 - 2nd European IRPA Congress on Radiation Protection CY - Paris, France DA - 2006-05-15 KW - Radiation protection KW - Type approval PY - 2006 SP - 1(?) EP - 6(?) PB - IRPA CY - Paris AN - OPUS4-12815 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krause, Ulrich A1 - Wappler, Mike A1 - Radzewitz, S. A1 - Ferrero, Fabio T1 - On the minimum ignition temperature of dust clouds T2 - 6th International Symposium on hazards, prevention, and mitigation of industrial explosions CY - Halifax, Canada DA - 2006-08-27 KW - Dust explosions KW - Ignition KW - Hot surfaces KW - Minimum ignition temperature PY - 2006 VL - 1 SP - 68 EP - 76 PB - Dalhousie University CY - Halifax AN - OPUS4-12787 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Jäger, Christian A1 - Maltsev, Sergey A1 - Karrasch, Andrea T1 - Progress of Structural Elucidation of Amorphous Calcium Phosphate (ACP) and Hydroxyapatite (HAp): Disorder and Surfaces as Seen by Solid State NMR KW - Hydroxyapatite KW - Amorphous calcium phosphate KW - Structural investigation KW - Surface KW - NMR PY - 2006 VL - 18 IS - 1 SP - 69 EP - 72 AN - OPUS4-11008 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Peters, P. W. M. A1 - Hemptenmacher, J. A1 - Günther, Burkhard A1 - Bettge, Dirk A1 - Portella, Pedro Dolabella ED - Galiotis, C. T1 - Analysis of the thermo-mechanical fatigue behaviour of SiC-fibre reinforced titanium alloy (SCS-6/TI-6242) T2 - 11th European Conference on Composite Materials (ECCM-11) CY - Rhodos (Greece) DA - 2004-05-31 KW - Ti-MMC KW - Ermüdung KW - Schädigungsmechanik PY - 2004 VL - 2 SP - 1 EP - 8 CY - Rhodos, Greece AN - OPUS4-11102 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bettge, Dirk A1 - Günther, Burkhard A1 - Wedell, Wolfgang A1 - Portella, Pedro Dolabella A1 - Hemptenmacher, J. A1 - Peters, P. W .M. ED - Portella, Pedro Dolabella T1 - Fatigue damage of a SiC fibre reinforced titanium matrix composite T2 - 5th International Conference on Low Cycle Fatigue (LCF-5) CY - Berlin, Germany DA - 2003-09-09 KW - Metal matrix composite KW - Thermo-mechanical fatigue KW - Damage analysis PY - 2003 VL - 5 SP - 81 EP - 86 PB - DVM, Deutscher Verband für Materialforschung und -prüfung CY - Berlin AN - OPUS4-11103 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bettge, Dirk A1 - Günther, Burkhard A1 - Wedell, Wolfgang A1 - Portella, Pedro Dolabella A1 - Hemptenmacher, J. A1 - Peters, P.W.M. T1 - Fatigue Mechanisms of a SiC Fibre Reinforced Titanium Matrix Composite T2 - 15. Symposium Verbundwerkstoffe und Werkstoffverbunde CY - Kassel, Deutschland DA - 2005-04-06 KW - Ti-MMC KW - Ermüdung KW - Schädigungsmechanik PY - 2005 SP - 519 EP - 524 PB - DGM CY - Kassel AN - OPUS4-11106 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Arlt, N. A1 - Burkert, Andreas A1 - Isecke, Bernd T1 - Edelstahl Rostfrei in Kontakt mit anderen Werkstoffen (Merkblatt) KW - Edelstahl Rostfrei KW - Bimetallkorrosion KW - Galvanische Korrosion KW - Elektrolytwiderstand KW - Abhilfemaßnahmen PY - 2005 IS - MB 829 SP - 1 EP - 12 PB - Informationsstelle Edelstahl Rostfrei CY - Düsseldorf ET - 4. überarb., erw. AN - OPUS4-11052 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Streicher, Doreen A1 - Kohl, Christoph A1 - Wiggenhauser, Herbert T1 - Assessment of post tensioned concrete bridges applying automated non-destructive testing systems T2 - 1st Munich Bridge Assessment Conference (MBAC 2005) CY - Munich, Germany DA - 2005-06-20 KW - Automatisierte ZfPBau-Verfahren KW - Radar KW - Ultraschallecho KW - Impact-Echo KW - Spannbetonbrücken KW - Scannersysteme KW - Bridge investigations KW - Ultrasonic echo KW - Data fusion KW - Scanning system PY - 2005 SP - 13 pages PB - University of the German Armed Forces CY - München AN - OPUS4-11077 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Streicher, Doreen A1 - Wiggenhauser, Herbert T1 - Automatisierte Brückenuntersuchungen mit kombinierten Verfahren T2 - DAfStb-Fachtagung CY - Berlin, Deutschland DA - 2005-03-10 PY - 2005 SP - A25 EP - A30 PB - BAM CY - Berlin AN - OPUS4-11076 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wloka, Monika ED - Davies, P. T1 - Alignment of ISO/IEC 17025:1999 with ISO 9001:2000 - The new edition of ISO/IEC 17025 KW - Management system KW - Laboratory KW - Compliance with ISO 9001:2000 KW - Conformity assessment services KW - Certification KW - Technical requirement PY - 2005 VL - 7 IS - 27 SP - 16 EP - 18 PB - ILAC Secretariat AN - OPUS4-11122 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reiche, I. A1 - Börst, F.-M. A1 - Krietsch, Torsten T1 - Aspects of safety assessments for package designs with additional equipment T2 - 14th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Berlin, Germany DA - 2004-09-20 KW - Transport Packagings KW - Radioactive Materials KW - Safety Assessments PY - 2004 IS - 235 SP - 1 EP - 2 PB - BAM CY - Berlin AN - OPUS4-11227 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koch, Frank A1 - Ballheimer, Viktor A1 - Zeisler, Peter A1 - Krietsch, Torsten T1 - New BAM-Guideline for the Calculation and Assessment of Lid and Trunnion Systems for RAM Packages with Respect to IAEA-96 Requirements T2 - 7th International Conference on Radioactive Materials Transport 2005 CY - Cambridge, England, UK DA - 2005-09-27 PY - 2005 SP - 11 pages PB - The Institution of Nuclear Engineers (INucE) CY - Cambridge AN - OPUS4-11231 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krietsch, Torsten A1 - Wolff, Dietmar A1 - Knopp, U. A1 - Brocke, H.-D. T1 - Behaviour of neutron moderator materials at high temperatures in CASTOR-casks - qualification and assessment T2 - 14th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Berlin, Germany DA - 2004-09-20 KW - Transport Packagings KW - Radioactive Materials KW - Neutron Shielding Materials PY - 2004 UR - http://www.iaea.org/inis/collection/NCLCollectionStore/_Public/37/088/37088730.pdf VL - 14 IS - 235 SP - 1 EP - 8(?) PB - BAM CY - Berlin AN - OPUS4-11226 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Just, Ulrich A1 - Much, H. T1 - Characterization of Polymers using Supercritical Fluid Chromatographie -Application of the three modes in liquid chromatography T2 - International GPC Symposium CY - Florida, USA DA - 1995-06-05 PY - 1995 SP - 861 EP - 877 AN - OPUS4-11334 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Taffe, Alexander A1 - Wiggenhauser, Herbert T1 - Zerstörungsfreie Prüfverfahren im Bauwesen (ZfPBau) T2 - Seminar des Eisenbahnbundesamtes (EBA) CY - Langenporzelten, Deutschland DA - 2005-08-25 KW - Zerstörungsfreie Prüfung im Bauwesen KW - ZfP KW - Bauwerksdiagnose KW - Schadensanalyse PY - 2005 SP - 18 Seiten PB - Eisenbahnbundesamt CY - Langenporzelten AN - OPUS4-11343 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz ED - Natke, H. T1 - Die Wechselwirkung starrer und flexibler Strukturen mit dem Baugrund T2 - Tagung des Curt-Risch-Institutes CY - Hannover, Deutschland DA - 1987-10-01 PY - 1987 VL - 87 IS - 1 SP - 197 EP - 215 PB - Curt-Risch-Inst. der Univ. CY - Hannover AN - OPUS4-11515 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz A1 - Schmid, G. T1 - Bauwerksstrukturen unter Wellenfeldanregung T2 - 3. Gemeinschaftsseminar CY - Innsbruck, Österreich DA - 1989-01-01 PY - 1989 N1 - Serientitel: Report / Universität Innsbruck, Institut für Mechanik – Series title: Report / Universität Innsbruck, Institut für Mechanik IS - 24 SP - 45 EP - 50 CY - Innsbruck AN - OPUS4-11558 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dantan, Nathalie A1 - Habel, Wolfgang A1 - Hillemeier, B. A1 - Hüttl, R. T1 - Entwicklung eines faseroptischen pH-Sensors zur Früherkennung korrosionsgefährdender Zustände in Stahlbeton T2 - Tagung Bauchemie der GDCh-Fachgruppe Bauchemie CY - Berlin, Deutschland DA - 2005-09-29 KW - Korrosion KW - Stahlbeton KW - Monitoring KW - pH KW - Faseroptischer Sensor KW - Langzeitstabilität KW - Indikator KW - Immobilisierung PY - 2005 SP - 242 EP - 248 PB - GDCh CY - Frankfurt am Main AN - OPUS4-11559 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz T1 - A simple 2-dimensional method for the effectiveness of ballast mats and other isolators of railway vibration T2 - 12. International Congress on Sound and Vibration CY - Lisboa, Portugal DA - 2005-07-11 PY - 2005 SP - 1(?) EP - 8(?) CY - Lissabon AN - OPUS4-11564 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF ED - Beckhoff, B. ED - Görner, Wolf ED - Kanngießer, B. T1 - EDXRS 2002, European Conference on Energy Dispersive X-Ray Spectrometry, 16-21 June 2002, Berlin, Germany - Book of Abstracts T2 - European Conference on Energy Dispersive X-Ray Spectrometry CY - Berlin, Germany DA - 2002-06-16 PY - 2002 SP - 1 EP - 234 PB - Technische Univ. CY - Berlin AN - OPUS4-11565 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Pastuska, Gerhard A1 - Lehmann, Volker A1 - Just, Ulrich T1 - Untersuchungen über das mechanische Verhalten dünnwandiger Kunstoff-Bauelemente in Abhängigkeit von der Bewitterung - Abschlußbericht zur Forschungsarbeit PY - 1980 SP - 1 EP - 19 CY - Berlin AN - OPUS4-11495 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kley, Gerd A1 - Brenneis, Rudolf A1 - Adamczyk, Burkart A1 - Simon, Franz-Georg A1 - Köcher, Peter T1 - Thermochemical treatment - Technologies for recovery and upvaluation of materials T2 - 7th World Congress on Recovery, Recycling and Re-integration CY - Bejing, China DA - 2006-05-25 KW - Thermochemie KW - Lichtbogenofen KW - Dekontaminierung KW - Recycling KW - Verwertung KW - Ressourcenschutz KW - Silikatprodukte KW - Feuerfest KW - Schlacken PY - 2005 SP - 1 EP - 10(?) PB - Beijing Kexin Printing House CY - Peking AN - OPUS4-11540 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Qiao, Linan A1 - Droste, Bernhard T1 - Entwicklung von Beurteilungsmethoden für Transport- und Lagerbehälter mit erhöhten metallischen Reststoffanteilen - Ein zusammenfassender Überblick T2 - 7. Internationales Symposium "Konditionierung radioaktiver Betriebs- und Stilllegungsabfälle" (KONTEC 2005) CY - Berlin, Deutschland DA - 2005-04-20 KW - Duktiles Gusseisen KW - Behälterdesign KW - Sicherheitstechnische Bewertung KW - Bruchmechanik KW - Dynamische Belastungsbedingungen PY - 2005 SP - 797 EP - 804 PB - KONTEC CY - Hamburg AN - OPUS4-11550 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz T1 - Structural dynamics and soil-structure-interaction induced by railway traffic T2 - Dynamics of Structures '89 CY - Karlovy Vary, Czech Republic DA - 1989-09-12 PY - 1989 SP - 21 EP - 25 AN - OPUS4-11554 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Pastuska, Gerhard A1 - Just, Ulrich T1 - Abschlußbericht zum Forschungsvorhaben ERP 2297 - Änderung der Molekulargewichtsverteilung in Polyamiden in Abhängigkeit von der Vearbeitung PY - 1977 SP - 1 EP - 26 PB - Bundesanstalt für Materialprüfung CY - Berlin AN - OPUS4-11497 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Pastuska, Gerhard A1 - Barnheim, D. A1 - Just, Ulrich A1 - Lehmann, Volker T1 - Untersuchungen zur Beurteilung des Langzeitverhaltens von PVC-Abdichtungsbahnen (nicht bitumenbeständig) durch Kurzzeitversuche - Abschlußbericht zur Forschungsarbeit PY - 1983 SP - 1 EP - 65 CY - Berlin AN - OPUS4-11499 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Pastuska, Gerhard A1 - Lützow, Wolfgang A1 - Just, Ulrich A1 - Riecke, Rudolf T1 - Dynamische Beanspruchung von Bauteilen aus Polyolefinen und ihr Einfluß auf die Spannungsrißbildung PY - 1978 SP - 1 EP - 52 CY - Berlin AN - OPUS4-11500 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz T1 - Dynamic Soil-Structure Interaction of Rigid and Flexible Foundations T2 - 5th International Conference on Soil Dynamics and Earthquake Engineering CY - Karlsruhe, Germany DA - 1991-09-23 PY - 1991 VL - 5 SP - 467 EP - 478 CY - Berlin AN - OPUS4-11569 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weise, Frank A1 - Patitz, G. A1 - Müller, Urs A1 - Reschke, Thorsten T1 - Zerstörungsarme baustoffliche Zustandsbewertung von AKR-geschädigten Wasserbauwerken mit innovativen Prüftechniken T2 - DAfStb-Fachtagung 2005 "Zerstörungsfreie Prüfverfahren und Bauwerksdiagnose im Betonbau" CY - Berlin, Deutschland DA - 2005-03-10 KW - Betonbau KW - Strukturaufklärung KW - Zerstörungsfreie Prüfung KW - Radar KW - Ultraschall-Echo KW - Röntgen3D-CT KW - Mikro-RFA PY - 2005 SP - A47 EP - A56 PB - BAM CY - Berlin AN - OPUS4-11527 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Binkowski, Sigrid A1 - Woydt, Mathias A1 - Dietrich, E. T1 - Außergewöhnliche Aufhärtung von 100Cr6 in einem ausgefallenen Keramik-Hybrid-Wälzlager N2 - An einem defekten Keramik-Hybrid-Wälzlager wurde eine Metallographische Schadensanalyse durchgeführt um die Ursache des plötzlichen Ausfalls zu bestimmen. T2 - 39. Metallographietagung 2005 CY - Erlangen DA - 2005-09-14 KW - 100Cr6 KW - Tribologie KW - Laufbahn KW - Präparation KW - Aufhärtung KW - Nanokristallin PY - 2005 UR - http://www.struers.com/resources/elements/12/79041/e-Structure%208T.pdf IS - e-8 SP - 2 EP - 5 PB - Struers CY - Willich AN - OPUS4-11179 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krause, Ulrich A1 - Schmidt, Martin A1 - Lohrer, Christian T1 - Computations on the coupled heat and mass transfer during fires in bulk materials, coal deposits and waste dumps T2 - I. FEMLAB Konferenz CY - Frankfurt am Main, Deutschland DA - 2005-11-02 PY - 2005 SP - 74 EP - 79 PB - FEMLAB CY - Göttingen AN - OPUS4-11189 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rolle, Annette A1 - Buhlemann, Lothar T1 - Quality assurance in production and use of special form radioactive material - focal points in BAM approvals N2 - BAM, as the competent authority for approval of special form radioactive material, attaches great importance to a detailed audit of the required quality assurance programmes for design, manufacture, testing, documentation, use, maintenance and inspection. Applicants have to submit, together with their application documentation, information on general arrangements for quality assurance, as well as on quality assurance in production and in operation. Fields where BAM has often found deficiencies are leak test methods, weld seam quality and the safety level after use. T2 - 14th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Berlin, Germany DA - 2004-09-20 KW - Zulassung KW - Special form KW - Qualitätssicherung PY - 2004 IS - 235 SP - 1(?) EP - 5(?) PB - BAM CY - Berlin AN - OPUS4-11190 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simon, Franz-Georg A1 - Gerstung, Vanessa T1 - Improvement of Materials Efficiency for a Sustainable Resource Management T2 - R `05 - 7th World Congress on Recovery, Recycling and Re-integration CY - Beijing, PR China DA - 2005-09-25 KW - Materials efficiency KW - Resources efficiency KW - Environmental impact PY - 2005 IS - 104 SP - 1(?) EP - 8(?) CY - Peking AN - OPUS4-11145 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Müller, Karsten A1 - Droste, Bernhard A1 - Rödel, Roland A1 - Völzke, Holger T1 - The application of fracture mechanics to the safety assessment of transport casks for radioactive materials T2 - 14th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Berlin, Germany DA - 2004-09-20 KW - Ductile iron KW - Cask design KW - Safety assessment KW - Fracture mechanics KW - BAM GGR 007 PY - 2004 UR - http://www.iaea.org/inis/collection/NCLCollectionStore/_Public/37/088/37088572.pdf IS - 235 SP - 1 EP - 7(?) PB - BAM CY - Berlin AN - OPUS4-11477 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Qiao, Linan A1 - Droste, Bernhard T1 - Development of Assessment Methods for Transport and Storage Containers with Higher Content of Metallic Recycling Material T2 - 14th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Berlin, Germany DA - 2004-09-20 KW - Ductile iron KW - Container design KW - Safety assessment KW - Fracture mechanics KW - Dynamic loading conditions PY - 2004 UR - http://www.iaea.org/inis/collection/NCLCollectionStore/_Public/37/088/37088594.pdf IS - 235 SP - 1(?) EP - 7(?) PB - BAM CY - Berlin AN - OPUS4-11478 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niederleithinger, Ernst A1 - Kruschwitz, Sabine A1 - Behrens, Matthias T1 - Spectral induced polarization (SIP) measurements for stability assessment of tailings dams T2 - 18th Annual Meeting SAGEEP, Symposium on the Application of Geophysics to Engineering and Environmental Problems, "Geophysical Solutions for Today´s Challenges" CY - Atlanta, GA, USA DA - 2005-04-03 KW - Geophysik KW - Geotechnik KW - Halden KW - Umwelt KW - Bergbau PY - 2005 SP - 298 EP - 305 PB - Environmental and Engineering Geophysical Society CY - Atlanta AN - OPUS4-11469 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gründer, Klaus-Peter A1 - Quercetti, Thomas T1 - Determination of lid displacements by photogrammetry in full-scale cask drop tests T2 - 3rd International Conference on Materials Testing "TEST 2005" CY - Nuremberg, Germany DA - 2005-05-10 PY - 2005 SP - C7-93 - C7-96 PB - AMA Service GmbH CY - Nürnberg AN - OPUS4-11472 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hertwig, Andreas A1 - Martin, S. A1 - Kautek, Wolfgang A1 - Krüger, Jörg ED - Maruray, L. T1 - Ultra-short Pulse Laser Safety - a Challenge to Materials Science N2 - In this paper, safety-related experiments with ultra-short laser pulses (down to 30 fs) on various components (goggles, curtains) for laser protection are presented. The damage and failure behaviour of protective devices has been investigated dependent on practical conditions such as pulse duration, laser .uence, pulse number, and repetition rate. The e.ects of laser-irradiation on materials can be roughly divided into transient ones like laserinduced transmission (LIT) or short-lived colour centres and permanent damages like the stable colour centres and ablation. The former e.ects are particularly important for transparent devices like laser goggles. To obtain a complete overview on laser safety issues and the prevention of failure there are two important .elds of investigation: 1. the e.ects of laser radiation on human eyes and skin, and 2. on the possible protection materials. Both .elds have been addressed during the recently .nished German project SAFEST (safety aspects in femtosecond technology). The amount of safety data available in the ultrashort pulse region has been increased remarkably. This allows for a re-evaluation of known laser protection materials for this region of pulse durations and for the evaluation of new designs that promise high protection levels while being light-weight and convenient to use. T2 - Optical design and engineering II CY - Jena, Germany DA - 2005-09-13 PY - 2005 N1 - Serientitel: Proceedings of SPIE – Series title: Proceedings of SPIE IS - 5962 SP - 59622J-1 - 59622J-10 PB - SPIE CY - Bellingham AN - OPUS4-11593 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rücker, Werner A1 - Auersch, Lutz A1 - Said, Samir T1 - Reduzierung von Schienenverkehrserschütterungen T2 - D-A-CH-Tagung CY - Zürich, Schweiz DA - 1997-09-25 PY - 1997 IS - D 145 SP - 1(?) EP - 6(?) PB - SIA CY - Zürich AN - OPUS4-11581 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Beständigkeitsbewertungen von Werkstoffen für den Transport von Gefahrgütern durch die BAM-Liste T2 - GfKORR-Seminar: Auswahl korrosionsbeständiger Werkstoffe für den industriellen Einsatz CY - Iserlohn, Deutschland DA - 2005-11-17 KW - Stoffbezogene Baumusterzulassung KW - Gefahrgüter KW - Metallische Tankwerkstoffe KW - Polymere Dichtungs-, Beschichtungs- und Auskleidungswerkstoffe KW - BAM-Liste KW - Bewertung der Korrosionsbeständigkeit PY - 2005 SP - - PB - Fachhochschule Südwestfalen - Hochschule für Technik und Wirtschaft CY - Iserlohn AN - OPUS4-11600 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Korzen, Manfred T1 - Substrukturtechnik: Eine hybride Prüfmethode - Überblick mit Anwendung im Brandingenieurwesen T1 - Substructuring: A hybrid test method - Survey with application in fire engineering N2 - Im Gegensatz zu realen Bränden werden Bauelemente bei klassischen Brandversuchen als Einzelbauteile ohne Wechselwirkung mit dem umgebenden Gebäude betrachtet. Um einen Brandversuch realistischer durchführen zu können, ist die Entwicklung spezieller experimenteller Methoden erforderlich. Als Beitrag zur Verbesserung der Situation wurde die Anwendung der Substrukturtechnik, einer speziellen hybriden Prüfmethode, die aus dem Erdbebeningenieurwesen bekannt ist, auf das Brandingenieurwesen übertragen. N2 - In contrast to real fires in classical fire resistance tests building elements are considered as stand alone elements without interaction with the surrounding building. In order to run a fire test in a more realistic fashion the development of special experimental techniques is required. As a contribution to overcome the situation the application of the substructuring method, a special hybrid method known from earthquake engineering, has been adopted to fire engineering. T2 - Tagung Werkstoffprüfung 1999 CY - Bad Nauheim, Germany DA - 02.12.1999 PY - 1999 SP - 215 EP - 218 PB - Deutscher Verband für Materialforschung und -prüfung (DVM) CY - Berlin AN - OPUS4-11676 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kroggel, O. A1 - Krause, Martin A1 - Schickert, M. A1 - Langenberg, K.-J. T1 - Moderne Verfahren der Bauwerksdiagnose, Entwicklung und Anwendung - Die DFG-Forschergruppe FOR384 stellt ihre Ergebnisse vor - Ultraschall T2 - Fachtagung 2005 des Deutschen Ausschusses für Stahlbeton in Zusammenarbeit mit der Bundesanstalt für Materialforschung und -prüfung "Zerstörungsfreie Prüfverfahren und Bauwerksdiagnose im Betonbau" CY - Berlin, Deutschland DA - 2005-03-10 KW - Ultraschallecho-Verfahren KW - Beton KW - Fundamente KW - Erhärtungsverhalten KW - Tomographie PY - 2005 SP - A5 EP - A10 PB - BAM CY - Berlin AN - OPUS4-11718 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stark, Wolfgang A1 - Fritsch, Sebastian A1 - Kelm, Jürgen T1 - Vulcanization Monitoring in the Mould by Means of Ultrasound T2 - German Rubber Conference 2006 CY - Nuremberg, Germany DA - 2006-07-03 KW - Vulkanisation KW - Ultraschall KW - Prozesskontrolle KW - Rheologie PY - 2006 SP - 189 EP - 193 PB - Deutsche Kautschuk-Gesellschaft CY - Frankfurt am Main AN - OPUS4-13082 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilke, Olaf T1 - Teppich, Holzboden oder elastischer Bodenbelag? T2 - IBK-Symposium 330 - "Bauen, leben, wohnen - Gesundheit als Einheit" CY - Berlin, Deutschland DA - 2006-09-06 KW - Emissionen KW - Bodenbeläge KW - Blauer Engel KW - AgBB PY - 2006 SP - 8 Seiten PB - IBK CY - Darmstadt AN - OPUS4-13199 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Qiao, Linan A1 - Wieser, Günter A1 - Zencker, Uwe A1 - Droste, Bernhard T1 - Dynamische Analyse eines mit Stoßdämpfern ausgerüsteten Gefahrgutbehälters beim 9 m - Fallversuch T2 - 18. ABAQUS-Benutzerkonferenz 2006 CY - Erfurt, Deutschland DA - 2006-09-18 KW - Gefahrgutbehälter KW - Fallversuch KW - Finite-Elemente-Methoden PY - 2006 SP - 1 EP - 11(?) PB - ABAQUS CY - Aachen AN - OPUS4-13207 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ullner, Robert A1 - Reimann, E. T1 - Effect and measurement of the machine compliance in the macro range of instrumented indentation test T2 - XVIII IMEKO World Congress CY - Rio de Janeiro, Brazil DA - 2006-09-17 KW - Indentation KW - Compliance KW - Uncertainty PY - 2006 SP - 1 EP - 6(?) PB - Letra Capital Ed. CY - Rio de Janeiro AN - OPUS4-13987 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - von Oertzen, Alexander T1 - Das CHAF-Projekt: Quantifizierung und Beherrschung der Gefahren beim Transport sowie bei der Massenlagerung von Feuerwerk T2 - 55. Jahresfachtagung der Vereinigung zur Förderung des Deutschen Brandschutzes e.V. CY - Salzburg, Österreich DA - 2006-05-21 KW - Feuerwerk KW - Gefahrgut KW - CHAF KW - Klassifizierung PY - 2006 SP - 583 EP - 601 PB - VFDB - Vereinigung zur Förderung des Deutschen Brandschutzes CY - Salzburg AN - OPUS4-13937 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Klobes, Peter A1 - Meyer, Klaus A1 - Munro, R.G. T1 - Porosity and specific surface area measurements for solid materials KW - Poröse Materialien KW - Gasadsorption KW - Hg-Porosimetrie KW - Referenzmaterialien KW - Normen PY - 2006 UR - http://www.nist.gov/manuscript-publication-search.cfm?pub_id=854263 IS - 960-17 SP - 1 EP - 79 PB - U. S. Government Printing Office CY - Washington, DC AN - OPUS4-13943 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Taffe, Alexander T1 - Ultraschall an Beton - Entwicklung eines ZfPBau-Verfahrens zur Bauwerkssicherheit T2 - 29. Darmstädter Massivbauseminar, "Sicherheitsgewinn durch Monitoring?" CY - Darmstadt, Germany DA - 2006-09-14 KW - Zerstörungsfreie Prüfung im Bauwesen KW - Bauwerkssicherheit KW - Ultraschallecho KW - Messunsicherheit KW - Fundamente KW - Tunnelinnenschalen PY - 2006 SP - 489 EP - 499 PB - Freunde des Instituts für Massivbau der Technischen Universität Darmstadt CY - Darmstadt AN - OPUS4-13726 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simon, Franz-Georg T1 - Kostensenkung durch Steigerung der Materialeffizienz T2 - Seminar "Produktionsintegrierter Umweltschutz (PIUS) CY - Kaiserslautern, Deutschland DA - 2006-05-19 KW - Materialeffizienz KW - Globaler Materialverbrauch KW - Förderprogramme PY - 2006 SP - 4 Seiten PB - PIUS CY - Kaiserslautern AN - OPUS4-13732 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Molnarne, Maria T1 - Gefährdungsbeurteilung nach der GefStoffV T2 - DECHEMA-Weiterbildungskurs "Grundlagen und rechtliche Anforderungen des Explosionsschutzes" CY - Frankfurt am Main, Deutschland DA - 2006-10-23 PY - 2006 IS - Kurshandbuch SP - 16 Seiten PB - DECHEMA CY - Frankfurt am Main AN - OPUS4-13735 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz T1 - Experimental observation and theoretical calculation of technically induced surface waves in inhomogeneous soil T2 - 1st European Conference on Earthquake Engineering and Seismology (ECEES) CY - Geneva, Switzerland DA - 2006-09-03 PY - 2006 IS - Paper 1292 SP - 1 EP - 10(?) PB - ETH Zürich CY - Geneva AN - OPUS4-13737 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Hartmut A1 - Munz, Martin A1 - Böhning, Martin A1 - Lorenz, Edelgard A1 - Kneip, Gisela T1 - New method for testing the resistance to oxidation - Application and Evaluation: Polyolefinic Products T2 - EUROCORR 2006 CY - Maastricht, The Netherlands DA - 2006-09-25 PY - 2006 N1 - Serientitel: EFC-Event – Series title: EFC-Event IS - 280 SP - 1 EP - 8 PB - European Federation of Corrosion CY - Maastricht AN - OPUS4-13706 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Hässelbarth, Werner A1 - Golze, Manfred A1 - Noack, Siegfried A1 - Subaric-Leitis, Andreas T1 - Guide to the Evaluation of Measurement Uncertainty for Quantitative Test Results PY - 2006 IS - 1 SP - 1 EP - 49 PB - EUROLAB Technical Secretariat CY - Paris AN - OPUS4-13871 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bohse, Jürgen T1 - Acoustic emission for non-destructive evaluation of composites T2 - Structural Composites Conference, Applications in Corrosion Prevention, Transportation, Defense and Infrastructure CY - Birmingham, AL, USA DA - 2006-02-08 PY - 2006 SP - 1 EP - 30(?) PB - American Composites Manufactures Association (ACMA) CY - Birmingham, USA AN - OPUS4-13904 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eberstein, Markus A1 - Rabe, Torsten A1 - Schiller, Wolfgang Arno T1 - Liquid Phases in LTCC - Key to Tailored Materials T2 - MAPS/ACerS 2nd International Conference and Exhibition on Ceramic Interconnect and Ceramic Microsystems Technologies (CICMT 2006) CY - Denver, CO, USA DA - 2006-04-24 KW - LTCC KW - Ceramic composites KW - Liquid phase sintering KW - Viscosity KW - Dielectric properties KW - Crystallization PY - 2006 SP - 1(?) EP - 8(?) PB - American Ceramic Society CY - Denver AN - OPUS4-14043 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Marotzke, Christian A1 - Kalinka, Gerhard ED - Zachariev, G. T1 - Microscopical Failure Processes in Fiber Reinforced Polymers - Mechanical Aspects of the Adhesion between Fiber and Matrix T2 - 11th International Conference on Mechanics and Technology of Composite Materials CY - Sofia, Bulgaria DA - 2006-10-02 KW - Composite materials KW - Failure process KW - Adhesion PY - 2006 SP - 37 EP - 42 PB - Bulgarian Academy of Sciences CY - Sofia AN - OPUS4-14027 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Unger, Wolfgang A1 - Oran, Umut A1 - Senoner, Mathias A1 - Schmidt, M. T1 - Chemische Charakterisierung von mikro- und nanotechnologischen Bauteilen: Verfahrensentwicklung und Referenzmaterialien T2 - VDI/VDE-Tagung "Messtechnik für Mikro- und Nano-Engineering" CY - Erlangen, Germany DA - 2006-11-29 KW - Referenzmaterial KW - Mikrofluidik KW - Nanoanalytik PY - 2006 N1 - Serientitel: VDI-Berichte – Series title: VDI-Berichte IS - 1950 SP - 197 EP - 206 PB - VDI-Verl. CY - Düsseldorf AN - OPUS4-14110 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niebergall, Ute A1 - Mertlová, O. A1 - Nezbedová, E. T1 - Full notch creep test - ISO round robin test T2 - Full Notch Creep Test - ISO Round Robin test CY - Washington, D. C., USA DA - 2006-10-02 KW - Spannungsrissempfindlichkeit KW - Full Notch Creep Test (FNCT) KW - Netzmittellösung PY - 2006 SP - 1 EP - 6(?) PB - PPCA, Plastics Pipes Conference Association CY - Washington AN - OPUS4-14188 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kohlhoff, Harald A1 - Ullner, Christian T1 - Design and capability of a new calibration machine for the macro range of instrumented indentation test N2 - The instrumented indentation test provides a versatile method to determine several materials parameter. In order to provide reference specimens, a calibration machine according to ISO 14577-3 is designed for the macro range. Using innovative technology, the new machine design may lead to a standard solution not only for calibration machines. T2 - XVIII IMEKO World Congress CY - Rio de Janeiro, Brazil DA - 2006-09-17 KW - Indentation KW - Reference KW - Uncertainty KW - Machine design PY - 2006 SP - 1 EP - 5(?) PB - Letra Capital Ed. CY - Rio de Janeiro AN - OPUS4-14222 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maierhofer, Christiane A1 - Arndt, Ralf A1 - Borchardt, Kerstin A1 - Hasenstab, Andreas A1 - Röllig, Mathias A1 - Wöstmann, Jens ED - Radic, J. ED - Rajcic, V. ED - Zarnic, R. T1 - Structural assessment with radar and active thermography T2 - Conference and Brokerage Event "The Construction Aspects of the Heritage Protection" CY - Dubrovnik, Croatia DA - 2006-10-14 KW - Non-destructive testing in civil engineering KW - Radar KW - Active thermography KW - Historic structures KW - Masonry KW - Stone KW - Wood KW - Plaster PY - 2006 IS - CD-ROM SP - 77 EP - 86 PB - SECON (Structural Engineering Conferences) CY - Dubrovnik AN - OPUS4-14255 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wehr, A. A1 - Hemmleb, Matthias A1 - Maierhofer, Christiane T1 - Multi-spectral Laser Scanning for Inspection of Building Surfaces - state of the art and future concepts T2 - 7th International Symposium on Virtual Reality, Archaeology and Cultural Heritage (VAST) CY - Nicosia, Cyprus DA - 2006-10-30 KW - Non-destructive testing in civil engineering KW - Multispectral laser scanning KW - Multispectral classification KW - 3D laser scanning PY - 2006 SP - 8 pages PB - The Eurographics Association CY - Nicosia AN - OPUS4-14241 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nolze, Gert T1 - The Orientation of carlsbergite in iron meteorites T2 - EBSD Users Meeting 2006 CY - Hindsgavl, Denmark DA - 0006-12-04 PY - 2006 SP - 34 EP - 46 PB - Oxford Instruments HKL CY - Hindsgavl AN - OPUS4-14426 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Schurig, Michael T1 - The vertex effect in polycrystalline materials - simulation, a macroscopic model, and structural application N2 - Der Vertex-Effekt beschreibt den Einfluss mehrerer koexistenter plastischer Fließmechanismes in ihrer Interaktion. Sie bewirken, dass am Schnittpunkt der Fließflächen im Spannungsraum eine Ecke (Corner, Vertex) im zusammengesetzten Fließort entsteht, was zur Namensgebung geführt hat. Wenn sehr viele Mechanismen existieren, wie in Polykristallen, is von größerer Bedeutung der Einfluss auf die sich ergebende Fließregel. Ein Verfleich der Mehrflächenplastizität (Abschnitt 4.3) mit regularisierten Versionen (Abschnitt 4.4) zeigt in Abschnitt 4.5, dass dieses einerseits auf den Rang des inkrementellen linearen Operators und andererseits auf den den nichtlinearen Einfluss der Belastungsbedingungen für die Gleitsysteme zurückzuführen ist. Berücksichtigt man die stückweise Definition des aktiven Set der Gleitsysteme, so kann dieser Einfluss durch ein einzelnes, aber stückweise definiertes plastisches Potential beschrieben werden. Dieser Weg wird in Kapitel 6 beschritten. Das vorgeschlagene plastische Potential erweitert die assoziierte Fließregel nach von Mieses um Terme, die eine Fließflächenparallele Komponente des plastischen Fließens in Abhängigkeit von der Abweichung vom proportionalen Belastungspfad gestattet. Dieser Einfluss wird durch einen einzelnen skalaren Parameter α beschrieben, der den Richtungskosinus der Rate des elastischen Mandel-Spannugnstensors bei eingefrorenen plastischen Variablen im Verhältnis zur proportionalen Prozessrichtung wiedergibt. Diese Wahl wurde getroffen, weil dieser Parameter für die Belastungsbedingungen der Mehrflächenplastizität maßgeblich ist. Es zeigt sich, dass die Null-Fläche des gewählten Potentials mit der der Fließfläche übereinstimmt, da die Normale der von-Mises-Fließfläche mit der radialen Richtung eines proportionalen Prüfprozesses übereinstimmt. Die zusätzlichen Materialfunktionen werden mit Hilfe einer Simulation mit dem Taylor-Modell, das als numerisches Laboratorium dient, bestimmt. In einem einzelnen Zeitschritt ergibt sich eine deutliche Verbesserung der Fließrichtung und der dissipierten Leistung im Gegensatz zur J2-Theorie. Weitere Untersuchungen mit Hilfe des Taylor-Modells zeigen in Kapitel 5 die Entwicklung einer Ecke in der Polykristallfläche, die nach dem Dissipationskriterium bestimmt wurde. Diese Ecke wandert auf proportionalen und nichtproportionalen Pfaden mit dem Spannungspunkt und entsteht durch das intergranulare Eigenspannungsfeld schon nach kleiner Verformung. Die vorgeschlagene Theorie wird in Abschnitt 6.5 durch einen Vergleich mit experimentellen Befunden einen mehrachsigen Zug-Torsions-Versuches (Lensky, 1960) verifiziert. Auch auf einem komplexen Prozesspfad zeigt sich die Verbesserung gegenüber der J2-Theorie. Als letztes Anwendungsbeispiel wird das Drillknicken einer kreuzförmigen Säule untersucht. Diese Beispiel sorgte in den 1940er und 1950er Jahren für erhebliche Zweifel an der Richtigkeit der J2-Fließtheorie, da die entsprechende Deformationstheorie weitaus bessere Ergebnisse für die kritische Knicklast lieferte. Später wurde dies mit der zu großen tangentialen Steifigkeit bei nichtproportionalen Prozessen erklärt, die aus dem fehlenden Vertex-Effekt herrührt. Im Gegensatz dazu ist der Modul der Deformationstheorie völlig pfadunabhängig. Dieser Fehler zeigt sich bei diesem speziellen Problem als günstig. Mit dem vorgeschlagenen Vertex-Modell lässt sich auf analytischem Weg zeigen, dass die richtige Steifigkeit aus der geeigneten Mittelung der Steifigkeiten über die Plattendicke resultiert. Die experimentell ermittelten Knicklasten lassen sich korrekt wiedergeben, im Gegensatz zur J2-Theorie, die infolge der postulierten Entlastung ein Verfestigungsunabhängiges Ergebnis lieferte. KW - Polycrystal Plasticity KW - Corner KW - Vertex-Effect KW - Microscale KW - Yield-Vertex KW - Macroscale KW - Multiaxial KW - Torsional Buckling KW - Cruciform Column KW - Polykristall-Plastizität KW - Ecken in Fließflächen KW - Vertex-Effekt KW - Mikroskala KW - Makroskala KW - Mehrachsig KW - Drill-Knicken KW - Säule mit Kreuzquerschnitt PY - 2006 UR - https://nbn-resolving.org/urn:nbn:de:101:1-201010181141 UR - http://diglib.uni-magdeburg.de/Dissertationen/2006/micschurig.htm SP - 1 EP - 149 AN - OPUS4-14408 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - von Oertzen, Alexander A1 - Schreck, Andreas A1 - Myatt, S. A1 - Davies, M. T1 - Deliverable D6-3, Results from two sets of UN tests done to national methods / Deliverable D6-4, Guidance and recommendations for other WPs PY - 2004 SP - 1(?) EP - 129(?) AN - OPUS4-14409 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thiele, E. A1 - Erth, H. A1 - Arnold, R. A1 - Habel, Wolfgang A1 - Krebber, Katerina A1 - Döring, H. A1 - Glötzl, R. T1 - Applikation optischer Fasern in Textilflächen T2 - 45. Internationale Chemiefasertagung CY - Dornbirn, Österreich DA - 2006-09-21 KW - Optische Fasern KW - Faseroptische Sensoren KW - Geotextilien PY - 2006 SP - 1 EP - 5(?) CY - Dornbirn AN - OPUS4-14457 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wieser, Günter A1 - Qiao, Linan T1 - FEM Simulation of extreme thermal and mechanical accident loads on screwed spent fuel cask lid structures T2 - ASME Pressure Vessels and Piping Division Conference 2006 CY - Vancouver, Canada DA - 2006-07-23 KW - Thermo-mechanische Kopplung KW - Extreme thermische und mechanische Lastfunktionen KW - Gefahrgutbehälter KW - Finite-Element Methode PY - 2006 SP - 1 EP - 7(?) PB - American Society of Mechanical Engineers CY - New York AN - OPUS4-14439 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Werner A1 - Tatzky-Gerth, Renate A1 - Jakob, Ines A1 - Li, Chunshan ED - Jost, D. T1 - Funktionsdauer von Kunststoff-Dränelementen für Oberflächenabdichtungen von Deponien und Altlasten T2 - 23. Fachtagung "Die sichere Deponie - Sicherung von Deponien und Altlasten mit Kunststoffen" CY - Würzburg, Deutschland DA - 2007-02-01 KW - Kunststoff-Dränelemente KW - Lebensdauer KW - Oberflächenabdichtungen PY - 2007 SP - 1 EP - 20 PB - SKZ CY - Würzburg AN - OPUS4-14539 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eichler, Thorsten A1 - Burkert, Andreas T1 - Investigations on black steel in high alkaline environment by means of electrochemical noise T2 - CORROSION 2007 CY - Nashville, TN, USA DA - 2007-03-11 KW - Electrochemical noise KW - Unalloyed steel KW - Concrete KW - High alkaline environment KW - Pitting corrosion KW - Steel in Concrete KW - Chlorides KW - Cement KW - Mortar KW - Black steel PY - 2007 SP - 1(?) EP - 15(?) PB - NACE International CY - Houston AN - OPUS4-14544 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krause, Ulrich T1 - Brand- und Explosionsgefahren durch technische Stäube T2 - Brandschutz-Fachtagung CY - St. Pölten, Österreich DA - 2007-02-12 KW - Brände KW - Explosionen KW - Sicherheitstechnische Kenngrößen KW - Explosionsschutz PY - 2007 SP - 148 EP - 152 PB - FSE Ruhrhofer & Schweitzer CY - St. Pölten AN - OPUS4-14546 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ludwig, Jörg A1 - Konersmann, Rainer A1 - Balke, Christian A1 - Kühl, Christiane T1 - Durchs Feuer gehn - Brandlast-Analyse - Vorkehrungen T2 - 9. Gefahrgut-Technik-Tage "Innovative Tanktechnik" CY - Berlin, Deutschland DA - 2006-11-23 PY - 2006 VL - 9 IS - Beitrag 12 SP - 1(?) EP - 9(?) PB - Bundesanstalt für Materialforschung und -prüfung CY - Berlin AN - OPUS4-14520 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - August, Hans T1 - Die Mehrschichtdichtung - Permeationsbremse und Problemlösung für die totale Schadstoffsperre T2 - 4. Abfallwirtschaftliches Fachgespräch CY - Nottensdorf, Deutschland DA - 1988-03-16 PY - 1988 VL - 4 SP - 1 EP - 19 CY - Hildesheim AN - OPUS4-14491 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - August, Hans A1 - Hanisch, J. ED - Knipschild, F. T1 - Zulassungsfragen bei Deponieabdichtungssystemen T2 - 6. Fachtagung "Die sichere Deponie" CY - Würzburg, Deutschland DA - 1990-02-15 PY - 1990 IS - 6 SP - 1(?) EP - 17(?) CY - Würzburg AN - OPUS4-14492 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Pfender, Max T1 - Untersuchungen über das Verhalten der Werkstoffe bei behinderter Verformung PY - 1938 SP - 1 EP - 15 PB - Stahleisen CY - Düsseldorf AN - OPUS4-14554 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sapich, B. A1 - Fischer, T. A1 - Haferkorn, J. A1 - Geue, T. A1 - Fritz, Andreas A1 - Schönhals, Andreas A1 - Date, R. A1 - Fawcett, A. A1 - Stumpe, J. T1 - Anisotropic films of poly(olefin sulfone)s with cinnamoyl side groups prepared by self-organisation and photoreactions T2 - Liquid Crystals and its practical application PY - 2006 VL - 4 IS - 18 SP - 9 EP - 21 AN - OPUS4-14594 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Qiao, Linan A1 - Weber, Mike A1 - Kovacs, Oliver A1 - Droste, Bernhard T1 - Sicherheitstechnische Analyse von Transport- und Lagerbehältern aus Gusseisen mit erhöhten metallischen Reststoffanteilen mittels Fallversuchen T2 - KONTEC 2007 CY - Dresden, Deutschland DA - 2007-03-21 KW - Behälterdesign KW - Bruchmechanik KW - Duktiles Gusseisen KW - Dynamische Belastungsbedingungen KW - Sicherheitstechnische Bewertung PY - 2007 SP - 869 EP - 875 PB - Gesellschaft für technische Kommunikation mbH / Kerntechnische Gesellschaft CY - Dresden AN - OPUS4-14712 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Burkert, Andreas A1 - Isecke, Bernd T1 - Electrochemical devices for determination of corrosion related values for reinforced concrete structures T2 - NACE International Corrosion 2007 - Conference & Expo CY - Nashville, TN, USA DA - 2007-03-11 KW - Chloride Induced Corrosion KW - Moisture Content KW - Embedded Sensors KW - Reinforced Concrete KW - Monitoring PY - 2007 SP - 07377/1 EP - 07377/13 PB - NACE CY - Nashville AN - OPUS4-14707 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erhard, Anton T1 - Fehlercharakterisierung in Bauteilen mit Hilfe der zerstörungsfreien Prüfung T2 - FORMAT Hochschulpraktikum Schadenanalyse CY - München, Deutschland DA - 2007-03-12 PY - 2007 SP - 1 EP - 32(?) PB - Bayerischer Forschungsverbund Materialwissenschaften CY - München AN - OPUS4-14621 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Witt, Jens T1 - Farbmetrische Methoden zur Herstellung von Prüfvorlagen für Farbkopierer, Farbscanner und Farbmonitore N2 - Die Herstellung von Prüfvorlagen erfordert Methoden, mit denen sich geräteunabhängig definierte Farben gezielt reproduzieren lassen. Hierzu werden in dieser Arbeit Methoden vorgestellt, mit denen sich im CIELAB-Farbraum (geräteunabhängig) definierte Farben in Ansteuerwerte (z. B. rgb-Werte) eines geeigneten Ausgabegerätes transformieren lassen. Die Methoden basieren auf geometrischen Modellen, die sich dadurch auszeichnen, dass sie zwischen einem Satz vorgegebener Referenzwerte, d. h. einem Satz von geräteunabhängigen Farbwerten und dazugehörigen Ansteuerwerten lokal interpolieren, um so die zwischen den Referenzwerten liegenden Farbwerte zu berechnen. Zur Interpolation werden die trilineare Interpolation, die kubischen Spline-Interpolation, die Tetraeder-Interpolation in einer Delaunay-Tetraedrisierung und die Shepard-Interpolation verwendet. Des Weiteren wurden zwei iterative Methoden entwickelt, bei denen die Referenzfarben nach jedem Iterationsschritt angepasst werden. Die von den Modellen benötigten Referenzwerte erhält man durch die Ausgabe einer Prüfvorlage mit einer entsprechenden Auswahl von Farben, definiert im Signalraum des Ausgabegerätes. Hierzu wurden verschiedene digitale Prüfvorlagen entwickelt, die kubisch-primitive Referenzfarbverteilungen, kubisch-primitive Referenzfarbverteilungen mit zusätzlichen Farbwerten am Rand des Gerätefarbraums und kubisch-raumzentrierte Referenzfarbverteilungen realisieren. Unter Verwendung eines Digital-Bilddrucksystems wurden die Reproduktionseigenschaften der verschiedenen Methoden bestimmt. Dabei zeigte sich, dass mit den Methoden im CIELAB-Farbraum definierte Farben mit einer Farbabweichung von im Mittel weniger als ΔE = 1,0 reproduziert werden können, was der Stabilität des verwendeten Drucksystems entspricht. Auf Basis dieser Untersuchungen wurden Methoden ausgewählt und mit ihnen ISO/IEC-Prüfvorlagen in photographischer Technik in Reflexion und Transmission hergestellt. -------------------------------------------------------------- The production of test charts makes it necessary to reproduce colours which are defined in a device independent colour space. This thesis presents methods to transform device independend CIELAB data into device dependend colour values (e. g. rgb-values) of an appropriate device. The methods are based on geometric models. The geometric models are using a set of reference data for a local interpolation, for example a set of device independent CIELAB data and corresponding signal values, for the calculation of values between the reference data. The interpolation uses the trilinear interpolation, the cubic spline interpolation, the tetrahedral interpolation in a Delaunay tetrahedrisation and the Shepard interpolation. Furthermore two iterative methods were developed, which are adjusting the reference colours after each iteration The reference data is determined by printing and measuring a test chart with a selection of colours defined in the device signal space. Different test charts were developed, which are using simple cubic reference colour arrangements, simple cubic reference colour arrangements with additional colour values near the boundary of the colour gamut and body-centered cubic reference colour arrangements. Using a digtal image printer the reproduction properties of the different methods were determined. It is shown that CIELAB colour data can be reproduced with a colour difference below ΔE = 1.0 which is in the range of the printer reproducibility. Based on this results the most accurate methods were used to produce ISO/IEC-test charts in reflection and transmission mode with photographic printing technology. KW - Farbwiedergabe KW - Gerätekalibrierung KW - Farbmessung KW - Prüfvorlage KW - Farbmetrik KW - Colour reproduction KW - Device calibration KW - Colour measurement KW - Test chart KW - colorimetry PY - 2006 SP - 1 EP - 178 PB - Technische Universität CY - Berlin AN - OPUS4-14809 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Reinholz, Uwe T1 - Darstellung eines Referenzmaterials für die ortsaufgelöste Wasserstoffanalytik in oberflächennahen Schichten mittels Kernreaktionsanalyse N2 - Obwohl Wasserstoff omnipräsent ist, ist seine Analytik anspruchsvoll und es stehen nur wenige analytische Verfahren zur Auswahl. Unter diesen nimmt die auf einer Kernreaktion von Wasserstoff und Stickstoff basierende N-15-Methode einen herausragenden Platz ein. Sie liefert eine ortsaufgelöste Wasserstoffkonzentration bis in den ppm-Bereich in oberflächennahen Schichten (kleiner 2 µm). Gegenstand der Arbeit sind die Darstellung der Theorie der N-15-Kernreaktionsanalyse (NRA), des experimentellen Aufbaus des entsprechenden Strahlrohrs am Ionenbeschleuniger der BAM und der Auswertung der Messergebnisse. Ziel ist die erstmalige Charakterisierung eines Referenzmaterials für die H-Analytik auf Basis von amorphen Silizium (aSi) auf einem Si[100]-Substrat. International wird von den metrologischen Instituten NIST [REE90] und IRMM [VAN87] je ein Referenzmaterial für die Heißextraktion in Form von Titanplättchen angeboten. Diese sind aber für die oberflächennahen Verfahren (NRA, ERDA, GDOES, SIMS) nicht nutzbar, da die oberflächennahe Konzentration von Wasserstoff in Titan nicht konstant ist. Die Homogenität der mittels CVD abgeschiedenen aSi:H-Schichten wurde untersucht. Dazu wurden pro Substrat für ca. 30 Proben die Wasserstofftiefenprofile gemessen, mittels eines innerhalb der Arbeit entstandenen Programms entfaltet und der statischen Auswertung unterzogen. Das Ergebnis waren Mittelwert und Standardabweichung der Wasserstoffkonzentration, sowie ein Schätzer für den Beitrag der Inhomogenität zur Meßunsicherheit. Die Stabilität des potentiellen Referenzmaterials wurde durch die Konstanz der Ergebnisse von Wiederholtungsmessungen der Wasserstoffkonzentrtion während der Applikation einer hohen Dosis von N-15 Ionen bewiesen. In einem internationalen Ringversuch wurde die Rückführbarkeit der Messergebnisse nachgewiesen. Teilnehmer waren 13 Labore aus 7 Ländern. Eingesetzt wurden N-15 und F-19 NRA, ERDA und SIMS. Besonderer Beachtung wurde der Bestimmung der Messunsicherheiten gewidmet. Für die Charakterisierung der aSi:H-Schichten wurden neben der NRA die Weißlichtinterferometrie, Ellipsometrie, Profilometrie und Röngenreflektometrie, sowie die IR- und Ramanspektroskopie genutzt. Die Stöchiometrie des eingesetzten Standardmaterials Kapton wurde mittels NMR-Spekroskopie und CHN-Analyse überprüft. KW - Referenzmaterial KW - Ionenstrahlanalytik KW - Kernreaktion KW - Wasserstoffkonzentration KW - Schichtdicke KW - Dünne Schicht KW - Amorphes Silizium PY - 2005 SP - 1 EP - 135 CY - Dresden AN - OPUS4-14810 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bremser, Wolfram T1 - Incertidumbre: Su estimación según las guías, y el papel de materiales de referencia (Messunsicherheit: Ermittlung nach Leitfäden und die Rolle von Referenzmaterialien) T2 - Materiales de referencia y comparaciones interlaboratorios KW - Messunsicherheit KW - Rückführbarkeit KW - Leitfäden GUM und EURACHEM KW - Referenzmaterial PY - 2007 SP - 23 EP - 29 PB - CENMA AN - OPUS4-14823 LA - spa AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Burkert, Andreas A1 - Fischer, Joachim A1 - Isecke, Bernd T1 - Bimetallkorrosion - Befestigungsmittel in Kontakt mit anderen Werkstoffen T2 - 3-Länder-Korrosionstagung "Befestigungsmittel im Hochbau - Korrosionsprobleme und Abhilfemaßnahmen" CY - Stuttgart, Deutschland DA - 2007-04-18 KW - Bimetallkorrosion KW - Nichtrostender Stahl KW - Atmosphärische Korrosion KW - Abhilfemaßnahmen PY - 2007 SP - 68 EP - 79 PB - GfKORR CY - Frankfurt am Main AN - OPUS4-14782 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Martin A1 - Malow, Marcus A1 - Krause, Ulrich A1 - Neumann, F. T1 - Untersuchung des Verhaltens von Steinkohlen unter dem Gesichtspunkt des Ex-Schutzes N2 - Die Kenntnis des Brenn- und Explosionsverhaltens von Stäuben ermöglicht die Festlegung geeig-neter Explosionsschutzmaßnahmen. Am Beispiel von Steinkohle- Mahlanlagen werden Untersu-chungen zur Bestimmung sicherheitstechnischer Kenngrößen (STK) von Stäuben vorgestellt. Hier-bei erfolgt zunächst die auf den Anwendungsfall abgestimmte Auswahl geeigneter Untersuchungs-verfahren und deren Anpassung an vorliegende Randbedingungen. Aufbauend auf die gewonnenen Erkenntnisse werden Schlussfolgerungen für den sicheren Betrieb von Steinkohle- Mahlanlagen getroffen. T2 - VGB-Konferenz "Kraftwerke im Wettbewerb 2007, Neue Kraftwerke - mit Erfahrung und Innovation die Zukunft gestalten" CY - Hamburg, Deutschland DA - 2007-04-25 KW - Explosionsschutz KW - Steinkohle KW - Mahlanlagen KW - Selbstentzündung PY - 2007 IS - CD-ROM SP - 15 Seiten PB - VGB PowerTech e.V. CY - Hamburg AN - OPUS4-14785 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Habel, Wolfgang A1 - Dantan, Nathalie A1 - Hofmann, Detlef A1 - Krebber, Katerina A1 - Schallert, Matthias T1 - Ausgewählte Anwendungsbeispiele faseroptischer Sensoren im Ingenieurbau und in der Geotechnik T2 - Ingenieurvermessung 07 CY - Graz, Österreich DA - 2007-04-17 PY - 2007 SP - 281 EP - 294 PB - Wichmann CY - Graz AN - OPUS4-14760 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wiggenhauser, Herbert A1 - Krause, Martin A1 - Maierhofer, Christiane A1 - Algernon, Daniel A1 - Gardei, André A1 - Gräfe, Boris A1 - Kohl, Christoph A1 - Lausch, Regine A1 - Mielentz, Frank A1 - Milmann, Boris A1 - Streicher, Doreen A1 - Zacher, Gerhard T1 - Grundlagen kombinierter zerstörungsfreier Prüfverfahren zur Untersuchung von Betonbauteilen T2 - Forschergruppe 384 Abschlusskolloquium CY - Bergisch Gladbach, Deutschland DA - 2007-05-03 PY - 2007 SP - 23 EP - 44 PB - BAM CY - Berlin AN - OPUS4-14805 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fischer, Joachim A1 - Held, N. T1 - So kommen Planer nicht ins Schwimmen - Schöck Isokorb Typ KST - nichtrostende Stähle in Schwimmhallenatmosphäre KW - Korrosion KW - Korrosionsschutz KW - Nichtrostender Stahl KW - Schwimmhallen PY - 2007 IS - 1 SP - 6 EP - 9 AN - OPUS4-14856 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Haid, August T1 - Explosive Stoffe PY - 1955 VL - 1 IS - Abschnitt 7/XIX SP - 1318 EP - 1323 PB - Ernst CY - Berlin ET - 28., neubearb. AN - OPUS4-15134 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rühl, Karl H. T1 - Formzahlen gekerbter Bauteile PY - 1955 VL - 1 IS - Abschnitt 6/VII SP - 960 EP - 964 PB - Ernst CY - Berlin ET - 28., neubearb. AN - OPUS4-15146 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schlosser, Franz T1 - Teer, Bitumen, bituminöse Baustoffe PY - 1955 VL - 1 IS - Abschnitt 7/XV SP - 1280 EP - 1287 PB - Ernst CY - Berlin ET - 28., neubearb. AN - OPUS4-15147 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hillebrand, K. T1 - Natürliche Steine und Erden PY - 1955 VL - 1 IS - Abschnitt 7/V SP - 1164 EP - 1175 PB - Ernst CY - Berlin ET - 28., neubearb. AN - OPUS4-15148 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mendrzyk, Hildegard T1 - Textilstoffe PY - 1955 VL - 1 IS - Abschnitt 7/XVI SP - 1287 EP - 1296 PB - Ernst CY - Berlin ET - 28., neubearb. AN - OPUS4-15149 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Richter, Manfred T1 - Optik PY - 1955 VL - 1 IS - Abschnitt 2/IV SP - 393 EP - 423 PB - Ernst CY - Berlin ET - 28., neubearb. AN - OPUS4-15150 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Wiederholt, Wilhelm A1 - Toeldte, W. T1 - Korrosion und Korrosionsschutz PY - 1955 VL - 1 IS - Abschnitt 7/I/C SP - 1039 EP - 1045 PB - Ernst CY - Berlin ET - 28., neubearb. AN - OPUS4-15151 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Toeldte, W. T1 - Anstrichmittel PY - 1955 VL - 1 IS - Abschnitt 7/XIII SP - 1273 EP - 1276 PB - Ernst CY - Berlin ET - 28., neubearb. AN - OPUS4-15152 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Umstätter, Hans T1 - Schmierstoffe PY - 1955 VL - 1 IS - Abschnitt 7/XII SP - 1267 EP - 1272 PB - Ernst CY - Berlin ET - 28., neubearb. AN - OPUS4-15153 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Werner, W. T1 - Kunststoffe und ihre Verarbeitung PY - 1955 VL - 1 IS - Abschnitt 7/XXI SP - 1340 EP - 1362 PB - Ernst CY - Berlin ET - 28., neubearb. AN - OPUS4-15154 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Vaupel, Otto T1 - Zerstörungsfreie Werkstoffprüfung PY - 1955 VL - 1 IS - Abschnitt 6/X SP - 981 EP - 1001 PB - Ernst CY - Berlin ET - 28., neubearb. AN - OPUS4-15155 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mendrzyk, Hildegard A1 - Riepe, Wilhelm T1 - Beiträge zur Bestimmung der Reinigungswirkung von Waschmitteln (Fortsetzung aus Heft 4/1954) PY - 1954 IS - 5 SP - 312 EP - 316 PB - Verl. Neuer Merkur CY - München AN - OPUS4-15070 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mendrzyk, Hildegard A1 - Riepe, Wilhelm T1 - Beiträge zur Bestimmung der Reinigungswirkung von Waschmitteln (Fortsetzung aus Heft 5/1954) PY - 1954 IS - 6 SP - 378 EP - 380 PB - Verl. Neuer Merkur CY - München AN - OPUS4-15073 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mendrzyk, Hildegard A1 - Riepe, Wilhelm T1 - Beiträge zur Bestimmung der Reinigungswirkung von Waschmitteln (Fortsetzung aus Heft 6/1954) PY - 1954 IS - 8 SP - 529 EP - 532 PB - Verl. Neuer Merkur CY - München AN - OPUS4-15075 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mendrzyk, Hildegard A1 - Riepe, Wilhelm T1 - Beiträge zur Bestimmung der Reinigungswirkung von Waschmitteln (Fortsetzung aus Heft 8/1954) PY - 1954 IS - 10 SP - 642 EP - 645 PB - Verl. Neuer Merkur CY - München AN - OPUS4-15076 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Steyer, S. A1 - Bandt, G. A1 - Völzke, Holger T1 - Bauartprüfung von Endlagerbehältern; Anforderungen an die Kompatibilität von Abfallprodukt und Behälter T2 - KONTEC 2007 CY - Dresden, Deutschland DA - 2007-03-21 KW - Behälter KW - Radioaktive Abfälle KW - Bauartprüfung KW - Endlager Konrad PY - 2007 SP - 868 PB - Gesellschaft für technische Kommunikation mbH / Kerntechnische Gesellschaft CY - Dresden AN - OPUS4-15008 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz ED - M. Papadrakakis, ED - D.C. Charmpis, ED - N.D. Lagaros, ED - Tsompanakis, Y. T1 - Simple and advanced boundary-element method for the soil and its application to railway dynamics T2 - COMPDYN 2007 CY - Rethymno, Crete, Greece DA - 2007-06-13 KW - Finite-element boundary-element method KW - Explicit Green´s functions KW - Track vibration KW - Tunnel vibration KW - Vehicle-track-soil interaction KW - Radiation damping PY - 2007 SP - 1 EP - 12 CY - Athen AN - OPUS4-15015 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kloß, Heinz A1 - Wäsche, Rolf T1 - Analytical approach for wear prediction of metallic and ceramic materials in tribological applications T2 - ECOTRIB 2007 CY - Ljubljana, Slovenia DA - 2007-06-12 KW - Wear KW - Surface temperature KW - Activation energy KW - Simulation KW - Movable cellular automata (MCA) PY - 2007 VL - I SP - 223 EP - 234 PB - Slovenská Akadémia Vied CY - Ljubljana AN - OPUS4-14972 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Isecke, Bernd A1 - Beck, Matthias T1 - Electrochemical investigations of corrosion with small cathodes in steel reinforced concrete N2 - Corrosion of steel reinforcement in concrete exposed to chloride containing environments is a serious problem in civil engineering practice. The standards and guidelines contain only minimum requirements regarding concrete quality and concrete cover. In very critical cases, for example the ingress of chlorides, the application of different coatings is currently the only possibility to protect the reinforced concrete structures. In this case the modelling of reinforcement corrosion would be more practical. One sub-project of a DFG-research project (FOR 537) is currently performed at the Federal Institute for Materials Research and Testing (BAM). Aim of the sub-project is the description of corrosion propagation and the characterization of the corrosion on specimens with small and large cathodes, by electrochemical parameters. The electrochemical parameters are determined by suitable electrochemical measurements, considering concrete parameters as well as different environmental conditions. T2 - EUROCORR 2007 CY - Freiburg im Breisgau, Germany DA - 2007-09-09 PY - 2007 N1 - Serientitel: EFC-Event – Series title: EFC-Event IS - 289 SP - 1 EP - 17 PB - DECHEMA CY - Frankfurt am Main AN - OPUS4-15820 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Isecke, Bernd A1 - Eichler, Thorsten A1 - Burkert, Andreas T1 - Investigations on the repassivation of carbon steel in consequence of cathodic polarization N2 - Pitting corrosion of carbon steel and iron in chloride containing alkaline environment is already well investigated, although a couple of questions are not clarified satisfactorily. The critical chloride content for steel in concrete and the critical chloride to hydroxide ion ratio for steel in alkaline solutions is still a major concern, considering chloride induced corrosion problems of steel in concrete. Another not satisfactorily clarified point is the repassivation of carbon steel in consequence of cathodic polarization. In the recent literature some indications are shown that repassivation occurs after a certain time of polarization. GLASS [4-9] and PEDEFERRI [1-3] draw the conclusion that the ennoblement of open circuit potentials (OCP) indicates re-passivation effects due to cathodic polarization. SAGÜÉS [10] carried out potentiodynamic repassivation tests and draws the conclusion that the repassivation potential Er is nearly independent of the solution composition, but influenced by severity of corrosion attack and is in the potential range from - 0.8 V to - 0.4 V vs. Saturated Calomel Electrode (SCE). The transferability of SAGÜÉS’ results to questions concerning cathodic protection (cp) is questionable, as potentiodynamic polarization tests (PPT) give no information on changes induced by long time polarization. Therefore, the investigations discussed in this paper aim to clarify, to what extend the re-passivation of carbon steel due to cathodic polarization occurs, and if the ennoblement of OCP is a sufficient indication for repassivation. In a first step the corrosion state of five nominal equal test specimens was determined by electrochemical techniques, i.e. electrochemical noise measurements (ENM) and electrochemical impedance spectroscopy (EIS). After determining the initial corrosion state by evaluating the charge transfer resistance and the polarization resistance respectively as well as evaluating potential and current noise signals, the specimens were polarized cathodically. Impedance data were recorded previous to, during and after polarization. The impedance data were evaluated by equivalent circuit fitting with special attention to charge transfer resistances and diffusion properties. The results show that reduction of oxides and oxygen diffusion during cathodic polarization has strong impact on the system’s behavior. T2 - EUROCORR 2007 CY - Freiburg im Breisgau, Germany DA - 2007-09-09 KW - Concrete KW - Carbon steel KW - Cathodic protection KW - Re-passivation KW - Pitting corrosion PY - 2007 N1 - Serientitel: EFC-Event – Series title: EFC-Event IS - 289 SP - 1 EP - 15 PB - DECHEMA CY - Frankfurt am Main AN - OPUS4-15822 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simon, Franz-Georg A1 - Biermann, Vera T1 - Langzeitverhalten von elementarem Eisen und Hydroxylapatit in reaktiven Wänden für die Grundwassersanierung T2 - Internationales Bergbausymposium WISMUT 2007 CY - Gera, Deutschland DA - 2007-09-10 KW - Grundwassersanierung KW - Uran KW - Reaktive Wände KW - Hydroxylapatit PY - 2007 SP - 361 EP - 367 CY - Chemnitz AN - OPUS4-15825 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Anders, Stefan T1 - Residual Stresses in Composite-Metal Structures for High Pressure H2 Gas Cylinders T2 - CANCOM 2007, 6th Canadian-International Composites Conference "Development and Commercialization of Composite Materials and Technologies CY - Winnipeg, Manitoba, Canada DA - 2007-08-14 KW - Composite-Hybrid-Structure KW - Stress Analysis KW - Residual Stress KW - High Pressure Gas Cylinders PY - 2007 SP - 1 EP - 12 CY - Winnipeg, Manitoba, Canada AN - OPUS4-15838 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Binkowski, Sigrid A1 - Woydt, Mathias A1 - Dietrich, E. T1 - Unusual hardening of 100Cr6 steel in a defective ceramic hybrid roller bearing N2 - Metallographic failure analysis has been carried out on a defective ceramic hybrid roller bearing to determine the cause of the defect. PY - 2005 UR - http://www.struers.com/resources/elements/12/79040/e-Structure%208E.pdf IS - e-8 SP - 2 EP - 5 PB - Struers CY - Willich AN - OPUS4-15497 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Binkowski, Sigrid A1 - Woydt, Mathias A1 - Dietrich, E. T1 - Durcissement inhabituel de l'acier 100Cr6 dans un roulement à rouleaux de céramique hybride défectueux N2 - Une analyse de défaut métallographique a été accomplie sur un palier hybride céramique défectueux afin de déterminer la cause du défaut. PY - 2005 UR - http://www.struers.com/resources/elements/12/79042/e-Structure%208F.pdf IS - e-8 SP - 2 EP - 5 PB - Struers CY - Willich AN - OPUS4-15498 LA - fra AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Richter, Manfred ED - Richter, Manfred T1 - Entwicklungstendenzen und Probleme der Farbmeßtechnik T2 - Internationale Farbtagung CY - Luzern, Schweiz DA - 1965-06-01 PY - 1965 VL - 1 SP - 433 EP - 444 PB - Musterschmidt CY - Göttingen AN - OPUS4-15485 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weise, Hans-Peter ED - Richter, M. T1 - Vergleich dreier skandinavischer Farbsysteme mit dem der DIN-Farbenkarte PY - 1966 VL - 1 SP - 389 EP - 398 PB - Musterschmidt CY - Göttingen AN - OPUS4-15486 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Strogies, Wolfgang A1 - Thomescheit, Alfred ED - Richter, Manfred T1 - Klischeeberechnung für den autotypischen Druck nach Neugebauer T2 - Internationale Farbtagung ; Journées Internationales de la Couleur ; International Colour Meeting CY - Luzern, Schweiz DA - 1965-06-01 PY - 1966 VL - 2 SP - 871 EP - 878 PB - Musterschmidt CY - Göttingen AN - OPUS4-15487 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hansen, Max T1 - Die Löslichkeit von Kupfer in Silber PY - 1930 IS - 10 SP - 29 EP - 33 PB - Springer CY - Berlin AN - OPUS4-15529 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - von Göler, A1 - Sachs, Georg T1 - Die Veredelung einer Aluminiumlegierung im Röntgenbild PY - 1930 IS - 10 SP - 33 EP - 43 PB - Springer CY - Berlin AN - OPUS4-15530 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sachs, Georg T1 - Schmiedespannungen, Vergütungsspannungen und Wärmespannungen PY - 1930 IS - 10 SP - 43 EP - 48 PB - Springer CY - Berlin AN - OPUS4-15531 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Arndt, H. T1 - Der Einfluß des Einwalzens von Rohren auf gewöhnliches Kesselblech und auf Izett-Blech PY - 1930 IS - 10 SP - 48 EP - 53 PB - Springer CY - Berlin AN - OPUS4-15533 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Friedrich Wilhelm A1 - Sachs, Georg A1 - Sieglerschmidt, H. T1 - Elastizität, statische Versuche und Dauerprüfung PY - 1930 IS - 10 SP - 53 EP - 58 PB - Springer CY - Berlin AN - OPUS4-15534 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sachs, Georg A1 - Stenzel, W. T1 - Die Dehnung von Blechen PY - 1930 IS - 10 SP - 58 EP - 68 PB - Springer CY - Berlin AN - OPUS4-15535 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sachs, Georg A1 - Sieglerschmidt, H. T1 - Prüfung von Seildrähten durch Zug- und Biegeversuche PY - 1930 IS - 10 SP - 68 EP - 78 PB - Springer CY - Berlin AN - OPUS4-15536 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nix, F. C. A1 - Schmid, Erich T1 - Über die Gußtextur von Metallen und Legierungen PY - 1930 IS - 10 SP - 79 EP - 87 PB - Springer CY - Berlin AN - OPUS4-15537 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmid, Erich A1 - Wassermann, G. T1 - Über die Textur gezogener Magnesium- und Zinkdrähte PY - 1930 IS - 10 SP - 87 EP - 89 PB - Springer CY - Berlin AN - OPUS4-15538 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - von Göler, A1 - Sachs, Georg T1 - Walz- und Rekristallisationstextur regulär-flächenzentrierter Metalle - III PY - 1930 IS - 10 SP - 90 EP - 93 PB - Springer CY - Berlin AN - OPUS4-15539 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - von Göler, A1 - Sachs, Georg T1 - Walz- und Rekristallisationstextur regulär-flächenzentrierter Metalle - IV PY - 1930 IS - 10 SP - 94 EP - 98 PB - Springer CY - Berlin AN - OPUS4-15540 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - von Göler, A1 - Sachs, Georg T1 - Walz- und Rekristallisationstextur regulär-flächenzentrierter Metalle - V PY - 1930 IS - 10 SP - 98 EP - 101 PB - Springer CY - Berlin AN - OPUS4-15541 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Polanyi, M. A1 - Schmid, Erich T1 - Zur Frage der Plastizität - Verformung bei tiefen Temperaturen PY - 1930 IS - 10 SP - 101 EP - 104 PB - Springer CY - Berlin AN - OPUS4-15542 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Boas, W. A1 - Schmid, Erich T1 - Bemerkungen zur Kristallplastizität PY - 1930 IS - 10 SP - 105 EP - 108 PB - Springer CY - Berlin AN - OPUS4-15543 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - von Göler, A1 - Sachs, Georg T1 - Zugversuche an Kristallen aus Kupfer und alpha-Messing PY - 1930 IS - 10 SP - 108 EP - 126 PB - Springer CY - Berlin AN - OPUS4-15544 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Masima, M. A1 - Sachs, Georg T1 - Wärmeeffekte bei der Dehnung von Messingkristallen PY - 1930 IS - 10 SP - 127 EP - 128 PB - Springer CY - Berlin AN - OPUS4-15545 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Boas, W. A1 - Schmid, Erich T1 - Über die Temperaturabhängigkeit der kritischen Schubspannung von Kadmiumkristallen PY - 1930 IS - 10 SP - 128 EP - 130 PB - Springer CY - Berlin AN - OPUS4-15546 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmid, Erich A1 - Vaupel, Otto T1 - Festigkeit und Plastizität von Steinsalzkristallen PY - 1930 IS - 10 SP - 130 EP - 139 PB - Springer CY - Berlin AN - OPUS4-15547 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Deiß, Eugen T1 - Zur Probenahme und Analyse von Rotguß und anderen zur Seigerung neigenden Legierungen PY - 1930 IS - 10 SP - 139 EP - 142 PB - Springer CY - Berlin AN - OPUS4-15548 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Zunker, P. T1 - Einfluß der Temperatur und der Abkühlungsverhältnisse beim Gießen von Zink PY - 1930 IS - 10 SP - 3 EP - 26 PB - Springer CY - Berlin AN - OPUS4-15527 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmid, Erich T1 - Gefügeuntersuchungen an gegossenen Metallen und Legierungen PY - 1930 IS - 10 SP - 26 EP - 29 PB - Springer CY - Berlin AN - OPUS4-15528 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gonell, Hans-Wolfgang T1 - Über die Erkennung von Hochofenschlacke in Zementen PY - 1929 IS - 7 SP - 24 EP - 29 PB - Springer CY - Berlin AN - OPUS4-15609 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rodt, V. T1 - Wasseraufnahme von Portlandzement bei Luftlagerung PY - 1929 IS - 7 SP - 29 EP - 31 PB - Springer CY - Berlin AN - OPUS4-15610 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burchartz, Heinrich T1 - Kann Traß durch anderes Steinmehl ersetzt werden? PY - 1929 IS - 7 SP - 32 EP - 37 PB - Springer CY - Berlin AN - OPUS4-15611 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burchartz, Heinrich T1 - Der Einfluß des Zusatzes von Gesteins- und Tonmehl auf die Erhärtung bzw. Festigkeit von Zement- und Kalkmörtel PY - 1929 IS - 7 SP - 38 EP - 41 PB - Springer CY - Berlin AN - OPUS4-15612 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burchartz, Heinrich T1 - Dichtigkeit und Festigkeit von Kiesbeton im Vergleich zu Kiessplittbeton PY - 1929 IS - 7 SP - 41 EP - 44 PB - Springer CY - Berlin AN - OPUS4-15613 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rodt, V. T1 - Beitrag zur Feststellung der mechanischen Zusammensetzung von Mörtel und Beton - Mischverhältnis von Bindemittel zum Zuschlagstoff PY - 1929 IS - 7 SP - 44 EP - 47 PB - Springer CY - Berlin AN - OPUS4-15614 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Saenger, Georg T1 - Vergleichsversuche mit Loch- und Maschensieben PY - 1929 IS - 7 SP - 105 EP - 107 PB - Springer CY - Berlin AN - OPUS4-15629 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burchartz, Heinrich T1 - Versuche zur Bestimmung der Mahlfeinheit von Kohlenstaub PY - 1929 IS - 7 SP - 108 EP - 114 PB - Springer CY - Berlin AN - OPUS4-15630 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gonell, Hans-Wolfgang T1 - Ein Windsichtverfahren zur Bestimmung der Kornzusammensetzung staubförmiger Stoffe PY - 1929 IS - 7 SP - 114 EP - 121 PB - Springer CY - Berlin AN - OPUS4-15631 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gonell, Hans-Wolfgang T1 - Zur Frage der Ausscheidung der Asche aus Kohlenstaub PY - 1929 IS - 7 SP - 122 EP - 125 PB - Springer CY - Berlin AN - OPUS4-15632 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Memmler, Karl T1 - Die Eigenschaften des Hartmessings MS 58 (Schraubenmessing) PY - 1929 IS - 8 SP - 1 EP - 58 PB - Springer CY - Berlin AN - OPUS4-15633 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hansen, Max A1 - Sachs, Georg T1 - Die elektrische Leitfähigkeit von Silberlegierungen PY - 1929 IS - 5 SP - 152 EP - 154 PB - Springer CY - Berlin AN - OPUS4-15569 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Deiß, Eugen T1 - Zur Analyse der Stellite, Akrite und ähnlich zusammengesetzter Legierungen PY - 1929 IS - 5 SP - 154 EP - 157 PB - Springer CY - Berlin AN - OPUS4-15570 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schürmann, E. A1 - Böhm, W. T1 - Die Bestimmung von Lithium in Seleronmetall und ähnlichem Aluminiumlegierungen PY - 1929 IS - 5 SP - 158 EP - 162 PB - Springer CY - Berlin AN - OPUS4-15571 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schürmann, E. A1 - Blumenthal, Herbert T1 - Über die Prüfung der Zinnauflage von Kupferdrähten PY - 1929 IS - 5 SP - 162 EP - 164 PB - Springer CY - Berlin AN - OPUS4-15572 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Blumenthal, Herbert T1 - Über ein Verfahren zur Bestimmung kleinster Antimonmengen im Kupfer PY - 1929 IS - 5 SP - 164 EP - 166 PB - Springer CY - Berlin AN - OPUS4-15573 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Deiß, Eugen A1 - Schikorr, Gerhard T1 - Über das Ferrohydroxyd (Eisen-2-hydroxyd) PY - 1929 IS - 5 SP - 167 EP - 170 PB - Springer CY - Berlin AN - OPUS4-15574 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burgeni, A. A1 - Weissenberg, K. T1 - Symmetriegruppen mit zwei Translationen PY - 1929 IS - 5 SP - 171 EP - 189 PB - Springer CY - Berlin AN - OPUS4-15575 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schulze, Bruno T1 - Beitrag zur ältesten Geschichte der Papiererzeugung - (ein Papier aus dem 3. Jahrhundert n. Chr.) PY - 1929 IS - 6 SP - 1 EP - 3 PB - Springer CY - Berlin AN - OPUS4-15576 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Korn, Rudolph T1 - Einfluß des Wasserzeichens auf die Festigkeitseigenschaften von Wertzeichenpapieren PY - 1929 IS - 6 SP - 4 PB - Springer CY - Berlin AN - OPUS4-15577 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Herzberg, Wilhelm T1 - Einfluß höherer Wärmegrade auf die Festigkeitseigenschaften von Sackpapier PY - 1929 IS - 6 SP - 4 EP - 6 PB - Springer CY - Berlin AN - OPUS4-15578 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burchartz, Heinrich T1 - Vergleich der Würfelfestigkeit von Beton zu der Druckfestigeit des Betons im Bauwerk PY - 1929 IS - 7 SP - 47 EP - 54 PB - Springer CY - Berlin AN - OPUS4-15619 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burchartz, Heinrich T1 - Etwas über Mörtelsande PY - 1929 IS - 7 SP - 54 EP - 57 PB - Springer CY - Berlin AN - OPUS4-15620 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gonell, Hans-Wolfgang T1 - Beitrag zur Frage der Beeinflussung des Abbindens und Erhärtens von Portlandzement durch Zusätze zum Anmachewasser, insbesondere durch Zuckerlösung - vorläufige Mitteilung PY - 1929 IS - 7 SP - 58 EP - 65 PB - Springer CY - Berlin AN - OPUS4-15621 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burchartz, Heinrich T1 - Versuche über den Einfluß von Kalischachtlauge auf das Abbinden und Erhärten von Zement PY - 1929 IS - 7 SP - 65 EP - 71 PB - Springer CY - Berlin AN - OPUS4-15622 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rodt, V. T1 - Die Einwirkung von Schwefelwasserstoff auf Kalkmörtel, Zementmörtel und Beton PY - 1929 IS - 7 SP - 71 EP - 73 PB - Springer CY - Berlin AN - OPUS4-15623 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burchartz, Heinrich T1 - Kalkpulver als Ersatz für Kalkteig in der Traßnormenmischung PY - 1929 IS - 7 SP - 73 EP - 78 PB - Springer CY - Berlin AN - OPUS4-15624 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rodt, V. T1 - Beitrag zur Bestimmung und Auswertung der Kohlensäure im Wasser - (eine kritische Studie) PY - 1929 IS - 7 SP - 79 EP - 86 PB - Springer CY - Berlin AN - OPUS4-15625 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burchartz, Heinrich T1 - Das Verfahren zur Prüfung von Mauersteinen auf Druckfestigkeit PY - 1929 IS - 7 SP - 87 EP - 92 PB - Springer CY - Berlin AN - OPUS4-15626 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burchartz, Heinrich T1 - Die Ursachen des Rissigwerdens von Steinholzfußbodenbelag PY - 1929 IS - 7 SP - 92 EP - 95 PB - Springer CY - Berlin AN - OPUS4-15627 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burchartz, Heinrich A1 - Saenger, Georg T1 - Versuche mit Hochofenstückschlacke als Gleisbettungsstoff PY - 1929 IS - 7 SP - 95 EP - 105 PB - Springer CY - Berlin AN - OPUS4-15628 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wilke, P. T1 - Über einige Versuche mit dem Berstdruckprüfer Schopper-Dalén bei 8,04 und 100qcm Einspannfläche PY - 1929 IS - 6 SP - 6 EP - 7 PB - Springer CY - Berlin AN - OPUS4-15579 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Herzberg, Wilhelm T1 - Erfahrungen bei der Prüfung von Rohdachpappe PY - 1929 IS - 6 SP - 8 EP - 9 PB - Springer CY - Berlin AN - OPUS4-15580 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dalén, Gustaf A1 - Wilke, P. T1 - Ermittlung der Lichtechtheit farbiger Papiere durch Belichtung mit der Quarz-Quecksilberlampe PY - 1929 IS - 6 SP - 9 EP - 12 PB - Springer CY - Berlin AN - OPUS4-15581 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Korn, Rudolph T1 - Sklerenchym in Strohzellstoffen PY - 1929 IS - 6 SP - 13 EP - 15 PB - Springer CY - Berlin AN - OPUS4-15582 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Korn, Rudolph T1 - Sklerenchymflecke in Papier PY - 1929 IS - 6 SP - 15 EP - 17 PB - Springer CY - Berlin AN - OPUS4-15583 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Korn, Rudolph T1 - Die Sutermeister-Lösung in der Papiermikroskopie PY - 1929 IS - 6 SP - 17 EP - 18 PB - Springer CY - Berlin AN - OPUS4-15584 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Herzberg, Wilhelm T1 - Metallschädliche Bestandteile in Papier PY - 1929 IS - 6 SP - 18 PB - Springer CY - Berlin AN - OPUS4-15585 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Korn, Rudolph T1 - Quantitative Bestimmung von Holzschiff in Papier auf chemischem Wege nach Cross, Bevan und Briggs PY - 1929 IS - 6 SP - 19 EP - 23 PB - Springer CY - Berlin AN - OPUS4-15586 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schulze, Bruno T1 - Quantiative Bestimmung von Wolle in Roh- und Wollfilzpappen auf chemischem Wege PY - 1929 IS - 6 SP - 23 EP - 24 PB - Springer CY - Berlin AN - OPUS4-15587 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Herzog, G. T1 - Über den Einfluß der Luftfeuchtigkeit auf die Eigenschaften der Faserstoffe und über Messung der Luftfeuchtigkeit PY - 1929 IS - 6 SP - 24 EP - 30 PB - Springer CY - Berlin AN - OPUS4-15588 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald T1 - Das Gußeisen als Werkstoff und Baustoff PY - 1929 IS - 5 SP - 1 EP - 11 PB - Springer CY - Berlin AN - OPUS4-15549 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald T1 - Flußstähle mit geringer Alterungseigenschaft PY - 1929 IS - 5 SP - 12 EP - 22 PB - Springer CY - Berlin AN - OPUS4-15550 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hansen, Max T1 - Über die Sättigungsgrenze des Alpha (Cu-Sn)-Mischkristalls PY - 1929 IS - 5 SP - 23 EP - 25 PB - Springer CY - Berlin AN - OPUS4-15551 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hansen, Max T1 - Zur Kenntnis der Zinnbronzen PY - 1929 IS - 5 SP - 25 EP - 29 PB - Springer CY - Berlin AN - OPUS4-15552 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hansen, Max T1 - Der Aufbau der aluminiumreichen Silber-Aluminiumlegierungen PY - 1929 IS - 5 SP - 29 EP - 38 PB - Springer CY - Berlin AN - OPUS4-15553 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - von Göler, A1 - Sachs, Georg T1 - Zur Entstehung des Gußgefüges PY - 1929 IS - 5 SP - 38 EP - 43 PB - Springer CY - Berlin AN - OPUS4-15554 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Seidl, Erich T1 - Der Einfluß der chemischen und kristallographischen Beschaffenheit des Gußmaterials auf da Verhalten beim Walzen - erläutert an Industrie-Aluminium, -Kupfer und -Zink PY - 1929 IS - 5 SP - 43 EP - 50 PB - Springer CY - Berlin AN - OPUS4-15555 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - von Göler, A1 - Sachs, Georg T1 - Gefüge und Festigkeitseigenschaften von sehr reinem Aluminium PY - 1929 IS - 5 SP - 50 EP - 53 PB - Springer CY - Berlin AN - OPUS4-15556 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - von Göler, A1 - Sachs, Georg T1 - Festigkeitseigenschaften von Metallkristallen PY - 1929 IS - 5 SP - 54 EP - 61 PB - Springer CY - Berlin AN - OPUS4-15557 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Sieglerschmidt, H. T1 - Die Ausdehnung des Zinks bei steigenden Temperaturen PY - 1929 IS - 5 SP - 62 EP - 63 PB - Springer CY - Berlin AN - OPUS4-15558 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sommer, Herbert T1 - Die Wirkung atmosphärischer Einflüsse auf Faserstoffe PY - 1929 IS - Sonderheft 6 SP - 30 EP - 51 PB - Springer CY - Berlin AN - OPUS4-15589 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sommer, Herbert T1 - Der Nachweis chemischer Schädigung bei Erzeugnissen aus Pflanzenfasern PY - 1929 IS - 6 SP - 51 EP - 55 PB - Springer CY - Berlin AN - OPUS4-15590 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sommer, Herbert T1 - Zur Frage der Gleichmäßigkeitsprüfung von Gespinsten PY - 1929 IS - 6 SP - 55 EP - 60 PB - Springer CY - Berlin AN - OPUS4-15591 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sommer, Herbert T1 - Die technologischen Eigenschaften der nach dem Einkardenverfahren hergestellten Jutegarne PY - 1929 IS - 6 SP - 60 EP - 62 PB - Springer CY - Berlin AN - OPUS4-15592 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Herzog, G. T1 - Schäden an Papierfilzen PY - 1929 IS - 6 SP - 62 EP - 65 PB - Springer CY - Berlin AN - OPUS4-15593 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sommer, Herbert T1 - Über den Wert des Glühverfahrens bei der Bestimmung des Baumwollgehalts in Asbestzeugnissen PY - 1929 IS - 6 SP - 65 EP - 67 PB - Springer CY - Berlin AN - OPUS4-15594 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Frederking, H. T1 - Einige Neuerungen bei photographischem Kopierprozessen PY - 1929 IS - 6 SP - 67 EP - 69 PB - Springer CY - Berlin AN - OPUS4-15595 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Marcusson, J. A1 - Bauerschäfer, W. T1 - Katalytische Bildung von Erdölkohlenwasserstoffen aus Fetten PY - 1929 IS - 6 SP - 69 EP - 70 PB - Springer CY - Berlin AN - OPUS4-15596 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Marcusson, J. A1 - Bauerschäfer, W. T1 - Autoxydation der Mineralöle PY - 1929 IS - 6 SP - 70 EP - 71 PB - Springer CY - Berlin AN - OPUS4-15597 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Marcusson, J. T1 - Die Vorgänge beim Erhitzen und Eintrocknen fetter Öle PY - 1929 IS - 6 SP - 71 EP - 78 PB - Springer CY - Berlin AN - OPUS4-15598 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmid, Erich A1 - Wassermann, G. T1 - Über die mechanische Zwillingsbildung von Zinkkristallen PY - 1929 IS - 5 SP - 63 EP - 68 PB - Springer CY - Berlin AN - OPUS4-15559 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schiebold, Ernst A1 - Richter, G. T1 - Studien über den Zugversuch an kristallinen Stoffen PY - 1929 IS - 5 SP - 68 EP - 96 PB - Springer CY - Berlin AN - OPUS4-15560 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Wilhelm T1 - Abhängigkeit der elastischen Dehnungszahl Alpha des Kupfers von der Vorbehandlung und Versuchsführung PY - 1929 IS - 5 SP - 97 EP - 113 PB - Springer CY - Berlin AN - OPUS4-15561 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sachs, Georg A1 - Shoji, H. T1 - Zug-Druckversuche an Messingkristallen (Bauschingereffekt) PY - 1929 IS - 5 SP - 113 EP - 122 PB - Springer CY - Berlin AN - OPUS4-15562 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Seidl, Erich T1 - Kerbwirkung in Technik und Wissenschaft PY - 1929 IS - 5 SP - 122 EP - 130 PB - Springer CY - Berlin AN - OPUS4-15563 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sachs, Georg T1 - Versuche zum Walz- und Schmiedevorgang PY - 1929 IS - 5 SP - 130 EP - 137 PB - Springer CY - Berlin AN - OPUS4-15564 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sachs, Georg T1 - Zur Theorie des Ziehvorganges PY - 1929 IS - Sonderheft 5 SP - 137 EP - 138 PB - Springer CY - Berlin AN - OPUS4-15565 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sachs, Georg T1 - Der Nachweis innerer Spannungen in Stangen und Rohren PY - 1929 IS - 5 SP - 138 EP - 144 PB - Springer CY - Berlin AN - OPUS4-15566 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sachs, Georg T1 - Innere Spannungen in Metallen PY - 1929 IS - 5 SP - 144 EP - 151 PB - Springer CY - Berlin AN - OPUS4-15567 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - von Göler, A1 - Sachs, Georg T1 - Innere Spannungen im Röntgenbild PY - 1929 IS - 5 SP - 151 EP - 152 PB - Springer CY - Berlin AN - OPUS4-15568 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Marcusson, J. T1 - Nachweis von Holzöl in Ölgemischen PY - 1929 IS - 6 SP - 78 EP - 79 PB - Springer CY - Berlin AN - OPUS4-15599 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schlüter, H. T1 - Vereinheitlichung der Ölprüfungsverfahren PY - 1929 IS - 6 SP - 79 EP - 87 PB - Springer CY - Berlin AN - OPUS4-15600 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Marcusson, J. T1 - Die Analyse der Kaltasphalte PY - 1929 IS - 6 SP - 87 EP - 88 PB - Springer CY - Berlin AN - OPUS4-15601 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Marcusson, J. T1 - Der chemische Aufbau der Braunkohlen PY - 1929 IS - 6 SP - 89 EP - 90 PB - Springer CY - Berlin AN - OPUS4-15602 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nitsche, Rudolf T1 - Siegellackprüfungen PY - 1929 IS - 6 SP - 90 EP - 92 PB - Springer CY - Berlin AN - OPUS4-15603 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burchartz, Heinrich T1 - Die geschichtliche Entwicklung der Zementprüfung nach den Normen PY - 1929 IS - 7 SP - 3 EP - 10 PB - Springer CY - Berlin AN - OPUS4-15604 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burchartz, Heinrich T1 - Ergebnisse der Prüfung hochwertiger Portlandzemente nach den Normen PY - 1929 IS - 7 SP - 10 EP - 14 PB - Springer CY - Berlin AN - OPUS4-15605 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gonell, Hans-Wolfgang T1 - Tonerdezement PY - 1929 IS - 7 SP - 14 EP - 17 PB - Springer CY - Berlin AN - OPUS4-15606 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gonell, Hans-Wolfgang T1 - Über die Ursache der Abbindestörungen bei Tonerdezement PY - 1929 IS - 7 SP - 18 EP - 19 PB - Springer CY - Berlin AN - OPUS4-15607 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burchartz, Heinrich T1 - Versuche mit Hochofenzement PY - 1929 IS - 7 SP - 19 EP - 24 PB - Springer CY - Berlin AN - OPUS4-15608 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meng, Birgit A1 - Fontana, Patrick A1 - Müller, Urs A1 - Kühne, Hans-Carsten T1 - Nanotechnologische Anwendungen im Baustoffbereich T2 - Nanotechnologie und Bauwesen (NanoTecture) CY - Düsseldorf DA - 2006-12-05 KW - Nanotechnologie KW - Analytik KW - Gefüge KW - Zement KW - Beton PY - 2006 SP - 13 EP - 27 CY - Düsseldorf AN - OPUS4-15703 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Helmerich, Rosemarie A1 - Röllig, Mathias A1 - Maierhofer, Christiane A1 - Schultz, A. A1 - Vielhaber, J. A1 - Loehr, M. T1 - Non-destructive CFRP-bond evaluation T2 - 8th International Symposium on Fiber Reinforced Polymer Reinforcement for Concrete Structures (FRPRCS-8) CY - Patras, Greece DA - 2007-07-16 KW - Bond behaviour KW - Impulse thermography KW - Effectiveness of repair KW - CFRP-strengthening KW - Large scale testing KW - Validation KW - Acoustic emission KW - Combination of NDT-methods PY - 2007 SP - 106-107 (2-24) CY - Patras, Greece AN - OPUS4-15706 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maierhofer, Christiane A1 - Arndt, Ralf A1 - Röllig, Mathias A1 - Helmerich, Rosemarie A1 - Walther, A. A1 - Hillemeier, B. A1 - Rieck, C. T1 - Quantification of Voids and Elaminations in Real Concrete and Masonry Structures with Active Thermography: Case Studies T2 - 8th International Conference on Quantitative InfraRed Thermography (QIRT 2006) CY - Padova, Italy DA - 2006-06-28 KW - Non-destructive testing in civil engineering KW - Active thermography KW - Pulse-phase thermography KW - Plaster KW - Tiles KW - Asphalt KW - Numerical simulation PY - 2006 UR - http://qirt.gel.ulaval.ca/archives/qirt2006/papers/049.pdf SP - 49, 1 EP - 10 (?) CY - Padova, Italy AN - OPUS4-15710 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bierett, Georg T1 - Ein Beitrag zur Frage der Spannungsstörungen in Bolzenverbindungen - experimentelle Untersuchung eines Augenstabes PY - 1931 IS - 15 SP - 3 EP - 39 PB - Springer CY - Berlin AN - OPUS4-15676 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Memmler, Karl A1 - Laute, K. T1 - Untersuchungen metallischer Baustoffe auf Schwingungsfestigkeit mit der Hochfrequenz-Zug-Druck-Maschine (Bauart Schenck) PY - 1931 IS - 15 SP - 39 EP - 70 PB - Springer CY - Berlin AN - OPUS4-15677 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schallert, Matthias T1 - Static and dynamic strain measurements of deep foundation concrete structures by embedded fibre-optic Fabry-Perot sensors T2 - 5th BSSM International Conference on Advances in Experimental Mechanics - Young Stress Analyst Competition 2007 CY - Manchester, UK DA - 2007-09-04 PY - 2007 SP - 13 EP - 18 CY - Manchester, UK AN - OPUS4-15815 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wassermann, G. T1 - Einfluß der alpha-gamma-Umwandlung eines irreversiblen Nickelstahls auf Kristallorientierung und Zugfestigkeit PY - 1934 IS - 23 SP - 16 EP - 21 PB - Springer CY - Berlin AN - OPUS4-15779 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Weerts, J. T1 - Die Eigenschaften von Monel-Metall und ähnlichen Kupfer-Nickellegierungen PY - 1934 IS - 23 SP - 21 EP - 34 PB - Springer CY - Berlin AN - OPUS4-15780 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weerts, J. T1 - Über die Umwandlungsvorgänge im beta-Messing und in beta-Silber-Zink-Legierungen PY - 1934 IS - 23 SP - 38 EP - 43 PB - Springer CY - Berlin AN - OPUS4-15781 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Boas, W. T1 - Rönthenographische Bestimmung der Löslichkeit von Kadmium in Zink PY - 1934 IS - 23 SP - 36 EP - 38 PB - Springer CY - Berlin AN - OPUS4-15782 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Hansen, Max T1 - Der Einfluß von dritten Metallen auf die Konstitution der Messinglegierungen - V. Der Einfluß von Mangan - ein Beitrag zur Kenntnis des Dreistoffsystems Kupfer-Zink-Mangan PY - 1934 IS - 23 SP - 43 EP - 49 PB - Springer CY - Berlin AN - OPUS4-15783 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Obinata, I. A1 - Schmid, Erich T1 - Röntgenographische Untersuchungen an Antimon-Blei- und Zinn-Blei-Legierungen PY - 1934 IS - 23 SP - 49 EP - 51 PB - Springer CY - Berlin AN - OPUS4-15784 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmid, Erich A1 - Seliger, H. T1 - Untersuchungen an binären Mischkristallen des Magensiums PY - 1934 IS - 23 SP - 52 EP - 58 PB - Springer CY - Berlin AN - OPUS4-15787 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmid, Erich A1 - Siebel, G. T1 - Über die Dehnung ternärer Magnesium-Mischkristalle PY - 1934 IS - 23 SP - 58 EP - 60 PB - Springer CY - Berlin AN - OPUS4-15788 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kühn, B. A1 - Sedlacek, G. A1 - Helmerich, Rosemarie A1 - Nussbaumer, A. ED - Gebbeken, N. T1 - Assessment of existing steel structures - A guideline for estimation of the remaining fatigue life T2 - Munich Bridge Assessment Conference (MBAC 2007) CY - Munich DA - 2007-07-09 KW - Existing structures KW - Fatigue life KW - Bridge assessment KW - Non-destructive testing PY - 2007 SP - 1 EP - 15 PB - Institut für Konstruktiven Ingenieurbau CY - Neubiberg AN - OPUS4-15743 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schikorr, Gerhard T1 - Über Theorie und Systematik der Korrosion der Metalle PY - 1933 IS - 22 SP - 3 EP - 9 PB - Springer CY - Berlin AN - OPUS4-15765 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schikorr, Gerhard T1 - Über die Theorie der Korrosion des Eisens PY - 1933 IS - 22 SP - 9 EP - 16 PB - Springer CY - Berlin AN - OPUS4-15766 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schikorr, Gerhard T1 - Über die Auflösung von Aluminium in Laugen PY - 1933 IS - 22 SP - 16 EP - 22 PB - Springer CY - Berlin AN - OPUS4-15767 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schikorr, Gerhard T1 - Über die Korrosion des Aluminiums durch Natriumchloridlösung unter Wasserstoffentwicklung PY - 1933 IS - 22 SP - 22 EP - 25 PB - Springer CY - Berlin AN - OPUS4-15768 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Blumenthal, Herbert A1 - Hansen, Max T1 - Über aushärtbares magnesiumhaltiges Silumin PY - 1934 IS - 23 SP - 60 EP - 65 PB - Springer CY - Berlin AN - OPUS4-15789 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Deiß, Eugen T1 - Seigerung in einem Silberblock PY - 1934 IS - 23 SP - 65 EP - 67 PB - Springer CY - Berlin AN - OPUS4-15790 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Obinata, I. A1 - Schmid, Erich T1 - Über die Dehnung von Zinnkristallen PY - 1934 IS - 23 SP - 67 EP - 71 PB - Springer CY - Berlin AN - OPUS4-15791 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gonell, Hans-Wolfgang T1 - Schüttgewicht, Rüttelgewicht und Sedimentvolumen als Kenngrößen feinkörnigen Arbeitsgutes PY - 1934 IS - 24 SP - 1 EP - 10 PB - Springer CY - Berlin AN - OPUS4-15792 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sommer, Herbert T1 - Neue Wege der Lichtechtheitsprüfung von Färbungen PY - 1934 IS - 24 SP - 11 EP - 32 PB - Springer CY - Berlin AN - OPUS4-15793 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Jovanovits, J. A. T1 - Diskussion PY - 1934 IS - 24 SP - 33 EP - 36 PB - Springer CY - Berlin AN - OPUS4-15794 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Wilhelm T1 - Ermittlung des Einflusses ungleichförmiger Spannungen und Querschnitte auf die Streckgrenze PY - 1934 IS - 24 SP - 37 EP - 44 PB - Springer CY - Berlin AN - OPUS4-15795 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald T1 - Über die Entwicklung von alkoholhaltigen Treibstoffen auf Aluminium und Aluminiumlegierungen PY - 1933 IS - 22 SP - 25 EP - 32 PB - Springer CY - Berlin AN - OPUS4-15769 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Deiß, Eugen A1 - Blumenthal, Herbert T1 - Die Analyse von kupfer-nickel-plattiertem Stahlmaterial PY - 1933 IS - 22 SP - 32 EP - 37 PB - Springer CY - Berlin AN - OPUS4-15770 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schürmann, E. A1 - Charisius, Kurt T1 - Zur gewichtsanalytischen Bestimmung des Gehalts an Bleioxyd in Mennige PY - 1933 IS - 22 SP - 37 EP - 40 PB - Springer CY - Berlin AN - OPUS4-15771 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Blumenthal, Herbert T1 - Antimontrichloridverfahren zur Bestimmung des Bleidioxydgehaltes in Mennige PY - 1933 IS - 22 SP - 40 EP - 41 PB - Springer CY - Berlin AN - OPUS4-15772 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Blumenthal, Herbert T1 - Zur Bestimmung des Kupfergehaltes von Handelsmennige PY - 1933 IS - 22 SP - 41 PB - Springer CY - Berlin AN - OPUS4-15773 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Blumenthal, Herbert T1 - Zur Bestimmung des Magnesiums in manganhaltigen Aluminium-Magnesiumlegierungen PY - 1933 IS - 22 SP - 42 EP - 43 PB - Springer CY - Berlin AN - OPUS4-15774 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rodt, V. A1 - Charisius, Kurt T1 - Über das Verhalten von Eisen-II-salzlösungen bei Oxydieren mit Brom PY - 1933 IS - 22 SP - 43 EP - 45 PB - Springer CY - Berlin AN - OPUS4-15775 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rodt, V. T1 - Zur Entstehung von Eisen-II-II-oxyd (F3O4x aq) in wässriger Lösung PY - 1933 IS - 22 SP - 45 EP - 49 PB - Springer CY - Berlin AN - OPUS4-15776 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - von Göler, A1 - Sachs, Georg T1 - Zur Kinetik von Kristallisationsvorgängen PY - 1934 IS - 23 SP - 3 EP - 5 PB - Springer CY - Berlin AN - OPUS4-15777 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stenzel, W. A1 - Weerts, J. T1 - Präzisionsbestimmungen von Gitterkonstanten nichtkubischer Stoffe PY - 1934 IS - 23 SP - 5 EP - 16 PB - Springer CY - Berlin AN - OPUS4-15778 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Poisel, H. A1 - Kalymnios, D. A1 - Krebber, Katerina A1 - Scully, P. A1 - Werneck, M. A1 - Zubia, J. T1 - POF Sensors - applications in every day's life T2 - 33rd European Conference and Exhibition on Optical Communication CY - Berlin, Germany DA - 2007-09-16 PY - 2007 VL - 2 SP - 103 EP - 106 PB - VDI-Verl. CY - Berlin AN - OPUS4-15943 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Witt, Jens A1 - Bunge, C.-A. A1 - Schukar, Marcus A1 - Krebber, Katerina T1 - Real-time strain sensing based on POF OTDR N2 - We investigate two real-time strain sensing principles based on the optical time-domain reflectometry (OTDR) in polymer optical fibres (POF). The first sensing principle uses the increase of the level of backscattered light in a stretched POF. The second sensing principle uses the effect of losses due to bending. T2 - 16th International Conference on Plastic Optical Fibers (POF 2007) CY - Turin, Italy DA - 2007-09-10 KW - Strain sensor KW - Fibre optic sensor KW - POF sensor KW - OTDR KW - Strain rate PY - 2007 SP - 210 EP - 213 PB - International Cooperative of Plastic Optical Fibers (ICPOF) CY - Turin, Italy AN - OPUS4-15922 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rühl, Karl H. A1 - Schwaigerer, S. T1 - Grundlagen der Festigkeitslehre PY - 1955 VL - 1 IS - Abschnitt 6/II SP - 838 EP - 866 PB - Ernst CY - Berlin ET - 28., neubearb. AN - OPUS4-15979 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rühl, Karl H. T1 - Stabartige Tragwerke PY - 1955 VL - 1 IS - Abschnitt 6/III SP - 867 EP - 940 PB - Ernst CY - Berlin ET - 28., neubearb. AN - OPUS4-15980 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rühl, Karl H. T1 - Druckkräfte zwischen gewölbten Oberflächen PY - 1955 VL - 1 IS - Abschnitt 6/VIII SP - 964 EP - 967 PB - Ernst CY - Berlin ET - 28., neubearb. AN - OPUS4-15981 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Sommer, Herbert ED - Stauch, A. ED - Sinner, G. T1 - Textile Rohstoffe und Erzeugnisse PY - 1937 IS - Abschnitt 4/IV/A a-d SP - 589 EP - 621 PB - Ernst CY - Berlin ET - 2., neu bearb. AN - OPUS4-15982 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Viertel, O. ED - Stauch, A. ED - Sinner, G. T1 - Textilfarben PY - 1937 IS - Abschnitt 4/IV/A e SP - 621 EP - 623 PB - Ernst CY - Berlin ET - 2., neu bearb. AN - OPUS4-15983 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Alekseychuk, Oleksandr A1 - Zscherpel, Uwe T1 - Recent developments for longitudinal crack detection using a Continuous Density Hidden Markov Model (CDHMM) N2 - Recent developments for automatic detection of crack indications in welding seams are presented addressing the task from a probabilistic point of view. This work improves the algorithm developed several years ago. The distinctive feature of these algorithms is a translation of the task of detection into an optimisation task in such a way, that the the maximum of a scoring function in the space of all possible positions, lengths and shapes can be found exactly and computationally effective. The progress of the new algorithm presented here consists in the replacement of the discrete (binary) model of crack indications (i.e. defect present vs. defect absent) previously used with a continuous grey value model and the development of a new scoring function. The restriction of the noise model to additive Gaussian allowed the utilisation of conjugate priors for the posterior probability estimation in a computationally effective way too. Results of experimental evaluation of the developed algorithm are presented. T2 - DIR 2007 - International Symposium on Digital industrial Radiology and Computed Tomography CY - Lyon, France DA - 2007-06-25 KW - Industrial radiographic testing KW - Crack detection KW - Curve detection KW - Detection in noisy images KW - Bayesian network KW - HMM KW - CDHMM KW - Dynamic programming KW - Kalman filter PY - 2007 UR - http://www.ndt.net/article/dir2007/papers/p1.pdf IS - (Poster P1) SP - 1 EP - 16 CY - Lyon, France AN - OPUS4-16065 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schumm, A. A1 - Zscherpel, Uwe T1 - Using the EN584-1 film characterization in radiographic modelling T2 - DIR 2007 - International Symposium on Digital industrial Radiology and Computed Tomography CY - Lyon, France DA - 2007-06-25 KW - Radiography KW - Simulation KW - Film PY - 2007 UR - http://www.ndt.net/article/dir2007/papers/s3.pdf IS - (Poster S3) SP - 1 EP - 4 CY - Lyon, France AN - OPUS4-16070 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zscherpel, Uwe A1 - Ewert, Uwe A1 - Bavendiek, K. T1 - Possibilities and Limits of Digital Industrial Radiology: The new high contrast sensitivity technique - Examples and system theoretical analysis T2 - DIR 2007 - International Symposium on Digital industrial Radiology and Computed Tomography CY - Lyon, France DA - 2007-06-25 KW - Digital radiography KW - High contrast sensitivity technique KW - Digital detector arrays KW - NDT film systems KW - Computed Radiography (CR) with imaging plates KW - Film replacement KW - Image quality KW - Basic spatial resolution KW - Signal/noise ratio KW - Contrast sensitivity PY - 2007 IS - (Vortrag V1) SP - 1 EP - 17 CY - Lyon, France AN - OPUS4-16073 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Stamer, J. T1 - Nutzhölzer PY - 1931 VL - 1 IS - 6 SP - 876 EP - 888 CY - Berlin ET - 26., neubearb. AN - OPUS4-15971 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Wiederholt, Wilhelm ED - Stauch, A. ED - Rögnitz, H. T1 - Metallische Überzüge PY - 1957 VL - 1 IS - Abschnitt 1/V/A SP - 112 EP - 120 PB - Ernst CY - Berlin ET - 5., neu bearb. und erw. AN - OPUS4-15972 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pfender, Max ED - Stauch, A. ED - Rögnitz, H. T1 - Warmpressen von Nichteisenmetallen im Gesenk PY - 1957 VL - 1 IS - Abschnitt 2/II/D SP - 189 EP - 192 PB - Ernst CY - Berlin ET - 5., neu bearb. und erw. AN - OPUS4-15973 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pfender, Max ED - Stauch, A. ED - Rögnitz, H. T1 - Strangpressen PY - 1957 VL - 1 IS - Abschnitt 2/II/E SP - 193 EP - 195 PB - Ernst CY - Berlin ET - 5., neu bearb. und erw. AN - OPUS4-15974 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pfender, Max ED - Stauch, A. ED - Rögnitz, H. T1 - Kaltpressen von Metallen im Gesenk PY - 1957 VL - 1 IS - Abschnitt 2/II/F SP - 196 EP - 198 PB - Ernst CY - Berlin ET - 5., neu bearb. und erw. AN - OPUS4-15975 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Wiederholt, Wilhelm ED - Stauch, A. ED - Rögnitz, H. T1 - Email- und andere anorganische nichtmetallische Überzüge PY - 1957 VL - 1 IS - Abschnitt 1/V/B SP - 120 EP - 122 PB - Ernst CY - Berlin ET - 5., neu bearb. und erw. AN - OPUS4-15976 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Wiederholt, Wilhelm ED - Stauch, A. ED - Rögnitz, H. T1 - Anorganische, nichtmetallische Schichten durch chemische und elektrochemische Behandlung PY - 1957 VL - 1 IS - Abschnitt 1/V/C SP - 122 EP - 123 PB - Ernst CY - Berlin ET - 5., neu bearb. und erw. AN - OPUS4-15977 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Toeldte, W. T1 - Klebemittel PY - 1955 VL - 1 IS - Abschnitt 7/XIV SP - 1276 EP - 1279 PB - Ernst CY - Berlin ET - 28., neubearb. AN - OPUS4-15978 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koch, Frank A1 - Droste, Bernhard A1 - Krietsch, Torsten T1 - Consequences of drop test parameter limitations for subsequent package design safety analysis T2 - PATRAM 2007, 15th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Miami, Florida, USA DA - 2007-10-21 KW - Transportbehälter KW - Fallprüfung KW - Sicherheitsbericht KW - Parameter KW - Assessment Cube PY - 2007 SP - 1 EP - 7 PB - Institute of Nuclear Materials Management AN - OPUS4-16129 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Seeger, Stefan A1 - Gusovius, H.-J. A1 - Wallot, G. ED - Peukert, W. ED - Schreglmann, C. T1 - A new measurement method to evaluate length related properties of natural bast fibres T2 - PARTEC 2007 - International Congress on Particle Technology CY - Nuremberg, Germany DA - 2007-03-27 KW - Bast fibres KW - Natural fibres KW - Fibre length distribution KW - Image analysis PY - 2007 SP - 1 EP - 4 PB - Nürnberg Messe CY - Nürnberg AN - OPUS4-16099 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erhard, Anton A1 - Völzke, Holger A1 - Noack, Volker A1 - Weber, Wolfgang A1 - Wolff, Dietmar A1 - Rittscher, D. A1 - Schmidt, H. T1 - Long term interim storage facility for nuclear reactor compartments of submarines - German support for utilization of nuclear submarines in Russia T2 - PATRAM 2007, 15th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Miami, Florida, USA DA - 2007-10-21 PY - 2007 SP - 155 PB - Institute of Nuclear Materials Management AN - OPUS4-16157 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heß, P. A1 - Erhard, Anton T1 - RSK-Recommendations for German Nuclear Power Plant Ageing Management System PY - 2006 SP - 1 EP - 8 CY - Washington D.C. USA AN - OPUS4-16158 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brandes, Klaus T1 - Vzdálenosti dilatacních spar v plochých strechách - Simulace chování se konstrukcí plochých strech methodou Monte-Carlo T2 - Die Lebensdauer von Tragkonstruktionen von Betonbauten und Großplattenhäusern CY - Brno, Czech Republic DA - 1975-10-13 PY - 1975 SP - 188 EP - 192 CY - Brno AN - OPUS4-16140 LA - ces AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Gert A1 - Mellmann, Günter T1 - Zkušenosti o úcincích vnejších vlivù na prevnost v tlaku u predpjatých betonových mostù T2 - Die Lebensdauer von Tragkonstruktionen von Betonbauten und Großplattenhäusern CY - Brno, Czech Republic DA - 1975-10-13 PY - 1975 SP - 249 EP - 252 CY - Brno AN - OPUS4-16141 LA - ces AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wille, Frank A1 - Ballheimer, Viktor A1 - Droste, Bernhard T1 - Suggestions for correct performance of IAEA 1 m puncture bar drop test with reduced-scale packages considering similarity theory aspects T2 - PATRAM 2007, 15th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Miami, Florida, USA DA - 2007-10-21 KW - Similarity KW - Puncture Bar Drop Test KW - Scale Models KW - IAEA Regulations PY - 2007 IS - CD-ROM SP - 1 EP - 8 PB - Institute of Nuclear Materials Management AN - OPUS4-16104 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wille, Frank A1 - Droste, Bernhard A1 - Koch, Frank A1 - Schubert, Sven A1 - Komann, Steffen T1 - State-of-the-art assessment of package design safety analyses T2 - PATRAM 2007, 15th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Miami, Florida, USA DA - 2007-10-21 KW - Transportation of radioactive materials KW - Safety KW - Design assessment KW - Mechanical tests KW - Thermal tests KW - Drop tests KW - Numerical calculations KW - Quality assurance PY - 2007 SP - 1 EP - 8 PB - Institute of Nuclear Materials Management AN - OPUS4-16105 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koch, Frank A1 - Bletzer, Claus Wilhelm A1 - Wieser, Günter T1 - Consideration of asymmetrical heat transmission and distribution using numerical methods T2 - PATRAM 2007, 15th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Miami, Florida, USA DA - 2007-10-21 KW - Temperaturverteilung KW - CFD KW - FEA KW - Transportbehälter KW - Wärmeübergang PY - 2007 SP - 1 EP - 8 PB - Institute of Nuclear Materials Management AN - OPUS4-16131 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schickert, Gerald T1 - Zkoušky zatížení od rozpínání u vrtaných vzorkù dálnicního mostu z predpjatého betonu, který je silne namáhán vnejšími vlivy T2 - Die Lebensdauer von Tragkonstruktionen von Betonbauten und Großplattenhäusern CY - Brno, Czech Republic DA - 1975-10-13 PY - 1975 SP - 244 EP - 248 CY - Brno AN - OPUS4-16138 LA - ces AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thiel, R. A1 - Nabel, Eberhard A1 - Hecht, A. A1 - Neumann, Eberhard A1 - Mundry, Eberhard T1 - Zerstörungsfreie Korngrößenbestimmung an austenitischen Feinblechen mit Hilfe der Ultraschallrückstreuung T2 - 1. Najnovejsi dosezki na podrocju preiskav materiala brez porusitve CY - Krsko, Jugoslawien DA - 1979-09-05 PY - 1979 SP - 1(?) EP - 9(?) CY - Krsko AN - OPUS4-16178 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erning, Johann Wilhelm A1 - Ebner, M. A1 - Priggemeyer, S. A1 - Rapp, T. T1 - Development of a test method to determine lead on brass surfaces: From the idea to a standardized procedure, an european round-robin-test T2 - EUROCORR 2007 CY - Freiburg im Breisgau, Germany DA - 2007-09-09 KW - Copper alloys KW - Drinking water KW - Leaching test KW - Lead on surface PY - 2007 N1 - Serientitel: EFC-Event – Series title: EFC-Event IS - 289 SP - 1 EP - 6 PB - DECHEMA CY - Frankfurt am Main AN - OPUS4-16203 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erning, Johann Wilhelm T1 - Korrosion und Hygiene in Trinkwasserhausinstallationen T2 - 1. Deutsches Forum Innenraumhygiene CY - Bochum, Deutschland DA - 2007-10-10 PY - 2007 SP - 66 EP - 74 PB - Fachverband SHK Nordrhein-Westfalen CY - Düsseldorf AN - OPUS4-16204 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erning, Johann Wilhelm A1 - Mikó, Annamária A1 - Schlerkmann, H. A1 - Mathiesen, T. T1 - Qualification of materials for use in drinking water applications: Test method for stainless steel T2 - EUROCORR 2007 CY - Freiburg im Breisgau, Germany DA - 2007-09-09 KW - Stainless steel KW - Drinking water KW - Slow polarisation KW - Leaching test PY - 2007 N1 - Serientitel: EFC-Event – Series title: EFC-Event IS - 289 SP - 1 EP - 6 PB - DECHEMA CY - Frankfurt am Main AN - OPUS4-16199 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Bartmann, S. A1 - Brocks, Wolfgang A1 - Fricke, Stefan A1 - Künecke, Georgia A1 - Schicker, J. A1 - Serce, O. T1 - FE-Analysen des duktilen Rißwachstums seitengekerbter Proben aus StE 460 (DFG-Forschungsvorhaben Br-521-3-1) N2 - Großes duktiles Rißwachstum zweier seitengekerbter Proben, CTsg und CCTsg, aus StE 460 wird mit der Finite-Elemente-Methode an 2D EVZ-Modellen numerisch simuliert. Zwei verschiedene Simulationsmodelle des Rißwachstums, Knotenfreisefczung mit und ohne vorausgehende Knotenversetzung, werden untersucht. Die rechnerischen Analysen liefern detaillierte Aussagen über die Spannungs- und Verformungszustände in den Proben. Die unterschiedlichen Dehnungsbehinderungen beider Probengeometrien im Ligament (in-plane constraint) begründen die bekannten Geometrieabhängigkeiten ihrer Rißwiderstandskurven. Eine ergänzende 3D Analyse der CCT-Probe liefert Aussagen über Dickeneffekte und lokales Rißwiderstandsverhalten. KW - Bruchmechanik KW - Finite Elemente KW - Duktiles Rißwachstum KW - Rißwiderstandskurven KW - in-plane constraint KW - Geometrieeinfluß KW - Lokaler Rißwiderstand KW - Mehrachsigkeit PY - 1991 SP - 1 EP - 88 PB - Bundesanstalt für Materialforschung und -prüfung CY - Berlin AN - OPUS4-16220 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Schickert, Gerald A1 - Winkler, Helmut T1 - Biaxial compressive tests stress-strain curves PY - 1976 IS - 3 SP - 2 EP - 122 CY - Berlin AN - OPUS4-16217 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Schickert, Gerald A1 - Winkler, Helmut T1 - Concise report on studies of multiaxial strength of concrete and mortar PY - 1976 IS - 2 SP - 2 EP - 65 CY - Berlin AN - OPUS4-16218 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Schickert, Gerald A1 - Danßmann, Jürgen A1 - Schimmelwitz, Peter T1 - Bruch- und Verformungsverhalten von Beton während und nach hoher hydrostatischer Beanspruchung PY - 1976 SP - 1 EP - 100 CY - Berlin AN - OPUS4-16219 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burkert, Andreas T1 - Flecken aus dem Nichts KW - Nichtrostender Stahl KW - Dekorative Oberflächen KW - Fleckenbildung KW - Korrosion PY - 2007 VL - 10 SP - 7 EP - 8 PB - Wirtschaftsges. des Fachverbandes Metall Bayern CY - München AN - OPUS4-16265 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Brenneis, Rudolf A1 - Dettmer, T. A1 - Baeck, Burkhard A1 - Bock, R. A1 - Kley, Gerd T1 - Verbesserung der Umweltverträglichkeit bei überwachungsbedürftigen Abfällen - Enzymkatalysiertes Verfahren zur Herstellung von Esterölen KW - Kühlschmierstoffe KW - Esteröle KW - Enzymatische Alkoholyse KW - Ökobilanzierung KW - Altfett PY - 2007 IS - Artikel 57 SP - 1 EP - 3 PB - Branch CY - Berlin AN - OPUS4-16313 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kohlhoff, Harald A1 - Ullner, Christian T1 - Verification of the standard machine for the macro range of instrumented indentation test N2 - A new calibration machine according to the requirements given by ISO 14577-3 [1] was described in [2]. The results of the verification are reported in this paper. It is shown that the calibration machine can be used as a national standard for the materials parameter of the instrumented indentation test. T2 - HARDMEKO 2007 - Recent Advancement of Theory and Practice in Hardness Measurement CY - Tsukuba, Japan DA - 2007-11-19 KW - Indentation KW - Standard KW - Verification PY - 2007 IS - CD-ROM SP - 30 EP - 34 CY - Tsukuba, Japan AN - OPUS4-16319 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Niebergall, Ute T1 - Übertragbarkeit von Materialkennwerten auf das Baumusterverhalten von Verpackungen aus HDPE T2 - Gefahrgut-Technik-Tage Berlin 2007 "Gefahrgut-Verpackungen" CY - Berlin, Deutschland DA - 2007-11-22 KW - BAM-GGR 003 KW - Verpackungen KW - HDPE KW - Formstoffkennwerte KW - Baumusterprüfungen KW - Versagensgrenzen PY - 2007 SP - 1 EP - 13 CY - Berlin AN - OPUS4-16273 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Reiners, Georg T1 - Internationale und Europäische Normung in der Nanotechnologie PY - 2007 VL - 8 IS - Abschnitt 2.4 SP - 17 EP - 21 CY - Wiesbaden AN - OPUS4-16362 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Habel, Wolfgang A1 - Krebber, Katerina A1 - Dantan, Nathalie A1 - Schallert, Matthias A1 - Hofmann, Detlef ED - Bin Shi, T1 - Recent examples of applied fibre optic sensors in geotechnical areas to evaluate and monitor structural integrity T2 - OSMG-2007 - 2nd International Workshop on Opto-electronic Sensor-based Monitoring in Geo-engineering CY - Nanjing, China DA - 2007-10-18 KW - Fibre optic sensors KW - Monitoring KW - Geotechnique KW - Pile load test KW - pH sensor KW - Geotextile monitoring KW - Ground anchor monitoring KW - Distributed sensor PY - 2007 SP - 27 EP - 35 CY - Nanjing, China AN - OPUS4-16431 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lenke, Philipp A1 - Liehr, Sascha A1 - Krebber, Katerina A1 - Weigand, F. A1 - Thiele, E. T1 - Distributed strain measurement with polymer optical fiber integrated in technical textiles using the optical time domain reflectometry technique N2 - The presented research is carried out on the background of the development of a new strain sensor, integrated in technical textiles using the optical time domain reflectometry (OTDR) technique. We investigated the effect of increased scattering in POF due to applied strain as a distributed sensor including research on long-term stability and reliability of this sensor. T2 - 16th International Conference on Plastic Optical Fibers (POF 2007) CY - Turin, Italy DA - 2007-09-10 PY - 2007 SP - 21 EP - 24 PB - International Cooperative of Plastic Optical Fibers (ICPOF) CY - Turin, Italy AN - OPUS4-16435 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz T1 - The influence of the soil on track dynamics and ground-borne vibration T2 - 9th International Workshop on Railway Noise (IWRN) CY - Munich, Germany DA - 2007-09-04 PY - 2007 SP - S.4.1, 1 EP - 9 PB - International Workshop on Railway Noise CY - München AN - OPUS4-16438 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Barbier, J.-P. A1 - Bissolotti, G. A1 - Christian, S. A1 - Cleaver, K. A1 - Heller, D. A1 - Injaian, M. A1 - Schröder, Volkmar A1 - Witte, F. T1 - Safe preparation of compressed oxidant-fuel gas mixtures in cylinders KW - Sicherheitstechnik KW - Biogas KW - Explosionsgrenzen KW - Prozesssicherheit PY - 2007 IS - 139/07/E SP - 1 EP - 36 PB - European Industrial Gases Association (EIGA) CY - Brussels AN - OPUS4-16501 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Arndt, Ralf T1 - Rechteckimpuls-Thermografie im Frequenzbereich - Adaption der Puls-Phasen-Thermografie für die qualitative und quantitative zerstörungsfreie Prüfung oberflächennaher Strukturen im Bauwesen N2 - In der folgenden als Promotionsschrift verfassten Arbeit wird ein methodischer Ansatz zur qualitativen und quantitativen zerstörungsfreien Prüfung von oberflächennahen Strukturen im Bauwesen mittels aktiver Thermografie entwickelt und erprobt. Er adaptiert das aus der Werkstoffprüfung bekannte Verfahren der Puls-Phasen-Thermografie (PPT) für die besonderen Anforderungen im Bauwesen. Das mit „Rechteckimpuls-Thermografie im Frequenzbereich“ bezeichnete Konzept gründet auf dem vom Fachgebiet „Baustoffe und Baustoffprüfung“ der Technischen Universität Berlin (TUB) und der Fachgruppe VIII.2 „Zerstörungsfreie Schadensdiagnose und Umweltmessverfahren“ der Bundesanstalt für Materialforschung und -prüfung (BAM) durchgeführten Forschungsvorhaben: „Struktur- und Feuchteuntersuchungen von Bauteil- und Bauwerksoberflächen mit der Impuls- Thermografie, Teil 1 und Teil 2“, gefördert durch die Deutsche Forschungsgemeinschaft (DFG). Es werden zunächst die Grundlagen der elektromagnetischen Strahlung, der Wärmeübertragung, der Signalverarbeitung sowie der aktiven Thermografie dargestellt. Es folgt ein Kapitel über das Thermografie-Konzept von TUB und BAM. Nach einer Zusammenfassung von bereits unter Mitwirkung des Verfassers veröffentlichten qualitativen Ergebnissen der Auswertung im Zeit- und Frequenzbereich wird ein neuer Ansatz für die Defekttiefenbestimmung im Frequenzraum mittels der charakteristischen Frequenz des maximalen negativen Phasen- und Amplitudenkontrastes zwischen Fehlstelle und ungestörtem Bereich entwickelt und anhand von systematischen Untersuchungen an Probekörpern der BAM überprüft. Die vom Verfasser in der Arbeit mit Rechteckimpuls-Spektral-Thermografie (RST) bezeichnete Methode, die auch als eine Rechteckimpuls-Thermografie (RIT) im Frequenzbereich oder eine durch Amplitudenauswertung ergänzte PPT für Rechteckimpulse verstanden werden kann, soll die aus der Literatur bekannten Ansätze ergänzen und bietet eine Alternative für die Tiefenbestimmung von Defekten bei Messungen mit langen Erwärmungs- und Beobachtungszeiten, wie sie im Bauwesen häufig vorkommen. Die Arbeit wird vervollständigt durch analytische Untersuchungen über den angeregten Wärme- fluss sowie ergänzende Simulationsrechnungen und die Beschreibung werkstoffübergreifender Praxisanwendungen zur Qualitätssicherung und zur Schadensdiagnose sowie zur Strukturuntersuchung von Kulturgütern im Bauwesen. Sie schließt ab mit möglichen Perspektiven der aktiven Thermografie im Bauwesen sowie mit einer Zusammenfassung. KW - Zerstörungsfreie Prüfung KW - Puls-Phasen-Thermografie KW - Bauwesen KW - Rechteckimpuls-Thermografie KW - Auswertung im Frequenzbereich PY - 2007 SP - 1-178, Anhang 1-14 CY - Berlin AN - OPUS4-16484 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rückert, Joachim A1 - Isecke, Bernd A1 - Zietelmann, Christina T1 - Gebrauchssicherheit von Kochgerät aus Edelstahl - Elektrochemische Messungen zur Ni-Abgabe (Teil 2) KW - Nickelabgabe KW - Nickelübergang aus Edelstahl in Kochgut PY - 1998 IS - 246 SP - 1 EP - 26 CY - Düsseldorf AN - OPUS4-16486 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schartel, Bernhard ED - Troitzsch, J. T1 - Entwicklung von flammgeschützten Polymerwerkstoffen - Interpretation von Cone Calorimeter Daten T2 - 9. SKZ-Fachtagung "Kunststoffe, Brandschutz und Flammschutzmittel" CY - Würzburg, Deutschland DA - 2007-12-05 KW - Flammschutz von Polymeren KW - Fire Retardancy KW - Cone Calorimeter PY - 2007 N1 - Sprachen: Deutsch/Englisch - Languages: German/English SP - 1 EP - 25 PB - SKZ CY - Würzburg AN - OPUS4-16487 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Korn, Rudolph T1 - Fortschritte in der Papier- und Zellstoffprüfung im Jahre 1932 PY - 1934 IS - 24 SP - 45 EP - 50 PB - Springer CY - Berlin AN - OPUS4-16519 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Richter, G. T1 - Qualitätsvorschriften für Bleche, Rohre, Schrauben, Niete und Drähte PY - 1934 IS - 24 SP - 99 EP - 102 PB - Springer CY - Berlin AN - OPUS4-16530 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Becker, W. A1 - Macht, F. A1 - Stöcke, K. T1 - Über die Beziehungen zwischen den geologisch-petrographischen Merkmalen und den straßenbautechnischen Eigenschaften schlesischer Granite - III. Teil: Ergebnisse der technologischen Prüfungen PY - 1934 IS - 24 SP - 103 EP - 108 PB - Springer CY - Berlin AN - OPUS4-16531 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Obinata, I. A1 - Wassermann, G. T1 - Röntgenographische Untersuchung der Löslichkeit von Aluminium in Kupfer PY - 1934 IS - 24 SP - 109 EP - 112 PB - Springer CY - Berlin AN - OPUS4-16532 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hansen, Max A1 - Stenzel, W. T1 - Die Löslichkeit von Kupfer in Zink PY - 1934 IS - 24 SP - 113 EP - 120 PB - Springer CY - Berlin AN - OPUS4-16534 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hansen, Max A1 - Stenzel, W. T1 - Die Löslichkeit von Kupfer in Zink PY - 1933 VL - 12 IS - 38 SP - 539 EP - 542 PB - N.E.M.-Verl. CY - Berlin AN - OPUS4-16535 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - v. Vargha, G. A1 - Wassermann, G. T1 - Über die Abhängigkeit der Kristallitanordnung in gewalzten Aluminiumblechen von der Blechdicke PY - 1934 IS - 24 SP - 121 EP - 126 PB - Springer CY - Berlin AN - OPUS4-16536 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - v. Vargha, G. A1 - Wassermann, G. T1 - Über die Abhängigkeit der Kristallitanordnung in gewalzten Aluminiumblechen von der Blechdicke PY - 1933 VL - 12 IS - 36 SP - 511 EP - 513 PB - N.E.M.-Verl. CY - Berlin AN - OPUS4-16537 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Saenger, Georg T1 - Mit Schwefel getränkter Zementmörtel PY - 1934 IS - 24 SP - 127 EP - 135 PB - Springer CY - Berlin AN - OPUS4-16538 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Weerts, J. A1 - Beck, F. T1 - Mechanische Eigenschaften von Elektrolytzinkblechen PY - 1934 IS - 24 SP - 137 EP - 144 PB - Springer CY - Berlin AN - OPUS4-16539 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schikorr, Gerhard T1 - Über Eisen(II)-hydroxyd und ein ferromagnetisches Eisen(III)-hydroxyd PY - 1934 IS - 24 SP - 51 EP - 58 PB - Springer CY - Berlin AN - OPUS4-16520 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Toeldte, W. T1 - Über mechanische Filmeigenschaften von Nitrozelluloselacken PY - 1934 IS - 24 SP - 59 EP - 68 PB - Springer CY - Berlin AN - OPUS4-16522 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kindscher, Erich T1 - Die Bindefähigkeit des Bitumens PY - 1934 IS - 24 SP - 69 EP - 72 PB - Springer CY - Berlin AN - OPUS4-16524 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kindscher, Erich A1 - Weerts, J. T1 - Die Bindefähigkeit des Bitumens PY - 1933 IS - 5 SP - 104 EP - 107? PB - Plaum CY - Halle, S. AN - OPUS4-16525 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stenzel, W. A1 - Weerts, J. T1 - Die Anlaßwirkungen in abgeschreckten Kupfer-Aluminiumlegierungen PY - 1934 IS - 24 SP - 73 EP - 93 PB - Springer CY - Berlin AN - OPUS4-16526 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stenzel, W. A1 - Weerts, J. T1 - Die Anlaßwirkungen in abgeschreckten Kupfer-Aluminiumlegierungen PY - 1933 VL - 12 IS - 25-26 SP - 353-356 u. 369-374 PB - N.E.M.-Verl. CY - Berlin AN - OPUS4-16527 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Zunker, P. T1 - Die Dichte von Zink in Abhängigkeit von der Verformung durch Kalt- und Warmwalzen PY - 1934 IS - 24 SP - 93 EP - 98 PB - Springer CY - Berlin AN - OPUS4-16528 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bierett, Georg T1 - Dauerfestigkeit von Schweißverbindungen PY - 1934 IS - 25 SP - 87 EP - 89 PB - Springer CY - Berlin AN - OPUS4-16580 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmid, Erich T1 - Über die Mischkristallbildung bei ein- und vielkristallinem Material PY - 1935 IS - 26 SP - 1 EP - 20 PB - Springer CY - Berlin AN - OPUS4-16581 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stöcke, K. T1 - Die Normenblätter DIN DVM 2201-2206 zur Prüfung von Dachschiefer PY - 1935 IS - 26 SP - 21 EP - 26 PB - Springer CY - Berlin AN - OPUS4-16584 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schulze, A. T1 - Verhalten verschiedener Bauweisen im Feuer und Wirkung von Holzschutzmitteln PY - 1935 IS - 26 SP - 27 EP - 32 PB - Springer CY - Berlin AN - OPUS4-16585 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wassermann, G. A1 - v. Vargha, G. T1 - Über den Einfluß des Formgebungsverfahrens auf die Kristallgleichrichtung in Drähten PY - 1935 IS - 26 SP - 33 EP - 35 PB - Springer CY - Berlin AN - OPUS4-16587 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fiek, Georg A1 - Matting, A. T1 - Eignung des Faltversuches zur Prüfung von Schweissverbindungen PY - 1934 IS - 25 SP - 39 EP - 45 PB - Springer CY - Berlin AN - OPUS4-16570 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bierett, Georg A1 - Kommerell, O. T1 - Über die statische Festigkeit und die Dauerfestigkeit genieteter, vorbelasteter und unter Vorlast durch Schweißung verstärkter Stabanschlüsse PY - 1934 IS - 25 SP - 47 EP - 64 PB - Springer CY - Berlin AN - OPUS4-16571 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Grüning, G. T1 - Die Schrumpfspannungen beim Schweißen - Versuch einer statischen Berechnung PY - 1934 IS - 25 SP - 65 EP - 70 PB - Springer CY - Berlin AN - OPUS4-16574 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bierett, Georg T1 - Schrumpfspannungen in autogen geschweissten Teilen PY - 1934 IS - 25 SP - 79 EP - 86 PB - Springer CY - Berlin AN - OPUS4-16578 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bierett, Georg T1 - Versuche zur Ermittlung der Schrumpfspannungen in geschweißten Stumpfnahtverbindungen PY - 1934 IS - 25 SP - 71 EP - 77 PB - Springer CY - Berlin AN - OPUS4-16579 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fiek, Georg T1 - Prüfverfahren für Schweißungen - Stand der Arbeiten zu ihrer Vereinheitlichung PY - 1934 IS - 25 SP - 23 EP - 26 PB - Springer CY - Berlin AN - OPUS4-16567 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Laute, K. T1 - Korrosion und Ermüdung PY - 1934 IS - 25 SP - 27 EP - 37 PB - Springer CY - Berlin AN - OPUS4-16569 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schürmann, E. A1 - Charisius, Kurt T1 - Zur Bestimmung des Bleidioxydgehaltes in Mennige PY - 1935 IS - 26 SP - 37 EP - 39 PB - Springer CY - Berlin AN - OPUS4-16599 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Weerts, J. A1 - Beck, F. T1 - Mechanische Eigenschaften von Elektrolytzinkblechen PY - 1933 VL - 12 IS - 43 SP - 615 EP - 619 PB - N.E.M.-Verl. CY - Berlin AN - OPUS4-16540 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Wilhelm A1 - Krisch, A. T1 - Berechnung der Bruchdehnung einschnürender metallischer Werkstoffe für beliebig große Meßlängen PY - 1934 IS - 24 SP - 145 EP - 149 PB - Springer CY - Berlin AN - OPUS4-16541 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tanimura, H. A1 - Wassermann, G. T1 - Über das System Beryllium-Kupfer PY - 1934 IS - 24 SP - 151 EP - 153 PB - Springer CY - Berlin AN - OPUS4-16545 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kindscher, Erich A1 - Lederer, Ph. T1 - Die Reaktionen der Bleiglätte mit Leinöl bei Zimmertemperatur PY - 1934 VL - 38 IS - 24 SP - 155 EP - 160 PB - Springer CY - Berlin AN - OPUS4-16547 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bierett, Georg T1 - Die Schweißverbindung bei dynamischer Beanspruchung PY - 1934 IS - 25 SP - 1 EP - 10 PB - Springer CY - Berlin AN - OPUS4-16549 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weißwange, W. T1 - Prüfverfahren zur Ermittlung des Wärmeschutzes von Wänden und Decken PY - 1935 IS - 26 SP - 41 EP - 48 PB - Springer CY - Berlin AN - OPUS4-16601 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wassermann, G. T1 - Über die Umwandlungsvorgänge in beta-Aluminiumbronze PY - 1935 IS - 26 SP - 49 EP - 55 PB - Springer CY - Berlin AN - OPUS4-16603 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Arndt, H. A1 - Bauer, Oswald T1 - Das Verhalten von Kupfer, Nickel und Kupfer-Nickellegierungen gegenüber dem Angriff von Wasch- und Bleichmitteln PY - 1935 IS - 26 SP - 57 EP - 61 PB - Springer CY - Berlin AN - OPUS4-16604 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Arndt, H. A1 - Bauer, Oswald T1 - Das Verhalten von Kupfer, Nickel und Kupfer-Nickellegierungen gegenüber dem Angriff von Wasch- und Bleichmitteln PY - 1934 VL - 13 IS - 14 SP - 241 EP - 245 PB - N.E.M.-Verl. CY - Berlin AN - OPUS4-16605 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wassermann, G. T1 - Über die Umwandlungsvorgänge in beta-Aluminiumbronze PY - 1934 VL - 13 IS - 8 SP - 133 EP - 139 PB - N.E.M.-Verl. CY - Berlin AN - OPUS4-16606 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Schikorr, Gerhard T1 - Über die Korrosion von Elektrolytzink und Raffinadezink PY - 1935 IS - 26 SP - 63 EP - 70 PB - Springer CY - Berlin AN - OPUS4-16607 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gonell, Hans-Wolfgang T1 - Gesteinsmehle als Füller im Bitumenstraßenbau PY - 1935 IS - 26 SP - 77 EP - 84 PB - Springer CY - Berlin AN - OPUS4-16609 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bierett, Georg A1 - Grüning, G. T1 - Spannungszustand und Festigkeit von Stirnkehlnahtverbindungen PY - 1934 IS - 25 SP - 11 EP - 22 PB - Springer CY - Berlin AN - OPUS4-16551 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schürmann, E. A1 - Charisius, Kurt T1 - Beitrag zur Herstellung von Chromgelb PY - 1935 IS - 26 SP - 85 EP - 90 PB - Springer CY - Berlin AN - OPUS4-16610 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rodt, V. T1 - Über das Fluatieren PY - 1935 IS - 26 SP - 91 EP - 95 PB - Springer CY - Berlin AN - OPUS4-16613 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schulze, Bruno A1 - Rieger, E. T1 - Über den getrennten Nachweis von Tierleim und Kasein im Papier PY - 1935 IS - 26 SP - 97 EP - 98 PB - Springer CY - Berlin AN - OPUS4-16615 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Hansen, Max T1 - Der Einfluß von dritten Metallen auf die Konstitution der Messinglegierungen - VI. Der Einfluß von Eisen - ein Beitrag zur Kenntnis des Dreistoffsystems Kupfer-Zink-Eisen PY - 1935 IS - 26 SP - 99 EP - 107 PB - Springer CY - Berlin AN - OPUS4-16617 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schürmann, E. A1 - Esch, W. T1 - Über die korrodierenden Einwirkungen von Asbest auf Nickel und dessen Legierungen PY - 1934 IS - 26 SP - 109 EP - 114 PB - Springer CY - Berlin AN - OPUS4-16619 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmid, Erich A1 - Wassermann, G. T1 - Über das System Aluminium-Zink PY - 1935 IS - 26 SP - 115 EP - 120 PB - Springer CY - Berlin AN - OPUS4-16621 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Wilhelm T1 - Zusammenhänge zwischen Kohäsion und Plastizität - (zum Festigkeitseffekt gereckter und gedrückter Proben) PY - 1935 IS - 26 SP - 121 EP - 122 PB - Springer CY - Berlin AN - OPUS4-16623 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rodt, V. T1 - Die Bestimmung des freien Kalkes im Zement PY - 1935 IS - 26 SP - 123 EP - 127 PB - Springer CY - Berlin AN - OPUS4-16625 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krisch, A. T1 - Apparatur zur Messung der Querdehnung, besonders in Kerben PY - 1935 IS - 26 SP - 129 EP - 132 PB - Springer CY - Berlin AN - OPUS4-16626 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krisch, A. T1 - Apparatur zur Messung der Querdehnung, besonders in Kerben PY - 1934 VL - 10 IS - 10 SP - 1 EP - 4(?) CY - Halle AN - OPUS4-16627 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Wilhelm T1 - Neuzeitliche Festigkeitsfragen PY - 1935 IS - 26 SP - 133 EP - 148 PB - Springer CY - Berlin AN - OPUS4-16628 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Shokouhi, Parisa A1 - Feldmann, Rüdiger A1 - Wiggenhauser, Herbert T1 - Stress-Dependency of Sonic Velocity in Concrete under Unaxial Load KW - Design KW - Public Transportation and Ferries KW - Safety PY - 2008 IS - CD-ROM (Paper 08-1450 / Session 568) SP - 1 EP - 15 PB - TRB CY - Washington, DC AN - OPUS4-16650 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Laute, K. T1 - Korrosion und Ermüdung PY - 1933 VL - 2 IS - ? SP - ? CY - Berlin AN - OPUS4-16656 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fiek, Georg A1 - Matting, A. T1 - Eignung des Faltversuches zur Prüfung von Schweissverbindungen PY - 1934 VL - 27 IS - 8 SP - ? CY - Halle, S AN - OPUS4-16657 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bierett, Georg A1 - Grüning, G. T1 - Schrumpfspannungen in autogen geschweissten Teilen PY - 1934 VL - 27 IS - 16 SP - ? CY - Halle, S AN - OPUS4-16659 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bierett, Georg T1 - Dauerfestigkeit von Schweißverbindungen PY - 1934 VL - 13 IS - 15-16 SP - 1015 EP - 1017 PB - VDI-Verl. CY - Berlin AN - OPUS4-16660 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Barbe, J. A1 - Barbier, J.-P. A1 - Currie, J. A1 - Jourdan, A. A1 - Schröder, Volkmar A1 - Schwarze, T. A1 - Stianchie, G. T1 - Code of practice - Compressed fluorine and mixtures with inert gases KW - Sicherheitstechnik KW - Industriegase KW - Prozesssicherheit KW - Materialkompatibilität PY - 2007 IS - 140/07/E SP - 1 EP - 28 PB - European Industrial Gases Association (EIGA) CY - Brussels AN - OPUS4-16661 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stöcke, K. T1 - Die Normenblätter DIN DVM 2201-2206 zur Prüfung von Dachschiefer PY - 1933 VL - 28 IS - 24 SP - 239 EP - 241 CY - Berlin AN - OPUS4-16663 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Burkert, Andreas A1 - Mietz, Jürgen A1 - Lehmann, Jens A1 - Eich, Gerd A1 - Burkert, Annette T1 - Verzinkte Bauteile in Kontakt mit Spanngliedern (Abschlussbericht für den Zeitraum 01.02.2005 bis 31.10.2007; Forschungsvorhaben 14218 N / 1) KW - Spannbeton KW - Spannstahl KW - Wasserstoffinduzierte Spannungsrisskorrosion KW - Verzinkte Einbauteile PY - 2007 SP - 1 EP - 42 PB - Bundesanstalt für Materialforschung und -prüfung CY - Berlin AN - OPUS4-16694 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schürmann, E. A1 - Esch, W. T1 - Über die Zerstörungserscheinungen an drahtgewickelten Rundfunkwiderständen mit Steatit-Isolierkörper PY - 1935 IS - 26 SP - 149 EP - 151 PB - Springer CY - Berlin AN - OPUS4-16630 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rodt, V. T1 - Zur Bestimmung des freien Kalkhydrates in erhärteten Zementen und Zement-Traßmischungen sowie des gebundenen Kalkhydrates in erhärteten Kalk-Traßmischungen PY - 1935 IS - 26 SP - 153 EP - 156 PB - Springer CY - Berlin AN - OPUS4-16632 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sieglerschmidt, H. A1 - Fiek, Georg T1 - Festigkeitsuntersuchungen antimonhaltiger Bleirohre PY - 1935 IS - 26 SP - 157 EP - 159 PB - Springer CY - Berlin AN - OPUS4-16633 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kindscher, Erich T1 - Unterwasseranstrich von Stahlbauteilen PY - 1935 IS - 26 SP - 161 EP - 166 PB - Springer CY - Berlin AN - OPUS4-16635 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Korn, Rudolph T1 - Fortschritte in der Papier- und Zellstoffprüfung im Jahre 1932 PY - 1933 VL - 13 IS - 5 CY - Berlin AN - OPUS4-16639 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Vollenbruck, O. T1 - Über den Angriff von Metallen durch Insekten - II. Mitteilung PY - 1931 IS - 18 SP - 3 PB - Springer CY - Berlin AN - OPUS4-16770 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ageew, N. A1 - Hansen, Max A1 - Sachs, Georg T1 - Entmischung und Eigenschaftsänderungen übersättigter Silber-Kupferlegierungen PY - 1931 IS - 18 SP - 3 EP - 15 PB - Springer CY - Berlin AN - OPUS4-16772 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Sipp, K. T1 - Der Einfluß von Phosphor, Schwefel, Nickel udn Chrom auf das Wachstum des Gußeisens PY - 1931 IS - 18 SP - 15 EP - 23 PB - Springer CY - Berlin AN - OPUS4-16776 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmid, Erich T1 - Über die Temperaturabhängigkeit der Plastizität von Kristallen PY - 1931 IS - 18 SP - 23 EP - 25 PB - Springer CY - Berlin AN - OPUS4-16777 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fahrenhorst, W. A1 - Schmid, Erich T1 - Über die Temperaturabhängigkeit der Kristallplastizität - II. PY - 1931 IS - 18 SP - 26 EP - 30 PB - Springer CY - Berlin AN - OPUS4-16779 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bierett, Georg A1 - Grüning, G. T1 - Versuche zur Ermittlung der statischen Wirkung von Verstärkungen massiver Bauwerke, ausgeführt an den Bogen der Berliner Stadtbahn und am Chemnitztalviadukt in Chemnitz PY - 1936 IS - 27 SP - 1 EP - 14 PB - Springer CY - Berlin AN - OPUS4-16732 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Meissner, W. A1 - Polanyi, M. A1 - Schmid, Erich T1 - Messungen mit Hilfe von flüssigem Helium. XII. - Plastizität von Metallkristallen bei tiefsten Temperaturen PY - 1931 IS - 18 SP - 30 EP - 35 PB - Springer CY - Berlin AN - OPUS4-16780 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wassermann, G. T1 - Über die Zerreißfestigkeit und Spaltbarkeit von Wismut- und Antimonkristallen PY - 1931 IS - 18 SP - 35 EP - 38 PB - Springer CY - Berlin AN - OPUS4-16782 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sachs, Georg A1 - Weerts, J. T1 - Elastizitätsmessungen mit Röntgenstrahlen PY - 1931 IS - 18 SP - 39 EP - 45 PB - Springer CY - Berlin AN - OPUS4-16783 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Boas, W. A1 - Rupp, E. T1 - Über Elektronenbeugung an sauerstoffbedecktem Wolfram PY - 1931 IS - 18 SP - 45 EP - 51 PB - Springer CY - Berlin AN - OPUS4-16784 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Vogel, O. T1 - Untersuchungen an technischen Gußlegierungen PY - 1931 IS - 18 SP - 51 EP - 83 PB - Springer CY - Berlin AN - OPUS4-16785 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Vollenbruck, O. A1 - Schikorr, Gerhard T1 - Spannungsmessungen und Lösungsversuche mit Zinn-Kupfer und Zink-Kupfer-Legierungen PY - 1932 IS - 19 SP - 3 EP - 15 PB - Springer CY - Berlin AN - OPUS4-16787 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmid, Erich T1 - Beiträge zur Physik und Metallographie des Magnesiums PY - 1932 IS - 19 SP - 16 EP - 25 PB - Springer CY - Berlin AN - OPUS4-16788 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Boas, W. A1 - Schmid, Erich T1 - Über die Temperaturabhängigkeit der Kristallplastizität PY - 1932 IS - 19 SP - 25 EP - 29 PB - Springer CY - Berlin AN - OPUS4-16789 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sachs, Georg T1 - Untersuchungen über Tiefziehen PY - 1931 IS - 16 SP - 11 EP - 38 PB - Springer CY - Berlin AN - OPUS4-16750 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Linicus, W. A1 - Sachs, Georg T1 - Versuche über die Eigenschaften gezogener Drähte und den Kraftbedarf beim Drahtziehen PY - 1931 IS - 16 SP - 38 EP - 67 PB - Springer CY - Berlin AN - OPUS4-16751 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Eisbein, W. A1 - Sachs, Georg T1 - Kraftbedarf und Fließvorgänge beim Stangenpressen PY - 1931 IS - 16 SP - 67 EP - 96 PB - Springer CY - Berlin AN - OPUS4-16752 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Friedrich Wilhelm A1 - Sachs, Georg T1 - Eindruckvorgänge in Metallen PY - 1931 IS - 16 SP - 96 EP - 127 PB - Springer CY - Berlin AN - OPUS4-16754 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Hansen, Max T1 - Der Einfluß von dritten Metallen auf die Konstitution der Messinglegierungen - III. der Einfluß von Zinn PY - 1931 IS - 17 SP - 3 EP - 20 PB - Springer CY - Berlin AN - OPUS4-16755 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmid, Erich A1 - Wassermann, G. T1 - Über die Anistropie von Zinkblechen PY - 1931 IS - 17 SP - 20 EP - 24 PB - Springer CY - Berlin AN - OPUS4-16756 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Zunker, P. T1 - Einfluß geringer Mengen von Fremdmetallen auf die Eigenschaften von Raffinadezink PY - 1931 IS - 17 SP - 24 EP - 34 PB - Springer CY - Berlin AN - OPUS4-16758 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hengstenberg, J. A1 - Wassermann, G. T1 - Über röntgenographische Untersuchungen der Kaltvergütung des Duralismus PY - 1931 IS - 17 SP - 34 EP - 38 PB - Springer CY - Berlin AN - OPUS4-16759 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Richter, Matthias A1 - Jann, Oliver A1 - Kemski, J. A1 - Klingel, R. A1 - Schneider, Uwe A1 - Krocker, Christian T1 - Investigations on radon exhalation of different building materials N2 - The inhalation of 222Rn (radon) is one of the most important reasons for lung cancer, after smoking. Usually, the geological subsoil and the building ground are the dominant sources for enhanced indoor radon levels. Additionally, building materials can increase indoor radon concentrations when these materials contain higher contents of 226Ra (radium), especially in combination with low air exchange rates. For a realistic estimation of indoor radon concentrations, it is helpful to carry out measurements of radon exhalation rates from relevant materials using emission test chambers. In Germany, it is aspired to limit the total indoor radon concentration to 100 Bq/m3, whereby building materials should contribute at most 20 Bq/m3. Within a project financed by the German Institute for Construction Technology (DIBt), a practical oriented measurement procedure of the radon exhalation of building materials in accordance to ISO 16000-9 was developed to have a means for the assessment of these materials with respect to their indoor use. Test chambers with different volumes were used. The tested materials were mainly used for wall constructions (e.g., bricks, light-weight concrete) and have known specific radium activities and radon exhalation rates. T2 - Indoor Air 2011, 12th International conference on indoor air quality and climate CY - Austin, TX, USA DA - 05.06.2011 KW - Radon exhalation KW - Building material KW - Emission test chamber KW - Indoor air PY - 2011 IS - Paper 768 SP - 1 EP - 2 AN - OPUS4-24155 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wille, Frank A1 - Wolff, Dietmar A1 - Droste, Bernhard A1 - Völzke, Holger T1 - Requirements for transport packages after interim storage N2 - In Germany the concept of dry interim storage of spent fuel and vitrified high active waste in dual purpose metal casks is implemented (currently for periods of up to 40 years). The casks being used have an approved package design in accordance with the international transport regulations. The license for dry storage is granted on the German Atomic Energy Act with respect to the guidelines of the German Reactor Safety Commission for dry interim storage of spent fuel. Currently part of the assessment process of the cask design for transport on public routes is to evaluate the suitability of the used materials with respect to their properties and their compatibility for possible transport periods. For transport on public routes during or after long term interim storage periods, it has to be ensured that the transport and storage casks fulfill the specifications of the transport approval or other sufficient properties which satisfy the proofs for the compliance of the safety objectives at that time. This paper describes the state-of-the-art technology in Germany and points out arising prospective challenges and which related questions have to be answered in future. Present research and knowledge concerning the long term behavior of transport and storage cask components (such as gaskets and shielding components) have to be consulted as well as experiences from interim cask storage operations. Challenges in the safety assessment are therefore i.e. the behavior of aged metal and elastomeric gaskets under IAEA test conditions to ensure that the results of drop tests can be transferred to the compliance of the safety objectives at the time of transport after the interim storage period (aged package). Assessment methods for the material compatibility, the behavior of fuel assemblies and the aging behavior of shielding parts (e. g. influence of radiation) are further issues as well. T2 - 52nd INMM Annual meeting CY - Palm Desert, CA, USA DA - 17.07.2011 KW - Transport package design KW - Interim storage KW - Inspections KW - Log term behavior KW - Dual purpose casks PY - 2011 SP - 1 EP - 9 AN - OPUS4-24172 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völzke, Holger A1 - Probst, Ulrich A1 - Wolff, Dietmar A1 - Nagelschmidt, Sven A1 - Schulz, Sebastian T1 - Investigations on the long term behavior of metal seals for spent fuel storage casks N2 - Metal seals are in common use as an essential component for the leak tight closure of transport and storage casks for spent fuel and vitrified high active waste from reprocessing. They are placed between the massive monolithic cask body made of ductile cast iron or forged steel and the primary and secondary lids, which are fixed with screws around the lid circumference, in order to ensure long term safe enclosure of the radioactive cask inventory. Hereby, long term reliable pressure forces in combination with a tight surface contact are as important as well maintained seal and surface qualities and dry and clean conditions during seal assembly and operation. A few years ago BAM started systematic investigation on the long term seal behavior with re-spect to longer storage periods and seal behavior in accidental cask scenarios with dynamic de-formations of the seal groove geometry or short term drop in pressure force up to lid lifting. BAM has developed test flanges for seals with full scale cross section diameter but much small-er outer diameter to gain representative data for metal-sealed lid systems. They are placed in appropriate testing machines for relevant mechanical loading under static and dynamic condi-tions with the ability to measure the standard helium leakage rate continuously during each test phase. This paper focuses on BAM long term tests of different seal types with aluminum and silver jackets at three different temperatures of +20°C, +100°C and +150°C under static conditions over longer periods of time. Due to creeping effects, a reduction of the pressure force does ap-pear during loading and unloading depending on prior holding times. So far, test results of up to 2 years indicate a clear correlation between seal pressure forces and holding time, temperature and seal type allowing for extrapolating to much longer periods of time. The paper presents basic correlations, test and evaluation procedures as well as important provisional results and gives an outlook on further investigations. T2 - 52nd INMM Annual meeting CY - Palm Desert, CA, USA DA - 17.07.2011 PY - 2011 SP - 1 EP - 9 AN - OPUS4-24173 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Torge, Manfred A1 - Müller, Wolfgang A1 - Adam, Karin T1 - Scientific examinations of historical stained glass N2 - The aim of this article is to provide an overview of the composition of historical glasses, to discuss the ensuing problems when attempting to restore medieval church windows, and to illustrate how scientific examination of glass surfaces can be used to select an appropriate cleaning method. PY - 2001 UR - http://www.struers.com/resources/elements/12/2436/38art6.pdf IS - 38 SP - 25 EP - 29 PB - Struers CY - Willich AN - OPUS4-24076 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Binkowski, Sigrid A1 - Pahl, Regina A1 - Woydt, Mathias T1 - Comparing preparation techniques using microstructural images of ceramic materials N2 - The article describes different materialographic preparation techniques and shows images of a large variety of different types of ceramics obtained using different examination methods. PY - 2002 UR - http://www.struers.com/resources/elements/12/3698/39art2.pdf IS - 39 SP - 8 EP - 19 PB - Struers CY - Willich AN - OPUS4-24077 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Köppe, Enrico A1 - Bartholmai, Matthias ED - Tsamis, C. ED - Kaltsas, G. T1 - Wireless sensor network with temperature compensated measuring technology for long-term structural health monitoring of buildings and infrastructures N2 - Damage to buildings occurs if a construction component fails. The result is a partial or total collapse which can be dangerous for people for example if it's a bridge or a large hall. The collapse of the terminal building at the Airport Charles de Gaulle in Paris and the damage at the historic City Archives of Cologne are typical examples of such accidents. Another problem is the contradiction of the increasing volume of traffic (particularly heavy traffic) and the great age of bridges. The probability increases that the load-bearing capacity of a bridge decreases. For example the collapses of the Mississippi Bridge and of the Inntal Motorway Bridge can be seen as results. Therefore it is necessary to control endangered structures during their life span. In order to prevent these kinds of accidents, the Federal Institute for Materials Research and Testing developed a radio-based, self-configuring measuring system in cooperation with the ScatterWeb Company, Berlin (Germany). This measuring system consists of identically designed sensor modules which are self-sustaining, wireless, act as transmitters and receivers and are equipped with a special sensor technology for long-term monitoring of buildings or engineering facilities. The sensor unit uses strain gauges for stress analysis and contains interfaces for additional sensors. The system in particular applies to buildings and structures for transport and traffic and large-scale industrial facilities, where a subsequent wiring installation is difficult or impossible. T2 - Eurosensors XXV CY - Athens, Greece DA - 04.09.2011 KW - Multi-Hop WSN KW - SHM KW - Temperature and Frequency Compensation KW - Funksensorik KW - Sensornetzwerk KW - Multihop KW - Strukturüberwachung KW - Temperaturkompensation PY - 2011 UR - http://www.sciencedirect.com/science/article/pii/S1877705811059236 IS - Paper 1197 SP - 1 EP - 5 PB - Elsevier AN - OPUS4-24401 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Köppe, Enrico A1 - Bartholmai, Matthias A1 - Liers, A. A1 - Schiller, J. T1 - Tracking persons using a radio-based multi-sensor system N2 - A multi-sensor system for 3D localization was developed and named BodyGuard. It combines body movement sensing and a guard system for the tracking and recording of the status of persons. BodyGuard was designed to monitor and transmit the movement of a person radio-based and to transform that data into a spatial coordinate. This paper describes how the BodyGuard system works, what components the system consists of, how the individual sensor data is converted into 3D motion data, with which algorithms the individual sensors are processed, how individual errors are compensated and how the sensor data are fused into a 3D Model. T2 - IPIN 2011 - International conference on indoor positioning and indoor navigation CY - Guimaraes, Portugal DA - 21.09.2011 KW - Wireless sensor network (WSN) KW - Embedded systems KW - Sensor calibration and validation KW - Person tracking KW - Inertial navigation system KW - Inertial measurement unit PY - 2011 SP - 1 EP - 4 AN - OPUS4-24402 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Horn, Wolfgang A1 - Müller, B. A1 - Panaskova, J. A1 - Jann, Oliver A1 - Plehn, W. A1 - Müller, D. T1 - VOC emissions from building materials accompanying sensory tests for different evaluation schemes N2 - Within a follow up project of a former study (Horn et al. 2005) emissions and odor from different types of construction products were investigated (financed by the German Federal Environmental Agency - FKZ 37 07 62 300). The tested materials were mainly those used for construction of floors indoors. For this type of materials in Germany several labeling procedures exist which are based on Emission chamber testing. Two important labeling procedures in Germany are based on the AgBBevaluation scheme (Däumling et al. 2005). For some applications (flooring material) it is the mandatory Ü-mark of DIBt (German Institute for Construction Technology). Furthermore for carpets, adhesives and many other products, like sealants, mattresses, furniture and so on the voluntary blue angel mark exist. Within this scheme the volatile organic compounds (VOC) compounds are measured with well established procedures and are evaluated with LCI-values which were derived from health information. Beyond that many complaints according to building products are caused by odors. Therefore an evaluation procedure for the odor is very important and should be implemented into all of the mentioned labeling schemes. T2 - Indoor Air 2011, 12th International conference on indoor air quality and climate CY - Austin, TX, USA DA - 05.06.2011 KW - Odor KW - Construction product KW - VOC-emission KW - Evaluation KW - AgBB PY - 2011 IS - Paper 768 SP - 1 EP - 2 AN - OPUS4-23881 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, B. A1 - Panaskova, J. A1 - Jann, Oliver A1 - Horn, Wolfgang A1 - Müller, D. A1 - Plehn, W. T1 - Results of sensory tests and sensory-limit settings for building materials in Germany N2 - Indoor air pollutants influence the health and comfort of building occupants and consequently the energy consumption of the building. The pollutants are emitted by various sources. Among these sources, building products are of particular importance. To control the emission of pollutants from building materials, a few different voluntary labelling Systems have been introduced in Europe. In Germany also mandatory “Principles for the health assessment of construction products used in interiors” have been applied for the technical approval of floor coverings since 2004. This procedure is based on the assessment scheine of the Committee for Health-related Evaluation of Building Products (AgBBScheme). The sensory-limit settings for building-material label Blue Angel offer consumer to differ not only low-emission but also low-odour Building materials from another building materials. T2 - Indoor Air 2011, 12th International conference on indoor air quality and climate CY - Austin, TX, USA DA - 05.06.2011 KW - Perceived air-quality KW - Odour evaluation KW - Odour labelling KW - Test procedure KW - Standardisation PY - 2011 IS - Paper 768 SP - 1 EP - 2 AN - OPUS4-23882 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilke, Olaf A1 - Horn, Wolfgang A1 - Wiegner, Katharina T1 - Inter-laboratory study to check the performance ot test chamber measurements for product emission testing N2 - The labelling of construction products or building materials as “low-emitting” is based on measurements using third-party emission test chambers. Unfortunately there is no method to validate the performance of such test chamber measurements. This might give a Variation of results when testing one material at different laboratories. Therefore it is necessary to hold round robin tests as part of the quality management System to ensure comparable results. A research project financed by the Federal Environmental Agency focused on the development of an external quality management System for the detection of relevant Chemical compounds from products and in ambient air. The project was structured in four phases (Horn et al., 2009 and 2011; Wilke et al., 2009a) This paper shows results of the fourth phase of the project, which was an inter-laboratory study for VOC-emission testing by means of emission test chambers. T2 - Indoor Air 2011, 12th International conference on indoor air quality and climate CY - Austin, TX, USA DA - 05.06.2011 KW - Emission test chamber KW - Product emission testing KW - VOC-Emission KW - Round robin test PY - 2011 IS - Paper 768 SP - 1 EP - 2 AN - OPUS4-23884 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Mike A1 - Wille, Frank A1 - Ballheimer, Viktor A1 - Musolff, André T1 - From experiment to an appropriate finite element model-safety assessment for ductile cast iron casks demonstrated by means of IAEA puncture drop test N2 - In the approval procedure of transport packages for radioactive materials, the competent authority mechanical and thermal safety assessment is carried out in Germany by BAM Federal Institute for Materials Research and Testing. The combination of experimental investigations and numerical calculations in conjunction with materials and components testing is the basis of the safety assessment concept of the BAM. Among other mechanical test scenarios a 1 meter drop test onto a steel bar has to be considered for hypothetical accident conditions of Type B packages according to IAEA regulations. Within the approval procedure for the new German package design of the HLW cask CASTOR® HAW 28M, designed by GNS Gesellschaft für Nuklear-Service Germany, a puncture drop test was performed with a half-scale model of the cask at -40°C. For independent assessment and to control the safety analysis presented by applicant, BAM developed a complex finite element model for a dynamical ABAQUS/ExplicitTM analysis. This paper describes in detail the use of the finite element (FE) method for modeling the puncture drop test within an actual assessment strategy. At first investigations of the behaviour of the steel bar are carried out. Different friction coefficients and the material law of the bar are analysed by using a 'rigid-body' approximation for the cask body. In the next step a more detailed FE model with a more realistic material definition for the cask body is developed. Strain verification is possible by results of the strain gauges located at the relevant points of the cask model. The influence of the finite element meshing is described. Finally, the verified FE half-scale model is expanded to full-scale dimension. Scaling effects are analysed. The model is used for safety assessment of the package to be approved. T2 - PATRAM 2010 - 16th International symposium on the packaging and transport of radioactive materials CY - London, UK DA - 2010-10-03 KW - IAEA KW - Puncture drop test KW - Numerical analysis KW - Verification PY - 2010 SP - 1-8 (Tuesday/T19/26-115) AN - OPUS4-23928 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard A1 - Ulrich, Armin A1 - Borch, Jörg-Peter T1 - Brandnew fire test facilities at 'BAM test site technical safety' N2 - Fire testing is an essential part of the hypothetical, cumulative mechanical and thermal accident test conditions that shall guarantee package safety in severe accidents. Not only for radioactive material transport packages but also for other containments of dangerous goods international standards require specific thermal load specifications. Following the guideline 'Safety in tech-nology and chemistry' BAM as a scientific and technical German federal government institute operates a 12 km² large open air test facility for experimental investigations of dangerous goods and their containments. On an area besides the well-known 200-ton drop test facility we put into operation new fire test facilities. This facility area provides two fire test stands that are utilized with liquid Propane as fuel from a central earth-covered 60 m³ LPG storage tank. From that stor-age the Propane is pumped via pipelines to the test stands where the gas is released from nozzles, and ignited by ignition burners. The fire exposed test facility areas are 12 m x 8 m. Fire test facil-ity B (with gas release nozzles below water-covered ground) is designed for fire testing of con-tainers that may burst during the test. Fire test facility A (with ring burner systems) is designed for heavy test objects up to 200 tons, e.g. for full-scale spent fuel casks. The paper will present a detailed description of the facility, insight into first test performances, and results of calorimeter fire tests, using containers of various sizes, to verify the absorbed heat fluxes, demonstrating that regulatory fire test conditions are met, and that the Propane fire can be compared with a kerosene or heating oil pool fire. T2 - PATRAM 2010 - 16th International symposium on the packaging and transport of radioactive materials CY - London, UK DA - 2010-10-03 KW - Transport und Lagerung radioaktiver Stoffe KW - Gefahrgutrechtliche Bauartprüfung KW - Brandversuche PY - 2010 SP - 1 EP - 8 (Wednesday/Poster Session/218) AN - OPUS4-23900 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Perret, Birgit A1 - Schartel, Bernhard T1 - TGA-FTIR: Von der Untersuchung der Pyrolyse zur Aufklärung von Flammschutzmechanismen KW - TGA-FTIR KW - Flammschutz KW - Pyrolyse PY - 2010 VL - 32 SP - 16 EP - 19 AN - OPUS4-23904 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Perret, Birgit A1 - Schartel, Bernhard T1 - TGA-FTIR: From the investigation of pyrolysis to the elucidation of fire retardancy mechanisms KW - TGA-FTIR KW - Flammschutz KW - Pyrolyse PY - 2010 VL - 32 SP - 16 EP - 19 AN - OPUS4-23905 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Perret, Birgit A1 - Schartel, Bernhard T1 - TGA-FTIR: Détermination des mécanismes ignifuges par l´étude de la pyrolyse KW - TGA-FTIR KW - Flammschutz KW - Pyrolyse PY - 2010 VL - 32 SP - 16 EP - 19 AN - OPUS4-23906 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erhard, Anton A1 - Völzke, Holger A1 - Probst, Ulrich A1 - Wolff, Dietmar T1 - Ageing management for long term interim storage casks T2 - PATRAM 2010 - 16th International symposium on the packaging and transport of radioactive materials CY - London, UK DA - 2010-10-03 KW - Ageing management KW - Lifetime KW - Material degradation PY - 2010 SP - 1 EP - 17 (Tuesday/T20/61) AN - OPUS4-23907 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Musolff, André A1 - Komann, Steffen A1 - Droste, Bernhard A1 - Müller, Karsten A1 - Quercetti, Thomas T1 - Drop test program with a HLW cask model - performance, measurements and results N2 - BAM (Federal Institute for Material Research and Testing) is the competent authority for mechanical and thermal safety assessment of transport packages for spent fuel and high level waste (HLW) in Germany. In context with package design approval of the new German HLW cask CASTOR HAW28M, BAM performed several drop tests with a half-scale model of the CASTOR HAW/TB2. The test model was manufactured by GNS (Gesellschaft fur Nuklear Service mbH) and tested under accident transport conditions on the 200 tons BAM drop test facility at the BAM Test Site Technical Safety. For this comprehensive test program the test specimen CASTOR HAW/TB2 was instrumented at 21 measurement planes with altogether 23 piezo-resistive accelerometers, five temperature sensors and 131 tri-axial strain gauges in the container interior and exterior, respectively. The strains of four representative lid bolts were recorded by four uniaxial strain gauges per each bolt. Helium leakage rate measurements were performed before and after each test in the above noted testing sequence. The paper presents some experimental results of the half-scale CASTOR HAW/TB2 prototype (14,500 kg) and measurement data logging. T2 - 52nd INMM Annual meeting CY - Palm Desert, CA, USA DA - 17.07.2011 KW - Drop test results KW - Spent fuel transport cask KW - Impact limiter KW - Measurement methods KW - Drop test program PY - 2011 SP - 1 EP - 9 AN - OPUS4-24245 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Beck, M. A1 - Burkert, Andreas T1 - Korrosion von Stahl in Beton N2 - Die Sicherstellung der Dauerhaftigkeit von Stahlbetonbauwerken erfolgt über Regelwerke, die auf einem umfangreichen Wissen über die Eigenschaften der verwendeten Baustoffe beruhen. Weiterhin dienen Beobachtungen und Untersuchungen dazu, eine genaue Aussage über den Ist-Zustand von Bauwerken abgeben zu können. Eine detaillierte Bestandsaufnahme und Zustandsanalyse auf Grundlage geeigneter Messdaten ermöglicht eine Prognose über die verbleibende Nutzungsdauer. Fortlaufende Untersuchungen können auch dazu genutzt werden, Wartungs- und Sanierungsintervalle auf der Grundlage von Regelwerken zu koordinieren und so den Erhalt von Bauwerken zu sichern. KW - Stahlbeton KW - Passivität KW - Depassivierung KW - Karbonatisierung KW - Chlorinduzierte Korrosion PY - 2011 VL - 2 SP - 5 EP - 8 PB - VBD-Geschäftsstelle CY - Hannover AN - OPUS4-24246 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Marotzke, Christian A1 - Basan, Ricardo T1 - Micromecanics based failure analysis of laminates under off-axis loading N2 - The debonding of a fiber in a glass fiber / epoxy composite under transverse loading is studied. The stress field in the interface as well as the energy release rate are analysed for two fiber volume fractions. The circumferential propagation of an Interface crack starting at the center of a fiber which is located within a hexagonal fiber array is studied. The analysis is performed by a finite element Simulation under plane stress conditions. Two fiber volume fractions are considered, this is 30% and 70%. The stress distribution before and during crack propagation is calculated for different stages of the crack. The crack opens by dominating tensile stresses in the first phase while it closes when propagating along the interface. The total energy release rate as well as the mode I and mode II parts are calculated. In the first phase the crack is driven by an increasing mode I energy release rate, indicating an unstable crack propagation. Then the mode II energy release rate increases rapidly and dominates the debonding process while the mode I part decreases and finally vanishes. Subsequently also the mode II part decreases, indicating stable crack propagation. In the last phase the crack becomes unstable again due to a strongly increasing mode I energy release rate. During the debonding process a remarkable change the mode ratio takes place. The main features of the debonding process are similar for low and high fiber volume fraction. In case of the high fiber content, however, the mode I part is more pronounced and the maximum of the total energy release rate is shifted to lower crack angles. T2 - ICCM 18 - 18th International conference on composite materials CY - Jeju Island, Korea DA - 21.08.2011 KW - Composite Materials KW - Interface Crack KW - Failure Analysis KW - Adhesion PY - 2011 IS - T35-3-IF2032 SP - 1 EP - 6 AN - OPUS4-24252 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eisenacher, Germar A1 - Scheidemann, Robert A1 - Neumann, Martin A1 - Wille, Frank A1 - Droste, Bernhard T1 - Approach for a finite element material model for wood for application in mechanical safety cases of transport packages N2 - BAM Federal Institute for Materials Research and Testing is the competent authority for mechanical safety assessment of transport packages for radioactive material in Germany. The further development of state-of-the-art technology concerning assessment methods is essential for a qualified work of involved designers and authority experts. The paper gives an example of current development done to improve understanding and modeling capabilities of wood filled impact limiter. In order to reduce the loads applied to the package containment, which result from regulatory drop tests, most packages are protected by energy dissipating impact limiter. Wood, encapsulated by steel sheets, is one of the materials typically used for energy dissipation in these impact limiter. Very often, mechanical safety cases regarding the 9 m drop test are performed computationally, where it is essential to use reliable and verified computational methods and models. In this context, the paper presents an approach for a finite element material model for wood. Thereby, the mechanical behavior of wood under compression loading is the focus of the development work. Additionally, material orientation as well as strain rate, temperature and lateral constraint may vary. A large number of experiments, particularly compression tests, was designed and performed to establish an adequate experimental database for modeling verification. The experimental results enabled the derivation of necessary requirements: The material model has to take into account strain rate and temperature dependencies as well as the anisotropic characteristics of the material, a proper yield criterion, flow rule and hardening law. Such a material model is currently not available in established commercial dynamic finite element codes. Thus it is necessary to create a user-defined material model considering the mentioned requirements. A first step was done by determining a yield surface as well as detecting flow and hardening mechanisms from experimental force-deflection curves. In a next step the LS-DYNA material model MAT_75 was altered according to conclusions of former BAM development work, regarding the modeling of post-peak softening as a function of lateral constraint. Future research will contain the further development, implementation and verification of a material model for wood. T2 - 52nd INMM Annual meeting CY - Palm Desert, CA, USA DA - 17.07.2011 KW - Impact limiter KW - Material model wood KW - Transport package PY - 2011 SP - 1 EP - 8 AN - OPUS4-24236 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mishra, Kirti Bhushan A1 - Wehrstedt, Klaus-Dieter A1 - Schönbucher, A. T1 - Interpretations of temperature measurements in organic peroxide pool fires N2 - Most of the measurements of temperatures in large pool fires are indirect and present a number of complexities due to the interactions of convection, radiation and soot blockage. In the present work these influences for two organic peroxide [tert-butyl peroxybenzoate (TBPB) and tert-butyl peroxy-2-ethylhexanoate (TBPEH)] pool fires are analysed. Thermocouple measured temperature in the clear flame zone i.e. combustion zone are found to be 250-400 K lower than from the thermographic measurements. The convective and radiative heat flux contributions from the fire on temperature measurements are discussed. CFD (Computational Fluid Dynamics) simulations have been performed for large pool fires and the predicted time averaged flame temperatures were found to be in qualitative agreement with measurements due to the stoichiometric combustion model used in the present simulations. T2 - 5th European combustion meeting 2011 CY - Cardiff, UK DA - 28.06.2011 KW - Pool fire KW - Organic peroxides KW - TBPB KW - TBPEH KW - CFD KW - Temperature measurement PY - 2011 UR - http://www.uni-due.de/tchem/as/skripte/paper_mishra_et_al_cardiff_2011.pdf SP - 1 EP - 5 AN - OPUS4-24686 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schälike, Stefan A1 - Wehrstedt, Klaus-Dieter A1 - Schönbucher, A. T1 - CFD simulation to predict the thermal radiation of large LNG pool fires N2 - Flame temperature (T), surface emissive power (SEP) of Liquefied Natural Gas (LNG) pool fires (d = 1 m, 6.1 m, 30 m) are investigated by CFD (Computational Fluid Dynamics) simulation and compared with experimental results. Time averaged flame temperatures of T = 1320 K, T = 1298 K and T = 1281 K are obtained. Surface emissive power (SEP) of 55 kW=m2, 130 kW=m2 and 230 kW=m2 are predicted. T2 - 5th European combustion meeting 2011 CY - Cardiff, UK DA - 28.06.2011 KW - Pool fire KW - LNG KW - CFD KW - Thermal radiation KW - Surface emissive power PY - 2011 SP - 1 EP - 6 AN - OPUS4-24687 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nöther, N. A1 - Krebber, Katerina A1 - Schneider-Glötzl, J. T1 - An all-digital implementation of the Brillouin optical frequency domain analysis for long-range distributed strain and temperature monitoring N2 - For long-range measurements in geotechnical and industrial applications, distributed optical fiber sensors have become a tool of increasing importance throughout the past decade. Classic deformation monitoring (performed by strain gauges etc.) and temperature monitoring (Pt100 and alike) deliver data from fixed, single spots of a structure; quasidistributed measurements (fiber bragg gratings) provide a Chain of discrete measurement points along a limited sensing length. In contrast, an opticai fiber connected to a device for distributed strain and temperature sensing (DTSS) will provide a continuous profile of strain and temperature - spatially resolved down to less than 1 m - over a ränge of several tens of kilometers. In DTSS measurements, the nonlinear opticai effect of stimulated Brillouin Scattering (SBS) is employed: two light waves with a stable, tunable frequency offset are injected into opposite ends of the sensing fiber, where they will form a beat pattem, at which parts of the light will be scattered. By matching the frequency offset of the light waves to the propagation of acoustic fluctuation in the opticai fiber, a power transfer from one light wave to the other can be measured; since the acoustic propagation directly shifts with train and temperature of the fiber, these two quantities can be measured by tuning the light waves’ frequency offset. T2 - 8th International symposium on field measurements in geomechanics - FMGM 2011 CY - Berlin, Germany DA - 12.09.2011 PY - 2011 SP - 1 EP - 6 AN - OPUS4-24664 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mishra, Kirti Bhushan A1 - Wehrstedt, Klaus-Dieter T1 - An efficient and clean fuel for high temperature process industries N2 - The use of energetic materials as a main fuel in high temperature process industries are not known to the scientific community as such. This paper highlights some of the features and advantages of using organic peroxides especially di-tert-butyl peroxide (DTBP) in high temperature process industries. The feasibility of using DTBP as a main or supporting fuel in process industries have also been justified with the help of Computational Fluid Dynamics (CFD) simulations. For peroxides requirement of less fuel and air for the same amount of heat flux has been shown. The resulted emission from the combustion of DTBP is also discussed. T2 - 11th Conference on Energy for a Clean Environment CY - Lisbon, Portugal DA - 2011-07-05 KW - Energetic materials KW - Process industries KW - Organic peroxide KW - Di-tert-butylperoxide (DTBP) KW - CFD simulation KW - Emission PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-247071 SP - 1 EP - 10 AN - OPUS4-24707 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mishra, Kirti Bhushan A1 - Wehrstedt, Klaus-Dieter T1 - Combustion of peroxy-fuels N2 - The diffusion flames of organic peroxides exhibit quite different characteristics than hydrocarbons. What makes them interesting to study is their fast burning behaviour. As a result the flame temperature enhances and so does the thermal radiation. Due to all these they demand safe handling during processing. However, they can be utilised at several places in different industries where a fuel with fast burning, high temperature and intense radiation are desired. Some of the possibilities to use them as a main or supporting fuel in a wide range of industrial utilities are the major content of this paper. T2 - ERCOFTAC conference - Highly resolved experimental and numerical diagnostics for turbulent combustion CY - Rouen, France DA - 25.05.2011 KW - Energetic materials KW - Process industries KW - Organic peroxide KW - Di-tert-butyl peroxide (DTBP) KW - CFD simulation KW - Emission PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-247083 SP - 1 EP - 5 AN - OPUS4-24708 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scholz, Christian A1 - Woydt, Mathias T1 - Highly stressable and low friction slip-rolling contacts through thin film coatings, uncoated, alternative steels or lubricants N2 - OEMs perceive diamond-like carbon (DLC) coatings as part of a strategy for low frictional tribosystems. Especially the automotive industry anticipates a benefit in applying such coatings in association with the lightweight construction of mechanical parts, for instance in gears and engines. In previous investigations it was shown, that DLC, amorphous carbon (a-C) and tetragonal amorphous carbon (ta-C) coatings can be slip-rolling resistant at least up to ten million load cycles at Hertzian contact pressures P0max of 2.9 GPa lubricated by engine oil at 120°C, Further improvements in load carrying capacity up to P0mean of 2.62 GPa (FN= 5,000 N) were achieved with alternative, available Steel metallurgies as Substrates for thin film coatings. Additional factors, such as influences of the lubrication on the surface chemistry (additives and base oils), wear and friction behavior were investigated. T2 - International tribology conference 2011 CY - Hiroshima, Japan DA - 30.10.2011 KW - Slip-rolling KW - Additives KW - DLC KW - ZrCN KW - High toughness steel KW - High pressure PY - 2011 IS - B4-08 SP - 1 EP - 1 AN - OPUS4-24702 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Witt, Jens A1 - Breithaupt, Mathias A1 - Erdmann, Jessica A1 - Krebber, Katerina T1 - Humidity sensing based on microstructured POF long period gratings N2 - We investigated the capabilities of long period gratings (LPG) in single-mode microstructured polymer optical fibre (mPOF) for humidity sensing. For that mPOF LPGs were exposed to different humidity levels at a constant temperature of 30°C in a climate chamber. During the long term tests, which took up several weeks, the humidity was changed in several steps while mPOF LPG wavelength and fibre attenuation were measured. We also measured the water uptake of mPOF in environment with different relative humidity. T2 - POF 2011 - 20th International conference on plastic optical fibers CY - Bilbao, Spain DA - 14.09.2011 KW - Microstructured polymer optical fibre (mPOF) KW - Long period grating (LPG) KW - Humidity sensor PY - 2011 SP - 1 EP - 6 AN - OPUS4-24501 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz ED - Papadrakakis, M. ED - Fragiadakis, M. ED - Plevris, V. T1 - High-speed railway tracks of a surface, bridge and tunnel line and some effects on the train-induced bridge and ground vibrations T2 - COMPDYN 2011 - 3rd International thematic conference - Computational methods in structural dynamics and earthquake engineering CY - Corfu, Greece DA - 2011-05-25 KW - Track compliance KW - Surface line KW - Bridge track KW - Tunnel track KW - Ground vibration KW - Layered soil KW - Bridge resonance KW - Train speed KW - Axle sequence KW - Track irregularities PY - 2011 SP - 1 EP - 17(?) AN - OPUS4-24555 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Patrick P. A1 - Asadi, S. A1 - Schiller, J.H. A1 - Lilienthal, A.J. A1 - Bartholmai, Matthias T1 - An artificial potential field based sampling strategy for a gas-sensitive micro-drone N2 - This paper presents a sampling strategy for mobile gas sensors. Sampling points are selected using a modified artificial potential field (APF) approach, which balances multiple criteria to direct sensor measurements towards locations of high mean concentration, high concentration variance and areas for which the uncertainty about the gas distribution model is still large. By selecting in each step the most often suggested close-by measurement location, the proposed approach introduces a locality constraint that allows planning suitable paths for mobile gas sensors. Initial results in simulation and in real-world experiments with a gas-sensitive micro-drone demonstrate the suitability of the proposed sampling strategy for gas distribution mapping and its use for gas source localization. T2 - IEEE/RSJ International conference on intelligent robots and systems (IROS '11) / Workshop on robotics for environmental monitoring (WREM2011) CY - San Francisco, CA, USA DA - 25.09.2011 KW - Autonomous UAV KW - Chemical sensing KW - Gas distribution modelling KW - Gas source localization KW - Gas sensors KW - Mobile sensing system KW - Quadrocopter KW - Sensor planning KW - Artificial potential field PY - 2011 SP - 34 EP - 38 AN - OPUS4-24537 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Balke, Christian A1 - Schendler, Thomas T1 - Möglichkeiten und Grenzen der Ereignisauswertung - aufgezeigt am Beispiel Human Factor T2 - VdS-Seminar - 12. Meinungs- und Erfahrungsaustausch für Sachverständige nach § 29a Abs. 1 BlmSchG, Immissionsschutz- und Störfallbeauftragte CY - Köln, Deutschland DA - 2011-07-13 KW - Ereignisauswertung KW - Menschlicher Faktor KW - Beinahe-Ereignisse KW - Störfälle KW - Unfälle PY - 2011 VL - 3652 SP - 1 EP - 9 AN - OPUS4-24482 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Habel, Wolfgang A1 - Kusche, Nadine A1 - Münzenberger, Sven A1 - Schukar, Vivien T1 - KALFOS - a validation facility for strain transfer characterization of surface-applied strain sensors N2 - Strain sensors embedded in or attached to structural components have to measure the real deformation of the structure over the whole period of use. The user must know how reliably installed sensors provide strain measurement results. For this purpose, test facilities or coupon tests are used. In order to characterize the strain transfer quality from the host structure into surface-applied strain sensors, a unique testing facility has been developed. This facility can be used both for fiber optic and resistance strain sensors. Originally developed for fiber Bragg grating based sensors, the KALFOS facility (=calibration of fiber optic sensors) uses Digital Image Correlation (DIC) and Electronic Speckle Pattern Interferometer (ESPI) as unbiased referencing methods. It is possible to determine experimentally the strain transfer mechanism under combined thermal and mechanical loading conditions. This experimental characterization method will reveal weaknesses in commonly used strain sensors, and the investigation of the material systems used for fiber optic and other strain sensors (particularly the coating/substrate - adhesive combination). The KALFOS facility allows matching of specific measurement requirements with environmental conditions. T2 - SAE 2011 AeroTech Congress & Exhibition CY - Toulouse, France DA - 18.10.2011 KW - Fiber optic sensors KW - Structural health monitoring KW - Validation KW - Strain sensor KW - Surface application PY - 2011 DO - https://doi.org/10.4271/2011-01-2606 IS - Paper 2011-01-2606 SP - 1 EP - 7 AN - OPUS4-24643 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmigalla, S. A1 - Heyn, Andreas A1 - Wesling, V. A1 - Reiter, R. A1 - Echtermeyer, P. T1 - Investigation of the pitting corrosion behaviour of nickel based alloy claddings by evaluation of electrochemical noise measurements N2 - Claddings of different nickel based alloys were generated on a mild Steel (S235JR) and a stainless steel type 304 by Cold Metal Transfer (CMT). This welding procedure possesses a low degree of mixing between the Substrate and cladding material. Thus it improves the corrosion behaviour of the claddings. The aim of our investigations was to examine the effect of the welding parameters: energy per unit length, shielding gas and finishing surface treatment on the pitting corrosion behaviour of the claddings. However, under Standard test conditions nickel based alloys are often resistant to pitting corrosion. Moreover these test methods are inaccurate and require a large period of time resulting from the iterative progress to determine the critical pitting temperature (CPT). A potentiostatic test method was modified using a high concentrated CaCI2-solution and a conventional three electrode measuring cell. The pitting corrosion behaviour is calculated from current noise charges. During the test the course of corrosion is detected online by the evaluation of electrochemical noise Signals while a continuous increase of temperature by a defined heating rate is realised. Thus a critical pitting temperature can be estimated by only one attempt. Furthermore the deviation of the measured CPT is very low compared to Standard tests using gravimetrical and microscopic evaluation. That enables to figure out the influence of the welding parameters in an exact way. T2 - EUROCORR 2011 - Developing solutions for the global challenge CY - Stockholm, Sweden DA - 04.09.2011 KW - Nickelbasislegierung KW - Plattieren KW - Schweißverfahren KW - Cold metal transfer KW - Korrosionsprüfung KW - Elektrochemie KW - Elektrochemisches Rauschen PY - 2011 SP - 1 EP - 9 AN - OPUS4-24565 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neser, A. A1 - Schreiber, D. A1 - Magallanes, J. A1 - Martinez, R. A1 - Zencker, Uwe A1 - Weber, Mike T1 - A material testing program to characterize the concrete behavior under static and dynamic loads N2 - In this paper a comprehensive material testing program is described to characterize a German final repository concrete material (BERB1) subjected to static and dynamic loads. The BERB1 material was developed und specified by the German Bundesanstalt für Materialforschung und -prüfung (BAM) for targets used for drop tests according to the KONRAD requirements. The testing consists of three concurrent laboratory experimental programs performed in the USA. An extensive preliminary testing program in Germany was performed to assure the required concrete specifications during fabrication and curing. The first set of data is the static basic material test program consisting of structural tests to quantify macroscopic concrete properties under quasi-static loads. Cubic and cylindrical specimens are investigated under this effort. The second set of test data is from the static complete material test program, where cylindrical concrete specimens are subjected to a variety of quasi-static axial and radial stress and strain paths using a high-pressure hydraulic tri-axial chamber. The material is characterized for confining pressures up to 400 MPa. The third set of data is from the dynamic complete material test program, which uses a modified Split-Hopkinson Pressure Bar to induce dynamic compression and tension waves into cylindrical concrete specimens that generate strain-rates up to 400 s-1. The ensemble of data generated in these experiments provides a complete set of data that effectively describes the behavior of this concrete and can be used to develop a constitutive calculation model. In addition, the results of the tests show a significant effect of moisture on the strength and rheology of this concrete for quasi-static pressures greater than 50 MPa. Numerical drop test simulations with the developed constitutive model in the Lagrangian finite element code, LS-DYNA, show good agreement with the experimental results from a BAM research project. T2 - PATRAM 2010 - 16th International symposium on the packaging and transport of radioactive materials CY - London, UK DA - 2010-10-03 KW - Testing program KW - Concrete behavior KW - Static loads KW - Dynamic loads KW - KONRAD acceptance criteria KW - Ductile cast iron cask PY - 2010 SP - 1 EP - 8 (Session T40 / Paper 123) AN - OPUS4-23845 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilke, Olaf A1 - Wiegner, Katharina A1 - Scheffer, Harald A1 - Brödner, Doris T1 - VOC-Emissions from Plywood boards N2 - Wood and wood products are often used as construction material for buildings and even more for furniture and indoor decoration. Therefore Chemical emissions from wood have an influence on the indoor air quality. A research project financed by the Federal Environmental Agency focused on VOC emissions from oriented Strand boards (OSB) and also from plywood made from pine and spruce (Wilke et al., 2011a). This paper shows results of the plywood testing because only little information is available about plywood emission behaviour and its impact on indoor air quality. T2 - Indoor Air 2011, 12th International conference on indoor air quality and climate CY - Austin, TX, USA DA - 05.06.2011 KW - VOC-Emission KW - Plywood KW - Terpenes KW - Aldehydes KW - Indoor air quality PY - 2011 IS - Paper 768 SP - 1 EP - 2 AN - OPUS4-23885 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klinger, Christian A1 - Bettge, Dirk A1 - Häcker, Ralf A1 - Heckel, Thomas A1 - Gohlke, Dirk ED - Pohl, M. T1 - Schadensanalyse zum Radsatzwellenbruch ICE3 T2 - DGM-Tagung Werkstoffprüfung 2010 CY - Neu-Ulm, Deutschland DA - 2010-12-02 KW - Radsatzwellenbruch KW - Nichtmetallische Einschüsse KW - Reinheitsgrad KW - Ultraschall-Hohlwellenprüfung PY - 2010 SP - 235 EP - 239 AN - OPUS4-23855 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mix, Renate A1 - Friedrich, Jörg Florian T1 - Improvement of adhesivity of polypropylene by its surface modification using the aerosol dielectric barrier discharge N2 - Plasma processes are used in many fields of Science and technology. While a plasma oxygen treatment produces a broad variety of different oxygen-containing functional groups, tailored - surface functionalisation demands preset functional groups in known concentration. Due to the fact that most of plasma experiments need expensive vacuum equipment increased efforts are to observe to apply atmospheric pressure plasma processes. Thus, Dielectric Barrier Discharge (DBD) and corona treatment of polymer foils have a long tradilion in industry to modify them for printing, laminating, adhesion promotion, etc. Thercibre, increasing interest is observed to make these atmospheric pressure processes more effeclive. Newly developed methods like plasma-printing were used for surfaces in biological and medical applications or for printed circuits. T2 - ADHESION `11 - 11th Triennial conference on the science and technology of adhesion and adhesives CY - York, UK DA - 07.09.2011 PY - 2011 SP - 253 EP - 256 AN - OPUS4-24337 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kuschke, Christian A1 - Ballheimer, Viktor A1 - Wille, Frank A1 - Komann, Steffen T1 - Mechanical assessment criteria of spent fuel assemblies basket design N2 - Packages for the transport of radioactive material are generally equipped with specific structures (basket) to support the radioactive content in defined position. The safety function of the basket depends on the kind of transported inventory. In case of transport cask for spent fuel, the basket design has to ensure the subcriticality of the fissile material in all conditions of transport in particular. Therefore the evaluation of structural integrity and neutron absorption capability of the basket is an important part of complete safety analysis. Sufficient heat transfer to maintain fuel assembly and cask temperature within allowable limits has to be verified as well. Corrosion resistance is an additional requirement on basket materials owing to contact with water during loading and unloading operations. Computational and experimental methods or their combination along with additional material and component tests can be used to analyse the mechanical and thermal basket behaviour under transport conditions defined in IAEA regulations. By deciding between the analysis methods, the design features (including material selection concept) as well as specific safety function should be accounted. In approval procedures of transport packages for radioactive materials, the competent authority mechanical and thermal safety assessment is carried out in Germany by BAM. Some questions of safety evaluation of basket designs are discussed in this paper based on the BAM experience within approval procedures. The paper focuses primarily on the mechanical behaviour of baskets with regard to the assumptions that have to be used in the criticality safety demonstration. The state of the art methodologies for computational basket stress and deformation analysis as well as for interpretation of drop tests results are presented. T2 - PATRAM 2010 - 16th International symposium on the packaging and transport of radioactive materials CY - London, UK DA - 2010-10-03 KW - Transport conditions KW - Spent fuel assemblies KW - Basket design PY - 2010 SP - 1 EP - 7 (Thursday T36/92) AN - OPUS4-24345 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Niebergall, Ute T1 - Comparison of the material parameters of polyethylene grades with the test performance behaviour of packagings for the transport of dangerous goods in dependence on the pre-storage time with 55% nitric acid N2 - The material parameters melt flow rate MFR, density D, notched impact strength N.I.S. at -30 °C, stress crack resistance FNCT and resistance to oxidative degradation Ox (determined by the increase of MFR) have been selected for a comparison of polyethylene grades for one design type in the “European Standard EN 15507 - Transport packaging for dangerous goods - Comparative material testing of polyethylene grades”. The parameters have a systematic relationship with design type tests. The notched impact strength at -30 °C and the resistance to oxidative degradation of polyethylene grades determined with test specimens of compression moulded sheets are directly comparable with drop tests at -18 °C of design types produced of these grades after pre-storage with 55 % nitric acid for 21 days at 40 °C. The impact of the pre-storage time of jerricans with 55 % nitric acid at 40 °C and 23 °C on the marginal drop heights in drop tests at -18 °C, on the MFR and on the tensile properties tensile strength, breaking elongation and the elastic modulus were investigated. Packaging design types (jerricans) made of three polyethylene grades from different producers were pre-stored with 55 % nitric acid for 21,42 and 84 days at 40 °C as well as for six months at 23 °C. The MFR and tensile properties of test specimens taken from the design type side walls as well as the marginal drop heights of the jerricans in drop tests at -18 °C were determined. The values of the notched impact strength at -30 °C of polyethylene grades are not comparable with the marginal drop heights determined in drop tests at -18 °C. The oxidative damaging impact of nitric acid has a greater effect on the grade with lower resistance to oxidative degradation by reducing more significantly the marginal drop heights with increasing pre-storage time. Pre-damage with 55 % nitric acid for 21 days at 40 °C, as recommended in ISO 16101 and EN 15507 caused an increase in the marginal drop heights of most design types in drop tests when compared with design types without pre-damage. The test results demonstrated clearly that pre-storage of the jerricans for six months at 23 °C caused a higher increase in the MFR and lower marginal drop heights of the jerricans in drop tests at -18 °C compared with pre-storage of the jerricans for 21 days at40 °C. The mechanical properties change as a result of diffusion of nitric acid into the polyethylene grades and the reaction of the nitric acid with the polymers. The percentage decrease and increase in the tensile strength, breaking elongation and elasticity modulus of test specimens taken from the design type side walls after different pre-storage times were only partly comparable with the marginal drop heights in drop tests at -18 °C. T2 - EUROCORR 2011 - Developing solutions for the global challenge CY - Stockholm, Sweden DA - 04.09.2011. KW - Gefahrgutverpackungen KW - Polyethylenformstoffe KW - Baumusterprüfungen KW - Nachweis der chemischen Verträglichkeit KW - Oxidativer Abbau PY - 2011 SP - 1 EP - 12 AN - OPUS4-24346 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Plarre, Rüdiger ED - Robinson, W.H. ED - De Carvalho Campos, A.E. T1 - Wood protection by interfering with insect behavior: adequacy of laboratory test designs N2 - Standardized test methods by which the efficacies of conventional Chemical wood preservatives against insects determine their toxic effects against larvae of wood boring beetles or their feeding prevention by termites. Although alternative control strategies to the application of biocides exist, such as interference with insect behavior during mating or when searching for suitable breeding and feeding sites, their acceptance, too, depends on efficacy evaluation. This is why new test set ups are needed which take behavior modifying control strategies into account. This paper will demonstrate how new laboratory tests must be designed or how existing Standards can be altered to reliably interpret insect behavior including its successful manipulation in a standardized format. T2 - 7th ICUP - International conference on urban pests CY - Ouro Preto, Brazil DA - 07.08.2011 KW - Standardized tests KW - IPM KW - Efficacy evaluation KW - Wood borers KW - Termites PY - 2011 SP - 23 EP - 26 PB - Instituto Biológico CY - Sao Paulo, Brazil AN - OPUS4-24295 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Lexow, Jürgen A1 - Fellenberg, R. A1 - Krauß, O. T1 - Zwischenauditierung des BMBF-Förderprogramms 'Werkstoffinnovationen für Industrie und Gesellschaft . WING' N2 - Das Bundesministeriums für Bildung und Forschung (BMBF) fördert die Werkstofftechnologien und in Teilen die Nanotechnologie seit dem Jahr 2004 im Rahmen des Förderprogramms „Werkstoffinnovationen für Industrie und Gesellschaft - WING“. Die vorliegende Studie wurde im Auftrag des BMBF von der VDI Technologiezentrum GmbH und der BAM Bundesanstalt für Materialforschung und -prüfung erarbeitet. Sie stellt die Ergebnisse der Zwischenauditierung des WING-Programms dar, die im Kontext einer begleitenden Programmentwicklung nach fünf Jahren Laufzeit vorgesehen ist. Mit dem empirischen Teil des Zwischenaudits wurde im Jahr 2010 begonnen, so dass alle Projekte, deren Laufzeit vor dem 31.12.2009 begann, berücksichtigt werden konnten. Zweck des Zwischenaudits war es, die Wirkung der bisherigen Fördermaßnahmen seit Beginn des Programms anhand quantitativer und qualitativer Indikatoren zu erfassen und zu bewerten. Diese Wirkungsanalyse soll auch als Basis dienen, um in der weiteren Programmlaufzeit programmatische Ausrichtungen und prozessuale Abläufe bei Bedarf zu verbessern. KW - Innovation KW - Evaluation KW - Auditierung KW - WING KW - BMBF KW - Programm KW - Werkstoff PY - 2011 SP - 1 EP - 31 AN - OPUS4-24296 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Recknagel, Christoph T1 - Erfahrungen mit flexiblen Fahrbahnübergängen und Stand der Technik in Deutschland N2 - Mehr als 25 Jahre nach dem ersten Einbau eines sogenannten Fahrbahnüberganges aus Asphalt und nach nunmehr 13-jähriger Erfahrungen mit den gütesichernden Maßnahmen des technischen Regelwerks in Deutschland kann eine insgesamt positive Bilanz gezogen werden. Diese Ausführungsvariante der Bauart flexibler Fahrbahnübergang hat mittlerweile einen akzeptierten Platz auf dem Gebiet der Brückenausstattung für Bauwerke mit einer freien Dehnlänge bis zu 30 m eingenommen. Die generelle Bewährung ist aktuelle Motivation, durch stoffliche und konstruktive Weiterentwicklungen die bauartbedingten Vorteile in einen größeren Anwendungsbereich zu überführen. Die baurechtliche Grundlage dafür bilden die neuen europäisch harmonisierten Zulassungsregelungen. Erste Erfahrungen aus der versuchstechnischen Bewertung neuartiger Ausführungsvarianten werden vorgestellt. T2 - ASTRA-EMPA-Tagung - Flexible Fahrbahnübergänge - Erfahrungen und Stand der Technik CY - Dübendorf, Switzerland DA - 18.10.2011 PY - 2011 SP - 1 EP - 7 AN - OPUS4-24809 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burkert, Andreas A1 - Beck, M. T1 - Detektion von Bewehrungsstahlkorrosion nach dem DGZfP - Merkblatt B 3 zur elektrochemischen Potentialfeldmessung N2 - Im ersten Teil dieses Beitrags [1] sind die Grundlagen der Passivität und der Depassivierung sowie des Korrosionsfortschritts von Stahl in Beton eingehend dargestellt worden. Die entstehenden Korrosionsprodukte werden zunächst vom Porengefüge des Betons aufgenommen, ohne dass es zu äußerlich sichtbaren Veränderungen an der Betonoberfläche kommt. Infolge der sich einstellenden Sättigung des Porenraumes mit Korrosionsprodukten und des daraus resultierenden Spannungsaufbaus im Beton können Folgeschäden, wie Risse und Abplatzungen am Bauwerk entstehen, die notwendige Sanierungsmaßnahmen bedingen. KW - Stahlbeton KW - Passivität KW - Chlorinduzierte Korrosion KW - Potentialmessung KW - Einflüsse KW - Fehlerquellen PY - 2011 VL - 3 SP - 5 EP - 8 PB - VBD-Geschäftsstelle CY - Hannover AN - OPUS4-24830 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gili, F. A1 - Igartua, A. A1 - Luther, R. A1 - Woydt, Mathias T1 - The impact of biofuels on engine oil's performance T2 - 17th International colloquium tribology CY - Esslingen, Germany DA - 2010-01-19 KW - Lubricants KW - Engine oil KW - Additives KW - Bio-fuel KW - Ester KW - Polyglycol KW - Thin film coatings KW - Slip-rolling KW - DLC KW - Dilution KW - FAME KW - Jatropha KW - Rape seed KW - Stem valve KW - Piston ring PY - 2010 SP - 17_Woydt_Biofuels_Plenary, 1 EP - 13 AN - OPUS4-24832 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Häcker, Ralf A1 - Knothe, Esther A1 - Memhard, D. A1 - Andrieux, F. T1 - Containmentsicherheit - Entwicklung und Verifikation von Materialmodellen und numerischen Methoden zur Vorhersage der Containment Sicherheit beim Bersten von Laufrädern in Abgasturboladern (ATL) KW - Containmentsicherheit KW - Hochgeschwindigkeitsprüfung KW - Beschussversuche PY - 2011 IS - 928 - 2011 SP - 1 EP - 214 CY - Frankfurt/M. ET - Abschlussbericht zu Forschungsvorhaben 936 AN - OPUS4-25010 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Schoßig, Jörg A1 - Schmidt, Martin A1 - Krause, U. T1 - Validierung von formalkinetischen Größen aus der adiabatischen Warmlagerung KW - Selbstentzündung KW - Adiabate Warmlagerung KW - Reaktionskinetik PY - 2011 SP - 1 EP - 57 ET - Abschlussbericht Forschungsvorhaben AN - OPUS4-25012 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Fischer, C. A1 - Schmidt, Martin A1 - Meyer, U. A1 - Barth, Uli A1 - Drebenstedt, C. A1 - Wuttke, M. W. T1 - Innovative Technologien für die Erkundung, Löschung und Beobachtung von Kohlebränden - Phase B - N2 - Aufbauend auf den Erkenntnissen der Phase A, die sich auf das grundlegende Verständnis von Kohlebränden, sowie der Voraussetzung und des prinzipiellen Ablaufs der physikalischchemischen Brandprozesse konzentriert haben, erfolgte in Phase B eine Fokussierung auf Methoden zur Vermeidung von Kohlebränden, sowie der Löschung und Überwachung von Kohlebrandzonen, um einen Beitrag zur Verminderung von C02-Emissionen und zum Erhalt der nutzbaren Energieressourcen leisten zu können. Diese Arbeiten erfolgten insbesondere mit Bezug zu den „Clean Development Mechanisms“ (CDM), die im Rahmen des Kyoto-Protokolls entwickelt worden sind. Eine Zertifizierung von Löschaktivitäten im Rahmen des Kyoto-Protokolls setzt dabei eine nachvollziehbare Ermittlung der kohlebrandbezogenen C02-Emissionen und eine belastbare Abschätzung der durch die Löschung verringerten Emissionsmengen voraus. Wesentliche Arbeiten konzentrierten sich auf die Entwicklung von Verfahren, die eine solche Abschätzung gewährleisten können. Dazu wurden unterschiedliche Ansätze entwickelt und anhand der erhobenen Felddaten überprüft. Die untersuchten Ansätze konzentrierten sich dabei auf Verfahren, die eine Ermittlung des vorhandenen Kohlevolumens, die Erfassung der emittierten Gase und die durch die Kohlebrände verursachten Temperaturanomalien an der Tagesoberfläche ermöglichen. Die direkten Arbeiten zum Thema CDM wurden dabei in einem Arbeitspaket unter Federführung der BGR gebündelt. Die deutsche Initiative zur Erforschung der Kohlenbrände in der V.R. China leistete zweifelsfrei signifikante Beiträge zu den oben genannten Zielen. Durch die inventiven Ansätze im Bereich der Brandbewältigung konnte darüber hinaus auch in Teilen die ökonomischen Chancen für ein Engagement deutscher Unternehmen aufgezeigt werden. KW - Kohlebrände KW - Brandbekämpfung KW - Branderkundung PY - 2011 DO - https://doi.org/10.2314/GBV:664529690 SP - 1 EP - 39 AN - OPUS4-25013 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Priebe, Nsesheye Susan A1 - Schmidt, W. T1 - Spearhead network for innovative, clean and safe cement and concrete technologies (SPIN) project in east, central and southern Africa T2 - 2nd Environmental cement Africa conference CY - Nairobi, Kenya DA - 2011-05-11 KW - SPIN KW - Africa KW - Cement KW - Concrete KW - Construction PY - 2011 N1 - Geburtsname von Priebe, Nsesheye Susan: Msinjili, N. S. - Birth name of Priebe, Nsesheye Susan: Msinjili, N. S. SP - 1 EP - 3(?) AN - OPUS4-25156 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Komann, Steffen A1 - Kiyak, Yusuf A1 - Wille, Frank A1 - Zerbst, Uwe A1 - Weber, Mike A1 - Klingbeil, Dietmar T1 - Assessment of ductile cast iron fracture mechanics analysis within licensing of German transport packages N2 - In the approval procedure of transport packages for radioactive materials, the mechanical and thermal safety assessment is carried out in Germany by competent authority BAM. In recent years BAM was involved in several licensing procedures of new spent fuel and HLW package designs, where the cask body was made of Ductile Cast Iron (DCI). According to IAEA regulations package designs have to fulfill requirements for specific conditions of transport. Type B(U) packages must withstand the defined accident conditions of transport. The temperature range from -40°C up to the operational temperature has to be considered. For the cask material DCI, it is necessary to determine the brittle fracture behavior. The German guideline BAM-GGR 007 defines requirements for the fracture mechanics of DCI. Due to complex structure of the cask body and the dynamic loading a fracture mechanical assessment in an analytical kind is not always possible. Experience of recent design approval procedures show that the application of numerical calculations are applicable to determine the fracture mechanical load in the cask body. At the first step a numerical analysis has to be done to identify the loading state at the whole cask body. Secondly an analysis of a detail of the cask body is made considering the displacement boundary conditions of the global model. An artificial flaw is considered in this detailed model to calculate the fracture mechanical loading state. The finite element mesh was strongly refined in the area of flaw. The size of the artificial flaw is characterized by the ultrasonic inspection used for the quality assurance of the package. The applicant developed additional analysis tools for calculation of stress intensity factor and/or J-Integral. The assessment approach by BAM led to the decision to develop own tools to the possibility for independent check of the results. The paper describes the authority assessment approach for the DCI fracture mechanics analysis. The validation procedure incl. the development of own tools is explained. BAM developed a post-processor called JINFEM to determine the fracture mechanical loads. The regulatory 1 m puncture bar drop test is used to give an example of the assessment procedure. T2 - 52nd INMM Annual meeting CY - Palm Desert, CA, USA DA - 17.07.2011 KW - Mechanische Bewertung KW - Radioaktives Material KW - Numerische Analyse KW - Bruchmechanik PY - 2011 SP - 1 EP - 10 AN - OPUS4-25022 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hertwig, Andreas A1 - De Castro, F.A. T1 - Newsletter - Metrology for the manufacturing of thin films KW - Metrology KW - Thin films KW - Optoelectronics KW - Photovoltaics KW - Coatings technology KW - Traceability PY - 2012 UR - http://projects.npl.co.uk/optoelectronic_films/documents/EMRP%20ThinFilms_Newsletter%20Feb%202012.pdf IS - February SP - 1 EP - 4 AN - OPUS4-25505 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Schulz, Sabrina A1 - Linke, Barbara A1 - Kranzmann, Axel T1 - Supercritical CO2-corrosion in pipe steels during carbon capture and storage CCS N2 - The CCS technique involves the compression of emission gasses in deep geological layers. To guarantee the safety of the site, C02-corrosion of the injection pipe steels has to be given special attention when engineering CCSsites. To get to know the corrosion behaviour samples of the heat treated Steel 1.72252CrMo4, used for casing, and the stainless injection-pipe Steel 1.4034 X46Cr 13 were kept at T=60 °C and ambient pressure as well as p=100 bar for 700 h - 8000 h in a C02-saturated synthetic aquifer environment similar to possible geological on-shore CCS-sites in the northern German Basin. The isothermal corrosion behaviour obtained by mass gain of the steels in the gas phase, the liquid phase and the intermediate phase gives surface corrosion rates around 0.1 to 0.8 mm/year at ambient pressure and much lower about 0.02 to 0.2 mm/year at 100 bar where the C02 is in its supercritical state. Severe pit corrosion with pit heights around 4.5 mm are only located on the 42CrMo4 Steel. Main phase of the continuous complicated multi-layered carbonate/oxide structure is siderite FeCO} in both types of Steel. T2 - 4th International conference on sustainable energy and environment (SEE 2011) - A paradigm shift to low carbon society CY - Bangkok, Thailand DA - 23.11.2011 KW - Steel KW - Pipeline KW - Corrosion KW - Carbonate layer KW - CCS KW - Supercritical CO2- KW - CO2-storage PY - 2011 SP - 1 EP - 6 AN - OPUS4-25534 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Linke, Barbara A1 - Schulz, Sabrina A1 - Kranzmann, Axel T1 - Supercritical CO2-corrosion in pipe steels during carbon capture and storage CCS N2 - The CCS technique involves the compression of emission gasses in deep geological layers. To guarantee the safety of the site, CC>2-corrosion of the injection pipe steels has to be given special attention when engineering CCS-sites. To get to know the corrosion behaviour samples of the heat treated Steel 1.72252CrMo4, used for casing, and the stainless injection-pipe Steel 1.4034 X46Crl3 were kept at T=60 °C and ambient pressure as well as p=100 bar for 700 h - 8000 h in a CC>2-saturated synthetic aquifer environment similar to possible geological onshore CCS-sites in the northern German Basin. The isothermal corrosion behaviour obtained by mass gain of the steels in the gas phase, the liquid phase and the intermediate phase gives surface corrosion rates around 0.1 to 0.8 mm/year at ambient pressure and much lower about 0.02 to 0.2 mm/year at 100 bar where the CO2 is in its supercritical state. Severe pit corrosion with pit heights around 4.5 mm are only located on the 42CrMo4 Steel. Main phase of the continuous complicated multi-layered carbonate/oxide structure is siderite FeCCh in both types of Steel. T2 - 3rd International congress on green process engineering (GPE 2011) CY - Kuala-Lumpur, Malaysia DA - 06.12.2011 KW - Steel KW - Pipeline KW - Corrosion KW - Carbonate layer KW - CCS KW - Supercritical CO2- KW - CO2-storage PY - 2011 SP - 1 EP - 6 AN - OPUS4-25535 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Wojtas, P. A1 - Spengler, I. A1 - Kranzmann, Axel T1 - Effect of heat treatment of injection pipe steels on the formation of local corrosion in CCS-environment N2 - When engineering a Carbon Capture and Storage site (CCS) local corrosion (pitting) of the injection pipe steel may become an issue when emission gasses from oxyfuel power plants are compressed into deep geological layers. This highly corrosive environment arises when the flue gasses, mainly composed of CO2 , are injected into saline aquifer water. Immediately carbonic acid is formed causing corrosive attack of the injection steels. The influence of heat treatment on the local corrosion resistance was demonstrated in laboratory experiments at 60 °C and ambient pressure for three steels X46Cr13 (1.4034), X20Cr13 (1.4021) and X5CrNiCuNb16-4 (1.4543) under a similar liquid corrosive environment as found at a geological onshore CCS-site in the Northern German Bassin. T2 - 2nd Oxyfuel combustion conference CY - Yeppoon, Queensland, Australia DA - 12.09.2011 KW - Steel KW - Pipe KW - Corrosion KW - Heat treatment KW - CO2-injection KW - CO2-storage CCS KW - Carbonate KW - Ambient pressure KW - CCS KW - Steels PY - 2011 SP - 1 EP - 3 AN - OPUS4-25536 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Raedel, Martina A1 - Torge, Manfred A1 - Bücker, Michael T1 - Adhesives for stained glass windows - development of a new system for wide cracks N2 - To improve the adhesives used for restoring stained glass windows, various adhesives were tested and modified. Stained glass windows often show gaps that are too wide to be glued with conventional adhesives, and complementing the gap with spare glass is very time-consuming. To solve this problem, a filler with improved adhesive strength was developed to bridge wider gaps and cracks. The new filler combines glass adhesives with specially treated glass powder. Three different glass adhesives were selected and mixed with the specially treated glass powder. The adhesive – glass powder mixture developed was then subjected to accelerated aging and analysed with Fourier transform infrared analysis, scanning electron microscopy, colourimetry, and bending and tensile tests. The results were excellent and the mixture was subsequently used to restore glass windows from four 19th-century churches and chapels. The restoration process was described in conjunction with the advantages of using this approach. This new adhesive – glass powder mixture provides an adhesive process that can be adapted to the special needs of any object being restored and thus provides a ready answer to the specific damage of each object. T2 - CCI Symposium 2011 - Adhesives and consolidants for conservation: research and applications CY - Ottawa, Canada DA - 17.10.2011 KW - Adhesives KW - Stained glass windows KW - Conservation KW - Restoration KW - New adhesive for wide cracks PY - 2011 UR - http://www.cci-icc.gc.ca/symposium/2011/Paper%2034%20-%20Raedel%20et%20al.%20-%20English.pdf SP - 1 EP - 21 AN - OPUS4-25549 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Noack, Volker A1 - Nieslony, Gregor A1 - Völzke, Holger A1 - Hörning, Tony A1 - Kovacs, Oliver A1 - Hagenow, Peter T1 - Aktueller Stand bei den Behälter-Bauartprüfungen für das Endlager Konrad N2 - In Deutschland werden zwei Arten von radioaktiven Abfällen unterschieden: Wärme entwickelnde Abfälle und Abfälle mit vernachlässigbarer Wärmeentwicklung. Im Endlager Konrad werden ausschließlich radioaktive Abfälle mit vernachlässigbarer Wärmeentwicklung endgelagert (im internationalen Sprachgebrauch: schwach- und mittelradioaktive Abfälle). Solche Abfälle stammen zum Beispiel aus dem laufenden Betrieb, der Stilllegung und dem Rückbau von Kernkraftwerken, aus der Forschung, der Medizin oder von der Bundeswehr und beinhalten unter anderem kontaminierte Baustoffe, Schrott, Werkzeuge, Schutzkleidung, Schlämme und Suspensionen. Vor dem Endlagern dieser Abfälle werden sie konditioniert, d. h. die festen Abfälle werden teilweise zerkleinert, verpresst oder zementiert, flüssige eingedampft oder zementiert und häufig anschließend in Fässer verpackt. Im nächsten Schritt werden die konditionierten Abfälle in Abfallbehälter verpackt. Geeignete Behältertypen sind (gemäß IM, 121) kubische Container oder Rundbehälter mit definierten Abmaßen aus Stahlblech, Beton oder Gusseisen. Diese Abfallbehälter sind für die Endlagerung, für eine vorausgehende längerfristige Zwischenlagerung sowie ggf. für den Transport über öffentliche Verkehrswege zu qualifizieren. T2 - Jahrestagung Kerntechnik 2011 CY - Berlin, Germany DA - 17.05.2011 KW - Kerntechnik KW - Endlagerung KW - Gutachten KW - Behälter KW - Bauartprüfung PY - 2011 IS - Session TS-19 / Paper 91 SP - 1 EP - 5 AN - OPUS4-25550 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Weltschev, Margit T1 - UNS S44400 - A low cost and corrosion-resistant alternative to the austenite containing nickel for tank applications N2 - In Germany the “BAM-List - Requirements for Tanks for the Transport of Dangerous Goods” is the basis for substance-related prototype approvals for tank Containers undertaken by the BAM1 - Federal Institute for Materials Research and Testing. Compatibility evaluations of selected metallic materials as well as of polymeric gasket and lining materials under the influence of approximately 7200 dangerous goods have been published in the BAM-List since 1989. The ferritic Steel UNS S44400 (X2CrMoTil8-10, 1.4521) was originally developed as alternative for the austenitic grade AISI316L (X2CrNiMo 17-12-2, 1.4404). Due to its characteristic profile this Steel was qualified for applications requiring high strength values at concomitant adequate corrosion resistance. Because of the lack of Nickel this Steel is a cost-efficient alternative to the Ni-containing austenites. No corrosion test results of UNS S44400 under the influence of dangerous goods were published in the BAM-List so far. Only data on the behavior of AISI 316L are listed. Therefore test specimens of this Steel were exposed to selected corrosive substances in order to compare both steels. Due to the reduced alloy content a reduced corrosion resistance of the Steel UNS S44400 in acidic substances, such as formic acid, acetic acid and sulfuric acid, in comparison to the austenitic CrNiMosteels was expected but not observed. Tests in an alkaline medium showed sufficient resistance. T2 - NACE International Corrosion Conference 2012 CY - Salt Lake City, USA DA - 01.03.2012 KW - Steel KW - Dangerous goods KW - Transport tanks KW - Duplex steel KW - Corrosion KW - 1.4362 KW - X2CrNiN23-4 PY - 2012 SP - 1-7 (C2012-0001290) AN - OPUS4-25979 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Simone A1 - Deubel, Jan A1 - Raspe, Tina A1 - Fettig, Ina A1 - Piechotta, Christian T1 - Chemische Brandspurenanalytik T2 - Vfdb 2012 -Jahresfachtagung CY - Köln, Deutschland DA - 2012-05-21 KW - Brandbeschleuniger KW - Brandgase KW - Brand KW - Partikel KW - Analytik PY - 2012 SP - 517 EP - 539 PB - VdS Schadenverhütung CY - Köln AN - OPUS4-25933 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schilder, Constanze A1 - Hofmann, Detlef A1 - Kohlhoff, Harald A1 - Habel, Wolfgang ED - Ramos, G. A. T1 - Structure-integrated fiber-optic strain wave sensor for concrete pile testing and monitoring N2 - Reinforced concrete piles are used in case of structures that are constructed on soft ground to transfer the loads into deeper strata with sufficient bearing capacity. In order to determine the pile’s behavior and possible damage, static and dynamic pile tests are carried out. Dynamic measurements taken from the pile head can show the bearing behavior and structural integrity by using the theory of wave propagation. In order to receive more precise information about the pile features, now, a string of sensors is embedded at different levels of the pile. A fiber optic strain wave sensor, based on the extrinsic Fabry-Perot interferometer (EFPI), has already been developed and tested in full-scale field tests by Schallert (2010). It was possible to detect the introduced deformation caused by the static load and the dilatational wave during dynamic loading. Although the full-scale tests were successful, the engineering design of the sensor body left room - from the economical point of view - to be optimized. After laboratory tests with the optimized sensor, a cast-in-situ bored pile has been built at the BAM Test Site Technical Safety in Horstwalde, South of Berlin. Additionally to the EFPI sensors, fiber Bragg grating (FBG) sensors, temperature sensors and resistance strain gauge (RSG) sensors are embedded in order to compare the signals with each other. In this paper, the modified sensor and the Setup of the cast-in-situ bored pile along with results of dynamic tests are shown. T2 - SHMII-5 - 5th International conference on structural health monitoring of intelligent infrastructure CY - Cancún, Mexico DA - 11.12.2011 KW - Fibre optic sensors KW - Monitoring KW - Concrete pile KW - Foundation KW - Integrity testing PY - 2011 IS - Topic_04.Cat_4.2-abs002 SP - 1 EP - 8 PB - National Autonomous University of Mexico CY - Mexico City AN - OPUS4-25142 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Bürgisser, Philip T1 - Der Einfluss von puzzolanischen Zusatzstoffen vulkanischen Ursprungs auf die Alkali-Kieselsäure-Reaktion (AKR) im Beton PY - 2011 SP - 1 EP - 135 CY - Berlin AN - OPUS4-25287 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krebber, Katerina ED - Ramos, G. A. T1 - Structural health monitoring by smart technical textiles based on fiber optic sensors N2 - Technical textiles with embedded distributed fiber optic sensors have been developed for the purposes of structural health monitoring in geotechnical and civil engineering. The distributed fiber optic sensors are based on Brillouin Scattering in silica optical fibers and OTDR in polymer optical fibers. Such “smart” technical textiles can be used for reinforcement of geotechnical and masonry structures and the embedded fiber optic sensors can provide information about the condition of the structures and detect the presence of any damages and destructions in real time. Thus, structural health monitoring of critical geotechnical and civil infrastructures can be realized. The paper highlights the results achieved in this innovative field in the framework of several German and European projects. T2 - SHMII-5 - 5th International conference on structural health monitoring of intelligent infrastructure CY - Cancún, Mexico DA - 11.12.2011 PY - 2011 IS - Keynote Lecture SP - 1 EP - 10 PB - National Autonomous University of Mexico CY - Mexico City AN - OPUS4-25261 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klinger, Christian A1 - Bettge, Dirk A1 - Häcker, Ralf A1 - Heckel, Thomas A1 - Gohlke, Dirk A1 - Klingbeil, Dietmar T1 - Schadensanalyse zum Radsatzwellenbruch ICE3 N2 - Am 9. Juli 2008 entgleiste ein Hochgeschwindigkeits-Triebzug der Baureihe 403, ICE3, bei der Ausfahrt aus dem Kölner Hauptbahnhof. Ursache dafür war der Schwingbruch einer Radsatzwelle. Im Auftrag der Staatsanwaltschaft Köln untersuchte die BAM die Schadensteile, insbesondere die gebrochene Treibradsatz-Hohlwelle. Zunächst wurden das Drehgestell, der Antriebsstrang, die Räder, die Bremsen und die gebrochene Radsatzwelle visuell untersucht und deren Zustand dokumentiert. Anschließend erfolgte die zerstörungsfreie Prüfung der beiden Bruchstücke der Hohlwelle mit teilmechanisierter Ultraschall-Handprüfung. Vor der Zerlegung der Radsatzwelle wurden ausgewählte Maße kontrolliert und die Oberfläche eingehend untersucht. Nach der Probenahme und Präparation wurden die relevanten spezifizierten Eigenschaften des Wellenwerkstoffs überprüft. Mittels Bruchflächenanalyse konnte die Startstelle des Schwingrisses lokalisiert, aufgrund der starken Sekundärschäden auf der Bruchfläche und an den Bruchkanten jedoch nicht direkt ausgewertet werden. Durch die Kombination von Mikro-Computertomographie und Ultraschall-Tauchtechnik wurden u. a. nahe der Schwingriss-Startstelle Inhomogenitäten erkannt, die durch metallographische Zielpräparation als nichtmetallische Einschlüsse identifiziert wurden. Die Größe dieser Einschlüsse ist gemäß gefordertem Reinheitsgrad unzulässig. Vergleichbare Einschlüsse in diesem hochbeanspruchten Bereich der Radsatzwelle haben vermutlich den Schwingriss initiiert. T2 - 43. Tagung des DVM-Arbeitskreises Bruchvorgänge - Bruchmechanische Werkstoff- und Bauteilbewertung: Beanspruchungsanalyse, Prüfmethoden und Anwendungen CY - Rostock, Germany DA - 22.02.2011 KW - Radsatzwellenbruch KW - Nichtmetallische Einschlüsse KW - Reinheitsgrad KW - Ultraschall-Hohlwellenprüfung KW - Railway axle KW - Fatigue crack KW - Root cause KW - Cologne accident PY - 2011 SP - 1 EP - 6 AN - OPUS4-25275 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völz, Uwe T1 - Visualisierung der Schallausbreitung in Festkörpern mit elektrodynamischen Sonden N2 - Die Prinzipien der Ultraschallausbreitung in festen Medien sind seit langem bekannt und können heute durch mathematische Modelle recht umfassend beschrieben und simuliert werden. In der Praxis zeigt sich aber, dass gerade bei komplexen Geometrien, sowie inhomogenen und anisotropen Materialien die Modelle immer noch an ihre Grenzen stoßen. Das ist insbesondere in der fehlenden Möglichkeit begründet, die akustischen Eigenschaften inhomogener Prüfgegenstände vollständig mathematisch zu beschreiben. Deshalb wird in letzter Zeit verstärkt nach Techniken gesucht, mit denen man die Schallausbreitung in solchen Materialien messen und anschaulich darstellen kann. Ziel dieser Entwicklung ist es, die Schallausbreitung in Festkörpern, insbesondere in solchen mit akustisch anisotropen Eigenschaften, besser zu verstehen und die Möglichkeit zu schaffen, die Simulationsrechnungen am realen Objekt zerstörungsfrei verifizieren zu können. In der Literatur werden verschiedene Methoden zur messtechnischen Visualisierung der Ultraschallausbreitung in Festkörpern beschrieben. Am bekanntesten sind optische Verfahren wie die Schlierentechnik, die schon seit langem genutzt wird, um den momentanen Schallfeldverlauf im Inneren von optisch transparenten Materialien sichtbar zu machen. Heute kommen verstärkt lasertechnische Methoden, wie z. B. das Laserinterferometer, zum Abtasten von nicht transparenten Materialoberflächen zum Einsatz. Da diese Verfahren mit einem hohen technischen Aufwand verbunden sind, werden häufig auch einfachere Methoden, wie z. B. das Abtasten mit punktförmigen piezoelektrischen Aufnehmern, verwendet. T2 - DAGA 2011 - 37. Jahrestagung für Akustik - Fortschritte der Akustik CY - Düsseldorf, Germany DA - 21.03.2011 KW - Ultraschall KW - Schallfeld KW - Elektrodynamische Sonde KW - Visualisierung PY - 2011 SN - 978-3-939296-02-7 SP - 347 EP - 348 PB - Deutsche Gesellschaft für Akustik CY - Berlin AN - OPUS4-25227 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Jacobs, R. A1 - Meneve, J. A1 - Dyson, G. A1 - Jennett, N. M. A1 - von Stebut, J. A1 - Feuchter, P. A1 - Cavalleri, A. A1 - Ronkainen, H. A1 - Beck, Uwe A1 - Reiners, Georg A1 - Ingelbrecht, C. D. T1 - SMT4-CT98-2238 - A certified reference material for the scratch test - REMAST - Final technical report PY - 2002 SP - 1 EP - 110 PB - Vito CY - Mol, Belgium AN - OPUS4-25601 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Tränkle, G. A1 - Fabich, F. A1 - Schiller, Wolfgang A1 - Reiners, Georg A1 - Hübert, Thomas A1 - Beck, Uwe T1 - Abschlussbericht zum Vorhaben Aufbau und Inbetriebnahme eines Zentrums für Mikrosystemtechnik (ZEMI) in Berlin-Adlershof PY - 2003 SP - 1 EP - 17 PB - Europäischer Fond für Regionale Entwicklung (EFRE) CY - Berlin AN - OPUS4-25603 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Jacobs, R. A1 - Meneve, J. A1 - Dyson, G. A1 - Jennett, N. A1 - von Stebut, J. A1 - Feuchter, P. A1 - Cavaleiro, A. A1 - Ronkainen, H. A1 - Beck, Uwe A1 - Reiners, Georg A1 - Ingelbrecht, C. T1 - SMT4-CT98-2238 - A certified reference material for the scratch test - REMAST - Synthesis report PY - 2002 SP - 1 EP - 9 PB - Vito CY - Mol, Belgium AN - OPUS4-25625 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Blind, K. A1 - Jungmittag, A. A1 - Mangelsdorf, Axel T1 - The economic benefits of standardization - An update of the study carried out by DIN in 2000 N2 - Economists have been searching for the sources of economic growth since the end of the 18th century. For Adam Smith the division of labour and the accumulation of capital were causes for the increasing wealth of nations. The Austrian-American economist Joseph Alois Schumpeter further established that innovations in products and processes are prerequisites for economic growth: »The fundamental drive that starts up the capitalist machine and keeps it running comes from the new consumer goods, the new production and transport methods, the new markets, the new forms of industrial organisation, which capitalist entrepreneurship creates.« Building on these fundamental ideas, during the 1950s American Robert M. Solow – later a Nobel prize winner – developed the first formal mathematical model of economic growth. Solow was able to use a simple model to Show that economic growth within the USA could be described by three determinants: an increase in capital (e.g. machinery and infrastructure), an increase in labour, and technical progress. Later other economists were able to further refine Solow‘s growth theory. While technical progress was accepted during the early years as a fact, it became ever easier to theoretically describe and quantify its causes. The central idea of these new models is that the state and businesses invest in research and development, thus continually stimulating economic growth through new products and production methods. KW - Standards KW - Economic growth KW - Value KW - Technical progress PY - 2011 SP - 1 EP - 20 CY - Berlin AN - OPUS4-25073 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sojref, Regine A1 - Güther, Wolfgang T1 - Solvent-based redispersion of fine (<200 nm) corundum powder pre-milled in water T2 - ECerS XII - 12th Conference of the European ceramic society CY - Stockholm, Sweden DA - 2011-06-19 KW - Powder processing KW - Redispersion KW - Tape casting KW - Corundum KW - Hydrophobization PY - 2011 SP - 1 EP - 4 AN - OPUS4-25379 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mishra, Kirti Bhushan A1 - Wehrstedt, Klaus-Dieter T1 - CFD simulation to predict the performance of a peroxy-fuel burner N2 - new burner concept for peroxy-fuels is proposed. The performance of the proposed peroxy-fuel burner is predicted with the help of Computational Fluid Dynamics (CFD) simulation. It is found that peroxy-fuel burner not only requires considerable less amount of fuel for the same output/power but also at the same time the overall size of the processing unit can be reduced. As peroxy-fuels contain oxygen atoms within the molecule itself a similar to oxy-fuel combustion environment is created without even supplying pure oxygen. CFD simulations also support the above facts and demonstrate the existence of less favorable conditions to form NOx. T2 - 38th National conference on fluid mechanics and fluid power CY - Bhopal, India DA - 15.12.2011 KW - Burner KW - Peroxy-fuels KW - Performance KW - CFD simulation PY - 2011 IS - Paper HT-07 SP - 1 EP - 6 AN - OPUS4-25380 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kolkoori, Sanjeevareddy A1 - Rahman, Mehbub-Ur A1 - Chinta, P.K. A1 - Prager, Jens T1 - Computationally efficient ray tracing algorithm for simulation of transducer fields in anisotropic materials N2 - This contribution describes a computationally efficient ray tracing algorithm for evaluating transducer generated ultrasonic wave fields in anisotropic materials such as austenitic cladded and austenitic weld components. According to this algorithm, ray paths are traced during its propagation through various layers of the material and at each Interface the problem of reflection and transmission is solved. The presented algorithm evaluates the transducer generated ultrasonic fields accurately by taking in to account the directivity, divergence, density of rays, phase relations as well as transmission coefficients. The ray tracing algorithm is able to calculate the ultrasonic wave fields generated by a point source as well as a finite dimension transducer. The simulation results are compared quantitatively with the results obtained from Elastodynamic Finite Integration Technique (EFIT) on several configurations generally occuring in the ultrasonic non destructive testing of anisotropic materials. The excellent agreement between both models confirms the validity of the presented ray tracing algorithm. Finally, the ray tracing model results are also validated by means of experiments. T2 - NDE 2011 - National seminar & exhibition on non-destructive evaluation CY - Chennai, India DA - 08.12.2011 KW - Ultrasonic sound field KW - Ray tracing KW - Directivity KW - Anisotropy KW - Austenitic weld PY - 2011 SP - 482 EP - 486 AN - OPUS4-25329 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Habel, Wolfgang A1 - Schukar, Vivien ED - Ramos, G. A. T1 - Validation of strain sensors to achieve reliable measurement results N2 - Fiber optic strain sensors are increasingly used and sensor Systems are provided with specifications. Even if the performance is well specified, the strain characteristics of the sensor, strain transfer factor, mechanical stability under thermal influences, the performance of applied strain sensors can seriously differ from virgin sensor’s the performance. Therefore the contribution considers validation issues to come to reliable strain measurements and how to validate strain measurements of applied sensors. A new validation facility will be presented. T2 - SHMII-5 - 5th International conference on structural health monitoring of intelligent infrastructure CY - Cancún, Mexico DA - 11.12.2011 PY - 2011 IS - Session 20, Topic 2.3 SP - 1 EP - 13 PB - National Autonomous University of Mexico CY - Mexico City AN - OPUS4-25309 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Habel, M. A1 - Vaterrodt, K. A1 - Heidmann, G. A1 - Habel, Wolfgang A1 - Vogelsang, R. A1 - Weissenberg, W. A1 - Sekula, O. A1 - Pepper, D. A1 - Emanuel, H. A1 - Plath, R. T1 - Optical PD detection in stress cones of HV cable accessories N2 - Sensitive partial discharge (PD) measurements on HV/EHV cable systems are usually based on electrical or electromagnetic PD detection. Unfortunately, interferences may significantly reduce sensitivity, especially in on-site after-installation testing and, even more, in on-line PD monitoring. This paper deals with optical PD detection, which is absolutely immune to any kind of electromagnetic interference. Optical PD detection necessarily requires transparent or translucent insulation systems to be applicable. Stress cone elements for HV/EHV cable accessories meet the requirements for optical PD detection, if made from transparent silicone elastomers. T2 - 8th International Conference on Insulated Power Cables CY - Versailles, France DA - 19.06.2011 PY - 2011 IS - B.8.4 SP - 1 EP - 5 PB - Jicable CY - Paris AN - OPUS4-25310 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Habel, Wolfgang A1 - Röben, R. A1 - Hüttl, R. A1 - Kuchejda, M. ED - Ramos, G. A. T1 - Monitoring of corrosion protection in reinforced concrete structures using an integrated pH optode N2 - Corrosion in steel-reinforced concrete structures is a critical issue. Corrosion appears if the pH value of the concrete matrix decreases due to deterioration of the Calcium hydroxide layer on the Steel surface. The safest Information about potential danger of Steel corrosion is the knowledge of the pH value of concrete. The paper presents a Tiber optic pH sensor for long-term monitoring of the pH value of reinforced concrete structures at risk from corrosion. The sensor probe is small (about 8 mm in diameter), can be embedded into the concrete matrix and observe changes in pH over years. Several sensor probes can be staggered to detect the progression of pH decrease. The pH values can be resolved with 0.1 to 0.2 pH value in the ränge between 12.0 and 9.5. The structure of the pH measurement System, longterm test results and the design to achieve stable probes will be explained. Experienee from test applications of pH sensors embedded in grouted anchors and in concrete components for a cooling tower will be presented. T2 - SHMII-5 - 5th International conference on structural health monitoring of intelligent infrastructure CY - Cancún, Mexico DA - 11.12.2011 PY - 2011 IS - Session 15, Topic 4.5 SP - 2 EP - 8 PB - National Autonomous University of Mexico CY - Mexico City AN - OPUS4-25311 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Helm, C. A1 - Eichler, Thorsten A1 - Raupach, M. A1 - Isecke, Bernd T1 - Time dependency of current and potential distribution during the cathodic protection of RC structures N2 - Cathodic protection (CP) is a common method for rehabilitation of reinforced concrete structures suffering from Chloride induced corrosion. A sufficient protection of the corroding rebar can be ensured by use of several protection criteria. The use of these assessment criteria, in particular the so called 100 mV-criterion, can lead to erroneous resuits for certain unconventional arrangements of rebar and cp anode. Therefore a joint research project of the Institute for Building Materials Research, RWTH-Aachen University, Germany, (ibac) and the Federal Institute for Materials Research and Testing, Berlin, Germany, (BAM) has been set up to determine the applicability of CP under arbitrary geometrical conditions. A special focus was set on the applicability of surface applied anode Systems for protection of the reinforcement of structures opposite to the accessible side (e.g. outer side of tunnel Shell, Bridge deck protected from inside a box girder) In this paper, the impact of the time dependent changes of the Polarisation behaviour of the rebar on the current and potential distribution is shown by means of parametric studies using the FEM method. T2 - EUROCORR 2011 - Developing solutions for the global challenge CY - Stockholm, Sweden DA - 04.09.2011 KW - Cathodic protection KW - Long time effects of cathodic polarisation KW - FEM-modelling KW - Steel in concrete PY - 2011 SP - 1 EP - 11 AN - OPUS4-25326 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Gaal, Mate A1 - Bertovic, Marija A1 - Müller, Christina A1 - Zickler, S. A1 - Fahlbruch, B. A1 - Spokoiny, V. A1 - Schombach, D. A1 - Just, Tilman A1 - Cramer, H.-J. T1 - Untersuchungen zum Einfluss menschlicher Faktoren auf das Ergebnis von zerstörungsfreien Prüfungen, Möglichkeiten zur Minimierung dieses Einflusses und Bewertung der Prüfergebnisse KW - Menschliche Faktoren KW - ZfP KW - Manuelle Ultraschallprüfung KW - WkP KW - KKW PY - 2009 IS - BfS-Projekt SR 2514 / Endbericht SP - 1 EP - 79 CY - Salzgitter AN - OPUS4-26081 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pitkänen, J. A1 - Salonen, T. A1 - Bertovic, Marija A1 - Müller, Christina A1 - Pavlovic, Mato T1 - NDT reliability in risk minimization during manufacturing and welding of spent nuclear fuel disposal components - a realistic tool for reliable inspections T2 - 4th European-American workshop on reliability of NDE CY - Berlin, Germany DA - 2009-06-24 KW - NDT reliability KW - Spent nuclear fuel KW - EB-weld PY - 2009 UR - http://www.ndt.net/article/reliability2009/Inhalt/fr1a2.pdf IS - Fr.1.A.2 SP - 1 EP - 21 AN - OPUS4-26082 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burkert, Andreas A1 - Fischer, Joachim A1 - Zietelmann, Christina A1 - Lehmann, Jens T1 - Sauber! - Erhaltung des Korrosionsschutzes bei 'rostfreiem Stahl' N2 - Es ist mittlerweile eine zunehmend bekannte Tatsache, dass „nichtrostende“ Stähle trotz ihres Namens rosten können. Werden die spezifischen Besonderheiten und Anforderungen, die sich beim Einsatz nichtrostender Stähle ergeben, aus Unkenntnis oder Nachlässigkeit nicht beachtet, kann dies zu unerwarteten Korrosionserscheinungen und auch zum funktionalen Versagen von Konstruktionen führen. Im Folgenden wird dargestellt, dass nichtrostende Stähle nur dann korrosionsbeständig bleiben, wenn auch Reinigung und Pflege der Oberflächen mehr Beachtung finden. Bereits in der Planungsphase, spätestens aber bei der Ausführung muss klar sein, wie mit den Oberflächen urngegangen werden soll, um ihre positiven Eigenschaften zu erhalten. Nicht zuletzt müssen auch die Betreiber und Nutzer wissen, dass nichtrostende Stähle in vielen Bereichen erheblichen Pflege- und Erhaltungsbedarf haben. KW - Nichtrostender Stahl KW - Austenit KW - Ferrit KW - Lean Duplex KW - Korrosionsverhalten PY - 2011 VL - III SP - 9 EP - 14 PB - Bernheine AN - OPUS4-26059 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eisenacher, Germar A1 - Kuschke, Christian A1 - Schubert, Sven A1 - Neumann, Martin A1 - Sterthaus, Jens A1 - Nitz, Thilo A1 - Wille, Frank T1 - Moisture content of wood - influence on mechanical behavior of wood filled impact limiter and importance for quality surveillance during manufacturing N2 - The moisture content of wood is known to have a significant influence on the wood’s mechanical properties. Using wood as an energy absorber in impact limiter of packages for the transport of radioactive material, it is of particu-lar importance to ensure the moisture content and thus relevant mechanical properties to be in specified limits. The paper surveys the influence of wood moisture content on the mechanical properties of wood. Different measuring methods are discussed with respect to in-situ applicability, accuracy and effort. The results of an experimental ana-lysis of the accuracy of hand-held moisture meters using the electrical resistance method are discussed. Conclu-sions are drawn regarding the measurement of moisture content of wood upon delivery as well as of complete im-pact limiter assemblies. Requirements for quality surveillance during manufacturing of wood filled impact limiter are derived and it is exemplified how to meet them. Construction, manufacturing and inspection of impact limiter encapsulation with regard to leak-tightness are addressed. T2 - RAMTRANSPORT 2012 - 9th International Conference on the Radioactive Materials Transport and Storage CY - London, UK DA - 2012-05-22 KW - Mechanical behavior of wood KW - Moisture content KW - Impact limiter PY - 2012 IS - 4.4 RAM 30 SP - 1 EP - 11 AN - OPUS4-26241 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erhard, Anton A1 - Noack, Volker A1 - Völzke, Holger T1 - Storage facilities at Sayda Bay N2 - Within the framework of the G8 partnership, the German Ministry of Economics and Technology has been realizing a 300 EUR million project of the storage of decommissioned Russian nuclear submarines based on a German-Russian agreement. The main parts of the project are the construction of the long-term storage facility as well as a radioactive waste storage facility at Sayda Bay. Long-term interim storage facility for this particular case has a period of about 70 years. The Energiewerke Nord GmbH (EWN) under the technical controlling of BAM carried out the project management. Foremost in this presentation is the finalization of the long-term storage facility for nuclear submarine compartments and the planning and realization of the radioactive waste storage building with special emphases of the parts carried out by BAM. Because BAM staff cannot stay permanently on site, a random inspection of different topics was the bases for the activities of BAM. The key aspects of activities are the long-term storage of the nuclear compartments, maintenance building, the decommissioning of the compartments and the transportation of the very heavy weight compartments (1600 metric tons). Details relating of the progress of the construction work as well as information about technical recommendations will also be briefly illustrated. Within this scope, problems and difficulties during the construction of the storage facility as well as logistical challenges including transportation of the reactor compartments will also be discussed. T2 - 52nd INMM Annual meeting CY - Palm Desert, CA, USA DA - 17.07.2011 KW - Storage facility KW - Nuclear reactor compartments PY - 2011 SP - 1 EP - 7 AN - OPUS4-26197 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burkert, Andreas A1 - Lehmann, Jens T1 - Edelstahl Rostfrei - Alternativen zu den Standardausteniten KW - Nichtrostender Stahl KW - Austenit KW - Lean Duplex KW - Ferrit KW - Korrosionsprüfung PY - 2012 VL - 2012 SP - 1 EP - 3 CY - Düsseldorf AN - OPUS4-26259 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ballheimer, Viktor A1 - Wille, Frank A1 - Rolle, Annette A1 - Droste, Bernhard T1 - Mechanical behaviour of high burn-up SNF under normal and accident transport conditions - present approaches and perspectives N2 - Transport packages for spent fuel have to meet the International Atomic Energy Agency requirements for different transport conditions. Physical state of spent fuel and fuel rod cladding as well as geometric configuration of fuel assemblies are important inputs for the evaluation of package capabilities under these conditions. In this paper, the mechanical behaviour of high burn-up spent fuel assemblies under transport conditions is analysed with regard to assumptions to be used in the activity release and criticality safety analysis. In particular the different failure modes of the fuel rods (fine cracks or complete breakage), which can cause release of gas, volatiles, fuel particles or fragments have to be properly considered in these assumptions. In view of the complexity of interactions between the fuel rods as well as between fuel assemblies, basket, and cask containment, the exact mechanical analysis of such phenomena is nearly impossible. The gaps in information concerning the material properties of cladding and pellets, especially for the high burn-up fuel, make the analysis more complicated additionally. In this context some practical approaches based on experiences of BAM Federal Institute for Material Research and Testing within safety assessment of packages for transport of spent fuel are discussed. T2 - ASME 2012 Pressure vessels & piping division conference CY - Toronto, Ontario, Canada DA - 15.07.2012 KW - Fuel rods KW - High burn-up KW - Mechanical behaviour KW - Transport conditions PY - 2012 SP - PVP2012-78302, 1-7 PB - American Society of Mechanical Engineers CY - New York AN - OPUS4-26320 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nehrig, Marko A1 - Bletzer, Claus Wilhelm A1 - Wille, Frank T1 - Pressure build-up inside packages containing wet intermediate level radioactive waste due to thermal loads N2 - Over the last years several transport approval procedures were finished for ductile cast iron containers containing wet intermediate level waste. BAM was involved in the assessment of mechanical and thermal aspects, activity release and material and component behavior regarding fulfillment of the regulatory requirements. The radioactive contents of these package designs which were not dried, only drained, consist of saturated ion exchange resin and a small amount of free water. Regarding wet contents, the most interesting point, however, is the pressure build-up inside the package due to vaporization. This could be aused by radiolysis of the liquid and must be taken into account for the storage period. The paper deals primarily with the pressure build-up inside the package aused by the regulatory thermal test (30 min at 800°C) as part of the cumulative test scenario under accident conditions of transport. The pressure build-up is estimated by calculation in a very conservative way regarding conduction and heat radiation. To get trustworthy results without an exact specification of the content, physical fire tests should be conducted. This paper will result in the strong advice, that contents should be dried to ensure a positive outcome of the safety assessment. T2 - ASME 2012 Pressure vessels & piping division conference CY - Toronto, Ontario, Canada DA - 15.07.2012 KW - Radioactive material KW - Pressure build-up KW - Wet intermediate level waste PY - 2012 SP - PVP2012-78282, 1-6 PB - American Society of Mechanical Engineers CY - New York AN - OPUS4-26321 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - King, M.J. A1 - Iacobucci, P.A. A1 - Mak, W.A. A1 - Wehrstedt, Klaus-Dieter T1 - Report about the IGUS EOS meeting 2011 in Washington, D.C. N2 - IGUS is the International Group of Experts on the Explosion Risks of Unstable Substances. IGUS was established in 1962 with the objective to harmonize test methods used by different countries to identify and quantify the explosive properties of unstable materials. Over the years, IGUS has continued to offer scientists, who are advisers to their governments, and others, a forum to exchange data and information. The Energetic and Oxidizing Substances (EOS) working group as a sub-group of IGUS is dealing with test methods, Classification and safety aspects relating to organic peroxides, self-reactive substances and other energetic substances, fertilizers, ammonium nitrate and oxidizers. The EOS working group holds an annual meeting alternating between Europe, the United States and Japan. The 2011 meeting took place from the 27th to the 29th of April 2011 at the Madison Hotel in Washington, D. C. The meeting was hosted by the Organic Peroxide Producers Safety Division (OPPSD) of the Society of Plastics Industry, Inc. (SPI). This was the fourth EOS meeting held in the USA since 1994. Of particular importance is the fact that 39 colleagues from authorities, universities, research institutes and industries attended the meeting. The delegates came from USA, Canada, China, France, The Netherlands, Norway, Sweden, Italy, Japan, United Kingdom and Germany. This confirms the breadth and scope of this forum and the value the participants associate with being able to contact other colleagues from around the world enabling the effective exchange of scientific results and discussion on the wide-ranging Problems concerning energetic and oxidizing materials. T2 - IGUS EOS Meeting 2011 CY - Washington D.C., USA DA - 27.04.2011 KW - IGUS KW - EOS KW - Organic peroxides KW - Self-reactive substances KW - Test methods KW - Oxidizers KW - Round robin test PY - 2011 SP - 1 EP - 4 AN - OPUS4-26364 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Wiederholt, Wilhelm ED - Steudel, H. T1 - Korrosionsprüfung PY - 1960 IS - II E7 SP - 1 EP - 14 PB - VDI-Verl. CY - Düsseldorf AN - OPUS4-25048 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Göbel, E. O. A1 - Hasche, K. A1 - Ulm, G. A1 - Krumrey, M. A1 - Ade, G. A1 - Stümpel, J. A1 - Herrmann, K. A1 - Koenders, L. A1 - Thomsen-Schmidt, P. A1 - Pohlenz, F. A1 - Xu, M. A1 - Dai, G. A1 - Hoffmann, K.-P. A1 - Busch, I. A1 - Frank, W. A1 - Procop, M. A1 - Beck, Uwe T1 - Kalibrierte Schichtdicken-Maßverkörperungen für Nanometerschichten, Teilvorhaben - Kalibrierung von Schichtdicken-Maßverkörperungen im Nanometerbereich - Abschlussbericht des BMBF Verbundvorhabens 13N7704 - 13N77041 KW - Schichtdicke KW - Nanometerbereich PY - 2003 UR - http://edok01.tib.uni-hannover.de/edoks/e01fb02/373214030.pdf SP - 1 EP - 131 PB - Physikalisch-Technische Bundesanstalt CY - Dresden AN - OPUS4-25428 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Bobe, U. A1 - Beck, Uwe A1 - Wegwerth, Tillmann A1 - Sahre, Mario A1 - Weise, Matthias A1 - Strauß, Birgid A1 - Reetz, Susanne A1 - Schondelmaier, D. A1 - Kutz, O. A1 - Winzer, B. A1 - Schaule, G. T1 - Nanotechnologische Entwicklung von "easier-to-clean"- Oberflächenstrukturen für eine zukünftig gesteigerte Lebensmittel- und Produktsicherheit - Abschlussbericht AiF-Vorhaben Nr.: 210 ZN III N2 - Reinigung wird in der Lebensmittel- und Pharmaindustrie aufgrund des stetig steigenden Kosten- und Zeitdrucks sowie der hohen Verbrauchererwartungen hinsichtlich Produktsicherheit und -haltbarkeit ein immer zentraleres Thema. Eine verbesserte Reinigbarkeit bedeutet für die produzierende Industrie eine Steigerung der Effizienz der Produktionsanlage. Besonders in der heutigen medienintensiven Zeit kommt ein "Lebensmittelskandal" durch ein unsicheres Produkt einem finanziellen Desaster und immensem Imageverlust gleich. Aus diesem Grund ist die Reinigbarkeit der produktberührenden Oberflächen stets ein wichtiges Kriterium für die Werkstoffauswahl. Basierend auf den Theorien zu Schmutzhaftung und -entfernung wurde im Rahmen dieser Arbeit überprüft, ob und wie die theoretisch relevanten Parameter auch in den Experimenten den Reinigungserfolg beeinflussen. Der Schwerpunkt wurde auf die Einflussgrößen des Werkstoffes gelegt, um herauszufinden, wie stark eine Oberfläche selbst zu ihrer Reinigbarkeit beitragen kann (self-cleaning). In den durchgeführten Versuchen hat sich gezeigt, dass die Oberflächenrauheit lediglich bei der Reinigung von kohäsiven Schmutzfilmen eine entscheidende Rolle gespielt hat. Hingegen ist ihr Einfluss auf das Reinigungsergebnis von sich auflösenden Schmutzfilmen und Partikeln nur begrenzt bis gar nicht zur Geltung gekommen. Das Oberflächenmaterial hatte keinen starken, aber dennoch signifikanten Einfluss auf die Reinigbarkeit der untersuchten Oberflächen. Dass die Reinigbarkeit einer Oberfläche keine Materialkonstante sein kann, wurde unter Verwendung spezieller Oberflächen mit definiert geätzten Rauheitsstrukturen nachgewiesen. Der Reinigungserfolg hängt immer auch von der Verunreinigungsart ab, was sich auch in vergleichbaren Versuchen der Einzelpartikelablösung mittels AFM in dem Einfluss der Elastizität bzw. Plastizität der Partikeln geäußert hat. Praxistaugliche Empfehlungen gehören mit zu den wichtigsten Zielen dieser Arbeit gewesen. Mit Fokus auf die Oberflächenparameter und auf Basis der durchgeführten Untersuchungen wurde zur Optimierung der Reinigung produktberührender Oberflächen für bekannte Kontaminationen eine Checkliste als Orientierungshilfe erarbeitet. Ist die Verunreinigungsart dennoch unbekannt, so sollte der "Grenzwert" von Ra = 1 µm unterschritten werden, um bei Vorhandensein filmartiger Verschmutzungen keine negativen Auswirkungen auf die Reinigbarkeit zu haben. Die Notwendigkeit nach hochpolierten Oberflächen (Ra < 0,3 µm) aus Reinigbarkeitsgründen kann aufgrund der Untersuchungen nicht nachvollzogen werden. Das Ziel des Vorhabens wurde erreicht. PY - 2007 SP - I EP - 148 PB - TU München CY - Weihenstephan AN - OPUS4-25430 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Berger, Anka A1 - Schmidt, Martin A1 - Ferrero, Fabio A1 - Krause, Ulrich T1 - Leitfaden zur Brandvermeidung durch Selbstentzündung bei der Lagerung von Recycling- und Deponiestoffen KW - Selbstentzündungsgefährdung KW - Recycling- und Deponiestoffe KW - Brandschutzmaßnahmen PY - 2010 SP - 1 EP - 16 PB - MUGV Brandenburg - Referat Presse- und Öffentlichkeitsarbeit CY - Potsdam AN - OPUS4-25391 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Carvalho, José Joao T1 - Immunochemical and chromatographic methods for two anthropogenic markers of contamination in surface waters: caffeine and coprostanol N2 - Caffeine (1,3,7-trimethylxanthine) and coprostanol (5β-cholestan-3β-ol) were detected in samples of Berlin's surface water. Their concentrations correlated with the contamination status of the samples, suggesting their usefulness as markers of human activity. Remarkably, caffeine concentrations were always well above the limit of quantitation of 0.025 µg/L. In order to screen surface water samples in larger series, the development of two novel methods was required: a monoclonal antibody-based immunoassay for caffeine and a dispersive liquid-liquid microextraction (DLLME) method, followed by liquid chromatography tandem mass spectrometry (LC-MS/MS) for coprostanol. The caffeine immunoassay developed shows the best analytical limit of detection (LOD) obtained so far for caffeine (0.001 µg/L), allows high-throughput analysis, and does not require sample pre-treatment. The assay was also successfully employed to measure caffeine in beverages, shampoos, caffeine tab-lets, and human saliva. Antibodies to coprostanol are not commercially available. A new strategy to generate anti-coprostanol antibodies was elaborated using an analogous com-pound as hapten – isolithocholic acid (ILA) – and immunizing a group of mice. A polyclonal anti-ILA serum was produced, which binds coprostanol but the low affinity did not permit setting up an immunoassay to measure environmental concentrations of the analyte (in the range of ng/L). Specific anti-ILA immunoglobulin G were also found in the faeces of the immunized mice. Coprostanol was quantified in the water samples using a newly developed LC-MS/MS method using atmospheric pressure chemical ionisation (APCI). Concentrations above 0.1 µg/L were determined after sample preconcentration using DLLME. This extraction method also proved to be successful for enrichment of coprostanol-related compounds such as cholesterol, cholestanol, cholestanone, ergosterol, and stigmasterol. KW - Immunoassay KW - ELISA KW - Koffein KW - Coprostanol KW - Marker KW - Umweltanalytik KW - LC-MS/MS KW - Hybridoma-Technik PY - 2011 DO - https://doi.org/10.18452/16420 SP - 1 EP - 280 CY - Berlin AN - OPUS4-26389 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gaal, Mate A1 - Döring, Joachim A1 - Bartusch, Jürgen A1 - Beck, Uwe A1 - Weise, Matthias A1 - Bovtun, Viktor Petrovic A1 - Brekow, Gerhard A1 - Kreutzbruck, Marc T1 - Parameter reproducibility of polypropylene ferroelectret transducers for air-coupled ultrasonic testing N2 - The extremely low acoustic impedance of polypropylene ferroelectret combined with its piezoelectric properties makes this material suitable for construction of aircoupled ultrasonic transducers for non-destructive testing. For the fabrication of transducers with a stable quality, the reproducibility of their key parameters is of interest. The reproducibility was evaluated by means of (i) impedance spectroscopy and (ii) pulse-echo measurements. (i) Impedance spectroscopy was applied to identify the resonance frequency, the coupling factor and the acoustic impedance of several nominally identical transducers. (ii) Pulse-echo measurements yielded the signal form of these transducers. The variation of the signal amplitude measured with pulseecho technique was about 10 dB. A part of this variation Comes from the deposition of transducer electrodes and another part from local variations of ferroelectret properties. The variation of the signal amplitude was caused by the observed variation of the coupling factor, which was also about 10 dB. The variation of the acoustic impedance was only about 1 dB, thus having no effect on the variation of the signal amplitude. These results indicate that the variability can be reduced by improving the control of electrode deposition and by optimizing the production technology affecting the reproducibility of material properties. T2 - 2011 IEEE International ultrasonics symposium (IUS) CY - Orlando, FL, USA DA - 18.10.2011 KW - Air-coupled ultrasonic transducers KW - Polypropylene ferroelectret KW - Reproducibility PY - 2011 IS - Abstract-ID 258 SP - 1 EP - 3 AN - OPUS4-26405 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Adamczyk, Burkart A1 - Schütze, M. T1 - Entwicklung eines neuartigen korrosionsfesten Schutzschichtsystems für einen Prozess zur thermochemischen Aufbereitung von Klärschlammaschen zu Düngemitteln N2 - Zur Erschließung anthropogener Phosphorquellen wurde an der BAM ein Prozess zur Umwandlung von Klärschlammasche in Phosphordünger entwickelt. Die erforderliche Entfernung der Schwermetalle erfolgt in hoch Chlor- oder Chlorwasserstoffhaltigen Atmosphären bei 1000°C. Zur wirtschaftlichen Umsetzung dieses Verfahrens muss ein Ofenwerkstoff verwendet werden, der unter diesen extremen Korrosionsbedingungen beständig ist. Solche Werkstoffe sind derzeit nicht verfügbar. Ziel des Projektes war es, ein unter den Prozessbedingungen beständiges Schutzschichtsystem zu finden, das für die großtechnische Umsetzung geeignet ist. Dazu wurde die Entwicklung eines neuartigen Schutzschichtsystems angestrebt, das die hohe chemische Beständigkeit einer Keramik als Deckschicht mit den hervorragenden Materialeigenschaften eines Metalls als Trägerwerkstoff kombiniert. Die Schichten wurden durch thermisches Spritzen als großtechnisch einsetzbare Applikationsmethode aufgebracht. Es wurden Systeme aus verschiedenen Keramiken (Korund, Magnesiumoxid, Aluminium-Magnesium-Spinell, Y-stabilisiertes Zirkoniumoxid, sowie Mischungen von Spinell bzw. Korund mit MgO) in Kombination mit einem neuartigen Haftvermittler auf NiAlMo-Basis untersucht. Die Versuche zeigten, dass diese neu entwickelte Haftvermittlerschicht unter einer Keramik mit geringer Durchlässigkeit für Sauerstoff bzw. bei geeigneter Vorbehandlung (Voroxidation bei niedrigen Sauerstoffpartialdrücken) eine dichte Oxiddeckschicht bildet. Sie verzögert selbst unter diesen extremen Bedingungen das Fortschreiten der Korrosion und übertrifft in ihrer korrosionsinhibierenden Wirkung alle bekannten metallischen Systeme (wie z.B. auch bekannte kommerzielle NiCrAlYHaftvermittler oder Nickelbasis-Superlegierungen) bei weitem. Die Schichthaftung der keramischen Deckschichten ist dabei von der Anpassung des thermischen Ausdehnungskoeffizienten auf das Gesamtsystem abhängig. Zusätzlich werden eine niedrige Sauerstoffleitfähigkeit bei gleichzeitig hoher Korrosions- und Abrasionsbeständigkeit benötigt. Mit Hilfe der Erkenntnisse aus dem Projekt lässt sich durch eine Modifikation des Haftvermittlers die Haftung der Deckschicht verbessern, so dass eine Einsatzmöglichkeit im direkten Reaktorbetrieb zu erwarten ist. Auf diese Weise wurde im Rahmen dieses Projektes eine Beschichtungslösung entwickelt, die alle bekannten metallischen Systeme bei weitem übertrifft und sich für den Einsatz unter chlorhaltigen Hochtemperaturbedingungen eignet. Das Ziel des Projektes wurde somit erreicht. PY - 2012 IS - Vorh. 16432 N SP - 1 EP - 61 CY - Frankfurt/M. AN - OPUS4-26527 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Adamczyk, Burkart T1 - RECARC - Verwertung von Rückständen aus der Metallurgie mit der Lichtbogenofentechnologie N2 - The project RECARC is to demonstrate the complete recycling of slag gained from the stainless steel production after the AOD-process. Due to the high content of chromium, this slag is only usable in qualitative inferior applications. Thermochemical treatment by arc furnace enables the separation of chromium from the mineral fraction. The recovered chromium can be returned as raw material into the stainless steel production. Furthermore, the processing turns the slag into a useful building material. The investigations focused mainly on nearly complete reduction and removal of the chromium from the mineral fraction. The process parameters were optimised and different reducing agents (carbon, aluminium, FeSi and SiC) were tested. The chromium content of an AOD-slag was successfully significant decreased to >0.1% by resistance melting in addition of petroleum coke as reducing agent. By adding adequate additives and a granulation of the slag the mineral fraction can be simply improved to a phase, which is similar to typical cement components. Furthermore, EOF-slag, which consist much more chromium compounds, was tested. In this slag 80% of the chromium was successfully removed. Totally 30 melting experiments with a total conversion of 5.5 tons of stainless steel slag had been carried out. Thus, totally 220 melting products were gained. Although the characterisation of the products was affected by technical reasons, appearing problems could be solved by choosing alternative characterisation methods. The project results were published more than 20 times (presentations in journals and on international conferences, press releases, poster presentations, internet page).------------------------------------------------------------------------------------------------------------------------------------ Im Projekt RECARC wird eine Möglichkeit für die vollständige Wiederverwertung einer bei der Herstellung von Edelstahl nach dem AOD-Verfahren anfallenden Schlacke demonstriert. Die Schlacke enthält erhebliche Mengen Chrom in Form metallischer Einschlüsse (2-5%) und mineralisch gebunden (3-4%) und wird daher gegenwärtig nur minderwertig bzw. nicht genutzt. Durch eine thermochemische Behandlung im Lichtbogenofen wird das Chrom von der mineralischen Fraktion getrennt, so dass es als Rohstoff bei der Edelstahlherstellung wiederverwendet werden kann. Die schwermetallfreie Schlacke wird durch geeignete Maßnahmen so konditioniert, dass sie als Baustoff uneingeschränkt verwendet werden kann. Die Effektivität der Reduktion und der Chromabscheidung wurde für unterschiedliche Betriebsparameter und die Reduktionsmittel Koks, Aluminium, FeSi und SiC mit dem Ziel der Optimierung des Verfahrens bestimmt. Optimal für das angestrebte Ziel ist der Betrieb im Widerstand mit Petrolkoks als zusätzlichem Reduktionsmittel. Unter diesen Bedingungen kann der Cr-Gehalt einer AOD-Schlacke auf > 0,1% gesenkt werden. Durch entsprechende Zusätze und eine Schlackegranulation beim Abguss lässt sich die Schlackequalität so einstellen, dass sie den Anforderungen eines Zementzumahlstoffes genügt. Neben AOD-Schlacken wurde auch eine EOF-Schlacke mit wesentlich höheren Chromgehalten untersucht, der um ca. 80% durch die thermochemische Behandlung gesenkt wurde. Es wurden 30 Schmelzversuche durchgeführt, in denen ca. 5,5 t AOD bzw. EOF-Schlacke umgesetzt wurden. Die Gesamtzahl an unterschiedlichen Schmelzprodukten beläuft sich auf ca. 220. Die Charakterisierung der erhaltenen Produkte wurde wegen zeitweiser Geräteausfälle erschwert, konnte aber durch Einsatz alternativer Charakterisierungsmethoden immer duchgeführt werden. Inhalt und Ergebnisse des Projektes wurden durch über 20 Publikationen (Präsentationen in Fachzeitschriften und auf internationalen Tagungen, Pressemitteilungen, Posterpräsentationen und nicht zuletzt durch die Internetseite) der Öffentlichkeit zugänglich gemacht. PY - 2006 IS - Technischer Abschlussbericht (LIFE03 ENV/D/043 SP - 1 EP - 60 AN - OPUS4-26528 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beck, Uwe T1 - Charakterisierung idealer, realer und modifizierter Oberflächen für den sterilen Behälterbau N2 - Technische Oberflächen - im Anlieferungszustand oder modifiziert — werden hinsichtlich topographischer und energetischer Merkmale in der Abweichung von der »idealen « Oberfläche beschrieben. Die Topographie wird dabei durchgehend vom Makro- über den Mikro- bis in den Nano-Bereich mit den Methoden Streifenlichtprojektion (FP), Lichtmikroskopie (LM), mechanischem Tastschnitt (MS), Weißliehtinterferenzraikroskopie (WLIM), Rasterelektronen- (SEM) und Rasterkraftmikroskopie (AFM) erfasst. Replika-Verfahren ermöglichen dabei auch die indirekte Erfassung der Topographie an Bauteilen. Zur makroskopischen Bestimmung der Oberflächenenergie werden Randwinkelmessungen nach der Tropfen- bzw. der Plattenmethode herangezogen. Im Fokus stehen Materialien der Steriltechnik (Edelstahl, Emaille, PTFE), Passivschichten, Beschichtungen (Si02, a-C:H) und mikrostrukturierte Modelloberflächen (Silizium). Neben Standardisierungsaspekten (Mikro- vs, Nano-Rauheit) ist die Wechselwirkung der Oberflächen mit Partikeln (Haftung) von immanenter Bedeutung. Dabei sind Größe, Form und Plastizität der Partikel im Kontext mit der Oberflächentopographie zu betrachten. T2 - BMBF-Innovationsforum - Schützen und Veredeln von Oberflächen CY - Wildau, Germany DA - 28.02.2012 KW - Funktionelle Oberflächen KW - Oberflächentopographie KW - Oberflächenenergie KW - Haftung von Partikeln PY - 2012 SP - 59 EP - 68 AN - OPUS4-26943 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beck, Uwe T1 - Plasmabeschichtungsverfahren - eine Übersicht N2 - Einleitend wird eine kurze Einordnung der Plasmaverfahren innerhalb der Beschichtungstechnologien vorgenommen. Die vielfältigen Möglichkeiten der Plasmaverfahren werden an Hand von Beispielen zu Sehichtfunktionalitäten, Produktemund:Anlagenkonzepten, erläutert. Es wird aufgezeigt, dass die Plasmaverfahren industriell angewandte Nanotechnologie sind und branchenübergreifend eine Schlüsseltechnologie darstellen, die in der Verschränkung mit der Nanotechnologie noch ein enormes Zukunftspotenzial aufweist, und; für alle Kernbranchen des Wirtschaftstandortes Deutschland unverzichtbar sind. Dieser Aufgabe widmen sich in Deutschland unter dem Dach von PLASMA Germany insbesondere die EFDS in Dresden und INPLAS in Braunschweig. Der in Cannes prämierte INPLAS-Film »Plasma leuchtet ein«, der unter Federführung des FhG IST in Braunschweig entstand, zeigt auf, in wie vielfältiger Weise die Plasmatechnik schon heute unseren Alltag bestimmt. T2 - BMBF-Innovationsforum - Schützen und Veredeln von Oberflächen CY - Wildau, Germany DA - 28.02.2012 KW - Funktionelle Schichten KW - Plasmabeschichtung KW - PVD KW - PECVD PY - 2012 SP - 37 EP - 40 AN - OPUS4-26944 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Alexander, I. A1 - Braun, H.-J. A1 - Dettmann, T. A1 - Fimmen, H. A1 - Haberkamp, H. A1 - Katz, H. A1 - Krischok, Frank A1 - Otremba, Frank A1 - Pötzsch, Klaus-Michael A1 - Zentgraf, R. A1 - Putzschke, M. T1 - Bericht über den Ablauf und die Ursachen der Havarie des Tankmotorschiffes 'Waldhof' am 13. Januar 2011 auf dem Mittelrhein (Rhein-km 553,75) KW - Schiffshavarie KW - Gefahrgut-Tankschiff KW - Schwimmstabilität PY - 2013 IS - S-312.4/016 SP - 1 EP - 224 AN - OPUS4-27729 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Burkert, Annette A1 - Gümpel, P. T1 - Substitution von Standardausteniten - Welches Potenzial bieten nickelreduzierte Legierungen? N2 - Durch systematische Labor- und Auslagerungsuntersuchungen ist es möglich sieben unterschiedliche nichtrostende Stahllegierungen untereinander sowie in Bezug auf zwei weit verbreitete austenitische Standardwerkstoffe (1.4301, 1.4404) hinsichtlich ihres Korrosionsverhaltens zu vergleichen. Die parallele Untersuchung von fünf verschiedenen Oberflächenausführungen der jeweiligen Werkstoffe ermöglicht zudem branchenspezifische Besonderheiten der Oberflächenausführung beim Werkstoffvergleich zu berücksichtigen. Der Einfluss der Oberflächenausführung wird überwiegend bei den Ergebnissen der Auslagerungsversuche in kritischen Atmosphären sichtbar, weniger bei den elektrochemischen Untersuchungen. Die drei Vertreter aus dem Bereich der Duplexstähle zeigten innerhalb des Versuchsprogramms unter den meisten Bedingungen eine hervorragende Korrosionsbeständigkeit. Insbesondere für lastabtragende Bauteile können die Lean-Duplexstähle deutliche Vorteile bieten. Der Manganaustenit 1.4376 sowie der Ferrit 1.4509 sind nur eingeschränkt als Alternativen geeignet, da die Werkstoffe bei einigen Versuchen signifikante Schwächen zeigten. T2 - 12. Tagung Korrosionsschutz in der maritimen Technik CY - Hamburg, Germany DA - 23.01.2013 KW - Korrosion KW - Nichtrostender Stahl KW - Duplexstahl KW - Ferritischer Stahl PY - 2013 SP - 5 EP - 21 CY - Hamburg AN - OPUS4-27721 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Simone A1 - Deubel, Jan A1 - Werrel, Martin A1 - Fettig, Ina A1 - Raspe, Tina A1 - Piechotta, Christian T1 - Experimental studies on the effect of fire accelerant during living room fires N2 - The influence of fire accelerants on the fire behavior during living room fires was experimentally investigated by performing 5 different room fire scenarios. During the tests flre-technological quantities were determined as well as chemical-analytical studies were carried out. The focus was on the detection of smoke gases and the proof of used fire accelerants. The evaluation of traceable fire accelerants and the reconstruction of the fire development are based on a precise Chemical analysis of the combustion products. In this work an innovative methodology was developed to combine available analyticai techniques to draw conclusions from solid, liquid and gaseous fire residues about the fire process. Each ofthe fire rooms was equipped with the same living room inventory. The location and amount of fire accelerant (a mixture of diesel/gasoline) differed in 4 of 5 tests. Orte room fire experiment was carried out without fire accelerant. The following fire technological characteristics were determined during the room fire experiments: mass loss (of the complete room), temperatures (at several locations in the room), heat release and smoke gas emission (measured at three different locations: in the chimney, in the fire room and at the door opening). While the smoke gases were analysed by using Fourier Transform Infrared spectroscopy, the fire residues and swipe samples (particles) were examined by Headspace-Solid Phase Microextraction- Gaschromatography-Mass spectrometry. These procedures make it possible to detect low concentrations of volatile components of the fire accelerants. The Chemical analyticai results of the fire accelerant detection are presented. T2 - Fire and materials 2013 - 13th International conference and exhibition CY - San Francisco, CA, USA DA - 28.01.2013 KW - Accelerant KW - Chemical analysis KW - Toxicity PY - 2013 SP - 729 EP - 743 PB - Interscience Communications CY - London, UK AN - OPUS4-27708 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Richter, Regina A1 - Maierhofer, Christiane A1 - Kreutzbruck, Marc ED - Cardone, G. T1 - Numerical method of active thermography for the reconstruction of back wall geometry T2 - QIRT 11 - 11th International conference on Quantitative InfraRed Thermography CY - Prague, Czech Repubilc DA - 11.06.2012 KW - Rekonstruktion KW - Inverse Probleme KW - Defekte PY - 2012 SP - 1 EP - 9 AN - OPUS4-26446 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Apel, Andreas A1 - Ballheimer, Viktor A1 - Kuschke, Christian A1 - Schubert, Sven A1 - Wille, Frank T1 - Approach for the use of acceleration values for packages of radioactive material under routine conditions of transport N2 - The most relevant source of reference for load cases of packages for the transport of radioactive material under routine conditions is Appendix IV of the International Atomic Energy Agency (IAEA) Advisory Material TS-G-1·1. The acceleration values given there leave many questions open and have to be agreed upon with the involved competent authorities. Consequently, the actual load cases applied for a safety analysis may differ widely and could cause problems for international transport. To avoid such difficulties, it seems obvious that the according passages in TS-G-1·1 should be modified with the objective of making the load case data more consistent for a harmonized application in the IAEA member states. Papers pointing out in this direction were discussed at the PATRAM 2010 conference. The way to improve the acceleration data may lie in investigations and measurements considering, for example different types of vehicles and package masses. However, what should be the goal of such kind of surveys? Can such investigation provide values for every worldwide load case possible under routine conditions of transport? In particular, the different designs of vehicles give a reason to doubt that such an aim is realistic. The approach in this paper is to show that a less ambitious aim is more effective. Therefore, an approximate scheme is preferred, which renders better assistance in determining the appropriate acceleration values. T2 - RAMTRANSPORT 2012 - 9th International Conference on the Radioactive Materials Transport and Storage CY - London, UK DA - 22.05.2012 KW - Radioactive materials KW - Safety assessment KW - IAEA regulations KW - Lost cases KW - Routine conditions of transport PY - 2012 SP - 1 EP - 8 AN - OPUS4-26747 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quercetti, Thomas A1 - Musolff, André A1 - Müller, Karsten T1 - Instrumented measurements on radioactive waste disposal containers during experimental drop testing N2 - In context with disposal container safety assessment of containers for radioactive waste the German Federal Institute for Materials Research and Testing (BAM) performed numerous drop tests in the last years. The tests were accompanied by extensive and various measurement techniques especially by instrumented measurements with strain gages and accelerometers. The instrumentation of a specimen is an important tool to evaluate its mechanical behavior during impact. Test results as deceleration-time and strain-time functions constitute a main basis for the validation of assumptions in the safety analysis and for the evaluation of calculations based on finite-element methods. Strain gauges are useful to determine the time dependent magnitude of any deformation and the associated stresses. Accelerometers are widely used for the measuring of motion i.e. speed or the displacement of the rigid cask body, vibration and shock events. In addition high-speed video technique can be used to visualize and analyze the kinematical impact scenario by motion analysis. The paper describes some selected aspects on instrumented measurements and motion analysis in context with low level radioactive waste (LLW) container drop testing T2 - ICEM 2011 - 14th International Conference on environmental remediation and radioactive waste management CY - Reims, France DA - 25.09.2011 KW - Drop test KW - Radioactive KW - Disposal container KW - Instrumented measurements PY - 2011 DO - https://doi.org/10.1115/ICEM2011-59142 SP - 929 EP - 938 AN - OPUS4-27044 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nakagami, M. A1 - Quercetti, Thomas A1 - Komatsuki, S. A1 - Fujisawa, K. A1 - Nishio, T. A1 - Musolff, André A1 - Müller, Karsten A1 - Droste, Bernhard T1 - Waste container drop tests onto a concrete target N2 - The paper presents technical details of the drop test performance as well as some experimental results of tests carried out with the Japanese 'Yoyushindo-disposal' waste container for intermediate depth disposal. The tests were accompanied by various metrology to collect data as basis for safety assessment. T2 - PATRAM 2010 - 16th International symposium on the packaging and transport of radioactive materials CY - London, UK DA - 2010-10-03 KW - Waste container KW - Drop test KW - Concrete target PY - 2010 SP - 1 EP - 8 (Paper 367) AN - OPUS4-27045 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Adamczyk, Burkart A1 - Rammer, B. A1 - Schütze, M. T1 - Materialoptimierung für einen neuartigen Prozess zur thermochemischen Aufarbeitung von Klärschlammasche zu Düngemitteln N2 - Zur Überführung von Klärschlammaschen in phosphorhaltige Düngemittel wurde an der BAM ein Prozess entwickelt, bei dem die in der Asche noch enthaltenen Schwermetalle in einem Drehrohrofen bei Temperaturen von 1000°C durch einen hochchlorhaltigen Luftstrom in flüchtige Chloride überführt und entfernt werden. Die Anwendung dieses Prozesses im industriellen Maßstab setzt die Verwendung von Werkstoffen voraus, die unter den extremen Korrosionsbedingungen ausreichend beständig sind. Derzeit sind solche Werkstoffe nicht auf dem Markt. Ziel des Projektes war es, einen unter den Prozessbedingungen beständigen Werkstoff zu finden. Dazu wurden alitierte Nickelbasislegierungen und Siliziumcarbid- und Korundbasierte Keramiken unter statischen und dynamischen Bedingungen untersucht. In den statischen Versuchen wurde der Einfluss der chlorhaltigen Atmosphäre und der KSA auf die chemische Beständigkeit der untersuchten Materialien betrachtet. In den dynamischen Versuchen wurden die Proben zusätzlich zur chemischen noch einer abrasiven Belastung durch eine bewegte Klärschlammascheschicht unterzogen. Für eine effektive Schwermetallentfrachtung der Klärschlammasche sind Chlorkonzentrationen von mindestens 10% bei 1000°C erforderlich. Unter diesen Bedingungen zeigen alitierte Nickelbasislegierungen, die sich bei Chlorgehalten bis zu 5% und 800°C gut bewährt haben, jedoch bereits in den statischen Korrosionsversuchen eine mangelnde Beständigkeit. Durch eine zusätzliche abrasive Belastung wird die Schutzschicht so schwer beschädigt, dass der Werkstoff seinen Korrosionsschutz verliert und vollständig zerstört wird. Auch die untersuchten SiC-Keramiken wiesen bei 1000°C und 10% Cl2 eine unzureichende Beständigkeit auf. Hier kommt es durch den Kontakt mit Komponenten aus der Klärschlammasche zur Erweichung der äußeren, passivierend wirkenden, SiO2-Schicht und zur Herauslösung des in allen Werkstoffen vorhandenen 'freien' Siliziums durch das Chlor. Unter zusätzlicher abrasiver Belastung wird das Gefüge dadurch nachhaltig beschädigt oder sogar vollständig zerstört. Eine ausgezeichnete Beständigkeit wurde dagegen für Korund gefunden. Sowohl unter statischen als auch unter dynamischen Bedingungen kann keine chemische Schädigung festgestellt werden. In den dynamischen Versuchen bewirkt lediglich die Abrasion einen geringfügigen Materialabtrag. Als Werkstoff für die Behandlung von Klärschlammasche bei hohen Temperaturen und Chlorgehalten von 10% bietet somit nur Korund eine ausreichende Beständigkeit; sowohl alitierte Nickelbasislegierungen als auch SiC-basierte Keramiken sind für diesen Zweck ungeeignet. Gegenüber Korund als Werkstofflösung bestehen aufgrund seiner hohen Bruchgefahr und seiner Porosität jedoch erhebliche sicherheitsrelevante Bedenken. Darüber hinaus ist die Herstellung ausreichend großer Bauteile aus Korund derzeit nicht realisierbar. Obwohl ein Werkstoff mit sehr guter Beständigkeit im Projekt gefunden wurde, kann keine Empfehlung für eine geeignete Werkstofflösung gegeben werden. Durch die Forschungsarbeiten in diesem Projekt wurden jedoch wertvolle Erkenntnisse gewonnen, die die Grundlage für ein bereits beantragtes und von den Gutachtern befürwortetes Anschlussprojekt bilden. Das Ziel des Projektes wurde somit teilweise erreicht. PY - 2009 IS - 224 ZN Endbericht SP - 1 EP - 46 CY - Frankfurt/M. AN - OPUS4-26526 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Beständigkeit von Polyethylenformstoffen und Dichtungswerkstoffen gegenüber Biokraftstoffen T2 - 13. Gefahrgut-Technik-Tage Verpackungen + IBC CY - Berlin, Germany DA - 2012-11-12 KW - Biokraftstoffe KW - Beständigkeit KW - Polyethylen KW - Verpackungen KW - Dichtungswerkstoffe PY - 2012 UR - http://www.storck-verlag.de/gtt/2012/09_weltschev.pdf SP - 1 EP - 48 PB - Storck AN - OPUS4-27135 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ecker, Melanie A1 - Pretsch, Thorsten T1 - Durability of QR code carriers based on shape memory polymer N2 - The surface of a shape memory poly(ester urethane) (PEU) was either black- or blue-colored to obtain switchable quick response (QR) codes after laser engraving and thermomechanical functionalization (programming). The investigation of dye and functional stability against UVA and hydrolytic aging (at 23 and 60 °C) gave that contrast decline due to dye decolorization (in case of UVA aging) or distinct dye diffusion (in case of hydrolytic aging) finally inhibited the QR code readability. By contrast, PEU as marked base material could be adequately fixed and recovered even when the Michelson contrast in the QR code region was falling in course of aging below a crucial value of 0.1, whereupon the QR code was no longer readable. Hence, we concluded that under the given experimental conditions the decisive parameter for tag applicability was the surface contrast. T2 - SMASIS2012 - ASME 2012 Conference on smart materials, adaptive structures and intelligent systems CY - Stone Mountain, Georgia, USA DA - 2012-09-19 KW - Shape memory polymer KW - Durability KW - QR code KW - Poly(ester urethane) KW - Product and brand protection applications KW - Counterfeit-proof labels KW - Tags KW - QR code carriers KW - Switchable information carriers KW - Functionalization KW - Surface-specific dyeing PY - 2012 IS - SMASIS2012-8038 SP - 1 EP - 8 PB - ASME AN - OPUS4-27884 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mirtschin, Nikolaus A1 - Pretsch, Thorsten T1 - Miniturization of QR code carriers based on shape memory polymer N2 - Here we present a suitable tag prototype with phasesegregated poly(ester urethane) (PEU) as base material for effectively switching a quick response (QR) code in its surface from non-readable to readable. In comparison with recently introduced tags (different geometry) we minimized the thickness from plaque (2 mm) to foil size (0.5 mm) and reduced the lateral QR code length from 15 to 5 mm. Subsequent to surface-dyeing by means of guest diffusion, the QR code was laser-engraved. The implementation of thermo-mechanical functionalization via tensile deformation and cooling resulted in the formation of stable shapes, which exceeded the barrier of QR code readability at an elongation of 20%. Once functionalized, tags were switched on demand by heating. As such the recovery of the PEU was accomplished and the QR code could again be read out. QR code carriers based on shape memory polymer can be used in product and brand protection applications. T2 - SMASIS2012 - ASME 2012 Conference on smart materials, adaptive structures and intelligent systems CY - Stone Mountain, Georgia, USA DA - 2012-09-19 KW - Shape memory polymer KW - QR code KW - Poly(ester urethane) KW - Product and brand protection applications KW - Counterfeit-proof labels KW - Tags KW - Switchable information carriers KW - Functionalization KW - Miniaturization KW - Surface-specific dyeing KW - Victoria Blue B PY - 2012 N1 - Geburtsname von Mirtschin, Nikolaus: Fritzsche, N. - Birth name of Mirtschin, Nikolaus: Fritzsche, N. IS - SMASIS2012-8036 SP - 1 EP - 8 PB - ASME AN - OPUS4-27886 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ecker, Melanie A1 - Pretsch, Thorsten T1 - Freely configurable functionalization tool for switchable information carriers N2 - The selective compression of quick response (QR) and Data Matrix code carriers based on shape memory polymer (SMP) with a freely configurable steel ball type indenter and adjacent thermo-mechanical shape fixing gave notched, room temperature (23 °C) stable, temporary shapes with non-decipherable codes. The microscopic investigation of cryomicrotome sections unveiled indentation-related shape fixities of about 90%. Independent of the selected two-dimensional code, the triggering of the SM effect resulted in sufficient shape recoveries to restore the code readability so that a maximum number of characters including 122 for a QR code (version 7) and 112 in case of a Data Matrix code (version 12) could be read with a scanning and decoding device. Due to the large number of difficult to copy shapes with on demand releasable information, SMPs may serve as viable information carriers for product and brand protection applications. T2 - 3rd WMRIF Workshop for young materials scientists CY - Pathumthani, Thailand DA - 2012-08-28 KW - Shape memory polymer KW - QR code KW - Data matrix code KW - Poly(ester urethane) KW - Product and brand protection applications KW - Tags KW - Switchable information carriers KW - Freely configurable functionalization KW - Selective deformation KW - Steel ball type indenter KW - Spherical indentation KW - Cryomicrotome sections KW - Surface-specific dyeing PY - 2012 SP - 1 EP - 10(?) AN - OPUS4-27887 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mehdianpour, Milad A1 - Stengel, Dominik T1 - Wind measurements along a high-voltage overhead transmission line in Northern Germany - Appraisal of results N2 - The paper focuses on a unique project of wind measurements along a high voltage Overhead transmission line. For reliable information on the horizontal distribution of the wind flow, 13 positions along two spans of an overhead electrical line of about 400 m length each are selected for wind velocity measurements. Simultaneously, the structural response is measured at the towers. Preliminary analyses aim at the appraisal of results what is important for the upcoming system identification. It is shown that system identification of long span transmission lines exposed to gusty wind is possible by derivation of a so called joint acceptance function which describes the admittance from wind velocity to the system’s response. T2 - EACWE 2013 - 6th European-African conference on wind engineering CY - Cambridge, UK DA - 07.07.2013 PY - 2013 SP - 1 EP - 8 (Paper 13) AN - OPUS4-28863 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Karsten A1 - Scheidemann, Robert A1 - Auster, Jürgen T1 - Mechanical testing of component size specimen under impact conditons N2 - For validation of structural integrity under normal and hypothetical accident conditions during transport and storage of radioactive material the Federal Institute for Materials Research and Testing (BAM) focuses its safety related scientific research on advanced mechanical safety assessment methods including simulation of high rate impact of model components and structures. A drop and crash test facility with an unyielding target and a load capacity of 1.200 kg was designed for materials testing of component size specimen under impact conditions at elevated and higher loading rates. The maximum drop height is 12 meters which enables impact velocities up to 15 m/s. An exactly falling test object or drop weight allows impact, bending, compression as well as crash and crush tests with maximum input energy of 118 kJ. An arresting unit has been developed to avoid multiple impacts during instrumented drop tests. The paper presents experimental techniques and examples of various measurement methods and advancements in order to assess assumption of materials and components behavior by definite displacement and stresses within mechanical testing. Instrumented drop weight tests are performed to complete materials data base and energy absorption of shock-absorbing materials and structures as well as to implement materials and structural parameters into FEA of reference structures. Furthermore, fracture mechanics parameters of thick walled DCI containers by means of dynamic bending tests are characterized by crack initiation and crack resistance behavior at the lowest operational temperature depending on the strain rate. T2 - PVP2013 - ASME 2013 Pressure vessels & piping division conference CY - Paris, France DA - 14.07.2013 KW - Component size KW - Impact test KW - Dynamic compression KW - J-integral PY - 2013 DO - https://doi.org/10.1115/PVP2013-98000 IS - PVP2013-98000 SP - 1 EP - 7 AN - OPUS4-28893 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Marotzke, Christian A1 - Feldmann, Titus T1 - Fracture mechanics of composite plies on microscale N2 - The determination of the strength and the failure behaviour of fiber reinforced composites is a complex task. This is mainly due to the anisotropy and the inhomogeneiety of the material on the microscale. The strength or the fracture toughness of the interface between fiber and matrix is the key factor controlling the failure process on microscale, especially under loads transverse to the fiber axes. The ultimate failure of a laminate is a complex process consisting of a large number of different subprocesses. Due to its highly dynamic nature on one hand and the microscopical scale on the other it is not possible to observe the ultimate failure directly or even to analyse it theoretically. However, long before ultimate failure occurs a large number of elementary failure processes take place in a rather static manner or at least at low crack Propagation speed. T2 - ICCM19 - 19th International conference on composite materials CY - Montreal, Canada DA - 28.07.2013 KW - Fracture mechanics KW - Laminate KW - Interface KW - Debonding KW - Energy release rate PY - 2013 SP - 5354 EP - 5363 AN - OPUS4-28913 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ellouz, Manel A1 - Kasparek, Eva Maria A1 - Völzke, Holger T1 - Konkretisierung der Anforderungen an Abfallbehälter für das Endlager Konrad N2 - Nicht wärmeentwickelnde radioaktive Abfälle, die in der Schachtanlage Konrad endgelagert werden sollen, müssen entsprechend den geltenden Anforderungen für die Endlagerung radioaktiver Abfälle konditioniert und in vom Bundesamt für Strahlenschutz (BfS) zugelassene Behälter verpackt werden. Gemäß einer Verwaltungsvereinbarung erfolgt die zugehörige Bauartprüfung für diese Behälter im Auftrag des BfS durch die BAM. Angesichts des geplanten baldigen Beginns der Betriebsphase des Endlagers Konrad steigt die Anzahl an Zulassungsverfahren, wobei die für alle Behälter gültigen Spezifikationen als auch die nach Behältertyp und -Werkstoff, einzulagerndem Inventar und erforderlichem Sicherheitsniveau differenzierten Anforderungen Gegenstand einer intensiven Diskussion zwischen Behörden, Sachverständigen und Antragstellern sind. Die BAM wurde aufgrund ihrer Erfahrungen in der Behälterqualifikation beauftragt nicht hinreichend konkretisierte behälterspezifische Aspekte in den oben genannten Berichten zu identifizieren und Vorschläge zur Präzisierung unter Berücksichtigung der hierfür relevanten Nebenbestimmungen aus dem Planfeststellungsbeschluss zu erarbeiten. Das Ziel ist Textteile, die unterschiedliche Interpretationen erlauben, zu überarbeiten oder zu kommentieren und somit die Konsistenz, Eindeutigkeit und Verständlichkeit der Konrad-Anforderungen zu verbessern. Ein weiterer wichtiger Aspekt ist die Notwendigkeit der Vervollständigung bestimmter Anforderungen wie zum Beispiel der Prüfanweisung zur Stapelung von Rundgebinden. Ohne das Niveau der Konrad-Anforderungen zu verändern, soll sowohl für die Antragstellerseite eine verbesserte und aktualisierte Grundlage zur Vorbereitung und Erstellung der Nachweisunterlagen, als auch für die prüfenden Institutionen auf dem Weg von der Bauartprüfung über die Konditionierungskampagnen bis hin zur späteren Ablieferung an das Endlager eindeutigere Prüfrandbedingungen vorgegeben werden. Insgesamt können dadurch auf allen Seiten sowohl Aufwand als auch Zeitbedarf für die zahlreichen notwendigen Bauartprüfungen verringert werden. Zu diesem Zweck hat die BAM zunächst einen Themenkatalog mit behälterspezifischen Fragestellungen vorbereitet, der die bisher in der Praxis der durchgeführten oder durchzuführenden Bauartprüfungen festgestellten Diskussionspunkte bündelt. Dieser Themenkatalog wird mit dem BfS laufend erörtert, aktualisiert und mit Prioritäten versehen. Schwerpunkte sind dabei zunächst Prüfanforderungen an Rundgebinde (Stapeldruckprüfung), die Aktualisierung von verwendeten Normen (z.B. ISO 1496-1), der Umgang mit Behälterbeschädigungen (z.B. Abplatzungen bei Betonbehältern), Spezifikationen zu formstabil fixierten Abfällen und Begrifflichkeiten zum Qualitätsmanagement. Dieser Beitrag erläutert die Motivation, Hintergründe und Zielstellungen der laufenden Arbeiten und präsentiert den gegenwärtigen Bearbeitungsstand hinsichtlich der Konkretisierung behälterspezifischer Aspekte in den Endlageranforderungen. Die Themen Stapeldruckprüfung von Rundgebinden und Begrifflichkeiten zum Qualitätsmanagement bilden hierbei die Schwerpunkte. T2 - KONTEC 2013 - 11. Internationales Symposium 'Konditionierung radioaktiverBetriebs- und Stilllegungsabfälle' CY - Dresden, Germany DA - 13.03.2013 PY - 2013 IS - Sektion 4 / Vortrag 031 SP - 727 EP - 744 AN - OPUS4-28914 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kasparek, Eva Maria A1 - Völzke, Holger A1 - Scheidemann, Robert T1 - Simulation of shock absorbing materials loaded by drop weights T1 - Simulation von stoßdämpfenden Werkstoffen unter dem Aufprall von Fallgewichten N2 - Zur numerischen Simulation von Transport- und Lagerbehältern für radioaktive Stoffe unter mechanischen Unfallbedingungen sind geeignete Materialmodelle und zugehörige Parametersätze für alle relevanten Behälterbauteile und den Aufpralluntergrund sowie gegebenenfalls für weitere am Störfall beteiligte Komponenten erforderlich. Sie bilden eine wesentliche Grundlage um für unterschiedliche Belastungsvarianten und Temperaturen zuverlässige Berechnungsergebnisse zu ermitteln, die umfangreiche experimentelle Erprobungen zumindest in Teilen ersetzen und damit einen zentralen Bestandteil von sicherheitstechnischen Nachweisen in gefahrgut- und atomrechtlichen Zulassungs- und Genehmigungsverfahren bilden können. Für die Auslegung der Behälter von besonderer Bedeutung ist die Effizienz der eingesetzten energieabsorbierenden Elemente, wie beispielsweise Stoßdämpfer am Behälterdeckel oder -boden bzw. äquivalente Strukturen auf oder im Fundament von Zwischen- und Endlagern. Diese Bauteile, die häufig aus Holz, Polyurethan (PU) - Schaum oder Dämpferbeton hergestellt werden, erfahren beim Auf- oder Anprall erhebliche plastische Deformationen, deren Verteilung und Größenordnung u.a. von der Belastungsgeschwindigkeit, dem Belastungsverlauf und der Temperatur bestimmt werden. Die Berücksichtigung dieser Faktoren in dynamischen Finite Elemente (FE) Berechnungen, die den heutigen Stand der Simulationstechnik repräsentieren, setzt eine systematische Datenbasis für den stoßdämpfenden Werkstoff voraus und die Implementierung dieser Informationen in numerischen Materialformulierungen. An der BAM wird seit Ende 2008 im Rahmen des vom BMBF geförderten Forschungsvorhabens ENREA (Entwicklung rechnerischer Analysemethoden für stoßdämpfende Strukturen beim Anprall oder Absturz von Abfallgebinden) die experimentelle Bestimmung derartiger Daten sowie die Anpassung und teilweise Neuentwicklung geeigneter Materialmodelle betrieben. T2 - KONTEC 2013 - 11. Internationales Symposium 'Konditionierung radioaktiverBetriebs- und Stilllegungsabfälle' CY - Dresden, Germany DA - 13.03.2013 KW - Polyurethane foam KW - Spruce KW - Guided drop tests KW - Material models KW - Fem KW - Strain rate sensitivity KW - Temperature sensitivity PY - 2013 IS - Sektion 4 / Vortrag 031 SP - 781 EP - 787 AN - OPUS4-28871 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kasparek, Eva Maria A1 - Völzke, Holger A1 - Scheidemann, Robert T1 - Simulationen von stoßdämpfenden Werkstoffen unter dem Aufprall von Fallgewichten T2 - KONTEC 2013 - 11. Internationales Symposium 'Konditionierung radioaktiverBetriebs- und Stilllegungsabfälle' CY - Dresden, Germany DA - 2013-03-13 KW - PU-Schaum KW - Fichtenholz KW - Geführte Fallversuche KW - Materialmodellierung KW - Dehnratenabhängigkeit KW - Temperatursensitivität PY - 2013 IS - Sektion 4 / Vortrag 031 SP - 774 EP - 780 AN - OPUS4-28872 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Patrick P. A1 - Schnürmacher, M. A1 - Bennetts, V.H. A1 - Lilienthal, A.J. A1 - Bartholmai, Matthias A1 - Schiller, J.H. T1 - A probabilistic gas patch path prediction approach for airborne gas ource localization in non-uniform wind fields N2 - In this paper, we show that a micro unmanned aerial vehicle (UAV) equipped with commercially available gas sensors can address environmental monitoring and gas source localization (GSL) tasks. To account for the challenges of gas sensing under real-world conditions, we present a probabilistic approach for GSL that is based on a particle filter (PF). Simulation and real-world experiments demonstrate the suitability of this algorithm for micro UAV platforms. T2 - ISOEN 2013 - 15th International symposium on olfaction and electronic nose CY - Deagu, South Korea DA - 02.07.2013 KW - Autonomous micro UAV KW - Chemical and wind sensing KW - Gas source localization KW - Particle filter PY - 2013 IS - Symposia / Applications of remote and local gas sensing ... SP - 15 EP - 16 AN - OPUS4-28878 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Patrick P. A1 - Bartholmai, Matthias T1 - Mikrodrohne zur Gefährdungsbeurteilung im Einsatz in Gasfreisetzungsszenarien N2 - Systementwicklung und Validierung o Motivation o Stand der Technik o Realisierung o Systemkomponenten o Integration o Gastransport o Windvektorbestimmung Anwendungsbeispiele o Mikrodrohne im Einsatz o Lokalisierung von Emissionsquellen o Erstellung von Gasverteilungskarten T2 - KAT 14 - 14. Berliner Katastrophenschutzforum CY - Berlin, Germany DA - 12.09.2013 KW - Mikrodrohne KW - Gefährdungsbeurteilung KW - Gasfreisetzung PY - 2013 SP - 1 EP - 22 AN - OPUS4-29093 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scholz, Christian A1 - Wäsche, Rolf T1 - Stick-slip and wear behavior of ceramic and polymer materials under reciprocating sliding conditions N2 - In many technical applications not only the actual friction coefficient is of importance, but rather the constancy relevant for the functionality. Due to inconstant ffiction values, positioning processes can be substantially influenced as well as vibrations can be induced. The appearance of this tribological effect, named stick-slip, depends on different factors such as sliding speed, relative humidity and ambient temperature occurring primarily after long operating periods. Beside ambient conditions the choice of materials in contact is the main influencing factor of an inconstant coefficient of friction during operating. Certain polymers are well known for their stick-slip tendencies in technical applications. These are on the one hand different modifications of PTFE (polytetrafluoroethylene) reinforced with glass fibers, bronze or graphite and on the other hand thermoplastics such as PE (polyester) or Pf (polyimide). The difference between static and dynamic values of the ffiction force is decisive for stick-slip phenomena. Furthermore, the stick-slip tendency of polymers strongly depends on the elastic material properties. Main softening material areas, which can be found in the contact, represent particularly vulnerable areas. The high friction value in the contact area decreases in most cases by increasing sliding speeds. However, beside polymers ceramic materials can also offer tendencies to stick-slip motion. Klaffke et al. already investigated the influence of ceramic materials on the stick-slip behavior in. T2 - WTC 2013 - 5th World tribology congress CY - Torino, Italy DA - 08.09.2013 KW - Stick-slip KW - Sliding speed KW - Polymers KW - Ceramics KW - Humidity PY - 2013 SP - 1 EP - 4 AN - OPUS4-29091 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scholz, Christian A1 - Woydt, Mathias T1 - The influence of high toughness silicon steels on applications demanding low friction and high load carrying capacity N2 - Highly concentrated or loaded contacts in powertrain and gear applications offer significant weight savings in C02 emissions. Today, thin film coatings, alternative base oils and new additives are populär as working fields and strategies of OEMs to realize low friction tribosystems. Especially the automotive industry anticipates environmental and performance benefits in applying light-weight construction of mechanical parts, for instance in gears and engines. Light-weight strategies increase the contact stresses above 2.14 GPa (or FZG load stage 14) due to the reduction of component sizes. These demands directly raise questions about the suitability of the most promising technical solution. Alternative steels with improved mechanical properties, i.e. toughness values, which offer low coefficients of friction, optimal resistance to high contact pressure and potential to apply low friction surface coatings representing a valid alternative to conventional gear steels. Traditional bearing and gear steels, such as 100Cr6 (SAE E52100) or 16MnCr5 (1.7131) have reached their mechanical limits at contact pressures above FZG load stage 14. T2 - WTC 2013 - 5th World tribology congress CY - Torino, Italy DA - 08.09.2013 KW - Slip-rolling KW - Silicon steel KW - DLC KW - High load KW - Gear steel PY - 2013 SP - 1 EP - 4 AN - OPUS4-29092 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sklorz, Christian T1 - Fire testing N2 - The phenomenon whereby the tank fails in a fire is described as a BLEVE. BLEVE Stands for boiling liquid expanding vapour explosion. This describes the sudden Vaporisation of a boiling, liquid under pressure followed by ignition. BLEVE are very complex phenomena which are influenced by a number of factors. T2 - Source term characterization of the consequences of storage tank aggressions (STO-AVT-VKI Lecture series 2012/13 - AVT 219) CY - Brussels, Belgium DA - 04.06.2013 KW - BLEVE KW - Storage tank KW - Fire protection coating PY - 2013 N1 - Serientitel: STO-AVT-VKI Lecture Series 2012/13 – Series title: STO-AVT-VKI Lecture Series 2012/13 SP - 1 EP - 11 AN - OPUS4-28927 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lenke, Karoline A1 - Hentschel, Yvonne A1 - Trappe, Volker T1 - Multiaxially loaded short fibre polyamide: a contribution to non-destructive evaluation of micro cracking and damage evolution N2 - Short fibre reinforced thermoplastics are increasingly used in automotive applications because of their potential for light weight design and cost efficient manufacturing by injection moulding. The fibre orientation, tuneable in the production process, defines the degree of anisotropy which causes different damage behaviour depending on the multiaxial stress state. Therefore, the multiaxial damage behaviour, based on micro cracking, is analysed by combining mechanical loading tests and non-destructive X-ray refractometry. T2 - ICCM19 - 19th International conference on composite materials CY - Montreal, Canada DA - 28.07.2013 KW - Short fiber reinforced composites KW - Multiaxial loading KW - Non-destructive testing KW - X-ray refraction KW - Damage mechanics PY - 2013 N1 - Geburtsname von Lenke, Karoline: Metzkes, K. - Birth name of Lenke, Karoline: Metzkes, K. SP - 5725 EP - 5733 AN - OPUS4-29004 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Qiao, Linan A1 - Kasparek, Eva Maria A1 - Völzke, Holger A1 - Zencker, Uwe A1 - Scheidemann, Robert T1 - Development of a finite element model for damping concrete under severe impact loads N2 - Finite element analysis (FEA) has been carried out for investigation of damping concrete under different impact loading conditions with a built-in material model and damage criteria available in FEA code ABAQUS. At first, all parameters for the selected material model had been derived from compression Tests of cubic specimens. After that, a validation was carried out with different static and dynamic penetration tests. Finally, a 5 meter real drop test with a 23 Mg cylindrical cask could successfully be simulated. T2 - PATRAM 2013 - 17th International symposium on the packaging and transportation of radioactive materials CY - San Francisco, CA, USA DA - 18.08.2013 PY - 2013 SP - Session D, Paper 127, 1 EP - 10 PB - Omnipress AN - OPUS4-29110 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dorgerloh, Ute T1 - Auswirkungen der externen Qualitätssicherung auf die Altlastenbearbeitung im Land Berlin N2 - Das Monitoring von Grundwasser erstreckt sich über Zeiträume von mehreren Jahren. Die analytischen Arbeiten der Laboratorien liefern die Datenbasis im Rahmen der Monitoringkampagnen und sind daher von maßgeblicher Bedeutung für den Erfolg des gesamten Projektes. Nicht selten sind auch Entscheidungen großer finanzieller Tragweite von der Qualität der analytischen Arbeiten abhängig. Daher müssen an die Probenahme und die Ausführungen der Analytik höchste Anforderungen für die Qualitätsstandards gestellt werden. Der Nachweis einer gültigen Akkreditierung ist Voraussetzung für die Durchführung der Laborarbeiten in hoher Qualität, allerdings keineswegs ausreichend als alleiniges Kriterium. Bei einer Akkreditierung nach IS017025 liegt der Schwerpunkt auf der Dokumentation des Managementsystems, nicht auf der Durchführung der eigentlichen Laborarbeiten. Die Qualität der Laborarbeiten wird im Rahmen der Akkreditierung über die Anwendung des Qualitätssicherungssystems sowie über die Teilnahme an Ringversuchen oder Eignungstests nachgewiesen. Die BAM ist 1998 vom Bundesamt für vereinigungsbedingte Sonderaufgabe (BvS) und dem Berliner Senat beauftragt worden, ein Konzept zur externen Qualitätssicherung im Ökologischen Großprojekt Berlin, für die Laboranalytik zu erarbeiten und umzusetzen. An ausgewählten Beispielen werden die einzelnen Teilschritte der Qualitätssicherungsmaßnahmen und die Effekte auf das Grundwassermonitoring dargestellt f1]. Die Maßnahmen zur externen Qualitätssicherung sind jedoch keine Einbahnstraße in Richtung Laborpraxis. Die Laboratorien sind gehalten, die Quantifizierung der Parameter in den Grundwasserproben nach Normverfahren (DEV-Reihe) durchzuführen. Da die BAM in die Erarbeitung der Normen (DIN, ISO) involviert ist, besteht die Möglichkeit der direkten Einflussnahme auf die Inhalte künftiger Normen (E DIN 38407 F43: 2013, VOC mit HS-GC/MS). Aber auch die Aktualität bestehender Normen wird durch Anwendungsbeispiele untermauert und ausgebaut (EN ISO 5667-3: 2013, Probenkonservierung) oder in Frage gestellt (DIN 38413 P2: 1988, VC-Bestimmung). Zum aktuellen Stand der Normung bezüglich der Bestimmung der organischen Parameter in Grundwasser wird eine Übersicht gegeben. T2 - Altlastensymposium 2013 CY - Berlin, Germany DA - 29.06.2013 KW - Grundwassermonitoring KW - Qualitätssicherung KW - Ökologisches Großprojekt Berlin PY - 2013 SP - 99 EP - 107 CY - Berlin AN - OPUS4-29138 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Linke, B. A1 - Schulze, S. A1 - Kranzmann, Axel T1 - Corrosion in pipe steels exposed to supercritical CO2 during carbon capture and storage CCS N2 - The CCS technique involves the compression of emission gasses in deep geological layers. To guarantee the safety of the site, CO2-corrosion of the injection pipe steels has to be given special attention when engineering CCS-sites. To get to know the corrosion behaviour samples of the heat treated steel 1.72252CrMo4, used for casing, and the stainless injection-pipe steel 1.4034 X46Cr13 were kept at T=60 °C and ambient pressure as well as p=100 bar for 700 h - 8000 h in a CC 2-saturated synthetic aquifer environment similar to possible geological on-shore CCS-sites in the northern German Basin. The isothermal corrosion behaviour obtained by mass gain of the steels in the gas phase, the liquid phase and the intermediate phase gives surface corrosion rates around 0.1 to 0.8 mm/year at ambient pressure and much lower about 0.02 to 0.2 mm/year at 100 bar where the CO 2 is in its supercritical state. Severe pit corrosion with pit heights around 4.5 mm are only located on the 42CrMo4 steel. Main phase of the continuous complicated multi-layered carbonate/oxide structure is siderite FeCO 3 in both types of steel. T2 - EUROCORR 2011 - Developing solutions for the global challenge CY - Stockholm, Sweden DA - 04.09.2011 KW - Steel KW - Pipeline KW - Corrosion KW - Carbonate layer KW - CCS KW - CO2-storage PY - 2011 SP - Paper 1044-1 EP - Paper 1044-8 AN - OPUS4-28008 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Glombitza, F. A1 - Berger, Wolfgang A1 - Kothe, E. A1 - Ondruschka, J. A1 - Pinka, J. A1 - Schippers, A. A1 - Willscher, S. A1 - Zehnsdorf, A. A1 - Brandl, H. ED - Schlömann, M. ED - Schippers, A. T1 - Rückstände aus Industrie und Umwelt - Aufbereitung mittels Geobiotechnologie? N2 - Um den Bedarf der Wirtschaft an Rohstoffen und Energie zu decken, werden ständig neue Rohstofflagerstätten erschlossen. Zusätzlich bemüht man sich darum, zumindest einen Teil der Rohstoffe wieder zu verwerten (Recycling). Der Erfolg hängt erheblich davon ab, wie gut es gelingt, die verschiedenen Stoffe voneinander zu trennen; diese Trennprozesse sind gegenwärtig immer noch unvollkommen. Dadurch fallen beim Recycling Reststoffe an, die noch erhebliche Mengen an Wertstoffen aufweisen. Besonders die Rückstände aus älteren Gewinnungstechnologien enthalten aus heutiger Sicht Konzentrationen, die zum Teil höher als in abbauwürdigen Erzen sind. Des-halb sieht die OECD die Erhöhung der Effizienz bei der Ressourcennutzung als eine der dringendsten Herausforderungen PY - 2013 SP - 23 EP - 28 AN - OPUS4-27948 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Linke, B. A1 - Schulze, S. A1 - Kranzmann, Axel T1 - Static and dynamic long term corrosion experiments in CCS-conditions N2 - Dealing with first corrosion screening experiments to predict the reliability and safety of Germanys first Carbon Capture and Storage site in the northern Bassin of Germany, northwest of the Capital Berlin, laboratory experiments have been established to simulate the particular conditions at T=60 °C, highly saline aquifer water similar to 'Stuttgart Aquifer', but only at ambient pressure. With mounting 2 independent full 2-grade titanium autoclave systems (running up to 250 bar and 300 °C) pressures up to p=100 bar are possible. In 2010 a specific corrosion chamber of 2-grade titanium working up to 100 °C, flowing aqui fer water with different gas mixtures was designed to fit to a high cycle fatigue testing machine. Long term fatigue experiments simulating fatigue crack growth under corrosive environments will soon start. These experiments may not only help engineering a CCS site, but results can be used to improve the maintenance of geothermal energy production sites, especially moved parts such as pumps and shafts. T2 - EUROCORR 2011 - Developing solutions for the global challenge CY - Stockholm, Sweden DA - 04.09.2011 KW - CO2 KW - Static corrosion KW - High cycle fatigue KW - Steel KW - CCS KW - CO2-storage KW - Corrosion PY - 2011 SP - 1 EP - 7 (Paper 1087) AN - OPUS4-28009 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Loughery, Z. A1 - Goedecke, Thomas T1 - Analysis of UN/DOT for the stacking of dangerous goods N2 - The purpose of this paper Is to demonstrate how the different interpretatlons of test Standards can lead to different results. For this study the United Nations (UN) stacking recommendation was examined. The critlcal points in the UN/DOT recommendation studied were guided or unguided compression, and the use of the stacking fixture. Locallzed stresses were analyzed using Digital Imaging Correlation (DIC). The positional tolerance of a packaging was also studied during unguided compression. During unguided compression the posltions of the jerricans were moved 1 cm in each direction from the center. The different positlons showed that was possible for a change in the deflection by 1.3 cm dependlng on the position. The DIC test was used to Show how stress concentrations form and the changes in the locallzed stress with guided and unguided compression. The DIC revealed differences in where and when the areas of higher stress would form. A guided and unguided compression test will give different results and change how stress concentrations form. The Position of the jerrlcan whlle using unguided compression methods will change the overall deflection and the locallzed stresses. These different acceptable methods will produce different results whlch could mean the dlfference between a failure and a package survlving the test. T2 - ISTA TransPack Forum CY - Orlando, FL, USA DA - 25.03.2013 KW - Position KW - Compression KW - Unguided KW - Guided KW - UN stacking test KW - DIC PY - 2013 SP - 1 EP - 13 AN - OPUS4-28092 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bletzer, Claus Wilhelm A1 - Nehrig, Marko A1 - Feldkamp, Martin A1 - Wille, Frank A1 - Völzke, Holger T1 - Druckaufbau in Behältern mit feuchtem Inventar N2 - Beim Betrieb von Kernkraftwerken fallen kontaminierte feuchte Abfallstoffe, wie z. B. Ionenaustauscherharze an, die in Transport- und Lagerbehältern der Entsorgung zugeführt werden. In Deutschland ist die BAM die zuständige Behörde für die Bauartprüfung von Typ B-Versandstücken. Im Zulassungsverfahren wird die Einhaltung der Schutzziele solcher Verpackungen überprüft. Basis für die Bewertung sind hierbei nationale und internationale gesetzliche Grundlagen sowie Regularien, welche in direkter Linie auf den IAEA SSR-6 [1] basieren. Die BAM ist ebenfalls im Rahmen einer Verwaltungsvereinbarung durch das BfS mit der Behälterbauartprüfung sowie der Beurteilung der qualitätssichernden Maßnahmen auf Grundlage von Kapitel 7 in [3] beauftragt. Typ-B(U) Verpackungen dienen zur Aufnahme verschiedenster radioaktiver oder radioaktiv kontaminierter Inhalte wie Brennelemente, Core-Bauteile, Rückbaurückstände oder belasteter Reinigungs- und Hilfsstoffe. In den meisten Fällen werden trockene bzw. getrocknete Inhalte verpackt. Potentiell feuchte oder nasse Inhalte wie z.B. Verdampferkonzentrate werden oftmals innerhalb der Verpackung getrocknet und können somit als trockene Inhalte behandelt werden. Beladene Ionenaustauscherharze werden i.d.R. mittels Transportwasser in die Verpackung eingespült und nur entwässert, aber nicht getrocknet. Die BAM war bereits in verschiedenen Zulassungsverfahren für Behälter mit feuchtem radioaktivem Inventar involviert. Bezüglich des Konrad Endlagers sind solche Verpackungen für feuchte, nicht Wärme entwickelnden Inhalte in der Regel als „Störfallfest verpackte Abfälle der Abfallbehälterklasse II [ABK II] mit spezifizierter Leckrate“ klassifiziert. In diesem Beitrag soll direkt Bezug zu den thermischen Prüfungen genommen werden. Im Transportfall sind hierbei die Unfallbeförderungsbedingungen zu unterstellen, die neben den mechanischen Prüfungen ein den Behälter vollständig einhüllendes Feuer von mindestens 800°C über 30 Minuten sowie der notwendigen Abkühldauer vorschreiben. Für eine geplante Endlagerung der Behälter ist im Zuge der Endlager-Bauartprüfung eine Branddauer von 60 Minuten mit nachfolgender 24-stündiger Abkühlphase unter abweichenden Randbedingungen gegenüber den verkehrsrechtlichen Regelwerksanforderungen zu beachten ([2] Kap. 5.3.). Bei einer möglichen Vorgehensweise zur Bestimmung des Druckaufbaus in einem Behälter aus den vorgeschriebenen Feuertests wird zuerst die Temperaturverteilung im Inhalt über den Zeitraum des Brands sowie der Abkühlphase berechnet. Der hier betrachtete Inhalt, der lediglich entwässert, aber nicht getrocknet ist, besteht sowohl aus gesättigtem Ionenaustauscherharz als auch aus einem geringen Anteil an freiem Wasser. Die Verdampfung von Wasser ist dabei ein kritischer Prozess der zum Druckaufbau im Behälter führt. Zur Einschätzung der aus dem thermischen Lastfall resultierenden Beanspruchungen des Behälters bis hin zur Gefährdung seiner Dichtheit und Integrität können sowohl rechnerische, als auch experimentelle Methoden Anwendung finden. Während sich die durch eine Brandbeanspruchung einstellenden Temperaturen in der Verpackung relativ genau berechnen lassen, erweist sich die Bestimmung der Temperatur- und Druckverteilung im Inventar aufgrund des komplexen thermischen und strömungsdynamischen Verhaltens als Herausforderung. Dabei ist der Wärmeübergang von der Behälterinnenwand in das Inventar sowie das thermische Verhalten des Inventars als inhomogen zu erhitzendes Gemisch aus Feststoffen, Fluiden (z.B. Wasser) und Gasen sehr komplex. Diese Vorgänge bestimmen jedoch den resultierenden und für die Sicherheitsbewertung maßgebenden Druckaufbau im Behälterinnenraum. Unter Berücksichtigung von Konvektion, Wärmeleitung und -strahlung werden thermische Zustände für den gewählten generischen Behälter aufgezeigt und die Effekte hinsichtlich Verdampfung und Druckaufbau erklärt. Anschließend werden zwei Ansätze zur Bestimmung des Partialdrucks durch Verdampfung im Behälter aufgezeigt. Para 663 und Para 664 der IAEA SSR-6 [1] der Transportbedingungen besagen, das - je nach Auslegung - der Feuertest bereits mit einem Innendruck von bis zu 700 kPa begonnen wird. Die beim Feuertest entstehenden Überdrücke müssen dann zum max. Auslegungsdruck hinzugefügt werden und der Behälter muss den Nachweis der Integrität mit den durch die Hitze reduzierten Werkstoffkennwerten des Behälters (Körper, Deckel, Verschlusssystem, Dichtung) nach der Vorschädigung durch die mech. Unfalltests erbringen. Bezüglich der Endlagerung besagt die Endlagerungsbestimmung [3] in Kap. 7.1.4.2.4, dass das “…Abfallprodukt so beschaffen sein muss, das bei der gemäß Unterkapitel 7.1.5.6 durchzuführenden thermischen Prüfung der maximal auftretende Innendruck 15 bar beträgt.”. T2 - KONTEC 2013 - 11. Internationales Symposium 'Konditionierung radioaktiverBetriebs- und Stilllegungsabfälle' CY - Dresden, Germany DA - 13.0,3.2013 KW - Druckaufbau KW - Radioaktive Abfälle KW - Endlager PY - 2013 IS - Sektion 4 / Vortrag 031 SP - 1 EP - 11 AN - OPUS4-28094 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bletzer, Claus Wilhelm A1 - Nehrig, Marko A1 - Feldkamp, Martin A1 - Wille, Frank A1 - Völzke, Holger T1 - Pressure build up in casks containing wet waste T2 - KONTEC 2013 - 11. Internationales Symposium 'Konditionierung radioaktiverBetriebs- und Stilllegungsabfälle' CY - Dresden, Germany DA - 2013-03-13 KW - Pressure build up KW - Radioactive waste KW - Disposal PY - 2013 IS - Sektion 4 / Vortrag 031 SP - 1 EP - 10(?) AN - OPUS4-28095 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hönig, D. A1 - Schneider, S. A1 - Domnick, R. A1 - Belzner, M. A1 - Beck, Uwe A1 - Hertwig, Andreas A1 - Stephanowitz, Ralph A1 - Weise, Matthias T1 - Optical layer systems for product authentication: interference, scattering, light diffusion and ellipsometric encoding as public, hidden and forensic security features N2 - Embedding of information on surfaces is state of the art for identification testing in which public, hidden and forensic features are used. In many instances, the legal authentication of a product, a material or a document is required. Among the surface-based encoded labels, bar codes and data matrices are most frequently applied. They are publicly visible. The material itself is irrelevant, only a sufficient optical contrast is required. However, a strong material dependence of the label can be achieved by means of Fabry-Perot layer stacks. Stack designs are described with regard to all three security levels: public features (e.g. color and tilt effect) perceptible by the human eye, hidden features (e.g. optical response in a given spectral range) detectable by commonly available instruments and forensic features (ellipsometric quantities Ψ and Δ as a function of wavelength λ and angle of incidence AOI) only detectable by sophisticated instruments. Regarding material-correlated authentication, ellipsometric quantities Ψ and Δ are used as encoded forensic features for the first time. Hence, Fabry-Perot layer stacks as information carriers in combination with imaging ellipsometry as optical read-out system provide all-in-one anti-counterfeiting capabilities. T2 - PSE 2012 - 13th International conference on plasma surface engineering CY - Garmisch-Partenkirchen, Germany DA - 10.09.2012 KW - Fabry-Perot layers KW - Ellipsometry KW - Anti-counterfeiting PY - 2012 UR - http://www.pse-conferences.net/tl_files/pse2012/abstractupload/PSE2012-PO1001-ext.pdf SP - 1 EP - 4 AN - OPUS4-27304 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beck, Uwe A1 - Hielscher, Stefan A1 - Weise, Matthias A1 - Mix, Renate A1 - Lerche, D. A1 - Rietz, U. T1 - Progress in quantitative adhesion testing of films and coatings by means of centrifuge technology - present state of the art N2 - Standardised conventional adhesion tests are time-consuming single-sample tests. Moreover, except for the pull-off test, all these tests provide only qualitative or semi-quantitative (ranking, respectively measurement of an adhesion-correlated quantity) information on adhesion. Sometimes, adhesion is evaluated even under compressive stress conditions (e.g. cross-cut and scratch test), which itself is a contradiction to adhesive strength as defined in terms of tensile force per area. For optical coatings it has been shown that the pull-off test in a centrifuge is definitely a promising alternative with respect to the reliable, fast and quantitative determination of adhesive strength in N/mm2. The force-controlled centrifuge test is the only multiple-sample test which provides reliable quantitative information on the adhesive strength in agreement with DIN EN 15870 and DIN EN ISO 4624 on a statistical basis for up to eight samples simultaneously tested under identical testing conditions. T2 - PSE 2012 - 13th International conference on plasma surface engineering CY - Garmisch-Partenkirchen, Germany DA - 10.09.2012 KW - Adhesion KW - Centrifuge test KW - Plasma modification KW - Tensile strength PY - 2012 UR - http://www.pse-conferences.net/tl_files/pse2012/abstractupload/PSE2012-OR2601-ext.pdf SP - 1 EP - 4 AN - OPUS4-27305 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hörold, Andreas A1 - Schartel, Bernhard A1 - Trappe, Volker A1 - Korzen, Manfred T1 - An intermediate-scale fire testing approach on the structural integrity of lightweight materials N2 - Carbon or glass über composites and Sandwich structures, the lightweight materials of choice for aviation, naval, offshore and construction show an enormous energy saving potential. Their combination of excellent specific mechanical properties, high corrosive resistance and thermal insulation properties in combination with various adoptable fabrication techniques leading to mass and fuel cost reduction. The most limiting single factor for a wider use of fibre reinforced plastics (FRP) in particular as elements for structural application is believed to be their fire behaviour (Mouritz and Gibson, 2006). FRPs promote burning by themselves consuming the stabilizing polymeric matrix while embedded fibers (glass, carbon) persisting the flame (Mouritz et ah, 2006). Already at elevated temperatures (100 - 200 °C) the matrix softens with a loss in mechanical properties (Perret et al., 2011, Mouritz and Gibson, 2006). For this reason the stability of the structural component is decreased severely. Fire behavior becomes the major hazard to worry about, increasingly demanding targetoriented investigation, suitable testing and tailored development. Experimental approaches in the bench-scale have been proposed to investigate the structural integrity in the past (La Delfa et al., 2009, Gibson et al., 2010, Seggewiß, 2011, Mouritz and Gardiner, 2002, Schartel et al.). Ascribed to the small-scale neither the mechanical properties nor the effects of fire may be represented satisfactorily. Flence, the task is to perform more realistic investigations under adequate compressive loads in fully developed fires, based on suitable specimen sizes. Also (La Delfa et al., 2009)) have announced that it is evident that larger scale test of composites are needed. The aim of this study is to present a developed intermediate-scale test setup to perform more realistic investigations (Hörold et al.). Mechanical loading is generated by a column furnace in terms of compression due to a more severe response of specimens in fire tests (Seggewiß, 2011, Gibson et al., 2012, Feih et al., 2008, Feih et al., 2007). An oil burner used to determine the burnthrough resistance of thermal/acoustic insulation materials provides fire directly onto one side of the specimen (Federal Aviation Administration, 2003). Generating a fully developed fire the NexGen burner offers a homogenous heat flux of ~ 180 kW/m2. The intermediate-scale is addressed by specimen sizes either 500 x 500 mm or 1000 x 500 mm with a maximum thickness of 50 mm. The specimen attachment is realized by a compression device that was designed to apply the compressive loads, figure 1. The test setup for specimens with component like dimensions allows realistic investigations up to structural failure in absence and presence of fire load. A first test series was carried out with different levels of loading while the fire remained unchanged. Failure mechanisms, temperature distributions, diversity of FRPs regarding fiber, matrix, lay-up and core as well as flame retardant Systems are in the scope of investigation. T2 - Fire and materials 2013 - 13th International conference and exhibition CY - San Francisco, CA, USA DA - 28.01.2013 PY - 2013 SP - 221 EP - 226 PB - Interscience Communications CY - London, UK AN - OPUS4-27782 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ellouz, Manel A1 - Völzke, Holger A1 - Protz, Christian T1 - Container safety assessment for the disposal of non-heat generating radioactive waste in the KONRAD repository T2 - 53rd INMM Annual meeting CY - Orlando, FL, USA DA - 2012-07-15 PY - 2012 SP - 1 EP - 9(?) AN - OPUS4-27217 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Habel, Wolfgang A1 - Krebber, Katerina T1 - Application of fiber-optic sensors for health monitoring purposes in geo-engineering T2 - 4th International forum on opto-electronic sensor-based monitoring in geo-engineering CY - Suzhou, China DA - 2012-10-11 KW - BOFDA KW - Fibre-optic sensor KW - Distributed sensor KW - Brillouin sensor KW - Polymer optical fibers (POF) KW - POF sensor KW - POF OTDR KW - Strain sensor KW - Technical textiles KW - Geotextiles KW - Geophone KW - Fabry-Perot sensor KW - Pile test KW - Impact KW - Acoustic wave PY - 2012 SP - 4 EP - 15 AN - OPUS4-27259 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Eichler, Thorsten T1 - Zu den sekundären Schutzmechanismen beim kathodischen Korrosionsschutz von Stahl in alkalischen Medien N2 - Die vorliegende Arbeit behandelt die Auswirkungen der sekundären Schutzmechanismen beim kathodischen Korrosionsschutz von Stahl in alkalischen Medien. Auf der Grundlage von Untersuchungen in künstlichen Betonporenlösungen wird ein Modell zur Wirkungsweise der sekundären Schutzmechanismen entwickelt. Die Ergebnisse belegen die wesentliche Bedeutung des Verhältnisses zwischen Chlorid- und Hydroxidionenkonzentration im Elektrolyten bezüglich der im System verbleibenden Korrosionsrate nach Abschalten des Schutzstroms sowie hinsichtlich der kathodischen Polarisierbarkeit des Schutzobjektes. Es konnte gezeigt werden, dass die Verringerung des Verhältnisses zwischen Chlorid- und Hydroxidionenkonzentration auf einen spezifischen Grenzwert zur nachhaltigen Verringerung der Korrosionsrate, um einen Faktor zwischen 10 und 1000, führend kann. Weiterhin belegen die Ergebnisse, dass durch den kathodischen Korrosionsschutz nur in Ausnahmefällen die Repassivierung des Schutzobjektes zu beobachten ist. Der zweite Teil der Untersuchungen befasst sich mit den messbaren Auswirkungen kathodischer Langzeitpolarisation auf das Korrosionsverhalten von Stahl in chloridhaltigen Mörtelprobekörpern. Hier konnte und praxisnahen Betriebsbedingungen gezeigt werden, dass signifikante Migrationseffekte auch bei verhältnismäßig geringer Feldstärke auftreten können. Weiterhin konnte die kathodische Polarisationskinetik als Funktion der während der Polarisation geflossenen Ladungsmenge dargestellt werden.---------------------------------------------------------------------------------------------------------------------------- The present work discusses the impact of the secondary protection mechanisms during cathodic protection of steel in alkaline media. On the basis of investigations in artificial concrete pore solutions a model was developed concerning the effectiveness of the secondary protection mechanisms. The results support the essential significance of the ratio between chloride and hydroxide ion in the electrolyte concerning the in the system remaining corrosion rate after switching off the protection current as well as regarding the polarisability of the object to be protected. It could be shown, that reducing the ratio between chloride and hydroxide ion concentration to a specific value results in a sustaining reduction of the remaining corrosion rate, of a factor between 10 and 1000. Further on the results prove that repassivation by cathodic protection was only observable in exceptional cases. The second part of the investigations deals with the measurable effects of cathodic long term polarisation on the corrosion behaviour of steel in chloride containing mortar specimens. It was possible to show under nearly practical conditions, that significant migration effects can occur even at comparably low field strengths. Further on the cathodic polarisation kinetics could be presented as function of the charge flown during polarisation. KW - Kathodischer Korrosionsschutz KW - Instandsetzung KW - Instandhaltung KW - Chlorinduzierte Korrosion KW - Stahlbeton KW - Elektrochemische Instandsetzungsverfahren KW - Lochkorrosion KW - Chlorid KW - Beton PY - 2012 SP - 1 EP - 169 CY - Aachen AN - OPUS4-27444 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Lang, Jacqueline A1 - Meyer-Plath, Asmus T1 - Charakterisierung von nanoskaligen Eigenschaften chemischer Stoffe als Grundlage für die Regulierung im Rahmen der Verordnung (EG) Nr. 1907/2006 (REACH) N2 - Die vorliegende Literaturarbeit zeigt auf, inwiefern die in der Verordnung 440/2008 EG enthaltenen Prüfnachweise für Nanomaterialien anwendbar sind. In einem ersten Teil werden die verschiedenen verwendeten Begriffe für Nanomaterialien erklärt und die Klassifizierung der Nanomaterialien erläutert. Daran schließen sich die Beschreibung der physikalisch-chemischen Eigenschaften von Nanomaterialien und die Charakterisierbarkeit der Nanoskaligkeit mit den in der Verordnung 440/2008 genannten Prüfmethoden an. Im letzten Teil werden die relevanten Eigenschaften von Nanomaterialien aus Sicht internationaler Institutionen beschrieben und die möglichen Bestimmungsmethoden aufgeführt. Abschließend wird analysiert, welche vorhandenen Prüfmethoden der Verordnung 440/2008 auf Nanomaterialien anwendbar sind und welche weiteren Eigenschaften im Rahmen einer Regulierung der Nanomaterialien geprüft werden sollten.---------------------------------------------------------------------------------------------------------------------------------- The presented literature documentation shows the applicability of the test methods listed in regulation EC 440/2008. The first part explains different terms and definitions of nanomaterials and the nanomaterials' classifications. Afterwards the physico-chemical properties of nanomaterials are described and the feasibility to characterise substances at nanoscale with the test methods listed in regulation 440/2008 is assessed. In the last part relevant properties of nanomaterials from the perspective of international institutions are listed and possible methods for the determination are given. Finally, it is analysed which test methods of the regulation EC 440/2008 are applicable to nanomaterials and which further properties should be investigated in the frame of the regulation of nanomaterials. KW - REACH KW - Nanomaterialien KW - Charakterisierung KW - Physikalisch-chemische Daten KW - Nanomaterials KW - Characterisation KW - Physico-chemical data PY - 2012 UR - http://www.baua.de/de/Publikationen/Fachbeitraege/F2261.pdf?__blob=publicationFile&v=3 SP - 1 EP - 112 CY - Dortmund AN - OPUS4-27383 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eichler, Thorsten A1 - Isecke, Bernd T1 - Kathodischer Korrosionsschutz von Stahl im Beton - Möglichkeiten und Grenzen mit praktischen Beispielen T2 - 23. Baupraktisches Informationsseminar für Auftraggeber, Planer und Ausführende von Instandsetzungsmaßnahmen CY - Bad Nauheim, Germany DA - 2012-11-07 KW - Kathodischer Korrosionsschutz KW - Instandsetzung KW - Instandhaltung KW - Chloridinduzierte Korrosion KW - Stahlbeton PY - 2012 SP - 15 EP - 19 AN - OPUS4-27453 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Prasad M, K. A1 - Wiggenhauser, Herbert A1 - Balasubramaniam, Krishnan T1 - Detection of honeycomb defects in reinforced concrete structures using acoustic pulse-echo methods and wavelet transforms N2 - Honeycombs/compaction faults occur in the concrete structures due to improper solidification of the concrete, which may reduce the strength of the concrete and also act as a passage for the water/acids that further corrodes the reinforcements. This paper explores about the acoustic pulse-echo techniques for the detection of honeycomb defects in a laboratory specimen located at the Federal Institute for Materials Research and Testing (BAM), Berlin. Since concrete is an inhomogeneous medium, the defect Signals are masked by the material noise due to large amount of scattering/ reflections of acoustic waves. A filtering method using the discrete wavelet transforms is applied on the ultrasonic time Signals for the better localization of defects. KW - Honeycomb defects KW - Acoustic pulse-echo methods KW - Wavelets transforms PY - 2011 SN - 0973-9610 VL - 10 IS - 3 SP - 53 EP - 59 PB - ISNT CY - Chennai AN - OPUS4-27631 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Akkerman, Floris T1 - Marktüberwachung für Ökodesign - Herausforderungen bei Industrieprodukten N2 - Die Ökodesignrichtlinie setzt einen Rahmen für vielfältige Anforderungen an Produkte. Ziel ist die Verringerung der Umweltauswirkungen über den gesamten Produktlebenszyklus. Dazu werden die vorgeschlagenen Produkte in Gruppen eingeteilt, Markt, Technik, Nutzerverhalten und bestehende Regelungen werden nach einer festen Methode ermittelt und Verbesserungspotenziale werfen identifiziert. Anhand von Szenarien, die das Vorgehen „weiter wie bisher" (BAU, business as usual) mit den Auswirkungen einer möglichen gesetzlichen Regelung vergleichen, wird eingeschätzt, ob eine solche Anforderung sinnvoll und lohnend ist. Die Entscheidung darüber, welche Regeln letztendlich gelten, trifft die EU-Kommission zusammen mit den Mitgliedsstaaten (Komitologieverfahren). Am Ende des Prozesses steht eine Verordnung der Kommission mit bindenden Mindestanforderungen für eine Produktkategorie. T2 - 11. Technischer Tag VEM CY - Wernigerode, Germany DA - 25.09.2012 KW - Energieeffizienz KW - Investitionsgüter KW - Marktüberwachung KW - Ökodesign PY - 2012 SP - 1 EP - 2 AN - OPUS4-27576 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bresch, Harald A1 - Meyer-Plath, Asmus A1 - Burgdorf, T. A1 - Packroff, R. A1 - Apel, P. A1 - Adolf, P. A1 - Jesse, A. A1 - Leuschner, C. A1 - Bosse, H. A1 - Dubbert, W. A1 - Epp, A. A1 - Gebel, T. A1 - Götz, M. A1 - Herzberg, F. A1 - Hornbogen, T. A1 - Kersten, N. A1 - Kneuer, C. A1 - Kujath, P. A1 - Pipke, R. A1 - Plitzko, s. A1 - Schlesier, K. A1 - Schröder, F. A1 - Schwirn, K. A1 - Sommer, Y. A1 - Tentschert, J. A1 - Völker, D. A1 - Wolf, T. T1 - 1. Bilanz zur gemeinsamen Forschungsstrategie der Ressortforschungseinrichtungen des Bundes 'Nanotechnologie - Gesundheits- und Umweltrisiken von Nanomaterialien' (2007 - 2011) KW - Nanotechnologie KW - Nanopartikel KW - Nanomaterial KW - Bundesoberbehörden KW - Forschungsstrategie PY - 2013 SP - 1 EP - 124 CY - Berlin AN - OPUS4-28538 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Herbrich, Uwe A1 - Nagelschmidt, Sven A1 - Weber, Wolfgang A1 - Wolff, Dietmar A1 - Völzke, Holger T1 - Die sicherheitstechnische Behälterbegutachtung für die trockene Zwischenlagerung bestrahlter Brennelemente aus Sicht der BAM N2 - Die Aufbewahrung von Kernbrennstoffen ist im Gesetz über die friedliche Verwendung der Kernenergie und den Schutz gegen ihre Gefahren (Atomgesetz-AtG) geregelt, insbesondere sind im § 6 AtG Regelungen für die Genehmigung zur Aufbewahrung außerhalb der staatlichen Verwahrung sowie deren Voraussetzungen enthalten. Als Voraussetzung zur Erteilung einer Genehmigung zur Aufbewahrung von Kernbrennstoffen ist u.a. durch die Antragstellerin die nach dem Stand von Wissenschaft und Technik erforderliche Vorsorge gegen Schäden durch dessen Aufbewahrung zu treffen. Das Bundesamt für Strahlenschutz (BfS) als Genehmigungsbehörde gemäß § 6 und § 23, Abs. 1, Nr. 4 AtG kann entsprechend § 20 AtG Sachverständige zur Prüfung der Genehmigungsvoraussetzungen hinzuziehen. Die BAM wird vom BfS in Genehmigungsverfahren nach § 6 AtG seit mehr als 30 Jahren mit der Beurteilung behälterspezifischer Fragen bei der Aufbewahrung von radioaktiven Stoffen in Behältern einer Bauart in einem (zentralen oder dezentralen) Zwischenlager beauftragt. Derzeit erfolgen solche behälterspezifischen Begutachtungen im Fachbereich 3.4 Sicherheit von Lagerbehältern der BAM. T2 - Jahrestagung Kerntechnik 2013 CY - Berlin, Germany DA - 14.05.2013 PY - 2013 SP - 1 EP - 6 AN - OPUS4-28585 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Feutlinske, Karl A1 - Wolff, Dietmar A1 - Völzke, Holger T1 - Sicherheitsbewertung von Lagerbehältern bei Auslaufen einer befristeten Zwischenlagergenehmigung N2 - Bei der sicherheitstechnischen Begutachtung der behälterspezifischen Aspekte nach Ablauf einer Zwischenlagergenehmigung ist entsprechend einer Neubeantragung zu verfahren. Die Sicherheitsbewertung erfolgt nach dem aktuellen Stand von Wissenschaft und Technik bei Berücksichtigung der zur Behälterbauart bereits vorliegenden Sicherheitsnachweise und Begutachtungsergebnisse sowie der physikalischen und chemischen Alterungseinflüsse der bisherigen Zwischenlagerung. Am Beispiel einer beantragten weiteren Zwischenlagerung nach Auslaufen einer auf 20 Jahre befristeten Genehmigung und dem notwendigen Behältertransport zu einem neuen Zwischenlager werden Erfahrungen bzgl. der durchgeführten Sicherheitsbewertung zur Erfüllung der Technischen Annahmebedingungen des neuen Behälterlagers dargestellt. T2 - Jahrestagung Kerntechnik 2013 CY - Berlin, Germany DA - 14.05.2013 PY - 2013 IS - Paper 8816 SP - 1 EP - 6 AN - OPUS4-28587 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Simone A1 - Deubel, Jan A1 - Werrel, Martin A1 - Raspe, Tina T1 - Welche stofflichen und energetischen Gefahren gehen von Wohnzimmerbränden aus? N2 - Welche stofflichen und energetischen Gefahren während und nach einem Wohnzimmerbrand auftreten können, werden im Rahmen dieses Vortrages vorgestellt. Im Mittelpunkt stehen dabei die Rauchgasentwicklung, die Wärmefreisetzung, die entstehenden Rauchgastemperaturen sowie die Rauchgaszusammensetzung. In den Einrichtungen der Gesellschaft für Materialforschung und Prüfungsanstalt für das Bauwesen Leipzig mbH (MFPA) wurden dazu fünf verschiedene Wohnzimmerbrandversuche durchgeführt. Die Modell-Zimmer wurden jeweils mit dem gleichen Mobiliar ausgestattet. Als Brandbeschleuniger kamen Benzin und Diesel als Gemisch zum Einsatz. Bei den Versuchen zeigte sich unter anderem, dass der Brandbeschleuniger deutlich die Zeit bis zum Flashover verkürzt. Aus den ermittelten Kennwerten zur Wärmefreisetzung und den Rauchgastemperaturen können Rückschlüsse auf die energetischen Gefahren abgeleitet werden. Die quantitative Erfassung toxischer Rauchgaskomponenten erfolgte mit Hilfe der Fourier-Transformations- Infrarot-(FTIR)-Spektroskopie. Die qualitative und quantitative Rauchgaszusammensetzung wurde dabei in der Brandraummitte, an der Brandraumöffnung, unter der Brandraumdecke und im Schlot ermittelt. Aus der Massenverlustrate und der quantitativen Rauchgasanalyse können Aussagen zur Rauchgastoxizität getroffen werden und die stofflichen Gefahren beurteilt werden. Das Wissen über die Bildung von energetischen und stofflichen Brandprodukten ermöglicht somit eine risikogerechte Beurteilung der Brandgefahren bei Raumbränden, auch in Hinblick auf die unterschiedlichen Brandphasen. T2 - Vfdb 2013 - 61. Jahresfachtagung CY - Weimar, Germany DA - 27.05.2013 KW - Brand KW - Rauchgasanalytik PY - 2013 SP - 771 EP - 787 CY - Altenberge AN - OPUS4-28628 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Komann, Steffen A1 - Droste, Bernhard A1 - Gröke, Carsten T1 - Qualitätssicherung und -überwachung bei Verpackungen für prüfpflichtige Versandstücke zur Beföderung radioaktiver Stoffe N2 - Ziel dieses Beitrages soll es sein, zum einen das Vorgehen bei der Erlangung einer Anerkennung zur qualitätsgesicherten Herstellung einer Verpackung für prüfpflichtige Versandstücke der zuständigen Behörde im Sinne des ADR Unterabschnittes 1.7.3 'Qualitätssicherung' darzustellen und zum anderen Probleme bei der Umsetzung der rechtsverbindlichen Vorschriften des Gefahrgutrechts aufzuzeigen. T2 - Jahrestagung Kerntechnik 2013 CY - Berlin, Germany DA - 14.05.2013 PY - 2013 IS - Sektion 5: Entsorgung radioaktiver Abfälle, Lagerung SP - 1 EP - 6 AN - OPUS4-28653 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reich, Franziska A1 - Pötzsch, Klaus-Michael T1 - Experimentell gestützte Untersuchungen zu brandschutztechnischen Maßnahmen im Gefahrguttransport N2 - Um das Risiko eines katastrophalen Versagens von Gefahrguttanks und deren Folgen zu mindern werden sicherheitstechnische Maßnahmen an der Bundesanstalt für Materialforschung und -prüfung (BAM) untersucht. Der Einsatz und die Dimensionierung von brandschutztechnischen Maßnahmen im Gefahrguttransport sind durch verkehrsträgerspezifische Vorschriften geregelt. Hiernach sind Gefahrguttanks für betriebliche Belastungen auszulegen. Bei dieser Auslegung werden unter Anderem Parameter, wie die Wanddicke eines Gefahrguttanks, stoffliche Aspekte des transportierten Gefahrguts und auch Betriebsdrücke berücksichtigt. Eine seit vielen Jahren bewährte Sicherheitsphilosophie ist es, Tanks oder druckführende Anlagen durch Sicherheitseinrichtungen gegen das unzulässige Überschreiten eines inneren Überdrucks zu schützen. Die regelkonforme Auslegung führt jedoch zu unterschiedlichen Sicherheitsniveaus in Europa und darüber hinaus. Denn hiernach werden Tanks nach zwei Philosophien befördert. Insbesondere betrifft dies die Ausrüstung der Tanks mit Druckentlastungseinrichtungen, wie Sicherheitsventile. Daraus ergeben sich Fragestellungen, die es im Rahmen der Untersuchungen in einem drittmittelgeförderten BMVBS-Projektes, zu beantworten galt: • Warum verkehren Tanks mit und ohne Sicherheitsventile? • Sind diese Sicherheitseinrichtungen auch in Unfallsituationen ausreichend, um die Temperatur und den Druck im Tank herabzusetzen? Bei den Untersuchungen des Forschungsprojektes wurde unter anderem die Zuverlässigkeit der Sicherheitseinrichtungen an Gefahrguttanks für den normalen Betrieb und für den Brandfall untersucht. Diese Untersuchungen zeigen, dass das Sicherheitsempfinden, welches Sicherheitsventile vermitteln, zu hinterfragen ist. T2 - Vfdb 2013 - 61. Jahresfachtagung CY - Weimar, Germany DA - 27.05.2013 KW - Gefahrguttanks KW - Transporttanks KW - Druckentlastungseinrichtung KW - Brandschutzbeschichtung PY - 2013 SP - 737 EP - 752 CY - Altenberge AN - OPUS4-28649 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wloka, Monika T1 - Erfolgreiche Audits zur Norm machen - Die überarbeitete DIN EN ISO 19011:2011 ist ein Leitfaden zur Auditierung von Managementsystemen. Welche Änderungen ergeben sich aus der Revision und an wen richtet sich die Norm? N2 - Im Dezember 2011 wurde die revidierte DIN EN ISO 19011 in ihrer deutschen Fassung veröffentlicht. Die Norm gibt Informationen zu Auditprinzipien, zur Erstellung von Auditprogrammen und zur Durchführung aller Arten von Audits von Managementsystemen. Während die Vorgängernorm nur auf Qualitätsmanagement- und Umweltmanagementsysteme ausgerichtet war, sieht diese überarbeitete Norm die Eignung für alle Managementsysteme vor. Sie ist eine spezielle Anleitung für alle, die interne Audits oder externe Audits planen und durchführen. Die überarbeitete Norm umfasst auch Ausführungen zur Kompetenz der Personen, die in die unterschiedlichen Phasen des Auditprozesses einbezogen sind – einschließlich der Vorbereitung, Leitung und Lenkung der Auditprogramme sowie der eigentlichen Durchführung der Audits (Auditoren und Auditteams). Die DIN EN ISO 19011:2011 ist somit das Grundlagendokument für die Auditierung. PY - 2013 VL - 1 SP - 12 EP - 13 AN - OPUS4-28650 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Friedrich, Jörg Florian A1 - Mix, Renate T1 - Combination of plasma-chemical and wet-chemical processes - a simple way to optimize interfaces in metal-polymer composites for maximal adhesion N2 - Different surface treatments of polypropylene (PP) were tested to improve the peel strength of aluminium-PP systems. Plasma exposure followed by chemical grafting of spacers with -SiOH endgroups and thin adhesion promoting layers deposited by aerosol-assisted DBD using aqu. solutions of classic polymers were compared. Both methods were effective, however, –SiOH terminated spacers effected no peeling also after ageing. T2 - ISPC 21 - 21st International Symposium on Plasma Chemistry CY - Cairns, QLD, Australia DA - 02.08.2013 KW - Adhesion polypropylene-aluminium KW - Tailored interface structures KW - Aerosol-assisted DBD PY - 2013 SP - Paper 549, 1 EP - 4 AN - OPUS4-28661 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Sipp, K. T1 - Der Einfluß von Kohlenstoff, Mangan und Silizium auf das Wachsen des Gußeisens PY - 1929 IS - IX SP - 40 EP - 63 PB - Springer CY - Berlin AN - OPUS4-28309 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Hansen, Max T1 - Der Einfluß von dritten Metallen auf die Konstitution der Messinglegierungen. I. Der Einfluß von Blei PY - 1929 IS - IX SP - 3 EP - 22 PB - Springer CY - Berlin AN - OPUS4-28293 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Göler, Frhr v. A1 - Sachs, Georg T1 - Untersuchungen an Kupfer und Messing PY - 1929 IS - IX SP - 22 EP - 29 PB - Springer CY - Berlin AN - OPUS4-28294 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmid, Erich A1 - Wassermann, G. T1 - Versuche zum Duraluminproblem PY - 1929 IS - IX SP - 29 EP - 37 PB - Springer CY - Berlin AN - OPUS4-28295 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hansen, Max T1 - Die Alterungshärtung der aluminiumreichen Silber-Aluminiumlegierungen PY - 1929 IS - IX SP - 37 EP - 39 PB - Springer CY - Berlin AN - OPUS4-28296 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Sieglerschmidt, H. T1 - Der Einfluß kleiner Zusätze von Kupfer und Nickel auf die Wärmeausdehnung und auf das Wachsen des Gußeisens PY - 1929 IS - IX SP - 63 EP - 68 PB - Springer CY - Berlin AN - OPUS4-28311 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmid, Erich T1 - Anordnung der Kristallite in Vielkristallen (Texturen) PY - 1929 IS - IX SP - 69 EP - 77 PB - Springer CY - Berlin AN - OPUS4-28312 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Karnop, R. A1 - Sachs, Georg T1 - Versuche über die Rekristallisation von Metallen. II. PY - 1929 IS - IX SP - 77 EP - 82 PB - Springer CY - Berlin AN - OPUS4-28313 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Friedrich Wilhelm A1 - Sachs, Georg T1 - Zur Kenntnis der Streckgrenze von Stahl PY - 1929 IS - IX SP - 82 EP - 88 PB - Springer CY - Berlin AN - OPUS4-28314 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Laute, K. A1 - Sachs, Georg T1 - Was ist Ermüdung? PY - 1929 IS - IX SP - 89 EP - 91 PB - Springer CY - Berlin AN - OPUS4-28315 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Eisenschitz, R. A1 - Rabinowitsch, B. A1 - Weissenberg, K. T1 - Zur Analyse des Formveränderungswiderstandes PY - 1929 IS - IX SP - 91 EP - 94 PB - Springer CY - Berlin AN - OPUS4-28316 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sachs, Georg T1 - Zur Ableitung einer Fließbedingung PY - 1929 IS - IX SP - 94 EP - 97 PB - Springer CY - Berlin AN - OPUS4-28317 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmid, Erich T1 - Festigkeit und Plastizität von Metallkristallen PY - 1929 IS - IX SP - 97 EP - 103 PB - Springer CY - Berlin AN - OPUS4-28318 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Boas, W. A1 - Schmid, Erich T1 - Über die Dehnung von Kadmiumkristallen PY - 1929 IS - IX SP - 103 EP - 115 PB - Springer CY - Berlin AN - OPUS4-28319 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ohshima, K. A1 - Sachs, Georg T1 - Röntgenuntersuchungen an der Legierung AuCu PY - 1930 IS - XIII SP - 129 EP - 135 PB - Springer CY - Berlin AN - OPUS4-28350 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sieglerschmidt, H. T1 - Untersuchung des Einflusses der Umwandlung auf die Wärmeausdehnung von Stählen unter besonderer Berücksichtigung der Änderung der Ausdehnungszahl beta PY - 1930 IS - XIII SP - 135 EP - 139 PB - Springer CY - Berlin AN - OPUS4-28351 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmid, Erich A1 - Vaupel, Otto T1 - Versuche an bewässerten Steinsalzkristallen PY - 1930 IS - XIII SP - 139 PB - Springer CY - Berlin AN - OPUS4-28352 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Blumenthal, Herbert T1 - Über ein Verfahren für die Trennung von Blei und Wismut PY - 1930 IS - XIII SP - 140 EP - 142 PB - Springer CY - Berlin AN - OPUS4-28353 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Wilhelm T1 - Elastische Messungen an Kupfer Mittels Martensscher Spiegel PY - 1930 IS - XIV SP - 3 EP - 7 PB - Springer CY - Berlin AN - OPUS4-28356 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Wilhelm T1 - Der Bruch gekerbter Zugproben PY - 1930 IS - XIV SP - 7 EP - 16 PB - Springer CY - Berlin AN - OPUS4-28357 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Wilhelm T1 - Statische Grundlagen zum Schwingungsbruch PY - 1930 IS - XIV SP - 17 EP - 22 PB - Springer CY - Berlin AN - OPUS4-28358 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sieglerschmidt, H. T1 - Apparat zur Messung der Querschnittsänderungen belasteter Stäbe PY - 1930 IS - XIV SP - 22 EP - 27 PB - Springer CY - Berlin AN - OPUS4-28359 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hansen, Max T1 - Zur Kenntnis des Vergütungsvorganges in Legierungen [Der Vorgang der Entmischung übersättigter beta(Cu-Zn)-Mischkristalle durch Alterung bei verschiedenen Temperaturen] PY - 1930 IS - XIII SP - 25 EP - 37 PB - Springer CY - Berlin AN - OPUS4-28330 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Frommer, L. A1 - Kuntze, Friedrich Wilhelm A1 - Sachs, Georg T1 - Der Einfluß von Poren auf die Festigkeit von Spritzguß PY - 1930 IS - XIII SP - 37 EP - 41 PB - Springer CY - Berlin AN - OPUS4-28331 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmid, Erich A1 - Wassermann, G. T1 - Röntgenographische Studien zum Vergütungsproblem I PY - 1930 IS - XIII SP - 41 EP - 46 PB - Springer CY - Berlin AN - OPUS4-28332 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wassermann, G. T1 - Zur Frage der molekularen oder atomaren festen Lösung einer Metallverbindung im Grundmetall PY - 1930 IS - XIII SP - 46 EP - 48 PB - Springer CY - Berlin AN - OPUS4-28333 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wassermann, G. T1 - Über die Vergütung einer Constructallegierung PY - 1930 IS - XIII SP - 48 EP - 50 PB - Springer CY - Berlin AN - OPUS4-28334 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ageew, N. A1 - Sachs, Georg T1 - Röntgenographische Bestimmung der Löslichkeit von Kupfer in Silber PY - 1930 IS - XIII SP - 50 EP - 55 PB - Springer CY - Berlin AN - OPUS4-28335 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hansen, Max T1 - Die Härte silberreicher Kupfer-Silberlegierungen (Bestimmung der Löslichkeit von Kupfer in Silber mit Hilfe von Härtemessungen) PY - 1930 IS - XIII SP - 55 EP - 58 PB - Springer CY - Berlin AN - OPUS4-28336 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald T1 - Arsen im Flußstahl PY - 1930 IS - XIII SP - 58 EP - 66 PB - Springer CY - Berlin AN - OPUS4-28337 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kurdjumow, G. A1 - Sachs, Georg T1 - Walz- und Rekristallisationstextur von Eisenblech PY - 1930 IS - XIII SP - 67 EP - 70 PB - Springer CY - Berlin AN - OPUS4-28338 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Karnop, R. A1 - Sachs, Georg T1 - Das Fließen von Metallkristallen bei Torsion PY - 1929 IS - IX SP - 116 EP - 122 PB - Springer CY - Berlin AN - OPUS4-28320 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Karnop, R. A1 - Sachs, Georg T1 - Fertigkeitseigenschaften von Kristallen einer veredelbaren Aluminiumlegierung PY - 1929 IS - IX SP - 122 EP - 129 PB - Springer CY - Berlin AN - OPUS4-28321 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Göler, Frhr v. A1 - Sachs, Georg T1 - Untersuchungen an Kristallen von beta-Messing PY - 1929 IS - IX SP - 129 EP - 132 PB - Springer CY - Berlin AN - OPUS4-28322 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Masima, M. A1 - Sachs, Georg T1 - Mechanische Eigenschaften von Messingkristallen PY - 1929 IS - IX SP - 133 EP - 143 PB - Springer CY - Berlin AN - OPUS4-28323 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Masima, M. A1 - Sachs, Georg T1 - Leitfähigkeit und Kaltverformung PY - 1929 IS - IX SP - 143 EP - 145 PB - Springer CY - Berlin AN - OPUS4-28324 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Masima, M. A1 - Sachs, Georg T1 - Dichte und Kaltverformung PY - 1929 IS - IX SP - 146 EP - 149 PB - Springer CY - Berlin AN - OPUS4-28325 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Vogel, O. A1 - Holthaus, C. T1 - Der Einfluß eines geringen Kupferzusatzes auf den Korrosionswiderstand von Baustahl PY - 1930 IS - XI SP - 1 EP - 25 PB - Springer CY - Berlin AN - OPUS4-28326 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Herzog, G. A1 - Fiek, Georg A1 - Holdt, P. T1 - Untersuchungen an Textilriemen zur Verbesserung der Leistung PY - 1930 IS - XII SP - 1 EP - 31 PB - Springer CY - Berlin AN - OPUS4-28327 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Vollenbruck, O. T1 - Über den Angriff von Metallen durch Insekten PY - 1930 IS - XIII SP - 3 EP - 7 PB - Springer CY - Berlin AN - OPUS4-28328 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, Oswald A1 - Hansen, Max T1 - Der Einfluß von dritten Metallen auf die Konstitution der Messinglegierungen PY - 1930 IS - XIII SP - 7 EP - 25 PB - Springer CY - Berlin AN - OPUS4-28329 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rupp, E. A1 - Schmid, Erich T1 - Elektronenbeugung an passivem Eisen I PY - 1930 IS - XIII SP - 78 EP - 80 PB - Springer CY - Berlin AN - OPUS4-28340 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sachs, Georg T1 - Ein neues Prüfgerät für Tiefziehbleche PY - 1930 IS - XIII SP - 80 EP - 85 PB - Springer CY - Berlin AN - OPUS4-28341 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Karnop, R. A1 - Sachs, Georg T1 - Zur Kinetik der Rekristallisation PY - 1930 IS - XIII SP - 86 EP - 92 PB - Springer CY - Berlin AN - OPUS4-28342 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sachs, Georg A1 - Weerts, J. T1 - Die Orientierung einzelner durch Rekristallisation gewonnener Kristalle PY - 1930 IS - XIII SP - 92 EP - 94 PB - Springer CY - Berlin AN - OPUS4-28343 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Karnop, R. A1 - Sachs, Georg T1 - Die Grobkristallisation von Aluminium PY - 1930 IS - XIII SP - 94 EP - 98 PB - Springer CY - Berlin AN - OPUS4-28344 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Boas, W. A1 - Schmid, Erich T1 - Grundtatsachen der Kristallplastizität und Versuche zu ihrer theoretischen Deutung PY - 1930 IS - XIII SP - 98 EP - 102 PB - Springer CY - Berlin AN - OPUS4-28345 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Boas, W. A1 - Schmid, Erich T1 - Über die Temperaturabhängigkeit der Kristallplastizität PY - 1930 IS - XIII SP - 103 EP - 109 PB - Springer CY - Berlin AN - OPUS4-28346 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sachs, Georg A1 - Weerts, J. T1 - Die Gitterkonstanten der Gold-Silberlegierungen PY - 1930 IS - XIII SP - 109 EP - 113 PB - Springer CY - Berlin AN - OPUS4-28347 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Polanyi, M. T1 - Über die Natur der Festigkeit PY - 1930 IS - XIII SP - 113 EP - 119 PB - Springer CY - Berlin AN - OPUS4-28348 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Wilhelm T1 - Kerbzähigkeit und statische Kennziffern PY - 1930 IS - XIV SP - 27 EP - 35 PB - Springer CY - Berlin AN - OPUS4-28360 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Wilhelm T1 - Zur Festigkeit im Schraubengewinde PY - 1930 IS - XIV SP - 35 EP - 38 PB - Springer CY - Berlin AN - OPUS4-28361 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stamer, T1 - Die Kugeldruck-Härteprüfung von Holz PY - 1930 IS - XIV SP - 38 EP - 40 PB - Springer CY - Berlin AN - OPUS4-28362 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sieglerschmidt, H. T1 - Beitrag zur Erkenntnis der elastischen Eigenschaften der Leichtmetalle PY - 1930 IS - XIV SP - 40 EP - 44 PB - Springer CY - Berlin AN - OPUS4-28363 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Wilhelm T1 - Kritische Kerbzähigkeitswerte PY - 1930 IS - XIV SP - 44 EP - 58 PB - Springer CY - Berlin AN - OPUS4-28364 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sieglerschmidt, H. A1 - Stamer, T1 - Elastische Formänderungen gezogener Holzstäbe PY - 1930 IS - XIV SP - 58 EP - 59 PB - Springer CY - Berlin AN - OPUS4-28365 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Wilhelm T1 - Die Bruchgefahr bei metallischen Werkstoffen PY - 1930 IS - XIV SP - 60 EP - 61 PB - Springer CY - Berlin AN - OPUS4-28366 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Wilhelm T1 - Zur Deutung und Bewertung der Bruchdehnung bei Metallen PY - 1930 IS - XIV SP - 61 EP - 71 PB - Springer CY - Berlin AN - OPUS4-28367 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Wilhelm T1 - Über die Kerbgefahr PY - 1930 IS - XIV SP - 71 EP - 77 PB - Springer CY - Berlin AN - OPUS4-28368 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Friedrich Wilhelm A1 - Sachs, Georg T1 - Der Fließbeginn bei wechselnder Zug-Druckbeanspruchung PY - 1930 IS - XIV SP - 77 EP - 82 PB - Springer CY - Berlin AN - OPUS4-28369 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Wilhelm T1 - Berechnung der Schwingungsfestigkeit aus Zugfestigkeit und Trennfestigkeit PY - 1930 IS - XIV SP - 82 EP - 85 PB - Springer CY - Berlin AN - OPUS4-28370 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuntze, Wilhelm T1 - Fragen der technischen Kohäsion PY - 1930 IS - XIV SP - 85 EP - 91 PB - Springer CY - Berlin AN - OPUS4-28371 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krebber, Katerina T1 - POFs for sensing applications N2 - The paper highlights the use of polymer optical fibers (POFs) as sensors in selected applications like structural health monitoring in geotechnical and civil engineering, composites monitoring, healthcare monitoring and personnel protection. The recent progress achieved in this field will be reviewed and the main challenges to these innovative fibre optic sensors will be adressed. T2 - 3rd Workshop on specialty optical fibers and their applications CY - Sigtuna, Sweden DA - 28.08.2013 PY - 2013 IS - T3.6 SP - 1 EP - 2 AN - OPUS4-29334 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz ED - Papadrakakis, M. ED - Papadopoulos, V. ED - Plevris, V. T1 - How to quantify the vibration reduction of railway tracks N2 - Railway tracks, which reduce the ground vibration, are necessary if the trains are passing near to building. Today the reduction effect of railway tracks is often determined by the complex (time domain) simulation of the passage of a complete train. This method of evaluating the reduction is very time consuming and the results include some arbitrary scatter. It is worth to look for simpler methods which yield clearer results in shorter time. This contribution presents the combined finite-element boundary-element method as a detailed method for the track-soil interaction and, on the other hand, some possible simplifications. One important idea for the reduction assessment is to split the reduction in a vehicle-track interaction part and a track transfer part. The track transfer is not influenced by the vehicle and by single axle loads and it can be calculated as a homogeneous problem along the track. The reduction of some tracks (for example of floating slab tracks) can be dominated by this track transfer function whereas other tracks (for example tracks with soft rail pads) are completely determined by the vehicle-track-interaction part. The different force transfer functions and the ground vibration ratios of tracks with elastic rail pads or elastic sleeper pads are shown as a result of the FEBEM model under a fixed harmonic axle load. The force transfer proves to be a useful quantity for to assess the vibration reduction of railway tracks. T2 - COMPDYN 2013 - 4th ECCOMAS Thematic conference on computational methods in structural dynamics and earthquake engineering CY - Kos Island, Greece DA - 2013-06-12 KW - Railway induced ground vibration KW - Mitigation measures KW - Railway tracks KW - Finite-element boundary-element method KW - Wavenumber integrals KW - 1-D insertion loss PY - 2013 SP - 1 EP - 19 AN - OPUS4-29313 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stuckert, J. A1 - Birchley, J. A1 - Große, M. A1 - Fernandez-Moguel, L. A1 - Onel, Yener A1 - Rössger, C. A1 - Steinbrück, M. T1 - The Quench-Debris test - Experimental results and modeling N2 - In the framework of the SARNET-2 WP5.1 the QUENCH-DEBRIS test was conducted as the 17th severe accident test using the QUENCH facility at KIT to investigate the formation and coolability of a prototypic debris bed. The test scenario was defined by pre-test calculations using the MELCOR code. This code was used also for post-test analysis. The test bundle with length of about 2 m contains the hafnium shroud tube and 12 heated peripheral rods with claddings made of hafnium. Hafnium was chosen because of its much higher melting temperature and the about one order of magnitude lower oxidation rate compared to zirconium. The claddings of the inner nine rods were made from Zry-4. They were filled with pre-fragmented zirconia pellets. The test started with an oxidation phase of 20 h at peek cladding temperature about 1800 K to reach complete oxidation of the Zry-4 claddings over a height of 500 mm. The temperatures expected from the pre-test simulation fitted well the experimentally observed evolution of the bundle conditions. The possibly surviving inner Zry-4 claddings were destroyed by the application of an axial mechanical force resulting in material relocation and formation of a heterogeneous debris bed consisting of segmented pellets and larger cladding tube fragments at the grid spacer 2 (350 mm elevation) and in a smaller amount at grid spacer 3 (1050 mm elevation). The so destroyed bundle was quenched with 10 g/s water. The evaporation rate generally showed an increasing trend during the reflood, except at the time of water penetration through the debris bed at spacer 2 when stagnation was observed. All peripheral hafnium claddings survived the whole test. During the oxidation phase about 100 g hydrogen was released. The time dependence of the hydrogen release predicted in the pre-test calculations fits well the measured one. The post-test examinations comprise videoscope inspections, high energy X-ray-tomography and metallographic investigations of the debris bed. T2 - ERMSAR-2013 - 6th European review meeeting on severe accident research CY - Avignon, France DA - 02.10.2013 KW - Hochenergie-Computertomographie KW - Nukleare Sicherheitsforschung PY - 2013 SP - 1 EP - 13 (Paper 2.6) AN - OPUS4-29467 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ellouz, Manel A1 - Völzke, Holger A1 - Kasparek, Eva Maria T1 - BAM challenges for design testing of waste containers for the final repository Konrad N2 - Up to the end of this decade, corresponding to the planned date of starting operation in the final disposal KONRAD for non-heat generating waste in Germany, a lot of efforts are needed to condition and package the radioactive waste in containers certified by BfS (Federal Institute for Radiation Protection). This waste is produced by public sector and industry as well as nuclear energy facilities, which result in more than a half of the actually declared quantity growing especially after the phase out decision of nuclear power production in Germany and the subsequent decommissioning of nuclear power plants. BAM (Federal Institute for Materials Research and Testing) acts as responsible authority on behalf of BfS for design testing under consideration of the KONRAD requirements. Within the assessment procedure of containers, BAM has to verify the application documents, including material qualification, container geometry, corrosion protection, leakage rate and operational and accidental loading, and to evaluate quality assurance measures. Besides the previous completed approvals for various containers such as steel sheet and cast iron box-shaped containers and concrete cylindrical ones, BAM is actually carrying assessments for other types such as cast iron cylindrical containers and “old” steel sheet box shaped ones. The so called “old” containers present already loaded containers without any KONRAD certification, currently stored at licensed interim storages. In the benefit of the container assessment, BAM operates design testing facilities for drop and fire tests which are also used for research objectives to improve and expand the evaluation methods such as research project ConDrop. The latter deals with numerical simulations and analyses tools for further precise predictions about unfavorable drop test scenarios, safety margins, and design sensitivities for steel sheet containers. Furthermore, during the assessment procedure, several specifications about the containers, the inventory to be disposed and the required safety level have been intensely debated by authorities and applicants. Based on its experience in qualifying containers, BAM has been commissioned to identify insufficiently specified aspects in the waste acceptance criteria and to propose clearer definitions with regard to the secondary regulations in the planning approval notice. This paper focuses on aspects of the contribution of BAM in certifying KONRAD waste containers. This will include the current state of design testing procedures, evaluation methods that are available or are being developed and the main topics within the KONRAD requirements being actually specified by BAM. T2 - ICEM 2013 - 15th International Conference on environmental remediation and radioactive waste management CY - Brussels, Belgium DA - 08.09.2013 PY - 2013 IS - ICEM2013-96258 SP - 1 EP - 9 AN - OPUS4-29468 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Lehmann, Christian T1 - Neue Perspektiven für Ultra-Hochleistungsbeton durch gezielte Beeinflussung des Nanogefüges KW - Ultra-Hochleistungsbeton KW - UHPC KW - C-S-H KW - Autoklavierung PY - 2013 SP - 1 EP - 193 CY - Berlin AN - OPUS4-29538 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Seuthe, T. A1 - Grehn, M. A1 - Mermillod-Blondin, A. A1 - Bonse, Jörn A1 - Eberstein, M. T1 - Compositional dependent response of silica-based glasses after femtosecond laser pulse irradiation N2 - Femtosecond laser pulse irradiation of inorganic glasses allows a selective modification of the optical properties with very high precision. This results in the possibility for the production of three-dimensional functional optical elements in the interior of glass materials, such as optical data storage, waveguide writing, etc. The influence of the chemical glass composition to the response upon ultrashort laser irradiation has not been studied systematically. For that, simple silicabased model glasses composed of systematically varying alkaline- and earth-alkaline components were prepared, irradiated on the surface and in the volume with single fs-laser pulses (~130 fs, 800 nm), and were subsequently analyzed by means of micro-Raman spectroscopy and quantitative phase contrast microscopy in order to account for changes in the glass structure and for alterations of the optical refractive index, respectively. The Raman spectroscopic studies of the laser-irradiated spots revealed no change in the average binding configuration (the so called Q-structure), but local changes of bond-angles and bond-lengths within the glass structure structure. Those changes are explained by structural relaxation of the glass network due to densification caused by a transient laser-induced plasma generation and the following shock wave and other thermal phenomena. Glasses with a low amount of network modifiers show changes in the Si-O network while glasses with a high amount of network modifiers react primarily via variation of the nonbridging oxygen ions. The results are discussed in terms of possible structural response mechanisms and conclusions are outlined regarding glass compositions with technical suitability for fs-laser modifications. T2 - Laser-induced damage in optical materials CY - Boulder, Colorado, USA DA - 22.09.2013 KW - Femtosecond laser modifications KW - Raman spectroscopy KW - Glass KW - Femtosecond phenomena KW - Networks KW - Silica KW - Laser irradiation KW - Lasers KW - Micro raman spectroscopy KW - Microscopy KW - Optical components KW - Optical storage PY - 2013 DO - https://doi.org/10.1117/12.2028713 N1 - Serientitel: SPIE proceedings series – Series title: SPIE proceedings series VL - 8885 SP - 1 EP - 8(?) AN - OPUS4-29539 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Helmerich, Rosemarie A1 - Hong, Shuxian ED - Miyamoto, A. ED - Hakola, I. ED - Yabe, A. ED - Emoto, H. T1 - Nondestructive evaluation and structural health monitoring N2 - The European project Smart Management of the Sustainable Human Environment (SmartEN) aims at developing and planning of early proactive measures to reduce the environmental impact of human actions, the influence of climate changes and to protect infrastructure as well as the environment. The work of SmartEN is organised in an initial training network (ITN) of early stage researchers (ESRs) in European universities, research Institutes and in industry. The participation of specialists from different disciplines as structural engineering, structural health monitoring, non-destructive testing, computational techniques and telecommunication allows a cross-themes Cooperation. The Cooperation between young engineers and scientists from different disciplines aims at improving the career perspectives of early stage researchers in both public and private sectors and enables them to create multidisciplinary networks in the field of structural monitoring. The project is structured into four thematic work Programmes: Wireless sensor networks, sensor signal processing, non-destructive evaluation and smart proactive management. Besides an in-depth theme about corrosion mapping with ground penetration radar (GPR) in work Programme 3, BAM is involved in specifying the links between NDE, inspection and SHM in structural engineering, including small and medium span bridges. The Work Programmes considers multidisciplinary tasks besides the PhDs that solve a specific open task in the defects detection. Multidisciplinary tasks to be considered in the field of NDE are the limitation and applicability of methods for the intended use for detection of the most critical parameter considering (1) Implementation of NDE in structural health monitoring, (2) Requirements on non-destructive evaluation, (3) Optimum sensor placement in infrastructure with special focus on small and medium span bridges and (4) Combined Monitoring and inspection Systems. In Smarten Work Programme 3, we studied the contribution of NDE to monitoring from a civil engineering point of view. An example presents NDE requirements from laboratory tests on demonstration specimens for ground penetration radar. T2 - CSHM-5 - 5th International workshop on civil structural health monitoring - Structural health monitoring and maintenance of short- & medium-span bridges CY - Ube, Yamaguchi, Japan DA - 24.10.2013 KW - Non-destructive testing KW - Requirements for NDE KW - Reinforced concrete bridges KW - Corrosion detection KW - Ground penetrating radar KW - Chloride contamination PY - 2013 IS - Keynote paper 4 SP - 49 EP - 56 AN - OPUS4-29510 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Helmerich, Rosemarie A1 - Milmann, Boris A1 - Wöstmann, Jens A1 - Röllig, Mathias A1 - Kind, Thomas A1 - Lai, W. T1 - Qualitätssicherung für textilfaserverstärkten Beton N2 - Beim Bauen im Bestand ist die zusätzlich aufzunehmende Last in der Regel zu beschränken. Das trifft insbesondere für schon gerissene Elemente wie Gewölbe odör alternde Betonkonstruktionen zu. Da Hochleistungsfasern wie Textilgelege aus Carbonfasern oder alkaliresistenten (AR-)Glasfasern keinen Korrosionsschutz erfordern, kann die Verbundschicht aus Feinkornbeton dünn gehalten werden, um das Bauwerk nur mit einer Mindestzusatzlast zu beanspruchen. Textilbeton heißt die neue Bauweise, für die es zurzeit noch kein festgeschriebenes Qualitätssicherungs- und Wartungskonzept für Bau und die spätere Nutzung gibt. T2 - 5. Anwendertagung Textilbeton CY - Friedrichshafen, Germany DA - 24.09.2013 KW - Textilfaserverstärkter Beton KW - Zerstörungsfreie Prüfung KW - Ultraschall-Echo KW - Radar-Echo PY - 2013 VL - 9 SP - 22 AN - OPUS4-29512 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schoknecht, Ute A1 - Bagda, E. T1 - Leaching of substances from facades - current knowledge and activities T2 - European coatings conference on facade coatings and plasters CY - Düsseldorf, Germany DA - 2013-10-29 PY - 2013 SP - 131 EP - 140 PB - Vincentz AN - OPUS4-29474 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Österle, Werner A1 - Dmitriev, Andrey A1 - Kloß, Heinz T1 - Assessment of sliding friction of a nanostructured solid lubricant film by numerical simulation with the method of movable cellular automata (MCA) N2 - Tribofilms formed during dry sliding usually exhibit a nanocrystalline structure and complicated composition. In the present study, tribofilms consisting mainly of a solid lubricant, namely graphite nanoparticles, are considered. Systems providing such tribofilms are candidates for anti-friction applications. Since sliding action always leads to mixing of the materials at both sides of the tribological interface, it was of major interest to study the impact of different amounts of a hard constituent, SiC in the considered case, within the soft matrix systematically. Furthermore, the impact of normal pressure was considered. A mechanically mixed layer was observed for the whole range of normal pressures and SiC volume fractions. The calculated coefficient of friction decreased significantly with increasing thickness of this layer but was only marginally affected by SiC volume fraction, which is good news for anti-friction applications. T2 - WTC 2013 - 5th World tribology congress CY - Torino, Italy DA - 08.09.2013 KW - Friction KW - Third body film KW - Numerical simulation KW - Nanostructure PY - 2013 SP - 1 EP - 4 AN - OPUS4-29659 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rohwetter, Philipp A1 - Habel, Wolfgang A1 - Heidmann, G. A1 - Pepper, D. T1 - Fibre-optic acoustic detection of damage processes in elastomeric insulation under AC and DC stress T2 - ISH 2013 - 18th International symposium on high voltage engineering CY - Seoul, Korea DA - 2013-08-25 KW - Fibre-optic condition monitoring KW - Acoustic emission KW - Partial discharge KW - High voltage DC KW - Silicone elastomer KW - Insulation failure KW - High voltage cable accessories PY - 2013 IS - OD1-03 SP - 663 EP - 668 AN - OPUS4-29716 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reich, Franziska A1 - Otremba, Frank A1 - Würsig, Andreas T1 - Fail-safe? A study about the integrity of safety valves for tanks for dangerous goods N2 - In Europe, tanks designed on different safety philosophies are used for transporting one and the same liquid dangerous goods (Krautwurst, 2011). Owing to this circumstance, the BAM was commissioned by the BMVBS to conduct a research project designed to analyse and assess the equipment of tanks. Furthermore in these project were researched some failure mechanism of pressure relief devices (PRD). Based on the knowledge gained, possible solutions were worked out under safety-relevant aspects that would benefit tank transport by providing a lower hazard potential. Besides looking at the mode of operation and the construction of PRV, their blow-off characteristics and total flow rate are considered from a safety engineering point of view. Based on in-depth studies, a concept for and the further approach to examinations of the failure limits of PRD, especially of spring loaded relief valves, was developed and comprehensively described in the report “The use of safety devices, particularly safety valves, on transport containers” (Pötzsch, Reich, & Jochems, 2011). The purpose of this study was to investigate failure causes of safety valves by normal modes and accidental fire heat loads. A series of investigations for different influences using safety valves for tanks were obtained. Testing vibration modes and corrosion presents some design limits. Experimental study of a pressure vessel engulfing in fire identify significant design limits. The complete set of results provides direct information of fail-safe modes and discusses the usage. T2 - ASME 2013 International mechanical engineering congress and exposition CY - San Diego, CA, USA DA - 15.11.2013 KW - Safety valves KW - Transporttanks KW - Dangerous goods KW - Fire prooving KW - Response behavior PY - 2013 IS - IMECE2013-62204 SP - 1 EP - 5 AN - OPUS4-29717 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Griesche, Axel A1 - Lexow, Jürgen T1 - Research on materials simulation and the promotion of global databases - activities within the world materials research institute forum (WMRIF) N2 - Worldwide 50 national materials research Institutes are organized within the World Materials Research Institute Forum (WMRIF). The forum aims at e.g. fostering the international networking of the major national materials research Institutes, sharing knowledge and Instrumentation and continued training of outstanding materials scientists. The forum operates 6 working groups, two of them, Research on Materials Simulation and Promotion of Global Databases, strongly contributing to Integrated Computational Materials Engineering (ICME). The WMRIF activities and similar activities within the Versailles Project on Advanced Materials and Standards (VAMAS) and the M-ERA.NET, a consortium that contributes to the restructuring of the European Research Area (ERA) in materials Science and engineering, are presented. T2 - Materials Science & Technology (MS&T) 2013 CY - Montreal, Quebec, Canada DA - 27.10.2013 KW - ICME KW - WMRIF KW - VAMAS KW - M-ERA.net KW - Materials simulation KW - Global databases PY - 2013 SP - 2551 EP - 2554 PB - Curran CY - Red Hook, NY AN - OPUS4-29718 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz A1 - Rücker, Werner ED - Nielsen, J. T1 - Mitigation measures for ballasted tracks - optimisation of sleepers, sleeper pads and the substructure by combined finite-element boundary-element calculations T2 - IWRN11 - 11th International workshop on railway noise CY - Uddevalla, Sweden DA - 2013-09-09 PY - 2013 SP - 463 EP - 470 AN - OPUS4-29446 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Greenhalgh, E.S. A1 - Ankersen, J. A1 - Asp, L. E. A1 - Bismarck, A. A1 - Fontana, Q.P.V. A1 - Houlle, M. A1 - Kalinka, Gerhard A1 - Kucernak, A. A1 - Mistry, M. A1 - Nguyen, S. A1 - Qian, H. A1 - Shaffer, M.S.P. A1 - Shirshova, N. A1 - Steinke, J.H.G. A1 - Wienrich, Malte T1 - Mechanical and microstructural characterisation of multifunctional structural power composites N2 - Although the inherent anisotropy of polymer composites has presented daunting technical challenges, these materials now offer engineers considerable opportunities for efficient structural design. More recently, the advent of multifunctional composites which can fulfill more than one role within a system has attracted considerable interest, providing designers with exciting opportunities to innovate. Of particular interest here are structural power composites, which simultaneously carry mechanical load whilst storing/delivering electrical energy. Although the development of these composites is highly challenging, often with conflicting constituent requirements, the STORAGE consortium has had considerable success in the development of these materials for automotive applications. The focus of this paper is structural supercapacitors, the basic architecture of a single cell of which is shown in Fig. 1. This entails two carbon fibre woven lamina (electrodes) which sandwich a glass fibre woven lamina (separator), all of which is embedded within a multifunctional matrix (electrolyte). This architecture has been the focus of the research to date, leading to components such as that shown in Fig.1 having been fabricated. This paper reports on the mechanical properties and microstructures of the different reinforcement and matrix combinations for structural supercapacitors. T2 - ICCM19 - 19th International conference on composite materials CY - Montreal, Canada DA - 28.07.2013 KW - Structural electrolyte KW - Multifunctional supercapacitor KW - Fractography KW - Ionic conductivity KW - Mechanical properties PY - 2013 SP - 2228 EP - 2237 AN - OPUS4-29272 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Shirshova, N. A1 - Bismarck, A. A1 - Carreyette, S. A1 - Greenhalgh, E.S. A1 - Johansson, P. A1 - Marczewski, M.J. A1 - Jacobsson, P. A1 - Kalinka, Gerhard A1 - Shaffer, M.S.P. A1 - Wienrich, Malte A1 - Steinke, J.H.G. T1 - Correlations between mechanical properties and ionic conduction of structural electrolytes with bicontinuous morphologies N2 - Electrolyte systems that can carry mechanical load while allowing for high levels of ionic conductivity are an important prerequisite for structural power storage devices. Introduction of structural power storage into the variety of consumer products will allow saving in weight and volume. Moreover, using a supercapacitor/battery system in hybrid electric vehicles (HEV), the supercapacitor part will extend the battery lifetime by protecting it from the high peak currents. To successfully produce structural power storage requires the development of multifunctional electrolytes where one has to simultaneously maximize mechanical properties and ionic conductivity. T2 - ICCM19 - 19th International conference on composite materials CY - Montreal, Canada DA - 28.07.2013 KW - Structural electrolyte KW - Multifunctional supercapacitor KW - Bicontinuous morphology KW - Epoxy resin KW - Ionic conductivity KW - Mechanical properties PY - 2013 SP - 72 EP - 79 AN - OPUS4-29273 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Madia, Mauro A1 - Foletti, S. A1 - Beretta, S. A1 - Cavalleri, E.A. T1 - A tool for the structural integrity assessment of turbine disks: probabilistic and numerical background N2 - Rotor disks for gas turbines are heavy components and are usually designed following a safe-life approach, where the low-cycle fatigue analysis is carried out referring to design life curves with suitable probabilistic margins. However, in the case of such a heavy component there is the possibility of rare occurrence of undetected defects or, better, the need to identify the defect acceptability for the different rotor regions (considering stress, temperature, mission profile).In order to carry out such calculations for a turbine rotor disk a software named AStrID (Assessment of the Structural Integrity of Disks) has been developed in close cooperation between Politecnico di Milano and Ansaldo Energia (AEN). This paper summarizes its background and some of the relevant features. T2 - ASME Turbo Expo 2013 - GT 2013 CY - San Antonio, TX, USA DA - 03.06.2013 PY - 2013 SP - GT2013-96029, 1-8 AN - OPUS4-29456 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe A1 - Klinger, Christian T1 - Anmerkungen zur Auslegung und zum sicheren Betrieb von Radsatzwellen aus der Sicht von Betriebsfestigkeit und Bruchmechanik N2 - Die Sicherheit von Radsatzwellen beruht gegenwärtig auf zwei Säulen: der Schwingfestigkeitsauslegung und periodischen Inspektionen. Ausgehend von einem Schadensfall, der gebrochenen ICE 3-Welle von Köln, 2008, sollen ausgewählte Aspekte beider Säulen diskutiert und Vorschläge zur weiteren Verbesserung gemacht werden. Diese betreffen u.a. Fragen einer Betriebszeitbegrenzung, Veränderungen der Schwingfestigkeit während des Betriebs infolge von Korrosion und Steinschlag, den Einfluss von Korrosion auf Schwingrissinitiierung und -fortschritt, den potentiellen Einfluss nichtmetallischer Einschlüsse auf die Schwingfestigkeit, die Möglichkeiten sie im Rahmen der Qualitätssicherung zu detektieren sowie Fragen der Bruchmechanik und der Zuverlässigkeit zerstörungsfreier Schwingriss-Prüfverfahren im Rahmen eines Konzepts regelmäßiger Inspektionen. T2 - 40. Tagung des DVM-Arbeitskreises Betriebsfestigkeit CY - Herzogenaurach, Germany DA - 09.10.2013 KW - Radsatzwellen KW - Schwingfestigkeit KW - Sichere Lebensdauer KW - Schadenstoleranz KW - Zerstörungsfreie Inspektion KW - Korrosion KW - Steinschlag KW - Nichtmetallische Einschlüsse KW - Railway axles KW - Fatigue strength KW - Safe life design KW - Damage tolerance design KW - Non-destructive inspection KW - Corrosion KW - Flying ballast impact KW - Non-metallic inclusions PY - 2013 N1 - Serientitel: DVM-Bericht – Series title: DVM-Bericht VL - 140 SP - 69 EP - 80 AN - OPUS4-29458 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hong, Shuxian A1 - Helmerich, Rosemarie T1 - Non-destructive corrosion monitoring in concrete with ground penetrating radar N2 - In this research, laboratory experiments were carried out to investigate the feasibility of using ground penetrating radar (GPR) for corrosion detection and/or monitoring, and the mechanism of corrosion caused GPR signal changes, taking into account the influence of several parameters: Chloride, rebar size and cover depth. With the understanding of the mechanism, a novel method for detecting reinforcement corrosion in concrete with GPR is proposed, together with a series of signal processing toolkits for corrosion visualization and image comparison. T2 - SmartEN Marie Curie ITN Final Conference CY - Limassol, Cyprus DA - 09.10.2013 KW - Concrete KW - Reinforcement corrosion KW - Nondestructive testing KW - Ground penetration radar KW - Long term corrosion monitoring KW - Periodic monitoring PY - 2013 SP - 1 EP - 6 AN - OPUS4-29580 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Philipp, Rosemarie T1 - Ermittlung der Messunsicherheit in der organisch-chemischen Analytik - ein Beispiel aus der Praxis T2 - DAP-Sektorkomitee Chemie CY - --- DA - 2000-10-26 PY - 2000 AN - OPUS4-1007 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Berger, Wolfgang A1 - Eckardt, Jürgen A1 - Fischer, Hildegard T1 - Praxiserfahrungen bei der Erkundung von Altlasten und Schadensfällen T2 - Symposium "Vor-Ort-Analytik nach BBodSchV- Anwendungsmöglichkeiten und Erfahrungen" CY - Stuttgart, Deutschland DA - 2000-11-22 KW - Vor-Ort-Analytik KW - BBodSchV KW - Kontaminationsbewertung KW - RFA KW - BTX KW - MKW PY - 2000 SP - 1(?) EP - 6(?) AN - OPUS4-1008 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Thomas, Hans-Martin A1 - Junger, M. A1 - Hintze, H. A1 - Krull, R. A1 - Rühe, S. T1 - Pioneering inspection of railroad rails with eddy currents N2 - Using a rail-inspection train, the Deutsche Bahn's system of railroads is continuously checked for traffic-induced defects. Until now, only ultrasonic inspection was used. In addition, eddy-current inspection could successfully and efficiently be used to detect and evaluate certain surface cracks - so-called head checks. There have already been reports about laboratory tests which proved the general suitability of this test method [1,2]. The next step - described here - consisted of practical trials under real-life conditions. A test system which is able to fulfil the strict requirements (test speeds of up to 100 km/h, complex probe guidance, suppression of electrical and mechanical interference, recording of data, filtering and evaluation of data) was developed. As part of the rail-inspection train and as a manual system, this inspection system was successfully tested on the Deutsche Bahn's system of railroads under real-life conditions. T2 - 15th World Conference on Non-Destructive Testing (WCNDT) CY - Roma, Italy DA - 2000-10-15 KW - Schienenprüfung PY - 2000 UR - http://www.ndt.net/article/wcndt00/papers/idn796/idn796.htm SN - 1435-4934 VL - 5 IS - 11 SP - 1 EP - 6(?) PB - NDT.net CY - Kirchwald AN - OPUS4-1010 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schultze, Karin A1 - Becker, Roland A1 - Win, Tin A1 - Nehls, Irene T1 - Entwicklung, Herstellung und Zertifizierung eines Referenzmaterials zur Bestimmung von "Organochlorpestiziden in Boden" T2 - Tagung "Tag der Chemie" CY - Potsdam, Deutschland DA - 2000-11-08 PY - 2000 AN - OPUS4-1001 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thomas, Hans-Martin T1 - Wirbelstromprüfung an verlegten Eisenbahnschienen T2 - 5. DELTA TEST Fachtagung CY - Celle, Deutschland DA - 2000-11-01 KW - Schienenprüfung PY - 2000 SP - 4-1-4-8 AN - OPUS4-1012 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gross, Thomas T1 - Resultate eines Ringversuchs mit SSI XPS-Spektrometern T2 - EMASS 2000 CY - Berlin, Deutschland DA - 2000-11-10 PY - 2000 AN - OPUS4-1019 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gross, Thomas A1 - Lippitz, Andreas A1 - Unger, Wolfgang T1 - Charakterisierung von Siliziumoxidschichten auf Silizium mit ESCA - Ein Beitrag zur Präszisionsbestimmung der Avogadro-Konstanten T2 - EMASS 2000 CY - Berlin, Deutschland DA - 2000-11-10 PY - 2000 AN - OPUS4-1020 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Brzezinka, Klaus-Werner A1 - Wachsmann-Hogiu, S. A1 - Dreyer, J. A1 - Elsaesser, T. A1 - Werncke, W. A1 - Vodchits, A.I. T1 - Ultrafast intramolecular electron transfer studied by stationary vibrational and time-resolved resonance raman spectroscopy combined with ab initio calculations PY - 2000 VL - 1 PB - Transworld Research Network CY - Trivandrum AN - OPUS4-1032 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Malz, Frank A1 - Jancke, Harald A1 - Radeglia, Reiner T1 - Ringversuche zur quantitativen 1H-NMR-Spektroskopie T2 - GDCh-Diskussionstagung CY - Bochum, Deutschland DA - 2001-01-15 PY - 2001 AN - OPUS4-1040 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kautek, Wolfgang T1 - Laser-Reinigung - Grundlagen und Anwendungen T2 - Mauterndorfer Laserseminar 2001 CY - Mauterndorf, Österreich DA - 2001-03-19 PY - 2001 AN - OPUS4-1022 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübert, Thomas A1 - Mosel, Günter T1 - The local order of zinc ions in oxide glasses investigated by Zn-K-EXAFS KW - Glass structure KW - EXAFS KW - Zinc ions KW - Local order PY - 2000 AN - OPUS4-1026 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Retter, Utz T1 - On the development of surfactant reference solutions - degradation of surfactants and formation of surface micelles T2 - Institutskolloquium CY - Thessaloniki, Greece DA - 2000-11-22 PY - 2000 AN - OPUS4-1029 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nehls, Irene A1 - Kuhnhardt, Claus T1 - Untersuchungen zur Homogenität und Stabilität von Referenzmaterialien zur Bestimmung von Schwefel in der Matrix Öl T2 - DGMK-Analytikertreffen 2000 CY - Hamburg, Deutschland DA - 2000-11-13 PY - 2000 CY - Hamburg AN - OPUS4-1030 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geißler, Heinz A1 - Reinholz, Uwe A1 - Geotti-Bianchini, F. A1 - Preo, M. T1 - Water content of hydrated soda lime silica surface layers with IR spectroscopy and Nuclear Reaction Analysis (NRA) T2 - 3rd ICG TC 14 forum on "water in glass" CY - Edinburgh, Scotland, UK DA - 2001-07-06 PY - 2001 AN - OPUS4-1065 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Retter, Utz T1 - Entwicklung von Tensid-Referenzlösungen T2 - Tagung der Krüss GmbH CY - Hamburg, Deutschland DA - 2001-01-12 PY - 2000 CY - Hamburg AN - OPUS4-1066 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geißler, Heinz A1 - Yozgatli, Hakan-Peter A1 - Zschunke, Adolf T1 - Richtigkeit und Präzision FT-IR-spektroskopischer Transmissionsmessungen an Gläsern T2 - 75. Glastechnische Tagung CY - Wernigerode, Deutschland DA - 2001-05-21 PY - 2001 PB - DGG, Deutsche Glastechnische Gesellschaft e.V. CY - Frankfurt/M. AN - OPUS4-1070 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meggyes, Tamás T1 - Reaktive Wände - eine innovative Methode für Grundwasserreinigung T2 - Dialog Geotechnik CY - Weimar, Deutschland DA - 2000-11-27 KW - Reaktive Wände KW - Grundwasserreinigung PY - 2000 AN - OPUS4-1054 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Witke, Klaus A1 - Dietrich, D. A1 - Marx, G. A1 - Götze, J. A1 - Rößler, R. T1 - Cathodoluminescence and RAMAN studies on permineralisations of medullosa sp. T2 - 11. Tagung Festkörperanalytik CY - Chemnitz, Germany DA - 2001-06-25 PY - 2001 PB - GDCh CY - Frankfurt am Main AN - OPUS4-1057 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Radeglia, Reiner A1 - Arrieta, A. T1 - Messung und Zuordnung von long-range 13C-1H-Kopplungen T2 - GDCh-Diskussionstagung CY - Bochum, Deutschland DA - 2001-01-15 PY - 2001 AN - OPUS4-1058 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lehmann, Andreas A1 - Walther, Wolfgang A1 - Rohde, Gabriele ED - Frenzel, W. ED - Linscheid, M. ED - Seubert, A. T1 - Einsatz der Kapillarelektrophorese für die Zertifizierung eines Referenzmaterials "Pentachlorphenol in Boden" T2 - 1. Konferenz über Ionenanalyse CY - Berlin, Deutschland DA - 2001-02-21 PY - 2001 CY - Berlin AN - OPUS4-1059 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfeil, Norbert T1 - GHS - Global Harmonisiertes System - Stand der Arbeiten T2 - Gefahrgut-Tage Hamburg CY - Hamburg, Deutschland DA - 2001-02-18 PY - 2001 SP - 1(?) EP - 20(?) AN - OPUS4-1113 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Steckert, Carsten A1 - Witt, Klaus T1 - Optical surface defects on paint coatings analysed by colorimetrically adjusted image analysis T2 - MAT 2001 ; International conference: material testing and research ; MAT Kongreß ; MAT Conference CY - Nuremberg, Germany DA - 2001-05-08 PY - 2001 IS - A6.5 SP - 163 EP - 168 PB - AMA Service GmbH CY - Wunstorf AN - OPUS4-1115 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gradt, Thomas A1 - Börner, Helmut A1 - Hübner, Wolfgang T1 - Friction and Wear Testing for Cryogenic Engineering T2 - MAT 2001 ; International conference: material testing and research ; MAT Kongreß ; MAT Conference CY - Nuremberg, Germany DA - 2001-05-08 PY - 2001 IS - A5.5 SP - 129 EP - 133 PB - AMA Service GmbH CY - Wunstorf AN - OPUS4-1116 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Molnarne, Maria A1 - Viczián, G. A1 - Kollár-Hunek, K. T1 - Explosion envelopes of flammable substances and their numerical approximation T2 - Workshop on Chemical Engineering Mathematics CY - Bad Honnef, Germany DA - 2001-08-12 PY - 2001 SP - - AN - OPUS4-1117 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Berger, Georg A1 - Mensing, M. A1 - Müller-Mai, C. A1 - Gross, U. A1 - Rahmanzadeh, R. A1 - Sittinger, M. T1 - Bioresorbable carriers for subchondral anchoring of tissue-engineered cartilage in articular defects T2 - 3rd Biennial Meeting of the Tissue Engineering Society International (TESI) CY - Lake Buena Vista, FL, USA DA - 2000-11-30 PY - 2000 AN - OPUS4-1042 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gogolin, Bernd A1 - Jahreiß, W. A1 - Tippl, W. A1 - Paulyini, W. A1 - Gehring, E. ED - Bauer, K. T1 - ANF-10 und ANF-18 - Neuentwicklung der Transportbehälter für unbestrahlte SWR- und DWR-Brennelemente T2 - Jahrestagung Kerntechnik 2001 ; Annual Meeting on Nuclear Technology 2001 CY - Dresden, Deutschland DA - 2001-05-15 PY - 2001 PB - INFORUM-Verl. CY - Bonn AN - OPUS4-1047 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grätz, Rainer T1 - Europäische Regelungen zum Inverkehrbringen und Betrieb nichtelektrischer Geräte und autonomer Schutzsysteme in explosionsgefährdeten Bereichen T2 - Internationale Fachmesse für Explosionsschutz und Anlagensicherheit CY - Nürnberg, Deutschland DA - 2001-03-27 PY - 2001 SP - 1(?) EP - 13(?) AN - OPUS4-1101 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stadthaus, Meinhard A1 - Thomas, Hans-Martin A1 - Baugatz, J. A1 - König, W. A1 - Migoun, N. A1 - Gnusin, A. T1 - Performance testing of detection media for magnetic particle and penetrant testing following the European standards T2 - Congrès COFREND 2001 CY - Reims, France DA - 2001-04-24 PY - 2001 SP - 1(?) EP - 6(?) PB - COFREND CY - Paris AN - OPUS4-1123 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weidemann, Gerd A1 - Goebbels, Jürgen A1 - Illerhaus, Bernhard A1 - Dittrich, R. A1 - Mangler, M. A1 - Tomandl, G. T1 - Charakterisierung von Gradientenwerkstoffen mittels hochauflösender Computertomographie T2 - Jahrestagung Zerstörungsfreie Materialprüfung 2001 CY - Berlin, Deutschland DA - 2001-05-21 PY - 2001 UR - http://www.ndt.net/article/dgzfp01/papers/p16/p16.htm N1 - Serientitel: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. – Series title: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. IS - 75-CD PB - DGZfP CY - Berlin AN - OPUS4-1128 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rabe, Torsten T1 - Types of defects in green ceramic components and methods of evaluation T2 - Evening Seminar of Powder Technology in TUAT CY - Tokyo, Japan DA - 2001-01-10 PY - 2001 AN - OPUS4-1072 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simon, Franz-Georg T1 - Deponien im Jahr 2020 T2 - GVC-Fachausschuss Abfallbehandlung CY - --- DA - 2001-01-01 KW - Abfallbehandlung KW - Deponietechnik PY - 2001 AN - OPUS4-1076 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thomas, Hans-Martin A1 - Krull, R. A1 - Hintze, H. ED - Edel, K.-O. T1 - Moderne Methoden der zerstörungsfreien Werkstoffprüfung im Oberbau T2 - Internationales Symposium "Schienenfehler" 2000 CY - Brandenburg, Deutschland DA - 2000-11-16 PY - 2000 SP - 3-1-3-16 PB - Fachhochsch., Der Rektor CY - Brandenburg AN - OPUS4-1102 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Erhard, Anton A1 - Schulz, Eduard A1 - Brekow, Gerhard A1 - Wüstenberg, Hermann A1 - Kreier, P. T1 - Critical Assessments of the TOFD Approach for Ultrasonic Weld Inspection N2 - Weld inspection using ultrasonic pulse-echo techniques needs high skilled operators especially if geometrical indications must be taken into consideration. A clear separation between geometrical indications and defects like cracks must be guaranteed. This requirement needs sensitive techniques like the 45(deg) shear wave technique using the mirror effect. Since more than twenty years the Time Of Flight Diffraction technique (TOFD) is still under discussion for defect sizing. But on the other hand the potential of the TOFD technique for defect detection is described in technical papers of manufacturers. The main task of examinations carried out at BAM was the comparison about the detectability of surface breaking cracks between the common methods and the TOFD approach. T2 - 7th European Conference on Non-Destructive Testing (ECNDT) CY - Copenhagen, Denmark DA - 1998-05-26 KW - Time of flight diffraction KW - TOFD KW - Ultrasonic weld PY - 2001 SP - AD 1 EP - 199 PB - Society of Manufacturing Engineers CY - Dearborn, Mich. AN - OPUS4-1105 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Riebe, Gundel A1 - Klingbeil, Patrick A1 - Pritzkow, Wolfgang A1 - Vogl, Jochen T1 - Erfahrungen mit mikrowelleninduzierten Aufschluss-Verfahren für die Elementspurenanalytik T2 - MLS-Tagesseminar CY - Berlin, Deutschland DA - 2001-03-19 PY - 2001 AN - OPUS4-1111 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Balke, Christian T1 - Schadenstechnische Beurteilung von Flüssiggasanlagen - aufgezeigt am Beispiel der Unterfeuerung eines mit Propan gefüllten Eisenbahnkesselwagens T2 - VdS-Fachtagung CY - Köln, Deutschland DA - 2001-10-10 PY - 2001 SP - ohne durchgehende Numerierung PB - VdS Schadenverhütung CY - Köln AN - OPUS4-1184 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brink, Arne A1 - Maierhofer, Christiane A1 - Röllig, Mathias A1 - Wiggenhauser, Herbert T1 - Anwendung der Impuls-Thermografie als zerstörungsfreies Prüfverfahren im Bauwesen T2 - Fachtagung Bauwerksdiagnose - Praktische Anwendungen Zerstörungsfreier Prüfungen CY - Leipzig, Deutschland DA - 2001-10-25 KW - Impuls-Thermografie KW - Thermografie KW - Zerstörungsfreie Prüfung KW - Abkühlungsprozess KW - Bauingenieurwesen KW - Beton KW - Spaltklinker KW - Simulation PY - 2001 N1 - Serientitel: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. – Series title: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. IS - 76-CD PB - DGZfP CY - Berlin AN - OPUS4-1187 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mielentz, Frank A1 - Milmann, Boris A1 - Krause, Martin A1 - Müller, W. A1 - Crail, S. T1 - Zerstörungsfreie Risscharakterisierung in Betonbauteilen mit Ultraschall N2 - Die Risstiefenbestimmung in Festen Fahrbahnen ist hinsichtlich der Dauerhaftigkeit der Konstruktion von wesentlichem Interesse. Im Rahmen eines gemeinsamen Forschungsvorhabens mit der DB AG wurden aus der Literatur bekannte Ansätze bewertet und darauf aufbauend ein Verfahren zur bildgebenden Rissdarstellung entwickelt. Rissüberbrückende Bewehrung sowie Kontaktstellen zwischen den Rissflanken wirken als Schallbrücken und erschweren die Risscharakterisierung, wie bei einem Einsatz an einer Betriebserprobungsstrecke festgestellt wurde. Ein aus der Literatur bekanntes Verfahren der einfachen Laufzeitmessung erwies sich für die Tiefenbestimmung von realen verunreinigten Rissen als ungeeignet. T2 - Fachtagung Bauwerksdiagnose - Praktische Anwendungen Zerstörungsfreier Prüfungen CY - Leipzig, Germany DA - 25.10.2001 PY - 2001 VL - 76-CD SP - 1 EP - 10 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-1188 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilsch, Gerd A1 - Schaurich, Dieter A1 - Wöstmann, Jens A1 - Wiggenhauser, Herbert T1 - Nachweis von Hydrophobierungsmitteln mit Laser Induced Breakdown Spectroscopy T2 - Fachtagung Bauwerksdiagnose - Praktische Anwendungen Zerstörungsfreier Prüfungen CY - Leipzig, Germany DA - 2001-10-25 PY - 2001 N1 - Serientitel: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. – Series title: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. IS - 76-CD PB - DGZfP CY - Berlin AN - OPUS4-1189 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Böcker, Wolfgang D. G. A1 - Bücker, Michael A1 - Reinsch, Stefan A1 - Unger, Brita A1 - Britz, Roswitha T1 - Mineralisiertes Holz - Verbundwerkstoff mit verbesserten Eigenschaften PY - 2001 CY - München AN - OPUS4-1197 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mittag, Kornelia A1 - Colla, Camilla A1 - Krause, Martin A1 - Maierhofer, Christiane A1 - Mielentz, Frank A1 - Milmann, Boris A1 - Schneider, Gerhard A1 - Wöstmann, Jens A1 - Wiggenhauser, Herbert T1 - Zerstörungsfreie Messungen zur Beurteilung des inneren Zustandes fester Fahrbahnen der Deutschen Bahn AG: Vergleichsmessungen an Probeaufbauten im Labor N2 - Im Rahmen eines FE-Projektes “Inspektion Fester Fahrbahnen“ der BAM und der Deutschen Bahn AG geht es um die Anwendung und weitere Entwicklung zerstörungsfreier Messverfahren zur Beurteilung des Zustandes Fester Fahrbahnen. Nach ersten Versuchsreihen direkt im Gleis wurden für verschiedene Bauarten die charakteristischen Herstellungsbedingungen simuliert und systematisch untersucht. Die kombinierte Anwendung der drei Messverfahren Ultraschall-Array-, Impakt-Echo- und Impuls-Radar-Verfahren wird hier an dem Beispiel “Betonschwelle in Betoneinbettung” dargestellt. T2 - Fachtagung Bauwerksdiagnose - Praktische Anwendungen Zerstörungsfreier Prüfungen CY - Leipzig, Germany DA - 25.10.2001 KW - Impakt-Echo-Messverfahren KW - Impuls-Radar-Messverfahren KW - Ultraschall-Array-Messverfahren PY - 2001 VL - 76-CD SP - 1 EP - 8 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-1201 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bishop, J. L. A1 - Pieters, C. M. A1 - Dyar, M. D. A1 - Hamilton, V. E. A1 - Harloff-Puhr, Jan T1 - A spectral, chemical and mineralogical study of Mars analogue rocks N2 - A consortium has recently been initiated to study the macroscopic and microscopic properties of basaltic and andesitic rocks as analogue materials for Mars. The goal of this project is the integration of diverse spectroscopic approaches to evaluate the composition and texture of Mars materials using both in situ and remote sensing techniques. Initial emphasis is placed on assessment of the mineral composition for low albedo areas (basalt vs andesite vs weathering) of the Martian surface through spectral analysis of a suite of samples that have been exceptionally well characterized in the laboratory. The initial results indicate that the visible/NIR reflectance spectra, mid-IR reflectance and emission spectra, and Mössbauer spectra contain consistent diagnostic features associated with the measured modal mineralogy and provide baseline data for the first group of well characterized basalts. The consortium study involves integrating multiple remote sensing techniques for recent and upcoming missions to Mars in order to compare the results obtained by these instruments and thereby strengthen interpretive results. T2 - 33rd Lunar and Planetary Science Conference CY - Houston, TX, USA DA - 2002-03-11 PY - 2002 UR - http://www.lpi.usra.edu/meetings/lpsc2002/pdf/1168.pdf SN - 0161-5297 N1 - Geburtsname von Harloff-Puhr, Jan: Harloff, J. - Birth name of Harloff-Puhr, Jan: Harloff, J. N1 - Serientitel: LPI contribution – Series title: LPI contribution IS - 1109 SP - 1 EP - 2, paper #1168 PB - Lunar and Planetary Institute CY - Houston, Tex. AN - OPUS4-1218 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reusch, Frederik A1 - Klingbeil, Dietmar A1 - Svendsen, B. ED - Habraken, A. M. T1 - Local and non-local Gurson-based models for ductile damage and failure T2 - 4th International ESAFORM Conference on Material Forming CY - Liège, Belgium DA - 2001-04-23 KW - Ductile damage and failure KW - Finite elements KW - Gradient type material models PY - 2001 VL - 2 SP - 511 EP - 514 CY - Liège AN - OPUS4-1133 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wüstenberg, Hermann A1 - Hauser, T. A1 - Boehm, R. A1 - Hintze, H. A1 - Fischer, E. T1 - Neue Ansätze zur Ultraschallprüfung von Eisenbahnachsen mit Array-Prüfköpfen T2 - Jahrestagung Zerstörungsfreie Materialprüfung ; 2001 (Berlin) : 2001.05.21-23 CY - Berlin, Deutschland DA - 2001-05-21 PY - 2001 UR - http://www.ndt.net/article/dgzfp01/papers/v20/v20.htm N1 - Serientitel: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. – Series title: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. IS - 75-CD PB - DGZfP CY - Berlin AN - OPUS4-1136 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Tessaro, Ute A1 - Wüstenberg, Hermann A1 - Erhard, Anton A1 - Boehm, Rainer T1 - Ultraschalluntersuchungen zur Fehlercharakterisierung im Plattierungsbereich T2 - Jahrestagung Zerstörungsfreie Materialprüfung ; 2001 (Berlin) : 2001.05.21-23 CY - Berlin, Deutschland DA - 2001-05-21 PY - 2001 UR - http://www.ndt.net/article/dgzfp01/papers/p09/p09.htm N1 - Serientitel: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. – Series title: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. IS - 75-CD PB - DGZfP CY - Berlin AN - OPUS4-1139 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brekow, Gerhard A1 - Erhard, Anton A1 - Schulz, Eduard A1 - Siebelmann, F. A1 - Kiechle, H. T1 - Optimierung der Ultraschall-Prüftechnik bei Engspaltschweißnähten T2 - Jahrestagung Zerstörungsfreie Materialprüfung 2001 CY - Berlin, Deutschland DA - 2001-05-21 PY - 2001 UR - http://www.ndt.net/article/dgzfp01/papers/p08/p08.htm N1 - Serientitel: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. – Series title: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. IS - 75-CD PB - DGZfP CY - Berlin AN - OPUS4-1140 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz, Eduard A1 - Erhard, Anton A1 - Montag, Hans-Joachim A1 - Beine, U. A1 - Lucht, B. T1 - Fehleranalyse an einer austenitischen Rohrschweißnaht T2 - Jahrestagung Zerstörungsfreie Materialprüfung 2001 CY - Berlin, Deutschland DA - 2001-05-21 PY - 2001 UR - http://www.ndt.net/article/dgzfp01/papers/p10/p10.htm N1 - Serientitel: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. – Series title: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. IS - 75-CD PB - DGZfP CY - Berlin AN - OPUS4-1141 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Merchel, Silke A1 - Ott, U. A1 - Altmaier, M. A1 - Herpers, U. A1 - Kuhnhenn, J. A1 - Michel, R. A1 - Mohapatra, R. K. T1 - Update on recoil loss of spallation products from presolar grains T2 - 64th Annual Meeting of the Meteoritical Society CY - Vatican City DA - 2001-09-10 PY - 2001 UR - http://adsabs.harvard.edu/abs/2001M&PSA..36Q.155O VL - 36 IS - 9, Suppl. SP - A155 EP - A156 PB - Allen Press CY - Lawrence, Kan. AN - OPUS4-1173 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klinger, Christian A1 - Klingbeil, Dietmar A1 - Kinder, Joachim A1 - Österle, Werner T1 - ESTONIA-Katastrophe - Werkstoffuntersuchungen der BAM an Prüfstücken des Frontschotts T2 - 5. Kolloquium "Werkstoff- und Bauteilprüfung in der Schweißtechnik" CY - Halle (Saale), Deutschland DA - 2001-10-10 PY - 2001 SP - 1(?) EP - 65(?) AN - OPUS4-1174 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Redmer, Bernhard A1 - Onel, Yener A1 - Ewert, Uwe T1 - Mechanised radiation techniques - an innovative technique of the mobile in-service inspection of circumferential welds T2 - 3rd International Conference "Pipeline Diagnostics" CY - Moscow, Russia DA - 2001-05-21 PY - 2001 SP - I34 AN - OPUS4-1176 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilsch, Gerd A1 - Schaurich, Dieter A1 - Wöstmann, Jens A1 - Wiggenhauser, Herbert ED - Forde, M. C. T1 - Application of laser induced breakdown spectroscopy for the detection of hydrophobic coatings T2 - 9th International Conference and Exhibition "Structural Faults and Repair" CY - London, England, UK DA - 2001-07-04 KW - LIBS KW - NDT KW - Hydrophobic Coating KW - Cement KW - Mortar KW - Brick PY - 2001 VL - 9 CY - Edinburgh AN - OPUS4-1177 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Osterloh, Kurt A1 - Ewert, Uwe T1 - Anwendung von Röntgenblitzröhren T2 - BAM-Workshop 2001 CY - Berlin, BAM, Deutschland DA - 2001-04-26 PY - 2001 AN - OPUS4-1180 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Osterloh, Kurt A1 - Ewert, Uwe T1 - Characterization of explosive devices by radiological methods T2 - MATEST 2001 "Non-Destructive Testing in Environmental Protection" CY - Cavtat-Dubrovnik, Croatia DA - 2001-09-23 KW - Unexploded ordnance (UXO) KW - Explosive ordnance disposal (EOD) KW - Improvised explosive devices (IED) KW - Radiological inspection KW - Image processing PY - 2001 SP - 15 EP - 26 AN - OPUS4-1163 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Czepluch, Wolf A1 - Daum, Werner A1 - Günther, Bernd T1 - Automated long-term transmission measurements of plastic optical fibres (POF) T2 - International Metrology Conference CY - Bucharest, Romania DA - 2001-09-18 PY - 2001 VL - 1 SP - 155 EP - 160 AN - OPUS4-1170 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mellmann, Günter A1 - Jansky, Hans-Joachim T1 - Recycling der Betonbrechsandfraktion T2 - Recycling-Baustoff-Tage CY - Berlin, Deutschland DA - 2001-11-08 PY - 2001 AN - OPUS4-1202 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grätz, Rainer T1 - Einfluss der EU auf das Regelwerk zum Explosionsschutz T2 - Fachtagung "Stand der Sicherheitstechnik bei Lagerung und Umschlag verflüssigter Gase" CY - Essen, Deutschland DA - 2001-10-30 PY - 2001 SP - 2 EP - 22 AN - OPUS4-1207 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brink, Arne A1 - Maierhofer, Christiane A1 - Röllig, Mathias A1 - Wiggenhauser, Herbert T1 - Auswertungsmethoden der Impuls-Thermografie zur Ortung von Fehlstellen in Betonstrukturen T2 - Thermografie-Kolloquium 2001 CY - Stuttgart, Deutschland DA - 2001-09-22 KW - Impuls-Thermografie KW - Thermografie KW - Zerstörungsfreie Prüfung KW - Abkühlvorgang KW - Bauingenieurwesen KW - Beton KW - Simulation PY - 2001 N1 - Serientitel: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. – Series title: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. IS - 77-CD SP - 1 EP - 10(?) PB - DGZfP CY - Berlin AN - OPUS4-1211 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niesel, Konrad A1 - Hoffmann, Dirk T1 - Relationship between some physico-technical characteristics of stone T2 - 2nd International Congress on Studies in Ancient Structures CY - Istanbul, Turkey DA - 2001-07-09 PY - 2001 SP - 589 EP - 598 AN - OPUS4-1149 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Berger, Georg T1 - Spongiosa-artige Formkörper und poröse Folien aus Calciumphosphat-Keramiken T2 - Statusseminar Bio-Med.Net - Tissue Engineering und zellbasierte Therapie in der Region Berlin CY - Berlin, Deutschland DA - 2001-06-29 PY - 2001 SP - 7 EP - 8 AN - OPUS4-1151 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stadthaus, Meinhard A1 - Thomas, Hans-Martin A1 - König, W. A1 - Baugatz, J. A1 - Migoun, N. A1 - Gnusin, A. T1 - Ermittlung der Eignung von Prüfmitteln für die Eindring- und Magnetpulverprüfung nach dem europäischen Normwerk T2 - Jahrestagung Zerstörungsfreie Materialprüfung 2001 CY - Berlin, Deutschland DA - 2001-05-21 PY - 2001 UR - http://www.ndt.net/article/dgzfp01/papers/p39/p39.htm N1 - Serientitel: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. – Series title: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. IS - 75-CD PB - DGZfP CY - Berlin AN - OPUS4-1302 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stadthaus, Meinhard A1 - Brose, M. A1 - Maier, G. T1 - Gefährdungen durch UV-Strahlung bei der Zerstörungsfreien Prüfung - Neue gesetzliche Grundlagen zum Schutz vor optischer Strahlung T2 - Jahrestagung Zerstörungsfreie Materialprüfung 2001 CY - Berlin, Deutschland DA - 2001-05-21 PY - 2001 UR - http://www.ndt.net/article/dgzfp01/papers/v29/v29.htm N1 - Serientitel: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. – Series title: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. IS - 75-CD PB - DGZfP CY - Berlin AN - OPUS4-1303 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Casperson, Ralf A1 - Pohl, Rainer A1 - Thomas, Hans-Martin T1 - Wirbelstrom-Prüfeinrichtung zur Qualitätskontrolle von Niob-Blechen T2 - Jahrestagung Zerstörungsfreie Materialprüfung 2001 CY - Berlin, Deutschland DA - 2001-05-21 PY - 2001 UR - http://www.ndt.net/article/dgzfp01/papers/p36/p36.htm N1 - Serientitel: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. – Series title: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. IS - 75-CD, CD-ROM PB - DGZfP CY - Berlin AN - OPUS4-1304 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thomas, Hans-Martin A1 - Pohl, Rainer A1 - Rühe, S. A1 - Krull, R. T1 - Weiterentwicklung der Wirbelstromhandprüftechnik für Schienenfehler T2 - Jahrestagung Zerstörungsfreie Materialprüfung 2001 CY - Berlin, Deutschland DA - 2001-05-21 PY - 2001 UR - http://www.ndt.net/article/dgzfp01/papers/p35/p35.htm N1 - Serientitel: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. – Series title: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. IS - 75-CD, CD-ROM PB - DGZfP CY - Berlin AN - OPUS4-1305 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thomas, Hans-Martin A1 - Pohl, Rainer T1 - Bewertung von Oberflächenschädigungen an Schienen mittels Wirbelstromverfahren T2 - Jahrestagung Zerstörungsfreie Materialprüfung 2001 CY - Berlin, Deutschland DA - 2001-05-21 PY - 2001 UR - http://www.ndt.net/article/dgzfp01/papers/v52/v52.htm N1 - Serientitel: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. – Series title: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. IS - 75-CD PB - DGZfP CY - Berlin AN - OPUS4-1306 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lüders, Günter T1 - Stand der Technik beim maschinellen Heizkeilschweißen von Dichtungsbahnen aus PEHD T2 - 18. Fachtagung "Die Sichere Deponie" CY - Würzburg, Deutschland DA - 2002-02-14 PY - 2002 UR - http://www.deponie-stief.de/pdf/fachlit_pdf/2002skz_lueders.pdf IS - 18 SP - L1 EP - L16 PB - SKZ CY - Würzburg AN - OPUS4-1292 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Klement, Ernst A1 - Rudolphi, Reinald A1 - Müller, Renate T1 - Beurteilung der Eignung von Dämmstoffen mehrschaliger Schornsteine PY - 1981 VL - T 752 SP - 1 EP - 220(?) AN - OPUS4-1235 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, Renate A1 - Rudolphi, Reinald A1 - Vater, Ernst-Joachim A1 - Herold, Christian T1 - Abrutschen von U-Bahn-Abdichtungen - Experimentelle und rechnerische Simulation PY - 1981 VL - 43 IS - 3 SP - 81 EP - 89 PB - Plaum CY - Halle, S. AN - OPUS4-1236 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rudolphi, Reinald A1 - Klement, Ernst A1 - Müller, Renate T1 - On the numerical calculation of the thermal resistance of chimneys under steady-state conditions T2 - 4th International Symposium on Industrial Chimneys CY - The Hague, Netherlands DA - 1981-01-01 PY - 1981 VL - 4 SP - 67 EP - 75 CY - Delft AN - OPUS4-1238 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rudolphi, Reinald A1 - Klement, Ernst A1 - Müller, Renate ED - Unteregger, L. T1 - Zur numerischen Berechnung der Wärmeverluste dreischaliger Schornsteine unter stationären Randbedingungen PY - 1982 VL - 34 IS - 2 SP - 7 EP - 9 CY - Kufstein AN - OPUS4-1241 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Simone A1 - Brademann-Jock, Kerstin A1 - Raabe, Hans-Joachim A1 - Kunze, Ralf T1 - Thermoluminescence - a new method to investigate weathering effects of automotive coatings T2 - 24th Meeting "Polymer Degradation Discussion Group (PDDG) - Environmental Degradation and Stabilisation of Polymers" CY - Brighton, England, UK DA - 2001-09-12 PY - 2001 IS - C10 SP - 13 AN - OPUS4-1161 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Müller, Renate T1 - Ein numerisches Verfahren zur simultanen Bestimmung thermischer Stoffeigenschaften oder Größen aus Versuchen - Anwendung auf das Heißdraht-Parallelverfahren und auf Versuche an Hausschornsteinen PY - 1989 SP - 1 EP - 130 CY - Clausthal AN - OPUS4-1255 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Rudolphi, Reinald A1 - Müller, Renate T1 - Calculs FORTRAN des champs de températures en bi- ou en tridimensionnel à l'aide d'éléments cubiques en régime stationnaire sur PC - Accompagné du logiciel STAT3DD en FORTRAN sur CD-ROM et de 29 figures PY - 2000 SP - 1 EP - 102(?) PB - Editions Universitaires CY - Fribourg AN - OPUS4-1261 LA - fra AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Rudolphi, Reinald T1 - Zur rechnerischen Übertragbarkeit der Ergebnisse von Brandprüfungen am Beispiel von Stahl- und Holzstützen PY - 1979 SP - 1 EP - 199 PB - Technische Universität CY - Berlin AN - OPUS4-1281 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Richter, Klaus T1 - Linear CIELAB - cmy* Color Workflow for the Color Office Devices and based on ISO/IEC 15775 and DIS ISO/IEC 19839-1 to 4 N2 - Four analog ISO/IEC-test charts according to ISO/IEC 15775 are designed for the test of colour copiers. The International Standard ISO/IEC 15775 includes the LAB* (CIELAB) data and many cmy* data of the colours used in the test charts. The digital ISO/IEC-test chart files include mainly cmy* colour data but also LAB* data for the CIE-test colours and are available on the recommended web servers. The files have been used for the production of the ISO/IEC-test charts in Germany and Japan. This paper uses either LAB* or cmy* data in the digital files and still the colour output is identical. With additional Output Linearisation (OL) the 16 step colour series are produced with equal spacing in CIELAB. The 16 step series are produced by linearized devices with an accuracy of less than 3 CIELAB units intended for the office environment. The CIELAB colour difference is often reduced by a factor 3 to 5 for the 16 step series on the surface of the colour solid. For the CIE-test colours which are mainly located inside the colour solid the accuracy seems to be similar compared to the accuracy of the ISO/ IEC-test chart productions in offset which is near 10 CIELAB units. The user requirement for a linear relationship between CIELAB data and cmy* data is realised. This linear CIELAB - cmy* colour workflow for offices seems to be both simple and effective. The yellowness data y*=0.5 will produce a yellow in CIELAB space visually in the middle between white W and yellow Y. This is similar for the other series, e. g. white - black. Therefore there is agreement with the basic user requirement. The linear relationship between cmy* and CIELAB has many advantages for colour image technology. Slightly different output colours compared to the intended CIELAB colours can be corrected in the digital input file by using the linear CIELAB difference of the output and the intended CIELAB colour. The CIELAB - cmy* workflow is linear which may be compared to the nonlinear rgb workflow of the International Standards IEC 61966-X. The spacing of the rgb coordinates of the Standards IEC 61966-X is incompatible with the CIELAB spacing. PY - 2001 UR - http://www.ps.bam.de/BAMCMY.PDF SP - 1 EP - 16 PB - Bundesanstalt für Materialforschung und -prüfung CY - Berlin AN - OPUS4-1375 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reinsch, Stefan A1 - Böcker, Wolfgang D. G. A1 - Bücker, Michael A1 - Seeger, Stefan A1 - Unger, Brita ED - Specht, K. T1 - Development of wood-inorganic composites with enhanced properties and environmental stability T2 - 4th International Wood and Natural Fibre Composites Symposium CY - Kassel, Germany DA - 2002-04-10 PY - 2002 VL - 4 SP - 50-1-50-6 CY - Kassel AN - OPUS4-1365 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böcker, Wolfgang D. G. A1 - Bücker, Michael A1 - Reinsch, Stefan A1 - Unger, Brita T1 - Holzverbundwerkstoffe mit verbesserten Eigenschaften N2 - Die offenporige Struktur des Holzes und dessen chemische Zusammensetzung bieten sich an, über Tränkverfahren geeignete Precursoren so an den inneren Oberflächen des Holzes zu fixieren, dass bei anschließender thermischer Behandlung ein umweltfreundlicher anorganisch-organischer Verbundwerkstoff entsteht. Aus der Literatur sind hierzu verschiedene Ansätze bekannt. - Ziel der vorliegenden Arbeit sind Verbesserungen der biologischen Beständigkeit, der Feuchtebeständigkeit unter Beibehaltung bzw. leichter Verbesserung der mechanischen Eigenschaften des Holzes. Dies wird durch eine chemische Verbindung (Haftung) zwischen den verbundbildenden Phasen Holz und Precursor und eventuell zusätzlichen Einbau von funktionellen organischen Gruppen realisiert. Als Precursoren dienen über den Sol-Gel Weg hergestellte Kieselsole, die nach vollständiger thermischer Umsetzung zu rein anorganischen Phasen (SiO2) führen. Die Sol-Gel Synthese konnte so optimiert werden, dass durch die Behandlung eine homogene Beschichtung aller Oberflächen erreicht werden kann. T2 - Integrierter Umweltschutz im Bereich der Holzwirtschaft CY - Göttingen, Deutschland DA - 2002-01-22 PY - 2002 SP - 100 EP - 102 PB - DGfH CY - München AN - OPUS4-1366 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thomas, Hans-Martin A1 - Stadthaus, Meinhard A1 - Baugatz, J. A1 - König, W. A1 - Migoun, N. P. A1 - Prokhorenko, P. P. A1 - Gnusin, A. B. T1 - Reproducibility Problem for the Procedure of Type Testing of Liquid Penetrants N2 - Apparently that the type testing procedure should be conducted under the conditions ensuring reproducibility of its outcomes. We investigated various factors effecting upon the reproducibility. To obtain quantitative characteristics of indication’s visibility the image-processing hard-and software were used. It was established that there are two main groups of these factors. The first depends on the differences between various test panels, which are used for type testing. The second one concerns the reproducibility of some stages of penetrant testing procedure (excess penetrant removing and developer application). The recommendations to increase the reproducibility of type testing are developed and illustrated experimentally. The determination of penetrant system sensitivity as a part of type testing should be conducted ensuring reproducibility of the result. We investigated some factors effecting the reproducibility. To obtain quantitative characteristics of indication’s visibility, an image processing system was used [1]. We used 3 different sets of reference blocks (rb1, rb2, rb3) corresponding to type 1 of EN ISO 3452-3 [2]. Two fluorescent penetrants with different sensitivities and the same wet solvent developer were used. It was established that the reproducibility of type testing is influenced by mainly two principal factors. First there are the differences between reference blocks. Second one concerns the reproducibility of penetrant testing procedure, especially excess penetrant removal and developer application. According to EN ISO 3452-3 a reference block for determination of sensitivity level of fluorescent penetrants consists of a set of three nickel-chrome plated panels with 10, 20 and 30 µm plating thickness. Transverse cracks are made in each panel by stretching the panels in the longitudinal direction and width to depth ratio of the cracks should be approximately 1/20. Each panel presents a certain sensitivity level, which is characterised by the level of visibility of the indication. The highest level 3 corresponds to the panel with 10 µm thickness plating. Each panel is cut longitudinally (perpendicular to the crack) so that 2 sheets (panels A and B) with nearly the same cracks will be produced. These panels A and B of a reference block are used for relative evaluation, for example to compare sensitivities of two penetrants. It is considered that the application of the same penetrant to both panels with subsequent adequate development results in the same visibility of the indications on these panels. Quantitative correlations between the abilities of the reference blocks used for determining of the sensitivity were obtained in our investigations. We used the relations between the measured values of light-fluxes from the indications of similar comparing areas on two panels. These indications correspond to certain cracks’ parts of the same total length on both comparing areas. The relations of the steps between the panel are responsible for the definition of the sensitivity groups. From our investigations it follows that the steps of the different sets are different. Besides it was established that the indication‘s visibility for the same penetrant applied on different reference blocks might have a considerable difference depending on the penetrant sensitivity: the higher penetrant’ sensitivity, the smaller is such a difference between the steps 30/20 and 20/10. For example, for rb3 the relations 30/20 and 20/10 for lower sensitive penetrant (I1) reached factor 3 comparing with factor 2 for higher sensitive penetrant (I2). Some results of the comparison between the 3 sets (rb1, rb2, rb3) investigations are summarised in Table 1 with rb1 as a reference. T2 - 8th ECNDT CY - Barcelona, Spain DA - 2002-06-17 PY - 2002 UR - http://www.ndt.net/article/ecndt02/199/199.htm VL - 8 SP - 1(?) EP - 5(?) PB - European Federation for Non-Destructive Testing CY - Barcelona AN - OPUS4-1396 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Riebe, Gundel A1 - Ostermann, Markus A1 - Pritzkow, Wolfgang A1 - Vogl, Jochen T1 - Combination of sophisticated sample digestion methods and highly accurate determination procedures shown for Sulphur in oil and Cadmium and Lead in sediment T2 - Internationale Konferenz "Trends in Sample Preparation 2002" CY - Seggau, Austria DA - 2002-06-30 PY - 2002 AN - OPUS4-1398 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ostermann, Markus A1 - Janisch, Nadine A1 - Vogl, Jochen T1 - On the determination of the moisture content in different matrix materials T2 - Internationale Konferenz "Trends in Sample Preparation 2002" CY - Seggau, Austria DA - 2002-06-30 PY - 2002 AN - OPUS4-1399 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klaffke, Dieter A1 - Wäsche, Rolf T1 - Tribological Performance of SiC and TiB2 sliding against SiC and Al2O3 T2 - 10th Nordic Symposium on Tribology ; 10th Nordtrib 2002 CY - Stockholm, Sweden DA - 2002-06-09 PY - 2002 SP - 1(?) EP - 10(?) PB - Royal Institute of Technology CY - Stockholm AN - OPUS4-1386 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klaffke, Dieter A1 - Yarim, Rasim A1 - Wäsche, Rolf T1 - Effect of pre-oxidation on friction and wear behaviour of a SiC-TiC-TiB2 composite T2 - 10th Nordic Symposium on Tribology ; 10th Nordtrib 2002 CY - Stockholm, Sweden DA - 2002-06-09 PY - 2002 SP - 1 EP - 10(?) PB - Royal Institute of Technology CY - Stockholm AN - OPUS4-1387 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klaffke, Dieter T1 - Test Concept for Tribological Characterisation of Implant Materials Prone to Fretting T2 - 10th Nordic Symposium on Tribology ; 10th Nordtrib 2002 CY - Stockholm, Sweden DA - 2002-06-09 PY - 2002 SP - 1(?) EP - 10(?) PB - Royal Institute of Technology CY - Stockholm AN - OPUS4-1388 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Walther, Wolfgang A1 - Becker, Roland A1 - Nehls, Irene A1 - Lehmann, Andreas A1 - Redlich, Christel A1 - Flemig, Sabine A1 - Dorgerloh, Ute A1 - Win, Tin A1 - Buge, Hans-Gerhard T1 - Pentchlorophenol (PCP) in Soil - Certified Reference Materials for Environmental Analysis T2 - Analytica Conference 2002 CY - Munich, Germany DA - 2002-04-23 PY - 2002 SP - 1(?) AN - OPUS4-1389 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Tscharntke, Dirk T1 - Fehlerdiagnose in der Ultraschallprüfung durch iterative Modellierung N2 - Ein Ziel der Arbeit bestand ursprünglich darin, ein Rechenmodell zur Ultraschallprüfung mit einer Evolutionsstrategie zu verknüpfen. Zunächst verlagerte sich der Schwerpunkt der Arbeit jedoch auf die Erarbeitung eines validierten und erprobten Modells, das den Anforderungen für die Verwendung der Evolutionsstrategie genügt. Aber selbst damit zeigte sich, dass ein Arbeiten mit der Evolutionsstrategie nicht ohne weiteres möglich ist. Daher wurde der Weg der iterativen Modellierung gewählt. Die Einschränkungen der verschiedenen Bewertungs- und Untersuchungsverfahren zur Fehlerdiagnose in der Ultraschallprüfung lassen in Abhängigkeit von der Prüfsituation nur eine fallweise Anwendung zu. Die erzielbaren Ergebnisse sind durch prinzipielle Grenzen, wie die orientierungsabhängigen Wechselwirkungen der Ultraschallwellen mit dem Fehler, in ihrer Genauigkeit stark begrenzt. Eine zuverlässige Bewertung ist meist durch die Zusammenfassung der Ergebnisse mit denen aus anderen ZfP- Verfahren und die Nutzung von a priori Informationen z. B. aus der Fertigungsgeschichte einer Komponente oder des Fehlerentstehungsmechanismus möglich. Die vorgeschlagene iterative Modellierung bietet dazu, wie die vorliegende Untersuchung zeigt, eine Möglichkeit. Die durch Einführung von a priori Informationen aufgestellten Fehlerhypothesen werden durch Modellrechnungen abgesichert oder wieder verworfen. Das Rechenmodell ermöglicht die Bewertung der Amplitude, der Laufzeit, der Echodynamik und des Anzeigenmusters, also aller auch bei anderen Diagnoseverfahren herangezogenen Bewertungskriterien. Die iterative Modellierung basiert auf drei Teilprozessen, der Analyse der möglichen Wechselwirkungen, der Separation dieser Wechselwirkungen in diverse Schallwege und schließlich der Synthese der auf den verschiedenen Wegen berechneten Signale zum Gesamtsignal. Die ersten beiden Teilprozesse müssen z. Zt. für jeden Prüffall neu gelöst werden und erfordern wie die Modellbedienung Expertenwissen. Die im Rahmen dieser Untersuchung erfolgten Modellmodifikationen konnten gemeinsam mit der Modellverifikation die Zuverlässigkeit der Modellrechnungen deutlich steigern. Die Berechnungen können schnell und interaktiv durchgeführt werden. Die Rechenzeit für ein TD- Bild mit 50 A- Bildern beträgt üblicherweise ein bis fünf Minuten. Durch die Kombination des Rechenmodells mit der Evolutionsstrategie wurde der Versuch unternommen, die iterative Modellierung zu systematisieren. Diese Kombination würde die Lösung des inversen Problems, d.h. die Bestimmung der Ursache für die akustische Störung, ohne Durchführung einer mathematischen Inversion ermöglichen. Der Anwendung der Evolutionsstrategie mit der hier gewählten einfachen Qualitätsfunktion steht ein hoher Zeitbedarf entgegen, ein schnelles und interaktives Arbeiten ist nicht möglich. Die Praxis erfordert die Definition einer komplexen Qualitätsfunktion, die eine Bewertung des Anzeigenmusters ermöglicht und unempfindlich auf Störeffekte reagiert. Die besondere Schwierigkeit besteht darin die Erfahrungen und die "Phantasie" eines Experten in das Modell zu integrieren. Dieser Umstand beinhaltet noch ein großes Entwicklungspotenzial. Ein gegenwärtiger Einsatz der Evolutionsstrategie erscheint daher verfrüht. Inwieweit Probleme mit in den Messdaten enthaltenen Mehrdeutigkeiten und Störanzeigen von Testblockkanten und anderen Reflektoren zukünftig überwunden werden können, kann gegenwärtig noch nicht abschließend geklärt werden. Eine zuverlässige Bewertung von kritischen Befunden mit mehreren möglichen Ursachen kann derzeit nur mit Expertenwissen über den Weg der iterativen Modellierung erfolgen. Dies ermöglicht auf einfache Weise die Einführung der a priori Informationen und gestattet ein schnelles und interaktives Arbeiten. KW - Ultraschallprüfung KW - Fehlerdiagnose KW - Iterative Modellierung KW - Echodynamikmuster KW - A priori Informationen KW - Schnelle, interaktive Rechenmodelle KW - Ultrasonic testing KW - Flaw diagnosis KW - Iterative modeling PY - 2002 SP - 1 EP - 161 PB - Technische Universität CY - Berlin AN - OPUS4-1390 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simon, Franz-Georg T1 - Recycling-orientated product development T2 - International Workshop on Ecomaterials CY - Tokyo, Japan DA - 2002-02-06 PY - 2002 SP - 86 AN - OPUS4-1356 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schultze, Karin A1 - Philipp, Rosemarie A1 - Redlich, Christel A1 - Dorgerloh, Ute A1 - Becker, Roland A1 - Win, Tin A1 - Nehls, Irene T1 - Development, preparation and certification of a reference material for the determination of chlorinated pesticides in soil T2 - Symposium "Reference Materials for Technologies in the New Millenium" CY - Berlin, BAM, Germany DA - 2000-05-22 PY - 2000 SP - 1(?) EP - 4(?) AN - OPUS4-1313 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schultze, Karin A1 - Nehls, Irene A1 - Bremser, Wolfram A1 - Becker, Roland A1 - Win, Tin T1 - Zertifiziertes Referenzmaterial "BAM-U007" - Organochlorpestizide in Boden T2 - ANAKON 2001 CY - Konstanz, Germany DA - 2001-04-04 PY - 2001 SP - 1(?) AN - OPUS4-1314 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gradt, Thomas A1 - Börner, Helmut A1 - Hübner, Wolfgang A1 - Ostrovskaya, Y. T1 - Friction and wear testing in cryogenic environment T2 - 3ème Colloque Européen sur la Technologie des Lanceurs ; 3rd European Conference on Launcher Technology CY - Strasbourg, France DA - 2001-12-11 PY - 2001 SP - 927 EP - 935 PB - CNES CY - Paris AN - OPUS4-1330 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ploska, Ute A1 - Kraus, Werner A1 - Berger, W. A1 - Lugscheider, E. A1 - Nyland, A. T1 - Calcium phosphate-containing materials in the system cati4(PO4)6-CaZr4(PO4)6 for using as coatings on titanium substrates KW - Calciumphosphat KW - Beschichtung KW - Titanträgermaterial PY - 1996 VL - 9 SP - 353 EP - 356 AN - OPUS4-1333 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erhard, Anton A1 - Bertus, Norbert A1 - Montag, Hans-Joachim A1 - Schenk, Gottfried A1 - Hintze, H. T1 - Ultrasonic Phased Array System for Railroad Axle Examination N2 - Introduction Due to the long history of railroad companies around the world, varying means of examination according to the specifications for the different railroad components have been carried out based on the general industrial progress of the country [1-3]. For more than 50 years the application of customized ultrasonic techniques for the examination of railroad components has increased, in comparison to conventional ultrasonic techniques used until to the end of 20th century. In this traditional atmosphere some accidents have disturbed the silent harmony of companies involved in the production of critical parts. More than ever high speed modern trains require modern and advanced examination techniques [4-8]. For practical application new ultrasonic techniques have been developed and optimized in co-operation with the German Railroad Company. In the present contribution the inspection of railroad axles will be described. The ultrasonic technique used for the examination is the phased array technique. The optimization of the phased array probes for the different geometries of the axles given was completed using a computer model for directivity calculations. In relation to the limited accessibility between wheel and brake angles of incidence for shear waves in the range between 28° and 72° are necessary. During the examination of the axles a a considerable amount of ultrasonic data must be stored (storage of the digitized A-scans). However, due to economic aspects the evaluation of this data should be carried out in a very short time. The whole examination of one axle should not exceed 5 minutes. Therefore we have developed a special evaluation program adapted to the particular problematic of the axle inspection. The build up of the whole inspection system was done with partners from the industry like Krautkramer and a division of the Research Department of the Deutsche Bahn AG. In this consortium the Research Department of the Deutsche Bahn AG was responsible for the specification of the inspection problem, Krautkramer for the organization of the whole technical follow up and BAM for the development and optimization of the ultrasonic inspection technique as well as for the evaluation software. Some examples concerning the optimization process will be described in the present contribution. T2 - 8th ECNDT CY - Barcelona, Spain DA - 2002-06-17 PY - 2002 UR - http://www.ndt.net/article/ecndt02/75/75.htm PB - European Federation for Non-Destructive Testing CY - Barcelona AN - OPUS4-1414 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Senoner, Mathias A1 - Unger, Wolfgang A1 - Koenders, L. A1 - Wilkening, G. T1 - Accuracy of step height determination by Atomic Force Microscopy - results of an inter-laboratory comparison T2 - 3rd International Conference European Society for Precision Engineering and Nanotechnology (euspen) CY - Eindhoven, The Netherlands DA - 2002-05-26 PY - 2002 SP - 773 EP - 776 AN - OPUS4-1415 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Daum, Werner A1 - Scholl, M. T1 - VDI/VDE-Guideline 5570 - The First Comprehensive Standard on Characterization and Testing of POF T2 - 11th POF 2002 ; 11th International Plastic Optical Fibers Conference ; 11th International POF Conference CY - Tokyo, Japan DA - 2002-09-18 PY - 2002 SP - 243 EP - 246 CY - T¯oky¯o AN - OPUS4-1418 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Döring, Günter T1 - Der Einfluss von DIN EN ISO/IEC 17025 auf die Bestimmung der spektralen Reflexionsfaktoren optischer Referenzmaterialien T2 - COSP 2002 ; Colloquium Optical Spectrometry 2002 CY - Berlin, BAM, Deutschland DA - 2002-11-11 PY - 2002 AN - OPUS4-1420 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wäsche, Rolf A1 - Naito, M. ED - Puri, V. ED - Adair, J. ED - Knobloch, C. ED - Huang, C. T1 - Electrokinetic Characterization of Aqueous Ceramic Suspensions T2 - Fine Powder Processing Conference '99 CY - State University, PA, USA DA - 1999-09-20 KW - Meßverfahren KW - Zeta Potenzial KW - Hochleistungskeramik PY - 1999 SP - 177 EP - 183 AN - OPUS4-1441 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jansen, Kirsten ED - Trubiroha, P. T1 - Einflüsse saurer Niederschläge beim künstlichen Bewittern HALS-stabilisierter Agrarfolien T2 - 22nd Colloquium of Danubian Countries on Natural and Artificial Ageing of Polymers CY - Berlin, Deutschland DA - 2001-09-16 PY - 2001 SP - 16-1-16-7 CY - Berlin AN - OPUS4-1407 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Habel, Wolfgang A1 - Bismarck, A. A1 - Ajuriagojeaskoa, E. E. A1 - Springer, J. T1 - Modification et caractérisation de la surface de fibres de verre pour son insertion postérieure dans des matériaux cimentaires PY - 1999 IS - 096 SP - 1269 EP - 1294 PB - Société de Chimie Physique CY - Paris AN - OPUS4-1455 LA - fra AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Simone A1 - Brademann-Jock, Kerstin A1 - Raabe, Hans-Joachim A1 - Schulz, Ulrich A1 - Kunze, Ralf T1 - Thermoluminescence - A new method to investigate Weathering Effects of Greenhouse Coverings T2 - 2nd International Conference on Polymer Modification, Degradation and Stabilisation (MoDeSt) CY - Budapest, Hungary DA - 2002-06-30 PY - 2002 VL - 82 IS - 2 PB - Elsevier CY - Orlando, Fla. AN - OPUS4-1448 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schneider, Thomas A1 - Meine, Kerstin A1 - Spaltmann, Dirk T1 - Influence of Hydrogen Adsorption on the Friction of Silicon T2 - WE-Heraeus Seminar Integrating Friction and Wear Research CY - Ilmenau, Germany DA - 2002-05-27 PY - 2002 SP - 63 AN - OPUS4-1450 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hitzegrad, Frank A1 - Berger, Georg T1 - Untersuchung viskoelastischer Eigenschaften von porösen biokeramischen Werkstoffen und Bestimmung der durch applikationsbedingten Medieneinfluss verursachten Eigenschaftsänderungen T2 - Kolloquium des Lehrstuhls für Technische Mechanik CY - Erlangen, Deutschland DA - 2002-07-15 PY - 2002 AN - OPUS4-1463 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Witt, Klaus ED - Kovácsné Stahl, Á. T1 - CIEDE2000 - an optimised colour-difference formula for industrial application T2 - 28 Kolorisztikai Szimpózium ; 28th Colouristic Symposium CY - Tata, Hungary DA - 2001-09-03 PY - 2001 SP - 84 EP - 88 CY - Budapest AN - OPUS4-1470 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Binkowski, Sigrid A1 - Pahl, Regina A1 - Woydt, Mathias T1 - Vergleich der Präparationsverfahren an Gefügen keramischer Werkstoffe N2 - Der Artikel beschreibt verschiedene materialographische Präparationsverfahren und zeigt Aufnahmen von einer ganzen Reihe unterschiedlicher Keramiken, die mit verschiedenen Untersuchungsmethoden gemacht wurden. PY - 2002 UR - http://www.struers.com/resources/elements/12/3699/39art2_de.pdf IS - 39 SP - 8 EP - 19 PB - Struers CY - Willich AN - OPUS4-1471 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Unger, Wolfgang T1 - Web site for information on reference materials T2 - Proceedings of the Final Meeting CY - Wiener Neustadt, Austria DA - 2002-03-04 PY - 2002 SP - 1(?) EP - 3(?) AN - OPUS4-1472 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rockland, Ulrike A1 - Plewinsky, Bodo A1 - Hieronymus, Hartmut A1 - Henschen, Philipp T1 - Gefahren bei Oxidationsreaktionen mit reinem Sauerstoff T2 - Beiträge zum Kolloquium CY - Berlin, Germany DA - 1997-05-27 PY - 1997 SP - 7 EP - 19 CY - Berlin AN - OPUS4-1487 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hieronymus, Hartmut A1 - Rockland, Ulrike A1 - Henschen, Philipp A1 - Plewinsky, Bodo T1 - Different types of heterogeneous explosion hazards during oxidation processes in the liquid phase T2 - 1st Internet Conference on Process Safety CY - --- DA - 1998-01-27 PY - 1998 IS - paper 27 PB - Prosicht GmbH CY - Hamm AN - OPUS4-1488 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Henschen, Philipp A1 - Hieronymus, Hartmut A1 - Rockland, Ulrike A1 - Wendler, Reinhold A1 - Plewinsky, Bodo T1 - Explosions and detonations of foams T2 - 9th International Symposium on Loss Prevention and Safety Promotion in the Process Industries CY - Barcelona, Spain DA - 1998-05-04 PY - 1998 VL - 2 SP - 632 EP - 640 AN - OPUS4-1489 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jansen, Kirsten A1 - Schulz, Ulrich A1 - Wachtendorf, Volker T1 - Testing the influence of acid precipitation on service life of greenhouse films T2 - 2nd International Conference on Polymer Modification, Degradation and Stabilisation (MoDeSt) CY - Budapest, Hungary DA - 2002-06-30 PY - 2002 VL - 82 IS - 2 PB - Elsevier CY - Orlando, Fla. AN - OPUS4-1544 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maultzsch, Matthias T1 - The utilization of processed building rubble - A contribution of sustainability in concrete technology T2 - Polish Concrete Days Conference CY - Szczyrk, Poland DA - 08.10.2002 PY - 2002 SP - 629 EP - 639 PB - Polski Cement CY - Kraków AN - OPUS4-1547 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wiggenhauser, Herbert T1 - NDT of Concrete Structures T2 - Workshop on NDE of concrete structures CY - Madras, India DA - 2002-12-02 KW - NDT KW - Maintenance KW - Ultrasound KW - Radar KW - Impact-Echo KW - Thermography KW - Post-Tensioned Concrete Structures PY - 2002 SP - 1 EP - 19 AN - OPUS4-1541 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Volkmar A1 - Daubitz, Ralph T1 - Bestimmung der Explosionsgrenzen von Gasen und Dämpfen - Ein Vergleich von 4 Standardverfahren PY - 2002 SP - 1(?) EP - 16(?) AN - OPUS4-1560 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Henschen, Philipp T1 - Untersuchungen von Oberflächen- und Schaumdetonationen KW - Detonation KW - Explosion PY - 1998 CY - Berlin AN - OPUS4-1494 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Hofmann, Martin T1 - Auswirkungen von Hindernissen auf Oberflächenexplosionen N2 - Um Oxidationsprozesse in der chemischen Industrie zu optimieren, wird verstärkt versucht, Luftsauerstoff durch reinen Sauerstoff zu ersetzen und den Prozessdruck zu erhöhen. Dadurch werden weitergehende sicherheitstechnische Betrachtungen notwendig. Bisherige Untersuchungen an Systemen bestehend aus einer glatten, ruhenden brennbaren Flüssigkeit unter einer Gasphase aus reinem Sauerstoff bei erhöhtem Anfangsdruck zeigten, dass in solchen Systemen nicht nur deflagrativ verlaufende Reaktionen, sondern auch detonative Reaktionen, sogenannte Oberflächendetonationen, auftreten. Bis dato wurde bei diesen Versuchsreihen hauptsächlich untersucht, unter welchen Anfangsbedingungen Oberflächendetonationen auftreten. Im Rahmen der vorliegenden Arbeit wurden die Vorgänge in einem heterogenen System, bestehend aus Toluol und Sauerstoff, systematisch untersucht. Dabei wurde eine Einteilung der gesamten Verbrennungsreaktion in unterschiedliche Stadien vorgenommen. Diese Stadien sind die Zündung, der Abbrand, die Oberflächendeflagration und die Oberflächendetonation. Mit Experimenten in einem 50 l Kugelautoklav konnte nachgewiesen werden, dass sich die Mechanismen bei einer solchen Oberflächenexplosion grundlegend von den Abläufen bei Explosionen in einem homogenen System unterscheiden. Darüber hinaus konnte nachgewiesen werden, dass Oberflächendetonationen im Gegensatz zu bisherigen Vermutungen über den gesamten untersuchten Druckbereich auftreten können. Ein weiteres Ziel der vorliegenden Arbeit war eine Untersuchung, ob mit einfachen, mechanischen Hindernissen ein sicherheitstechnisches Konzept zur Vermeidung von Oberflächendetonationen möglich ist. Dies muss nach den Ergebnissen der vorliegenden Arbeit verneint werden. Die Versuchsreihen mit unterschiedlichen Hindernissen erbrachten jedoch weitere Informationen über die Mechanismen von Oberflächenexplosionen. Diese Informationen führten zur Formulierung einer neuen Hypothese. Diese Hypothese diskutiert den Einfluss des Energieeintrags von der Flamme in die Flüssigkeit und einen sich daraus ergebenden selbstbeschleunigenden Prozessverlauf. KW - Brennbare Flüssigkeit KW - Sauerstoff KW - Verbrennung KW - Detonation PY - 2001 SP - 1 EP - 121 PB - Technische Universität CY - Berlin AN - OPUS4-1495 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz-Forberg, Bernd A1 - Nitsche, Michael T1 - Informationsmanagement - Sicherheitstechnik in der BAM T2 - VCI-Umwelttag für den Mittelstand CY - Frankfurt am Main, Deutschland DA - 2002-09-04 PY - 2002 SP - 1 EP - 21 AN - OPUS4-1496 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfeil, Norbert T1 - Ammoniumnitrat - Ursachen und Auswirkungen des Toulouse-Unfalles T2 - 4. Erfahrungsaustausch für Sachverständige nach § 29a BImSchG und Störfallbeauftragte CY - Frankfurt am Main, Deutschland DA - 2002-10-15 PY - 2002 AN - OPUS4-1498 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klobes, Peter A1 - Minor, D. B. A1 - Röhl-Kuhn, B. A1 - Zimathies, Annett A1 - Prinz, C. A1 - Leigh, S. D. A1 - Heckert, N. A. A1 - MacDonald, B. S. T1 - Porosimetrie-Standard NIST SRM 1917 / CRM BAM-P 127 - Das erste von NIST und BAM gemeinsam zertifizierte Referenzmaterial T2 - 6. Workshop über die Charakterisierung von Feinteiligen und Porösen Festkörpern CY - Bad Soden, Deutschland DA - 2002-11-14 PY - 2002 CY - Bad Soden AN - OPUS4-1500 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Peuker, Christel A1 - Geißler, Heinz T1 - Beeinflusst der Wassergehalt die Extinktionskoeffizienten der OH-Banden in den IR-Spektren wasserarmer Silicat- und Alumosilicatgläser? T2 - 76. Glastechnische Tagung CY - Bad Soden, Deutschland DA - 2002-05-27 PY - 2002 SP - 47 EP - 50 PB - DGG, Deutsche Glastechnische Gesellschaft e.V. CY - Frankfurt/M. AN - OPUS4-1501 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Yozgatli, Hakan-Peter A1 - Geißler, Heinz A1 - Zschunke, Adolf T1 - Erfahrungen aus dem Ringversuch des TC 14 der ICG zur Vergleichbarkeit IR-spektroskopischer Transmissionsmessungen an Gläsern T2 - 76. Glastechnische Tagung CY - Bad Soden, Deutschland DA - 2002-05-27 PY - 2002 SP - 238 EP - 241 PB - DGG, Deutsche Glastechnische Gesellschaft e.V. CY - Frankfurt/M. AN - OPUS4-1502 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jankowski, Lukasz T1 - Reliable Measurements of POF's Optical Properties with Low-End CCD Camera T2 - 11th POF 2002 ; 11th International Plastic Optical Fibers Conference ; 11th International POF Conference CY - Tokyo, Japan DA - 2002-09-18 PY - 2002 SP - 251 EP - 254 CY - T¯oky¯o AN - OPUS4-1578 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Appajaiah, Anilkumar A1 - Kretzschmar, Hans-Jürgen T1 - Climatic aging or degradation of plastic optical fibres (POFs) - Chemical analysis T2 - 11th POF 2002 ; 11th International Plastic Optical Fibers Conference ; 11th International POF Conference CY - Tokyo, Japan DA - 2002-09-18 PY - 2002 SP - 213 EP - 216 CY - T¯oky¯o AN - OPUS4-1579 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kautek, Wolfgang A1 - Handrea-Haller, Marlene A1 - Sahre, Mario T1 - Cobalt clusters on gold and graphite for electrochemical template nanostructuring T2 - 53th Annual meeting of the International Society of Electrochemistry CY - Düsseldorf, Germany DA - 2002-09-15 PY - 2002 SP - 1(?) PB - DECHEMA CY - Frankfurt a.M. AN - OPUS4-1582 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wehrstedt, Klaus-Dieter T1 - UN flow chart for organic peroxides and self-reactive substances - test results on formulations accepted for the transport in tanks and IBC's T2 - Energetic and Oxidising Substances (EOS) working group meeting CY - Buxton, England, UK DA - 2000-04-10 PY - 2000 AN - OPUS4-1523 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Volkmar T1 - Sicherheitstechnische Aspekte von Wasserstoff T2 - Vortrag im Forschungszentrum Jülich CY - Jülich, Deutschland DA - 2002-09-03 PY - 2002 SP - 1(?) EP - 18(?) AN - OPUS4-1526 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Simone A1 - Kunze, Ralf T1 - Thermolumineszenz-Untersuchungen zum Alterungsprozess in Polymeren T2 - GEFTA-Jahrestagung ; TA-Symposium CY - Bochum, Deutschland DA - 2002-09-18 PY - 2002 SP - 1(?) AN - OPUS4-1529 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Simone A1 - Brademann-Jock, Kerstin A1 - Raabe, Hans-Joachim A1 - Kunze, Ralf T1 - Thermoluminescence - a new method to investigate weathering effects in polymers T2 - Polydays 2002 CY - Berlin, Germany DA - 2002-09-30 PY - 2002 AN - OPUS4-1530 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wehrstedt, Klaus-Dieter T1 - Identifizierung gefährlich exotherm zersetzlicher Stoffe T2 - DECHEMA-Kurs "Sicherheit von chemischen Reaktionen" CY - Berlin und Frankfurt am Main, Deutschland DA - 2001-10-10 PY - 2001 AN - OPUS4-1503 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Michael-Schulz, Heike T1 - German regulations on ammonium nitrate and current modifications of the Directive 96/82/EC (Seveso-II) T2 - Energetic and Oxidising Substances (EOS) working group meeting CY - Verneuil-en-Halatte, France DA - 2002-03-20 PY - 2002 AN - OPUS4-1507 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wehrstedt, Klaus-Dieter A1 - Heitkamp, D. A1 - Klais, O. A1 - Wildner, W. T1 - Self-reactive substances, type G - Candidates for Class 4.2? T2 - Energetic and Oxidising Substances (EOS) working group meeting CY - Washington, DC, USA DA - 2001-03-12 PY - 2001 AN - OPUS4-1508 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wehrstedt, Klaus-Dieter A1 - Knorr, Annett T1 - Miniautoclave - test results on organic peroxides and self-reactive substances T2 - Energetic and Oxidising Substances (EOS) working group meeting CY - Washington, DC, USA DA - 2001-03-12 PY - 2001 AN - OPUS4-1509 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rudolph, Michael A1 - Wehrstedt, Klaus-Dieter A1 - Zemke, Gerhard-Reinhard T1 - Organische Peroxide in Großpackmitteln - Berechnung des Aufheizverhaltens eines im Außenfeuer stehenden IBC mit Hilfe von CFD-Methoden T2 - Tagung "Sicherheitsgerechtes Auslegen von Chemieapparaturen" CY - Frankfurt am Main, Deutschland DA - 2001-11-21 PY - 2001 AN - OPUS4-1511 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schreck, Andreas A1 - Knorr, Annett A1 - Wehrstedt, Klaus-Dieter A1 - Gmeinwieser, T. A1 - Steinbach, J. T1 - Sicherheitstechnische Untersuchungen zur Alkylierung von Wasserstoffperoxid mit verschiedenen Alkoholen T2 - 34. Sitzung des DECHEMA-Arbeitsausschusses "Sicherheitstechnische Kenngrößen" CY - Frankfurt am Main, Deutschland DA - 2001-05-17 PY - 2001 VL - 34 AN - OPUS4-1512 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wehrstedt, Klaus-Dieter T1 - Selbstzersetzliche Stoffe - Einstufung und Klassifizierung T2 - Schulungsveranstaltung CY - Pinneberg, Deutschland DA - 2001-04-10 PY - 2001 AN - OPUS4-1513 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wehrstedt, Klaus-Dieter T1 - Testing and classification of new reactive substances T2 - Energetic and Oxidising Substances (EOS) working group meeting CY - Washington, DC, USA DA - 2001-03-12 PY - 2001 AN - OPUS4-1514 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wehrstedt, Klaus-Dieter A1 - Knorr, Annett A1 - Schreck, Andreas T1 - Test results on energetic substances using the Miniautoclave T2 - Energetic and Oxidising Substances (EOS) working group meeting CY - Buxton, England, UK DA - 2000-04-10 PY - 2000 AN - OPUS4-1518 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wehrstedt, Klaus-Dieter A1 - Knorr, Annett T1 - Miniautoclave - test results on organic peroxides and self-reactive substances T2 - Energetic and Oxidising Substances (EOS) ad hoc group meeting CY - Tsukuba, Japan DA - 2000-11-13 PY - 2000 AN - OPUS4-1519 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wehrstedt, Klaus-Dieter T1 - Identifizierung explosionsfähiger Stoffe T2 - DECHEMA-Kurs "Sicherheit chemischer Reaktionen" CY - Berlin, Deutschland DA - 2000-10-09 PY - 2000 AN - OPUS4-1522 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kipphardt, Heinrich A1 - Recknagel, Sebastian T1 - Measurement of Nitrogen in Steel by Carrier Gas Hot Extraction - a Challenge in Calibration T2 - 6th International Workshop on progress in analytical chemistry in the steel and metals industries CY - Luxembourg, Luxembourg DA - 2002-05-14 PY - 2002 SP - 1(?) AN - OPUS4-1629 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kipphardt, Heinrich A1 - Matschat, Ralf T1 - Development of SI-traceable standards of high metrological quality for chemical analysis of the elements T2 - Towards an integrated infrastructure for measurements CY - Warszawa, Poland DA - 2002-06-18 PY - 2002 SP - 66 EP - 67 AN - OPUS4-1631 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Göllner, J. A1 - Burkert, Andreas A1 - Heyn, Andreas T1 - Korrosionsprüfung von PVD/CVD-Schichten T2 - 11. Sommerkurs Werkstofftechnik CY - Magdeburg, Deutschland DA - 2002-06-14 PY - 2002 SP - 87 EP - 100 PB - Univ. CY - Magdeburg AN - OPUS4-1618 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heyn, Andreas A1 - Göllner, J. A1 - Burkert, Andreas T1 - Innovation in der Korrosionsdiagnostik mit Hilfe elektrochemischer Rauschmessungen T2 - 11. Sommerkurs Werkstofftechnik CY - Magdeburg, Deutschland DA - 2002-06-14 PY - 2002 SP - 191 EP - 204 PB - Univ. CY - Magdeburg AN - OPUS4-1620 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kautek, Wolfgang A1 - Handrea-Haller, Marlene A1 - Sahre, Mario A1 - Conradi, Andrea A1 - Neubauer, A. A1 - Sleytr, U.B. T1 - Electrochemistry of nano-scale bacterial surface protein layers on gold T2 - 53th Annual meeting of the International Society of Electrochemistry CY - Düsseldorf, Germany DA - 2002-09-15 PY - 2002 N1 - Geburtsname von Handrea-Haller, Marlene: Handrea, M. - Birth name of Handrea-Haller, Marlene: Handrea, M. SP - 1(?) PB - DECHEMA CY - Frankfurt a.M. AN - OPUS4-1583 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krüger, Jörg A1 - Bonse, Jörn A1 - Lenzner, Matthias T1 - Modification and Ablation of Semiconductors by Femtosecond Laser Pulses N2 - Physical and chemical phenomena resulting from irradiation of silicon and indium phosphide with ultrashort laser pulses (~100fs) were investigated with respect to the difference between single- and multiple-pulse treatment. In the single-pulse case, several processes were identified: modification, recrystallization and ablation. All processes exhibit a distinct treshold behaviour. A two photon-absorption coefficient can be determined from a single spatial ablation profile. Accumulation effects were observed for multi-pulse illumination. Different morphological features like bubbles, rippels and microcolumns were found. PY - 2002 VL - 5 IS - 2 SP - 437 EP - 461 PB - Transworld Research Network CY - Trivandrum AN - OPUS4-1585 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kautek, Wolfgang A1 - Daminelli-Widany, Grazia A1 - Krüger, Jörg T1 - Femtosecond and Nanosecond Pulse Laser Electrochemistry of Aluminium Alloys T2 - 53th Annual meeting of the International Society of Electrochemistry CY - Düsseldorf, Germany DA - 2002-09-15 PY - 2002 SP - 1(?) PB - DECHEMA CY - Frankfurt a.M. AN - OPUS4-1586 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kautek, Wolfgang A1 - Rudolph, Pascale A1 - Nofz, Marianne T1 - ESR-Untersuchungen von Barium-Alumo-Borosilikatglas nach Wechselwirkung mit Ultrakurzpuls-Laserstrahlung T2 - Bunsentagung 2002 ; Industrie-Symposium Industrielle Anwendungen der NMR: Struktur und Dynamik ; 101. Hauptversammlung der Deutschen Bunsen-Gesellschaft für Physikalische Chemie CY - Potsdam, Germany DA - 2002-05-09 PY - 2002 IS - 101 SP - 1(?) CY - Potsdam AN - OPUS4-1587 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kautek, Wolfgang A1 - Krüger, Jörg A1 - Lenzner, Matthias A1 - Martin, Sven A1 - Lenner, M. A1 - Spielmann, C. A1 - Fiedler, A. ED - Meunier, M. T1 - Single- and multi-pulse femtosecond laser ablation of optical filter materials N2 - Commercially available absorption filters (Schott BG18 and BG36) were investigated with respect to their single- and multi-pulse ablation threshold using laser pulses from a Ti:Sapphire laser in the range between 30 and 340 fs. It could be observed, that the threshold fluence decreases for shorter pulse durations. The similarity of the measured multi-pulse threshold fluences with those of undoped glass material (around 1 J/cm^2 for a pulse duration of 30 fs) suggests that, for very short pulses, the threshold is independent on the doping level and therefore, linear absorption does not significantly contribute to laser-induced damage. For >100 pulses per spot and all pulse durations applied, the threshold fluences saturate. This independence on the number of applied pulses leads to technically relevant damage threshold values. T2 - Symposium D - European Materials Research Society CY - Strasbourg, France DA - 2002-06-18 PY - 2002 UR - http://www.emrs-strasbourg.com/files/pdf/2002_SPRING/02_Prog_Dv2.pdf N1 - Serientitel: Applied surface science – Series title: Applied surface science VL - 208/209.2003,1 IS - 1 SP - 1(?) PB - Elsevier CY - Amsterdam AN - OPUS4-1588 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kautek, Wolfgang A1 - Puchinger, L. A1 - Leichtfried, D. A1 - Pentzien, Simone ED - Meunier, M. T1 - Laser interaction with parchment in the near-ultraviolet and near-infrared wavelength range N2 - A detailed diagnostic study of the interaction of nanosecond laser pulses from the near-ultraviolet into the near-infrared wavelength range with various types of contemporary and ancient parchments is presented. The advantages of laser cleaning due to the absence of chemical agents, spectroscopic selectivity, micro-precision, computer-aided handling can only be verified when physico-chemical diagnostics guarantee destructionless processing. Scanning Electron Microscopy (SEM) data are correlated with morphological changes in dependence on the laser fluence and wavelength. The question, to what extent the chemical degradation of collagen is affected by various laser treatment parameters, could be resolved by Transmission Electron Microscopy (TEM) of collagen fibres collected from the outermost laser-exposed surface layer. It is also shown how Diffuse Reflectance Infrared Fourier Transform Spectroscopy (DRIFT), and Pyrolysis Capillary Gaschromatography (PY-CGC) can be employed in the chemical diagnostics of laser cleaning of parchment. This study suggests that the ageing status of parchment artefacts plays a major role in assessing the laser cleaning limits. T2 - Symposium D - European Materials Research Society CY - Strasbourg, France DA - 2002-06-18 PY - 2002 UR - http://www.emrs-strasbourg.com/files/pdf/2002_SPRING/02_Prog_Dv2.pdf N1 - Serientitel: Applied surface science – Series title: Applied surface science VL - 208/209.2003,1 IS - 1 SP - 1(?) PB - Elsevier CY - Amsterdam AN - OPUS4-1590 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kautek, Wolfgang A1 - Daminelli-Widany, Grazia T1 - Interfacial Processes during Pulse Laser Ablation of Oxides in Electrolytic Contact T2 - Bunsentagung 2002 ; Industrie-Symposium Industrielle Anwendungen der NMR: Struktur und Dynamik ; 101. Hauptversammlung der Deutschen Bunsen-Gesellschaft für Physikalische Chemie CY - Potsdam, Germany DA - 2002-05-09 PY - 2002 IS - 101 SP - 1(?) CY - Potsdam AN - OPUS4-1591 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kautek, Wolfgang A1 - Handrea-Haller, Marlene A1 - Sahre, Mario A1 - Neubauer, A. A1 - Sleytr, U.B. T1 - Nanoscale Bacterial Surface Layer Protein Crystallization on Gold T2 - Bunsentagung 2002 ; Industrie-Symposium Industrielle Anwendungen der NMR: Struktur und Dynamik ; 101. Hauptversammlung der Deutschen Bunsen-Gesellschaft für Physikalische Chemie CY - Potsdam, Germany DA - 2002-05-09 PY - 2002 N1 - Geburtsname von Handrea-Haller, Marlene: Handrea, M. - Birth name of Handrea-Haller, Marlene: Handrea, M. IS - 101 SP - 1(?) CY - Potsdam AN - OPUS4-1592 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beck, Uwe A1 - Reiners, Georg A1 - Bach, Reinhard T1 - Recycling von beschichteten Bauteilen N2 - R. Bach, U. Beck, G. Reiners Recycling von beschichteten Bauteilen Branchen-, produkt- und verfahrensübergreifende Literaturstudie zum Stand und zu den Möglichkeiten des Recyclings von beschichteten Bauteilen 32 S., ISBN 3-89701-522-6, 2000, Euro 11,50 T2 - 10. Neues Dresdner Vakuumtechnisches Kolloquium (NDVaK) CY - Dresden, Deutschland DA - 2002-10-17 PY - 2002 SP - 176 EP - 179 PB - DTVa CY - Dresden AN - OPUS4-1653 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kley, Gerd A1 - Köcher, Peter A1 - Brenneis, Rudolf A1 - Grothe, G. T1 - Möglichkeiten der Esterölherstellung aus Altfetten durch enzymatische Altfettalkoholyse T2 - DBU-Meeting "Verbundvorhaben Biokatalyse" CY - Osnabrück, Deutschland DA - 2002-04-15 PY - 2002 SP - 1 EP - 7 AN - OPUS4-1662 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz, Ulrich A1 - Klimmasch, T. ED - Storey, R. F. T1 - The Influence of Natural and Artificial Weathering on the Scratch and Mar Resistance of Automotive Coatings T2 - 29th International Waterborne, High-Solids, and Powder Coatings Symposium CY - New Orleans, LA, USA DA - 2002-02-06 PY - 2002 PB - Univ. CY - Hattiesburg, Miss. AN - OPUS4-1644 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz, Ulrich ED - Trubiroha, P. T1 - Influence of temperature, humidity and wettness on photodegradation T2 - 22nd Colloquium of Danubian Countries on Natural and Artificial Ageing of Polymers CY - Berlin, Germany DA - 2001-09-16 PY - 2001 SP - 1(?) CY - Berlin AN - OPUS4-1648 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz, Ulrich ED - Trubiroha, P. T1 - Simulation of acid precipitation and their influence on photodegradation T2 - 22nd Colloquium of Danubian Countries on Natural and Artificial Ageing of Polymers CY - Berlin, Germany DA - 2001-09-16 PY - 2001 SP - 1(?) CY - Berlin AN - OPUS4-1649 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eberstein, Markus T1 - Zur Permittivität oxidischer Gläser im Mikrowellenbereich T2 - 76. Glastechnische Tagung CY - Bad Soden, Deutschland DA - 2002-05-27 PY - 2002 SP - 213 EP - 217 PB - DGG, Deutsche Glastechnische Gesellschaft e.V. CY - Frankfurt/M. AN - OPUS4-1650 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eberstein, Markus A1 - Dernovsek, O. A1 - Nicolaides, Dagmar A1 - Schiller, Wolfgang Arno T1 - Modifikation von La2O3-B2O3-TiO2-Gläsern zur Einstellung von Mikrowelleneigenschaften niedrigsinternder Dielektrika T2 - 75. Glastechnische Tagung CY - Wernigerode, Deutschland DA - 2001-05-21 PY - 2001 SP - 301 EP - 305 PB - DGG, Deutsche Glastechnische Gesellschaft e.V. CY - Frankfurt/M. AN - OPUS4-1651 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eberstein, Markus A1 - Schiller, Wolfgang Arno A1 - Drüe, K.-H. A1 - Thust, H. T1 - Design and characterization of microwave LTCC modified by high permittivity glasses T2 - IMAPS Advanced Technology Workshop on Ceramic Applications for Microwave and Photonic Packaging CY - Providence, RI, USA DA - 2002-05-02 PY - 2002 SP - 1 EP - 6 CY - Washington, DC AN - OPUS4-1652 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Matschat, Ralf A1 - Kipphardt, Heinrich T1 - BAM System of Primary Pure Elements - Aim and Current State T2 - CCQM Annual Meeting of Inorganic Working Group CY - Ottawa, Canada DA - 2002-10-09 PY - 2002 AN - OPUS4-1603 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wachtendorf, Volker T1 - Natürliche und künstliche Alterung von Kunststoffen und Beschichtungen durch Witterungseinflüsse und ihre Analyse T2 - BAM-Kolloquium 2002 CY - Berlin, BAM, Deutschland DA - 2002-04-17 PY - 2002 SP - 1(?) AN - OPUS4-1607 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kipphardt, Heinrich A1 - Dudzus, Thomas A1 - Meier, Klaus A1 - Recknagel, Sebastian A1 - Hedrich, Martina A1 - Matschat, Ralf T1 - The measurement of O and N by classical carrier gas hot extraction (HE) - Carrier gas hot extraction after activation with photons T2 - CENAM CY - Mexico City, Mexico DA - 2002-01-28 PY - 2002 AN - OPUS4-1610 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kipphardt, Heinrich A1 - Matschat, Ralf T1 - Preparation of primary calibration substances - method development for trace analysis T2 - CENAM CY - Mexico City, Mexico DA - 2002-01-28 PY - 2002 AN - OPUS4-1611 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Buge, Hans-Gerhard A1 - Becker, Roland A1 - Nehls, Irene T1 - The preparation and characterization of solid matrix reference materials for the trace analysis of organic environmental pollutants - relevant aspects of quality management N2 - Feste Referenzmaterialien für die Spurenanalytik umweltrelevanter organischer Schadstoffe erfordern aufgrund der geringen thermischen Belastbarkeit der Analyten besondere Aufarbeitungsstrategien für die Herstellung repräsentativer Teilproben. Das in der Fachgruppe I.2 seit 1994 für diesen Zweck systematisch aufgebaute technologische Instrumentarium wird vorgestellt, und das im Laufe der Jahre angesammelte Know How wird anhand von Beispielen vermittelt. Das im Laboratorium I.21 entwickelte Qualitätssystem für eine optimale Logistik der Arbeitsabläufe der Probenherstellung und -verwaltung sowie für eine bedarfsgerechte Charakterisierung der Materialien wird ausführlich erläutert. Bezüglich der Verwendung der Referenzmaterialien wird herausgestellt, daß es zwei gleichberechtigte Anwendungsrichtungen gibt: die interne Qualitätskontrolle mit zertifizierten Referenzmaterialien (ZRM, z.B. für die Methodenvalidierung) und die externe Qualitätskontrolle (Proficiency Testing = Kompetenzbewertung von Prüflaboratorien). Referenzmaterialien für das Proficiency Testing, die im Umweltbereich in viel größeren Stückzahlen umgesetzt werden können als ZRM, weisen bezüglich Homogenität und Charakterisierung die gleichen Qualitätskriterien wie ZRM auf. Diese Materialien haben - auch im internationalen Maßstab - stark an Bedeutung gewonnen. Ein englisches Abstract gibt es nicht, aber eine Grobgliederung zur Vortragsankündigung: This lecture includes: · the technological and logistical aspects of reference material preparation and sub-sampling and subsequent sample management, · appropriate measurement strategies for homogeneity and stability studies, · the use of relevant statistical tests to evaluate those measurement data, · the organisation of interlaboratory studies based on traceable measurements T2 - CENAM CY - Querétaro, Mexico DA - 2002-03-01 PY - 2002 AN - OPUS4-1612 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kautek, Wolfgang A1 - Handrea-Haller, Marlene A1 - Sahre, Mario T1 - Nano-sized Cobalt Clusters on Gold and Graphite Electrodes T2 - Bunsentagung 2002 ; Industrie-Symposium Industrielle Anwendungen der NMR: Struktur und Dynamik ; 101. Hauptversammlung der Deutschen Bunsen-Gesellschaft für Physikalische Chemie CY - Potsdam, Germany DA - 2002-05-09 PY - 2002 N1 - Geburtsname von Handrea-Haller, Marlene: Handrea, M. - Birth name of Handrea-Haller, Marlene: Handrea, M. IS - 101 SP - 1(?) CY - Potsdam AN - OPUS4-1593 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz T1 - Zur praxisorientierten Berechnung der Steifigkeit und Dämpfung von Fundamenten und Fahrwegen T2 - D-A-CH-Tagung 2001 CY - Innsbruck, Österreich DA - 2001-09-19 PY - 2001 SP - 225 EP - 232 CY - Innsbruck AN - OPUS4-1596 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Matschat, Ralf A1 - Kipphardt, Heinrich A1 - Recknagel, Sebastian A1 - Noack, Siegfried ED - Abiko, K. ED - Takaki, S. T1 - Activities of Division "Inorganic Chemical Analysis; Reference Materials" of BAM in the Field of Analysis of Metals T2 - 9th international conference on ultrahigh-purity base metals CY - Sendai, Japan DA - 2002-10-14 PY - 2002 SP - 297 EP - 302 CY - Sendai AN - OPUS4-1602 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Senoner, Mathias T1 - Qualitätssicherung in der Nanoanalytik T2 - Hannover-Messe CY - Hannover, Deutschland DA - 2002-04-15 PY - 2002 SP - 1(?) AN - OPUS4-1733 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Korzen, Manfred A1 - Ziener, Kai-Uwe A1 - Riemer, Sven A1 - Magonette, G. A1 - Buchet, P. ED - Ural, O. ED - Abrantes, V. ED - Tadeu, A. T1 - Some remarks on the substructuring method applied to fire resistance tests of columns N2 - In fire resistance tests, building elements are considered as stand-alone elements without interaction with the surrounding building. As a contribution to overcome the situation, the application of the substructuring method has been adopted to fire engineering. The paper gives some remarks on the aforementioned experimental method. The analysis is based on the results of two built-in column fire resistance tests, i.e. one test with an unprotected column at the ground floor of the 8-storey steel framed building at Cardington and another test at BAM with an unprotected column and simulated axial restraining stiffness by the substructuring method. T2 - 30th IAHS World Congress on Housing ; Housing Construction CY - Coimbra, Portugal DA - 09.09.2002 KW - Fire engineering KW - Fire resistance KW - Computer supported testing KW - Hybrid method PY - 2002 SN - 972-9027-31-5 VL - 3 SP - 1601 EP - 1607 CY - Coimbra, Portugal AN - OPUS4-1757 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ulrich, Armin A1 - Heller, Winfried T1 - BAM-Liste 2001 - Anwendung und Hilfsmittel für sichere Tanktransporte T2 - Gefahrgut-Technik-Tage Berlin 2002 "Innovative Tanktechnik" CY - Berlin, Deutschland DA - 2002-11-14 PY - 2002 SP - 1(?) EP - 20(?) PB - Storck-Akademie CY - Hamburg AN - OPUS4-1762 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Habel, Wolfgang T1 - Lehrter Bahnhof Berlin - Neue optische Messverfahren für das Langzeitmonitoring und für die Baustoffcharakterisierung T2 - Technische Zementseminare 2002 "High-Tech-Baustoff Beton, Besondere Betone für besondere Bauwerke" CY - Schwerin, Deutschland DA - 2002-10-23 PY - 2002 SP - 1(?) EP - 20(?) AN - OPUS4-1726 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mietz, Jürgen A1 - Raupach, M. A1 - Goltermann, P. T1 - Integrated Monitoring System for Reinforced Concrete Structures T2 - 1st FIB congress CY - Osaka, Japan DA - 2002-10-13 KW - Reinforcement corrosion KW - Sensors KW - Inspection KW - Maintenance KW - Bridge management PY - 2002 IS - 15 SP - 29 EP - 38 CY - Osaka AN - OPUS4-1727 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mietz, Jürgen A1 - Isecke, Bernd A1 - Fischer, Joachim T1 - Long-term experiences with cathodic corrosion protection of steel reinforced concrete structures T2 - 15th International Corrosion Congress CY - Granada, Spain DA - 2002-09-22 PY - 2002 PB - CSIC, Spanish Council for Scientific Research CY - Madrid AN - OPUS4-1728 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kautek, Wolfgang A1 - Martin, Sven A1 - Krüger, Jörg A1 - Lenzner, Matthias A1 - Fiedler, A. ED - Meunier, M. T1 - Femtosecond laser multi-pulse interaction with optical filters and fabrics N2 - Optical filters and fabrics are important parts of laser safety equipment such as goggles and curtains. A choice of these materials with varying absorption spectra is investigated with respect to their resistance to Ti:sapphire femtosecond laser radiation (800 nm wavelength, 1 kHz repetition rate). Pulse durations down to 30 fs and multiple-pulse irradiation conditions are employed to evaluate technically relevant damage thresholds. The ablation threshold fluences of the absorbing filters are comparable to those observed for transparent materials with 30-fs-pulses. These investigations together with scanning electron microscopy of the surface morphology after laser treatment provide insight into the interaction mechanism of the short pulses with the materials. T2 - Symposium D - European Materials Research Society CY - Strasbourg, France DA - 2002-06-18 PY - 2002 UR - http://www.emrs-strasbourg.com/files/pdf/2002_SPRING/02_Prog_Dv2.pdf N1 - Serientitel: Applied surface science – Series title: Applied surface science VL - 208/209.2003,1 IS - 1 SP - 1(?) PB - Elsevier CY - Amsterdam AN - OPUS4-1730 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kautek, Wolfgang A1 - Daminelli-Widany, Grazia A1 - Krüger, Jörg ED - Meunier, M. T1 - Ultrashort pulse laser interaction with anodic metal oxide layers in electrolyte contact N2 - The removal and accelerated corrosion monitoring of metal coating systems is of general interest in materials science and engineering technology. The femtosecond and nanosecond laser ablation and delamination at 800 nm and 532 nm, respectively, of anodic oxide layers on aluminium alloys in electrolyte contact were investigated. Laser-induced modifications of the oxide layer resulted in an ionic contact between electrolyte and metal, which produced a current transient and thus allowed the in-situ electrochemical monitoring of the modification. Oxide coatings with different optical properties, almost transparent and opaque, were examined. The transparent anodic oxides showed contrasting ablation mechanisms in the nanosecond and femtosecond pulse duration regime: nanosecond pulses caused spallation, whereas femtosecond treatment led to ablation. Current signals measured in the transparent film were consistent with light absorption below the metal-oxide interface and with film spallation. Irradiation of the opaque coating yielded ionic current transients within the so-called shock-affected-zone of the oxide layer. This investigation provided insight into the role of the penetration depth of light and the heat-affected zone, the extent of the shock-affected zone, and the defect formation in the coating and at the solid-solid interface between metal and oxide. T2 - Symposium D - European Materials Research Society CY - Strasbourg, France DA - 2002-06-18 PY - 2002 UR - http://www.emrs-strasbourg.com/files/pdf/2002_SPRING/02_Prog_Dv2.pdf N1 - Serientitel: Applied surface science – Series title: Applied surface science VL - 208/209.2003,1 IS - 1 SP - 1(?) PB - Elsevier CY - Amsterdam AN - OPUS4-1731 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kautek, Wolfgang A1 - Rudolph, Pascale A1 - Brzezinka, Klaus-Werner A1 - Wäsche, Rolf ED - Meunier, M. T1 - Physical chemistry of the femtosecond and nanosecond laser-material-interaction with SiC and a SiC-TiC-TiB2 composite ceramic compound N2 - The interaction of nanosecond laser pulses in the ultraviolet wavelength range and femtosecond laser pulses in the near-infrared region with the direct semiconductor SiC and the composite compound SiC-TiC-TiB2 was investigated in respect to resulting physicochemical processes. Surface analytical techniques, such as XPS, µ-Raman, and EDX were used to identify the chemical changes between untreated and laser-treated areas. Single-pulse irradiation led to material modifications in the condensed state in most instances. Multi-pulse results differed depending on the pulse duration. In the nanosecond case, melting of the surface and redeposited material (debris) were observed. With femtosecond pulses instead, only negligible melting and few debris could be detected. Additionally, periodic structures (ripples) appeared, with parallel orientation and in most cases two different periodicities for a particular material. Laser ablation of all the studied compound materials exhibited preferential ablation of the lighter component elements. Crystal structure changes of the irradiated surface were observed as a consequence of laser-induced melting and resolidification. An oxidation process interfered with all this processes so that unstoichiometric oxides were formed. T2 - Symposium D - European Materials Research Society CY - Strasbourg, France DA - 2002-06-18 PY - 2002 UR - http://www.emrs-strasbourg.com/files/pdf/2002_SPRING/02_Prog_Dv2.pdf N1 - Serientitel: Applied surface science – Series title: Applied surface science VL - 208/209.2003,1 IS - 1 SP - 1 PB - Elsevier CY - Amsterdam AN - OPUS4-1732 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erhard, Anton A1 - Boehm, Rainer A1 - Tessaro, Ute A1 - Wüstenberg, Hermann T1 - Characterization and sizing of defects in the cladding area using ultrasonic methods T2 - 3rd International Conference on NDE in Relation to Structural Integrity for Nuclear and Pressurized Components CY - Seville, Spain DA - 2001-11-14 PY - 2002 CY - Seville AN - OPUS4-1748 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Novak, Pavel A1 - Liebich, R. A1 - Gasch, R. T1 - Numerical Simulation of a Multi-Angular Retainer Bearing with Regard to Contact Forces T2 - 9th International Symposium on Transport Phenomena and Dynamics of Rotating Machinery ; ISROMAC-9 CY - Honolulu, HI, USA DA - 2002-02-10 PY - 2002 SP - 1 EP - 8 CY - Osaka AN - OPUS4-1749 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Grätz, Rainer A1 - Schmidt, Dirk A1 - Schalau, Bernd T1 - Weiterentwicklung des Dokumentationssystems zum Stand der Sicherheitstechnik für sicherheitstechnisch bedeutsame Industrieanlagen - Teilvorhaben: Anlagen zur Lagerung und Umschlag von Flüssiggas (Forschungsbericht 297 48 903 / 03) N2 - Im Rahmen des FE-Vorhabens wurde das Dokumentationssystem zum Stand der Sicherheitstechnik (DOSIS) durch das Teilvorhaben „Anlagen zur Lagerung und Umschlag von Flüssiggas“ erweitert. Anhand von relevanten Gesetzen, Verordnungen, Technischen Regeln usw. und den Erfahrungen aus der Begutachtung von Flüssiggasanlagen wurden die sicherheitstechnischen Anforderungen entsprechend dem vorgegebenen Datenbankmodell dokumentiert. Hierzu wurde eine spezifische Vorgehensweise entwickelt, um die komplexen Anlagenkonzepte für die Eingabe in das Dokumentationsystem zu systematisieren. Auf die Anwendungsgrenzen des Dokumentationssystems, die erforderlichen Folgearbeiten zum inhaltlichen und informationstechnischen Abgleich aller Teilprojekte und die Notwendigkeit der Aktualisierung der Datenbank unter dem Gesichtspunkt der in nahen Zukunft zu erwartenden europäischen Harmonisierung der sicherheitsrelevanten Vorschriften ist hingewiesen worden. KW - Sicherheitstechnik KW - Störfallverordnung KW - Anlagensicherheit KW - Datenbank PY - 2001 SP - 91 EP - 112 PB - Umweltbundesamt CY - Dessau-Roßlau AN - OPUS4-1713 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Volkmar T1 - Oxidizing ability of gases and gas mixtures - Proposal for a test method to determine Ci coefficients T2 - ISO/TC58/SC2 meeting CY - Luxemburg, Luxemburg DA - 1998-01-26 PY - 1998 IS - ISO/TC58/SC2 AN - OPUS4-1684 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Volkmar T1 - Oxidationspotential von Gasen und Gasgemischen T2 - 30. Sitzung des DECHEMA/GVC-AA "Sicherheitstechnische Kenngrößen" CY - Frankfurt am Main, Deutschland DA - 1998-04-27 PY - 1998 CY - Frankfurt am Main AN - OPUS4-1686 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Volkmar A1 - Schulz, Stefan A1 - Dietlen, Siegmund T1 - Classification of gas mixtures for application in process safety, storage and transport - An experimental method to determine Tci values T2 - 9th International Symposium on Loss prevention and safety promotion in the process industries CY - Barcelona, Spain DA - 1998-05-04 PY - 1998 VL - 1 SP - 267 EP - 274 AN - OPUS4-1687 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Volkmar T1 - Oxidizing ability of gases and gas mixtures - Error calculation T2 - ISO/TC58/SC2 meeting CY - Berlin, Germany DA - 2000-03-21 PY - 2000 IS - ISO/TC58/SC2 AN - OPUS4-1689 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Volkmar T1 - Ermittlung von Sauerstoffgrenzkonzentrationen für brennbare Gase und Dämpfe T2 - DIN/FAM/DECHEMA-Ausschusssitzung "Explosionsgrenzen-Standardisierung" CY - Braunschweig, Deutschland DA - 2000-04-03 PY - 2000 AN - OPUS4-1690 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Volkmar T1 - Entzündlichkeit von Gasen und Gasgemischen N2 - In der vorliegenden Arbeit wird die sicherheitstechnische Eigenschaft "Entzündlichkeit" von Gasen und Gasgemischen vorgestellt. Die Definitionen und Prüfverfahren in den unterschiedlichen technischen Rechtsbereichen werden erläutert. Zur Klassifizierung von Gasgemischen in kleineren Mengen ist sowohl im europäischen Gefahrstoff-, als auch im Gefahrgutrecht ein Rechenverfahren nach ISO 10156, Nr. 4.6, zulässig. Für die Anwendung des Rechenverfahrens benötigt man Stoffkenngrößen (Tci, Kk), die im Anhang zur ISO 10156 für einige Stoffe aufgelistet sind. Im Rahmen einer Forschungskooperation wurden im europäischen Kernforschungszentrum (CERN) in Genf, an der Uni-GH Paderborn und in der BAM Explosionsbereiche von Dreistoffsystemen (Brenngas, Inertgas, Luft) nach DIN 51649 bestimmt, aus denen sich Tci- sowie KK-Werte berechnen lassen. Die so mit einheitlichen Apparaturen und Prüfverfahren ermittelten Werte weichen z.T. erheblich von den Angaben der ISO 10156 ab. Im letzten Abschnitt dieser Arbeit werden Druck- und Temperatureinfluss auf die Entzündlichkeit diskutiert. T2 - 5. Fachtagung Anlagen-, Arbeits- und Umweltsicherheit CY - Köthen, Deutschland DA - 2000-11-09 PY - 2000 SP - 227 EP - 234 PB - VDI-Gesellschaft Verfahrenstechnik und Chemieingenieurwesen CY - Düsseldorf AN - OPUS4-1691 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hieronymus, Hartmut A1 - Dietlen, Siegmund A1 - Plewinsky, Bodo A1 - Schröder, Volkmar T1 - Explosions- und Detonationsphänomene von 1,1,1,2-Tetrafluorethan/Luft-Gemischen T2 - DECHEMA-AA "Sicherheitstechnische Kenngrößen" CY - Frankfurt am Main, Deutschland DA - 1995-11-16 PY - 1995 CY - Frankfurt am Main AN - OPUS4-1676 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Molnarne, Maria A1 - Dietlen, Siegmund A1 - Funke, S. A1 - Schröder, Volkmar T1 - Beurteilung der Brennbarkeit von Gasgemischen anhand von Dreistoffdiagrammen - Vergleich mit der Methode nach der Gefahrstoffverordnung T2 - Dechema-Jahrestagung 1996 CY - Wiesbaden, Deutschland DA - 1996-05-21 PY - 1996 VL - 2 SP - 76 PB - DECHEMA CY - Frankfurt am Main AN - OPUS4-1677 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Volkmar A1 - Dietlen, Siegmund A1 - Stickling, J. A1 - Rennhack, R. T1 - Explosionsgrenzen von Brenngas/Inertgas/Luft-Gemischen unter Druck T2 - Dechema-Jahrestagung 1996 CY - Wiesbaden, Deutschland DA - 1996-05-21 PY - 1996 VL - 2 SP - 77 PB - DECHEMA CY - Frankfurt am Main AN - OPUS4-1678 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stickling, J. A1 - Dietlen, Siegmund A1 - Schröder, Volkmar A1 - Rennhack, R. T1 - Ein Simulationsmodell zur Berechnung von Explosionsgrenzen - Vergleich mit experimentell ermittelten Werten von Brenngas/Inertgas/Luft-Gemischen bei Anfangsdrücken bis 100 bar T2 - Beiträge von der Sitzung des DECHEMA-Arteitsausschusses "Gas- und Flammenreaktionen" CY - Frankfurt am Main, Deutschland DA - 1996-01-18 PY - 1996 PB - DECHEMA CY - Frankfurt a.M. AN - OPUS4-1679 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Volkmar T1 - Klassifizierung von Gasgemischen - ein Verfahren zur experimentellen Bestimmung von Tci-Werten T2 - Sicherheitstechnische Kenngrößen CY - Frankfurt am Main, Deutschland DA - 1997-02-25 PY - 1997 CY - Frankfurt am Main AN - OPUS4-1680 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Volkmar T1 - Klassifizierung von Gasgemischen nach nationalem und internationalem Gefahrgut- und Gefahrstoffrecht - Schwierigkeiten bei der Anwendung der Norm ISO 10156 T2 - BAM-Kolloquium 1997 CY - Berlin, Deutschland DA - 1997-05-21 PY - 1997 AN - OPUS4-1681 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stickling, J. A1 - Dietlen, Siegmund A1 - Schröder, Volkmar T1 - Explosionsgrenzen von Brenngas/Inertgas/Luft-Gemischen unter Druck T2 - GVC Fachausschußsitzung "Reaktionstechnik CY - Aachen, Deutschland DA - 1998-03-02 PY - 1998 CY - Aachen AN - OPUS4-1682 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kley, Gerd A1 - Köcher, Peter A1 - Brenneis, Rudolf A1 - Grothe, G. T1 - Enzymatische Alkoholyse unterschiedlicher Fette und Altfette zur Gewinnung von Kühlschmierstoffen und oleochemischen Sonderprodukten T2 - DBU-TU Hamburg-Harburg Kick-off Meeting im InnovationsCentrum Biokatalyse (ICBio) CY - Hamburg-Harburg, Deutschland DA - 2002-10-21 PY - 2002 SP - 1 EP - 11 AN - OPUS4-1663 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Brenneis, Rudolf A1 - Köcher, Peter A1 - Kley, Gerd T1 - Enzymatische Altfettalkoholyse zur Herstellung von Wertstoffen PY - 2002 UR - http://www.icbio.de/353.html SP - 1 EP - 2 PB - Deutsche Bundesstiftung Umwelt (DBU) CY - Osnabrück AN - OPUS4-1664 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Volkmar T1 - Oxidizing ability of gases and gas mixtures - Final report T2 - Report for ISO/TC58/SC2 meeting CY - Paris, France DA - 1999-08-30 PY - 1999 IS - ISO-TC58-SC2 SP - 1(?) EP - 12(?) AN - OPUS4-1669 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Schröder, Volkmar T1 - Explosionsgrenzen von Wasserstoff/Sauerstoff-Gemischen (Abschlussbericht zum Vorhaben VH2226) PY - 2002 SP - 1 EP - 23 AN - OPUS4-1670 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hieronymus, Hartmut A1 - Plewinsky, Bodo A1 - Schröder, Volkmar A1 - Dietlen, Siegmund T1 - Explosions- und Detonationsphänomene bei Mischungen aus 1,1,1,2-Tetrafluorethan und Luft T2 - 39. Sitzung des DECHEMA - AA "Gas- und Flammennreaktionen" CY - Frankfurt am Main DA - 1995-01-20 PY - 1995 AN - OPUS4-1672 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Volkmar T1 - Erfahrungen mit dem 80-mm-Rohr bei Bestimmung von Explosionsgrenzen nach der neuen europäischen Norm (prEN 1839) T2 - DIN-FAM-Meeting CY - Braunschweig, Deutschland DA - 2001-04-02 PY - 2001 AN - OPUS4-1693 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lohse, Volkmar A1 - Negendank, Detlef A1 - Buschbeck, Gerd T1 - Explosionsschutz mit Gaswarngeräten T2 - Internationale Fachmesse für Explosionsschutz und Anlagensicherheit CY - Nürnberg, Deutschland DA - 2001-03-27 PY - 2001 AN - OPUS4-1695 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lohse, Volkmar A1 - Negendank, Detlef A1 - Buschbeck, Gerd T1 - Explosionsschutz - Gaswarngeräte im Geltungsbereich der Richtlinie 94/9/EG T2 - Internationale Fachmesse für Explosionsschutz und Anlagensicherheit CY - Nürnberg, Deutschland DA - 2001-03-27 PY - 2001 AN - OPUS4-1696 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lohse, Volkmar T1 - Konformitäts-Bewertungsverfahren nach Richtlinie 94/9/EG für Gaswarngeräte zum Einsatz in explosionsgefährdeten Bereichen T2 - Behörden-Erfahrungsaustausch Gefahrgutsicherheit, Störfall-Verordnung und Explosionsschutz CY - Berlin, Deutschland DA - 2002-09-10 PY - 2002 AN - OPUS4-1697 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lohse, Volkmar T1 - Anforderungen an Gaswarngeräte für den Einsatz in abwassertechnischen Anlagen T2 - Fachtagung "Abwassertechnische Anlagen" CY - Waßmannsdorf, Deutschland DA - 2002-09-19 PY - 2002 AN - OPUS4-1698 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lohse, Volkmar A1 - Negendank, Detlef T1 - Explosionsschutz mit Gaswarngeräten - Die BAM als notifizierte Stelle für Richtlinie 94/9/EG T2 - ExploRisk 2002 CY - Nürnberg, Deutschland DA - 2002-10-08 PY - 2002 AN - OPUS4-1699 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lohse, Volkmar A1 - Negendank, Detlef T1 - Gemeinsame BAM- und PTB-Dienstleistung - Konformitäts-Bewertungsverfahren für Gaswarngeräte T2 - ExploRisk 2002 CY - Nürnberg, Deutschland DA - 2002-10-08 PY - 2002 AN - OPUS4-1700 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Dirk T1 - Zuverlässigkeitsspezifische Gestaltung und Betriebsführung Trocknungstechnischer Anlagen am Beispiel der Kautschuktrocknung Überblick zum gegenwärtigen Stand der Untersuchungen T2 - 35. Sitzung des DECHEMA/GVC-Arbeitsausschusses CY - Frankfurt am Main, Deutschland DA - 1993-02-18 PY - 1993 AN - OPUS4-1701 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Dirk T1 - Sicherheitsbezogene Untersuchungen des Kautschuks zur Ableitung thermischer und /oder konzentrationsabhängiger Prozess- und Zustandsgrößen zur Indikation ablaufender sicherheitsrelevanter Phänomene PY - 1994 AN - OPUS4-1702 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Dirk A1 - Schuster, H. A1 - Krause, Ulrich A1 - Winskowski, Jürgen T1 - Sicherheitstechnische Untersuchungen zur Gefährdungsbildung bei der Kautschuktrocknung T2 - 2. Fachtagung, Arbeits-, Anlagen- und Umweltsicherheit CY - Köthen DA - 1994-11-03 PY - 1994 AN - OPUS4-1703 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Dirk T1 - Numerische Simulation von Wasserstoffgas-Freisetzungen T2 - BAM-Kolloquium 1998 CY - Berlin, Deutschland DA - 1998-01-28 PY - 1998 AN - OPUS4-1704 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Dirk T1 - Numerische Simulation von Wasserstoffgasfreisetzungen T2 - Arbeitskreis Anlagensicherheit Berlin-Brandenburg CY - Berlin, Deutschland DA - 1998-09-25 PY - 1998 CY - Berlin AN - OPUS4-1705 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Dirk A1 - Schalau, V. T1 - TRGS 300- Sicherheitstechnik, die kleine Sicherheitsanalyse T2 - Fortbildung gemäß § 9 der 5. BimSchV CY - --- DA - 2001-01-01 PY - 2001 AN - OPUS4-1706 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Schuster, H. A1 - Schmidt, Dirk T1 - Zuverlässigkeitsspezifische Gestaltung und Betriebsführung eines Sicherheitssystems für trocknungstechnische Anlagen am Beispiel der Kautschukproduktion (Abschlussbericht, BMFT-FKZ 13RG9111) PY - 1995 AN - OPUS4-1707 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schuster, H. A1 - Schmidt, Dirk T1 - Sicherheitsforschung und Sicherheitstechnik - Jahresberichte 1993 und 1994 PY - 1995 VL - 1994 IS - 13RG9111 CY - Düsseldorf AN - OPUS4-1709 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Schmidt, Dirk T1 - Ein Beitrag zur Gestaltung eines Sicherheitssystems auf der Grundlage des Gefährdungsbildungsprozesses für verfahrenstechnische Anlagen, bezogen auf die Trocknung von Synthesekautschuk KW - chemische Verfahrenstechnik KW - Sicherheitstechnik KW - Synthesekautschuk KW - Trocknung PY - 1996 SP - 1 EP - 150 CY - Halle AN - OPUS4-1710 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Isecke, Bernd A1 - Mietz, Jürgen T1 - Einsatz nichtrostender Stähle in Schwimmbädern T2 - Fachtagung des Nederlands Corrosie Centrum CY - Breda, Niederlande DA - 2002-11-14 PY - 2002 AN - OPUS4-1845 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Isecke, Bernd T1 - Korrosionsschutz und Normung an sicherheitsrelevanten Bauteilen T2 - 60 Jahre - Normenausschuss Materialprüfung CY - Berlin, Deutschland DA - 2007-08-30 PY - 2007 SP - 31 EP - 40 CY - Berlin AN - OPUS4-1846 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Isecke, Bernd T1 - Einsatzmöglichkeiten des kathodischen Korrosionsschutzes im Brückenbau T2 - Fachtagung des BAST CY - Wiesbaden, Deutschland DA - 2002-11-19 PY - 2002 AN - OPUS4-1847 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Isecke, Bernd T1 - Spannungsrißkorrosion an hochfesten Rohrleitungsstählen T2 - Fachseminar WINGAS CY - Kassel, Deutschland DA - 2002-11-29 PY - 2002 AN - OPUS4-1848 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Steinborn, Gabriele A1 - Wäsche, Rolf A1 - Reichel, U. T1 - Fabrication of porous ceramics made from nano sized alumina powder by gelcasting N2 - The gelcasting process was used for manufacturing porous ceramic bodies from nano sized powders. 3 different powders with specific surface areas between 12 and 30 m²/g were used. Solid content of the corresponding slurries was dependent on the milling procedure and the use of a suitable dispersant. For bimodal GradeA powder solid content was as high as 58 vol%. For sintering temperatures between 1250 and 1600°C the porosity varied between 45 and 20%, whereas the pore radii varied between 50 and 91nm. The grain size of crystallites in the sintered microstructures was about 1um. The reflection ratio for visible light increased in comparison to a reference sample made from conventional powder from 0.8 to 0.95 in the wavelenght range around 400nm. T2 - 2nd International Conference on Shaping of Advanced Ceramics CY - Gent, Belgium DA - 2002-10-24 PY - 2002 SP - 103 EP - 108 AN - OPUS4-1813 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Razus, D. A1 - Molnarne, Maria T1 - Limiting Oxygen Concentration Evaluation in Flammable Gaseous Mixtures by means of Calculated Adiabatic Flame Temperatures T2 - 3rd International Conference of the Chemical Societies of the South-Eastern European Countries ; International Conference of the Chemical Societies of the South-Eastern European Countries on Chemistry in the New Millennium - an Endless Frontier CY - Bucharest, Romania DA - 2002-09-22 PY - 2002 IS - PO 253 SP - 30 PB - Nemira CY - [S.l.] AN - OPUS4-1815 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fuß, Oliver A1 - Molnarne, Maria A1 - Schröder, Volkmar A1 - Schönbucher, A. T1 - Bestimmung der Sauerstoffgrenzkonzentration von Gasen und Dämpfen - Normungsvorhaben bei CEN/TC 305 T2 - DECHEMA/GVC-Arbeitsausschuss "Sicherheitstechnische Kenngrößen" CY - Frankfurt am Main, Deutschland DA - 2002-02-28 PY - 2002 AN - OPUS4-1816 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Balke, Christian T1 - Fire Tests with LPG Vessels T2 - International Symposium on Protection of Dangerous Goods Tanks and Cylinders in Fire CY - Ottawa, Canada DA - 2002-10-22 PY - 2002 AN - OPUS4-1817 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Balke, Christian T1 - Verification of Fire Protection Systems for LPG Tanks N2 - The results and execution of many full scale fire engulfment tests on 3.6 and 4.85 m³ LPG tanks, protected with thin sublimation and intumescent coatings, mineral wool with steel jackets, vermiculite coatings and water spray systems, are presented. Additional furnace tests with coated steel plates have been carried out to optimize the necessary coating thickness. Similarly, an overview of the test conditions for the recognition based on technical rules and BAM requirements for fire protection systems of LPG tanks will be shown and explained. When the internal pressure reaches the vessel bursting pressure a violent tank rupture, fragmenting of the shell and spontaneous release of the content are the consequences. In case of LPG this event is called "boiling liquid expanding vapour explosion (BLEVE)" with expanding fireball as an additional severe consequence. For this reason the sufficient fire protection of LPG vessels is an important item. The tests demonstrated sufficient vessel safety during 90 minutes of a full fire engulfment. It will also be shown that the examinations and results are transferable to bigger tanks. The transferability of the test results is illustrated by diagrams which show the dependence of the coating thickness against the shell thickness of the tank. All tested tanks were equipped with pressure relief valves (PRVs) and partially filled with propane. T2 - International Symposium on Protection of Dangerous Goods Tanks and Cylinders in Fire CY - Ottawa, Canada DA - 2002-10-22 PY - 2002 UR - http://www.tc.gc.ca/tdg/consult/symposium/abstracts.htm AN - OPUS4-1818 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Trubiroha, Peter T1 - Interpretation of the spectral sensitivity and of the action spectrum of polymers T2 - 22. Donauländergespräche CY - Berlin, BAM, Germany DA - 2001-09-16 PY - 2002 SP - 4-1-4-10 CY - Wien AN - OPUS4-1820 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pötzsch, Klaus-Michael T1 - Einfluß der Ausrüstung von Transporttanks und Tankschiffen auf die Transportsicherheit T2 - Gefahrgut-Technik-Tage Berlin 2002 "Innovative Tanktechnik" CY - Berlin, Deutschland DA - 2002-11-14 PY - 2002 PB - Storck-Akademie CY - Hamburg AN - OPUS4-1784 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ludwig, Jörg A1 - Pötzsch, Klaus-Michael A1 - Schulz-Forberg, Bernd A1 - Ulrich, Armin T1 - The effectiveness of pressure relief devices on cylinders and tanks from a German point of view N2 - Fire accidents during road and rail transport are not occurring very often. In particular fire accidents with total fire engulfment of tanks seem to be rather rare. Up to now authorities in Europe officially are of the opinion that in densely populated regions like Europe in the space of time between the beginning of a fire and the rupture of a tank measures could be taken like cooling of the heated tank surface and evacuation of the area probably affected by an explosion. Therefore, no requirements with regard to fire protection measures concerning transport tanks for land mode like the application of safety relief devices have to be met. Due to some catastrophic accidents being discussed in public even European authorities are considering the pros and cons of fire protection measures. Nevertheless in sparsely populated regions and during transport at sea fire accidents have been looked at since ever as seriously dangerous events. Therefore, multi modal tanks for the transport of dangerous goods have to be fitted with safety relief devices. The delivery capacity of these devices has to be such that, in the event of total fire engulfment, the pressure inside the tank does not exceed certain limits. With regard to accident records and results of fire tests it has to be stated that portable tanks may rupture violently, even if the tanks are fitted with pressure-relief devices adequately designed for the heat flux of full fire engulfment. Therefore, the lecture will be dealing with the results of fire testing of tanks and conclusions to be drawn and considerations on: the advantages of different fire protection measures for transport tanks, the pros and cons of safety relief devices for cylinders and transport tanks, improvement of regulations and recommendations. T2 - International Symposium on Protection of Dangerous Goods Tanks and Cylinders in Fire CY - Ottawa, Canada DA - 2002-10-22 PY - 2002 UR - http://www.tc.gc.ca/tdg/consult/symposium/abstracts.htm AN - OPUS4-1785 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pötzsch, Klaus-Michael A1 - Schalau, Bernd A1 - Ludwig, Jörg T1 - Thermal protection of rail tank wagons for UN 1051 Hydrogen cyanide, stabilized T2 - International Symposium on Protection of Dangerous Goods Tanks and Cylinders in Fire CY - Ottawa, Canada DA - 2002-10-22 PY - 2002 SP - 1 EP - 10 AN - OPUS4-1786 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit T1 - Einsatz von höherlegierten Sonderedelstählen und Nickelbasislegierungen im Tankbau T2 - Gefahrgut-Technik-Tage Berlin 2002 "Innovative Tanktechnik" CY - Berlin, Deutschland DA - 2002-11-14 PY - 2002 PB - Storck-Akademie CY - Hamburg AN - OPUS4-1787 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Brunner, A. J. A1 - Bohse, Jürgen T1 - Acoustic emission standards and guidelines 2002 - a comparative assessment and perspectives N2 - A comparative analysis of selected standards and guidelines on Acoustic Emission testing published by international and national organisations yields an assessment of the current status of standardisation. Areas where existing documents do not yet exist or appear unsatifactory for some reason are identified and formulated as perspectives for further work. In the future, structural integrity assessment with Acoustic Emission methods is expected to gain in importance. PY - 2002 UR - http://www.ndt.net/article/v07n09/21/21.htm SN - 1435-4934 VL - 7 IS - 9 SP - 1 EP - 10 PB - NDT.net CY - Kirchwald AN - OPUS4-1792 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maierhofer, Christiane A1 - Wendrich, Astrid A1 - Köpp, Christian T1 - On-site investigation techniques for the structural evaluation of historic masonry buildings (EC-Project in the Environment and Sustainable Development Programme (EESD) T2 - 6th International Masonry Conference CY - London, England, UK DA - 2002-11-04 PY - 2002 N1 - Geburtsname von Wendrich, Astrid: Ziebolz, A. - Birth name of Wendrich, Astrid: Ziebolz, A. VL - 6 SP - 1(?) EP - 4(?) AN - OPUS4-1823 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kind, Thomas A1 - Krause, Ingo A1 - Maierhofer, Christiane T1 - Development of an Utility Finding Impulse Radar T2 - German Radar Symposium (GRS 2002) CY - Bonn, Germany DA - 2002-09-03 KW - Ground penetration radar KW - Utility finding KW - Antenna KW - Impulse radar PY - 2002 SP - 341 EP - 344 AN - OPUS4-1826 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maierhofer, Christiane A1 - Brink, Arne A1 - Röllig, Mathias A1 - Wiggenhauser, Herbert A1 - Hillemeier, B. A1 - Rieck, C. ED - Kupfer, K. ED - Trinks, E. T1 - Untersuchung des Einflusses von Feuchtigkeit auf die Ortung von Hohlstellen in Betonstrukturen mit der Impuls-Thermografie T2 - 11. Feuchtetag CY - Weimar, Deutschland DA - 2002-09-18 KW - Impuls-Thermografie KW - Thermografie KW - Zerstörungsfreie Prüfung im Bauwesen KW - Simulation KW - Hohlstellen KW - Kiesnester KW - Feuchtigkeit KW - Beton PY - 2002 SP - 47 EP - 58 PB - MFPA an der Bauhaus-Univ. CY - Weimar AN - OPUS4-1827 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maierhofer, Christiane A1 - Brink, Arne A1 - Röllig, Mathias A1 - Wiggenhauser, Herbert T1 - Impulse Thermography for locating voids and honeycombing in concrete structures supported by numerical simulations T2 - 11. Bauklimatisches Symposium ; 11th Symposium of Building Physics CY - Dresden, Germany DA - 2002-09-26 PY - 2002 SP - 242 EP - 252 PB - TU CY - Dresden AN - OPUS4-1828 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rudolph, Hans-Volker A1 - Hentschel, Manfred P. A1 - Ivers, Heinz T1 - Damage accumulation in short fiber reinforced thermoplast by X-Ray refraction N2 - Micro damage structures of fiber reinforced polymers (FRP) can be characterized nondestructively by X-ray refraction topography, which images inner surfaces. The damage accumulation after fatigue treatment of short glass fiber reinforced polybutylene terephthalate (PBT-GF) is correlated to the applied load and the number of cycles. Micro cracks and fiber/matrix debonding during fatigue can be detected separately due to their different direction of X-ray small angle scattering. The residual strength over the crack surface decreases by a linear decay as 30 %, 60 % and 90 % of the materials lifetime is passed. T2 - 8th ECNDT CY - Barcelona, Spain DA - 2002-06-17 PY - 2002 UR - http://www.ndt.net/article/ecndt02/193/193.htm VL - 8 SP - 1 EP - 5 PB - European Federation for Non-Destructive Testing CY - Barcelona AN - OPUS4-1840 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eltanany, G. A1 - Munz, Martin T1 - Investigation of interphases between thermoplastic and thermosetting polymers - an AFM approach T2 - Polydays 2002 CY - Berlin, Germany DA - 2002-09-30 PY - 2002 SP - P 6.9 AN - OPUS4-1842 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Ralph-Peter A1 - Schöch, M. A1 - Müller, G. A1 - Hahne, D.-B. T1 - Strukturuntersuchungen an Makromonomeren für partiell kristalline polymere Netzwerke T2 - Vortragstagung "Funktionspolymere für Systemlösungen" CY - Darmstadt, Germany DA - 2002-03-18 PY - 2002 AN - OPUS4-1806 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pötzsch, Klaus-Michael T1 - Einfluss der Ausrüstung von Transporttanks und Transportschiffen auf die Transportsicherheit T2 - Gefahrgut-Technik-Tage Berlin 2002 "Innovative Tanktechnik" CY - Berlin, Deutschland DA - 2002-11-14 PY - 2002 PB - Storck-Akademie CY - Hamburg AN - OPUS4-1808 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Altkrüger, Sabine A1 - Vater, Ernst-Joachim A1 - Müller, Renate A1 - Mews, Oliver A1 - Robeck, Peter T1 - Vergleich des auf europäischer Ebene festgelegten Prüfverfahrens für die Bestimmung der Abreißfestigkeit der einzelnen Schichten für die Abdichtung von Betonfahrbahntafeln mit nationalen Regelungen und Schaffung eines Bewertungshintergrundes (Abschlußbericht ; Forschungsbericht FE 15.325/2000/ARB) PY - 2003 SP - 1 EP - 102 CY - Berlin AN - OPUS4-1809 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Goedecke, Thomas T1 - Lebensdaueruntersuchungen an vergütetem 34 CrMo 4 und an CuZn37 bei spannungs- und gesamtdehnungsgesteuerter Zug-Druck-Beanspruchung PY - 1991 SP - 1 EP - 165 CY - Berlin AN - OPUS4-1773 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Goedecke, Thomas T1 - Umweltsimulation von Verpackungen in der BAM T2 - Symposium "Gefahrgutverpackungen aus Wellpappe" CY - Berlin, Deutschland DA - 2002-10-25 PY - 2002 AN - OPUS4-1775 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Goedecke, Thomas T1 - Stand der Normung T2 - AK-Prüfstellen der BAM CY - Unterlüß, Deutschland DA - 2002-10-08 PY - 2002 AN - OPUS4-1776 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Goedecke, Thomas T1 - Testing of packagings for dangerous chemicals T2 - Conference on Chemical Safety CY - Portoroz, Slovenia DA - 2002-09-03 PY - 2002 AN - OPUS4-1777 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Goedecke, Thomas T1 - Determination of Transportation Loads during a Container Transport to New York and back T2 - CEEES Workshop "Distribution Environment and Transportation Loads - a Key Factor for Safe Cargo Handling" CY - Brussels, Belgium DA - 2002-02-22 PY - 2002 AN - OPUS4-1778 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Blümel, Peter T1 - Zulassung und Verwendung von Verpackungen für gefährliche Güter T2 - 12. Münchner Gefahrgut-Tage CY - München, Deutschland DA - 2002-05-06 PY - 2002 SP - 1(?) EP - 9(?) PB - Verl. Moderne Industrie CY - Landsberg AN - OPUS4-1782 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Goedecke, Thomas T1 - Lebensdaueruntersuchungen an vergütetem 34 CrMo 4 bei spannungs- und gesamtdehnungsgesteuerter Versuchsführung T2 - Tagung Werkstoffprüfung 1988 CY - Bad Nauheim, Deutschland DA - 1988-12-01 PY - 1988 CY - Berlin AN - OPUS4-1763 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Goedecke, Thomas T1 - Einsatz der Radionuklidtechnik zur Untersuchung des Verschleißverhaltens randschichtbehandelter und beschichteter Bauteile T2 - Tagung Werkstoffprüfung 1990 CY - Bad Nauheim, Deutschland DA - 1990-12-06 PY - 1988 CY - Berlin AN - OPUS4-1764 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Goedecke, Thomas T1 - Verpackungsprüfung bei der BAM T2 - 3. Berlin-Brandenburger Gefahrguttage CY - Berlin DA - 1994-11-21 PY - 1994 CY - Berlin AN - OPUS4-1766 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Goedecke, Thomas T1 - Was ist wie und wo geregelt? T2 - DVZ/CUB-Tagung "Wie sicher ist die Ladungssicherung?" CY - Bonn, Deutschland DA - 1995-04-23 PY - 1995 CY - Bonn AN - OPUS4-1767 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Goedecke, Thomas T1 - Rechtliche Rahmenbedingungen T2 - DVZ/CUB-Tagung "Wie sicher ist die Ladungssicherung?" CY - Bonn, Deutschland DA - 1996-04-23 PY - 1996 CY - Bonn AN - OPUS4-1768 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Goedecke, Thomas T1 - Verpackung und Ladungssicherung T2 - ecomed Spezialseminare für Gefahrgutexperten CY - Bad Honnef, Deutschland DA - 1995-10-05 PY - 1995 PB - ecomed-Verlagsges. CY - Bad Honnef AN - OPUS4-1769 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Goedecke, Thomas T1 - Einsatz der Radionuklidtechnik zur Untersuchung des Verschleißverhaltens randschichtbehandelter und beschichteter Bauteile (Abschlußbericht des EHD-Verbundvorhabens) PY - 1991 AN - OPUS4-1772 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meinhold, Uwe A1 - Mellmann, Günter A1 - Maultzsch, Matthias ED - Malhotra, V. M. T1 - Performance of high-grade concrete with full substitution of aggregates by recycled concrete N2 - On the background of the need for reuse of building rubble and the saving of natural resources, a European Union research project was performed covering concrete technology and durability aspects. A very special precondition was the use of large-scale processed building rubble with unknown origin and the total replacement of aggregates above 2 mm. Comprehensive tests were carried out on the properties of the starting material from different processing plants and fresh concrete, particularly the interdependence of water addition and wor ability. Investigations on hardened concrete properties included strength devel-opment, creep and shrinkage, modulus of elasticity, capillary absorption, freezing and thawing resistance, and carbonation behavior over a long period. The results demonstrate that the industrial production of a high-grade, durable concrete is possible. The project is a promising contribution for sustainable development. T2 - Third CANMET/ACI International Symposium on Sustainable Development of Cement and Concrete CY - San Francisco, CA, USA DA - 16.09.2001 KW - Aggregates KW - Compressive strength KW - Concrete KW - Creep KW - Modulus of elasticity KW - Recycled concrete KW - Shrinkage PY - 2001 SN - 0-87031-041-0 N1 - Serientitel: ACI SP – Series title: ACI SP IS - SP 202 SP - 85 EP - 96 PB - American Concrete Institute (ACI) CY - Farmington Hills, Mich. AN - OPUS4-1933 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thomsen-Schmidt, P. A1 - Hasche, K. A1 - Ulm, G. A1 - Herrmann, K. A1 - Krumrey, M. A1 - Ade, G. A1 - Stümpel, J. A1 - Procop, Mathias A1 - Beck, Uwe T1 - Realisation and metrological characterisation of thickness standards below 100 nm T2 - DVG Jahrestagung 2002 CY - Magdeburg, Germany DA - 2002-06-17 PY - 2002 SP - 1 EP - 9 PB - Deutsche Vakuum-Gesellschaft CY - Kaiserslautern AN - OPUS4-1936 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jahreiß, W. A1 - Bergmann, W. A1 - Brzoska, B. A1 - Gogolin, Bernd T1 - ANF-18/MOX - A modular transport system for fresh PWR MOX fuel assemblies T2 - PATRAM 2001 ; Annual International Symposium on Packaging and Transportation of Radioactive Materials CY - Chicago, IL, USA DA - 2001-09-03 PY - 2001 IS - CD-ROM PB - PATRAM CY - Chicago, Ill. AN - OPUS4-1941 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rödel, Roland A1 - Krietsch, Torsten A1 - Zeisler, Peter T1 - Current type B package approval procedures in Germany - selected topics from safety assessment T2 - PATRAM 2001 ; Annual International Symposium on Packaging and Transportation of Radioactive Materials CY - Chicago, IL, USA DA - 2001-09-03 PY - 2001 IS - CD-ROM PB - PATRAM CY - Chicago, Ill. AN - OPUS4-1942 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Döring, Joachim A1 - Mc Hugh, Jarlath A1 - Schmachtenberg, E. A1 - Töpker, J. T1 - RTM Process optimization using incorporated ultrasonic sensors T2 - 5. Internationale AVK-TV Tagung für Verstärkte Kunststoffe und Duroplastische Formmassen ; 5th International AVK-TV Conference on Reinforced Plastics and Thermoset Moulding Compounds CY - Baden-Baden, Germany DA - 2002-09-17 PY - 2002 SP - B10-1-B10-10 CY - Frankfurt am Main AN - OPUS4-1853 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Harbich, Karl-Wolfram A1 - Hentschel, Manfred P. T1 - Charakterisierung von porösen Materialien und Pulvern mittels Röntgen-Refraktion T2 - Jahrestagung Zerstörungsfreie Materialprüfung 2001 CY - Berlin, Deutschland DA - 2001-05-21 PY - 2001 UR - http://www.ndt.net/article/dgzfp01/papers/p48/p48.htm N1 - Serientitel: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. – Series title: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. IS - 75-CD PB - DGZfP CY - Berlin AN - OPUS4-1862 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmitz, V. A1 - Müller, W. A1 - Krause, Martin A1 - Wiggenhauser, Herbert T1 - Improved Detection of Tendon Ducts and Defects in Concrete Structures Using Ultrasonic Imaging N2 - At the beginning of the 90s the general opinion was, that ultrasonic inspection methods using pulse-echo technique were not suitable for the inspection of concrete because of the inhomogeneity and the strong scattering behavior of the embedded aggregates. In the meantime the progress in the development of new equipment and inspection strategies in connection with ultrasonic imaging techniques turns the pulse-echo technique into a powerful tool to solve problems related to concrete materials. These imaging techniques - developed for the inspection of homogenous materials like steel of aluminum - could be adopted to the very low frequencies needed for concrete inspections. T2 - Workshop on the Evaluation of Defects, Repair Criteria & Methods of Repair for Concrete Structures on Nuclear Power Plants CY - Berlin, Germany DA - 2002-04-10 PY - 2002 UR - http://publica.fraunhofer.de/documents/N-15451.html VL - 2 SP - 125 EP - 132 PB - NEA CY - Issy-les-Moulineaux AN - OPUS4-1921 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Redmer, Bernhard A1 - Ewert, Uwe A1 - Hofmann, E. A1 - Neundorf, B. T1 - New System for Mechanised X-Ray Inspection of Welded Austenic Pipes N2 - One of the most important tasks for in-service weld inspection of Circumferential welds is the detection of planar defects and its sizing. The information about the shape, length and depth of defects like cracks and lack of fusion can be measured quantitatively with a mechanised system for manipulation of X-ray source and line camera. The well adjusted manipulation system allows the testing of pipes with a diameter between 176 mm and 500 mm. The system is based on several modules, which can be adjusted to the testing problem. The energy of the X-ray tube amounts 225 keV. The pixel resolution of the line camera is 50µm for 2048 pixels per line. The camera and the X-ray tube are separated on the pipe by an angle of 180°. They are moved line by line around the circumference to acquire the radiometric image. The basic problem of radiography as well as of the radiometric scan technique is the dependence of the measured crack contrast on the radiation direction in relation to the crack location. Only parallel transmission to the crack plane provides sufficient contrast. This requires application of the multi-angle technique. The developed scanner enables modification of the radiation direction. It is possible to set up the system for a special inspection of side wall flaws. Scanning the weld under different angles provides multi -angle projections which improve the probability of detection for planar inhomogeneities in the material like cracks and lack of fusion. Furthermore, the multi-angle technique provides enough information for a 3D-reconstruction of the weld structure. New methods of digital laminography and tomosynthesis permit the measurement of the shape and depth of the indications. The developed system, which is applicable for mobile in service inspection, is presented together with the results of the measurement techniques like planar scan, coplanar laminography, tomosynthesis and cross-sectional planar tomography. T2 - 3rd International Conference on NDE in Relation to Structural Integrity for Nuclear and Pressurized Components CY - Seville, Spain DA - 2001-11-14 PY - 2001 UR - http://www.ndt.net/abstract/ndesi01/data/51.htm SP - 52 EP - 60 CY - Seville AN - OPUS4-1903 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Redmer, Bernhard A1 - Robbel, Joachim A1 - Ewert, Uwe A1 - Vengrinovich, Valery T1 - Mechanised weld inspection by tomographic computer aided radiometry (TomoCAR) T2 - 8th European Conference on NDT CY - Barcelona, Spain DA - 2002-06-17 PY - 2002 UR - http://www.ndt.net/article/ecndt02/308/308.htm SN - 1435-4934 VL - 44 IS - 9 SP - 564 EP - 567 PB - NDT.net CY - Kirchwald AN - OPUS4-1904 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bomas, H. A1 - Hünecke, Joachim A1 - Laue, S. A1 - Schöne, Dieter T1 - Anrisslebensdauervorhersage am Beispiel glatter und gekerbter Proben des Werkstoffes Cm15 T2 - 2. Kolloquium "Mechanismenorientierte Lebensdauervorhersage für zyklisch beanspruchte metallische Werkstoffe" CY - Berlin, Deutschland DA - 2002-02-13 KW - Kurze Risse KW - Simulation KW - Kerben KW - Korngröße KW - Ermüdung PY - 2002 N1 - Serientitel: DVM-Bericht – Series title: DVM-Bericht IS - 684 SP - 81 EP - 96 PB - Deutscher Verband für Materialforschung und -prüfung CY - Berlin AN - OPUS4-1906 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübert, Thomas T1 - Qualitätsmanagement in der Feuchtemesstechnik T2 - VDI Wissensforum "Qualitätssicherung und Prozeßoptimierung durch Feuchtebestimmung bei Trocknungsprozessen" CY - Stuttgart, Deutschland DA - 2002-11-07 PY - 2002 IS - 91 PB - VDI-Verl. CY - Düsseldorf AN - OPUS4-1909 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Almagro, J.-F. A1 - Busch, P. A1 - Gohil, D. D. A1 - Heikinheimo, E. A1 - Karduck, P. A1 - Richter, S. A1 - Sloof, W. G. A1 - Thiot, J.-F. A1 - Wirth, Thomas T1 - Electron-Probe MICROanalysis of LighT Elements - Measurement Methods and Certified Reference Materials (MICROLITE) PY - 2002 IS - 65 SP - 1 EP - 156 PB - National Physical Laboratory CY - Teddington, Middlesex AN - OPUS4-1911 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz-Forberg, Bernd T1 - Sicherheitstechnik und Informationsmanagement T2 - 5. Gefahrgut-Technik-Tage "Innovative Tanktechnik" CY - Berlin, Deutschland DA - 2002-11-14 PY - 2002 VL - 5 SP - 1(?) EP - 13(?) PB - Storck-Akademie CY - Hamburg AN - OPUS4-1912 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klinger, Christian A1 - Klingbeil, Dietmar A1 - Kinder, Joachim A1 - Österle, Werner T1 - ESTONIA - Katastrophe - Werkstoffuntersuchungen der BAM an Prüfstücken des Frontschotts T2 - Landesfachtagung 2002 "Schweißtechnik" CY - --- DA - 2002-11-15 PY - 2002 SP - 1(?) EP - 6(?) AN - OPUS4-1925 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klingbeil, Dietmar T1 - Schwerpunkte der BAM aus Forschungsvorhaben zur Komponentensicherheit sowie zukünftige Entwicklungen T2 - 2. Workshop Kompetenzverbund Kerntechnik "Komponentensicherheit und Integritätsbewertung" CY - Köln, Deutschland DA - 2002-09-18 PY - 2002 AN - OPUS4-1927 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zeisler, Peter A1 - Gogolin, Bernd A1 - Ballheimer, Viktor A1 - Pöppinghaus, J. T1 - Strain of Lid Bolts of Type B Packages During 9 m Drop Tests - Results of Real Tests and Problems of Analytical Predition T2 - PATRAM 2001 ; Annual International Symposium on Packaging and Transportation of Radioactive Materials CY - Chicago, IL, USA DA - 2001-09-03 PY - 2001 IS - CD-ROM PB - PATRAM CY - Chicago, Ill. AN - OPUS4-1883 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Millan, P. A1 - Vaughan, C. A1 - Gogolin, Bernd A1 - Droste, Bernhard T1 - Drop Test for the Licensing of the "RA-3D" Package in the Transport of BWR Fresh Fuel Assembllies T2 - PATRAM 2001 ; Annual International Symposium on Packaging and Transportation of Radioactive Materials CY - Chicago, IL, USA DA - 2001-09-03 PY - 2001 IS - CD-ROM PB - PATRAM CY - Chicago, Ill. AN - OPUS4-1884 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bergmann, W. A1 - Brozoska, B. A1 - Jahreiß, W. A1 - Gogolin, Bernd T1 - ANF 18 MOX - A modular transport system for fresh PWR MOX fuel assemblies T2 - PATRAM 2001 ; Annual International Symposium on Packaging and Transportation of Radioactive Materials CY - Chicago, IL, USA DA - 2001-09-03 PY - 2001 IS - CD-ROM PB - PATRAM CY - Chicago, Ill. AN - OPUS4-1885 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jahreiß, W. A1 - Phillippczyk, U. A1 - Paulinyi, W. A1 - Quercetti, Thomas T1 - ANF-18 - A new transport container for fresh PWR fuel assemblies according to IAEA requirements T2 - PATRAM 2001 ; Annual International Symposium on Packaging and Transportation of Radioactive Materials CY - Chicago, IL, USA DA - 2001-09-03 PY - 2001 IS - CD-ROM PB - PATRAM CY - Chicago, Ill. AN - OPUS4-1887 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Droste, Bernhard A1 - Schulz-Forberg, Bernd A1 - Probst, Ulrich T1 - Investigation of a Spent Fuel Cask Beside an Exploding Propane Tank T2 - PATRAM 2001 ; Annual International Symposium on Packaging and Transportation of Radioactive Materials CY - Chicago, IL, USA DA - 2001-09-03 PY - 2001 IS - CD-ROM PB - PATRAM CY - Chicago, Ill. AN - OPUS4-1888 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Qiao, Linan A1 - Droste, Bernhard T1 - Assessment of dynamically loaded surface cracks in cubic containers T2 - 13th International Conference on Packaging and Transportation of Radioactive Materials ; PATRAM 2001 CY - Chicago, IL, USA DA - 2001-09-03 PY - 2001 IS - CD-ROM PB - PATRAM CY - Chicago, Ill. AN - OPUS4-1889 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jahreiß, W. A1 - Phillippczyk, U. A1 - Paulinyi, W. A1 - Masslowski, Jörg-Peter T1 - ANF-10 - A new transport container for fresh BWR fuel assemblies according to IAEA requirements T2 - PATRAM 2001 ; Annual International Symposium on Packaging and Transportation of Radioactive Materials CY - Chicago, IL, USA DA - 2001-09-03 PY - 2001 IS - CD-ROM PB - PATRAM CY - Chicago, Ill. AN - OPUS4-1890 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Knabe, C. A1 - Howlett, C. A1 - Markovic, B. A1 - Gildenhaar, Renate A1 - Berger, Georg A1 - Reif, D. A1 - Zreiqat, H. T1 - The functional expression of human bone derived cells grown on resorbable bioactive glass ceramics T2 - 28th Annual Meeting & Exposition of the Society for Biomaterials CY - Tampa, FL, USA DA - 2002-04-23 PY - 2002 SP - 706 PB - Society for Biomaterials AN - OPUS4-1892 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gross, U. A1 - Müller-Mai, C. A1 - Knabe, C. A1 - Berger, Georg A1 - Ploska, Ute A1 - Gildenhaar, Renate ED - Vincenzini, P. T1 - Animal experiments with biomaterials for direct bone contact which possess in comparison to TCP and HA products higher or lower solubility T2 - 10th International Ceramics Congress ; 3rd Forum on New Materials ; 10th CIMTEC 2002 CY - Florence, Italy DA - 2002-07-14 PY - 2003 PB - Techna CY - Faenza AN - OPUS4-1894 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Berger, Georg T1 - Offenporige Keramiken für den Knochenersatz T2 - Vorlesung im Rahmen der Ringvorlesung 0334 VL 113 "Aufbau und Eigenschaften moderner Biomaterialien" (Technische Universität Berlin/Humboldt Universität zu Berlin, Charité/Freie Universität Berlin) CY - Berlin, Deutschland DA - 2002-01-28 PY - 2002 AN - OPUS4-1896 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Berger, Georg T1 - Calciumhaltiger resorbierbarer Knochenersatz - Beginn und aktuelle Entwicklungen T2 - 1. Workshop "Keramische Biomaterialien" CY - Freiberg, Deutschland DA - 2002-06-14 PY - 2002 AN - OPUS4-1897 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Knabe, C. A1 - Howlett, C.R. A1 - Markovic, B. A1 - Gildenhaar, Renate A1 - Berger, Georg A1 - Zreiqat, H. T1 - Beeinflussung der Gen- und Proteinexpression von Osteoblasten durch bioaktive resorbierbare Glaskeramiken T2 - Bericht der 2. gemeinsamen Jahrestagung der Deutschen Gesellschaft für Implantologie im Zahn-, Mund- und Kieferbereich, der Österreichischen Gesellschaft für orale Chirurgie und Implantologie sowie der Schweizerischen Gesellschaft für orale Implantologie CY - München, Deutschland DA - 2002-12-05 PY - 2002 AN - OPUS4-1898 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jäger, Christian A1 - Pauli, Jutta A1 - Berger, Georg A1 - Spitzer, Andrea T1 - Entwicklung neuartiger Knochenersatzwerkstoffe und strukturelle Charakterisierung mittels der 31P-NMR-Spektroskopie T2 - Tagung "Tag der Chemie" CY - Berlin, Deutschland DA - 2002-12-04 PY - 2002 AN - OPUS4-1900 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Giese, Lutz A1 - Seibt, A. A1 - Pekdeger, A. A1 - Woith, H. T1 - Geochemische Charakterisierung der Fluide der Bohrung E Groß Schönebeck 3/90 im Hinblick auf eine geothermische Nutzung PY - 2002 UR - http://www.gtn-online.de/frame/index-publik.htm VL - 10 IS - Sonderausgabe anläßlich des 10. Firmenjubiläums des Herausgebers SP - 8 EP - 9 CY - Neubrandenburg AN - OPUS4-1874 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Trappe, Volker T1 - Zerstörungsfreie Charakterisierung des Schädigungszustandes von CFK infolge intralaminarer Ermüdungsbeanspruchung T2 - Jahrestagung Zerstörungsfreie Materialprüfung 2001 CY - Berlin, Deutschland DA - 2001-05-21 PY - 2001 UR - http://www.ndt.net/article/dgzfp01/papers/v39/v39.htm N1 - Serientitel: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. – Series title: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. IS - 75-CD PB - DGZfP CY - Berlin AN - OPUS4-1875 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Trappe, Volker A1 - Harbich, Karl-Wolfram A1 - Ernst, Hardy T1 - Intralaminar Fatigue Behaviour of CFRP T2 - European Conference on Spacecraft Structures Materials and Mechanical Testing CY - Toulouse, France DA - 2002-12-11 PY - 2002 AN - OPUS4-1878 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grätz, Rainer A1 - Förster, H. T1 - Prüfung und Auswahl von Flammendurchschlagsicherungen T2 - 6. Fachtagung Anlagen-, Arbeits- und Umweltsicherheit CY - Köthen, Deutschland DA - 2002-11-07 PY - 2002 IS - Abschnitt P04 SP - P13 PB - GVC CY - Düsseldorf AN - OPUS4-1880 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weh, Lothar T1 - Selbstorganisation in Filmen von PMMA-Lösungen auf Glasfasern T2 - 16. Vortragstagung der GDCh-Fachgruppe Waschmittelchemie ; 11. Ostwald-Kolloquium der Kolloidgesellschaft e. V. "Strukturierte Oberflächen" CY - Würzburg, Deutschland DA - 2002-04-08 PY - 2002 SP - P4 AN - OPUS4-1871 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reinsch, Stefan A1 - Chládek, Jirí A1 - Müller, Ralf A1 - Weh, Lothar T1 - Viskoses Fließen und Oberflächenkristallisation an Vickerseindrücken T2 - 76. Glastechnische Tagung CY - Bad Soden, Deutschland DA - 2002-05-27 PY - 2002 SP - 250 EP - 253 PB - DGG, Deutsche Glastechnische Gesellschaft e.V. CY - Frankfurt/M. AN - OPUS4-1872 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Osterloh, Kurt A1 - Ewert, Uwe T1 - EFNDT WG5 APMD, achievements and future tasks N2 - The existence of some 100 million active mines threatens human life and curtails substantially the economic base in over 70 countries. Humanitarian demining is tedious and it currently only employs metal detectors, prodders, dogs and armoured mechanical vehicles. Achieving a world free of mines within a period of 10 years as stipulated in international treaties requires safer and more efficient technologies. In response to this challenge the Working Group 5 of the European Federation for Non-Destructive Testing (EFNDT WG5) was founded in Berlin in March 1999. The subject of this working group now consisting of 50 members from 17 countries is the detection of antipersonnel mines (APMD). The basic idea was to investigate existing NDT methods into their ability to aid mine detection. The scope of activities ranged from collecting available information, setting up links to related organisation, defining terminology and standards to selecting dedicated research projects. Since some of these tasks are already conducted by other organisations on an European and international level the attention of the working group has been focused mainly on two R&D areas and on reliability assessment studies. Otherwise, EFNDT WG5 APMD nevertheless remains open to novel approaches in mine detection. Aim of all activities is to provide deminers with safer and more efficient tools than merely with prodders and metal detectors currently used for their dangerous task. T2 - 8th ECNDT CY - Barcelona, Spain DA - 2002-06-17 PY - 2002 UR - http://www.ndt.net/article/ecndt02/455/455.htm SP - 1 EP - 10 PB - European Federation for Non-Destructive Testing CY - Barcelona AN - OPUS4-1981 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Osterloh, Kurt A1 - Ewert, Uwe T1 - Technologies and Recent Developments to Inspect Suspicious Objects (Principles) T2 - EFNDT Working Group 5 - for Antipersonnel Mines Detection CY - Zagreb, Croatia DA - 2002-03-04 PY - 2002 VL - 5 SP - 1 EP - 4 AN - OPUS4-1982 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beckmann, Jörg A1 - Osterloh, Kurt A1 - Malitte, Hans-Joachim A1 - Ewert, Uwe T1 - Radiographic Imaging for Assessment of UXO, Suspected of Chemical Warfare Material N2 - Radiography is a helpful method to identify the inherent structure of unexploded ordnances (UXO’s). Portable Computed Radiography (CR) systems on the basis of phosphor imaging plates , have attracted attention for NDT-applications during the last few years. A portable IP system “ACR 2000” has been tested for X-ray inspection of UXO's in the field. Digitised radiographs are presented to explain the needs and demands for a reliable characterisation of UXO's. Computed radiographs of UXO’s are compared with film radiographs exposed in the same way, to evaluate the reliability and to identify advantages and disadvantages of the CR system for UXO inspection. Film based and CR systems provide sufficient information for identification of chemical warfare agents in UXO's, which is an essential problem for explosive ordnance disposal. The advantages and the potential of the portable CR system is discussed on the basis of experiences gathered during different field trails. T2 - 8th ECNDT CY - Barcelona, Spain DA - 2002-06-17 PY - 2002 UR - http://www.ndt.net/article/ecndt02/146/146.htm PB - European Federation for Non-Destructive Testing CY - Barcelona AN - OPUS4-1996 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Unger, Wolfgang T1 - Methoden der Oberflächen- und Schichtanalytik - Anwendungen, Normung und Qualitätssicherung T2 - 12. Jahreskolloquium "Analyse von Feststoffen unterschiedlicher Materialien aus Industrie und Umwelt" CY - Berlin, Deutschland DA - 2002-11-19 PY - 2002 AN - OPUS4-1997 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kautek, Wolfgang A1 - Daminelli-Widany, Grazia A1 - Cortona, Anna A1 - Kühnemund, Lutz T1 - Pulse laser electrochemistry - a novel approach for accelerated corrosion monitoring of lightweight alloys T2 - ECS Conference "Corrosion Problems in Industry" CY - Sharm El-Sheikh, Egypt DA - 2002-12-16 PY - 2002 AN - OPUS4-1998 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Christina A1 - Elagin, Mstislav A1 - Rosenthal, Martina A1 - Redmer, Bernhard A1 - Ewert, Uwe A1 - Schafer, Lloyd A1 - Wilrich, Peter-Th. T1 - Reliability Investigation of NDE Systems by Modular Analysis of Recorded Data N2 - During the second European-American Workshop on NDE Reliability, September 99 in Boulder, the term NDE reliability was defined as the degree that an NDT system is capable of achieving its purpose regarding detection, characterization and false calls. The most common – but also most expensive - way to determine this degree of capability in e.g. defect detection is to make just a performance demonstration using realistic test samples and to count the correct detections and false calls. For a more efficient way of reliability evaluation we propose to decompose the system into main modules e.g. according to the reliability formula set up on the first workshop: into f(IC) – a function of IC the intrinsic capability, determined by the physics and the technique of the NDE method representing an ideal upper bound of the reliability and g(AP) – a function of AP the industrial application factor like surface state or limited access to a component in general diminishing the ideal capability and finally h(HF) the function of the human factor which is in general also diminishing the ideal capability. The workshop proposed a rather plain mathematical shape for the formula R = f(IC) – g(AP) – h(HF) which should be considered merely as a “philosophical” expression but not as exact mathematical formula to be applied for evaluation of e.g. POD data. We propose to decompose the NDE system into modules in terms of functions of IC, AP and HF if appropriate or additional ones if necessary and then to analyze the mutual relationships of the terms via fault tree analysis. Finally the total reliability of the system is composed of the reliability of the subsystems via the rules of statistical systems theory. First trials for this approach of data analysis will be presented via examples from NDE systems in the aerospace industry. T2 - 8th ECNDT CY - Barcelona, Spain DA - 2002-06-17 PY - 2002 UR - http://www.ndt.net/article/ecndt02/428/428.htm N1 - Geburtsname von Rosenthal, Martina: Scharmach, M. - Birth name of Rosenthal, Martina: Scharmach, M. VL - 8 SP - 1(?) EP - 14(?) PB - European Federation for Non-Destructive Testing CY - Barcelona AN - OPUS4-2013 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Christina T1 - 3rd European-American Workshop on Reliability of NDE and Demining T2 - NDRF Summer Conference 2002 CY - Rosersberg, Sweden DA - 2002-08-28 PY - 2002 SP - 1(?) AN - OPUS4-2014 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Christina A1 - Rosenthal, Martina A1 - Konchina, V. A1 - Markucic, D. A1 - Piscenec, Z. T1 - General principles of reliability assessment of NDE systems and its applicability to the mine detection practice N2 - The reliability investigations are dedicated to throw light on the performance of the NDE system with respect to the required aim. This is especially of interest when it is looked for life damaging objects in the case of mine seeking and when it is even more difficult to distinguish between the different suppliers of methods concerning their actual capability. In accordance with the conception of EFNDT WG5 and CEN BT 126 CW 07 the authors have the aim to transfer the knowledge in reliability measurement of NDE systems to the reliability measurement of mine detection systems. For this the three basic ways to investigate the reliability of NDE signals will be described. The first way of investigation, the performance demonstration, is preferred e.g. in the US American nuclear power industry. This is an integral consideration of the non destructive test as a system where the whole NDE system is packed in a black box and only the input in terms of the real existing flaws in the component is considered and compared to the output in terms of the indications of the human inspector or of the automated system. The second - the European tradition – relies on a standardized description of physical/technical parameters of the NDE system which are preconditions for successful system performance. The third approach - the modular conception - is a marriage of both: The signal chain is cut into main modules. Each module is assessed in a most appropriate individual way e.g. via modeling calculations. The single results are joint together according to the reliability theory of systems where the reliability of the total system is composed of the reliability of the subsystems. Separating criteria for the system were proposed through a reliability formula developed during a series of European-American workshops on NDE reliability. A further essential parameter especially for demining systems are the repeatability and reproducibility. Their affect on the reliability and its scatter will be investigated. Examples for the ROC/POD approach in terms of the investigation of the reliability of ultrasonic manual testing and for first attempts for the reliability investigation of demining data will be presented. It will be strongly recommended to apply the ROC/POD and Modular Conceptions to the assessment and optimization of mine seeking systems. T2 - 8th ECNDT CY - Barcelona, Spain DA - 2002-06-17 PY - 2002 UR - http://www.ndt.net/article/ecndt02/397/397.htm N1 - Geburtsname von Rosenthal, Martina: Scharmach, M. - Birth name of Rosenthal, Martina: Scharmach, M. PB - European Federation for Non-Destructive Testing CY - Barcelona AN - OPUS4-2015 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Christina A1 - Rosenthal, Martina A1 - Henley, St. T1 - Metal Detector Test Trials in Afghanistan March 2002 T2 - NDRF Summer Conference 2002 CY - Rosersberg, Sweden DA - 2002-08-28 PY - 2002 N1 - Geburtsname von Rosenthal, Martina: Scharmach, M. - Birth name of Rosenthal, Martina: Scharmach, M. SP - 1(?) AN - OPUS4-2016 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Christina A1 - Rosenthal, Martina A1 - Wilrich, Peter-Th. A1 - Konchina, V. A1 - Markucic, D. A1 - Piscenec, Z. T1 - Proposals for Performance Demonstration and Modular Validation T2 - NDRF Summer Conference 2002 CY - Rosersberg, Sweden DA - 2002-08-28 PY - 2002 N1 - Geburtsname von Rosenthal, Martina: Scharmach, M. - Birth name of Rosenthal, Martina: Scharmach, M. SP - 1(?) EP - 10(?) AN - OPUS4-2017 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Christina A1 - Ewert, Uwe A1 - Rosenthal, Martina A1 - Völker, J. A1 - Schafer, Lloyd A1 - Wilrich, Peter-Th. T1 - Concepts in reliability measurement T2 - European-American Workshop 2002 CY - Berlin, BAM, Germany DA - 2002-09-11 PY - 2002 N1 - Geburtsname von Rosenthal, Martina: Scharmach, M. - Birth name of Rosenthal, Martina: Scharmach, M. SP - 1 EP - 9 AN - OPUS4-2018 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Christina T1 - Proposals for Performance Demonstration and Modular Validation T2 - 3rd DTIF workshop CY - Ispra, Italy DA - 2002-09-23 PY - 2002 SP - 1 EP - 8 AN - OPUS4-2019 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Christina A1 - Rosenthal, Martina T1 - Metal Detector Test Trials in Afghanistan March 2002 T2 - European-American Workshop 2002 CY - Berlin, BAM, Germany DA - 2002-09-11 PY - 2002 N1 - Geburtsname von Rosenthal, Martina: Scharmach, M. - Birth name of Rosenthal, Martina: Scharmach, M. SP - 1(?) AN - OPUS4-2020 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Smith, A. A1 - Müller, Christina A1 - Rosenthal, Martina T1 - Accidents and Incidents in Humanitarian Demining (HD) - the Need to Keep Accurate Records for Meaningful Analysis T2 - European-American Workshop 2002 CY - Berlin, BAM, Germany DA - 2002-09-11 PY - 2002 N1 - Geburtsname von Rosenthal, Martina: Scharmach, M. - Birth name of Rosenthal, Martina: Scharmach, M. AN - OPUS4-2021 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fücsök, F. A1 - Müller, Christina A1 - Rosenthal, Martina T1 - Reliability of Routine Radiographic Film Evaluation - an Extended ROC Study of the Human Factor N2 - Many radiographic exposures and film evaluations are made daily in a typical industrial NDT laboratory. But questions remain regarding the precise probability of detecting discontinuities, including the reliability of each individual inspector or laboratory. Although most experienced inspectors of the laboratories evaluate each radiograph, the actual quantitative reliability of each of these inspectors remains unknown. In order to estimate the performance of representative inspectors and laboratories involved in NDE, volunteer laboratories from Croatia and Hungary conducted a series of round-robin inspections using X-ray films of welds. While the RRT is still in progress, the authors try to summarize the results of the “second round” and discuss the evaluation method. The results of the “first round” had been reported already. The focus is here to present the new results in terms of additional inspectors and a new more field oriented evaluation scheme. So far the results of a total of 35 inspectors of the different laboratories were evaluated. Those inspectors were selected who have done usually the work of radiographic film interpretation. They have from a half up to 35 years professional experience. For better overview we created four groups: maximum 4 year-experience, from 5 to 12 year-experience, from 15 to 25 year- experience and from 26 to 35 year-experience. Discussing the circumstances of the RRT with the participants, many of them expressed, they could not exactly follow the prescription of the test. According to their professional experience the small discontinuities can be omitted because of the strictest acceptance level accept them. So the most experienced evaluators did not write the small gases and slags into the list, which yield a wrong reliability of detection. As a consequence we should accomplish two types of evaluation: taking into consideration of all discontinuity and only the bigger once they are over the acceptance level. In addition we analyzed the “true values” in a critical review. These developments were made and the new results of the evaluation of the testers were more precise and reliable. The corresponding results are evaluated and presented in a ROC diagram where the p(TP) is plotted against the p(FP). The p(TP) means the probability of a true positive indication (correct defect finding) and p(FP) means the probability of a false positive (false alarm) indication. From the mean value of all inspectors maximum operation points we can estimate a representative overall reliability in terms of a correct indication rate of about 68 % (64 % new) and a false call rate of about 17 % (8 % new). This is a reasonable result within the strict 1 cm score. T2 - 8th ECNDT CY - Barcelona, Spain DA - 2002-06-17 PY - 2002 UR - http://www.ndt.net/article/ecndt02/429/429.htm N1 - Geburtsname von Rosenthal, Martina: Scharmach, M. - Birth name of Rosenthal, Martina: Scharmach, M. PB - European Federation for Non-Destructive Testing CY - Barcelona AN - OPUS4-2022 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Richter, Klaus T1 - Analog and digital ISO/IEC-colour charts for different colour reproduction tests and for the efficient use of colour in design T2 - AIC Color 2002 ; Color & Textiles ; Proceedings of the Interim Meeting CY - Maribor, Slovenia DA - 2002-08-29 PY - 2002 UR - http://www.ps.bam.de/AICMAR.PDF SP - 356 EP - 367 AN - OPUS4-2005 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Merchel, Silke A1 - Dudzus, Thomas A1 - Ecker, Klaus A1 - Hedrich, Martina A1 - Kipphardt, Heinrich A1 - Recknagel, Sebastian T1 - Viele (BAM-) Wege führen zu den leichten Elementen T2 - 12. Jahrescolloquium "Analyse von Feststoffen unterschiedlicher Materialien aus Industrie und Umwelt" CY - Berlin, Deutschland DA - 2002-11-19 PY - 2002 SP - 1(?) AN - OPUS4-2024 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schönhals, Andreas A1 - Goering, Harald A1 - Schick, C. ED - Schick, C. T1 - Molecular dynamics and thermodynamics of polymers confined to nanoporous glasses T2 - 7th Lähnwitzseminar on Calorimetry ; 17th IUPAC Conference on Chemical Thermodynamics CY - Rostock, Germany DA - 2002-07-28 PY - 2002 VL - 403 IS - 1 PB - Elsevier CY - Amsterdam AN - OPUS4-2030 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rudert, Rainer A1 - Rabe, Torsten T1 - Characterisation of ceramic samples by scanning acoustic microscopy (SAM) T2 - DKG & NKV Annual Meeting CY - Eindhoven, The Netherlands DA - 2002-10-21 PY - 2002 SP - 108 AN - OPUS4-2031 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Keller, Christian T1 - Beitrag zur numerischen Beanspruchungsanalyse an dünnwandigen Stahlblechcontainern im Fallversuch - Schädigungsmechanische Materialmodellierung duktiler Werkstoffe unter Berücksichtigung der Dehnratenabhängigkeit der plastischen Instabilität N2 - Gegenstand der vorliegenden Arbeit ist die Bereitstellung expliziter numerischer Simulationen von Fallversuchen mit dünnwandigen Stahlblechcontainern, die als Endlagerbehälter für radioaktive Abfälle mit vernachlässigbarer Wärmeentwicklung, d. h. schwach- und mittelradioaktive Abfälle, für die Verbringung in das Endlager Konrad vorgesehen sind. Die Betrachtung von potentiellen Absturzszenarien ist ein grundlegender und zentraler Bestandteil der Sicherheitsnachweise zur Auslegung der verschiedenen endlagergängigen Behälter- und Containertypen gegen mechanische Störfallbelastungen. Für dünnwandige Stahlblechcontainer existierten bislang keine sicherheitstechnischen Untersuchungen, die auf numerischen Bewertungsmethoden basieren und eine Bewertung der vorhandenen Sicherheitsreserven hinsichtlich der mechanischen Integrität ermöglichen. Daraus resultierte die Motivation, ein verifiziertes Finite-Elemente-Modell eines repräsentativen Referenzcontainers zu entwickeln, das das dynamische Verformungs- sowie duktile Schädigungs- und Versagensverhalten in numerischen Simulationen von dynamischen Lastfällen physikalisch mit der erforderlichen Güte beschreibt. Duktile Schädigungs- und Versagensvorgänge metallischer Werkstoffe gehen grundsätzlich mit großen plastischen Dehnungen einher und führen somit unweigerlich zu der Notwendigkeit der Diskussion von plastischer Instabilität und damit verknüpften Lokalisierungseffekten, die einen wesentlichen Einfluss auf die Entwicklung des lokalen Beanspruchungszustands haben. Für die schädigungsmechanische Materialmodellierung folgt hieraus das grundsätzliche Erfordernis der korrekten Berücksichtigung des Instabilitätsbeginns, der in der Regel dehnratenunabhängig angenommen wird. Für dynamische Randbedingungen ist der werkstoffspezifische Einfluss der Dehnrate auf das Einsetzen der Lokalisierung jedoch nicht uneingeschränkt vernachlässigbar, so dass im Rahmen dieser Arbeit ein theoretischer Ansatz ausgearbeitet wird, der die plastische Instabilität dehnratenabhängiger Werkstoffe anhand des zeit- und ortsabhängigen Dehnungsgradienten im einachsigen Zugversuch diskutiert. Darüber hinaus ist für eine hinreichend genaue Materialmodellierung neben der korrekten Prognose des Instabilitätsbeginns auch die korrekte Beschreibung des Verformungsverhaltens jenseits der Gleichmaßdehnung notwendig. Zu diesem Zweck wird in dieser Arbeit eine konstitutive Beziehung entwickelt, die sowohl unter Berücksichtigung der plastischen Instabilität als auch unter der Beachtung von ver- sowie entfestigenden Einflussfaktoren der dynamischen Plastizität formuliert werden kann. Insgesamt wird eine praxistaugliche Bewertungsmethode der mechanischen Integrität dünnwandiger Stahlblechcontainer unter Störfallbedingungen auf Basis expliziter dynamischer Simulationen erarbeitet, die die komplexen duktilen Schädigungs- und Versagensmechanismen dehnratenabhängiger Werkstoffe berücksichtigt. Mit der zur Simulation von Fallversuchen entwickelten numerischen Modellbildung und den zur Verifizierung entsprechend mit Testcontainern im Originalmaßstab durchgeführten Fallversuchen wird nachgewiesen, dass anhand des Finite-Elemente-Modells eines repräsentativen Referenzcontainers zum einen eine quantitativ belegte Bestimmung ungünstiger Fallorientierungen hinsichtlich maximaler Verformungen und zum anderen eine realistische Abbildung des duktilen Versagensverhaltens ermöglicht wird. Damit können tatsächlich vorhandene Sicherheitsreserven bei potentiell zu unterstellenden Behälterabstürzen quantitativ aufgezeigt und zukünftig eine verbesserte sicherheitstechnische Beurteilung von Stahlblechcontainern im Fallversuch bereitgestellt werden. Damit leistet die vorliegende Arbeit einen wichtigen Beitrag für die Bewertung von Sicherheitsnachweisen von Endlagerbehältern für radioaktive Abfälle und trägt dazu bei, den langfristigen Schutz von Mensch und Umwelt vor Schäden durch radioaktive Stoffe zu gewährleisten. N2 - The subject of the present work is the provision of explicit numerical simulations of drop tests with thin-walled sheet steel containers, which are intended as repository containers for radioactive waste with negligible heat generation, i.e. low and intermediate level waste, for shipment to the Konrad repository. The consideration of potential crash scenarios is a fundamental and central component of the safety analyses for the design of the various types of casks and containers suitable for final disposal against mechanical accident loads. For thin-walled sheet steel containers, no safety investigations based on numerical assessment methods existed so far that would allow an evaluation of the existing safety reserves with regard to mechanical integrity. This resulted in the motivation to develop a verified finite element model of a representative reference container that physically describes the dynamic deformation and ductile damage and failure behaviour in numerical simulations of dynamic load cases with the required quality. Ductile damage and failure processes of metallic materials are fundamentally accompanied by large plastic strains and thus inevitably lead to the need to discuss plastic instability and associated localisation effects, which have a significant influence on the development of the local stress state. For damage-mechanical material modelling this results in the fundamental requirement of correctly considering the onset of instability, which is usually assumed to be strain-rate independent. For dynamic boundary conditions, however, the material-specific influence of the strain rate on the onset of localisation cannot be neglected without restriction, so that a theoretical approach is elaborated within the scope of this work that discusses the plastic instability of strain-rate-dependent materials on the basis of the time- and location-dependent strain gradient in the uniaxial tensile test. Furthermore, for a sufficiently accurate material modelling, besides the correct prediction of the onset of instability, the correct description of the deformation behaviour in the postcritical region, i.e., beyond the uniform strain, is necessary. For this purpose, a constitutive relationship is developed in this work, which can be formulated both under consideration of the plastic instability as well as under consideration of hardening as well as softening influencing factors of the dynamic plasticity. Overall, a practical assessment method of the mechanical integrity of thin-walled sheet steel containers under accident conditions is developed based on explicit dynamic simulations, which takes into account the complex ductile damage and failure mechanisms of strain rate-dependent materials. With the numerical modelling developed for the simulation of drop tests and the drop tests carried out accordingly with full-scale test containers for verification, it is demonstrated that, on the basis of the finite element model of a representative reference container, on the one hand a quantitatively proven determination of unfavourable drop orientations with regard to maximum deformations and, on the other hand, a realistic representation of the ductile failure behaviour is made possible. This allows it to quantitatively demonstrate actually existing safety reserves in case of potential container crashes and to provide an improved safety assessment of sheet steel containers in drop tests in the future. This work thus makes an important contribution to the evaluation of safety verifications of final storage containers for radioactive waste and helps to ensure the long-term protection of humans and the environment from damage caused by radioactive substances. KW - FEM KW - Dynamische Plastizität KW - Plastische Instabilität KW - Duktile Schädigung KW - Endlager Konrad PY - 2024 DO - https://doi.org/10.14279/depositonce-21874 SP - 1 EP - 188 PB - DepositOnce CY - Berlin AN - OPUS4-61581 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hertwig, Andreas A1 - Ermilova, Elena T1 - Optical constants of a single AlN layer on Si N2 - Spectroscopic ellipsometry was used to determine the thickness and dielectric function of a Aluminium Nitride (AlN) layer on a Si wafer. The layer was determined to be 170 nm thick. The layer was provided by AIXTRON and manufactured by means of MOVPE. The data was created using a M2000DI spectroscopic ellipsometer from Woollam Co. Inc. Analysis was done using the CompleteEASE software. The model used is a multi-peak oscillator model for the AlN layer. The data resembles common database values for the material AlN. KW - Aluminium nitride KW - Thin solid layers KW - Spectroscopic ellipsometry KW - Compund semiconductors KW - MOVPE PY - 2024 UR - https://zenodo.org/records/12743500 DO - https://doi.org/10.5281/zenodo.12743499 PB - Zenodo CY - Geneva AN - OPUS4-60661 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völker, Christoph A1 - Kruschwitz, Sabine A1 - Moreno Torres, Benjami A1 - Firdous, R. A1 - Zia, G. J. A. A1 - Stephan, D. T1 - Accelerating the search for alkali-activated cements with sequential learning N2 - With 8% of man-made CO2 emissions, cement production is an important driver of the climate crisis. By using alkali-activated binders, part of the energy-intensive clinker production process can be dispensed. However, as numerous raw materials are involved in the manufacturing process here, the complexity of the materials increases by orders of magnitude. Finding a properly balanced binder formulation is like looking for a needle in a haystack. We have shown for the first time that artificial intelligence (AI)-based optimization of alkali-activated binder formulations can significantly accelerate research. The "Sequential Learning App for Materials Discovery" (SLAMD) aims to accelerate practice transfer. With SLAMD, materials scientists have low-threshold access to AI through interactive and intuitive user interfaces. The value added by AI can be determined directly. For example, the CO2 emissions saved per ton of cement can be determined for each development cycle: the more efficient the AI optimization, the greater the savings. Our material database already includes more than 120,000 data points of alternative binders and is constantly being expanded with new parameters. We are currently driving the enrichment of the data with a life cycle analysis of the building materials. Based on a case study we show how intuitive access to AI can drive the adoption of techniques that make a real contribution to the development of resource-efficient and sustainable building materials of the future and make it easy to identify when classical experiments are more efficient. T2 - fib International Congress CY - Oslo, Norway DA - 12.06.2022 KW - Concrete KW - Materials Design KW - Sequential Learning KW - Machine Learning PY - 2022 SP - 1 EP - 9 AN - OPUS4-56634 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Duarte, Larissa A1 - Madia, Mauro A1 - Zerbst, Uwe T1 - The use of effective fatigue crack propagation data obtained at closure-free conditions for component assessment N2 - The knowledge of fatigue crack propagation data in terms of their effective values is important for a conservative and safe life assessment of components subjected to cyclic loading. To overcome issues related to the precise consideration of the crack-closure effects on experimental data obtained at small R ratios, closure-free data have been obtained at R ≈ 0.8 by different experimental procedures. The statistical analysis of the intrinsic fatigue crack propagation threshold obtained experimentally has shown a small data scatter and good agreement between procedures. When compared with effective values obtained from analytical corrections of closure-affected data, the data obtained at R ≈ 0.8 should lead to a conservative life estimation. T2 - 43rd International Conference on Materials Mechanics CY - Sani, Greece DA - 05.06.2022 KW - Component assessment KW - Effective crack propagation data KW - Experimental procedure KW - Crack-closure PY - 2022 SP - 104 EP - 108 AN - OPUS4-56851 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bulling, Jannis A1 - Jurgelucks, B. A1 - Prager, Jens A1 - Walther, A. T1 - Modellierung und Validierung eines inversen Verfahrens zur Schadensrekonstruktion mittels Lamb-Wellen im Ultraschallbereich N2 - Das Ausbreitungsverhalten geführter Ultraschallwellen ermöglicht die großflächige Prüfung von Platten und schalenförmigen Bauteilen wie Rohren und Laminaten auf Fehlstellen von wenigen Prüfpunkten aus. Während die beschränkte Divergenz der geführten Wellen die Ultraschallprüfung begünstigt, erschwert das dispersive und multimodale Verhalten der Lamb-Wellen die Auswertung der Ultraschallsignale. Die dispersive und multimodale Wellenausbreitung verkompliziert die Bestimmung der Fehlerposition bei der Auswertung der Geschwindigkeiten einzelner Wellenpakete. Zudem ist es herausfordernd, einen einfachen Zusammenhang zwischen den Reflexionen der Fehlstelle und deren Größe und Form herzustellen. Eine Möglichkeit zur genauen Bestimmung der Fehlerposition und -geometrie bietet der direkte Vergleich der Messsignale mit den Signalen aus einem Simulationsmodell. Die Nachbildung des Schadens im Simulationsmodell stellt ein inverses Problem dar, das iterativ gelöst werden kann, indem ein Vorwärtsmodell immer weiter optimiert wird. Klassische Ansätze wie die Finite Elemente Methode (FEM) sind für die Simulation von Ultraschallwellen aufgrund der kleinen Wellenlängen im Vergleich zur Bauteilgröße meist ineffizient. Aus diesem Grund basiert das vorgestellte Vorwärtsmodell auf der semi-analytischen Scaled Boundary Finite Element Method (SBFEM), die große Teile der Wellenausbreitung analytisch berechnet. In diesem Beitrag wird die Validierung des zweidimensionalen Modells an Platten mit einer rechteckigen Nut als Ersatzfehler präsentiert und es werden erste Schritte zur Validierung von 3D-Modellen vorgestellt. T2 - DAGA 2024 CY - Hannover, Germany DA - 18.03.2024 KW - Geführter Ultraschall KW - Inverse Verfahren KW - SBFEM PY - 2024 UR - https://www.dega-akustik.de/publikationen/online-proceedings SP - 644 EP - 647 AN - OPUS4-60212 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Duarte, Larissa A1 - Madia, Mauro A1 - Zerbst, Uwe A1 - Schönherr, J. A. A1 - Geilen, M. B. A1 - Klein, M. A1 - Oechsner, M. T1 - Recent developments in the determination of fatigue crack propagation thresholds N2 - The impact of crack closure and environmental effects on the experimental determination of the fatigue crack propagation threshold is a major problem for the assessment of cyclically loaded components, especially at low stress ratios 𝑅. In this work, the influence of the experimental procedure and air humidity on d𝑎∕d𝑁 − 𝛥𝐾 data at different 𝑅 is discussed. Unlike the results at 𝑅 = −1, the threshold values obtained at 𝑅 ≈ 0.8, i.e. under negligible crack closure levels, show a very small scatter band regardless of the variation of the test parameters and environmental conditions. KW - Fatigue crack propagation threshold KW - Component assessment KW - Crack closure KW - Environmental effects KW - Testing parameters PY - 2022 DO - https://doi.org/10.1016/j.ijfatigue.2022.107131 SN - 0142-1123 VL - 164 SP - 1 EP - 15 PB - Elsevier Ltd. AN - OPUS4-55403 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Laskina, Sofya T1 - Computing the forward and inverse problem of X-ray scattering N2 - Continuing progress in the field of X-ray scattering methods empowers scientists with new possibilities to capture the most important piece of information about the structure of the sample - its 3D electron density. Although the first methods appeared almost a century ago, recovering the density structure of a sample is still very problematic. Most avail-able imaging techniques transform a 3D electron density of a realspace structure into the 2D Fourier Transform of the intensity of scattered waves in the reciprocal space. This process causes a loss of information. Firstly, instead of a 3D sample, a 2D image is created, and secondly, the phase information of the scattered waves is lost. The latter is known as the ”phase problem” and poses a serious obstacle on a way to recover a 3D electron density. In this work, we draw attention to the problem of forward and inverse Small Angle X-Ray Scattering. In the first, forward, part, we rethink the existing pipelines to computationally simulate such scattering experiments. Although there are efficient implementations of fast Fourier transformation, they often have some drawbacks. For instance, to calculate a 3D fast Fourier transform it is required to place its density in the RAM. For high-resolution structures of size > 1024 3 , this becomes very problematic, as the whole density structure requires more than 16 GB of memory. CUDA solution allows for a very fast and parallelizable implementation of high-resolution data on hundreds of last-generation machines. Such computations are very pricy and inaccessible for most scientists. To bypass this limitation, we propose a solution for a split-up 3D fast Fourier transform, which is implemented as a sequence of 2D and 1D operations. We compare our implementation on the simulated 3D shapes and show the result of a proof-of-concept on 4096 3 Metallorganic framework density structure. In the second, inverse problem, we train an invertible neural network, that given scattering data can predict the shape and its parameters. The architecture is built such, that the inverse problem is learned together with the forward process - the Fourier Transformation. We achieved very good results with this architecture, nonetheless, further testing is required, as the current training set only encompasses three simple shapes: sphere, hard sphere and cylinder. All code to reproduce and analyze the results is available at https: //github.com/sofyalaski/SAXS-simulations. KW - Machine Learning KW - SAXS KW - DFT PY - 2023 SP - 1 EP - 76 PB - Freie Universität Berlin CY - Berlin AN - OPUS4-56798 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Schmidt, Alexandra A1 - Bresch, Harald A1 - Kämpf, K. A1 - Bachmann, V. A1 - Peters, T. A1 - Kuhlbusch, T. T1 - Development of a specific OECD Test Guideline on Particle Size and Particle Size Distribution of Nanomaterials N2 - In this research project, a new OECD Test Guideline (TG) for the determination of “Particle Size and Particle Size Distributions of Nanomaterials” was developed as the existing OECD TG 110 is considered to be outdated in terms of applicable size range (not covering sizes <200 nm) and methods. By its scope with an applicable size range from 1 to 1000 nm the new Test Guideline (TG PSD) covers the whole nanoscale. The TG PSD is applicable for particulate and fibrous nanomaterials. The prescribed, pairwise measurement of fibre diameter and length in the TG PSD allows for the first time to differen-tiate fibres with regard to their size-dependent hazard properties. Measurement instructions for each included method were validated within two separated interlaboratory comparisons, as a distinction between near spherical particles and fibres when applying the methods has to be made. Besides information on content and structure of the TG PSD, this final report outlines essential steps, considerations and organisational aspects during the development of the TG. Insights into the selec-tion, preparation and prevalidation of test materials used in the interlaboratory comparison are given. Finally, main results of the interlaboratory comparisons and their impacts on the TG PSD are pre-sented. N2 - Im Rahmen des Forschungsprojekts wurde eine neue OECD-Prüfrichtlinie (TG) für die Bestimmung von Partikelgrößen und Partikelgrößenverteilungen von Nanomaterialien entwickelt, da die existie-rende OECD TG 110 zur Bestimmung von Partikelgrößen in Bezug auf den anwendbaren Größenbe-reich und die gegebenen Methoden veraltet ist bzw. den Nanometerbereich < 200 nm nicht abdeckt. Mit ihrem Anwendungsbereich von 1 bis 1000 nm deckt die neue Prüfrichtlinie (TG PSD) die gesamte Nanoskala ab. Die TG PSD ist für partikel- und faserförmige Nanomaterialien anwendbar. Durch die, in der TG PSD vorgeschriebene, paarweise Messung von Faserdurchmesser und -länge ermöglicht diese TG zum ersten Mal Fasern hinsichtlich ihrer größenabhängigen Gefahrstoffeigenschaften zu unter-scheiden. Die Messanweisungen aller enthaltenen Methoden wurden im Rahmen von zwei getrennten Ringversuchen validiert, da bei der Anwendung der Methoden eine Unterscheidung zwischen Parti-keln und Fasern gemacht werden muss. Neben Angaben zum Inhalt und Struktur der TG PSD, befasst sich der vorliegende Abschlussbericht mit den wesentlichen Schritten, Überlegungen und organisatorischen Aspekten bei der Entwicklung der Prüfrichtlinie. Darüber hinaus werden Einblicke in die Auswahl, Vorbereitung und Prävalidierung der im Ringversuch verwendeten Testmaterialien gegeben. Schließlich werden die wichtigsten Ergeb-nisse aus den Ringversuchen und ihre Auswirkungen auf die TG PSD vorgestellt. KW - Nano KW - OECD KW - Particle size distribution KW - Testguideline KW - Nanoparticle PY - 2021 VL - 2021 SP - 1 EP - 47 PB - German Environment Agency CY - Dessau AN - OPUS4-54021 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Babutzka, Martin A1 - Valet, Svenja A1 - Kotula, Stefan A1 - Burkert, Andreas A1 - Gümmer, K. A1 - Bender, S. A1 - Huckshold, M. T1 - Normentwurf für ein Prüfverfahren zur Bestimmung von Deckschichtwiderständen an Zinküberzügen mittels gelartiger Elektrolyte N2 - Das Grundproblem der heute verfügbaren und normativ geregelten Prüfverfahren für Zinküberzüge besteht neben den realitätsfernen Prüfbedingungen vor allem in der subjektiv geprägten Auswertung der Prüfergebnisse. Die systematische Betrachtung der Entwicklungen der letzten Jahre zeigt, dass die üblichen Verfahren den aktuellen Anforderungen damit schon vom Ansatz her nicht gerecht werden können und auch die bisher betriebene, fortlaufende Variation und Anpassung von Prüfbedingungen keinen grundlegend neuen Lösungsansatz bieten können. Ein solcher ergibt sich nur, wenn die Zinküberzüge hinsichtlich der kinetischen Eigenschaften der Deckschichtbildung und -auflösung umfassend beschrieben werden können, was nur durch den Einsatz elektrochemischer Untersuchungsmethoden mittels Gelelektrolyten möglich ist. Aus diesem Grund wurde im Verbundforschungsvorhaben GELELEK auf der Basis elektrochemischer Methoden unter Verwendung eines Gelelektrolyten ein Normenvorschlag für eine Prüfnorm erarbeitet und zur Normungsreife geführt, welcher den Anforderungen an ein Messsystem für Feldanwendungen entspricht. Im Verbundforschungsvorhaben GELELEK wurde eine gezielte Kombination von Laboruntersuchungen mit Untersuchungen im Feld und Bauteilen unter realen Einsatzbedingungen angestrebt. Randbedingungen für eine gesicherte Messung von atmosphärisch bewitterten Zinküberzügen unter Einsatz von Gelelektrolyten wurden erarbeitet und im Normenvorschlag festgeschrieben. Darüber hinaus wurde ein mobiles Messgerät für Messungen mit Gelelektrolyten an realen Bauteilen entwickelt. Nach Abschluss des Forschungsvorhabens steht Industrievertretern und Prüfinstituten ein wissenschaftlich gesichertes Messverfahren basierend auf Kennwerten zur Verfügung, um Zinküberzüge und deren momentane Schutzwirkung unter praxisrelevanten Bedingungen einschätzen und normativ geregelt prüfen zu können. Der vorliegende Forschungsbericht gibt einen Überblick über die Motivation zur Durchführung des Forschungsvorhabens, wichtige Arbeitsschritte, Details zur entwickelten Prüfmethode sowie Einsatzmöglichkeiten für Prüfinstitute und Unternehmen. KW - Normung KW - Zink KW - Korrosion KW - Deckschichtbildung KW - Atmosphärische Korrosion KW - Korrosionsprüfung PY - 2022 UR - https://www.gav-verzinken.de/forschung/wissenspool SP - 1 EP - 24 AN - OPUS4-54947 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Piquemal, François A1 - Hoffmann, Johannes A1 - Gautier, Brice A1 - Hertwig, Andreas A1 - Frabricius, Norbert T1 - Publishable Summary for 20IND12 Elena Electrical nanoscale metrology in industry N2 - Consumer electronics, innovative quantum technologies, and Internet of Things applications all rely on semiconductors, where reliable characterisation of electrical properties at the nanoscale is essential for European innovation and competitiveness. The measurement of these properties allows the evaluation of critical parameters used to define the performance of electronic materials and components. Currently, Conductive Atomic Force Microscopes and Scanning Microwave Microscopes enable nanoscale electrical characterisation, but they are costly, complicated and, in many cases where they are used, unreliable as measurements are not traceable. The aim of the project was to make such measurements traceable for the first time, with stated uncertainties, and affordable by developing and testing cost effective instrumentation and the first “out of lab” reference standards from DC to GHz and by elaborating robust calibration methods and good practice guides using simplified uncertainty budgets. All the objectives were achieved. The project has successfully improved the user-friendly uncertainty quantification for the electrical measurements at the nanoscale in the industrial environment. The design of calibration standards has been improved and new standards for DC resistance / current as well as HF impedance have been introduced and quantified. Good practice guides for the calibration and uncertainty quantification have been written and will be available to the users’ community. New ways of determining the properties of standard samples like ellipsometry have been evaluated. The interaction with stakeholders and industry collaborators was very important for the consortium and several case studies were carried out with industry-relevant samples. All data, procedures, and example uncertainty data from the project are included into the standardisation process and two IEC standards projects have been started during this project. These standards will be used as one important dissemination ways for the results of the project. KW - Electrical Properties KW - Nanometrology KW - Scanning Probe Microscopy KW - Optical Surface Analysis PY - 2024 SP - 1 EP - 9 AN - OPUS4-61812 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Redmer, Bernhard A1 - Bellon, Carsten A1 - Malitte, Hans-Joachim A1 - Sölter, B. T1 - Reduction of radiation exposure through the application of new detector techniques in industrial radiography T2 - 5th Workshop on "Industrial Radiography - Improvements in Radiation Protection" CY - Rome, Italy DA - 2001-10-17 PY - 2001 SP - 1(?) EP - 24(?) AN - OPUS4-1217 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bresch, Harald A1 - Schmidt, Alexandra A1 - Kämpf, K. A1 - Bachmann, V. A1 - Peters, T. A1 - Kuhlbusch, T. T1 - Draft OECD Test Guideline for the Testing of Chemicals - Particle Size and Particle Size Distribution of Nanomaterials N2 - Final Draft of the OECD Test Guideline for Particle Size and Particle Size Distribution of Nanomaterials. The OECD Working Party on Manufactured Nanomaterials (WPMN) has actively worked towards understanding possible safety issues for manufactured nanomaterials and has contributed significantly to resolving these by developing Test Guidelines, Guidance Documents, Test Reports and other publications with the aim of a safe use of manufactured nanomaterials. The OECD website (www.oecd.org/science/nanosafety) and the referenced publications contain more background information. Among others, the OECD Test Guideline “Particle Size Distribution/Fibre Length and Diameter Distributions” (TG 110, adopted in 1981) was identified to require an update to address the specific needs of manufactured nanomaterials as the TG 110 is currently only valid for particles and fibres with sizes above 250 nm. The WPMN prioritised to either update TG 110 to be applicable also to particles at the nanoscale or draft a new nanomaterial specific Test Guideline (TG). Eventually, it was decided to develop a new TG for particle size and particle size distribution measurements of nanomaterials covering the size range from 1 nm to 1000 nm for further justification. This TG overlaps with TG 110 in the size range from 250 nm to 1000 nm. When measuring particulate or fibrous materials, the appropriate TG should be selected depending on the size range of particles tested. In line with TG 110, the new TG for nanomaterials includes separate parts for particles and fibres. For the part of this TG which addresses particles, several methods applicable to nanomaterials were reviewed and included to take into account developments since 1981 when the TG110 was adopted. This TG includes the following methods: Atomic Force Microscopy (AFM), Centrifugal Liquid Sedimentation (CLS)/Analytical Ultracentrifugation (AUC), Dynamic Light Scattering (DLS), Differential Mobility Analysis System (DMAS), (Nano)Particle Tracking Analysis (PTA/NTA), Small Angle X-Ray Scattering (SAXS), Scanning Electron Microscopy (SEM), and Transmission Electron Microscopy (TEM). For measuring the diameter and length of fibres, analysing images captured with electron microscopy is currently the only method available. This TG includes Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM). To test the validity of this TG, an ILC was performed. Test materials were chosen to reflect a broad 68 range of nanomaterial classes, e.g. metals, metal oxides, polymers and carbon materials. Where possible, well-characterised test materials were used. Additionally, the test materials were chosen, so that they reflect a broad range of sizes representing the size range 1 nm to 1000 nm and finally, for fibres only, aspect ratios from length/diameter of 3 to > 50. KW - Nano KW - OECD KW - Test guideline KW - Nanomaterial KW - Nanoparticle PY - 2021 UR - https://www.oecd.org/chemicalsafety/testing/draft-test-guideline-particle-size-distribution-nanomaterials.pdf SP - 1 PB - Organisation for Economic Co-operation and Development CY - Paris AN - OPUS4-53828 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schilling, Markus A1 - Marschall, Niklas A1 - Niebergall, Ute A1 - Böhning, Martin T1 - Dataset of comprehensive Full-notch creep tests (FNCT) of selected high-density polyethylene (PE-HD) materials N2 - The dataset provided in this repository comprises data obtained from a series of full-notch creep tests (FNCT) performed on selected high-density polyethylene (PE-HD) materials (for further details, see section 1 Materials in this document) in accordance with the corresponding standard ISO 16770. The FNCT is one of the mechanical testing procedures used to characterize polymer materials with respect to their environmental stress cracking (ESC) behavior. It is widely applied for PE-HD materials, that are predominantly used for pipe and container applications. It is based on the determination of the time to failure for a test specimen under constant mechanical load in a well-defined and temperature controlled liquid environment. The test device used here also allows for continuous monitoring of applied force, specimen elongation and temperature. KW - Polyethylene KW - Environmental Stress Cracking KW - Full-notch creep test KW - PE-HD KW - Crack growth PY - 2023 DO - https://doi.org/10.5281/zenodo.10143351 PB - Zenodo CY - Geneva AN - OPUS4-58835 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Kuchenbecker, Petra A1 - Lindemann, Franziska T1 - Particle size determination of a commercially available CeO2 nano powder - SOPs and reference data N2 - Compilation of detailed SOPs for characterization of a commercially available CeO2 nano powder including - suspension preparation (indirect and direct sonication), - particle size determination (Dynamic Light Scattering DLS and Centrifugal Liquid Sedimentation CLS) with reference data, respectively. For sample preparation and analysis by Scanning Electron Microscopy (SEM) of this powder see related works (submitted, coming soon). KW - Wet dispersion KW - Nano powder KW - Particle size KW - CeO2 KW - Ceria KW - DLS KW - CLS PY - 2023 DO - https://doi.org/10.5281/zenodo.10061079 PB - Zenodo CY - Geneva AN - OPUS4-58785 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Kuchenbecker, Petra A1 - Lindemann, Franziska T1 - SOP and reference data for determination of the Volume-specific Surface Area (VSSA) of a commercially available CeO2 nano powder N2 - Detailed SOP and reference data for the determination of the VSSA of a commercially available CeO2 nano powder: specific (BET-) Surface Area by gas adsorption (Ar and N2) skeletal (true solid state) density by gas pycnometry. Estimation of the particle size by VSSA screening method. KW - Nano powder KW - VSSA KW - Volume specific surface area KW - Screening method KW - Ceria KW - CeO2 PY - 2023 DO - https://doi.org/10.5281/zenodo.10061235 PB - Zenodo CY - Geneva AN - OPUS4-58786 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Johann, Sergej A1 - Strangfeld, Christoph A1 - Bartholmai, Matthias ED - Cosmi, Francesca T1 - RFID sensor system embedded in concrete –validation of UHF antenna geometries in different concrete depths N2 - This paper is a further research on the topic of the complete embedding of radio frequency identification (RFID) sensors in concrete. The focus is on the antenna of the transponder. Earlier investigations of different RFID technologies, embedded in concrete, showed a difference in energy transmission. The transmission through concrete at ultra high frequency (UHF), in spite of the large signal range, does not match the targeted application specific task. Therefore, the antenna characteristics have been examined more closely. The antenna is an important component for the application of RFID. Through the antenna, energy and data transfer takes place, so it is important to design an optimal antenna to accomplish a maximum embedding depths in concrete. To identify the optimal antenna geometry, different UHF antenna types were selected and investigated. An experimental comparison was performed to gain more information about the damping behavior and antenna characteristics in concrete. T2 - 34th Danubia-Adria Symposium on Advances in Experimental Mechanics CY - Trieste, Italy DA - 19.09.2017 KW - RFID sensors KW - Structural health monitoring KW - Passive RFID KW - UHF antenna KW - Sensors in concrete KW - Smart structures PY - 2017 SN - 978-88-8303-863-1 SP - 114 EP - 115 CY - Trieste AN - OPUS4-42093 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stelzner, Ludwig A1 - Powierza, Bartosz ED - Breit, W. ED - Kurz, W. ED - Pahn, M. ED - Sadegh-Azar, H. ED - Schnell, J. ED - Thiele, C. T1 - Thermisch induzierter Feuchtetransport in HPC N2 - Die Entwicklung von leistungsfähigen Fließmitteln in den letzten Jahrzehnten ermöglicht die Herstellung von Beton mit sehr geringem w/z-Wert, bei gleichzeitig guter Verarbeitbarkeit. Die Reduzierung des w/z-Wertes führt zu einer Erhöhung der Festigkeit und zu einer Verdichtung der Gefügestruktur. Aufgrund der hohen Druckfestigkeit finden Hochleistungsbetone vermehrten Einsatz im Hoch-, Brücken-, und Tunnelbau. Allerdings neigen diese Hochleistungsbetone unter Brandbeanspruchung zu explosionsartigen Abplatzungen, die nach derzeitigem Stand auf thermomechanische und thermohydraulische Prozesse zurückgeführt werden. Letztere beruhen auf der Generierung hoher Wasserdampfdrücke in einseitig brandbeanspruchten Betonbauteilen, die zum einen auf die geringe Permeabilität des Hochleistungsbetons und zum anderen auf die Bildung einer wassergesättigten Zone, der sogenannten „moisture clog“ zurückzuführen sind. Dabei spielen Verdampfungs- und Kondensationsvorgänge sowie der vorhandene Temperaturgradient eine wichtige Rolle. Die Interaktion des Feuchtetransportes mit den Gefügeveränderungen während der thermischen Beanspruchung soll im Rahmen weiterer Versuche eingehend untersucht werden. Zur Analyse des Feuchtetransports während der thermischen Beanspruchung werden miniaturisierte Prüfkörper aus Hochleistungsbeton hergestellt, die mit Hilfe eines elektrischen Heizelements einseitig erwärmt werden. Zur Sicherstellung eines eindimensionalen Wärme- und Feuchtetransportes ist der Betonprüfkörper mit einer speziellen Glaskeramik und einer Hochtemperaturwolle ummantelt. Simultan zur Erwärmung werden eine Reihe röntgentomografischer Aufnahmen durchgeführt. Durch Differenzbildung aufeinanderfolgender Aufnahmen können Dichteveränderungen lokal und zeitlich werden, die Rückschlüsse auf Änderungen der Feuchteverteilung im Prüfkörper während der Erwärmung zulassen. Parallel dazu werden Untersuchungen mittels NMR-Relaxometrie (nuclear magnetic resonance) vor und nach der thermischen Beanspruchung durchgeführt. Die entwickelte Prüfmethodologie ermöglicht es, Veränderungen der Feuchteverteilung infolge thermischer Beanspruchung im Hochleistungsbeton von den Gelporen bis hin zu vorhandenen Verdichtungsporen abzubilden. Erste Ergebnisse zeigen, dass die gewählten Untersuchungsmethoden Veränderungen der Feuchteverteilung im Prüfkörper räumlich und zeitlich auflösen können. T2 - 5. DAfStb-Jahrestagung mit 58. Forschungskolloquium CY - Kaiserslautern, Germany DA - 20.09.2017 KW - Baustoffe KW - Abplatzen KW - Brand KW - Feuchtetransport KW - Hochleistungsbeton KW - Röntgen-3D-Computertomographie KW - NMR KW - ZfP PY - 2017 SN - 978-3-00-057267-8 VL - Band 1 SP - 162 EP - 173 AN - OPUS4-42565 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koch, Claudia T1 - Standardization in Emerging Technologies - The Case of Additive Manufacturing N2 - Additive Manufacturing provides an important enabling technology for the digital transformation of the economy. As an emerging technology it has seen a remarkable development over the last three decades. Nevertheless, it is far from a broad adoption with several barriers to overcome yet. One of the major challenges is the lack of standards. The critical role of standardization for innovation is generally recognized, still the topic too often has been neglected in strategic roadmapping exercises for emerging technologies. Too little is known about the complex dynamics and interrelations of standardization and innovation. The anticipation of standardization needs and the timely and efficient implementation of standards is challenging. This paper aims at contributing to a better understanding of the role that standards play in the multi-dimensional system of innovation. It analyzes the trajectories of innovation in Additive Manufacturing in a systematic and holistic way, focusing on standardization activities with regard to coordination, stakeholders involved, the timing and types of standards developed. Putting standardization in context of the multi-dimensional innovation system of Additive Manufacturing the research shows where standards can support the diffusion of an emerging technology. T2 - ITU Kaleidoscope Academic Conference: Challenges for a data-driven society CY - Nanjing, China DA - 27.11.2017 KW - Additive Manufacturing KW - Emerging technologies KW - Technological innovation KW - Standards KW - Standardization KW - 3D-Printing PY - 2017 SN - 978-92-61-24291-6 SN - 978-92-61-24281-7 SN - 978-92-61-24301-2 SP - 193 EP - 200 CY - Geneva AN - OPUS4-43501 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bartholmai, Matthias A1 - Johann, Sergej A1 - Strangfeld, Christoph ED - Chan, T. ED - Mahini, S, T1 - Embedded wireless sensor systems for long-term SHM and corrosion detection in concrete components N2 - State-of-the-art communication standards like RFID and Bluetooth Low Energy enable the development of sensor systems which can be completely embedded into concrete components for long-term SHM and early damage detection. Objective of the project KonSens which is carried out at BAM is the development, implementation, and validation of sensors for measuring of Parameters relevant for corrosion, like moisture, pH value, and electrical conductivity, inside steel reinforced concrete components. The primarily addressed application is detection and evaluation of corrosion processes in concrete bridges. In contrast to cable connected sensors, embedded wireless sensors avoid any pathways for intrusion of moisture and chemicals, e.g., chlorides which could trigger corrosion activity. To allow for long-term, ideally life-time operation, the once embedded sensor systems must work highly energy efficient. One option are passive RFID sensor systems, which work without battery. The energy is transmitted to the system through the electromagnetic field, even to operate sensors. A crucial parameter is the transmission depth in concrete. First experiments with RFID sensors working at frequencies of 13.56 MHz (HF) and 868 MHz (UHF) embedded in concrete specimen resulted positive for transmission depths of up to 13 cm, which is quite promising, considering that corrosion would appear first at the top level of rebars. A second generation of passive RFID sensor systems has been implemented with improved antenna design. Current experiments using these systems focus on the Transmission characteristics in terms of transmission depths and the impact of concrete moisture. Low-energy humidity sensors are used and analysed regarding their capability for measuring the material moisture. Additionally, a relation between transmitted power to the embedded sensor and the moisture content of the concrete specimen caused by energy absorption can be presumed and is under systematic investigation. T2 - International Conference on Structural Health Monitoring of Intelligent Infrastructure 2017 CY - Brisbane, Australia DA - 05.12.2017 KW - RFID sensors KW - Structural health monitoring KW - Sensors in concrete KW - Smart structures PY - 2017 SN - 978-1-925553-05-5 SP - 1 EP - 7 AN - OPUS4-43492 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Shamsuddoha, Md A1 - Hüsken, Götz A1 - Baeßler, Matthias A1 - Kühne, Hans-Carsten A1 - Thiele, Marc T1 - Critical factors affecting the capacity of cylindrical grouted connections in offshore energy structures N2 - Current trend suggests that global energy consumption will increase in the future. This growing energy demand and advancement of technology lead to explore all potential offshore fossil and non-fossil energy sources, necessitating erection of exploration and production structures, rigs, platforms and towers, which are susceptible to adverse environmental conditions along with their maintenances. Cylindrical grouted joints provide suitable connections between steel substructure and foundation in these offshore platforms and wind structures especially monopiles for ease of installation. However, these are composite connections with exterior sleeve, interior pile and infill grout. The capacity of these connections is affected by number of factors. The literature over last four decades by numerous researchers has shown the development of these connections with increasingly higher capacities and influences on these capacities due to various factors. This paper provides a comprehensive review on the factors affecting the connection capacity along with technical challenges for the future. Critical aspects and shortcomings of the current connection systems and potential solutions may be sought after for these issues are also discussed. T2 - 36th International Conference on Ocean, Offshore and Arctic Engineering CY - Trondheim, Norway DA - 25.06.2017 KW - Offshore wind energy KW - Grouted connection KW - Joint capacity KW - Shear keys PY - 2017 SN - 978-0-7918-5766-3 DO - https://doi.org/10.1115/OMAE2017-62510 VL - 3B SP - UNSP V03BT02A037, 1 EP - 10 AN - OPUS4-42387 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Strangfeld, Christoph A1 - Johann, Sergej A1 - Müller, Maximilian A1 - Bartholmai, Matthias T1 - Embedded passive RFID-based sensors for moisture monitoring in concrete N2 - Damages in infrastructure due to moisture amount to billions of Euros every year. For a more predictive structural health monitoring in civil engineering, the detection and monitoring of hazardous moisture in steel reinforced concrete constructions is of high interest. The sensors have to be wireless, elsewise they weaken the concrete cover of the rebars. The lifetime of such constructions is normally decades, thus the sensors have to be battery-free and fully passive. Considering these requirements, passive RFID-based sensors are developed. Communication and energy supply are realized wireless via the electromagnetic field of a RFID transmitter. The passive RFIDbased sensors are embedded into the concrete to enable the monitoring of moisture transport in porous materials. Results of the hydration process are shown. T2 - IEEE Sensors 2017 CY - Glasgow, Scotland, UK DA - 30.10.2017 KW - Embedded sensors KW - Wireless sensors KW - Passive sensors KW - RFID-based sensors KW - Structural health monitoring KW - Moisture PY - 2017 SN - 978-1-5386-4056-2 DO - https://doi.org/10.1109/ICSENS.2017.8234166 SP - 870 EP - 872 PB - IEEE AN - OPUS4-43033 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Shamsuddoha,, Md A1 - Hüsken, Götz A1 - Pirskawetz, Stephan A1 - Baeßler, Matthias A1 - Kühne, Hans-Carsten A1 - Thiele, Marc T1 - Remediation of Cracks Formed in Grouted Connections of Offshore Energy Structures under Static Loads N2 - The future energy demand necessitates the exploration of all potential energy sources both onshore and offshore. Global trend has shifted towards offshore energy, which can be obtained from either carbon intensive or renewable options, hence requiring structures such as rigs, platforms, and monopiles. Most of these structures adopt easily installable construction techniques, where lower foundation need to be connected with the super structure by mean of grouted composite joints. Generally, these composite connections have exterior sleeve, interior pile and infill grout. Being located in remote offshore conditions, connections can experience considerable adverse loading during their lifetimes. Degradations were reported inside similar connections, which were installed in last three decades. Besides, grouting in the offshore sites may often be proven difficult, which eventually leads to reduced capacity of connections in the long run. Thus, repair and rehabilitation of such connections should be planned ahead to minimize operational delays and costs in the future. This study aims at characterizing the nature of crack generation in grouted connections and thereby identifying the potential of repair using suitable repair material. Scaled grouted joints were manufactured using a novel mold, and connections were loaded under static load to visualize the main failure pattern. The failure mechanism and loading capacity are found compatible to previous results from earlier literature. Grouted connection was then repaired using cementitious injectable grout. The effectiveness of the repair system is also discussed. T2 - Twenty-eighth (2018) International Ocean and Polar Engineering Conference CY - Sapporo, Japan DA - 10.06.2018 KW - Offshore KW - Energy KW - Grouted Connection KW - Cracks KW - Repair KW - Rehabilitation PY - 2018 SP - 120 EP - 126 AN - OPUS4-45227 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Strangfeld, Christoph A1 - Maack, Stefan T1 - Verfahren und Vorrichtung zur Untersuchung einer Probe N2 - Ein Verfahren zur Untersuchung einer Probe (50) weist die Schritte des Anregens einer sich ausbreitenden mechanische Deformation (2) in der Probe (50) mittels eines fluidischen Oszillators (10), und des Bestimmens einer Charakteristik der mechanischen Deformation (2) auf. KW - Luftgekoppelter Ultraschall KW - Fluidischer Oszillator KW - Zerstörungsfreie Prüfung KW - Beton PY - 2018 SP - 1 EP - 23 CY - Berlin AN - OPUS4-44945 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Patrick P. A1 - Grotelüschen, Bjarne A1 - Bartholmai, Matthias A1 - Strangfeld, Christoph ED - Kossa, A. ED - Kiss, R. T1 - Towards Autonomous NDT Inspection: Setup and Validation of an Indoor Localization System N2 - Monitoring and maintenance of civil infrastructure are of great importance, as any undetected damage can cause high repair costs, unintended deadtime, or endanger structural integrity. The inspection of large concrete structures such as bridges and parking lots is particularly challenging and time-consuming. Traditional methods are mostly manual and involve mapping a grid of measurement lines to record the position of each measurement. Current semi-automated methods, on the other hand, use GPS or tachymeters for localization but still require trained personnel to operate. An entirely automated approach using mobile robots would be more cost- and time-efficient. While there have been developments in using GPS-enabled mobile robots for bridge inspection, the weak signal strength in indoor areas poses a challenge for the automated inspection of structures such as parking lots. This paper aims to develop a solution for the automated inspection of large indoor concrete structures by addressing the problem of robot localization in indoor spaces and the automated measurement of concrete cover and rebar detection. T2 - 39th Danubia-Adria Symposium on Advances in Experimental Mechanics CY - Siófok, Hungary DA - 26.09.2023 KW - NDT Inspection KW - Mobile Robot KW - Indoor Localization KW - Setup and Validation PY - 2023 SN - 978-963-421-927-9 SP - 88 EP - 89 PB - Hungarian Scientific Society of Mechanical Engineering (GTE) CY - Siófok, Hungary AN - OPUS4-58660 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kullolli, Borana A1 - Stutz, H. A1 - Bronsert, Jeffrey A1 - Dutto, Paola A1 - Baeßler, Matthias ED - Onate, E. ED - Owen, D. R. J. ED - Peric, D. ED - Chiumenti, M. T1 - A contact problem aplication for the local behaviour of soil pile interaction N2 - The purpose of the work presented in this paper is to analyze locally (at the element level) the contact behavior of a soil-pile contact problem. Therefore, a 2D shear test is modeled using the Finite Element Method. The formulation of a 4 nodded zero-thickness interface element of Beer is chosen with a linear interpolation function. Four constitutive contact models adapted for contact problems have been implemented. The Mohr-Coulomb and Clough and Duncan models were chosen initially, due to the ease of implementation and few number of parameters needed. After, more complicated models in the framework of elasto-plasticity such as: Lashkari and Mortara were implemented for the first time into the finite element code of the shear test problem. They include other phenomena such as: relative density of soil, the stress level and sand dilatancy. From the results the relation between shear displacement and shear stress has been deduced. Finally, a discussion of the advantages and the drawbacks during computation of each model is given at the end. T2 - Conference CY - Barcelona, Spain DA - 05.09.2017 KW - Soil-pile interaction KW - Numerical modelling PY - 2017 SN - 978-84-946909-6-9 SP - 490 EP - 501 PB - CIMNE CY - Barcelona,Spain AN - OPUS4-42960 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brecht, Katja A1 - Pistol, Klaus A1 - Klemmstein, Frank A1 - Rogge, Andreas T1 - Novel test setup for the quantification of the size effect in spalling tests N2 - Within a current research project which is funded by the German Research Foundation (DFG) the influence of the size and the geometry of specimens on the spalling result in fire tests is going to be investigated at Bundesanstalt für Materialforschung und -prüfung (BAM). This paper describes some preliminary results and a newly developed test setup. The novel setup enables the efficient and precise quantification of spalling by using a special photogrammetric measurement system. T2 - 5th International Workshop on Concrete Spalling CY - Boras, Sweden DA - 12.10.2017 KW - Size effect KW - Test setup KW - Photogrammetry PY - 2017 SN - 0284-5172 SP - 281 EP - 287 AN - OPUS4-42529 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Strangfeld, Christoph T1 - Moisture testing and mapping N2 - Discussion and presentation of different methods for moisture measurements in civil engineering. T2 - NDT&E Advanced Training Workshop CY - Berlin, Germany DA - 05.07.2017 KW - Building materials KW - Moisture measurements KW - Concrete PY - 2017 SP - 87 EP - 107 CY - Berlin, Germany AN - OPUS4-42624 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Wiggenhauser, Herbert A1 - Kind, Thomas A1 - Mielentz, Frank A1 - Strangfeld, Christoph A1 - Völker, Christoph A1 - Wilsch, Gerd T1 - Non-destructive testing in civil engineering at BAM N2 - Research and Development in Non-Destructive Testing in Civil Engineering at BAM has de-veloped over more than two decades. Highlights of present research are ultrasound phase array probes, ground penetrating radar applications for the assessment of existing structures and Laser Induced Breakdown Spec-troscopy (LIBS) to determine which chemical elements on the surface of a specimen are. RFID sensor devel-opments for wireless moisture monitoring and data fusion for the combined analysis of sensor data are fast developing areas. In addition, a selection of application cases is briefly described. T2 - Vortrag über die Aktivitäten des Fachbereichs 8.2 in der zerstörungsfreien Prüfung im Bauwesen. KW - Ultrasonic testing KW - RFID-sensors KW - Data fusion KW - Ground penetrating radar KW - LIBS PY - 2017 SP - 1 EP - 10 CY - Berlin AN - OPUS4-44132 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Viefhues, Eva A1 - Döhler, M. A1 - Hille, Falk A1 - Mevel, L. T1 - Stochastic subspace-based damage detection with uncertainty in the reference null space N2 - This paper deals with uncertainty considerations in damage diagnosis using the stochastic subspace-based damage detection technique. With this method, a model is estimated from data in a (healthy) reference state and confronted to measurement data from the possibly damaged state in a hypothesis test. Previously, only the uncertainty related to the measurement data was considered in this test, whereas the uncertainty in the estimation of the reference model has not been considered. We derive a new test framework, which takes into account both the uncertainties in the estimation of the reference model as well as the uncertainties related to the measurement data. Perturbation theory is applied to obtain the relevant covariances. In a numerical study the effect of the new computation is shown, when the reference model is estimated with different accuracies, and the performance of the hypothesis tests is evaluated for small damages. Using the derived covariance scheme increases the probability of detection when the reference model estimate is subject to high uncertainty, leading to a more reliable test. T2 - International Workshop on Structural Health Monitoring CY - Stanford, CA, USA DA - 12.09.2017 KW - Subspace-methods KW - Uncertainty KW - Damage detection PY - 2017 SN - 978-1-60595-330-4 SP - 1007 EP - 1014 AN - OPUS4-42731 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koch, Claudia ED - Jakobs, K. ED - O'Connor, R. V. T1 - Standardization for the Industrial Internet of Things: Engagement by China, Germany and the USA N2 - Standardization is a major challenge for a successful digital transformation of manufacturing. Industry and governments have put this topic on their agenda and stakeholders worldwide are engaged in various Standard Development Organizations, consortia and fora, seeking to shape the standards for the Industrial Internet of Things (IIoT). This paper for the first time analyzes how well participants from the USA, China and Germany are actually represented and engaged in standards development for the IIoT. Using quantitative metrics, the study specifically investigates standardization activities for Wireless Sensor Networks at the Internet Engineering Taskforce (IETF). The results are divergent: Measuring the authorships of IETF Internet-Drafts, China’s successful catch-up in international standardization is confirmed, having even outperformed the USA. When it comes to the authorship of the actual standards at IETF, China could not assert its top position. Here, US authors are leading, followed by German participants. The paper discusses different engagement patterns in depth and analyzes the national economic, institutional and political backgrounds that influence them. T2 - 23rd EURAS Annual Standardisation Conference "Standards for a Smarter Future" CY - Dublin, Irland DA - 13.06.2018 KW - Wireless Sensor Networks KW - IETF KW - Standards PY - 2018 SN - 978-3-95886-229-6 SP - 145 EP - 164 PB - Verlagshaus Mainz GmbH Aachen CY - Aachen AN - OPUS4-45496 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nicolai, Marcel A1 - Bulling, Jannis A1 - Lugovtsova, Yevgeniya A1 - Zeipert, Henning A1 - Prager, Jens A1 - Henning, Bernd ED - van Keulen, Wim ED - Kok, Jim T1 - On the repulsion effect of coupled Lamb wave modes N2 - Lamb waves, recognized for their significance in material characterisation, structural health monitor-ing, and non-destructive testing, exhibit complex behaviours that are crucial for industrial applica-tions. This paper delves into the mathematical and physical principals of the repulsion effect that can be observed in the dispersion curves of coupled Lamb wave modes. This effect is the result from the mechanical coupling of thin-walled solid plates and prevents the crossing of the dispersion curves. The study employs the Scaled Boundary Finite Element Method to calculate the dispersion curves of coupled plates and to simulate their interaction for a weak and ideal coupling. Through a mathemati-cal framework and a physical analogy with simple harmonic oscillators, the paper elucidates the un-derlying principals of this effect. Furthermore, the paper highlights the practical significance of the repulsion effect in Lamb waves, suggesting its application for testing and monitoring the integrity of multi-layer structures like adhesive bonds, which are important for various industrial applications. A deepened understanding of this effect could contribute to the enhancement of non-destructive evalua-tion techniques. T2 - ICSV 2024 CY - Amsterdam, The Netherlands DA - 08.07.2024 KW - Scaled Boundary Finite Element Method (SBFEM) KW - Lamb waves KW - Mode repulsion KW - Mechanical coupling KW - Dispersion curves PY - 2024 SN - 978-90-90-39058-1 SN - 2329-3675 SP - 410 EP - 418 PB - The International Institute of Acoustics and Vibration (IIAV) CY - Amsterdam AN - OPUS4-62855 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nicolai, Marcel A1 - Bulling, Jannis A1 - Lugovtsova, Yevgeniya A1 - Zeipert, Henning A1 - Prager, Jens A1 - Henning, Bernd T1 - On the repulsion effect of coupled Lamb wave modes N2 - This work investigates the phenomenon of mode repulsion in coupled Lamb wave systems. By mechanically coupling two dissimilar plates using spring elements, it is shown that previously intersecting Lamb wave modes are repelled, avoiding any crossing in the dispersion curves. The effect, rooted in eigenvalue theory and first observed in quantum systems, is explained through both mathematical models and classical analogies with coupled harmonic oscillators. Numerical simulations using the Scaled Boundary Finite Element Method validate the theoretical predictions, revealing a correlation between strain distribution and frequency splitting. The observed mode repulsion provides new insights into interface properties and offers potential for applications such as monitoring adhesive degradation in layered structures. T2 - DAGA 2024 CY - Hannover, Germany DA - 18.03.2024 KW - Scaled Boundary Finite Element Method (SBFEM) KW - Lamb waves KW - Mode repulsion KW - Mechanical coupling KW - Dispersion curves PY - 2024 SP - 632 EP - 635 AN - OPUS4-62854 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kühnel, Alena A1 - Stelzner, Ludwig A1 - Weise, Frank T1 - Measurement and analysis of concrete pavement surface textures using hand-held 3D laser scanning technology N2 - Concrete pavement surface textures are divided by means of their dimension into four categories: microtexture, macrotexture, megatexture and roughness. They influence the most important performance characteristics of road surfaces, such as friction (also referred to as “skid resistance”), tire/pavement noise, evenness and surface drainage. These properties are relevant for driving safety, comfort and environmental aspects. Up to now, research in Germany has focused on monitoring these characteristics by tire/pavement noise and skid resistance measurements. However, the topography of surface textures has not been sufficiently investigated and evaluated until now. The development and availability of high-performance, hand-held 3D scanning systems during the last years enable measurements of the microtexture and macrotexture of concrete pavement surfaces at short measuring times and high resolution. This paper shows the ability of modern laser-based technology to record three-dimensional data of different concrete pavement surface textures in situ. For this purpose, a special measuring frame has been developed. The presented results were primarily obtained within the framework of a research project commissioned by the German Federal Highway Research Institute (BASt) and processed by the Federal Institute for Materials Research and Testing. Various concrete pavement surface textures by means of diamond grinding and hybrid of diamond grinding and grooving were investigated in situ. In addition, exposed aggregate concretes (EAC), which were introduced as a standard type of concrete for motorway pavements in Germany in 2006, have been analyzed. Based on the gathered 3D data, evaluation routines for qualitative and quantitative analysis have been developed and applied. The aim was to derive the statistical parameters such as the relative and cumulative frequency distribution of the profile depth as well as the roughness coefficient for diamond ground pavements and EAC. Also, the “mean profile depth” (MPD) as a common texture-related parameter was determined. T2 - 14th International Symposium on Concrete Roads CY - Krakow, Poland DA - 25.06.2023 KW - Concrete pavement surface textures KW - 3D Laser Scanning KW - Diamond Grinding KW - Exposed aggregate concrete KW - Data analysis KW - Surface characteristics PY - 2023 SP - 1 EP - 14 AN - OPUS4-57893 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - von Werder, Julia A1 - Simon, Sebastian A1 - Meng, Birgit T1 - Internal sulfate resistance of concrete N2 - If the amount of sulfate within the mix design for concrete is not balanced, ettringite formation which first controls solidification continues while the concrete is hardening. Ettringite forms by reaction of sulfate contained in the cement or in some admixture with calcium aluminate (C3A) as cement component. The “late primary ettringite formation” promotes an increase in volume within the hardened concrete leading to cracks. To analyze the effect of substituting part of ordinary Portland cement (OPC) by a treated brown coal fly ash mortar bars were tested according to ASTM C452. This test method was originally developed to extrapolate from the internal to external sulfate attack and is based on the idea that by testing a concrete mixture containing sulfate the process of deterioration is accelerated because it does not have to diffuse into the concrete before reaction first. In addition to the samples prescribed in ASTM C452 further samples in the size of the German SVA procedure were tested also designed for accessing the external sulfate resistance. The results show that while the replacement of 25 % of cement by brown coal fly ash leads to length changes around the limit defined by ASTM, the substitution of 50 % cement exceeded the limit by a multiple. The progress of expansion is the very similar for the two geometries tested. In-situ XRD measurements confirmed that while for pastes made of OPC the formation of ettringite is completed after 20 hours, this is not true for the mixtures containing the brown coal fly ash. In a different study the effect of hydrothermal treatment on the phase composition of ultra-high-performance concrete was analyzed. The results show that the sulfate and aluminate resulting from the decomposition of ettringite are bound into new phases. If this binding is permanent this might allow the larger use of sulfate bearing raw materials. T2 - EuroCoalAsh 2021 Conference CY - Online meeting DA - 02.11.2021 KW - Brown coal fly ash KW - Ettringite KW - Internal sulfate resistance KW - Test methods KW - In-situ XRD KW - Hydrothermal treatment PY - 2021 SP - 131 EP - 137 CY - Thessaloniki AN - OPUS4-54133 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Giese, Marcel T1 - Experimentelle Charakterisierung der WIG-Schweißeignung einer Hoch- und Mediumentropie-Legierung N2 - Equiatomic multi-element systems with defined entropy are a relatively new mate-rial concept for alloy production. These alloys consist of at least five elements in equiatomic distribution in the case of high entropy alloys (HEA) and three to four elements in equiatomic distribution in the case of medium entropy alloys (MEA). Previous studies on these alloys have focused primarily on their production, micro-structure and the resulting material properties. Meanwhile, the focus here is on the processing of the alloys and their influence on future applications. Up to now, there has been insufficient knowledge of the materials and processes involved in weld-ing. In this work, therefore, the weldability of a CoCrFeMnNi-HEA and a CoCrNi-MEA by means of a TIG welding process was investigated as a basic system. To this end, the welding parameters were first determined on a reference alloy (Ni-based: 2.4858) and transferred to the welding of the CoCrFeMnNi-HEA and CoCrNi-MEA. Weldability was assessed by testing the absence of defects and microstructures obtained. The weld metal exhibited the dendritic microstructure typical of TIG, with microsegregations forming as interdendritic phases. Increased hardness was de-tected in the weld metal compared to the base metal. In the heat-affected zone, there was little grain growth and, in both alloys, the formation of hot cracks after welding. The cause of the cracks was to be found in the specimen preparation, which had an influence on the subsequent processing. After elimination of this in-fluence, no welding process-related imperfections were found in the CoCrFeMnNi-HEA and CoCrNi-MEA. In summary, both materials show good fusion weldability by TIG welding. The re-sults of this work thus contribute to the understanding of the weldability of HEA and in particular for CoCrNi-MEA, which was considered in this depth for the first time. KW - WIG-Schweißen KW - Hochentropielegierung KW - Mediumentropielegierung PY - 2021 SP - 1 EP - 79 CY - Otto von Guericke Universität AN - OPUS4-53644 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kühne, Hans-Carsten T1 - Technische Umsetzung und Verwendung der DIN EN 1504-3 für Instandsetzungsmörtel und -betone in Deutschland? KW - Betoninstandsetzung KW - DIN EN 1504 KW - Instandsetzungsmörtel PY - 2010 N1 - Serientitel: Heftreihe Deutscher Beton- und Bautechnik-Verein e.V. – Series title: Heftreihe Deutscher Beton- und Bautechnik-Verein e.V. IS - 19 SP - 35 EP - 49 AN - OPUS4-22315 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Recknagel, Christoph T1 - Strukturanalyse von offenporigen Asphalten KW - Moderne Fahrbahnbeläge KW - Strukturaufklärung KW - Phasendifferenzierung KW - Bildgebende Auswertung KW - Modellierung KW - Asphaltforschung PY - 2010 IS - Kap. 4.3 SP - 226 EP - 258 AN - OPUS4-22940 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jakubcová, Petra A1 - Ramge, Peter A1 - Rübner, Katrin T1 - New lightweight aggregates from heterogeneous construction and demolition waste for the use in lightweight concrete N2 - Concrete containing lightweight aggregates has been known since ancient times. To reduce weight, natural aggregates of volcanic origin, such as crushed lava or pumice, were used in construction purposes, for example for the Pyramids during the Mayan period in Mexico or for monumental structures in the Roman Empire. The most famous examples of this first application of lightweight aggregate concrete (LWAC) in Europe are certainly the Colosseum and the Pantheon. The Roman constructors used natural as well as artificial aggregates, such as pumice, crushed lava and crushed brick, to realise lightweight concrete applications in parts of these buildings. Still today, pumice is used in Germany, Italy, Japan and Iceland as aggregate for structural lightweight concrete. T2 - European coatings congress CY - Nuremberg, Germany DA - 28.03.2011 KW - Sekundärrohstoffe KW - Sekundäre Gesteinskörnung KW - Recycling KW - Leichtbeton PY - 2011 SP - 1 EP - 8 AN - OPUS4-23674 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Robens, E. A1 - Rübner, Katrin T1 - Gravimetrische Wasserdampfsorptions- und Feuchtemessung an Feststoffen - Eine Übersicht über Messverfahren und Normung T2 - 6. Workshop über die Charakterisierung von Feinteiligen und Porösen Festkörpern CY - Bad Soden, Deutschland DA - 2002-11-14 PY - 2002 VL - 6 SP - 1(?) EP - 2(?) CY - Bad Soden AN - OPUS4-1992 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rübner, Katrin A1 - Rübner, J. A1 - Knölle, G. T1 - Porenstruktur von Polyurethan/Kieselsäure-Nanocompositen T2 - 6. Workshop über die Charakterisierung von Feinteiligen und Porösen Festkörpern CY - Bad Soden, Deutschland DA - 2002-11-14 PY - 2002 VL - 6 SP - 1(?) EP - 2(?) CY - Bad Soden AN - OPUS4-1991 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weise, Frank A1 - Schaurich, Dieter T1 - Long-Term Investigations on Drying out of the Main Cornice of the Berlin Zeughaus T2 - 11. Bauklimatisches Symposium ; 11th Symposium of Building Physics CY - Dresden, Germany DA - 2002-09-26 PY - 2002 SP - 722 EP - 737 PB - TU CY - Dresden AN - OPUS4-1839 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Recknagel, Christoph T1 - Performance - related testing of asphaltic plug joints in Germany T2 - Internationales Symposium "Flexible binder in road and bridge building" CY - Crawley, England, GB DA - 2000-11-06 PY - 2000 AN - OPUS4-1043 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Recknagel, Christoph T1 - Quality Improvement of Expansion Joint Systems by Performance Related Tests of System Behaviour PY - 2002 IS - 21 SP - 5 PB - BRE CY - Garston AN - OPUS4-2303 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weise, Frank A1 - Patitz, G. A1 - Redmer, Bernhard A1 - Hübner, M. A1 - Maier, Bärbel A1 - Ewert, Uwe T1 - Kombination zerstörungsfreier Prüfverfahren zur Strukturaufklärung beim Säulenjoch der Heiligen Halle am Markt von Priene KW - Baudenkmäler KW - Strukturaufklärung KW - Zerstörungsfreie Prüfung KW - Videoskopie KW - Radar KW - Radiografie PY - 2004 VL - 2 SP - 97 EP - 116 PB - Wissenschaftlich-Technische Arbeitsgemeinschaft für Bauwerkserhaltung und Denkmalpflege CY - München AN - OPUS4-4819 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weise, Frank A1 - Pirskawetz, Stephan A1 - Müller, Urs A1 - Meng, Birgit T1 - Charakterisierung der Schädigungsprozesse in Betonen mit innovativen Prüftechniken KW - Beton KW - Naturstein KW - Schadensanalyse KW - Innovative Prüftechnik PY - 2007 IS - 13 SP - 14 EP - 20 AN - OPUS4-15715 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weise, Frank T1 - Feuchtemessung im Beton - eine Gegenüberstellung gängiger Verfahren KW - Zerstörungsfreie Prüftechnik KW - Bauwesen PY - 2008 VL - 2 SP - 60 EP - 68 PB - Ernst & Sohn CY - Berlin AN - OPUS4-17366 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quell, P. A1 - Knops, M. A1 - Heinicke, M. A1 - Rettenmeier, A. A1 - Kühn, M. A1 - Rücker, Werner A1 - Baeßler, Matthias A1 - Rolfes, R. A1 - Haake, G. A1 - Hahn, B. A1 - Benesch, M. A1 - van Radecke, H. A1 - Finger, K. A1 - Neumann, T. A1 - Herklotz, K. T1 - Offshore Wind Energy Research in Germany - RAVE - Research at Alpha VEntus N2 - To start the large-scale deployment of offshore wind in German waters, the German Federal Ministry for the Environment (BMU) supports the offshore test site "alpha ventus" in the North Sea with a research budget of about 50 million Euro in the next years. The overall objective of the research is to reduce the costs of offshore wind energy deployment in deep water. In order to provide all participating research projects with detailed data, the test site will be equipped with extensive measurement instrumentation. This research initiative was named RAVE – Research at Alpha VEntus – and consists of a variety of projects in connection with the installation and operation of alpha ventus. As part of the RAVE initiative, so far the participating institutes and companies have prepared projects on the following topics: • Realization of the joint measurements and data management • Analysis of loads, modelling and further development of the different components of offshore wind turbines • Loads at offshore foundations and structures • Further development of LIDAR wind measuring techniques • Grid integration of offshore wind energy • Monitoring of the offshore wind energy deployment in Germany – "Offshore WMEP" • Measurement of the operating noises and modelling of the sound propagation between tower and water • Ecologic research T2 - European Offshore Wind 2007 Conference & Exhibition CY - Berlin, Germany DA - 2007-12-04 KW - Offshore Wind Energy KW - Rave KW - Foundations PY - 2007 SP - 1 EP - 10 AN - OPUS4-17976 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reuter, T. A1 - Borges de Oliveira, F. A1 - Abt, Ch. A1 - Ballach, F. A1 - Bartscher, M. A1 - Bellon, Carsten A1 - Dennerlein, F. A1 - Fuchs, P. A1 - Günnewig, O. A1 - Hausotte, T. A1 - Hess, J. A1 - Kasperl, S. A1 - Maass, N. A1 - Kimmig, W. A1 - Schielein, R. A1 - von Schmid, M. A1 - Suppes, A. A1 - Wagner, G. A1 - Watzl, Ch. A1 - Wohlgemuth, F. T1 - Introduction to “Realistic Simulation of real CT systems with a basic-qualified Simulation Software - CTSimU2“ N2 - The lack of traceability to meter of X-ray Computed Tomography (CT) measurements still hinders a more extensive acceptance of CT in coordinate metrology and industry. To ensure traceable, reliable, and accurate measurements, the determination of the task-specific measurement uncertainty is necessary. The German guideline VDI/VDE 2630 part 2.1 describes a procedure to determine the measurement uncertainty for CT experimentally by conducting several repeated measurements with a calibrated test specimen. However, this experimental procedure is cost and effort intensive. Therefore, the simulation of dimensional measurement tasks conducted with X-ray computed tomography can close these drawbacks. Additionally, recent developments towards a resource and cost-efficient production (“smart factory”) motivate the need for a corresponding numerical model of a CT system (“digital twin”) as well. As there is no standardized procedure to determine the measurement uncertainty of a CT system by simulation at the moment, the project series CTSimU was initiated, aiming at this gap. Concretely, the goal is the development of a procedure to determine the measurement uncertainty numerically by radiographic simulation. The first project (2019-2022), "Radiographic Computed Tomography Simulation for Measurement Uncertainty Evaluation - CTSimU" developed a framework to qualify a radiographic simulation software concerning the correct simulation of physical laws and functionalities. The most important outcome was a draft for a new guideline VDI/VDE 2630 part 2.2, which is currently under discussion in the VDI/VDE committee. The follow-up project CTSimU2 "Realistic Simulation of real CT systems with a basic-qualified Simulation Software" will deal with building and characterizing a digital replica of a specific real-world CT system. The two main targets of this project will be a toolbox including methods and procedures to configure a realistic CT system simulation and to develop tests to check if this replica is sufficient enough. The result will be a draft for a follow-up VDI/VDE guideline proposing standardized procedures to determine a CT system's corresponding characteristics and test the simulation (copy) of a real-world CT system which we call a "digital twin". T2 - 12th Conference on Industrial Computed Tomography (iCT) 2023 CY - Fürth, Germany DA - 27.02.2023 KW - dXCT KW - X-ray computed tomography KW - Simulation PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-589204 DO - https://doi.org/10.58286/27715 VL - 28 IS - 3 SP - 1 EP - 5 PB - NDT.net AN - OPUS4-58920 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rogge, Andreas T1 - Vorbeugender Brandschutz in Tunnelbauwerken T2 - Deutscher Bautechnik-Tag CY - Hamburg, Germany DA - 2013-04-11 PY - 2013 N1 - Serientitel: DBV-Hefte – Series title: DBV-Hefte IS - 21 SP - 157 EP - 158 AN - OPUS4-28289 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thiele, Marc ED - Breitenbücher, R. ED - Mark, P. T1 - Experimentelle Untersuchung der Schädigungsevolution in Beton unter Ermüdungsbeanspruchung N2 - Im vorliegenden Beitrag werden einige Ergebnisse von Ermüdungsversuchen an Betonprobekörpern vorgestellt, die in den letzten Jahren an der BAM Bundesanstalt für Materialforschung und -prüfung in Zusammenarbeit mit dem Fachgebiet Statik und Dynamik der TU Berlin durchgeführt wurden. Dabei wurde der Fokus auf die Untersuchung des Ermüdungsprozesses an sich und seine Ursachen gelegt. Aufbauend auf diesen Erkenntnissen wird ein Modell entwickelt, welches das beobachtete Materialverhalten realitätsnah abbilden kann, sich derzeit aber noch in der Entwicklung befindet. T2 - 1. DAfStb-Jahrestagung mit 54. Forschungskolloquium CY - Bochum, Germany DA - 07.11.2013 KW - Beton KW - Ermüdung KW - Schädigung PY - 2013 SP - 423 EP - 428 PB - Ruhr-Universität Bochum CY - Berlin AN - OPUS4-29522 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weise, Frank T1 - Verfahren der Feuchtemessung an Betonbauteilen - Ein Überblick mit Anwendungsgrenzen N2 - Die Überprüfung der Dichtheit von Betonkonstruktionen (z.B. "Weiße Wannen") erfordert den Einsatz geeigneter Feuchtemessverfahren. Darüber hinaus ermöglicht die Kenntnis der Feuchtesituation in Betonbauteilen auch eine Abschätzung des Schädigungspotentials. So gilt es beispielsweise bei potentiell frostinduzierten Schädigungsprozessen zu untersuchen, ob im Beton der kritische Feuchtegehalt erreicht wurde. Zusätzlich gestattet eine differenzierte Ermittlung der Bindungszustände des Wassers im Beton auch Aussagen zum Hydratationsfortschritt. Aus den vorstehend genannten Gründen kommt der Feuchtemessung im Beton am Bauwerk und im Labor eine große Bedeutung zu. Zur Lösung dieses Prüfproblems werden zahlreiche Messverfahren auf dem Markt angeboten. Weiterhin befinden sich verschiedenste Messsysteme in der Entwicklung bzw. Erprobung. Aufgrund der Vielfalt der Feuchtemessverfahren ist es für den Anwender oft schwierig, das geeignete Prüfverfahren zur Lösung seines speziellen Problems auszuwählen. So stehen neben den klassischen direkten Methoden auch vielfältige mehr oder minder moderne zerstörungsfrei bzw. zerstörungsarm arbeitende indirekte Messverfahren zur Verfügung. Nachfolgend wird basierend auf dem vom Verfasser in ausführlich dargestellten Sachstand ein allgemeiner Überblick über die Arten und die Leistungsfähigkeit der existierenden Feuchtemessverfahren in gestraffter Form gegeben. Dabei wird auf die speziellen Aspekte der Feuchtemessung in Betonen eingegangen. T2 - Fachtagung 'Weiße Wannen - Wasserundurchlässige Konstruktionen aus Beton' CY - Berlin, Germany DA - 05.11.2013 KW - Frost KW - Frost-Tausalz KW - Alkalikieselsäure-Reaktion KW - Photogrammetrie KW - Röntgen 3D-CT KW - Schallemissionsanalyse KW - Ultraschallprüfung KW - Dehnungsmessung PY - 2013 SP - 87 EP - 105 PB - BetonMarketing Nordost CY - Berlin AN - OPUS4-30046 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Herbst, Tristan A1 - Rübner, Katrin T1 - Nanoskaliger Kieselsäureschlamm - Technologieentwicklungen zur Verwertung in mineralischen Baustoffen mit dem Ziel der Verbesserung der Werkstoffeigenschaften, Teilprojekt: Stoffcharakterisierung, hydraulische Bindemittel und NJachhaltigkeits- und Wirtschaftlichkeitsbetrachtungen KW - Kieselsäuren KW - Reststoff KW - Nanopartikel KW - Recycling KW - Mineralischer Baustoff PY - 2012 SP - 1 EP - 36 CY - Berlin AN - OPUS4-30065 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Döhler, Michael A1 - Mevel, L. A1 - Hille, Falk T1 - Efficient computation of minmax tests for fault isolation and their application to structural damage localization N2 - Fault detection and isolation can be handled by many different approaches. This paper builds upon a hypothesis test that checks whether the mean of a Gaussian random vector has become non-zero in the faulty state, based on a chi2 test. For fault isolation, it has to be decided which components in the parameter set of the Gaussian vector have changed, which is done by variants of the chi2 hypothesis test using the so-called sensitivity and minmax approaches. While only the sensitivity of the tested parameter component is taken into account in the sensitivity approach, the sensitivities of all parameters are used in the minmax approach, leading to better statistical properties at the expense of an increased computational burden. The computation of the respective test variable in the minmax test is cumbersome and may be ill-conditioned especially for large parameter sets, asking hence for a careful numerical evaluation. Furthermore, the fault isolation procedure requires the repetitive calculation of the test variable for each of the parameter components that are tested for a change, which may be a significant computational burden. In this paper, dealing with the minmax problem, we propose a new efficient computation for the test variables, which is based on a simultaneous QR decomposition for all parameters. Based on this scheme, we propose an efficient test computation for a large parameter set, leading to a decrease in the numerical complexity by one order of magnitude in the total number of parameters. Finally, we show how the minmax test is useful for structural damage localization, where an asymptotically Gaussian residual vector is computed from output-only vibration data of a mechanical or a civil structure. T2 - 19th World congress of the international federation of automatic control CY - Cape Town, South Africa DA - 24.08.2014 KW - Fault isolation KW - Residual evaluation KW - Statistical tests KW - Numerical computation KW - Mechanical systems PY - 2014 SP - 7382 EP - 7387 PB - IFAC AN - OPUS4-31573 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Recknagel, Christoph A1 - Staude, Andreas T1 - Leiser Straßenverkehr - Leise Straßenbeläge KW - Infrastruktur KW - Strukturaufklärung KW - Leise Fahrbahnbeläge PY - 2014 UR - http://www.strassenforschung.de/ SP - 1 EP - 44(?) AN - OPUS4-31452 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reuter, T. A1 - Wohlgemuth, F. A1 - Bellon, Carsten A1 - Hausotte, T. T1 - Measurement-based Detector Characteristics for Digital Twins in aRTist 2 N2 - Various software products for the simulation of industrial X-ray radiography have been developed in recent years (e.g., aRTist 2, CIVA CT, Scorpius XLab, SimCT, Wilcore) and their application potential has been shown in numerous works. However, full systematic approaches to characterise a specific CT system for these simulation software products to obtain a truthful digital twin are still missing. In this contribution, we want to present two approaches to obtain realistic grey values in X-ray projections in aRTist 2 simulations based on measured projections. In aRTist 2, the displayed grey value of a pixel is based on the energy density incident on that pixel. The energy density is calculated based on the X-ray tube spectrum, the attenuation between source and detector as well as an energy-dependent sensitivity curve of the detector. The first approach presented in this contribution uses the sensitivity curve as a free modelling parameter. We measured the signal response at different thicknesses of Al EN-AW6082 at different tube voltages (i.e., different tube spectra). We then regarded the grey values displayed by these projections as a data regression respectively an optimisation problem and obtained the sensitivity curve that is best able to reproduce the measured behaviour in aRTist 2. The resulting sensitivity curve does not necessarily hold physical meaning but is able to simulate the real system behaviour in the simulation software. The second approach presented in this contribution is to estimate the sensitivity curve based on assumptions about the characteristics of the scintillation detector (e.g., scintillator material, scintillator thickness and signal processing characteristics). For this approach, a linear response function (linear relationship between the deposited energy per pixel and the resulting grey value) is assumed. If the detector characteristics, which affect the simulated deposited energy, are properly modelled, the slope and offset of the response function to match the measured grey values should be the same for different tube spectra. As the offset is constant and given by the grey values measured at no incident radiation, the slope is the remaining parameter to evaluate the success of the detector modelling. We therefore adapted the detector characteristics by changing the detector setup until the slope was nearly the same for all measured tube spectra. We are aware that the resulting parameters of the scintillator material and thickness might not be the real ones, but with those modelling parameters we are able to simulate realistic grey values in aRTist 2. Both of those approaches could potentially be a step forward to a full systematic approach for a digital twin of a real CT system in aRTist 2. T2 - 20th World Conference on Non-Destructive Testing (WCNDT 2024) CY - Incheon, South Korea DA - 27.05.2024 KW - Digital Twin KW - Computed Tomography KW - Simulation PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-602046 DO - https://doi.org/10.58286/29910 SP - 1 EP - 10 PB - NDT.net CY - Mayen, Germany AN - OPUS4-60204 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kaatz, Rico A1 - Recknagel, Christoph T1 - Advanced evaluation of structural sealant glazing systems by a new system test approach N2 - More Information about the capability and especially about the dnrabi 1 ity of Structural Sealant Glazing (SSG) Systems are needed. To make a contribution to questions unanswered a suitable System evaluation test is necessary. The Basis for such a test is a load function, vvhich accounts for the decisive loads SSG Systems are exposed to during their working life. This paper proposes a general load function for Standard SSG Systems at central German locations for accelerated durability tests. Decisive loads are determined and different SSG construction types defmed. The performance of these SSG Systems under exposure to externa! loads and to a dynamic pendulum impact is investigated via finite element analyses using a hyperelastic material niodel. The external loads are applied separately and superimposed. Compression, tensile and shear deformations of the sealant are determined. It is found that the sealant is subjected to normal and shear stresses simultaneously. The requirements for a representative specimen are derived. The results will be taken as basics for the development and the construction of a test facility to evaluate the durability of Structural Sealant Glazing Systems. T2 - ICBEST 2014 CY - Aachen, Germany DA - 09.06.2014 PY - 2014 SP - 1 EP - 19 AN - OPUS4-30946 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hille, Falk A1 - Petryna, Y. A1 - Rücker, Werner T1 - Subspace-based detection of fatigue damage on jacket support structures of offshore wind turbines N2 - The paper describes the application of the Stochastic Subspace-based Damage Detection (SSDD) method on model structures for an utilization of this approach on offshore wind turbine structures. Aim of the study was therefore to analyze the usability and efficiency of the detection method as well as to determine an optimized set of parameter for realistic damage on support structures of wind energy turbines. Based on results of an experimental fatigue test on a Steel frame laboratory structure a strategy for a numerical verification of the experimentally evolved damage detection was developed, utilizing a time integration approach to simulate the dynamic response. In a second Step the identified modeling and computing methodology is used to numerically investigate the ability to detect damage in real size structural components of offshore wind turbines. T2 - EWSHM 2014 - 7th European workshop on structural health monitoring CY - Nantes, France DA - 08.07.2014 KW - Damage detection KW - Offshore wind turbines KW - Numerical response PY - 2014 SP - 229 EP - 236 AN - OPUS4-31218 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baeßler, Matthias A1 - Hille, Falk ED - Powers, N. ED - Frangopol, D. T1 - A study on diverse strategies for discriminating environmental from damage based variations in monitoring data N2 - Right from the beginning of applying SHM to bridge structures it was obvious that environmental based perturbations on the measurement significantly influence the ability to identify structural damage. Strategies are needed to classify such effects and consider them appropriately in SHM. Various methods have been developed and analyzed to separate environmental based effects from damage induced changes in the measures. Generally, two main approaches have emerged from research activity in this fields: (a) statistics based tools analyzing patterns in the data or in computed parameters and (b) methods, utilizing the structural model of the bridge taking into account environmental as well as damage based changes of stiffness values. With the back-ground of increasing affordability of sensing and computing technology, effort should be made to increase sensitivity, reliability and robustness of procedures, separating environmental from damage caused changes in SHM measures. The contribution describes both general strategies and points out their Advantages and drawbacks. As basis, a review on relevant methods was conducted. The aim of the study is to classify approaches for separating damage describing information from environmental based perturbations in dependency of the SHM objective. And such, it is intended to describe a best practice in designing concepts for Monitoring infrastructure, naturally effected by environmental influences. T2 - IABMAS CY - Melbourne, Australia DA - 09.07.2018 KW - SHM KW - Environmental changes KW - temperature PY - 2018 SN - 978-1-138-73045-8 SP - 1557 EP - 1564 PB - CRC Press AN - OPUS4-46059 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schnell, A. A1 - Rübner, Katrin A1 - Ihlenfeldt, Toni A1 - Vöge, M. A1 - Ludwig, H.-M. ED - Ludwig, H.-M. T1 - Leichtbetone mit Recycling-Granulaten aus Mauerwerkbruch-Ton-Mischungen N2 - Mineralische Bauabfälle stellen in den Industrienationen den größten Abfallstrom dar. Allein in Deutschland fallen jährlich mehr als 50 Mio. Tonnen Bauschutt an, der hauptsächlich aus Beton- und Mauerwerkbruch besteht. Dabei nehmen die Verwertungs- und Recyclingquoten bei den bereits etablierten herkömmlichen Einsatzgebieten für aufbereitete Bau- und Abbruchabfälle mit zunehmender Heterogenität des Materials ab. Ein höherwertiges Recycling mit dem Ziel das aufbereitete Material in hochwertigen Betonprodukten einzusetzen erfolgt heute in Deutschland lediglich im Rahmen von Pilotprojekten. So können die groben Körnungen des Betonbruchs als rezyklierte Gesteinskörnung im Beton eingesetzt werden. Besonders eingeschränkte Verwertungsmöglichkeiten liegen für Mauerwerkbruch vor, einem Gemisch aus Beton, Ziegel, Kalksandstein, Porenbeton, Mörtel, Natursteinen und anderen mineralischen Bestandteilen. Die Ursache hierfür ist neben der heterogenen Zusammensetzung des Materials auch dessen feine Kornverteilung, die durch den bei der mechanischen Aufbereitung zwangsläufig anfallenden Feinkornanteil von 30 bis über 40 Prozentbedingt ist. Defizite in der Verwertung bestehen also besonders bei heterogenen feinkörnigen Gemischen. Hier müssen Ansätze gefunden werden, um eine hochwertige Wiederverwertung zu ermöglichen. Dafür ist eine möglichst gute Trennung der einzelnen Materialfraktionen ein bewährter Ansatz. Während Metalle mittels Band- und Wirbelstromabscheidern und leichte Fremdbestandteile über Windsichtung und Dichtesortierung ausgetragen werden können, ist eine Trennung der Materialien Ziegel, Mörtel und Beton, insbesondere für die feinen Fraktionen, derzeit technologisch und wirtschaftlich nicht umsetzbar. Ein rohstoffliches Recycling dieser heterogen zusammengesetzten Abfälle unter Nutzung ihrer chemisch-mineralogischen Zusammensetzung ohne eine vorherige Trennung in die einzelnen Materialfraktionen bietet sich als Alternative an. Ergebnisse zur Herstellung von Leichtgranulaten aus Mauerwerkbruch und Tonen in einem thermischen Prozess ähnlich der Blähtonherstellung wurden bereits mehrfach veröffentlicht. Diese Recycling-Granulate (RCG) sollen unter anderem als leichte Gesteinskörnung für Betone verwendet werden. Gegenstand dieses Beitrags sind Ergebnisse aus dem Verbundforschungsprojekt „RC-Leichtgranulate“ zum Einsatz der RCG in Leichtbeton. T2 - ibausil 2018 - 20. Internationale Baustofftagung CY - Weimar, Germany DA - 12.09.2918 KW - Recycling KW - Mauerwerkbruch KW - Leichte Gesteinskörnungen KW - Recyclinggranulat KW - Leichtbeton KW - Ton PY - 2018 SN - 978-3-00-059950-7 VL - 2 SP - 2-381 EP - 2-388 PB - F.A. Finger-Institut für Baustoffkunde CY - Weimar AN - OPUS4-46697 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Jansen, D. A1 - Bald, S. A1 - Birbaum, J. A1 - Küttenbaum, Stefan A1 - Krause, J. A1 - Maack, Stefan A1 - Pichottka, S. A1 - Scherkenbach, M. A1 - Strangfeld, Christoph A1 - Villaret, K. A1 - Wöllenstein, J. T1 - Sensorik zur Substanzbewertung von Straßen N2 - Das vorliegende Arbeitspapier stellt den Stand des Wissens und der Forschung zum Einsatz von Sensorik in Straßenbefestigungen zur Erfassung von Eingangsgrößen und Merkmalen für die Substanzbewertung zusammenfassend dar. Unter Sensorik versteht dieses Arbeitspapier ganz allgemein technische Einrichtungen, mit denen man die Werte von physikalischen Größen erfassen und zur Interpretation darstellen kann. KW - Sensorik KW - Beton KW - Asphalt KW - Messkette KW - Zustandsbewertung PY - 2022 SN - 978-3-86446-314-3 SP - 1 EP - 28 PB - Forschungsgemeinschaft für Straßen- und Verkehrswesen e.V. CY - Köln AN - OPUS4-54530 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - van Beek, F. A1 - Kuijper, P. A1 - Voskuilen, J. A1 - Hean, S. A1 - Recknagel, Christoph A1 - Mookhoek, S. D. A1 - van Vliet, D. T1 - Guidlines for flexible joint transition systems RTD 1007-4:2020 N2 - Flexible joint transition systems in the form of bituminous joint transitions, type 4.1a according to RTD1007-1, have been used in the Netherlands with varying success. The lifespan in practice was found to vary greatly: between 1 and 5 years. This is too short a lifespan in relation to the lifespan of the layers of asphalt pavement. Ideally, the replacement of these bituminous joint transitions should take place simultaneously as the maintenance of the asphalt layers. In the meantime, research has been carried out nationally and internationally into improving the life span of bituminous joint transitions. In Germany and Switzerland, the regulations have been shown to lead to a life span of more than 10 years. On this basis, ETAG032-3 was established in the context of EOTA in 2013. In a competition "Silent sustainable joint transitions" held by the Dutch Directorate-General for Public Works and Water Management in the period 2007-2012, three flexible bituminous joint transitions have already been tested, two of which were ultimately found to be suitable. These have been included in the multi-choice matrix (RTD 1007-1) as concept 4.1b (anchored bituminous joint transition) and 4.1c (unanchored bituminous joint transition with stretch-spreading inlay and poured asphalt edge beams). Monitoring these joint transitions in practice over the past 8 years has shown that the desired life span is achievable with these improved joint transitions. It is expected that the improvement in life span achieved abroad can also be realised in the Netherlands if several aspects specific to the Netherlands are taken into account:  For large parts of the Dutch main road network, the traffic intensity of 500,000 heavy vehicles per year assumed in the ETAG032-3 is insufficient. This is a factor 4 to 5 higher on the busiest main roads in the Netherlands.  On 90% of the Dutch main road network, in contrast to countries such as Germany and Switzerland, an open layer (ZOAB (zeer open asfaltbeton [very open asphalt concrete])) is used.  In the Netherlands, in contrast to countries such as Germany and Switzerland, bridges and viaducts are made on a large scale of prefabricated beams and 'floating' support systems that consist entirely of rubber supports that can be deformed all-round. Such constructions have a less favourable, high-frequency deformation behaviour under traffic load.  In Germany and Switzerland, a minimum joint mass temperature of -20 °C is assumed to test bituminous joint transitions. For the Netherlands, -15 °C is assumed, which has a favourable effect. The present second version of RTD 1007-4 is a guideline for the development and realisation of a new generation of more durable flexible joint transitions with a minimum design life of 10-15 years and is a guideline for contractors to demonstrate that a flexible joint transition system meets the requirements as set out in the Directorate-General for Public Works and Water Management guideline RTD 1007-2. KW - Technical rule KW - Approval requirements KW - Extension joints KW - Highway pavements PY - 2020 VL - Version 2.0 SP - 1 EP - 77 CY - Rijkswaterstaat AN - OPUS4-54599 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weise, Frank A1 - Fladt, Matthias A1 - Wieland, M. T1 - Internal water-repellent treatment - a novel strategy for mitigating alkali-aggregate reaction in concrete pavements N2 - To prevent future alkali-aggregate reaction (AAR) damage, which has occurred frequently in the Germanhighway network in recent years, a new regulation has been drafted. This regulation severely limits the use of alkali-sensitive aggregates by requiring that their suitability be verified by certified inspectors using newly developed AAR concrete tests that involve the external supply of alkali. This has led to a significant limitation in the number of aggregates usable for concrete pavements. A novel AAR avoidance strategy is now being pursued, which aims to enable the use of borderline alkali-sensitive aggregates through the application of an internal water-repellent treatment. The addition of water repellents during concrete production should significantly reduce the ingress of water and external de-icing salts into the concrete pavement, thus reducing the potential for AAR damage. This paper presents the results of laboratory tests to assess the suitability of this new AAR prevention strategy. Representative, highly AAR-susceptible road paving concrete made with an alkali- sensitive greywacke and various water repellents were used as the basis for these experiments. The tests for concrete suitability included determining the conventional fresh and hardened concrete properties as well as concrete prism tests with external alkaline supply. Building on these results, laser-induced breakdown spectroscopy (LIBS) analyses of de-icing-salt intrusion as well as microscopic examinations for verification of the AAR characteristics were carried out. The results of the AAR concrete tests with external alkaline supply support the conclusion that, when hydrophobic agents containing a suitable active ingredient are used, the AAR damage process in road paving concrete can be sufficiently prevented. T2 - 16th International Conference on Alkali-Aggregate Reaction in Concrete CY - Lisboa, Portugal DA - 31.05.2022 KW - Concrete pavements KW - Internal water-repellent treatment KW - Preventive measures KW - Testing for potential AAR PY - 2021 SN - 978-972-49-2315-4 VL - 1 SP - 511 EP - 524 AN - OPUS4-54551 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kositz, M. A1 - Hünger, K.-J. A1 - Weise, Frank T1 - Regression analysis of ASR expansions and silica dissolution in the presence of NaCl N2 - The durability of concrete structures due to alkali-silica-reaction (ASR) is usually been assessed by ASR concrete prism tests (CPT). Therefore, the expansion of concrete specimens indicates an alkalisensitivity. In Germany these tests are performed at 40°C or accelerated 60°C. Nevertheless, ASR prism tests are expensive, power and time-consuming. For these reasons, an alternative chemical test (“mod. BTU-test”) was developed in the past. The “mod. BTU-test” was correlated with German standard CPT. In this test, the solubility of silica and alumina in the liquid phase is measured by ICP-OES. For special requirements in concrete road construction, stricter test procedures are necessary. The specimens are repeatedly subjected to cyclic alternating storage in NaCl. On the one hand, the presence of NaCl increases the ASR expansion, on the other hand NaCl also changes the dissolution behaviour of silica and alumina. For now is not possible to correlate the solubilities of “mod. BTU-test” and ASR expansions influenced by NaCl. Therefore, four aggregates with different ASR sensitivities were chosen and ASR concrete prism tests (in addition with NaCl) have been performed. According to the “mod. BTU-test” the solubilities of silica and alumina in presence of different NaCl concentrations were measured. This paper is about the regression analysis of silica and alumina dissolution and ASR expansion tests in presence of NaCl. The regression analysis shows the influence of a quasi-continuous and an interrupted cyclic alternating storage. Additionally the effects of temperature and NaCl concentration are investigated. In the end, a suitable NaCl concentration of the “mod. BTU-test” for dissolution experiments is recommended. The “mod. BTU-Test” with NaCl might be a serious and reliable test method for ASR classification for concrete road construction. T2 - 16th International Conference on Alkali-Aggregate Reaction in Concrete CY - Lisboa, Portugal DA - 31.05.2022 KW - Alkali silica reaction KW - Alkaline solution KW - Alumina & silica dissolution KW - NaCl KW - Regression analysis PY - 2021 SN - 978-972-49-2315-4 VL - 1 SP - 711 EP - 723 AN - OPUS4-54552 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krütt, Enno A1 - Pirskawetz, Stephan A1 - Wallau, Wilma A1 - Meng, Birgit T1 - Development of an automated 60 °C Concrete Prism Test N2 - ln most of the ASR-test procedures, the expansion of concrete or mortar specimens is used as an indicator to assess the ASR-potential of an aggregate or a specific concrete mix. For these tests, the specimens are stored in an ASR-provoking environment, where the reaction is accelerated by elevated temperature and humidity. To measure the length change, the storage must be interrupted for at least a few minutes. Düring the 60 °C Concrete Prism Test (60 °C-CPT), the specimens are cooled down to 20 °C for 24 hours, to ensure the same hygrothermal conditions for every measurement. This limits the number of measurements during the test period and may lead to additional effects, that probably influence the expansion development. With a recently developed device, it is possible to continuously monitor the expansion ofprisms without interrupting the ASR-provoking storage. Due to the dense database of this automated test, the results can contribute to a better understanding of the ASR-process. This study compares results of the automated and conventional 60 °C-CPT. Tests of different aggregates showed, that the results of the automated and conventional test are consistent, but the expansions during the conventional test are generally higher. Preliminary results led to the conclusion, that the cooling for the measurements leads to additional expansions. Therefore, a modified threshold should be discussed for the automated 60 °C-CPT. T2 - 16th International Conference on Alkali-Aggregate Reaction in Concrete CY - Lisboa, Portugal DA - 31.05.2022 KW - 60 °C-CPT KW - ASR expansion monitoring KW - Automated testing PY - 2021 SN - 978-972-49-2315-4 VL - 1 SP - 789 EP - 799 AN - OPUS4-54553 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eichner, Lukas A1 - Schneider, Ronald A1 - Simon, Patrick A1 - Baeßler, Matthias T1 - Optimal sensor placement for vibration-based structural health monitoring obtained via value of information analysis as part of a digital structural integrity management of offshore structures N2 - A digital structural integrity management of offshore structures enables an optimized planning of inspections and repairs with risk-based methods. In a risk-based approach, the inspection and repair strategy that minimizes the expected lifetime costs consisting of the expected inspection, repair and failure costs is determined. In addition to inspections, information on the structural condition can be continuously obtained by monitoring the vibration response of the structural system. Changes in the vibration characteristics quantified in terms of modal properties can be an indication of structural damage. In risk-based inspection and repair planning, the effect of monitoring results is determined via Bayesian updating of the structural condition and reliability. This information should be applied to inform decisions on inspections and may result in a reduced inspection effort. The benefit of continuously monitoring the structural health can be quantified in terms of the value of information, which corresponds to the difference between the expected lifetime costs with and without monitoring. In this work, we demonstrate in a numerical example how an optimized sensor placement for a vibration-based structural health monitoring system can be determined by maximizing the value of information. T2 - 3rd International Conference on Health Monitoring of Civil & Maritime Structures (HeaMES 2022) CY - Online meeting DA - 08.06.2022 KW - Structural Health Monitoring KW - Value of Information KW - Offshore Wind Energy KW - Optimal Sensor Placement KW - Bayesian System Identification PY - 2022 UR - https://www.researchgate.net/publication/362569906_Optimal_sensor_placement_for_vibration-based_structural_health_monitoring_obtained_via_value_of_information_analysis_as_part_of_a_digital_structural_integrity_management_of_offshore_structures SN - 978-1-8383226-7-0 SP - 23 EP - 32 AN - OPUS4-55465 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hille, Falk A1 - Nerger, Deborah A1 - Moosavi, Robabeh A1 - Grunwald, Marcel T1 - Discussion on data evaluation of tomographic and numerical results N2 - The contribution discusses the processing and analysis of data generated on two different ways of investigations for impact damage in reinforced concrete structures. Damage investigations are essential to determine type and characteristics of damage and thus the residual capacity. Damage describing data is generated using two different types of investigation, a non-destructive tomographic as well as numerical examination. Subsequently, data of both sources was merged and analysed. Within the research project “Behaviour of structural components during impact load conditions caused by aircraft fuel tank collision” reinforces concrete plates were damaged by impact loading, see Hering (2020). Afterwards the damaged specimens were investigated tomographically as well as numerically using several methods and models. Aim of the presented research work was to specify an objective comparability of numerical data with experimentally determined damage patterns and based on this, to establish a quantitative damage evaluation. T2 - 26th International Conference on Structural Mechanics in Reactor Technology CY - Potsdam, Germany DA - 10.07.2022 KW - Impact damage on reinforced concrete KW - Tomographic damage evaluation KW - Numerical damage simulation PY - 2022 SP - 1 EP - 8 AN - OPUS4-55474 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eichner, Lukas A1 - Gerards, Paul A1 - Herrmann, Ralf A1 - Schneider, Ronald A1 - Hille, Falk A1 - Baeßler, Matthias T1 - A framework for data and structural integrity management for support structures in offshore wind farms based on building information modelling N2 - Support structures of wind turbines in German offshore wind farms are regularly inspected. Currently, inspection outcomes are generally not systematically recorded. This prevents their consistent handling and processing, which is a key requirement to enable an efficient structural integrity management. As part of the DiMoWind-Inspect project, a data model and reference designation system for such inspection results is developed to facilitate their identification, localization, quantification, tracing and linking throughout the lifetime of a wind farm and beyond. The inspection results together with structural health monitoring results and information on repairs form the basis for assessing and predicting the structural condition, estimating the remaining lifetime, and planning of future inspections, structural health monitoring, and repairs. As a basis for developing a digital structural integrity management, a generic framework is proposed in this paper, which describes the stakeholders, data, models, processes and workflows of the integrity management of support structures in offshore wind farms and their interrelations. The framework adopts a building information modelling approach to describe the information relevant to the structural integrity management. The central digital space of the framework is a common data environment. An implementation of the framework will enable a digital structural integrity management in which inspection, structural health monitoring, repair, assessment and planning outcomes generated throughout the life cycle of a wind farm can be consistently collected, managed, shared and processed by the relevant shareholders. T2 - 8th International Symposium on Reliability Engineering and Risk Management CY - Hannover, Germany DA - 04.09.2022 KW - Offshore wind energy KW - support structures KW - structural health monitoring KW - building information modelling KW - structural integrity management PY - 2022 DO - https://doi.org/10.3850/978-981-18-5184-1_MS-04-161-cd SP - 111 EP - 117 PB - Research Publishing CY - Singapore AN - OPUS4-55656 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kremberg, Jan A1 - Häßler, Dustin A1 - Stelzner, Ludwig A1 - Hothan, Sascha T1 - Brandversuche an mechanisch belasteten Carbonzuggliedern N2 - Der Beitrag stellt experimentelle Untersuchungen zum Feuerwiderstand von Carbonzuggliedern vor. Die Anwendung von Zuggliedern aus Carbon ist durch die außergewöhnlich gute Ermüdungs- sowie hohe Zugfestigkeit des Werkstoffs motiviert. Ferner ergibt sich gegenüber Stahl eine deutliche Reduzierung des Querschnitts. Perspektivisch sollen damit Stahlzugglieder im Netzwerkbogenbrückenbau ersetzt werden. Durch die Materialsubstitution werden Ressourcen nicht nur beim Zugglied selbst, sondern auch am Gesamttragwerk der Brücke eingespart. Da zum Tragverhalten von Carbonzuggliedern im Brandfall bislang keine Erkenntnisse vorliegen, sollen mit Hilfe von Bauteilbrandversuchen die Versagensmechanismen sowie die grundsätzliche Gleichwertigkeit gegenüber konventionellen Stahlhängern untersucht werden. Der Beitrag beschreibt die Durchführung und die Ergebnisse von Brandversuchen an mechanisch belasteten Carbonzuggliedern. Die realmaßstäblichen Versuche werden am unikalen Zugbauteil-prüfofen der BAM im Mai 2022 durchgeführt. Das Versuchsprogramm umfasst vier Carbonzugglieder mit kreisrunden Querschnitten in zwei verschiedenen Durchmessern, ⌀36 mm und ⌀51 mm. Aus Gründen der Vergleichbarkeit erfolgt die Brandbeanspruchung nach Einheits-Temperaturzeitkurve (ETK). Während des Brandversuches wird die axiale Prüfkraft von 750 kN bzw. 1500 kN bis zum Eintreten des Probenversagens konstant gehalten. Zusätzlich werden die Längsverformung sowie die Bauteil- und Brandraumtemperaturen aufgezeichnet. In einem Vorversuch an einem unbelasteten Bauteilabschnitt eines Carbonzuggliedes konnte das Brand- und Erwärmungsverhalten des Verbundmaterials untersucht werden. Dabei zeigten sich Makrorisse und eine Zersetzung der Kunststoffmatrix sowie eine hohe Temperaturbeständigkeit der Kohlenstofffasern. Durch das Fehlen der schützenden Matrix reagierten die Carbonfasern sensibel auf Querbeanspruchung. Dies führte zu einem Bruch und Ablösen der oberflächennahen Fasern. T2 - 8th Symposium Structural Fire Engineering CY - Brunswick, Germany DA - 13.09.2022 KW - Carbon KW - Zugglied KW - Brandversuch KW - Feuerwiderstand KW - Brandschutz PY - 2022 SP - 1 EP - 13 PB - TU Braunschweig CY - Braunschweig AN - OPUS4-55704 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klimek, André A1 - Stelzner, Ludwig A1 - Hothan, Sascha A1 - Zehfuß, J. T1 - Auswirkung von passivem Zwang auf das Abplatzverhalten von Beton im Brandfall N2 - Der diesjährige Beitrag zeigt den Einfluss ausgewählter Versuchsrandbedingungen auf das Abplatzverhalten von Normalbeton im kleinskaligen Brandversuch. Im Rahmen der Untersuchungen wurde die Abplatzneigung von acht zylindrischen Betonprüfkörpern der Maße Ø47 cm x 29 cm aus Normalbeton analysiert. Vier Prüfkörper wurden aus Normalbeton mit quarzitischer Gesteinskörnung hergestellt, wohingegen die grobe Gesteinskörnung (>2 mm) der anderen vier Prüfkörper durch Basaltsplitt ersetzt wurde. Neben der Art der groben Gesteinskörnung wurden zusätzlich ausgewählte Versuchsrandbedingungen variiert. Dies umfasste zum einen die Vorlagerung der Prüfkörper bei verschiedenen Umgebungsfeuchten und zum anderen die Ummantelung der Prüfkörper mit zwei Ringen aus Stahl bzw. einem durchgehenden Stahlblech. Die Ummantelung der Prüfkörper mit Stahlringen im Brandversuch führt zu einer Behinderung der thermischen Ausdehnung der Prüfkörper und zum Aufbau thermomechanischer Zwangsdruckspannungen. Diese Zwangsdruckspannungen werden maßgeblich von der thermischen Ausdehnung der verwendeten Gesteinskörnung beeinflusst. Zusätzlich wird die Feuchteabgabe über die Mantelfläche behindert. Der Einsatz des Stahlblechs reduziert lediglich die Abgabe der Feuchtigkeit über die Mantelfläche und induziert vernachlässigbare Zwangsdruckspannungen im Beton. Die Brandbeanspruchung der Prüfkörper erfolgte einseitig nach der Einheits-Temperaturzeitkurve (ETK) über einen Zeitraum von 60 Minuten. Mit Hilfe eines Laser Scanners wurden vergleichende 3D-Messungen der brandbeanspruchten Oberfläche vor und nach dem Brandversuch durchgeführt. Aus diesen Messungen konnten das Abplatzvolumen, die Abplatztiefenverteilung und die maximale Abplatztiefe ermittelt werden. Während des Brandversuchs wurde die Temperaturverteilung im Prüfkörper mittels fünf eingebetteter Mantelthermoelemente in verschiedenen Tiefen bestimmt. Die Ergebnisse zeigen, dass die Abplatzungen an der brandbeanspruchten Oberfläche infolge der Prüfkörperummantelung mit Stahlringen bzw. Stahlblech zunehmen. Bei einer Ummantelung mit Stahlringen mit gleichzeitiger Vortrocknung der Betonrandzone platzt der Prüfkörper mit quarzitischer Gesteinskörnung ab, wohingegen der Prüfkörper mit basaltischer Gesteinskörnung keine Abplatzungen aufweist. Dies wird auf die unterschiedliche Ausprägung der thermomechanischen Schädigung infolge der unterschiedlichen thermischen Ausdehnungskoeffizienten von Quarzkies und Basalt zurückgeführt. Die Ergebnisse der Brandprüfserie zeigen, dass die Variation der Prüfrandbedingungen bei Beibehaltung der Prüfkörpergröße einen maßgeblichen Einfluss auf das Abplatzverhalten haben. Die Randbedingungen sind daher bei kleinskaligen Brandversuchen, die zukünftig als „Screening-Tests“ ersatzweise für kostenintensive Bauteilversuche verwendet werden sollen, zu berücksichtigen. T2 - 8th Symposium Structural Fire Engineering CY - Brunswick, Germany DA - 13.09.2022 KW - Brand KW - Beton KW - Abplatzen KW - Zwang PY - 2022 SP - 1 EP - 12 PB - TU-Braunschweig CY - Braunschweig AN - OPUS4-55731 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Strangfeld, Christoph A1 - Bühling, Benjamin A1 - Hauke, M. A1 - Schweitzer, T. A1 - Maack, Stefan T1 - Frequency modulated, air-coupled ultrasound generated by fluidic oscillators N2 - The majority of ultrasonic devices used for non-destructive testing in civil engineering require contact with the surface of the concrete (specimen), which significantly increases the time required for the measurement. This makes it impractical for extensive investigation of large-scale structures such as bridge decks, foundations, or tunnels. In a pioneering approach, fluidic oscillators are used as contact free ultrasonic sources to overcome the aforementioned limitations. These robust and cost-effective actuators require only pressurised air and are ideally suited for harsh environments. At a constant supply pressure, they generate a continuous mono-frequent actuation signal. Further, varying the supply pressure via a fast pressure regulator was found to generate a frequency modulated signal which enabled time-of-flight measurement with an added advantage of increased signal to noise ratio. To demonstrate the feasibility of this novel idea of non-contact ultrasound, the results of the initial tests are presented. T2 - IEEE International Ultrasound Symposium CY - Venice, Italy DA - 11.10.2022 KW - Air-coupled ultrasound KW - Frequency modulation KW - Non-destructive testing KW - Civil engineering KW - Building materials KW - Fluidic oscillators PY - 2022 DO - https://doi.org/10.1109/IUS54386.2022.9958740 SP - 1 EP - 4 AN - OPUS4-56073 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Dietrich, P. A1 - Beblo-Vranesevic, K. A1 - Kjærvik, Marit A1 - Unger, Wolfgang A1 - Schwibbert, Karin A1 - Hardie, K. A1 - Brown, J. T1 - XPS surface analysis of bacterial samples N2 - This application note presents how EnviroESCA can be used to analyze bacterial samples under near ambient pressure conditions in various states of hydration using different levels of humidity. Such investigations of bacterial cell wall surfaces in their hydrated state are essential for studying biological interfaces at work. The use of innovative near-ambient pressure (NAP-)XPS instrumentation allows the detailed analysis of irregularly-surfaced biofilms. NAP-XPS enables the surface analysis of bacterial samples in their natural hydrated state without complex sample preparation techniques such as freeze-drying or fast-freezing, which are needed for XPS analysis in ultrahigh vacuum. KW - Near ambient pressure XPS KW - Biofilms PY - 2018 UR - http://www.enviroai.com/uploads/1/0/2/8/102861712/xps_surface_analysis_of_bacillus_subtilis_biofilms_final.pdf IS - Application Note #000399 SP - 1 EP - 5 CY - Berlin AN - OPUS4-44588 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Kjaervik, Marit A1 - Schwibbert, Karin A1 - Dietrich, P. A1 - Thissen, A. A1 - Unger, Wolfgang T1 - Near-ambient pressure XPS of hydrated Escherichia coli samples with EnviroESCA N2 - This application note presents how EnviroESCA can be used to analyze E. coli biofilms on silicon under near ambient pressure conditions in various states of hydration. Such investigations of the outer bacterial cell surface in their hydrated state are essential for studying biological interfaces at work. KW - Biofilms KW - E. coli KW - NAP-XPS PY - 2018 UR - http://www.enviroai.com/uploads/1/0/2/8/102861712/nap_xps_of_escherichia_coli_samples.pdf IS - Application Note #000400 SP - 1 EP - 4 CY - Berlin, Germany AN - OPUS4-45720 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fürst, Richard A1 - Häßler, Dustin A1 - Stelzner, Ludwig A1 - Hothan, Sascha T1 - In situ test procedure to determine the fire resistance of exisiting steel structures with aged intumescent coating N2 - Intumescent coatings are commonly used in civil engineering to increase the fire resistance of steel structures. In case of a fire, the intumescent coating reacts and forms a thermally protective char around the steel member. Thus, the heating of the steel is significantly delayed, and as a result, a higher fire resistance can be achieved. Throughout the working life, intumescent coatings are aged by climatic factors. To predict durability for several years, the behaviour of the intumescent coatings is extrapolated based on accelerated artificial ageing. The established German and European assessment procedures to test and predict durability assume a working life of at least 10 years. For an extended period, additional evidence is required; yet the procedure and specifications to justify this are not described. Available in situ methods to assess the thermal performance of intumescent coatings are currently limited in their information content. Therefore, BAM is conducting a research project to develop a minimally invasive in situ test procedure to determine the fire resistance of existing steel structures with applied intumescent coating. The paper will describe the test setup, the developed prototype furnace, and the results of the performed test programme with uncoated and coated steel specimens. Based on this, recommendations for the test procedure are given. T2 - Structures in Fire 2024 CY - Coimbra, Portugal DA - 19.06.2024 KW - In situ KW - Intumescent coating KW - Steel structures KW - Test procedure PY - 2024 SN - 978-989-35292-2-5 DO - https://doi.org/10.30779/cmm_SIF24 SP - 1217 EP - 1228 AN - OPUS4-61258 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Andrés Arcones, Daniel A1 - Diercks, Philipp A1 - Robens-Radermacher, Annika A1 - Rosenbusch, Sjard Mathis A1 - Tamsen, Erik A1 - Tyagi, Divyansh A1 - Unger, Jörg F. T1 - FenicsXConcrete N2 - FenicsXConcrete is a Python package for the simulation of mechanical problems. The general PDE solving software FEniCSx is extended with classes describing experimental setups, mechanical problems, thermo-mechanical problems, additive manufacturing and sensors. KW - FEM KW - Fenics KW - Concrete modelling PY - 2023 UR - https://github.com/BAMresearch/FenicsXConcrete DO - https://doi.org/10.5281/zenodo.7780757 PB - Zenodo CY - Geneva AN - OPUS4-59121 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Unger, Jörg F. A1 - Robens-Radermacher, Annika A1 - Tamsen, Erik T1 - Data provenance - from experimental data to trustworthy simulation models and standards N2 - FAIR (findable, accessible, interoperable and reusable) data usage is one of the main principals that many of the research and funding organizations include in their strategic plans, which means that following the main principals of FAIR data is required in many research projects. The definition of data being FAIR is very general, and when implementing that for a specific application or project or even setting a standardized procedure within a working group, a company or a research community, many challenges arise. In this contribution, an overview about our experience with different methods, tools and procedures is outlined. We begin with a motivation on potential use cases for the applications of FAIR data with increasing complexity starting from a reproducible research paper over collaborative projects with multiple participants such as Round-Robin tests up to data-based models within standardization codes, applications in machine learning or parameter estimation of physics-based simulation models. In a second part, different options for structuring the data are discussed. On the one hand, this includes a discussion on how to define actual data structures and in particular metadata schema, and on the other hand, two different systems for storing the data are discussed. The first one is the openBIS system, which is an open-source Lab notebook and PostgreSQL based data management system. A second option are a semantic representations using RDF based ontologies for the domain of interest. In a third section, requirements for workflow tools to automate data processing are discussed and their integration into reproducible data analysis is presented with an outlook on required information to be stored as metadata in the database. Finally, the presented procedures are exemplarily demonstrated for the calibration of a temperature dependent constitutive model for additively manufactured mortar. Metadata schemata for a rheological measurement setup are derived and implemented in an openBIS database. After a short review of a potential numerical model predicting the structural build-up behaviour, the automatic workflow to use the stored data for model parameter estimation is demonstrated. T2 - 4th International Congress on Materials & Structural Stability CY - Rabat, Morocco DA - 08.03.2023 KW - Data provenance KW - Experimental data to trustworthy KW - Simulation models and Standards PY - 2023 UR - https://www.rsc-cmss23.asmatec.org/RILEM%20Committees%20Program.php SP - 1 EP - 9 CY - Rabat, Morocco AN - OPUS4-57349 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Maack, Stefan A1 - Küttenbaum, Stefan A1 - Bühling, Benjamin T1 - Low-frequency ultrasound data (pulse-echo technique) with shear horizontal and longitudinal waves on the step-shaped concrete specimen “Pk266” with tendons N2 - This dataset contains raw data acquired in ultrasound measurements on a reference specimen made of concrete at Bundesanstalt für Materialforschung und -prüfung (BAM), Berlin (Germany). The internal specimen identifier is “Pk266”. The measurements were conducted using the pulse-echo method. The upper surface of the specimen was defined as measuring area. The aim of the measurements is to determine both the geometrical dimensions (thickness) and the position of tendons to the measuring area. In addition to this, a second dataset of a second specimen with identifier is existing named “Pk050” has been acquired. Pk050 has the same geometrical dimensions and concrete recipe as Pk266 recipe but does not contain tendons [Reference: https://doi.org/10.7910/DVN/9EID5D]. KW - Ultrasound KW - Pulse echo method KW - Synthetic Aperture Focusing Technique KW - Validation KW - Elastic wave PY - 2023 DO - https://doi.org/10.7910/DVN/NUU0WZ PB - Harvard College CY - Cambridge, MA, USA AN - OPUS4-57232 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hering, Marcus A1 - Fiedler, Georg A1 - Schubert, T. A1 - Hille, Falk A1 - Hüsken, Götz A1 - Beckmann, B. A1 - Grunwald, Marcel A1 - Redmer, Bernhard A1 - Rogge, Andreas T1 - Investigation of multiple impact-damaged reinforced concrete structures as a reference for liquid penetration behavior and tomographic studies N2 - The structural integrity of outer reinforced concrete (RC) containments of nuclear power plants provides an essential shield against external hazards. If this containment is damaged by an impact event, such as an aircraft crash, the question arises to which degree the reinforced concrete containment still has its protective capability. This concerns both purely structural protection and protection against liquids penetrating the interior of the containment. Due to the dimensions of the containment structures, it is difficult to perform real scale impact experiments, so in the past decades plate geometries at medium scale have been used for investigations. Detailed investigations on the structural behaviour of RC members or RC plates subjected to impact loading have already been presented in Just et al., Hering, Hering et al., Bracklow et al., Hille et al. and Nerger et al. The following investigations deal with the single and multiple impact event (first hard impact and/or subsequent soft impact) on a RC specimen, which provides the basis for further investigations. A description of the test setup and the test procedure as well as a presentation of the test results from the impact tests are provided. Furthermore, the experimental program is presented, which the damaged RC specimens are to undergo to deal with the question of how much the impact-damaged RC structure has become permeable to liquid media, such as water and kerosene, depending on the intensity of the impact. The aim of these following investigations is to develop a test setup that can be applied to investigate the liquid penetration behaviour (LPB) of small, medium, and large-scale RC members. In addition to the liquid penetration experiments, the damaged specimens are to be examined by planar tomography to obtain the damage inside the specimen. The combination of damaging event, fluid penetration behaviour and tomography should enable a comprehensive understanding of the damage to the RC specimen. T2 - Conference: 27th International Conference on Structural Mechanics in Reactor Technology (SMiRT) CY - Yokohama, Japan DA - 04.03.2024 KW - Drop tower KW - Hard impact KW - Soft impact KW - Multiple impact PY - 2024 SP - 1 EP - 10 PB - IASMiRT CY - Yokohama, Japan AN - OPUS4-59723 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Karapanagiotis, Christos ED - Krebber, Katerina T1 - Machine learning for strain, temperature and humidity discrimination in Brillouin optical frequency domain analysis N2 - We propose to our knowledge for the first time an ensemble of probabilistic machine learning models for strain, temperature and humidity discrimination in Brillouin optical frequency domain analysis (BOFDA) applying a two-fiber configuration. T2 - 28th International Conference on Optical Fiber Sensors CY - Hamamatsu, Japan DA - 20.11.2023 KW - Multiparameter sensing KW - Machine learning KW - Fiber optic sensors KW - Structural health monitoring PY - 2023 SP - 1 EP - 4 PB - Optica Publishing Group AN - OPUS4-59397 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Diercks, Philipp A1 - Veroy, K. A1 - Robens-Radermacher, Annika A1 - Unger, Jörg F. T1 - Multiscale modeling of linear elastic heterogeneous structures via localized model order reduction N2 - In this paper, a methodology for fine scale modeling of large scale linear elastic structures is proposed, which combines the variational multiscale method, domain decomposition and model order reduction. The influence of the fine scale on the coarse scale is modelled by the use of an additive split of the displacement field, addressing applications without a clear scale separation. Local reduced spaces are constructed bysolving an oversampling problem with random boundary conditions. Herein, we inform the boundary conditions by a global reduced problem and compare our approach using physically meaningful correlated samples with existing approaches using uncorrelated samples. The local spaces are designed such that the local contribution of each subdomain can be coupled in a conforming way, which also preserves the sparsity pattern of standard finite element assembly procedures. Several numerical experiments show the accuracy and efficiency of the method, as well as its potential to reduce the size of the local spaces and the number of training samples compared to the uncorrelated sampling KW - Multiscale methods KW - Variational multiscale method KW - Localized model order reduction KW - Proper orthogonal PY - 2024 UR - https://arxiv.org/abs/2201.10374 DO - https://doi.org/10.48550/arXiv.2201.10374 PB - Arxiv; Cornell Tech CY - New York, NY AN - OPUS4-59803 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eichner, Lukas A1 - Schneider, Ronald A1 - Baeßler, Matthias T1 - Probabilistische Systemidentifikation einer Versuchsstruktur für Substrukturen von Offshore-Windenergieanlagen mit statischen und dynamischen Messdaten N2 - In diesem Beitrag wird ein probabilistischer Ansatz zur Systemidentifikation für Tragstrukturen von Offshore-Windkraftanlagen vorgestellt. Der Schwerpunkt der Forschung liegt auf der Integration von globalen Systemantworten in Form von Eigenfrequenzen und -formen sowie Verschiebungen und Dehnungen als lokale Messdaten. Die unterschiedlichen Daten werden kombiniert für die Aktualisierung der Parameter eines Finite-Elemente-Modells genutzt. Zu diesem Zweck wird ein probabilistischer Ansatz nach Bayes verfolgt, um Vorwissen sowie Unsicherheiten einzubeziehen. Die Methodik wird bei einer Versuchsstruktur angewandt, die eine Jacket-Substruktur von Offshore-Windenergieanlagen nachbildet. Eine Systemidentifikation mit Hilfe von Überwachungsdaten ist wertvoll für Jacket-Substrukturen, da eine Zustandsanalyse für die Gewährleistung der strukturellen Integrität unerlässlich ist, aber hinsichtlich der schwierigen Offshore-Bedingungen möglichst effizient sein muss. In diesem Zusammenhang schafft diese Arbeit die Grundlage für eine Schadenserkennung, eine verbesserte Vorhersage der Ermüdungslebensdauer und optimierte Instandhaltungsstrategien. Während das Modell hinsichtlich der statischen Messdaten erfolgreich aktualisiert werden kann, sind Schwierigkeiten bei der Identifizierung der dynamischen Systemeigenschaften erkennbar. T2 - 8. VDI-Fachtagung Baudynamik 2025 CY - Würzburg, Germany DA - 02.04.2025 KW - Systemidentifikation KW - Versuchsstruktur KW - Jacket KW - Offshore-Windenergie PY - 2025 VL - 8 SP - 175 EP - 188 AN - OPUS4-62879 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Borges de Oliveira, F. A1 - Reuter, T. A1 - Plotzki, David A1 - Bartscher, M. A1 - Hausotte, T. T1 - Novel reference standards for the qualification of radiography-based computed tomography simulation software N2 - This contribution presents a set of largely novel reference standards specially designed for testing different important physical effects and functionalities of radiography-based computed tomography (CT) simulation software. These standards were developed within the scope of the German cooperation project “CTSimU – Radiographic Computed Tomography Simulation for Measurement Uncertainty Evaluation” [1] and serve as tools for the basic qualification of the sufficient physical correctness and required features of simulation software of CT-based coordinate measurement systems (CMSs) via the analyses either of 2D projection images only or of full CT scans. The results serve as input to the German standardisation committee for the development of a new national VDI/VDE guideline in the series VDI/VDE 2630 dealing with the basic qualification aspect of CT simulation software and shall lay ground for the measurement uncertainty determination of dimensional measurements using CT. T2 - 11th Conference on Industrial Computed Tomography (iCT 2022) CY - Online meeting DA - 08.02.2022 KW - Multi-geometry cuboid KW - Radiographic simulation software KW - Basic qualification KW - CT simulation, spherical step-wedge KW - Conical hole sheet KW - Tungsten-Edge PY - 2022 SP - 1 EP - 12 PB - Research Group Computed Tomography, Upper Austrian University of Applied Sciences (FH OÖ) CY - Wels, Austria AN - OPUS4-54569 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bircher, B. A1 - Meli, F. A1 - Küng, A. A1 - Bellon, Carsten A1 - Evsevleev, Sergei A1 - Katic, M. A1 - Heikkinen, V. A1 - Hemming, B. A1 - Lassila, A. T1 - Traceable determination of non-static XCT machine geometry: New developments and case studies N2 - It is fundamental to determine the machine geometry accurately for dimensional X-ray computed tomography (XCT) measurements. When performing high-accuracy scans, compensation of a non-static geometry, e.g. due to rotary axis errors or drift, might become necessary. Here we provide an overview of methods to determine and account for such deviations on a per projection basis. They include characterisation of stage error motions, in situ geometry measurements, numerical simulations, and reconstruction-based optimization relying on image quality metrics and will be discussed in terms of their metrological performance. Since a radiographic calibration is always required to provide an initial absolute geometry, this method will be presented as well. The improvements of the XCT geometry correction methods are presented by means of case studies. The methods can be applied individually or in combination and are intended to provide a toolbox for XCT geometry compensation. T2 - 11th Conference on Industrial Computed Tomography (iCT 2022) CY - Online meeting DA - 08.02.2022 KW - Radiographic XCT geometry determination KW - Dimensional metrology KW - traceability KW - XCT machine geometry KW - Calibrated reference standards PY - 2022 SP - 1 EP - 10 PB - Research Group Computed Tomography, Upper Austrian University of Applied Sciences (FH OÖ) CY - Wels, Austria AN - OPUS4-54479 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Plotzki, David A1 - Hartlaub, Bendix A1 - Borges de Oliveira, F. A1 - Reuter, T. A1 - Wohlgemuth, F. A1 - Bellon, Carsten A1 - Hausotte, T. T1 - The CTSimU software toolbox for CT-related image processing and quality assessment N2 - A software toolbox is introduced that addresses several needs common to computed tomography (CT). Built for the WIPANO CTSimU project to serve as the reference implementation for its image processing and evaluation tasks, it provides a Python 3 interface that is adaptable to many conceivable applications. Foremost, the toolbox features a pipeline architecture for sequential 2D image processing tasks, such as flat field corrections and image binning, and enables the user to create their own processing modules. Beyond that, it provides means to measure line profiles and image quality assessment algorithms to calculate modulation transfer functions (MTF) or to determine the interpolated basic spatial resolution (iSRb) using a duplex wire image. It can also be used to calculate projection matrices for the reconstruction of scans with arbitrary industrial CT geometries and trajectories. The CTSimU project defined a framework of projection- and volume-based test scenarios for the qualification of radiographic simulation software towards its use in dimensional metrology. The toolbox implements the necessary evaluation routines and generates reports for all projection-based tests. T2 - 11th Conference on Industrial Computed Tomography (iCT 2022) CY - Online meeting DA - 08.02.2022 KW - Image processing KW - CT KW - Geometry KW - Software KW - Python PY - 2022 SP - 1 EP - 7 PB - Research Group Computed Tomography, Upper Austrian University of Applied Sciences (FH OÖ) CY - Wels, Austria AN - OPUS4-54476 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reuter, T. A1 - Borges de Oliveira, F. A1 - Plotzki, David A1 - Hausotte, T. T1 - Influence of detector misalignments on different geometrical and dimensional measurands using a dedicated test specimen N2 - An important focus of research in Industrial X-ray Computed Tomography (CT) is to determine the task-specific measurement uncertainty of CT measurements numerically by using simulations. For this, all relevant influence factors need to be identified and quantified. It is known, for example, that geometrical misalignments of the detector lead to measurement deviations if the reconstruction does not consider these misalignments. This contribution uses computer simulation of CT data to investigate the influence of geometrical misalignments of the detector on several measurands found in typical measurements tasks in the industry. A newly developed test specimen with a broad variety of features is used for this study. Angular and positional detector deviations are systematically introduced into the simulations and deliberately left uncompensated during the CT reconstruction. The resulting measurement deviations are shown and discussed. T2 - 11th Conference on Industrial Computed Tomography (iCT 2022) CY - Online meeting DA - 08.02.2022 KW - Geometrical misalignment KW - Task specific numerical measurement uncertainty KW - Dimensional metrology PY - 2022 SP - 1 EP - 7 PB - Research Group Computed Tomography, Upper Austrian University of Applied Sciences (FH OÖ) CY - Wels, Austria AN - OPUS4-54568 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Strangfeld, Christoph A1 - Klewe, Tim ED - Rizzo, P. ED - Milazzo, A. T1 - Hygrometric Moisture Measurements Based on Embedded Sensors to Determine the Mass of Moisture in Porous Building Materials and Layered Structures N2 - Subfloors are layered structures, consisting largely of porous building materials, such as screed. They are often suffering damage from tap water leakage, which is a typical problem in buildings, and which has largely contributed to repair costs of almost 3 billion Euro in 2018 alone in Germany. In this context, especially mould plays a role, which is both destroying the structure and posing severe health risks. To determine the damaging effects of moisture, it is necessary to know the respective processes occurring in building materials, especially to quantify the amount of moisture and its progress in the material. In this study, humidity sensors are used to derive the material moisture experimentally. Capacitive sensors recording the relative humidity are embedded into the screed and in the insulation materials such as expanded polystyrene, extruded polystyrene, perlite and glass wool. For the application in screed, the sensors need to be shielded against the aggressive alkaline materials. To ensure an appropriate exchange with the environment, a permeable membrane is requested. Different membrane materials have been investigated regarding their robustness and their permeability. In the first experimental setup, two humidity sensor arrays with seven individual sensors are embedded in homogeneous screed samples. The measured corresponding relative humidity of the screed is converted to the material moisture based on the approach of Hillerborg. In a second experimental setup, a layered structure of a complete subfloor is built in a box of 0.8 m times 0.8 m. The humidity sensors are positioned in the different insulation materials of various thicknesses. By adding water, leakage damage is simulated and its progress and effect is investigated experimentally. The investigations point at the question if the observed moisture is able to generate damage such as mould. The moisture and corresponding humidity values are discussed. It will be shown that this low-cost hygrometric approach can be used easily for moisture monitoring of screed and insulation materials as well KW - Moisture monitoring KW - Material moisture KW - Building materials KW - Embedded humidity sensors PY - 2021 DO - https://doi.org/10.1007/978-3-030-64594-6_22 VL - 1 SP - 213 EP - 225 PB - Springer Nature CY - Cham AN - OPUS4-52013 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Koch, Claudia A1 - Mirtsch, Mona A1 - Blind, K. T1 - Resilient gegen Corona? Auswirkungen der Corona-Pandemie auf Konformitätsbewertungsstellen N2 - Covid 19 stellt Gesellschaft und Wirtschaft vor immense Herausforderungen – auch die Konformitätsbewertungsbranche ist betroffen. Die Bundesanstalt für Materialforschung und -prüfung (BAM) hat gemeinsam mit der TU Berlin und dem Fraunhofer ISI die Auswirkungen der Pandemie auf die wirtschaftliche und operative Lage von Konformitätsbewertungsstellen in Deutschland untersucht. Dabei standen auch die Digitalisierung sowie die Resilienz der Branche im Fokus. KW - Corona KW - Konformitätsbewertungsstellen KW - Resilienz KW - Qualitätssicherung KW - Qualitätsinfrastruktur KW - COVID-19 KW - Zertifizierung KW - Digitalisierung KW - Konformitätsbewertung PY - 2021 VL - 66 IS - 01/2021 SP - 36 EP - 39 PB - Carl Hanser CY - München AN - OPUS4-51974 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simon, Patrick A1 - Schneider, Ronald A1 - Viefhues, Eva A1 - Said, Samir A1 - Herrmann, Ralf A1 - Baeßler, Matthias ED - Papadrakis, M. ED - Fragiadakis, M. ED - Papadimitriou, C. T1 - Vibration-based Structural Health Monitoring of a Reinforced Concrete Beam Subjected to Varying Ambient Conditions Using Bayesian Methods N2 - Inspection and maintenance contribute significantly to the lifetime cost of bridges. There is significant potential in using information obtained through structural health monitoring to update predictive models of the condition and performance of such structures, and thus ena-ble an improved decision-making regarding inspection and maintenance activities. Within the AISTEC project funded by the German Federal Ministry of Education and Research, we develop vibration-based structural health monitoring systems aimed at continuously provid-ing information on the structural condition of bridges. Environmental variations such as changing ambient temperatures can significantly influence the dynamic characteristics of bridges and thus mask the effect of structural changes and damages. It remains a challenge to account for such influences in structural health monitoring. To study the effect of ambient temperatures on the dynamic characteristics of beam structures, we monitor the vibration response of a reinforced concrete beam in the uncracked and cracked state at varying tem-peratures in a climate chamber. We postulate a set of competing parameterized probabilistic structural models, which explicitly account for the effect of varying ambient temperatures on the mechanical properties of the system. We then combine the information provided by the structural models with the information contained in the recorded vibration data to learn the parameters of the temperature-dependent structural models and infer the plausible state of the beam using Bayesian system identification and model class selection. T2 - EURODYN 2020, XI International Conference on Structural Dynamics CY - Online meeting DA - 23.11.2020 KW - Structural health monitoring KW - Bayesian methods KW - Environmental effects PY - 2020 SN - 978-618-85072-2-7 SN - 978-618-85072-0-3 SP - 1254 PB - Institute of Structural Analysis and Antiseismic Research, School of Civil Engineering, National Technical University of Athens (NTUA) CY - Athens, Greece AN - OPUS4-51590 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Viefhues, Eva A1 - Döhler, M. A1 - Hille, Falk A1 - Mevel, L. T1 - Fault detection for linear parameter varying systems under changes in the process noise covariance N2 - Detecting changes in the eigenstructure of linear systems is a comprehensively investigated subject. In particular, change detection methods based on hypothesis testing using Gaussian residuals have been developed previously. In such residuals, a reference model is confronted to data from the current system. In this paper, linear output-only systems depending on a varying external physical parameter are considered. These systems are driven by process noise, whose covariance may also vary between measurements. To deal with the varying parameter, an interpolation approach is pursued, where a limited number of reference models -- each estimated from data measured in a reference state -- are interpolated to approximate an adequate reference model for the current parameter. The problem becomes more complex when the different points of interpolation correspond to different noise conditions. Then conflicts may arise between the detection of changes in the eigenstructure due to a fault and the detection of changes due to different noise conditions. For this case, a new change detection approach is developed based on the interpolation of the eigenstructure at the reference points. The resulting approach is capable of change detection when both the external physical parameter and the process noise conditions are varying. This approach is validated on a numerical simulation of a mechanical system. T2 - IFAC World Congress 2020 CY - Online meeting DA - 11.07.2020 KW - Linear parameter varying systems KW - Fault detection KW - Changing process noise KW - Subspace-based residual KW - Model interpolation PY - 2020 SP - 13858 AN - OPUS4-51617 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schönsee, Eric T1 - Entwicklung eines Prüfstandes zur Erfassung von Frischbetoneigenschaften während der additiven Fertigung T1 - Development of a test rig for detecting parameters of fresh concrete during additive manufacturing N2 - In den vergangenen Jahren ist die Entwicklung additiver Fertigungsverfahren branchenübergreifend fortgeschritten. In der Industrie ist die Verarbeitung von Polymeren wie z. B. Polylactide (PLA) oder Acrylnitril-Butadien-Styrol-Copolymer (ABS) am weitesten verbreitet, aber auch die Verarbeitung von Metallen nimmt zu. Umfragen des Fraunhofer-Institut für Produktionstechnik und Automatisierung IPA aus dem Jahr 2016 verdeutlichen, wie hoch das Potential additiver Fertigungsverfahren eingeschätzt wird und auch die Anzahl der jährlich angemeldeten Patente im Bereich des 3D-Drucks hat sich in den letzten Jahren vervielfacht. KW - Additive Fertigung KW - 3D Druck von Beton KW - Prozessüberwachung PY - 2021 SP - 1 EP - 145 CY - Berlin AN - OPUS4-52550 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bühling, Benjamin T1 - Acoustic and flow data of an ultrasonic fluidic switch and an ultrasonic piezoelectric transducer N2 - This dataset contains acoustic and flow data of an ultrasonic fluidic switch, which have been acquired using a microphone, a hot-wire anemometer and a pitot tube. Furthermore, acoustic data of a commercial piezoelectric transducer is provided. KW - Fluidics KW - Air-coupled ultrasound KW - Ultrasound KW - Non-destructive testing KW - Acoustic-flow interaction KW - Piezoelectric transducer PY - 2020 DO - https://doi.org/10.7910/DVN/OQYPC9 PB - Harvard College CY - Cambridge, MA, USA AN - OPUS4-52392 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Viefhues, Eva A1 - Döhler, M. A1 - Simon, Patrick A1 - Herrmann, Ralf A1 - Hille, Falk A1 - Mevel, L. ED - Cunha, A. ED - Caetano, E. T1 - Stochastic subspace-based damage detection of a temperature affected beam structure N2 - Structural health monitoring (SHM) of civil structures often is limited due to changing environmental conditions, as those changes affect the structural dynamical properties in a similar way like damages can do. In this article, an approach for damage detection under changing temperatures is presentedand applied to a beam structure. The used stochastic subspace-based algorithm relies on a reference null space estimate, which is confronted to data from the testing state in a residual function. For damage detection the residual is evaluated by means of statistical hypothesis tests. Changes of the system due to temperature effects are handled with a model interpolation approach from linear parameter varying system theory. From vibration data measured in the undamaged state at some few reference temperatures, a model of the dynamic system valid for the current testing temperature is interpolated. The reference null space and the covariance matrix for the hypothesis test is computed from this interpolated model. This approach has been developed recently and was validated in an academic test case on simulations of a mass-spring-damper. In this paper, the approach is validated experimentally on a beam structure under varying temperature conditions in a climate chamber. Compared to other approaches, the interpolation approach leads to significantly less false positive alarms in the reference state when the structure is exposed to different temperatures, while faults can still be detected reliably. T2 - 10th International Conference on Structural Health Monitoring of Intelligent Infrastructure, SHMII 10 CY - Online meeting DA - 30.06.2021 KW - Damage detection KW - Subspace methods KW - Temperature effects KW - Model interpolation KW - Climate chamber KW - Laboratory beam structure PY - 2021 SP - 1 EP - 6 AN - OPUS4-52999 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bühling, Benjamin A1 - Schweitzer, T. A1 - Maack, Stefan A1 - Strangfeld, Christoph T1 - Influence of operating conditions on the fluidic ultrasonic transducer signal N2 - While contact and immersion ultrasonic testing are established methods in non-destructive testing (NDT), generating high power air-coupled ultrasound remains a challenging task. Solutions often involve setups that are restricted to lab environments. When field measurements are required, such as in NDT for civil engineering, a handy, robust and safe transducer is needed. For this purpose, an ultrasonic transducer based on a fluidic switch has been developed. A sonic air flow inside the device is switched rapidly so that an ultrasonic signal is generated. Both theory and previous flow simulations suggest that the control flow pressure ramp has only little influence on the switching time of the device. This publication gives an overview over the operating principle of the fluidic ultrasonic transducer and investigates the influence of control tube length and pulsing repetition rate on the ultrasonic pressure amplitude. High repetition rates are found to reduce the signal amplitude, whereas long tubing has only little negative influence on the amplitude while improving signal quality. T2 - 47. Jahrestagung für Akustik (DAGA 2021) CY - Vienna, Austria DA - 15.08.2021 KW - Ultrasound KW - Non-destructive testing KW - Fluidic devices PY - 2021 UR - https://pub.dega-akustik.de/DAGA_2021 SN - 978-3-939296-18-8 SP - 48 EP - 51 CY - Berlin, Germany AN - OPUS4-53493 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Frei, Vivian A1 - Pirskawetz, Stephan A1 - Thiele, Marc A1 - Rogge, Andreas T1 - Experimental investigation of size effect on fatigue behavior of high strength concrete - concept and preliminary results N2 - The worldwide spread of windfarms brings new challenges, especially for concrete structures as a part of towers, connecting joints and foundations of wind turbines. High-cyclic loadings in such structures lead to a high relevance of the subject of fatigue. A proper assessment of the fatigue strength of concrete demands therefore a basis of reliable experimental data and the development of standardized testing methods. This article presents first results of an ongoing research program of BAM (Bundesanstalt für Materialforschung und -prüfung) which is a part of a joint project (WinConFat) funded by the German Federal Ministry for Economic Affairs and Energy. The subproject investigates the effects of size and slenderness of the specimens on the fatigue behaviour of high strength concrete at different stress levels. Not only the fatigue strength, but also the fatigue process itself is monitored by means of several measurement methods. Strain measurements are used to calculate the load dependent elastic modulus in the fatigue hysteresis as indicators for fatigue development. Furthermore, the application of non-destructive methods like acoustic emission analysis and ultrasonic measurement in laboratory tests gives a deeper insight into damage processes under cyclic loading. The results shall be used to improve design rules for concrete members under fatigue load and to develop or improve non-destructive techniques for in-service structural health monitoring. T2 - 5th International fib Congress: Better - Smarter - Stronger CY - Melbourne, Australia DA - 08.10.2018 KW - Acoustic emission testing KW - Compressive cyclic loading KW - Fatigue KW - High-strength concrete KW - Non-destructive testing KW - Size effect KW - Slenderness effect KW - Ultrasonic testing PY - 2018 SN - 978-1-877040-14-6 SP - 1 EP - 11 AN - OPUS4-46408 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simon, Patrick A1 - Schneider, Ronald A1 - Baeßler, Matthias A1 - Recknagel, Christoph ED - Cunha, Á. ED - Caetano, E. T1 - Enhancing structural models with material tests and static response data - a case study considering a steel beam with asphalt layer subject to temperature variations N2 - Gradual or sudden changes in the state of structural systems caused, for example, by deterioration or accidental load events can influence their load-bearing capacity. Structural changes can be inferred from static and/or dynamic response data measured by structural health monitoring systems. However, they may be masked by variations in the structural response due to varying environmental conditions. Particularly, the interaction of nominally load-bearing components with nominally non-load bearing components exhibiting characteristics that vary as a function of the environmental conditions can significantly affect the monitored structural response. Ignoring these effects may hamper an inference of structural changes from the monitoring data. To address this issue, we adopt a probabilistic model-based framework as a basis for developing digital twins of structural systems that enable a prediction of the structural behavior under varying ambient condition. Within this framework, different types of data obtained from real the structural system can be applied to update the digital twin of the structural system using Bayesian methods and thus enhance predictions of the structural behavior. In this contribution, we implement the framework to develop a digital twin of a simply supported steel beam with an asphalt layer. It is formulated such that it can predict the static response of the beam in function of its temperature. In a climate chamber, the beam was subject to varying temperatures and its static response wass monitored. In addition, tests are performed to determine the temperature-dependent properties of the asphalt material. Bayesian system identification is applied to enhance the predictive capabilities of the digital twin based on the observed data. T2 - International Conference on Structural Health Monitoring of Intelligent Infrastructure (SHMII-10) CY - Online meeting DA - 30.06.2021 KW - Digital twin KW - Structural health monitoring KW - Material tests KW - Bayesian updating PY - 2021 SN - 2564-3738 SP - 1537 EP - 1544 AN - OPUS4-54126 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Viefhues, Eva A1 - Döhler, M. A1 - Hille, Falk A1 - Mevel, L. ED - Simani, S. ED - Patan, K. T1 - Asymptotic analysis of subspace-based data-driven residual for fault detection with uncertain reference N2 - The local asymptotic approach is promising for vibration-based fault diagnosis when associated to a subspace-based residual function and efficient hypothesis testing tools. It has the ability of detecting small changes in some chosen system parameters. In the residual function,the left null space of the observability matrix associated to a reference model is confronted to the Hankel matrix of output covariances estimated from test data. When this left null space is not perfectly known from a model, it should be replaced by an estimate from data to avoid model errors in the residual computation. In this paper, the asymptotic distribution of the resulting data-driven residual is analyzed and its covariance is estimated, which includes also the covariance related to the reference null space estimate. The advantages of the data-driven residual are demonstrated in a numerical study, and the importance of including the covariance of the reference null space estimate is shown, which increases the detection Performance. T2 - 10th IFAC Symposium on Fault Detection, Supervision and Safety for Technical Processes SAFEPROCESS 2018 CY - Warsaw, Poland DA - 29.08.2018 KW - Subspace-based method KW - Fault detection KW - Uncertainty in reference KW - Residual evaluation KW - Statistical tests KW - Vibration measurements PY - 2018 DO - https://doi.org/10.1016/j.ifacol.2018.09.610 SN - 2405-8963 VL - 51 IS - 24 SP - 414 EP - 419 PB - Elsevier AN - OPUS4-46303 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kowitz, Astrid A1 - Wu, Cheng-Chieh A1 - Hille, Falk A1 - Helmerich, Rosemarie A1 - Kadoke, Daniel A1 - Gründer, Klaus-Peter A1 - Hauser, S. A1 - Schwarzinger, H. ED - Pastramă, Ş. D. ED - Constantinescu, D. M. T1 - Impact on a micro-reinforced UHPC: Experimental studies versus numerical modeling N2 - Within the presented research project, experimental and numerical investigations were performed to develop a thin-shelled, modular, mobile element system made of a micro-reinforced ultra-high-performance ductile concrete (DUCON®). Material parameters were experimentally determined to adapt the material model within the numerical analysis applying the Drucker-Prager relationship. Afterwards, for validation of the numerical models, quasi-static and high-velocity impact tests were performed on plate-like structures. Finally, a suitable geometry of transportable barrier elements will be designed, which provides a maximum of resistance against impact by a minimum of weight and a maximum of mobility. T2 - 35th Danubia-Adria Symposium on Advances in Experimental Mechanics CY - Sinaia, Romania DA - 25.09.2018 KW - E-modulus KW - Impact KW - UHPC KW - DUCON® KW - Quasi-static and dynamic tests KW - Micro-reinforcement KW - Ductility KW - Mobile elements KW - Numerical modeling KW - Stereo photogrammetry KW - Compressive strength PY - 2018 UR - https://www.das2018.ro/ SN - 978-606-23-0874-2 SP - 11 EP - 12 PB - Editura Printech CY - Bucarest, Romania AN - OPUS4-47001 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Thieme-Hack, M. A1 - Berghaus, U. A1 - Brümmer, F. A1 - Elsner, U. A1 - Färber, C. A1 - Frank, D. A1 - Illgas, M. A1 - Kalbe, Ute A1 - Kathage, J. A1 - Leers, A. A1 - Müller, B. A1 - Röger-Göpfert, C. A1 - Russland, H.-J. A1 - Schnabel, B. A1 - Schneider, O. A1 - Schockmann, D. A1 - Schomakers, H. A1 - Schwalbe, D. A1 - Stegemann, D. A1 - van den Berg, T. A1 - Kramps, S. T1 - Fachbericht Kunststoffsportböden - Nachhaltige Kunststoffbelagsauswahl für Sportfreianlagen N2 - Kunststoff- und Kunststoffrasenflächen kommt bei intensiv genutzten Flächen als Allwetterbeläge eine große Bedeutung zu. Sie leisten einen wichtigen Beitrag zur Absicherung eines ganzjähriger Sportangebote. Gerade Kunststoffrasen ist aber in den letzten Jahren häufig in die Kritik geraten, insbesondere durch gefährliche Inhaltsstoffe und andere negative Einflüsse auf die Umwelt. Dies hat bei Bauherren zu einer Verunsicherung geführt und Fragen aufgeworfen, die erst teilweise beantwortet sind. Die Diskussionen rund um diesen Allwetterbelag haben bereits dazu geführt, dass von Seiten der Industrie viel verändert wurde und neue innovative Lösungen gefunden werden. Der Fachbericht stellt eine Handreichung für Fachleute und interessierte Laien dar, um mehr Klarheit besonders hinsichtlich der Umweltanforderungen zu erzielen. KW - Kunststoffsportbeläge KW - Kunstrasen KW - Umweltverträglichkeit KW - Schadstofftransfer KW - Mikroplastik PY - 2022 UR - https://shop.fll.de/de/fachbericht-kunststoffsportboeden-broschuere.html SP - 1 EP - 70 PB - Forschungsgesellschaft Landschaftsentwicklung Landschaftsbau (FLL) CY - Bonn AN - OPUS4-54390 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nietzke, Jonathan A1 - Rhode, Michael A1 - Mente, Tobias A1 - Kannengießer, Thomas T1 - Experimental and numerical characterization of hydrogen diffusion in thick-walled submerged arc welded joint of S420G2+M offshore steel grade N2 - Offshore wind turbines are an important goal in national energy strategies worldwide. Foundation structures are manufactured from submerged arc welded (SAW) plates with thicknesses up to 200 mm. In that connection, high-strength steels like the S420G2+M are more and more applied offering the possibility for increased stability and load-bearing capacity of the foundations. These offshore steel grades can show a susceptibility for delayed hydrogen assisted cold cracking of the weld joints. For that purpose, a minimum waiting time (MWT) of up to 48 h (dependent on applied standards) is recommended before non-destructive testing is allowed and conducted. But this concept is based on older steel grades that have been used for three or more decades. Nowadays, the metallurgical improvements (clean steels, proper rolling, and heat treatment) of base materials and well as welding consumables must be anticipated. Hence, the MWT concept should be critically discussed as it is assumed to be very conservative. For that reason, the focus of this study was to investigate the diffusion behavior in S420G2+M steel and its multi-layer SAW joint. Electrochemical permeation experiments were carried at room temperature. Boundary conditions were anticipated in terms of using different sample thicknesses. From the experimental data, hydrogen diffusion coefficients and absorbed diffusible hydrogen concentrations had been calculated. It was shown that hydrogen diffusion in the base material is increased compared to the weld metal. In addition, the sample thickness had a significant on the calculated diffusion coefficients. The minimum and maximum diffusion coefficients had been used for numerical modelling of the hydrogen diffusion in the welding joint. It became clear that a MWT must be always regarded together with a critical initial diffusible hydrogen concentration for the evaluation of a possible delayed cracking as diffusion times were mostly > 48 h due to the thick plates. T2 - 4th International Conference on Metals and Hydrogen - Steely & Hydrogen 2022 CY - Ghent, Belgium DA - 11.10.2022 KW - Hydrogen KW - Submerged arc welding KW - Diffusion KW - Minimum waiting time KW - Electrochemical permeation PY - 2022 SP - 1 EP - 11 CY - Ghent, Belgium AN - OPUS4-56075 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Nina A1 - Rhode, Michael A1 - Kannengießer, Thomas T1 - Experimentelle Bestimmung und thermodynamische Modellierung des Ausscheidungsverhaltens in der WEZ eines S690QL bei unterschiedlichen Mikrolegierungsrouten N2 - Für eine signifikante Festigkeitssteigerung von vergüteten, hochfesten Feinkornbaustählen mit einer Normstreckgrenze > 690 MPa, ist die Zugabe von Mikrolegierungselementen, wie Nb und Ti, unerlässlich. Die Normvorgaben zur chemischen Zusammensetzung dieser Stähle (bspw. in DIN EN 10025-6) geben zur Erzielung der vorgeschriebenen Eigenschaften dabei oft nur Grenzgehalte für die Hersteller vor. Die Wirkung der Legierungselemente bzw. ihrer Karbide und/oder Nitride ist teilweise komplett konträr, insbesondere bei Auflösung und Wiederausscheidung in der WEZ bei identischem Schweißzusatz. Somit wird eine adäquate Vorhersage der Chargenabhängigkeit hinsichtlich der Schweißeignung und des Tragverhaltens der Schweißverbindung erschwert. Zuzüglich können moderne Schweißprozesse, wie MSG mit modifiziertem Sprühlichtbogen (mod. SLB) durch ihre hohe Wärmeeinwirkung die Phasenumwandlung in der Wärmeeinflusszone negativ beeinflussen. Eine unerwünschte Eigenschaft ist dabei die Erweichung (engl.: softening) der WEZ, wie auch u.U. der gegenteilige Effekt der Aufhärtung (engl.: hardening). Vor diesem Hintergrund werden im Rahmen eines DFG-Vorhabens systematisch Mikrolegierungsrouten mit variierenden Ti- und Nb-Gehalten des hochfesten und vergüteten Feinkornbaustahls S690QL untersucht. Dazu wird das MAGSchweißen mit mod. SLB verwendet, welches durch hohe Abschmelzleistung gekennzeichnet ist und schmalere Fugenöffnungswinkel (α = 30°) ermöglicht. An diesen Schweißungen wird der Effekt der metallurgischen Zusammensetzung in Kombination mit hoher Wärmeeinwirkung auf die Ausbildung einer kritischen WEZ-Gefügezone mit Erweichung und/oder exzessiver Aufhärtung untersucht. Ein besonderes Augenmerk wird auf die Phasenumwandlungen und das Ausscheidungsverhalten im Gefüge der Wärmeeinflusszone gelegt. Neben umfangreichen metallographischen Untersuchungen einzelner WEZ-Bereiche wurden, unter Variation der chemischen Zusammensetzung, thermodynamische Phasenberechnungen mittels ThermoCalc durchgeführt. Hierdurch wird ein Verständnis zur Phasentransformation und Ausscheidungswachstum und -auflösung während des Schweißens in Abhängigkeit von Temperatur und Abkühlbedingungen geschaffen. Das Ziel ist es, mittels erster Untersuchungen den Einfluss der Wärmeeinwirkung auf die Gefügeausbildung in der WEZ zu zeigen. Insbesondere wird hier auf die Auswirkung der unterschiedlichen Mikrolegierungskonzepte (Ti oder Nb) geachtet. T2 - DVS CONGRESS 2022 - Große Schweißtechnische Tagung CY - Koblenz, Germany DA - 19.09.2022 KW - WEZ-Erweichung KW - Hochfester Feinkornbaustahl KW - ThermoCalc KW - Thermodynamische Simulation KW - Mikrolegierungselemente KW - Modifizierter Sprühlichtbogen PY - 2022 SN - 978-3-96144-189-1 SN - 978-3-96144-190-7 VL - 382 SP - 131 EP - 137 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-55834 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quackatz, Lukas A1 - Griesche, Axel A1 - Kannengießer, Thomas A1 - Treutler, K. A1 - Gehling, T. A1 - Eissel, A. A1 - Wesling, V. T1 - In situ Messung der chemischen Konzentration in der Schmelze während des WIG-Schweißens von Duplexstählen N2 - Duplexstähle besitzen ein zweiphasiges Gefüge und werden aufgrund ihrer verbesserten Schweißeignung gegenüber den Vollausteniten häufig im Anlagen- bzw. Apparatebau eingesetzt. Aufgrund der hohen Abkühlgeschwindigkeit und dem Abbrand von Legierungselementen kommt es zu einer Ferritisierung des Schweißguts und damit zu einer Degradation der mechanischen Eigenschaften. Zur Vorhersage des Phasenverhältnisses im Schweißgut wird das WRC1992-Diagramm genutzt. Dieses Diagramm zeigt einige Ungenauigkeiten und benötigt zur genaueren Vorhersage der Phasenverhältnisse eine Überarbeitung. Um den Einfluss einzelner Elemente auf das Schweißnahtmikrogefüge besser zu verstehen, wurden drahtförmige Schweißzusatzwerkstoffe mit dem Ferrit-Bildner Nb und dem Austenit-Bildner Cu beschichtet und für Schweißungen verwendet. Die Messmethode der Laser-induzierten Plasmaspektroskopie (LIBS) bietet hier eine gute Möglichkeit der in situ Überwachung der chemischen Konzentrationen, während des WIG-Schweißens von Duplexstählen. Die LIBS-Messergebnisse, konnten mit der Ferritnummer und der Schweißnahtmikrostruktur korreliert werden. T2 - Symposium Materialtechnik der TU Clausthal CY - Clausthal-Zellerfeld, Germany DA - 23.02.2023 KW - LIBS KW - In situ measurement KW - WRC 1992 diagram KW - Dduplex stainless steel KW - TIG welding PY - 2023 VL - 12 SP - 612 EP - 627 PB - Shaker CY - Aachen AN - OPUS4-57991 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quercetti, Thomas A1 - Wille, Frank A1 - Neumann, Martin A1 - Linnemann, Konrad T1 - Full-scale drop testing with a heavy-weight package for radioactive waste N2 - Packages for the transport of radioactive materials shall fulfil the requirements of the IAEA regulations for the safe transport. The requirements define mechanical and thermal test conditions including criteria ensuring the package design’s ability to withstand severe accidents and provide a high level of technical safety. Different methods can be used for safety demonstration showing compliance with the regulations. The central part of a safety demonstration which is presented in this paper was a comprehensive drop test program with a full-scale model of a transport package accompanied by pre- and post-test FE analyses. Using full-scale drop test models allow the benefit that similarity and scaling issues become a significant smaller issue, additional material investigations can be limited and analyses for transferring test results to the original package design are reduced. Additionally, experience for the future serial packaging manufacturing and handling procedures can be collected in a very early state of the design approval process. The pre-test finite element analyses derived and justified the drop test program consisting of several drop sequences with different drop orientations of the specimen. The performance and the results of the drop test sequences shows the manageability and the advantage e.g., in view of the direct availability of test results for the package licensing. On the other hand, the drop test performance shows the difficulties during handling and the need for additional equipment during preparation of the specimen. The package presented was intended for the transport and storage of compacted radioactive waste from reprocessing of spent nuclear fuel assemblies - designed and applied for approval by the AGC consortium. The project ended in 2021. The package design was characterized by a cask body made of a forged thick stainless-steel shell, a bolted double lid system with metallic gaskets and wood filled shock absorbers at both ends. The total mass of the entire transport package including content was 120,000 kg, the total length was about 7000 mm and the diameter approximately 3000 mm, both measures include the shock absorbers. The paper provides an insight into the performance of a full-scale drop testing campaign within the package safety evaluation and shows some selected test results. T2 - 20th International Symposium on the Packaging and Transportation of Radioactive Materials (PATRAM 22) CY - Juan-Les-Pins, France DA - 11.06.2023 KW - Full-scale KW - Drop testing KW - Package KW - Radioactive materials transport PY - 2023 SP - 1 EP - 10 AN - OPUS4-57732 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schubert, Sven A1 - Reichardt, Adrian A1 - Müller, Lars A1 - Neumann, Martin A1 - Komann, Steffen A1 - Wille, Frank T1 - Introduction of the German ageing management guide for packages for transport of radioactive materials N2 - The consideration of ageing mechanisms is with integration of the new para 613A into IAEA SSR-6 (Rev. 1) now obligatory for the design of transport packages. In addition, para 809(f) requires for packages intended to be used for shipment after storage the consideration of the effects of ageing mechanisms during storage in safety analyses and the implementation of corresponding instructions for operation and maintenance. Para 503(e) requires that all packaging components and radioactive contents have been maintained during storage in a manner that all requirements specified in IAEA SSR-6 (Rev.1) and in the applicable certificates of approval have been fulfilled. The evaluation of ageing mechanisms and their effects including monitoring are part of BAM’s authority assessment tasks related to the mechanical and thermal package design and quality assurance aspects. BAM has compiled a guideline for the implementation of ageing assessment and of the measures for ageing management of the approval procedure based on requirements of IAEA SSR-6 (Rev.1). The guideline is applicable only for packages requiring a competent authority approval. The paper aims to describe the structure of the guideline and the general approach for ageing management requirements. The type and amount of measures for ageing management depend mainly on the use of the package and on the ageing effects for the component, which result from relevant ageing mechanisms during package operation time. The implementation of measures for ageing management is divided into three levels – systemic measures, package design related measures and documentation. The systemic measures are attributed to the general management system and define the whole activities for organization of ageing management like structure, responsibilities, documentation, reports and evaluation. The package design related measures are defined in an ageing management plan (AMP). These measures shall ensure that the anticipated changes of the package design under consideration of ageing effects still complies with the design approval specification. Therefore, an ageing surveillance program (ASP) and, if necessary, a gap analysis program shall be developed. The ageing management documentation (AMD) ensures the continuous documentation of the compliance of a specific package to the approved package design, comprising mainly records resulting from operation and surveillance. T2 - PATRAM22 - 20th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Juan-les-Pins, France DA - 11.06.2023 KW - Guide KW - Ageing KW - Mechanism KW - Package KW - Management PY - 2023 SP - 1 EP - 10 PB - World Nuclear Transport Institute (WNTI) CY - London AN - OPUS4-57770 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Martin A1 - Quercetti, Thomas A1 - Wille, Frank A1 - Gröke, Carsten A1 - Neumeyer, Tino T1 - Design assessment, approval of management systems and ageing aspects of transport packages for radioactive material not requiring competent authority approval of design N2 - Most transports of radioactive materials are carried out with packages not requiring competent authority approval of design. These encompass – in accordance with the IAEA SSR-6 regulations – packages of the classification excepted, Industrial packages Type 1, 2 and 3 and Type A packages. Currently an upsurge in number and variation of these package designs can be seen in Germany, resulting from the phase out of nuclear energy in Germany as well as e. g. increased use of radioactive material for medical purposes. A design assessment regarding the package safety is required in the international IAEA SSR-6 regulations. BAM operates facilities for the performance of all regulatory tests required such as drop towers for a wide range of package masses and dimensions, fire test, leak tightness measurements and pressure test facilities. Experiences with several package types are shown. Additionally, IAEA SSR-6 requires the establishment of a management system for design, manufacture, maintenance, and repair of the packaging as well as for the preparation, consigning, loading, carriage, unloading and receipt of the package. Relevant for Germany, BAM has published guidance material on the process of management system acceptance in the technical guide BAM-GGR 016. The requirements encompass quality management plans for the manufacturing of packages including independent manufacturing surveillance and specific instructions for operation, maintenance, and repair of packagings. Examples for management system specifics and requirements are given. Since the latest edition of the IAEA SSR-6 regulations an ageing evaluation including systematic ageing management measures are required for all kind of package types. BAM is going to update the guidance material BAM-GGR 016 to support the stakeholders with relevant information to fulfil the ageing aspect for packages not requiring competent authority approval. The paper explains how the ageing aspect may be included in the safety evaluation process and the management system measures and will give an outlook for the future guidance material. T2 - 20th International Symposium on the Packaging and Transportation of Radioactive Materials (PATRAM 22) CY - Juan-Les-Pins, Antibes, France DA - 11.06.2023 KW - Typ KW - Radioactive material KW - Non-approved PY - 2023 SP - 1 EP - 8 AN - OPUS4-57703 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schilling, Richard A1 - Oehrl, A. A1 - Wischerhoff, E. A1 - Schukar, Marcus T1 - A fibre optic temperature sensor based on thermoresponsive polymer N2 - We present a temperature sensor based on a polymer exhibiting a Lower Critical Solution Temperature (LCST) in aqueous solution encapsulated in a capillary. Parameters are chosen such that the solution exhibits a cloud point in a temperature range of 30° C to 39°C. The characteristic of thermoresponsive polymers with an LCST, is that above that temperature phase separation of the polymer takes place which leads to a temperature-dependent formation of a cloudy suspension. An optical intensity measurement over the desired temperature range is established by an increase of optical attenuation inside the polymer solution caused by a rising temperature. For our purpose, the polymer capillary is connected to transmitter and receiver via a Polymer Optical Fibre (POF). Our intensity measurement is, to the best of our knowledge, a novel method and can be considered simple when compared to existing fibre-based temperature measurement techniques. Due to the lack of electrical components at the probe, this sensor is suitable for measurements in strong electromagnetic fields and environments for which flying sparks are hazardous, i.e., inflammable fluids or gases. Furthermore, all manufactured sensors share the same temperature dependence and, therefore, are well-suited for comparative measurement, e.g., flow measurement systems. With the given temperature range, a body temperature measurement is also suitable. T2 - European Workshop on Optical Fibre Sensors (EWOFS 2023) CY - Mons, Belgium DA - 23.05.2023 KW - Thermoresponsive polymer KW - Aqueous polymer solution KW - Temperature sensor KW - LCST KW - POF PY - 2023 DO - https://doi.org/https://doi.org/10.1117/12.2678418 SP - 12643-69 PB - SPIE CY - Bellingham, Wash. AN - OPUS4-57735 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Seifert, Lando A1 - Müller, Thoralf A1 - Ebell, Gino ED - Pillai, Radhakrishna G. T1 - Development of a new test method for assessing the susceptibility of prestressing steels to hydrogen-induced stress corrosion cracking N2 - For prestressing steel’s factory production control, approvals, and continuous surveillance in Germany, a susceptibility test against hydrogen-induced stress corrosion cracking is performed. The measured time to fracture results (in hours) must be reproducible and reliable in the test. ISO 15630-3 gives currently unpersuasive and diverging results using a free corrosion approach for hydrogen charging. A newly developed test method uses cathodic polarization for defined hydrogen charging instead of an uncontrolled and variable electron supply by metal dissolution during free corrosion. With this new test method, a reliable differentiation is possible between highly susceptible-known “old-type” quenched and tempered prestressing steel, i.e., Neptun, Hennigsdorfer, Sigma, and currently approved cold-drawn wires St 1470/1670 (CDS-1670) and St 1570/1770 (CDS-1770). The reproducibility of the new test method was evaluated in a round-robin test with eight attended testing institutes on a St 1470/1670 (CDS-1670) batch. T2 - Conference CONSEC24 CY - Chennai, India DA - 25.09.2024 KW - Hydrogen charging KW - ISO 15630-3 KW - Prestressing steels KW - Round-robin KW - Stress corrosion cracking PY - 2024 UR - https://consec24.com/# SP - 1 EP - 8 PB - Indian Institute of Technology (IIT) Madras, Centre of Excellence on Technologies for Low Carbon & Lean Construction CY - Chennai, India AN - OPUS4-61163 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Karapanagiotis, Christos A1 - Schukar, Marcus A1 - Breithaupt, Mathias A1 - Krebber, Katerina T1 - Monitoring of composite pressure vessels using surface applied distributed fiber optic sensors N2 - In this paper, we report on surface-applied distributed fibre optic sensors for monitoring composite pressure vessels designed for hydrogen storage. Previous reports have revealed that integrating optical fibres within vessel composite structures effectively enables the monitoring of structural behavior throughout their lifetime. However, integrating optical fibres during the manufacturing process is complex and time-consuming. Therefore, we aim to simplify this process by attaching the optical fibres to the vessel’s surface. This method is significantly more timeefficient than the integration process and can be applied to any vessel. Our results demonstrate that surface-applied fibre optic sensors can detect and precisely localise damage. Additionally, signs of damage can be recognised even before the damage occurs. Predictive maintenance using fibre optic sensors could reduce premature maintenance costs and periodic inspections while increasing safety and extending the vessel’s useful service life. The role of machine learning in predictive maintenance is also discussed. T2 - 20th Sensors & their Applications Conference CY - Limerick, Ireland DA - 11.08.2024 KW - Hydrogen KW - Fiber optic sensors KW - Composites KW - Machine learning KW - Structural health monitoring PY - 2024 SP - 1 EP - 4 AN - OPUS4-60911 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino A1 - Müller, Thoralf A1 - Burkert, Andreas ED - G. Pillai, R. T1 - Stress Corrosion Cracking in Prestressed Concrete Bridge – A Case Study N2 - Bridge structures built using the prestressing block method can exhibit hydrogen-induced stress cracks across the entire cross-section of a prestressing channel due to their design. Crack growth can progress over the service life as a result of dynamic loading and lead to prestressing wire fractures. T2 - Consec 2024 CY - Chennai, India DA - 25.09.2024 KW - Corrosion KW - Spannungsrisskorrosion KW - Stress corrosion cracking KW - Hydrogen KW - Spannstahl PY - 2024 SP - 72 EP - 78 CY - Chennai AN - OPUS4-61330 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Burkert, Andreas A1 - Müller, Thoralf A1 - Lehmann, Jens T1 - Langzeitkorrosionsverhalten nichtrostender Stähle in maritimer Atmosphäre N2 - Durch Fortführung der Untersuchungen aus einem Forschungsvorhaben wurden neun verschiedene Stahllegierungen unter maritimen Umgebungsbedingungen über fünf Jahre ausgelagert und deren Korrosionsverhalten untereinander verglichen und bewertet. Die parallele Untersuchung von vier verschiedenen 0berflächenausführungen der jeweiligen Legierungen ermöglichte zudem branchenspezifische Besonderheiten der Oberflächenausführung beim Werkstoffvergleich zu berücksichtigen. Anhand der Ergebnisse der Auslagerungsprüfungen konnten Rückschlüsse auf die Einflüsse der Legierungszusammensetzung, der 0berfächenausführung und der Auslagerungszeit unter maritimen Auslagerungsbedingungen gewonnen werden. Die Proben der drei untersuchten Duplexwerkstoffe zeigten über den Auslagerungszeitraum von fünf Jahren sowohl mit als auch ohne Spaltgeometrie die beste Korrosionsbeständigkeit. Ebenso konnte der molybdänlegierte Ferrit 1.4521 eine vergleichbar gute Korrosonsbeständigkeit erzielen, wie die klassischen austenitischen Werkstoffe 1.4301 und 1.4404. T2 - Korrosionsschutz in der maritimen Technik CY - Hamburg, Germany DA - 25.01.2017 KW - Korrosionsschutz KW - Nichtrostende Stähle KW - Auslagerungsversuche PY - 2017 SN - 978-3-935406-64-2 SP - 7 EP - 20 AN - OPUS4-39054 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Burkert, Andreas A1 - Müller, Thoralf A1 - Modersohn, W. A1 - Busch, W.-B. T1 - Innovation und Sicherheit im Bauwesen durch Einsatz von Duplexstahl N2 - Der Einsatz von nichtrostenden Duplexstählen im Bauwesen findet in den letzten Jahren zu-nehmende Verbreitung. Insbesondere die Lean-Duplexstähle sind aufgrund geringerer not-wendiger Legierungszuschläge von Nickel und Molybdän eine kostengünstigere Alternative zu den jahrzehntelang etablierten austenitischen Stahlsorten. Verschiedene Korrosionsuntersu-chungen an der BAM sowie Erfahrungen aus der Anwendung konnten nachweisen, dass Lean-Duplexstähle unter verschiedenen Einsatzbedingungen ein vergleichbar gutes, in man-chen Fällen sogar besseres Korrosionsverhalten aufweisen als austenitische Referenzwerkstoffe der gleichen Korrosionswiderstandsklasse. Im Hinblick auf die technisch-mechanischen Eigenschaften konnten von der Fa. Modersohn initiierte Untersuchungen zeigen, dass unter Beachtung der gefügebedingten Einsatzgrenzen eine gute Verarbeitbarkeit und mechanische Sicherheit bei gleichzeitiger Materialeinsparung gewährleistet werden kann. Die positiven Ver-suchsergebnisse haben wesentlich zur Akzeptanz und einer damit einhergehenden Erweiterung der Einsatzgebiete dieser alternativen Werkstoffe im Bauwesen beigetragen. T2 - GfKorr-Jahrestagung 2016 CY - Frankfurt/Main, Germany DA - 15.11.2016 KW - Duplexstähle KW - Bauwesen KW - Korrosionsbeständigkeit KW - Kerbschlagzähigkeit PY - 2016 SN - 978-3-935406-63-5 VL - 2016 SP - 82 EP - 95 PB - DECHEMA e.V. CY - Frankfurt/Main AN - OPUS4-38663 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stajanca, Pavol A1 - Woyessa, G. A1 - Schukar, Marcus A1 - Bang, O. A1 - Krebber, Katerina T1 - Response of microstructured plastic optical fiber Bragg grating to gamma radiation N2 - Response of PMMA-based plastic optical fiber Bragg grating (FBG) to gamma radiation is investigated for the first time. FBG wavelength shift as large as 150 pm is observed for irradiation to 18 kGy. T2 - 5th Workshop on specialty optical fibers and their applications CY - Limassol, Cyprus DA - 11.10.2017 KW - Fiber Bragg gratings KW - Optical sensing and sensors KW - Plastic optical fibers KW - Gamma radiation PY - 2017 SP - Poster 19, 1 EP - 2 AN - OPUS4-42586 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hering, Marcus A1 - Agasty, Amit A1 - Costard, René A1 - Hüsken, Götz A1 - Chruscicki, Sebastian A1 - Hicke, Konstantin T1 - Explosion effects on reinforced concrete structures – A preliminary study of scaling laws N2 - Blast tests are required to investigate accidental or intentional blast events and to assess the level of protection for people and facilities in critical infrastructures. Conducting large-scale field tests for complex scenarios is very resource intensive. Reliable small-scale experiments are a promising alternative. However, the scaling laws for the design of reinforced concrete structures under blast loads are not sufficiently established. In our research work, a consortium made up of three BAM departments, focuses on reinforced concrete structures that are suitable for the standardization of scaled blast tests. As part of the feasibility study, blast tests were carried out on test specimens of different sizes on the BAM Test Site for Technical Safety (TTS). Various reinforced concrete plates were tested and subjected to different blast loads. The blast tests included various measurement techniques to quantify the blast load and the behavior of the reinforced concrete plate. The blast load was measured with flush-mounted piezoelectric pressure gauges, while accelerometers and embedded fiber optic sensor cables were used to characterize the dynamic behavior of the plate under blast loading. In addition, damage characteristics were also determined using distributed fiber optic sensing. The application of these measurement techniques as well as the use of different numerical software tools offer the possibility to verify or adapt the scaling laws. T2 - 19th International Symposium on Interaction of the Effects of Munitions with Structures (19th ISIEMS) CY - Bonn, Germany DA - 09.12.2024 KW - Scaling KW - Blast KW - Fiber optic sensing PY - 2024 SP - 1 EP - 9 AN - OPUS4-62258 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Wiehle, Philipp T1 - Einfluss der Feuchtigkeit auf das Tragverhalten von Lehmmauerwerk N2 - Im Mittelpunkt der vorliegenden Arbeit steht der Einfluss der Feuchte auf die mechanischen Eigenschaften von Lehmmauerwerk. Der Wissensstand zum feuchteabhängigen Tragverhalten von Lehm(mauerwerk) ist bisher lückenhaft, sodass keine explizite Berücksichtigung der Bauteilfeuchte bei der Bemessung tragender Konstruktionen erfolgt. Aktuelle und verlässliche Daten zum Einfluss der Feuchte auf die mechanischen Kenngrößen moderner Lehmbaustoffe fehlen bisher ebenso wie Messwerte in Bezug auf die Bauteilfeuchte unter natürlichen Klimabedingungen. Deswegen wurden im Rahmen dieser Arbeit umfangreiche Untersuchungen zum mechanischen und hygrothermischen Verhalten von Lehmmauerwerk durchgeführt. Die experimentellen Untersuchungen bestehen im Wesentlichen aus Druckversuchen an Lehmsteinen, -mörteln, kleinformatigen Lehmmauerwerksprobekörpern und geschosshohen Lehmmauerwerkswänden. Um das Feuchteverhalten beschreiben zu können, fanden außerdem erstmalig magnetresonanzspektroskopische Messungen an Lehmsteinen statt und es wurden die tatsächlich auftretenden Feuchtegehalte an einer Lehmmauerwerkswand unter natürlichen Klimabedingungen in Form von Langezeitmessungen ermittelt. Es konnte festgestellt werden, dass ein linearer Zusammenhang zwischen Druckfestigkeit und relativer Luftfeuchte besteht, wobei sich die Druckfestigkeit umgekehrt proportional zur relativen Luftfeuchte verhält. Je Prozent Steigerung der relativen Luftfeuchte kommt es zur Abnahme von einem Prozent der Druckfestigkeit. Gleiches gilt für das Elastizitätsmodul. Weiterhin konnte auf Basis der feuchtetechnischen Untersuchungen ein numerisches Modell zur Berechnung des instationären hygrothermischen Verhaltens für Lehmbaustoffe kalibriert werden. Anhand dieses Modells gelang es die bemessungsrelevanten Feuchtegehalte unter Berücksichtigung des instationären hygrothermischen Verhaltens realitätsnah zu berechnen. Die maximalen Feuchtegehalte im Lehmmauerwerk konnten somit in Form einer Parameterstudie in Abhängigkeit des Anwendungsfalls ermittelt werden, wodurch eine explizite Berücksichtigung des Feuchtegehaltes bei der Bemessung ermöglicht wurde. Die Verknüpfung der Erkenntnisse aus den mechanischen und hygrothermischen Untersuchungen dieser Arbeit bildet die Grundlage für das Bemessungskonzept der im Juni 2023 veröffentlichten DIN 18940: Tagendes Lehmsteinmauerwerk. KW - NMR KW - Lehm KW - Mauerwerk KW - Druckfestigkeit KW - Feuchtigkeit PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-637794 DO - https://doi.org/10.14279/depositonce-20800 SP - 1 EP - 114 CY - Berlin AN - OPUS4-63779 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Auersch, Lutz T1 - Mitigation measures for ballasted tracks - sleepers, sleeper pads and substructure - Results from the finite element boundary element method N2 - The ground vibrations, which are generated by trains on different tracks, have been calculated by finite-element boundary-element models. The ballasted track is modelled in detail by the finite element method. The infinite soil is modelled by the boundary element method as a homogeneous or layered half-space. The track-soil system is coupled with a simple rigid mass model of the vehicle so that the vehicle-track interaction is completely included. Transfer functions are calculated in frequency domain without and with vehicle-track interaction, the compliance of the track and the mobilities of the soil at different distances from the track. Finally, the ratios between the ground vibration amplitudes with and without mitigation measure are calculated to quantify the effectiveness of the mitigation measure. Tracks with under sleeper pads have been investigated in a wide parameter study. The main parameters that influence the reduction of ground vibration are the stiffness of the under sleeper pad, the mass and the width of the sleeper. The softest sleeper pad yields the best reduction of the ground vibration. The influence of the sleeper mass is not as strong as the characteristic frequency is ruled by the mass of the sleeper and the mass of the wheelset as well. The influence of other parameters has been examined. The stiffness of the rail pads, the bending stiffness of the track, the stiffness of the ballast, the sub-soil, and the soil, and the layering of the soil. All these parameters show no or only a minor influence on the mitigation effect. As the standard isolated track, a track with an under sleeper pad of a stiffness of kS = 5 107 N/m has been chosen, which can also be expressed as a stiffness per area of kS ’’ = 7.4 107 N/m3 = 0.074 N/mm3. The resonance frequency for this pad stiffness is observed between 32 and 40 Hz. The reduction of the ground vibration is about vi,I /vi,U = 0.2 and 0.1 at 100 Hz. The reduction can be improved by softer sleeper pads. But the compliance of the track gets higher than tolerable. A possibility to use softer sleeper pads without increasing the static compliance of the track is their combination with wide sleepers. The softer sleeper pads under wider sleepers yield the same compliance of the track and a better reduction of the ground vibration. KW - Heavy sleeper KW - Under sleeper pad KW - Finite-element boundary-element method KW - Mitigation KW - Ground vibration KW - Ballasted track PY - 2011 SP - 1 EP - 81 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-56607 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz T1 - Railway-induced ground and building vibrations – Analysis in frequency-wavenumber domain and fast prediction with approximate models N2 - A simple and fast prediction scheme is presented for train-induced ground and building vibrations. For the emission, finite-element boundary-element or multiple-beam-on-continuous-soil models of the track have been analysed and approximated by faster track-on-Winkler-soil models. The vehicle-track interaction due to irregularities yields the excitation forces. For the transmission of waves in the soil, the wavenumber integral of the compliance of layered soils has been evaluated. The calculation time is reduced for the prediction by using the solution of a homogeneous half-space with a frequency-dependent wave velocity (the dispersion) of the soil. For the immision, many 2 and 3-dimenisonal finite-element building models have been investigated, and a good approximation has been established by a 1-dimensional soil-wall-floor model. In addition, the axle sequence of the train, the quasi-static and the “scattered” response of the soil, and the wave propagation from a tunnel to a pile foundation of a building have been included. T2 - ISMA-Conference 2022 CY - Leuven, Belgium DA - 12.09.2022 KW - Ground vibration KW - Simple prediction KW - Vehicle-track interaction KW - Layered soil KW - Soil-building interaction KW - Soil-wall-floor model KW - Propagation from a tunnel KW - Tunnel-pile transfer PY - 2022 SP - 1 EP - 13 PB - KU Leuven CY - Leuven AN - OPUS4-56603 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Auersch, Lutz T1 - Mitigation measures for slab tracks - wide sleepers on soft pads and different slabs - Results from the finite element boundary element method N2 - The ground vibrations, which are generated by trains on different slab tracks, have been calculated by finite-element boundary-element models. The slab track is modelled in detail by the finite element method. The infinite soil is modelled by the boundary element method as a homogeneous half-space. The track-soil system is coupled with a simple rigid mass model of the vehicle so that the vehicle-track interaction is completely included. Transfer functions are calculated in frequency domain without and with vehicle-track interaction, the compliance of the track and the mobilities of the soil at different distances from the track. Finally, the ratios between the ground vibration amplitudes with and without mitigation measure are calculated to quantify the effectiveness of the mitigation measure. Tracks with under sleeper pads have been investigated in a parameter study. The main parameter that influences the reduction of ground vibration is the stiffness of the under sleeper pad. The softest sleeper pad yields the best reduction of the ground vibration. The influence of other parameters has been examined. The stiffness of the rail pads, the stiffness of the slab material, the stiffness of the sleeper material, and the distance of the sleepers. All these parameters show no or only a minor influence on the mitigation effect. As the standard isolated track, a track with an under sleeper pad of a stiffness of kS = 5 107 N/m has been chosen, which can also be expressed as a stiffness per area of kS ’’ = 3.7 107 N/m3 = 0.037 N/mm3. The resonance frequency for this pad stiffness is observed between 32 and 40 Hz. The reduction of the ground vibration is about vi,I /vi,U = 0.1 at 100 Hz. KW - Wide sleeper KW - Under sleeper pad KW - Finite-element boudnary-element method KW - Slab track KW - Mitigation KW - Ground vibration PY - 2012 SP - 1 EP - 50 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-56608 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz A1 - Said, Samir A1 - Rohrmann, R. T1 - Measurement and evaluation tools for ground and building vibrations from industrial pro-cesses, construction work, traffic and other sources N2 - Vibration measurements have many causes and many technical and natural sources. Problems can sometimes be solved by short-term measurements, but in many cases, a long-term measurement is necessary. In long-term measurements of days, weeks, months and even years, it is easy to collect a huge quantity of raw data, but at the end, the post-processing of these data can be exhausting (for example one-year vibration data of a wind energy tower). A software has been developed which con-sists of measuring and evaluation routines where the measuring routines can operate different meas-uring systems and different measuring cards. The main advantage of this software is the fact that the interesting evaluations can be integrated in the measuring process so that the characteristics of the vibration can be extracted without storing all the raw data. Only important time segments are stored, for example train passages. The overall concept of the software and the main evaluation routines will be described in some details. Examples of our measurement experience will illustrate the capabilities of the software. 1) Surveying construction work in nearby sensitive buildings (for example an old wind tunnel), including a stable alarm system and meaningful vibration limits. 2) Prediction of train-induced vibration for a planned building to prevent annoyance and to improve the building design. 3) Modal analysis and long term measurements of several single- or multi-span, concrete or steel bridges 4) Modal and wave analysis of coupled floors in a historical building (“Neues Palais” at Potsdam). 5) Soil properties of various measurement sites (different routines to evaluate the dispersion). Moreover, from many projects, amplitudes, frequencies, and attenuation laws have been collected and analysed for the different sources such as vibratory or impact pile driving and ground compaction, demolition work with different machines, blasting in quarries and in tunnel works, bomb and mine clearing. T2 - 28th International Congress on Sound and Vibration CY - Online meeting DA - 24.07.2022 KW - Ground vibration KW - Building vibration KW - Measurement KW - Evaluation KW - Modes KW - Waves PY - 2022 SP - 1 EP - 8 AN - OPUS4-56602 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz T1 - Effects of a varying track and soil stiffness on ground vibrations near railway lines N2 - Usually, geometric irregularities are considered as the main cause of ground vibrations from trains. A varying stiffness of the track, the track support and the soil can also generate ground vibrations. The regular stiffness variation of the track on and between the sleepers results in a deterministic dynamic axle load. The random stiffness variation of the track support yields also dynamic axle loads which are generated by the acceleration of the unsprung mass (from the varying wheel displacements under the static axle load). The random stiffness variation has a second effect. The pulses from the passage of the static axle loads are superposed regularly to the quasi-static response, but also irregularly to yield a “scattered” part of the axle pulses. The same holds for a random variation of the soil stiffness. All these effects of stiffness variations have been calculated by wavenumber-domain multi-beam track models, a random finite-element soil model and the superposition of axle impulses in a stochastic simulation. The results are confronted with many measurements at different sites. It is concluded that the stiffness variation of the track and the soil generate an important ground vibration component near railway lines. T2 - International Conference Railways 2022 CY - Montpellier, France DA - 22.08.2022 KW - Ground vibration KW - Axle loads KW - Irregularities KW - Varying stiffness PY - 2022 SP - 1 EP - 11 AN - OPUS4-56605 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mair, Georg W. A1 - Becker, Ben T1 - Monte-Carlo-analysis of minimum load cycle requirements for composite cylinders for hydrogen N2 - Existing regulations and standards for the approval of composite cylinders in hydrogen service are currently based on deterministic criteria (ISO 11119-3, UN GTR No. 13). This paper provides a systematic analysis of the load cycle properties resulting from these regulations and standards. Their characteristics are compared with the probabilistic approach of the BAM. Based on Monte-Carlo simulations the available design range of all concepts is compared. In addition, the probability of acceptance for potentially unsafe design types is determined. T2 - ICHS 2017 CY - Hamburg, Germany DA - 11.09.2017 KW - Monte-Carlo KW - Hydrogen KW - Regulations KW - Probabilitic approach PY - 2017 SP - ID 202, 1 EP - 11 PB - HySafe CY - Hamburg AN - OPUS4-41944 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - John, Sebastian A1 - Mair, Georg W. T1 - Sensitivity analysis of residual stresses in composite pressure vessels via modal analysis N2 - Due to high specific stiffness a nd strength properties, fibre reinforced plastics are used more and more often for the construction of pressure vessels. Within a recent research project run by the Federal Institute for Materials Research and Testing (BAM), aging process of composite pressure vessels is investigated in order to be able to give more accurate lifetime predictions in the future. Focus is set on type III pressure vessels consisting of an aluminium tank which is fully wrapped with carbon fibre reinforced plastics. In order to increase high-cycle fatigue, residual stresses are induced into the pressure vessel during manufacturing process. In particular, residual compressive stresses within the inner aluminium layer have been defined as a main parameter affecting fatigue strength. The aim is to identify and evaluate residual stresses of the pressure vessel by analysing its modal parameters. Through the set-up of a finite-element model potential capability and validity for the use of modal analysis is proven and evaluated, considering influences resulting from manufacturing deviations, too. In the following, a number of stress sensitive modes are defined. Based on these preliminary numerical investigations, a test bench is set up in order to measure pressure vessels via an experimental modal analysis. A final critical evaluation regarding the accuracy of the modal analysis is made by comparing experimental results with data obtained through simulations. T2 - INTER-NOISE 2017 46th International Congress and Exposition on Noise Control Engineering CY - Hong Kong, People's Republic of China DA - 27.08.2017 KW - Composite pressure vessel KW - Modal analysis PY - 2017 SP - 6309 EP - 6316 CY - Hong Kong AN - OPUS4-41842 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völzke, Holger A1 - Wolff, Dietmar A1 - Kasparek, Eva Maria A1 - Botsch, W. A1 - Drotleff, H.-W. A1 - Hinterding, P. A1 - Smalian, S. T1 - Safety aspects of dry spent fuel storage and spent fuel management N2 - Dry storage Systems are characterized by passive and inherent safety systems ensuring safety even in case of severe incidents or accidents. After the events of Fukushima, the advantages of such passive and inherently safe dry storage systems have become more and more obvious. In Germany dry storage of spent nuclear fuel (SNF) and high level wastes (HLW) in dual purpose casks fulfills both transport and storage requirements. Basic safety requirements consider safe enclosure of the radioactive materials under normal operation and accident conditions, safe decay heat removal, subcriticality and shielding. Mostly, storage facilities are designed as concrete buildings above the ground, but due to regional constraints, one storage facility has also been built as a rock tunnel. The decay heat is always removed by natural air flow; further technical equipment is not needed. Safe enclosure, subcriticality and shielding are mainly guaranteed by massive thick-walled metal casks. TÜV NORD Nuclear and BAM present their long experience concerning the licensing process for sites and casks and inform about spent fuel management and issues concerning dry storage of spent fuel and high level waste. T2 - ENC 2012 - European Nuclear Conference CY - Manchester, UK DA - 10.12.2012 KW - Spent nuclear fuel (SNF) KW - High level waste (HLW) KW - Dry storage systems KW - Safety assessment PY - 2012 SN - 978-92-95064-14-0 SP - 1 EP - 5 PB - European Nuclear Society CY - Brussels, Belgium AN - OPUS4-27557 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Blind, Knut A1 - Gutknecht, Ralph A1 - Kirstgen, Martin A1 - Neuhäusler, Peter A1 - Schirmeister, Elna A1 - Schubert, Torben ED - Koch, Claudia T1 - Die Bedeutung der Qualitätsinfrastruktur: Studie zu wirtschaftlichen und nicht-wirtschaftlichen Wirkungen sowie Trendstudie Digitalisierung N2 - Um Qualität, Sicherheit und Umweltverträglichkeit von Waren, Dienstleistungen und Verfahren zu unterstützen und zu verbessern braucht es eine starke und verlässliche Qualitätsinfrastruktur (QI). Die empirische Studie erfasst erstmals quantitativ die wirtschaftlichen und nicht-wirtschaftlichen Wirkungen der QI. Im Rahmen dieser Studie wurden die ökonomischen Wirkungsdimensionen der QI und ihrer Einzelkomponenten, insb. im Hinblick auf Bruttowertschöpfung, Wirtschaftswachstum, Außenhandel, Innovation, und weitere Aspekte konzeptionell erfasst und quantifiziert. Dabei wurden sektorspezifische Besonderheiten berücksichtigt. Komplementär wurden auch ausgewählte nicht-ökonomische Wirkungsdimensionen der QI quantitativ bestimmt. Diese quantitative Analyse wird ergänzt durch eine qualitative Untersuchung der QI Deutschlands, wobei sowohl auf die Interaktionen der verschiedenen QI-Komponenten eingegangen als auch auf die Besonderheiten ausgewählter Sektoren abgehoben wird. Die Möglichkeiten der rasch voranschreitenden Digitalisierung für die QI und ihre einzelnen Komponenten wurden in einem zweiten Teil im Rahmen eines Szenarioansatzes identifiziert und bewertet. Hier wurden auf Basis von Schlüsselfaktoren vier Szenarien entwickelt und entsprechende strategische Implikationen und Anknüpfungspunkte abgeleitet. Abschließend gibt die Studie Empfehlungen differenziert nach den einzelnen Komponenten der QI, aber auch speziell für verschiedenen Akteure und Institutionen auf Basis der gewonnenen Erkenntnisse. KW - Qualitätsinfrastruktur KW - Wirtschaftsleistung KW - Trendanalyse KW - Szenarioanalyse KW - Szenarien PY - 2025 DO - https://doi.org/10.24406/publica-4411 N1 - Endbericht zu einem Projekt im Rahmen von QI-Digital, gefördert vom Bundesministerium für Wirtschaft und Klimaschutz. SP - 1 EP - 154 PB - Fraunhofer-Institut für System- und Innovationsforschung (ISI) CY - Karlsruhe AN - OPUS4-62710 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völzke, Holger A1 - Probst, Ulrich A1 - Wolff, Dietmar A1 - Nagelschmidt, Sven A1 - Schulz, Sebastian T1 - Seal and closure performance in long term storage N2 - In Germany thick walled metallic transport and storage casks are the established concept for dry interim storage of spent nuclear fuel and high active waste from reprocessing. For the long term safe and leak tight closure of the casks metal seals (consisting of an inner helical spring and two outer jackets made of Steel and aluminum or silver) together with screwed lids are major components. So far 40 years storage periods are evaluated and licensed but extended storage periods are expected in the future due to delays in final repository siting and licensing procedures. For that reason additional knowledge of the long term performance of the lid seal Systems is required and BAM has started investigation programs on these issues. Technically, long term reliable pressure forces in combination with a tight surface contact is as important as well maintained seal and surface qualities and dry and clean conditions during seal assembly and Operation to ensure sufficient seal function. To gain representative data BAM has developed test flanges for seals with full scale cross section diameter but much smaller outer diameter to be placed in appropriate testing machines for relevant mechanical loading under static and dynamic conditions with the ability to measure the Standard helium leakage rate continuously during each test phase. This paper presents an update on running long term seal tests at different temperatures (+20°C, +100°C, +15O°C) under static conditions over longer periods with different seal types. Due to creeping effects a reduction of the pressure force over deflection during loading and unloading does appear depending on prior holding times. Analytical approaches on basis of test data are developed and discussed to extrapolate seal performance (pressure force, elastic recovery, leak tightness) to longer periods of cask operation. T2 - PSAM 11 ESREL 2012 - 11th International Probabilistic Safety Assessment and Management Conference & The Annual European Safety and Reliability Conference CY - Helsinki, Finland DA - 25.06.2012 KW - Metal seal KW - Interim storage KW - Long term performance PY - 2012 SP - 1 EP - 8 PB - European Safety and Reliability Association (ESRA) CY - Bruxelles, Belgium AN - OPUS4-26175 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völzke, Holger A1 - Nieslony, Gregor A1 - Ellouz, Manel A1 - Noack, Volker A1 - Hagenow, Peter A1 - Kovacs, Oliver A1 - Hörning, Tony T1 - Container approval for the disposal of radioactive waste with negligible heat generation in the German Konrad repository N2 - Since the license for the Konrad repository was finally confirmed by legal decision in 2007, the Federal Institute for Radiation Protection (BfS) has been performing further planning and preparation work to prepare the repository for operation. Waste conditioning and packaging has been continued by different waste producers as the nuclear industry and federal research institutes on the basis of the official disposal requirements. The necessary prerequisites for this are approved containers as well as certified waste conditioning and packaging procedures. The Federal Institute for Materials Research and Testing (BAM) is responsible for container design testing and evaluation of quality assurance measures on behalf of BfS under consideration of the Konrad disposal requirements. Besides assessing the container handling stability (stacking tests, handling loads), design testing procedures are performed that include fire tests (800°C, 1 hour) and drop tests from different heights and drop orientations. This paper presents the current state of BAM design testing experiences about relevant container types (box shaped, cylindrical) made of steel sheets, ductile cast iron or concrete. It explains usual testing and evaluation methods which range from experimental testing to analytical and numerical calculations. Another focus has been laid on already existing containers and packages. The question arises as to how they can be evaluated properly especially with respect to lack of completeness of safety assessment and fabrication documentation. T2 - WM2012 - Waste Management Conference CY - Phoenix, AZ, USA DA - 26.02.2012 PY - 2012 SN - 978-0-9836186-1-4 N1 - Serientitel: WM Symposia – Series title: WM Symposia IS - Paper 12148 SP - 1 EP - 9 PB - WM Symposia CY - Tempe, AZ, USA AN - OPUS4-26272 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lozano, Daniel A1 - Gravenkamp, Hauke A1 - Birk, Carolin T1 - Simulations of ultrasonic guided wave scattering using the scaled boundary finite element method N2 - This paper presents a numerical framework employing the Scaled Boundary Finite Element Method (SBFEM) for efficiently solving ultrasonic guided wave modal scattering problems and constructing scattering matrices (S-matrices). The framework integrates hierarchical octree meshing and an enhanced far field formulation. It incorporates boundary integrals, enabling an accurate representation of defect interactions with guided waves. Validation is performed using a benchmark test supported by an error estimation method based on energy balance. Two practical examples are used to showcase the simulation framework, where the scattering of guided waves with surface-breaking and subsurface cracks near rivet holes is studied. KW - Guided waves KW - Scattering matrix KW - Scaled boundary finite element method KW - Elastodynamics PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-638295 DO - https://doi.org/10.1016/j.cma.2025.118204 SN - 0045-7825 VL - 445 SP - 1 EP - 23 PB - Elsevier B.V. AN - OPUS4-63829 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weise, Frank A1 - Voland, Katja A1 - Pirskawetz, Stephan A1 - Meinel, Dietmar ED - Drimalas, T. ED - Ideker, J.H. ED - Fournier, B. T1 - Innovative measurement techniques for characterising internal damage processes in concrete due to ASR N2 - This paper describes an innovative, non destructive measurement methodology that has already been successfully applied. For the first time a combination of continuous recording of length change, acoustic emission and ultrasonic velocity as well as discontinuous 3-dimensional micro X-ray computed tomography (µ-3DCT) measurements has been carried out. This unique combination of innovative measurement techniques enables a continuous monitoring of internal damage processes in concrete samples due to theASR. Three phases of the ASR process have been observed in both types of concrete storage by application of the above mentioned continuous methods. In the beginning the hydration of concrete dominates, followed by the crack formation due to the ASR and finally the occurred cracks are presumably filled with reaction products. Moreover, the formation of cracks can be temporally and spatially visualized by µ-3D-CT. Microscopic analysis confirm the µ-3D-CT results. T2 - 14th ICAAR - International conference on alkali aggregate reaction CY - Austin, TX, USA DA - 20.05.2012 KW - Fog chamber KW - Concrete prism test KW - Length change KW - Acoustic emission KW - Ultrasonic velocity KW - µ-3D-CT PY - 2012 IS - 021811-WEIS SP - 1 EP - 10 AN - OPUS4-26053 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erhard, Anton A1 - Schulz, Eduard T1 - Influences on crack detection in the near surface area with ultrasonic inspection techniques T2 - 29th Annual Conference of the Czech Society for Nondestructive Testing CY - Hradec Králové, Czech Republic DA - 1999-11-17 KW - Crack detection KW - Rißprüfung KW - Ultraschallprüfung PY - 1999 SP - 153 EP - 164 AN - OPUS4-717 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Terstiege, Heinz T1 - Fluoreszierende Materialien im Straßenverkehr T2 - Progress in Automobile Lighting CY - Darmstadt, Germany DA - 1995-09-26 KW - Material, fluoreszierend KW - Straßenverkehr PY - 1995 SP - 202 EP - 205 CY - Darmstadt AN - OPUS4-585 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jancke, Harald A1 - Altenburg, Wolfgang T1 - NMR Studies an Soil and Peat - The Problem of True Signal Intensities T2 - 2nd European Symposium "NMR in Soil Science" CY - Freising/Weihenstephan, Germany DA - 2000-02-27 KW - NMR KW - Signal Intensities PY - 2000 SP - 1 EP - 27 AN - OPUS4-762 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Gert A1 - Burmeister, J. T1 - Online Process Monitoring by Fuzzy Classification during AC Resistance Welding T2 - International Conference at the 53rd Annual Assembly of the International Institute of Welding CY - Florence, Italy DA - 2000-07-13 KW - Online Process Monitoring PY - 2000 SP - 1 EP - 12 AN - OPUS4-763 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Hartmut A1 - Lorenz, Edelgard A1 - Bahr, Horst A1 - Seifert, Ingetraut A1 - Neyen, Volker A1 - Hofmann, Silvia A1 - Strauß, Birgid A1 - Volland, G. A1 - Lange, B. T1 - Untersuchungen zum Langzeit-Hydrolyse-Verhalten von Polyestergeweben T2 - Zhongguo Guoji Fei-Zhizaobu/Chanye-Yong Fangzhipin Yantaohui ; China International Nonwovens/Techtextiles Conference CY - Beijing, China DA - 2000-05-23 KW - Langzeit-Hydrolyse-Verhalten KW - Polyestergewebe PY - 2000 N1 - Geburtsname von Hofmann, Silvia: Benemann, S. - Birth name of Hofmann, Silvia: Benemann, S. SP - 165 EP - 183 CY - Beijing AN - OPUS4-764 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Munikoti, Vijayendra K. T1 - On the propagation of elastic waves in acoustically anisotropic austenitic materials and at their boundaries during non-destructive inspection with ultrasound KW - Ultraschall KW - Anisotropie KW - Austenit PY - 2000 SP - 1 EP - 206 AN - OPUS4-767 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rückert, Joachim A1 - Isecke, Bernd A1 - Zietelmann, Christina T1 - Gebrauchssicherheit von Kochgerät aus Edelstahl - Elektrochemische Messungen zur Ni-Abgabe (Teil 1) KW - Nickelabgabe KW - Nickelübergang aus Edelstahl in Kochgut PY - 1998 IS - 246 SP - 1 EP - 91 CY - Düsseldorf AN - OPUS4-772 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Häcker, Ralf A1 - Hünecke, Joachim T1 - An optical system for the measurement of specimen deformations in tensile and compression tests T2 - International Workshop on Video-Controlled Materials Testing and In-Situ Microstructural Characterization CY - Nancy, France DA - 1999-11-16 KW - Optical Systems PY - 1999 SP - 129 EP - 132 AN - OPUS4-781 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Driessens, F. C. M. A1 - De Maeyer, E. A. P. A1 - Fernández, E. A1 - Boltong, M. G. A1 - Berger, Georg A1 - Verbeeck, R. M. H. A1 - Ginebra, M. P. A1 - Planell, J. A. T1 - Amorphous calcium phosphate cements and their transformation into calcium deficient hydroxyapatite KW - Zement KW - Kalzium-Phosphat PY - 1996 VL - 9 SP - 231 EP - 234 AN - OPUS4-704 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Seeger, Stefan T1 - Anforderungen an Dichtungskontrollsysteme aus der Sicht des Anwenders T2 - 15. Fachtagung "Die Sichere Deponie" CY - Würzburg, Deutschland DA - 1999-02-18 KW - Dichtungskontrollsysteme KW - Oberflächenabdichtungen PY - 1999 IS - 15 SP - 1 EP - 13 PB - SKZ CY - Würzburg AN - OPUS4-752 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kunze, Ralf A1 - Neubert, Dietmar A1 - Brademann-Jock, Kerstin T1 - TG/MS-Untersuchungen an geschäumten Polymeren T2 - Symposium on Thermal Analysis in Industry and Research ; 27e Journées de Calorimétrie et d'Analyse Thermique (AFCAT) ; 22. Jahrestagung der Gesellschaft für Thermische Analyse e.V. (GEFTA) CY - Freiburg, Deutschland DA - 1996-09-24 KW - Polymer, geschäumt KW - Thermogravimetrie, TG KW - Massenspektrometer, MS KW - Dämmstoff PY - 1996 SP - 166 EP - 168 PB - GEFTA Office CY - Freiburg AN - OPUS4-692 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz, Ulrich A1 - Trubiroha, Peter T1 - Autolacke im sauren Regen - künstliche Bewitterung mit saurer Benässung im Vergleich zu herkömmlichen Prüfverfahren T2 - 23. FATIPEC Congress CY - Brüssel, Belgien DA - 1996-06-10 KW - Autolack KW - Bewitterung, künstlich KW - Prüfverfahren KW - ADF-Test KW - Regen, saurer PY - 1996 VL - D SP - D-89-D-104 CY - Brussels AN - OPUS4-694 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaenicke, Bernd ED - Zenner, H. T1 - Randschichtverfestigte Schweißverbindungen in Leichtbaustirnrädern T2 - 22. Vortragsveranstaltung des DVM-Arbeitskreises Betriebsfestigkeit CY - Berlin, Germany DA - 1996-10-16 KW - Großzahnrad KW - Zahnrad KW - Getriebe KW - Vergütung KW - Einsatzhärtebehandlung PY - 1996 N1 - Serientitel: Vortragsveranstaltung des DVM-Arbeitskreises Betriebsfestigkeit – Series title: Vortragsveranstaltung des DVM-Arbeitskreises Betriebsfestigkeit IS - 122 SP - 9 EP - 28 PB - DVM CY - Berlin AN - OPUS4-696 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Harbich, Karl-Wolfram A1 - Mücke, Udo A1 - Rabe, Torsten T1 - Röntgen-Refraktions-Topographie als neue Methode zur Charakterisierung von keramischen Werkstoffen T2 - Jahrestagung Zerstörungsfreie Materialprüfung 1996 CY - Lindau, Deutschland DA - 1996-05-13 KW - Röntgen-Refraktion KW - Topographie KW - Keramik PY - 1996 IS - 52.2 SP - 755 EP - 764 PB - DGZfP CY - [Berlin] AN - OPUS4-698 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klement, Ernst T1 - Objektbezogene Brandschutzplanung KW - Brandschutz PY - 1996 SP - 1 EP - 16 AN - OPUS4-700 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz-Forberg, Bernd T1 - UN-Empfehlung als weltweite Konvention/Harmonisierung als Ansatz zur Vereinfachung der Vorschriften? T2 - Fachtagung "Chemikalien sicher transportieren" CY - Wien, Österreich DA - 1999-11-09 KW - Gefahrguttransporte PY - 1999 SP - 1 EP - 4 PB - CEFIC AN - OPUS4-745 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Berger, Wolfgang A1 - Kalbe, Ute A1 - Goebbels, Jürgen ED - Srodo´n, J. T1 - Fabric studies on contaminated mineral layers in composite liners T2 - 9th Conference of the European Clay Groups Association (Euroclay) CY - Krakow, Poland DA - 1999-09-04 KW - Composite liner KW - Mineral layer KW - Fabric KW - Organic contaminants PY - 1999 SP - 63 CY - Kraków AN - OPUS4-749 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalbe, Ute A1 - Berger, Wolfgang A1 - Eckardt, Jürgen A1 - Müller, Werner ED - Srodo´n, J. T1 - Transport of concentrated hydrocarbons within base liner systems T2 - 9th Conference of the European Clay Groups Association (Euroclay) CY - Krakow, Poland DA - 1999-09-04 KW - Hydrocarbon PY - 1999 SP - 1 CY - Kraków AN - OPUS4-750 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simon, Franz-Georg A1 - Köcher, Peter A1 - Kley, Gerd T1 - Products from the vitrification of residues - an example for an Ecomaterial T2 - 4th International Conference on Ecomaterials CY - Gifu, Japan DA - 1999-11-10 KW - Vitrification KW - Ash treatment KW - heavy metals KW - Arc furnace KW - Verglasung KW - Asche KW - Schwermetalle KW - Lichtbogenofen PY - 1999 IS - P-5 SP - 467 EP - 470 AN - OPUS4-730 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Malz, Frank A1 - Jancke, Harald A1 - Radeglia, Reiner A1 - Hässelbarth, Werner T1 - Intercomparisons for quantitative 1H NMR spectroscopy T2 - 22nd GDCh-Discussion Meeting CY - Regensburg, Germany DA - 2000-09-27 PY - 2000 SP - 92 AN - OPUS4-966 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hünecke, Joachim A1 - Schöne, Dieter T1 - Anrisslebensdauer bei gekerbten Proben durch optische Beobachtung des Kurzrissverhaltens T2 - 27. Tagung des DVM-Arbeitskreises Betriebsfestigkeit CY - Koblenz, Deutschland DA - 2000-10-18 KW - Ermüdung KW - Kurze Risse KW - Optische Beobachtung KW - Schädigungsparameter KW - Simulation PY - 2000 N1 - Sprachen: Deutsch/Englisch - Languages: German/English N1 - Serientitel: Tagung des DVM-Arbeitskreises Betriebsfestigkeit – Series title: Tagung des DVM-Arbeitskreises Betriebsfestigkeit IS - 127 SP - 273 EP - 282 PB - DVM CY - Berlin AN - OPUS4-993 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Witke, Klaus A1 - Polak, W. A1 - Beining, K. A1 - Beining, B. A1 - Kleinert, T. A1 - Fischer, C. A1 - Kircher, D. T1 - TCDO complex - a substance with great features T2 - WAPOTEC Workshop 2000 CY - Bougival-Versailles, France DA - 2000-10-13 PY - 2000 AN - OPUS4-998 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Unger, Wolfgang T1 - Bewertung & Charakterisierung technischer Oberflächen für die verarbeitende Industrie T2 - Workshop und Präsentation CY - Bergisch Gladbach, Deutschland DA - 2000-05-11 PY - 2000 CY - Dresden AN - OPUS4-999 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nehls, Irene A1 - Wachholz, Sigrid A1 - Lehnik-Habrink, Petra A1 - Becker, Roland A1 - Win, Tin T1 - Neue Referenzmaterialien für die organische Analytik als Instrumente der Qualitätssicherung T2 - Tagung "Tag der Chemie" CY - Potsdam, Deutschland DA - 2000-11-08 PY - 2000 AN - OPUS4-1000 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reiners, Georg T1 - Glow Discharge Optical Emission Spectroscopy (GDOES) - A powerful tool for the characterisation of coatings T2 - Workshop on the development and standardisation of test methods for engineering coatings CY - Garmisch-Partenkirchen, Germany DA - 2000-09-17 PY - 2000 CY - Düsseldorf AN - OPUS4-983 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schalau, Bernd A1 - Grätz, Rainer T1 - Wurfweiten von Fragmenten beim Behälterbersten T2 - 5. Fachtagung Anlagen-, Arbeits- und Umweltsicherheit CY - Köthen, Deutschland DA - 2000-11-09 PY - 2000 VL - 5 SP - 1(?) EP - 8(?) PB - VDI-Gesellschaft Verfahrenstechnik und Chemieingenieurwesen CY - Düsseldorf AN - OPUS4-984 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rudolph, Pascale A1 - Krüger, Jörg A1 - Kautek, Wolfgang T1 - Mikrostrukturierung von Glas zur Erzeugung kristalliner Si-Schichten PY - 2000 IS - 12 SP - 7 EP - 36 PB - VDI-Verl. CY - Düsseldorf AN - OPUS4-985 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wachtendorf, Volker A1 - Krüger, Simone A1 - Schulz, Ulrich A1 - Trubiroha, Peter T1 - Chemiluminescence of polyethylenes as accelerated test for the efficiency of stabilisers and of the effect of recycling procedures T2 - Workshop on chemiluminescence CY - Leipzig, Germany DA - 2000-10-19 PY - 2000 SP - 1 EP - 10(?) AN - OPUS4-991 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schultze, D. T1 - Thermische Analyse - eine Gruppe temperaturdynamischer Methoden PY - 2000 AN - OPUS4-974 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schultze, D. T1 - Reaktionskontrolliertes Sintern - eine moderne Variante der Dilatometrie PY - 2000 AN - OPUS4-975 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eberle, Arno A1 - Sievert, Rainer T1 - Verifizierung von Flip-Chip-Demonstratoren unter Verwendung belastbarer Materialkennwerte T2 - Öffentliches Status-Seminar "Projekt SIMIKO" CY - München, Deutschland DA - 2000-09-29 PY - 2000 AN - OPUS4-976 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erhard, Anton A1 - Bäßler, Ralph A1 - Weltschev, Margit T1 - Regulating the use of new materials in containment systems for dangerous goods N2 - Transportation of dangerous goods are worldwide regulated in the rules or standards e.g. in the recommendations on the Transport of Dangerous Goods of the United Nations, in the Accord Européen Relatif au Transport International des Marchandises Dangereuses par Route (ADR) etc. Addi-tional to these international regulations also national regulations and stan-dards e.g. Gefahrgutverordnung Straße und Eisenbahn (GGVSE) in Ger-many are bases for the transport of hazardous materials. For the material properties of tanks in the “BAM-List – Requirements for Tanks for the Transport of Dangerous Goods” specifications for the sub-stance prototype approval for tank materials are listed. Further compati-bility evaluations of selected metallic material groups as well as of poly-meric gasket and lining materials under the influence of dangerous goods are published in the List. There are a large number of highly corrosive dangerous goods listed, in which conventional steels are not resistant. Chemical companies, transportation providers and tank producers need tanks made of corrosion-resistant materials (corrosion retardant materi-als) in order to protect the tank shell. The application of high-alloyed stainless steels and nickel alloys as there are alloy 926 (1.4529; X1NiCrMoCuN25-20-7), alloy 31 (1.4562;X1NiCrMoCu31-27-7) and Nickel-Chromium-Molybdenum Alloy 59 (2.4605; NiCr23Mo16Al) is an al-ternative solution compared with the lining of the tanks with a polymeric material. Due to the limited number of corrosion test results with welded test sam-ples of these high-alloyed materials under the influence of corrosive dan-gerous goods BAM, Institute for Corrosion Protection (IKS) Dresden and ThyssenKrupp VDM have been performing a comprehensive test program since 2002. The program comprised corrosion resistance evaluations of the three high-alloyed materials exposed to substances representing cor-rosive dangerous goods such as inorganic halogenides, organic acidic halogenides, sulfonic acids and nitrating acids. T2 - MRS Fall Meeting 2008 - Symposium SS -Selecting and Qualifying New Materials for Use in Regulated Industries CY - Boston, MA, USA DA - 2008-12-01 KW - Korrosionsbeständigkeit KW - Superaustenite KW - Nickellegierung KW - Gefahrguttransport PY - 2008 DO - https://doi.org/10.1557/PROC-1151-SS01-02 VL - 1151E IS - Paper #: 1151-SS01-02 SP - 1 EP - 8(?) CY - Warrendale, PA, USA AN - OPUS4-19610 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bohse, Jürgen A1 - Mair, Georg W. T1 - Schädigungsanalyse mittels Schallemissionsprüfung (AT): Ein Beitrag zur Sicherheit von Composite-Druckbehältern T2 - 12. Problemseminar - Deformation und Bruchverhalten von Kunststoffen CY - Merseburg, Deutschland DA - 2009-06-24 KW - Schallemissionsprüfung KW - Schädigungsanalyse KW - Composite KW - Druckbehälter PY - 2009 SP - 1 EP - 8 AN - OPUS4-19601 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mair, Georg W. T1 - Hydrogen onboard storage - an insertion of the probalistic approach into standards & regulations? T2 - International Conference on Hydrogen Safety CY - Pisa, Italy DA - 2005-09-08 PY - 2005 UR - http://www.storhy.net/pdf/ICHS_Hydrogen_Onboard_Storage_BAM_2005-09-09.pdf SP - 42 pages PB - University of Pisa CY - Pisa AN - OPUS4-11299 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Jaenisch, Gerd-Rüdiger A1 - Artemiev, Valentin M. A1 - Naumov, A. T1 - Dynamic image reconstruction - General estimation principle for process tomography T2 - 15th World Conference on Non-Destructive Testing (WCNDT) CY - Roma, Italy DA - 2000-10-15 KW - Dynamic image KW - Stochastic estimation KW - Dynamic reconstruction KW - Kalman filter PY - 2000 UR - http://www.ndt.net/article/wcndt00/papers/idn326/idn326.htm SN - 1435-4934 N1 - Geburtsname von Jaenisch, Gerd-Rüdiger: Tillack, G.-R. - Birth name of Jaenisch, Gerd-Rüdiger: Tillack, G.-R. VL - 5 IS - 11 SP - 1 EP - 8(?) PB - NDT.net CY - Kirchwald AN - OPUS4-868 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gildenhaar, Renate A1 - Berger, Georg A1 - Knabe, C. A1 - Howlett, C. A1 - Markovic, B. A1 - Klar, F. A1 - Zreiqat, H. T1 - The Effect of Different Dental Titanium and Calcium Phosphate Implant Surfaces on the Expression of Bone-Related Genes and Proteins in vitro T2 - 6th World Biomaterials Congress CY - Kamuela, Big Island, HI, USA DA - 2000-05-15 KW - Dental Implant Surfaces PY - 2000 VL - 1 SP - 238 PB - Society for Biomaterials CY - Minneapolis, Minn. AN - OPUS4-869 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gildenhaar, Renate A1 - Berger, Georg A1 - Knabe, C. A1 - Howlett, C. A1 - Markovic, B. A1 - Reif, D. A1 - Zreiqat, H. T1 - The Functional Expression of Human Bone Derived Cells Grown on Rapidly Resorbable Calcium Phosphate Ceramics T2 - 6th World Biomaterials Congress CY - Kamuela, Big Island, HI, USA DA - 2000-05-15 KW - Calcium Phosphate Ceramics PY - 2000 SP - 970 PB - Society for Biomaterials CY - Minneapolis, Minn. AN - OPUS4-870 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geißler, Heinz A1 - Peuker, Christel A1 - Brzezinka, Klaus-Werner A1 - Kohl, Anka A1 - Pilz, Walter T1 - OH- und H2O-Schwingungsbanden in den IR- und Raman-Spektren von Gläsern T2 - 74. Glastechnische Tagung CY - Ulm, Deutschland DA - 2000-05-29 KW - Raman-Spektren KW - IR-Spektren PY - 2000 SP - 164 EP - 167 PB - DGG, Dt. Glastechn. Ges. CY - Frankfurt/M. AN - OPUS4-889 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Hartmut A1 - Bahr, Horst A1 - Kneip, Gisela A1 - Lorenz, Edelgard A1 - Kunze, Ines A1 - Seifert, Ingetraut T1 - Long-Term-Resistance of PET-Geofibers to Inner and Outer Hydrolysis T2 - Zhongguo Guoji Fei-Zhizaobu/Chanye-Yong Fangzhipin Yantaohui ; China International Nonwovens/Techtextiles Conference CY - Beijing, China DA - 2000-05-23 KW - Hydrolysis KW - PET-Geofibers PY - 2000 N1 - Geburtsname von Kunze, Ines: Schmücking, I. - Birth name of Kunze, Ines: Schmücking, I. SP - 1(?) EP - 17(?) CY - Beijing AN - OPUS4-890 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Günther, Bernd A1 - Czepluch, Wolf A1 - Mäder, Klaus A1 - Zedler, Steffen T1 - Multiplexer for Attenuation Measurements during POF Durability Testing T2 - International POF Technical Conference 2000 (POF 2000) CY - Cambridge, MA, USA DA - 2000-09-05 KW - POF Durability Testing PY - 2000 SP - 209 EP - 213 PB - Information Gatekeepers Inc. CY - Cambridge, Mass. AN - OPUS4-877 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Karsten A1 - Rehmer, Birgit T1 - Dynamic Fracture Toughness of Ductile Cast Iron for Transport and Storage Casks T2 - Jahrestagung Kerntechnik 2000 ; Annual Meeting on Nuclear Technology 2000 CY - Bonn, Germany DA - 2000-05-23 KW - DCI KW - Ductile Cast Iron KW - Transport and Storage Casks PY - 2000 SP - 609 EP - 612 PB - INFORUM-Verl. CY - Bonn AN - OPUS4-893 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hennecke, Manfred T1 - Neuausrichtung einer Bundesanstalt unter den Bedingungen des "schlanken Staates" T2 - Tagung GOCh-Arbeitsgemeinschaft "Chemiker im öffentlichen Dienst" CY - Jena, Deutschland DA - 2000-10-02 PY - 2000 SP - 1(?) AN - OPUS4-899 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weh, Lothar T1 - Oberflächencharakterisierung von Polymer- und Polymermatrix-Keramik-Schichten T2 - Kolloquium "Innovative Forschung in der WIP-Nachfolge" CY - Berlin, Deutschland DA - 2000-06-29 KW - Polymere KW - Keramik KW - Oberfläche KW - Fließprozesse PY - 2000 SP - 121 EP - 124 AN - OPUS4-930 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meier, Klaus A1 - Recknagel, Angelika A1 - Recknagel, Sebastian T1 - New Certified Reference Materials (CRM) of the Federal Institute for Materials Research and Testing (BAM) for the analysis of non ferrous metals and their alloys T2 - Symposium "Reference Materials for Technologies in the New Millenium" CY - Berlin, BAM, Germany DA - 2000-05-22 PY - 2000 SP - 1(?) EP - 9(?) AN - OPUS4-931 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Recknagel, Sebastian T1 - Certified reference materials for the analysis of iron and steel products (EURONORM-CRMS) - Preparation, certification, programme T2 - Symposium "Reference Materials for Technologies in the New Millenium" CY - Berlin, BAM, Germany DA - 2000-05-22 PY - 2000 SP - 1 EP - 7(?) AN - OPUS4-932 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weh, Lothar A1 - Müller, Ralf A1 - Moseler, D. A1 - Heide, G. A1 - Frischat, G. T1 - Topographische Untersuchungen von Glasoberflächen mit Vickers-Eindrücken T2 - 74. Glastechnische Tagung CY - Ulm, Deutschland DA - 2000-05-29 PY - 2000 SP - 237 EP - 240 PB - DGG, Dt. Glastechn. Ges. CY - Frankfurt/M. AN - OPUS4-934 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nehls, Irene T1 - Entwicklung, Herstellung und Einsatz von Referenzmaterialien für die organische Umweltanalytik T2 - Analytica Conference 2000 CY - München, Deutschland DA - 2000-04-11 PY - 2000 SP - 1(?) CY - München AN - OPUS4-939 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kipphardt, Heinrich A1 - Ruße, K. A1 - Bréas, O. A1 - Valkiers, S. A1 - Taylor, P. T1 - Fluorination of organic materials into CF4 for the measurements of carbon isotope ratios T2 - V Isotope Workshop CY - Krakow, Poland DA - 2000-07-01 PY - 2000 IS - poster P1-1 AN - OPUS4-914 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kipphardt, Heinrich A1 - De Bièvre, P. T1 - How to establish traceability in chemical measurements and reference materials? T2 - Symposium "Reference Materials for Technologies in the New Millenium" CY - Berlin, BAM, Germany DA - 2000-05-22 KW - Traceability KW - Reference materials KW - Uncertainty KW - Matrix reference materials KW - Amount standards PY - 2000 SP - 1(?) EP - 7(?) AN - OPUS4-916 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Berger, Georg A1 - Steinhauser, E. A1 - Willmann, G. A1 - Liesner, C. A1 - Willems, U. A1 - Grössl, H. T1 - Biokompatible Werkstoffe - Ersatzteile für Menschen T2 - Podiumsdiskussion zur Materialica 2000 CY - München, Deutschland DA - 2000-09-26 PY - 2000 AN - OPUS4-918 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Günther, Achim T1 - Gefährlichkeit und Gefahr für die Umwelt - Kriterien für die Einstufung chemischer Stoffe T2 - Jahrestagung der Gesellschaft Deutscher Chemiker, Fachgruppe Umweltchemie und Ökotoxikologie 2000 ; GDCh-Jahrestagung 2000 CY - Bayreuth, Deutschland DA - 2000-10-07 KW - Umweltchemie KW - Ökotoxikologie PY - 2000 SP - 1(?) AN - OPUS4-920 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Steffen, Bernd T1 - The flexible scope of Accreditation T2 - 5th Eurolab Symposium CY - Edinburgh, Scotland, UK DA - 2000-10-04 PY - 2000 SP - 1(?) EP - 7(?) AN - OPUS4-921 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maultzsch, Matthias T1 - The use of polymers for repair and protection of concrete structures in the light of RTD and regulations in Europe T2 - 10th International Congress on Polymers in Concrete ; ICPIC/ICRI International Concrete Repair Workshop CY - Honolulu, HI, USA DA - 2001-05-21 KW - Polymer modified cement concrete (PCC) KW - Surface protection systems (SPS) KW - Concrete repair KW - Standardization KW - Test methods PY - 2001 SP - 1(?) EP - 21(?) AN - OPUS4-954 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Andreas T1 - Information on Proficiency Testing Schemes (Database EPTIS) T2 - 5th Eurolab Symposium CY - Edinburgh, Scotland, UK DA - 2000-10-04 PY - 2000 SP - 1(?) EP - 9(?) AN - OPUS4-957 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nehls, Irene T1 - Aufgaben der BAM - Referenzmaterialien T2 - Veranstaltung der SEPAWA CY - Berlin, BAM, Deutschland DA - 2000-09-08 PY - 2000 AN - OPUS4-959 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reiners, Georg T1 - New component properties by combined processes T2 - 15th INTERFINISH - world congress and exhibition CY - Garmisch-Partenkirchen, Germany DA - 2000-09-13 PY - 2000 SP - 137 CY - Garmisch-Partenkirchen AN - OPUS4-961 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kautek, Wolfgang T1 - Laserstrahlreinigung von historischem Pergament und Papier T2 - 4. Forum "Laser in der Restaurierung und Denkmalpflege" CY - Leipzig, Deutschland DA - 2000-10-27 KW - Laser PY - 2000 CY - Leipzig AN - OPUS4-903 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Menzel, Michael A1 - Maltsev, Y. T1 - Possibilities to improve the precision in Mössbauer spectroscopy T2 - 10th Mössbauer Colloquium CY - Freiberg, Germany DA - 2000-10-04 KW - Mössbauer Spectroscopy PY - 2000 AN - OPUS4-907 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lehmann, Andreas T1 - Vergleich HPLC <-> CE T2 - HPLC-Grundkurs CY - Berlin, Deutschland DA - 2000-09-04 PY - 2000 PB - Wista CY - Berlin AN - OPUS4-910 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Buge, Hans-Gerhard T1 - Development and certification of a reference material for the determination of Pentachlorophenol (PCP) and five selected Polycyclic Aromatic Hydrocarbons (PAH) in wood (PCP & PAH in wood) T2 - 4th TRA EFCT Annual Workshop (Statusreport zu Projekt SMT4-CT97-2147) CY - Prague, Czech Republic DA - 2000-10-12 PY - 2000 SP - 1(?) EP - 4(?) AN - OPUS4-943 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böhning, Martin A1 - Wald, Oliver A1 - Turky, Gamal A1 - Goering, Harald A1 - Brzezinka, Klaus-Werner A1 - Schartel, Bernhard A1 - Schönhals, Andreas T1 - Dielectric Relaxation and Gas Transport Properties in Polypropylene Based Nanocomposites T2 - ACS 2002 Biennial Symposium "Polymeric Nanomaterials" CY - Rohnert Park, CA, USA DA - 2002-11-17 PY - 2002 SP - 1(?) EP - 3(?) AN - OPUS4-2035 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böhning, Martin A1 - Turky, Gamal A1 - Goering, Harald A1 - Wald, Oliver A1 - Schartel, Bernhard A1 - Schönhals, Andreas T1 - Polypropylene/Clay Nanocomposites - Dielectric Relaxation and Gas Transport Properties T2 - 2nd International Conference on Broadband Dielectric Spectroscopy and Its Applications CY - Leipzig, Germany DA - 2002-09-02 PY - 2002 AN - OPUS4-2037 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schönhals, Andreas A1 - Goering, Harald A1 - Böhning, Martin A1 - Fritz, Andreas A1 - Rübner, J. T1 - Structure Analysis of Polymeric Nanomaterials by Relaxation Spectroscopy T2 - Polydays 2002 CY - Berlin, Germany DA - 2002-09-30 PY - 2002 SP - 1(?) AN - OPUS4-2044 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Goering, Harald A1 - Böhning, Martin A1 - Turky, Gamal A1 - Hao, Ning A1 - Schönhals, Andreas T1 - Molecular Dynamics in Polymer Nanocomposites T2 - Workshop "Glasübergang" CY - Rostock, Germany DA - 2002-12-16 PY - 2002 AN - OPUS4-2061 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böhning, Martin A1 - Goering, Harald A1 - Hao, Ning A1 - Schönhals, Andreas T1 - Gas Transport in Polymer based Nanocomposite Systems T2 - Workshop "Glasübergang" CY - Rostock, Germany DA - 2002-12-16 PY - 2002 AN - OPUS4-2054 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böhning, Martin A1 - Goering, Harald T1 - Herstellung und Charakterisierung von Nanopartikel/Polymer Composites T2 - BAM-Seminar der Abteilung VI "Funktion von Polymeren" CY - Berlin, BAM, Deutschland DA - 2002-09-19 PY - 2002 AN - OPUS4-2040 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Böhning, Martin A1 - Goering, Harald A1 - Hao, Ning A1 - Mach, Reinhard A1 - Schönhals, Andreas ED - Cassidy, P. T1 - Polycarbonate/SiC nanocomposites - Influence of nanoparticle dispersion on molecular mobility and gas transport T2 - 7th International Symposium on Polymers for Advanced Technologies CY - Fort Lauderdale, FL, USA DA - 2005-09-21 KW - Nanocomposites KW - Nanoparticles KW - Polycarbonates KW - Dielectric properties KW - Gas permeation PY - 2005 VL - 16 IS - 2-3 SP - 262 EP - 268 PB - Wiley CY - Chichester AN - OPUS4-7062 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böhning, Martin A1 - Tidjani, Adams A1 - Wald, Oliver A1 - Turky, Gamal A1 - Goering, Harald A1 - Brzezinka, Klaus-Werner A1 - Schartel, Bernhard A1 - Schönhals, Andreas T1 - Polypropylene/Clay Nanocomposites - Gas Transport Characteristics and Molecular Mobility T2 - Polydays 2002 CY - Berlin, Germany DA - 2002-09-30 PY - 2002 SP - 1(?) EP - 2(?) AN - OPUS4-2038 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Blind, Knut A1 - Neuhäusler, Peter A1 - Schubert, Torben ED - Koch, Claudia T1 - The importance of quality infrastructure in Germany: Study on economic and non-economic effects N2 - A strong and reliable quality infrastructure (QI) is vital for supporting and improving the quality, safety, and environmental compatibility of goods, services, and processes. This empirical study is the first to quantitatively assess the economic and non-economic effects of QI. As part of this study, the economic impact dimensions of QI and its individual components were conceptualized and quantified, particularly with regard to gross value added, economic growth, foreign trade, innovation, and other aspects. Sector-specific characteristics were taken into account. This quantitative analysis is supplemented by a qualitative analysis of Germany's QI, which examines both the interactions between the various QI components and the specific characteristics of selected sectors. This report is an English summary version of the original German report. KW - Quality infrastructure KW - Econometrics KW - Gross domestic product KW - Economic growth KW - Innovation KW - Quality assurance KW - Economy PY - 2025 DO - https://doi.org/10.24406/publica-5041 SP - 1 EP - 21 CY - Karlsruhe, Berlin AN - OPUS4-63913 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rolle, Annette A1 - Wille, Frank A1 - Komann, Steffen A1 - Neumann, Martin T1 - Qualification Procedure for Seal Designs for Spent Fuel Transport and Storage Cask Containments N2 - The seal is a key component of the containment and closure system of transport and storage casks for radioactive material. It is a major contributor to ensuring compliance with the acceptable limits for activity release according to IAEA regulations. The requirements for a safe seal performance are high, accordingly. Every new seal design intended for use in the containment of a transport cask for radioactive material passes a qualification process in Germany. The qualification process is supervised by BAM as German competent authority for mechanical, thermal and containment assessment of packages requiring design approval. The closure system including the seal shall be able to withstand the corrosive, mechanical and thermal loads associated with routine, normal and accident conditions of transport according to the IAEA regulations without losing the required sealing function. Metal seals of the Helicoflex® type are often used to ensure required package leak tightness for both storage and transport, including transport after long term interim storage. The poster will provide an overview of requirements during a seal qualification process on the example of a Helicoflex® type metal seal. T2 - 21st International Symposium on the Packaging and Transportation of Radioactive Materials, PATRAM 2025 CY - San Antonio, Texas , US DA - 27.07.2025 KW - Spent fuel transport KW - Seals KW - Radioactive KW - Containment PY - 2025 SP - 1 EP - 5 AN - OPUS4-63911 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Algernon, Daniel A1 - Wiggenhauser, Herbert A1 - Abraham, O. T1 - Scanning impact-echo for the investigation of tendon ducts in concrete T2 - Workshop of COST on NDT Assessment and New Systems in Prestressed Concrete Structures DA - 2005-09-18 PY - 2005 SP - 55 EP - 62 AN - OPUS4-11051 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Streicher, Doreen A1 - Algernon, Daniel A1 - Wöstmann, Jens A1 - Behrens, Matthias A1 - Wiggenhauser, Herbert T1 - Automated NDE of post-tensioned concrete bridges using imaging echo methods T2 - 29. Darmstädter Massivbauseminar, "Sicherheitsgewinn durch Monitoring?" CY - Darmstadt, Germany DA - 2006-09-14 KW - Zerstörungsfreie Prüfung im Bauwesen KW - Brückenuntersuchungen PY - 2006 SP - 477 EP - 487 PB - Freunde des Instituts für Massivbau der Technischen Universität Darmstadt CY - Darmstadt AN - OPUS4-14397 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Algernon, Daniel A1 - Wiggenhauser, Herbert T1 - Impact-Echo Data Analysis Based on the Hilbert-Huang Transform T2 - TRB 86th Annual Meeting CY - Washington, D.C., USA DA - 2007-01-21 KW - Impact-Echo KW - Hilbert-Huang KW - Transformation PY - 2007 SP - 1 EP - 14 CY - Washington, D.C., USA AN - OPUS4-17469 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - George, Janine A1 - Naik, Aakash A1 - Ueltzen, Katharina T1 - Reflections from the 2024 Large Language Model (LLM) Hackathon for Applications in Materials Science and Chemistry N2 - Here, we present the outcomes from the second Large Language Model (LLM) Hackathon for Applications in Materials Science and Chemistry, which engaged participants across global hybrid locations, resulting in 34 team submissions. The submissions spanned seven key application areas and demonstrated the diverse utility of LLMs for applications in (1) molecular and material property prediction; (2) molecular and material design; (3) automation and novel interfaces; (4) scientific communication and education; (5) research data management and automation; (6) hypothesis generation and evaluation; and (7) knowledge extraction and reasoning from scientific literature. Each team submission is presented in a summary table with links to the code and as brief papers in the appendix. Beyond team results, we discuss the hackathon event and its hybrid format, which included physical hubs in Toronto, Montreal, San Francisco, Berlin, Lausanne, and Tokyo, alongside a global online hub to enable local and virtual collaboration. Overall, the event highlighted significant improvements in LLM capabilities since the previous year's hackathon, suggesting continued expansion of LLMs for applications in materials science and chemistry research. These outcomes demonstrate the dual utility of LLMs as both multipurpose models for diverse machine learning tasks and platforms for rapid prototyping custom applications in scientific research. KW - Large Language Models KW - Materials Design KW - Materials Properties KW - Phonons KW - Bonding Analysis KW - Machine Learning PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-622113 DO - https://doi.org/10.48550/arXiv.2411.15221 SP - 1 EP - 98 AN - OPUS4-62211 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Zimmermann, Yoel A1 - Bazgir, Adib A1 - Al-Feghali, Alexander A1 - Ansari, Mehrad A1 - Bocarsly, Joshua A1 - Brinson, L. Catherine A1 - Chiang, Yuan A1 - Circi, Defne A1 - Chiu, Min-Hsueh A1 - Daelman, Nathan A1 - Evans, Matthew L. A1 - Gangan, Abhijeet S. A1 - George, Janine A1 - Harb, Hassan A1 - Khalighinejad, Ghazal A1 - Khan, Sartaaj Takrim A1 - Klawohn, Sascha A1 - Lederbauer, Magdalena A1 - Mahjoubi, Soroush A1 - Mohr, Bernadette A1 - Moosavi, Seyed Mohamad A1 - Naik, Aakash A1 - Ozhan, Aleyna Beste A1 - Plessers, Dieter A1 - Roy, Aritra A1 - Schöppach, Fabian A1 - Schwaller, Philippe A1 - Terboven, Carla A1 - Ueltzen, Katharina A1 - Wu, Yue A1 - Zhu, Shang A1 - Janssen, Jan A1 - Li, Calvin A1 - Foster, Ian A1 - Blaiszik, Ben T1 - 34 Examples of LLM Applications in Materials Science and Chemistry: Towards Automation, Assistants, Agents, and Accelerated Scientific Discovery N2 - Large Language Models (LLMs) are reshaping many aspects of materials science and chemistry research, enabling advances in molecular property prediction, materials design, scientific automation, knowledge extraction, and more. Recent developments demonstrate that the latest class of models are able to integrate structured and unstructured data, assist in hypothesis generation, and streamline research workflows. To explore the frontier of LLM capabilities across the research lifecycle, we review applications of LLMs through 34 total projects developed during the second annual Large Language Model Hackathon for Applications in Materials Science and Chemistry, a global hybrid event. These projects spanned seven key research areas: (1) molecular and material property prediction, (2) molecular and material design, (3) automation and novel interfaces, (4) scientific communication and education, (5) research data management and automation, (6) hypothesis generation and evaluation, and (7) knowledge extraction and reasoning from the scientific literature. Collectively, these applications illustrate how LLMs serve as versatile predictive models, platforms for rapid prototyping of domain-specific tools, and much more. In particular, improvements in both open source and proprietary LLM performance through the addition of reasoning, additional training data, and new techniques have expanded effectiveness, particularly in low-data environments and interdisciplinary research. As LLMs continue to improve, their integration into scientific workflows presents both new opportunities and new challenges, requiring ongoing exploration, continued refinement, and further research to address reliability, interpretability, and reproducibility. KW - Automation KW - LLM KW - Machine Learning KW - Agent KW - Bonding Analysis KW - Materials Searches KW - Finetuning PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-631720 DO - https://doi.org/10.48550/arXiv.2505.03049 SP - 1 EP - 33 AN - OPUS4-63172 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Ueltzen, Katharina A1 - Naik, Aakash A. A1 - Ertural, Christina A1 - Benner, Philipp A1 - George, Janine T1 - Can simple exchange heuristics guide us in predicting magnetic properties of solids? N2 - A popular heuristic derived from the Kanamori-Goodenough-Anderson rules of superexchange connects bond angles and magnetism in certain transition metal compounds. We evaluate the fulfillment of this heuristic on databases of magnetic structures. The heuristic is partly satisfied in magnetic structures from experiment, and exceptions can be rationalized. We further show that incorporating this heuristic into machine learning models for magnetism improves the prediction. KW - Magnetism KW - Transition Metal Compounds KW - Materials Design KW - Sustainable Materials Design KW - Machine Learning KW - Materials Understanding PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-639290 DO - https://doi.org/10.26434/chemrxiv-2025-xj84d VL - Version 1 SP - 1 EP - 43 AN - OPUS4-63929 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Liu, Yuanbin A1 - Morrow, Joe D. A1 - Ertural, Christina A1 - Fragapane, Natascia L. A1 - Gardner, John L. A. A1 - Naik, Aakash A1 - Zhou, Yuxing A1 - George, Janine A1 - Deringer, Volker L. T1 - An automated framework for exploring and learning potential-energy surfaces N2 - Machine learning has become ubiquitous in materials modelling and now routinely enables large-scale atomistic simulations with quantum-mechanical accuracy. However, developing machine-learned interatomic potentials requires high-quality training data, and the manual generation and curation of such data can be a major bottleneck. Here, we introduce an automated framework for the exploration and fitting of potential-energy surfaces, implemented in an openly available software package that we call autoplex ('automatic potential-landscape explorer'). We discuss design choices, particularly the interoperability with existing software architectures, and the ability for the end user to easily use the computational workflows provided. We show wide-ranging capability demonstrations: for the titanium-oxygen system, SiO2, crystalline and liquid water, as well as phase-change memory materials. More generally, our study illustrates how automation can speed up atomistic machine learning -- with a long-term vision of making it a genuine mainstream tool in physics, chemistry, and materials science. KW - Machine learned interatomic potentials KW - Ab initio KW - DFT KW - Automation KW - Workflows KW - Machine learning KW - Materials design KW - Materials discovery PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-623188 DO - https://doi.org/10.48550/arXiv.2412.16736 SN - 2331-8422 SP - 1 EP - 27 PB - Cornell University CY - Ithaca, NY AN - OPUS4-62318 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Amariamir, Sasan A1 - George, Janine A1 - Benner, Philipp T1 - SynCoTrain: A Dual Classifier PU-learning Framework for Synthesizability Prediction N2 - Material discovery is a cornerstone of modern science, driving advancements in diverse disciplines from biomedical technology to climate solutions. Predicting synthesizability, a critical factor in realizing novel materials, remains a complex challenge due to the limitations of traditional heuristics and thermodynamic proxies. While stability metrics such as formation energy offer partial insights, they fail to account for kinetic factors and technological constraints that influence synthesis outcomes. These challenges are further compounded by the scarcity of negative data, as failed synthesis attempts are often unpublished or context-specific. We present SynCoTrain, a semi-supervised machine learning model designed to predict the synthesizability of materials. SynCoTrain employs a co-training framework leveraging two complementary graph convolutional neural networks: SchNet and ALIGNN. By iteratively exchanging predictions between classifiers, SynCoTrain mitigates model bias and enhances generalizability. Our approach uses Positive and Unlabeled (PU) Learning to address the absence of explicit negative data, iteratively refining predictions through collaborative learning. The model demonstrates robust performance, achieving high recall on internal and leave-out test sets. By focusing on oxide crystals, a well-characterized material family with extensive experimental data, we establish SynCoTrain as a reliable tool for predicting synthesizability while balancing dataset variability and computational efficiency. This work highlights the potential of co-training to advance high-throughput materials discovery and generative research, offering a scalable solution to the challenge of synthesizability prediction. KW - Materials Design KW - Materials Discovery KW - Synthesizability KW - Machine Learning KW - Cotraining KW - New Materials KW - Materials Acceleration Platforms PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-622104 DO - https://doi.org/10.48550/arXiv.2411.12011 SP - 1 EP - 39 AN - OPUS4-62210 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Ganose, Alex A1 - Sahasrabuddhe, Hrushikesh A1 - Asta, Mark A1 - Beck, Kevin A1 - Biswas, Tathagata A1 - Bonkowski, Alexander A1 - Bustamante, Joana A1 - Chen, Xin A1 - Chiang, Yuan A1 - Chrzan, Daryl A1 - Clary, Jacob A1 - Cohen, Orion A1 - Ertural, Christina A1 - George, Janine A1 - Gallant, Max A1 - George, Janine A1 - Gerits, Sophie A1 - Goodall, Rhys A1 - Guha, Rishabh A1 - Hautier, Geoffroy A1 - Horton, Matthew A1 - Kaplan, Aaron A1 - Kingsbury, Ryan A1 - Kuner, Matthew A1 - Li, Bryant A1 - Linn, Xavier A1 - McDermott, Matthew A1 - Rohith Srinivaas Mohanakrishnan, A1 - Naik, Aakash A1 - Neaton, Jeffrey A1 - Persson, Kristin A1 - Petretto, Guido A1 - Purcell, Thomas A1 - Ricci, Francesco A1 - Rich, Benjamin A1 - Riebesell, Janosh A1 - Rignanese, Gian-Marco A1 - Rosen, Andrew A1 - Scheffler, Matthias A1 - Schmidt, Jonathan A1 - Shen, Jimmy-Xuan A1 - Sobolev, Andrei A1 - Sundararaman, Ravishankar A1 - Tezak, Cooper A1 - Trinquet, Victor A1 - Varley, Joel A1 - Vigil-Fowler, Derek A1 - Wang, Duo A1 - Waroquiers, David A1 - Wen, Mingjian A1 - Yang, Han A1 - Zheng, Hui A1 - Zheng, Jiongzhi A1 - Zhu, Zhuoying A1 - Jain, Anubhav T1 - Atomate2: Modular workflows for materials science N2 - High-throughput density functional theory (DFT) calculations have become a vital element of computational materials science, enabling materials screening, property database generation, and training of “universal” machine learning models. While several software frameworks have emerged to support these computational efforts, new developments such as machine learned force fields have increased demands for more flexible and programmable workflow solutions. This manuscript introduces atomate2, a comprehensive evolution of our original atomate framework, designed to address existing limitations in computational materials research infrastructure. Key features include the support for multiple electronic structure packages and interoperability between them, along with generalizable workflows that can be written in an abstract form irrespective of the DFT package or machine learning force field used within them. Our hope is that atomate2’s improved usability and extensibility can reduce technical barriers for high-throughput research workflows and facilitate the rapid adoption of emerging methods in computational material science. KW - Automation KW - DFT KW - Digitalisation KW - Materials design KW - Machine learning KW - Machine learned interatomic potentials PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-624487 DO - https://doi.org/10.26434/chemrxiv-2025-tcr5h SN - 2573-2293 SP - 1 EP - 66 PB - American Chemical Society (ACS) CY - Washington, D.C. AN - OPUS4-62448 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - VIDEO A1 - George, Janine T1 - Materials design using chemical heuristics, workflows, and machine learning N2 - Bonds and local atomic environments are key descriptors of material properties, used to establish design rules and heuristics, and serve as descriptors in machine-learned interatomic potentials and the general machine learning of material properties. Software implementations such as ChemEnv and LobsterEnv identify local atomic environments based on geometrical characteristics and quantum-chemical bonding analysis (here using Crystal Orbital Hamilton Populations as computed with LOBSTER). Fully automated workflows and analysis tools now enable large-scale quantum-chemical bonding analysis. The first part of the lecture will demonstrate how these tools help develop new machine-learning models and intuitive understandings of material properties. New universal machine-learned interatomic potentials, such as MACE-MP-0, have been developed. The second part of the lecture will showcase how these potentials, combined with DFT, can accelerate research. It will focus on the interplay between DFT and machine-learned interatomic potentials, presenting automated workflows for training, fine-tuning, and benchmarking these potentials, implemented in our software autoplex. Additionally, it will show how to train new interatomic potentials from scratch by exploring potential energy surfaces, with the potential to enhance current universal machine-learned potentials. The lecture will also discuss the trend toward automation in computational materials science and our recent contributions. T2 - FAIRmat Seminar CY - Berlin, Germany DA - 05.06.2025 KW - Materials Design KW - Machine Learning KW - Chemical Bonding KW - Batteries KW - Amorphous Materials KW - Workflows KW - Machine Learned Interatomic Potentials KW - Phonons KW - Magnetism KW - Synthesizability PY - 2025 UR - https://www.youtube.com/watch?v=Sfco48s1fpU PB - YouTube, LLC CY - San Bruno, CA, USA AN - OPUS4-63744 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Grandel, Jonas A1 - George, Janine T1 - Mace-mp-03b Phonon Benchmark N2 - This repository contains phonon calculations and evaluations for the MACE MP-0b3 model. First release of the scripts used for the phonon benchmark in the paper benchmarking the MACE-MP-03b model. See https://arxiv.org/abs/2401.00096 for a previous version of the paper. Full Changelog: https://github.com/JaGeo/mace-mp-03b-phonon-benchmark/commits/v0.0.1 KW - Machine Learned Interatomic Potentials KW - Phonons KW - Thermal Conductivity KW - Materials Searches KW - Foundation Model PY - 2025 DO - https://doi.org/10.5281/zenodo.15462975 PB - Zenodo CY - Geneva AN - OPUS4-63174 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Yang, Fan A1 - Meng, Xiangmeng A1 - Putra, Stephen Nugraha A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Assessment of keyhole stability in laser beam welding with external magnetic field using numerical simulation N2 - The challenge of understanding the physical mechanisms behind porosity reduction by a magnetic field during laser beam welding (LBW) is partly due to the difficulty in quantitatively evaluating keyhole stability. The commonly used index, such as keyhole depth, is typically one-dimensional, which is insufficient to capture the dynamic and three-dimensional fluctuations of the keyhole. In this paper, by utilizing a 3D multiphysical model of LBW with magnetic field, a novel keyhole geometry reconstruction algorithm has been developed to describe the keyhole profile and its fluctuation in a statistical manner to evaluate keyhole stability quantitatively. An equivalent diameter is proposed in this algorithm to reduce the irregularity of the keyhole geometry. The calculation results indicate that the time-averaged keyhole shape over 300 ms in the LBW of steel is conical, regardless of the application of an external magnetic field, which provides a more representative shape. Meanwhile, it is observed from the statistical aspect that the keyhole diameter becomes smaller, except the top part, under the influence of the magnetic field. The standard deviation of the equivalent diameter can be used as a physical variable to assess the keyhole stability quantitatively. The application of an external magnetic field can produce a noticeable reduction of the standard deviation of the equivalent diameter, namely, stabilizing the keyhole during LBW of steel. However, the different contribution from the keyhole stability affected by a magnetic field in suppressing porosity is different with materials. T2 - International Congress of Applications of Lasers & Electro-Optics 2024 CY - Hollywood, Los Angeles, USA DA - 04.11.2024 KW - Deep penetration laser beam welding KW - Numerical simulation KW - Keyhole shape KW - Keyhole stability KW - Magnetic field PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-616024 DO - https://doi.org/10.2351/7.0001528 VL - 36 IS - 4 SP - 1 EP - 7 PB - AIP Publishing AN - OPUS4-61602 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gleim, Tobias A1 - Monavari, Mehran A1 - Bertovic, Marija A1 - Wille, Frank T1 - AI-driven Documentation Analysis for Safety Assessment of Packages with Hazardous Goods N2 - Transport packages for radioactive material require, dependent on type und quantity of the radioactive material, a regulatory approval. Safety assessments shall be conducted in compliance with the IAEA regulations and documented in a comprehensive package design safety report to obtain approval from authority. This comprehensive safety report evaluates a broad range of requirements from the regulations, including physical specifications, control measures, and testing assessments. Additionally, it encompasses supporting documents such as specifications, plans in a variety of complex documents. Safety and manufacturing reports contain multiple interconnected sub-reports covering various topics. Changes, such as component modifications, material property updates, standards, or regulatory revisions, often impact multiple sections of the safety analysis reports, making even minor adjustments complex and time-consuming. Each transport package has unique constraints, making every safety report distinct, despite following the same regulatory framework. This project aims to enhance data analysis and processing through AI-based approaches [4]. Automated methods for analysing and interlinking documentation will improve efficiency, accuracy, and consistency while reducing human error in safety assessments. A key challenge is that pre-trained Large Language Models (LLMs) lack domain-specific data on packaging safety, potentially leading to inaccurate results. To mitigate this, the project applies Retrieval-Augmented Generation (RAG) in conjunction with LLMs. This approach integrates the strengths of pre-trained models with expert knowledge from databases and document repositories, ensuring accurate, well-founded, and transparent assessments. Beyond technical challenges, human factors must be considered early. New technologies often trigger resistance, if not introduced properly. Furthermore, long-term AI-reliance may lead to loss of expertise needed to solve complex problems. User-centred approach ensures effective implementation and lasting viability. This study evaluates the feasibility of using LLMs [2] and RAG [1, 3] for regulatory compliance in radioactive material transport. By analysing current documentation workflows, we assess how AI-driven tools can interpret complex safety reports and identify critical dependencies. Furthermore, we highlight the necessity of robust data governance, confidentiality measures, and AI reliability in this highly regulated domain. T2 - KONTEC 2025 CY - Dresden, Germany DA - 17.09.2025 KW - AI-driven KW - QI-Digital KW - Retrieval-Augmented Generation KW - Large Language Model PY - 2025 SP - 1 EP - 9 PB - Kontec Gesellschaft für technische Kommunikation GmbH CY - Dresden AN - OPUS4-64154 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lay, Vera A1 - Baensch, Franziska A1 - Johann, Sergej A1 - Sturm, Patrick A1 - Mielentz, Frank A1 - Prabhakara, Prathik A1 - Hofmann, Detlef A1 - Niederleithinger, Ernst A1 - Kühne, Hans-Carsten T1 - SealWasteSafe: materials technology, monitoring techniques, and quality assurance for safe sealing structures in underground repositories N2 - Within the project SealWasteSafe, we advance construction materials and monitoring concepts of sealing structures applied for underground disposal of nuclear or toxic waste. As these engineered barriers have high demands concerning integrity, an innovative alkali-activated material (AAM) is improved and tested on various laboratory scales. This AAM has low reaction kinetics related to a preferential slow release of the heat of reaction in comparison to alternative salt concretes based on Portland cement or magnesium oxychloride cements. Hence, crack formation due to thermally induced strain is reduced. After successful laboratory scale analysis (Sturm et al., 2021), the AAM is characterised on a larger scale by manufacturing test specimens (100–300 L). Conventional salt concrete (DBE, 2004) and the newly developed AAM are compared using two specimen geometries, i.e. cylindrical and cuboid. A comprehensive multisensor monitoring scheme is developed to compare the setting process of AAM and salt concrete for these manufactured specimens. The analysed parameters include temperature and humidity of the material, acoustic emissions, and strain variations. Passive sensor systems based on radiofrequency identification technology (RFID) embedded in the concrete, enable wireless access to temperature and humidity measurements and are compared to conventional cabled systems. Additionally, fibre-optic sensors (FOS) are embedded to record strain, but also have potential to record temperature and moisture conditions. Part of this project aims at demonstrating the high reliability of sensors and also their resistance to highly alkaline environments and to water intrusion along cables or at sensor locations. Further technical improvements were implemented so that first results clearly show the scalability of the setting process from previous small-scale AAM experiments and particularly the high potential of the newly developed approaches. Furthermore, ultrasonic methods are used for quality assurance to detect obstacles, potential cracks and delamination. On the one hand, both active and passive ultrasonic measurements complement the results obtained from the multisensor monitoring scheme for the produced specimens. On the other hand, the unique large aperture ultrasonic system (LAUS) provides great depth penetration (up to nearly 10 m) and can thus be applied at in situ sealing structures built as a test site in Morsleben by the Federal Company for Radioactive Waste Disposal (Bundesgesellschaft für Endlagerung, BGE) as shown by Effner et al. (2021). An optimised field lay-out identified from forward modelling studies and advanced imaging techniques applied to the measured data will further improve the obtained results. To characterise the inside of the test engineered barrier and achieve a proof-of-concept, an ultrasonic borehole probe is developed to enable phased arrays that can further improve the detection of potential cracks. Modelling results and first analysis of semispherical specimens confirmed the reliability of the directional response caused by the phased arrays of the newly constructed ultrasonic borehole probe. Overall, the project SealWasteSafe improves the construction material, multisensor monitoring concepts and ultrasonics for quality assurance. This will help to develop safe sealing structures for nuclear waste disposal. The outcomes are particularly valuable for salt as a host rock but partly also transferrable to alternative conditions. T2 - Safe ND Interdisciplinary research symposium on the safety of nuclear disposal practices CY - Berlin, Germany DA - 10.11.2021 KW - Borehole probe KW - SealWasteSafe KW - Engineered barrier KW - Materials technology KW - Monitoring KW - AAM KW - Ultrasound PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-539172 DO - https://doi.org/10.5194/sand-1-127-2021 VL - 1 SP - 127 EP - 128 PB - Copernicus AN - OPUS4-53917 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maack, Stefan A1 - Küttenbaum, Stefan A1 - Niederleithinger, Ernst T1 - Practical procedure for the precise measurement of geometrical tendon positions in concrete with ultrasonic echo N2 - Existing concrete structures were usually designed for lifetimes of several decades. The current and urgently required efforts to increase sustainability and protect the environment will likely result in extended service lives up to 100 years. To achieve such objectives, it is required to assess structures over their entire lifecycles. Non-destructive testing (NDT) methods can reliably support the assessment of existing structures during the construction, operational, and decommissioning phases. One of the most important and safety-relevant components of a prestressed concrete structure are the tendons. NDT methods such as the ultrasonic echo method are suitable for both the detection and the localization of the tendons, i.e., the measurement of their geometrical position inside the component. The uniqueness of structures, concrete heterogeneity, and varying amounts of secondary components such as the reinforcement represent obstacles in the application of these methods in practice. The aim of this contribution is to demonstrate a practicable procedure, that can be used in the field to determine the parameters required for the measuring data analysis without extensive knowledge about the investigated components. For this purpose, a polyamide reference specimen is used to show which steps are required to obtain reliable imaging information on the position of tendons from the measurement data. The procedure is then demonstrated on a concrete test specimen that covers various relevant and practice-oriented test scenarios, such as varying tendon depths and component thicknesses. T2 - International Conference on Concrete Repair, Rehabilitation and Retrofitting (ICCRRR 2022) CY - Cape Town, South Africa DA - 03.10.2022 KW - Validation KW - Non-destructive testing KW - Ultrasonic KW - Reconstruction KW - Concrete KW - Tendon duct PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-559979 DO - https://doi.org/10.1051/matecconf/202236403007 SN - 2261-263X SP - 1 EP - 8 AN - OPUS4-55997 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Lengas, Nikolaos T1 - Parameter study of impact targets in the drop test of packaging for dangerous goods N2 - Within the transportation chain, impact loading of dangerous goods packagings can happen. Thus, a package’s resistance against mechanical damage needs to be assessed. In the context of dangerous goods transport, drop tests are used for damage assessment as a part of packaging approval. Hence, a horizontal, flat unyielding surface must be provided to ensure maximum damage on impact and univocal test results. Leading adopted regulations like ADR/RID reference ISO 2248 to specify the requirements for the impact surface. The main requirement states that the impact surface must belong to an impact target with a mass at least 50 times higher than that of the heaviest package to be tested. However, many manufacturers in Germany, especially manufacturers of fibreboard boxes, do not have their own testing device with the required mass ratio for the drop test. Furthermore, the necessity of requirement revision has been addressed at UN level. It is unclear if mass ratio is the decisive criterion or if alternative design parameters can be defined to guarantee rigidity of the impact surface. The focus of the research reported in this thesis lays in the development and implementation of an analysis and testing concept for a comprehensive investigation of impact targets in drop testing. To this end, an experimental setup consisting of regulation compliant model impact targets is used in drop tests with two packaging types of significantly different mechanical properties. The variation of drop test parameters, such as the mass ratio, provides new insights into their respective significance in the drop test outcome. In addition, experimental findings are enhanced with numerical Finite-Element (FE) analyses to propose new improved criteria which incorporate all relevant influencing factors. In this way, firstly, critical impact target designs can be identified, and secondly, the kinetic energy of a real impact target in a drop test can be reliably approximated and compared to the respective theoretical threshold derived from a worst-case assumption. Thus, the rigid mass ratio currently specified in ISO 2248 can be regarded obsolete. The results of this work are highly beneficial for industrial application since they form the basis for introducing a standardized method for evaluating impact targets, replacing the 50 times mass ratio requirement. This would enable manufacturing and testing facilities to ensure a uniform level of safety assessment and to avoid the considerably high construction costs of impact targets with mass ratio of 1:50 in relation to packaging gross masses of several hundred kilograms. Hence, to make the results attained under laboratory conditions usable in practical application, preliminary investigations of the mechanical response of installed impact targets are conducted. For this purpose, important factors such as the interaction between impact target and ground in dynamic impact testing conditions are examined using validated FE models to establish an evaluation method. The investigations aim to create the basis for the revision of ISO 2248 and to define a standardized reference method for impact target characterization. KW - Drop test KW - Structural dynamics KW - Dangerous goods packaging KW - Mass ratio KW - Finite-element-method PY - 2025 DO - https://doi.org/10.14279/depositonce-24333 SP - 1 EP - 189 CY - Berlin AN - OPUS4-64090 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bakir, Nasim A1 - Artinov, Antoni A1 - Gumenyuk, Andrey A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Numerical simulation on the origin of solidification cracking in laser welded thick-walled structures N2 - One of the main factors affecting the use of lasers in the industry for welding thick structures is the process accompanying solidification cracks. These cracks mostly occurring along the welding direction in the welding center, and strongly affect the safety of the welded components. In the present study, to obtain a better understanding of the relation between the weld pool geometry, the stress distribution and the solidification cracking, a three-dimensional computational fluid dynamic (CFD) model was combined with a thermo-mechanical model. The CFD model was employed to analyze the flow of the molten metal in the weld pool during the laser beam welding process. The weld pool geometry estimated from the CFD model was used as a heat source in the thermal model to calculate the temperature field and the stress development and distributions. The CFD results showed a bulging region in the middle depth of the weld and two narrowing areas separating the bulging region from the top and bottom surface. The thermo-mechanical simulations showed a concentration of tension stresses, transversally and vertically, directly after the solidification during cooling in the region of the solidification cracking. T2 - 27TH INTERNATIONAL CONFERENCE ON METALLURGY AND MATERIALS - METAL 2018 CY - Brno, Czech Republic DA - 23.05.2018 KW - Laser beam welding KW - Weld pool KW - Full penetration KW - Finite element method (FEM) KW - CFD model KW - Numerical simulation KW - Solidification cracking PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-450595 DO - https://doi.org/10.3390/met8060406 SN - 2075-4701 VL - 8 IS - 6 SP - 406, 1 EP - 15 PB - MDPI CY - Basel, Switzerland AN - OPUS4-45059 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niederleithinger, Ernst A1 - Herbrand, Martin A1 - Müller, Matthias T1 - Codawelleninterferometrie zur Detektion von Spannungszuständen in Betonbauteilen N2 - Informationen zu in Betonbauteilen stattfindenden Umlagerungsprozessen sowie Druckspannungsverteilungen können mit konventioneller Messtechnik bislang nicht zweifelsfrei beantwortet werden. Ultraschallmessungen mit eingebetteten Sensoren könnten hier eine sinnvolle Ergänzung zur konventionellen Messtechnik sein. Durch Einsatz der Codawelleninterferometrie (CWI) sind hiermit schon sehr kleine Änderungen im Material detektierbar. Um diese neue Methodik zu evaluieren, wurde das Forschungsprojekt „Querkrafttragfähigkeit von Spannbetonbrücken – Erfassung von Spannungszuständen in den Spannbetonversuchsträgern mit Ultraschallsensoren“ durch die Bundesanstalt für Straßenwesen (BASt) initiiert. In diesem Projekt wurden durch die Bundesanstalt für Materialforschung und –prüfung (BAM) Ultraschall-Transducer in mehrere Spannbetonträger des Instituts für Massivbau der RWTH Aachen eingebettet, die anschließend bis zum Bruch belastet wurden. Der Belastungsversuch an einem der Spannbetondurchlaufträger zeigte das große Potential dieser Methodik. Die im Netzwerk erfassten Änderungen der Ultraschallwellengeschwindigkeit geben die Spannungsverhältnisse im Längsschnitt des Trägers schon bei sehr niedrigen Belastungen qualitativ richtig wieder und zeigen bei hohen Belastungen eine gute Korrelation zum Rissbild. Dabei weisen räumliche Anomalien und Änderungen in der Charakteristik der Geschwindigkeitsänderungen oft schon auf Rissbildung hin, wenn diese noch nicht an der Oberfläche sichtbar ist. Dies zeigt das Potential im Hinblick auf eine Frühwarnung. Hierfür und ebenso in Bezug auf eine Quantifizierung der Effekte ist aber noch Entwicklungsarbeit notwendig. Ein Vorteil der Methodik ist, dass die Transducer nicht direkt am Ort der Änderung platziert werden müssen und einen relativ großen Bereich um die Transducer herum erfassen. T2 - DGZfP Jahrestagung 2018 CY - Leipzig, Germany DA - 07.05.2018 KW - Ultraschall KW - Monitoring KW - Codawelleninterferometrie KW - Brückenträger PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-448642 SP - Mo.3.A.4, 1 EP - 8 PB - DGZfP AN - OPUS4-44864 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Coelho Lima, Isabela A1 - Grohmann, Maria A1 - Niederleithinger, Ernst T1 - Advanced ultrasonic imaging for concrete: Alternative imaging conditions for reverse time migration N2 - Ultrasound echo is a widely used NDT technique for determining the internal geometry of structures. Reverse-time migration (RTM) has been recently introduced to NDT applications, as an imaging method for ultrasound data, to overcome some of the limitations (e.g. imaging steeply dipping reflector) experienced by the Synthetic Aperture Focusing Technique (SAFT), the most commonly used imaging algorithm for these measurements. The standard implementation of RTM also experiences some drawbacks caused by its imaging condition, which is based on the zero-lag of the cross-correlation between source and receiver wavefields and generates high-amplitude low-frequency artifacts. Three alternative imaging conditions, developed for seismic data applications, were tested for their ability to provide better images than the standard cross-correlation: illumination compensation, deconvolution and wavefield decomposition. A polyamide specimen was chosen for the simulation of a synthetic experiment and for real data acquisition. The migrations of both synthetic and real data were performed with the software Madagascar. The illumination imaging condition was able to reduce the low-frequency noise and had a good performance in terms of computing time. The deconvolution improved the resolution in the synthetic tests, but did not showed such benefit for the real experiments. Finally, as for the wavefield decomposition, although it presented some advantages in terms of attenuating the low-frequency noise and some unwanted reflections, it was not able to image the internal structure of the polyamide as well as the cross-correlation did. Suggestions on how to improve the cost-effectiveness of the implementation of the deconvolution and wavefield decomposition were presented, as well as possible investigations that could be carried out in the future, in order to obtain better results with those two imaging conditions. T2 - DGZfP Jahrestagung 2018 CY - Leipzig DA - 07.05.2018 KW - Ultrasound KW - Reverse time migration KW - Imaging condition KW - Concrete PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-448704 SP - Mi.3.A.4, 1 EP - 10 PB - DGZfP AN - OPUS4-44870 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niederleithinger, Ernst A1 - Wiggenhauser, Herbert A1 - Milmann, Boris T1 - LAUS - Erste praktische Erfahrungen mit einem neuartigen Ultraschallsystem großer Eindringtiefe N2 - Konventionelle Systeme zur Ultraschall-Echo-Prüfung von Betonbauteilen sind in ihrer Eindringtiefe auf etwa einem Meter begrenzt. Zur Prüfung stärkerer Objekte war die Entwicklung eines neuartigen Prüfsystems notwendig. Das LAUS-System (Large Aperture UltraSound) besteht aus 12 einzelnen Arrays, die mit jeweils 32 Einzelprüfköpfen (Scherwellen, 25 – 50 kHz) als Sender oder Empfänger betrieben werden können. Sie werden unabhängig auf Betonoberflächen mit Unterdruck befestigt und kommunizieren drahtlos untereinander und mit der Zentraleinheit. Alle möglichen Kombinationen ergeben 132 Einzelmessungen, die zur Rekonstruktion des durchschallten Volumens genutzt werden. Mehrere dieser Datensätze lassen sich zu einer 3D-Auswertung kombinieren. Das System wurde an mehreren Testobjekten und Bauwerken erfolgreich erprobt. So konnte die fünf Meter dicke, sehr stark bewehrte Fundamentplatte des Fallturms auf dem BAM-Testgelände bei Horstwalde durchschallt werden. Ein zweites Beispiel ist die erfolgreiche Detektion von Spannkanälen in 1,8 m Tiefe in einem massiven Brückenbauwerk. T2 - Fachtagung Bauwerksdiagnose 2018 CY - Berlin DA - 15.2.2018 KW - Beton KW - Ultraschall KW - LAUS KW - Brücke KW - Fundament PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-445786 UR - https://www.bauwerksdiagnose2018.de/Portals/bauwerksdiagnose2018/BB/16.pdf SP - Paper 16, 1 EP - 8 CY - Berlin AN - OPUS4-44578 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Niederleithinger, Ernst A1 - Wang, Xin A1 - Mierschke, Vivien A1 - Bertschat, Anja Sophie T1 - Concepts from seismic interferometry transferred to sonic and ultrasonic concrete inspection and monitoring N2 - Seismic interferometry (SI) deals either with the sensible detection of changes in the subsurface or with the reconstruction of virtual signals between two receivers by crosscorrelation of signals from diffuse sources. These concepts can be applied in NDT in civil engineering for various purposes, e. g. to detect changes in bridges. Here it is demonstrated using data from a reference structure on our test site. Practical applications can be expected in the very near future. T2 - 12th European Conference on Non-Destructive Testing (ECNDT 2018) CY - Gothenburg, Sweden DA - 11.6.2018 KW - Ultrasound KW - Concrete KW - Monitoring KW - Coda KW - Interferometry PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-468465 UR - http://www.ndt.net/?id=22760 SN - 1435-4934 VL - 23 IS - 8 SP - 1 EP - 2 PB - NDT.net CY - Kirchwald AN - OPUS4-46846 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Biegler, M. A1 - Wang, J. A1 - Kaiser, L. A1 - Rethmeier, Michael T1 - Automated Tool-Path Generation for Rapid Manufacturing of Additive Manufacturing Directed Energy Deposition Geometries N2 - In additive manufacturing (AM) directed energy deposition (DED), parts are built by welding layers of powder or wire feedstock onto a substrate with applications for steel powders in the fields of forging tools, spare parts, and structural components for various industries. For large and bulky parts, the choice of toolpaths influences the build rate, the mechanical performance, and the distortions in a highly geometry-dependent manner. With weld-path lengths in the range of hundreds of meters, a reliable, automated tool-path generation is essential for the usability of DED processes. This contribution presents automated tool-path generation approaches and discusses the results for arbitrary geometries. Socalled “zig-zag” and “contour-parallel” processing strategies are investigated and the tool-paths are automatically formatted into machine-readable g-code for experimental validation to build sample geometries. The results are discussed in regard to volume-fill, microstructure, and porosity in dependence of the path planning according to photographs and metallographic cross-sections. KW - Porosity KW - Path planning KW - Mechanical properties KW - Laser metal deposition KW - Additive manufacturing PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-510454 DO - https://doi.org/10.1002/srin.202000017 VL - 91 IS - 11 SP - 2000017 PB - WILEY-VCH Verlag GmbH & co. KGaA CY - Weinheim AN - OPUS4-51045 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mielentz, Frank A1 - Stolpe, Heiko A1 - Effner, Ute A1 - Behrens, Matthias A1 - Bernstein, Thomas A1 - Niederleithinger, Ernst T1 - Entwicklung einer Bohrlochsonde für Ultraschalluntersuchungen an Abschlussbauwerken in Endlagern N2 - Für die Qualitätssicherung von Abschlusswerken für Endlager wird eine Ultraschall-Bohrlochsonde entwickelt. Mithilfe dieser Sonde, die aus einer Vielzahl von einzelnen koppelmittelfreien Ultraschall-Punktkontaktprüfköpfen besteht, soll die Rissfreiheit der Versuchsbauwerke überprüft werden. Ein erster Prototyp der Sonde wurde mit einem kommerziellen Ultraschallgerät betrieben und bestand aus 12 Transversalwellen-Punktkontaktprüfköpfen von denen jeweils sechs als Sender und sechs als Empfänger parallelgeschaltet waren. Um den erzeugten Schalldruck der Bohrlochsonde zu steigern, wurde bei der Neuentwicklung die Prüfkopfanzahl erhöht und zusätzlich die laufzeitgesteuerte Anregung der einzelnen Prüfköpfe vorgesehen. Für die Anregung der Prüfköpfe mit programmierten Zeitverzögerungen wurde ein neuartiger mehrkanaliger Sender für bipolare Rechtecksignale entwickelt. Durch die Entwicklung der Bohrlochsonde soll eine dynamische Anpassung der Prüfkopf-Apertur sowie eine Fokussierung des Schallfeldes in Abhängigkeit der zu untersuchenden Tiefe erfolgen. Mithilfe entsprechender Anregungsfunktionen kann das Schallfeld der Bohrlochsonde unterschiedlich geformt werden, z. B. ist auch ein Schwenken des fokussierten Schallbündels möglich. Dadurch wird das erfasste Prüfvolumen begrenzt und auf diese Weise das Signal-Störverhältnis der Empfangssignale verbessert. In Kombination mit SAFT-Rekonstruktionsrechnungen wird durch eine optimierte Abstrahlcharakteristik der Sonde mit einem hohen Schalldruck unter verschiedenen Winkeln eine verbesserte Signalqualität und damit eine erhöhte Aussagesicherheit der Ergebnisse in der Objektabbildung erwartet. T2 - DGZfP-Jahrestagung 2021 CY - Online meeting DA - 10.05.2021 KW - Abdichtbauwerk KW - Bohrlochsonde KW - Ultraschall-Echoverfahren KW - Verschlussbauwerk KW - Zerstörungsfreie Prüfung KW - Ultraschall-Messtechnik PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-526746 UR - https://jahrestagung.dgzfp.de/portals/jt2021/bb176/inhalt/poster.htm SN - 978-3-947971-18-3 VL - 176 SP - 1 EP - 7 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-52674 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Arndt, R.W. A1 - Grosse, C.U, A1 - Maehner, D. A1 - Niederleithinger, Ernst A1 - Taffe, A. A1 - Algernon, D. A1 - Berger, J. A1 - Kessler, S. A1 - Krueger, M. A1 - Kruschwitz, Sabine A1 - Ufermann-Wallmeier, D. A1 - Walther, A. T1 - Non-destructive testing in civil engineering: A memorandum for teaching at German-speaking universities N2 - This contribution summarizes actual developments and draft fundamental teaching topics in the field of nondestructive testing in civil engineering (NDT-CE). It is based on the first memorandum on teaching and research in the field of NDT-CE at German speaking universities and provides an overview of the academic education and highlights possible focuses, especially in teaching but also takes into account noteworthy developments and topics in research in the field of NDT-CE. Suggestions are given for the development and advancement of the teaching curricula in regards to a comprehensive and sound professional education of students in civil engineering and adjacent disciplines. T2 - NDT-CE 2022 CY - Zurich, Switzerland DA - 16.08.2022 KW - Curriculum KW - NDT-CE KW - University KW - Competencies PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-563269 UR - https://www.ndt.net/article/ndtce2022/paper/61547_manuscript.pdf SP - 1 EP - 10 PB - NDT.net AN - OPUS4-56326 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Epple, Niklas A1 - Niederleithinger, Ernst A1 - Fontoura Barroso, Daniel T1 - Coda Wave Interferometry for Monitoring Bridges with Embedded Ultrasonic Transducers – Lessons Learned at the Gänstorbrücke Bridge Ulm, Germany N2 - Ultrasonic Coda Wave interferometry has the potential to detect minute changes in scattering materials like concrete. By permanently installing ultrasonic transducers in concrete, DFG Research unit CoDA aims to develop methods for concrete damage assessment in Germany's aging infrastructure. To test the methods developed in simulations and laboratory experiments on a large scale, we have implemented several ultrasonic transducers at the Gänstorbrücke Ulm, one of Germany's most monitored road bridges. Since fall 2020 we are monitoring parts of the center of the Bridge, as well as an abutment, and compare the results to the commercial monitoring system. All data is recorded with a self-made data collection device, the so-called W-Box, and analyzed with different coda wave-based algorithms to detect signal and volumetric velocity changes. The long-term measurements show that the influence of temperature changes on strains and therefore ultrasound velocity changes calculated with coda waves can be monitored. The capabilities and limitations of the coda wave-based monitoring system are tested in a controlled experiment. Static loading using a truck with varying loads at several positions allows the calibration of the system to improve the detectability of possibly damaging loads and changes induced by this loading. A map of velocity change analyzing data from this load experiment shows that the influence of load on the material and strain distribution can be detected with array measurements. T2 - NDT-CE 2022 - The International Symposium on Nondestructive Testing in Civil Engineering CY - Zurich, Switzerland DA - 16.08.2022 KW - Coda Wave Interferometry KW - Ultrasound KW - Embedded sensors KW - Bridge Monitoring KW - Load Experiment PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-564531 SP - 1 EP - 8 AN - OPUS4-56453 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rabe, U. A1 - Pudovikov, S. A1 - Herrmann, H.-G. A1 - Wiggenhauser, H. A1 - Prabhakara, Prathik A1 - Niederleithinger, Ernst T1 - Evaluation of retroreflective corner echo for detection of surface breaking cracks in concrete by ultrasound N2 - The retroreflective corner echo is used, for example, in ultrasonic non-destructive testing of metals to find fatigue cracks in tubes or shafts. If the much weaker crack tip signal is additionally detected, the crack length can also be determined. A corner reflection occurs in cases of surface breaking cracks with predominantly perpendicular orientation to the surface. The intensity of the corner reflection depends on the angle of incidence and on the ultrasonic wave mode used. For the reliable detection of vertical surface breaking cracks in metals, transversal waves are commonly used, which propagate at an angle of 37° to 53° to the inspection surface. As shown in this contribution, the wide spread low frequency ultrasonic arrays with dry point contact sources available for ultrasonic testing of concrete also allow to receive corner echoes. These devices generate transversal waves in concrete structures with a large divergence of the sound field. A series of experiments was carried out with such dry point contact arrays on concrete specimens with artificial test defects and controlled induced cracks of different depths. The ultrasonic time-of-flight signals were recorded, exported and reconstructed utilising the SAFT (Synthetic Aperture Focusing Technique) algorithm. The SAFT reconstruction parameters were adjusted to visualize the corner echo indication. As will be shown, with this targeted processing, the reproducible detection of surface breaking cracks in concrete is possible. The retroreflective corner echo can thus be exploited in civil engineering for non-destructive inspection of concrete. T2 - NDT-CE 2022 CY - Zurich, Switzerland DA - 16.08.2022 KW - Concrete KW - Crack depth KW - Ultrasound KW - SAFT PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-563365 UR - https://www.ndt.net/article/ndtce2022/paper/27256_manuscript.pdf IS - 27256 SP - 1 EP - 4 PB - NDT.net AN - OPUS4-56336 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Landis, E. A1 - Hassefras, Emiel A1 - Oesch, Tyler A1 - Niederleithinger, Ernst T1 - A Microstructural Basis for Diffuse Ultrasound in Concrete N2 - Attenuation of ultrasonic signals in concrete has the potential to carry much information about the microstructure of the material. In this work a series of concrete specimens of varying porosities and pore size distributions were internally imaged with x-ray computed tomography (CT), and then subsequently examined with throughtransmission ultrasound. The CT images were used to quantify both capillary porosity of cement paste as well as internal interfaces that are likely to produce elastic wave scattering. Ultrasound signals were represented as a diffusion process such that absorption and scattering attenuation could be isolated. As implemented, the diffusion model was a poor predictor of capillary porosity, while diffusivity was a reasonable predictor of scattering interfaces. Diffusivity was found to scale extremely well with small scale porosity, which made it a good predictor of compressive strength. T2 - NDT-CE 2022 CY - Zurich, Switzerland DA - 16.08.2022 KW - Concrete KW - X-ray tomography KW - Ultrasound PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-563371 UR - https://www.ndt.net/article/ndtce2022/paper/61592_manuscript.pdf SP - 1 EP - 4 PB - NDT.net AN - OPUS4-56337 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schumacher, T. A1 - Niederleithinger, Ernst T1 - Combining Passive and Active Ultrasonic Stress Wave Monitoring Techniques: Opportunities for Condition Evaluation of Concrete Structures N2 - Concrete structures are invaluable assets to a society and managing them efficiently and effectively can be supported by information gathered through structural health monitoring (SHM). In this paper, a combined approach based on passive, i.e., acoustic emission (AE), and active, i.e., ultrasonic stress wave (USW) monitoring techniques for application to concrete structures is proposed and evaluated. While AE and USW are based on the same underlying physics, i.e., wave motion in solids, they differ fundamentally with respect to the nature of the source. For the former, external stimuli such as mechanical loads or temperature cause the rapid release of energy from initially unknown locations. As a result, AE events are unique and cannot be repeated. For the latter, a known source at a known location is employed at a specified time. This approach is thus controlled and repeatable. It is argued that a combination of these two techniques has the potential to provide a more comprehensive picture of ongoing fracture processes, damage progression, as well as slowly occurring aging and degradation mechanisms. This combined approach does thus promise new opportunities to support condition assessment of concrete structures. After providing an overview and comparison of the two techniques, results, and observations from a full-scale laboratory experiment and an in-service bridge monitoring study are discussed to demonstrate the promise of the proposed combined monitoring approach. Finally, suggestions for further work are presented. T2 - NDT-CE 2022 CY - Zurich, Switzerland DA - 16.08.2022 KW - Ultrasound KW - Acoustic emission KW - Concrete structures KW - Monitoring PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-563242 UR - https://www.ndt.net/article/ndtce2022/paper/61607_manuscript.pdf SP - 1 EP - 11 PB - NDT.net AN - OPUS4-56324 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Feistkorn, S. A1 - Algernon, D. A1 - Arndt, R. A1 - Ebell, Gino A1 - Friese, M. A1 - Grosse, C. U. A1 - Holstein, R. A1 - Niederleithinger, Ernst A1 - Schickert, M. A1 - Schulze, S. A1 - Taffe, A. A1 - Walther, A. A1 - Wolf, J. A1 - Zoega, A. A1 - Zwanzig, M. T1 - Introduction to DIN 4871: Qualification of NDT Personnel in Civil Engineering (NDT-CE) N2 - Recently, non-destructive testing in civil engineering (NDT-CE), in particular of concrete components, has successfully mastered the leap from research to practice. Several methods have been established for field inspections to determine the concrete cover of reinforcement or to estimate the compressive strength as well as other parameters related to the concrete material. In addition, the application of nondestructive testing is indispensable, if information about the inner structure - such as the location of rebars and tendon ducts or the damage-related condition assessment to detect grouting defects, honeycombs, delamination, or corrosion - is required. Besides the selection of a suitable NDT method and an appropriate inspection system, the reliability of the results depends largely on the person who applies the non-destructive inspection technique and evaluates the inspection results. To ensure a high quality of non-destructive concrete evaluation as well as to keep the uncertainty caused by the inspection personnel to a minimum, structured, consistent and regulated theoretical as well as practical training of inspection personnel is essential. To close this gap, the subcommittee of education (UA-A) within the committee for NDT-CE of the German Society for Nondestructive Testing (DGZfP) has been reactivated in 2018 to establish uniform training standards for nondestructive concrete inspections in the long term. The subcommittee consists of scientists, practitioners, authorities, and clients. So far, the national standard DIN 4871 “Non-destructive testing - Qualification and Certification of NDT personnel in Civil Engineering (NDT-CE)” was developed and is currently under review. This standard considers the civil-industry-specifics, for example, that standards for NDT of concrete, as well as related product standards with a few exceptions, still do not exist at the moment. Within this presentation, the concept, the connection to ISO 9712 and other standards as well as an overview of the developed German standard DIN 4871 will be presented. T2 - NDT-CE 2022 CY - Zurich, Switzerland DA - 16.08.2022 KW - Non-destrucive testing KW - Civil engineering PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-555250 UR - https://www.ndt.net/article/ndtce2022/paper/66594_manuscript.pdf VL - 2022/09 SP - 1 EP - 12 PB - NDT.net CY - Bad Breisig AN - OPUS4-55525 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niederleithinger, Ernst A1 - Guangliang, Y. A1 - Mahon, D. A1 - Gardner, S. T1 - Muon tomography applied to assessment of concrete structures: First experiments and simulations. N2 - Non-destructive techniques for reinforced or prestressed concrete inspection such as ultrasound or radar have found regular, successful practical application but sometimes suffer from limited resolution and accuracy, imaging artefacts or restrictions in detecting certain features. Until the 1980s X-ray transmission was used in case of special demands and showed a much better resolution than other NDT techniques. However, due to safety concerns and cost issues, this method is almost never used anymore. Muon tomography has received much attention recently. Novel detectors for cosmic muons and tomographic imaging algorithms have opened new fields of application. As a first step towards practical application in civil engineering and as a proof of concept we used an existing system to image the interior of a reference reinforced 600 kg concrete block. Even with a yet not optimized setup for this kind of investigation, the muon imaging results are at least of similar quality compared to ultrasonic and radar imaging, potentially even better. In a second step, we have performed simulations to assess the potential for a set of important testing problems such as grouting defects in tendon ducts. The next steps include the development of mobile detectors and optimizing acquisition and imaging parameters. T2 - NDT-CE 2022 CY - Zurich, Switzerland DA - 16.08.2022 KW - Muon tomography KW - Concrete KW - Inspection KW - Simulation PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-563224 UR - https://www.ndt.net/article/ndtce2022/paper/60943_manuscript.pdf SP - 1 EP - 8 PB - NDT.net AN - OPUS4-56322 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lay, Vera A1 - Effner, Ute A1 - Niederleithinger, Ernst A1 - Arendt, J. A1 - Kudla, W. T1 - Ultrasonic quality assurance for underground salt shotcrete sealing structures in Teutschenthal mine, Germany N2 - Underground sealing structures are necessary to seal radioactive or toxic waste in underground repositories. A special version of MgO concrete is used in the mine in Teutschenthal and applied at a large-scale test with the aim to provide a low permeability barrier. The test structures (up to 10 m long) were created by shotcreting. Besides destructive tests, non-destructive ultrasonic measurements have been evaluated for quality assurance to monitor potential anomalies such as cracks, concrete inhomogeneities, and delamination. We show results of ultrasonic measurements with a multi-transducer system used at the front and from the side of the concrete structure. Images are obtained by synthetic aperture focusing techniques. The boundaries between concreting sections are not visible in the ultrasonic images systematically so that a successful concreting is assumed, which is confirmed by the low permeabilities observed. Several reflectors up to a depth of 1.2 m are identified and interpreted as potential damages in the concrete. Phase analysis of prominent reflectors reveal a negative impedance contrast thus indicating air filled voids, cracks or delamination. Boreholes through some of the identified reflectors are used to verify the results from ultrasonic measurements. Additionally, an experiment with incorporated artificial defects was undertaken to analyse the reliability of the applied methods. Overall, the conducted tests show the potential of ultrasonic measurements to detect critical anomalies. Despite challenges at small-scale structures (cm-order), large-scale anomalies can be identified. Consequently, implementing ultrasonic monitoring during and after the construction of concrete sealing structures has shown its potential as a tool for quality assurance, but needs further development and validation. T2 - NDT-CE 2022 CY - Zurich, Switzerland DA - 16.08.2022 KW - Ultrasound KW - Ultrasonic imaging KW - Magnesia shotcrete KW - Underground KW - Engineered barrier systems PY - 2022 UR - https://www.ndt.net/events/proceedings/topic.php?eventID=292&TopicID=27209 SP - 1 EP - 4 PB - NDT.net AN - OPUS4-55824 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Abraham, O. A1 - Niederleithinger, Ernst A1 - Schmidt, F. A1 - Sörensen, J.D. A1 - Thöns, S. A1 - Chapeleau, X. A1 - Ferria, H. T1 - Infrastar Training School on Fatigue and Reliability Analysis of Structures - Training for Assessment of Risk N2 - The Infrastar training school provides lectures and hands-on training to Master and PhD students, early-stage researchers and (young) professionals on all aspects of asset management of civil infrastructures with respect to fatigue of materials. It is organized yearly since 2019 and up to 20 profiles are selected to attend the 3.5-day training. A team of 7 teachers provides insight in multi-disciplinary and intersectoral basic concepts in three core fields, ranging from the design to the dismantling of the structures (bridges and wind turbines): 1. Monitoring and auscultation, 2. Structural and action models, 3. Reliability, risk and decision analyses. Each year, a recognized expert is invited to deliver a keynote lecture to raise interest in a specific aspect of one of the fields covered. The presentation is recorded and published on the training school website. T2 - NDT-CE 2022 CY - Zurich, Switzerland DA - 16.08.2022 KW - Doctoral School KW - Multidisciplinary KW - Fatigue KW - Reliability PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-563253 UR - https://www.ndt.net/article/ndtce2022/paper/61021_manuscript.pdf SP - 1 EP - 3 PB - NDT.net AN - OPUS4-56325 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Prabhakara, Prathik A1 - Mielentz, Frank A1 - Stolpe, Heiko A1 - Behrens, Matthias A1 - Lay, Vera A1 - Niederleithinger, Ernst T1 - Construction and validation of a novel phased array borehole probe for ultrasonic investigations at sealing structures in radioactive repositories N2 - A new type of ultrasonic borehole probe is currently under development for the quality assurance of sealing structures in radioactive waste repositories using existing research boreholes. The goal is to examine the sealing structures made of salt concrete for possible cracks, delamination, and embedded objects. Earlier prototype probes use 12 or 16 individual dry point contact (DPC) horizontal shear wave transducers grouped into a transmitter and a receiver array, each made up of six or eight individual transducers. They are operated with a commercially available portable ultrasonic flaw detector used in the civil engineering industry. To increase the generated sound pressure of the borehole probe, the number of transducers in the novel probe is increased to 32. In addition, timed excitation of each probe is used to direct a focused sound beam to a specific angle and distance based on calculated time delays. Hence, the sensitive test volume is limited, and the signal-to-noise ratio of the received signals is improved. This paper presents the validation of the newly developed phased array borehole probe by beam computation in CIVA software and experimental investigations on a semi-cylindrical test specimen to investigate the directional characteristics. In combination with geophysical reconstruction techniques, an optimised radiation pattern of the probe is expected to improve the signal quality and thus increase the reliability of the imaging results. This is of great importance for the construction of safe sealing structures needed for the disposal of radioactive or toxic waste. T2 - NDT-CE 2022 CY - Zurich, Switzerland DA - 16.08.2022 KW - Borehole probe KW - Phased array technique KW - SealWasteSafe KW - Monitoring KW - Engineered barrier; PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-568016 SN - 1435-4934 SP - 1 EP - 4 PB - NDT.net AN - OPUS4-56801 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lay, Vera A1 - Mielentz, Frank A1 - Prabhakara, Prathik A1 - Baensch, Franziska A1 - Johann, Sergej A1 - Hofmann, Detlef A1 - Sturm, Patrick A1 - Stamm, Michael A1 - Niederleithinger, Ernst T1 - Multi-sensory monitoring and ultrasound for quality assurance at underground sealing structures N2 - Within the safety concepts of underground disposal sites of nuclear waste, engineered barriers play an important role. As these sealing structures have high demands concerning integrity, we aim at advancing the available construction materials, monitoring, and inspection techniques within the project SealWasteSafe. A specifically developed alkali-activated material is compared to classical salt concrete. A comprehensive multi-sensory monitoring scheme is used at 150-340 l specimens to monitor setting and hardening of both materials. All sensors are demonstrated to resist the highly alkaline environments. Besides cabled and wireless temperature and humidity of the materials, strain variations using fibre optic sensors and acoustic emissions are recorded over periods of at least 28 days, partly for more than eight months. After hardening of the specimens, further nondestructive evaluations using ultrasonic echo and thermographic measurements are conducted. Preliminary results proof the suitability of the tested sensors and clearly highlight differences between the tested materials. Particularly, the newly developed alkali-activated material shows lower acoustic emission activity indicating less cracking activity. Additionally, unique ultrasonic methods will enable better images of potential internal objects and cracks at in-situ sealing structures. A largescale ultrasonic system is optimised to reliably detect objects at a depth exceeding 9 m while still obtaining a good resolution. Modelling studies show the potential of further increasing the distance between individual transducer arrays. Additionally, a new ultrasonic borehole probe using phased arrays allowing for beam focussing is constructed and tested. Laboratory measurements at a halfcylindrical concrete specimen coincide well with the previous modelling. In total, the presented safe materials, detailed monitoring approaches and ultrasonic quality assurance methods will help to obtain safe sealing structures within salt as a host rock. The concepts can partly be transferred to sealing structures in alternative host rocks and will also be valuable for non-nuclear waste repositories. T2 - NDE NucCon CY - Espoo, Finland DA - 25.01.2023 KW - SealWasteSafe KW - Engineered barriers KW - Monitoring KW - Embedded sensors KW - Ultrasonic imaging PY - 2023 SP - 2 EP - 10 AN - OPUS4-56928 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Maack, Stefan T1 - Low-frequency ultrasound data (pulse-echo technique) with shear horizontal and longitudinal waves on a reference polyamide specimen “BAM-Pk218” N2 - This dataset contains raw data observed with ultrasound measurements on a polyamide reference specimen at Bundesanstalt für Materialforschung und -prüfung (BAM), Berlin. The internal specimen identifier is „Pk218“. The measurements were conducted using the pulse-echo method. KW - Nondestructive testing KW - Ultrasound KW - Pulse-echo technique KW - Validation KW - Reference material KW - Reconstruction algorithm PY - 2022 DO - https://doi.org/10.7910/DVN/KVN7CY PB - Harvard College CY - Cambridge, MA, USA AN - OPUS4-54959 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bahrami Eskandari, Ardalan A1 - Küttenbaum, Stefan T1 - NDT Data-Supported Structural Reassessments based on Regression Relations in Measuring Data Analysis N2 - Non-destructive Testing (NDT) provides valuable data about structural elements, supporting the assessment of existing infrastructures without incurring additional structural damage from inspections. Simultaneously, the uncertainty in measurement, which quantifies the quality of measurement results, plays a crucial role in decisions aimed at, e.g., optimizing maintenance strategies, rehabilitation works and Structural Health Monitoring (SHM) implementations. The Guide to the Expression of Uncertainty in Measurement (GUM) framework has already been considered for non-destructive concrete testing. Regarding that, extensive measurements with sophisticated scopes need to be conducted by experts as an obligatory process. This study illustrates how NDT results describing the inner structure of a concrete element can effectively support the reassessment of bridges in operation. To achieve this, the study considers the various measurable positions of the resisting longitudinal tendons of a bridge structure to investigate the displacement change under dynamic service loads. Furthermore, this study aims to simplify and optimize existing NDT data analysis procedures by employing regression analysis, enabling the detection of structural features. This regression analysis yields a modifier for determining the correct depth of an object within the structural element. The method is validated through laboratory experiments, including the use of an ultrasonic measurement system. As a result, it provides unbiased and accurately measured results, while ensuring that the measurement data can remain uncorrelated. Major advantages include efficient computation, a wider scope, and avoiding redundant information about the measuring process. The findings demonstrate that employing the proposed NDT analysis method, with its enhanced practicability, can significantly augment the efficiency of NDT data-supported structural reassessments across various scenarios. T2 - EWSHM 2024 CY - Potsdam, Germany DA - 10.06.2024 KW - Existing structures KW - Non-destructive testing KW - Practicality measurement KW - Bridge reassessment KW - Statistical analysis PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-604825 DO - https://doi.org/10.58286/29714 SN - 1435-4934 SP - 1 EP - 9 PB - NDT.net AN - OPUS4-60482 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bertola, N. A1 - Schumacher, T. A1 - Niederleithinger, Ernst A1 - Bruehwiler, E. T1 - Early detection of structural damage in UHPFRC structures through the combination of acoustic emission and ultrasonic stress wave monitoring N2 - Ultra-High-Performance Fiber-Reinforced Cementitious Composite (UHPFRC) offers several advantages compared to concrete, notably due to the strain hardening behavior under tensile actions. Structures made of this composite material are lightweight and highly durable, thanks to the UHPFRC waterproofing quality. Nonetheless, the tensile behavior leads to a different cracking pattern than conventional concrete and is not fully understood yet. This paper presents a combined approach using both passive ultrasonic (US) stress wave (or acoustic emission) and active US stress wave monitoring to localize and quantify damage progression in a full-scale UHPFRC beam during experimental load testing. The proposed monitoring approach involves 24 US transducers that are embedded randomly throughout a 4.2- meter-long laboratory UHPFRC T-beam. Continuous monitoring enabled accurate localization of US stress sources caused by loading-induced cracking as well as from pulses generated by the embedded US transducers. This study shows that it is possible to predict the location and shape of the macro-crack that is linked to structural failure early on, i.e., just after the end of the elastic domain. This combined approach opens new possibilities to monitor the structural behavior and detect damage on UHPFRC structures before they affect the structural behavior in terms of deflection and strain. T2 - 11th European Workshop on Structural Health Monitoring (EWSHM 2024) CY - Potsdam, Germany DA - 11.6.2024 KW - UHPFRC KW - Acoustic emission KW - Damage detection PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-604708 UR - https://www.ndt.net/article/ewshm2024/papers/477_manuscript.pdf DO - https://doi.org/10.58286/29698 SN - 1435-4934 SP - 1 EP - 8 PB - NDT.net AN - OPUS4-60470 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schumacher, T. A1 - Bertola, N. A1 - Epple, Niklas A1 - Bruehwiler, E. A1 - Niederleithinger, Ernst T1 - Combined Passive and Active Ultrasonic Stress Wave Monitoring of Concrete Structures: An Overview of Data Analysis Techniques and Their Applications and Limitations N2 - Combined passive ultrasonic (US) stress wave [better known as acoustic emission (AE)] and active US stress wave monitoring has been shown to provide a more holistic picture of ongoing fracture processes, damage progression, as well as slowly occurring aging and degradation mechanisms in concrete structures. Traditionally, different data analysis techniques have been used to analyze the data generated from these two monitoring techniques. For passive US stress wave monitoring, waveform amplitudes, hit rates, source localization, and b-value analysis, among others, have been used to detect and locate cracking. On the other hand, amplitude tracking, magnitude squared coherence (MSC), and coda wave interferometry (CWI) are examples of analyses that have been employed for active US stress wave monitoring. In this paper, we explore some of these data analysis techniques and show where their respective applications and limitations might be. After providing an overview of the monitoring approach and the different data analysis techniques, results and observations from selected laboratory experiments are discussed. Finally, suggestions for further work are proposed. T2 - 11th European Workshop on Structural Health Monitoring (EWSHM 2024) CY - Potsdam, Germany DA - 11.06.2024 KW - Ultrasound KW - Acoustic emission KW - Concrete KW - Stress PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-604687 UR - https://www.ndt.net/article/ewshm2024/papers/824_manuscript.pdf DO - https://doi.org/10.58286/29863 SN - 1435-4934 SP - 1 EP - 8 PB - NDT.net AN - OPUS4-60468 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Skłodowska, Anna A1 - Baensch, Franziska A1 - Lay, Vera A1 - Niederleithinger, Ernst A1 - Kühne, Hans-Carsten T1 - Acoustic emission monitoring for engineered barriers in nuclear waste disposal N2 - To safely dispose of nuclear waste in underground facilities, engineered barrier systems are needed to seal shafts and galleries. The material used in these barriers must be adapted to the host rock parameters. Shrinking and cracking must be avoided to provide a barrier with almost zero permeability. For repositories in salt rock environments, several types of salt concrete (SC) are possible construction materials. Within the project SealWasteSafe, we compared the behavior of an innovative alkali-activated material (AAM) with standard SC in their hydration and hardening phase. To monitor the microstructural changes within the two materials SC and AAM, acoustic emission (AE) signals have been recorded for up to ~250 days on 340-litercubic specimens. The phenomenon of AE is defined as the emission of elastic waves in materials due to the release of localized internal energy. Such energy release can be caused by the nucleation of micro-fracture, e.g., in concrete while curing or when exposed to load. The occurrence of AE events gives first rough indications of microstructural changes and potentially occurring cracking and thus, provides insights for structural health monitoring (SHM). The results show, that for the first 28 days after casting, less AE activity was detected in the AAM compared to SC. After 61 days, in the AAM material, the number of AE events exceeded those observed in the SC. However, the majority of the AE detected and located in AAM was related to surface effects, and not to microstructural changes or occurring cracks within the bulk volume. Additionally, the source location analysis indicated, that despite lower activity in SC, we observed some clustering of the events. In contrast, in AAM, the activity inside the specimen is randomly distributed over the whole volume. The monitoring results help to estimate the material’s sealing properties which are crucial to assess their applicability as sealing material for engineered barriers. T2 - 11th European Workshop on Structural Health Monitoring (EWSHM 2024) CY - Potsdam, Germany DA - 11.06.2024 KW - Endlager KW - Barriere KW - AAM KW - Akustische Emission PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-604699 UR - https://www.ndt.net/article/ewshm2024/papers/768_manuscript.pdf DO - https://doi.org/10.58286/29834 SN - 1435-4934 SP - 1 EP - 7 PB - NDT.net AN - OPUS4-60469 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Artinov, Antoni T1 - On the mathematical analysis of the relationship between the bulging region and the centerline solidification cracking in laser beam welding N2 - The present Ph.D. thesis provides a comprehensive experimental and theoretical study of the bulging-cracking relationship in laser beam welding of thick unalloyed steel sheets. It focuses on experimentally proving the existence of the bulging region and on developing a coupled multiphysics mathematical framework to analyze its influence on the three critical factors controlling the susceptibility to solidification cracking, namely the thermal, metallurgical, and mechanical factors. The research employs a novel experimental setup, utilizing a combination of transparent quartz glass and thick unalloyed steel sheet, enabling real-time visualization of the weld pool geometry and confirming the existence of a distinctive bulging region. To deepen the understanding of these experimental insights, an extensive multiphysics mathematical framework was developed and rigorously verified and validated. This framework introduces an innovative approach using Lamé curves for accurately describing complex three-dimensional weld pool geometries, including the bulging region's characteristics. Through analytical solutions and numerical procedures, it facilitates the computation of solidification parameters, which are crucial for understanding the metallurgical aspects of crack formation. The framework also incorporates a mechanical model to assess and evaluate the local stress distribution within the bulging region. The findings indicate that an elongated, sharply shaped bulging region significantly increases the susceptibility to solidification cracking. This is attributed to its adverse impact on the distribution and local dwell time of liquid metal residing at grain boundaries during solidification, combined with the localized tensile stresses identified in the bulging region. In essence, this research contributes to the broader understanding of solidification cracking in laser beam welding of thick unalloyed steel sheets, with a particular focus on the bulging region. The insights and methodologies developed in this thesis are valuable for future research and advancements in the application of the laser beam welding technology for joining high-thickness unalloyed steel components. KW - Bulging effect KW - Centerline solidification cracking KW - Mathematical modeling KW - Structural steel KW - High power laser beam welding PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-599010 DO - https://doi.org/10.14279/depositonce-20090 SP - 1 EP - 152 CY - Berlin AN - OPUS4-59901 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Niederleithinger, Ernst A1 - Chapuzet, C. A1 - Ben Lagha, S. A1 - Zovini, C. A1 - Uras, S. A1 - Doupou, S. A1 - Köpp, Christian T1 - Assess potential technologies for implementation phase, considering cost-benefit ratio and availability (Technology Selection) N2 - Technology selection is an important part of the planning process when setting up a waste management programme. This continues to be crucial during implementation of the programme to evaluate if suitable technologies are being implemented. This Domain Insight document provides guidance on the assessment and selection of potential technologies for implementation during the pre-disposal phase of the waste management lifecycle, considering factors such as cost-benefit ratio and availability (EURAD Pre-disposal theme overview, domain 2.1.3, Technology Selection), as a part of the sub-theme “Planning pre-disposal management of radioactive waste in close cooperation with waste generators” (Planning) and, on the broader theme 2 “Pre-disposal Activities prior to geological disposal” (Pre-disposal). In the planning process for a waste management programme, it is critical for the waste owner to assess the feasibility of technologies for processing, storage, and monitoring, taking economic constraints into account and considering subsequent stages in the waste management lifecycle, including final disposal. In addition, technology selection must be based on the waste inventory that has been generated, planned waste stream composition and the evolution of resulting waste packages in storages. The accuracy, effectiveness and efficiency of the technologies deployed in a facility require periodic review and update, as needed, throughout the lifetime of the facility. KW - Radioactive waste KW - Management KW - Final disposal KW - Intermediate storage KW - Technology selection PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-608795 UR - https://predis-h2020.eu/wp-content/uploads/2024/05/EURAD_PREDIS-DI-2.1.3.-Technology-selection.pdf SP - 1 EP - 16 AN - OPUS4-60879 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Habib, Abdel Karim A1 - Kluge, Martin A1 - van Wingerden, Kees T1 - Untersuchung der Freisetzung von Flüssigwasserstoff auf und unter Wasser N2 - In einer Reihe von Experimenten wurden die möglichen Folgen der Freisetzung von verflüssigtem Wasserstoff (LH2) auf, bzw. unter Wasser untersucht. Die Experimente zielten darauf ab, eine unbeabsichtigte Freisetzung von LH2 (z.B. durch Schlauchabriss) insbesondere bei der Betankung eines Schiffes zu simulieren. Für verflüssigtes Erdgas (LNG) wurden dabei sog. RPT’s (rapid phase transition) nachgewiesen, bei denen die spontane Verdampfung relevante Druckwellen erzeugt. Es kann nicht ausgeschlossen werden, dass RPTs auch im Falle von LH2 möglich sind. Die Versuche wurden auf dem Testareal Wasserstoffsicherheit auf dem Testgelände Technische Sicherheit der Bundesanstalt für Materialforschung und -prüfung (BAM-TTS) in Horstwalde, im Rahmen einer Forschungskooperation zwischen der BAM und Gexcon im Rahmen des SH2IFT-Programms durchgeführt. Die LH2-Freisetzungen erfolgten direkt aus einem LH2-Tanklastwagen über eine lange, flexible, vakuumisolierte Transferleitung. Während die Freisetzung oberhalb und unterhalb der Wasseroberfläche jeweils vertikal orientiert war, wurde bei der Unterwasserfreisetzung zusätzlich eine horizontale Ausströmung, parallel zur Wasseroberfläche realisiert. Zur Bestimmung des Massenstromes, wurde ein Wägesystem unter dem Tankwagen eingesetzt. Spezielle Drucksensoren wurden verwendet, um die durch die Freisetzungsvorgänge erzeugten Stoßwellen sowohl im Wasser als auch in der Luft zu messen. Die Gaskonzentrationen über dem Wasserbecken wurden an verschiedenen Positionen gemessen. Hochgeschwindigkeits-, Infrarot- (IR) und normale Kameras wurden eingesetzt, um die Phänomenologie der Freisetzung aufzuzeichnen und das Verhalten der Gaswolke im Zeitverlauf zu verfolgen. Neben den fest installierten Systemen an Land, kamen auch Unterwasserkameras sowie eine Drohne mit Normal- und IR-Kameras zum Einsatz. Zwei Wetterstationen wurden zur Messung von Windgeschwindigkeit, Windrichtung, Temperatur und Luftfeuchtigkeit während aller durchgeführten Tests eingesetzt. Des Weiteren kamen Bolometer zur Wärmestrahlungsmessung zum Einsatz. Zwar führten die Freisetzung zu einer hochturbulenten LH2/Wasser Mischzone, jedoch zu keinen nennenswerten Überdrücken durch RPT. Im Gegensatz dazu wurde unerwartet, aber reproduzierbar, eine Zündung der Gaswolke in freier Luft in einiger Entfernung von den Instrumenten und dem Ort der Freisetzung beobachtet. Die daraus resultierenden Gaswolkenexplosionen führten zu relevanten Überdrücken und zur Wärmeabstrahlung in die Umgebung. T2 - Magdeburg-Köthener Brandschutz- und Sicherheitstagung 2024 CY - Magdeburg, Germany DA - 14.03.2024 KW - Flüssigwasserstoff KW - LH2 KW - Freisetzung KW - RPT KW - Gaswolkenexplosion PY - 2024 SN - 978-3-948749-42-2 SP - 127 EP - 136 CY - Magedburg AN - OPUS4-59709 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baeßler, Matthias A1 - Bronsert, Jeffrey A1 - Thiele, Marc ED - Pombo, J. T1 - Track assessment and track optimization using a train track interaction model N2 - This paper deals with the assessment of track deterioration using a train-track interaction model. While modelling a train-track system a balance has to be found between the complexity and effort of the model on the one side and the needs for the assessment. The choice of assessment criteria are decisive for the given task. For an optimization of the track and its components simple assessment criteria are needed to allow for a variation of parameters. The paper describes the generalized process for track assessment and optimization and gives examples for specific members. T2 - Railways 2016: The Third International Conference on Railway Technology: Research, Development and Maintenance CY - Cagliari, Sardinia, Italy DA - 5.04.2016 KW - Train-track-modelling KW - Degradation KW - Track assessment KW - Track optimisation KW - Ballast KW - Concrete sleepers PY - 2016 SP - Paper 270, 1 EP - 12 PB - Civil-Comp Press CY - Stirlingshire, Scotland, UK AN - OPUS4-36085 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hu, Wei-Hua A1 - Said, Samir A1 - Rohrmann, Rolf A1 - Rücker, Werner A1 - Cunha, A. A1 - Rogge, Andreas ED - De Stefano, A. T1 - Vibration-based structural health monitoring of a highway bridge based on continuous dynamic measurements during 14 years N2 - This paper presents the continuous dynamic measurements of an aging prestressed box-beam bridge during the period from 2000 to 2013, which consists of dynamic properties and environmental/operational factors, as well as the Variation of the extracted health features after removing the environmental/operational effects. Firstly, the variations of frequency estimates, temperatures and traffic loads from 2000 to 2013 are described. Subsequently, correlation analysis between them indicates the nonlinear influences of the temperature on the frequency estimates. The Multiple Linear Regression (MLR) method is used to remove the environmental/operational effects and the health index is proposed by performing the Novelty Detection analysis of the residual errors. Finally, the variations of the health index may indicate clear structural modifications that can be also characterized by the long term monitoring of the dynamic strain in the prestressed cable. T2 - SHMII-7 - 7th International conference on structural health monitoring of intelligent infrastructure CY - Torino, Italy DA - 01.07.2015 KW - Westend bridge PY - 2015 SP - 1 EP - 12 AN - OPUS4-35124 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bronsert, Jeffrey A1 - Baeßler, Matthias ED - Pombo, J. T1 - A numerical approach of the train-track interaction along discontinuous tracks N2 - This paper presents a three dimensional numerical model which is can be used to investigate the effects on the track and in its vicinity due to a train passage. The numerical model for train track interaction is based on a time domain dynamic finite element model. Due to the unbounded nature of the soil the truncated boundary of the finite element domain is modelled with the scaled boundary finite element method, which is a semi-analytical approach. The application for a heterogeneous track along the track line is exemplified by a track with a bridge structure, where close attention is paid to the wheel-rail contact force. The results indicate that the wheel-rail contact force is not symmetrical around the bridge structure and an optimisation in terms of a backfilling area and under-sleeper-pads can improve such a transition. T2 - Railways 2016: The Third International Conference on Railway Technology: Research, Development and Maintenance CY - Cagliari, Sardinia, Italy DA - 5.04.2016 KW - Train-track interaction KW - Coupled FE-SBFE model KW - Finite element method KW - Scaled boundary finite element method KW - Bridge transition zone PY - 2016 SP - Paper 274, 1 EP - 14 PB - Civil-Comp Press CY - Stirlingshire, Scotland, UK AN - OPUS4-36089 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dutto, Paola A1 - Baeßler, Matthias A1 - Geißler, Peter T1 - Suction bucket foundations for wind energy turbines: a numerical study with FEM N2 - Suction Bucket Jackets (SBJ) are found as a suitable alternative to driven piles for the support of jacket or tripod foundations for offshore wind energy converters. Offshore wind energy turbines are characterized by a small self weight and they can be subjected to different load combinations. The work presented here aims to show the numerical investigation on the behavior of suction bucket foundations under different kind of loads as well as load combinations. In order to do so, a suitable numerical model is much needed. The theoretical basis of the model lies on the Swansea formulation of Biots equations of dynamic poroelasticity combined with a constitutive model that reproduces key aspects of cyclic soil behavior in the frame of the theory of generalized plasticity. An adequate FE formulation, the representation of appropriate soil-structure interfaces and the computational efficiency are key aspects in order to successfully model such complex systems. The 3D numerical simulation allows a special insight into the fundamental behavior of the founding of Suction Bucket Jackets such as the evolution of the pore water pressure or the occurrence of the so called soil liquefaction. T2 - OMAE 2016 - 35th ASME International Conference on Ocean, Offshore and Arctic Engineering CY - Busan, South Korea DA - 20.06.2016 KW - Suction bucket jacket KW - Finite Element KW - Offshore geotechnics PY - 2016 SN - 978-0-7918-4992-7 VL - 1 SP - Article UNSP V001T10A004, 1 EP - 8 PB - ASME AN - OPUS4-36688 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thiele, Marc A1 - Petryna, Y. A1 - Rogge, Andreas ED - Saouma, V. ED - Bolander, J. ED - Landis, E. T1 - Experimental investigation of damage evolution in concrete under high-cycle fatigue N2 - The current knowledge about fatigue behavior of concrete is still incomplete. This concerns especially the progress of fatigue which precedes the fatigue failure. Therefore, the process of fatigue itself under cyclic compressive loading was investigated in a systematic and comprehensive way. The aim of this investigation was to obtain a deeper insight and to provide a better understanding of the damage process occurring within the material during fatigue loading. Concrete cylinders were tested with a number of cycles to failure between 106 and 107. To investigate macroscopic and microscopic changes in the material, various methods of non-destructive and destructive testing were used. One main result was, in contrast to other authors, that the investigated changes in macroscopic material behavior could not be explained only by a development of micro-cracks. The results indicated rather, that the related changes in the fatigue behavior are mainly a result of viscous processes in the hardened cement paste, similar to the processes of creep. Based on the experimental results a description of the possible processes was derived which take place in the material structure during fatigue loading and also leads to the observed macroscopic changes in the material behavior. In this context, the results have shown that in case of isotropic material behavior a stiffness reduction related to a scalar value could not capture the damage effect on the stress-strain-relationship caused by fatigue. T2 - The 9th International Conference on Fracture Mechanics of Concrete and Concrete Structures CY - Berkeley, CA, USA DA - 29.5.2016 KW - Fatigue KW - Concrete KW - High-Cycle KW - Damage Evolution PY - 2016 DO - https://doi.org/10.21012/FC9.302 SP - 1 EP - 9 AN - OPUS4-36686 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kruschwitz, Sabine A1 - Strangfeld, Christoph A1 - Wöstmann, Jens T1 - Measuring screed moisture with EM methods – a comparison of capacitive handheld and microwave resonator probes N2 - We have compared the performance of the typical Darr and CM moisture testing techniques, which are destructive with several non-destructive testing techniques on two types of floor screeds. In case of cement based screeds these destructive tests failed to deliver reliable results. Moreover, our measurements indicate significantly different drying and moisture transport behavior for the investigated cement based and calcium-sulphate based screeds. Whereas we have strong with depth decreasing moisture gradients in the CT material, we observe in the penetrated volumes of our ndt methods basically no clear moisture gradient in the CA samples. The findings with ndt methods could be supported by moisture gradient studies with nuclear magnetic resonance measurements. T2 - 11th Int. Conference on electromagnetic wave interaction with water and moist substances CY - Florenz, Italy DA - 23.5.2016 KW - Moisture KW - Screed KW - Microwave KW - Nuclear magnetic resonance PY - 2016 SP - 77 EP - 84 AN - OPUS4-36674 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nery de Araújo Neto, Gilberto A1 - Hille, Falk A1 - Rogge, Andreas T1 - Post-impact assessment of reinforced concrete plate load capacity N2 - The modeling and prediction of the behavior of reinforced concrete under impact load is still an engineering challenge. The scientific community has put a lot of effort into the development of this knowledge, especially after the unfortunate events of 09/11 in Manhattan. The main concern is with nuclear power plants and how to design structures that can withstand such extreme situations. An experimental investigation has been carried out to collect fundamental data and to develop a deeper understanding of the effect of impact damage on the load capacity of concrete plates. The paper presents the process on the definition of procedures and the first results of an experimental investigation on the damage and residual load capacity of reinforced concrete plates after impact load. Two types of reinforced concrete plates measuring 1.5 x 1.5 x 0.3 m were subjected to the impact of a flat-nose hard projectile. The two types were casted with the same reinforcement and 80 or 40 MPa concrete. After the impact, the plates go through planar tomography, visual inspection and an ultimate load capacity test. The results showed that the planar tomography can be used for the assessment of internal damage on concrete plates, as long as the number of scans in each direction is more than four. The visual inspection gave a good. The formation of cone cracking after the impact load showed the highest influence on the remaining load capacity of the concrete plates. More plates will be tested to confirm the indications at different damage conditions. T2 - International Concrete Sustainability Conference 2016 CY - Washington DC, USA DA - 15.05.2016 KW - Impact damage KW - Concrete damage KW - Load capacity PY - 2016 SP - Paper Nery, 1 EP - 9 AN - OPUS4-36621 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thiele, Marc A1 - Petryna, Y. A1 - Rogge, Andreas ED - Saouma, V. ED - Bolander, J. ED - Landis, E. T1 - Experimental investigation of damage evolution in concrete under high-cycle fatigue N2 - The current knowledge about fatigue behavior of concrete is still incomplete. This concerns especially the progress of fatigue which precedes the fatigue failure. Therefore, the process of fatigue itself under cyclic compressive loading was investigated in a systematic and comprehensive way. The aim of this investigation was to obtain a deeper insight and to provide a better understanding of the damage process occurring within the material during fatigue loading. Concrete cylinders were tested with a number of cycles to failure between 106 and 107. To investigate macroscopic and microscopic changes in the material, various methods of non-destructive and destructive testing were used. One main result was, in contrast to other authors, that the investigated changes in macroscopic material behavior could not be explained only by a development of micro-cracks. The results indicated rather, that the related changes in the fatigue behavior are mainly a result of viscous processes in the hardened cement paste, similar to the processes of creep. Based on the experimental results a description of the possible processes was derived which take place in the material structure during fatigue loading and also leads to the observed macroscopic changes in the material behavior. In this context, the results have shown that in case of isotropic material behavior a stiffness reduction related to a scalar value could not capture the damage effect on the stress-strain-relationship caused by fatigue. T2 - The 9th International Conference on Fracture Mechanics of Concrete and Concrete Structures CY - Berkeley, CA, USA DA - 29.5.2016 KW - Fatigue KW - Concrete KW - High-cycle KW - Damage evolution PY - 2016 DO - https://doi.org/10.21012/FC9.302 SP - 1 EP - 9 AN - OPUS4-38242 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bartholmai, Matthias A1 - Johann, Sergej A1 - Kammermeier, Michael A1 - Müller, Maximilian A1 - Strangfeld, Christoph T1 - Transmission characteristics of RFID sensor systems embedded in concrete N2 - Completely embedded sensor systems for long-term operation offer innovative possibilities for structural health monitoring of concrete structures. Measuring of relevant parameters, e.g., temperature, humidity, or indication of corrosion can be performed with low energy sensors. This allows to implement passive RFID sensor systems without cable connection and battery, which are power supplied exclusively by the electromagnetic field from the external reader device. To evaluate characteristics and conditions of this concept, a systematical investigation of the transmission characteristics with variation of relevant parameters, as communication frequency, installation depth, type of concrete, moisture content, etc. is currently carried out in an interdisciplinary research project at BAM. First results are presented in this paper. T2 - IEEE Sensors 2016 CY - Orlando, FL, USA DA - 30.10.2016 KW - Embedded sensors KW - Energy harvesting KW - Wireless sensors KW - RFID sensors KW - Transmission characteristics KW - Structural health monitoring PY - 2016 SN - 978-1-4799-8287-5 SN - 1930-0395 SP - 1541 EP - 1543 PB - IEEE AN - OPUS4-38388 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thiele, Marc A1 - Petryna, Y. A1 - Rogge, Andreas A1 - Baeßler, Matthias ED - Beushausen, Hans T1 - Experimental investigation of fatigue process in concrete under high-cycle loading N2 - Fatigue is of relevance not only for metals but also for concrete. The current knowledge about fatigue behaviour of concrete is, however, incomplete. This concerns especially the progress of fatigue which precedes the fatigue failure. Some macroscopic effects of this process are well known but the governing material changes behind them are still less studied. The focus of the present contribution lay on a systematic and comprehensive investigation of the fatigue process under cyclic compressive loading. The aim was to obtain a deeper insight and to provide a better understanding of the damage process in the material. Cylindrical specimens were tested with a number of cycles to failure between 106 and 107. Various methods of non-destructive and destructive testing were used to investigate macroscopic and microscopic changes in the material. One main result was that the changes in the macroscopic material behaviour could not be explained only by the development of micro cracks. The results indicated that the related changes in the fatigue behaviour originate rather from viscous processes in the cement stone, similar to the process of creep. A sound description of the possible processes was derived from the obtained experimental results which concerns material structure during fatigue loading. It has been shown that in case of isotropic material behaviour a stiffness reduction related to a scalar value could not capture the damage effect on the stress-strain relationship caused by fatigue. T2 - fib symposium 2016 CY - Cape Town, South Africa DA - 21.11.2016 KW - High-cycle KW - Fatigue KW - Concrete KW - Damage evolution PY - 2016 SN - 978-2-88394-121-2 VL - 2016 SP - 1 EP - 10 PB - University of Cape Town CY - Cape Town AN - OPUS4-38720 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pahlavan, L. A1 - Pirskawetz, Stephan A1 - Hüsken, Götz A1 - Blacquière, G. T1 - Sensitivity of ultrasonic waves to surface-breaking cracks in reinforced concrete beams N2 - The interaction mechanism of ultrasonic waves with surface-breaking cracks in reinforced concrete has been studied. For this, a detailed numerical analysis of the medium was first conducted using the spectral finite element method. Subsequently, measurements were conducted on a reinforced beam sample before and after mechanical-load-induced cracking. It was concluded that for the considered configuration, waves passing through the cracks dominated the tip-diffracted ones. In addition, substantial changes in the travel time and amplitude of the signals were observed when cracks were present. T2 - 8th International Conference on Acoustic Emission - IIIAE 2016 CY - Kyoto, Japan DA - 5 December 2016 KW - Ultrasonic waves KW - Reinforced concrete beam KW - Cracks PY - 2016 SP - 237 EP - 242 AN - OPUS4-38913 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baeßler, Matthias A1 - Hille, Falk A1 - Said, Samir ED - Baeßler, Matthias ED - Rogge, Andreas ED - Möller, Gerd ED - Schiefelbein, Norbert T1 - Bauwerksüberwachung von Brücken im Kontext saisonaler Einflüsse N2 - Anhand verschiedener Bespiele wird diskutiert, wie Temperaturbeanspruchungen in einer Bauwerksüberwachung sichtbar werden und wie sie zu bewerten sind. Insbesondere der Einfluss auf die Zustandsbewertung im Sinne der Standsicherheit stellt häufig eine große Schwierigkeit dar. Behelfsweise besteht eine grundlegende Möglichkeit darin, ein Tragwerk immer zu seiner schwächsten Phase, d.h. in der Regel im Sommer zu beurteilen. Wie aufgezeigt, können zudem statistische Verfahren geeignet sein, Tragfähigkeitsänderungen zu detektieren. Als wesentliche Zukunftsaufgaben werden verbesserte Detektionsalgorithmen und physikalisch begründete Modelle zum mechanischen Verhalten angesehen. Die Akzeptanz schwingungsbasierter Verfahren zur Detektion und Lokalisierung von Schäden in der praktischen Anwendung ist alleinig von der Fähigkeit abhängig, Einflüsse aus veränderlichen Umwelt- und Betriebsbedingungen, insbesondere aber die aus der Temperatur zu eliminieren. Da die in den letzten Jahren immer wichtiger werdenden stochastischen Verfahren zur Schadensde-tektion und -lokalisierung die (statistische) Charakteristik der Messdaten bereits implizit nutzen, sind hier Entwicklung, Anpassung und Anwendung statistischer Algorithmen zur Eliminierung der variierenden Umwelteinflüsse naheliegend. Auf der anderen Seite wird der saisonale Einfluss auf Bauwerksmessungen in sehr vielen Veröf-fentlichungen dargestellt und es werden häufig verdachtsweise begründete physikalische Zu-sammenhänge für das Verhalten aufgezeigt. Im Regelfall sind die Aussagen aber nicht experi-mentell überprüft und von eher allgemeiner Natur („Asphalt reagiert temperaturabhängig“). Ob-jektspezifische Zusammenhänge, beispielsweise über Versuch an Repräsentanten in der Klima-kammer ermittelt, könnten jedoch sehr hilfreich sein. T2 - Messen Im Bauwesen CY - BAM, Berlin, Germany DA - 08.11.2016 KW - Bauwerksüberwachung KW - SHM KW - Temperatureinfluss PY - 2016 SN - 978-3-9817853-6-4 VL - 2016 SP - 89 EP - 102 PB - Eigenverlag BAM AN - OPUS4-39354 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hüsken, Götz A1 - Pirskawetz, Stephan A1 - Meinel, Dietmar ED - Banjad Pecur, Ivana ED - Baricevic, Ana ED - Stirmer, Nina ED - Bjegovic, Dubravka T1 - Experimental characterization of the fracture behavior of UHPFRC N2 - Ultra-high performance fiber-reinforced concretes (UHPFRCs) are most suitable for applications with extreme mechanical loads. These extreme conditions require ductile behavior under tensile loading, which is obtained solely by the working mechanism of steel fibers. Profound knowledge on the working mechanism of the steel fibers is necessary to optimize this material. Usually, this knowledge is obtained by means of classical destructive measuring techniques. Adopting measuring techniques from non-destructive material testing helps to analyze and to identify the different stages of the fracture mechanism of UHPFRC in detail. The application of different non-destructive measuring techniques is shown exemplary on tensile tests conducted on an UHPFRC mix and its applicability for analyzing the fracture behavior of such concretes is discussed. The main focus is on the characterization of the relevant failure modes under tensile loading by the different measuring techniques and the comparison with classical measuring techniques (e.g. extensometer). The tensile tests have been analyzed by optical deformation measurements using digital image correlation (DIC), acoustic emission analysis (AE), and 3D computed tomography (CT). T2 - 1st International Conference on Construction Materials for Sustainable Future (CoMS_2017) CY - Zadar, Croatia DA - 19.04.2017 KW - UHPFRC KW - Tensile strength KW - Acoustic emission analysis KW - Optical deformation measurement KW - 3D computed tomography PY - 2017 SN - 978-953-8168-04-8 SP - 293 EP - 299 AN - OPUS4-39910 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nery de Araújo Neto, Gilberto A1 - Hüsken, Götz A1 - Kühne, Hans-Carsten ED - Grantham, Michael ED - Basheer, P. A. Muhammed ED - Magee, Bryan ED - Soutsos, Marios T1 - Design of a cementitious coating system for corrosion protection: Phase 1 binder materials selection N2 - This paper presents the first results of an ongoing research project on the development of a cementitious thin layer coating system with high resistance against chloride penetration and carbonation. It is intended to display the decision process used for selecting raw materials as well as the conclusions based on test results and theoretical deliberations. In this phase, only the influence of the binder materials was analyzed concerning mechanical properties. The system should enhance the durability of new and old concrete structures exposed to aggressive environments, be based on market available materials and fulfill the requirements of the German guideline for concrete repair (Rili-SIB). T2 - Concrete Solutions 5th International Conference on Concrete Repair CY - Queen’s University Belfast, Northern Ireland, UK DA - 01.09.2014 KW - Concrete repair KW - Durability KW - Chloride penetration KW - Carbonation PY - 2014 SN - 978-1-138-02708-4 SN - 978-1-315-73731-7 DO - https://doi.org/10.1201/b17394-66 SP - Chapter 60, 423 EP - 429 PB - CRC Press AN - OPUS4-40114 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Shamsuddoha, Md A1 - Baeßler, Matthias A1 - Hüsken, Götz A1 - Pirskawetz, Stephan A1 - Kühne, Hans-Carsten A1 - Thiele, Marc ED - Banjad Pecur, Ivana ED - Baricevic, Ana ED - Stirmer, Nina ED - Bjegovic, Dubravka T1 - Identification of failure pattern in cylindrical grouted connection for wind structures - a pilot study N2 - At present, Wind Turbine Generators (WTGs) operating in onshore and offshore wind farms are primary sources of renewable energy around the world. Cylindrical grouted sleeve connections are usually adopted in these WTG structures to connect the upper structure and foundation for ease of installation. These structures including grouted connections experience considerable adverse loading during their lifetimes. Settlements were reported inside similar connections used in energy structures especially oil and gas platforms, which were installed in last three decades. Thus, repair and rehabilitation of such connections in existing wind structures should also be planned ahead to keep them operating in the future. The nature of failure and crack generation in grouted connections are crucial prior to adopt a strengthening strategy. This pilot study is carried out to actualize the failure mechanism in the grouted connection, when subjected to axial loading. A novel reusable scaled cylindrical grouted connection with shear keys was designed and tested for its load bearing behaviour. The mechanical test was accompanied by classical measuring techniques (e.g. displacement transducer) as well as non-destructive measuring techniques (e.g. digital image correlation (DIC), acoustic emission analysis (AE)). The failure mechanism incorporating slippage of the shear keys and cracking of the grout was investigated. The capacity and applicability of such test mould were also discussed. The knowledge is expected to pave way towards repair of deteriorated grouted connections with similar geometry and failure pattern. T2 - 1st International Conference on Construction Materials for Sustainable Future (CoMS_2017) CY - Zadar, Croatia DA - 19.04.2017 KW - Grouted connections KW - Cracks KW - Failure KW - Strengthening strategy KW - Digital image correlation KW - Acoustic emission analysis PY - 2017 SN - 978-953-8168-04-8 SP - 544 EP - 551 AN - OPUS4-39914 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kühne, Hans-Carsten A1 - Maier, Bärbel A1 - Maultzsch, Matthias A1 - Meng, Birgit A1 - Meinhold, Uwe T1 - Verification of the suitability of shotcrete on low strength concrete surfaces T2 - 10th International Conference on Durability of Building Materials and Components (DBMC) CY - Lyon, France DA - 2005-04-17 KW - Hydraulic engineering structures KW - Low strength concrete KW - Repair systems KW - Performance tests PY - 2005 SP - 8 pages CY - Lyon AN - OPUS4-7413 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Urs A1 - Pliett, H. A1 - Wenzel, F. A1 - Meng, Birgit T1 - A sustainable approach for the conservation of the Timur Shah Mausoleum in Kabul, Afghanistan T2 - 10th International Conference on Durability of Building Materials and Components (DBMC) CY - Lyon, France DA - 2005-04-17 PY - 2005 SP - 1 EP - 8(?) CY - Lyon AN - OPUS4-7411 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fontana, Patrick A1 - Meng, Birgit A1 - Habel, Wolfgang A1 - Wagenknecht, E. A1 - Hillemeier, B. T1 - Measurement of viscoelastic properties of cement pastes with oscillation rheometry T2 - 24th conference on Cement and Concrete Science CY - Warwick, England, UK DA - 2004-09-16 KW - Cement paste KW - Oscillation rheometry KW - Viscoelastic properties PY - 2004 SP - 1(?) EP - 4(?) AN - OPUS4-11178 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Recknagel, Christoph T1 - Qualitätssicherung der Fugenfüllung - gegenwärtiger Stand der Regelungen, zukünftige Entwicklungen, Forschungsaktivitäten T2 - VSVI-Seminar "Betondeckenbau" CY - Hannover, Deutschland DA - 2005-03-01 PY - 2005 SP - 20 Seiten PB - VSVI-Niedersachsen CY - Hannover AN - OPUS4-11285 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz A1 - Baeßler, Matthias A1 - Rücker, Werner T1 - Dynamik, Emissionen und Langzeitstabilität von innovativen Bahnfahrwegen N2 - Seit 25 Jahren betreibt die Bundesanstalt für Materialprüfung intensive Forschung auf dem Gebiet der Eisenbahndynamik unter Einbeziehung aller Systemkomponenten. Das umfasst theoretisch/numerische Arbeiten, Feldmessungen und Laborversuche zu den folgenden Fragen: - die Erschütterungs- und Körperschallweiterleitung durch den natürlichen Boden, - das Schwingungsverhalten der verschiedenen Fahrwege auf dem Untergrund, - die dynamischen Kräfte aus der Wechselwirkung zwischen dem Fahrzeug und dem Fahrweg sowie - die Gleislageentwicklung unter dieser Belastung bei verschiedenen Fahrwegen. Es werden Ergebnisse zu den dynamischen Kräften bei Geschwindigkeiten von 40 bis 300 km/h und zum Vergleich der Festen Fahrbahn mit dem Schottergleis vorgestellt, woraus Möglichkeiten für die T2 - VDEI Fachtagung BahnBau 2000 ; Technical Meeting and Exhibition on Railway Construction ; InnoTrans CY - Berlin, Germany DA - 12.09.2000 PY - 2000 SP - 265 EP - 271 CY - Frankfurt AN - OPUS4-11586 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baeßler, Matthias A1 - Rücker, Werner T1 - Zur Problematik des Schotteroberbaus auf Eisenbahnbrücken in Schnellfahrstrecken T2 - VDEI-Ingenieurbaufachtagung "Bahnbau 2004" CY - Berlin, Deutschland DA - 2004-09-24 KW - Schotteroberbau KW - Beschleunigung KW - Eisenbahnbrücken KW - Gleislage KW - Destabilisierung PY - 2004 SP - 9 Seiten PB - Verband Deutscher Eisenbahn-Ingenieure (VDEI) CY - Berlin AN - OPUS4-11483 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Strangfeld, Christoph A1 - Kruschwitz, Sabine A1 - Wöstmann, Jens A1 - Munsch, Sarah Mandy A1 - Hase, Felix T1 - Moisture in screed: a non-destructive multi-sensor approach N2 - Eight different screed types are tested including two different sample heights of 35 and 70 mm. The moisture of the four cement based and four sulphate based screeds are monitored during hydration and evaporation. All samples are stored in a climatic chamber at 23◦ C and 50 % relative humidity. Embedded sensors like temperature arrays, humidity sensor arrays, and multi-ring electrodes are embedded in the samples to yield a detailed moisture evolution with high depth resolution. Furthermore, nuclear magnetic resonance is used to quantify the water content at different depths. This multi-sensor approach allows a comprehensive monitoring of the moisture and its gradient in the different screed samples. This yields a deeper insight into the hydration, moisture convection, and diffusion processes. T2 - 8th European Workshop On Structural Health Monitoring CY - Bilbao, Spain DA - 05.07.2016 KW - NMR KW - Screed KW - Embedded sensors KW - Moisture KW - Corresponding relative humidity PY - 2016 N1 - Geburtsname von Munsch, Sarah Mandy: Nagel, S. M. - Birth name of Munsch, Sarah Mandy: Nagel, S. M. SP - 1 EP - 11 AN - OPUS4-36814 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Curosu, I. A1 - Pirskawetz, Stephan A1 - Mechtcherine, V. ED - Saouma, V. ED - Bolander, J. ED - Landis, E. T1 - Characterizing the crack development in strain-hardening cement-based composites (SHCC) by means of acoustic emission N2 - The article at hand presents an investigation on crack development in three different types of strain-hardening cement-based composites (SHCC) subjected to uni-axial tensile loading. The aim of the work was to evaluate the applicability of acoustic emission (AE) measurements for determining the progressive damage within the material, as well as for differentiating the individual damage events by their origin and decisive mechanisms, such as matrix cracking, fiber pullout or fiber rupture. The acoustic emission method proved to be fully appropriate for recording and evaluating the fracture related processes in various types of SHCC. Valuable information on failure mechanisms and quantitative description of damage depending on SHCC composition was obtained and evaluated with respect to the measured stress-displacement curves and under consideration of fracture surfaces and crack patterns observed on the specimens. T2 - 9th International Conference on Fracture Mechanics of Concrete and Concrete Structures CY - Berkeley,California, USA DA - 29.05.2016 KW - Building Materials KW - SHCC KW - Fiber KW - Tension KW - Fracture KW - Acoustic Emission PY - 2016 DO - https://doi.org/10.21012/FC9.207 SP - 1 EP - 10 AN - OPUS4-37199 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bartholmai, Matthias A1 - Johann, Sergej A1 - Kammermeier, Michael A1 - Müller, Maximilian A1 - Strangfeld, Christoph T1 - RFID sensor systems embedded in concrete – systematical investigation of the transmission characteristics N2 - Long-term completely embedded sensor systems offer innovative possibilities for structural health monitoring of concrete structures. Measuring of relevant parameters, e.g., temperature, humidity, or indication of corrosion can be performed with low energy sensors. This allows to implement passive RFID sensor systems without cable connection and battery, which are power supplied exclusively by the electromagnetic field from the external reader device. To evaluate characteristics and conditions of this concept, a systematical investigation of the transmission characteristics with variation of relevant parameters, as communication frequency, installation depth, type of concrete, moisture content, etc. is currently carried out in an interdisciplinary research project at BAM. First results are presented in this paper. T2 - 8th European Workshop On Structural Health Monitoring CY - Bilbao, Spain DA - 05.07.2016 KW - Structural health monitoring KW - Embedded sensor KW - Energy harvesting KW - Wireless sensors KW - RFID sensors KW - Transmission characteristics PY - 2016 SP - 1 EP - 5 AN - OPUS4-37129 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hauke, Max T1 - Autonomes mobiles Scanner-System zur zerstörungsfreien Prüfung von Stahlbeton N2 - Der BetoScan Light ist eine mobile autonome Messplattform zur automatisierten Ausführung von verschiedenen zerstörungsfreien Messverfahren. Das System besitzt eine kamerabasierte Navigation und ist fähig, anhand eines aufgestellten Schildes, welches als Ziel dient, eine Spur mit möglichst geringer Abweichung von der geraden Luftlinie abzufahren. Dabei wer-den in kurzen Abständen Bilder von einer, auf dem System angebrachten, Kamera aufge-nommen, welche dann einer Kantenanalyse unterzogen werden. Anhand der erkannten Kan-ten, kann ein Schild, welches ein spezielles Muster trägt, vom System geortet werden. Das System verfügt über drei Steuerungsmodi: der direkten Steuerung per Controller, der automa-tisierten Steuerung bei schrittweiser Fahrt, hierbei stoppt das System in bestimmten Abstän-den für eine bestimmte Zeit und die automatisierte Steuerung ohne Stopps. Die abschließen-den Testfahrten wurden mit einer Logitech C270 Webcam durchgeführt. Dabei ergab sich mit der C270 eine maximale Abweichung von 3,8 cm auf 10 Meter Teststrecke. Das System kann als genau und zuverlässig betrachtet werden. KW - Autonomer Messroboter KW - Zerstörungsfreie Prüfung KW - Stahlbeton PY - 2016 SP - 1 CY - Berlin AN - OPUS4-37696 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Wilzeck, René T1 - Methodenentwicklung zur akustischen Detektion von Delaminationen in Stahlbeton N2 - Die vorliegende Arbeit beschäftigt sich mit der Methodenentwicklung eines automatischen Messverfahrens zur akustischen Detektion von Delaminationen in Stahlbeton. Ziel war das Konstruieren einer Messeinheit, welche mittels eines Zahnrads kontinuierlich auf eine Stahlbetonoberfläche klopft und den somit einstehenden Körperschall mit einem Richtmikrofon aufnimmt. Somit können Rückschlüsse über den Zustand des Betons getroffen werden. Das Grundkonzept bildet die Frequenzbandanalyse von Audioaufnahmen mittels einer gefensterten Schnellen Fourier Transformation. Ein auftragen des Frequenzbands über die gefahrene Strecke bietet die exakte Positionierung einer Fehlstelle. Für die Validierung der Methodengenauigkeit entstand ein Betonprobekörper mit eingebrachten Fehlstellen, welche unter mechanischer Anregung durch das Zahnrad ähnlich dumpfe Töne wie eine reale Delamination erzeugen. Die Ergebnisse der Tonanalyse zeigen eindeutige Frequenzänderungen beim Übergang von einem intakten zu einen fehlerhaften Bereich. Im Bauwesen angesiedelt, ist die vorliegende Arbeit besonders für LeserInnen aus dem Bereich der Zerstörungsfreie Schadensdiagnose interessant. KW - Resonanzverfahren KW - Stahlbeton KW - Delaminationen PY - 2016 SP - 1 CY - Berlin AN - OPUS4-37697 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Johann, Sergej A1 - Strangfeld, Christoph A1 - Müller, Maximilian A1 - Bartholmai, Matthias ED - Aulova, Alexandra ED - Rogelj Ritonja, Alenka ED - Emri, Igor T1 - RFID sensor systems embedded in concrete - requirements for long-term operation N2 - One of the more difficult tasks for structural health monitoring is the continuous evaluation of the stability and load capacity of the building materials. This knowledge can be won, e.g., by taking material samples at the examining place with the drawback of partly destroying the structure. To avoid this, modern sensor and communication technologies offer promising methods for non-destructive testing. To address the tasks for monitoring of concrete structures, in the presented study, different sensors were combined with RFID transponders and embedded in concrete components. T2 - 33rd Danubia - Adria Symposium on Advances in Experimental Mechanics CY - Portorož, Slovenia DA - 20.09.2016 KW - Structure health monitoring KW - Concrete KW - Embedded KW - RFID sensors PY - 2016 SN - 978-961-94081-0-0 SP - 68 EP - 69 CY - Ljubljana AN - OPUS4-37535 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Manninger, Tanja A1 - Rübner, Katrin A1 - von Werder, Julia T1 - Eco friendly stabilization of loam with calcined clay and potassium hydroxide: a new approach to improve water resistance N2 - Earth buildings and adobe construction have been in use for thousands of years. Loam is locally available, environmentally friendly and has a small CO2 footprint mainly resulting from extraction and transport. Because of these reasons loam is one of the building materials of the future. Water resistance is an important aspect when using loam as a construction material. If the structural option of building protruding roofs cannot be implemented, the water resistance of clay can be improved by stabilization. Positive properties of the material should not be diminished by stabilization. For example, the desired regulation of air humidity, which however cannot be fully preserved by cement stabilization. For an alternative and more appropriate stabilisation, different mixtures with calcined clays with alkali activator were examined. The calcination temperature for clays is usually lower than for cement and starts at 600° C. The calcined clays therefore also have a lower CO2 footprint compared to cement. To keep the mixture environmentally friendly potassium was used as alkali ion. It could be proven that the alkali activated polymer enhances water resistance of the loam mixture. Provided some further optimization the material shows potential to replace cement without compromising on the positive properties of clay. T2 - International Conference on Regeneration and Conservation of Structures (ICRCS 2022) CY - Kyoto, Japan DA - 07.09.2022 KW - Loam KW - Alkali activation PY - 2022 SP - 1 EP - 4 AN - OPUS4-56396 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rübner, Katrin A1 - Sajna, A. T1 - High performance concrete - microstructure and durability T2 - 4th German-Slovenian seminar on joint projects in material science and technology CY - Berlin, Germany DA - 2000-11-09 KW - Hochleistungsbeton KW - Beton KW - Mikrosilica KW - Mikrostruktur KW - Dauerhaftigkeit PY - 2000 SP - 1(?) EP - 2(?) CY - Stuttgart AN - OPUS4-1090 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rübner, Katrin A1 - Fritz, Thomas T1 - Untersuchungen zur Präzision von Porositätsmessungen an Zementmörtel T2 - 10. Workshop über die Charakterisierung von Feinteiligen und Porösen Festkörpern CY - Bad Soden, Germany DA - 2000-11-15 KW - Mörtel KW - Beton KW - Ringversuch KW - Porosität PY - 2000 SP - 1(?) EP - 3(?) AN - OPUS4-1089 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meng, Birgit T1 - Mikrostruktur und Dauerhaftigkeit zementgebundener Baustoffe T2 - 8. Münchener Baustoffseminar "Dauerhaftigkeit von Betonkonstruktionen - Von den Mechanismen zum Lebensdauermanagement" CY - München, Deutschland DA - 2008-10-10 KW - Beton KW - Gefüge KW - Zement KW - Dauerhaftigkeit PY - 2008 SP - 1 EP - 9 AN - OPUS4-18594 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maack, Stefan ED - U. Kuhlmann, ED - J. Schänzlin, T1 - Ultraschall-Echoverfahren zur Strukturanalyse von Holzbauteilen T2 - Doktorandenkolloquium Holzbau Forschung + Praxis CY - Stuttgart, Deutschland DA - 2008-03-05 PY - 2009 SP - 25 EP - 32 AN - OPUS4-19096 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mehdianpour, Milad A1 - Herter, Jürgen A1 - Hille, Falk T1 - Service life extension of a railway viaduct in Berlin N2 - Bridge retrofitting of a section of the Berlin subway which is designed as railway on steel viaduct is presented. Fatigue damage in the superstructure of the over 70-years-old viaduct made an investigation of the damage causes necessary prior to the planning of retrofitting measures. The damage specifically occurred at the inverted arched steel plates of the ballast support elements. Those plates were provided for carrying the track ballast as well as the traffic load. For the retrofitting, the inverted arched plates were unloaded. The superstructure was redesigned into a fixed track system, which is able to transfer the traffic load directly into the substructure. The new rail fastening system made it necessary to verify the structural integrity of single elements as well as of the main system of the existing viaduct. The verification was based on several experimental investigations at BAM laboratory and on-site. Based on the evaluation of all test results the operation license could be issued. T2 - Munich Bridge Assessment Conference (MBAC 2009) CY - Munich, Germany DA - 2009-05-27 KW - Life time extension KW - Fatigue KW - Load test KW - Experimental investigations KW - On-site tests PY - 2009 IS - Paper # T13 SP - 1 EP - 18 CY - Munich, Germany AN - OPUS4-19483 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Binder, F. A1 - Bellon, Carsten A1 - Wohlgemuth, F. A1 - Hausotte, T. T1 - Ein praxisnaher Leitfaden für computertomografische Untersuchungen mit der radiografischen Simulationsumgebung aRTist N2 - Radiografische Simulationswerkzeuge wie aRTist, ScorpiusXLab, SimCT oder CIVA CT verwenden analytische Methoden und physikalische Monte-Carlo-Teilchentransportsimulationen, um die Interaktionsprozesse zwischen Röntgenstrahlung und Materie zu simulieren. Die berechneten Projektionen bilden anschließend unter Berücksichtigung einer definierten Scan-Trajektorie die Basis der Simulation einer röntgencomputertomografischen Untersuchung. Für den erfolgreichen Einsatz der Computertomografie, sei es als zerstörungsfreie Prüfmethode oder beim dimensionellen Messen, ist es generell notwendig, bekannte Fehler- bzw. Abweichungsquellen des Messverfahrens auszuschließen oder zu reduzieren. Dabei hat sich gezeigt, dass die Auswahl der Messparameter und die Erfahrung des Anwenders direkten Einfluss auf das erzielbare Messergebnis einer computertomografischen Untersuchung nehmen. Es ist daher sinnvoll, die Parameterauswahl in einem virtuellen Simulationsaufbau vorher zu erproben und an die Messaufgabe anzupassen. Neben der Optimierung von Messparametern finden radiografische Simulationswerkzeuge auch Anwendung für Machbarkeitsstudien und werden zur Schulung von Anwendern im Bereich der Röntgen-Computertomografie verwendet. Radiografische Simulationswerkzeuge befinden sich in einem stetigen Wandel, beispielsweise durch die Entwicklung neuer Rekonstruktionsmethoden, durch Erweiterung von analytischen Modellen, durch Integration komplexer Trajektorien oder durch Berücksichtigung von prozessbedingten geometrischen Abweichungen. Im laufenden EMPIR-Projekt „AdvanCT“ entsteht deshalb ein „Good Practice Guide“ für die Simulationsumgebung aRTist. Ziel dieses Guides ist es, die mit steigender Komplexität verbundenen Einstiegshürden für Anwender von aRTist zu reduzieren, um damit einen praxisnahen Zugang zur virtuellen Computertomografie zu ermöglichen. Dabei werden anhand von praktisch nachvollziehbaren Beispielen die grundlegenden Mechanismen der Simulationsumgebung erklärt und ein strukturierter Leitfaden zur Simulation röntgencomputertomografischer Untersuchungen mit aRTist vermittelt. In diesem Beitrag werden erste Auszüge des Guides sowie eine Übersicht der weiteren geplanten Themen für die anschließende Diskussion vorgestellt. T2 - DGZfP-Jahrestagung 2021 CY - Online meeting DA - 10.05.2021 KW - Computertomografie KW - Simulation PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-530476 UR - https://jahrestagung.dgzfp.de/portals/jt2021/bb176/inhalt/poster.htm SN - 978-3-947971-18-3 VL - 176 SP - 1 EP - 9 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-53047 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Diercks, Philipp A1 - Gläser, D. A1 - Unger, Jörg F. A1 - Crusoe, M. R. A1 - Huber, S. T1 - BAMresearch/NFDI4IngScientificWorkflowRequirements: Initial version N2 - Software-driven scientific workflows are often characterized by a complex interplay of various pieces of software executed in a particular order. The output of a computational step may serve as input to a subsequent computation, which requires them to be processed sequentially with a proper mapping of outputs to inputs. Other computations are independent of each other and can be executed in parallel. Thus, one of the main tasks of a workflow tool is a proper and efficient scheduling of the individual processing steps. Each processing step, just as the workflow itself, typically processes some input and produces output data. Apart from changing the input data to operate on, processing steps can usually be configured by a set of parameters to change their behavior. Moreover, the behavior of a processing step is determined by its source code and/or executable binaries/packages that are called within it. Beyond this, the computation environment not only has a significant influence on its behavior, but is also crucial in order for the processing step to work at all. The environment includes the versions of the interpreters or compilers, as well as all third-party libraries and packages that contribute to the computations carried out in a processing step. KW - Zenodo KW - 7790634 PY - 2023 DO - https://doi.org/10.5281/zenodo.7790633 PB - Zenodo CY - Geneva AN - OPUS4-59687 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schiek, Manuela A1 - Minenkov, Alexey A1 - Hollweger, Sophia A1 - Duchoslav, Jiri A1 - Erdene-Ochir, Otgonbayar A1 - Weise, Matthias A1 - Ermilova, Elena A1 - Hertwig, Andreas T1 - Optical constants of In2O3-SnO2 (Indium tin oxide, ITO) N2 - Optical constants of In2O3-SnO2 (Indium tin oxide, ITO) Minenkov et al. 2024: on glass; n,k 0.191–1.69 µm Optical constants of In2O3-SnO2 (Indium tin oxide, ITO) Minenkov et al. 2024: on Si wafer, top; n,k 0.191–1.69 µm Optical constants of In2O3-SnO2 (Indium tin oxide, ITO) Minenkov et al. 2024: on Si wafer, bottom; n,k 0.191–1.69 µm KW - Indium Tin Oxide KW - Optical constants KW - Magnetron Sputtering KW - Electrochemical Degradation KW - Spectroscopic Ellipsometry PY - 2024 UR - https://refractiveindex.info/?shelf=other&book=In2O3-SnO2&page=Minenkov-glass UR - https://refractiveindex.info/?shelf=other&book=In2O3-SnO2&page=Minenkov-wafer-top UR - https://refractiveindex.info/?shelf=other&book=In2O3-SnO2&page=Minenkov-wafer-bottom PB - Refractiveindex.info AN - OPUS4-59766 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Vater, Ernst-Joachim A1 - Recknagel, Christoph A1 - Kelling, Andreas T1 - Erstellung einer Videodokumentation über die Herstellung von Brückenbelägen auf Betonfahrbahntafeln (Abschlussbericht zum Forschungsvorhaben 7107) KW - Verkehrsflächen KW - Beläge auf Ingenieurbauwerken aus Beton KW - Gütesicherungssystem KW - Herstellung KW - Ausgangsmaterialien KW - Verarbeitung PY - 2001 N1 - Sprachen: Deutsch/Englisch - Languages: German/English SP - 1 EP - 28 PB - Bundesanstalt für Materialforschung und -prüfung CY - Berlin AN - OPUS4-12473 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maultzsch, Matthias A1 - Kühne, Hans-Carsten ED - Zachariev, G. T1 - Performance Aspects of Polymer Modified Cement Concrete and Respective Testing T2 - 11th International Conference on Mechanics and Technology of Composite Materials CY - Sofia, Bulgaria DA - 2006-10-02 KW - PCC PY - 2006 SP - 43 EP - 48 PB - Bulgarian Academy of Sciences CY - Sofia AN - OPUS4-14035 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weise, Frank T1 - Verfahren der Feuchtemessung an Betonbauteilen - eine Gegenüberstellung aller gängigen Verfahren T2 - Fachseminar "Trockene Bauwerke aus wasserundurchlässigem Beton" CY - Berlin, Deutschland DA - 2006-11-30 KW - Beton KW - Schadensanalyse KW - Innovative Prüftechnik PY - 2006 SP - 73 EP - 91 PB - Verlag Bau + Technik CY - Berlin AN - OPUS4-14399 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weise, Frank A1 - Onel, Yener A1 - Goebbels, Jürgen T1 - Analyse des Gefüge- und Feuchtezustandes in mineralischen Baustoffen mit der Röntgen-3D-Computertomografie T2 - 12. Bauklimatisches Symposium CY - Dresden, Deutschland DA - 2007-03-29 PY - 2007 VL - 1 SP - 395 EP - 405 PB - TU Dresden CY - Dresden AN - OPUS4-14717 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baeßler, Matthias A1 - Rücker, Werner T1 - Improved acceptance limits for bridge deck vibrations in light of test results T2 - 9th International Conference and Exhibition, "Railway Engineering - 2007" CY - London, U.K. DA - 2007-06-20 KW - Ballast KW - Destabilisation KW - Acceleration KW - Bridge deck PY - 2007 SP - - CY - London, U.K. AN - OPUS4-15072 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jakubcová, Petra A1 - Rübner, Katrin A1 - Schnell, A. T1 - Leichte Gesteinskörnungen auf der Basis thermisch und hydrothermal hergestellter Blähgranulate aus Abbruchabfällen N2 - Beton mit leichten Gesteinskörnungen (Leichtzuschlägen) ist seit dem Altertum bekannt. Leichte Gesteinskörnungen vulkanischen Ursprungs wurden bereits zur Errichtung der Maya-Pyramiden in Mexiko und von monumentalen Bauwerken im Römischen Reich verwendet. Zu den berühmtesten Beispielen der ersten Anwendung von Leichtbeton in Europa gehören das Kolosseum und das Pantheon in Rom, Hier wurden sowohl natürliche als auch künstliche Zuschlagstoffe, wie Bims, Lava und zerkleinerter Ziegelsplitt, benutzt. Mit steigender Nachfrage nach leichten Gesteinskörnungen und einer weltweit begrenzten Verfügbarkeit natürlicher Leichtzuschläge wurden synthetische leichte Gesteinskörnungen entwickelt. Ihre großtechnische Herstellung begann nach dem Ersten Weltkrieg. Heute werden leichte Gesteinskörnungen in einem breiten Schüttdichtespektrum von 100 bis 1200 kg/m3 hergestellt. Sie stellen einen wichtigen Teil der Gesteinskörnungen in der Baubranche dar. T2 - 15. Seminar 'Beschichtungen und Bauchemie' - Reaktive und filmbildende organische Bindemittel: Der Klimawandel und der Einfluss auf die Rezepturen Teil II CY - Kassel, Germany DA - 29.11.2011 KW - Sekundärrohstoffe KW - Sekundäre Gesteinskörnung KW - Recycling KW - Leichtbeton PY - 2011 SP - 55 EP - 66 AN - OPUS4-25086 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bhuyan, M.D. A1 - Viefhues, Eva A1 - Döhler, M. A1 - Lecieux, Y. A1 - Mevel, L. A1 - Hille, Falk A1 - Schoefs, F. T1 - Output-only Subspace and Transfer Matrix-based Damage Localization and Quantification N2 - This paper deals with vibration-based damage localization and quantification from output-only measurements. We describe an approach which operates on a data-driven residual vector that is statistically evaluated using information from a finite element model, without updating the parameters of the model. First, the damaged elements are detected in statistical tests, and second, the damage is quantified only for the damaged elements. We propose a new residual vector in this context that is based on the transfer matrix difference between reference and damaged states, and compare it with a previously introduced subspace-based residual. We show localization and quantification on both residuals in simulations. T2 - 7th International Operational Modal Analysis Conference CY - Ingolstadt, Germany DA - 10.05.2017 KW - Hypothesis tests KW - Damage localization KW - Damage quantification PY - 2017 SN - 978-3-8440-5247-3 SN - 1610-4773 SP - 278 EP - 288 AN - OPUS4-40489 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koch, Claudia ED - Jakobs, K. ED - Blind, K. T1 - Standardization in emerging technologies - The case of additive manufacturing N2 - Additive Manufacturing provides an important enabling technology for the digital transformation of the economy. As an emerging technology it has seen a remarkable development over the last three decades. Nevertheless, it is far from a broad adoption with several barriers to overcome yet. One of the major challenges is the lack of standards. The critical role of standardization for innovation is generally recognized, still the topic too often has been neglected in strategic roadmapping exercises for emerging technologies. Too little is known about the complex dynamics and interrelations of standardization and innovation. The anticipation of standardization needs and the timely and efficient implementation of standards is challenging. This paper aims at contributing to a better understanding of the role that standards play in the multi-dimensional system of innovation. It analyzes the trajectories of innovation in Additive Manufacturing in a systematic and holistic way, focusing on standardization activities with regard to coordination, stakeholders involved, the timing and types of standards developed. Putting standardization in context of the multi-dimensional innovation system of Additive Manufacturing the research shows where standards can support the diffusion of an emerging technology. T2 - 22nd EURAS Annual Standardisation Conference: Digitalisation: Challenge and Opportunity for Standardisation CY - Berlin, Germany DA - 28.06.2017 KW - Additive manufacturing KW - 3D Printing KW - Innovation KW - Emerging technologies KW - Standards PY - 2017 SN - 978-3-95886-172-5 VL - 2017 SP - T117 EP - T135 PB - Wissenschaftsverlag Mainz CY - Aachen ET - 1. AN - OPUS4-41020 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dutto, Paola A1 - Baeßler, Matthias A1 - Geißler, Peter T1 - Suction buckets behaviour under tensile loads: A numerical study with FEM N2 - Suction Bucket Jackets (SBJ) are found as a suitable alternative to driven piles for the support of foundations for offshore wind energy converters. In the case of jackets or multipods, a predominant vertical load is to be expected. The effect of such a tensile loading is the generation of suction in the soil inside the bucket which leads to an increment of tensile capacity. This paper aims to study the bearing behaviour of a suction foundation by taking into account how the soil permeability and the loading rate influence the foundation behaviour. Moreover, after submitting the structure to a storm load, the bearing capacity is studied again, in order to see the effect of such a load on the bucket's bearing behaviour. This study is carried out by means of Finite Element numerical simulations based on the formulation of Biot's equations combined with a constitutive model that reproduces the key aspects of cyclic soil behaviour in the frame of Generalized Plasticity. T2 - International Ocean and Polar Engineering Conference CY - San Francisco, USA DA - 25/06/2017 KW - Finite element method KW - Offshore wind energy converter KW - Suction bucket KW - Generalized plasticity KW - Sand KW - Numerical simulation KW - Tensile capacity PY - 2017 SN - 978-1-880653-97-5 SP - 485 AN - OPUS4-41051 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pirskawetz, Stephan A1 - Hüsken, Götz A1 - Curosu, I. A1 - Mechtcherine, V. ED - Mechtcherine, V. ED - Slowik, V. ED - Kabele, P. T1 - Combination of Digital Image Correlation and Acoustic Emission for Characterizing Failure Modes in Strain-Hardening Cement-Based Composites (SHCC) N2 - The tensile behavior of strain-hardening cement-based composites (SHCC) is usually investigated on macroscopic scale by means of direct tension tests or bending tests. Additionally, the micromechanical properties of the composites are often described based on single fiber tension and pull-out tests. Such investigations, performed both on macroscopic and microscopic scales, are based on ‘classical’ force and displacement measuring techniques. Advanced test methods such as digital image correlation (DIC) and acoustic emission analysis (AE) may facilitate the identification and the analysis of the failure mechanisms in SHCC, which is important for both monitoring loaded SHCC elements and further material development and optimization. In this study, these two techniques are combined to characterize the failure mechanisms of three different types of SHCC in direct tension tests. The results are related to data of stress and strain measurements. It is shown that DIC provides detailed spatially resolved and stress related strain measurements. Furthermore, it is demonstrated that AE allows for the localization of active cracks, quantification of the damage accumulation under increasing stresses, and characterization of the dominant crack bridging mechanisms and failure modes observed in the different types of SHCC. T2 - 4th International RILEM Conference on Strain-Hardening Cement-Based Composites (SHCC4) CY - Technische Universität Dresden, Germany DA - 18.09.2017 KW - Cementitious composites KW - Strain-hardening KW - Fiber reinforcement KW - Tension KW - Multiple cracking KW - Acoustic emission analysis KW - Digital image correlation PY - 2017 SN - 978-94-024-1194-2 DO - https://doi.org/10.1007/978-94-024-1194-2 VL - 15 SP - 300 EP - 307 PB - Springer Science+Business Media B.V. CY - Dordrecht, The Netherlands AN - OPUS4-42129 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Larcher, M. A1 - Arrigoni, A. A1 - Bedon, C. A1 - van Doormaal, A. A1 - Haberacker, C. A1 - Hüsken, Götz A1 - Millon, O. A1 - Saarenheimo, A. A1 - Solomos, G. A1 - Thamie, L. A1 - Valsamos, G. A1 - Williams, A. A1 - Stolz, A. T1 - Recommendations for a new generation of standards for testing numerical assessment of blast-loaded glass windows N2 - The determination of the blast protection level of civil engineering buildings components against explosive effects represents a topic of crucial importance, in current practice. However, some key aspects of blast resistant structures design have been only marginally considered in the last decade, and currently still require appropriate regulations. This is especially true in the case of windows and facades, where the intrinsic material brittleness is the major influencing parameter for blast-resistant assemblies. While blast assessment of buildings and systems is usually achieved by means of experimental investigations, as well as numerical simulations, general regulations and guidelines are currently missing. In this regard, the European Reference Network for Critical Infrastructure Protection (ERNCIP) Thematic Group “Resistance of Structures to Explosion Effects” attempts to develop guidelines and recommendations aimed to harmonise test procedures in experimental testing of glass windows under blast, as well as standardized approaches for their vulnerability assessment via numerical modelling. In this paper, major Thematic Group outcomes and next challenges are briefly summarized. T2 - International Conference on Structural and Mechanical Engineering for Security and Prevention - ICSMESP 2017 CY - Prague, Czech Republic DA - 14.06.2017 KW - Blast protection KW - Blast loaded glass windows KW - Experimental testing KW - Finite element numerical modelling KW - Standardisation PY - 2017 DO - https://doi.org/10.4028/www.scientific.net/KEM.755.121 SN - 1662-9795 VL - 755 SP - 121 EP - 130 PB - Trans Tech Publications Inc. CY - Zurich, Switzerland AN - OPUS4-41927 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Villani, P. A1 - Unger, Jörg F. A1 - Weiser, M. T1 - Adaptive Gaussian process regression for Bayesian inverse problems N2 - We introduce a novel adaptive Gaussian Process Regression (GPR) methodology for efficient construction of surrogate models for Bayesian inverse problems with expensive forward model evaluations. An adaptive design strategy focuses on optimizing both the positioning and simulation accuracy of training data in order to reduce the computational cost of simulating training data without compromising the fidelity of the posterior distributions of parameters. The method interleaves a goal-oriented active learning algorithm selecting evaluation points and tolerances based on the expected impact on the Kullback-Leibler divergence of surrogated and true posterior with a Markov Chain Monte Carlo sampling of the posterior. The performance benefit of the adaptive approach is demonstrated for two simple test problems. T2 - Algoritmy 2024 - Central-European Conference on Scientific Computing CY - Vysoké Tatry, Slovakia DA - 15.03.2024 KW - Gaussian process regression KW - Bayesian inverse problems KW - Surrogate models KW - Parameter identification KW - Active learning PY - 2024 SP - 1 EP - 10 PB - Slovak University of Technology CY - Bratislava AN - OPUS4-60738 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sperlich, Tim A1 - Häßler, Dustin A1 - Stelzner, Ludwig A1 - Hothan, Sascha T1 - In situ Prüfmethode zur Untersuchung des Feuerwiderstands von bestehenden Stahlkonstruktionen mit reaktivem Brandschutzsystem N2 - Der Beitrag beschreibt die Entwicklung eines neuartigen in situ Nachweisverfahrens zur Beurteilung des Feuerwiderstandes von bestehenden Stahlkonstruktionen mit gealtertem reaktivem Brandschutzsystem (RBS). Derzeit ist ein solcher Nachweis ausschließlich anhand eines Bauteilbrandversuchs möglich. Hierzu muss ein Bauteil aus der Bestandskonstruktion entnommen und einer zerstörenden Brandprüfung unterzogen werden. In Zusammenhang mit der Dauerhaftigkeitsbewertung von RBS für Zeiträume von mehr als 10 Jahren besteht in der Praxis vermehrt der Bedarf an einem minimal invasiven Prüfverfahren, mit dessen Hilfe sich direkt am Bestandsbauwerk die tatsächlich vorhandene Leistungsfähigkeit des gealterten RBS überprüfen lässt. Durch einen erfolgreichen Funktionsnachweis wäre eine Weiternutzung der Bestandkonstruktion bei Aufrechterhaltung des bestehenden Sicherheitsniveaus möglich. T2 - Symposium Heißbemessung - Structural Fire Engineering CY - Braunschweig, Germany DA - 05.09.2023 KW - Brandschutz KW - Stahlbau KW - reaktives Brandschutzsystem KW - Prüfmethode KW - Brandversuch PY - 2023 SP - 1 EP - 16 PB - TU Braunschweig CY - Braunschweig AN - OPUS4-58180 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Diercks, Philipp A1 - Gläser, D. A1 - Lünsdorf, O. A1 - Selzer, M. A1 - Flemisch, B. A1 - Unger, Jörg F. T1 - Evaluation of tools for describing, reproducing and reusing scientific workflows N2 - In the field of computational science and engineering, workflows often entail the application of various software, for instance, for simulation or pre- and postprocessing. Typically, these components have to be combined in arbitrarily complex workflows to address a specific research question. In order for peer researchers to understand, reproduce and (re)use the findings of a scientific publication, several challenges have to be addressed. For instance, the employed workflow has to be automated and information on all used software must be available for a reproduction of the results. Moreover, the results must be traceable and the workflow documented and readable to allow for external verification and greater trust. In this paper, existing workflow management systems (WfMSs) are discussed regarding their suitability for describing, reproducing and reusing scientific workflows. To this end, a set of general requirements for WfMSswere deduced from user stories that we deem relevant in the domain of computational science and engineering. On the basis of an exemplary workflow implementation, publicly hosted at GitHub (https:// this http URL), a selection of different WfMSs is compared with respect to these requirements, to support fellow scientists in identifying the WfMSs that best suit their requirements. KW - FAIR KW - Reproducibility, scientific workflow KW - Tool comparison KW - Workflow management PY - 2024 UR - https://arxiv.org/abs/2211.06429 DO - https://doi.org/10.48550/arXiv.2211.06429 PB - Arxiv; Cornell Tech CY - New York, NY AN - OPUS4-59804 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gerards-Wünsche, Paul A1 - Ratkovac, Mirjana A1 - Schneider, Ronald A1 - Hille, Falk A1 - Baeßler, Matthias T1 - A framework for assessing the reliability of crack luminescence – an automated fatigue crack detection system N2 - The new crack luminescence method offers the possibility of making fatigue surface cracks in metallic materials more visible during inspections through a special coating system. This coating system consists of two layers, whereby the first layer has fluorescent properties and emits visible light as soon as it is irradiated by UV light. The top layer is black and is designed to prevent the fluorescent layer from emitting if no crack develops in the underlying material. The technique proved particularly useful in a wide variety of fatigue tests of steel components under laboratory conditions. Moreover, it has the potential to be used in various industrial applications. To enable industrial deployment and integration into maintenance strategies, a concept study is developed in this contribution, resulting in a qualification framework that can serve as a foundation for determining the reliability of the crack luminescence system in terms of a probability of detection curve. Within this study, factors causing measurement variability and uncertainty are being determined and their influences assessed. Due to the extension of the system by a moving computer vision system for automated crack detection using artificial intelligence, additional long-term effects associated with structural health monitoring systems need to be incorporated into an extended probability of detection study as part of the technical justification. Finally, important aspects and findings related to design of experiments are discussed, and a framework for reliability assessment of a new optical crack monitoring method is presented, emphasizing the influence of various uncertainty parameters, including long-term effects such as system ageing. T2 - SPIE Conference Smart Structures + Nondestructive Evaluation 2023 CY - Long Beach, CA, USA DA - 24.03.2023 KW - Structural Health Monitoring KW - Non-Destructive Evaluation KW - Probability of Detection KW - Reliability KW - Artificial Intelligence KW - Computer Vision KW - Crack Luminescence KW - Wind PY - 2023 SN - 978-1-5106-6086-1 DO - https://doi.org/10.1117/12.2658390 SP - 1 EP - 15 AN - OPUS4-57244 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Johann, Sergej A1 - Stührenberg, Jan A1 - Tandon, Aditya A1 - Dragos, Kosmas A1 - Bartholmai, Matthias A1 - Strangfeld, Christoph A1 - Smarsly, Kay T1 - Implementation and validation of robot-enabled embedded sensors for structural health monitoring N2 - In the past decades, structural health monitoring (SHM) has matured into a viable supplement to regular inspections, facilitating the execution of repair and maintenance work in the early stages of structural damage. With the advent of wireless technologies and advancements in information and communication technologies, civil infrastructure has been increasingly instrumented with wireless sensor nodes to record, analyze, and communicate data relevant to SHM. A promising method for SHM is to embed sensors directly into concrete for recording SHM data from inside structural elements. In this paper, a sensor system for embedment into concrete is proposed, able to assess SHM data recorded from concrete. Power is supplied to the sensors on-demand by quadruped robots, which also collect the SHM data via radio-frequency identification (RFID), providing an automated and efficient SHM process. In laboratory experiments, the capability of the sensor system of automatically collecting the SHM data using quadruped robots is validated. In summary, the integration of RFID technology and robot-based inspection presented in this study demonstrates a vital approach to evolve current SHM practices towards more digitalized and automated SHM. T2 - 11th European Workshop On Structural Health Monitoring CY - Potsdam, Germany DA - 10.06.2024 KW - Structural health monitoring KW - RFID-based sensors KW - Smart sensors KW - Embedded sensors KW - Legged robots KW - Quadruped robots PY - 2024 SP - 1 EP - 8 AN - OPUS4-60335 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Koch, Claudia A1 - Elert, Anna Maria A1 - Meyer, Lena T1 - Vertrauen stärken und Innovation ermöglichen: Eine digitale Qualitätsinfrastruktur für ein modernes Made-in-Germany N2 - Produktion und Handel in immer komplexeren Wertschöpfungsnetzwerken, die fortschreitende digitale und grüne Transformation sowie technologische Innovationen sind in hohem Maße auf die verlässliche Sicherung und den effizienten Nachweis der Qualität, Sicherheit und Nachhaltigkeit von Waren, Dienstleistungen und Prozessen angewiesen. Unverzichtbar dafür ist eine moderne und leistungsfähige Qualitätsinfrastruktur (QI). Der Artikel stellt die Initiative QI-Digital, ihre Ziele und Aktivitäten für die digitale Transformation der QI vor. KW - Qualitätsinfrastruktur KW - Qualitätssicherung KW - Digitalisierung KW - digitale Transformation KW - Smart Standard KW - Digitales Zertifikat KW - DPP PY - 2024 UR - https://www.dgq.de/fachbeitraege/vertrauen-staerken-und-innovation-ermoeglichen-eine-digitale-qualitaetsinfrastruktur-fuer-ein-modernes-made-in-germany/ SP - 1 EP - 5 AN - OPUS4-60345 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eiz Eddin, Ahmad A1 - Stelzner, Ludwig A1 - Häßler, Dustin A1 - Hothan, Sascha T1 - Zum Feuerwiderstand von filigranen Deckenelementen aus vorgespanntem Carbonbeton N2 - Der Einsatz von hoch zugbeanspruchbarem und korrosionsbeständigem Carbongelege anstelle von herkömmlichem Spannstahl ermöglicht es Beton vorzuspannen und gleichzeitig die Betondeckung auf ein für den Verbund nötiges Minimum zu reduzieren. Das Carbongelege besteht aus Carbonfasern in einer Kunststoffmatrix. Mit dieser Bauweise können dünnwandige und damit ressourcenschonende Deckenelemente realisiert werden. Der Wechsel von massiven zu filigranen und vergleichsweise leichten Bauteilen führt jedoch aufgrund der geringeren Masse und der damit einhergehenden schnelleren Erwärmung zu einer Abnahme des Feuerwiderstands. Ferner führt die Erweichung der Matrix im Brandfall zu einer Abnahme der Verbundfestigkeit zwischen Carbongelege und Beton. Die Brennbarkeit des Carbongeleges sowie die Abplatzneigung des verwendeten Feinbetons stellen weitere Herausforderungen für den baulichen Brandschutz dar. Der Beitrag stellt Versuchsergebnisse zum Abplatz- und Hochtemperaturverhalten von Carbonbeton vor, die im Rahmen des Verbundvorhabens „Vorgespannte Carbonbetondecken mit reduzierten Querschnitten“ (CaPreFloor) erzielt wurden. Für die Untersuchung der Tragfähigkeit bei hohen Temperaturen wurden 4-Punkt-Biegeversuche an balkenförmigen Prüfkörpern (150 x 30 x 6 cm³) mit einlagiger Carbonbewehrung und instationärer Temperaturbeanspruchung durchgeführt. Neben dem Vorspanngrad des Carbongeleges wurde auch der Gelegetyp variiert. Im Bereich der konstanten Biegezugzone erfolgt die einseitige Erwärmung mittels elektrisch betriebener Heizmatten. Während der kontinuierlichen Erwärmung werden die Prüfkörper mit einer konstanten Kraft belastet, deren Betrag aus zuvor durchgeführten Biegeversuchen bei Raumtemperatur abgeleitet wurde. Die Abplatzversuche werden mit Einheits-Temperaturzeitkurve an rechteckigen (60 x 60 x 6 cm³) und kreisrunden (Ø 47 x 6 cm³), plattenförmigen Prüfkörpern am 1m³-Ofen der BAM durchgeführt. Die kreisrunden Prüfkörper sind zusätzlich mit einem Stahlring zur Behinderung der thermischen Dehnung des Betons versehen. Um den Einfluss des Geleges auf das Abplatzverhalten zu analysieren, werden sowohl Prüfkörper mit Carbongelege als auch unbewehrte Prüfkörper untersucht. Die daraus resultierenden Erkenntnisse fließen in die weitere Entwicklung der vorgespannten Carbonbetondeckenelemente ein. Anhand von realmaßstäblichen Brandversuchen wird der Feuerwiderstand dieser Bauteile im weiteren Projektverlauf bestimmt. T2 - Symposium Heißbemessung 2024 CY - Braunschweig, Germany DA - 24.09.2024 KW - Carbonbeton KW - Feuerwiderstand KW - Brandversuch KW - Carbon PY - 2024 SP - 23 EP - 39 AN - OPUS4-61253 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaenisch, Gerd-Rüdiger A1 - Bellon, Carsten A1 - Samadurau, Uladzimir T1 - Are Monte Carlo models applicable to radiological techniques? T2 - National Seminar on NDE of the Indian Society for Non-Destructive Testing CY - Kolkata, India DA - 2005-12-02 KW - Radiation techniques KW - Scattered radiation KW - Monte Carlo simulation KW - CAD PY - 2005 SP - 11 pages PB - Indian Society for Non-Destructive Testing CY - Kalkutta AN - OPUS4-11835 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaenisch, Gerd-Rüdiger A1 - Bellon, Carsten A1 - Ewert, Uwe T1 - Simulation for high energy radiography and reliability assessment T2 - National Seminar on NDE of the Indian Society for Non-Destructive Testing CY - Kolkata, India DA - 2005-12-02 KW - Radiation techniques KW - Simulation KW - High-energy radiography KW - CAD PY - 2005 SP - 14 pages PB - Indian Society for Non-Destructive Testing CY - Kalkutta AN - OPUS4-11834 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaenisch, Gerd-Rüdiger A1 - Bellon, Carsten A1 - Ewert, Uwe T1 - aRTist - Analytical RT Inspection Simulation Tool for Industrial Application T2 - 17th World Conference on Non-Destructive Testing CY - Shanghai, China DA - 2008-10-25 KW - Computer Simulation KW - Radiography KW - Computed Tomography KW - Ray Tracing PY - 2008 SP - 1 EP - 6 PB - International Committee for Non-Destructive Testing CY - Shanghai AN - OPUS4-18584 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bellon, Carsten A1 - Jaenisch, Gerd-Rüdiger T1 - aRTist - Analytical RT Inspection Simulation Tool T2 - DIR 2007 - International Symposium on Digital industrial Radiology and Computed Tomography CY - Lyon, France DA - 2007-06-25 KW - Computer Simulation KW - Radiography KW - Computed Tomography KW - Ray Tracing PY - 2007 UR - http://www.ndt.net/article/dir2007/papers/s1.pdf SP - 1 EP - 5 CY - Lyon, France AN - OPUS4-16086 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zhukovskiy, M. A1 - Skachkov, M. A1 - Jaenisch, Gerd-Rüdiger A1 - Bellon, Carsten A1 - Deresch, Andreas T1 - Monte Carlo simulating the electron emission from surfaces of objects being under radiation T2 - 10th European conference on non-destructive testing CY - Moscow, Russia DA - 2010-06-07 KW - Simulation KW - Elektronentransport PY - 2010 IS - Paper 4.02.18 SP - 1 EP - 10 AN - OPUS4-22764 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Deresch, Andreas A1 - Jaenisch, Gerd-Rüdiger A1 - Bellon, Carsten A1 - Warrikhoff, A. T1 - Optimization of X-ray sources by modeling T2 - 10th European conference on non-destructive testing CY - Moscow, Russia DA - 2010-06-07 KW - Simulation KW - Elektronentransport KW - Röntgenquellen PY - 2010 IS - Paper 4.02.18 SP - 1 EP - 10 AN - OPUS4-22766 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaenisch, Gerd-Rüdiger A1 - Bellon, Carsten A1 - Ewert, Uwe T1 - Simulation supported reliability analysis in radiography T2 - 10th European conference on non-destructive testing CY - Moscow, Russia DA - 2010-06-07 KW - Simulation KW - Zuverlässigkeit KW - POD PY - 2010 IS - Paper 4.02.18 SP - 1 EP - 13 AN - OPUS4-22767 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zubia Aranburu, Judith A1 - Cappella, Brunero A1 - Zabala Eguren, A. A1 - Buruaga Lamarain, L. A1 - Aginagalde Lopez, A. A1 - Bonse, Jörn A1 - Schwibbert, Karin T1 - Quantification of the adhesion force of E. coli on Ti via single-cell force spectroscopy N2 - Antibiotic resistance is a growing global problem which poses a massive threat to human health. Although human activity contributes to the acceleration of the process, bacteria have a self-driven stabilisation mechanism to protect themselves from such and other external threats: biofilm formation. Nonetheless, it is the adhesion of a single bacterial cell to a surface that triggers the formation of such network of biomolecules and microorganisms, as well as its hazardous consequences. The main objective of this work was to quantify the adhesion force of a single E. coli cell on a Ti substrate via the AFM-related single-cell force spectroscopy, with both the cell and the substrate material being of high clinical relevance. A set of 25 x 25 force displacement curves was acquired with a maximum force of 3.2 nN without dwell time, yielding a topography map and an adhesion force map that showed to be correlated. A mean adhesion force of 0.85 ± 0.175 nN was measured and the presence of cell appendages on the bacterial cell wall was verified through individual force-displacement curves. Bacterial viability was assessed after the measurements via live/dead staining. T2 - XL Congreso Anual de la Sociedad Española de Ingeniería Biomédica CASEIB 2022 CY - Valladolid, Spain DA - 23.11.2022 KW - Bacteria KW - Atomic force microscopy KW - Force distance curve PY - 2022 SN - 978-84-09-45972-8 SP - 217 EP - 220 AN - OPUS4-57039 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Andrés Arcones, Daniel A1 - Weiser, M. A1 - Koutsourelakis, F.-S. A1 - Unger, Jörg F. T1 - Evaluation of Model Bias Identification Approaches Based on Bayesian Inference and Applications to Digital Twins N2 - In recent years, the use of simulation-based digital twins for monitoring and assessment of complex mechanical systems has greatly expanded. Their potential to increase the information obtained from limited data makes them an invaluable tool for a broad range of real-world applications. Nonetheless, there usually exists a discrepancy between the predicted response and the measurements of the system once built. One of the main contributors to this difference in addition to miscalibrated model parameters is the model error. Quantifying this socalled model bias (as well as proper values for the model parameters) is critical for the reliable performance of digital twins. Model bias identification is ultimately an inverse problem where information from measurements is used to update the original model. Bayesian formulations can tackle this task. Including the model bias as a parameter to be inferred enables the use of a Bayesian framework to obtain a probability distribution that represents the uncertainty between the measurements and the model. Simultaneously, this procedure can be combined with a classic parameter updating scheme to account for the trainable parameters in the original model. This study evaluates the effectiveness of different model bias identification approaches based on Bayesian inference methods. This includes more classical approaches such as direct parameter estimation using MCMC in a Bayesian setup, as well as more recent proposals such as stat-FEM or orthogonal Gaussian Processes. Their potential use in digital twins, generalization capabilities, and computational cost is extensively analyzed. T2 - 5th ECCOMAS Thematic Conference on Uncertainty Quantificationin Computational Sciences and Engineering CY - Athen, Greece DA - 12.06.2023 KW - Model bias KW - Bayesian Uncertainty Quantification KW - Digital Twins KW - Gaussian Processes KW - Statistical Finite Element Method PY - 2023 UR - https://2023.uncecomp.org/ SP - 1 EP - 15 AN - OPUS4-58227 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bellon, Carsten A1 - Deresch, Andreas A1 - Jaenisch, Gerd-Rüdiger T1 - Radiography simulation with aRTist - Combining analytical and Monte Carlo methods N2 - Modelling becomes more and more important in modern NDE. It is increasingly used to optimize techniques for complex applications and to support the preparation of written procedures. Hence, computer simulation nowadays has to be able to handle all significant properties of an NDE system with sufficient accuracy. In case of radiographic applications this includes models of the radiation source, of the interaction of radiation with materials, of the detection process, and the geometrical description of the part or the construction. Depending on the given inspection problem and the influencing factors that should be addressed by the simulation an appropriate physical model has to be chosen to describe the underlying interaction mechanisms. The simulator aRTist combines analytical and Monte Carlo methods to efficiently model the radiation transport. Simulation is a powerful tool to separate different influencing factors. Here we focus on Monte-Carlo simulation of scatter contributions within aRTist. T2 - DIR 2015 - International symposium on digital industrial radiology and computed tomography CY - Ghent, Belgium DA - 22.06.2015 KW - CT KW - Multi-angle radiography KW - Modelling KW - Laminography KW - Radiographic testing (RT) PY - 2015 SP - 1 EP - 7 AN - OPUS4-33738 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hilpert, U. A1 - Bartscher, M. A1 - Neugebauer, M. A1 - Goebbels, Jürgen A1 - Weidemann, Gerd A1 - Bellon, Carsten T1 - Simulation-aided computed tomography (CT) for dimensional measurements N2 - Carrying out dimensional measurements by CT means assessing coordinates in space. CT must therefore be treated as a coordinate measuring technique similar to optical or tactile Coordinate Measuring Machines (CMMs). The well-established standards and guidelines for the acceptance- and verificationtesting of CMMs require the use of calibrated reference standards to achieve measurement machine characteristics. Hence, transferring these concepts from coordinate metrology to CT, a dedicated CT-specific reference standard was designed, manufactured and calibrated using a tactile CMM. For comparison purposes, a CAD model was created by reverse engineering using the calibration data. The calibrated model was fed into a virtual CT and the measurement process was simulated. The reference standard was measured by micro-CT. By comparing the characteristics of the measurement output of CT and the output gained from simulation, the influences of measurement artefacts can be judged, for the first time, in analogy to existing Guidelines of coordinate metrology. T2 - DIR 2007 - International Symposium on Digital industrial Radiology and Computed Tomography CY - Lyon, France DA - 25.06.2007 KW - Computed tomography KW - X-ray KW - Simulation KW - Coordinate metrology PY - 2007 UR - http://www.ndt.net/article/dir2007/papers/12.pdf SP - Paper 6, 1 EP - 15 AN - OPUS4-37045 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Johann, Sergej A1 - Mansurova, Maria A1 - Kohlhoff, Harald A1 - Gkertsos, Aris A1 - Neumann, Patrick P. A1 - Bell, Jérémy A1 - Bartholmai, Matthias T1 - Wireless Mobile Sensor Device for in-situ Measurements with Multiple Fluorescent Sensors N2 - This paper describes a wireless mobile prototype able to perform optical measurements by means of a miniatur-ized spectrometer for low light analysis, e.g. fluorescent sensors. Evaluations, calculations, calibration management and result display are performed by a computer or a standard tablet. The device was designed primarily to detect traces of oil in drinking or ground water and for the analyses of crude oils. However, it can also address a wide range of fluorescent sensors. The fast and user-friendly inspection of water quality or oil properties, as well as the adaptability and mobility, make the device attractive for a variety of users. Further application areas could be easily imple-mented by adapting the optics and the software (database, data processing and calibration plots, etc.) T2 - IEEE Sensors 2018 CY - New Delhi, India DA - 28.10.2018 KW - Wireless mobile sensor device KW - Fluorescent sensor KW - Embedded system KW - Water quality KW - Oil PY - 2018 SN - 978-1-5386-4707-3 SP - 1067 EP - 1070 PB - IEEE CY - New Delhi, India AN - OPUS4-46556 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino A1 - Scheerer, S. A1 - Fiedler, M. A1 - Schacht, G. A1 - Ritter, R. A1 - Marzahn, G. A1 - Marx, S. T1 - Die wechselvolle Geschichte der Carolabrücke in Dresden N2 - Am 11. September 2024 fand in Dresden ein Ereignis statt, welches man in Deutschland nicht erwartet hatte: der Teileinsturz einer Spannbetonbrücke unter Betrieb ohne Vorankündigung. Die Dresdner Carolabrücke war eine Ikone der Ingenieurbaukunst ihrer Zeit. Sie war ein sehr ästhetisches und schlankes Bauwerk. Ihre Konstruktion und Bau wären auch heute noch eine Herausforderung. Die vorhandenen Unterlagen zeugen von einer hohen Entwurfsqualität und einer sehr sorgsamen Bauausführung. Im Beitrag werden die Entstehungsgeschichte, die Konstruktion selbst und der Bau der Brücke vorgestellt. Es wird der Versuch der Rekonstruktion des Einsturzvorgangs unternommen und die Suche nach der Einsturzursache beschrieben. Am Schluss des Beitrags wird auf das aktuelle Überwachungskonzept eingegangen und ein Ausblick auf das mögliche weitere Vorgehen gegeben. T2 - 34. Dresdner Brückenbausymposium CY - Dresden, Germany DA - 19.03.2025 KW - Spanungsrisskorrosion KW - Wasserstoff KW - Spannstahl KW - Brücke PY - 2025 SP - 15 EP - 33 CY - Dresden AN - OPUS4-63063 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pauw, Brian Richard A1 - Smales, Glen Jacob T1 - Complete set of raw and processed datasets, as well as associated Jupyter notebooks for analysis, associated with manuscript entitled: "The MOUSE project: a practical approach for obtaining traceable, wide-range X-ray scattering information" N2 - This dataset is a complete set of raw, processed and analyzed data, complete with Jupiter notebooks, associated with the manuscript mentioned in the title. In the manuscript, we provide a "systems architecture"-like overview and detailed discussions of the methodological and instrumental components that, together, comprise the "MOUSE" project (Methodology Optimization for Ultrafine Structure Exploration). Through this project, we aim to provide a comprehensive methodology for obtaining the highest quality X-ray scattering information (at small and wide angles) from measurements on materials science samples. KW - X-ray scattering KW - Measurement methodology KW - Traceability derivation KW - Multi-scale measurements KW - Systems architecture KW - Nanomaterials PY - 2020 DO - https://doi.org/10.5281/zenodo.4312953 PB - Zenodo CY - Geneva AN - OPUS4-51825 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bernardy, Christopher A1 - Habib, Abdel Karim A1 - Kluge, Martin A1 - Schalau, Bernd A1 - Schulze, Marcel A1 - Kant, Hanjo A1 - Orchini, Alessandro ED - Di Benedetto, Almerinda ED - Portarapillo, Maria T1 - Investigation of the thermal radiation from hydrogen jet flames N2 - For industrial applications dealing with hydrogen, the definition of safety distances and the assessment of possible hazards emanating from releases is mandatory. Since hydrogen is usually stored and transported under pressure, one scenario to be considered is the momentum driven release of hydrogen from a leakage with subsequent ignition. In this scenario, the emitted heat radiation from the resulting jet flame to the surroundings has to be determined to define adequate safety distances. For hydrocarbon flames, different jet flame models are available to assess the hazards resulting from an ignited jet release. Since hydrogen flames differ from hydrocarbon flames in their combustion behavior, it has to be checked if these models are also applicable for hydrogen. To evaluate the accuracy of these models for hydrogen jet flames, tests at real-scale are carried out at the BAM Test Site for Technical Safety (BAM-TTS). Herein, the flame geometry and the heat radiation at defined locations in the surroundings are recorded for varying release parameters such as leakage diameter (currently up to 30 mm), release pressure (currently up to max. 250 bar) and mass flow (up to max. 0.5 kg/s). The challenge here is the characterization of the flame geometry in an open environment and its impact on the thermal radiation. Existing heat radiation data from the literature are mostly based on unsteady outflow conditions. For a better comparability with the steady state jet flame models, the experiments presented here are focused on ensuring a constant mass flow over the release duration to obtain a (quasi) stationary jet flame. In addition, stationary outflow tests with hydrocarbons (methane) were also carried out, which are intended to serve as reference tests for checking flame models based on hydrocarbon data. T2 - 15th International Symposium on Hazards, Prevention and Mitigation of Industrial Explosions (ISHPMIE) CY - Neaples, Italy DA - 10.06.2024 KW - Hydrogen KW - Release KW - Jet flame KW - Thermal radiation PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-605107 DO - https://doi.org/10.5281/zenodo.12515710 VL - 2024 SP - 1322 EP - 1333 PB - Zenodo CY - Geneva AN - OPUS4-60510 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maack, Stefan A1 - Torrent, R. A1 - Ebell, Gino A1 - Völker, Tobias A1 - Küttenbaum, Stefan T1 - Testing to reassess – Corrosion activity assessment based on NDT using a prestressed concrete bridge as case-study N2 - Corrosion of concrete reinforcement is one of the major damage mechanisms affecting both the load-bearing capacity and the serviceability of re-inforced concrete structures significantly. When externally discernible damages are observed during visual inspections on the structure, the extent of the damage inside the concrete is often already significant. Corrosion caused by carbonation often leads to severe discoloration of the surface or even large-area spalling of the concrete cover. In contrast, chloride-induced corrosion is usually difficult to observe visually but can cause much more serious damage in less time. The effect occurs locally and can lead to weakening of the cross-section of the reinforce-ment. This, in turn, can cause sudden structural collapses without prior notice. In the meanwhile, various non-destructive and minimally invasive testing methods are available to evaluate the resistance to penetration of corrosion-pro-moting pollutants and to detect active corrosion. In this paper, a bridge crossing the river Regen is used as a case-study to demonstrate how the information ob-tained applying different testing methods can be combined and evaluated in the context of structural reassessments. Both the results of the permeability testing and the electrical resistance measurement are considered, as well as active corro-sion areas are localized using the half-cell potential mapping combined with the concrete cover measurement with the eddy current method and ground penetrat-ing radar. The results are evaluated using drill cores and in addition laser-induced breakdown spectroscopy was applied to obtain information about possible chlo-ride ion transport into the concrete. T2 - EUROSTRUCT 2021 – 1ST conference of the european association on quality control of bridges and structures - Eurostruct CY - Padova, Italy DA - 30.08.2021 KW - Nondestructive testing KW - Corrosion KW - Bridge KW - Durability assessment KW - Civil engineering PY - 2022 SN - 978-3-030-91876-7 SP - 1 EP - 9 PB - Springer International Publishing AN - OPUS4-54006 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Seifert, Lando T1 - Exposé on the PhD-thesis: Initiation of stress corrosion cracking in prestressing steels N2 - The exposé is a mandatory part of the doctoral process at TUM and should outline the topic of the thesis and the future research focus. Ideally, the exposé forms the basis for the subsequent dissertation. The candidates topic is about hydrogen-induced stress corrosion cracking (HiSCC) of prestressing steels, which is a significant concern in civil engineering, particularly for prestressed concrete roofs and bridges. The susceptibility of prestressing steels to HiSCC is mainly influenced by manufacturing processes and the chemical composition, while the ability to hydrogen charging is influenced by the environmental and surface conditions. To know about the real nature of susceptibility of the prestressing steel might be an important puzzle piece to contribute to safe prestressed concrete structures in the future. The material susceptibility of prestressing steels toward HiSCC is a topic which must be studied independently of the environmental conditions. This cumulative dissertation will focus on the most important aspects of material properties that play a role in the initiation point of HiSCC. KW - Prestressing Steels KW - Hydrogen-induced stress corrosion cracking KW - Stress corrosion cracking KW - Brittle Fracture PY - 2024 SP - 1 EP - 8 CY - Graduate Center, TUM School of Engineering and Design, Technische Universität München AN - OPUS4-62051 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ebell, Gino A1 - Bösche, T. A1 - Steinbock, O. T1 - Rückschlüsse aus den Schadensbildern N2 - Wasserstoffinduzierte Spannungsrisskorrosion an hochfesten und hochempfindlichen Spannstählen führt an bestehenden Brückenbauwerken nach Jahren der Rissinitiierung zu Trag- und Standsicherheitsverlusten. Anhand des Beispiels der Brücke am Altstädter Bahnhof gibt es eine bauartbedingte Schadensinitiierung die über den gesamten Spannkanalquerschnitt zu Spannungsrisskorrosion führen kann. KW - Korrosion KW - Spannstahl KW - Spannungsrisskorrosion PY - 2021 SP - 85 EP - 87 PB - Landesbetrieb Straßenwesen Brandenburg CY - Hoppegarten AN - OPUS4-53506 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino A1 - Burkert, Andreas T1 - Standortabhängige Dauerhaftigkeitsbetrachtungen von Zink unter atmosphärischer Korrosion N2 - In maritimer Exposition können Zinkbauteile Nutzungsdauern von 50 Jahren erreichen. Dabei werden Expositionen mit Spritzwasserbelastung durch Meerwasser nicht betrachtet. Normative Betrachtungen und Korrosionsprognosen basierend auf Einjahreswerten liefern hier grundlegend falsche Ergbnisse, da sie eine signifikant höhere Belastung der Atmosphäre mit SO2 voraussetzen. T2 - GAV-Forschungsbeiratssitzung CY - Darmstadt, Germany DA - 17.05.2022 KW - Korrosion KW - Zink PY - 2023 AN - OPUS4-57631 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Ebell, Gino A1 - Fischer, O. A1 - Mensinger, M. T1 - Neuartiger Vergussstoß mit ultrahochfestem, faserverstärktem Beton für feuerverzinkte integrale Rahmenbrücken in Verbundbauweise N2 - Neuartige Technik zur Erstellung Einfeld-Brückenbauwerken aus feuerverzinkten Stahlbauteilen. Ziel des Vorhabens ist einen Vergussknoten zu konzipieren der zwei Brückensegmente fügt ohne jegliche nachträgliche Schraub- oder Schweißverbindung. Realisiert wurde dies mit ultrahochfestem Vergussbeton. KW - Feuerverzinken KW - Korrosion KW - Brücke PY - 2023 UR - https://www.gav-verzinken.de/forschung/wissenspool SP - 1 EP - 23 AN - OPUS4-57504 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bernardy, Christopher A1 - Habib, Abdel Karim A1 - Kluge, Martin A1 - Schalau, Bernd A1 - Kant, Hanjo A1 - Schulze, Marcel A1 - Orchini, Alessandro ED - Nabizada, A. ED - Dechany, A. ED - B. Carré, B. ED - Stendardo, E. ED - Lappa, F. ED - Vanlaere, J. ED - Mendoza, M.J. ED - Dejonghe, M. ED - Daese, M. ED - Namazifard, N. ED - Jacops, R. ED - Jottrand, S. ED - Pahlavan, S. T1 - Real scale safety investigations of hydrogen jet flames at high pressure N2 - In order to reduce the human footprint of CO2 emissions and limit global warming effects hydrogen combustion is becoming increasingly important. To enable fuel cells and gas turbines to operates this carbon free fuel, unprecedently large amounts of hydrogen need to be produced and safely transported and stored. The investigation of the effects of accidents involving hydrogen is therefore becoming of outmost importance. Since hydrogen is usually stored and transported under pressure, one scenario to be considered is the release of hydrogen from a leakage with subsequent ignition. The resulting jet flame must be characterized with respect to the thermal radiation emitted into the environment to define safety regulations. Various models that characterize the resulting flame shape and radiation already exist in the literature, but these are mainly based on empirical data from hydrocarbon jet flames.[1-4] To verify these models, a H2 Jet Flame project conducted at BAM, is investigating the safety of momentum driven hydrogen jet flames. For this purpose, large-scale tests are carried out at the Test Site Technical Safety (BAM-TTS). The object of the investigations is to assess the effects of real scale release scenarios regarding flame geometry and the thermal radiation emitted. Parameters such as release angle, leakage diameter (currently 1 mm to 10 mm), pressure (currently up to max. 250 bar) and mass flow (up to max. 0.5 kg/s) are varied. In addition, influences such as the type of ignition, ignition location as well as delayed ignition can also be investigated. The gained knowledge will be compared with existing jet flame models, to validate these and identify a possible need for further development. In particular, the focus will be laid on the thermal radiation of hydrogen flames. The challenge here is the visualization and characterization of the flame geometry in an open environment. Visualization is performed using infrared (IR) camera systems from at least two viewing angles. Measurements of the heat radiation of jet flames, which can be found in the literature, are mostly based on unsteady outflow conditions. The experimental setup used here allows for the generation of a steady-state outflow for several minutes and thus a direct comparability with existing (steady-state) models. Furthermore, the tests can be carried out for comparative measurements with hydrocarbons (methane, etc.) as well as mixtures of hydrogen and hydrocarbons. T2 - European PhD Hydrogen Conference 2024 (EPHyC2024) CY - Gent, Belgium DA - 20.03.2024 KW - Thermal radiation KW - Release KW - Hydrogen KW - Jet flame PY - 2024 SP - 551 EP - 556 AN - OPUS4-59910 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kern, Simon A1 - Michalik-Onichimowska, Aleksandra A1 - Riedel, Jens A1 - Panne, Ulrich A1 - King, R. A1 - Maiwald, Michael ED - Herwig, Christoph T1 - “Click” analytics for “click” chemistry – a simple method for calibration-free evaluation of online NMR spectra N2 - Currently, research in chemical manufacturing moves towards flexible plug-and-play approaches focusing on modular plants, capable of producing small scales on-demand with short down-times between individual campaigns. This approach allows for efficient use of hardware, a faster optimization of the process conditions, and thus, an accelerated introduction of new products to the market. Driven mostly by the search for chemical syntheses under biocompatible conditions, so-called “click” chemistry rapidly became a growing field of research. The resulting simple one-pot reactions are so far only scarcely accompanied by an adequate optimization via comparably straightforward and robust analysis techniques. Here we report on a fast and reliable calibration-free online high field NMR monitoring approach for technical mixtures. It combines a versatile fluidic system, continuous-flow measurement with a time interval of 20 s per spectrum, and a robust, automated algorithm to interpret the obtained data. All spectra were acquired using a 500 MHz NMR spectrometer (Varian) with a dual band flow probe having a 1/16-inch polymer tubing working as a flow cell. Single scan 1H NMR spectra were recorded with an acquisition time of 5 s, relaxation delay of 15 s. As a proof-of-concept, the thiol-ene coupling between N-boc cysteine methyl ester and allyl alcohol was conducted in non-deuterated solvents while its time-resolved behaviour was characterised with step tracer experiments. Through the application of spectral modeling the signal area for each reactant can be deconvoluted in the online spectra and thus converted to the respective concentrations or molar ratios. The signals which were suitable for direct integration were used herein for comparison purposes of both methods. T2 - 11. Interdisziplinäres Doktorandenseminar CY - Berlin, Germany DA - 12.03.2017 KW - Process Monitoring KW - Online NMR Spectroscopy KW - Indirect Hard Modeling KW - Process Control KW - Process Analytical Technology KW - CONSENS KW - Click Chemistry PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-435531 SP - 33 EP - 35 PB - Gesellschaft Deutscher Chemiker (GDCh) CY - Frankfurt a. M. AN - OPUS4-43553 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zinas, Orestis A1 - Papaioannou, Iason A1 - Schneider, Ronald A1 - Cuéllar, Pablo A1 - Baeßler, Matthias T1 - 3D spatial modelling of CPT data for probabilistic preliminary assessment of potential pile tip damage upon collision with boulders N2 - Tip damage of monopiles from boulder collisions during installation has emerged as a critical design issue, primarily due to the combination of the widespread use of large-diameter piles and the complexity of the ground conditions at the available sites. Recently, a framework relating potential pile tip damage to cone tip resistance from Cone Penetration Tests (CPTs) has been proposed in the literature. Gaussian processes are powerful stochastic models that enable probabilistic spatial interpolation of soil data at any location within a site. On this basis, this study utilizes sparse CPT data from a site in the North Sea, to first develop an efficient Gaussian process regression model, which is used to derive a three-dimensional (3D) probabilistic predictive map of the cone tip resistance. Assuming deterministic loading conditions and a factual collision with a boulder of pre-defined properties, the cone tip resistance predictive model is subsequently used for a probabilistic preliminary assessment of potential pile tip damage. Results of the analysis are realistic 3D probability maps of potential damage that aim to support engineering judgment and contribute towards cost-effective site investigation planning and offshore wind farm design. T2 - 5th International Symposium on Frontiers in Offshore Geotechnics (ISFOG 2025) CY - Nantes, France DA - 09.06.2025 KW - CPT data KW - Gaussian process regression KW - Boulder impact KW - Preliminary pile tip damage assessment PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-634417 SN - 978-2-85782-758-0 DO - https://doi.org/10.53243/ISFOG2025-323 SP - 505 EP - 510 PB - International Society for Soil Mechanics and Geotechnical Engineering CY - London AN - OPUS4-63441 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baeßler, Matthias A1 - Balscheit, Hagen A1 - Geißler, Peter A1 - Schepers, Winfried A1 - Cuèllar, Pablo T1 - Evaluation of pile tip buckling based on large scale tests N2 - Der Beitrag beschreibt eine groß angelegte Versuchskampagne mit Pfahlrammungen, um das Risiko des plastischen Versagens der Pfahlspitze besser zu verstehen und numerische Modelle zu validieren. Ein numerisches Modell mit transientem Bodenkontakt zeigt eine gute Übereinstimmung mit den Testergebnissen. Parametervariationen verdeutlichen, wie empfindlich die Pfahlreaktion auf Imperfektionen und Randbedingungen ist. T2 - 5TH INTERNATIONAL SYMPOSIUM ON FRONTIERS IN OFFSHORE GEOTECHNICS CY - Nantes, France DA - 09.06.2025 KW - Pile Tip Buckling KW - Monopile KW - Offshore Windenergy KW - Driving Refusal KW - Large Scale Test PY - 2025 SN - 978-2-85782-758-0 DO - https://doi.org/10.53243/ISFOG2025-476 SP - 1218 EP - 1223 PB - International Society for Soil Mechanics and Geotechnical Engineering (ISSMGE) CY - Nantes AN - OPUS4-63387 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kullolli, Borana A1 - Stutz, H. H. A1 - Cuéllar, Pablo A1 - Baeßler, Matthias A1 - Rackwitz, F. ED - Cardoso, A. S. ED - Borges, J. L. ED - Costa, P. A. ED - Gomes, A. T. ED - Marques, J. C. ED - Vieira, C. S. T1 - A generalized plasticity model adapted for shearing interface problems N2 - The response of many geotechnical systems, whose structural behavior depends on shearing effect, is closely related to soil structure interaction phenomenon. Experimentally it is found that the localisation of these effect happens at a narrow soil layer next to the structure. Numerically, this behavior can be modelled through inter-face elements and adequate constitutive models. In this work, a constitutive model in the framework of Gen-eralized Plasticity for sandy soils has been chosen to be adapted for the interface zone. From the direct shear experiments a sandy soil at loose and dense states under different normal pressures is considered. The adapted constitutive model is able to reproduce contraction and dilatation of the soil according to its relative density and it shows a good agreement with the experimental data. T2 - Conference CY - Porto, Portugal DA - 25.06.2018 KW - Numerical modelling KW - Soil-pile interaction KW - Interface KW - Shearing PY - 2018 SN - 978-1-138-33198-3 VL - 1 SP - 97 EP - 102 PB - NUMGE CY - Porto, Portugal AN - OPUS4-45721 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Merz, Benjamin A1 - Poka, Konstantin A1 - Mohr, Gunther A1 - Hilgenberg, Kai A1 - Polte, Julian T1 - Advanced camera calibration for lens distortion correction in hybrid manufacturing processes: An exemplary application in laser powder bed fusion (PBF-LB/M) N2 - Hybrid additive manufacturing is becoming increasingly important in the field of additive manufacturing. Hybrid approaches combine at least two different manufacturing processes. The focus of this work is the build-up of geometries onto conventionally manufactured parts using Powder Bed Fusion with Laser Beam of Metals (PBF-LB/M). The hybrid build-up requires a precise position detection system inside the PBF-LB/M machines to determine the exact position of the existing component. For this purpose, high-resolution camera systems can be utilized. However, the use of a camera system is associated with several challenges. The captured images are subject to various distortions of the optical path. Due to these distortions, it is not possible to use the images for measurements and, therefore, it is not possible to calculate the positions of objects. In this study a homography matrix is calculated to correct keystone distortion in the images. Different calibration patterns have been tested for the calculation of the homography matrix. The influence of the number of calibration points on the precision of position detection of objects is determined. Furthermore, the influence of an additional camera calibration by using ChArUco boards is evaluated. The result is a camera calibration workflow with associated calibration pattern for a precise position detection of parts inside PBF-LB/M machines allowing a hybrid build-up with minimum physical offset between base component and build-up. T2 - euspen’s 24th International Conference & Exhibition CY - Dublin, Ireland DA - 10.06.2024 KW - Additive manufacturing KW - Hybrid build-up KW - Position detection KW - Camera calibration PY - 2024 SP - 1 EP - 4 AN - OPUS4-60599 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Pasternak, H. A1 - Launert, B. A1 - Rhode, Michael A1 - Kannengießer, Thomas T1 - Erhöhung der Tragfähigkeit geschweißter I-Träger aus hochfestem Baustahl durch verbesserte Ansätze zur Berücksichtigung von Eigenspannungen N2 - In vielen Bereichen des modernen Stahlbaus kommen geschweißte Vollwandträger, wie I-Träger zum Einsatz. Im Gegensatz zu Walzprofilen können die Bauhöhe, die Querschnittsform und die Blechdicken an die Beanspruchung angepasst werden, wodurch sich wirtschaftliche Vorteile erzielen lassen. Dabei werden heutzutage immer häufiger hochfeste Feinkornbaustähle mit (Mindest-) Fließgrenzen bis 690 MPa eingesetzt. Zur verbesserten Ausnutzung des Tragfähigkeitspotenzials geschweißter Profile aus diesen Stählen existieren keine geeigneten Modelle zur Erfassung der schweißfertigungsbedingten Eigenspannungen an realen Komponenten. Diese Daten werden durch konservative Annahmen angenähert. Die potentielle Tragfähigkeit geschweißter Konstruktionen wird daher in der Regel unterschätzt. Die Eigenspannungsannahmen in DIN EN 1993 basieren auf starken Vereinfachungen, bspw. im Rahmen sog. „Ersatzstabnachweise“. Diese setzen die Proportionalität der Eigenspannungsamplituden zur Fließgrenze voraus. Vergleichsrechnungen mit einem parametrisierten Eigenspannungsmodell zeigten mögliche Abweichungen in den berechneten Tragfähigkeiten über mehrere Knicklinien. Die Festlegungen hinsichtlich der anzuwendenden Knicklinie beeinflussen jedoch die Blechdicken und somit in erheblichem Maße auch die Fertigungskosten. Als Optimierungsstrategie wurden in diesem Forschungsprojekt deswegen unterschiedliche anwendungsorientierte Modellansätze entwickelt, welche mithilfe nichtlinearer Traglastberechnungen, die höhere Ausnutzung von Tragfähigkeitsreserven ermöglichen sollen. Forschungsziel war somit primär die Entwicklung und Bereitstellung entsprechender Berechnungsansätze. Experimentell wurde hierzu der Eigenspannungszustand von konventionell geschweißten Strukturen am Beispiel der im Stahlbau besonders häufig verwendeten I-Träger aus zwei gängigen Baustählen, einem unlegierten Baustahl S355J2+N und einem Feinkornbaustahl S690QL, erfasst und durch numerische Schweißstruktursimulationen ergänzt. Anschließend erfolgte die Ableitung eines vereinfachten Berechnungsmodells zur weiteren Berücksichtigung in nichtlinearen Tragfähigkeitsberechnungen. Die Erkenntnisse sollen in einen entsprechenden Anwenderleitfaden, herausgegeben durch das Technical Committee 8 der Europäischen Konvention für Stahlbau, einfließen und diesbezüglich als Orientierung einer möglichen zukünftigen Anpassung der Knicklinien in DIN EN 1993-1-1 dienen. Im Projekt wurden die genannten Stähle in zwei typischen Dickenkombinationen von 25/15 mm und 20/10 mm (Gurt- und Stegbleche) zu Großprobekörpern „I-Träger“ unter industrienahen Fertigungsbedingungen mittels Metall-Aktivgasschweißen gefügt. Diese erzeugten die typischen Eigenspannungen, die in solchen Trägern nach der Fertigung vorliegen. Während des Schweißens wurden die Temperaturfelder durch Thermoelemente aufgezeichnet. Die Eigenspannungen wurden nach dem Schweißen experimentell durch eine Kombination aus mechanischem Zerlegen (Zerlegemethode) und anschließender mobiler Röntgendiffraktometrie (XRD) festgestellt. Der Einfluss der industriell üblichen Brennschnittkantenvorbereitung der Bleche auf die finalen Eigenspannungszustände wurde experimentell zusätzlich an kleinmaßstäblichen Proben untersucht. Metallographische Analysen (Schliffbilder und Härtemessungen) komplettierten das experimentelle Programm der FE 2 (BAM, Berlin). Die Ergebnisse zeigten, dass beim mechanischen Zerlegen bereits ein Großteil der Eigenspannungen herausgelöst wurde. Eine Aussage zu den nahtnahen Zugeigenspannungen war allerdings erst durch die Überlagerung mit der XRD möglich. Dabei zeigte der S690QL überwiegend ein besseres Verhalten als der S355J2+N, welches sich unter anderem in abgesenkten Zugeigenspannungen im Verhältnis zur jeweiligen Fließgrenze äußerte. Die maximalen Eigenspannungen wurden dabei zumeist in der Wärmeeinflusszone (WEZ) der Schweißnaht gemessen, unabhängig von der eingebrachten Streckenenergie oder der Festigkeit des Grundwerkstoffs. Die baupraktische Annahme, dass die maximalen Eigenspannungen in Höhe der Fließgrenze vorliegen können, wurde nur in Einzelfällen und nur für den S355J2+N bestätigt. Die experimentellen Ergebnisse zeigten für die Druckeigenspannungen ebenfalls reduzierte relative Eigenspannungswerte des S690QL. Dies zeigt die notwendige weitere Optimierung bei der Wahl der Bewertungsansätze für Eigenspannungen auf die Tragfähigkeit. Die erzeugten Messwerte dienten im weiteren Verlauf als Eingangswerte für die Modellentwicklung und die numerischen Simulationen an I-Trägern durch die FE 1 (LSH, Cottbus). Die numerischen Schweißsimulationen erfolgten in Simufact.Welding® für die Simulationsmodelle mit „klassischem“ Schweißsimulationsansatz sowie in Ansys® für vereinfachte Simulationen und Näherungsansätze. Die Modelle lieferten insgesamt vergleichbare Ergebnisse für die Längseigenspannungen mit teils jedoch erheblichen Unterschieden in den Rechenzeiten. Durch eine angepasste Vernetzung konnte die Rechenzeit in allen Fällen deutlich reduziert werden. Aufgrund der verwendeten Bauteilgrößen ist die Anwendung der Modellierung mit Volumenelementen allerdings meistens nicht praktikabel. Für typische Trägerschweißungen bieten stattdessen Querschnittsmodelle mit der Annahme eines verallgemeinerten ebenen Verzerrungszustands eine mögliche Alternative. Der Abgleich der Ergebnisse mit den Experimenten lieferte zusammenfassend überwiegend gute bis befriedigende Übereinstimmungen. Die experimentell festgestellten Tendenzen wurden dabei in allen Fällen richtig vorhergesagt. Eine umfassende Bewertung der erzielbaren Genauigkeiten war bisher nicht möglich. Dies lag einerseits daran, dass die Datendichte der mit der durch die Zerlegung gewonnen Ergebnisse gering war. Anderseits lieferten die überlagerten Ergebnisse mit der XRD in Teilen, insbesondere in den interessierenden Druckbereichen, widersprüchliche Aussagen zum Eigenspannungseinfluss, was bisher nicht abschließend geklärt werden konnte. Darüber hinaus entstanden etwaige Abweichungen in den Simulationen auch durch die zugrunde gelegten Materialdaten selbst. Diese entsprachen Standarddatensätzen aus Materialbibliotheken. Die Skalierung dieser erfolgte gleichmäßig über den gesamten Temperaturbereich. Insbesondere für den S690QL existierten zu wenige belastbare Materialkennwerte. Entsprechende Versuche konnten im Rahmen dieses Vorhabens nicht mit durchgeführt werden. Dennoch konnten hinsichtlich eines vereinfachten Berechnungsvorgehens zur Berücksichtigung der Schweißeigenspannungen in Tragfähigkeitsberechnungen einige wichtige Erkenntnisse gewonnen werden. Auf Basis der in den numerischen Schweißsimulationsmodellen ermittelten plastischen Dehnungsmuster, auch „Eigenspannungsquellen“, wurde eine vereinfachte Simulationsvorgehensweise vorgeschlagen und verifiziert. Die dabei eingeführten Vereinfachungen wurden im Hinblick auf die Berechnung ausschließlich der plastischen Längsdehnungen bzw. der Längseigenspannungen gewählt. Die Anwendbarkeit ist daher auf ausreichend lange Schweißträger mit Längsnähten beschränkt. Einige Modellmodifikationen zur weiteren Vereinfachung bzw. Modellimplementierung in die strukturmechanische Berechnung an großen Komponenten wurden vorgestellt. Abschließend erfolgt die Einstufung in eine mögliche Knicklinie auf Basis eines mittels GMNIA (geometrisch und materiell nichtlineare Analyse mit Imperfektionen) Berechnungen simulierten Streubands der Tragfähigkeiten mittels Abaqus® und Ansys®. Die anfängliche Hypothese einer günstigeren Knicklinie eines S690QL im Vergleich zum S355J2+N wurde dabei rechnerisch bestätigt. Der experimentelle Nachweis mittels entsprechender Trägerfähigkeitsversuche ist allerdings noch ausstehend. KW - Schweißeigenspannungen KW - Numerische Simulation KW - Traglastverhalten KW - I-Träger KW - Hochfeste Stähle PY - 2018 SN - 978-3-946885-32-0 VL - Forschung für die Praxis P 1035 SP - 1 EP - 144 PB - Verlag und Vertriebsgesellschaft mbH CY - Düsseldorf AN - OPUS4-45271 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Quackatz, Lukas T1 - In situ Untersuchung der Phasenverteilung und der Schmelzbaderstarrung von Duplexstählen mittels laserinduzierter Plasmaspektroskopie (LIBS) N2 - Nichtrostende Duplexstähle (DSS) werden in allen Branchen eingesetzt, bei denen eine hohe Festigkeit in Verbindung mit einer hohen Korrosionsbeständigkeit in aggressiven Medien ge-fordert wird. Beispiele hierfür sind Kraftwerkskomponenten und maritime Strukturen. DSS ha-ben ein ausgewogenes Phasenverhältnis von Ferrit (α) und Austenit (γ). Im Gegensatz zu einphasigen nichtrostenden Stählen vereinen DSS die Vorteile dieser beiden Phasen und kön-nen daher viele Anforderungen der Industrie erfüllen, wie z. B. Gewichtseinsparung oder hohe mechanische Festigkeit. In vielen industriellen Anwendungen werden diese Stähle ge-schweißt. Die Schweißbarkeit wird weitgehend durch die chemische Zusammensetzung be-stimmt. Legierungen mit ferritischer oder ferritisch-austenitischer Erstarrung weisen die höchste Widerstandsfähigkeit gegen Heißrissbildung auf. Das resultierende Phasengleichge-wicht beeinflusst die endgültigen Eigenschaften des Bauteils. Daher kann es von Vorteil sein, den Ferritgehalt des Schweißguts vorherzusehen bzw. zu messen. Das neueste und präzi-seste Gefügediagramm ist das WRC-1992 Diagramm und basiert auf der chemischen Zusam-mensetzung der Grund- und Zusatzwerkstoffe. In diesem Diagramm kann vor dem Schweiß-prozess abgeschätzt werden, welche Volumenanteile von Ferrit und Austenit im resultierenden Schweißgut vorliegen werden. Genutzt wird es bei der schweißtechnischen Verarbeitung von nichtrostenden, austenitischen bzw. Duplex-Stählen. Verschiedene Quellen berichten, dass diverse Legierungselemente nicht berücksichtigt werden und Optimierungen nötig sind. Wei-terhin können Legierungselemente während des Schweißens abdampfen, was die Mikrostruk-tur zum Negativen beeinflusst. Diese Arbeit eruiert zunächst die theoretischen Grundlagen zur laserinduzierten Plasmaspekt-roskopie (LIBS, engl.: laser induced breakdown spectroscopy), die zur in situ Messung chemi-scher Konzentrationen während des Schweißens genutzt werden soll. Weiterhin werden die Grundlagen zur Erstarrung und zur Schweißbarkeit von DSS aufgezeigt. Mithilfe verschiede-ner Kalibriermodelle werden quantitative Messungen mittels LIBS ermöglicht. Um die Ergeb-nisse der LIBS-Analysen zu validieren, wurden Schweißproben angefertigt und LIBS-Messun-gen mit konventionellen Messmethoden, wie die Röntgenfluoreszenzanalyse (RFA) und die energiedispersive Röntgenspektroskopie (EDX) verglichen. Folglich wurden dann in situ LIBS-Versuche, während des Wolfram-Inertgas-Schweißens (WIG), mit und ohne Schweißzusatz-werkstoff durchgeführt. Hierbei konnten die chemischen Konzentrationen in der Schweißnaht mittels LIBS mit der gleichen Genauigkeit wie die konventionellen Verfahren gemessen wer-den. Ein weiteres Ziel dieser Arbeit ist es, die Gültigkeit und Vorhersagegenauigkeit des WRC-1992 Diagramms zu überprüfen. Hierfür wurde der Schweißzusatzwerkstoff mittels PVD-Be-schichtung mit den Legierungselementen Kohlenstoff, Nickel, Mangan, Silizium, Niob und Kup-fer beschichtet. Diese Elemente nehmen maßgeblich Einfluss auf das Phasengleichgewicht Austenit/Ferrit im Schweißgut der Duplexstähle, da sie entweder Ferrit- bzw. Austenitstabilisa-toren sind. Die Messung der ferritischen und austenitischen Phasenanteile im resultierenden Schweißgut wurde mit drei verschiedenen Methoden vergleichend durchgeführt. Mithilfe der Bildanalyse im Lichtmikroskop, einem Fischerscope® sowie der Röntgendiffraktion (XRD). Da-mit sollte auch geprüft werden, inwieweit die Verwendung der jeweiligen Messmethode die Aussagekraft des WRC-1992 Diagramms beeinflusst. Die Vorhersage anhand des WRC-1992 Diagramms war für Nickel, Silizium und Mangan akzeptabel, jedoch bei Niob, Kupfer und Koh-lenstoff waren deutliche Abweichungen zu beobachten. Anpassungen im WRC-1992 Dia-gramm sollten daher für die Elemente Niob, Kupfer und Kohlenstoff vorgenommen werden. Die geringste Genauigkeit und die größte Streuung wurden mit dem XRD-Verfahren erzielt. Daher kann dieses Verfahren für Ferritmessungen an Schweißnähten von Duplexstählen nicht empfohlen werden. KW - LIBS KW - Duplexstahl KW - Vorhersage Phasenanteile PY - 2025 SP - 1 EP - 118 AN - OPUS4-62622 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Becker, Amadeus A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas A1 - Michael, Thomas T1 - Konstruktive Einflüsse bei der beanspruchungsgerechten Reparatur geschweißter Bauteile aus hochfesten Feinkornbaustählen N2 - Für eine nachhaltige und ressourceneffiziente Fertigung von Windkraftanlagen ist der Einsatz moderner hochfester Feinkornbaustähle vielfach notwendig. Bei der Montage hochfester Stahlkonstruktionen kommt es trotz anforderungsgerechter schweißtechnischer Fertigung vereinzelt zur Detektion von unzulässigen Unregelmäßigkeiten im Schweißbereich. Derzeitige Normen und Verarbeitungsrichtlinien geben hierbei kaum Informationen zu adäquaten Reparaturkonzepten, insbesondere für hochfeste Stähle. Vor diesem Hintergrund werden an der Bundesanstalt für Materialforschung und -prüfung (BAM) bauteilrelevante Untersuchungen zu den schweißbedingten Beanspruchungen und Gefügeveränderungen bei der schweißtechnischen Reparatur durch lokales thermisches Ausfugen und erneutes Schweißen durchgeführt. Hierzu werden einige wesentliche Ergebnisse an Beispielen des Ingenieurbaus, mit Blick auf die mechanisch-technologischen Eigenschaften und Eigenspannungen erörtert. In einem aktuellen Vorhaben (FOSTA P1311, IGF 20162N) sind darauf aufbauend die Einflüsse durch die Schrumpfbehinderung und Wärmeführung beim Reparaturschweißen hochfester Feinkornbaustähle (S500MLO, S960QL) sowie die Reparaturzyklenanzahl Fokus systematischer Untersuchungen. Mittels strukturmechanischer Berechnungen ließen sich hierzu selbstbeanspruchende Probenformen identifizieren, die unterschiedliche definierte Steifigkeitsverhältnisse von Reparaturschweißnähten realer Bauteile abbilden. Schweißnähte an diesen bauteilähnlichen Proben weisen signifikant erhöhte schweißbedingte Beanspruchungen mit zunehmenden (Biege-)Einspanngraden auf. Im Vergleich mit bisherigen Erkenntnissen wird gezeigt, dass eine sichere Reparatur solcher Schweißnähte nur mittels optimaler Reparaturkonzepte und Wärmeführung gelingt, um diesen hohen Beanspruchungen und auch den speziellen Gefügen hochfester Stähle Rechnung zu tragen. Ziel der Untersuchungen ist es letztlich, Empfehlungen für beanspruchungs- und werkstoffgerechte Reparaturkonzepte gerade für KMU abzuleiten, um Schäden und zumeist teure Nacharbeiten zu vermeiden. T2 - 4. Niedersächsisches Symposium Materialtechnik CY - Online meeting DA - 25.02.2021 KW - Eigenspannungen KW - Gefügedegradation KW - Hochfester Feinkornbaustahl KW - Reparatur KW - Schweißen PY - 2021 SN - 978-3-8440-8021-6 SN - 2364-0804 VL - 10 SP - 488 EP - 501 PB - Shaker Verlag CY - Düren AN - OPUS4-53315 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eissel, A. A1 - Treutler, K. A1 - Wesling, V. A1 - Engelking, Lorenz A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas T1 - Modifikation von CoCr-Legierungen für die additive lichtbogenbasierte Fertigung N2 - Für Komponenten im Turbinen- oder Anlagenbau werden aufgrund ihrer Eigenschaften häufig Kobalt-Chrom-Legierungen verwendet. Diese weisen eine hohe Korrosionsbeständigkeit und hohen Verschleißwiederstand auf. Aufgrund der komplexen Strukturen und dem Bestreben nach Ressourceneffizienz wird zur Herstellung der Komponenten die additive Fertigung verwendet. Hierbei sind hinsichtlich der Inhomogenität und Anisotropie der Gefüge und deren Eigenschaften weitere Kenntnisse notwendig. Bei den vorliegenden Belastungen liegt ein erhöhter Anspruch an die Oberflächenintegrität vor, welcher durch komplementären Einsatz von additiven und abtragenden Fertigungsschritten sichergestellt wird. Dabei sind gerade Co-Cr-Legierungen wegen der niedrigen Wärmeleitfähigkeit verbunden mit hoher Festigkeit und Zähigkeit äußerst herausfordernd mit Blick auf eine wirtschaftliche Zerspanung mit geometrisch bestimmter Schneide. Ausgehend von dieser Problemstellung erfolgt im Zuge eines Gemeinschaftsvorhabens des ISAF in Kooperation mit der BAM eine gezielte Beeinflussung des Gefüges. Ziel des Projektes ist die Zusammenhänge zwischen verschiedenen Legierungsmodifikationen, der entstehenden Gefügemorphologie und den Zerspanungseigenschaften von Co- Cr-Legierungen für die additive Fertigung mittels PTA darzustellen. Der Fokus liegt auf dem Beheben der bestehenden Nachteile bei gleichzeitigem Aufrechthalten der besonderen Eigenschaften der Legierung. Durch das Hinzulegieren von variierenden Gehalten von Zirkonium und Hafnium wird die Gefügeveränderung eingestellt. Es hat sich gezeigt, dass Hafnium als zusätzliches Legierungselement einen deutlichen Einfluss auf die Gefügemorphologie hat. Darüber hinaus wird die Auswirkung der Legierungsmodifikation auf die Härte und die Zerspanbarkeit dargestellt. T2 - 42. Assistentenseminar der Wissenschaftlichen Gesellschaft Fügetechnik e.V. CY - Blankenau, Germany DA - 06.10.2021 KW - Legierungsmodifikation KW - ultraschallunterstütztes Fräsen KW - Additive Fertigung PY - 2022 SN - 978-3-96144-210-2 VL - 385 SP - 103 EP - 113 PB - DVS Media GmbH AN - OPUS4-56658 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kern, Simon A1 - Michalik-Onichimowska, Aleksandra A1 - Riedel, Jens A1 - Panne, Ulrich A1 - King, Rudibert A1 - Maiwald, Michael ED - Maiwald, Michael T1 - “Click” analytics for “click” chemistry – a simple method for calibration-free evaluation of online NMR spectra N2 - Currently research in chemical manufacturing moves towards flexible plug-and-play approaches focusing on modular plants, capable of producing small scales on-demand with short down-times between individual cam-paigns. This approach allows for efficient use of hardware, a faster optimization of the process conditions, and thus, an accelerated introduction of new products to the market. Driven mostly by the search for chemical syntheses under biocompatible conditions, so-called “click” chemistry rapidly became a growing field of research. The re-sulting simple one-pot reactions are so far only scarcely accompanied by an adequate optimization via compara-bly straightforward and robust analysis techniques. Here we report on a fast and reliable calibration-free online high field NMR monitoring approach for technical mixtures. It combines a versatile fluidic system, continuous-flow measurement with a time interval of 20 s per spectrum, and a robust, automated algo-rithm to interpret the ob-tained data. All spectra were acquired using a 500 MHz NMR spectrometer (Varian) with a dual band flow probe having a 1/16 inch polymer tubing working as a flow cell. Single scan 1H spectra were recorded with an acquisition time of 5 s, relaxation delay of 15 s. T2 - 12. Kolloquium des Arbeitskreises Prozessanalytik CY - Berlin, Germany DA - 28.11.2016 KW - “Click” chemistry KW - Online NMR KW - Online monitoring PY - 2016 SP - 72 EP - 74 AN - OPUS4-38385 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geißler, Peter A1 - Cuéllar, Pablo A1 - Hüsken, Götz A1 - Kühne, Hans-Carsten A1 - Baeßler, Matthias T1 - Insights into compaction grouting for offshore pile foundations N2 - The authors are currently investigating the possibility to apply compaction grouting for offshore pile foundations (Jacket piles as well as monopiles) as a possible retrofitting technique for an optimised foundation concept. In this research project, we are developing a design approach aiming to predict the ideal amount and properties of a grout for a specific soil situation and desired improvement of pile bearing capacity after Installation and during service time. Both numerical and experimental tests have been carried out to investigate the injection process during which a highly viscous grout is injected into the soil under high pressure to displace and compact the surrounding soil without fracturing it. The implicit Material Point Method (MPM) based on a mixed formulation is the numerical technique chosen to deal with the expected large deformations and the arbitrary shape of the developing grout bulb. The usage of MPM prevents both the need of remeshing and the numerical instability induced by extensive mesh distortion. For validation with experimental results, we have constructed a testing chamber with one transparent sidewall. This chamber enables us to observe the injection process directly at the transparent vertical window and to measure the in-plane soil displacements and strains by means of the Digital Image Correlation (DIC) technique. The results already reveal the interrelation of soil and grout properties for a successful usage of this common ground improvement technique. T2 - 37th International Conference on Ocean, Offshore and Arctic Engineering (OMAE 2018) CY - Madrid, Spain DA - 18.06.2018 KW - Offshore pile foundation KW - Compaction grouting KW - Material Point Method (MPM) KW - Mixed formulation KW - Digital Image Correlation (DIC) PY - 2018 SN - 978-0-7918-5130-2 SN - 2153-4772 VL - 9 SP - V009T10A013, 1 EP - 9 AN - OPUS4-46004 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Patrick P. A1 - Hüllmann, Dino A1 - Krentel, Daniel A1 - Kluge, Martin A1 - Kohlhoff, Harald A1 - Lilienthal, A. J. T1 - Gas Tomography Up In The Air! N2 - In this paper, we present an autonomous aerial robot to reconstruct tomographic 2D slices of gas plumes in outdoor environments. Our platform, the so-called Unmanned Aerial Vehicle for Remote Gas Sensing (UAV-REGAS) combines a lightweight Tunable Diode Laser Absorption Spectroscopy (TDLAS) sensor with a 3-axis aerial stabilization gimbal for aiming on a versatile octocopter. The TDLAS sensor provides integral gas concentration measurements but no information regarding the distance traveled by the laser diode's beam or the distribution of the gas along the optical path. We complemented the set-up with a laser rangefinder and apply principles of Computed Tomography (CT) to create a model of the spatial gas distribution from these integral concentration measurements. To allow for a rudimentary ground truth evaluation of the applied gas tomography algorithm, we set up a unique outdoor test environment based on two 3D ultrasonic anemometers and a distributed array of 10 infrared gas transmitters. We present first results showing the 2D plume reconstruction capabilities of the system under realistic conditions. T2 - IEEE Sensors 2018 CY - New Delhi, India DA - 28.10.2018 KW - Aerial robot KW - TDLAS KW - Gas tomography KW - Plume PY - 2018 SN - 978-1-5386-4707-3 SP - 396 EP - 398 PB - IEEE AN - OPUS4-46477 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas T1 - Einsatz modifizierter Sprühlichtbogenprozesse zur Optimierung schweißbedingter Beanspruchungen an Bauteilen aus hochfesten Feinkornbaustählen N2 - In dem IGF-Vorhaben IGF-Nr. 17978 N (P 1011) wurden unter gezielter definierter Schrumpfbehinderung Schweißexperimente an hochfesten Feinkornbaustählen durchgeführt, um den Einfluss der Wärmeführung sowie den Einsatz modifizierter Sprühlichtbogenprozesse verbunden mit schmaleren Nahtfugen auf die lokalen Eigenspannungen und die Gesamteigenbeanspruchungen an geschweißten Bauteilen zu analysieren. Diese Kurzdarstellung fasst die wesentlichen Zusammenhänge zu schweißbedingten Beanspruchungen an hochfesten Schweißverbindungen sowie einige der erarbeiteten Erkenntnisse und erreichten Ziele des Forschungsprojektes zusammen. KW - Schweißverbindung KW - Eigenspannungen KW - Hochfester Feinkornbaustahl KW - Schweißprozess PY - 2016 SP - 1 EP - 2 AN - OPUS4-38653 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kannengießer, Thomas T1 - Crack resistance of supermartensitic steel pipeline welds in offshore industry N2 - The increasing application of supermartensitic steels for welded pipelines is an economical alternative to the hitherto used higher-alloyed materials in the North Sea oil and gas indus-try. Failure in such constructions must at any rate be excluded for economical and ecologi-cal reasons. The application of these steels for the transport of corrosive mixtures may, however, involve hydrogen pickup with subsequent hydrogen-assisted stress corrosion cracking. It is therefore necessary not only to assure the weldability, but particularly to have best possible knowledge of the service behaviour and of the failure risk. In order to ensure the transferability of test results to real joined components, innovative test methods are in-creasingly required to be incorporated into a closed test sequence. It will be demonstrated how it is possible to gain significant advantages from the direct comparison between ex-perimentally determined results from component weld tests on the one hand and material-specific data from small-scale tests on the other hand and numerical simulations. These data that have now been made available are of major importance for industrial applications and are considered to provide a sound basis for realistic lifetime assessments. T2 - Conference Welding and Related Inspection Technologies, IIW CY - Stellenbosch, South Africa DA - 08.03.2006 KW - Supermartensitics KW - Hydrogen pickup KW - Hydrogen diffusion KW - Permeation experiments KW - Component tests KW - Numerical simulation KW - Closed test sequence PY - 2006 SP - 1 EP - 14 PB - Beta Products cc CY - Lyttelton, South Africa AN - OPUS4-38925 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Kannengießer, Thomas T1 - List of questions relating to the revision of ISO 3690 regarding the acceptance of the carrier gas hot extraction method N2 - Is it reasonable to restrict ISO 3690 any longer to the determination of the weld metal hydrogen content of ferritic steel? In what respect is the determination of the content of the diffusible and of the total hydrogen content, respectively, (still) merely a research task (supermartensite, duplex materials, austenite, magnesium, aluminium), or is there actually a demand in industry and is there already a first cause for monitoring in view of damage prevention, respectively? Is there a need, arising from the development of materials and filler materials and from their intended applications, for more extensive standards dealing with hydrogen analyses for these materials? Which parts of ISO 3690 could also be applied to any other metallic material/filler material, if necessary, and where would a complete alteration be required, respectively? KW - ISO 3690 KW - List of questions KW - Carrier gas KW - Extraction method PY - 2004 SP - 1 EP - 11 PB - IIW CY - USA AN - OPUS4-39260 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Altenburg, Simon A1 - Scheuschner, Nils A1 - Straße, Anne A1 - Gumenyuk, Andrey A1 - Maierhofer, Christiane T1 - Towards the determination of real process temperatures in the LMD process by multispectral thermography N2 - Due to the rapid thermal cycles involved in additive manufacturing of metals, high internal stresses and peculiar microstructures occur, which influence the parts mechanical properties. To systematically examine their formation, in-process measurements of the temperature are needed. Since the part emissivity is strongly inhomogeneous and rapidly changing in the process, the applicability of thermography for the determination of thermodynamic temperatures is limited. Measuring the thermal radiation in different wavelengths simultaneously, temperature and emissivity can be separated. Here, we present results of a preliminary study using multispectral thermography to obtain real temperatures and emissivities in directed energy deposition (DED) processes. T2 - Thermosense: Thermal Infrared Applications XLIII CY - Online meeting DA - 12.04.2021 KW - Additive Manufacturing KW - Process monitoring KW - Multispectral thermography KW - Laser metal deposition KW - TES KW - LMD KW - Temperature emissivity separation PY - 2021 DO - https://doi.org/10.1117/12.2587881 VL - 2021 SP - 77 EP - 83 PB - SPIE AN - OPUS4-52516 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Breese, Philipp Peter A1 - Becker, Tina A1 - Oster, Simon A1 - Altenburg, Simon A1 - Metz, C. A1 - Maierhofer, Christiane T1 - Aktive Laserthermografie im L-PBF-Prozess zur in-situ Detektion von Defekten N2 - Die zerstörungsfreie Prüfung von metallischen Bauteilen hergestellt mit additiver Fertigung (Additive Manufacturing - AM) gewinnt zunehmend an industrieller Bedeutung. Grund dafür ist die Feststellung von Qualität, Reproduzierbarkeit und damit auch Sicherheit für Bauteile, die mittels AM gefertigt wurden. Jedoch wird noch immer ex-situ geprüft, wobei Defekte (z.B. Poren, Risse etc.) erst nach Prozessabschluss entdeckt werden. Übersteigen Anzahl und/oder Abmessung die vorgegebenen Grenzwerte für diese Defekte, so kommt es zu Ausschuss, was angesichts sehr langer Bauprozessdauern äußerst unrentabel ist. Eine Schwierigkeit ist dabei, dass manche Defekte sich erst zeitverzögert zum eigentlichen Materialauftrag bilden, z.B. durch thermische Spannungen oder Schmelzbadaktivitäten. Dementsprechend sind reine Monitoringansätze zur Detektion ggf. nicht ausreichend. Daher wird in dieser Arbeit ein Verfahren zur aktiven Thermografie an dem AM-Prozess Laser Powder Bed Fusion (L-PBF) untersucht. Das Bauteil wird mit Hilfe des defokussierten Prozesslasers bei geringer Laserleistung zwischen den einzelnen gefertigten Lagen unabhängig vom eigentlichen Bauprozess erwärmt. Die entstehende Wärmesignatur wird ort- und zeitaufgelöst durch eine Infrarotkamera erfasst. Durch diese der Lagenfertigung nachgelagerte Prüfung werden auch zum Bauprozess zeitversetzte Defektbildungen nachweisbar. In dieser Arbeit finden die Untersuchungen als Proof-of-Concept, losgelöst vom AM-Prozess, an einem typischen metallischen Testkörper statt. Dieser besitzt eine Nut als oberflächlichen Defekt. Die durchgeführten Messungen finden an einer eigens entwickelten L-PBF-Forschungsanlage innerhalb der Prozesskammer statt. Damit wird ein neuartiger Ansatz zur aktiven Thermografie für L-PBF erforscht, der eine größere Bandbreite an Defektarten auffindbar macht. Der Ansatz wird validiert und Genauigkeit sowie Auflösungsvermögen geprüft. Eine Anwendung am AM-Prozess wird damit direkt forciert und die dafür benötigten Zusammenhänge werden präsentiert. T2 - DGZfP-Jahrestagung 2022 CY - Kassel, Germany DA - 23.05.2022 KW - Additive Manufacturing KW - Laser Powder Bed Fusion KW - Thermografie KW - Zerstörungsfreie Prüfung KW - Aktive Laserthermografie PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-550353 SN - 978-3-947971-25-1 VL - 177 SP - 1 EP - 9 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung e.V. AN - OPUS4-55035 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Oster, Simon A1 - Scheuschner, Nils A1 - Chand, Keerthana A1 - Breese, Philipp Peter A1 - Becker, Tina A1 - Heinrichsdorff, F. A1 - Altenburg, Simon T1 - From Thermographic In-situ Monitoring to Porosity Detection – A Deep Learning Framework for Quality Control in Laser Powder Bed Fusion N2 - In this study, we present an enhanced deep learning framework for the prediction of porosity based on thermographic in-situ monitoring data of laser powder bed fusion processes. The manufacturing of two cuboid specimens from Haynes 282 (Ni-based alloy) powder was monitored by a short-wave infrared camera. We use thermogram feature data and x-ray computed tomography data to train a convolutional neural network classifier. The classifier is used to perform a multi-class prediction of the spatially resolved porosity level in small sub-volumes of the specimen bulk. T2 - SMSI - Sensor and Measurement Science International 2023 CY - Nürnberg, Germany DA - 08.05.2023 KW - Porosity KW - Laser powder bed fusion KW - In-situ monitoring KW - Thermography KW - Machine Learning PY - 2023 UR - https://www.ama-science.org/proceedings/details/4404 DO - https://doi.org/10.5162/SMSI2023/C5.4 SP - 179 EP - 180 AN - OPUS4-57616 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Nina A1 - Rhode, Michael A1 - Kannengießer, Thomas T1 - Einfluss unterschiedlicher Mikrolegierungsrouten eines S690QL auf das Ausscheidungsverhalten in der Wärmeeinflusszone N2 - Mikrolegierungselementen, wie Nb und Ti sind für eine signifikante Festigkeitssteigerung von vergüteten, hochfesten Feinkornbaustählen mit einer Nominalstreckgrenze ≥ 690 MPa unerlässlich. Normvorgaben zur chemischen Zusammensetzung dieser Stähle geben zur Erzielung der vorgeschriebenen Eigenschaften dabei oft nur Grenzgehalte für die Hersteller vor. Die Wirkung der Mikrolegierungselemente bzw. ihrer Karbide und/oder Nitride ist teilweise komplett konträr, insbesondere bei Auflösung und Wiederausscheidung in der WEZ bei identischem Schweißzusatz. Somit wird eine adäquate Vorhersage der Chargenabhängigkeit hinsichtlich der Schweißeignung und des Tragverhaltens der Schweißverbindung erschwert. Eine unerwünschte Eigenschaft ist dabei die Erweichung der WEZ, wie auch u.U. der gegenteilige Effekt der Aufhärtung. Vor diesem Hintergrund werden im Rahmen eines DFG-Vorhabens systematisch Mikrolegierungs-routen mit variierenden Ti- und Nb-Gehalten des hochfesten und vergüteten Feinkornbaustahls S690QL untersucht. Dazu wird das MAG-Schweißen mit modifizierten Sprühlichtbogen verwendet, welches durch hohe Abschmelzleistung gekennzeichnet ist und schmalere Nahtöffnungswinkel (α = 30°) ermöglicht. An Dreilagen-Schweißungen wird der Effekt der metallurgischen Zusammensetzung in Kombination mit hoher Wärmeeinwirkung auf die Ausbildung einer kritischen WEZ-Gefügezone mit Erweichung und/oder exzessiver Aufhärtung untersucht. Ein besonderes Augenmerk wird auf die Phasenumwandlungen und das Ausscheidungsverhalten im Gefüge der Wärmeeinflusszone gelegt. Neben umfangreichen metallographischen Untersuchungen einzelner WEZ-Bereiche wurden, unter Variation der chemischen Zusammensetzung, thermodynamische Phasenberechnungen mittels Thermo-Calc durchgeführt. Hierdurch wird ein Verständnis zur Phasentransformation und Ausscheidungswachstum und -auflösung während des Schweißens in Abhängigkeit von Temperatur und Abkühlbedingungen geschaffen. Das Ziel ist es, den Einfluss der Wärmeeinwirkung auf die Gefügeausbildung in der WEZ und dessen mechanischer Eigenschaften zu analysieren. Insbesondere wird hier auf die Auswirkung der unterschiedlichen Mikrolegierungskonzepte (Ti oder Nb) geachtet. T2 - 5. Symposium Materialtechnik CY - Clausthal-Zellerfeld, Germany DA - 23.02.2023 KW - WEZ Erweichung KW - Thermodynamische Simulation KW - Mikrolegierungseinfluss KW - Schweißen von hochfesten FKB PY - 2023 SN - 978-3-8440-9105-2 VL - 12 SP - 332 EP - 343 PB - Shaker Verlag AN - OPUS4-58006 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gibmeier, J. A1 - Weidemann, Jens A1 - Dixneit, Jonny A1 - Kannengießer, Thomas A1 - Kromm, Arne T1 - Influence of structural stiffness on the residual stresses during welding of low transformation temperature alloys N2 - Low Transformation Temperature (LTT) alloys are high alloyed filler materials, which exhibit a martensitic phase transformation at comparatively low temperatures in order to prevent high tensile residual stresses. A number of publications have already shown that even compressive residual stresses can be observed when using LTT filler materials. Up to know it is not clear in which way this it applicable to multi-run welding exhibiting high shrinkage restraint and complex heat input. In this study the potential for stress reduction during welding of LTT alloys was studied by numerical simulation. This allows for evaluation of the stress development in every single weid run. Additionally, the impact of the structural stiffness was incorporated by modelling a special sample geometry exhibiting a high intensity of restraint. The results show that the stress formation in weid longitudinal direction is determined by the phase transformation as high compressive residual stresses were found here independent from the weid run. On the other hand the transformation induced stresses in weid transverse direction are superimposed by tensile stresses originated from shrinkage restraint. With increasing number of runs the tensile residual stress level is raised. The results were confirmed by residual stress measurements using diffraction methods. T2 - 11th International Seminar - Numerical Analysis of Weldability CY - Graz, Austria DA - 27.09.2015 KW - Influence KW - Structural stiffness KW - Residual stresses KW - Low transformation KW - Temperature alloys KW - Welding PY - 2016 SN - 978-3-85125-490-7 SN - 2410-0544 SP - 259 EP - 276 PB - Verlag der Technischen Universität Graz CY - Graz AN - OPUS4-38998 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ecke, Alexander A1 - Bell, Jérémy A1 - Schneider, Rudolf T1 - From Laboratory Immunoassays to Immunosensors with an Integrated Microfluidic Flow System N2 - This research summary describe efforts to the development of a three-dimensional microfluidic flow cell for improved electrochemical substrate detection in HRP/TMB-based immunoassays. This work provides a valuable advancement in the sensitivity and integration of immunoassay technologies, aiding in the refinement of diagnostic tools. KW - Antikörper KW - Immunoassay KW - Microfluidics KW - Electrochemical detection KW - Biosensor PY - 2025 UR - https://www.elveflow.com/microfluidics-research-summaries/from-laboratory-immunoassays-to-immunosensors-with-an-integrated-microfluidic-flow-system/ SP - 1 EP - 4 CY - Paris AN - OPUS4-62674 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kannengießer, Thomas A1 - Schröpfer, Dirk T1 - Key aspects of component welding applying higher-strength fine-grained structural steels N2 - The increased application of higher-strength steels and filler materials necessitates a more profound understanding of the interactions between the welding process, the heat input, the cooling conditions and the resulting metallurgical processes in the weid and its surroundings. Strategies, which help to improve the strength properties and life-time of welded stmctures to such an extent that the utilisation of higher-strength materials can be justified and their lightweight construction potential can thus be exploited to the füll, can only be derived from the interaction between all the influencing factors. Examples of a few investigations on welded joints between higher-strength fine-grained structural steels with regard to the interactions between the main variables influencing the cold cracking are presented in this article. T2 - 7th International Conference on Weiding Science and Engineering in conjunction with 3rd International Symposium on Computer-Aided Welding Engineering CY - Jinan, China DA - 18.10.2017 KW - Higher-strength steels KW - Cold cracking KW - Residual stresses KW - Heat control PY - 2017 SP - 437 EP - 446 AN - OPUS4-43235 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Griesche, Axel A1 - Dabah, Eitan A1 - Hilger, A. A1 - Kardjilov, N. A1 - Manke, I. A1 - Kannengießer, Thomas T1 - Neutron imaging of hydrogen in steels N2 - Transmission images with neutrons show a high contrast between hydrogen and iron when using state-of-the-art scintillator materials and digital Cameras. Monitoring the 2D hydrogen distribution evolution with good temporal resolution is possible if a high flux of neutrons is provided. The mass transport of hydrogen can be quantified by Converting the intensity distribution of the images in a hydrogen concentration distribution by using Standards with known composition and similar thickness. Then neutron radiography can be used quantitatively as a non-destructive measurement technique to determine diffusion coefficients e.g. for hydrogen in Steel. We report about measurements at Research Reactors in Germany. The capabilities and limitations, s well as perspectives of this method will be discussed and illustrated with selected examples. T2 - Materials Science & Technology (MS&T) 2013 CY - Montreal, Quebec, Canada DA - 27.10.2013 KW - Neutron radiography KW - Hydrogen KW - Diffusion KW - Steel PY - 2013 SP - 945 EP - 950 PB - Curran CY - Red Hook, NY AN - OPUS4-29506 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Martin A1 - Wille, Frank A1 - Linnemann, Konrad A1 - Schubert, Sven A1 - Ballheimer, Viktor A1 - Sterthaus, Jens A1 - Droste, Bernhard T1 - Reflection on BAM mechanical design assessment of TN®24E spent fuel transport package N2 - TN®24 E, a new package design, was developed and applied for by Areva TN for German transport approval certificate. The certificate was issued by BfS, Federal Office for Radiation Protection, on 24th of July 2013. The package is designed as a dual purpose cask for transport and storage of up to 21 PWR spent fuel assemblies from German NPPs. BAM is the German competent authority responsible for the design assessment of RAM packages regarding mechanical and thermal safety cases, activity release analysis and all issues of quality assurance during manufacturing and operation of packages. Certain assessment experiences as well as new developments resulting from the BAM TN®24E approval procedure are presented. The mechanical safety case of the TN®24E is based mainly on finite element calculations, which were verified by the TN®81 1/3 scale drop test program performed at BAM. Thermal analyses rely upon calculations, while the activity release criterion is based upon leakage rate results of TN®81 drop tests. The BAM-GGR 012 guideline for the analysis of bolted lid and trunnion systems has been fully implemented. Due to requirements by BAM, AREVA TN developed a new assessment strategy for fracture mechanical evaluation of welding seams. The material qualification and documentation is also an important aspect of BAM assessment; the qualification of borated aluminum basket material, the determination of strength values for thermal aged hardened aluminum alloys for the basket or consideration of high burn-up fuel assemblies are remarkable issues in this context. In addition, the consideration of the material compatibility, especially taking into account a transport after 40 years of dry interim storage in German facilities, has gained significant importance in the licensing process of the TN®24E. Next to obvious mechanical issues such as the assessment of shell ovalization under 9 m drop test scenario and its impact on basket load, thermo-mechanical interactions had to be addressed in the safety case. Due to BAM requirements, AREVA TN performed a full thermo-mechanical analysis of the cask behavior under fire test conditions. T2 - PATRAM 2013 - 17th International symposium on the packaging and transportation of radioactive materials CY - San Francisco, CA, USA DA - 18.08.2013 KW - Transport KW - RAM KW - Radioactive material cask KW - Nuclear fuel PY - 2013 SP - 1 EP - 12 PB - Omnipress AN - OPUS4-30270 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eisenacher, Germar A1 - Scheidemann, Robert A1 - Neumann, Martin A1 - Wille, Frank A1 - Droste, Bernhard T1 - Crushing characteristics of spruce wood used in impact limiters of type B packages N2 - The material spruce wood is frequently used in impact limiters of Type B transport packages. In order to develop and parametrize an appropriate finite element material model, the crushing characteristics of spruce wood have been determined. A large number of crush tests was performed at BAM test facilities to generate a comprehensive data base. The parameter range in the crush test series results amongst others from the IAEA Regulations for the Safe Transport of Radioactive Material: e. g., the minimum temperature considered was -40 °C and the maximum strain rate applied was derived from the 9 m drop test. Cubical spruce wood specimens were tested using a servo hydraulic impact testing machine for initial strain rates of up to 30 1/s. A machine for guided drop tests was used for initial strain rates of up to 133 1/s. Drop masses of up to 1,200 kg were therefore used from drop heights of up to 9 m. The results presented in the paper include force-displacement characteristics and deformation behavior of spruce wood. Thereby the effects of strain rate, temperature, fiber-load orientation and lateral constraint are considered. Higher strain rates led to increasing crush forces, especially for loading perpendicular to the fiber. Higher temperature resulted in decreasing crush forces. The crush force level was significantly lower for load perpendicular to the fiber and the crushing characteristics differed compared to load parallel to the fiber. Without lateral constraint, the specimens expanded laterally, i. e. the plastic Poisson's ratio (if wood is considered a continuum) was not zero. Crush forces were comparably low and for load parallel to the fiber there was a significant softening effect. Lateral constraint of the specimens increased the crush force level and limited the softening effect. The results of the crush tests are used to derive modeling requirements and some assumptions for the development of a finite element material model for spruce wood. Possible future research work is pointed out. T2 - PATRAM 2013 - 17th International symposium on the packaging and transportation of radioactive materials CY - San Francisco, CA, USA DA - 18.08.2013 KW - Spruce wood KW - Crush test KW - Impact limiter PY - 2013 SP - 1 EP - 10 PB - Omnipress AN - OPUS4-30219 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Martin A1 - Wille, Frank A1 - Droste, Bernhard T1 - Experience feedback from BAM safety assessment of transport packages N2 - BAM as competent authority regarding assessment of mechanical and thermal design, activity release and quality assurance measures of Type-B(U) transport packages developed a thesaurus of experience feedback topics from recent assessment procedures. The list is structured according to the European PDSR guide. It involves issues, which from BAM's point of view, needed clarification during the last package design assessment procedures. The list contains issues from Operation (e.g. deactivation of handling lugs not intended for package handling), maintenance (e.g. leak tightness of impact limiting devices) to technical assessment (e.g. formation of hydrogen by radiolysis and its impact on pressure and ignitability, consideration of ageing mechanisms, thermo-mechanical assessment, impact of gaps between content and flask) as well as to general and specific safety analysis report requirements (e.g. report structure and required data). T2 - RAMTRANS 2015 - 10th International conference on radioactive materials transport and storage CY - Oxford, UK DA - 19.05.2015 KW - Transport KW - RAM KW - Radioactive material KW - Cask KW - Flask KW - Nuclear fuel PY - 2015 SP - 1 EP - 7 AN - OPUS4-33420 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hahn, Oliver A1 - Rabin, Ira A1 - Wolff, Timo A1 - Kanngießer, B. A1 - Malzer, W. A1 - Mantouvalou, I. A1 - Schade, U. A1 - Masic, Admir A1 - Weinberg, G. T1 - Non-destructive investigation of the dead sea scrolls N2 - The Dead Sea Scrolls belong to the most important cultural assets of mankind. Their long term preservation and study is a challenge that demands an interdisciplinary approach. As early as the 1950s natural scientists assisted the scholars in studying the scrolls. It was at this time that the first extensive study of the scroll material took place. It was found that most fragments were written not on leather but on parchment. In addition, a method for determining the age of the parchment was developed which is still of value today. In the 1990s the AMS-C14 method confirmed the palaeographic determination of the age of the manuscripts. The use of carbon ink throughout the scrolls is also consistent with the known scribal practices of that time. There are, however, manuscripts, and among them the famous Genesis Apocryphon Scroll, which exhibit ink corrosion, normally associated with iron-gall inks. Today, 60 years after their discovery, a community of scientists from the Jewish National and University Library (JNUL), the Technical University of Berlin (TU Berlin), the Federal Institute for Materials Research and Testing (BAM) and Fritz-Haber-Institute of the MPG (FHI) set out to scientifically investigate the finds of Qumran using the most modern methods. The results of the study will be used to determine the provenance of the texts as well as to contribute to their long-term preservation. A considerable part of the non-destructive investigation is taking place in the Berlin State Library and at the Berliner Elektronenspeicherring-Gesellschaft für Synchrotronstrahlung , BESSY II. Preliminary investigations, performed at the BAM on some fragments, were used to evaluate the extent to which X-ray analytical methods can provide information regarding the geographical origin of the fragments and match the individual pieces. The interpretation of the measurement results is made more difficult by age and storage of the objects. It is believed that ageing processes as well as conservation methods have altered the samples in addition to the changes caused by environmental influences. In collaboration with the TU Berlin, the samples from the parchments found in the caves near Qumran were tested by means of three-dimensional synchrotron based X-ray fluorescence analysis (3D-SyXRF). The aim of this non-destructive investigation was the identification of the inorganic material used in the manufacture of the parchments. The XRF experiments are supported by the non-destructive analysis by means of synchrotron based infrared spectroscopy (SyFTIR) in collaboration with BESSY II as well as optical and electron microscopy in collaboration with Fritz-Haber-Institute (FHI). T2 - Art 2008, 9th International Conference CY - Jerusalem, Israel DA - 2008-05-25 KW - Cultural heritage KW - Archaeometry KW - Micro-XRF KW - Quantification KW - Parchment KW - DSS PY - 2008 IS - CD-ROM SP - 1 EP - 7 PB - ISAS International Seminars CY - Jerusalem, Israel AN - OPUS4-17547 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rabin, Ira A1 - Hahn, Oliver A1 - Wolff, Timo A1 - Mantouvalou, I. A1 - Kanngießer, B. A1 - Weinberg, G. T1 - Material studies on the Dead Sea scrolls T2 - Conference "Preservation and access of monuments of culture and history: modern approaches" CY - Saint Petersburg, Russia DA - 2009-10-20 KW - Dead Sea scrolls KW - Archaeometry KW - Restoration and conservation science KW - Cultural heritage KW - Writing materials PY - 2009 SP - 122 EP - 129 AN - OPUS4-23177 LA - rus AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wiegner, Katharina A1 - Hahn, Oliver A1 - Farke, M. A1 - Kalus, Sabine A1 - Horn, Wolfgang T1 - Determination of formic and acetic acids in air N2 - Formic and acetic acids are often responsible for damage of cultural objects, e. g. glass and metal corrosion or changing and fading of colours. Museums all around the world are equipped with different show cases. Display cases should protect cultural objects from dust as well as from mechanical damage. Several construction materials which are used for display cases, including wood, glue and coatings, are possible sources of very volatile organic compounds (VVOCs), volatile organic compounds (VOCs) and semi volatile organic compounds (SVOCs). These construction products can emit formic and acetic acids into the indoor or display case air. Modern display cases with small air change rates can cause higher concentrations of formic and acetic acids if any source is installed in the display case (Salthammer and Uhde, 2009). To minimize the risk of damage emissions from building products must be quantified. There is a need for a method for identification and quantification of acetic and formic acid. Some possibilities for the identification of acetic acid exist. The quantification of acetic acid for example after sampling on TENAX® or CARBOTRAP and thermal desorption-GC in accordance with ISO 16000-6 and ISO 16017-1 results in very low recovery rates. A new method should be stabile, robust, reproducible and comparable, with an easy local sampling and determination in laboratories. Miniaturised emission test chambers and model display cases were used to study the recovery rates. T2 - Indoor Air 2011, 12th International conference on indoor air quality and climate CY - Austin, TX, USA DA - 05.06.2011 KW - VOCs KW - Detection of formic and acetic acid KW - Quantification of formic and acetic acid KW - Air sampling PY - 2011 IS - Paper 768 SP - 1 EP - 2 AN - OPUS4-23876 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hahn, Oliver A1 - Malzer, W. A1 - Kanngießer, B. A1 - Waldschläger, U. T1 - A fingerprint model for inhomogeneous ink-paper layer systems measured with micro X-ray fluorescence analysis N2 - Nowadays, micro-x-ray fluorescence analysis has become an established tool for the non-destructive investigation of art objects. However, as these types of sample often forms complex and inhomogeneous layer systems, the quantitative evaluation of the measurements is far from a standard routine. In this paper a fingerprint model is described, which we developed to discriminate between different iron-gall inks of historical manuscripts or compositions. Fundamental parameter methods are used to take self-attenuation, interference from the paper background and diffusion of the ink into the paper into account. The capability of the method to contribute to the solution of archaeometric problems is exemplified by the investigation of an ancient composition. Finally, the restrictions of the model and possible improvements are discussed. Copyright © 2004 John Wiley & Sons, Ltd. T2 - 10th European Conference on Energy Dispersive X-Ray Spectrometry (EDXRS) CY - Berlin, Germany DA - 2002-06-16 PY - 2002 SP - 120 AN - OPUS4-1403 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hahn, Oliver A1 - Malzer, W. A1 - Kanngießer, B. T1 - Characterization of iron gall inks in historical manuscripts and music compositions using X-ray fluorescence spectrometry T2 - 7th International Conference on Non-destructive testing and Microanalysis for the Diagnostics and Conservation of the Cultural and Environmental Heritage ; art 2002 CY - Antwerp, Belgium DA - 2002-06-02 PY - 2002 SP - 80 AN - OPUS4-1394 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hahn, Oliver A1 - Malzer, W. A1 - Kanngießer, B. T1 - Model for inhomogeneous ink paper layer systems measured with micro X-ray fluorescence analysis T2 - 7th International Conference on Non-destructive testing and Microanalysis for the Diagnostics and Conservation of the Cultural and Environmental Heritage CY - Antwerp, Belgium DA - 2002-06-02 PY - 2002 SP - 202 AN - OPUS4-1393 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hahn, Oliver A1 - Malzer, W. A1 - Kanngießer, B. A1 - Beckhoff, B. A1 - Waldschläger, U. T1 - Characterization of iron gall inks in historical manuscripts using micro X-ray fluorescence spectrometry T2 - European Conference on Energy Dispersive X-Ray Spectrometry (EDXRS) CY - Berlin, Germany DA - 2002-06-16 PY - 2002 SP - 83 AN - OPUS4-1404 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Kemmlein, Sabine A1 - Hahn, Oliver A1 - Jann, Oliver T1 - Emission of Flame Retardants from Consumer Products and Building Materials (Research Report 299 65 321 / UBA-FB 00,475) N2 - Various insulating boards, assembly foams, PC-systems, upholstery and a mattress were examined for possible emissions of polybrominated and organophosphorus flame retardants. 0.02 m3- and 1m3- emission test chambers and 1Llitre cells were used to perform the investigations. The substances of interest are mainly classified as SVOC. A sampling technique using polyurethane foam plugs and special analytical methods was developed. The PUF-plugs were extracted by ultrasonic and soxhlet extraction and the extracts were concentrated. The analyses were performed by GC/MS and HPLC/DAD. Chamber measurements were generally taken over 28 days, but in the case of SVOC, a test period of a minimum of 100 days was necessary to achieve equilibrium. The determination of most of OPCs was successful using emission test chambers. Due to sink effects the determination of low volatile OPC such as RDP and BDP needs to be improved. Brominated flame retardants are quantifiable up to hexabrominated compounds using emission test chambers as a reference method. The emission of lower volatile compounds, e.g. HBCD, was strongly affected by sink effects. Emission of decaBDE was not quantifiable at all. Based on the results presented further investigations are required for an adequate risk assessment of flame retarded products and their contribution to the contamination of the indoor air environment. TCPP was found to be one of the most commonly used organophosphorus flame retardants in polyurethane foam applications. Depending on the sample type 0.012 to 140 µg m-2 h-1 was obtained for area-specific emission rates (SERa) for TCPP. PBDEs, for example, exhibited product-specific emission rates (SERu) between 0.1 and 14.2 ng unit-1 h-1 and SERa between 0.2 and 6.6 ng m-2 h-1. More data about the emission behaviour of FR are required with special regard to substance migration, aging and long-term emission in particular. KW - Emission KW - Semi volatile organic compounds (SVOC) KW - Polybrominated flame retardants KW - Organophosphorus flame retardants PY - 2003 UR - http://www.umweltbundesamt.de/publikationen/emission-of-flame-retardants-from-consumer-products SP - 1 EP - 188 PB - Umweltbundesamt CY - Dessau-Roßlau AN - OPUS4-11186 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Glaser, L. A1 - Shevchuk, I. A1 - Tolkiehn, M. A1 - Rabin, Ira A1 - Hahn, Oliver T1 - Improving Iron Gall Ink Palimpsest X-ray Fluorescence Element Mapping Analysis N2 - In the recent years multispectral imaging and X-ray Fluorescence element mapping have established themselves as a well working two step approach, when dealing with faded, erased or overwritten text in iron gall ink. During the last years a lot was done to improve the mere technical side of the techniques. Especially in the case of XRF mapping experiments the acquisition speed needed to be increased to allow mapping in the high resolution demanded by the challenges at hand. High resolution in moderate times can now be achieved, but with the price of proportionally increased amount of data that needs to be processed ideally in parallel to the measurement. The classical approach in XRF spectroscopy of elemental fitting of the spectral data does not even come close to fulfill any on the fly processing time constraints and will consume too much processing time in the foreseeable future. In this paper we will discuss the applicability of modern statistical data processing methods to XRF mapping of iron gall ink palimpsests. We will present a comparison of a new approach based on principle and independent component analysis (PCA and ICA) and the standard element mapping method. We will show that a reduction in processing time of almost two orders of magnitude can easily be achieved. T2 - Kongress Visual Heritage, CHNT 23 CY - Vienna, Austria DA - 15.11.2018 KW - Palimpsest KW - Iron-gall ink PY - 2020 SP - 1.1 EP - 1.9 AN - OPUS4-50243 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rabin, Ira A1 - Hahn, Oliver A1 - Kaska, K. ED - Uhlirz, T1 - Why Do We Need to Study Inks? N2 - While studying the socio-geographic history of inks, division 4.5 (Analysis of cultural artefacts and assets) of the BAM (Bundesanstalt für Materialforschung und -prüfung) in Berlin together with the Centre for the Study of Manuscript Cultures in Hamburg has developed a protocol for ink analysis. It consists of a primary screening to determine the type of the ink, and a subsequent in-depth analysis using several spectroscopic techniques. Using this protocol, scientists can assist scholars in addressing a rather broad range of historical questions that cannot be answered unequivocally through scholarly research alone. Among these are investigations on collaboration between scribes and scriptoria, on the usage and annotation of manuscripts and on their path through time and space in general. This research can thus help to reconstruct the circumstances of the production of written heritage as well as their history and transmission. To facilitate the dialogue between the scholars and the scientists a simple optical tool was developed to allow the scholars to perform preliminary ink analysis required for formulation of the question that in turn can be answered by scientific in-depth investigations. In this paper, ink types and their identification method is accompanied by examples of the recent work conducted on parchment manuscripts in the Austrian National Library. T2 - Congress Visual Heritage, CHNT 23 CY - Vienna, Austria DA - 15.12.2018 KW - Ink KW - Parchment PY - 2020 SP - 1.1 EP - 1.9 CY - Wien AN - OPUS4-50242 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Steger, Simon T1 - Non-invasive spectroscopic investigation of cultural artefacts: shedding light on modern reverse glass paintings N2 - This thesis addresses the development of a methodological approach for the non-invasive identification of colourants and for the classification of binding media in reverse glass paintings from the early 20th century. For this purpose, mobile and miniaturized devices were used to measure the paintings in situ. The methodology includes X-ray fluorescence (XRF), VIS spectroscopy (VIS), Raman spectroscopy and diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS). In a first step the capabilities of DRIFTS for binding media classification and pigment identification were tested. DRIFTS enables, besides Raman spectroscopy, the collection of molecular information of a substance that can be used as characteristic fingerprint spectrum. However, the simultaneous collection of both specular (surface) and diffuse (volume) reflection leads to complicated mixed DRIFT spectra, that can vary strongly for one substance depending on the dominant fraction of reflected light. Specular reflection causes several spectral distortions like inverted bands, band shifts and derivative-like features whereas pure diffuse reflections leads to an intensity enhancement of combination bands and overtones. Both specular and diffuse reflection cannot be optically separated, and their proportion depends on material properties like the absorption coefficient and the refractive index as well as on Parameters like surface roughness, porosity, grain size and angle of incidence and detection. A direct comparison of DRIFT spectra with IR spectra of other methods (e.g. transmission, ATR) is not possible, hence the creation of DRIFTS databases was needed. The next step was the complimentary utilization of Raman spectroscopy and DRIFTS for the dentification of synthetic organic colourants. Such colourants are in the further chapters called synthetic organic pigments (SOP) even when it’s not always entirely clear if they are soluble dyes or pigments that are practically insoluble in the medium in which they are incorporated. Raman spectroscopy is generally the method of choice when dealing with SOP, but fluorescence can hamper the Raman spectrum severely, inhibiting the proper identification of the pigment. DRIFTS was successfully applied and several SOP like synthetic alizarin (PR83), the yellow azo pigments (e.g. PY1) or the red and orange β-naphthol pigments (e.g. PR3) could be identified in the paintings solely by means of DRIFTS. The holistic methodological sequence was defined after the successful establishment of DRIFTS as serious analytical alternative. As the time is always the most limiting factor for in situ measurement campaigns in museums, the 9 sequence needs to be time saving but also efficient. The methodology starts with quick measurements by XRF and VIS to get a first idea of the pigment composition, followed by the validation of the results with the vibrational spectroscopies for selected points. Measurements of reverse glass paintings by Carlo Mense and Wassily Kandinsky were conducted to test the entire procedure. A high number of pigments could be identified, including several rare ones like strontium white (SrSO4), PR60 and PB52. The binding media were classified using the previously recorded references. The results were set in the art historian context and were discussed in a multidisciplinary way. The influence of Asian art, especially of Chinese reverse glass paintings as source of inspiration for artists of the “Blauer Reiter” collective (e.g. Wassily Kandinsky, Gabriele Münter, Franz Marc und Heinrich Campendonk) is shown. Non-invasive measurements of two Chinese reverse glass paintings from the late 19th and early 20th century were conducted, enabling a comparison of the palettes of Chinese and European painters. The Chinese palette includes heavy use of red lead and orpiment, pigments that were hardly sed in Europe anymore. More modern pigments like zinc white, cadmium yellow, viridian, chromates, cobalt blues or SOP were not found at all in the Chinese paintings. KW - Reverse glass painting KW - Raman spectroscopy KW - DRIFTS KW - Non invasive analysis PY - 2020 SP - 12 EP - 104 CY - Hamburg AN - OPUS4-51160 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gleim, Tobias A1 - Neumann, Martin A1 - Linnemann, Konrad A1 - Komann, Steffen A1 - Wille, Frank T1 - Fracture Mechanical Analyses of a Welding Seam of a Thick-Walled Transport Package N2 - Transport packages shall satisfy various safety criteria regarding mechanical, thermal and radiation phenomena. Typical requirements focusing mechanical aspects are usually drop tests in accordance with IAEA regulations. The drop tests are usually carried out experimentally and, as an additional measure, finite element analyses (FEA) are performed. A specific part of the investigations presented is the evaluation of the welding seam connecting cask shell and cask bottom. Experimental results and FEA are presented and compared. The evaluation of the welding seam performed includes a variety of aspects. In addition to the experimental and analytical stresses determined, different standards are used to investigate a possible crack initiation. Several destructive and non-destructive tests are performed for quality assurance in the manufacturing process as well as for different input parameters. The necessary monitoring and non-destructive measurement methods to define the boundary conditions of the standards are introduced. Taking into account all required parameters, the welding seam is examined and evaluated using the failure assessment diagrams (FAD) of the respective standards. It can be shown under the given boundary conditions that considering the experimental data, the welding seam is in the context of crack initiation below the enveloping curve in the acceptable region. More critical drop tests to be conducted are proposed and need to be investigated in future work. T2 - Pressure Vessels & Piping Conference® 2022 CY - Las Vegas, NV, USA DA - 17.07.2022 KW - Transport package KW - Drop test KW - Fracture initiation PY - 2022 SP - 1 EP - 9 AN - OPUS4-55375 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schubert, Sven A1 - Reichardt, Adrian A1 - Wille, Frank A1 - Komann, Steffen A1 - Neumann, Martin T1 - Introduction of an ageing management approach for packages for the transport of radioactive materials N2 - With integration of the new para 613A into SSR-6 [1] the consideration of ageing mechanisms is now obligatory for the design of packages and their approval. In addition, para 809(f) of SSR-6 [1] requires consideration of the effects of storage on ageing mechanisms, safety analyses and operation and maintenance instructions. German competent authorities Bundesanstalt für Materialforschung und -prüfung (BAM) and Bundesamt für die Sicherheit der nuklearen Entsorgung (BASE) are considering the aspect of ageing in approval procedures. Ageing assessment is mainly focused on dual purpose casks (DPC) package designs which are long-term stored in interim storage facilities. For these package designs, the evaluation of ageing management is now mandatory for the maintenance of the package design approvals with a validity period of 5 years and beyond. The ageing management includes amongst others a gap analysis, the assessment of ageing effects and operational experiences during operation and interim storage. BAM works on the compilation of a guideline for implementation of paras 613A, 809(f) and 809(k) for packages requiring competent authority approval at the application procedure in Germany. The paper describes essential items of ageing mechanisms and will give a foresight to the ageing management evaluation by BAM. T2 - INMM & ESARDA Joint Annual Meeting CY - Online meeting DA - 30.08.2021 KW - Dual purpose casks KW - Ageing KW - SSR-6 KW - Interim storage KW - Ageing mechanisms KW - Transport of radaioactive materials PY - 2021 UR - https://www.abstractsonline.com/pp8/#!/10383/presentation/964 SP - 1 EP - 6 PB - Institute of Nuclear Materials Management (INMM) CY - Mount Laurel, NJ AN - OPUS4-53180 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nöller, Renate A1 - Hahn, Oliver ED - Dora, C. ED - Fabian, C. ED - Knoche, M. ED - Linder, M. ED - Mittler, E. ED - Schmitz, W. T1 - VIS-Spectroscopy of Aztec colors. Possible application of a non-destructive analytical method N2 - VIS-spectrometry is a rapid, non- invasive, mobile method that offers a first overview of possible colorants used for painting. This is worked out in detail for European paintings and applied for artefacts and illuminated manuscripts. Manuscripts from Asia for example show colorful decoration identified to be mostly prepared with mineral pigments such as cinnabar, azurite, malachite or orpiment, which can be well confirmed by elemental analyses due to their color-giving metal ions. This is not the case for the colorants used in pictorial manuscripts from pre-Hispanic America, painted mainly with organic dyes from plants. The palette of colors used by the Aztecs is very rich due to their extensive empire and long- distance communication with vassal states liable to tributes including dyes of high quality. These include for example red cochineal, yellow zacatlaxcalli, tagetes, safflower, and achiotl, as well as blue indigo, or matlalli. T2 - Manuscripta Americana: Aufarbeitung einer Sammlung CY - Ibero-Amerikanisches-Institut, SPK DA - 14.02.2019 KW - Pigments KW - Dyes KW - Humboldt Codices KW - Non-destructive test PY - 2020 SN - 978-3-447-11511-7 SN - 0067-8236 VL - 53 SP - 35 EP - 57 PB - Harrassowitz Verlag CY - Wiesbaden AN - OPUS4-51934 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hahn, Oliver A1 - Nöller, Renate ED - Dora, C. ED - Fabian, C. ED - Knoche, M. ED - Linder, M. ED - Mittler, E. ED - Schmitz, W. T1 - Writing inks in the Manuscripta Americana – a pilot study N2 - The manuscripts – which have been inventoried as Manuscripta Americana in the State Library of Berlin and the Biblioteka Jagellońska in Krakow with the signatures Ms. Americ. 1-15 – are codices mainly from the colonial times of the 16th to 18th centuries. They uniquely reflect the relationships between indigenous culture and Spanish colonial masters. This study focusses on the scientific investigation of three manuscripts (Manuscripta Americana 3, 8, and 10) that are kept today in Krakow. It is assumed that these three parts belong together in a certain way, so various material analyses were carried out to prove this assumption. The scientific investigation focusses on the different black and brown writing inks. T2 - Manuscripta Americana: Aufarbeitung einer Sammlung CY - Ibero-Amerikanisches-Institut, SPK DA - 14.02.2019 KW - Humboldt Codices KW - Writing inks KW - Non-destructive testing PY - 2020 SN - 978-3-447-11511-7 SN - 0067-8236 VL - 53 SP - 21 EP - 32 PB - Harrassowitz Verlag CY - Wiesbaden AN - OPUS4-51935 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nagelschmidt, Sven T1 - Application study of time-temperature correlation methods on test data of metal seals N2 - Reliable experimental data and prediction models are required to evaluate the behavior of components and materials over long periods of time. One method is based on the time-temperature equivalence principle, according to which a state or material property occurs or can be achieved equivalently at different time-temperature combinations. Higher temperatures generally shorten the duration and vice versa. Based on this approach, the long-term behavior of metal seals, as used in storage containers for spent nuclear fuels and high-level radioactive waste, has been studied at BAM and other institutions around the world for several years. However, such tests are often not planned as a preliminary point regarding the basic conditions of time-temperature related models. Gaps are then sometimes identified during the evaluation, for example because certain temperature values are missing, or the measurement intervals were not selected appropriately. This study evaluates exemplarily the status of the test data of metal seals at the BAM regarding the applicability of existing time-temperature correlation methods and corresponding models. Based on the existing database, the aim is to show which method and model are more likely to be applicable and which additional tests might be necessary to obtain a more suitable database. The tests so far have provided important findings for the planning and adaptation of possible further tests and for suitable model developments. Identified gaps in the data basis led to further development of the methods. In the present work, a time-temperature correlation was determined based on a time-temperature parameter from GRAHAM and WALLES for a selected data range. T2 - Pressure Vessels & Piping Conference PVP2025 CY - Montreal, Canada DA - 20.07.2025 KW - Time-temperature equivalence KW - Metal seals, KW - Time-temperature superposition KW - Time-temperature parameters PY - 2025 VL - 2025 SP - 1 EP - 4 PB - ASME CY - USA AN - OPUS4-63789 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz T1 - Vibrations of multi-span structures like floors, rail and road bridges N2 - Resonances of rail bridges due to the passage of trains have been mainly investigated for sin-gle-span bridges. When multi-span bridges are to be considered, it is of interest if stronger resonance amplifications must be taken into account. Measurements of several multi-span structures have been evaluated for natural frequencies and mode shapes. An integral rail bridge with three different spans shows a separated local resonance of the longest main span and clearly higher natural frequencies of the shorter side spans. A two-span continuous beam on the test area of the Federal Institute of Material Research and Testing showed a regular pattern of natural frequencies where always a pair of frequencies is found with a certain fre-quency ratio. The corresponding mode shapes are the out-of-phase and in-phase combinations of the first, second, third … bending mode. A seven-span road bridge has been monitored for one of the almost equally long spans. Similar mode shapes have been observed for different, clearly separated natural frequencies. Three modal analyses measurement campaigns have been performed on the whole bridge. The combined mode shapes of the seven spans have been clearly identified where different combinations of spans are dominating in the different mode shapes. Equal weakly coupled spans have been analysed for a large wooden floor in a castle. A cluster of natural frequencies has been observed and a special method to extract the mode shapes has been developed and tested. The consequences of multi-span bridges for rail traffic will be discussed. If n simply supported bridge spans have no coupling, n equal modes with amplitude A/n exist and their superposition would yield the same resonance as for a single bridge. Real simply supported bridges have always a weak coupling due to the track or the common piers. Therefore, the natural frequencies differ a little and they cannot be in reso-nance at the same time for the same train passage so that the resonance amplification cannot be as strong as for the single bridge. This rule holds also for the average amplitude of the time history of the bridge passage which is an adequate quantity to judge for the bridge behaviour. The maximum amplitude of the time histories of different bridge points are quite random and could exceed the values of a single bridge. The meaning of such criteria is questioned and fre-quency domain analyses are suggested for a clearer bridge analysis and understanding. T2 - DinEst 2024 Third Conference on Structural Dynamics CY - Seville, Spain DA - 12.09.2024 KW - Rail bridge PY - 2024 SP - 41 EP - 59 PB - Escuela Tecnica Superior de Ingenieria CY - Sevilla AN - OPUS4-61238 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz T1 - Die Minderung von Bahnerschütterungen – Messergebnisse aus Österreich, Deutschland und der Schweiz N2 - Die Minderung von Bahnerschütterungen neben Eisenbahnstrecken ist an vielen Stellen gemessen worden. Dabei ist neben der hochfrequenten Wirkung von elastischen Gleiselementen wie Schienenlager, Schwellensohlen und Unterschottermatten auch oft eine tieffrequente Minderung beobachtet worden. Diese tieffrequente Minderung wird interpretiert und mit der weiteren Lastverteilung der statischen Last erklärt. T2 - 3. Wiener Dynamik Tage CY - Vienna, Austria DA - 25.07.2024 KW - Bahnerschütterungen KW - Minderung KW - Messungen KW - Schwellensohlen KW - Unterschottermatten KW - Gleistrog PY - 2024 SP - 1 EP - 13 AN - OPUS4-61244 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz T1 - Prediction of ground vibrations from rail tunnels –finite-element, boundary-element and wavenumber calculations N2 - The prediction of ground and building vibrations has been established for surface lines and has now been extended to tunnel lines. The wave propagation in homogeneous or layered soils (the transmission) is calculated by an integration in wavenumber domain. The wave amplitudes at different distances and for different frequencies will be analysed for the following situations. 1. The horizontal propagation from a surface point to a surface point constitutes the basic rules. 2. The horizontal propagation from a source point at depth to a receiver point at depth which is related to a building with a deep basement or on a pile foundation. 3. The propagation from depth to the surface, which is the normal case for free-field measurements, has some different characteristics, for example a weaker attenuation with the horizontal distance from the source, which can be approximated by the full-space solution and the reflection rules for incident waves. The emission from a tunnel structure has been calculated by a finite-element model of the tunnel combined with a boundary-element model of the soil giving the reduction compared to a point-load excitation. The immission has been analysed by finite-element models of tunnel-soil-building systems for examples of research and consultancy work. Measurement results from a high-speed and a metro line confirm some of the established rules. Figure T2 - Int. Conf. RASD, Recent Advance in Structural Dynamics CY - Southampton, GB DA - 01.07.2024 KW - Ground vibration KW - Tunnel line KW - Wave propagation KW - Wavenumber method KW - Building vibration KW - Thin layer method PY - 2024 SP - 1 EP - 12 CY - Southampton AN - OPUS4-61266 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Auersch, Lutz T1 - Prognosemethoden für die Erschütterungsübertragung in Gebäude N2 - Es wurde ein Prognosemodell für die Bauwerksschwingungen entwickelt. Es besteht aus einer Gesamtbauwerkswand, die alle Wände und Stützen eines Bauwerks repräsentiert, und aus den Decken in den einzelnen Stockwerken. Das Modell wird stockwerkweise mit Übertragungsmatrizen berechnet. Hinsichtlich der Decken besteht im Programm die Möglichkeit, die Deckeneigenfrequenz aus den Abmessungen und den Auflagerbedingungen berechnen zu lassen. Die Decken werden dann im Rechenprogramm als Modalmodelle realisiert und an den Deckenauflagern in die Übertragungsmatrizenkette eingebaut. Aus diesem Komplexmodell des Gebäudes wurde entsprechend den Messerfahrungen ein praxisnäheres Standardmodell abgeleitet. Dazu werden die Wandamplituden aller Stockwerke gemittelt und bei den Decken wird eine gewisse Bandbreite der vorhandenen Deckeneigenfrequenzen unterstellt. Entsprechend der hohen Bedeutung, den experimentelle Ergebnisse für die Prognose der Erschütterungsimmission haben, wurden sehr viele in der BAM vorhandene Messdaten erneut ausgewertet und darüber hinaus neue Gebäudemessungen durchgeführt. Die Messergebnisse wurden bei der Definition des Standardmodells herangezogen. Außerdem wurde die Auswahl der Fundamentparameter mit den Messerfahrungen abgeglichen. Schließlich geben die Messdaten von etwa 80 Decken wichtige Hinweise auf die richtige Wahl der Deckenparameter Eigenfrequenz und Dämpfung. Eine Parameterstudie gibt Auskunft über die praktisch vorkommende Bandbreite der einzelnen Parameter und deren Auswirkung auf die Bauwerksamplituden. Die wichtigsten Parameter sind die Bodensteifigkeit und die Deckeneigenfrequenz, die die Abminderung der Gesamtbauwerksamplituden einerseits und die Amplitudenverstärkungen in der Deckenresonanzen andererseits bestimmen. Für diese beiden Parameter ergaben die Untersuchungen wesentliche Hinweise: Für die Gebäudegründung sind die weicheren oberen Bodenschichten maßgeblich, und die Deckeneigenfrequenzen lassen sich in erster Näherung gut durch eine allseitig gelenkige Lagerung abbilden. Mit den theoretischen und experimentellen Arbeiten konnte somit ein praxisgerechter Immissionsteil für die Erschütterungsprognose erstellt werden. KW - Immissionsprognose KW - Bauwerk-Boden-Wechselwirkung KW - Deckenschwingungen KW - Decke-Wand-Boden-Modell KW - Übertragungsmatrizen PY - 2006 SP - 1 EP - 87 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) AN - OPUS4-56223 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Auersch, Lutz T1 - Prognosemethoden für die Erschütterungsausbreitung im Boden N2 - In diesem Bericht werden die Berechnungsmethoden für die Transmission der Erschütterungen dargelegt. Da es sich um die Wellenausbreitung im Boden handelt, sind drei große Abschnitte dem Einfluss und den Berechnungsmöglichkeiten verschiedener homogener und geschichteter Böden gewidmet. Dabei kommt ein exaktes aufwändiges Rechenverfahren und daraus abgeleitete einfachere Näherungsverfahren zum Einsatz. Zum Bodeneinfluss wurden verschiedene homogene und geschichtete Böden exakt berechnet. Daraus wird ein Näherungsverfahren abgeleitet, dass auf der Dispersionsbeziehung v(f) beruht. Die Dispersion einiger Fälle wird exakt berechnet und ein Näherungsverfahren gefunden, mit dem man aus dem Tiefenprofil v(z) die Dispersion v(f) ermitteln kann. Mitden Näherungsverfahren werden die Wellenfelder der verschiedenen Böden nachgerechnet. Es ergeben sich sehr gute Übereinstimmungen mit den exakten Ergebnissen. Die Zuganregung wird in erster Linie mit ortsfesten dynamischen Achslasten erfasst. Mit der Lastverteilung über die gesamte Zuglänge ergibt sich eine deutlich andere, nämlich schwächere Abnahmegesetzmäßigkeit als für die elementare Punktlast. Für die Prognose von Schienenverkehrserschütterungen wurden verschiedene Verfahren vorgestellt, die die theoretischen Methoden zur Wellenausbreitung im Boden auf der experimentellen Seite ergänzen. Dies beginnt bei der notwendigen Ermittlung der Bodenkennwerte für den Prognoseort, das führt weiter zur sehr hilfreichen Bestimmung der Übertragungsfunktion am Prognoseort, und schließlich zur kritischen Verwendung von gemessenen Spektren als Emissionsgröße. Die verschiedenen Verfahren werden anhand der Messungen der ICE 3-und Thalys-Versuchsfahrten bei Gardelegen vorgeführt. Die wichtigsten Aussagen dieser Untersuchung sind: – Die Ergebnisse der Schwinger- und Impulsmessungen, die Bodenkennwerte und die Übertragungsfunktionen, Theorie und Messungen stimmen alle sehr gut miteinander überein. – Es sind gute Prognosen der Schienenverkehrserschütterungen sowohl mit den theoretischen als auch den experimentellen Übertragungsfunktionen möglich (s. Bild 39 im Vergleich zu Bild 40). – Die Verwendung von gemessenen Schienenverkehrserschütterungen als Emissionsspektrum wird ermöglicht. Sie ist aber an die Kenntnis der Bodenkennwerte am Messort gekoppelt. Mit den Bodenkennwerten am Messort können dann bodenunabhängige Lastspektren als Emissionsgröße berechnet werden. Damit steht eine Vielfalt von theoretischen und messtechnischen Varianten für die Prognose der Erschütterungsausbreitung im Boden zur Verfügung. KW - Geschichter Boden KW - Wellengeschwindigkeit KW - Übertragungsfunktion KW - Wellenzahlmethode KW - Approximationsverfahren KW - Bodensteifigkeit KW - Bodendämpfung PY - 2006 SP - 1 EP - 83 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) AN - OPUS4-56222 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Gerstberger, Ulf T1 - Prognosemethoden für die Emission von Bahnerschütterungen N2 - Die Emission von Erschütterungen wird durch ein physikalisches Modell der Fahrzeug-Fahrweg-Wechselwirkung unter Annahme eines stationären Zustands im Frequenzbereich berechnet. Dazu kommen analytische oder einfache numerische Formulierungen für Modelle des Fahrzeugs und des Gleises zum Einsatz mit deren Hilfe die Gesamtkraft auf den Boden unter dem Gleis infolge einer Achse prognostiziert wird. Das Gleis wird durch Systeme von kontinuierlich gebetteten schubstarrer Balken beschrieben, wobei sich die Bettung ggf. aus der „Verschmierung“ der diskreten Lagerung der Schiene über den Schwellenabstand ergibt. Die Bettung der Schiene des Schottergleises wird aus einem detaillierten Modell des Schienenstützpunkts im Frequenzbereich hergeleitet und kann folgende Komponenten enthalten: - Zwischenlage, - Schwelle, - Schwellenbesohlung, - Schotter, - Unterschottermatte. Für die Systeme der Festen Fahrbahn oder des Schottergleises im Tunnel kann unterhalb des gebetteten Balkens der Schiene ein zusätzlicher gebetteter Balken der Fahrbahn- oder Tunnelplatte angeordnet werden kann. Für Masse-Feder-System kann außerdem noch ein dritter Balken angeordnet werden. Das Fahrzeug wird mindestens durch die unabgefederte, starre Masse des Radsatzes beschrieben und kann durch Reihenschaltungen von weiteren Massen sowie Federn und Dämpfern erweitert werden, wobei folgende Komponenten enthalten sein können: - Wagenkastenmasse und Primärstufe, - Drehgestell und Sekundärstufe, - Motor- und Getriebemasse und deren Federstufe. Die Anregung des Schwingungssystems aus Fahrzeug und Gleis erfolgt durch eine im Kontakt von Rad und Schiene wirkenden Wegstörung, welche sich im Allgemeinen aus vertikalem Gleislagefehler, Schienen- und Radrauhigkeit, Radunrundheiten und der Parametererregung infolge der Schwellenüberrollung zusammensetzt. Auch wenn Zwischenergebnisse der Berechnung als Schmalbandspektrum vorhanden sind, erfolgt die Ausgabe der Emissionsgröße „Kraft auf den Untergrund“ als Terzspektrum und dient als Eingangsgröße für die Prognose der Transmission von Erschütterungen über den Boden oder zur Berechnung von Einfügedämmungen. KW - Emissionsprognose KW - Fahrwegmodell KW - Fahrzeugmodell KW - Bodenfedern KW - Fahrzeug-Fahrweg-Boden-Wechselwirkung KW - Störanregung KW - Terzspektren PY - 2006 SP - 1 EP - 63 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) AN - OPUS4-56224 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz T1 - Frequenz- und bodenabhängige Prognose und Minderung von Bahnerschütterungen N2 - Die Prognose und Minderung von Bahnerschütterungen haben eine lange Tradition in der Bundesanstalt für Materialforschung und -prüfung. Im Jahr 2006 wurde eine Prognose-Software fertiggestellt, die viele Forschungs- und Messergebnisse zusammenfasst. Sie umfasst die Teilbereiche Emission (die Anregung durch die Fahrzeug-Fahrweg-Untergrund-Wechselwirkung), die Transmission (die Ausbreitung durch den Boden) und die Immission (die Übertragung vom Freifeld in ein Gebäude). Die Prognose geschieht in allen Teilen mit einfachen Formeln, die veröffentlicht sind und zur Anwendung für Jedermann zur Verfügung stehen. Es werden Beispiele zur Emission und zur Transmission gezeigt. Im Bereich Transmissionsprognose werden zu den Anregungskräften (aus dem Emissionsteil) die Bodenerschütterungen als Schwinggeschwindigkeitsterzspektren berechnet. Das Ergebnis hängt stark von der Bodensteifigkeit, -dämpfung und -schichtung ab. Dies wurde später mit einer Messkampagne in der Schweiz an 10 Messorten bestätigt. Die Berechnung erfolgt näherungsweise für einen geschichteten Boden mit einer frequenzabhängigen Wellengeschwindigkeit (Dispersion) oder einem tiefenabhängigen Wellengeschwindigkeitsprofil. Die Anregungskräfte werden im Prognosebereich Emission mit einem 2-dimensionalen Gleismodell berechnet. 1-dimensionale Modelle liefern meist falsche Ergebnisse und 3-dimensionale Modelle (zum Beispiel mit der kombinierten Finite-Element-Randelement-Methode) sind für eine Erschütterungs¬prognose sicherlich zu aufwändig. Das 2-dimensionale Modell wurde an 3-dimensionale Ergebnisse so angepasst, dass die Ergebnisse für viele Gleise und Böden annähernd zutreffen. Auch Minderungs¬maßnahmen am Gleis können mit diesem Modell sehr gut berechnet werden. Die Prognoseverfahren wurden in den folgenden Jahren weiter verfeinert. Es wurde die quasi-statische Anregung durch die bewegten statischen Zuglasten mit einer Näherungsformel ergänzt, so dass auch das tieffrequente Nahfeld realistisch erfasst werden kann. Mit der Berücksichtigung der Achsfolge (insbesondere zwischen den Achsen im Drehgestell) ergeben sich zwei typische Minima in den Erschütterungsspektren, die oft auch in den Messungen beobachtet werden. Der Amplitudenanteil zwischen diesen beiden Minima ist oft stärker angehoben, so dass hier eine zusätzliche Erschütterungsanregung vermutet wird. Dieser Anteil kann rein empirisch prognostiziert werden, so wie das in den englischen Prognosen (zuletzt für das Highspeed2-Projekt) enthalten ist. Die Begründung dieses Anteils ist allerdings nicht die Achsfolge, sondern die Zerstreuung der statischen Achslastimpulse durch einen unregelmäßigen Gleisuntergrund und Boden. Die messtechnische Ermittlung eines Minderungseffektes ist komplizierter als allgemein angenommen. Es reicht nicht aus, jeweils an einem Messpunkt in der Nähe eines Gleises mit und ohne Minderungsmaßnahme die Erschütterungen zu messen und aus dem Verhältnis der Amplituden (beziehungsweise aus der Differenz der Pegel) „die Einfügedämmung“ zu ermitteln. Es wird an Beispielen gezeigt, wie man hier sinnvoller vorgehen kann. 1. Zunächst ist es wichtig, nicht nur die Einfügedämmung sondern auch die Originalspektren mit und ohne Minderung zu dokumentieren und zu veröffentlichen, damit man kontrollieren kann, ob wesentliche Amplituden und Frequenzbereiche reduziert sind oder ob es sich um eher zufällige Minderungen oder Verstärkungen handelt. (Beispiel Unterschottermatte/Raron, Müller/SBB) 2. Der Messpunkt sollte nicht im Nahbereich des Gleises liegen, da ansonsten eine zu günstige, falsche Einfügedämmung bestimmt wird. (Beispiel Tunnel/ Leipzig/Breitsamter) 3. Um Zufälligkeiten zu vermeiden, sollte man an mehr als einem Punkt messen. (Beispiel Unterschotterplatte/Altheim/Auersch) 4. Man sollte eigentlich immer auch die Bodenkennwerte (Steifigkeit, Dämpfung, Amplituden-abnahme, Übertagungsfunktion) messen. Selbst bei nahegelegene Messquerschnitten kann man Überraschungen erleben. (Beispiel erste ICE-Messungen/bei Würzburg/Auersch) 5. Bei verschiedenen Bodenkennwerten kann man eine Korrektur durchführen. (Beispiel Gleis-tröge/Mistler) Am besten bestimmt man ein äquivalentes Kraftspektrum zu jedem Messort und jedem Messzug (Beispiel Feste Fahrbahn/Gardelegen/Auersch) 6. Prinzipiell gibt es nicht die Einfügedämmung einer Maßnahme. Die Einfügedämmung ist immer boden- und referenzsystemabhängig. Die „beste“ Einfügungsdämmung erhält man mit einem steifen Untergrund (Beispiel Unterschottermatte/Tunnel/München Gasteig/Wettschureck) Das heißt aber nicht, dass die Maßnahme durch einen künstlich versteiften Untergrund besser wird (Beispiel Unterschottermatten/RRT2006/Auersch) Es werden Messbeispiele gezeigt, die alle neben einer hochfrequenten dynamischen Minderung auch eine mittelfrequente quasi-statische Minderung aufweisen. Dabei wird der mittelfrequente Zerstreuanteil der statischen Achslastimpulse durch die breitere Lastverteilung und damit die Impulsdehnung der Achslastimpulse reduziert. Diese Impulsdehnung lässt sich mit dem 2-dimensionalen Gleismodell berechnen. Die Minderungswirkung hängt aber wiederum vom Referenzsystem und dessen unregelmäßiger Steifigkeitsverteilung ab. Je unregelmäßiger der Boden und Gleisuntergrund des Referenzsystems, desto stärker ist die Minderungswirkung. T2 - 24. Symposium für Baudynamik und Erschütterungsmessungen CY - Dübendorf, Sitzerland DA - 09.06.2023 KW - Bahnerschütterungen KW - Erschütterungsprognose KW - Erschütterungsminderung KW - Elastische Gleiselemente KW - Gleiströge KW - Zerstreute Achsimpulse PY - 2023 SP - 1 EP - 32 PB - Ziegler Consultants CY - Zürich AN - OPUS4-57953 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz T1 - Soil-foundation-structure problems related to train induced vibrations - the kinematic interaction of tunnel excited pile foundations and the inertial interaction of high rise buildings N2 - The soil-foundation-structure interaction is always important when building vibrations due to train passages have to be considered. The frequency range for train vibrations is up to 100 Hz. Normally, soft surface soils are crucial so that the wavelength can be much smaller than the foundation dimensions. Three topics are of interest for the prediction and the under-standing of building vibrations. 1. The „kinematic interaction“ or the „added foundation ef-fect“, which is calculated either by the combined boundary-element finite-element method or by the wavenumber domain method, results in a reduction of the free-field vibration. The stiff-ness of the foundation resists the wave deformation, plates and walls for horizontally propa-gating waves or piles for vertically incident waves. 2. The „inertial interaction“ or the „added building effect“ yields an amplification around the vertical building resonance, which may be a rigid mode on the compliant soil or a flexible mode for high-rise buildings, and a reduction at higher frequencies. This has been analysed by detailed finite element models of apartment and office buildings. 3. Base isolation is a method to further reduce building vibrations. It is important to know the soil-foundation impedance for the possible reduction, as well as the correct building impedance. A high-rise building cannot be considered as a rigid mass model. It has a frequency-dependent behaviour with longitudinal waves travelling from the founda-tion to the top of the building which include the effect of floor vibrations. Experiences from building projects in Vienna, Frankfort and Berlin will give some additional results for the ex-citation from tunnel lines, the kinematic response of pile foundations, and the inertial re-sponse of the flexible multi-storey buildings. T2 - COMPDYN 2023 CY - Athen, Greece DA - 12.06.2023 KW - Kinematic Interaction KW - Inertial Interaction KW - Surface Foundation KW - Pile Foundation KW - High-Rise Building PY - 2023 SP - 1 EP - 14 PB - NTUA CY - Athens AN - OPUS4-57959 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz T1 - Some resonance effects of non-typical trains and railway bridges investigated by a frequency-domain method N2 - The resonances of railway bridges have often been analysed for short bridges under periodical high-speed trains, for simply supported one-span bridges, for the fundamental bridge mode, and by time-domain analyses. Many time-consuming calculations have been performed to establish simplified rules for standards. In this contribution, the passage of different (existing, new and hypothetic) trains over different bridges will be analysed in frequency domain by using three separated spectra with the purpose to get a better physical insight in the phenomena. At first, the excitation spectrum of the modal forces is built by the mode shape and the passage time of the train over the bridge. The second spectrum is the frequency response function of the bridge which include the modal frequency, damping and mass. The third part is the spectrum of the axle sequence of an arbitrary train which is not limited to periodical or specific (conventional, articulated, regular or standard) trains and which does not include any bridge parameters. The final solution in frequency domain is obtained as the product of these three complex, strongly varying spectra for the dominating bridge mode or in general as the sum of these products over all relevant bridge modes. The time domain solution is obtained via the inverse Fourier transform, and the resulting time histories have been successfully compared with some measurement results. The method is applied to the vertical and torsional modes of a mid-long 1-span bridge on elastomeric bearings under standard train speeds, and to a long multi-span integral bridge under long periodical freight trains. Different resonance and cancellation effects have been found for systematically varied train speeds according to the axle sequence of the whole train which is dominated by the two locomotives in that case. To be more specific, the first torsional mode of the mid-span bridge is excited for a train speed of 100 km/h whereas the second bending mode is excited for a train speed of 160 km/h. In both cases, the other mode is suppressed by the minima of the axle-distance spectra. In addition, the case of the German high-speed train ICE4 and the very high-speed hyperloop case will be discussed briefly. In general, it is shown that resonance effects are also worth to be studied for freight and passenger trains with lower speeds. T2 - XII International Conference on Structural Dynamics CY - Delft, The Netherlands DA - 03.07.2023 KW - Railway bridge KW - Transfer function KW - Modal force spectrum KW - Axle-sequence spectrum KW - Freight train KW - Passenger train KW - High-speed train KW - 2-span bridge KW - Long-span bridge PY - 2023 SP - 1 EP - 10 PB - TU Delft CY - Delft AN - OPUS4-57961 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz T1 - Train-induced ground vibrations - the emission and transmission from tunnel and surface lines N2 - Train-induced ground vibrations are quite different for tunnel and surface lines. The excitation of the track and ground vibration by the vehicle-track-soil interaction maybe influenced by the stiffer track support of the tunnel invert. The excited waves are propagating on a different path compared to the surface line. The wave propagation in the interior of the soil is calculated by a wavenumber integral in a similar way as the propagation along the surface and a general reduction of < 0.5 has been found. An additional reduction has been found because of the missing Rayleigh wave. The different excitation of tunnel lines is analysed theoretically by the combined finite-element boundary-element method and some results about the influencing tunnel and soil parameters will be shown. Measurements have been made at the Mühlberg-Tunnel in Germany. The vibrations of the train, the track and the soil have been measured simultaneously at the tunnel and a nearby surface line. Spectra will be shown for different train speeds between 60 and 160 km/h. A clear reduction effect for the tunnel line compared to the surface line has been observed in a specific (train-speed-dependent) frequency range. This agrees well with the observations of other research institutes. The mid-frequency tunnel-surface reduction seems to be a consequence of the stiffer track structure which leads to a wider distribution of the axle loads. Therefore, the axle impulses due to the train passage are longer and have a lower frequency content. This will have an effect on the ground vibrations at some distance which are present in case of an irregular transmission path through a ballast and soil with varying stiffness. A similar reduction effect can also be found for other track forms where the axle impulses are distributed on a longer track segment, for example slab tracks, tracks with under ballast plates, under ballast mats or under sleeper pads. T2 - 29th International Congress on Sound and Vibration CY - Prague, Czech Republic DA - 09.07.2023 KW - Ground vibration KW - Railway tunnel KW - Layered soil KW - Surface-tunnel reduction KW - Measurements PY - 2023 SP - 1 EP - 8 PB - IIAV CY - Auburn, USA AN - OPUS4-57962 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koenen, Heinrich A1 - Ide, Karl-Heinz T1 - Neuere Prüfmethoden für explosive Stoffe T2 - 31. Congrès international de chimie industrielle CY - Liege, Belgien DA - 07.09.1958 PY - 1959 VL - 2 SP - 181 EP - 186 CY - Bruxelles AN - OPUS4-10042 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lu, Xin A1 - Schukar, Marcus A1 - Großwig, S. A1 - Weber, U. A1 - Krebber, Katerina T1 - Monitoring acoustic events in boreholes using wavelengthscanning coherent optical time domain reflectometry in multimode fiber N2 - A distributed acoustic sensor (DAS) based on wavelength-scanning coherent optical time domain reflectometer (WS-COTDR) is tested in an underground gas storage based on a multimode fiber for the first time to the best of our knowledge. The WS-COTDR acquires the reflection spectrum by scanning the wavelength of the laser and uses the spectra to calibrate strain. It overcomes the fading problem which is common for all DAS systems, and possesses the advantage of simple configuration and low-cost. The working principle of the system is well explained and the measurement results are presented. Various artificial and natural acoustic events have been successfully detected by the WS-COTDR. Such a sensor demonstrates several advantages over the traditional DAS systems, so it is supposed to be widely used in the oil and gas industry. T2 - EAGE GeoTech 2021 Second EAGE Workshop on Distributed Fibre Optic Sensing CY - Online meeting DA - 01.03.2021 KW - Leakage detection KW - Distributed acoustic sensing KW - Distributed fiber optic sensing PY - 2021 DO - https://doi.org/10.3997/2214-4609.202131010 SP - Paper 10, 1 PB - European Association of Geoscientists & Engineers CY - Houten, Niederlande AN - OPUS4-52248 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krebber, Katerina A1 - Weege, S. A1 - Großwig, S. A1 - Obermöller, M. A1 - Perk, M. A1 - Lu, Xin A1 - Schukar, Marcus A1 - Weber, U. A1 - Pfeiffer, T. A1 - Rembe, M. T1 - Kombinierte faseroptische Messungen in Bohrlöchern helfen bei der Detektion von Kleinstleckagen N2 - Seit November 2019 läuft ein breit angelegtes und vom BMWi gefördertes ZIM-Kooperationsprojekt zwischen der Bundesanstalt für Materialforschung und -prüfung (BAM), der IAB'Weimar gGmbH, der GKSO GmbH & Co. Projekt KG, der DEEP.KBB GmbH sowie der Rembe Consulting PartG mbB. Ziel des Forschungsvorhabens sind sowohl die Lokalisierung als auch die Quantifizierung insbesondere sehr kleiner Leckagen in einer Bohrlochverrohrung durch die Nutzung faseroptischer Messtechnik. Durch Messdatenkopplung und den Wegfall bewegungsbedingter Nachteile einer Messsonde werden wesentlich präzisere Ergebnisse zur Bewertung der Bohrlochintegrität als üblich erwartet. T2 - DGMK/ÖGEW-Frühjahrstagung 2020 CY - Meeting was canceled DA - 15.04.2020 KW - Wasserstoffspeicher KW - Kavernenspeicher KW - Verteilte faseroptische akustische Sensorik PY - 2020 VL - 6 SP - 43 EP - 43 PB - DVV Media Group CY - Hamburg AN - OPUS4-52233 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF ED - John, Sebastian ED - Mair, Georg W. ED - Schoppa, André ED - Szczepaniak, Mariusz T1 - Erfassung und Bewertung von bauteilspezifischen Einflussfaktoren bei einer experimentellen Modalanalyse an Composite-Druckbehältern N2 - Auf Grund ihres Gewichtsvorteils sind Faserverbundwerkstoffe beim Bau von Hochdruckbehältern die dominierenden Werkstoffe. Mit dem zunehmenden Optimierungsdruck, Materialkosten und Gewicht einzusparen, nimmt das Lastniveau zu, weshalb auch die Bedeutung der Degradationsprozesse steigt. An der Bundesanstalt für Materialforschung und –prüfung (BAM) wird das Alterungsverhalten von Composite-Atemluftflaschen untersucht, um künftig genauere Aussagen zur Abschätzung der Lebensdauer und der damit einhergehenden Festlegung von Prüffristen geben zu können. Gegenstand der vorgestellten Untersuchungen sind Typ-III Druckbehälter, bestehend aus einem Aluminium-Liner und einer kohlefaserverstärkten Armierung. Dabei werden insbesondere Untersuchungen bezüglich der im Metall vorherrschenden Druckeigenspannungen betrachtet, welche zur Steigerung der Lastwechselfestigkeit fertigungsseitig induziert werden. Ziel ist es, mittels einer experimentellen Modalanalyse die inneren Spannungsverhältnisse zerstörungsfrei identifizieren und bewerten zu können. Auf Grund einer Vielzahl von Einflussfaktoren, wie beispielsweise alterungsbedingter Strukturveränderungen im Faserverbundmaterial oder Fertigungsabweichungen, ist jedoch die Einzelbewertung eines Prüfmusters sowie ein qualitativer Vergleich zwischen Behältern desselben Baumusters bisweilen nur schwer möglich. Durch die Vermessung einer Vielzahl von Testbehältern werden zunächst Maß und Umfang der auftretenden Abweichungen modaler Parameter erfasst. Mittels gezielter Modifikation einiger Messobjekte werden anschließend Abhängigkeiten identifiziert. Unterstützt werden die experimentellen Messungen durch die simultane Anwendung eines FE-Models, wobei simulative und experimentelle Ergebnisse verglichen sowie Einflüsse weiterer Parametervariationen numerisch erfasst und abgebildet werden können. T2 - DAGA 2018 CY - Munich, Germany DA - 19.03.2018 KW - Druckbehälter KW - Unsicherheiten KW - CODE AGE KW - Modalanalyse KW - Composite PY - 2018 VL - 44 SP - 91 EP - 94 CY - Berlin AN - OPUS4-45429 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - John, Sebastian A1 - Mair, Georg W. A1 - Schoppa, André A1 - Szczepaniak, Mariusz T1 - Monitoring of residual stresses in composite pressure vessels via modal analysis N2 - Within a current research project at the Federal Institute for Materials Testing and Research (BAM), the degradation process of composite pressure vessels is studied to be able to give more accurate lifetime predictions in future. The presented research is based on type III pressure vessels consisting of an aluminium tank which is fully wrapped with carbon fibre reinforced plastics. Focus is set on the analysis of residual stresses which are induced into the pressure vessel during manufacturing process in order to increase high cycle fatigue. However, with increasing lifetime residual stress conditions do change. To be able to measure and monitor stress conditions, the application of a non-destructive measurement method is aspired. In this paper, potential of an experimental modal analysis is worked out to capture and monitor aging and degradation effects in pressure vessels. With the presented method, information about changes in residual stress can be obtained via an analysis of the modal parameters. To realize an application, first, a finite element simulation is used to prove and evaluate potential capability and validity. In the following, a test bench is set up and successively optimized in its accuracy and efficiency. Sensitivity of the applied measurement technique is experimentally ascertained trough the measurement of several prestress modified pressure vessels. Finally, experimental results are interpreted and evaluated with the help of numerically gained findings. T2 - NOVEM 2018 CY - St. Eulalia, Ibiza, Spain DA - 07.05.2018 KW - Composite pressure vessel KW - Residual stress KW - Modal analysis PY - 2018 VL - 6 SP - Paper 175090, 1 EP - 9 AN - OPUS4-45220 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - John, Sebastian A1 - Eisermann, René A1 - Mair, Georg W. T1 - Application of an experimental modal analysis on composite pressure vessels for monitoring prestress conditions N2 - Due to high specific stiffness, fibre reinforced plastics are the dominant material group for the design of mobile pressure vessels. At the Federal Institute of Materials Research and Testing (BAM) aging process of composite pressure vessels is studied to be able to give more accurate lifetime predictions in future. Investigations are based on type III breathing air cylinders consisting of an aluminium tank which is fully wrapped with carbon fibre reinforced plastics. Goal is to detect changes of residual stresses over life time which directly affect fatigue strength. Within this paper an approach is presented to monitor residual stresses via an experimental modal analysis (EMA). First, the influence of changed stress conditions on modal parameters is analysed via a numerical study. Secondly, a test bench for an EMA is set up. To be able to analyse cylinders of different prestress condition, several specimens are prestress modified via high-temperature and high-pressure treatment. During modification processes, specimens are monitored via optical fibres to control prestress modifications. Through experimental measurements of the modified specimens via EMA changes in prestressing can be detected. Finally, validity and accuracy of the EMA is evaluated critically by comparing all numerically and experimentally obtained data. T2 - INTERNOISE 2018 CY - Chicago, Illinois, USA DA - 25.08.2018 KW - Modal analysis KW - Residual stress KW - Composite KW - Pressure vessel PY - 2018 SN - 978-0-7918-5142-5 SP - 6143, 1 EP - 10 AN - OPUS4-46329 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mair, Georg W. A1 - Hoffmann, Martin A1 - Scherer, Florian T1 - Type approval of composite gas cylinders - Probabilistic analysis of rc&s concerning minimum burst pressure T2 - EHEC 2014 - European hydrogen energy conference CY - Seville, Spain DA - 2014-03-12 KW - Composite cylinders KW - Cost optimisation KW - Hydraulic cycle testing KW - Residual strength KW - Safety KW - Scatter KW - Slow burst KW - Pressure rate KW - Sustained load PY - 2014 SP - HS2-6, 242-244 AN - OPUS4-30739 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - de Miguel, N. A1 - Mair, Georg W. A1 - Acosta, B. A1 - Szczepaniak, Mariusz A1 - Moretto, P. T1 - Hydraulic and pneumatic pressure cycle life test results on composite reinforced tanks for hydrogen storage N2 - Current standards governing the design, qualification and in-service inspection of carbon fibre composite cylinders do not facilitate to optimise cylinder design. The requirements have been adapted from standards for metallic cylinders and cannot easily quantify the degradation processes in composite materials. In this article, the results of hydraulic and hydrogen pressure cycle life tests performed on composite reinforced tanks with a metal liner (type 3) and with a high density polymer liner (type 4) are shown. Moreover, the degradation measured by means of residual strength of the tanks after the cycling tests have been compared. It has been found that the most critical aging for metal based composite cylinder is the gaseous cycling while type 4 designs seem to be more sensitive to hydraulic cycling at high temperature. T2 - ASME 2016 Pressure Vessels and Piping Conference CY - Vancouver, British Columbia, Canada DA - 17.07.2016 KW - Composite reinforced tanks KW - Compressed hydrogen storage KW - Design and qualification standards KW - Pressure cycle life tests KW - Safety factors PY - 2016 SN - 978-0-7918-5035-0 VL - 1A SP - 63568-1 EP - 63568-10 PB - ASME CY - Vancouver, British Columbia, Canada AN - OPUS4-36275 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Becker, Ben A1 - Mair, Georg W. T1 - Risks and safety level of composite cylinders N2 - The increasing amount of composite transport systems for hydrogen leads to new and therefore unknown potential hazards for general public. Due to lack of experience, risks of new technologies tend to be rated as higher than existing familiar applications. An approach for probabilistic safety assessment of technologies or products requires the definition of minimal acceptable reliability levels. This ensures that the probability of a critical failure with a certain consequence is limited to an acceptable risk. But what is the acceptable risk and which risk results from specific probabilities of occurrence and consequences? This is always a very complex question. The following example is based on a probabilistic approach for safety assessment of composite cylinders developed at the BAM (Federal Institute for Materials Research and Testing). T2 - WHEC 2016 CY - Saragossa, Spain DA - 13.06.2016 KW - Hydrogen composite cylinder risk consequence PY - 2016 VL - 2016 SP - 41 EP - 42 AN - OPUS4-36666 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mair, Georg W. T1 - Verhalten im Brandfall von Carbonfaser-Druckgefäßen T2 - 7. Gefahrgut-Technik-Tage (GTT) CY - Berlin, Deutschland DA - 2004-11-25 PY - 2004 VL - 7 SP - 61 EP - 70 PB - Storck CY - Hamburg AN - OPUS4-5076 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mair, Georg W. T1 - Druckführende Verpackungen - der Übergang von der Verpackung zum Druckgefäß T2 - 6. Gefahrgut-Technik-Tage CY - Berlin, Deutschland DA - 2003-01-01 PY - 2003 VL - 6 PB - Storck CY - Hamburg AN - OPUS4-5895 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz-Forberg, Bernd A1 - Mair, Georg W. T1 - Auswirkung von Yellow Paper auf internationale Regelwerke und Normen T2 - 3. Gefahrgut-Technik-Tage Berlin "Innovative Tanktechnik" CY - Berlin, Deutschland DA - 2000-11-09 PY - 2000 IS - Projekt-Nr. 0206-III-0445 SP - 5 EP - 11 PB - Storck-Akademie CY - Hamburg AN - OPUS4-6038 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völzke, Holger A1 - Mair, Georg W. A1 - Wiedemann, J. T1 - Gewichts- und kostengünstige Auslegung faserbewehrter Hochdruckbehälter T2 - 23. Internationale AVK-Tagung CY - Mainz, Deutschland DA - 1990-11-05 PY - 1990 IS - Report-Nr. MBB-Z--0325-90-PUB; OTN--030839 SP - B1-1-B1-11 PB - Zentrale Berichtsstelle, Technisch-wissenschaftliche Information, Messerschmitt-Bölkow-Blohm GmbH CY - München AN - OPUS4-6015 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mair, Georg W. T1 - Der Einfluss unterschiedlicher Klimazonen auf Betriebssicherheit und Lebensdauer von Behältern T2 - 9. Gefahrgut-Technik-Tage "Innovative Tanktechnik" CY - Berlin, Deutschland DA - 2006-11-23 KW - Klimadaten KW - Ermüdungsfestigkeit KW - Eigenspannungen KW - Versuchstechnik KW - Gasdruck KW - Regelwerksanforderungen PY - 2006 VL - 9 IS - Beitrag 12 SP - 1(?) EP - 10(?) PB - Bundesanstalt für Materialforschung und -prüfung CY - Berlin AN - OPUS4-14212 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bohse, Jürgen A1 - Mair, Georg W. T1 - Schädigungsanalyse von Composite-Druckbehältern mittels Schallemissionsprüfung N2 - Im Rahmen von nationalen und europäischen Forschungsvorhaben wurde die Schallemissionsprüfung (SEP) in den letzten Jahren an der BAM zur Prüfung und Zustandsbeurteilung von Composite-Druckbehältern eingesetzt und weiterentwi-ckelt. Das aktiv arbeitende SEP-Verfahren detektiert bereits frühe, erste Schädigungen mit geringer SE-Intensität, z.B. durch Zwischenfaserbruchversagen. Später einset-zende Faserbrüche oder Delaminationsvorgänge erzeugen sehr starke Schallemissi-onen. Im Vortrag werden anhand von Beispielen die unterschiedlichen Zielstellungen der SEP bei der Behälterprüfung dargestellt: - Design-Optimierung von Behälterstrukturen durch Analyse der Schädigungs- entwicklung bei Berstversuchen - Qualitätskontrolle von Composite-Druckbehältern beim Autofrettageprozess (Fertigung) oder bei der Erstdruckprüfung (Abnahmeprüfung) - Nachweis von Beschädigungen im Betrieb (Ermüdungsrisse, Impacts, Delami- nationen, Kerben etc.) durch eine Wiederkehrende Druckprüfung - Zustandsüberwachung (Structural Health Monitoring) zum Online-Nachweis von kritischen Ermüdungszuständen oder aktuellen Beschädigungen. Das Zukunftspotenzial des Schallemissionsverfahrens besteht vor allem in seinem Einsatz bei der Prüfung und Zustandsüberwachung von Composite-Hochdruck-behältern für die 700 bar-Wasserstofftechnologie aber auch für Faserverbundbau-teile in anderen sicherheitsrelevanten Anwendungen, wie Windkraftanlagen, Luft- und Raumfahrt. T2 - 15. Nationales Symposium SAMPE Deutschland e.V. CY - Berlin, Deutschland DA - 2009-02-18 KW - Schallemissionsprüfung KW - Schädigungsanalyse KW - Composite KW - Druckbehälter PY - 2009 IS - Kap. Messverfahren SP - 1 EP - 14 AN - OPUS4-19202 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Artinov, Antoni A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Transient Process Simulation of Heat Transfer in Laser Beam Welding with an Equivalent Heat Source N2 - This paper presents a multiphysics modelling framework developed for the prediction of the three-dimensional transient temperature field of the laser welding process. The numerical model consists of two studies. In the first study, a steady-state CFD process simulation of full-penetration keyhole laser beam welding was performed. Considering the effects of, thermo-capillary and natural convection, latent heat of fusion and temperature-dependent material properties up to evaporation temperature the local weld pool geometry and temperature field were obtained. These results were used in the second subsequent study as an equivalent volumetric heat source by the prediction of the transient thermal cycle during and after fusion welding. Here the energy input and the movement of the heat source were realized by a novel technique, making use of pointwise constraints and a moving mesh provided with helper lines and additional remeshing condition. The numerically calculated results were compared to experimentally observed weld pool shapes and time-temperature curves showing a very good agreement. T2 - COMSOL Conference 2017 CY - Rotterdam, Netherlands DA - 18.10.2017 KW - High power laser beam welding KW - Transient heat transfer KW - Equivalent volumetric heat source KW - Moving mesh KW - Pointwise constraints PY - 2017 SP - 1 EP - 7 CY - Rotterdam AN - OPUS4-42701 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meng, Xiangmeng A1 - Putra, Stephen Nugraha A1 - Bachmann, Marcel A1 - Artinov, Antoni A1 - Rethmeier, Michael T1 - The influence of the free surface reconstruction on the spatial laser energy distribution in high power laser beam welding modeling N2 - An accurate and efficient description of the spatial distribution of laser energy is a crucial factor for the modeling of laser material processing, e.g., laser welding, laser cutting, or laser-based additive manufacturing. In this study, a 3D heat transfer and fluid flow model coupled with the volume-of-fluid algorithm for free surface tracking is developed for the simulation of molten pool dynamics in high-power laser beam welding. The underlying laser-material interactions, i.e., the multiple reflections and Fresnel absorption, are considered by a ray-tracing method. Two strategies of free surface reconstruction used in the ray-tracing method are investigated: a typical piecewise linear interface calculation (PLIC)-based method and a novel localized Level-Set method. The PLIC-based method is discrete, resulting in non-continuous free surface reconstruction. In the localized Level-Set method, a continuous free surface is reconstructed, and thus the exact reflection points can be determined. The calculated spatial laser energy distribution and the corresponding molten pool dynamics from the two methods are analyzed and compared. The obtained numerical results are evaluated with experimental measurements to assure the validity of the proposed model. It is found that distinct patterns of the beam multiple reflections are obtained with the different free surface reconstructions, which shows significant influence not only on the molten pool behaviors but also on the localized keyhole dynamics. T2 - International Congress of Applications of Lasers & Electro-Optics 2022 CY - Orlando, FL, USA DA - 17.10.2022 KW - Laser beam welding KW - laser energy distribution KW - Weld pool dynamics KW - Ray-tracing PY - 2022 SP - 1 EP - 9 AN - OPUS4-56533 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Investigation of solidification cracking susceptibility of laser welded joints of austenitic stainless steels N2 - Laser welding is a widely established manufacturing process in many industry sectors. Solidification cracking represents one of the most inadequately solved problems in welding and has major economic implications. The avoidance of hot crack forms for most fusion welding processes poses a key challenge for an important range of metallic construction materials and affects not only the manufacturers of welding equipment and material manufacturers, but also a large number of customers using welding technologies, as well as welding technical standardization and research. Solidification cracking susceptibility was examined with the help of the Controlled Tensile Weldability Test (CTW) developed by Federal Institute for Materials Research and Testing (BAM), Berlin. The test is based on the fact that hot crack formation depends on a critical strain that emerges within a critical temperature range, the so called brittle temperature range (BTR). Using this test and defined investigation programme a centreline solidification crack was generated. By controlling the applied strain during the laser beam welding process, it was possible to determine the critical strain and strain rate that led to solidification cracking formation. The hot cracking susceptibility of the tested stainless steels was qualified and quantified. The results demonstrate that the crack length increases with increasing applied strain. Furthermore, the strain rate has a significant influence on the formation of the solidification crack. T2 - 3rd International conference in Africa and Asia CY - Luxor, Egypt DA - 02.11.2015 KW - Laser beam welding KW - Hot cracking KW - Solidification cracking KW - Hot cracking test PY - 2015 SP - A-29, 1 EP - A-29, 9 AN - OPUS4-36522 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gumenyuk, Andrey A1 - Gook, Sergej A1 - Rethmeier, Michael A1 - Kohn, H. T1 - Orbitalschweißen im Pipelinebau - Neue Möglichkeiten durch die Anwendung von Hochleistungslasern T2 - 8. Internationale Konferenz Strahltechnik CY - Halle/Saale, Deutschland DA - 2010-04-14 KW - Laser-MSG-Hybrid Schweißen KW - Orbitalschweißen KW - Hochleistungslaser PY - 2010 SP - 74 EP - 79 CY - Halle (Saale) AN - OPUS4-21225 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brauser, Stephan A1 - Pepke, Lutz-Alexander A1 - Weber, Gert A1 - Rethmeier, Michael A1 - Göklü, S. T1 - Einfluss der Schweißstromform auf die Schweißbereiche und die Festigkeit beim Widerstandpunktschweißen moderner Automobilwerkstoffe T2 - 21. DVS-Sondertagung "Widerstandsschweissen 2010" CY - Duisburg, Deutschland DA - 2010-05-05 KW - Widerstandschweißen KW - Schweißbereiche KW - Anlagenkonfiguration KW - Schwingfestigkeit PY - 2010 SP - 1 EP - 7(?) CY - Duisburg AN - OPUS4-21561 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schwenk, Christopher A1 - Rethmeier, Michael T1 - Simulation based approach for distortion analysis and optimisation of beam welded automotive parts T2 - VI. International conference "Beam technologies & laser application" CY - Saint Petersburg, Russia DA - 2009-09-23 KW - Numerical welding simulation KW - Distortion KW - Optimisation KW - Laser and electron beam welding KW - Automotive parts PY - 2009 SP - 1 EP - 9(?) CY - Saint Petersburg, Russia AN - OPUS4-20797 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Gert A1 - Rethmeier, Michael A1 - Brauser, Stephan T1 - Extended weldability lobes in resistance spot welding of advanced high strength steels (AHSS) T2 - EUROJOIN 7 - 7th European congress on joining technology CY - Venice, Italy DA - 2009-05-21 KW - Resistance welding KW - High strength steels PY - 2009 IS - Technical Session 2 SP - 1 EP - 15 AN - OPUS4-20524 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quiroz Penaranda, Vanessa A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Laser beam welding of austenitic manganese-alloyed stainless steels T2 - INOX 2010 - 10th Brazilian stainless steel conference CY - Rio de Janeiro, Brazil DA - 2010-09-20 PY - 2010 SP - 254 EP - 269 AN - OPUS4-22165 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quiroz Penaranda, Vanessa A1 - Gebhardt, Moritz Oliver A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Hot crack susceptibility of laser and laser-hybrid welded joints T2 - VI. International conference "Beam technologies & laser application" CY - Saint Petersburg, Russia DA - 2009-09-23 PY - 2009 SP - 127 EP - 136 CY - Saint Petersburg, Russia AN - OPUS4-20941 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Perret, William A1 - Thater, R. A1 - Alber, U. A1 - Schwenk, Christopher A1 - Rethmeier, Michael T1 - Case study for welding simulation in the automotive industry T2 - INPRO - Intermediate meeting - IIW-Select committee "automotive and road transport" DA - 2010-04-21 KW - Welding simulation KW - Temperature field KW - Distortion KW - Automotive industry KW - Experimental validation PY - 2010 IS - IIW-Doc. No. SC-Auto-37-10 SP - 1 EP - 13 AN - OPUS4-22541 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thater, Raphael A1 - Perret, William A1 - Schwenk, Christopher A1 - Alber, U. A1 - Rethmeier, Michael T1 - Industrial application of welding temperature field and distortion visualization using FEA N2 - The non-uniform heat input during the welding process leads to problematic permanent deformations of welded parts. The control of these welding distortions is, with the absence of the knowledge of the fundamental mechanisms responsible for these deformations, an extremely time and cost consuming iterative “trial-and-error” optimization process. The visualization of the involved physical phenomena, like temperature and distortions, .is an indispensable tool to clearly identify these mechanisms in order to adapt the welding parameters and clamping conditions target-oriented. Both experimental and virtual methods exist to obtain these physical data, however the possibilities to visualize them with experimental methods are laborious, expensive and limited in their application. Welding Simulation using finite element analysis (FEA) offers many benefits and has a great potential to reduce the experimental effort. Nevertheless, the industrial application of welding Simulation is not yet established widely because of reservations regarding the computation costs and the resulting accuracy for instance. In this paper, the results of a case study for a welding Simulation with an industrial background are presented. A welded assembly from the automotive industry has been investigated with numerical and experimental methods. A comparison between both methods demonstrates the Potentials of welding Simulation in terms of visualization. Furthermore, the numerical results reveal the possibilities of current resources. regarding calculation time and result accuracy of an industrial applied welding Simulation. T2 - VISUAL-JW 2010 - The international symposium on visualization in joining & welding science through advanced measurements and simulation CY - Osaka, Japan DA - 11.11.2010 KW - Numerical welding simulation KW - Temperature field KW - Distortion KW - Industrial application KW - Automotive assembly PY - 2010 VL - 1 IS - PT-31 SP - 245 EP - 246 AN - OPUS4-22721 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bachmann, Marcel A1 - Avilov, Vjaceslav A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Magnets improve quality of high-power laser beam welding N2 - High-power laser beam welding uses a localized heat source to achieve narrow deep welds and high welding rates. Engineers run into some difficulties because the use of a localized heat source often results in the distortion of metal components; spattering and the ejection of droplets from the weld pool results in underfills, undercuts, craters, blowholes, or blowouts. A stationary magnetic field is applied to the laser welding process to improve its quality and counteract effects such as spattering. BAM Federal Institute For Materials Research and Testing in Germany are working to improve the quality of high-power laser beam welding using COMSOL Multiphysics. To model and simulate the laser beam welding, heat transfer, fluid dynamics, and electromagnetics were coupled and solved. This allowed BAM to accurately model the process by including Marangoni effects, gravity, latent heats of fusion, and Lorentz forces. KW - Laser beam welding KW - Electromagnetic weld pool control KW - Marangoni effect PY - 2013 SP - 30 EP - 32 AN - OPUS4-28655 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quiroz Penaranda, Vanessa A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Laser beam weldability of austenitic and austenitic-ferritic high-manganese stainless steel sheets T2 - 63rd IIW Annual Assembly and International Conference CY - Istanbul, Turkey DA - 2010-07-12 KW - Manganese alloyed stainless steels KW - Laser beam welding KW - Weldability KW - Shielding gas KW - Weld metal KW - Corrosion resistance KW - Mechanical properties PY - 2010 IS - IIW Doc.-No. IV-1023-10 SP - 1 EP - 13 AN - OPUS4-22615 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Karkhin, Victor A1 - Pittner, Andreas A1 - Schwenk, Christopher A1 - Rethmeier, Michael ED - Halmoy, E. T1 - Simulation of the temperature field in laser beam welding by inverse technique N2 - This paper presents volume heat sources and the corresponding functional analytical Solutions for the transient temperature field. The considered energy distributions are normal, exponential and parabolic. The method follows the common approach in Computational Welding Mechanics (CWM) to account for the physics of the welding process and the resulting temperature field by phenomenological models for heat conduction. Therefore, the used heat source models are apparent heat sources that incorporate the real heat input as well as the fluid flow in the weld pool and the latent heat connected with phase transformations. The heat source models provide welding characteristics like thermal cycle and Fusion line in the cross section within short computational time. Consequently, inverse techniques on basis of optimisation algorithms enable the adaptation of the models to the experimental data efficiently. Furthermore, the direct evaluation of the energy distribution for the experimental fusion line in the cross section is demonstrated which enhances the numerical optimisation by reducing the number of unknown model Parameters and providing a reasonable initial guess within the model parameter space. The proposed temperature field models are validated with real laser beam welding experiments. T2 - 13th Conference on laser materials processing in the nordic countries CY - Trondheim, Norway DA - 27.06.2011 KW - Volume heat source KW - Inverse modelling KW - Functional analysis KW - Laser beam welding PY - 2011 SP - 223 EP - 234 AN - OPUS4-24165 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Shcheglov, Pavel A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael A1 - Uspensky, S.A. A1 - Petrovsky, V.N. T1 - Study of welding plume in high-power fiber laser welding T2 - LTWMP '11 - 5th International conference "Laser technologies in welding and materials processing" CY - Crimea, Ukraine DA - 2011-05-24 PY - 2011 SP - 142 EP - 147 AN - OPUS4-25473 LA - rus AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quiroz Penaranda, Vanessa A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Investigations on laser beam welding of high-manganese austenitic and austenitic-ferritic stainless steels N2 - Influence of the main laser welding parameters on process stability and resulting weld quality were investigated. Effects of weld edge preparation on the weld appearance and quality were considered. The obtained welded joints were subjected to radiographic tests for detection of internal imperfections. Metallurgical characterisation of the samples regarding the resulting phase composition and hardness was conducted. Tensile and potentiodynamic tests were performed to evaluate the mechanical and corrosion properties. The results provide an insight into the advantages and limitations of the laser welding process for joining high-manganese alloyed stainless steels. Conditions for the production of defect-free and corrosion-resistant welds having good mechanical properties could be determined. T2 - LTWMP '11 - 5th International conference "Laser technologies in welding and materials processing" CY - Crimea, Ukraine DA - 24.05.2011 PY - 2011 SP - 55 EP - 59 AN - OPUS4-25475 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Frei, Julian A1 - Rethmeier, Michael T1 - Influence of manufacturing conditions on the cracking susceptibility of AHSS during resistance spot welding N2 - The complex microstructure and the advanced mechanical properties of AHSS steel types lead to an increased susceptibility to weld cracking, especially during resistance spot welding under ‘rough’ manufacturing conditions. Various activities have been conducted in recent years at the Federal Institute for Materials Research and Testing (BAM) and the Fraunhofer IPK on this matter. Understandings about the safe spot weldability and the process of crack-forming itself were gained, and solutions for handling this issue given. The performed work includes investigations on the influence of initial gaps as well as restraint intensity. An experimental method for the determination of the general cracking susceptibility, i.e. a material ranking of AHSS in respective to current restraints was developed. Coupled mechanical and thermal simulations of the welding process show the present internal stress-strain-conditions and values responsible for the formation of cracks, deepening the understanding of the process. By using this easy to perform and material-independent method for the determination of the cracking susceptibility in resistance spot welded joints, small and medium sized companies can profit by rapidly evaluating the joinability of their handled material combinations as well as OEMs. T2 - Sheet Metal Welding Conference XVII CY - Livonia, Michigan, USA DA - 18.10.2016 KW - Welding under external loading KW - Cracking susceptibility of AHSS KW - Resistance spot welding KW - Initial gap PY - 2016 SP - Session 1-2, 1 EP - Session 1-2, 15 AN - OPUS4-38137 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Graf, B. A1 - Schuch, M. A1 - Petrat, T. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Combined laser additive manufacturing with powderbed and powder nozzle for turbine parts N2 - Metal additive manufacturing is often based on laser beam processes like Laser Metal Fusion (LMF) or Laser Metal Deposition (LMD). The LMF process is in particular suitable for very complex geometries. However build rate, part volume and material flexibility are limited in LMF. In contrast, LMD achieves higher deposition rates, less restricted part sizes and the possibility to change the material composition during the build-up process. On the other hand, due to the lower spatial precision of the material deposition process, the complexity of geometries is limited. Therefore, combined manufacturing with both LMF and LMD has the potential to utilize the respective advantages of both technologies. In this paper, combined additive manufacturing with LMF and LMD is described for Ti-6Al-4V and Inconel 718. First, lattice structures with different wall thickness and void sizes are built with LMF. The influence of LMD material deposition on these LMF-structures is examined regarding metallurgical impact and distortion. Cross-sections, x-ray computer tomography and 3D-scanning results are shown. For the titanium alloy specimen, oxygen and Nitrogen content in the deposited material are analysed to evaluate the LMD shielding gas atmosphere. The results are used to develop guidelines for a LMD build-up strategy on LMF substrates. With these findings, a gas turbine burner is manufactured as reality test for the combined approach. T2 - 6th International Conference on Additive Technologies iCAT 2016 CY - Nürnberg, Germany DA - 29.11.2016 KW - Ti-6Al-4V KW - Inconel 718 KW - Combined laser manufacturing PY - 2016 SN - 978-691-285-537-6 SP - 317 EP - 323 AN - OPUS4-38702 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neubert, S. A1 - Pittner, Andreas A1 - Rethmeier, Michael T1 - Numerical Sensitivity Analysis of TRIP-Parameter K on Weld Residual Stresses and Weld Distortion N2 - A combined experimental numerical approach is applied for a sensitivity analysis of the transformation induced plasticity (TRIP)-parameter K on welding residual stresses and welding distortion for the welding of the low-alloyed high-strength S960QOL with the high-alloyed hig-strength filler material CN13-4-IG. A thermo-mechanical FE model of a real GMA welding process was experimentally validated against termperature field, X-Ray stress measurments and optical distortion measurement. Within the sensititvity analysis K was varied and the influence on the calculated welding residual stresses and welding distortion is evaluated by performing corresponding FEA. The correct order of K magnitude is necessary in order to reproduce the residual stresses qualitatively and quantitatively. For the sufficient reproducing of the welding distortion the transformation induced plasticity can be neglected. T2 - 11th International Seminar - Numerical Analysis of Weldability CY - Graz, Austria DA - 27.09.2015 KW - TRIP PY - 2016 SN - 978-3-85125-490-7 SN - 2410-0544 SP - 361 EP - 383 PB - Verlag der Technischen Universität Graz CY - Graz AN - OPUS4-38904 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Rethmeier, Michael A1 - Suwala, H. A1 - Frei, J. T1 - Entwicklung eines Verfahrens zur Bestimmung der Rissanfälligkeit von hochfesten Stählen beim Widerstandspunktschweißen N2 - Die stetig zunehmenden Anforderungen hinsichtlich geringeren Kraftstoffverbrauchs, verminderter Schadstoffemission sowie der Erhöhung der passiven Sicherheit haben die Automobilindustrie vor Herausforderungen gestellt, denen nur durch einen konsequenten Einsatz moderner Stahlwerkstoffe zu begegnen ist. Die komplexe Gefügestruktur sowie die besonderen mechanischen Eigenschaften dieser Werkstoffe verursachen jedoch eine erhöhte Neigung zur Ausbildung von Rissen insbesondere bei Widerstandspunktschweißverbindungen.Insbesondere für kleine und mittelständische Unternehmen, die keine zeitaufwendigen und teuren Voruntersuchungen bezüglich der Rissanfälligkeit von Stählen während des Widerstandspunktschweißens durchführen können, ist zum Erhalt der Wettbewerbsfähigkeit die Kenntnis der Rissanfälligkeit einer von ihnen zu verarbeitenden Materialkombination von erheblicher Bedeutung. Durch eine einfach durchzuführende, werkstoffunabhängige Methode zur Bestimmung der Rissanfälligkeit beim Widerstandspunktschweißen, kann den KMUs die Möglichkeit zur schnellen und kostengünstigen Bewertung der Verarbeitungssicherheit zu verarbeitender Materialverbindungen bereitgestellt werden. Ziel des Forschungsvorhabens ist daher die Entwicklung einer einfachen und fertigungsnahen Methode zur Bestimmung der Rissanfälligkeit hochfester Stähle während des Widerstandspunkschweißens, die auf der gezielten, reproduzierbaren Erzeugung von Rissen basiert. Es wurde eine solche Prüfmethodik entwickelt, die auf einfach durchzuführenden experimentellen Versuchen basiert. Zu untersuchende Proben werden während des Schweißvorgangs mit einer Zugkraft belastet. Hierfür wird eine hydraulische Vorrichtung genutzt, die taillierte Flachzugproben mit definierter Kraft beaufschlagt. Infolge dessen stellt sich ein Spannungszustand ein, der die Rissbildung begünstigt. Somit können ausreichende Rissentstehungsraten erzielt werden, die eine vergleichende Beurteilung der resultierenden Risslängen zwischen den Werkstoffen zulassen. Die einfache, mobile Zugvorrichtung ermöglicht eine Nutzung der bestehenden Anlagentechnik. Durch eine Normierung der resultierenden Risslängen auf die Streckgrenze des Werkstoffs und die belastete Querschnittsfläche lassen sich ein Werkstoffranking beziehungsweise eine Klassifizierung der Rissanfälligkeit der untersuchten hochfesten Materialkombinationen erstellen. Auch zukünftig entwickelte Stahlwerkstoffe potentiell höherer Festigkeiten können untersucht werden. Weiterhin kann die entwickelte Methode als Grundlage für die Gewinnung von Basisdaten zur Untersuchung verschiedener Rissentstehungsarten während des Widerstandspunktschweißens eingesetzt werden. KW - Rissanfälligkeit PY - 2017 SN - 978-3-946885-09-2 VL - 921 SP - 1 EP - 78 PB - Verlag und Vertriebsgesellschaft mbH CY - Düsseldorf AN - OPUS4-39651 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Epple, Niklas A1 - Sanchez Trujillo, Camila A1 - Fontoura Barroso, Daniel A1 - Hau, Julia A1 - Niederleithinger, Ernst ED - Lienhart, Werner ED - Krüger, Markus T1 - Monitoring of Concrete Infrastructure with Active Ultrasound Coda Wave Interferometry N2 - Coda Wave Interferometry has been used in Geophysics to detect weak changes in scattering media. Past research in Structural Health Monitoring has shown that this methodology can be applied to concrete structures to detect material changes by calculation of relative velocity changes. Successive measurements with embedded ultrasonic transducers provide a repeatable signal for reliable long-term monitoring of concrete. To research the application in real-world structures, we have embedded ultrasonic transducers in a bridge in Ulm and a Metro station in Munich, Germany. This study gives an overview of the monitoring of these two structures. The results show the potential and challenges of the method. Data evaluation can be largely automated to gain insights into material changes and other influences on the structure, such as traffic-induced load and temperature variations. The experiments demonstrate the ease of installation, longevity of the sensor installation, and sensitivity of the measurement technique, but highlight problems with the application, especially if electromagnetic noise affects data quality. As no confirmed substantial damage was recorded during the monitoring period on both structures, we evaluate load tests to investigate the effect of static load on the structures and the coda monitoring results. The experiments show that the influence of load can be detected, even if the temperature influence is not removed from the data. This indicates that online damage detection with coda monitoring is possible, but further research on damage detection in real-world structures has to be conducted to confirm laboratory findings. T2 - 13th International Conference on Structural Health Monitoring of Intelligent Infrastructure CY - Graz, Austria DA - 01.09.2025 KW - Active Ultrasound Measurements KW - Coda Wave Monitoring KW - Embedded Transducers PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-640582 DO - https://doi.org/10.3217/978-3-99161-057-1-012 SP - 45 EP - 51 PB - Technische Universität Graz CY - Graz AN - OPUS4-64058 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Traub, Heike T1 - Erste praktische Erfahrungen mit einem ETV ICP OES-System T2 - Anwenderseminar über die direkte Analyse von Festproben mit simultaner ICP-OES / Analyse organischer und anorganischer Proben mit elektrothermischer Verdampfung (ETV) und Lichtbogen-Emission CY - Neu-Isenburg, Deutschland DA - 2002-09-23 PY - 2002 AN - OPUS4-1932 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niederleithinger, Ernst A1 - Kruschwitz, Sabine A1 - Behrens, Matthias A1 - Brink, Arne T1 - Multichannel Spectral Induced Polarization (SIP) - Application to Geotechnics and Construction Materials T2 - 10th European Meeting of Environmental and Engineering Geophysics (Near Surface 2004) CY - Utrecht, Niederlande DA - 2004-09-06 KW - SIP KW - Geotechnik KW - Geoelektrik KW - Baustoffe KW - Feuchtigkeit KW - Porosität KW - Spülhalden PY - 2004 SP - 4 pages PB - EAEG CY - Houten AN - OPUS4-4053 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kruschwitz, Sabine A1 - Niederleithinger, Ernst T1 - Mehrkanalige SIP - erste Erfahrungen T2 - 64. Jahrestagung der Deutschen Geophysikalischen Gesellschaft (DGG) CY - Berlin, Deutschland DA - 2004-03-08 KW - SIP KW - Geotechnik KW - Geoelektrik KW - Baustoffe KW - Feuchtigkeit KW - Porosität KW - Spülhalden PY - 2004 SP - 571 EP - 572 PB - Deutsche Geophysikalische Gesellschaft CY - Berlin AN - OPUS4-3440 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niederleithinger, Ernst A1 - Taffe, Alexander A1 - Fechner, Th. T1 - Improved parallel seimic technique for foundation assessment T2 - 18th Annual Meeting SAGEEP, Symposium on the Application of Geophysics to Engineering and Environmental Problems, "Geophysical Solutions for Today´s Challenges" CY - Atlanta, GA, USA DA - 2005-04-03 KW - Parallel Seismik KW - Fundamente KW - Pfahlprüfung KW - Baugrund PY - 2005 SP - 1004 EP - 1011 PB - Environmental and Engineering Geophysical Society CY - Atlanta AN - OPUS4-11470 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Helmerich, Rosemarie A1 - Niederleithinger, Ernst A1 - Wiggenhauser, Herbert T1 - A toolbox with non-destructive testing methods for the condition assessment of railway bridges N2 - The unified economic structure of the European market requires a unified transport infrastructure to ensure seamless and barrierfree transportation of passengers and goods. The European commission is funding the European Integrated Project Sustainable Bridges to comply with future traffic demands. The main objective of the project is to reliably assess and upgrade the bridge infrastructure for the required increase of axle loads and transport volume. 32 Institutes from 12 countries develop unified procedures for the assessment and improvement of the existing railway bridge stock under the guidance and review of six major European railway companies. Non destructive testing (NDT) is given a high priority. One of the work packages concentrates on the potential of advanced NDT-methods and creates a toolbox with advisable methods for the condition assessment of all types of railway bridges. Although NDT-methods are implemented in the quality assurance process in many industries, their application in the railway infrastructure is not common. Only a few countries have included selected NDT-methods into advanced condition assessment procedures for the management of their bridge stock. This paper describes also current activities to enhance pulse-phase thermography, impulse-radar and acoustic methods. The advanced methods enable infrastructure owners to verify construction plans, to assess structures, repair and strengthening quality or to identify in-service damages. Latest development is an automated scanning system for combined acoustic and electromagnetic measurements. The results are then combined through data fusion techniques to further increase their value for the bridge owners. T2 - 85th TRB Annual Meeting CY - Washington, DC, USA DA - 2006-01-22 KW - Non-Destructive Testing KW - Thermography KW - Railway Bridges KW - NDT-toolbox PY - 2006 SP - 1 EP - 12(?) PB - TRB CY - Washington, D.C. AN - OPUS4-12037 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pittner, Andreas A1 - Weiss, D. A1 - Schwenk, Christopher A1 - Rethmeier, Michael ED - V.I. Makhnenko, T1 - Fast generation and prediction of welding temperature fields for multiple experiments N2 - The objective of this paper is to demonstrate a new simulation technique which allows the fast and automatic generation to temperature fields based on a combination of empirical and phenomenological modelling techniques. The automatic calibration of the phenomenological model is performed by a multi-variable global optimisation routine which yields the optimal fit between simulated and experimental weld charcteristics without the need for initial model parameters. For exemplary welding processes it is shown that linear 3D heat conduction models can approximate measured temperature fields with a high accuracy. The modelling approach presented comprises the automatic calibration against multiple experiments which permits simulating the temperature field for unknown process parameters. The validation of this composite simulation model is performed for exemplary welding processes and includes the prediction of the fusion line in the cross section and the corresponding thermal cycles. T2 - 4th International Conference - Mathematical modelling and information technologies in welding and related processes CY - Katsiveli, Crimea, Ukraine DA - 2008-05-27 KW - Welding simulation KW - GMA-laser hybrid welding KW - Laser beam welding KW - Neural networks KW - Global optimisation KW - Stochastic search method KW - Inverse heat conduction problem KW - Model prediction PY - 2008 SP - 134 EP - 140 CY - Kiev, Ukraine AN - OPUS4-19639 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kruschwitz, Sabine A1 - Niederleithinger, Ernst A1 - Wiggenhauser, Herbert ED - Nüesch, R. T1 - Charakterisierung von Feuchte- und Salzbelastungen in Baumaterial durch Impedanzspektroskopie T2 - Charakterisierung von Feuchte- und Salzbelastungen in Baumaterial durch Impedanzspektroskopie CY - Karlsruhe, Deutschland DA - 2006-10-17 KW - Impedanzspektroskopie KW - Spektrale Induzierte Polarisation KW - SIP KW - Feuchte KW - Mauerwerk KW - Salzgehalt PY - 2006 SP - 185 EP - 192 PB - Aedificatio Verl. CY - Karlsruhe AN - OPUS4-14378 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schwenk, Christopher A1 - Rethmeier, Michael ED - F. Vollertsen, ED - J. Sakkiettibutra, T1 - Influence of Material Properties on Numerically Calculated Welding Distortions T2 - International Workshop on Thermal Forming and Welding Distortion (IWOTE `08) CY - Bremen, Germany DA - 2008-04-22 KW - Schweißen KW - Simulation KW - Werkstoffe KW - Sensitivität PY - 2008 SP - 35 EP - 44 AN - OPUS4-17447 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Helmerich, Rosemarie A1 - Niederleithinger, Ernst A1 - Algernon, Daniel A1 - Streicher, Doreen A1 - Wiggenhauser, Herbert T1 - Bridge inspection and condition assessment in Europe T2 - TRB 87th annual meeting CY - Washington, D.C., USA DA - 2008-01-13 KW - Construction KW - Environment and Energy PY - 2008 IS - CD-ROM (Paper 08-1450 / Session 568) SP - 1 EP - 13 PB - TRB CY - Washington, DC AN - OPUS4-16651 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wohlgemuth, V. A1 - Niederleithinger, Ernst A1 - Helmerich, Rosemarie A1 - Hieksch, Torsten A1 - Stülpner, Doreen T1 - Entscheidung vor Ort: Eine Software unterstützt bei der Prüfung von Eisenbahnbrücken - Mit effektiveren Untersuchungs-, Bewertungs- und Verstärkungsmaßnahmen lassen sich zahlreiche europäische Brücken ertüchtigen KW - Infrastruktur KW - Zerstörungsfreie Prüfung KW - Inspektion KW - Brücke PY - 2008 SP - 74 EP - 79 CY - Berlin AN - OPUS4-17995 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pittner, Andreas A1 - Schwenk, Christopher A1 - Rethmeier, Michael A1 - Weiß, D. ED - Hirata, Yoshinori ED - Manabu Tanaka, T1 - Automated generation of temperature fields for numerical welding simulation T2 - 8th International Welding Symposium - Innovations in Welding and Joining for a New Era in Manufacturing CY - Kyoto, Japan DA - 2008-11-16 KW - Welding simulation KW - Temperature Field Generation KW - Optimization KW - Neural Networks PY - 2008 SP - 158 PB - Japan Welding Society CY - Kyoto AN - OPUS4-18614 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schwenk, Christopher A1 - Rethmeier, Michael ED - H.-W. Zoch, ED - T. Lübben, T1 - Distortion optimisation of beam-welded industrial parts by means of numerical welding simulation T2 - 2nd International Conference on Distortion Engineering (IDE 2008) CY - Bremen, Germany DA - 2008-09-17 KW - Distortion KW - Optimisation KW - Industrial Parts KW - Numerical Welding Simulation KW - Beam Welding PY - 2008 SP - 483 EP - 490 AN - OPUS4-18278 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gumenyuk, Andrey A1 - Gook, Sergej A1 - Stelling, Karen A1 - Lammers, Marco A1 - Rethmeier, Michael T1 - Laserstrahl- und Laser-MSG-Hybridschweißen mit einem 20-kW-Faserlaser PY - 2008 SP - 20 EP - 30 AN - OPUS4-18321 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rethmeier, Michael T1 - Welding of light metals in the automotive industry T2 - 1st VI-IPSUS Summer School CY - Hamburg, Germany DA - 2008-09-08 PY - 2008 SP - 206 EP - 230 CY - Geesthacht AN - OPUS4-18883 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rethmeier, Michael A1 - Gook, Sergej A1 - Lammers, Marco A1 - Gumenyuk, Andrey ED - Hirata, Yoshinori ED - Manabu Tanaka, T1 - Laser-Hybrid Welding of Thick Plates up to 32 mm Using a 20 kW Fibre Laser T2 - 8th International Welding Symposium - Innovations in Welding and Joining for a New Era in Manufacturing CY - Kyoto, Japan DA - 2008-11-16 KW - Laser Beam Welding KW - High Power Fibre Laser KW - Laser-Hybrid Welding PY - 2008 SP - 43 PB - Japan Welding Society CY - Kyoto AN - OPUS4-18679 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bien, J. A1 - Helmerich, Rosemarie A1 - Niederleithinger, Ernst A1 - Kubiak, Z. T1 - Condition assessment of old railway bridges, a scientific cooperation between Berlin and Wroclaw N2 - Two years ago, the East Prussian and the Low-Silesian Railway lines celebrated their 160th anniversaries. The history of both first railway connections in the Eastern railway network development in the whole region in the 19th century is presented together with information about the railway between Berlin and Wroclaw. Special attention is paid to the railway bridges built in this period. The first large iron bridges and typical masonry arch structures are presented. Special attention is paid to masonry arches. The condition appraisal of existing masonry arches requires new developed technical methodologies, effective tools and procedures for the description of the bridges current state and function. Their current technical condition as well as service-ability is described. T2 - 3rd international congress on construction history CY - Cottbus, Germany DA - 2009-05-20 KW - Historische Eisenbahnlinien KW - Infrastruktur KW - Erhaltung KW - Wissenschaftliche Zusammenarbeit PY - 2009 VL - 1 SP - 205 EP - 211 AN - OPUS4-19532 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gumenyuk, Andrey A1 - Gook, Sergej A1 - Lammers, Marco A1 - Rethmeier, Michael T1 - High power fibre laser welding for pipeline applications N2 - With an availability of the modern high power fibre lasers the application range of laser and laser hybrid welding can be significantly increased. For the implementation of this new technology in the economically extremely interesting application of pipeline construction it is necessary to fulfil a series of systematic research studies. As it has been shown in the past the fibre laser hybrid wielding of pipeline Steel X65 up to 32 mm thickness is possible with appropriate quality. For the use of laser-hybrid welding in pipe laying insensibility towards tolerances and the possibility of girth welding are very important factors in addition to the weld seam quality. The aim of a Research project carried out in the Federal Institute for Materials Research and Testing (BAM) was the development of a welding procedure using high power fibre laser in combination with GMAWProcess which could be applied for welding of pipelines. For tests segments of linepipes with an outer diameter of 914 mm and a wall thickness of 16 mm have been welded using specially designed equipment for girth welding of pipes. First promising results for the use of laser-hybrid welding of thick materials could be demonstrated. The gap-bridgeability and misalignement was studied. T2 - LAMP2009 - 5th International congress on laser advanced materials processing CY - Kobe, Japan DA - 29.06.2009 KW - High power fiber laser KW - Laser beam welding KW - Hybrid welding KW - Pipeline construction KW - Orbital welding PY - 2009 SP - 1 EP - 5 AN - OPUS4-19936 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Straße, Anne A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Nahteigenschaftsverbesserung von dickwandigen laserstrahlgeschweißten Duplexblechen mittels pulveraufgetragenen Pufferschichten N2 - Duplexstähle finden aufgrund ihrer Eigenschaften, wie der guten Korrosionsbeständigkeit, einer hohen Festigkeit bei gleichzeitig guter Duktilität häufig industrielle Anwendung. Durch die hohen Abkühlraten beim Laserstrahlschweißen weisen Schweißnähte jedoch anstelle eines ausgeglichenen Duplexgefüges einen deutlich erhöhten Ferritanteil, im Vergleich zum Basiswerkstoff, auf. Dies führt zu einer verringerten Duktilität sowie Korrosionsbeständigkeit. Um dieses Problem zu lösen, wurde ein Prozess entwickelt, der auf einer Kantenbeschichtung mit nickelhaltigem Zusatzmaterial der zu fügenden Bleche mittels Laser-Pulver-Auftragschweißen (LPA) basiert. Die resultierenden Schweißnähte wurden zerstörend anhand von Schliffbildern, EDX-Aufnahmen, Härtemessungen und Kerbschlagbiegeversuchen geprüft. T2 - 40. Assistentenseminar der Füge- und Schweißtechnik CY - Braunlage, Germany DA - 25.09.2019 KW - Laser-Pulver-Auftragschweißen; Laserstrahlschweißen, Duplex, Pufferschichten PY - 2020 VL - 357 SP - 131 EP - 140 PB - DVS Media CY - Düsseldorf AN - OPUS4-50144 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Straße, Anne A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Quality improvement of laser welds on thick duplex plates by laser cladded buttering N2 - Because of its excellent corrosion resistance, high tensile strength and high ductility, duplex stainless steel 2205 offers many areas of application. Though laser beam welding accompanied by high cooling rates, duplex steels tend to perform higher ferrite contents in weld metal as the base metal, which leads to a reduction of ductility and corrosion resistance of the weld joint. To overcome this problem, a solution, based on buttering the plate edges by laser metal deposition (LMD) with material containing higher Ni concentrations prior to laser welding was suggested. In this context different process parameters for LMD process were investigated. In a second step the possibility of welding those edges defect free while achieving balanced austenite-ferrite ratio was verified with metallographic analysis, Electron Backscatter Diffraction (EBSD) and impact testing according to Charpy. T2 - Lasers in Manufacturing (LiM) 2019 CY - Munich, Germany DA - 24.06.2019 KW - Laser Metal Deposition; Laser Beam Welding; Duplex; Stainless Steel PY - 2020 SP - We_A31_4_4-1 EP - We_A31_4_4-6 PB - WLT (Wissenschaftliche Gesellschaft für Lasertechnik) AN - OPUS4-50143 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Putra, Stephen Nugraha A1 - Meng, Xiangmeng A1 - Yang, Fan A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Einfluss der temperaturabhängigen Modellierung der Laserstrahlabsorption auf die Schmelzbadgeometrie beim Hochleistungslaserstrahlschweißen N2 - Der Absorptionsgrad metallischer Werkstoffe spielt bei Fügeprozessen mit einer Strahlungsquelle wie dem Hochleistungslaserstrahltiefschweißen eine bedeutende Rolle. Dieser beeinflusst die Menge der absorbierten Laserenergie, welche zum Aufschmelzen sowie zur lokalen Verdampfung des zu verbindenden Materials führt. Die Laserstrahlabsorption wird von vielen physikalischen Faktoren, z.B. Laserprofil, Laserwellenlänge, Materialeigenschaft sowie Temperatur, entschieden. Dennoch wird die Temperaturabhängigkeit in vielen Simulationsarbeiten häufig ignoriert und stattdessen ein empirisch angepasster Parameter zur Kalibrierung der Ergebnisse implementiert. Diese Vorgehensweise wirkt sich negativ auf die Zuverlässigkeit des numerischen Modells sowie auf die Vorhersagbarkeit der Simulationsergebnisse aus. In der vorliegenden Arbeit wird die Temperaturabhängigkeit des Laserabsorptionsgrades in ein selbstkonsistentes zweiphasiges Modell unter Berücksichtigung der gekoppelten 3D-Fluidströmung und Wärmeübertragung einbezogen. Die berechnete Laserstrahlabsorption wird durch die temperaturabhängigen Materialeigenschaften, die Lasercharakteristik und den Einfallswinkel des Laserstrahls bestimmt. Die freie Oberfläche jeder Phase wird mithilfe der Volume-of-Fluid Methode (VOF), berechnet und die Laser-Material-Wechselwirkung wird durch ein implementiertes Ray-Tracing-Verfahren modelliert, welches auf einem lokalisierten Level-Set-Algorithmus basiert. Anschließend wird die transiente Wärmeeinbringung und die Geometrie der Schweißnaht analysiert und mit dem temperaturunabhängigen Absorptionsmodell verglichen. Es wurde festgestellt, dass die Temperaturabhängigkeit der Laserabsorption entscheidend für die genaue Bestimmung der Wärmeeinbringung und der Schmelzbadgeometrie ist. Das entwickelte Modell wurde anhand der experimentellen Untersuchungen validiert und die Bedeutung der Temperaturabhängigkeit bei der Laserstrahlabsorption wurde für die Simulation des Laserstrahltiefschweißens quantifiziert. T2 - 44. Assistentenseminar Füge- und Schweißtechnik CY - Päwesin, Germany DA - 20.09.2023 KW - Laser beam welding KW - Numerical modeling KW - Ray tracing method KW - Weld pool dynamics PY - 2024 UR - https://www.dvs-media.eu/de/neuerscheinungen/4671/44.-assistentenseminar-fuegetechnik SN - 978-3-96144-267-6 VL - 394 SP - 57 EP - 68 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-60779 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Fabry, Çağtay A1 - Hirthammer, Volker A1 - Scherer, Martin K. T1 - weldx - welding data exchange format N2 - Scientific welding data covers a wide range of physical domains and timescales and are measured using various different sensors. Complex and highly specialized experimental setups at different welding institutes complicate the exchange of welding research data further. The WelDX research project aims to foster the exchange of scientific data inside the welding community by developing and establishing a new open source file format suitable for the documentation of experimental welding data and upholding associated quality standards. In addition to fostering scientific collaboration inside the national and international welding community an associated advisory committee will be established to oversee the future development of the file format. The proposed file format will be developed with regard to current needs of the community regarding interoperability, data quality and performance and will be published under an appropriate open source license. By using the file format objectivity, comparability and reproducibility across different experimental setups can be improved. KW - Welding KW - Research data management KW - Open science KW - Open Data KW - WelDX PY - 2021 DO - https://doi.org/10.5281/zenodo.6563282 PB - Zenodo CY - Geneva AN - OPUS4-55226 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heßmann, Jennifer A1 - Hilgenberg, Kai A1 - Rethmeier, Michael T1 - Entwicklung einer neuartigen Fügetechnologie N2 - Vorstellung einer neuartigen Fügetechnologie für artungleiche Werkstoffe (Aluminium und Stahl) mit Hilfe von Laserstrahlschweißen und elektromagnetischer Schmelzbadbeeinflussung. T2 - Assistentenseminar CY - Braunlage, Germany DA - 25.09.2019 KW - Laserstrahlschweißen KW - Artungleiche Werkstoffe KW - Elektromagnetische Schmelzbadbeeinflussung KW - Fügetechnologie KW - Stahl und Aluminium PY - 2020 SN - 978-3-96144-071-9 VL - 357 SP - 34 EP - 43 PB - DVS Media GmbH CY - Deutschland, Düsseldorf AN - OPUS4-51052 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Pittner, Andreas A1 - Rethmeier, Michael T1 - Ökologische Bilanzierung von Schmelzschweißverfahren unter Berücksichtigung vor- und nachgelagerter Prozessschritte N2 - Schweißen ist ein industriell relevantes Fertigungsverfahren mit einer branchenübergreifenden Bedeutung. Die Umweltwirkungen von Schweißverfahren sind jedoch bisher unbekannt und werden im Entstehungsprozess eines Produktes entlang seiner Fertigungskette daher meist nicht berücksichtigt. Ferner ist der Schweißprozess durch einen hohen Verbrauch an Energie sowie Ressourcen gekennzeichnet. Zahlreiche Arbeiten zeigen, dass der Bedarf einer Ökobilanzierung enorm ist. Ursächlich für die bisher mangelhafte Etablierung der Ökobilanzierung von Schweißverfahren und damit Motivation für die Forschungsarbeiten ist die Unkenntnis relevanter Einflussgrößen und damit verbunden ein nicht abschätzbarer Aufwand bei der Durchführung sowie Implementierung einer Ökobilanz im fertigungstechnischen Kontext. Demgegenüber ist die Ökobilanzierung in anderen Branchen ein oft genutztes Werkzeug zur Ableitung von Umweltwirkungen. Aufgrund der aktuellen Diskussionen bezüglich des Übergangs hin zu einer klimaneutralen Produktion erfährt auch die Analyse und Optimierung der Umweltwirkungen schweißtechnischer Fertigungsverfahren derzeit eine gesteigerte Aufmerksamkeit. Für Unternehmen stellt die Verfügbarkeit umweltverträglicher Produkte bzw. Prozesse eine gewisse Werbewirksamkeit dar, wie dies im Bereich der Schweißstromquellentechnik aktuell zu beobachten ist. Gleichzeitig wird das Thema des „green welding“ auch bezogen auf die gesamte Fertigungskette immer häufiger diskutiert. Dies zeigt sich durch eine in den letzten Jahren deutlich gestiegene Publikationsaktivität. Neben Analysen zu den Einflussfaktoren auf die Nachhaltigkeit in schweißtechnischen Produktionsumgebungen stehen vor allem auch konkrete Implementierungen in der Fertigung bzw. der Produktentstehung im Fokus. Die grundlegende Vorgehensweise einer Ökobilanzierung (Life-Cycle-Assessment bzw. Abk. LCA) ist als standardisierte Methode in geltenden Normen] sowie in entsprechender Fachliteratur beschrieben. Kernelement der Ökobilanzierung ist die Sachbilanzierung, d.h. die Erfassung der relevanten Inputs sowie Outputs bezogen auf das System „Schweißprozess“. Aus dem entlang der schweißtechnischen Fertigungskette akkumulierten Ressourcenverbrauch während des Schweißens (z.B. Zusatzwerkstoff, elektrische Energie, Schutzgas, etc.) und Abfallprodukten bzw. Emissionen wird die Umweltwirkung entsprechend verschiedener Kategorien, z.B. dem CO2-Äquivalent, gemäß der World Steel Association abgeleitet. In der schweißtechnischen Community ist es bekannt, dass die Umweltwirkung von Schweißprozessen qualitativ direkt aus dem Ressourcenverbrauch abgeleitet werden kann. Der Einfluss der verschiedenen Input- sowie Outflüsse auf ausgewählte Wirkkategorien ist jedoch nicht ad-hoc quantifizierbar. Die Forschungsarbeiten haben gezeigt, dass der Materialverbrauch (z.B. Grund-/Zusatzwerkstoff, etc.), der Energieverbrauch (z.B. Wirkleistung sämtlicher elektrischer Verbraucher während der Prozesszeit), Gasverbrauch (Prozess-, Schutzgas oder Druckluft) sowie Hilfsmittel (z.B. Schutzgläser) signifikante Inputgrößen darstellen, deren Berücksichtigung im Rahmen einer Prozessökobilanz ausreichend ist. Eine wesentliche Forderung des projektbegleitenden Ausschusses war, Methoden für eine direkte Implementierung, um somit Nachnutzung der Ergebnisse zu entwickeln. Um die Ökobilanzierung als festen Bestandteil in die schweißtechnische Dokumentation einfließen zu lassen, sind die notwendigen Arbeitsschritte zu automatisieren. Daher wurden im Rahmen der Forschungsarbeiten sämtliche zu berücksichtigenden Größen durch ein an der Forschungsstelle entwickelten Schweißdatenmanagements digital erfasst sowie archiviert und in eine Umweltwirkung durch Zugriff auf entsprechende Open-Source Datenbanken „übersetzt“. Das Datenmanagement ermöglicht die eindeutige Zuordnung der Umweltwirkung eines geschweißten Bauteiles ohne Dokumentationsaufwand für den Anwender. Dadurch werden insbesondere KMU in die Lage versetzt, den Anforderungen bezüglich der Bewertung der Ökoeffizienz von Fertigungsverfahren gerecht zu werden und somit auf die nationalen sowie internationalen klimapolitischen Rahmenbedingungen vorbereitet zu sein. Die Analysen eines breiten Spektrums an Schweißverfahren haben gezeigt, dass eine Verringerung der Umweltwirkungen von Schweißverfahren demnach nur primär durch eine Reduktion des Zusatzwerkstoff- sowie Energieverbrauches zu realisieren ist. Hierbei zeigen Verfahren mit niedrigem Werkstoffeinsatz, im Extremfall autogene Verfahren, die geringsten Umweltwirkungen. Im Produktentstehungsprozess ist es daher notwendig, unter Berücksichtigung der Schweißbarkeit die ökologischen Verfahrenscharakteristika hinsichtlich konstruktiver, fertigungstechnischer sowie werkstoffspezifischer Randbedingungen zu bewerten, um die vorgeschriebenen Produkteigenschaften zu gewährleisten und die Umweltbelastung zu minimieren. Damit der Workflow, der bei der Ökobilanzierung zu durchlaufen ist, vereinheitlicht und für jeden verständlich ist, fließen die Forschungsergebnisse direkt in die DIN SPEC 35235 „Nachhaltigkeit in der Schweißtechnik – Ökobilanzierung von Schweißverfahren“ ein. Dies ist die Grundlage, um die Vergleichbarkeit von Ökobilanzen in der Schweißtechnik zu gewährleisten und so deren Akzeptanz in der Industrie zu erhöhen. Damit ist ein optimaler Transfer der Forschungsergebnisse in die Industrie gewährleistet. KW - Schweißverfahren KW - Ökobilanzierung PY - 2020 SP - 1 EP - 38 PB - DVS Media CY - Düsselorf AN - OPUS4-51856 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rethmeier, Michael A1 - Gumenyuk, Andrey A1 - Gook, S. T1 - Laser-hybrid welding for pipe production and pipe laying of thick large diameter pipes T2 - IIW 2013 - 7th Asia Pacific IIW International congress 2013 CY - Singapore DA - 2013-07-08 PY - 2013 SP - 417 EP - 423 AN - OPUS4-28935 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gumenyuk, Andrey A1 - Petrovskiy, V.N. A1 - Rethmeier, Michael A1 - Shcheglov, Pavel A1 - Uspenskiy, S.A. T1 - Condensed metal particles influence during the high power fiber laser welding N2 - Different types of lasers are used nowadays for a number of technological Solutions, Modem high power solid-state lasers with high brightness of Radiation like Fiber or disc lasers find ever more applications in welding technology. Apart from the replacement of the CC>2-iasers traditionaHy used fcr these purposes, they provide new technological possibilities of metal treatment, such as using industrial robots and remote welding with high power laser radiation. The possibility of flexible optical fiber delivery of the radiation to any point gives a great technological advantage and permits welding processes to be realized with complicated weld seam geomelries and different positions using a minimum of additional fixtures. The short wavelength of the high power solid state lasers (1.07 ’m) causes another advantage. The coefflcient of inverse 170 Bremsstrahlung absorption from free electrons in plasma for such radiation is about 100 times lower than for the COi-iaser radiation. Owing to this fact, using the solid state lasers allows it to avoid a negative influence of the welding plume. However, a short wavelength can lead to another kind of laser Radiation attenuation, which is connected with the formation of a cloud consisting of small metal particles that absorb and scatter laser radiation. This cloud arises due to the condensation of hot metal vapor by flying out from the deep Penetration channel and broadening in relatively cold atmosphere over the metal Surface. Some theoretical and experimental approaches were made in advance in Order to estimate the influence of the Condensed particles on laser radiation and welding quality. In this paper a systematic study including the determination of the Cloud size and its dynamical characteristics is presented. The results were obtained within the scope of the first stage of the metal vapor condensation process Investigation during welding with high power fiber lasers. T2 - International Conference 'Lasers in Science, Technology, Medicine' CY - Moscow, Russia DA - 19.09.2011 PY - 2011 VL - 22 SP - 170 EP - 177 AN - OPUS4-29166 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niederleithinger, Ernst A1 - Sens-Schönfelder, C. A1 - Grothe, Sven A1 - Wiggenhauser, Herbert T1 - Coda wave interferometry used to localize compressional load effects on a concrete specimen N2 - Coda Wave Interferometry (CWI), a method to evaluate subtle changes of elastic wave velocity in a medium, has been proven to be effective to detect small changes or ultrasonic velocity in concrete caused by load, temperature, moisture, damage or other means. While classical CWI is just able to determine velocity changes globally in relatively large areas between and around pairs of transmitters and receivers, several approaches have been proposed to identify the area affected by the changes more precisely. Most of them are based on the calculation of sensitivity kernels for de-correlation of signals measured at a specific state against a reference. Others follow simplified approaches. In a laboratory setup a concrete specimen of 1:5 x 1:5 x 0:5 m3 was compressed at a certain point. Maximum loads of 20 to 100 kN have been applied in 5 to 10 kN steps in various cycles. The specimen is equipped with 18 embedded ultrasonic broadband piezo transceivers (60 kHz central frequency). Ten of these receivers have been connected to a multiplexer and ultrasonic transmitting and receiving equipment in a way that allowed almost continuous two way measurements between all sensor pairs. Even simple ways to evaluate the data (e.g. crosscorrelation between signals at different load states) allowed pinpointing the load center at least approximately. A more detailed data evaluation either using CWI or even more one of the more sophisticated localization algorithms gave “sharper” results in terms of localization and a better correlation between load and velocity change/de-correlation. The results are used in upcoming monitoring systems for concrete structures. T2 - 7th European workshop on structural health monitoring CY - Nantes, France DA - 08.07.2014 KW - Concrete KW - Ultrasound KW - Coda wave inteferometry KW - Tomography KW - Correlation KW - Stress KW - Monitoring PY - 2014 SP - Paper WeBT6.3, 1427 EP - 1433 AN - OPUS4-31204 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sens-Schönfelder, C. A1 - Niederleithinger, Ernst A1 - Gassenmeier, M. A1 - Thiemann, K. A1 - Köllner, F. T1 - Monitoring and imaging based on interferometric concepts N2 - Utilization of coherent phase information in complex wave fields forms the basis of interferometric time series analysis. The concept is known since decades, but until about 15 years ago there have been no practical implementations. Meanwhile seismic interferometry is used in a wide range from investigations of the earth’s deep crust to engineering applications. Focused on monitoring and imaging the MIIC (Monitoring and Imaging based on Interferometric Concepts) project as part of the German GeoTechnologien program has contributed to this development. Special attention was given to the transfer of methodology to different length scales that range from centimeters, in laboratory applications, over geotechnical scales to even kilometers in seismological applications. General purpose methods and open source software was developed, which can be used on all scales. The core of the MIIC software is a Python library organized in different modules for various processing tasks. A graphical user interface facilitates the creation of processing routines by visualizing connections and dependencies of variables and by checking the consistency of data types. Example applications have included carbon sequestration, salt mine and railroad embankment monitoring as well as imaging changes in concrete constructions. T2 - 7th European workshop on structural health monitoring CY - Nantes, France DA - 08.07.2014 KW - Ultrasound KW - Seismics KW - Interferometry KW - Monitoring KW - Tomography KW - Concrete KW - Correlation KW - Stress KW - Coda wave interferometry PY - 2014 SP - Paper WeBT6.5, 1441 EP - 1448 AN - OPUS4-31205 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niederleithinger, Ernst A1 - Amir, J. M. A1 - Schneider, N. T1 - New possibilities for quality assurance of diaphragm wall joints N2 - Diaphragm walls are used to provide a stable and watertight confinement for the construction of tunnels, Underground railway stations, deep basements and other structures requiring deep excavations. Water seepage and soil loss through the joints have occurred on several occasions, causing extensive damage. This may have been due to uncontrolled concrete flow between the joints, unexpected geologic conditions or just poor workmanship. Different ways of quality assurance are applied on construction sites. Most of them rely on recording Parameters of the construction equipment and conventional concrete quality control. In the frame of the EUREKA/ZIM project DiWaQ we have looked at several ways to perform non-destructive Quality control. Some methods are to be applied after excavation before concreting (phase 1); others after the wall is completed (phase 2). For phase 1 we have used two different principles for checking the shape of the excavation, especially the joint to existing panels. A mechanical device which can be adapted to the excavating Equipment was developed; field tested and validated on test and construction sites. It is described in detail in another paper in the same volume. A sonar-based device with a 10 mm resolution has shown good performance in the lab, but is still under development. For phase 2 different temperature sensors have been lowered into access holes to monitor the hydration heat developed during concrete curing. The same tubes can also be used to perform electromagnetic and ultrasonic crosshole measurements across or along joints to detect flaws. Especially the ultrasonic method has shown promising results on Validation specimen at the BAM test site at Horstwalde, but limitations as well. Success substantially depended on the joint type, flaw size and distance of the sensors to the joint. T2 - International conference on piling & deep foundations CY - Stockholm, Sweden DA - 21.05.2014 KW - Diaphragm walls KW - Joints KW - Integrity KW - Crosshole sonic logging KW - Sonar PY - 2014 UR - http://www.piletest.com/papers/Niederleithinger_et_al_2014_Stockholm_2014.pdf SP - 911 EP - 918 AN - OPUS4-31201 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Algernon, D. A1 - Arndt, R. A1 - Ebsen, B. A1 - Feistkorn, S. A1 - Friese, M. A1 - Große, C. A1 - Kathage, S. A1 - Keßler, S. A1 - Kurz, J. A1 - Küttenbaum, Stefan A1 - Lohse, C. A1 - Maack, Stefan A1 - Niederleithinger, Ernst A1 - Schickert, M. A1 - Schröder, G. A1 - Taffe, A. A1 - Walther, A. A1 - Wilcke, M. A1 - Wolf, J. A1 - Wöstmann, Jens T1 - Leitfaden zur Erstellung von Prüfanweisungen für die Zerstörungsfreie Prüfung im Bauwesen (ZfP Bau) N2 - Der vorliegende Leitfaden dient zur Unterstützung der Entwicklung und Umsetzung von Prüfanweisungen für ZfP-Verfahren im Bauwesen. Er gibt einen Überblick über Verwendungszweck, Erstellung und Inhalte von Prüfanweisungen unter Berücksichtigung einheitlicher Standardisierungsziele. KW - Prüfanweisung KW - Beton KW - Leitfaden PY - 2022 SN - 978-3-947971-23-7 VL - Richtlinie B-LF 01 SP - 1 EP - 9 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin ET - Ausgabe April 2022 AN - OPUS4-54985 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bachmann, Marcel A1 - Artinov, Antoni A1 - Meng, Xiangmeng A1 - Rethmeier, Michael T1 - Numerical study of the bulging effect in deep penetration laser beam welding N2 - This article is devoted to the study of the bulging effect in deep penetration laser beam welding. The numerical results of the investigations are based upon experimental results from previous studies to reveal the relationship between the bulging effect and the hot cracking formation, as well as the mixing of alloying elements in the weld pool. The widening of the molten pool in its center area can be observed in full penetration as well as in partial penetration welds on 8 mm and 12 mm thick structural steel plates, respectively. The weld pool shape is extracted from the simulations to evaluate the extent of the necking of the solidification line as well as the bulging phenomena and its influence on the hot cracking phenomena. Relying on an earlier numerical study utilizing a fixed keyhole, simulation models considering a dynamic keyhole are developed thereto. Additionally, the mixing behavior of alloying elements during partial penetration is investigated. The link between the bulge and the studied phenomena is found to be significant. T2 - Lasers in Manufacturing Conference 2021 CY - Online meeting DA - 21.06.2021 KW - Deep penetration laser beam welding KW - Welding simulation KW - Solidification cracking KW - Bulging effect PY - 2021 SP - 1 EP - 8 AN - OPUS4-52848 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Graf, Benjamin A1 - Schuch, M. A1 - Kersting, R. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Additive process chain using selective laser melting and laser metal deposition N2 - Selective Laser Melting (SLM) and Laser Metal Deposition (LMD) are prominent methods in the field of additive manufacturing technology. While the powder-bed based SLM allows the manufacturing of complex structures, buildrate and part volumes are limited. In contrast, LMD is able to operate with high deposition rates on existing parts, however shape complexity is limited. Utilizing their respective strengths, a combination of these two additive technologies has the potential to produce complex parts with high deposition rates. In this paper, a process chain consisting of additive technologies SLM and LMD is described. The experiments are conducted using the alloys Ti-6Al-4V and Inconel 718. A cylindrical test specimen is produced and the microstructure along the SLM-LMD zone is described. In addition, this process chain was tested in the manufacturing of a turbine blade. The feasibility of implementing this process chain for small batch production is discussed. The results are evaluated to show advantages and limitations of the SLM-LMD process chain. This paper is relevant for industrial or scientific users of additive manufacturing technologies, who are interested in the feasibility of a SLM-LMD process chain and its potential for increased deposition rates. T2 - LiM 2015 - Lasers in manufacturing conference 2015 CY - Munich, Germany DA - 22.06.2015 KW - Macro processing KW - Additive manufacturing KW - Laser metal deposition KW - Ti-6Al-4V KW - Inconel 718 KW - Process chain KW - Deposition rate PY - 2015 SP - 1 EP - 6 AN - OPUS4-33778 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Cotic, P. A1 - Jaglicic, Z. A1 - Bosiljkov, V. A1 - Niederleithinger, Ernst T1 - GPR an IR thermography for near-surface defect detection in building structures N2 - Ground penetrating radar (GPR) and infrared (IR) thermography techniques have been used in many civil engineering applications for the structural visualization and defect detection. However, validation tests of the methods performance for the defection of defects in the nearsurface region with respect to the defects different material and depth below the surface are lacking. To overcome this, we performed GPR and IR thermography tests where the different material properties, shape and depth of defects were studied on concrete and the evaluation of seismic related damage propagation was assessed on stone masonry walls. The results showed that IR thermography, though being greatly affected by the presence of water in the specimen, outperformed GPR in the detection of defects very close to the surface. However, already at the depth of 3 cm and further up till almost 7.5 cm, the performance of GPR resembles the one of IR thermography for the detection of polystyrene (air) voids. On the plastered masonry walls, IR thermography could detect an air gap resulting from plaster delamination as small as 2 mm. Moreover, structural cracking resulting from the induced lateral load could be detected at an early stage. T2 - 12th International conference of the Slovenian society for non-destructive testing - Application of contemporary non-destructive testing in engineering CY - Ljubljana, Slovenia DA - 04.09.2013 KW - Radar KW - Thermography KW - Defects KW - Non-destructive testing validation KW - Concrete KW - Masonry KW - Near-surface defects KW - Ground PY - 2013 UR - http://www.ndt.net/article/ndt-slovenia2013/papers/225.pdf SP - 1 EP - 8 AN - OPUS4-33793 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niederleithinger, Ernst T1 - Progress in using geophysical methods in foundation quality assurance and inspection N2 - Modern geophysical methods might be either directly applied to foundations or integrated into existing testing schemes to assist in quality assurance and inspections. This paper gives an overview on available ideas and some more detailed examples from the author `s work including: - Vibrator technologies to improve pile integrity testing. - Ideas from vertical seismic profiling used in multichannel pile inspection - Cross- and downhole seismics to check the diameter of jet grouting columns - Improving the parallel seismic methods for precise length measurement of piles and foundation walls - Seismic migration methods to improve ultrasonic imaging of foundation slabs - Seismological tools to monitor subtle changes in concrete constructions The author strongly believes that the cooperation between geophysics and civil engineering, which is obviously becoming stronger and stronger, will lead to a large number of innovative approaches for investigations tasks currently still unresolved. A lot of challenges and chances for science and technology are right here. T2 - SAGEEP CY - Denver, CO, USA DA - 20.03.2016 KW - Non-destructive testing KW - Piles KW - Foundations KW - Slabs KW - Parallel seismic KW - Vibrator KW - Integrity PY - 2016 SP - paper 45, 1 EP - 7 AN - OPUS4-35704 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sproesser, G. A1 - Chang, Y.-J. A1 - Pittner, A. A1 - Finkbeiner, M. A1 - Rethmeier, Michael T1 - Laser-MSG-Hybridschweissen und die Ökobilanz: Sieg nach Punkten PY - 2015 UR - http://www.laser-community.com/de/11945 IS - 21 SP - 6 PB - Trumpf GmbH + Co. KG CY - Ditzingen AN - OPUS4-35252 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schneider, André A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Mobile vacuum device for laser beam welding of thick materials N2 - The development of the vapour plume during the laser beam welding of metals with propagation directions along the laser beam axis leads to a reduction of the absorbed laser power in the keyhole. These unfavourable effects can be significantly mitigated by the application of a reduced ambient pressure thus decreasing the interaction between the laser beam and evaporation products, which leads to more stable welding process and results in increased penetration depth. A conventional technique use a vacuum chamber principle, similar to that, used for electron beam welding. Application of this technique is restricted by the camera size and reduces thus the advantages of this approach especially for large components. We demonstrate a possibility of mobile local vacuum application, which allows to generate a reduced pressure only in small region around the keyhole. By using of specially designed mobile pressure lock which can be moved along the welding direction absolute pressure of around 200 mbar could be obtained. This is sufficient to increase the welding depth by around 50%. Coupons from S355 were welded with an incremental laser power from 5 kW to 12 kW at atmospheric pressure and compared to those welded at ambient pressure of 200 mbar. The evaluation of the longitudinal section revealed an increase of the welding depth by about 35%. Furthermore, the welding trials in butt joint configuration on 15 mm thick plates at various laser beam power performed for atmospheric and reduced ambient pressure of around 200 mbar. The increase in welding depth up to 40% was established for reduced pressure. Particularly, low welding speeds under reduced pressure were especially advantageous in terms of increasing the welding depth. T2 - 3rd International conference in Africa and Asia "Welding and failure analysis of engineering materials" CY - Luxor, Egypt DA - 02.11.2015 KW - High power laser beam welding KW - Mobile vacuum KW - Local reduced pressure KW - Vapour plume KW - Keyhole PY - 2015 SP - 1 EP - 7 AN - OPUS4-35094 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Using the optical measuring techniques to investigate the hot cracking susceptibility laser welded joints N2 - The safety of components or constructions is of great importance in the manufacturing and processing of metallic materials. Solidification cracking as well as the weldability of materials remain still for many years a highly contentious issues, particularly with regard to the causes of the hot crack formation. Many of studies have been conducted to determine the critical condition of occurrence of the solidification cracking. In this study different digital image correlation measuring techniques in conjunction with laser diodes as the illuminating source have been employed to measure the arising strain field during the laser welding process at the surface of the workpiece directed to the laser beam in the close vicinity of the weld pool. The Controlled Tensile Weldability test (CTW) was used to apply an external tensile load during the laser beam welding in order to generate the solidification cracks. The results showed that by means of those techniques it is possible to measure the strain field without any disturbances from the intense welding light or the smoke. Additionally, the strain and the strain rate as a critical factor determining solidification crack formation can be measured and analyzed. T2 - LiM 2015 - Lasers in manufacturing conference 2015 CY - Munich, Germany DA - 22.06.2015 KW - Solidification cracking KW - Laser beam wlding KW - Optical measuring technique KW - Hot cracking test PY - 2015 SP - 1 EP - 7 AN - OPUS4-35100 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schneider, André A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Laser beam welding of thick materials under the influence of local reduced ambient pressure N2 - The development of the vapour plume during the laser beam welding of metals with propagation directions along the laser beam axis leads to a reduction of the absorbed laser power in the keyhole. The main reasons are the scattering of the laser radiation on the condensed phase of metallic vapour as well as the defocusing of the laser beam due to the density gradient in the vapour plume. These unfavourable effects can be significantly mitigated by the application of a reduced ambient pressure thus decreasing the interaction between the laser beam and evaporation products, which leads to more stable welding process and results in increased penetration depth, as known from previous studies. A conventional technique use a vacuum chamber principle, similar to that, used for electron beam welding. Application of this technique is restricted by the chamber size and reduces thus the advantages of this approach especially for large components. We demonstrate a possibility of mobile local vacuum application, which allows to generate a reduced pressure only in small region around the keyhole. By using of specially designed mobile pressure lock which can be moved along the welding direction absolute pressure of around 200 mbar could be obtained. This is sufficient to increase the welding depth by around 50%. Coupons from S355 were welded with an incremental laser power from 5 kW to 12 kW at atmospheric pressure and compared to those welded at ambient pressure of 200 mbar. The evaluation of the longitudinal section revealed an increase of the welding depth by about 35%. Furthermore, the welding trials in butt joint configuration on 15 mm thick plates at various laser beam power performed for atmospheric and reduced ambient pressure of around 200 mbar. The increase in welding depth up to 40% was established for reduced pressure. Particularly, low welding speeds under reduced pressure were especially advantageous in terms of increasing the welding depth. T2 - VIII BTLA 2015 - 8th International conference "Beam technologies & laser application" CY - St. Petersburg, Russia DA - 21.09.2015 KW - High power laser beam welding KW - Mobile vacuum KW - Local reduced pressure KW - Vapour plume KW - Keyhole PY - 2015 SP - 45 EP - 46 AN - OPUS4-34973 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Investigation of hot crack susceptibility of laser welded joints of four austenitic steels N2 - Laser welding is a widely established manufacturing process in many industry sectors. Solidification cracking represents one of the most inadequately solved problems in welding and has major economic implications. The avoidance of hot crack is for most fusion welding processes a key challenge for an important range of metallic construction materials and affects not only the manufacturers of welding equipment and material manufacturers, but also a large number of customers using welding technologies, as well as welding standardization and research. In this study a new investigation programme has been developed to qualify the hot cracking susceptibility of a variety of austenitic stainless steels. The results show the possibility of using this technique to determinate the critical values that occur with initiation of solidification cracking during laser beam welding T2 - The METEC and 2nd European Steel Technology and Application Days CY - Düsseldorf, Germany DA - 15.06.2015 KW - Laser beam welding KW - Hot cracking KW - Solidification cracking KW - Hot cracking test PY - 2015 SP - 1 EP - 5 AN - OPUS4-36525 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Experimental study and numerical simulation of hot crack formation for novel laser weldability test. N2 - Laser beam welding is a widely established manufacturing process in several industries. The solidification cracking seriously effecting the safety of welded joints could arise during the beam welding of stainless steels caused by high solidification rates. In this study the controlled tensile weldability test (CTW) was used to investigate the solidification cracking susceptibility the fully austenitic stainless steels CrMnNi (1.4376), CrNi (1.4301), CrNiMo (1.4404) and CrNiSi (1.4828) during laser beam welding. The test facility allows welding of specimens with simultaneous application of tensile load along or cross to the welding direction while the speed of tensile force application is either constant or increases linearly. The tensile force increment and/or the displacement are set by means of a CNC controller. Trials were conducted by varying the ultimate tensile strain and cross-head speed while keeping the welding parameters constant. By observing the crack-no crack behaviour and estimating the generated crack length for each trail using a new optimized experimental procedure the influence of the two important conditions (the strain and the strain rate) for the formation of solidification cracks can be investigated, the critical values of strain and strain rate that are responsible for solidification cracking formation have been determined. In the present study a three-dimensional FEM using the contact element technique was developed to simulate the solidification cracking during laser full penetration welding under external load conditions for the steel 1.4376 in order to get a better understanding of the mechanisms of hot crack initiation and the theoretical results were compared to the experimental ones. By comparing the resulting solidification crack with simulated crack, it is possible to determine the critical condition of solidification crack formation in the region where the strains and the strain rates cannot be measured due to the high temperature. The results show a good agreement between numerical calculation and experiment. It is proposed that the solidification cracking susceptibility may be predicted by FEM analysis by using the correct mechanical and thermo-physical constants of the materials. T2 - BEAM TECHNOLOGIES & LASER APPLICATION CY - St. Petersburg, Russia DA - 21.09.2015 KW - Solidification cracking KW - Hot cracking test KW - FEM KW - Laser beam welding PY - 2015 SN - 978-5-7422-5150-7 SP - 55 EP - 68 AN - OPUS4-36615 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gook, S. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael ED - Schneider, G. ED - Zschech, E. ED - Petzow, G. T1 - Laserstrahl-MSG-Hybridschweißen von Rohren aus Hochfestem Stahl API-X80/ -X100 N2 - Das Laser-MSG-Hybridschweißverfahren führt bei untersuchten hochfesten Pipelinestählen API X80 und X120 reproduzierbar zu Schweißverbindungen mit anforderungsgerechten Zähigkeitseigenschaften. Eine metallurgische Beeinflussung der Schweißnahtzähigkeit ist durch eine gezielte Auswahl des Zusatzwerkstoffes möglich, wobei die maximale Eindringtiefe des Zusatzwerkstoffes in die Tiefe der Laserhybridnaht zu beachten ist. Die maximal erzielbare Eindringtiefe des Zusatzwerkstoffes ist auf ca. 14 mm begrenzt. Die eingesetzte Art des MSG-Lichtbogens hatte keinen erkennbaren Einfluss auf die Aufmischung im Laseranteil der Laserhybridnaht. Die besseren Ergebnisse der Kerbschlagzähigkeit konnten mit Metallpulverdrähten erreicht werden. Mit den erzielten gemittelten Werten der Schlagarbeit: ca. 200 J bei -60°C für X80 und ca. 53 J bei -40°C für X120 werden Anforderungen der Norm API 5L und DIN EN 10208-2 für die beiden untersuchten Grundwerkstoffe erfüllt. T2 - 49. Metallographie-Tagung CY - Dresden, Germany DA - 16.09.2015 KW - Hochfester Stahl KW - Laserstrahl-MSG-Hybridschweißen PY - 2015 SN - 978-3-88355-410-5 VL - 47 SP - 139 EP - 144 PB - Inventum CY - Sankt Augstin AN - OPUS4-44419 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Petrat, T. A1 - Graf, B. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Build-up Strategies for Laser Metal Deposition in Additive Manufacturing N2 - Laser Metal Deposition (LMD) as a technology for additive manufacturing allows the production of large components outside of closed working chambers. Industrial applications require a stable process as well as a constant deposition of the filler material in order to ensure uniform volume growth and reproducible mechanical properties. This paper deals with the influence of travel path strategies on temperature profile and material deposition. Meandering and spiral hatching strategies are used in the center as well as in the edge of a specimen. The temperature is measured with thermocouples attatched to the backside of the specimen. The tests are carried out on the materials S235JR and 316L. The results show a strong dependence of the maximum temperatures on the travel path strategy and the welding position on the component. T2 - Fraunhofer Direct Digital Manufacturing Conference (DDMC) CY - Berlin, Germany DA - 14.03.2018 KW - Additive Manufacturing KW - Temperature behavior KW - Laser Metal Deposition KW - Stainless Steel KW - 316L KW - Edge effects PY - 2018 SN - 978-3-8396-1320-7 VL - 1 SP - 1 EP - 6 PB - Fraunhofer-Gesellschaft CY - München AN - OPUS4-44719 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pavlov, V.A. A1 - Zavialov, S.V. A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Development of a measuring technology of strain field in welds N2 - In the article considered the problem of hot cracks occurrence during laser welding process. The main reason of their appearance is strain. The optical method for measuring full field strain locally near the solidification front during laser welding process is proposed. The proposed method of optical measurement allows to determine the real values of the critical strain for various materials characterizing the occurrence of hot cracks in laser welding process. T2 - 20th international conference "Digital signal processing and applications DSPA-2018" CY - Moskau, Russia DA - 28.03.2018 KW - Solidification cracking KW - Critical strain KW - Strain rate KW - Optical measurement KW - Laser welding KW - In situ strain PY - 2018 SN - 978-5-905278-33-4 SP - 749 EP - 754 AN - OPUS4-44910 LA - rus AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Rethmeier, Michael A1 - Gumenyuk, Andrey A1 - Bakir, Nasim T1 - Entwicklung eines Verfahrens zur Untersuchung der Heißrissresistenz lasergeschweißter Verbindungen N2 - In den letzten Jahrzehnten hat sich die Strahlschweißtechnik signifikant weiterentwickelt und als effizientes und wirtschaftliches Werkzeug in der Industrie etabliert. Für die Untersuchung der Heißrissresistenz verschiedener Werkstoffe existieren zahlreiche eigen- und fremdbeanspruchende Tests. Diese wurden aber speziell für andere Schweißverfahren, insbesondere das Lichtbogenschweißen, konzipiert. Daher besteht die Notwendigkeit eines geeigneten Heißrisstests, bei dem Werkstoffe realen Strahlschweißbedingungen ausgesetzt werden können. Die Entwicklung sowie die Standardisierung einer aussagekräftigen experimentellen Methode stellen einen wichtigen Schritt auf dem Weg zur Vermeidung von Heißrissen und damit für die Gewährleistung der Sicherheit von gefügten Bauteilen dar. Ziel der Forschungsarbeiten ist es, einen geeigneten Test zur effektiven Untersuchung der Heißrissanfälligkeit von lasergeschweißten Verbindungen zu konzipieren und zu entwickeln. KW - Heißrissresistenz PY - 2016 SN - 978-3-942541-94-7 SP - 1 EP - 110 PB - Verlag und Vertriebsgesellschaft mbH CY - Düsseldorf AN - OPUS4-41846 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Untersuchungen der Heißrissanfälligkeit laserstrahlgeschweißter Verbindungen austenitischer Stähle N2 - Die lokalen Dehnungen bzw. Dehngeschwindigkeiten im heißrisskritischen Temperaturintervall sind Funktionen des Temperaturfeldes im Nahbereich des Schmelzbades (Schweißverfahren, Werkstoff), der thermo-mechanischen Kennwerte des Versuchswerkstoffes sowie von außen aufgebrachten Verfor-mungen. Da die lokal vorherrschenden Dehnungen im Nahbereich des Schmelzbades nicht bzw. nur mit sehr aufwendigen Methoden ermittelt werden können, dienen bespielweise die im CTW-Test (Controlled Tensile Weldability) von außen aufgebrachten Dehnungen oder Dehnraten als Kriterium für die Heißriss-empfindlichkeit. In dieser Studie wurde CTW-Test zur Untersuchung der Heißrissresistenz verschiedenen austenitischen Stählen eingesetzt. T2 - 36. Assistentenseminar Füge- und Schweißtechnik CY - Brunswick, Germany DA - 05.10.2015 KW - Heißriss KW - Heißrissresistenz KW - Austenitische Stähle KW - CTW-Test PY - 2017 SN - 978-3-945023-57-0 SP - 106 EP - 111 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-41246 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niederleithinger, Ernst A1 - Grohmann, Maria A1 - Ertel, Jens-Peter T1 - Using geophysical methods in quality assurance and inspection of foundations N2 - Modern geophysical methods might be either directly applied to concrete structures or integrated into existing testing schemes to assist in quality assurance and inspections. This paper gives an overview on some ideas and developments from the author’s work: • Vibrator technologies to improve pile integrity testing. • Ideas from vertical seismic profiling used in multichannel pile inspection • Cross- and downhole seismics to check the diameter of jet grouting columns • Improving the parallel seismic methods for precise length measurement of piles and foundation walls • Seismic migration methods to improve ultrasonic imaging of foundation slabs • Seismological tools to monitor subtle changes in concrete constructions The authors strongly believe that the cooperation between geophysics and civil engineering, which is obviously becoming stronger and stronger, will lead to a large number of innovative approaches. T2 - ICEG 2017 CY - Al Ain, United Arab Emirates DA - 09.10.2017 KW - Foundations KW - NDT KW - Geophysics PY - 2017 SP - Paper EG02, 1 EP - 5 PB - UAE University CY - Al Ain, United Arab Emirates AN - OPUS4-42552 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Biegler, M. A1 - Rethmeier, Michael ED - Mayr, P. ED - Berger, M. T1 - Vorhersage zur Bauteilmaßhaltigkeit bei der additiven Fertigung mittels Schweißstruktursimulation N2 - Ziel bei der Anwendung von Schweißstruktursimulation in der additiven Fertigung ist die Anzahl an notwendigen Experimenten bis zur Erreichung von Maßhaltigkeit und gewünschter Bauteilqualität zu reduzieren. Für die Laser-Metal-Deposition besteht durch die im Vergleich zu pulverbettbasierten Verfahren größeren Auftragsraten und Spurgrößen - die Möglichkeit, schon heute volltransiente thermomechanische Simulationen für kleine Bauteile durchzuführen. Da das Bauteil nicht von Pulver umschlossen ist, kann im Prozess die Wärmeverteilung und der Bauteilverzug gemessen werden. In diesem Vortrag wird der Arbeitsablauf beim additiven Aufbau einer kleinen Struktur aus Inconel 718 demonstriert. Im Experiment werden die Temperaturverteilungen mittels Thermoelementen sowie der Verzug der Bodenplatte durch einen Laserabstandssensor gemessen. Die phänomenologische Wärmequelle in der Simulation wird anhand von Temperaturmessungen und Querschliffen kalibriert und der mechanische Verzug der Basisplatte wird mit in-situ Messwerten abgeglichen. Abschließend wird die Rechenzeit des Modells bewertet und gezeigt wie die Simulation die Bauteilqualität vorhersagen kann. T2 - Füge- und Montagetechnik Chemnitz 2017 CY - Chemnitz, Germany DA - 14.11.2017 KW - Schweißstruktursimulation KW - Additive KW - Laser-Metal-Deposition KW - Pulverbettbasiert KW - Spurgröße KW - Volltransient KW - Thermomechanisch KW - Inconel 718 KW - Phänomenologisch PY - 2017 SN - 978-3-96100-034-0 SN - 2365-8096 SN - 2365-810X VL - 2017/2 SP - 37 EP - 46 PB - readbox unipress CY - Münster AN - OPUS4-43105 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fabry, Çağtay A1 - Pittner, Andreas A1 - Rethmeier, Michael T1 - Gap width detection in automated narrow-gap GMAW with varying process parameters N2 - An approach to develop an arc sensor for gap-width estimation during automated NG-GMAW with a weaving electrode motion is introduced by combining arc sensor readings with optical measurement of the groove shape to allow precise analyses of the process. The two test specimen welded for this study were designed to feature a variable groove geometry in order to maximize efficiency of the conducted experimental efforts, resulting in 1696 individual weaving cycle records with associated arc sensor measurements, process parameters and groove shape information. Gap width was varied from 18 to 25 mm and wire feed rates in the range of 9 to 13 m/min were used in the course of this study. Artificial neural networks were used as a modelling tool to derive an arc sensor for estimation of gap width suitable for online process control that can adapt to changes in process parameters as well as changes in the weaving motion of the electrode. Wire feed rate, weaving current, sidewall dwell currents and angles were used as inputs to calculate the gap width. Evaluation the proposed arc sensor model show very good estimation capabilities for parameters sufficiently covered during experiments. T2 - IIW Annual Assembly 2017 CY - Shanghai, China DA - 25.06.2017 KW - Arc sensor KW - Automation KW - GMAW KW - Narrow-gap welding KW - Neural network PY - 2017 SP - 1 EP - 19 AN - OPUS4-44283 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Häberle, Nicolas A1 - Pittner, Andreas A1 - Rethmeier, Michael T1 - Rechenzeitersparnis bei der numerischen Lösung der nicht- linearen transienten 3D-Wärmeleitungsgleichung durch explizite Zeitintegration N2 - Die transiente nichtlineare 3D-Wärmeleitungsgleichung wurde zur numerischen Lösung mittels der Finite-Elemente-Methode im Ort und mittels explizitem Eulerschema in der Zeit diskretisiert. Der resultierende Algorithmus wurde in ein Computerprogramm überführt wobei besonderer Wert auf paralleles Rechnen gelegt wurde. Das Programm wurde auf die numerische Berechnung eines schweißtypischen transienten Temperaturfelds angewandt. Die Rechenzeit und Skalierbarkeit des Computerprogramms bezüglich der Anzahl verwendeter CPU Kerne wurde untersucht und mit dem kommerziellen FEM Programm Abaqus 6.14 verglichen. Die Anwendung der expliziten Zeitintegration resultiert in verbesserter Skalierbarkeit bezüglich der Anzahl verwendeter CPU Kerne und Rechenzeitersparnis gegenüber der in Abaqus implementierten impliziten Zeitintegrationsmethode. T2 - 37. Assistentenseminar Füge- und Schweißtechnik CY - Päwesin, Germany DA - 5. September 2016 KW - Schweißsimulation PY - 2017 SN - 978-3-96144-025-2 VL - 339 SP - 115 EP - 120 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-44282 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fu, B. A1 - Shen, J. A1 - Suhuddin, U. A1 - Su, H. A1 - dos Santos, J. A1 - Rethmeier, Michael T1 - Microstructure and mechanical properties of a modified refill friction stir spot welds of AM50 magnesium alloy N2 - Magnesium (Mg) alloys have attracted much attention due to their merits of meeting requirements of lightweight, energy-efficient and environmental friendly engineering. In this study, a modified refill friction stir spot welding (refill-FSSW) method is proposed to weid AMSO Mg alloy, in which pin and sleeve rotate at different states. Effects of process parameters on the microstructure, material flow, and mechanical properties of welds were studied. Results showed that, the modified refill-FSSW technology could enhance the intennixing of material by changing the flow state. Lap shear strength of welds could be significantly improved with changed failure modes. The modified refill FSSW technology is a competitive welding method for Mg alloy. T2 - 7th International Conference on Welding Science and Engineering in conjunction with 3rd International Symposium on Computer-Aided Welding Engineering CY - Jinan, China DA - 18.10.2017 KW - Refill friction stir spot welding KW - Friction spot welding KW - Magnesium KW - Microstructure KW - Mechanical properties PY - 2017 SP - 203 EP - 206 AN - OPUS4-43234 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niederleithinger, Ernst A1 - Baeßler, Matthias A1 - Georgi, Steven A1 - Herten, M. T1 - Comparison of static and dynamic load tests on bored piles in glacial soil N2 - BAW and BAM have performed a large scale comparison and calibration test on static and dynamic load capacity evaluation of bored piles in glacial sandy soil. The test was performed using eight piles at the BAM test site for technical safety at Horstwalde 50 km south of Berlin. The test area has been prepared and investigated in great detail using boreholes, cone penetration tests, pore pressure sensors and geophysical methods to assure controlled conditions for all piles and tests. The piles (10 m length, 0.9 m diameter) are mainly friction piles (low toe resistance) and have been checked by integrity testing. Five piles have been tested by five contractors using the dynamic method in a blind experiment, the other ones piles by static load and/or later on by the dynamic method. Some piles have been equipped with additional fibre optic Instrumentation which proved to be robust and helpful in interpreting the results of static, dynamic and integrity tests. We have experienced a deviation of the dynamic load test results gathered in the blind experiment from the static values of up to 20% in most cases, sometimes even up to 30%. This can be related to the known soil inhomogeneities, interpretation and modelling in CAPWAP and method inherent uncertainties. In cases where the static values were known by the testers for calibration, the deviations were significantly smaller. It has to be taken into account, that the two static load tests showed different results as well. Due to the low toe resistance, use of a big drop weight (11 tons) and large drop heights most piles suffered from cracking, which was clearly seen in follow up integrity tests and confirmed by excavation. The piles are available for further research. T2 - International conference on piling & deep foundations CY - Stockholm, Sweden DA - 21.05.2014 KW - Piles KW - Static load test KW - Dynamic load test KW - Integrity PY - 2014 SP - 1 EP - 8 AN - OPUS4-31202 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Petrat, T. A1 - Graf, B. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael ED - Witt, G. ED - Eichmann, M. ED - Kniffka, W. T1 - Strategien zur Erreichung eines konstanten Volumenaufbaus bei der additiven Fertigung mittels Laser-Pulver-Auftragschweißen T1 - Strategies to achieve constant build-up with laser metal deposition N2 - Der Einsatz von Hochleistungswerkstoffen verlangt nach einer hohen Endformnähe der zu fertigenden Bauteile, um den Aufwand und somit die Kosten für Materialeinsatz und Nachbearbeitung möglichst gering zu halten. Der additive Einsatz in Form des Laser-Pulver-Auftragschweißens bietet hierfür durch den gezielten Materialauftrag ein hohes Potential. Herausforderungen bestehen in Bereichen der Vorhersagbarkeit und der Reproduzierbarkeit des Materialauftrages, sowie der Fertigungszeit. Unterschiedliche Einflüsse bei der Schichterzeugung führen dabei zu Abweichungen von der Soll-Geometrie. Die vorliegenden Untersuchungen behandeln den Einfluss von Spurgeometrie, Spurüberlappung, Verfahrweg und Aufbaureihenfolge auf die entstehende Bauteilform. Die Teilung einer Lage in Rand- und Kernbereich ermöglicht einen konturangepassten Verfahrweg und eine Erhöhung der Endformnähe innerhalb einer Ebene. Die Verwendung unterschiedlicher Spurgrößen bei der Bauteilerzeugung verdeutlicht die Möglichkeiten einer hohen Auftragsrate bei gleichzeitig hoher Formgenauigkeit. Bereits kleine Unterschiede beim Materialauftrag zwischen Kern- und Randbereichen, Start- und Endpunkten sowie in Bereichen des Richtungswechsels führen aufgrund von Fehlerfortpflanzung nachmehreren Lagen zu Abweichungen in der Aufbaurichtung. Kompensierungen mittels angepasster Baustrategien werden aufgezeigt und diskutiert. Die Nickelbasislegierung Inconel 718, die Titanlegierung Ti-6Al-4V sowie der austenitische Stahl 316L sind Bestandteil der vorliegenden Untersuchungen. Die gewonnenen Erkenntnisse verdeutlichen das Potenzial einer angepassten Aufbaustrategie zur reproduzierbaren Erzeugung von Bauteilen am Beispiel unterschiedlicher Körpergeometrien. T2 - Rapid.Tech International Trade Show & Conference for Additive Manufacturing CY - Erfurt, Germany DA - 14.06.2016 KW - Laser-Pulver-Auftragschweißen KW - Additive Fertigung KW - Aufbaustrategie KW - 3DDruck KW - Ti-6Al-4V KW - Inconel 718 KW - 316L PY - 2016 SN - 978-3-446-45017-2 SP - 49 EP - 60 PB - Carl Hanser Verlag CY - München, Germany AN - OPUS4-36571 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brunner-Schwer, C. A1 - Graf, B. A1 - Rethmeier, Michael A1 - Schreiber, F. T1 - Hybrides Auftragschweißen: Potentiale des laserunterstützten Plasma-Pulver-Auftragschweißens (PTA) N2 - In diesem Beitrag wurden Untersuchungen zu einem neuartigen hybriden Laser-Plasma-Beschichtungsverfahren vorgestellt. Mit dem Ziel, die Produktivität und Wirtschaftlichkeit von Korrosions- und Verschleißschutzschichten zu steigern, wurde das kostengünstige PTA-Verfahren durch einen Laser als zweite Energiequelle ergänzt. Die vorlaufende Laserstrahlung stabilisiert den Plasmalichtbogen und ermöglicht erst eine Auftragsschweißung bei hohen Geschwindigkeiten. Die hohen Auftragraten von 4,2-5,7 kg/h bei gleichzeitig Streckenenergien von 630-720 J/cm zeigen das mögliche Potential des vorgestellten hybriden Ansatzes. In weiteren Untersuchungen muss der Prozess z.B. in Bezug auf die Oberflächenwelligkeit der Beschichtungen über eine Parameteroptimierung weiter verbessert werden. Nach den bisherigen gesammelten Erfahrungen mit dem Hybridprozess ist davon auszugehen, dass durch eine Anpassung der Energiedichteverteilung das Lasers, die Prozessgeschwindigkeiten noch einmal gesteigert werden können. T2 - 12. Fachtagung Verschleissschutz von Bauteilen durch Auftragschweissen CY - Halle, Germany DA - 13.06.2018 KW - Laser- und Lichtbogenenergie PY - 2018 SP - 104 EP - 108 AN - OPUS4-45230 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Häberle, Nicolas T1 - Multi-phase viscoplastic material modelling for grade S960QL steel N2 - Overview of recent scientific contributions on the experimental investigation and modeling of the grade S960QL steel multi-phase viscoplastic deformation behaviour with applications to computational welding mechanics. T2 - The 12th International Seminar "Numerical Analysis of Weldability" CY - Seggau, Austria DA - 23.09.2018 KW - Residual stress KW - Viscoplasticity KW - Material modeling KW - Grade S960QL steel PY - 2018 AN - OPUS4-46510 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakir, Nasim A1 - Artinov, Antoni A1 - Bachmann, Marcel A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - About the origin of solidification cracking in laser welded thick-walled structures N2 - In this study, a three-dimensional CFD-simulation model was developed to simulate the fluid flow in the weld pool. The CFD-model showed a bulging region in the middle of the depth, which is separated from the top surface and bottom surface by two narrowing regions. It can be concluded that the interaction of the movement of the laser source with the Marangoni vortex leads to a teardrop shape at the upper and bottom surface of the workpiece. Additionally, it shows that the bulging in the weld is a result of the backflows on the upper and lower sides due to the thermo-capillary-driven flows. The weld pool shape was used as a heat source in a two-dimensional thermomechanical model, which allows a highly accurate transformation of the weld pool dimensions obtained from the CFD model. This developed technique allows the consideration of physical aspects, which cannot be considered when using traditional heat sources. The mechanical model has shown that the chronological order of the solidification of the weld has a significant influence on the nature and distribution of the stresses in the weld. High tensile stress has been observed in the bulging region, i.e. in the susceptible region for solidification cracking, when compared to the other narrowing regions, which show compressive stress. T2 - 4th International Conference on Welding and Failure Analysis of Engineering Materials CY - Aswan, Egypt DA - 19.11.2018 KW - Laser beam welding KW - Solidification cracking KW - Numerical simulation KW - Weld pool geometry KW - CFD-model KW - FE-model PY - 2018 SP - W-6, 1 EP - 10 CY - Aswan, Egypt AN - OPUS4-46735 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Niederleithinger, Ernst T1 - Ultrasonic monitoring of concrete constructions using embedded transducers N2 - Ultrasonic transmission measurements are used to monitor concrete elements mostly on a laboratory scale since decades. Recently, coda wave interferometry, a technique adapted from seismology, has been introduced to civil Engineering experiments. It can be used to reveal subtle changes in concrete samples and even large construction elements without having a transducer directly at the location where the change is taking place. The methodology works best with embedded transducers to avoid coupling issues or excessive environmental influence. These transducers can be used for newly built and existing structures. Recently, large concrete beams have been equipped with a network of transducers and loaded until failure. Using code wave interferometry, it was possible to visualize stress fields and damaged areas. T2 - International Symposium on Structural Health Monitoring and Nondestructive Testing CY - Saarbrücken, Germany DA - 4.10.2018 KW - Ultrasound KW - Monitoring KW - Concrete PY - 2018 UR - http://www.ndt.net/?id=23542 SN - 1435-4934 VL - 23 IS - 12 SP - 1 EP - 6 PB - NDT.net CY - Kirchwald AN - OPUS4-46842 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Siayah, A. A1 - El-Batahgy, A. A1 - Khafagi, S. A1 - Gumenyuk, Andrey A1 - Gook, S. A1 - Rethmeier, Michael T1 - A study on shielded metal arc welding of 9%Ni steel using non-conventional ferritic welding electrode for LNG facilities N2 - The present research work aims at clarification of the effect of the welding electrode type on the mechanical properties of SMA welded joints of 9%Ni steel plates. Properties of produced SMA welded joints were evaluated using different non-destructive and destructive investigation methods. In comparison with the conventionally used Ni-based welding electrode ENiCrMo-3 (AWS A5.11), an experimentally produced non-conventional ferritic welding electrode with 11%Ni (ENi11-Company specification) has resulted in a better combination of the mechanical properties of SMA welded joints of this steel type for critical cryogenic applications. Besides, a positive economic impact for the experimentally produced non-conventional ferritic welding electrode, due to its lower cost, could be another attractive aspect. T2 - 4th International Conference on Welding and Failure Analysis of Engineering Materials CY - Aswan, Egypt DA - 19.11.2018 KW - 9%Ni steel, KW - SMAW KW - Conventional Ni-based austenitic welding electrode KW - Mechanical properties KW - Ferritic welding electrode PY - 2018 SP - W-21, 1 EP - 3 AN - OPUS4-46736 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Avilov, Vjaceslav A1 - Schneider, André A1 - Lammers, Marco A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Electromagnetic control of the weld pool dynamics in partial penetration laser beam welding of aluminium alloys N2 - An oscillating (AC) magnet field was used to suppress porosity formation and to stabilize the surface of the weld pool in bead-on-plate partial penetration 4.4 kW Nd:YAG laser beam welding of AW-5754 plates in PA position. The magnet was mounted on the laser welding head. The magnet field (up to 0.4 T and 10 kHz) was oriented perpendicular the welding direction. The analysis of the weld cross-sections and x-ray images shows a drastic reduction (up to 90%) of porosity contents in the welds. The observed effects can be explained in terms of electromagnetically (EM) induced 'Archimedes' forces as well as the EM stirring flow in the weld pool. Moreover, usage of AC magnetic fields results in a significant reduction (up to 50%) of the surface roughness of the welds. This effect can be explained in terms of electromagnetic (EM) contribution to the surface tension (the Garnier-Moreau effect) T2 - ICALEO 2012 - 31st International congress on applications of lasers & electro-optics CY - Anaheim, CA, USA DA - 23.09.2012 PY - 2012 IS - Paper 701 SP - 250 EP - 256 AN - OPUS4-27257 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rethmeier, Michael A1 - Suwala, Hubert ED - Bleck, W. ED - Raabe, D. T1 - Influence of crack-imperfections on mechnical properties of resistance spot welded ferritic-austenitic steel sheet combinations N2 - In order to respond to the challenge of the intensifying energy crisis and to meet customer requirements for automobiles, such as weight reduction for energy saving and enhancement of passenger safety, new materials have to be applied in the automotive industry. Modern Steel types with advanced mechanical properties and a complex microstructure are used. These Steel types have an increased susceptibility to weid cracking, especially during resistance spot welding. Since the influence of weid cracks on the mechanical properties of spot welded joints is not sufficiently known, specifications offen require crack-free welds. Therefore it is necessary to examine the actual effect of crack-imperfections in resistance spot welded sheets on its fatigue and impact behavior. The influence of cracks in the welding area of resistance spot welded dissimilar joints between a ferritic- and an austenitic FeMn-steel sheet has been studied. Investigations of crack-free welds and crack-afflicted welds with focus on fatigue strength were made according to the Wöhler fatigue test. The Investigation of the fatigue behavior of resistant spot welded sheets is done by analyzing the quotient of force and the oscillation amplitude. By comparing the stiffness curves and load cycles between a crack-free weid and weid with cracks. Beside the fact that it was nearly impossible to specifically produce crack-afflicted specimen by welding operations, there were later on found no significant influences of those cracks on fatigue life time behavior. T2 - 2nd HMnS -2nd International conference on high manganese steels 2014 CY - Aachen, Germany DA - 31.08.2014 KW - Resistance spot welding KW - Frequency KW - Stiffness KW - Advanced high strength steels KW - FeMn-steels KW - Cracking KW - Defects PY - 2014 SP - A-107, 1-5 AN - OPUS4-32549 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mackens, S. A1 - Fechner, T. A1 - Rios, N.I.C. A1 - Tweeton, D. A1 - Galindo Guerreros, Julio Cesar A1 - Niederleithinger, Ernst T1 - A new approach to determine the diameter of a jet grouted column using seismic methods N2 - Jet grouting is a geotechnical method of ground improvement to increase shear strength and stiffness of soils. The method is typically used to construct in-situ geometries of grouted soil such as panels or columns. The diameter of grouted columns and its material strength depend on various process parameters and the subsurface soil properties. It is only vaguely possible to predict the final column diameter. Therefore, it is a general practice to excavate a test column and perform a visual examination. However, an excavation to control the in situ diameter is often impossible, especially under complex site conditions, such as a high ground water table. Therefore, as part of a research project, borehole seismic measurements (crosshole, downhole and tomography) were tested as a quality control to verify the extent of the column and to monitor the influence of the jet grout injection on the soil over time. The field surveys were conducted before and after the jet grouting process at different time intervals. The acquired seismic data show clear traveltime differences which allow the determination of the specific column depth and diameter. The tomogram measured in the natural soil and the tomograms of the measurements after the injection process were used to visualize the time dependent effects of the jet grout injection on the soil. T2 - SAGEEP 2015 - 28th Symposium on the application of geophysics to engineering and environmental problems CY - Austin, TX, USA DA - 22.03.2015 KW - Jet grouting KW - Grouted column KW - Column diameter KW - Seismic tomography KW - Quality assurance KW - Diameter PY - 2015 DO - https://doi.org/10.4133/SAGEEP.28-021 SP - 142 EP - 146 AN - OPUS4-33678 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niederleithinger, Ernst A1 - Vrana, J. ED - Krieger, J. T1 - ZfPBau 4.0 – Herausforderungen an die ZfP im Bauwesen im Rahmen der Digitalisierung N2 - Die ZfP ist im Bauwesen bisher deutlich weniger reguliert (und auch akzeptiert) als in anderen Industriebereichen. Zum Beispiel gibt für die meisten Prüfverfahren weder Normen noch ein allgemein akzeptiertes Ausbildungs- und Zertifizierungssystem. Dies hat auch Konsequenzen für die Digitalisierung. Im Gegensatz dazu wird im Bauwesen derzeit für viele Bereiche verbindlich ein neues Verfahren zur Unterstützung von Design, Planung, Herstellung und Betrieb eingeführt: BIM (Building Information Modeling). Der Vortrag beleuchtet das Spannungsfeld zwischen dem geringen Organisations- und Standardisierungsgrad und den neuen digitalen Möglichkeiten und stellt den neuen Arbeitskreis zur ZfP 4.0 im Bauwesen vor. Er beleuchtet auch, in welchen Bereichen die ZfP im Bauwesen von Entwicklungen aus „Industrie 4.0“ und der zerstörungsfreien Prüfung in anderen Anwendungsbereichen profitieren kann - z. B. bei Datenformaten, Datenarchivierung und Schnittstellen. T2 - Fachkongress Digitale Transformation im Lebenszyklus der Verkehrsinfrastruktur CY - Esslingen, Germany DA - 29.06.2021 KW - ZfPBau KW - BIM KW - Datenbank KW - SHM KW - Industrie 4.0 PY - 2021 SP - 187 EP - 190 PB - expert CY - Esslingen AN - OPUS4-52915 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Liao, Chun-Man A1 - Hille, Falk A1 - Fontoura Barroso, Daniel A1 - Niederleithinger, Ernst ED - Papadrakakis, M. ED - Fragiadakis, M. T1 - Monitoring of a prestressed bridge model byultrasonic measurement and vibration recordings N2 - The aim of this work is to improve the current structural health monitoring (SHM) methods for civil structures. A field experiment was carried out on a two-span bridge with a built-in un-bonded prestressing system. The bridge is a 24-metre long concrete beam resting on three bear-ings. Cracks were formed subsequently when a prestressing force of 350 kN was changed to 200 kN, so that different structural states could be demonstrated. The structural assessment of this reference bridge was accomplished by the non-destructive testing using ultrasonic devices and vibration measurements. The ultrasonic velocity variations were investigated by using the coda wave interferometry method. The seismic interferometry technique was applied to the vi-bration recordings to reconstruct the wave propagation field in the bridge. This investigation shows that the wave velocity is sensitive to the current structural state and can be considered as the damage indicator. Overall, the implementation of coda cave interferometry and seismic interferometry technique facilitates structural health monitoring (SHM) in civil engineering. T2 - COMPDYN 2021 8th ECCOMAS Thematic Conference on Computational Methods in Structural Dynamics and Earthquake Engineering CY - Online meeting DA - 28.06.2021 KW - Structural health monitoring KW - Non-destructive testing KW - Coda wave interferometry KW - Seismic interferometry KW - Ultrasonic measurement KW - Prestress PY - 2021 SP - 1 EP - 9 PB - European Community on Computational Methods in Applied Sciences (ECCOMAS) AN - OPUS4-52957 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - John, Sebastian A1 - Duffner, Eric A1 - Mair, Georg W. T1 - Degradation and damage analysis of composite pressure vessels via experimental modal analysis N2 - For mobile gas storage systems, the application of type IV pressure vessels is state of the art. Type IV tanks consist of an inner polymer liner fully wrapped with fibre-reinforced plastic (FRP). Because of the complex fabric of the FRP as well as a difficulty estimable interaction behaviour between the single components under load, there are still no satisfying non-destructive testing methods to assess the current state of failure nor to estimate the level of degradation accurately and economically. At BAM division 3.5, analysing the ageing process of mobile composite pressure vessels is a major task to ensure safe usage over the whole lifetime. In this context, key aspects of our ongoing research activities are the invention of new test procedures and the development of accurate lifetime prediction models. In order to determine the level of degradation or damage, one meaningful non-destructive approach is to analyse the structural dynamic behaviour via an experimental modal analysis (EMA). Over the last few years, different types and sizes of composite pressure vessels have been tested in several research projects. The presented paper gives an insight into how to extract and interpret modal parameters and how to fit them to the results of residual strength tests. T2 - NOVEM Conference 2023 CY - Auckland, New Zealand DA - 09.01.2023 KW - Composite material KW - Pressure vessel KW - Degradation KW - Modal analysis PY - 2023 SP - 57-1 EP - 57-6 AN - OPUS4-58062 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mair, Georg W. A1 - Novak, Pavel A1 - Pötzsch, Klaus-Michael T1 - Faser-Verbundflaschen als Hochdruckspeicher für Wasserstoff - Spezielle Aspekte der Umschließungssicherheit T2 - BAM-Sonderheft 2003 "Polymere Verbundwerkstoffe zwischen Raumtemperatur und 4,2 K" ; 2. Symposium im DFG-Projekt: Eigenschaften von PTFE- und PEEK-Matrix-Werkstoffen bei tribologischer Beanspruchung CY - Berlin, Deutschland DA - 2003-02-27 PY - 2003 SP - 60 AN - OPUS4-2674 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wang, Kun A1 - Lu, Xin A1 - Schukar, Marcus A1 - Hicke, Konstantin T1 - Water absorption effects on distributed temperature sensing using polyimide-coated optical fiber N2 - Polyimide-coated fibers are becoming more popular for distributed temperature sensing (DTS) because this coating can withstand much higher temperatures than the standard acrylate coating. As a hygroscopic material, polyimide can absorb water from the air, changing its properties, which may result in a modified temperature response of the sensing fiber. This study investigates the effect of water absorption on the performance of polyimide-coated optical fibers with different sizes and properties. The thermal response of these fibers was determined experimentally from 20°C to 90°C at a broad relative humidity level ranging from 10% to 90%. The results show that all the fibers experienced a decrease in temperature sensitivity as humidity increased, with the most noticeable non-linear spectral shift observed at higher humidity levels. These findings highlight the importance of optimizing fiber design and coating properties to balance stability and sensitivity, ensuring the reliable performance of DTS systems under extreme environmental conditions. T2 - 29th International Conference on Optical Fiber Sensors CY - Porto, Portugal DA - 26.05.2025 KW - Humidity sensing KW - Distributed temperature sensing KW - Optical fiber sensors KW - Temperature sensing KW - Water absorption KW - Polyimide-coated fiber PY - 2025 SN - 978-1-5106-9187-2 DO - https://doi.org/10.1117/12.3062748 VL - 13639 SP - 136393W-1 EP - 136393W-4 PB - SPIE AN - OPUS4-63642 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lu, Xin A1 - Schukar, Marcus T1 - Humidity response analysis of optical fibers with hygroscopic coatings based on Lamé’s equations N2 - Optical fibers with hygroscopic coatings are widely used for humidity sensing, where the coating expands upon absorbing water, inducing strain in the fiber. This strain is then used to determine humidity. However, previous studies have oversimplified the strain generation process. A comprehensive three-dimensional model of the mechanical interaction between the coating and the fiber is built based on Lamé’s equations. An analytical expression for the induced strain is derived. The proposed model predicts larger humidity-induced strain compared to the reported ones, given the same Young’s modulus or coefficient of humidity expansion for the coating. Interestingly, the effect of coating thickness on strain response are quite similar for both methods. Experimental validation using fibers with a polyimide coating shows strong agreement with the theoretical predictions. T2 - 29th International Conference on Optical Fiber Sensors CY - Porto, Portugal DA - 26.05.2025 KW - Reflectometry KW - Distributed fiber sensing KW - Humidity sensors KW - Lamé’s equations KW - Optical fiber sensors KW - Structural health monitoring KW - Rayleigh scattering PY - 2025 SN - 978-1-5106-9188-9 DO - https://doi.org/10.1117/12.3060891 VL - 13639 SP - 1 EP - 4 PB - SPIE AN - OPUS4-63257 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lu, Xin A1 - Hicke, Konstantin T1 - Polarization-diversity-detection-based wavelength-scanning coherent-optical-time-domain reflectometer and its application for bus monitoring N2 - Although wavelength scanning coherent optical time-domain reflectometry (WS-COTDR) system is immune to fading effect, it suffers from occasional and localized large errors caused by the false peak in the correlation spectrum due to the large signal generated in the random interference of the backscattered light. Polarization diversity detection is applied to a standard WS-COTDR system to suppress large measurement errors. In this way, the orthogonally polarized components of backscattered light can be obtained and processed separately. Due to the birefringence of the sensing fiber, the components experience different interference processes, so the average of their correlation spectrum can suppress the false peaks and finally reduce the occurrence of larger errors. The effectiveness of the proposed method is validated in laboratory for monitoring of sinusoidal vibrations and in field for tracking the bus movement via a dark fiber. T2 - 29th International Conference on Optical Fiber Sensors CY - Porto, Portugal DA - 26.05.2025 KW - Traffic monitoring KW - Coherent optical time domain reflectometry KW - Distributed fiber sensing KW - Polarization diversity detection PY - 2025 SN - 978-1-5106-9187-2 DO - https://doi.org/10.1117/12.3060889 VL - 13639 SP - 1 EP - 4 PB - SPIE AN - OPUS4-63258 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Grohmann, Maria T1 - Low-frequency ultrasound data (pulse-echo technique) of shear horizontal and longitudinal waves acquired on the concrete step specimen “Pk401” with embedded polystyrene foam cuboids N2 - This dataset includes raw pulse-echo ultrasound measurements of a stepped concrete specimen (ID “Pk401”) from BAM, Berlin. The specimen (2000 × 800 mm) has four thicknesses—573.8, 453.4, 333.1, 210.4 mm—and contains polystyrene cuboids (120 × 120 × 60 mm) centered at depths of 270, 210, 150, and 90 mm. Measurements utilized both shear (M2502) and longitudinal (M2503) probes, combining commercial and in-house BAM equipment. KW - Reference data KW - Non destructive testing and evaluation KW - Validation KW - Ultrasonic PY - 2025 DO - https://doi.org/10.7910/DVN/0HHJFF PB - Harvard College CY - Cambridge, MA, USA AN - OPUS4-63912 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schubert, Sven A1 - Neumann, Martin A1 - Reichardt, Adrian A1 - Komann, Steffen A1 - Wille, Frank T1 - Experiences with the implementation of ageing management for packages for transport of radioactive materials in Germany N2 - The consideration of ageing mechanisms is now obligatory for the design of transport packages with integration of the para 613A into IAEA SSR-6 (Rev. 1). In addition, para 809(f) of SSR-6 (Rev. 1) requires for packages intended to be used for shipment after storage the consideration of the effects of ageing mechanisms during storage in safety analyses and the implementation of corresponding instructions for operation and maintenance. Para 503(e) requires that these packages have been maintained during storage in a manner that all requirements specified in SSR-6 (Rev.1) and in the applicable certificates of approval have been fulfilled. The evaluation of ageing mechanisms and their effects including monitoring are part of BAM’s authority assessment tasks related to the mechanical and thermal package design and quality assurance aspects. BAM has compiled the guideline BAM-GGR 023 for the implementation of ageing assessment and related measures into the approval procedure. The implementation of ageing management measures is obligatory in case of extension/renewal of package design approval certificates. BAM has evaluated package designs which are used only for transport as well as package designs for long term interim storage. The assessment of ageing mechanisms associated with the identification of ageing effects on components is the main part of the ageing management plan (AMP). Different approaches regarding AMP structure are introduced. Experiences and approaches about the evaluation of components for the expected package operating time are shown. We are focusing the evaluations of proofs for not accessible and not replaceable components. Operational experiences for these package designs are available and should be considered in the ageing evaluation. Corresponding measures for package monitoring are to be derived based on these results. The measures for monitoring shall be fixed in the Ageing Surveillance Program (ASP) to maintain a specification conform package for the transport on public routes. We show exemplary how results from ageing evaluation during the approval procedure are transferred into the ASP. T2 - PATRAM 2025 CY - San Antonio, Texas , US DA - 27.07.2025 KW - RAM KW - Ageing management KW - Radioactive material KW - Transport PY - 2025 SP - 1 EP - 8 PB - INMM CY - Washington D.C. AN - OPUS4-63987 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Martin A1 - Feldkamp, Martin A1 - Linnemann, Konrad A1 - Wille, Frank T1 - Conclusions from the first return campaign of vitrified High-Level Waste on sea going vessels from the competent authority N2 - Germany has to take back vitrified waste from the reprocessing plants in France and Great Britain. The waste resulted from decades of transporting spent fuel for reprocessing to La Hague and Sellafield. The return campaign from France was concluded in 2024 with the transport of five CASTOR® HAW28M casks to the interim storage facility in Philippsburg in southern Germany. The return of waste from Sellafield comprises three campaigns and a total of 20 CASTOR® HAW28M casks. The first campaign was performed in 2020, consisting of six CASTOR® HAW28M casks, while the second campaign was performed in March 2025, consisting of seven CASTOR® HAW28M casks. The casks were transported by rail from Sellafield to the port in Barrow-in-Furness, where they were loaded into a dedicated seagoing vessel, certified as INF Class 3 according to the INF Code. This was the first time that vitrified high level waste with considerable heat load was transported under a German design approval certificate. The third campaign is expected to be performed during 2026. BAM as part of the German competent authority system was among others involved in the assessment of the sea transport. BAM required for the first transport, among others, an assessment of temperature distribution during transport, logging of temperatures of cargo bays and graphical imaging of temperatures of the bay with the cask to ensure compliance with temperature specifications, e.g. maximal neutron absorber and gasket temperatures. Special interest was taken in the identification of possible events exceeding the specified temperatures considering the different philosophies of the IMDG code and its supplement the INF code regarding temperature control of hatches. Results show compliance with assumed conditions. T2 - PATRAM 2025 CY - San Antonio, Texas, USA DA - 27.07.2025 KW - RAM KW - Transport KW - Radioactive material KW - Sea PY - 2025 SP - 1 EP - 8 PB - INMM CY - Washington D.C. AN - OPUS4-63984 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klinge, Andrea A1 - Mönig, Julian A1 - Kalbe, Ute A1 - Richter, Matthias A1 - Horn, Wolfgang A1 - Ziegert, Christof A1 - Röhlen, Ulrich A1 - Roswag-Klinge, Eike T1 - upMIN 100 – upcycling MINeralischer Bau- und Abbruchabfälle zur Substitution natürlicher Gesteinskörnungen in Lehmbaustoffen T1 - upMIN 100 – Upcycling mineral construction and demolition debris as a substitute for natural aggregates in earth building materials N2 - Um zukünftig die Entnahme von Primärrohstoffen und die Deponierung von geeignetem Bodenaushub zu vermeiden, wurde im Forschungsvorhaben «upMIN100» der Einsatz von rezyklierten Gesteinskörnungen < 2 mm in Lehmbaustoffen untersucht. Diese Korngrößen aus Rezyklaten, die je nach Ausgangsstoffen und Produkt 5 – 70 % des fertigen Baustoffs ausmachen, waren zum Zeitpunkt des Projektstarts in den gültigen Lehmbaustoff-Normen DIN 18945 – 18948 nicht zugelassen, da diese als Zusatzstoffe nur natürliche Gesteinskörnungen nach DIN EN 12620, Mehl aus mörtelfreien Ziegeln sowie Blähperlit etc. nach DIN EN 13055-1 und als Bindemittel nur Baulehm aus natürlichen Vorkommen vorsahen. Um den Einsatz von rezyklierten Bau- und Abbruchabfällen für Lehmbaustoffe in der Norm zu ermöglichen, mussten daher die technische Durchführbarkeit, Qualitätsanforderungen an Ausgangsstoffe (z.B. Schadstoffgrenzwerte in Bezug auf Gesundheits- und Umweltverträglichkeit) sowie zulässige Anteile der Rezyklate geregelt werden. Aktuelle Sortier- und Aufbereitungsmethoden wurden im Hinblick auf die technische sowie die wirtschaftliche Machbarkeit überprüft und auf eine mögliche Optimierung untersucht. Um Fragen zur technischen Machbarkeit beantworten zu können, wurde im Vorhaben die exemplarische Entwicklung von zwei wiederverwendbaren Lehmbaustoffen (Lehmstein, Lehmputzmörtel) angestrebt, um zukünftig sowohl das Abfallaufkommen als auch die Rohstoffinanspruchnahme zu reduzieren. Zum einen sollten die Zuschläge bis zu 100% aber auch das natürliche Bindemittel Ton zu 80% – 100% substituiert werden. Der Machbarkeitsnachweis für beide Entwicklungen wurde in Form eines Prototyps mit einem Technologie-Reifegrad 4–5 (TRL 4–5) erbracht. N2 - To avoid the extraction of primary raw materials and the landfilling of suitable excavated soil in the future, the use of recycled aggregates < 2 mm in earth building materials was investigated in the “upMIN 100” research project. These grain sizes from recycled materials, which make up 5–70 % of the finished building material depending on the source materials and product, were not permitted in the applicable earth building material standards DIN 18945–18948 at the time the project started, as these only allow natural aggregates in accordance with DIN EN 12620, flour from mortarfree bricks and expanded perlite etc. as additives in accordance with DIN EN 13055-1 and only building clay from natural sources as a binder. For the use of recycled construction and demolition waste for earth building materials in the standard, the technical feasibility, quality requirements for source (e. g. limit values for harmful substances in terms of health and environmental compatibility) and permissible proportions of recyclates had to be regulated. Current sorting and processing methods were reviewed in terms of technical and economic feasibility and examined for possible optimisation. To ascertain the technical feasibility of the use of recycled construction demolition waste for earth building materials, the project developed two reusable earth building materials (earth blocks, clay plaster mortar) as examples of both waste reduction and of the use of raw materials in the future. On the one hand, up to 100 % of the aggregates and 80–100 % of the natural binder clay should be substituted. The proof of concept for both developments was provided in the form of a prototype with a technology readiness level 4–5 (TRL 4–5). T2 - Lehm 2024 Fachtagung CY - Weimar, Germany DA - 27.09.2024 KW - Recycled aggregates KW - Earthen building materials KW - Contaminants KW - Reuse KW - Resources PY - 2024 SP - 1 EP - 10 CY - Weimar AN - OPUS4-62612 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Hildebrandt, R. A1 - Seifert, M. A1 - George, Janine A1 - Blaurock, S. A1 - Botti, S. A1 - Krautscheid, H. A1 - Grundmann, M. A1 - Sturm, C. T1 - Determination of acoustic phonon anharmonicities via second-order Raman scattering in CuI N2 - We demonstrate the determination of anharmonic acoustic phonon properties via second-order Raman scattering exemplarily on copper iodide single crystals. The origin of multi-phonon features from the second-order Raman spectra was assigned by the support of the calculated 2-phonon density of states. In this way, the temperature dependence of acoustic phonons was determined down to 10 K. To determine independently the harmonic contributions of respective acoustic phonons, density functional theory (DFT) in quasi-harmonic approximation was used. Finally, the anharmonic contributions were determined. The results are in agreement with earlier publications and extend CuI's determined acoustic phonon properties to lower temperatures with higher accuracy. This approach demonstrates that it is possible to characterize the acoustic anharmonicities via Raman scattering down to zero-temperature renormalization constants of at least 0.1 cm⁻¹. KW - DFT KW - Quasi-harmonic approximation KW - Raman KW - Phonons KW - Anharmonicity PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-583699 DO - https://doi.org/10.48550/arXiv.2305.18931 SN - 2331-8422 SP - 1 EP - 14 PB - Cornell University CY - Ithaca, NY AN - OPUS4-58369 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ghosh, Sheuly A1 - Ueltzen, Katharina A1 - George, Janine A1 - Neugebauer, Jörg A1 - Körmann, Fritz T1 - Chemical ordering and magnetism in face-centered cubic CrCoNi alloy N2 - The impact of magnetism on chemical ordering in face-centered cubic CrCoNi medium entropy alloy is studied by a combination of ab initio simulations, machine learning potentials, and Monte Carlo simulations. Large magnetic energies are revealed for some mixed L12 /L10 type ordered configurations, which are rooted in strong nearest-neighbor magnetic exchange interactions and chemical bonding among the constituent elements. There is a delicate interplay between magnetism and stability of MoPt2 and L12 /L10 type of ordering which may explain opposing experimental and theoretical findings. KW - Bonding analysis KW - Alloys KW - Magnetism KW - Material design PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-600040 DO - https://doi.org/10.21203/rs.3.rs-3978660/v1 SN - 2693-5015 SP - 1 EP - 13 PB - Research Square Platform LLC CY - Durham, NC AN - OPUS4-60004 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Große, C. A1 - Wiggenhauser, Herbert A1 - Algernon, Daniel A1 - Schubert, F. A1 - Beutel, R. T1 - Impact-Echo - Stand der Technik und Anwendungen des Verfahrens T2 - DAfStb-Fachtagung 2005 "Zerstörungsfreie Prüfverfahren und Bauwerksdiagnose im Betonbau" CY - Berlin, Deutschland DA - 2005-03-10 PY - 2005 SP - 1 EP - 8 PB - BAM CY - Berlin AN - OPUS4-7366 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - George, Janine A1 - Petretto, G. A1 - Naik, Aakash A1 - Esters, M. A1 - Jackson, A. J. A1 - Nelson, R. A1 - Dronskowski, R. A1 - Rignanese, G.-M. A1 - Hautier, G. T1 - Automated bonding analysis with crystal orbital Hamilton populations (program code LobsterPy) N2 - This is the code for the program LobsterPy that can be used to automatically analyze and plot outputs of the program Lobster. KW - Automation KW - High-throughput computations KW - Bonding analysis PY - 2022 UR - https://doi.org/10.5281/zenodo.6320074 UR - https://doi.org/10.5281/zenodo.6415169 UR - https://doi.org/10.5281/zenodo.6415336 UR - https://doi.org/10.5281/zenodo.6581118 UR - https://doi.org/10.5281/zenodo.15034145 DO - https://doi.org/10.5281/zenodo.6320073 PB - Zenodo CY - Geneva AN - OPUS4-55174 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - George, Janine A1 - Naik, Aakash A1 - Jackson, A. J. A1 - Baird, S. T1 - Scripts to reproduce "Automated bonding analysis with crystal orbital Hamilton populations" N2 - This repo allows to recreate our publication: https://doi.org/10.1002/cplu.202200123 In contrast to 0.2.2, we fixed an issue with absolute path. KW - Automation KW - High-throughput computations KW - Bonding analysis PY - 2022 UR - https://github.com/JaGeo/LobsterAutomation UR - https://doi.org/10.5281/zenodo.6421928 UR - https://doi.org/10.5281/zenodo.6595062 UR - https://doi.org/10.5281/zenodo.6599556 UR - https://doi.org/10.5281/zenodo.6674670 UR - https://doi.org/10.5281/zenodo.6704163 DO - https://doi.org/10.5281/zenodo.6421927 PB - Zenodo CY - Geneva AN - OPUS4-55177 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - George, Janine A1 - Naik, Aakash T1 - DFT raw data for "Investigations on electron beam irradiated rare-earth doped SrF2 for application as low fading dosimeter material: Evidence for and DFT simulation of a radiation-induced phase" N2 - DFT raw data for the publication https://doi.org/10.1039/D2TC01773C It includes all predicted structures, the structure optimizations and the phonon computations in VASP format. Phonon computations were performed with the finite displacement method. KW - DFT KW - Phonons KW - Structure prediction PY - 2022 DO - https://doi.org/10.5281/zenodo.5942729 PB - Zenodo CY - Geneva AN - OPUS4-55417 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - George, Janine T1 - Raw data for "Automated bonding analysis with crystal orbital Hamilton populations" N2 - Raw data corresponding to the following paper: 10.1002/cplu.202200123. KW - Automation KW - High-throughput computations KW - Bonding analysis PY - 2022 UR - https://doi.org/10.5281/zenodo.6373369 DO - https://doi.org/10.5281/zenodo.6373368 PB - Zenodo CY - Geneva AN - OPUS4-55175 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Naik, Aakash A1 - Ertural, Christina A1 - Dhamrait, Nidal A1 - Benner, Philipp A1 - George, Janine T1 - A Quantum-Chemical Bonding Database for Solid-State Materials (JSONS: Part 2) N2 - This database consists of bonding data computed using Lobster for 1520 solid-state compounds consisting of insulators and semiconductors. The files are named as per ID numbers in the materials project database. Here we provide the larger computational data JSON files for the rest of the 820 compounds. This file consists of all important LOBSTER computation output files data stored as a dictionary. KW - Bonding analysis KW - Automation KW - Materials Informatics KW - Computational Chemistry KW - Database PY - 2023 DO - https://doi.org/10.5281/zenodo.7821727 PB - Zenodo CY - Geneva AN - OPUS4-57440 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Naik, Aakash A1 - Ertural, Christina A1 - Dhamrait, Nidal A1 - Benner, Philipp A1 - George, Janine T1 - A Quantum-Chemical Bonding Database for Solid-State Materials (JSONS: Part 1) N2 - This database consists of bonding data computed using Lobster for 1520 solid-state compounds consisting of insulators and semiconductors. It consists of two kinds of json files. Smaller lightweight JSONS consists of summarized bonding information for each of the compounds. The files are named as per ID numbers in the materials project database. Here we provide also the larger computational data json files for 700 compounds. This files consists of all important LOBSTER computation output files data stored as dictionary. KW - Bonding analysis KW - Automation KW - Materials Informatics KW - Computational Chemistry KW - Database PY - 2023 DO - https://doi.org/10.5281/zenodo.7794811 PB - Zenodo CY - Geneva AN - OPUS4-57439 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Naik, Aakash A1 - Ertural, Christina A1 - Dhamrait, Nidal A1 - Benner, Philipp A1 - George, Janine T1 - Quantum-Chemical Bonding Database (Unprocessed data : Part 1) N2 - This data is associated with the manuscript "A Quantum-Chemical Bonding Database for Solid-State Materials." Refer to mpids.txt to see data related to which compounds are available in the tar file. (mp-xxx refer to Materials Project ID) Refer to README.md file instructions to reproduce the data. KW - Bonding analysis KW - Automation KW - Materials Informatics KW - Computational Chemistry KW - Database PY - 2023 DO - https://doi.org/10.5281/zenodo.7852082 PB - Zenodo CY - Geneva AN - OPUS4-57441 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Naik, Aakash A1 - Ertural, Christina A1 - Dhamrait, Nidal A1 - Benner, Philipp A1 - George, Janine T1 - Quantum-Chemical Bonding Database (Unprocessed data : Part 3) N2 - This data is associated with the manuscript "A Quantum-Chemical Bonding Database for Solid-State Materials." Refer to mpids.txt to see data related to which compounds are available in the tar file. (mp-xxx refer to Materials Project ID) KW - Bonding analysis KW - Automation KW - Materials Informatics KW - Computational Chemistry KW - Database PY - 2023 DO - https://doi.org/10.5281/zenodo.7852791 PB - Zenodo CY - Geneva AN - OPUS4-57443 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Naik, Aakash A1 - Ertural, Christina A1 - Dhamrait, Nidal A1 - Benner, Philipp A1 - George, Janine T1 - Quantum-Chemical Bonding Database (Unprocessed data : Part 4) N2 - This data is associated with the manuscript "A Quantum-Chemical Bonding Database for Solid-State Materials." Refer to mpids.txt to see data related to which compounds are available in the tar file. (mp-xxx refer to Materials Project ID) KW - Bonding analysis KW - Automation KW - Materials Informatics KW - Computational Chemistry KW - Database PY - 2023 DO - https://doi.org/10.5281/zenodo.7852798 PB - Zenodo CY - Geneva AN - OPUS4-57444 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Naik, Aakash A1 - Ertural, Christina A1 - Dhamrait, Nidal A1 - Benner, Philipp A1 - George, Janine T1 - Quantum-Chemical Bonding Database (Unprocessed data : Part 2) N2 - This data is associated with the manuscript "A Quantum-Chemical Bonding Database for Solid-State Materials." Refer to mpids.txt to see data related to which compounds are available in the tar file. (mp-xxx refer to Materials Project ID) KW - Bonding analysis KW - Automation KW - Materials Informatics KW - Computational Chemistry KW - Database PY - 2023 DO - https://doi.org/10.5281/zenodo.7852107 PB - Zenodo CY - Geneva AN - OPUS4-57442 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - George, Janine T1 - Handling of orbital-resolved "ICOHPLIST.lobster" files from the software Lobster in pymatgen N2 - Python Materials Genomics (pymatgen) is a robust materials analysis code that defines classes for structures and molecules with support for many electronic structure codes. This open-source software package powers the Materials Project. In this particular contribution, the handling of obital-resolved "ICOHPLIST.lobster" files from Lobster was implemented in the software package (github handle: @JaGeo). KW - Bonding analysis KW - Density functional theory PY - 2023 UR - https://github.com/materialsproject/pymatgen/pull/2993 PB - Zenodo CY - Geneva AN - OPUS4-57569 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Naik, Aakash A1 - Ertural, Christina A1 - Dhamrait, Nidal A1 - Benner, Philipp A1 - George, Janine T1 - Quantum-Chemical Bonding Database (Unprocessed data : Part 5) N2 - This data is associated with the manuscript "A Quantum-Chemical Bonding Database for Solid-State Materials." Refer to mpids.txt to see data related to which compounds are available in the tar file. (mp-xxx refer to Materials Project ID) KW - Bonding analysis KW - Automation KW - Materials Informatics KW - Computational Chemistry KW - Database PY - 2023 DO - https://doi.org/10.5281/zenodo.7852806 PB - Zenodo CY - Geneva AN - OPUS4-57445 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Naik, Aakash A1 - Ertural, Christina A1 - Dhamrait, Nidal A1 - Benner, Philipp A1 - George, Janine T1 - Quantum-Chemical Bonding Database (Unprocessed data : Part 6) N2 - This data is associated with the manuscript "A Quantum-Chemical Bonding Database for Solid-State Materials." Refer to mpids.txt to see data related to which compounds are available in the tar file. (mp-xxx refer to Materials Project ID) KW - Bonding analysis KW - Automation KW - Materials Informatics KW - Computational Chemistry KW - Database PY - 2023 DO - https://doi.org/10.5281/zenodo.7852808 PB - Zenodo CY - Geneva AN - OPUS4-57446 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Naik, Aakash A1 - Ertural, Christina A1 - Dhamrait, Nidal A1 - Benner, Philipp A1 - George, Janine T1 - Quantum-Chemical Bonding Database (Unprocessed data : Part 7) N2 - This data is associated with the manuscript "A Quantum-Chemical Bonding Database for Solid-State Materials." Refer to mpids.txt to see data related to which compounds are available in the tar file. (mp-xxx refer to Materials Project ID) KW - Bonding analysis KW - Automation KW - Materials Informatics KW - Computational Chemistry KW - Database PY - 2023 DO - https://doi.org/10.5281/zenodo.7852820 PB - Zenodo CY - Geneva AN - OPUS4-57447 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ueltzen, Katharina A1 - George, Janine T1 - Bonding analysis results for "Chemical ordering and magnetism in face-centered cubic CrCoNi alloy" N2 - This repository contains the code and data to produce the results of chapter IIIC. Covalent bonding analysis for L12/L10 type configurations of the publication Chemical ordering and magnetism in face-centered cubic CrCoNi alloy by Sheuly Ghosh et al. KW - Magnetism KW - Bonding Analysis KW - Medium Entropy Alloys PY - 2024 DO - https://doi.org/10.5281/zenodo.11104874 PB - Zenodo CY - Geneva AN - OPUS4-59987 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hahn, Sarah-K. A1 - Janßen, Marvin A1 - Tschirschwitz, Rico T1 - Was macht eigentlich… der Demonstrator aus dem Forschungsprojekt SEE-2L? N2 - In den Jahren 2021 bis 2023 hat die BAM im Verbund mit weiteren Institutionen das BMBF-Vorhaben SEE-2L bearbeitet. Der Artikel gibt einen kurzen Überblick über die daraus weitergeführten Aktivitäten. KW - Auswirkungsbetrachtungen KW - Thermisches Durchgehen KW - Stationäre Energiespeicher KW - Lithium-Ionen-Batterie KW - Elektrische Energiespeicher PY - 2025 UR - https://info.sifo.de/-lp/GZ5jd25436/c5350177#SEE-2L VL - 2025 IS - 06 SP - 24 EP - 28 PB - Bundesministerium für Forschung, Technologie und Raumfahrt (BMFTR) CY - Bonn AN - OPUS4-63996 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Liepold, Philipp A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Semantic Segmentation for Hot Cracking N2 - The images in this dataset are light microscope images of the surfaces of modified Varestraint-Transvarestraint test samples. The training images show the surface of a tungsten inert gas weld with possible hot cracks. The dataset is intended for use in training crack segmentation networks. This database consists of images in .png format. The training images were taken in 24-bit, 3-color channels with an optical light microscope (Keyence). The corresponding mask images are 8-bit grayscale images, where 255-valued pixels (white) denote crack areas and 0-valued pixels (black) denote non-cracked areas. This dataset was created manually with the help of a self-written segmentation program based on OpenCV. I used it to train networks based on ViT, ConvNeXt, U-Net, and EfficientNet architectures. The images were taken at magnifications of 50x and 100x. The dataset is structured as follows: Wire → Magnification (50, 100) → Data (train, mask = label) → Numbered images (1, 2, 3, …) (There may be missing numbers. The reasons are: 1) I did not take images of all surfaces if they were not cracked, and 2) the 100x magnification images were taken at a later point, by which time some samples had already been prepared for further evaluation, so no images could be taken.) For every image number in train, there is an equivalent number in mask with the same image size (but a different channel size, since train is 3-channel color and mask is single-channel). There is no fixed image size (h × w). If you want to train a network, I recommend either rescaling or taking sub-images for both the training and mask sets, or using architectures that can handle varying input sizes. The research project " Evaluation of design-induced solidification cracks during welding of high-strength fine-grained structural steels" is funded by the Federal Ministry of Economics and Climate Protection as part of the "Industrial Collective Research" programme on the basis of a resolution of the German Bundestag. This project IGF 01IF21837N FE 1 / P 1516 from the Research Association for steel Application (FOSTA), Düsseldorf, is carried out at Bundesanstalt für Materialforschung und -prüfung. KW - CNN KW - Segmentation KW - Hot cracking KW - AI PY - 2025 DO - https://doi.org/10.5281/zenodo.16919144 PB - Zenodo CY - Geneva AN - OPUS4-64031 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Liu, Yuanbin A1 - Zhou, Yuxing A1 - Ademuwagun, Richard A1 - Walterbos, Luc A1 - George, Janine A1 - Elliott, Stephen R. A1 - Deringer, Volker L. T1 - Medium-range structural order in amorphous arsenic N2 - Medium-range order (MRO) is a key structural feature of amorphous materials, but ist origin and nature remain elusive. Here, we reveal the MRO in amorphous arsenic (a-As) using advanced atomistic simulations, based on machine-learned potentials derived using automated workflows. Our simulations accurately reproduce the experimental structurefactor of a-As, especially the first sharp diffraction peak (FSDP), which is a signature of MRO. We compare and contrast the structure of a-As with that of its lighter homologue, red amorphous phosphorus (a-P), identifying the dihedral-angle distribution as a key factor differentiating the MRO in both. The pressure-dependent structural behaviors of a-As and a-P differ as well, which we link to the interplay of ring topology and structural entropy. We finally show that the origin of the FSDP is closely correlated with the size and spatial distribution of voids in the amorphous networks. Our work provides fundamental insights into MRO in an amorphous elemental system, and more widely it illustrates the usefulness of automation for machine-learning-driven atomistic simulations. KW - Materials Design KW - Amorphous KW - Machine Learning KW - Machine Learning Interatomic Potentials KW - Automation PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-640204 DO - https://doi.org/10.48550/arXiv.2509.02484 SP - 1 EP - 43 AN - OPUS4-64020 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Lars A1 - Scheidemann, Robert A1 - Neumeyer, Tino A1 - Neumann, Martin A1 - Komann, Steffen A1 - Wille, Frank T1 - Thightness Assessment of welded Lids for Encapsulations of damaged Spent Nuclear Fuel in the Design Approval Process of Dual-Purpose Casks (DPC) N2 - The disposal of spent nuclear fuel in Germany is ensured using dual-purpose casks (DPC) for transport and interim storage. The leak tightness of the DPC and resulting containment is one of the most important aspects. Additional encapsulations are required for damaged spent nuclear fuel (DSNF) to guarantee safe handling and a separate tight closure. Due to the general design of DPCs for standard fuel assemblies should special requirements be considered for the design of the encapsulations for DSNF to ensure the loading in existing package designs. The absence of a replaceable sealing in the tightness barrier is the main difference for the encapsulations for damaged spent nuclear fuel. Instead, they are welded shut with a lid. The leak tightness of the encapsulation shall be proven in the design approval process for all transport conditions. This is especially valid for accident conditions of transport, where high internal impact forces may occur. BAM as German competent authority is responsible for the safety assessment of mechanical and thermal design, retention of radioactive material and quality assurance aspects of manufacturing and operation. BAM carried out a comprehensive safety assessment concerning the mechanical package design. As there are no representative standards for verifying the leak tightness of a welded lid, two approaches were being pursued. Established German standards may be used for verifying the leak tightness of a weld - but limited to low stresses. Therefore, physical tests were required for higher impact loads. Representative drop tests and highly sensitive leakage tests were performed. The paper presents an overview of the containment assessment by BAM and points out the main findings for the design of welds regarding leak tightness. Both verification procedures are described, on one hand with German standards for lower loads and on the other hand with physical tests for higher impact loads. The leak tightness of the encapsulation weld could be approved based on leakage tests and a corresponding evaluation for all transport conditions. T2 - PATRAM 2025 CY - San Antonio, Texas, USA DA - 27.07.2025 KW - Transport packages KW - Tightness assessment KW - Welded lids KW - Encapsulations PY - 2025 VL - 2025 SP - 1 EP - 11 PB - Institute of Nuclear Materials Management (INMM) CY - Indianapolis AN - OPUS4-64023 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Guitton, Matthieu A1 - Chrupek, Thierry A1 - Leblanc, Vincent A1 - Van derTuijn, Jeroen A1 - Kaufhold, Dominik A1 - Kesting, Frederik A1 - Müller, Lars T1 - Multilateral approval of a SCO-III (three spent steam generator lower parts from EDF Fessenheim nuclear power plant) multimodal shipment N2 - A Surface Contaminated Object (SCO) is defined as a solid object which is not itself radioactive, but which has radioactive material distributed on its surfaces. The 2018 Edition of the IAEA Regulations for the Safe Transport of Radioactive Material (SSR-6 Rev. 1) introduced the group SCO-III to transport unpackaged large objects. The two pressurized water reactors of the Fessenheim Nuclear Power Plant, owned by EDF, were shut down in 2020. Previously, for maintenance operations in the year 2002 and 2010, the three steam generators – over 20 metres long, 300 tons – of each reactor were taken out from the reactors, divided in two and stored on site: - EDF shipped the six upper parts, as SCO-I, to Cyclife, in Studsvik (Sweden), in 2021, to be recycled; - EDF plans two transports of the lower parts (three parts for each transport), as SCO-III (considering the higher activity due to the NPP primary coolant) to the same facility. Modes of transport are, from consignor to consignee, road, inland waterways and maritime. The countries crossed by inland waterways, from Neuf-Brisach to Dunkerque (France), are France, Germany, Belgium and the Netherlands. According to the para. 825 of SSR-6 Rev. 1, “multilateral approval shall be required for the shipment of SCO-III”. EDF has submitted to all Competent Authorities an application (para. 827A of SSR-6 Rev. 1), including a transport plan and demonstrations to withstand normal conditions of transport. Despite SSR-6 Rev. 1, national regulations have their own specificities and each Competent Authority has its own assessment procedures. Nevertheless, involved Authorities agreed for a joint review, which included: - the understanding of national regulatory requirements, - the expected level of detail and quality of the safety case, - the feedback from previous shipments of similar type, - the contents, including the conditions, of the approvals to be issued. This joint review demonstrated good coordination between authorities, enabling the application to be processed rapidly, and the various authorities to benefit from each other's expertise and feedback. This was of particular importance, as it was the first application for the transport of an SCO-III assessed by the Competent Authorities involved. Finally, the authorities were able to issue approvals, whose format is certainly in line with their national provisions, but whose content and level of requirements in terms of transport safety are consistent. T2 - PATRAM 2025 CY - San Antonio, Texas, USA DA - 27.07.2025 KW - Shipment KW - Multilateral approval KW - Steam generator KW - SCO-III PY - 2025 VL - 2025 SP - 1 EP - 8 PB - Institute of Nuclear Materials Management (INMM) CY - Indianapolis AN - OPUS4-64026 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Tscheuschner, Frank A1 - Eiben, Mario T1 - The Database Dangerous Goods (Datenbank GEFAHRGUT) of the BAM N2 - To ensure the safe transport of dangerous goods, the Federal Institute for Materials Research and Testing (BAM) in Germany created a database that delivers specially prepared and compressed information from relevant German, European and international regulations and includes an overview about authorized packaging for each mode of transport for more than 8,000 substances. T2 - DIMENSIONS.05 CY - Orlando, FL, USA DA - 2005-03-08 PY - 2005 SP - 7 pages PB - International Safe Transit Association (ISTA) CY - Orlando AN - OPUS4-7294 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schartel, Bernhard T1 - Fire Retardancy Featuring Sustainability: Food for Thought between Fake Fiction and Future N2 - Sustainability, or in other words, exploiting resources under the terms of environmental conservation for the economic welfare and prosperity continuously over time, would revolutionise the plastics industry were it to become predominant practice as a linear, fossil-fuel–based economy is switched to a carbon circular economy. Food for though is given by dint of a critical overview of the current trends and mainly by sketching our own key projects performed in the field of sustainable flame-retardant polymeric materials in the recent years. T2 - Interflam 2025 CY - London, United Kingdom DA - 30.06.2025 KW - Biocomposites KW - Sustainability KW - Renewable KW - Bio wastefibres KW - Fire Behavior PY - 2025 VL - 1 SP - 187 EP - 190 PB - Interscience Communications Ltd AN - OPUS4-63681 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Winkler, Nicolas P. A1 - Neumann, Patrick P. A1 - Schaffernicht, Erik A1 - Lilienthal, Achim T1 - Gas Distribution Mapping With Radius-Based, Bi-directional Graph Neural Networks (RABI-GNN) N2 - Gas Distribution Mapping (GDM) is essential in monitoring hazardous environments, where uneven sampling and spatial sparsity of data present significant challenges. Traditional methods for GDM often fall short in accuracy and expressiveness. Modern learning-based approaches employing Convolutional Neural Networks (CNNs) require regular-sized input data, limiting their adaptability to irregular and sparse datasets typically encountered in GDM. This study addresses these shortcomings by showcasing Graph Neural Networks (GNNs) for learningbased GDM on irregular and spatially sparse sensor data. Our Radius-Based, Bi-Directionally connected GNN (RABI-GNN) was trained on a synthetic gas distribution dataset on which it outperforms our previous CNN-based model while overcoming its constraints. We demonstrate the flexibility of RABI-GNN by applying it to real-world data obtained in an industrial steel factory, highlighting promising opportunities for more accurate GDM models. T2 - International Symposium on Olfaction and Electronic Nose (ISOEN) CY - Grapevine, TX, USA DA - 12.05.2024 KW - Gas distribution mapping KW - Spatial interpolation KW - Graph neural networks KW - Mobile robot olfaction PY - 2024 SN - 979-8-3503-7053-9 DO - https://doi.org/10.1109/isoen61239.2024.10556309 SP - 1 EP - 3 PB - IEEE AN - OPUS4-60103 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stanisavljevic, Mila A1 - Essel, S. A1 - Karbach, N. A1 - Zirzow, Johannes A1 - Hoffmann, T. A1 - Neumann, Patrick P. T1 - Performance Assessment of Methane and Carbon Dioxide Sensors for D rone Based Environmental Gas Monitoring N2 - This study evaluates the performance of methane (CH₄) and carbon dioxide (CO₂) sensors mounted on an unmanned aerial vehicle (UAV) for gas detection in open-field environments. Sensors were tested simultaneously during UAV flights over artificial gas sources, with wind data collected from two anemometers to understand plume dynamics. Field-deployed CH₄ sensors provided validation for the UAV-based measurements. The results demonstrate the sensors' effectiveness in gas detection. T2 - Sensor and Measurement Science International (SMSI) CY - Nuremberg, Germany DA - 06.05.2025 KW - UAV-based gas sensing KW - Sensor comparison KW - Methane and carbon dioxide detection PY - 2025 SN - 978-3-910600-06-5 DO - https://doi.org/10.5162/SMSI2025/B1.3 SP - 77 EP - 78 PB - AMA Service GmbH CY - Wunstorf AN - OPUS4-64038 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Patrick P. A1 - Hüllmann, Dino A1 - Winkler, Nicolas P. A1 - Lohrke, Heiko A1 - Lilienthal, A. J. ED - Lee, J. B. T1 - Outdoor Gas Plume Reconstructions: A Field Study with Aerial Tomography N2 - This paper outlines significant advancements in our previously developed aerial gas tomography system, now optimized to reconstruct 2D tomographic slices of gas plumes with enhanced precision in outdoor environments. The core of our system is an aerial robot equipped with a custom-built 3-axis aerial gimbal, a Tunable Diode Laser Absorption Spectroscopy (TDLAS) sensor for CH4 measurements, a laser rangefinder, and a wide-angle camera, combined with a state-of-the-art gas tomography algorithm. In real-world experiments, we sent the aerial robot along gate-shaped flight patterns over a semi-controlled environment with a static-like gas plume, providing a welldefined ground truth for system evaluation. The reconstructed cross-sectional 2D images closely matched the known ground truth concentration, confirming the system’s high accuracy and reliability. The demonstrated system’s capabilities open doors for potential applications in environmental monitoring and industrial safety, though further testing is planned to ascertain the system’s operational boundaries fully. T2 - 20th International Symposium on Olfaction and Electronic Nose CY - Grapevine, Texas, USA DA - 12.05.2024 KW - Aerial robot KW - TDLAS KW - Gas Tomography KW - Plume PY - 2024 SN - 979-8-3503-4865-1 DO - https://doi.org/10.1109/isoen61239.2024.10556071 SP - 1 EP - 3 PB - IEEE CY - USA AN - OPUS4-60107 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lohrke, Heiko A1 - Kohlhoff, Harald A1 - Neumann, Patrick P. ED - Lee, J. B. T1 - Robotic Scanning Absorption Spectroscopy for Methane Leak Detection: the Virtual Gas Camera N2 - This paper explores combining a gimbal-mounted tunable diode laser absorption spectroscopy (TDLAS) sensor and a video camera to create a virtual gas camera for methane leak detection. This provides a low-to-zero-cost extension of typical TDLAS gas tomography systems. A prototype setup mounted on a ground robot is evaluated. Results acquired using a simulated methane leak show the feasibility of the virtual gas camera, accurately detecting methane leaks by overlaying concentrations onto a visual image. While the acquisition time is significantly longer than for traditional gas cameras, potential enhancements are discussed. The study concludes that the virtual gas camera is feasible and useful, despite its longer acquisition time. It serves as a valuable software-only addition to typical TDLAS gas tomography systems, offering quickly-available on-site data augmentation for visual leak assessment at low-to-zero cost. T2 - 20th International Symposium on Olfaction and Electronic Nose CY - Grapevine, Texas, USA DA - 12.05.2024 KW - Mobile Robotic Olfaction KW - TDLAS KW - Gas Tomography KW - Gas Camera KW - Plume PY - 2024 SN - 979-8-3503-4865-1 DO - https://doi.org/10.1109/isoen61239.2024.10556012 SP - 1 EP - 3 PB - IEEE CY - USA AN - OPUS4-60109 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wendt, Mario A1 - Krebber, Katerina T1 - Using optical POF switches for distributed fiber optical strain measurements N2 - During recent research projects FOS sensor Systems based on PMMA (see fig.l) and perfluorined POF have been developed in order to observe critical earth structures [1,2], The sensor Systems enables real distributed Observation of objects due to the use of OTDR technique, whereas an increased Rayleigh backscatter level is observed at the strained fiber section. Fürther both used POF types are very robust which makes the sensor System suitable for harsh environment condilions and secure continuous measurements even within strong deformed structures. These characteristics offer opportunities to complement the arsenal of established electric based sensor Systems. However, due to high cost of OTDR devices the developed sensor System is not ready for the market yet. To make an improvement here the feasibility of optical switches have been investigated in order to use multiple single sensor lines connected to one OTDR device. Despite to the fact that optical switches are established in the field of telecommunication the use for distributed optical measurements is to our knowledge not investigated yet. One question which has to be answered is if strong reflections which occur at fiber couplings disable the Signals of the single sensor lines. A further interest is to secure that the known sensing characteristics of the single System is still provided via optical switch. For this purpose two optical switches each adapted to PMMA and perfluorined characteristics respectively have been tested. Laboratory tests have been conducted, whereas two OTDR units for PMMA and perfluorined POF were available. Finally the switches have been tested during field tests. T2 - POF 2012 - 21st International conference on plastic optical fibers CY - Atlanta, Georgia, USA DA - 10.09.2012 KW - Distributed strain sensors KW - Optical switch KW - OTDR PY - 2012 SP - 133 EP - 136 AN - OPUS4-26743 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Popiela, Bartosz A1 - Günzel, Stephan A1 - Mair, Georg W. A1 - Seidlitz, Holger ED - Nabizada, A. ED - Dechany, A. ED - Carré, B. ED - Ghogare, D. ED - Stendardo, E. ED - Lappa, F. ED - Vanlaere, J. ED - Mendoza, M. J. ED - Dejonghe, M. ED - Daese, M. ED - Namazifard, N. ED - Jacops, R. ED - Jottrand, S. ED - Pahlavan, S. T1 - Modelling of the Manufacturing Process Related Residual Stresses in Type 4 Pressure Vessels for Hydrogen Storage N2 - The publication is an extended abstract on the modelling of the manufacturing process related residual stresses in type 4 pressure vessels for hydrogen storage. A 2D analytical model based on the classical laminate theory and a 3D finite element model are introduced. The calculated residual stress state after the filament winding process as well as the stress state in service are presented and discussed. T2 - European PhD Hydrogen Conference 2024 (EPHyC2024) CY - Ghent, Belgium DA - 20.03.2024 KW - Composite KW - Hydrogen KW - Pressure vessel KW - Residual stresses KW - Filament winding KW - Carbon fiber PY - 2024 VL - 2024 SP - 445 EP - 450 PB - Hydrogen Europe Research, BE-HyFE AN - OPUS4-59779 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mair, Georg W. A1 - Scherer, Florian A1 - Scholz, Irene A1 - Schönfelder, Thorsten T1 - The residual strength of breathing air composite cylinders towards the end of their service life - A first assessment of a real-life sample N2 - Emergency response units increasingly use pressure cylinders made from fibre composites for breathing air as elements of personal protective equipment (PPE). Such applications expose the composite cylinders to harsh temperature and handling conditions. At least in Europe, standards have been used for certifying PPE, which are designed and mandatory for the approval of pressure receptacles for the transport of dangerous goods. Therefore, service conditions specific to PPEs are not accounted for in these standards. In this paper, BAM (Federal Institute for Materials Research and Testing) investigates the residual safety of a composite cylinder design at the end of their designated service life of 15 years. The cylinders (test pressure PH 450 bars; 6.8 Litres) are of one design type with aluminium liner and fully wrapped with carbon fibres, which is commonly considered a “Type III” cylinder. All cylinders were used as PPE by the Berlin fire department and randomly picked in three samples of 25 cylinders each before tested. At BAM, the cylinder samples underwent hydraulic load cycle tests (LCT), conventional burst tests (BT) and so called slow burst tests (SBT). A concept for quantification of strength degradation already introduced by BAM was applied. This concept is based on a probabilistic assessment of the average strength and scatter of each sample of cylinders. The strength distributions of the used PPEcylinders is shown and analysed. Some unexpected effects are shown and a refinement of the statistical assessment is introduced. T2 - ASME 2014 Pressure Vessels and Piping Conference CY - Anaheim, CA, USA DA - 20.07.2014 KW - Composite KW - Assessment KW - Cylinder KW - Residual strenght PY - 2014 SN - 978-0-7918-4603-2 SP - PVP2014-28168, 1 EP - 9 AN - OPUS4-40173 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Schönfelder, Thorsten T1 - Einfluss thermischer Betriebsbelastungen auf die Sicherheit von Typ-III-Druckgasbehältern N2 - Das Einsatzspektrum von den besonders leichten Druckbehältern aus Faserverbund-werkstoffen erweitert sich kontinuierlich. Dies führt dazu, dass mit der erweiterten Verwendung auch die thermisch zulässigen Einsatzgrenzen dieser Behälter ausgeschöpft und sogar teilweise überschritten werden. So können bspw. Atemluftflaschen im Brandeinsatz der Feuerwehr an der Behälteroberfläche derart hohen Umgebungstemperaturen ausgesetzt werden, dass die zulässige Höchsttemperatur von 65 °C um bis zu 185 °C überschritten wird. Diese Arbeit untersucht und bewertet die Auswirkungen dieser erhöhten thermischen Betriebslasten auf die Typ-III-Atemluftflasche. Dieser Behältertyp besteht aus einem Innenbehälter aus Aluminium, der von einem Faserverbundwerkstoff umschlossen ist. Durch Analyse der thermischen Betriebslasten in ausgewählten Anwendungsbereichen und durch experimentelle Temperaturversuche an Probebehältern konnte gezeigt werden, dass bei der Brandbekämpfung die untersuchten Atemluftflaschen lokal über das in der Zulassung abgeprüfte Temperaturspektrum erhitzt werden. Der Glasübergangsbereich des Faserverbundwerkstoffs wird partiell um bis zu 95 °C überschritten. Um die reale Sicherheit der Atemluftflasche bewerten zu können, wurde ein analytisches Hybridbehältermodell entwickelt, das die Beanspruchungen mit validierten Materialtemperaturverläufen berechnet. Mit der Einbindung von Schädigungsansätzen konnte ein bisher nicht hinreichend beachtetes thermisches Degradationsverhalten in den Berechnungen berücksichtigt werden. Die sicherheitstechnische Bewertung basierte auf der Gegenüberstellung der Beanspruchungen aus den realen Betriebsbelastungen und abzuprüfenden Zulassungskriterien. Zudem wurden insgesamt 90 altersbedingt ausgesonderte Feuerwehr-Atemluftflaschen zerstörend geprüft, um nähere Erkenntnisse über den Sicherheitszustand am Ende der Lebenszeit zu erhalten. Die Versuche wurden ebenfalls zur Validierung der Schädigungsansätze genutzt. Als Ergebnis der Arbeit wird am Beispiel des untersuchten Baumusters gezeigt, dass die Sicherheit dieser Atemluftflasche am Lebensende noch hinreichend ist. Jedoch konnte an einigen Exemplaren dieses großzügig dimensionierten Baumusters eine erhöhte Abnahme der Festigkeit festgestellt werden. Sollten Atemluftflaschen auf die vorgeschriebenen Normanforderungen optimiert werden, d.h. weniger überdimensioniert sein, wäre dem thermisch bedingten Sicherheitsverlust eine erheblich detailliertere Aufmerksamkeit zu widmen. N2 - The application range of the particularly light pressure cylinders made of fiber composite material is continuously expanding. The result is that the thermally permissible operating limits of these cylinders are fully exploited or even partly exceeded. Thus, for example the breathing air cylinder used by fire fighters is exposed to such high ambient temperatures that the upper temperature of the applied test of 65 °C is exceeded for up to 185 °C. This thesis analyzes and assesses the effects of these increased thermal operating loads on the type III breathing air cylinder. This type of cylinder consists of an inner cylinder made of aluminum, enclosed by fiber composite material. By analyzing the thermal operating loads in selected application areas and by experimental temperature tests on sample cylinders it could be shown that the analyzed breathing air cylinder during firefighting is heated locally above the tested approval temperature range. The glass transition range of the fiber composite material is exceeded partially by up to 95 °C. In order to assess the real safety of the breathing air cylinder, an analytical composite-hybrid cylinder model has been developed which calculates the stresses using validated material temperature gradients. With the integration of theoretical concepts as regards various damages a thermal degradation which has not been sufficient acclaimed yet could be included in the calculations. The safety assessment is based on the comparison of the stresses from the real operating loads and the evaluated approval criterias. In addition, a total of 90 firefighting breathing air cylinders which have become obsolete and thus taken out of service, were destructively tested to obtain more precise knowledge about the safety status at the end of life. The tests were also used to validate the damage approaches. Based on the example of the analyzed sample of a breathing air cylinder the results of this thesis show that the safety of this sample at the end of life is still sufficient. However, an increased reduction in strength was observed at some specimens of this highly overdimensioned design type. If breathing air cylinders are optimized to the required standards, i.e. being less overdimensioned, a more detailed attention must be focused on the thermally induced loss of safety. KW - Druckgasbehälter KW - Sicherheit KW - Composite KW - Faserverbundwerkstoff KW - Temperatur KW - Feuerwehr KW - Zulassung KW - Degradation PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:hbz:468-20171108-090008-4 SP - 1 EP - 158 PB - Bergische Universität CY - Wuppertal AN - OPUS4-43332 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eisermann, René A1 - Basedau, Frank A1 - Kadoke, Daniel A1 - Gründer, Peter A1 - Schoppa, André A1 - Lehr, Christian A1 - Szczepaniak, Mariusz A1 - John, Sebastian A1 - Schukar, Marcus A1 - Munzke, Dorit A1 - Mair, Georg W. T1 - Distributed strain sensing with sub-centimetre resolution for the characterisation of structural inhomogeneities and material degradation of industrial high-pressure composite cylinders N2 - Fibre-reinforced plastics (FRP) especially carbon-fibre-reinforced polymer (CFRP) and glass-fibre-reinforced polymer (GFRP) are commonly used materials in high pressure vessels and storage units for automotive and aerospace purposes. Optical fibres are suitable to be integrated or directly applied to the surface of FRP components. Using optical fibres it is possible to monitor the distributed strain profiles and changes within the fatigue life of a pressure vessel to ensure the operational safety. Within artificial ageing experiments we used swept wavelength interferometry (SWI) based distributed strain sensing for the monitoring of commercial high-pressure composite cylinder. This artificial ageing was performed using test conditions of 503bar pressure load (service pressure 300 bar) and 89 °C for 100 h. The polyimide coated optical fibres were glued to the surface externally in circumferential and axial direction. Using distributed strain sensing (DSS) material expansion of over 0.5% were monitored with sub-centimetre spatial resolution. Within the circumferential direction we observed up to 10 % local fluctuation compared to the median strain caused by inhomogeneous material expansion, which could cause local material fatigue. In addition, we determined material degradation manifested itself as localized remaining material expansion and/or contraction. Results have been validated by other non-destructive methods like digital strip projection. T2 - 9th European Workshop on Structural Health Monitoring (EWSHM) CY - Manchester, UK DA - 10.07.2018 KW - Distributed fibre optic sensors KW - Optical backscatter reflectometry KW - Swept wavelength interferometry (SWI) KW - Structural health monitoring (SHM) KW - Composite structures KW - Optical fibre PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-458926 SP - 1 EP - 8 AN - OPUS4-45892 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gleim, Tobias ED - Monavari, Mehran ED - Bertovic, Marija ED - Wille, Frank T1 - AI-Based Documentation Analysis for Safety Assessment of Packages for Radioactive Material N2 - The transportation of radioactive material requires, dependent on type and quantity of the radioactive material, a regulatory approval based on the package type. Safety assessments shall be conducted in compliance with the International Atomic Energy Agency (IAEA) regulations and documented in a comprehensive package design safety report to obtain approval from authority. This comprehensive safety report evaluates a broad range of requirements from the regulations, including mechanical, thermal, shielding, criticality and transport requirements and controls, and testing assessments. Additionally, it encompasses supporting documents such as specifications, inspections, certifications, drawings, and guidelines in a variety of complex documents. Safety and manufacturing reports contain multiple interconnected sub-reports covering various topics. Changes, such as component modifications, material property updates, or regulatory revisions, often impact multiple sections of the safety analysis reports, making even minor adjustments complex and time-consuming. Each transport package has unique requirements to be fulfilled, making every safety report distinct, despite following the same regulatory framework. Most documentation exists in standard digital formats but is often not machine interpretable, preventing automated analysis of the critical dependencies between them. This paper argues that moving beyond simple digitization towards structured knowledge representation is essential for addressing these challenges. We propose a multi-stage approach, beginning with foundational AI technologies such as Large Language Models (LLMs) and Retrieval-Augmented Generation (RAG), and progressing toward the construction of Knowledge Graphs (KGs). KGs convert unstructured and semi-structured information into a connected, queryable network, enabling precise tracing and visualization of complex interdependencies within the documentation landscape. By linking interpretable content directly to datasheets, tables, simulations, experimental results, standards, and regulations, such a system would automatically identify changes and interdependencies. Related conditions could be validated using AI-based tools, reducing the need for manual intervention, improving both efficiency and safety. Human error plays a significant role in drafting, reviewing, and revising safety reports, often requiring iterative review cycles and multiple reviewers before approval. A digital quality infrastructure could reduce iterations and further improve efficiency. Integrating AI into this process could optimize safety assessments and enhance their robustness by leveraging interpretability to enhance safety. This preliminary study explores the readiness and requirements for using intelligent documentation analysis system in the context of regulatory compliance for package safety for the transport of radioactive material. By analysing current documentation workflows, we identify how LLM-based tools can interpret complex safety reports and highlight critical interdependencies and then demonstrate why a KG-based architecture is necessary to robustly manage and query critical interdependencies. This lays the groundwork for future agentic AI systems capable of proactively supporting the safety assessment lifecycle, while stressing the importance of robust data governance and AI reliability in this highly regulated context. T2 - PATRAM 2025 CY - San Antonio, TX, USA DA - 27.07.2025 KW - AI, RAG, LLM, Knowledge Graph PY - 2025 SP - 1 EP - 10 PB - Institute of Nuclear Materials Management (INMM) AN - OPUS4-63863 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Naster, Maximilian A1 - Gleim, Tobias A1 - Wille, Frank T1 - Experimental and numerical analyses of hydrogen flames for the thermal testing of transport packages for radioactive material N2 - In this paper we present an update of the hydrogen based test rig for an ongoing feasibility study of using hydrogen as an energy source for the thermal testing of transport packages containing radioactive materials [ The test rig is capable of combusting hydrogen for a wide range of different burner geometries, mass flows , hydrogen blends and single jet flame operation s as well as a full array of burners for thermal testing can be set up. As this type of fire test according to the IAEA boundary conditions does not yet exist, a large number of preliminary investigations, safety assessments and simulations must be carried out in order to develop a viable concept for hydrogen fires. In a first step of the feasibility study, the temperature , structure, and radiative behavior of hydrogen jet flames must be surveyed. The simulation with a single hydrogen flame was investigated in a previous work. In the next step the results are used to study the interaction and structural behavior of multiple jet flames in proximity with varying nozzle distances. With the test rig completed, it will be possible in future works to design burner frames suitable for fire reference tests to make comparisons with pool and propane fires used in assessment procedure today. Thus, preliminary comparative numerical simulations are conducted to model the behavior of overlapping hydrogen jet flames using the software package Ansys®. This paper gives an overview on the current state and design of the test rig. Furthermore, the results of the simulations show that nozzle geometry, mas s flow and nozzle distance provide significant design margin for designing a test fire capable of fully engulfing a specimen. T2 - PVP2025, Pressure Vessels & Piping Conference CY - Montreal, Quebec, Canada DA - 20.07.2025 KW - Computational Fluid Dynamics (CFD) KW - Fire testing KW - Hydrogen KW - IAEA PY - 2025 SP - 1 EP - 10 AN - OPUS4-63864 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Affagard, Jean-Sebastien A1 - Gleim, Tobias A1 - Louis, Baptiste A1 - Quercetti, Thomas A1 - Ledroit, Frédéric A1 - Létang, Eric T1 - Towards a simplifiedmodel of the delayed impact: numerical and experimental outlook N2 - The IAEA Regulations for the Safe Transport of Radioactive Material No. SSR-6 require drop tests for demonstrating the ability of a package to withstand accident conditions of transport. In case a gap exists between the contents and the lid, it can result in a delayed impact of the content onto the lid system during a vertical drop test. The kinematic energy transmitted to the lid in such cases can be significant due to the stiffness of the impact, leading to high stresses in the bolts compared to a configuration without a gap. In the past, IRSN and BAM have individually investigated the modelling of the delayed impact phenomenon. BAM has examined the effects of the delayed impact phenomenon for spent fuel packages in a comparative analysis between experiments and simulations, which was presented at SMIRT 2013. Meanwhile, IRSN’s has developed a simple numerical tool that can quickly evaluate the influence of various parameters before considering a more complex finite element numerical calculation. This tool was presented at PATRAM 2022. In 2023, BAM and IRSN (now ASNR - French nuclear safety and radiation protection authority) decided to jointly pursue their study on the delayed impact phenomenon, incorporating damping effects, by developing new insights and techniques. To this end, a controlled and simplified set of experiments needs to be developed to calibrate and validate the simplified model. These experiments will record velocity, position of parts, strain and accelerations. The parameters and the configurations necessary for the development of the mock-up, as well as the placement and quantity of sensors, are determined through extensive pre-calculations using both complex finite element models and the simplified approach. A key challenge involves precisely controlling the drop of the mock-up to accurately replicate the theoretical contact and damping conditions. Advanced sensor technologies will be employed to acquire reliable and sufficient data. The tests are designed and conducted at BAM's TTS drop test facility in collaboration with ASNR. T2 - PATRAM 2025 CY - San Antonio, TX, USA DA - 27.07.2025 KW - Experiments KW - Impact KW - Drop Tower PY - 2025 SP - 1 EP - 11 CY - Institute of Nuclear Materials Management (INMM) AN - OPUS4-63870 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quercetti, Thomas A1 - Feldkamp, Martin A1 - Gleim, Tobias A1 - Musolff, André A1 - Werner, Jan A1 - Wille, Frank T1 - Fire Test Stand for Thermal Testing of Large Packages for the Transport of Radioactive Materials N2 - Packages for the transport of high level radioactive materials are designed to withstand severe accidents. These packages must comply with the specific safety requirements SSR 6 [ of the International Atomic Energy Agency (IAEA). To guarantee compliance with these requirements, specific mechanical and thermal tests need to be addressed r egard ing the package type. Typically, the r egulations prescribe mechanical tests followed by a thermal test as part of a cumulative test scenario. The thermal test is specified by the exposure of a test specimen for a period of 30 minutes to a thermal environment that provides a heat flux equivalent to that of a hydrocarbon fuel air fire with an av erage fire temperature of at least 800 °C fully flame engulfing the test specimen. The Federal Institute for Materials Research and Testing (BAM) operates various test facilities for this purpose at their Test Site for Technical Safety (near Berlin in Germany). Thermal tests for large packages are conducted in an established fire test stand that may be adapted by the test setup to the geometric boundary conditions of a test specimen. This fire test stand is built for test specimens with masses up to 200,000 kg an d geometric dimensions relating to large transport packages including their impact limiters. The test specimen is usually placed on a water cooled support frame in the middle of the test stand. The fire is realized by burning propane gas which is released in liquid state from an array of gas nozzles arranged in the form of a burner ring surrounding the test specimen. For particularly extra large test specimens, two burner rings are used on top of each other and at different heights to firstly achieve full f ire engulfment with a significantly larger volume of fire and secondly to achieve the required heat output , cf. In advance of a regular thermal test BAM usually performs so called fire reference tests to determine the test conditions for compliance with the IAEA requirements. These tests are performed using a generic package which corresponds to the external geometr ic dimensions of the test specimen used later in the approval test. Then, this reference package is exposed to a fire under defined test parameters whereas the corresponding heat input determined from the temperature changes measured is regarded as main cr iterion for proofing compliance with the IAEA criteria. The paper shows the experimental proof of the suitability of BAM’s fire test stand for thermal testing of extra large packages. The heat input and fire temperatures fully meet the IAEA criteria and can also be set significantly higher for example for extra regulatory testing. T2 - PATRAM 2025 CY - San Antonio, TX, USA DA - 27.07.2025 KW - IAEA Regu-lations KW - Fire Test Stand KW - Accident Scenario KW - Fire Qualification PY - 2025 SP - 1 EP - 10 CY - Institute of Nuclear Materials Management (INMM) AN - OPUS4-63872 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Komann, Steffen A1 - Müller, Lars A1 - Neumann, Martin A1 - Wille, Frank T1 - Shipment of SCO-II – Authority assessment of mechanical aspects and quality management N2 - The decommissioning of nuclear facilities necessitates either the storage or disposal of large radioactive components such as steam generators, pressurizers, reactor pressure vessels and heads, or coolant pumps. These components or objects are large in size and mass with up to 6 meters in diameter and 20 meters in length and a weight of up to 400 tons. They are often transported to a storage, disposal, or recycling facility. Large components from nuclear facilities may often not be packed and need to be transported unpackaged due to size and weight. T2 - PATRAM 2025 CY - San Antonio, TX, USA DA - 27.07.2025 KW - radioaktive Stoffe, Rückbau kerntechnischer Anlagen, Transport, Gefahrgut PY - 2025 SP - 1 EP - 10 AN - OPUS4-63878 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Simbruner, Kai A1 - Völzke, Holger T1 - Analysis of Zirconium Hydride Structures in Spent Fuel Claddings Subjected to Storage Conditions N2 - Pre-storage drying and the early stage of storage can subject spent fuel claddings to higher temperatures and higher tensile hoop stresses than those associated with in-reactor operation. Under these conditions, existing circumferential hydrides in zirconium-based alloys can be partly reoriented into radial ones that may result in embrittlement of the cladding material. As a consequence, the failure limits may be reduced under mechanical loads caused by handling or during transport after storage. The potential occurrence of brittle fracture strongly depends on the specific location, size, and orientation of the zirconium hydrides. The morphology of such hydride structures was experimentally investigated in unirradiated, hydrogen-loaded samples made of a zirconium-based alloy. The hydrogen was introduced into the cladding sample by means of a cathodic charging process. The loading process was followed by a thermal treatment to precipitate the hydrides in the circumferential direction and then a thermomechanical treatment to reorient the hydrides in the radial direction. Metallographic methods were used to describe and classify the hydride morphology. The resulting metallographic micrographs were evaluated using suitable radial hydride metrics. The determination of the maximum length of a hydride structure was carried out in two different ways, each with its own advantages and disadvantages. Both methods consider neighboring hydrides as continuous according to the definition of the Radial Hydride Continuity Factor (RHCF). The first option is to measure the Euclidean distance between the two most distant pixels of the hydride structure in the image analysis, whereby the actual maximum size of the hydride structure is determined. The second possibility is to measure the maximum size of a hydride or a hydride structure within a certain arc length in the radial direction of the cladding tube. This value is of particular interest because the ratio of the maximum radial size of a hydride structure to the wall thickness of the cladding tube is used for the safety assessment of spent fuel claddings with radial hydrides using the RHCF. T2 - 21st International Symposium on the Packaging and Transportation of Radioactive Materials - PATRAM 2025 CY - San Antonio, TX, USA DA - 27.07.2025 KW - Extended Interim Storage KW - Nuclear Fuel Cladding KW - Zirconium Hydride Structure KW - Ring Compression Test KW - Micrograph Analysis PY - 2025 SP - 1 EP - 8 CY - Indianapolis, IN, USA AN - OPUS4-63875 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Popiela, Bartosz A1 - Schukar, Marcus A1 - Breithaupt, Mathias A1 - Günzel, Stephan A1 - Mair, Georg W. A1 - Krebber, Katerina A1 - Seidlitz, Holger T1 - Embedding of Fiber Optic Sensors Under Industrial Conditions and Distributed Strain Sensing in Type 4 Composite Pressure Vessels N2 - The number of in-operation composite pressure vessels is increasing, partly due to their attractiveness for on-board compressed gas storage and transport applications. A possible way to maintain the highest safety levels is through the structural health monitoring of the composite cylinders. Here, the use of fiber optic sensors appears to be a promising approach. However, the integration of the optical fibers into the composite structure of a pressure vessel has been shown to be challenging. In this study, insights on the embedding of optical fibers in the composite structure under industrial conditions are provided. A protection concept for the ingress and egress of the optical fibers is presented. Finally, the results from destructive slow burst tests are evaluated, showing no clear trend in the impact of the embedded optical fibers on the performance of composite pressure vessels. T2 - 24th International Conference on Composite Materials CY - Baltimore, Maryland, USA DA - 04.08.2025 KW - Composite KW - Pressure vessel KW - Filament winding KW - Fiber optic sensors PY - 2025 SP - 3710 EP - 3717 AN - OPUS4-63886 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Torge, Manfred A1 - Müller, Wolfgang A1 - Schaaf, U. T1 - Restaurierung von Holzfenstern KW - Restaurierung KW - Fenster PY - 2012 N1 - Sprachen: Deutsch/Polnisch - Languages: German/Polish IS - Faltblatt 9 SP - 1 EP - 8 PB - Druckhaus Köthen GmbH AN - OPUS4-26803 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Torge, Manfred A1 - Müller, Wolfgang A1 - Schaaf, U. T1 - Restaurierung von Holzfenstern KW - Restaurierung KW - Fenster PY - 2012 N1 - Sprachen: Deutsch/Polnisch - Languages: German/Polish IS - Faltblatt 8 SP - 1 EP - 8 PB - Druckhaus Köthen GmbH AN - OPUS4-26798 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Werner, Jan A1 - Brandt, S. T1 - Compatibility of high density polyethylene grades with bioethanol-gasoline blends and biodiesel N2 - Biofuels including ethanol and biodiesel (fatty acid methyl ester) represent an important renewable fuel alternative to petroleum-derived transport fuels. Increasing biofuels use would have some benefits, such as a reduction in oil demand and greenhouse gas emissions, and an improvement in air quality. Materials compatibility is a major concern whenever the fuel composition is changed in a fuel System. The aim of this work is to study the interaction between high density polyethylene (HDPE) grades and biofuels such as E85 (fuel with 85 % ethanol) and biodiesel. 10 I jerricans made of two different polyethylene grades were filled with E85 and biodiesel and exposed to temperatures of 20°C and 40°C for one year. Tensile properties (tensile strength, breaking elongation and elasticity modulus) were determined in accordance with EN ISO 527-2 at 23±2 °C once a month, and Fourier Transform Infrared Spectroscopy (FTIR) was used to evaluate possible changes. The tensile properties of HDPE jerrican cuttings decreased, but not significantly, after immersion in E85 and biodiesel. In particular, the elasticity modulus of the polyethylene grades was reduced after exposure to biodiesel. Pin impression tests according to EN ISO 16101 were performed with test specimens of a HDPE grade in White Spirit, E85 and biodiesel. Measurements of the remaining tensile strength showed that biofuels had a stronger effect than White Spirit. The FTIR spectra of HDPE jerrican cuttings showed that immersion tests for one year with E85 at 20°C and 40°C only caused an increase in the peak of 1585 cm'1 (C=C Stretching vibrations) in the Chemical structure of HDPE. The FTIR spectra of HDPE jerrican cuttings showed that immersion tests for one year with biodiesel at 20°C and 40°C led to a broadening of the C=O peak of 1740 cm'1 and the appearance of the hydroxyl group at 3500 cm'1. Both results are explained by secondary degradation products of the polyethylene decomposition process caused by the temperature and unsaturated fatty acid content in the biodiesel since biodiesel decomposes quickly at elevated temperatures. The broadening of the C=O peak to 1740 cm'1 can be attributed to aldehyde carbonyl and ester Carbonyl groups mutually overlapping. Measurements of the melt flow rate (MFR) showed an increase in the MFR with immersion time in biodiesel due to the unsaturated fatty acid formed in the biodiesel. Diffusions of oxygen and rapeseed methyl ester increase the Chemical impact on polyethylene grades. T2 - EUROCORR 2012 - The European corrosion congress CY - Istanbul, Turkey DA - 09.09.2012 PY - 2012 SP - 1 EP - 12 AN - OPUS4-26534 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wille, Frank A1 - Ballheimer, Viktor A1 - Rolle, Annette A1 - Droste, Bernhard T1 - Mechanical behaviour of high burn-up SNF under normal and accident transport conditions - present approaches and perspectives - N2 - Transport packages for spent fuel have to meet the International Atomic Energy Agency requirements for different transport conditions. Physical state of spent fuel and fuel rod cladding as well as geometric configuration of fuel assemblies are important inputs for the evaluation of package capabilities under these conditions. In this paper, the mechanical behaviour of high burn-up spent fuel assemblies under transport conditions is analysed with regard to assumptions to be used in the activity release and criticality safety analysis. In particular the different failure modes of the fuel rods (fine cracks or complete breakage), which can cause release of gas, volatiles, fuel particles or fragments have to be properly considered in these assumptions. In view of the complexity of interactions between the fuel rods as well as between fuel assemblies, basket, and cask containment, the exact mechanical analysis of such phenomena is nearly impossible. The gaps in information concerning the material properties of cladding and pellets, especially for the high burn-up fuel, make the analysis more complicated additionally. In this context some practical approaches based on experiences of BAM Federal Institute for Material Research and Testing within safety assessment of packages for transport of spent fuel are discussed. T2 - PSAM 11 ESREL 2012 - 11th International probabilistic safety assessment and management conference & The annual european safety and reliability conference CY - Helsinki, Finland DA - 25.06.2012 KW - Spent fuel KW - High burn-up KW - Transport conditions KW - Mechanical analysis PY - 2012 SP - 1 EP - 9 AN - OPUS4-33850 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Witt, Jens A1 - Schukar, Marcus A1 - Krebber, Katerina A1 - Demuth, J. A1 - Pazoutová, H. A1 - Sasek, L. A1 - Santostefano, N. A1 - Fiore, L. A1 - Uotila, J. A1 - Pietrowski, P. T1 - POF sensors for personal protective equipment (PPE) N2 - This paper reports about the EU project i-Protect in which fibre optic sensors for measuring heart rate, respiratory rate and skin temperature are being developed. The sensors and monitoring units are integrated into underwear and are communicating wireless via body area network and communication unit with the rescue command centre. All sensors can be removed from the underwear to allow washing the textile. T2 - POF 2012 - 21st International conference on plastic optical fibers CY - Atlanta, Georgia, USA DA - 10.09.2012 KW - Physiological sensor KW - Heart rate KW - Respiratory rate KW - Photoplethysmography KW - Technical textile PY - 2012 SP - 333 EP - 338 AN - OPUS4-27397 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Wilke, Olaf A1 - Wiegner, Katharina A1 - Jann, Oliver A1 - Brödner, Doris A1 - Scheffer, Harald T1 - Emissionsverhalten von Holz und Holzwerkstoffen (UBA-FB 001580) N2 - In diesem Vorhaben wurden 8 OSB-Platten und sieben Leimholzplatten aus Baumärkten gemäß den Vorgaben des AgBB-Schemas in Emissionsmesskammern geprüft. Hinzu kamen Messungen an 17 im Technikum hergestellten OSB, an denen der Einfluss von Herstellungsparametern auf VOCEmission untersucht wurde. Grundsätzliches Ziel war es, durch die Untersuchungen Lösungsansätze für die Emissionsminderung von VOC aus Holzwerkstoffen zu finden. Dazu wurde auch der Einsatz von Antioxidantien bei der OSB-Herstellung getestet. Die Emissionen des Rohstoffes Kiefernholz wurden an 6 Proben aus Splint- oder Kernholz aus unterschiedlichen Stammabschnitten einer frisch gefällten Kiefer untersucht. Insgesamt konnte mit dem Projekt gezeigt werden, dass einige der im Handel erhältlichen OSB und auch Leimhölzer eine Bewertung nach dem AgBB-Schema aufgrund von zu hohen Aldehyd- und Terpenemissionen nicht bestehen. Für die Aldehydemissionen (insbesondere Hexanal und ungesättigte höhere Aldehyde) konnte durch den Einsatz von Antioxidantien bei der OSB-Herstellung eine Verminderung auf ein Drittel erreicht werden, allerdings stiegen dadurch die Terpenemissionen an. In this project, eight Oriented Strand Boards (OSB) and seven plywood boards from DIY stores were tested in emission test chambers according to the AgBB scheme’s specifications. In addition, 17 OSBs manufactured in a pilot plant were tested to investigate the effect of production parameters on VOC emission. The use of antioxidants in OSB production was also tested. The main objective of the investigation was to find potential solutions for reducing VOC emissions from timber materials. The emissions from pine wood were investigated on six sapwood or heartwood samples from different trunk sections of freshly felled pine. The project’s results show that, due to their high aldehyde and terpene emissions, some types of commercially available OSB and plywood did not meet the AgBB scheme’s requirements. By using antioxidants in OSB production it was possible to reduce aldehyde emissions (especially hexanal and unsaturated higher aldehydes) to one third. However, this caused an increase in terpene emissions. KW - Bauprodukte KW - AgBB-Schema KW - Emissionsprüfkammern KW - Geruchsmessungen KW - VOC KW - VVOC KW - SVOC KW - Thermodesorption KW - GC/MS KW - Holzwerkstoffe KW - OSB KW - Leimholz KW - Construction products KW - AgBB Scheme KW - Emission test chamber KW - Odour measurement KW - Thermal desorption KW - Wood Products KW - Oriented Strand Board KW - Plywood Board PY - 2012 UR - http://www.umweltbundesamt.de/publikationen/emissionsverhalten-von-holz-holzwerkstoffen IS - 07 SP - 1 EP - 224 PB - Umweltbundesamt CY - Dessau-Roßlau AN - OPUS4-25843 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Feldkamp, Martin A1 - Gleim, Tobias A1 - Quercetti, Thomas A1 - Wille, Frank T1 - Evaluation of Convective Heat Transfer Coefficients with CFD for Heat Flux Calculation in Combustion Chamber N2 - Packages for the transport of high-level radioactive waste are designed to withstand severe accidents. To obtain approval for transport, these packages must adhere to the specification-based criteria of regulations established by the International Atomic Energy Agency (IAEA). To ensure compliance with the regulations, mechanical and thermal tests need to be conducted regarding the package type. The requirements define mechanical tests followed by a thermal test, including criteria ensuring the package design’s ability to withstand severe accidents. Heavy-weight packages for the safe transport of radioactive materials are equipped with impact limiters, which are often built with porous materials such as densely packed wood reinforced by steel sheet structures. These components absorb the kinetic energy during the impact of the package in drop tests and thus dampen the acceleration of other package components which supports the package to meet the requirements of the IAEA regulations. Following the mechanical tests, the package must, with its predamaged impact limiters, endure a thermal test defined precisely in the IAEA regulations. The thermal test is defined as a 30-min, fully engulfing 800 °C fire and a following time under ambient conditions for a sufficient period to ensure that temperatures in the specimen decrease in all parts of the specimen. During and following the thermal test, the specimen shall not be artificially cooled, and any combustion of materials of the specimen shall be permitted to proceed naturally. A wood-filled impact limiter can continue to release thermal energy during an ongoing combustion process, thus defining relevant package temperatures. Heat flux from a potentially burning impact limiter to the package is important for the safety evaluation of transport packages. A test setup was developed to approach the energy flow investigation and examine the combustion behaviour of porous materials encapsulated in predamaged cylindrical metal enclosures under various conditions. The setup consists of a combustion chamber for thermal tests under adjustable and defined boundary conditions. The temperature development of the test specimens can be observed from outside using a thermographic imager with high-definition cameras, and the mass loss of the test specimen can be measured in the combustion chamber. Convective heat transfer coefficients for various boundary conditions must be defined for use with experimentally gathered test specimen surface temperature data for heat flux evaluations. The airflow conditions in the combustion chamber were analysed using computational fluid dynamics (CFD) calculations in OpenFOAM with respect to the convective heat transfer coefficients at the surface of a hot test specimen. A convergence study was performed, and sensitivity analyses for different test specimen surface temperatures and exhaust gas volume flows were conducted. T2 - ASME PVP2025, Pressure Vessels & Piping Conference CY - Montreal, Quebec, Canada DA - 20.07.2025 KW - Heat Transfer KW - Convection KW - OpenFOAM KW - Combustion PY - 2025 SP - 1 EP - 7 PB - American society of mechanical engineers (ASME) AN - OPUS4-63901 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quercetti, Thomas A1 - Feldkamp, Martin A1 - Gleim, Tobias A1 - Musolff, Andre A1 - Werner, Jan A1 - Wille, Frank T1 - A fire test stand for thermal testing of extra-large packages N2 - Packages for the transport of high-level radioactive materials are designed to withstand severe accidents. These packages must adhere to the specification-based criteria of the International Transport Regulations of the International Atomic Energy Agency (IAEA). To ensure compliance with these requirements, specific mechanical and thermal tests need to be addressed with respect to the package type. Typically, the Regulations prescribe mechanical tests followed by a thermal test as part of a cumulative test scenario. The thermal test is specified by the exposure of a test specimen for a period of 30 minutes to a thermal invironment that provides a heat flux equivalent to that of a hydrocarbon fuel-air fire with an average fire temperature of at least 800 °C fully flame engulfing the test specimen. The Federal Institute for Materials Research and Testing (BAM) operates various test facilities for this purpose at their test site (TTS) near Berlin in Germany. Thermal tests for large packages are carried out in an established fire test stand that can be adapted by the test-setup to the geometric boundary conditions of a test specimen. This fire test stand is built for test specimens with masses up to 200,000 kg and geometric dimensions relating to large transport packages including their impact limiters. The test specimen is usually placed on a water-cooled support frame in the middle of the test-stand. The fire is realized by burning propane gas which is released in liquid state from an array of gas nozzles arranged in the form of a burner ring surrounding the test specimen. For particularly extra-large test specimens, two burner rings are used on top of each other and at different heights in order to firstly achieve full fire engulfment with a significantly larger volume of fire and secondly to achieve the required heat output. In advance of a regular thermal test BAM usually performs so-called fire reference tests to determine the test conditions for compliance with the IAEA requirements. These tests are performed using a generic package which corresponds to the external geometric dimensions of the test specimen used later in the approval test. Then, this reference package is exposed to a fire under defined test parameters whereas the corresponding heat input determined from the temperature changes measured is regarded as main criterion for proofing compliance with the IAEA criteria.The paper shows the experimental proof of the suitability of BAM’s fire test stand for thermal testing of extra-large packages. The heat input and fire temperatures fully meet the IAEA criteria but can also be set significantly higher for e.g. extra-regulatory testing. T2 - ASME PVP 2025 CY - Montreal, Quebec, Kanada DA - 20.07.2025 KW - Test stand KW - Thermal testing KW - Package KW - Fire PY - 2025 SP - 1 EP - 6 AN - OPUS4-63892 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mayer, Norbert A1 - Hofstötter, P. ED - Ficker, E. T1 - Einsatz elektrischer und mechanischer Meßverfahren zur Langzeitmessung N2 - Anhand von Anwendungsbeispielen werden mechanische und elektrische Verfahren für Langzeit- bzw. Überwachungsmessungen dagestellt. Nach der Beschreibung von Einsatzmöglichkeiten für Ritzdehnungsschreiber und Setzdehungsmesser werden Dehnungsmessungen mit Dehnungsmeßstreifen und kapazitiven Sensoren v. a. an Rohrleitungen behandelt. Im Zusammenhang mit dem Einsatz intelligenter Meßsysteme bzw. Monitoring-Systeme wird auf Fragen der automatisierten Auswertung und Datenreduktion eingegangen. T2 - GESA-Symposium CY - Schliersee, Deutschland DA - 1996-10-10 KW - Verformungsmessung KW - Dehnungsmessung KW - Langzeitmessung PY - 1996 N1 - Serientitel: GMA-Bericht – Series title: GMA-Bericht IS - 29 SP - 225 EP - 235 PB - VDI/VDE-Ges. Meß- und Automatisierungstechnik (GMA) CY - Düsseldorf AN - OPUS4-642 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schulz, Ulrich A1 - Trubiroha, Peter A1 - Zwick, W. ED - Roller, D. T1 - Environmental etch resistance of automotive coatings-predicted by the ADF-weathering test T2 - 30th International Symposium on Automotive Technology and Automation (ISATA) CY - Florence, Italy DA - 1997-06-16 KW - Lack KW - Fahrzeug KW - Bewitterung KW - Ätzen PY - 1996 PB - Automotive Automation Ltd. CY - Croydon AN - OPUS4-648 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Knabe, C. A1 - Gildenhaar, Renate A1 - Berger, R. A1 - Ostapowicz, W. A1 - Fitzner, R. A1 - Radlanski, R. A1 - Gross, U. A1 - Siebert, G. T1 - In vitro examination of novel calcium phosphates using osteogenic cultures T2 - 5th World Biomaterials Congress CY - Toronto, Canada DA - 1996-05-29 KW - In-vitro Untersuchung KW - Kalzium-Phosphat KW - Zahnersatz KW - Knochen PY - 1996 VL - 1 SP - 890 CY - Toronto AN - OPUS4-672 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Driessens, F. C. M. A1 - Boltong, M. G. A1 - Fernández, E. A1 - Ginebra, M. P. A1 - Planell, J. A. A1 - Verbeeck, R. M. H. A1 - De Maeyer, E. A. P. A1 - Berger, Georg T1 - Amorphous calcium phosphate cements T2 - 5th World Biomaterials Congress CY - Toronto, Canada DA - 1996-05-29 KW - Kalzium Phosphat Zement, amorph. PY - 1996 VL - 2 SP - 346 CY - Toronto AN - OPUS4-673 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reiners, Georg T1 - Standards for thin film technologies T2 - 5th International Symposium on Trends and New Applications in Thin Films ; TATF '96 CY - Colmar, France DA - 1996-04-01 KW - Normung KW - Dünnschichttechnologie PY - 1996 N1 - Serientitel: Le vide, les couches minces, Suppl. – Series title: Le vide, les couches minces, Suppl. VL - 279 IS - 179 SP - 1 EP - 23 PB - sfv CY - Paris AN - OPUS4-635 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Schöne, Dieter A1 - Neikes, F. W. T1 - Largest dynamic test system performance enhanced with modern digital controls and software KW - Steuerung, digital KW - Prüfen, automatisch KW - Servohydraulik PY - 1996 SP - 1 EP - 7 PB - MTS Systems Corp. CY - Minnesota AN - OPUS4-664 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Frenz, Holger A1 - Kinder, Joachim A1 - Klingelhöffer, Hellmuth A1 - Portella, Pedro Dolabella T1 - Microstructural evolution and fracture mechanisms of single crystal superalloys under cyclic loading at high temperatures T2 - 17. Tagung des DVM-Arbeitskreises Rastermikroskopie in der Materialprüfung CY - Halle (Saale), Deutschland DA - 1996-03-27 KW - Einkristall KW - Superlegierung KW - Hochtemperatur PY - 1996 N1 - Serientitel: Tagung des DVM-Arbeitskreises Rastermikroskopie in der Materialprüfung – Series title: Tagung des DVM-Arbeitskreises Rastermikroskopie in der Materialprüfung IS - 17 SP - 275 EP - 280 PB - DVM, Geschäftsstelle CY - Berlin AN - OPUS4-665 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krause, Martin A1 - Maierhofer, Christiane A1 - Ewert, Uwe T1 - Prüfung von bewehrtem Beton mit Radar, Ultraschall-Impulsecho und Durchstrahlverfahren (Erweitertes Abstract) T2 - Erstes franz.-dt. Seminar für zerstörungsfreie Prüfung CY - Metz, Frankreich DA - 1995-10-12 KW - Beton, bewehrt KW - Prüfung KW - Radar KW - Ultraschall-Impulsecho KW - Durchstrahlungsverfahren PY - 1995 CY - Metz AN - OPUS4-594 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mosel, Günter A1 - Unger, Brita A1 - Hähnert, Manfred T1 - Zn-K EXAFS investigations of sol-gel derived ZnO-SiO2 powders KW - Zink KW - Erde PY - 1995 SP - 603 EP - 604 PB - Hamburger Synchrotonstrahlungslabor CY - Hamburg AN - OPUS4-599 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mosel, Günter A1 - Nofz, Marianne T1 - Zn-K EXAFS investigations of zinc aluminosilicate glasses and ZnO-doped calcium aluminosilicate glasses KW - Zink KW - Glas PY - 1995 SP - 615 PB - Hamburger Synchrotronstrahlungslabor CY - Hamburg AN - OPUS4-600 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mosel, Günter A1 - Hübert, Thomas T1 - EXAFS investigation of an intermediate crystalline phase in TiO2-rich strontium borate glasses KW - Glas KW - EXAFS PY - 1995 SP - 605 EP - 606 PB - Hamburger Synchrotronstrahlungslabor CY - Hamburg AN - OPUS4-601 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Trubiroha, Peter T1 - Grundlagen der Alterung durch Witterungseinwirkung T2 - Bewitterung von Kunststoffen - Fachtagung CY - Würzburg DA - 1995-11-08 KW - Alterung KW - Witterungseinwirkung KW - Prüfverfahren PY - 1995 SP - A-2-A-16 CY - Würzburg AN - OPUS4-608 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Banach, Ulrich A1 - Steinborn, Gabriele A1 - Hübert, Thomas A1 - Willfahrt, Manfred T1 - Dotierte Strontiumtitanat-Keramiken hergestellt nach dem Gelcasting-Verfahren T2 - DKG Jahrestagung CY - Aachen, Deutschland DA - 1995-01-01 KW - Keramik KW - Gußverfahren KW - Hochleistungskeramik KW - Eigenschaft, elektrisch PY - 1995 SP - 187 EP - 189 CY - Aachen AN - OPUS4-609 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gogolin, Bernd A1 - Droste, Bernhard A1 - Quercetti, Thomas T1 - Drop-test program with the German "POLLUX" cask for final disposal of spent fuel T2 - PATRAM ´95 - 11th International Conference on the packaging and transportation of radioactive materials CY - Las Vegas, Nevada, USA DA - 1995-12-03 KW - Container KW - Brennelement KW - Endlagerung KW - Abfall, radioaktiv PY - 1995 VL - 1 SP - 159 EP - 166 AN - OPUS4-610 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rödel, Roland A1 - Droste, Bernhard A1 - Buhlemann, Lothar A1 - Hübner, Heinz W. T1 - Compliance assurance aspects for Type-A and industrial packages T2 - PATRAM ´95 - 11th International Conference on the packaging and transportation of radioactive materials CY - Las Vegas, Nevada, USA DA - 1995-12-03 KW - Verpackung PY - 1995 VL - 1 SP - 294 EP - 298 AN - OPUS4-611 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Forkel, K. A1 - Kosslick, H. A1 - Lippitz, Andreas A1 - Rolle, S. ED - Dufour, L.-C. T1 - Investigation of thermal properties of Fe75Cr5P8C10Si2 metal-metalloid glassy T2 - XIIIth International Symposium ; 13th International Symposium on the Reactivity of Solids CY - Hamburg, Germany DA - 1996-09-08 KW - Glasoberfläche KW - Beanspruchung, thermisch PY - 1996 PB - North-Holland CY - Amsterdam AN - OPUS4-686 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Strehlow, P. A1 - Banach, Ulrich A1 - Hübert, Thomas T1 - Keramische Tieftemperatursensoren KW - Tieftemperatursensor KW - Keramik KW - Sensor PY - 1996 VL - 1995 SP - 274 EP - 275 CY - Braunschweig AN - OPUS4-691 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zeisler, Peter A1 - Droste, Bernhard A1 - Rödel, Roland A1 - Rehmer, Birgit T1 - Current approval procedures for type-B packages in Germany: Overview T2 - PATRAM ´95 - 11th International Conference on the packaging and transportation of radioactive materials CY - Las Vegas, Nevada, USA DA - 1995-12-03 KW - Gefahrgutumschließung KW - Zertifizierung PY - 1995 VL - 1 SP - 496 EP - 503 AN - OPUS4-613 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völzke, Holger A1 - Droste, Bernhard A1 - Wieser, Günter A1 - Gogolin, Bernd T1 - Extended brittle fracture safety demonstrations of cubic ductile cast iron containers T2 - PATRAM ´95 - 11th International Conference on the packaging and transportation of radioactive materials CY - Las Vegas, Nevada, USA DA - 1995-12-03 KW - Container KW - Sprödbruch PY - 1995 VL - 3 SP - 1356 EP - 1363 AN - OPUS4-614 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kowalewsky, Helmut T1 - Modeling contents and leaks - advantages and limitations T2 - PATRAM ´95 - 11th International Conference on the packaging and transportation of radioactive materials CY - Las Vegas, Nevada, USA DA - 1995-12-03 KW - Simulation PY - 1995 VL - 3 SP - 1783 EP - 1790 AN - OPUS4-615 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quercetti, Thomas A1 - Gogolin, Bernd A1 - Droste, Bernhard T1 - Integrity of the "POLLUX" cask for final disposal: Experimental results of the mechanical tests T2 - PATRAM ´95 - 11th International Conference on the packaging and transportation of radioactive materials CY - Las Vegas, Nevada, USA DA - 1995-12-03 KW - Container KW - Gefahrgutumschließung KW - Integrität PY - 1995 VL - 3 SP - 1091 EP - 1098 AN - OPUS4-616 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hünecke, Joachim A1 - Schöne, Dieter A1 - Bomas, H. A1 - Laue, S. T1 - Anrisslebensdauervorhersage am Beispiel glatter und gekerbter Proben des Werkstoffes Cm15 T2 - Kolloquium "Mechanismenorientierte Lebensdauervorhersage für zyklisch beanspruchte metallische Werkstoffe" CY - Bremen, Deutschland DA - 2000-02-24 KW - Probenfertigung KW - Rissdatengewinnung PY - 2000 N1 - Serientitel: DVM-Bericht – Series title: DVM-Bericht IS - 683 SP - 65 EP - 80 PB - Deutscher Verband für Materialforschung und -prüfung CY - Berlin AN - OPUS4-806 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Procop, Mathias T1 - Instrumental Specification for Semiconductor X-ray Detectors and their check in an Analytical Laboratory PY - 1999 VL - 20 IS - 1 SP - 96 EP - 103 PB - Società Italiana di Microscopia Elettronica CY - Modena AN - OPUS4-835 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erhard, Anton A1 - Schenk, Gottfried A1 - Hauser, Th. A1 - Völz, Uwe ED - Roos, E. T1 - Anwendungsmöglichkeiten der Gruppenstrahlertechnik T2 - 25th MPA-seminar CY - Stuttgart, Germany DA - 1999-10-07 KW - Gruppenstrahlertechnik PY - 1999 VL - 206 IS - 2-3 SP - 25.1 EP - 25.10 PB - North-Holland CY - Amsterdam AN - OPUS4-796 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Unger, Wolfgang T1 - The application of X-ray Photoelectron Spectroscopy (ESCA) and X-Ray Absorption Spectroscopy (NEXAFS) in Interface Analysis of Metallized Polymers T2 - Summer Workshop "Functionalized Surfaces: Applications and Analytical Tools" CY - Zurich, Switzerland DA - 1999-07-05 KW - ESCA KW - NEXAFS PY - 1999 SP - F1 EP - F12 AN - OPUS4-797 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Ralf A1 - Weh, Lothar A1 - Reinsch, Stefan T1 - Oberflächenprofile partiell kristallisierter Silikatgläser T2 - 73. Glastechnische Tagung CY - Halle (Saale), Deutschland DA - 1999-05-31 KW - Kristallisation KW - Silikatgläser PY - 1999 SP - 26 EP - 29 CY - Frankfurt/Main AN - OPUS4-819 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Jaenisch, Gerd-Rüdiger A1 - Vengrinovich, V. T1 - Optimal processing of the information available from NDE measured data T2 - 15th World Conference on Non-Destructive Testing (WCNDT) CY - Roma, Italy DA - 2000-10-15 KW - NDE data processing KW - Inverse problems KW - Bayesian restoration KW - Data fusion PY - 2000 UR - http://www.ndt.net/article/wcndt00/papers/idn429/idn429.htm SN - 1435-4934 N1 - Geburtsname von Jaenisch, Gerd-Rüdiger: Tillack, G.-R. - Birth name of Jaenisch, Gerd-Rüdiger: Tillack, G.-R. VL - 5 IS - 11 SP - 1(?) EP - 8(?) PB - NDT.net CY - Kirchwald AN - OPUS4-860 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reiners, Georg T1 - Standardization in Surface Technologies - Role of BAM PY - 2000 AN - OPUS4-861 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Goebbels, Jürgen T1 - Computed Tomography in NDT of Materials PY - 2000 SP - 1(?) EP - 9(?) PB - Pergamon Press CY - Amsterdam AN - OPUS4-844 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rückert, Joachim A1 - Isecke, Bernd A1 - Zietelmann, Christina T1 - Gebrauchssicherheit von Kochgerät aus Edelstahl - Elektrochemische Messungen zur Nickelabgabe an Lebensmittel (Teil 2) KW - Kochversuche KW - Nickelabgabe an Lebensmittel KW - Chromabgabe an Lebensmittel KW - Chrom-Nickel-Stahl PY - 1999 IS - 246 SP - 1 EP - 26 CY - Düsseldorf AN - OPUS4-787 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böhning, Martin A1 - Robertson, Daniela A1 - Schröder, Hartmut T1 - Autoclave testing: a new approach for the evaluation of oxidative long-term resistance of geosynthetics N2 - Oxidative long time resistance is essential for many polyolefin based products, especially if repair or exchange is not possible as encountered in many building and geotechnical applications. Current regulations and recommendations for geosynthetics cover mainly the needs of a maximum lifetime of 25 years, though many applications require longer lifetimes up to 100 years and more. Reliable testing of the long time oxidation resistance is complicated by the complex interplay of physicochemical processes and reactions in combination with the need of relatively short testing durations, usually not exceeding 12 months. Thus for conventional atmospheric oven testing, the use of temperatures higher than 100 °C is inevitable, making conclusive Arrhenius extrapolations often questionable. Practical assessments of oxidative durability consist of exposures under accelerated ageing conditions with subsequent characterization of exposed material samples with respect to their residual stabilization and/or their mechanical properties. The autoclave test combines exposures at elevated temperatures with higher oxygen pressures and is performed with material samples immersed in a well defined aqueous medium representing critical environments in geosynthetic applications and including extraction of additives. Under these conditions meaningful results can be obtained within reasonable testing durations at only moderately elevated temperatures up to 80 °C. Application of different physicochemical methods, such as tensile testing, OIT /HP-OIT and analysis of residual antioxidant content (ICOT), in order to determine the time dependent degradation behaviour, reveal valuable information about mechanisms and effectiveness of the used antioxidants. Corresponding results for exposures at different temperatures and oxygen pressures are the basis for a 3D-extrapolation in order to estimate the expected service life. Different empirical models are presented and discussed with respect to their practical impact. T2 - EuroGeo4, 4th European Geosynthetics Conference CY - Edinburgh, UK DA - 2008-09-07 KW - Ageing KW - Degradation KW - Geotextiles KW - Polyolefin KW - Polypropylene KW - Oxidative resistance KW - Lifetime prediction PY - 2008 IS - Paper 143 SP - 1 EP - 8 AN - OPUS4-18424 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heuchel, M. A1 - Hölck, Ole A1 - Böhning, Martin A1 - Siegert, R. A1 - Hofmann, D. ED - Qi, Y. ED - H.E. Fang, ED - N. Reynolds, ED - Liu, Z.-K. T1 - Knowledge-based approach to gas sorption in glassy polymers by combining experimental and molecular simulation techniques N2 - We present a method which allows to calculate gas sorption in complex polymers where, as slow processes, gas induced plasticization and volume dilation are important factors. Since the relaxational swelling of the polymer matrix that is observed at elevated gas concentrations takes hours or days, the swelling process is orders of magnitudes too slow to simulate the respective molecular dynamics in reasonable time and effort. To address this apparent incompatibility of experiment and simulation, we use single representative reference states from experiment and construct atomistic packing models according to these specifications. Gas sorption of CO2 and CH4 was successfully calculated on polysulfone, a 6FDA-polyimide, and a polymer of intrinsic microporosity, PIM-1, at 308 K and pressures up to 50 bar. T2 - MRS Fall Meeting 2008 - Symposium W - Computational Materials Design via Multiscale Modeling CY - Boston, MA, USA DA - 2008-12-01 KW - Gas sorption KW - Molecular modelling KW - Simulation KW - Glassy polymers PY - 2009 DO - https://doi.org/10.1557/PROC-1130-W06-10 VL - 1130 SP - W06 EP - W10 AN - OPUS4-19106 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Kern, Simon A1 - Liehr, Sascha A1 - Wander, Lukas A1 - Bornemann-Pfeiffer, Martin A1 - Müller, S. A1 - Maiwald, Michael A1 - Kowarik, Stefan T1 - Training data of quantitative online NMR spectroscopy for artificial neural networks N2 - Data set of low-field NMR spectra of continuous synthesis of nitro-4’-methyldiphenylamine (MNDPA). 1H spectra (43 MHz) were recorded as single scans. Two different approaches for the generation of artificial neural networks training data for the prediction of reactant concentrations were used: (i) Training data based on combinations of measured pure component spectra and (ii) Training data based on a spectral model. Synthetic low-field NMR spectra First 4 columns in MAT-files represent component areas of each reactant within the synthetic mixture spectrum. Xi (“pure component spectra dataset”) Xii (“spectral model dataset”) Experimental low-field NMR spectra from MNDPA-Synthesis This data set represents low-field NMR-spectra recorded during continuous synthesis of nitro-4’-methyldiphenylamine (MNDPA). Reference values from high-field NMR results are included. KW - NMR spectroscopy KW - Real-time process monitoring KW - Artificial neural networks KW - Online NMR spectroscopy KW - Automation KW - Process industry PY - 2020 DO - https://doi.org/10.5281/zenodo.3677139 PB - Zenodo CY - Geneva AN - OPUS4-50456 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Even, Morgane A1 - Juritsch, Elevtheria A1 - Richter, Matthias T1 - Weiterentwicklung und Validierung eines leistungsfähigen Verfahrens zur Bestimmung von leicht flüchtigen organischen Verbindungen (VVOC) bei Emissionsmessungen aus Bauprodukten und in der Innenraumluft N2 - Ziel dieses Forschungsprojekts war es, eine leistungsfähige Gesamtstrategie zur Bestimmung von leicht flüchtigen organischen Verbindungen (VVOC) auf Grundlage der Prüfmethode aus ISO 16000-6 in Verbindung mit EN 16516 vorzuschlagen. Es soll bei Emissionsmessungen sowohl aus Bauprodukten als auch in der Innenraumluft angewendet werden können und ein großes Emissionsspektrum abdecken, um möglichst wenige Einzelprüfungen durchführen zu müssen. Als Gegenstand für sämtliche Untersuchungen diente ein 60-komponentiger Testgasstandard. Mit dessen Hilfe erfolgten dann schließlich systematische Eignungsuntersuchungen für Chromatographiesäulen und Adsorbenzien für die Probenahme, die Untersuchung der Einflüsse von Luftfeuchtigkeit, Probenahmevolumen und -volumenstrom auf die Analyse, Untersuchungen zum Umgang mit Feuchtigkeit in der Probenluft, die Bestimmung von Wiederfindungsraten, Nachweis- und Bestimmungsgrenzen sowie der Robustheit des Verfahrens und der Messunsicherheit im Rahmen der Verfahrensvalidierung. Die entwickelte Messmethode wurde im Rahmen einer Emissionsmessung an einem Polyurethanschaum erprobt. Im Ergebnis entstand eine robuste Methode, die es erlaubt, komplexe VVOC-Gemische mit sehr guter Auflösung und niedrigen Nachweis- und Bestimmungsgrenzen zu analysieren. Ferner wurde ein Vorschlag zur Erweiterung des zu erfassenden Flüchtigkeitsspektrums bis C22 erarbeitet, der zwar nicht vollständig validiert werden konnte, jedoch die prinzipielle Machbarkeit zeigt. KW - VVOC KW - Thermodesorptions-GC/MS KW - Bauproduktemission KW - Innenraumluftqualität PY - 2024 UR - https://www.umweltbundesamt.de/publikationen/weiterentwicklung-validierung-eines SN - 1862-4804 VL - 131/2024 SP - 1 EP - 154 PB - Umweltbundesamt CY - Dessau-Roßlau AN - OPUS4-61147 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Liehr, Sascha T1 - ANNforPAT - Artificial Neural Networks for Process Analytical Technology N2 - This code accompanies the paper "Artificial neural networks for quantitative online NMR spectroscopy" published in Analytical and Bioanalytical Chemistry (2020). KW - Artificial neural networks KW - Automation KW - Online NMR spectroscopy KW - Process industry KW - Real-time process monitoring PY - 2020 UR - https://github.com/BAMresearch/ANNforPAT PB - GitHub CY - San Francisco AN - OPUS4-54481 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT ED - Tuma, Dirk ED - Weide, T. ED - Rasmusson, H. T1 - MefHySto - Metrology for advanced hydrogen storage solutions N2 - The “Metrology for Advanced Hydrogen Storage Solutions” (MefHySto) project is a European initiative addressing the need for large-scale energy storage solutions, that is crucial for the successful transition to renewable energy sources. The main objective of this project was to develop and provide metrological standards and validated techniques for the storage and utilization of hydrogen. Hydrogen is increasingly recognized as an important component in the future energy system due to its ability to store and supply energy during peak demand periods when renewable sources, such as solar and wind, are not generating power. KW - Water electrolysis KW - Thermophysical properties KW - Fuel cell KW - Hydrogen storage PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-625952 DO - https://doi.org/10.5281/zenodo.12684898 SP - 1 EP - 40 PB - ERIG European Research Institute for Gas and Energy Innovation a.i.s.b.l. CY - Bruxelles AN - OPUS4-62595 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Klinke, A. A1 - Horn, Wolfgang A1 - Kalbe, Ute A1 - Mönig, J. A1 - Richter, Matthias A1 - Roswag-Klinge, E. A1 - Röhlen, U. A1 - Ziegert, C. T1 - Upcycling mineralischer Bau- und Abbruchabfälle (upMIN 100) N2 - Der Bausektor ist einer der ressourcenintensivsten Sektoren in Deutschland und ist für 40 % der CO2-Emissionen verantwortlich. Für den Bau von Gebäuden werden in Deutschland jährlich rund 517 Millionen Tonnen mineralische Rohstoffe benötigt. Gleichzeitig stellen mineralische Bauabfälle mit 229,3 Millionen Tonnen (2020) den größten Stoffstrom dar. Die Quoten des Baustoffrecyclings sind seit 2000 gestiegen, insbesondere bei mineralischen Abfällen. Dennoch wird der Großteil der recycelten Gesteinskörnungen in technisch weitgehend ungeregelten Anwendungen (z.B. Straßenbau) eingesetzt. Durch dieses Downcycling gehen wertvolle Ressourcen für technisch und wirtschaftlich wertvolle Anwendungen verloren. Das Forschungsprojekt upMIN100 geht der Frage nach, ob und inwieweit sich rezyklierte mineralische Bau- und Abbruchabfälle als Zusatzstoff in Lehmbaustoffen wie Lehmputzen und Lehmsteinen eignen. Der Fokus liegt dabei auf der Korngröße < 2 mm, die derzeit überwiegend deponiert wird, da es derzeit keine Vorschriften für den Einsatz in Bauprodukten gibt. Um den Einsatz von Bau- und Abbruchabfällen zu ermöglichen, müssen die technische Machbarkeit sichergestellt, Qualitätsanforderungen an die Ausgangsmaterialien (z.B. Grenzwerte für gesundheits- und umweltrelevante Schadstoffe und gefährliche Substanzen) und zulässige Anteile an rezyklierten Gesteinskörnungen definiert werden. Um negative Auswirkungen auf die Gebäudenutzer zu vermeiden, wurden die entwickelten Baumaterialien auf die in den mineralischen Abfällen enthaltenen Schadstoffe sowie auf Emissionen in die Innenraumluft geprüft. Außerdem sollen die aus mineralischen Abfällen hergestellten Lehmbauprodukte frei von Schadstoffen sein, um eine Rückführung in die Umwelt zu ermöglichen. Nach der Ersatzbaustoffverordnung (EBV) entspricht dies dem Kriterium BM-0. KW - Mineralische Baustoffe KW - Baustoffrecycling KW - Lehmbaustoffe PY - 2024 SN - 1868-0097 SP - 1 EP - 150 AN - OPUS4-61820 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - von Preetzmann, N. A1 - Eckmann, P. A1 - Tuma, Dirk A1 - Richter, M. T1 - Thermodynamics of LNG N2 - Densities of eight gravimetrically prepared ternary and quaternary gas mixtures consisting of methane, ethane, propane, and partially nitrogen were investigated along the four isotherms of –250, –230, –210, and –190 °F at pressures of 350, 500, 650, and 1000 psig using a cryogenic single-sinker densimeter. The experimental densities were compared to densities calculated by various models, namely the EOS-LNG fundamental Helmholtz equation of state, the COSTALD correlation, the Lee-Kessler-Plöcker equation of state, and the Peng-Robinson equation of state. The best performance was shown by the EOS-LNG equation of state which is capable of predicting the liquid densities within the specified uncertainty of the model of 0.05 %. The other models, however, showed significant differences that disqualify for calculation within the p,T-region investigated of the gas mixtures. KW - Density measurement KW - Liquefied natural gas-like mixtures KW - Cryogenic state KW - Single-sinker densimeter KW - Equations of state PY - 2020 SP - 1 EP - 55 AN - OPUS4-50741 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Horn, Wolfgang A1 - Wilke, Olaf A1 - Richter, Matthias T1 - Round robin tests of odour and VOC emissions from building products – What have we learned so far? N2 - Emission testing of volatile organic compounds (VOC) and odour from materials and products is commonly based on emission test chamber measurements. These measurements are often the basis of mandatory or voluntary labelling procedures. To ensure the comparability of results from different testing laboratories their performance must be verified. For this purpose, round robin tests (RRTs) are conducted. Bundesanstalt für Materialforschung und - prüfung (BAM) offers such a RRT every two years using well characterised test materials with defined VOC emissions. In addition to the VOC quantification, the evaluation of odour is also implemented in the round robin tests. At the beginning, only perceived intensity (PI) was tested but over the years also the acceptance evaluation was considered. In principle, the results of PI and acceptance evaluation are comparable. The advantage of PI is the lower number of panel members necessary for one evaluation. T2 - Healthy Buildings 2023 Europe CY - Aachen, Germany DA - 11.06.2023 KW - Perceived intensity KW - VOC-emission KW - Poficiency test KW - Chamber test KW - Odour PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-580001 SP - 434 EP - 436 PB - ISIAQ (International Society of Indoor Air Quality and Climate) CY - Herndon, VA, USA AN - OPUS4-58000 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Liao, Chun-Man A1 - Bernauer, F. A1 - Igel, H. A1 - Hadziioannou, C. A1 - Niederleithinger, Ernst T1 - Real-time bridge monitoring using ultrasonic techniques combined with six-component (6-C) measurements N2 - This study aims to develop a real time structural health monitoring method by ultrasonic tests combined with advanced six component (6C) translation and rotation measurements. Conventionally, the investigation of the velocity and acceleration response in the translation direction is used to obtain the eigenfrequencies of structures. Recently the measurement of rotation has been considered to fully characterize the dynamic behavior of structures. This research undertakes the evaluation of a novel 6C sensor (IMU50-iXblue) with components originally developed for navigation for the purpose of bridge monitoring. However, as for all vibration recordings, there is a certain influence of environmental conditions (mainly temperature) which may affect evaluation and the results of structural assessment. We propose applying the cross-correlation function to the 6C ambient vibration signals to reconstruct wave propagation and using coda wave interferometry (CWI) to obtain internal velocity variation from waveforms. A field experiment on a large-scale prestressed concrete bridge model is presented. To verify that we are able to identify the pre-stress loss even in presence of temperature effects, we perform measurements in two different scales: the ultrasonic and output-only, vibration measurements. The change in the structural properties due to the pre-stress loss should be detected by the pulse velocity change. The results reveal both the performance and advantages of ultrasonic techniques and the capabilities of 6C sensors. To conclude, the application of CWI to wave signals contributes to a comprehensive assessment for bridge monitoring. T2 - NDT-CE 2022 CY - Zurich, Switzerland DA - 16.08.2022 KW - Structural health monitoring KW - Ultrasonic KW - Coda wave interferometry PY - 2022 SP - 1 EP - 10 AN - OPUS4-55660 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Strangfeld, Christoph A1 - Hindersmann, I. A1 - Niederleithinger, Ernst T1 - Smart Bridge The duraBASt test bridge equipped with RFID-based sensors N2 - The duraBASt area at the highway intersection “Köln-Ost” is a large test field for road testing. It includes the duraBASt test bridge which is approximately 66 m long and 14.25 m broad. This bridge is part of the “road in the 21st Century” project and is equipped with several sensors for structural health monitoring. This feasibility study is carried out to investigate the prerequisites necessary for the constraction of intelligent bridges in the foture. Embedded sensors are able to measure quantities such as temperature, strain, moisture, corrosion, etc. In the presented work, the focus is set on passive RFID-based sensors. The communication and energy supply are realised by a mobile transmitter through the concrete cover. Hence, no cables or batteries are required. The sensors are designed to withstand the alkaline environment in concrete. Thus, moisture and corrosion values are measurable for several decades. T2 - 10th International Conference on Bridge Maintenance, Safety and Management CY - Online meeting DA - 11.04.2021 KW - RFID based sensors KW - Embedded sensors KW - Bridge Monitoring PY - 2021 DO - https://doi.org/10.1201/9780429279119-321 VL - 2021 SP - 2353 EP - 2358 PB - Taylor & Francis Group CY - London AN - OPUS4-53816 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Üstündag, Ömer A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Thermal Cycles and Charpy Impact Toughness of Single-Pass Hybrid Laser-Arc Welded Thick-Walled Structures N2 - The study deals with the influence of the heat input on the thermal cycles and Charpy impact toughness for hybrid laser-arc welding of 25 mm thick structural steel S355J2 using a 20-kW high-power laser in combination with an electromagnetic weld pool support. The main focus is on the change of the mechanical properties over the entire seam thickness. The cooling times were measured using a pyrometer in combination with an optical fibre in three different locations near to fusion lines corresponding to different heights of the seam. Also, Charpy impact specimens were taken from different parts of the weld joint corresponding to the different heights. The influence of the heat input was investigated for 1.8 kJ mm-1 and 3.2 kJ mm-1. Despite the observed decreased values of both t8/5-cooling time and the Charpy impact toughness in the root part of the seam, the required values could be reached in dependance on applied heat input. T2 - Lasers in Manufacturing Conference 2021 CY - Online meeting DA - 21.06.2021 KW - laser hybrid welding KW - Charpy impact toughness KW - thick plate welding KW - thermal cycles PY - 2021 SP - 1 EP - 8 AN - OPUS4-53926 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Epple, Niklas A1 - Fontoura Barroso, Daniel A1 - Hau, Julia A1 - Niederleithinger, Ernst ED - Cunha, A. ED - Caetano, E. T1 - Accounting for Long Term Environmental Influences on Ultrasonic Monitoring Measurements of Reinforced Concrete Constructions with Embedded Transducers N2 - Ultrasound measurements in concrete are a well-known technique in civil engineering and non-destructive testing. For consistent monitoring of a concrete structure, the common techniques, using external sensors can often not provide the appropriate degree of repeatability, as the surface of structures changes, and comparable coupling conditions cannot be guaranteed when a measurement is repeated after some time. By embedding ultrasound transducers in concrete, we aim to develop a strategy for long-term monitoring of infrastructure, especially bridges, as a supplement and extension to other techniques. Applying the so-called coda wave interferometry to these measurements we can detect subtle changes in the medium far beyond the Resolution limit of traditional time of flight methods. A smart sensor layout enables cost-efficient sensing of the entire area of interest. Embedding the transducers might remove uncertainties like coupling or positioning changes, while other challenges remain. Temperature and moisture content influence the structure and the transducers. These drifts need to be recorded and removed and good coupling must be ensured while not being able to visually inspect the sensor. In a multidisciplinary research group funded by the German Research Foundation, we aim to solve these problems on the way towards an ultrasound monitoring system for reinforced concrete structures. In various experiments in the lab and field, we determine the influence of temperature variations on the measurements and the equipment. As the monitoring task is the detection of irreversible damages - not reversible changes - a smart system requires a smart way of discrimination between permanent damages and reversible changes. With the data collected in these experiments, we present an approach to an environmental correction to ultrasound data to avoid a misinterpretation of these environmental changes as damage indicators. T2 - 10th International Conference on Structural Health Monitoring of Intelligent Infrastructure CY - Porto, Portugal DA - 30.06.2021 KW - Ultrasound KW - Coda Wave Interferometry (CWI) KW - Structural Health Monitoring KW - Embedded Sensors PY - 2021 SP - 1 EP - 7 AN - OPUS4-54007 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Straße, Anne A1 - Gumenyuk, Andrey A1 - Scheuschner, Nils A1 - Altenburg, Simon A1 - Pignatelli, Giuseppe A1 - Gornushkin, Igor B. A1 - Baensch, Franziska A1 - Rethmeier, Michael T1 - In-situ Prozessüberwachung beim Laser-Pulver-Auftragschweißen (LPA) mittels Thermografie, optischer Emissionsspektroskopie (OES) und Schallemissionsanalyse (SEA) N2 - Vor allem in den letzten Jahren ist das Interesse der Industrie an der additiven Fertigung deutlich gestiegen. Die Vorteile dieser Verfahren sind zahlreich und ermöglichen eine ressourcenschonende, kundenorientierte Fertigung von Bauteilen, welche zur stetigen Entwicklung neue Anwendungsbereiche und Werkstoffe führen. Aufgrund der steigenden Anwendungsfälle, nimmt auch der Wunsch nach Betriebssicherheit unabhängig von anschließenden kostenintensiven zerstörenden und zerstörungsfreien Prüfverfahren zu. Zu diesem Zweck werden im Rahmen des von der BAM durchgeführten Themenfeldprojektes „Prozessmonitoring in Additive Manufacturing“ verschiedenste Verfahren auf ihre Tauglichkeit für den in-situ Einsatz bei der Prozessüberwachung in der additiven Fertigung untersucht. Hier werden drei dieser in-situ Verfahren, die Thermografie, die optische Emissionsspektroskopie und die Schallmissionsanalyse für den Einsatz beim Laser-Pulver-Auftragschweißen betrachtet. T2 - 41. Assistentenseminar der Füge- und Schweißtechnik CY - Magdeburg, Germany DA - 02.09.2020 KW - Laser-Pulver-Auftragschweißen (LPA) KW - Thermographie KW - Optische Emissionsspektroskopie (OES) KW - Schallemissionsanalyse (SEA) PY - 2021 SN - 978-3-96144-141-9 VL - 370 SP - 132 EP - 140 PB - DVS MEdia CY - Düsseldorf AN - OPUS4-53967 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Winterkorn, René A1 - Pittner, Andreas A1 - Rethmeier, Michael T1 - Lichtbogenbasierte additive Fertigung dickwandiger Strukturen aus einer höherfesten Al-Mg-Si-Aluminiumlegierungen N2 - Die lichtbogenbasierte, additive Fertigung ist dank hoher erreichbarer Aufbauraten und nahezu uneingeschränktem Bauraum zur Fertigung großvolumiger Bauteile prädestiniert. Die Kombination etablierter Maschinenkomponenten aus Robotertechnik, Schweißtechnik und Sensorik ermöglicht den präzisen schichtweisen Materialauftrag. Die Wirkmechanismen zwischen Prozessparametern und den daraus resultierenden mechanisch-technologischen Eigenschaften der additiv gefertigten Bauteile stellen eine Herausforderung dar. Dies gilt insbesondere auch für dickwandige Bauteile. Bei der Fertigung von Bauteilen aus höherfesten Al-Mg-Si-Aluminiumlegierungen ist aufgrund der hohen Anfälligkeit für Erstarrungsrisse und der Neigung zu wasserstoffinduzierter Porosität im besonderen Maße auf das Temperaturregime und die gewählte Aufbaustrategie zu achten. Der Einfluss der Prozessparameter auf die Bauteilqualität wurde durch die Analyse der Größe und Verteilung von Poren sowie der resultierenden Festigkeit untersucht. Darüber hinaus wurde der Einfluss einer Wärmenachbehandlungsstrategien auf das Festigkeitsverhalten analysiert. Es konnte gezeigt werden, dass dickwandige Strukturen aus höherfesten Al-Mg-Si-Aluminiumlegierungen mit mechanischen Kennwerten im Bereich des Referenzmaterials mittels MSGLichtbogenverfahren additiv gefertigt werden können. T2 - Additive Fertigung – Werkstoffe – Prozesse – Wärmebehandlung 2022 CY - Bremen, Germany DA - 29.06.2022 KW - WAAM KW - Al-Mg-Si-Legierungen KW - Porosität KW - Wärmenachbehandlung KW - Mechanisch technologische Kennwerte PY - 2022 SP - 169 EP - 181 PB - Arbeitsgemeinschaft Wärmebehandlung und Werkstofftechnik e. V. CY - Bremen AN - OPUS4-56673 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Yang, Fan A1 - Meng, Xiangmeng A1 - Putra, Stephen Nugraha A1 - Artinov, Antoni A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Numerical analysis of the effect of the metal vapor plume on the keyhole and the molten pool behavior during deep penetration laser beam welding N2 - The effect of the oscillating metal vapor plume on the keyhole and molten pool behavior during the laser beam welding of AlMg3 aluminum alloys is investigated by the experimental and numerical method. The real-time height of the metal vapor plume is measured by high-speed camera observation. The obtained experimental results are used to evaluate the additional heating source and laser beam attenuation caused by the scattering and absorption based on the Beer-Lambert theory. Furthermore, the dynamic behavior of the metal vapor plume is incorporated into a 3D transient heat transfer and fluid flow model, coupled with the ray tracing method, for the laser beam welding of the AlMg3 alloy. It is found that the additional heating resulting from the scattered and absorbed laser beam energy by the metal vapor plume significantly expands the shape of the molten pool on the top region. Moreover, the oscillating metal vapor plume caused the fluctuation of the molten pool shape. The probability of keyhole collapse at the bottom increases significantly to 72% due to the oscillating laser power induced by the laser beam attenuation. The internal interplay between the metal vapor plume, molten pool shape, and the keyhole collapse are obtained. The developed model has been validated by the experiments, which shows a good agreement. T2 - International Congress of Applications of Lasers & Electro-Optics 2023 CY - Chicago, Illinois, USA DA - 16.10.2023 KW - Deep penetration laser beam welding KW - Numerical simulation KW - Oscillating vapor plume KW - Keyhole collapse PY - 2023 SP - 1 EP - 10 AN - OPUS4-58841 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Weinel, Kristina A1 - Hahn, Marc Benjamin A1 - Lubk, Axel A1 - Feng, Wen A1 - Martinez, Ignacio Gonzalez A1 - Büchner, Bernd A1 - Agudo Jácome, Leonardo T1 - Electron-beam-induced modification of gold microparticles in an SEM N2 - Electron-beam-induced conversion of materials in a transmission electron microscope uses the high power density of a localized electron beam of acceleration voltages above 100 kV as an energy source to transform matter at the sub-micron scale. Here, the e-beam-induced transformation of precursor microparticles employing a low-energy e-beam with an acceleration voltage of 30 kV in a scanning electron microscope is developed to increase the versatility and efficiency of the technique. Under these conditions, the technique can be classified between e-beam lithography, where the e-beam is used to mill holes in or grow some different material onto a substrate, and e-beam welding, where matter can be welded together when overcoming the melting phase. Modifying gold microparticles on an amorphous SiOx substrate reveals the dominant role of inelastic electron-matter interaction and subsequent localized heating for the observed melting and vaporization of the precursor microparticles under the electron beam. Monte-Carlo scattering simulations and thermodynamic modeling further support the findings. KW - Scanning electron microscopy KW - Electron-beam-induced modification KW - Heat transfer KW - Gold microparticles KW - Nanoparticles synthesis PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-609513 UR - https://arxiv.org/html/2408.02409v1 SP - 1 EP - 9 AN - OPUS4-60951 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niederleithinger, Ernst A1 - Hille, Falk A1 - Hofmann, Detlev A1 - Kind, Thomas ED - Isecke, B. ED - Krieger, J. T1 - Überwachung der Brücke Altstädter Bahnhof, Brandenburg./H. Begleituntersuchungen mit moderner Sensorik und zerstörungsfreier Prüfung N2 - Die B1 Brücke am Altstädter Bahnhof in Brandenburg an der Havel wurde im Dezember 2019 aufgrund von während einer turnusmäßigen Inspektion entdeckten Rissen und Hohlstellen entlang der vorgespannten Längsträger gesperrt und im Mai 2021 abgebrochen. In der Zwischenzeit wurde die Brücke detailliert überwacht. Vor dem Abriss wurden zudem umfangreiche Untersuchungen zur Bestandsaufnahme und Schadensanalyse sowie Tests moderner Sensorik vorgenommen. Dabei konnte sowohl die richtige, zuvor nicht sicher bekannte Anzahl von Spanngliedern in den Querträgern sicher ermittelt werden als auch durch moderne Varianten der Schwingungsmessungen und der faseroptischen Sensorik zusätzliche Kenntnisse püber das Bauwerksverhalten ermittelt werden . In dem Beitrag werden die Verfahren mit ihren Möglichkeiten und Grenzen vorgestellt, die Ergebnissee an der Brücke in Brandenburg erläutert und zukünftige Einsatzmöglichkeiten diskutiert. T2 - 5. Brückenkolloquium CY - Ostfildern, Germany DA - 06.09.2022 KW - Monitoring KW - Brücke KW - Radar KW - Vibration KW - Faseroptik PY - 2022 SN - 978-3-8169-3549-0 SP - 555 EP - 566 PB - Expert Verlag CY - Tübingen AN - OPUS4-55627 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Liao, Chun-Man A1 - Hicke, Konstantin A1 - Bernauer, F. A1 - Igel, H. A1 - Hadziioannou, C. A1 - Niederleithinger, Ernst ED - Isecke, B. ED - Krieger, J. T1 - Multi-Sensor measurements on a large-scale bridge model N2 - This contribution introduces an investigation of a large-scale prestressed concrete bridge model (“BLEIB” structure at the BAM-TTS open air test site) by means of on-site cooperative measurements. This bridge has an external post-tensioning system and has been instrumented with the ultrasonic transducers, temperature sensors and optical fibers for Distributed Acoustic Sensing (DAS). Our experiment was designed to test the suitability of the novel 6C sensors developed within the framework of the GIOTTO project – the IMU50. The IMU50 sensor enables vibration measurements in translation along three axes and rotation around three axes. The geophone sensors were considered for complementary measurements of vertical velocity response. In the experiment, several perturbations were achieved by controlling the external influence factors such as loading and prestressing changes. The aim of the integrated measurement strategy was to fully observe the results of the condition change and to verify the effectiveness of multiple sensors for bridge monitoring. T2 - 5. Brückenkolloquium CY - Ostfildern, Germany DA - 06.09.2022 KW - Concrete KW - Bridge KW - Monitoring KW - Rotation KW - Distributed acoustic sensing PY - 2022 SN - 978-3-8169-3549-0 SP - 223 EP - 230 PB - Expert Verlag CY - Tübingen AN - OPUS4-55625 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bachmann, Marcel A1 - Meng, Xiangmeng A1 - Artinov, Antoni A1 - Rethmeier, Michael T1 - Investigating defects caused by narrow pool shapes in deep penetration welding N2 - Laser beam welding is a widely used joining technique in many industrial applications. This is mainly due to its many unique advantages, especially compared to conventional arc welding processes. These advantages include, among others, highly concentrated energy deposition, low total heat input and a capacity to penetrate deep into the material while causing only small welding distortions. However, at the same time, the small dimension of the laser spot, high solidification rates, and small dimensions of the weld pool itself can provoke issues regarding the assembly tolerances of the workpiece, the hot-cracking phenomena, as well as keyhole-induced bubbles escaping from the melt. Weld pool shapes in laser beam welding are elongated at the external, free surfaces under the action of the main driving forces in the melt – such as recoil pressure and surface tension forces – while being shorter in the internal areas of the weld pool. This leads to a regular solidification sequence from the internal zones toward the free surfaces, e.g. from the bottom to the top in partial penetration welding. However, in recent studies reported in the literature and seen in the experimental and numerical investigations of BAM Bundesanstalt für Materialforschung und -prüfung in Berlin, it was found that an internal narrowing phenomenon can occur that is often accompanied by a distinct bulging of the weld bead in deeper zones. As the internal behaviour of the melt during the process is hardly optically accessible, several numerical models and experimental techniques were established to visualise the mechanisms of the formation of the bulging and the narrowing phenomenon and to reveal the consequences on the solidification sequence, pore formation, and filler metal dilution. KW - Weld pool shape KW - Laser beam welding KW - Solidification PY - 2022 SN - 1759-0752 IS - 57 SP - 28 EP - 29 PB - Europa Science CY - Cambridge, UK AN - OPUS4-56995 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kempf, A. A1 - Agudo Jácome, Leonardo A1 - Hilgenberg, Kai T1 - Influence of process-relevant parameters and heat treatments on the microstructure and resulting mechanical behavior of additively manufactured AlSi10Mg via Laser Powder Bed Fusion N2 - Within the group of additive manufacturing (AM) technologies for metals, laser powder bed fusion (L-PBF) has a leading position. Nevertheless, reproducibility of part properties has not reached sufficient maturity hindering the use for industrial applications especially for safety-relevant components. This article presents the results of various experimental tests performed with the aluminium alloy AlSi10Mg identifying reasons for the high deviations in mechanical properties. Herein, it is discussed how microstructure is influenced by different process parameters (laser power, scanning speed, energy density, building height) and how it can be adjusted by suitable post process heat treatments. The impact of resulting changes in microstructure is shown by monotonic tensile and cyclic fatigue tests considering specimens manufactured with different L-PBF machines. T2 - LiM 2021 CY - Online meeting DA - 21.06.2021 KW - Additive manufacturing KW - Laser powder bed fusion KW - AlSi10Mg PY - 2021 SP - 1 EP - 9 AN - OPUS4-52991 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Merz, Benjamin A1 - Knobloch, Tim A1 - Mohr, Gunther A1 - Hilgenberg, Kai T1 - Concepts for bridging voids in metal additive manufacturing for repair of gas turbine blades using laser powder bed fusion N2 - One of the main advantages of additive manufacturing (AM) processes such as laser powder bed fusion (PBF-LB/M) is the possibility to manufacture complex near-net-shape components. Therefore, the PBF-LB/M process is becoming increasingly important for the manufacturing and repair of gas turbine blades. Despite the great freedom in design, there are also limitations to the process. Manufacturing overhangs or bridging voids are some of the main challenges. In the conventional PBF-LB/M process, overhangs with angles up to 45° can be manufactured. However, gas turbine blades feature voids for cooling, which have to be bridged when using PBF-LB/M. In this work, different concepts for bridging voids are developed for future application in gas turbine blade repair. For this purpose, a test geometry is derived from the tip area of a gas turbine blade as a reference. By changing the initial geometry of the reference body, different designs for bridging voids are developed based on the PBF-LB/M requirements. Subsequently, these distinct designs are manufactured by PBF-LB/M. The different approaches are compared with respect to their volume increase. In addition, the specimens are visually inspected for warpage, shrinkage and imperfections by overheating. Out of the seven concepts developed, three concepts can be recommended for gas turbine blade repair based on low volume increase, distortion and shrinkage. T2 - Metal Additive Manufacturing Conference - MAMC 2022 CY - Graz, Austria DA - 26.09.2022 KW - Repair of gas turbine blades KW - Laser Powder Bed Fusion (PBF-LB/M) KW - Selective Laser Melting (SLM) KW - Design for Additive Manufacturing (DfAM) KW - Bridging voids KW - Supportless PY - 2022 SP - 19 EP - 28 PB - TU Graz CY - Graz AN - OPUS4-55868 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Merz, Benjamin A1 - Poka, Konstantin A1 - Nilsson, R. A1 - Mohr, Gunther A1 - Hilgenberg, Kai T1 - On the challenges of hybrid repair of gas turbine blades using laser powder bed fusion N2 - Additive manufacturing (AM) processes such as laser powder bed fusion (PBF-LB/M) are rapidly gaining popularity in repair applications. Gas turbine components benefit from the hybrid repair process as only damaged areas are removed using conventional machining and rebuilt using an AM process. However, hybrid repair is associated with several challenges such as component fixation and precise geometry detection. This article introduces a novel fixturing system, including a sealing concept to prevent powder sag during the repair process. Furthermore, a high-resolution camera within an industrial PBF-LB/M machine is installed and used for object detection and laser recognition. Herein, process related inaccuracies such as PBF-LB/M laser drift is considered by detection of reference objects. This development is demonstrated by the repair of a representative gas turbine blade. The final offset between AM build-up and component is analysed. An approximate accuracy of 160 μm is achieved with the current setup. T2 - LiM 2023 CY - Munich, Germany DA - 26.06.2023 KW - Laser powder bed fusion KW - Additive manufacturing KW - Hybrid repair KW - Position detection KW - High-resolution camera PY - 2023 SP - 1 EP - 9 AN - OPUS4-57836 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Kalbe, Ute A1 - Berger, Wolfgang A1 - Simon, Franz-Georg T1 - Durchführung von Ringversuchen zur Validierung der Normen E DIN 19528 und E DIN 19529 N2 - Um den Erfordernissen des Grundwasser- und Bodenschutzes zu entsprechen ist die Kenntnis des Elutionsverhaltens von Abfall- und Bodenmaterialien erforderlich, wenn diese z.B. zur Verwertung im Straßen- oder Landschaftsbau vorgesehen sind. Im Zusammenhang mit der Novellierung der Bundes-Bodenschutzverordnung und der Einführung der Ersatzbaustoffverordnung sowie in Auswertung der Ergebnisse des BMBF-Verbundvorhabens „Sickerwasserprognose“ wurden vom DIN-Normenaus-schuss Wasserwesen, Unterausschuss „Eluierungsverfahren“ zwei Verfahren zur Elution von Fest-stoffen erarbeitet, die im Oktober 2007 als Entwürfe veröffentlicht wurden. Dabei handelt es sich um ein Säulenperkolationsverfahren zur gemeinsamen Untersuchung des Elutionsverhaltens von orga-nischen und anorganischen Stoffen (E DIN 19528) und ein Schüttelverfahren mit einem Wasser-/ Feststoff-Verhältnis (W/F) von 2 l/kg zur Untersuchung der Elution von anorganischen Stoffen (E DIN 19529). Beide Verfahren sind für Bodenmaterialien und mineralische Abfälle mit einer Korngröße bis 32 mm vorgesehen. Für Normen die in Verordnungen zitiert werden sollen, ist eine Verfahrensvalidierung erforderlich. Im Rahmen dieses Vorhabens waren die Verfahrenskenndaten auf der Grundlage von Ringversuchen zu ermitteln. Zunächst wurden vier für die Verordnungen relevante Materialien (Hausmüllverbrennungs-asche, Recyclingbaustoff, Bodenmaterial, Stahlwerksschlacke) als Referenzmaterialien (RM) aufberei-tet. Die zu analysierenden Parameter wurden unter Berücksichtigung der Regelungsrelevanz in Abstimmung mit dem Auftraggeber ausgewählt. Die RM wurden gemeinsam mit Referenzlösungen an die 53 Teilnehmer der Ringversuche ausgegeben. Die statistische Auswertung der Ringversuchsergebnisse erfolgte nach DIN 38402-42, wobei der Gesamtmittelwert aller Teilneh-mer als Sollwert herangezogen wurde. Es konnte gezeigt werden, dass akzeptable Reproduzierbarkeiten für organische und anorganische Schadstoffe durch geeignete Vorgaben sowohl für Schütteltests als auch für Säulenversuche erzielt werden können. Dies gilt insbesondere unter Berücksichtigung des breiten Korngrößenspektrums der RM, der relativ hohen zugelassenen Toleranzen für das W/F bei den Säulenversuchen und des kurzen Bekanntheitsgrades der Normenentwürfe. Die ermittelten Verfahrenskenndaten finden Eingang in die abschließende Bearbeitung der Normen. KW - Verwertung KW - Abfallmaterialien KW - kontaminierter Boden KW - Auslaugungsverhalten KW - Eluierungsverfahren KW - Schütteltest KW - Säulenperkolationsversuch KW - Sickerwasserprognose KW - Standardisierung KW - Validierung KW - Ringversuche PY - 2008 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-354756 SP - 1 EP - 275 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-35475 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simon, Franz-Georg A1 - Kalbe, Ute A1 - Bandow, Nicole T1 - Potential use of incineration bottom ash in construction – Evaluation of environmental impact N2 - The results from a long-term lysimeter experiment with incineration bottom ash irrigated with artificial rain are reported. Whereas chloride concentration dropped significantly, the release of antimony increased during the course of the experiment as a result of aging processes. T2 - 10th International Conference on the Environmental and Technical Implications of Construction with Alternative Materials, WASCON 2018 CY - Tampere, Finland DA - 06.06.2018 KW - Leaching KW - MSWI Bottom Ash KW - Lysimeter KW - Antimony PY - 2018 SN - 978-951-758-631-3 SN - 0356-9403 SP - 108 EP - 110 AN - OPUS4-45416 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Völzke, Holger A1 - Cherkouk, Andrea A1 - Zajec, Bojan A1 - Debelle, Aurélien A1 - Alonso, Ursula A1 - Ganster, Patrick A1 - Generelo-Casajus, Lidia A1 - Merroun, Mohamed L. A1 - Morales-Hidalgo, Mar A1 - Pakarinen, Janne A1 - Rossignol, Fabrice A1 - Trentin, Andressa T1 - Durability of traditional and innovative disposal container materials and coatings: State-of-the-art and further research within InCoManD N2 - This document provides a consolidated state-of-the-art overview of current knowledge on containers designed to safely isolate heat-generating high-level radioactive waste in deep geological repositories (DGRs). These containers form a vital part of the multi-barrier safety system that ensures long-term protection of people and the environment. Their durability — especially their resistance to corrosion and mechanical stress — is essential, as they are expected to perform over time scales ranging from hundreds to hundreds of thousands of years. The findings presented here are taken from recent research studies out of the EURAD programme and also from the EURAD-1 ConCorD project (Work Package 15, 2021–2024), which reviewed the performance of various container materials, including copper, carbon steel and silicon carbide. The report covers experimental results under relevant disposal conditions, the impact of manufacturing and sealing processes, and the current capabilities of modelling tools to simulate the complex underground environment in which these containers will operate. In addition to summarising knowledge on traditional materials, the document highlights recent progress and remaining challenges related to innovative ceramic-based containers. Key issues include ensuring effective sealing and mechanical integrity, particularly under harsh and evolving conditions over long periods. The report also emphasizes the importance of understanding how different environmental and mechanical factors interact to influence container degradation. Neither corrosion nor stress alone can fully explain long-term behaviour, and both must be studied together. Finally, this state-of-the-art sets the stage for future work, especially the EURAD-2 InCoManD project (Work Package 9), which will build on these findings to improve testing methods, refine models, and explore promising new materials and design solutions for safer and more reliable waste containment. Research activities within InCoManD are hence briefly described throughout this document. KW - Disposal container KW - Radioactive waste KW - Deep geological repository KW - Corrosion resistance KW - Durability PY - 2025 UR - https://www.ejp-eurad.eu/sites/default/files/2025-06/EURAD2_WP09_INCO_T02_01_D09.1_SOTA_0.pdf N1 - This document is a deliverable of the European Partnership on Radioactive Waste Management 2 (EURAD-2); EURAD-2 is co-funded by the European Union under Grant Agreement N°101166718. VL - Deliverable 9.1 SP - 1 EP - 60 PB - Agence Nationale pour la Gestion des Déchets Radioactifs (ANDRA) CY - Châtenay-Malabry AN - OPUS4-63303 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Heisterkamp, I. A1 - Gartiser, S. A1 - Kretzschmar, M. A1 - Schoknecht, Ute A1 - Kalbe, Ute A1 - Happel, O. A1 - Ratte, M. T1 - Methoden und Kriterien zur Bewertung der Ökotoxizität von Produkten N2 - Die Umweltverträglichkeit von Bauprodukten, die in Kontakt mit Regen- oder Sickerwasser kommen, wurde durch Kombination normierter Elutions- (DSLT, Perkolationstest) und Ökotoxizitätstests (Algen, Daphnien, Fischeier, Leuchtbakterien) sowie Gentoxizitätstests (Ames, umu) untersucht. Ziel des Projektes war es einerseits, einen Beitrag zur Harmonisierung der Prüfmethoden unter CEN/TC 351 zu leisten und andererseits potentielle Produktgruppen, die sich für die Umweltzeichenvergabe des Blauen Engels eignen würden, zu erkennen. Durch umfangreiche qualitative und quantitative chemische Analysen (u. a. GC-MS- sowie LC-MS-Screening) wurden einige der freigesetzten Stoffe identifiziert und anhand von Literaturdaten ökotoxikologisch charakterisiert. Insgesamt wurden 34 Bauprodukte (Dachbahnen, Lacke, Wood-Plastic-Composites, Pflasterfugenmörtel, Korkgranulate, Schaumglasschotter, Wegedecken, Dichtmassen) untersucht. Hierbei wurden insbesondere bei den Fugenmörteln und Korkgranulaten sehr hohe Ökotoxizitäten (bis LID = 16384 bei den Fugenmörteln und LID = 24578 bei den Korkgranulaten) beobachtet. Algen- und Leuchtbakterientests waren in der Regel deutlich empfindlicher als der Daphnien- und Fischeitest. Die untersuchten Dachbahnen, Lacke, Wood-Plastic-Composites und Schaumglasschotter zeigten hingegen keine oder nur sehr geringe Ökotoxizitäten. Zur Qualitätssicherung und Validierung wurde ein Europäischer Ringversuch gemäß den Vorgaben der DIN ISO 5725 organisiert, durchgeführt und ausgewertet. Hierzu wurde ein Fugenmörtel als flächiges Produkt im DSLT und als gebrochenes körniges Produkt im Perkolationstests eluiert und die Eluate nachfolgend in den 29 teilnehmenden Laboren hinsichtlich ihrer Ökotoxizität untersucht. Hierbei wurden insgesamt plausible Ergebnisse und gute (<50 %) bis sehr gute (<20 %) Reproduzierbarkeiten erzielt. Es wird empfohlen, für die Produktgruppen Dachbahnen, Kunstrasen und Sportböden sowie Fugenmörtel Vergabekriterien für den Blauen Engel zu entwickeln KW - Bauprodukte KW - Umweltbewertung KW - Ökotoxizität PY - 2022 UR - https://www.umweltbundesamt.de/publikationen/methoden-kriterien-zur-bewertung-der-oekotoxizitaet SN - 1862-4804 VL - 151/2022 SP - 1 EP - 135 PB - Umweltbundesamt CY - Dessau-Roßlau AN - OPUS4-56679 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalbe, Ute A1 - Berger, Wolfgang A1 - Eckardt, Jürgen A1 - Christoph, Gabriele A1 - Walzel, Hans-Peter T1 - Soil water investigations based on laboratory tests T2 - Eurosoil 2004 CY - Freiburg, Germany DA - 2004-09-04 PY - 2004 SP - 1(?) EP - 5(?) AN - OPUS4-4576 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Oliver A1 - Kalbe, Ute A1 - Berger, Wolfgang A1 - Simon, Franz-Georg A1 - López Meza, S. T1 - Leaching experiments on the release of heavy metals and PAH from C&D waste and MSWI bottom ash N2 - Leaching tests are fundamental tools for the assessment of long-term impact of contaminated waste materials on the soil-groundwater pathway. Waste materials should be tested under conditions equal to their actual application in re-use scenarios to achieve reliable results. Since the standards for leaching procedures available on international level so far are either not validated or considered inadequate in respect to coarse grained materials, new standards had to be developed. Therefore column percolation and batch test procedures have been standardized and validated to enable their introduction to new German regulations concerning waste management. Practical aspects of the test procedures as well as the boundary conditions compared to the already existing standards will be described. Examples including round robin test results will be given to justify the selection of the new specifications. T2 - 2nd International conference on hazardous and industrial waste management CY - Chania, Crete, Greece DA - 2010-10-05 KW - Leaching KW - Bioavailability KW - Column tests KW - Batch tests PY - 2010 IS - Session A, A5.1. SP - 1 EP - 8 AN - OPUS4-22128 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalbe, Ute A1 - Krüger, Oliver A1 - Berger, Wolfgang A1 - Simon, Franz-Georg T1 - Source term determination by leaching procedures - new developments in Germany T2 - Global waste management symposium CY - San Antonio, TX, USA DA - 2010-10-03 KW - Elutionsverfahren KW - Abfall PY - 2010 SP - 1 EP - 11(?) AN - OPUS4-22256 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalbe, Ute A1 - Berger, Wolfgang A1 - Simon, Franz-Georg T1 - Results of German ring tests on the vaildation of leaching standards for source term determination T2 - WASCON 2009 - Sustainable management of waste and recycled materials in construction CY - Lyon, France DA - 2009-06-03 KW - Ringversuche KW - Validierung Normen KW - Kontaminierter Boden KW - Abfall KW - Säulenversuche KW - Schüttelversuche PY - 2009 SP - 1 EP - 10(?) AN - OPUS4-19569 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Berger, Wolfgang A1 - Eckardt, Jürgen A1 - Fischer, Hildegard A1 - Jansky, Hans-Joachim A1 - Kalbe, Ute T1 - Herstellung von Referenzmaterialien für die Sickerwasserprognose T2 - 1. Workshop der AG "Quellstärke" des BMBF-Verbundvorhabens CY - Hamburg-Harburg, Deutschland DA - 2001-10-24 PY - 2001 AN - OPUS4-2550 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Berger, Wolfgang A1 - Kalbe, Ute T1 - Herstellung von Referenzmaterialien T2 - Statusseminar, Zwischenpräsentation zum BMBF-Förderschwerpunkt "Sickerwasserprognose" CY - Karlsruhe, Deutschland DA - 2003-02-18 PY - 2003 SP - 1(?) EP - 10(?) AN - OPUS4-2549 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalbe, Ute A1 - Berger, Wolfgang A1 - Bredow, Andrea A1 - Krüger, Oliver A1 - Piechotta, Christian A1 - Schoknecht, Ute T1 - Säulenperkolationsversuche mit perfluorierten Tensiden und Bioziden in Böden N2 - Säulenperkolationsversuche werden u.a. zur Ermittlung der Freisetzung von Schadstoffen aus Böden durchgeführt. Im Entwurf der novellierten Bundesboden-schutz- und Altlastenverordnung ist neben Schüttelverfahren (DIN 19527 und 19529) ein Säulenperkolationsverfahren (DIN 19528) zur Eluatgewinnung aus Böden festgeschrieben. Mit diesem Verfahren kann im Vergleich zu den Schüttelversuchen auch der zeitliche Verlauf der Schadstofffreisetzung erfasst und bewertet werden. Allerdings sind die Verfahren bisher nur für anorganische Stoffe und wenige prioritäre organische Schadstoffe validiert worden (PAK, MKW, PCB, Phenole). Aber auch Schadstoffe wie perfluorierte Tenside (PFT), die z.B. für die Veredlung von Papier, Textilien und Haushaltsgeräten eingesetzt werden oder Biozide, mit denen Bauprodukte zum Schutz vor mikrobiellem Befall ausgerüstet werden (z.B. Fassadenbeschichtungen und Holz), geraten auf Grund ihrer gesundheits- und umwelt-schädlichen Eigenschaften immer stärker in die Diskussion. T2 - DBG-Jahrestagung 2013 - Kommission VI - Böden - Lebensgrundlage und Verantwortung CY - Rostock, Germany DA - 07.09.2013 KW - Elutionsverfahren KW - Säulenperkolationsverfahren KW - Kontaminierte Böden KW - Organische Schadstoffe PY - 2013 N1 - Serientitel: Berichte der DBG – Series title: Berichte der DBG SP - 1 EP - 3 PB - DBG (Deutsche Bodenkundliche Gesellschaft) CY - Göttingen AN - OPUS4-29453 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Berger, Wolfgang A1 - Kalbe, Ute A1 - Krüger, Oliver A1 - Hennecke, D. T1 - Vergleichende Bewertung von Elutionsverfahren für die Beurteilung des Auslaugverhaltens organischer Stoffe aus Böden N2 - Es wurde eine vergleichende Bewertung der Ergebnisse von Schüttel- und Säulenverfahren als Übereinstimmungstest für die Untersuchung des Auslaugverhaltens von organischen Schadstoffen aus Böden vorgenommen. Dafür wurden die Ergebnisse von Ringversuchen zur Validierung der entsprechenden Elutionsverfahren genutzt. Der Methodenvergleich zeigte, dass keine signifikanten Unterschiede zwischen den Ergebnissen beider Elutionsverfahren beobachtet wurden. Es wurden beim Schüttelverfahren tendenziell etwas geringere Gesamtmittelwerte der Ringversuchsteilnehmer als beim Säulenverfahren erzielt. T2 - DBG-Jahrestagung 2013 - Kommission VI - Böden - Lebensgrundlage und Verantwortung CY - Rostock, Germany DA - 07.09.2013 KW - Elutionsverfahren KW - Methodenvergleich KW - Säulenverfahren KW - Schüttelverfahren KW - Kontaminierte Böden KW - Organische Schadstoffe PY - 2013 N1 - Serientitel: Berichte der DBG – Series title: Berichte der DBG SP - 1 EP - 3(?) PB - DBG (Deutsche Bodenkundliche Gesellschaft) CY - Göttingen AN - OPUS4-29405 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Berger, Wolfgang A1 - Kalbe, Ute A1 - Krüger, Oliver A1 - Hennecke, D. A1 - Kördel, W. T1 - Evaluierung von Elutionsmethoden - Durchführung von Robustheitsuntersuchungen zur Validierung von E DIN 19527 für ausgewählte Böden und Bodenmaterialien mit prioritären organischen Schadstoffen N2 - Ziel des Vorhabens ist es, die Robustheit des Schüttelverfahrens nach E DIN 19527 mit einem Wasser-/Feststoffverhältnis von 2 l/kg für unterschiedliche Bodenarten und Bodenmaterialien zu überprüfen. Gleichzeitig soll bei diesen Untersuchungen das Stoffspektrum auf weitere prioritäre organische Kontaminanten erweitert werden. Dies stellt die Voraussetzung für die Durchführung von Ringversuchen zur Validierung der Norm DIN 19527 dar. KW - Kontaminierter Boden KW - PAK KW - PCB KW - MKW KW - Phenole KW - Elutionsverfahren KW - Schütteltests KW - Robustheitsuntersuchungen KW - Standardisierung KW - Validierung KW - Laborvergleich PY - 2013 UR - https://www.umweltbundesamt.de/sites/default/files/medien/378/publikationen/texte_77_2013_robustheitsuntersuchung_terytze_0.pdf VL - 77 SP - 1 EP - 124 PB - Umweltbundesamt CY - Dessau-Roßlau AN - OPUS4-28990 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Paul, Andrea A1 - Breitfeld, S. A1 - Sauer, Andreas A1 - Becker, Roland A1 - Kalbe, Ute A1 - Bremser, Wolfram A1 - Braun, Ulrike T1 - A Raman spectroscopic method for the monitoring of microplastics in soil N2 - Due to the increasing presence of microplastic particles (MP) in the Environment and the unknown risks arising from them, there is an urgent need for analytical methods that allow for an efficient identification and quantification of microplastics (MP), i.e. particles < 5 mm, in environmental samples. So far, mostly timeconsuming (micro) infrared or micro-Raman spectroscopic methods are applied. Here an faster alternative Approach is presented based on a Raman processspectrometer with fiber-optical probes in combination with multivariate data analysis. T2 - 12. Kolloquium Prozessanalytik CY - Berlin, Germany DA - 28.11.2016 KW - Raman spectroscopy KW - Microplastics KW - Soil KW - Chemometrics KW - PLS-DA PY - 2016 SP - P10, 59 EP - 60 AN - OPUS4-38392 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Müller, Birgit A1 - Brandt, Simone A1 - Badura, André A1 - Knigge, Anton A1 - Horn, Wolfgang A1 - Jann, Oliver T1 - Geruchs- und emissionsarme Produkte für eine gesunde Innenraumluft - Entwicklung von Anforderungen für den Blauen Engel bei innenraumrelevanten, großflächigen Produkten N2 - Gerüche in Innenräumen können belästigend wirken und das Wohlbefinden sowie die Gesundheit beeinflussen. Hauptziel der Untersuchungen ist es zu prüfen, ob die Vergabekriterien des Blauen Engels für die Produktgruppen „Elastische Bodenbeläge“ (DE-UZ 120) und „Emissionsarme Bodenbeläge, Paneele und Türen aus Holz und Holzwerkstoffen für Innenräume“ (DE-UZ 176) um geruchsrelevante Aspekte ergänzt werden können. Dies ist erstrebenswert, da Untersuchungen in Vorgängerprojekten gezeigt haben, dass die gemessenen Emissionen untersuchter Produkte zwar abnehmen, die Geruchsbelastung jedoch in etwa gleichgeblieben ist. Die Ergebnisse der Untersuchungen zeigen, dass es möglich ist Anforderungen an den Geruch der Produkte zu stellen. Ferner wird untersucht und gezeigt, dass die bislang vorläufig festgelegte Schwelle einer empfundenen Intensität von 7 pi für die Zulassung von Bauprodukten gemäß Schema des Ausschusses zur gesundheitlichen Bewertung von Bauprodukten (AgBB) und Blauer Engel, als Beurteilungsmaßstab geeignet ist. Der im AgBB-Schema zugrunde gelegte Zusammenhang zwischen der geruchlichen Zumutbarkeit und der empfundenen Intensität kann mit den durchgeführten Messungen untermauert werden. Es kann gezeigt werden, dass bei Tests mit großen, ungeschulten Personengruppen etwa 70% der Probandinnen und Probanden Produkte mit einer empfundenen Intensität von bis zu 7 pi geruchlich als zumutbar empfinden. Zur Bewertung der empfundenen Intensität wird ein Vergleichsmaßstab verwendet. Die Einhaltung konstanter Bedingungen für die Temperatur und die relative Feuchte bei den Messungen ist von großer Bedeutung, da diese einen Einfluss auf die Messergebnisse haben. Daher werden Untersuchungen bei unterschiedlichen Temperaturen und relativer Luftfeuchte, die mit einer eigens dafür gebauten kleinen raumlufttechnischen Anlage eingestellt werden können, durchgeführt. Die Ergebnisse belegen, dass die Einhaltung konstanter Prüfbedingungen wichtig ist und zeigen deren Einfluss auf die Geruchwahrnehmung. In einem neuen Luftqualitätslabor der HTW Berlin können Innenräume unter standardisierten Bedingungen geprüft werden. Es werden vergleichende Messungen mit Emissionsprüfkammertests durchgeführt, um zu prüfen, ob ähnliche Ergebnisse erreicht werden können. Das Ziel ist es, die Räume später für sensorische Messungen mit verschiedenen Ausstattungen zu nutzen. Das Vorhaben baut auf den Ergebnissen der Vorhaben UBA Texte 35/2011 „Sensorische Bewertung der Emissionen aus Bauprodukten – Integration in die Vergabegrundlagen für den Blauen Engel und das Bewertungsschema des Ausschusses zur gesundheitlichen Bewertung von Bauprodukten“ (Müller, 2011) und UBA Texte 92/2019 „Emissions- und geruchsarme Bauprodukte für energieeffiziente Gebäude – Entwicklung von Anforderungen und Konzepten für den Blauen Engel aus Klimaschutzsicht“ (Müller, 2019) auf. KW - Emission KW - Indoor air quality KW - VOC KW - Geruch KW - Bauprodukte PY - 2025 DO - https://doi.org/https://doi.org/10.60810/openumwelt-7610 SN - 1862-4804 VL - 78/2025 SP - 1 EP - 214 PB - Umweltbundesamt CY - Dessau-Roßlau AN - OPUS4-63341 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holm, Olaf A1 - Bandow, Nicole A1 - Kalbe, Ute A1 - Simon, Franz-Georg T1 - Innovative treatment trains of bottom ash (BA) from municipal solid waste incineration (MSWI) in Germany N2 - The industrial sector of bottom ash (BA) treatment from municipal solid waste incineration (MSWI) in Germany is currently changing. In order to increase the recovery rates of metals or to achieve a higher quality of mineral aggregates derived from BA, new procedures have been either implemented to existing plants or completely new treatment plants have been built recently. Three treatment trains, which are designated as entire sequences of selected processing techniques of BA, are introduced and compared. One treatment train is mainly characterized by usage of a high speed rotation accelerator whereas another is operating completely without crushing. In the third treatment train the BA is processed wet directly after incineration. The consequences for recovered metal fractions and the constitution of remaining mineral aggregates are discussed in the context of legislative and economical frameworks. Today the recycling or disposal options of mineral residues still have a high influence on the configuration and the operation mode of the treatment trains of BA despite of the high value of recovered metals. T2 - Sardinia 2015 - 15th International waste management and landfill symposium CY - S. Margherita di Pula, Cagliari, Italy DA - 05.10.2015 KW - MSWI KW - Bottom ash KW - Treatment train KW - High velocity impact crushing KW - Wet treatment KW - Recovery rates KW - Non-ferrous metals KW - Mineral aggragates KW - Recycling KW - Secondary construction material PY - 2015 SP - 1 EP - 11 AN - OPUS4-34936 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Hjelmar, O. A1 - Hyks, J. A1 - Wahlström, M. A1 - Laine-Ylijoki, M. A1 - van Zomeren, A. A1 - Comans, R. A1 - Kalbe, Ute A1 - Schoknecht, Ute A1 - Krüger, Oliver A1 - Grathwohl, P. A1 - Wendel, T. A1 - Abdelghafour, M. A1 - Méhu, J. A1 - Schiopu, N. A1 - Lupsea, M. T1 - Robustness validation of TS-2 and TS-3 developed by CEN/TC351/WG1 to assess release from products to soil, surface water and groundwater KW - Bauprodukte KW - Umweltverträglichkeit KW - Leachingtest KW - Europäische Harmonisierung PY - 2013 IS - Final Report (NEN - Secretariat of CEN/TC 351) SP - 1 EP - 278 ET - Project-No. 11810594 AN - OPUS4-28291 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Berger, Wolfgang A1 - Eckardt, Jürgen A1 - Kalbe, Ute A1 - Grabner, Angela T1 - Examination of volatile organic compounds (VOC) in contaminated soil T2 - Eurosoil 2004 CY - Freiburg, Germany DA - 2004-09-04 PY - 2004 SP - 1(?) EP - 4(?) AN - OPUS4-4577 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalbe, Ute T1 - Validation of leaching tests - a key issue towards reliable use of results T2 - Workshop "Source Term: from characterization to prediction" CY - Paris, France DA - 2006-10-19 PY - 2006 SP - 1(?) EP - 5(?) PB - Bureau de recherches géologiques et minières (BRGM) CY - Paris AN - OPUS4-14114 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Berger, Wolfgang A1 - Kalbe, Ute A1 - Helm, Renate T1 - Ermittlung des Anteils der Probenahme an der Ergebnisunsicherheit bei Bodenuntersuchungen N2 - Bei der Beurteilung von Schadstoffkonzentrationen in Böden ist es erforderlich, den Anteil der Unsicherheit der Probenahme an der Gesamtunsicherheit des Bewertungsverfahrens abzuschätzen. Die Gesamtunsicherheit einer Bewertung setzt sich zusammen aus dem Anteil der pedogeochemischen Heterogenität der Grundgesamtheit, der Unsicherheit bei der Probenahme und der chemischen Analytik. Auf der Grundlage einer systematischen Beprobung eines Rieselfeldbodens wurden beispielhaft für das Element Zink unter Nutzung der Varianzanalyse die einzelnen Varianzkomponenten getrennt und die Anteile der Ergebnisunsicherheit ermittelt. T2 - DBG Jahrestagung 2009 "Böden - eine endliche Ressource" CY - Bonn, Deutschland DA - 2009-09-05 KW - Probenahme KW - Rieselfeldboden KW - Varianzanalyse KW - Ergebnisunsicherheit PY - 2009 UR - http://eprints.dbges.de/173/ SP - 1 EP - 3 AN - OPUS4-20312 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalbe, Ute A1 - Bredow, Andrea A1 - Berger, Wolfgang A1 - Wessel-Bothe, Stefan A1 - Keller, T. T1 - Optimierung des Säulenperkolationsverfahrens durch Automatisierung N2 - Elutionstests im Labormaßstab werden zur Ermittlung der Freisetzung von Schadstoffen aus Böden oder mineralischen Abfällen für die Verwertung in technischen Erdbau-werken durchgeführt. Sie sollen die Feldbedingungen möglichst realitätsnah wider-spiegeln und auch die Beurteilung der Freisetzung von Schadstoffen über längere Zeiträume ermöglichen. Aus diesem Grunde werden im Entwurf der novellierten BBodSchV neue Verfahren zur Eluatgewinnung aus den genannten Materialien festgeschrieben. T2 - DBG-Jahrestagung, Kommission VI, 'Böden verstehen - Böden nutzen - Böden fit machen' CY - Berlin, Germany DA - 03.09.2011 KW - Schadstofffreisetzung KW - Säulenperkolation KW - Werkstoffauswahl KW - Elutionsverfahren PY - 2011 UR - http://eprints.dbges.de/565/1/Berichte_der_DBG_Kalbe_2753.pdf SP - 1 EP - 4 AN - OPUS4-24648 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Berger, Wolfgang A1 - Kalbe, Ute A1 - Krüger, Oliver A1 - Litzba, Andreas T1 - Vergleich der Ergebnisse von Übereinstimmungstests bei Säulen- und Schüttelversuchen N2 - In der Bundes-Bodenschutz- und Altlasten-verordnung (BBodSchV) und im Arbeits-entwurf der Novellierung ist für den Wirkungspfad Boden-Grundwasser eine Sickerwasserprognose vorgesehen, um die Gefahren, die von kontaminierten Stand-orten für das Schutzgut Grundwasser ausgehen, beurteilen zu können. Bei der Sickerwasserprognose kann u.a. auf der Grundlage von Materialuntersuchungen im Labor die Quellstärke kontaminierter Ma-terialen ermittelt werden, welche dann bei Transportmodellierungen Berücksichtigung findet. Der Entwurf der Novellierung der BBodSchV sieht für die Ermittlung der Quellstärke den Übereinstimmungstest des Säulenversuchs nach DIN 19528 bis zu einem Wasser/Feststoff - Verhältnis (W/F) von 2 l/kg für anorganische und organische Stoffe (PAK) oder den Schüttelversuch nach DIN 19529 für anorganische Stoffe und E DIN 19527 für organische Stoffe auch jeweils mit einem W/F von 2 l/kg vor. Die Zulassung beider Elutionsverfahren setzt die Gleichwertigkeit der Ergebnisse beider Verfahren voraus. Im Folgenden werden die Ergebnisse des Vergleichs der Auslaugung von polyzyklischen aromat-ischen Kohlenwasserstoffen (PAK) aus unterschiedlichen Böden mit Hilfe beider Elutionsverfahren vorgestellt. T2 - DBG-Jahrestagung, Kommission VI, 'Böden verstehen - Böden nutzen - Böden fit machen' CY - Berlin, Germany DA - 03.09.2011 KW - Elutionsverfahren KW - Übereinstimmungstest KW - Säulenverfahren KW - Schüttelverfahren KW - Kontaminierte Böden KW - Polyzyklische aromatische Kohlenwasserstoffe (PAK) PY - 2011 UR - http://eprints.dbges.de/551/1/Berichte_der_DBG_Berger3376.pdf SP - 1 EP - 2 AN - OPUS4-24649 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Oliver A1 - Christoph, Gabriele A1 - Kalbe, Ute A1 - Berger, Wolfgang T1 - Monitoring of PAH in aqueous samples - a comparison of different sample preparation techniques T2 - International conference environmental (bio)technologies CY - Gdansk, Poland DA - 2011-09-05 KW - Stir bar sorptive extraction KW - Liquid-liquid extraction KW - Leaching, batch test KW - Column test KW - Complex aqueous matrix PY - 2011 IS - Paper 21 SP - 1 EP - 16 AN - OPUS4-24562 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalbe, Ute A1 - Vogel, Christian A1 - Simon, Franz-Georg T1 - Antimony in incineration bottom ash – Leaching behavior and conclusions for treatment processes N2 - Antimony (Sb) is used in industrial products mainly as flame retardant in plastic material. Due to such additives in plastics, about a half of Sb ends up in municipal solid waste incineration at the end-of-life and consequently in relevant amounts in the generated bottom ash. In contact with water, the initial leachability is low, as antimonates form sparingly soluble compounds with Ca2+. Following the carbonation of the incineration bottom ash (IBA) during the proceeding ageing the pH in the leachates decreases. With decreasing concentration of Ca in the eluate the solution equilibrium changes and antimonates dissolve. In Germany it is intended to regulate Sb in IBA with the planned implementation of the so called Mantelverordnung (MantelVO, containing provisions on the utilisation of mineral waste) in the near future. The limit values set in the draft might be critical for IBA and therefore pose a risk for the utilisation of the mineral fraction of IBA in the well-established recycling routes. T2 - SUM 2020 – 5th Symposium on Urban Mining and Circular Economy CY - Online meeting DA - 18.11.2020 KW - Bottom ash KW - Leaching KW - Antimony PY - 2020 SP - 1 EP - 4 AN - OPUS4-51622 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Berger, Wolfgang A1 - Kalbe, Ute A1 - Krüger, Oliver A1 - Hennecke, D. A1 - Hoffe, S. T1 - Validierungsringversuche für E DIN 19527 Elution von Feststoffen - Schüttelverfahren zur Untersuchung des Elutionsverhaltens von organischen Stoffen mit einem Wasser/ Feststoff-Verhältnis von 2 l/kg für Boden- und andere geeignete Materialien N2 - Für die vom Bundesumweltministerium vorgesehene Mantelverordnung sind validierte Unter-suchungsmethoden erforderlich. Dazu gehört auch die Herstellung von wässrigen Eluaten, z.B. zur Beurteilung der Mobilität von Schadstoffen und der Ableitung von Grenzwerten. Ziel des Vorhabens war es, auf der Grundlage geeigneter Testmaterialien (mit prioritären organischen Schadstoffen kontaminierte Böden und Bodenmaterialien) Ringversuche zur Validierung des Schüttelverfahrens nach E DIN 19527 und des Säulenverfahrens für die Übereinstimmungs-untersuchung nach DIN 19528 durchzuführen. Auf der Grundlage der Untersuchungsergebnisse sollten beide Normen bezüglich der Vorgehensweise präzisiert werden und es sollten die während des Ringversuchs ermittelten Verfahrenskenndatenn zur Validierung der Normen herangezogen werden. Darüber hinaus sollten Säulen- und Schüttelverfahren als Übereinstimmungstest vergleichend bewertet werden. Es wurden vier geeignete Ringversuchsmaterialien hergestellt und an insgesamt 18 Ringversuchsteilnehmer ausgegeben. Die Auswertung der Ringversuche erfolgte auf der Grundlage klassischer Statistik nach DIN ISO 5725 mit Hilfe der AuswertesoftwareProLab 2011 (quo data). Auf der Grundlage der Validierungsringversuche wurden die Verfahrenskenndaten für die Norm DIN 19527 ermittelt. Die statistische Auswertung der eingereichten Datensätze war aufgrund der großen Streubreite der Daten schwierig. Die vorgeschriebenen statistischen Methoden zur Datenauswertung adressieren die Behandlung nicht gleichverteilter Datensätze nur ungenügend. Das muss bei der Bewertung der Ergebnisse und deren Zuverlässigkeit berücksichtigt werden. Generell kann festgestellt werden, dass keine signifikanten Unterschiede zwischen den Ergebnissen der Schüttel- und Säulenelution beobachtet werden. Dabei werden beim Schüttelverfahren tendenziell etwas geringere Gesamtmittelwerte erzielt als beim Säulenverfahren, die berechneten Vergleichsvariationskoeffizienten sind für das Schüttelverfahren meist etwas niedriger. Dennoch erweisen sich beide Elutionsverfahren bei den eingesetzten Ringversuchsmaterialien als gut vergleichbar. N2 - Validated investigation methods are required for the drafted decree, called “Mantelverordnung”, comprising the amendment of the Federal Ordinance on Soil Protection and Contaminated Sites, the Federal Ordinance on Mineral Waste Utilization and Groundwater Ordinance published by the German Federal Ministry for the Environment, Nature Conservation and Nuclear Safety in January 2011. These methods include such for the creation of aqueous eluates, which contribute to the evaluation of the mobility of pollutants and the derivation of threshold values. Objectives of the R&D project were interlaboratory tests for the validation of the batch test (E DIN 19527) and the column test using the compliance test option according to DIN 19528 based on contaminated soil test materials with organic pollutants of high priority. Dependent on the test results both standards should be specified concerning the experimental details. Furthermore, the standards shall be validated using the determined performance characteristics. The comparability of column and batch test procedures as compliance tests shall be evaluated in addition. Four appropriate test materials were prepared from two different types of soils, each with the pollutant combinations PAH/PCB and Phenols/TPH/PAH, respectively. These materials were delivered along with test solutions to 18 participants of the interlaboratory comparision. The evaluation of the interlaboratory comparison was carried out on the basis of classical statistics according to DIN ISO 5725. The software ProLab 2011 (quodata) was used for the evaluation. The performance characteristic parameters for the standard DIN 19527 were determined on the basis of the interlaboratory tests. The main challenge was the statistical evaluation due to the fact that the common statistical procedures do not address the evaluation of nonuniformly distributed datasets. This must be considered for the assessment of the results and reliability of the conclusions. However, on a more general level it can be concluded that no significant differences between the batch and column percolation test procedure were observed. The total mean values determined by batch tests tend to be slightly below the values from column tests. The between labvariation coefficients representing the reproducibility of the methods follow the same trend. All in all both methods can be assessed to be equivalent using the materials tested. KW - Kontaminierter Boden KW - PAK KW - PCB KW - MKW KW - Phenole KW - Elutionsverfahren KW - Schütteltest KW - Säulenversuch KW - Validierungsringversuche PY - 2012 SP - 1 EP - 189 AN - OPUS4-53610 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brandt, S. A1 - Brozowski, F. A1 - Plehn, W. A1 - Horn, Wolfgang A1 - Müller, B. T1 - Further Development of Odour Testing of Building Products – Sample Presentation and Evaluation of Perceived Intensity N2 - Indoor air quality is affected by the emission of volatile organic compounds (VOC) or the odour from building products. Odours can be measured by applying the standard ISO 16000-28:2020. In the study presented here proposals for further technical development of the ISO method are presented. The sampling procedure and evaluation method of the perceived intensity are investigated in particular because they have a major influence on reproducibility of measurement results. T2 - 17th International Conference HEALTHY BUILDINGS EUROPE 2021 CY - Online meeting DA - 21.06.2021 KW - Geruchsmessung KW - Emissionen KW - Bauprodukte KW - VOC KW - Perceived Intensity PY - 2021 SN - 978-82-536-1728-2 VL - 2021 SP - 1 EP - 4 PB - SINTEF Books CY - Oslo, Norwegen AN - OPUS4-54574 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brandt, S. A1 - Brozowski, F. A1 - Horn, Wolfgang A1 - Plehn, W. A1 - Müller, B. T1 - New developments in odour testing: Adapter connects emission test chamber and funnel N2 - Healthy and energy efficient buildings must be free from disturbing odours. Odour emissions from building materials can be measured with the well-known and accepted standard ISO 16000-28 “Indoor air – Part 28: Determination of odour emissions from building products using test chambers”. For commonly used emission test chambers the sample air is collected in containers (bags) and presented to a group of panel members for the purpose of evaluating the odour. A standard sets requirements for the on-demand presentation in detail. These include the validation procedure for container materials, pre-treatment of bags, details on storage of filled bags and how to carry out the measurements. However, although these measures are proven in practice, incorrect measurements are still possible. Also errors can occur due to a very complex measurement procedure. So, there is a great need for research into how the odour samples are presented. The proposal planned to be presented will introduce a new development in sample provision by using an adapter which enables collection and provision of sample air without storage or transport of bags. The adapter is a sample container which is permanently positioned on the emission test chamber´s outlet and continuously filled with sample air flowing through it. The flow is briefly interrupted at the time when a sample is taken by a panel member for the test. The size of the container is sufficient to provide enough sample air for evaluation by at least one panel member via a funnel. Since sampling and presentation are technically connected, it means you can almost do away with storage or transportation and thus it can be presented almost unchanged to the panelmembers. The aim is to reduce measurement errors in the odour samples provision process and the improvement of measurement reproducibility. The paper presents the construction of the adapter as well as the results of emission and odour tests carried out so far. T2 - CLIMA 2022 The 14th REHVA HVAC World Congress CY - Rotterdam, The Netherlands DA - 22.05.2022 KW - Perceived Intensity KW - Emissionen KW - Geruch KW - Bauprodukte PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-556192 DO - https://doi.org/10.34641/clima.2022.168 SP - 1 EP - 5 PB - TU Delft open CY - Delft, Niederlande AN - OPUS4-55619 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brandt, S. A1 - Brozowski, F. A1 - Horn, Wolfgang A1 - Müller, B. T1 - Odour testing of building products: Examinations for an on-going development of the test standard ISO 16000-28 N2 - VOC-emissions and their odours from building products and furnishings present indoors should not have an impact on personal well-being or health. Odours can be measured by applying the standard ISO 16000-28. Indoor air determination of odour emissions from building products using test chambers. One of the described procedures is the assessment of perceived intensity using a comparative scale by a group of panellists. In this paper, the perceived intensity sampling procedure and its evaluation method are investigated and shown to need improvement. New technical developments in the methodology used to increase the reproducibility of measurement results are discussed. Since odour tests are used for labelling, they have a major influence on the assessment of construction products, similar to the procedure of the German Committee for Health Evaluation of Building Products (AgBB). In the original ISO standard, the evaluation is typically performed using a sampling container separated from the emission chamber. For a better sample presentation, an adapter was developed to connect the emission test chamber to the evaluation funnel and thus enable an odour assessment which is comparable to a direct measurement. The investigations show that losses of odourous substances can be greatly reduced, which is very desirable when seeking to obtain reliable results in odour measurement. Another experimental series was carried out to reduce the measurement effort in the evaluation of perceived intensity. Application of the developed greater than or less than/equal to. query could be helpful here. The results show that the query mostly leads to the same result as the evaluation of the perceived intensity using the method according to the standard but is much easier to perform. Overall, the results can contribute to improving the acceptance of the evaluation of perceived intensity using ISO 16000-28 and to determining odours from building materials increasingly more precisely. T2 - Healthy Buildings 2023 Europe CY - Aachen, Germany DA - 11.06.2023 KW - Building material KW - Odour KW - Perceived intensity KW - VOC KW - Emission test chamber PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-580070 SP - 345 EP - 352 PB - ISIAQ (International Society of Indoor Air Quality and Climate) CY - Herndon, VA, USA AN - OPUS4-58007 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Habib, Abdel Karim A1 - Schalau, Bernd ED - Przygodda, J. T1 - Erweiterung der empirischen Modellierung der Lachenverdunstung für geringe Windgeschwindigkeiten und hohe Dampfdrücke N2 - Bei der Freisetzung von brennbaren und/oder toxischen Stoffen mit einem Siedepunkt nahe der Umgebungstemperatur (z.B. Fluorwasserstoff) oder von erhitzten Flüssigkeiten, findet die Verdunstung bei höheren Dampfdrücken statt. In diesem Bereich ist der Massenstrom beim Stoffübergang von der flüssigen in die gasförmige Phase mit herkömmlichen Modellen nur noch schwer zu beschreiben. Während der Annäherung an den Siedepunkt findet ein gleitender Übergang von der konzentrationsgradient-dominierten Verdunstung in die wärmestrom-dominierte Verdampfung statt. Die meisten Verdunstungsmodelle wurden entwickelt, um den Stoffübergang bei geringen Dampfdrücken zu beschreiben. Der Verdunstungsmassenstrom berechnet sich aus dem Stoffübergangskoeffizienten, der anhand der Grenzschichtparameter, wie die charakteristische Länge, Windgeschwindigkeit und die Stoffeigenschaften bestimmt wird, und einem Druckterm, der je nach Modell in linearer oder logarithmischer Formulierung vorliegt. Während letztere am Siedepunkt zu einem unendlichen Massenstrom führt, liefert der lineare Ansatz (unterschiedliche) finite Werte. Obwohl unbestritten sein dürfte, dass die Annahme eines unendlichen Massenstromes nicht plausibel ist, stellt sich die Frage welcher Ansatz die Realität in der Nähe der Siedetemperatur am besten wiedergibt. Da für den hier diskutierten Dampfdruckbereich keine veröffentlichten Daten zu finden waren, wurden in der BAM neue Messreihen durchgeführt. In einer beheizbaren Wanne mit 90 cm Durchmesser wurde in Freilandversuchen der Massenstrom für verschiedene Substanzen bei unterschiedlichsten Temperaturen und somit Dampfdrücken bestimmt. Zusammen mit den Ergebnissen früherer Experimente in der BAM zur Verdunstung unter Freilandbedingungen liegt jetzt eine ausreichende Datenbasis für die Bewertung der Modelle und insbesondere der Ansätze für den Druckterm vor. T2 - 12. Fachtagung Anlagen-, Arbeits-und Umweltsicherheit CY - Köthen, Germany DA - 05.11.2015 KW - Lachenverdunstung KW - Dampfdruck KW - Modell PY - 2015 SN - 978-3-86011-091-1 VL - 2015 SP - 1 EP - 11 AN - OPUS4-37189 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Ebell, Gino A1 - Burkert, Andreas A1 - Breit, W. A1 - Adams, R. A1 - Oechsner, M. A1 - Hoche, H. A1 - Körber, D. T1 - Bericht Nr. 165 Technologie- und Sicherheitszuwachs bei der Anwendung von feuerverzinktem Betonstahl zum Ausbau einer nachhaltigen Marktposition im Stahlbetonbau N2 - Die Feuerverzinkung von Betonstahl stellt auf der Grundlage der im Stahlbetonbau geltenden Regelwerke eine zusätzliche Maßnahme zur Steigerung der Dauerhaftigkeit insbesondere bei Korrosionsbeanspruchung infolge Karbonatisierung und/oder Chlorideinwirkung dar. Anders als im Ausland ist die Anwendung von feuerverzinktem Betonstahl in Deutschland bisher kaum verbreitet. Im Rahmen des AiF-Forschungsprojekts IGF 499 „Technologie- und Sicherheitszuwachs bei der Anwendung von feuerverzinktem Betonstahl zum Ausbau einer nachhaltigen Marktposition im Stahlbetonbau“ sollten die einem breiteren Einsatz feuerverzinkter Betonstähle in Deutschland bisher entgegenstehenden offenen Fragestellungen beantwortet werden. Die interdisziplinäre Forschergruppe bestand aus dem Fachgebiet Werkstoffe im Bauwesen, Technische Universität Kaiserslautern (Forschungsstelle 1), mit dem Arbeitsschwerpunkt Fertigungstechnik, der staatlichen Materialprüfungsanstalt Darmstadt an der Technischen Universität Darmstadt (Forschungsstelle 2), mit dem Arbeitsschwerpunkt Werkstofftechnik, und der Bundesanstalt für Materialforschung und –prüfung, Berlin (Forschungsstelle 3), mit dem Arbeitsschwerpunkt Korrosionsschutz. KW - Verzinkter Betonstahl PY - 2017 UR - http://www.gav-verzinken.de/index.php?id=14 SP - 1 EP - 106 AN - OPUS4-40219 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Lucon, E. A1 - Abiko, K. A1 - Lambrecht, M. A1 - Rehmer, Birgit T1 - Tensile properties of commercially pure, high-purity and ultra-high-purity iron: Results of an international round-robin N2 - The room temperature tensile properties of iron with different purity levels (commercially pure, high-purity, and ultra-high-purity) were characterized at different strain rates in the framework of an international Round-Robin involving four laboratories (BAM, IMR-TU, NIST, and SCK•CEN). The test results were collected and analyzed by NIST, and are presented in this Technical Note. Data from all the participating laboratories were found in good agreement, thus allowing a clear assessment of the influence of strain rate and purity level on tensile properties (mechanical resistance and ductility). A clear increase of yield strength and, to a lesser extent, tensile strength was observed for all materials as strain rate increases and purity level decreases. The highest strain rate sensitivity was associated with the highest purity level (ultra-high-purity Fe). Ductility trends were less unequivocal, but typically an increase of elongation at fracture and reduction of area was detected as strain rate and purity level increase. Significant differences in tensile properties were observed between the two investigated types of high-purity Fe, which can be attributed to an influence of the production process in terms of melting environment (atmosphere and crucible), as well as differences in chemical compositions. KW - Commercially pure iron KW - Ductility KW - High-purity iron KW - Purity level KW - Round-Robin KW - Strain rate KW - Tensile strength KW - Ultra-high-purity iron KW - Yield strength KW - Tensile properties KW - Pure iron PY - 2015 DO - https://doi.org/10.6028/NIST.TN.1879 SP - 1 EP - 36 AN - OPUS4-33190 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Henkel, S. A1 - Weidner, A. A1 - Biermann, H. A1 - Kühn, Hans-Joachim A1 - Rehmer, Birgit A1 - Sonntag, Nadja T1 - LCF behavior and microstructure of alpha-brass CuZn30 under uniaxial, planar-biaxial and tension-torsion loading conditions N2 - The low-cycle fatigue behavior of cc-brass CuZn30 was irtvestigated in uniaxial (tension-compression and torional) and biaxial tests under total strain control at room temperature. Planar-biaxial fatigue tests were carried out on a servohydraulic tension-compression testing machine with and without phase shift using a cruciform specimen geometry with fixed principal stress axes. In phase and out of phase tensiontorsion tests were performed using tube shape specimens on a servohydraulic tensiontorsion testing machine. Microstructural investigations were performed by transmission electron microscopy as well as by scanning electron microscope. For all proportional load cases the equivalent strain amplitude based on a maximum shear strain energy criterion results in a similar hardening behavior and in fatigue life times within a scatter band of three. Out of phase loading results in additional cyclic hardening and reduced life time. Planar glide structures were observed in all tested cases as well as areas of pronounced strain localization in the torsional load cases. No evidence of transition to wavy glide behavior was observed. T2 - ICMFF10 - 10. International conference Multiaxial fatigue and fracture CY - Kyoto, Japan DA - 03.06.2013 KW - Fatigue biaxial PY - 2013 SP - 1 EP - 8 AN - OPUS4-32877 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Paetsch, O. A1 - Baum, D. A1 - Prohaska, S. A1 - Ehrig, Karsten A1 - Meinel, Dietmar A1 - Ebell, Gino T1 - 3D corrosion detection in time-dependent CT images of concrete N2 - In civil engineering, the corrosion of steel reinforcements in structural elements of concrete bares a risk of stability-reduction, mainly caused by the exposure to chlorides. 3D computed tomography (CT) reveals the inner structure of concrete and allows one to investigate the corrosion with non-destructive testing methods. To carry out such investigations, specimens with a large artificial crack and an embedded steel rebar have been manufactured. 3D CT images of those specimens were acquired in the original state. Subsequently three cycles of electrochemical pre-damaging together with CT imaging were applied. These time series have been evaluated by means of image processing algorithms to segment and quantify the corrosion products. Visualization of the results supports the understanding of how corrosion propagates into cracks and pores. Furthermore, pitting of structural elements can be seen without dismantling. In this work, several image processing and visualization techniques are presented that have turned out to be particularly effective for the visualization and segmentation of corrosion products. Their combination to a workflow for corrosion analysis is the main contribution of this work. T2 - DIR 2015 - International symposium on digital industrial radiology and computed tomography CY - Ghent, Belgium DA - 22.06.2015 KW - Concrete KW - Corrosion detection KW - 3D computer tomography (CT) imaging KW - Image processing KW - Visualization PY - 2015 SP - 1 EP - 10 AN - OPUS4-33711 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Hydrogen evolution on galvanized rebar in fresh concrete with different chromate-reduced cements N2 - The reduction of the chromate contents in cements affects the electrochemical reactions of galvanized reinforcing steels in fresh concrete. It is important to investigate the critical conditions in the first hours following the pouring of the concrete. T2 - EUROCORR 2015 - European corrosion congress CY - Graz, Austria DA - 06.09.2015 KW - Hydrogen evolution KW - Concrete KW - Galvanized rebar KW - Reinforcement KW - Chromate PY - 2015 SP - paper 9_703 AN - OPUS4-34619 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ebell, Gino T1 - Potentialfeldmessung in Theorie und Praxis N2 - Durch das alkalische Porenwassermilieu ist Stahl im Beton vor Korrosion geschützt. Unter ungünstigen Umgebungsbedingungen (Karbonatisierung, Chlorideintrag) kann die passive Deckschicht auf der Stahloberfläche zerstört werden. Im weiteren Verlauf können sich korrosionsbedingte Folgeschäden, wie Risse und Abplatzungen am Bauwerk ergeben. Um notwendige Sanierungsmaßnahmen sind frühzeitige und weitgehend zerstörungsfrei ermittelte Informationen über das aktuelle Korrosionsverhalten der Stahlbewehrung von großer Bedeutung. Die Potentialfeldmessung ist ein etabliertes und weit verbreitetes Verfahren zur Beurteilung des Korrosionszustandes der Bewehrung in Stahlbetonbauwerken. Mit Hilfe dieses Verfahrens können Bereiche aktiv korrodierender Bewehrung zerstörungsfrei lokalisiert werden. In der Regel kommt diese Messmethode bei der Detektion chloridinduzierter Korrosion zum Einsatz. KW - Korrosion KW - Potentialfeldmessung KW - Corrosion PY - 2018 SP - 1 EP - 21 CY - Berlin AN - OPUS4-45048 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF ED - Ebell, Gino T1 - Lehrgang zum Erwerb des Sachkundenachweises zur Durchführung von potentialfeldmessungen N2 - Durch das alkalische Porenwassermilieu ist Stahl im Beton vor Korrosion geschützt. Unter ungünstigen Umgebungsbedingungen (Karbonatisierung, Chlorideintrag) kann die passive Deckschicht auf der Stahloberfläche zerstört werden. Im weiteren Verlauf können sich korrosionsbedingte Folgeschäden, wie Risse und Abplatzungen am Bauwerk ergeben. Um notwendige Sanierungsmaßnahmen sind frühzeitige und weitgehend zerstörungsfrei ermittelte Informationen über das aktuelle Korrosionsverhalten der Stahlbewehrung von großer Bedeutung. Die Potentialfeldmessung ist ein etabliertes und weit verbreitetes Verfahren zur Beurteilung des Korrosionszustandes der Bewehrung in Stahlbetonbauwerken. Mit Hilfe dieses Verfahrens können Bereiche aktiv korrodierender Bewehrung zerstörungsfrei lokalisiert werden. In der Regel kommt diese Messmethode bei der Detektion chloridinduzierter Korrosion zum Einsatz. T2 - Lehrgang zum Erwerb des Sachkundenachweises zur Durchführung von Potentialfeldmessungen CY - Berlin, Germany DA - 11.06.2018 KW - Korrosion KW - Potentialfeldmessung PY - 2018 SP - 1 EP - 57 CY - Berlin AN - OPUS4-45185 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Corrosion behavior of galvanized reinforcement in chloride containing mortar and carbonated mortar N2 - Korrosionseigenschaften von feuerverzinktem Betonstahl unterscheiden sich grundlegend von herkömmlichen Betonstahl. In diesem Vortrag sind Beispiele für das Korrosionsverhalten in chloridhaltigen und carbonatisierten Mörteln dargestellt T2 - Intergalva 2018 - 25th International Galvanizing Conference CY - Berlin, Germany DA - 17.06.2018 KW - Corrosion KW - Korrosion KW - Verzinkt KW - Betonstahl PY - 2018 SP - 301 EP - 309 AN - OPUS4-45240 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino A1 - Burkert, Andreas ED - Isecke, B. ED - Krieger, J. T1 - Potentialmessung in Theorie und Praxis N2 - Die Potentialfeldmessung dient der kosteneffektiven Instandsetzung von Brückenbauwerken. Mikttels diesem Messverfahren können lokal, aktiv korrodierende, Teilbereiche sondiert werden und im Nachgang instandgesetzt werden. T2 - 3. Brückenkolloquium CY - TAE Esslingen, Germany DA - 18.06.2018 KW - Korrosion KW - Potentialfeldmessung PY - 2018 SN - 978-3-943563-03-0 SP - 271 PB - Technische Akademie Esslingen e.V. CY - Esslingen AN - OPUS4-45239 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kruschwitz, Sabine A1 - Ebell, Gino A1 - Shen, J. T1 - Towards Data Based Corrosion Analysis of Concrete with Supervised Machine Learning N2 - Half-Cell-Potential Mapping (HP) is the most popular non-destructive testing (NDT) method for the detection of active corrosion in reinforced concrete. HP is influenced by parameters such as moisture and chloride gradients in the component. The sensitivity to the spatially small, but dangerous pitting is low. In this study we show how additional measurement information can be used with multi-sensor data fusion to improve the detection performance and to automate data evaluation. The fusion is based on supervised machine learning (SML). SML are methods that recognize relationships in (sensor) data based on given labels. We use SML to distinguish "defective" and "intact" labeled areas in our dataset. It consists of 18 measurement - each contains HP, ground radar, microwave moisture and Wenner resistance data. Exact labels for changing environmental conditions were available in a laboratory study on a reinforced concrete slab, which deteriorated controlled and accelerated. The deterioration progress was monitored continuously and corrosion was generated targeted at a predefined location. The detection results are quantified and statistically evaluated. The SML results shows a significant improvement over the best single method (HP). T2 - NDE/NDT for Highway and Bridges: Structural Materials Technology (SMT 2018) and the International Symposium Non-Destructive Testing in Civil Engineering (NDT-CE 2018) CY - New Brunswick, NJ, USA DA - 27.08.2018 KW - Data fusion KW - Half-cell potential mapping KW - Data based decision making KW - Non-destuctive corrosion testing of concrete KW - Supervised machine learning PY - 2018 SP - 1 EP - 7 AN - OPUS4-45512 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kluge, Martin A1 - Ferrero, Fabio T1 - Modeling helps improve safety in the production of teflon KW - Self ignition KW - Numerical simulation KW - MITD KW - TFE PY - 2011 N1 - Geburtsname von Kluge, Martin: Beckmann-Kluge, M. - Birth name of Kluge, Martin: Beckmann-Kluge, M. SP - 44 EP - 45 AN - OPUS4-23831 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kannengießer, Thomas A1 - Kromm, Arne T1 - Design-specific influences on local weld displacement and hot cracking N2 - The action of thermomechanical effects and of external geometrical restraint conditions on hot crack formation was to be investigated. Autogenous GTA welds have been made on Aluminium 6083 plate under the conditions of free shrinkage as well as varied restraint intensity. Local deformation associated with the moving weld pool was monitored using extensometers placed at opposite ends of the joint. Linear interpolation was used to approximate displacement between the extensometers. External structural restraint and defined variation of the restraint intensity, respectively, have a major impact on the transverse displacement mechanism of the weld edges during welding and are directly linked to solidification cracking. Crack initiation and growth is believed associated with the rapid outward displacement of the material behind the moving weld pool, experienced at the weld start. Outward displacement makes it more difficult to feed solidification shrinkage, the root cause of solidification cracking. As welding proceeds, the rate of outward movement gradually decreases and crack growth eventually stops when local base material begins moving inward (i.e. helping to feed solidification shrinkage). The direction, magnitude, and rate of local deformation (inward vs outward) depends upon a complex interaction between thermal expansion and restraining forces, affected by the restraint intensity. T2 - II. International Conference on Welding and Joining of Materials (ICWJM 2007) CY - Cusco, Peru DA - 2007-04-16 KW - Hot cracking KW - Local weld displacement KW - Restraint intensity KW - Aluminium alloy PY - 2007 SP - 1 EP - 9 PB - Pontificia Universidad Católica del Perú CY - Lima AN - OPUS4-14770 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Gibmeier, J. A1 - Genzel, C. A1 - Mee, V. van der T1 - Determination of Residual Stresses in Low Transformation Temperature (LTT-) Weld Metals using X-ray and High Energy Synchrotron Radiation KW - Filler material KW - Low transformation temperature KW - Synchrotron radiation KW - Phase specific residual stresses KW - Energy dispersive diffraction PY - 2007 IS - II-1658r1-07 SP - 1 EP - 17 PB - International Institute of Welding CY - Paris AN - OPUS4-15716 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Keßler, S. A1 - Gehlen, C. A1 - Eng, M. A1 - Ebell, Gino A1 - Burkert, Andreas T1 - Validierung zerstörungsfreier Messmethoden zur zuverlässigen Erfassung von Bewehrungskorrosion N2 - Die Ergebnisse der Untersuchungen sind in ein Konzept zur Durchführung und Auswertung der Potentialfeld- und Polarisationsmessung eingegangen, um den Ingenieuren in der Praxis ein effizienten Werkzeug zur zerstörungsfreien Erfassung des Korrosionszustandes anzubieten. Das Ziel des Vorhabens wurde erreicht. KW - Potentialfeldmessung KW - Korrosion KW - Betonstahl KW - Elektrolytwiderstand PY - 2011 UR - http://www.cbm.bv.tum.de/fileadmin/w00bdr/www/pdf/Kurzberichte/KB_26.pdf IS - 26 SP - 1 EP - 2 PB - Technische Universität CY - München AN - OPUS4-23838 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Volkmar A1 - Kluge, Martin T1 - Zündgrenzen von Wasserstoff-Sauerstoff-Wasserdampfgemischen unter SWR-typischen Randbedingungen T2 - Jahrestagung Kerntechnik 2004 ; Annual Meeting on Nuclear Technology 2004 CY - Düsseldorf, Deutschland DA - 2004-05-25 PY - 2004 N1 - Geburtsname von Kluge, Martin: Beckmann-Kluge, M. - Birth name of Kluge, Martin: Beckmann-Kluge, M. SP - 75 EP - 84 PB - INFORUM-Verl. u. Verwaltungsges. CY - Berlin AN - OPUS4-3590 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kluge, Martin A1 - Habib, Abdel Karim A1 - van Wingerden, Kees ED - Beyer, Michael ED - Lucassen, Arnas T1 - Large-scale tests to investigate the consequences of exposing cryogenic storage vessels containing liquid hydrogen to a fire load N2 - Large Scale Experiments have been performed to determine whether a storage vessel containing liquid hydrogen (LH2) and caught in a fire engulfing the vessel can result in a BLEVE (Boiling Liquid Expanding Vapour Explosion) and if so its consequences. The tests were performed at the Test Site Technical Safety of the Bundesanstalt für Materialforschung und –prüfung (BAM) in Germany at the Hydrogen Test Area (H2TA) within a research cooperation between BAM and Gexcon as part of the SH2IFT program. Three tests were performed using double-walled vacuum insulated vessels of 1 m3 volume. The cylindrical Vessels differed in orientation (horizontal or vertical) and the insulation material used (perlite or multi-layer insulation (MLI)). The degree of filling of the vessels was approximately 35-40 % in each of the tests performed. The fire load was provided by a propane fed burner-system positioned under the storage vessel and designed to give a homogeneous fire load. The conditions in the vessel (temperatures and pressure) as well as external effects (heat radiation, blast waves, flame ball development and fragmentation) were measured. All vessels were equipped with K-type thermocouples at several locations at the inner and outer vessel shell. The pressure inside the inner vessel and in the space between the inner and outer vessels (vacuum pressure) was measured. Bolometers were used to measure the heat radiation generated by both the propane fire and that generated by a possible fireball/BLEVE. To measure blast generated by the vessel burst/BLEVEs blast pencils were positioned at up to three locations. Further several cameras were used to monitor the events: normal cameras, infrared (IR)-cameras, high-speed cameras also on board of an UAV. Two of these vessels, a horizontal and a vertical vessel both insulated with perlite withstood the fire loading for 1 hour 20 minutes and 4 hours respectively without catastrophic failure. A horizontal vessel insulated with MLI failed by bursting after 1 hour and 6 minutes resulting in a fireball, fragments, and blast wave. T2 - 14th International Symposium on Hazards, Prevention and Mitigation of Industrial Explosions CY - Braunschweig, Germany DA - 11.07.2022 KW - Prevention KW - Industrial explosions KW - BLEVE KW - LH2 KW - Fire ball KW - Fragments PY - 2022 DO - https://doi.org/10.7795/810.20221124 SP - 168 EP - 181 AN - OPUS4-59440 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Potentialfeldmessung in Theorie und Praxis N2 - Durch das alkalische Porenwassermilieu wird Stahl im Beton durch Ausbildung einer Deck-schicht vor Korrosion geschützt. Unter ungünstigen Umgebungsbedingungen (Karbonatisie-rung, Chlorideintrag) kann die passive Deckschicht auf der Stahloberfläche zerstört werden. Im weiteren Verlauf können sich durch Volumenexpansion der Korrosionsprodukte korrosi-onsbedingte Folgeschäden, wie Risse und Abplatzungen am Bauwerk ergeben. Um notwen-dige Sanierungsmaßnahmen sind frühzeitige und weitgehend zerstörungsfrei ermittelte In-formationen über das aktuelle Korrosionsverhalten der Stahlbewehrung von großer Bedeu-tung. Die Potentialfeldmessung ist ein etabliertes und weit verbreitetes Verfahren zur Beur-teilung des Korrosionszustandes der Bewehrung in Stahlbetonbauwerken. Mit Hilfe dieses Verfahrens können Bereiche aktiv korrodierender Bewehrung zerstörungsfrei lokalisiert werden. In der Regel kommt diese Messmethode bei der Detektion chloridinduzierter Korro-sion zum Einsatz. T2 - 3-Länder-Korrosionstagung CY - Zürich, Switzerland DA - 12.04.2018 KW - Korrosion KW - Corrosion KW - Potentialfeldmessung PY - 2018 SN - 978-3-935406-66-6 SP - 123 EP - 128 AN - OPUS4-44697 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Scheuerlein, C. A1 - Rehmer, Birgit T1 - Tensile properties of a non-reacted internal tin NB3SN composite wire calculated from the vickers hardness of its individual phases according to the rule of mixtures N2 - The load-independent Vickers hardness (HV) of the individual phases in a non-reacted Nb3Sn wire has been measured and the yield strength (YS) of the individual components estimated from the HV values. The YS and tensile strength (Rm) of the composite wire are calculated according the rule of mixtures (ROM). Calculated tensile properties are compared with tensile test results that were obtained for the entire composite wire, for the wire after removal of the Cu stabiliser and for single Nb-7.5wt.%Ta fibres. KW - MMC KW - Supraleiter KW - Mischungsregel PY - 2005 UR - https://edms.cern.ch/file/673338/2/Technote-2005-08.pdf SP - 1 EP - 15 PB - CERN CY - Geneva AN - OPUS4-14723 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beckmann, Jörg A1 - Onel, Yener A1 - Finn, Monika A1 - Rehmer, Birgit T1 - Charakterisierung des oxidativen Schädigungsverhaltens infiltrierter faserverstärkter 2D-C/C-Keramiken mit Hilfe der Röntgencomputertomographie T2 - 15. Symposium Verbundwerkstoffe und Werkstoffverbunde CY - Kassel, Deutschland DA - 2005-04-06 KW - Schädigungsuntersuchung KW - Röntgencomputertomographie KW - Oxidation KW - Keramische Verbundwerkstoffe KW - Kohlenwerkstoffe PY - 2005 SP - 421 EP - 426 PB - DGM CY - Kassel AN - OPUS4-7622 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino A1 - Burkert, Andreas A1 - Lehmann, Jens T1 - Auswirkungen des Einsatzes chromatreduzierter Zemente in Verbindung mit verzinktem Stahl T2 - GAV-Forschungskolloquium - Feuerverzinken - Korrosionsschutz zwischen Tradition und Moderne CY - Hannover, Deutschland DA - 2010-03-08 KW - Chromatreduzierter Zement KW - Verzinkter Betonstahl KW - Wasserstoff KW - Beton KW - Verbundzone PY - 2010 SP - 1 EP - 13 CY - Hannover AN - OPUS4-21221 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zeisler, Peter A1 - Droste, Bernhard A1 - Rehmer, Birgit A1 - Rödel, R. ED - Droste, B. ED - Kowalewsky, H. T1 - A new fracture mechanics assessment method for ferritic steel components of type B packages T2 - PATRAM 98 - 12th International conference on the packaging and transportation of radioactive materials CY - Paris, France DA - 1998-05-10 PY - 1998 VL - 1 SP - 309 EP - 316 PB - Nuclear Technology Publishing CY - Paris, France AN - OPUS4-21558 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zeisler, Peter A1 - Droste, Bernhard A1 - Rödel, Roland A1 - Rehmer, Birgit T1 - Current approval procedures for type-B packages in Germany: Selected topics T2 - PATRAM ´95 - 11th International Conference on the packaging and transportation of radioactive materials CY - Las Vegas, Nevada, USA DA - 1995-12-03 PY - 1995 SP - 488 EP - 495 AN - OPUS4-21638 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maierhofer, Christiane A1 - Krankenhagen, Rainer A1 - Röllig, Mathias A1 - Rehmer, Birgit A1 - Gower, M. A1 - Baker, G. A1 - Lodeiro, M. A1 - Aktas, A. A1 - Knaszovicka, L. A1 - Blahut, A. A1 - Monte, C. A1 - Adibekyan, A. A1 - Gutschwager, B. T1 - Characterisation of artificial defects in CFRP and GFRP sheets designed for energy applications using active thermography N2 - The increased use of fibre-reinforced plastic (FRP) composites for improved efficiency and reliability in energy related applications e.g. wind and marine turbine blades, nacelles, oil and gas flexible risers, also increases the demand for innovative non-destructive testing technologies. Thus, in order to achieve increased acceptance of suited and optimized non-destructive testing (NDT) methods in industry, the European Metrology Research Programme (EMRP) project ENG57 Validated Inspection Techniques for Composites in Energy Applications (VITCEA) deals with the development and validation of innovative NDT technologies. In this contribution, results concerning thermographic investigations at test specimens during tensile loading and active thermography testing after tensile loading are presented. Additionally, the determination of the optical properties (relative transmittance and directional spectral emissivity) of CFRP and GFRP test specimens is described. T2 - Conference QIRT 2016 CY - Gdansk, Poland DA - 04.07.2016 KW - Active thermography KW - CFRP KW - GFRP KW - Validation of methods PY - 2016 UR - http://qirt.gel.ulaval.ca/archives/qirt2016/papers/076.pdf DO - https://doi.org/10.21611/qirt.2016.076 SN - 2371-4085 SP - Paper 076, 527 EP - 536 CY - Quebec, Canada AN - OPUS4-37512 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Patrick P. A1 - Kohlhoff, Harald A1 - Hüllmann, Dino A1 - Lilienthal, A.J. A1 - Kluge, Martin T1 - Bringing Mobile Robot Olfaction to the Next Dimension – UAV-based Remote Sensing of Gas Clouds and Source Localization N2 - This paper introduces a novel robotic platform for aerial remote gas sensing. Spectroscopic measurement methods for remote sensing of selected gases lend themselves for use on mini-copters, which offer a number of advantages for inspection and surveillance. No direct contact with the target gas is needed and thus the influence of the aerial platform on the measured gas plume can be kept to a minimum. This allows to overcome one of the major issues with gas-sensitive mini-copters. On the other hand, remote gas sensors, most prominently Tunable Diode Laser Absorption Spectroscopy (TDLAS) sensors have been too bulky given the payload and energy restrictions of mini-copters. Here, we introduce and present the Unmanned Aerial Vehicle for Remote Gas Sensing (UAV-REGAS), which combines a novel lightweight TDLAS sensor with a 3-axis aerial stabilization gimbal for aiming on a versatile hexacopter. The proposed system can be deployed in scenarios that cannot be addressed by currently available robots and thus constitutes a significant step forward for the field of Mobile Robot Olfaction (MRO). It enables tomographic reconstruction of gas plumes and a localization of gas sources. We also present first results showing the gas sensing and aiming capabilities under realistic conditions. T2 - IEEE International Conference on Robotics and Automation (ICRA) CY - Singapore DA - 29.05.2017 KW - Tunable Diode Laser Absorption Spectroscopy (TDLAS) KW - 3-axis gimbal KW - Mobile Robot Olfaction KW - Tomographic reconstruction of gas plumes KW - Localization of gas sources KW - Aerial platform PY - 2017 SN - 978-1-5090-4632-4 SP - 3910 EP - 3916 PB - IEEE AN - OPUS4-40545 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröpfer, Dirk A1 - Mente, Tobias A1 - Kannengießer, Thomas T1 - Kaltrissbildung in Baustählen im Lichte der Regelwerke N2 - Der verstärkte Einsatz höherfester Stähle und Zusatzwerkstoffe erfordert ein vertieftes Verständnis der Zusammenhänge zwischen Schweißverfahren, Wärmeeinbringung, Abkühlbedingungen sowie den daraus resultierenden metallurgischen Vorgängen in der Schweißnaht und deren Umgebung. Nur aus dem Zusammenwirken aller Einflussfaktoren lassen sich Strategien ableiten, mit deren Hilfe die Festigkeitseigenschaften bzw. die Lebensdauer von Schweißkonstruktionen in einem Maße verbessert werden können, die den Einsatz höherfester Werkstoffe rechtfertigen und somit deren Leichtbaupotenzial voll ausgenutzt werden kann. Vorgestellt werden einige beispielhafte Untersuchungen an Schweißverbindungen aus höherfesten Feinkornbaustählen zu Interaktionen der Haupteinflussgrößen auf die Kaltrissbildung. T2 - 17. Tagung Schweißen in der maritimen Technik und im Ingenieurbau CY - Hamburg, Germany DA - 19.04.2017 KW - Kaltrisse KW - hochfeste Feinkornbaustähle KW - Eigenspannungen KW - Wasserstoffbedingte Eigenschaftsdegradation KW - Regelwerke KW - Schweißen KW - Wärmeführung PY - 2017 VL - 2017 SP - 54 EP - 67 AN - OPUS4-41068 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Engelking, Lorenz A1 - Eissel, A. A1 - Schröpfer, Dirk A1 - Treutler, K. A1 - Kannengießer, Thomas A1 - Wesling, V. T1 - Effect of alloy modification for additive manufactured Ni alloy components on microstructure and subsequent machining properties N2 - Ni alloys are generally classified as difficult-to-cut materials and cost intensive. Additive manufacturing (AM) offers economic advantages. However, machining of these AM components is mandatory to create the final contour or surface. The inhomogeneous and anisotropic microstructure and properties of AM components causes an unstable cutting process. Moreover, undesirable tensile residual stresses are generated due to subsequent machining. In this investigation, the initial alloy 36 is modified with Ti and Nb up to 1.6 wt.-% and build-up welded via gas metal arc welding (GMAW) and plasma-transferred-arc (PTA). Then, finish-milling tests are carried out to investigate the influence of the modification as well as the cutting parameters on the resulting cutting force and the surface integrity. In addition, the conventional milling process (CM) is compared with the ultrasonic-assisted milling process (US), which has a significant influence on the machinability as well as on the surface integrity. T2 - Additive Fertigung – Werkstoffe – Prozesse – Wärmebehandlung 2022 CY - Bremen, Germany DA - 29.06.2022 KW - Additive manufacturing KW - Alloy 36 KW - Alloy modification KW - Ultrasonic-assisted milling KW - Surface integrity PY - 2022 SP - 57 EP - 67 AN - OPUS4-55430 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erxleben, Kjell A1 - Kaiser, Sebastian A1 - Rhode, Michael A1 - Kannengießer, Thomas A1 - Hadick, C. A1 - Schu, K. T1 - Quantification of hydrogen uptake during in-service hydrogen pipeline welding N2 - Hydrogen must be transported on a large scale from producers to consumers to ensure the energy transition. The necessary pipeline grid is achieved by conversion of the natural gas (NG) grid and building new pipelines. Welding during service as part e.g. of “hot-tapping” is unavoidable for maintenance/repair/expansion. Based on existing studies, the basic material compatibility of (low-alloyed) pipeline steels with hydrogen is postulated. However, this cannot be assumed for the case of in-service welding on pipelines in pressurized condition. The reason is the increased temperature e.g. by preheating and (in particular) during welding of the single passes. As a result, the inner pipeline surface undergoes multiple short-term heating but to high temperatures. In particular, the first passes can result in a temperature close to the austenitic transformation of the material for small wall thicknesses. Both increase the hydrogen uptake into the welded joint. If hydrogen embrittlement is likely to occur, depends on the hydrogen uptake, which must be quantified. For this purpose, welding experiments on pressurized demonstrators were conducted. The hydrogen uptake at 100 bar was compared to reference experiments with nitrogen. A new sample extraction routine for the quantification of the weld-zone specific hydrogen uptake was established. Comprehensive experiments with different steels (P235, L360, L485), wall thicknesses (4.1 mm to 7.8 mm) and diameters (DN50 and DN200) were conducted. In addition, the influence of the welding layer sequence on the hydrogen uptake between single- and multi-layer welds was investigated. Analytical approaches were used to approximate the hydrogen uptake in the respective weld zones. The main findings were that the layer sequence and especially the wall thickness have a large influence on the hydrogen uptake. T2 - 20th Pipeline Technology Conference ptc2025 CY - Berlin, Germany DA - 06.05.2025 KW - In-service KW - Hydrogen KW - Pipeline KW - Repair welding KW - component test PY - 2025 SP - 1 EP - 12 AN - OPUS4-63166 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Monavari, Mehran A1 - Prellwitz, Matthias A1 - Muth, Thilo A1 - Eichstädt, Sascha A1 - Koch, Claudia T1 - Quality-X: A Federated Digital Ecosystem for the Future Quality Infrastructure N2 - Harmonized and interoperable national Quality Infrastructure (QI) systems are essential for fostering cooperation, promoting mutual trust, and facilitating trade. The true potential of the QI is realized when its elements and actors are seamlessly integrated into a cohesive digital QI ecosystem. Recent developments towards industrial international data spaces enable such an ecosystem but require the integration of QI principles. Recognizing the lack of such a platform, Quality-X aims at setting the stage for the implementation of a QI ecosystem in international data spaces (IDS), GAIA-X and related German and European projects dedicated to secure data sharing. Quality-X is not about the construction of a platform; it is the creation of an inclusive QI ecosystem with harmonized interfaces. Instead of imposing rigid data structures, it prioritizes interoperability. Through the utilization of Decentralized Identifiers (DIDs), Verifiable Credentials, and Identity Hubs, Quality-X seeks seamless interactions across diverse service provider systems. This white paper introduces the concept and vision of Quality-X and discusses the general prerequisites for integrating QI processes within data spaces. Further on, we introduce existing testbeds, which will serve as an experimental proving ground for exploring various use cases related to the implementation of the vision of a QI-Digital. +++ Harmonisierte und interoperable nationale Qualitätsinfrastrukturen (QI) sind für die Förderung der Zusammenarbeit, des gegenseitigen Vertrauens und der Erleichterung des Handels unerlässlich. Das wahre Potenzial der QI kommt zum Tragen, wenn ihre Elemente und Akteure nahtlos in ein kohärentes digitales QI-Ökosystem integriert werden. Die jüngsten Entwicklungen hin zu industriellen internationalen Datenräumen ermöglichen ein solches Ökosystem, erfordern jedoch die Integration von QI-Prinzipien. Angesichts des Fehlens einer solchen Plattform zielt Quality-X darauf ab, die Voraussetzungen für die Umsetzung eines QI-Ökosystems in internationalen Datenräumen (IDS), GAIA-X und verwandten deutschen und europäischen Projekten zum sicheren Datenaustausch zu schaffen. Bei Quality-X geht es nicht um den Aufbau einer Plattform, sondern um die Schaffung eines umfassenden QI-Ökosystems mit harmonisierten Schnittstellen. Anstatt starre Datenstrukturen aufzuerlegen, steht die Interoperabilität im Vordergrund. Durch die Verwendung von dezentralen Identifikatoren (DIDs), überprüfbaren Berechtigungsnachweisen und Identitäts-Hubs strebt Quality-X eine nahtlose Interaktion zwischen verschiedenen Systemen von Dienstleistern an. Dieses Whitepaper stellt das Konzept und die Vision von Quality-X vor und erörtert die allgemeinen Voraussetzungen für die Integration von QI-Prozessen in Datenräumen. Darüber hinaus stellen wir bestehende Testbeds vor, die als experimentelles Versuchsfeld für die Erforschung verschiedener Anwendungsfälle im Zusammenhang mit der Umsetzung der Vision einer QI-Digital dienen sollen. KW - Quality Assurance KW - Quality Infrastructure KW - Data Spaces KW - Digitalization KW - Quality Management KW - Interoperability KW - Verification KW - Identification KW - Certificate KW - Datenräume KW - Qualitätsinfrastruktur KW - Gaia-X KW - Manufacturing-X KW - Catena-X KW - Datenökosystem KW - Qualitätssicherung KW - Qualitätsmanagement PY - 2023 UR - https://www.qi-digital.de/fileadmin/user_upload/website/publikationen/1022_Brosch%C3%BCre_Quality-X_v4.pdf SP - 1 CY - Berlin AN - OPUS4-59354 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - O'Connor, Daniel A1 - Evans, Alexander A1 - Balsamo, Alessandro A1 - Favres, Georges A1 - Przyklenk, Anita A1 - Bosse, Harald A1 - Phillips, Dishi T1 - European Metrology Network (EMN) for Advanced Manufacturing ─ Development of the Strategic Research Agenda (SRA) N2 - The European Commission has identified Advanced Manufacturing and Advanced Materials as two of six Key Enabling Technologies (KETs). It is considered that Metrology is a key enabler for the advancement of these KETs. Consequently, EURAMET, the association of metrology institutes in Europe, has strengthened the role of Metrology for these KETs by enabling the creation of a European Metrology Network (EMN) for Advanced Manufacturing. The EMN is comprised of National Metrology Institutes (NMIs) and Designated Institutes (DIs) from across Europe and was formally established in October 2021. The aim of the EMN is to provide a high-level coordination of European metrology activities for the Advanced Manufacturing community. The EMN itself is organized in three sections representing the major stages of the manufacturing chain: 1) Advanced Materials, 2) Smart Manufacturing Systems, and 3) Manufactured Components & Products. The EMN for Advanced Manufacturing is engaging with stakeholders in the field of Advanced Manufacturing (large companies & SMEs, industry organisations, existing networks, and academia), as well as the wider Metrology community, including Technical Committees, to provide input for the Strategic Research Agenda (SRA) on Metrology for Advanced Manufacturing. This contribution will give an overview about the first version of the SRA prepared by the EMN for Advanced Manufacturing T2 - Euspen, 23rd International Conference & Exhibitio CY - Copenhagen, Danmark DA - 12.06.2023 KW - European Metrology Network (EMN) KW - Advanced Manufacturing KW - Metrology KW - Strategic Research Agenda (SRA) PY - 2023 SP - 363 EP - 364 AN - OPUS4-59196 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Breese, Philipp Peter A1 - Becker, Tina A1 - Oster, Simon A1 - Metz, C. A1 - Altenburg, Simon T1 - In-situ defect detection via active laser thermographic testing for PBF-LB/M N2 - Great complexity characterizes Additive Manufacturing (AM) of metallic components via laser powder bed fusion (PBF-LB/M). Due to this, defects in the printed components (like cracks and pores) are still common. Monitoring methods are commercially used, but the relationship between process data and defect formation is not well understood yet. Furthermore, defects and deformations might develop with a temporal delay to the laser energy input. The component’s actual quality is consequently only determinable after the finished process. To overcome this drawback, thermographic in-situ testing is introduced. The defocused process laser is utilized for nondestructive testing performed layer by layer throughout the build process. The results of the defect detection via infrared cameras are shown for a research PBF-LB/M machine. This creates the basis for a shift from in-situ monitoring towards in-situ testing during the AM process. Defects are detected immediately inside the process chamber, and the actual component quality is determined. T2 - Lasers in Manufacturing (LiM) CY - Munich, Germany DA - 26.06.2023 KW - Additive manufacturing KW - Laser powder bed fusion KW - Nondestructive testing KW - Laser thermography KW - Defect detection PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-585060 SP - 1 EP - 10 PB - Wissenschaftliche Gesellschaft Lasertechnik und Photonik (WLT) CY - Hannover AN - OPUS4-58506 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mohr, Gunther A1 - Altenburg, Simon A1 - Hilgenberg, Kai ED - Wei, Z. ED - Pang, J. T1 - On critical shifts of the process window due to heat accumulation in laser powder bed fusion N2 - Safety-critical applications of products manufactured by laser powder bed fusion (PBF-LB/M) are still limited to date. This is mainly due to a lack of knowledge regarding the complex relationship between process, structure, and resulting properties. The assurance of homogeneity of the microstructure and homogeneity of the occurrence and distribution of defects within complexly shaped geometries is still challenging. Unexpected and unpredicted local inhomogeneities may cause catastrophic failures. The identification of material specific and machine specific process parameter windows for production of fully dense simple laboratory specimens is state of the art. However, the incorporation of changing thermal conditions that a complexly shaped component can be faced with during the manufacturing process is often neglected at the stage of a process window determination. This study demonstrates the tremendous effect of changing part temperatures on the defect occurrence for the broadly used stainless steel alloy AISI 316L. Process intrinsic variations of the surface temperature are caused by heat accumulation which was measured by use of a temperature adjusted mid-wavelength infrared (MWIR) camera. Heat accumulation was triggered by simple yet effective temporal and geometrical restrictions of heat dissipation. This was realized by a variation of inter layer times and reduced cross section areas of the specimens. Differences in surface temperature of up to 800 K were measured. A severe development of keyhole porosity resulted from these distinct intrinsic preheating temperatures, revealing a shift of the process window towards unstable melting conditions. The presented results may serve as a warning to not solely rely on process parameter optimization without considering the actual process conditions a real component is faced with during the manufacturing process. Additionally, it motivates the development of representative test specimens. T2 - The 76th IIW Annual Assembly and International Conference On Welding And Joining (IIW 2023) CY - Singapore, Singapore DA - 16.07.2023 KW - Additive manufacturing KW - Laser powder bed fusion KW - Laboratory specimens KW - Process parameter optimization KW - Heat accumulation KW - Keyhole porosity KW - Infrared thermography PY - 2023 SP - 1 EP - 8 AN - OPUS4-58024 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Oster, Simon A1 - Maierhofer, Christiane A1 - Mohr, Gunther A1 - Hilgenberg, Kai A1 - Ulbricht, Alexander A1 - Altenburg, Simon T1 - Investigation of the thermal history of L-PBF metal parts by feature extraction from in-situ SWIR thermography N2 - Laser powder bed fusion is used to create near net shape metal parts with a high degree of freedom in geometry design. When it comes to the production of safety critical components, a strict quality assurance is mandatory. An alternative to cost-intensive non-destructive testing of the produced parts is the utilization of in-situ process monitoring techniques. The formation of defects is linked to deviations of the local thermal history of the part from standard conditions. Therefore, one of the most promising monitoring techniques in additive manufacturing is thermography. In this study, features extracted from thermographic data are utilized to investigate the thermal history of cylindrical metal parts. The influence of process parameters, part geometry and scan strategy on the local heat distribution and on the resulting part porosity are presented. The suitability of the extracted features for in-situ process monitoring is discussed. T2 - Thermosense: Thermal Infrared Applications XLIII CY - Online meeting DA - 12.04.2021 KW - SWIR camera KW - Additive manufacturing (AM) KW - Selective laser melting (SLM) KW - Laser beam melting (LBM) KW - In-situ monitoring KW - Infrared thermography PY - 2021 SN - 978-1-5106-4324-6 DO - https://doi.org/10.1117/12.2587913 VL - 11743 SP - 1 EP - 11 PB - SPIE - The international society for optics and photonics AN - OPUS4-52535 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Altenburg, Simon A1 - Scheuschner, Nils A1 - Maierhofer, Christiane A1 - Mohr, Gunther A1 - Hilgenberg, Kai T1 - Thermography in laser powder bed fusion of metals: time over threshold as feasible feature in thermographic data N2 - Thermography is one on the most promising techniques for in-situ monitoring of metal additive manufacturing processes. Especially in laser powder bed fusion processes, the high process dynamics and the strong focus of the laser beam cause a very complex thermal history within the produced specimens, such as multiple heating cycles within single layer expositions. This complicates data interpretation, e.g., in terms of cooling rates. A quantity that is easily calculated is the time a specific area of the specimen is at a temperature above a chosen threshold value (TOT). Here, we discuss variations occurring in time-over-threshold-maps during manufacturing of an almost defect free cuboid specimen. T2 - 15th Quantitative InfraRed Thermography conference CY - Online meeting DA - 21.09.2020 KW - Additive Manufacturing KW - Process monitoring KW - Thermography KW - L-PBF KW - Time over threshold PY - 2020 DO - https://doi.org/10.21611/qirt.2020.005 SP - 1 EP - 5 PB - QIRT Council CY - Quebec, Canada AN - OPUS4-52014 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erxleben, Kjell A1 - Kaiser, Sebastian A1 - Rhode, Michael A1 - Kannengießer, Thomas A1 - Kromm, Arne T1 - Reparaturschweißen zukünftiger, in Betrieb befindlicher Wasserstoffpipelines N2 - Wasserstoff leistet als Energieträger der Zukunft einen entscheidenden Beitrag zur nachhaltigen Energieversorgung, wobei der Transport auf Basis des europäischen Ferngasleitungsnetzes erfolgen wird. Bisherige Untersuchungen zur Werkstoffkompatibilität zeigen, dass die hier verwendeten, niedriglegierten Rohrstähle für Wasserstofftransport unter normalen Betriebsbedingungen (≤ 60 °C, max. 100 bar) grundsätzlich geeignet sind. Die Eignung kann nicht ohne Weiteres übertragen werden, sobald Reparaturschweißungen beispielsweise aufgrund von Wartungsarbeiten an druckführenden, in Betrieb befindlichen, Hochdruckgasleitungen erfolgen. Aus technisch-ökonomischen Gründen werden Schweißarbeiten dabei im Betrieb unter fortwährendem Druck und Gasfluss durchgeführt. Dies soll auch bei Wasserstoffpipelines erfolgen. Dazu im Erdgasnetz angewandte und etablierte Konzepte sind beispielsweise das „Hot-Tapping“ und „Stoppling“. Beim „Hot-Tapping“ wird eine druckführende Pipeline durch Anflanschen eines abgeschlossenen, druckdichten Systems aus Absperrventil und Bohrvorrichtung angebohrt. Dazu müssen sogenannte Überschieber (aus vorgeformten Zylinderhalbschalen) durch Längsnaht verbunden und dann mit Rohrrundnähten am Produktrohr verbunden werden. Für das zum überwiegenden Teil durchgeführte E-Hand-Schweißen sind dabei Vorwärmtemperaturen von ca. 100 °C bzw. 250 °C für die maximale Zwischenlagentemperatur einzuhalten. Besonderer Fokus liegt auf der Betrachtung dünnwandiger Leitungen, da hier beim Schweißen der Rundnähte die Austenitisierungstemperatur an der Innenseite der Pipeline überschritten wird. Dadurch wird eine signifikant höhere Wasserstoffaufnahme in den Leitungsstahl vermutet, mit einer möglichen Degradation der mechanischen Kennwerte bzw. Rissbildung. Durch die langen Schweiß- und Abkühlzeiten wird der Rohrleitungsstahl zudem teilweise stundenlang Temperaturen von bis zu 250 °C ausgesetzt. Neben der klassischen „Versprödung“ muss daher eventuell auch ein sogenannter Hochtemperatur-Wasserstoffangriff betrachtet werden. Diese vorliegende Studie gibt Einblick zur Übertragbarkeit der bekannten Konzepte aus der Erdgastechnik zum Reparaturschweißen. Dazu werden Möglichkeiten und Grenzen momentaner Prüfkonzepte sowie deren Weiterentwicklungen aufgezeigt. Dies umfasst bspw. geeignete Methodiken zur Werkstoffprüfung als auch skalierte Bauteilversuche unter realistischen Druckgas-Betriebsbedingungen einer Pipeline. In diesem Rahmen erfolgt auch die Kurzvorstellung des Kooperationsprojektes von BAM, DVGW und Ferngasnetzbetreibern „H2-SuD“ zum Einfluss der Temperaturführung und Rohrgeometrie auf die Wasserstoffaufnahme. T2 - DVS CONGRESS 2024 CY - Erfurt, Germany DA - 16.09.2024 KW - Reparaturschweißen KW - Pipeline KW - Wasserstoff KW - Im Betrieb PY - 2024 SN - 978-3-96144-269-0 VL - 395 SP - 341 EP - 349 AN - OPUS4-61478 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Altenburg, Simon A1 - Maierhofer, Christiane A1 - Straße, Anne A1 - Gumenyuk, Andrey T1 - Comparison of MWIR thermography and high-speed NIR thermography in a laser metal deposition (LMD) process N2 - Additive manufacturing (AM) offers a range of novel applications. However, the manufacturing process is complex and the production of defect-free parts with high reliability and durability is still a challenge. Thermography is a valuable tool for process surveillance, especially in metal AM processes. The high process temperatures allow one to use cameras usually operating in the visible spectral range. Here, we compare the results of measurements during the manufacturing process of a commercial laser metal deposition setup using a mid-wavelength-IR camera with those from a visual spectrum high-speed camera with band pass filter in the near-IR range. T2 - Conference QIRT 2018 CY - Berlin, Germany DA - 25.06.2018 KW - Additive manufacturing KW - Laser metal deposition KW - ProMoAM KW - Thermography PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-454993 UR - http://www.qirt.org/archives/qirt2018/papers/p35.pdf DO - https://doi.org/10.21611/qirt.2018.p35 SP - 1 EP - 5 PB - QIRT Council CY - Quebec, Canada AN - OPUS4-45499 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ziegler, Mathias A1 - Altenburg, Simon A1 - Krankenhagen, Rainer A1 - Maierhofer, Christiane A1 - Scheuschner, Nils A1 - Marquardt, E A1 - Mühlberger, W. A1 - Nagel, F. A1 - Neumann, E. A1 - Rohwetter, P. A1 - Rutz, F. A1 - Schwake, C. A1 - Schramm, S. A1 - Schwaneberg, F. A1 - Taubert, R. D. T1 - Thermografie und Strahlungsthermometrie - Stand und Trends N2 - In vielen Umgebungen, besonders bei hohen Temperaturen, korrosiven Umgebungen oder auf bewegten oder schlecht zugänglichen Flächen, kann die Temperatur nicht oder nur mit nicht akzeptablem Aufwand mit Berührungsthermometern gemessen werden. Diese Umgebungsbedingungen sind unter anderem in der chemischen Industrie, der Lebensmittel-, Metall-, Glas-, Kunststoff- und Papierherstellung sowie bei der Lacktrocknung anzutreffen. In diesen Bereichen kommen Strahlungsthermometer zum Einsatz. Der VDI-Statusreport zeigt typische Anwendungsfelder von nicht radiometrisch kalibrierten Wärmebildkameras und von radiometrisch kalibrierten Thermografiekameras. Um verlässlich mit spezifizierten Messunsicherheiten berührungslos Temperaturen zu messen, müssen die Strahlungsthermometer und Thermografiekameras nicht nur kalibriert, sondern radiometrisch und strahlungsthermometrisch umfassend charakterisiert werden. Auch die optische Materialeigenschaft, der spektrale Emissionsgrad und die Gesamtstrahlungsbilanz (Strahlung des Messobjekts und der Umgebung) sind bei der industriellen Temperaturmessung von großer Bedeutung. In den letzten Jahrzehnten ist dazu ein umfassendes technisches Regelwerk entstanden, das wir Ihnen mit diesem VDI-Statusreport vorstellen. Manche in den Richtlinien beschriebenen Kennwerte mögen abstrakt wirken. In diesem Statusreport zeigen wir an konkreten Beispielen, was diese Kenngrößen für die berührungslose Temperaturmessung bedeuten. Beispiele von Anwendungen zeigen, wo temperaturmessende Thermografiekameras und ausschließlich bildgebende Wärmebildkameras in der Praxis eingesetzt werden. Mit einer Analyse, welche Themen und Anwendungen derzeit besonders intensiv diskutiert werden, versuchen wir Trends für zukünftige Entwicklungen herauszuarbeiten. KW - Thermografie KW - Temperaturmessung PY - 2021 UR - https://www.vdi.de/ueber-uns/presse/publikationen/details/thermografie-und-strahlungsthermometrie-stand-und-trends SP - 1 EP - 40 PB - VDI Verein Deutscher Ingenieure e.V. CY - Düsseldorf AN - OPUS4-52904 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kluge, Martin A1 - Habib, Abdel Karim A1 - van Wingerden, Kees T1 - Unterfeuerung von Flüssigwassersttofftanks - Topologie eines kritischen Behälterversagens N2 - In einer Versuchsreihe im Realmaßstab wurden drei Flüssigwasserstofftanks (LH2) unterfeuert. Hierbei sollte unter anderem geklärt werden, ob es, analog zu druckverflüssigten Gasen, zu einem BLEVE (Boiling Liquid Expanding Vapor Cloud Explosion) kommen kann. Die Experimente wurden auf dem Testareal Wasserstoffsicherheit des Testgeländes Technische Sicherheit der Bundesanstalt für Materialforschung und -prüfung (BAM-TTS) im Rahmen einer Forschungskooperation zwischen der BAM und Gexcon, als Teil des SH2IFT-Programms durchgeführt. Es handelte sich um doppelwandige, vakuumisolierte Tanks von 1 m³ Volumen. Die zylindrischen Tanks unterschieden sich durch ihre Ausrichtung (horizontal oder vertikal) und das verwendete Isoliermaterial (Perlit oder Mehrschichtisolierung (MLI). Der Füllgrad der Tanks betrug bei jedem der durchgeführten Tests etwa 35-40 %. Die Brandlast wurde homogen durch ein propangasbetriebenes Brennersystem erzeugt. Gemessen wurden die Bedingungen im Behälter (Temperaturen und Druck) sowie äußere Randbedingungen und Auswirkungen beim Versagen (Wärmestrahlung, Druckwellen, Flammenballentwicklung und Fragmentierung). Mit Bolometern wurde die Wärmestrahlung gemessen, die sowohl durch das Propanfeuer als auch durch einen möglichen Feuerball/BLEVE erzeugt wurde. Zur Messung der durch das Bersten von Behältern/BLEVEs erzeugten Druckwellen wurden sog. Pencil-Probes verwendet. Des Weiteren wurden mehrere Kameras zur Überwachung der Experimente eingesetzt: Normalbildkameras, Infrarot (IR)-Kameras und Hochgeschwindigkeitskameras, sowohl bodengestützt als auch mittels einer Drohne. Zwei der untersuchten Tanks, ein horizontaler und der vertikale, die beide mit Perlit isoliert waren, hielten der Brandbelastung stand, ohne dass es zu einem Behälterversagen kam. Der mit MLI isolierte horizontale Behälter barst nach 1 Stunde und 6 Minuten und erzeugte dabei einen Feuerball, Trümmerflug und eine Druckwelle. Neben der Beschreibung der Auswirkungen eines kritischen Versagens eines LH2-Tanks sind weitere Ziele der Arbeit die Identifizierung kritischer Behälterzustände sowie die Erstellung eines umfassendes Datensatzes der Trümmer des geborstenen Tanks. Die größten Abstände für kritische Abstände ergaben sich durch Fragmentwurf. Hier sollen 3D-Scans für die Verwendung in CAD und FEM Anwendungen bereitgestellt werden. Umfassende Daten zu den Fragmentwurfweiten, -massen und -positionen wurden bereits publiziert. Damit soll die Voraussetzung geschaffen werden, um vorhandene Wurfweitenmodelle, die bisher nur für einschalige Behälter konzipiert wurden auf ihre Eignung für mehrschalige Behälter zu überprüfen oder mögliche Anpassungen anhand der realen Daten vornehmen zu können. Zudem wurde damit begonnen die nicht geborstenen Tanks zu vermessen und zu zerlegen, um u.a. die Perlit-Schüttung auf Beeinträchtigungen durch den Transport und die Unterfeuerung zu untersuchen. T2 - Magdeburg-Köthener Brandschutz- und Sicherheitstagung 2024 CY - Magdeburg, Germany DA - 14.03.2024 KW - LH2 KW - Flüssigwasserstoff KW - Bleve KW - Tank KW - Bersten KW - Unterfeuerung PY - 2024 SN - 978-3-948749-42-2 SP - 117 EP - 126 CY - Magdeburg AN - OPUS4-59711 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Nina A1 - Kromm, Arne A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas T1 - Innovatives Instandsetzungsschweißen von Altstahl: Materialverhalten und Herausforderungen N2 - Aus Gründen der Nachhaltigkeit und Wirtschaftlichkeit gibt es in der stahlverarbeiten-den Industrie einen Trend zum Bauen im Bestand, um kostenintensive Sperrungen oder Rückbau zu vermeiden. Schweißen wird dabei als wirtschaftliches Fügeverfahren im Zusammenhang mit Altstählen kaum genutzt, obwohl Nieten- und Schraubenverbindungen oft unwirtschaftlich sind. Für die Instandsetzung ist häufig beschädigtes Bestands-material durch neue Stähle zu ersetzen bzw. Alt-Neu-Stahl-Mischverbindungen herzu-stellen. Aufgrund der verschiedenen Herstellungsprozesse von Altstählen ist nicht jeder Stahl aus dem 20. Jahrhundert schweißgeeignet. Daher ist zunächst eine Schweißeignungsprüfung erforderlich. In den vorliegenden Untersuchungen wurden verschiedene Altstähle hinsichtlich ihres Schweißverhaltens mittels Dilatometrie analysiert. Ziel war es, eine Datenbasis aus Schweiß-Zustands-Zeit-Diagrammen und Simulationen der Wärmeeinflusszone zu erstellen, um praxisrelevante Schweißuntersuchungen ableiten zu können. Diese geben wesentlichen Aufschluss hinsichtlich ihres schweißmetallurgischen Verhaltens und ihrer Schweißeignung. Solche Grundlagen sind zur Entwicklung innovativer schweißtechnischer Konzepte zur beanspruchungsgerechten Instandsetzung bestehender Altstahl-Infrastruktur in Deutschland notwendig. T2 - 6. Symposium Materialtechnik, 20. bis 21. Februar 2025 CY - Clausthal-Zellerfeld, Germany DA - 20.02.2025 KW - Altstahl KW - Schweiß-ZTU Diagramme KW - Instandsetzungsschweißen KW - Schweißeignungsprüfung KW - Dilatometrie PY - 2025 SN - 978-3-8440-9961-4 DO - https://doi.org/10.21268/20250505-1 VL - 15 SP - 370 EP - 380 PB - Shaker Verlag GmbH CY - Düren AN - OPUS4-63377 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krankenhagen, Rainer A1 - Altenburg, Simon A1 - Eisenkrein, Helena T1 - Photothermische Schichtdickenmessung an Betonbeschichtungen - unter Laborbedingungen und auf der Baustelle N2 - Bei der Realisierung von Oberflächen-Schutz-System (OSS) auf Betonflächen ist die tatsächlich erreichte Dicke der Beschichtung ein wesentlicher Parameter, der über die Funktionalität und Langzeitstabilität der aufgetragenen Schicht entscheidet. Die Firma IBOS und die BAM haben in den letzten Jahren gemeinsam einen funktionstüchtigen Prototyp eines Messgeräts zur zerstörungsfreien Schichtdickenmessung für Bodenbeschichtungen entwickelt. Hierin wird die Abkühlkurve eines vorher erwärmten Bereichs berührungslos mit einer IR-Kamera erfasst und mit einem Modell verglichen, was die Bestimmung der Schichtdicke ermöglicht. Im Rahmen dieses Beitrags wird die Umsetzung der Methode unter Laborbedingungen und in der Praxis auf der Baustelle erläutert und diskutiert. T2 - DGZfP-Jahrestagung CY - Leipzig, Germany DA - 07.05.2018 KW - Betonbeschichtung KW - Oberflächenschutzsystem KW - Schichtdickenmessung KW - Zerstörungsfreie Prüfung KW - Photothermisch PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-449433 UR - https://www.ndt.net/?id=23060 SN - 1435-4934 VL - 23 IS - 9 SP - 1 EP - 8 PB - NDT.net CY - Kirchwald AN - OPUS4-44943 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Czeskleba, Denis A1 - Rhode, Michael A1 - Kannengießer, Thomas T1 - Vermeidung von Kaltrissen in UP-Dickblechschweißungen aus hochfesten Stählen N2 - Der Einsatz hochfester Stähle wie S690 erlaubt durch geringeren Materialeinsatz nicht nur eine immer wichtiger werdende Verringerung von CO₂-Emissionen, sondern auch eine effektive Kosten- und Gewichtsreduktion dickwandiger Bauteile. Insbesondere bei Wandstärken von bis zu 200 mm ist das Unterpulver- (UP-)Mehrdrahtschweißen aufgrund seiner hohen Effizienz eine gängige Praxis. Allerdings steigt bei hochfesten Stählen, hier vorliegend S690, die Gefahr wasserstoffunterstützter Kaltrisse (HAC), aufgrund ihrer Mikrolegierungskonzepte im Zusammenspiel mit hohen Eigenspannungen aus dem Schweißprozess und resultierend aus hohen Bauteilsteifigkeiten. Zusätzlich kann die erhebliche Aufmischung von Grund- und Zusatzwerkstoff beim UP-Schweißen zu risskritischen Gefügen führen, in denen der diffusible Wasserstoff besonders schädlich wirkt. Für Gefüge UP-geschweißter Bauteile liegen keine gesicherten Daten bezüglich Wasserstoffdiffusionskoeffizienten bzw. HAC-Rissanfälligkeit vor. Insbesondere die mikrostrukturabhängige Diffusion von durch den UP-Schweißprozess eingebrachtem Wasserstoff war nicht hinreichend gesichert. Ziel des Forschungsvorhabens war es daher, einen Beitrag zur kaltrisssicheren UP-Schweißverarbeitung hochfester Dickbleche zu leisten. Hierzu wurden systematisch unterschiedliche GW (S690 TM/QL) untersucht, die sich insbesondere in ihren Mikrostrukturen unterscheiden. Diese zeigten in Voruntersuchungen stark divergente Härteverteilungen im Besonderen in der letzten Lage der Schweißung, sodass ein ebenfalls stark divergentes Diffusionsverhalten postuliert wurde. Zunächst wurde der Wasserstoffeintrag über die Draht-Pulver-Kombination gemäß ISO 3690 ermittelt. Anschließend erfolgten mehrlagige Schweißungen sowohl unter freiem Schrumpfen als auch unter äußerer Zwängung. Eine detaillierte Gefügecharakterisierung und mechanisch-technologische Prüfungen, sowie Eigenspannungsmessungen ermöglichten die Bewertung der Rissanfälligkeit bei variierter Wärmeführung (schweißgeschwindigkeitsgesteuert). Zur quantitativen Beschreibung der Wasserstoffdiffusion wurden das Schweißgut (SG), die Wärmeeinflusszone (WEZ) und die Grundwerkstoffe (GW) mittels elektrochemischer Beladung und Trägergasheißextraktion (TGHE), sowie Permeationsversuchen untersucht. Basierend auf den ermittelten Diffusionskoeffizienten wurden numerische Modelle erstellt, um den Einfluss verschiedener Diffusionskoeffizienten auf die Wasserstoffverteilung in der Schweißnaht zu evaluieren. Entgegen dem Postulat wurden keine signifikanten Unterschiede in der Wasserstoff-Diffusionsgeschwindigkeit gemessen. Beide GW-Klassen (QL vs. TM) als auch das SG und die WEZ wiesen für diesen Werkstofftyp charakteristische Diffusionskoeffizienten mit nur geringen Unterschieden auf. Dies zusammen mit den nur sehr geringen Unterschieden in der Ausprägung der Eigenspannungen und mechanisch-technologischen Eigenschaften der Nähte, weisen auf eine hohe Kaltrisssicherheit hin. Die in allen Untersuchungen geringen Unterschiede zwischen QL und TM sprechen, hinsichtlich des HAC-Risikos aufgrund einer differenten Wasserstoffdiffusion, für die Austauschbarkeit der beiden Werkstoffe in der Produktion. KW - Wasserstoffrisse KW - Unterpulverschweißen KW - Wasserstoffdiffusion PY - 2025 SP - 1 EP - 150 AN - OPUS4-63127 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rhode, Michael A1 - Mente, Tobias A1 - Kannengießer, Thomas A1 - Czeskleba, Denis T1 - Simulation of hydrogen distribution in submerged arc welded heavy plates as tool for evaluating cold cracking sensitivity for offshore structures N2 - Foundation structures for offshore wind turbines are typically made of heavy plate struc-tural steels, such as S420ML, welded by submerged arc welding. Due to the welding process conditions, higher amounts of hydrogen can be introduced. In this context, large plate thicknesses result in long diffusion paths and a prolonged diffusion time for hydrogen at ambient temperature and possible delayed hydrogen-assisted cold cracking. As a result, hydrogen can accumulate in areas of high mechanical stress and strain. Due to the delayed diffusion, a minimum waiting time of up to 48 h must be observed before non-destructive testing can be performed. In addition, the assessment of possible cold crack locations is very complex. For this reason, a numerical model of a component-like weld test was developed to simulate the temperature field during welding and subsequent cooling. A hydrogen diffusion model based on the temporal-local temperature distribution was established. It was applied to simulate the change of hydrogen distribution as a function of temperature cycle during multi-layer welding and further for the entire waiting time interval ≤ 48 h. As a result, crack critical areas could be evaluated in terms of accu-mulated hydrogen. An advantage of the diffusion model is the simulation of a normalized concentration, i.e. between "0" (no hydrogen) and "1" (max. concentration), which can be scaled to experimentally determined hydrogen concentrations. Finally, selected results for increased real hydrogen ingress are presented, which confirm the relatively high crack resistance of the S420 submerged arc welded joint. KW - Hydrogen assisted cracking KW - Diffusion KW - Numerical simulation KW - Offshore steel PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-632416 DO - https://doi.org/10.21268/20250507-6 SP - 1 EP - 12 PB - Technische Universität Clausthal CY - Clausthal-Zellerfeld, Deutschland AN - OPUS4-63241 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erxleben, Kjell A1 - Kaiser, Sebastian A1 - Rhode, Michael A1 - Kannengießer, Thomas A1 - Hadick, C. A1 - Schu, K. T1 - Component test concept for evaluation of in-service welding on pressurized hydrogen pipelines N2 - Hydrogen is set as the energy carrier of tomorrow and most countries will achieve large-scale hydrogen transport through the conversion of the natural gas (NG) grid and the construction of new pipelines. The interaction between hydrogen and the pipeline materials differs fundamentally from that of NG, as hydrogen is readily absorbed into the material. Considering the possible hydrogen embrittlement (HE), the compatibility of the pipeline materials (low-alloyed steels with a wide strength/thickness range) must be investigated. However, pipelines require intervention for maintenance, repair, or grid expansion with welding on/onto the pipelines while in service, i.e. the well-known "hot tapping" and "plugging" or “stoppling”. The challenges compared to NG can be broadly divided into the possible austenitization of the inner pipe material exposed to hydrogen and the welding itself. Both result in a significant increase in hydrogen solubility and could potentially pose challenges in terms of HE. Emphasis is placed on the word "could" because knowledge of "hot tapping" on hydrogen pipelines is scarce due a lack of service experience. To this end, this study proposes a concept for a component-like demonstrator with the objectives: (1) safe feasibility of "hot tapping" on pressurized model hydrogen pipeline sections, (2) facilitate ex-post sample extraction for the purpose of quantifying the absorbed hydrogen concentrations, and (3) ensure in-situ temperature measurement during welding to monitor the pipeline surface temperature. For safety reasons in the event of an unintentional "burn-through", a solid cylinder was inserted in the demonstrator to restrict the hydrogen gas volume to a small, pressurized layer. Reference pipeline surface temperature measurements were ensured on comparable, unpressurized geometries. The investigated range of welding conditions was investigated for representative material/thickness combinations (DN50 to DN200), suggesting the feasibility of the demonstrator for the determination of reliable in-service welding conditions for both installed and new pipelines for hydrogen service. T2 - 20th Pipeline Technology Conference ptc2025 CY - Berlin, Germany DA - 06.05.2025 KW - In-service KW - Hydrogen KW - Pipeline KW - Repair welding KW - component test PY - 2025 SP - 1 EP - 11 AN - OPUS4-63168 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kutz, Philipp A1 - Otremba, Frank A1 - Werner, Jan T1 - Mechanical and Thermal Properties of Composite Material and Insulation for a Single Walled Tank for Cryogenic Liquids N2 - This paper describes the testing methods used to determine the thermal properties of insulation materials and mechanical properties of materials used for the load-bearing structure for pressure tanks (up to 4 bar, relative) and cryogenic liquids (LNG, −166 °C to -157 °C at atmospheric pressure). Goal is to design a transportation tank that does not exceed 4 bars (relative) within 10 h, starting at atmospheric pressure. PUR-foam is a suitable material for the insulation. A 12,5 l small scale tank prototype reached 4 bar (relative) within 87 minutes, which is, regarding the influence of the size, a satisfying result. The mechanical properties change significantly at cryogenic temperatures. The bending modulus is similar at first, but decreases at a certain point by appr. 50 %. However, the maximum stress is much higher and could not be reached within this testing setup. T2 - 26th Assembly Advanced Materials Congress CY - Stockholm, Sweden DA - 10.06.2019 KW - GFRP KW - LNG KW - Lightweight design KW - Thermal properties KW - Mechanical prtoperties PY - 2020 DO - https://doi.org/10.5185/amlett.2020.011457 VL - 11 IS - 1 SP - 1 EP - 6 PB - VBRI Press AN - OPUS4-50216 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Romero-Navarrete, José A. A1 - Otremba, Frank A1 - Sklorz, Christian A1 - Martínez Madrid, M. T1 - Quasistatic rollover threshold of atmospheric road tankers N2 - Several geometrical analytical tools can be used for assessing the potential benefits of any alternative tank shape. The quasistatic evaluation of the cargo-vehicle behavior represents a fast way to objectively determine the roll stability benefits of any potentially new tank shape. In this paper, the geometrical, quasistatic rollover performance of a convex bottom tank shape is compared with that of standard tank shapes, finding that in spite of the lower position of the cargo´s center of gravity in such a tank shape for the un-perturbed condition, it has the same performance as the elliptical tank shape when subjected to Steady lateral acceleration. That as a result of the large cargo´s lateral displacement. Consequently, the combination of a lower center of gravity for the cargo when it is not perturbed, and a Minimum lateral shift due to lateral accelerations inputs, define the conditions for an ideal tank shape. T2 - CONIIN 2020 CY - Online meeting DA - 28.09.2020 KW - Tank shape KW - Road tankers KW - Center of gravity shifting KW - Quasistatic KW - Convex bottom KW - Geometrical analysis PY - 2020 SP - 1 EP - 6 AN - OPUS4-51388 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Romero-Navarrete, José A. A1 - Otremba, Frank A1 - Lozano Guzmán, A. A. T1 - An energy frame of reference to assess vehicle´s physical externalities N2 - Externalities of the road transportation are multidimensional in nature and involve the road-vehicle interaction under different environmental conditions. Estimating the pavement and vehicle damage potentials as a function of the condition sunder which such interaction takes place, is important to avoid accelerated or catastrophic damages in these systems. Such an assessing is crucial from the perspective of pricing the effects of the vehicle on the infrastructure and vice versa. The existing models for pricing such interaction, critically depends on gross average statistical models. In this paper, it is proposed a deterministic approach to realize such an assessment, based upon validated approaches for the pavement damage. The simulation scheme considers different degrees-of-freedom vehicle models, and a discrete asphalt pavement, that make possible the simulation of massive traffic situations on realistic road lengths. T2 - IMECE 2020 CY - Online meeting DA - 16.11.2020 KW - Energy KW - Frame KW - Assess KW - Vehicles PY - 2020 SP - 1 EP - 9 AN - OPUS4-51645 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Richter, Tim A1 - Schröpfer, Dirk A1 - Rhode, Michael A1 - Börner, Andreas T1 - Rührreibschweißen von Hoch- und Mittelentropie-Legierungen N2 - Hoch- und Mittelentropie-Legierungen (engl. High/Medium Entropy Alloys–HEA/MEA) sind relativ neue Werkstoffklassen. Im Gegensatz zu herkömmlichen Le-gierungen bestehen HEA aus fünf bzw. MEA aus drei oder vier Legierungselementen im äquiatomaren Gleichgewicht. Viele HEA weisen aufgrund hervorragender struktu-reller Eigenschaftskombinationen von sehr tiefen bis zu hohen Temperaturen enor-mes Anwendungspotential auf. Die Anwendung für reale Bauteile stellt jedoch die zentrale Frage der Eignung für die fügetechnische Verarbeitung. Dieser Aspekt findet in der weltweiten Materialforschung bisher kaum Beachtung. Anforderungen an die zuverlässige und sichere fügetechnische Verarbeitung dieser Werkstoffe sind von wesentlicher Bedeutung hinsichtlich wirtschaftlicher Bauteilfertigung für spätere po-tenzielle Anwendungsbereiche, bspw. in der Energietechnik. Das Rührreibschweißen (engl. Friction Stir Welding–FSW) stellt hierbei einen vielversprechenden Fügepro-zess dar, dessen Hauptvorteil in der Schweißprozesstemperatur unterhalb der Schmelztemperatur der zu fügenden Werkstoffe liegt. Dies bedingt die Vermeidung der Ausbildung von harten, versprödenden intermetallischen Phasen, wie sie z. B. beim konventionellen Schmelzschweißen von Eisen-Aluminium-Verbindungen auf-treten. Die vorliegende Arbeit stellt grundlegende Untersuchungen zur Schweißbar-keit einer CoCrFeMnNi-Legierung (HEA) und einer CoCrNi-Legierung (MEA) mit dem FSW-Prozess vor. Die Versuchsschweißungen werden mittels mikroskopischer Analysen hinsichtlich des Schweißnahtaufbaus sowie Schweißnahtfehlern charakte-risiert. FSW zeigt sich als grundlegend geeignet zur Verbindungsschweißung der HEA bzw. MEA. Anhand dieser Ergebnisse kann eine weitere Bewertung der Schweißbar-keit erfolgen. T2 - 4 Niedersächsisches Symposium Materialtechnik Clausthal CY - Online meeting DA - 25.02.2021 KW - Hochentropie Legierung KW - Rührreibschweißen KW - Mediumentropie Legierung PY - 2021 SP - 502 EP - 511 AN - OPUS4-52255 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kullolli, Borana A1 - Cuéllar, Pablo A1 - Baeßler, Matthias T1 - On contact problem application for the local behavior of soil-pile interaction N2 - In this paper a shear test, which helps to study local behavior of the soil-pile interaction, is modelled numerically with the Finite Element Method as a 2D plane strain problem. A normal pressure on top and shear displacement on side were applied. So far, the material behavior was considered elastic for the sake of simplicity. The effect of thickness on contact elements and the presence of in plane stress has been highlighted. The purpose of the paper is to find a suitable contact element which represents more close to reality a soil-pile interaction problem under cyclic axial loading. Moreover, an insight on the presence of in-plane stress shows that it needs to be considered cautiously. T2 - ICCE2017 CY - Tirana, Albania DA - 12.10.2017 KW - Contact problem KW - Numerical modelling PY - 2017 SP - 167 EP - 174 PB - Polytechnic University of Tirana CY - Tirana, Albania AN - OPUS4-42962 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schneider, Rudolf T1 - Wasserdiagnose durch die Verwendung von Markern N2 - Die Überwachung des gesamten Wasserkreislaufs auf Mikroverunreinigungen ist aus gesundheitlicher und ökologischer Hinsicht wünschenswert und gewinnt durch den Klimawandel und das zunehmende Erfordernis der Wiederverwendung des Brauchwassers weiter an Bedeutung. Die schnellen und kostengünstigen antikörperbasierten Methoden („Immunoassays“) können helfen, Informationslücken zu schließen und kürzere Reaktionszeiten zu ermöglichen. Von Labormethoden über tragbare Analysengeräte bis hin zu Online-Sensoren sind viele Formate möglich (u. a. ELISA, Abb. 1). Es muss zudem die Bereitstellung der notwendigen, hochqualitativen Antikörper gewährleistet werden. Da aber gilt „1 Analyt – 1 Antikörper“, ist die Herstellung eines Konsenses bezüglich der vordringlich zu bestimmenden Indikatoren/Marker notwendig. Auch die Normung der Verfahren ist parallel in Angriff zu nehmen. KW - Antikörper KW - Immunoassay KW - Abwasser KW - ELISA PY - 2025 UR - https://analyticalscience.wiley.com/content/article-do/wasserdiagnose-durch-die-verwendung-von-markern VL - 2025 IS - 1 SP - 1 EP - 4 PB - WILEY CY - Hoboken, NJ, USA AN - OPUS4-63508 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Karabeliov, Krassimire A1 - Cuéllar, Pablo A1 - Baeßler, Matthias T1 - Großmaßstäbliche zyklische Versuche zum Zugtragverhalten von gerammten Stahlrohrpfählen N2 - Gerammte Stahlrohrpfähle sind das wesentlichste Gründungselement für Offshore-Konstruktionen. Typischerweise kommen diese als Monopiles oder als Mehrpfahlgründungen für Jacket-Konstruktionen zum Einsatz. Für die verhältnismäßig leichten Windenergieanlagen auf See wird bei Mehrpfahlgründungen regelmäßig die Zugtragfähigkeit maßgebend in der Bemessung. Zusätzlich sind Effekte aus wiederholten zyklischen Belastungen zu beachten, die sich auch auf die Zugtragfähigkeit auswirken können. Auch hier ergibt sich eine Besonderheit dadurch, dass im extremwertverteilten Lastspektrum wenige große (Wechsel-)Last-Amplituden entscheidend sind. Die gründungstechnischen Herausforderungen bei der Planung solcher Windparks auf See wurden von einer Reihe von Untersuchungen begleitet. Eine Versuchsserie zur Zugtragfähigkeit von großmaßstäblichen Pfählen wurde auf dem Testgelände der BAM nahe Horstwalde bei Berlin durchgeführt. Hierfür wurde ein Testfeld mit 10 Pfählen angelegt. Die Pfähle wurden monoton auf Zug und zyklisch belastet. Vergleichend wurden dynamische Pfahlprobebelastungen durchgeführt. Zwei der Pfähle wurden mit Dehnungssensoren instrumentiert und es konnte die Pfahl-Boden-Interaktion abschnittsweise ermittelt werden. T2 - 32. Christian Veder Kolloquium CY - Technische Universität Graz, Graz, Austria DA - 20.04.2017 KW - Offshore Windenergieanlagen KW - Pfahlgründungen KW - Zugtragfähigkeit KW - Zyklisches Tragverhalten PY - 2017 SN - 978-3-900484-75-0 IS - 58 SP - 103 EP - 120 PB - Gruppe Geotechnik Graz AN - OPUS4-40201 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kern, Simon A1 - Michalik-Onichimowska, Aleksandra A1 - Riedel, Jens A1 - Panne, Ulrich A1 - King, R. A1 - Maiwald, Michael T1 - “Click” analytics for “click” chemistry – a simple method for calibration-free evaluation of online NMR spectra N2 - Currently research in chemical manufacturing moves towards flexible plug-and-play approaches focusing on modular plants, capable of producing small scales ondemand with short down-times between individual campaigns. This approach allows for efficient use of hardware, a faster optimization of the process conditions, and thus, an accelerated introduction of new products to the market. Driven mostly by the search for chemical syntheses under biocompatible conditions, so-called “click” chemistry rapidly became a growing field of research. The resulting simple one-pot reactions are so far only scarcely accompanied by an adequate optimization via comparably straightforward and robust analysis techniques. Here we report on a fast and reliable calibration-free online high field NMR monitoring approach for technical mixtures. It combines a versatile fluidic system, continuous-flow measurement with a time interval of 20 s per spectrum, and a robust, automated algorithm to interpret the obtained data. All spectra were acquired using a 500 MHz NMR spectrometer (Varian) with a dual band flow probe having a 1/16 inch polymer tubing working as a flow cell. Single scan 1H spectra were recorded with an acquisition time of 5 s, relaxation delay of 15 s. As a proof-of-concept, the thiol-ene coupling between N-boc cysteine methyl ester and allyl alcohol was conducted in non-deuterated solvents while its time-resolved behaviour was characterised with step tracer experiments Through the application of spectral modeling the signal area for each reactant can be deconvoluted in the online spectra and thus converted to the respective concentrations or molar ratios. The signals which were suitable for direct integration were used herein for comparison purposes of both methods. T2 - 4th European Conference on Process Analytics and Control Technology (EuroPACT 2017) CY - Potsdam, Germany DA - 10.05.2017 KW - Online NMR Spectroscopy KW - Process Analytical Technology KW - Click Chemistry KW - Reaction Monitoring KW - Process control KW - Indirect Hard Modeling KW - Spectral Modeling PY - 2017 SP - 156 EP - 157 CY - Frankfurt a. M. AN - OPUS4-40232 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sanayei, Mohammad Hassan A1 - Farhat, A. A1 - Luu, L.-H. A1 - Werner, L. A1 - Rettinger, C. A1 - Philippe, P. A1 - Cuéllar, Pablo T1 - Micromechanical framework for a 3d solid cohesion model - implementation, validation and perspectives N2 - This article presents a solid cohesion model for the simulation of bonded granular assemblies in the frame of 3D discrete element approaches (DEM). A simple viscoplastic cohesion model for 2D geometries is extended to 3D conditions, while its yield criterion is generalized as a hyper-surface in the space of bond solicitations to include torsional moments. The model is then calibrated using experimental results of uniaxial traction at both the microscopic and macroscopic scales with an artificial granular cohesive soil. The paper finally presents some simulated results on the macromechanical sample traction application and briefly discusses the model's current limitations and promising prospects for subsequent works. T2 - VII International Conference on Particle-Based Methods PARTICLES 2021 CY - Hamburg, Germany DA - 04.10.2021 KW - Granular Cohesive Materials KW - DEM KW - Micromechanical Tensile Failure KW - Macromechanical Sample Strength PY - 2021 SP - 1 EP - 10 AN - OPUS4-53716 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mohr, Gunther A1 - Hilgenberg, Kai ED - Eiber, M. T1 - Prozessinduzierte Vorerwärmung beim pulverbettbasierten Laserstrahlschmelzen und deren Auswirkung auf die Bauteileigenschaften austenitischer Stahlbauteile N2 - Heterogene Fehlstellendichten und Mikrostrukturausbildungen sind große Herausforderungen für den Einsatz des pulverbettbasierten Laserstrahlschmelzens (L PBF) besonders für sicherheitskritische Bauteile. Unter der Vielzahl an Einflussfaktoren auf die Qualität und die mechanischen Eigenschaften von L PBF-Bauteilen hat die Zwischenlagenzeit (ILT) bisher wenig Beachtung gefunden. Sie nimmt ebenso wie die Bauteilgeometrie Einfluss auf die thermische Historie während der Fertigung. Ihr Einfluss auf die intrinsische Vorerwärmung ist in Kombination mit der Bauteilhöhe mittels thermografischer Temperaturmessung untersucht worden. Signifikante Unterschiede in der thermischen Historie konnten dabei mit variierenden Schmelzbaddimensionen, Korngrößen und Fehlstellendichten am Beispiel der austenitischen Stahllegierung AISI 316L in Zusammenhang gebracht werden. T2 - DVM 6. Tagung Additiv gefertigte Bauteile und Strukturen CY - Berlin, Germany DA - 03.11.2021 KW - Additive Fertigung KW - Laserstrahlschmelzen KW - In-situ Prozessüberwachung KW - Wärmeakkumulation KW - Zwischenlagenzeit PY - 2021 DO - https://doi.org/10.48447/Add-2021-003 SP - 19 EP - 30 PB - Deutscher Verband für Materialforschung und -prüfung (DVM) CY - Berlin AN - OPUS4-54287 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Richter, Tim A1 - Rhode, Michael A1 - Schröpfer, Dirk T1 - Innovative Multielement-Legierungen: Aktuelle Ergebnisse zur Schweißbarkeit und Anwendungseigenschaften N2 - Multielement-Legierungen (MPEA – multiple pricipal element alloys) stellen eine neue Klasse von Werkstoffen dar, die aus mindestens drei äquiatomaren Legierungselementen mit jeweils einem Gehalt von 5–35 Atom-% bestehen. Somit unterscheidet sich das Legierungskonzept fundamental von konventionellen bspw. Stahl- oder Al-basierten Legierungen. In jüngster Zeit lag der Schwerpunkt auf dem Legierungs-Design der MPEA und der Überprüfung bzw. Erreichung der gewünschten Eigenschaften bzw. -kombinationen. Hierzu werden die egierungselemente gezielt ausgewählt und die Mikrostrukturen ein- und zum Teil auch mehrphasig eingestellt. Ziel sind hochinnovative MPEA mit angepassten Eigenschaften für die industrielle Anwendung. Dabei sollen insbesondere die bei konventionellen Legierungen wesentlichen Zielkonflikte, wie bspw. der Trade-off zwischen Festigkeit und Duktilität, überwunden werden. Darüber hinaus sind mechanische Eigenschaften bei sehr hohen sowie kryogenen Temperaturen bei gleichzeitig höchster Korrosionsbeständigkeit von hohem Interesse. Die Herstellung von Bauteilen erfordert dazu werkstoff- und beanspruchungsgerechte Füge- bzw. Schweißverfahren. Der Schweißeignung von MPEA wurde bis Ende 2021 nur äußert wenig Aufmerksamkeit zuteil. Die Auswirkungen durch Schweißprozesse auf die Metallurgie und die gewünschten Eigenschaften sind bisher kaum bekannt und limitieren die potenzielle Anwendbarkeit als Funktions- oder Konstruktionswerkstoffe. In einem interdisziplinären BAM-Forschungsprojekt werden aktuell grundlegende Untersuchungen zur Schweißverarbeitung und resultierender Mikrostruktur-Anwendungseigenschafts-Beziehung verschiedener MPEA durchgeführt. Insbesondere Wärmeeinflusszone und Schweißgut sind geprägt durch eine Mikrostruktur, die aus Ungleichgewichtszuständen resultiert. Im Falle von MPEA wurde dies bisher nicht systematisch untersucht. Dazu erfolgte im Rahmen des Projektes eine umfassende Literaturauswertung zum Schweißen von MPEA und Zusammenfassung in einer umfassenden, systematischen Datenbasis. Aus diesem Grund sollen in der vorliegenden Studie die bisher bedeutsamsten Erkenntnisse zur Schweißbarkeit von MPEA systematisch nach MPEA-Typ und Schweißverfahren geordnet und mit eigenen aktuellen Forschungsergebnissen verglichen werden. Durch WIG- und Rührreibschweißversuche an den MPEA-Systemen CoCrNiFeMn bzw. CoCrNi konnten im Projektverlauf bereits wesentliche Fragestellungen beantwortet werden. Dazu zählen Auftreten bzw. Verhinderung intermetallischer Phasen/Seigerungen oder deren Auswirkung auf die Eigenschaften der Schweißverbindung (bspw. Festigkeit oder Korrosionsbeständigkeit). T2 - DVS Congress 2022 CY - Koblenz, Germany DA - 19.09.2022 KW - High Entropy Alloy KW - Schweißen KW - Multielementlegierungen PY - 2022 SP - 62 EP - 67 AN - OPUS4-56706 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ebell, Gino T1 - Materialtechnische Untersuchungen an den Spanndrähten N2 - Wasserstoffinduzierte Spannungsrisskorrosion führt zu Standsicherheitsproblemen an Spannbetonbrückenbauwerken mit hochempfindlichen Spannstählen im Spannblockverfahren. KW - Korrosion KW - Spannstahl KW - Spannungsrisskorrosion PY - 2021 SP - 37 EP - 44 PB - Landesbetrieb Straßenwesen Brandenburg CY - Hoppegarten AN - OPUS4-53501 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Sturm, Patrick T1 - Hardening, High-Temperature Resistance and Acid Resistance of One-Part Geopolymers N2 - In this work, one-part geopolymers were synthesized by mixing solid silica and sodium aluminate with water. Pastes were cured at elevated temperatures (60–90 °C) and relative humidity (r.H.) of 80–98 %. After curing the pastes at 80 °C and 80% r.H for one day, the reaction virtually ceased. Depending on the silica source either geopolymer- zeolite composites or zeolite-free geopolymeric gel forms. The compressive strength of the geopolymer-zeolite composites was lower as the compressive strength of a pure geopolymer, mainly due to a significantly denser and glassy microstructure with less interfaces of the latter one. The major part of the thermal dehydration occurred between 60 °C and 200 °C. Up to 700–800 °C only minor changes of the phase assemblage have been observed for the composites. Depending on the paste composition either ceramic or amorphous phases form during exposure to 1000 °C. Compared to other AAM, very low ambient drying/wetting shrinkage/expansion was observed for the mortars The mortars furthermore provide very high resistance against sulfuric acid (pH 1). Huge parts of the corroded layer are not dissolved from the specimen and can still provide protection for a potential substrate. In terms of sulfuric acid resistance, above a critical CaO content, the formation of gypsum is introduced. This causes expansion, cracking and the decrease of the sulfuric acid resistance. KW - Alkali-activation KW - Geopololymers KW - Heat-resistance KW - Acid-resistance PY - 2018 UR - https://pure.tue.nl/ws/files/99010767/20180702_Sturm.pdf SN - 978-90-386-4524-7 SP - 1 EP - 225 PB - Eindhoven University of Technology (TU/e) CY - Eindhoven AN - OPUS4-45597 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kemmlein, Sabine A1 - Rockstroh, Jens A1 - Jann, Oliver ED - Reichl, H. T1 - Investigation on emissions of volatile and semivolatile compounds (VOC, SVOV), dust and ozone from electronic consumer products T2 - Joint International Congress and Exhibition Electronics Goes Green 2004+ CY - Berlin, Germany DA - 2004-09-06 KW - Emission test chamber KW - Emission test cells KW - VOC KW - SVOC KW - Flame retardants KW - Ozone KW - Dust KW - Hardcopy devices KW - Electronics PY - 2004 SP - 1051 EP - 1052 PB - Fraunhofer IRB Verl. CY - Stuttgart AN - OPUS4-5047 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wilke, Olaf A1 - Jann, Oliver A1 - Brödner, Doris T1 - Direkte thermische Extraktion versus Prüfkammer - Emissionsverhalten von Teppichklebstoffen sicher bestimmen PY - 2004 UR - http://www.gerstel.de/pdf/GERSTEL_Aktuell_32_4-5_de.pdf IS - 32 SP - 4 EP - 5 CY - Mülheim an der Ruhr AN - OPUS4-3498 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rockstroh, Jens A1 - Horn, Wolfgang A1 - Juritsch, Elevtheria A1 - Kalus, Sabine A1 - Jann, Oliver ED - de Oliveira, F. ED - Gameiro da Silva, M. ED - Pinto, R. T1 - Investigations on the Emission of organic Acids from Building Products in Emission Test Chambers - Development of a new Test Method T2 - 8th International Conference "Healthy Buildings" CY - Lisboa, Portugal DA - 2006-06-04 KW - Building products KW - Organic acids KW - VOC KW - GC/MS PY - 2006 VL - 4 SP - 45 EP - 48 PB - Universidade do Porto CY - Lissabon AN - OPUS4-12447 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Horn, Wolfgang A1 - Kasche, J. A1 - Jann, Oliver A1 - Müller, D. T1 - Emissions- und Geruchsuntersuchungen an Bauprodukten - Ergebnisse eines UFO-Planprojektes T2 - 8th Workshop "Odour and Emissions of Plastic Materials" CY - Kassel, Germany DA - 2006-03-27 KW - Bauprodukte KW - Emissionen KW - Geruch KW - RAL UZ PY - 2006 SP - 13-1- 13-7 CY - Kassel AN - OPUS4-12259 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kasche, J. A1 - Dahms, A. A1 - Müller, B. A1 - Müller, D. A1 - Horn, Wolfgang A1 - Jann, Oliver T1 - Olfaktorische Bewertung von Baumaterialien T2 - 7th Workshop "Odour and Emissions of Plastic Materials" CY - Kassel, Germany DA - 0005-04-04 KW - Bauprodukte KW - Emissionen KW - Geruch KW - Kammerverfahren KW - VOC PY - 2005 SP - 5-1-5-12 PB - Kassel University Press GmbH CY - Kassel AN - OPUS4-7363 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Schoknecht, Ute A1 - Horn, Wolfgang A1 - Jann, Oliver A1 - Wegner, R. T1 - Biozidemissionen aus Materialien - Umweltforschungsplan des Bundesministeriums für Umwelt, Naturschutz und Reaktorsicherheit PY - 2002 SP - 1 EP - 139 CY - Berlin AN - OPUS4-7299 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Horn, Wolfgang A1 - Jann, Oliver A1 - Kalus, Sabine A1 - Brödner, Doris A1 - Juritsch, Elevtheria ED - de Oliveira, F. ED - Gameiro da Silva, M. ED - Pinto, R. T1 - Classification of OSB Emissions Assessed with a German Evaluation Scheme T2 - 8th International Conference "Healthy Buildings" CY - Lisboa, Portugal DA - 2006-06-04 KW - Construction product KW - VOC emission KW - Odour KW - Chamber test KW - AgBB-Scheme KW - OSB PY - 2006 VL - 4 SP - 59 EP - 62 PB - Universidade do Porto CY - Lissabon AN - OPUS4-12448 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Dürkop, J. A1 - Horn, Wolfgang A1 - Englert, N. A1 - Plehn, W. T1 - Bauprodukte: Schadstoffe und Gerüche bestimmen und vermeiden - Ergebnisse aus einem Forschungsprojekt KW - Bauprodukte KW - Emissionen KW - Geruch KW - AbBB-Schema KW - Kammermessungen PY - 2006 UR - http://www.umweltbundesamt.de/publikationen/bauprodukte-schadstoffe-gerueche-bestimmen SP - 1 EP - 100 CY - Berlin AN - OPUS4-14518 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jann, Oliver A1 - Horn, Wolfgang A1 - Brödner, Doris A1 - Kalus, Sabine A1 - Juritsch, Elevtheria T1 - VOC-Emissionen aus Bauprodukten T2 - VDI Wissensforum "Schadstoffe in bauprodukten - Stoffe, Beurteilung, Sanierung" CY - Mannheim, Deutschland DA - 2007-04-24 PY - 2007 SP - 22 Seiten PB - VDI-Verl. CY - Düsseldorf AN - OPUS4-14818 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Däumling, C. A1 - Brenske, K.-R. A1 - Crump, D. A1 - Funch, L. W. A1 - Hansen, K. A1 - Horn, Wolfgang A1 - Kephalopoulos, S. A1 - Maupetit, F. A1 - Saarela, K. A1 - Tirkkonen, T. A1 - Witterseh, T. T1 - Harmonisation of material emission labelling schemes in the EU T2 - Indoor Air 2008, 11th International Conference on Indoor Air Quality and Climate CY - Copenhagen, Denmark DA - 2008-08-17 KW - Labelling scheme KW - Evaluation system KW - Material emission KW - Harmonisation PY - 2008 SP - 1 AN - OPUS4-18046 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilke, Olaf A1 - Horn, Wolfgang A1 - Jann, Oliver A1 - Kalus, Sabine A1 - Brödner, Doris A1 - Juritsch, Elevtheria A1 - Süßmilch, C. A1 - Kirchner, D. T1 - European interlaboratory study for sampling VOC emissions - Step 2 - Sampling with Tenax tubes at an emission test chamber T2 - Indoor Air 2008, August 17-22, 2008 CY - Copenhagen, Denmark DA - 2008-08-17 KW - VOC KW - Tenax thermal desorption KW - Emission test chamber KW - Proficiency testing KW - Interlaboratory study PY - 2008 IS - Paper ID: 238 SP - 1 AN - OPUS4-17864 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Horn, Wolfgang A1 - Jann, Oliver A1 - Juritsch, Elevtheria A1 - Ramalho, O. A1 - Wargocki, P. A1 - Knudsen, H. A1 - Müller, B. T1 - Detecting odorous compounds emitted from building and consumer products within the European Project SysPAQ T2 - Indoor Air 2008, 11th International Conference on Indoor Air Quality and Climate CY - Copenhagen, Denmark DA - 2008-08-17 KW - Olfactory detection port KW - VOC analysis KW - Thermal extraction KW - Building material KW - Consumer products PY - 2008 IS - Paper 230 SP - 1 AN - OPUS4-18045 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Horn, Wolfgang A1 - Wilke, Olaf A1 - Kirchner, D. A1 - Jann, Oliver A1 - Kemmlein, S. A1 - Kalus, Sabine A1 - Süßmilch, C. T1 - European interlaboratory study for sampling VOC emissions - Step 1 - Liquid samples added on Tenax tubes T2 - Indoor Air 2008, 11th International Conference on Indoor Air Quality and Climate CY - Copenhagen, Denmark DA - 2008-08-17 KW - ISO 16000-6 KW - VOC analysis KW - Interlaboratory study KW - Emission tests KW - Building material PY - 2008 IS - Paper 226 SP - 1 AN - OPUS4-18048 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, B. A1 - Dahms, A. A1 - Knudsen, H.N. A1 - Afshari, A. A1 - Wargocki, P. A1 - Olesen, B. A1 - Berglund, B. A1 - Ramalho, O. A1 - Goschnick, J. A1 - Häringer, D. A1 - Jann, Oliver A1 - Horn, Wolfgang A1 - Nesa, D. A1 - Chanie, E. A1 - Ruponen, M. A1 - Müller, D. T1 - Measuring perceived air quality and intensity by a Sensor System, the European Project SysPAQ T2 - Indoor Air 2008, 11th International Conference on Indoor Air Quality and Climate CY - Copenhagen, Denmark DA - 2008-08-17 KW - Perceived air quality KW - Perceived odour intensity KW - Profiling KW - Sensor system PY - 2008 IS - Paper ID: 530 SP - 1 EP - 8 AN - OPUS4-18302 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jann, Oliver A1 - Horn, Wolfgang A1 - Brödner, Doris A1 - Kalus, Sabine A1 - Juritsch, Elevtheria T1 - Emissionen flüchtiger organischer Verbindungen aus Bauprodukten T2 - VDI Wissensforum "Schadstoffe in Bauprodukten" CY - Mannheim, Deutschland DA - 2008-11-12 KW - Emissionen KW - Bauprodukte KW - Emissionsmesskammern KW - VOC KW - SVOC KW - Geruch KW - AgBB PY - 2008 SP - 1 EP - 22 PB - VDI-Verl. CY - Düsseldorf AN - OPUS4-18452 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Horn, Wolfgang A1 - Jann, Oliver A1 - Müller, B. A1 - Danielak, M. A1 - Müller, D. A1 - Plehn, W. T1 - Bauproduktprüfung und Geruch - Neue Entwicklungen im Rahmen von Label-Systemen T2 - 11. Workshop - Geruch und Emissionen bei Kunststoffen CY - Kassel, Deutschland DA - 2009-03-30 KW - AgBB-Schema KW - VOC KW - Emissionen KW - Geruch KW - Bauprodukte KW - Bewertung Emissionen PY - 2009 SP - 8-1 - 8-9 AN - OPUS4-19224 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kephalopoulos, S. A1 - Däumling, C. A1 - Crump, D. A1 - Funch, L. W. A1 - Horn, Wolfgang A1 - Maupetit, F. A1 - Saarela, K. A1 - Säteri, J. A1 - Tirkkonen, T. A1 - Witterseh, T. T1 - Harmonisation of indoor material emission labelling schemes in the EU - VOC workshop T2 - Healthy buildings 2009 - 9th International conference & exhibition CY - Syracuse, NY, USA DA - 2009-09-13 KW - Labelling schemes KW - Indoor material emissions KW - VOC KW - Framework KW - Harmonisation PY - 2009 IS - Paper 635 SP - 1 EP - 4 CY - Syracuse, NY, USA AN - OPUS4-19925 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Horn, Wolfgang A1 - Wilke, Olaf A1 - Wiegner, Katharina A1 - Jann, Oliver A1 - Kalus, Sabine A1 - Till, Carola T1 - Interlaboratory study with Tenax thermal desorption - Phase 1 - liquid samples added onto tenax tubes T2 - Healthy buildings 2009 - 9th International conference & exhibition CY - Syracuse, NY, USA DA - 2009-09-13 KW - ISO 16000-6 KW - Interlaboratory study KW - VOC KW - External quality management system PY - 2009 IS - Paper 355 SP - 1 EP - 2 CY - Syracuse, NY, USA AN - OPUS4-19923 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wiegner, Katharina A1 - Wilke, Olaf A1 - Jann, Oliver A1 - Brödner, Doris A1 - Scheffer, Harald A1 - Kalus, Sabine A1 - Till, Carola T1 - Study on VOC-Emissions from Oriented Strand Boards (OSB) T2 - Healthy buildings 2009 - 9th International conference & exhibition CY - Syracuse, NY, USA DA - 2009-09-13 KW - Volatile organic compound (VOC) KW - Aldehyde KW - Antioxidant KW - Wood KW - Oriented strand boards (OSB) PY - 2009 IS - Paper 247 SP - 1 EP - 4 CY - Syracuse, NY, USA AN - OPUS4-19928 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, B. A1 - Danielak, M. A1 - Zeidler, O. A1 - Jann, Oliver A1 - Horn, Wolfgang A1 - Müller, D. A1 - Panaskova, J. A1 - Plehn, W. T1 - Labelling of building materials - A combination of emission tests with odour tests T2 - Healthy buildings 2009 - 9th International conference & exhibition CY - Syracuse, NY, USA DA - 2009-09-13 KW - Labelling systems KW - VOCs KW - Odour KW - Sensory tests KW - Emission tests PY - 2009 IS - Paper 323 SP - 1 EP - 4 CY - Syracuse, NY, USA AN - OPUS4-19927 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Horn, Wolfgang A1 - Danielak, M. A1 - Müller, B. A1 - Jann, Oliver A1 - Plehn, W. A1 - Müller, D. T1 - Implentation of odour test methods into labelling procedures of flooring materials T2 - Healthy buildings 2009 - 9th International conference & exhibition CY - Syracuse, NY, USA DA - 2009-09-13 KW - AgBB-Scheme KW - Labelling KW - Flooring material KW - VOC emission KW - Odour PY - 2009 IS - Paper 356 SP - 1 EP - 3 CY - Syracuse, NY, USA AN - OPUS4-19926 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Plehn, W. A1 - Horn, Wolfgang T1 - The blue angel - VOC workshop T2 - Healthy buildings 2009 - 9th International conference & exhibition CY - Syracuse, NY, USA DA - 2009-09-13 KW - AgBB-Scheme KW - Labeling KW - VOC emission PY - 2009 IS - Paper 427 SP - 1 EP - 3 CY - Syracuse, NY, USA AN - OPUS4-19924 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Richter, Matthias A1 - Horn, Wolfgang A1 - Jann, Oliver A1 - Brödner, Doris A1 - Till, Carola T1 - Application of a new gas mixing device to test adsorptive wall materials N2 - With a gas mixing system (GMS) developed in our laboratory we created a gas mixture of four substances. Adsorptive wall materials of four different compositions were exposed to this gas mixture, consisting of 1-pentanol, hexanal, butyl acetate and n-decane. Aim of this study was to scrutinize the ability of these samples to reduce the concentration of the supplied gas. This capacity is expressed in the sorption flux F or area specific adsorption rate respectively. The test was performed referring to a draft of ISO 16000-24. T2 - Healthy buildings 2009 - 9th International conference & exhibition CY - Syracuse, NY, USA DA - 2009-09-13 KW - Gas mixing device KW - Adsorptive wall material KW - Sorption flux PY - 2009 IS - Paper 259 SP - 1 EP - 2 CY - Syracuse, NY, USA AN - OPUS4-20126 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, B. A1 - Dahms, A. A1 - Jakob, B. A1 - Knudsen, H.N. A1 - Afshari, A. A1 - Wargocki, P. A1 - Olesen, B. A1 - Berglund, B. A1 - Ramalho, O. A1 - Häringer, D. A1 - Jann, Oliver A1 - Horn, Wolfgang A1 - Nesa, D. A1 - Loubet, F. A1 - Ruponen, M. T1 - Measuring perceived air quality and intensity by means of sensor systems, the European Project SysPAQ T2 - Healthy buildings 2009 - 9th International conference & exhibition CY - Syracuse, NY, USA DA - 2009-09-13 KW - Sensor systems KW - Perceived air quality KW - Perceived intensity PY - 2009 IS - Paper 326 SP - 1 EP - 4 CY - Syracuse, NY, USA AN - OPUS4-20106 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Richter, Matthias A1 - Jann, Oliver A1 - Horn, Wolfgang A1 - Pyza, Lars T1 - Development and validation of a new gas mixing device for low concentrations N2 - In our laboratory we developed a gas mixing system (GMS) that is capable of producing stable VOC gas mixtures with concentrations of 1-1000 µg m-3. The single gases are produced by evaporating the pure and liquid substances. T2 - Healthy buildings 2009 - 9th International conference & exhibition CY - Syracuse, NY, USA DA - 2009-09-13 KW - Gas mixing device KW - Low VOC concentrations KW - Gas atmosphere PY - 2009 IS - Paper 263 SP - 1 EP - 2 CY - Syracuse, NY, USA AN - OPUS4-20124 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilke, Olaf A1 - Horn, Wolfgang A1 - Jann, Oliver A1 - Kalus, Sabine A1 - Brödner, Doris A1 - Juritsch, Elevtheria A1 - Till, Carola A1 - Kirchner, D. T1 - European interlaboratory study for sampling VOC emissions - Step 3 - Emission test chamber measurements T2 - Healthy buildings 2009 - 9th International conference & exhibition CY - Syracuse, NY, USA DA - 2009-09-13 KW - VOC emission KW - Emission test chamber KW - Round robin test KW - Construction products KW - Tenax thermal desorption PY - 2009 IS - Paper 343 SP - 1 EP - 4 CY - Syracuse, NY, USA AN - OPUS4-20093 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilke, Olaf A1 - Horn, Wolfgang A1 - Wiegner, Katharina A1 - Jann, Oliver A1 - Kalus, Sabine A1 - Till, Carola T1 - Interlaboratory study with Tenax thermal desorption - Phase 2 - Tenax tubes spiked by BAM T2 - Healthy buildings 2009 - 9th International conference & exhibition CY - Syracuse, NY, USA DA - 2009-09-13 KW - ISO 16000-6 KW - Interlaboratory study KW - VOC KW - External quality management system PY - 2009 IS - Paper 345 SP - 1 EP - 2 CY - Syracuse, NY, USA AN - OPUS4-20094 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wiegner, Katharina A1 - Wilke, Olaf A1 - Jann, Oliver A1 - Brödner, Doris A1 - Scheffer, Harald A1 - Kalus, Sabine T1 - Emissionsminderung von Aldehyden durch den Einsatz von Antioxidantien bei der OSB-Plattenherstellung T2 - 8. Holzwerkstoff-Kolloquium - Ressourcenschonender Rohstoffeinsatz und energieeffiziente Technologien CY - Dresden, Deutschland DA - 2009-12-10 KW - OSB KW - VOC KW - Oriented strand board KW - Volatile organic compound KW - Emissionen KW - Reduktion KW - Aldehyde KW - Antioxidantien KW - Holz PY - 2009 SP - 1 EP - 7 AN - OPUS4-20675 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jann, Oliver A1 - Horn, Wolfgang A1 - Brödner, Doris A1 - Kalus, Sabine A1 - Juritsch, Elevtheria T1 - Emissionen flüchtiger organischer Verbindungen aus Bauprodukten T2 - VDI Wissensforum "Schadstoffe in Bauprodukten" CY - Stuttgart, Deutschland DA - 2009-10-21 KW - Emissionen KW - Bauprodukte KW - Emissionsmesskammern KW - VOC KW - SVOC KW - Geruch KW - AgBB PY - 2009 SP - 1 EP - 22 PB - VDI-Verl. CY - Düsseldorf AN - OPUS4-20306 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jann, Oliver A1 - Horn, Wolfgang A1 - Brödner, Doris A1 - Kalus, Sabine A1 - Juritsch, Elevtheria T1 - Emissionen flüchtiger organischer Verbindungen aus Bauprodukten T2 - VDI Wissensforum "Schadstoffe in Gebäuden - Gesunde Innenraumluft - Stoffe, Beurteilung, Sanierung" CY - Köln, Deutschland DA - 2010-11-09 KW - Emissionen KW - Bauprodukte KW - Emissionsmesskammern KW - VOC KW - SVOC KW - Geruch KW - AgBB PY - 2010 N1 - Serientitel: VDI Wissensforum – Series title: VDI Wissensforum IS - Seminar 06F0067005 / Kap. 10 SP - 1 EP - 22 PB - VDI-Verl. CY - Düsseldorf AN - OPUS4-22358 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Horn, Wolfgang A1 - Wiegner, Katharina A1 - Wilke, Olaf A1 - Jann, Oliver T1 - Method validation study for VOC emission measurements N2 - Quality and trueness of results received from measurements are very important for all involved parties, producers and consumers as well; for instance, if the results were used for acceptance of a product within a labeling procedure. Based on an inter-laboratory study with many German, European and US-American laboratories an extemal quality assurance System for the analysis of VOC emitting from products or the measurement in indoor air should be implemented (financed by the German Federal Environmental Agency). A focus was set on the emission test chamber experiments and the connected analytical procedure. VOC have a dominating influence when applying the German AgBB scheme for health evaluation of building products. Therefore it is necessary to ensure that the results between the testing laboratories are comparable. The successful participation to such round robin tests is offen essential for the acceptance of results given by an analytical laboratory. T2 - Indoor Air 2011, 12th International conference on indoor air quality and climate CY - Austin, TX, USA DA - 05.06.2011 KW - Round robin test KW - VOC KW - Construction product KW - Emission PY - 2011 IS - Paper 768 SP - 1 EP - 2 AN - OPUS4-23880 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wiegner, Katharina A1 - Brödner, Doris A1 - Horn, Wolfgang T1 - Correlation of aldehyde emissions and fatty acids content in pine wood and oriented strand boards N2 - Indoor air quality is important for human health and comfort. To ensure good indoor air quality contamination by volatile organic compounds (VOC) should be minimised. The aim of the project is the reduction of unsaturated aldehydes which can emit from oriented Strand boards (OSB): These aldehydes have an impact on the health based evaluation of emissions from products for indoor use according to the AgBB (Ausschuss zur gesundheitlichen Bewertung von Bauprodukten, Committee for Health Evaluation of Building Products) scheine (AgBB 2010). The model OSB were produced in a pilot plant using well known raw materials (Pinus sylvestris at different trunk heights) under using various processing parameters (Wilke et al. 2011). OSB emit predominantly monoterpenes and aldehydes. Aldehydes are oxidation products of fatty acids in wood. The conditions which affect the oxidation process are the fatty acid concentration and composition, the oxygen content, the sample surface and the presence of compounds which indicate, inhibit or stop the oxidation respectively. The oxidation rate rises with an increasing number of double bounds in the fatty acid, e.g. the oxidation rate between oleic, linoleic and linolenic acid correspond to 1:12:24. One of the most important products of fatty acid oxidation is hexanal. It is generated during the oxidation of linoleic acid. This study shows a direct correlation between aldehyde emission and oxidation, hexanal can be used as an indicator for oxidation. T2 - Indoor Air 2011, 12th International conference on indoor air quality and climate CY - Austin, TX, USA DA - 05.06.2011 KW - VOCs KW - Oxidation products KW - Fatty acid KW - Saturated and unsaturated aldehyde KW - Hexanal PY - 2011 IS - Paper 768 SP - 1 EP - 2 AN - OPUS4-23878 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Howard-Reed, C. A1 - Liu, Z. A1 - Cox, S. A1 - Little, J. A1 - Horn, Wolfgang A1 - Wilke, Olaf A1 - Wiegner, Katharina A1 - Persily, A. T1 - Inter-laboratory study approach to validate the performance of a prototype reference material for product emissions testing N2 - Product emissions chamber testing involves a complex protocol with several sources of measurement uncertainty (ASTM, 2010; ISO, 2006). Despite the potential for significant variability in measurement results within and among laboratories, there is no Standard method available to assess the accuracy of emissions chamber test results. Recently, Germany’s Federal Institute for Materials Research and Testing (BAM) started a program to evaluate the performance of laboratories testing for the AgBB (German Committee for Health-related Evaluation of Building Products) labelling scheme (Wilke et al., 2009). Test method validation was conducted through interlaboratory studies (ILS) with over 30 participants. Simultaneously, the National Institute of Standards and Technology (NIST) and Virginia Tech (VT) started a program to develop a series of reference materials that mimic real building products, can be tested in typical emissions chambers, and have independently known emission rates (Cox et al., 2010). BAM, NIST and VT subsequently joined forces to conduct a series of inter-laboratory studies using the prototype reference material. A pilot ILS was conducted with BAM and NIST followed by an expanded ILS with several participating countries. Results from these interlaboratory studies have the potential to define an internationally-accepted Standard approach to validate results from product emissions tests. T2 - Indoor Air 2011, 12th International conference on indoor air quality and climate CY - Austin, TX, USA DA - 05.06.2011 KW - Test method validation KW - Volatile organic compounds KW - Product certification PY - 2011 IS - Paper 768 SP - 1 EP - 2 AN - OPUS4-23883 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brosig, Laura A1 - Horn, Wolfgang A1 - Pyza, Lars A1 - Jann, Oliver T1 - Applicability: Odour measurement based on ISO 16000-28 - enhanced determination of indoor air quality N2 - Odours might cause offensive nuisance and are under suspicion to be directly harmful to health. Surprisingly their assessment is by definition no part of the determination of indoor air quality (yet). As odours emit from building materials as well as from common consumer goods the users awareness increases continuously and demand for improved consumer protection raises. In comparison to well established methods for the determination of volatile organic compounds (VOC) in the air, there is little experience regarding the applicability, comparability and reproducibility of odour measurements. Considering this, the international and the German standardisation take into account odour assessment, e.g. ISO 16000-28 and VDI 4302-1. In Germany the AgBB-Scheme is a mandatory tool for the evaluation of building products and it is intended to implement odour measurement into it. Initially and essentially the newly developed method had to be put to test involving institutes that deal with VOC measurements. To test the applicability of the method an interlaboratory test was conducted. The results and identified potential improvements are presented in this study (Brosig, 2013). T2 - Indoor Air 2014 - 13th International conference on indoor air quality and climate CY - Hongkong, China DA - 07.07.2014 KW - Odour measurement KW - Perceived intensity KW - Hedonic tone KW - VOC KW - Building materials PY - 2014 SP - HP1079, 1 EP - 4 AN - OPUS4-31390 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Richter, Janine A1 - Wilke, Olaf A1 - Jann, Oliver T1 - Emissions of formaldehyde and VOC from wood-based building products N2 - Wood-based materials are well-known sources for formaldehyde emission in the indoor environment. Different testing standards lead to different emission values for the materials. Such standards are compared in this study. Besides scenarios with varying loading factors, air exchange rates and climatic conditions were investigated to evaluate the formaldehyde emission potential of different building products. Under realistic indoor conditions used for the emission chamber tests, exceeding of formaldehyde indoor guide values were obtained. Results showed the need for improvement of wood-based materials with lower formaldehyde emissions and the adaption of testing parameters closer to realistic conditions. T2 - Healthy Buildings 2017 Europe CY - Lublin, Poland DA - 02.07.2017 KW - Formaldehyde KW - Emission chamber testing KW - Particle board KW - OSB PY - 2017 SN - 978-83-7947-232-1 SP - Paper 0175, 1-6 AN - OPUS4-41575 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilke, Olaf A1 - Jann, Oliver T1 - Comparison of Formaldehyde Concentrations in Emission Test Chambers Using EN 717-1 and EN 16516 N2 - For more than 25 years EN 717-1 (Wood-based panels - Determination of formaldehyde re-lease - Part 1: Formaldehyde emission by the chamber method) is the standard for formalde-hyde emission testing of wooden boards. In 2017 EN 16516 (Construction products - Assess-ment of release of dangerous substances - Determination of emissions into indoor air) was published as a new harmonised standard for the emission testing of construction products. Because test chamber conditions are different, both standards give different concentrations for formaldehyde. To determine a conversion factor four test series were set up with different wooden boards. For a loading of 1 m²/m³ the conversion factor is 1.6. This means that the formaldehyde concentration measured under the conditions of EN 16516 is a factor of 1.6 higher compared to EN 717-1. T2 - Conference on Indoor Air CY - Philadelphia, PA, USA DA - 22.07.2018 KW - Loading factor KW - European standard KW - Construction products KW - Air exchange rate PY - 2018 SP - paper 627 AN - OPUS4-45630 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Richter, Matthias A1 - Horn, Wolfgang A1 - Mölders, N. A1 - Sauerwald, T. A1 - Schultealbert, C. A1 - Mull, B. T1 - Two new promising approaches for quality assurance measures for materials emissions testing N2 - Two new approaches towards an emission reference material for use in quality assurance measures for materials emissions testing were developed and intensively tested. The overall goal was to obtain solid materials with homogenous and reproducible (S)VOC release. Since the application in inter-laboratory comparisons is aimed at, it should furthermore be long-term stable to ensure safe shipment to the customer without sustaining compound losses. In the first approach, thermoplastic polyurethane (TPU) was impregnated with the VOC texanol under high-pressure with liquid CO2 as solvent. In the second, styrene (VOC) and the SVOC 2,6-diisopropylnaphthalene (DIPN) were spiked into vacuum grease (VG) and a mixture of paraf-fin/squalane (P/S). For the prediction of the emission rates a finite element model (FEM) was developed for the VG and P/S type materials. All requirements for reference materials were fulfilled, whereas the TPU samples need to be aged for about 10 days until repeatable and re-producible emission rates were obtained. T2 - Indoor Air 2018 CY - Philadelphia, PA, USA DA - 22.07.2018 KW - Emission reference material KW - Volatile organic compounds KW - CO2 assisted impregnation KW - FEM model PY - 2018 SP - 1 EP - 8 AN - OPUS4-45610 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Braun, Ulrike A1 - Eisentraut, Paul A1 - Altmann, Korinna A1 - Kittner, Maria A1 - Dümichen, Erik A1 - Thaxton, K. A1 - Kleine-Benne, E. A1 - Anumol, T. T1 - Accelerated Determination of Microplastics in Environmental Samples Using Thermal Extraction Desorption-Gas Chromatography/Mass Spectrometry (TED-GC/MS) N2 - There is growing interest in quantifying microplastics in environmental samples. This application note presents a thermal extraction desorption-gas chromatography/mass spectrometry (TED-GC/MS) method that is well suited to automation and increased sample throughput. The method is also able to detect all particle sizes in the sample as long as the limit of detection (LOD) is reached and allows analysis of larger samples of 15 to 25 mg or more. Samples were decomposed by thermogravimetric analysis (TGA), and the gaseous decomposition products were trapped on a solid-phase sorbent, followed by thermal desorption‑gas chromatography/mass spectrometry (TD-GC/MS) using an Agilent 5977B GC/MSD coupled to an Agilent 7890B GC. Target microplastic particle (MP) polymers were identified in environmental samples including surface water, finished compost, house dust, and drinking water. Quantification of MP polymers in environmental samples provided LODs of 0.06 to 2.2 μg, allowing the detection of MPs in trace amounts with sample weights of up to 1 g. Method repeatability was adequate for reliable quantification with RSDs of approximately 6 to 12%. KW - Environment KW - Microplastic particles KW - TED-GC/MS KW - Mass content KW - Thermoanalytical PY - 2020 VL - 2020 SP - 1 EP - 8 PB - Agilent Technologies Inc. CY - USA AN - OPUS4-51672 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bernardy, Christopher A1 - Habib, Abdel Karim A1 - Kluge, Martin A1 - Schalau, Bernd A1 - Kant, Hanjo A1 - Schulze, Marcel A1 - Orchini, Alessandro T1 - Sicherheitstechnische Untersuchungen von Wasserstoff Freistrahlflammen bei Hochdruck im Realmaßstab N2 - Wasserstoff als Energieträger gewinnt zunehmend an Bedeutung. Die Untersuchung von Störfallauswirkungen mit Wasserstoff rückt somit stärker in den Fokus. Da Wasserstoff meist unter Druck gelagert und transportiert wird, ist ein zu betrachtendes Szenario die Freisetzung aus einer Leckage mit anschließender Zündung. Die daraus resultierende Freistrahlflamme (Jet Flame) muss hinsichtlich der in die Umgebung emittierten Wärmestrahlung charakterisiert werden. In der Literatur existieren bereits verschiedene Modelle, welche jedoch vermehrt auf Daten aus Kohlenwasserstoffflammen mit geringem Impuls basieren. Zur Überprüfung dieser Modelle wird im Zuge des BAM internen H2 Jet Flame Projektes die sicherheitstechnische Untersuchung von impulsbehafteten Wasserstoff Freistrahlflammen vorgenommen. Hierfür finden Versuche im Realmaßstab auf dem Testgelände Technische Sicherheit der BAM (BAM-TTS) statt. Gegenstand der Untersuchungen ist die Beurteilung der Auswirkungen von realistischen Freisetzungsszenarien hinsichtlich der Flammengeometrie und der freigesetzten Wärmestrahlung. Dabei werden Parameter wie Freisetzungswinkel, Leckagedurchmesser (z.Zt. 1 mm bis 10 mm), Druck (z.Zt. bis max. 250 bar) und Massenstrom (bis max. 0,5 kg/s) variiert. Zusätzlich können auch Einflüsse wie Art der Zündung, Zündort sowie Zündung mit zeitlichem Verzug untersucht werden. Gewonnene Erkenntnisse werden mit den Ergebnissen bereits vorhandener Modelle verglichen und diese im Bedarfsfall weiterentwickelt. Insbesondere wird der Fokus auf die Modellierung der freigesetzten Wärmestrahlung von Wasserstoffflammen gelegt. Herausforderung dabei stellt die IR-Vermessung und Modellierung von Sichtmodellen der Flammen dar. Die Visualisierung der Flammengeometrie wird mit Hilfe mehrerer Infrarot Kamerasystemen (aus mindestens zwei Blickwinkeln) vorgenommen. Bisherige Messungen, die in der Literatur zu finden sind, basieren meist auf instationären Auströmbedingungen. Der hier verwendete Versuchsaufbau ermöglicht ein stationäres Ausströmen für mehrere Minuten und somit eine direkte Vergleichbarkeit mit den existierenden (stationären) Modellen. Weiterhin ist der Versuchsstand umrüstbar für Vergleichsmessungen mit Kohlenwasserstoffen (Methan etc.) sowie Mischungen aus Wasserstoff und Kohlenwasserstoffen. T2 - Magdeburg-Köthener Brandschutz- und Sicherheitstagung 2024 CY - Magdeburg, Germany DA - 14.03.2024 KW - Wärmestrahlung KW - Wassersoff KW - Freistrahlflamme PY - 2024 SN - 978-3-948749-42-2 SP - 137 EP - 146 CY - Magdeburg AN - OPUS4-59912 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Tschirschwitz, Rico A1 - Krentel, Daniel A1 - Kluge, Martin T1 - Druckgasbehälter im Feuer - Auswirkungen im Versagensfall N2 - Es wurden insgesamt 57 Einzelversuche zum Versagen von Druckgasbehältern durchgeführt. Untersucht wurden dabei 11-kg-Propangasflaschen, PKW-Radmuldentanks für LPG sowie CNG-Tanks vom Typ III (Compositetanks mit Aluminiumliner) und Typ IV (Compositetanks mit Polymerliner). Mit 18 hydraulischen Berstversuchen wurde das Versagensverhalten unter kalten Bedingungen charakterisiert. In 39 Unterfeuerungsversuchen mit den gefüllten LPG- und CNG-Tanks, davon 36 mit Tanks ohne Sicherheitseinrichtung, wurde das Behälterversagen durch Brandbeaufschlagung untersucht. Neben verschiedenen Behältermanteltemperaturen und dem Behälterinnendruck wurde auch die Temperatur des gespeicherten Mediums dokumentiert. Dadurch war es möglich, genau zu dokumen-tieren, unter welchen Bedingungen und bei welchem Zustand der Behälter versagt hat. In einem Großteil der Unterfeuerungsversuche mit Behältern ohne Sicherheitseinrichtungen kam es zur Bildung eines Feuerballs, einer massiven Druck- und Temperaturwirkung auf den Nahbereich sowie einer Vielzahl von Fragmenten im Nah- und Fernbereich. In einer Entfernung von l = 7 m wurden Überdrücke von bis zu p = 0,41 bar gemessen. In 30 Unterfeuerungsversuchen kam es zur Fragmentierung des Behälters. Dabei konnten 159 Fragmente mit Wurfweite und Masse dokumentiert werden. Die dabei maximal festgestellte Wurfweite eines Fragments lag bei l = 311 m. T2 - 15. BAM-PTB-Kolloquium zur chemischen und physikalischen Sicherheitstechnik CY - Brunswick, Germany DA - 21.05.2019 KW - Behälterversagen KW - Druckgasbehälter KW - Propan KW - LPG KW - CNG PY - 2020 DO - https://doi.org/10.7795/310.20200199 SN - 0030-834X VL - 130 IS - 1 SP - 55 EP - 70 AN - OPUS4-50570 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Mietz, Jürgen A1 - Raupach, M. A1 - Ebell, Gino A1 - Poltavtseva, Marina A1 - Helm, C. T1 - Untersuchungen zur Anwendbarkeit leitfähiger Beschichtungen auf Karbonbasis für den Einsatz als Fremdstromanode im Kathodischen Korrosionsschutz von Stahlbetonbauteilen (Schlussbericht) N2 - Zur Wirkungsweise und zum Einfluss unterschiedlicher Parameter beim Kathodischen Korrosionsschutz von Stahl in Beton wurden in der Vergangenheit bereits zahlreiche Untersuchungen durchgeführt. Über die Dauerhaftigkeit leitfähiger Beschichtung auf Karbonbasis als Fremdstromanode beim KKS von Stahlbeton liegen bislang keine umfassenden wissenschaftlichen Untersuchungen vor. Die in den einzelnen Arbeitspaketen (AP) erzielten Ergebnisse und gewonnenen Erkenntnisse tragen zum Verständnis über die Elektrodenreaktion der einzelnen Systeme bei. Die Frage der Dauerhaftigkeit konnte im Rahmen dieses Forschungsvorhabens nicht zur Gänze geklärt werden. Die Ergebnisse aus dem AP 1a liefern einen wesentlichen Beitrag zur Beantwortung der offenen Fragestellung hinsichtlich der vorherrschenden Elektrodenreaktion. In Verbindung mit dem Pourbaixdiagramm für Kohlenstoff lässt sich für die Beschichtungssysteme CBCC 1 und CBCC 2, nach 500 h andauernder Polarisation mit 10 mA/m² in ges. Calziumhydroxidlösung, die vorherrschende Elektrodenreaktion als Sauerstoffelektrode verifizieren. Im AP 1b wurde festgestellt, dass die an einem Praxisobjekt applizierten Systeme CBCC 1 und CBCC 2 in der Lage sind, die Schutzkriterien zu erfüllen. Die an diesem Objekt erforderlichen Schutzspannungen liegen jeweils zwischen 1 und 2 V. Die Anodenstromdichten betragen ca. 2,5 mA/m². Aufgrund der hohen Depolarisationsraten kann das Niveau der anliegenden Anodenstromdichten in Zukunft noch nach unten angepasst werden. Die Ergebnisse aus dem AP 1b und 1a sind erst zeitlich nach Festlegung der Prüfparameter für das AP 2a erzielt worden. Mit den ursprünglich veranschlagten Stromdichten von max. 40 mA/m² traten langfristig nachfolgende Problemstellungen auf: Bei der Stromeinleitung mittels Primärelektrode und Stromdichten größer gleich 20 mA/m² wurde festgestellt, dass die Versuche bei allen Systemen eine deutliche Entkopplung zwischen Primärelektrode und Beschichtung verursacht haben. Dies ist auf die hohen lokalen Stromdichten am Übergang Primärelektrode/leitfähige Beschichtung zurückzuführen. Eine Untersuchung der erforderlichen Kontaktfläche der Primärelektrode bezogen auf die effektive Stromdichte konnte nicht erfolgen. Weiterhin wurden die Haftzugwerte über die Dauer der Polarisation untersucht und mit unpolarisierten Proben verglichen. Eine Reduktion des Verbundes infolge Polarisation mit den angesetzten Stromdichten konnte verzeichnet werden. Es wurde jedoch auch festgestellt, dass mit zunehmenden Probenalter auch reduzierte Haftzugwerte an den geschliffenen und unpolarisierten Oberflächen der Referenzprobekörper ermittelt wurden. Die Grundlagen für die Simulation konnten in AP 3 anhand der gewonnen Ergebnisse erstellt werden und Feldverteilungen unter Berücksichtigung verschiedener Parameter berechnet werden. Eine auf den gewonnenen Erkenntnisse basierende Modellentwicklung für die Dauerhaftigkeitsprognose unter variierenden Randbedingungen, wie sie für AP 4 vorgesehen war, konnte auf Basis der erzielten Ergebnisse nicht erfolgen. Dass die Beschichtungssysteme unter praxisüblichen Randbedingungen einsetzbar sind und bei dem Vergleich der Schutzspannung mit klassischen Systemaufbauten gleiche Schutzstromdichten erzielt werden, zeigt das AP 1b deutlich. Die zukünftigen Ergebnisse aus der Praxisanwendung (AP 1b) werden über die Projektlaufzeit hinaus ausgewertet und publiziert. Das Ziel des Vorhabens wurde teilweise erreicht. KW - KKS KW - Kathodischer Korrosionsschutz KW - Korrosion KW - Betonstahl KW - Stahlbeton KW - Beschichtung PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-336230 SP - 1 EP - 101 PB - Bundesanstalt für Materialforschung und-prüfung (BAM) / ibac RWTH Aachen AN - OPUS4-33623 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Völker, Christoph A1 - Kruschwitz, Sabine A1 - Ebell, Gino T1 - Datengesteuerte Multisensor-Fusion zur Korrosionsprüfung von Stahlbetonbauteilen N2 - Potentialfeldmessung (PM) ist die beliebteste Methode der Zerstörungsfreien Prüfung (ZfP) zur Lokalisierung von aktiver Betonstahlkorrosion. PM wird durch Parameter wie z. B. Feuchtigkeits- und Chloridgradienten im Bauteil beeinflusst, so dass die Sensitivität gegenüber der räumlich sehr begrenzten, aber gefährlichen Lochkorrosion gering ist. Wir zeigen in dieser Studie, wie zusätzliche Messinformationen mit Multisensor-Datenfusion genutzt werden können, um die Detektionsleistung zu verbessern und die Auswertung zu automatisieren. Die Fusion basiert auf überwachtem maschinellen Lernen (ÜML). ÜML sind Methoden, die Zusammenhänge in (Sensor-) Daten anhand vorgegebener Kennzeichnungen (Label) erkennen. Wir verwenden ÜML um „defekt“ und „intakt“ gelabelte Bereiche in einem Multisensordatensatz zu unterscheiden. Unser Datensatz besteht aus 18 Messkampagnen und enthält jeweils PM-, Bodenradar-, Mikrowellen-Feuchte- und Wenner-Widerstandsdaten. Exakte Label für veränderliche Umweltbedingungen wurden in einer Versuchsanordnung bestimmt, bei der eine Stahlbetonplatte im Labor kontrolliert und beschleunigt verwittert. Der Verwitterungsfortschritt wurde kontinuierlich überwacht und die Korrosion gezielt erzeugt. Die Detektionsergebnisse werden quantifiziert und statistisch ausgewertet. Die Datenfusion zeigt gegenüber dem besten Einzelverfahren (PM) eine deutliche Verbesserung. Wir beschreiben die Herausforderungen datengesteuerter Ansätze in der zerstörungsfreien Prüfung und zeigen mögliche Lösungsansätze. T2 - DGZfP Jahrestagung 2018 CY - Leipzig, Germany DA - 07.05.2018 KW - Maschinelles Lernen KW - Datenfusion KW - ZfP KW - Beton KW - Korrosion PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-444852 UR - http://www.ndt.net/?id=23106 SN - 1435-4934 VL - 23 IS - 9 SP - 1 EP - 9 PB - NDT.net CY - Kirchwald AN - OPUS4-44485 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Rhode, Michael T1 - Normungsroadmap Wasserstofftechnologien 2024 N2 - Im Auftrag des Bundesministeriums für Wirtschaft und Klimaschutz (BMWK) wurden Anfang 2023 unter Leitung der Projektpartner DIN, DKE, DVGW, NWB, VDA, VDI und VDMA die Arbeiten an der Normungsroadmap Wasserstofftechnologien (NRM H2) begonnen. Ziel des Verbundprojekts war es, einen strategischen Fahrplan für eine schnelle und gezielte Erweiterung und Anpassung des technischen Regelwerks im Bereich der Wasserstofftechnologien auszuarbeiten und die aufgezeigten Lücken effizient zu schließen. Die Erarbeitung erfolgte in 39 Arbeitsgruppen mit einer Beteiligung von mehr als 600 Expertinnen und Experten. Die Clusterung erfolgte auf Basis von fünf großen Themenfeldern, die die gesamte Wertschöpfungskette abdecken: - Erzeugung - Infrastruktur - Anwendung - Qualitätsinfrastruktur - Weiterbildung, Zertifizierung und Sicherheit. Im Rahmen der des AK Infrastruktur erfolgte die Mitarbeit in der Arbeitsgruppe „Rohrleitungen“ (AG 2.1.1). Die AG war zuständig für die Ermittlung der Normungsbedarfe auf dem Gebiet der industriellen Rohrleitungen zur Werksversorgung sowie dem Gebiet der Flansche und ihren Verbindungen wie auch Prozessleitungen. Dies umfasst unter anderem Anforderungen für oberirdische oder in Kanälen verlegte oder erdgedeckte Rohrleitungen aus metallischen und nichtmetallischen Werkstoffen für Wasserstoff und -gemische. Mit dem Ziel, sicherer Betriebsbedingungen, waren hierbei insbesondere Anforderungen für industrielle Rohrleitungssysteme von Bedeutung (z. B. Normenreihe DIN EN 13480). Dabei unterscheiden sich die industriellen Rohrleitungssysteme von Fern- bzw. Transportleitungen, außerhalb der industriellen Werke, bspw. Raffinerien. Diese waren Bestandteil der AG 2.1.2 „Transportleitungen“. KW - Normung KW - Wasserstoff KW - Rohrleitungen KW - Metallische Werkstoffe KW - Regelwerke PY - 2024 SP - 49 EP - 54 AN - OPUS4-62442 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Ebell, Gino T1 - Zur Deckschichtbildung an feuerverzinkten Betonstählen in chloridhaltigen Mörteln N2 - In der vorliegenden Dissertation wurde das Korrosionssystem verzinkter Stahl in alkalischen, zementbasierten Feststoffelektrolyten untersucht. Dabei kamen drei Zementarten mit je vier Chloridgehalten zur Anwendung. Neben dem Korrosionssystem lag das Augenmerk ebenso auf einer adäquaten Beschreibung der Elektrolyteigenschaften. Hierzu wurde die Masseänderung, die Änderung des elektrischen Mörtelwiderstandes und des IR-Drop über die Zeit sowie die Porosität und die Porenwasserzusammensetzung, um nur einige Kenngrößen zu nennen, untersucht. Das Hauptaugenmerk ruht jedoch auf der Beschreibung des Korrosionssystems verzinkter Stahl in Mörtel. Dazu wurden die gebildeten Deckschichten und deren Einfluss auf den Korrosionsfortschritt in Abhängigkeit von der Zementart und des Chloridgehaltes sowie die daraus resultierenden elektrochemischen Kennwerte bestimmt. Die aus den Untersuchungen hervorgehenden Ergebnisse ermöglichen es, die Korrosionssysteme in Abhängigkeit vom Chloridgehalt oder von geometrischen Inhomogenitäten, im Phasengrenzbereich Mörtel/verzinkter Stahl zu differenzieren. Dabei konnte unabhängig von den verwendeten Zementen eine Klassifizierung der Korrosionssysteme über den Phasenwinkel 0,1 Hz erfolgen. Klassifiziert wurden durchtrittskontrollierte und diffusionskontrollierte Korrosionssysteme, Mischsysteme, Übergangssysteme und Korrosionssysteme mit Spaltgeometrie. Für diese Korrosionssysteme konnte festgestellt werden, welche Deckschichten maßgebenden Einfluss auf die Ausbildung eines durchtrittskontrollierten Korrosionssystem haben. Dazu gehören das bereits bekannte Simonkolleit und eine Deckschichtvariante, die bisher noch nicht in der Literatur als Deckschicht an verzinktem Betonstahl in Mörtel oder Beton beschrieben wurde. Für die Mischsysteme erfolgte eine Darstellung der anteiligen Bedeckung mit Simonkolleit, um den Übergang zu einem durchtrittskontrollierten Korrosionssystemen zu beschreiben. Neben der Klassifizierung der Korrosionssysteme kann über die Bestimmung des Phasenwinkels bei 0,1 Hz jedem Korrosionssystem nun auch ein spezifischer B-Wert zugewiesen werden. In Kombination mit der für diese Korrosionssysteme angepassten LPR-Messungen zur Bestimmung des Polarisationswiderstandes können Korrosionsraten ohne signifikante Beeinflussung des Korrosionssystems bestimmt werden. KW - Korrosion KW - Feuerverzinken KW - Betonstahl PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-631696 DO - https://doi.org/10.26204/KLUEDO/7427 SP - 1 EP - 166 PB - RPTU CY - Kaiserslautern AN - OPUS4-63169 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Ebell, Gino A1 - Burkert, Andreas A1 - Breit, W. A1 - Adams, R. A1 - Oechsner, M. A1 - Hoche, H. A1 - Körber, D. T1 - Technologie- und Sicherheitszuwachs bei der Anwendung von feuerverzinktem Betonstahl zum Ausbau einer nachhaltigen Marktposition im Stahlbetonbau N2 - Die Feuerverzinkung von Betonstahl stellt auf der Grundlage der im Stahlbetonbau geltenden Regelwerke eine zusätzliche Maßnahme zur Steigerung der Dauerhaftigkeit insbesondere bei Korrosionsbeanspruchung infolge Karbonatisierung und/oder Chlorideinwirkung dar. Anders als im Ausland ist die Anwendung von feuerverzinktem Betonstahl in Deutschland bisher kaum verbreitet. Im Rahmen des AiF-Forschungsprojekts IGF 499 „Technologie- und Sicherheitszuwachs bei der Anwendung von feuerverzinktem Betonstahl zum Ausbau einer nachhaltigen Marktposition im Stahlbetonbau“ sollten die einem breiteren Einsatz feuerverzinkter Betonstähle in Deutschland bisher entgegenstehenden offenen Fragestellungen beantwortet werden. Die interdisziplinäre Forschergruppe bestand aus dem Fachgebiet Werkstoffe im Bauwesen, Technische Universität Kaiserslautern (Forschungsstelle 1), mit dem Arbeitsschwerpunkt Fertigungstechnik, der staatlichen Materialprüfungsanstalt Darmstadt an der Technischen Universität Darmstadt (Forschungsstelle 2), mit dem Arbeitsschwerpunkt Werkstofftechnik, und der Bundesanstalt für Materialforschung und –prüfung, Berlin (Forschungsstelle 3), mit dem Arbeitsschwerpunkt Korrosionsschutz. KW - Verzinkter Betonstahl PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-402215 SP - 1 EP - 253 PB - AiF-Forschungsvereinigung Gemeinschaftsausschuss Verzinken e.V. (GAV) AN - OPUS4-40221 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pauw, Brian Richard A1 - Smales, Glen Jacob T1 - Electric Safety Interlock N2 - This interlock is designed to prevent electrical shock from high voltage (>60V) equipment. While the general safety interlock can be generically applied, this particular example employs an external vacuum-activated switch. It is for safeguarding human operations inside a vacuum sample chamber while the chamber doors are open. The circuit is closed (output is active) when a sufficient level of vacuum is reached, i.e. when all accessible openings are necessarily closed. The initial application is to interrupt power to a 220V, 250W heating cartridge (itself mounted inside a small sample holder with potentially exposed contacts) when the sample chamber is open. The external circuit can be modified to use different interlock mechanisms as needed. Note that the external interlock circuit is only a single circuit (with two signal lines) and thus is not protected against external shorts. To accomodate a range of safety interlocks, the 4-pin M12 connector is wired as follows: Pin 1 (Brown): +24V for power supply, max current 0.6A Pin 2 (White): Safety interlock system signal 1 (0 or 24V) Pin 3 (Blue) : Safety interlock system signal 2 (0 or 24V) Pin 4 (Black): 0V for power supply The safety is interlocked (output active) when both signal pins are set high (24V), with sufficient current to activate the two relays. Pin 1 and 4 can be used to power safety hardware (such as light curtains or proximity detectors) with 24VDC up to a current of 0.6A. A larger power supply can be installed when higher currents are needed, while staying within the current limits imposed by the wiring cross-section. KW - Electric Safety Interlock KW - MOUSE KW - 60-230V PY - 2023 DO - https://doi.org/10.6084/m9.figshare.22265920.v1 PB - Digital Science CY - Cambridge, MA, USA AN - OPUS4-57138 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Smales, Glen Jacob A1 - Pauw, Brian Richard A1 - Kolmangadi, Mohamed Aejaz T1 - X-ray scattering datasets associated with the publication "Molecular Mobility of Polynorbornenes with Trimethylsiloxysilyl side groups: Influence of the Polymerization Mechanism" N2 - X-ray scattering datasets for samples described in the 2022 publication "Molecular Mobility of Polynorbornenes with Trimethylsiloxysilyl side groups: Influence of the Polymerization Mechanism". This dataset includes both raw and processed X-ray scattering data for samples APTCN and MPTCN, alongside background measurements files (BKG). KW - X-ray scattering KW - SAXS KW - MOUSE KW - Membrane polymers KW - Microporous polymers PY - 2023 DO - https://doi.org/10.5281/zenodo.7621204 PB - Zenodo CY - Geneva AN - OPUS4-56972 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Smales, Glen Jacob A1 - Pauw, Brian Richard A1 - Kolmangadi, Mohamed Aejaz T1 - X-ray scattering datasets associated with the publication "Side chain length dependent dynamics and conductivity in self assembled ion channels" N2 - X-ray scattering datasets for samples described in the 2022 publication "Side chain length dependent dynamics and conductivity in self assembled ion channels". This dataset includes both raw and processed X-ray scattering data for samples ILC8, ILC10, ILC12, ILC14 and ILC16 alongside background measurement files (BKG). KW - X-ray scattering KW - SAXS KW - MOUSE KW - Columnar ionic liquid crystals KW - Liquid crystals PY - 2023 DO - https://doi.org/10.5281/zenodo.7621358 PB - Zenodo CY - Geneva AN - OPUS4-56973 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pauw, Brian Richard A1 - Smales, Glen Jacob T1 - Small-angle scattering data analysis round robin dataset - Original for participants N2 - These are four datasets that were made available to the participants of the Small-angle Scattering data analysis round robin. The intent was to find out how comparable results from different researchers are, who analyse exactly the same processed, corrected dataset. In this repository, there are: 1) a PDF document with more details for the study, 2) the datasets for people to try and fit, 3) an Excel spreadsheet to document the results. Datasets 1 and 2 were modified from: Deumer, Jerome, & Gollwitzer, Christian. (2022). npSize_SAXS_data_PTB (Version 5) [Data set]. Zenodo. https://doi.org/10.5281/zenodo.5886834 Datasets 3 and 4 were collected in-house on the MOUSE instrument. KW - Round robin KW - SAXS KW - Small angle scattering KW - SANS KW - X-ray KW - Neutron KW - Human factor KW - Data analysis KW - Data fitting KW - Human influence PY - 2023 DO - https://doi.org/10.5281/zenodo.7506365 PB - Zenodo CY - Geneva AN - OPUS4-56799 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pauw, Brian Richard T1 - McSAS3 N2 - McSAS3 is a refactored version of the original McSAS (see DOI 10.1107/S1600576715007347). This software fits scattering patterns to obtain size distributions without assumptions on the size distribution form. The refactored version has some neat features: - Multiprocessing is included, spread out over as many cores as number of repetitions! - Full state of the optimization is stored in an organized HDF5 state file. - Histogramming is separate from optimization and a result can be re-histogrammed as many times as desired. - SasModels allow a wide range of models to be used - If SasModels does not work (e.g. because of gcc compiler issues on Windows or Mac), an internal sphere model is supplied - Simulated data of the scattering of a special shape can also be used as a McSAS fitting model. Your models are infinite! - 2D fitting also works. KW - X-ray scattering KW - Polydispersity KW - Monte carlo KW - Scattering pattern analysis KW - Analysis approach KW - Neutron scattering KW - Automation KW - Command line PY - 2023 DO - https://doi.org/10.6084/m9.figshare.21814128.v1 PB - Digital Science CY - Cambridge, MA, USA AN - OPUS4-56787 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pauw, Brian Richard A1 - Smales, Glen Jacob T1 - X-ray scattering Datasets of gold and silver nanoparticle composites, relating to the publication "Gold and silver dichroic nanocomposite in the quest for 3D printing the Lycurgus cup" N2 - Wide-range X-ray scattering datasets and analyses for all samples described in the 2020 publication "Gold and silver dichroic nanocomposite in the quest for 3D printing the Lycurgus cup". These datasets are composed by combining multiple small-angle x-ray scattering and wide-angle x-ray scattering curves into a single dataset. They have been analyzed using McSAS to extract polydispersities and volume fractions. They have been collected using the MOUSE project (instrument and methodology). KW - X-ray scattering KW - MOUSE KW - Saxs KW - Waxs KW - Analyses KW - Datasets PY - 2022 DO - https://doi.org/10.5281/zenodo.7193859 PB - Zenodo CY - Geneva AN - OPUS4-55979 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Smales, Glen Jacob A1 - Pauw, Brian Richard T1 - Technical Drawings for The MOUSE Modular Sample Holder: Capillary Flow-through Cell N2 - OpenSCAD, STL and technical drawings for the capillary flow-through cell designed primarily for use with The MOUSE instruments. This flow-through cell can be used in conjunction with: - Modular sample holder (10.5281/zenodo.7499416) - Solid sample rack/plate (10.5281/zenodo.7499424) - Laser-cut sample holder (10.5281/zenodo.7499437) KW - X-ray scattering KW - SAXS KW - Sample holder KW - MOUSE PY - 2023 DO - https://doi.org/10.5281/zenodo.7499421 PB - Zenodo CY - Geneva AN - OPUS4-56776 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Smales, Glen Jacob A1 - Pauw, Brian Richard T1 - Technical Drawings for The MOUSE Modular Sample Holder: Solid Sample Rack/Plate N2 - OpenSCAD, STL and technical drawings for the solid sample rack designed primarily for use with The MOUSE instruments. This solid sample rack can be used in conjunction with: - Laser-cut sample holder (10.5281/zenodo.7499437) - Modular sample holder (10.5281/zenodo.7499416) - Capillary flow-cell for liquid samples (10.5281/zenodo.7499421) KW - X-ray scattering KW - SAXS KW - Sample holder KW - MOUSE PY - 2023 DO - https://doi.org/10.5281/zenodo.7499424 PB - Zenodo CY - Geneva AN - OPUS4-56778 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Smales, Glen Jacob A1 - Pauw, Brian Richard T1 - Technical Drawings for The MOUSE Modular Sample Holder: Laser-cut Sample Holder N2 - PDF file for the laser-cut sample holder designed primarily for use with The MOUSE instruments. This sample holder can be used in conjunction with: - Solid sample rack/plate (10.5281/zenodo.7499424) - Modular sample holder (10.5281/zenodo.7499416) - Capillary flow-cell for liquid samples (10.5281/zenodo.7499421) KW - X-ray scattering KW - SAXS KW - Sample holder KW - MOUSE PY - 2023 DO - https://doi.org/10.5281/zenodo.7499437 PB - Zenodo CY - Geneva AN - OPUS4-56779 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Smales, Glen Jacob A1 - Hahn, Marc Benjamin A1 - Hallier, Dorothea C. A1 - Seitz, H. T1 - X-ray scattering datasets and simulations associated with the publication "Bio-SAXS of single-stranded DNA-binding proteins: Radiation protection by the compatible solute ectoine" N2 - This dataset contains the processed and analysed small-angle X-ray scattering data associated with all samples from the publications "Bio-SAXS of Single-Stranded DNA-Binding Proteins: Radiation Protection by the Compatible Solute Ectoine" (https://doi.org/10.1039/D2CP05053F). Files associated with McSAS3 analyses are included, alongside the relevant SAXS data, with datasets labelled in accordance to the protein (G5P), its concentration (1, 2 or 4 mg/mL), and if Ectoine is present (Ect) or absent (Pure). PEPSIsaxs simulations of the GVP monomer (PDB structure: 1GV5 ) and dimer are also included. TOPAS-bioSAXS-dosimetry extension for TOPAS-nBio based particle scattering simulations can be obtained from https://github.com/MarcBHahn/TOPAS-bioSAXS-dosimetry which is further described in https://doi.org/10.26272/opus4-55751. This work was funded by the Deutsche Forschungsgemeinschaft (DFG, German Research Foundation) under grant number 442240902 (HA 8528/2-1 and SE 2999/2-1). We acknowledge Diamond Light Source for time on Beamline B21 under Proposal SM29806. This work has been supported by iNEXT-Discovery, grant number 871037, funded by the Horizon 2020 program of the European Commission. KW - SAXS KW - Radiation protection KW - Microdosimetry KW - G5P KW - Ectoine KW - DNA-Binding protein PY - 2023 DO - https://doi.org/10.5281/zenodo.7515394 PB - Zenodo CY - Geneva AN - OPUS4-56811 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pauw, Brian Richard A1 - Röder, Bettina A1 - Smales, Glen Jacob T1 - High temperature in-vacuum flow-through sample holder (sandwich design version 1.1) N2 - Technical drawings and documents for building a compact, heated, vacuum compatible flow-through sample holder. This holder is in use at the BAM MOUSE instrument as well as at the I22 beamline at the Diamond Light Source (see references for instrument details). This holder has several features: - The holder can be used in vacuum environments as well as in atmosphere - It has two G 1/4" UNF fittings to attach HPLC tubing for (optionally) flowing a medium through the sample cell - There are two additional (unflowed) sample positions for backgrounds and calibrants, held at the same temperature - The low-mass design coupled with a 250W heating element can achieve heating rates of 1 degree C per second, when coupled (for example) with an Omron E5CC PID controller. - The sample holder insert can be made from various materials depending on the application. Sealing the sample from the vacuum can be achieved using kapton, teflon or Magic tape, depending on the temperature requirements. The inlet and outlet holes will need to be punctured with a needle to enable flow. - Large exit cones ensure a clear exit angle of at least 45 degrees two theta. - It has been tested with temperatures up to 400 degrees C. - Compression area has been raised and polished to ensure a good vacuum seal. KW - SAXS KW - X-ray scattering KW - Sample cell KW - Sample holder KW - Heated KW - Flow-through KW - Vacuum compatible KW - XRD KW - WAXS PY - 2023 DO - https://doi.org/10.5281/zenodo.7501030 PB - Zenodo CY - Geneva AN - OPUS4-56777 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Smales, Glen Jacob A1 - Pauw, Brian Richard A1 - Kolmangadi, Mohamed Aejaz T1 - X-ray scattering datasets associated with the publication "Molecular Dynamics of Janus Polynorbornenes: Glass Transitions and Nanophase Separation" N2 - X-ray scattering datasets for samples described in the 2020 publication "Molecular Dynamics of Janus Polynorbornenes: Glass Transitions and Nanophase Separation". This dataset includes both raw and processed X-ray scattering data for samples PTCHSiO-Pr, Bu, Hx, Oc and De, alongside background measurements files (BKG). This data was collected using the MOUSE project (instrument and methodology). KW - X-ray scattering KW - SAXS KW - MOUSE KW - Alkyls KW - Polymers PY - 2023 DO - https://doi.org/10.5281/zenodo.7614835 PB - Zenodo CY - Geneva AN - OPUS4-56971 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Smales, Glen Jacob A1 - Sprachmann, J. T1 - Datasets of Antiaromatic COFs associated with the publication "Antiaromatic Covalent Organic Frameworks Based on Dibenzopentalenes" N2 - X-ray scattering and sorption data associated with the publication "Antiaromatic Covalent Organic Frameworks Based on Dibenzopentalenes". X-ray scattering data is provided for COF and POP materials, including data from stability tests, as three-column ascii files with columns q (nm-1), I (m-1) and uncertainty on I, as well as being provided in 2θ. KW - X-ray scattering KW - SAXS KW - Covalent Organic Frameworks KW - Antiaromaticity KW - MOUSE PY - 2023 DO - https://doi.org/10.5281/zenodo.7509377 PB - Zenodo CY - Geneva AN - OPUS4-56868 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pauw, Brian Richard A1 - Smales, Glen Jacob A1 - Rosalie, Julian T1 - Small-angle scattering data analysis round robin - Anonymized results, figures and Jupyter notebook N2 - The intent of this round robin was to find out how comparable results from different researchers are, who analyse exactly the same processed, corrected dataset. This zip file contains the anonymized results and the jupyter notebook used to do the data processing, analysis and visualisation. Additionally, TEM images of the samples are included. KW - Round robin KW - Small-angle scattering KW - Data analysis PY - 2023 DO - https://doi.org/10.5281/zenodo.7509710 PB - Zenodo CY - Geneva AN - OPUS4-56803 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Ebell, Gino A1 - Burkert, Andreas A1 - Gehlen, C. A1 - Keßler, S. T1 - Validierung zerstörungsfreier Messmethoden zur zuverlässigen Erfassung von Bewehrungskorrosion (Schlussbericht) N2 - Determining a pore structure’s mechanical and chemical data on lime rendering exposed outdoors and including masonry in the laboratory, with regard to their behaviour on moisture transport and weathering was the objective. In search of clues for a dose-response relation - i.e. upon a connection between the emission rate of SO2 and NOx on one hand and the degree of damage to mainly plaster having a lime component on the other - it has been of interest to what extent their structural characteristics including pore space are modified and so consequently also physico-technical properties and chemical composition. For determining corresponding criteria, a widely diversified spectrum of test methods such as to obtain data concerning porosity and moisture transport, mechanical behaviour, and chemistry as well is available. A description of the manufacture of plate-shaped rendering specimens with lime putty, industrially hydrated lime and dolomitic hydrate (the last two also having a cement admixture) and also hydraulic lime as binding agents is included. First deposition velocity and absorption rate for SO2 were determined in laboratory tests on these materials in dry and moist states. After their exposure on outdoor racks at six locations in the Berlin region with differing SO2 atmospheric contents over at least 5 years, the samples of course show timedependent modifications of chemical and physical qualities which are especially reflected in the form of profiles of structure, strength and concentration, e.g. for sulphate. Local climatic differences, however, partly exert a greater influence on material than emissions. Similar investigations were performed on samples of comparable composition exposed 4 and 17 years. But the real surprise is furnished by the renderings’ behaviour depending upon orientation and upon height at a building. Since weathering behaviour and moisture Transport (absorption, storage, release) are directly interdependent, further criteria are necessary for a critical assessment of a plasters’ pore structure. Starting from sands, plasters were characterized. The structural parameters were lastly influenced by the respective contents of sand, binder and mixing water. These results and those gained from bricks naturally find their expression in masonry sections manufactured there from, and above all in their capillary and evaporative behaviours, and also when applying different test liquids. Summary and cited literature is given at the end of this report. KW - Potentialfeldmessung KW - Potential mapping KW - Korrosion KW - Stahlbeton KW - Betonstahl KW - Merkblatt B 3 PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-336229 SP - 1 EP - 92 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) / Technische Universität München AN - OPUS4-33622 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Nietzke, Jonathan A1 - Richter, Tim T1 - Hydrogen diffusion and desorption characteristics of a CoCrFeMnNi high entropy and a CoCrNi medium entropy alloy N2 - High-entropy alloys (HEAs) are innovative high-performance materials that have attracted more and more research attention. HEAs are characterized by a solid solution of typically five equiatomic metallic elements. In addition, medium-entropy alloys (MEA, with three elements) are of interest and become more and more important. Depending on the alloy concept, HEAs and MEAs show exceptional mechanical properties, especially high-strength and ductility combinations at both cryogenic and elevated temperatures combined with excellent corrosion resistance. Future structural HEA/MEA components can be exposed to potential applications with hydrogen containing environments like high-temperature water in pressurized nuclear reactors or aerospace structures. Other potential applications could be in materials for vessel walls in the field of cryogenic and high-pressure hydrogen storage. So far, the susceptibility of HEAs/MEAs to hydrogen assisted cracking (if any) and the hydrogen diffusion is not investigated in detail yet and can limit or extend possible applications of HEA/MEA as structural materials. In our work, we focused on the hydrogen absorption, diffusion, and distribution in a HEA (CoCrFeMnNi the original Cantor-alloy) and a MEA (CoCrNi). Cathodic hydrogen charging was carried out for the hydrogen ingress, and thermal desorption analysis (TDA) revealed complex hydrogen trapping in both alloy types up to 300 °C. The absorbed total hydrogen concentrations were > 100 ppm for the HEA and > 40 ppm for MEA. In addition, the assessment of the peak deconvolution is not trivial and must consider both experimental and microstructure influences. T2 - 4th International Conference on Metals and Hydrogen - Steely & Hydrogen 2022 CY - Ghent, Belgium DA - 11.10.2022 KW - Hydrogen KW - High-entropy alloy KW - Multiple principal element alloy KW - Thermal desorption analysis KW - Diffusion PY - 2022 SP - 1 EP - 11 CY - Ghent, Belgium AN - OPUS4-56076 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kluge, Martin A1 - Ferrero, Fabio A1 - Schröder, Volkmar A1 - Acikalin, Hatice Aydan A1 - Steinbach, J. T1 - Improvements in the modeling of the self ignition of tetrafluoroethylene N2 - In order to prevent incidents in the industrial production of Teflon® from Tetrafluoroethylene (TFE), the safety related aspects of the self-heating process of TFE must be taken into account. Simulations of this self heating process were performed with COMSOL Reaction Engineering Lab® and COMSOL® COMSOL Multiphysics®. A complex reaction net was employed, resulting in a model allows for a good agreement with experimentally achieved results. T2 - COMSOL Conference 2010 CY - Paris, France DA - 2010-11-17 KW - Heating KW - Free convection KW - Reactive flow KW - Gas reaction KW - Self ignition PY - 2010 N1 - Geburtsname von Kluge, Martin: Beckmann-Kluge, M. - Birth name of Kluge, Martin: Beckmann-Kluge, M. SP - 1 EP - 7 AN - OPUS4-24174 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ebell, Gino A1 - Achenbach, R. A1 - Angst, U. A1 - Brem, M. A1 - Dauberschmidt, C. A1 - Eichler, T. A1 - Hariri, K. A1 - Harnisch, J. A1 - Keßler, S. A1 - Mayer, T.F. A1 - Mietz, Jürgen A1 - Pruckner, F. T1 - Elektrochmische Potentialmessung zur Detektion von Bewehrungsstahlkorrosion N2 - Die Potentialmessung kann zum Auffinden korrosionsaktiver Bereiche neben Stahlbetonbauwerken auch bei Spannbetonbauwerken angewandt werden, die mit Spannstählen im direkten Verbund hergestellt werden. Bei Vorspannsystemen mit metallischen Hüllrohren im nachträglichen Verbund ist eine Aussage über den Korrosionszustand des Hüllrohrs, nicht aber des Spannstahls möglich. Messungen an Spannbetonbauteilen erfordern grundsätzlich die besonderen Kenntnisse eines Spezialisten. KW - Korrosion KW - Potentialfeldmessung KW - Corrosion KW - Concrete PY - 2021 SN - 978-3-947971-16-9 VL - Merkblatt B 03 SP - 1 EP - 22 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-53091 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kanzler, Daniel A1 - Bertovic, Marija T1 - Expertise oder KI – Was hilft uns in der ZfP'? N2 - Die zunehmende Integration von Automatisierung und KI in die zerstörungsfreie Prüfung (ZfP) verändert nicht nur die Prüfprozesse selbst, sondern auch die Art und Weise, wie Entscheidungen getroffen werden. Während technische Systeme die Fehleranfälligkeit verringern und die Datenverarbeitung unterstützen können, bleibt die letztendliche Verantwortung beim Menschen. Dieser Beitrag untersucht die Rolle der Intuition in der Entscheidungsfindung und analysiert typische Fehleinschätzungen mithilfe der Prospekttheorie und Erkenntnissen aus der kognitiven Psychologie. Zudem wird aufgezeigt, wie fundierte Entscheidungen in KI-gestützten ZfP Prozessen unterstützt werden können – durch Schulung, erklärbare Systeme, nutzerzentrierte Gestaltung, geeignete Metriken und eine gezielte Aufgabenverteilung zwischen Mensch und Technik. T2 - DGZfP-Jahrestagung 2025 CY - Berlin, Germany DA - 26.05.2025 KW - Zerstörungsfreie Prüfung KW - Künstliche Intelligenz KW - Entscheidungsfindung KW - Mensch-Maschine-Interaktion KW - Human Factors PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-634070 DO - https://doi.org/10.58286/31237 SP - 1 EP - 10 PB - NDT.net AN - OPUS4-63407 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino A1 - Burkert, Andreas T1 - Neue Erkenntnisse zu wasserstoffinduzierten Spannungsrissen infolge korrosiver Belastung hochempfindlicher Spannstähle in Spannblockverfahren nach TGL 173-33 N2 - Brückenbauwerke, die im Spannblockverfahren hergestellt wurden, können bauartbedingt wasserstoffinduzierte Spannungsrisse über den gesamten Querschnitt eines Spannkanals aufweisen. Das Risswachstum kann infolge dynamischer Beanspruchung über die Nutzungsdauer fortschreiten und zu Spanndrahtbrüchen führen. T2 - 5. Brückenkolloquium CY - Ostfildern, Germany DA - 06.09.2022 KW - Korrosion KW - Spannungsrisskorrosion KW - Spannstahl PY - 2022 SP - 567 EP - 572 PB - Expert -TAE CY - Esslingen AN - OPUS4-55662 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lehmann, Jens A1 - Ebell, Gino A1 - Burkert, Andreas T1 - Potentialfeldmessung - Korrosionsprüfung von Stahlbetonbauwerken N2 - Durch das alkalische Porenwassermilieu ist Stahl im Beton vor Korrosion geschützt. Unter un-günstigen Umgebungsbedingungen (Karbonatisierung, Chlorideintrag) kann die passive Deck-schicht auf der Stahloberfläche zerstört werden. Im weiteren Verlauf können sich korrosionsbe-dingte Folgeschäden, wie Risse und Abplatzungen am Bauwerk ergeben. Um notwendige Sanie-rungsmaßnahmen sind frühzeitige und weitgehend zerstörungsfrei ermittelte Informationen über das aktuelle Korrosionsverhalten der Stahlbewehrung von großer Bedeutung. Die Potentialfeld-messung ist ein etabliertes und weit verbreitetes Verfahren zur Beurteilung des Korrosionszu-standes der Bewehrung in Stahlbetonbauwerken. Mit Hilfe dieses Verfahrens können Bereiche aktiv korrodierender Bewehrung zerstörungsfrei lokalisiert werden. In der Regel kommt diese Messmethode bei der Detektion chloridinduzierter Korrosion zum Einsatz. T2 - Fachtagung Prüfen von Beton CY - Berlin und Hamburg, Germany DA - 06.10.2016 und 11.10.2016 KW - Stahlbeton KW - Spannbeton KW - Korrosion KW - Zerstörungsfreie Prüfung PY - 2016 SP - 51 EP - 57 AN - OPUS4-37710 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Large scale reinforced concrete test specimen for potential mapping under practical conditions N2 - Electrochemical potential mapping according to guideline B3 of DGZfP German Society for Non- Destructive Testing) is a recognized technique for the localization of corroding reinforcing steels. In reinforced concrete structures the measured potentials are not necessarily directly linked to the corrosion likelihood of the reinforcing steel. The measured values may be significantly affected, different from e.g. stress measurement, by different influences on the potential formation at the phase boundary metal/concrete itself as well as the acquisition procedure. Due to the complexity of influencing factors there is a risk that the results are misinterpreted. To investigate these influencing factors under practical conditions it requires a specimen with similar damage patterns, dimensions and more factors e.g. metallic mounting parts. Recently the BAM realized such a large scale test specimen for this purpose. T2 - NDE 2017 CY - Chennai, TN, India DA - 14.12.2017 KW - Potential mapping KW - Corrosion PY - 2017 UR - http://thehashtag.in/NDE17/chennai/wp-content/uploads/2017/12/Ebell-NDE-2017.pdf SP - 1 EP - 1 AN - OPUS4-43469 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ebell, Gino A1 - Mayer, T. F. T1 - Korrosions- und Verbundverhalten bei beschichteten Fugenblechen N2 - Wechselwirkung von feuerverzinkten Fugenblechen und Beton bei Einsatz in WU-Bauwerken. Mögliche Wasserstoffentwicklung an feuerverzinkten Fugenblechen durch Einwirkung hochalkalischer Medien wie Beton kann durch ausreichend großflächigen, kathodisch wirksamen, Betonstahl unterbunden werden. KW - Korrosion KW - Feuerverzinkter Stahl KW - Korrosionsschutz PY - 2023 SP - 1 EP - 6 CY - online DBV AN - OPUS4-57488 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Habib, Abdel Karim A1 - Kluge, Martin A1 - van Wingerden, Kees ED - Beyer, Michael ED - Lucassen, Arnas T1 - Experimental investigation into the consequences of release of liquified hydrogen onto and under water N2 - Large-scale experiments have been performed to investigate the possible consequences of realistic amounts of liquified hydrogen (LH2) encountering water. The experiments aimed at simulating an accidental release of LH2 during especially the fuelling of a ship. For liquified natural gas (LNG) it has been demonstrated that when spilled onto water the evaporation rate can be that high that physical explosions occur which are referred as rapid phase transitions (RPTs). It cannot be excluded that RPTs are also possible in the case of LH2. The tests were performed in a 10 m x 10 m x 1.5 m basin filled with water, at the Test Site Technical Safety of the Bundesanstalt für Materialforschung und –prüfung (BAM) in Horstwalde, Germany within a research cooperation between BAM and Gexcon as part of the SH2IFT program. LH2 releases were established releasing directly from a trailer carrying LH2 through a long flexible double vacuum insulated transfer line. The releases occurred from a height of 50 cm above and 30 cm under the water surface both pointing downwards and 30 cm under the water surface pointing along the water surface too. The release rate was determined based on the weight loss rate of the road tanker which was placed onto load cells. Special blast pressure sensors were used to measure the shock waves generated by the release processes both in the water and in the air. At several locations the gas concentration was measured. Heat radiation was measured at 3 distances from the point of release. High speed, Infrared (IR) and normal cameras were used to record events and to follow the gas cloud behaviour in time. This includes cameras mounted on a UAV and underwater cameras. Two weather stations were used to measure wind speed, wind direction, temperature and humidity during all tests performed. All investigated release configurations resulted in a very chaotic LH2-water mixing zone, causing considerable evaporation but only minor over pressures. The main phenomenon observed was an ignition of the released gas cloud, resulting in significant blast wave overpressures and heat radiation to the surroundings. The location of the ignition occurred in free air at some distance from the instrumentation and release location. T2 - 14th International Symposium on Hazards, Prevention and Mitigation of Industrial Explosions (ISHPMIE 2022) CY - Braunschweig, Germany DA - 11.07.2022 KW - LH2 KW - RPT KW - Release KW - Gas cloud explosion KW - Heat radiation PY - 2022 SP - 182 EP - 196 AN - OPUS4-59441 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schubert, Sven A1 - Komann, Steffen A1 - Neumann, Martin A1 - Reichardt, Adrian A1 - Müller, Lars A1 - Wille, Frank T1 - Ageing management measures of transport packages for radioactive materials N2 - The consideration of ageing mechanisms is with integration into the IAEA-requirements now obligatory for the design of transport packages. For packages intended to be used for shipment after storage the consideration of the effects of ageing mechanisms during storage in safety analyses and the implementation of corresponding instructions for operation and maintenance are required. Therefore, these packages have been maintained during storage in a manner that all requirements specified in the IAEA-requirements and in the applicable certificates of approval have been fulfilled. BAM is the competent authority in Germany for evaluating the thermal and mechanical design of packages for the transport of radioactive materials. In this context, BAM also evaluates the aging mechanisms and aging effects occurring during the long-term storage period of such transport packages. BAM has developed a guideline for the implementation of ageing assessment and of the measures for ageing management into the approval procedure based on IAEA-requirements. The goal of the presented paper is to introduce this guideline and the general approach for ageing management requirements and to describe the application to a specific package design. The type and amount of the ageing management not only depend on the use of the packaging, but also on the accessibility of the components that are considered in the ageing assessment. The different operating phases of a packaging are considered for the ageing assessment, such as loading, interim storage or transport. The implementation of measures for ageing management is divided into three levels – systemic measures, package design related measures and documentation. The systemic measures are attributed to the general management system and define the whole activities for organization of ageing management like structure, responsibilities, documentation, reports and evaluation. The package design related measures are defined in an ageing management plan. These measures shall ensure that the anticipated changes of the package design under consideration of ageing effects still complies with the design approval specification. Therefore, an ageing surveillance program and, if necessary, a gap analysis program shall be developed. The ageing management documentation ensures the continuous documentation of the compliance of a specific package to the approved package design, comprising mainly records resulting from operation and surveillance. T2 - RAMTRANS 2024 CY - London, United Kingdom DA - 15.05.2024 KW - Radioactive Materials KW - Ageing Management KW - Transport Packages KW - Dual Purpose Casks PY - 2024 VL - 2024 SP - 1 EP - 8 PB - Nuclear Institute CY - London AN - OPUS4-60186 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Werner, Jan A1 - Kutz, P. W. A1 - Otremba, Frank T1 - Testing of Small Scale Tank Prototypes under Cryogenic Conditions N2 - Climate change, CO2 reduction, resource efficiency are only 3 current keywords that describe the current industrial-economic situation. In order to influence climate change effectively, the conversion of supply systems with technically usable forms of energy must succeed in the next decade. The international network founded in Baku in 2015 bundles research activities in the broad field of energy supply and energy efficiency. Discuss current research approaches and results with scientists and experts from renowned universities and follow Azerbaijan's efforts to implement the energy revolution. T2 - Neseff 2020 CY - Online meeting DA - 28.09.2020 KW - Mud pumps KW - Mud circulation system KW - Pistons KW - Hydrostatic pressure KW - Friction wear KW - Ceramic liners KW - Tribology PY - 2020 SN - 978-3-940471-59-8 SP - 4 EP - 9 AN - OPUS4-52149 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Nina A1 - Rhode, Michael A1 - Kannengießer, Thomas T1 - Ausscheidungsverhalten und Eigenschaften der schweißbedingten Wärmeeinflusszonen hochfester Stähle in Abhängigkeit der Mikrolegierungsroute N2 - Für eine signifikante Festigkeitssteigerung von vergüteten, hochfesten Feinkornbaustählen mit einer Nominalstreckgrenze ≥ 690 MPa, ist die Zugabe von Mikrolegierungselementen, wie Nb und Ti, unerlässlich. Die Normvorgaben zur chemischen Zusammensetzung dieser Stähle (bspw. in DIN EN 10025-6) geben zur Erzielung der vorgeschriebenen Eigenschaften dabei oft nur Grenzgehalte für die Hersteller vor. Die Wirkung der Legierungselemente in der WEZ ist teilweise komplett konträr. Somit wird eine adäquate Vorhersage der Chargenabhängigkeit hinsichtlich der Schweißeignung und des Tragverhaltens der Schweißverbindung erschwert. Neben metallographischen Untersuchungen einzelner WEZ-Bereiche wurden unter Variation der chemischen Zusammensetzung, thermodynamische Phasenberechnungen mittels ThermoCalc durchgeführt. Hierdurch wird ein Verständnis zur Phasentransformation, Ausscheidungswachstum und -auflösung während des Schweißens in Abhängigkeit von Temperatur und Abkühlbedingungen geschaffen. T2 - 40. Vortrags- und Diskussionstagung Werkstoffprüfung 2022 CY - Dresden, Germany DA - 27.10.2022 KW - WEZ-Erweichung KW - Mikrolegierungseinflüsse KW - Thermodynamische Modellierung PY - 2022 SP - 1 EP - 6 AN - OPUS4-56168 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Otremba, Frank A1 - Romero-Navarrete, José A. A1 - Jáuregui Correa, J.C.A. T1 - Forces on rails in turns: A review N2 - Regardless of the mode of transportation, directional changes generate greater forces on the infrastructure as a result of the lateral load transfer and of the respective steering forces in the vehicles. In the case of Railway transportation, a concentrated damage occurs in the rail at the initiation of the turning maneuver, whose magnitude depends on the bogie´s yaw stiffness and on the level of friction at its centre plate. To mitigate such rail-damaging effects, some new designs have been proposed and used for the bogies´ wheelset. However, no new designs for the centre plate have been used. In this paper, a review of the causality for the forces arising during Railway Vehicle's turn negotiations, is presented, including the description of a modeling framework to analyze the influential Parameters for determining the magnitude of such forces. T2 - CONIIN 2020 CY - Online meeting DA - 28.09.2020 KW - Turning maneuvers KW - Rail damage KW - Yaw stiffness KW - Yaw resistance KW - Self-aligning bogies KW - Lateral load transfer KW - Steering forces PY - 2020 SP - 1 EP - 6 AN - OPUS4-51390 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Otremba, Frank A1 - Romero Navarrete, J. A. T1 - Experimental Assessing of the Energy Transformation in Turns N2 - Turning maneuvers of rail vehicles involve demanding situations for the infrastructure because of the steering forces generated and the resultant lateral load transfers. Such forcing situation involves increased tangential forces that consume kinetic energy from the vehicle. While much attention has been paid in the literature to the damage in such infrastructure segments, the energy that is dissipated in these maneuvers, has not been explicitly addressed. In this paper, a specialized scale-down infrastructure is used to characterize the effect of the initial speed of the vehicle and its mass, on the magnitude of both the rail forces developed and the amount of dissipated energy during turning maneuvers. The outputs of the experiments suggest that most of the original kinetic energy is dissipated at the first portion of the turn. Also, that the magnitude of the wheel forces and the amount of dissipated energy, correlate. That is, a greater rail damage would correspond to greater energy dissipation. T2 - IMECE2022 CY - Columbus, OH, USA DA - 30.10.2022 KW - Turning maneuvers KW - Energy dissipation KW - Rail damage KW - Experimental approaches PY - 2022 SP - 1 EP - 6 AN - OPUS4-56334 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rappsilber, Tim A1 - Krüger, Simone A1 - Raspe, Tina ED - Grayson, Stephen T1 - Engineering Safety in EV's: Analysis of occupant safety using a multifunctional real-scale model car N2 - For vehicle occupant safety, it is important to investigate the effects on people of the pollutants and temperatures emitted by electric vehicle traction batteries in the event of a fire. Fire tests on complete vehicles are the most realistic way of investigating the effects on vehicle occupants. However, these types of real fire tests are very complex and only represent one specific fire scenario with the corresponding specific boundary conditions. We would like to present an engineering method that makes it possible to investigate the effects on the occupants' ability to escape in various damage scenarios with different vehicle geometries without wasting expensive resources. T2 - Interflam 2025 CY - London, United Kingdom DA - 30.06.2025 KW - Lithium ion battery KW - Occuoant safety KW - Gas KW - Flames PY - 2025 SP - 422 EP - 425 AN - OPUS4-63617 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schubert, Thomas A1 - Máca, Petr A1 - Hering, Marcus A1 - Fiedler, Georg A1 - Beckmann, Birgit T1 - Impact Experiments on Reinforced Concrete Specimens - Investigation of Repeatability and Scaling N2 - Nowadays, the impact resistance of concrete structures has become a prominent concern for critical infrastructure operators, particularly amidst escalating geopolitical tensions. Regulators and design engineers know that reinforced concrete structures can only be developed with high efficiency by considering nonlinear structural and highly nonlinear material behavior. Therefore, specific guidelines on impact design provide instructions for design and analysis of structures required to resist impact loading. These instructions are usually based on published results and evaluated data of impact experiments carried out in laboratories. To widen the knowledge and increase the scientific data the Institute of Concrete Structures (IMB) at TUD Dresden University of Technology (TUD) has carried out many impact experiments on reinforced concrete specimens in recent years. A specially designed drop tower is available for this purpose on the premises of the Otto Mohr Laboratory, TUD. In the framework of the past research at TUD some important issues, such as influence of rebar arrangement, structural thickness, scalability of specimen and repeatability, with regard to experimental impact testing were investigated. This article presents the drop tower facility and research results of impact experiments on reinforced concrete slabs. First, the scalability of impact experiments will be discussed in conjunction with already known theoretical scaling parameters provided by researchers in the past, e.g. Rüdiger et al. [1]. Scalability of experimental data is of huge importance since protective structures made of reinforced concrete differ usually in size in comparison to experimental specimens. The second important research focus is on repeatably of impact experiments. Since impact experiments are usually time consuming and expensive, a certain impact scenario is mostly carried out only once. It is intended to show the range of deviation of impact tests on some already carried out experiments on reinforced concrete slabs. A possible standard deviation is estimated for the applied test setup. T2 - 15th International Conference on Shock & Impact Loads on Structures CY - Gothenburg, Sweden DA - 12.06.2025 KW - Reinforced concrete KW - Drop-weight impact KW - Scaling KW - Repeatability KW - Digital image correlation PY - 2025 SP - 80 EP - 91 AN - OPUS4-63627 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Andrés Arcones, Daniel A1 - Weiser, M. A1 - Koutsourelakis, P-S. A1 - Unger, Jörg F. T1 - Quantifying the uncertainty of predictive simulations in digital twins through the identification of model bias N2 - This work presents a novel approach to quantifying uncertainty in digital twin simulations by addressing model bias through embedded parameter distributions. Traditional Bayesian methods often underestimate uncertainty due to assumptions of model correctness. We propose a hierarchical Bayesian framework combined with Polynomial Chaos Expansion to better capture and propagate uncertainty. The methodology is validated on an analytical example and a real-world case involving thermal deformation predictions of the Nibelungen Bridge, demonstrating improved predictive accuracy and reliability. T2 - fib Symposium 2025 CY - Antibes, France DA - 16.06.2025 KW - Digital Twins KW - Model Bias KW - Predictive simulations KW - Quantifying the uncertainty PY - 2025 SP - 2867 EP - 2873 PB - The fib, Fédération international du béton CY - Antibes, France AN - OPUS4-63629 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Romero-Navarrete, José A. A1 - Otremba, Frank ED - Zobory, I. T1 - Conceptual design of an active centre plate N2 - The efficiency and safety of railway transportation depend both on numerous factors linked to the vehicle, the infrastructure, the operator and the environment. Curved tracks are subjected to demanding situations due to elevated stress levels, as a function of the operating conditions and vehicle/infrastructure design. In such segments, steering forces are superimposed to lateral load transfers. The steering forces depend on the condition and the design of the centre plate and bogies’ suspensions design. While the friction at the centre plate provides the needed damping to mitigate the hunting vibration of the bogie in straight track segments, such yaw resistance originates high steering forces and rail damage on curved tracks. A centre plate with low friction at turns and high friction at straight track segments would thus be highly advantageous. In this paper, a centre plate design is proposed which provides a yaw-rotation resistance torque that depends on the bogie-car relative position. Two different designs are considered for that purpose, one that combines a spring-acted centring mechanism with a lower pair kinematics, while the other one involves higher kinematic pairs which should incorporate lateral damping elements. As a result of using an engineering design approach, the higher kinematic pairs-based design is recommended however, the validation of such operational principles, including the introduction of the needed damping, should be configured on the basis of experimental models. T2 - 11th International Conference on Railway Bogies and Running Gears CY - Budapest, Hungary DA - 09.09.2019 KW - Steering torques KW - Railway transportation KW - Bogie design KW - Conceptual design KW - Engineering design KW - Transport externalities PY - 2020 SN - 978-963-9058-42-2 SP - 77 EP - 86 PB - Scientific Society of Mechanical Engineers (SSME/GTE) CY - Budapest AN - OPUS4-54086 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Romero-Navarrete, José A. A1 - Otremba, Frank A1 - Lozano Guzmán, A. A. T1 - Experimental methods for road tankers. A critical review N2 - The transportation of liquids involves several situations derived from the curved shape of the cargo containers, including a comparatively high center of gravity, which negatively shifts when the container is partially loaded, and the vehicle is subjected to steering or braking accelerations. Aiming at reducing these effects several experimental approaches have been applied, involving different tank shapes and the use of baffles, tested under laboratory or field conditions, at full scale or at a down-scale. However, the scope of such approaches has been limited, mainly because the potential effect of other components of the vehicle on the road tanker behavior, has been neglected. In this paper, a critical review is presented of the experimental approaches considered so far, identifying specific experimental needs to improve the performance of the vehicles, from both the road safety and the environmental perspective. T2 - IMECE 2020 CY - Online meeting DA - 16.11.2020 KW - Tank KW - Road KW - Methods PY - 2020 SP - 1 EP - 8 AN - OPUS4-51641 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jauregui-Correa, J. C. A1 - Otremba, Frank A1 - Hurtado-Hurtado, G. A1 - Romero-Navarrete, J. A. T1 - Experimental test rig for simulating dynamic loads on subway systems N2 - Scaled-down experimental facility: Can reproduce actual failures; can produce simulated data for identifying cracks in the substructure or other defects. The acceleration data can be converted into an equivalent deformation. The experimental facility can analyse dynamic loads. Equivalent force data: Facilitates the application to a health monitoring system; simplifies the development of predictive maintenance. These data is helpful in validating analytical or simulation models. T2 - Fifth International Conference on Railway Technology CY - Montpellier, France DA - 22.08.2022 KW - Test rig KW - Dynamic loads KW - Subway system PY - 2020 SP - 1 EP - 6 AN - OPUS4-55566 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gollnow, Christian A1 - Kannengießer, Thomas T1 - Optical in-situ measurement system for determination of material behaviour in welds T2 - Visual-JW2012 - International Symposium on Visualization in Joining & Welding Science through Advanced Measurements and Simulation CY - Osaka, Japan DA - 2012-11-28 KW - Digital image correlation KW - In-situ measurement KW - Local weld deformation KW - Hot cracking KW - Local weld displacement KW - Controlled tensile weldability test PY - 2012 VL - 1 IS - JWP-12 SP - 27 EP - 28 AN - OPUS4-27547 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kannengießer, Thomas A1 - Dabah, Eitan ED - Marquis, F. T1 - Energy dispersive synchrotron diffraction for in-situ analyses of hydrogen behavior in steels N2 - The extent of hydrogen embrittlement phenomenon is dependent on the interaction of hydrogen with the material i.e. diffusion behavior, lattice distortions, phase transformations and residual stresses developments. For the better understanding of the hydrogen interaction with the metal, possibilities of performing in-situ observations of the mentioned factors has to be accomplished. The EDDI (Energy Dispersive Diffraction) beamline at the BESSY II facility in Berlin provides this possibility and was used in order to investigate the aspects of this phenomenon in in-situ scale. The energy dispersive method entails a synchrotron X-ray white beam with a wide energy range (20–120 keV) which allows a fixed position of the sample and the detector, and combined with the high photons flux it allows a very short measurement time for obtaining a full scale X-Ray Diffraction patterns. In this contribution, the successful usage of high energy X-rays, applied for the first time for hydrogen behavior observations, provided the ability for evaluating in-situ the hydrogen diffusion behavior and the hydrogen interaction with stresses fields in the material. Steel samples were charged with hydrogen and examined by Synchrotron radiation. Two different methods were used in this research; the first is diffusible hydrogen concentration evaluation extracted from the lattice distortions, i.e. changes of the lattice parameter. The second is calculation of the residual stresses present in the sample and the interaction of hydrogen with them, using the known sin2ψ method. T2 - PRICM-8 - 8th Pacific rim international congress on advanced materials and processing CY - Waikoloa, Hawaii, USA DA - 04.08.2013 KW - Hydrogen embrittlement KW - Energy dispersive diffraction KW - Hydrogen diffusion KW - Residual stresses PY - 2013 SP - 3481 EP - 3487 AN - OPUS4-28975 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Martin A1 - Eisenacher, Germar A1 - Schönfelder, Thorsten A1 - Wille, Frank T1 - Finite element simulation of the crush of package components made of encapsulated wood N2 - Typical transport packages used in Germany are equipped with encapsulated wooden impact limiting devices. We would like to present the current status regarding the development of a Finite Element (FE) material model for the crush of wood for the FE-code LS-DYNA. The crush of is a phenomenon governed by macroscopic fracture. Here, we would like to reproduce fracture and failure mechanisms over the continuous volume. In a first step we altered an existing LS-DYNA material model for foams, which considers an ellipse shaped yield surface. For the use for longitudinal compression of wood, we modified the existing material model to consider the deviatoric strain for the evolution of the yield surface as well. This is in accordance with the results of crush tests with spruce wood specimens, where the crushing deformation was rather deviatoric for uniaxial stress states and rather volumetric for multiaxial stress states We rate the basic idea of this approach to be reasonable, though other problems exist regarding the shape of the yield surface and the assumption of isotropic material properties. Therefore we developed a new transversal isotropic material model with two main directions, which considers different yield curves according to the multiaxiality of the stress state via a multi-surface yield criterion and a non-associated flow rule. The results show the ability to reproduce the basic strength characteristics of spruce wood. Nevertheless, problems with regularization etc. show that additional investigations are necessary. T2 - 11th International Conference on the Transport, Storage and Disposal of Radioactive Materials CY - London, UK DA - 15.05.2018 KW - Wood KW - FEM PY - 2018 SP - Paper 18517, 1 EP - 12 AN - OPUS4-45091 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas A1 - Rhode, Michael A1 - Yahyaoui, Hamza A1 - Kannengießer, Thomas ED - Duprez, Lode T1 - Hydrogen distribution in multi-layer welds of steel S960QL N2 - High-strength low-alloyed (HSLA) steels with yield strength ≥ 690 MPa have increasing importance in steel construction and civil engineering. However, weld processing of those steels is a major challenge. The susceptibility for degradation of mechanical properties of weld joints significantly increases in presence of hydrogen and can result in hydrogen assisted cracking (HAC). Generally, risk for HAC increases with increasing yield strength of HSLA steels. To minimize the incidence of HAC, it is essential to gain knowledge about both the (1) absorbed hydrogen amount and its distribution in the weld seam and (2) options to lower the amount of introduced hydrogen. Existing standards recommend heat treatment procedures (interpass temperature or post weld heat treatment) to reduce the diffusible hydrogen concentration in weldments. In this context, different weld seam geometries should be considered. For HSLA steel fabrication weld processing with seam opening angles of 45° to 60° is typical. Modern weld technologies allow welding with seam opening angles of 30° - reduced welding time and costs. In the present study, the hydrogen distribution in multi-layer welds of a 960 MPa HSLA steel was analysed. Influence of different seam opening angles as well as heat input, interpass temperature and post weld heat treatments were investigated. The welded samples were quenched in ice water immediately after welding and subsequently stored in liquid nitrogen. After defined warming up, small specimens were machined from the weld seam by water jet cutting. The diffusible hydrogen concentration was measured by carrier gas hot extraction with coupled mass spectrometer. The results showed, that low heat input and post weld heat treatment procedures can lower hydrogen concentrations in welds. Furthermore, a gradient of the hydrogen concentration was identified with increasing weld pool depth. By varying the seam opening angles different hydrogen concentrations were measured. T2 - Third International Conference on Metals & Hydrogen CY - Ghent, Belgium DA - 29.05.2018 KW - Hydrogen concentration KW - Welding KW - High-strength steel KW - Heat treatment KW - carrier gas hot extraction PY - 2018 SN - 978-9-08179-422-0 SP - P44 AN - OPUS4-45358 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas T1 - Online Monitoring of Reaction Forces and Stresses in Welded Components N2 - Today’s light weight design trends lead to a growing application of high-strength structural steels (yield strength ≥ 690 MPa). The mechanical properties of the weld and the component safety have to meet the increased requirements of these steel grades. However, high residual stresses in welded components are detrimental to their safety and integrity. Analyses concerning weld stresses in high-strength steels welded under component related restraint conditions revealed that heat control significantly affects global and local stresses. This occurs especially in highly restrained joints due to superimposing local and global stresses and may cause crack-critical stress-levels. In this study weld tests were performed with plates of high-strength steel in a special test facility. The experimental setup allowed transferring defined restraint conditions to the test welds similarly to real components. Temperature and reaction forces due to restraint were observed online while welding and cooling of multilayer-component MAG-welds. Mobile X-ray diffraction was used for local stress determination in the weld seam areas of the restrained specimens. It was found that interpass temperature has a major influence on the local and global welding forces and stresses. Thus, among the analysed results especially transverse residual stresses of the heat affected zone were strongly affected. T2 - The International Symposium on Visualization in Joining & Welding Science through Advanced Measurements and Simulation CY - Osaka, Japan DA - 26.11.2014 KW - Residual Stress KW - GMA welding KW - High-strength steel PY - 2014 VL - 2014, Volume 1 SP - 115 EP - 116 PB - Joining and Welding Research Institute, Osaka University CY - Osaka AN - OPUS4-47716 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Characterising Phase Transformations of Different LTT Alloys and their Effect on Residual Stresses and Cold Cracking N2 - Novel martensitic filler materials with specially adjusted martensite start temperatures (Ms) can counteract the cooling specific shrinkage due to expansion effects of the weld metal associated with phase transformations. That can be exploited to create compressive residual stresses in the weld and adjacent areas, i.e. beneficial for increasing fatigue strength. The Ms temperature is shifted via the chemical composition, mainly by the alloying elements nickel and chromium, resulting as well in different retained austenite contents. Investigations were made using different Low Transformation Temperature (LTT) alloys with varying nickel content. The resulting phase transformation temperatures were - for the first time - detected using high energy synchrotron diffraction and Single Sensor Differential Thermal Analysis (SS-DTA). Compared to angle dispersive diffraction, energy dispersive diffraction offers the possibility to measure residual stresses of the martensite and austenite phase parallel fast in one experiment up to depths of 100 µm. The residual stresses show significant distributions dependent on Ms temperature. The effect on the cold cracking behaviour of these alloys was investigated using the Tekken test. Results show that cold cracking can be avoided when appropriate contents of retained austenite are existent. PY - 2009 IS - IX-2311-09 SP - 1 EP - 9 PB - International Institute of Welding CY - Paris AN - OPUS4-19749 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Martin A1 - Wille, Frank T1 - Modelling of compression of wood filled impact limiter of casks for transportation of radioactive material N2 - Impact limiters of packages for transport of radioactive materials are in Germany typically steel-wood-sandwich-constructions, combining a relatively stiff steel structure bolted to the cask body, outer steel plates and different types of wood. By crushing the wood-steel-sandwich-structure between unyielding target and cask, kinetic energy of 9-m-free-fall is absorbed. Main energy absorber is wood under a high level of deformation. Wood under large deformations exhibits destruction of the fibre matrix. By analysing compression of impact limiter wood after drop tests with prototype casks for radioactive material, underlying mechanisms of wood crushing and corresponding energy absorption under large deformations are identified. Softening occurring at compression of wood is a function of lateral strain restriction of wood. Against the background of continuum mechanics an analogous model for compression of fibre bundle is presented. The model takes lateral strain restriction as triaxiality of stress state into account. Further modelling possibilities for wood with a continuum approach are described. Different material laws in the explicit Finite Element code LS-DYNA are analysed for possible application on the analogous model for the fibre bundle. Small scale compression tests with wooden specimens were modelled in order to evaluate the ability of different modelling techniques to simulate softening. Although modelling of compression of wood under large deformations is possible, softening could not be simulated purposefully. A drop test of a cask with impact limiting devices similar to existing impact limiters is simulated with different material laws for wood. Behaviour of impact limiting devices could not be simulated universally including influence of lateral strain restriction; nevertheless loading of the cask by crushing of impact limiter could be simulated purposefully. Verification with experimental results is compulsory. T2 - Ramtransport 09 - 8th International Conference on radioactive materials transport 2009 CY - Manchester, Great Britain DA - 2009-05-12 KW - Radioactive material KW - Transport KW - Impact limiter KW - Simulation KW - FEM PY - 2009 IS - PAP31 SP - 1 EP - 20 AN - OPUS4-19751 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Komann, Steffen A1 - Neumann, Martin A1 - Ballheimer, Viktor A1 - Wille, Frank A1 - Weber, Mike A1 - Qiao, Linan A1 - Droste, Bernhard T1 - Static and dynamic calculation approaches for mechanical design assessment of type B packages for radioactive material transport - 10193 T2 - WM2010 Conference CY - Phoenix, Arizona, USA DA - 2010-03-07 KW - Mechanische Bewertung KW - Radioaktives Material KW - Numerische Analyse KW - Typ B(U)-Verpackung PY - 2010 SP - 1 EP - 9 AN - OPUS4-21240 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kannengießer, Thomas A1 - Brauser, Stephan A1 - Kromm, Arne T1 - Synchrotron diffraction for in-situ characterizations of materials behaviour T2 - 3rd Inter-university research seminar (IURS 2010) - Advances in welding and joining CY - Pusan, Korea DA - 2010-05-13 KW - In-situ diffraction KW - Phase transformation KW - High strength steel KW - Residual stress PY - 2010 SP - 127 EP - 131 CY - Pusan, Korea AN - OPUS4-21352 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kannengießer, Thomas A1 - Lausch, Thomas A1 - Kromm, Arne T1 - Effects of heat control on the stress build up during high strength steel welding under defined restraint conditions T2 - International Conference on high strength steels for hydropower plants CY - Takasaki, Japan DA - 2009-07-20 KW - Welding KW - Heat control KW - Stress build up KW - High-strength steel KW - Restraint intensity PY - 2009 UR - http://www-it.jwes.or.jp/proceedings/en/3-10.pdf SP - 10-1 - 10-8 AN - OPUS4-22317 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kannengießer, Thomas A1 - Kromm, Arne T1 - In-situ studiesof phase transformation and residual stress build up in martensitic materials using synchrotron radiation T2 - 2nd IURS - Inter-university research symposium CY - Canmore, Alberta, Canada DA - 2009-05-20 KW - In-situ diffraction KW - Phase transformation KW - LTT alloy KW - Residual stress PY - 2009 IS - Paper 12 SP - 1 EP - 5 AN - OPUS4-22499 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kannengießer, Thomas A1 - Lausch, Thomas A1 - Kromm, Arne T1 - Effects of heat control on the stress build up during high-strength steel welding under defined restraint conditions T2 - 62nd IIW Annual assembly and conference CY - Singapore DA - 2010-07-12 KW - Welding KW - Heat control KW - Stress build up KW - High-strength steel KW - Restraint intensity PY - 2009 IS - IIW Doc IX-2316-09 (IX-L-1055-09) SP - 1 EP - 8 AN - OPUS4-22316 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kannengießer, Thomas A1 - Kromm, Arne A1 - Brauser, Stephan T1 - Synchrotron diffraction for visualization of solid state phase transformations T2 - VISUAL-JW 2010 - The international symposium on visualization in joining & welding science through advanced measurements and simulation CY - Osaka, Japan DA - 2010-11-11 KW - Synchrotron KW - EDXRD KW - Martensite KW - Residual stress KW - TRIP steel KW - Phase transformation PY - 2010 IS - MTJW-1 SP - 123 EP - 124 AN - OPUS4-22653 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eisenacher, Germar A1 - Scheidemann, Robert A1 - Neumann, Martin A1 - Sterthaus, Jens A1 - Kasparek, Eva Maria A1 - Völzke, Holger T1 - Stauchversuche mit querdehnungsbehinderten Fichtenholzproben verschiedener Faserorientierungen bei veränderlicher Dehnrate T1 - Compression tests with laterally constrained spruce specimens with varying fiber orientations and loading rates N2 - Im Zuge des Forschungsvorhabens ENREA (Entwicklung rechnerischer Analysemethoden für stoßdämpfende Strukturen beim Anprall oder Absturz von Abfallgebinden) führt die BAM systematische Untersuchungen an stoßdämpfenden Werkstoffen, unter anderem an Fichtenholz, durch. Zweck der mit diesen Untersuchungen erzeugten Datenbasis ist die Erstellung und Parametrierung eines Finite-Elemente- (FE-) Materialmodells, das die Modellierung holzgefüllter stoßdämpfender Bauteile von Transportbehältern für radioaktive Stoffe in der FE-Simulation ermöglichen soll. Anhand von Ergebnissen aus der ersten Versuchsphase werden der Einfluss der Dehnrate und der Faserorientierung auf das Kraft-Verformungs-Verhalten von Fichtenholz diskutiert. Anschließend wird die rechnerische Modellierung von Fichtenholz diskutiert und die Anforderungen an ein Materialmodell werden erläutert. N2 - In the course of research project ENREA (development of numerical methods for analyzing impact limiters subjected to impact or drop scenarios), BAM is systematically investigating impact limiting materials, e. g. spruce wood. Goal of these investigations is to establish and parameterize a finite element (FE) material model which enables the modeling of wood filled impact limiting devices of transport casks for radioactive materials. Using results of the first test stage, the effect of loading rate and fiber orientation on the force-deflection characteristics of spruce wood will be presented. Following, computational modeling of spruce wood including requirements for a material model will be discussed. T2 - KONTEC 2011 - 10. Internationales Symposium "Konditionierung radioaktiver Betriebs- und Stilllegungsabfälle" CY - Dresden, Germany DA - 06.04.2011 PY - 2011 N1 - Sprachen: Deutsch/Englisch - Languages: German/English SP - 465 EP - 478 AN - OPUS4-23684 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Martin A1 - Wille, Frank T1 - Rechnerische Simulation des mechanischen Verhaltens von holzgefüllten Stoßdämpfern von Transportbehältern für radioaktive Stoffe N2 - Basierend auf Fallversuchen mit Transportbehältern für radioaktive Stoffe sowie auf einem Versuchsprogramm mit Holzproben wurden die Energieabsorptionsmechanismen identifiziert und ein Modell für das Verhalten von Fichtenholz bei axialer Belastung entwickelt. Das Modell zieht für die Kompression von Holz die seitliche Dehnungsbehinderung – im kontinuumsmechanischen Zusammenhang wäre das die Mehrachsigkeit des Spannungszustandes im Kontinuum – in Betracht. Die Energie, die vom Holz absorbiert werden kann, ist umso größer, je größer die seitliche Dehnungsbehinderung ist. Für die Modellierung mit Finite Elemente Methoden wurden verschiedene Modellierungsstrategien untersucht, keine der vorgeschlagenen Modellierungsstrategien war in der Lage, dass Verhalten von Holz bei Druckbeanspruchung und großen Deformationen inkl. der Entfestigung zu modellieren. Bei Verwendung einer entfestigenden Fließkurve zeigt das Modell ausgeprägte Netzabhängigkeiten und numerischen Instabilitäten. Für die Modellierung der Entfestigung mit Hilfe einer von der Mehrachsigkeit des Spannungszustandes gesteuerten Fließflächenevolution ist kein geeignetes Materialmodell vorhanden. Anhand der Simulation eines Fallversuchs mit einem Behälterkörper und stoßdämpfenden Bauteilen im Maßstab 1:2 wurde gezeigt, dass zwar eine vollständige Modellierung des Stoßdämpferverhaltens inkl. Entfestigung nicht möglich war, aber das Stoßdämpferverhalten mit einer nicht-entfestigenden Fließkurve sinnvoll modelliert werden konnte. Eine Verifikation des Modellierungsansatzes am real zu modellierenden Bauteil ist zwingend erforderlich. Wenn signifikante Änderungen zwischen Verifikations- und Simulationsobjekt auftreten, ist die Zuverlässigkeit der Rechenergebnis als gering zu bewerten. Nur wenn die auftretenden Kompressionsmechanismen durch eine Analyse des Stoßdämpferholzes bestimmt werden können, ist eine zuverlässige Ermittlung von Stoßdämpferkräften- und verformungen möglich. T2 - Jahrestagung Kerntechnik 2011 CY - Berlin, Germany DA - 17.05.2011 KW - Radioaktive Stoffe KW - Transport KW - Stoßdämpfende Bauteile KW - FEM KW - Simulation PY - 2011 SP - 1 EP - 6 AN - OPUS4-23851 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kannengießer, Thomas A1 - Cross, Carl Edward T1 - Effect of tack placement on local weld displacement and solidification cracking during arc welding of aluminium alloy 6083 T2 - 1st South-east Asia International Institute of Welding Congress "Welding in South-East-Asia: A Challenge for the Future" CY - Bangkok, Thailand DA - 2006-11-21 KW - Heißriss KW - Aluminiumlegierung KW - Erstarrungsriss KW - Heften PY - 2006 SP - 480 EP - 491 (Paper No. 52) PB - Welding Institute of Thailand CY - Bangkok AN - OPUS4-14218 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kannengießer, Thomas T1 - Influence of Arc Welding Process and of Stabilization Annealing on Welding Residual Stresses of Ni-Base Alloy KW - Ni-base alloy KW - Alloy 617 KW - Welding residual stresses KW - Hole drilling method PY - 2008 SP - 915 EP - 921 AN - OPUS4-16508 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Martin A1 - Ballheimer, Viktor A1 - Wille, Frank T1 - Estimation of cask deceleration and impact limiter deformation under 9m drop test conditions using the calculation tool “ImpactCalc” T2 - PATRAM 2007, 15th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Miami, Florida, USA DA - 2007-10-21 KW - Impact limiter KW - Calculation KW - Maximum deceleration KW - Maximum deformation PY - 2007 SP - 1 EP - 8 PB - Institute of Nuclear Materials Management AN - OPUS4-17496 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Martin A1 - Droste, Bernhard A1 - Wille, Frank T1 - Using Scale Model Impact Limiter in the Type Assessment of Transport Casks for Radioactive Material T2 - PATRAM 2007, 15th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Miami, Florida, USA DA - 2007-10-21 KW - Impact limiter KW - Similarity KW - Scaling PY - 2007 IS - (Abstract # 86) SP - 1 EP - 8 PB - Institute of Nuclear Materials Management AN - OPUS4-17495 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Musolff, André A1 - Müller, Karsten A1 - Neumann, Martin A1 - Kadji, Arsène Brice A1 - Droste, Bernhard T1 - Drop Test Results of the Full-scale CONSTOR V/TC Prototype T2 - PATRAM 2007, 15th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Miami, Florida, USA DA - 2007-10-21 PY - 2007 IS - Abstract #65 SP - 1 EP - 7 PB - Institute of Nuclear Materials Management AN - OPUS4-17838 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Komann, Steffen A1 - Neumann, Martin A1 - Ballheimer, Viktor A1 - Wille, Frank A1 - Weber, Mike A1 - Qiao, Linan A1 - Droste, Bernhard T1 - Mechanical assessment within type B packages approval - the application of static and dynamic calculation approaches T2 - PATRAM 2010 - 16th International symposium on the packaging and transport of radioactive materials CY - London, UK DA - 2010-10-03 KW - Mechanische Bewertung KW - Radioaktives Material KW - Numerische Analyse PY - 2010 SP - 1 EP - 8(?) AN - OPUS4-23384 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Griesche, Axel A1 - Beyer, Katrin A1 - Kannengießer, Thomas A1 - Calzada, E. T1 - Hydrogen diffusion measurements in steels using neutron imaging N2 - Revealing hydrogen embrittlement mechanisms in steels is of great interest to scientists and engineers. Neutron radiography makes it possible to measure in-situ hydrogen diffusion with high spatial and temporal resolution at concentrations as low as 20 ppm. We compare hydrogen-charged specimens with hydrogen-free reference specimens and use calibration standards to normalize the hydrogen concentrations. This allows quantitative tracking of the hydrogen concentration evolution as a function of time, space and temperature. Furthermore, a view into the material with 'neutron eyes' facilitates the detection of cavities that contain molecular hydrogen. KW - Hydrogen KW - Diffusion KW - Steel KW - Neutron radiography PY - 2012 UR - http://cdn.frm2.tum.de/fileadmin/stuff/information/documents/annualReports/Annual_Report_2011_online_version.pdf SP - 50 EP - 51 AN - OPUS4-25981 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Witte, Julien A1 - Schröpfer, Dirk A1 - Börner, Andreas A1 - Kannengießer, Thomas A1 - Michels, H. A1 - Hamm, C. A1 - Appelt, M. A1 - Hamacher, M. T1 - Ultraschallunterstütztes Fräsen zur Reduzierung der Belastung auf Werkzeug und Bauteiloberfläche von Eisenaluminid-Bauteilen N2 - Intermetallische Werkstoffe werden für Hochtemperaturanwendungen immer wichtiger. Insbesondere Aluminide mit hohen spezifischen Festigkeiten haben ein großes Potenzial für Leichtbauanwendungen, z. B. werden Titanaluminide bereits in Flugzeugturbinen eingesetzt. Ökonomische und ökologische Aspekte sind die treibende Kraft zur Substitution konventioneller Legierungen, z. B. Nickelbasislegierungen, die eine wesentlich höhere Kostenintensität und ein höheres Gewichts-Festigkeits-Verhältnis aufweisen. Insbesondere Eisenaluminide (FeAl) sind aufgrund guter mechanischer Eigenschaften und der guten Verfügbarkeit der wichtigsten Hauptlegierungselemente attraktiv. Speziell entwickelte FeAl-Legierungskonzepte ermöglichen eine wirtschaftliche Produktion im Kokillenguss, bei der die Erstarrung der Schmelze spezielle komplexe Gefüge ermöglicht, um die hohen thermischen und mechanischen Eigenschaften durch eine hohe Anzahl von harten Ausscheidungen entlang der Korngrenzen zu erreichen. Zu diesen Eigenschaften gehört aber auch, dass notwendige Bearbeitungsschritte, wie das Schlichtfräsen, zur Erzielung komplexer Endkonturen, zu vorzeitigem Werkzeugverschleiß und geringen Oberflächengüten führen. Für das finale FeAl-Bauteil ist eine hohe Oberflächenintegrität insbesondere in sicherheitsrelevanten Anwendungen in der Luftfahrt oder im Energiebereich erforderlich. Aus diesem Grund konzentriert sich die vorliegende Untersuchung auf die Mechanismen und die Minimierung des Werkzeugverschleißes und die Auswirkungen auf die Oberfläche eines in Kokille vergossenen FeAl-Bauteils. Neben den Optimierungen des Fräsprozesses und der Werkzeugparameter (Geometrie, Material) wird ein modernes hybrides Bearbeitungsverfahren, das ultra-schallunterstützte Fräsen (USAM), eingesetzt, bei dem eine Überlagerung mit einer hochfrequenten Schwingung des rotierenden Werkzeugs erzeugt wird. Analysen der Kräfte und Temperaturen im Fräsprozess, der Verschleißerscheinungen am Werkzeug und der Oberflächenintegrität zeigen positive Auswirkungen durch USAM. Darüber hinaus wird eine valide Grundlage für die Optimierung des Werkzeugs und des Fräsprozesses geschaffen, um eine hohe Oberflächenintegrität (z. B. Verringerung von Zugeigenspannungen und Defekten) und eine längere Werkzeuglebensdauer zu gewährleisten, die zukünftig eine wirtschaftliche Herstellung von FeAl-Bauteilen ermöglicht. T2 - 5. Symposium Materialtechnik CY - Clausthal-Zellerfeld, Germany DA - 23.02.2023 KW - Eisenaluminid KW - Ultraschallunterstütztes Fräsen KW - Werkzeugverschleiß KW - Oberflächenintegrität PY - 2023 VL - 12 SP - 738 EP - 748 PB - Shaker Verlag CY - Düren AN - OPUS4-59219 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wosniok, Aleksander A1 - Schukar, Marcus A1 - Woody, Paul A1 - Wang, Bin A1 - Breithaupt, Mathias A1 - Kriegsmann, Andreas T1 - Distributed fiber optic strain sensing for structural health monitoring of 70 MPa hydrogen vessels N2 - We report on the development and testing of 70 MPa hydrogen pressure vessels with integrated fiber optic sensing fibers for automotive use. The paper deals with the condition monitoring of such composite pressure vessels (CPVs) using the optical backscatter reflectometry (OBR) applied for a distributed fiber optic strain sensing along fully integrated polyimide-coated single-mode glass optical fiber (SM-GOF). The sensing fibers were embedded into the vessel structure by wrapping them over the polymer liner during the manufacturing process of the carbon fiber reinforced polymer (CFRP). Detecting local strain events by the integrated fiber optic sensors can be an opportunity for monitoring the material degradation of CPVs under static and cyclic loading. T2 - 11th European Workshop on Structural Health Monitoring CY - Potsdam, Germany DA - 10.06.2024 KW - Fiber optic sensor KW - Distributed strain sensing KW - Composite pressure vessel KW - Structural health monitoring KW - Fiber-reinforced plastics PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-603105 SP - 1 EP - 8 PB - NDT.net AN - OPUS4-60310 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heunisch, Andreas A1 - Marzok, Ulrich A1 - Münchow, Marco A1 - Müller, Ralf A1 - Rabe, Torsten T1 - In situ characterization of the sintering behavior of LTCC laminates with embedded cavities by high temperature laser profilometry N2 - Three-dimensionally structured LTCC multilayer with channels and inner cavities are required for numerous applications like microreactors, microfluidic systems or sensors. For the performance of such devices, the dimensional accuracy of the embedded structures is crucial. In the green state, the desired structures can be precisely implemented in the LTCC tapes by laser cutting, punching or milling. Unfortunately, during lamination and sintering, shape integrity of cavities and channels is notably affected by warpage and deformation. To investigate the sintering behavior of structured LTCC laminates, a newly developed High Temperature Laser Profilometer (HTLP) can be used. The HTLP allows 3D in-situ shape detection of flat ceramic samples and tapes all along the sintering process. It is applicable for temperatures up to 1000 °C and sample sizes up to 200 mm × 200 mm × 10 mm. During a measurement, the rotating sample is scanned spirally by a linearly moving laser distance sensor through a slot in the furnace top wall. Distance and position values deliver a 3D surface image of the sample. Current lateral dimensions, which are determined by sintering shrinkage, can be measured continuously. Local deformation and warpage can be visualized time- and temperature-resolved. This new method was used, to analyze the sintering behavior of LTCC multilayer laminates containing large size cavities. These were fabricated out of punched green sheets by low pressure lamination without inserts. Samples with cavities of varying cross sections, as well as cavities with and without connection to the surface were observed. T2 - CICMT 2013 - IMAPS/ACerS 9th International conference and exhibition on ceramic interconnect and ceramic microsystems technologies CY - Orlando, FL, USA DA - 23.04.2013 KW - LTCC multilayer KW - Embedded cavities KW - High temperature laser profilometry KW - Low pressure lamination KW - Micro fluidics PY - 2013 DO - https://doi.org/10.4071/cicmt-tha44 SP - 275 EP - 282 AN - OPUS4-35077 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stajanca, Pavol A1 - Lacraz, A. A1 - Kalli, K. A1 - Schukar, Marcus A1 - Krebber, Katerina ED - Berghmans, F. ED - Mignani, A. G. T1 - Strain sensing with femtosecond inscribed FBGs in perfluorinated polymer optical fibers N2 - In this work, the potential of fiber Bragg gratings (FBGs) in low-loss perfluorinated polymer optical fibers (PF-POFs) is explored. The FBG is femtosecond-inscribed in a commercial multi-mode (MM) PF-POF based on Cytop® polymer. Femtosecond inscription leads to creation of a highly saturated grating with a number of higher order reflection Peaks visible throughout the visible and near-infrared spectral region. For 2 mm long FBG having a pitch of 2.2895 μm, a total of nine higher-order MM reflection bands are visible spanning from 1548 nm (4th order) to 520 nm (12th order). Strain sensitivity was measured for 6 peak bands in 500-900 nm region, where relatively low cost CCD based spectrometers and broadband LEDs are available. Strain sensitivity increases almost linearly with increasing initial peak wavelength, growing from 4.82 ± 0.02 nm/% measured for 12th order peak at 517 nm to 8.12 ± 0.04 nm/% measured for 7th order peak at 883 nm. These values correspond to roughly 20 % higher sensitivity than silica FBGs exhibit in this spectral range. The gratings in PF-POFs combine the higher strain sensitivity and low-loss operation while maintaining the mechanical advantages of polymer optical fibers. Therefore, they hold a high potential for considerable broadening of polymer optical fiber Bragg gratings application range. T2 - Photonics Europe 2016, Optical Sensing and Detection IV CY - Brussels, Belgium DA - 03.04.2016 KW - Fiber Bragg gratings KW - Fiber optics sensors KW - Perfluorinated polymer optical fiber KW - Cytop KW - Strain sensitivity PY - 2016 SN - 978-1-5106-0144-4 DO - https://doi.org/10.1117/12.2225081 SN - 0277-786X VL - 9899 SP - 989911-1 EP - 989911-7 PB - SPIE AN - OPUS4-35926 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Burkert, Andreas A1 - Burkert, Annette A1 - Lehmann, Jens A1 - Müller, Thoralf A1 - Bohlmann, Tatjana T1 - Detektion korrosionsempfindlicher Oberflächen nichtrostender Stähle durch die Verarbeiter N2 - Umfangreiche Untersuchungen im Vorhaben "Passivschichtstabilität" (IGF-Nr.: 15554N) haben gezeigt, dass werkstoffseitig ein breites Spektrum an produktionsseitigen Fehlern und Un-gänzen für unerwartete Korrosionserscheinungen an nichtrostenden Stählen ursächlich ist. Dazu gehören chemische Inhomogenitäten (Ausscheidungen, Aufkohlung), geometrische Oberflächenfehler (Hinterschnitte, Walzfehler) und die Ablagerung von Fremdstoffen aus dem Herstellungsprozess. Im Bereich derartiger Ungänzen wird die Passivschichtausbildung verhindert bzw. erschwert. Damit ist die erwartete Korrosionsbeständigkeit der Werkstoffe selbst bei geringer Korrosivität der Umgebung nicht sichergestellt, so dass ein örtlicher Korrosionsangriff auftritt. Werden solche Materialien weiterverarbeitet, kommt es in der Folge zu Schadensfällen und Rechtsstreitigkeiten. Die Schadenssummen liegen in Größen-ordnungen um 10.000 € bis hin zu mehren hunderttausend Euro. Da Stabmaterial auch als Vormaterial für die Herstellung von Befestigungsmitteln wie Dübeln und Ankern zum Einsatz kommt, sind auch sicherheitsrelevante Probleme nicht ausgeschlossen. Die zugrunde-liegenden Werkstoff- und Oberflächenfehler sind bei der Inaugenscheinnahme auch mit umfangreichen Erfahrungen nicht zu erkennen, da diese mikroskopisch klein bzw. durch das Schliffbild überdeckt sind. Erst durch metallographische Untersuchungen lassen sich die Fehler eindeutig belegen. Es fehlt deshalb ein Nachweisverfahren, mit dem die Verarbeiter Oberflächen mit erhöhter Korrosionsneigung identifizieren können, um sich vor wirtschaftlichen Folgeschäden zu schützen. Als interessanter Ansatz bzgl. der relevanten Zielgruppen hat sich eine Indikatorlösung mit Zusatz eines Aktivators erwiesen, welche durch ein Bindemittel in einen gelartigen Zustand gebracht wird. Erste Tastversuche an gezielt hergestellten korrosionsempfindlichen Oberflächen, sowie einem fehlerhaften Werkstoffzustand aus der Praxis konnten mittels dieses Tests identifiziert werden. KW - Korrosionsschnelltest KW - Nichtrostender Stahl KW - Edelstahl Rostfrei PY - 2014 SP - 1 EP - 72 CY - Berlin AN - OPUS4-33584 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Burkert, Andreas A1 - Fischer, Joachim A1 - Lehmann, Jens A1 - Müller, Thoralf T1 - Korrosionsbeständigkeit nichtrostender Stähle an der Atmosphäre N2 - Über das Korrosionsverhalten nichtrostender Stähle bei atmosphärischer Beanspruchung liegen umfangreiche Erfahrungen aus jahrzehntelangen praktischen Anwendungen weltweit vor. Systematische Auslagerungsversuche unter spezifischen Umgebungsbedingungen ergänzen diese Erfahrungen. Die daraus gewonnenen Daten erlauben die beanspruchungsgerechte Werkstoffauswahl. Unter vielen atmosphärischen Bedingungen sind die nichtrostenden Stähle bei freier Bewitterung, auch unter langzeit- oder dauerfeuchten Bedingungen vollständig korrosionsbeständig. Die Auswahl der nichtrostenden Stähle muss den jeweiligen Einsatzbedingungen angepasst werden, um in jedem Fall sicherzustellen, dass der passive Zustand aufrechterhalten bzw. eine erneute Passivierung unter den Einsatzbedingungen möglich ist. Störungen der Passivschichtausbildung führen zu verminderter Korrosionsbeständigkeit mit den für nichtrostende Stähle typischen örtlichen Korrosionserscheinungen. Das Merkblatt gibt Hinweise zur Werkstoffauswahl, zur Oberflächenausführung, zur Konstruktion sowie zu Verarbeitung, Nachbehandlung und Reinigung. KW - Verarbeitung KW - Werkstoffauswahl KW - Oberflächenausführung PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-367612 UR - http://www.edelstahl-rostfrei.de/page.asp?pageID=1583 VL - 828 SP - 1 EP - 12 PB - Informationsstelle Edelstahl Rostfrei CY - Düsseldorf ET - 3. Auflage AN - OPUS4-36761 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Prewitz, Marc T1 - Charakterisierung von Glas-Polymer Verbundmaterialien fur die Hochdruckspeicherung von Wasserstoff N2 - In der vorliegenden Arbeit werden Glaskapillaren und Strukturen aus Borosilikatglas (Simax) f¨ur die Hochdruckspeicherung von Wasserstoff betrachtet. Um die mechanischen Belastungen zu analysieren und anschließend ein optimiertes Speicherdesign abzuleiten, findet die Finite Element Methode (FEM) Einsatz. Die notwendigen Materialkennwerte werden zuvor experimentell ermittelt. Dazu geh¨oren die Festigkeit, die Schubfestigkeit der Grenzfl¨ache Klebung/Glas, der Wasserstoffpermeationskoeffizient, das Temperatur-Zeit-abh¨angige Verhalten, sowie die obere Temperatureinsatzgrenze. Die Glasfestigkeit ist stark abh¨angig von der Oberfl¨acheng¨ute. Daher werden in dieser Arbeit Kapillaren selber gezogen und beschichtet. Der Einfluss auf die Festigkeit wird mit Hilfe von Berstversuchen untersucht. Die eingesetzten Polymere werden zus¨atzlich mit dem Push-out Versuch, der dynamisch mechanischen Analyse und der Permeationsmessung charakterisiert. Dar¨uber hinaus wird aus den DMA Versuchen ein viskoelastisches Materialmodell abgeleitet, womit der Temperatur- und Zeiteinfluss auf die mechanische Belastung simuliert wird. Unter Beachtung der experimentell gewonnenen Erkenntnisse, sowie der durchgef¨uhrten Simulation ist es m¨oglich, ein optimiertes Speicherdesign zu erstellen und Aussagen ¨uber die Einsatzgrenzen zu treffen. KW - Wasserstoffspeicherung KW - Glaskapillaren KW - Polymercoating PY - 2017 UR - https://depositonce.tu-berlin.de/handle/11303/6261 SP - 1 EP - 150 CY - Berlin AN - OPUS4-51065 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Liepold, Philipp A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Einfluss des Einspanngrades auf die Bildung von Erstarrungsrissen in Überlappverbindungen hochfester Stähle N2 - Im Beitrag werden Ergebnisse aus Versuchen mit dem Controlled Thermal Severity (CTS)-Test vorgestellt, der für sehr stark eingespannte Kehlnähte bekannt ist. Niedriglegierte Schweißungen an hochfesten Stählen sind nicht anfällig für Erstarrungsrissbildung. Unter dem besonderen Einfluss eines hohen Einspanngrades wurde die Erstarrungsrissneigung durch Abmessen der Rissflächen als Funktion der Schweißparameter und des Einspanngrades für vier hochfeste Schweißzusätze im MAG-Schweißen untersucht. Die Tests zeigen, dass sowohl eine Erhöhung des Einspanngrades als auch eine Änderung der Schweißparameter (hinsichtlich Streckenenergie und Geschwindigkeit) zu mehr Erstarrungsrissfläche führen. Besonders die Kombination aus sehr hohem Einspanngrad und hoher Streckenenergie plus hoher Schweißgeschwindigkeit sollte im Sinne der Erstarrungsrissminimierung vermieden werden. T2 - DVS-Congress CY - Erfurt, Germany DA - 16.09.2024 KW - CTS KW - Erstarrungsrisse KW - Kehlnähte PY - 2024 VL - 2024 SP - 193 EP - 200 AN - OPUS4-61069 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Nina T1 - Auswirkungen von Ti und Nb auf die physikalisch simulierten WEZ- Bereiche von hochfestem Feinkornbaustahl S690QL N2 - Mikrolegierungselemente, wie Nb und Ti, sind für die signifikante Festigkeitssteigerung von vergüteten, hochfesten Feinkornbaustählen mit einer Nominalstreckgrenze ≥ 690 MPa unerlässlich. Nominalvorgaben zur chemischen Zusammensetzung geben den Herstellern dieser Stähle dabei nur obere Grenzwerte für die Legierungsanteile in der chemischen Zusammensetzung vor. Weiterhin wirken sich bereits kleine Abweichungen in der Legierungsroute teilweise drastisch auf die mechanischen Eigenschaften aus. Somit wird eine adäquate Vorhersage der Schweißeignung und der Integrität der Schweißverbindung aufgrund der variierenden Mikrostruktur erschwert oder ist gar nicht möglich. Unerwünschte Nebeneffekte sind die mögliche Erweichung der Wärmeeinflusszone (WEZ) als auch der gegenteilige Effekt der Aufhärtung. Vor diesem Hintergrund werden erstmals systematisch die unterschiedlichen Mikrolegierungsrouten mit variierenden Ti- und Nb-Gehalten an Versuchsschmelzen untersucht. Die Stahlgüte S690QL bildet dabei die Grundlage der chemischen Zusammensetzung sowie der entsprechenden Wärmebehandlung. Zur Untersuchung des Einflusses von unter-schiedlichen Mikrolegierungsrouten auf die Ausbildung der WEZ wurden physikalische Simulationen an Abschreckproben an einem Dilatometer durchgeführt. Der Fokus der analytischen Betrachtungen lag hier auf der Identifikation der Phasenumwandlungen beim Abkühlen und der finalen WEZ-Gefüge. Ein besonderes Untersuchungsmerkmal bestand in der vorliegenden Arbeit bei der Untersuchung des doppelten Anlassvorganges bzw. der Simulation der interkritischen WEZ (IKWEZ), die sich beim Mehrlagenschweißen ausbildet. Ergeb-nisse haben gezeigt, dass der Effekt unterschiedlicher Mikrolegierungsrouten einen signifikanten Einfluss auf die Ausbildung der einzelnen WEZ-Bereiche aufweist. Insbesondere haben Einflüsse, wie die thermische Stabilität der Ausscheidungen wie Ti- oder Nb-Karbonitride und Synergieeffekte zwischen anderen Elementen wie Mo eine Wirkung auf die Phasenumwandlung in der WEZ. Die Ergebnisse lassen sich gut mit den realen Schweißungen kongruieren und stellen hier eine systematische Validierung und einen umsetzbaren Wissenstransfer in die Entwicklung der Stahlherstellung und ihrer fügetechnischen Verarbeitung dar. T2 - DVS CONGRESS 2024 CY - Erfurt, Germany DA - 16.09.2024 KW - WEZ-Erweichung KW - Mikrolegierungseinflüsse KW - Dilatometrie PY - 2024 SP - 1 EP - 9 AN - OPUS4-61379 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröpfer, Dirk A1 - Reichel, Levin A1 - Kannengießer, Thomas T1 - Beanspruchungsgerechte Reparatur von Schweißverbindungen bei der Fertigung von Bauteilen aus hochfesten Feinkornbaustählen N2 - Zunehmende Anlagengrößen im Bereich Windenergie erfordern hochfeste Stähle, um vorhandene Leichtbaupotenziale auszuschöpfen. An die schweißtechnische Verarbeitung dieser Stahlgüten werden hohe Anforderungen gestellt. Bei mittels zerstörungsfreier Prüfung festgestellten Fehlstellen empfehlen geltende Verarbeitungsrichtlinien lokales Ausfugen und Reparaturschweißen. Degradationen der speziellen hochfesten Gefüge und Werkstoffeigenschaften sowie hohe Schrumpfbehinderungen der umliegenden Struktur ausgefugter Bereiche erhöhen das Risiko erneuter Schweißdefekte, insbesondere durch Überlagerung von globalen und lokalen schweißbedingten Eigenspannungen nach dem Reparaturschweißen. Fehlende Informationen über geeignete Reparaturkonzepte in den Regelwerken können dazu führen, dass reparaturbedingte Beanspruchungen unzureichend berücksichtigt werden. Das FOSTA-Vorhaben P1311 (IGF20162N) fokussiert das Reparaturschweißen zweier hochfester Stähle: S500MLO für Offshore-Anwendungen und S960QL für Errichterstrukturen, z. B. Mobilkräne. Simulationen von Einspannbedingungen und Bauteilanalysen sowie Versuche mit anwendungs- bzw. realitätsnahen Bauteilstrukturen ließen sich auftretende schweißbedingte Beanspruchungen mittels Röntgendiffraktometrie (XRD), Härtemessungen und metallografischer Untersuchungen ermitteln. In diesem Beitrag steht die Interaktion aus Wärmeführung und konstruktiver Steifigkeit als Einfluss auf die entstehenden Beanspruchungen bei einfacher und mehrfacher Reparatur im Vordergrund. Die Ergebnisse zeigen, dass sich risskritische Eigenspannungen durch adaptierte Wärmeführungskonzepte vermeiden lassen, und dass dies eine Grundlage für Verarbeitungsempfehlungen und für normative Vorgaben ist. Dies kann insbesondere kleine und mittelständischen Unternehmen bei einer wirtschaftlichen, beanspruchungsgerechten Reparatur hochfester geschweißter Bauteilen unterstützen. T2 - DVS Innovationstage 2024 CY - Düsseldorf, Germany DA - 10.04.2024 KW - Mod. Sprühlichtbogen KW - Reparaturschweißen KW - Thermisches Ausfugen KW - Offshore KW - P1311 PY - 2024 SP - 120 EP - 126 AN - OPUS4-61931 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wandtke, Karsten A1 - Engelking, Lorenz A1 - Schröpfer, Dirk A1 - Scharf-Wildenhain, Ronny A1 - Hälsig, Andre A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Fertigungsbedingte Beanspruchungen und Kaltrisssicherheit in generativ gefertigten Bauteilen aus hochfesten Feinkornbaustählen N2 - Additive Fertigungsverfahren wie das Direct Energy Deposition-Arc (DED-Arc) oder Wire Arc Additive Manufacturing (WAAM) ermöglichen die effiziente Herstellung gewichtsoptimierter, endkonturnaher Bauteile im modernen Stahlbau. Steigerungen der Effizienz können durch den Einsatz hochfester Stähle erreicht werden, insbesondere durch Verringerung von Wandstärken und Bauteilgewicht sowie signifikante Einsparung von Kosten, Zeit und Ressourcen. DED-Arc Schweißzusatzwerkstoffe sind bereits auf dem Markt verfügbar, allerdings fehlen Richtlinien und quantitative Kenntnisse über die schweißbedingte Beanspruchung während der Fertigung und im Betrieb, welche den industriellen Einsatz stark limitieren. In einem gemeinsamen Projekt der BAM und der Technischen Universität Chemnitz wurden die wesentlichen Einflüsse und komplexen Wechselwirkungen von Werkstoff, Fertigungsverfahren, Konstruktion und Bearbeitungsschritten auf die Eigenspannungen untersucht. Ziel war es, den stahlverarbeitenden Anwendern, insbesondere KMU, eine risssichere und beanspruchungsgerechte Herstellung und Modifizierung von Bauteilen und Halbzeugen aus hochfesten Feinkornbaustahl unter Verwendung MSG-basierter generativer Verfahren zu ermöglichen. T2 - DVS Innovationstage 2024 CY - Düsseldorf, Germany DA - 10.04.2024 KW - Wire Arc Additive Manufacturing (WAAM) KW - Feinkornbaustähle KW - Additive Fertigung KW - Kaltrisssicherheit KW - Direct Energy Deposition-Arc (DED-Arc) PY - 2024 SP - 96 EP - 104 AN - OPUS4-61932 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wandtke, Karsten A1 - Schröpfer, Dirk A1 - Scharf-Wildenhain, R. A1 - Hälsig, A. A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - WAAM process influences on local microstructure and residual stresses in high-strength steels N2 - High-strength fine-grain structural steels have great potential for weight optimization of many modern engineering structures. Efficient manufacturing can be achieved here above all by Wire Arc Additive Manufacturing (WAAM). First commercial high-strength welding consumables for WAAM are already available. Due to a lack of knowledge and guidelines for the industry regarding welding residual stresses and component safety in manufacturing and operation, their application is still severely limited. Residual stresses play a crucial role here, as the special microstructure of high-strength steels is sensitive to cold cracking. For this reason, process- and material-related influences, as well as the design effects on residual stress formation, are being investigated in a project funded by the AiF (FOSTA P1380/IGF 21162 BG). This study focuses on determining the interactions between heat control during WAAM process, resulting hardness, microstructure, and residual stresses, analyzed by X-ray diffraction. Welding experiments using geometrically similar AM specimens show that, with regard to the heat input, the energy per unit length in particular leads to significantly affected cooling times and microstructures and causes pronounced localized effects in terms of residual stresses in the upper weld beads. T2 - 46th MPA-Seminar CY - Stuttgart, Germany DA - 12.10.2021 KW - Wire Arc Additive Manufacturing KW - High-strength structural steels KW - Vickers hardness KW - Residual stresses PY - 2021 VL - 46 SP - 296 EP - 306 PB - MPA-Stuttgart AN - OPUS4-53571 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Liepold, Philipp ED - Kromm, Arne ED - Kannengießer, Thomas T1 - Anwendung von Convolutional Neural Networks (CNNs) bei der Erkennung von Rissen im Modifizierten Varestraint-Transvarestraint-Heißrisstest (MVT-Test) N2 - Der Modifizierte Varestraint-Transvarestraint-Test wird an der Bundesanstalt für Materialforschung und -prüfung als Variante des Varestraint-Tests verwendet. Die Auswertung dieser Tests findet klassisch durch Abmessungen der entstandenen Risse unter dem Lichtmikroskop statt. Eine solche Auswertung ist aufwendig und fehleranfällig. Convolutional Neural Networks können trainiert werden, um die Risse auf digitalen Bildern zu segmentieren, wodurch der menschliche Fehler in der Auswertung eliminiert werden kann. Die Ergebnisse können durch Overlay mit den Originalbildern verglichen werden. T2 - DVS-Congress, Große Schweißtechnische Tagung CY - Essen, Germany DA - 11.09.2023 KW - CNN KW - MVT KW - KI PY - 2023 SN - 978-3-96144-231-7 SN - 978-3-96144-230-0 VL - 2023 SP - 153 PB - Print Media Group GmbH & Co. KG CY - Hamm AN - OPUS4-59336 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bonnerot, Olivier A1 - Del Mastro, G. A1 - Hammerstaedt, J. A1 - Mocella, V. A1 - Rabin, Ira ED - Capasso, M. ED - Davoli, P. ED - Pellé, N. T1 - XRF Ink Analysis of Selected Fragments from the Herculaneum Collection of the Biblioteca Nazionale di Napoli N2 - Hundreds of papyrus rolls, carbonized during the 79CE eruption of Mount Vesuvius, were discovered in 1754 at Herculaneum. Sophisticated mechanical methods for unrolling the best-preserved scrolls have been applied, with varying success. However, such processes have been abandoned, to prevent risk from irremediable damage or loss and to preserve the integrity of the extremely fragile rolls. Following the development of X-ray based non-invasive techniques, attempts to virtually unroll the scrolls were made. The most common ink in Antiquity was carbon-based, and the main element of carbonized papyrus is carbon, making these investigations difficult. However, some attempts with synchrotron X-ray phase-contrast tomography (XPCT) were successful. Recently, the identification of antique inks containing metals raised hope that if some of the inks contain metal the rolls can be virtually unrolled using conventional CT- technique. We investigated the inks of a selection of partially unrolled fragments stored at the Biblioteca Nazionale di Napoli with X-ray fluorescence in order to select the best candidates for tomography. Despite the many difficulties (analysis of several layers sticking together, letters barely visible, difficulty to separate contribution from the ink and from the papyrus, inhomogeneity of the support, fragility of the fragments…), encouraging results were found, with a number of inks from Greek fragments found to contain additions to the soot (Fe, Pb, Cu P). KW - XRF KW - ink KW - Herculaneum KW - papyrus PY - 2022 UR - http://siba-ese.unisalento.it/index.php/29th_ICP/issue/view/1881 SN - 978-88-8305-177-7 DO - https://doi.org/10.1285/i99788883051760 SP - 200 EP - 213 PB - Centro di Studi Papirologici dell’Università del Salento CY - Lecce AN - OPUS4-54756 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gleim, Tobias A1 - Neumann, Martin A1 - Linnemann, Konrad A1 - Wille, Frank T1 - Fracture Mechanical Analyses of a Welding Seam of a Thick-Walled Transport Package N2 - The safety demonstration of heavy weight type B transport packages used for storing spent nuclear fuel (SNF) or radioactive waste is ensured by a combination of physical testing and numerical calculations. While experiments are performed in accordance with the IAEA regulations for selected drop scenarios, Finite-Element-Method (FEM) simulations are used to predict the most damaging case and to investigate additional drop positions. BAM as competent authority in Germany has performed different investigations of a welding seam for a typical large transport package made of A508 forged steel, where the bottom plate is welded to the cylindrical shell. The package has a mass of approx. 120 t. Results of physical drop tests with a full-scale model and accompanying preliminary FEM simulations are presented to determine the decisive stresses in the welding seam. A drop test only represents one set of a package and test parameters. A further parameter analysis is considered to account for allowable variations of packaging properties (e.g. resulting from the manufacturing process) and, based on IAEA requirements, the temperature dependence of the material behaviour. The results of the stress analyses from the drop test and the simulation form the basis and provide the input parameters for a fracture mechanics analysis. In addition to the IAEA specifications, further standards are taken into account for an in-depth investigation, see R6, BS 7910 and API 579-1/ASME FFS1. All the above-mentioned standards require a manufacturer-specific defect analysis with respect to size and position. Both result from the welding process and the following heat treatment regime. The maximum defect sizes are ensured with non-destructive test methods (such as ultrasonic or particle methods) as integral part of the manufacturing process of the welding seam. Another important parameter in the welding process is the residual stress (secondary stress). The combination of the primary and secondary stress determines the total stress in the welding seam. The most damaging case of the welding seam is determined and evaluated with help of the above-mentioned standards and taking into account the IAEA requirements with respect to defect sizes, material properties, primary and residual stress, yield strength etc. T2 - PATRAM 22 - The International Symposium on the Packaging and Transportation of Radioactive Materials CY - Juan-Les-Pins, Antibes, France DA - 11.06.2023 KW - Transport Package KW - Welding KW - Fracture Mechanics PY - 2023 SP - 1 EP - 10 AN - OPUS4-57696 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scharf-Wildenhain, R. A1 - Hälsig, A. A1 - Hensel, J. A1 - Wandtke, Karsten A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas T1 - Korrelation von Wärmeführung, Nahtgeometrie, Bauteildesign und Eigenspannungen bei DED-Arc mit hochfesten Zusatzwerkstoffen N2 - Hochfeste Feinkornbaustähle verfügen über großes Potenzial für gewichtsoptimierte, effiziente Strukturen in vielen modernen Stahlkonstruktion. Weitere Effizienzsteigerungen können durch additives Fertigen sowie bionische Bauweisen erreicht werden. Hochfeste Zusatzwerkstoffe für formgebendes MSG-Schweißen (engl.: Wire Arc Additive Manufacturing, WAAM) sind bereits von den Schweißzusatzherstellern lieferbar. Eine breite industrielle Anwendung insbesondere für KMU ist aufgrund fehlender quantitativer Erkenntnisse und Richtlinien bezüglich schweißbedingter Beanspruchungen und Bauteilsicherheit während der Herstellung und des Betriebs derzeit stark limitiert. In einem gemeinsamen Forschungsprojekt (FOSTA-P1380/IGF21162BG) der BAM und der TU Chemnitz werden daher die mit Eigenspannungsausbildung und der Gefahr einer Kaltrissbildung verbundenen prozess- und werkstoffbedingten sowie konstruktiven Einflüsse beim WAAM hochfester Stähle untersucht. Der vorliegende Beitrag fokussiert die Analyse der Auswirkungen von Schweißwärmeführung und Design der WAAM-Bauteile auf Nahtgeometrie, Materialausnutzung und Eigenspannungen. Hierfür werden geometrisch definierte Probenkörper (Hohlquader) vollautomatisiert mit einem speziellen, hochfesten WAAM-Massivdraht (Streckgrenze >790 MPa) geschweißt. Die Wärmeführung wird innerhalb eines statistischen Versuchsplans so variiert, dass die Dt8/5-Abkühlzeiten im empfohlenen Verarbeitungsbereich (ca. 5 s bis 20 s) liegen. Das WAAM-Schweißen komplexer Geometrien mit variierenden Schweißwärmeführungen und geometrischen Verhältnissen bzw. Wanddicken bedingt neben den Auswirkungen auf die Abkühlbedingungen, Abkühlzeiten und Gefüge deutliche Einflüsse auf die konstruktiven Steifigkeitsverhältnisse beim Schweißen. Es zeigen sich anhand der Schweißexperimente signifikante Auswirkungen durch Probenskalierung und Wärmeeinbringung auf die resultierenden lokalen Eigenspannungen. Die Folge können ungünstige Bauteileigenschaften und risskritische Zugeigenspannungen sein. T2 - 43. Assistentenseminar Füge- und Schweißtechnik 2022 CY - Chemnitz, Germany DA - 27.09.2022 KW - Additive Fertigung KW - Hochfester Stahl KW - Eigenspannungen PY - 2023 VL - 386 SP - 1 EP - 7 PB - DVS Media CY - Düsseldorf AN - OPUS4-59232 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Giese, Marcel A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas A1 - Gräbner, Maraike A1 - Treutler, Kai A1 - Wesling, Volker T1 - Legierungsmodifikation und Einsatz hybrider Fräsprozesse zur Optimierung der Zerspanungssituation Ni-basierter Verschleißschutzauftragschweißungen mit definierten Oberflächen N2 - Die Verringerung der CO2-Emissionen ist eng mit der Entwicklung hocheffizienter und wirtschaftlicher Komponenten aus Stahl in der Anlagen- und Verfahrenstechnik verknüpft. Um den hohen kombinier-ten korrosiven, tribologischen, thermischen und mechanischen Beanspruchungen stand zu halten, werden auf Anwendungsfall und Stahlwerkstoff abgestimmte Verschleißschutzschichten eingesetzt. Neben der zunehmenden Forderung konventionelle Kobalt- durch Nickellegierungen zu ersetzen, wächst auch der Bedarf nach definierten Ober- bzw. Funktionsflächen hoher Güte. Aufgrund hohen Werkzeugverschleißes ist die erforderliche Fräsbearbeitung zu Herstellung der komplexen Geomet-rien der Bauteile für KMU oftmals wirtschaftlich nicht möglich. Mittels Legierungsmodifikation der Schweißzusätze für nickelbasierte plasmaauftraggeschweißte Verschleißschutzschichten und durch den Einsatz innovativer ultraschallunterstützter Fräsprozesse soll eine günstigere Zerspanbarkeit er-reicht werden, ohne das Verschleißschutzpotential zu mindern. Im vorliegenden Beitrag wird der Ein-fluss der mittels Legierungsmodifikation eingestellten Gefüge- und Ausscheidungsmorphologie auf die Zerspanbarkeit untersucht. Dies erfolgt anhand einer typischerweise für Schneckenmaschinen einge-setzten Verschleißschutzlegierung NiCrMoSiFeB-Legierung („Colmonoy 56 PTA“), die konventionelle CoCr-Legierungen (Stellite) substituiert. Metallurgische Untersuchungen und In-situ-Messungen auf-tretender Prozesskräfte an der Werkzeugschneide beim Fräsen sowie anschließende Untersuchungen von Werkzeugverschleiß und Oberflächenintegrität ermöglichen eine detaillierte Analyse und Korrela-tion zwischen mikrostrukturellen Eigenschaften und Zerspanbarkeit. T2 - DVS Congress 2023 CY - Essen, Germany DA - 11.09.2023 KW - Werkzeugverschleiß KW - Oberflächenintegrität KW - Ultraschallunterstütztes Fräsen KW - Zerspankräfte PY - 2023 SP - 742 EP - 747 AN - OPUS4-59210 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Giese, Marcel A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas A1 - Müller, Thomas A1 - Treutler, Kai A1 - Wesling, Volker T1 - Legierungsmodifikation und Einsatz hybrider Fräsprozesse zur Optimierung der Zerspanungssituation Ni-basierter Verschleißschutzauftragschweißungen mit definierten Oberflächen N2 - Die Bestrebungen zur Verringerung der CO2-Emissionen erfordern hochbelastbare und effiziente Komponenten aus Stahl in der Anlagen-, Verfahrens- und Kraftwerkstechnik. Hierfür sind in zunehmendem Maße auf den Anwendungsfall und Stahlwerkstoff abgestimmte Verschleißschutzschich-ten und definierte, zerspante Oberflächen notwendig. Die hohen Härten dieser Schichten und der Einsatz konventioneller Co-basierter Verschleißwerkstoffe führen oftmals zu unwirtschaftlichen Bauteilen, gerade aufgrund hohen Werkzeugverschleißes bei der Zerspanung mit geometrisch bestimmter Schneide. Er-kenntnisse über den Einsatz Ni-basierter Verschleißwerkstoffe und die Optimierung der Zerspanbarkeit mittels Legierungsmodifikationen und moderner hybrider Fräsprozesse ohne Verschlechterung der Ver-schleißschutzeigenschaften sind deshalb für die Anwender und Verarbeiter zur wirtschaftlichen Fertigung hochbelasteter Stahlbauteile wesentlich. Der vorliegende Beitrag stellt die Untersuchungsmethodik eines aktuell laufenden Vorhabens der TU Clausthal und BAM, Berlin, vor. Fokus liegt hierbei auf den hochin-strumentierten Fräsexperimenten, die eine reproduzierbare Analyse und Korrelation zwischen den mik-rostrukturellen Eigenschaften der auftraggeschweißten Legierungen, dem Zerspanprozess und der Zer-spanbarkeit, insbesondere der resultierenden Oberflächenintegrität, ermöglichen sollen. T2 - Tagung Werkstoffprüfung 2022 CY - Dresden, Germany DA - 27.10.2022 KW - Werkzeugverschleiß KW - Oberflächenintegrität KW - Ultraschallunterstütztes Fräsen KW - Zerspankräfte PY - 2022 SP - 368 EP - 374 AN - OPUS4-59211 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Martin A1 - Feldkamp, Martin A1 - Linnemann, Konrad A1 - Wille, Frank T1 - Transport of HLW canisters on sea vessels N2 - Germany had been transporting spent fuel to the reprocessing plant in Sellafield and La Hague for decades until around 2005. Resulting from the obligation to take back the vitrified high-level waste from reprocessing six CASTOR® HAW28M filled with 168 canisters with radioactive waste in vitrified form were transported from Sellafield to the interim storage facility Biblis in 2020. Rail wagons were used for the transport to the port in Barrow-in-Furness, where they were loaded into a dedicated seagoing vessel, certified as INF Class 3 according to the INF Code. This was the first time that vitrified high level waste with considerable heat load was transported under a German design approval certificate. BAM was involved in the authority assessment of the conditions for the sea transport. For the first transport BAM required among others, assessment of temperature distribution during transport, logging of temperatures of cargo bays and graphical imaging of temperatures of the bay with the cask in order to ensure compliance with temperature specifications, e.g. maximal neutron absorber and gasket temperatures. Special interest was taken in the identification of possible events exceeding the specified temperatures considering the different philosophies of IMDG code and its supplement INF code regarding temperature control of hatches. Results show compliance with assumed conditions. T2 - RAMTrans 2024 CY - London, United Kingdom DA - 14.05.2024 KW - Transport KW - Spent nuclear fuel KW - Ship KW - Sea KW - High level waste PY - 2024 SP - 1 EP - 8 AN - OPUS4-60092 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Ralf A1 - Gaber, Martin A1 - Gottschling, Peter T1 - Volatile concentration and diffusivity determined by vacuum hot extraction T2 - XX. International Congress on Glass CY - Kyoto, Japan DA - 2004-09-26 KW - Silicate glass KW - Water KW - Hydrogen KW - Degassing KW - Diffusion coefficient PY - 2004 SP - 6 pages PB - Ceramic Society of Japan CY - Tokio AN - OPUS4-6951 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gottschling, Peter A1 - Müller, Ralf A1 - Gaber, Martin T1 - Finite-Differenzen-Berechnung der Abgabe von Gasen aus Glaspulvern T2 - 78. Glastechnische Tagung CY - Nürnberg, Deutschland DA - 2004-06-07 KW - Finite Differenzen KW - Diffusion KW - Pulvermethode PY - 2004 SP - 25 EP - 29 PB - Deutsche Glastechnische Gesellschaft CY - Offenbach AN - OPUS4-6952 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Seeger, Stefan A1 - Müller, Werner T1 - Requirements and testing of protective layer systems for geomembranes T2 - 9th GRI Conference, Geosynthetics in Infrastructure - Enhancement and Remediation CY - Philadelphia, PA, USA DA - 1995-12-12 PY - 1995 SP - 175 EP - 184 CY - Philadelphia AN - OPUS4-7578 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Werner ED - Jost, D. T1 - Eignungsgutachten für Kunststoff-Dränelemente durch die BAM KW - Kunststoff-Dränelemente KW - Eignungsgutachten KW - Deponieoberflächenabdichtung PY - 2005 SP - 213 EP - 232 PB - SKZ CY - Würzburg AN - OPUS4-11159 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Werner ED - Herrmann, R. T1 - Eignungsnachweise bei Geokunststoffen für Dämme, Deiche und Stauanlagen T2 - 2. Symposium Sicherung von Dämmen, Deichen und Stauanlagen CY - Siegen, Deutschland DA - 2006-02-09 KW - Geokunststoffe KW - Wasserbau KW - Deiche PY - 2006 VL - 2 SP - 435 EP - 440 PB - IfG CY - Siegen AN - OPUS4-14445 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krebber, Katerina A1 - Lenke, Philipp A1 - Liehr, Sascha A1 - Witt, Jens A1 - Schukar, Marcus A1 - Large, M. A1 - Thiel, T. T1 - Technology and Applications of Smart Technical Textiles Based on POF T2 - 17th International Conference on Plastic Optical Fibers (POF 2008), August 25-28, 2008 CY - Santa Clara, California, USA DA - 2008-08-25 KW - Fiber optic sensors KW - Polymer optical fibers (POF) KW - POF sensors KW - Smart technical textiles PY - 2008 SP - 1 EP - 10 AN - OPUS4-17870 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hsuan, Y.G. A1 - Schröder, Hartmut A1 - Rowe, K. A1 - Müller, Werner A1 - Greenwood, J. A1 - Cazzuffi, D. A1 - Koerner, R.M. ED - Neil Dixon, T1 - Long-term performance and lifetime prediction of geosynthetics N2 - To properly understand and assess the long-term behaviour of geosynthetic materials it is necessary to investigate the various types of possible degradation mechanims. This includes both chemical and mechanical behaviour, and sometimes even their interactions with one another. Clearly, chemical degradation of geosynthetics depends on the polymer type. For example, polyolefins are vulnerable to oxidation; polyesters are susceptible to hydrolysis; and plasticizers can leach from polyvinyl chloride. This paper describes the concept of these three types of degradation, but focuses on the oxidation of polyolefins since the majority of the geosynthetics is made from this type of polymer. The methods used to predict the lifetime of antioxidants and service life of the geosynthetic material will be illustrated. Furthermore, the influence of temperature, pressure, and ultraviolet light on the service life are also demonstrated. Finally, the current specifications targeting the longevity of different geosynthetics are presented. Regarding mechanical degradation, the paper mainly focuses upon the creep deformation of geogrids and stress crack resistance (SCR) of polyethylene geomembranes and geopipe. The method to assess stress crack resistance is described, and the microscopic mechanisms that lead to such failure are explained. For creep evaluation, different acceleration tests are presented and their applicability with respect to the different types of polymers is illustrated. In addition, the long-term shear behaviour of geocomposites and geosynthetic clay liners is presented. T2 - 4th European Geosynthetics Conference - EuroGeo4 CY - Edinburgh, Scotland, UK DA - 2008-09-07 KW - Geosynthetic KW - Durability KW - Degradation KW - Antioxidant KW - Weathering PY - 2008 SP - 1 EP - 41 AN - OPUS4-17975 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Werner T1 - Dichtungsbahnen zur Abdichtung von Deponien und Altlasten T2 - 25. Fachtagung - Die sichere Deponie - Sicherung von Deponien und Altlasten mit Kunststoffen CY - Würzburg, Deutschland DA - 2009-02-26 KW - Kunststoffdichtungsbahnen KW - Deponien KW - Altlasten PY - 2009 IS - Abschnitt C SP - 1 EP - 22 CY - Würzburg AN - OPUS4-19064 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Steffen, Milan A1 - Schukar, Marcus A1 - Witt, Jens A1 - Krebber, Katerina A1 - Large, M. A1 - Argyros, A. T1 - Investigation of MPOF-LPGs for sensing applications N2 - The versatility of MPOF offers a variety of sensing applications. In this paper the influence of strain, temperature and humidity is investigated. The results show that MPOF LPGs are well suited for strain sensing. Further investigations have to be made to clarify the behaviour on temperature and humidity in more detail. T2 - POF 2009 - 18th International conference on plastic optical fibers CY - Sydney, Australia DA - 2009-09-07 KW - Mikrostrukturierte Polymerfasern (MPOF) KW - Langperiodische Gitter (LPG) KW - Faseroptische Sensorik KW - Dehnungssensor KW - Klimatische Effekte PY - 2009 IS - Session 1 (S1_25) SP - 1 EP - 4 CY - Sydney, Australia AN - OPUS4-19887 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Witt, Jens A1 - Schukar, Marcus A1 - Krebber, Katerina A1 - Jonckheere, J. de A1 - Paquet, B. A1 - Depré, A. T1 - Respiratory sensor based on POF OTDR N2 - We report on the characterization and test of a respiratory sensor based on POF OTDR, developed for monitoring of patients during MRI examination. The sensor is based on an optical fibre integrated into an elastic belt using a macrobending layout. T2 - POF 2009 - 18th International conference on plastic optical fibers CY - Sydney, Australia DA - 2009-09-07 KW - Faseroptischer Sensor KW - Medizinische Textilien KW - Intelligente Textilien KW - Atmungssensor KW - OTDR KW - POF PY - 2009 IS - Session 6 ( S6_74) SP - 1 EP - 4 CY - Sydney, Australia AN - OPUS4-19889 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schukar, Marcus A1 - Krebber, Katerina A1 - Large, M. A1 - Lwin, R. T1 - Climatic investigations of microstructured polymer optical fibers N2 - The behaviour of optical transmission of microstructured polymer optical fibers (MPOFs) by varying temperature and humidity was investigated whereas different MPOFs with varying hole structures and manufacturing procedures were used. T2 - POF 2009 - 18th International conference on plastic optical fibers CY - Sydney, Australia DA - 2009-09-07 KW - Mikrostrukturierte Polymerfasern (MPOF) KW - Klimatische Effekte KW - Faseroptische Sensorik KW - Langperiodische Gitter (LPG) PY - 2009 IS - Session 1 (S1_25) SP - 1 EP - 4 CY - Sydney, Australia AN - OPUS4-19916 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krebber, Katerina A1 - Lenke, Philipp A1 - Liehr, Sascha A1 - Nöther, Nils A1 - Schukar, Marcus A1 - Wendt, Mario A1 - Witt, Jens A1 - Wosniok, Aleksander T1 - Technology and applications of smart technical textiles based on fibre optic sensors N2 - Technical textiles with embedded fibre optic sensors habe been developed for the purposes of the structural health monitoring in geotechnical and civil engineering as well as for healthcare monitoring in the medical sector. The paper shows selected examples of using such sensor-based smart textiles for different applications. T2 - International conference "Optical sensors" CY - Karlsruhe, Germany DA - 2010-06-21 PY - 2010 IS - STuC2.pdf SP - 1 EP - 2(?) AN - OPUS4-21567 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalbe, Ute A1 - Berger, Wolfgang A1 - Eckardt, Jürgen A1 - Müller, Werner ED - Srodo´n, J. T1 - Transport of concentrated organic compounds within base liner systems T2 - 9th Conference of the European Clay Groups Association (Euroclay) CY - Krakow, Poland DA - 1999-09-04 KW - Composite liner KW - Organic contaminants KW - Contaminant transport PY - 1999 SP - 97 CY - Kraków AN - OPUS4-1344 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gaber, Martin A1 - Müller, Ralf A1 - Brzezinka, Klaus-Werner A1 - Peuker, Christel A1 - Langer, A. T1 - Analyse von Wasserstoff in Quarzglas T2 - 76. Glastechnische Tagung CY - Bad Soden, Deutschland DA - 2002-05-27 PY - 2002 SP - 242 EP - 245 PB - DGG, Deutsche Glastechnische Gesellschaft e.V. CY - Frankfurt/M. AN - OPUS4-1636 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Werner A1 - Seeger, Stefan A1 - Thies, Martina ED - Knipschild, F. W. T1 - Langzeit-Scherfestigkeit von Geokunststoffen aus mehreren Komponenten T2 - 19. Fachtagung "Die Sichere Deponie" CY - Würzburg, Deutschland DA - 2003-02-13 PY - 2003 IS - 19 SP - L1 EP - L14 PB - SKZ CY - Würzburg AN - OPUS4-2806 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalbe, Ute A1 - Berger, Wolfgang A1 - Müller, Werner ED - Christensen, T. T1 - Long term behaviour of composite liners under exposure to a mixture of concentrated hydrocarbons T2 - 7th International Waste Management and Landfill Symposium ; Sardinia 99 CY - S. Margherita di Pula, Cagliari, Italy DA - 1999-10-04 KW - Landfill KW - Composite liner KW - Organic contaminants KW - Contaminant transport PY - 1999 VL - 3 SP - 165 EP - 172 PB - CISA, Environmental Sanitary Engineering Centre CY - Cagliari AN - OPUS4-1343 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Werner T1 - Prüfung und Bemessung von Kunststoff-Dränmatten T2 - 18. Fachtagung "Die Sichere Deponie" CY - Würzburg, Deutschland DA - 2002-02-14 PY - 2002 UR - http://www.deponie-stief.de/pdf/fachlit_pdf/2002skz_mueller.pdf IS - 18 SP - F1 EP - F13 PB - SKZ CY - Würzburg AN - OPUS4-1301 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Altantsog, Pagvajav A1 - Ojunbileg, L. A1 - Tserenshimed, M. A1 - Chadraabal, Shgdariin A1 - Müller, Ralf A1 - Nofz, Marianne A1 - Gaber, Martin A1 - Batdemberel, G. A1 - Sangaa, D. T1 - Some experimental results of glass melting by using sands from Buir nuur PY - 2002 VL - 1 SP - 103 EP - 118 AN - OPUS4-3113 LA - mon AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Chadraabal, Shgdariin A1 - Gaber, Martin A1 - Müller, Ralf A1 - Altantsog, Pagvajav A1 - Tserenshimed, M. A1 - Ojunbileg, L. T1 - Degassing features of quartz crystals from the Mongolian pegmatite deposite Gorkhi PY - 2001 VL - 28 SP - 76 EP - 83 AN - OPUS4-3114 LA - mon AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eberstein, Markus A1 - Müller, Ralf A1 - Reinsch, Stefan A1 - Rabe, Torsten A1 - Schiller, Wolfgang Arno A1 - Thiel, A. A1 - Deubener, J. T1 - Kinetic Modeling of LTCC-Shrinkage T2 - 3rd International Conference and Exhibition on Ceramic Interconnect and Ceramic Microsystems Technologies (CICMT 2007) CY - Denver, CO, USA DA - 2007-04-23 KW - LTCC KW - Glass matrix composites KW - Inclusions KW - Sintering kinetics KW - Modeling PY - 2007 SP - 1 EP - 8 PB - American Ceramic Soc. CY - Denver AN - OPUS4-14948 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krebber, Katerina A1 - Grillet, A. A1 - Witt, Jens A1 - Schukar, Marcus A1 - Kinet, D. A1 - Thiel, T. A1 - Pirotte, F. A1 - Depré, A. T1 - Optical fibre sensors embedded into technical textile for healthcare (ofseth) T2 - 16th International Conference on Plastic Optical Fibers (POF 2007) CY - Turin, Italy DA - 2007-09-10 PY - 2007 SP - 227 EP - 233 PB - International Cooperative of Plastic Optical Fibers (ICPOF) CY - Turin, Italy AN - OPUS4-15824 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Werner T1 - Langzeit-Scherfestigkeit von Bentonitmatten und Kunststoff-Dränelementen T2 - 4. Geokunststoff-Kolloquium CY - Garmisch-Partenkirchen, Deutschland DA - 2005-01-27 KW - Geokunststoffe KW - Scherfestigkeit KW - Lebensdauer PY - 2005 SP - 1 EP - 22 CY - Espelkamp-Fiestel AN - OPUS4-15940 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Werner T1 - Kunststofftechnische Fremdprüfung beim Bau von Abdichtungen für Deponien und Altlasten KW - Deponietechnik KW - Fremdprüfung KW - Geokunststoffe PY - 2008 IS - Abschnitt C SP - 1 EP - 18 CY - Würzburg AN - OPUS4-16716 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geißler, Heinz A1 - Peuker, Christel A1 - Müller, Ralf T1 - Zuordnung von Hydroxylgruppen- und Wasserbanden in den Schwingungsspektren wasserarmer Silicatgläser T2 - 75. Glastechnische Tagung CY - Wernigerode, Deutschland DA - 2001-05-21 PY - 2001 PB - DGG, Deutsche Glastechnische Gesellschaft e.V. CY - Frankfurt/M. AN - OPUS4-1071 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - de Moraes, Flavia A1 - Frischat, G. H. A1 - Heide, G. A1 - Müller, Wolfgang A1 - Müller, Ralf T1 - Korrosions- und Kristallisationsphänomene an der Innenoberfläche von Glasbausteinen T2 - 77. Glastechnische Tagung CY - Leipzig, Deutschland DA - 2003-05-26 PY - 2003 VL - 77 SP - 71 EP - 74 PB - DGG CY - Offenbach AN - OPUS4-2527 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Werner T1 - Langzeit-Scherfestigkeit von Bentonitmatten und Kunststoff-Dränmatten T2 - Fachtagung "Deponietechnik 2003 - Abschluss und Sicherung von Deponien in Sachsen-Anhalt" CY - Halle (Saale), Deutschland DA - 2003-05-22 PY - 2003 SP - C1 EP - C12 AN - OPUS4-2524 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reinsch, Stefan A1 - Müller, Ralf T1 - Kristallwachstumsgeschwindigkeit und -mechanismen von mu-Cordierit zwischen 800 und 1350°C T2 - 77. Glastechnische Tagung CY - Leipzig, Deutschland DA - 2003-05-26 PY - 2003 VL - 77 SP - 1 EP - 4 PB - DGG CY - Offenbach AN - OPUS4-2526 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reinsch, Stefan A1 - Müller, Ralf A1 - Nascimento, M.L.F. A1 - Zanotto, E. D. T1 - Crystal Growth Mechanism in Cordierite and Diopside Glasses in Wide Temperature Ranges T2 - XX. International Congress on Glass CY - Kyoto, Japan DA - 2004-09-26 KW - Cordierite KW - Diopside KW - Glass KW - Crystal growth PY - 2004 SP - 6 pages PB - Ceramic Society of Japan CY - Tokio AN - OPUS4-4389 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Witt, Jens A1 - Schukar, Marcus A1 - Krebber, Katerina A1 - Demuth, J. A1 - Sasek, L. T1 - Heart rate sensor for integration into personal protective equipment N2 - This paper reports on a fibre optic sensor for heart rate measurement which is developed within the framework of the FP7 EU project i-Protect. Goal is integration of the sensor into personal protective equipment Two different sensor prototypes based on polymer optical fibre (POF) were developed. One is based on long period gratings in microstrutured POF and the other one is based on macrobending effects in POF. T2 - POF 2011 - 20th International conference on plastic optical fibers CY - Bilbao, Spain DA - 14.09.2011 KW - Heart rate sensor KW - Long period grating KW - Macrobending sensor KW - Microstructured POF (mPOF) KW - Personal protective equipment (PPE) KW - Physiological sensor PY - 2011 SP - 1 EP - 5 AN - OPUS4-24500 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schukar, Marcus A1 - Wischerhoff, E. A1 - Kalbitz, R. T1 - Novel fibre optic temperature sensors based on thermoresponsive polymers N2 - In this paper we present the development of a novel of a fibre optic temperature sensor based on thermoresponsive polymers. The principle of our invention that is already applied for a patent is based on the detection of the optical power that is transmitted through an optical fibre, whilst a temperature sensitive element is integrated in this fibre. T2 - POF 2015 - 24th International conference on plastic optical fibers CY - Nürnberg, Germany DA - 22.09.2015 KW - Optical fibre sensor KW - Temperature sensor KW - Thermoresponsive polymer KW - Optical power measurement PY - 2015 SP - 1 AN - OPUS4-33453 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Thoralf A1 - Burkert, Andreas A1 - Heyn, A. A1 - Balzer, Martin A1 - Fenker, M. T1 - Investigation on the improved corrosion behavior of TiMgN hard coating on steel substrate T2 - EUROCORR 2015 - European corrosion congress CY - Graz, Austria DA - 06.09.2015 KW - Hard coatings KW - TiMgN KW - Corrosion PY - 2015 SP - paper 11.1_693 AN - OPUS4-34618 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Karapanagiotis, Christos A1 - Heimann, Jan A1 - Duffner, Eric A1 - Charmi, Amir A1 - Schukar, Marcus A1 - Hashemi, Seyedreza A1 - Prager, Jens T1 - Towards predictive maintenance of hydrogen pressure vessels based on multi-sensor data fusion and digital twin modeling N2 - Hydrogen pressure vessels are among the most essential components for reliable hydrogen technology. Under current regulations, a mostly conservative strategy is employed, restricting the usage time of hydrogen pressure vessels without providing information on the real remaining lifetime. During the service life, pressure vessels are inspected periodically. However, no established method that can provide continuous monitoring or information on the remaining safe service life of the vessel. In this paper, we propose a sensor network for Structural Health Monitoring (SHM) of hydrogen pressure vessels where data from all sensors are collected and centrally evaluated. Specifically, we integrate three different SHM sensing technologies namely Guided Wave ultrasonics (GW), Acoustic Emission testing (AT), and distributed Fiber Optic Sensing (FOS). This integrated approach offers significantly more information and could therefore enable a transition from costly and time-consuming periodic inspections to more efficient and modern predictive maintenance strategies, including Artificial Intelligence (AI)-based evaluation. This does not only have a positive effect on the operational costs but enhances safety through early identification of critical conditions in the overall system in real-time. We demonstrate an experimental set-up of a lifetime test where a Type IV Composite Overwrapped Pressure Vessel (COPV) is investigated under cyclic loading instrumented with AT, FOS, and GW methods. We acquired data from the sensor network until the pressure vessel failed due to material degradation. The data collected using the three different SHM sensor technologies is planned to be evaluated individually, using data fusion, and AI. In the future, we aim to integrate the measurement setup into a hydrogen refueling station with the data stream implemented into a digital signal processing chain and a digital twin. T2 - 11th European Workshop on Structural Health Monitoring CY - Potsdam, Germany DA - 10.06.2024 KW - Acoustic emission KW - Ultrasonic guided waves KW - Fiber optic sensors KW - Hydrogen KW - Pressure vessels KW - Structural health monitoring KW - Machine learning PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-602764 UR - https://www.ndt.net/search/docs.php3?id=29702 SP - 1 EP - 8 PB - NDT.net AN - OPUS4-60276 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Karapanagiotis, Christos A1 - Schukar, Marcus A1 - Breithaupt, Mathias A1 - Duffner, Eric A1 - Ulbricht, Alexander A1 - Prager, Jens A1 - Krebber, Katerina T1 - Structural health monitoring of hydrogen pressure vessels using distributed fiber optic sensing N2 - We report on distributed fiber optic sensing-based monitoring of hydrogen composite overwrapped pressure vessels (COPV) to simultaneously increase the operational lifespan and mitigate maintenance costs. Our approach represents, to the best of our knowledge, the first application of distributed fiber optic sensing for COPV Type IV monitoring, where the sensing fibers are attached to the surface, rather than integrated into the composite material. Specifically, we attach an optical fiber of 50 m to the pressure vessel's surface, covering both the cylindrical and dome sections. We note that our fiber optic sensing technique relies on swept wavelength interferometry providing strain information along the entire length of the optical fiber with high spatial resolution even at the millimeter scale. When the vessel is pressurized, the sensing optical fiber shows a linear strain response to pressure at every position along the fiber. After thousands of load cycles, the vessel finally fails with the optical fiber detecting and precisely localizing the damage in the vessel’s blind dome area. Furthermore, we discuss the potential of state-of-the-art signal processing methods and machine learning for advancing predictive maintenance. This could reduce the number of regular inspections, mitigate premature maintenance costs, and simultaneously increase the vessel’s remaining safe service life. We believe that the structural health monitoring of hydrogen pressure vessels with fiber optic sensors can enhance trust in hydrogen technology contributing to the energy transition in the future. T2 - 11th European Workshop on Structural Health Monitoring CY - Potsdam, Germany DA - 10.06.2024 KW - Hydrogen KW - Fiber optic sensors KW - Composites KW - Machine learning KW - Structural health monitoring PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-602731 UR - https://www.ndt.net/search/docs.php3?id=29701 SP - 1 EP - 7 PB - NDT.net AN - OPUS4-60273 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Martin A1 - Gleim, Tobias A1 - Gradt, Thomas A1 - Wille, Frank T1 - Friction coefficients for wood-wood and wood-steel interfaces in impact limiters for transport casks N2 - Wood is widely used in impact limiters of transport casks for radioactive material. Encapsulated by an outer and inner steel structure, spruce wood is often applied in layers of alternating direction. The friction at the interfaces between these layers is of crucial importance for the impact and energy absorption e.g., at an accidental impact of a cask against a hard target. In order to get detailed information for corresponding numerical calculations, in this study the friction coefficient for the combinations wood-wood and wood-steel was measured in the temperature range between -40°C and 90°C according to the relevant stress conditions for such casks. Results show decreasing friction with increasing temperature, ranging from 0.43 at -40°C to 0.22 for 90°C for wood-steel combinations and from 0.3 at -40°C to 0.24 at 90°C to for a wood-wood combination. T2 - 20th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Juan-les-Pins, France DA - 11.06.2023 KW - Wood KW - Friction KW - Transport cask PY - 2023 SP - 1 EP - 11 AN - OPUS4-57334 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Otremba, Frank A1 - Romero Navarrete, J. A. T1 - Assesing rail damage in turns due to lateral load transfer N2 - A testing procedure is proposed and used, to estimate the rail damage potentials of variations in both, the height of the cargo´s center of gravity and the railway car suspension´s spring constant. The experimental setup consist ed of a tilt table that slowl y exer ted an increasing lateral acceleration on a two axle bog ie type vehicle equipped with a spring supported container. The potential damaging effect derived from the resulting lateral load transfer, was assessed on the basis of the fourth power law. Results suggest that the cargo having a higher center of gravity could be more damagi ng to the outside rail when compared with the effect of the shorter center of gravity of the cargo, in a range from 0.94% to 3.17%, as a function of the spring constant of the suspension. Consequently and comparatively there would be a long term damaging effect on the rail when having a cargo with a high er center of gravity, so that specific cargo, having a high center of would be more aggressive to the infrastructure On the other hand for the range of time rate changes of the lateral acceleration, it was not found a consisten t trend regarding the effect of the value of the spring constant on the magnitude of the load transfers . T2 - IMECE 2024 CY - Portland, Oregon, USA DA - 17.11.2024 KW - Railway damage KW - Load transfer KW - Fourth power law KW - Experimental methods KW - Center of gravity KW - Tilt table KW - Suspension spring constant PY - 2024 SN - 978-0-7918-8869-8 SP - 1 EP - 4 PB - ASME AN - OPUS4-61785 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Artinov, Antoni A1 - Meng, Xiangmeng A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Numerical study on the formation of a bulging region in partial penetration laser beam welding N2 - A transient three-dimensional thermo-fluid dynamics numerical model was developed to study the formation of a bulging region in partial penetration laser beam welding. The model accounts for the coupling between the fluid flow, the heat transfer, and the keyhole dynamics by considering the effects of multiple reflections and Fresnel absorption of the laser beam in the keyhole, the phase transitions during melting and evaporating, the thermo-capillary convection, the natural convection, and the phase-specific and temperature-dependent material properties up to the evaporation temperature. The validity of the model was backed up by experimentally obtained data, including the drilling time, the weld pool length, the local temperature history outside the weld pool, the process efficiency, and a range of metallographic crosssections. The model was applied for the cases of partial penetration laser beam welding of 8 mm and 12 mm thick unalloyed steel sheets. The obtained experimental and numerical results reveal that the bulging region forms transiently depending on the penetration depth of the weld, showing a tendency to transition from a slight bulging to a fully developed bulging region between penetration depths of 6 mm and 9 mm, respectively. T2 - 13th International Seminar "Numerical Analysis of Weldability" CY - Seggau, Austria DA - 04.09.2022 KW - Laser beam welding KW - Deep penetration KW - Bulge formation KW - Numerical modeling PY - 2023 SN - 978-3-85125-968-1 SN - 978-3-85125-969-8 SN - 2410-0544 VL - 13 SP - 101 EP - 126 PB - Verlag der Technischen Universität Graz AN - OPUS4-58802 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Artinov, Antoni A1 - Kising, Pascal A1 - Bachmann, Marcel A1 - Meng, Xiangmeng A1 - Rethmeier, Michael T1 - Numerical analysis of the dependency of the weld pool shape on turbulence and thermodynamic activity of solutes in laser beam welding of unalloyed steels N2 - A three-dimensional numerical model was developed to accurately predict the steady-state weld pool shape in full penetration laser beam welding. The model accounts for the coupling between the heat transfer and the fluid dynamics by considering the effects of solid/liquid phase transition, thermo-capillary convection, natural convection, and phase-specific and temperature-dependent material properties up to the evaporation temperature. A fixed right circular cone was utilized as a keyhole geometry to consider the heat absorbed from the laser beam. The model was used to analyze the influence of the thermodynamic activity of solutes and turbulence on the weld pool shape. A mesh sensitivity analysis was performed on a hybrid mesh combining hexahedral and tetrahedral elements. For the case of full penetration laser beam welding of 8 mm thick unalloyed steel sheets, the dependence of the weld pool shape on the surface-active element sulfur was found to be negligible. The analysis of the results showed that a laminar formulation is sufficient for accurately predicting the weld pool shape since the turbulence has a minor impact on the flow dynamics in the weld pool. The validity of the numerical results was backed up by experimental measurements and observations, including weld pool length, local temperature history, and a range of metallographic crosssections. T2 - 13th International Seminar Numerical Analysis of Weldability CY - Seggau, Austria DA - 04.09.2022 KW - Weld pool shape KW - Numerical modeling KW - Laser beam welding KW - Thermo-capillary convection KW - Turbulence PY - 2023 SN - 978-3-85125-968-1 SN - 978-3-85125-969-8 SN - 2410-0544 VL - 13 SP - 161 EP - 188 PB - Verlag der Technischen Universität Graz AN - OPUS4-58803 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Yang, Chunliang A1 - Wu, Chuansong A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Numerical analysis of ultrasonic vibration enhanced friction stir welding of dissimilar Al/Mg alloys N2 - The ultrasonic vibration enhanced friction stir welding (UVeFSW) process has unique advantages in joining dissimilar Al/Mg alloys. While there are complex coupling mechanisms of multi-fields in the process, it is of great significance to model this process, to reveal the influence mechanism of ultrasonic vibration on the formation of Al/Mg joints. In this study, the acoustic-plastic constitutive equation was established by considering the influence of both ultrasonic softening and residual hardening on the flow stress at different temperatures and strain rates. And the ultrasonic induced friction reduction (UiFR) effect on friction coefficient in different relative directions at the FSW tool-workpiece interface was quantitatively calculated and analyzed. The Al/Mg UVeFSW process model was developed through introducing the above acoustic effects into the model of Al/Mg friction stir welding (FSW). The ultrasonic energy is stronger on the aluminum alloy side. In the stirred zone, there is the pattern distribution of ultrasonic sound pressure and energy. The heat generation at the tool-workpiece contact interface and viscous dissipation were reduced after applying ultrasonic vibra-tion. Due to the UiFR effect, the projection of friction coefficient and heat flux distributions at the tool-workpiece interface present a "deformed" butterfly shape. The calculated results show that ultrasonic vibra-tion enhanced the material flow and promoted the mixing of dissimilar materials. T2 - 13th International Seminar Numerical Analysis of Weldability CY - Seggau, Austria DA - 04.09.2022 KW - Friction stir welding KW - Ultrasonic vibration KW - Al/Mg alloys KW - Numerical simulation PY - 2023 SN - 2410-0544 VL - 13 SP - 517 EP - 538 PB - Verlag der Technischen Universität Graz AN - OPUS4-58805 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meng, Xiangmeng A1 - Artinov, Antoni A1 - Bachmann, Marcel A1 - Üstündag, Ömer A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - A numerical study on the suppression of a detrimental weld pool profile in wire feed laser beam welding by magnetohydrodynamic technique N2 - The weld quality and the possible defect formation are directly determined by the weld pool shape and the thermo-fluid dynamics therein. In this paper, an untypical weld pool profile, i.e., elongated at its top and bottom but narrowed at the middle, is found experimentally and numerically in the wire feed laser beam welding. The detrimental influence of the weld pool narrowing on the element transport is analyzed and discussed. A magnetohydrodynamic technique is utilized to suppress the narrowing, aiming at a more homogenous element distribution. It is found that a low-temperature region is formed in the middle of the weld pool due to the interaction of the two dominant circulations from the top and bottom regions. The weld pool is significantly narrowed due to the untypical growth of the mushy zone in the low-temperature region, which results in a direct blocking effect on the downward flow and the premature solidification in the middle region. The Lorentz force produced by a transverse oscillating magnetic field shows the potential to change the flow pattern into a single-circulation type and the low-temperature-gradient region is mitigated. Therefore, the downward transfer channel is widened, and its premature solidification is prevented. The numerical results are well validated by experimental measurements of metal/glass observation and X-ray fluorescence element mapping. T2 - 13th International Seminar Numerical Analysis of Weldability CY - Seggau, Austria DA - 04.09.2022 KW - Thermo-fluid flow KW - Element transport KW - Laser beam welding KW - Magnetohydrodynamics KW - Multi - physical modeling PY - 2023 SN - 2410-0544 VL - 13 SP - 143 EP - 160 PB - Verlag der Technischen Universität Graz AN - OPUS4-58806 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Yang, Chunliang A1 - Yang, Fan A1 - Meng, Xiangmeng A1 - Putra, Stephen Nugraha A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Experimental and numerical study on grain refinement in electromagnetic assisted laser beam welding of 5754 al alloy N2 - Through experimental observation and auxiliary numerical simulation, this investigation studies the different types of grain refinement of 5754 aluminum alloy laser beam welding by applying a transverse oscillating magnetic field. Scanning electron microscope results have proved that the application of a magnetic field can reduce the average crystal branch width and increase its number. The interaction between the induced eddy current generated by the Seebeck effect and the applied external magnetic field produces a Lorentz force, which is important for the increase of the number of crystal branches. Based on the theory of dendrite fragmentation and the magnetic field-induced branches increment, the grain size reduction caused by the magnetic field is studied. Furthermore, the effects of the magnetic field are analyzed by combining a phase field method model and simulations of nucleation and grain growth. The grain distribution and average grain size after welding verifies the reliability of the model. In addition, the introduction of a magnetic field can increase the number of periodic three-dimensional solidification patterns. In the intersection of two periods of solidification patterns, the metal can be re-melted and then re-solidified, which prevents the grains that have been solidified and formed previously from further growth and generates some small cellular grains in the new fusion line. The magnetic field increases the building frequency of these solidification structures and thus promotes this kind of grain refinement. T2 - International Congress of Applications of Lasers & Electro-Optics 2023 CY - Chicago, USA DA - 16.10.2023 KW - Laser beam welding KW - Magnetic field KW - Crystal branch development KW - Grain refinement KW - Periodic solidification pattern PY - 2023 SP - 1 EP - 10 AN - OPUS4-58809 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Marquardt, R. A1 - Biegler, M. A1 - Rethmeier, Michael T1 - Funktional gradierte Materialien auf Basis von Stellite und Stahl im Laserpulver-Auftragschweißen N2 - Das Hinzufügen von Stellite auf Stahl ist eine typische Vorgehensweise um Bauteile gegen Verschleiß und Korrosion zu schützen. Der Sprung in den Materialeigenschaften kann jedoch zu Rissen und somit zum Versagen der Beschichtung führen. Um die Lebensdauer von Beschichtungen zu erhöhen wird daher ein gradierter Übergang mit verschiedenen Materialpaarungen untersucht. T2 - 13. Fachtagung Verschleiss- und Korrosionsschutz von Bauteilen durch Auftragschweißen CY - Haale (Saale), Germany DA - 22.06.2022 KW - FGM KW - DED KW - AM KW - Functionally Graded Materials KW - Additive Manufacturing KW - Directed Energy Deposition PY - 2022 SP - 66 EP - 73 AN - OPUS4-55504 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maack, Stefan A1 - Niederleithinger, Ernst T1 - Imaging of Ultrasonic Echo Measurements for Reconstruction of Technical Data of Bridges – Possibilities, Limitations and Outlook N2 - When reassessing existing concrete bridges, the challenge is often to obtain missing or incomplete information on the internal structure. In particular, the number and position of the existing reinforcement as well as the geometric dimensions of the components are of interest. Non-destructive testing methods, like radar or ultrasound, which work on the basis of the pulse-echo method, have been established for this purpose, as they only require access to the component from one side. The measurement data recorded on the structure require pre-processing to be able to reproduce the internal structure geometrically accurately. Besides different steps of data processing, the geometrical reconstruction of the measured data based on the Synthetic Aperture Focusing Technique (SAFT) is state of the art today. In this paper, the technical possibilities of the ultrasonic echo method are presented based on measurements in the laboratory and on a real bridge structure. The precision of the reconstruction and its limitations are shown. In addition to the state of the art SAFT technique, open questions and the latest research approaches, such as imaging by reverse time migration (RTM) including initial results are discussed. T2 - 13th German-Japanese Bridge Symposium CY - Osaka, Japan DA - 29.08.2023 KW - Bridge KW - Non destructive testing and evaluation KW - Concrete KW - Validation PY - 2023 SP - 1 EP - 8 AN - OPUS4-58327 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bachmann, Marcel A1 - Artinov, Antoni A1 - Meng, Xiangmeng A1 - Putra, Stephen Nugraha A1 - Rethmeier, Michael T1 - Challenges in dynamic heat source modeling in high-power laser beam welding N2 - The amount of absorbed energy in the keyhole as well as its spatial and temporal distribution is essential to model the laser beam welding process. The recoil pressure, which develops because of the evaporation process induced by the absorbed laser energy at the keyhole wall, is a key determining factor for the macroscopic flow of the molten metal in the weld pool during high-power laser beam welding. Consequently, a realistic implementation of the effect of the laser radiation on the weld metal is crucial to obtain reliable and accurate simulation results. In this paper, we discuss manyfold different improvements on the laser-material interaction, namely the ray-tracing method, in the numerical simulation of the laser beam welding process. The first improvement relates to locating the exact reflection points in the ray tracing method using a so-called cosine condition in the determination algorithm for the intersection of the reflected rays and the keyhole surface. A second correction refers to the numerical treatment of the Gaussian distribution of the laser beam, whose beam width is defined by a decay of the laser intensity by a factor of 1/e2 thus ignoring around 14 % of the total laser beam energy. In a third step, the changes in the laser radiation distribution in the vertical direction were adapted by using different approximations for the converging and the diverging regions of the laser beam thus mimicking the beam caustic. Finally, a virtual mesh refinement was adopted in the ray tracing routine. The obtained numerical results were validated with experimental measurements. T2 - International Congress of Applications of Lasers & Electro-Optics 2023 CY - Chicago, USA DA - 16.10.2023 KW - Laser beam welding KW - Laser energy distribution KW - Ray tracing KW - Numerical modeling PY - 2023 SP - 1 EP - 10 AN - OPUS4-58475 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Lisec, Jan T1 - CorMID - Correct Mass Isotopologue Distribution Vectors N2 - The investigation of metabolic fluxes and metabolite distributions within cells by means of tracer molecules is a valuable tool to unravel the complexity of biological systems. Technological advances in mass spectrometry (MS) technology such as atmospheric pressure chemical ionization (APCI) coupled with high resolution (HR), not only allows for highly sensitive analyses but also broadens the usefulness of tracer-based experiments, as interesting signals can be annotated de novo when not yet present in a compound library. However, several effects in the APCI ion source, i.e., fragmentation and rearrangement, lead to superimposed mass isotopologue distributions (MID) within the mass spectra, which need to be corrected during data evaluation as they will impair enrichment calculation otherwise. Here, we present and evaluate a novel software tool to automatically perform such corrections. We discuss the different effects, explain the implemented algorithm, and show its application on several experimental datasets. This adjustable tool is available as an R package from CRAN. KW - Mass Spectrometry KW - Software KW - R package KW - Mass Isotopomer Distribution KW - Flux Analysis PY - 2022 UR - https://github.com/cran/CorMID/ PB - GitHub CY - San Francisco, CA, USA AN - OPUS4-56442 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Shen, Z. A1 - Uno, H. A1 - Ono, N. A1 - Rurack, Knut A1 - Daub, J. T1 - Synthesis, electrochemical and spectroscopic studies on a new class of boron dipyrromethene based fluoroionophores PY - 2002 VL - 18 SP - 100 EP - 102 (Suppl. A) PB - Elsevier CY - Amsterdam AN - OPUS4-2082 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lisec, Jan A1 - Jaeger, C. A1 - Zaidi, Nousheen T1 - Cancer cell lipid class homeostasis is altered under nutrient-deprivation but stable under hypoxia N2 - Under oxygen/nutrient deprivation cancer cells modify the Balance between fatty acid (FA) synthesis and uptake, which alters the levels of individual triglyceride or phospholipid sub-species. These modifications may affect survival and drug-uptake in cancer cells. Here, we aimed to attain a more holistic overview of the lipidomic profiles of cancer cells under stress and assess the changes in Major lipid-classes. First, expressions of markers of FA synthesis/uptake in cancer cells were assessed and found to be differentially regulated under metabolic stress. Next, we performed a broad lipidomics assay, comprising 244 lipids from six major classes, which allowed us to investigate robust stress induced changes in median levels of different lipid classes -additionally stratified by fatty acid side chain saturation status. The lipidomic profiles of cancer cells were predominantly affected by nutrient-deprivation. Neutral lipid compositions were markedly modified under serum-deprivation and, strikingly, the cellular level of triglyceride subspecies decreased with increasing number of double bonds in their fatty acyl chains. In contrast, cancer cells maintained lipid class homeostasis under hypoxic stress. We conclude that although the levels of individual lipid moieties alter under hypoxia, the robust averages of broader lipid class remain unchanged. KW - Mass-Spectrometry KW - Tumor metabolism KW - Fatty acid metabolism KW - Lipidomic profile KW - Metabolic stress PY - 2018 DO - https://doi.org/10.1101/382457 SP - 1 EP - 25 PB - Cold Spring Harbor Laboratory CY - Cold Spring Harbor, NY AN - OPUS4-46814 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tjaden, B. A1 - Baum, K. A1 - Marquardt, V. A1 - Simon, M. A1 - Trajkovic-Arsic, M. A1 - Kouril, T. A1 - Siebers, B. A1 - Lisec, Jan A1 - Siveke, J. T. A1 - Schulte, J. H. A1 - Benary, U. A1 - Remke, M. A1 - Wolf, J. A1 - Schramm, A. T1 - MYCN-induced metabolic rewiring creates novel therapeutic vulnerabilities in neuroblastoma N2 - MYCN is a transcription factor that is aberrantly expressed in many tumor types and is often correlated with poor patient prognosis. Recently, several lines of evidence pointed to the fact that oncogenic activation of MYC family proteins is concomitant with reprogramming of tumor cells to cope with an enhanced need for metabolites during cell growth. These adaptions are driven by the ability of MYC proteins to act as transcriptional amplifiers in a tissue-of-origin specific manner. Here, we describe the effects of MYCN overexpression on metabolic reprogramming in neuroblastoma cells. Ectopic expression of MYCN induced a glycolytic switch that was concomitant with enhanced sensitivity towards 2-deoxyglucose, an inhibitor of glycolysis. Moreover, global metabolic profiling revealed extensive alterations in the cellular metabolome resulting from overexpression of MYCN. Limited supply with either of the two main carbon sources, glucose or glutamine, resulted in distinct shifts in steady-state metabolite levels and significant changes in glutathione metabolism. Interestingly, interference with glutamine-glutamate conversion preferentially blocked proliferation of MYCN overexpressing cells, when glutamine levels were reduced. Thus, our study uncovered MYCN induction and nutrient levels as important metabolic master switches in neuroblastoma cells and identified critical nodes that restrict tumor cell proliferation. KW - Mass-spectrometry KW - Tumor metabolism KW - MYCN PY - 2018 DO - https://doi.org/10.1101/423756 SP - 1 EP - 21 PB - Cold Spring Harbor Laboratory CY - Cold Spring Harbor, NY AN - OPUS4-46815 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rurack, Knut T1 - Towards simple and efficient molecular reporters by combining electron and/or charge transfer processes in fluorescent bifunctional dyes T2 - 57th Southwest Regional Meeting CY - San Antonio, TX, USA DA - 2001-10-17 KW - Donor-Acceptor-Systems KW - Heterocycles KW - Electron Transfer KW - Fluorescence KW - Chelates PY - 2001 VL - 57 SP - 1(?) EP - 2(?) AN - OPUS4-1183 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Richter, Silke A1 - Meckelburg, Angela A1 - Recknagel, Sebastian A1 - Matschat, Ralf A1 - Panne, Ulrich T1 - Determination of trace elements in iron ore, cast iron and steel using the 7500cs KW - Steel KW - Iron ore KW - Cast iron KW - ICP-MS PY - 2009 IS - 38 SP - 4 EP - 5 PB - Agilent Technologies CY - Santa Clara, CA, USA AN - OPUS4-19476 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rurack, Knut A1 - Martínez-Mánez, Ramon ED - Robert H. Crabtree, T1 - Functional supramolecular hybrid materials N2 - The combination of suitable nanoscopic inorganic supports with supramolecular concepts and bioconjugation strategies opens up exciting perspectives for the development of bioinorganic and organic–inorganic hybrid materials with improved functionalities. Many of the examples from the period 2004 to mid-2007 reviewed here bridge the gap between molecules, materials sciences, biochemistry, and nanotechnology. The synergistic use of these approaches has led to the advancement of various functions such as enhanced recognition, amplified signaling, the controlled assembly and disassembly of aggregates and 3-D architectures. Many of the implemented active functions can be carried out in a reversible and directed fashion on purpose by triggering with an external stimulus. These ideas bring tunability to properties of inorganic solids and new perspectives of application to biochemical and supramolecular concepts. Classic inorganic chemistries such as metal or semiconductor nanoparticles, silica or carbon materials, and coordination chemistry are thus elevated to another level of sophistication and contribute significantly to frontier research areas in directed transport and delivery, nanoelectronics and mechanics, chip technology, smart materials, memory devices, and bioanalytics. KW - Biochemie KW - Biomakromoleküle KW - DNA KW - Gold KW - Hybridmaterialien KW - Nanopartikel KW - Quantenpunkte KW - Selbstorganisation KW - Sensorik KW - Silica KW - Supramolekulare Chemie PY - 2009 DO - https://doi.org/10.1002/0470862106.ia400 SP - 1 EP - 23 PB - Wiley CY - Chichester AN - OPUS4-19847 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - BOOK A1 - Rurack, Knut A1 - Martínez-Mánez, Ramon T1 - Biomimetic chemistry of hybrid materials N2 - The article discusses representative examples published in the field of functional biomimetic chemistry of hybrid materials between 2004 and mid-2007. First, we focus on the modification of morphological aspects of (bio)organic–inorganic hybrid materials to create sophisticated gating and switching mechanisms. The architecture of the systems is presented and the elements of control by external stimuli that have been established in recent years, such as optical, electrochemical, chemical, thermal, or magnetic means, are described. Various functions ranging from (site-specific) delivery to indication at the nanometric level are reported. Next we develop the idea of utilizing hybrid frameworks for biomimetic signaling inspired by the way nature has created binding pockets and the concept of induced-fit. Such a merging of inorganic scaffolds with supramolecular concepts results in enhanced molecular recognition and signaling. Finally selected recent advances in the field of hybrid biomimetic motors both of linear and rotary types are presented. The contribution shows how novel biomimetic functions can arise from synergisms between specifically designed hybrid materials and the implementation of supramolecular and/or bioorganic concepts. KW - Biochemie KW - Biomimetika KW - DNA KW - Gold KW - Hybridmaterialien KW - Molekulare Schalter KW - Molekulare Motoren KW - Nanopartikel KW - Quantenpunkte KW - Schalter KW - Sensorik KW - Silica KW - Supramolekulare Chemie PY - 2009 DO - https://doi.org/10.1002/0470862106.ia420 SP - 1 EP - 20 PB - Wiley CY - Chichester AN - OPUS4-19846 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Sommerfeld, Thomas A1 - Koch, Matthias A1 - Mauch, Tatjana A1 - Jung, Christian A1 - Riedel, Juliane A1 - Lisec, Jan T1 - CRM BAM-A001 eCerto data file N2 - Data file (RData) containing measurement data recorded during the production process of the Certified Reference Material BAM-A001 containing Polycyclic Aromatic Hydrocarbons (PAH) in olive oil. The data can be most conveniently openend using the Shiny-App eCerto which is accessible at https://www.bam.de/eCerto. KW - Certified reference material KW - Mass spectrometry KW - Olive oil KW - Aromatic hydrocarbons KW - Reference data PY - 2023 UR - https://doi.org/10.5281/zenodo.8380870 DO - https://doi.org/10.5281/zenodo.8380869 PB - Zenodo CY - Geneva AN - OPUS4-58488 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Resch-Genger, Ute A1 - Rurack, Knut A1 - Bricks, J. A1 - Koval'chuk, A. A1 - Slominskii, J. T1 - Synthesis and Photophysical Properties of Cation-sensitive styryl bases derived from substituted Benzothiazole T2 - 1st All-Russian Conference on Heterocyclic Chemistry CY - Suzdal, Russia DA - 2000-09-19 PY - 2000 SP - 1 AN - OPUS4-858 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Biyikal, Mustafa A1 - Rurack, Knut T1 - Development of a Lab-on-a-Chip for the Detection of Nerve Agents with a Handheld Device N2 - The development of a Lab-on-a-Chip (LoC) is presented, which can detect reactive phosphorous compounds in the gas phase in combination with an optochemical hand-held sensor. The LoC prototype contains three pairs of sensing materials containing fluorescent indicator dyes in various carrier materials. By measuring the fluorescence response to phosphoryl chloride, a surrogate compound, the detection of chemical warfare agents (CWAs) in gas phase becomes possible within seconds, introducing a novel approach to CWA detection. T2 - 2023 IEEE SENSORS Conference CY - Vienna, Austria DA - 29.10.2023 KW - Lab-on-a-Chip KW - Nerve agents KW - Hand-held KW - Fluorescence KW - Toxic industrial chemicals PY - 2023 UR - https://ieeexplore.ieee.org/document/10325263 SN - 979-8-3503-0387-2 DO - https://doi.org/10.1109/SENSORS56945.2023.10325263 SP - 1 EP - 4 PB - IEEE CY - New York AN - OPUS4-59367 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Matschat, Ralf A1 - Kipphardt, Heinrich A1 - Czerwensky, Michael A1 - Richter, Silke A1 - Heinrich, Hans-Joachim ED - Abiko, K. ED - Takaki, S. T1 - The System of Primary Pure Metals Established at BAM - Recent Developments T2 - 9th international conference on ultrahigh-purity base metals CY - Sendai, Japan DA - 2002-10-14 PY - 2002 SP - 119 CY - Sendai AN - OPUS4-1601 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rethmeier, Michael A1 - Gook, Sergej A1 - Biegler, Max A1 - Gumenyuk, Andrey T1 - Anwendung einer Kombination aus Laserhybrid- und Unterpulverschweißen zum Fügen dicker Bleche aus Schiffbaustahl EH36 N2 - In diesem Beitrag wird ein Schweißverfahren vorgestellt, mit dem 30 mm dicke Bleche aus Schiffbaustahl EH36 effizient und werkstoffgerecht gefügt werden können. Die wirtschaftlichen Vorteile des Verfahrens ergeben sich aus dem Wegfall der aufwendigen Kantenvorbereitung und der Reduzierung des Schweißzusatzbedarfs. Die Stumpfschweißnähte werden in einer Lagen-/Gegenlage-Technik durch Laserhybridschweißen und Unterpulverschweißen ausgeführt. Dabei erfolgt die Laserhybridschweißung als Einschweißung mit einer Tiefe von etwa 25 mm, während die Unterpulvernaht als zweiter Durchgang auf der gegenüberliegenden Seite des Bauteils mit einer Einschweißtiefe von 8 mm aufgebracht wird. Die Überlappung der beiden Lagen gewährleistet einen geschlossenen Nahtquerschnitt. Dank der partiellen Durchschweißung der Laserhybridnaht entfällt die Notwendigkeit zur Wurzelformierung. Darüber hinaus bietet die Prozesskombination eine höhere Toleranz gegenüber Ungenauigkeiten in der Kantenvorbereitung, was die Prozesskomplexität reduziert. Der Einsatz dieses robusteren Verfahrens, das weniger von einer präzisen Kantenvorbereitung abhängig ist, erleichtert die Produktionsvorbereitung, minimiert die Fehleranfälligkeit und senkt die Nachbearbeitungskosten. Dies macht das Laserhybridschweißen besonders attraktiv für Anwendungen im Schiffbau. T2 - 22. Tagung Schweißen in der maritimen Technik und im Ingenieurbau CY - Hamburg, Germany DA - 13.05.2025 KW - Laserhybridschweißen KW - Unterpulverschweißen KW - Kerbschlagbiegeversuch PY - 2025 SP - 87 EP - 98 PB - DVS – Deutsche Verband für Schweißen und verwandte Verfahren e. V AN - OPUS4-63342 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Unger, Brita A1 - Rurack, Knut A1 - Müller, Ralf A1 - Jancke, Harald T1 - Untersuchungen zur Alterung von Kieselsolen und -gelen T2 - 11. Arbeitstagung des AK Nichtkristalline und Partiellkristalline Strukturen CY - Wolfersdorf, Deutschland DA - 2003-09-08 PY - 2003 UR - http://www2.uni-jena.de/chemie/DGK-AK4/VOR_03/Unger.pdf SP - 1(?) EP - 10(?) AN - OPUS4-3119 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Agudo Jácome, Leonardo A1 - Manzoni, Anna Maria T1 - Elementverteilung in Hochentropiewürfelchen N2 - Seit Beginn der Luftfahrt Anfang des letzten Jahrhunderts ist die Menschheit auf der Suche nach neuen Materialien, die das Abenteuer Fliegen sicherer, angenehmer, schneller und rentabler gestalten. Hochentropielegierungen sind solche vielversprechenden Materialien. Die richtige Analytik hilft dabei, besser zu verstehen, wie deren Zusammensetzung und atomare Anordnung die makroskopischen Eigenschaften beeinflusst. KW - Chemically complex alloy KW - Transmissionselektronenmikroskopie KW - Energiedisersive Röntgenspektroskopie PY - 2022 UR - https://www.gdch.de/fileadmin/downloads/Netzwerk_und_Strukturen/Fachgruppen/Analytische_Chemie/Mitteilungsblatt/Internet_AC04-2022.pdf SN - 0939-0065 IS - 4 SP - 12 EP - 14 PB - Gesellschaft Deutscher Chemiker CY - Frankfurt, Main AN - OPUS4-56699 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Resch-Genger, Ute A1 - Behnke, Thomas A1 - Brehm, Robert A1 - Grabolle, Markus A1 - Hennig, Andreas A1 - Hoffmann, Angelika A1 - Hoffmann, Katrin A1 - Linck, Lena A1 - Lochmann, Cornelia A1 - Pauli, Jutta A1 - Spieles, Monika A1 - Würth, Christian T1 - Funktionelle Chromophor-Systeme, innovative Validierungskonzepte und rückführbare Standards für die fluoreszenzbasierte multiparametrische Bioanalytik N2 - Unter dem Motto „Innovation und Qualitätssicherung in der (Bio)Analytik“ werden in der Arbeitsgruppe Fluoreszenzspektroskopie der BAM, Bundesanstalt für Materialforschung und -prüfung, funktionelle Chromophor-Systeme, einfache Signalverstärkungs- und Multiplexingstrategien sowie innovative Validierungs- und rückführbare Standardisierungskonzepte für verschiedene fluorometrische Messgrößen und Methoden entwickelt. Im Mittelpunkt stehen dabei molekulare Fluorophore, Nanokristalle mit größenabhängigen optischen Eigenschaften (sogenannte Quantenpunkte, QDs) und fluoreszierende Partikel variabler Größe sowie Sonden und Sensormoleküle für neutrale und ionische Analyte und für die Charakterisierung von funktionellen Gruppen. Dabei erfolgen auch methodische Entwicklungen für die Fluoreszenzspektroskopie, die Fluoreszenzmikroskopie, die Milcrofluorometrie, die Sensorik und die Mikroarraytechnologie. Ziele sind u. a. das Design und die Untersuchung von multiplexfähigen selektiven und sensitiven Sonden für die Biomarkeranalytik, die Entwicklung von Methoden zur Charakterisierung der signalrelevanten Eigenschaften dieser Chromophor-Systeme und zur Charakterisierung von funktionellen Gruppen an Oberflächen und ihre Validierung sowie die Entwicklung und Bereitstellung von formatadaptierbaren, flexibel ersetzbaren Standards für die fluoreszenzbasierte Multiparameteranalytik. T2 - 5. Senftenberger Innovationsforum Multiparameteranalytik CY - Senftenberg, Deutschland DA - 10.03.2011 KW - Multiparametric KW - Multiplexing KW - Fluorescence KW - Nanoparticles KW - NIR dyes KW - Surface analysis KW - Quantum yield KW - Quantum dot KW - Lifetime PY - 2011 SP - 86 EP - 108 CY - Senftenberg AN - OPUS4-23635 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Retter, Utz A1 - Koch, Matthias A1 - Nehls, Irene T1 - On the improvement of the standard method DIN 38409 T2 - Institutskolloquium CY - Thessaloniki, Greece DA - 2000-11-29 PY - 2000 AN - OPUS4-1028 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, L. A1 - Jakobs, F. A1 - Spelthann, S. A1 - Zaremba, D. A1 - Radunz, Sebastian A1 - Resch-Genger, Ute A1 - Evert, R. A1 - Kielhorn, J. A1 - Kowalsky, W. A1 - Johannes, H.-H. T1 - Integration of β-NaYF4 Upconversion Nanoparticles into Polymers for Polymer Optical Fiber Applications N2 - Producing active polymer optical fibers (POFs) is a key step towards new applications such as fluorescent fiber solar concentrators (FFSCs), sensors, contactless coupling devices, or fiber integrated light sources and lasers. Therefore, integration of fluorescent nanoparticles into the polymer matrix is necessary and becomes accessible via in situ polymerization. For optical applications, the polymer has to fulfill various requirements such as chemical and physical stability, optical transparency in the application-relevant spectral region as well as a good synthetic accessibility. A common material for these is poly(methyl methacrylate) (PMMA). The β-phase NaYF4:Yb3+,Er3+ upconversion nanoparticles (UCNP) were synthesized from the rare earth salts via thermal decomposition method in high-boiling point solvent 1-octadecene and capping agent oleic acid. Current results show hazy samples of the polymer with integrated nanoparticles made from monomer solution of methyl methacrylate. However, further optical tuning such as increasing the transparency of the bulk samples by changing the monomer solution to non-polar n-butyl methacrylate (nButMA) or cyclohexyl methacrylate (CHMA) or further optimization of the UCNP shell could lead to more suitable polymer bulk samples. T2 - PCNSPA 2018 - Photonic Colloidal Nanostructures: Synthesis, Properties, and Applications CY - St. Petersburg, Russia DA - 04.06.2018 KW - Copolymer KW - Active fibers KW - Rare earth nanoparticles KW - Upconversion PY - 2018 SP - 1 EP - 9 AN - OPUS4-45883 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hoffmann, Katrin A1 - Resch-Genger, Ute A1 - Marlow, Frank T1 - Reversible Photosensitive Refractive Index Changes of Chromophor/Zeolite Nanocomposites T2 - Abschlußkolloquium "Nanostrukturierte Wirt/Gast-Systeme" CY - Berlin, Germany DA - 2002-10-21 PY - 2002 AN - OPUS4-1753 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lörchner, Dominique A1 - Koch, Matthias A1 - Kroh, L. W. A1 - Köppen, Robert T1 - Photodegradation of the „novel“ brominated flame retardant tris-(2,4,6-tribromophenoxy)-s-triazine N2 - Brominated flame retardants (BFRs) comprise a class of structurally diverse compounds that are functionally related and used in materials to reduce the flammability of polymers. Due to their global distribution, potential persistence, bioaccumulation and toxicity most of the BFRs of the first Generation are banned or restricted, and replaced by new ones. However, based on similar properties these new compounds may also pose a serious risk by causing adverse effects to human health and the environment. These alternative BFRs were grouped into two classes: „novel” and „emerging” BFRs. Emerging BFRs are defined as compounds that have been identified in any environmental compartments whereas novel BFRs are only detected in materials and/or goods above 0.1 wt.-%. The environmental fate of these alternative BFRs is partially unknown. Over the past years a multitude of studies on the photodegradation of BFRs in environmental matrices have been conducted to assess the photochemical behavior and fate in the environment. The photolytic debromination reaction is particularly induced among BFRs by UV exposure. The novel brominated triazine-based flame retardant tris-(2,4,6-tribromophenoxy)-s-triazine (TTBPTAZ) (Table 1) is a BFR that is mainly used in acrylonitrile butadiene styrene and high impact polystyrene. Ballesteros-Gómez et al. detected TTBP-TAZ in 8 of 13 plastic parts of consumer products and in 9 of 17 indoor dust samples but the photochemical behavior and fate is not known until now. The results of the present study, focused on photodegradation processes were performed for the first time for TTBP-TAZ to identify the photolysis intermediates and products to assess the environmental fate. T2 - DIOXIN CY - Florence, Italy DA - 29.08.2016 KW - Brominated flame retardants KW - TTBP-TAZ KW - Photodegradation PY - 2016 VL - 78 SP - 699 EP - 702 CY - Bayreuth AN - OPUS4-39037 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, L. A1 - Jakobs, F. A1 - Spelthann, S. A1 - Zaremba, D. A1 - Radunz, Sebastian A1 - Resch-Genger, Ute A1 - Evert, R. A1 - Kowalsky, W. A1 - Johannes, H.-H. T1 - Upconverting POF by Incubation of β-NaYF4:Yb3+, Er3+ Nanoparticles via in situ Polymerization for Production of active Polymer Optical Fibers N2 - In the past, integration of fluorescent dyes into polymers for active polymer optical fibers (POFs) is well studied, however, photobleaching of organic chromophores is still a problem for several optical applications. Inorganic luminescent nanoparticles like lanthanide-based systems can present an alternative due to their high chemical stability. Furthermore they do not show photobleaching and photoblinking. Certainly, integration of nanoparticles into a polymer matrix is challenging because of their high affinity to agglomeration which leads to scattering of the polymer samples. T2 - 27th International Conference on Plastic Optical Fibers CY - Seattle, Washington, USA DA - 04.09.2018 KW - Copolymer KW - Active fibers KW - Rare earth nanoparticles KW - Upconversion PY - 2018 SP - 1 EP - 5 CY - Seattle, Washington, USA AN - OPUS4-45882 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rurack, Knut A1 - Unger, Brita A1 - Müller, Ralf A1 - Resch-Genger, Ute T1 - SiO2-Gele als Matrices für Fluoreszenzmarker T2 - 75. Glastechnische Tagung CY - Wernigerode, Deutschland DA - 2001-05-21 PY - 2001 SP - 8 EP - 11 PB - DGG, Deutsche Glastechnische Gesellschaft e.V. CY - Frankfurt/M. AN - OPUS4-2084 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Retter, Utz A1 - Koch, Matthias A1 - Nehls, Irene T1 - Rückgewinnung von Mineralölen durch Salzbrechung von Öl-Wasser-Emulsionen T2 - Veranstaltung der SEPAWA CY - Berlin, BAM, Deutschland DA - 2000-09-08 PY - 2000 AN - OPUS4-956 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Deumer, J. A1 - Andresen, Elina T1 - SAXS data of bipyramidal LiYF4 nanoparticles N2 - SAXS data of bipyramidal LiYF4 nanoparticles synthesized by the Federal Institute for Materials Research and Testing (BAM) and measured by the Physikalisch-Technische Bundesanstalt (PTB) at the synchrotron facility Bessy II, Berlin, Germany. KW - Reference data set KW - Simulation KW - Reference material KW - Upconversion nanoparticles KW - Particle number concentration KW - SAXS PY - 2024 DO - https://doi.org/10.5281/zenodo.13691409 PB - Zenodo CY - Geneva AN - OPUS4-62134 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Resch-Genger, Ute A1 - Richter, Maria A1 - Güttler, Arne A1 - Pauli, Jutta A1 - Vogel, K. A1 - Homann, Christian A1 - Würth, Christian T1 - Extending Certified Spectral Fluorescence Standards for the Calibration and Performance Validation of Fluorescence Instruments to the NIR – Closing the Gap from 750 nm to 940 nm with Two Novel NIR Dyes N2 - Fluorescence methods provide spectral, intensity, polarization, and lifetime information, which contain sample- and instrument-specific contributions. Fluorescence data, comparable across instruments and laboratories, require validated calibration procedures and certified fluorescence standards. KW - Quality assurance KW - Reference material KW - Fluorescence KW - Dye KW - Traceability KW - Metrology KW - Calibration KW - Reference data KW - Reference product KW - Digital certificate KW - NIR KW - Instrument performance validation PY - 2025 SP - 1 EP - 4 PB - Springer Nature CY - London AN - OPUS4-62739 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Agasty, Amit A1 - Costard, Rene A1 - Hering, Marcus A1 - Chruscicki, Sebastian A1 - Hicke, Konstantin A1 - Hüsken, Götz T1 - Assessment of the Application of Scaling Concepts for Blast Effects Analysis N2 - Blast testing finds its implementation in several applications, e.g. for the purpose of investigation into accidental or intentional explosions, or for an assessment of the level of protection provided by a certain structural configuration. Analytical and/or semi-empirical methods are generally limited to preliminary assessments prior to blast testing. Applications of numerical simulations with hydrocodes coupled with finite element methods (FEM) can only reduce the amount of blast testing required, as these necessitate fulfillment of the fundamental prerequisites of model verification and that of model validation. Field tests are implemented for contact detonations as well as near-field blast scenarios and shock tube tests for far-field blast scenarios. However, these can be extremely resource intensive. Reliable small-scale experiments are a promising alternative. The concepts of dimensional analysis and similarity based on Buckingham’s Π-theorem (1914) have been applied in different fields. For applications to the phenomenon of shock wave propagation, Hopkinson-Cranz or cube-root scaling is a well-established concept. When it comes to scaling the structural response, research has predominantly focused on structures made of metallic materials. Scaled investigations with concrete or reinforced concrete (RC) structures remain limited. The lack of even the most basic guidelines (far from any ‘standardized scaling methods’ for blast tests) show that scaling as a method is not yet established in blast effects analysis. In this preliminary study, we present a systematic approach and evaluation of scaling of blast effects analysis for RC slabs in order to develop guidelines for resource efficient testing methods. We study the blast scenario at two different scales. The focus of these investigations has been on evaluation of scaling of dynamics using pressure sensors, acceleration sensors and fiber optic sensing cables for distributed acoustic sensing (DAS). Further, the resulting plastic behavior upon blast is characterized by distributed strain sensing (DSS) along the same cables. T2 - 27th International Symposium on Military Aspects of Blast and Shock (MABS27) CY - Colmar, France DA - 06.10.2025 KW - Similarity and scaling KW - Blast KW - RC-slabs PY - 2025 SP - 1 EP - 11 AN - OPUS4-64617 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Plarre, Rudy ED - Robinson, W. H. T1 - “From Saul to Paul” - Urban Pests in Cultural Entomology N2 - Harmful insects like clothes moths and termites occurring in the synanthropic environment are considered pests which need to be controlled. However, human culture has also always widely utilized them as central characters in philosophy, in classic and modern world literature, in music and arts, and much more. This article will highlight some recent exploitations of pest insects in Cultural Entomology. It will provide examples of pieces of art and ephemeral displays with clothes moths and termites as protagonists. The insects´ destructive nature on textiles or wood was turned around to a process of creation with aesthetic, philosophical and metaphoric messages, or simply for unique ways of entertainment. References will be provided to milestones of pest insect use in Cultural Entomology. T2 - International Conference on Urban Pests (ICUP) CY - Lund, Schweden DA - 29.06.2025 KW - Termites KW - Cultural Entomology KW - Material pests KW - Performance art KW - Tineola bisselliella PY - 2025 SP - 298 EP - 304 AN - OPUS4-64639 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Abilio, André T1 - Working Group 3 (WG3) Inputs N2 - During its first two years, the [WG3 of] COST Action CA20130 (Euro-MIC)progressed the achievement of this as described below Working group 3(WG3) increased collaboration in the field of microbiologically influenced corrosion (MIC) not only by partnering up with other CA20130 WGs to deliver MIC dedicated training sessions, but also by having regular meetings with its members on sensors and technologies for MIC monitoring. Through such online and in-person meetings, members from different countries and different technical backgrounds were brought together for an open share of knowledge and mutual benefit where gaps between microbiology and corrosion were bridged. KW - Monitoring KW - Sensor KW - Microbiologically Influenced Corrosion PY - 2023 SP - 1 EP - 7 PB - COST Action AN - OPUS4-64604 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Lisec, Jan T1 - fioRa N2 - R package providing a wrapper for the python module 'FIORA' as well as a 'shiny'-App to facilitate data processing and visualization. 'FIORA' allows to predict Mass-Spectra based on the SMILES code of chemical compounds. It is described in the Nature Communications article by Nowatzky et al. (2025). KW - Mass Spectrometry PY - 2025 UR - https://github.com/cran/fiora/ PB - GitHub CY - San Francisco AN - OPUS4-64663 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bustamante, Joana A1 - Naik, Aakash A1 - Ueltzen, Katharina A1 - George, Janine A1 - Ertural, Christina T1 - Thermal Transport in Ag8TS6 (T= Si, Ge, Sn) Argyrodites: An Integrated Experimental, Quantum-Chemical, and Computational Modelling Study. DFT-part N2 - This repository contains computational data supporting the manuscript titled *“Thermal Transport in Ag8TS6 (T= Si, Ge, Sn) Argyrodites: An Integrated Experimental, Quantum-Chemical, and Computational Modelling Study”* It includes raw data for vibrational properties, elastic properties and Bonding analysis. KW - DFT KW - QHA KW - Lattice thermal conductivity KW - Grüneisen parameter PY - 2025 DO - https://doi.org/10.5281/zenodo.17399975 PB - Zenodo CY - Geneva AN - OPUS4-64671 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bustamante, Joana A1 - Naik, Aakash A1 - Ueltzen, Katharina A1 - Ertural, Christina A1 - George, Janine T1 - Thermal Transport in Ag8TS6 (T= Si, Ge, Sn) Argyrodites: An Integrated Experimental, Quantum-Chemical, and Computational Modelling Study. N2 - This repository includes raw data for bonding analysis and lattice thermal conductivity using MLIP-MACE-MP03b, supporting the manuscript “Thermal Transport in Ag8TS6 (T= Si, Ge, Sn) Argyrodites: An Integrated Experimental, Quantum-Chemical, and Computational Modelling Study” KW - DFT KW - LOBSTER KW - Lattice thermal conductivity KW - MLIP PY - 2025 DO - https://doi.org/10.5281/zenodo.17397456 PB - Zenodo CY - Geneva AN - OPUS4-64674 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Müller, Bernd R. A1 - Lange, Axel A1 - Harwardt, Michael A1 - Hentschel, Manfred P. A1 - Illerhaus, Bernhard A1 - Goebbels, Jürgen A1 - Bamberg, J. A1 - Heutling, F. T1 - Micro Crack Characterization of Metal Matrix Composites by 3D-Refraction-Computed-Tomography T2 - 16th World Conference on Nondestructive Testing CY - Montreal, Canada DA - 2004-08-30 KW - NDE KW - X-ray refraction KW - Composites KW - MMC PY - 2004 SP - 9 pages PB - International Committee for Non-Destructive Testing CY - Montreal AN - OPUS4-5486 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hentschel, Manfred P. A1 - Müller, Bernd R. A1 - Lange, Axel A1 - Harbich, Karl-Wolfram A1 - Schors, Jörg A1 - Wald, Oliver T1 - New Developments in X-ray-Topography of Advanced Non-Metallic Materials T2 - 15th World Conference on Non-Destructive Testing (WCNDT) CY - Roma, Italy DA - 2000-10-15 PY - 2000 UR - http://www.ndt.net/article/wcndt00/papers/idn258/idn258.htm SN - 1435-4934 VL - 5 IS - 11 PB - NDT.net CY - Kirchwald AN - OPUS4-928 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, Bernd R. A1 - Hentschel, Manfred P. A1 - Harbich, Karl-Wolfram A1 - Lange, Axel A1 - Schors, Jörg T1 - X-Ray Refraction Topography for Non-Destructive Evaluation of Advanced Materials KW - X-Ray Refraction KW - Fibre Debonding KW - Topography KW - Crack Density KW - Pore Size KW - SAXS PY - 2001 SP - 1 EP - 7 PB - Society of Manufacturing Engineers CY - Dearborn, Mich. AN - OPUS4-1097 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bachmann, Marcel A1 - Putra, Stephen Nugraha A1 - Yang, Fan A1 - Meng, Xiangmeng A1 - Pusbatzkies, Pablo A1 - Rethmeier, Michael T1 - Elucidation of the Laser Beam Energy Attenuation by the Vapor Plume Formation during High Power Laser Beam Welding N2 - In high-power laser beam welding, a common phenomenon is the formation of a keyhole caused by the rapid evaporation of the material. Under atmospheric pressure, this evaporation generates a vapor plume that interacts with the laser beam, leading to energy attenuation and scattering of the laser radiation along its path. These interactions affect the stability of the process and the overall weld quality. This study investigates the influence of the vapor plume on the weld pool and keyhole dynamics during high-power laser beam welding of AlMg3 aluminum alloy through experimental and numerical approaches. The primary goal is to identify key vapor plume characteristics, particularly its length fluctuations, and to improve the accuracy of the numerical models. To achieve this, an algorithm was developed for the automated measurement of the vapor plume length using high-speed imaging and advanced data processing techniques. The measured plume length is then used to estimate the additional vapor heating and laser energy attenuation using the Beer–Lambert law. A refined numerical CFD model, incorporating 3D transient heat transfer, fluid flow, and ray tracing, was developed to evaluate the vapor plume’s impact. Results show that already the time-averaged plume length effectively captures its transient influence and aligns well with experimental weld seam geometries. Additionally, energy scattering and absorption caused by the vapor plume led to a wider weld pool at the top surface. The study also shows an increased percentage of keyhole collapses due to the reduced laser power absorption at the keyhole bottom, further highlighting the importance of accurately modeling vapor plume effects. T2 - International Congress of Applications of Lasers & Electro-Optics 2025 CY - Orlando, USA DA - 12.10.2025 KW - Laser beam welding KW - Vapor plume formation KW - Weld pool KW - Keyhole dynamics KW - Numerical modeling PY - 2025 SP - 1 EP - 10 AN - OPUS4-64817 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jeyifous, Olubunmi Anthony A1 - Schönsee, Eric A1 - Strangfeld, Christoph A1 - Hüsken, Götz T1 - Investigating the impact of material rheology on geometric accuracy in 3D concrete printing using real-time monitoring N2 - Additive manufacturing of concrete structures is an innovative and rapidly advancing technology. One of its key advantages is the ability to achieve freeform designs in civil engineering, enabling entirely new architectural possibilities. However, despite the demonstrated benefits of this technology, maintaining consistent print quality during the printing process remains a significant challenge and is seldom implemented. The continuous mixing process inherent in 3D concrete printing introduces potential variations in the dry mix composition or water content, making a single test sample insufficient to represent the entire structure. Moreover, defects in a single layer can compromise the integrity of the whole structure. This underscores the need for continuous, real-time monitoring to document and ensure the quality of the printing process. At the Bundesanstalt für Materialforschung und prüfung (BAM), a 3D concrete printer was developed to enable real-time non-destructive monitoring of material properties during the printing process. This study examines the impact of rheological variations, influenced by water content variations, on the geometric characteristics of printed elements. Geometric measurements are captured in real time using a high-precision laser scanner. Concrete elements are printed under controlled conditions with systematically varied process parameters. Preliminary results reveal a strong correlation between rheological behaviour and the geometric properties of the printed components. T2 - NDT-CE 2025 - The International Symposium on Nondestructive Testing in Civil Engineering CY - Izmir, Turkiye DA - 24.09.2025 KW - 3D concrete printing KW - Real-time monitoring KW - Quality control PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-645394 DO - https://doi.org/10.58286/31704 SN - 1435-4934 SP - 1 EP - 10 PB - NDT.net AN - OPUS4-64539 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Stawski, Tomasz A1 - Miliute, Aiste T1 - Structural Refinement of ZrV₂O₇ with Negative Thermal Expansion Using Pair Distribution Function Analysis N2 - This repository contains Python scripts specifically developed for structural refinement of Zirconium Vanadate (ZrV₂O₇), a material known for its negative thermal expansion (NTE). The scripts implement Pair Distribution Function (PDF) analysis to refine crystal structures directly from experimental X-ray diffraction (XRD) data. The refinement workflow is built around the DiffPy-CMI library, enhanced with custom functionalities tailored for ZrV₂O₇ and similar oxide materials. KW - Zirconium vandate KW - Total scattering KW - Pair distribution function KW - Structure refinement PY - 2025 DO - https://doi.org/10.5281/zenodo.15395752 PB - Zenodo CY - Geneva AN - OPUS4-64750 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lange, Axel A1 - Hentschel, Manfred P. A1 - Kupsch, Andreas T1 - Enhanced spatial resolution using iterative focal desmearing in computed tomography N2 - Computed tomography reconstructions of projected data usually assume an ideal point-like focal spot. However, in practice, the actual finite focus size leads to blurred projections, unavoidably. The elements (voxels) of the reconstruction array are smeared differently as a function of their individual position relative to source and detector. Neglecting the focal smearing generates considerably blurred reconstructions. Previous attempts were based on directly deconvolving blurred projections from a constant kernel, which yields better results but still exhibits artefacts. Iterative algorithms can be adopted to take into account focal smearing as a function of position. However, this requires detailed prior knowledge of quantitative smear functions. The DIRECTT (Direct Iterative Reconstruction of Computed Tomography Trajectories) algorithm is a promising candidate to meet these requirements. It has been demonstrated elsewhere that DIRECTT copes with limited data sets such as limited view and region-of- interest data by tracing single sinusoidal-like trajectories in Radon space, which are selected from the set of all possible trajectories by appropriate criteria. Currently, position-dependent smearing is used in the projection part of iterations. At the example of model reconstructions we demonstrate the gain of spatial resolution by iterative variable desmearing according to the DIRECTT algorithm in comparison to the standard filtered back-projection. T2 - 10th European conference on non-destructive testing CY - Moscow, Russia DA - 2010-06-07 KW - Computed tomography KW - Spatial reslution KW - Reconstruction algorithm KW - Focal smearing PY - 2010 UR - http://www.ndt.net/article/ecndt2010/reports/1_09_18.pdf IS - Paper 4.02.18 SP - 1 EP - 9(?) AN - OPUS4-21466 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Grandel, Jonas T1 - Harmonic phonon dataset N2 - Phonon Dataset calculated with DFT PBE and the foundational MACE-MP-0b3 model. The data are presented and discussed in the following publication: https://doi.org/10.1063/5.0297006 KW - Phonon KW - MACE KW - DFT PY - 2025 UR - https://github.com/ACEsuit/mace-foundations PB - GitHub CY - San Francisco, CA, USA AN - OPUS4-64747 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Seifarth, A. T1 - 3D-Analytik poröser Filterstrukturen N2 - Die Beschaffenheit des Gefüges hat entscheidenden Einfluss auf die Eigenschaften eines Werkstoffes. Besonders die Faktoren „Porosität“ und „Anisotropie“ sind für viele industrielle Anwendungen von großem Interesse. Ein Beispiel ist deren Einfluss auf die Permeabilität und Tortuosität von Filterstrukturen. An der Bundesanstalt für Materialforschung und -prüfung wurde zur Analyse von offen-porigen Strukturen ein Algorithmus zur Anwendung auf rekonstruierte 3D CT-Datensätze beliebiger Probenkörper entwickelt. Dieser basiert auf der Analyse von Grenzflächen und ermittelt anhand deren richtungsabhängigen Häufigkeiten die Orientierungsverteilung sowie den Anisotropiegrad der Poren im Raum. Im Rahmen dieser Arbeit wurde der Algorithmus in einer C++-basierten Software implementiert und an simulierten Porenvolumen und realen, binarisierten Datensätzen am Beispiel eines Polymers mit geschlossener Porosität sowie einer (offen) porösen Keramik getestet. Dabei ergab sich eine zuverlässige Bestimmung der gesuchten Parameter in drei Dimensionen. Die Verwendung des Algorithmus ist dabei nicht auf offen-porige Strukturen beschränkt, sondern kann auch zur Analyse von geschlossenen Porositäten eingesetzt werden. KW - Porosität KW - Anisotropie KW - Dieselpartikelfilter KW - Keramik PY - 2017 SP - 1 EP - 97 CY - Berlin AN - OPUS4-47484 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Strobl, Dominic A1 - Unger, Jörg F. A1 - Chady, G. A1 - Klawoon, Alexander A1 - Pittner, Andreas A1 - Rethmeier, Michael A1 - Robens-Radermacher, Annika T1 - Efficient bead-on-plate weld model for parameter estimation towards effective wire arc additive manufacturing simulation N2 - Despite the advances in hardware and software techniques, standard numerical methods fail in providing real-time simulations, especially for complex processes such as additive manufacturing applications. A real-time simulation enables process control through the combination of process monitoring and automated feedback, which increases the flexibil- ity and quality of a process. Typically, before producing a whole additive manufacturing structure, a simplified experiment in form of a bead-on- plate experiment is performed to get a first insight into the process and to set parameters suitably. In this work, a reduced order model for the transient thermal problem of the bead-on-plate weld simulation is devel- oped, allowing an efficient model calibration and control of the process. The proposed approach applies the proper generalized decomposition (PGD) method, a popular model order reduction technique, to decrease the computational effort of each model evaluation required multiple times in parameter estimation, control and optimization. The welding torch is modeled by a moving heat source, which leads to difficulties separating space and time, a key ingredient in PGD simulations. A novel approach for separating space and time is applied and extended to 3D problems allowing the derivation of an efficient separated representation of the tem- perature. The results are verified against a standard finite element model showing excellent agreement. The reduced order model is also leveraged in a Bayesian model parameter estimation setup, speeding up calibrations and ultimately leading to an optimized real-time simulation approach for welding experiment using synthetic as well as real measurement data. KW - Ermüdung PY - 2023 DO - https://doi.org/10.5281/zenodo.7456813 PB - Zenodo CY - Geneva AN - OPUS4-59651 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakir, Nasim A1 - Üstündag, Ömer A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Observation of the weld pool shape in partial penetration welding and its influence on solidification crack formation for high-power laser beam welding N2 - In this study, steel-glass experiments were conducted to observe the melt pool geometry using a high-speed camera. The high-speed recordings and optical flow analysis show that two main flows take place in form of vortices. The lower vortex drives the melt backwards from the front keyhole wall and thus causes an extension of the melt pool, which is called bulging. This bulging promotes solidification cracking by forming a closed area filled with melt and the accumulation of impurities in the final solidification phase, resulting in low-melting phases which are under tensile stress at the end of solidification. T2 - Lasers in Manufacturing Conference 2021 CY - Online meeting DA - 21.06.2021 KW - Laser beam welding KW - Weld pool shape KW - Solidification craking KW - Partial penetration PY - 2021 SP - 1 EP - 5 AN - OPUS4-53587 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baeßler, Matthias A1 - Ebell, Gino A1 - Herrmann, Ralf A1 - Hille, Falk A1 - Schneider, Ronald ED - Lienhart, Werner ED - Krüger, Markus T1 - On potentials and challenges of physics-informed SHM for civil engineering structures N2 - Physics-informed structural health monitoring, which integrates realistic physical models of material behavior, structural response, damage mechanisms, and aging processes, offers a promising approach to improve monitoring capabilities and inform operation and maintenance planning. However, the associated technical challenges and model requirements are context-specific and vary widely across applications. To illustrate the relevance and potential of the topic, two application examples are presented. The first focuses on monitoring the modal characteristics of a prestressed road bridge, where strong sensitivity to temperature variations limits the diagnostic capabilities of conventional vibration-based global monitoring. The discussion highlights how environmental influences can obscure structural changes, and emphasizes that purely data-based approaches are inherently limited to detecting anomalies and do not enable comprehensive condition diagnostics. The second example explores a physics-informed monitoring approach for prestressed concrete bridges affected by hydrogen-induced stress corrosion cracking. T2 - SHMII-13 CY - Graz, Austria DA - 01.09.2025 KW - Hydrogen Stress Corrosion Cracking KW - SHM KW - Physics informed PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-643271 SN - 978-3-99161-057-1 DO - https://doi.org/10.3217/978-3-99161-057-1-039 SP - 245 EP - 251 PB - Verlag der Technischen Universität Graz CY - Graz, Austria AN - OPUS4-64327 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Elert, Anna Maria A1 - Meyer, Lena A1 - Brunner, Nanine A1 - Melzer, Micheal A1 - Koch, Claudia T1 - Advancing Digital Quality Infrastructure: Transforming Laboratory Processes for Enhanced Efficiency and Reliability N2 - The digital Quality Infrastructure (QI) holds significant potential for ensuring and enhancing the accuracy, reliability, and efficiency of laboratory processes. Establishing digital QI tools and processes and the integration into the larger digital QI ecosystem however comes with many technical and organizational challenges at the laboratory but also larger system level. This paper presents solutions of a digital QI tool set that are being developed within the German initiative QI-Digital, our own experiences in the implementation of Digital Calibration Certificates (DCCs) as eAttestation in our laboratory, as well as the structured process we have been establishing to engage with the laboratory community to support adoption of the digital QI. T2 - 2025 IMEKO TC-6 International Conference of Metrology and Digital Transformation - M4DConf CY - Benevento, Italy DA - 03.09.2025 KW - Digital Calibration Certificate KW - Digitalization KW - Laboratories KW - Quality Inflastructure PY - 2025 VL - 2025 SP - 1 EP - 6 AN - OPUS4-64283 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schönsee, Eric A1 - Hüsken, Götz A1 - Kocherla, Amarteja A1 - Strangfeld, Christoph T1 - A framework for characterising the reflection intensity of a 3D-CP mortar N2 - The growing interest of 3D Concrete Printing (3DCP) arises new challenges for quality control. A major challenge lies in evaluation of the interlayer bond strength. An optical approach is developed to monitor the surface properties of the printed layer. Commercial laser profile scanners are utilised to record the reflection intensity of the mortar’s surface. To be applicable in the printing process, the reflection intensity needs to be characterised for each material within the printable region and further effects, like geometry and environmental light, need to be considered. The presented work aims to provide a framework for implementing the laser reflection intensity to 3DCP monitoring. T2 - NDT-CE 2025 - The International Symposium on Nondestructive Testing in Civil Engineering CY - Izmir, Türkiye DA - 24.09.2025 KW - 3D Concrete Printing KW - In Situ Measurements KW - Laser reflection intensity PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-643047 DO - https://doi.org/10.58286/31728 SN - 1435-4934 SP - 1 EP - 4 PB - NDT.net AN - OPUS4-64304 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Lisec, Jan T1 - IsoCor N2 - Despite numerous advantages offered by hyphenation of chromatography and electrokinetic separation methods with multicollector (MC) ICP-MS for isotope analysis, the main limitation of such systems is the decrease in precision and increase in uncertainty due to generation of short transient signals. To minimize this limitation, most authors compare several isotope ratio calculation methods and establish a multi-step data processing routine based on the precision and accuracy of the methods. However, to the best of our knowledge, there is no universal data processing tool available that incorporates all important steps of the treatment of the transient signals. Thus, we introduce a data processing application (App) IsoCor that facilitates automatic calculation of isotope ratios from transient signals and eases selection of the most suitable method. The IsoCor App performs baseline subtraction, peak detection, mass bias correction, isotope ratio calculation and delta calculation. The feasibility and reliability of the App was proven by reproducing the results from isotope analysis of three elements (neodymium, mercury and sulfur) measured on-line via hyphenated systems. The IsoCor App provides trackability of the results to ensure quality control of the analysis. KW - Shiny-App KW - ICP-MS KW - Software PY - 2022 UR - https://github.com/cran/IsoCor/ PB - GitHub CY - San Francisco, CA, USA AN - OPUS4-56307 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Lisec, Jan T1 - ABID N2 - In order to automate the spectral comparison for larger libraries of antibodies, we developed the online software ABID 2.0. This open-source software determines the number of matching peptides in the fingerprint spectra. We propose that publications and other documents critically relying on monoclonal antibodies with unknown amino acid sequences should include at least one antibody fingerprint. By fingerprinting an antibody in question, its identity can be confirmed by comparison with a library spectrum at any time and context. KW - Software KW - Antibody KW - MALDI PY - 2022 UR - https://github.com/BAMresearch/ABID PB - GitHub CY - San Francisco, CA, USA AN - OPUS4-56192 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Lisec, Jan T1 - InterpretMSSpectrum (R package to annotate mass spectra) N2 - Gas chromatography using atmospheric pressure chemical ionization coupled to mass spectrometry (GC/APCI-MS) is an emerging metabolomics platform, providing much-enhanced capabilities for structural mass spectrometry as compared to traditional electron ionization (EI)-based techniques. To exploit the potential of GC/APCI-MS for more comprehensive metabolite annotation, a major bottleneck in metabolomics, we here present the novel R-based tool InterpretMSSpectrum assisting in the common task of annotating and evaluating in-source mass spectra as obtained from typical full-scan experiments. After passing a list of mass-intensity pairs, InterpretMSSpectrum locates the molecular ion (M0), fragment, and adduct peaks, calculates their most likely sum formula combination, and graphically summarizes results as an annotated mass spectrum. Using (modifiable) filter rules for the commonly used methoximated-trimethylsilylated (MeOx-TMS) derivatives, covering elemental composition, typical substructures, neutral losses, and adducts, InterpretMSSpectrum significantly reduces the number of sum formula candidates, minimizing manual effort for postprocessing candidate lists. We demonstrate the utility of InterpretMSSpectrum for 86 in-source spectra of derivatized standard compounds, in which rank-1 sum formula assignments were achieved in 84% of the cases, compared to only 63% when using mass and isotope information on the M0 alone. We further use, for the first time, automated annotation to evaluate the purity of pseudospectra generated by different metabolomics preprocessing tools, showing that automated annotation can serve as an integrative quality measure for peak picking/deconvolution methods. As an R package, InterpretMSSpectrum integrates flexibly into existing metabolomics pipelines and is freely available from CRAN (https://cran.r-project.org/). KW - Mass Spectrometry KW - Spectra annotation KW - Software KW - R package PY - 2016 UR - https://github.com/cran/InterpretMSSpectrum/ PB - GitHub CY - San Francisco, CA, USA AN - OPUS4-57856 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Noureen, N. A1 - Shah, F. A. A1 - Lisec, Jan A1 - Usman, H. A1 - Khalid, M. A1 - Munir, R. A1 - Zaidi, N. T1 - Revisiting the Association between Human Leukocyte Antigen and End-Stage Renal Disease N2 - Multiple works have studied possible associations between human leukocyte antigen (HLA) alleles and end stage renal disease (ESRD). However, there are several contradictions in these previous works and no consistent HLA associations with ESRD itself have been identified. Most of these works have several limitations, for instance, the population size was too small, or only limited HLA loci were studied. The presented work aims to revisit the association between ESRD and HLA antigens while taking in to account the previously overlooked limitations. Here, we compared the HLA polymorphism (at HLA-A, -B, -C, -DRB1, -DQB1 and DQA1 loci) in ESRD patients (n=497) and controls (n=672). Our data identified several HLA alleles that displayed a significant positive or negative association with ESRD. We also determined whether heterozygosity or homozygosity of the ESRD-associated HLA alleles at different loci could modify the prevalence of the disease. Few HLA allele combinations displayed significant associations with ESRD among which HLA-A*3 –HLA-A*26 combination showed the highest strength of association (OR= 4.488, P≤ 0.05) with ESRD. However, the age of ESRD onset was not affected by HLA allele combinations at different loci. Most of the previous works have studied the association of HLA with ESRD in homogeneous ethnic groups and have interpreted their data accordingly. Here, we also performed an extensive literature analysis to determine whether the association of HLA to ESRD can be similar across different ethnic groups. This analysis showed that at least for certain alleles, the association of HLA to ESRD can be similar in different ethnic groups. For instance, HLA-A*11, HLA-DRB1*11, and HLA-DRB1*4 all showed significant positive associations with ESRD in different ethnic groups. The findings of our study will help in determining possible protective or susceptible roles of various HLA alleles in ESRD. KW - Mass-Spectrometry KW - HLA KW - Renal disease PY - 2020 DO - https://doi.org/10.1101/2020.03.18.996330 SP - 1 EP - 23 AN - OPUS4-50720 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Lisec, Jan T1 - MetabolomicsBasics (R package to process and analyze metabolomics datasets) N2 - Raw data from metabolomics experiments are initially subjected to peak identification and signal deconvolution to generate raw data matrices m × n, where m are samples and n are metabolites. We describe here simple statistical procedures on such multivariate data matrices, all provided as functions in the programming environment R, useful to normalize data, detect biomarkers, and perform sample classification. KW - Software KW - Mass Spectrometry KW - R package KW - Data processing PY - 2018 UR - https://github.com/cran/MetabolomicsBasics/ PB - GitHub CY - San Francisco, CA, USA AN - OPUS4-57854 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gawlitza, Kornelia T1 - Wieviel Schmutz ist rein? Über das Arbeiten im Reinraum N2 - Um verlässliche Methoden für die medizinische Diagnostik und Umweltanalytik zu entwickeln sowie Zellen zu kultivieren, ist staub- bzw. keimfreies Arbeiten in einem Reinraum erforderlich. Aber was ist ein Reinraum? Viele stellen sich hier sterile Räume, keine Fenster und Personen in weißen Anzügen und Schutzmaske vor. Hier können die Besucher einen Blick hinter die Kulissen werfen und erfahren, was die Eigenschaften und Bedingungen eines Reinraumes sind und welche Anforderungen an die dort Beschäftigten gestellt werden. KW - Reinraum PY - 2017 UR - http://www.aktuelle-wochenschau.de/main-navi/aktuelle-wochenschau-2017/kw49-wieviel-schmutz-ist-rein-ueber-das-arbeiten-im-reinraum.html SP - 1 EP - 2 AN - OPUS4-43355 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Agudo Jácome, Leonardo A1 - Mosquera Feijoo, Maria A1 - Nolze, Gert A1 - Rizzo, F. ED - Militzer, M. ED - Botton, G. ED - Chen, L.-Q. ED - Howe, J. ED - Sinclair, C. ED - Zurob, H. T1 - Nano-sized precipitates in an Fe-13Cr alloy formed under oxidizing water vapor atmosphere N2 - Oxidation of a Fe –13Cr alloy under water vapor at 600°C produced a zone of nano-sized precipitation underneath the outside scale formed by iron oxides and Fe–Cr spinel. The majority of the spinel layer shows a fixed orientation relationship to the ferritic matrix: {1 0 0}α || {1 0 0}sp & <0 1 1>α || <0 0 1>sp . However, also the discovered precipitated particles are characterized by the same crystallographic orientation relationship to the respective ferritic parent grain. The habit of the precipitates is best described by a lath morphology with their main axis parallel to <1 0 0> of ferrite. Energy dispersive X-ray spectroscopy (EDX) and electron backscatter diffraction (EBSD) in scanning electron microscope (SEM) have been applied to characterize the oxide layer in micrometer scale. The clearly smaller precipitates were subsequently investigated by transmission electron microscopy (TEM). Specimens have been prepared by focused ion-beam (FIB) milling at an area previously characterized by EBSD. They cover the ferritic base material, but mainly the precipitation zone and the Fe–Cr spinel layer. Energy filtered selected area diffraction (SAD) in the conventional (C)TEM and high-angle annular dark field (HAADF) imaging in the scanning (S)TEM mode were employed in the characterization of the specimens. T2 - PTM 2015 - International conference on solid-solid phase transformations in inorganic materials CY - Whistler, BC, Canada DA - 28.06.2015 KW - Precipitation KW - Nano-crystals KW - Oxidation KW - Phase transformation KW - EBSD KW - TEM PY - 2015 SP - 379 EP - 386 AN - OPUS4-34444 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meng, Xiangmeng A1 - Putra, Stephen Nugraha A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Parametric study of the laser energy absorption in high-power laser beam welding N2 - Laser energy absorption on the keyhole wall is decisive for the thermodynamic behavior and the resultant weld properties in the high-power laser beam welding process. However, its highly transient nature on a microsecond scale makes the quantitative analysis challenging. In this paper, the influence of the relevant welding parameters on laser energy absorption is studied statistically by utilizing multiphysical modeling, in which the three-dimensional transient keyhole dynamics and thermo-fluid flow are calculated. A dynamic mesh adaption technique and a localized level-set-based ray-tracing method are employed to improve the model accuracy further. The results show that the focus position has a remarkable effect on the time-averaged laser absorption, and in contrast, the laser energy distribution regime is only slightly influenced by the welding speed in the studied parameter range (1.5–3.0 m/min). The absorption ratio of the laser energy on the keyhole front wall decreases with increasing welding speed and increases with upward-moving focus positions. The comparison between the calculated results and the experimental measurements ensures the validity of the proposed model. T2 - International Congress of Applications of Lasers & Electro-Optics 2024 CY - Los Angeles, CA, USA DA - 03.11.2024 KW - Laser beam welding KW - Laser energy absorption KW - Multiphysics modeling KW - Parametric study KW - Weld pool PY - 2024 SP - 1 EP - 8 AN - OPUS4-61629 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niederleithinger, Ernst A1 - Sein, Sander A1 - Kervalisvil, Andrei A1 - Wöstmann, Jens A1 - Helm, Marek T1 - Muon tomography - ready for practical application? N2 - Muon tomography uses naturally occurring nuclear particles to 'X-ray' technical objects. It has applications in security and nuclear safeguards, but not yet in civil engineering. The potential is enormous, as muon tomography could replace traditional X-ray imaging of infrastructure, a method that was popular in the past but has mostly been abandoned due to concerns about radiation safety. In 2020, a report on the first large-scale muon tomography experiment on a reinforced concrete specimen was published. However, robust mobile detectors and faster data acquisition methods are still needed. This is now changing, however. Prototype mobile detectors have been announced or are in development, and data acquisition time has been reduced from weeks to days. This presentation will showcase current developments and focus on a validation experiment at BAM. T2 - NDT-CE 2025 - The International Symposium on Nondestructive Testing in Civil Engineering CY - Izmir, Türkiye DA - 24.09.2025 KW - Concrete KW - Muon tomography KW - Inspection PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-642517 DO - https://doi.org/10.58286/31696 SN - 1435-4934 VL - 30 IS - 10 SP - 1 EP - 10 PB - ndt.net AN - OPUS4-64251 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rabe, Ute A1 - Emge, Julia A1 - Klein, Samuel A1 - Oswald, Jan A1 - Shpakova, Nina A1 - Stopp, Philipp A1 - Weingard, Christoph A1 - Koster, Dirk A1 - Schönsee, Eric A1 - Hille, Frank A1 - Niederleithinger, Ernst T1 - Development of distributed sensor electronics for energy-efficient and proactive maintenance of buildings N2 - Permanently installed sensor systems are becoming increasingly important for monitoring critical infrastructure. The research institutes Fraunhofer IZFP and BAM, together with industrial partners and users, are developing a concept for an electronic system consisting of an Edge-Gateway as a central high-performance node and a variable number of Sensor-Edge units that establish the connection between the sensors of the permanent monitoring system and the gateway, which also provides connection to a cloud. A software tool allows identification and localization of sensors and visualization of sensor data. The principle of the system is demonstrated using sensors installed in the road surface to monitor traffic loads as an example. Two test structures, a full-scale laboratory at Fraunhofer IZFP, Saarbrücken, and the “BLEIB” reference structure at BAM, test site technical safety (TTS) Horstwalde, were used to demonstrate the principle and the functioning of the electronic system. T2 - NDT-CE 2025 - The International Symposium on Nondestructive Testing in Civil Engineering CY - Izmir, Türkiye DA - 24.09.2025 KW - Edge computing KW - Bridge monitoring KW - Multi-sensor PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-642530 DO - https://doi.org/10.58286/31650 SN - 1435-4934 VL - 30 IS - 10 SP - 1 EP - 3 PB - ndt.net AN - OPUS4-64253 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Roumia, N. A1 - Niederleithinger, Ernst A1 - Mazotti, C. T1 - Post-tensioned concrete inspection and imaging using 2D and 3D Dry Point Contact ultrasound array N2 - by the asset owners. Advancements were introduced to the method by distributing numerous shear horizontal Dry Point Contact (DPC) transducers in a uniform way, forming a linear array that allows for immediate two-dimensional imaging of the subsurface using Synthetic Aperture Focusing Technique (SAFT). Recent developments were implemented, allowing for the full potential use of the array by means of three-dimensionaldata acquisition instead of two-dimensional. This work provides a practical comparison between the 2D Linear scanning mode and the newly introduced 3D Matrix scanning mode regarding the tendon duct inspection, grouting quality, and reinforcement localization. Imaging the subsurface was performed through research-oriented software, namely InterSAFT, which allows for 2D and 3D imaging using Linear and Matrix data acquisitions. T2 - NDT-CE 2025 - The International Symposium on Nondestructive Testing in Civil Engineering CY - Izmir, Türkiye DA - 24.09.2025 KW - Ultrasound KW - Imaging KW - Concrete KW - SAFT PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-642551 DO - https://doi.org/10.58286/31690 SN - 1435-4934 VL - 30 IS - 10 SP - 1 EP - 4 PB - ndt.net AN - OPUS4-64255 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kupsch, Andreas A1 - Lange, Axel A1 - Hentschel, Manfred P. T1 - Enhanced Spatial Resolution in 2D CT-Reconstruction without Filtered Back Projection: DIRECTT T2 - 17th World Conference on Non-Destructive Testing CY - Shanghai, China DA - 2008-10-25 KW - Computed tomography KW - Reconstruction algorithm KW - Spatial resolution PY - 2008 SP - 1 EP - 6 PB - International Committee for Non-Destructive Testing CY - Shanghai AN - OPUS4-18569 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, Bernd R. A1 - Hentschel, Manfred P. A1 - Harbich, Karl-Wolfram A1 - Lange, Axel A1 - Schors, Jörg T1 - X-ray refraction topography for non-destructive evaluation of advanced materials T2 - 15th World Conference on Non-Destructive Testing (WCNDT) CY - Roma, Italy DA - 2000-10-15 KW - X-ray refraction PY - 2000 UR - http://www.ndt.net/article/wcndt00/papers/idn257/idn257.htm SN - 1435-4934 VL - 5 IS - 11 SP - 1 EP - 7(?) PB - NDT.net CY - Kirchwald AN - OPUS4-871 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Bernd R. A1 - Hentschel, Manfred P. A1 - Harbich, Karl-Wolfram A1 - Lange, Axel A1 - Schors, Jörg T1 - Charakterisierung von Mikroschäden in polymeren Faserkompositen mittels Röntgen-Refraktions-Topography T2 - Jahrestagung Zerstörungsfreie Materialprüfung 2001 CY - Berlin, Deutschland DA - 2001-05-21 PY - 2001 UR - http://www.ndt.net/article/dgzfp01/papers/p49/p49.htm N1 - Serientitel: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. – Series title: Berichtsband / Deutsche Gesellschaft für zerstörungsfreie Prüfung e. V. IS - 75-CD PB - DGZfP CY - Berlin AN - OPUS4-1298 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Vogel, Christian A1 - Helfenstein, J. A1 - Massey, M. A1 - Kretzschmar, R. A1 - Schade, U. A1 - Verel, R. A1 - Chadwick, O. A1 - Frossard, E. T1 - Spectroscopic analysis shows crandallite can be a major component of soil phosphorus N2 - Phosphorus (P) bioavailability is crucial for the productivity of natural and agricultural ecosystems, and soil P speciation plays a major role therein. Better understanding of P forms present in soil is thus essential to predict bioavailability. Most studies on soil P forms differentiate between Ca-bound P (e.g. apatite), organic P, Fe-bound P, and Al-bound P. In our analysis of a Ca, Al, and P rich soil from the Kohala region of Hawaii, we identified the mineral crandallite, CaAl3(PO4)2(OH)5∙H2O, a mineral previously not considered to play a significant role in soils. Crandallite was first identified with powder X-ray diffraction, and then confirmed with microfocused P K-edge X-ray absorption near edge structure (XANES) spectroscopy, micro-infrared spectroscopy, and solid-state 31P nuclear magnetic resonance (NMR) spectroscopy. Crandallite XANES spectra were distinct from other common XANES spectra due to the presence of features in the post-edge region of the spectrum. Linear combination fitting of bulk P K-edge XANES spectra allowed the determination of the proportion of crandallite to the total P content, indicating that crandallite comprises up to half, possibly even more of the soil P in the samples. Crandallite is therefore an important and potentially overlooked component of soil P, which pedogenically forms in soils with high P, Al, and Ca contents, where it likely plays an important role in P bioavailability. KW - Phosphor KW - XANES spectrosocpy KW - infrared spectroscopy PY - 2025 DO - https://doi.org/10.2139/ssrn.5556609 SP - 1 EP - 31 PB - SRN AN - OPUS4-64739 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Solodov, Dmitry A1 - Nazari, Narges A1 - Gaal, Mate A1 - Kersten, Holger T1 - Exploring the Potential of Plasma Microhollow Cathode Transducers for Air-Coupled Ultrasonic Non-Destructive Testing N2 - This study examines the feasibility of using Microhollow Cathode (MHC) plasma transducers as contactless, broadband sources for air-coupled ultrasonic nondestructive testing (NDT). To improve the detection of small or weakly bonded defects, the approach integrates Local Defect Resonance (LDR), which amplifies flaw responses at their natural vibrational frequencies. T2 - ICU2025 - International Congress on Ultrasonics 2025 CY - Paderborn, Germany DA - 21.09.2025 KW - Microhollow cathodes KW - NDT KW - LDR KW - Air-coupled ultrasound PY - 2025 SP - 1 EP - 4 AN - OPUS4-64738 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rübner, Katrin A1 - Stuff, Maria A1 - Großmann, Karsten A1 - Pniok, Nicole A1 - Dreisow, Bianca T1 - A silica-based protective system modified with rock powder for the preservation of tuff stone N2 - Tuffs are lightweight and porous pyroclastic rocks composed of a volcanic ash matrix containing pumice and rock fragments, quartz, sanidine and other individual crystals, zeolites, and clay minerals. Due to their low density and high porosity, tuff stones are easy to work with and transport. They have been used as construction material in many historical buildings in Germany. However, most tuff stones exhibit poor resistance to weathering due to their morphology and porosity. If the physico-chemical degradation of the stones is already well advanced, ensuring the safety of the buildings often requires extensive stone replacement. However, this contradicts the fundamental principle of conservation, which prioritises the preservation of the original material. In a recently completed research project, a silica-based protective system modified with rock powder was developed for the preservation of tuff stone. Suitable colloidal silica dispersions and modified rock powders customised produced from tuff waste were used. The protective system was optimised to reduce the capillary water absorption of tuff while maintaining its water vapour diffusion properties, to build a durable protective system-tuff bond, and to achieve a visual and tactile resemblance to tuff. The protective system was developed at laboratory scale. It was subsequently applied to a test area at a restoration site in Berlin-Zehlendorf, Germany, to assess its performance under outdoor conditions. By applying the new protective system, the historic building structure is better preserved, tuff stone resources are saved, and tuff waste is effectively recycled. T2 - STONE 2025 - 15th international congess on the deterioration and conservation of stone CY - Paris, France DA - 08.09.2025 KW - Protective system KW - Rock powder KW - Silica sol KW - Stone preservation KW - Tuff stone KW - Tuff waste recycling PY - 2025 SP - 743 EP - 749 AN - OPUS4-64748 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ramge, Peter A1 - Kühne, Hans-Carsten ED - Kusterle, W. T1 - Entwicklung und Modifikation von PCC- und SPCC-Mörteln für die Betoninstandsetzung T1 - Entwicklung und Modifikation von PCC- und SPCC-Mörteln für die Betoninstandsetzung T2 - Spritzbeton - Tagung 2012 CY - Alpbach, Tirol, Austria DA - 12.01.2012 PY - 2012 SP - 1 EP - 18 AN - OPUS4-25389 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Dengiz, Nizamettin A1 - Fuchs, Martin A1 - Gaal, Mate A1 - Gautzsch, Tobias A1 - Herzog, Thomas A1 - Kornely, Mike A1 - Littner, Linus A1 - Marhenke, Torben A1 - Schmid, Simon A1 - Sommerhuber, Ryan A1 - Steinhausen, Ralf A1 - Szewieczek, Artur A1 - Wachter, Luis A1 - Waschkies, Thomas A1 - Wunderl, Stefan ED - Gaal, Mate T1 - Guideline to performing air-coupled ultrasonic testing N2 - The areas of application of air-coupled ultrasonic testing (ACUT) can be very diverse and often differ greatly from the areas of application of classic ultrasonic testing. In fact, ACUT is an independent method that often overlaps with X-ray or thermography or enables tests that cannot yet be reliably performed non-destructively. Although air-coupled ultrasonic testing is not a new technology, it remains a rarely used method compared to other NDT methods. This is not least due to the lack of standards, specialised books and training opportunities for interested inspectors and inspection supervisors. This creates a barrier to entry for many areas of application, which prevents more frequent use. For these reasons, experts from research institutes and industry have decided to set up an "Air-Coupled Ultrasonic Testing" (ACUT) sub-committee as part of the DGZfP's Ultrasonic Testing Technical Committee to work on these topics. It was decided to draw up a guideline to make it easier for interested users to get started with ACUT and to provide assistance with the specification and implementation of such tests. This document is the result of this co-operation. KW - air-coupled ultrasound KW - guideline KW - non-destructive testing PY - 2025 SP - 1 EP - 28 CY - Berlin AN - OPUS4-64847 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gottschalk, Götz-Friedrich A1 - Chaurasia, Prashant Kumar A1 - Goecke, Sven-Frithjof T1 - Zero-defect Printing with DED-GMA via Adaptive Controls N2 - Gas metal arc assisted directed energy deposition (DED-GMA) is a metal additive manufacturing process for fabricating large-scale parts with a higher printing rate. An accurate monitoring and control of the melt pool geometric features is critical for printing zero-defect parts. In this study, the melt pool thermography is used for the real-time detection of the melt pool boundary, centreline, and transient cooling time using an efficient deep learning technique. The presented real-time process monitoring and control methodology using deep learning allows adaptive control of the DED-GMA process. T2 - Twenty-Second International Conference on Flow Dynamics (ICFD 2025) CY - Sendai, Japan DA - 10.11.2025 KW - Additive manufacturing KW - DED-Arc KW - Monitoring KW - Control PY - 2025 SP - 1332 EP - 1335 AN - OPUS4-64837 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wander, Lukas A1 - Paul, Andrea A1 - Rurack, Knut A1 - Biyikal, Mustafa A1 - Juritsch, Elevtheria A1 - Bernstein, Thomas A1 - Bartholmai, Matthias A1 - Noske, Reinhard T1 - Kompaktsensor zur Online-Überwachung von Nitroaromaten N2 - Nitroaromaten und insbesondere Trinitrotoluol (TNT) sind weit verbreitete Spreng- und Umweltschadstoffe. Die größte Herausforderung bei der Detektion von TNT in der Gasphase ist der geringe Dampfdruck. Derzeit werden vielerorts günstige, schnelle, handliche und einfach zu bedienende Alternativen zur klassischen TNT-Analytik entwickelt. Aktuell existieren keine einheitlichen Richtlinien für Sprengstoffsensoren. Hier wird die Entwicklung eines Messplatzes zur Validierung von Sprengstoffsensoren sowie die Erprobung eines kompakten Mustersensors vorgestellt. T2 - 12. Kolloquium Prozessanalytik CY - Berlin, Germany DA - 28.11.2016 KW - Nitroaromaten KW - Fluoreszenzlöschung KW - Sensor PY - 2016 SP - P11, 61 EP - 62 AN - OPUS4-38402 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Akyel, Fatma A1 - Gook, Sergej A1 - Üstündag, Ömer A1 - Bakir, Nasim A1 - Brunner-Schwer, Christian A1 - Rethmeier, Michael T1 - Hochleistungs-Lichtbogenschweißen von dicken Stahlblechen mit elekt-romagnetischer Schweißbadunterstützung N2 - Das Unterpulverschweißen (UP) ist das Lichtbogenschweißverfahren mit der höchsten Abschmelzrate. Beim Schweißen von dicken Blechen ist dieses Verfahren jedoch besonders für die Wurzellage von Nachteil. Voll-ständiges Umschmelzen ohne extremen Wurzeldurchhang oder ein Austropfen der Schmelze ist ohne weitere Hilfsmittel schwer zu erreichen. Aus diesem Grund werden Pulver-, Kupfer-, keramische Badstützen oder Ble-che zur Vermeidung des Wurzeldurchhangs verwendet. Bei der Verwendung von Kupfer- oder Keramikstützen beeinflusst beispielsweise die Diffusion chemischer Elemente in die Schweiß- oder Schmelzlinie die mecha-nischen Eigenschaften der Schweißnaht. All diese Badstützen erfordern zusätzliche Schritte zur Vorbereitung und Entfernung sowie zur Reinigung der Schweißwurzel. Die Verwendung einer elektromagnetischen Bad-stütze hat dagegen viele Vorteile. Der Magnet kommt nicht mit dem Werkstück in Kontakt, sodass ein zusätz-licher Schritt des Entfernens nicht erforderlich ist. Versuche mit Laserstrahlschweißen oder Laserhybrid-schweißen haben bereits erstmalig gezeigt, dass Blechdicken bis 30 mm einlagig einseitig geschweißt werden können und zusätzlich ein Spalt oder Kanterversatz von bis zu 2 mm überbrückt werden können. In dieser Arbeit wird die elektromagnetische Badstütze für den UP-Prozess eingesetzt. Die Wurzellage wird an 15 mm dicken Blechen mit einer Spaltgröße von 2 mm geschweißt. Die Verwendung eines elektromagnetischen Sys-tems stellt hier sicher, dass die Schmelze nach oben gedrückt und in Position gehalten wird. Ferner kann die Schweißtiefe entsprechend den magnetischen Parametern angepasst werden. Dieses Verfahren kann die Produktivität im Schweißbereich von vielen Betrieben deutlich steigern und Kosten gleichzeitig senken und kann dazu beitragen, diese Arbeitsplätze in Deutschland zu sichern. T2 - DVS CONGRESS 2024 Große Schweißtechnische Tagung CY - Erfurt, Germany DA - 16.09.2024 KW - Unterpulverschweißen KW - Hochleistungs-Lichtbogenschweißen PY - 2024 SN - 978-3-96144-269-0 VL - 395 SP - 134 PB - DVS Media CY - Düsseldorf AN - OPUS4-61613 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Cornelsen Sampaio Kling, I. A1 - Pauw, Brian Richard A1 - Agudo Jácome, Leonardo A1 - Archanjo, B. S. A1 - Simão, R. A. T1 - Development and characterization of starch film and the incorporation of silver nanoparticles N2 - Starch is one of the biopolymers being used for bioplastic synthesis. For production, starch can be combined with different plasticizers, starches from different plant sources and even with nanomaterials to improve or to add film properties. The challenge of adding these, e.g. in the form of silver nanoparticles (AgNp) is to determine the concentration so as to avoid impairing the properties of the film, agglomeration or altering the visual characteristics of the film. In this study, a starch film synthesis route and the incorporation of silver nanoparticles has been proposed in order not to alter the properties of the film while maintaining the transparency and a clear colour of the starch film. The results showed that the proposed synthesis route is promising, efficient, reproducible, fast and the film has good mechanical properties. T2 - Semana MetalMat & Painal PEMM 2020 CY - Online meeting DA - 23.11.2020 KW - Biofilm KW - Silver nanoparticle KW - Starch KW - Starch nanoparticle PY - 2020 SP - 1 EP - 2 AN - OPUS4-51940 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neugum, Tim A1 - Stelzner, Ludwig A1 - Häßler, Dustin A1 - Zehfuß, Jochen A1 - Hothan, Sascha T1 - Application of the substructure method to assess the fire resistance of thermally restrained columns N2 - Usually, the fire resistance of load-bearing structural elements is determined by single members testing. A mechanical load is applied to the member in a force-controlled manner and is maintained constant throughout the fire test. After applying the mechanical load, the thermal exposure starts according to the ISO 834 fire curve. In this conventional test method, no interaction between the tested member and the entire building structure is considered. In buildings, the surrounding structure can restrain the thermal expansion of a member in case of fire. This may have both positive and negative effects on the fire resistance of this structural element. Several years ago, the Institute for Sustainability and Innovation in Structural Engineering (ISISE) at the University of Coimbra in Portugal and the Bundesanstalt für Materialforschung und prüfung (BAM) in Germany carried out fire tests on circular and square steel-reinforced concrete columns with restrained thermal expansion. BAM´s column test furnace allows the specimen to be subjected to thermal exposure and mechanical loading simultaneously. In addition, this device has a substructure test module, which can also provide restrained test conditions. In an ongoing research project at BAM and Technische Universität Braunschweig, the effect of restrained test conditions on the behaviour of steel-reinforced columns under fire exposure is further investigated. T2 - 8th International RILEM Workshop on Concrete Behaviour due to Fire Exposure CY - Krakow, Poland DA - 18.09.2025 KW - Substructure method KW - Surrounding structure KW - Fire resistance KW - Restrained columns KW - Concrete PY - 2025 SP - 1 EP - 2 AN - OPUS4-64582 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Nowatzky, Yannek T1 - Fiora: Source Data for Training and Testing N2 - This repository contains source data for training and testing the Fiora model (see GitHub and DOI: 10.5281/zenodo.14651774). As part of the Fiora study (Nowatzky et al., 2025), which introduces a GNN-based fragmentation algorithm for simulating MS/MS spectra, this dataset enables the reproduction of the study’s findings and the training of new spectral prediction models. KW - Bioinformatics KW - Mass spectrometry KW - Machine Learning PY - 2025 DO - https://doi.org/10.5281/zenodo.14782249 PB - Zenodo CY - Geneva AN - OPUS4-64587 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eiz Eddin, Ahmad A1 - Merz, P. A1 - Dombrowski, M. A1 - Loutfi, J. A1 - Zeitler, B. T1 - Building acoustic analysis of doubly curved beam-like shell floors made of CFRP prestressed concrete and its integration into an interdisciplinary optimisation tool N2 - An optimisation tool was developed to reduce the embodied carbon of floor systems. The considered system consists of a doubly curved beam-like shell made of carbon-fibre-reinforced polymer (CFRP) prestressed concrete and an infill layer. The thin-walled design of the system makes it susceptible to sound excitation. Therefore, the optimisation tool considers the static ultimate and serviceability limit states and the sound insulation aspect. Due to a lack of experience with the building acoustic properties of this floor system, it is, in practice, often simplified as a homogeneous floor. This paper aims to investigate its acoustic behaviour in more detail using numerical simulations and to integrate the gained knowledge into the optimisation tool. For this purpose, a simulation concept is set up and implemented. Simulations are carried out for different combinations of geometry and material parameters of the floor system. The data obtained is summarised into linear regression equations that estimate the weighted airborne sound reduction index and the weighted equivalent normalised impact sound pressure level of the system. The optimisation results based on these equations show a clear difference compared to those based on the above-mentioned simplified approach. T2 - IASS 2024 Annual Symposium: Redefining the Art of Structural Design CY - Zurich, Switzerland DA - 26.08.2024 KW - Building acoustic simulation KW - Impact sound pressure level KW - Airborne sound reduction index KW - Doubly curved beam-like shells KW - CFRP KW - Interdisciplinary optimisation PY - 2024 SP - 2752 EP - 2761 PB - International Association for Shell and Spatial Structures (IASS) CY - Zürich, Schweiz AN - OPUS4-63089 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Witt, Jens A1 - Schukar, Marcus A1 - Breithaupt, Mathias A1 - Müller, Bernd R. A1 - Krebber, Katerina T1 - MPOF LPGs as radiation sensors N2 - We investigated to our knowledge for the first time the capabilities of long period gratings (LPG) in single-mode microstructured polymer optical fibre (mPOF) as real-time gamma dosimeter. The fibre is made from polymethyl methacrylate (PMMA) with a polycarbonate jacket. We measured the radiation-induced wavelength shift of the mPOF LPG loss feature wavelength and the radiation-induced attenuation of a mPOF for different wavelength between 600 nm and 800 nm for gamma radiation with an energy distribution between 6 keV and 18 keV. T2 - POF 2011 - 20th International conference on plastic optical fibers CY - Bilbao, Spain DA - 14.09.2011 KW - Microstructured polymer optical fibre (mPOF) KW - Long period grating (LPG) KW - Radiation sensor PY - 2011 SP - 1 EP - 3 AN - OPUS4-24499 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lange, Axel A1 - Hentschel, Manfred P. A1 - Kupsch, Andreas T1 - True 3D-CT-reconstruction in comparison to the FDK-algorithm T2 - 17th World Conference on Non-Destructive Testing CY - Shanghai, China DA - 2008-10-25 KW - Computed tomography KW - Spatial resolution KW - Reconstruction algorithm PY - 2008 SP - 1 EP - 5 PB - International Committee for Non-Destructive Testing CY - Shanghai AN - OPUS4-18568 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Bernd R. A1 - Soares, A.P. A1 - Kupsch, Andreas A1 - Baum, D. A1 - Hesse, B. A1 - Zaslansky, P. T1 - Untersuchung der Integrität von glasfaserverstärkten Zahnstiften mittels Synchrotron-Röntgenrefraktion N2 - Die Integrität der Verstärkungsfasern in Komposit-Zahnstiften ist entscheidend für die Biegefestigkeit und die langfristige Haftung am Zement in den Wurzelkanälen. Es wurde vermutet, dass die Integrität von glasfaserverstärkten Zahnstiften durch das Beschleifen während der zahnmedizinischen Behandlung beeinträchtigt wird. Eine Beschädigung der Fasern führt zu einer erheblichen strukturellen Schwächung über den gesamten Stiftdurchmesser. Glasfragmente, die durch den Kontakt mit dem Zahnbohrer entstehen, können sich vom Stift lösen und die Haftfähigkeit erheblich verringern. Mit Hilfe hochauflösender Synchrotron-Röntgen-Refraktions-Radiographie (SXRR) konnte das Ausmaß der Schäden zuverlässig identifiziert und charakterisiert werden. Dazu wurden die Glasfaserstifte sowohl im Herstellungszustand als auch nach der Bearbeitung mit einem Diamantbohrer untersucht. Die Datensätze wurden zur Visualisierung und Quantifizierung der morphologischen Charakteristika intakter und durch das Beschleifen beschädigter Regionen analysiert. Sie zeigen Schäden im bearbeiteten Bereich (z. B. Brüche, Splitter und Risse) sowie herstellungsbedingte Inhomogenitäten der Fasern mit einer signifikanten Zunahme der inneren Oberflächen in Probenregionen, die durch das Beschleifen beschädigt wurden. T2 - DGZfP Jahrestagung 2022 CY - Kassel, Germany DA - 23.05.2022 KW - Röntgen-Refraktion KW - Verbundwerkstoffe KW - Zahnstifte PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-549231 SP - 1 EP - 7 AN - OPUS4-54923 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Trappe, Volker A1 - Nielow, D. A1 - Hickmann, Stefan A1 - Kupsch, Andreas A1 - Gaal, Mate A1 - Redmer, Bernhard A1 - Krankenhagen, Rainer T1 - Sandwich-Schalenstrukturen in situ charakterisiert mit Thermographie und Felddehnungsmessungen N2 - An der BAM wurde ein Schalenprüfstand entwickelt, mit dem typische Sandwichschalenstrukturen unter simulierter Betriebsbeanspruchung belastet werden können. Im mechanischen Ermüdungsversuch wurden in situ die Entstehung von Schäden in Schalenprüfkörpern mit Test-Imperfektionen mittels der passiven Thermographie und Felddehnungsmessungen verfolgt. Damit konnten der Zeitpunkt, der Schadensursprung und der Schadensfortschritt zerstörungsfrei bestimmt werden. Zudem wurden vergleichend Schalenprüfkörper mit Luftultraschall und der Röntgen-Laminographie untersucht. Im Rahmen eines BMWi-Forschungsvorhabens wurden die Schädigungsmechanismen evaluiert und Empfehlungen für die Praxis der Fertigung von Rotorblättern abgeleitet. In diesem Beitrag wird sich auf die Darstellung der ZfP-Verfahren und der ZfP-Ergebnisse konzentriert. T2 - DGZfP-Jahrestagung 2018 CY - Leipzig, Germany DA - 07.05.2018 KW - Windkraft KW - Rotorblatt KW - Schalenprüfstand KW - Thermographie KW - Laminographie KW - Luftultraschall PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-469395 VL - 166 SP - 1 EP - 11 AN - OPUS4-46939 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Bernd R. A1 - Lange, Axel A1 - Harwardt, Marco A1 - Hentschel, Manfred P. A1 - Illerhaus, Bernhard A1 - Goebbels, Jürgen T1 - Synchrotron Refraction CT and Synchrotron Bragg Magnification CT for NDE T2 - International Symposium on Digital industrial Radiology and Computed Tomography (DIR 2007) CY - Lyon, France DA - 2007-06-25 KW - X-ray Refraction KW - Diffraction Enhanced Imaging (DEI) KW - Bragg Magnification KW - Synchrotron Radiation KW - Computed Tomography (CT) KW - Metal Matrix Composites (MMC) KW - Lightweight Materials KW - Aerospace PY - 2007 IS - CD-ROM SP - 1 EP - 8 CY - Lyon, France AN - OPUS4-16366 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ewers, Benjamin A1 - Kupsch, Andreas A1 - Lange, Axel A1 - Hentschel, Manfred P. T1 - Terahertz spectral imaging techniques in NDT: Topography and computed tomography N2 - The emerging technology of generation and detection of Terahertz waves (1 THz = 1012 Hz) offers diverse potentials in non-destructive testing (NDT) regarding security as well as safety aspects. Herein, we focus on the latter with emphasis on imaging techniques. The THz range (0.1 … 10 THz, 3mm …30 µm) closes the technological gap between ultra high frequency electronics and FIR optics in the electro-magnetic (EM) spectrum. Electro-optical sampling provides straight access to the EM wave including its phase (rather than intensity). THz waves are well suited to characterize non-metallic materials since they penetrate paper, plastics, ceramics and certain composites (e.g. GFC). We employ a commercial fibre-coupled THz time domain spectrometer (TDS) for scanning the samples laterally through a focal spot. At each position the entire temporal pulse train is recorded, which offers the opportunity to use various parameters derivable for imaging. Topographic measurements are performed as reflection set-up. The achievable spatial resolution is diffraction limited at about 100 µm -300 µm (which allows for perception of single defects on a sub-mm scale). In contrast to typical pulse echoed ultrasound testing THz topography is a non-contact inspection tool without coupling agents. Several reflections of subsequent concealed layers are detected instead of just the first encountered one. Comparing to X-ray (radiology) the non-ionizing THz-waves generate images of similar contrast regarding metal and plastic (organic) components, while conventional radiography emphasizes one type of material depending on the energy preselected. Moreover, the full temporal information is exploited to derive spectra in certain selected time windows, i.e. separated spectral properties of each layer in multilayered structures. Tomographic measurements are performed in transmission mode. The sample is mounted on a rotation stage in order to allow for lateral scanning under the different projection angles. The reconstruction is typically performed by filtered backprojection, which is widely used for X-ray CT. The adaption of this technique to the THz range comes along with several experimental drawbacks such as considerable refraction and scattering. According to these difficulties we investigate the occurring artefacts. The THz-TDS provides the opportunity to calculate a separate backprojection of each frequency interval as obtained by the Fourier transformation of the recorded time resolved amplitude. This results in a spectrally resolved reconstruction of each voxel, which is unique in computed tomography technology. T2 - 10th European conference on non-destructive testing CY - Moscow, Russia DA - 2010-06-07 KW - Terahertz time domain spectroscopy KW - Spectral computed tomography KW - 3D topography PY - 2010 UR - http://www.ndt.net/article/ecndt2010/reports/1_09_10.pdf IS - Paper 4.02.18 SP - 1 EP - 10(?) AN - OPUS4-21465 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Teutenberg, Thorsten A1 - Blöth, Anton A1 - Bolling, Janina A1 - Kuch, Susanne A1 - Meyer, Lena A1 - Rösch, Richard T1 - Auf dem Weg in die digitale Transformation N2 - Die Digitalisierung in der Laborbranche stellt eine komplexe Herausforderung dar – nicht zuletzt aufgrund zahlreicher Einzelprojekte und vieler proprietärer Insellösungen. Um eine konsequente und wirkungsvolle Labordigitalisierung und Prozessautomatisierung zu erreichen, braucht es eine übergreifende Sichtbarkeit und Vernetzung bestehender Initiativen. Diese Notwendigkeit haben verschiedene Akteure der Laborbranche erkannt und, angestoßen durch die Initiative QI-Digital, den Digital LabHub ins Leben gerufen. Ziel ist es, eine Plattform für Wissensaustausch und -transfer, gegenseitige Unterstützung und praxisnahe Umsetzung zu schaffen – offen für Labore aller Branchen und Anwendungsfelder. Der Digital LabHub soll gezielte Hilfestellung beim Einstieg in die Digitalisierung bieten, Labore zukunftssicher aufstellen und dabei helfen, regulatorische Anforderungen zu erfüllen. KW - Digitale Transformation KW - Digitalisierung KW - Kalibrierlabor KW - Prüflabor KW - QI-Digital KW - Qualitätsinfrastruktur PY - 2025 UR - https://analyticalscience.wiley.com/content/article-do/auf-dem-weg-die-digitale-transformation SP - 1 EP - 3 PB - Wiley Analytical Science CY - Weinheim AN - OPUS4-64482 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gaal, Mate A1 - Ahmadzadeh, Majid A1 - Weise, Matthias T1 - Air-coupled ultrasonic transmission using thermoacoustic transmitters and optical microphones N2 - Background, Motivation and Objective Air-coupled ultrasonic transducers are usually applied for testing of some lightweight components. To increase the bandwidth or air-coupled testing systems and thus increase their application range, thermoacoustic transducers can be paired with optical microphones in a transmission mode. Thermoacoustic transmitters are based on the thermal excitation of sound waves, while optical microphones are based on laser interferometry and Fabri-Pérot etalon. We studied the spectrum and the efficiency of the transmission of an air gap using a thermoacoustic transmitter and an optical microphone. Statement of Contribution/Methods Thermoacoustic transmitters with an electrically conductive layer of indium tin oxide (ITO) on a curved quartz glass substrate were developed. Their sound field was measured using a commercially available optical microphone Eta450 Ultra based on Fabri-Perot etalon. The curvature and the conductive layer thickness of the thermoacoustic transmitter were systematically varied to investigate their impact on the sound field and the spectrum of the measured signal for frequencies up to 1 MHz. The transmitters were excited using rectangular burst signals with a varied width. We examined the influence of all parameters on the focusing, spectrum, and sensitivity. The directivity of the microphone was evaluated as well. Results/Discussion The focusing of the sound fields of all transmitters most strongly depends on the curvature radius of the substrate. The spectrum recorded in the focus of each transducer has several maxima and minima, as shown in the left-hand diagram, which are mostly a consequence of the irregularities of the microphone spectrum. These irregularities are visible also in the directivity diagram on the right, which was recorded by rotating the microphone. The 20 dB bandwidth of the measurement system covers the range up to about 1 MHz, depending strongly on the width of the excitation pulse (left-hand diagram). This highlights a key advantage of thermoacoustic transmitters: their spectral characteristics can be controlled through the excitation conditions, offering a potentially broader range of applications compared to conventional air-coupled transmitters. One promising example is localized ultrasound spectroscopy based on the detection of local resonances. T2 - IEEE International Ultrasonic Symposium CY - Utrecht, The Netherlands DA - 15.09.2025 KW - Air-coupled ultrasound KW - Thermoacoustic transmitter KW - Sound field PY - 2025 SP - 1 EP - 4 AN - OPUS4-64541 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Li, Yong A1 - Hu, Kaixiong A1 - Lilleodden, Erica T. A1 - Huber, Norbert T1 - Datasets for structural and mechanical properties of nanoporous networks from FIB reconstruction N2 - This dataset includes 3D tomographic reconstruction image files, volume mesh files for finite element simulations, and data on the structural and mechanical properties of nanoporous gold (NPG) structures. It serves as a supplement to a dataset paper, with the corresponding DOI provided in the “Related Identifiers” section. Detailed descriptions of the data, as well as the procedures for their preparation and curation, are presented in that paper. The base material, nanoporous gold, was fabricated via a dealloying process and has a solid fraction of approximately 0.30. NPG samples with ligament sizes ranging from 20 nm to 400 nm were prepared through dealloying and subsequent thermal annealing. Tomographic TIFF files were obtained via Focused Ion Beam/Scanning Electron Microscopy (FIB/SEM) 3D reconstruction, with the procedure detailed in Philosophical Magazine (2016, 96(32–34), 3322–3335). Based on the 3D image data, new simulations and analyses were performed. The resulting structural and mechanical property data of nanoporous gold are reported for the first time in the dataset paper and are archived here. This dataset provides a valuable database for the study of nanoporous network materials and can be reused for numerical simulations, additive manufacturing, and machine learning applications within the materials science community. KW - Nanoporous gold KW - Dealloying KW - Coarsening KW - FIB/SEM tomography KW - Connectivity KW - Finite element KW - Volume mesh KW - Young’s modulus KW - Yield stress KW - Poisson’s ratio PY - 2025 DO - https://doi.org/10.15480/882.15230 PB - Technische Universität Hamburg Open Research CY - Hamburg AN - OPUS4-64534 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - An, Biwen Annie A1 - Kunte, Hans-Jörg A1 - Koerdt, Andrea ED - Eibergen, N. ED - Poulassichidis, T. T1 - Microbiologically Influenced Corrosion (MIC) by Halophilic (Salt-Loving) Nitrate and Sulfate-Reducing Microorganisms N2 - The survey of Canadian shale sites showed a dominance of halophilic microorganisms, including Halomonas (HA). Nitrate-amended incubations of the field samples under high salinity (14.6% NaCl), revealed a dominance of HA (>72%) and an accumulation of nitrite. Nitrite accumulation directly inhibited the growth of SRB, thereby decreasing their souring and corrosion risks. However, accumulated nitrite may also contribute to iron corrosion, which will be tested by using different concentrations of nitrate as an electron acceptor to HA. Different salinities are further tested on HA strains supplemented with iron coupons to determine their effects on iron corrosion rates. HA incubated with separate cultures of corrosive methanogen and SRB were tested to determine whether a positive or adverse effect will occur between them. Lastly, analyses of iron coupons will be conducted using TOF-SIMS, FIB-SEM and EDS for corrosion product characterization T2 - Corrosion 2021 CY - Online Meeting DA - 19.04.2021 KW - MIC KW - Bacteria KW - Halophile KW - Corrosion KW - Environmental condition KW - Korrosion KW - High salinity PY - 2021 UR - https://my.nace.org/PaperTrail/Authors/Submission.aspx?id=2914f145-7f8f-ea11-813a-005056a95a7c SP - Paper C2021-16284, 1 AN - OPUS4-52479 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Lecompagnon, Julien T1 - Thermographic Reference Dataset: Experimentally simulated Gaussian-shaped internal defects in GFRP N2 - We introduce a thermographic reference dataset consisting of 100 experimentally recorded temperature fields that replicate defect-like heat signatures in glass fiber reinforced polymer (GFRP) composites. Instead of relying on the fabrication of numerous damaged specimens, the dataset was generated by directly imprinting defect signatures onto an intact laminate using a near-infrared laser projector with spatial light modulation. The projected patterns are derived from parameterized Gaussian distributions, enabling systematic variation in defect size, shape, and orientation. The resulting steady-state thermal responses were captured with infrared thermography, providing high-resolution temperature distribution measurements for each case. This novel approach ensures that the heat transfer physics are preserved experimentally, while no special samples with different defects need to be manufactured to acquire datasets for different defect parameters. The dataset is ultimately designed as a resource for the benchmarking of thermographic non-destructive testing techniques, the validation of numerical heat transfer simulations, and the training of data-driven algorithms for defect detection in composite materials. KW - Thermography KW - Temperature KW - Composites KW - GFRP KW - Reference Data KW - Laser Projector KW - Nondestructive Testing PY - 2025 DO - https://doi.org/10.5281/zenodo.17378681 PB - Zenodo CY - Geneva AN - OPUS4-64472 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koerdt, Andrea A1 - An, Biwen Annie A1 - Deland, Eric ED - Eibergen, N. ED - Poulassichidis, T. T1 - Novel Multiport Flow-Column Corrosion Monitoring System (MFC) Revealed High Corrosion Rates by Corrosive Methanogenic Archaea N2 - MFC was used to study the corrosiveness of iron-utilizing methanogen, Methanobacterium IM1 under flow conditions. Comparing against electrical SRM, Desulfovibrio ferrophilus IS5, results showed under standard mesophilic conditions, average corrosion rates of Methanobacterium IM1 was double that of SRM. The highest corrosion rate of Methanobacterium IM1 reached up to 0.60 mm/yr under neutral conditions, and severe pitting was observed on the iron surface. Furthermore, the corrosion products of Methanobacterium IM1 were characterized with TOF-SIM, FIB-SEM and EDX, and preliminary results revealed FeCO3 is not the only corrosion product of Mi-MIC, as previously reported. Under low pH conditions, the maximum corrosion rate of Methanobacterium IM1 reached 1.57 mm/yr, which resulted in severed deformity of the iron specimen. Additional comparisons using different types of incubation material were conducted to standardize MFC MIC testing. T2 - Corrosion 2021 CY - Online Meeting DA - 19.04.2021 KW - MIC KW - Microbiologically influenced corrosion KW - Biocorrosion KW - Hi-Tension KW - Environmental condition KW - Flow Model KW - Modelling KW - Korrosion PY - 2021 UR - https://my.nace.org/PaperTrail/Authors/Submission.aspx?id=2b6387be-7390-ea11-813a-005056a95a7c SP - Paper C2021-16303, 1 AN - OPUS4-52480 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neugum, Tim A1 - Stelzner, Ludwig A1 - Häßler, Dustin A1 - Zehfuß, Jochen A1 - Hothan, Sascha T1 - Berücksichtigung der Tragwerksumgebung bei Brandversuchen an Stahlbetonstützen N2 - Das Tragwerk eines Gebäudes ist aus einzelnen Bauteilen zusammengesetzt. Insbesondere bei lokalen Brandereignissen bauen sich durch die Ausdehnung der vom Brand betroffenen Bauteile gegen das umgebende kältere Gesamttragwerk Zwangsbeanspruchungen auf. Bei konventionellen Brandprüfungen werden diese Zwangsbeanspruchungen in der Regel nicht berücksichtigt, da die Prüfsystematik auf Einzelbauteilprüfungen bei konstanter mechanischer Last ausgelegt ist. Die Prüfung komplexer, realmaßstäblicher Tragwerke ist oftmals nicht möglich. Die Interaktion des Einzelbauteils mit dem umgebenden Tragwerk kann sich sowohl positiv als auch negativ auf den Feuerwiderstand auswirken. Als nachteilig ist der thermische Zwang und die daraus resultierende Lasterhöhung zu nennen. Gleichzeitig kann eine Stauchung der Stütze zu einer Umlagerung von Kräften in das umgebende Tragwerk führen und damit den Versagenszeitpunkt der Stütze verzögern. Mit Hilfe der Substrukturtechnik kann das Verhalten einer Stütze im Brandfall unter Berücksichtigung der Interaktion mit dem umgebenden Tragwerk analysiert werden. In einem gemeinsamen DFG-Vorhaben der Bundesanstalt für Materialforschung und -prüfung (BAM) und dem Institut für Baustoffe, Massivbau und Brandschutz (iBMB) der TU Braunschweig werden 14 Stahlbetonstützen mit freier und behinderter axialer Ausdehnung untersucht. Auf Basis eines realen Gebäudes werden unter anderem die Steifigkeit, welche das umgebende Tragwerk repräsentiert, der Lastausnutzungsgrad und die Brandeinwirkung variiert. Mit dem Ziel das Stützenverhalten unter thermischem Zwang im Detail zu analysieren, erfolgen Brandversuche und numerische Simulationsberechnungen. Dabei werden die erforderlichen mechanischen Materialeigenschaften des Betons bei erhöhten Temperaturen aus experimentellen Daten abgeleitet. Der Beitrag liefert einen Einblick in die experimentellen und numerischen Ergebnisse. Es zeigt sich, dass die behinderte axiale Ausdehnung und die Möglichkeit einer Lastumlagerung bei Stauchung der Stütze einen erheblichen Einfluss auf das Versagen im Brandfall haben. Die mittels Substrukturtechnik erzeugte Zwängung des umgebenden Tagwerks führt zu einem Anstieg der Axialkraft in der Stütze sowie einer Abnahme der maximalen Stützenausdehnung. Gleichzeitig setzt die Stauchung der Stütze früher ein. Wird eine Stütze-Tragwerk-Interaktion auch für den Stauchungsbereich der Stütze angesetzt, kann der Vorteil einer Lastumlagerung genutzt werden. Somit kann trotz einer höheren mechanischen Belastung während der Ausdehnungsphase der Stütze ein späterer Versagenszeitpunkt als bei einer konventionell geprüften Stütze erreicht werden. T2 - Symposiums Heißbemessung – Structural Fire Engineering 2025 CY - Braunschweig, Germany DA - 29.09.2025 KW - Substrukturtechnik KW - Stahlbetonstützen KW - Feuerwiderstand KW - Stützenbrandversuche KW - Numerik PY - 2025 SP - 38 EP - 52 PB - TU Braunschweig AN - OPUS4-64581 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Resch-Genger, Ute A1 - Maiwald, Michael T1 - Analytical Sciences an der BAM N2 - Die Bundesanstalt für Materialforschung und -prüfung (BAM) ist eine wissenschaftlich technische Bundesoberbehörde im Geschäftsbereich des Bundesministeriums für Wirtschaft und Energie (BMWi), die über einen gesetzlichen Auftrag für die Sicherheit in Technik und Chemie verfügt und auf nahezu 150 Jahre zurückblicken kann. Vor diesem Hintergrund forscht, entwickelt, und prüft die BAM in den fünf Themenfeldern Energie, Infrastruktur, Umwelt, Material und Analytical Sciences mit einer unikalen Vielfalt an analytischen Methoden. KW - BAM KW - Analytik KW - Analytical Sciences PY - 2016 SN - 0939-0065 IS - 2 SP - 6 EP - 8 AN - OPUS4-36508 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Steiger, Martina A1 - Pfeifer, Dietmar A1 - Pilz, Walter A1 - Spieles, Monika A1 - Resch-Genger, Ute A1 - Fischer, F. T1 - Traceable Characterization of Fluorometers T2 - 10th Sensor 2001 Conference ; 10. Sensor 2001 Kongress CY - Nuremberg, Germany DA - 2001-05-08 KW - Fluorometrie KW - Rückführbarkeit KW - Fluoreszenzstandards KW - Radiometrische Terminologie PY - 2001 PB - AMA Service GmbH CY - Wunstorf AN - OPUS4-992 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Koch, Matthias A1 - Neuhof, Torsten A1 - Nehls, Irene ED - Jörg Peter Matthes, ED - Markus Frasch, ED - Marx, Wolfram ED - Johannes Oeler, T1 - Lebensmittelanalytik - Neue Referenzmaterialien KW - Referenzmaterialien KW - Acrylamid KW - Ochratoxin A KW - Methylquecksilber PY - 2007 VL - 3 IS - 5 SP - 16 EP - 17 PB - Succidia Verl. & Kommunikation CY - Darmstadt AN - OPUS4-16691 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Koch, Matthias T1 - Entwicklung und Vergleich von Analysenmethoden zur Bestimmung von Mineralölkohlenwasserstoffen in Wasser und in Böden PY - 1999 SP - 1 EP - 154 CY - Berlin AN - OPUS4-7042 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koch, Matthias T1 - Stand der Normung - Bestimmung von Mineralölkohlenwasserstoffen (MKW) mittels GC-FID in verschiedenen Matrices (Wasser, Boden, Abfall) T2 - DGMK-Analytikertreffen 2000 CY - Hamburg, Deutschland DA - 2000-11-13 PY - 2000 CY - Hamburg AN - OPUS4-1031 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rurack, Knut A1 - Unger, Brita A1 - Müller, Ralf A1 - Jancke, Harald A1 - Resch-Genger, Ute T1 - Die Strukturentwicklung von SiO2 Solen und Gelen im Vergleich mikroskopischer und makroskopischer Untersuchungsmethoden T2 - 77. Glastechnische Tagung CY - Leipzig, Deutschland DA - 2003-05-26 PY - 2003 VL - 77 SP - 101 EP - 104 PB - DGG CY - Offenbach AN - OPUS4-3121 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Radunz, Sebastian T1 - Upconverting nanoparticle based assays and sensor systems for bacteria/biofilm detection N2 - Results of the short term scientific mission of Sebastian Radunz funded by the european upconversion network. T2 - Short term scientific mission CY - Turku, Finland DA - 09.01.2017 KW - Upconverting nanoparticles KW - Assays PY - 2017 AN - OPUS4-39328 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rurack, Knut A1 - Bricks, J. L. A1 - Slominskii, J. L. A1 - Resch-Genger, Ute ED - Dähne, S. T1 - Long wavelength emitting fluorescence probes for metal ions T2 - NATO Advanced Research Workshop on Syntheses, Optical Properties and Applications of Near-Infrared (NIR) Dyes in High Technology Fields CY - Trest', Czech Republic DA - 1997-09-24 PY - 1998 IS - 52 SP - 191 EP - 200 PB - Kluwer CY - Dordrecht AN - OPUS4-2097 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Scholtz, Lena A1 - Resch-Genger, Ute T1 - Behind the Paper - Dual color pH probes made from silica and polystyrene nanoparticles and their performance in cell studies N2 - In this contribution we highlight the importance of comparison for scientific research while developing a new, functional pH sensor system, and the valuable insights this can provide. KW - Dye KW - Optical Spectroscopy KW - pH probe KW - Silica and Polystyrene Particles KW - Nano KW - Surface groups KW - Safe-by-Design KW - Cell studies KW - Sensors KW - Particle Synthesis KW - Fluorescence PY - 2023 UR - https://communities.springernature.com/posts/dual-color-ph-probes-made-from-silica-and-polystyrene-nanoparticles-and-their-performance-in-cell-studies SP - 1 EP - 2 PB - Springer Nature CY - London AN - OPUS4-59150 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Tschiche, Harald T1 - A Polymeric Nanosensor for Sensing of Broad pH Changes in Biofilm as Tool for the Investigation of Microbial Induced Corrosion N2 - One of today’s major problems in many technical plants as well as fuel tanks is Microbial induced corrosion (MIC), leading to considerable damage and huge financial losses. Successful prevention of MIC requires the localization of first signs of corrosion as well as the identification of factors influencing the corrosion process. Hence, there is a growing need for sensitive and preferably inexpensive tools that enable the early detection of MIC. Of utmost importance are methods, which provide spatially and time-resolved information and allow the determination of corrosion rates at sites of interest for possible prevention of MIC. T2 - First European / 10th German BioSensor Symposium CY - Potsdam, Germany DA - 20.03.2017 KW - Nanoparticel based pH-probes KW - Microbial induced corrosion KW - Imaging PY - 2017 AN - OPUS4-40261 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Lisec, Jan A1 - Sommerfeld, Thomas A1 - Riedel, Juliane A1 - Mauch, Tatjana A1 - Koch, Matthias T1 - CRM BAM-B003 eCerto data file N2 - Data file (RData) containing measurement data recorded during the production process of the Certified Reference Material BAM-B003 containing per- and polyfluoroalkyl substances (PFAS) in textiles. The data can be most conveniently openend using the Shiny-App eCerto which is accessible at https://www.bam.de/eCerto. KW - Certified reference material KW - Mass spectrometry KW - PFAS PY - 2025 DO - https://doi.org/10.5281/zenodo.15907581 PB - Zenodo CY - Geneva AN - OPUS4-64544 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schackmann, Oliver A1 - Márquez Reyes, Octavio A1 - Memmolo, Vittorio A1 - Lozano, Daniel A1 - Prager, Jens A1 - Moll, Jochen A1 - Kraemer, Peter T1 - Intelligent damage detection in composite pressure vessels under varying environmental and operational conditions N2 - Despite proven approaches available in the literature, structural health monitoring by ultrasonic guided waves under varying environmental and operational conditions is still challenging. The use of machine learning approaches is discussed in this work, considering the complex problem of experimental damage detection under varying load conditions in a composite overwrapped pressure vessel for hydrogen storage. Specifically, unsupervised methods originally developed for image and time series classification are combined with ensemble voting to conceive reliable damage detection technique. This enables the effective combination of the predictions of multiple transducer pairs, even with a limited number of strong individual classifiers. A performance demonstration of the technique is presented using a real damage scenario dataset. T2 - IEEE 12th International Workshop on Metrology for AeroSpace (MetroAeroSpace) CY - Napoli, Italy DA - 18.06.2025 KW - Guided ultrasonic waves KW - Structural health monitoring KW - Artificial intelligence KW - Hydrogen storage PY - 2025 SN - 979-8-3315-0152-5 DO - https://doi.org/10.1109/MetroAeroSpace64938.2025.11114628 SN - 2575-7490 SP - 608 EP - 613 AN - OPUS4-64894 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eiz Eddin, Ahmad A1 - Stelzner, Ludwig A1 - Häßler, Dustin A1 - Hothan, Sascha T1 - Tragfähigkeit und Abplatzverhalten von Carbonbeton bei hohen Temperaturen N2 - Zur Bewertung der Biegetragfähigkeit dünnwandiger, carbonbewehrter Betonbauteile unter Temperatureinfluss wurden 4-Punkt-Biegeversuche in drei thermischen Konfigurationen durchgeführt. Die Ergebnisse zeigen, dass bei Raumtemperatur kein signifikanter Einfluss der Vorspannung auf die Bruchkraft vorliegt. Mit steigender Temperatur nimmt die Biegetragfähigkeit infolge des Festigkeitsverlustes von Beton und Carbonbewehrung sowie durch das Schmelzen der Tränkungsmatrix deutlich ab. Zwei Versagensmechanismen konnten identifiziert werden, d.h. Zugversagen bei hoher Vorspannung und Verbundversagen bei niedriger Vorspannung. Die Abnahme der Verbundfestigkeit ist auf das Erweichen der Tränkungsmatrix bei Überschreitung der Glasübergangstemperatur zurückzuführen. Bei Temperaturen oberhalb von etwa 200 °C ist keine Tränkungsmatrix und daraus resultierende Verbundwirkung mehr vorhanden. Darüber hinaus wurden im Rahmen von Abplatzversuchen drei Schutzmaßnahmen zur Vermeidung von Betonabplatzungen im Brandfall untersucht, d.h. reaktives Brandschutzsystem (RBS), zementgebundene Brandschutzplatten sowie Zugabe von Polypropylenfasern (PP-Fasern) zur Betonmischung. Die Ergebnisse zeigen, dass der Typ des Carbongeleges die Wirksamkeit der Schutzmaßnahmen beinflusst. Während die Zugabe von PP-Fasern das Abplatzen bei beiden untersuchten Gelegetypen verhindern konnte, war dies bei RBS und Brandschutzplatten nur bei einem Gelegetyp erfolgreich. Die Ursache der Abplatzungen ist auf das temperaturbedingte Schmelzen und die damit einhergehende Volumenzunahme der im Gelege Q85 vorhandenen Hilfsfäden zurückzuführen. Dies führt zu einer Rissbildung parallel zur brandbeanspruchten Betonoberfläche. Der Dampfdruck im Beton ist trotz reduzierter Erwärmungsgeschwindigkeit zu hoch, weshalb es zum Abplatzen kommt. Im Gegensatz dazu bewirkt das Schmelzen der PP-Fasern eine Erhöhung der Permeabilität des Betons. Dadurch kann der entstehende Wasserdampf frühzeitig entweichen, sodass der Dampfdruck unterhalb der kritischen Schwelle bleibt, die für das Abplatzen erforderlich wäre. T2 - Symposium Heißbemessung 2025 CY - Braunschweig, Germany DA - 29.09.2025 KW - Carbonbeton KW - Biegetragfähigkeit KW - Abplatzverhalten PY - 2025 SP - 1 EP - 13 PB - Institut für Baustoffe, Massivbau und Brandschutz (iBMB), Technische Universität Braunschweig CY - Braunschweig, Deutschland AN - OPUS4-64882 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Patrick P. A1 - Winkler, Nicolas P. A1 - Nerger, Tino A1 - Lohrke, Heiko A1 - Bartholmai, Matthias T1 - Robotic Olfaction in Action: Field Applications and Results from Current Research N2 - In recent decades, robotics, particularly in environmental monitoring, has made significant advances. Robots of various forms and sizes have become essential tools for data collection in environmental research. Mobile Robot Olfaction (MRO) involves mobile robots equipped with gas sensors and requires the integration of multiple disciplines, including signal processing, machine perception, autonomous navigation, and pattern recognition. Common applications of MRO include mapping gas distributions, locating and detecting gas sources, and tracking gas plumes. Aerial Robot Olfaction (ARO) is a specialized branch of MRO that adapts these concepts to aerial robots, addressing the challenges of airborne gas sensing. This presentation highlights recent developments and results from ongoing research projects in MRO and ARO, with a focus on real-world deployment scenarios and the challenges encountered in practice. T2 - Drohnen in der Zerstörungsfreien Prüfung CY - Magdeburg, Germany DA - 26.11.2025 KW - Ground and Aerial robots KW - Gas distribution mapping KW - Gas source localization KW - Gas Tomography KW - Mobile Robotic Olfaction PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-648928 UR - https://www.ndt.net SP - 1 EP - 15 PB - DGZfP AN - OPUS4-64892 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hille, Falk A1 - Schneider, Ronald A1 - Simon, Patrick A1 - Herrmann, Ralf A1 - Baeßler, Matthias ED - Döhler, Michael ED - Mélot, Adrien ED - Aenlle Lopez, Manuel T1 - System identification and model calibration of a steel road bridge N2 - The Bundesanstalt für Materialforschung und -prüfung (BAM), in cooperation with the Netherlands Organization for Applied Scientific Research (TNO), is working on a framework for integrating frequently updated structural models into an asset management process for bridge structures. A multi-span steel road bridge was selected as a test case for the development of this framework. In order for the structural model to represent the real behavior of the bridge with sufficient accuracy, model calibration is required. In this case, we have planned to calibrate the model based on the dynamic response of the bridge. To determine its dynamic properties, a multi-setup operational modal analysis was performed on one of the bridge spans. In parallel, a structural model of the span was developed based on the available design and service life information. Both eigenfrequencies and mode shapes were used as reference parameters to calibrate the model. A sensitivity analysis was performed to identify the most influential design parameters. Subsequently, a genetic algorithm was applied for minimizing the difference between measured and simulated characteristic responses. In the proposed paper, we summarize the measurements as well as the determination of the modal response of the bridge and describe the process of calibration of the structural model using the identified dynamic response. T2 - 11th International Operational Modal Analysis Conference (IOMAC 2025) CY - Rennes, France DA - 20.05.2025 KW - Bridge structure KW - Operational modal analysis KW - Model calibration PY - 2025 SN - 978-84-09-75120-4 SP - 114 EP - 121 PB - International Group of Operational Modal Analysis CY - Gijón, Spain AN - OPUS4-64416 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz A1 - Said, Samir A1 - Rohrmann, Rolf ED - Döhler, Michael T1 - Modal analysis of road and rail bridges for damage detection and resonance prediction N2 - In the 1980s, the Federal Institute of Material Research and Testing started with modal analysis measurements of some bridges before and after repair. For one of the bridges, a structural health monitoring was installed 1994 which is still working up to now. It has been modified and extended several times. The monitoring was extended from the critical span to three neighbouring spans. A modal analysis of the whole bridge with seven spans have been done three times, twice together with EMPA of Switzerland. Additional calibration measurements have been done and additional evaluation procedures have been implemented for the monitoring of the steadily increasing loads from the road traffic. Additional sensors were installed such as strain gauges, crack-width, and temperature sensors. The strong influence of the temperature on the natural frequencies has been studied over the years. Later, a temperature compensation has been established and a weak aging trend has been found in the monitoring data. Now, the bridge will be demolished and replaced by a new bridge. Some results of this long-term monitoring will be shown and possible damages (changes of the pre-stress or the support structure) will be discussed. A second application of modal analysis will be demonstrated: the prediction of the resonances due to passing trains. The response of a bridge to passing trains can be calculated in frequency domain as the multiplication of three spectra, the axle sequence spectrum of the train, the transfer function of the bridge, and the modal force spectrum of a single passing load. A resonance occurs if a maximum of the train spectrum coincides with the maximum of the bridge spectrum. The amplitude at this resonance is strongly influenced by the modal force spectrum which is identical to the frequency or wavenumber spectrum of the corresponding mode shape. Therefore, modal analysis from calculation, impact measurements, wind and train measurements are necessary for the prediction of the resonance occurrence and amplification. Examples of mode shape spectra for single or multi-span bridges with simply supported or continuous spans will be shown, and some relations between mode shapes and resonance amplifications will be concluded. T2 - 11th International Operational Modal Analysis Conference (IOMAC) CY - Rennes, France DA - 20.05.2025 KW - Bridge monitoring KW - Multi-span bridges KW - Damage detection KW - Resonance PY - 2025 SP - 39 EP - 46 PB - INRIA CY - Rennes AN - OPUS4-63473 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz A1 - Song, Jiaojiao T1 - Analysis of intact and damaged (floating) slab tracks by finite-element boundary-element models and by measurements N2 - The damage detection and repair control have become important tasks for slab tracks. Different intact and damaged slab tracks have been investigated theoretically and experimentally for train passages and hammer impacts. The following damages have been considered: The loss of contact between the sleeper and the track slab, between the track slab and the base slab, and between the base slab and the base layer. At first, a slab track with a gap between the track slab and the base layer has been calculated by the combined finite-element boundary-element method which correctly incorporates the behaviour of the infinite soil. The basic results are the track displacements of the rail, the track slab, and the base layer along the track which are caused by a single axle load. These solutions are properly superposed for to get the complete train load. The influence of track and soil parameters and of the track damage has been analysed. For the intact track, the compliance of the soil is dominant whereas the track bending stiffness becomes more important for the damaged track. By comparing the calculated results with the measurements, the length of the gap could be quantified. A slab track with a loose sleeper (without contact to the supporting track slab) was analysed by the transfer function between the displacements and the hammer force (receptance functions) where a resonance appeared in case of the damage. Differences between the different track elements confirmed the detection of the damage. A floating slab track with a thin rubber layer has been investigated for a possible gap between the base slab and the base layer. The behaviour of the intact track has been calculated by a wavenumber-domain method, and the same behaviour has been found in the measurements at several track sections, indicating that there is no damage. Finally, a floating slab track with steel springs and viscous fluid dampers has been measured in the Tongji laboratory. The modes of the floating track slab and the transfer function with corresponding resonances have been calculated and successfully compared with results from wheelset drop tests. T2 - Third International Conference on Rail Transportation (ICRT2024) CY - Shanghai, China DA - 07.08.2024 KW - Railway track KW - Damage KW - Vibration measurement KW - Finite element method KW - Boundary element method KW - Frequency response function KW - Moving load response KW - Floating slab track PY - 2025 SN - 978-0-7844-8594-1 SP - 591 EP - 600 AN - OPUS4-61267 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rurack, Knut A1 - Resch-Genger, Ute A1 - Rettig, W. T1 - Fluoreszenzmarker für Schwer- und Übergangsmetallionen - Selektivität durch gezieltes Rezeptordesign und ionenspezifische Fluoreszenzverstärkung T2 - Tagung "Tag der Chemie 2000" CY - Potsdam, Deutschland DA - 2000-11-08 KW - Fluoreszenzmarker KW - Schwermetalle KW - Rezeptoren PY - 2000 SP - 87 AN - OPUS4-1016 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mix, Renate A1 - Hoffmann, Katrin A1 - Decker, Renate A1 - Friedrich, Jörg Florian A1 - Resch-Genger, Ute ED - Blasek, G. T1 - Möglichkeiten der kovalenten Anbindung von Funktionsmolekülen an Polymeroberflächen T2 - 13. Neues Dresdner Vakuumtechnisches Kolloquium "Beschichtung und Modifizierung von Kunststoffoberflächen" CY - Dresden, Deutschland DA - 2005-10-13 PY - 2005 SP - 35 EP - 41 PB - VDI-Verl. CY - Dresden AN - OPUS4-11946 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Thoralf A1 - Lehmann Schlag, Jens A1 - Burkert, Andreas T1 - KorroPad®-Ein Kurzzeitprüfverfahren zur Qualitätssicherung der Oberflächen- und Schweißnahtnachbearbeitung nichtrostender Stähle N2 - Die Ausbildung einer stabilen Passivschicht ist entscheidend für den Korrosionsschutz nichtrostender Stähle. KorroPad® bietet eine schnelle, zerstörungsfreie Bewertung der Passivschichtstabilität und ist seit 2025 als DIN 50024 genormt. Die Methode ermöglicht eine 15‑minütige Vor‑Ort‑Prüfung ohne Spezialwissen und schließt die Lücke zwischen teuren Laborverfahren und fehlender prozessbegleitender Qualitätssicherung. Der Beitrag beschreibt Funktionsprinzip, Anwendung sowie Beispiele aus der Oberflächen- und Schweißnahtbearbeitung. T2 - 43. Vortrags- und Diskussionstagung Werkstoffprüfung 2025 CY - Dresden, Germany DA - 26.11.2025 KW - KorroPad KW - Nichtrostender Stahl KW - Korrosion KW - Passivität PY - 2025 SN - 978-3-88355-454-9 VL - 43 SP - 1 EP - 7 PB - DGM Deutsche Gesellschaft für Materialkunde e.V. CY - Sankt Augustin AN - OPUS4-64933 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klaus, Christian A1 - Soruco Aloisio, Ricardo A1 - Koch, Claudia A1 - Prellwitz, Matthias T1 - Towards Safety and Accuracy of Hydrogen Refuelling Stations through Digital Twins N2 - This paper presents digital quality infrastructure methods for hydrogen refueling stations using the Asset Administration Shell as a standardized digital twin. Implemented at BAM’s test platform, it integrates real-time sensor data, calibration certificates, and compliance documents to support traceable, interoperable asset management. In combination with AI and semantic tools, the system will enable predictive maintenance, remote audits, and improved safety. This approach reduces downtime, enhances transparency, and offers a scalable model demonstrating the potential of digital twins in advancing metrological traceability and operational efficiency in hydrogen technologies. T2 - IMEKO TC-6 International Conference on Metrology and Digital Transformation - M4DConf 2025 CY - Benevento, Italy DA - 03.09.2025 KW - Datenintregration KW - IT KW - Verwaltungsschale KW - Infrastruktur KW - OT KW - Open Source KW - Software PY - 2025 UR - https://www.m4dconf.org/ UR - https://www.sciencedirect.com/journal/measurement-digitalization SP - 1 EP - 6 AN - OPUS4-64951 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Fabry, Çağtay A1 - Hirthammer, Volker A1 - Scherer, Martin K. T1 - weldx-widgets: advanced visualisation and jupyter widgets for weldx N2 - This package provides advanced visualisation and interactive widgets for the weldx core package. KW - Weldx KW - Welding KW - Research data KW - Visualisation PY - 2025 DO - https://doi.org/10.5281/zenodo.17790485 PB - Zenodo CY - Geneva AN - OPUS4-64973 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Fabry, Çağtay T1 - pytcs: a TwinCAT Scope text export file reader N2 - A Python package for reading exported TwinCAT Scope Files. Export your TwinCAT Scope .svdx files to .txt/.csv and read them into Python. KW - Python KW - TwinCAT Scope KW - File reader KW - File format KW - Measurement data PY - 2025 DO - https://doi.org/10.5281/zenodo.17791125 PB - Zenodo CY - Geneva AN - OPUS4-64975 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Han, Ying T1 - Segmented primary phases of Al-alloy EN AW-2618A in the T61 state using synchrotron computed tomography N2 - The video file contains data from a synchrotron computed tomography measurement of the primary phases of the Al-alloy EN AW-2618A in the T61 state. The volume fraction of the primary phases was determined. KW - Aluminum alloy KW - EN AW-2618A KW - Computed tomography KW - Primary phases PY - 2024 DO - https://doi.org/10.5281/zenodo.12730717 PB - Zenodo CY - Geneva AN - OPUS4-60657 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mieller, Björn A1 - Rabe, Torsten T1 - Surface characteristics of LTCC substrates fabricated by pressure-assisted sintering N2 - Plane LTCC substrates can be produced in zero-shrinkage technology by pressure-assisted sintering. The application of axial pressure during sintering supports densification, enhances cofiring of different materials, and restrains deformation. However, the sintered surfaces are affected by the release tapes and by the setters used in the pressure-assisted sintering process. In this study, the effect of release tape particle size on the surface properties of sintered substrates was investigated. Moreover, the substitution of release tape by the use of a vitreous carbon setter was tested. Surface roughness and sheet resistances of metallic thin films on the respective samples were determined. It was found that the roughness of the substrates is not directly correlated with the adequacy of the surface for thin-film deposition. Compared with a freely sintered sample with an average roughness (Ra) of 0.31 μm, pressure-assisted sintering created smoother surfaces using fine-grained release tapes (Ra = 0.18 μm) and rougher surfaces using coarse release tapes (Ra = 0.46 mm). Still, sheet resistances were higher on all sinter-pressed samples. The vitreous carbon setter created unusual trenched surface structures, characterized by varying roughness values and intermediate sheet resistances on the LTCCs tested. T2 - CICMT 2013 - IMAPS/ACerS 9th International conference and exhibition on ceramic interconnect and ceramic microsystems technologies CY - Orlando, FL, USA DA - 23.04.2013 PY - 2013 N1 - Geburtsname von Mieller, Björn: Brandt, B. - Birth name of Mieller, Björn: Brandt, B. SP - 000261 EP - 000267 AN - OPUS4-30300 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Popiela, Bartosz A1 - Günzel, Stephan A1 - Oktaviany, Jennifer A1 - Widjaja, Martinus Putra A1 - Mair, Georg W. A1 - Seidlitz, Holger T1 - Influence of Internal Pressure Regulation During Filament Winding on Failure Mechnism in Type 4 Pressure Vessels: A Case Study N2 - Hydrogen storage is a crucial part of the hydrogen value chain, particularly in terms of safety and social acceptance of hydrogen technologies. For on-board and transportation applications, hydrogen is commonly stored as a compressed gas in pressure vessels. Full composite wrapped Type 4 pressure vessels are especially beneficial due to their high weight-saving potential and their capability to withstand high working pressures. To maintain an appropriate safety level, the mechanical behavior of the composite structure has been the subject of investigation in numerous studies. In this study, the failure mechanisms of two designs of Type 4 cylinders are investigated. The two designs differ solely in the manufacturing process parameters, particularly the internal pressure applied during the filament winding process. Variations in internal pressure result in different residual stress states and changes in the quality of the composite structure. The stacking sequence, materials used, and other manufacturing parameters remain unchanged. The cylinders show different failure mechanisms in slow burst tests: one design fails in hoop windings, while the other one fails in helical windings, despite no stress exaggeration in the fiber direction being observed with embedded optical fibers or in numerical simulations. To explain the failure mechanisms, the quality of the cylinders is investigated. The results of X-ray computed tomography and pulse-echo investigation, highlight the complexity of the interactions between manufacturing process parameters, residual stresses, manufacturing quality, and the mechanical behavior of composite pressure vessels. Resin-rich areas in the composite material are identified as a possible cause of the differing failure mechanisms. T2 - 11th International Conference on Hydrogen Safety ICHS 2025 CY - Seoul, South Korea DA - 22.09.2025 KW - Composite KW - Pressure vessel KW - Filament winding KW - Burst test PY - 2025 SP - 1 EP - 12 AN - OPUS4-64452 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thiede, Tobias A1 - Mishurova, Tatiana A1 - Cabeza, S. A1 - Nadammal, Naresh A1 - Bode, Johannes A1 - Kromm, Arne A1 - Haberland, C. A1 - Bruno, Giovanni ED - Richard, H. A. T1 - Der Einfluss der Hatch-Länge und der Probenabtrennung von der Bauplatte auf den Eigenspannungszustand in SLM-Bauteilen aus IN718 N2 - Die Schicht-für-Schicht additive Fertigung (AM) in Form des selektiven Laserschmelzens (SLM) bietet einerseits Vorteile bezüglich des Probendesigns, andererseits sind thermische Eigenspannungen (ES) aufgrund des hohen Temperaturgradienten unvermeidbar. Diese Eigenspannungen wurden in zwei SLM-gefertigten Proben aus IN718 zerstörungsfrei mit Neutronenstreuung hinsichtlich der folgenden zwei Einflüsse analysiert: der Einfluss der Hatch-Länge und das Abtrennen des Werkstücks von der Bauplatte. Begleitet wurden die Messungen der Eigenspannungen durch optische Mikroskopie und die taktile Vermessung der Oberfläche. Eine Korrelation zwischen den Eigenspannungen und der Hatch-Länge konnte beobachtet und erklärt werden. T2 - 2. Tagung des DVM-Arbeitskreises Additiv gefertigte Bauteile und Strukturen CY - Berlin, Germany DA - 09.11.2017 KW - IN718 KW - Additive Fertigung KW - Selektives Laserschmelzen KW - Eigenspannungen KW - Neutronenstreuung PY - 2017 SN - 2509-8772 VL - Bericht 402 SP - 137 EP - 146 PB - DVM CY - Berlin AN - OPUS4-42946 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mieller, Björn A1 - Gemeinert, Marion A1 - Koppert, R. A1 - Bolte, J. A1 - Rabe, Torsten T1 - LTCC substrates for high performance strain gauges N2 - Recent advances in the development of high gauge factor thin-films for strain gauges prompt the research on advanced substrate materials. A glass ceramic composite has been developed in consideration of a high coefficient of thermal expansion and a low modulus of elasticity for the application as support material for thin-film sensors. Constantan foil strain gauges were fabricated from this material by tape casting, pressure-assisted sintering and subsequent lamination of the metal foil on the planar ceramic substrates. The sensors were mounted on a strain gauge beam arrangement and load curves and creep behavior were evaluated. The accuracy of the assembled load cells correspond to accuracy class C6. That qualifies the load cells for the use in automatic packaging units and confirms the applicability of the LTCC substrates for fabrication of accurate strain gauges. To facilitate the deposition of thin film sensor structures onto the LTCC substrates, the pressure-assisted sintering technology has been refined. By the use of smooth setters instead of release tapes substrates with minimal surface roughness were fabricated. Metallic thin films deposited on these substrates exhibit low surface resistances comparable to thin films on commercial alumina thin-film substrates. The presented advances in material design and manufacturing technology are important to promote the development of high performance thin-film strain gauges. T2 - CICMT 2012 - 8th International conference on ceramic interconnect & ceramic microsystems technologies CY - Erfurt, Germany DA - 16.04.2012 KW - LTCC KW - Thin-film substrate KW - Pressure-assisted sintering KW - Strain gauge PY - 2012 N1 - Geburtsname von Mieller, Björn: Brandt, B. - Birth name of Mieller, Björn: Brandt, B. SP - 000175 EP - 000180 (Session TP 4 / TP 43) AN - OPUS4-27567 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Widjaja, Martinus Putra A1 - Islam, F. A1 - Joannes, S. A1 - Bunsell, A. A1 - Mair, Georg W. A1 - Thionnet, A. T1 - Effect of input properties on the predicted failure of a composite pressure vessel using a multiscale model N2 - It is pertinent to have a correct description of fibre strength described by the twp parameter Weibull distribution when evaluating a type Iv pressure vessel using the fibre break multiscale model developed at Mines ParisTech. Earlier studies have shown a positive comparison result when T600S fibre strength were used. This study has discovered what would be the effect on the predicted strength when T700S strength is used. T2 - FiBreMoD Conference CY - Leuven, Belgium DA - 11.12.2019 KW - Composite Pressure Vessel KW - Fibre break KW - Multiscale model KW - Weibull parameter PY - 2019 SP - 55 EP - 56 AN - OPUS4-50109 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hothan, Sascha A1 - Häßler, Dustin A1 - Stelzner, Ludwig A1 - Fürst, Richard A1 - Eiz Eddin, Ahmad T1 - Lösungsansätze für neue Herausforderungen im konstruktiven baulichen Brandschutz N2 - Der Klimawandel und die zunehmende Ressourcenknappheit stellen Herausforderungen dar, die in Zukunft grundlegende Anpassungen in der Art des Umgangs mit Rohstoffen, Energie und des Wirtschaftens an die Gesellschaft stellen werden. In der Leichtbaustrategie der Bundesregierung wird zusammenfassend festgestellt, dass der fortschreitende Klimawandel Technologien erfordert, die die Transformation der Wirtschaft, eine ressourcenschonende Wertschöpfung und eine nachhaltige und resiliente Rohstoffversorgung sicherstellen. Aus diesen für alle Wirtschaftszweige sehr allgemein formulierten Anforderungen und vor dem Hintergrund eines wachsenden Bedarfs schnell verfügbarer Bausubstanz, lassen sich konkrete Anforderungen für das Bauwesen ableiten. Es geht um die Reduktion des Ressourcenverbrauchs für die Errichtung und den Betrieb neuer Gebäude sowie die Nach- und Weiternutzung bestehender Bausubstanz. In der Bundesanstalt für Materialforschung und -prüfung (BAM) wurde im Themenfeld Infrastruktur das Aktivitätsfeld Leichtbau ins Leben gerufen, das die Forschungsaktivitäten zum Leichtbau bündelt. Im vorliegenden Beitrag werden ausgewählte Projekte in Bezug auf den konstruktiven baulichen Brandschutz vorgestellt und die besonderen Herausforderungen verdeutlicht sowie die daraus abgeleiteten technischen Lösungsmöglichkeiten aufgezeigt. Als Beispiel einer Bauweise mit höchstmöglicher Effizienz in der Materialausnutzung sowie exzellenter Recyclingfähigkeit des Werkstoffs wird im Abschnitt „Einsatz reaktiver Brandschutzsysteme auf Stahlzuggliedern mit Vollprofil“ gezeigt, wie der Feuerwiderstand von Stahlzuggliedern mit minimalem Materialaufwand sichergestellt werden kann. Anhand des Beispiels der „Alten Aktienspinnerei“ verdeutlicht sich die Relevanz der Methode für die Nachnutzung historischer Bausubstanz. Im Abschnitt „In situ Überprüfung des Feuerwiderstands von Stahltragwerken mit gealterten reaktiven Brandschutzsystemen“ wird gezeigt, wie in Zukunft die minimalinvasive Überprüfung der Wirksamkeit bereits über Jahrzehnte in Nutzung befindlicher reaktiver Brandschutzsysteme (RBS) ermöglicht wird. Dies bildet die Grundvoraussetzung für eine Weiternutzung sowie möglicherweise erforderliche Instandsetzung auch nach Überschreitung der ursprünglich vorgesehenen Nutzungsdauer des RBS anhand einer quantitativen Aussage zum noch vorhandenen Feuerwiderstand. Eine wichtige Strategie im Betonbau zur Verringerung des CO2-Ausstoßes wird im Abschnitt „Feuerwiderstand von Leichtbaukonstruktionen aus vorgespanntem Carbonbeton“ vorgestellt. Das Verbundforschungsvorhaben verfolgt die Entwicklung eines neuen Deckensystems aus vorgespanntem Carbonbeton. Die angestrebte Leichtbauweise verringert den Einsatz von Zement durch Minimierung des erforderlichen Betonvolumens. Um einen möglichst dünnen Deckenspiegel zu erzeugen ist eine Reduzierung der Betondeckung erforderlich, weshalb für den Brandfall Maßnahmen zu ergreifen sind, die die Erwärmung der Carbonbewehrung und die damit einhergehende Degradation des Materials begrenzen. In diesem Zusammenhang sind auch wirksame Strategien zur Eindämmung von Beton-abplatzungen zu entwickeln. Abschließend wird im Abschnitt „Gebäude in Stahl-Modulbauweise mit selbstaussteifenden Raumzellen“ herausgearbeitet, wie diese Bauweise zukünftig noch effizienter werden kann, indem eine Nachweismöglichkeit der aussteifenden Wände in Leichtbauweise für den Brandfall geschaffen wird. T2 - Bauphysikertreffen 2025 - Hochschule für Technik Stuttgart CY - Stuttgart, Germany DA - 28.11.2025 KW - Klimawandel KW - Ressourcenknappheit KW - Bausupstanz KW - Brandfall PY - 2025 VL - Bauphysikertagung 2025 SP - 1 EP - 12 AN - OPUS4-65371 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krankenhagen, Rainer A1 - Chaudhuri, Somsubhro A1 - Pittner, Andreas A1 - Winterkorn, Rene A1 - de Finis, Rosa A1 - Palumbo, Davide A1 - Galietti, Umberto T1 - Thermographic investigation of the anisotropic behaviour of additively manufactured AISI316 steel using DED-Arc N2 - Additive manufacturing is one of the most promising techniques for industrial production and maintenance, but the specifics of the layered structure must be considered. The Direct Energy Deposition-Arc process enables relatively high deposition rates, which is favourable for larger components. For this study, specimens with different orientations were prepared from one AISI316 steel block – parallel and orthogonal to the deposition plane. Quasistatic tensile loading tests were carried out, monitored by an infrared camera. The obtained surface temperature maps revealed structural differences between both orientations. The consideration of surface temperature transients yields more details about the behaviour of the material under tensile loading than the conventional stress-strain-curve. These preliminary investigations were supplemented by thermographic fatigue trials. Although the anisotropy was also observed during fatigue loading the fatigue behaviour in general was the same, at least for both inspected specimens. The presented results demonstrate the abilities and the potential of thermographic techniques for tensile tests. T2 - 17th Quantitative Infrared Thermography Conference CY - Bologna, Italy DA - 07.07.2025 KW - Thermoelastic effect KW - Wire-arc-additive manufacturing KW - thermal stress analysis KW - fatigue testing PY - 2026 DO - https://doi.org/10.21611/qirt-2024-029 SP - 1 EP - 8 AN - OPUS4-65372 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gaal, Mate T1 - Zwischen Leitfaden und Labor - Der UA ACUT stärkt Austausch und Sichtbarkeit N2 - Den Bekanntheitsgrad der luftgekoppelten Ultraschallprüfung zu erhöhen – dieses Ziel steht weiterhin im Mittelpunkt der Arbeit des Unterausschusses Luftgekoppelte Ultraschallprüfung (UA ACUT). Am 8. Oktober 2025 trafen sich neun Mitglieder und ein Gast zur 16. Sitzung bei der Bundesanstalt für Materialforschung und -prüfung (BAM) in Berlin. KW - Luftgekoppelter Ultraschall KW - Leitfaden KW - Normung PY - 2025 UR - https://www.dgzfp.de/wp-content/uploads/2025/12/ZfP-Magazin-197.pdf SN - 1616-069X IS - 197 SP - 14 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-65368 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mieller, Björn A1 - Rabe, Torsten T1 - Structuring of LTCC substrates by a combination of pressure-assisted sintering and hot-embossing N2 - A novel technology for the structuring of LTCC surfaces is introduced. The material is shaped in a zero-shrinkage process by embossing a glassy carbon mold into the softened LTCC directly after termination of the shrinkage. Three commercially available LTCC compositions (Ceramtape GC, Heratape CT707, and DP951) were tested. Diverse raised and lowered structures including rings, grids, and characters were fabricated. Different material behavior was observed for the tested compositions. Promising results were achieved with Ceramtape GC. Embossing of precise, 40 µm deep circular cavities and 50 µm high raised characters is demonstrated. Processing of 100 × 100 mm² substrates is possible. DP951 showed very good moldability, but also unwanted material displacement due to evaporating lead. A high displacement capacity but uneven heights of embossed structures were observed on CT707 samples. SEM investigations proved the precise transfer of surface contours from the mold to the LTCC. Thereby, the high potential of the hot-embossing process for micro-patterning of LTCC is illustrated. T2 - 11th International Conference and Exhibition on Ceramic Interconnects and Ceramic Microsystem Technologies (CICMT 2015) CY - Dresden, Germany DA - 20.04.2015 KW - LTCC KW - Glass-like carbon PY - 2015 DO - https://doi.org/10.4071/CICMT-THA24 SN - 2380-4491 VL - 2015 IS - CICMT SP - 000297 EP - 000303 AN - OPUS4-40135 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rockenhäuser, Christian A1 - Augenstein, E. A1 - Skrotzki, Birgit T1 - Long term ageing of alloy 2618A N2 - The result of an Investigation of the "Long term ageing of alloy 2618A" are discussed. T2 - International Conference on Aluminium Alloys 16 CY - Montreal, Canada DA - 17.06.2018 KW - Alloy 2818A KW - Aluminium KW - Coarsening KW - Transmission electron microscopy KW - S-phase PY - 2018 SP - Paper 400101 AN - OPUS4-45287 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hodoroaba, Vasile-Dan A1 - Fagan, J. T1 - Contributors invited for two studies on concentration of bimodal silica nanoparticle and bipyramidal titania N2 - International standardisation network VAMAS is calling for participants in two studies on the measurement of (relative) number concentration of bimodal silica nanoparticles including deposition from liquid suspension and the measurement of particle size and shape distribution of bipyramidal titania including deposition from liquid suspension. KW - Nanoparticles KW - VAMAS KW - Inter-laboratory comparison KW - TiO2 KW - SiO2 PY - 2021 UR - https://www.iom3.org/resource/contributors-invited-for-two-studies-on-concentration-of-bimodal-silica-nanoparticle-and-bipyramidal-titania.html SP - 1 EP - 2 PB - Institute of Materials, Minerals and Mining (IOM3) CY - London, UK AN - OPUS4-54410 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hodoroaba, Vasile-Dan T1 - BAM reference data - EDS raw data of Al-coated titania nanoparticles (JRCNM62001a and JRCNM62002a) N2 - EDS spectra of Al-coated titania nanoparticles (JRCNM62001 and JRCNM62002a) provided by the JRC repository are provided. KW - EDS KW - Titania nanoparticles KW - BAM reference data PY - 2021 DO - https://doi.org/10.5281/zenodo.4986420 PB - Zenodo CY - Geneva AN - OPUS4-52833 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bennet, Francesca A1 - Hodoroaba, Vasile-Dan T1 - BAM reference data - SEM raw data for the particles size distribution of Al-coated titania nanoparticles (JRCNM62001a and JRCNM62002a) N2 - SEM raw images of Al-coated titania nanoparticles (JRCNM62001 and JRCNM62002a) provided by the JRC repository are provided together with the particle size distribution of the minimum Feret Diameter extracted from the given images. KW - SEM KW - Titania nanoparticles KW - Particle size distribution KW - BAM reference data PY - 2021 DO - https://doi.org/10.5281/zenodo.5007367 PB - Zenodo CY - Geneva AN - OPUS4-52836 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Knigge, Xenia A1 - Radnik, Jörg T1 - Advanced materials for the energy transition N2 - The climate crisis is the burning issue of our time. In order to avert the impending consequences, global efforts are being made in a wide variety of social and scientific fields. This report looks at a small part of these efforts, a technical aspect, namely the question of which AdMa are currently considered in techniques to support the energy transition. AdMa, i.e. materials that are rationally designed to have new or enhanced properties, and/or targeted or enhanced structural features, are used in all sectors of the energy transition. Questions of energy generation, storage and saving are considered here. This report is based on literature research and contains a general compilation of various AdMa that are used in the energy transition or are being researched for this purpose. From this compilation, ten materials that are considered particularly relevant for various reasons were selected and examined in more detail in relation to their use. The specific question here lies in the conflicting objective that the development of technologies for the energy transition is welcomed, but the use of AdMa may entail possible challenges in view of chemical safety as well as sustainability and circular economy. KW - Energy generation KW - Energy saving KW - Eneergy storage KW - Energy transportation PY - 2025 DO - https://doi.org/10.60810/openumwelt-7853 SN - 1862-4804 VL - 83 SP - 1 EP - 64 PB - Umweltbundesamt CY - Dessau-Roßlau AN - OPUS4-63529 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ávila Calderón, Luis Alexander A1 - Matzak, Kathrin A1 - Olbricht, Jürgen A1 - Dolabella Portella, Pedro A1 - Skrotzki, Birgit T1 - BAM Reference Data: High Temperature Tensile Data of Single-Crystal Ni-Based Superalloy CMSX-6 N2 - This publication provides comprehensive metadata and test results of tensile tests at elevated temperature according to DIN EN ISO 6892-2:2018-09 on the single crystal Ni-based superalloy CMSX-6 at T = 980 °C. The tests were performed in an ISO 17025-accredited test laboratory. The calibrations of measuring equipment are documented, meet the requirements of the measurement standard, and are metrologically traceable. The provided data were audited and are BAM reference data. KW - Digitalisierung KW - Referenzdaten KW - CMSX-6 KW - Zugversuch KW - NFDI-MatWerk KW - Ni-Basis-Superlegierung PY - 2025 DO - https://doi.org/10.5281/zenodo.17846616 PB - Zenodo CY - Geneva AN - OPUS4-65338 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Skrotzki, Birgit A1 - Koch, B. T1 - Microstructural characterization of the metastable Beta-titanium alloy TIMETAL LCB after fatigue loading N2 - In the present work, the titanium alloy Ti-6.8Mo-4.5Fe-1.5Al (Timetal LCB) was investigated with respect to the microstructural evolution during strain controlled fatigue loading. The alloy was developed to reduce the generally high material costs of β-alloys by substituting expensive beta stabilizers by using a standard Fe-Mo master alloy. One possible application seen in the automotive industry is the substitution os suspension structural parts currently made of steel, suc as suspension springs. These components require a high strength and fatigue resistance. T2 - International conference on electron nanoscopy & XXXII Annual meeting of EMSI CY - Hyderabad, India DA - 2011-07-06 KW - Titanium KW - Fatigue KW - Microstructure KW - Deformation mechanism PY - 2011 SP - 255 EP - 256 AN - OPUS4-24167 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Uckert, Danilo A1 - Kühn, Hans-Joachim A1 - Matzak, Kathrin A1 - Rehmer, Birgit A1 - Skrotzki, Birgit T1 - Ermüdungsverhalten des warmfesten austenitischen Gusseisens EN-GJSA-XNiSiCr35-5-2 bei hoher Temperatur N2 - Die warmfeste austenitische Gusseisenlegierung EN-GJSA-XNiSiCr35-5-2 (häufig auch als Ni-Resist D-5S bezeichnet) wurde hinsichtlich ihres mechanischen Verhaltens bei hoher Temperatur charakterisiert. Dazu wurden (isotherme) niederzyklische (LCF-) und (nicht-isotherme) thermomechanische Ermüdungsversuche (TMF) zwischen Raumtemperatur und 900 °C durchgeführt. Diese Ergebnisse dienten (zusammen mit weiteren Versuchsdaten) der Kalibrierung werkstoffmechanischer Modelle. Bei den höchsten Prüftemperaturen wurde Schädigung in Form von Kriechen beobachtet und metallographisch dokumentiert. T2 - Langzeitverhalten warmfester Stähle und Hochtemperaturwerkstoffe CY - Dusseldorf, Germany DA - 30.11.2018 KW - Kriechen KW - LCF KW - Lebensdauer KW - Ni-Resist KW - Schädigung KW - TMF PY - 2018 SN - 978-3-00-061694-5 SP - 29 EP - 38 CY - Düsseldorf AN - OPUS4-46919 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - BOOK A1 - Czichos, Horst A1 - Skrotzki, Birgit A1 - Simon, Franz-Georg T1 - Das Ingenieurwissen: Werkstoffe KW - Werkstoffe KW - Materialprüfung KW - Werkstoffkennwerte PY - 2014 DO - https://doi.org/10.1007/978-3-642-41126-7 SP - 1 EP - 110 PB - Springer-Vieweg CY - Berlin Heidelberg AN - OPUS4-29654 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sonntag, Nadja A1 - Skrotzki, Birgit ED - Beck, T. ED - Charkaluk, E. T1 - Imaging of potential crack initiation sites in ferritic steels by the Bitter method N2 - It is widely known that the magnetic domain structure of stress-sensitive ferromagnetic materials may be altered by external or internal mechanical stresses due to magnetoelastic effects. In this contribution, localized magnetic domain changes arising from inhomogeneous deformation and multiaxial loading conditions are imaged by the Bitter method for the first time. It is demonstrated that these domain changes provide deformation-related information and thus, allow for the visualization of macroscopic strain gradients in fine-grained polycrystalline steels, while keeping a sufficient spatial resolution. This approach has been developed within the framework of BAM-MI-project “MICRONET”. T2 - LCF8 Eighth International Conference on Low Cycle Fatigue CY - Dresden, Germany DA - 27.06.2017 KW - Bitter method KW - Magnetic domains KW - Strain gradients PY - 2017 SN - 978-3-9814516-5-8 SP - 263 EP - 265 PB - DVM Deutscher Verband für Materialforschung und -prüfung CY - Berlin, Germany AN - OPUS4-40862 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kling e Silva, Lucas A1 - Sonntag, Nadja A1 - Skrotzki, Birgit T1 - CARACTERIZAÇÃO MAGNÉTICA PRÉ E PÓS DEFORMAÇÃO DE AÇOS DE CONSTRUÇÃO NÃO LIGADOS ATRAVÉS DA TÉCNICA BITTER (FERROFLUIDO) T1 - Magnetic characterization before and after deformation of non-alloyed contruction steels using bitter technic N2 - The plastic deformation results in irreversible microstructure changes in the steel, which can be considered as the initial stage of the fracture process. However, detecting, monitoring and evaluating, damage states and small defects non-destructively in advance still proves challenging. Dubov reported the phenomenon of the spontaneous emergence of weak magnetic fields in ferritic structural steel and pipelines, which originate due to heterogeneous mechanical and / or thermal stresses. This observation is not associated with induced phase transformations by deformation and appears to be a promising tool for the prior characterization of damage in ferromagnetic steels. To provide a better understanding of the physical bases of the process, the magnetic microstructure of such materials and a change of magnetic domains after undergoing plastic deformation were studied. A colloidal solution with paramagnetic particles in the nanometer range (ferrofluid), which allowed, through the Bitter technique, not only to observe a change in size of the magnetic domains of the material, but also changes in their morphology. Ferritic steels with their concentrations of carbon in its composition (0.12%; 0.17% and 0.45%) were studied in this work. T2 - 15° ENEMET - ABM Week 2015 CY - Rio de Janeiro, Brazil DA - 17.08.2015 KW - Magnetic Domains KW - Bitter Technique KW - Steels KW - Ferrofluid PY - 2015 DO - https://doi.org/10.5151/1516-392X-26931 SN - 2594-4711 VL - 15 IS - 15 SP - 2942 EP - 2950 PB - Blucher Preceedings CY - Rio de Janeiro, Brazil AN - OPUS4-48875 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Zapala, P. A1 - Abel, Andreas A1 - Michels, H. A1 - Skrotzki, Birgit T1 - Werkstoffanwendungen für Eisenaluminide (FeAl), (WAFEAL) N2 - Die zunehmende geopolitische Bedeutung der Ressourcenverfügbarkeit sowie die Anforderungen an einen geschlossenen Materialkreislauf treiben die Materialforschung voran, um konventionelle Werkstoffe mit weniger kritischen Zusätzen zu legieren oder sogar vollständig mit nachhaltigeren Alternativen zu substituieren. Eine potenzielle Alternative stellen die intermetallischen Eisenaluminid-Legierungen (FeAl) dar. Im Labormaßstab wurden bereits viele Legierungskonzepte für verbesserte Hochtempera- tureigenschaften oder Duktilität erfolgreich gießtechnisch umgesetzt. Eine erfolgreiche Erprobung von FeAl-Legierungen im industriellen Maßstab stand zu Beginn des Projekts aber weiterhin aus. Ziel des Vorhabens war daher die Entwicklung von simulationsgestützten Gießkonzepten in industrienahe Gießprozesse anhand der Modelllegierung Fe-26Al-4Mo-0,5Ti-1B und die Eingrenzung der prozesstechnischen Verfahrensgrenzen durch Warmrissversuche. Erkenntnisse hieraus wurden in einen praxisorientierten, für zukünftige Anwender in KMUs zugänglichen Handlungskatalog für die gießgerechte Auslegung von Bauteilen aus Eisenaluminiden überführt. Fokus wurde insbesondere auf das Feinguss- und Kokillengussverfahren im Schleuderguss gesetzt. Neben zahlreicher Konstruktions- und Gießprozessparameter wurden auch Wärmebehandlungen und Legierungszusätze (Al, Mo, B) variiert, um den Einfluss von Legierungselementen auf Gießbarkeit, Mikrostruktur und mechanische Kennwerte zu be- stimmen. Eine umfangreiche Basis an Daten aus Mikrostrukturanalysen (Mikroskopische Bildgebung, Bestimmung von Korngrößen sowie Phasenzusammensetzungen und -anteilen, Fraktographie), mechanischen Tests (Härtemessungen, Druckversuch, Zugversuch, Warmzugversuch, Kriechversuch) sowie Messungen thermophysikalischer Eigenschaften konnte für die Modelllegierung erzeugt werden. Korrelationen dieser Informationen mit Prozessvariablen erlaubten Schlussfolgerungen zu Härtungsmechanismen und Duktilität in der Legierung und wie sie prozesstechnisch in Gieß- und Bauteilauslegung gesteuert werden können. Der erfolgreiche Abguss von hochkomplexen Bauteilgeometrien mit dünnen Wandstärken sowie optimierte Legierungszusammensetzungen zeigen Perspektiven auf neue Anwendungsfelder auf. Das Ziel des Forschungsvorhabens ist erreicht worden. KW - Simulationsgestützte Gießkonzepte KW - Intermetallische FeAl-Legierungen PY - 2023 IS - 1322 SP - 1 EP - 168 PB - Forschungsvereinigung Verbrennungskraftmaschinen (FVV) CY - Frankfurt am Main AN - OPUS4-56932 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Abel, Andreas A1 - Zapala, P. A1 - Michels, H. A1 - Skrotzki, Birgit T1 - Materials applications of iron aluminide (FeAl), (WAFEAL) T1 - Werkstoffanwendungen für Eisenaluminide (FeAl), (WAFEAL) N2 - The increasing importance of resource availability and closed-loop material cycles are driving materials research to reduce alloying content in conventional materials or even substitute them with more sustainable alternatives. Intermetallic iron aluminide alloys (FeAl) present a potential alternative. Many alloy concepts for improved high-temperature properties or ductility have already been successfully implemented in casting technologies on a laboratory scale. However, successful testing of FeAl alloys on an industrial scale was still pending at the beginning of the project. Therefore, the aim of the project was to develop simulation based casting concepts for industrial casting processes using the base alloy Fe-26Al-4Mo-0.5Ti-1B and to narrow down process limits by means of hot cracking tests. Findings were transferred into practice-oriented guidelines for casting of iron aluminides, which is accessible to future applicants in SMEs. The focus was placed on centrifugal casting combined with investment casting or die casting. In addition to numerous design and casting process parameters, heat treatments and alloying additions (Al, Mo, B) were varied to determine the influence of alloying elements on castability, microstructure and mechanical properties. Data from microstructure analyses (microscopic imaging, determination of grain sizes as well as phase compositions and volume fractions, fractography), mechanical tests (hardness measurements, compression tests, ambient and high-temperature tensile tests, creep tests) as well as measurements of thermophysical properties could be generated on the base alloy. Correlations of materials data with process variables allowed conclusions to be drawn on strengthening mechanisms and ductility of the alloy and how they can be controlled in terms of processing and component design. Successful casting of highly complex components with thin wall thicknesses and optimised alloy compositions points out prospects for new fields of application. N2 - Die zunehmende geopolitische Bedeutung der Ressourcenverfügbarkeit sowie die Anforderungen an einen geschlossenen Materialkreislauf treiben die Materialforschung voran, um konventionelle Werkstoffe mit weniger kritischen Zusätzen zu legieren oder sogar vollständig mit nachhaltigeren Alternativen zu substituieren. Eine potenzielle Alternative stellen die intermetallischen Eisenaluminid-Legierungen (FeAl) dar. Im Labormaßstab wurden bereits viele Legierungskonzepte für verbesserte Hochtemperatureigenschaften oder Duktilität erfolgreich gießtechnisch umgesetzt. Eine erfolgreiche Erprobung von FeAl-Legierungen im industriellen Maßstab stand zu Beginn des Projekts aber weiterhin aus. Ziel des Vorhabens war daher die Entwicklung von simulationsgestützten Gießkonzepten in industrienahe Gießprozesse anhand der Modelllegierung Fe-26Al-4Mo-0,5Ti-1B und die Eingrenzung der prozesstechnischen Verfahrensgrenzen durch Warmrissversuche. Erkenntnisse hieraus wurden in einen praxisorientierten, für zukünftige Anwender in KMUs zugänglichen Handlungskatalog für die gießgerechte Auslegung von Bauteilen aus Eisenaluminiden überführt. Fokus wurde insbesondere auf das Feinguss- und Kokillengussverfahren im Schleuderguss gesetzt. Neben zahlreicher Konstruktions- und Gießprozessparameter wurden auch Wärmebehandlungen und Legierungszusätze (Al, Mo, B) variiert, um den Einfluss von Legierungselementen auf Gießbarkeit, Mikrostruktur und mechanische Kennwerte zu bestimmen. Eine umfangreiche Basis an Daten aus Mikrostrukturanalysen (Mikroskopische Bildgebung, Bestimmung von Korngrößen sowie Phasenzusammensetzungen und -anteilen, Fraktographie), mechanischen Tests (Härtemessungen, Druckversuch, Zugversuch, Warmzugversuch, Kriechversuch) sowie Messungen thermophysikalischer Eigenschaften konnte für die Modelllegierung erzeugt werden. Korrelationen dieser Informationen mit Prozessvariablen erlaubten Schlussfolgerungen zu Härtungsmechanismen und Duktilität in der Legierung und wie sie prozesstechnisch in Gieß- und Bauteilauslegung gesteuert werden können. Der erfolgreiche Abguss von hochkomplexen Bauteilgeometrien mit dünnen Wandstärken sowie optimierte Legierungszusammensetzungen zeigen Perspektiven auf neue Anwendungsfelder auf. T2 - FVV Transfer + Netzwerktreffen | Informationstagung – Frühjahr 2023 CY - Würzburg, Germany DA - 29.03.2023 KW - Fe-Al alloys KW - Intermetallics KW - Iron aluminides KW - Microstructure-property-correlation KW - High temperature mechanical properties KW - Creep data KW - Tensile data KW - Fractography KW - Casting PY - 2023 VL - R604 SP - 1 EP - 32 PB - FVV e. V. CY - Frankfurt a.M. AN - OPUS4-57247 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hodoroaba, Vasile-Dan T1 - External Liaison Report ISO/TC 202 'Microbeam Analysis' to ISO/TC 229 'Nanotechnologies' N2 - The liaison report from the ISO Technical Committee ISO/TC 202 'Microbeam Analysis' for the November 2022 ISO/TC 229 Nanotechnologies Plenary Meeting Nanotechnologies Liaison Coordination Group (NLCG) is provided. Essential Information such as newly published standards and projects in develeopment relevant for ISO/TC 229 resulted from the progress within the last year and additional comments on behalf of ISO/TC 202 are included in the report. KW - ISO/TC 202 KW - ISO/TC 229 KW - VAMAS KW - Nanotechnologies KW - Microbeam Analysis KW - Standardisation PY - 2022 SP - 1 EP - 4 CY - ISO, Geneva, CH AN - OPUS4-56734 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Sonntag, Nadja A1 - Jürgens, M. A1 - Uhlemann, Patrick A1 - Skrotzki, Birgit A1 - Olbricht, Jürgen T1 - Datasets for Service-Like Creep-Fatigue Experiments on Grade P92 Steel N2 - The dataset contains experimental mechanical data from complex service-like creep-fatigue experiments performed isothermally at 620 °C and a low strain amplitude of 0.2 % on tempered martensite-ferritic grade P92 steel. The data sets in text file format provide cyclic deformation (min. and max. stresses) and the total (hysteresis) data of all recorded fatigue cycles for three different creep-fatigue experiments: 1) a standard relaxation fatigue (RF) test with symmetrical dwell times of three minutes introduced at minimum and maximum strain, 2) a fully strain-controlled service-like relaxation (SLR) test combining these three-minute peak strain dwells with a 30-minute dwell in between at zero strain, and 3) a partly stress-controlled service-like creep (SLC) test combining the three-minute peak strain dwells with 30-minute dwells at constant stress. Further information on data and data acquisition, analysis, and experimental details are given in “Experimental Data from Service-Like Creep-Fatigue Experiments on Grade P92 Steel”, submitted to Data in Brief. Additional analyses of these datasets, as well as experimental findings and discussions are presented in “Creep-Fatigue of P92 in Service-Like Tests with Combined Stress- and Strain-Controlled Dwell Times”, submitted to International Journal of Fatigue. KW - Creep-fatigue KW - Stress relaxation KW - Dwell-Fatigue KW - Tempered martensite-ferritic steel PY - 2022 DO - https://doi.org/10.5281/zenodo.7198218 PB - Zenodo CY - Geneva AN - OPUS4-55995 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hodoroaba, Vasile-Dan T1 - Delivering Impact - A new ISO standard on the identification of nanoparticles N2 - Nanoparticles (NPs) are tiny – around 1 to 100 billionths of a meter – and can have different chemistries and behaviours than the same material of larger size. This property has led to advances in a wide range of industries, but it can also confer toxicity. Size measurements are the main way NPs are identified but a lack of standardised methods for identifying ones with complex shapes has hindered evaluation of their potential harm. KW - Nanoparticles KW - Standardisation KW - Particle size distribution KW - nPSize KW - ISO 21363 PY - 2024 UR - https://www.euramet.org/casestudies/casestudiesdetails/news/default-c3b26209e8 SP - 1 EP - 2 PB - EURAMET CY - Braunschweig AN - OPUS4-59626 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Popiela, Bartosz T1 - Einfluss fertigungsbedingter Eigenspannungen auf die Betriebssicherheit von nassgewickelten Composite-Druckbehältern mit einem nichttragenden Liner N2 - Im Hinblick auf die globale Herausforderung der Energietransformation steigt der Bedarf an Möglichkeiten zur Energiespeicherung. Eine Technologie, die zunehmend in den Fokus rückt, ist die Energiespeicherung mittels komprimiertem Wasserstoffgas. Insbesondere für mobile und Transport-Anwendungen ist eine geringe Masse des Speichers vorteilhaft, weshalb vollumwickelte Composite-Druckbehälter des Typs 4 zum Einsatz kommen. Diese werden überwiegend im Nasswickelverfahren gefertigt, das durch zahlreiche Prozessparameter und physikalische Effekte charakterisiert wird. Die Wahl der Wickelprozessparameter sowie Schwankungen der Materialkennwerte beeinflussen den Eigenspannungszustand in der Composite-Struktur eines Druckbehälters. Somit wirken sie sich auch auf den Spannungszustand im Betrieb aus. Die vorliegende Dissertation beinhaltet Untersuchungen des Einflusses von fertigungsbedingten Eigenspannungen auf die Sicherheit von Composite-Druckbehältern mit nichttragendem Kunststoff-Liner. Ziel ist es, das mechanische Verhalten von Composite-Druckbehältern besser zu verstehen und deren Sicherheitsniveau sowie Konkurrenzfähigkeit weiter zu steigern. Schwerpunkte der Arbeit sind experimentelle Untersuchungen der Eigenspannungsentstehung und -entwicklung sowie deren Einfluss auf die Behälter-Sicherheit. Im Fokus befindet sich die Exploration von Möglichkeiten zur Verbesserung der Zuverlässigkeit der Behälter durch Variation der Fertigungsparameter und eine Konditionierung nach der Fertigung. Der Eigenspannungszustand wird in numerischen Simulationen sowie mit dem zerstörenden Bohrlochverfahren charakterisiert. Die Überwachung der Spannungsumlagerung während einer Konditionierung unter Zeitstandbelastung erfolgt mit eingebetteten faseroptischen Sensoren, die später zur Dehnungsmessung in zerstörenden, langsamen Berstprüfungen eingesetzt werden. Zur Vertiefung des Verständnisses des Versagensverhaltens der verwendeten 6,8 l-Druckbehälter wird die Finite-Elemente-Methode eingesetzt. Darüber hinaus werden Qualitätsuntersuchungen der Composite-Struktur mittels Mikro-Computertomographie und Impuls-Echo-Verfahren beschrieben. Die Ergebnisse der Untersuchungen zeigen, dass eine Steigerung der Zuverlässigkeit durch eine gezielte Innendruckbeanspruchung der gewickelten Behälter nahezu kostenneutral möglich ist. Dies wird im Rahmen der Arbeit anhand eines Baumusters demonstriert. Darüber hinaus wird die Verbesserung der Zuverlässigkeit der Behälter im Rahmen einer Konditionierung unter Zeitstandbelastung vertieft diskutiert. Diese stellt eine weiterführende Möglichkeit dar, das Behälterverhalten positiv zu beeinflussen und das Sicherheitsniveau zu steigern. N2 - Considering the global challenge of energy transformation, the demand for energy storage solutions is increasing. One of the technologies, which is gaining attention, is the storage of hydrogen gas under high operating pressures. Particularly for on-board and transport applications, lightweight storage systems are advantageous. Therefore, fully wrapped composite pressure vessels of Type 4 are increasingly used. These are mostly manufactured using the wet filament winding process, which is characterized by numerous process parameters and physical effects. The choice of winding process parameters and variations in material properties influence the residual stress state in the finished component and thus also the stress state under operational loads. This dissertation includes insights into the impact of manufacturing-induced residual stresses on the safety of Type 4 pressure vessels, which contribute to a deeper understanding of the mechanical behavior of composite pressure vessels and support the further enhancement of safety levels and competitiveness. The work focuses on experimental investigations of the induction and development of residual stresses and their impact on the safety of the composite pressure vessels. A core of the dissertation is an exploration of the possibilities to improve pressure vessel performance through variation of manufacturing parameters and conditioning after manufacturing. The residual stress state is characterized in numerical simulations as well as with the destructive hole-drilling method. Embedded fiber optic sensors are used for the monitoring of stress redistribution during conditioning. The fiber optic sensors are later used for strain measurement in destructive, slow burst tests. Finite element analyses are performed to deepen the understanding of the failure behavior of the used 6.8-liter pressure vessels. Additionally, quality investigations of the composite structure using micro-computed tomography and impulse-echo ultrasonic propagation imaging are described. The results of the investigations show that an increase in performance is possible through targeted internal pressure regulation during the winding process pressure vessels. This is demonstrated almost cost-neutrally, i.e., without increasing process time and material usage. Furthermore, the improvement of vessel performance through conditioning under increased pressure and temperature is discussed in depth. This represents a further possibility to favorably influence vessel behavior and enhance safety levels. KW - Composite KW - Druckbehälter KW - Eigenspannung KW - Faserverstärkter Kunststoff KW - Nasswickelverfahren PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:co1-opus4-72383 DO - https://doi.org/10.26127/BTUOpen-7238 SP - 1 EP - 153 CY - Cottbus, Deutschland AN - OPUS4-65348 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Strangfeld, Christoph A1 - Maack, Stefan T1 - Grundlagenuntersuchungen zur Anregung von niederfrequentem Ultraschall mit fluidischen Bauteilen N2 - Die zerstörungsfreie Prüfung (ZFP) mittels Ultraschalls wird häufig im Bauwesen eingesetzt, um innere Defekte in Betonstrukturen zu erkennen. Dabei werden Ultraschallwellen im Frequenzbereich von 50 bis 200 kHz genutzt, um Schäden zu entdecken, ohne das Material zu beschädigen. Die meisten derzeit verwendeten Geräte müssen direkten Kontakt mit der Oberfläche haben, was bei großen Bauwerken sehr zeitaufwendig und umständlich ist. Deshalb wird nach alternativen Lösungen gesucht, wie zum Beispiel die luftgekoppelte Ultraschalltechnik, bei der Luft als Übertragungsmedium dient. Solche Geräte könnten die Messzeit um das 50- bis 100-fache verkürzen, was die Inspektion ganzer Strukturen wie Tunnel oder Brücken ermöglichen würde. Dies würde eine zuverlässige Bewertung des Zustands der Infra-struktur erleichtern. Allerdings führt die große Impedanzdifferenz zwischen dem Transducer und der Luft zu erheblichen Energieverlusten, was die Signalstärke schwächt. Geräte, die auf dünnen Membranen oder laserinduzierter Signalanregung basieren, sind oft nicht robust genug für den rauen Baustellenbetrieb. Eine potentielle Lösung sind sogenannte fluidische Oszillatoren, die in der Strömungskontrolle sowie beim Kühlen und Mischen von Flüssigkeiten eingesetzt werden. Sie erzeugen komplett ohne bewegliche Teile schwingende Strömungen, indem sie selbstangeregte Strömungsinstabilitäten nutzen, bei denen der Freistrahl zwischen zwei Kammerwänden durch Feedback-Kanäle hin und her schwingt. Dabei entstehen zeitlich und räumlich schwingende Strömungen am Ausgang. Kleinere Oszillatoren können höhere Frequenzen bis zu 50 kHz erzeugen. Die Frequenz lässt sich durch den Versorgungsdruck steuern, entweder direkt oder über ein Ventil, was die Erzeugung von frequenzmodulierten Signalen ermöglicht. Solche Geräte könnten bei der Untersuchung von Betonelementen eingesetzt werden, um die Dicke und innere Delaminationen zu bestimmen. Die Düsen sind klein, robust und können aus Keramik oder Stahl gefertigt werden, was sie ideal für den Einsatz auf der Baustelle macht. Im Rahmen dieses Projekts wurden fluidische Oszillatoren an der BAM entwickelt, hergestellt und getestet. Dabei wurden die Frequenzinhalte, die Frequenzbandbreite und die Schalldruckamplitude experimentell untersucht. Akustische Messungen mit Mikrophonen sowie erste Tests an Betonproben wurden durchgeführt. Die Düsen wurden geometrisch skaliert, um die Mittenfrequenz und die Schalldruckamplitude zu optimieren. Mit Hilfe von hochfrequenten Druckregeln konnten frequenzmodulierte Anregungssignale (Chirps) erzeugt werden. Die momentan erreichte Frequenzbandbreite von ca. 10 % stellte sich als zu gering heraus für reproduzierbare und statistisch abgesicherte Ultraschall-Messungen durch Beton. KW - Luftgekoppelter Ultraschall KW - Fluidischer Oszillator KW - Verkehrsinfrastruktur PY - 2025 SP - 1 EP - 10 AN - OPUS4-65346 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Widjaja, Martinus Putra A1 - Moosavi, Robabeh A1 - John, Sebastian A1 - Schumacher, David A1 - Grunwald, Marcel A1 - Auster, Jürgen A1 - Szczepaniak, Marius A1 - Mair, Georg W. A1 - Waske, Anja T1 - Impact damage evaluation of hydrogen composite pressure vessels by analysing computed tomography images N2 - The objective of this work is to find a method that describes the degree of damage from an impact experiment. This experiment was performed on Composite Pressure Vessels (CPV) in order to find the correlation of impact damage to the residual burst pressure. Computed Tomography (CT) approach was used to capture the before and after impact condition of the CPVs. The Wasserstein function was used to calculate how much the after impact image has differed from the original one. In the end, a good correlation was obtained to the residual burst pressure. T2 - HyFiSyn Conference CY - Online meeting DA - 15.09.2021 KW - Hydrogen KW - Composite pressure vessel KW - Carbon fibre KW - Burst test KW - Image analysis KW - Computed tomography (CT) PY - 2021 SP - 31 EP - 32 AN - OPUS4-53494 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Le, Quynh Hoa A1 - Bäßler, Ralph A1 - Kratzig, Andreas A1 - Bettge, Dirk A1 - Kranzmann, Axel A1 - Knauer, S. T1 - Droplet corrosion of CO2 transport pipeline steels N2 - In this work, the focus was set on the corrosion process of condensate as drops on the surface of carbon steels (X52, X70), martensitic steel UNS S41500, and superaustenite UNS N08031 in CO2 atmosphere with impurities at 278 K (to simulate the transportation condition in a buried pipeline). Exposure tests were performed at both normal pressure and high pressure where CO2 is supercritical or in dense phase. The drop, 1 ‑ 10 μL in volume, was prepared by dropping CO2 saturated ultra-pure water onto the surface of steel coupons in a one-liter-autoclave. The CO2 gas stream, simulating the oxyfuel flue gas with varying concentration of impurities (SO2 and O2 ), was then pumped into the autoclave to observe the condensation and corrosion impacts of impurities. Comparable exposure tests were carried out with the same gas mixture and the same volume of water as vapor to observe the drop formation and the corrosion process that follows. The wettability and stability of drops on the surface of steel coupons in CO2 supercritical/dense phase environment was evaluated additionally by contact angle measurement. T2 - NACE International Annual Corrosion Conference CY - Phoenix, AZ, USA DA - 15.04.2018 KW - Geothermal KW - Coating KW - SiO2 KW - Polyaniline KW - Corrosion PY - 2018 SP - 10845, 1 EP - 11 PB - Omnipress CY - Houston AN - OPUS4-44917 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Yevtushenko, Oleksandra A1 - Carillo Salgado, I. T1 - Corrosion behavior of highly alloyed steels in artificial saline aquifer fluids containing carbon dioxide N2 - C02-corrosion on piping steels might cause problems during injection of flue gases for their storage in deep geological aquifer fluids. Therefore, the selection of appropriate piping steels is a key factor to increase safety and reliability of the Carbon Capture and Storage (CCS) technology, and to keep the process cost-efficient. Within the project COORAL (German acronym for “C02 purity for capture and storage”) corrosion studies on injection piping steels exposed to C02 and artificial brine with high Chloride concentration have been carried out. Corrosion of the injection pipe in C02-rich aquifer fluid may occur within the aquifer brine or when at injection interruptions the aquifer fluid may flow back into the injection pipe. Because of high salinity of aquifer brine and C02-corrosion an appropriate material ranking of injection piping steels should be made. Corrosion resistance of steels 1.4034, 1.4021, 1.4542, 1.4162 and 1.4562 was investigated in a corrosive environment using electrochemical and metallographic techniques. Electrochemical experiments in order to investigate the surface corrosion kinetics and polarization measurements in order to investigate localized corrosion phenomena have been carried out. Critical pitting potentials and repassivation potentials were determined by polarization curves of investigated materials and compared with measured corrosion potentials. Measured values were used in order to determine the suitability and performance of tested steels in C02-injection conditions. T2 - Latincorr 2014 - IX Latin American congress of corrosion CY - Medellín, Colombia DA - 28.10.2014 KW - Highly alloyed steels KW - Carbon dioxide KW - Pitting corrosion PY - 2014 SP - Paper 2445981, 1 EP - 5 AN - OPUS4-32746 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rütters, H. A1 - Fischer, S. A1 - Le, Quynh A1 - Bettge, Dirk A1 - Bäßler, Ralph A1 - Maßmann, J. A1 - Ostertag-Henning, C. A1 - Wolf, J. Lennard A1 - Pumpa, M. A1 - Lubenau, U. A1 - Knauer, S. A1 - Jaeger, P. A1 - Neumann, A. A1 - Svensson, K. A1 - Lempp, C. A1 - Menezes, F. A1 - Hagemann, B. T1 - Towards defining reasonable minimum composition thresholds – impacts of variable CO2 stream compositions on transport, injection and storage N2 - The collaborative project “Impacts of impurities in CO2 streams captured from different emitters in a regional cluster on transport, injection and storage (CLUSTER)” aimed to set up recommendations on how to define “reasonable minimum composition thresholds” that CO2 streams should meet when accessing CO2 transport pipeline networks. Within CLUSTER, we investigated potential impacts of CO2 streams with different and temporally variable compositions and mass flow rates along the whole CCS chain. Investigations included, amongst others, impacts on: Corrosion of pipeline steel, pipeline network design and related transport costs, alteration of well bore cements, pressure development and rock integrity, geochemical reactions, and petrophysical and geomechanical rock properties. All investigations are based on a generic CCS chain scenario. In this scenario, CO2 streams are captured from a spatial cluster of eleven emitters and collected in a regional pipeline network. Emitters comprise seven fossil fuel-fired power plants equipped with different capture technologies, two cement plants, one refinery and one integrated iron and steel plant. In total, 19.78 Mio t CO2 (including impurities) are captured in the emitter cluster annually. The combined CO2 stream is transported in a trunk line with a length of 400 km (100 km of these offshore) and is injected into five generic storage structures. The storage reservoirs are saline aquifers of the Buntsandstein. The investigations revealed beneficial and deteriorating impacts of different impurities and combinations thereof. Overall, no fundamental technical obstacles for transporting, injecting and storing CO2 streams of the modelled variable compositions and mass flow rates were observed. Based on the results, the CLUSTER project team recommends not to define “minimum composition thresholds” for CO2 streams as strict threshold values for each individual impurity in the stream. Instead, CO2 stream compositions and variabilities for specific CCS projects should be constrained with regard to a set of parameters including i) the overall CO2 content, ii) maximum contents of relevant impurities or elements, iii) acceptable variability of CO2 stream composition, and iv) impurity combinations to be avoided. T2 - 15th International Conference on Greenhouse Gas Control Technologies, GHGT-15 CY - Online meeting DA - 15.03.2021 KW - Corrosion KW - Impurities KW - CO2 quality KW - Pipeline network KW - Whole-chain CCS scenario KW - Recommendations PY - 2021 DO - https://doi.org/10.2139/ssrn.3816427 SP - 1 EP - 18 AN - OPUS4-52418 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Bäßler, Ralph A1 - Werner, H. A1 - Alves, H. A1 - Behrens, R. T1 - Corrosion-resistant higher-alloyed metallic materials for the transport of corrosive dangerous goods in tanks T2 - CORROSION 2006 CY - San Diego, CA, USA DA - 2006-03-12 KW - BAM-List KW - Dangerous goods KW - High-alloyed metallic tank materials KW - Corrosion tests KW - Korrosionsbeständigkeit KW - Tankwerkstoffe KW - Korrosionsuntersuchungen KW - Höherlegierte metallische Werkstoffe KW - BAM-Liste PY - 2006 SP - 06688/1 EP - 06688/12 PB - NACE CY - San Diego AN - OPUS4-12281 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Burkert, Andreas A1 - Eich, Gerd T1 - Portable Equipment for Determination of Corrosion Stage of Concrete Structures - Comparison of Laboratory and On-Site Experiences T2 - Western States Corrosion Seminar : 40th CY - San Diego, CA, USA DA - 2006-03-12 KW - Galvanostatic Pulse KW - Reinforcement Corrosion KW - Corrosion Rate PY - 2006 SP - 06407\1 EP - 06407\11 PB - NACE CY - Houston AN - OPUS4-12151 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Bäßler, Ralph T1 - Bewertung der Beständigkeit von hochlegierten Sonderedelstählen und Nickellegierungen für den Transport von Gefahrgütern T2 - 8. Dresdener Korrosionsschutztage CY - Dresden, Deutschland DA - 2007-10-24 KW - Korrosionsbeständigkeit KW - Korrosionsuntersuchungen KW - Sonderedelstähle KW - Nickellegierungen KW - Gefahrgüter KW - BAM-Liste PY - 2007 IS - (Teil 1) SP - 1 EP - 16 CY - Dresden AN - OPUS4-16077 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Burkert, Andreas A1 - Eich, Gerd A1 - Bäßler, Ralph A1 - Isecke, Bernd T1 - Corrosion Monitoring im Bauwesen T2 - 29. Darmstädter Massivbauseminar, "Sicherheitsgewinn durch Monitoring?" CY - Darmstadt, Germany DA - 2006-09-14 KW - Potentialfeldmessung KW - Galvanische Pulsmessung KW - Feuchtemessung KW - Korrosionssensoren PY - 2006 SP - 115 EP - 135 PB - Freunde des Instituts für Massivbau der Technischen Universität Darmstadt CY - Darmstadt AN - OPUS4-13719 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Burkert, Annette A1 - Eich, Gerd A1 - Mietz, Jürgen T1 - Galvanized constructional elements in contact with prestressing steel tendons T2 - 22nd International Galvanizing Conference CY - Madrid, Spain DA - 2009-06-08 KW - Prestressed concrete KW - Prestressing steel KW - Hydrogen-induced stress corrosion cracking KW - Galvanized construction elements PY - 2009 SP - 1 EP - 11 AN - OPUS4-20700 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Gerrits, Ruben T1 - An experimental study of fungal olivine weathering N2 - Free-living and (ecto)-mycorrhizal fungi enhance rock weathering. In their roles as mineral weathering agents and mutualistic partners of phototrophs, fungi supply primary producers like plants and phototrophic microorganisms with mineral-derived nutrients. The exact mechanisms behind fungus-induced mineral weathering processes are however not well understood. Progress can be achieved here by reproducible experimental simulations of the natural processes, using well-characterised model organisms and minerals. In this study, the weathering-affecting, rock-inhabiting fungus, Knufia petricola A95 and the Fe-bearing olivine (Fe0.2Mg1.8SiO4) were selected to investigate fungi-induced effects on mineral dissolution. The availability of a melanin-deficient mutant (ΔKppks) of K. petricola A95, that produced more extracellular polymeric substances (EPS) than the wild type (WT), enabled comparative studies of the role of melanin and EPS in weathering processes. Three experimental systems, which generate long-term microbiological stability, were developed to study the impact of the WT and ΔKppks on olivine weathering: (1) batch and (2) mixed flow dissolution experiments, and (3) biofilm cultivation experiments. In addition, state-of-the-art analytical techniques were used to monitor changes in the growth medium, as well as of the mineral surface and biofilm-mineral interface. Inductively coupled plasma optical emission spectrometry (ICP-OES) analysis of the Mg, Si and Fe concentrations in the reacted growth medium was used to quantify olivine dissolution. In abiotic controls, Mg and Si dissolved congruently, while Fe precipitated. The measured olivine dissolution rates at pH 6 were two orders of magnitude lower than previously reported, but similar at acidic pH. X-ray photoelectron spectroscopy (XPS) analyses of the olivine surface confirmed the presence of Fe (oxyhydr)oxide precipitates. Transmission electron microscopy (TEM) imaging of an abiotically reacted polished olivine section from the long-term cultivation experiment showed the presence of an amorphous layer enriched in Fe. All these observations indicate that the precipitation of Fe (oxyhydr)oxides on the olivine surface inhibits olivine dissolution. Both tested rock-inhabiting fungal strains affect Fe precipitation as well as olivine dissolution. Evaluation of the WT and ΔKppks revealed that the WT formed less biomass but could take up higher amounts of metals (e.g. Fe) and was more efficient in its attachment to olivine. The WT and ΔKppks enhanced olivine dissolution as demonstrated by higher Mg and Si concentration in the reacted growth medium. They furthermore prevented Fe precipitation by binding Fe and retaining it in solution, thereby allowing olivine dissolution to proceed. The WT cells that were attached to the olivine surface were particularly efficient at inhibiting Fe precipitation. By binding Fe directly at the olivine surface, the WT cells removed the inhibition of olivine dissolution almost completely. TEM analysis of polished olivine sections, colonised by a fungal biofilm for seven months, supported this hypothesis. After long-term fungus-olivine interaction, the Fe-enriched, amorphous layer did not develop, and the olivine surface was stronger etched compared to the abiotic control. To study the effect of mutualism on mineral weathering, K. petricola was grown with the cyanobacterium, Nostoc punctiforme ATCC 29133. Both partners showed an enhanced growth and formed a stratified biofilm which attached more strongly to olivine. Nevertheless, the olivine dissolution rate of the fungus-cyanobacterium consortium was moderate. Rock weathering simulation systems developed here are promising research instruments. The experimental conditions allow for the alteration of the studied mineral surface, while the clear definition of these conditions delivers a stable growth of microorganisms. The latter makes these systems universally applicable, especially in combination with integrative multidisciplinary analytics. Processes underlying environmental and biological effects on rock weathering, metal corrosion, plastic degradation, or the deterioration of any other substrate can be studied reproducibly and over a long period of time. The chemical and biological complexity of these simulation systems mimics natural rock weathering processes. The mineral dissolution rates generated in this study are therefore relevant to natural ecosystems. KW - Olivine KW - Weathering KW - Fungus PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:188-refubium-25125-1 DO - https://doi.org/10.17169/refubium-2880 SP - 1 EP - 178 PB - Freie Universität Berlin CY - Berlin AN - OPUS4-48825 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Le, Quynh Hoa A1 - Yevtushenko, Oleksandra A1 - Bettge, Dirk T1 - Corrosion Aspects for Materials to be Used in CC(U)S Applications N2 - This contribution provides current findings regarding materials susceptibility for carbon capture, utilization and storage (CCUS) applications. Basing on results gathered in 2 German long-term projects (COORAL and CLUSTER) suitable materials are introduced as well as dominating impurities of the CO2-stream and corrosion mechanisms. Investigations cover the whole CCUS process chain and provide material recommendations for certain parts. T2 - 1st International Conference on Corrosion Protection and Application CY - Chongqing, China DA - 09.10.2019 KW - Carbon KW - Capture KW - Storage KW - Utilization KW - CCS KW - CCU KW - CO2 KW - Corrosion KW - Steel PY - 2019 SP - Paper 31 PB - Chinese Society for Corrosion and Protection CY - Chongqing/China AN - OPUS4-49301 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Alves, H. A1 - Bäßler, Ralph T1 - New results on the selection of Nickel alloys and a 6% Mo special stainless steel for high temperature acid service T2 - NACE International corrosion conference 2009 CY - Atlanta, Georgia, USA DA - 2009-03-22 KW - Alloy 59 (UNS N06059) KW - Alloy 31 (UNS N08031) KW - Alloy B-2 (UNS N10665) KW - Inorganic acids KW - Organic acids KW - Corrosion PY - 2009 SP - 1 EP - 18 (Paper 09369) AN - OPUS4-19250 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Keserovic, Amela A1 - Sobetzki, Joana A1 - Sarmiento Klapper, Helmuth T1 - Materials evaluation for geothermal applications N2 - The corrosion behavior of different high-alloyed metals including duplex and austenitic stainless steels as well as a nickel alloy have been evaluated in artificial geothermal fluids simulating the conditions in some locations with geothermal potential in Germany as well as two sites in Indonesia. The suitability of low alloyed steel UNS G41300, stainless steels UNS S31603 UNS S31803, UNS S32760 and super austenitic steel UNS N08031 in these geothermal fluids, investigated by electrochemical measurements and exposure tests, is limited. The nickel based alloy UNS N06059 shows excellent corrosion resistance against pitting corrosion. Excluding its high cost, it is a very good alternative to be used in the construction of geothermal facilities having highly saline brines. Stainless and duplex steels exhibit a limited corrosion resistance concerning pitting and crevice corrosion. Beside of the higher alloyed materials, also the low-alloyed steel UNS G41300 could be employed as a constructional material for the geothermal power plant in non-saline environments, as long as the wall thickness of the material vs. corrosion rate is taken into account. T2 - ISCMD 2014 - International symposium on corrosion & materials degradation 2014 / IMTCE 2014 - 9th International materials technology conference & exhibition CY - Kuala Lumpur, Malaysia DA - 13.05.2014 KW - Localized corrosion KW - Stainless steel KW - Ni-based alloy KW - Geothermal energy PY - 2014 SP - Paper 10, 1 EP - 9 AN - OPUS4-30775 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Aristia, Gabriela A1 - Bäßler, Ralph T1 - A Coating System for Corrosion Protection of Carbon Steel as an Alternative for High Alloyed Materials N2 - Corrosive geothermal brines are a major challenge to geothermal power-plants. For cost reasons, plant designers favorize low alloyed steels, e.g., carbon steel, which are susceptible to uniform and localized corrosion when exposed to geothermal brines having acidic and saline properties. To solve such problem, coatings or inhibitors would be a protective solution as an alternative to the use of high alloyed materials. This study investigated a coating system consisting of polyaniline/silicon dioxide basing on locally available resources. Protection against corrosion of carbon steel is shown by long-term exposure and electrochemical tests of coated carbon steels, performed in an artificial acidic and saline geothermal brine, comparable to real conditions at a site in Indonesia. Therefore, an integrated coating system is presented for corrosion protection, combining the electro-chemical functionality of polyaniline and the physical advantages of silica. T2 - European Geothermal Congress CY - Berlin, Germany DA - 17.10.22 KW - Corrosion KW - Geothermal KW - Coatings KW - Polyaniniline KW - Silicate PY - 2022 SP - 1 EP - 7 CY - Berlin AN - OPUS4-56085 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Bäßler, Ralph A1 - Otremba, Frank T1 - Use of higher-alloyed metallic materials and duplex steels for transport tanks of dangerous goods N2 - Compatibility evaluations of selected metallic materials under the influence of dangerous goods are published in the BAM-List - Requirements for Tanks for the Transport of Dangerous Goods” as basis for substance-related prototype approvals for tank Containers designed for the carriage of dangerous goods. There is a request of the tank manufacturing industry and transportation Companies to incorporate additional materials into the BAM-List, especially corrosion-resistant materials because of the large number of corrosive dangerous goods. One solution to solve corrosion Problems is to line the tank with a polymer, an alternative solution is the application of high-alloyed stainless steels and nickel-based alloys as there are 1.4529 (XINiCrMoCu 25-20-7, alloy 926), 1.4562 (X1NiCrMoCu32-28-7, alloy 31) and 2.4605 (NiCr23Mo16AI, alloy 59). There is an interest to use cost-efficient steels with high strength values and concomitant adequate corrosion resistance such as duplex steel 1.4362 (X2CrNiN23-4). This steel grade was originally developed as a substitute for the austenitic grades 1.4404 (X2CrNiMo17-12-2) and 1.4571 (X6CrNiMoTi17-12-2). Due to the lower content of the alloy elements nickel and molybdenum this duplex steel is a cost-efficient alternative to molybdenum containing austenite. Due to the limited number of corrosion test results with welded test samples of these high-alloyed materials and the duplex steel under the influence of corrosive dangerous goods a comprehensive test Programme was performed with these materials in Cooperation with ThyssenKrupp VDM and Deutsche Edelstahlwerke GmbH. It can be concluded from the test results that the superaustenitic steels 1.4529 and 1.4562 as well as the nickel-based alloy 2.4605 are a really good alternative as tank materials for the transport of dangerous goods in comparison to the lining of the tanks. The nickel-based alloy 2.4605 shows the best resistance and is suitable as material for tanks transporting all tested corrosive substances. One exception is the temperature limit during the transport of hydrochloric acid. The superaustenit 1.4562 is a resistant material with a wide ränge of application. Exceptions for use are: ammonium bifluoride, brine, 34 % calcium Chloride solution, hydrochloric acid, perchloric acid, 90 % 2-chloropropionic acid, nitrating acid with nitric acid content > 50 % and molten monochloroacetic acid. The alloy is limited suitable for allyl Chloride, aluminum Chloride, copper (II) -Chloride and ferric Chloride. The superaustenit 1.4529 showed the lowest resistance compared to the other two materials. This steel is not resistant in hydrochloric acid, perchloric acid, sodium Chlorite and sodium hypochlorite. The application is limited in the concentration ränge of aqueous Solutions of aluminum Chloride, copper (II) Chloride and ferric Chloride. Due to the reduced alloying content of the duplex steel 1.4362 (X2CrNiN23-4) compared to the austenitic CrNiMo-steels, a lower resistance especially in acidic media like formic, acetic or sulfuric acid was observed. Within the more than 7.000 substances contained in the BAM-List there is a large amount of dangerous goods such as hydrocarbons, alcohols, aldehydes, ketones, ethers, esters, and inorganic alkaline substances which have a large transport volume and do not corrode the duplex steel 1.4362 (X2CrNiN23-4). The test results are included in the actual 11th edition of the BAM-List and therefore available for the costumer. T2 - Stainless steel world conference & exhibition 2011 CY - Maastricht, The Netherlands DA - 29.11.2011 KW - Duplexstahl KW - Tankcontainer KW - Tankfahrzeuge KW - Beständigkeitsbewertung KW - BAM-Liste PY - 2011 SP - 1 EP - 12 PB - KCI Publ. AN - OPUS4-24975 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Wolfram A1 - Brouwers, H.J.H. A1 - Kühne, Hans-Carsten A1 - Meng, Birgit ED - Wang, K. ED - Shah, S.P. ED - Khayat, K. T1 - Casting process improvement by optimization of mixture composition and high range water reducing agent modification N2 - Since its invention in the early 1990’s, self-consolidating concrete has never become well established in the ready-mix sectors worldwide. The reason for this can be mainly found in the fact that the sophisticated compositions are sensitive against changing environments. This lack of robustness can be attributed to the interaction between cement hydration reaction and high range water reducing agent (HRWRA). Understanding the relevant mechanisms that control the initial flow performance as well as the flow retention helps optimizing SCC mixtures that perform either steadily in one specific environment or that perform largely similarly at steadily changing environments. This paper depicts how HRWRAs interact with clinker and hydration phases and discusses the important role of the charge density of a polycarboxylic HRWRA in the way the rheology is affected. Based on rheometric results and observations of the Vicat setting times, it is shown that increasing charge densities of the HRWRA and decreasing water to powder ratios (w/p) reduce the flow retention and have lesser retarding effect on the setting. Based on the discussion, optimization procedures for the mixture composition and the HRWRA modification are suggested to achieve optimized performance for varying environmental situations or highest robustness for specific conditions. T2 - SCC 2013 - 5th North American conference on the design and use of self-consolidating concrete CY - Chicago, IL, USA DA - 12.05.2013 KW - Polycarboxylate KW - Cement hydration KW - Adsorption KW - Mixture composition KW - Environmental conditions PY - 2013 SP - 1 EP - 10 AN - OPUS4-28581 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Wolfram T1 - Potentials for savings in the production of self-compacting and high strength concrete for precast concrete elements N2 - Over the course of the last decades, concrete construction has significantly changed from mass application towards sophisticated more innovative, future oriented, and performance based materials technology. Today concrete no longer consists of cement, water, and aggregates, but can be enhanced significantly by using supplementary additions and chemical admixtures. Advancements in admixtures eventually facilitated the development of new concrete types such as self-compacting concrete (SCC) and high performance concrete (HPC) by uncoupling the workability from the water-cement ratio (w/c). While for traditional concrete types the major mixture parameter for the workability and strength were the w/c and the grading of the aggregates, for SCC and HPC the performance parameters are more complicated and the performance depends highly on the powder components. This makes the system more sophisticated and in parallel more prone to scatter during the production. The complexity and difficulty to predict the effects of changes in the process and mixture makes it very difficult to identify the right potentials for savings. T2 - ICCX Central Europe CY - Ossa, Poland DA - 11.02.2016 KW - Rheology KW - Self-compacting concrete KW - High strength concrete KW - Packing density KW - Superplasticizers PY - 2016 SP - 18 EP - 20 AN - OPUS4-36883 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Wolfram A1 - Grünewald, S. A1 - Ferrara, L. A1 - Dehn, F. T1 - Design of concrete for high flowability: progress report of fib task group 4.3 N2 - Flowable concretes can differ significantly from traditional vibrated concrete. Concrete types like self-compacting concrete (SCC), ultra high performance concrete (UHPC) and high performance fibre reinforced cementitious composites (HPFRCCs) require novel mix design approaches. This has consequences for the production and the performance in the hardened state. Mix designs for flowable concretes can incorporate a wide variety of innovative admixtures or components: e.g. superplasticisers increase the flowability and allow for significant reduction of the water content, shrinkage compensating admixtures or superabsorbent polymers support sound and damage free curing processes, viscosity modifying admixtures enhance the robustness, and new fibre types allow for sophisticated and tailored structural performance. The new Model Code has limitations regarding the application of flowable concrete, e.g. thresholds for the minimum aggregate size and the maximum strength. Provisions are added to include fibres for structural design. fib Task Group 4.3 aims at facilitating the use of innovative flowable materials for designing concrete structures and considers three aspects of flowable concrete: material properties, production effects and structural boundary conditions and performance. This paper reports about the progress of fib TG 4.3 related to the mix design of flowable concrete and discusses the present state-of-the-art concerning admixtures and robustness. T2 - fib Symposium (Proceedings) - Concrete - Innovation and design CY - Copenhagen, Denmark DA - 18.05.2015 KW - Admixtures KW - Fib model code KW - Fibres KW - Flowable concrete KW - Mix design KW - Robustness PY - 2015 SP - 1 EP - 10 AN - OPUS4-33800 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Janssen, Jan A1 - George, Janine A1 - Geiger, Julian A1 - Bercx, Marnik A1 - Wang, Xing A1 - Ertural, Christina A1 - Schaarschmidt, Joerg A1 - Ganose, Alex M. A1 - Pizzi, Giovanni A1 - Hickel, Tilmann A1 - Neugebauer, Joerg T1 - A Python workflow definition for computational materials design N2 - Numerous Workflow Management Systems (WfMS) have been developed in the field of computational materials science with different workflow formats, hindering interoperability and reproducibility of workflows in the field. To address this challenge, we introduce here the Python Workflow Definition (PWD) as a workflow exchange format to share workflows between Python-based WfMS, currently AiiDA, jobflow, and pyiron. This development is motivated by the similarity of these three Python-based WfMS, that represent the different workflow steps and data transferred between them as nodes and edges in a graph. With the PWD, we aim at fostering the interoperability and reproducibility between the different WfMS in the context of Findable, Accessible, Interoperable, Reusable (FAIR) workflows. To separate the scientific from the technical complexity, the PWD consists of three components: (1) a conda environment that specifies the software dependencies, (2) a Python module that contains the Python functions represented as nodes in the workflow graph, and (3) a workflow graph stored in the JavaScript Object Notation (JSON). The first version of the PWD supports directed acyclic graph (DAG)-based workflows. Thus, any DAG-based workflow defined in one of the three WfMS can be exported to the PWD and afterwards imported from the PWD to one of the other WfMS. After the import, the input parameters of the workflow can be adjusted and computing resources can be assigned to the workflow, before it is executed with the selected WfMS. This import from and export to the PWD is enabled by the PWD Python library that implements the PWD in AiiDA, jobflow, and pyiron. KW - Automation KW - Workflows KW - Materials Design KW - Multi-scale simulation KW - Digitalization PY - 2025 DO - https://doi.org/10.5281/zenodo.15516179 PB - Zenodo CY - Geneva AN - OPUS4-63233 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hickel, Tilmann A1 - Richter, Silke A1 - Bitzek, E. A1 - Ávila Calderón, Luis A1 - Gedsun, A. A1 - Forti, M. A1 - Hammerschmidt, T. A1 - Olbricht, Jürgen A1 - Skrotzki, Birgit T1 - NFDI-MatWerk/IUC02 Definition for Reference Data of Materials N2 - This definition was agreed within the infrastructure use case IUC02 “Framework for curation and distribution of reference datasets” of the consortium NFDI-MatWerk. It is broadly formulated to cover experimental and simulation MSE data and will be developed further in agreement with the MSE community. KW - Referenzdaten KW - Digitalisierung KW - NFDI-MatWerk KW - Research Data Management KW - Reference Data PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-611688 DO - https://doi.org/10.5281/zenodo.11667673 PB - Zenodo CY - Geneva AN - OPUS4-61168 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Schmidt, Wolfram A1 - Ramirez Caro, Alejandra A1 - Sojref, Regine A1 - Mota Gassó, Berta ED - Greim, M. ED - Kusterle, W. ED - Teubert, O. T1 - Contribution of the coarse aggregates to rheology - effects of flow coefficient, particle size distribution, and volume fraction N2 - In order to observe the effect of the aggregate phases between 2 mm and 16 mm without overlap with rheological effects induced by the cement hy-dration and without interactions with a threshold fine sand particle size that affects both, paste and aggregates, rheological experiments were conducted on a limestone filler based paste mixed with aggregates up to 16 mm. Vari-ous aggregate fractions were blended and mixed with the replacement paste in different volumetric ratios. The dry aggregates’ flow coefficients were determined and compared to yield stress and plastic viscosity values at different aggregate volume fractions. The results indicated that the flow coefficient is not a suitable parameter to predict the performance of the aggregates in the paste. It was shown that the yield stress of pastes is largely determined by the blend of different aggregate fractions, while the plastic viscosity to large extend depends upon the coars-est aggregate fraction. Based on the results, ideal aggregate composition ranges for minimised yield stress are presented. For the plastic viscosity no such grading curves to achieve minimum values could be found, but high viscosity curves are identified. KW - Rheology KW - Flow Coefficient KW - Particle Size Distribution KW - Volume Fraction KW - Cement KW - Concrete KW - Reference Material KW - Limestone Filler PY - 2018 SN - 978-3-7469-1878-5 SP - 96 EP - 108 PB - tredition GmbH CY - Hamburg AN - OPUS4-44434 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mezhov, Alexander A1 - Bright, Asante A1 - Schmidt, Wolfram T1 - Increasing the Incorporation of CO2-Sequestering Materials in Concrete N2 - Concrete is the most widely used construction material accounting for approximately half of all human production throughout history. The production of one ton of cement emits around 600 kg of CO2. With a global cement production estimate of 4.2 billion tons, this results in about 2.5 billion tons of CO2 emissions. This accounts for roughly 7.2% of the total global carbon emissions in 2021. Strategies to decrease carbon emissions in the cement and concrete industry include carbon capture and storage (CCS), reduced binders like ordinary Portland cement (OPC) clinker and optimizing material use through improved processes and structural design. This also means changing architectural vision [6], avoiding concrete where its structural performance is not required and use alternative materials instead, and optimizing the communication among the entire production value chain. T2 - 1st International Conference on Net-Zero Built Environment: Innovations in Materials, Structures, and Management Practices (Net-Zero Future 2024) CY - Oslo, Norway DA - 19.06.2025 KW - Concrete KW - CO2-Sequestering PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-638531 DO - https://doi.org/10.1007/978-3-031-69626-8_4 VL - 237 SP - 39 EP - 48 PB - Springer Nature Switzerland AG CY - Schweiz AN - OPUS4-63853 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Piechotta, Christian A1 - Iznaguen, Hassan A1 - Traub, Heike A1 - Feldmann, Ines A1 - Köppen, Robert A1 - Witt, Angelika A1 - Jung, Christian A1 - Becker, Roland A1 - Oleszak, Katrin A1 - Bücker, Michael A1 - Urban, Klaus A1 - Reger, Christian A1 - Ostermann, Markus T1 - Bewitterungsszenarien im Vergleich – Veränderungen in der Oberflächenmorphologie von Polypropylen (PP) und Polystyrol (PS) unter dem Aspekt des Austrags von polybromierten Flammschutzmitteln N2 - Gegenstand der vorzustellenden Arbeiten ist die Prüfung der Umwelt-beständigkeit und -verträglichkeit von Materialien und Produkten hinsichtlich der Emission von potenziellen Schadstoffen in die Umwelt. Hierzu werden chemisch-physikalische Einflüsse (Bewitterung) und mikrobielle Beanspruchungen an Modellmaterialien evaluiert. So werden die Freisetzungsraten von Schadstoffen in Abhängigkeit der Beanspruchung beschrieben. Als Modellmaterialien kommen die Polymere Polystyrol (PS) und Polypropylen (PP) zum Einsatz. Synergistische Effekte der Bewitterungsparameter und der mikrobiologischen Beanspruchung sollen dabei ebenso betrachtet werden, wie die gezielte Alterung. Auch findet eine Beschreibung des Verhaltens der ausgetragenen Schadstoffe in den Umweltkompartimenten Boden oder Wasser statt. Hier sind mit Hilfe der zu entwickelnden Screening- und non-Target-Analyseverfahren die Transformation und der Metabolismus durch Mikroorganismen zu beschreiben. Aus den Ergebnissen sollen Korrelationen zwischen den künstlichen Alterungsverfahren und realen Szenarien abgeleitet werden. T2 - 47. Jahrestagung der GUS CY - Blankenloch-Stutensee, Germany DA - 21.03.2018 KW - Schadstoffaustrag KW - Umweltsimulation KW - Bewitterung PY - 2018 SN - 978-981-18507-2-7 VL - 47 SP - 115 EP - 128 AN - OPUS4-49802 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - An, Q. A1 - Bäßler, Ralph A1 - Hertwig, Andreas A1 - Rehfeldt, Rainer A1 - Hidde, Gundula A1 - Otremba, Frank T1 - Investigation of Mechanical Stress and B10 Exposure on FKM Polymer N2 - Mechanical stress often accelerates the failure of polymer materials. The aim of this research is to study the interaction between the sealing material FKM and biofuels B10 (heating oil with 10% biodiesel). The mechanical stress test was carried out in a special apparatus. Both mechanical and non-mechanical stress tests were conducted on specimens at 20, 40, and 70 °C for 28 days to document changes in mass, volume, and tensile properties. Both increasing temperature and mechanical stress have a significant effect on the tensile strength of the FKM polymer when exposed to B10. The combination of increasing temperature and mechanical stress induced rupture within 2 h. It was also established that FKM polymer with pre-exposure in B10 survived longer during mechanical stress compared to specimens exposed only to air. With the support of infrared (IR) spectroscopy, we were able to confirm the penetration of B10 into the FKM polymer. T2 - TMS 2024 Annual Meeting & Exhibition Teilnahme mit Präsentation CY - Orlando-Florida / USA DA - 03.03.2024 KW - Biofuels KW - Sealing materials KW - Mechanical stress KW - Change in tensile properties PY - 2024 SN - 978-3-031-50349-8 DO - https://doi.org/10.1007/978-3-031-50349-8_108 SP - 1253 EP - 1261 PB - Springer CY - Orlando-Florida / USA AN - OPUS4-59638 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Torge, Manfred A1 - Krug, Sonja A1 - Bücker, Michael A1 - Feldmann, Ines A1 - Scharf, Holger A1 - Witthuhn, Heike T1 - Investigation of mercury emissions of historic tin-mercury mirrors N2 - With the implementation of glass casting in France in the second half of the 17th century, larger mirrors could be produced. So-called tin-mercury mirrors were made by coating glass with tin amalgam. Today, many historical mirrors are partly damaged, the image quality is compromised, and the material integrity of the mirror is threatened. The transformation from tin into an oxide starts at the surface of the amalgam and proceeds down to the glass surface. The mercury dissolves as a liquid or gaseous phase. The amalgam layer is destroyed, so that conservation is necessary. Conservators must follow strict safety precautions while handling amalgam mirrors because of possible mercury emissions and corrosion of the amalgam, during which elemental mercury accumulates near the mirror frame in droplets and is emitted into the air. In a research project, the quantity of the mercury emissions from historical mirrors was examined and a technique to decrease these emissions was developed. T2 - ART 2011 -10th International Conference on non-destructive investigations and microanalysis for the diagnostics and conservation of cultural and environmental heritage CY - Florence, Italy DA - 13.04.2011 KW - Zinn-Amalgamspiegel KW - Quecksilber KW - Emission PY - 2011 SP - 1 EP - 8 AN - OPUS4-23879 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Schmidt, C. A1 - Alves, H. T1 - Suitability of Nickel-based alloys and titanium for applications in acids at 200 °C N2 - In the literature there are not much data available to describe the corrosion behavior of titanium, nickel alloys and special stainless steels in acids at high temperature, in particular above the boiling point. Therefore, a laboratory testing program was performed with two titanium alloys (grade 2 - UNS R50400 and grade 12 - UNS R53400) to obtain corrosion data in formic acid, acetic acid, phosphoric acid, polyphosphoric acid, p-toluene sulfonic acid and lactic acid at 200 °C. Results were compared to previously published ones obtained on alloy 31 (UNS N08031), alloy 59 (UNS N06059) and B-2 (UNS N10665). From the results it can be concluded that titanium does not always Show better corrosion resistance than Ni-based alloys, Alloy 59 was the best choice for formic and acetic acids at temperatures of 200°C. Both Ti-alloys are resistant in acetic acid. Some slight differences were observed for formic acid, where Ti grade 2 is only resistant up to a 20 % solution and grade 12 in concentrated acid too. The phosphoric acid is extremely corrosive and none of the investigated materials was resistant. In the diluted acid (5 %) only Ti grade 12 is resistant, whereas in 1 % solution all investigated materials withstand. Alloy B-2 and alloy 59 showed the best behavior in polyphosphoric acid. In 30 % concentrated p-toluene sulfonic acid at 200 °C all alloys tested were unsuitable. In very diluted acid (0.1 %) both Ti-alloys and the other three alloys behaved well. In lactic acid at 180 °C increased corrosion underneath deposits was detected; the best performance was observed for alloy 59 and Ti grade 2. T2 - VDM Symposium "Nickel alloys, titanium and zirconium in the chemical process industry" CY - Frankfurt am Main, Germany DA - 17.06.2015 KW - Titanium grade 2 (UNS 50400) KW - grade 12 (UNS 53400) KW - Alloy 59 (UNS N06059) KW - Alloy 31 (UNS N08031) KW - Alloy B-2 (UNS N10665) KW - Inorganic acids KW - Organic acids KW - Corrosion PY - 2015 SP - paper 3 AN - OPUS4-34752 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Le, Quynh Hoa A1 - Bäßler, Ralph A1 - Yevtushenko, Oleksandra A1 - Bettge, Dirk T1 - On the corrosion mechanism of CO2 transport pipeline steels caused by impurities: roles of each impure components and benchmarks N2 - Carbon Capture, Utilization and Storage (CCUS) has been proposed as a promising technology for the mitigation of CO2 emissions into the atmosphere from fossil-fuel-operated power generation plants. As the reliability and cost effectiveness of the pipeline transport network is crucial to the overall operability and resilience of the CCUS system, it is vital to realize the possible corrosion risks of the employed pipeline steels corresponding to the impurity level of the gas source. Recent studies have shown that even the high alloyed materials might be susceptible to general and/or localized corrosion by the condensates forming from the impurities such as SOx, NOx, CO, O2 and water [1]. Up to now, however, there is no regulation procedure which defines the maximum acceptable level of impurities and the combination of them for each employed pipeline steels. Herein, systematic experiment series were conducted by mixing pure CO2 gas with varying concentration of each impurity and with the varying combination of them. Each time, the mixture was then fed (1 L/min) into the reactor containing 12 specimens for 120-600 h at 5°C (to simulate the sub-level pipeline transport). The resulted condensate was collected and analyzed by ionic chromatography and atomic absorption spectroscopy to determine the chemical composition. In this study, the “worst-case scenario” gas mixture, containing 2.5 % H2O, 1.8 % O2, 1000 ppm NO2, and 220 ppm SO2 as impurities, resulted in the condensate containing H2SO4 0.114 M and HNO3 0.0184 M (pH 2.13). This “original” condensate was then re-produced to carry out exposure tests and electrochemical characterization including corrosion potentials and impedance spectroscopy in CO2 saturated condition for 7-14 days at the same temperature. The corrosion rate was also measured by mass loss method. We can conclude that, at the initial stage, HNO3 plays the dominant role in Fe dissolution process, while H2SO4 is responsible for the pit initiation followed by pitting corrosion. Future studies will be focused on the combination effect from the impurities and the exposure test under the regularly changing condensate to mimic the real CO2 pipeline system. T2 - Eurocorr 2016 CY - Montpellier, France DA - 11.09.2016 KW - Carbon capture utilization KW - CO2 KW - Pipeline transport KW - Condensation KW - Corrosion PY - 2016 SP - paper 69810, 1 EP - 2 PB - EFC CY - Montpellier AN - OPUS4-37747 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Bäßler, Ralph A1 - Werner, H. A1 - Behrens, R. T1 - Assessment of the corrosion resistance of high-alloyed metallic tank materials in the BAM-list-requirements for tanks for the transport of dangerous goods T2 - EUROCORR 2003 CY - Budapest, Hungary DA - 2003-09-28 KW - BAM-List KW - Dangerous goods KW - Compatibility evaluations KW - High-alloyed metallic tank materials KW - Corrosion tests PY - 2003 N1 - Serientitel: EFC-Event – Series title: EFC-Event IS - 261 SP - 1 EP - 12 PB - European Federation of Corrosion CY - Budapest AN - OPUS4-2683 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Burkert, Andreas A1 - Eich, Gerd T1 - Use of Multiring-Electrodes for Humidity Measurements in Reinforced Concrete Blocks T2 - Corrosion 2004 ; 59th NACExpo 2004 ; 59th Annual conference & exposition. NACE International - The Corrosion Society CY - New Orleans, LA, USA DA - 2004-03-28 PY - 2004 IS - Paper 04426 PB - NACE International CY - New Orleans, La. AN - OPUS4-2600 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Bäßler, Ralph T1 - Techno Economic Evaluation of the Reinforce/Protection Techniques Developed under CFC/LZSG/03 Project PY - 2003 SP - 43 pages AN - OPUS4-2602 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Bäßler, Ralph A1 - Werner, H. A1 - Behrens, R. T1 - Suitability of More Noble Materials for Tanks for Transport of Dangerous Goods T2 - Corrosion 2004 ; 59th NACExpo 2004 ; 59th Annual conference & exposition. NACE International - The Corrosion Society CY - New Orleans, LA, USA DA - 2004-03-28 KW - BAM-List KW - Dangerous goods KW - Compatibility evaluations KW - High-alloyed metallic tank materials KW - Corrosion tests PY - 2004 IS - CD-ROM, Paper 04228 SP - 04228-1-04228-13 PB - NACE International CY - New Orleans, La. AN - OPUS4-3476 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Bäßler, Ralph T1 - Bewertung der Beständigkeit von hochlegierten Sonderedelstählen und Nickellegierungen für den Transport von Gefahrgütern T2 - Korrosionsschutzseminar "Hochlegierte nichtrostende Stähle und Nickellegierungen in der Prozesstechnik" CY - Dresden, Deutschland DA - 2004-10-06 KW - Korrosionsbeständigkeit KW - Hochlegierte Tankwandungswerkstoffe KW - Gefahrgüter KW - BAM-Liste PY - 2004 SP - 1 EP - 10 CY - Dresden AN - OPUS4-4423 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Bäßler, Ralph A1 - Werner, H. A1 - Alves, H. A1 - Behrens, R. T1 - Use of corrosion resistant high-alloyed metallic materials for transport tanks of dangerous goods and water-polluting substances N2 - In Germany the “BAM-List – Requirements for Tanks for the Transport of Dangerous Goods” is the basis for substance-related prototype approvals for tank containers designed for the carriage of dangerous goods. Such approval is undertaken by the Federal Institute for Materials Research and Testing (BAM). Compatibility evaluations of selected metallic material groups as well as of polymeric gasket and lining materials under the influence of dangerous goods and water-polluting substances are published in section 5 of the BAM-List. According to the relevant regulations for rail, road and sea transportation a compulsory internal inspection after certain intervals is required. The required corrosion resistance depends on the length of the inspection interval. There is a large number of dangerous goods with a high corrosivity to metals, where the standard steels are not corrosion resistant. Chemical companies, transportation providers and tank producers need tanks made of corrosion-resistant materials in order to protect the tank shell and prevent contamination of high-value cargo as well as the environment. One solution is to line the tank with a polymeric material, an alternative solution to corrosion problems is the application of high-alloyed materials. Only a narrow limited number of corrosion test results of these high-alloyed materials under the influence of corrosive dangerous goods are available. In order to change this situation and include the superaustenitic steels X1NiCrMoCuN25-20-7 (Alloy 926), X1NiCrMoCu32-28-7 (Alloy 31) and the nickel-based alloy NiCr23Mo16Al (Alloy 59) in the BAM-List, BAM, IKS Dresden and ThyssenKrupp VDM started an comprehensive test program with welded specimens made. The program comprises corrosion resistance evaluations of the high-alloyed materials in substances representing 12 major groups of corrosive dangerous goods (e.g. inorganic halogenides, organic acidic halogenides, halogenic carbonic acids, chlorosilanes, chlorates, perchlorates, chlorites, hypochlorites and hydrogen sulphates). The test results, presented in this paper, will be included in the upcoming 8th edition of the BAM-List and therefore available for the costumer. T2 - EUROCORR 2005 CY - Lisbon, Portugal DA - 2005-09-04 KW - BAM-List KW - Dangerous goods KW - Compatibility evaluations KW - High-alloyed metallic tank PY - 2005 SP - Paper 010, 1 EP - 11 PB - Fundação para a Ciência e a Tecnologia CY - Lisbon AN - OPUS4-11255 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Bäßler, Ralph A1 - Werner, H. A1 - Alves, H. A1 - Behrens, R. T1 - Use of Corrosion Resistant High-Alloyed Metallic Materials for Transport Tanks of Dangerous Goods T2 - Stainless Steel World 2005 Conference CY - Maastricht, The Netherlands DA - 2005-11-08 KW - BAM-List KW - Dangerous goods KW - Compatibility evaluations KW - High-alloyed metallic tank materials KW - Corrosion tests PY - 2005 SP - P5003 (6 pages) PB - KCI Publ. CY - Masstricht AN - OPUS4-11254 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Torge, Manfred A1 - Feldmann, Ines A1 - Knabe, Nicole A1 - Toepel, J. T1 - Organic surface coatings on medieval stained glass and microbiological investigation N2 - Mediaeval stained glass has been treated with Polymethylmetacrylate coatings by Kwiatkowski in Poland during the 1950th. Such treated panels were found in the Johannis Church of Toruń (without protective glazing), in the Cathedral of Włocławek (behind a protective glazing), and on glass kept in exhibition cases in the museum of Toruń. Surface coatings have been detected and analyzed. There was no extensive contamination by fungi or bacteria if the glass was either coated or not. T2 - Glass Science in Art and Conservation 2017 CY - Lisbon, Portugal DA - 06.06.2017 KW - Microbiological investigation KW - Medieval stained glass KW - SEM analysis PY - 2017 SN - 978-989-99528-3-6 SP - 112 EP - 113 PB - NOVA:FCT Editorial CY - Lisbon AN - OPUS4-40568 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Le, Quynh Hoa A1 - Bäßler, Ralph A1 - Bettge, Dirk T1 - Electrochemical behaviors of casing steel/mortar interface in CO2 saturated aquifer fluid N2 - To reveal the corrosion resistance of casing steel/mortar interface in CO2 injection condition, sandwich samples were prepared and exposed up to 20 weeks in aquifer fluid under 10 MPa and 60 °C. Cross section analysis revealed the crevice corrosion as main mechanism instead of pitting corrosion, which would be expected to happen in the extremely high Chloride concentration. Detailed analysis using EDS line scan shown the slow diffusion of Chloride, suggesting why pitting did not happen after 20 weeks. To mimic the passivated steel surface, the steel coupon was passivated in simulated pore solution having pH 13.5 for 42 days. The passivated coupon was further exposed to NGB solution for 28 days. Electrochemical characterization was performed along the exposure processes to reveal the change in impedance, indicating the corrosion resistance of steel casing/mortar interface. T2 - EUROCORR 2022 CY - Berlin, Germany DA - 28.08.2022 KW - Corrosion KW - CO2 quality KW - Pipeline network KW - CCS PY - 2022 SP - 859 EP - 865 PB - European Federation of Corrosion AN - OPUS4-55622 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Weltschev, Margit A1 - Bäßler, Ralph T1 - Bewertung der Beständigkeit von metallischen Tank(Behälter)-werkstoffen und polymeren Dichtungswerkstoffen unter dem Einfluss von Biokraftstoffen und -heizöl (INS 1252) N2 - In der DIN 6601 - Beständigkeit der Werkstoffe von Behältern/Tanks aus Stahl gegenüber Flüssigkeiten (Positiv-Flüssigkeitsliste) ist die Beständigkeit unlegierter Stähle, austenitischer CrNi- und CrNiMo-Stähle gegenüber den reinen Ottokraftstoffen bewertet. Mit der verstärkten Verwendung bioethanol- und biodieselhaltiger Kraftstoffe und Heizöl stellt sich auch die Frage nach der Beständigkeit der handelsüblichen Tank- und Behälterwerkstoffe sowie der Dichtungswerkstoffe unter dem Einfluss dieser Medien. KW - Biokraftstoffe KW - Tankwerkstoffe KW - Dichtungswerkstoffe KW - Beständigkeitsuntersuchungen PY - 2014 SP - Abschlussbericht, 1 EP - 37 CY - Berlin AN - OPUS4-32984 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Burkert, Andreas A1 - Klinghoffer, O. A1 - Froelund, T. T1 - Various Aspects for Usage of GPM-Portable Equipment for Determination of Corrosion Stage of Concrete Structures T2 - 15th International Corrosion Congress CY - Granada, Spain DA - 2002-09-22 KW - Galvanostatic Pulse KW - Portable Equipment KW - Corrosion Risk KW - Chloride Induced Corrosion KW - Reinforced and Prestressed Concrete Structures PY - 2002 SP - 1 EP - 8 PB - CSIC, Spanish Council for Scientific Research CY - Madrid AN - OPUS4-1540 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Burkert, Andreas A1 - Frolund, T. A1 - Klinghoffer, O. T1 - Usage of GPM-Portable Equipment for Determination of Corrsoion Stage of Concrete Structures T2 - Corrosion 2003 CY - San Diego, CA, USA DA - 2003-03-16 KW - Galvanostatic Pulse KW - Portable Equipment KW - Corrosion Risk KW - Chloride Induced Corrosion KW - Reinforced and Prestressed Concrete Structures PY - 2003 IS - 03388 SP - 1(?) EP - 12(?) PB - NACE International CY - Houston, Tex. AN - OPUS4-2380 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Mietz, Jürgen A1 - Raupach, M. A1 - Goltermann, P. T1 - Use of Embeddable Sensors in an Integrated Monitoring System for Reinforced Concrete Structures T2 - Corrosion 2003 CY - San Diego, CA, USA DA - 2003-03-16 KW - Chloride Induced Corrosion KW - Integrated Monitoring System KW - Embedded Sensors PY - 2003 IS - 03436 SP - 1(?) EP - 13(?) PB - NACE International CY - Houston, Tex. AN - OPUS4-2381 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Lamers, D. A1 - Alhassan, S. T1 - Suitability of Galvanized Rebars in Tropical Marine Environment T2 - Corrosion 2003 CY - San Diego, CA, USA DA - 2003-03-16 KW - Galvanized Reinforcement KW - Chloride Induced Corrosion KW - Tropical Marine Atmosphere KW - Long-term Atmospheric Corrosion KW - Zinc KW - Corrosion Protection PY - 2003 IS - 03250 SP - 1(?) EP - 10(?) PB - NACE International CY - Houston, Tex. AN - OPUS4-2382 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Isecke, Bernd A1 - Bäßler, Ralph T1 - Bewertung der Korrsionsbeständigkeit von Metallen für Behälter zum Transport von Gefahrgut T2 - GfKorr/VDEh-Arbeitskreis "Korrosion und Korrosionsschutz von Eisen und Stahl" CY - Frankfurt am Main, Deutschland DA - 2003-06-12 PY - 2003 AN - OPUS4-2543 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Le, Quynh Hoa A1 - Bäßler, Ralph A1 - Bettge, Dirk A1 - Kratzig, Andreas A1 - Knauer, S. T1 - Factors Influencing Droplet Corrosion in Dense Phase CO2 N2 - Recent studies have shown that even at a very low concentration of impurities (less than 100 ppmv of SO2, NO2, O2 and H2O) the droplet formation and condensation of sulfuric and nitric acids in dense phase CO2 are possible and observable. To reveal the mechanism of droplet corrosion in dense phase CO2 at high pressure and low temperature, further studies on factors that affect wettability and resulting corrosion behaviors of transport pipeline steels are needed. In this study, effects of surface morphology were investigated by varying surface roughness of carbon steel coupons exposed to CO2 stream containing impurities to measure the wettability by contact angle and to observe the condensation as well as possible droplet corrosion that followed. Other considered factors were: pH of the droplet, temperature, droplet volume, and exposure time. T2 - NACE International Corrosion Conference 2019 CY - Nashville, TN, USA DA - 24.03.2019 KW - CCUS KW - Dense phase KW - CO2 KW - Droplet KW - Corrosion KW - Condensation KW - Carbon steel PY - 2019 SP - 13017-1 EP - 13017-13 PB - NACE International CY - Houston AN - OPUS4-47915 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Breitenbach, Romy T1 - Biochemische und physiologische Charakterisierung der extrazellulären Matrix eines Modellbiofilms N2 - An der Grenzschicht zwischen einer festen Oberfläche und der umgebenden Luft wachsende subaerische Biofilme (SAB) zeichnen sich durch eine erhöhte Toleranz gegenüber extremen Umweltbedingungen und dem Eintrag von Bioziden aus. Dieser Schutz vor äußeren Umwelteinflüssen wird vornehmlich durch den Beitrag von extrazellulären polymeren Substanzen (EPS) und Pigmenten, wie Melanin und Carotinoiden, vieler unterschiedlicher Organismen gewährleistet. Deren Synthese wird wiederum durch intrazelluläre Botenstoffe reguliert. Das Cyanobakterium Nostoc punctiforme und der mikrokoloniale Pilz Knufia petricola, als Partner eines etablierten SAB-Modells und Vertreter zweier typischer Organismengruppen in SAB, wurden genutzt, um Botenstoffe und Pigmente genetisch zu manipulieren und die Biofilmmatrix dieser Mutanten strukturell zu untersuchen. In dieser Arbeit konnten erstmals die EPS beider Organismen extrahiert und die Struktur der extrazellulären Polysaccharide beschrieben werden. Daneben wurden die extrazellulären Polysaccharide von K. petricola Wildtyp mit denen verschiedener Pigmentmutanten verglichen. Das Fehlen des Schutzpigmentes Melanin führte zu einer ausgeprägteren extrazellulären Matrix in den Biofilmen. Gleichzeitig änderte sich die Struktur der extrazellulären Polysaccharide. Während der Wildtyp zu ~80% ein α-Glucan und zu ~20% ein α/β-Galaktomannan sekretierte, war der Anteil des Galaktomannans bei den Melaninmutanten erhöht. Das Ausschalten der Carotinoid-Synthese hatte jedoch keinen Einfluss auf die Beschaffenheit der extrazellulären Polysaccharide. Ein deutlich komplexeres extrazelluläres Polysaccharid aus acht verschiedenen Monosaccharid-Einheiten bildete N. punctiforme. Durch die Überproduktion des bakteriellen sekundären Botenstoffes c-di-GMP konnte zudem ein grundlegender Einfluss auf die Reaktion des Cyanobakteriums gegenüber externen Signalen und die damit verbundene Zelldifferenzierung gezeigt werden. Ein artifiziell erhöhtes c-di-GMP-Level in den Zellen führte zur Ausbildung eines sessilen Lebensstils durch Hemmung der Differenzierung motiler Hormogonien und vermehrte Produktion von EPS. Die Struktur der extrazellulären Polysaccharide wurde dadurch nicht verändert. Neben der strukturellen Analyse konnten die Veränderungen der extrazellulären Matrix beider Organismen zusätzlich durch mikroskopische Methoden visualisiert werden. Beide Organismen steuern komplexe Polymere, deren Produktion maßgeblich mit intrazellulären Faktoren verknüpft ist, zu der extrazellulären Matrix des Modellbiofilms bei. KW - Biofilm KW - EPS KW - Extrazelluläre Polysaccharide PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-471747 SP - 1 EP - 198 CY - Berlin AN - OPUS4-47174 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rütters, H. A1 - Fischer, S. A1 - Le, Quynh Hoa A1 - Bettge, Dirk A1 - Bäßler, Ralph A1 - Maßmann, J. A1 - Ostertag-Henning, C. A1 - Lennard Wolf, J. A1 - Pumpa, M. A1 - Lubenau, U. A1 - Knauer, S. A1 - Jaeger, P. A1 - Neumann, A. A1 - Svensson, K. A1 - Pöllmann, H. A1 - Lempp, C. A1 - Menezes, F. A1 - Hagemann, B. T1 - Towards Defining Reasonable Minimum Composition Thresholds – Impacts of Variable CO2 Stream Compositions on Transport, Injection and Storage N2 - The collaborative project “Impacts of impurities in CO2 streams captured from different emitters in a regional cluster on transport, injection and storage (CLUSTER)” aimed to set up recommendations on how to define “reasonable minimum composition thresholds” that CO2 streams should meet when accessing CO2 transport pipeline networks. Within CLUSTER, we investigated potential impacts of CO2 streams with different and temporally variable compositions and mass flow rates along the whole CCS chain. Investigations included, amongst others, impacts on: • corrosion of pipeline steel, • pipeline network design and related transport costs, • alteration of well bore cements, • pressure development and rock integrity, • geochemical reactions, and • petrophysical and geomechanical rock properties. All investigations are based on a generic CCS chain scenario. In this scenario, CO2 streams are captured from a spatial cluster of eleven emitters and collected in a regional pipeline network. Emitters comprise seven fossil fuel-fired power plants equipped with different capture technologies, two cement plants, one refinery and one integrated iron and steel plant. In total, 19.78 Mio t CO2 (including impurities) are captured in the emitter cluster annually. The combined CO2 stream is transported in a trunk line with a length of 400 km (100 km of these offshore) and is injected into five generic storage structures. The storage reservoirs are saline aquifers of the Buntsandstein. The investigations revealed beneficial and deteriorating impacts of different impurities and combinations thereof. Overall, no fundamental technical obstacles for transporting, injecting and storing CO2 streams of the modelled variable compositions and mass flow rates were observed. Based on the results, the CLUSTER project team recommends not to define “minimum composition thresholds” for CO2 streams as strict threshold values for each individual impurity in the stream. Instead, CO2 stream compositions and variabilities for specific CCS projects should be constrained with regard to a set of parameters including i) the overall CO2 content, ii) maximum contents of relevant impurities or elements, iii) acceptable variability of CO2 stream composition, and iv) impurity combinations to be avoided. T2 - The 15th Greenhouse Gas Control Technologies Conference CY - Online meeting DA - 15.03.2021 KW - Corrosion KW - Impurities KW - CO2 quality KW - Pipeline network KW - Whole-chain CCS scenario KW - Recommendations PY - 2021 DO - https://doi.org/10.2139/ssrn.3816427 SP - 1 EP - 18 PB - Elservier AN - OPUS4-52940 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zekhnini, Khalid A1 - Babutzka, Martin A1 - Seifert, Lando A1 - Burkert, Andreas A1 - Ebell, Gino A1 - Bäßler, Ralph T1 - Investigation of corrosion behavior of S355 steel in artificial seawater and sediment N2 - The safe operation of offshore wind turbines places high demands on corrosion protection. This is particularly the case about the planned future extension of the service life beyond 25 years. The highly corrosive environment towards metallic materials leads to a loss of material thickness of the tower structure and thus to a deterioration of mechanical properties. This can be counteracted by corrosion protection measures adapted to the respective load case, such as organic coatings and cathodic corrosion protection (CCP). Much research has already been done in this area about inhibiting the corrosion process and there are regulations and guidelines that specify requirements for corrosion protection to achieve the required service lives. However, gaps exist regarding free corrosion. This plays a greater role especially for time intervals during the installation of the plants and their maintenance, during which often no CCP can be operated. This applies to the exposure areas in the underwater and sediment area. This problem is intensified by the difficult to estimate corrosion rates caused by the different zones, with their different amounts of dissolved oxygen and the various influencing factors. This paper deals with experiments conducted in a laboratory container with artificial seawater and sediment in basins. T2 - AMPP Annual Conference + Expo 2025 CY - Nashville, TN, USA DA - 06.04.2025 KW - Seawater KW - Sediment KW - Corrosion KW - Offshore KW - Foundation KW - Element current PY - 2025 DO - https://doi.org/10.5006/C2025-00002 SP - 1 EP - 16 PB - AMPP CY - Houston TX USA AN - OPUS4-62963 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Taffe, Alexander T1 - Einsatz von zerstörungsfreien Prüfverfahren (ZfP) bei der Bestandsaufnahme von Bauwerken T2 - Brücken- und Ingenieurbautagung 2012 CY - München, Germany DA - 25.04.2012 KW - Zerstörungsfreie Prüfung im Bauwesen KW - ZfPBau KW - Bestandsaufnahme KW - Brückenprüfung KW - Bauwerkscanner KW - Ultraschall KW - Wirbelstrom KW - Radar KW - Statik KW - Statische Nachrechnung PY - 2012 SP - 51 EP - 55 PB - Bundesministerium für Verkehr, Bau und Stadtentwicklung CY - Berlin AN - OPUS4-28594 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grohmann, Maria A1 - Niederleithinger, Ernst T1 - Application of Elastic Reverse Time Migration to Ultrasonic Echo Data from Concrete Structures N2 - To enhance ultrasonic imaging of concrete structures, we adapted the geophysical migration method, Reverse Time Migration (RTM), for non-destructive testing (NDT) in civil engineering. First, two 2D elastic RTM algorithms, each considering different wave types, were implemented and evaluated with synthetic ultrasonic data. The algorithm that best resolved numerical concrete structures was subsequently applied to real ultrasonic data from a concrete specimen. Compared with conventional synthetic aperture focusing technique (SAFT) imaging, elastic RTM reproduced a greater number of structural features in both the numerical model and the concrete specimen. In particular, elastic RTM reconstructed vertical interfaces as well as hidden lower edges of modeled cavities and tendon ducts. Notably, imaging the full cross-sections of tendon ducts, which enables direct diameter estimation, represents a novel achievement for ultrasonic NDT. T2 - NDT-CE 2025 - The International Symposium on Nondestructive Testing in Civil Engineering CY - Izmir, Turkey DA - 24.09.2025 KW - Concrete Structures KW - Ultrasonic Echo Technique KW - Ultrasonic Imaging KW - Elastic Reverse Time Migration KW - Synthetic Aperture Focusing Technique PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-650350 DO - https://doi.org/10.58286/31680 SN - 1435-4934 SP - 1 EP - 3 PB - e-Journal of Nondestructive Testing CY - www.ndt.net AN - OPUS4-65035 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Duffner, Eric A1 - el Dsoki, Chalid A1 - John, Sebastian A1 - Schmidt, Anita A1 - Mair, Georg W. A1 - Loechner, Derek A1 - Drousch, Björn T1 - Sicherheitstechnische Bewertung thermischer Betriebsbelastung auf sicherheitskritische Ausrüstung am Beispiel von Composite-Atemluftflaschen und Lithiumbatterien N2 - Ziel des Vorhabens war es, den Einfluss der realen Temperaturbelastung auf Atemschutzflaschen und Lithiumbatterien in Funkgeräten (FG) im Löscheinsatz von Rettungskräften zu ermitteln und deren Auswirkung auf die Alterung und Lebensdauer sowie die potenziellen Gesundheitsgefahren bei deren Nutzung besser beurteilen zu können und Handlungshilfen abzuleiten. Im Rahmen dieses Vorhabens wurden zum einen unterschiedlich thermisch gealterte Composite-Atemluftflaschen systematisch hinsichtlich ihrer Restfestigkeiten untersucht. Zum anderen wurden Lithiumbatterien aus FG hinsichtlich der Einwirkung von kritischen Temperaturen untersucht, ab denen es zu einem thermischen Durchgehen der Batterien kommen kann. Für diese beiden wichtigen Komponenten, Lithiumbatterien und Composite-Atemluftflaschen, wurden kritische Temperatur-Zeit-Profile ermittelt, die Auswirkungen durch geeignete Methodiken untersucht und die sich ergebenden Gefährdungen für den Träger bewertet. Als Methodische Vorgehensweise wurden durch Realversuche die tatsächlichen und zuvor durch Literatur-recherche ermittelten Temperaturprofile verifiziert und auf deren Grundlage die Laborbelastungen abgeleitet. Um den Eigenschaften der aus Faserverbundwerkstoffen hergestellten Composite-Atemluftflaschen Rechnung zu tragen, wurden an zwei repräsentativen Baumustern unterschiedlicher Hersteller Stichprobengruppen unterschiedlicher thermischer Belastung ausgesetzt und hinsichtlich ihrer verbleibenden Restfestigkeitsabnahme geprüft und mit thermisch unbelasteten Baumustern verglichen. Neben den statischen Berstversuchen wurden auch kombinierte Alterungs- und Restfestigkeitsuntersuchungen an zyklisch belasteten Behältern durchgeführt. Die FG wurden thermisch sowohl statischen als auch zyklischen Belastungen ausgesetzt und mit Kapazitätsmessungen begleitet. Die statischen Versuche dienten dem Zweck, die maximale thermische Belastbarkeit der Akkus zu ermitteln, bei der noch kein Versagen auftritt. Bei den zyklischen Versuchen wurde der Temperaturverlauf bei Löscheinsätzen so nah wie möglich im Labor nachgestellt. Hierbei wurden die Akkus wiederholt einem Belastungsprofil mit konstanter Temperatur ausgesetzt und nach einigen Intervallen die Restkapazitäten am Akku gemessen und so die Degradation bestimmt. Als Fazit der im Rahmen dieses Vorhabens durchgeführten Untersuchungen an zwei repräsentativen Baumustern von Atemschutzflaschen kann gefolgert werden, dass die thermischen Belastungen abhängig vom Baumuster einen z.T. deutlichen Einfluss auf die Restfestigkeiten der Atemschutzflaschen haben. Höhere thermische Exposition ist, zumindest an den untersuchten Atemschutzflaschen, deutlich zu erkennen und die Flaschen können durch die zuständigen Gerätewarte leicht ausgesondert und ersetzt werden. Die thermischen Belastungen, wie sie im Rettungseinsatz auftreten, waren für die untersuchten Atemschutzflaschen und die Rettungskräfte nicht kritisch sind. Die langjährige Erfahrung etablierter Hersteller dürfte hier aber nicht ohne Einfluss sein. Es ist somit kein Grund erkennbar, von der Verwendung der leichteren Typ 4 Atemschutzflaschen abzuraten, wenn Atemschutzflaschen, die visuell erkennbare thermische Einwirkungen (Farbänderungen, Materialschmelzungen o.ä.) aufweisen, unmittelbar ersetzt werden. Die Ergebnisse an den FG zeigen, dass trotz hoher Temperaturen keine Selbstentzündung der Lithiumbatterien ausgelöst wird. Der Kapazitätsverlust der Batterien infolge der Belastung führt ebenfalls nicht zu einem Funktionsausfall. Es konnte gezeigt werden, dass die Kapazitätsbestimmung als zuverlässiges und geeignetes Kriterium für die Sicherheitsbewertung der Akkus herangezogen werden kann, wenn die Kapazitätsmessung bei gleichbleibenden Bedingungen (gleiche Raumtemperaturen, gleiche Messgeräte, etc.) stattfindet. Es wird empfohlen, die Akkus ab einer Restkapazität von unter 80% zu tauschen. Als schnelle und sehr einfache Überprüfung kann eine Sichtprüfung an den FG stattfinden. Die im Projekt verwendeten FG zeigten eine Verformung der Kunststoffhülle bei zu hohen Belastungen. N2 - The aim of the project was to determine the influence of the real temperature load on breathing apparatus cylinders and Lithium batteries in radio devices in firefighting operations by rescue services and to be able to better assess their effect on ageing and service life time as well as the potential health hazards and to derive guidelines for action. As part of this project, composite breathing air cylinders that had undergone different thermal ageing processes were systematically analysed with regard to their residual strength. as a second use case, lithium batteries used in radio devices were analysed with regard to the effect of critical temperatures above which thermal runaway of the batteries can occur. Critical temperature-time profiles were determined for these two important components, lithium batteries and composite breathing air cylinders, the effects for the user were analysed using suitable methods and the resulting hazards for the wearer were assessed. As a methodical approach, the actual temperature profiles previously determined by literature research were first verified in real tests and the laboratory loads were derived on this basis. In order to take into account the properties of composite breathing air cylinders made of fibre composites, sample groups were subjected to different thermal loads and examined with regard to their residual strength reduction and in comparison to thermally unloaded samples from two representative samples from different manufacturers. In addition to the static burst tests, combined ageing and residual strength tests were also carried out on cyclic loaded cylinders. The radio devices were subjected to both static and cyclic thermal loads with accompanying capacity measurements. The purpose of the static tests was to determine the maximum thermal load capacity of the batteries at which no failure occurs. In the cyclic tests, practical conditions were simulated as closely as possible in the laboratory. For this purpose, the batteries were repeatedly subjected to a load profile at a constant temperature and the residual capacity of the battery was measured after several intervals to determine the degradation. As a conclusion of the tests carried out on two representative types of breathing apparatus cylinders as part of this project, it can be concluded that the thermal loads have a sometimes significant influence on the residual strength of the breathing apparatus cylinders, depending on the type. Higher thermal exposure is clearly recognizable, at least on the breathing apparatus cylinders tested, and the cylinders can be easily remove and replaced by the responsible equipment maintainers. The thermal loads that occur during rescue operations were not critical for the tested breathing protection cylinders and the rescue teams. However, the many years of experience of established manufacturers should not be without influence here. There is therefore no reason to advise against the use of the lighter Type 4 breathing protection breathing apparatus cylinders if cylinders with visually recognizable thermal effects (color changes, material melting, etc.) are replaced immediately. The results on the radio devices showed that determination of the capacity can serve as a suitable criterion for the safety assessment for the batteries. The loss of capacity of the batteries as a result of the load also does not lead to a functional failure. The capacity determination can be used as a reliable and suitable criterion for the safety assessment of the batteries if the capacity measurement is carried out under constant conditions (same room temperatures, same measuring devices, etc.). It is recommended to replace the batteries when the remaining capacity is below 80%. A visual inspection of the radio devices can be carried out as a quick and very simple check. The radio devices used in the project showed deformation of the plastic casing when subjected to excessive loads. KW - Composite KW - Atemluftflaschen KW - Litiumbatterien KW - Funkgeräte KW - Thermische Belastung KW - Rettungskräfte KW - Feuerwehr KW - PSA KW - DGUV PY - 2024 UR - https://www.dguv.de/ifa/forschung/projektverzeichnis/ff-fp0462.jsp N1 - Abschlussbericht zum Vorhaben mit der Projekt-Nr. FF-FP 0462 (CoLiBri), Laufzeit 01.03.2021–29.02.2024, Bericht vom 15.04.2024 SP - 1 EP - 66 PB - Deutsche Gesetzliche Unfallversicherung (DGUV) CY - Berlin AN - OPUS4-59877 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Gogates, G. A1 - Eberhard, H. A1 - Pedersen, P. L. A1 - Ellison, S. A1 - Schmidt, Anita A1 - Abrantes da Costa, M. E. A1 - Holmgren, M. A1 - Tasic, T. A1 - Hald, J. T1 - Guidance for the Management of Computers and Software in Laboratories with Reference to ISO/IEC 17025:2005 N2 - This guideline is intended to be used as an aid to laboratories when they are managing the use of software and computers with respect to the requirements of ISO/IEC 17025. The working group consisted of representatives from accreditation bodies and conformity assessment operators, specifically laboratory organisations, but also included certification bodies, inspection bodies and metrology institutes. KW - Software KW - Laboratory KW - ISO/IEC 17025 PY - 2006 UR - http://www.eurolab.org/documents/2-2006.pdf VL - 2/2006 SP - 1 EP - 31 PB - EUROLAB CY - Paris AN - OPUS4-35414 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Breese, Philipp Peter T1 - Additive Manufacturing with In-situ Measurement and Closed-loop Control for the Powder Flow in Laser Metal Deposition N2 - The powder mass flow rate is one of the three main factors directly influencing geometry and quality in the Additive Manufacturing (AM; also 3D printing) process of Laser Metal Deposition (LMD), also known as Directed Energy Deposition (DED-LB/M). However, the pneumatic transport of the metal powder lacks stability, repeatability, and traceability. There is currently no reliable in-situ measurement of the mass flow rate available in industry. As a result, time-consuming powder flow measurements before the manufacturing are typical while no recording or feedback takes place during the manufacturing. Based on this problem statement, this thesis introduces a holistic approach for in-situ measurement and closed-loop control of pneumatic powder flows. For the in-situ measurement, a widely available nonintrusive optoelectronic sensor was used. Found mathematical dependencies reliably convert the sensor output into a powder mass flow rate dependent on powder parameters and feeding conditions. Therefore, the model is usable with various powder types while achieving a Mean Relative Error (MRE) of less than 4% at 125 Hz. Similarly, a model was introduced for the powder velocity using a second sensor further downstream. This provided insight into the powder’s movement while the model achieved an MRE of less than 3%. As a second main research endeavor, the sensor output was used to implement and investigate a closed-loop powder flow control on a vibration feeder. PID controller gains were calculated empirically at set operating points for the nonlinear system. Again, a usage with various metal powders is possible as the influences of powder parameters and feeding conditions were investigated and incorporated into the model. In addition, the dependence on the previous powder flow (memory effect) was factored in as well. With this, faster recovery from blockages and a reduction in standard deviation during steady state feeding by more than 20% were demonstrated. Complementary numerical CFD simulations investigated the effect of the carrier gas flow rates on powder flow homogeneity and powder particle size separations. A second modeling approach demonstrated the use of machine learning with the optoelectronic sensor output. A 1D convolutional neural network (CNN) was shown to be able to predict the powder flow with a Weighted Absolute Percentage Error (WAPE) of less than 4% compared to the actual flow. With this, the model’s capability to detect slightly elevated moisture (at <0.4wt%) in the powder as well as differences in particle size distribution was proven on in-situ data from powder feeding. Finally, the methods were validated on the LMD process by additively manufacturing test components. The active closed-loop powder flow control shows a significant improvement in repeatability for LMD. The in-situ measurement allows a monitoring of the powder mass flow rate with the recorded data throughout the entire AM process. In addition, Scanning Electron Microscopy (SEM) images showed potential benefits at the microscopic level like reduced defects. With this, the whole chain for a powder flow improvement method was investigated, implemented, and validated in the context of Laser Metal Deposition. Furthermore, a high potential for retrofitting is given while at low cost. This lays the foundation for a more traceable and digital AM process in industry leading to repeatable and safe products. KW - Pneumatic powder flow KW - Direct Energy Deposition KW - DED-LB/M KW - 3D printing KW - In-situ monitoring PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-650261 DO - https://doi.org/10.14279/depositonce-23032 SP - 1 EP - 198 PB - TU Berlin CY - Berlin AN - OPUS4-65026 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Neuhaus, B. A1 - Allspach, A. A1 - Bartsch, P. A1 - Burckhardt, D. A1 - Coleman, C.O. A1 - Fries, I. A1 - Fuchs, R. A1 - Gudo, M. A1 - Kotrba, M. A1 - Mentjes, M. A1 - Moore, S. A1 - Neumann, D. A1 - Oberer, C. A1 - Potthast, A. A1 - Riedel, Juliane A1 - Rudolf, R. A1 - Schnalke, T. A1 - Schönbohm, D. A1 - Schuda, M. A1 - van Dam, A. A1 - Widulin, N. T1 - KUR-Projekt: Aufbau und öffentliche Kommunikation eines wissenschafts-basierten Sammlungsmanagements für naturkundliche Nasssammlungen N2 - Im Rahmen eines von der Kulturstiftung des Bundes und der Kulturstiftung der Länder geförderten Projektes zum Erhalt naturkundlicher Nasssammlungen wurden 1) der Zustand der Sammlungen bewertet (Profiling; Analyse der Vergällungsmittel), 2) über Workshops Expertenwissen in das Projekt gebracht, 3) neue archivbeständige Materialien und Managementmaßnahmen eingeführt (Borosilikat-Gläser und - Röhrchen, Augenwatte, Tefloneinlagen, Japanpapier, archivbeständige Kleber und Papier, Etikettenaufbewahrung; digitales Dichtemessgerät, Alcomon-Indikator, Kontrollintervalle), 4) Erhaltungsmaßnahmen zur langfristigen Konservierung in großem Umfange durchgeführt (Messen der Alkoholkonzentration, Umsetzen von Präparaten in geeignetere Gefäße, Wiederverschluss von Schaugläsern) und 5) Erfahrungen und Diskussionsergebnisse zusammengestellt, nicht ohne auf Wissenslücken und wünschenswerte Forschungsaspekte hinzuweisen. Das Projekt profitierte besonders von der Expertise aus den Materialwissenschaften und der Papierrestaurierung. Das Museum für Naturkunde Berlin kooperierte eng mit dem Berliner Medizinhistorischen Museum der Charité, der Zoologischen Staatssammlung München und dem Forschungsinstitut Senckenberg in Frankfurt. Letzteres Museum führte ein eigenes, themenverwandtes KUR-Projekt Restauration der Sammlungen 'Vergleichende Anatomie, Embryologie und Histologie' des Naturmuseums Senckenberg durch. KW - Nasssammlung KW - Ethanol KW - Vergällungsmittel PY - 2012 DO - https://doi.org/10.5165/hawk-hhg/epublication/44 SP - 1 EP - 32 AN - OPUS4-25491 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - VIDEO A1 - Pauw, Brian Richard T1 - The human factor: A round robin study on the variation in data analyses N2 - This is a remote presentation I gave at the 2022 Small-angle Scattering conference in Campinas, Brazil. The video has been obtained from the conference organisers with their explicit permission for use on YouTube. I've tried to spruce up the audio from the remote recording the best I could. The conference abstract for this talk was: "How much do we, the small-angle scatterers, influence the results of an investigation? What uncertainty do we add by our human diversity in thoughts and approaches, and is this significant compared to the uncertainty from the instrumental measurement factors? After our previous Round Robin on data collection, we know that many laboratories can collect reasonably consistent small-angle scattering data on easy samples. To investigate the next, human component, we compiled four existing datasets from globular (roughly spherical) scatterers, each exhibiting a common complication, and asked the participants to apply their usual methods and toolset to the quantification of the results (https://lookingatnothing.com/index.php/archives/3274). Accompanying the datasets was a modicum of accompanying information to help with the interpretation of the data, similar to what we normally receive from our collaborators. More than 30 participants reported back with volume fractions, mean sizes and size distribution widths of the particle populations in the samples, as well as information on their self-assessed level of experience and years in the field. While the Round Robin is still underway (until the 25th of April, 2022), the initial results already show significant spread in the results. Some of these are due to the variety in interpretation of the meaning of the requested parameters, as well as simple human errors, both of which are easy to correct for. Nevertheless, even after correcting for these differences in understanding, a significant spread remains. This highlights an urgent challenge to our community: how can we better help ourselves and our colleagues obtain more reliable results, how could we take the human factor out of the equation, so to speak? In this talk, we will introduce the four datasets, their origins and challenges. Hot off the press, we will summarize the anonymized, quantified results of the Data Analysis Round Robin. (Incidentally, we will also see if a correlation exists between experience and proximity of the result to the median). Lastly, potential avenues for improving our field will be offered based on the findings, ranging from low-effort yet somehow controversial improvements, to high-effort foundational considerations." T2 - International Small-Angle Scattering Conference (SAS2022) CY - Campinas, Brazil DA - 11.09.2022 KW - Round robin KW - Data analysis KW - X-ray scattering KW - Neutron scattering KW - Nanomaterials KW - Metrology KW - Interlaboratory comparison PY - 2023 UR - https://www.youtube.com/watch?v=t1Rowo--Osg DO - https://doi.org/10.26272/opus4-56897 PB - YouTube, LLC CY - San Bruno, CA, USA AN - OPUS4-56897 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Völker, Christoph T1 - WEBSLAMD N2 - The objective of SLAMD is to accelerate materials research in the wet lab through AI. Currently, the focus is on sustainable concrete and binder formulations, but it can be extended to other material classes in the future. 1. Summary Leverage the Digital Lab and AI optimization to discover exciting new materials Represent resources and processes and their socio-economic impact. Calculate complex compositions and enrich them with detailed material knowledge. Integrate laboratory data and apply it to novel formulations. Tailor materials to the purpose to achieve the best solution. Workflow Digital Lab Specify resources: From base materials to manufacturing processes – "Base" enables a detailed and consistent description of existing resources Combine resources: The combination of base materials and processes offers an almost infinite optimization potential. "Blend" makes it easier to design complex configurations. Digital Formulations: With "Formulations" you can effortlessly convert your resources into the entire spectrum of possible concrete formulations. This automatically generates a detailed set of data for AI optimization. AI-Optimization Materials Discovery: Integrate data from the "Digital Lab" or upload your own material data. Enrich the data with lab results and adopt the knowledge to new recipes via artificial intelligence. Leverage socio-economic metrics to identify recipes tailored to your requirements. KW - Materials informatics KW - Scientific software KW - Sequential learning PY - 2022 UR - https://github.com/BAMresearch/WEBSLAMD DO - https://doi.org/10.26272/opus4-56640 PB - GitHub CY - San Francisco, CA, USA AN - OPUS4-56640 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rethmeier, Michael A1 - Gook, Sergej A1 - Gumenyuk, Andrey ED - Turichin, G. T1 - Prospects of application of laser-GMA hybrid welding for manufacturing of large diameter longitudinal welded high strength steel pipes N2 - To a large extend, longitudinally welded large-diameter pipes are used for modern oil- und gas-pipelines. Thereby the mostly applied base materials are made from the API-steels X65 and X70. Constantly increasing natural gas and oil delivery rates demand advancements of the assigned materials. Wall thickness minimization or operating pressure increase is achieved by material Substitution, e.g. employment of a high strength Steel grade API-X80, API-X100 or API-X120. For the production of such pipes a large plate is first formed to an open ring. Subsequent, it is continuously tacked along its longitudinal gap by means of a GMA-process. In the further process, the remaining double-sided joint gaps are filled up by cost-intensive multiple-wire submerged arc welding (SAW) processes. The GMA-tack weld is being completely remelted in the process. The maximal root face is dependent on the welding process and which is currently 8 mm. The innovative laser hybrid welding technology offers a significant increase in the full penetrated root face and welding speed, compared to conventional wielding technologies. It means for the pipe production, that the amount of SAW filier layers will be reduced and, parallel to that, the increased welding speed will led to the shortening of the production cycle for the longitudinal welded pipes. T2 - VII. International scientific and technical conference 'Beam technologies & laser application' CY - Saint-Petersburg, Russia DA - 18.09.2012 KW - High strength steel KW - Laser hybrid welding KW - Modified spray arc KW - Longitudinal weld KW - Pipeline PY - 2013 SP - 130 EP - 140 PB - Publishing house SPbSPU AN - OPUS4-28040 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pohl, Rainer A1 - Commandeur, C. A1 - Erthner, Thomas A1 - Kreutzbruck, M. A1 - Pelkner, Matthias T1 - GMR-Streufluss-Prüfsystem zur Detektion verdeckter Fehler in Feinblechen N2 - BAM und TATA Steel untersuchen gemeinsam, ob sich die Prüfung von ferritischen Feinblechen mit einer Stärke von etwa 0,2 mm während der Fertigung durch den Einsatz von GMR-Sensorik verbessern lässt. Hierzu wurde eine Vorstudie an Feinblechen mit eingebrachten Mikronuten durchgeführt. Diese Nuten variieren in ihrer Tiefe zwischen 5 μm und 60 μm und wurden verdeckt mit ZfP-angepassten GMR-Sensorarrays geprüft. Die Ergebnisse der Vorstudie zeigten, dass bei verdeckter Prüfung schon kleinste Defekte mit einer Tiefe von 10 μm - gleichbedeutend mit einer Restwanddicke von 90 % – mit einem SNR > 6 dB detektiert werden konnten, wobei der Abstand der Prüfsonde zur Oberfläche bis zu 500 μm betrug. Zudem wurden in der Vorstudie Untersuchungen zur Prüfgeschwindigkeit und Praxistauglichkeit durchgeführt. Basierend auf den hier gewonnenen Ergebnissen wird ein erster Demonstrator für eine zuverlässige Prüfung eines Teilbereiches von 50 mm des Feinbleches innerhalb einer Produktionslinie aufgebaut. Zum Einsatz kommen Prüfsonden mit jeweils 24 GMR-Sensorelementen. Hierbei wird das Ziel einer umfassenden Prüfung des Feinblechs über die gesamte Breite von 1200 mm angestrebt. Eine besondere Herausforderung stellt dabei die hohe Anzahl von mehr als 1000 Sensorelementen dar. Das hierfür entwickelte Prüfkonzept umfasst neben einer angepassten Erzeugung des Magnetfeldes die Entwicklung einer geeigneten schnellen und sicheren Elektronik für die neuen Mehrkanalprüfköpfe. Neben der Vorstellung des Prüfkonzeptes und seiner Eigenschaften vergleichen wir die erzielten Prüfergebnisse an verschiedenen Vergleichsfehlern mit denen der Vorstudie. T2 - DACH-Jahrestagung 2015 CY - Salzburg, Austria DA - 11.05.2015 KW - Streuflussprüfung KW - GMR PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-343354 UR - https://jt2015.dgzfp.de/Portals/jt2015/BB/mi2b3.pdf SN - 978-3-940283-68-9 IS - DGZfP BB 152 SP - 1 EP - 9 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-34335 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rohrmann, Rolf A1 - Thöns, Sebastian A1 - Rücker, Werner A1 - Bicker, S. A1 - Said, Samir A1 - Schmid, Wolfgang T1 - Structural investigations and monitoring results on a prototype of offshore wind turbines of multibrid M5000 series N2 - The concept and technical details of the implementation of the developed integrated monitoring system within the IMO-WIND project are presented. The tasks of the components of the system and its requirements are described. Selected results from the continuous monitoring during operation of the plant M5000_2 regarding the task design verification and dynamic structural analysis are given. T2 - DEWEK 2010 - 10th German wind energy conference CY - Bremen, Germany DA - 2010-11-17 KW - Integrated monitoring system KW - Offshore wind turbines KW - Design verification KW - Structural assessment KW - Limit values KW - Load transfer KW - Data management KW - Dynamic analysis KW - Rotor blades KW - Embedded sensors PY - 2011 IS - S03 SP - 1 EP - 5 PB - DEWI GmbH AN - OPUS4-23712 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rohrmann, Rolf A1 - Rücker, Werner A1 - Thöns, Sebastian T1 - Integrated Monitoring Systems for Offshore Wind Turbines T2 - 6th International Workshop on Structural Health Monitoring CY - Stanford, USA DA - 2007-09-11 KW - Integrated Monitoring System KW - Damage Identification KW - Load Monitoring KW - Wind turbines PY - 2007 SP - 1 EP - 8 AN - OPUS4-16280 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Berchtold, Florian A1 - Thöns, Sebastian A1 - Knaust, Christian A1 - Rogge, Andreas T1 - Review of road tunnel risk assessment - common aspects? N2 - Safety measures like tunnel emergency Ventilation Systems cause high financial costs. Hence, safety measures have to be chosen with the focus on the expected reduction of the consequences like fatalities or damage on structures and in conjunction with the investments. Since 2004, the European directive EU 2004/54/EC proposes therefore the application of risk assessments. Because the EU directive provides only few legal requirements on risk assessments, the methodologies developed on this basis have large differences. After one decade of intensive research, the comparative study now highlights common aspects and differences of several methodologies. T2 - 6th International symposium on tunnel safety and security CY - Marseille, France DA - 12.03.2014 KW - Tunnel KW - System KW - Risk assessment KW - Fire KW - Safety KW - Comparative study PY - 2014 SP - 669 EP - 670 AN - OPUS4-31256 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Thöns, Sebastian A1 - Schneider, Ronald T1 - The Influence of brittle Daniels system characteristics on the value of load monitoring information N2 - This paper addresses the influence of deteriorating brittle Daniels system characteristics on the value of structural health monitoring (SHM). The value of SHM is quantified as the difference between the life cycle benefits with and without SHM. A value of SHM analysis is performed within the framework of the Bayesian pre-posterior decision theory and requires (1) structural performance modelling and prediction, (2) structural integrity management models, (3) the (pre-posterior) modelling of SHM and (4) the coupling of SHM and the structural performance models. The pre-posterior decision theoretical framework facilitates that the value of SHM can be quantified before the SHM system is quantified and before data are acquired. The results of this study support decisions to select structural systems for which the SHM strategy load monitoring is optimal. T2 - 8th European Workshop on Structural Health Monitoring (EWSHM 2016) CY - Bilbao, Spain DA - 05.07.2016 KW - Value of information KW - Structural performance KW - Deterioration KW - Daniels systems PY - 2016 UR - http://www.ndt.net/?id=20186 SN - 1435-4934 VL - 21 IS - 8 SP - 1 EP - 9 PB - NDT.net CY - Kirchwald AN - OPUS4-38217 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rohrmann, Rolf A1 - Rücker, Werner A1 - Thöns, Sebastian A1 - Said, Samir T1 - Design and operation of integrated monitoring systems for offshore wind turbines N2 - To ensure a high operational reliability of future generations of offshore wind conversion systems (OWEC) with economically acceptable repair and maintenance efforts, comprehensive diagnosis and supervision concepts are required. Automatic monitoring systems will be an essential part of such concepts. Because of the fact, that during operation there will be static and dynamic interaction between the components 'structure', 'machinery' and 'blades' it is necessary to develop the monitoring techniques in an overall concept. These monitoring systems are supposed to be applied for the design and testing as well as for the operation and maintenance phases. The used methods are focused on the design requirements for the structure, which are stated in the respective standards and certification guidelines. For the validation of the design, methods are specified which would be also applicable for SHM in the operating condition, e.g. for the evaluation of the structural conditon possibly after the occurrence of damages or changes. The further task consists in the realization of condition monitoring for all components, aiming at early damage detection and the observation of the damage development and its evaluation. Here the task consists of determining with assessment procedures the optimum time for maintenance actions to be carried out. T2 - DEWEK 2008 - 9th German wind energy conference CY - Bremen, Germany DA - 2008-11-26 KW - Integrated monitoring system KW - Offshore wind turbines KW - Assessment KW - Damage identification KW - Load monitoring PY - 2008 SP - 1 EP - 4(?) AN - OPUS4-19872 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mair, Georg W. A1 - Günzel, Stephan A1 - Bock, Robert T1 - Risk management and consequence control in hydrogen transport - volume dependent pressure limitation as a scientific approach for consequence control N2 - With technological development, the transport units for compressed gases are becoming larger and their number is increasing. Simultaneously, the filling pressure for hydrogen in transport has increased far beyond the 200 bar, which has been the common European standard for decades. In total, this increases the potential consequences of an incident, which needs to get limited for ensuring acceptance in current practice with pressure vessels from large serial production. Consequently, the measures for new developments of extremely large and highly pressurised pressure vessels should meet a risk based higher level of requirements. For this purpose, the so-called pressure-volume product was proposed as a safety related criteria to the relevant regulatory bodies in 2020. The approach was accepted, and a working group was set up at the United Nations for developing a broadly accepted limitation of today's established pressure vessels compared to future units with even more gas content. The path to the finally decided limit value of 1.5 million bar litres is presented here for hydrogen with its individual steps: ‘Boundary between major accident and disaster’, ‘The effect of pressure waves on the human body’, ‘The propagation of pressure waves’, ‘The reference value for population density’ and ‘Impact of pressure waves’. This result of the UN working group has been accepted in December 2023 and will lead to a binding limitation of the pressure volume product for the so called pressure receptacles by 2027. The work on units larger than this pV-limit is going on at ISO level. T2 - 11th International Conference on Hydrogen Safety ICHS 2025 CY - Seoul, South Korea DA - 22.09.2025 KW - Safety KW - Hydrogen transport KW - Major accident KW - Pressure wave KW - Population density KW - UN Model Regulations PY - 2025 SP - 1 EP - 14 AN - OPUS4-64199 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gradt, Thomas A1 - Theiler, Geraldine T1 - Polymerwerkstoffe für Tribosysteme in tiefkalt verflüssigtem Erdgas N2 - Der Beitrag handelt von der Eignung von Polymeren für Anwendungen in LNG. Um dies zu testen, wurde das tribologische Verhalten von PEEK-, PTFE-, PI-, und UHMW-PE-basierten Werkstoffen im Gleitkontakt gegen CrNi-Stahl untersucht. T2 - 59. Tribologie-Fachtagung CY - Göttingen, Germany DA - 24.09.2018 KW - Alternative Kraftstoffe KW - CNG KW - LNG KW - Trockenreibung KW - Polymerkomposite PY - 2018 SN - 978-3-9817451-3-9 SP - 59/1 EP - 59/4 AN - OPUS4-46177 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holtappels, Kai A1 - Dietlen, Siegmund A1 - Stickling, J. A1 - Schönbucher, A. T1 - Druckeinfluss auf die Explosionsgrenzen der Gassyteme C2H4/N2/Luft und C2H4/CO2/Luft T2 - 4. Fachtagung Anlagen-, Arbeits- und Umweltsicherheit CY - Köthen, Deutschland DA - 1998-11-05 PY - 1998 PB - VDI-Gesellschaft Verfahrenstechnik und Chemieingenieurwesen CY - Düsseldorf AN - OPUS4-1714 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine A1 - Cano Murillo, Natalia A1 - Hausberger, A. T1 - Fretting behavior of elastomer materials in hydrogen N2 - Safety and reliability are the major challenges to face for the development and acceptance of hydrogen technology. It is therefore crucial to study deeply material compatibility, in particular polymer materials that are directly in contact with hydrogen. This paper presents an experimental study on the fretting wear behavior of two types of cross-linked hydrogenated acrylonitrile butadiene rubbers against 316L steel ball in hydrogen environment. Furthermore, aging experiments were conducted for 7 days under static conditions in 100 MPa hydrogen. the influences of hydrogen pressure as well as the aging exposure on the fretting behavior are discussed by means of surface analyses along with the material properties. T2 - 63. Tribologie-Fachtagung 2022 CY - Göttingen, Germany DA - 26.09.2022 KW - Hydrogen KW - Polymer materials KW - Fretting KW - Wear PY - 2022 SN - 978-3-9817451-7-7 SP - 58/1 EP - 58/3 AN - OPUS4-56022 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Holtappels, Kai A1 - Pasman, H. J. T1 - Interpretation of gas explosion tests - extremes in explosion severity; Contract No. EVG1-CT-2002-00072 KW - Explosion limits KW - Explosion pressures KW - KG-values PY - 2007 UR - http://www.morechemistry.com/SAFEKINEX/deliverables/Del.%20No.10.pdf IS - 10 SP - 1 EP - 30 PB - Bundesanstalt für Materialforschung und -prüfung CY - Berlin AN - OPUS4-15926 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Johann, Sergej A1 - Baensch, Franziska A1 - Strurm, Patrick A1 - Tiebe, Carlo A1 - Pötschke, Samuel A1 - Lay, Vera ED - Hall, H. T1 - HF RFID-based Measurement Comparison for Method Optimization in M2 Concrete and Alkali-Activated Mortars N2 - The internal project "SealWasteSafe" of the Federal Institute for Materials Research and Testing is dedicated to the further improvement in the construction of sealing systems for underground repositories of radioactive waste. Particularly, a multi-sensory concept is developed to ensure quality assurance and continuous long-term monitoring on the engineered barriers. Therefore, beside other measures, the temperature and equilibrium moisture of the construction shall be monitored and respective multi-sensoric monitoring concepts are tested first on the laboratory scale. One focus in this project is on embedded application in alkali-activated mortars (AAM), which results in special requirements for the resistance of the sensors to strongly alkaline environments with up to pH 14. In addition, the ingress of water along cables or at sensor positions is critical for sensors embedded in concrete, as the cable access of the sensor housing is a major weak point. It is therefore advisable to equip wireless high frequent radio frequency identification-based sensors, so called HF RFID sensors (short: RFID), that do not require cable access and thus have a stable and leak-proof sensor housing for long-term monitoring. In this contribution, the results from temperature, moisture and transmitted power monitoring of a AAM and a M2 specimens by means of HF RFID sensor systems are presented. T2 - 35th Danubia - Adria Symposium on Advances in Experimental Mechanics CY - Linz, Österreich DA - 21.09.2021 KW - Passive sensor interface KW - RFID KW - Structural Health Monitoring KW - Alkali-Activated Mortars PY - 2021 SN - 978-3-9504997-0-4 SP - 116 EP - 117 AN - OPUS4-53397 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Johann, Sergej A1 - Lapalus, Antoin A1 - Tiebe, Carlo A1 - Bartholmai, Matthias T1 - Design and Implementation of Smart Multisensor Monitoring System for Safe Workplaces with LoRaWAN N2 - This project addresses the application of safe workplaces in offices and chemical laboratories where indoor air quality plays an important role. The LoRaWAN (Long Range Wide Area Network) is used as a communication interface to make important sensor data globally accessible. The goal of the development is to create a sensor node and an online and offline solution that collects the data from the sensor nodes and stores it on a local server or in a cloud. In cooperation with the companies WISTA GmbH and IONOS, a test sensor network is going to be established in the Berlin-Adlershof area. T2 - SMSI 2020 CY - Meeting was canceled DA - 22.06.2020 KW - Smart sensors KW - Air quality monitoring KW - LoRaWAN KW - VOC KW - Multisensor system PY - 2020 DO - https://doi.org/10.5162/SMSI2020/E5.4 SP - 388 EP - 389 AN - OPUS4-50878 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Scharff, Erik T1 - Untersuchungen zur Ausbreitung brennbarer Schwergase in längsdurchströmten Straßentunneln N2 - In combination with new types of drive technologies, more and more flammable gases could be introduced into the traffic area “road tunnel” in future. If these vehicles have an accident and the gases are subsequently released, there is the possibility that the mentioned substances show a heavy gas behavior due to their storage conditions. From a safety point of view, this scenario has to be assessed with regard to its effects on the tunnel structure and the people involved. The aim of the experimental investigations carried out in this work is to create the basis for such an analysis by investigating the spreading behavior of the gases after they have been released in the tunnel and determining the influence of individual geometric and operational parameters on this behavior. Specifically, this work is based on the scenario of a continuous, momentum-free release of propane within a vaulted road tunnel with active longitudinal ventilation. The tunnel-specific boundary conditions that are relevant to this scenario are first worked out by a theoretical analysis. The basis of the subsequent experimental part is formed by two test rigs built as part of the work, which are similar in their essential features, but differ in scale. In both facilities, the aforementioned release scenario was simulated under various boundary conditions based on an idealized tunnel segment. The dispersion behavior is primarily assessed by the averaged concentration distribution near the ground, which results from a large number of detectors arranged in the experimental area. The detectors operate on the principle of weakening infrared light in the presence of hydrocarbons. Measurements of the flow field properties accompany the concentration measurements. The conception of the test rig on a scale of 1:12 is based on dimensional analysis. The actual release campaign comprises a large number of individual experiments in which selected parameters were varied over the tunnel-relevant range. The predicted heavy gas behavior for propane emerged clearly in the experiments. In cases in which the cloud laterally reaches the tunnel walls, the gases are channeled, which is accompanied by reduced longitudinal dilution. It was possible to identify the release rate and the flow velocity as the factors that have the greatest influence. The former basically increased the concentration, while the latter decreased it. All other tested parameters resulted in more complex propagation situations, which force a differentiated consideration of the influence. Lifting the source from the ground also reduced the concentration. In the case of an eccentrically arranged source and a transverse slope of the roadway, the influence is largely limited to the lateral concentration distribution in the immediate vicinity of the source. Nevertheless, both parameters plus a possible longitudinal slope of the roadway only showed a slight effect on the area far-downstream from the source. In addition, the phenomenon of backlayering, which is known from the spreading of fire smoke in the tunnel, could be demonstrated with a steep longitudinal slope. Obstacles increased the complexity of the situation. While globally the dilution of the cloud is partly invariant to obstacles, locally an increase as well as a decrease in concentration can be observed under certain conditions. For the unobstructed tunnel, it was finally possible to define a dimensionless parameter that describes the curve of the longitudinal dilution on the ground within the heavy gas cloud. From this, a simple graphical nomogram is derived for the continuous release of heavy gases in an unobstructed tunnel environment, which can be used to estimate the concentration in relation of a dimensionless source distance. For exploring the real, undistorted behavior experiments were also carried out in original scale. Due to the similarity of both test rigs in terms of scale, the test results can also be used to check the scalability of the spreading situations. For that, two configurations that have already been examined in small scale were selected. The main limitation for test execution and regarding the scalability comparison was the dependence of the flow conditions within the test rig from external wind conditions which occurred despite of taken countermeasures. The large-scale release was associated with pronounced fog formation. The near-ground spreading corresponding to the heavy gas behavior could be confirmed. However, in detail the spread was far more unsteady. Looking at the time-averaged concentrations, the processes already known from the small-scale test were qualitatively well approximated. Remaining quantitative differences, however, require critical consideration. This discrepancy is more likely a consequence of the experimental compromises have to be made in the specific case. From the observed gas behavior, the development of a surface fire initiated by ignition of the re-leased gases is considered to be the most likely subsequent scenario for the release of heavy, flam-mable gases in tunnel-like enclosures. The thesis concludes with recommendations on the methodological approach to be favored in the future. KW - LNG KW - Schwergas KW - Stoffausbreitung KW - Propan PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:gbv:ma9:1-1981185920-1206411 DO - https://doi.org/10.25673/118683 VL - 2025 SP - 1 EP - 225 PB - Otto-von-Guericke-Universität Magdeburg, Fakultät für Verfahrens- und Systemtechnik CY - Magdeburg AN - OPUS4-65012 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thöns, Sebastian A1 - McMillan, D. T1 - Condition monitoring benefit for offshore wind turbines N2 - As more offshore wind parks are commissioned, the focus will inevitably shift from a planuing, construction and warranty focus to an Operation, maintenance and investment payback focus. In this latter case, both short-term risks associated with wind turbine component assemblies, and longterm risks related to structural integrity of the Support structure, are highly important. This research focuses on the role of condition monitoring to lower costs associated with short-term reliability and long-term asset integrity. This enables comparative estimates of life cycle costs and reduction in uncertainty, both of which are of value to Investors. T2 - PMAPS 2012 - 12th International Conference on Probabilistic Methods Applied to Power Systems CY - Istanbul, Turkey DA - 10.06.2012 KW - Condition monitoring KW - Offshore wind KW - Operation KW - Risk KW - Life cycle KW - Cost KW - Cost benefit analysis KW - Offshore wind turbine KW - Operation management KW - Structural integrity management PY - 2012 SP - 37 EP - 42 PB - Istanbul Technical University CY - Instanbul, Turkey AN - OPUS4-26117 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gawlitza, Kornelia A1 - Tiebe, Carlo A1 - Banach, Ulrich A1 - Noske, Reinhard A1 - Bartholmai, Matthias A1 - Rurack, Knut T1 - Novel sensor for long-term monitoring of ammonia in gas phase N2 - Because ammonia and its reaction products can cause considerable damage to human health and ecosystems, there is a need for reliably operating and reversibly interacting sensor materials to monitor traces of gaseous ammonia in ambient air, which at best can be used on-site for in-the-field measurements. Herein, the development of a sensor material for gaseous ammonia in the lower ppm to ppb range using optical fluorescence as transduction mechanism is presented. A fluorescent dye, which shows reversible fluorescence enhancement in the presence of ammonia is incorporated into a polymer matrix, the latter to ensure the accumulation of ammonia. The sensor material is integrated into a prototype of a miniaturized sensor device, facilitating long-term operation. To calibrate the optical sensor system a gas standard generator, producing standard gas mixtures, is used, leading to a sensitivity down to lower ppm concentrations of ammonia. T2 - 13. Dresdner Sensor-Symposium 2017 CY - Dresden, Germany DA - 04.12.2017 KW - Ammonia gas sensor KW - Fluorescence KW - Air quality monitoring KW - Standard gas generator KW - Miniaturized sensor device PY - 2017 DO - https://doi.org/10.5162/13dss2017/P4.02 SP - P4.02, 272 EP - 276 AN - OPUS4-43352 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holtappels, Kai A1 - Brinkmann, C. A1 - Dietlen, Siegmund A1 - Stickling, J. A1 - Schönbucher, A. T1 - Experimentelle Bestimmung und Simulation der Stabilitätsgrenzdrücke von Gasgemischen mit zerfallsfähigen Komponenten T2 - Tagung der BASF AG 2001 CY - Ludwigshafen, Deutschland DA - 2001-01-18 PY - 2001 AN - OPUS4-1722 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Detjens, Marc A1 - Tiebe, Carlo A1 - Banach, Ulrich A1 - Ritter, U. T1 - Ionic Liquid Based Coulometric Trace Humidity Sensors N2 - This work presents a first attempt to use ionic liquids as a new coating for planar coulometric sensors. These sensors are used for the measurement of trace humidity in various gases. Usually, the coating of the sensors is tetraphosphorus decaoxide and its hydrolysis products. Instead, a hygroscopic ionic liquid was used as sensor coating in this work. Generated frost point temperatures tf in the gas ranged from -80 °C to -30 °C, which is equivalent to vapour mole fractions xv from 0.5 μmol·mol-1 to 376 μmol·mol-1. In addition to the coulometric sensors, the generated humidity is determined by a precision dew point hygrometer as reference. First results show that it is possible to measure humidity with ionic liquid based coulometric sensors. T2 - ALLSENSOR 2018 CY - Rom, Italy DA - 25.03.2018 KW - Ionic liquids. KW - Coulometric sensors KW - Sensor coating KW - Trace humidity measurement PY - 2018 SN - 978-1-61208-621-7 SP - 13 EP - 14 PB - IARIA AN - OPUS4-44609 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nattuveettil, Keerthana A1 - Liebner, Christian A1 - Tiebe, Carlo T1 - Hydrogen safety- Dealing with Closed Spaces N2 - Hydrogen is under discussion as a potentially clean energy source, but its safe usage and handling in enclosed environments remains a critical challenge due to the properties of hydrogen. This work focuses on detecting and monitoring hydrogen concentration in closed spaces to improve safety by developing a sensor network-based leak detection system to prevent of the accumulation of hazardous mixtures. Furthermore, the study details the implementation of a hydrogen sensor network within a container, analysing sensor placement, data collection, and safety improvements. The findings contribute to better risk assessment and enhanced safety protocols in hydrogen storage and usage facilities. T2 - SMSI 2025 CY - Nuremberg, Germany DA - 06.05.2025 KW - Sensor Network KW - Hydrogen safety KW - QI-Digital PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-640630 SN - 978-3-910600-06-5 DO - https://doi.org/10.5162/SMSI2025/C6.2 SP - 167 EP - 168 PB - AMA Verband für Sensorik und Messtechnik e.V. CY - Berlin AN - OPUS4-64063 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holtappels, Kai A1 - Brinkmann, C. A1 - Stickling, J. A1 - Schönbucher, A. T1 - Inertgaseinfluss auf Explosionsgrenzen am Beispiel von Ethen/Luft-Gasgemischen - Experimentelle Bestimmung und Simulation T2 - Osterkolloquium CY - Duisburg, Deutschland DA - 2001-04-24 PY - 2001 SP - 1(?) EP - 13(?) AN - OPUS4-1104 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine A1 - Hübner, Wolfgang A1 - Klein, P. A1 - Friedrich, K. T1 - Oberflächencharakterisierung von Paarungen PTFE-Komposit/Stahl nach tribologischer Beanspruchung in LN2, LH2 und LHe - Rolle der Kältemittel T2 - BAM-Sonderheft 2003 "Polymere Verbundwerkstoffe zwischen Raumtemperatur und 4,2 K" ; 2. Symposium im DFG-Projekt: Eigenschaften von PTFE- und PEEK-Matrix-Werkstoffen bei tribologischer Beanspruchung CY - Berlin, Deutschland DA - 2003-02-27 PY - 2003 SP - 17 EP - 23 AN - OPUS4-2670 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krentel, Daniel A1 - Kluge, Martin A1 - Tschirschwitz, Rico A1 - Holtappels, Kai A1 - Pelzl, T. T1 - Feuerwehrmerkblätter zu Druckgasbehältern im Brandeinsatz N2 - Die BAM hat zum Verhalten von Acetylen- und Propangasflaschen bei einer Vollunterfeuerung umfangreiche Versuchsreihen zur Auswirkungsbetrachtung des Behälterversagens auf dem TTS durchgeführt. In Zusammenarbeit mit verschiedenen Partnern entstanden zwei Merkblätter mit praktischen Hinweisen für Einsatzkräfte, die die aktuellen Forschungsarbeiten der BAM berücksichtigen. T2 - 13. Fachtagung Anlagen, Arbeits- und Umweltsicherheit CY - Köthen, Germany DA - 16.11.2017 KW - Behälterversagen KW - Gassicherheit KW - Feuerwehr KW - Acetylen KW - Propan PY - 2017 SN - 978-3-96057-032-5 SP - 1 EP - 9 AN - OPUS4-42953 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holtappels, Kai A1 - Kluge, Martin A1 - Gebauer, Marek A1 - Grüneberg, Miriam A1 - Eliezer, D. T1 - Hydrogen storage in glass capillary arrays for portable and mobile systems T2 - 3rd International conference on hydrogen safety CY - Ajaccio, Corsica, France DA - 2009-09-16 KW - Glaskapillare KW - Hochdruckwasserstoff KW - Gasspeicherung KW - Mobile Speichersysteme PY - 2009 N1 - Geburtsname von Kluge, Martin: Beckmann-Kluge, M. - Birth name of Kluge, Martin: Beckmann-Kluge, M. IS - ID 204 SP - 1 EP - 8(?) AN - OPUS4-19905 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gradt, Thomas A1 - Theiler, Geraldine T1 - Influence of solid lubricant fillers on the tribological behaviour of peek composites in vacuum T2 - ESMATS 2009 - 13th European space mechanisms and tribology symposium CY - Vienna, Austria DA - 2009-09-23 KW - Tribologie KW - Vakuum KW - Polymere KW - Kompositwerkstoffe KW - Festschmierstoffe PY - 2009 SP - 1 EP - 4 CY - Vienna, Austria AN - OPUS4-19913 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine A1 - Cano Murillo, Natalia A1 - Hashimoto, H. A1 - Aoyagi, A. A1 - Dobbelaar, E. T1 - On the way to sustainable and hydrogen compatible sealing materials N2 - In this contribution, the sliding performance of newly formulated polymer materials with improved sustainability are investigated and compared with conventional materials. Tribological tests were performed in hydrogen at ambient temperature as well as cryogenic medium. The samples were arranged in a pin-on-disk configuration with a flat pin sliding against a rotating austenitic steel disk. The friction and wear mechanisms are described and discussed by means of surface analyses. T2 - PolyTrib 2024 CY - Portoroz, Slowenia DA - 03.10.2024 KW - High-performance polymers KW - Sliding wear KW - Hydrogen KW - Cryogenic PY - 2024 SP - 1 EP - 2 AN - OPUS4-61421 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Holtappels, Kai T1 - Inert- und Brenngaseinfluss auf die Stabilitätsgrenzdrücke von Ethen und Ethin - Experimentelle Bestimmung und Simulation N2 - The theoretical basics for the simulation of the inert gas influence on explosion limits of fuel gas/air-gas mixtures of the halfempirical simulation model EPSIM are detailed described. Through modifications of this model it is possible to simulate the inert gas and fuel gas influence on the pressure limits of stability of C2H2 at different initial temperatures for the first time. The simulation model is based on the conservation equations for the minority species and energy without consideration of heat losses by radiation for the propagation of an one dimensional, stationary, premixed, laminar flame. The necessary border criterion for an explosion limit or a stability limit is a certain flame temperature, which is than constantly assumed about the further process of the limit curve. This flame temperature is calculated using measured stability limits or explosion limits. For the determination of the reaction enthalpy of the system the equilibrium constants of the formulated gross reactions are iterative calculated. Apart from homogeneous also heterogeneous gross reactions, especially the important decomposition reaction with the formation of elementary carbon, are considered for the first time. The simulation results are validated by pressure limits of stability determined experimentally at several initial temperatures for C2H2, C2H4 and C2H2/N2-, C2H2/CO2-, C2H2/H2-, C2H2/NH3-, C2H2/C2H4-gas mixtures. By visualization of a C2H2-decomposition with high speed videotakes and from the simultaneously measured pressure/time-curves the detailed form of the pressure/time-curve can be explained physically for the first time. The connection of stability limits and explosion limits is represented by the example of the ternary gas system C2H4/N2/Luft at an initial pressure of 100 bar and different initial temperatures. The inert gas influence on the explosion limits of C2H4/air-systems is also simulated. KW - heat transfer KW - safety related properties KW - mass transfer KW - soot formation KW - unstable gases KW - conservation equations KW - decomposition PY - 2002 UR - http://duepublico.uni-duisburg-essen.de/servlets/DerivateServlet/Derivate-5205/holtappelsdiss.pdf SP - 1 EP - 127 CY - Duisburg AN - OPUS4-1720 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübert, Thomas A1 - Majewski, J. A1 - Banach, Ulrich A1 - Detjens, Marc A1 - Tiebe, Carlo T1 - Response Time Measurement of Hydrogen Sensors N2 - The efficiency of gas sensor application for facilitating the safe use of hydrogen depends considerably on the sensor response to a change in hydrogen concentration. Therefore, the response time has been measured for five different-type commercially available hydrogen sensors. Experiments showed that all these sensors surpass the ISO 26142 standard; for the response times t90 values of 2 s to 16 s were estimated. Results can be fitted with an exponential or sigmoidal function. It can be demonstrated that the results on transient behaviour depend on both the operating parameters of sensors and Investigation methods, as well as on the experimental conditions: gas change rate and concentration jump. T2 - 7th International Conference on Hydrogen Safety (ICHS 2017) CY - Hamburg, Germany DA - 11.09.2017 KW - Response time KW - Hydrogen sensor KW - Test facility KW - t90 value PY - 2017 SN - 978-88-902391 SP - 1251 EP - 1261 AN - OPUS4-47592 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gradt, Thomas A1 - Theiler, Geraldine T1 - Tribological properties of polymer composites for applications in LNG environment N2 - In a first test series, the friction and wear properties of 6 polymeric candidate materials for application in LNG tribosystems were tested. The most favorable properties showed PTFE composite, filled with carbon fibers and PEEK, which showed low and stable friction and a wear coefficient in the order of 10-7 mm3N-1m-1. PTFE containing PEEK composites seem to be also appropriate for LNG applications. Admixtures of graphite as solid lubricant result in lower wear. Contrary, a lubricating mechanism of MoS2 was not observed. The PI-materials showed comparatively high friction and medium wear. T2 - 21th International Colloquium Tribology CY - Stuttgart/Ostfildern, Germany DA - 09.01.2018 KW - Tribology KW - PEEK KW - PTFE composites KW - Friction PY - 2018 SP - 1 EP - 2 AN - OPUS4-43900 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Holtappels, Kai A1 - Liebner, Christian A1 - Schröder, Volkmar A1 - Schildberg, H.-P. T1 - Report on experimentally determined explosion limits, explosion pressures and rates of explosion pressure rise - Part 1: methane, hydrogen and propylene; Contract No. EVG1-CT-2002-00072 KW - Explosion indices KW - Dependence of pressure KW - Temperature KW - Ignition energy and fuel content PY - 2006 UR - http://www.morechemistry.com/SAFEKINEX/deliverables/44.Del.%20No.%208.pdf IS - 8 SP - 1 EP - 149 PB - Bundesanstalt für Materialforschung und -prüfung CY - Berlin AN - OPUS4-12434 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Giese, Lutz A1 - Weimann, Karin A1 - Loge, K. T1 - Wiederverwertung von Erneuerbaren Energieanlagen - Forschungsbedarf in der Abfallbehandlung T2 - 13. Internationales Sonnenforum CY - Berlin, Deutschland DA - 2002-09-12 PY - 2002 IS - CD-ROM PB - Deutsche Gesellschaft für Sonnenenergie e.V. (DGS) CY - München AN - OPUS4-1454 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Cross, Carl Edward A1 - Eliezer, Dan A1 - Böllinghaus, Thomas T1 - The Role of Hydrogen in Titanium Alloy Weldments T2 - Titanium Conference 2006 CY - San Diego, CA, USA DA - 2006-10-01 PY - 2006 VL - 22 SP - 1 EP - 9 CY - San Diego AN - OPUS4-14488 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eliezer, Dan A1 - Tal-Gutelmacher, E. A1 - Böllinghaus, Thomas T1 - Hydrogen embrittlement in hydride- and non hydride-forming systems - microstructural/phase changes and cracking mechanisms, effects of high fugacity and internal hydrogen on beta-21S titanium alloy T2 - EUROCORR 2005 CY - Lisbon, Portugal DA - 2005-09-04 PY - 2005 PB - Fundação para a Ciência e a Tecnologia CY - Lisbon AN - OPUS4-11854 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Zimmer, Peter A1 - Böllinghaus, Thomas A1 - Kannengießer, Thomas T1 - Effects of hydrogen on weld microstructure mechanical properties of the high strength steels S 690Q and S 1100QL PY - 2004 UR - http://www.china-weldnet.com/English/information/II-1525-04.htm IS - II-1525-04 SP - 1 EP - 16 PB - International Institute of Welding CY - Paris AN - OPUS4-11851 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Cross, Carl Edward A1 - Böllinghaus, Thomas T1 - The Effect of Restraint on weld Solidification Cracking in Aluminium T2 - IIW Conference 2005 CY - Prague, Czech Republic PY - 2005 PB - IIW CY - Prag AN - OPUS4-11857 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eliezer, Dan A1 - Tal-Gutelmacher, E. A1 - Kannengießer, Thomas A1 - Cross, Carl Edward A1 - Böllinghaus, Thomas T1 - The effects of high fugacity and internal hydrogen on beta-21S titanium alloy T2 - EUROCORR 2005 CY - Lisbon, Portugal DA - 2005-09-04 KW - Titanium alloys KW - Beta-21S KW - Hydrogen desorption KW - Thermal Desorption Spectroscopy (TDS) PY - 2005 SP - 1 EP - 9 PB - Fundação para a Ciência e a Tecnologia CY - Lisbon AN - OPUS4-14451 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ben-Hamu, G. A1 - Eliezer, Dan A1 - Cross, Carl Edward A1 - Böllinghaus, Thomas T1 - Microstructure and Corrosion Resistance of TIG Welded AZ31B Magnesium Sheet T2 - 2nd International Conference on Magnesium CY - Beijing, China DA - 2006-06-25 KW - AZ31B KW - TIG welded KW - Microstructure KW - Corrosion behavior PY - 2006 VL - 2 IS - A-044 SP - 1 EP - 8 CY - Beijing AN - OPUS4-14486 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Böllinghaus, Thomas A1 - Kannengießer, Thomas T1 - Cold Cracking Tests - Overview KW - High strength steel KW - Multi-pass weld KW - Numerical simulation KW - Intensity of restraint KW - IRc-Test KW - Preheating KW - Interpass temperature KW - Hydrogen assisted cold cracking PY - 2007 IS - II-1635-07 SP - 1 EP - 22 PB - International Institute of Welding CY - Paris AN - OPUS4-15755 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Tschirschwitz, Rico A1 - Krentel, Daniel A1 - Kluge, Martin A1 - Askar, Enis A1 - Habib, Abdel Karim A1 - Kohlhoff, Harald A1 - Neumann, Patrick P. A1 - Rudolpf, Michael A1 - Schoppa, André A1 - Storm, Sven-Uwe A1 - Szczepaniak, Mariusz T1 - Propangasbehälter im Feuer: Auswirkungen des Versagens N2 - In einer Großversuchsserie wurden auf dem BAM-TTS 15 11-kg-Propangasflaschen ohne Sicherheitseinrichtung mit drei verschiedenen Methoden (Holz, Benzinpool, Gas) unterfeuert. Der Beitrag beschreibt die dokumentierten Auswirkungen (z. B. Fragmentierung, Überdruck), die Art des Versagens sowie den Behälterzustand zum Zeitpunkt des Versagens. T2 - 13. Fachtagung Anlagen-, Arbeits- und Umweltsicherheit CY - Köthen, Germany DA - 16.11.2017 KW - Behälterversagen KW - Gassicherheit KW - Feuerwehr KW - Propan KW - Auswirkungsbetrachtung PY - 2017 SN - 978-3-96057-032-5 SP - 1 EP - 2 AN - OPUS4-42954 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klippel, Andrea A1 - Hofmann-Böllinghaus, Anja A1 - Heydick, Lukas A1 - Piechnik, Kira A1 - Wu, Hongyi A1 - Köhler, Florian T1 - Experimental Analysis of Fire Behaviour in Pine Forests and Agricultural Fields Large Scale Tests conducted within the TREEADS Project N2 - In two large-scale tests fire spread mechanisms in vegetation ground fires were studied in a pine forest and a crop field. Both fires were ignited with a drip torch using a gasoline-diesel mix. The tests were part of the European TREEADS project, specifically in the research work from the German Pilot focusing on Saxony-Anhalt and Brandenburg. These regions are known for dry, sandy soil, with pine trees covering approximately 73% of forested areas in Brandenburg and 48% in Saxony-Anhalt. The results of both experiments make a substantial contribution to optimizing extinguishing methods and strategies and enhancing a continued wildfire research in Germany. The test areas included a 16 x 22 m plot in a Saxony-Anhalt pine forest and a 20 x 100 m plot on a crop field, with fires ignited along a line using a drip torch at both locations. Fire spread was monitored with video and IR cameras mounted on a drone. In the pine forest, 96 thermocouples and gas sensors were attached to trees and a mobile FTIR spectrometer was used for real-time gas measurements. A protective strip was created around the test area using a soil tiller and fire-retardant foam to prevent uncontrolled fire spread. The experiment showed a consistent temperature rise as the fire was ignited and spread. Thermocouple data captured detailed thermal dynamics, while tree-mounted gas sensors recorded significant fluctuations in combustible gases. Real-time gas spectra from the FTIR spectrometer enabled precise smoke analysis. Conducted in stable weather - 23°C, light wind, low soil moisture—this setup improved reproducibility, with a weather station monitoring temperature, humidity and wind conditions to assess fire-environment interactions. After ignition process the fire showed a slow spread and distinct combustion phases. Smouldering was more pronounced in areas with grasses and deadwood, highlighting vegetation-specific burn patterns critical to wildfire research. The experiment showed numerous smouldering and burning spots, with flames igniting and extinguishing repeatedly. However, flame height did not exceed half a meter. Due to substantial smoke production, visibility in the test field was limited and team members wore respirators to collect specific smoke gases such as benzene and formaldehyde for analysis. Field measurements showed flame temperatures exceeding 500°C. Toxic smoke gas concentrations of up to 238 ppm CO were measured, although precise gas capture appeared challenging due to wind turbulence. The second large-scale area in Nauen, a cut wheat field (stubble height approx. 30 cm) was burned, with fire spreading across approximately 700 m². A 20 m ignition line directed flames with the wind. Fire spread was observed using drones equipped with IR cameras. Experiments demonstrated how unpredictable and challenging it is to measure large outdoor fires. To enable a comprehensive theoretical and numerical description of fire dynamics in wildfires, it is essential to conduct further large-scale experiments. T2 - Interflam 2025, 16th International Fire Science and Engineering Conference CY - London, United Kingdom DA - 30.06.2025 KW - Wildfire PY - 2025 SP - 1435 EP - 1444 PB - Interscience CY - London AN - OPUS4-63926 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hofmann-Böllinghaus, Anja A1 - Klippel, Andrea A1 - Piechnik, Kira T1 - Vehicle fires: significant fire hazard in transportation infrastructure N2 - The zeolitic imidazole framework-8 (ZIF-8) is a crystalline porous material that has been widely employed as template to fabricate porous nitrogen-doped carbons with high microporosity via thermal treatment at high temperatures. The properties of the carbon scaffold are influenced by the pore structure and chemical composition of the parent ZIF. However, the narrow pore size distribution and microporous nature from ZIF-8 often results in low mesopore volume, which is crucial for applications such as energy storage and conversion. Here we show that insertion of N-heterocyclic amines can disrupt the structure of ZIF-8 and dramatically impact the chemical composition and pore structure of the nitrogen-doped carbon frameworks obtained after high-temperature pyrolysis. Melamine and 2,4,6-triaminopyrimidine were chosen to modify the ZIF-8 structure owing to their capability to both coordinate metal ions and establish supramolecular interactions. Employing a wide variety of physical characterization techniques we observed that melamine results in the formation of a mixed-phase material comprising ZIF-8, Zn(Ac)6(Mel)2 and crystallized melamine, while 2,4,6-triaminopyrimidine induces the formation of defects, altering the pore structure. Furthermore, the absence of heterocyclic amine in the ZIF-8 synthesis leads to a new crystalline phase, unreported to date. The thermal conversion of the modified ZIFs at 1000 °C leads to nitrogen-doped carbons bearing Zn moieties with increased surface area, mesopore volume and varying degree of defects compared to ZIF-8 derived carbon. This work therefore highlights both the versatility of heterocyclic amines to modify the structure of framework materials as well as their role in tuning pore structure in nitrogen-doped carbons, paving the way to targeted design of high-performance electrodes for energy storage and conversion. T2 - Interflam 2025, 16th International Fire Science and Engineering Conference CY - London, United Kingdom DA - 30.06.2025 KW - Vehicle fires PY - 2025 SP - 1291 EP - 1298 PB - Interscience CY - London AN - OPUS4-63924 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Piechnik, Kira A1 - Hofmann-Böllinghaus, Anja A1 - Klippel, Andrea T1 - Characterization and assessment of smoke emissions from smouldering forest fires: a combined experimental and numerical approach N2 - This article builds upon the publication "Comprehensive Laboratory Study on Smoke Gases During the Thermal Oxidative Decomposition of Forest and Vegetation Fuels"1 in Fire and Materials, 2024, summarizing the experimental methodology and highlighting key findings. The study investigates the gas-phase composition of smoke emissions from forest and vegetation fuels. The study focuses on pine-dominated ecosystems in Eastern Germany, with the objective of improving the understanding of wildfire-related gaseous emissions, as a contribution to the German pilot activities within the EU Project TREEADS. Using a modified DIN tube furnace in a bench-scale setup, the investigation centers on gaseous emissions from five trees and two ground cover species, explicitly excluding particulate matter. T2 - Interflam 2025, 16th International Fire Science and Engineering Conference CY - London, UK DA - 30.06.2025 KW - Wildfire PY - 2025 SP - 288 EP - 294 PB - Interscience CY - London AN - OPUS4-63999 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böllinghaus, Thomas A1 - Kannengießer, Thomas A1 - Jochum, C. A1 - Stiebe-Springer, I. T1 - Effect of filler material selection on stress strain build up and stress corrosion cracking resistance of welded supermartensitic stainless steel pipes T2 - Corrosion 2002 CY - Denver, CO, USA DA - 2002-04-07 KW - Supermartensitic stainless steel KW - Filler material KW - Orbital TIG welding KW - Duplex stainless steel KW - Hydrogen assisted cracking KW - Stress strain distribution KW - Shrinkage restraint KW - Formation water PY - 2002 SP - Paper 02061, 1 EP - 20 PB - NACE International CY - Houston, Tex. AN - OPUS4-1794 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fedelich, Bernard A1 - Affeldt, E. E. ED - Portella, Pedro Dolabella T1 - Modeling the non isothermal cyclic mechanical behavior of a single crystal superalloy T2 - 5th International Conference on Low Cycle Fatigue (LCF-5) CY - Berlin, Germany DA - 2003-09-09 KW - Single crystal superalloys KW - Low Cycle Fatigue KW - Thermo-Mechanical Fatigue KW - Modeling KW - Constitutive laws PY - 2003 VL - 5 SP - 475 EP - 480 PB - DVM, Deutscher Verband für Materialforschung und -prüfung CY - Berlin AN - OPUS4-3721 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Seeger, Dirk A1 - Böllinghaus, Thomas T1 - Hydrogen Permeation in Supermartensitic Stainless Steels Exposed to Realistic Formation Water Compositions T2 - Corrosion 2003 CY - San Diego, CA, USA DA - 2003-03-16 KW - hydrogen permeation KW - Supermartensitic stainless steel KW - Formation water KW - Realistic environments KW - diffusion coefficient KW - HDss PY - 2003 IS - 03098 SP - 03098-1-03098-15 PB - NACE International CY - Houston, Tex. AN - OPUS4-2898 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nofz, Marianne A1 - Sojref, Regine A1 - Dreßler, Martin A1 - Dörfel, Ilona A1 - Reinsch, Stefan A1 - Saliwan Neumann, Romeo T1 - Korundhaltige Aluminiumoxidschichten T2 - 15. Symposium: Verbundwerkstoffe und Werkstoffverbunde CY - Kassel, Germany DA - 2005-04-06 PY - 2005 UR - http://www.dgm.de/download/tg/706/706_85.pdf SP - 5 Seiten PB - DGM CY - Kassel AN - OPUS4-7522 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fedelich, Bernard A1 - Noack, Hans-Dieter A1 - Levkovitch, Vladislav A1 - Sievert, Rainer T1 - Übersicht über Verformungsmechanismen, Modellierung und LCF Lebensdauervorhersage von Superlegierungen bei hoher Temperatur T2 - FVHT-Vortragsveranstaltung DA - 2005-11-25 KW - Superlegierungen KW - LCF KW - Modellierung PY - 2005 SP - 10 Seiten PB - Arbeitsgemeinschaft für warmfeste Stähle (FVW) AN - OPUS4-11221 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böllinghaus, Thomas A1 - Holler, K. A1 - Kannengießer, Thomas A1 - Schobbert, H. T1 - Nd: YAG laser plasma powder hybrid welding of austenitic stainless steels N2 - As an approach towards more rough industrial laser welding applications, the Nd:YAG laser welding process has been coupled to the plasma powder welding process for the first time. Process stabilities have been achieved by such hybrid welding which are even better than those known from previous coupling of the laser process with gas metal arc welding (GMAW), for instance. The present contribution focuses on the technology and potentials of the novel laser hybrid welding technique and addresses the realisation and the perspectives for practical applications. The experimental results demonstrate that the new process coupling enables welding of austenitic stainless steels in the thickness range between 3 mm and 8 mm at various weld geometries and joint configurations and at welding speeds exceeding 2 m/min. In addition it has been proven that the laser plasma powder arc welding (LPPAW) technique can also be applied to out-of-position conditions. Continuous advancement of the welding equipment ensures a high gap bridging ability and levelling of misalignment due to higher powder feeding rates. The recent development of a new plasma powder torch even provides a higher efficiency of powder feeding and guarantees smoth weld surfaces. Up to the present, the investigations demonstrated that the novel laser plasma powder hybrid welding technique offers all perspectives for application in pipe fabrication, ship building and offshore as well as transportation industry. T2 - Seminar in Mechanical and Metallurgical Approaches to New Joining Process CY - Awaji Island, Japan DA - 20.07.2004 KW - Nd:YAG KW - Laser plasma KW - Powder KW - Hybrid KW - Welding KW - Austenitic stainless steels PY - 2004 SP - 140 EP - 145 CY - Japan AN - OPUS4-39261 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fedelich, Bernard A1 - Noack, Hans-Dieter A1 - Levkovitch, Vladislav A1 - Sievert, Rainer T1 - Übersicht über Verformungsmechanismen, Modellierung und LCF-Lebensdauervorhersage von Superlegierungen bei hoher Temperatur T2 - 28. VDEh Vortragsveranstaltung der Arbeitsgemeinschaft für warmfeste Stähle und der Arbeitsgemeinschaft für Hochtemperaturwerkstoffe "Langzeitverhalten warmfester Stähle und Hochtemperaturwerkstoffe" CY - Düsseldorf, Deutschland DA - 2005-11-25 KW - Superlegierungen KW - LCF KW - Modellierung PY - 2005 SP - 127 EP - 136 PB - Stahlinstitut VDEh CY - Düsseldorf AN - OPUS4-11526 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Kannengießer, Thomas A1 - Böllinghaus, Thomas A1 - Florian, Wolfgang A1 - Herold, H. T1 - Effect of weld metal strength and welding conditions on reaction forces and stress distribution of restrained components N2 - Düring the past decades, weldability studies have predominantly been concentrated on the material and the welding process. In order to achieve a closer insight into the structural effects, component weldability tests have been performed by online monitoring of the reaction forces and moments. As a particular item, the effects of different strengths of the base and filier material on the reaction force and stress build up transverse to the welding direction have been studied at a specific structural restraint. As a most relevant result for practical welding it is demonstrated that the final reaction force and also the reaction stress level in the multilayer butt welds decreases with overmatch of the weld metal. PY - 2000 IS - IX-1971-00 SP - 1 EP - 18 PB - International Institute of Welding CY - Paris AN - OPUS4-11842 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grützner, Stefan A1 - Fedelich, Bernard A1 - Rehmer, Birgit A1 - Buchholz, B. ED - Clark, G. ED - Wang, C.H. T1 - Material modelling and lifetime prediction of Ni-base gas turbine blades under TMF conditions N2 - Under cyclic thermomechanical loading conditions, various damage mechanisms such as strain accumulation, creep cavitation, ageing, fatigue surface cracking etc. may take place in the material of a gas turbine blade. Depending on the loading conditions, all these effects can contribute to reduce the lifetime of the component. Subject of the present work is the development of a material model to describe the mechanical effects mentioned above, as well as the development of a lifetime model able to discriminate the different damage mechanisms. T2 - Fatigue 2014 - 11th International Fatigue Congress CY - Melbourne, Australia DA - 2014-03-02 KW - Creep KW - Fatigue KW - Ni-base superalloy KW - Oxidation damage KW - Ratcheting KW - Strain induced ageing KW - Viscoplastic PY - 2014 DO - https://doi.org/10.4028/www.scientific.net/AMR.891-892.1277 N1 - Serientitel: Advances materials research – Series title: Advances materials research VL - 891-892 IS - XXX. Thermomechanical Fatigue SP - 1277 EP - 1282 AN - OPUS4-30721 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Tschirschwitz, Rico A1 - Krentel, Daniel A1 - Kluge, Martin A1 - Askar, Enis A1 - Habib, Abdel Karim A1 - Kohlhoff, Harald A1 - Neumann, Patrick P. A1 - Storm, Sven-Uwe A1 - Rudolph, Michael A1 - Schoppa, André A1 - Szczepaniak, Mariusz T1 - Mobile gas cylinders in fire: Consequences in case of failure N2 - Commercial, off-the shelf propane cylinders are subjected to high safety regulations. Furthermore, those cylinders are equipped with safety devices like pressure relief valves (PRV). Despite these regulations and safety measures, a failure of the Container is possible if exposed to an intense fire. The result of this is severe hazard for users, rescue forces and infrastructure. Within the framework of a destructive test series, 15 identical propane cylinders, without pressure relief devices, were exposed to an intensive fire in horizontal Position until failure. Each cylinder was filled with a mass of m =11 kg of liquid propane. Three different fire sources were used (wood, petrol, propane). The experiments revealed the failure of all cylinders in a time period t < 155 s. The failure lead to a fragmentation into several major parts with throwing distances of up to l =262 m. In all trials, the temperature of the cylinder wall (top, side, bottom), of the liquid phase inside and of the surrounding fire (top, side, bottom) was recorded. In addition, the inner cylinder pressure and the induced overpressure of the blast wave after the failure were recorded. Overpressures of up to p=0.27 bar were recorded close to the cylinder (l =5 m). AM tests were documented hy video from several positions (general view, close-up, high-speed 5000 fps). This test series creates the basis for further experimental studies in the field of alternative fuels for vehicles. The aim of this test series is to assess and analyse the consequences of the failure of gas vessels (for LPG, CNG, CGH2) in the aftermath of severe incidents. T2 - 12th International Symposium on Fire Safety Science CY - Lund, Sweden DA - 12.06.2017 KW - Explosion KW - Gas cylinders KW - Consequences PY - 2017 DO - https://doi.org/X0.1016/j.firesaf.2017.05.006 SN - 0379-7112 VL - 91 SP - 989 EP - 996 PB - Elsevier Ltd. AN - OPUS4-43028 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Davydenko, L. A1 - Nazarchuk, M. A1 - Nasiedkin, D. A1 - Plyuto, Y. A1 - Mosquera Feijoo, Maria A1 - Nofz, Marianne A1 - Sojref, Regine A1 - Dörfel, Ilona A1 - Saliwan Neumann, Romeo A1 - Kranzmann, Axel A1 - Pérez, F.J. T1 - Anticorrosion hybrid AlPO4/Al2O3 coatings on the surface of P92 steel for oxy-fuel power plant application T2 - XtremeCOAT 2014 - Surface engineering for functional applications under extreme conditions CY - Madrid, Spain DA - 2014-10-20 KW - Corrosion protection KW - Hybrid coatings KW - Boehmite KW - AlPO4 PY - 2014 SP - P 5, 1 EP - 2 AN - OPUS4-31453 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hofmann-Böllinghaus, Anja T1 - What can we learn from European train fire safety regulations for fire safety regulations for busses? N2 - Recent bus fires in Europe, such as the bus fire in France 2015 with 43 fatalities and the bus fire in Germany 2017 with 19 fatalities, show that these fires can be very hazardous and time for escape can be too short. Recently, several fire safety measures came into force for busses. Engine compartment suppression systems will be mandatory for all busses in Europe. This is a big step in fire safety as about 80 % of fires start in the engine compartment. However, in several recent bus fires a time of less than 5 minutes has been reported from detection of the fire to a fully developed fire. As normally many people are on board of a bus, a bus fire is not comparable to fire in a home. Especially for people with reduced mobility or for fires after a collision the available times for escape are too short. When the fire service is on scene the transition to a fully developed fire might have happened already. Passengers who are not able to escape in this short period of time mostly cannot be rescued by the fire service even with quick response times because of the dramatic fire development. Fires that do not start in the engine compartment but develop in the cabin are rarer but extremely dangerous because fire and smoke spread very rapidly. The reason for the fast fire and smoke development in the cabin are the materials which are used. Over the last tens of years materials in busses had major developments. The amount of plastic in the cabin has grown significantly. In a modern coach the biggest fire load often is not the fuel anymore but the interior materials. Bus fire safety is mainly regulated by ECE regulations R 118 and R 107. A comparison with European standards for trains shows that for trains, in contrast to busses, a holistic fire concept exists. Fire scenarios as well as escape scenarios and passenger behaviour are taken into account, resulting in fire safety regulations on a high level compared with bus regulations. In contrast to regulations for train materials no limits for heat or smoke production are given for bus materials. Larger heat release values promote more rapid fire spread. Also smoke production and toxicity are key factors in fires. The smoke reduces the visibility in the case of fire, and together with the toxicity of the smoke can make escape from the vehicle impossible. Figure 1 shows the remains of the bus from the recent severe bus fire in Germany in 2017. As a result of experience with real cases and results from research projects we think it is necessary to develop a holistic fire safety concept for busses as it exists for other transport means like railways. The fire safety concept should include vehicle configuration and design as well as areas of use, e.g. use in cities, use in long-distance traffic on motorways and use in tunnels. T2 - FIVE Conference CY - Boras, Sweden DA - 03.10.2018 KW - Fire safety concept KW - Busses KW - Trains KW - Reaction-to-fire PY - 2018 SN - 978-91-88695-95-6 VL - 2018 SP - 215 EP - 225 PB - RISE CY - Boras, Schweden AN - OPUS4-46544 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hussels, Maria-Teresa A1 - Chruscicki, Sebastian A1 - Baer, Wolfram A1 - Wossidlo, Peter A1 - Weltschev, Margit A1 - Schmidt, Dirk A1 - Baensch, Franziska A1 - Bohse, Jürgen A1 - Prager, Jens A1 - Habib, Abdel Karim T1 - AGIFAMOR – Application of distributed acoustic and fibre optic sensors for continuous monitoring of pipes N2 - Pipelines and industrial piping systems are particularly relevant regarding technical safety, availability and maintenance. Large flow rates of hazardous substances imply that even smallest leakages can lead to high environmental impacts. Therefore, and to ensure the availability of infrastructure, an early detection and localization of potentially hazardous degradations to the walls (e.g. cracks, pittings, sedimentation, etc.) of the containments is necessary. However, in many cases it is not feasible to equip pipelines with a large number of point sensors at reasonable expense. The principle of distributed fibre optic sensing relies on one single optical fibre, which simultaneously acts as a spatially continuous sensor as well as the signal transducer. Therefore, extensive structures can be provided with this type of sensor with comparatively low efforts. As a consequence, monitoring oil and gas pipelines using distributed fibre optic sensors is on the upswing. Besides the established methods to measure temperature and strain, distributed acoustic sensing (DAS) has lately received considerable attention as a means to detect and localize third party threats to pipelines (approach of vehicles, digging, mechanical manipulation). The so far not utilized potential of DAS as a means for continuous condition monitoring of pipes by detecting and localizing acoustic signals that point to certain damage scenarios, is currently under investigation in an interdisciplinary research project at BAM (AGIFAMOR, Ageing Infrastructures – Fibre Optic Monitoring of Pipes). In order to qualify distributed acoustic fibre optic sensors for this application area, we especially focus on detecting and identifying the relevant acoustic emissions of interesting degradations as well as on the optimal way of application of the optical fibres to the specimen to achieve an optimal signal transmission of acoustic signals. T2 - 12th Pipeline Technology Conference CY - Berlin, Germany DA - 02.05.2017 KW - Monitoring KW - Pipelines KW - Fibre optic sensing KW - Acoustic emission KW - Accelerometer PY - 2017 SN - 2198-428X VL - 2017 SP - Session 3.2 Leak Detection, 1 EP - 8 PB - EITEP (Euro Institute for Information and Technology Transfer in Environmental Protection) CY - Hannover AN - OPUS4-40186 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Karsten A1 - Baer, Wolfram A1 - Wossidlo, Peter T1 - Investigation on the Dynamic Fracture Toughness of Heavy-Section Ductile Cast Iron for Transport and Storage Casks T2 - PATRAM 2001 ; Annual International Symposium on Packaging and Transportation of Radioactive Materials CY - Chicago, IL, USA DA - 2001-09-03 PY - 2001 IS - CD-ROM PB - PATRAM CY - Chicago, Ill. AN - OPUS4-1886 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baensch, Franziska A1 - Baer, Wolfram A1 - Wossidlo, Peter A1 - Habib, Abdel Karim T1 - Non-threshold acoustic emission analysis of damage evolution in pipe segments of steel S355J2H under bending load N2 - Four-point bending tests were carried out to analyze the acoustic characteristics of damage development in pipe segments made of steel, grade S355J2H, being 2.5 m long with an outer diameter of 168 mm and 16 mm wall thickness. To induce stable crack growth, the pipe segments were pre-damaged by a 90°circumferential notch in the middle of the pipe length. While the pipe was quasi-statically loaded, microscopic damage and plastic deformation accumulated to form a macroscopic crack that grew through the pipe wall until leakage. For acoustic emission (AE) monitoring, four broadband sensors of type VS 900 M were mounted close to the notch. Continuous AE signal detection was performed by the non-threshold method. Advantages and disadvantages of the non-threshold AE monitoring compared to a commonly employed method analyzing only signals exceeding a predefined threshold are discussed. The results of AE analysis are compared to additional information on the crack growth detected by the direct current potential drop (DCPD) technique. These studies were carried out in the course of the interdisciplinary research project AGIFAMOR, Ageing infrastructures - distributed acoustic monitoring of pipes at BAM. T2 - 33rd European Conference on Acoustic Emission Testing CY - Senlis, France DA - 12.09.2018 KW - Acoustic emissions (AE) KW - Four-point bending test KW - Steel pipe KW - Crack initiation KW - Crack growth PY - 2018 SP - 340 EP - 347 CY - France, Senlis AN - OPUS4-45960 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Bashiri, Termeh A1 - Yu, Phelan A1 - Hutzler, Nicholas R. A1 - Steimle, Timothy C. A1 - Abad Andrade, Carlos Enrique A1 - Okumura, Mitchio T1 - A Molecular Beam Study of the (0,0) A2Π<- X2Σ+ Band of CaF Isotopologues N2 - This study presents an experimental determination of spectroscopic parameters for the less-abundant isotopologues 42CaF and 44CaF, alongside 40CaF, by high resolution laser-induced fluorescence spectroscopy in a skimmed free jet expansion. We recorded spectra near the natural linewidth limit and derived spectroscopic constants for both X2Σ+ and A2Π states, including the fine and 19F magnetic hyperfine parameters. We also estimated the r (44Ca/40Ca) isotope amount ratio, demonstrating the potential use of optical spectroscopy for isotope analysis. KW - High-resolution spectroscopy KW - Molecular beam spectrometer KW - Isotope ratios KW - Calcium isotopes KW - Isotopologues PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-648804 DO - https://doi.org/10.48550/arXiv.2505.03045 SP - 1 EP - 23 PB - Cornell University AN - OPUS4-64880 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geoerg, Paul A1 - Polzin, R.M. A1 - Holl, S. A1 - Hofmann-Böllinghaus, Anja T1 - Berücksichtigung von Personen mit körperlichen, geistigen oder altersbedingten Beeinträchtigungen in der Evakuierungsforschung N2 - Studien zur Erforschung von Kenngrößen der Bewegung von Personen wurden in der Vergangenheit meistens mit jungen und fitten Menschen durchgeführt. In Folge des demographischen Wandels und der Anforderungen an barrierefreies Bauen stellt sich die Frage, ob die so ermittelten Kenngrößen der Bewegung auch auf heterogene Personengruppen übertragen werden können. Da bei der Berechnung von Räumungszeiten zunehmend Ingenieurmethoden eingesetzt werden, deren Ergebnisse ganz wesentlich von den zu Grunde gelegten Bewegungsparametern, wie z. B. der freien Gehgeschwindigkeit, abhängen, hat die Validität der Kenngrößen maßgeblichen Einfluss auf die sicherheitstechnische Evaluation von Gebäuden und Versammlungsstätten. In diesem Artikel wird anhand aktueller Forschungsergebnisse aus Bewegungsstudien, an denen Menschen mit und ohne Beeinträchtigungen teilgenommen haben, der Einfluss der Heterogenität auf Kenngrößen der Bewegung vorgestellt. Darüber hinaus werden die Besonderheiten des Studienablaufs und die Möglichkeiten und Grenzen der Untersuchungsmethode dargestellt. Die Untersuchungen bestätigen, dass die Berücksichtigung besonderer Personengruppen signifikanten Einfluss auf die Kenngrößen der Bewegung hat und daher die Ergebnisse der Ingenieurmethoden beeinflusst und zukünftig bei heterogenen Personengruppen beachtet werden muss. T2 - 65. Jahresfachtagung der Vereinigung zur Förderung des Deutschen Brandschutzes e.V. CY - Duisburg, Germany DA - 28.05.2018 KW - Evakuierung KW - Egress KW - Heterogenität KW - ASET KW - RSET PY - 2018 SN - 978-3-936050-28-8 SP - 189 EP - 204 PB - VdS Schadensverhütung GmbH Verlag CY - Köln AN - OPUS4-45082 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hofmann-Böllinghaus, Anja A1 - Mühlnikel, Rüdiger T1 - Computermodellierung von Brandszenarien - LA2200S dient als Abbrandwaage PY - 2007 N1 - Geburtsname von Hofmann-Böllinghaus, Anja: Hofmann, A. - Birth name of Hofmann-Böllinghaus, Anja: Hofmann, A. IS - 21 SP - 19 CY - Göttingen AN - OPUS4-15721 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böllinghaus, Thomas A1 - Viyanit, Ekkarut A1 - Hoffmeister, H. T1 - Numerical modelling of hydrogen assisted cracking N2 - Hydrogen might be introduced during fabrication welding or might be taken up from an environment during sour service or cathodic protection. Thus, hydrogen assisted stress corrosion and cold cracking is still a major topic regarding the reliability of welded steel components, as for instance offshore platforms and pipelines. In order to support conclusive testing and life time evaluation of welded steel components, a numerical model for hydrogen assisted cracking has been developed, particularly taking into consideration the geometrical effects of crack propagation on the respective hydrogen distribution alongside and ahead of the crack. Numerical calculations were based on finite element analysis of the hydrogen and stress-strain distribution by using a commercially available program. The model has been verified experimentally by slow strain rate experiments of supermartensitic stainless steels which are intended to be used more extensively as materials for welded flowlines in North Sea oil and gas production. As first results of such simulations the influence of the subsurface concentration provided by different H2S saturation levels in the NACE TM 0177-96 standard solution on crack propagation and the effect of crack shape on the hydrogen distribution profile are presented in this contribution. T2 - Corrosion 2001 CY - Houston, TX, USA DA - 2001-03-11 KW - Hydrogen assisted cracking KW - Numerical simulation KW - Welded steel components KW - Low carbon martensitic stainless steel KW - Sour service KW - Slow strain rate test KW - Crack propagation PY - 2001 UR - http://www.nace.org/nacestore/department.asp?ID=671 IS - Paper 01226 PB - NACE International CY - Houston, Tex. AN - OPUS4-1015 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krentel, Daniel A1 - Tschirschwitz, Rico A1 - Kluge, Martin A1 - Askar, Enis A1 - Kohlhoff, Harald A1 - Mair, Georg W. A1 - Rudolph, Michael A1 - Schoppa, Andre A1 - Storm, Sven-Uwe A1 - Szcepaniak, Mariusz T1 - Consequences of the failure of mobile gas vessels N2 - Small, mobile propane gas vessels are widely spread and comprise additional hazards in case of a surrounding, intensive fire. The aim of the presented work is to holistically investigate the potential consequences of failure of these off-the-shelf propane gas vessels in case of an absence or malfunction of safety devices. In order to generate a statistically valid dataset, a total of 15 identical propane gas bottles without pressure relief device, each containing m = 11 kg of liquid propane, were underfired in horizontal position. For each selected fire type (wood fire, petrol pool fire, propane gas fire), five vessels were tested under identical conditions. Next to extensive camera equipment including a high-speed camera, systems to record the internal pressure of the gas cylinder, the resulting shock wave overpressure (three positions) and the flame and vessel temperature (three + three positions) during the underfiring were used. Also the unsteady, highly dynamical thermal radiation caused by the explosion of the expanding gas cloud was logged. The fragments were georeferenced and weighed after each test. The experiments prove the failure of all the gas cylinders at a burst pressure of pb = [71 … 98 bar] with a fragmentation into up to seven parts (average: four objects) and a subsequent explosion of the expanding vapour after mixing with the surrounding air. The overpressure measured in the close-up range (distance to the cylinder d = 5 m) resulting from the shockwave caused by the cylinder burst was up to pmax = 0.27 bar, which can potentially lead to significant injuries to humans and damage to building structures and infrastructure, especially in connection with the explosion and the resultant thermal radiation. The distance covered by the fragments after the failure was up to r = 260 m; 47% of the fragments hit the ground more than r = 50 m away from the position of failure. T2 - Hazards 27 CY - Birmingham, UK DA - 10.05.2017 KW - Failure of gas vessels KW - Propane cylinder KW - Gas explosion KW - Consequences KW - Fragmentation PY - 2017 SN - 978-1-911446-57-6 SP - 1 EP - 12 PB - Instiution of Chemical Engineers CY - Rugby, UK AN - OPUS4-41160 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Böllinghaus, Thomas T1 - Hydrogen absorption and diffusion in T24 steel weld joints and effect on mechanical properties N2 - The present contribution summarizes results obtained from experiments with low-alloyed boiler steel grades T24 (CrMoV alloy), T22 (CrMo) and thermally simulated T24 HAZ microstructure and pure weld metal. The hydrogen absorption and diffusion behavior was investigated by permeation experiments and thermal desorption analysis (TDA). The results showed significant weld microstructure influence on diffusion by hydrogen trapping. Trapped hydrogen was determined in the T24 BM at temperatures up to 120 °C compared to 75 °C in the T22. In addition, the T24 HAZ showed decreased diffusion coefficients (at room temperature) of approximately one magnitude compared to the BM. For the mechanical properties, tensile tests were conducted with electrochemically hydrogen charged specimens and compared to results obtained from slow strain rate tests (SSRT) in high-temperature water up to 200 °C. The as-welded HAZ had remarkably increased susceptibility compared to the BM already at low hydrogen concentration of 1-2 ppm. The SSRT were conducted for free corrosion and acidic environment and confirmed this behavior at elevated temperatures for both HAZ microstructures of T24 and T22. Summarized, each weld microstructure has specific diffusion coefficients and shows different susceptibility to degradation of the mechanical properties, i.e. delayed hydrogen assisted cracking or stress corrosion cracking. T2 - NACE Italia - 2nd Conference & Expo 2018 CY - Genoa, Italy DA - 28.05.2018 KW - Hydrogen KW - Stress corrosion cracking KW - Welding KW - Creep-resistant steel PY - 2018 SP - Paper 10, 1 EP - 7 AN - OPUS4-45081 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hofmann-Böllinghaus, Anja A1 - Knaust, Christian A1 - Beard, A. T1 - Computermodellierung von Wohnungsbränden unter Berücksichtigung von Rauchmeldern und Flammschutzmitteln T2 - 8. SKZ-Fachtagung "Kunststoffe, Brandschutz und Flammschutzmittel" CY - Würzburg, Deutschland DA - 2006-06-21 KW - Wohnungsbrände KW - CFD Modellierung KW - Großversuch KW - Flammschutzmittel PY - 2006 N1 - Geburtsname von Hofmann-Böllinghaus, Anja: Hofmann, A. - Birth name of Hofmann-Böllinghaus, Anja: Hofmann, A. VL - 8 SP - 1 EP - 23(?) PB - SKZ CY - Würzburg AN - OPUS4-12906 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hofmann-Böllinghaus, Anja A1 - Rabe, Frederik A1 - Gnutzmann, Tanja A1 - Kaudelka, Sven T1 - Einfluss moderner Materialien auf die Rauchentwicklung bei Wohnungsbränden N2 - Bei einzelnen Objekten, die unter Laborbedingungen verbrennen, konnte schon seit längerer Zeit ein großer Unterschied zwischen älteren und neuen Möbeln hinsichtlich der Entflammbarkeit und der Rauchentwicklung sowie der Rauchgaszusammensetzung festgestellt werden [1, 2]. In einer Serie von Großversuchen im Rahmen des vom BMBF geförderten Forschungsvorhabens TIBRO wurde in Zusammenarbeit mit der Feuerwehr Frankfurt in vier Großversuchen die Brand- und Rauchentwicklung in einem Wohnzimmer und einem angrenzenden Zimmer untersucht. Es wurden ältere Möbel und moderne Möbel sowie unterschiedliche Belüftungsbedingungen untersucht. Alle vier Brände gingen von einem Sessel aus, der mit einem Papierkissen entzündet wurde. Es wurden jeweils im Brandraum und im Nachbarraum Temperaturen gemessen sowie die zeitlich veränderliche Rauchgaszusammensetzung in zwei unterschiedlichen Raumhöhen in der Zimmermitte des Nachbarraums bestimmt [3]. Der Einfluss der in der Wohnung vorhandenen Materialien sowie der Einfluss der Belüftung auf die Brandentwicklung wurden untersucht. Sowohl die Art der Materialien als auch die Belüftung beeinflussen die Brandentwicklung signifikant. Statistiken und die Erfahrung der Feuerwehren zeigen, dass für Personen, die sich im Brandentstehungsraum befinden, die Hilfe der Feuerwehr in den meisten Fällen zu spät kommt. Für den Nachbarraum können anhand der Großversuche Abschätzungen über den Zeitgewinn für Personen, die sich dort befinden, abgeleitet werden. T2 - 63. vfdb Jahresfachtagung 2016 CY - Stuttgart, Germany DA - 8.05.2016 KW - Rauchentwicklung KW - Brand KW - Wohnung KW - Materialien PY - 2016 VL - 2016 SP - 253 EP - 266 PB - vfdb, Vereinigung zur Förderung des deutschen Brandschutzes CY - Altenberge AN - OPUS4-36021 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mente, Tobias A1 - Grimault de Freitas, Tomás A1 - Nietzke, Jonathan A1 - Konert, Florian A1 - Sobol, Oded A1 - Wackermann, Ken A1 - Ruchti, Peter A1 - Elsen-Humberg, Stefan A1 - Systermans, Thomas ED - Zimmermann, Martina T1 - Hohlzugprüfung als kostengünstige Methode zur Werkstoffcharakterisierung für die Wasserstoffwirtschaft N2 - Wasserstoff ist ein notwendiger Baustein zur Erreichung zukünftiger Klimaziele. Für eine schnell hochlaufende Wasserstoffwirtschaft ist es daher notwendig sowohl bestehende Infrastruktur als auch neue Werkstoffe für den sicheren und nachhaltigen Einsatz in Wasserstofftechnologien zu qualifizieren. Die akzeptierten und standardisierten Prüfverfahren zur Ermittlung des Einflusses gasförmigen Wasserstoffs auf die mechanischen Eigenschaften metallischer Werkstoffe sind meist sehr komplex, mit hohem technologischem und finanziellem Aufwand verbunden und stehen nur Wenigen Instituten weltweit zur Verfügung. Die Hohlzugprüftechnik bietet hier eine kostengünstige und einfach zu realisierende Alternative. Mit der im Jahr 2024 erstmals veröffentlichten ISO 7039 wurde diese Prüftechnik auch für die Wirtschaft anwendbar gemacht. Der Standard gilt allgemein für die Prüfung mit gasförmigen Medien, weist jedoch in Bezug auf die Prüfung mit gasförmigem Wasserstoff noch einige Wissenslücken auf. Im Teilvorhaben H2HohlZug des Leitprojekt TransHyDE werden die Lücken zum Einfluss der Geometrie, Oberflächenqualität sowie Gasreinheit in einzelnen Arbeitspaketen geschlossen und die Erkenntnisse in einen Standard überführt. T2 - 43. Vortrags- und Diskussionstagung Werkstoffprüfung 2025 - Werkstoffe und Bauteile auf dem Prüfstand CY - Dresden, Germany DA - 27.11.2025 KW - Hohlzugprüfung KW - Druckwasserstoff KW - ISO 7039 KW - H2HohlZug - TransHyDE PY - 2025 SN - 978-3-88355-454-9 SP - 11 EP - 17 PB - Deutsche Gesellschaft für Materialkunde e.V. (DGM) CY - Dresden AN - OPUS4-64937 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Werrel, Martin A1 - Deubel, Jan A1 - Krüger, Simone A1 - Hofmann-Böllinghaus, Anja A1 - Antonatus, E. A1 - Krause, U. A1 - Duerler, F. T1 - Use and benefit of a controlled-atmosphere cone calorimeter N2 - A controlled-atmosphere cone calorimeter that is built by modifying the Standard apparatus with the addition of a controlled-atmosphere chamber offers a time- and cost-saving approach for reaction-to-fire testing in vitiation- and ventilation-controlled atmospheres. Due to the design of the added enclosure no mechanical changes on cone calorimeter’s Standard ductwork are required. This offers some advantages but also important limitations. The design has an open connection between the outlet of the added enclosure and the cone calorimeter’s exhaust hood. Therefore, sufficient ambient air from the laboratory surroundings is drawn into the System to introduce effects which have the potential to affect test results significantly. A procedure which is is suitable to consider physical effects of the ambient air on the calculation of the heat release rate is presented as well as initial results of an application towards toxic potency assessment. Signs for Chemical effects of the ambient air such as post reactions are shown but subject of an ongoing work. T2 - Fire and materials 2013 - 13th International conference and exhibition CY - San Francisco, CA, USA DA - 28.01.2013 KW - Controlled-atmosphere cone calorimeter KW - Heat release rate KW - Oxygen consumption KW - Smoke toxicity PY - 2013 SP - 273 EP - 286 PB - Interscience Communications CY - London, UK AN - OPUS4-27707 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geoerg, Paul A1 - Schumann, J. A1 - Boltes, M. A1 - Holl, S. A1 - Hofmann-Böllinghaus, Anja T1 - The influence of physical and mental constraints to a stream of people through a bottleneck N2 - Understanding movement in heterogeneous groups is important for a meaningful evaluation of evacuation prediction and for a proper design of buildings. The understanding of interactions and influencing factors in heterogeneous groups on key performance figures is fundamental for a safe design. This contribution presents results of experimental studies on movement of a crowd through a bottleneck involving participants with and without disabilities. High precise trajectories of the attendees extracted from video recordings were used to calculate density and velocity of the participants. Besides the well-established fundamental diagram new insights into the individual relation between density and velocity are discussed. A complex structure and considerate behaviour in movement implicates a strong influence of the heterogeneity on key performance values of safe movement. T2 - 9th international conference on Pedestrian and Evacuation Dynamics (PED2018) CY - Lund, Sweden DA - 21.08.2018 KW - Human behaviour KW - Egress KW - Evacuation KW - Pedestrians with disabilities KW - Engineering data PY - 2018 SP - 57-1 EP - 57-6 CY - Lund, Sweden AN - OPUS4-46266 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nolze, Gert A1 - Saliwan Neumann, Romeo A1 - Buchheim, Michaela T1 - Microstructure investigations of iron meteorites by EBSD and EDS analyses T2 - EMC 2012 - 15th European Microscopy Congress CY - Manchester, UK DA - 2012-09-16 KW - Orientation relationship KW - Weathering KW - Hibbingite PY - 2012 UR - http://www.emc2012.org.uk//documents/Abstracts/Abstracts/EMC2012_0090.pdf SP - 1 EP - 2(?) AN - OPUS4-27922 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hofmann-Böllinghaus, Anja T1 - Brandverhalten von Wärmedämmverbundsystemen mit Polystyroldämmung N2 - Der Brandschutz von Fassaden ist deshalb so komplex, da sich sowohl die Fassadensysteme hinsichtlich ihres Aufbaus und er verwendeten Materialien als auch durch die Bandbreite an Brandschutzmaßnahmen stark voneinander unterscheiden. Da die Regelungen zum Brandschutz in der Verantwortung des jeweiligen Landes liegen, sind auch die Brandprüfungen und die Klassifizierung der Systeme sehr unterschiedlich in Europa. Auch weltweit ist die Brandsicherheit von Fassaden seit einigen Jahren ein wichtiges Thema. Brände in den letzten Jahren haben in mehreren Ländern dazu geführt, dass die Vorschriften verschärft worden sind. In Deutschland haben sich die Vorschriften für Wärmedämmverbundsystemen mit Polystyroldämmung (EPS) verschärft, nach dem mehrere Brände Untersuchungen nach sich gezogen haben, die diese Systeme bei Brandbeanspruchungen durch außerhalb des Gebäudes entstehende Brände untersucht haben. Systeme, die nicht zulassungskonform eingebaut wurden sowie beschädigte oder gealterte Systeme können höhere Ansprüche an die Robustheit der Brandschutzmaßnahmen. T2 - VdS-Fachtagung Wärmedämmung von Gebäuden CY - Köln, Germany DA - 06.12.2017 KW - Fassaden KW - Polysytyrol KW - Experimente PY - 2017 SP - 1 EP - 14 PB - VdS Schadenverhütung CY - Köln AN - OPUS4-43386 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zhu, Jiangchao A1 - Madia, Mauro A1 - Schurig, Michael A1 - Fedelich, Bernard A1 - Schlums, H. A1 - Zerbst, Uwe T1 - Burst Behaviours Of Aero Engine Turbine Disk At Overspeed Conditions N2 - Aero-engine turbine disks are safety-relevant components which are operated under high thermal and mechanical stress conditions. The actual part qualification and certification procedures make use of spin-tests conducted on production-similar disks. The aim of this work is to present part of a fracture mechanics-based procedure under development which aims at replacing the tests on production-similar disks with lab tests on fracture mechanics specimens. The finite element simulation of the cracked disk considers the real thermal and mechanical loading conditions. In order to design a lab representative specimen, beside the crack driving force, expressed in terms of 𝐽-integral, also the constraint to plastic deformation e.g., stress triaxiality, at the crack-tip must be similar for the same crack in the specimen and in the disk. This has been achieved and as expected, both the highest 𝐽 -integral and constraint factor are calculated at the same location along the crack front for both disk and specimen. The results of the structural integrity assessment in the form of a Failure Assessment Diagram (FAD) show good agreement between designed specimen and disk both in terms of expected failure mode and value of the critical speed. In addition, probabilistic aspects are also considered in the calculations. T2 - 43rd Int. Conference on Materials Mechanics, June 5-10, 2022, Greece CY - Sani, Chalkidiki, Greece DA - 05.06.2022 KW - Structural integrity KW - Turbine disk KW - Fracture mechanics KW - Overspeed PY - 2022 SP - 1 EP - 13 AN - OPUS4-57279 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Seefeldt, Henrik A1 - Braun, Ulrike A1 - Hofmann-Böllinghaus, Anja T1 - Influence of structure, wood content, moisture and additives on the burning behaviour of wood plastic composites T2 - Fire and materials 2011 - 12th International conference and exhibiton CY - San Francisco, CA, USA DA - 2011-01-31 PY - 2011 SP - 1 EP - 10 PB - Interscience Communications AN - OPUS4-24650 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Kempel, Florian A1 - Hofmann-Böllinghaus, Anja A1 - Schartel, Bernhard A1 - Krause, Ulrich T1 - Investigations on a real fire case with downward fire spread in a family home T2 - 11th International symposium on fire protection CY - Leipzig, Germany DA - 2010-06-08 KW - Fire spread KW - Heat release rate KW - Fire simulation KW - Foam mattress PY - 2010 N1 - Geburtsname von Hofmann-Böllinghaus, Anja: Hofmann, A. - Birth name of Hofmann-Böllinghaus, Anja: Hofmann, A. SP - 1 EP - 12 AN - OPUS4-22354 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hofmann-Böllinghaus, Anja A1 - Dülsen, Steffen A1 - Klippel, Alexander T1 - Problems in bus fire safety - recent developments and possible solutions N2 - Not only the severe bus fire in 2008 near Hanover in Germany with 20 fatalities showed the fire danger for coaches1,2. Also two other similar fires in Germany in May 2011 and February 2012 showed the extremely hazardous situations a fire can cause in bus3,4. In both cases young and fit passengers (pupils) could only escape because they were able to destroy Windows and escaped by jumping out of these Windows. In one case they had to escape out of the Windows of the upper deck and several were severe injured. These numerical and experimental investigations of bus fires in coaches and city buses performed by BAM are funded by the German Ministry of Transport, Building and Urban Development. Web and literature research showed that fires occur much more often than assumed. Most of the fires Start in the engine compartment. However, often the whole bus is destroyed after a fire. One reason for the rapid fire development are the fire safety regulations for the bus materials which are on a much lower level than in the other transport sectors1,2,5,6’. A lot of materials from suppliers and of operating city buses were investigated experimentally. The results were compared with regulations in the train sector because trams and city buses, trains and coaches are working under similar operating conditions, e.g. for escape possibilities. These results were used to investigate bus fires also numerically to identify very hazardous scenarios by varying materials properties, geometries and air condition settings. Additionally real scale experiments were performed on different bus seats; ignited by a paper cushion. Especially the newer bus seats showed a very low fire performance with high heat and smoke release rates. Surprisingly a city bus seat of an older bus (built in 1995) showed a better fire performance. It is assumed that the trend to cheaper and lightweight plastics is one reason that modern seats have worse fire performance. Large scale tests were performed on a city bus - smoke development, fire detection and suppression in the engine area. Several possible enhancements are discussed and recommendations are given to make buses more fire safe. T2 - Fire and materials 2013 - 13th International conference and exhibition CY - San Francisco, CA, USA DA - 28.01.2013 KW - Large scale fire tests KW - Bus materials investigation KW - Numerical fire simulation KW - CFD KW - Recommendations PY - 2013 SP - 563 EP - 574 PB - Interscience Communications CY - London, UK AN - OPUS4-28600 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hofmann-Böllinghaus, Anja T1 - Europäische Harmonisierung von Brandstatistiken für Wohngebäude N2 - Das EU Projekt EU FireStat SI2.830108, das vom Europäischen Parlament finanziert und von der DG GROW der Europäischen Kommission in Auftrag gegeben wurde, hat aufgearbeitet, welche Terminologie in den europäische Mitgliedsstaaten verwendet wird und die von den Mitgliedstaaten erhobenen Daten über Gebäudebrände zu analysieren. Dabei wurden die Schwierigkeiten bei der Erfassung und die Unterschiede bei der Auslegung ermittelt und eine gemeinsame Terminologie sowie eine Methode zur Erfassung der erforderlichen Daten vorgeschlagen. Folgende Schwerpunkte wurden bearbeitet: Zunächst erfolgte eine Diagnose von Terminologie-, Datenerhebungs- und Auslegungsproblemen, Erhebung der Terminologie und der Datenerfassung, Identifizierung der für die Entscheidungsfindung benötigten Daten, Analyse der Methoden zur Datenerhebung Definition einer gemeinsamen Terminologie, Methodik der Kosten-/Nutzenbewertung zur Unterstützung politischer Entscheidungen, Fallstudie zur Anwendung der Methode der Kosten-/Nutzenbewertung, Beschreibung einer zukünftigen Datenerhebungsmethode. Das Ergebnis des Projekts ist eine Empfehlung, welche Daten in den Mitgliedstaaten erhoben werden sollten, um wissensbasierte Entscheidungen in Bezug auf den Brandschutz zu ermöglichen. Damit wird die Grundlage für Maßnahmen und Initiativen geschaffen, die den Brandschutz und die Brandverhütung der Mitgliedstaaten unterstützen, so dass knappe Ressourcen gezielt eingesetzt werden können. T2 - 69. Jahresfachtagung der Vereinigung zur Förderung des Deutschen Brandschutzes CY - Münster, Germany DA - 15.05.2023 KW - Statistik PY - 2023 SN - 976-3-936050-36-3 VL - 2023 SP - 391 EP - 401 PB - VdS CY - Köln AN - OPUS4-57573 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kannengießer, Thomas A1 - Florian, Wolfgang A1 - Böllinghaus, Thomas T1 - Einfluss des Einspanngrades auf die Beanspruchung beim Schweißen eingespannter Bauteile T2 - 18. Tagung Werkstoffprüfung 2000 ; 18. Vortrags- und Diskussionstagung Werkstoffprüfung 2000 CY - Bad Nauheim, Deutschland DA - 2000-12-07 PY - 2000 SP - 95 EP - 102 PB - Dt. Verband für Materialforschung CY - Berlin AN - OPUS4-980 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz, Wencke A1 - Hünert, Daniela A1 - Nitschke, Heike A1 - Saliwan Neumann, Romeo A1 - Kranzmann, Axel T1 - Comparison of the corrosion behaviour of 9-12 % Cr steels in H2O, H2O-CO2 and H2O-CO2-O2 T2 - NACE International corrosion conference 2009 CY - Atlanta, Georgia, USA DA - 2009-03-22 KW - 9-12%Cr-steels KW - Steam KW - CO2 KW - O2 KW - High-temperature corrosion KW - Evaporation of chromium PY - 2009 SP - 1 EP - 10 (Paper No. 09264) AN - OPUS4-19464 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Weingärtner, A. A1 - Sobol, Oded A1 - Schümann, H. T1 - The SHIMMER project N2 - In the EU project SHIMMER, the German institute for materials research and testing BAM is working on a comprehensive knowledge database. There, important information on standards for safe materials and components as well as on the European gas infrastructure is to be made available. SHIMMER will be led by the Norwegian research organization SINTEF. The project brings together twelve European institutions, including national institutes and gas network operators from the countries Spain, Italy, Norway, Poland, Belgium, the Netherlands and Germany. The injection of hydrogen (H₂) into existing gas networks brings with it both technical and regulatory challenges. They particularly concern the material integrity of pipelines and the harmonization of legal requirements. The project SHIMMER (Safe Hydrogen Injection Modelling and Management for European Gas Network Resilience) involves improving understanding for the integration of hydrogen into the existing gas infrastructure and with that support overall the market ramp-up of safe hydrogen technologies. The research project already started in September 2023 and will end in August 2026. Financing comes from the EU program “Horizon Europe – Clean Hydrogen Partnership.” KW - European gas grid KW - Hydrogen transport and distribution KW - Database KW - Decarbonization PY - 2025 UR - https://h2-international.com/2025/01/20/the-shimmer-project/ IS - January 20, 2025 SP - 1 EP - 4 PB - Hydrogeit Verlag CY - Oberkraemer AN - OPUS4-62503 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ávila Calderón, Luis A1 - Schriever, Sina T1 - BAM Reference Data: Creep of Single-Crystal Ni-Based Superalloy CMSX-6 N2 - This publication provides comprehensive metadata and test results of constant force creep tests according to DIN EN ISO 204:2019-4 on the single crystal Ni-based superalloy CMSX-6 at T = 980 °C and initial stresses between 140 MPa and 230 MPa. The tests were carried out in an accredited test laboratory using calibrated measuring equipment. The data were audited and are BAM reference data. KW - NFDI-MatWerk KW - Digitalisierung KW - CMSX-6 KW - Creep KW - Reference Data KW - Referenzdaten KW - Ni-Based Superalloy PY - 2024 DO - https://doi.org/10.5281/zenodo.13937986 PB - Zenodo CY - Geneva AN - OPUS4-61649 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Leo, Reinhold A1 - Sobol, Oded A1 - Hango, Silas Ithete A1 - Saliwan Neumann, Romeo A1 - Askar, Enis A1 - Boellinghaus, Thomas T1 - Ex-situ investigation of the compatibility of Duplex Stainless Steel for high-pressure hydrogen applications N2 - The key to a successful transition into clean energy carriers such as hydrogen requires the construction of safe transportation pipelines made of alloys which are not susceptible to hydrogen assisted cracking. Duplex Stainless Steels (DSS) are considered as a proper class for components because of their many distinctive qualities. As this consideration depends strongly on the susceptibility level to Hydrogen Assisted Cracking (HAC), the DSS class has been broadly investigated under electrochemical charging conditions. In this work, the interplay between several factors controlling the level of HAC, was examined using light microscopy, high-pressure gaseous hydrogen pre-charging, Electron Backscatter Diffraction (EBSD), tensile testing, fractography and hydrogen concentration measurements using Carrier Gas Hot Extraction (CGHE). The effect of gaseous hydrogen on the mechanical properties with the role of hydrogen induced phase transformation have been investigated both in unused material and in high pressure pipeline section. In contrary to the common electrochemical charging described broadly in the literature, no significant martensitic phase transformation of the austenitic phase was observed. On the other hand, the influence of hydrogen on parameters such as elongation at fracture and reduction of area was noticeable. It is concluded based on the performance of DSS in gaseous hydrogen, that this material has a better potential for utilization in hydrogen applications. As for future experiments, the intention is to analyse the impact of high-pressure gaseous hydrogen on the welded components of this grade, and under mechanical load using the hollow specimen technique. T2 - 5th International Conference on Metals and Hydrogen CY - Ghent, Belgium DA - 14.10.2025 KW - High-Pressure Hydrogen KW - Pipelines KW - Duplex Stainless Steels KW - Hydrogen Assisted Cracking KW - Hollow Specimen Technique PY - 2025 SN - 978-9-08179-424-4 SP - 1 EP - 19 AN - OPUS4-64426 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Askar, Enis A1 - Grunewald, Thomas T1 - Experimental Study on the ignition of hydrogen containing atmospheres by mechanical impacts N2 - Mechanical friction, impact or abrasion is one of the ignition sources that must be avoided in hazardous zones with explosive atmospheres. The effectiveness of mechanical impacts as ignition source is dependent from several parameters including the minimum ignition energy of the explosive atmosphere, the properties of the material pairing, the kinetic impact energy or the impact velocity. By now there is no standard procedure to determine the effectiveness of mechanical impacts as ignition source. In this work the effectiveness of mechanical impacts with defined and reproducible kinetic impact energy as ignition source for hydrogen containing atmospheres was studied systematically in dependence from the inhomogeneous material pairing considering materials with practical relevance like stainless steel, low alloy steel, concrete, and non-iron-metals. It was found that ignition can be avoided, if non-iron metals are used in combination with different metallic materials, but in combination with concrete even the impact of non-iron-metals can be an effective ignition source if the kinetic impact energy is not further limited. Moreover, the consequence of hydrogen admixture to natural gas on the effectiveness of mechanical impacts as ignition source was studied. In many cases ignition of atmospheres containing natural gas by mechanical impacts is rather unlikely. No influence could be observed for admixtures up to 25% hydrogen and even more. The results are mainly relevant in the context of repurposing the natural gas grid or adding hydrogen to the natural gas grid. T2 - International Conference on Hydrogen Safety (ICHS) 2023 CY - Quebec City, Canada DA - 19.09.2023 KW - Explosion protection KW - Hydrogen transport in pipelines KW - ATEX KW - Hazardous areas KW - Mechanical sparks KW - Ignition source PY - 2023 SN - 979-12-210-4274-0 SP - 82 EP - 93 AN - OPUS4-58515 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hofmann-Böllinghaus, Anja A1 - Mühlnikel, Rüdiger T1 - Experimental and numerical investigation of fire development in a real fire in a five storey dwelling N2 - A fire in a five storey dwelling was investigated experimentally and numerically. The room of origin of the fire was a living room in the second floor and the fire was started by a candle on a television set. The fire spread externally over the building facade and internally along the stair case and affected all the flats above and leading to two fatalities. The fire thought to have been detected minutes after ignition and the fire service was called very short after the detection and was at the scene 9 minutes after the call. By this time large sections of the facade were on fire already. The rapid fire spread over the facade and the stair case necessitated detailed investigations. Compliance of building products with the building regulations was investigated. One conclusion ot the investigations was that the person who caused the fire by leaving the candle on the TV set unattended should not be held responsible for the two fatalities in the upper floors. T2 - Fire and materials 2009 - 11th International conference and exhibiton CY - San Francisco, USA DA - 2009-01-26 PY - 2009 N1 - Geburtsname von Hofmann-Böllinghaus, Anja: Hofmann, A. - Birth name of Hofmann-Böllinghaus, Anja: Hofmann, A. SP - 723 EP - 733 PB - Interscience Communications AN - OPUS4-20026 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hofmann-Böllinghaus, Anja A1 - Dülsen, Steffen T1 - Verbesserung der Brandsicherheit von Bussen N2 - Bei ca. 1 % aller Busse im Jahr tritt ein Brandereignis auf. Die Brände, die sich oft vom Motorraum aus entwickeln, breiten sich in den meisten Fällen sehr schnell aus und haben oft den Totalverlust des Busses zur Folge. Die Zeit, die Passagieren zur Selbstrettung bleibt, ist sehr kurz. Das zeigen sehr deutlich die schweren Busbrände vom November 2008, Mai 2011 und Februar 2012 in Deutschland. Im November 2008 kamen 20 der 32 Passagiere ums Leben, weil sie sich nicht mehr selbst aus dem Bus retten konnten. Im Mai 2011 und im Februar 2012 war es nur der Fitness und Entschlossenheit der jungen Passagiere zu verdanken, dass es nicht zu Todesopfern kam: die Passagiere konnten die Scheiben des Busses einschlagen und sich durch den Sprung aus dem Fenster retten, einige verletzten sich dabei schwer. In dem von der Bundesanstalt für Straßenwesen (BASt) geförderten Projekt wurde sowohl anhand von Realfällen als auch von umfangreichen experimentellen Untersuchungen an Busmaterialien und begleitend dazu mit numerischen Untersuchungen die aktuelle Brandsicherheit von Bussen untersucht. Der Vergleich mit den anderen Transportsektoren - insbesondere mit der Bahn - ergab, dass die Brandsicherheit von Bussen weit unter der Brandsicherheit der anderen Transportsektoren liegt, obwohl die Bedingungen bei Straßenbahnen und Linienbussen und Fernzügen und Reisebussen durchaus vergleichbar sind. Auf Grund der umfangreichen Untersuchungen wurden Verbesserungsvorschläge erarbeitet, die die Zeit, die den Passagieren zur Selbstrettung bleibt, signifikant verlängern können. Es wurden dabei sowohl die in Bussen eingesetzten Materialien hinsichtlich ihrer Entflammbarkeit, der Wärme- und Rauchfreisetzung, als auch andere Maßnahmen wie Löschanlagen untersucht und bewertet. Dazu wurden auch Großversuche an einem intakten Bus durchgeführt. Ein Katalog an Maßnahmen wurde erarbeitet, der die Brandsicherheit in Bussen entscheidend verbessern kann. T2 - Vfdb 2013 - 61. Jahresfachtagung CY - Weimar, Germany DA - 27.05.2013 KW - Bus KW - Brand KW - Materialien KW - Anforderungen KW - Simulationen KW - FDS PY - 2013 SP - 481 EP - 494 CY - Altenberge AN - OPUS4-29980 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hofmann-Böllinghaus, Anja A1 - Kaudelka, Sven A1 - Gnutzmann, Tanja A1 - Rabe, Frederik A1 - Klippel, A. T1 - Influence of modern furniture on the fire development in fires in homes N2 - About 80 % of all fire fatalities in Germany occur in fires in homes1. UK statistics show that living and bed room fires are more often responsible for fatalities than kitchen fires although kitchen fires occur much more often2. It has been known for some time that modern materials tend to burn differently from older materials and it has been acknowledged that the amount of combustible plastics in homes has increased significantly over the last decades3-7. To investigate the influence of modern furniture and ventilation conditions of fires in homes a series of four large scale tests in two living rooms with adjacent rooms was performed by BAM and the Frankfurt fire service8. Two living rooms, one with older furniture and one with modern furniture were tested twice each. Each test started with the ignition of a paper cushion on an upholstered chair. The influence of modern materials on the fire development was investigated as well as the influence of the ventilation on the fire development. Two tests with closed windows and two tests with open windows were performed. Temperatures were measured in the living rooms and the adjacent rooms, gas compositions were measured in the adjacent rooms and videos were taken in all rooms. The ventilation as well as the different materials influenced the fire development regarding temperatures in the rooms and smoke production and composition significantly. The fire in the living room with modern furniture developed faster than the same setting with older furniture. More ventilation (open window) led to higher temperatures in the rooms and faster fire development as well. Smoke gas composition was measured in the adjacent rooms to assess the positive effect for a person being in the adjacent room and not in the room of fire origin. In all settings an upholstered chair was the first burning item. The modern upholstered chair was investigated in three pre-experiments under different conditions to enhance the understanding of the living room fires. The measured mass losses and derived mass loss rates have been used for numerical modelling of the pre-experiments. T2 - Fire and Materials Konferenz CY - San Francisco, USA DA - 06.02.2017 KW - Furniture KW - Fire KW - Large scale PY - 2017 SP - 280 EP - 294 PB - Interscience AN - OPUS4-42925 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mente, Tobias A1 - Böllinghaus, Thomas ED - Somerday, B. P. ED - Sofronis, P. T1 - Mesoscale Numerical Simulation of Hydrogen-Assisted Cracking in Duplex Stainless Steels N2 - A two-dimensional numerical mesoscale model has been created representing a microstructure of a typical 2205/1.4462 duplex stainless steel to further elucidate the mechanisms of hydrogen-assisted crack initiation and propagation in multiphase non-hydride forming metallic microstructures. Hydrogen-assisted cracking (HAC) was simulated by considering different stress and strain behavior as well as different diffusion behavior in both phases. For simulation of crack initiation and propagation, the element elimination technique has been applied. The model allows the simulation of path-free crack propagation which contributes to a better understanding of the HAC process in two-phase microstructures. As a particular result, the analyses revealed that a global macroscopic elastic deformation might already cause plastic deformation in both phases entailing respective HAC. T2 - International Hydrogen Conference CY - Jakson Lake Lodge, Wyoming, USA DA - 11.09.2016 KW - Computer simulation KW - Cracking (Materials) KW - Fracture (Process) KW - Hydrogen KW - Stainless steel PY - 2017 SN - 978-0-7918-6138-7 DO - https://doi.org/10.1115/1.861387_ch67 SP - 589 EP - 596 PB - The American Society of Mechanical Engineers (ASME) CY - New York AN - OPUS4-45680 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böllinghaus, Thomas A1 - Hoffmeister, H. A1 - Stiebe-Springer, I. A1 - Florian, Wolfgang A1 - Michael, Thomas T1 - Component testing of welded supermartensitic stainless steel pipes T2 - EUROCORR 2000 CY - London, England, UK DA - 2000-09-10 PY - 2000 SP - 1 EP - 10 PB - IOM Communications CY - London AN - OPUS4-22138 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Suárez Ocano, Patricia A1 - Agudo Jácome, Leonardo A1 - Lopez-Galilea, I. A1 - Darvishi Kamachali, Reza A1 - Fries, S. G. T1 - Data regarding the experimental findings compared with CALPHAD calculations of the AlMo0.5NbTa0.5TiZr refractory high entropy superalloy N2 - This contribution contains the raw data used to compare experimental results with thermodynamic calculations using the CALPHAD method, which is related to the research article “The AlMo0.5NbTa0.5TiZr refractory high entropy superalloy: experimental findings and comparison with calculations using the CALPHAD method” [1] , and therefore this article can be used as a basis for interpreting the data contained therein. The AlMo0.5NbTa0.5TiZr refractory superalloy was characterized in the cast and annealed condition (1400 °C for 24 h) in order to measure grain size and to identify and measure the size and area fraction of the phases present. The raw data of this article include X-ray diffraction (XRD) measurements, microstructural characterization by scanning and transmission electron microscopy (SEM and TEM), and elemental analysis by energy dispersive X-ray spectroscopy (EDX). XRD includes the determination of phases and the lattice parameters (A2, B2, and hexagonal structure). Microstructural analysis by scanning and transmission electron microscopy includes (1) identification of composition, size, and volume fraction of the present phases and (2) determination of grain size. Based on these experimental data, it is possible to identify similarities and discrepancies with the data calculated using the CALPHAD method for the alloy under study in Ref. [1] , which provides the basis for better and more efficient development of reliable databases. KW - Microstructural characterization KW - Refractory high entropy alloys KW - Scanning electron microscopy KW - Transmission electron microscopy PY - 2023 DO - https://doi.org/10.17632/d742ccty5f.4 PB - Mendeley Data CY - Oxford, UK AN - OPUS4-56861 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scholz, A. A1 - Nazmy, M. A1 - Fedelich, Bernard A1 - Tinga, T. A1 - Huls, R. T1 - Modelling of microstructure and mechanical property changes in gas turbine alloys T2 - 9th Liège conference: Materials for advanced power engineering 2010 CY - Liège, Belgium DA - 2010-09-27 KW - Nickel base superalloys KW - Degradation KW - Modelling KW - Microstructure KW - Mechanical properties PY - 2010 SP - 567 EP - 587 AN - OPUS4-22261 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Kianinejad, Kaveh T1 - Multiscale Modelling of Creep Anisotropy in Additively Manufactured IN738LC N2 - Excellent creep resistance at elevated temperatures, i.e. T / Tm> 0.5, due to gamma-gamma’ microstructure is one of the main properties of nickel-based superalloys. Due to its great importance for industrial applications, much research has been devoted to understanding the underlying deformation mechanism in a broad spectrum of temperature and loading conditions. Additive Manufactured (AMed) nickel-based superalloys, while being governed by similar \gamma-gamma’ microstructure, exhibit AM-process specific microstructural characteristics, such as columnar grains, firm crystallographic texture (typically <001> fibre texture parallel to build direction) and compositional inhomogeneity, which in turn leads to anisotropic creep response in both stationary and tertiary phases. Despite the recent insights on the correlation between process parameters and the resulting microstructure, these materials' anisotropic creep behaviour and corresponding deformation mechanism are insufficiently understood. One reason is the lack of capable material models that link the microstructure to the mechanical behaviour. Within the present work, a multiscale approach has been developed to overcome this challenge by combining microstructure-based mesoscale and phenomenological macroscale models. The mesoscale model utilizes the Crystal Plasticity Finite Element Method (CPFEM) to include the microstructural characteristics and the relevant deformation mechanism on the polycrystalline scale. The mesoscale model was then used to perform virtual creep experiments required to calibrate the macroscale model. The developed approach has been applied to characterise the creep behaviour of AMed IN738LC. The effect of different slip systems, crystallographical texture, grain morphology, and Grain Boundary Sliding (GBS) on creep anisotropy at 850°C has been investigated. The approach's ability to capture the AM-specific characteristics and link them to the observed macroscale anisotropic response has been demonstrated, and the contribution of primary underlying deformation mechanisms to creep anisotropy has been elucidated. KW - Creep anisotropy KW - Crystal plasticity KW - Addtively manufactured Nickel-based Alloys alloy PY - 2025 SP - 1 EP - 135 PB - RWTH Aachen CY - Aachen AN - OPUS4-64598 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Meyer, Ronald T1 - The Pressure Resistance of hollow Glass Fibers at internal Pressure Load N2 - Glass has different outstanding material-specific properties which offer theoretically the application of thin-walled hollow fibers in the field of high pressure gas storage. Especially the storage of hydrogen as renewable and environmental friendly energy carrier is possible. Glass is an amorphous material which is characterized by a theoretical tensile strength much higher than this of other materials. However, in practice the tensile strength is decreased significantly by defects on the glass surface or in the material and its network structure. As part of this thesis the burst pressures of hollow glass fibers were determined. The burst pressure correlates very well with the tensile strength of hollow glass fibers. By using the Weibull statistic the results of different test series were evaluated in respect to failure probabilities and compared to each other. Thereby the influence of various parameters on the pressure resistance was investigated. Beside the influence of the chemical composition of the material the aging by environmental and their effect on the pressure resistance was investigated. Additionally hollow glass fibers were loaded dynamically and statically with different gases. Afterwards the burst pressure was determined and the effect of used gas on the pressure resistance could be determined as well as the impact of method and duration of loading. A further influence of the dimension of hollow glass fibers on their resistance against inner pressure load is the ratio between wall thickness and inner diameter which was investigated as well as the combination of different glasses and the utilization of their disparate coefficient of thermal expansion which lead to prestressing of the hollow glass fiber. Finally, the impact of the variation of several production parameters on the pressure resistance was determined experimentally as like as the influence of surface coatings. These shall protect the glass surface from subsequently procured defects and, hence, increase the pressure resistance. As essential part of current thesis the defect analysis of test samples of various series was done whereby the differentiation between material and production dependent defects was important. Not only a light microscope but a scanning electron microscope was used for the investigation, as well. Beside volume defects like bubbles or inclusions surface defects in the form of scratches or spalling can be detected and observed. A calculation of the failure-causing defect size from measured burst pressure is possible. Dependent on the dimension and determined burst pressure value of each single fiber defect sizes of less than one micron were calculated. Particularly the geometry of the test samples inappropriate for many examination methods and the fact that the calculated defect size occurs only under loaded conditions at actual burst pressure the local detection of corresponding defect rendered impossible. In the end, the present thesis shows the pressure resistance of hollow glass fibers and their potential to store safely gases under high pressure. N2 - Glas besitzt einige herausragende materialspezifische Eigenschaften, die theoretisch den Einsatz von dünnwandigen Hohlfasern zur Hochdruckspeicherung von Gasen zulassen. Besonders die Speicherung von Wasserstoff als regenerativer Energieträger ist denkbar. Glas ist ein amorphes Material, welches sich durch eine theoretische Zugfestigkeit auszeichnet, die mehrfach höher ist als anderer Materialien. Jedoch wird die Zugfestigkeit in der Praxis durch Defekte auf der Glasoberfläche oder im Material und dessen Netzwerk deutlich herabgesetzt. In dieser Arbeit wurde der Berstdruck von hohlen Glasfasern ermittelt, wobei der Berstdruck sehr gut mit der Zugfestigkeit von Gläsern korreliert. Unter Verwendung der Weibull Statistik wurden die Ergebnisse der verschiedenen Versuchsreihen hinsichtlich möglicher Ausfallwahrscheinlichkeiten ausgewertet und miteinander verglichen. Der Einfluss verschiedener Parameter wurde untersucht. Neben der chemischen Materialzusammensetzung wurde auch die Alterung durch Umwelteinflüsse und deren Wirkung auf die Druckfestigkeit gegen innere Belastung untersucht. Zusätzlich wurden die Hohlglasfasern unter Verwendung verschiedener Prüfgase zyklisch und statisch vor der Berstdruckbestimmung belastet, um die Wirkung des verwendeten Gases als auch der Art und Dauer der Belastung auf das Material zu bestimmen. Ein weiterer Einfluss auf die Druckfestigkeit von Hohlglasfasern ist das Wandstärken-Innendurchmesser-Verhältnis, welcher ebenso untersucht wurde wie die Kombination verschiedener Gläser mit unterschiedlichen thermischen Ausdehnungskoeffizienten, die zu Vorspannungen in den Glasfasern führen. Abschließend wurde die Auswirkung von Variationen verschiedener Produktionsparameter auf die Druckresistenz ebenso experimentell bestimmt wie der Einfluss von Beschichtungen, die die Glasoberflächen vor nachträglich beigebrachten Defekten schützen und die Druckfestigkeit bei innerer Belastung erhöhen sollen. Wichtiger Bestandteil der Arbeit ist die Defektanalyse von Prüfmustern einzelner Testreihen. Es muss zwischen material- und produktionsbedingten Defekten unterschieden werden. Neben der Untersuchung von Hohlglasfasern mittels Lichtmikroskop wurde auch ein Rasterelektronenmikroskop verwendet. Sowohl Volumendefekte, wie Blasen und Steinchen, als auch Oberflächendefekte, in Form von Kratzern oder Ablagerungen, konnten als produktionsbedingte Defekte beobachtet werden. Materialbedingte Fehler wie Fehlstellen im Netzwerk konnten mit den verwendeten Untersuchungsmöglichkeiten nicht ermittelt werden. Aus den ermittelten Berstdücken von Hohlglasfasern lassen sich die zum Versagen führenden Defektgrößen errechnen. Abhängig von Dimension der Faser und erreichtem Berstdruck ergeben sich Defektgrößen kleiner als ein Mikrometer. Insbesondere durch die für viele Untersuchungsmethoden ungünstige Geometrie der Prüfmuster sowie die Tatsache, dass die errechneten Defektgrößen nur unter Spannung beim vorliegenden Berstdruck auftreten, war eine örtliche Bestimmung des entsprechenden Defekts bzw. die Zuordnung zu ermittelten Defekten nicht möglich. Letztlich zeigt die vorliegende Arbeit, dass Hohlglasfasern unter bestimmten Voraussetzungen die erforderliche Druckfestigkeit aufweisen, um Gase unter Druck sicher speichern zu können. KW - Wasserstoffspeicherung KW - Glaskapillaren KW - Festigkeiten KW - Defekte KW - Einflussparameter PY - 2015 SP - 1 EP - 237 PB - Otto-von-Guericke-Universität CY - Magdeburg AN - OPUS4-37075 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hofmann-Böllinghaus, Anja A1 - Kaudelka, Sven T1 - Wärmedämmverbundsysteme - Neue Erkenntnisse aus Brandversuchen und Analysen aktueller Brandereignisse N2 - Die aktuellen, mit Wärmedämmverbundsystemen (WDVS) in Verbindung stehenden Brandereignisse wurden zum Anlass genommen, eine Serie von Brandversuchen im Kleinmaßstab in der Single Burning Item (SBI) Prüfeinrichtung durchzuführen. Dabei wurde die auf das WDVS wirkende Wärmefreisetzungsrate variiert und der Einfluss von Grad und Größe von Beschädigungen der Putzschicht hinsichtlich des Brandverhaltens untersucht. Deutliche Unterschiede im Brandverhalten konnten sowohl quantitativ als auch qualitativ nachgewiesen werden. Neben der den Versuchsbedingungen zugrunde liegenden Wärmefreisetzungsrate konnten Art und Lage der Beschädigung in der Putzschicht als brandbeeinflussende Größen charakterisiert und beschrieben werden. Zusätzlich zu den Versuchen und der Auswertung der Realbrandereignisse wurden Abfallcontainer aus Kunststoff als mögliche Zündquelle für Fassadenbrände hinsichtlich des Brandverhaltens untersucht. T2 - Vfdb 2014 - 62. Jahresfachtagung der Vereinigung zur Förderung des Deutschen Brandschutzes e.V. CY - Dortmund, Germany DA - 16.16.2014 PY - 2014 SP - 293 EP - 304 AN - OPUS4-30906 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fedelich, Bernard A1 - Kiyak, Yusuf A1 - Toulios, M. A1 - Voudouris, G. ED - Portella, Pedro Dolabella ED - T. Beck, ED - M. Okazaki, T1 - Modelling of high temperature crack growth in a single crystal superalloy under low cycle fatigue loading T2 - 6th International Conference on Low Cycle Fatigue (LCF 6) CY - Berlin, Germany DA - 2008-09-08 KW - Single Crystal Superalloy KW - Fatigue Crack Growth KW - Creep-Fatigue-Oxidation interactions PY - 2008 SP - 409 EP - 414 AN - OPUS4-18946 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hofmann-Böllinghaus, Anja A1 - Knaust, Christian A1 - Krüger, Simone T1 - Brandverhalten von Bauprodukten - Brauchen wir Regelungen für die Menge und Giftigkeit der Rauchgase? PY - 2008 N1 - Geburtsname von Hofmann-Böllinghaus, Anja: Hofmann, A. - Birth name of Hofmann-Böllinghaus, Anja: Hofmann, A. IS - 3 SP - 24 EP - 27 PB - Vds Schadenverhütung Verl. CY - Köln AN - OPUS4-18378 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Krüger, Simone A1 - Hofmann-Böllinghaus, Anja A1 - Krause, Ulrich T1 - Chemical analysis of smoke of burning upholstered bus seats T2 - 11th International symposium on fire protection CY - Leipzig, Germany DA - 2010-06-08 KW - Upholstered seats KW - FTIR spectroscopy KW - Combustion KW - Smouldering KW - Fire behaviour PY - 2010 N1 - Geburtsname von Hofmann-Böllinghaus, Anja: Hofmann, A. - Birth name of Hofmann-Böllinghaus, Anja: Hofmann, A. SP - 1 EP - 12(?) AN - OPUS4-21445 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hünert, Daniela A1 - Schulz, Wencke A1 - Nitschke, Heike A1 - Saliwan Neumann, Romeo A1 - Oder, Gabriele A1 - Kranzmann, Axel T1 - Corrosion behaviour of ferritic and martensitic power plant steels under conditions of dual atmospheres N2 - The most efficient construction materials for boiler water walls and superheaters in steam power plants are ferritic and martensitic steels. In practical operation tubes are simultaneously exposed to combustion gas and air/steam on their opposite surfaces. The corrosion behaviour of ferritic-martensitic steels under such dual atmospheres is nondistinctive and has therefore been investigated in a special designed test equipment between 500 and 620°C. The power plant conditions were simulated wi th a flowing and pressurised (80 bar) combustion gas on the inner side of the tube which mainly consists of H2O and/or CO2. On the outer side, the tube material was exposed to air. It was discovered that under similar temperatures the oxides formed on the air side under dual atmosphere conditions were significantly different to the oxide scales formed when the alloy was exposed to air only. It is assumed that the anomalous corrosion behaviour during the dual atmosphere exposure is due to the hydrogen transport through the bulk alloy from the combustion gas side to the air side. T2 - NACE International corrosion conference 2009 CY - Atlanta, Georgia, USA DA - 2009-03-22 KW - High temperature corrosion KW - Dual atmosphere KW - Corrosive gases KW - Mild steels KW - 9-12% Cr-steels KW - Hydrogen transport PY - 2009 SP - 1 EP - 10 (Paper 09263) AN - OPUS4-22335 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ben-Hamu, G. A1 - Eliezer, D. A1 - Cross, Carl Edward A1 - Böllinghaus, Thomas T1 - Volta potential of second phase particles in TIG welded AZ31 magnesium sheet T2 - EUROCORR 2006 CY - Maastricht, The Netherlands DA - 2006-09-25 KW - TIG welding KW - AZ31 Magnesium Alloy KW - Corrosion behavior PY - 2006 N1 - Serientitel: EFC-Event – Series title: EFC-Event IS - 280 SP - 1 EP - 10 PB - European Federation of Corrosion CY - Maastricht AN - OPUS4-22134 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hofmann-Böllinghaus, Anja A1 - Krause, Ulrich T1 - Wer kontrolliert den Brandschutz im Bestand? T2 - 58. Jahrestagung der Vereinigung zur Förderung des Deutschen Brandschutzes e.V. (vfdb) CY - Mannheim, Deutschland DA - 2009-05-24 PY - 2009 N1 - Geburtsname von Hofmann-Böllinghaus, Anja: Hofmann, A. - Birth name of Hofmann-Böllinghaus, Anja: Hofmann, A. SP - 426 EP - 440 AN - OPUS4-19461 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fedelich, Bernard A1 - Owen, J. ED - Bell, R. ED - Merati, A. ED - M. Nganbe, ED - Tyson, B. ED - Wang, X. T1 - Creep damage by multiple cavity growth controlled by grain boundary diffusion T2 - ICF12 - 12th International Conference on Fracture CY - Ottawa, Canada DA - 2009-07-12 KW - Grain boundary cavitation KW - Hochtemperatur KW - Kriechen KW - Schädigung KW - Korngrenzenporosität KW - High temperature KW - Creep KW - Damage PY - 2009 SP - 1 EP - 10 AN - OPUS4-20623 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geoerg, Paul A1 - Polzin, R. M. A1 - Schumann, J. A1 - Holl, S. A1 - Hofmann-Böllinghaus, Anja T1 - Small-scale studies on evacuation characteristics of pedestrians with physical, mental or age-related disabilities N2 - Evaluation of evacuation process is common separated by two phases: pre-movement and movement-phase. Individual capabilities of pedestrians have an impact on both and therefore on the time required for safe escape. In view of evaluating the evacuation process, characteristics of realistic movements of pedestrians involved are needed, but so far such data are mainly available for individuals with unrestricted evacuation capabilities only. Due to the lack of available data, parameter studies in an assisted living for people with disabilities were performed to explore the movement during evacuation. Preparation times for assistance (n=10), unimpeded walking speeds (n=34) depending on the assistance devices in the plane as well as walking speeds on stairs (n=11) were focussed. Time to prepare an assistance device for utilisation depends significantly on the kind of device type. Further on, practical experience in handling the devices for assistance has an impact on the preparation time. In contrast to the results of the preparation times, any relation on assistance devices were investigated for the unimpeded walking speed in the plane. A remarkable decrease of walking speed on stairs was observed which is independent from the utilised assistance device. The presented data improve and extend the insufficient engineering data base and raised up questions regarding the complexity of considering pedestrians movement with impairments in evacuation planning. T2 - 3rd European Symposium on Fire Safety Science CY - Nancy, France DA - 12.09.2018 KW - Evacuation KW - Human behaviour KW - Egress KW - Pedestrians with disabilities KW - Engineering data KW - Unimpeded walking speed KW - Pre-movement KW - Movement PY - 2018 SP - 214966-1 EP - 214966-6 AN - OPUS4-46268 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dülsen, Steffen A1 - Hofmann-Böllinghaus, Anja A1 - Krause, Ulrich T1 - Untersuchung zu Brandursachen und Brandverlauf bei Busbränden N2 - Busbrände treten relativ häufig auf, auch wenn sich das im öffentlichen Bewusstsein nicht unbedingt widerspiegelt. Nach einer eigenen Internetrecherche brennt etwa an jedem zweiten Tag ein Bus in Deutschland. Die grundlegenden Brandschutzvorschriften für Busse gehen auf die amerikanische Norm FMVSS 302 zurück, die in den 60er Jahren entwickelt wurde und ist quasi weltweit noch immer in sämtlichen nationalen und internationalen Brandschutzvorschiften wiederzufinden. Ziel der FMVSS 302 ist es vor allem, Fahrzeugbrände durch das Rauchen zu verhindern. Verschiedene Untersuchungen zeigen jedoch, dass die meisten Busbrände andere Ursachen haben und zu ca. 80 % im Motorraum entstehen. Auch das Versagen von elektrischen Komponenten ist häufiger die Brandursache. Dies geschah z.B. im Jahr 2008 bei einem schweren Busbrand in der Nähe von Hannover, bei dem sich gerade einmal 13 Passagiere selber retten konnten und 20 Menschen ihr Leben verloren. Einige Brandleichen wurden sogar noch am Sicherheitsgurt angeschnallt aufgefunden. Durch die enorme Zunahme brennbarer Kunststoffteile in Bussen entstand ein bisher unberücksichtigtes Risiko, das bei der Normentwicklung in den 1960er Jahren nicht berücksichtigt wurde. So hat sich die Brandlast seitdem etwa verzehnfacht und das toxische Potential erheblich gesteigert. Nach wenigen Minuten muss bei den Brandopfern bereits mit einem schnellen Tod durch Rauchgasvergiftungen gerechnet werden. Aufgrund der schnellen Brandentwicklung in Bussen können Passagiere in den allermeisten Fällen nicht bis zum Eintreffen der Feuerwehr warten und müssen sich selber retten. Die Zeit für die Selbstrettung muss signifikant verlängert werden, so dass auch mobilitätseingeschränkte Passagiere eine Chance zum Verlassen des Busses haben. Der Vergleich mit Brandschutzanforderungen anderer Transportsektoren (Bahn, Schiff, Flugzeug) zeigt, dass die Anforderungen dort sehr viel höher sind. Sowohl die Entflammbarkeit als auch die Wärmefreisetzung sowie die Rauchfreisetzung werden in diesen Normen begrenzt. Zudem werden Materialanforderungen hinsichtlich der Rauchgastoxizität gestellt. Im Ergebnis dieser Arbeit sollen einerseits Brandschutzempfehlungen für die zweckmäßige und zugleich wirtschaftlich vertretbare Ausstattung von Bussen im Innenbereich unterbreitet werden. Andererseits sollen auch Überarbeitungsvorschläge für Prüftests vorgestellt werden, die den Brandschutz von Kraftomnibussen sicherstellen und erstmals auch Grenzwerte für die Rauchgastoxizität beinhalten. Dazu werden neben den Brandversuchen auch numerische Simulationen mit dem Fire Dynamics Simulator (FDS, Version 5, NIST) durchgeführt, in denen verschiedene Brandszenarien mit unterschiedlichen Buskategorien simuliert werden. T2 - 59. vfdb-Jahresfachtagung CY - Berlin, Deutschland DA - 2011-05-30 PY - 2011 SP - 805 EP - 816 AN - OPUS4-23847 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Gröschl, Christian T1 - Examination of stress and strain in glass structures during pressure treatment using FEM simulation and experimental tests N2 - Glass is an amorphous material. When compared to steel, both its density and weight is three times lower. Its high theoretical strength makes it stand out as a premier material for a variety of applications. One such application is acting as a pressure resistant vessel for gas storage. Because glass has a high theoretical strength this makes it potentially suitable to withstand much higher pressures than steel or composite vessels. As a result of its brittle character, glass breaks when reaching a critical stress level. Therefore, the stress distribution during pressure load needs to be homogeneous without local stress peaks. At those peaks an initial crack will occur and the material will break. This PhD thesis is primarily concerned with the determination of the strength of several structures made of single hollow glass fibers during inner pressure treatment. Therefore, different kinds of hollow glass structures with varying parameters of shape and dimension were examined concerning their strength by determining the burst pressure. The burst pressure method was compared to the tensile test method, which poses the common test method for examining the strength of a material. The conclusion reached was that both test methods lead to comparable results and therefore, the burst pressure method poses an adequate tool for examining the strength of a hollow material against inner pressure. Another tool used in this thesis is the Finite Elements Method (FEM) simulation of internal stress and expansion of glass structures during pressure treatment. FEM was used to validate the burst pressure test results. A few selected material parameters needed to be incorporated, most notably the Young’s Modulus. Therefore, the expansion of single glass fibers was measured with light microscope during pressure load. Within the parameters of expansion, wall thickness and applied pressure, the Young’s Modulus was calculated with the Barlow’s Formula. According to the results, different two-dimensional models from single fibers to complex structures with up to 1000 single fibers were constructed and simulated with the CFD software Comsol Multiphysics. The expansion as well as the principal stress during pressure load was calculated. Different dimensions as well as different geometries of the glasses were considered to find a structure with the highest possible free volume and at the same time as less stress peaks as possible. This calculation was made in order to determine the best structure for gas storage. For this purpose the calculations were done with different dimensions of round single fibers right up to hexagonal structures consisting of more than one thousand round single fibers, which resulted in constant expansion of the structure. Furthermore, the problem of occurring interspaces between round single fibers, regarding their burst pressure-decreasing influence, was approached. Closing these interspaces with glass or other materials to avoid unsolicited pressure load led to increased strength of the structure and low storage capacities due to the increased weight and less free inner volume. The behavior of hexagonal fibers was determined as single fiber as well as in bundled condition. The walls between two hexagonal single fibers with applied inner pressure showed homogeneously distributed stress. Merely the outer walls without counter pressure showed high deformation and high structural stress. Based on that knowledge, several structures were modeled varying in different aspects. The fibers with hexagonal shape showed optimal stress distribution and high storage capacities because of high free inner volume, provided that these fibers are surrounded by additional fibers with identical inner pressure. Reducing the wall thickness for even higher free inner volume led to similar distribution but higher stress and expansion. To overcome the problem with the high stress at the outer fibers, the influence of outer fibers with different shape and dimension was simulated as well as the influence of solid glass fibers at the outer layer of the structure. The results showed that a structure with hexagonal thin-walled fibers should be surrounded by round fibers with higher wall thickness. This way the high stress peaks at the outer fibers are lowered. The examined practical strength of glass is about 100 to 1000 times lower than the theoretical strength. This is caused by defects, which may occur at the glass surface by handling or inside the material by defective production. Since the modeled results are based on the theoretical strength, the optimal wall thickness with a good compromise of strength and free inner volume needs to be found in practical tests. If further handling of the structures is necessary, an outer layer of solid fibers works as a protection layer against damages at the outer hollow glass fibers and increases the strength. Additionally, the influence of collapsing fibers inside a structure on the remaining system has been modeled as well as the influence of defects like holes or cracks at the surface or manufacturing induced defects inside the material. Any kind of defect leads to areas of high stress, whereby failure occurrence will be encouraged. In order to approve the theoretical results, the simulated structures were compared to the previously manufactured and tested ones. Due to the burst pressure test results, the tested structures showed low strength compared to the theoretical strength. This was primarily caused by the existence of defects in the material and on the surface of the glass structures. Therefore, the production process needs to be optimized in order to prevent such defects. Furthermore, an additional protection against outer influence like air humidity or the physical contact to other materials is required. KW - Glass structures KW - Hollow fibres KW - Stress and strain PY - 2016 SP - 1 EP - 252 PB - Universitätsbibliothek CY - Magdeburg AN - OPUS4-39257 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Askar, Enis A1 - Schmidt, Martin A1 - El Harrab, Hayat A1 - Pekalski, Andrzej T1 - Ignition Indices of Hydrogen Mixtures under Electrolysis Process Conditions N2 - The formation of hydrogen-oxygen mixtures for example due to cross-over, malfunction or start-up and shut-down processes is a hazard very specific to given electrolysis processes that must be properly addressed. In this work the explosion limits of hydrogen-oxygen-mixtures at conditions up to 30 bar and 300 °C were determined experimentally. It was found that the existing experimental data can be interpolated with good accuracy using empirical approaches. Moreover, explosion limits at atmospheric conditions were also determined with reduced ignition energy, down to 1 mJ. Although in the literature it can be found that the ignition energy of flammable gases increases strongly when the concentration changes from stoichiometric to near the explosion limits, no significant influence on the mixture concentration was found within tested ignition energy range for H2/O2 mixtures. Finally, hot surface ignition for mixtures with 6 mol% hydrogen in oxygen, thus slightly above the explosion limit, were experimentally studied at different pressures up to 30 bara. Similarly, only slight difference from the ignition temperatures determined for stoichiometric mixtures were found. A 0D adiabatic, constant-volume reactor model was used to calculate the ignition temperatures. The model was tested for its prediction of ignition temperatures of hydrogen mixtures at different pressures. T2 - 11th International Conference on Hydrogen Safety (ICHS) 2025 CY - Seoul, South Korea DA - 22.09.2025 KW - Explosion limits KW - Ignition temperature KW - Ignition energy KW - Electrolyzer PY - 2025 SN - 979-12-243-0274-2 VL - 11 SP - 1259 EP - 1271 AN - OPUS4-64525 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Stelling, Karen A1 - Lammers, Marco A1 - Gumenyuk, Andrey A1 - Böllinghaus, Thomas A1 - Rethmeier, Michael T1 - Laser Plasma Hybrid Welding of Austenitic Stainless Steels - Phenomena of Process Instability N2 - Laser plasma hybrid welding has been proved to be a very stable hybrid welding process and welds of high quality can be produced, especially if high surface quality and low spattering is demanded such as in welding fabrication of high alloyed austenitic stainless steels. In particular cases, even though welds display high outer quality, X-ray examinations revealed weld defects which may range from low porosity to blowhole-like cavities. The phenomena and the main influencing parameters such as arc current, welding speed and focal point position are discussed. Parameter fields will be suggested for welding plates of different austenitic stainless steel grades with thicknesses ranging from 3 to 8 mm. The results are based on welding experiments carried out using a 4.4 kW diode pumped Nd:YAGlaser. Thus, also the influence of the feeding fibre diameter has been investigated and it was found that the resulting beam shape has a major effect on the welding performance. T2 - 60th IIW Annual Assembly CY - Dubrovnik, Croatia DA - 2007-07-01 KW - Laser KW - Plasma KW - Hybrid welding KW - Pores KW - Cavities KW - Root dropping KW - Austenitic steel PY - 2007 IS - IV-933-07 SP - 1 EP - 14 PB - International Institute of Welding CY - Paris AN - OPUS4-18677 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bettge, Dirk A1 - Klinger, Christian A1 - Ell, Matthias A1 - Klingbeil, Dietmar A1 - von Oppel, Kay A1 - Singh, Kai A1 - Eberle, Arno A1 - Engelhardt, Monika A1 - Bogel, Bärbel A1 - Saliwan Neumann, Romeo T1 - Schadensanalyse an Rohrbögen von Dampferzeugeranlagen T2 - VGB-Fachtagung "Dampferzeuger, Industrie und Heizkraftwerke 2006" CY - Würzburg, Deutschland DA - 2006-09-04 KW - Schadensanalyse KW - Brüche KW - Dampferzeuger KW - Transportschaden PY - 2006 PB - VGB PowerTech e.V. CY - Essen AN - OPUS4-12817 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hofmann-Böllinghaus, Anja A1 - Krüger, Simone A1 - Knaust, Christian T1 - Untersuchung realer Wohnungsbrände durch Großversuch und Computermodellierung T2 - 10. SKZ Fachtagung - Kunststoffe, Brandschutz und Flammschutzmittel CY - Würzburg, Deutschland DA - 2009-05-13 PY - 2009 N1 - Geburtsname von Hofmann-Böllinghaus, Anja: Hofmann, A. - Birth name of Hofmann-Böllinghaus, Anja: Hofmann, A. IS - Abschnitt F SP - 1 EP - 17 PB - SKZ CY - Würzburg AN - OPUS4-19612 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Hofmann-Böllinghaus, Anja T1 - Modellierung eines Entstehungsbrandes und die Anwendung auf den Single Burning Item Test KW - Entstehungsbrand KW - Modellierung KW - Computational Fluid Dynamics KW - Brandschutz im Bauwesen KW - Europäische Normung PY - 2003 N1 - Geburtsname von Hofmann-Böllinghaus, Anja: Hofmann, A. - Birth name of Hofmann-Böllinghaus, Anja: Hofmann, A. SP - 1 EP - 220 CY - Berlin AN - OPUS4-3220 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Askar, Enis A1 - Schröder, Volkmar A1 - Tashqin, Temir A1 - Habib, Abdel Karim A1 - Schütz, S. A1 - Seemann, A. T1 - Explosion protection for mixtures of hydrogen and natural gas N2 - Safety characteristics for explosion protection for mixtures of hydrogen and natural gas were studied in laboratory tests. Also calculations on the explosion zones for mixtures of hydrogen and natural gas were conducted. Moreover calculation methods for the safety characteristics of such mixtures were tested aiming to reduce the high effort for the experimental determination of safety characteristics prospectively. Admixture of up to 10 mole% hydrogen to natural gas has very low influence on safety characteristics for explosion protection. With increasing hydrogen fraction the mixtures become mainly more „critical“ considering explosion protection, an substantial influence on explosion protection occurs for hydrogen fractions of more than 25 mole%. T2 - 21st World Hydrogen Energy Conference 2016 (WHEC) CY - Saragossa, Spain DA - 13.06.2016 KW - Power-to-gas KW - Explosion regions KW - Safety of hydrogen KW - Hydrogen energy KW - Explosion groups PY - 2016 SP - 818 EP - 819 AN - OPUS4-37998 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dülsen, Steffen A1 - Hofmann-Böllinghaus, Anja A1 - Scholzen, G. T1 - Brände in Busdepots - eine bisher nicht beachtete Gefahr? N2 - Im Dezember 2011 verursachte ein Feuer in einem Busdepot in Nordrhein-Westfalen (NRW) einen Totalverlust der kompletten Abstellhalle mitsamt aller 70 dort abgestellten Busse und weiteren Fahrzeuge. Die Grundfläche der im Jahre 1976 erstellten Halle betrug ca. 5.000 m2. Es handelte sich um ein massives Gebäude mit Stahlbetonstützen und Stahlbetonbindern für die Dachkonstruktion. Die Dacheindeckungbestand aus Trapezblechen mit Wärmedämmung und Bitumenbahnen. Lichtkuppeln waren ebenso vorhanden wie integrierte Rauch-/Wärmeabzugsanlagen. KW - Busdepot KW - Brand PY - 2014 VL - 21 IS - 1 SP - 18 EP - 24 PB - Vds Schadenverhütung Verl. CY - Köln AN - OPUS4-32064 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Le, Quynh Hoa A1 - Bäßler, Ralph A1 - Peetz, Christoph A1 - Buggisch, Enrico A1 - Bettge, Dirk A1 - Kranzmann, Axel T1 - Electrochemical study on wellbore constellations for CO2 injection N2 - Carbon Capture and Storage (CCS) is identified as an excellent technology to reach the target of CO2 reduction. However, the safety issue and cost effectiveness hinder the future of CCS. For the reliability and safety issues of injection wells the corrosion resistance of the materials used needs to be determined. In this study, representative low cost materials including carbon steel 1.8977 and low alloyed steel 1.7225 were embedded in cement to mimic the realistic casing-cement interface. Electrochemical studies were carried out using these metal-cement specimens in comparison with those made of metal only in CO2 saturated synthetic aquifer fluid, at 333 K, to reveal the effect of cement on the steel performance. The results showed the protective effect of cement on the performance of pipeline metals during polarisation process. However, the corrosion current density was high in all cases, with and without cement, indicating that the corrosion resistance of these materials is low. This conclusion was supported by the surface analysis of the polarized specimens, which revealed both homogenous and pitting corrosions. T2 - EUROCORR 2018 CY - Krakow, Poland DA - 09.09.2018 KW - CCUS KW - Supercritical/dense phase CO2 KW - Carbon steels KW - Martensitic steel KW - Superaustenite steel KW - Injection KW - Impurities PY - 2018 SP - 1 EP - 4 PB - EFC CY - Krakau, Poland AN - OPUS4-46291 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Swanson, C. A1 - Böhme, Susanne A1 - Günster, Jens ED - Singh, Gurpreet T1 - Mechanistic Studies of Compacted and sintered rock salt N2 - This chapter discusses different approaches for the densification of rock salt powders via compaction and sintering, focusing on the use of powder qualities obtained by crunching and milling of the natural rock salt. The chapter also examines the effect of compaction pressure, time and temperature on sintering of rock salt. Natural rock salt samples were crushed and milled in a disc mill to obtain fine powders in an experiment. The hot stage microscope allowed observing the in-situ volumetric shrinkage to be determined during the sintering process by measuring the area of the sample's projection in an optical setup by a CCD camera. Images were collected at a rate of 40 frames per minute. After the application of high pressures, the obtained samples are translucent and show the formation of macroscopic crack. Powder compacts prepared by uniaxial pressing, at different maximum pressures, were annealed at a constant heating rate (10 K min-1) to different maximum temperatures. These experiments were performed in a conventional sintering furnace under ambient atmosphere. T2 - Materials Science and Technology (MS&T '15) CY - Columbus, Ohio, USA DA - 04.10.2015 KW - Rock Salt Sintering PY - 2016 SN - 978-1-119-32463-8 DO - https://doi.org/10.1002/9781119323303.ch14 VL - 259 SP - 159 EP - 172 PB - John Wiley & Sons CY - New York AN - OPUS4-39149 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Goebbels, Jürgen A1 - Isecke, Bernd A1 - Beck, Matthias A1 - Burkert, Andreas A1 - Bäßler, Ralph T1 - Monitoring of corrosion processes in chloride contaminated mortar by electrochemical measurements and X-ray tomography N2 - Corrosion of steel reinforcement in concrete exposed to chloride containing environments is a serious problem in civil engineering practice. Electrochemical methods, e.g. potential mapping, provide information whether the steel reinforcement is still passive or depassivation has been initiated. By applying such techniques no information on the type of corrosion, its extent and distribution of corrosion products is available. Particular the corrosion progress is a significant problem. Especially in the case of element corrosion in reinforced concrete structures, the development at the anode can not be separated into corrosion damage causing by element corrosion or self-corrosion. Until now also in laboratory tests it is impossible to collect such information without destroying specimens after electrochemical testing was performed place. To overcome this problem it was tried to study the steel surface within the mortar specimens by X-ray tomography (CT). Within the scope of these investigations it could be shown, that X-ray tomography is suitable to make corrosion pits visible which are embedded in a mortar with a cover thickness of about 35 mm. In this publication the corrosion damage of reinforced steel is documented timedependent by X-ray tomography. T2 - EUROCORR 2008 CY - Edinburgh, Scotland, UK DA - 2008-09-07 KW - Self-corrosion KW - X-ray tomography KW - Reinforcement KW - Concrete parameters PY - 2008 N1 - Serientitel: EFC-Event – Series title: EFC-Event IS - 299 SP - 1 EP - 10 PB - DECHEMA CY - Frankfurt am Main AN - OPUS4-17868 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kratzig, Andreas A1 - Bettge, Dirk A1 - Le, Quynh Hoa A1 - Bäßler, Ralph A1 - Kranzmann, Axel T1 - Interaction of Oxidizing and Reductive Components in CO2 Streams with Transport Pipeline Steel X70 at High Pressure and Low Temperature N2 - Specific amounts of oxidizing and reductive impurities as well as some moisture were added to dense phase CO2 to replicate CO2 streams from sources in a CCS pipeline network. Due to the moisture content being only 50 ppmV no visible acid condensation took place. To simulate stress conditions at the inside pipeline surface due to fluid pressure (10 MPa) specimens were preloaded using a load frame. Experiments conducted at 278 K and at 313 K revealed the highest corrosion rate at lower temperature. Corrosive effect of impurities was strongest applying mixed atmosphere, containing oxidizing and reductive components, closely followed by CO2 streams with pure oxidizing character. By far, the lowest corrosion rate (10x lower) resulted from reductive atmosphere. In general, at constant temperature and pressure the CO2 stream composition strongly influences the morphology, thickness and composition of the corrosion products. Applying oxidizing or mixed impurities, iron hydroxides or oxides (e.g. goethite, hematite) occur as dominating corrosion products, capable to incorporate different amounts of sulfur. In contrast, using reductive atmosphere very thin corrosion layers with low crystallinity were developed, and phase identification by XRD was unfeasible. SEM/EDX analysis revealed the formation of Fe-O compounds, most likely attributed to the oxygen partial pressure in the system induced by CO2 (≥0.985 volume fraction) and volatile H2O. In addition to the surface covering corrosion layer, secondary phases had grown locally distributed on top of the layer. These compounds are characteristic for the applied atmosphere and vary in number, shape and chemical composition. T2 - 14th Greenhouse Gas Control Technologies Conference (GHGT-14) CY - Melbourne, Australia DA - 21.10.2018 KW - CCS KW - CO2 Corrosion KW - Pipelines PY - 2019 UR - https://ssrn.com/abstract=3365756 VL - 2019 SP - 1 EP - 15 AN - OPUS4-49711 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pötzsch, Sina A1 - Weltschev, Margit A1 - Bäßler, Ralph T1 - Compatibility of polymers exposed to heating oil blends with 10 % and 20 % biodiesel (FAME) N2 - Biodiesel (FAME) from rapeseed is an environmentally friendly alternative to common fossil fuels. It is also suitable to serve as blending component to fuels like heating oil. If the fuel composition is changed, materials compatibility must be guaranteed. Adding polar biodiesel to nonpolar heating oil, changes the blend’s solvency and might cause swelling, extraction and solvation of polymers. The objective of this research was to investigate the compatibility of polymeric materials, which are commonly used for components in middle distillate facilities, along with blends of heating oil and 20 % biodiesel (B20). For this propose, ACM, HNBR, FKM, PE, PA 6, POM, PUR and PVC were exposed to heating oil and B20 for 42 and 84 days at 40 °C. In addition, the polymers HNBR, FKM, PA, POM and PVC were also exposed at 70 °C. Furthermore, the resistance of polymers in eight-year aged B10 at 40 °C was evaluated. Ageing of biodiesel increases acidity which might propagate polymer corrosion. The materials were evaluated as resistant, if the loss in tensile properties (tensile strength and elongation at break) and Shore hardness remained under 15 % compared to the initial unexposed material values. For investigations under compressed conditions, the compression set was determined for specimens of ACM, FKM and HNBR after exposure in heating oil B0 and B20 for 3,7,14, 28, 56 and 90 days at 40 °C according to ISO 815-1. It was found that the resistance in B20 at 40 °C was given for all tested polymers except PUR. In the 8 years aged B10, PUR and POM were not compatible and ACM just conditionally compatible. At 70 °C, FKM and PVC were resistant in B20, whereas HNBR and PA 6 were not compatible. Swelling occurred for the elastomers ACM, HNBR and PUR. T2 - AMPP Annual International Corrosion Conference 2021 CY - Online Meeting DA - 19.04.2021 KW - Biodiesel KW - FAME KW - RME KW - Polymer in fuels PY - 2021 SP - 16222-01 EP - 16222-12 CY - Houston AN - OPUS4-52499 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dudziak, Mateusz T1 - Thermal properties of polymer nanocomposites based on polycarbonate (PC) and boehmite N2 - Nanocomposites are extremely versatile due to their physicochemical properties, which differ significantly from bulk homopolymers. One of the inorganic nanomaterials which are increasingly used as a filler in polymer matrices is boehmite, typically used as an inexpensive flame retardant. Here, it is used as a nanofiller in polycarbonate and polyamide, expecting to improve their mechanical properties. For industrial use boehmite is obtained by the solvothermal method, resulting in a layered nanomaterial, whereas naturally it occurs as single crystals with the size of <100µm. In this work we are obtaining and isolating boehmite crystals by a bottom-up method, in which a reaction between aluminum nitride and sodium hydroxide. Obtaining boehmite as microcrystals is necessary for its analysis and characterization, as well as to investigate its interaction with polymer matrices at the polymer/particle interface. Here, the obtained particles in polymer matrices are characterized with differential scanning calorimetry and thermogravimetry analysis. T2 - DPG-Frühjahrstagung 2019 CY - Regensburg, Germany DA - 31.03.2019 KW - Boehmite KW - Polycarbonate PY - 2019 AN - OPUS4-47768 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wöhlecke, Andreas ED - Al-Akel, Said T1 - Aktuelle Diskussionen aus dem Fachbeirat der BAM N2 - Im Folgenden soll über aktuelle Diskussionen und Arbeitsschwerpunkte im Fachbeirat der BAM und von der Zulassungsstelle berichtet werden. Es werden Änderungen im Zusammenhang mit der Zulassungsrichtlinie für Kunststoffdichtungsbahnen vorgestellt. Es wird über die aktuelle Diskussion über die Anforderungen z. B. an metallische Sensoren für Dichtungskontrollsysteme berichtet. Änderungen der Fremdprüfung von sogenannten Sandschutzmatten, des Standards zur Qualitätsüberwachung (SQÜ) von Kunststoff Dränelementen (KDE) und der Anpassung der Formulierungen zum Überbau der in Abdichtungen verwendeten Produkte werden aufgezeigt. T2 - 20. Leipziger Deponiefachtagung CY - Leipzig, Germany DA - 12.03.2024 KW - Dichtungskontrollsystem KW - Deponie KW - Kunststoffdichtungsbahn PY - 2024 SN - 978-3-943443-54-7 VL - 20 SP - 16 EP - 23 CY - Leipzig AN - OPUS4-59893 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wöhlecke, Andreas T1 - Die Zulassung von Geokunststoffen nach der deutschen Deponieverordnung N2 - Seit dem Erscheinen der Deponieverordnung (DepV) bedürfen Geokunststoffe, Polymere und Dichtungskontrollsysteme einer Zulassung durch die BAM, wenn diese in deutschen Deponieabdichtungssystemen eingesetzt werden sollen. Die DepV ermöglicht den Einsatz verschiedener Komponenten. Sie stellt dabei allgemeine Anforderungen an die Geokunststoffprodukte auf. Dadurch beschreibt sie den Stand der Technik für Geokunststoffe, die in deutschen Abdichtungen eingesetzt werden. Diese Anforderungen werden durch die Zulassungsrichtlinien der BAM in konkrete technische Spezifikationen überführt. In dem Beitrag wird eine Übersicht über die Produkte und die entsprechenden Anforderungen gegeben. Zudem soll erläutert werden, durch welche Qualitätsmanagementmaßnahmen eine gleichbleibende Qualität und Funktionserfüllung der Produkte gewährleistet wird. T2 - 14. DEPONIEWORKSHOP Liberec - Zittau 2018 CY - Liberec, Czech Republic DA - 15.11.2018 KW - Deponie KW - Geokunststoffe KW - Polymere KW - Dichtungskontrollsysteme PY - 2018 VL - 14 SP - 149 EP - 158 PB - Technische Universität Liberec, Hochschule Görlitz/Zittau CY - Liberec, Tschechien AN - OPUS4-46660 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wöhlecke, Andreas ED - Kim, Bumjoo ED - Kim, Yun-Tae ED - Hong, Gigwon ED - Jung, Young-Hoon ED - Chong, Song-Hun T1 - The “zero leakage” approach and German regulations for geosynthetics used in landfill liner and capping systems N2 - An approach to achieve “zero leakage” is discussed with respect to the experience in Germany, where strict regulations for landfill lining and capping systems have been developed and issued because of large environmental problems related to landfills that accumulated in the 1970’s and 1980’s. These regulations for landfills and geosynthetics which are used in landfill liner and capping systems are shortly described. The main certification requirements for the products as well as conclusions for their use are presented. Using a thick, high quality HDPE geomembrane (GMB), which is installed free of residual waves and wrinkles in intimate contact with a compacted clay liner (CCL) or geosynthetic clay liner (GCL) of very low permeability, by a qualified, experienced, well equipped and properly third‐party controlled installer and which are protected by heavy protection layers designed with respect to long‐term performance of the GMB, may result in a liner or capping system of practically no leakage. This is demonstrated by analyzing results of measurements obtained from permanently installed leak detection systems in combination with HDPE GMBs. T2 - 11th International Conference on Geosynthetics CY - Seoul, Korea DA - 16.09.2018 KW - HDPE geomembrane KW - Landfill liner KW - Leak detection KW - Regulations PY - 2018 VL - 11 SP - 1 EP - 8 AN - OPUS4-46030 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wöhlecke, Andreas ED - Al-Akel, S. T1 - Aktuelle Diskussionen zur vorläufigen Zulassungsrichtlinie von Bewehrungsgittern für Deponieoberflächenabdichtungen und zu Auftragsnähten in Kunststoffdichtungsbahnen N2 - Die BAM wurde 2009 u. a. mit der Zulassung von Bewehrungsgittern für den Deponiebau beauftragt. Der Stand von Wissenschaft und Technik bot jedoch keine ausreichende Grundlage, die tatsächlich relevanten Widerstände und die mit diesen Widerständen verbundene Wechselwirkung zwischen Gitter und Boden im Hinblick auf eine mindestens 100-jährige Funktionsdauer realistisch beurteilen zu können. Es wurde daher nur eine vorläufige Zulassungsrichtlinie für diese Produkte erarbeitet. In der Zwischenzeit hat sich ein neuer Kenntnisstand ergeben. Vor diesem Hintergrund hat die AG (Arbeitsgruppe) Geogitter des Fachbeirats der BAM am 26.09.2017 getagt. Es sollen die aktuellen Erkenntnisse und Schlussfolgerungen für die Zulassung in Kürze vorgestellt werden. Die entsprechenden Kapitel beruhen dabei auf einem Arbeitspapier von W.W. Müller und dem Autoren, das der Arbeitsgruppe zur Diskussion vorgelegt wurde. Weiterhin soll über Entwicklungen in Zusammenhang mit Kunststoffdichtungsbahnen (KDB) berichtet werden. Die Anforderungen an die Schweißzusätze für das Extrusionsschweißen wurden angepasst. Zudem soll über die aktuelle Diskussion der Schweißbarkeit unterschiedlicher HDPE Materialien informiert werden. Die maßgebliche DVS (Deutscher Verband für Schweißen und verwandte Verfahren) Richtlinie 2225-4 wird derzeit offenbar so ausgelegt, dass Materialien mit völlig unterschiedlichen Schmelze-Massefließrate miteinander verbunden werden können. Dies steht allerdings im grundlegenden Widerspruch zum Stand der Technik. T2 - 14. Leipziger Deponiefachtagung - Planung, Bau, Betrieb, Stilllegung, Nachsorge und Nachnutzung von Deponien CY - Leipzig, Germany DA - 06.03.2018 KW - Deponietechnik KW - Bewehrungen aus Kunststoff KW - Kunststoffschweißen PY - 2018 SN - 978-3-943443-47-9 VL - 14 SP - 53 EP - 68 AN - OPUS4-44417 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Adam, Christian A1 - Suhendra, Suhendra A1 - Vogel, Christian A1 - Krüger, Oliver A1 - Tetzlaff, K. T1 - Production of marketable multi-nutrient fertilisers from different biomass ashes and industrial by-products N2 - Sewage sludge ashes (SSA) contain considerable mass fractions of phosphorus (5-10 w-% P) suitable for fertiliser production. Unfortunately, also most of the heavy metals remain in the ashes. A thermochemical process was developed for the treatment of SSA to i) remove heavy metals and ii) transform phosphates into bio-available mineral phases. The technology was already demonstrated in technical scale (capacity of 300 kg/h) and the company OUTOTEC is currently planning the first industrial plant. In order to manufacture a marketable multi-nutrient fertiliser from the thermochemically treated SSA further wastes and industrial by-products were taken into account. Ammonium sulphate occurs as a by-product of the caprolactam production and was chosen as N-carrier (21 w-% N). Straw ash was tested as potassium carrier (11-15 w-% K). Granulation campaigns were carried out with intensive mixers in lab-, medium-and technical scale. NPS-and NPKS-fertilisers were produced that were characterised by suitable particle size distributions and strength. T2 - ASH Utilisation 2012 CY - Stockholm, Sweden DA - 25.01.2012 KW - Sewage sludge ash KW - Recycling fertiliser KW - Heavy metals KW - Thermochemical treatment KW - Bioavailability PY - 2012 SP - 1 EP - 7 CY - Stockholm, Sweden AN - OPUS4-25496 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Crasselt, Claudia A1 - Schmidt, Wolfram A1 - Sturm, Heinz ED - M. Tyrer, ED - E. Ganjian, ED - West, A. T1 - Influence of rheology modifying admixtures on hydration of cementitious suspensions N2 - The presence of polycarboxylate ether (PCE) based superplasticizers (SPs) has an enormous influence on the early hydration of cement. The hydration is retarded and the timing of formation and the morphology of hydrates is affected. This short paper presents experimental results about the influence of delayed Addition time of PCE SPs on hydration of cement and tricalcium aluminate (C3A) pastes, investigated by isothermal heat flow calorimetry. For cement pastes the hydration is retarded with SP, whereby the high charge PCE has a stronger retarding effect than the low charge PCE. With delayed PCE addition the cement shows a less retarded setting than with simultaneous addition. The alteration caused by PCE is much more pronounced for C3A and gypsum mixes than for cement. If the SP is added simultaneous, the exothermic peak of C3A is retarded. However, with delayed addition of SP the hydration is shortened, the gypsum depletion is fastened and the exothermic peak occurs less retarded or even accelerated compared to simultaneous addition. It is obvious that for C3A pastes there is less retardation the later the Addition of SP. Furthermore, the PCE alter the hydration of C3A when added delayed and exhibit changes in kinetics and hydration rates. The rate of reaction in the second stage is lower, discernible in decreased slopes and broader peaks. Besides this, a distinct ramp in the C3A heat flow curves within the first stage of C3A hydration occurs for all pastes with delayed addition of SP, which suggests an accelerated ettringite formation. T2 - 38th Cement and Concrete Science Conference CY - Coventry, UK DA - 10.09.2018 KW - Cement hydration KW - Polycarboxylate ether KW - C3A hydration PY - 2018 SN - 978-1-84600-088-1 SP - 64 EP - 67 CY - Coventry, UK AN - OPUS4-45995 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hahn, Marc Benjamin A1 - Solomun, Tihomir A1 - Sturm, Heinz T1 - Standard procedure for the irradiation of biomolecules with radiation of different linear energy transfer N2 - The damage caused by ionizing radiation to DNA and proteins is the reason to treat cancer by radiation therapy. A better understanding of the molecular processes and quantification of the different damaging mechanisms is the prerequisite to develop more efficient therapies. Hereby the understanding of the processes involved in the damage to DNA are of key interest due to its central role in reproduction and mutation. For radiation with low linear energy transfer (LET), most of the damage is caused by the secondary particles produced by scattering of the ionizing radiation with water. Thereby a multitude of species are produced, whereby especially kinetic low energy electrons, prehydrated electrons, OH-radicals and ions are of importance. With higher LET the relative amount of the direct damaging effects increases. This is especially important considering the increased usage of high LET nucleons in radiation therapy. Therefore, the quantification of the contribution to DNA damage of direct and indirect effects and the different secondary species is of high interest due to the increase of radio biological efficiency when applying high LET radiation. Here we present an approach to investigate the relative contributions to DNA strand break yield for radiation of different LET within a single electron microscope in combination with electron scattering simulations. T2 - XI International Radiation Protection Association Conference 2018 America CY - Havanna, Cuba DA - 16.04.2018 KW - Dosimetry KW - Linear energy transfer KW - Radiation damage KW - LET KW - Electron irradiation KW - Low energy electrons KW - Hydroxyl radicals KW - DEA KW - DET KW - Microdosimetry KW - Geant4 KW - Electron irradiation of DNA KW - DNA PY - 2018 VL - 2018 SP - 1 EP - 5 AN - OPUS4-44848 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schraut, Katharina A1 - Adamczyk, Burkart A1 - Simon, Sebastian A1 - von Werder, Julia A1 - Meng, Birgit A1 - Stephan, D. A. A1 - Adam, Christian T1 - Zementklinker durch Nachbehandlung von Stahlwerksschlacken N2 - Die Klinkerphasenbildung durch Sinterung in Drehrohröfen bei der Herstellung von Portlandzementklinker (PZK) ist gründlich erforscht und optimiert. Im Hinblick auf mögliche ökonomische und ökologische Vorteile befassen sich aktuelle Forschungsvorhaben darüber hinaus mit der Herstellung von Klinkermineralen aus Stahlwerksschlacken, die eine vergleichbare chemische Zusammensetzung aufweisen. Neuste Untersuchungen zeigen, dass nach der reduzierenden Behandlung schmelzflüssiger Linz-Donawitz-(LD)-Schlacken und Abscheidung des gebildeten metallischen Eisens eine mineralische Schlacke entsteht, die unabhängig von ihren Abkühlbedingungen ca. 50–60 Gew.% des wichtigsten Klinkerminerals Alit (C3S) enthält und eine hohe hydraulische Reaktivität aufweist. Die Stabilität des Alits auch nach langsamer Abkühlung deutet auf eine Stabilisierung des Minerals durch Nebenelemente aus den LD-Schlacken hin. Ein sinkender Anteil an LD-Schlacke durch Zusatz synthetischer Schlackemischung, die sich hinsichtlich ihrer Hauptkomponenten wie eine ausreduzierte LD-Schlacke zusammensetzt, führt zu einem Rückgang des Alitgehaltes und dem Zerfall der Schlacke beim Erstarren. T2 - 5. Schlacken-Symposium CY - Meitingen, Germany DA - 25.10.2018 KW - LD-Schlacke KW - Zement KW - Tricalciumsilikat PY - 2018 SP - 219 EP - 229 PB - Max Aicher Unternehmensgruppe AN - OPUS4-46412 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mota Gassó, Berta A1 - Schmidt, Wolfram A1 - Pauli, Jutta A1 - Sturm, Heinz T1 - Influences of hydration effects on the flow phenomena of concrete with admixtures N2 - Today, chemical admixtures like superplasticisers and stabilising agents are extremely important for modern concrete technology. These agents have meanwhile become common practice in concrete technology, but the understanding within the entire system lags far behind their application. The macroscopic rheology of concrete in the presence of superplasticizers strongly depends upon effects on a much smaller scale such as the hydration of the cement, the adsorption of superplasticizers, and the pore solution chemistry. T2 - 2nd International Conference on the Chemistry of Construction Materials CY - München, Germany DA - 10.10.2016 KW - Rheology KW - Cement KW - Superplasticiser PY - 2016 SN - 978-3-936028-96-6 VL - 50 SP - 276 EP - 279 PB - Gesellschaft Deutscher Chemiker e.V. CY - Frankfurt am Main AN - OPUS4-38849 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wöhlecke, Andreas A1 - Müller, Werner ED - Al-Akel, S. T1 - Aktuelle Themen aus der Arbeit des BAM-Fachbeirats und von der -Zulassungsstelle N2 - Welche Themen und Fragestellungen haben den Fachbeirat der BAM, seine Arbeitsgruppen und die BAM seit der letzten Fachtagung in Leipzig beschäftigt? Die Richtlinie Fremdprüfer und deren Anlagen wurden entsprechend der aktuellen Anforderungen angepasst. Die einzelnen Punkte wollen wir vorstellen. Im Zusammenhang mit Geotextilien zum Filtern und Trennen und Kunststoff Dränelementen wurden zwei Themen bearbeitet: (1) Die europäischen Anwendungsnormen und das deutsche Straßenbaumerkblatt für Geokunststoffe verwenden statistische Begriffe. Deren nur „beiläufige“ Erwähnung lässt jedoch offen, was genau im Zusammenhang gemeint ist. Produkte unterschiedlicher Hersteller können daher trotz gleicher Angaben zu den Mindestwerten in den Leistungserklärungen oder Datenblättern deutlich unterschiedliche Eigenschaften haben. Um vorschriftsmäßig bemessen zu können, muss man jedoch wissen, was sich hinter den Zahlen verbirgt. Eine Zulassung oder Zertifizierung ist nur dann sinnvoll, wenn darüber hinaus einheitlich definiert wird, was die Angaben für die werkseigene Produktionskontrolle, die Inspektion durch benannte Stellen und die Kontrolle durch Dritte bedeuten. In den vergangenen Jahren seit 2009 wurde versucht, die Zulassungen stärker auf die Vorgaben aus der europäischen Normung zu stützen. Daher musste nun diskutiert werden, welche statistische Bedeutung die Angaben in den Zulassungen für Kunststoff Dränelementen und Geotextilien zum Filtern und Trennen haben. Hier musste eine einheitliche Regelung getroffen werden. (2) Die Langzeiteigenschaften von polyolefinen Geokunststoffen sind maßgeblich von den eingesetzten Stabilisatoren abhängig. Wie kann hier eine Überwachung während der Produktion der Geokunststoffe implementiert werden, wenn die Rezepturbestandteile der Produkte sensible Firmengeheimnisse der Rohstoffhersteller sind? Hier musste eine Lösung erarbeitet werden. Über die Ergebnisse soll berichtet werden. Wir möchten weiterhin über Entwicklungen in Zusammenhang mit Kunststoffdichtungs-bahnen (KDB) berichten. Die DVS (Deutscher Verband für Schweißen und verwandte Verfahren) Richtlinie 2225-4 regelt das Schweißen der KDB auf der Deponiebaustelle. Werden KDB im strukturierten Bereich miteinander verschweißt, werden die Strukturen in der Regel vorher abgetragen. Die DVS Richtlinie sieht unter bestimmten Voraussetzungen von einem Abtragen der Strukturen ab. Vor diesem Hintergrund wurde vom AK GWS ein Untersuchungsprogramm initiiert, das die Auswirkungen aufzeigen soll. Darüber haben wir bereits im letzten Jahr berichten. Das Untersuchungsprogramm wurde abgeschlossen. Die Ergebnisse und Schlussfolgerungen werden nun vorgestellt. T2 - 13. Leipziger Deponiefachtagung CY - Leipzig, Germany DA - 07.03.2017 KW - Deponie KW - Fremdprüfung KW - Kunststoffdichtungsbahnen KW - Geotextilien PY - 2017 SN - 978-3-943443-43-1 SP - 43 EP - 56 AN - OPUS4-39312 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Stephan, Ina A1 - Rupp, K. A1 - Blech, B. T1 - Test development to show the efficacy of preservatives in spin finishes N2 - Test development to Show the efficacy of biocides against bacteria in spin finishes as used in textile industries to influence surface characteristics of threads. KW - Biocide KW - Spin finish KW - Textile KW - Bacteria KW - Efficacy PY - 2017 SN - 978-0-9926498-1-4 SP - 128 EP - 128 CY - Manchester, UK AN - OPUS4-42004 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hahn, Marc Benjamin A1 - Solomun, Tihomir A1 - Meyer, Susann A1 - Kunte, Hans-Jörg A1 - Schröter, Maria-Astrid A1 - Sturm, Heinz T1 - Development of a standard procedure for the irradiation of biomolecules N2 - In dosimetry the determination of the effectiveness of the damaging processes is standardized and accounted for by the radiation and tissue weighting factor. For the underlying constituents of the tissue, that is the various biomolecules, such a systematic approach doesn't exist. This makes it difficult to compare results obtained under different experimental conditions. In the following work, we will describe a method to obtain comparable values for the radiation-biomolecule interaction, measured under different conditions. This approach can lead to standardization of dosedamage relationship at the molecular level. Such approach is necessary for a better understanding of the relations between the damage of the single constituents of biological tissue and the whole – finally gaining a more complete picture of irradiation damage. T2 - 14th International Congress of the International Raditation Protection Association (IRPA) CY - Cape Town, South Africa DA - 09.05.2016 KW - Dosimetry PY - 2017 VL - 14 SP - 1 EP - 5 AN - OPUS4-41164 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stephan, Ina A1 - Kutnik, M. A1 - Conti, E. A1 - Klamer, M. A1 - Nunes, L. A1 - van Acker, J. A1 - Plarre, Rüdiger T1 - Guidance on the European Biocidal Products Regulation concerning Efficacy of Wood Preservatives N2 - In Europe wood preservatives belong to Product Type 8 (PT8) of the Biocidal Products Regulation (BPR, EU n. 528/2012), which regulates the authorisation of biocidal active substances and products in the European market. The applicant, who aims to obtain authorization to place a product onto the European market, needs to submit data to substantiate the label claims for the intended uses. Label claims are a central issue in the assessment of efficacy. The aim of this paper is to raise awareness of the recently issued “Guidance on the Biocidal Products Regulation” concerning the evaluation of efficacy of wood preservatives. This guidance document is addressed to the applicants as well as to the competent authorities of the member states of Europe in charge of assessing efficacy data, and has been in the public domain, in its latest version, since February 2017. The CEN/Technical Committee 38 “Durability of wood and wood based products” / WG 22 "Performance, assessment and specification” decided to bring the Guidance to a wider audience with the aim of disseminating the information and to trigger discussion among the experts of IRGWP. An excerpt of the Guidance that is relevant to wood preservative products is presented in an Annex to this paper. Keywords: Biocidal Products Regulation, BPR, authorisation, Guidance, PT8, curative wood preservatives, preventive wood preservatives. T2 - IRG48 Scientific Conference on Wood Protection CY - Universität Ghent, Belgium DA - 04.06. 2017 KW - Preventive wood preservatives KW - Biocidal Products Regulation KW - BPR KW - Authorisation KW - Guidance KW - PT8 KW - Curative wood preservatives PY - 2017 SN - 2000-8953 SP - IRG/WP 17-20627-1 EP - 17 AN - OPUS4-40576 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wöhlecke, Andreas ED - Egloffstein, Thomas ED - Burkhardt, Gerd T1 - Arbeits- und Diskussionsthemen aus dem Fachbeirat der BAM und von der Zulassungsstelle N2 - Die BAM wurde 2009 u. a. mit der Zulassung von Bewehrungsgittern für den Deponiebau beauftragt. Der Stand von Wissenschaft und Technik bot jedoch keine ausreichende Grundlage, die tatsächlich relevanten Widerstände und die mit diesen Widerständen verbundene Wechselwirkung zwischen Gitter und Boden im Hinblick auf eine mindestens 100-jährige Funktionsdauer realistisch beurteilen zu können. Es wurde daher nur eine vorläufige Zulassungsrichtlinie für diese Produkte erarbeitet. In der Zwischenzeit hat sich ein neuer Kenntnisstand ergeben. Vor diesem Hintergrund hat die AG (Arbeitsgruppe) Geogitter des Fachbeirats der BAM am 26.09.2017 getagt. Es sollen die aktuellen Erkenntnisse und Schlussfolgerungen für die Zulassung in Kürze vorgestellt werden. Die entsprechenden Kapitel beruhen dabei auf einem Arbeitspapier von W.W. Müller und dem Autoren, das der Arbeitsgruppe zur Diskussion vorgelegt wurde. Weiterhin soll über Entwicklungen in Zusammenhang mit Kunststoffdichtungsbahnen (KDB) berichtet werden. Die Anforderungen an die Schweißzusätze für das Extrusionsschweißen wurden angepasst. Zudem soll über die aktuelle Diskussion der Schweißbarkeit unterschiedlicher HDPE Materialien informiert werden. Die maßgebliche DVS (Deutscher Verband für Schweißen und verwandte Verfahren) Richtlinie 2225-4 wird derzeit offenbar so ausgelegt, dass Materialien mit völlig unterschiedlichen Schmelze-Massefließrate miteinander verbunden werden könnten. Dies steht allerdings im grundlegenden Widerspruch zum Stand der Technik. Derzeit gibt es intensive Diskussion über die Entlassung von Deponien aus der Nachsorge. Sind Geokunststoffe in den Böschungen einer Deponie verwendet worden, wäre eine Entlassung aus der Nachsorge demnach im Moment nicht möglich. Die Deponie müsste dafür nach der Deponieverordnung (DepV) u. a. „insgesamt dauerhaft standsicher“ sein. Geokunststoffe erfüllten ihre Funktion über einen Zeitrahmen von mindestens hundert Jahren. Die Dauerhaftigkeit wird bei der Diskussion aber offenbar als „Ewigkeit“ verstanden. Dies stehe somit im Widerspruch – so die Argumentation. Auf dieser Veranstaltung wurde im vergangenen Jahr darüber berichtet. Auch auf dieses Thema wird eingegangen. T2 - Abschluss und Rekultivierung von Deponien und Altlasten - Planung und Bau neuer Deponien CY - Karlsruhe, Germany DA - 18.10.2017 KW - Bewehrungen aus Kunststoff KW - Deponien KW - Schweißen PY - 2017 SN - 978-3-939662-21-1 VL - 32 SP - 61 EP - 76 PB - ICP Eigenverlag Bauen und Umwelt CY - Karlsruhe AN - OPUS4-42595 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Stoljarova, A. A1 - Regenspurg, S. T1 - Influence Of Brine Precipitates On Materials Performance In Geothermal Applications N2 - Since geothermal wells are a feasible energy source to replace fossil fuel supply, many technologies have been developed to take advantage of geothermal energy. Nevertheless, service conditions in geothermal facilities are in many cases extreme in terms of corrosion due to the chemical composition of hydrothermal fluids and temperatures. Therefore, materials selection based on preliminary material qualification is essential to guarantee a secure and reliable operation of the facilities. During operation of a geothermal research facility in Groß Schönebeck copper and lead effects have been found downhole. Occurring mechanisms and measures to prevent precipitation or scaling needed to be investigated as well as potential influences of such precipitates on corrosion resistance of metallic materials used for equipment. This contribution deals with the evaluation of the corrosion behavior of carbon steel and corrosion resistant alloys in copper and/or lead containing artificial geothermal water, simulating the conditions in the Northern German Basin. The behavior of these materials in an artificial geothermal water obtained by electrochemical measurements and exposure tests are presented. While carbon steel exhibits precipitation and deposition, higher alloyed material shows different response to such species and a higher resistance in saline geothermal water. Basing on these results the suitability of the investigated corrosion resistant alloy is given for use in such conditions, whereas carbon steel creates difficulties due to its susceptibility to Cu- and Pb-precipitation. T2 - AMPP Annual 2023 Conference CY - Denver, CO, USA DA - 19.03.2023 KW - Geothermal KW - Electrochemistry KW - Copper KW - Lead KW - Corrosion PY - 2023 SP - 1 EP - 15 PB - AMPP CY - Houston TX USA AN - OPUS4-57233 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Stohl, Leonie T1 - MI Funktionsbeton: Funktionalisierte Betonoberflächen zur gezielten Einstellung der Biorezeptivität N2 - Beschreibung des Projektes MI Funktionsbeton 1462, Update nach 15 Monaten. Der Bericht umfasst Hintergrund, Projektzeitplan und aktuellen Stand. KW - Biorezeptivität KW - Beton KW - Biofilm KW - Struktur PY - 2022 SP - 1 EP - 13 AN - OPUS4-58376 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Erdmann, Eileen A. T1 - Genetic tools for targeted genome editing and random mutagenesis of the rock-inhabiting black fungus Knufia petricola N2 - Rock-inhabiting black fungi are ubiquitously found on sun-exposed natural and human-made surfaces. These stresstolerant biofilm-formers are known to force the deterioration of the colonized surfaces. Black fungi belong to different classes of Ascomycota (Arthoniomycetes, Eurotiomycetes, and Dothideomycetes) but evolved the same morpho-physiological adaptations such as strong melanized multilayered cell walls and slow yeast-like or meristematic growth to resist extreme environmental conditions. The rock-inhabitant Knufia petricola was chosen as representative of the polyphyletic group of black fungi for studying mineral weathering, biofilm formation, and interaction with phototrophic microbes. For understanding the molecular basis of these traits, the genetic information and its regulation must be explored. Thus, the genome was sequenced, first -omics datasets obtained and protocols for the transformation of protoplasts and CRISPR/Cas9-based genome editing were implemented to enable genetic studies. In scope of this work, the transformation protocol was optimized to improve the regeneration of K. petricola protoplasts. The successful implementation of multiplexed CRISPR/Cas9 and three additional selection marker systems (geneticin/nptII, glufosinate/bar, chlorimuron ethyl/sur) extended the existing strategies for targeted genome editing. While in the first promoter studies only constitutive promoters (PoliC, PgpdA) were identified as appropriate for expression of fluorescent reporter genes in K. petricola, the functionality of an inducible promoter (synthetic TET-on promoter system) could later be demonstrated. The identification and validation of defined genomic insertion sites enabled the neutral or color-based selection (igr1-5 or pks1, phs1, ade2) as well as the detection of correctly integrated expression constructs. Using the color-based transformant screening (black – pink/white/rose) accelerated the selection of transformants, especially for localization and protein-protein interaction studies (e.g., by studying bimolecular fluorescence complementation). Additionally, the fusion of two or three genes via the viral P2A motif was shown to allow the expression of multiple genes from a single expression cassette/integration site. Finally, the established tools enabled the implementation of a forward genetics tool (customized Ac/Ds transposon system) for regulatable in-vivo mutagenesis of K. petricola. The isolation and characterization of revertants/Ds reinsertion mutants demonstrated the functionality of the system which marks an important milestone for assigning functions to yet unknown species- and/or trait-specific genes. In sum, the genetic engineering toolbox is now fully equipped which paves the way for exploring the biology of K. petricola and other black fungi. KW - Microcolonial fungi KW - Genetic engineering KW - CRISPR/Cas9-mediated genome editing KW - DHN melanin KW - Transposon mutagenesis PY - 2024 SP - 1 EP - 231 CY - Berlin AN - OPUS4-62364 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Morys, Michael A1 - Illerhaus, Bernhard A1 - Sturm, Heinz A1 - Schartel, Bernhard T1 - Revealing the inner secrets of intumescent chars by advanced small scale tests combined with µ-CT N2 - Testing of intumescent coatings for Steel is usually done in intermediate scale or even full scale experiments and is hence quite expensive. We developed two complementary small scale tests, simulating fully developed Tire. First is a strongly modified electrical muffle furnace, which is now able to follow the Standard temperature-time curve (according EN 1363-1) for 90 min in a very accurate manner. Düring the experiment backside temperatures are recorded and the growth of the char is observed with a custom made high temperature endoscope. Second is a testing apparatus based on a propane-oxygen-bumer for direct severe flame impingement of coated samples, reaching temperatures far above 1500 °C. Our small scale samples are coated Steel plates of a size of 75 x 75 x 2 mm3. The structure-propertyrelation between additives, thermal properties and morphology of the char were examined using a well determined series of samples consisting of basic composition mixed with different additives. With the burner-testing-apparatus we studied the behavior of a high performance coating, which shows a transformation of the carbonaceous char into a ceramic foam at temperatures as high as 1600 °C. Nondestructive micro-computed tomography was used to characterize the morphology of the char. According to the structure of the foams we used different analytic methods like cell-detection or wallthickness-analysis. Additional scanning electron and optical microscopy were performed. The combination of the CT-data with the measured backside temperatures of the different samples provides us a deep understanding of the interaction between isolating properties and morphology of intumescent chars. T2 - Fire and materials 2015 - 14th International conference and exhibition CY - San Francisco, CA, USA DA - 02.02.2015 PY - 2015 SP - 478 EP - 483 PB - Interscience Communications AN - OPUS4-32710 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Adam, Christian A1 - Schneider, Joachim A1 - Schraut, Katharina T1 - Strategien für die Nutzung von Schlacken zukünftiger wasserstoffbasierter Stahlproduktionsrouten – Herstellung von Stahlwerksschlacke basierten Ausgangsstoffen für die Zementindustrie N2 - Die Europäische Kommission präsentierte am 11. Dezember 2019 den European Green Deal, ein Konzept mit dem Ziel, bis zum Jahr 2050 als erster Kontinent Klimaneutralität zu erreichen. Mit Inkrafttreten der Verordnung (EU) 2021/1119 des Europäischen Parlaments und des Europäischen Rates am 29. Juli 2021 zur Schaffung des Rahmens für die Verwirklichung der Klimaneutralität („Europäisches Klimagesetz“), ist dieses, sowie das Ziel der Reduzierung der Nettotreibhausgasemissionen um mindestens 55 % bis 2030 in der Gesetzgebung der Europäischen Union verankert. Die Stahlindustrie in der Europäischen Union mit ca. 57 Mio. t Nettotreibhausgasemissionen im Jahr 2020, die annähernd 2 % der Emissionen der Europäischen Union ausmachen (Inklusive Energie: 127 Mio. t; 4 %), bekennt sich zur erheblichen Reduzierung der CO2-Emissionen bis zum Jahr 2030 und zum Erreichen der Klimaneutralität bis zum Jahr 2050. Als Schlüsselwege zur Verwirklichung dieser Zielstellung hat sie zum einen Smart Carbon Usage (SCU) und zum anderen Carbon Direct Avoidance (CDA) in einer Roadmap formuliert. SCU umfasst CO2-reduzierende Maßnahmen in bestehenden Eisen- und Stahlproduktionsprozessen, Carbon Capture and Storage- (CCS) sowie Carbon Capture and Usage-Technologien (CCU). Wohingegen bei CDA CO2-Emissionen durch erneuerbare elektrische Energie sowie wasserstoffbasierte Reduktion des Eisenerzes gar nicht erst entstehen sollen. Der CDA-Weg, der voraussichtlich beschritten werden muss, um eine klimaneutrale Stahlproduktion zu erreichen [38], geht mit einer kostenintensiven Transformation der Stahlproduktion einher, die bereits von vielen Unternehmen der Stahlindustrie eingeleitet wurde und von der im Wesentlichen die beiden in Europa vorherrschenden Stahlproduktionsrouten Hochofen-Konverter-Route und Elektrolichtbogenofen-Route betroffen sind. Die CO2-Emissionen der Hochofen-Konverter-Route, von denen der überwiegende Anteil auf den Hochofen fällt, liegen laut einer für das Jahr 2015 erstellten Studie bei 1921 kg CO2/t Rohstahl inklusive der CO2-Last der Pellets als Einsatzmaterial sowie der Emissionen der nachgelagerten Stranggießanlagen und Walzwerke. Im Hochofen wird das Eisenerz durch Kohlenstoff (C) bzw. Kohlenstoffmonoxid (CO) – welche größtenteils aus dem Koks, der dem Hochofen zusammen mit dem Möller über die Gicht zugeführten wird, stammen – unter Entstehung von Roheisen und Kohlenstoffdioxid (CO2) reduziert. Das neben dem CO2 im Prozessgas enthaltene CO wird zum Beispiel zur Energiegewinnung in peripheren Prozessen ebenfalls unter Bildung von CO2 verbrannt. Zusätzlich zur Reduktion hat der Koks unter anderem physikalische Aufgaben, wie die Errichtung eines Stützgerüstes und die Gewährleistung der Permeabilität im Hochofenprozess. Somit ist eine vollkommene Substitution des Kokses zur Vermeidung der CO2-Emissionen im Hochofen nicht denkbar. Viele Strategien der Stahlunternehmen zum Erreichen der Klimaziele verfolgen daher den Wechsel von der Rohstahlproduktion aus der Hochofen-Konverter-Route hin zur Rohstahlproduktion im Elektrolichtbogenofen (EAF – Electric Arc Furnace) mit dem Einsatz von direkt reduziertem Eisen (Eisenschwamm, DRI – Direct Reduced Iron) aus vorgelagerten Direktreduktionsanlagen, die mit Wasserstoff (H2) als Reduktionsmittel betrieben werden können. Dabei ist die Elektrostahlerzeugung kein neuer Prozess und nimmt in der europäischen Union bereits jetzt einen Anteil von ca. 44 % der Rohstahlproduktion ein, jedoch überwiegend mit Schrott als Einsatzmaterial. Bei der Elektrostahlerzeugung mit Schrotteinsatz fallen laut der oben genannten Studie von Lüngen für das Jahr 20152 410 kg CO2-Emissionen pro Tonne Rohstahl an, von denen der Großteil auf die CO2-Last der fremd bezogenen elektrischen Energie zurückzuführen ist und daher nicht im Produktionsprozess selbst entsteht. Auch die Direktreduktion wird schon seit 1972 in der weltweit zweiten und bis heute in Westeuropa einzigen Direktreduktionsanlage in Hamburg betrieben. Während hier noch mit einem Reduktionsgas gearbeitet wird, das hauptsächlich aus einem aus Erdgas gewonnenen Wasserstoff-Kohlenstoffmonoxid-Gemisch besteht, liegt eine aktuelle Kernherausforderung in der Bereitstellung des in der Größenordnung der von der Transformation betroffenen Rohstahlproduktionskapazitäten notwendigen, mit erneuerbarer elektrischer Energie hergestellten Wasserstoffs. Wird zusätzlich der Strom für das Einschmelzen im Elektrolichtbogenofen aus erneuerbaren Quellen gewonnen und werden schließlich als Brennstoff verwendete Kohle und als Brennstoff verwendetes Erdgas durch CO2-neutrale Bio-Brennstoffe ersetzt, sind sowohl für den Einsatz von mit Wasserstoff reduziertem und auf Pellets ohne CO2-Last basiertem Eisenschwamm als auch für den Einsatz von Schrott CO2-Emissionen von jeweils nur 60 kg CO2/t Rohstahl erreichbar, was eine Reduktion der Emissionen, ausgehend von der Konverter-Hochofen-Route um 97 % und ausgehend von der Schrott-Elektrolichtbogenofen-Route um 85 % bedeuten würde. Der Betrieb von Elektrolichtbogenöfen macht die an den Standorten vorhandenen Konverter sowie die Infrastruktur für Behandlung und Transport des Roheisens überflüssig. Die fortwährende Nutzung dieser bestehenden Anlagenstruktur dient daher unter anderem als Motivation für die Entwicklung einer zweiten Transformationsstrategie, die einen sogenannten Einschmelzer (SAF – Submerged Arc Furnace) als der Direktreduktionsanlage nachgelagerten Prozess vorsieht, in dem wiederum Roheisen erschmolzen wird, das anschließend im Konverter zu Rohstahl veredelt wird. Die Transformation der Stahlindustrie beeinflusst einen weiteren CO2-intensiven Industriesektor, nämlich die Zementindustrie die verantwortlich ist für rund 4 % der CO2-Emissionen in der EU. Etwa zwei Drittel dieser Emissionen entfallen als Prozessemissionen auf die Entsäuerung des Rohstoffs Kalkstein (CaCO3), also auf die Abspaltung von CO2 unter Entstehung des für die Herstellung von Zementklinker notwendigen Branntkalks (CaO) als Zwischenstufe bei der Bildung der hydraulischen Phasen Tri- und Dicalciumsilikat. Als eines der fünf Themenfelder (5C-Ansatz: Clinker, Cement, Concrete, Construction, Carbonation), welche die europäische Zementindustrie entlang ihrer Wertschöpfungskette zum Erreichen der gesetzlichen Vorgaben der europäischen Union erarbeitet hat, umfasst das Feld "Cement" zum größten Teil die Reduzierung des Klinker-Zement-Faktors. Im Jahr 2017 betrug er 77 %, das heißt, dass 23 % des Klinkers durch alternative Materialien ersetzt wurden. Bis zum Jahr 2030 wird ein Faktor von 74 % und bis zum Jahr 2050 von 65 % angestrebt. Den größten Anteil an den Klinkersubstituten hat mit 33 % der Hüttensand aus der Stahlindustrie. Bei der Roheisenproduktion im Hochofen entsteht als Nebenprodukt Hochofenschlacke, die unter Zugabe von Schlackebildnern die Gangart des Möllers und mineralische Koksbestandteile abbindet, sowie weitere unerwünschte Begleitelemente wie Schwefel und Alkalien aufnimmt. Allein in Deutschland wurden im Jahr 2021 6,90 Mio. t – das entspricht 90 % der gesamten produzierten Hochofenschlacke – zu glasig erstarrtem Hüttensand granuliert. Dieser Hüttensand besitzt latent hydraulische Eigenschaften und wird daher seit mehr als 140 Jahren als Zementbestandteil eingesetzt, wodurch in Deutschland jährlich rund 4,5 Mio. t CO2-Emissionen eingespart werden. Alle Transformationsstrategien der Stahlindustrie beinhalten die notwendige Außerbetriebnahme der CO2-intensiven Hochöfen. Dies hat unter anderem zur Folge, dass die Hochofenschlacke als Nebenprodukt der Rohstahlerzeugung im Hochofen nicht mehr zur Verfügung stehen wird, wodurch die weitere Reduzierung des Klinker-Zement-Faktors erhebliche Zusatzmengen alternativer Materialien benötigen wird. Derzeit ist noch unklar, ob z.B. calcinierte Tone im benötigten Umfang erzeugt werden können. Der Fachbereich Thermochemische Reststoffbehandlung und Wertstoffrückgewinnung der Bundesanstalt für Materialforschung und -prüfung (BAM) und das Institut für Baustoffforschung FEhS forschen zusammen mit Industriepartnern und weiteren Forschungseinrichtungen im Rahmen zweier Projekte in den Kooperationssphären der Stahl- und Zementindustrie, die zur Bewältigung dieser Herausforderungen beitragen. Im Projekt SlagCEM wird die Produktion eines hydraulischen Zementbestandteils durch Reduktion von Konverter- bzw. Linz-Donawitz-Schlacke (LDS) untersucht. Die mit den zusätzlich aufgenommen Lichtbogenofenkapazitäten steigenden Mengen an Elektrolichtbogenofenschlacke (EOS, engl. electric arc furnace slag, EAFS) werden im Projekt DRI-EOS behandelt, welches die Produktion eines latent hydraulischen Hüttensandsubstituts zum Ziel hat. T2 - Berliner Konferenz Mineralische Nebenprodukte und Abfälle CY - Berlin, Germany DA - 12.06.2023 KW - Stahlwerksschlacke KW - Zementersatz PY - 2023 SN - 978-3-944310-72-5 VL - 10 SP - 222 EP - 233 PB - TK-Verlag CY - Neuruppin AN - OPUS4-57684 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Naik, Aakash A. A1 - Dhamrait, Nidal A1 - Ueltzen, Katharina A1 - Ertural, Christina A1 - Benner, Philipp A1 - Rignanese, Gian-Marco A1 - George, Janine T1 - A critical assessment of bonding descriptors for predicting materials properties N2 - Most machine learning models for materials science rely on descriptors based on materials compositions and structures, even though the chemical bond has been proven to be a valuable concept for predicting materials properties. Over the years, various theoretical frameworks have been developed to characterize bonding in solid-state materials. However, integrating bonding information from these frameworks into machine learning pipelines at scale has been limited by the lack of a systematically generated and validated database. Recent advances in high-throughput bonding analysis workflows have addressed this issue, and our previously computed Quantum-Chemical Bonding Database for Solid-State Materials was extended to include approximately 13,000 materials. This database is then used to derive a new set of quantum-chemical bonding descriptors. A systematic assessment is performed using statistical significance tests to evaluate how the inclusion of these descriptors influences the performance of machine-learning models that otherwise rely solely on structure- and composition-derived features. Models are built to predict elastic, vibrational, and thermodynamic properties typically associated with chemical bonding in materials. The results demonstrate that incorporating quantum-chemical bonding descriptors not only improves predictive performance but also helps identify intuitive expressions for properties such as the projected force constant and lattice thermal conductivity via symbolic regression. KW - Bonding Analysis KW - Machine Learning KW - Symbolic Regression KW - Chemical Understanding KW - Phonons KW - Thermal Conductivity PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-655150 DO - https://doi.org/10.48550/arXiv.2602.12109 SP - 1 EP - 28 PB - Cornell University CY - Ithaca, NY AN - OPUS4-65515 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holm, O. A1 - Leube, Peter A1 - Vogel, Christian A1 - Kennedy, E. A1 - Stockenhuber, M. A1 - Lucas, J. A1 - Truong, T. A1 - Rappé, A. A1 - Lu, W. A1 - Blotevogel, J. T1 - Thermische Zerstörung von PFAS in der Sondermüllverbrennung: Einfluss von Temperatur und PFAS-Konzentration N2 - Aufgrund ihrer einzigartigen molekularen Beschaffenheit werden per- und polyfluorierte Alkylsubstanzen (PFAS) in vielen unterschiedlichen Produkten und Anwendungsgebieten eingesetzt. Da sie generell eine hohe Persistenz aufweisen und je nach individueller Struktur unterschiedlich mobil sind, sind sie mittlerweile in allen Umweltkompartimenten und ubiquitär nachzuweisen. Ihre potenzielle (ökologische) Toxizität birgt dabei erhebliche Umweltrisiken, weshalb PFAS in den letzten Jahren mehr und mehr in den Fokus von Umweltverbänden und -behörden gelangten. Gleichzeitig beschäftigen sich Forschungseinrichtungen mit der möglichst weitreichenden Entfernung aus der Umwelt sowie mit deren (anschließender) Zerstörung. Im Projekt ER24-4073 „Untersuchung des thermischen Abbaus von PFAS in einer kommerziellen Großanlage zur Verbrennung gefährlicher Abfälle“, welches vom U.S. Department of Defense (DoD ) über das Strategic Environmental Research and Development Program (SERDP) gefördert wird, untersuchen deutsche, australische und amerikanische Partner die Behandlung von PFAS-haltigen Abfallströmen in einer großtechnischen Verbrennungsanlage, um die Einsatzbereitschaft, Machbarkeit und Sicherheit dieser Zerstörungsmethode zu demonstrieren. T2 - Berliner Konferenz Abfallwirtschaft und Energie CY - Berlin, Germany DA - 28.01.2026 KW - Per- and polyfluoroalkyl substances (PFAS) KW - Verbrennung KW - Kontaminierter Boden PY - 2026 SN - 978-3-911006-65-1 SP - 66 EP - 77 PB - TK Verlag AN - OPUS4-65513 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalbe, Ute T1 - Identifikation und Einordnung von historischen Lehmbauteilen für die Wiederverwendung hinsichtlich Anreicherung von Schadstoffen und bauschädlichen Salzen N2 - Lehmbaustoffe, einschließlich Lehm aus dem historischen Baubestand, bieten ein hohes Potenzial für ihre Wiederverwendbarkeit und die Schonung natürlicher Ressourcen. Zur Bewertung des Wiederverwendungspotenzials gibt es nur wenige Studien hinsichtlich der Schadstoffbelastung und der Anreicherung von Salzen in Gebäuden aus dem historischen Bestand. Tonminerale, die in Lehmbaustoffen als Bindemittel fungieren, können Schadstoffe binden. Die Region Mitteldeutschland ist geprägt durch jahrzehntelange Einwirkung erheblicher Schadstoffemissionen aus der Chemie- und Braunkohleindustrie. Der Eintrag von Schadstoffen in Lehmbaustoffe ist außerdem aus geogenen Hintergrundbelastungen denkbar, z. B. in Auenböden beeinflusst durch Einträge aus dem Erzbergbau. Salzbildende Anionen wie Chloride oder Nitrate können aufgrund ihrer hohen Löslichkeit mittels kapillarer Kräfte durch die Porenstruktur transportiert werden. In Lehmwänden können sie vor allem in oberflächennahen Lagen, in denen höhere Verdunstungsraten vorherrschen, durch Bindung mit in Lösung vorliegenden oder baustoffeigenen Kationen auskristallisieren und bauschädliche Salze ausbilden. Auch durch spezifische Nutzungen akkumulierte Schadstoffe, z. B. durch die Einwirkung von Tabakrauch, könnten theoretisch einer Wiederverwendung von Lehm entgegenstehen. In Anbetracht der Herausforderungen hinsichtlich der klimatischen und gesellschaftlichen Veränderungen, sind wissenschaftliche Erkenntnisse im Lehmbau erforderlich, die eine Integration in eine nachhaltige Kreislaufwirtschaft ermöglichen. Bei bisherigen Gesetzgebungsverfahren zu rezyklierten Baustoffen wurden Lehmbaustoffe noch nicht berücksichtigt. Ziel einer Vorstudie im Rahmen der WIR!-Initiative GOLEHM ist die Überprüfung der Wiederverwendbarkeit Wiederverwendbarkeit von Lehmbaustoffen aus historischen Bauten an Stichproben hinsichtlich der Umwelt- und Nutzerverträglichkeit. Für den Raum Mitteldeutschland können damit Anhaltspunkte darüber gegeben werden, welche Schadstoffe und bauschädlichen Salze in welchem Maße in Lehmbaustoffen aus dem Gebäudebestand erwartet werden können. Daraus können Hinweise zum Umgang mit Lehmbaustoffen aus historischen Gebäuden abgeleitet werden. Darüber hinaus wurden exemplarisch an zwei Gebäuden mikrobiologische Untersuchungen zur Ermittlung einer möglichen Belastung mit Schimmelpilzen vorgenommen. T2 - Lehm 2024 Fachtagung CY - Weimar, Germany DA - 27.09.2024 KW - Lehm KW - Schadstoffe KW - Wiederverwendung KW - Historischer Baubestand PY - 2024 AN - OPUS4-61881 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Fritzsche, Sven A1 - Weimann, Christiane A1 - Pauw, Brian Richard A1 - Sturm, Heinz T1 - 2PP-TestArtifact N2 - This repository contains a test artifact (TA), also called test structure, designed for two-photon polymerization (also known as Direct Laser Writing (DLW) or Two/Multi-photon lithography (2PA/MPA)). Test artifacts can be used to compare structures, to check options used by the slicer, check the state of the 2PP machine itself or to get a construction guidelines for a certain combination of power, velocity and settings. The associated paper can be found here: https://dx.doi.org/10.1088/1361-6501/acc47a General ideas behind the test artifact: 1. optimized for 2PP-DLW 2. should be fast and easy to analyse with optical microscopy or 3. scanning electron microscopy without tilt. 3. short time to fabricate 4. include a reasonable amount of different features 5. bulk and small structures on the substrate KW - Reference structure KW - Calibration structure KW - Test structure KW - Laser writing KW - Two-photon polymerization KW - 3D printing KW - Additive manufacturing KW - Microprinting KW - Multi-photon light structuring PY - 2023 DO - https://doi.org/10.6084/m9.figshare.22285204.v2 PB - Digital Science CY - Cambridge, MA, USA AN - OPUS4-57165 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Keserovic, Amela A1 - Sobetzki, Joana A1 - Sarmiento Klapper, Helmuth A1 - Dimper, Matthias T1 - Laboratory evaluation of metallic materials for geothermal applications N2 - In the last years, geothermal power has become a reliable and significant energy source. Because service conditions in geothermal facilities from deeply located aquifers are usually critical in terms of corrosion, materials selection is a very important issue. Preliminary evaluation of the material's suitability represents therefore a valuable strategy to ensure a secure and reliable operation of the facilities. In geothermal applications, the use of high-alloyed materials such as superaustenitic stainless steels, duplex stainless steels, and nickel-based alloys has been considered as a good alternative because of their remarkable corrosion resistance and appropriate mechanical properties. Nevertheless, the corrosion behavior of those metallic materials in geothermal fluids at service conditions has not been determined in many cases. In this work, laboratory tests including electrochemical investigations and exposure tests at 100 degrees C and 150 degrees C (1,500 kPa) showed the limits of suitability concerning localized corrosion of three different, corrosion-resistant alloys in the highly saline fluid of the North German Basin. T2 - EPRI International Conference on Corrosion in Power Plants CY - San Diego, CA, USA DA - 12.10.2015 KW - Geothermal KW - Corrosion KW - Crevice corrosion KW - Suitability PY - 2015 DO - https://doi.org/10.5006/1.3676631 SP - paper 6 AN - OPUS4-34754 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Landsberger, Petra A1 - Boenke, Viola A1 - Gorbushina, Anna A1 - Rodenacker, K. A1 - Pierce, B.F. A1 - Kratz, K. A1 - Lendlein, A. T1 - Bacterial attachment on poly[acrylonitrile-co-(2-methyl-2-propene-1-sulfonic acid)] surfaces N2 - The influence of material properties on bacterial attachment to surfaces needs to be understood when applying polymer-based biomaterials. Positively charged materials can kill adhered bacteria when the charge density is sufficiently high but such materials initially increase the adherence of some bacteria such as Escherichia coli. On the other hand, negatively charged materials have been shown to inhibit initial bacterial adhesion, but this effect has only been demonstrated in relatively few biomaterial classes and needs to be evaluated using additional systems. Gradients in surface charge can impact bacterial adhesion and this was tested in our experimental setup. Moreover, the evaluation of bacterial adhesion to biomaterials is required to assess their potential for biological applications. Here, we studied the bacterial adhesion of E. coli and Bacillus subtilis on the surfaces of acrylonitrile-based copolymer samples with different amounts of 2-methyl-2-propene-1-sulfonic acid sodium salt (NaMAS) comonomer. The content related to NaMAS based repeating units nNaMAS varied in the range from 0.9 to 1.5 mol%. We found a reduced colonized area of E. coli for NaMAS containing copolymers in comparison to pure PAN materials, whereby the bacterial colonization was similar for copolymers with different nNaMAS amounts. A different adhesion behavior was obtained for the second tested organism B. subtilis, where the implementation of negative charges into PAN did not change the overall adhesion pattern. Furthermore, it was observed that B. subtilis adhesion was significantly increased on copolymer samples that exhibited a more irregular surface roughness. T2 - MRS Spring meeting 2013 CY - San Francisco, CA, USA DA - 01.04.2013 KW - Biomaterial KW - Biological KW - Polymer PY - 2013 DO - https://doi.org/10.1557/opl.2013.832 VL - 1569 IS - MRSS13-1569-NN15-13.R1 SP - 1 EP - 6 AN - OPUS4-30161 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Sarmiento Klapper, Helmuth A1 - Feigl, Michael A1 - Hilker, Nico T1 - Corrosion resistance of high-alloyed and alternative materials in an artificial geothermal water N2 - Many technologies have been developed to take advantage of geothermal energy, which became a feasible energy source to replace fossil fuel supply. Nevertheless, service conditions in geothermal facilities are due to the chemical composition of hydrothermal fluids and involved high temperatures, in many cases, extreme in terms of corrosion. Therefore, materials selection based on preliminary material qualification is essential to guarantee a secure and reliable operation of the facilities. This contribution deals with the evaluation of the corrosion behavior of two high-alloyed metallic materials and α-Al2O3 in an artificial geothermal fluid simulating the conditions in the Northern German Basin, a location with high geothermal potential. The suitability of the super austenitic stainless steel UNS N08031 and the nickel base alloy UNS N06059 in this geothermal fluid obtained by electrochemical measurements and exposure tests is addressed. As an alternative to the suitable but costly UNS N06059 that showed excellent corrosion resistance against pitting corrosion, ceramic made of α-Al2O3 represents an interesting possibility for selected components to be used in the construction of geothermal facilities T2 - Corrosion 2014 CY - San Antonio, TX, USA DA - 09.03.2014 KW - Localized corrosion KW - Stainless steel KW - Ni-based alloy KW - Ceramic KW - Geothermal energy PY - 2014 SP - Paper 3826, 1 EP - 8 AN - OPUS4-30632 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Boduch, Alicja A1 - Sobetzki, Joana T1 - Corrosion resistance of high-alloyed materials in flowing artificial geothermal water N2 - Since geothermal wells are a feasible energy source to replace fossil fuel supply, many technologies have been developed to take advantage of geothermal energy. Nevertheless, service conditions in geothermal facilities are due to the chemical composition of hydrothermal waters and temperatures, in many cases, extreme in terms of corrosion. Therefore, materials selection based on preliminary material qualification is essential to guarantee a secure and reliable operation of the facilities. This contribution deals with the evaluation of the corrosion behavior of different steels in flowing low saline, slightly alkaline, artificial geothermal water simulating the conditions in the Molasse-Basin, a location with geothermal potential in Germany. Test results for steels UNS S31603 and UNS S31803 exposed to this geothermal water obtained by electrochemical measurements and exposure tests are presented. Results obtained in static and flowing water condition show good performance of both alloys with a possible onset of localized corrosion at UNS S31603 in static conditions. T2 - Corrosion 2014 CY - San Antonio, TX, USA DA - 09.03.2014 KW - Localized corrosion KW - Steel KW - Duplex steel KW - Flow KW - Sulfide KW - Geothermal energy PY - 2014 SP - Paper 3825, 1 EP - 8 AN - OPUS4-30631 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalbe, Ute A1 - Schröder, Simon Alexander A1 - Richter, Matthias A1 - Horn, Wolfgang A1 - Stephan, Ina A1 - Hohmann, Gloria A1 - Ziegert, Christof T1 - Identifikation und Einordnung von historischen Lehmbauteilen für die Wiederverwendung hinsichtlich Anreicherung von Schadstoffen und bauschädlichen Salzen T1 - Identification and classification of historical earth construction elements for recycling in respect of accumulation of pollutants and structurally damaging salts N2 - Lehmbaustoffe, einschließlich Lehm aus dem historischen Baubestand, bieten ein hohes Potenzial für ihre Wiederverwendbarkeit und die Schonung natürlicher Ressourcen. Zur Bewertung des Wiederverwendungspotenzials gibt es nur wenige Studien hinsichtlich der Schadstoffbelastung und der Anreicherung von Salzen in Gebäuden aus dem historischen Bestand. Tonminerale, die in Lehmbaustoffen als Bindemittel fungieren, können Schadstoffe binden. Die Region Mitteldeutschland ist geprägt durch jahrzehntelange Einwirkung erheblicher Schadstoffemissionen aus der Chemie- und Braunkohleindustrie. Der Eintrag von Schadstoffen in Lehmbaustoffe ist außerdem aus geogenen Hintergrundbelastungen denkbar, z. B. in Auenböden beeinflusst durch Einträge aus dem Erzbergbau. Salzbildende Anionen wie Chloride oder Nitrate können aufgrund ihrer hohen Löslichkeit mittels kapillarer Kräfte durch die Porenstruktur transportiert werden. In Lehmwänden können sie vor allem in oberflächennahen Lagen, in denen höhere Verdunstungsraten vorherrschen, durch Bindung mit in Lösung vorliegenden oder baustoffeigenen Kationen auskristallisieren und bauschädliche Salze ausbilden. Auch durch spezifische Nutzungen akkumulierte Schadstoffe, z. B. durch die Einwirkung von Tabakrauch, könnten theoretisch einer Wiederverwendung von Lehm entgegenstehen. In Anbetracht der Herausforderungen hinsichtlich der klimatischen und gesellschaftlichen Veränderungen, sind wissenschaftliche Erkenntnisse im Lehmbau erforderlich, die eine Integration in eine nachhaltige Kreislaufwirtschaft ermöglichen. Bei bisherigen Gesetzgebungsverfahren zu rezyklierten Baustoffen wurden Lehmbaustoffe noch nicht berücksichtigt. Ziel einer Vorstudie im Rahmen der WIR!-Initiative GOLEHM ist die Überprüfung der Wiederverwendbarkeit Wiederverwendbarkeit von Lehmbaustoffen aus historischen Bauten an Stichproben hinsichtlich der Umwelt- und Nutzerverträglichkeit. Für den Raum Mitteldeutschland können damit Anhaltspunkte darüber gegeben werden, welche Schadstoffe und bauschädlichen Salze in welchem Maße in Lehmbaustoffen aus dem Gebäudebestand erwartet werden können. Daraus können Hinweise zum Umgang mit Lehmbaustoffen aus historischen Gebäuden abgeleitet werden. Darüber hinaus wurden exemplarisch an zwei Gebäuden mikrobiologische Untersuchungen zur Ermittlung einer möglichen Belastung mit Schimmelpilzen vorgenommen. N2 - Earth construction materials, including earth from historical building stock, offer high potential in terms of their recyclability and sparing use of natural resources. Yet, only a few studies have been conducted on the levels of pollutants and the accumulation of salts in buildings from the historical building stock to enable an assessment of the potential for recycling. The aim of a preliminary study as part of the GOLEHM Initiative from WIR! is to use spot checks to review the recyclability of earth construction materials from historical buildings in terms of environmental impact and tolerance by users. This could provide indicators for the Central Germany region on which pollutants and structurally damaging salts can be expected in earth construction materials from the building stock and to what extent, allowing conclusions to be drawn on how to manage earth construction materials from historical buildings. Additionally, microbiological inspections of two sample buildings were performed to assess a potential contamination with mould. T2 - Lehm 2024 Fachtagung CY - Weimar, Germany DA - 27.09.2024 KW - Lehm KW - Wiederverwendung KW - Kreislaufwirtschaft KW - Schadstoffe KW - Bauschädliche Salze PY - 2024 SP - 1 EP - 8 CY - Weimar AN - OPUS4-61883 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wöhlecke, Andreas ED - Al-Akel, S. T1 - Aktuelle Diskussionen aus dem Fachbeirat der BAM N2 - Vor nun 30 Jahren im Jahre 1989 wurde die erste Zulassung für eine Kunststoffdichtungsbahn von der BAM auf der Grundlage des „Niedersächsischen Dichtungserlasses“ erteilt. Vor ungefähr 10 Jahren wurde die BAM mit dem Erscheinen der Deponieverordnung (DepV) mit der Zulassung von Geokunststoffen, Polymeren und Dichtungskontrollsystemen beauftragt. Wir möchten dies zum Anlass nehmen, an dieser Stelle den viele ehrenamtlichen Experten des Fachbeirats und seiner Arbeitsgruppen für ihren Einsatz und die Unterstützung zu danken. Darüber hinaus soll über aktuelle Arbeitsthemen und Entwicklungen im Fachbeirat berichtet werden. So soll in einer Sondersitzung des Fachbeirats über die Entlassung aus der Nachsorgephase beim Einsatz von Geokunststoffprodukten in Böschungen diskutiert werden. Es ist geplant, in einer Unterarbeitsgruppe eine Sitzung über die Fremdüber¬wachung in der Produktion abzuhalten. Darüber hinaus werden Änderungen in den Zulassungsrichtlinien für Kunststoff Dichtungsbahnen und Kunststoff Dränelemente kurz vorgestellt. In der Zwischenzeit wurde auch die abschließende Zulassungsrichtlinie für Geogitter verabschiedet. Neue Fragestellungen sind hier entstanden. Unter welchen Voraussetzungen können Geogitter in Zwischenabdichtungen eingesetzt werden. Bisher können diese Produkte formal nur in Oberflächenabdichtungen eingesetzt werden. Auch auf diese beiden Themen soll im Folgenden in Kürze eingegangen werden. T2 - 15. Leipziger Deponiefachtagung CY - Leipzig, Germany DA - 05.03.2019 KW - Deponie KW - Abdichtungssysteme KW - Geogitter PY - 2019 SN - 978-3-943443-48-6 VL - 15 SP - 29 EP - 40 PB - HTWK Leipzig CY - Leipzig AN - OPUS4-47490 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Crasselt, Claudia A1 - Schmidt, Wolfram A1 - Sturm, Heinz T1 - Influence of rheology modifying admixtures on early hydration of cementitious suspensions N2 - The presence of polycarboxylate ether (PCE) based superplasticizers (SPs) has enormous influence on the early hydration of cement. C3A as the most reactive phase of Portland cement plays a significant role in early hydration reactions and affects the rheological performance. Therefore, this paper presents experimental results about the influence of delayed addition of PCEs on the Hydration of cement and C3A-gypsum pastes investigated by isothermal heat flow calorimetry. Complementary in-situ XRD was carried out on C3A pastes to analyze hydration and phase changes related to the addition of PCE. Cement pastes with a delayed addition of PCE showed less Retardation compared to simultaneous addition. The alteration caused by PCE is much more pronounced for C3A-gypsum mixes. With a delayed addition of SP, the hydration of C3A is less retarded or even accelerated. It is obvious that there is less retardation the later the addition of SP. Furthermore, the PCE alter the hydration of C3A when added delayed and exhibit changes in kinetics and hydration rates. XRD results showed that more C3A is dissolved in the presence of PCE. Also, the gypsum depletion occurs earlier in the presence of PCE and even faster with delayed addition. Without PCE AFm starts to form just after the gypsum depletion. However, in the presence of PCE AFm already starts to form at the beginning of the hydration. Due to the faster gypsum depletion in the presence of PCE, also the transformation from ettringite into AFm begins earlier, but takes longer as without SP. T2 - 15th International Congress on the Chemistry of Cement CY - Prague, Czech Republic DA - 16.09.2019 KW - Cement KW - C3A KW - Early hydration KW - Polycarboxylate ether (PCE) KW - Delayed addition PY - 2019 SP - 1 EP - 8 AN - OPUS4-49104 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wöhlecke, Andreas T1 - Aktuelle Themen aus der Arbeit des Fachbeirats der BAM N2 - Vor nun 30 Jahren, im Jahre 1989, wurde die erste Zulassung für eine Kunststoffdichtungsbahn (KDB) von der BAM auf der Grundlage des Niedersächsischen Dichtungserlasses“ erteilt. Vor ungefähr 10 Jahren wurde die BAM mit dem Erscheinen der Deponieverordnung (DepV) mit der Zulassung von Geokunststoffen, Polymeren und Dichtungskontrollsystemen beauftragt. Wir möchten dies zum Anlass nehmen, an dieser Stelle den viele ehrenamtlichen Experten des Fachbeirats und seiner Arbeitsgruppen für ihren Einsatz und die Unterstützung zu danken. Darüber hinaus soll über aktuelle Arbeitsthemen und Entwicklungen im Fachbeirat berichtet werden. So wurde in einer Sondersitzung des Fachbeirats über die Entlassung aus der Nachsorgephase beim Einsatz von Geokunststoffprodukten in Böschungen diskutiert. Die Unterarbeitsgruppe Fremdüberwachung in der Produktion hat getagt. Darüber hinaus werden Änderungen in den Zulassungsrichtlinien für Kunststoffdichtungsbahnen, Kunststoff-Dränelemente und Geogitter kurz vorgestellt. T2 - 29. Karlsruhe Deponie- und Altlastenseminar CY - Karlsruhe, Germany DA - 16.10.2019 KW - Kunststoffdichtungsbahnen KW - Deponie KW - Geokunststoffe PY - 2019 SN - 978-3-939662-25-9 VL - 36 SP - 15 EP - 28 PB - ICP Eigenverlag Bauen und Umwelt CY - Karlsruhe AN - OPUS4-49321 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Yevtushenko, Oleksandra A1 - Hattendorf, H. T1 - Electrochemical characterization of high alloyed materials in molten salts for solar energy applications N2 - Within the last years the use of feasible alternative energy sources has risen and is going to replace fossil resources more and more. Nevertheless, service conditions in solar facilities are due to the chemical composition of heat transmission media and temperatures, in many cases, extreme in terms of corrosion. Since the construction of power plants shall be economical with maximum life service, materials selection based on preliminary material qualification is essential to guarantee a secure and reliable operation of those facilities. The materials selection depends on the operation temperature of a power plant on the chemical composition of the transmission fluid used. In high corrosive environments Ni-based alloys are often used as an all-round solution for the construction of corrosion resistant parts, because of their good corrosion properties. However, there might be limits for their use regarding their corrosion behavior, with which this contribution deals. Experiences from the electrochemical characterization of materials in aqueous solutions are transferred to molten salts, providing a good addition to common exposure tests at temperatures from 450 0C to 600 0C. By means of electrochemical measurements and exposure tests the suitability of high alloyed materials in molten nitrate salt (60 % NaNO3/40 % KNO3) can be characterized. The method was verified on different Ni-based alloys (UNS N08810, UNS N06600) and Titanium (UNS R50250). T2 - NACE International Corrosion Conference 2015 CY - Dallas, TX, USA DA - 15.03.2015 KW - Localized corrosion KW - Nickel based alloys KW - Solar energy KW - Renewables KW - Electrochemical characterization KW - UNS N08810 KW - UNS N06600 KW - UNS R50250 PY - 2015 SP - paper 5659, S. 1 EP - 9 AN - OPUS4-34748 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Sarmiento Klapper, Helmuth A1 - Feigl, Michael A1 - Hilker, Nico T1 - Suitability of high-alloyed or alternative non-metallic materials in high saline artificial geothermal waters N2 - Many technologies have been developed to take advantage of geothermal energy, which became a feasible energy source to replace fossil fliel supply. Nevertheless, Service conditions in geothermal facilities are due to the Chemical composition of hydrothermal fluids and involved high temperatures, in many cases, extreme in terms of corrosion. Therefore, materials selection based on preliminary material qualification is essential to guarantee a secure and reliable Operation ofthe facilities. This contribution deals with the evaluation of the corrosion behavior of two high-alloyed metallic materials and a-A1203 in an artificial geothermal fluid simulating the conditions in the Northern German Basin, a location with high geothermal potential. The suitability of the super austenitic stainless Steel, alloy 31, and the nickel base alloy 59 in this geothermal fluid obtained by electrochemical measurements and exposure tests is addressed. As an alternative to the suitable but costly alloy 59 that showed excelient corrosion resistance against pitting corrosion, ceramic made of a-A1203 represents an interesting possibility for selected components to be used in the construction of geothermal facilities. T2 - Corrosion-2014 - XIIth International conference "Problems of corrosion and corrosion protection of structural materials" CY - Lviv, Ukraine DA - 11.06.2014 KW - Localized corrosion KW - Steel KW - Ni-alloy KW - Ceramic KW - Geothermal energy PY - 2014 SP - 18 EP - 22 AN - OPUS4-32743 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Aristia, Gabriela A1 - Le, Quynh Hoa A1 - Bäßler, Ralph T1 - Integrated Coating System for Corrosion Protection of Carbon Steel in Artificial Geothermal Brine N2 - Corrosive geothermal brines are a major challenge to geothermal power-plants. For cost reasons, plant designers prefer to use carbon and low alloyed steels, which are susceptible to uniform and localized corrosion when exposed to geothermal brines having acidic and saline properties. To solve such problem, coatings or inhibitors would be a protective solution as an alternative to the use of high alloyed materials. This study investigated a coating system consisting of polyaniline/silicon dioxide based on resources locally available in Indonesia. Protection against corrosion of carbon steel was shown by long-term (28 day) exposure and electrochemical tests of coated carbon steels, performed in an artificial acidic and saline geothermal brine, comparable to the conditions encountered at a site in Indonesia. Therefore, an integrated coating system is proposed for corrosion protection, combining the electrochemical functionality of polyaniline and the physical advantages of silica. T2 - AMPP International Corrosion Conference CY - Online meeting DA - 06.03.2022 KW - Geothermal KW - Corrosion KW - Coating KW - Polyaniline KW - Silicon dioxide PY - 2022 SP - 1 EP - 11 CY - Houston TX (USA) AN - OPUS4-54451 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Sarmiento Klapper, Helmuth A1 - Dimper, Matthias A1 - Keserović, Amela A1 - Sobetzki, Joana A1 - Zimmer, Sebastian T1 - Corrosion behavior of duplex stainless steel S31803 in artificial geothermal waters N2 - Since geothermal wells are a feasible energy source to replace fossil fuel supply, many technologies have been developed to take advantage of geothermal energy. Nevertheless, service conditions in geothermal facilities are due to the chemical composition of hydrothermal fluids and temperatures, in many cases, extreme in terms of corrosion. Therefore, materials selection based on preliminary material qualification is essential to guarantee a secure and reliable operation of the facilities. This contribution deals with the evaluation of the corrosion behavior of duplex steel S31803 (318LN, X2CrNiMoN22-5-3, 1.4462) conducted by electrochemical measurements and exposure tests in artificial geothermal waters simulating the conditions in different locations with geothermal potential in Germany. The duplex steel S31803 shows limited suitability for applications in artificial geothermal waters due to its susceptibility to pitting and crevice corrosion. For low saline geothermal waters it can be considered suitable at moderate temperatures. Slight crevice corrosion susceptibility needs to be considered. Results are being incorporated into a materials catalogue for geothermal applications which shall provide basic information for designers and users of geothermal facilities. T2 - NACE International Corrosion Conference 2016 CY - Vancouver, BC, Canada DA - 6.3.2016 KW - S31803 KW - Crevice corrosion KW - Duplex steel KW - Geothermal energy PY - 2016 SP - 7361-1 EP - 7361-8 PB - NACE International CY - Houston TX, USA AN - OPUS4-36986 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Torge, Manfred A1 - Bücker, Michael A1 - Feldmann, Ines T1 - Corrosion of historic timber T2 - IAQ 2014 - 11th International conference indoor air quality in heritage and historic environments CY - Prague, Czech Republic DA - 2014-04-13 KW - Klimamessungen KW - Mazeration PY - 2014 SP - P016, 79 AN - OPUS4-31483 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Torge, Manfred A1 - Krug, Sonja A1 - Bücker, Michael A1 - Feldmann, Ines A1 - Scharf, Holger A1 - Witthuhn, Heike T1 - Investigation of mercury emissions of historic tin-mercury-mirrors N2 - With the implementation of glass casting in France in the second half of the 17th century, larger mirrors could be produced. So-called tin-mercury mirrors were made by coating glass with tin amalgam. Today, many historical mirrors are partly damaged, the image quality is compromised, and the material integrity of the mirror is threatened. The transformation from tin into an oxide starts at the surface of the amalgam and proceeds down to the glass surface. The mercury dissolves as a liquid or gaseous phase. The amalgam layer is destroyed, so that conservation is necessary. Conservators must follow strict safety precautions while handling amalgam mirrors because of possible mercury emissions and corrosion of the amalgam, during which elemental mercury accumulates near the mirror frame in droplets and is emitted into the air. In a research project, the quantity of the mercury emissions from historical mirrors was examined and a technique to decrease these emissions was developed. T2 - International Conference on Non-destructive Investigations and Microanalysis for the Diagnostics and Conservation of Cultural and Environmental Heritage (ART 2011) CY - Florence, Italy DA - 13.04.2011 KW - Emission KW - Quecksilber KW - Zinn-Amalgamspiegel PY - 2011 UR - https://www.ndt.net/search/docs.php3?id=11425 SN - 1435-4934 VL - 16 IS - 10 SP - 1 EP - 8 PB - NDT.net CY - Kirchwald AN - OPUS4-25270 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wöhlecke, Andreas ED - Egloffstein, T. ED - Burkhardt, G. T1 - Aktuelles aus der Arbeit des BAM-Fachbeirats N2 - Der Fachbeirat kommt bereits seit 13 Jahren in seiner jetzigen Form zusammen, um Zulassungsrichtlinien, weitere Dokumente und fachliche Fragestellungen zu beraten. Die Zeit bringt auch personelle Veränderungen mit sich, darüber wollen wir berichten. Derzeit wird die Zulassungsrichtlinie für Schutzschichten im Fachbeirat und in seiner Arbeitsgruppe Geotextilien und Kunststoff Dränelemente (AG Geotextilien) überarbeitet. Zudem wurde die Zulassungsrichtlinie für Kunststoffdichtungsbahnen auf den aktuellen Stand der Regelsetzung und Normung gebracht. Bestimmte Medien, die hier bei einigen Prüfungen verwendet werden, dürfen nicht mehr in der EU in Verkehr gebracht werden. Hier werden die Hintergründe und Zusammenhänge in Kürze aufgezeigt. Zuletzt wird die Diskussion in Bezug auf den Einsatz von Rezyklaten in den zugelassenen Produkten aufgeführt. T2 - Karlsruher Deponie- und Altlastenseminar 2022 CY - Karlsruhe, Germany DA - 19.10.2022 KW - Deponie KW - Abdichtungssystem KW - Schutzschichten PY - 2022 SN - 978-3-939662-31-0 VL - 42 SP - 23 EP - 32 PB - ICP Eigenverlag Bauen und Umwelt CY - Karlsruhe AN - OPUS4-56209 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wöhlecke, Andreas ED - Al-Akel, S. T1 - Die Spannungsrissbeständigkeit von Kunststoffdichtungsbahnen aus PE-HD und die Zulassungsrichtlinie für Schutzschichten N2 - Kunststoffdichtungsbahnen (KDB) aus PE-HD (Polyethylen hoher Dichte) werden häufig zur Abdichtung von Bauwerken in der Geotechnik verwendet. Diese Produkte werden aus einem Kunststoff mit relativ komplexer Zusammensetzung hergestellt. Um eine Aussage über die Haltbarkeit von KDB aus PE-HD treffen zu können, muss das Materialverhalten berücksichtigt werden. In diesem Zusammenhang sind die wichtigsten Aspekte der Dauerhaftigkeit die Spannungsrissbeständigkeit und die Beständigkeit gegen Oxidation. Verschiedene PE-Sorten weisen eine unterschiedliche Spannungsrissbeständigkeit auf. Um dieser Eigenschaft von PE-HD zu begegnen, werden nur KDB aus sehr hochwertigen Rohstoffen zugelassen. Auf der anderen Seite werden hohe Anforderungen an die umgebenden Schichten, wie Auflager und Schutzschicht gestellt, um möglichst geringe Spannungen zu erzeugen und damit Dehnungen die Dehnungen der KDB gering zu halten. Bestimmte Medien, die bei den betreffenden Prüfungen verwendet werden, dürfen nicht mehr in der EU in Verkehr gebracht werden. Im Folgenden sollen die Zusammenhänge in Kürze dargestellt werden. Darüber hinaus sollen Diskussionen und Änderungen der Zulassungsrichtlinie für Schutzschichten im und durch den Fachbeirat vorgestellt werden. T2 - 19. Leipziger Deponiefachtagung CY - Leipzig, Germany DA - 14.03.2023 KW - Spannungsrissbeständigkeit KW - Deponie KW - Kunststoffdichtungsbahn PY - 2023 SN - 978-3-943443-53-0 VL - 19 SP - 25 EP - 32 PB - PRESSEL Digitaler Produktionsdruck AN - OPUS4-57194 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Boetcher, U. A1 - Steinborn, Gabriele A1 - Kuchenbecker, Petra A1 - Scheler, S. T1 - Bericht über einen Ringversuch zur Messung des Zetapotenzials und der Partikelgröße an Suspensionen submikroskaliger Pulver N2 - In diesem von der BAM (Bundesanstalt für Materialforschung und -prüfung, Berlin) Ende 2009 initiierten und koordinierten Ringversuch zur Methodenbewertung ging es um die Fragestellung der Verlässlichkeit von aus der Akustik bzw. Elektroakustik gewonnenen Ergebnissen (Gesamtmittelwert und Gesamtpräzision) zur Teilchengrößenverteilung bzw. der Zetapotenziale konzentrierter Suspensionen. Zum Einsatz kamen dabei in den jeweiligen Laboratorien baugleiche Ultraschallspektrometer des Herstellers Dispersion Technology, USA. Da es sich bei den verwendeten Pulvern und Solen nicht um zertifizierte Referenzmaterialien handelt, sind die Messergebnisse nicht auf ihre Richtigkeit überprüfbar. Jedoch lieferten die Untersuchungen der gewichtsbasierten d₅₀-Teilchengröße gute Übereinstimmungen bei den Ultraschallspektrometern in den unterschiedlichen Laboren. Beim Zetapotenzial ergab sich für die beiden kommerziellen Sole eine gute Übereinstimmung an den verschiedenen Standorten. KW - Partikelgröße KW - Zetapotenzial KW - Keramische Suspension PY - 2012 VL - 14 IS - April SP - 8 EP - 11 PB - Quantachrome CY - Odelzhausen AN - OPUS4-25837 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bettge, Dirk A1 - Ruhl, Aki Sebastian A1 - Bäßler, Ralph A1 - Yevtushenko, Oleksandra A1 - Kranzmann, Axel T1 - Corrosion aspects of materials selection for CO2 transport and storage N2 - The geological storage of carbon dioxide (Carbon Capture and Storage, CCS) in depleted gas reservoirs or in saline aquifers is a widely discussed issue. Carbon dioxide may induce corrosion on the piping steels during compression, transportation and injection. Therefore, selection of appropriate piping steels is a key factor in order to increase the safety and reliability of the CCS technology, and to keep the processes cost-effective. The here described subproject of the COORAL project (German acronym for “C02 purity for capture and storage”) deals with the levels of impurities in the C02 stream that will be acceptable when using specific steels. Material exposure to carbon dioxide (C02) containing specific amounts of water vapor, oxygen (02) sulfur dioxide (S02), nitrogen dioxide (N02), carbon monoxide (CO) can be a challenge to steels. Within this subproject 13 different Steels are tested for suitability as materials used for compression, transportation and injection Units within the CCS chain. T2 - 2nd ICEPE International conference on energy process engineering - Efficient carbon capture for coal power plants CY - Frankfurt/M., Germany DA - 20.06.2011 KW - Carbon capture KW - CCS KW - Corrosion PY - 2011 SP - 76 EP - 78 AN - OPUS4-24250 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Le, Quynh Hoa A1 - Bäßler, Ralph A1 - Knauer, S. A1 - Bettge, Dirk T1 - Korrosion von CO2-Rohrleitungswerkstoffen durch kondensierte Tröpfchen N2 - CCUS-Technologie (CO2-Abtrennung; Nutzung und Speicherung, engl. Carbon Dioxide Capture, Utilization and Storage) gilt als eine vielversprechende Methode zur Abschwächung des Beitrags von fossilen Emissionen zur globalen Erwärmung. Dabei wird das in den Verbrennungsprozessen entstandene Treibhausgas aufgefangen, zu verschiedenen Lagerstätten transportiert und langzeitig gespeichert bzw. einer chemischen Nutzung zugeführt. In bisher veröffentlichten Untersuchungen wurde gezeigt, dass die CO2-Transport-Pipelines in hohem Maße gefährdet sind, wenn sie korrosiven Begleitstoffen des CO2-Stroms, wie SOx, NOx bei einem hohen Wasserdampfanteil ausgesetzt sind. Screening-Tests zeigten, dass bei einer Konzentration von 1000 ppmv H2O die Reaktionen und Kondensation von SO2 und NO2 mit O2 und H2O zu Säuretropfen (pH ~ 0,5) auf der Oberfläche von Metall-Prüfkörper und Gefäß führen. Die Werkstoffe 1.0582, 1.8977, 1.4313 und 1.4562 wurden in CO2-gesättigtem Kondensat mit unterschiedlichem Verhältnis der säurebildenden Komponenten untersucht. Diese Studien zeigten grundsätzlich den Mechanismus sowie die Rolle jedes CO2-Strom-Begleitstoffes auf den Korrosionsprozess. Allerdings spiegeln die bei Auslagerung und elektrochemischen Messungen in der künstlichen CO2-gesättigten Kondensat-Lösung auftretenden Bedingungen nicht im Detail die Realität in der Praxis, wo sich nur Tröpfchen bilden, wider. Diese Arbeit konzentriert sich auf den Korrosionsprozess von Kondensat in Form von Tröpfchen, auf der Oberfläche von Rohrleitungswerkstoffen unter CO2-Atmosphäre bei 5 °C (Simulation des Transportzustandes). Die Experimente wurden nicht nur für Auslagerungsversuche, sondern auch für elektrochemische Tests mit nur einem Tröpfchen (weniger als 20 µL) konzipiert. Die Auslagerungs-versuche wurden sowohl unter Normaldruck als auch bei hohem Druck (> 70 bar) durchgeführt, wobei das CO2 als dichte – den Tropfen umgebende - Phase vorliegt. Die korrodierten Prüfkörper wurden rasterelektronenmikroskopisch (REM) und mittels Energiedispersiver Röntgenspektroskopie (EDX) analysiert, um nicht nur Korrosionsform, sondern auch die Elementverteilung der Korrosionsprodukte zu zeigen. T2 - 49. Kraftwerkstechnischen Kolloquium CY - Dresden, Germany DA - 17.10.2017 KW - CCUS KW - Korrosion KW - Stählen KW - Überkritisch KW - CO2 PY - 2017 SN - 978-3-934409-79-8 VL - 2017 SP - 1450 EP - 1463 CY - DRESDEN AN - OPUS4-42939 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Burkert, Andreas A1 - Eich, Gerd T1 - Integrated Protection System for Chloride Deteriorated Concrete Structures T2 - Corrosion 2004 ; 59th NACExpo 2004 ; 59th Annual conference & exposition. NACE International - The Corrosion Society CY - New Orleans, LA, USA DA - 2004-03-28 KW - Chloride Induced Corrosion KW - Thermal-Sprayed Zinc KW - Moisture Content KW - Embedded Sensors PY - 2004 PB - NACE International CY - New Orleans, La. AN - OPUS4-2601 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Schmidt, C. A1 - Alves, H. T1 - Recent experiences on suitability of titanium and high alloyed materials in acids at 200°C N2 - In the literature there are not much data available to describe the corrosion behavior of titanium, nickel alloys and special stainless steels in acids at high temperature, in particular above the boiling point. Therefore, a laboratory testing program was performed with two titanium alloys (UNS R50400 and UNS R53400) to obtain corrosion data in formic acid, acetic acid, phosphoric acid, polyphosphoric acid, p-toluene sulfonic acid and lactic acid at 200 °C. Results were compared to previously published ones obtained on UNS N08031, UNS N06059 and UNS N10665. From the results it can be concluded that titanium does not always show better corrosion resistance than Ni-based alloys. UNS N06059 was the best choice for formic and acetic acids at temperatures of 200 °C. Both Ti-alloys are resistant in acetic acid. Some slight differences were observed for formic acid, where UNS R50400 is only resistant up to a 20 % solution and UNS R53400 in concentrated acid too. The phosphoric acid is extremely corrosive and none of the investigated materials was resistant. In the diluted acid (5 %) only UNS R53400 is resistant, whereas in 1 % solution all investigated materials performed satisfactory. UNS N10665 and UNS N06059 showed the best behavior in polyphosphoric acid. In 30 % concentrated p-toluene sulfonic acid at 200 °C all alloys tested were unsuitable. In very diluted acid (0.1 %) both Ti-alloys and the other three alloys behaved well. In lactic acid at 180 °C increased corrosion underneath deposits was detected; the best performance was observed for UNS N06059 and UNS R50400. T2 - NACE International Corrosion Conference 2015 CY - Dallas, TX, USA DA - 15.03.2015 KW - Titanium grade 2 (UNS 50400) KW - grade 12 (UNS 53400) KW - alloy 59 (UNS N06059) KW - alloy 31 (UNS N08031) KW - alloy B-2 (UNS N10665) KW - Inorganic acids KW - Organic acids KW - Corrosion PY - 2015 SP - paper 5658, S. 1 EP - 13 AN - OPUS4-34749 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Yevtushenko, Oleksandra A1 - Le, Quynh Hoa A1 - Bettge, Dirk T1 - Suitability of Metallic Materials in CC(U)S Applications N2 - Carbon Capture Utilization and Storage (CCUS) is a promising technology to reach the target for reduction of CO2 emissions, e.g. from fossil-fuel operated power plants or cement mills. Crucial points for a sustainable and future-proof CCUS procedure are reliability and cost efficiency of the whole process chain, including separation of CO2 from the source, compression of CO2, its subsequent transportation to the injection site and injection into geological formations, e.g. aquifers. Most components that are in contact with CO2-stream consist of steel. Depending on the operating conditions (e.g. temperature, pressure, and CO2-stream composition) specific suitable steels should be used. The compressed CO2-stream is likely to contain process specific impurities; small amounts of SO2 and NO2 in combination with oxygen and water are most harmful. One approach, as currently preferred by pipeline operators, is to clean the CO2-stream to such levels, acceptable for carbon steel, commonly used as pipeline material. Another consideration would be, to use more corrosion resistant alloys for CO2-streams with higher amounts of impurities. Due to the absence of certified benchmarks for upper limits, systematic experiments with impurities in the CO2-stream were carried out reflecting mainly transport and injection conditions. Within the COORAL project (German acronym for “CO2 purity for capture and storage”) levels of impurities in the CO2-stream, being acceptable when using specific steels, were evaluated. Material exposure to dense or multiphase carbon dioxide (CO2) containing specific amounts of water vapor, oxygen (O2) sulfur dioxide (SO2), nitrogen dioxide (NO2), carbon monoxide (CO) can be a challenge to steels. In some situations, condensation of impurities and reaction products from the CO2 stream can occur. CO2 saturated brine is supposed to rise in the well when the injection process is interrupted. The material selection shall ensure that neither CO2 nor brine or a combination of both will leak out of the inner tubing. This COORAL-work was extended by a follow-up project, called CLUSTER. Here the additional influence of impurities was investigated when merging CO2 streams from different sources, combined within a “so-called” cluster. Results are summarized within the following table regarding suitability for different parts of the process chain. T2 - EUROCORR 2021 CY - Online meeting DA - 20.09.2021 KW - Carbon capture storage KW - Corrosion KW - Steel KW - CCS KW - CCU KW - CO2 PY - 2021 SP - 1 EP - 2 AN - OPUS4-53460 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Bäßler, Ralph A1 - Werner, H. A1 - Alves, H. T1 - Evaluation of the resistance of alloy 31 and alloy 59 for the transport of mixed acids in tanks T2 - EUROCORR 2007 CY - Freiburg im Breisgau, Germany DA - 2007-09-09 KW - Korrosionsbeständigkeit KW - Höherlegierte Werkstoffe KW - Mischsäuren KW - BAM-Liste KW - BAM-List KW - Acid corrosion KW - High-alloyed stainless steel KW - Nickel-base alloy KW - Corrosion test PY - 2007 N1 - Serientitel: EFC-Event – Series title: EFC-Event IS - 289 SP - 1 EP - 10 PB - DECHEMA CY - Frankfurt am Main AN - OPUS4-15853 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hamann, Christopher A1 - Adam, Christian A1 - Stolle, Dirk A1 - Spanka, M. A1 - Auer, G. T1 - Thermochemical treatment of waste products from iron and steel production N2 - Blast furnace (BF) sludge and electric arc furnace (EAF) dust are typical wastes that incur from iron and steel production. In addition to iron, calcium, carbon, and silicon they usually contain high concentrations of heavy metals such as zinc, lead, and cadmium that are potentially hazardous to the environment, rendering disposal in landfills ecologically problematic and costly. Consequently, pyrometallurgical, hydrometallurgical, and hybrid methods for selective elimination of non-ferrous heavy metals from BF sludge and EAF dust have been conceived, of which only the carbothermic reduction route taken in the so-called Waelz rotary kiln process has been proven to be economically successful. However, this process has several drawbacks regarding efficiency of heavy-metal removal and recovery of iron, and it does not allow processing of BF sludge. In this study, we investigated the efficiency and feasibility of selective chlorination and evaporation of non-ferrous heavy metals, particularly zinc and lead, in both BF sludge and EAF dust as an alternative, thermochemical processing route. To this end, hydrochloric acid and iron(II) chloride solution have been used as chlorinating agents, and the process of heavy-metal chlorination and evaporation has been investigated under inert operating conditions, at variable chlorine concentrations, and at temperatures between 500 and 1200 °C. High zinc and lead removal efficiencies of > 99.5 % were achieved with both chlorinating agents, but iron(II) chloride turned out to be overall more efficient for removal of zinc and lead from BF sludge and EAF dust. Interestingly, and in contrast to previous studies, the iron was completely retained in the processed solid residue, therefore rendering the processed residues virtually zinc- and lead-free raw materials that may either be used internally (e.g., feeding processed BF sludge and EAF dust back into the respective furnaces) or externally (e.g., for cement production). T2 - European Metallurgical Conference 2019 CY - Düsseldorf, Germany DA - 23.06.2019 KW - Blast furnace sludge KW - Electric arc furnace dust KW - Recycling KW - Selective chlorination KW - Zinc PY - 2019 SN - 978-3-940276-89-6 VL - 3 SP - 1267 EP - 1282 PB - GDMB CY - Clausthal-Zellerfeld AN - OPUS4-48362 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Wiesler, F. A1 - Hund-Rinke, K. A1 - George, E. A1 - Greef, J.-M. A1 - Holz, F. A1 - Hölze, L.E. A1 - Hülsbergen, K.-J. A1 - Martin, S. A1 - Severin, K. A1 - Spielvogel, S. A1 - Geiger, P. A1 - Nawotke, C. A1 - Kehlenbeck, H. A1 - Schenkel, H. A1 - Adam, Christian A1 - Bloem, E. A1 - Frank, D. A1 - Goldbach, H.E. A1 - Heene, M. A1 - Kratz, S. A1 - Kruse, A. A1 - Möller, K. A1 - Pinnekamp, J. A1 - Schoumans, O.F. A1 - Vogel, Christian A1 - Wulf, S. T1 - Recyclingphosphate in der Düngung – Nutzen und Grenzen N2 - Weltweit werden etwa 80–85 % aller abgebauten Rohphosphate für die Produktion von Düngemitteln verwendet. Bei noch steigendem Bedarf an Phosphor (P) geht man derzeit davon aus, dass die weltweiten P-Reserven noch über 200 Jahre ausreichen. Um den P-Vorrat langfristig abzusichern, sollte der in Reststoffen enthaltene Phosphor möglichst umfänglich genutzt werden. Dieser Forderung trägt das von der Bundesregierung 2012 erstmals beschlossene Deutsche Ressourceneffizienzprogramm ProgRess Rechnung. Rohphosphat wird auch seitens der Europäischen Kommission aufgrundseiner ökonomischen Bedeutung und des unsicheren Angebots als „kritischer Rohstoff“ eingestuft. Vor diesem Hintergrund hat die Bundesregierung in der Verordnung zur Neuordnung der Klärschlammverwertung vom 27. September 2017 in Deutschland eine verpflichtende technische Rückgewinnung von Phosphor für Abwasserbehandlungsanlagen ab einer Ausbaugröße von 100.000 Einwohnerwerten (12 Jahre nach Inkrafttreten der Verordnung) bzw. ab einer Ausbaugröße von über 50.000 Einwohnerwerten (15 Jahre nach Inkrafttreten der Verordnung) vorgeschrieben. Die Verordnung enthält keine Vorgaben hinsichtlich der anzuwendenden Technologie bei der Phosphorrückgewinnung. Ausgenommen von der Rückgewinnungspflicht sind Klärschlämme mit niedrigen Phosphorgehalten (weniger als 20 Gramm Phosphor je Kilogramm Klärschlamm-Trockenmasse). Auch die im Jahre 2017 verabschiedeten neuen Rechtsvorschriften für die Düngung verlangen zukünftig einen nachhaltigen und ressourceneffizienten Umgang mit Nährstoffen bei der landwirtschaftlichen Erzeugung und schränken die P-Zufuhr insbesondere auf hoch versorgten Böden ein (Düngeverordnung vom 26. Mai 2017). Dies wird zu einem mehr am Pflanzenbedarf orientierten und ggf. vermehrt überbetrieblichen Einsatz von wirtschaftseigenen Düngern führen. Um den politischen und gesetzlichen Anforderungen gerecht zu werden, müssen einerseits wirksame und kosteneffiziente technische Verfahren zum P-Recycling (weiter)entwickelt werden. Andererseits müssen die Recyclingprodukte die Anforderungen für eine direkte Verwendung in der Landwirtschaft oder als Rohstoff für die Herstellung von Düngemitteln erfüllen. In dem vorliegenden Standpunkt wird zunächst der potenzielle Beitrag von Reststoffen zur Deckung des P-Bedarfs in der deutschen Pflanzenproduktion geschätzt. Für die wichtigsten Reststoffe werden technische Verfahren zur P-Rückgewinnung bzw. Aufarbeitung skizziert. Auf Basis der Anforderungen der Landwirtschaft bzw. der Düngemittelindustrie an die P-Recyclingprodukte werden deren Herstellungsverfahren bewertet. Schließlich wird der Regelungs- und Forschungsbedarf formuliert. KW - Phosphor KW - Düngemittel KW - Diffusive Gradients in thin films (DGT) PY - 2020 SP - 1 EP - 19 PB - Bundesministerium für Ernährung und Landwirtschaft (BMEL) CY - Berlin AN - OPUS4-51011 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wöhlecke, Andreas T1 - Aktuelle Themen aus der Arbeit des Fachbeirats der BAM N2 - Es wird über aktuelle Arbeitsthemen und Entwicklungen im Fachbeirat berichtet. So wurde in einer Sondersitzung des Fachbeirats über die Entlassung aus der Nachsorgephase beim Einsatz von Geokunststoffprodukten in Böschungen diskutiert. Die Unterarbeitsgruppe Fremdüberwachung in der Produktion hat getagt. Darüber hinaus werden Änderungen in den Zulassungsrichtlinien für Kunststoffdichtungsbahnen, Kunststoff-Dränelemente und für die Fremdüberwachung kurz vorgestellt. T2 - 16. Leipziger Deponiefachtagung CY - Leipzig, Germany DA - 03.03.2020 KW - Deponie KW - Geogitter KW - Kunststoffdichtungsbahn PY - 2020 SN - 978-3-943443-49-3 VL - 16 SP - 35 EP - 43 PB - HTWK Leipzig CY - Leipzig AN - OPUS4-50507 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Adam, Christian A1 - Schraut, Katharina A1 - Weingart, Eric A1 - Hamann, C. T1 - Technische Möglichkeiten der Abfallvermeidung in der Stahlproduktion N2 - Bei der Stahlproduktion fallen verfahrensbedingt große Mengen an Nebenprodukten und Abfällen wie Stahlwerksschlacken, Filterstäube und Gichtgasschlämme an. Hohe Anteile dieser Stoffströme werden aufgrund ihrer Zusammensetzung immer noch deponiert, obwohl sie ein hohes Wertstoffpotential aufweisen. An der Bundesanstalt für Materialforschung und -prüfung (BAM) werden Verfahren untersucht und entwickelt, welche eine Verwertung und Kreislaufführung dieser Materialströme ermöglichen. Aus sogenannten Linz-Donawitz-(LD)-Schlacken können durch carbothermische Nachbehandlung Roheisen und ein dem Portlandzementklinker (PZK) ähnliches Bindemittel erzeugt werden. Aus Elektroofenstäuben und Gichtgasschlämmen kann Zink gewonnen und die Anteile an Eisen und Kohlenstoff in den Stahlproduktionsprozess zurückgeführt werden. Durch diese technischen Maßnahmen kann es gelingen die Deponierung von Abfällen der Stahlproduktion zukünftig deutlich zu reduzieren. T2 - Recy&Depotech 2020 CY - Online meeting DA - 18.11.2020 KW - Stahlwerksschlacke KW - Filterstaub KW - Gichtgasschlamm PY - 2020 SP - 1 EP - 9 PB - Montanuniversität Leoben CY - 8700 Leoben, Österreich AN - OPUS4-51605 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Stephan, Ina A1 - Boenke, Viola A1 - Drecker, Sigrid T1 - Weiterentwicklung und Verbesserung des Konzeptes zur Begrenzung von Konservierungsmitteln für Produkte mit dem Blauen Engel N2 - Im Rahmen des Forschungsvorhabens wurde die biologische Prüfmethode der Checkliste zur stoffli-chen Bewertung im Rahmen des Aufnahmeverfahrens für weitere Topfkonservierungsmittel in den Anhang 1 zur Vergabegrundlage RAL-UZ102 „Emissionsarme Innenwandfarben“ überarbeitet. Der Test für den Einsatz von Konservierungsmitteln in seiner jetzigen Fassung besteht seit nahezu 20 Jah-ren und erfolgt ausschließlich an weißer Dispersionsfarbe für den Innenraum. Die hierbei ermittelten Höchstmengen für den Einsatz von Topfkonservierern werden z.Zt. auch auf andere Innenraumbau-produkte übertragen. Ziel war es zu klären, ob die Anforderungen an die Topfkonservierung bei Far-ben tatsächlich für andere Innenraumbauprodukte übernommen werden können. Die im Vorhaben durchgeführten Versuche deuten darauf hin, dass dies nicht ohne weiteres möglich ist. Nach Rückspra-che mit Vertretern aus der Industrie wurde das Keimspektrum für die Prüfung zudem um Hefe- und Schimmelpilze erweitert. Des Weiteren wurde eine künstliche Alterung eingeführt und überprüft, ob dies einen Einfluss auf den Gehalt an Isothiazolinonen hat. Die Konzentration von Isothialzolinonen wurde mittels Ultra-Hochleistungsflüssigkeitschromatographie kontrolliert und hinsichtlich einer Kor-relation mit dem Wachstum von Mikroorganismen ausgewertet. Da die in den Innenraumbauproduk-ten zugesetzten Isothiazolinone als Kontaktallergene bekannt sind, ist es ein Ziel des „Blauen Engel“-Umweltzeichens, die geringste erforderliche Menge an Konservierungsmittel in den Produkten zu ver-wenden, ohne die positive Auswirkung der Topfkonservierung zu gefährden. Daher sind die Optimie-rung der Leistungsstärke von Konservierungsmitteln und die Kontrolle der Hygiene im Herstellungs-prozess von zunehmender Bedeutung. Um Einblicke in den Herstellungsprozess von Farben zu gewin-nen, wurden im Rahmen des Vorhabens vier Farbwerke besichtigt, in denen weiße Innenraumfarben produziert werden, die mit dem Umweltzeichen „Blauer Engel“ ausgezeichnet sind. Gemeinsam mit den Fachleuten vor Ort wurde diskutiert, welche Maßnahmen zur Verbesserung der Werkshygiene er-griffen werden können, um den Einsatz von Topfkonservierern möglichst gering zu halten. Des Weite-ren wurde in dem Forschungsvorhaben untersucht, ob eine schnellere Bestimmung der Keimzahl in den Rohstoffen mittels quantitativer Polymerasekettenreaktion bereits im Farbwerk realisierbar ist. KW - Methode KW - Isothiazolinone KW - Gebindekonservierung KW - Bakterien KW - Schimmel KW - Wirksamkeit KW - Biozide PY - 2020 SN - 1862-4804 VL - 54 SP - 4 EP - 149 PB - Umweltbundesamt CY - Dessau AN - OPUS4-50972 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Werner A1 - Wöhlecke, Andreas T1 - The role of junction strength in the performance of geogrids N2 - Designing the performance of geogrids in reinforce soil constructions usually does not consider long-term behavior and possible failure modes of junctions between longitudinal and transverse ribs. How could behavior of junctions be included? To which extend is it necessary? On the conference Geo-Chicago 2016, Swan and Yuan presented an ultimate limit state equation for the short-term material resistance of junctions. We discuss limitations and suggest improvements to include long-term behavior of junctions. Nevertheless, the approach applies only to a specific mode of shear-tensile failure of junctions and only to strictly rigid geogrids. A new design concept presented in the same year by Jacobs on the conference GeoAmerica for the special case of the anchorage of geogrids, which reinforce capping system on long and steep slopes of landfills, tried to overcome these drawbacks. We discuss the aspects of this concept related to the long-term behavior of junctions and the interplay between the load applied to junctions and the flexibility of longitudinal ribs. This interplay and the long-term junction strength determine the long-term behavior of geogrids. T2 - GeoAmericas 2020 CY - Online meeting DA - 26.10.2020 KW - Geogitter KW - Geokunststoffe KW - Deponie PY - 2020 VL - 4 SP - 1 EP - 10 AN - OPUS4-51484 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Barnefske, Lena T1 - PDMS-POS-capsules for prospective self-healing silicone rubber N2 - Capsules made of a polydimethylsiloxane (PDMS) core with a poly(organosiloxane) (POS) shell can be used as a new filler system for self-healing silicone rubber. Synthesis of these PDMS-POS capsules, as well as the characterization based on TGA, SEM and fluorescence spectroscopy is presented. T2 - 6th ICSHM 2017 CY - Friedrichshafen, Germany DA - 25.06.2017 KW - Self-healing KW - Capsules KW - PDMS PY - 2017 AN - OPUS4-40856 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Abel, Andreas T1 - Microstructural and mechanical characterisation of cast Fe-Al-Mo-Ti-B alloys N2 - With the advent of variable renewable energies, long-term energy storage capacities and flexible power generation technologies will be required for reliable grid stability. Hence, power plant technologies and turbomachinery components will continue to be developed and employed for efficient re-conversion of stored energy. With the introduction of new working fluids for higher thermal efficiencies, the working conditions of exposed components and materials will require higher corrosion resistance, but with the same mechanical performance, manufacturability and cost. Intermetallic iron aluminide alloys with their outstanding oxidation and corrosion resistance and good high-temperature properties depict a possible candidate for use in high-temperature structural applications. A quinary Fe-26Al-4Mo-0.5Ti-1B solid-solution alloy with eutectic particle hardening particularly demonstrated competitive mechanical properties compared to high-alloy P92 steels in previous studies. To derive standard material specifications with industrially relevant casting strategies, centrifugal investment-cast Fe-25Al-3.7Mo-0.4Ti-1B was characterised with respect to microstructure, thermophysical properties and mechanical properties under quasi-static tensile and creep loading up to 700 °C. Compared to P92 steel, the alloy demonstrated superior tensile strength above 550 °C and lower creep rates at 650 °C if stresses increase above 170 MPa. At lower temperatures though, the mechanical properties were inferior to P92 steel and related Fe-Al-Mo-Ti-B alloys, which was correlated to large grain sizes, a high tendency to surface and bulk cracking and a pronounced effect of tension-compression asymmetry. In further studies on alloy composition with varying Al, Mo and B concentration, a non-linear relationship of solid-solution hardening with solute Mo concentration was found. In this regard, halving Mo was the most effective measure for reducing brittleness without decreasing strength at room and elevated temperatures. Higher solidification rates and grain refinement down to 30 µm by die casting had a positive effect on ambient tensile strength, but were not achievable by investment casting. Dilatometry and hardness measurements indicated a low thermal vacancy hardening effect which was less sensitive to low-temperature annealing than in B2 FeAl alloys. Although mechanical properties up to 550 °C could be considerably improved by alloy development and processing, ductility at room temperature generally remained below 1%, necessitating substantial design margins for components from Fe-Al-Mo-Ti-B alloys. Despite the inherent limitations of alloy and casting process, the gained insights will help to prioritise future areas of research to mature cost-effective higher-order Fe Al alloys for high-temperature structural applications. KW - Hardness KW - Iron aluminide alloy KW - Micro structure KW - Tensile strength KW - Creep strength PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-632810 DO - https://doi.org/10.5445/IR/1000181739 SP - 1 EP - 179 PB - Karlsruher Institut für Technologie (KIT) CY - Karlsruhe AN - OPUS4-63281 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pirskawetz, Stephan A1 - Zaripova, Gulshat A1 - Brinkman, Nienke A1 - Gebraad, Lars A1 - Boehm, Christian A1 - Trattnig, Horst T1 - Digital Twin for the Simulation of Acoustic Emission Wave Propagation in Prestressed Concrete Elements N2 - In the 1950s, the use of prestressed concrete construction for bridges became widespread. The lack of experience in the early days causes problems today regarding a combination of corrosion and fatigue of the tendons. Wire breaks can lead to structural failure without warning. Acoustic emission analysis is the only reliable monitoring method to prevent catastrophic damage. Through an acoustic simulation of the structure and its fusion with measurement data, the research project "Digital Twin for the Simulation of Acoustic Emission Wave Propagation in Prestressed Concrete Elements" lays the foundation for optimizing the monitoring systems. T2 - III AE 2025 Nagoya CY - Nagoya, Japan DA - 04.11.2025 KW - Acoustic emission monitoring KW - Digital acoustic twin KW - Prestressed concrete bridge KW - Wire break KW - Stress corrosion cracking PY - 2025 SP - 113 EP - 117 PB - Japanese Society for Non-Destructive Inspection (JSNDI) AN - OPUS4-65456 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Österle, Werner A1 - Deutsch, Cornelius A1 - Rooch, Heidemarie A1 - Dörfel, Ilona T1 - Friction films on C-SiC discs after dynamometer tests with different commercial brake pads N2 - Brake discs on the basis of carbon fibre reinforced SiC-ceramics are appreciated as a light weight high performance alternative to conventional cast iron brake discs. Although efforts are going on to develop ceramic pads of a similar material but with additions of friction modifiers, comfort requirements cannot be reached with a full ceramic system and therefore commercial solutions still are based on polymer matrix composites (PMCs) and in some rare cases on sinter metallic (SM) friction materials. In previous studies with conventional automotive brakes an iron oxide based friction film on the surfaces of pads and discs was observed. This seemed to be plausible since iron is the major element of the cast iron disc and furthermore is contained in most pad formulations in the form of steel fibres. Therefore it was of great scientific interest to determine the relevance and composition of friction films on ceramic brake discs which do not contain any iron. T2 - EuroBrake 2012 CY - Dresden, Germany DA - 16.04.2012 KW - Ceramic disc KW - Friction film KW - PMC-pad KW - SM-pad KW - Third body PY - 2012 IS - EB2012-FM-01 SP - 1 EP - 9 AN - OPUS4-26823 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Martin A1 - Günther, U. A1 - Ballheimer, Viktor A1 - Linnemann, Konrad A1 - Wille, Frank A1 - Droste, Bernhard T1 - Experiences by German authority with safety case approach for welding seams as part of SNF transport package containments N2 - Federal Institute for Materials Research and Testing (BAM) is the responsible authority for the assessment of mechanical and thermal safety as well as quality issues within the licensing procedure for transport casks for radioactive materials. The assessment includes a brittle fracture analysis of all relevant cask components. For cask bodies where a steel bottom is welded to a steel shell, specimens for testing of sufficient fracture resistance can normally not be extracted directly from the welding seam area of the cask. Therefore, a methodology has to be developed to ensure compliance with the safety Analysis considerations and the approved design specification. This paper describes such a methodology including brittle fracture analysis and de-termination of required material properties as well as aspects of quality assurance during manufacturing. T2 - RAMTRANSPORT 2012 - 9th International Conference on the Radioactive Materials Transport and Storage CY - London, UK DA - 22.05.2012 PY - 2012 IS - Session 4.2 RAM 18 SP - 1 EP - 6 AN - OPUS4-26344 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Martin A1 - Ballheimer, Viktor A1 - Sterthaus, Jens A1 - Schubert, Sven A1 - Eisenacher, Germar A1 - Wille, Frank T1 - Material characterization and modeling within safety analysis of packages for transport of radioactive material N2 - In mechanical design safety assessment ofpackages for the transport of radioactive material the International Atomic Energy Agency (IAEA) regulations [1,2] require the use of one of four methods of demonstration of compliance with regulations: tests with prototypes, reference to previous satisfactory demonstrations, tests with scaled models as well as calculation or reasoned argument. In all cases characterization of material behavior is necessary. The need for material characterization can be split into three groups: characterization for material modeling in the design and verification process, determination of assessment criteria and inspections during manufacturing. The paper deals primarily with material characterization for the material modeling in the design phase and authorities approval process. Main package components are discussed: cask body and lids, screws, trunnions, impact limiter and basket(structure holding the content in specified position). Depending on the material used for these components this paper Shows exemplary a possible set of material investigations in order to allow modeling in design and assessment during the approval process. T2 - ASME 2012 Pressure vessels & piping division conference CY - Toronto, Ontario, Canada DA - 15.07.2012 PY - 2012 SP - PVP2012-78297, 1-6 PB - American Society of Mechanical Engineers CY - New York AN - OPUS4-26271 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schmidt, Wolfram A1 - Tlhatlha, Pheladi A1 - Obeng, Emmanuel A1 - Tsaku, Mawuli Kwaku A1 - Arthur, Daniel Vincent A1 - Dodoo, Alex ED - Schmidt, Wolfram ED - Tlhatlha, Pheladi T1 - A practical handbook for safe, smart and durable construction in Ghana N2 - The handbook provides practical guidelines for safe, efficient, and effective construction in Ghana, focusing on proper cement use, mixing consistencies and techniques, and environmental protection. It emphasizes quality control, safety in handling construction materials, and the importance of using protective equipment to prevent health hazards. KW - Cement strength classifications KW - Cement mixing ratios KW - Quality control PY - 2025 SN - 978-3-00-083134-8 SP - 1 EP - 35 PB - Ghana Standards Authority (GSA) CY - Accra AN - OPUS4-63641 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Schmidt, Wolfram A1 - Tchetgnia Ngassam, Ines Leana ED - Schmidt, Wolfram ED - Tchetgnia Ngassam, Ines Leana T1 - Cement proficiency testing scheme 2016/2017 - Final report N2 - The cement proficiency testing (PT) scheme was set up by the German Metrology Institute (PTB) and the Federal Institute for Materials Research and Testing (BAM) in 2012. The PT scheme was a spin-off from a European Commission and African, Caribbean and Pacific-Group of States funded project entitled SPIN – Spearhead Network for Innovative, Clean and Safe Cement and Concrete Technologies (www.spin.bam.de). The SPIN project aimed at crosslinking experts in industry and policy making bodies, with the prospect of establishing a sustainable cement and concrete construction capacity in Africa. After a successful first pan-African proficiency testing scheme in 2012/2013, it was decided to establish the scheme permanently and independent of the SPIN project. The main focus of setting up a testing scheme was to enable all cement testing laboratories in Africa to evaluate their competence and efficiency in cement testing and further enhance their capacity to obtain better quality products according to their environment. The acronym developed for the PT scheme is PACE-PTS (Pan-African Cement Proficiency Testing Scheme). The framework for the PT scheme was set up jointly among the organisers and the first participants. The first PT scheme was initiated in Dar Es Salaam in 2012 followed by a final workshop in Berlin in 2013. The second PT scheme began in 2014. A final workshop was organised in Dar es Salaam in 2015. The third and current scheme was started in 2016 and the final workshop is held in Yaoundé. KW - PACE-PTS KW - Round Robin KW - Proficiency testing KW - Cement KW - Quality infrastructure PY - 2017 VL - 3 SP - 1 EP - 74 PB - BAM CY - Berlin AN - OPUS4-43546 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ramirez Caro, Alejandra A1 - Pauli, Jutta A1 - Mota, Berta A1 - Crasselt, Claudia A1 - Artemeva, Elena A1 - Schmidt, Wolfram A1 - Resch-Genger, Ute T1 - A Spectroscopic Study of the Superplasticizer Effect on Early Cement Hydration N2 - Organic/inorganic mixtures were prepared from ordinary Portland cement (OPC), water (w/c 0.22), a fluorescent dye in aqueous solution (stable at alkaline pH; BAM-I), and two different comb shape polycarboxylates (PCEs), i.e., high charge (PCE-HC) and low charge (PCE-LC), respectively. Rheological and calorimetric measurements were performed prior to optical studies in order to select PCE concentrations. Absorption and fluorescence spectroscopy of the system OPC + BAM-I (CBAM-I) revealed maxima of dye BAM-I located at 645 nm and 663 nm, respectively. In presence of PCE-HC and PCE-LC, these mixtures displayed a small red shift in reflectance and a faster decrease in intensity compared to studies with CBAM-I; however, only slight differences were observed between the different PCEs. With time, all systems exhibited a decrease in intensity of BAM-I in absorption/reflectance and emission. This could be caused by dye adsorption and possibly decomposition when in contact with cement particles or hydration products. T2 - The Sixth International Symposium on Nanotechnology in Construction (NICOM6) CY - Hong Kong, China DA - 02.12.2018 KW - Cement KW - Optical Spectroscopy KW - Dye KW - Hydration PY - 2018 SP - 1 EP - 9 AN - OPUS4-49378 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pirskawetz, Stephan A1 - Wolf, Julia A1 - Schmidt, Wolfram A1 - Rogge, Andreas T1 - Einsatzmöglichkeiten der Schallemissionsanalyse im Bauwesen N2 - Die Schallemissionsanalyse (SEA) ist ein passives zerstörungsfreies Prüfverfahren. mit dem Rissbildung, Risswachstum und andere Gefügeveränderungen delektiert und lokalisiert werden können. Anhand von zwei Beispielen aus der Forschung der Bundesanstalt für Materialforschung und -prüfung (BAM) wird gezeigt welche Möglichkeiten die SEA beim Bauwerksmonitoring und bei der Untersuchung von Baustoffen bietet. Im ersten Beispiel wird die Ortung von Schallemissionen zur Verfolgung des Risswachstums in Beton eingesetzt. Weiterhin wird mit Zugversuchen an Faserbeton illustriert, dass mit der SEA Versagensmechanismen identifiziert werden können. T2 - 8. Symposium Experimentelle Untersuchungen von Baukonstruktionen CY - Dresden, Germany DA - 24.09.2015 KW - Schallemission KW - SHCC PY - 2015 SN - 1613-6934 N1 - Serientitel: Schriftenreihe Konstruktiver Ingenieurbau Dresden – Series title: Schriftenreihe Konstruktiver Ingenieurbau Dresden VL - 40 SP - 61 EP - 72 PB - Technische Universität Dresden CY - Dresden AN - OPUS4-34581 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ramirez Caro, Alejandra A1 - Pauli, Jutta A1 - Schmidt, Wolfram A1 - Resch-Genger, Ute T1 - Study of the superplasticizer-cement hydration interaction by optical spectroscopy N2 - Nowadays, superplasticizers (SPs) are widely used to increase fluidity and reduce water content in concrete; thus, allowing better workability for final applications. The present study will focus on the hydration effect using comb shape polycarboxylates (PCEs), which are known to allow a very low water/cement ratio (w/c of 0.20) or less.Optical methods have been successfully used for the analysis and monitoring of the interactions between a broad variety of nanoscale and molecular systems like nanoparticles of various chemical composition and different types of organic ligands or biomolecules.This encouraged us to assess the potential of these methods, and particularly fluorescence, for the investigation of the interactions that occur at the interface between hydrate surfaces of cement particles and PCE at a very early stage of concrete formation and to differentiate between the impact of PCE’s molecular structures on such interactions. T2 - 2nd International Conference on the Chemistry of Construction Materials CY - Munich, Germany DA - 10.10.2016 KW - Cement KW - Dye KW - Superplasticizers KW - Fluorescence PY - 2016 SN - 978-3-936028-96-6 VL - 50 SP - 260 EP - 263 PB - Gesellschaft Deutscher Chemiker e.V. CY - Frankfurth am Main AN - OPUS4-38881 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Janssen, Jan A1 - George, Janine A1 - Geiger, Julian A1 - Bercx, Marnik A1 - Wang, Xing A1 - Ertural, Christina A1 - Schaarschmidt, Joerg A1 - Ganose, Alex M. A1 - Pizzi, Giovanni A1 - Hickel, Tilmann A1 - Neugebauer, Joerg T1 - A Python workflow definition for computational materials design N2 - Numerous Workflow Management Systems (WfMS) have been developed in the field of computational materials science with different workflow formats, hindering interoperability and reproducibility of workflows in the field. To address this challenge, we introduce here the Python Workflow Definition (PWD) as a workflow exchange format to share workflows between Python-based WfMS, currently AiiDA, jobflow, and pyiron. This development is motivated by the similarity of these three Python-based WfMS, that represent the different workflow steps and data transferred between them as nodes and edges in a graph. With the PWD, we aim at fostering the interoperability and reproducibility between the different WfMS in the context of Findable, Accessible, Interoperable, Reusable (FAIR) workflows. To separate the scientific from the technical complexity, the PWD consists of three components: (1) a conda environment that specifies the software dependencies, (2) a Python module that contains the Python functions represented as nodes in the workflow graph, and (3) a workflow graph stored in the JavaScript Object Notation (JSON). The first version of the PWD supports directed acyclic graph (DAG)-based workflows. Thus, any DAG-based workflow defined in one of the three WfMS can be exported to the PWD and afterwards imported from the PWD to one of the other WfMS. After the import, the input parameters of the workflow can be adjusted and computing resources can be assigned to the workflow, before it is executed with the selected WfMS. This import from and export to the PWD is enabled by the PWD Python library that implements the PWD in AiiDA, jobflow, and pyiron. KW - Automation KW - Workflow KW - Materials Design KW - Multi-scale simulation KW - Digitalization PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-632328 DO - https://doi.org/10.48550/arXiv.2505.20366 SP - 1 EP - 12 AN - OPUS4-63232 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Wolfram T1 - Möglichkeiten zur Steuerung der Robustheit von selbstverdichtendem Beton gegenüber veränderlichen Umgebungstemperaturen N2 - Selbstverdichtender Beton (SVB) findet kaum Anwendung als Transportbeton. Ein wesentlicher Grund hierfür ist, dass die Außentemperaturen auf der Baustelle nicht gesteuert werden können. Während des Betonierens können allerdings Schwankungen in der Umgebungstemperatur die rheologischen Eigenschaften aber auch das Erstarrungsverhalten signifikant beeinflussen, wodurch in der Folge auch Veränderungen im Festbeton auftreten können. Durch geeignete Wahl der Komponenten kann die Robustheit von SVB gegenüber Einflüssen aus den Umgebungsbedingungen deutlich verbessert werden. In der vorgestellten Arbeit werden anhand von Untersuchungen am Betonrheometer, am Setzfließmaß und am Erstarren nach Vicat die Einflüsse von veränderlichen Umgebungstemperaturen auf die frühen Eigenschaften von SVB dargestellt. Der Fokus liegt auf Effekten, die durch die Modifikation von Polycarboxylatether-Fließmitteln und durch Stabilisierer eingetragen werden. Darüber hinaus wird der Einfluss des Mischungsentwurfes gezeigt. Die Ergebnisse werden mit Relevanz für praktische Betonanwendungen analysiert und es werden die wichtigen Einflussgrößen zur Verbesserung der Robustheit von SVB gegenüber Temperaturschwankungen herausgearbeitet. T2 - DAfStb Doktorandensymposium 2010 - 51. Forschungskolloquium CY - Kaiserslautern, Deutschland DA - 2010-11-11 KW - Selbstverdichtender Beton KW - Erstarren KW - Verarbeitungseigenschaften KW - Rheologie KW - Stabilisierer KW - Fließmittel PY - 2010 VL - 2 IS - Kap. C1 SP - 527 EP - 538 AN - OPUS4-22664 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF ED - Schmidt, Wolfram ED - Uzoegbo, H. T1 - Global issues in concrete construction - Markets, perspectives, technologies N2 - Many African economies are booming with steady and increasing velocity. Along with the economic upturn comes an immense need for construction activities. There i$ no viable substitute for concrete to satisfy the needs of the world's popuiation for buildings and infrastructure. The world only needs to seek to use concrete more smartly with more environmental consideration. The Symposium „Global Issues in Concrete Construction - Markets, Perspectives, Technologies" focuses on today's issues of global concern and aims to initiate a dialogue on creating a sustainable built environment. Presenters have been carefully selected from around the world with a high level of expertise in concrete engineering and construction. T2 - Bauma Africa 2013 CY - Johannesburg, South Africa DA - 18.09.2013 PY - 2013 SP - 1 EP - 67 AN - OPUS4-30028 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Wolfram T1 - Controlling rheology - The key to individual concrete performance specifications N2 - During the last three decades concrete has emerged from a rather simple mass construction material based on only the three components cement, water, and aggregates towards a high performance material, which can be adjusted for high performance applications and according to ultimate user specifications. The reason for the rapid evolvement was the increasing awareness about how the rheology of concrete can be improved without negatively affecting the mechanical properties of concrete. Hence, mineral additions and in particular Chemical admixtures have been the most influential factors for the technological boost since approximately the 1980s. The incorporation of superplasticizers into concrete mixture compositions eventually facilitated concrete engineers to improve the workability properties without need to increase the water-cement-ratio (w/c) and furthermore to significantly reduce the w/c without loss of workability. This finally resulted in concrete with higher performance and specified properties. Fillers are basically used to improve the particle packing of cementitious Systems, but they can also be used beneficially to support the rheology, since they modify the water demand and may interact with superplasticizers as well. Finally, supplementary admixtures like polysaccharides have become more populär in the field of mortar, plaster, and grout technology. They can have a variety of rheological effects on cementitious Systems, which can be used to individually adjust their performance. The possibility to control the rheology and the significantly widened ränge of consistencies that can be adjusted opened up the gates for modern concrete and any type of high performance concrete. Therefore, without doubt, it can be concluded that the capability to control the rheology of concrete Systems can be considered as the catalyst for the invention of the many recent mortar and concrete innovations such as polymer modified cementitious composites (PCC) self-compacting concrete (SCC), high-performance concrete (HPC), ultra-high performance concrete (UHPC) or engineered cementitious composites (ECC). Therefore, understanding the rheology of cementitious Systems and how to control the workability by the use of Chemical admixtures is the key to innovations in concrete technology. However, the other side of the coin of versatility is that sophisticated cementitious Systems have become more sensitive. Hence, concrete mixture composition with admixtures demands for a high level of expertise and often there is lack of awareness about the mode of Operation of rheology modifying admixtures among concrete technoiogists. The paper gives a comprehensive overview about rheology modifying constituents such as superplasticizers, stabilising agents, and mineral fillers, and how they can be used depending upon the application in the most favourable way. T2 - Facade coatings and plasters - European coatings conference CY - Düsseldorf, Germany DA - 29.10.2013 PY - 2013 SP - 93 EP - 102 PB - Vincentz AN - OPUS4-30827 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Wolfram T1 - Einfluss der Fließmittelmodifikation auf die Verarbeitungseigenschaften fließfähiger Betone - Hintergründe und Optimierungspotential N2 - Durch die Möglichkeit, die Konsistenz weitgehend vom Wasserzementwert zu entkoppelt, stellen verflüssigende Zusatzmittel ein starkes Werkzeug zur Verbesserung der Betontechnologie dar. Deswegen ermöglichen auch erst neuere Entwicklungen im Bereich der Fließmittel betontechnologische Innovationen wie den selbstverdichtenden Beton, hochfesten und ultrahochfesten Beton. Eine besondere Bedeutung haben Polycarboxylatether-Fließmittel. Diese sind in einer sehr großen Vielfalt und mit einer großen Bandbreite an Leistungseigenschaften am Markt erhältlich. Allerdings werden aufgrund der Vielseitigkeit Betone mit hohen Fließmittelgehalten auch sehr anfällig gegenüber äußeren Einflüssen, so dass Veränderungen in den Umgebungsbedingungen ungewünschte Effekte hervorrufen können. Folglich erfordern Betone mit Rießmitteln ein hohes Maß an Expertise, die nicht immer in der Praxis vorhanden ist. Der vorliegende Artikel gibt einen Überblick über die Wirkungsweisen von Fließmitteln und wie deren Leistungseigenschaften genutzt werden kann, um betontechnologische Fragestellungen optimal zu lösen. T2 - Fachtagung Betonbau aktuell 2014 CY - Apolda, Germany DA - 13.02.2014 PY - 2014 SP - 1 EP - 7 AN - OPUS4-30945 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baier, Johanna A1 - Wiehle, Philipp A1 - Thiele, Marc ED - Nille-Hauf, Konstantin T1 - Structural design of rammed earth – Influence of manufacturing parameters on the compressive strength N2 - At present, no structural design code for rammed earth exists that is based on the semiprobabilistic safety concept and adequately reflects the mechanical performance of modern rammed earth structures. This research aims to establish a scientifically grounded design framework for load-bearing rammed earth walls, incorporating the semi-probabilistic safety approach to ensure reliability and structural integrity. As a first step within the research project the influence of the manufacturing parameters of rammed earth on its mechanical properties are investigated. Compressive strength tests are carried out on cylinders produced with varying initial moisture contents and different compaction energies. Moreover, it is investigated whether the Proctor test according to DIN 18127 is suitable for determining the optimal moisture content (OMC) of rammed earth production. T2 - Earth Builder Summit EBS 2025 CY - Biberach, Germany DA - 06.03.2025 KW - Rammed earth KW - Structral design KW - Mechanical parameters PY - 2025 SP - 41 EP - 44 PB - Hochschule Biberach CY - Biberach AN - OPUS4-64343 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Wolfram A1 - Olonade, Kolawole Adisa A1 - Tchetgnia Ngassam, Ines Leana A1 - Mbugua, Rose A1 - Athman Mwende, Carol A1 - Kühne, Hans-Carsten ED - Ludwig, Horst-Michael T1 - Pflanzenbasierte Betonzusatzmittel für Hochleistungsbeton N2 - Während für die Bauwirtschaft in den meisten Ländern der nördlichen Halbkugel die Instandhaltung bestehender Strukturen und Infrastruktur im Vordergrund steht, geht es in vielen Ländern der Südhalbkugel in der Hauptsache um die Schaffung von Bauwerken und Infrastruktur zur Verwirklichung angemessener Lebensbedingungen, was wiederum das schnelle Wirtschaftswachstum weiter befeuert. Beton ist als Massenbaustoff, trotz landläufig anderer Bewertung, aufgrund seines im Vergleich zu anderen Baustoffen günstigen CO2-Footprints und der globalen Verfügbarkeit hierbei aktuell ohne Alternative. Allerdings ist Beton nach Wasser das am zweithäufigsten genutzte Produkt auf Erden [1] und die globale Nachfrage und Produktion steigt dramatisch. Dies hat Konsequenzen für das globale Klima, denn gerade die als Bindemittel eingesetzten Portlandzemente verursachen bei ihrer Herstellung selbst unter modernsten Produktionsbedingungen große Mengen an CO2. Deshalb müssen für zukünftige nachhaltigere Technologien neuartige Betone entwickelt werden, die bei gleicher oder verbesserter Leistungsfähigkeit, einen geringeren Bedarf an Portlandzement aufweisen. Um den CO2-Ausstoß, der mit der Betonherstellung verbunden ist zu minimieren, müssen Anteile an Portlandzement im Bindemittel reduziert und durch nachhaltigere Ersatzstoffe ausgetauscht werden. Darüber hinaus muss das eingesetzte Bindemittel im Beton so effizient wie möglich ausgenutzt werden. Das heißt, ein Bauteil oder Bauwerk sollte gerade so viel Bindemittel enthalten, wie für die Tragfähigkeit und Dauerhaftigkeit erforderlich ist. Hierfür erscheint der Einsatz von leistungsfähigen bauchemischen Produkten unumgänglich. Diese können zum einen die veränderten Verarbeitungseigenschaften, die Zementersatzstoffe mit sich bringen, ausgleichen und gleichzeitig helfen, den Gesamtwassergehalt zu minimieren, so dass das Bindemittel seine maximale Leistungsfähigkeit erzielt. Fließmittel sind aktuell die wichtigsten Zusatzmittel für Beton. Sie reduzieren den Wasserbedarf und ermöglichen, Zement im Beton effizienter auszunutzen. Darüber hinaus sind Stabilisierer wichtig zur Erhöhung der Robustheit, insbesondere im Hinblick auf die bautechnischen Herausforderungen der Zukunft – vom Pumpen über weite Distanzen, dem Spritzen, dem Betonieren bei extremen Klimabedingungen bis hin zum 3D-Druck. T2 - ibausil CY - Weimar, Germany DA - 12.09.2018 KW - Bauchemie KW - Zusatzmittel KW - Rheologie KW - Polysaccharide KW - Akaziengummi KW - Triumfetta Pendrata A. Rich PY - 2018 SN - 978-3-00-059950-7 VL - 20 SP - 1-874 EP - 1-885 CY - Weimar AN - OPUS4-47048 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Nazari, Narges T1 - Mikrohohlkathoden als Ultraschallquellen für zerstörungsfreie Prüfung N2 - Das Ziel dieser Arbeit ist es, das akustische Potenzial von Mikrohohlkathoden als Ultraschallquelle in der zerstörungsfreie Prüfung zu beleuchten. Im Mittelpunkt stehen Schalldruck, Richtverlauf und spektrale Anteile im Ultraschallbereich sowie der Einfluss der elektrischen Anregung. Es geht um eine praxisnahe Einordnung: Welche Stärken bringen MHCs als Sender mit, wo liegen die Grenzen. Die Ergebnisse sollen eine Grundlage schaffen, um MHCDs als neue Klasse kompakter Luft-Ultraschallquellen weiterzuentwickeln und gezielt in Prüfaufgaben einzusetzen. KW - Luftgekoppelter Ultraschall KW - Mikrohohlkathoden KW - Plasmaakustik PY - 2025 SP - 1 EP - 57 PB - Technische Universität Berlin CY - Berlin AN - OPUS4-65479 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Wallis, Theophilus T1 - Density-Based Phase-Field Modeling of Grain Boundary Segregation and Structural Transitions N2 - Polycrystalline materials are central to everyday engineering applications and technological advancements. The mechanical and functional properties of these materials can be influenced either negatively or positively by the presence of grain boundaries (GBs). These properties are interconnected with the structure, chemistry, or a combination of both (referred to as chemo-structure) at the GB. Therefore, an in-depth understanding of GBs, and their associated phenomena is key to tuning these materials properties for desired applications. Nevertheless, the intricate and unique characteristics of GBs impose constraints on their general descriptions in existing models designed for studying and understanding them. In this dissertation, a comprehensive tool, the CALPHAD-integrated density-based phase-field (DPF) model \cite{darvishikamachali2020model}, that harnesses atomic-scale GB characteristics, is employed and extended to reveal a deeper understanding of the GB structure, chemistry, chemo-structural coupling and their potential contributions to GB phenomena such as GB structural (and/or chemo-structural) transitions and liquid metal embrittlement. Although GBs possess distinctive crystallographic properties that render them unique and individualistic, it is important to note that they cannot exist independently; rather, they are made of the same constituents as the corresponding bulk material. To this end, the DPF model uses a continuous atomic density field ($\rho$), derived from atomistic simulations, to characterize the GB with reference to its corresponding homogeneous bulk (grain interior). This perspective allows the DPF model to approximate the GB free energy functional based on available bulk thermodynamic data. The DPF model has been utilized to investigate a variety of systems, form unary to multi-component systems \cite{kamachali2024giant,darvishikamachali2020model,darvishikamachali2020segregation,wang2021density,li2020grain,wang2021incorporating,zhou2021spinodal}. Among several novelties in the elucidation of the thermodynamics and kinetics of GBs, the DPF model has shown that GBs can have their own miscibility gap. It further reveals a temporal co-evolution of low and high segregation levels at the GB, which can act as precursor states for the formation of new phases \cite{kwiatkowskidasilva2018phase, kwiatkowskidasilva2019thermodynamics}. In the recent publication on Fe-Mn \cite{darvishikamachali2020segregation} and in various other works \cite{kamachali2024giant,darvishikamachali2020model,darvishikamachali2020segregation,wang2021density,li2020grain,wang2021incorporating,zhou2021spinodal, ikeda2023segregation, ahmadian2023interstitial} of the DPF model, the variation of atomic density field was allowed normal to the GB plane. At the GB plane, the in-plane GB density $\rho^{GB}$ was treated as a constant average value, representing its intrinsic dependence on the GB nature and misorientation. Although this assumption provides a useful simplification in studying GB phenomena, it does have the drawback of overlooking the significance of the in-plane structure variation. This seems to be particularly central in the view of experimental observations that confirm relatively stable grain boundary composition fluctuation \cite{darvishikamachali2020segregation}. In this thesis, the significance and impact of the atomic structure of GBs on their thermodynamics is investigated. This is achieved in two ways: On one hand, by extending the CALPHAD-integrated density-based free energy functional to account for structural degrees of freedom of GBs, and on the other hand, by deducing and linking density-related GB properties to the GB structure through the results of atomistic simulation of the GBs. Naturally, the structure (atomic density) within the GB plane fluctuates. This variation may also be linked to changes in composition due to solute segregation at the GB. While the fact that the GB structure can undergo transitions (referred to as complexions) \cite{frolov2015segregation, cantwell2020grain, cantwell2014grain} is not entirely new, the quantitative measurements of co-existing GB phases are scarce. Recently, instances were reported where the coexistence of two in-plane GB phases was revealed through the application of high-resolution transmission electron microscopy and atomistic simulation \cite{frommeyer2022dual, meiners2020observations}. To this end, the potential of GB structural variation within the DPF model is introduced in this thesis, where the GB in-plane density $\rho^{GB}$ is described as a field, that can vary both in time and space. This extension enables the in-plane GB density $\rho^{GB}$ to evolve and exhibit two distinct low-energy states, denoted as $\rho^{GB} = \rho_1$ and $\rho^{GB} = \rho_2$, where $\rho_2 > \rho_1$. Separating these two structural states is an in-plane line defect. This way, the model allows the studies of the co-evolution between the chemical and structural states of the GB. As a proof of concept and benchmark study, the extended-DPF model is implemented for studying Fe-Mn system. The results show that the GB structure's capacity to respond to chemical variations, as incorporated in the DPF model, enhances the Mn segregation transition at the GB, even in the absence of any alterations to the GB structure. When the GB structure undergo changes (or is non-uniform), the model reveals a coupling between the GB structure and chemical evolution. The ability of the GB structure to change allows the coexistence of spinodally formed low- and high-Mn phases within the GB during segregation transition. The acquired equilibrium segregation isotherms provides insight into the range of alloy compositions where these GB phases remain stabilised. Moreover, the observations indicate that the tendency of the GB to undergo a structural transition (change) is associated with the energy of the in-plane line defect, between low- and high-density domains within the GB plane. The extended-DPF model is further applied to Zn-coated advanced high strength steels (Fe-Zn systems), where Zn segregation to the GB is known to cause severe performance degradation due to liquid metal embrittlement \cite{razmpoosh2021pathway, ikeda2022early, bhattacharya2018liquid}. The effect of GB type and its chemo-structural coupling on Zn segregation is investigated. The results showed a sharp Zn segregation that is strongly influenced by the nature of the GB itself, as well as the coupling between its chemistry and structure. Additionally, GB phase diagrams were constructed across a wide range of alloy compositions and temperatures. The impact of the GB type and chemo-structural coupling on the miscibility gap of GBs is discussed. The DPF model's ability to incorporate atomic-scale characteristics into the construction of Gibbs free energies at the mesoscale ensures it retains key physical insights when predicting microstructure properties. To this end, a robust investigation of the model’s parameters and outputs in comparison to atomistic simulations of GBs is presented. This not only serves as a gauge for the models reliability, but also provide a new framework in establishing an atomistically-informed density-based description of GBs. First, by examining a large dataset of GBs in BCC-Fe and -Mo from atomistic simulations, a connection between their discrete atomic structure and the continuous atomic density function $\rho$ is established. This is achieved by a systematic coarse-graining approach wherein an atomsitically-obtained density function (delta function) is substituted with a normalised Gaussian function, so that, a smooth and continuous atomic density profile in real space can be obtained, where the minimum is the average atomic density at the GB plane $\rho^{GB}$. The investigation revealed a linear proportional relationship between the GB excess free volume and $\rho^{GB}$. This correlation simplifies the computation of the excess free volume as the integration over the portion of the density profile where the atomic density is less than one. Furthermore, the GB energies calculated by atomistic simulations revealed a correlation with $\rho^{GB}$ for certain classification of GB types, therefore enhancing the model's predictive accuracy. Concurrently, the atomic-scale characteristics of GBs can be further harnessed in the DPF models by replacing the simple functional form of the potential energy as given in the original DPF model formulation with a material specific interatomic potential (expressed as a function of the atomic density $\rho$) from molecular dynamic simulations. This way, a reliable prediction of the atomic density gradient energy coefficient for mesoscale simulations can be obtained. KW - Grain boundary structure KW - Grain boundary chemistry KW - Density-based phase-field modelling KW - Grain boundary thermodynamics KW - Grain boundary segregation transition PY - 2025 SP - 1 EP - 134 CY - Aachen AN - OPUS4-64455 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Robens-Radermacher, Annika T1 - Dataset for publication: Characterization of temperature influence on the structural built-up of 3D concrete N2 - Implementation, data, and results for the generation of the study "Characterization of temperature influence on the structural built-up of 3D concrete". In this study, the influence of temperature on structural build-up is investigated. A significant temperature influence is demonstrated for three experimental setups (small amplitude oscillatory shear, constant shear rate, and small amplitude oscillatory extensional tests) using different materials. A common modeling framework capturing the time- and temperature evolution is derived based on the maturity approach. Two alternative formulations for the time evolution were proposed. Both models were calibrated using a probabilistic approach, allowing for uncertainty quantification. The calibrated models successfully predict the structural build-up under different ambient temperature conditions. KW - Structural build-up KW - 3D concrete printing KW - Modeling KW - Parameter identification KW - Temperature influence PY - 2025 DO - https://doi.org/10.5281/zenodo.15845818 PB - Zenodo CY - Geneva AN - OPUS4-64982 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Riechers, Birte A1 - Maaß, Robert T1 - nanoindentation data associated with the publication "On the elastic microstructure of bulk metallic glasses" in Materials&Design 2023 N2 - This dataset consists of indentation data measured with a conospherical tip in a Hysitron-Bruker TI980 Nanoindenter on the surface of a <100> Silicon wafer and a polished cross-sectional cut of a Zr65Cu25Al10 bulk metallic glass. It is associated with the following publication: Birte Riechers, Catherine Ott, Saurabh Mohan Das, Christian H. Liebscher, Konrad Samwer, Peter M. Derlet and Robert Maass "On the elastic microstructure of bulk metallic glasses" Materials and Design xxx, (2023) 111929. https://doi.org/10.1016/j.matdes.2023.111929 All experimental information can be found in this paper and in the accompanying supplementary information. This electronic version of the data was published on the "Zenodo Data repository" found at http://zenodo.org/deposit in the community "Bundesanstalt fuer Materialforschung und -pruefung (BAM)". The authors have copyright to these data. You are welcome to use the data for further analysis, but are requested to cite the original publication whenever use is made of the data in publications, presentations, etc. Any questions regarding the data can be addressed to birte.riechers@bam.de who would also appreciate a note if you find the data useful. KW - Metallic glasses KW - Nanoindentation KW - Elastic microstructure PY - 2023 DO - https://doi.org/10.5281/zenodo.7818224 PB - Zenodo CY - Geneva AN - OPUS4-57352 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Wolfram ED - Banjad Pecur, Ivana ED - Baricevic, Ana ED - Stirmer, Nina ED - Bjegovic, Dubravka T1 - Potentials for sustainable cement and concrete technologies - Comparison between Africa and Europe N2 - The fundamental knowledge about cement and concrete has made enormous progress over the last decades, and today it would be possible to find optimised sustainable concrete solutions tailored for every given boundary framework and raw material supply. However, this knowledge barely finds implementation into practice despite the urgent global need to minimise carbon emissions and energy consumption. A major reason is that most concrete developments were historically made in the northern hemisphere, where today over-regulations and stagnating market perspectives slow down innovation drive towards higher sustainability. In most African countries, however, sustainable building is simply an urgent real-life problem. The demand for building is enormous, Standard solutions are not an option, and the pool of innovative local raw materials and concrete concepts is enormous. The paper provides a comprehensive comparison between the boundary frameworks of Europe and Africa, and it is explained why local African solutions shall be given priority over imported solutions. Examples of local African concrete solutions are given, and ideas for a rapid implementation are developed. Most of the potentially useful materials such as agricultural ashes, natural and calcined pozzolans, polysaccharides, etc. have not yet been subject to intensive research to date. Therefore, it is not unlikely to assume that with an open mind for non-Standard solutions, combined with creativity and particularly knowledge and awareness, the next generation of innovative and sustainable concretes will be developed and applied on the African continent. Therefore, the conclusion is that particularly the African continent provides the best starting position to develop better and more sustainable concrete solutions than anywhere else in the world. Hence, Africa can become a global pioneer in green cement and concrete technology with impact to the entire world. N2 - Posljednih desetljeća načinjen je golem napredak u temeljnim znanjima o cementu i betonu. Danas bi bilo moguće naći rješenja za optimalni održivi beton primjeren svakom danom okviru i dobavi sirovina. Međutim, takvo znanje jedva da se primjenjuje u praksi unatoč hitnoj globalnoj potrebi smanjenja na najmanju mjeru emisija ugljika i potrošnje energije. Glavni je razlog što je većina razvoja u području betona tijekom povijesti načinjena u sjevernoj hemisferi gdje danas preregulacija i perspektiva stagnirajućeg tržišta usporavaju inovacije ka većoj održivosti. Međutim, u većini afričkih zemalja održiva gradnja jednostavno je hitni problem svakodnevice. Zahtjevi za gradnjom su golemi, obična rješenja nisu opcija, rezerve inovativnih lokalnih sirovina i mogućnosti primjene betona su golemi. U radu se daje sveobuhvatna usporedba graničnih okosnica Europe i Afrike, a objašnjeno je zašto se lokalnim afričkim rješenjima mora dati prioritet pred uvezenim rješenjima. Većina potencijalno korisnih materijala kao što su pepeli iz poljoprivrede, prirodni i kalcinirani pucolani, polisaharidi itd. do danas nisu bili predmetom intenzivnih istraživanja. Stoga nije nevjerojatno pretpostaviti da će se Nova generacija inovativnih i održivih betona razviti i primijeniti na afričkom kontinentu uz otvorenost prema nestandardnim rješenjima i u kombinaciji s kreativnošću i posebno znanjem i sviješću. Stoga je zaključeno da naročito afrički kontinent osigurava najbolju početnu poziciju za razvoj boljih i održivijih betona nego bilo gdje u svijetu. Prema tome Afrika može postati svjetski pionir u tehnologiji zelenoga cementa i betona s utjecajem na cijeli svijet. T2 - 1st International Conference on Construction Materials for a Sustainable Future CY - Zadar, Croatia DA - 19.4.2017 KW - Africa KW - Sustainability KW - Cement KW - Concrete KW - Admixtures KW - Carbon emissions PY - 2017 SN - 978-953-8168-04-8 SP - 829 EP - 835 CY - Zagreb, Croatia AN - OPUS4-40977 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lorenzoni, Renata A1 - Mezhov, Alexander A1 - Fritsch, Tobias A1 - Schmidt, Wolfram A1 - Kruschwitz, Sabine T1 - Effect of Biochar on the Microstructure and Mechanical Response of Cement Paste N2 - The use of biochar as a supplementary cementitious material is proposed to reduce the global greenhouse gas emissions. Since biochar is non-reactive, has a low density and complex porosity, its incorporation into cementitious materials results in microstructural changes and consequently affects the mechanical response. This work advances the mechanical response understanding of Portland cement composites with 0, 5, and 25 volume percent (vol%) of cement replaced with biochar by using in-situ computed tomography, correlating with the microstructural changes analyzed by HFC, gas sorption, MIP, gas sorption, and NMR. The results highlight the influence of the mesoscale structure on mechanical responses and relate the lack of loss of mechanical strength at 5 vol% replacement to the compensation of decreasing larger pores with biochar addition. At 25 vol% replacement, the amount of weakened zones in the paste due to biochar overcompensates the positive effect of the reduction in larger pores, resulting in a loss of mechanical properties. Hence, small amounts of biochar can enhance the microstructure, but the reduction of the carbon footprint is limited. T2 - 24th International Conference on Composite Materials (ICCM24) CY - Baltimore, Maryland, USA DA - 04.08.2024 KW - Supplementary cementitious materials KW - Biochar KW - Microstructure KW - In-situ computed tomography KW - Mechanical proprieties. PY - 2024 DO - https://doi.org/10.14359/51742027 VL - 362 SP - 1020 EP - 1032 PB - International Concrete Abstracts Portal AN - OPUS4-62115 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kruschwitz, Sabine A1 - Lorenzoni, Renata A1 - Telong, Melissa A1 - Lauinger, Robert A1 - Munsch, Sarah Mandy A1 - Schmidt, Wolfram T1 - Investigation of the hydration of clinker-reduced cementitious binders by 1H NMR N2 - In this paper, we demonstrate the value of 1H NMR relaxometry for studying the hydration of clinker-reduced, more climate-friendly cementitious binders. The results were obtained on typical CEM I cements and sister samples containing two different reactive agricultural ashes as well as non-reactive biochars as supplementary cementitious materials. The findings prove that time-resolved NMR measurements provide valuable additional information when combined with classical heat flow calorimetry. T2 - International Conference on Electromagnetic Wave Interaction with Water and Moist Substances of the International Society for Electromagnetic Aquametry (ISEMA) 2023 CY - Brisbane, Ausralia DA - 25.09.2023 KW - Carbon emission KW - 1H NMR relaxometry KW - Heat flow calorimetry KW - Cement, hydration KW - Clinker reduction PY - 2023 SP - 1 EP - 3 AN - OPUS4-58936 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bintz, Thilo A1 - Munsch, Sarah Mandy A1 - Stelzner, Ludwig A1 - Lauinger, Robert A1 - Schmidt, Wolfram A1 - Kruschwitz, Sabine T1 - An NMR tomograph for building materials - applications, experimental studies and limitations - N2 - A summary of the possibilities, technical limitations and application examples for a unique NMR tomograph at BAM. T2 - 13th International Conference on Electromagnetic Wave Interaction with Water and Moist Substances (ISEMA), 2021 CY - Kiel, Germany DA - 27.06.2021 KW - Relaxation time distribution KW - NMR imaging KW - Capillary suction PY - 2021 SN - 978-1-7281-8738-9 N1 - Geburtsname von Munsch, Sarah Mandy: Nagel, S. M. - Birth name of Munsch, Sarah Mandy: Nagel, S. M. SP - 106 EP - 110 PB - IEEE AN - OPUS4-53116 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ramirez Caro, Alejandra A1 - Mota, Berta A1 - Artemeva, E. A1 - Pauli, Jutta A1 - Schmidt, Wolfram A1 - Resch-Genger, Ute T1 - A spectroscopic study of the superplasticizer effect on early cement hydration N2 - Organic/inorganic mixtures were prepared from ordinary Portland cement (OPC), water (w/c 0.22), a fluorescent dye in aqueous solution (stable at alkaline pH; BAM-I), and two different comb shape polycarboxylates (PCEs), i.e., high charge (PCE-HC) and low charge (PCE-LC), respectively. Rheological and calorimetric measurements were performed prior to optical studies in order to select PCE concentrations. Absorption and fluorescence spectroscopy of the system OPC + BAM-I (CBAM-I) revealed maxima of dye BAM-I located at 645 nm and 663 nm, respectively. In presence of PCE-HC and PCE-LC, these mixtures displayed a small red shift in reflectance and a faster decrease in intensity compared to studies with CBAM-I; however, only slight differences were observed between the different PCEs. With time, all systems exhibited a decrease in intensity of BAM-I in absorption/reflectance and emission. This could be caused by dye adsorption and possibly decomposition when in contact with cement particles or hydration products. T2 - 20. Internationale Baustofftagung CY - Weimar, Germany DA - 12.09.2018 KW - Optical spectroscopie KW - Cement hydration KW - Dyes PY - 2018 SN - 978-3-00-059950-7 VL - 20 SP - 1 EP - 6 PB - F.A. Finger-Institut für Baustoffkunde CY - Weimar AN - OPUS4-46277 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Wolfram T1 - Influence of the processing temperature and combined admixtures on the properties of Self-Compacting Concrete T2 - 7th International PhD Symposium in Civil Engineering CY - Stuttgart, Germany DA - 2008-09-11 PY - 2008 IS - Kap. 16.8 SP - 75 EP - 84 AN - OPUS4-17948 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Shamsuddoha, Md A1 - Hüsken, Götz A1 - Schmidt, Wolfram A1 - Kühne, Hans-Carsten A1 - Baeßler, Matthias T1 - Superplasticizer and Shrinkage Reducing Admixture Dosages for Microfine Cement in Grout Systems N2 - Grouts have numerous applications including crack repair as maintenance in construction industries. Microfine cements are intensively used for high strength mortar and grout products. They are ideal for injection grouting in structural repair. Such grouts should have suitable rheological properties to be injectable, especially those used in repair and rehabilitation. The use of superplasticizers (SP) in these products is thus becoming increasingly crucial to achieve favorable workability and viscosity properties. A difficulty in such grouts is the plastic shrinkage due to finer particles used. It is thus necessary to determine optimum SP and shrinkage reducing admixture (SRA) dosages for a microfine cement based grout. In this study, a saturation dosage was decided from two Polycarboxylate ether (PCE) based SPs in relation to neat cement using slump flow and rheological parameters. A range of grout mixtures was formulated containing micro silica (MS) and fly ash (FA), and tested for suitable rheological and mechanical parameters. Based on the results, a grout mixture with MS and FA was selected to determine optimum SRA content. According to the results, a SP dosage of 3% by weight of neat cement is sufficient to achieve saturation. The grout material including MS and FA can produce comparable properties to neat cement grout. MS is found to improve compressive strength within the range considered, whereas a higher FA content provides favourable rheological properties. Finally, a SRA dosage of 4%, which could reduce the shrinkage by about 43% after 28d days, is determined for the grout system. T2 - 2nd International Conference on Building Materials and Materials Engineering (ICBMM 2018) CY - University of Lisbon, Portugal DA - 26.09.2018 KW - Grout KW - Microfine Cement KW - Superplasticizer KW - Supplementary Cementitious Materials KW - Shrinkage Reducing Admixture PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-478319 DO - https://doi.org/10.1051/matecconf/201927801001 VL - 278 SP - Article Number 01001 PB - EDP Sciences AN - OPUS4-47831 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Shamsuddoha, Md A1 - Hüsken, Götz A1 - Schmidt, Wolfram A1 - Kühne, Hans-Carsten A1 - Baeßler, Matthias ED - Alexander, M.G. ED - Beushausen, H. ED - Dehn, F. ED - Moyo, P. T1 - Workability and mechanical properties of ultrafine cement based grout for structural rehabilitation: A parametric study on the partial replacement with SCMs N2 - Grouting is a universal repair and strengthening technique, which is constantly used for structural remediation of concrete components, trenches, mine subsidence, dam joints, restoration of masonry structures, and geological stabilizations. Having an extremely small particle size of only few microns, ultrafine cements are ideal for grouting applications due to their superior permeability and compressive strength properties of the hardened cement paste compared to that of the less-expensive, but coarser ordinary Portland cements. Supplementary cementitious materials (SCMs) are often used to replace ultrafine cement in order to modify certain properties and to reduce costs. The aim of this experimental study is to investigate the effect of three supplementary materials: microsilica (MS), fly ash (FA), and metakaolin (MK) on the workability, and mechanical properties of an ultrafine cement based grout with a constant water-binder ratio and constant superplasticizer content. Maximum percentages of replacement with ultrafine cement were 6% by volume of cement for MS and 16% for FA, and MK. In general, results suggest that the workability is improved by addition of FA, whereas is reduced, when modified with MS and MK. The compressive strength of grout after cement replacement remains comparable to that of pure cement grout. However, there is a tendency of the MS to positively affect the compressive strength opposite to FA, whereas flexural strength is positively affected by FA. Based on the results, it is evident that grouts with Hägerman cone flow more than 500 mm and compressive strength of more than 90 MPa after 28 days can be produced. T2 - International Conference on Concrete Repair, Rehabilitation and Retrofitting (ICCRRR 2018) CY - Cape Town, South Africa DA - 19.11.2018 KW - Grouting KW - Repair KW - Box-Behnken KW - Supplementary cementitious materials KW - Analysis of variance PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-464769 DO - https://doi.org/10.1051/matecconf/201819907006 SN - 2261-236X VL - 199 SP - 07006-1 EP - 07006-7 PB - MATEC Web of Conferences AN - OPUS4-46476 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Wolfram ED - Schmidt, W. ED - Uzoegbo, H. T1 - Peculiarities of African cement and concrete markets - Challenges and opportunities N2 - The African environment for the construction with concrete differs greatly from the Situation that can be found in Europe, Japan or North America. Europe can look back upon a concrete tradition of more than 150 years. Standardising documents and guidelines exist since more than 100 years, which formed the foundation of modern Standards that are adopted and applied and in many regions of the world. The technological developments in cement production are also strongly influenced by environmental conditions of the Northern hemisphere. In contrast, with the exception of South Africa, in most countries of sub-Saharan Africa, cement production started in the 1950s to 1960s, followed by a period of political and economical disturbances in many countries. As a result, there have not been serious approaches towards customised Solutions for the construction with concrete for the specific boundary conditions of sub-Saharan Africa. In most countries Standards from overseas are applied. Today, most African economies are growing at a rapid pace and construction activities in infrastructure and housing are urgently required to support and keep up the economic verve. Concrete technology will become of major interest in this context, since no other material can be produced similarly efficiently based on raw materials, which can be found largely only locally. In order to produce concrete with high efficiency, the local boundary framework has to be taken into account. Sub-Saharan Africa exhibits special peculiarities that are not covered by the recently applied technological guidelines and Standards. These need to be addressed to in local codes of practice in order to maximise the benefit of concrete technology. T2 - Bauma Africa 2013 - Global issues in concrete construction - Markets, perspectives, technologies CY - Johannesburg, South Africa DA - 18.09.2013 PY - 2013 SP - 25 EP - 28 AN - OPUS4-30032 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Klewe, Tim T1 - Synthetic Dataset for Sequential Learning-Based Optimisation of Bio-Ash Binder Formulations under Seasonal Availability Constraints N2 - This dataset accompanies the study on sequential learning–based optimisation of bio-ash–cement binder formulations under seasonally varying material availability. It provides a fully synthetic but chemically inspired benchmark design space for evaluating data-driven optimisation strategies in cementitious materials research. The dataset comprises 5,006 unique binder formulations, each defined by the mass fractions of cement and five bio-based ash components (A1–A5). Ash components represent generic bio-ash types derived from agricultural residues (e.g. rice husk ash, cassava peel ash), and their internal proportions are systematically varied under mass-balance constraints. Cement content ranges from 0 to 100 wt% in discrete steps. To reflect dynamic supply conditions, the dataset includes season-specific ash usage metrics for four seasons (S1–S4), expressing the fraction of available ash resources consumed by each formulation. A synthetic compressive strength value is assigned to every formulation using a nonlinear scoring function based on chemically inspired descriptors, with added noise to generate a structured yet non-trivial optimisation landscape. These strength values do not represent calibrated physical predictions and are intended solely as a hidden objective function for benchmarking sequential learning algorithms. The dataset is designed for in silico benchmarking, reproducibility studies, and methodological comparisons of optimisation and active learning strategies. It enables systematic evaluation of algorithmic performance without the need for physical experiments. KW - Sequential learning KW - Bio-based ashes KW - Low-clinker cement KW - Mixture optimisation KW - Supplementary cementitious materials PY - 2026 DO - https://doi.org/10.5281/zenodo.18389681 PB - Zenodo CY - Geneva AN - OPUS4-65420 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Adam, Christian T1 - Phosphorrückgewinnung aus Klärschlammaschen: Forschungsergebnisse aus Deutschland T2 - Klärschlammbehandlung heute und morgen CY - Wels, Österreich DA - 2007-11-21 PY - 2007 SP - 1 EP - 4 CY - Wien, Österreich AN - OPUS4-16467 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stephan, Ina A1 - Grinda, Manfred A1 - Rudolph, Dieter T1 - Comparison of different methods for assessing the performance of preservatives in the BAM fungus cellar test N2 - The fungus cellar test is a common means to get reliable data on the long term performance of treated wood in soil contact. A constantly high humidity and a suitable of water holding capacity for a range of micro-organisms provide high decay rates in untreated wood and produce intensive microbial pressures on wood treated with biocides. Presently a range of biocides are under test in the BAM fungus cellar and the results will be presented for the following types of biocides: Tebuconazole in combination with copper and boron (5 years fungus cellar), quats with copper and boron (5 years fungus cellar) and Cu-organic compound combined with copper and boron (3 years fungus cellar). Figures will be shown on the development of the Modulus of Elasticity (MOE) over the years and on an assessment of the stakes according to EN 252. T2 - 29th Annual Meeting of the International Research Group on Wood Preservation CY - Maastricht, Netherlands DA - 1998-06-14 KW - Fungus cellar KW - Soil contact KW - Triazoles KW - Cu-HDO KW - Quats KW - MOE PY - 1998 UR - http://www.irg-wp.com/irgdocs/details.aspx?id=08ae393d-c7db-419b-a0b5-dfeb2970d7ba SP - Paper IRG/WP 98-20149, 1-17 PB - International Research Group on Wood Preservation CY - Stockholm AN - OPUS4-4454 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stephan, Ina A1 - Göller, Stephan A1 - Rudolph, Dieter T1 - Improvements of monitoring the effects of soil organisms on wood in fungal cellar tests T2 - Paper prepared for the 27th Annual Meeting CY - Gosier, Guadeloupe DA - 1996-05-19 KW - Bending strength KW - Modulus of elasticity KW - Monitoring KW - Non-destructive testing KW - Fungal cellar KW - Soil-bed PY - 1996 IS - 20093 SP - 1(?) EP - 11(?) PB - IRG CY - Stockholm AN - OPUS4-4452 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Munz, Martin A1 - Schulz, Eckhard A1 - Sturm, Heinz T1 - Reliability of polymer materials - the nanoscopic view on interphases T2 - Kick-off Meeting zu einem gemeinsamen DAAD-Projekt mit der Universidad Pais Vasco (UVP), Dept. of Chemical and Environmental Engineering, Industrial Engineering School (EITI), Materials and Technologies Group CY - San Sebastián, Spain DA - 2002-08-08 PY - 2002 SP - 1(?) EP - 12(?) AN - OPUS4-1832 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wöhlecke, Andreas A1 - Müller, Werner ED - Kilchert, M. T1 - Aktuelle Informationen zum Stand der Arbeit und zu den Arbeitsergebnissen des Fachbeirates der BAM zur Zulassung von Geokunststoffen und Dichtungskontrollsystemen N2 - Die Geschichte der BAM-Zulassung begann vor nunmehr 20 Jahren. Durch die neue Deponieverordnung (DepV - diese Abkürzung bezeichnet im Folgenden immer die novellierte Fassung vom 17.10.2011) erhielt die Zulassungstätigkeit der BAM jedoch eine neue gesetzliche Grundlage. Geokunststoffe, Polymere und Dichtungskontrollsysteme müssen nun von der BAM zugelassen und die Eignung sonstiger Baustoffe bundeseinheitlich nachgewiesen werden. Bei der Umsetzung von Anforderungen in Zulassungsrichtlinien der BAM wirkt ein Fachbeirat beratend mit. Die Zuständigkeit und die Aufgaben der BAM werden im Folgenden erläutert. Der Fachbeirat beschloss bereits die Zulassungsrichtlinien für Kunststoffdichtungsbahnen, Schutzschichten, Kunststoff-Dränelemente, Geotextilien zum Filtern und Trennen, eine vorläufige Richtlinie für Bewehrungsgitter aus Kunststoff und eine Richtlinie über Anforderungen an Verlegefachbetriebe, die von seinen Arbeitsgruppen vorbereitet worden waren und somit die Grundlage für die Zulassungstätigkeit bilden. Den vorläufigen Charakter hat die Richtlinie für Bewehrungsgitter deshalb, weil bestimmte technische Fragen noch nicht abschließend geklärt werden konnten. Daran wird weiter gearbeitet. Der Beschluss über die Richtlinie für Dichtungskontrollsysteme steht ebenfalls bevor. In diesem Beitrag wird kurz über wesentliche Anforderungen und Zulassungsvoraussetzungen berichtet. Die Novellierung der Deponieverordnung vom 17.10.2011 berührt die Vorschriften für die Zulassung durch die BAM nicht. Sie erweitert jedoch die Art und Weise, wie ein Eignungsnachweis gegenüber der zuständigen Behörde als gleichwertig zur Zulassung durch die BAM geführt werden könnte. Es geht dabei um CE-Kennzeichnungen und um ausländische Produkte aus dem Europäischen Wirtschaftsraum. T2 - 8. Leipziger Deponiefachtagung - Planung, Bau, Betrieb, Stolllegung, Nachsorge, Nachnutzung und Rückbau von Deponien CY - Leipzig, Deutschland DA - 28.02.2012 PY - 2012 SP - 37 EP - 49 AN - OPUS4-25556 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simon, Franz-Georg A1 - Kalbe, Ute A1 - Adam, Christian A1 - Adamczyk, Burkart A1 - Weimann, Karin T1 - Recovery of non-renewable resources from waste T2 - 7th International Conference on EcoBalance CY - Tsukuba, Japan DA - 2006-11-14 KW - Natural resources KW - Thermo-chemical treatment KW - Waste management KW - Sewage sludge KW - Aggregetes PY - 2006 IS - E2-4 SP - 499 EP - 502 PB - The Society of Non-Traditional Technology CY - Tsukuba, Japan AN - OPUS4-14115 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Stephan, Ina T1 - International Biodeterioration Research Group - Functional Fluids Working Party (WP) - Annual Report 2003 KW - Metal working fluid KW - Lithographic fount solutions KW - Methodology KW - Laboratory test PY - 2004 SP - 1 EP - 2 PB - International Biodeterioration Research Group CY - Hampshire, UK AN - OPUS4-7601 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Oliver A1 - Adam, Christian T1 - Use of secondary phosphates to reduce soil pollution N2 - Phosphorous is essential for all living creatures and indispensable in its functions regarding bone structure, energy metabolism, and storage and expression of genetic information. It is removed from the soils through farming and husbandry and has to be replaced. Annually, more than 17 million tons of phosphorous are applied to soils in the form of mineral fertilizer worldwide (Killiches, 2013). In Germany, this accounts for 150,000 t/a. This fertilizer is produced from rock phosphate, which is often contaminated with heavy metals (Dissanayake et al., 2009), especially cadmium and uranium. Cd concentrations are around 30 mg/kg, U around 100 mg/kg, with even higher peak values. Since rock phosphate is treated with acids to make the phosphorous bioavailable, those heavy metals were also mobilized. When the fertilizer is applied to the farmland, the contaminants can pollute the soil and pose an environmental risk. Sewage sludge is another phosphorous source for farming. In Germany, 15,000 t/a phosphorous are applied to farmlands this way. However, there is a growing concern of possible environmental hazards since sewage sludge contains not only inorganic contaminants but also organic pollutants, especially pharmaceuticals and personal care products (Guardia et al., 2004). T2 - 4th International conference on environmental pollution and remediation CY - Prague, Czech Republic DA - 11.08.2014 PY - 2014 SP - Paper 136-1 EP - 136-2 AN - OPUS4-33432 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schoknecht, Ute A1 - Plarre, Rüdiger A1 - Stephan, Ina ED - Lang, A. ED - Zimmer, J. T1 - Einführung in die biologische Wirksamkeitsprüfung von Bioziden im Materialschutz KW - Biozide KW - Materialschutz KW - Wirksamkeitsprüfung KW - Biocide KW - Material preservation KW - Efficiency test PY - 2015 SN - 9783861021940 SP - 48 EP - 50 PB - Deutsches Historisches Museum CY - Berlin AN - OPUS4-35411 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hoffmann, Heike A1 - Stephan, Ina A1 - Schwibbert, Karin ED - Bismayer, U. ED - Schleicher, H. T1 - Auswirkung von Bioziden auf die Bakterienpopulation im Boden T2 - 80. Jahrestagung der Deutschen Mineralogischen Gesellschaft CY - Hamburg, Deutschland DA - 2002-09-08 PY - 2002 N1 - Geburtsname von Schwibbert, Karin: Göller, K. - Birth name of Schwibbert, Karin: Göller, K. VL - 14 IS - 1 SP - 72 CY - Hamburg AN - OPUS4-2540 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Noll, Matthias A1 - Stephan, Ina T1 - Seasonal shifts of fungal community structure at the interface of treated or untreated wood and soil T2 - 41st Annual meeting of the international research group on wood protection CY - Biarritz, France DA - 2010-05-09 KW - Fungal community KW - Chromated-copper-arsenate wood preservative (CCA) KW - Soil contact KW - Field test PY - 2010 IS - IRG/WP 10-10721 SP - 1 EP - 10 CY - Stockholm, Sweden AN - OPUS4-21329 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stephan, Ina A1 - Heidrich, Gabriele A1 - Stegemann, A. T1 - Isolation of soil borne bacteria and fungi from treated timber N2 - Most research in the last few decades has focused on the development of new strategies to control biological attack and the means to quantify this. Comparatively little work has been done to examine the effect that treated timber might have on its surrounding environment. This presentation will describe a methodology that attempts to detect any changes which might occur in the soil microflora following the introduction of timber treated with a number of chemical agents containing organic active ingredients (a.i.). It was also the purpose to isolate organisms that can break down organic a.i.. A technique was developed to determine whether the presence and nature of a timber preservative influenced the size and composition of a microbial population that colonised timber when buried in soil. Samples of treated timber were incubated in a solution eluted from soil that contained a diverse, viable microbial population. After incubation, the size and composition of the microflora both in the eluate and adhering to the timber was examined. T2 - 32nd Annual meeting of IRG, The International Research Group on Wood Preservation CY - Nara, Japan DA - 2001-05-20 KW - Wood preservatives KW - Organic active ingredients KW - Isolation method KW - Soil microorganisms KW - Environmental impact KW - Biodegradation PY - 2001 UR - http://www.irg-wp.com/irgdocs/details.aspx?id=631b6758-939a-43fd-bd68-dea2a2b7cc46 IS - 50174 PB - IRG Secretariat CY - Stockholm AN - OPUS4-1198 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ante, A. A1 - Trumpler, A. A1 - Niermann, S. A1 - Decker, R. A1 - Herrmann, L. A1 - Adam, Christian T1 - SUSAN - Sustainable and safe re-use of municipal sewage sludge for nutrient recovery - Large scale considerations of the thermo-chemical heavy metal removal from sewage sludge for the safe recycle of phosphorus T2 - Bremer Colloquium - Produktionsintegrierte Wasser-/Abwassertechnik - "Abwasser als Ressource" Kreislaufschließung, Energie- und Wertstoffrückgewinnung CY - Bremen, Germany DA - 2009-09-28 KW - Sewage sludge KW - Phosphorus KW - Recycling KW - Thermochemical treatment PY - 2009 SP - 1 EP - 14(?) AN - OPUS4-22183 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Leithoff, H. A1 - Stephan, Ina A1 - Lenz, M.T. A1 - Peek, R.-D. T1 - Growth of the Copper Tolerant Brown Rot Fungus Antrodia vaillantii on Different Substrates T2 - Annual Meeting of the International Research Group on Wood Preservation CY - Helsingör, Denmark DA - 1995-06-11 KW - Antrodia vaillantii KW - Copper tolerance KW - Growth behaviour PY - 1995 SP - 10 pages PB - International Research Group on Wood Preservation CY - Stockholm AN - OPUS4-4450 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wöhlecke, Andreas A1 - Müller, Werner T1 - The behaviour of HDPE geomembranes and installation quality control in geotechnical application N2 - The German Landfill Ordinance regulates the use of geosynthetics and other materials in the field of waste Containment Systems. It requires a certification of the geosynthetics by the BAM. The certification-guidelines define the state of the art by giving detailed requirements and specifications i the various geosynthetic products used in landfill constructions. According to the German Landfill Ordinance geosynthetic products have to fulfil their function for more than 100 years. Beyond, supported by an advisory board of landfill experts, BAM has developed installation requirements and demands on quality management for production, installation and third party control. The BAM is responsible to define tests and testing criteria for geosynthetics, to include provisions into the certification document and in addition to stipulate requirements with regard to installation procedure and quality management in Germany. All documents of the BAM such as certification guidelines, recommendations and testing specifications which are approved by the advisory board are published in German language on the website and in the Official Gazette*** of the BAM. For the certification one of the basic requirements is that the geosynthetic product is produced with well defined and well reproducible properties. Thus, a sophisticated quality management System is needed. In addition, not only production control, but also a quality assurance for the installation is necessary. T2 - International Symposium Geosynthetics India 2013 and seminar on geosynthetic barriers CY - New Delhi, India DA - 23.10.2013 PY - 2013 SP - 29 EP - 39 AN - OPUS4-29694 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Habibimarkani, Heydar A1 - Prinz, Carsten A1 - Sahre, Mario A1 - Hodoroaba, Vasile-Dan A1 - Radnik, Jörg T1 - CV, TEM, XRD and XPS/HAXPES datasets of FeNi-based nanoparticles for the oxygen evolution reaction N2 - The datasets from Cyclic Voltammetry, Transmision Electron Microscopy, X-ray Diffraction, and (Hard Energy) X-ray Photoelectron Spectroscopy are related to the publication H. Habibimarkani, S.-L. Abram, A. Guilherme Buzanich, C. Prinz, M. Sahre, V.-D. Hodoroaba and J. Radnik "In-depth analysis of FeNi-based nanoparticles for the oxygen evolution reaction" Scientific Reports (2025), https://doi.org/10.1038/s41598-025-92720-3 Details of the materials and the experimental procedures are described in this publications. KW - Oxygen evolution reaction KW - Fe-Ni nanopartices KW - Comprehensive analysis PY - 2025 DO - https://doi.org/10.5281/zenodo.14975964 PB - Zenodo CY - Geneva AN - OPUS4-63335 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Rieck, Arielle A1 - Low, Jian Liang A1 - Dietzmann, Simon A1 - Radnik, Jörg A1 - Teimouri, Zahra A1 - Higgins, Drew A1 - Hodoroaba, Vasile-Dan A1 - Mehmood, Asad A1 - Fellinger, Tim-Patrick T1 - Understanding the Activity Trade-Off between Tetrapyrrolic Fe-NCs and Co-NCs in the Alkaline Oxygen Reduction Reaction N2 - A water-free ionothermal synthesis of porous magnesium-imprinted nitrogen-doped carbon (Mg–NC) materials is introduced to prepare a platform material to investigate electrocatalytic structure-performance relations. Atomically dispersed Co- and Fe-NCs isomorphic to the pristine Mg-NCs are prepared by ion-exchange reactions. The current Mg-templating strategy enables relatively high pyrolysis product yields of up to 50 wt% and resultant Fe-NC and Co-NC catalysts contain high and comparable active metal loading of up to 2.52 wt% Fe and 2.29 wt% Co, respectively. A combination of X-ray spectroscopies with DFT studies reveals a tetrapyrrolic structure of the coordination sites, originating from a pyrolytic magnesium template ion reaction within the ionothermal synthesis. Two sets of highly active isomorphic tetrapyrrolic Fe-NCs and Co-NCs are utilized to understand the differences in intrinsic electrocatalytic performance of Co-NCs and Fe-NCs towards the alkaline oxygen reduction reaction (ORR). Despite their superior valence electronic properties to facilitate the initial outer-sphere electron transfer to O2, Co-NCs show significantly lower performance than Fe-NC with comparable loading. Although the generally discussed weaker binding of peroxide intermediates to CoN4 sites compared to FeN4 sites is evident, experimental and theoretical investigation reveal that it is the underlying peroxide oxidation activity that suppresses the oxygen reduction activity of M-NCs. The high peroxide oxidation activity of Co-NCs explains their reduced alkaline ORR relative to Fe-NCs, shedding light on the understated significance of controlling peroxide chemistry for the optimizing cathodic performance. KW - Magnesium Imprinting KW - Tetrapyrrolic Sites KW - Metal- and nitrogen-doped carbon (M-N-C) KW - Oxygen Reduction Reaction (ORR) KW - Nitrogen doped Carbon PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-651487 DO - https://doi.org/10.26434/chemrxiv-2025-s59s5 SP - 1 EP - 24 AN - OPUS4-65148 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pauw, Brian Richard A1 - Smales, Glen Jacob T1 - Raw and processed X-ray scattering datasets for: "Entering a new dimension in powder processing for advanced ceramics shaping" N2 - This dataset is a complete set of raw, processed and analyzed data, associated with the manuscript mentioned in the title. All associated metadata and processing history has been added. Particle size distribution analyses using McSAS are included as well. The samples consisted of a 4.2 mass% dispersion of yttria-stabilized zirconia nanoparticles in a cross-linked matrix. The measurements show a good dispersion with minimal agglomeration. The wide-angle region shows diffraction information consistent with zirconia. KW - X-ray scattering KW - Nanocomposite KW - Ceramic microprinting KW - Yttria-stabilized zirconia KW - SAXS KW - Nanomaterials KW - Two-photon polymerization KW - Transparency KW - Mechanical testing PY - 2023 DO - https://doi.org/10.5281/zenodo.7498647 PB - Zenodo CY - Geneva AN - OPUS4-56766 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Fritzsche, Sven A1 - Pauw, Brian Richard A1 - Weimann, Christiane A1 - Sturm, Heinz T1 - Test artifact for fs-LDW N2 - Data to generate the given graphs in the publication as well as raw images of the shown images. KW - stl code KW - Images KW - Graphs KW - Data PY - 2023 DO - https://doi.org/10.5281/zenodo.7671945 PB - Zenodo CY - Geneva AN - OPUS4-58096 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wöhlecke, Andreas ED - Egloffstein, Thomas ED - Burkhardt, Gerd T1 - Zum Spannungsrissverhalten von PE-HD Kunststoffdichtungsbahnen und zu aktuellen Themen aus dem Fachbeirat der BAM N2 - Kunststoffdichtungsbahnen (KDB) aus PE-HD (Polyethylen hoher Dichte) werden häufig zur Abdichtung von Bauwerken in der Geotechnik verwendet. Diese Produkte werden aus einem Kunststoff mit relativ komplexer Zusammensetzung hergestellt. Um eine Aussage über die Haltbarkeit von KDB aus PE-HD treffen zu können, muss das Materialverhalten berücksichtigt werden. In diesem Zusammenhang sind die wichtigsten Aspekte der Dauerhaftigkeit die Spannungsrissbeständigkeit und die Beständigkeit gegen Oxidation. Verschiedene PE-Sorten weisen eine unterschiedliche Spannungsrissbeständigkeit auf. Um dieser Eigenschaft von PE-HD zu begegnen, werden nur KDB aus sehr hochwertigen Rohstoffen zugelassen. Auf der anderen Seite werden hohe Anforderungen an die umgebenden Schichten, wie Auflager und Schutzschicht gestellt, um möglichst geringe Spannungen zu erzeugen und damit Dehnungen die Dehnungen der KDB gering zu halten. Bestimmte Medien, die bei den betreffenden Prüfungen verwendet werden, dürfen nicht mehr in der EU in Verkehr gebracht werden. Im Folgenden sollen die Zusammenhänge in Kürze dargestellt werden. Darüber hinaus sollen Diskussionen und Änderungen im Zusammenhang mit der Zulassungsrichtlinie für KDB vorgestellt werden. Der aktuelle Stand der Diskussion im Zusammenhang mit den verwendeten Tensiden in Bezug auf die Spannungsrissprüfung und weiterer Prüfungen wird aufgezeigt. Änderungen der Fremdprüfung von sogenannten Sandschutzmatten, des Standards zur Qualitätsüberwachung (SQÜ) von Kunststoff Dränelementen (KDE) und der Anpassung der Formulierungen zum Überbau der in Abdichtungen verwendeten Produkte werden in Kürze aufgezeigt. T2 - Karlsruher Deponie- und Altlastenseminar 2023 CY - Karlsruhe, Germany DA - 18.10.2023 KW - Spannungsrissbeständigkeit KW - Deponie KW - Kunststoffdichtungsbahn PY - 2023 SN - 978-3-939662-33-4 VL - 44 SP - 17 PB - ICP Eigenverlag Bauen und Umwelt CY - Karlsruhe AN - OPUS4-58633 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sichler, Theresa A1 - Adam, Christian A1 - Montag, D. A1 - Ehm, J.H. T1 - Schwankungen der P-Gehalte in Klärschlämmen im Kontext der Klärschlammverordnung N2 - Ab 2029 gilt für alle Kläranlagen in Deutschland eine Pflicht zur Rückgewinnung von Phosphor (P) aus Klärschlamm. Ausgenommen sind nur Anlagen mit Schlämmen mit weniger als 20 g P/kg bezogen auf die Trockenmasse (TM). Für eine Überprüfung der Phosphorschwankungen im Klärschlamm wurden neun verschiedene Kläranlagen ausgewählt mit Phosphorgehalten nahe der "Rückgewinnungsgrenze" von 20 g/kg TM. Der entwässerte Klärschlamm dieser Anlagen wurde monatlich beprobt und auf seinen Phosphorgehalt geprüft. Die Phosphorschwankungen betrugen je nach Anlage zwischen 4 % und 13 % (relative Standardabweichung), im Mittel rund 7 %. T2 - KlärschlammTage CY - Online Meeting DA - 09.06.2021 KW - Phosphor KW - Klärschlamm KW - Phosphorrückgewinnung KW - Abwasserbehandlung KW - Klärschlammverordnung PY - 2021 SP - 102 EP - 108 PB - Deutsche Vereinigung für Wasserwirtschaft, Abwasser und Abfall e. V. (DWA) CY - Hennef AN - OPUS4-52839 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sichler, Theresa A1 - Adam, Christian A1 - Montag, D. A1 - Barjenbruch, M. ED - Holm, O. ED - Quicker, P. ED - Kopp-Assenmacher, S. T1 - Nährstoffrückgewinnung aus Klärschlamm: Eine Betrachtung zukünftiger Verwertungsszenarien für Deutschland N2 - Agricultural sewage sludge utilization becomes less important in Germany. In 2017, new fertilizer and waste laws caused the agricultural sewage sludge utilization to collapse by more than a quarter. From 2029, in German wastewater treatment plants (WWTPs) phosphorus (P) must be recovered from sewage sludge ifit contains more than 2 wt % P. Agricultural utilization will be prohibited for large WWTPs > 100,000 population equivalents (pe) from 2029 and > 50,000 pe from 2032. In Germany, each federal state must annually report amounts and quality of agriculturally utilized sewage sludge which was 17 % of the total disposal in 2019. The reports of 10 States were evaluated for 2016 and 2017 representing approx. 60 % ofthe total agriculturally used sludge volume. Whereas phosphorus recovery is mandatory this does not apply to other nutrients. However, many P recovery processes recover other nutrients, too. Considering three differentscenariosfor future German sewage sludge disposal Shows that 70 - 77 % ofthe P load in sewage sludge will probably be recovered in the future. At the same time, this applies for about 0 - 16 % of nitrogen, 36 - 52 % of calcium, 31-53 % of potassium, and 40 - 52 % of magnesium. However, these recovered nutrient loads can substitute only 1 % or less ofthe commercial fertilizer demand except from phosphorus which is about 45 % ofthe demand. T2 - Berliner Klärschlammkonferenz CY - Berlin, Germany DA - 15.11.2021 KW - Phosphor KW - Klärschlamm KW - Phosphorrückgewinnung KW - Landwirtschaftliche Klärschlammverwertung KW - Klärschlammverordnung PY - 2021 SN - 978-3-944310-56-5 VL - 4 SP - 252 EP - 265 PB - Thomé-Kozmiensky-Verlag GmbH CY - Neuruppin AN - OPUS4-54117 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Werner A1 - Jakob, Ines A1 - Robertson, Daniela A1 - Tatzky-Gerth, Renate A1 - Wöhlecke, Andreas T1 - Die oxidative Alterung von Geokunststoffen aus Polyethylen und Polypropylen N2 - Geokunststoffe aus Polyethylen (PE) oder Polypropylen (PP) müssen mit Antioxidantien (AO) stabilisiert werden, damit sie die für die Anwendung in der Geotechnik erforderliche Lebensdauer erreichen. Die Lebensdauer ist dann aber nicht durch die Empfindlichkeit des Polymers gegen Oxidation, sondern durch den Verlust der AO im Laufe der Zeit bedingt. AO können durch den Verbrauch bei Oxidationsreaktionen, durch den Abbau im Polymer, durch die Wanderung an dessen Oberfläche, durch den Abbau auf der Oberfläche, schließlich durch Abdampfen von der Oberfläche oder durch sich Lösen in einem umgebenden flüssigen Medium verloren gehen. Bei den Geokunststoffen aus PP und PE wie auch bei anderen polyolefinen Kunststoffprodukten findet man häufig zwei bestimmte „Pakete“ aus Antioxidantien: (1) eine Kombination von Substanzen aus bestimmten Klassen von sterisch gehinderten Phenolen und Phosphiten und (2) eine Substanz aus der Klasse der sterisch gehinderten Amine (HAS) in Verbindung mit einer geringfügigen phenolischen und phosphitischen Verarbeitungsstabilisierung der Formmasse. Der Verlust der AO wie auch der oxidative Abbau der mechanischen Eigenschaften des Geokunststoffs verläuft ganz unterschiedlich, je nachdem mit welchem Paket stabilisiert wurde. Diese Unterschiede werden im Rahmen eines „3-Stadien-Modells“ diskutiert. Stadium A: die Antioxidantien gehen verloren. Stadium B: die Oxidation läuft langsam an. Stadium C: die Oxidation wirkt sich mehr oder weniger drastisch auf die Produkteigenschaften aus. Dabei zeigt sich, dass das Modell nur auf das Paket 1 anwendbar ist. Im Falle des Pakets 2 findet in gewissem Umfang schon im Stadium A ein oxidativer Abbau statt, ln beiden Fällen ist es aber die AO-Verlustzeit die eigentlich die Lebensdauer bestimmt. Es werden dann Abschätzungen der Lebensdauer von PEHDDichtungsbahnen und von PP-Vliesstoffen gegeben. Die Prüfung und Bewertung der oxidativen Beständigkeit muss die Eigenart der Wirkung und des Verlusts unterschiedlicher Stabilisierungen berücksichtigen. Vor diesem Hintergrund wird die Hochdruck-Autoklav-Prüfung beurteilt. Es werden die Besonderheiten dieser Prüfmethode aufgezeigt, die sich jeweils bei der Anwendung auf Produkte ergeben, die entweder mit dem Paket 1 oder dem Paket 2 stabilisiert wurden. Eine Vorhersage der Lebensdauer unter Anwendungsbedingungen aus den Ergebnissen der Autoklav-Prüfung ist sehr schwierig und vermutlich nur in bestimmten Fällen überhaupt möglich. Ähnliches gilt auch für die vergleichende Bewertung der oxidativen Beständigkeit von Produkten. T2 - Fachtagung Nutzungsdauer von Rohren und Geokunststoffen aus Polyolefinen CY - Würzburg, Germany DA - 14.11.2013 KW - Geokunststoffe KW - PE KW - PP KW - Oxidative Alterung PY - 2013 SP - 1 EP - 48 PB - SKZ - Das Kunststoff-Zentrum CY - Würzburg AN - OPUS4-29606 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Werner A1 - Wöhlecke, Andreas T1 - Quo vadis Geokunststoffe? CE-Kennzeichnung und BAM-Zulassung T2 - 31. Fachtagung - Die sichere Deponie - Sicherung von Deponien und Altlasten mit Kunststoffen CY - Würzburg, Germany DA - 2015-02-03 KW - Europäische Normen KW - CE-Kennzeichnung KW - BAM-Zulassung KW - Deponieverordnung KW - Bauproduktenverordnung PY - 2015 SP - 43 EP - 55 AN - OPUS4-32567 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Leithoff, H. A1 - Stephan, Ina A1 - Härtner, H. T1 - Suitability of cotton strip testing as a screening method for the development of wood preservative formulations T2 - 34th Annual Meeting of the International Research Group on Wood Preservation CY - Brisbane, Australia DA - 2003-05-18 KW - Screening method KW - Efficacy testing KW - Soft rot KW - ENV 807 KW - Field test PY - 2003 IS - IRG-WP 03-20270 SP - 1(?) EP - 8(?) PB - International Research Group on Wood Preservation CY - Stockholm AN - OPUS4-4445 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sierra-Alvarez, R. A1 - Le Bayon, I. A1 - Carey, J. A1 - Stephan, Ina A1 - van Acker, J. A1 - Grinda, Manfred A1 - Kleist, G. A1 - Militz, H. A1 - Peek, R.-D. T1 - Laboratory Testing of Wood Natural Durability in Soil-Bed Assay T2 - 29th Annual Meeting of the International Research Group on Wood Preservation CY - Maastricht, Netherlands DA - 1998-06-14 KW - Wood KW - Fungal decay KW - Soft rot fungi KW - Natural durability KW - Test method KW - Soil exposure KW - Mass loss KW - Static bending PY - 1998 SP - Paper IRG/WP 98-20141, 1-15 PB - International Research Group on Wood Preservation CY - Stockholm AN - OPUS4-4453 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Hahn, Marc Benjamin A1 - Sturm, Heinz A1 - Bier, F A1 - Solomun, Tihomir T1 - Biologische Konsequenzen einer nanoskaligen Energiedeposition: Fokussierung auf die Rolle niederenergetischer Elektronen T1 - Biological Consequence of Nanoscale Energy Deposition: Focusing on the Role of Low-Energy Electrons N2 - Bei der Behandlung von Krebs mittels Strahlentherapie sollen Tumorzellen abgetötet werden ohne das umliegende gesunde Gewebe zu zerstören. Um Strahlentherapien für Patienten verträglicher zu machen, ist ein besseres Verständnis der zugrundeliegenden Prozesse auf der molekularen Ebene nötig. Dabei sind der Energieeintrag und die Streuprozesse der Strahlung in der Umgebung der DNA von besonderem Interesse. Durch Streuung von hochenergetischer Strahlung in Wasser werden besonders viele Sekundärelektronen mit niedriger Energie erzeugt. Zur Untersuchung der Schädigungseffizienz dieser Elektronen wurde ein Verfahren zur direkten Bestrahlung von Lösungen mittels Elektronen variabler Energien enwtickelt. Dies wurde durch einen neu entwickelten Probenhalter mit einer für Elektronen durchlässigen Nanomembran ermöglicht. Mit diesem können Bestrahlungen an DNA, Proteinen, und Zellen bei verschiedenen pH-Werten oder Salzkonzentrationen durchgeführt werden. Parallel dazu wurde der ortsabhängige Energieeintrag innerhalb des Wassers durch Elektronenstreusimulationen bestimmt. Diese neuartige Kombination von Experiment und Simulation ermöglicht die Bestimmung der Schaden-Dosis-Relation für Elektronenbestrahlung von biologischen Systemen unter realistischen physiologischen Bedingungen. So konnten für die genutzten Primärelektronen wie die mittlere letale Dosis, bei der 50 Prozent der DNA geschädigt sind, mit 1,7 Gy bestimmt. Ebenfalls wurde das für mikrodosimetrische Modellierungen und Betrachtungen der sogenannten Linear energy transfer (LET) Effekte, wichtige Verhältnis von DNA Einzelstrangbrüchen (SSB) zu Doppelstrangbrüchen (DSB) als SSB/DSB = 12/1 bestimmt. Mit Hilfe eines Modells für das Targetvolumen der DNA wurde der mittlere mikroskopische letale Energieeintrag berechnet als E1/2 = 6 ± 4 eV . Es wurde gefolgert, dass weniger als zwei Ionisationsprozesse im sensitiven Targetvolumen der DNA im Mittel zu einem Einzelstrangbruch führen. Diese Methode ist unabhängig von den Primärpartikel und geometrischen Bedingungen. Deshalb ermöglicht sie die Vergleichbarkeit experimenteller Systeme mit inhomogenen Energieverteilungen, welches sonst nicht gegeben ist. Des weiteren wurden die Strahlenschutzfunktionen des Zellschutzmoleküls Ectoines und sein Einfluss auf Wasser und Biomoleküle untersucht. Seine Schutzfunktion gegen ionisierende Strahlung wurde auf die Erhöhung des Streuquerschnitts niederenergetischer Elektronen und seine Eigenschaft als OH-Radikalfänger zurückgeführt. Aufbauend auf unseren Erkenntnissen finden in klinischen Arbeitsgruppen Untersuchungen zu Einsatzmöglichkeiten im Umfeld der Strahlentherapie statt. Projektkennung Deutsche Forschungsgemeinschaft (DFG) - Projektnummer 245767821 N2 - To cure cancer radiation therapy is used to kill tumor cells. It is based on radiation induced damage to biomolecules. Here DNA damage is of key interest due to its central role in apoptosis and mutation. Because of the high amount of water in biological tissue, most of the damage is caused by the secondary particles produced by the inelastic scattering of ionizing radiation and water. A detailed understanding of the underlying molecular processes under physiological conditions is the prerequisite to develop more efficient the-rapies. Therefore irradiations have to be performed in liquid, under consideration of the chemical environment. To make it possible to irradiate liquids with electrons within scanning electron microscopes a new sample holder was constructed incorporating an electron transparent nanomembrane. It makes it possible to irradiate DNA, proteins or cells at different pH and salinity. The median lethal dose for a model system of plasmid DNA and water was determined by the combination of experimental data, particle scattering simulations (Geant4-DNA) and diffusion calculations as D1/2 = 1.7 ± 0.3 Gy. From the convolution of plasmid positions and the spatially resolved energy deposit, as determined by electron scattering simulations, the histogram of the energy deposit within the target volume of the plasmids and the microscopic median lethal energy deposit was calculated as E1/2 = 6 ± 4 eV . It could be deduced, that on average less than two ionization Events are sufficient to cause a single-strand-break. The relation of single-strand-breaks (SSB) to double-strand-breaks (DSB), which is of importance for microdosimetric modeling, was determined as SSB : DSB = 12 : 1. The presented method for the Determination of microscopic dose-damage relations was further extended to be applicable for General irradiation experiments. It is independent of the type of primary radiation used, the experimental geometry, and the diffusional properties of the molecules under investigation. This way different experimental systems with varying, inhomogeneous energy deposit characteristics become comparable with each other, which is not possible when only macroscopic averaged values are taken into account. In addition, the radiation protection properties of the compatible solute Ectoine was investigated. The protective properties of ectoine result from the increase of the inelastic scattering probabilities of low Energy electrons at the acoustic vibrational modes of water and its properties as OH-radical scavenger. Based on our results, further investigations are conducted to evaluate the application of Ectoine in the context of radiation therapy. Projektkennung Deutsche Forschungsgemeinschaft (DFG) - Projektnummer 245767821 KW - Ectoin KW - Ectoine KW - DNS KW - DNA KW - Cancer therapy KW - DNA damage KW - DNA radiation damage KW - Dosimetry KW - DFG KW - Electron irradiation KW - Ectoine DNA interaction KW - Ectoine radiation protection KW - Hydroxyl radicals KW - OH radicals KW - LEE KW - Low energy electrons KW - Microdosimetry KW - Radiation KW - Geant4 KW - Geant4-DNA KW - Radiation therapy KW - LET PY - 2021 UR - https://gepris.dfg.de/gepris/projekt/245767821/ergebnisse?context=projekt&task=showDetail&id=245767821&selectedSubTab=2& SP - 1 EP - 14 AN - OPUS4-52389 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wöhlecke, Andreas ED - Al-Akel, S. T1 - Aktuelle Diskussion aus dem Fachbeirat der BAM N2 - Das Jahr 2020 war vor allen Dingen von der Pandemie geprägt, die alle Bereiche des Lebens und Arbeitens beeinflusst hat und immer noch beeinflusst. Dies hat sich auch auf verschiedene Maßnahmen im Zusammenhang mit zugelassenen Produkten ausgewirkt. In diesem Zusammenhang sollen die Punkte kurz aufgeführt werden. Des Weiteren soll aufgezeigt werden, wie bei der Bearbeitung der Richtlinien, der Zulassungstätigkeit und Beurteilung der Produkte an der BAM und im Fachbeirat vorgegangen wird. Darüber hinaus soll noch einmal kurz auf die Entlassung aus der Nachsorgephase eingegangen werden. Am Ende sollen verschiedene aktuelle Fragestellungen des Fachbeirat aufgezeigt werden. T2 - 17. Leipziger Deponiefachtagung CY - Online meeting DA - 02.03.2021 KW - Deponie KW - Geokunststoffe KW - Kunststoffdichtungsbahn PY - 2021 SN - 978-3-943443-50-9 VL - 17. SP - 31 CY - Leipzig AN - OPUS4-52212 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wöhlecke, Andreas A1 - Müller, Werner T1 - Geosynthetics and their certification for landfill liner and capping systems in Germany N2 - This paper informs about the BAM Federal Institute of Materials Research and Testing certification procedure for geosynthetics used for landfill liner and capping Systems in Germany. The German Landfill Ordinance regulates the use of geosynthetics and other materials in the field of waste Containment Systems. It requires such a certification by the BAM. The certification-guidelines of the BAM define the state of the art by giving detailed requirements and specifications for the various geosynthetic products. According to the German Landfill Ordinance geosynthetic products have to fulfil their function for more than WOyears. Beyond, supported by an advisory board of landfill experts, BAM has developed installation requirements and demands on quality management for production, installation and third party control. The paper describes some of the requirements for products, installation and quality assurance. Some remarks on on-going discussions with respect to special topics of product behaviour are made. T2 - 5th International conference geosynthetics Middle East 2012 CY - Abu Dhabi, UAE DA - 19.11.2012 PY - 2012 IS - Chapter 15 SP - 173 EP - 184 CY - Würzburg AN - OPUS4-27784 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Werner A1 - Wöhlecke, Andreas T1 - Voraussetzungen für die Zulassung von Geokunststoffen (insbesondere Bewehrungsgittern) für Deponieabdichtungen N2 - Der Fachbeirat beschloss im vergangenen Jahr Zulassungsrichtlinien für Kunststoffdichtungsbahnen, Schutzschichten, Kunststoff-Dränelemente und Geotextilien zum Filtern und Trennen und eine Richtlinie über Anforderungen an Verlegefachbetriebe, die von seinen Arbeitsgruppen vorbereitet worden waren, und nunmehr die Grundlage für die Zulassungstätigkeit bilden. In diesem Beitrag wird im Anschluss an die Ausführungen auf der letzten Fachtagung kurz über wesentliche Anforderungen und Zulassungsvoraussetzungen berichtet. Noch nicht verabschiedet sind die Richtlinien für Dichtungskontrollsysteme und Bewehrungsgitter aus Kunststoff. Auf den Diskussionsstand bei den Anforderungen an die Bewehrungsgitter wird etwas ausführlicher eingegangen, da sich neben den materialtechnischen auch bemessungstechnische Probleme ergeben. T2 - 27. Fachtagung - Die sichere Deponie - Sicherung von Deponien und Altlasten mit Kunststoffen CY - Würzburg, Germany DA - 24.02.2011 KW - Deponieverordnung KW - Zulassung KW - Geokunststoffe KW - Bewehrungsgitter aus Kunststoff PY - 2011 IS - Kap. B SP - 1 EP - 23 CY - Würzburg AN - OPUS4-23305 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Adam, Christian A1 - Kley, Gerd A1 - Simon, Franz-Georg A1 - Lehmann, Annekatrin ED - Filibeli, A. ED - F. Dilek Sanin, ED - Ayol, A. ED - Selim L. Sanin, T1 - Recovery of nutrients from sewage sludge - Results of the European research-project SUSAN T2 - IWA-Specialist Conference "Facing Sludge Diversities: Challenges, Risks and Opportunities" CY - Antalya, Turkey DA - 2007-03-28 KW - Phosphorus recovery KW - Sewage sludge ash KW - Thermo-chemical treatment KW - Fertiliser PY - 2007 N1 - Serientitel: Journal of environmental science and health : Part A, Toxic/hazardous substances & environmental engineering – Series title: Journal of environmental science and health : Part A, Toxic/hazardous substances & environmental engineering IS - 43.2008,13 SP - 297 EP - 305 PB - Taylor & Francis CY - Philadalphia, PA AN - OPUS4-16468 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wöhlecke, Andreas T1 - Aktuelle Themen aus dem Fachbeirat der BAM N2 - Die Anforderungen an Geokunststoffprodukte und deren Qualitätssicherung unterliegen einem stetigen Wandel, der sowohl durch technische Veränderungen als auch durch normative und organisatorische Entwicklungen geprägt ist. Insbesondere der Fachbeirat der BAM gemäß Deponieverordnung (DepV) spielt hier im Bereich der Deponietechnik eine wichtige Rolle. An dieser Stelle sollen aktuelle Themen aus dem Fachbeirat der BAM vorgestellt werden, die wesentliche Änderungen in der Zulassungs- und Anwendungspraxis betreffen. Der Beitrag beleuchtet unter anderem Veränderungen innerhalb der BAM, die Modernisierung der Publikationsformate sowie die fachliche Weiterentwicklung der Zulassungsrichtlinien. Besondere Aufmerksamkeit gilt der Diskussion um die Einbauhilfe im Schutzschichtsystem, der Einführung einer europäischen Zugversuchsnorm für Kunststoffdichtungsbahnen sowie der Fremdüberwachung der Produktion geosynthetischer Komponenten. Darüber hinaus werden neue Anforderungen an Edelstahlelektroden in Dichtungskontrollsystemen und die Spannungsrissbeständigkeit von PE-HD-Dichtungsbahnen thematisiert. T2 - 35. Karlsruher Deponie- und Altlastenseminar CY - Karlsruhe, Germany DA - 15.10.2025 KW - Deponie PY - 2025 VL - 48 SP - 26 EP - 35 PB - ICP AN - OPUS4-64408 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Wolfram A1 - Weba, Luciana A1 - Silbernagl, Dorothee A1 - Mota Gassó, Berta A1 - Höhne, Patrick A1 - Sturm, Heinz A1 - Pauli, Jutta A1 - Resch-Genger, Ute A1 - Steinborn, Gabriele ED - Khayat, Kamal Henry T1 - Influences of nano effects on the flow phenomena of self-compacting concrete N2 - Chemical admixtures like superplasticisers or stabilising agents are of ever increasing importance for modern concrete technology. They liberate the workability of concrete from its dependency on water content, and thus, open the gate towards innovative and future oriented concrete technologies such as selfcompacting concrete. Meanwhile admixtures have become common practice in concrete technology, but the understanding of these highly complex polymers in the entire concrete system lags far behind their application. Due to its complex time-dependent, multi-phase and multi-scale behaviour, flowable concrete systems are highly complicated and cannot be described comprehensively by simple models. It is therefore extremely challenging to identify the relevant parameters that predominantly control flow phenomena on different size scales, since these may occur on any scale between the nano scale (e.g. superplasticizer adsorption) and macro scale (e.g. grading of the aggregates). The present study discusses fundamental mechanisms at the interface between particle or hydrate surfaces and the fluid phase at a very early stage of concrete formation, and links these effects to macroscopic flow phenomena. Methods are discussed that appear promising interdisciplinary tools for enhancement of the understanding of the relevant interactions that are responsible for the macroscopic flow of flowable concrete. T2 - 8th International RILEM Symposium on Self-Compacting Concrete CY - Washington, D.C., USA DA - 15.05.2016 KW - Adsorption KW - Analytics KW - Hydration KW - Polycarboxylate ether KW - Rheology PY - 2016 SP - 245 EP - 254 AN - OPUS4-36882 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Leithoff, H. A1 - Stephan, Ina A1 - Peek, R.-D. T1 - Penetration as Key Factor for Determining the Performance of Wood Preservatives T2 - 35th Annual Meeting of the International Research Group on Wood Preservation CY - Ljubljana, Slovenia DA - 2004-06-06 KW - Penetration KW - Testing KW - Screening KW - Test fungi KW - Wood preservation KW - Performance KW - Fungi PY - 2004 SP - 13 pages PB - International Research Group on Wood Preservation CY - Stockholm AN - OPUS4-4444 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Werner A1 - Wöhlecke, Andreas ED - Jost, D. ED - Albers, K. T1 - Langzeitverhalten von Kunststoff-Dränelementen und Bewehrungsgittern und die Anforderungen der Deponieverordnung N2 - Ein Geokunststoffprodukt muss in einer Deponieabdichtung unter allen relevanten Einwirkungen seine Funktion mindestens 100 Jahre lang erfüllen. Diese Annahme ist nicht schon allein dann gerechtfertigt, wenn Alterungsuntersuchungen gezeigt haben, dass der verwendete Werkstoff voraussichtlich so lange halten wird. Darüber hinaus gehende Fragestellungen zur Funktionserfüllung, die im Zulassungsverfahren bearbeitet werden müssen, werden am Beispiel von Kunststoff-Dränelementen und Bewehrungsgittern diskutiert. Es geht dabei um die Auswirkung von äußeren Kräften, die über diesen sehr langen Zeitraum einwirken. Die Grenze für noch zulässige Druck- und Scherkräfte bei einem Kunststoff-Dränelement muss ausgelotet und das zugehörige Wasserableitvermögen bestimmt werden. Mögliche Einschränkung für den Herausziehwiderstand eines Bewehrungsgitters müssen abgeschätzt werden. Damit werden auch die Aufgaben zukünftiger Normungstätigkeit Umrissen. Ergänzend werden einige Erläuterungen zu aktuellen Entwicklungen gegeben: Eine neue Ausgabe der Fremdprüferrichtlinie wurde erarbeitet. Zulassungen für Bewehrungsgitter wurden erteilt. Schließlich wird kurz erklärt, was Befristung einer Zulassung, Erlöschen einer Zulassung und Widerruf einer Zulassung bedeuten. T2 - 29. Fachtagung - Die sichere Deponie - Sicherung von Deponien und Altlasten mit Kunststoffen CY - Würzburg, Germany DA - 31.01.2013 KW - Deponieverordnung KW - Zulassung KW - Kunststoff-Dränelemente KW - Bewehrungsgitter aus Kunststoff PY - 2013 SP - 1 EP - 18 CY - Würzburg AN - OPUS4-27705 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stephan, Ina T1 - Fungizide in Beschichtungen T2 - 2. Mykologisches Kolloquium "Pilze an Holz und Baustoffen Erkennen - Bewerten - Vermeiden" CY - Dresden, Deutschland DA - 2007-11-15 KW - Fungizid KW - Beschichtung KW - Biozid KW - Prüfung KW - Schimmelpilz KW - Ascomyceten KW - Normverfahren PY - 2007 SP - 1 EP - 3 AN - OPUS4-16266 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Adam, Christian A1 - Schick, J. A1 - Kratz, S. A1 - Hermann, L. T1 - Phosphorus recovery by thermochemical treatment of sewage sludge ash T2 - 5th IWA Leading-Edge Conference on Water and Wastewater Technologies CY - Zürich, Switzerland DA - 2008-06-01 KW - Phosphorus recovery KW - Sewage sludge ash KW - Thermochemical treatment KW - Fertiliser KW - Greenhouse pot experiments PY - 2008 SP - 1 EP - 10 PB - International Water Association (IWA) CY - London AN - OPUS4-17568 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Strangfeld, Christoph A1 - Prinz, Carsten A1 - Hase, F. A1 - Kruschwitz, Sabine T1 - Data of embedded humidity sensors, sample weights, and measured pore volume distribution for eight screed types N2 - Four cement-based and four calcium-sulphate-based screed types are investigated. The samples have a diameter of 300 mm and a height of 35 or 70 mm. Up to ten humidity sensors are embedded directly during the concreting of the screed samples. Thus, the humidity over the sample height is monitored during hardening, hydration, evaporation, and oven drying. Furthermore, the screed samples are weighted during every measurement to determine the total mass and the corresponding moisture loss. To define the pore system precisely, mercury intrusion porosimetry as well as gas adsorption is performed. According to the data, the entire pore volume distribution is known. The measured pore diameters range from 0.8 nm to 100 μm and the total porosity of the examined screeds ranges between 11 % and 22 %. Based on these measurement data, moisture transport, pore saturation as well as sorption isotherms and their hysteresis may be calculated quantitatively as described by Strangfeld et al. KW - Concrete and screed KW - Material moisture KW - Pore volume distribution KW - Embedded humidity sensors KW - Data in brief PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-448261 UR - https://data.4tu.nl/repository/uuid:d2ba436f-78c0-4105-8a1f-5422fcb37851 DO - https://doi.org/10.4121/uuid:d2ba436f-78c0-4105-8a1f-5422fcb37851 SP - 1 EP - 4 PB - 4TU.Centre for Research Data CY - Delft AN - OPUS4-44826 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stajanca, Pavol A1 - Mihai, L. A1 - Sporea, D. A1 - Negut, D. A1 - Sturm, Heinz A1 - Schukar, Marcus A1 - Krebber, Katerina ED - Webb, D. J. ED - Scully, P. ED - Sugden, K. T1 - Impacts of gamma irradiation on cytop plastic optical fibres N2 - Impact of gamma radiation on transmission of a commercial Cytop polymer optical fibre (Lucina, Asahi Glass Company) is investigated. Spectral dependence of radiation induced attenuation in the investigated fibre is measured in the VIS-NIR spectral region. Besides attenuation increase, radiation is found to increase fibre susceptibility to water as well. While pristine Cytop fibre is rather humidity insensitive, strong humidity related absorption in the NIR region is observed after fibre irradiation. Selective irradiation of separate fibre sections is proposed as a way of fibre humidity sensitization and quasi-distributed water detection is demonstrated using optical time domain reflectometry at 1310 nm. T2 - POF 2016: 25th International Conference on Plastic Optical Fibres CY - Birmingham, UK DA - 13.09.2016 KW - Polymer optical fibers KW - Cytop KW - Gamma radiation PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-403216 SN - 9781854494085 SP - 114 EP - 117 CY - Birmingham AN - OPUS4-40321 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Hahn, Marc Benjamin T1 - Quantifizierung der Schädigung von DNA in wässriger Lösung unter direkter Elektronenbestrahlung N2 - Bei der Behandlung von Krebs wird Strahlentherapie zur Zerstörung von Tumorzellen eingesetzt. Der zugrunde liegende Wirkmechanismus ist die durch ionisierende Strahlung verursachte Schädigung an Biomolekülen. Dabei kommt den Schädigungsprozessen an DNA aufgrund ihrer zentralen Rolle in Mutation und Zelltod eine besondere Bedeutung zu. Durch den hohen Wasseranteil in menschlichen Zellen findet ein Großteil der inelastischen Streuprozesse an Wassermolekülen statt und führt zur deren Radiolyse. Die so entstehenden Radiolyseprodukte sind für einen Großteil des Schadens an DNA verantwortlich. Ein detailliertes Verständnis der zugrunde liegenden molekularen Interaktion ist die Voraussetzung um effizientere Therapien zu entwickeln. Ziel dieser Arbeit ist es, die Schädigung von DNA durch ionisierende Strahlung in Abhängigkeit der inelastischen Streuevents und des Energieeintrags innerhalb des biologisch relevanten mikroskopischen Treffervolumens zu quantifizieren. Die Bestrahlungen müssen dazu in Flüssigkeit, unter Berücksichtigung der chemischen Umgebung durchgeführt werden, welche die indirekten Schäden vermittelt. Deshalb wurde eine neuartige Kombination aus Experiment und Monte- Carlo-Simulationen entworfen und angewandt. Um Elektronenbestrahlung flüssiger Lösungen innerhalb eines Rasterelektronenmikroskops zu ermöglichen, wurde ein Probenhalter mit einer für Elektronen durchlässigen Nanomembran entwickelt. So können Bestrahlungen an DNA, Proteinen, und Zellen bei verschiedenen pH-Werten, Salzkonzentrationen oder in Anwesenheit von Kosoluten durchgeführt werden. Für ein Modellsystem aus Plasmid-DNA in Wasser wurde damit die mittlere letale Dosis aus der Kombination der experimentellen Daten, Partikelstreusimulationen (Geant4-DNA) und Diffusionsberechnungen zu D1/2 = 1.7 ± 0.3 Gy bestimmt. Aus der Konvolution der Plasmidpositionen mit dem durch Elektronenstreusimulationen bestimmten ortsaufgelösten Energieeintrag wurde dessen Häufigkeitsverteilung im Targetvolumen der Plasmide sowie der mittlere mikroskopische letale Energieeintrag berechnet als E1/2 = 6 ± 4 eV . Es wurde gefolgert, dass weniger als zwei Ionisationsprozesse im sensitiven Targetvolumen der DNA im Mittel zu einem Einzelstrangbruch führen. Das für mikrodosimetrische Modellierungen wichtige Verhältnis von Einzelstrangbrüchen (SSB) zu Doppelstrangbrüchen (DSB) wurde als SSB : DSB = 12 : 1 bestimmt. Die vorgestellte Methode zur Bestimmung mikroskopischer Schaden-Dosis Relationen wurde auf weitere Klassen von Bestrahlungsexperimenten verallgemeinert. Dadurch ist die Methode unabhängig von der verwandten Primärstrahlung, der Probengeometrie und den Diffusionseigenschaften der untersuchten Moleküle anwendbar. So wird eine Vergleichbarkeit experimenteller Systeme mit inhomogenen Energieverteilungen erreicht, die bei ausschließlicher Betrachtung makroskopischer, gemittelter Größen nicht gegeben ist. Des weiteren wurden die Strahlenschutzfunktionen des kompatiblen Soluts Ectoine und sein Einfluss auf Wasser und Biomoleküle untersucht. Mittels Ramanspektroskopie wurde ein kon-zentrationsabhängiger Anstieg des Anteils der Kollektivmoden des Wassers der OH-Streckschwingungen und dessen Unabhängigkeit von der Natriumchloridkonzentration beobachtet. Molekulardynamik-Simulationen zeigten, dass die zwitterionischen Eigenschaften zur Bildung einer half-chair Konformation Ectoines führen. Die Wasserstoffbrückenbindungen in der ersten Hydrationshülle sind signifikant stabiler und besitzen höhere Lebensdauern als das Bulk-Wasser. Bestrahlung von DNA in Anwesenheit von 1 M Ectoine führt zu einer Erhöhung der Überlebensrate um den Faktor 1,41. Die Schutzfunktion wurde auf die Erhöhung des Streuquerschnitts niederenergetischer Elektronen an den akustischen Vibrationsmoden des Wasser durch Ectoine und seine Wirkung als OH-Radikalfänger zurückgeführt. Dies wurde mittels Ramanspektroskopie und Elektronenspinresonanzmessungen (ESR) nachgewiesen. N2 - To cure cancer radiation therapy is used to kill tumor cells. It is based on radiation induced damage to biomolecules. Especially DNA damage is of key interest due to its central role in apoptosis and mutation. Because of the high amount of water in biological tissue, most of the damage is caused by the secondary particles produced by the inelastic scattering of ionizing radiation and water. A detailed understanding of the underlying molecular processes under physiological conditions is the prerequisite to develop more efficient therapies. Goal of this work is to quantify the DNA damage caused by ionizing radiation in dependence of the inelastic scattering events and the energy deposit within the microscopic target volume of biological relevance. The irradiations have to be performed in liquid, under consideration of the chemical environment. Therefore, a new combination of experiment and Monte-Carlo simulations was developed and tested. To make it possible to irradiate liquids with electrons within scanning electron microscopes a new sample holder was constructed incorporating an electron transparent nanomembrane. It makes it possible to irradiate DNA, proteins or cells at different pH, salinity and in the presence of cosolutes. The median lethal dose for a model system of plasmid DNA and water was determined by the combination of experimental data, particle scattering simulations (Geant4-DNA) and Diffusion calculations as D1/2 = 1.7 ± 0.3 Gy. From the convolution of plasmid positions and the spatially resolved energy deposit, as determined by electron scattering simulations, the histogram of the energy deposit within the target volume of the plasmids and the microscopic median lethal energy deposit was calculated as E1/2 = 6 ± 4 eV . It could be deduced that on average less than two ionization events are sufficient to cause a single-strand-break. The relation of single- strand-breaks (SSB) to double-strand-breaks (DSB), which is of importance for microdosimetric modeling, was determined as SSB : DSB = 12 : 1. The presented method for the determination of microscopic dose-damage relations was further extended to be applicable for general irradiation experiments. It becomes independent of the type of primary radiation used, the experimental geometry, and the diffusional properties of the molecules under investigation. This way different experimental systems with varying, inhomogeneous energy deposit characteristics become comparable with each other, which is not possible when only macroscopic averaged values are taken into account. In addition, the radiation protection properties of the compatible solute ectoine, as well as ist influence on the water properties and biomolecules were investigated. Raman spectroscopy revealed a concentration dependent increase of the collective water modes in the OH-stretching region, which was found to be independent of the sodium chloride concentration. Molecular dynamic simulations showed that the zwitterionic properties of ectoine lead to its half-chair conformation. The hydrogen bonds in the first hydration shell are more stable and have an increased lifetime compared to the bulk water. Irradiation experiments with DNA in the presence of 1 M ectoine revealed an increase of the survival rate by a factor of 1.41 as compared to the absence of ectoine. The protective properties of ectoine result from the increase of the inelastic scattering probabilities of low energy electrons at the acoustic vibrational modes of water and its properties as OH-radical scavenger. This was shown by Raman spectroscopy and electron paramagnetic resonance measurements (EPR). KW - DNA KW - Radiation KW - Radiation damage KW - Dosimetry KW - Microdosimetry KW - DNA damage KW - DNA radiation damage KW - Low energy electrons KW - Electron irradiation KW - Hydroxyl radicals KW - Ectoine KW - Ectoine protein interaction KW - Ectoine DNA interaction KW - Ectoine radiation protection KW - Ectoine salt KW - Cancer therapy KW - Radiation therapy KW - Ectoin PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:188-fudissthesis000000106497-4 UR - http://www.diss.fu-berlin.de/diss/receive/FUDISS_thesis_000000106497 SP - 1 EP - 108 CY - Berlin AN - OPUS4-44510 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Dümichen, Erik T1 - Einsatz neuer thermoanalytischer Verfahren zur Untersuchung thermischer und thermo-oxidativer Degradationsmechanismen sowie dem Netzwerkaufbau von Polymeren N2 - Die Anwendung thermoanalytischer Methoden für die Polymercharakterisierung hat aufgrund der makromolekularen Struktur von Polymere Vorteile. Es wurden zwei neue thermoanalyti-sche Verfahren entwickelt und deren Einsatz anhand von Anendungsbeispielen demons-triert, sowie mit etablierten, thermoanalytischen Methoden verglichen. Für die thermische- und thermo-oxidative Zersetzungsgasanalytik wurde die Thermogravi-metrie (TGA) gekoppelt mit der Thermodesoptions-Gaschromatographie-Massenspektrometrie (TDS-GC-MS). Die Zersetzungsgase der TGA wurden dafür über ei-nen Festphasenadsorber geleitet, auf dem eine repräsentative Auswahl von polymerspezifi-schen Analyten adsorbiert wurde. Die thermische Extraktion der Analyten erfolgte in der TDS-GC-MS. Dies ermöglichte die Trennung der Analyten sowie die eindeutige Identifizie-rung mittels charakteristischer Massenfragmentmuster. Sie wurde als TED-GC-MS bezeichnet. Es stellte sich heraus, dass sie sich besonders für die Analyse von komplexen Kohlen-wasserstoffgemischen mit Molmassen von mehr als 100 g/mol eignet. In Kombination mit anderen Kopplungstechniken wie beispielsweise die TGA-FTIR/MS, die speziell für die Ana-lyse von kleineren Molekülen verwendet wurde, konnten neue grundlegende Zersetzungs-mechanismen entwickelt werden. Es wurde beispielsweise sichtbar, dass sowohl bei der thermischen als auch bei der thermo-oxidativen Degradation von Polyamid 66 (PA 66) Kon-densationsreaktionen eine wichtige Rolle spielen. Die Methode erwies sich darüber hinaus als besonders geeignet für die Identifizierung und Quantifizierung von Polymeren in Umweltproben. Es entstand dazu eine erste grundlegende Arbeit für die quantitative Bestimmung von Polyethylen (PE) Mikroplastik in Umweltproben. Im zweiten Teil der Arbeit wurde eine steuerbare beheizbare Zelle eingeführt. Mit ihr war es möglich, mit Hilfe der Nahinfrarotspektroskopie (NIR), sich verändernde Netzwerkstrukturen während der Härtung sichtbar zu machen. Vergleichend dazu wurden etablierte, kalorische Messungen durchgeführt. Somit konnten für verschiedene Epoxidsysteme die Aushärtegrade während der Härtung mit variablen Heizraten bestimmt werden. Dadurch konnten Aushär-tungskinetiken erstellt werden, die durch isotherme und komplexe Aushärtungsszenarien validiert wurden. KW - Thermische Methoden KW - Polymer KW - Analytik PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:188-fudissthesis000000100982-9 UR - http://www.diss.fu-berlin.de/diss/receive/FUDISS_thesis_000000100982 SP - 1 EP - 65 PB - FU Berlin CY - Berlin AN - OPUS4-42171 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Oliver A1 - Adam, Christian T1 - Potenzialermittlung der in Deutschland anfallenden Klärschlammaschen - Mögliche Phosphor- und Metallrückgewinnung N2 - In Europa fallen jedes Jahr mehr als 10 Millionen Tonnen Klärschlamm an (Trockenmasse), etwa 2 Millionen davon in Deutschland, Bild 1 zeigt die Entwicklung der Klärschlammentsorgung in Deutschland. Nach dem Deponierungsverbot hat die Verbrennung des Klärschlamms stetig zugenommen. Die Verwendung im Landschaftsbau bzw. als Düngemittel ist nach einem Maximum um die Jahrtausendwende herum zugunsten der Verbrennung zurückgegangen, so dass heute jeweils etwa die Hälfte des Klärschlamms verbrannt und in der Landwirtschaft genutzt wird. Der Anteil an verbranntem Klärschlamm wird in Zukunft vermutlich weiter steigen. Ein wesentlicher Grund dafür ist die zunehmende Besorgnis über Schadstoffe im Klärschlamm, die Mensch und Umwelt schädigen könnten. Neben verschiedenen organischen und anorganischen Schadstoffen handelt es sich insbesondere um Emerging Pollutants of Concern (EMPOC) wie Antibiotika und Kosmetika. T2 - 8. Klärschlammtage CY - Fulda, Germany DA - 04.06.2015 PY - 2013 SP - 1 EP - 5 AN - OPUS4-33344 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schraut, Katharina T1 - Formation of tricalciumsilicate from post-treated metallurgical slags N2 - LD-slags differ from Ordinary Portland Cement (OPC) mainly in a higher content of iron oxides and a low content of Tricalciumsilicate (Alite). In the context of an improved resource usage, a procedure to convert LDslags into cement clinker was investigated. T2 - 15th International Congress on the Chemistry of Cement CY - Prague, Czech Republic DA - 16.09.2019 KW - Tricalcium-silicate KW - Portland Cement KW - Alite KW - Steelmaking slag PY - 2019 AN - OPUS4-49591 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Werner A1 - Wöhlecke, Andreas ED - Jost, D. ED - Albers, K. T1 - Stand der Zulassungen für Geokunststoffe nach der novellierten Deponieverordnung N2 - Auf den vergangenen beiden Tagungen 2010 und 2011 wurden bereits Vorträge über das Thema Zulassung von Geokunststoffen nach der Deponieverordnung (DepV) gehalten. Im Anschluss an diese Beiträge wird hier über den aktuellen Stand berichtet. Die Novellierung der Deponieverordnung berührt die Vorschriften über die Zulassung nicht, wohl aber die Regelung, wie ein Eignungsnachweis der zuständigen Behörde gegenüber „gleichwertig“ zur Zulassung geführt werden könnte. Es geht um die CE-Kennzeichnung und um bestimmte ausländische Produkte aus dem Europäischen Wirtschaftsraum. Darauf wird kurz eingegangen. Weiterhin werden die Anforderungen an die geotextilen Filter in den Kunststoff-Dränelementen diskutiert. Das Thema „innere Scherfestigkeit“ dieser Elemente wird etwas ausführlicher behandelt, da hier offenbar „Klärungsbedarf“ im Hinblick auf die Vorgaben in den Zulassungsscheinen besteht. T2 - 28. Fachtagung - Die sichere Deponie - Sicherung von Deponien und Altlasten mit Kunststoffen CY - Würzburg, Germany DA - 09.02.2012 KW - Deponieverordnung KW - BAM-Zulassung KW - Geokunststoffe KW - Kunststoff-Dränelemente KW - Geotextile Filter PY - 2012 IS - Kap. B SP - 1 EP - 22 CY - Würzburg AN - OPUS4-25462 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, S. A1 - Herzel, Hannes A1 - Adam, Christian A1 - Montag, D. ED - Holm, O. ED - Thomé-Kozmiensky, E. ED - Quicker, P. ED - Kopp-Assenmacher, S. T1 - Langzeitlagerung von Klärschlammaschen ab 2029? Erste Erfahrungen zur Phosphorrückgewinnung aus deponierten Klärschlammverbrennungsaschen N2 - Das Institut für Siedlungswasserwirtschaft (ISA) der RWTH Aachen University sowie die Bundesanstalt für Materialforschung und -prüfung (BAM) untersuchen gemeinsam fünf deponierte KSA, die von drei Deponiebetreibern ausgebaut und zur Verfügung gestellt wurden sind. Im Fokus der Untersuchungen stehen die physikalische und chemische Charakterisierung der deponierten KSA sowie deren P-Rückgewinnungspotenzial bei der Behandlung in thermochemischen sowie nasschemischen Verfahren. Diese Ergebnisse werden im Vergleich mit „frischen“, also nicht deponierten KSA-Proben vergleichbarer Herkunft bewertet, um so den Einfluss der Lagerung auf die KSA zu erfassen. T2 - Berliner Klärschlamm Konferenz CY - Berlin, Germany DA - 11.11.2025 KW - Klärschlammasche KW - Recycling KW - Deponie KW - Monoverbrennung PY - 2025 SN - 978-3-911006-63-7 VL - 8 SP - 192 EP - 202 PB - Thomé-Kozmiensky Verlag GmbH CY - Neuruppin AN - OPUS4-65017 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schneider, Joachim A1 - Adamczyk, Burkart A1 - Ebert, Dominik A1 - Ehrenberg, Andreas A1 - Schraut, Katharina A1 - Algermissen, David A1 - Adam, Christian T1 - Usage of BOF slag and next generation EAF slag in the cement industry N2 - When the transformation of its production routes, which the European steel industry aims to complete within the next two decades, is accomplished, increased amounts of EAF slag will be generated. In most cases the BF/BOF production route is intended to be substituted by a DRI/EAF combination. But in some cases only the BF will be substituted by a DRI/SAF (smelter) combination and the BOF process remains. Then BOF slags will remain, too. BAM and FEhS cooperate together with further research and industry partners in two research projects dealing on the one hand with the utilisation of modified BOF slag as a cement clinker substitute ("SlagCEM") and on the other hand with the use of modified and granulated EAF slag as granulated blast furnace slag (GBS) substitute ("DRI-EOS"). T2 - 9th International Slag Valorisation Symposium CY - Leuven, Belgium DA - 08.04.2025 KW - Steel slags KW - Basic oxygen furnace (BOF) KW - Electric arc furnace (EAF) KW - Cement KW - Slag valorisation PY - 2025 SP - 187 EP - 191 AN - OPUS4-64713 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Keserović, Amela A1 - Sobetzki, Joana A1 - Sarmiento Klapper, Helmuth A1 - Dimper, Matthias T1 - Evaluation of Metallic Materials for Geothermal Applications N2 - Since geothermal wells are a feasible energy source to replace fossil fuel supply, many technologies have been developed to take advantage of geothermal energy. Nevertheless, service conditions in geothermal facilities are due to the chemical composition of hydrothermal fluids and temperatures, in many cases, extreme in terms of corrosion. Therefore, materials selection based on preliminary material qualification is essential to guarantee a secure and reliable operation of the facilities. The corrosion behavior of different high-alloyed metals including duplex and austenitic stainless steels as well as a nickel alloy have been evaluated in artificial geothermal fluids simulating the conditions in some locations with geothermal potential in Germany as well as two sites in Indonesia. The suitability of carbon steel 25CrMo4, stainless steels X2CrNiMo17-12-2, X2CrNiMo-22-5, X2CrNiMoCuWN25-7-4 and super austenitic steel X1CrNiMoCu32-28-7 in these geothermal fluids obtained by electrochemical measurements and exposure tests is limited. The nickel alloy NiCr23Mo16Al shows an excellent corrosion resistance against pitting corrosion. Excluding its high cost, it is a very good alternative to be used in the construction of geothermal facilities having highly saline brines. Stainless and duplex steels exhibit a limited corrosion resistance concerning pitting and crevice corrosion. Beside of the higher alloyed materials, also the low-alloyed steel 25CrMo4 could be employed as a constructional material for the geothermal power plant in stagnant highly acidic non saline environments, as long as the wall thickness of the material vs. corrosion rate is taken into account. T2 - European Geothermal Congress 2016 CY - Starsbourg, France DA - 19.09.2016 KW - Localized corrosion KW - Stainless steel KW - Ni-based alloy KW - Geothermal energy PY - 2016 SP - paper THP-248, 1 EP - 7 AN - OPUS4-37750 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Raedel, Martina A1 - Feldmann, Ines A1 - Bücker, Michael A1 - Kömmling, Anja ED - Roemich, Hannelore ED - Fair, Lauren T1 - Testing bulked adhesives for the Restoration of Stained-Glass Windows N2 - In this study, bulked adhesives were examined regarding changes in properties for their use in the restoration of stained-glass windows. Two epoxy adhesives commonly used in the restoration of flat glass, Araldite® 2020 and Hxtal NYL-1™, were investigated. The adhesives were mixed with various silica-based micro- and nano-particles as fillers. Different tests were carried out on the adhesives with and without fillers in order to characterise their chemical and mechanical properties. The tests included colorimetry, dynamic-mechanical methods of analysis and tests on bending strength. No property changes could be ascertained in the bulked adhesives that would be negative for the restoration of delicate flat glass. T2 - Recent advances in glass and ceramics - ICOM-CC Glass and Ceramics Working Group Interim Meeting CY - Breslau / Wroclaw, Poland DA - 25.05.2016 KW - bulked epoxy adhesives KW - micro-fillers KW - nano-fillers PY - 2016 SN - 978-83-64419-80-5 SP - 155 EP - 163 AN - OPUS4-36457 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Yevtushenko, Oleksandra A1 - Hattendorf, H. T1 - Suitability of high alloyed materials in molten salts at 600 °C N2 - Within the last years the use of feasible alternative energy sources has risen and is going to replace fossil resources more and more. Nevertheless, service conditions in solar facilities are due to the chemical composition of heat transmission media and temperatures, in many cases, extreme in terms of corrosion. Since the construction of power plants shall be economical with maximum life service, materials selection based on preliminary material qualification is essential to guarantee a secure and reliable operation of those facilities. The materials selection depends on the operation temperature of a power plant on the chemical composition of the transmission fluid used. In high corrosive environments Ni-based alloys are often used as an all-round solution for the construction of corrosion resistant parts, because of their good corrosion properties. However, there might be limits for their use regarding their corrosion behavior, with which this contribution deals. By means of electrochemical measurements and exposure tests the suitability of two high alloyed materials X8NiCrSi38 18 and NiCr25FeAlYB in molten nitrate salt (60 % NaNO3/40 % KNO3) was characterized at 600 °C. T2 - NACE International Corrosion Conference CY - Vancouver, BC, Canada DA - 06.03.2016 KW - Localized corrosion KW - Nickel based alloys KW - Solar energy KW - Renewables KW - Electrochemical characterization KW - X8NiCrSi38-18 KW - NiCr25FeAlYB PY - 2016 SP - 7363-1 EP - 7363-9 CY - Houston, USA AN - OPUS4-36988 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sobetzki, Joana A1 - Le Manchet, S. A1 - Bäßler, Ralph T1 - Corrosion Resistance of the Super-Austenitic Stainless Steel UNS S31266 for Geothermal Applications N2 - Super-austenitic stainless steels cover grades with high chromium (20 to 27 %), high nickel (18 to 31 %) and high molybdenum (4 to 6 %) contents. Within this family, the 6%Mo high nitrogen grade S31266 was developed to combine the beneficial influence of chromium, tungsten, molybdenum and nitrogen on its mechanical and corrosion properties. Due to 22 % nickel, 24 % chromium and 0.4 % nitrogen additions, this alloy exhibits a very stable microstructure, being less prone to intermetallic phase precipitation than the other highly alloyed super-austenitic stainless steels. This paper deals with the corrosion resistance of S31266 in artificial geothermal water with moderate salinity and low pH. Long-term static exposures and electrochemical tests were conducted at various temperatures to evaluate the pitting, crevice and stress corrosion cracking resistance of this material. The results show that S31266 is resistant up to 220 °C. As a consequence, it can be a good candidate material for geothermal applications involving a highly corrosive environment, especially salinity and low pH. T2 - NACE International Corrosion Conference 2107 CY - New Orleans LA, USA DA - 26.03.2017 KW - Geothermal energy KW - S31266 KW - Crevice corrosion KW - Super-austenitic stainless steel PY - 2017 SP - Paper 8825, 1 EP - 11 PB - NACE CY - Houston TX, USA AN - OPUS4-39830 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Stoljarova, A. A1 - Regenspurg, S. T1 - Material qualification in Saline, copper containing geothermal water N2 - By exposure and electrochemical tests in the laboratory the Cu-effect on corrosion behavior of carbon steel, high-alloyed steels and Ti-alloy can be assessed. Critical materials specific properties were determined by static exposure and electrochemical tests in an artificial geothermal water with high salinity and low pH, containing Cu. Conclusions were drawn using characteristic potential values. It could be shown that significant Cu-deposition and -precipitation only occurred in combination with carbon steel. High-alloyed materials (S31603, S31653, S31700, S31703, S31803 and N08904) prevent the disturbing Cu-agglomeration. Therefore, they are suitable to be chosen for future design of the piping system, either in massive or in cladded form, if formation of crevices with non-metallic materials can be excluded. From the interactions and pitting corrosion point of view, R50400 seems to be most favorable. T2 - NACE International Corrosion Conference 2019 CY - Nashville, TN, USA DA - 24.03.2019 KW - Copper KW - Corrosion KW - Steel KW - Geothermal energy PY - 2019 SP - 1 EP - 11 PB - NACE International CY - Houston AN - OPUS4-47911 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brandić Lipińska, M. A1 - Davenport, R. A1 - Imhof, A. B. A1 - Waclavicek, R. A1 - Fateri, M. A1 - Meyer, Lena A1 - Gines-Palomares, J. C. A1 - Zocca, Andrea A1 - Makaya, A. A1 - Günster, Jens T1 - PAVER - Contextualizing laser sintering within a lunar technology roadmap N2 - The Global Exploration Strategy of the International Space Exploration Coordination Group (ISECG) describes a timeframe of 2020 and beyond with the ultimate aim to establish a human presence on Mars towards the 2040ies. The next steps lie on the Moon with a focus on the coming 10 years. Early lunar surface missions will establish a capability in support of lunar science and prepare and test mission operations for subsequent human exploration of Mars and long-duration human activities on the Moon. Given the extreme costs involved in the shipping of material from Earth, a prerequisite for future human exploration is the manufacturing of elements directly on the Moon’s surface. Unlike the equipment, which at the beginning will have to be brought from Earth, raw materials and energy could be available following the concept of In-Situ Resource Utilization. The ESA OSIP PAVING THE ROAD (PAVER) study investigates the use of a laser to sinter regolith into paving elements for use as roadways and launch pads thus mitigating dust issues for transport and exploration vehicles. The ESA-funded study examines the potential of using a laser (12 kW CO2 laser with spot beam up to 100 mm) for layer sintering of lunar and martian regolith powders to manufacture larger 3D elements and provide know-how for the automatic manufacture of paving elements in the lunar environment. The project contributes to the first step toward the establishment of a lunar base and will lead to the construction of equipment capable of paving areas and manufacturing 3D structures. PAVER project sets the starting point for an examination of the larger context of lunar exploration. Mission scenarios will look at different phases of lunar exploration: Robotic Lunar Exploration, Survivability, Sustainability, and Operational Phase. A proposed Technology Roadmap investigates the mission scenario and analyses how, and to which extent, laser melting/sintering will play a role in the various phases of exploration. The paper contextualizes laser sintering within selected mission scenarios and discusses the different kinds of infrastructure that can be produced at each phase of the mission. The outcome of the study includes the detailing of the TRL steps in the project and an outline of a timeline for the different elements. Covered aspects include terrain modelling such as operation pads, roadways, or towers, non-pressurized building structures to protect machinery, and habitat envelopes, to protect and shield humans against dust, micrometeoroids, and radiation. T2 - 73rd International Astronautical Congress (IAC) CY - Paris, France DA - 18.09.2022 KW - Additive manufacturing KW - Solar sintering KW - ISRU KW - Infrastructure KW - Lunar habitat KW - Paving PY - 2022 SP - 1 EP - 9 AN - OPUS4-56519 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Aristia, Gabriela A1 - Nofz, Marianne A1 - Bäßler, Ralph A1 - Sojref, Regine A1 - Le, Quynh Hoa T1 - Preliminary Study on Al2O3 Sol-Gel Coating for Corrosion Protection of Martensitic Stainless Steel in Artificial Geothermal Water N2 - Al2O3 coatings are often used as protective layers on steels against electrochemical and high-temperature corrosion because they are chemically inert and stable at elevated temperatures. This study presents preliminary work on the possibilities of using Al2O3 sol-gel coatings for corrosion protection of martensitic stainless steels in geothermal environments. Al2O3 sol-gel coatings were applied on UNS S42000, which is known to be susceptible to uniform and localized corrosion. The coated steel specimens were then tested in two types of artificial geothermal water, which simulate the geothermal fluids found in Sibayak (SBY), Indonesia, and North German Basin (NGB), Germany, respectively. SBY has pH 4 and 1.5 g/L of chloride ions, whereas NGB has a pH of 6 and 166 g/L of chloride ions. All experiments were carried out in autoclaves at 150 °C and 1 MPa under the deaerated condition. Evaluations were performed by investigating the surface profiles of both uncoated and coated steels before and after the corrosion test using a Laser Scanning Microscope (LSM) and Scanning Electron Microscope (SEM). Finally, Electrochemical Impedance Spectroscopy (EIS) was performed to compare the corrosion resistance of Al2O3 coated steels in SBY and NGB solutions. It was observed from the corrosion test that Al2O3 coatings are more suitable for use in the geothermal water with a higher pH. T2 - AMPP Annual International Corrosion Conference 2021 CY - Online Meeting DA - 19.04.2021 KW - Protective coating KW - Sol-gel coating KW - Geothermal KW - Martensitic steel KW - Corrosion PY - 2021 SP - 16777-01 EP - 16777-12 CY - Houston AN - OPUS4-52501 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Bäßler, Ralph T1 - Comparison of the corrosion resistance to dangerous goods of austenitic CrNiMo and duplex steels N2 - The “BAM-List - Requirements for Tanks for the Transport of Dangerous Goods” is the basis in Germany for substance-related prototype approvals for tank Containers in Germany. Compatibility evaluations of selected metallic materials and polymeric materials under the influence of approximately 7200 dangerous goods have been published in the BAM-List since 1989. The austenitic CrNi- and CrNiMo-steels - UNS S30403, UNS S31600, UNSS31603 and UNS S31635 - are the materials mostly used worldwide for transport tanks. The duplex Steel UNS S31803 has been put on the BAMList due to the great interest of tank producers and transport Companies. Using UNS S31803 instead of 316L, the weight of the tanks can be reduced, and the list of transportable goods can be extended. The objective of these investigations was to compare the corrosion resistance of duplex Steel UNS S31803 and austenitic Steel UNS S31603. Therefore, test specimens of both steels were exposed to selected corrosive substances, such as formic acid, acetic acid, phosphoric acid, sulfuric acid, nitrating acid, monochloroacetic acid and trichloroacetone at 55 °C (30 °C, 70 °C). The test results have shown that the duplex Steel UNSS31803 is a good alternative to austenitic CrNiMo-steel UNS S31603 for tanks carrying corrosive dangerous goods. T2 - Corrosion 2014 CY - San Antonio, TX, USA DA - 09.03.2014 KW - Austenitic CrNiMo steel KW - Duplex steel KW - Corrosion resistance KW - Dangerous goods KW - BAM-list PY - 2014 SP - Paper 3786, 1 EP - 11 AN - OPUS4-30412 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Keserovic, A. A1 - Bäßler, Ralph A1 - Kamah, Y. T1 - Suitability of alloyed steels in highly acidic geothermal environments N2 - This study aims to evaluate which of the materials currently available on the market could overcome the Problem of corrosion and withstand highly aggressive conditions in the exploitation of geothermal resources in volcanic environments. Our investigations were triggered by the conditions on Lahendong geothermal field (North Sulawesi, Indonesia): well LHD-23 presents one of the greatest challenges due to its capacity of producing > 20 MWe of energy from a single well and in the same time having very low pH (2-3) and relatively high Chloride (1,500 mg/L) and sulphate (1,600 mg/L) concentration. Three different Steel grades (low-alloyed Steel UNS G41300, stainless Steel UNS S31603 and high-alloyed stainless Steel UNS N08031) were selected, and their corrosion behavior was evaluated by means of short-term electrochemical methods (potentiodynamic polarization) and long-term exposure tests (up to 6 months). The research was carried out in the laboratory under stagnant conditions in the artificial LHD-23 geothermal brine (1,500 mg/L Chlorides, 1,600 mg/L sulphates, pH 2) at 100 °C (100 kPa) and 175 °C (900 kPa), simulating the conditions present at the site. T2 - Corrosion 2014 CY - San Antonio, TX, USA DA - 09.03.2014 KW - Geothermal KW - Corrosion KW - Carbon steel KW - Stainless steel KW - Electrochemistry PY - 2014 SP - Paper 4031, 1 EP - 14 AN - OPUS4-30542 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lee, Jun-Seob A1 - Radnik, Jörg A1 - Bäßler, Ralph T1 - Electrochemical behavior of UNS N08031 in Green-Death-solution N2 - The electrochemical behavior of UNS(1) N08031 was investigated as a function of electrode potential in Green-Death(2) solution at 40 °C. The UNS N08031 surface is in a stable passive state during cyclic potentiodynamic polarization without an initiation and/or propagation of localized corrosion. In potentiostatic polarization of UNS N08031 for 3600 s, passive current density increases with an increase in the passivation potential from 0.7 to 1.0 VSSE (silver/silver chloride reference electrode in saturated potassium chloride) Electrochemical impedance spectroscopy (EIS) and Mott-Schottky (M-S) analysis showed that a more defective n-type semiconductive passive film forms as the potential increases. X-ray photoelectron spectroscopy (XPS) revealed that passive film consists of mainly chromium and minor iron and nickel oxides. The mechanism of the defective passive film formation is discussed. The increase of the applied potential is considered to be a reason for the change in passive film stability. T2 - NACE International Annual Corrosion Conference CY - Phoenix, AZ, USA DA - 15.04.2018 KW - Steel KW - Passive film KW - X-ray photoelectron spectroscopy PY - 2018 SP - 10631, 1 EP - 9 PB - Omnipress CY - Houston AN - OPUS4-44915 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Stoljarova, A. A1 - Regenspurg, S. T1 - Influence of Precipitating Brine Components on Materials Selection for Geothermal Applications N2 - Since geothermal wells are a feasible energy source to replace fossil fuel supply, many technologies have been developed to take advantage of geothermal energy. Nevertheless, service conditions in geothermal facilities are in many cases extreme in terms of corrosion due to the chemical composition of hydrothermal fluids and temperatures. Therefore, materials selection based on preliminary material qualification is essential to guarantee a secure and reliable operation of the facilities. During operation of a geothermal research facility in Groß Schönebeck copper and lead effects have been found downhole. Occurring mechanisms and measures to prevent precipitation or scaling needed to be investigated as well as potential influences of such precipitates on corrosion resistance of metallic materials used for equipment. This contribution deals with the evaluation of the corrosion behavior of carbon steel and corrosion resistant alloys in copper and/or lead containing artificial geothermal water, simulating the conditions in the Northern German Basin. The behavior of these materials in an artificial geothermal water obtained by electrochemical measurements and exposure tests are presented. While carbon steel exhibits precipitation and deposition, higher alloyed material shows different response to such species and a higher resistance in saline geothermal water. Basing on these results the suitability of the investigated corrosion resistant alloy is given for use in such conditions, whereas carbon steel creates difficulties due to its susceptibility to Cu- and Pb-precipitation. T2 - World Geothermal Congress CY - Online meeting DA - 30.03.2021 KW - Copper KW - Lead KW - Corrosion KW - Steel KW - Geothermal energy PY - 2021 SP - 1 EP - 11 AN - OPUS4-52828 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kratzig, Andreas A1 - Le, Quynh Hoa A1 - Bettge, Dirk A1 - Bäßler, Ralph A1 - Kranzmann, Axel ED - EUROCORR, T1 - Interaction of oxidizing and reductive components in CO2 fluids in transport pipelines at low and high pressure and low temperature N2 - Carbon Capture Utilization and Storage (CCUS) is a promising technology for the reduction of CO2 emissions, e.g. from fossil-fuel operated power plants or cement mills. Crucial points for a sustainable and future-proof CCUS procedure are reliability and cost efficiency of the pipeline transport network. Due to the absence of certified benchmarks for upper limits, systematic experiments with impurities in the CO2 stream were carried out. For oxidation processes SO2 and NO2 acted as corrosive components, and for reductive atmosphere H2S. Carbon steel L485MB (pipeline), martensitic steel 1.4313 (compression) and austenitic steel 1.4562 (injection) were selected as specimens. Experiments were performed at 0 bar or 100 bar and within a temperature range 278 K ≤ T ≤ 313 K. High-alloyed Cr-Ni steels revealed no corrosion (1.4562, 1.4313), while for carbon steel considerable corrosion was observed. The type and intensity of corrosion was strongly coupled with the applied corrosive species and the level of humidity in the CO2 stream, leading to different compositions of acidic condensates. Applying a reducing atmosphere results in very little corrosion rates, but provokes pitting corrosion. In contrast, oxidizing or mixed settings lead to a clearly increased growth of the corrosion layer, but exhibit shallow uniform corrosion. Exceptional nitric acid results in intergranular corrosion. Investigations on the specimens were carried out by optical microscopy, XRD, SEM/EDX, and AAS/IC. T2 - EUROCORR 2017 CY - Prague, Czech Republic DA - 03.09.2017 KW - CCS KW - Pipeline transport KW - CO2 corrosion KW - Carbon steels KW - Condensation PY - 2017 SP - Paper 80181, 1 EP - 4 AN - OPUS4-41918 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF ED - Schraut, Katharina ED - Adamczyk, Burkart ED - Adam, Christian ED - Stephan, D. ED - Simon, Sebastian ED - von Werder, Julia ED - Meng, Birgit T1 - Production of a hydraulic material from post treated steelmaking slags N2 - Steelmaking slag is a by-product of steel production, of which 4.5 Mt were produced in 2020 in Germany alone. It is mainly used in road construction, earthwork and hydraulic engineering. A smaller part is returned to the metallurgical cycle, used as fertiliser or landfilled. With this use, iron oxides still contained in steelmaking slag are lost. In addition, the possibility of producing higher-grade products from steelmaking slag is foregone. In recent decades, many researchers have investigated the production of Portland cement clinker and crude iron from basic oxygen furnace slags (BOFS) via a reductive treatment. Carbothermal treatment of liquid BOFS causes a reduction of iron oxides to metallic iron, which separates from the mineral phase due to its higher density. Simultaneously, the chemical composition of the reduced slag is adapted to that of Portland cement clinker. In this study, German BOFS was reduced in a small-scale electric arc furnace using petrol coke as a reducing agent. The resulting low-iron mineral product has a similar chemical composition to Portland cement clinker and was rich in the tricalcium silicate solid solution alite (Ca3SiO5). Based on its chemical and mineralogical composition, similar to that of Portland cement clinker, the reduced BOFS has the potential to react comparably. In our study, the reduced BOFS produced less hydration heat than OPC, and its hydraulic reaction was delayed. However, adding gypsum has shown to accelerate the hydration rate of the reduced BOFS compared to that known from the calcium silicates of Portland cement clinker. Further research to improve the hydraulic properties of the reduced slag is essential. If successful, producing a hydraulic binder and crude iron from BOFS has economic and ecological benefits for both the cement and steel industries. T2 - The 16th International Congress on the Chemistry of Cement 2023 (ICCC2023) CY - Bangkok, Thailand DA - 18.09.2023 KW - Steelmaking slag KW - Alite KW - Clinker substitute KW - Hydraulic reactivity PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-590522 UR - https://www.iccc-online.org/archive/ SP - 432 EP - 436 CY - Bangkok AN - OPUS4-59052 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Scholl, Juliane A1 - Bagheri, Abbas A1 - Meiers, Emelie A1 - Lisec, Jan A1 - Russo, Francesco A1 - Haase, Hajo A1 - Koch, Matthias T1 - Unveiling Aging Mechanisms of Electrolytes in Commercial End-of-Life Lithium-Ion Batteries N2 - In this study, 77 end-of-life (EOL) commercial lithium-ion batteries (LIBs) of different formats were systematically analyzed to investigate electrolyte degradation mechanisms and the influence of pristine electrolyte composition on aging. Comprehensive chemical characterization employed targeted and non-targeted mass spectrometry (MS), combining liquid and gas chromatography (LC-MS/MS, GC-MS) with high-resolution MS (HRMS). This approach identified confirmed pristine components and complex degradation products. Commercial rechargeable pouch and cylindrical cells often deviated from conventional research model systems, using mixed lithium salt anions, ionic liquids (ILs), and high concentrations of triflates, triflimides, and bis(fluorosulfonyl)imide (FSI), functioning as solvents, salts, or additives. Specific IL degradation products and previously unreported pathways were proposed. A novel series of oligomerization products from propylene carbonate (PC) was also identified. In contrast, non-rechargeable coin cells showed prevalent use of per- and polyfluoroalkyl substances (PFAS) in their original electrolytes. Distinct PFAS degradation mechanisms were proposed for the first time. The absence of carbonate oligomers and lithium salt-derived products in coin cells, alongside standard carbonates, suggests lithium counterion coordination critically influences Lewis acid-catalyzed degradation. These findings provide new insight into real-world LIB aging, highlighting differences between commercial devices and model systems. KW - Mass Spectrometry KW - PFAS KW - Electrolyte degradation KW - Transformation products KW - Battery aging PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-641059 DO - https://doi.org/10.2139/ssrn.5395937 SP - 1 EP - 15 PB - Elsevier BV AN - OPUS4-64105 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hajhariri, Aliasghar A1 - Eberwein, Robert T1 - Cryogenic storage system behaviour under fire N2 - The transition from fossil fuels to low-emission alternatives is essential to mitigate carbon emissions in energy-intensive sectors. Liquid hydrogen (LH2) is a promising energy carrier due to its high gravimetric energy density, but its storage requires advanced insulation to minimize heat ingress and prevent excessive boil-off losses. Multilayer insulation (MLI), perlite, and microspheres are commonly used under vacuum conditions, yet their performance under fire exposure remains a critical concern. This study investigates the thermal degradation of insulation materials and its impact on heat transfer in an event with extreme thermal load conditions using the Cryogenic High-Temperature Thermal Vacuum Chamber (CHTTVC). The heat flow dynamics are analyzed, and an equivalent heat transfer coefficient is proposed to quantify the impact of insulation deterioration as the outer wall temperature increases. Additionally, a novel liquid-vapor interface monitoring method is introduced to improve real-time detection of phase changes within the tank. The results highlight that insulation failure substantially increases the heat flow, which, if not mitigated, can lead to boiling liquid expanding vapor explosions (BLEVE), jet fires, or catastrophic tank failure. The findings provide valuable insights into optimizing LH2 storage safety and improving emergency response strategies for cryogenic tanks exposed to extreme thermal conditions. T2 - International Conference of Hydrogen Safety CY - Seoul, Korea DA - 23.09.2025 KW - Hydrogen Storages KW - Liquid Hydrogen KW - Fire safety KW - Heat Transfer PY - 2025 SN - 979-12-243-0274-2 SP - 1149 EP - 1160 AN - OPUS4-65546 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stephan, Ina T1 - Kupfertoleranz von Braunfäuleerregern - Beschreibung von Schadensfällen und deren Ursache(n) N2 - Verschiedene Labor- und Freilandstudien zeigen, dass Antrodia vaillantii ein Braunfäuleerreger ist, der chemisch geschütztes Holz (gemäss den Anforderungen der Gefährdungsklasse 4) stark abbauen kann. Hierbei spielt die erhöhte Oxalsäureproduktion des Pilzes und die daraus resultierende Kupferoxalatausfällung im Holz die entscheidende Rolle. Das Kupfer wird auf diese Weise für den Pilz weitgehend unschädlich gemacht und andere Holzschutzmittelbestandteile wie z.B. Chrom- und Arsenverbindungen verlieren ihre Fixierung im Holz und werden wasserlöslich. Dies führt zu Frühausfällen von chemisch geschütztem Holz im Erdkontakt innerhalb weniger Jahre. Laboruntersuchungen haben gezeigt, dass der Holzabbau durch A. vaillantii bei hoher Wasserverfügbarkeit außerhalb des Holzes angeregt werden kann. Das hohe Feuchtigkeitsbedürfnis des Pilzes ist möglicherweise die Ursache für den Befall von Holz in bis zu 1,2 m Bodentiefe. Neben der hohen Bodenfeuchte gibt es Anhaltspunkte für weitere Parameter, die zur positiven Selektion von A. vaillantii und damit seiner stellenweise starken Ausbreitung führen. Diese sind hohe Toleranz gegenüber bereits vorhandenen niedrigen pH-Werten im Boden, das aktive Einstellen niedriger pH-Werte im Boden durch Säureabgabe und die Festlegung von Kuper als Kupferoxalat. T2 - 22. Holzschutz-Tagung CY - Bad Kissingen, Deutschland DA - 2000-10-17 PY - 2000 SP - 93 EP - 99 PB - DGfH CY - München AN - OPUS4-1308 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Werner A1 - Wöhlecke, Andreas ED - Hsuan, Y. G. ED - Bhatia, S. K. ED - Soong, T. Y. T1 - A study on high oxygen pressure autoclave testing for the oxidative resistance of polyolefin-based geosynthetics N2 - Testing of the oxidative resistance of polyolefin based geosynthetics in autoclaves at high oxygen pressure has been suggested as an alternative method to conventional forced-air oven aging. The intention is to shorten considerably the testing time and to ensure that aging is performed under the condition of rate-controlled and not diffusion-limited oxidation. We compare data from high pressure autoclave tests (HPAT) with data from oven aging and water immersion tests at 80 °C. For this, the stabilization of the samples has to be taken into account. Polyolefin based geosynthetics are usually stabilized by two types of “packages” of antioxidants (AO), designated here as P1 and P2. P1 consists of phenols and phosphites, P2 of hindered amine stabilizers (HAS) in addition to a marginal stabilization P1 of the resin for the manufacturing process. Phenolic and phosphite AO are quickly consumed in the HPAT. Failure time is tremendously reduced compared to forced-air oven aging or water immersion. The results are discussed within the framework of a basic autoxidation scheme (Wise et al., 1997). The reduction is much greater than expected from theoretical considerations. Therefore, a direct and degrading reaction of oxygen with the AO has to be assumed. In case of HAS, the time dependence of the degradation of tensile properties in the HPAT is significantly different from the dependence observed in conventional forced-air oven aging and their effectiveness is likewise strongly reduced. A conclusive interpretation of HPAT results needs a better understanding of what happens to the AO at high oxygen pressure. T2 - Geo-Chicago 2016 CY - Chicago, IL, USA DA - 14.08.2016 KW - Oxidative resistance KW - Geosynthetics KW - Autocalve testing PY - 2016 UR - http://ascelibrary.org/doi/book/10.1061/geochicago2016 DO - https://doi.org/10.1061/9780784480182.030 VL - Geosynthetics, Forging a Path to Bona Fide Engineering Materials, GSP 275 SP - 332 EP - 341 PB - ASCE CY - Reston, USA AN - OPUS4-37412 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Adam, Christian A1 - Giese, Lutz A1 - Segebade, Christian A1 - Steglich, Hans-Eckhart A1 - Weimann, Karin T1 - Recycling von Photovoltaik-Dünnschichtmodulen T2 - 4. Kolloquium SORTIEREN - Innovationen und Anwendungen CY - Berlin, Deutschland DA - 2005-10-06 KW - Photovoltaik KW - Recycling KW - Dünnschichtmodul KW - Cadmiumtellurid KW - Nassmechanische Aufbereitung KW - Photonenaktivierungsanalyse PY - 2005 SP - 55 EP - 65 PB - TU Berlin CY - Berlin AN - OPUS4-11053 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Adam, Christian T1 - Case study 2 - Recovery of phosphorus from sewage sludge ashes T2 - Resources that don't cost the earth Workshop CY - Berlin, Germany DA - 2011-12-01 KW - Resources KW - Phosphorus recovery PY - 2011 SP - 17 AN - OPUS4-26930 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Munz, Martin A1 - Sturm, Heinz A1 - Schulz, Eckhard T1 - Zuverlässigkeit von Polymer-Werkstoffen - Interphasen nanoskopisch betrachtet T2 - 3. Workshop "Rasterkraftmikroskopie in der Werkstoffwissenschaft" CY - Berlin, BAM, Deutschland DA - 2002-02-28 PY - 2002 SP - 14 AN - OPUS4-1831 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stephan, Ina A1 - Mierke, Wilma T1 - Measuring Soil Respiration as a New Approach to Describe the Interaction Between Wood (Treated and Untreated) and Microbiologically Active Soil T2 - 37th Annual Meeting of the International Research Group on Wood Protection CY - Tromsø, Norway DA - 2006-06-18 KW - Wood KW - Wood preservation KW - Preservative KW - Soil respiration KW - CO2 PY - 2006 SP - 28 pages PB - IRG CY - Tromsö AN - OPUS4-14209 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Stephan, Ina T1 - IBRG Functional Fluids Group: Annual Report 2004 KW - Metal working fluid KW - Lithographic fount solutions KW - Methodology KW - Laboratory test PY - 2005 SP - 1 PB - International Biodeterioration Research Group CY - Hampshire, UK AN - OPUS4-7600 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Adam, Christian A1 - Brenneis, Rudolf A1 - Adamczyk, Burkart A1 - Simon, Franz-Georg T1 - Recycling of waste materials by thermochemical treatment T2 - ISWA World congress 2010 - Urban development and sustainbility - a major challenge for waste management in the 21st century CY - Hamburg, Germany DA - 2010-11-15 KW - thermochemical substance separation KW - Thermodynamics KW - Thermochemistry PY - 2010 SP - 1 EP - 10(?) AN - OPUS4-22467 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sturm, Heinz T1 - Nanoröhren und -drähte - Lithographie, Manipulation und Analyse in ESEM und AFM T2 - Vorbereitungstreffen zum DFG Schwerpunkt "Nanodrähte und Nanoröhren" CY - Halle (Saale), Deutschland DA - 2003-01-17 PY - 2003 CY - Halle AN - OPUS4-2130 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Deroubaix, G. A1 - Labat, G. A1 - Lebayon, I. A1 - Legay, S. A1 - Marchal, P. A1 - Yrieix, C. A1 - Melcher, E. A1 - Peek, R.-D. A1 - De Geyter, S. A1 - van Acker, J. A1 - Homan, W. A1 - Dickinson, D. A1 - Murphy, R. A1 - Suttie, E. A1 - Nurmi, A. A1 - Ritschkoff, A. A1 - Rudolph, Dieter A1 - Stephan, Ina A1 - Aston, D. A1 - Baines, E. A1 - Simonin, J. T1 - Environmental Risk Assessment of Treated Timber in Service - the Environment Focus Group Approach N2 - In the context of the Biocidal Products Directive (98/8/EC), and of the OECD work on wood preservatives, the Environment Focus Group (EFG), comprising 8 institutes and the European Wood Preservative Manufacturers Group, has been working on the environmental risk assessment of treated timber in service. A literature review of emissions from treated timber has revealed that very little existing data is usable for environmental risk assessment; the most relevant data are kinetic curves of emissions over time, which show clearly the non-linear emissions behaviour of treated wood over time. The EFG has suggested real exposure conditions for treated timber in the environment, and listed typical exposure scenarios. Five representative scenarios are characterised in detail, for use in the calculation of Predicted Environmental Concentrations (PECs). The existing methods to determine emissions from treated wood have been reviewed. Most existing experimental models cannot be used to predict environmental emissions. Monitoring of commodities in service has its specific constraints. Chemical analysis and ecotoxicity testing have also been reviewed and their relationship has been discussed. Principles for the design of experimental models, for the determination of emission fluxes from treated wood to the environment, have been established. T2 - 31th Annual Meeting of the International Research Group on Wood Preservation CY - Kona, HI, USA DA - 2000-05-14 PY - 2000 UR - http://www.irg-wp.com/irgdocs/details.aspx?id=42bc629a-609f-4689-8a62-3542121b4a79 SP - Paper 50162, 1 EP - 17 PB - International Research Group on Wood Preservation CY - Stockholm AN - OPUS4-4455 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Adam, Christian A1 - Schraut, Katharina A1 - Adamczyk, Burkart A1 - Weimann, Karin A1 - Gluth, Gregor T1 - Erzeugung klimaschonender Bindemittel als Alternativen zu Zement durch thermochemische Behandlung von mineralischen Nebenprodukten und Abfällen N2 - Die Zementindustrie erzeugt etwa 6-7% der globalen CO2-Emissionen und steht damit als Industriezweig vor dem Hintergrund einer anvisierten Klimaneutralität vor gewaltigen Herausforderungen. Der Prozess der Klinkerherstellung wurde über die vergangenen Jahrzehnte bereits kontinuierlich optimiert. Seit 1990 ist es der deutschen Zementindustrie gelungen, die spezifischen CO2-Emissionen der Zementproduktion u. a. durch den Einsatz alternativer, nicht fossiler Brennstoffe und durch Absenkung des Klinkergehalts im Zement um 20 % zu senken. Weitere konventionelle Minderungsstrategien versprechen jedoch nur noch wenig zusätzliche Reduktion. Im Falle des Portlandklinkers besteht die Schwierigkeit darin, dass zwei Drittel der CO2-Emissionen rohstoffbedingt durch die Entsäuerung des Kalksteins (CaCO3) anfallen, die durch die beschriebenen Maßnahmen nicht weiter abgesenkt werden können. Vielmehr wird es erforderlich sein, noch zu entwickelnde oder zu optimierende Technologien anzuwenden und ggf. alle relevanten Ebenen wie Produktion, Weiterverarbeitung und Anwendung von Zement und Beton neu zu denken. Neben technologischen Ansätzen zur CO2-Abscheidung mit nachfolgender langfristiger Speicherung (Carbon Capture and Storage – CCS) oder Verwertung (Carbon Capture and Utilisation – CCU) werden auch alternative Rohstoffe für die Zementproduktion und alternative Bindemittel in Betracht zu ziehen sein. T2 - Berliner Konferenz Mineralische Nebenprodukte und Abfälle CY - Berlin, Germany DA - 25.04.2022 KW - Zement KW - Sekundärrohstoff PY - 2022 SN - 978-3-944310-58-9 SP - 372 EP - 385 PB - TK-Verlag CY - Neuruppin AN - OPUS4-54737 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pedersen, Angus T1 - Mg-Templated Porosity as a Descriptor of Activity and Durability in ZIF-Derived Fe–N–C O2 Reduction Catalysts - Dataset N2 - Atomically dispersed Fe in N-doped carbon (Fe-N-C) catalysts are leading platinum-group-metal-free candidates for the O2 reduction reaction in proton exchange membrane fuel cells (PEMFCs). Zeolitic imidazolate framework (ZIF-8) derived Fe-N-C present the most promising performance; however, they possess a narrow distribution of small micropores, which limits active site accessibility. Here, to induce hierarchical porosity in Fe-N-C, we report a systematic study on MgCl₂·6H₂O-templated ZIF-8-derived Fe-N-C catalysts for the O2 reduction reaction. MgCl₂·6H₂O addition induced complete Zn removal, collapse of the ZIF-8 framework, and formation of large micro- and mesopores, with graphene-like structures. N content was markedly reduced, with conversion from pyridinic to pyrrolic N species. Rotating disc electrode tests showed a progressive increase in O2 reduction activity with MgCl₂·6H₂O, which is strongly correlated (R2 = 0.98) to the formation of large micropores and small mesopores (1-4 nm). This introduces a clear structure-activity design principle for Fe-N-Cs. The enhanced Fe-N-C porosity also leads to increased degradation rates under accelerated stress test conditions, which we attributed to the oxidation of disordered carbon domains and active Fe loss. This study highlights a key trade-off between porosity-driven O2 reduction activity and durability in Fe-N-C catalysts. KW - Single atom KW - Zeolitic imidazolate framework KW - Oxygen reduction PY - 2026 DO - https://doi.org/10.26272/opus4-65228 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-65228 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mishra, Kirti Bhushan A1 - Wehrstedt, Klaus-Dieter A1 - Krebs, Holger T1 - Lessons learned from recent fuel storage fires N2 - Industrial fire and explosion hazards due to accidents in fuel storage units have gained a considerable attention in the recent times. Both the regulatory bodies and scientific communities are heavily concerned about the proper safety measures to avoid such calamities in future. This paper aims to bring some essentials related to the hazards arose from the recent fuel storage fire accident occurred in Buncefield, UK (2005), Puerto Rico, USA (2009) and Sitapura, India (2009). The potential similarities behind occurrence of these accidents are studied. The applicability of various methods (models) and also computer simulations to estimate the safety distancesaccording to the international standards for both explosion and fire hazard are verified. Theoverpressures caused by the Vapor Cloud Explosion (VCE) and radiation flux emitted by the fireare considered for respective explosion and fire hazard estimations. The prime focus is placedon the regulations laid down by the National Fire Protection Agency of the United States and the European Norms. T2 - ICCEU 2012 - 11th International conference on combustion and energy utilization CY - Coimbra, Portugal DA - 09.05.2012 KW - Industrial fires KW - Storage units KW - Safety measures KW - Explosion KW - Overpressure KW - CFD simulation PY - 2012 SP - 1 EP - 10 AN - OPUS4-26186 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mishra, Kirti Bhushan A1 - Wehrstedt, Klaus-Dieter T1 - CFD modeling of spill characteristics of flammable liquids N2 - Present work deals with safe storage and transportation of flammable liquids. A flammable liquid can spill as a result of an overflow, leakage, failure of mechanical parts, mistakes by personnel or some deliberate acts. If the spilled fuel finds an ignition source depending on flammability limits a pool fire develops. The fire and spill continue until steady state conditions are achieved. Under such conditions a steady state diameter of spill (pool) can be established. However, this theoretical diameter is based on the assumption that the volumetric spill and burning rates are equal. Determination of spill size (D) independent of burning rate (or if there is no burning) is not reported as such in the existing literature. We develop a Computational Fluid Dynamics (CFD) model to predict the spill size which is independent of burning rate and is based on the definition of overflow Reynolds number (Re). By changing Re different spill scenarios can be predicted. Here five cases with Re = 100, 500, 1000, 2000 and 2500 are considered. One liquid hydrocarbon (Jet A) and one organic peroxide (DTBP: di-tert butyl peroxide) spill are simulated. The model considers two phases i.e. air as a continuous phase and liquid fuel as a dispersed phase. Fig. 1 shows such predicted spill sizes for DTBP for five overflow Reynolds numbers. The spill characteristics of Jet A and DTBP found to be similar for a defined Reynolds number. A correlation between spill size and overflow Reynolds number is also established. In order to estimate the spill diameter and the height of vapor cloud the explosion limits of air-fuel mixtures are taken into consideration. The model makes it possible to estimate the spill characteristics of a wide variety of flammable liquids. T2 - 22nd Journées d´Etudes of the Belgian section of the combustion institute CY - Heverlee, Belgium DA - 11.09.2012 KW - Flammable liquids KW - Spill characteristics KW - CFD modeling KW - Overflow Reynolds number KW - Jet A KW - DTBP KW - Vapor cloud PY - 2012 SP - 18 EP - 19 AN - OPUS4-27924 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mishra, Kirti Bhushan A1 - Wehrstedt, Klaus-Dieter T1 - Applications of peroxy-fuels in vehicle propulsion N2 - The combustion of petroleum derived conventional fuels (diesel, gasoline etc.) takes place relatively at a slower rate. In many applications they are forced to combust faster in order to match the specific power/output requirement. To accelerate the combustion process fuel (and oxidiser) supply has to be correspondingly increased by some means. These imply the necessity of high pressure fuel feed pump, air compressor (super or turbo charger) and a large volume of chamber to combust these mixtures. As an outcome the overall compactness of the vehicle declines. Furthermore, as an additional consequence in form of emissions e.g. COx and NOx occur as a result of fast combustion of fuel and air, We investigate combustion of a dass of energetic materials commonly known as organic peroxides (or peroxy-fuels) as a main fuel in vehicle propulsion. Peroxy-fuels are typically known as reaction enhancer’s, polymerizing agents and cross linkers. Sometimes, they have been also utilised in small amounts (1% to 5%) to conventional fuels successfully. It was found that combustion process was improved and emission was drastically turned down. Therefore, they are termed as combustion improvers as well. Also it was shown that with a peroxy-fuel an engine can be run anaerobically. T2 - COMBURA 2012 - Combustion research and application CY - Maastricht, The Netherlands DA - 03.10.2012 KW - Peroxy-fuels KW - Vehicle propulsion KW - Pool flame KW - Internal combustion engine PY - 2012 SP - 49 EP - 50 AN - OPUS4-26821 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maierhofer, Christiane A1 - Reischel, Mercedes A1 - Steinfurth, Henrik A1 - Röllig, Mathias A1 - Myrach, Philipp A1 - Ziegler, Mathias ED - Cardone, G. T1 - Development of reference test specimens for the standardisation of active thermography with flash excitation N2 - In this paper, results of a project concerning the development of a testing standard for active thermography with flash excitation are presented. In addition to the standardisation of the appropriate selection of equipment and procedures for testing and data analysis, the standard will describe suitable reference test specimens. These test specimens can be used for the qualification of the equipment as well as for the validation of the method including data processing concerning different areas of application. T2 - QIRT 11 - 11th International conference on Quantitative InfraRed Thermography CY - Naples, Italy DA - 11.06.2012 KW - Active thermography KW - Flash lamp KW - Standardisation KW - Reference test specimen PY - 2012 SP - 1 EP - 10 AN - OPUS4-26360 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maierhofer, Christiane A1 - Reischel, Mercedes A1 - Krankenhagen, Rainer A1 - Myrach, Philipp A1 - Steinfurth, Henrik A1 - Röllig, Mathias T1 - Anwendungsbereiche und Grenzen der Blitzthermografie - Entwicklung eines anwendungsnahen Standards N2 - Ein anwendungsnaher Standard zur aktiven Thermografie mit Blitzanregung soll die Auswahl und Bewertung der geeigneten Messtechnik, die Durchführung der Messungen sowie die Auswertung und Darstellung der Messdaten in Abhängigkeit vom Prüfproblem festlegen. In diesem Beitrag werden zum einen Möglichkeiten zur Charakterisierung der Blitzlichtanregung sowie alternative Anregungstechniken vorgestellt. Zum anderen wurden für verschiedene Prüfprobleme Referenzprobekörper entwickelt, die systematische Untersuchungen zur Optimierung der Messparameter ermöglichten. T2 - DACH Jahrestagung 2012 CY - Graz, Österreich DA - 17.09.2012 PY - 2012 AN - OPUS4-32798 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kruschwitz, Sabine A1 - Halisch, M. A1 - Prinz, Carsten A1 - Weller, Andreas A1 - Müller-Petke, M. A1 - Dlugosch, R. T1 - Towards a better understanding of electrical relaxation N2 - Other than commonly assumed the relaxation times observed in the electrical low-frequency range (1 mHz – 40 kHz) of natural porous media like sandstones and tuff stones cannot be directly related to the dominant (modal) pore throat sizes, measured (e.g.) with mercury intrusion porosimetry (MIP). Working with a great variety of sandstones from very different origins and featuring great variations in textural and chemical compositions as well as in geometrical pore space properties, it was observed that particularly samples with narrow pore throats were characterized by long (low-frequency) relaxations. These, however, can (following the current theories) be rather explained by long “characteristic length scales” in these media or low diffusion coefficients along the electrical double layer. However, there is no straightforward way (or single approved method) of getting reliable numbers for properties such as the lengths of pore throats, the diameter and length of the wide pores and their respective distributions. Consequently we follow a multi-methodical approach and combine the benefits of MIP, micro-computed tomography (μ-CT) and nuclear magnetic resonance (NMR) to achieve much deeper insight due to the different resolutions and sensitivities to either pore constrictions (throats) or wide pores. This helps us to understand, whether the observed electrical relaxation phenomena actually depend on geometric length scales or rather on other properties such as chemical composition, clay content, clay type or cation exchange capacity. In this paper, we showcase selected results of a systematic study of a total of 16 sandstones and three tuffs. Findings and the particular advantage of the used method combination are discussed and shown in detail for a representative sample selection. T2 - Annual Symposium of the Society of Core Analysts (SCA) CY - Vienna, Austria DA - 28.08.2017 KW - Electrical relaxation KW - Complex resistivity KW - Spectral induced polarization KW - Nuclear magnetic resonance KW - Mercury intrusion porosimetry KW - Pore size distribution KW - Sandstone PY - 2017 VL - SCA2017-080 SP - 1 EP - 9 AN - OPUS4-42599 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zhang, Zeyu A1 - Kruschwitz, Sabine A1 - Weller, Andreas A1 - Halisch, M. A1 - Prinz, Carsten T1 - Enhanced pore space analysis by use of μ-CT, MIP, N2 - We investigate the pore space of rock samples with respect to different petrophysical parameters using various methods, which provide data upon pore size distributions, including micro computed tomography (μ-CT), mercury intrusion porosimetry (MIP), nuclear magnetic resonance (NMR), and spectral induced polarization (SIP). The resulting cumulative distributions of pore volume as a function of pore size are compared. Considering that the methods differ with regard to their limits of resolution, a multiple length scale characterization of the pore space geometry is proposed, that is based on a combination of the results from all of these methods. The findings of this approach are compared and discussed by using Bentheimer sandstone. Additionally, we compare the potential of SIP to provide a pore size distribution with other commonly used methods (MIP, NMR). The limits of resolution of SIP depend on the usable frequency range (between 0.002 and 100 Hz). The methods with similar resolution show a similar behavior of the cumulative pore volume distribution in the overlapping pore size range. The methods μ-CT and NMR provide the pore body size while MIP and SIP characterize the pore throat size. Using this difference, the average pore body to throat ratio is determined to be about three for the Bentheimer sandstone. Our study shows that a good agreement between the pore radii distributions can only be achieved if the curves are adjusted considering the resolution and pore volume in the relevant range of pore radii. The MIP curve with the widest range in resolution should be used as reference T2 - Annual Symposium of the Society of Core Analysts 2017 CY - Vienna, Austria DA - 27.08.2017 KW - Spectral induced polarization KW - Mercury intrusion porosimetry KW - µ-CT KW - Nuclear magnetic resonance KW - Bentheimer Sandstone PY - 2017 SP - 086, 1 EP - 086, 8 AN - OPUS4-43082 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schwarz, I. A1 - Rieck, Arielle A1 - Fellinger, Tim-Patrick A1 - Weuster-Botz, Dirk T1 - Bio-electrochemical CO2 conversion into organic products using precious-metal free electrocatalysts N2 - For the realization of a sustainable economy, it is of great importance to make use of CO2 for the production of multi-carbon organic chemicals used as feedstock in the chemical industry as well as carbon-neutral fuels (Varela et al. 2019). A promising approach is the electrochemical CO2 reduction followed by microbial conversion of the reduced products. KW - Bio-electrochemical KW - Organic products KW - Electrocatalysts PY - 2024 SP - 1 EP - 2 AN - OPUS4-59572 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eddah, Mustapha A1 - Markötter, Henning A1 - Mieller, Björn A1 - Widjaja, Martinus Putra A1 - Beckmann, Jörg A1 - Bruno, Giovanni T1 - Multi-Energy High Dynamic Range (HDR) Synchrotron X-ray Computed Tomography applied to LTCC samples N2 - Synchrotron X-ray computed tomography (SXCT) is regularly used in materials science to correlate structural properties with macroscopic properties and to optimize manufacturing processes. The X-ray beam energy must be adapted to the sample properties, such as size and density. If both strongly and weakly absorbing materials are present, the contrast to the weakly absorbing materials is lost, resulting in image artifacts and a poor signal-to-noise ratio (SNR). One example is a low-temperature co-fired ceramics (LTCC), in which metal connections are embedded in a ceramic matrix and form 3-dimensional conducting structures. This article describes a method of combining SXCT scans acquired at different beam energies, significantly reducing metal artifacts, and improving image quality. We show how to solve the difficult task of merging the scans at low and high beam energy. Our proposed merging approach achieves up to 35% improvement in SNR within ceramic regions adjacent to metallic conductors. In this way, previously inaccessible regions within the ceramic structure close to the metallic conductors are made accessible. The paper further discusses methodological requirements, limitations, and potential extensions of the presented multienergy SXCT merging technique. T2 - iCT 2026 CY - Linz, Austria DA - 10.02.2026 KW - Synchrotron x-ray CT KW - Multi-energy CT KW - Low-Temperature cofired ceramics PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-655848 SP - 1 EP - 7 CY - e-Journal of Nondestructive Testing AN - OPUS4-65584 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Fritzsche, Sven A1 - Pauw, Brian Richard A1 - Weimann, Christiane A1 - Sturm, Heinz T1 - First of its kind: A test artifact for direct laser writing N2 - With Direct Laser Writing (DLW) maturing in all aspects as a manufacturing technology a toolset for quality assurance must be developed. In this work we want to introduce a first of its kind test artifact. Test artifacts are standardized 3D models with specific geometric feature to evaluate the performance of writing parameters. Test artifacts are already common in other 3D additive manufacturing technologies e.g. Selective Laser Melting. The test artifact introduced in this work was developed in particular to accommodate 1) the high geometrical resolution of DLW structures and 2) the limited possibilities to examine the resulting structure. Geometric accuracy, surface adhesion as well as confocal raman spectroscopy results were considered when evaluating the design of the test artifact. We will explain the individual features and design considerations of our DLW test artifact. The difference between two slicers, Cura and 3DPoli, and the implications on measured feature sizes and the general shape is quantified. The measured geometries are used to derive a general design guide for a specific combination of photoresist, laser power and scanning speed and to analyse the geometric accuracy of a structure produced using these guidelines. KW - Multi photon lithography KW - Test artifact KW - Two photon polymerization KW - Direct Laser Writing KW - Quality infrastructure PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-560530 DO - https://doi.org/10.20944/preprints202210.0259.v1 SP - 1 EP - 29 PB - MDPI CY - Basel AN - OPUS4-56053 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bruhn, D. A1 - Köhler, S. A1 - Regenspurg, S. A1 - Schumann, F. A1 - Bäßler, Ralph A1 - Dunkelberg, E. A1 - Huenges, E. A1 - Frick, M. A1 - Hirschl, B. A1 - Sass, I. T1 - Positionspapier Wärmeversorgung in Berlin und Brandenburg durch GeoEnergie - Empfehlungen der GeoEnergie Allianz Berlin Brandenburg zu Forschung und Umsetzung N2 - Das gesellschaftliche Ziel der Defossilisierung der Energieversorgung erfordert eine disruptive Veränderung der Wärmebereitstellung. In Berlin und in den größten Brandenburger Städten Potsdam und Cottbus werden noch über 80 % der Nutzwärme über fossile Energieträger bereitgestellt. Die notwendigen Veränderungen erfordern Lösungen, die den tiefen Untergrund der Region nutzen. Allein die Nutzung der tiefen Geothermie kann mindestens 25% des Wärmebedarfs in Deutschland decken. Die Infrastruktur zur Verteilung dieser erneuerbaren Wärme ist bereichsweise vorhanden. Sie muss allerdings lokal und in ländlichen Gebieten weiter ausgebaut werden. Für die Sektoren Strom und Verkehr steht zwar Energie insbesondere aus Sonne und Wind bereit, aber wegen des zeitlich variablen Angebots besteht ein erheblicher Bedarf an großtechnischen Speichern für Strom und Wärme oder auch für Energieträger (z. B. Wasserstoff). Die saisonale oder temporale Überproduktion an Strom und Wärme aus erneuerbaren Energien zwingt dazu, eine urbane Speicherinfrastruktur aufzubauen, um eine grundlastfähige und bedarfsgerechte Lieferung zu realisieren. Hinzu kommt die Aufgabe das Treibhausgas Kohlendioxid aus der Atmosphäre zu reduzieren und unterirdisch dauerhaft zu lagern. Auch hier werden Speichertechnologien und ‐räume benötigt. Die nachhaltige energetische Nutzung des unterirdischen Raumes ist geeignet, entscheidende Beiträge zu einer zukünftigen Energiewirtschaft ohne fossile Brennstoffe zu leisten. Diese große interdisziplinäre Aufgabe erfordert die Zusammenarbeit vieler Fach‐, und Forschungseinrichtungen, die im Raum Berlin‐ Brandenburg vorhanden sind und in einer regionalen Forschungsallianz gebündelt werden sollen. Für die Region Berlin‐Brandenburg ergibt sich daraus die Chance, eine Schlüsselrolle in der Grundlagen‐ und angewandter Forschung zur Transformation des Energiesystems zu übernehmen und weltweit als Vorbild zu dienen. Im vorliegenden Papier werden die Formen einer nachhaltigen Geoenergienutzung, das geologische Potenzial der Region Berlin Brandenburg und dessen bisherige geoenergetische Nutzung dargestellt. Aus diesem Wissen wird der Ist‐Zustand hinsichtlich des energiewirtschaftlichen Potenzials und der sich daraus ergebenden Nutzungsoptionen abgeleitet, um darauf aufbauend Maßnahmen darzustellen, mit denen spürbare Beiträge zur Dekarbonisierung erreicht werden können. Daraus ergeben sich Handlungsempfehlungen für die Region, verbunden mit einem möglichen Beitrag der GEB² zum Risikomanagement, Investitionen in Schlüsseltechnologien, der Aus‐ und Weiterbildung, sowie der Akzeptanzerhöhung für geoenergetische Projekte. T2 - Gründungsveranstaltung der GeoEnergie Allianz Berlin Brandenburg CY - Berlin, Germany DA - 24.11.2023 KW - Geoenergie KW - Geothermie KW - Nachhaltigkeit PY - 2023 SP - 1 EP - 18 CY - Berlin & Potsdam AN - OPUS4-58924 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Aristia, Gabriela A1 - Le, Quynh Hoa A1 - Bäßler, Ralph T1 - Effect of CO2 gas on carbon steel corrosion in an acidic-saline based geothermal fluid N2 - Geothermal energy is one of the most promising energy resources to replace fossil fuel. To extract this energy, hot fluids of various salts and gases are pumped up from a geothermal well having a certain depth and location. Geothermal wells in volcanic regions often contain highly corrosive CO2 and H2S gases that can be corrosive to the geothermal power-plants, which are commonly constructed of different steels, such as carbon steel. This research focuses on the corrosion behaviour of carbon steel exposed to an artificial geothermal fluid containing CO2 gas, using an artificial acidic-saline geothermal brine as found in Sibayak, Indonesia. This medium has a pH of 4 and a chloride content of 1,500 mg/L. Exposure tests were conducted for seven days at 70 °C and 150 °C to simulate the operating temperatures for low and medium enthalpy geothermal sources. Surface morphology and cross-section of the specimens from the above experiments were analysed using scanning electron microscope (SEM) and energy dispersive X-ray (EDX). Electrochemical tests via open circuit potential (OCP) and electrochemical impedance spectroscopy (EIS) were performed to understand the corrosion processes of carbon steel in CO2-containing solution both at 70 °C and 150 °C. Localized corrosion was observed to a greater extent at 70 °C due to the less protectiveness of corrosion product layer compared to that at 150 °C, where FeCO3 has a high corrosion resistance. However, a longer exposure test for 28 days revealed the occurrence of localized corrosion with deeper pits compared to the seven-day exposed carbon steel. In addition, corrosion product transformation was observed after 28 days, indicating that more Ca2+ cations incorporate into the FeCO3 structure. T2 - EUROCORR 2019 CY - Sevilla, Spain DA - 09.09.2019 KW - Carbon steel KW - CO2 KW - EIS KW - Geothermal KW - Corrosion PY - 2019 SP - Paper 200245, 1 EP - 5 CY - Madrid, Spain AN - OPUS4-49099 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Le, Quynh Hoa A1 - Bäßler, Ralph A1 - Schiller, B.N. A1 - Beck, M. A1 - Bettge, Dirk T1 - On the corrosion behaviour of co 2 injection pipe steels: role of cement N2 - Carbon Capture and Storage (CCS) is identified as an excellent technology to reach the target of CO2 reduction. However, the safety issue and cost-effectiveness hinder the future of CCS. For the reliability and safety issues of injection wells, the corrosion resistance of the materials used needs to be determined. In this study, representative low-cost materials including carbon steel 1.8977 and low alloyed steel 1.7225 were investigated in simulated pore water at 333 K and under CO2 saturation condition to represent the worst-case scenario: CO2 diffusion and aquifer fluid penetration. These simulated pore waters were made from relevant cement powder to mimic the realistic casing-cement interface. Electrochemical studies were carried out using the pore water made of cement powder dissolved in water in comparison with those dissolved in synthetic aquifer fluid, to reveal the effect of cement as well as formation water on the steel performance. Two commercially available types of cement were investigated: Dyckerhoff Variodur® and Wollastonite. Variodur® is a cement containing high performance binder with ultra-fine blast furnace slag which can be used to produce high acid resistance concrete. On the other hand, Wollastonite is an emerging natural material mainly made of CaSiO3 which can be hardened by converting to CaCO3 during CO2 injection. The results showed the pH-reducing effect of CO2 on the simulated pore water/aquifer (from more than 10 to less than 5) leading to the active corrosion process that happened on both 1.8977 and 1.7225. Electrochemical characterization showed negative free corrosion potential and polarisation curves without passive behaviors. The tested coupons suffered from pitting corrosion, which was confirmed by surface analysis. Interestingly, basing on the pit depth measurements from the tested coupons and the hardness of cement powder, it is suggested that Variodur® performed better than Wollastonite in both aspects. The electrochemical data was compared to that resulted from exposure tests to give a recommendation on material selection for bore-hole construction. T2 - EUROCORR 2019 CY - Sevilla, Spain DA - 09.09.2019 KW - Cement KW - Carbon capture KW - Corrosion and storage (CCUS) technology KW - Utilization KW - Carbon steel KW - Crevice corrosion PY - 2019 SP - Paper 200597, 1 EP - 4 PB - SOCIEMAT CY - Madrid, Spain AN - OPUS4-49109 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Ackermann, H. A1 - Pötzsch, Sina A1 - Weltschev, Margit A1 - Bäßler, Ralph A1 - Plum, W. T1 - Entwicklung einer Prüfmethode zur Bewertung der Materialbeständigkeit von Bauteilen in Mitteldestillatanwendungen N2 - Im Vorhaben wurde eine forcierte Prüfmethode zur Bestimmung der Beständigkeit von metallenen Werkstoffen gegenüber Brennstoffen aus Mitteldestillaten und Gemischen aus Mitteldestillat und paraffinischen Kohlenwasserstoffen, die jeweils Fettsäuremethylester (FAME) als biogene Komponente enthalten, entwickelt. Bei der Prüfmethode werden Prüfkörper des jeweiligen Werkstoffes in speziellen Prüfmedien ausgelagert. Die Zusammensetzung von zwei Prüfmedien wurde im Vorhaben erarbeitet. Diese Prüfmedien erfassen die Effekte der Alterung des FAME, die zu erwarten sind, wenn der Brennstoff länger als 2 Jahre im Feld lagert. Sie decken den Bereich bis 20 % (V/V) FAME-Anteil ab. Die Auslagerung kann bei geringem Aufwand unter Atmosphärendruck durchgeführt werden. Die Eignung einer Auswahl von metallenen Werkstoffen und Polymerwerkstoffen, die für Versorgungsanlagen für Mitteldestillat relevant sind, wurde durch Auslagerung in folgenden nicht gealterten Brennstoffen bestimmt: Heizöl EL schwefelarm (B0), Heizöl EL schwefelarm mit 20 % (V/V) FAME (B20), FAME (B100) und hydriertes Pflanzenöl (HVO). Die Werkstoffe wurden auch in einem 1 Jahr gealterten B20 und einem 8 Jahre gealtertem B10 ausgelagert. Die Temperatur bei der Auslagerung betrug 50 °C für die metallenen Werkstoffe und 40 °C und 70 °C für die Polymerwerkstoffe. Die Ergebnisse der Beständigkeitsbewertung wurden in Beständigkeitslisten zusammengefasst. Die mit B20 erhaltenen Bewertungen gelten generell für Gemische aus Heizöl EL schwefelarm und FAME mit einem FAME-Gehalt bis 20 % (V/V). Sie sind auch auf Gemische aus Dieselkraftstoff und FAME mit einem FAME-Gehalt bis 20 %(V/V) übertragbar. Die forcierte Prüfmethode kann insbesondere KMUs bei der Weiterentwicklung von bestehenden Produkten und der Entwicklung von neuen Produkten als ein kostengünstiger Schnelltest zur Überprüfung der Werkstoff- und Bauteilbeständigkeit gegenüber Mitteldestillaten mit hohem FAME-Anteil dienen. Sie kann für die Hersteller die Sicherheit erhöhen, dass Bauteile die Freigabeprüfungen der Bauaufsicht bestehen, wobei die Freigabe jedoch nur für Deutschland gültig ist. Die Erkenntnisse des Forschungsvorhabens können in eine harmonisierte Europäische Norm für alternative Brenn- und Kraftstoffe einfließen. Diese ist für die Bauteilhersteller die Voraussetzung für die Erschließung des europäischen Marktes.   N2 - Within this project, a forced test method was developed to determine the resistance of metallic materials to middle distillate fuels and mixtures of middle distillate and paraffinic hydrocarbons both with fatty acid methyl ester (FAME) as a biogenic component. In the method, specimens of the material are immersed in special test media. The compositions of two test media were developed within the project. These test media include the influence of aging of the FAME which is to be expected after a storage of the fuel exceeding 2 years in the field. They cover a range of up to 20 % (v/v) FAME content. The exposure test can be carried out at ambient pressure with little effort. Suitability of selected metallic and polymer materials relevant for middle distillate supply systems was determined by exposure to the following non-aged fuels: low-sulfur light fuel oil (B0), low-sulfur light fuel oil with 20 % (v/v) FAME (B20), FAME (B100) and hydrogenated vegetable oil (HVO). The materials were also exposed in the 1-year-aged B20 and 8-year-aged B10. Test temperature was 50 °C for metallic materials and 40 °C and 70 °C for polymers. Resulting materials resistances were summarized in resistance tables. Resistances obtained in B20 are valid for any mixture of low-sulfur light fuel oil and FAME containing up to 20 % (v/v) FAME. They are also transferable to mixtures of diesel and FAME having a FAME content of up to 20 % (v/v). This method with special test media is a cost-effective rapid test for checking resistance of materials to middle distillates having a high FAME content. It can support SMEs manufacturing components for supply systems in further development of existing and new products. It increases the manufacturers' certainty that components will pass approval tests of authorities. Results of this research project can be incorporated into a harmonized European standard for alternative fuels. This is the prerequisite for component manufacturers to access the European market. KW - Heizöl KW - FAME KW - Biobrennstoff PY - 2020 UR - https://dgmk.de/publikationen/entwicklung-einer-pruefmethode-zur-bewertung-der-materialbestaendigkeit-von-bauteilen-in-mitteldestillatanwendungen/ SN - 978-3-947716-14-2 SN - 0937-9762 SP - 1 EP - 153 PB - DGMK CY - Hamburg AN - OPUS4-51110 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Aristia, Gabriela A1 - Bäßler, Ralph A1 - Roth, C. T1 - Polyaniline/silicon dioxide containing coating for use in artificial geothermal brines N2 - Geothermal brine is a complex system containing a wide variety of dissolved salts resulting from the condition s in a geothermal well. These fluids lead to corrosion in pipes and other parts of geothermal system construction and necessitate intense research efforts in finding new suitable materials. Carbon steel is susceptible to corrosion in geothermal brine especially when it is exposed to a high temperature and high-pressure medium, which is considered to be an aggressive environment. An artificial geothermal water, bas ed on a brine composition found in Indonesia, was used to investigate the performance of high alloyed materials. The electrolyte has pH 4 and contains 1,500 mg/l Cl-, 20 mg/l SO4 2-, 15 mg/l HCO3 -, 200 mg/l Ca 2+, 250 mg/l K+, and 600 mg/l Na+. In order to protect the bare material in geothermal application, it is necessary to either use high alloyed material s or coatings. In this research, a coating system consisting of polyaniline and silicon dioxide was investigated regarding its behavior to protect carbon steel. In detail, the effect of SiO2 and polyaniline (PANi) addition was evaluated by exposure and electrochemical tests for 7 days, i.e. electrochemical impedance spectroscopy (EIS) and open circuit potential (OCP ) at room temperature and 150 °C with 1 MPa pressure . T2 - NACE International Annual Corrosion Conference CY - Phoenix, AZ, USA DA - 15.04.2018 KW - Geothermal KW - Coating KW - SiO 2 KW - Polyaniline KW - Corrosion PY - 2018 SP - 10708, 1 EP - 14 PB - Omnipress CY - Houston AN - OPUS4-44916 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Aristia, Gabriela A1 - Le, Quynh Hoa A1 - Bäßler, Ralph T1 - Study of Polyaniline/Silicon Dioxide based Coating on Carbon Steel in Artificial Geothermal Brine N2 - Geothermal brines are corrosive in nature because of their salt contents and high temperatures. Therefore, they pose a major challenge to geothermal power-plants, which are mostly built of low alloyed steels, e.g., carbon steel. Carbon steel is susceptible to uniform and localized corrosion when exposed to geothermal brines having acidic-saline properties. To overcome this limitation, geothermal power plants should be built by either high alloyed materials or by integrating protection systems on carbon steel, such as coatings and inhibitors. We studied a coating system containing polyaniline/silicon dioxide basing on locally available resources that provides protection against corrosion of carbon steel and enhance the thermal resistance in geothermal environments. Here, exposure and electrochemical tests of coated carbon steels were performed in an artificial geothermal brine. The solution had a pH of 4, with the composition of 1,500 mg/L of chlorides, which is based on the chemical analysis of geothermal brine found in Sibayak, Indonesia. All exposure tests were conducted using autoclaves at 150 °C with a total pressure of 1 MPa, which was performed for up to six months to evaluate the durability of the coating system. Post-experimental analyses were performed by assessing the surface of specimens using optical and electron microscopes. On the other hand, electrochemical tests were performed for seven days at 25 °C and 150 °C to investigate the kinetics of electrochemical reactions by measuring open circuit potential and electrochemical impedance spectra. Experimental results showed the corrosion resistance of PANI/SiO2 composite coatings, where polyaniline and SiO2 play their roles as stabilizers. T2 - World Geothermal Congress CY - Online meeting DA - 30.03.2021 KW - Coatings KW - Corrosion KW - Polyaniline KW - Sibayak KW - SiO2 PY - 2021 SP - 1 EP - 7 AN - OPUS4-52830 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Alves, H. A1 - Bäßler, Ralph T1 - New experiences with nickel alloys and special stainless steels for an optimized material selection in acids at high temperatures T2 - NACE - International Corrosion Conference CY - New Orleans, USA DA - 2008-03-16 KW - Alloy 59 (UNS N06059) KW - Alloy 31 (UNS N08031) KW - Alloy B-2 (UNS N10665) KW - Formic acid KW - Acetic acid KW - Phosphoric acid KW - P-toluene sulfonic acid KW - Corrosion PY - 2008 SP - 1 EP - 15 (Paper 08189) AN - OPUS4-18194 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Burkert, Andreas A1 - Saadat, A. A1 - Kirchheiner, R. A1 - Finke, M. T1 - Evaluation of corrosion resistance of materials for geothermal applications T2 - NACE International corrosion conference 2009 CY - Atlanta, Georgia, USA DA - 2009-03-22 KW - Stainless steel KW - Ni-alloy KW - Ti-alloy KW - Geothermal KW - Corrosion PY - 2009 SP - 1 EP - 20 (Paper 09377) AN - OPUS4-19249 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph T1 - ISO 27913 - Example For Successful Standardization Activities In The Field Of CCUS N2 - Since 2016 ISO Technical Committee (TC) 265 is working on standardization the whole CCS-process chain. Around 30 countries are working together to provide international guidelines. As ISO 27913 was the first standard finished within these activities it is already in the stage of first revision. The objective of ISO 27913 is “to provide specific requirements and recommendations on certain aspects of safe and reliable design, construction and operation of pipelines intended for the large-scale transportation of CO2 that are not already covered in existing pipeline standards such as ISO 13623, ASME B31.8, EN 1594, AS 2885 or other standards. Existing pipeline standards cover many of the issues related to the design and construction of CO2 pipelines; however, there are some CO2 specific issues that are not adequately covered in these standards. The purpose of this document is to cover these issues consistently. Hence, this document is not a standalone standard, but is written to be a supplement to other existing pipeline standards for natural gas or liquids for both onshore and offshore pipelines.” This contribution shall provide information on the content, the current stage of the revision process, encourage to contribute to this standard and make listeners aware to consider the influence of ISO standard on documents currently in draft. T2 - AMPP's Annual Conference + Expo 2024 CY - New Orleans, LA, USA DA - 02.03.2024 KW - Corrosion resistant materials KW - Carbon dioxide KW - Corrosion prevention KW - Standardization KW - CCUS KW - CCS KW - CCU PY - 2024 SP - 1 EP - 6 PB - AMPP CY - Houston AN - OPUS4-59735 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schraut, Katharina A1 - Adamczyk, Burkart A1 - Simon, Sebastian A1 - von Werder, Julia A1 - Meng, Birgit A1 - Stephan, D. A1 - Kargl, F. A1 - Adam, Christian T1 - Formation and chemical stabilisation of tricalcium-silicate during solidification from the melt of post-treated metallurgical slags N2 - Tricalcium-silicate (C3S) or Alite is the most important mineral in Portland cement. Since pure tricalcium-silicate is only stable above temperatures of 1250 °C, its decomposition has to be prevented technically by fast cooling after the sintering process. At room temperature, the decomposition velocity is very slow so that metastable tricalcium-silicate is obtained. Although the mechanisms of clinker phase formation during burning process of Portland cement in a rotary kiln were solved and improved over the years, in view of possible economic and ecological benefits current projects aim to produce clinker phases from metallurgical slags. Recent studies discovered that the mineral phase which remained after a reducing treatment and separation of formed metallic iron from molten Linz-Donawitz (LD-) slags contained about 60 wt.% Alite despite it was cooled slowly. Because the results could be verified using slags from different origins and varying cooling velocities a chemical stabilisation of the Alite can be assumed. First tests in mortars indicate that workability, hardening and solid state properties are comparable with an ordinary Portland cement. An application of the observed phenomenon in cement production requires enhanced knowledge about formation and stabilisation conditions of Alite during crystallisation from melts in contrast to the sintering reactions in conventional Portland cement production. Therefore, this study focuses on the stabilisation mechanisms of Alite in consolidating melts. Samples from different melting experiments are analysed to determine stabilising factors. T2 - 15th International Congress on the Chemistry of Cement CY - Prag, Czech Republic DA - 16.09.2019 KW - Tricalcium-silicate KW - Portland Cement KW - Alite KW - Steelmaking slag PY - 2019 SP - Paper 492, 1 EP - 10 AN - OPUS4-49050 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dudziak, Mateusz T1 - Thermal properties of polymer nanocomposites based on polycarbonate (PC) and boehmite N2 - Nanocomposites are extremely versatile due to their physicochemical properties, which differ significantly from bulk homopolymers. One of the inorganic nanomaterials which are increasingly used as a filler in polymer matrices is boehmite, typically used as an inexpensive flame retardant. Here, it is used as a nanofiller in polycarbonate and polyamide, expecting to improve their mechanical properties. For industrial use boehmite is obtained by the solvothermal method, resulting in a layered nanomaterial, whereas naturally it occurs as single crystals with the size of <100µm. In this work we are obtaining and isolating boehmite crystals by a bottom-up method, in which a reaction between aluminum nitride and sodium hydroxide. Obtaining boehmite as microcrystals is necessary for its analysis and characterization, as well as to investigate its interaction with polymer matrices at the polymer/particle interface. Here, the obtained particles in polymer matrices are characterized with differential scanning calorimetry and thermogravimetry analysis. T2 - 6th International Conference on Multifunctional, Hybrid and Nanomaterials CY - Sitges, Spain DA - 11.03.2019 KW - Boehmite KW - Polycarbonate PY - 2019 AN - OPUS4-47769 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Crasselt, Claudia A1 - Schmidt, Wolfram A1 - Sturm, Heinz T1 - Influence of Rheology Modifying Admixtures on Hydration of Cementitious Suspensions N2 - The presence of polycarboxylate ether (PCE) based superplasticizers (SPs) has an enormous influence on the early hydration of cement. The hydration is retarded and the timing of formation and the morphology of hydrates is affected. This short paper presents experimental results about the influence of delayed addition time of PCE SPs on hydration of cement and alite pastes, investigated by isothermal heat flow calorimetry. For cement as well as for alite pastes the hydration is retarded with SP, whereby the high charge PCE has a stronger retarding effect than the low charge PCE. The retardation caused by PCE is much more pronounced for alite than for cement mixes. If PCE is added later to the mix, the induction period is shortened and the hydration is accelerated compared to simultaneous addition. This applies for cement and alite pastes. With delayed PCE addition the alite shows a clearly less retarded setting and main hydration than after simultaneous addition. It is obvious that for alite pastes there is less retardation the later the addition of SP. T2 - 6th International Symposium on Nanotechnology in Construction CY - Hong Kong, China DA - 02.12.2018 KW - Polycarboxylate ether (PCE) KW - Early hydration KW - Cement PY - 2018 SP - 1 EP - 8 AN - OPUS4-47204 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wöhlecke, Andreas A1 - Müller, Werner ED - Al-Akel, S. ED - Kilchert, M. T1 - Zulassung von Geokunststoffen für den Deponiebau - Stand der Zulassung und aktuelle Diskussionsthemen in der BAM und im Fachbeirat N2 - Seit dem Jahr 1989 erteilt die BAM Bundesanstalt für Materialforschung und -prüfung Zulassungen für Geokunststoffe im Bereich der Deponieabdichtungssysteme. Diese Zulassungen etablierten sich seitdem zunehmend und wurden in Genehmigungsverfahren gefordert, Das Produktportfolio der im Deponiebau verwendeten Geokunststoffe und damit das Aufgabengebiet der BAM wurden in den vergangenen Jahren stark erweitert. Zudem entwickelten sich die Arbeitsschwerpunkte von der chemischen Beständigkeit von Kunststoffdichtungsbahnen über die Schadstoffpermeation bis hin zu der Alterung und Lebensdauer der Produkte. Um den hohen Anforderungen der Deponieverordnung (DepV) zu entsprechen, mussten darüber hinaus die Qualitätssicherung bei der Produktion und dem Einbau der Produkte betrachtet werden. Ein historischer Abriss der Arbeit der BAM und ihrer Zulassungsrichtlinien findet sich z. B. unter. Geokunststoffe müssen ihre Funktion über einen Zeitraum von mindestens 100 Jahren erfüllen. Bei der Beurteilung müssen alle relevanten und damit zu erwartenden Einwirkungen auf die Produkte berücksichtigt werden. Dies gilt im besonderen Maße für Produkte, die befristetet zugelassen werden. Bei der Beurteilung der Produkte reicht es nicht ausschließlich, den reinen chemischen Abbau des Grundwerkstoffes zu betrachten. Weitergehende Fragestellungen müsse geklärt werden. Was die erteilten Zulassungen selbst anbelangt, so kann sich jeder an Hand einer Liste im Internet1 informieren. Dort findet man auch alle Dokumente zur Zulassung. T2 - 10. Leipziger Deponiefachtagung - Planung, Bau, Betrieb, Stilllegung, Nachsorge, und Nachnutzung von Deponien CY - Leipzig, Germany DA - 11.03.2014 PY - 2014 SP - 53 EP - 67 AN - OPUS4-30406 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hartmann, S. A1 - Shaporin, A. A1 - Hermann, S. A1 - Bonitz, J. A1 - Heggen, M. A1 - Meszmer, P. A1 - Sturm, Heinz A1 - Hölck, O. A1 - Blaudeck, T. A1 - Schulz, S. E. A1 - Mehner, J. A1 - Gessner, T. A1 - Wunderle, B. T1 - Towards nanoreliability of CNT-based sensor applications: Investigations of CNT-metal interfaces combining molecular dynamics simulations, advanced in situ experiments and analytics N2 - In this paper we present results of our recent efforts to understand the mechanical interface behaviour of single-walled carbon nanotubes (CNTs) embedded in metal matrices. We conducted experimental pull-out tests of CNTs embedded in Pd or Au and found Maximum forces in the range 10 - 102 nN. These values are in good agreement with forces obtained from molecular Dynamics simulations taking into account surface functional Groups (SFGs) covalently linked to the CNT material. The dominant failure mode in experiment is a CNT rupture, which can be explained with the presence of SFGs. To qualify the existence of SFGs on our used CNT material, we pursue investigations by means of fluorescence labeling of surface species in combination with Raman imaging. We also report of a tensile test system to perform pull-out tests inside a transmission electron microscope to obtain in situ images of CNT-metal interfaces under mechanical loads at the atomic scale. T2 - 2015 16th International Conference on Thermal, Mechanical and Multi-Physics Simulation and Experiments in Microelectronics and Microsystems CY - Budapest, Hungary DA - 20.4.2015 KW - Carbon nanotube CNT KW - Metal matrix KW - Pull-out test KW - Molecular dynamics simulation KW - Surface functional groups KW - Fluorescence labeling KW - Raman imaging KW - Tensile test inside a TEM PY - 2015 SN - 978-1-4799-9950-7 VL - 2015 SP - 1 EP - 8 PB - IEEE AN - OPUS4-37625 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Werner A1 - Wöhlecke, Andreas T1 - Was gibt es Neues? Stand der Zulassungen von Geokunststoffen nach der DepV N2 - Was gibt es Neues? In diesem Beitrag wird über den aktuellen Stand bei der Zulassung von Geokunststoffen berichtet. Was die erteilten Zulassungen selbst anbelangt, so kann sich jeder an Hand einer Liste im Internet1 informieren. Dort findet man auch alle Dokumente zur Zulassung. Im Folgenden geht es daher um einige aktuelle fachliche Themen und zugehörige Fragen, die bereits in der obigen Zusammenfassung umrissen wurden. T2 - 30. Fachtagung - Die sichere Deponie - Geokunststoffe im Umweltschutz CY - Würzburg, Germany DA - 02.02.2014 KW - Zulassung KW - Geokunststoffe KW - Deponieverordnung KW - Deponieabdichtung PY - 2014 IS - Kap. B SP - 1 EP - 29 CY - Würzburg AN - OPUS4-30283 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sturm, Heinz T1 - Charakterisierung und Strukturierung von nm-Bereichen in Polymer-Werkstoffen - Ein AFM-ESEM-EBL-Hybridsystem T2 - BAM-Sonderheft 2003 "Polymere Verbundwerkstoffe zwischen Raumtemperatur und 4,2 K" ; 2. Symposium im DFG-Projekt: Eigenschaften von PTFE- und PEEK-Matrix-Werkstoffen bei tribologischer Beanspruchung CY - Berlin, Deutschland DA - 2003-02-27 PY - 2003 SP - 58 EP - 59 AN - OPUS4-2673 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wöhlecke, Andreas A1 - Müller, Werner ED - Kilchert, M. T1 - Aktueller Stand der Zulassung für Geokunststoffe durch die BAM und derzeitige Arbeitsthemen des Fachbeirats und seiner Arbeitsgruppen N2 - Bereits vor der vergangenen Leipziger Deponiefachtagung waren eine Reihe von Zulassungsrichtlinien für Geokunststoffprodukte verabschiedet worden. Dokumente wurden nun überarbeitet und weitere sind hinzugekommen. Die Zulassungsscheine für bereits bestehende und auch neue Zulassungen werden auf dieser Basis für die Produkte erneuert oder erstellt. T2 - 9. Leipziger Deponiefachtagung CY - Leipzig, Germany DA - 26.02.2013 PY - 2013 SP - 29 EP - 43 AN - OPUS4-27901 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wöhlecke, Andreas A1 - Müller, Werner T1 - Kunststoff-Dränelemente - Belastungsgrenzen und Qualitätssicherung beim Einbau in Deponieoberflächenabdichtungssystemen N2 - Bereits auf der letzten Leipziger Deponiefachtagung wurde über die Anforderungen an Kunststoff-Dränelemente berichtet. Vor dem Hintergrund unserer Beiträge in Leipzig und Würzburg (Tagung: Die sichere Deponie) zu diesem Thema, entstand eine intensive Fachdiskussion, u. a. im Fachbeirat der BAM. Hier wurde auch über das Qualitätsmanagement beim Einbau der Produkte auf der Deponiebaustelle diskutiert. Diese verhältnismäßig "empfindlichen" Produkte können nur dann ihre volle Wirkung entfalten, wenn sie sachgemäß behandelt und eingebaut werden. Es wurde daher im Fachbeirat beschlossen, dass dieses Thema in einer Musterverlegeanweisung behandelt werden sollten. Diese wurde im Fachbeirat und in seiner Arbeitsgruppe Geotextilien und Kunststoff-Dränelemente erarbeitet und beschlossen. Auf diese Musterverleganweisung wird im Folgenden eingegangen. Es könnte leicht der Eindruck entstehen, dass Kunststoff-Dränelemente mittlerweile in dem Sinne Stand der Technik sind, dass sie ohne weiteres in allen Bauprojekten eingesetzt werden könnten. Dies ist nicht der Fall. Eine messtechnische Analyse des mechanischen Langzeitverhaltens im Rahmen der Zulassung zeigt die Anwendungsgrenzen jedes Produkts. Das Langzeit-Wasserableitvermögen und die noch zulässigen mechanischen Beanspruchungen müssen bei der Anwendung betrachtet werden. Wir möchten daher unser Konzept zur Beurteilung der Langzeiteigenschaften der Kunststoff-Dränelemente vorstellen und auf die resultierenden Anwendungsgrenzen hinweisen. Der daraus resultierende Umfang der relevanten Produkteigenschaften, die beachtet werden müssen, ist erheblich größer als der bescheidene Umfang, der etwa einer CE-Kennzeichnung zugrunde liegt. Auch auf dieses Thema möchten wir in Kürze eingehen. T2 - 11. Leipziger Deponiefachtagung - Planung, Bau, Betrieb und Schließung von Deponien CY - Leipzig, Germany DA - 03.03.2015 PY - 2015 SP - 70 EP - 80 AN - OPUS4-33189 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wöhlecke, Andreas A1 - Müller, Werner T1 - Requirements and performance tests on leak detection systems (LDS) for HDPE geomembranes in landfill covers in Germany N2 - The German landfill ordinance regulates the use of geosynthetics, polymers and leak detection systems (LDS) in the field of landfill engineering in Germany. It governs the certification process and sets a framework for the requirements on these products. The certification guidelines of the BAM Federal Institute of Materials Research and Testing turn these requirements into detailed technical specifications and associated test procedures. The present paper describes the procedure of developing certification guidelines for LDS by BAM and its advisory board. The requirements for the certification of LDS under the terms of the new German landfill ordinance with regard to operation and capability are listed and the technical criteria are described. The performance test for LDS used in connection with geomembranes is discussed in detail. T2 - 10th ICG - International Conference on Geosynthetics CY - Berlin, Germany DA - 21.09.2014 KW - Leak detection systems KW - Landfill cover systems KW - Geomembranes KW - German landfill ordinance KW - Efficiency testing PY - 2014 SP - 1 EP - 8 AN - OPUS4-31865 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Adamczyk, Burkart A1 - Mory, D. A1 - Schilller, D. A1 - Adam, Christian T1 - Chemische Onlineanalyse von Schmelzen im Lichtbogenofen durch LIBS N2 - Die Reduktion von Metalloxiden zum Metall in einer schmelzflüssigen mineralischen Matrix stellt die Grundlage vieler metallurgischer Verfahren dar. Eine Prozessoptimierung und -kontrolle setzt allerdings die genaue Kenntnis der chemischen Zusammensetzung der Schmelze voraus. Im Beitrag wird LIBS als Methode zur Online-Analyse von Hochtemperaturschmelzen vorgestellt. T2 - Schlacken Symposium 2016 CY - Meitingen, Germany DA - 13.10.2016 KW - Online-Analyse KW - LIBS KW - Lichtbogenofen KW - Prozessoptimierung PY - 2016 SP - 49 EP - 58 AN - OPUS4-38155 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Oliver A1 - Adam, Christian T1 - Sewage sludge ashes - composition, mass flows, and recovery potential N2 - Sewage sludge ashes (SSA) represent a possible source of phosphorus (P) and technology metals. So far, the sole external source for P, that is indispensable for all animate beings, is rock phosphate, a finite resource. The EU depends completely on the import from possible politically instable regions. Furthermore, rock phosphate is often contaminated with heavy metals like Cd and U, leading to health and environmental hazards. P recovered from SSA might diminish these problems. SSA of German mono incineration facilities are analyzed for their elemental composition. More than 95% of the emerging SSA is monitored, enabling the determination of complete mass flows of the ashes and their components. Initial results indicate a P recovery potential of 16,000 t/a (11% of the annual P demands for fertilizer production). The concentrations of Cd and U in SSA are one to two Orders of magnitude lower than in rock phosphate and could help to reduce possible hazards. T2 - 14th International waste management and landfill symposium - Sardinia 2013 CY - Cagliari, Italy DA - 30.09.2013 PY - 2013 SP - 1 EP - 5 PB - CISA Publisher AN - OPUS4-29734 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stephan, Ina A1 - Nimz, H. A1 - Peek, R.-D. T1 - Detoxification of salt-impregnated wood by organic acids in a pulping process N2 - The paper descibes a novel method to detoxify pine wood (Pinus silvestris L.) treated with CCB-, CCF- CC-, and Cu-HDO-type salt preservatives. In the process of biological detoxification organic acids produced by strains of Antrodia vaillantii and other brown rot fungi are used for the dissolution of the previously fixed inorganic compounds. These findings are the basis for applying an acid pulping process (FORMACELL) developed by Nimz and Schone (1992) at the BFH, Hamburg, to detoxify salt impregnated wood waste with a mixture of acetic and formic acid. First results achieved with wood chips from treated poles after approximately 20 years of service life show that the obtained pulp contains less than 100 ppm of Cr and Cu. The pulp properties were neither influenced by the Cr and Cu ions nor by the age of the poles. The extracted quantities of Cr and Cu remain with the lignin whereas the acids are evaporated and recycled in the pulping process. T2 - 24th Annual meeting of the International Research Group on Wood Preservation CY - Orlando, FL, USA DA - 1993-05-16 KW - Detoxification KW - Wood waste KW - Disposal KW - Acidification KW - Pulping KW - CCB KW - CC KW - CCF KW - CuHDO PY - 1993 UR - http://www.irg-wp.com/irgdocs/details.aspx?id=d44a2d82-2c63-4a45-bfc3-193e23215b4f N1 - Serientitel: IRG WP – Series title: IRG WP IS - 93-50012 SP - 1 EP - 11 PB - IRG CY - Stockholm AN - OPUS4-4447 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Adam, Christian A1 - Eicher, N. A1 - Hermann, L. A1 - Herzel, Hannes A1 - Mallon, J. A1 - Schaaf, M. A1 - Stemann, J. T1 - Comparative review of ash processes N2 - This report gives technological information about processes for the recovery of phosphorus from sewage sludge ash including mass- and energy balance, process conditions and product quality. The information in this report aim at giving an overview on different concepts for the recovery of phosphorus from sewage sludge ash and are intended to allow a general qualitative comparison between the different technical approaches. This report also describes the technological backgrounds of the processes that were furthermore investigated by life cycle assessment (LCA) and life cycle cost (LCC) analysis. However, most process data stated in this report are site specific data. The LCA/LCC study includes the definition of a common base line for all processes, detailed process modeling and plausibility assessments. Results of the LCA/LCC-studies are reported in deliverables D9.2 und D10.1. PY - 2015 UR - http://p-rex.eu/uploads/media/P-REX_D4_1_Comparative_review_of_ash_processes.pdf SP - 1 EP - 30 AN - OPUS4-34858 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simon, Franz-Georg A1 - Brenneis, Rudolf A1 - Adam, Christian T1 - Verwertungsoptionen für Verbrennungsrückstände biogenen Ursprungs PY - 2009 N1 - Serientitel: Schriftenreihe: Club Niederösterreich – Series title: Schriftenreihe: Club Niederösterreich VL - 4/5 SP - 46 EP - 56 CY - Wien, Österreich AN - OPUS4-20389 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Adam, Christian T1 - Enzymkatalysierte Synthese von Schmierstoffen aus Altfett N2 - Im Rahmen eines vom BMBF geförderten KMU-Innovativ Forschungsprojekts (KKZ 0316199B) konnte in Kooperation mit der Firma Greibo Chemie GmbH ein bio-katalysierter Prozess zur Hydrolyse und Veresterung von gastronomischen Altfetten etabliert werden. Unter Anwendung des Enzyms Candida antarctica lipase-A (CAL-A) kann dieser Prozess mit einem teilweise wässrigen Medium durchgeführt werden was prozesstechnisch einige Vorteile mit sich bringt. Im Gegensatz zu anderen Acyltransferasen ist die CAL-A nicht nur in der Lage die Alkoholyse zu katalysieren sondern auch Fettsäuren zu verestern. Dies eröffnet eine breitere Anwendung des Prozesses auf weitere Produktgruppen und Abfallströme. Es wurden Optimierungen mit modifizierten Enzymen und verschiedenen Fetten und Alkoholen vorgenommen. Des Weiteren wurden die verfahrenstechnischen Parameter optimiert und ein Scale-up auf den 0,5 Tonnen Maßstab durchgeführt. Die aus dem Prozess resultierenden Fettsäureester eignen sich als Motoren- oder Hydraulikbasisöle sowie als Metallbearbeitungsöle. Im Vergleich zu den Mineralölkosten von ca. 1,0 - 1,5 € pro kg muss bei einer Umstellung eines Hydrauliköls auf Fettsäureester (konventionell hergestellt) allerdings bei einem Preis von 3 – 5 € pro kg mit Mehrkosten bei gleichbleibendem Verbrauch gerechnet werden. Für die erfolgreiche Markteinführung müssten vermutlich die durchaus vorhandenen ökologischen Vorteile der Altfett-basierten Produkte beworben werden. T2 - Deutsche Biotechnologietage 2016 CY - Leipzig DA - 26.04.2016 KW - Altfett KW - Enzymkatalyse PY - 2016 SP - 11 EP - 11 PB - Forschungszentrum Jülich CY - 52425 Jülich AN - OPUS4-35969 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Adam, Christian A1 - Brenneis, Rudolf T1 - Schlacken/Aschen - Herstellung von Düngemitteln T2 - 19. Kölner Abfalltage - Von der Abfallwirtschaft zur Rohstoffwirtschaft - Wer sind die Gewinner, wer die Verlierer? CY - Köln, Deutschland DA - 2010-11-02 KW - Klärschlammasche KW - Phosphor KW - Rückgewinnung PY - 2010 IS - Kap. 3.5 SP - 1 EP - 20(?) PB - Kirsten Gutke Verlag AN - OPUS4-22468 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Werner A1 - Wöhlecke, Andreas T1 - Die Zulassung von Geokunststoffen, Polymeren und Dichtungskontrollsystemen nach der neuen Deponieverordnung T2 - 26. Fachtagung - Die sichere Deponie CY - Würzburg DA - 2010-02-18 KW - Geokunststoffe KW - Zulassung KW - Deponieabdichtungen KW - Deponieverordnung PY - 2010 N1 - Geburtsname von Wöhlecke, Andreas: Tuchscherer, A. - Birth name of Wöhlecke, Andreas: Tuchscherer, A. IS - Kap. B SP - 1 EP - 15 CY - Würzburg AN - OPUS4-20923 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völzke, Holger T1 - Stand bei den Behälterbauartprüfungen für das Endlager Konrad N2 - Die Verfügbarkeit von Behältern für die Entsorgung nicht Wärme entwickelnder radioaktiver Abfälle im Endlager Konrad stellt ein wesentliches Element des nationalen Entsorgungskonzeptes für diese Abfallart dar. Grundlage für die Verfügbarkeit geeigneter Behälter sind typspezifische Bauartprüfungen, auf deren Grundlage eine Eignungs-feststellung in Form eines Prüfzeugnisses durch die Bundesgesellschaft für Endlagerung mbH (BGE), vormals Bundesamt für Strahlenschutz (BfS), erfolgt. Die Prüfgrundlagen sind in den durch das BfS (heute BGE) veröffent-lichten „Anforderungen an endzulagernde radioaktive Abfälle“ (Endlagerungsbedingungen) sowie der zugehörigen „Produktkontrolle radioaktiver Abfälle, radiologische Aspekte“ (PK) verankert. Die Eignungsfeststellung für eine Be-hälterbauart ist gleichzeitig die Grundlage für eine Behälterserienfertigung entsprechend den im Prüfzeugnis veran-kerten Spezifikationen und Randbedingungen. Mit den Gesetzen zur Neuordnung der Organisationsstruktur im Bereich der Endlagerung (Mitte 2016) und zur Neuordnung der Verantwortung in der kerntechnischen Entsorgung (Mitte 2017) mit der Finanzierung des Kern-energieausstiegs wurden wesentliche Weichenstellungen im Hinblick auf den anstehenden Rückbau der bereits stillgelegten und in den kommenden Jahren noch stillzulegenden deutschen Kernkraftwerke vorgenommen. Bezüg-lich der nicht Wärme entwickelnden radioaktiven Abfälle führt dies zu einer spürbaren Intensivierung der Anstren-gungen zur Bereitstellung qualifizierter Gebinde für das Endlager Konrad, das nach aktueller Planung bis 2027 sei-nen Einlagerungsbetrieb aufnehmen soll. Dies wiederum führt zu einer erheblichen Verdichtung der Verfahren zur Behälterbauartprüfung, die allen Seiten (Antragsteller, BGE, Gutachter) erhebliche Anstrengungen abfordert. Die Bundesanstalt für Materialprüfung und –forschung (BAM) ist auf Grundlage des Kap. 7 der o. g. „Produktkon-trolle …“ (PK) von der BGE mit den Behälterbauartprüfungen für das Endlager Konrad beauftragt. Hierbei ist eine Vielzahl von Anforderungen zu berücksichtigen, wozu neben den Anforderungen an Abfallbehälter gemäß Kap. 5 der Endlagerungsbedingungen weitere Anforderungen an die Verpackung (Kap. 3.2.2 PK), Kenngrößen (Kap. 3.5.1 PK) und schließlich die eigentliche Prüfung von Behältern/Verpackungen zählt (Kap. 7 PK). Letzteres beinhaltet die umfassende Behälterbeschreibung und –spezifikation, die Behälterauslegung, die thermischen und mechanischen Baumusterprüfungen (z.B. Brand- und Fallprüfungen), und schließlich die qualitätssichernden Maßnahmen für Her-stellung und Betrieb der Behälter. Neben der klassischen Bauartprüfung neuer Behältertypen spielt auch die Prü-fung bereits hergestellter Behälter, sog. Altbehälter, eine wesentliche Rolle, da sich etliche tausend Gebinde bereits in der Zwischenlagerung befinden und nach Möglichkeit für das Endlager Konrad qualifiziert werden sollen. Dieser Beitrag berichtet aktuell über den Umfang und Stand der laufenden Bauartprüfungen bei der BAM unter Be-rücksichtigung der besonderen Herausforderungen und der zuletzt erzielten Fortschritte. Dabei erfordert die paral-lele Bearbeitung der zahlreichen Verfahren einen verstärkten Koordinierungsbedarf hinsichtlich vergleichbarer fach-licher Aspekte sowie hinsichtlich Priorisierung und Ressourceneinsatz. Bei den experimentellen Nachweisen (Fall- und Brandversuche) betrifft das hinsichtlich der Nutzung der Versuchseinrichtungen bei der BAM die Koordination mit anderen Prüfaufträgen, wie z. B. verkehrsrechtliche Baumusterprüfungen. Schließlich erfordern diverse Fach-fragen zur Interpretation der Anforderungen aus Endlagerungsbedingungen und Produktkontrolle intensive Abstim-mungsprozesse zwischen BAM, BGE und Antragstellern. Wichtige Ergebnisse mit übergeordneter Bedeutung wer-den in Form erläuternder Fachnotizen durch die BGE veröffentlicht und können so bei zukünftigen Antragsverfahren berücksichtigt werden. T2 - KONTEC 2019 CY - Dresden, Germany DA - 27.03.2019 KW - Endlager KW - Container KW - Bauartprüfung KW - Konrad PY - 2019 SP - Paper 017, 205 EP - 212 PB - Kontec GmbH CY - Hamburg AN - OPUS4-47667 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schumacher, David A1 - Ou, D. A1 - Ghafafian, Carineh A1 - Zscherpel, Uwe A1 - Trappe, Volker T1 - Wind turbine rotor blade testing by dual-energy laminography N2 - Modern wind turbine rotor blades consist of sandwich shell segments made from glass fiber reinforced polymers. During manufacturing, defects can arise which could lead to failure of the whole component under dynamic mechanical and thermal loads. Hence during operation defects can arise which, if detected, can be repaired locally and in-situ by applying repair patches instead of taking the whole rotor blade down and repair it remotely. This method is much more time and cost effective, since the shut-down time of the energy converter is limited to a minimum. These repair patches can, however, also lead to new defects if not applied optimally. Therefore, it is necessary to control the quality of the repair patches to ensure the best possible restoration of structural integrity of the component. As a rotor blade is an object with a large aspect ratio, X-ray laminography is predestined to provide 3D information of the objective volume. To enhance the amount of information gained from laminographic reconstruction, we use in this study a photon counting and energy discriminating X-ray detector and apply a material decomposition algorithm to the data. By inherently separating the incident spectra within the detection process into two distinct energy bins, the basis material decomposition can provide material resolved images. Choosing glass and epoxy resin as basis materials and numerically solving the inverse dual-energy equation system, the reconstructed laminographic datasets contain highly valuable information about the distribution of the basis materials within the structure. Furthermore, cross- artifacts arising from the limited angle of the projection data can be reduced by this method which allows to investigate structures that were hidden underneath the artefacts. T2 - International Symposium on Digital Industrial Radiology and Computed Tomography – DIR2019 CY - Fürth, Germany DA - 02.07.2019 KW - Laminography KW - Wind energy KW - Fiber reinforced polymer KW - Photon counting detector KW - Repair patch PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-484380 UR - https://www.dir2019.com/portals/dir2019/bb/Tu.3.A.1.pdf SN - 978-947971-06-0 SP - 1 EP - 13 AN - OPUS4-48438 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kullolli, Borana A1 - Baeßler, Matthias A1 - Cuéllar, Pablo A1 - Rica, S. A1 - Rackwitz, F. T1 - An enhanced interface model for friction fatigue problems of axially loaded piles N2 - The shaft bearing capacity often plays a dominant role for the overall structural behaviour of axially loaded piles in offshore deep foundations. Under cyclic loading, a narrow zone of soil at the pile-soil interface is subject to cyclic shearing solicitations. Thereby, the soil may densify and lead to a decrease of confining stress around the pile due to microphenomena such as particle crushing, migration and rearrangement. This reduction of radial stress has a direct impact on the shaft capacity, potentially leading in extreme cases to pile failure. An adequate interface model is needed in order to model this behaviour numerically. Different authors have proposed models that take typical Interface phenomena in account such as densification, grain breakage, normal pressure effect and roughness. However, as the models become more complex, a great number of material parameters need to be defined and calibrated. This paper proposes the adoption and transformation of an existing soil bulk model (Pastor- Zienkiewicz) into an interface model. To calibrate the new interface model, the results of an experimental campaign with the ring shear device under cyclic loading conditions are here presented. The constitutive model shows a good capability to reproduce typical features of sand behaviour such as cyclic compaction and dilatancy, which in saturated partially-drained conditions may lead to liquefaction and cyclic mobility phenomena. T2 - Conference: OMAE CY - Glasgow, Scotland, UK DA - 09.06.2019 KW - Soil-structure interaction KW - Interface PY - 2019 VL - 2019 SP - Article Number: UNSP V001T10A013 PB - ASME CY - Glasgow, Scotland AN - OPUS4-48444 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geißler, Peter A1 - Schwarz, Johannes A1 - Cuéllar, Pablo A1 - Hüsken, Götz A1 - Baeßler, Matthias A1 - Kühne, Hans-Carsten A1 - Morrone, C. T1 - Compaction grouting to improve the pile bearing capacity in non-cohesive soil N2 - The aim of an ongoing research project is to develop a design approach for typical offshore driven piles (e.g. Jacket piles) based on the application of injections by compaction grouting directly at the pile shaft. The paper aims to present the results of laboratory and in-situ tests, which reveal the efficiency and the promising potential of the optimised foundation concept for a more economic dimensioning of pile foundations and to increase their bearing capacity in non-cohesive soil at any moment after installation. T2 - Twenty-ninth International Ocean and Polar Engineering Conference CY - Honolulu, HI, USA DA - 16.06.2019 KW - Offshore Pile Foundation KW - Compaction Grouting KW - Grout KW - Injection Sequence KW - Tensile Capacity PY - 2019 SN - 978-1-880653-85-2 SN - 1098-6189 VL - II SP - 2178 EP - 2184 PB - International Society of Offshore and Polar Engineers (ISOPE) CY - Cupertino, California, USA AN - OPUS4-48505 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schönfelder, Thorsten A1 - Müller, Lars A1 - Komann, Steffen A1 - Wille, Frank ED - Schönfelder, Thorsten T1 - Design assessment of a dual purpose cask for damaged spent nuclear fuel N2 - German package design approvals were granted recently for dual purpose casks (DPC) intended for loading with encapsulated damaged spent nuclear fuel (DSNF). Comprehensive assessment procedures were carried out by the authority BAM with respect to the mechanical and thermal package design, the activity release of radioactive material and quality assurance aspects for manufacturing and operation of each packaging. The objective of each procedure was to verify the Package Design Safety Report (PDSR) and the relevant guidelines fulfils the requirements of the IAEA regulations. Previous approvals of German SNF package designs consider mainly standard fuel assemblies with defined specifications and properties for transport and interim storage. Due to the nuclear power phase-out in Germany all kinds of SNF, e.g. damaged spent fuel rods shall be packed in DPC now. Therefore specific requirements shall be considered in accordance with international experiences including IAEA technical reports. The main requirement for DSNF is a tight encapsulation with specific defined properties under transport and storage conditions. Due to the interim storage period of currently up to 40 years the encapsulation with DSNF in the casks shall also be long term durable. Thus specific loading and drying procedures are necessary and had to be qualified during the approval process. BAM assessed these drying procedures and could confirm the long-term behaviour of the encapsulation and the suitability of the drying equipment. This special equipment was qualified in a “cold handling”. In addition, it was shown that the behaviour of the test equipment used in the qualification process was comparable with the original equipment, e.g. test fuel rods or test encapsulation. In the development of the drying process, experience was obtained in how to put the requirements of the IAEA regulations and related IAEA technical reports into practice. The paper gives an overview of approval assessment and testing experience made by BAM and point out the main resulting requirements on drying processes for these kinds of encapsulations with DSNF. T2 - Proceedings of the 19th International Symposium on the Packaging and Transportation of Radioactive Materials PATRAM 2019 CY - New Orleans, USA DA - 04.08.2019 KW - Assessment KW - Dual purpose cask KW - Spent nuclear fuel PY - 2019 SP - Paper 1204, 1 EP - 10 AN - OPUS4-48685 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Linnemann, Konrad A1 - Müller, Lars A1 - Schönfelder, Thorsten A1 - Komann, Steffen A1 - Wille, Frank T1 - Authority Experience during Design Approval Procedure for Packages Loaded with Special Encapsulations for Damaged Spent Nuclear Fuel N2 - The first German package design approval certificate for a dual purpose cask intended for loading with damaged spent nuclear fuel was issued recently. BAM as part of the competent authority system in Germany carried out a comprehensive assessment procedure with respect to the mechanical and thermal design, the release of radioactive material and the quality assurance aspects of manufacturing and operation. Packages for the transport and storage of radioactive material have been assessed by BAM for many years, thus the common assessment procedure is well-known and good practice. Up to now only SNF without defects or HLW with well-defined properties were designated for long-term Interim storage and transports afterwards. Due to Germany’s nuclear phase out all other kinds of spent nuclear fuel in particular damaged spent nuclear fuel shall be packed as well. Damaged spent nuclear fuel needs a tight closure with Special encapsulations and clearly defined properties in Germany. In addition, these encapsulations shall be long-term durable, because they are not accessible after loading in a packaging within periodical inspections. The main difference to Standard package components is that encapsulations with a permanent closure achieve their specified conditions not after manufacturing but only during operation, after loading and closing. To ensure compliance with the specific conditions, special measures for quality assurance are necessary during operation of each encapsulation, e.g. drying and sealing, which were assessed by BAM. The present paper gives an overview of the conducted assessment from BAM and point out the findings concerning to the special closure lid of the approved encapsulation, which is screwed and welded. A wide verification concept is necessary to show the specific tightness under transport conditions. Together with quality assurance measures during first operation steps these encapsulations with damaged spent nuclear fuel can be handled like standard fuel assemblies in approved package designs. T2 - International Conference on the Management of Spent Fuel from Nuclear Power Reactors CY - Vienna, Austria DA - 24.06.2019 KW - Transport package KW - Design approval KW - Spent nuclear fuel KW - Special encapsulation PY - 2019 SP - 1 EP - 9 AN - OPUS4-48749 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schneider, Ronald T1 - Effect of repair models on risk based optimal inspection strategies for support structures of offshore wind turbines N2 - Owners or operators of offshore wind farms perform inspections to collect information on the condition of the wind turbine support structures and perform repairs if required. These activities are costly and should be optimized. Risk-based methods can be applied to identify inspection and repair strategies that ensure an optimal balance between the expected total service life cost of inspection and repair, and the achieved risk reduction. Such an optimization requires explicit modeling of repairs. In this paper, the impact of different repair models on the results of a risk-based optimization of inspection and repair strategies is quantified in a numerical example considering a jacket-type steel frame subject to high-cycle fatigue. The example showed that, in this specific application, there is no need for detailed modeling of the behavior of repaired welded connections. T2 - 5th International Conference on Smart Monitoring, Assessment and Rehabilitation of Civil Structures (SMAR 2019) CY - Potsdam, Germany DA - 27.08.2019 KW - Risk KW - Reliability KW - Inspection planning KW - Offshore wind turbines PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-488297 UR - https://www.smar2019.org/Portals/smar2019/bb/Th.2.A.4.pdf SP - Paper Th.2.A.4, 1 EP - 8 AN - OPUS4-48829 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hüsken, Götz A1 - Shamsuddoha, Md A1 - Thiele, Marc A1 - Baeßler, Matthias A1 - Kühne, Hans-Carsten T1 - Comparison of cracks formed in scaled grouted connection of offshore energy structures under static and cyclic loads N2 - Global energy consumption will increase in the future necessitating both fossil fuels and renewable energy choices - especially wind energy. Such high energy demand requires installation of offshore energy structures, rigs, platforms and towers, which are susceptible to adverse environmental conditions along with maintenances. Due to their large size and remote locations, cylindrical grouted joints are often adopted between substructure and foundation in these offshore platforms and wind structures such as monopiles. However, these connections are composite structures with exterior sleeve, interior pile and infill mortar. Degradation and settlements were reported inside similar connections, which were installed in last three decades. Besides, grouting in the offshore sites were proven difficult to obtain ideal load bearing capacity. In-situ loading conditions were also found to be affecting the failure mechanism inside such connections. This study aims at characterizing the nature of cracks generated in these grouted connections under both static and cyclic loading. Scaled grouted joints were manufactured using a novel reusable mold, and connections were loaded to failure to visualize the main failure patterns. An assessment between failure under these two types of load is drawn along with comparison to previously available literature. T2 - 5th International Conference on Smart Monitoring, Assessment and Rehabilitation of Civil Structures CY - Potsdam, Germany DA - 27.08.2019 KW - Grouted connection KW - Crack formation KW - Crack pattern KW - Static load KW - Cyclic load PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-487961 SP - Th.2.A.1-1 EP - Th.2.A.1-9 AN - OPUS4-48796 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Feldkamp, Martin A1 - Quercetti, Thomas A1 - Wille, Frank T1 - Fire reference test for IAEA package thermal testing in a propane gas fire test facility N2 - Packages for the transport of radioactive material shall withstand severe accidents. Therefore, the IAEA Regulations define different test scenarios to cover severe hypothetical accident conditions. One of these tests defined in detail is the thermal test, mainly consisting of a 30 minute fully engulfing 800 °C pool fire or an equally severe fire test. The heat fluxes into the package are of significant importance and depend substantially on the fire characteristics and the surface temperature of the package. In order to investigate the heat fluxes over a wide range of surface temperatures during a propane gas fire test and to get information about local fire impact a fire reference package, representing the outer geometry of a specific type of transport cask for radioactive waste, was designed. A closed steel sheet cylinder with a wall thickness of 10 mm was chosen as fire reference package. The cylinder was filled with refractory insulation material and instrumented with thermocouples distributed all over the cylinder. The local steel sheet temperatures measured allow the determination of local as well as global heat fluxes as a function of time and surface temperature. With this fire reference package three open-air propane gas fire tests were performed at BAM’s open air fire test stand. The flame exposure time period was changed for the different fire tests. Furthermore, the wind conditions changed between and during the tests. Test stand parameters like wind shield location and propane gas volume flow were chosen constant for the three tests. The test results were used to determine the changes of heat flux into the fire reference package in relation to the package surface temperature. This data also allows the calculation of local characteristics of the propane gas fire as there are the flame temperature, the fire convection coefficient and the radiation exchange coefficient in a first approach. The recently conducted tests provide an initial picture of local fire characteristics of the propane gas fire test facility. The test shows that the propane gas fire covers the IAEA-fire over a wide range of surface temperatures with the chosen test stand parameters. T2 - 19th International Symposium on the Packaging and Transportation of Radioactive Materials PATRAM 2019 CY - New Orleans, LA, USA DA - 04.08.2019 KW - Fire test KW - Propane gas KW - Calorimetric test KW - IAEA fire testing PY - 2019 SP - Paper 1141, 1 EP - 10 AN - OPUS4-48840 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Simbruner, Kai A1 - Völzke, Holger T1 - Brittle failure of spent fuel claddings under long-term dry interim storage conditions – Preliminary analysis N2 - The evaluation of cladding integrity is a major issue to be demonstrated in Germany for extended interim storage periods up to 100 years and subsequent transportation considering operational and accidental conditions with respect to reactor operation, cask drying and dry interim storage. The chemical reaction between the zirconium fuel cladding and the cooling water in water-cooled reactors produces hydrogen and zirconium oxide. Hydrogen diffuses into the cladding and precipitates as zirconium hydrides when the solubility limit is reached, preferably oriented in hoop direction. At high temperatures during vacuum drying procedures, the hydrides can dissolve. Over a succeeding period of slow cooling with existing hoop stress the hydrides precipitate again, but partly reoriented along the radial direction of the cladding. This change of microstructure in combination with a decreasing temperature (0.5...2 K/year) during (extended) interim storage and additional mechanical load by handling procedures or under accident conditions could lead to a potential cladding embrittlement and consequently increased failure probability. The current research project BRUZL (Fracture mechanical analysis of spent fuel claddings under long-term dry interim storage conditions) has been launched by BAM to investigate potential sudden brittle failure of spent fuel claddings at small deformation under long-term dry interim storage conditions and is presented. T2 - IAEA International Conference on the Management of Spent Fuel from Nuclear Power Reactors CY - Vienna, Austria DA - 24.06.2019 KW - Ageing Management KW - Cladding Embrittlement KW - Extended Storage KW - Ring Compression Test KW - Spent Nuclear Fuel PY - 2019 SP - Paper IAEA-CN-272/49, 1 EP - 8 AN - OPUS4-48869 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Palkowski, Carsten A1 - von Schwarzenberg, Stefan A1 - Simo, Anne T1 - Dynamic testing to better reflect real use for the seasonal performance of air conditioners N2 - In this contribution, a dynamic test method to determine the seasonal performance of invertertype air conditioners has been developed and verified. In comparison to current test standards, where test modes for fixing the compressor speed are required, a dynamic approach is applied with unfixed compressor speed and thus better reflects the performance of air conditioners under real operating conditions. The dynamic tests are conducted in two calorimeter chambers. The indoor chamber is kept at a constant temperature whereas the outdoor chamber is subjected to a temperature profile based on the climate BIN-distribution, representing the reference cooling demand. The proposed dynamic test considers the dynamic control of an air conditioner and delivers results which could indicate the units' performance in the field. T2 - 25th International Congress of Refrigeration 2019 CY - Montréal, Canada DA - 25.09.2019 KW - Seasonal Performance Factor KW - Inverter-type Air Conditioner KW - Dynamic Test Method KW - Real Use Behavior PY - 2019 SN - 978-2-36215-035-7 SN - 1025-9031 SP - 672, 3891 EP - 3899 PB - International Institute of Refrigeration IIR CY - Paris AN - OPUS4-48865 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kullolli, Borana A1 - Cuéllar, Pablo A1 - Baeßler, Matthias A1 - Stutz, H. H. T1 - Modelling and calibration for cyclic soil-structure interface behaviour N2 - The structural performance of many geotechnical systems (e.g. axially-loaded pile foundations), depends on the shearing resistance at the soil interface, which may govern the load bearing capacity of the foundation. Experimental investigations have shown that this interaction is mainly localised within a narrow shear band next to the structure. Under cyclic loading, a contraction of the soil at the interface may arise (net volume loss), possibly leading to a stress relaxation and thus to a reduction of the load bearing capacity (the so-called friction fatigue). Based on the constitutive similarities between soil continua and interfaces, we propose here the adaption of a Generalized Plasticity model for sandy soils for the numerical analysis of interface problems. In this contribution, the results of an experimental campaign for the parameter calibration of the constitutive model are presented. The tests have been conducted with a ring shear device involving different normal stresses, roughness of the steel plates as well as cyclic loading. The new modelling approach shows promising results and has the additional practical advantage that the interface zone and the soil continuum can both be described with the same constitutive model in general boundary value problems. T2 - Konferenz 7th International Symposium on Deformation Characteristics of Geomaterials CY - Glasgow, Scotland DA - 26.06.2019 KW - Soil-structure interaction KW - Offshore foundations PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-489096 DO - https://doi.org/10.1051/e3sconf/20199213007 VL - 92 SP - 13007 EP - 13013 PB - EDP Sciences CY - Glasgow, Scotland AN - OPUS4-48909 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Babutzka, Martin T1 - Investigation of the salinization in marine and offshore environment - test methods and challenges N2 - Salinization and contamination of metal surfaces by chloride-containing aerosols is of great importance with regard to corrosion phenomena in the maritime sector and in offshore applications. Especially Offshore Wind Turbines are exposed to extreme corrosive conditions due to high chloride concentrations in the atmosphere and the resulting high chloride deposition rates. It is of great importance to evaluate to what extent salinization of the surface influences the corrosion protection of coatings and pitting occurrence on stainless steels under atmospheric conditions to evaluate the durability of metallic building structures in offshore and marine environments. The evaluation of the scientific literature and regulatory guidelines has shown that there are still many open questions regarding the contamination of metal surfaces by chlorides. This contribution will discuss how salinization of metal surfaces is evaluated and monitored according to current standards and guidelines. Future challenges concerning test methods and the application of evaluated salinization values and deposition rates will be discussed. T2 - 5th International Conference on Smart Monitoring, Assessment and Rehabilitation of Civil Structures CY - Potsdam, Germany DA - 27.08.20019 KW - Maritime Atmosphäre KW - Versalzung KW - Maritime atmosphere KW - Salinization PY - 2019 SP - Th.2.A.5, 1 EP - 8 PB - SMAR 2019 AN - OPUS4-48905 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Qiao, Linan A1 - Völzke, Holger T1 - Fracture mechanical analysis of a cylindrical cast iron cask N2 - The safety evaluation of cask components made of ductile cast iron includes investigations to prevent brittle fracture. Generally, ductile cast iron is endangered by brittle fracture especially at low temperatures (down to -40°C) and in combination with existing crack-like material defects. An applicable method is the assessment of fracture resistance using fracture mechanics according to the IAEA guidelines. The approach is based on the prevention of fracture initiation. For application of these principles for drop loads, account must be taken both of dynamic stresses within the component and dynamic material behavior. Basically, the dynamic stress intensity factor of postulated pre-existing crack-like defects is compared with the dynamic fracture toughness of the material. Applicable numerical and experimental methods for the safety assessment of cask components are demonstrated for the case of an artificially pre-cracked cylindrical cast iron cask which undergoes dynamic loading conditions as result of the hard impact between the cask and a concrete target. The proposed evaluation procedure is a combination of numerical and experimental steps. Exemplarily, the calculated stress intensity factor is compared with measured fracture toughness values from single edge notched bending specimens. T2 - 19th International Symposium on the Packaging and Transportation of Radioactive Materials (PATRAM 2019) CY - New Orleans, LA, USA DA - 04.08.2019 KW - Ductile Cast Iron KW - Brittle Fracture KW - Cylindrical Cask PY - 2019 SP - Paper 1209, 1 EP - 7 AN - OPUS4-48914 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Johann, Sergej A1 - Kohlhoff, Harald A1 - Gawlitza, Kornelia A1 - Bell, Jérémy A1 - Mansurova, Maria A1 - Tiebe, Carlo A1 - Bartholmai, Matthias T1 - Semi-automatic Gas Measurement Device Based on Fluorescent Multi-gas Sensors N2 - This paper describes the development of a semi-automatic gas measurement device presenting potentially a broad range of applications, noteworthy in the agricultural sector. Non-reversible fluorescent molecular sensors were designed and syn-thesized. Upon, integration into a hydrogel matrix with an optimal ratio of co-solvents, the sensors reacting selectively to ammonia were illuminated by excitation light to produce a concentration-correlated fluorescence emission. An automated mechanical-elec-trical device initiates a given gas mixture and thus simulates con-centrations similar to a threshold value. The aim of this project is to develop a sensor or a low-cost method which can monitor low concentrations of harmful gases and aid in their elimination or regulation in livestock housing, barns or stables. T2 - IEEE Sensors 2019 CY - Montreal, Canada DA - 27.10.2019 KW - gas analysis KW - fluorescence KW - embedded sensor KW - spectroscopy KW - environment KW - agricultural economy PY - 2019 SN - 978-1-7281-1634-1 SP - 88 EP - 92 PB - IEEE AN - OPUS4-49506 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Maiwald, Michael A1 - Völker, J. T1 - Wir dürfen uns nicht zu sicher werden N2 - Die Erwartungen der Prozessindustrie an die NAMUR Open Architecture sind groß, schließlich soll das Konzept der Garant für die digitale Transformation der Branche sein. Im atp-Interview warnt Dr. Michael Maiwald, Fachbereichsleiter „Prozessanalytik“ an der Bundesanstalt für Materialforschung und -prüfung (BAM), allerdings davor, NOA als Allheilmittel zu betrachten. KW - Prozessindustrie KW - NAMUR Open Architecture KW - NOA KW - Industrie 4.0 KW - Digitale Transformation PY - 2019 UR - https://www.atpinfo.de/produkte/2019-atp-magazin-10-2019/ SN - 2190-4111 IS - 10 SP - 40 EP - 43 PB - Vulkan-Verlag GmbH CY - Essen AN - OPUS4-49501 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Potthoff, A. A1 - Unger, Wolfgang T1 - Report on SOP for dispersing nanomaterials in water and report on round robin test. N2 - This report describes a standard operation procedure for dispersion of nanomaterials in liquids prior to toxicological or ecotoxicological testing. Main factors, who determine the state of agglomeration and aggregation of ENMs after dispersion are specific energy input, particle concentration and fluid composition. The method was validated in two round robin tests, where two typical nanomaterials (a nanopowder and a nanodispersion) were investigated. One main result arising out of the data comparison was that only those participants, who were able to follow the instructions in the SOPs completely, received similar results regarding particle size and zeta potential. The SOP is easy to adapt for other types of nanomaterials. The results provide the standardization process and were presented at DIN working group. KW - Dispersion of nano materials KW - AEROSIL® OX50 KW - LEVASIL 50/50 PY - 2019 UR - http://publica.fraunhofer.de/documents/N-541033.html DO - https://doi.org/10.24406/ikts-n-541033 SP - 1 EP - 24 AN - OPUS4-48022 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Casperson, Ralf A1 - Pohl, Rainer A1 - Lohde, Sebastian A1 - Aydoğdu, M. T1 - Zerstörungsfreie Prüfung von Composite-Druckgefäßen mit konventioneller und hochfrequenter Wirbelstromtechnik N2 - Composite-Druckgefäße für den Gefahrguttransport sowie für Wasserstoff- und Erdgasfahrzeuge bestehen aus einem lasttragenden Composite und einer gasdichten, metallischen oder polymeren Barriereschicht (Liner). Zur Untersuchung des Alterungsverhaltens solcher Composite-Druckgefäße wurde in der BAM das interdisziplinäre Themenfeldprojekt COD-AGE durchgeführt. Ziel des Projektes war die Entwicklung von Methoden und Modellen zur Beschreibung und Bestimmung des Alterungsverhaltens von Carbonfaser-Compositen am Beispiel von Druckgefäßen, um eine bessere Vorhersage der Alterung und der sicheren Gebrauchsdauer zu ermöglichen. Ein Schwerpunkt in diesem Projekt war die Bereitstellung geeigneter ZfP-Methoden. Dabei ging es sowohl um versuchsbegleitende Prüfungen, als auch um die mögliche Entwicklung von Prüfeinrichtungen für den späteren praktischen Gebrauch. In dem Vortrag werden Prüfergebnisse der alterungsbegleitenden Wirbelstromprüfung an Composite-Druckgefäßen vorgestellt. In Alterungsversuchen wurden Druckgefäße aus einem ca. 4 mm dicken Aluminiumliner und ca. 8 mm dicker CFK-Ummantelung untersucht. Typisches Einsatzgebiet solcher Druckgefäße sind Atemschutzgeräte der Feuerwehr. Die Druckgefäße wurden sowohl mit konventioneller Wirbelstromtechnik von außen und von innen als auch mit hochfrequenter Wirbelstromtechnik von außen geprüft. Es konnten sowohl Beschädigungen des metallischen Liners, als auch Strukturen des CFK-Geflechts nachgewiesen werden. Eine besondere mechanische Herausforderung bestand in der Prüfung der Innenseite der Liner, da hier eine zylindrische Fläche mit einem Innendurchmesser von 150 mm durch einen Zugang von nur 15 mm Durchmesser geprüft werden muss. T2 - DACH-Jahrestagung CY - Friedrichshafen, Germany DA - 26.05.2019 KW - Wirbelstromprüfung KW - COD-AGE KW - Composite-Druckgefäß KW - CFK PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-481243 SN - 978-3-947971-02-2 VL - 171 SP - 1 EP - 8 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-48124 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brandt, S. A1 - Müller, B. A1 - de Lima Vasconcelos, S. A1 - Plehn, W. A1 - Brozowski, F. A1 - Horn, Wolfgang A1 - Sattler, M. T1 - Präzisierung der Geruchsprüfung für Bauprodukte nach DIN ISO 16000-28 – Untersuchung von Vergleichsmaßstäben N2 - Bauprodukte, die in Innenräumen verwendet werden, sollten die Gesundheit und das Wohlbefinden der Personen die sich darin aufhalten nicht durch das Ausdünsten von Geruchsstoffen stören. Die DIN ISO 16000-28 „Bestimmung der Geruchsstoffemissionen aus Bauprodukten mit einer Emissionsprüfkammer“ (DIN ISO 16000-28) beschreibt umfassend die Möglichkeiten der Geruchsprüfung. In Verbindung mit der Anwendung der VDI-Richtlinie 4302 Blatt 1 „Geruchsprüfung von Innenraumluft und Emissionen aus Innenraummaterialien“ (VDI 4302 Blatt 1) ist sie zur Bewertung der empfundenen Intensität von Bauprodukten mit Vergleichsmaßstab geeignet (Umweltbundesamt 2015). In einem vom Umweltbundesamt (UBA) geförderten Forschungsprojekt der Hochschule für Technik und Wirtschaft Berlin (HTW Berlin) und der Bundesanstalt für Materialforschung und –prüfung (BAM) wurden erstmals verschiedene Vergleichsmaßstäbe miteinander verglichen. Ziel des derzeitigen Folgeprojektes ist nun, Mindestanforderungen an Vergleichsmaßstäbe zu erarbeiten, welche die Reproduzierbarkeit der Ergebnisse erhöhen und mit denen die Norm konkretisiert werden kann. Dieser Beitrag stellt die Untersuchungen und Ergebnisse des ersten Projektes und die Schlussfolgerungen für die Durchführung des zweiten Projektes dar. T2 - 12. Fachkongress der Arbeitsgemeinschaft ökologischer Forschungsinstiute (AGÖF) CY - Hallstadt (Bamberg), Germany DA - 17.10.2019 KW - Geruch KW - Emission KW - Bauprodukte KW - VOC KW - Emissionskammer PY - 2019 SN - 978-3-930576-11-1 VL - 12. Fachkongress SP - 214 EP - 223 PB - Arbeitsgemeinschaft ökologischer Forschungsinstiute (AGÖF) e. V. CY - Springe-Eldagsen AN - OPUS4-49702 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Artinov, Antoni A1 - Bakir, Nasim A1 - Bachmann, Marcel A1 - Gumenyuk, Andrey A1 - Na, S.-J. A1 - Rethmeier, Michael T1 - On the search for the origin of the bulge effect in high power laser beam welding N2 - The shape of the weld pool in laser beam welding plays a major role to understand the dynamics of the melt and its solidification behavior. The aim of the present work was its experimental and numerical investigation. To visualize the geometry of the melt pool in the longitudinal section a butt joint configuration of 15 mm thick structural steel and transparent quartz glass was used. The weld pool shape was recorded by means of a high-speed video camera and two thermal imaging MWIR and VIS cameras. The observations show that the dimensions of the weld pool vary depending on the depth. The regions close to the surface form a teardrop shaped weld pool. A bulge-region and its temporal evolution were observed approximately in the middle of the depth of the weld pool. Additionally, a transient numerical simulation was performed until reaching a steady state to obtain the weld pool shape and to understand the formation mechanism of the observed bulging phenomena. A fixed keyhole with an experimentally obtained shape was used to represent the full-penetration laser beam welding process. The model considers the local temperature field, the effects of phase transition, thermo-capillary convection, natural convection and temperature-dependent material properties up to evaporation temperature. It was found that the Marangoni convection and the movement of the laser heat source are the dominant factors for the formation of the bulging-region. Good correlation between the numerically calculated and the experimentally observed weld bead shapes and the time-temperature curves on the upper and bottom surface were found. T2 - International Congress on Applications of Lasers & Electro-Optics (ICALEO®) CY - Orlando, USA DA - 14.10.2018 KW - Bulging effect KW - High power laser beam welding KW - Numerical modelling KW - Solidification cracking PY - 2019 SP - 1 EP - 8 AN - OPUS4-47139 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine A1 - Gradt, Thomas T1 - High performance polymer materials for tribological applications in hydrogen and methane N2 - The development of hydrogen technologies is a key strategy to reduce greenhouse gas emission worldwide. Power-to-Gas is a challenging solution, in which hydrogen and methane can be used in mobility, industry, heat supply and electricity generation applications. This presentation deals with the tribological behaviour of polymer materials in hydrogen and methane, both in gas and in liquefied form. T2 - ECOTRIB 2019, MaTri'19 CY - Vienna, Austria DA - 12.06.2019 KW - Slidng wear KW - Polymer materials KW - Hydrogen KW - Methane PY - 2019 SN - 978-3-901657-60-3 SP - 228 EP - 229 AN - OPUS4-48253 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schirdewahn, S. A1 - Spranger, Felix A1 - Hilgenberg, Kai A1 - Merklein, M. ED - M., Oldenburg ED - J., Hardell ED - D., Caellas T1 - Tribological performance of localized dispersed X38CrMoV5-3 surfaces for hot stamping of Al-Si coated 22MnB5 sheets N2 - Over the last years, the weight of modern car bodies has risen significantly due to the increasing customers’ demand for comfort and safety equipment. However, this ongoing trend leads to an increasing fuel consumption and thus to higher carbon dioxide emissions. In order to counteract these problems, hot stamping has been established in the automotive industry as a key technolo-gy for lightweight construction, regarding the manufacturing of safety-relevant car body compo-nents. Hot stamped parts are commonly made out of boron-manganese steel 22MnB5, which is initially austenized and subsequently formed and quenched in one process step. As a result, geo-metrical complex structures with an ultimate tensile strength of 1500 MPa are generated. The surfaces of the workpieces are coated with an Al-Si layer to avoid oxide scale formation and to ensure corrosion protection. However, the coating system leads to an increased adhesive wear on the tool surface due to the high thermo-mechanical tool stresses. Therefore, a time and cost con-suming rework of the hot stamping tools is required. The aim of this study is to increase the tribological performance of hot stamping tools by using a laser implantation process. This tech-nique allows the ma-nufacturing of separated, elevated and dome-shaped microstructures on the tool surface in consequence of a localized dispersing of hard ceramic particles by pulsed laser radiation. The generated surface features offer great potential for reducing the tribological load, due to their high hardness and wear resistance. For this purpose, the friction coefficient of un-modified and laser implanted tool surfaces were examined and compared by using a modified pin-on-disk test. In addition, the surfaces were analyzed by optical measurements in order to quantify the amount of wear. T2 - 7th International Conference on Hot Sheet Metal Forming of High-Performance Steel CHS2-2019 CY - Lulea, Sweden DA - 02.06.2019 KW - Laser implantation KW - Surface texturing KW - X38CrMoV5-3 KW - TiB2 KW - Hot-Stamping PY - 2019 VL - 2019 SP - 357 EP - 364 AN - OPUS4-48285 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mohr, Gunther A1 - Seeger, Stefan A1 - Hilgenberg, Kai T1 - Measurement of particle emissions in Laser Powder Bed Fusion (L-PBF) processes and its potential for in-situ process monitoring N2 - Laser Powder Bed Fusion (L-PBF) is a promising additive manufacturing (AM) technology for metal part production especially for complex and lightweight structures or functional designs. In L PBF processes several by-products including welding plume and its condensates, spatter and ejected powder are generated during laser exposure. Investigations of micro- and nano-sized by-products have received little attention in literature. This study focuses on the analysis of particle emissions in L PBF of 316L stainless steel using a scattered light aerosol spectrometer and a fast mobility particle sizer spectrometer during the process which allows for in-situ analysis of particle sizes in the range of 6 nm to 100 µm. A distinct correlation of emission signals to part position can be revealed. In addition, a significant influence of laser scanning vector directions on emission signals is presented. Furthermore, differing powder layer thicknesses can be recognised by deviations in emission signals. T2 - Euro PM 2019 CY - Maastricht, The Netherlands DA - 13.10.2019 KW - Plume KW - Laser Powder Bed Fusion (L-PBF) KW - Additive Manufacturing (AM) KW - Spatter KW - Fume KW - Particle gas emission KW - Aerosol measurements PY - 2019 SP - 1 EP - 7 AN - OPUS4-49388 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Werner, Tiago ED - Madia, Mauro ED - Zerbst, Uwe T1 - Experimental investigation on cyclic R-curves for additively manufactured 316L steel N2 - The present study deals with the experimental characterization of short crack propagation in SLM (selective-laser-melting) manufactured stainless steel. More specifically, the determination of cyclic R-curves is discussed. This describes the dependency of the crack propagation threshold on crack growth during the short crack propagation stage. For metals, the threshold, starting at a material-intrinsic value, increases until it reaches a value independent of the crack length due to crack closure phenomena which build up at that stage. The cyclic R-curve, when used in the frame of a cyclic R curve analysis, characterizes the resistance of a material to fatigue crack growth and the ability to arrest a physically short crack. Thus, it is the link between classical fatigue and fracture mechanics. In the high-cycle-fatigue range, the short crack propagation stage dominates the overall lifetime, i.e., the number of cycles until failure. Below the fatigue limit crack arrest of hitherto propagable micro-cracks will occur. The effort for the experimental characterization of the short fatigue crack propagation behavior and the cyclic R-curve is very high compared to experiments on long crack propagation. A very exact measurement of crack extension is required, since small increments need to be depicted. Pre-cracking must leave a closure free initial crack, since closure must be build up only by the cyclic R-curve. The closure-free status is achieved by compression pre-cracking. The aim of the present study is an insight into the influence of an AM process on the short crack propagation threshold. Cyclic R-curves are experimentally determined at different load-ratios for 316L austenitic steel specimens produced by SLM and conventional manufacturing. Residual stresses are measured in the crack plane and their influence on the cyclic R-curve is discussed. T2 - ESIAM19 CY - Trondheim, Norway DA - 09.09.2019 KW - Fatigue crack growth KW - Additive Manufacturing KW - 316L KW - Cyclic R-curve KW - Laser Powder Bed Fusion KW - AM KW - L-PBF PY - 2019 SP - 1 EP - 8 AN - OPUS4-49416 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Spranger, Felix A1 - Schirdewahn, S. A1 - Kromm, Arne A1 - Merklein, M. A1 - Hilgenberg, Kai T1 - On the influence of tib2, tic and tin hard particles on the microstructure of localized laser dispersed aisi d2 tool steel surfaces N2 - The control of friction and wear is a major concern in many industrial applications. A promising method for a tailored surface modification is the so-called laser implantation technique. This method combines surface texturing and material optimization in one processing step by a localized dispersing of hard ceramic particles using pulsed laser radiation. Wear resistant, protruding micrometric features (implants) with defined geometry can be created in deterministic pattern where needed on highly stressed surfaces, i.e. on forming or cutting tools. However, in order to maintain the implants over the tool’s lifetime, a suitable selection of hard ceramic particles is a prerequisite. They must provide a defect-free Metal Matrix Composite with a high share of homogeneously distributed particles and especially a high implant hardness. In this study TiN, TiC and TiB2 hard particles were compared as implant materials for the first time. By a systematic variation of the pulse power and pulse duration, their dispersing behavior and influence on the material properties of AISI D2 tool steel was investigated. Although all powder materials had grain sizes smaller than 10 µm, it was possible to disperse them by pulsed laser radiation and to obtain defect-free protruding implants. The highest share of dispersed particles (~64 %) was observed for TiB2. By scanning electron microscopy and energy dispersive X-ray spectroscopy, it was also shown that a significant share of the pre-placed particles was dissolved by the laser beam and precipitated as nanometer sized particles within the matrix during solidification. These in-situ formed particles have a decisive influence on the material properties. While the TiN and TiC implants have shown maximum hardness values of 750 HV1 and 850 HV1, the TiB2 implants have shown the highest hardness values with more than 1600 HV1. By X-ray diffraction, it was possible to ascribe the lower hardness values of TiC and TiN implants to high amounts of retained austenite in the metal matrix. By implanting TiB2, the formation of retained austenite was successfully suppressed due to the in-situ formation of TiC particles, which was proven by electron backscatter diffraction. In conclusion, all the implant materials are basically suitable for laser implantation on AISI D2 tool steel. However, TiB2 has shown the most promising results. T2 - 38th International Congress on Applications of Lasers & Electro-Optics CY - Orlando, FL, USA DA - 07.10.2019 KW - Laser implantation KW - Surface texturing KW - AISI D2 KW - TiB2 PY - 2019 SN - 978-1-940168-1-42 SP - 1 EP - 10 AN - OPUS4-49317 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Voigt, Marieke A1 - von Werder, Julia A1 - Meng, Birgit ED - Caprai, V. ED - Brouwers, H. J. H. T1 - Investigation of the zonation of thermally treated ultra high performance concrete N2 - Ultra high performance concrete (UHPC) is characterised by its high compressive strength of more than 150 MPa and its high durability. Due to thermal treatment at 90°C a strength comparable to the 28-days-strength can be achieved immediately after the treatment and in some cases can be even further increased up to 30 %. The explanations for the increase in strength are the accelerated hydration of the clinker minerals and the intensified pozzolanic reaction contributing to a denser microstructure and hence, a high performance in compressive strength. Former research shows that thermal treatment can lead to inhomogeneities in form of a visible zonation within the cross-section. The width of the margin increases with shorter pre-storage time before the thermal treatment and with omitting protective measures against desiccation during the treatment. Specimens exhibiting a zonation typically show a lower compressive strength compared to the undisturbed reference whereas changes in chemistry, mineral content and microstructure were not reported in detail. In this study the zonation of thermally treated UHPC is investigated with respect to its chemistry, mineral composition and microstructure to allow predictions on durability and strength development. Measurements show a change in pore sizes, minerals phase composition and element distribution leading to the visible zonation and weaker bending tensile strength compared to the reference. T2 - 2nd International Conference of Sustainable Building Materials CY - Eindhoven, Netherlands DA - 12.08.2019 KW - UHPC KW - Thermal treatment KW - Zonation KW - Desiccation KW - Microstructure KW - Durability PY - 2019 VL - 2 SP - 185 EP - 193 AN - OPUS4-49479 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Babutzka, Martin A1 - Burkert, Andreas A1 - Heise, Svenja A1 - Heyn, A. T1 - Korrosionsuntersuchungen mit gelartigen Elektrolyten an Zink - Eine innovative Prüfmethodik N2 - Ein neuer Ansatz bei elektrochemischen Korrosionsuntersuchungen kann durch den Einsatz von gelartigen Elektrolyten als Alternative zu wässrigen Prüfelektrolyten beschritten werden. Gelartige Elektrolyte ermöglichen minimalinvasive Untersuchungen an natürlich gebildeten Zinkdeckschichten. Dadurch können korrosionsrelevante Kennwerte ermittelt werden, die Aussagen zur Deckschichtbildung und zur Stabilität von atmosphärisch gebildeten Deckschichten erlauben. In diesem Beitrag wird anhand verschiedener Untersuchungen an Reinzink der Mehrwert von gelartigen Elektrolyten für die Korrosionsforschung und -prüfung verdeutlicht. Darüber hinaus werden neue Erkenntnisse zur Deckschichtbildung von Zink unter atmosphärischen Bedingungen vorgestellt. T2 - GfKORR-Jahrestagung 2019 CY - Frankfurt a. M. DA - 12.11.2019 KW - Zink KW - Gelartige Elektrolyte KW - Korrosionsuntersuchungen KW - Deckschichtbildung PY - 2019 SN - 978-3-935406-71-0 SP - 53 EP - 64 AN - OPUS4-49642 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schnell, A. A1 - Rübner, Katrin A1 - Ihlenfeldt, Toni A1 - Vöge, M. T1 - Leichtgranulate aus heterogenen Bau- und Abbruchabfällen N2 - Mineralische Bauabfälle stellen in den Industrienationen den größten Abfallstrom dar. Allein in Deutschland fallen jährlich mehr als 50 Mio. Tonnen Bauschutt an, der hauptsächlich aus Beton- und Mauerwerkbruch besteht. Dabei nehmen die Verwertungs- und Recyclingquoten bei den bereits etablierten herkömmlichen Einsatzgebieten für aufbereitete Bau- und Abbruchabfälle mit zunehmender Heterogenität des Materials ab. Ein höherwertiges Recycling mit dem Ziel das aufbereitete Material beispielsweise in Betonprodukten einzusetzen erfolgt heute in Deutschland lediglich im Rahmen von Pilotprojekten. So können die groben Körnungen des Betonbruchs als rezyklierte Gesteinskörnung im Beton eingesetzt werden. Besonders eingeschränkte Verwertungsmöglichkeiten liegen für Mauerwerkbruch vor, einem Gemisch aus Beton, Ziegel, Kalksandstein, Porenbeton, Mörtel, Natursteinen und anderen mineralischen Bestandteilen. Die Ursache hierfür ist neben der heterogenen Zusammensetzung des Materials auch dessen feine Kornverteilung, die durch den bei der mechanischen Aufbereitung zwangsläufig anfallenden Feinkornanteil von 30 bis über 40 Prozent bedingt ist. Defizite in der Verwertung bestehen also besonders bei heterogenen feinkörnigen Gemischen. Hier müssen Ansätze gefunden werden, um eine hochwertige Wiederverwertung zu ermöglichen. Dafür ist eine möglichst gute Trennung der einzelnen Materialfraktionen ein bewährter Ansatz. Während Metalle mittels Band- und Wirbelstromabscheidern und leichte Fremdbestandteile über Windsichtung und Dichtesortierung ausgetragen werden können, ist eine Trennung der Materialien Ziegel, Mörtel und Beton, insbesondere für die feinen Fraktionen, derzeit technologisch und wirtschaftlich nicht umsetzbar. Ein rohstoffliches Recycling dieser heterogen zusammengesetzten Abfälle unter Nutzung ihrer chemisch-mineralogischen Zusammensetzung ohne eine vorherige Trennung in die einzelnen Materialfraktionen bietet sich als Alternative an. Ergebnisse zur Herstellung von Leichtgranulaten aus Mauerwerkbruch und Tonen in einem thermischen Prozess ähnlich der Blähtonherstellung wurden bereits mehrfach veröffentlicht. Diese Recycling-Granulate (RCG) könnten unter anderem als leichte Gesteinskörnung für Betone verwendet werden. T2 - 24. Tagung Siedlungsabfallwirtschaft Magdeburg CY - Magdeburg, Germany DA - 18.09.2019 KW - Leichte Gesteinskörnungen KW - Bau- und Abbruchabfälle KW - Mauerwerkbruch KW - Recycling PY - 2019 VL - 2019 SP - 89 EP - 94 PB - Otto-von-Guericke-Universität Magdeburg CY - Magdeburg AN - OPUS4-50189 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Titscher, Thomas T1 - Efficient computational mesoscale modeling of concrete under cyclic loading N2 - Concrete is a complex material and can be modeled on various spatial and temporal scales. While simulations on coarse scales are practical for engineering applications, a deeper understanding of the material is gained on finer scales. This is at the cost of an increased numerical effort that can be reduced by the three methods developed and used in this work, each corresponding to one publication. The coarse spatial scale is related to fully homogenized models. The material is described in a phenomenological approach and the numerous parameters sometimes lack a physical meaning. Resolving the three-phase mesoscopic structure consisting of aggregates, the mortar matrix and the interfaces between them allow to describe similar effects with simpler models. KW - Concrete KW - Fatigue failure KW - Damage KW - Mesoscale PY - 2019 VL - 9 SP - 1 EP - 52 PB - UPC - Universitat Politecnica de Catalunya Barcelona CY - Barcelona AN - OPUS4-50362 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Otto, Peter T1 - Explicit dynamics and regularization in impact simulation N2 - Die Simulation des Materialverhaltens für ein Aufprallproblem erfordert sowohl präzise Methoden für die Kontaktformulierung als auch für die Wellenausbreitung nach dem Aufprall. Das numerische Modell des Aufprallproblems ist schlecht gestellt, weil die plötzliche Änderung der Geschwindigkeiten im Kontaktbereich zu unbegrenzten Beschleunigungen bei gleichzeitig kleiner werdenden Zeitschritten führt. Daraus resultieren Oszillationen in den Kontaktspannungen, die sich im Material ausbreiten. Bei einem dehnratenabhängigen Material, wie z.B. Beton, führen diese Oszillationen zu erheblichen numerischen Fehlern und falschen Vorhersagen für die Festigkeit des Materials. Eine Regularisierung ist daher erforderlich, um die Oszillationen zu vermeiden. Ein weiterer wichtiger Punkt ist die numerische Lösung des Kontaktproblems. Bei der Simulation des Aufprallproblems muss das nichtlineare Kontaktproblem in jedem Zeitschritt gelöst werden. Die Mortar-Methode mit der Segmentierung des Kontaktbereichs hat sich als sehr präzise erwiesen, stellt aber ein rechen- und entwicklungstechnisch aufwendiges Verfahren, vor allem für 3D Probleme, dar. Die numerische Modellierung des nachfolgenden Wellenausbreitungsproblems erfordert kleine Zeitschritte, um die Ausbreitung der Welle genau zu erfassen. Implizite Verfahren sind deshalb zu aufwendig. Explizite Verfahren sind effizient, allerdings nur wenn die Massenmatrix diagonal ist. In diesem Fall wird die Lösung eines linearen Gleichungssystems in jedem Zeitschritt vermieden. In dieser Arbeit wird für die numerische Lösung des Kontaktproblems ein gekoppelter finite Elemente - Non-Uniform Rational B-Spline (FE-NURBS) Ansatz verwendet. In dem gekoppelten Ansatz, wird eine NURBS Kurve bzw. Oberfläche zwischen die im Kontakt befindlichen Körper gebracht. Die Körper sind mit finiten Elementen vernetzt und die NURBS Schicht wird verwendet, um die Kontaktkräfte zu berechnen. Dadurch wird eine glatte isogeometrische Kontaktformulierung erreicht. Folglich kann eine Segmentierung des Kontaktbereichs vermieden und eine effiziente elementweise Integration zur Berechnung der Kontaktkräfte eingesetzt werden. Die Regularisierung des Aufprallproblems erfolgt mit einer nichtlinearen Penalty-Formulierung. Die Penalty-Funktion ist ein Polynom, was einen glatten Übergang zwischen Nicht-Kontakt und Kontakt während des Aufpralls ermöglicht. Die Penalty-Formulierung ist netzabhängig und wird steifer mit feiner werdendem Netz, wobei Oszillationen in den Kontaktpannungen weiterhin nicht auftreten. Zur effizienten Raum- und Zeitdiskretisierung für das Wellenausbreitungsproblem werden Verfahren höherer Ordnung eingesetzt. Explizite Zeitintegration wird kombiniert mit Raumdiskretisierung, die mit spektralen finiten Elementen erfolgt. N2 - The simulation of the structural response for impact scenarios strongly requires an accurate simulation of both the impact event as well as the subsequent wave propagation. The numerical modeling of the impact event is intrinsically ill-posed due to the instantaneous changes of velocities in the contact area, leading to unbounded accelerations for decreasing time steps which causes oscillations in the contact stresses. These oscillations then propagate into the bulk material. Using a rate dependent material model, like concrete, they might lead to significant errors and a wrong prediction of the structural response. A regularization is thus required to avoid oscillations in the contact stresses. Another issue is related to the numerical computation of the contact conditions. In impact simulations, the nonlinear contact computation needs to be evaluated in every time step. A segmentation technique of the contact area is accurate but time consuming and may result in a bottleneck for the simulation and implementation, especially for 3D problems. The modeling of the subsequent wave propagation requires small time steps, which is primarily due to accuracy reasons. Implicit schemes are thus not affordable. Explicit time integration schemes are efficient only for diagonal mass matrices, as in this case no solution of a linear system is required. In this work, a coupled finite element - Non-Uniform Rational B-Spline (FE-NURBS) approach is applied to impact problems. The coupled approach uses an intermediate NURBS layer to compute the contact forces between the contacting bodies discretized by FEs. The advantages of a smooth isogeometric contact formulation are used to compute the contact forces. A segmentation of the contact area is avoided and an efficient element-based integration is used. The impact event is regularized using a mesh dependent nonlinear penalty approach. The penalty function is a polynomial which ensures a smooth transition between the noncontact and the contact state during the impact. For finer meshes, the penalty regularization becomes stiffer while still avoiding artificial oscillations in the contact stresses. Efficient higher order space and time discretizations are used to model the wave propagation. Explicit time integration is combined with higher order spectral element spatial discretization. KW - Explicit dynamics KW - Impact simulation KW - Isogeometric analysis KW - Mortar method KW - Spectral elements PY - 2019 SN - 978-3-920395-70-8 SP - 1 EP - 104 CY - Braunschweig AN - OPUS4-51032 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Habib, Abdel Karim A1 - Kluge, Martin T1 - Experimentelle Untersuchungen zu Schäden an Membranabdeckungen im Biogasbereich N2 - Bei Störfallauswirkungsbetrachtungen an Biogasanlagen muss das Versagen der Membranabdeckung des Fermenters untersucht werden. Hierbei sind insbesondere Risse in derselben hinsichtlich des austretenden Massenstromes an Biogas zu bewerten, ebenso wie der durch eine Zündung resultierende Flammenstrahl. Zurzeit existieren für Membranabdeckungen jedoch keine Erkenntnisse zu realistischen Ausflussziffern für die Massenstromberechnung. Im Leitfaden KAS-32 wird für Störfallauswirkungsbetrachtungen für die Berechnung des austretenden Massenstromes eine Ausflussziffer von 1 und eine „Leckfläche" von 0,6 m2 vorgegeben. Die Anwendbarkeit verfügbarer Modelle zur Berechnung des Flammenstrahls ist bisher ebenso ungeklärt. Um diese Fragestellungen zu untersuchen, wurden in der BAM Versuche zur Bestimmung der Ausflussziffer, sowie der Zündung des austretenden Gases an einem 80 m3 Sack zur Speicherung von Biogas durchgeführt, der aus demselben Material besteht wie die in Biogasanlagen verwendeten Membranabdeckungen. T2 - 14. Fachtagung Anlagen-, Arbeits- und Umweltsicherheit CY - Köthen, Germany DA - 07.11.2019 KW - Biogas KW - Ausflussziffer KW - Membranabdeckung PY - 2019 SN - 978-3-89746-220-5 VL - 2019 SP - 142 EP - 152 AN - OPUS4-50857 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baensch, Franziska A1 - Baer, Wolfram A1 - Wossidlo, Peter A1 - Habib, Abdel Karim T1 - Frequenzanalyse von Schallemission an einem Stahlrohr unter Biegebeanspruchung N2 - Um ein tieferes Verständnis über die Schallemission bei der Entstehung und Ausbreitung von Rissen in Stahlrohrleitungen zu erlangen, wurde ein Stahlrohr der Güte S355J2H im Vierpunkt-Biegeversuch quasistatisch bis hin zum Wanddurchbruch (Leckage) belastet und mittels Schallemissionsmessung und Gleichstrompotentialmessung überwacht. Das Rohrsegment wurde durch einen 90°- Außenumfangskerb in der Mitte der Rohrlänge definiert vorgeschädigt, um davon ausgehend ein stabiles Risswachstum zu induzieren und die Analyse von Schallemission aus Rissereignissen, die am Kerb eintraten, sicherzustellen. Für die Schallemissionsmessung wurden vier Breitbandsensoren max. 105 mm vom Kerb entfernt montiert. Die Signalaufzeichnung erfolgte kontinuierlich und schwellwertunabhängig. Für die Gleichstrompotentialmessung wurde ein Gleichstrom von 300 A eingeleitet und der Potentialabfall über dem Kerb mit fünf Sonden entlang des Kerbs gemessen. Beide Messverfahren identifizieren die Rissinitiierung sowie Veränderungen im Risswachstum. Die detektierten Schallemissionsereignisse werden, unter Berücksichtigung spektraler Eigenschaften, mit fortschreitender Belastung und Rissentwicklung analysiert. Diese Studien wurden im Rahmen des interdisziplinären Forschungsprojekts AGIFAMOR, Aging infrastructure - Faseroptisches Monitoring von Rohrleitungen, an der BAM durchgeführt. T2 - 22. Kolloquium Schallemission und 3. Anwenderseminar Zustandsüberwachung mit geführten Wellen CY - Karlsruhe, Germany DA - 27.03.2019 KW - Schallemission KW - Frequenzanalyse KW - Rissbildung in Stahl PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-476888 SN - 978-3-947971-00-8 VL - 169 SP - 1 EP - 8 PB - Deutsche Gesellschaft für zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-47688 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kurth, Lutz T1 - Determination of measures for a safe production depending on the hazardous properties of explosive substances (pyrotechnic compositions) N2 - During manufacturing and production processes of pyrotechnic compositions, semi-finished devices and regular pyrotechnic articles an inadvertent reaction or even explosion cannot be fully excluded. The optimization of the design of the involved single work processes can only reduce the risk of such a scenario. For doing so, one must consider the respective properties regarding thermal, mechanical, chemical and electrostatic sensitivities of the compositions being processed. One major key parameter in reducing the risks of such an event is to minimize the consequences, if the likelihood of this event cannot be further reduced. Minimizing the consequences in cases of unintended explosions during production processes comprises of construction measures regarding buildings (different walls, orientation etc.), increasing safety distances to other buildings, and lowering the maximum net explosive masses and the number of people per room or production process. Important criteria for defining and setting protection measures are the so-called ‘hazard groups’ (in German ‘Gefahrgruppen’), net explosive masses and the main impacts or hazards (such as blast pressure, heat/radiation and debris). This paper aims at presenting some approaches used in Germany to minimize the impacts of possible reactions or inadvertent explosions during production processes of pyrotechnic compositions and articles in work spaces. This includes also the determination of safety distances and discussions on reducing thermal impacts. T2 - 17th International Symposium on Fireworks CY - Puerto Vallarta, Mexico DA - 06.05.2019 KW - Hazard group KW - Explosions KW - Manufacturing KW - Pyrotechnic KW - Safety PY - 2019 SN - 978-1-988778-05-1 VL - 2019 SP - 202 EP - 216 AN - OPUS4-48032 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kurth, Lutz T1 - The assessment of the dangerous characteristics of pyrotechnic Composition and articles (for safe production) N2 - To minimize hazards during manufacturing and production processes of pyrotechnic compositions, semifinished and regular pyrotechnic articles, related properties of the pyrotechnic compositions must be determined and assessed with focus on those parameters that influence the exothermic reactions and explosion phenomena. Estimated impacts of these reactions as well as the sensitivities towards Initiation by thermal, mechanical or electrostatic stresses are relevant for this assessment. Since the 50s of the last century so-called ‘Hazard Groups’(in German ‘Gefahrgruppen’) of pyrotechnic compositions were defined, to assess these properties which aim was to set appropriate safety measures for production purposes. This system of Hazard Groups is currently under review to determine if they are still relevant with the latest composition developments in this field and still represent the state of the art. Several necessary changes and new approaches have already been identified. The new system will contain the following Hazard Groups, all with associated protection measures: 1.1 (and further sub-groups 1.1-1, 1.1-2 and 1.1-3), 1.2, 1.3 and 1.4. This structure is aligned to the international principles for the classification of such substances according to the TDG and GHS regulations. New or updated test and assessment criteria for these (sub-) groups are under development, and comprise of aspects such as sensitivity towards friction, impact, temperature and explosion effects. This paper aims at giving an overview of this system of hazard Groups in Germany to optimize production safety including pyrotechnic compositions. An overview of this system is given along with example cases for testing and assessment, including a short differentiation of the energetic processes during the reactions. T2 - 17th International Symposium on Fireworks CY - Puerto Vallarta, Mexico DA - 06.05.2019 KW - Sensitivities KW - Pyrotechnic KW - Assessment KW - Explosion phenomena PY - 2019 SN - 978-1-988778-05-1 VL - 2019 SP - 217 EP - 228 AN - OPUS4-48035 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Otremba, Frank A1 - Romero-Navarrete, José A. T1 - Experimental modeling of railway car wheel-forces during turning N2 - An experimental testing rig has been proposed to study the dynamic interaction between a liquid cargo and the carrying vehicle during turning maneuvers. The basic operational principle of the testing rig consists in simulating the lateral accelerations associated to turning maneuvers through the use of a tilt table. While the experimental capabilities of the testing rig include the analysis of the effects of the cars on the whole transport infrastructure, including sleepers and ballast, a first use of the rig considered the effect of sloshing cargo on the level of dynamic forces transmitted to the rails. Such test was used to validate a simplified theoretical approach consisting of a two degree-of-freedom double pendulum mechanical system, where a simple pendulum, representing the sloshing cargo, is articulated to the spring-supported vehicle chassis, which is modelled as an inverted torsional pendulum. While the theoretical results exhibit a high correlation with the experimental data, the main discrepancy between both outputs, relates with the frequency of the residual vibration, once the lateral acceleration input is ceased. Such difference in frequency, would imply an underestimation of the number of loading cycles to which the infrastructure is subjected. On the other hand, the peak values are within acceptable difference levels. T2 - IEEE/ASME Joint Rail Conference CY - Snowbird, Utah, USA DA - 09.04.2019 KW - Railway KW - Wheel-forces KW - Turning PY - 2019 SP - 1 EP - 8 PB - ASME AN - OPUS4-47880 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pirskawetz, Stephan A1 - Gründer, Klaus-Peter A1 - Kadoke, Daniel A1 - Unger, Jörg F. T1 - Überwachung von Stahlbetonbrücken - Ein Modellprojekt N2 - Die Brücken im Netz der Bundesverkehrswege sind überwiegend in einem ausreichenden bis guten Zustand. Allerdings steigt der Unterhalts- und Sanierungsaufwand aufgrund des inzwischen hohen Alters vieler Brücken sowie des ständig wachsenden Schwerlastverkehrs. Techniken zur Einschätzung der verbleibenden Lebensdauer von Brücken sowie zur dauerhaften Beobachtung des Tragverhaltens bzw. des Erfolges von Sanierungsmaßnahmen werden daher für den sicheren und wirtschaftlichen Betrieb dringend benötigt. Zur Evaluierung dafür geeigneter holistischer Ansätze wurde in der BAM das Projekt BLEIB - Bewertung, Lebensdauerprognose und Instandsetzung von Brückenbauwerken - ins Leben gerufen. Ein zentrales Ergebnis des Projektes ist eine extern vorgespannte Stahlbetonbrücke als Zweifeldträger mit einer Gesamtlänge von 24 m, die für den Test verschiedenster Sensorsysteme, zur Validierung numerischer Modelle und zur Erprobung von Sanierungs- und Verstärkungsmaßnahmen entwickelt wurde. Für die Simulation unterschiedlicher Schädigungsgrade kann die Vorspannung der Brücke variiert werden. Die Brücke wird mit beweglichen Gewichten belastet und über einen Shaker zum Schwingen angeregt. Das Brückenmodell wurde bewusst geschädigt, indem die Vorspannung der Struktur erstmalig schrittweise bis auf null reduziert wurde. Unter der Eigenlast verformte sich die Brücke, wodurch eine Rissbildung im Beton einsetzte. Die Zugspannung, die zuvor durch die Vorspannung aufgenommen wurde, übernahm Schritt für Schritt der Beton. Als die Zugspannungen die relativ geringe Zugfestigkeit des Betons überstiegen, begann dieser zu reißen und die schlaffe Bewehrung der Struktur nahm die Spannungen auf. Dieser Versuch wurde unter anderem von Schallemissionsmessungen begleitet. Der Rissbildungsprozess konnte damit, bei gleichzeitiger Aufzeichnung der Vorspannung, früh detektiert und die Risse geortet werden. Die Ergebnisse korrelieren gut mit den Ergebnissen der stereophotogrammetrischen Verformungsmessungen der Struktur. T2 - 22. Kolloquium Schallemission und 3. Anwenderseminar Zustandsüberwachung mit geführten Wellen CY - Karlsruhe, Germany DA - 27.03.2019 KW - Brückenmonitoring KW - Schallemissionsanalyse PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-477878 SN - 978-3-947971-00-8 VL - 169 SP - 1 EP - 5 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-47787 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Vahlsing, Thorsten A1 - Raum, Hanne A1 - Casperson, Ralf A1 - Pohl, Rainer A1 - Heckel, Thomas A1 - Beilken, D. A1 - Dilz, K. A1 - Rühe, S. T1 - FE-simulation of eddy current signals produced from basic model cracks for running surface rail defects N2 - Non-destructive testing for surface crack detection and head check depth quantification at the gauge corner of railway tracks can be achieved using eddy current methods. With the extension of the tested zone to the running surface, rail defect signal types other than head checks can be measured. Due to their mostly irregular shape, a quantitation based on a calibration against regular test cracks of varying depth may not be linear. Estimates of the expected influence of more complex crack patterns may be obtained by a finite element simulation of sufficiently simple limiting cases, like two displaced or intersecting cracks or a simply branched or flexed crack. As a first step, a 3D finite element model of the HC10 eddy current probe distributed by Prüftechnik Linke und Rühe (PLR), Germany was built and verified against measured results from an (easily fabricated) reference block with isolated long cracks. T2 - 15th Railway Engineering Conference CY - Edinburgh, UK DA - 03.07.2019 KW - Finite element analysis KW - Eddy current testing KW - Rail inspection PY - 2019 SP - 1 EP - 11 AN - OPUS4-48529 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz A1 - Said, Samir T1 - Measurement of slab track behaviour at different sites N2 - Measured train passages and hammer impacts in combination with track-soil calculation have been successfully used for the detection of damaged slab tracks. This approach is now extended to intact slab and ballast tracks. The vibrations of many tracks have been measured at several levels from rail, sleeper, track plate, base plate, base layer to the subsoil by velocity or acceleration sensors. The time histories have to be integrated once or twice to get the displacements. The displacement signals include an arbitrary time-dependent shift which must be eliminated or respected in the interpretation. On the other hand, the calculation of slab and ballast tracks have been done in frequency-wavenumber domain. The displacements along the track and the frequency-dependent compliance transfer functions can be calculated. The latter can be compared with the results of the hammer impacts on the track. The deformation of the track can be transformed to time histories for a whole train and compared to the measured train passages. Many slab (and ballast) tracks have been measured at different sites. The displacements of the tracks are presented, and the following parameters have been analysed in the measurement results: slab track vs. ballast track, different types of slab tracks, damaged slab tracks, different trains, switches at different measuring points, an elastic layer, the mortar layer, different soils at different places. The soil should have the dominant influence on the track-plate displacements. Slab and ballast track yield also big differences in maximum displacement and width of deformation. Some of the preceding aspects will be analysed in comparison of measurement and theory. T2 - 26th International Congress on Sound and Vibration (ICSV26) CY - Montreal, Canada DA - 07.07.2019 KW - Displacements KW - Slab track KW - Train passage KW - Hammer impact KW - Vibration measurements PY - 2019 SN - 978-1-9991810-0-0 SN - 2329-3675 SP - T15RS01_316_1 EP - T15RS01_316_8 PB - Canadian Acoustical Association CY - Montreal, Kanad AN - OPUS4-48498 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Al-Neshawy, F. A1 - Ferreira, M. A1 - Bohner, E. A1 - Ojala, T. A1 - Sjöblom, V. A1 - Niederleithinger, Ernst A1 - Effner, Ute A1 - Puttonen, J. T1 - Design, Construction and NDT of a Mock-up for Reinforced Concrete Walls in NPP N2 - Construction methods, environmental stressors, and aging factors are the main causes for defects of reinforced concrete in nuclear power plants (NPP). These defects are typically occurred as corrosion of reinforcement steel, delamination, cracks, malfunction of post-tensioning or steel composite systems etc. Some of the challenges for assessing the performance of these structures by nondestructive testing methods (NDT) are that the assessment could be performed only during the annual overhauls when testing is time-limited and uncertainty of the accuracy and reliability of the available NDT testing devices combined with the lack of the international uniformity of the methods used for NDT tests. To overcome these challenges, a mock-up wall representing a section of the concrete containment of the NPP was built. The mock-up wall included simulated defects, which mimic the most common types of defects in NPP concrete structures such as dimensional errors, honeycombing, delamination, defects adjacent to the steel liner and voids in grouted tendon ducts for the post-tensioned structures. This paper introduces the design and construction of the wall including the concrete properties, reinforcement, tendon ducts and the types of the simulated defects. The paper also introduces the NDT methods and techniques that are suitable for assessing the condition of the mock-up wall under the real environmental conditions. These techniques include mechanical methods as rebound hammer, ultrasonic and electromagnetic methods. This mock-up wall will enable to investigate reliably available NDT methods and experts’ skills providing also an important and very much need educational platform for future NDE experts. T2 - SMIRT-25 CY - Charlotte, NC, USA DA - 04.08.2019 KW - NDE KW - Defects KW - Thick-walled KW - Concrete KW - Deterioration KW - Steel liner PY - 2019 SP - 1 EP - 12 AN - OPUS4-48965 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thiele, Marc A1 - Hille, Falk A1 - Makris, Ruben ED - Helmerich, Rosemarie ED - Ilki, A. ED - Motavalli, M. T1 - Comparison of fatigue crack detection methods for high-cyclic loaded steel structures N2 - At present, to produce renewable energy offshore wind farms play an important role. The available space combined with the more valuable wind conditions make offshore locations very attractive for wind powered energy production. In Europe a significant number of offshore wind farms already exist, especially in the North and Baltic Sea. In future this trend will continue, and further offshore wind farms will be built. The majority of offshore wind turbines are mounted on steel foundation structures. Due to the high-cyclic loading by wind and waves fatigue stress plays a substantial role regarding structural safety. Besides the consideration of fatigue within the design process, to monitor existing steel structures for potential fatigue cracks during their life time is a major topic and a challenge. For the structures of the offshore wind turbines are large and partially under water effective reliable methods for the detection of fatigue cracks are required. This contribution presents investigations on different crack detection methods applied at high-cycle fatigue tests on small-scale welded steel samples as well as on large-scale welded steel components. The tests were conducted at the BAM laboratories. For crack detection mainly three different methods were used and compared. The first method regards to the measurement of strain by conventionally strain gauges. Secondly, the crack luminescence was used as a new and effective optical method for surface monitoring. And finally, crack detection by pressure differentials of the inner and outer section of tubular steel elements was investigated. A comparison study will emphasize the advantages and disadvantages of the different methods and show which of the described methods is potentially more suitable for an application on real offshore wind structures. T2 - 5th International Conference on Smart Monitoring, Assessment and Rehabilitation of Civil Structures CY - Potsdam, Germany DA - 27.08.2019 KW - Fatigue KW - Steel structures KW - Crack detection PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-489433 SP - Th.2.A.1-1 EP - Th.2.A.1-8 AN - OPUS4-48943 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niederleithinger, Ernst A1 - Maak, Stefan A1 - Mielentz, Frank A1 - Effner, Ute A1 - Strangfeld, Christoph A1 - Timofeev, Juri T1 - Review of recent developments in ultrasonic echo testing of concrete N2 - Ultrasonic methods are used in concrete investigations since decades. While being limited to transmission testing in the laboratory for a while, in-situ echo measurements for structural investigations and condition assessment have made their way into practical application in the past 20 years. However, several challenges remain. On one side, there are technical issues as limitations in depth of penetration, resolution and imaging capabilities. On the other side there are still gaps in validation, standardization and certification, which are limiting the applicability in condition/load capacity assessment. This review reports a couple of developments which will help to overcome these issues. This includes technical developments as new devices which are easier to handle on site or giving a much deeper penetration depth (e.g. the LAUS device at BAM) as well as improvements in imaging by hardware update (e. g. air coupled ultrasound or coded signals) or new software (e. g. RTM imaging). To foster the application in real world projects we are as well working on standardization by developing new reference specimen with international partners which will ensure world-wide comparability of ultrasonic and other methods and quality assurance codes. Further, non-destructive methods are being used to update probabilistic models used for the reassessment of existing structures to support the structural engineer’s decisions. T2 - SMAR 2019 CY - Potsdam, Germany DA - 27.08.2019 KW - Engineered Barrier System (EBS) KW - Ultraschall KW - NDT KW - Re-assessment of exiting bridges PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-489686 SP - 1 EP - 6 AN - OPUS4-48968 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Mike A1 - Ballheimer, Viktor A1 - Wille, Frank A1 - Zencker, Uwe T1 - Numerical approach to determine a package dependent bar length for the iaea pin drop test N2 - The Federal Institute for Materials Research and Testing (BAM) is assessing the mechanical and thermal safety performance of packages for the transport of radioactive materials. Drop testing and numerical calculations are usually part of the safety case concepts, where BAM is performing the regulatory tests at their own test facility site. Among other mechanical tests the 1 meter drop onto a steel puncture bar shall be considered for accident safe packages. According to the IAEA regulations “the bar shall be of solid mild steel of circular section, 15.0 ± 0.5 cm in diameter and 20 cm long, unless a longer bar would cause greater damage…”. Particularly with regard to the German transport- and storage cask designs, often made from ductile cast iron, an accurate determination of the puncture bar length to guarantee a load impact covering the worst case scenario can be imperative. If the fracture mechanical proof for the cask material shall be provided by a test, small deviations in the concentrated load applied can be decisive for the question if the cask fails or not. The most damaging puncture bar length can be estimated by iterative procedure in numerical simulations. On the one hand, a sufficient puncture bar length shall guarantee that shock absorbers or other attachments do not prevent or reduce the local load application to the package, on the other hand, a longer and thus less stiff bar causes a smaller maximum contact force. The contrary influence of increasing puncture bar length and increasing effective drop height shall be taken into account if a shock absorber is directly placed in the target area. The paper presents a numerical approach to identify the bar length that causes maximum damage to the package. Using the example of two typical package masses the sensitivity of contact forces and puncture bar deformations to the initial length are calculated and assessed with regard to the international IAEA package safety requirements. T2 - PATRAM 2019 CY - New Orleans, LA, USA DA - 04.08.2019 KW - IAEA KW - 1-m-punch-bar-drop-test KW - Numerical approach KW - Bar length KW - Finite element analysis PY - 2019 UR - https://www.inmm.org/INMM-Resources/Proceedings-Presentations/PATRAM-Proceedings.aspx SP - 1 EP - 10 AN - OPUS4-49016 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rolle, Annette A1 - Ballheimer, Viktor A1 - Neumeyer, Tino A1 - Wille, Frank T1 - Application of leakage rates measured on scaled cask or component models to the package containment safety assessment N2 - The containment systems of transport and storage casks for spent fuel and highlevelradioactive waste usually include bolted lids with metallic or elastomeric seals. The mechanical and thermal loadings associated with the routine, normal and accident conditions of transport can have a significant effect on the leak tightness of such containment system. Scaled cask models are often used for providing the required mechanical and thermal tests series.Leak tests have been conducted on those models. It is also common practice to use scaled component tests to investigate the influence of deformations or displacements of the lids and the seals on the standard leakage rate as well as to study the temperature and time depending alteration of the seals. In this paper questions of the transferability of scaled test results to the full size design of the containment system will be discussed. T2 - 19th International Symposium on the Packaging and Transportation of Radioactive Materials PATRAM 2019 CY - New Orleans, LA, USA DA - 04.08.2019 KW - Leakage rate KW - Transport packages KW - Seals KW - Radioaktive PY - 2019 SP - Paper 1147, 1 AN - OPUS4-49053 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Komann, Steffen A1 - Ballheimer, Viktor A1 - Quercetti, Thomas A1 - Scheidemann, Robert A1 - Wille, Frank T1 - Design assessment by bam of a new package design for the transport of snf from a german research reactor N2 - For disposal of the German research reactor of the Technical University Munich FRM II a new transport and storage cask design was under approval assessment by the German authorities. The Bundesanstalt für Materialforschung und -prüfung (BAM) assessed the mechanical and thermal package safety and performed drop tests. The activity release approaches and subjects of quality assurance and surveillance for manufacturing and operation of the package were assessed by BAM as well. The cask body is made of ductile cast iron and closed by two bolted lid systems with metal seals. The material of the lids is stainless steel. On each end of the cask a wood-filled impact limiter is installed to reduce impact loads to the cask under drop test conditions. In the cavity of the cask a basket for five spent fuel assemblies is arranged. For the safety case a combination of experimental testing and analytical/numerical calculations were applied. In total, four drop tests were carried out at the BAM large drop test facility. Two tests were carried out as a full IAEA drop test sequence consisting of a 9m drop test onto an unyielding target and a 1m puncture bar drop test. The other two drop test were performed as single 9m drop tests and completed by additional analyses for considering the effects of an IAEA drop test sequence. The main objectives of the drop tests were the investigation of the integrity of the package and its safety against release of radioactive material as well as the test of the fastening system of the impact limiters. Furthermore, the acceleration and strain signals measured during the tests were used for the verification of Finite-Element-Analysis (FEA) used for the safety analysis of the package design. The finite-element models incorporated in the package design safety report include the cask body, the lid system, the inventory and the impact limiters with the fastening system. In this context special attention was paid to the modeling of the encapsulated wood-filled impact limiters. Additional calculations using the verified numerical models were done by the applicant and assessed by BAM to investigate e.g. the brittle fracture of the cask body made of ductile cask iron within the package design approval procedure. This paper describes the package design assessment from the view of the competent authority BAM including the applied assessment strategy, the conducted drop tests and the additional calculations by using numerical and analytical methods. T2 - 19th International Symposium on the Packaging and Transportation of Radioactive Materials PATRAM 2019 CY - New Orleans, LA, USA DA - 04.08.2019 KW - Numerical modelling KW - Drop test KW - Assessment method KW - Ductile cast iron KW - Package design KW - Experimental testing PY - 2019 SP - Paper 1176, 1 AN - OPUS4-49054 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auster, Jürgen A1 - Müller, Karsten A1 - Gründer, K.-P. T1 - Dynamic impact tests on materials & components of RAM packages - Advanced experimental and measurement methods N2 - In accident scenarios of transport packages or hypothetical crashes of containers in a storage facility or repository, the materials resistance against dynamic failure of the involved components is a deciding factor for package and container integrity during the handling, transport and storage for each type of radioactive material. For example, different dynamic impact tests on containers and components like lid sealing systems and specimens made of ductile cast iron and shock-absorbing materials are carried out by BAM. In order to perform dynamic impact tests with packages and its parts BAM operates two free-fall drop test facilities with maximum capacities of 200 t and 55 t, and a test bench for guided drop tests. This latter drop test machine enables a clearly specified component loading by a precisely positioned test object or drop weight and has been used recently for numerous investigations. The paper gives an overview of the wide range of experimental testing methods carried out within guided Impact and bending tests. Examples of methodological challenges are presented, especially such experimental analysis of dynamic impact conditions. In addition to known applied methods of dynamic, non-contact displacement measurements like high-speed 3-D surface deformation a recently patented 2-D tracking method is presented. By means of in-situ determination of fracture parameters with relevance to the materials stress intensity factor, the method has been successfully applied for a typical specimen geometry. Also shown are the possibility of detecting in-situ He-leakage rates on laterally impact loaded lid sealing systems as well as a method of acceleration sensor-temperature control under test conditions in the low temperature range. T2 - 18th International Symposium on the Packaging and Transportation of Radioactive Materials PATRAM 2019 CY - New Orleans, LA, USA DA - 04.08.2019 KW - Dynamic impact tests KW - Materials KW - RAM packages KW - Advanced experimental KW - Measurement methods PY - 2019 SP - Paper 1374, 1 EP - 10 AN - OPUS4-49067 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Martin A1 - Schilling, O. A1 - Kuschke, Christian A1 - Darnstädt, A. A1 - Schubert, Sven A1 - Günther, U. A1 - Wille, Frank T1 - Requirements for management systems for manufacturing of transport packages: the new revision of BAM-GGR 011 guideline N2 - In accordance with IAEA SSR-6 para 306 a management system shall be established and implemented to ensure compliance with the relevant provisions of the IAEA regulations. BAM has issued an update of the guideline: the BAM-GGR 011. The new revision describes necessary quality assurance measures for design, manufacture, testing, documentation, use, maintenance and inspection of packagings for package designs requiring competent authority approval for the transport of radioactive material. The measures can be categorised as system-related and design-related. They are independently approved and monitored by the German competent authority BAM and its authorised expert (BAM/T). The qualification of the organisation applying for the design approval certificate is reviewed in the context of the design approval procedure. The quality assurance measures for manufacture consist of three main steps. Pre-assessment of manufacturing documents such as quality plans, specifications etc., Manufacturing inspections according the pre-assessed documents and inspection before commissioning including documentation review. Periodic inspections during operation as well as relevant specifications for use and maintenance ensure that the properties specified in the approval certificate are preserved over the package life time. Special provisions for the return on experience regarding operational feedback for design, manufacture, use, maintenance and inspection are given. Special focus shall be given here to the rearranged and meanwhile established system of manufacturing inspections. This includes more transparent roles for a) the Producers authorised inspection 11282 representative, b) the independent inspection expert (S), acting on behalf of the manufacturer with acceptance of BAM, and c) BAM or its authorised expert (BAM/T). Additional attention shall be drawn to the management of deviations during manufacturing and provisions for maintenance and periodic inspections. T2 - 19th International Symposium on the Packaging and Transportation of Radioactive Materials PATRAM 2019 CY - New Orleans, LA, USA DA - 04.08.2019 KW - Quality assurance KW - Transport KW - Manufacturing KW - Surveillance KW - Radioactive material PY - 2019 SP - Paper 1128, 1 AN - OPUS4-49059 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Karsten A1 - Quercetti, Thomas A1 - Borch, Jörg-Peter T1 - Fire tests of RAM packages and containers under high thermal load N2 - Fire testing is an essential part of the hypothetical, cumulative mechanical and thermal test conditions that shall guarantee package safety in severe accidents. Within regulatory approval of transport or storage packages for radioactive material, specific thermal load tests are required in accordance to licensing conditions and international standards, respectively. The specifications of these thermal tests are based on test conditions with equivalent heat input to that of a hydrocarbon fuel fire. In the past, light heating oil, diesel or kerosene was mostly used as the fuel to generate the pool fire. In accordance with IAEA regulations for a fire in an accident, the temperature of 800 °C over a period of 30 minutes must be fulfilled. Furthermore, the delivery acceptance criteria for containers in nuclear waste repositories could reach for example average temperatures of 800 °C during a period of one hour in combination with defined requirements on activity release. BAM as a scientific and technical German federal government institute operates an open air Technical Safety Test Site for experimental investigations of dangerous good and its containment. In this areal a large fire test facility is under operation. Liquid Propane is utilized as fuel which is pumped via pipelines from a central storage tank to the fire exposed test facility areas. In the ring burner system, the gas is released from nozzles, and ignited by ignition burners. The paper includes examples of fire test performance with prototypes of a transport package and a storage container, respectively. In preparation of the thermal load, calorimeter tests have been performed using test specimens of appropriate size and behavior. For the fire test scenario is demonstrated that the IAEA thermal test requirements are fulfilled. T2 - 19th International Symposium on the Packaging and Transportation of Radioactive Materials PATRAM 2019 CY - New Orleans, LA, USA DA - 04.08.2019 KW - IAEA Thermal Test KW - Thermal package testing KW - Transport package KW - Container for radioactive waste PY - 2019 SP - Paper 1298, 1 EP - 6 AN - OPUS4-49093 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wille, Frank A1 - Ballheimer, Viktor A1 - Apel, Andreas A1 - Kuschke, Christian A1 - Moutarde, M. A1 - Desnoyers, B. A1 - Kalinina, E. A1 - Ammerman, D. T1 - ISO-Standard and IAEA guidance material for package load attachment Points - Current approaches and developments N2 - For transport package design and operation according to the IAEA regulations, the package shall be securely stowed and its retention system shall be capable to withstand load conditions of routine transport. The supporting IAEA Advisory Material SSG-26 provides information how to do that. Up to now package designers in different countries use other load factors for the design of attachment points than those specified in the IAEA guidance material. In particular the acceleration values vary between different countries and lead to difficulties during the validation of foreign approval certificates. Therefore the IAEA started a discussion process to review the existing guidance text. An international working group was constituted in 2013. Representatives came from different stakeholders, e.g. transport operators, competent authorities and modal organizations. The discussions concluded especially on the transport conditions which has to be considered for stowage design, including on the one hand the relevance of the load factors used for strength and fatigue analysis and on the other hand the criteria which have to be considered for the attachment points. The proposed acceleration values will be compared to those measured during recent multi-modal testing by Sandia National Laboratories that measured the acceleration levels experienced by a spent fuel flask during heavy-haul truck, sea, and rail transport. The ISO standard 10276 is dealing with the load attachment systems of packages as well. This standard considers the trunnion design, manufacturing and operational aspects. The regular standard revision phase started in 2017. An expert group discussed new state-of-the-art technology, different analysis approaches for strength and fatigue analysis and proposed revised text for the ISO standard for international discussion. The finite-element analysis approach incl. appropriate acceptance criteria are described and referenced. The paper describes relevant tie-down aspects, gives background argumentation relevant to analysis approaches, and tries to support harmonized application of the revised IAEA guidance material and the future revised ISO standard. T2 - 19th International Symposium on the Packaging and Transportation of Radioactive Materials PATRAM 2019 CY - New Orleans, LA, USA DA - 04.08.2019 KW - Load attachment KW - Stowage KW - Trunnion KW - Bolt design KW - Retention KW - Acceleration KW - Transport KW - Load cycles PY - 2019 SP - Paper 1130, 1 EP - 10 AN - OPUS4-49095 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wille, Frank A1 - Debruyne, M. A1 - Eckert, B. A1 - Gauthier, F. A1 - Ben Ouaghrem, K. A1 - Le Bars, I. A1 - Jouve, A.-C. A1 - Cordier, N. T1 - Assessment of safety demonstrations relative to packages containing UF6 N2 - The safety demonstrations realized by applicants in the case of approval request for the package designs containing enriched UF6 have to take into account some specific technical issues. Concerning the shipment of enriched UF6, the package designs consist in general of a filled 30B cylinder surrounded by an overpack. The description of the content, considering the UF6 origin, i.e. natural or reprocessed, shall be clearly justified especially when the UF6 isotopic composition exceeds the limits specified in ASTM standards. Concerning the containment of the UF6, the applicant shall demonstrate in all conditions of transport the leak-tightness of the valve and plug of the cylinders filled with enriched UF6. In this regard, when mechanical justifications are based on numerical calculations, the absence of contact between these components of the cylinder and the internal surfaces of the overpack after the regulatory drop tests shall be shown to respect the IAEA regulations. Furthermore, the representativeness of the ballast used to simulate the behaviour of the UF6 loaded within the cylinder shall be justified if drop tests are performed. The representativeness of the ballast should also be justified for numerical calculations. In addition, the applicant shall demonstrate that the melting temperature of the valve and the plug, including the tinned joint, will not be exceeded during the regulatory fire test. Finally, specific provisions relative to the use of plugs and the maintenance of cylinders should be included in the safety analysis report. T2 - 19th International Symposium on the Packaging and Transportation of Radioactive Materials PATRAM 2019 CY - New Orleans, LA, USA DA - 04.08.2019 KW - Valve KW - Fire test KW - Content simulation KW - UF6 KW - Intumescent material PY - 2019 SP - Paper 1208, 1 EP - 8 AN - OPUS4-49094 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Komann, Steffen A1 - Reiche, I. A1 - Ramsay, J. A1 - Pilecki, L. A1 - Hirose, M. A1 - Fukuda, T. A1 - Moutarde, M. A1 - Fiaccabrino, V. A1 - Malesys, P. A1 - Nöring, R. T1 - Development of the IAEA safety guide_format and content of the package design safety report_PDSR for the transport of radioactive material N2 - Since 2005, several European countries, coordinated by the European Association of Competent Authorities (EACA), have been developing a guide on contents and structure of the documentation demonstrating the compliance with the regulations for packages for the transport of radioactive material (package design safety report, PDSR). This guide has been periodically improved, considering feedback from Designers and authorities. Taking into account the successful application of this guide in Europe, in 2013 the International Atomic Energy Agency (IAEA) decided to establish a similar guide as an IAEA document for promotion of worldwide use. The development of this IAEA guide started from the latest version of the European PDSR guide. In 2016/2017, during a 120-day review period, comments on the draft were received from member states and international organizations. These were incorporated into the draft in a series of meetings in 2017. In another meeting in December 2018 the draft was updated to be in line with the latest revision of the IAEA Regulations for the Safe Transport of Radioactive Material (SSR-6). In this process the draft has been improved significantly, regarding structure as well as implementation of a graded approach depending on the package type, and clarified. This paper points to the major considerations in developing the guide and important improvements over the last version of the European PDSR guide. T2 - 19th International Symposium on the Packaging and Transportation of Radioactive Materials PATRAM 2019 CY - New Orleans, LA, USA DA - 04.08.2019 KW - IAEA KW - Safety report KW - Radioactive material KW - European Guide KW - Guidance material KW - Package types KW - Package design PY - 2019 SP - Paper 1172, 1 EP - 7 AN - OPUS4-49097 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Florian, Camilo A1 - Kirner, Sabrina V. A1 - Krüger, Jörg A1 - Bonse, Jörn T1 - Surface functionalization by laser-induced periodic surface structures N2 - In recent years, the improved understanding of the formation of laser-induced periodic surface structures (LIPSS) has led to an emerging variety of applications that modify the optical, mechanical and chemical properties of many materials. Such structures strongly depend on the laser beam polarization and are formed usually after irradiation with ultrashort linearly polarized laser pulses. The most accepted explanation for the origin of the structures is based on the interference of the incident laser radiation with electromagnetic surface waves that propagate or scatter at the surface of the irradiated materials. This leads to an intensity modulation that is finally responsible for the selective ablation in the form of parallel structures with periods ranging from hundreds of nanometers up to some micrometers. The versatility when forming such structures is based on the high reproducibility with different wavelength, pulse duration and repetition rate laser sources, customized micro- and nanometric spatial resolutions, and the compatibility with industrially relevant processing speeds when combined with fast scanning devices. In this contribution, we review the latest applications in the rapidly emerging field of surface functionalization through LIPSS, including biomimetic functionalities on fluid transport, control of the wetting properties, specific optical responses in technical materials, improvement of tribological performance on metallic surfaces and bacterial and cell growth for medical devices, among many others. T2 - 38th International Congress on Applications of Lasers & Electro-Optics CY - Orlando, FL, USA DA - 07.10.2019 KW - Laser-induced periodic surface structures (LIPSS) KW - Laser processing KW - Surface functionalization KW - Applications PY - 2019 SN - 978-1-940168-1-42 SP - Paper Nano 404 AN - OPUS4-50070 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz ED - Ruspighi, Emiliano T1 - Vehicle-track-soil interaction and train-induced ground vibration: Theory and measurements in Germany, Switzerland and France N2 - Abstract. Three measurement campaigns of train-induced ground vibrations are evaluated for the vehicle-track-soil interaction. Ground vibrations, track vibrations and vehicle vibrations have been measured for train passages and impulse excitation and compared with theoretical results. The soil and the track-soil system are calculated by wavenumber integrals. The influence of the vehicle is introduced by a substructure method. By comparing theory and measurement the different components of excitation force and ground vibration can be analysed, the quasi-static excitation, track-alignment errors, the out-of-roundness of wheels, the wheel and rail roughness, and moreover, scattered axle impulses and ineffective high-frequency parts of the wheelset accelerations and forces. T2 - 13th International Conference on recent Advances in Structural Dynamics CY - Lyon, France DA - 15.4.2019 KW - Vehicle-track interaction KW - Train-induced ground vibration KW - Ground vibration measurements PY - 2019 SP - 810 EP - 821 PB - University of Southampton CY - Southampton AN - OPUS4-48423 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Aristia, G. A1 - Le, Quynh Hoa A1 - Bäßler, Ralph A1 - Roth, C. T1 - The Effect of Different Polyaniline Types in Silicon Dioxide Containing Coatings for Carbon Steel Protection in Artificial Geothermal Brines N2 - According to the results of the experiments carried out, the following points can be concluded: 1. Exposure tests showed that specimens with the addition of SiO2 particles and polyaniline particles exhibit better corrosion resistance than specimens with the addition of only polyaniline particles or binder only. 2. Open circuit potential measurements showed that in the beginning of the experiments, both coatings had an open circuit potential 100 mV higher than carbon steel. Within one day of immersion, the potential of carbon steel increased significantly, indicating the formation of oxide layer. After extended exposure the carbon steel potential sat between PS1 (which had higher potential) and PS2 (which had a lower potential) and all three were in the range –600 mV to –500 mV vs Ag/AgCl. 3. Both coatings PS-1 and PS-2 were degraded with increasing exposure time, shown by the decrease of absolute impedance value at low frequency range after 2, 4, and 6 days exposure. 4. Potentiodynamic test was performed after 3 hours and 6 days exposure, and it was shown that the coating in the initial stage exhibited more passive behavior than the specimens exposed for 6 days. T2 - NACE International Corrosion Conference 2019 CY - Nashville, TN, USA DA - 24.03.2019 KW - Geothermal KW - Coating KW - Polyaniline KW - Corrosion PY - 2019 SP - 13121-1 EP - 13121-14 PB - NACE International CY - Houston AN - OPUS4-47913 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Duffner, Eric A1 - Mair, Georg W. A1 - Munzke, Dorit A1 - Szczepaniak, Mariusz A1 - Schukar, Marcus T1 - Lebensdauerversuche an Faserverbund-Druckbehältern überwacht mittels Schallemissionsprüfung und optischen Fasern N2 - Kurzfassung. Die meisten Faserverbundbehälter, die in Europa für den Transport gefährlicher Stoffe oder als Speicherbehälter für Wasserstoff oder Erdgas in Fahrzeugen Verwendung finden, werden für eine nicht begrenzte Lebensdauer ausgelegt. In regelmäßigen Abständen sind für diese Druckbehälter wiederkehrende Prüfungen vorgeschrieben, die in der Regel aus visuellen Inspektionen und hydraulischen Innendruckprüfungen bestehen. Die wiederkehrenden Prüfungen sind jedoch weder geeignet, die sichere Betriebsdauer festzulegen noch den Alterungszustand der Druckbehälter zu beurteilen. Aufgrund des weiter steigenden Drucks zur Kosten- und Gewichtsreduktion von Faserverbundbehältern und der damit einhergehenden Ausnutzung der existierenden Sicherheitsmargen gewinnen Methoden zur Beurteilung des Alterungsverhaltens dieser Druckbehälter immer mehr an Bedeutung. Vor diesem Hintergrund wurde in der BAM das Vorhaben „Alterungsverhalten von Composite-Druckgefäßen mit Carbonfaser-Compositen unter gekoppelten Beanspruchungen (COD-AGE)“ gestartet, um die Alterung von Faserverbundbehältern mittels verschiedener zerstörungsfreier Prüfverfahren zu untersuchen. Die hier vorgestellten Ergebnisse wurden an einem Typ 4 Hybridbehälter mit Kunststoffliner gewonnen, in den im Rahmen des Herstellungsprozesses optische Glasfasern in verschiedenen Schichten integriert wurden. Der Behälter wurde mittels hydraulischem Innendruck und erhöhter Umgebungstemperatur zyklisch bis zum Lebensende belastet. Zwischen den einzelnen Lastsequenzen erfolgte eine an die wiederkehrende Prüfung im Betrieb angelehnte hydraulische Druckbelastung. Sowohl die hydraulische Alterung als auch die Druckrampen wurden mittels Schallemissionsprüfung (SEP) und verteilter faseroptischer Sensorik mit dem Ziel einer frühzeitigen Versagensvorhersage überwacht. Durch die Schallemissionsanalyse sollte untersucht werden, ob zum Lebensende hin ein signifikanter Anstieg der Schallemissionsaktivität und -intensität, unterteilt in verschiedene Lastbereiche, beobachtet werden kann. Zusätzlich zum kontinuierlichen Monitoring der Zyklierung sollten die Druckrampen separat untersucht werden, um hier Potenziale für die wiederkehrende Prüfung zu erkennen. T2 - 22. Kolloquium Schallemission und 3. Anwenderseminar Zustandsüberwachung mit geführten Wellen CY - Karlsruhe, Germany DA - 27.03.2019 KW - Faserverbund KW - Druckbehältern KW - Lebensdauerversuche KW - Schallemissionsprüfung PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-479534 SP - 1 EP - 10 PB - DGZfP CY - Berlin AN - OPUS4-47953 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ghafafian, Carineh A1 - Popiela, Bartosz A1 - Nielow, Dustin A1 - Trappe, Volker T1 - Restoration of structural integrity – a comparison of various repair concepts for wind turbine rotor blade shells N2 - Localized patches are a cost- and time-effective method for repairing fiber-reinforced polymer (FRP) sandwich wind turbine rotor blade shells. To increase the understanding of their effect on the fatigue of the blades, this study examines the effect of various layup methods of localized repair patches on the structural integrity of composite sandwich structures. Manufactured with the vacuum-assisted resin infusion (VARI) process, the shell test specimens are produced as a curved structure with glass fiber reinforced polymer (GFRP) sandwiching a polyvinyl chloride (PVC) foam core. Patch repairs are then introduced with varying layup techniques, and material properties are examined with cyclic fatigue tests. The transition region between patch and parent material is studied in greater detail with finite element method (FEM) simulations, with a focus on the effect of fiber orientation mismatch. Damage onset, crack development, and eventual failure are monitored with in-situ non-destructive testing methods to develop a robust understanding of the effects of repair concepts on material stiffness and strength. T2 - SMAR 2019 - 5th International Conference on Smart Monitoring, Assessment and Rehabilitation of Civil Structures CY - Potsdam, Germany DA - 27.08.2019 KW - Lightweight materials KW - Glass fiber reinforced polymers KW - Sandwich KW - Wind turbine blades PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-482170 SP - 1 EP - 8 PB - German Society for Non-Destructive Testing (DGZfP e.V.) AN - OPUS4-48217 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Palkowski, Carsten A1 - Simo, Anne T1 - Quick Seasonal Performance Testing for Heat Pumps N2 - To determine the seasonal performance of heat pumps for energy labelling this study proposes a two-point-method that could conceivably be an alternative to the European standard EN 14825 and similar test standards such as ISO 13256. Heat pumps were tested in line with the EN 14825. The reduction of measurement points, from between five to seven (EN 14825) to only two (two-point-method), leads to 60 % savings in cost and time. It is shown that the shortened method can be used to determine the seasonal energy efficiency of heat pumps with the same degree of precision compared to EN 14825. T2 - ECEEE Summer Study 2019 CY - Hyerès, France DA - 03.06.2019 KW - Heat pump KW - Energy label KW - Testing KW - Coefficient of performance KW - Screening PY - 2019 SP - 1547 EP - 1552 AN - OPUS4-48275 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nagelschmidt, Sven A1 - Herbrich, Uwe A1 - Qiao, Linan T1 - Applicability of developed calculation models to predict long-term behavior of metal seals – Necessary scope of tests N2 - The long-term sealing behavior of metal seals, assembled in the lid system of casks for transportation and storage of radioactive materials, has been investigated. For that purpose, phenomenological models describing the time- and temperature dependent behavior have been introduced by BAM since 2016, e.g. by using the time-temperature superposition principle. Results have shown that these models describe the relaxation behavior adequately and are suitable for extrapolations. In this work, the applicability of these models is checked by analyzing the necessary scope of tests, which must be carried out to get sufficient information about the long-term behavior of metal seals based on short-term tests. T2 - Waste Management Conference CY - Phoenix, Arizona, USA DA - 03.03.2019 KW - Metal seal KW - Time-temperature superposition principle KW - Transportation and storage cask KW - Long-term interim storage PY - 2019 SP - 19311, 1 EP - 6 AN - OPUS4-48353 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hofmann-Böllinghaus, Anja A1 - Webb, A. T1 - Changes in façade regulations N2 - Recent facade fires worldwide have driven change in regulations for façade fire safety in different parts of the world. The Grenfell Tower fire 2017 in London triggered a thorough investigation of many aspects of the fire. One investigation was about the UK building regulations from Dame Judith Hackett 1,2. This investigation compares the UK with the situation other parts of the world. T2 - Interflam 2019 CY - London, UK DA - 01.07.2019 KW - Facade KW - Regulations KW - Australia KW - UK KW - Germany PY - 2019 SP - 183 EP - 197 PB - Interscience CY - London AN - OPUS4-48426 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hofmann-Böllinghaus, Anja A1 - Boström, L. A1 - Anderson, J. A1 - Chiva, R. A1 - Guillaume, E. A1 - Colwell, S. A1 - Toth, P. T1 - European approach to assess the fire performance of façades N2 - Several attempts have been made in the past to develop a European harmonized testing and assessment method for façades before the European commission decided to publish a call for tender on the topic. A project consortium from five countries (Sweden, UK, France, Germany and Hungary) applied to the call for tender and was contracted to develop a European approach to assess the fire performance of façades. 24 sub-contractors and 14 stakeholder entities were part of the project. The objective of the European project was to address a request from the Standing Committee of Construction (SCC) to provide EC Member States regulators with a means to regulate the fire performance of façade systems based on a European approach agreed by SCC. In addressing this objective, the project team was asked to consider a number of issues which are presented and discussed. T2 - Interflam 2019 CY - London, UK DA - 01.07.2019 KW - Facade KW - European KW - Fire scenario KW - Testing PY - 2019 SP - 213 EP - 227 PB - Interscience AN - OPUS4-48428 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Romero-Navarrete, José A. A1 - Otremba, Frank T1 - Oblique testing of a partially filled tank on a tilt table N2 - Braking-in-a-turn maneuvers represent a critical operational condition for any vehicle, due to the associated longitudinal and lateral perturbations to which it is subjected, which maximize the load transfer among the different wheels, and result in vehicle´s poor lateral stability and deficient braking performance. In this paper, a suspended vehicle supporting a partially filled 10 litter-capacity container, is set on a tilt table at oblique angles, in order to simulate a braking-in-a-turn maneuver. The measurements are assessed in the time and frequency domains, on the basis of the lateral load transfer ratio and the infrastructure fatigue damage. The outputs from the experiment show that the Minimum fill level (one-quarter), generates the larger lateral load transfer (0.45). Such fill level also causes the greatest ratios for the alternate stress over the mean stress on the infrastructure. The spectral analysis reveals the dominance of one of the sloshing frequencies during such combined perturbation condition. T2 - IFToMM world congress CY - Krakow, Poland DA - 30.06.2019 KW - Sloshing KW - Lateral stability KW - Load transfer KW - Braking-in-a-turn maneuvers KW - Infrastructure damage KW - Experimental approach PY - 2019 SN - 978-3-030-20130-2 SN - 978-3-030-20131-9 DO - https://doi.org/10.1007/978-3-030-20131-9_359 SN - 2211-0984 VL - 73 SP - 3641 EP - 3650 PB - Springer Nature Switzerland AG 2019 AN - OPUS4-48454 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wosniok, Aleksander T1 - Messgenauigkeit und Reproduzierbarkeit bei der Messung der Brillouin-Frequenzverschiebung für die faseroptische Bestimmung der Temperaturverteilung N2 - Auf der Grundlage der in DIN EN 61757-2-2:2017 beschriebenen Standardisierungsmethoden wurden in dieser Arbeit wichtige Leistungsparameter von vier kommerziellen Messsystemen zur ortsaufgelösten faseroptischen Erfassung der temperatur- und dehnungsabhängigen Brillouin-Frequenzverschiebung untersucht. Gemäß der oben genannten Norm konzentrierte sich hier die Ermittlungsprüfung auf messtechnische Aspekte reiner Temperaturmessungen. Dabei diente die Ermittlung von einem festgelegten Satz dreier Betriebsverhaltenskenngrößen in Form von quantitativen Angaben des Messfehlers, der Wiederholgenauigkeit sowie der räumlichen Unsicherheit einem Vergleich der getesteten Messsysteme. Alle faseroptischen Messungen wurden mit einer Faserschleife ausgeführt, d. h. als Sensorkonfiguration der Messfaser wurde eine Schleifenanordnung gewählt. Die Messverfahren der getesteten Messysteme basierten somit auf der Brillouin-optischen Zeit- bzw. Frequenzbereichsanalyse. Die Betriebsverhaltenskenngrößen wurden ferner bei unterschiedlichen Werten zweier messtechnischer Parameter, des Frequenzschrittes und der Mittelungsrate, für Standardeinstellungen der Laserleistungswerte der in die Sensorfaser einzukoppelnden Laserlichtsignale ermittelt. Auf diesem Weg lassen sich relevante Aussagen zur Optimierung der Messgenauigkeiten in Bezug auf Messdauer treffen. T2 - 20. GMA/ITG-Fachtagung Sensoren und Messsysteme 2019 CY - Nuremberg, Germany DA - 25.06.2019 KW - Faseroptischer Sensor KW - Ortsaufgelöste Brillouin-Sensorik KW - Verteilte faseroptische Temperaturmessung KW - Brillouin-Frequenzverschiebung KW - Betriebsverhaltenskenngrößen PY - 2019 SN - 978-3-9819376-0-2 DO - https://doi.org/10.5162/sensoren2019/P2.1 SP - 656 EP - 662 PB - AMA Service GmbH CY - Wunstorf AN - OPUS4-48346 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Long, Lijia A1 - Alcover, I. F. A1 - Thöns, Sebastian T1 - Quantification of the posterior utilities of SHM campaigns on an orthotropic steel bridge deck N2 - This paper contains a quantification and decision theoretical optimization of the posterior utilities for several options for monitoring campaigns on the particular case of fatigue life predictions of an orthotropic steel deck. The monitoring campaigns are defined by varying monitoring durations and phases. The decision analysis is performed with real data from the Structural Health Monitoring (SHM) of the Great Belt Bridge (Denmark) which, among others, consist of measured strains, pavement temperatures and traffic intensities. The fatigue loading prediction model is based on regression models linking daily averaged pavement temperatures, daily aggregated heavy-traffic Counts and derived S-N fatigue damages, all of them derived from the outcomes of different monitoring campaigns. A probabilistic methodology is utilized to calculate the fatigue reliability profiles of selected instrumented welded joints. The posterior utilities of SHM campaigns are then quantified by considering the structural fatigue reliability, various monitoring campaigns and the corresponding cost-benefit models. The decisions of identifying the optimal monitoring campaign and of extending the service life or not in conjunction with monitoring results are modelled. The optimal monitoring campaign is identified - retrospectively - by maximizing the expected benefits and minimize risks in dependency of the monitoring duration and the monitoring associated costs. The results, despite relying on a number of simplistic assumptions, pave the way towards the use of pre-posterior decision support to optimise the design of monitoring campaigns for similar bridges, with an overall goal to proof the cost efficiency of SHM approaches to civil infrastructure management. T2 - IWSHM 2019, The 12th International Workshop on Structural Health Monitoring, Stanford, California, USA CY - Stanford, California, USA DA - 10.09.2019 KW - Quantification KW - SHM information KW - Steel bridge deck PY - 2019 SP - 1 EP - 9 AN - OPUS4-48481 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Harnisch, J. A1 - Dauberschmidt, C. A1 - Ebell, Gino A1 - Mayer, T. T1 - The new DGZfP Specification B12 "Corrosion Monitoring of Reinforced Concrete Structures" N2 - The corrosion of steel in reinforced concrete structures is one of the main threats to their durability. Based on the scientific achievements of the past decades the knowledge about the deterioration mechanisms and possible repair strategies for corrosion induced damages have found their way into practice. It is common sense, that a detailed assessment of the structure is the foundation for a successful repair measure. In addition to the “traditional” singular on-site-procedures such as measurement of concrete cover, carbonation depth, half-cell potentials and chloride contents the monitoring of corrosion related parameters has gained in importance over the past few years. The advantages of a corrosion monitoring are obvious. In new buildings, structural elements which cannot be assessed after completion (e.g. tunnel segments), or members with electrically isolating coatings can be monitored by means of integrated sensors providing an insight into the development of crucial parameters such as electrochemical potentials, corrosion currents and the electrical resistivity of the concrete. A less known but very beneficial field of application is the use of corrosion monitoring as an integral part of a repair measure based on principles such as the cathodic protection of steel in concrete (CP) or increasing the electrical resistivity of the concrete (IR). By implementing a corrosion monitoring system, it is possible to survey the time dependent effect of the repair measure on the corrosion process which may lead to a confirmation of successful repair measure or to a modification of the repair strategy. As the principle of cathodic protection for steel in concrete is a recognized repair measure today, the number of applications increases steadily and thus increasing the relevance for corrosion monitoring. Nevertheless, no standards or guidelines concerning the corrosion monitoring are available in Germany today, making it difficult to implement corrosion monitoring in common practice. With this in mind an international task group formed to develop the specification B12 “Corrosion Monitoring of Reinforced and Prestressed Concrete Structures” published by the German Society for Non-Destructive Testing, DGZfP, spring 2018. This paper will present the new specification B12 by highlighting the basic measurement principles and illustrating the potentials of corrosion monitoring for new and existing concrete structures by means of case studies. T2 - SMAR 2019 CY - Potsdam, Germany DA - 27.08.2019 KW - Monitoring KW - Corrosion KW - Concrete structures PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-487980 SP - We.4.A.1, 1 PB - SMAR 2019 AN - OPUS4-48798 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Spilker, A. A1 - Stelzner, Ludwig T1 - Analyse der thermischen Dehnung von Fahrbahndeckenbetonen aus dem BAB-Netz N2 - Die Kenntnis von Materialeigenschaften spielt bei der Entwicklung oder Optimierung von Betonen und Bauweisen für den Straßenbau sowie der Qualitätskontrolle und -sicherung eine bedeutende Rolle. Gleichermaßen bilden physikalische Materialkennwerte die Grundlage für die rechnerische Dimensionierung und die Restsubstanzbewertung von Betonfahrbahndecken. Einen relevanten Kennwert bei der Untersuchung thermisch induzierter Spannungsund Verformungszustände stellt der thermische Ausdehnungskoeffizient von Beton dar. Dieser beeinflusst beispielsweise maßgeblich das Längsdehnungsverhalten des Deckensystems sowie das Ausmaß von Plattenkrümmungen und Fugenbewegungen. Im Zuge der systematischen Weiterentwicklung der rechnerischen Dimensionierung aber auch im Zusammenhang mit der gezielten Verbesserung der Gebrauchseigenschaften von Fahrbahndecken gilt es zu hinterfragen, ob lastunabhängige Formänderungseigenschaften, wie z. B. der thermische Ausdehnungskoeffizient der verwendeten Betone, aktuell ausreichend Beachtung finden, ob allgemeine Literaturwerte für die heutigen Fahrbandeckenbetone stets Gültigkeit besitzen und ob deren Implementierung in moderne Rechenmodelle zu validen Ergebnissen führt. Für eine empirische Herangehensweise ist die Verfügbarkeit adäquater Prüfverfahren von entscheidender Bedeutung. In Deutschland existiert aktuell jedoch kein standardisiertes oder genormtes Verfahren für die prüftechnische Bestimmung des thermischen Ausdehnungskoeffizienten von Beton. Daher wurden unter Beachtung straßenbauspezifischer Gesichtspunkte zwei Prüfansätze entwickelt, die in diesem Beitrag vorgestellt und hinsichtlich möglicher Messunsicherheiten und Messungenauigkeiten diskutiert werden. Außerdem erfolgt die Darstellung ausgewählter Ergebnisse aus Analysen an Bestandsbetonen aus dem BAB-Netz. Im Ergebnis sollen die Untersuchungen einen Beitrag zur Schaffung der prüftechnischen Voraussetzungen für eine abgesicherte Quantifzierung der thermischen Dehnung von Fahrbahndeckenbetonen leisten. T2 - Betonstraßentagung 2019 CY - Aschaffenburg, Germany DA - 26.09.2019 KW - Thermische Dehnung KW - Fahrbahndeckenbetone KW - Baustoffe PY - 2019 SN - 978-3-86446-260-3 SP - 1 EP - 13 AN - OPUS4-49485 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weise, Frank A1 - Fladt, Matthias T1 - Innenhydrophobierung - neuartige AKR-Vermeidungsstrategie bei Betonfahrbahndecken N2 - Verstärkt auftretende Schäden in Betonfahrbahndecken des Bundesfernstraßennetzes, die mit einer Alkali-Kieselsäure-Reaktion (AKR) in Verbindung gebracht werden, haben zu einer massiven Verschärfung der Prüfvorschriften zur Bewertung der Alkaliempfindlichkeit von Ge-steinskörnungen geführt. Die damit verbundene Einschränkung potenziell für den Straßenbau einsetzbarer Gesteinskörnungen ruft eine verstärkte Ressourcenknappheit und ein erhöhtes Transport- und damit einhergehendes Kostenaufkommen hervor. Vor diesem Hintergrund wird nach neuartigen AKR-Vermeidungsstrategien gesucht, die auch eine Verwendung grenzwertig alkaliempfindlich eingestufter Gesteinskörnungen erlaubt. Einen möglichen Lösungsansatz stellt in diesem Kontext die Innenhydrophobierung des Fahrbahndeckenbetons dar. Es soll so durch die Behinderung des Feuchte- und Tausalzeintrags in den Beton der AKR-Schädigungs-prozess signifikant vermindert werden. Für die Bewertung der Leistungsfähigkeit der Innen-hydrophobierung zur Vermeidung einer schädigenden AKR in Betonfahrbahndecken wird zur-zeit im Auftrage der BASt an der BAM ein Forschungsvorhaben bearbeitet. Im Rahmen dieses Beitrags werden erste ausgewählte Ergebnisse dieses Forschungsvorhabens vorgestellt. So wird exemplarisch an einem Oberbeton (0/8) mit einer alkaliempfindlichen Gesteinskörnung der Einfluss eines Hydrophobierungsmittels auf die Frisch- und Festbetoneigenschaften ganz-heitlich aufgezeigt und bewertet. Bei Letzteren stehen zunächst die mechanischen und hygri-schen Parameter sowie der Frost-Tausalzwiderstand im Vordergrund. In einem weiteren Schritt wird der Einfluss der Innenhydrophobierung auf die schädigende AKR mittels verschie-denartiger AKR-Performanceprüfungen beleuchtet. T2 - Betonstraßentagung 2019 CY - Aschaffenburg, Germany DA - 26.09.2019 KW - Alkali-Kieselsäure-Reaktion KW - AKR KW - Innenhydrophobierung PY - 2019 SN - 978-3-86446-260-3 SP - 1 EP - 15 AN - OPUS4-49484 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kasch, Thomas A1 - Woitzek, Andreas T1 - Beurteilungsmöglichkeiten nichtmetallischer Materialien für den Einsatz in Sauerstoff N2 - Nichtmetallische Materialien dürfen generell als Gleitmittel, Dichtungsmaterialien, Flanschdichtungen und Füllflüssigkeiten nur dann in Sauerstoffanwendungen eingesetzt werden, wenn sie sicherheitstechnisch für die entsprechenden Betriebsbedingungen geeignet sind. Genormte Prüfverfahren sowie weitere Untersuchungsmöglichkeiten wie die Sauerstoff- Druckstoßprüfung, die Bestimmung der Zündtemperatur in verdichtetem Sauerstoff, die Untersuchung des Alterungsverhaltens, die Flanschprüfung sowie die Prüfung des Reaktionsverhaltens des Materials mit flüssigem Sauerstoff bei mechanischer Einwirkung sollen dies gewährleisten und können auch bei der BAM durchgeführt werden. Die vorhandenen Prüfungen und Beurteilungskriterien verursachen jedoch manchmal Probleme, wenn es um die Übertragbarkeit auf die tatsächliche, praktische Anwendung oder um die Interpretation von Prüfergebnissen geht. Der Vortrag stellt diesbezüglich die BAM- Sicherheitsphilosophie vor. T2 - Deutsche Industriearmaturen Messe & Fachmesse für Dichtungstechnik CY - Bochum, Germany DA - 09.10.2019 KW - Beurteilungskriterien KW - Sauerstoff KW - Prüfverfahren KW - Untersuchungsmöglichkeiten der BAM, Chargenprüfung PY - 2019 SP - 33 EP - 37 PB - Vulkan-Verlag GmbH CY - Essen AN - OPUS4-49523 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Askar, Enis A1 - Schröder, Volkmar A1 - Göpfert, T. A1 - Winterleitner, E. A1 - Schwarze, M. T1 - Safety related properties of low-GWP refrigerants N2 - Most fluorinated hydrocarbons that shall replace refrigerants with high GWP, like R134a, are flammable. For evaluating inertization measures for explosion protection, flammability of low-GWP refrigerants R1234yf, R32 and R1132a blended with carbon dioxide, nitrogen and argon were studied experimentally in a closed autoclave at atmospheric conditions. Furthermore, a calculation method was adapted to reduce the experimental costs for flammability studies on these gas mixtures. For igniting R1234yf in the closed autoclave a newly developed ignition system was used that allows generating electric arcs with high ignition energy. Gas mixtures containing the mildly flammable R1234yf and R32 could be inerted by adding much less inert gas than mixtures containing R1132a, which is more similar to unfluorinated hydrocarbons regarding the explosion regions. By using the adapted model of constant adiabatic flame temperature profiles estimating the explosion limits of fluorinated hydrocarbons was possible with similar accuracy as for unfluorinated hydrocarbons. Keywords: Explosion Protection, Inertization, Flammability, HFOs, HFC., R1234yf, R32, R1132a T2 - 25th IIR Internationa Congress of Refrigeration CY - Montreal, Canada DA - 24.08.2019 KW - Explosion Protection KW - Inertization KW - Flammability KW - HFOs KW - R1234yf KW - R1132a KW - R32 KW - HFC PY - 2019 SN - 978-2-36215-035-7 DO - https://doi.org/10.18462/iir.icr.2019.0767 SN - 1025-9031 SP - 1 EP - 9 AN - OPUS4-49546 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krietsch, Arne A1 - Dufaud, O. A1 - Santandrea, A. A1 - Vignes, A. A1 - Perrin, L. A1 - Laurent, A. T1 - Some keys considerations when evaluating explosion severity of nanopowders N2 - Protection from explosion events requires the determination of key safety parameters like lower explosion limit. maximum Explosion over-pressure. and maximum rate of pressure rise. These Parameters are routinely obtained through standard tests performed typically either in a 20 L -sphere or a 1 m3-container. But several aspects are worth a closer investigation. Firstly, the test apparatus must be able to disperse a fairly uniform dust cloud. However. previous investigations showed that actually the current dispersion System can be improved. Secondly, the influence of humidity on the explosivity is not considered in current standards. lt is just stated that the relative humidity should be checked and noted down. though some provisions exist in American standards. Thirdly. the ignition delay time is sometimes modified to study the impact of the dust cloud turbulence on flame propagation but is often misunderstood. Maybe these aspects have not been thoroughly considered for micron powders. However. in the case of nanopowders. the importance of these influencing factors was shown in order to duly evaluate explosion parameters. Experimental evidences confirm these aspects and alternative solutions will be presented. T2 - Loss Prevention Symposium 2019 CY - Delft, Netherlands DA - 16.06.2019 KW - Nanopowders KW - Dust explosion KW - Safety characteristics PY - 2019 SN - 978-88-95608-72-3 SN - 2283-9216 VL - 75 SP - 1 EP - 6 PB - AIDIC AN - OPUS4-49547 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woitzek, Andreas A1 - Kasch, Thomas T1 - Beurteilung der Ausbrennsicherheit von Armaturen und Anlagenteilen für Sauerstoff N2 - In der Praxis kommt es immer wieder zu Ausbränden von medizinischen Geräten und industriellen Anlagen mit Sauerstoff. Armaturen und Anlagenteile dürfen deshalb nur dann mit Sauerstoff verwendet werden, wenn sie sicherheitstechnisch für die entsprechenden Betriebsbedingungen geeignet sind. Neben ganz konkreten Anforderungen aus produktspezifischen Normen und Richtlinien, müssen die Prüfungen in vielen Fällen individuell auf die jeweilige Anwendung zugeschnitten werden. Der Vortrag stellt die BAM-Sicherheitsphilosophie hinsichtlich der unterschiedlichen Anforderungen und Möglichkeiten der Beurteilung der Ausbrennsicherheit vor. T2 - Deutsche Industriearmaturen Messe & Fachmesse für Dichtungstechnik CY - Bochum, Germany DA - 09.10.2019 KW - Beurteilungskriterien KW - Sauerstoff KW - Beurteilungsmethoden der BAM KW - Prüfverfahren PY - 2019 SP - 69 EP - 72 PB - Vulkan-Verlag GmbH CY - Essen AN - OPUS4-49526 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Winkler, Nicolas P. A1 - Lilienthal, A. J. A1 - Neumann, Patrick P. ED - Zemčík, R. ED - Krystek, J. T1 - Boosting a Low-Cost Sensor Network with Mobile High-Quality Sensors N2 - Occupational health is an important topic, especially in industry, where workers are exposed to airborne by-products (e.g., dust particles and gases). Therefore, continuous monitoring of the air quality in industrial environments is crucial to meet safety standards. For practical and economic reasons, high-quality, costly measurements are currently only carried out sparsely, both in time and space, i.e., measurement data are collected in single day campaigns at selected locations only. Recent developments in sensor technology enable cost-efficient gas monitoring in real-time for long-term intervals. This knowledge of contaminant distribution inside the industrial environment would provide means for better and more economic control of air impurities, e.g., the possibility to regulate the workspace’s ventilation exhaust locations, can reduce the concentration of airborne contaminants by 50%. This paper describes a concept proposed in the project “Robot-assisted Environmental Monitoring for Air Quality Assessment in Industrial Scenarios“ (RASEM). RASEM aims to bring together the benefits of both – low- and high-cost – measuring technologies: A stationary network of low-cost sensors shall be augmented by mobile units carrying high-quality sensors. Additionally, RASEM will develop procedures and algorithms to map the distribution of gases and particles in industrial environments. T2 - 36th Danubia-Adria Symposium on Advances in Experimental Mechanics CY - Pilsen, Czech Republic DA - 24.09.2019 KW - RASEM KW - Sensor network KW - Low-cost KW - Occupational health KW - Mobile Robot Olfaction PY - 2019 SP - 61 EP - 62 CY - Plzeň AN - OPUS4-49630 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino A1 - Burkert, Andreas T1 - Korrosionsverhalten von feuerverzinktem Betonstahl in karbonatisierten und chloridhaltigen Mörteln N2 - Der Einsatz von feuerverzinkten Betonstählen in karbonatisiewrten Betonen führt bei reduzierten Betondeckungen zu einer signifikanten Nutzungsdauerverlängerung. Bei einwirken von chloriden kann keine signifikanten Verlängerung der Nutzungsdauer durch feuerverzinkte Betonstähle erzielt werden. T2 - GfKORR Jahrestagung 2019 CY - Frankfurt a.M., Germany DA - 12.11.2019 KW - Korrosion KW - Verzinkter Betonstahl PY - 2019 SP - 65 EP - 76 AN - OPUS4-49613 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schalau, Sebastian A1 - Habib, Abdel Karim T1 - CFD-Simulation von Schwergasausbreitungen in bebautem Gelände N2 - Um die Ausbreitung von Schwergaswolken infolge störfallbedingter Freisetzungen in bebautem Gelände besser vorhersagen zu können, wird eine praxisorientierte Methode zur numerischen Simulation von Schwergasausbreitungen vorgestellt. T2 - 14. Fachtagung Anlagen-, Arbeits- und Umweltsicherheit CY - Köthen, Germany DA - 07.11.2019 KW - Schwergasausbreitung KW - CFD KW - OpenFOAM PY - 2019 SN - 978-3-89746-220-5 SP - 130 EP - 139 AN - OPUS4-49570 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schalau, Bernd A1 - Schalau, Sebastian T1 - Die neue VDI-Richtlinie 3783 Blatt 1. Stand der Diskussion N2 - Die VDI-Richtlinien 3783 Blatt 1 und Baltt 2 gelten immer noch im Bereich der Störfallauswirkungsbetrachtungen als Stand der Technik, obwohl sie aus den Jahren 1987 und 1990 stammen. In der Kommission Reinhaltung der Luft im VDI und DIN wurde 2009 die Arbeitsgruppe „Ausbreitung von störfallbedingten Freisetzungen – Sicherheitsanalyse“ mit der Zielsetzung gegründet, die VDI-Richtlinie 3783 zu überarbeiten. Der Inhalt des jetzt vorliegenden Gründrucks wird vorgestellt. T2 - 14. Fachtagung Anlagen-, Arbeits- und Umweltsicherheit CY - Köthen, Germany DA - 07.11.2019 KW - Störfall-Verordnung KW - Auswirkungsbetrachtung PY - 2019 SN - 978-3-89746-220-5 SP - 120 EP - 129 AN - OPUS4-49573 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heckel, Thomas A1 - Wack, Y. A1 - Mook, G. T1 - Simulation von mechanisierten Eisenbahnschienenprüfungen mit Ultraschall N2 - Bei der mechanisierten Prüfung von verlegten Eisenbahnschienen mit Schienenprüfzügen werden große Prüfdatenmengen mit einer komplexen Prüfkopfanordnung in kurzer Zeit bei hohen Prüfgeschwindigkeiten aufgenommen. Der Typ und der Zustand des Gleises kann während der Prüfung in schnellem Wechsel streckenabhängig variieren, z.B. unterschiedliche Schienentypen oder Abnutzung sowie beim Durchfahren von Weichenstraßen. Der logistische Aufwand diese Prüfung insgesamt durchzuführen ist dabei sehr hoch und eine Wiederholung der Prüfung in einem kurzen Zeitintervall nicht möglich. Es werden während der Prüfdatenaufnahme bereits Datenreduktionsverfahren, Rekonstruktionsverfahren und Online-Parametervariationen eingesetzt, um die Ergebnisdaten zum einen in Ihrer Menge zu begrenzen zum anderen auf die lokalen Geometrie- und Zustandsänderungen des Prüfobjektes Schiene zu reagieren. Im Regelwerk EN 16729-1 „Zerstörungsfreie Prüfung an Schienen im Gleis -Teil 1: Anforderungen an Ultraschallprüfungen und Bewertungsgrundlagen“ werden Bezugsreflektoren definiert, um die Leistung automatisierter Ultraschallsysteme für die Schienenprüfung zu verifizieren. Um die Einflüsse der komplexen Randbedingungen der mechanisierten Schienenprüfung auf das Prüfergebnis evaluieren zu können, wurde ein Softwarewerkzeug erarbeitet, mit dem eine Prüffahrt auf einer Schiene simuliert werden kann. Basierend auf der Datenaufnahme mit dem Glassy-Rail-Diagramm können alle relevanten Prüfparameter und Artefakte in Schienen sowie Störeinflüsse bei der Simulation berücksichtigt werden. T2 - DGZfP DACH Tagung 2019 CY - Friedrichshafen, Germany DA - 27.05.2019 KW - Schiene KW - Zerstörungsfreie Prüfung KW - Ultraschall PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-496749 VL - 2019 SP - 1 EP - 8 AN - OPUS4-49674 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heckel, Thomas A1 - Boehm, Rainer A1 - Mook, G. T1 - Ultrasonic rail inspection with array probes N2 - For more than 60 years ultrasonic rail inspection is used as non-destructive testing method to ensure the safe operation of rail tracks. Constantly increasing traffic density and heavy loads have been the motor for the development of new test equipment from handheld devices to rail inspection trains. (Krull 2003)Up to the present most of the system solutions feature conventional ultrasonic transducers housed in wheel-type and slide-type probes. Different tasks have to be carried out during an in-service inspection for flaws in the rail head, rail web and rail foot as well as rolling contact fatigue (Heckel 2018). The more tasks the inspection system has to perform, the more probes are needed. Compared against standard ultrasonic testing methods the application of array probes offers advantages and flexibility by the electronic steering possibilities to control the transmitted and received sound fields. This allows to increase functionality by software while decreasing the number of probes needed in hardware in parallel. One drawback in application of phased array probes is that the repetition frequency of the subsequent measurements will be reduced by the number of virtual probe functions each phased array probe has to perform. This may limit the range of use for phased array probes in high speed applications. To overcome these limits special designs for array probes and signal processing are necessary. T2 - Railway Engineering 2019 CY - Edinburgh, UK DA - 03.07.2019 KW - High speed KW - Ultrasound KW - Rail inspection KW - Phased array probes PY - 2019 VL - 2019 SP - 1 EP - 3 AN - OPUS4-49680 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beilken, D. A1 - Rühe, S. A1 - Heckel, Thomas A1 - Casperson, Ralf T1 - Aktuelle Entwicklungen der Wirbelstrom- und Ultraschallprüfung an verlegten Eisenbahnschienen N2 - Die kombinierte Schienenprüfung mit Wirbelstrom und Ultraschall ermöglicht eine ganzheitliche Detektion von Inhomogenitäten im Kopf und Steg der Schiene und gewährleistet das Auffinden sowohl von Volumen-als auch Oberflächeneffekten wie z. B. Head Checks. Für die verbesserte Detektion von Rollkontaktermüdung (rolling contact fatique, RCF) und den daraus resultierenden Schienenfehlern (Head-Checks, Squats, Riffel, …) wurde für die Wirbelstromprüfung der Prüfbereich auf die gesamte Rollkontaktfläche erweitert. Der Fokus liegt im Neudesign der Wirbelstrom-Prüfvorrichtung und der damit verbundenen normgerechten Auslegung der Konstruktion für die fahrzeugspezifischen Gegebenheiten. Ferner wurde die Anwendersoftware des kombinierten Prüfsystems vereinheitlicht. Um die wirtschaftliche Effektivität unsere Prüftechnik zu steigern, wird die Multiplex-Gerätetechnologie in die automatisierte Schienenprüfung eingeführt. Damit wird der freizuhaltende Einbauraum innerhalb der Fahrzeuge sowie Kabelwege deutlich reduziert. Durch den Übergang zu der Multiplextechnologie wurde weiterhin die Stromaufnahme um mehr als 50% reduziert. T2 - DGZfP DACH Tagung 2019 CY - Friedrichshafen, Germany DA - 27.05.2019 KW - Schienenprüfung KW - Zerstörungsfreie Prüfung KW - Ultraschall KW - Wirbelstrom PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-496775 VL - 2019 SP - 1 EP - 10 AN - OPUS4-49677 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krüger, Simone A1 - Schartel, Bernhard A1 - Schoch, Rebecca A1 - Schubert, Martina T1 - Holz-Kunststoff-Verbundwerkstoffe - Wie beeinflussen Flammschutzmittel die Rauchgaszusammensetzung im Brandfall? N2 - Der steigende Einsatz von Holz-Kunststoff-Verbundwerkstoffen (Wood Plastic Composite, WPC) erfordert das Wissen um seine spezifischen Eigenschaften, insbesondere dem Brand risiko. Dabei können Flammschutzmittel die Entflammbarkeit, Wärmeabgabe und die Brandausbreitung des Materials verringern. Deshalb sind der gezielte und effiziente Einsatz und die Kenntnis über die Wirkungsweise der Flammschutzmittel im WPC für den Brandschutz von enormer Bedeutung. Dazu gehört auch die Rauchentwicklung im Brandfall. Rauch beeinflusst aufgrund seiner Toxizität und seiner Sichttrübung die Fluchtmöglichkeit der betroffenen Personen. In der Rauchkammer nach ISO 5659-2 wird die Rauchentwicklung von flachen Werkstoffproben ermittelt. Die Rauchgastoxizität bzw. die Rauchgaszusammensetzung wird mithilfe der FTIR (Fourier Transformierte Infrarot)-Spektroskopie ermittelt. Frei werdende Partikel schädigen die Atemorgane und beeinflussen damit auch die Fluchtfähigkeit von Personen im Brandfall. Aussagen zur Partikelemission können mithilfe eines an die Rauchkammer gekoppelten Partikelanalysators getroffen werden. Im Rahmen dieser Arbeit wurden verschiedene flammgeschützte WPC-Systeme hinsichtlich ihres Rauchverhaltens in der Rauchkammer untersucht. Die Ergebnisse zu emittierten toxischen Gasen, Partikeln und zur Rauchentwicklung werden vorgestellt und in Abhängigkeit von den eingesetzten Flammschutzmitteln im WPC diskutiert. KW - Rauchgase KW - Holz-Kunststoff-Verbundwerkstoffe KW - Partikel KW - Flammschutz PY - 2019 DO - https://doi.org/10.1002/bate.201900020 VL - 96 SP - 1 EP - 12 PB - Wiley AN - OPUS4-48157 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bhuyan, Md Delwar Hossain A1 - Le Touz, N. A1 - Gautier, G. A1 - Döhler, M. A1 - Hille, Falk A1 - Dumoulin, J. A1 - Mevel, L. T1 - Load vector based damage localization with rejection of the temperature effect N2 - The Stochastic Dynamic Damage Locating Vector (SDDLV) approach is a vibration-based damage localization method based on both a finite element model of a structure and modal parameters estimated from output-only measurements in the damage and reference states. A statistical version of the Approach takes into account the inherent uncertainty due to noisy measurement data. In this paper, the effect of temperature fluctuations on the performance of the method is analyzed in a model-based approach using a finite element model with temperature dependent parameters. Robust damage localization is carried out by rejecting the temperature influence on the identified modal parameters in the damaged state. The algorithm is illustrated on a simulated structure. T2 - 8. International Operational Modal Analysis Conference CY - Kopenhagen, Denmark DA - 12. Mai 2019 KW - SDDLV KW - Load vector KW - Temperature rejection KW - Statistical evaluation PY - 2019 SP - 1 EP - 10 AN - OPUS4-48182 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bhuyan, Md Delwar Hossain A1 - Döhler, M. A1 - Lecieux, Y. A1 - Lupi, C. A1 - Thomas, J.-C. A1 - Schoefs, F. A1 - Hille, Falk A1 - Mevel, L. T1 - Statistical subspace based damage localization on Saint-Nazaire bridge mock-up N2 - The subject of damage localization is an important issue for Structural Health Monitoring (SHM) particularly in mechanical or civil structures under ambient excitation. In this paper, the statistical subspacebased damage localization method has been applied on a benchmark application, namely a 1/200 scale model of the Saint-Nazaire Bridge, which is a cable-stayed bridge located on the Loire River near the river’s mouth. The employed damage localization method combines data-driven features with physical parameter information from a finite element model in statistical tests, avoiding typical ill-conditioning problems of FE model updating. Damage is introduced in the mockup for cable failures on some of the 72 cables. The purpose of the experiment is to assess the capability of damage assessment methods to find a cable failure. T2 - 8. International Operational Modal Analysis Conference CY - Kopenhagen, Denmark DA - 12. Mai 2019 KW - Damage localization KW - Cable-stayed bridge KW - Cable failure KW - Structural health monitoring PY - 2019 SP - 1 EP - 9 AN - OPUS4-48183 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Viefhues, Eva A1 - Döhler, M. A1 - Zhang, Q. A1 - Hille, Falk A1 - Mevel, L. T1 - Subspace-based Damage Detection with Rejection of the Temperature Effect and Uncertainty in the Reference N2 - Temperature variation can be a nuisance that perturbs vibration based structural health monitoring (SHM) approaches for civil engineering structures. In this paper, temperature affected vibration data is evaluated within a stochastic damage detection framework, which relies on a null space based residual. Besides two existing temperature rejection approaches – building a reference state from an averaging method or a piecewise method – a new approach is proposed, using model interpolation. In this approach, a general reference model is obtained from data in the reference state at several known reference temperatures. Then, for a particular tested temperature, a local reference model is derived from the general reference model. Thus, a well fitting reference null space for the formulation of a residual is available when new data is tested for damage detection at an arbitrary temperature. Particular attention is paid to the computation of the residual covariance, taking into account the uncertainty related to the null space matrix estimate. This improves the test performance, contrary to prior methods, for local and global damages, resulting in a higher probability of detection (PoD) for the new interpolation approach compared to previous approaches. T2 - International Operational Modal Analysis Conference CY - Copenhagen, Danmark DA - 13.05.2019 KW - Uncertainty KW - Statistical method KW - Subspace-based method KW - Temperature rejection KW - Model interpolation PY - 2019 SP - 1 EP - 11 AN - OPUS4-48240 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bhuyan, Md Delwar Hossain A1 - Le Touz, N. A1 - Gautier, G. A1 - Döhler, M. A1 - Hille, Falk A1 - Dumoulin, J. A1 - Mevel, L. T1 - Load Vector Based Damage Localization with Rejection of the Temperature Effect N2 - The Stochastic Dynamic Damage Locating Vector (SDDLV) approach is a vibration-based damage localization method based on both a finite element model of a structure and modal parameters estimated from output-only measurements in the damage and reference states. A statistical version of the Approach takes into account the inherent uncertainty due to noisy measurement data. In this paper, the effect of temperature fluctuations on the performance of the method is analyzed in a model-based approach using a finite element model with temperature dependent parameters. Robust damage localization is carried out by rejecting the temperature influence on the identified modal parameters in the damaged state. The algorithm is illustrated on a simulated structure. T2 - International Operational Modal Analysis Conference CY - Copenhagen, Danmark DA - 13.05.2019 KW - Statistical evaluation KW - Damage localization KW - SDDLV KW - Load vector KW - Temperature rejection PY - 2019 SP - 1 EP - 10 AN - OPUS4-48241 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bhuyan, Md Delwar Hossain A1 - Döhler, M. A1 - Lecieux, Y. A1 - Lupi, C. A1 - Thomas, J. A1 - Schoefs, F. A1 - Hille, Falk A1 - Mevel, L. T1 - Statistical Subspace-based Damage Localization on Saint-Nazaire Bridge Mock-Up N2 - The subject of damage localization is an important issue for Structural Health Monitoring (SHM) particularly in mechanical or civil structures under ambient excitation. In this paper, the statistical subspacebased damage localization method has been applied on a benchmark application, namely a 1/200 scale model of the Saint-Nazaire Bridge, which is a cable-stayed bridge located on the Loire River near the river’s mouth. The employed damage localization method combines data-driven features with physical parameter information from a finite element model in statistical tests, avoiding typical ill-conditioning problems of FE model updating. Damage is introduced in the mockup for cable failures on some of the 72 cables. The purpose of the experiment is to assess the capability of damage assessment methods to find a cable failure. T2 - International Operational Modal Analysis Conference CY - Copenhagen, Danmark DA - 13.05.2019 KW - Structural health monitoring KW - Damage localization KW - Cable-stayed bridge KW - Cable failure PY - 2019 SP - 1 EP - 9 AN - OPUS4-48243 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hüllmann, Dino A1 - Neumann, Patrick P. A1 - Monroy, J. A1 - Lilienthal, A. J. T1 - A realistic remote gas sensor model for three-dimensional olfaction simulations N2 - Remote gas sensors like those based on the Tunable Diode Laser Absorption Spectroscopy (TDLAS) enable mobile robots to scan huge areas for gas concentrations in reasonable time and are therefore well suited for tasks such as gas emission surveillance and environmental monitoring. A further advantage of remote sensors is that the gas distribution is not disturbed by the sensing platform itself if the measurements are carried out from a sufficient distance, which is particularly interesting when a rotary-wing platform is used. Since there is no possibility to obtain ground truth measurements of gas distributions, simulations are used to develop and evaluate suitable olfaction algorithms. For this purpose several models of in-situ gas sensors have been developed, but models of remote gas sensors are missing. In this paper we present two novel 3D ray-tracer-based TDLAS sensor models. While the first model simplifies the laser beam as a line, the second model takes the conical shape of the beam into account. Using a simulated gas plume, we compare the line model with the cone model in terms of accuracy and computational cost and show that the results generated by the cone model can differ significantly from those of the line model. T2 - 2019 IEEE International Symposium on Olfaction and Electronic Nose (ISOEN) CY - Fukuoka, Japan DA - 26.05.2019 KW - Remote gas sensor KW - Gas detector KW - TDLAS KW - Sensor modelling PY - 2019 SN - 978-1-5386-8327-9 SN - 978-1-5386-8328-6 DO - https://doi.org/10.1109/ISOEN.2019.8823330 SP - 1 EP - 3 PB - IEEE AN - OPUS4-48919 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Berchtold, Florian T1 - Metamodel for complex scenarios in fire risk analysis of road tunnels N2 - The risk analysis of road tunnels faces a growing complexity in fire scenarios, e.g. caused by new energy carriers. Essentially, such complex scenarios involve many interactions between the tunnel users, the fire source and the safety measures. One example is the alarm of tunnel users either initiated by the perception of smoke or by the fire alarm system. To consider these interactions for the quantification of consequences, e.g. fatalities, risk analysis requires a complex model. However, the complex model can compute in practice only few discrete scenarios due to its high computational cost, whereas risk analysis generally needs the consequences of a high number of random scenarios. Metamodels can solve this contradiction. They are able to approximate the consequences of many random scenarios with low computational cost based on the consequences of few discrete scenarios computed with the complex model. The efficiency of metamodels depends on the required number of these discrete scenarios. In this sense, this dissertation proposes an efficient metamodel within an innovative methodology for risk analysis of road tunnels to allow to consider an increased complexity of scenarios. This metamodel applies the following methods or models: the projection array-based design method specifies the experimental design for the discrete scenarios; the combination of the fire model FDS and the microscopic evacuation model FDS+Evac constitutes the complex model; and moving least squares produces the response surface model. The response surface model approximates the consequences of the random scenarios and therewith introduces an uncertainty, called metamodel uncertainty, which is quantified with the prediction interval method. Additionally, stochastic individual characteristics of tunnel users in discrete scenarios computed with FDS+Evac attribute evacuation uncertainties to the consequences. An original development in this dissertation, the ’direct approach’, directly transfers the evacuation uncertainties of the discrete scenarios to any random scenario. The evaluation of the metamodel in this dissertation shows following results. Firstly, the response surface model sufficiently represents the consequences of the complex model. Secondly, the metamodel uncertainty is also essential for this representation, but the prediction interval method reveals a drawback in the risk analysis. Potential approaches to deal with this drawback are discussed. Finally, the direct approach reproduces the evacuation uncertainty of the complex model which then clearly affects the consequences of random scenarios. Therefore, the consideration of the evacuation uncertainty plays an important role for the risk analysis. Furthermore, the projection array-based design method was adapted in this dissertation with two approaches, namely the combination of the experimental designs for FDS and FDS+Evac as well as their sequential refinement. Both approaches contribute to the efficiency of the metamodel. These results lead to following conclusions. Firstly, the metamodel efficiently integrates the consequences of discrete scenarios into risk analysis and thus allows to consider an increased complexity. Secondly, the metamodel is an advancement for risk analysis not only for road tunnelsbutalsomoregeneralinfiresafetyengineering. Forthesetworeasons,themetamodel might be interesting for other methodologies for risk analysis. In addition, the metamodel is generic and is therefore widely applicable on other issues beside from risk analysis, e.g. to assess the safety of structures related to time-consuming experiments depending on multiple variables. N2 - Risikoanalysen für Straßentunnel müssen eine immer größere Komplexität in Brandszenarien berücksichtigen, beispielsweise verursacht durch neue Energieträger. Dabei hängt die Komplexität von Szenarien mit einer Vielzahl von Interaktionen zwischen den Tunnelnutzern, der Brandquelle und den Sicherheitsmaßnahmen zusammen. Zum Beispiel werden Tunnelnutzer entweder direkt durch Rauch oder durch die Brandmeldeanlage alarmiert. Um die Interaktionen bei der Berechnung der Konsequenzen, wie z.B. getötete Personen, zu berücksichtigen, benötigen Risikoanalysen komplexe Modelle. Allerdings können komplexe Modelle wegen ihres hohen Zeitaufwandes nur wenige diskrete Szenarien simulieren, wohingegen Risikoanalysen auf Konsequenzen einer Vielzahl von Zufallsszenarien basieren. Als Lösung dieses Widerspruchs kommen Metamodelle in Betracht. Sie können die Konsequenzen von vielen Zufallsszenarien innerhalb kurzer Zeit näherungsweise berechnen und verwenden dafür die Konsequenzen von wenigen mit dem komplexen Modell simulierten diskreten Szenarien. Die Effizienz von Metamodellen hängt dabei mit der nötigen Anzahl von diskreten Szenarien zusammen. Demnach wird in dieser Dissertation ein effizientes Metamodell in eine selbst erstellteMethodikzurRisikoanalysefürStraßentunnelintegriert,umdamiteinehöhereKomplexität der Szenarien einbeziehen zu können. Das Metamodell setzt sich aus folgenden Methoden und Modellen zusammen: die ’projection array-based design’-Methode definiert den Simulationsplan für die diskreten Szenarien; eine Kombination aus dem Brandmodell FDS und dem mikroskopischen Evakuierungsmodell FDS+Evac bildet das komplexe Modell; und ’moving least squares’ dient zur Erstellung des Antwortflächenmodells. DasAntwortflächenmodellberechnetnäherungsweisedieKonsequenzen der Zufallsszenarien und erzeugt dadurch eine Unsicherheit, die Metamodellunsicherheit. Sie wird mit der ’prediction interval’-Methode bestimmt. Zusätzlich verursachen individuelle Eigenschaften der Tunnelnutzer in den mit FDS+Evac simulierten diskreten Szenarien Evakuierungsunsicherheiten in den Konsequenzen. Ein in der Dissertation neu entwickelter Ansatz, der ’direkte Ansatz’, überträgt die Evakuierungsunsicherheit der diskreten Szenarien unmittelbar auf die Zufallsszenarien. Die Untersuchung des Metamodels in der Dissertation führte zu folgenden Ergebnissen. Erstens,dasAntwortflächenmodellbildetdieKonsequenzenderdiskretenSzenarienausreichend genau ab. Zweitens, dazu trägt die Metamodellunsicherheit wesentlich bei. Allerdings zeigt die ’prediction-interval’-Methode einen Nachteil für die Risikoanalyse. Zur Lösung dieses Nachteils werden potentielle Ansätze diskutiert. Und drittens, der direkte Ansatz gibt die Evakuierungsunsicherheiten des komplexen Modells wieder, welche dann die Konsequenzen der Zufallsszenarien deutlich beeinflussen. Aus diesem Grund ist die Evakuierungsunsicherheit für die Risikoanalyse wichtig. Zusätzlich wurde die ’projection array-based design’Methode in dieser Dissertation mit zwei Ansätzen angepasst: der Verknüpfung beider Simulationspläne für FDS und FDS+Evac sowie deren schrittweisen Verfeinerung. Die Effizienz des Metamodels wird durch beide Ansätze erhöht. Diese Ergebnisse führen zu folgenden Schlussfolgerungen: erstens, das Metamodell integriert die Konsequenzen der diskreten Szenarien auf eine effiziente Weise in die Risikoanalyse und ermöglicht dadurch die Berücksichtigung einer höheren Komplexität; und zweitens, das Metamodell stellt einen Fortschritt für Risikoanalysen nicht nur für Straßentunnel sondern auch allgemein im Brandingenieurwesen dar. Aus diesen beiden Gründen kann das Metamodell für andere Methodiken zur Risikoanalyse interessant sein. Zudem ist das Metamodel flexibel auf andere Problemstellungen außerhalb der Risikoanalyse anwendbar, wie z.B. der Bewertung der Bauwerkssicherheit, welche von zeitaufwändigen Untersuchung und mehreren Variablen abhängt. KW - Metamodel KW - Surrogate KW - Uncertainty KW - Risk KW - Consequence KW - Fire KW - Evacuation KW - Tunnel PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:hbz:468-20200114-101029-6 DO - https://doi.org/10.25926/evq8-h241 SP - 1 EP - 171 PB - Bergische Universität Wuppertal CY - Wuppertal AN - OPUS4-51039 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilsch, Gerd A1 - Günther, Tobias A1 - Völker, Tobias T1 - LIBS – Betonanalytik mit dem Laser N2 - Es wird ein alternatives Verfahren zur schnellen zweidimensionalen Analyse der chemischen Zusammensetzung von Baustoffen vorgestellt. Dieses beruht auf der Kombination des Abtrags einer geringen Materialmenge durch einen gepulsten Laser, der Plasmaerzeugung und der Analyse der Lichtemission des Plasmas mittels optischer Spektroskopie. Es können prinzipiell alle Elemente gleichzeitig nachgewiesen werden. Damit ist es möglich einerseits Informationen über den Baustoff an sich als auch über den Eintrag potentiell schädigender Elemente (z. B. Cl, C, Na, K, S) zu gewinnen. Das Verfahren kann automatisiert im Labor oder als mobile Version direkt vor Ort eingesetzt werden. Es liefert zweidimensionale Bilder der Elementverteilung in Echtzeit. Es kann ohne große Probenvorbereitung z. B. direkt an der Querschnittsfläche eines Bohrkernes gemessen werden. Die Messung dauert nur wenige Minuten. Das Prinzip der Messung, die Vor- und die Nachteile, sowie die verfügbare Gerätetechnik für den Einsatz im Labor oder direkt am Bauwerk werden vorgestellt. Abschließend werden praktische Beispiele für die Anwendung des LIBS-Verfahrens zur Erfassung des Chlorid-Eintrages, der Karbonatisierung und der Verteilung von Schwefel präsentiert. T2 - 9. Betonfachtagung CY - Berlin, Germany DA - 12.11.2019 KW - Chloride KW - Beton KW - LIBS KW - Schädigung PY - 2019 SP - 1 PB - InformationsZentrum Beton GmbH CY - Berlin AN - OPUS4-51675 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Burkert, Andreas A1 - Babutzka, Martin T1 - Korrosionsschutz durch Deckschichtbildung und Passivität N2 - Metallene Konstruktionswerkstoffe reagieren infolge ihres thermodynamisch instabilen Zustandes mehr oder weniger stark mit Stoffen aus der Umgebung. Eine große Rolle bei diesen Reaktionen spielt das Feuchtigkeitsangebot an der Metalloberfläche, welches nicht zwingend mit einem sichtbaren Wasserfilm einhergehen muss. An der Atmosphäre bilden sich an sauberen Metalloberflächen bei etwa 80 % relativer Luftfeuchte, bei versalzten Oberflächen auch schon ab etwa 25 % r. F., Feuchtfilme aus. Im Feuchtfilm laufen grundsätzlich die gleichen elektrochemischen Reaktionen ab, wie diese von wässrigen Medien bekannt sind. Dabei geht das Metall zunächst in Ionenform und in nachgelagerten Reaktionen in einen thermodynamisch stabilen Zustand in Form unterschiedlichster Oxid- und Hydroxidverbindungen über. Die so entstehenden Korrosionsprodukte können im Feuchtigkeitsfilm begrenzt löslich oder unlöslich sein und lagern sich auf den Oberflächen der Konstruktionswerkstoffe häufig als feste Korrosionsprodukte ab bzw. wachsen dort auf. Je nachdem wie die Korrosionsprodukte strukturell zum Untergrund passen, können sich dichte, sehr gut haftende Schichten ausbilden oder poröse, dicke Schichten ohne nennenswerte Haftung aufwachsen. Wachsen dichte, porenfreie Schichten mit guter Haftung auf, die im umgebenden Medium unlöslich sind, wird die weitere Auflösung des Metalls stark gehemmt. Man spricht dann von der Ausbildung schützender Deckschichten bzw. von Passivschichten auf welcher der Korrosionsschutz und damit die Dauerhaftigkeit vieler Konstruktionswerkstoffe beruhen. Kaesche bezeichnete die Passivität sehr treffend als „optimalen Grenzfall des Korrosionsschutzes durch Schichten von Korrosionsprodukten“. Aus technischer Sicht hält Kaesche eine Unterscheidung von Deckschichten bzw. Passivschichten für nicht zwingend erforderlich, da beide die Korrosionsgeschwindigkeit in gleichem Maß herabsetzen können. Die Übergänge zwischen den meist dickeren und dadurch sichtbaren Deckschichten und den meist dünnen, nicht sichtbaren Passivschichten sind fließend. T2 - 18. Tagung "Korrosionsschutz in der maritimen Technik" CY - Hamburg, Germany DA - 30.01.2019 KW - Korrosionsschutz KW - Überzüge KW - Deckschichten KW - Passivität PY - 2019 SN - 978-3-935406-70-3 VL - 18 SP - 25 EP - 38 AN - OPUS4-47307 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fischer, Daniel A1 - Beck, Uwe T1 - Visualisierung von mikro- und nanoskalierten Oberflächenstrukturen mittels abbildender Ellipsometrie N2 - In den letzten Jahren hat die Einbindung der abbildenden Ellipsometrie in die Gruppe der optischen Verfahren zur Oberflächencharakterisierung ein enormes Potential bei der Analyse von topologischen Strukturänderungen gezeigt. Der dabei abgebildete Kon-trast wurde typischerweise auf Änderungen im Brechungsindex, Absorptionseffekte oder Schichtdickenänderungen zurückgeführt. In späteren Studien wurde festgestellt, dass auch andere Faktoren, wie etwa die Krümmung der Oberfläche oder Kanten von Struktu-ren einen signifikanten Einfluss auf die Messung der ellipsometrischen Paramater haben. Um diese Effekte aus der ellipsometrischen Messung extrahieren zu können, wird auf die Analyse der Müller-Matrix zurückgegriffen. In dem hier vorliegenden Beitrag wird gezeigt, wie die Müller-Matrix-Imaging Ellipsomet-rie (MM-IE) zur Charakterisierung von Oberflächenstrukturen verwendet werden kann. Dazu werden mikro- und nanoskaliert gekrümmte Oberflächen zunächst mit verschiede-nen Referenzmethoden, wie Rasterelektronenmikroskopie (SEM), Lichtmikroskopie (OM), Weißlichtinterferenzmikroskopie (WLIM) und Rasterkraftmikroskopie (AFM) vali-diert erfasst. Der anschließende Vergleich mit den Ergebnissen der Müller-Matrix-Ima-ging-Ellipsometrie ermöglicht eine Korrelation der zugrunde liegenden Strukturphäno-mene mit den ellipsometrischen Daten. In diesem Artikel wird das Prinzip an drei industriell relevanten Strukturgruppen demonstriert: Sub-Mikropartikel, Mikropartikel und sub-mikroskalierte Vertiefungen. T2 - 14. ThGOT Thementage Grenz- und Oberflächentechnik und 6. Kolloquium Dünne Schichten in der Optik CY - Zeulenroda, Germany DA - 12.03.2019 KW - Ellipsometrie KW - Nanoskaliert KW - Mikroskaliert KW - Oberflächengeometrie KW - Brechungsindex KW - Müller-Matrix-Ellipsometrie PY - 2019 SN - 978-3-00-062102-4 SP - 1 EP - 5 AN - OPUS4-47646 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lange, Thorid A1 - Hidde, Gundula A1 - Beck, Uwe A1 - Naumann, F. A1 - Kärkkänen, I. A1 - Gargouri, H. T1 - Nanoskalige Haftvermittler zur Erhöhung der Haft- bzw. Klebfestigkeit unter Verwendung von ALD-Hybridprozessen N2 - Ziel des Projektes HARFE (Haftfestigkeit Reproduzierbarkeit Festigkeit) war es, eine Er-höhung der Haft- bzw. Klebfestigkeit auf Niedrigenergie-Polymeren (PE, PP, PTFE) zu erreichen. SENTECH realisierte dazu plasmachemische Oberflächenaktivierungen mit O2 und die Abscheidung von Aluminiumoxidschichten (Al2O3) mittels Atomic Layer Deposition (ALD), wobei die Ellipsometrie zum in-situ Monitoring der ALD-Prozesse diente. Die BAM charakterisierte die modifizierten Oberflächen bezüglich der Oberflächenenergie (OFE) und bestimmte die Verbund- bzw. Klebfestigkeit mittels der Zentrifugentechnologie T2 - 14. ThGOT Thementage Grenz- und Oberflächentechnik und 6. Kolloquium Dünne Schichten in der Optik CY - Zeulenroda, Germany DA - 12.03.2019 KW - Haftvermittler KW - ALD-Hybridprozesse KW - Klebfestigkeit KW - Atomic Layer Deposition KW - Al2O3-Schichten KW - Oberflächenenergie PY - 2019 SN - 978-3-00-062102-4 SP - 1 EP - 2 CY - Zeulenroda, Germany AN - OPUS4-47656 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Detjens, Marc T1 - Untersuchung des Elektrolyseprinzips zur Bestimmung von geringen Feuchtegehalten und der Einsatz von ionischen Flüssigkeiten als neuartige Sensorbeschichtung N2 - Feuchte, sei es Material- oder Gasfeuchte, ist eine wichtige Messgröße bei der Qualitätsbeurteilung von Kunststoffen, landwirtschaftlichen Erzeugnissen, Energieträgern, Arzneimitteln, industriell und medizinisch verwendeten Gasen. Deswegen gibt es ein Interesse Feuchtemesserfahren hinsichtlich Präzision, Wiederholbarkeit, Rückführbarkeit und Stabilität kontinuierlich zu verbessern. Ein bewährtes Messprinzip für diese Aufgabe wurde bereits 1959 von Keidel entwickelt und basiert auf der Absorption und Elektrolyse von Wasserdampf. Der einfache Aufbau dieses Prinzips besteht aus einem Sensorelement, einer Gleichspannungsquelle, einem Digitalmultimeter und einen geregelten Gasstrom über den Sensor. Nach dem Faraday’schen Gesetz der Elektrolyse korreliert bei dem Messprinzip die Ladungsmenge mit der elektrolysierten Wassermasse. Jedoch bedarf es in der heutigen Zeit einer Validierung der Sensoren, weil durch gezielte Miniaturisierung weniger aktive Fläche vorhanden ist und somit das Faraday’sche Gesetz nicht vollständig anwendbar ist. In dieser Arbeit wurden coulometrische Sensoren mit einer planaren Elektrodenstruktur hinsichtlich der Einflüsse von unterschiedlichen Gasen, der Gastemperatur und dem -druck untersucht. Zusätzlich wurde eine neuartige Sensorbeschichtung basierend auf einer ionischen Flüssigkeit getestet. Des Weiteren wurde ein Messgerät für die abgestufte Bestimmung der Materialfeuchte und Wasseraktivität entwickelt und dessen messtechnischer Einsatz untersucht. KW - Coulometrie KW - Feuchtigkeitsmessung KW - Ionische Flüssigkeit KW - Mikrosensor PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:gbv:ilm1-2019000209 SP - 1 EP - 118 CY - Technische Universität Ilmenau AN - OPUS4-52177 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kamaraj, Abinaya A1 - Erning, Johann Wilhelm A1 - Reimann, S. A1 - Ahrens, A. T1 - Susceptibility of 304 stainless steel to crevice corrosion in electrochemically active fluids N2 - The susceptibility of AISI 304 stainless steel to crevice corrosion on the effect of contact with electrochemically active fluids was investigated using exposure and stepwise potentiostatic polarisation. Crevice materials made up of 304 SS and Polyether ether ketone (PEEK) forming two kinds of crevices including 304 SS-to-PEEK and 304 SS-to-304 SS were tested. T2 - NACE International Corrosion Conference 2019 CY - Nashville, TN, USA DA - 24.03.2019 KW - Steel KW - Crevice KW - Corrosion KW - ECA KW - Stainless PY - 2019 SP - Paper 12868 PB - NACE International CY - Houston AN - OPUS4-49286 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rietz, U. A1 - Küchler, S. A1 - Lerche, D. A1 - Lange, Thorid A1 - Hielscher, Stefan A1 - Beck, Uwe T1 - Zentrifugalkraftbasierte Mehrprobenprüfung in einer analytischen Zentrifuge zur Bestimmung von Kleb- und Haftfestigkeiten: Metallische Referenzverbunde, Plasmaaktivierung von Polymeren, Schichthaftung auf GFK, Wirkung von Primern N2 - Das Fügeverfahren Kleben bietet viele Vorteile wie z.B. das Verbinden schwieriger Materialklassen, geringe thermische Belastung (Strukturveränderung/-schwächung) der Fügepartner und eine Lastverteilung über den gesamten Fügebereich. Die Auswahl an verfügbaren Klebstoffen und Vorbehandlungsoptionen ist dabei ebenfalls vielfältig. Einige Polymere weisen darüber hinaus Eigenschaften auf, die eine Herstellung von festen und dauerhaft beanspruchbaren Klebverbindungen erschweren. Mittels Oberflächenbehandlung, z.B. durch Plasmafeinreinigung bzw. –aktivierung, können die Grenzflächern solcher Polymere - bezogen auf die Eignung als Fügeteilpartner – optimiert werden. Schnelle Prüfverfahren zur Ermittlung von Verbundeigenschaften sind somit erforderlich. Das Messprinzip Centrifugal Adhesion Testing Technologie verwendet die radial gerichtete Zentrifugalkraft als Belastungsgröße des zu testenden Verbunds, die durch Variation der Drehzahl gesteuert wird. Bei Erreichen der kritischen Beanspruchung trennt sich ein aufgeklebter Prüfstempel vom Substrat. Zeitgleich wird ein positionsbezogenes IR-Signal aus dem drehenden Rotor an das Basisgerät gesendet und zusammen mit der Drehzahl an die PC-Software übertragen. Für jede Probe wird die Bruchkraft berechnet und in Echtzeit angezeigt. Der Adhesion Analyser LUMiFrac® untersucht bis zu acht Prüfkörper unter identischen Bedingungen. Das neue Messprinzip erfüllt die Anforderungen von DIN EN 15870, DIN EN 14869-2, ISO 4624 sowie DIN EN 13144. Die Multiprobentestung ermöglicht schnelle Charakterisierungen von Klebverbindungen. So kann der Effekt einer Plasmabehandlung von Bauteilen auf die Verbundfestigkeit zeitsparend bestimmt werden. Die gezielte Veränderung unterschiedlicher Plasma-Parameter, wie beispielsweise, die Plasmazusammensetzung, der Abstand vom Plasmabrenner zur Oberfläche oder die Verweildauer unter dem Brenner, beeinflußt die Festigkeit des Klebsystems und ist dem LUMiFrac direkt quantifizierbar. Neben der Festigkeitsbestimmung von Klebverbindungen ist die Haftung von Schichtsystemen ein wichtiger Anwendungsbereich. Ergebnisse für Zug- und Scherbeanspruchung, realisiert mit unterschiedlichen Prüfkörper-Geometrien, werden vorgestellt. Ferner werden verschiedene festigkeitsbeeinflussende Faktoren, wie Prüfgeschwindigkeit oder Substratverformung bei Beanspruchung untersucht T2 - 35. Workshop des ak-adp CY - Nuremberg, Germany DA - 20.11.2019 KW - Adhäsion KW - Mehrprobenprüfung KW - Analytische Zentrifuge KW - Kleb- und Haftfestigkeit PY - 2019 SN - 978-3-00-063646-2 SP - 100 EP - 109 AN - OPUS4-50149 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Biegler, M. A1 - Wang, J. A1 - Graf, B. A1 - Rethmeier, Michael T1 - Automated tool-path generation for rapid manufacturing and numerical simulation of additive manufacturing LMD geometries N2 - In additive manufacturing (AM) Laser Metal Deposition (LMD), parts are built by welding layers of powder feedstock onto a substrate. Applications for steel powders include forging tools and structural components for various industries. For large parts, the choice of tool-paths influences the build-rate, the part performance and the distortions in a highly geometry-dependent manner. With weld-path lengths in the range of hundreds of meters, a reliable, automated tool path generation is essential for the usability of LMD processes. In this contribution, automated tool-path generation approaches are shown and their results are discussed for arbitrary geometries. The investigated path strategies are the classical approaches: “Zig-zag-” and “contour-parallel-strategies”. After generation, the tool-paths are automatically formatted into g-code for experimental build-up and ASCII for a numerical simulation model. Finally, the tool paths are discussed in regards to volume-fill, microstructure and porosity for the experimental samples. This work presents a part of the IGF project 18737N “Welding distortion simulation” (FOSTA P1140) T2 - 4th European Steel Technology and Application Days CY - Dusseldorf, Germany DA - 24.06.2019 KW - Additive manufacturing KW - Directed Energy Deposition KW - Path planning KW - DED KW - Mechanical properties KW - Porosity PY - 2019 SP - 1 AN - OPUS4-50045 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, A. A1 - Kranzmann, Axel T1 - Effect of CO2, atmosphere and pressure on the stability of C35CrMo17 stainless steel in laboratory CCS-environment N2 - During carbon sequestration the CO2-induced corrosion of injection pipe steels is a relevant safety issue when emission gasses are compressed into deep geological layers. The reliability of the high alloyed steel X35CrMo17 suitable as injection pipe for the geological onshore CCS-site (Carbon Capture and Storage) in the Northern German Basin, is demonstrated in laboratory experiments in equivalent corrosive environment (T = 60 °CC, p = 1–100 bar, aquifer water, CO2-flow rate of 9 L/h, 700–8000 h exposure time). Corrosion kinetics and microstructure were characterized and compared to other potential injection pipe steels (42CrMo4, X46Cr13, X20Cr13 and X5CrNiCuNb16-4). T2 - 14th Greenhouse Gas Control Technologies Conference CY - Melbourne, Australia DA - 21.10.2018 KW - Steel KW - Supercritical CO2 KW - Pipeline KW - Corrosion KW - CO2-storage PY - 2019 SP - 1 EP - 9 PB - Elsevier Ltd. AN - OPUS4-50382 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, A. A1 - Gröber, A. A1 - Kranzmann, Axel T1 - The Role of Surface Texture on the Corrosion Behavior of High Alloyed Steel Exposed to Saline Aquifer Water Environments N2 - Coupons of X5CrNiCuNb16-4 that may be used as injection pipe with 16% Chromium and 0.05% Carbon (1.4542, AISI 630) were exposed for 3000 h to CO2-saturated saline aquifer water similar to the conditions in the Northern German Basin at ambient pressure and 60 °C. Surface corrosion layers and pits reveal carbonate corrosion products on the surface such as FeCO3 and FeOOH as the main precipitation phases with no dependence on the original surface roughness. Corrosion rates for polished and technical surfaces were below 0.005 mm/year compared to corrosion rates of 0.035 mm/year after shot peening. T2 - 14th Greenhouse Gas Control Technologies Conference CY - Melbourne, Australia DA - 21.10.2018 KW - High alloyed steel KW - Pitting KW - Surface KW - Roughness KW - CO2 PY - 2019 SP - 1 EP - 8 PB - Elsevier Ltd. AN - OPUS4-50375 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Beck, Uwe A1 - Hielscher, Stefan A1 - Lerche, D. T1 - Abschlussbericht zum BMWi - MNPQ – Verbundprojekt QUO VADIS PLUS (Mehr-Proben-Festigkeitsprüfung zur Qualitätssicherung in der Materialtechnik und Validierung der Zentrifugentechnologie bei Druck- bzw. Zugbeanspruchung) N2 - Im Fokus des Vorhabens steht das mit dem Innovationspreis Berlin-Brandenburg 2012 ausgezeichnete Mehr-Proben-Prüfverfahren zur Festigkeitsprüfung unter Verwendung einer analytischen Zentrifuge mit dem Ziel des Einsatzes in der Qualitätssicherung. Nachdem im MNPQ-Projekt QUO VADIS die grundsätzliche Anwendbarkeit der Zentrifugentechnologie auf Beanspruchungen auf Zug (Kleb-, Haft- und Verbundfestigkeit) nachgewiesen worden war, wurden im Vorhaben QUO VADIS PLUS folgende erweiterte Prüfszenarien und technische Weiterentwicklungen etabliert: 1. Beanspruchung auf Druck (Härte von Materialien, Kompressibilität von Schäumen, Kompaktierbarkeit von Pulvern), 2. Erweiterung der Beanspruchung auf Zug (Kombination von Normal- und Lateralkräften), 3. Erweiterung auf die Bewertung plasto-elastischenn Materialverhaltens, 4. Vermeidung von Schockwellen im Hochlastbereich KW - Analytische Zentrifuge KW - Mehr-Proben-Prüfverfahren KW - Härte KW - Kompressibilität KW - Kompaktierbarkeit KW - Haftfestigkeit KW - Klebfestigkeit KW - Verbundfestigkeit PY - 2019 N1 - Das Dokument unterliegt der Vertraulichkeit und kann nicht zugänglich gemacht werden Projektlaufzeit: 01.05.2015 bis 28.02.2019 The document is subject to confidentiality restrictions and cannot be made accessible Project runtime: 01.05.2015 to 28.02.2019 SP - 1 EP - 20 AN - OPUS4-50406 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - El-Sari, B. A1 - Biegler, M. A1 - Graf, B. A1 - Rethmeier, Michael T1 - Numerische Simulation einer AM-Prozesskette im DED Auftragschweißen N2 - Das DED Auftragschweißen ist ein additives Fertigungsverfahren für Metalle, bei dem das Material schichtweise auf ein Substrat aufgetragen wird. Die schnellen Temperaturzyklen rufen Spannungsgradienten im Bauteil hervor. Der schichtweise Aufbau der Bauteile verursacht eine anisotrope Mikrostruktur. Mittels nachgelagerter Wärmebehandlung können diese Effekte verringert werden. Im anschließenden Schritt der Prozesskette wird das additiv hergestellte Bauteil mittels Drahterodieren von dem Substrat abgetrennt. In diesem Beitrag wird eine thermo-mechanische Simulation der gesamten Prozesskette vorgestellt, welche den additiven Aufbau, Wärmebehandlung und das Abtrennen vom Substrat beinhaltet. Anstelle der in der Literatur üblichen schichtweisen Modellierungsstrategie für die DED Simulation wird das gesamte Bauteil in einem Stück vernetzt und der vollständig transiente, schichtweise Materialauftrag über Elementgruppen realisiert. Im Gegensatz zu früheren Simulationen muss der nichtlineare Kontakt zwischen den Schichten nicht berücksichtigt werden, was die Rechenzeiten deutlich verkürzt. Das Modell wurde validiert mittels Abgleiches des Verzugs aus Simulation und Experiment. Die Proben, bestehend aus DIN 1.4404 (AISI 316L), wurden nach jedem Prozessschritt 3D gescannt um den Verzug zu quantifizieren. Zusätzlich wurden Querschnitte und Härtetests nach Vickers von unterschiedlich behandelten Proben durchgeführt, um den Effekt der Wärmebehandlung auf die Mikrostruktur und die Härte des Bauteils zu untersuchen. T2 - 20. Roundtable Simulating Manufacturing CY - Marburg, Germany DA - 22.05.2019 KW - Numerische ISmulation KW - DED KW - AM KW - Laser-Pulver-Auftragschweißen PY - 2019 SP - 1 EP - 14 AN - OPUS4-50046 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Landsberger, B. A1 - Frauendorf, H. A1 - Adler, C. A1 - Plarre, Rüdiger ED - Nilsen, L. ED - Rossipal, M. T1 - Capability and Limitations of Anoxic Treatments for Protecting Museum Collections N2 - Without precaution, insects may cause serious damage to museum collections. Quarantine of potentially infested objects can be logistically challenging. Anoxia under controlled Nitrogen atmosphere is a most gentle but also time-consuming method to eradicate insect pests in all kinds of different materials. Treatment results are usually affected by duration, temperature, humidity and residual oxygen content. During a two-year research project, 34 relevant pest insect species of all developmental stages were tested in different materials (wood, paper, wool) to monitor treatment success and to determine optimum treatment parameters. Duration of treatment ranged from one to three weeks at temperatures of 20–27 °C. As expected, results showed significant differences in mortality among tested species. Highest tolerance of hypoxic conditions was found in elder larvae of Hylotrupes bajulus. Although this species is an unlikely museum pest, it may serve as an overall most tolerant reference. Anobiids and other wood boring beetles are more often an issue related to cultural heritage. A combination of three weeks exposure time at maximum 0.5% residual oxygen and 24 °C, alternatively 1% residual oxygen and 27 °C are recommended for infested artefacts. Imbedding materials in general had no influence on mortality. This study was funded by Deutsche Bundesstiftung Umwelt (DBU). T2 - 4th International Conference Integrated Pest Management (IPM) for Cultural Heritage CY - Stockholm, Sweden DA - 21.05.2019 KW - Controlled atmosphere KW - Museum insect pest KW - Anoxia KW - Nitrogen PY - 2019 SN - 978-91-7209-845-9 SP - 202 EP - 210 AN - OPUS4-50349 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ávila Calderón, Luis A1 - Shakeel, Y. A1 - Schriever, Sina A1 - Gedsun, A. A1 - Forti, M. A1 - Jordan, Hans A1 - Han, Ying A1 - Baer, O. A1 - Aversa, R. A1 - Olbricht, Jürgen A1 - Hammerschmidt, T. A1 - Hickel, T. A1 - Skrotzki, Birgit T1 - NFDI-MatWerk/IUC02 Data schema for creep data of Ni-based superalloys including a comprehensive documentation of test results and metadata N2 - This data schema was developed within the infrastructure use case IUC02: “Framework for curation and distribution of reference datasets” of the consortium NFDI-MatWerk. It intends to define a structured approach for collecting all required information on a creep experiment using the established terminology of the respective test standard ISO 204:2022 and additional terminology agreed upon by the domain experts. The individual entries are grouped according to their content type and sub-summarized under respective headlines, thereby suggesting a basic categorization and a related hierarchy of concepts. This hierarchy can be similarly applied to other test methods and different metallic (and other) materials. In version 1.1 some editorial and formal changes were made. KW - NFDI-MatWerk KW - Digitalisierung KW - Referenzdaten KW - Kriechen KW - Ni-based Superalloys PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-611629 DO - https://doi.org/10.5281/zenodo.11668375 PB - Zenodo CY - Geneva AN - OPUS4-61162 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Ávila Calderón, Luis T1 - Mechanisches Verhalten von additiv gefertigtem nichtrostendem Stahl X2CrNiMo17-12-2 (AISI 316L) und Vergleich zur konventionell gefertigten Variante T1 - Mechanical behavior of additively manufactured stainless steel X2CrNiMo17-12-2 (AISI 316L) and comparison with a conventionally manufactured variant N2 - Die additive Fertigung (AM) metallischer Werkstoffe ist eine Technologie, die zunehmend Gegenstand von Forschungsaktivitäten und industrieller Anwendung ist. Dennoch steht sie noch vor Herausforderungen, um eine breite Nutzung in sicherheitsrelevanten Anwendungen zu erreichen. Die Hauptgründe für die Verzögerung des technologischen Durchbruchs zugunsten von AM-Metallen gegenüber konventionell hergestellten Varianten sind das Fehlen eines tieferen Verständnisses der Prozess-Struktur-Eigenschafts-Beziehungen und die begrenzte Verfügbarkeit von Daten zu den Materialeigenschaften. In diesem Kontext stellt diese Arbeit einen Beitrag sowohl zum Verständnis der Prozess-Struktur-Eigenschafts-Beziehungen als auch zur Verbesserung der Datenlage von 316L dar, einem häufig als Konstruktionswerkstoff in verschiedenen Hochtemperaturbauteilen verwendeten Werkstoff. Die Arbeit legt den Fokus auf die mittels Laser-Pulverbettschmelzen hergestellte Werkstoffvariante, PBF-LB/M/316L. Eine konventionell hergestellte Variante, HR/316L, wurde auch untersucht. Bei PBF-LB/M/316L wurde zusätzlich der Effekt ausgewählter Wärmebehandlungen ausgewertet. Die Untersuchung umfasste die Charakterisierung der mechanischen Eigenschaften und der Verformungs- und Schädigungsmechanismen bei erhöhten Prüftemperaturen bei LCF und Kriechen, wo die Daten und Wissenslage am spärlichsten ist. Außerdem hat die untersuchte PBF-LB/M/316L-Wersktoffvariante einen geringen Porositätsgrad. Somit hat diese Arbeit die Mikrostruktur stärker in den Fokus genommen als die meisten bisher in der Literatur verfügbaren Studien. Die mechanische Prüfkampagne umfasste Zugversuche zwischen Raumtemperatur und 650 °C, LCF-Versuche zwischen Raumtemperatur und 600 °C sowie Kriechversuche bei 600 °C und 650 °C. In Ermangelung konkreter Richtlinien und Normen wurde die Charakterisierung zumeist anhand der bestehenden internationalen Prüfnormen und Probengeometrien durchgeführt. Aus jedem dieser Prüfverfahren wurden die entsprechenden Festigkeits- und Verformungskennwerte ermittelt. Darüber hinaus wurde mit Hilfe gezielter mikrostruktureller Untersuchungen ein Beitrag zum Verständnis des Zusammenhangs zwischen der Mikrostruktur und den mechanischen Eigenschaften in Bezug auf die Verformungs- und Schädigungsmechanismen geleistet. Die Dehngrenze von PBF-LB/M/316L ist etwa doppelt so hoch wie die von HR/316L und dieser Trend setzt sich mit ansteigender Prüftemperatur fort. Die Bruchdehnung ist bei allen Prüftemperaturen geringer. PBF-LB/M/316L weist über den größten Teil der Ermüdungslebensdauer vor allem bei Raumtemperatur höhere zyklische Spannungen als HR/316L auf. Ausschließlich bei den kleinsten Dehnungs-schwingbreiten sind die Ermüdungslebensdauer ausgeprägt kürzer. Das Wechselverformungsverhalten von PBF-LB/M/316L ist durch eine Anfangsverfestigung gefolgt von einer kontinuierlichen Entfestigung charakterisiert, welche bis zum Auftreten der zum Versagen führenden Entfestigung stattfindet. Die Kriechbruchzeiten und die Dauer jeder Kriechphase sind bei allen Kombinationen von Prüfparametern bei PBF-LB/M/316 kürzer als bei HR/316L. Die Spannungsabhängigkeit von PBF-LB/M/316L ist im Vergleich zu HR/316L geringer und die Duktilität beim Kriechen kleiner. Die minimale Kriechrate wird bei allen geprüften Parameterkombinationen bei deutlich geringeren Kriechdehnungen erreicht. Eine Wärmebehandlung bei 450 °C / 4 h bewirkt keine wesentliche Änderungen der Mikrostruktur und Zugversuchseigenschaften. Eine zusätzliche Wärmebehandlung bei 900 °C / 1 h verursacht eine Abnahme der Dehngrenze des PBF-LB/M/316L. Diese blieb aber immer noch um den Faktor 1,5x höher als bei HR/316L. Die Verformungsmerkmale wurden kaum davon beeinflusst. Bezüglich des Kriechverhaltens hat die Wärmebehandlung bei 900 °C / 1 h längere sekundäre und tertiäre Kriechstadien bewirkt und die Kriechdehnung hat sich signifikant erhöht. Die Bruchbilder unterscheiden sich generell nicht nur aber vor allem mit ansteigender Prüftemperatur, bei der bei PBF-LB/M/316L oft interkristalline Rissbildung beobachtet wurde. Die Zellstruktur trägt als der Hauptfaktor zu den unterschiedlichen mechanischen Eigenschaften im Vergleich zur HR/316L-Variante bei. Darüber hinaus spielen mutmaßlich die Kornmorphologie, die Stapelfehlerenergie und der Stickstoffgehalt eine Rolle. N2 - Metal additive manufacturing (AM) is a technology that is increasingly the subject of research activities and industrial applications. However, it still faces challenges to achieve widespread use in safety-relevant applications. The main reasons for the delay of this technological breakthrough in favor of AM metals over conventionally manufactured variants are the lack of a deeper understanding of process-structure-property relationships and the limited availability of data on material properties. In this context, this work contributes to both achieving a better understanding of process-structure-property relationships and the improvement of data for 316L, an alloy frequently used as a structural material in various high-temperature components. The work focuses on a material variant produced by laser pow-der bed fusion, PBF-LB/M/316L. A conventionally produced variant, HR/316L, was also investigated. For PBF-LB/M/316L, the effect of selected heat treatments was also evaluated. The investigation included the characterization of the mechanical properties and the related deformation and damage mechanisms at elevated test temperatures in LCF and creep, where data and knowledge are scarce. The PBF-LB/M/316L variant studied has a low degree of porosity. Thus, this work is more focused on the microstructure than most studies available in the literature. The mechanical test campaign included tensile tests between room temperature and 650 °C, LCF tests between room temperature and 600 °C, and creep tests at 600 °C and 650 °C. In the absence of concrete guidelines and standards for testing of AM metals, the characterization mostly took place using existing international test standards and specimen geometries. From each of the test methods, corresponding strength, and deformation characteristic values were determined. In addition, targeted microstructural investigations contributed to understanding the relationship between the microstructure and the mechanical properties in terms of deformation and damage mechanisms. The proof stress of PBF-LB/M/316L is about twice that of HR/316L. This trend remains with increasing test temperature. The elongation after fracture is lower at all test temperatures. Regarding LCF, PBF-LB/M/316L exhibits higher cyclic stresses than HR/316L for most of the fatigue life, especially at room temperature. Exclusively at the smallest strain amplitudes, the fatigue lives of PBF-LB/M/316L are markedly shorter than in HR/316L. The cyclic stress-strain deformation behavior of PBF-LB/M/316L features an initial strain hardening followed by a continuous softening, which occurs until the softening leading to failure takes place. The creep rupture times and the duration of each creep stage are shorter for PBF-LB/M/316 than for HR/316L for all combinations of test parameters. The stress dependence of PBF-LB/M/316L is lower, and the creep ductility is smaller compared to HR/316L. The minimum creep rate is reached at significantly lower creep extensions for all parameter combinations tested. A heat treatment at 450 °C / 4 h did not cause significant changes in the microstructure and tensile behavior. An additional heat treatment at 900 °C / 1 h caused a decrease in the proof stress of PBF-LB/M/316L. However, it still remained higher than the one of HR/316L by a factor of 1.5x. The deformation characteristics were hardly affected. Regarding the creep behavior, this latter heat treatment at 900 °C / 1 h caused longer secondary and tertiary creep stages, and the creep strain increased significantly. The fracture characteristics generally differed, which happened not only but especially with increasing test temperature, where intergranular cracking often took place in PBF-LB/M/316L. The cellular structure is considered the main factor contributing to the different mechanical properties compared to the HR/316L variant. In addition, grain morphology, stacking fault energy, and nitrogen content might play a role. KW - AGIL KW - Additive Fertigung KW - Laser-Pulverbettschmelzen KW - Mikrostrukturentwicklung KW - 316L KW - LCF KW - Kriechen KW - Additive Manufacturing KW - Microstructure KW - Mechanical Properties KW - Mechanische Eigenschaften PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-597143 DO - https://doi.org/10.14279/depositonce-19828 SP - 1 EP - 190 CY - Berlin AN - OPUS4-59714 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Bartczack, Dorota A1 - Taché, Olivier A1 - Hodoroaba, Vasile-Dan T1 - Report on the homogeneity assessment of bimodal gold materials (nPSize1 and nPSize2) and particle number concentration by frequency method N2 - The main objective was to assess homogeneity of two bimodal gold materials, namely nPsize1 and nPSize2, containing approximately 1:1 and 10:1 particle number-based ratio of ~30nm and ~60nm particles. Particle number-based concentration within the two size fractions was determined with spICP-MS using the particle frequency method of calibration. KW - Nanoparticles KW - Homogeneity KW - Particle number concentration KW - Gold KW - nPSize PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-595451 DO - https://doi.org/10.5281/zenodo.10654245 SP - 1 EP - 5 PB - Zenodo CY - Geneva AN - OPUS4-59545 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias A1 - Grelle, Tobias A1 - Kömmling, Anja A1 - Wolff, Dietmar A1 - Völzke, Holger ED - Stuke, M. T1 - Long-term evaluation of sealing systems for radioactive waste packages N2 - The investigation of the long-term performance of sealing systems employed in containers for radioactive waste and spent nuclear fuel is one research focus area for division 3.4 “Safety of Storage Containers” at the Bundesanstalt für Materialforschung und -prüfung (BAM). Our investigations comprise investigations on metallic and elastomeric seals and covers experimental investigations to get a database on the component/material behaviour, work on analytical descriptions and numerical analysis. Our aim is to understand the long-term behaviour of the sealing systems for evaluation of their performance during possible extended interim storage and subsequent transportation. T2 - 3rd Workshop on Safety of Extended Dry Storage of Spent Nuclear Fuel CY - Garching, Germany DA - 05.06.2019 KW - Seal performance KW - Rubber seal KW - Metallic seal KW - Ageing PY - 2019 SP - 57 EP - 62 AN - OPUS4-48225 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Gesell, Stephan A1 - Fedelich, Bernard A1 - Rehmer, Birgit A1 - Uhlemann, Patrick A1 - Skrotzki, Birgit A1 - Ganesh, R. A1 - Dude, D. P. A1 - Kuna, M. A1 - Kiefer, B. T1 - TMF-Rissverlaufsberechnung für ATL-Heißteile N2 - Die Steigerung der Leistung und des thermodynamischen Wirkungsgrades von Verbrennungsmotoren führt zu erhöhten Anforderungen an die Festigkeit abgasführender Komponenten wie z. Bsp. Abgasturbolader. Als Folge erhöhter thermomechanischer Wechselbeanspruchungen (TMF) im Betrieb kommt es an den mechanisch und/oder thermisch höchst beanspruchten Stellen der Bauteile zur Bildung von Rissen, wodurch die Lebensdauer der Komponenten begrenzt wird. Derzeit werden bei Turboladern heißgehende Bauteile mit detektierten Rissen zumeist prophylaktisch ersetzt, da die weitere Ausbreitung der Risse während des Betriebs nicht vorhergesagt werden kann. Um diese aufwändige und un- ökonomische Praxis zu vermeiden, wurde im vorliegenden Forschungsvorhaben eine rechnerische Bewertungsmethode auf Basis der experimentellen und numerischen Bruchmechanik erarbeitet, mit deren Hilfe bereits in der Auslegungsphase oder während des Betriebs die (restliche) Lebensdauer der abgasführenden Komponenten vorhergesagt werden kann. Damit wird erstmalig die quantitative Vorhersage der Rissentwicklung bei TMF-Beanspruchungsbedingungen unter Berücksichtigung großer zyklischer viskoplastischer Verformungen ermöglicht. Zentrales Ergebnis des Vorhabens ist eine automatisierte Berechnungsprozedur auf der Basis spezieller Finite-Elemente-Techniken (FEM), womit sowohl der Pfad als auch die Größe eines Risses als Funktion der Anzahl der Lastwechsel in Bauteilen unter TMF-Bedingungen berechnet werden kann. Als geeigneter Beanspruchungsparameter zur Bewertung des Rissfortschritts unter TMF wurde die zyklische Rissöffnungsverschiebung ΔCTOD verwendet. Das Werkstoffverhalten des betrachteten austenitischen Gusseisens Ni-Resist D-5S wurde mit einem validierten viskoplastischen, temperaturabhängigen Materialmodell modelliert, das zur Berücksichtigung große Verzerrungen und Rotationen am Riss erweitert wurde. Für die genaue Berechnung des ΔCTOD bei TMF wurden effiziente FEM-Techniken erarbeitet. Zur Simulation der Rissausbreitung wurde ein automatischer FEM-Algorithmus mit inkrementeller adaptiver Neuvernetzung entwickelt, bei dem die Verformungen und inelastischen Zustandsvariablen jeweils vom alten auf das neue Netz übertragen werden. Dieser Algorithmus wurde im Software-Paket ProCrackPlast implementiert, das in Verbindung mit dem kommerziellen FEM-Code Abaqus zur Lösung dreidimensionaler Rissprobleme zur Verfügung steht. Ziel der umfangreichen experimentellen Arbeiten war es, an isothermen LCF und anisothermen TMF-Versuchen mit gekerbten Flachzugproben (SENT) das Risswachstum im Temperaturbereich von 20 °C bis 700 °C zu ermitteln. Mit Hilfe begleitender 2D FEM Simulationen wurden anhand dieser Datenbasis die Rissfortschrittskurven des Werkstoffs unter Anwendung des ΔCTOD-Konzepts bestimmt und in geeigneter, parametrisierter Form den Nutzern zur Verfügung gestellt. Die Versuche an SENT-Proben wurden mit der entwickelten Software ProCrackPlast als 3D Modell simuliert. Der Vergleich der 2D und 3D Simulationen ergab einen systematischen Unterschied im CTOD und CTOD, der mit Hilfe eines Übertragungsfaktors korrigiert wurde. Der Vergleich der 3D Berechnungen mit den Experimenten zeigte eine zufriedenstellende Übereinstimmung der er- reichten Risslänge mit der Zahl der Lastzyklen im gesamten Temperaturbereich, wobei die numerische Prognose meist auf der konservativen / sicheren Seite lag. Die Übertragbarkeit der Ergebnisse der 2D Parameteridentifikation auf 3D Risskonfigurationen mit Mixed-Mode Beanspruchung ist mit zusätzlichen Versagenshypothesen verbunden, die aufgrund fehlender Versuchsdaten im Vorhaben nicht endgültig geklärt werden konnten. Zur Validierung des Gesamtkonzeptes wurden LCF-Proben mit einem bauteil- typischen Oberflächenriss experimentell und numerisch untersucht. In der Simulation konnte die komplexe Form und Größe der Rissentwicklung zufriedenstellend (richtig) vorhergesagt werden. Die Leis- tungsfähigkeit der erarbeiteten rechnerische Bewertungsmethode wurde an weiteren TMF-Beispielen vorgestellt und diskutiert. Die Software ProCrackPlast und die viskoplastische Materialroutine wurden dem Anwenderkreis des Vorhabens zusammen mit einem Nutzer-Handbuch und Verifikationsbeispielen zur Verfügung gestellt. Das Ziel des Forschungsvorhabens ist erreicht worden. KW - Abgasturbolader Heißteile KW - Numerische Simulation KW - Rissverlauf PY - 2023 VL - 1320 SP - 1 EP - 137 PB - Forschungsvereinigung Verbrennungskraftmaschinen (FVV) CY - Frankfurt am Main AN - OPUS4-56960 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Grelle, Tobias A1 - Wolff, Dietmar A1 - Probst, Ulrich A1 - Jaunich, Matthias A1 - Völzke, Holger T1 - Component and material investigations on metal seals for high level radioactive waste containers N2 - Long-term investigations performed at BAM look to extend the state of knowledge on safety-related components of interim storage containers. Metal seals act as the primary sealing barrier in the bolted double lid closure system of the containers. The behaviour of metal seals has been investigated for ageing times up to 8.5 years and for various temperatures. The main cause for reduction in useable resilience overtime was due to creep deformation of the outer jacket of the seal. KW - Metal seal KW - Radioactive waste containers KW - Creep KW - Long-term behaviour PY - 2018 SN - 1745-2058 SP - 32 EP - 34 PB - Nuclear Institute CY - London AN - OPUS4-48206 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ávila Calderón, Luis A1 - Han, Ying A1 - Matzak, Kathrin A1 - Olbricht, Jürgen A1 - Skrotzki, Birgit T1 - NFDI-MatWerk/IUC02 data schema for elevated temperature tensile data of Ni-based superalloys N2 - Strength characteristics, such as proof strength and tensile strength, of metallic materials are usually measured at room temperature. However, for high-temperature materials, the values at operational temperatures are equally important for analyzing the mechanical behavior of components or for designing purposes. Elevated temperature tensile tests (often referred to as hot tensile tests) generally enable the measurement of the same material parameters as those obtained at room temperature. Typically, tensile and proof strength, elongation after fracture, and reduction of area are analyzed, with the focus often being on proof strength. The attached data schema for elevated temperature tensile tests was developed within the German NFDI-MatWerk initiative (https://nfdi-matwerk.de/). It builds on a previously published creep data schema and follows a reference data methodology that has also been previously outlined. The presented schema constitutes a structured approach for collecting all relevant information on an elevated temperature tensile test experiment. Overall, this development, as defined in the previously published data schema for creep data, aims to provide a comprehensive hierarchical data description that can be implemented in data management platforms (such as electronic laboratory notebooks), facilitate consistent quality assessment across different users and data providers, and promote the alignment of datasets to the FAIR principles by providing easy interoperability and full reusability. The presented schema was initially developed for datasets of Ni-based high-temperature alloys. However, thanks to its modular structure, it can also be applied to tensile tests of various metallic and other materials. Although the focus is on elevated temperature tensile testing, the data schema also offers a solid foundation for documenting room temperature tensile tests. In such cases, an adjustment of the requirement profile might be necessary, and categories or entries specific to mechanical testing at elevated temperatures, such as “temperature-measuring system”, “specified temperature”, or “soaking time”, become irrelevant. Overall, a detailed approach was followed to ensure the collection of all relevant information, including both metadata and test results. This includes, for example, comprehensive descriptions of the material’s manufacturing history and of the laboratory equipment, and basic strength and deformation characteristic values. The resulting data schema aims to support the description and identification of high-quality datasets, which may qualify as reference data of materials. Our current definition of reference data of materials has been published elsewhere. It should be noted, however, that not all research datasets —depending on their origin and purpose— require this full level of detail. Nevertheless, the presented data schema can support data providers in evaluating the completeness and value of their datasets. This version of the data schema covers elevated temperature tensile tests on both single- and polycrystalline specimen materials. The terminology is aligned with DIN EN ISO 6892-1 and DIN EN ISO 6892-2. It is designed to record the use of temperature measurement using thermocouples and the use of contacting extensometer systems. The requirement profile refers to the highest quality class of reference data, taken from calibrated instruments, and which shall enable the following usages: 1. Checking one's own elevated temperature tensile test results on nominally similar material 2. Verification of own testing set-up (e.g., by testing the same or a similar material) 3. Using the data as input data for simulations in the context of design or alloy development KW - NFDI MatWerk KW - Referenzdaten KW - Zugversuch KW - CMSX-6 KW - Datenschema KW - NFDI MatWerk KW - CMSX-6 KW - Data schema KW - Reference data KW - Tensile test PY - 2025 UR - https://doi.org/10.5281/zenodo.17846436 DO - https://doi.org/10.5281/zenodo.17846435 PB - Zenodo CY - Geneva AN - OPUS4-65190 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hansen, B. A1 - Hodoroaba, Vasile-Dan T1 - Analysis of a certified copper alloy with Micro-XRF on SEM N2 - Copper alloys have found widespread application in various fields. The elemental composition determines the properties of the alloys and consequently their application. Therefore, knowing the composition of a copper alloy is very important. Metrological institutes like the BAM (German Federal Institute for Materials Research and Testing) offer reference materials that can be used to prove the accuracy of the applied analysis method. The aim of this application note is to demonstrate how Micro-X-ray fluorescence spectroscopy (Micro-XRF) expediently supplements the analysis of copper alloys by using Bruker’s micro-focus X-ray source XTrace attached to a scanning electron microscope (SEM) and operating with an energy dispersive spectrometer. KW - XRF KW - µ-XRF KW - SEM/EDX KW - Copper alloy PY - 2018 UR - https://www.bruker.com/fileadmin/user_upload/8-PDF-Docs/X-rayDiffraction_ElementalAnalysis/Microanalysis_EBSD/LabReports/App_mxrf_sem_03_analysis_Cu_alloy_lores.pdf SP - 1 EP - 4 PB - Bruker Nano GmbH CY - Berlin AN - OPUS4-44677 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Terborg, R. A1 - Hodoroaba, Vasile-Dan T1 - Analysis of the elemental composition and thickness of a Fe-Ni film on Si using Bruker ESPRIT and SAMx STRATAGem N2 - Quantitative analysis of a bulk sample requires that the composition of the sample is homogeneous over the analyzed volume. For inhomogenous samples the calculation of the matrix effects is not correct and this can lead to wrong results in the element concentrations. For samples containing a layer structure a different quantitative evaluation has to be applied. This can be provided with the standard-based analysis in ESPRIT in combination with the STRATAGem software. KW - Thin film analysis KW - SEM/EDX KW - EPMA KW - k-values PY - 2018 UR - https://www.bruker.com/products/x-ray-diffraction-and-elemental-analysis/eds-wds-ebsd-sem-micro-xrf-and-sem-micro-ct/quantax-eds-for-sem/applications/layer-analysis.html SP - 1 EP - 4 CY - Berlin AN - OPUS4-44594 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hodoroaba, Vasile-Dan A1 - Hoffmann, V. A1 - Steers, E. B. M. T1 - Exploitation of the hydrogen effect on an analytical glow discharge T2 - Final General Meeting of the EU-GDS Network CY - Wiener Neustadt, Austria DA - 2002-03-02 PY - 2002 SP - 1(?) EP - 6(?) AN - OPUS4-1467 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rockenhäuser, Christian A1 - von Hartrott, P. A1 - Metzger, M. A1 - Schriever, Sina A1 - Augenstein, E. A1 - Karlin, J. A1 - Piesker, Benjamin A1 - Schweizer, Ch. A1 - Skrotzki, Birgit T1 - Lebensdauerberechnung von Aluminium-Radialverdichterrädern unter Berücksichtigung der Werkstoffalterung N2 - In this project, a procedure was developed to improve the lifetime assessment precision of exhaust turbo charger radial compressor wheels made from the age hardenable aluminum alloy EN AW-2618A. This comprises particularly the consideration of material aging, which has to be anticipated during operation of such components under relevant service conditions (temperature, time, stress). First of all, a solid experimental database was established for the investigated material. This includes a mechanical as well as a microstructural characterization of the as-received state (T61) and after aging up to 25,000 h at relevant service temperatures (160 °C, 180 °C, 190 °C). The microstructural investigations focused on the development of the radii of the cylindrical hardening phase, which coarsens during aging. The relation between aging temperature, time and mechanical load (if applicable) was established for the first time to this extent. An interrelationship to describe the coarsening was established. The effect of aging on hardness, strength, creep behavior and fatigue lifetime (LCF, TMF) was studied and a correlation to the microstructure was established. The results of the creep tests were used to calibrate a modified hyperbolic sine creep model. A time and temperature dependent deformation model according to Chaboche, which describes the relevant phenomena of high temperature deformation and cyclic plasticity, was extended. It now considers material aging by describing the strength not only as a function of temperature but also as a function of aging, i.e. of the mean radius of the precipitates. A similar procedure was applied to extend the model in order to assess the fatigue lifetime. The calculated lifetimes of LCF and TMF tests completed during this project match well with the experimental results. Only one LCF test with a hold time of 900 s in tension deviates clearly from the mean value and shows the limits of the time independent damage model. Tests with shorter hold times of 60 s are within the scatter band, likewise the different aging conditions. A damage accumulation model additionally describing the progressive aging during lifetime was developed and implemented. Besides considering aging in the deformation and lifetime assessment, it is also possible to judge complex loading cycles in a postprocessing by rain flow classification of typical complex loading cycles. The methodology and the models were implemented into the Finite-Element software Abaqus and Ansys and are available for numerical assessment of components. N2 - In diesem Forschungsvorhaben wurde ein Verfahren entwickelt, um die Genauigkeit der Lebensdauerbewertung für Abgasturbolader (ATL)-Verdichterräder aus der ausscheidungs-härtbaren Aluminiumlegierung EN AW-2618A zu verbessern. Dies umfasst insbesondere die Berücksichtigung der Werkstoffalterung, mit der beim Einsatz dieser Bauteile unter entsprechender Betriebsbeanspruchung (Temperatur, Zeit, Spannung) gerechnet werden muss. Zunächst wurde eine solide experimentelle Datenbasis für den untersuchten Werkstoff geschaffen. Dies umfasste sowohl eine mechanische als auch eine mikrostrukturelle Charakterisierung des Ausgangszustands (T61) sowie von ausgelagerten Zuständen bis zu 25.000 h bei betriebsrelevanten Temperaturen (160 °C, 180 °C, 190 °C). Bei den Untersuchungen zur Mikrostruktur wurde der Fokus auf die Entwicklung der Radien der stäbchen-förmigen aushärtenden Phase gelegt, die während der Alterung vergröbern. Der Zusammenhang zwischen Auslagerungstemperatur, -zeit und ggfs. mechanischer Belastung wurde erstmals in diesem Umfang quantifiziert und entsprechende Gesetzmäßigkeiten zur Beschreibung der Vergröberung ermittelt. Vergleichend dazu wurde der Einfluss der Alterung auf die Härte, die Festigkeit, das Kriechverhalten und die Ermüdungslebensdauer (LCF, TMF) bestimmt, so dass eine Korrelation zur Mikrostruktur vorliegt. Die Ergebnisse der Kriechversuche wurden zur Kalibrierung eines modifizierten Sinus-hyperbolicus-Kriechmodells verwendet. Ein zeit- und temperaturabhängiges Verformungsmodell nach Chaboche, welches die wesentlichen Phänomene der Hochtemperaturverformung und der Wechselplastizität beschreibt, wurde erweitert und berücksichtigt nun die Werkstoffalterung, indem die Festigkeit nicht nur als Funktion der Temperatur, sondern auch des Alterungszustands (d. h. des mittleren Radius der Ausscheidungen) dargestellt wird. Für die Erweiterung des Modells zur Bewertung der Ermüdungslebensdauer wurde analog verfahren. Die berechnete Lebensdauer der im Verlauf des Vorhabens durchgeführten LCF- und TMF-Versuche stimmt gut mit den experimentellen Ergebnissen überein. Lediglich ein LCF-Versuch mit einer Haltezeit von 900 s im Zug weicht deutlich vom Mittelwert ab und zeigt die Grenzen des zeitunabhängigen Schädigungsmodells auf. Versuche mit kürzeren Haltezeiten bis zu 60 s liegen im Streuband, ebenso die verschiedenen Alterungszustände. Eine Schädigungsakkumulation unter Berücksichtigung der fortschreitenden Alterung über der Lebensdauer wurde entwickelt und implementiert. Neben der Berücksichtigung der Alterung in der Verformungs- und Lebensdaueranalyse besteht auch die Möglichkeit, komplexe Belastungszyklen in einem Postprozessing zu bewerten, indem Rainflow-Klassierungen typischer komplexer Belastungszyklen vorgenommen werden. Die Methodik und die Modelle wurden in die Finite-Elemente-Programme Abaqus und Ansys implementiert und stehen für die rechnerische Bewertung von Bauteilen zur Verfügung. T2 - FVV Frühjahrstagung 2018 CY - Bad Neuenahr, Germany DA - 22.03.2018 KW - Aluminium KW - Centrifugal compressor wheel KW - Dark-field transmission electron microscopy (DFTEM) KW - Degradation KW - S-phase PY - 2018 SP - 97 EP - 130 AN - OPUS4-44604 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schilling, Markus A1 - Skrotzki, Birgit T1 - Full dataset of several mechanical tests on an S355 steel sheet as reference data for digital representations N2 - The dataset provided in this repository comprises data obtained from a series of characterization tests performed to a sheet of typical S355 (material number: 1.0577) structural steel (designation of steel according to DIN EN 10025-2:2019). The tests include methods for the determination of mechanical properties such as, e.g., tensile test, Charpy test and sonic resonance test. This dataset is intended to be extended by the inclusion of data obtained from further test methods. Therefore, the entire dataset (concept DOI) comprises several parts (versions), each of which is addressed by a unique version DOI. The data were generated in the frame of the digitization project Innovationplatform MaterialDigital (PMD) which, amongst other activities, aims to store data in a semantically and machine understandable way. Therefore, data structuring and data formats are focused in addition to aspects in the field of material science and engineering (MSE). Hence, this data is supposed to provide reference data as basis for experimental data inclusion, conversion and structuring (data management and processing) that leads to semantical expressivity as well as for MSE experts being generally interested in the material properties and knowledge. KW - S355 steel sheet KW - Mechanical testing KW - Tensile test KW - Charpy test KW - Microstructure analysis KW - Digital representation KW - Data management KW - Data format PY - 2022 DO - https://doi.org/10.5281/zenodo.6778336 PB - Zenodo CY - Geneva AN - OPUS4-55141 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Jentzsch, Stefan A1 - Stock, Daniel A1 - Häcker, Ralf A1 - Skrotzki, Birgit A1 - Darvishi Kamachali, Reza A1 - Klingbeil, Dietmar A1 - Kindrachuk, Vitaliy T1 - Split Hopkinson Pressure Bar (SHPB) investigations of steel S355 specimens and complementary characterization methods N2 - The workbook SHPB_S355.xlsx contains in the main spreadsheet S355_TestOverview an overview on the S355 specimens, which were tested in Split Hopkinson Pressure Bar (SHPB) and complementary quasi-static (QS) tests. The tests were conducted with notched hat-shaped specimens without a notch offset (S355_TestOverview/column geometry: “no offset”) and a small notch offset of x=0.35 mm (S355_TestOverview/column geometry: “offset”), cf. Fig. 1 [1]. Furthermore, for selected specimens, links are provided to DIC and bar strain measurement files as well as to evaluations from further characterization methods (microhardness, EBSD). For the boundary conditions at the SHPB projectile impact, the pressures of the compressor p, driving the projectile, and the associated projectile impact velocities are provided in SHPB_S355.xlsx. The DIC displacement measurements are provided in FurtherMeasurements/DIC with frame output times in the file labels, which are associated with an imaginary trigger at the left end of the shortened incident bar (length 300 mm), which is considered within the SHPB simulation setup, see [1]. Furthermore, the DIC reference coordinate systems are provided as COS.jpg files in the respective DIC folders. Starting from the strain signals at the bars, captured by strain gauges at the incident (file name BC_Inc) and transmission bar (BC_Trans), displacement boundary conditions (which are provided for the tests in FurtherMeasurements/BarDisplBCs) are calculated by eq. (12) in [1], incorporating the acoustic velocity equal to 4639 m/s at the bars and a correction factor. Fig. 1 shows the shear specimen geometry (lengths in mm) with the offset of the notches x. For the quasi-static tests force(displacements)-values are directly provided in FurtherMeasurements/Fu_curves, which are considered from the relative displacements of the specimens, evaluated by DIC. The Vickers microhardness (HV 0.01) distribution across the shear localization zone was assessed by QNESS 60A+ EVO (DIN EN ISO 6507-1) for quasi-statically and dynamically tested specimens, applying the small notch offset, such that the specimens did not fail in the localization region. Therefore, raw data is provided in FurtherMeasurements/Microhardness. For fitting the microhardness distribution perpendicularly to the shear bands (as i.e. provided for the SHPB specimen in [1]), representative microhardness profiles were considered. Similarly for specimens with the small notch offset, EBSD data on dynamic and quasi-static tests is provided in FurtherMeasurements/EBSD. The grain size distributions for positions at the notch and the undeformed region are included in the subdirectory ./GrainLists_Shortened and EBSD images in the PowerPoint Presentations. Further information as the sizes and misorientations of the single grains, is incorporated in the subfolders ./GrainLists_FurtherInf. KW - Adiabatic shear bands KW - Split Hopkinson pressure bar KW - Digital image correlation PY - 2025 DO - https://doi.org/10.5281/zenodo.17591439 PB - Zenodo CY - Geneva AN - OPUS4-64842 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Uckert, Danilo A1 - Matzak, Kathrin A1 - Kühn, Hans-Joachim A1 - Rehmer, Birgit A1 - Peter, Frauke A1 - Fedelich, Bernard A1 - Falkenberg, Rainer A1 - Haftaoglu, Cetin A1 - Kindrachuk, Vitaliy A1 - Skrotzki, Birgit T1 - TMF-Lebensdauerberechnung ATL-Heißteile II - Erweiterung bestehender Werkstoff- und Rechenmodelle zur Lebensdauervorhersage für Abgasturbolader-Heißteile unter thermomechanischer Ermüdungsbeanspruchung (Abschlussbericht) N2 - In diesem Forschungsvorhaben erfolgte eine Überprüfung der Übertragbarkeit der Werkstoff- und Rechenmodelle für die Lebensdauervorhersage von ATL-Heißteilen unter TMF-Beanspruchung auf eine andere Werkstoffklasse als im Vorgängervorhaben, d.h. auf das austenitische Gusseisen EN-GJSA-XNiSiCr35-5-2 (Ni-Resist D-5S). Zunächst wurde dafür eine experimentelle Datenbasis geschaffen, da diese vor Beginn des Vorhabens nicht ausreichend war. Dazu wurden Zug-, Kriech-, LCF- und TMF-Versuche durchgeführt, die der Kalibrierung der Modelle dienten. Das Spannungs-Verformungs-Verhalten und die Lebensdauer in den LCF- und TMF-Versuchen werden durch das Modell auch für den neuen Werkstoff überwiegend gut beschrieben. LCF-Versuche mit Haltezeit bei 900 °C sowie IP-TMFVersuche mit einer Obertemperatur von 900 °C werden weniger gut vorhergesagt, da sich der Schädigungsmechanismus ändert. Eine Verifikation des Modells erfolgte mit Hilfe eines Bauteilversuchs an einem Abgassammler. Die überwiegende Anzahl der experimentell ermittelten Rissorte wurden von dem Modell vorhergesagt. Ein wesentliches Ziel des Vorhabens war, den Einfluss von HCF-Schwingungen auf die TMF-Lebensdauer vertieft experimentell zu untersuchen und das bereits bestehende Lebensdauermodell auf HCF-Überlagerung zu erweitern. Es wurde ein bruchmechanisch motivierter Ansatz entwickelt, in dem die Lebensdauerminderung durch die im TMF-Zyklus überlagerten HCF-Schwingungen abgebildet wird. Mit diesem Ansatz lassen sich die Lebensdauern sowohl für den Werkstoff SiMo 4.05 als auch für den Ni-Resist in guter Übereinstimmung mit dem Experiment Vorhersagen. Das Ziel des Forschungsvorhabens ist erreicht worden. PY - 2015 IS - 1082 SP - 1 EP - 168 CY - Frankfurt/Main AN - OPUS4-35112 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Skrotzki, Birgit A1 - Schriever, Sina T1 - BAM reference data - Results of ASTM E139-11 creep tests on a reference material of Nimonic 75 nickel-base alloy N2 - Results of creep tests on a certified reference material at T = 600°C and a tensile creep load of 160 MPa are provided. The evaluated results include the times to reach 2% and 4% creep strain, respectively, and the creep rate after 400 h. The data were audited and are BAM reference data. KW - Reference data KW - Creep KW - Nickel-base alloy KW - Nimonic 75 KW - Reference material BCR-425 PY - 2021 DO - https://doi.org/10.5281/zenodo.5106606 PB - Zenodo CY - Geneva AN - OPUS4-52970 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kling e Silva, Lucas A1 - Pereira, Gabriela Ribeiro A1 - Jardim, Paula Mendes A1 - Sonntag, Nadja A1 - Skrotzki, Birgit T1 - CARACTERIZAÇÃO MAGNÉTICA DOS EFEITOS DE DEFORMAÇÃO EM AÇOS ESTRUTURAIS ATRAVÉS DA TÉCNICA BITTER MODIFICADA N2 - The plastic deformation results in irreversible microstructure changes in the steel, which can be considered as the initial stage of the fracture process. However, detecting, monitoring and evaluating, damage states and small defects non-destructively in advance still proves challenging. It was reported in literature the phenomenon of the spontaneous emergence of weak magnetic fields in structural steels and pipelines, which originates due to heterogeneous mechanical and / or thermal stresses. This observation is not associated with induced phase transformations by deformation and appears to be a promising tool for the prior characterization of damage in ferromagnetic steels. To provide a better understanding of the physical bases of the process, the magnetic microstructure of such materials and the change of magnetic domains after undergoing plastic deformation were studied. For this purpose, a colloidal solution with paramagnetic particles in the nanometer scale (ferrofluid) was used, through the Bitter technique, in order to, not only observe a change in size of the magnetic domains of the material, but also changes in their morphology. Ferritic steels with different carbon contents (0.08%; 0.22% and 0.45%) were studied in this work. T2 - ABM Week 2017 CY - Sao Paulo, Brazil DA - 02.10.2017 KW - Magnetic domains KW - Steels KW - Ferrofluid KW - Plastic deformation PY - 2017 DO - https://doi.org/10.5151/1516-392X-30810 SN - 2594-5327 VL - 72 IS - 1 SP - 3003 EP - 3013 PB - Blucher Preceeding CY - Brasilien AN - OPUS4-48876 LA - por AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Beygi Nasrabadi, Hossein A1 - Skrotzki, Birgit T1 - Tensile test ontology (TTO) N2 - Tensile Test Ontology (TTO) has developed for representing the Tensile testing process, testing equipment requirements, test pieces charactristics, and related testing parameters and their measurement procedure according to DIN EN ISO 6892-1 standard. Versions info: V2 developed using BFO+CCO top-level ontologies. V3 developed using PROVO+PMDco top-level ontologies. Repositories: GitLab: https://gitlab.com/kupferdigital/process-graphs/tensile-test GitHub: https://github.com/HosseinBeygiNasrabadi/Tensile-Test-Ontology-TTO- MatPortal: https://matportal.org/ontologies/TTO IndustryPortal: https://industryportal.enit.fr/ontologies/TTO KW - Ontology KW - Tensile testing PY - 2024 UR - https://gitlab.com/kupferdigital/process-graphs/tensile-test UR - https://github.com/HosseinBeygiNasrabadi/Tensile-Test-Ontology-TTO- UR - https://matportal.org/ontologies/TTO UR - https://industryportal.enit.fr/ontologies/TTO PB - GitLab CY - San Francisco, CA, USA AN - OPUS4-60545 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, I. A1 - Moll, J. A1 - Kexel, C. A1 - Schubert, L. A1 - Tschöke, K. A1 - Prager, Jens A1 - Lugovtsova, Yevgeniya A1 - Bach, M. A1 - Vogt, T. T1 - SHM using Guided Waves – Recent Activities and Advances in Germany N2 - Issues that prevent Structural Health Monitoring (SHM) based on Guided Waves (GW) from being a part of today’s monitoring solutions in industry are not all obvious to the scientific community. To uncover and overcome these issues, scientists working on SHM and GW problems joined in an expert committee under the patronage of the German Society for Non-Destructive Testing. An initiated online survey among more than 700 experts and users reveals the hurdles hindering the practical application of GWbased SHM. Firstly, methods for proof of reliability of SHM approaches are missing. Secondly, detailed understanding of phenomenological described wave-damage interactions is needed. Additionally, there are significant unsolved implementation issues and unsolved problems of signal processing including handling of environmental influences. To enable substantial proof of reliability without unaffordable experimental effort also efficient simulation tools including realistic damage interaction are needed, enabling the joint use of experimental and simulated data to predict the capabilities of the Monitoring system. Considering these issues, the committee focusses on simulation, signal processing, as well as probability of detection and standardization. In the presented work, recent activities of the expert committee starting with survey results are summarized. An open access data basis of life-like measurements is presented to allow testing and comparison of signal processing and simulation algorithms. Finally, a strategy for efficient proof of reliability increasing the acceptance of SHM in industry and for successful Integration of SHM into real-world engineering structures is proposed. T2 - The 12th International Workshop on Structural Health Monitoring (IWSHM) CY - Stanford, California, USA DA - 10.09.2019 KW - Structural Health Monitoring KW - Ultrasonic Guided Waves KW - Non-Destructive Testing KW - Survey KW - Probability of Detection KW - Reliability PY - 2019 SP - 1 EP - 10 AN - OPUS4-49232 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Knigge, Xenia A1 - Radnik, Jörg T1 - Physico-chemical characterization of sterile Fe3O4 nanoparticles by XPS / HAXPES / SEM N2 - Here a dataset of XPS, HAXPES and SEM measurements for the physico-chemical characterization of sterile Fe3O4 nanoparticles is presented. The measurements are part of the H2020 project “NanoSolveIT”. KW - HAXPES KW - XPS KW - SEM KW - Fe3O4 KW - Nanoparticles PY - 2023 DO - https://doi.org/10.5281/zenodo.7990301 PB - Zenodo CY - Geneva AN - OPUS4-57764 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Radnik, Jörg T1 - BAM reference data - XPS raw data of Al-coated titania nanoparticles (JRCNM62001a and JRCNM62002a) N2 - XPS raw data of Al-coated titania nanoparticles (JRCNM62001 and JRCNM62002a) provided by the JRC repository are provided. KW - XPS KW - Titania nanoparticles KW - BAM reference data PY - 2021 DO - https://doi.org/10.5281/zenodo.4986068 PB - Zenodo CY - Geneva AN - OPUS4-52880 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Algernon, D. A1 - Arndt, R.W. A1 - Denzel, W. A1 - Ebsen, B. A1 - Feistkorn, S. A1 - Friese, M. A1 - Große, C.U. A1 - Kathage, S. A1 - Keßler, S. A1 - Köpp, Christian A1 - Küttenbaum, Stefan A1 - Lohse, C. A1 - Maack, Stefan A1 - Niederleithinger, Ernst A1 - Schickert, M. A1 - Schröder, G. A1 - Taffe, A. A1 - Timofeev, Juri A1 - Walther, A. A1 - Wilcke, M. A1 - Wolf, J. A1 - Wöstmann, Jens T1 - Test specimen concepts in regard to quality assurance and validation of nondestructive testing in civil engineering N2 - The process of ensuring reliability of NDT applications contains various aspects, such as determining the performance and probability of success, the uncertainty in measurement, the provision of clear and functional procedures and ensuring the correct application accordingly. Test specimens have become powerful elements in supporting many of these aspects. Within the committee for NDT in Civil Engineering (NDT-CE) of the German Society for Nondestructive Testing (DGZfP), the subcommittee on Quality Assurance (UA-QS) therefore addresses the design and the integration of test specimens in the quality assurance process. Depending on the specific purpose, the requirements on test specimens can vary significantly based on the defined simulated scenario. The most prominent purposes of test specimens might be seen in providing references for inspection systems in regard to function control, calibration and validation. Further aspects can be parametric studies, basic investigation of physical principles related to NDT or a simplified and therefore comprehensive demonstration of inspection concepts (e.g. for teaching purposes). The specific purpose of a test specimen dictates the requirements regarding its conception, including the exact design, the material or the fabrication accuracy and the conditioning. In the development of a general guideline by the UA-QS for application-specific procedures and their validation, the use of test specimens is addressed and specific concepts for the design of test specimens are made. This includes the analysis of the measurement process regarding any given application, deriving an adequate calibration approach for it and designing test specimens (calibration specimens) accordingly. Furthermore, it includes the validation of the procedure taking into account all conditions related to the specific application in the field. The validation requires a statistically sufficient number of trials. Thorough evaluation of each trial can only be established if the ground-truth is known. Therefore, test specimens providing a realistic but controlled simulation of the inspection problem are valuable and indispensable elements in the validation process. The requirement of being fully realistic will often not be possible to fulfill due to practical restrictions. Any aspect that cannot be included in the simulation realistically needs to be simulated conservatively. This again, requires a sufficient understanding of the inspection principle and technique to ensure conservativeness. Among other quality-assurance-related aspects, the UA-QS establishes concepts and guidelines regarding sound and efficient approaches for the specific purposes of test specimens. This subcommittee brings together representatives of different Groups along the entire value chain of NDT-CE, including researchers, practitioners, manufacturers and clients. They all work together in establishing a common understanding and level of quality assurance in the industry. T2 - SMT and NDT-CE 2018 CY - New Brunswick, NJ, USA DA - 27.08.2018 KW - Quality assurance KW - Procedure KW - Reliability KW - Validation KW - Reference specimen PY - 2019 UR - https://asnt.org/smt18papers SN - 978-1-57117-456-7 VL - 11/19 SP - 39 EP - 48 PB - The American Society for Nondestructive Testing, Inc. CY - Columbus, OH, USA AN - OPUS4-47240 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Algernon, D. A1 - Arndt, R.W. A1 - Denzel, W. A1 - Ebsen, B. A1 - Feistkorn, S. A1 - Friese, M. A1 - Große, C.U. A1 - Kathage, S. A1 - Keßler, S. A1 - Köpp, Christian A1 - Küttenbaum, Stefan A1 - Lohse, C. A1 - Maack, Stefan A1 - Niederleithinger, Ernst A1 - Schickert, M. A1 - Schröder, G. A1 - Taffe, A. A1 - Timofeev, Juri A1 - Walther, A. A1 - Wilcke, M. A1 - Wolf, J. A1 - Wöstmann, Jens T1 - NDT procedures in relation to quality assurance and validation of nondestructive testing in civil engineering N2 - The field of non-destructive testing of civil structures (NDT-CE) has been continuously growing. Due to the complexity and diversity of civil constructions as well as the heterogeneity of concrete, specific standards or guidelines for the application of modern NDT-CE are still missing. The development of individual solutions is the current approach, which is just as challenging as it is common for NDT-CE. With the increasing development and commercialization of NDT-CE technology, the group of practitioners is growing. To ensure a good level of quality in the industry, it appears necessary to establish adequate means. Naturally, the performance of NDT-CE methods regarding a specific application is strongly dependent on choosing the most suitable inspection technique and applying it correctly, generally referred to as the inspection procedure in the field of NDT. There are well-defined guidelines regarding procedure documentation and handling in many fields of NDT (e.g. nuclear, aerospace or automotive) according to the high importance of procedures in assuring a successful and reliable application. For a long time, this has not always been the case with NDT-CE, which is still considered a unique discipline of NDT. Part of the reason for that might be the young development state of NDTCE, the heterogeneity of building materials like concrete, timber or masonry as a material and the diversity of civil structures. In consequence, NDT-CE procedure development is considered challenging. Among other aspects, addressed in the subcommittee on Quality Assurance (UA-QS) within the committee for NDT-CE of the German Society for Nondestructive Testing (DGZfP), part of its work aims at establishing an adequate basis for NDT-CE procedure development. While some of the highly developed approaches from other industries are taken into consideration, they need to be analyzed regarding their suitability for NDT-CE and adapted accordingly. For a procedure to be as defined as possible, it needs to contain sufficient information, such as the scope and limitations regarding material, geometry and condition of the test object, inspection parameters, calibration, data acquisition, analysis criteria as well as requirements regarding the inspection personnel. For a successful implementation in the field, it is important to define the specific procedure as precisely as possible. Despite the necessity of a great amount of information to be included, the procedure needs to be suitable for efficient field application. The UA-QS is developing a guideline for NDT-CE procedures suitable for application in this field of NDT to ensure correct and reproducible application. To demonstrate and evaluate this concept, specific examples of procedures are also produced. In particular, the UA-QS has developed a procedure for the detection and positioning of tendon ducts using Ground Penetrating Radar (GPR). This procedure is tested regarding the practical applicability in a roundrobin on a defined type of reference test block. T2 - SMT and NDT-CE 2018 CY - New Brunswick, NJ, USA DA - 27.08.2018 KW - Quality assurance KW - Procedure KW - Reliability KW - Validation KW - Reference specimen PY - 2019 UR - https://asnt.org/smt18papers SN - 978-1-57117-456-7 VL - 11/19 SP - 31 EP - 38 PB - The American Society for Nondestructive Testing, Inc. CY - Columbus, OH, USA AN - OPUS4-47239 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niederleithinger, Ernst A1 - Wiggenhauser, Herbert T1 - The LAUS: First Applications of a New System for Ultrasonic Imaging of Very Concrete Structures N2 - The LAUS (Large Aperture Ultrasonic System) has been developed to image very thick concrete structures, which are not accessible for commercial systems. The device and the corresponding software is the result of joint Research of BAM, an ultrasonic instrument manufacturer and University of Kassel, Germany. It consists of 12 separate Arrays of 32 point-contact shear wave transducers each, which can be deployed in flexible configurations. Each array is combined with battery and transmitter, receiver and wireless communication electronics. Three case histories are presented. First the system was deployed on a 5-m thick heavily reinforced foundation slab. The reflection of the slab’s bottom was imaged clearly. In addition, a multiple reflection was registered, thus giving hope that even thicker elements might be imaged by the instrument. Second, the LAUS was used to investigate a massive bridge girder where a heavy rainstorm during concreting had led to imperfections that were visible after removing the formwork was removed. The LAUS could image tendon ducts in 1.8m depth and the backwall closely behind them. Some limited areas showed blurred reflections and were checked by drill holes; these areas were affected by diffuse damage which could be repaired by injections. Third, a large retaining wall was checked for thickness. Meanwhile, the LAUS has been used in underground waste deposits (nuclear and other) for quality assurance of sealing plugs. A confirmed penetration depth of about 7 m has been reached. T2 - SMT and NDT-CE 2018 CY - New Brunswick, NJ, USA DA - 27.08.2018 KW - LAUS (Large Apertur Ultrasonic System) KW - Ultrasonic echo KW - Deep penetration KW - Concrete PY - 2019 UR - https://asnt.org/smt18papers SN - 978-1-57117-456-7 VL - 11/19 SP - 208 EP - 213 PB - The American Society for Nondestructive Testing, Inc. CY - Columbus, OH, USA AN - OPUS4-47238 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bulling, Jannis A1 - Prager, Jens T1 - Bestimmung der Rissgeometrie bei der zerstörungsfreien Ultraschallprüfung mit geführten Wellen N2 - In der zerstörungsfreien Prüfung werden in zunehmendem Maße geführte Ultraschallwellen zur Lokalisation von Fehlstellen genutzt. Geführte Ultraschallwellen zeichnen sich dadurch aus, dass sie große Distanzen innerhalb des zu prüfenden Bauteiles zurücklegen können. Das Ultraschallwellenfeld setzt sich dabei aus verschieden Moden zusammen. Etablierte Prüfverfahren mit geführten Wellen ermitteln häufig nur die Position der Fehlstelle, wobei die Laufzeiten der reflektierten Signale ausgewertet wird. Modenumwandlung bleibt dabei zumeist unberücksichtigt. Die Charakterisierung der Fehlstelle, zum Beispiel hinsichtlich der Länge eines Risses, ist dagegen herausfordernd. Aussagekräftige Zusammenhänge zwischen der Dimension oder Geometrie der Fehlstelle und ihrer Interaktion mit der Ultraschallwelle zu finden, ist Teil aktueller Forschung. Insbesondere eine Betrachtung der Moden höherer Ordnung und deren Amplitudenverhältnisse kann beim Aufspüren dieser Zusammenhänge hilfreich sein. Im Beitrag werden zunächst die Zusammenhänge zwischen den beiden fundamentalen Moden in einer isotropen Platte und der Länge eines Risses untersucht. Aus den Ergebnissen wird ein inverses Verfahren motiviert. Ein Algorithmus wird vorgestellt, der die Risslänge im Modell solange variiert, bis er die modalen Zusammenhänge einer Vorgabe oder einer Messung rekonstruiert. Die eingesetzte Scaled Boundary Finite Element Method ermöglicht dabei eine sehr kurze Rechenzeit in jeden Optimierungsschritt. Zusätzlich ermöglicht die Methode eine Auswertung der modalen Zusammenhänge ohne Postprocessing, was die Rechenzeiten weiter verkürzt. T2 - DAGA 2019 - 45. Jahrestagung für Akustik CY - Rostock, Germany DA - 18.03.2019 KW - Geführte Ultraschallwellen KW - Zerstörungsfreien Prüfung KW - Scaled Boundary Finite Element Method PY - 2019 VL - 45 SP - 1063 PB - Deutsche Gesellschaft für Akustik e.V. AN - OPUS4-47783 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bühling, Benjamin A1 - Strangfeld, Christoph A1 - Maack, Stefan T1 - Entwicklung eines luftgekoppelten Ultraschall-Echo-Prüfverfahrens mittels fluidischer Anregung N2 - In vielen technischen Bereichen werden Ultraschallverfahren zur zer-störungsfreien Werkstoffprüfung eingesetzt. Dabei wird ein Schallpuls von einem Prüfkopf in ein Prüfobjekt eingebracht. Der Puls kann unter anderem durch Membra-nen oder Piezoelemente erzeugt werden und wird in der Regel durch direkten Kontakt oder über ein Koppelmittel an das Objekt übertragen. Luftgekoppelter Ultraschall spielt in kommerziellen Anwendungen bisher eine untergeordnete Rolle, da die Dif-ferenz der akustischen Impedanzen von Luft und Festkörpern immense Verluste beim Übergang des Schallsignals hervorruft. In diesem Beitrag soll ein neuartiges Anregungsprinzip vorgestellt werden, mit dem ein Großteil dieser Verluste vermieden wird. Anstelle eines Festkörpers soll mit Hilfe einer fluidischen Düse Druckluft zur Signalerzeugung eingesetzt werden. In die-ser Düse wird eine selbsterhaltende Strömungsinstabilität erzeugt, die einen Schall-puls von bis zu 100 kHz hervorruft, sodass der Impedanzverlust in die Umgebungsluft entfällt. Da die charakteristische Frequenz eines fluidisch generierten Pulses maßgeb-lich von der Bauform der Düse und dem anliegenden Druck abhängt, lässt sich mittels einer geeigneten Strömungsregelung ein breiter Frequenzbereich zur Abtastung nut-zen. Die so emittierten Pulse werden auf das Prüfobjekt gerichtet und die reflektierten Signale mit einem Laservibrometer an der Oberfläche des Objekts im Echo-Verfahren abgetastet. Von drei signalmindernden Materialübergängen bei gewöhnlichem luftge-koppeltem Ultraschall bleibt in dem hier vorgeschlagenen Messystem lediglich die Grenzfläche von Luft zu Prüfkörper, sodass eine höhere Signalausbeute als bisher er-wartet werden kann. T2 - DACH-Jahrestagung 2019 CY - Friedrichshafen, Germany DA - 27.05.2019 KW - Ultraschall KW - Ultrasound KW - Air-coupled KW - Luftgekoppelt KW - Fluidic oscillator KW - Fluidischer Oszillator KW - Laser-Doppler-Vibrometer KW - Refraktovibrometrie KW - Refracto-vibrometry KW - NDT KW - ZfP PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-481207 VL - 2019 SP - 1 EP - 8 PB - DGZfP Deutsche Gesellschaft für Zerstörungsfreie Prüfung AN - OPUS4-48120 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Knigge, Xenia A1 - Radnik, Jörg T1 - Physico-chemical characterization of sterilized AlOOH nanoparticles by XPS / HAXPES / SEM N2 - Here a dataset of XPS, HAXPES and SEM measurements for the physico-chemical characterization of sterilized AlOOH nanoparticles is presented. The measurements are part of the H2020 project “NanoSolveIT”. KW - HAXPES KW - XPS KW - SEM KW - AlOOH KW - Nanoparticles PY - 2023 DO - https://doi.org/10.5281/zenodo.7966245 PB - Zenodo CY - Geneva AN - OPUS4-57757 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Mike A1 - Zaghdoudi, Maha A1 - Brandt, Guido A1 - Kömmling, Anja A1 - Jaunich, Matthias A1 - Wolff, Dietmar T1 - Coefficients of Friction in Dependence on Aging State of Elastomers – Experimental Identification and Numerical Simulation of the Experiment N2 - Elastomer seals are mounted as barrier seals in lid systems of containers designed for transport and disposal of negligible heat generating radioactive waste and as auxiliary seals in spent fuel storage and transportation casks (dual purpose casks (DPC)). When the behavior of mounted seals under normal and hypothetical accident conditions of disposal and transport is to be simulated, a comprehensive knowledge of their complex mechanical properties at every state of aging is necessary. In previous works, BAM’s efforts in experimental investigations on specimen artificially aged at different temperatures and times and the implementation of the found results in finite element material models were presented. Additionally, our approaches to reproduce the aging process itself and to extrapolate the results of artificially accelerated aging to longer times were presented. Numerical simulations have shown that the behavior of the seal during mounting and one-sided pressurizing and the resulting performance values such as leakage rate strongly depend on the coefficient of friction (COF) between flange and seal. The friction coefficient, in turn, depends on the aging state of the elastomer material as several publications suggest (see below). Dynamic COF between an exemplary ethylene propylene diene rubber (EPDM) material and a stainless steel ball were determined by using a self-designed linear oscillation tribometer. Unaged and artificially aged EPDM specimen stored for 30 days and 100 days at a temperature of 150 °C were tested. A stainless steel ball (d=10 mm) is brought in contact with the specimen’s surface und loaded by normal forces of 2.5 N, 5 N, 10 N and 20 N. During a reciprocating movement of the EPDM sheet, the horizontal force/friction force is continuously measured, and the COF can be derived. It is well known that friction is a complex phenomenon especially in soft materials. It cannot be excluded that the measured friction force is influenced by additional force components, resulting from the ball’s grooving through the elastomer’s surface. This force depends on the penetration depth of the ball and on the resistance of the elastomer in its different states of aging. The latter results from microstructural changes i.e., chain scission and additional crosslinking that occur during aging which in turn influence the softening or hardening of the material. A finite element (FE) ABAQUS® model was developed to reproduce the measurement process. It should help to better understand the physical mechanisms and to quantify the percentage of measured forces resulting from real friction on the one hand and forces resulting from unintended side effects that could falsify the result on the other hand. The behavior of the elastomer in its different states of aging is reproduced by a FE material model already presented in previous works of BAM. T2 - ASME 2022 Pressure Vessels & Piping Conference (PVP2022) CY - Las Vegas, NV, USA DA - 17.02.2022 KW - Numerical Simulation KW - Radioactive Waste KW - Elastomers KW - Aging KW - Seal Behavior KW - Leakage Rate KW - Coefficient of Friction KW - Experiment PY - 2022 SP - 1 EP - 8 PB - American Society of Mechanical Engineers (ASME) CY - New York, NY, USA AN - OPUS4-57093 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Mike A1 - Zencker, Uwe A1 - Wolff, Dietmar A1 - Jaunich, Matthias A1 - Kömmling, Anja A1 - Völzke, Holger A1 - Schulze, Dietmar T1 - Numerical simulation of the behaviour of elastomer seals under consideration of time dependent effects N2 - Due to delays in the site-selection procedure to establish a deep geological repository for spent nuclear fuel and high level waste and in construction of the already licensed Konrad-repository for low and intermediate level waste without heat generation, extended periods of interim storage become more relevant in Germany. BAM is involved in most of the cask licensing procedures and especially responsible for the evaluation of cask-related long-term safety issues. The long-term performance of elastomer seals for lid Systems of transport and storage casks whether used as auxiliary seals in spent fuel caslcs or as primary seals for low and intermediate level waste packages is an important issue in this context (Jaunich, 2013; Jaunich, 2014; Kömmling, 2015). The polymeric structure of these seals causes a complex mechanical behaviour with time-dependent elasticity reduction and loss of elastic recovery. The paper presents first results of a comprehensive test Programme consisting of several static and dynamic mechanical short- and long-term tests which have been carried out at BAM on specimens made of representative types of elastomers, fluorocarbon rubber (FKM) and ethylene propylene diene rubber (EPDM). The investigation of the test results used to identify material models and their Parameters as well as the development of two finite element models for the numerical Simulation of tension and compression tests using the finite element code ABAQUS® are described. The calculation results are presented in comparison to the test results. The influence of important material and test parameters was investigated and discussed in sensitivity analyses. T2 - RAMTRANSPORT 2015 - International conference on the radioactive materials transport and storage CY - Oxford, UK DA - 19.05.2015 KW - Numerical analysis KW - Extended interim storage KW - Elastomer seals PY - 2015 SP - Session 4, Paper 28, 1 EP - 9 AN - OPUS4-33832 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias A1 - Grelle, Tobias A1 - Goral, Milan A1 - Wolff, Dietmar ED - Gehde, M. ED - Wagenknecht, U. ED - Bloß, P. T1 - Further investigations on the low temperature performance of rubber seals N2 - For many sealing applications low temperature performance is required. The overall understanding of the relevant influences on low temperature performance of rubber seals are summarized and the currently running investigations described. The correlation of the physical material properties with seal performance is studied. This includes as well purely static sealing applications as the performance during/after fast partial relief of seals at low temperatures. T2 - Technomer 2017 CY - Chemnitz, Germany DA - 09.11.2017 KW - Seal KW - Low temperature KW - Rubber KW - Recovery PY - 2017 SN - 978-3-939382-13-3 VL - 2017 SP - 40 EP - 40 AN - OPUS4-42845 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Wohlleben, W. A1 - Mielke, Johannes A1 - Hodoroaba, Vasile-Dan A1 - Zimathies, Annett A1 - Bianchin, A. A1 - Lecloux, A. A1 - Roebben, G. A1 - Rauscher, H. A1 - Gibson, N. T1 - Development of an integrated approach based on validated and standardized methods to support the implementation of the EC recommendation for a definition of nanomaterial N2 - The VSSA approach has the important advantage over classifying, imaging and counting techniques that it does not involve dispersion protocols. Further, the BET technique as the basis for VSSA determination it is in widespread use, generates low costs and is specified for many commercial materials. Finally, the same equipment allows for a deeper analysis by full isotherm evaluation. The present deliverable assesses all NanoDefine powders, supplemented by further real-world materials (in total 26 powders), and quantitatively compares the relationship between the median size (by Electron Microscopy – considered as benchmark for the EC nanomaterial definition) vs. the size derived from VSSA. The VSSA method mitigates the challenges of EM to assess the thickness of platelets, but worked as well on fibbers and particles of irregular shapes. A screening strategy is proposed. If applied to the further data from real-world materials as validation set, this screening does achieve a correct classification, leaving only borderline materials for tier 2 assessment. KW - Nanomaterial KW - Classification KW - Regulation KW - VSSA KW - Size measurement KW - Particle size PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-398938 DO - https://doi.org/10.1007/s11051-017-3741-x SP - 1 EP - 26 PB - The NanoDefine Consortium CY - Wageningen, The Netherlands AN - OPUS4-39893 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Hodoroaba, Vasile-Dan A1 - Mielke, Johannes T1 - Techniques evaluation report for selection of characterisation methods N2 - This report is the result of a comprehensive study on the available CMs which come potentially in question for the reliable analysis of the number based size distribution of a nanomaterial according to the EC recommendation for a definition of nanomaterial. Based on the performance criteria already established in NanoDefine the potential CMs are evaluated according to studies available in the literature as well as following the expertise of the NanoDefine consortium partners. The specific advantages and disadvantages of each method with respect to its applicability to the scope of NanoDefine are particularly highlighted. An CM evaluation table is produced so that the mostly suited CMs with respect to the EC definition can be grouped and recommended to the corresponding NanoDefine work packages for further specific development (improvement and adaption), or for direct validation and standardisation, respectively. The actual evaluation report including the recommended CMs will be revised and, if necessary, eventually updated at the mid time of the project. The update will be jointly discussed in the NanoDefine consortium on the basis of the results of testing the methods on the NanoDefine real world materials. KW - Nanomaterial KW - Characterization method KW - EC definition PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-389473 UR - http://www.nanodefine.eu/publications/reports/NanoDefine_TechnicalReport_D3.1.pdf SP - D3.1, 1 EP - 57 CY - Wageningen, The Netherlands AN - OPUS4-38947 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Radnik, Jörg A1 - Chemello, Giovanni A1 - Knigge, Xenia A1 - Al-Sabbgh, Dominik A1 - Hodoroaba, Vasile-Dan T1 - XPS, HAXPES, XRD and SEM datasets of functionalized graphene nanoplateletes N2 - The datasets from (Hard Energy) X-ray photoelectron spectroscopy, X-ray diffraction and Scanning Electron Microsopy are related to the publication G. Chemello, X. Knigge, D. Ciornii, B.P. Reed, A.J. Pollard, C.A. Clifford, T. Howe, N. Vyas, V.-D. Hodoroaba, J. Radnik "Influence of the morphology on the functionalization of graphene nanoplatelets analyzed by comparative photoelectron spectroscopy with soft and hard X-rays" Advanced Materials Interfaces (2023), DOI: 10.1002/admi.202300116. KW - Graphene related 2D materials KW - X-ray photoelectron spectroscopy KW - Hard-energy X-ray photoelectron spectroscopy KW - Scanning electron microscopy KW - Powder X-ray diffraction PY - 2023 DO - https://doi.org/10.5281/zenodo.7956497 PB - Zenodo CY - Geneva AN - OPUS4-57898 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias A1 - Stark, Wolfgang A1 - Wolff, Dietmar T1 - Properties of elastomeric seals at low temperature T2 - International rubber conference (IRC 2009) CY - Nürnberg, Germany DA - 2009-06-29 PY - 2009 IS - Poster 23 SP - 1 EP - 3 AN - OPUS4-19611 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bruno, Giovanni A1 - Hentschel, Manfred P. A1 - Onel, Yener A1 - Lange, Axel A1 - Kupsch, Andreas A1 - Wolk, Thomas A1 - Staude, Andreas A1 - Ehrig, Karsten A1 - Müller, Bernd R. T1 - Bewertung von Porositätsparametern in Cordierit-Diesel-Partikelfilter-Materialien mit fortgeschrittenen Röntgenverfahren und statistischer Analyse N2 - Bikontinuierliche poröse Keramiken für Filteranwendungen weisen eine komplizierte Mikrostruktur auf, in der Poren und Festkörperphase 'vermischt' sind. Mechanische, thermische sowie Filtereigenschaften können nur präzise bestimmt werden, wenn die Morphologie beider Phasen quantitativ angegeben werden kann. Hier werden unter Anwendung von 3D Computertomographie (CT) und verschiedenen Techniken, die auf der Röntgenrefraktion basieren, die Porosität und die Porenorientierung in keramischen Cordierit-Dieselpartikelfiltern bewertet. Dabei werden zur Auswertung der Tomogramme die Fouriertransformierten sowie eine neu entwickelte richtungssensitive Bildanalyse (DIVA, directional interface variance analysis) angewandt. Sowohl die genannten Messtechniken als auch der statistische Ansatz gestatten die Extraktion optional ortsaufgelöster oder gemittelter Werte. Es ergeben sich sehr gute Übereinstimmungen der experimentell ermittelten Porositätswerte mit Ergebnissen aus Quecksilberintrusionsversuchen als auch der ermittelten Porenorientierung im Vergleich zu publizierten Angaben zur kristallographischen Textur. Dies legt den Schluss nahe, dass die Kenntnis der Grenzflächen (zwischen Poren und Materie) genügt, die morphologischen Eigenschaften solcher Materialien hinreichend zu beschreiben. T2 - DGZfP-Jahrestagung 2014 CY - Potsdam, Germany DA - 26.05.2014 KW - Cordierit KW - Poröse Keramik KW - Porenorientierung KW - Röntgenrefraktion KW - Computer-Tomographie KW - 3D-Mikrostruktur PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-312946 SN - 978-3-940283-61-0 VL - 148 SP - 1 EP - 8 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-31294 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - John, Sebastian A1 - Widjaja, Martinus Putra A1 - Mair, Georg W. T1 - Modalanalyse als Werkzeug zur Lebensdauerabschätzung bei Composite-Druckbehältern N2 - Hochbeanspruchte Bauteile wie Druckbehälter bergen im Falle eines Versagens ein erhebliches Gefährdungspotential für Mensch und Umgebung. Trotz der Auslegung mit hohen Sicherheitsfaktoren kommt es durch die hauptsächlich bei mobilen Anwendungen eingesetzten Leichtbauwerkstoffe und Materialkombinationen zu komplexen Degradations- und Schädigungsvorgängen, welche unter ungünstigen Umständen zu einem frühzeitigen Versagen führen können. Die hier vorgestellten Untersuchungen beziehen sich auf Typ IV-Gasspeicher, die als Wasserstofftanks in KFZ zur Anwendung kommen. Durch den Einsatz eines Messverfahrens auf Basis einer experimentellen Modalanalyse (EMA) sollen Schädigungs- und Degradationsgrad künftig zerstörungsfrei erfasst und auch einsatzbegleitend überwacht werden können. T2 - DAGA 2021 - 47. Jahrestagung für Akustik CY - Wien, Österreich DA - 15.08.2021 KW - Impact KW - Modalanalyse KW - Druckbehälter PY - 2021 VL - 47 SP - 1202 EP - 1205 AN - OPUS4-53626 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Bernd R. A1 - Mack, D. E. A1 - Laquai, René A1 - Kupsch, Andreas A1 - Helle, O. A1 - Sebold, D. A1 - Vaßen, R. A1 - Bruno, Giovanni T1 - Charakterisierung der Porositäts- und Rissdichteentwicklung in Wärmedämmschichten von Gasturbinenschaufeln mittels Synchrotron Refraktions Radiographie N2 - Die Degradation von Wärmedämmschichten(thermal barrier coatings - TBCs) in Gasturbinen durch glasartige Calcium-Magnesium-Aluminiumsilikat (CMAS)Ablagerungen aus verschiedenen Quellen istseit vielen Jahren ein anhaltendes Problem. In dieser Studie wurde mit Hilfe derSynchrotron-Röntgen-Refraktions-Radiographie (SXRR), und vergleichend mit der Elektronenmikroskopie, das Eindringen von CMAS in die poröse Struktur von atmosphärisch plasmagespritzten (APS)TBCs sowie die Bildung und das Wachstum von Rissen unter thermisch zyklischer Belastung untersucht. Die Ergebnisse deuten darauf hin, dass die Infiltration sowie deren Kinetik im Brenner-Teststand wesentlich vom Benetzungsverhalten des CMAS beeinflusst werden. Trotz desoffensichtlichen Angriffs von CMAS auf die Korngrenzen hat die Wechselwirkung von Yttriumdioxid-stabilisiertem Zirkoniumdioxid (YSZ) mit intrudiertem CMAS keinen unmittelbaren Einfluss auf die Struktur und Dichte der innen Oberflächen(Risse, Poren). In einem späteren Stadium wird die Bildung von Rissen senkrecht zur äußeren Oberfläche in einer breiteren Zone der TBC-Schicht beobachtet. T2 - DGZfP-Jahrestagung 2021 CY - Online meeting DA - 10.05.2021 KW - CMAS - Calcium-Magnesium-Aluminiumsilikat KW - SXRR - Synchrotron X-ray Refraction Radiography KW - TBC - Thermal barrier coatings PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-526732 UR - https://jahrestagung.dgzfp.de/Programm#P32 SP - 1 EP - 15 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-52673 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Léonard, Fabien A1 - Hasenfelder, Uta A1 - Krebs, Holger A1 - Bruno, Giovanni T1 - Assessment of shock tube systems by synchrotron X-ray computed tomography N2 - Shock tube systems are non-electric explosive fuses employed in blasting and demolition applications to trigger the detonation of explosive charges. Their working principle is based on the explosive reaction of a fine explosive powder on the tubing's inner surface, generating a shock wave traveling at a velocity of 2,100 m/s along the length of the tube, without destroying it. One of the key aspects of the manufacturing process of these shock tubes is the size and morphology of the explosive powder grains and their distribution on the inner wall of the tube, in order to propagate the shockwave efficiently and reliably. For the first time, synchrotron X-ray computed tomography has been used to characterize non-destructively the explosive powder grains, typically Al/HMX between 10 and 20 μm in size, in terms of morphology and 3D distribution but also to characterise the presence and location of defects within the shock tube walls. KW - Explosives KW - Nonel KW - Shock wave KW - Blasting KW - Energetic systems PY - 2017 UR - http://www.ndt.net/events/iCT2017/app/content/Paper/61_Leonard.pdf SP - 1 EP - 7 CY - Leuven, Belgium AN - OPUS4-39345 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Léonard, Fabien A1 - Zhang, Zhen A1 - Krebs, Holger A1 - Bruno, Giovanni T1 - Morphological characterisation of explosive powders by XCT: When grain numbers count N2 - Ammonium nitrate (AN) prills are commonly used as an ingredient in industrial explosives and in fertilisers. Conventional techniques (such as BET or mercury intrusion porosimetry) can measure the open porosity and specific surface area of AN prill, but the closed porosity is not obtainable. This work was focused on evaluating X-ray computed tomography (XCT) as a non-destructive technique for the assessment of porosity in AN prills. An advanced data processing workflow was developed so that the segmentation and quantification of the CT data could be performed on the entire 3D volume, yet allowing the measurements (e.g.; volume, area, shape factor…) to be extracted for each individual phase (prill, open porosity, closed porosity) of each individual prill, in order to obtain statistically relevant data. Clear morphological and structural differences were seen and quantified between fertiliser and explosive products. Overall, CT can provide a very wide range of parameters that are not accessible to other techniques, destructive or non-destructive, and thus offers new insights and complementary information. T2 - 10th Conference on Industrial Computed Tomography (iCT 2020) CY - Wels, Austria DA - 04.02.2020 KW - Ammonium nitrate KW - Prill KW - Non-destructive characterisation KW - Porosity KW - Specific surface area PY - 2020 UR - http://www.ndt.net/?id=25118 SN - 1435-4934 VL - 25 IS - 2 SP - 1 EP - 6 PB - NDT.net CY - Kirchwald AN - OPUS4-50348 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Xing, Na A1 - Er, Jasmin A1 - Vidal, Ricardo M. A1 - Khadka, Sandhya A1 - Schusterbauer, Robert A1 - Rosentreter, Maik A1 - Etouki, Ranen A1 - Ahmed, Rameez A1 - Page, Taylor A1 - Nickl, Philip A1 - Bawadkji, Obida A1 - Wiesner, Anja A1 - Radnik, Jörg A1 - Hodoroaba, Vasile-Dan A1 - Ludwig, Kai A1 - Trimpert, Jakob A1 - Donskyi, Ievgen T1 - Scalable covalently functionalized black phosphorus hybrids for broadspectrum virucidal activity N2 - At the onset of viral outbreaks, broad-spectrum antiviral materials are crucial before specific therapeutics become available. We report scalable, biodegradable black phosphorus (BP) hybrids that provide mutation-resilient virucidal protection. BP sheets, produced via an optimized mechanochemical process, are covalently functionalized with 2-azido-4,6-dichloro- 1,3,5-triazine to form P=N bonds. Fucoidan, a sulfated polysaccharide with intrinsic antiviral activity, and hydrophobic chains are then incorporated to achieve irreversible viral deactivation. The material exhibits strong antiviral inhibition and complete virucidal activity against multiple viruses, including recent severe acute respiratory syndrome coronavirus-2 (SARS-CoV-2) variants. It maintains high biocompatibility, remains effective against viral mutations, and is shelf stable for at least five month. The combination of biodegradability, scalable synthesis, and synergistic antiviral and virucidal mechanisms establishes BP-conjugates as a new class of highly efficient antivirals. They offer a broad spectrum antiviral solutions that could bridge the gap between antiviral medicines and general antiseptics. KW - Black phosphorus KW - Antiviral materials KW - Functionalization KW - Biodegradability KW - Sheets PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-652941 DO - https://doi.org/10.48550/arXiv.2510.12854 SN - 2331-8422 SP - 1 EP - 22 PB - Cornell University CY - Ithaca, NY AN - OPUS4-65294 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzweber, Markus A1 - Hodoroaba, Vasile-Dan A1 - Unger, Wolfgang T1 - What about ionic liquids as a 'hot' certified reference material candidate to check your EDS below 1 keV? N2 - Energy-dispersive X-ray spectrometry (EDX) is one of the most applied methods used for the analysis of the chemical composition of solids and thin films. Recent progress in EDS (Energy Dispersive X-ray Spectrometer) technology has increased the general performance also in the energy range < 1 keV addressing low Z elements. Suitable test materials to be employed especially to check the low-energy EDS performance – also in line with ISO 15632 - are rather limited and mainly based on C K and F K lines. In order to obtain valid results in laboratories accredited in compliance with ISO/IEC 17025 it is necessary to periodically check the instrument performance. T2 - M&M 2015 - Microscopy & Microanalysis CY - Portland, Oregon, USA DA - 02.08.2015 KW - Reference material KW - EDX KW - Ionic liquids PY - 2015 DO - https://doi.org/10.1017/S1431927615009356 VL - 21 SP - Suppl. 3, Paper 0856 AN - OPUS4-34211 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Han, Ying T1 - Hochtemperaturermüdung der Aluminiumlegierung EN AW-2618A N2 - Abgasturbolader tragen wesentlich zur Effizienzsteigerung moderner Verbrennungsmotoren bei. Die im Abgasturbolader eingesetzten Radialverdichterräder werden überwiegend aus der warmfesten ausscheidungsgehärteten Aluminiumlegierung EN AW-2618A hergestellt. Die Anforderungen an die Radialverdichterräder steigen und die Betriebszeiten verlängern sich. Für eine optimale Auslegung des Bauteils ist unter anderem die Kenntnis des Ermüdungsverhaltens dieser Legierung erforderlich. Es ist bekannt, dass sich die Mikrostruktur dieser Legierung während des Betriebs vergröbert und dadurch die Festigkeit abnimmt. Das niederzyklische Ermüdungsverhalten für den Ausgangszustand des Werkstoffs und Prüftemperaturen bis 190 °C ist bereits gut untersucht. Für das hochzyklische Ermüdungsverhalten, insbesondere für Prüftemperaturen über 190 °C, liegen jedoch nur wenige Ergebnisse vor. Das Ziel dieser Arbeit ist es daher, die Datenbasis hinsichtlich der hochzyklischen Ermüdungslebensdauer bei erhöhten Prüftemperatur zu vervollständigen und das Werkstoffverhalten sowie die Schädigungsmechanismen zu charakterisieren. Zu diesem Zweck wurden axiale Ermüdungsversuche an glatten Proben durchgeführt. Neben dem T61-Ausgangszustand für eine Basischarakterisierung wurden zwei überalterte Zustände, jeweils bei 230 °C für 10 h und 1000 h ausgelagert und anschließend geprüft, um den Einfluss der Überalterung auf die Ermüdungslebensdauer zu erfassen. Die Auslagerungstemperatur von 230 °C der überalterten Zustände liegt deutlich über der Aushärtungstemperatur von 195 °C des T61-Zustands, was zu Veränderungen der optimal eingestellten Mikrostruktur führt, die sich wiederum in den mechanischen Eigenschaften widerspiegeln. Mit der Überalterungszeit von 10 h wurde ein Zustand untersucht, der einem Härteniveau entspricht, der bei Bauteilrückläufern nach Langzeitbetrieb beobachtet wurde und mit der Überalterungszeit von 1000 h wurden die Werkstoffgrenzen ermittelt. Zusätzlich wurde mittels Transmissionselektronenmikroskopie (TEM) die Vergröberung der festigkeitssteigernden S-Phase untersucht. Der Einfluss der Prüftemperatur auf die Ermüdungslebensdauer wurde durch Versuche bei 230 °C untersucht. Die Ermüdungsversuche wurde durch fraktographische Untersuchungen ergänzt und ausgewählte Ermüdungsversuche wurden mit zerstörungsfreien Prüfmethoden begleitet, um die Schädigung mit zunehmender Zyklenzahl dazustellen. Die Ergebnisse dieser Untersuchungen zeigen eine kürzere Ermüdungslebensdauer für die längere Überalterungszeit bei gleicher Spannungsamplitude. Die Transmissionselektronenmikroskopie zeigt, dass der mittlere Radius der S-Phase nach einer Überalterungszeit von 10 h um den Faktor 2,3 und nach 1000 h um den Faktor 2,7 im Vergleich zum Ausgangszustand zunimmt. Eine Erhöhung der Prüftemperatur auf 230 °C führt bei gleicher Spannungsamplitude zu einer Verkürzung der Ermüdungslebensdauer im Vergleich zu Raumtemperatur. Die fraktographischen Untersuchungen zeigen, dass unabhängig vom Werkstoffzustand und der Prüftemperatur die Rissinitiierung überwiegend an der Probenoberfläche oder in der Nähe der Primärphasen erfolgt. Das Risswachstum mit zunehmender Zyklenzahl kann mit der Replika-Methode erfolgreich abgebildet werden. Die Abbildung des Risses in der noch nicht gebrochenen Probe ist auch mit der Computertomographie möglich. KW - Aluminiumlegierung KW - EN AW-2618A KW - Ermüdung KW - HCF KW - Mikroskopie KW - Fraktographie PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-615288 DO - https://doi.org/10.14279/depositonce-21381 SP - 1 EP - 109 PB - Depostit Once CY - Berlin AN - OPUS4-61528 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jürgens, Maria A1 - Sonntag, Nadja A1 - Olbricht, Jürgen A1 - Skrotzki, Birgit T1 - Cyclic operation performance of 9-12% Cr ferritic-martensitic steels part 1: Cyclic mechanical behavior under fatigue and creep-fatigue loading N2 - The current competitive situation on electricity markets forces power plants into cyclic operation regimes with frequent load shifts and starts/shutdowns. In the present work, the cyclic mechanical behavior of ferritic-martensitic 9-12 % Cr steels under isothermal and thermomechanical loading was investigated for the example of grade P92 material. A continuous softening was observed under all loading conditions. The introduction of hold periods to the applied cycles reduced material lifetime, with most prominent effects at technologically relevant small strain levels. The microstructural characterization reveals a coarsening of the original “martensitic” lath-type microstructure to a structure with polygonal subgrains and reduced dislocation density. The microstructural data forms the input for a physically-based modelling approach, both of which are presented in “Part 2: Microstructural Evolution during Cyclic Loading and its Representation in a Physically-based Micromechanical Model“. T2 - 45. MPA-Seminar CY - Leinfelden-Echterdingen, Germany DA - 01.10.2019 KW - Tempered Martensite Ferritic Steels KW - P92 KW - Low Cycle Fatigue KW - Thermo-Mechanical Fatigue KW - Creep-Fatigue PY - 2019 SP - 75 EP - 79 PB - MPA (Materialprüfungsanstalt Universität Stuttgart) CY - Stuttgart AN - OPUS4-50051 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rehmer, Birgit A1 - Bayram, Faruk A1 - Ávila Calderón, Luis A1 - Mohr, Gunther A1 - Skrotzki, Birgit T1 - BAM reference data: Temperature-dependent Young's and shear modulus data for additively and conventionally manufactured variants of Ti-6Al-4V N2 - The elastic properties (Young's modulus, shear modulus) of titanium alloy Ti-6Al-4V were investigated between room temperature and 400 °C in an additively manufactured variant (laser-based directed energy deposition with powder as feedstock, DED-LB/M) and from a conventional process route (hot rolled bar). The moduli were determined using the dynamic resonance method. The data set includes information on processing parameters, heat treatments, microstructure, grain size, specimen dimensions and weight, Young’s and shear modulus as well as their measurement uncertainty. The dataset was generated in an accredited testing lab using calibrated measuring equipment. The calibrations meet the requirements of the test procedure and are metrologically traceable. The dataset was audited as BAM reference data. KW - Elastic modulus KW - Young's modulus KW - Shear modulus KW - Additive manufacturing KW - Ti-6Al-4V PY - 2023 DO - https://doi.org/10.5281/zenodo.7813732 PB - Zenodo CY - Geneva AN - OPUS4-57286 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Olbricht, Jürgen A1 - Bismarck, Marc A1 - Skrotzki, Birgit T1 - Size effects in miniature specimen creep testing of heat resistant ferritic-martensitic steels N2 - The use of miniaturized specimen geometries in mechanical testing allows extracting the sample material directly from the sidewall of critical components of power plants, like e.g. headers and steam pipes. In this way, both the impacts of the processing of the component (including all shaping and tempering influences) and of the exposure to the complex aging/loading/oxidation conditions in the plant (in case of post-Service tests) can be analyzed and representative mechanical properties are obtained. T2 - CREEP 2015 - 13th International conference on creep and fracture of engineering materials and structures CY - Toulouse, France DA - 31.05.2015 PY - 2015 SP - 163 EP - 164 AN - OPUS4-33528 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - von der Ehe, Kerstin A1 - Jaunich, Matthias A1 - Wolff, Dietmar A1 - Böhning, Martin A1 - Goering, Harald T1 - Radiation induced structural changes of (U)HMW polyethylene with regard to its application for radiation shielding N2 - The special properties of high molecular weight polyethylene (HMW-PE) and ultra high molecular weight polyethylene (UHMW-PE) result basically from their extreme chain lengths and their high degree of crystallinity. As high-performance polymers, they are used for a variety of applications. UHMW-PE in particular is often utilized for endoprothesis (due to its excellent slip and wear properties) and due to its high hydrogen content as a neutron moderator in casks for storage and transport of radioactive materials. To prepare the material for instance for its use as a total joint replacement, it is exposed to radiation for several reasons, such as sterilization and crosslinking, leading to partial improvement of the mechanical properties (e.g. fracture toughness, crack propagation resistance, wear resistance) and better chemical stability. To be applicable for long term radiation shielding purposes for instance over a period of 40 years, PE has to withstand any type of degradation affecting safety relevant aspects. The scope of our investigation comprises an estimation of the radiation impact on the molecular and supra molecular structure of two types of PE and to what extent these changes are detectable by thermo-analytical (TA) methods, such as Differential Scanning Calorimetry (DSC), Thermo Mechanical Analysis (TMA), Dynamic Mechanical Analysis (DMA) and Thermo Gravimetric Analysis (TGA). Additionally FT-IR spectroscopy as well as density and gas sorption measurements were carried out. Due to the poor solubility of HMW-PE and UHMW-PE, some classical analytical techniques are not applicable. But TA-methods represent a feasible approach to detect structural and morphological features of these materials as well as changes caused by external influences, such as thermal treatment and/or irradiation. With the combination of the applied TA-techniques it is possible to distinguish between crosslinking and degradation. T2 - PATRAM 2010 - 16th International symposium on the packaging and transport of radioactive materials CY - London, UK DA - 2010-10-03 PY - 2010 SP - 1 EP - 8 (T25/Paper 173) AN - OPUS4-24621 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias A1 - Wolff, Dietmar A1 - Stark, Wolfgang A1 - Völzke, Holger T1 - Investigation of elastomer seal behavior for transport and storage packages N2 - Rubbers are widely used as main sealing materials for containers for low and intermediate level radioactive waste and as additional component to metal seals in spent fuel and high active waste containers. According to appropriate guidelines and regulations safe enclosure of the radioactive container contents has to be guaranteed for long storage periods as well as down to temperatures of -40 °C for transportation. Therefore the understanding of seal behavior is of high importance. In this paper we focus on the behavior of elastomer seals at low temperatures with regard to poten-tial decrease of leak-tightness. In addition, changes in material properties due to aging effects over long periods of time and their influence on the seal performance is investigated. It is known that material properties of rubbers are strongly temperature dependent. At low tempera-tures this is caused by the rubber-glass transition (abbr. glass transition). During continuous cool-ing, the material changes from rubber-like entropy-elastic to stiff energy-elastic behavior, that al-lows nearly no strain or retraction due to the glass transition. Hence rubbers are normally used above their glass transition but the minimum working temperature limit is not defined precisely. Aging of elastomer seals is important, as possible dynamic loads may have to be considered during the whole interim storage period (so far approved in Germany for up to 40 years) and for transporta-tion after storage. For the investigations, fluorocarbon (FKM) and ethylene-propylene-diene (EPDM) rubbers were selected as they are often used in radioactive waste containers. Some materials were purchased from a commercial seal producer and some materials were compounded and cured at BAM. The elastom-ers where studied by several thermo-analytical methods and compression set to characterize the material behavior at low temperatures. Additionally component tests were performed to determine the breakdown temperature of the sealing function of complete elastomer O-rings. T2 - PATRAM 2013 - 17th International symposium on the packaging and transportation of radioactive materials CY - San Francisco, CA, USA DA - 18.08.2013 PY - 2013 SP - Paper 227, 1 EP - 8 PB - Omnipress AN - OPUS4-30377 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grelle, Tobias A1 - Wolff, Dietmar A1 - Probst, Ulrich A1 - Jaunich, Matthias A1 - Völzke, Holger T1 - Component and material investigations on metal seals for high level radioactive waste containers N2 - In Germany casks for interim storage of spent nuclear fuel and high level radioactive waste are equipped with Helicoflex® metal seals as main sealing barrier of the double lid system. The long-term behaviour of those seals is investigated at Bundesanstalt für Materialforschung und –prüfung (BAM) in order to evaluate the safety function of the containment at different temperatures over storage periods of 40 years or more in case extended interim storage becomes necessary. Long-term investigations have been done for ageing times of up to 8.5 years at temperatures ranging from room temperature to 150 °C. It was found that the seal force and useable resilience decrease over time, which is mainly caused by creep deformation of the aluminium (or silver) outer jacket of the seals. This effect becomes stronger with increasing temperature. The ageing processes of the seal material and the overall seal behaviour is under investigation in order to derive analytical descriptions for the long-term seal performance. Thus, standardized tests on the basic seal materials, with focus on aluminium, and additional investigations on the seals as a component are conducted. The current investigations include compression and tension creep measurements as well as tensile testing. Furthermore, ageing of seal segments provides information on the development of the contact area width, jacket thickness and microstructural changes in dependence of time and temperature. The obtained data are used for the development of material models and an analytical approach to describe and predict the time and temperature dependent sealing behaviour in the long-term. T2 - 11th International Conference on the Transport, Storage and Disposal of Radioactive Materials CY - London, UK DA - 15.05.2018 KW - Metal seal KW - Creep KW - Long-term behavior PY - 2018 SP - 18535, 1 EP - 6 AN - OPUS4-45452 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Salge, T. A1 - Wäsche, Rolf A1 - Hodoroaba, Vasile-Dan T1 - Advanced light element and low energy X-ray analysis of a TiB2 – TiC – SiC ceramic material using EDS spectrum imaging N2 - The accurate EDS microanalysis of light elements such as boron and carbon by spectrum imaging will be demonstrated using a sintered hard ceramic material composed of the three major phases titanium boride (TiB2), titanium carbide (TiC), silicon carbide (SiC) and minor phases, sub-μm in size. The combination of these three materials leads to improved mechanical and tribological properties. Silicon carbide is a material used for mechanical seals. It has the disadvantage of reduced failsafe running functions, causing increased wear when running dry. The added titanium components (TiC and TiB2) improve the failsafe running functions. This technology has already been transferred to industrial applications. KW - EDS KW - Spectrum imaging KW - Ceramic KW - Phase analysis KW - Light elements PY - 2018 UR - https://www.bruker.com/fileadmin/user_upload/8-PDF-Docs/X-rayDiffraction_ElementalAnalysis/Microanalysis_EBSD/LabReports/App_eds_10_LE_keramik_Rev1_1_lores.pdf SP - 1 EP - 5 CY - Berlin AN - OPUS4-44622 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wolff, Dietmar A1 - von der Ehe, Kerstin A1 - Jaunich, Matthias A1 - Böhning, Martin T1 - Performance of neutron radiation shielding material (U)HMW-PE influenced by gamma radiation N2 - Due to their extreme high hydrogen contents high molecular weight (HMW-) and ultra-high molecular weight (UHMW-) polyethylene (PE) are a comprehensible choice as neutron radiation shielding material in thick walled metallic casks for storage and transport of radioactive materials. For this application it has to be taken into consideration that gamma radiation – that is a direct consequence of inserting radioactive material in such casks – has a high influence on the molecular structure of polyethylene. In order to be applicable for long-term neutron radiation shielding purposes during the whole storage period (in Germany for instance up to 40 years) PE has to withstand any type of degradation affecting safety relevant aspects. The scope of our work comprises an estimation of the influence of gamma radiation and temperature on the molecular and supra molecular structure of (U)HMW-PE used as cask components for neutron radiation shielding. Therefore it was investigated to what extent these changes are detectable by a combination of conventional polymer characterization techniques such as Differential Scanning Calorimetry (DSC), Thermo Mechanical Analysis (TMA), Dynamic Mechanical Analysis (DMA), and Thermo Gravimetric Analysis (TGA). Additionally optical (FTIR) and weighing methods were applied. For UHMWPE the results are compared with those published for similar UHMW-PE material that is used in medical technology. For this application, gamma irradiation is applied deliberately for purposes such as sterilization and crosslinking, the latter leading to partial improvement of mechanical properties and better chemical stability. As a result the so far observed structural changes of the irradiated material are not safety relevant for the application of polyethylene as neutron shielding material; moreover, some properties actually improve via irradiation. T2 - PSAM 11 ESREL 2012 - 11th International probabilistic safety assessment and management conference & The annual european safety and reliability conference CY - Helsinki, Finland DA - 25.06.2012 KW - (U)HMW-PE KW - Gamma irradiation KW - Shielding material KW - Cask for storage and transport of radioactive materials PY - 2012 SP - 1 EP - 8 AN - OPUS4-26176 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Shirai, K. A1 - Namba, K. A1 - Wataru, M. A1 - Völzke, Holger A1 - Wolff, Dietmar A1 - Probst, Ulrich A1 - Jaunich, Matthias A1 - Schulz, Sebastian T1 - Numerical evaluation of the long-term sealing performance of the silver gasket for dual purpose metal cask under high temperature N2 - It is important to evaluate the effect of thermal ageing on the sealing performance of metal gaskets under high temperature for long-term usage. Therefore, in order to gain representative data for this kind of metal-sealed lid System, BAM is currently performing laboratory tests of different gasket types with aluminum and silver jackets at three different temperatures under static conditions up to four years so far, using test flanges for gaskets with full scale cross section diameter but much smaller outer diameter. On the other hand, in order to investigate the applicability of the numerical methodology to evaluate the long-term behavior of the metal gaskets, such as a correlation between seal pressure force and holding time, CRIEPI is developing a modeling method including material tests (tensile and creep tests) at high temperature. In this paper, the applicability of the finite element method (ABAQUS) to predict the recovery displacement and residual seal pressure force of the gasket complex was verified by comparing the calculated values with BAM’s laboratory test results under the joint research agreement between BAM and CRIEPI. T2 - PATRAM 2013 - 17th International symposium on the packaging and transportation of radioactive materials CY - San Francisco, CA, USA DA - 18.08.2013 KW - Metal seals KW - Extended storage KW - Long-term storage KW - Dual purpose cask PY - 2013 SP - 1 EP - 8 PB - Omnipress AN - OPUS4-31947 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rockenhäuser, Christian A1 - von Hartrott, P. A1 - Metzger, M. A1 - Skrotzki, Birgit T1 - Comparison of S-phase coarsening in alloy 2618A during ageing, creep, and fatigue N2 - The coarsening of S-phase precipitates in alloy 2618A was compared for different ageing conditions (heat treatment, creep, and fatigue). T2 - LightMAT 2017 CY - Bremen, Germany DA - 08.11.2017 KW - Alloy 2618A KW - Degradation KW - Coarsening KW - S-phase KW - Dark-field transmission electron microscopy (DFTEM) PY - 2017 SP - 1 EP - 3 AN - OPUS4-42837 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rockenhäuser, Christian A1 - Skrotzki, Birgit T1 - Microstructure evolution in a 2618A aluminium alloy during ageing N2 - The aluminium alloy 2618A is an Al-Cu-Mg alloy which is part of the 2xxx series of age-hardenable alloys. These materials are designed for long-term Operation in transportation and aerospace industries. The desired properties, e.g. creep behavior, hardness, and damage tolerance, are controlled by the distribution of fine precipitates formed within the matrix. However, the strength of the material declines du ring exposition to elevated temperatures due to the overageing of the S-phase precipitates (AI2CuMg) and the conversion of the S-phase into the stable equilibrium S-phase. A quantitative model of the overageing process at application relevant temperatures would be desirable for accurate predictions of component lifetime made from the 2618A alloy. T2 - MC 2015 - Microscopy conference CY - Göttingen, Germany DA - 06.09.2015 KW - Aluminium alloys KW - Transmission electron microscopy KW - Microstructure KW - Coarsening PY - 2015 SP - MS4.P078, 150 EP - 151 AN - OPUS4-34304 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hodoroaba, Vasile-Dan T1 - You Ask – ACEnano Replies N2 - The workshop starts with introductory information about the workshop and the H2020 project ACEnano, followed by two expert round tables, focussing on how the project could address regulator and industry needs, respectively. This is be followed by parallel sessions on tools (based on preferences expressed by those registered to attend, see “Questions”) and finally a question-and-answer session with the attendees. The experts invited in Round Table 1 have been prepared to answer to questions related to obstacles and advantages for stakeholders such as SMEs to use the ACEnano approaches/tools. Standardisation needs are discussed. T2 - nanoSafety Cluster Training (NSC) Day @ NanoSAFE 2020: ACEnano users’ workshop “You Ask – ACEnano Replies” CY - Online meeting DA - 23.11.2020 KW - ACEnano KW - Standardisation KW - Nanomaterials KW - Nano-characterisation PY - 2020 UR - https://www.nanosafetycluster.eu/ SP - 1 EP - 2 AN - OPUS4-51693 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jürgens, Maria ED - Skrotzki, Birgit ED - Olbricht, Jürgen T1 - Creep fatigue behavior of P91/P92 N2 - 9-12% Cr ferritic-martensitic stainless steels are widely used as high temperature construction materials in power plants due to their excellent creep resistance and good oxidation resistance. Creep resistance is considered as the primary parameter in material selection for base-load power plants, but the growing share of renewable energy sources in power generation forces many installations into more "flexible" operation with frequent load reductions and shutdowns. Under cyclic operation of power plants, temperature gradients occur especially in thick-walled components. Locally, these gradients lead to complex time- and temperature-dependent loading scenarios which may result in superimposed creep deformation/damage, creep-fatigue and thermo-mechanical fatigue. The combination of different damage processes may seriously reduce the lifetimes of respective components. A fundamental understanding of the damage evolution in ferritic-martensitic steels under combined static and cyclic loading is therefore required. In the present contribution, the creep-fatigue behavior of two different 9% Cr steel grades (P91 and P92) was investigated. Standard creep-tests as well as LCF/TMF tests with hold time have been carried out to study the material behavior of the new loading scenarios. Microstructural investigations help to identify the observed deformation characteristics and the dominating damage mechanisms under different loads. The test programme is complemented by cyclic creep-tests (temperature change) and creep-tests under atmospheres. In a next step, the experimental results will be used for parameter identification of a deformation and lifetime model to predict the material behavior. T2 - ECCC 2017 CY - Düsseldorf, Germany DA - 10.09.2017 KW - Near-service testing KW - Power plant KW - Ferritic-martensitic steels KW - P91 KW - P92 KW - Creep-Fatigue PY - 2017 SN - 978-3-514-00832-8 SP - 1 EP - 5 AN - OPUS4-42270 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rehmer, Birgit A1 - Bayram, Faruk A1 - Ávila Calderón, Luis A1 - Mohr, Gunther A1 - Skrotzki, Birgit T1 - BAM reference data: Temperature-dependent Young's and shear modulus data for additively and conventionally manufactured variants of Ni-based alloy Inconel IN718 N2 - The elastic properties (Young's modulus, shear modulus) of Ni-based alloy Inconel IN718 were investigated between room temperature and 800 °C in an additively manufactured variant (laser powder bed fusion, PBF‑LB/M) and from a conventional process route (hot rolled bar). The moduli were determined using the dynamic resonance method. The data set includes information on processing parameters, heat treatments, grain size, specimen dimensions and weight, Young’s and shear modulus as well as their measurement uncertainty. The dataset was generated in an accredited testing lab using calibrated measuring equipment. The calibrations meet the requirements of the test procedure and are metrologically traceable. The dataset was audited as BAM reference data. KW - Elastic modulus KW - Young's modulus KW - Shear modulus KW - Additive manufacturing KW - IN718 PY - 2023 DO - https://doi.org/10.5281/zenodo.7813824 PB - Zenodo CY - Geneva AN - OPUS4-57287 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zaghdoudi, Maha A1 - Kömmling, Anja A1 - Jaunich, Matthias A1 - Wolff, Dietmar A1 - Albouy, P.-A. A1 - Häcker, Ralf A1 - Stock, Daniel T1 - Overview of ongoing research and future prospects on polyethylene neutron shielding materials at bam N2 - The extension of the interim storage period of radioactive waste before disposal will cause additional challenges for the nuclear waste management in Germany, so that an extensive knowledge of the long-term performance of casks, including their components and inventories, will be required for future extended storage licenses. Ultra-high and high molecular weight polyethylenes ((U)HMW-PE) are used for neutron shielding purposes in casks for storage and transport of spent fuel and high-level waste due to their extremely high hydrogen content. During their service life of several decades as cask components, the PE materials are exposed to neutron and gamma radiation from the radioactive inventory of the casks, mechanical assembling stresses and temperature. All these combined effects affect the material properties of such components which in turn may be crucial for some possible accident scenarios. At the Bundesanstalt für Materialforschung und -prüfung (BAM), the effects of high temperature exposure in combination with subsequent or previous irradiation were investigated with a comprehensive aging program including thermal aging at 125 °C for different aging periods up to 5 years and irradiation with doses ranging from 50 to 600 kGy. This contribution provides an overview of the ongoing research related to the structural changes of (U)HMW-PE induced by gamma irradiation and high temperature exposure and focuses on current research perspectives at BAM with regard to the prediction of the dynamic behavior of the material during extended interim storage in case of an accident scenario. First results of the coupled effect of temperature, radiation and mechanical loading will be presented. The effect of microstructural changes induced by gamma irradiation and high temperature on the mechanical behavior of (U)HMW-PE will be assessed. T2 - PATRAM22 CY - Juan-Les-Pins, Antibes, France DA - 11.06.2023 KW - (U)HMWPE KW - Ageing KW - Irradiation KW - WAXD KW - SHPB PY - 2023 SP - 1 EP - 10 AN - OPUS4-57707 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rühle, Bastian A1 - Krumrey, Julian Frederic A1 - Hodoroaba, Vasile-Dan T1 - Dataset accompanying the publication "Workflow towards automated segmentation of agglomerated, non-spherical particles from electron microscopy images using artificial neural networks" N2 - This dataset accompanies the following publication, first published in Scientific Reports (www.nature.com/articles/s41598-021-84287-6): B. Ruehle, J. Krumrey, V.-D. Hodoroaba, Scientific Reports, Workflow towards Automated Segmentation of Agglomerated, Non-Spherical Particles from Electron Microscopy Images using Artificial Neural Networks, DOI: 10.1038/s41598-021-84287-6 It contains electron microscopy micrographs of TiO2 particles, the corresponding segmentation masks, and their classifications into different categories depending on their visibility/occlusion. Please refer to the publication and its supporting information for more details on the acquisition and contents of the dataset, as well as the GitHub repository at https://github.com/BAMresearch/automatic-sem-image-segmentation KW - Electron microscopy KW - Neural networks KW - Image segmentation KW - Automated image analysis PY - 2021 DO - https://doi.org/10.5281/zenodo.4563942 PB - Zenodo CY - Geneva AN - OPUS4-52246 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fedelich, Bernard A1 - Epishin, A. A1 - Link, T. A1 - Klingelhöffer, Hellmuth A1 - Portella, Pedro Dolabella A1 - Skrotzki, Birgit ED - Maruyama, K. ED - Abe, F. ED - Igarashi, M. ED - Kishida, K. ED - Suzuki, M. ED - Yoshimi, K. T1 - Implementation of creep induced rafting into mechanical modelling of superalloys T2 - 12th International conference on creep and fracture of engineering materials and structures CY - Kyoto, Japan DA - 2012-05-27 KW - Single-crystal nickel-base superalloys KW - Microstructural degradation KW - Creep KW - Modelling KW - Rafting PY - 2012 SP - 1 EP - 4(?) AN - OPUS4-27564 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Olbricht, Jürgen A1 - Agudo Jácome, Leonardo A1 - Jürgens, Maria A1 - Roohbakhshan, Farshad A1 - Fedelich, Bernard A1 - Skrotzki, Birgit T1 - Cyclic loading performance and related microstructure evolution of ferritic-martensitic 9-12% Cr steels N2 - The current competitive situation on electricity markets forces power plants into cyclic operation regimes with frequent load shifts and starts/shutdowns. In the present work, the cyclic mechanical behavior of ferritic-martensitic 9-12 % Cr steels under isothermal and thermomechanical loading was investigated for the example of grade P92 material. A continuous softening was observed under all loading conditions. The introduction of hold periods to the applied cycles reduced material lifetime, with most prominent effects at technologically relevant small strain levels. The microstructural characterization reveals a coarsening of the original “martensitic” lath-type microstructure to a structure with polygonal subgrains and reduced dislocation density. The microstructural data forms the input for a physically-based modelling approach. T2 - 44th MPA-Seminar CY - Leinfelden/Stuttgart, Germany DA - 17.10.2018 KW - Ferritic-martensitic steels KW - Cyclic loading KW - Microstructure evolution PY - 2018 SP - 259 EP - 265 AN - OPUS4-47118 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hodoroaba, Vasile-Dan A1 - Yamamoto, K. A1 - Grulke, E. A. A1 - Maurino, V. ED - Bosse, H. ED - Buhr, E. ED - Dziomba, T. ED - Hodoroaba, Vasile-Dan ED - Klein, T. ED - Krumrey, M. T1 - Shape controlled TiO2 nanoparticles as candidates for nano-CRM’s – an ISO case study N2 - Extraction of true, 3D shape (and size) of non-spherical nanoparticles (NPs) is associated with Errors by conventional 2D electron microscopy using projection images. Significant efforts within the ISO technical committee TC 229 ‘Nanotechnologies’ are aimed at establishing accurate TEM and SEM measurement of NP size and shape as robust, standard procedures. Study groups have been organizing inter-laboratory comparisons on well-selected NP systems according to the market needs, such as aggregated titania nano-powder for which size and shape distribution of primary crystallites of irregular shape must be measured accurately. To be noticed is e. g. the fact that the measurement procedure allows only manual selection of the particles clearly distinguishable for analysis as well as manual definition of the contour of the imaged NPs. An inter-laboratory exercise on titania NPs (pure anatase, grown by hydrothermal synthesis) of well-defined non-spherical shape, i.e. bipyramidal, has been recently started within ISO/TC 229 under similar conditions as for the irregular shaped titania. In the TEM micrograph the particles tracked manually according to the measurement protocol. Overlapped particles were allowed to be considered, as long as they are clearly distinguishable. One decisive NP selection criterion was to analyze only those NPs with a roundness value below 0.7, i.e. the NPs laying on the support foil and, hence, with projection areas clearly deviating from perfect circles (R=1). The overall evaluation (for 15 labs) of the size descriptors (area, Feret, minFeret, perimeter) and shape descriptors (aspect ratio, roundness, compactness, extent) by analysis of variance is just to be finished and included in ISO/WD 21363 Nanotechnologies -- Protocol for particle size distribution by transmission electron microscopy. T2 - NanoWorkshop 2018: Workshop on Reference Nanomaterials CY - Berlin, Germany DA - 14.05.2018 KW - Titanium dioxide KW - Nanoparticles KW - Shape-controlled KW - Electron microscopy PY - 2019 SN - 978-3-95606-440-1 DO - https://doi.org/https://doi.org/10.7795/110.20190412 SN - 0179-0609 VL - F-61 SP - 245 EP - 255 PB - Physikalisch-Technische Bundesanstalt CY - Braunschweig und Berlin AN - OPUS4-49990 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hodoroaba, Vasile-Dan A1 - Fontanges, Richard T1 - A new deep-learning AI tool for analysing images of complex nanoparticles N2 - A thousand times thinner than a human hair, nanoparticles (NPs) are finding applications in a range of modern products. However, as some can affect human health or the environment, knowing the types present is essential. Electron microscopy is the ‘gold standard’ for NP analysis, allowing identification based on manual size analysis, but a new method was required to analyse these particles quickly, accurately and in a consistent way. KW - Nanoparticles KW - Imaging KW - AI tool KW - Particle size and shape distribution PY - 2024 UR - https://www.euramet.org/casestudies/casestudiesdetails/news/a-new-deep-learning-ai-tool-for-analysing-images-of-complex-nanoparticles SP - 1 EP - 2 PB - EURAMET CY - Braunschweig AN - OPUS4-60095 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Olbricht, Jürgen A1 - Bismarck, Marc A1 - Skrotzki, Birgit T1 - Charakterisierung des Kriechverhaltens hochwarmfester Stähle durch Versuche an Miniaturproben N2 - Die Einsatzbedingungen der Bauteile von fossil befeuerten Kraftwerken unterliegen derzeit durch aktuelle Entwicklungen des Energiesektors (Stichwort „Energiewende“) erheblichen Veränderungen. Während das Interesse an einer weiteren Steigerung der Wirkungsgrade und den damit verbundenen Erhöhung der Prozessdrücke und -temperaturen prinzipiell anhält, werden parallel neue Verbrennungsprozesse wie z. B. die Oxyfuelverbrennung diskutiert und die Einsatzmöglichkeiten von Ersatzbrennstoffen wie Biomasse und hochkalorischen Müllfraktionen werden untersucht. Während diese Maßnahmen über veränderte Rauchgaszusammensetzungen ggf. zu einem generell verstärkten Hochtemperaturkorrosions-Angriff der Bauteile führen, zwingt der Ausbau der Stromerzeugung auf Basis von Wind- und Sonnenenergie die Anlagenbetreiber gleichzeitig zu einer lastflexiblen Anlagenfahrweise mit häufigen Warm- und Kaltstarts bei möglichst hohen Lastgradienten. Diese veränderten Betriebsbedingungen stellen eine Herausforderung für die Überwachung und Instandhaltung bestehender Kraftwerke sowie für die Konstruktion neuer Anlagen und Komponenten dar. N2 - Miniaturized specimen geometries in mechanicai testing allow extracting the sample material directly from critical components of power plants. In this way, both the Impacts of manufacturing and of the complex aging/loading/oxidation conditions during Service on life consumption are captured and representative mechanicai properties are obtained. In the present contribution, example results of a comparative creep/creep rupture study on P91 tempered martensite ferritic Steel, involving cylindrical Standard and miniature specimens (diameter 3 mm), are presented. The test results of miniature specimens exhibit all characteristic creep features of tempered martensite ferritic steels, and realistic stress and temperature dependences are obtained which correspond well to literature data. However, direct comparison with large scale specimen data reveals small but systematic variations in minimum creep rates, elongations at fracture and times to rupture. These differences are discussed in the light of literature findings on specimen size influences in other heat resistant alloys. Size effects need to be considered for a correct interpretation of results from miniature specimen creep tests. T2 - Langzeitverhalten warmfester Stähle und Hochtemperaturwerkstoffe - Beiträge zur 37. Vortragsveranstaltung der Arbeitsgemeinschaft für warmfeste Stähle und Hochtemperaturwerkstoffe CY - Düsseldorf, Germany DA - 28.11.2014 PY - 2014 SP - 106 EP - 116 AN - OPUS4-32402 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias A1 - Goral, Milan A1 - Sagradov, Ilja A1 - Wolff, Dietmar A1 - Völzke, Holger T1 - Aging investigations of metal seals used in containers for interim storage of spent fuel N2 - For bolted casks for used fuel and high level waste the sealing system has an important impact of ensuring safe enclosure of the inventory The used metal seals show some changes over time which have been addressed for nearly 15 years in running experiments at BAM The observed changes are temperature de pendent and therefore it is expected that test s at higher temperature allow for an acceleration of the effects and ideally the proposal of an ageing model covering the expected time of use . Nevertheless, questions concerning the influence of the experimental approach on the results and effects taking place at the initial days of ageing remain. To address these a new project was launched to give a better understanding of the seal behavior. T2 - PVP2024, Pressure Vessels & Piping Conference CY - Bellevue, WA, USA DA - 29.07.2024 KW - Metal seal KW - Aging KW - Interim storage PY - 2024 SN - 978-0-7918-8851-3 SP - 1 EP - 4 PB - ASME AN - OPUS4-61357 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Beygi Nasrabadi, Hossein A1 - Skrotzki, Birgit T1 - Tensile stress relaxation test ontology (TSRTO) N2 - Tensile Stress Relaxation Test Ontology (TSRTO) has developed for representing the tensile stress relaxation testing process, testing equipment requirements, test pieces charactristics, and related testing parameters and their measurement procedure according to DIN EN ISO 10319-1 standard. Versions info: V1 developed using BFO+CCO top-level ontologies. V3 developed using PROV+PMDco top-level ontologies. Repositories: GitLab: https://gitlab.com/kupferdigital/process-graphs/relaxation-test GitHub: https://github.com/HosseinBeygiNasrabadi/Tensile-Stress-Relaxation-Test-Ontology-TSRTO MatPortal: https://matportal.org/ontologies/TSRTO IndustryPortal: https://industryportal.enit.fr/ontologies/TSRTO KW - Ontology KW - Tensile stress relaxation testing KW - FAIR data PY - 2024 UR - https://gitlab.com/kupferdigital/process-graphs/relaxation-test UR - https://github.com/HosseinBeygiNasrabadi/Tensile-Stress-Relaxation-Test-Ontology-TSRTO UR - https://matportal.org/ontologies/TSRTO UR - https://industryportal.enit.fr/ontologies/TSRTO PB - GitLab CY - San Francisco, CA, USA AN - OPUS4-60546 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Skrotzki, Birgit T1 - Radii of S-phase Al2CuMg in Al-alloy EN AW 2618A after different aging times at 190°C N2 - The dataset contains data from quantitative microstructural analysis of transmission electron microscopy (TEM) studies of the S-phase (Al2CuMg) radii in Al-alloy EN AW 2618A. The investigated material and the applied methods were described in detail in two publications. KW - Aluminium alloy KW - EN AW 2618A a KW - S-phase KW - Al2CuMg KW - Aging KW - Creep KW - Radii distribution KW - TEM PY - 2022 UR - https://doi.org/10.5281/zenodo.6659461 UR - https://doi.org/10.5281/zenodo.7625259 DO - https://doi.org/10.5281/zenodo.6659460 PB - Zenodo CY - Geneva AN - OPUS4-55067 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schicker, Johannes A1 - Sievert, Rainer A1 - Fedelich, Bernard A1 - Noack, Hans-Dieter A1 - Kazak, Fedor A1 - Matzak, Kathrin A1 - Kühn, Hans-Joachim A1 - Klingelhöffer, Hellmuth A1 - Skrotzki, Birgit T1 - Entwicklung von Rechenmodellen zur Lebensdauervorhersage von Werkstoffen für Abgasturbolader-Heißteile unter thermo-mechanischer Ermüdungsbeanspruchung und Übertragung für Anwendung auf Bauteile T2 - Informationstagung Turbomaschinen 2010 CY - Bad Neuenahr, Deutschland DA - 2010-04-15 PY - 2010 IS - R550 SP - 111 EP - 134 AN - OPUS4-21268 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Rockenhäuser, Christian A1 - von Hartrott, P. A1 - Metzger, M. A1 - Karlin, J. A1 - Skrotzki, Birgit A1 - Schweizer, C. T1 - Lebensdauerberechnung von Aluminium-Radialverdichterrädern unter Berücksichtigung der Werkstoffalterung N2 - Die Mikrostruktur von ausscheidungsgehärteten Aluminiumlegierungen ist von herausragender Bedeutung für ihre Festigkeit, da nur Werkstoffe mit gezielt eingestellter Mikrostruktur für Radialverdichterräder ausreichende Festigkeiten erreichen. Diese optimierte Mikrostruktur ändert sich jedoch während des Betriebs, denn die Bauteile werden bei Temperaturen eingesetzt, die nahe der Aushärtetemperatur liegen oder sogar darüber hinausgehen und folglich ist mit Alterung der Mikrostruktur und damit einhergehender Degradation der Eigenschaften zu rechnen. Diese Effekte konnten bisher in der Lebensdauervorhersage nicht berücksichtigt werden, da ihre diesbezüglichen Auswirkungen lediglich qualitativ bekannt waren. In diesem Forschungsvorhaben wurde daher für die Legierung EN AW-2618A einerseits eine sorgfältige und umfassende Charakterisierung der Gefügeentwicklung für anwendungsrelevante Temperaturen und Zeiten bis zu 25.000 h vorgenommen und andererseits eine solide Datenbasis bezüglich der mechanischen Eigenschaften (Zugfestigkeit, Kriechwiderstand, LCF-, TMF-Verhalten) und ihren Änderungen geschaffen. Darauf aufbauend wurde ein Verfahren entwickelt, um die Genauigkeit der Lebensdauerbewertung für Abgasturbolader (ATL)-Verdichterräder aus EN AW-2618A zu verbessern. Ein zeit- und temperaturabhängiges Verformungsmodell nach Chaboche, welches die wesentlichen Phänomene der Hochtemperaturverformung und der Wechselplastizität beschreibt, wurde erweitert und berücksichtigt nun die Werkstoffalterung, indem die Festigkeit nicht nur als Funktion der Temperatur, sondern auch des Alterungszustands (d. h. des mittleren Radius der Ausscheidungen) dargestellt wird. Für die Erweiterung des Modells zur Bewertung der Ermüdungslebensdauer unter Rainflow-klassierten Betriebslastkollektiven wurde analog verfahren. Die berechnete Lebensdauer der im Verlauf des Vorhabens durchgeführten LCF- und TMF-Versuche stimmt gut mit den experimentellen Ergebnissen überein. KW - Alloy 2618A KW - Degradation KW - Dark-field transmission electron microscopy (DFTEM) KW - S-Phase KW - Aluminum PY - 2018 SP - 1 EP - 123 AN - OPUS4-44618 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bertovic, Marija T1 - Human-Related Risks in the Non-Destructive Testing (NDT) of Hollow Railway Axles: Implications for the Education and Training of the NDT Personnel N2 - Non-destructive testing (NDT) is a major contributor to the safe railway operation. Even though NDT reliability in railway maintenance is affected by human factors, there are only just a few studies published in this field so far. Education and training of the NDT personnel are some of the most important drivers of safe and reliable NDT. Continuously improving current practices and tools used for educational purposes can be achieved not only through technical con¬tent, but also through the attention to human factors. The aim of this study was to deepen the understanding of possible human-related risks in the manual ultrasonic inspection of the hollow railway axles and to suggest measures to improve the education and training of the NDT person¬nel. This was achieved by means of Failure Modes and Effects Analysis (FMEA) carried out with eight NDT experts and by a survey of 27 experienced inspectors. The results show that failures can happen throughout the entire NDT process. Prevention of those failures could be improved through the optimization of the organization, technology, documentation and regulations, working conditions and the general process, and through the optimization of the formal education and training. Specialized training of the executives, extended training of the supervisors and the inspectors and improvement of the inspection documentation have been suggested. The study also showed potential for the improvements of the inspection in the field. T2 - 29th European Safety and Reliability Conference CY - Hannover, Germany DA - 22.09.2019 KW - Human Factors KW - Non-Destructive Testing KW - NDT KW - Education KW - Training KW - Failure Modes and Effects Analysis KW - Railway KW - Axle Inspection KW - Ultrasonic Testing KW - Reliability PY - 2019 SN - 978-981-11-2724-3 DO - https://doi.org/10.3850/978-981-11-2724-3_1058-cd SP - 294 EP - 300 PB - Research Publishing CY - Singapore AN - OPUS4-49733 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wasmer, Paul A1 - Bulling, Jannis A1 - Gravenkamp, H. A1 - Prager, Jens T1 - Acoustic-structure interaction in the Scaled Boundary Finite Element Method for primsatic geometries N2 - Due to the short wavelength compared to the dimensions of the structure, the simulation of ultrasonic waves is still a challenging task. A numerical method well suited for this purpose is the semi-analytical Scaled Boundary Finite Element Method (SBFEM). When applying this method, only the boundary of a computational domain is discretized using finite elements, while the interior is described by an analytical ansatz. Hence, the number of degrees of freedom is reduced significantly compared to the classical Finite Element Method (FEM). In recent years, a particular formulation of the SBFEM for the simulation of ultrasonic guided waves was developed. The method constitutes an efficient algorithm for prismatic structures of arbitrary length, such as plates, pipes, or beams. Wave propagation phenomena in such structures can be modeled for isotropic and anisotropic inhomogeneous waveguides. Even though the method is an efficient tool for the simulation of guided waves in solid media, a reliable model for the simulation of acoustic wave propagation in fluids as well as acoustic-structure interaction in terms of SBFEM is still missing. In principle, the fluid can be described by a displacement-based formulation and thus be implemented in existing SBFEM algorithms for solid bodies. However, due to the discretization with classical finite elements, spurious modes occur, which cannot be separated from the physical modes straightforwardly. The spurious modes can be suppressed using a penalty parameter. Although very accurate results were achieved for some problems, this procedure has been proven unreliable for certain cases. For this reason, we propose a different approach in this contribution. We employ a pressure model to simulate the acoustic behavior of fluids. The implementation of the pressure model results in a higher effort due to the necessity of incorporating coupling terms, but it presents a stable alternative without spurious modes. The accuracy of the method is demonstrated in comparison with analytical solutions and results obtained using the FEM. T2 - GACM 2019 CY - Kassel, Germany DA - 28.08.2019 KW - Scaled Boundary Finite Element Method KW - Guided Waves KW - Ultrasound KW - Acoustic-Structure Interaction PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-497364 UR - https://www.upress.uni-kassel.de/katalog/abstract.php?978-3-7376-5093-9 SN - 978-3-86219-5093-9 DO - https://doi.org/10.19211/KUP9783737650939 SP - 347 EP - 350 AN - OPUS4-49736 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Boehm, Rainer T1 - Phased Array und Imaging, zwei raumzeitliche Interferenzverfahren N2 - Phased-Array-Technik und Bildgebung mit Ultraschallwellen sind nach langer Entwicklungszeit inzwischen auf dem Weg zu allgemeiner Verbreitung. Daher bietet sich an, die verschiedenen Techniken und deren Begriffe wie z.B. Phased-Array, SAFT, TFM, FMC und Sparse-Array zusammenfassend in Beziehung zu setzen. All diesen Techniken liegt dieselbe Idee zu Grunde, nämlich durch gezielte Überlagerung von Ultraschallsignalen den gewünschten Effekt zu erreichen. Die verschiedenen Techniken werden kurz charakterisiert und neben den Unterschieden wird beschreiben, auf welche Weise bei all diesen Techniken das Phänomen der konstruktiven Interferenz jeweils genutzt wird. T2 - Ultraschall-Array-Technologien und ihre Anwendungen, Seminar des FA Ultraschallprüfung der DGZfP CY - Berlin, Germany DA - 04.11.2019 KW - Phased Array KW - Imaging KW - Synthetic Aperture Focusing Technique KW - Total Focusing Methode KW - Full Matrix Capture PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-497924 UR - https://www.dgzfp.de/seminar/ultraschall# SP - 1 EP - 20 PB - DGZfP AN - OPUS4-49792 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bulling, Jannis A1 - Gravenkamp, H. T1 - Comparison of different models for stress singularities in higher order finite element methods for elastic waves N2 - In this contribution, we present three models to capture singularities in combination with the Spectral Element Method. The first model, the continued-fraction-based Scaled Boundary Finite Element Method, the second model, a new approach based on enrichment with static modes, and the third model, which uses an hp-refinement near the singularity, are compared among each other and evaluated in terms of their respective efficiency and accuracy. T2 - GAMM 2019 CY - Wien, Austria DA - 18.02.2019 KW - Enriched finite element method KW - Scaled boundary finite element method PY - 2019 DO - https://doi.org/10.1002/pamm.201900095 VL - 19 IS - 1 SP - 1 EP - 2 PB - Wiley-VHC AN - OPUS4-49794 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hirsch, Philipp Daniel T1 - Verbesserung der Tiefenreichweite der Impuls-Thermografie mithilfe von Hochleistungs-Laser-Array, kHz-Kamera und Virtual-Wave-Konzept N2 - Im weitverbreiteten Fall der thermografischen ZfP sollen Defekte im Probeninneren detektiert werden. Da diese eine Inhomogenität darstellen, genügt jegliche Mess- und Datenverarbeitungstechnik, die diese Inhomogenität als Kontrast in der transienten Temperaturverteilung herausarbeitet. Ein üblicher Ansatz ist eine extrem kurze und intensive Blitzlampenbeleuchtung zusammen mit einer nachträglichen Fourier-Transformation zu verwenden. Für die zusätzliche Tiefenbestimmung werden entweder rein phänomenologische Ansätze, semi-analytische Ansätze mit Kalibrationsmessungen oder Fits an analytische bzw. numerische Modelle verwendet. Ein üblicher semi-analytischer Ansatz ist z.B. die Analyse des Abknickens der transienten Abkühlkurve. Problematisch ist das schnelle Abklingen der Amplitude auf Rauschniveau und damit die inhärente Beschränkung der Tiefenreichweite. Eine äquivalente Beschreibung der Wärmeleitung ist über sehr stark gedämpfte thermische Diffusionswellen möglich. Die Eindringtiefe ist dann gleich der thermischen Diffusionslänge. Der semi-analytische Ansatz über normales Least-Squares-Fitting funktioniert für 1D-Schicht-Systeme sehr gut, versagt aber für höherdimensionale Messprobleme. Genau hier setzt eine seit Kurzem bekannte Transformation der diffusen Temperaturentwicklung (bzw. des Realteils der Diffusionswelle) in eine propagierende virtuelle Temperaturwelle an. Dieses sog. Virtual-Wave-Konzept stellt sich selbst als ein weiteres inverses Problem dar. Der Nutzen dieser in einer linearen virtuellen Zeitdomäne propagierenden Welle überkompensiert den numerischen Mehraufwand jedoch deutlich. Zusammen mit neuen Technologien in der Erwärmung durch Hochleistungs-Laser-Arrays und in der Datenakquisition durch kHz-Kameras erlaubt dieser Ansatz eine signifikante Verbesserung der Tiefenreichweite in der Impuls-Thermografie. Im Beitrag werden experimentelle Ergebnisse an einer additiv hergestellten Metallprobe mit überdeckten Schlitzen vorgestellt, die eine Detektion dieser Defekte bis zu einem Seitenverhältnis von Defektbreite/Defekttiefe ~ 0,25 erlauben, also ca. 4 mal tiefer als die übliche Faustformel. T2 - Thermografie Kolloquium CY - Halle, Germany DA - 19.09.2019 KW - Laserthermografie KW - Virtuelle Welle KW - VCSEL PY - 2019 AN - OPUS4-49809 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schönhals, Andreas ED - Zorn, R. T1 - Quasi-elastic scattering of high free volume polymers by neutron time-of-flight spectroscopy N2 - Neutron backscattering experiments have been carried out on a polymer of intrinsic microporosity KW - Polymers of Intrinsic Microporosity PY - 2019 SP - 1 EP - 2 CY - Garching AN - OPUS4-49852 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Knigge, Xenia A1 - Radnik, Jörg T1 - Physico-chemical characterization of sterilized Ce0.5Zr0.5O2 nanoparticles by XPS / HAXPES / SEM N2 - Here a dataset of XPS, HAXPES and SEM measurements for the physico-chemical characterization of sterilized Ce0.5Zr0.5O2 nanoparticles is presented. The measurements are part of the H2020 project “NanoSolveIT”. KW - XPS KW - HAXPES KW - SEM KW - NanoSolveIT KW - Ce0.5Zr0.5O2 nanoparticles PY - 2023 DO - https://doi.org/10.5281/zenodo.7965445 PB - Zenodo CY - Geneva AN - OPUS4-57670 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Knigge, Xenia A1 - Radnik, Jörg T1 - Physico-chemical characterization of CeO2/Co3O4 nanoparticles by XPS / HAXPES / SEM N2 - Here a dataset of XPS, HAXPES and SEM measurements for the physico-chemical characterization of CeO2/Co3O4 nanoparticles is presented. The measurements are part of the H2020 project “NanoSolveIT”. KW - HAXPES KW - XPS KW - SEM KW - Nanoparticles KW - CeO2/Co3O4 PY - 2023 DO - https://doi.org/10.5281/zenodo.7989698 PB - Zenodo CY - Geneva AN - OPUS4-57760 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Knigge, Xenia A1 - Radnik, Jörg T1 - Physico-chemical characterization of Fe3O4 nanoparticles by XPS / HAXPES / SEM N2 - Here a dataset of XPS, HAXPES and SEM measurements for the physico-chemical characterization of Fe3O4 nanoparticles is presented. The measurements are part of the H2020 project “NanoSolveIT”. KW - HAXPES KW - XPS KW - SEM KW - Fe3O4 KW - Nanoparticles PY - 2023 DO - https://doi.org/10.5281/zenodo.7990085 PB - Zenodo CY - Geneva AN - OPUS4-57759 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias A1 - Hagenow, Peter A1 - Kasparek, Eva Maria A1 - Kömmling, Anja A1 - Noack, Volker A1 - Völzke, Holger A1 - Wolff, Dietmar T1 - Requirements for the use of elastomer seals in casks for final disposal of low and intermediate level waste N2 - Elastomer seals are widely used as barrier seals in containers for low and intermediate level radioactive waste and in some countries for spent fuel transportation casks. Depending on the area of use, the rubber materials have to demonstrate proper sealing performance with regard to mechanical, thermal and environmental conditions as well as irradiation during the entire operation period. In Germany the low and intermediate level radioactive waste is planned to be disposed in the Konrad repository in standardized containers. Many of these containers use an elastomer seal between lid and container body. Depending on the radiactive inventory and a possible containment of the waste in inner barrels and/or concrete structures, such containers may require a specific leak tightness. In such cases, specified leakage rates are shall not be exceeded by the the seals to keep potential activity releases from the inventories well below defined limits. Generally, all waste containers have to fulfill the waste acceptance criteria for the Konrad repository as defined by the reports BfS SE-IB-29/08 and SE-IB-30/08. From these criteria several requirements for seal performance are derived. The seals have to: - ensure full functionality until final container disposal, - maintain its function in case of a thermal or mechanical accident, - ensure encapsulation also at -20 °C. This combination of requirements is challenging especially as a seal exchange, which is typical for many other applications, is hardly possible and thus a sound understanding of how to perform safety evaluation of containers is required. Therefore BAM has initiated investigations on elastomer seal behaviour. This work focuses on low temperature behaviour and sealing performance concerning static conditions as well as partial loss of compression and ageing of elastomer seals. Concerning ageing, property changes caused by long-term thermooxidative conditions as well as gamma irradiation are investigated. This contribution presents an overview and explanation of the aims of the ongoing research and gives an update of the most relevant results. T2 - 13th Internationales Symposium "Konditionierung radioaktiver Betriebs- und Stillegungsabfälle CY - Dresden, Germany DA - 22.03.2017 KW - Disposal KW - Konrad repository KW - Seal PY - 2017 SP - 595 EP - 601 AN - OPUS4-39870 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kömmling, Anja A1 - Jaunich, Matthias A1 - Wolff, Dietmar T1 - Ageing of elastomeric seals for storage containers N2 - At BAM Federal Institute for Materials Research and Testing in Germany, it is our responsibility to evaluate the safety of casks designed for transport and/or storage of radioactive material. This includes the investigation of elastomeric seals applied in the containers. Besides examining the low-temperature behavior of elastomeric seals, it is our goal to evaluate the service lifetime of the seals with regard to the requirements for long-term safety (40 years and more) of the containers. Furthermore, we deem it necessary to exceed the requirements given in the ageing standard DIN 53508 and take into account diffusion-limited oxidation (DLO) effects and non-Arrhenius behavior when making lifetime predictions. Therefore, we started an ageing programme with selected rubbers (HNBR, FKM and EPDM) which are oven-aged at four different temperatures (75 °C, 100 °C, 125 °C and 150 °C) in order to extrapolate the data to service temperature using different models and check which one is appropriate. Samples are examined at different times up to 5 years. In order to be able to compare between compressed and relaxed rubber, they are aged in two conditions: the undeformed O-ring state as well as compressed between plates with a compression of 25 % corresponding to the actual compression during service. Additionally, we are ageing samples in flanges that allow leakage rate measurements which is the central performance criterion. Analysis methods include hardness as a quick indicator, compression set and compression stress relaxation as measures reflecting the actual properties of a compressed seal. Additionally, we are applying classical polymer analysis methods like dynamic mechanic analysis and thermogravimetric analysis which show changes in the polymeric structure due to chain scission and crosslinking. Furthermore, we are testing the leakage rate of the O-rings in order to correlate the changes in physical properties to the actual performance of the seal. First results of samples aged up to 100 days show a strong increase in hardness for HNBR, a moderate increase for EPDM and hardly a change for FKM. A similar result is seen in the compression set of samples aged 100 d at 100 °C in compression as HNBR has reached 60 %, EPDM 25 % and FKM 15 % compression set. However, after ageing at 150 °C, EPDM shows a worse performance with 95 % compression set compared to HNBR with only 80 %. This is probably due to DLO effects in HNBR that appear because of the fast ageing and low oxygen permeability in HNBR. This leads to a deficit of oxygen in the center of the sample which is thus protected from ageing and can retain elastic properties. The full paper shall discuss the changes in material properties observed to date and the impact on the performance of elastomeric seals. T2 - IRC 2015 - International rubber conference CY - Nürnberg, Germany DA - 29.06.2015 KW - Elastomer KW - Rubber KW - Aging KW - Lifetime KW - Seal KW - Cask KW - Compression PY - 2015 SP - 1 EP - 10 AN - OPUS4-34939 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Rauscher, H. A1 - Mech, A. A1 - Gaillard, C. A1 - Stintz, M. A1 - Wohlleben, W. A1 - Weigel, St. A1 - Ghanem, A. A1 - Hodoroaba, Vasile-Dan A1 - Babick, F. A1 - Mielke, Johannes T1 - Recommendations on a revision of the EC definition of nanomaterial based on analytical possibilities; updated N2 - In October 2011 the European Commission (EC) published a "Recommendation on the definition of na-nomaterial" (2011/696/EU), to promote consistency in the interpretation of the term "nanomaterial" for legislative and policy purposes in the EU. The EC NM Definition includes a commitment to its review in the light of experience and of scientific and technological developments. This review is ongoing in 2017 and as a contribution to the review the Joint Research Centre of the European Commission (JRC) has already developed a series of three scientific-technical reports with the title: “Towards a review of the EC Recommendation for a definition of the term nanomaterial” which provides to the EC policy services sci-ence-based options on how the definition could be revised or supported with additional guidance. The overarching nature and wide scope of the EC NM Definition, as it does not exclude a priori any particulate material regardless the state, form and size, creates many analytical challenges in its imple-mentation for all stakeholders, including enterprises and regulators. The NanoDefine project has as core objective to support the implementation of the EC NM Definition. In an earlier report1 key aspects of the EC NM Definition were addressed, with the goal to improve the implementability of the EC NM Definition. Based on further developments and results obtained in NanoDefine project that first report was updated and is presented here. The key aspects are discussed based on the results of four years of research performed within the framework of the project. As a result this report assesses how well the requirements of the EC NM Definition can be fulfilled with currently available analytical possibilities. It presents recommendations and options on a revision of the EC NM Definition to improve the implementability of the definition based on currently available analytical possi-bilities, according to the state of the art in 2017. Of the technical issues considered in this report, the following seem to deserve the most attention in terms of clarification of the definition and/or provision of additional implementation guidance: 'external dimension', ‘number based particle size distribution‘, ‘polydispersity‘ and ‘upper size limit‘, the term ‘particle’, the ‘means to prove that a material is not a nanomaterial‘ and ‘the role of the volume specific sur-face area (VSSA)‘, and "particulate materials'. KW - EU definition of a nanomaterial KW - Nanoparticles KW - Revision KW - Update 2017 PY - 2017 UR - http://www.nanodefine.eu/index.php/nanodefine-publications/nanodefine-technical-reports SP - D7.10, 1 EP - D7.10, 71 PB - The NanoDefine Consortium CY - Wageningen, The Netherlands AN - OPUS4-43540 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias A1 - Kömmling, Anja A1 - Horn, Jutta A1 - Völzke, Holger A1 - Wolff, Dietmar T1 - Long-Term Performance of Elastomer seals - From Aging Tests to Lifetime Estimations N2 - Elastomers show a high versatility which makes them ideal materials for sealing applications in various fields. Especially under changing application conditions the high recovery potential of this class of material is beneficial to compensate temperature or pressure fluctuation, and geometrical changes resulting from mechanical loads in e.g. accident conditions. Out of these reasons elastomers are also used in containers for low and intermediate level radioactive waste and for spent fuel transportation casks. In casks designed for low and intermediate level waste elastomer seals can act as primary seal responsible for the containment function whereas in spent fuel storage and transportation casks (dual purpose casks (DPC)) elastomer seals are used as auxiliary seals to allow leakage rate measurements of metal barrier seals. An inherent prerequisite for this kind of application is the Long time-scale of operation without or with limited possibility of seal replacement. In Germany an interim storage license for DPC`s is typically issued for 40 years, a timeframe which might increase in the future due to challenges of the final repository siting procedure. For low and intermediate level waste, also long time periods are required before final disposal can be achieved. Therefore, the performance of elastomer seals over extended time periods is, as for other applications, of high importance. A typical approach to ensure long-term functionality is to perform accelerated aging tests to calculate an estimated lifetime by assuming e.g. Arrhenius like equations for the timetemperature relationship. This approach requires a suitable end of life criterion considering the application of interest. This often can represent a challenge on its own. As BAM is involved in most of the cask licensing procedures and especially responsible for the evaluation of cask-related long-term safety issues we initiated several test programs for investigating the behavior of elastomer seals. Experiments concerning the low temperature performance down to -40 °C and the influence of gamma irradiation have been started first. Currently the thermal aging behavior of elastomer seals, which is the topic of this contribution, is examined. For our aging investigations we use a broad approach to first determine the property changes in different elastomer materials due to thermo-oxidative aging at elevated temperatures and secondly, we test how the typical methods of lifetime extrapolation can be applied to these results. This Approach enables us to detect and exclude undesired side effects which very often influence lifetime estimations. In this contribution, our recent results are extended. The results show that lifetime estimation based on single material properties can be misleading and therefore a combination of several methods is recommended. T2 - ASME 2018 Pressure Vessels and Piping Conference CY - Prague, Czech Republic DA - 15.07.2018 KW - Seal performance KW - Rubber KW - Ageing PY - 2018 VL - PVP2018 SP - 84631-1 EP - 84631-8 AN - OPUS4-46346 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grelle, Tobias A1 - Wolff, Dietmar A1 - Probst, Ulrich A1 - Jaunich, Matthias A1 - Völzke, Holger T1 - Investigation programme for evaluation and prediction of the long-term behaviour of Helicoflex® metal seals N2 - In Germany, for the transport and storage of spent nuclear fuel, casks with double closure lid systems are used, which are equipped with Helicoflex® metal seals. The original interim storage period for these casks was planned to be 40 years. However, recent political developments indicate that a storage time of more than 80 years might be necessary. Therefore, the current storage licenses have to be renewed in due course, which requires extended knowledge of the long-term behaviour of all cask components. At the Bundesanstalt für Materialforschung und -prüfung (BAM), metal seals have been investigated after ageing at temperatures between room temperature and 150 °C for up to 7 years. At regular intervals the seals have been tested for leakage rate as well as for their mechanical behaviour. From these tests pronounced influence of ageing could be shown which results in the decrease of the seal force and the useable resilience. The main reason attributed to these performance changes is the increasing permanent deformation of the outer layer of the seal due to creep. So far, an explicit analytical description of the long-term behaviour that could be used for predictions exceeding the tested ageing times and temperatures was not suitable. In addition to the component tests that were already conducted, a comprehensive investigation programme has been started to describe the mechanical behaviour of the individual seal components. The individual seal components are tested regarding different material characteristics including creep, deformation and microstructural properties. The comparability of the material characterization is ensured by comparing the basic raw material of the specimen with the actual component material. Furthermore, detailed investigations of the time and temperature dependent deformation behaviour are realized by ageing seal segments at multiple temperatures for different periods of time and employing standardized tests. By analysing the acquired data in combination with the ongoing long-term component tests a dataset for analytical prediction of the long-term behaviour of the seals is intended for an extended period of time under a certain temperature regime. T2 - 48th Annual Meeting on Nuclear Technology (AMNT 2017) CY - Berlin, Germany DA - 16.05.2017 KW - Metal seal KW - Creep KW - Long-term behavior PY - 2017 SP - 1 EP - 7 AN - OPUS4-43418 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grelle, Tobias A1 - Wolff, Dietmar A1 - Probst, Ulrich A1 - Jaunich, Matthias A1 - Völzke, Holger T1 - Material investigation and long-term sealing behavior of Helicoflex® metal seals used in containers for spent nuclear fuel N2 - In Germany spent nuclear fuel is stored and transported in casks that possess bolted lid systems equipped with double jacket metal seals of Helicoflex® type in order to enable safe enclosure of the radioactive inventory. A dry interim storage period of 40 years was planned and the casks are licensed for that time span. However, due to political reasons and delayed disposal projects this time span is expected to increase significantly. It is therefore necessary to evaluate the long-term sealing behavior of the casks exceeding 40 years of operating time. In this paper, we discuss our approach to investigate the aging behavior of such metal seals, and to predict the long-term sealing behavior. Accelerated aging component tests with seals are performed at temperatures up to 150°C to investigate the course of seal force, useable resilience and leakage rate. Even though these tests have already shown a significant decrease in seal force and useable resilience after aging times of less than 1 year, for most seals the leakage rate stayed better than the specified value. However, observation of the leakage rate has to be continued to determine the aging effect on the seal properties. As a main influence on the seal long-term behavior the increasing permanent deformation of the outer jacket has been recognized. It is made of aluminum or silver which means that the temperatures that are relevant for the aforementioned application in casks lead to creep deformation. For further investigation of seal behavior a comprehensive research program concerning the material characteristics and aging behavior of the individual seal components, with an emphasis on the outer jacket material, has been launched. The aim is to get a better understanding of the time and temperature dependent creep mechanisms and deformation. The examinations are separated into tests on seal segments and tests on standardized specimen. In order to be able to study the aging process, seal segments are compressed in flanges and stored at temperatures ranging from room temperature to 150°C. After defined time intervals the segments are analyzed by using standardized tests including structure investigation and creep tests. The results are compared with the behavior of the specimen basic raw material. This is done to ensure comparability of the thin jacket material and additional sheet material used for standardized tests. Thus, the prediction of component changes after different aging times at different temperatures can be made. As a result forecasts on the long term seal behavior are intended. T2 - Waste Management Symposia CY - Phoenix, AZ, USA DA - 05.03.2017 KW - Metal seal KW - Creep KW - Long-term behavior PY - 2017 SN - 978-0-9828171-6-2 SP - Article 17135, 1 EP - 8 AN - OPUS4-40611 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bresch, Harald A1 - Schmidt, Alexandra A1 - Bachmann, V. A1 - Kämpf, K. A1 - Kuhlbusch, T. A1 - Schwirn, K. A1 - Völker, D. ED - Bosse, H. ED - Buhr, E. ED - Dziomba, T. ED - Hodoroaba, Vasile-Dan ED - Klein, T. ED - Krumrey, M. T1 - OECD Test Guideline on particle size and size distribution of manufactured nanomaterials N2 - The properties of nanomaterials are influenced not only by their chemical composition but also by physical properties (such as size, geometry and crystal structure). For the reliable determination and assessment of behaviour and effects of nanomaterials as well as for the determination of the exposure of humans and environment a comprehensive physical-chemical characterization of nanomaterials is essential. This is an important prerequisite to identify them as nanomaterials and to interpret and compare test results and - in future – to forecast interaction and effects of nanomaterials. In 2006, the OECD launched a sponsorship program for the testing of nanomaterials in which 11 nanomaterials were thoroughly investigated using a variety of methods. The aim of the project was, among other things, to find out where problems occur and where there are gaps in the measurement and test procedures and where are changes required. An important outcome of the sponsorship program was the finding that the OECD Test Guidelines should in several cases be extended to the specific needs in testing of nanomaterials. The existing standardized test methods of the OECD for physical-chemical characterization have not been developed for nanomaterials in particular. A high demand for an extension of the test guidelines was identified. Germany complied with the OECD's request in 2017 and has agreed to extend the “Test Guideline on Particle Size Distribution / Fiber Length and Diameter Distributions Test Guideline” for Manufactured Nanomaterials (MN). UBA commissioned BAM and BAuA with the preparation of the Test Guideline. The aim of the project is the development of a harmonized test protocol for a valid and reproducible determination of particle size and size distribution which is one of the most relevant physical-chemical properties for MNs. Different measuring methods provide different results for the size distribution of the particles. This is caused by the different measuring principles of the methods. Each method measures a specific parameter that ultimately determines particle size. First, the measured quantity differs for each method (Scattered light intensity, 2D image / projection, electric mobility, etc.). Second, the calculated diameters of the MN may differ (Feret Diameter, Area Projection, Mobility Diameter, Aerodynamic Diameter, Hydrodynamic Diameter). Third, a measuring method provides a size distribution which is measured either mass-based, surface-based or number-based. A conversion between the results requires additional parameters and thus possibly increases the measurement error. In addition to the technical differences, the individual parameters are strongly influenced by the structure and material of the nanoparticles. For example, a surface functionalization can lead to very different results in the size distribution. The suitability of measurement methods differs with the material of the MN. As a result, two very different results can be measured for the particle size distribution using two different methods, which are nevertheless both correct. Several large projects in recent years therefore concluded that nanomaterials should be characterized by at least two complementary method. Imaging techniques are regarded as one of these methods for the characterization, the complementary methods are supposed to be statistical methods. The different results for the size distribution of nanomaterials become problematic for the registration of new MN. A comparable and reproducible size distribution is a prerequisite for a standardized registration. In the future, the particle size distribution in the EU will also decide on the classification of a substance as a nanomaterial or as a non-nanomaterial. Especially in borderline cases, a standardized and comparable measurement methodology is therefore essential. T2 - NanoWorkshop 2018: Workshop on Reference Nanomaterials CY - Berlin, Germany DA - 14.05.2018 KW - OECD KW - Guideline KW - Particle size distribution KW - Nano KW - Prüfrichtlinie PY - 2019 SN - 978-3-95606-440-1 DO - https://doi.org/10.7795/110.20190412 SN - 0179-0609 VL - F-61 SP - 125 EP - 132 PB - Physikalisch-Technische Bundesanstalt CY - Braunschweig und Berlin AN - OPUS4-49511 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kämpf, K. A1 - Bachmann, V. A1 - Bresch, Harald A1 - Schmidt, Alexandra A1 - Kuhlbusch, T. A1 - Schwirn, K. A1 - Völker, D. ED - Bosse, H. ED - Buhr, E. ED - Dziomba, T. ED - Hodoroaba, Vasile-Dan ED - Klein, T. ED - Krumrey, M. T1 - OECD Test Guideline on particle size and particle size distribution of manufactured nanomaterials: simultaneous measurement of length and diameter of fibers N2 - The new OECD test guideline will address the following four main steps in the determination of the length and width distributions of fibers: sample preparation, image acquisition, data evaluation and uncertainty analysis. As the sample preparation has to be optimized for each material, general quality criteria will be given in the protocol. For full visibility of a fiber the appropriate resolution has to be chosen. In the data evaluation the length and diameter of each fiber will be determined concurrently to allow for application of different regulatory definitions. The quality of the results critically depends on the sample preparation as well as the data evaluation. In this step the classification rules have to be formulated and followed accurately in order to optimize reproducibility of the method. The SOP will be validated in an international round robin test, which is planned for 2018/2019. T2 - NanoWorkshop 2018: Workshop on Reference Nanomaterials CY - Berlin, Germany DA - 14.05.2018 KW - OECD KW - Nano KW - Guideline KW - Particle size distributuion KW - Prüfrichtlinie PY - 2019 SN - 978-3-95606-440-1 DO - https://doi.org/10.7795/110.20190412 SN - 0179-0609 VL - F-61 SP - 302 EP - 302 PB - Physikalisch-Technische Bundesanstalt CY - Braunschweig und Berlin AN - OPUS4-49514 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mech, A. A1 - Gaillard, C. A1 - Marvin, H. A1 - Wohlleben, W. A1 - Hodoroaba, Vasile-Dan A1 - Babick, F. A1 - Friedrich, C. M. A1 - Brüngel, R. A1 - Rückert, J. A1 - Ghanem, A. A1 - Weigel, S. T1 - The NanoDefine Decision Framework and NanoDefiner e-Tool: a practical guide to the identification of nanomaterials N2 - The European Commission's recommendation on the definition of nanomaterial [2011/696/EU] is broadly applicable across different regulatory sectors and requires the quantitative size Determination of constituent particles in samples down to 1 nm. A material is a nanomaterial if 50 % or more of the particles are in the size range 1-100 nm. The implementation of the definition in a regulatory context challenges measurement methods to reliably identify nanomaterials and ideally also nonnanomaterials as substance or product ingredient as well as in various matrices. The EU FP7 NanoDefine project [www.nanodefine.eu] addressed these challenges by developing a robust, readily implementable and cost-effective measurement strategy to decide for the widest possible range of materials whether it is a nanomaterial or not. It is based on existing and emerging particle measurement techniques evaluated against harmonized, material-dependent performance criteria and by intra- and inter-lab comparisons. Procedures were established to reliably measure the size of particles within 1-100 nm, and beyond, taking into account different shapes, coatings and chemical compositions in industrial materials and consumer products. Case studies prove their applicability for various sectors, including food, pigments and cosmetics. A main outcome is the establishment of an integrated tiered approach including rapid screening (Tier 1) and confirmatory methods (tier 2), a decision support flow scheme and a user manual to guide end-users, such as manufacturers, in selecting appropriate methods. Another main product is the “NanoDefiner” e-Tool which implements the flow scheme in a user-friendly software and guides the user in a semi-automated way through the entire decision procedure. It allows a cost-effective selection of appropriate methods for material classification according to the EC's nanomaterial definition and provides a comprehensive report with extensive explanation of all decision steps to arrive at a transparent identification of nanomaterials as well as non-nanomaterials for regulatory purposes. T2 - NanoWorkshop 2018: Workshop on Reference Nanomaterials CY - Berlin, Germany DA - 14.05.2018 KW - Definition of nanomaterial KW - Regulation PY - 2019 SN - 978-3-95606-440-1 SN - 0179-0609 VL - F-61 SP - 114 EP - 124 PB - Physikalisch-Technische Bundesanstalt CY - Braunschweig und Berlin AN - OPUS4-49992 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias A1 - von der Ehe, Kerstin A1 - Wolff, Dietmar A1 - Völzke, Holger A1 - Stark, Wolfgang T1 - Understanding the low temperature properties of rubber seals N2 - Rubbers are widely used as main sealing materials for containers for low and intermediate level radioactive waste and as additional component to metal seals in spent fuel and high active waste containers. The save encapsulation of the radioactive container inventory has to be guaranteed according to legislation and appropriate guidelines for long term storage periods as well as down to temperatures of -40 °C during transport. Therefore the understanding of failure mechanisms that lead to leakage at low temperatures is of high importance. It is known that the material properties of rubbers are strongly temperature dependent. At low temperatures this is caused by the rubber-glass transition (abbr. glass transition). During continuous cooling the material changes from rubber-like entropy-elastic to stiff energy-elastic behaviour, that allows nearly no strain or retraction, due to the glass transition. Hence rubbers are normally used above their glass transition but the minimum working temperature limit is not defined precisely, what can cause problems during application. Therefore the lower operation temperature limit of rubber seals should be determined in dependence of the material properties. The results of Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA) are combined with the results of standardized measurements as the compression set according to ISO 815. To reduce the test time of the standard tests a faster technique was developed. Additionally, the breakdown temperature of the sealing function of complete O-ring seals is measured in a component test setup to compare it with the results of the other tests. The experimental setup is capable of measuring the leakage rate at low temperatures by the pressure rise method. A fluorocarbon rubber (FKM) was selected for this investigation as it is often used for radioactive waste containers. Some materials (seals and test sheets) were purchased from a commercial seal producer and some materials were compounded and cured at BAM in form of rubber sheets. T2 - PATRAM 2010 - 16th International symposium on the packaging and transport of radioactive materials CY - London, UK DA - 2010-10-03 KW - Dichtungen KW - Elastomere KW - Tieftemperaturverhalten PY - 2010 SP - 1 EP - 7 (Session T41 / Paper 169) AN - OPUS4-23887 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kupsch, Andreas A1 - Müller, Bernd R. A1 - Hentschel, M. P. A1 - Lange, A. A1 - Trappe, Volker A1 - Laquai, René A1 - Shashev, Yury A1 - Evsevleev, Sergei A1 - Bruno, Giovanni T1 - Progress survey of X-Ray refraction imaging techniques N2 - The most substantial innovations in radiographic imaging techniques of the last two decades aim at enhanced image contrast of weakly absorbing micro and nano structures by taking advantage of X-ray refraction effects occurring at outer and inner surfaces. The applications range from fibre reinforced plastics to biological tissues. These techniques comprise, among others, X-ray refraction topography, diffraction enhanced imaging, phase contrast imaging, Talbot-Lau grating interferometry, and refraction enhanced imaging. They all make use of selective beam deflections up to a few minutes of arc: the X-ray refraction effect. In contrast to diffraction, this type of interaction has a 100 % scattering cross section, as shown experimentally. Since X-ray refraction is very sensitive to the orientation of interfaces, it is additionally a tool to detect, e.g., fibre or pore orientation. If the detector resolution exceeds the size of (small) individual features, one detects the integral information (of inner surfaces) within the gauge volume. We describe the above-mentioned techniques, and show their experimental implementation in the lab and at a synchrotron source. We also show strategies for data processing and quantitative analysis. T2 - 19th World Conference on Non-Destructive Testing CY - Munich, Germany DA - 13.06.2016 KW - grating KW - topography KW - refraction KW - X-ray PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-366194 SN - 978-3-940283-78-8 VL - 2016/158 SP - We.3.B.2, 1 EP - 9 AN - OPUS4-36619 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Laquai, René A1 - Schaupp, Thomas A1 - Müller, Bernd R. A1 - Griesche, Axel A1 - Kupsch, Andreas A1 - Lange, Axel A1 - Kannengießer, Thomas A1 - Bruno, Giovanni T1 - 3D Crack analysis in hydrogen charged lean duplex stainless steel with synchrotron refraction CT N2 - Hydrogen in metals can cause a degradation of the mechanical properties, the so-called hydrogen embrittlement. In combination with internal stresses, hydrogen assisted cracking (HAC) can occur. This phenomenon is not completely understood yet. To better characterise the cracking behaviour, it is important to gain information about the evolution of the 3D crack network. For this purpose samples of lean duplex stainless steel were loaded with hydrogen by means of electrochemical charging and investigated by means of synchrotron refraction CT and SEM fractography after uniaxial tensile loading. Synchrotron refraction CT is an analyser-based imaging (ABI) technique. It uses a Si (111) single crystal as analyser, which is placed into the beam path between sample and detector. According to Bragg’s law only incident x-rays within a narrow range around the Bragg-angle are diffracted from the analyser into the detector. Hence, the analyser acts as an angular filter for the transmitted beam. This filtering allows to turn the refraction and scattering of x-rays into image contrast. Refraction occurs at all interfaces, where the density of the material changes and is more sensitive to density changes than the attenuation. Therefore, it is possible to detect smaller cracks than with classical x-ray imaging techniques, like CT, with comparable spacial resolution. It also visualises the 3D structure of the cracks and gains quantitative information about their morphology and distribution. Since cracks introduced by HAC are usually very small and have a small opening displacement, synchrotron refraction CT is expected to be well suited for imaging this cracking mechanism and can be a valuable tool to characterise the formation and the evolution of a 3D crack network. T2 - WCNDT 2016 CY - München, Germany DA - 13.06.2016 KW - X-ray refraction KW - Computed tomography KW - Hydrogen assisted cracking KW - Duplex stainless steel PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-366481 SN - 978-3-940283-78-8 VL - BB 158 SP - Tu.4.B.3, 1 EP - 9 AN - OPUS4-36648 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kupsch, Andreas A1 - Hentschel, Manfred P. A1 - Lange, Axel A1 - Bruno, Giovanni A1 - Müller, Bernd R. T1 - Direkte Röntgenrefraktion an Mikrostrukturen N2 - Die durch Brechung an Mikrostrukturen abgelenkte Röntgenstrahlung wird direkt zweidimensional abgebildet. Dazu werden Modellproben einfacher Geometrie (Fasern, Kapillaren, monodisperse Nano- und Mikropartikel) mit einem auf 50 µm kollimierten Synchrotronstrahl (20 keV) gescannt. Die nach den Regeln der geometrischen Optik an prismatischen und linsenartigen Grenzflächen abgelenkte Strahlung wird in etwa 3 Metern Entfernung von einem Flächendetektor mit 7 µm Ortsauflösung zusätzlich zu der ungestörten Resttransmission des Primärstrahls registriert. In der Abfolge der Radiogramme werden die lokalen Orientierungsänderungen der Probekörper-Grenzflächen bei deren Abtastung mit wenigen Mikrometern Schrittweite bildhaft verfolgt. Mit der hier erreichten Winkelauflösung von etwa 3 Bogensekunden (Streuvektor-Inkremente Δk = 10-3nm-1) kann bei 50 µm Ortsauflösung das Materialvolumen bezüglich innerer Grenzflächen mit Nanometer-Separation auch bei hohen Abtastraten unterhalb einer Sekunde pro Bild charakterisiert werden. T2 - DGZfP-Jahrestagung 2014 CY - Potsdam, Germany DA - 26.05.2014 KW - Computertomographie (CT) KW - Rekonstruktionsalgorithmus KW - DIRECTT KW - Missing wedge KW - Statistische Bewertung PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-312931 UR - http://www.ndt.net/article/dgzfp2014/papers/di1b2.pdf SN - 978-3-940283-61-0 IS - DGZfP-BB 148 SP - Di.1.B.2, 1 EP - 9 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-31293 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Cabeza, Sandra A1 - Bruno, Giovanni A1 - Mishurova, Tatiana T1 - Characterization of multiphase metal matrix composites by means of CT and neutron diffraction N2 - The present study examines the relationship between the microstructure of multiphase metal matrix composites and their damage mechanisms. The matrix AlSi12CuMgNi was combined with 15% vol. Al₂O₃ (short fibers), and with 7% vol. Al₂O₃ + 15% vol. SiC (short fibers and whiskers, respectively). The experimental approach encompasses 3D microstructure characterization by means of computed tomography of samples (a) as-cast, (b) after heat treatment, and (c) after compression tests at room temperature. The volume fraction of different phases, their distribution, their orientation, and the presence of defects and damage are studied. The influence of the addition of SiC particles on mechanical properties of composite was investigated. Phase-specific load partition analysis for samples with fiber plane parallel to load was performed by using neutron diffraction (ND) during in-situ compression. ND results show damage in the Si phase, while Al₂O₃ short fibers carry load without damage until failure. The computed tomography observations confirm the load partition analysis. T2 - WCNDT CY - München, Germany DA - 13.06.2016 KW - thermal treatment KW - synchrotron CT KW - neutron diffraction KW - composite KW - aluminum KW - residual stress PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-365499 AN - OPUS4-36549 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Shashev, Yury A1 - Kupsch, Andreas A1 - Lange, Axel A1 - Evsevleev, Sergei A1 - Britzke, Ralf A1 - Bruno, Giovanni A1 - Müller, Bernd R. T1 - Talbot-Lau Röntgen-Interferometrie für die zerstörungsfreie Prüfung N2 - Im vergangenen Jahrzehnt sind gitterinterferometrische Röntgenabbildungen zunehmend in den Fokus des Interesses gerückt. Sie sind insbesondere dann Vorteil, wenn der in der Standardradiographie erreichbare Kontrast nicht genügt, schwach absorbierende Mikro- und Nanostrukturen abzubilden. Auf Kosten mehrerer Aufnahmen gestattet die Talbot-Lau Gitterinterferometrie, die Beiträge aus Absorption, Refraktion und (refraktiver) Streuung zu trennen. Dazu werden die Störungen der Interferenzmuster von Phasengittern ausgewertet. Im Gegensatz zu einer Vielzahl anderer refraktionsbasierter Abbildungsmethoden kann diese Technik mit konventionellen Röntgenröhren (mit divergenter, polychromatischer Strahlung) angewendet werden. Damit ist die Technik geeignet, typische ZfP-Fragestellungen zu lösen. Hier stellen wir Untersuchungen zur Effizienz von Phasengittern vor. Die Visibilität (d.h. die Höhe der Oszillation im Interferenzmuster) wird als Funktion verschiedener geometrischer Parameter verfolgt. Eine Rotation um die Achse parallel zu den Gitterstegen ändert die Form des Gitterprofils (d.h. die Verteilung der Phasenschiebungen). Die kontinuierliche Variation des Winkels und des Detektionsabstandes führt zur Identifikation von ausgezeichneten Kombinationen mit maximaler Visibilität, wobei die Abstände deutlich geringer sind als im Standardaufbau mit senkrechter Gitterbestrahlung. Unsere Studie umfasst Simulationen für monochromatische Quelle und den Vergleich zu experimentellen Ergebnissen mit der Synchrotronstrahlung. In der Literatur wurden die Vorteile der Talbot-Lau Interferometrie für die zerstörungsfreie Prüfung von Faserkompositen und Verbundwerkstoffen demonstriert. Hier werden als Beispiele Messungen an Aluminiumtitanat (Al2TiO5) Pulver gezeigt. T2 - DGZfP 2017 CY - Koblenz, Germany DA - 22.05.2017 KW - Gitterinterferometrische Röntgenabbildung KW - Phasengitter KW - Talbot-Lau Interferometrie KW - Zerstörungsfreie Prüfung PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-404691 SP - 1 EP - 10 PB - DGZfP AN - OPUS4-40469 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Laquai, René A1 - Müller, Bernd R. A1 - Kasperovich, G. A1 - Requena, G. A1 - Bruno, Giovanni T1 - Unterscheidung verschiedener charakteristischer Defekte in mittels selektivem Laserschmelzen hergestelltem Ti-6Al-4V durch Röntgen-Refraktionsradiographie N2 - Das selektive Laserschmelzen (SLM) ist eine pulverbasierte, additive Fertigungsmethode, welche die Herstellung von komplex und individuell geformten Bauteilen ermöglicht. Im Laufe der vergangenen Jahre haben verschiedene Branchen, unter anderem die Luft- und Raumfahrt Industrie, begonnen diese Technologie intensiv zu erforschen. Insbesondere die Titanlegierung Ti-6Al-V4, welche aufgrund ihrer Kombination von mechanischen Eigenschaften, geringer Dichte und Korrosionsbeständigkeit häufig in der Luft- und Raumfahrt eingesetzt wird, eignet sich für die Herstellung mittels SLM. Allerdings können durch nicht optimal gewählte Prozessparameter, welche für gewöhnlich in einer Energiedichte zusammengefasst werden, Defekte in den Bauteilen entstehen. In dieser Studie wurde untersucht, in wie weit Röntgen-Refraktionsradiographie geeignet ist diese Defekte zu detektieren und zu charakterisieren. Bei der Röntgen-Refraktionsradiographie wird die Röntgenstrahlung, nachdem sie die Probe transmittiert hat, über einen Analysatorkristall gemäß der Bragg-Bedingung in den 2D-Detektor reflektiert und dabei nach ihrer Ausbreitungsrichtung gefiltert. Dadurch wird neben der Schwächung auch die Ablenkung der Röntgenstrahlung durch Refraktion im inneren der Probe zur Bildgebung ausgenutzt. Aus den aufgenommen Refraktionsradiogrammen kann der Refraktionswert berechnet werden. Dieser ist ein Maß für die Menge an inneren Oberflächen in der Probe. Zum einen konnte gezeigt werden, dass die Röntgen-Refraktionsradiographie Defekte detektieren kann, die kleiner sind als die Ortsauflösung des verwendeten 2D-Detektors. Zum anderen können zwei verschiedene Typen von Defekten unterschieden werden. Bei dem ersten Typ handelt es sich um runde Poren mit geringer innerer Oberfläche. Diese, sogenannten „keyhole pores“ sind charakteristisch für eine zu hohe Energiedichte während des SLM Prozesses. Bei dem zweiten Typ handelt es sich um nicht komplett aufgeschmolzenes Pulver. Diese Defekte zeichnen sich durch eine hohe innere Oberfläche aus und sind charakteristisch für eine zu geringe Energiedichte. Vergleichende Messungen mit hochauflösender Synchrotron CT und optischer Mikroskopie bestätigen die charakteristischen Formen der verschiedenen Defekte. T2 - DGZfP-Jahrestagung 2018 CY - Leipzig, Germany DA - 07.05.2018 KW - Röntgen-Refraktion KW - Additive Fertigung KW - Porosität PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-449524 SN - 978-3-940283-92-4 VL - DGZfP BB166 SP - Mo.2.A.2., 1 EP - 7 AN - OPUS4-44952 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Shashev, Yury A1 - Kupsch, Andreas A1 - Lange, Axel A1 - Britzke, Ralf A1 - Bruno, Giovanni A1 - Müller, Bernd R. A1 - Hentschel, M. P. T1 - Talbot- Lau interferometry with a non- binary phase grating for non-destructive testing N2 - Grating interferometric set-ups have been established in the last decade. They are promising candidates to obtain enhanced image contrast from weakly absorbing micro and nano structures. They are based on X-ray refraction and near-field diffraction using the Talbot effect. At the expense of taking multiple images, Talbot-Lau grating interferometry allows separating the absorption, refraction, and scattering contributions by analysing the disturbances of a phase grating interference pattern. Contrary to other refraction enhanced methods, this technique can be applied using conventional X-ray tubes (divergent, polychromatic source). This makes it attractive to solve typical non-destructive testing problems. We investigated the efficiency of phase gratings, i.e. the visibility (the amplitude of oscillations) upon variation of propagation distance and phase grating rotation around an axis parallel to the grid lines. This grating rotation changes the grating shape (i.e. the distributions of phase shifts). This can yield higher visibilities than derived from rectangular shapes. Our study includes experimental results obtained from synchrotron radiation, as well as simulations for monochromatic radiation. The advantages of Talbot-Lau interferometry are demonstrated at the example of glass capillaries. T2 - 19th World Conference on Non-Destructive Testing 2016 CY - Munich, Germany DA - 13.06.2016 KW - Talbot- Lau interferometry KW - Phase grating KW - Non-destructive testing PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-383163 SP - Tu_3_G_2, 1 EP - 9 AN - OPUS4-38316 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Johann, Sergej A1 - Strangfeld, Christoph A1 - Müller, Maximilian A1 - Mieller, Björn A1 - Bartholmai, Matthias T1 - RFID sensor systems embedded in concrete – validation experiments for long-term monitoring N2 - Structural Health Monitoring (SHM) is an important part of buildings surveillance and maintenance to detect material failure as early as possible and to contribute in protection of structures and their users. The implementation of Radio Frequency Identification (RFID) sensor systems without cable connection and battery into building components offers innovative possibilities to enable long-term in-situ SHM of addressed structures, bridges. The objectives of the presented study are complete embedding of RFID sensors systems in concrete, full passive communication with the systems, at best for the whole life span of structures. One challenge for this task is the highly alkaline environment in concrete, which requires non-degrading and robust encapsulation. Further Requirements are passive communication and energy supply, appropriate antenna design, placement and fixation in concrete, and the selection and implementation of sensors and connections. The concept is to develop and optimize a simple and robust system, which meets the requirements, as well as comprehensive validation in concrete specimen and real world applications. Two different systems were developed (HF and UHF RFID, respectively). First tasks were the implementation of analog sensors using the superposition principle for the signal adaption. Investigation of suitable materials for robust encapsulation and sensor protection against basic environments. Four materials were investigated in pH 13 solution for 14 days - 3D-Printer-Polymer was completely resolved - PVC has no noticeable decrease in weight - (VitaPro) glass filter for the sensor protector, has weight loss 2.7 % - The epoxy resin has increased by 1.8 % due to moisture expansion Different concrete samples were prepared for the validation of the systems. RFID sensors were embedded in different integration depths. Investigate the energy- and data transfer through concrete, also with varying moisture content. Additionally, signal strength data was used to optimize and validate the antenna characteristics in concrete. Next steps are to guarantee a sufficient energy supply for UHF RFID systems embedded in different concrete mixtures and further embedding the HF and UHF RFID systems in real bridges and buildings to validate the long term monitoring. T2 - DGZfP-Jahrestagung 2017 CY - Koblenz, Germany DA - 22.05.2017 KW - Smart structures KW - RFID sensors KW - Long-term requirements KW - Structural health monitoring KW - Passive RFID KW - Sensor requirements KW - Sensors in concrete PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-403496 UR - https://www.ndt.net/?id=21499 SN - 1435-4934 VL - 22 IS - 9 SP - 1 EP - 7 PB - NDT.net CY - Kirchwald AN - OPUS4-40349 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Johann, Sergej A1 - Strangfeld, Christoph A1 - Müller, Maximilian A1 - Mieller, Björn A1 - Bartholmai, Matthias T1 - RFID sensor systems embedded in concrete – Validation experiments for long-term monitoring T1 - RFID Sensorsysteme eingebettet in Beton – Validierungsexperimente zum Langzeitmonitoring N2 - Structural Health Monitoring (SHM) is an important part of buildings surveillance and maintenance to detect material failure as early as possible and to contribute in protection of structures and their users. The implementation of Radio Frequency Identification (RFID) sensor systems without cable connection and battery into building components offers innovative possibilities to enable long-term in-situ SHM of addressed structures, bridges. The objectives of the presented study are complete embedding of RFID sensors systems in concrete, full passive communication with the systems, at best for the whole life span of structures. One challenge for this task is the highly alkaline environment in concrete, which requires non-degrading and robust encapsulation. Further Requirements are passive communication and energy supply, appropriate antenna design, placement and fixation in concrete, and the selection and implementation of sensors and connections. The concept is to develop and optimize a simple and robust system, which meets the requirements, as well as comprehensive validation in concrete specimen and real world applications. Two different systems were developed (HF and UHF RFID, respectively). First tasks were the implementation of analog sensors using the superposition principle for the signal adaption. Investigation of suitable materials for robust encapsulation and sensor protection against basic environments. Four materials were investigated in pH13 solution for 14 days - 3D-Printer-Polymer was completely resolved - PVC has no noticeable decrease in weight - (VitaPro) glass filter for the sensor protector, has weight loss 2.7% - The epoxy resin has increased by 1.8% due to moisture expansion Different concrete samples were prepared for the validation of the systems. RFID sensors were embedded in different integration depths. Investigate the energy- and data transfer through concrete, also with varying moisture content. Additionally, signal strength data was used to optimize and validate the antenna characteristics in concrete. Next steps are to guarantee a sufficient energy supply for UHF RFID systems embedded in different concrete mixtures and further embedding the HF and UHF RFID systems in real bridges and buildings to validate the long term monitoring. KW - RFID sensors KW - Structural health monitoring KW - Sensors in concrete KW - Smart structures KW - Sensor requirements PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-418331 UR - http://www.ndt.net/?id=21499 SN - 1435-4934 VL - 22 IS - 9 SP - Artikel 8, 1 EP - 7 PB - NDT.net CY - Bad Breisig AN - OPUS4-41833 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kupsch, Andreas A1 - Trappe, Volker A1 - Nielow, D. A1 - Schumacher, David A1 - Lange, A. A1 - Hentschel, M.P. A1 - Redmer, Bernhard A1 - Ewert, U. A1 - Bruno, Giovanni T1 - X-ray laminographic inspection of sandwich shell segments for wind turbine rotor blades N2 - 3D structural investigations are described by X-ray laminography studies of sandwich shell segments, made of a PVC foam core, covered by non-crimp fabric glass fibre composite lay-ups processed by vacuum assisted resin infusion of epoxy. The specific scope of this study is to image transversal flaws within the foam core (joints) and of single ply overlaps. Test flaws were purposely implemented in order to simulate typical failure under cyclic load. In a dedicated test rig for shell structures, the flaw evolution/propagation is monitored by thermography and optical 3D inspection of deformation. Due to the unfavourable preconditions for classical computed tomography as of large aspect ratio, the samples were investigated by coplanar translational laminography. Its limited range of observation angles of ± 45°, results in anisotropic artefacts about the normal to the sample surface, but the typical flaws are well visualized in the as-prepared state, in a state of early damage, and in the repaired state. T2 - 12th European conference on Non-Destructive Testing CY - Gothenburg, Sweden DA - 11.06.2018 KW - X-ray laminography KW - Wind turbine KW - Rotor blade PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-453931 SN - 978-91-639-6217-2 SP - 1 EP - 8 AN - OPUS4-45393 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dominguez-Macaya, A. A1 - Gaal, Mate A1 - Gómez Álvarez-Arenas, T. E A1 - Aurrekoetxea, J. A1 - Iturrospe, A. T1 - Air-coupled ultrasonic testing with Lamb waves for straight and curved GFRP plates N2 - The use of composite materials has been steadily growing during the last decades, as well as the requirements on quality, mechanical properties and geometries of the parts. Some processes, like the 3D UV pultrusion process, manufacture parts that are long and thin, whilst having a varying curvature radius along the same part or even no curvature at all. Studying their mechanical properties along the main fiber direction, which is of foremost interest, is not an easy task nor efficient with most nondestructive methods. The use of air-coupled ultrasonics to evaluate the properties of composite materials has been widely proved by several authors, mainly using guided waves that provide information on the orthotropic properties of this kind of materials. Most of this work has focused on analyzing straight plate-like geometries, due to the simplicity to generate desired Lamb modes in the plate and analyze the behavior of guided waves inside the plate. In our contribution, the differences in the propagation of Lamb waves for straight and curved geometry glass fiber reinforced polymers (GFRP) have been analyzed. A GFRP test sample cured with UV light with one straight and one curved area has been evaluated. The responses of the generated Lamb wave modes for the straight and curved geometries have been compared, accounting for variations in the transducer characteristics, e.g. resonance behavior and focusing. T2 - International Congress on Ultrasonics CY - Bruges, Begium DA - 03.09.2019 KW - Air-coupled KW - Guided waves KW - Composites PY - 2019 DO - https://doi.org/10.1121/2.0001072 VL - 38 SP - 045005 AN - OPUS4-50104 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hauke, Max T1 - Entwicklung eines Versuchsstandes zur Dickenbestimmung von Werkstoffen mithilfe von frequenzmoduliertem Ultraschall N2 - Die vorliegende Arbeit beschäftigt sich mit der Entwicklung eines Versuchsstandes zur Di-ckenbestimmung von Werkstoffen mithilfe von frequenzmoduliertem luftgekoppelten Ultra-schall. Zur Erzeugung des frequenzmoduliertem Signals wird ein fluidischer Oszillator ver-wendet. Die Schwingungsfrequenz des Oszillators ist von der Größe, der Geometrie und den Druckverhältnissen im Oszillator abhängig, welche durch ein Druckventil veränderbar sind. Zur Datenfassung dienen zwei Laservibrometer. Weiterhin soll die schlussendliche Dicken-bestimmung mithilfe eines Kreuzkorrelationsverfahrens erreicht werden. Während der Ent-wicklung wurden Messungen im Medium Luft, als auch mit Polyamid-Probekörpern durchge-führt. Für die Luftmessungen wurde das Ultraschallsignal an zwei Messpunkten erfasst und der Abstand zwischen diesen Messpunkten daraufhin versucht zu ermitteln. Diese Abstand-messungen wurden mit unterschiedlichen Abständen von 6 bis 15 Zentimeter durchgeführt, wobei der Abstand anhand der Daten mit einer Abweichung von unter einem Zentimeter er-folgreich bestimmt werden konnte. Die Messungen am Probekörper waren weniger Erfolg-reich, da keine reproduzierbare Dickenbestimmung erreicht werden konnte. Trotzdem kann die Entwicklung aufgrund der erfolgreichen Abstandmessung in der Luft sowie den neuen Erkenntnissen aus den Messungen am Probekörper als Erfolg betrachtet werden. KW - Berührungsloser Ultraschall KW - Bauwesen KW - Frequenzmodulation KW - Fluidische Anregung PY - 2019 SP - 1 EP - 74 CY - Berlin AN - OPUS4-50219 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Alhadad, Mohamad Saddik T1 - Entwicklung und Validierung eines luftgekoppelen Impakt-Echo-Messverfahrens mittels fluidischer Anregung N2 - Die steigende Nachfrage von zerstörungsfreien Prüfverfahren, welche die Zeitinvestition verbessern und eine kontinuierliche Messung ermöglichen, erfordert die Entwicklung des luftgekoppltes Impakt-Echo-Messverfahrens. Diese Entwicklung kann durch die fluidische Anregung ermöglicht werden. Das Ziel dieser vorliegenden Arbeit war der Aufbau einer Messapparatur, die auf Schnelligkeit setzt und kontinuierlich misst. Nach der Durchführung der fluidischen Anregung wurden mit Hilfe eines Laservibrometers die Daten aufgenommen. Zur Analysierung der auf diese Weise erhobenen Messwerte wurden sie mittels der Fast-Fourier-Transformation in den Frequenzbereich transformiert. Für den Zweck der Validierung wurden Zylinder-Probekörper und Platten-Probekörper wurden verwendet. Die Messungen an den Zylinder-Probekörpern lieferten erfolgreiche Ergebnisse, während die Messungen an den Platten-Probekörpern weitere Untersuchung und Entwicklung benötigten werden. KW - Bauwesen KW - Delamination KW - Kontaktloses Impakt-Echo KW - Dickenbestimmung PY - 2019 SP - 1 EP - 87 CY - Berlin AN - OPUS4-50320 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Pauw, Brian Richard A1 - Smith, A. J. A1 - Snow, T. A1 - Shebanova, O. A1 - Sutter, J. P. A1 - Ilavsky, J. A1 - Hermida-Merino, D. A1 - Smales, Glen Jacob A1 - Terrill, N. J. A1 - Thünemann, Andreas A1 - Bras, W. T1 - Extending SAXS instrument ranges through addition of a portable, inexpensive USAXS module N2 - Ultra-SAXS can enhance the capabilities of existing SAXS/WAXS beamlines and laboratory instruments. A compact Ultra-SAXS module has been developed, which extends the measurable q-range with 0:0015 < q 1/nm) < 0:2, allowing structural dimensions between 30 < D(nm) < 4000 to be probed in addition to the range covered by a high-end SAXS/WAXS instrument. By shifting the module components in and out on their respective motor stages, SAXS/WAXS measurements can be easily and rapidly interleaved with USAXS measurements. KW - Small-angle scattering PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-504867 DO - https://doi.org/10.48550/arXiv.1904.00080 SN - 2331-8422 SP - 1 EP - 25 PB - Cornell University CY - Ithaca, NY AN - OPUS4-50486 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF ED - Zscherpel, Uwe ED - Kasperl, S. T1 - Proceedings of the International Symposium on Digital Industrial Radiology and Computed Tomography (DIR) 2019 N2 - This international symposium is devoted to promote a broad exchange of information on technologies, applications and quality assurance in the area of digital industrial radiology and computed tomography. The meeting provides a unique opportunity for users, scientists, equipment suppliers and all who are interested to discuss the present and future possibilities for industrial applications of the following topics: - Xray detectors and sources - Image processing algorithms - Quantitative imaging - Defect detection & localisation - Feature extraction - Dimensional control - CT, multi-angle - radiography - Laminography & Tomosynthesis - Modelling - Film replacement - Phase contrast - Multi-energies and photon counting - Other radiation techniques (e.g. - neutrons) - Multi-techniques fusion - Standardisation - Qualification & system reliability - Inspection for Additive Manufacturing - Scattering T2 - International Symposium on Digital Industrial Radiology and Computed Tomography (DIR) 2019 CY - Fürth, Germany DA - 02.07.2019 KW - Digital Industrial Radiology KW - Computed Radiography KW - Image Processing PY - 2019 UR - https://www.ndt.net/search/docs.php3?MainSource=264 VL - 264 SP - Paper 24743-1 EP - Paper 24764-17 PB - NDT.net CY - Bad Breisig AN - OPUS4-50519 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niederleithinger, Ernst A1 - Abraham, Odile A1 - Larose, Eric T1 - A review on ultrasonic monitoring of concrete: coda wave interferometry and beyond N2 - The propagation of ultrasonic waves in concrete is affected by its micro- and macro-structure, geometry and properties as well as external influences as stress, temperature or moisture. In addition, age and degradation have a strong influence. Therefore, Ultrasound has been used to monitor concrete samples and structures since decades. However, early applications using conventional techniques as time-of flight or changes in amplitudes have been limited to detect changes in a late stage close to serviceability or ultimate load states. Around 2000, several new, more sensitive techniques adopted from geophysics or other field of material sciences have been introduced to research in ultrasonic monitoring of concrete. The most discussed methodologies are coda wave interferometry, a technique which allows to detect very subtle changes from repeated ultrasonic measurements. Nonlinear acoustic techniques help to identify e. g. cracks even in an inhomogeneous background. Both techniques can be combined. This paper reviews methods and results achieved so far on the laboratory scale and with full scale models the directions for future research and application is given as well. T2 - QNDE 2019 CY - Portland, OR, USA DA - 14.07.2019 KW - Ultrasound KW - Coda wave interferometry KW - Concrete KW - Nonlinear KW - Monitoring PY - 2019 SP - Paper 1234 AN - OPUS4-48686 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Knigge, Xenia A1 - Radnik, Jörg T1 - Physico-chemical characterization of sterilized Co0.75Fe2.25O4 nanoparticles by XPS / HAXPES / SEM N2 - Here a dataset of XPS, HAXPES and SEM measurements for the physico-chemical characterization of sterilized Co0.75Fe2.25O4 nanoparticles is presented. The measurements are part of the H2020 project “NanoSolveIT”. KW - XPS KW - HAXPES KW - SEM KW - NanoSolveIT KW - Co0.75Fe2.25O4 nanoparticles PY - 2023 DO - https://doi.org/10.5281/zenodo.7940769 PB - Zenodo CY - Geneva AN - OPUS4-57664 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Knigge, Xenia A1 - Radnik, Jörg T1 - Physico-chemical characterization of sterilized Ce0.75Zr0.25O2 nanoparticles by XPS / HAXPES / SEM N2 - Here a dataset of XPS, HAXPES and SEM measurements for the physico-chemical characterization of sterilized Ce0.75Zr0.25O2 nanoparticles is presented. The measurements are part of the H2020 project “NanoSolveIT”. KW - XPS KW - HAXPES KW - SEM KW - NanoSolveIT KW - Ce0.75Zr0.25O2 nanoparticles PY - 2023 DO - https://doi.org/10.5281/zenodo.7966133 PB - Zenodo CY - Geneva AN - OPUS4-57673 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Knigge, Xenia A1 - Radnik, Jörg T1 - Physico-chemical characterization of sterilized Ce0.1Zr0.9O2 nanoparticles by XPS / HAXPES / SEM N2 - Here a dataset of XPS, HAXPES and SEM measurements for the physico-chemical characterization of sterilized Ce0.1Zr0.9O2 nanoparticles is presented. The measurements are part of the H2020 project “NanoSolveIT”. KW - XPS KW - HAXPES KW - SEM KW - NanoSolveIT KW - Ce0.1Zr0.9O2 nanoparticles PY - 2023 DO - https://doi.org/10.5281/zenodo.7965602 PB - Zenodo CY - Geneva AN - OPUS4-57672 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Knigge, Xenia A1 - Radnik, Jörg T1 - Physico-chemical characterization of sterilized Co3O4 nanoparticles by XPS / HAXPES / SEM N2 - Here a dataset of XPS, HAXPES and SEM measurements for the physico-chemical characterization of sterilized Co3O4 nanoparticles is presented. The measurements are part of the H2020 project “NanoSolveIT”. KW - XPS KW - HAXPES KW - SEM KW - NanoSolveIT KW - Co3O4 nanoparticles PY - 2023 DO - https://doi.org/10.5281/zenodo.7941248 PB - Zenodo CY - Geneva AN - OPUS4-57666 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Knigge, Xenia A1 - Radnik, Jörg T1 - Physico-chemical characterization of sterilized ZrO2 nanoparticles by XPS / HAXPES / SEM N2 - Here a dataset of XPS, HAXPES and SEM measurements for the physico-chemical characterization of sterilized ZrO2 nanoparticles is presented. The measurements are part of the H2020 project “NanoSolveIT”. KW - XPS KW - HAXPES KW - SEM KW - NanoSolveIT KW - ZrO2 nanoparticles PY - 2023 DO - https://doi.org/10.5281/zenodo.7965536 PB - Zenodo CY - Geneva AN - OPUS4-57671 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Strangfeld, Christoph A1 - Stolpe, Heiko A1 - Kruschwitz, Sabine ED - Schumann, R. T1 - Correlation between the electric impedance and the water layer thickness in partially saturated screed samples N2 - The moisture content of screed samples is monitored by means of embedded sensors. Relative humidity sensors and multi-ring-electrodes are used to measure the spatial moisture distribution during desorption. Based on the humidity data and the pore volume distribution, the moisture and the water layer thickness within the pore space are predicted. Slit shape as well as cylindrical pores are evaluated. Finally, the measured real part of the electrical impedance and the calculated water layer thickness are correlated. Based on the available data, a significant trend change of the impedance is documented at a water layer thickness of approximately 3 nm. This water layer thickness corresponds to a relative humidity of 88.3%. T2 - 10. CMM Tagung CY - Ettlingen, Germany DA - 10.10.2019 KW - Material moisture KW - Screed KW - Embedded sensors KW - Electric impedance KW - Water layer thickness PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-494636 VL - 10 SP - 79 EP - 102 PB - CMM, Karlsruher Institut für Technologie CY - Karlsruhe AN - OPUS4-49463 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Prager, Jens A1 - Vogt, T. T1 - Zum Einsatz geführter Wellen für die Ultraschallprüfung – Ergebnisse der Onlineumfrage N2 - Der Unterausschuss „Geführte Wellen“ im Fachausschuss „Zustandsüberwachung“ der Deutschen Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) hat in einer Online-Umfrage den aktuellen Stand des Einsatzes geführter Ultraschallwellen für die zerstörungsfreie Prüfung und die Strukturüberwachung (structural health monitoring) ermittelt. Es wurden deutsche und internationale Firmen und Forschungseinrichtungen befragt und mehr als 400 beantwortete Fragebögen ausgewertet. Die Umfrageergebnisse zeigen deutlich, welche Vorteile geführte Wellen bringen, aber auch welche Probleme zu bewältigen sind, um einen breiteren Einsatz der Verfahren zu ermöglichen. Aus den Ergebnissen werden Schlussfolgerungen für die weitere Ausrichtung der Forschungs- und Entwicklungsarbeiten aber auch von Aktivitäten zur Normung und zur Bewertung der Zuverlässigkeit der Prüfverfahren abgeleitet KW - Structural Health Monitoring KW - Geführte Wellen KW - Zustandsüberwachung PY - 2019 UR - https://www.dgzfp.de/Portals/24/Zeitung/Ausgaben/Zeitung166.pdf SN - 1616-069X VL - 166 IS - Oktober SP - 8 EP - 9 PB - DGZfP e.V. CY - Berlin AN - OPUS4-49508 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Zorn, Sabine A1 - Bosch, S. A1 - Hahn, Oliver ED - Klemm, D. ED - Stolzenburg, A. T1 - Materialtechnologische Untersuchungen an vier Zeichnungen Leonardo da Vincis aus dem Kupferstichkabinett N2 - Das Kupferstichkabinett der Hamburger Kunsthalle besitzt seit seiner Gründung vier Zeichnungen von Leonardo da Vinci (1452–1519). Sie sind Teil eines umfangreichen Legats des Hamburger Kunsthändlers Georg Ernst Harzen, das der Stadt Hamburg für die 1869 eröffnete Kunsthalle als Besitz übereignet wurde. Die Zeichnungen gelten aufgrund ihrer Provenienzen und stilistischen Verankerung im Werk Leonardos als gesichert. Weiterführende materialtechnologische Untersuchungen wurden nun erstmals anlässlich der Ausstellung »Leonardo da Vinci – Die Zeichnungen im Hamburger Kupferstichkabinett« durchgeführt. KW - Zerstörungsfreie Prüfung KW - Zeichnung KW - Leonardo da Vinci PY - 2019 SN - 978-3-938002-56-8 SP - 128 EP - 135 PB - Druckhaus Köthen CY - Köthen AN - OPUS4-49667 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lugovtsova, Yevgeniya A1 - Mesnil, Olivier A1 - Bulling, Jannis A1 - Prager, Jens A1 - Boller, C. T1 - Damage Quantification in Aluminium-CFRP Composite Structures using Guided Wave Wavenumber Mapping N2 - The use of composite materials is associated not only with the advantages of weight reduction and improved structural performance but also with the risk of barely visible impacts or manufacturing damages. One of the promising techniques for the detection and characterisation of such damages is based on ultrasonic guided wave propagation and analysis. However, the multimodal nature and dispersive behaviour of these waves make their analysis difficult. Various signal processing techniques have been proposed for easier interpretation of guided wave signals and extraction of the necessary information about the damage. One of them is the wavenumber mapping which consists of creating a cartography of the wavenumber of a propagating mode over an inspected area, using a dense wavefield acquisition measured for example with a scanning laser Doppler vibrometer. This technique allows both the quantification of the in-plane size and the depth of damage, for example, impact-induced delamination in composite laminates. In this contribution, wavenumber mapping is applied to a delaminated aluminium-CFRP composite structure which corresponds to composite-overwrapped pressure vessels used for storing gases in aerospace and automotive industries. The analysis of experimental data obtained from measurements of guided waves propagating in an aluminium-CFRP composite plate with impact-induced damage is performed. The output of the imaging is a three-dimensional representation of the delamination induced by the impact. Good agreement between conventional ultrasonic testing and guided wave damage mapping can be found. T2 - 11th International Symposium on NDT in Aerospace CY - Paris Saclay, France DA - 13.11.2019 KW - Damage assessment KW - Lamb waves KW - Multilayered structures KW - Wavefield analysis KW - Impact damage PY - 2019 SP - 33 AN - OPUS4-49663 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmid, Thomas A1 - Dariz, P. ED - Ziemann, M. T1 - Raman band widths of anhydrite II reveal the burning history of high-fired medieval gypsum mortars N2 - The use of high-fired gypsum as binder for masonry and joint mortars or stuccowork in Central Europe in the Early and High Middle Ages was a regional specific as it depended on local gypsum deposits. The calcination technology possible at the time resulted in an assemblage of calcium sulphate phases dehydrated to different degrees and partly thermally damaged accessory minerals of the raw gypsum. Because of the absence of medieval textbooks, the observation of high-temperature, low-pressure mineral transformations and the correlation of phases coexisting in not hydrated binder relicts in the gypsum matrix to the mineralogy of the raw material and the burning conditions constitute the only source to the historical technological know-how. The CaSO4–H2O system consists of five crystalline phases, which can be discriminated by structural analysis methods, such as Raman spectroscopy, due to obvious differences in their spectroscopic data: gypsum (CaSO4 ⋅ 2 H2O), bassanite (hemihydrate, CaSO4 ⋅ ½ H2O), anhydrite III (CaSO4), anhydrite II (CaSO4), and anhydrite I (CaSO4). Only recently, it was possible to demonstrate that small spectroscopic variations exist also within the relatively large stability range of anhydrite II from approx. 180°C to 1180°C: all Raman bands narrow with increasing burning temperature applied in the synthesis from gypsum powder. The determination of band widths of down to 3 cm-1 and differences between them of a few tenths of a wavenumber is not a trivial task. Thus, this contribution discusses peak fitting and strategies for correction of instrument-dependent band broadening. Raman maps of polished thin sections of gypsum mortars provide access to the burning histories of individual remnant thermal anhydrite grains and enable the discrimination of natural anhydrite originating from the gypsum deposit. This novel analytical method was applied to samples from medieval South Tyrolean stucco decorations and sculptures. Beyond that, Raman microspectroscopy was employed for following pyrometamorphic reactions in natural impurities of the raw material. In the presented examples mineral thermometry indicates process temperatures above 800°C: the breakdown of magnesium-rich chlorite led to the formation of forsterite Mg2SiO4, while the thermal decomposition of dolomite CaMg(CO3)2 yielded – after hydration and carbonation – magnesite MgCO3, CaCO3 polymorphs and magnesian calcite. Lower burning temperatures, which leave the accessory minerals in their pristine form, can be traced by measuring the spectra of anhydrite crystalites in grains of firing products and evaluating Raman band widths. Throughout the applications of this analytical method so far, calcination temperatures ranging from approx. 600°C to 900°C were determined. T2 - 10th International Congress on the Application of Raman Spectroscopy in Art and Archaeology CY - Potsdam, Germany DA - 03.09.2019 KW - Raman microspectroscopy KW - High-fired medieval gypsum mortars KW - Raman band width KW - Gypsum dehydration KW - Thermal anhydrite PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-496204 SP - 36 EP - 37 PB - University of Potsdam CY - Potsdam AN - OPUS4-49620 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias A1 - Stark, Wolfgang A1 - Wolff, Dietmar T1 - Behaviour of rubber seals at low temperatures - results of component tests - N2 - The investigation of low temperature properties of elastomeric sealing materials by means of thermo-analytical methods is a sound way to get information about the glass transition process. The breakdown temperature of the sealing function of O-ring seals was measured in a component test setup depending on material and degree of compression. An in depth explanation of the observed component tests behaviour is currently in preparation. It requires the results of thermo-analytical methods and measurements as the compression set (not shown here). With that, a model was developed to describe the correlation between physical material parameters and observed component behaviour. T2 - Jahrestagung Kerntechnik 2013 CY - Berlin, Germany DA - 14.05.2013 PY - 2013 SP - 1 EP - 6 AN - OPUS4-28574 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Mike A1 - Jaunich, Matthias A1 - Goral, Milan A1 - Völzke, Holger T1 - Reproducing and discussion of mechanisms in the contact area between metallic seals and flange during aging by finite element analysis (FEA) N2 - When the first site-specific interim storage licenses for DPCs (dual purpose casks), loaded with spent nuclear fuel or vitrified high-level waste from reprocessing were issued, a duration of 40 years was considered for interim storage license application and the long-term safety assessment of casks. In the meantime, the availability of a final repository is further delayed by several decades and thus interim storage for more than a century becomes a necessity. To assess the long-term performance of the typically used metal seals (e.g. Helicoflex), consisting of a helical spring (Nimonic), an inner stainless steel liner and an outer liner made from silver or aluminum, several experimental programs were conducted and are still ongoing. The investigated metal seals are typically mounted in mock-up flange systems and stored at increased temperatures to accelerate the aging process. In certain intervals the remaining seal force, the useable resilience and the corresponding leakage rate are determined. BAM has accompanied such programs for many years and started independent investigations in 2009. Although the remaining seal force is often used as “…one of the key parameters regarding sealing performances over time…” the presented results so far have shown that the courses of the leakage rate and the remaining seal force do not always correlate as expected. In 2016 BAM firstly published results of seals with aluminum liners where the measured leakage rate started to rise after a quite short time period (< 1 year) at 150 °C, although the seal force decreased only slightly compared to the previous measurement. After exceeding the required leakage rate of 10-8 Pa*m3/s it decreased again to acceptable values in the further course of aging. With reference to already published works, BAM has developed a new detailed ABAQUS finite-element (FE) model to represent the behavior of the seal mounted in the mock-up flange during aging, mainly characterized by the creeping of the outer liner. The main goal of the numerical simulation is to reproduce and understand the changing distribution of contact stresses (outer liner/flange) during aging and to discuss if and how it could be causative for the observed early breach of the leak tightness criteria and its later recovery. T2 - PATRAM 2025, 21st International Symposium on the Packaging and Transportation of Radioactive Materials CY - San Antonio, Texas, USA DA - 27.07.2025 KW - Finite element analysis KW - Metallic seals KW - Aging KW - Contact area PY - 2025 SP - 1 EP - 10 PB - INMM CY - Indianopolis, Indiana, USA AN - OPUS4-63882 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias A1 - Kömmling, Anja A1 - Böhning, Martin A1 - Silbernagl, Dorothee T1 - Comparison of ageing behavior of O-ring seals under hydrogen and air N2 - Elastomeric seals are essential components in the infrastructure which prevent leakage of gas and ensure proper function of technical devices and are therefore highly safety relevant. For proper function a remaining resilience and tolerance to pressure changes is required. The ageing of elastomers is an undesirable but inevitable process leading to a limited lifetime of rubber products such as seals. Independent of the application, as e.g. automotive, piping or container applications, a long lifetime or at least a timely exchange of a seal before occurrence of critical failure is desired. Hydrogen is a key element for the energy turnaround and therefore the compatibility of seals with hydrogen is essential. In addition to the effect of hydrogen uptake and release, which might also cause destructive effects such as rapid gas decompression, ageing at high temperature under hydrogen atmosphere is of interest too. Most of the existing work is addressing the performance of new materials and comprises only very limited investigations concerning long-term use and the behaviour of aged materials in contact with hydrogen. As ageing can lead to substantial changes of material properties, it must be evaluated whether these changes are beneficial or deteriorating for the component function. In this work we present and compare results of the characterization of three sealing materials (EPDM, HNBR, FKM) after ageing at high temperature under hydrogen and air. Despite the common assumption that ageing under hydrogen atmosphere should be less severe for the material in comparison to air ageing, this is not the case for every material. T2 - ASME PVP2025, Pressure Vessels & Piping Conference CY - Montreal, Quebec, Canada DA - 20.07.2025 KW - Aging KW - Seal KW - Compression set KW - Atomic force microscopy PY - 2025 SP - 1 EP - 7 AN - OPUS4-63889 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kömmling, Anja A1 - Simbruner, Kai A1 - Grelle, Tobias A1 - Jaunich, Matthias A1 - Zencker, Uwe A1 - Wolff, Dietmar A1 - Orellana Pérez, Teresa A1 - Völzke, Holger T1 - Research at BAM for evaluating long term safety of container systems and components N2 - Safety of long term containment and storage of radioactive waste is an essential issue, which is increasingly gaining international attention. Extending interim storage beyond initial license periods is one of the major challenges worldwide. BAM has been involved in all kinds of radioactive waste container safety evaluation for storage and transportation including their long term performance from the very beginning. Today, all work related to the safe management of radioactive waste is linked by the activity field “Nuclear Waste Management” within the Focus Area “Energy” at BAM and in conjunction with a research strategy and agenda. Most recently, the working group “Long Term Safety of Container Systems and Components” was established to launch and perform research projects related to safety issues concerning the extended interim storage of radioactive waste. For example, within our project LaMEP, we investigate ageing effects of metal and elastomer seals as well as polymeric neutron shielding materials, which are container components that fulfil major safety functions. The results of the experiments help to understand the long term behaviour of these components. Likewise, our project BRUZL started at BAM in 2018 with the aim of developing a fracture mechanics approach to understand and describe a potential brittle failure mechanism of fuel cladding during long-term interim storage. BAM also contributes to the GRS project “Development of methods and models and international exchange for safety evaluation in the frame of interim storage of radioactive waste”. Additionally, BAM is involved in several international research programmes dealing with extended interim storage, such as the European Joint Programme on Radioactive Waste Management (EURAD), the Extended Storage Collaboration Program (ESCP) and IAEA Coordinated Research Projects. The present contribution provides a comprehensive overview of BAM research activities contributing to national and international gap analyses and to filling knowledge gaps regarding the safe long term management of radioactive waste. T2 - Annual Meeting on Nuclear Technology 2019 CY - Berlin, Germany DA - 07.05.2019 KW - Radioactive Waste KW - Long-term safety PY - 2019 SN - 978-3-926956-95-8 SP - 1 EP - 5 AN - OPUS4-51486 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kömmling, Anja A1 - Jaunich, Matthias A1 - Wolff, Dietmar T1 - Characterisation of degradation and determination of end-of-lifetime criterion for O-ring seals N2 - The ageing of polymers, including elastomers, is an undesirable but inevitable process leading to a limited lifetime of rubber products such as seals. Independent of the application, as e.g. in automotive, piping or container applications, a long lifetime or at least a timely exchange of a seal before occurrence of critical failure is desired. In order to investigate the degradation of material properties and to determine the lifetime of elastomers used as seals, an ageing programme was started with hydrogenated acrylonitrile butadiene rubber (HNBR), ethylene propylene diene rubber (EPDM) and fluorocarbon rubber (FKM) [1-3]. Both O-ring seals (uncompressed and compressed by 25 %) with a cord diameter of 10 mm as well as sheets with a thickness of 2 mm were aged at 75 °C, 100 °C, 125 °C and 150 °C for up to two years. The changes of material properties during ageing were characterised for each material using samples from the sheets by means of e.g. Dynamic Mechanical Analysis and tensile tests, while sealing properties such as leakage rate were determined on O-rings. The experimental results indicate that while material properties show considerable degradation effects, the static leakage rate stays constant or even decreases before failure occurs quite suddenly at advanced degradation levels. This reveals that static leakage rate has only limited sensitivity for the degradation of the seal material. Our approach to determine a suitable end of lifetime criterion, which involves a partial decompression of the seal during the leakage test, is presented and discussed. T2 - RubberCon 2017 CY - Prague, Czech Republic DA - 23.05.2017 KW - Life time prediction KW - Ageing KW - Rubber seal KW - Leakage PY - 2017 SN - 978-80-906662-0-7 SP - 65 EP - 72 AN - OPUS4-40391 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grelle, Tobias A1 - Probst, Ulrich A1 - Wolff, Dietmar A1 - Jaunich, Matthias A1 - Völzke, Holger T1 - Investigations on the long-term behavior of metal seals for dual purpose casks N2 - In Germany, spent nuclear fuel and high active waste from reprocessing is stored in transport and storage containers with double lid systems that are equipped with metal seals completing the primary sealing barrier. The tasks of the Bundesanstalt für Materialforschung und -prüfung (BAM) within the interim storage licensing procedures ruled by the German Atomic Energy Act include the long-term safety evaluation of the container design regarding the permanently safe enclosure of the inventory. In order to generate a knowledge base for the safety evaluation, research regarding the long-term behavior of the critical components is performed. So far, the containers are licensed for an interim storage period of 40 years. However, due to significant delays in establishing a final repository, the required time span for interim storage is expected to increase significantly. Thus, a widespread investigation program is run to gain systematic data on the long-term behavior of the seals and to develop prediction models. Long-term seal investigations consider the development of their restoring seal force, their useable resilience and their achievable leakage rate caused by aging at temperatures ranging from room temperature up to 150 °C. This year, the total time span of the tests reaches 10 years. Furthermore, seal segments are aged at the selected temperatures for up to 300 days. From these segments additional information on the sealing behavior, changes of the seal contact and the material behavior is gained. This contribution deals with the current results of the long-term seal investigations at BAM. Furthermore, insights of the more in-depth component and material investigations of the metal seals with focus on the seal contact development are discussed and the ongoing work aiming for an analytical description of the thermo-mechanical aging effects on metal seals are presented. T2 - 19th International Symposium on the Packaging and Transportation of Radioactive Materials PATRAM 2019 CY - New Orleans, LA, USA DA - 04.08.2019 KW - Metal seal KW - Radioactive waste containers KW - Creep KW - Long-term behaviour PY - 2019 SP - 1 EP - 6 AN - OPUS4-49019 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kotschate, Daniel A1 - Gohlke, Dirk A1 - Dobrovolskij, P. A1 - Vrana, J. A1 - Heckel, Thomas T1 - Herausforderungen bei der Prüfung von Schmiedeteilen durch Vorsatzkeile für Longitudinalwellenprüfköpfe N2 - Trotz moderner Sensortechnologien und Rekonstruktionsmethoden, findet die manuelle und automatisierte Ultraschallprüfung durch konventionelle Senkrecht- und Winkelprüfköpfe vielfach industriellen Einsatz. Um einen flexiblen Prüfeinsatz und die Prüfbarkeit von einfachen sowie komplexen Geometrien zu gewährleisten, werden dort oftmals Vorlaufkeile für die Winkelprüfung mit Longitudinalwellen angewendet um eine Anzeigenschräglage und deren Reflektivität auszugleichen bzw. zu verbessern. Durch den unterschiedlichen Aufbau, im Vergleich zu integrierten Scherwellen-Winkelprüfköpfen, können jedoch während der Prüfung Fehlanzeigen generiert werden. Diese fehlerhaften Anzeigen beruhen auf Mehrfachreflexionen und Wellenumwandlungen innerhalb des Vorlaufkeils, aufgrund der Geometrie und können im Feld nur bedingt von realen Anzeigen unterschieden werden. Dieser Beitrag zeigt die geometrische Betrachtung bei der Verwendung von Vorlaufkeilen und wurde experimentell durch die Bestimmung der Richtcharakteristik und dem Einsatz von elektrodynamischen Sonden validiert. Des Weiteren ermöglichen die so gewonnenen Abhängigkeiten einen vom Keilwinkel abhängigen Verstärkungsausgleich und somit eine korrekte Größenbestimmung durch einen geeigneten Vergleichsfehler. T2 - DACH-Jahrestagung 2019 CY - Friedrichshafen, Germany DA - 27.05.2019 KW - Richtcharakteristik KW - Vorlaufkeile KW - Mehrfachreflexion PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-480999 VL - 2019 SP - 1 EP - 7 PB - DGZfP Deutsche Gesellschaft für Zerstörungsfreie Prüfung AN - OPUS4-48099 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mirtsch, Mona A1 - Blind, K. ED - Jacobs, K. ED - Morone, P. T1 - Exploring the Diffusion of an ISMS Standard N2 - This paper introduces and discusses the applicability of Web Mining of Firm Websites to explore the Diffusion of Management System Standards using the example of an ISMS Standard. T2 - EURAS Conference CY - Rome, Italy DA - 13.06.2019 KW - Management System Standard KW - Information Security KW - Web Mining PY - 2019 SN - 978-3-95886-282-1 VL - 24 SP - 329 EP - 348 PB - Verlagshaus Mainz GmbH CY - Aachen, Germany AN - OPUS4-49031 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maurino, V. A1 - Pellutiè, L. A1 - Pellegrino, F. A1 - Ortel, Erik A1 - Hodoroaba, Vasile-Dan A1 - Isopescu, R. T1 - Synthesis of size and shape controlled TiO2 nanoparticles: possible CRM’s candidates for size, shape and functional properties N2 - Titanium dioxide is one of the most studied metal oxides due to its chemical, surface, electronic and (photo)catalytic properties, providing this material of multisectorial applications ranging from healthcare, photocatalysis, smart materials with self cleaning and self sterilizing properties and solar energy harvesting. However it is difficult to correlate the functional properties of TiO2 nanomaterials to the properties at single nanoparticle level due to the high polydispersity in shape, size and surface features of the currently available TiO2 nanoparticles (NPs). Although intensive experimental and theoretical studies have been conducted on the reactivity of different surfaces of metal oxides such as TiO2 much less attention is paid on the dependence of functional properties, like photocatalytic activity, dye adsorption, open circuit potential and fill factor in dye sensitized solar cells, on crystal facets in different orientations. One of the goal of SETNanoMetro project was the development of design rules to tune crystal facets of TiO2 NPs in order to optimize and control functional properties. In the present work we have developed a series of design rules in order to obtain sets of anatase TiO2 NPs with low polydispersity and to tune their shape and size by hydrothermal processing of Ti(IV)- Triethanolamine complex in presence of different shape controllers. Through a careful experimental design, a predictive soft model was developed. The model is able to predict the synthesis outcome allowing to tune the shape factor from 5 (prisms) to 1.5 (bipyramids) to 0.2 (platelets). This allows to control the main crystal facets exposed ranging from (100) to (001). Due to the dependence of functional properties of nanomaterials on shape distribution and not only size, the availability of NPs sets with uniform and well defined and tunable shapes can be of paramount relevance in order to produce reference nanomaterials for shape measurement. T2 - NanoWorkshop 2018: Workshop on Reference Nanomaterials CY - Berlin, Germany DA - 14.05.2018 KW - Anatase KW - shape control KW - Hydrothermal synthesis PY - 2019 SN - 978-3-95606-440-1 SN - 0179-0609 VL - F-61 SP - 146 EP - 162 PB - Physikalisch-Technische Bundesanstalt CY - Braunschweig und Berlin AN - OPUS4-49993 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Devi, Sarita A1 - Riedel, Soraya A1 - Döring, Sarah A1 - Hiller, Lukas A1 - Flemig, Sabine A1 - Singh, Chandan A1 - Konthur, Zoltán A1 - Hodoroaba, Vasile-Dan A1 - Schneider, Rudolf T1 - Antibodies Functionalized Magnetic Fe-Metal-Organic Framework Based Biosensor for Electrochemical Detection of Tetanus NeuroToxin N2 - This work presents a MOF-integrated microfluidic flow-cell based immunodetection of the tetanus toxoid (TT) using electrochemical technique for the first time. Metal-organic frameworks (MOFs) are coordination polymers, and composed of a metal center and organic linkers. Several synthesis methods have been reported to achieve the desired properties in MOFs. In this work, we report the hydrothermal synthesis of a magnetic and conductive iron-based MOF (Fe-MOF) which was utilized to develop a biosensor in conjugation with the human monoclonal antibody SA13 against TT (anti-TT mAb) for the detection of the tetanus neurotoxin (TeNT). The one-pot synthesis of this magnetic and conductive Fe-MOF was performed in a hydrothermal reactor (108℃) using the Fe3+/Fe2+ precursors as 1.2/1 mmol and dual ligands, i.e., tetrahydroxy-1,4-benzoquinone and 2-aminobenzene-1,4-dicarboxylic acid. The Fe-MOF was characterized using XRD, DLS, FTIR, and electron microscopy. The Fe-MOF was further conjugated with L-phenylalanine (pH 8.6) to increase the electric conductivity of the Fe-MOF (Fe-MOF/Phe) on the screen-printed gold electrode as studied by cyclic voltammetry (CV). The anti-TT mAb was conjugated on the Fe-MOF/Phe surface with the help of ethylenediamine (Fe-MOF/Phe/EDA/anti-TT mAb) delivered good binding affinity for the TT antigen revealing the applicability of this biosensor for TT detection by CV. The limit of detection of the Fe-MOF/Phe/EDA/anti-TT mAb-based biosensor for TT was 9.4 ng/ml in spiked buffer. There is negligible cross-reactivity in the presence of bovine serum albumin. This study shows the applicability of magnetic MOFs in the detection of various other microbial toxins or other biomolecules. KW - Magnetic Metal-Organic Framework KW - Tetanus toxoid KW - L-phenylalanine KW - Antibody KW - Label-free detection KW - Electrochemical immunosensor PY - 2024 DO - https://doi.org/10.2139/ssrn.4935745 SP - 1 EP - 48 PB - Elsevier Inc. AN - OPUS4-62196 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hülagü, Deniz A1 - Tobias, Charlie A1 - Dao, R. A1 - Komarow, P. A1 - Rurack, Knut A1 - Hodoroaba, Vasile-Dan T1 - Dataset accompanying the publication "Towards 3D determination of the surface roughness of core-shell microparticles as a routine quality control procedure by scanning electron microscopy" N2 - This dataset accompanies the following publication: Hülagü, D., Tobias, C., Dao, R., Komarov, P., Rurack, K., Hodoroaba, V.-D., Towards 3D determination of the surface roughness of core-shell microparticles as a routine quality control procedure by scanning electron microscopy. Sci.Rep, 14, 17936 (2024), https://doi.org/10.1038/s41598-024-68797-7. It contains SEM and AFM-in-SEM images of polystyrene (PS) core particles, polystyrene-iron oxide (PS/Fe3O4) core-shell particles, and polystyrene-iron oxide-silica (PS/Fe3O4/SiO2) core-shell-shell particles. Please refer to the publication and its supporting information for more details on the acquisition and contents of the dataset, as well as the GitHub repository at https://github.Com/denizhulagu/roughness-analysis-by-electron-microscopy. The investigated particles were produced at BAM laboratories as previously described in: Hülagü, D. et al. Generalized analysis approach of the profile roughness by electron microscopy with the example of hierarchically grown polystyrene–iron oxide–silica core–shell–shell particles. Adv. Eng. Mater. 24, 2101344, https://doi.org/10.1002/adem.202101344 (2022). Tobias, C., Climent, E., Gawlitza, K. & Rurack, K. Polystyrene microparticles with convergently grown mesoporous silica shells as a promising tool for multiplexed bioanalytical assays. ACS Appl. Mater. Interfaces 13, 207, https://dx.doi.org/10.1021/acsami.0c17940 (2020). KW - Core–shell particles KW - Image analysis KW - Roughness KW - Scanning electron microscopy KW - Atomic force microscopy KW - Tilting KW - Batch analysis PY - 2024 UR - https://zenodo.org/records/11108726 DO - https://doi.org/10.5281/zenodo.11108725 PB - Zenodo CY - Geneva AN - OPUS4-60760 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schwirn, K. A1 - Völker, D. A1 - Ahtianinen, J. A1 - Schmidt, Alexandra A1 - Bresch, Harald A1 - Kämpf, K. A1 - Bachmann, V. A1 - Kuhlbusch, T. ED - Bosse, H. ED - Buhr, E. ED - Dziomba, T. ED - Hodoroaba, Vasile-Dan ED - Klein, T. ED - Krumrey, M. T1 - OECD Test Guidelines development for chemicals safety assessment of nanomaterials N2 - The OECD test guidelines (TGs) for testing chemicals have been widely used for regulatory purposes all over the world since the establishment of the Mutual Acceptance of Data (MAD) principle in 1984. This MAD principle ensures that, if a chemical is tested under the Good Laboratory Practice (GLP) conditions accordingly to an OECD TG, the data should be accepted in all OECD countries. The TGs have been developed, harmonized, internationally validated (round robin tests) and adopted by OECD countries to be used for the physical-chemical characterisation, fate estimation, and hazard identification for risk assessment of various chemicals. In addition to the TGs, OECD Guidance Documents (GDs) usually provide guidance on how to use TGs and how to interpret the results. These GDs do not have to be fully experimentally validated, and hence they are not under MAD, but they are based on relevant published scientific research. But are the existing TGs and the related GDs applicable and adequate for the regulatory testing of nanomaterials? In general, for nanomaterials it is accepted that most of the "endpoints" or more precisely measurement variables are applicable. However, for some endpoints new or amended TGs are needed. In addition, several GDs are needed to give more precise advice on the test performance in order to gain regulatory relevant data on nanomaterials. T2 - NanoWorkshop 2018: Workshop on Reference Nanomaterials CY - Berlin, Germany DA - 14.05.2018 KW - OECD KW - Nano KW - Guideline KW - Nanomaterials KW - Prüfrichtlinie PY - 2019 SN - 978-3-95606-440-1 DO - https://doi.org/10.7795/110.20190412 SN - 0179-0609 VL - F-61 SP - 279 EP - 279 PB - Physikalisch-Technische Bundesanstalt CY - Braunschweig und Berlin AN - OPUS4-49515 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Knigge, Xenia A1 - Radnik, Jörg T1 - Physico-chemical characterization of sterilized Ce0.25Zr0.75O2 nanoparticles by XPS / HAXPES / SEM N2 - Here a dataset of XPS, HAXPES and SEM measurements for the physico-chemical characterization of sterilized Ce0.25Zr0.75O2 nanoparticles is presented. The measurements are part of the H2020 project “NanoSolveIT”. KW - XPS KW - HAXPES KW - SEM KW - NanoSolveIT KW - Ce0.25Zr0.75O2 nanoparticles PY - 2023 DO - https://doi.org/10.5281/zenodo.7966165 PB - Zenodo CY - Geneva AN - OPUS4-57674 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Knigge, Xenia A1 - Radnik, Jörg T1 - Physico-chemical characterization of sterilized Co1.5Fe1.5O4 nanoparticles by XPS / HAXPES / SEM N2 - Here a dataset of XPS, HAXPES and SEM measurements for the physico-chemical characterization of sterilized Co1.5Fe1.5O4 nanoparticles is presented. The measurements are part of the H2020 project “NanoSolveIT”. KW - XPS KW - HAXPES KW - SEM KW - NanoSolveIT KW - Co1.5Fe1.5O4 nanoparticles PY - 2023 DO - https://doi.org/10.5281/zenodo.7940271 PB - Zenodo CY - Geneva AN - OPUS4-57662 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Knigge, Xenia A1 - Radnik, Jörg T1 - Physico-chemical characterization of sterilized TiO2 nanoparticles by XPS / HAXPES / SEM N2 - Here a dataset of XPS, HAXPES and SEM measurements for the physico-chemical characterization of sterilized TiO2 nanoparticles is presented. The measurements are part of the H2020 project “NanoSolveIT”. KW - XPS KW - HAXPES KW - SEM KW - NanoSolveIT KW - TiO2 nanoparticles PY - 2023 DO - https://doi.org/10.5281/zenodo.7941566 PB - Zenodo CY - Geneva AN - OPUS4-57668 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Knigge, Xenia A1 - Radnik, Jörg T1 - Physico-chemical characterization of sterilized TiO2 PVP nanoparticles by XPS / HAXPES / SEM N2 - Here a dataset of XPS, HAXPES and SEM measurements for the physico-chemical characterization of sterilized TiO2 PVP nanoparticles is presented. The measurements are part of the H2020 project “NanoSolveIT”. KW - HAXPES KW - XPS KW - SEM KW - Nanoparticles KW - TiO2 PVP PY - 2023 DO - https://doi.org/10.5281/zenodo.7966354 PB - Zenodo CY - Geneva AN - OPUS4-57761 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Knigge, Xenia A1 - Radnik, Jörg T1 - Physico-chemical characterization of sterile ZnO nanoparticles by XPS / HAXPES / SEM N2 - Here a dataset of XPS, HAXPES and SEM measurements for the physico-chemical characterization of ZnO nanoparticles is presented. The measurements are part of the H2020 project “NanoSolveIT”. KW - HAXPES KW - XPS KW - SEM KW - Nanoparticles KW - ZnO PY - 2023 DO - https://doi.org/10.5281/zenodo.7990213 PB - Zenodo CY - Geneva AN - OPUS4-57762 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Knigge, Xenia A1 - Radnik, Jörg T1 - Physico-chemical characterization of Ce0.9Zr0.1O2 nanoparticles by XPS / HAXPES / SEM N2 - Here a dataset of XPS, HAXPES and SEM measurements for the physico-chemical characterization of Ce0.9Zr0.1O2 nanoparticles is presented. The measurements are part of the H2020 project “NanoSolveIT”. KW - HAXPES KW - XPS KW - SEM KW - Ce0.9Zr0.1O2 KW - Nanoparticles PY - 2023 DO - https://doi.org/10.5281/zenodo.7986672 PB - Zenodo CY - Geneva AN - OPUS4-57758 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Knigge, Xenia A1 - Radnik, Jörg T1 - Physico-chemical characterization of sterile citrated stabilized Au nanoparticles by XPS / HAXPES / SEM N2 - Here a dataset of XPS, HAXPES and SEM measurements for the physico-chemical characterization of Au nanoparticles is presented. The measurements are part of the H2020 project “NanoSolveIT”. KW - HAXPES KW - XPS KW - SEM KW - Au Nanoparticles KW - NanoSolveIT PY - 2023 DO - https://doi.org/10.5281/zenodo.7990250 PB - Zenodo CY - Geneva AN - OPUS4-57763 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Mike A1 - Kömmling, Anja A1 - Jaunich, Matthias A1 - Wolff, Dietmar A1 - Zencker, Uwe A1 - Völzke, Holger A1 - Schulze, Dietmar A1 - Probst, Ulrich T1 - Testing and Numerical Simulation of Elastomers - From Specimen Tests to Simulation of Seal Behavior under Assembly Conditions N2 - Due to delays in the siting procedure to establish a deep geological repository for spent nuclear fuel and high level radioactive waste as well as in construction of the already licensed Konrad repository for low and intermediate level radioactive waste, extended periods of interim storage become more relevant in Germany. BAM is involved in most of the cask licensing procedures and especially responsible for the evaluation of cask-related long-term safety issues. The long-term performance of elastomer seals for lid systems of transport and storage casks, whether used as auxiliary seals in spent fuel casks or as primary seals for low and intermediate level waste packages, is an important issue in this context. The polymeric structure of these seals causes a complex mechanical behavior with time-dependent sealing force reduction. The results of a comprehensive purpose-designed test program consisting of basic compression and tension tests as well as relaxation tests on unaged specimens of representative types of elastomers (fluorocarbon rubber (FKM) and ethylene propylene diene rubber (EPDM)) at different temperatures and strain rates are presented. They were used to identify the constitutive behavior and to obtain parameters for finite element material models provided by the computer code ABAQUS®. After estimating the influence of uncertainties such as Poisson’s ratio and friction coefficient by sensitivity analyses, the chosen parameters had to prove their suitability for the finite element simulation of the specimen tests themselves. Based on this preliminary work the simulation of a specific laboratory test configuration containing a typical elastomer seal with circular cross section is presented. The chosen finite element material model and the implemented parameters had to show that they are able to represent not only the specimen behavior under predominantly uniaxial load but also the more complex stress states in real components. Deviations between the measured and calculated results are pointed out and discussed. For the consideration of long-term effects in the simulation of elastomer behavior, test results of aged specimens are needed. First information about a new test program, started recently and planned to provide these data, are given. T2 - ASME 2017 Pressure Vessels & Piping Conference (PVP2017) CY - Waikoloa, Hawaii, USA DA - 16.07.2017 KW - Time dependent effects KW - Low temperature behavior KW - Elastomeric seals KW - Aging KW - Simulation KW - Testing PY - 2017 SN - 978-0-7918-5802-8 VL - 7 SP - Article UNSP V007T07A035, 1 EP - 8 AN - OPUS4-41841 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stark, Wolfgang A1 - Jaunich, Matthias T1 - Thermoanalytische Charakterisierung von Ethylen-Vinylacetat-Copolymer (EVA) für Photovoltaikmodule N2 - Das Ziel der Untersuchungen war mit Hilfe von DSC und DMA EVA-Folien im Anlieferungszustand hinsichtlich der Lage der Glasübergangstemperatur, des Schmelzverhaltens und der Temperaturabhängigkeit der Vernetzungsreaktion zu charakterisieren. Auf dieser Basis sollte die Lieferstabilität im Sinne einer Wareneingangskontrolle auf eine messtechnische Basis gestellt werden. In einem 2. Schritt sollte die vernetzte Folie dahingehend charakterisiert werden, ob infolge der Vernetzung eine Änderung der KW - Photovoltaik KW - Klebfolie KW - EVA KW - DSC KW - DMA PY - 2011 VL - 8 SP - 3 EP - 5 AN - OPUS4-24168 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - López de Ipina, J.-M. A1 - Arevalillo, A. A1 - Martín, A. A1 - Caillard, B. A1 - Marcoulaki, E. A1 - Aguerre- Charol, O. A1 - van Duuren-Stuurman, B. A1 - Hodoroaba, Vasile-Dan A1 - Viitanen, A.-K. A1 - Witters, H. A1 - Vercauteren, S. A1 - Persson, K. A1 - Bard, D. A1 - Evans, G. A1 - Jensen, K.A. A1 - Himly, M. A1 - Scalbi, S. A1 - Papin, A. A1 - Le Bihan, O. A1 - Kanerva, T. A1 - Tirez, K. A1 - Frijns, E. A1 - Niga, P. A1 - Eleftheriadis, K. A1 - Travlos, A. A1 - Geppert, M. A1 - Himly, M. A1 - Radnik, Jörg A1 - Kuchenbecker, Petra A1 - Resch-Genger, Ute A1 - Fraboulet, I. A1 - Bressot, C. A1 - Rissler, J. A1 - Gaucher, R. A1 - Binotto, G. A1 - Krietsch, Arne A1 - Braun, A. A1 - Abenet, S. A1 - Catalan, J. A1 - Verstraelen, S. A1 - Manier, N. A1 - Manzo, S. A1 - Fransman, S. A1 - Queron, J. A1 - Charpentier, D. A1 - Taxell, D. A1 - Säämänen, A. A1 - Brignon, J.-M. A1 - Jovanovic, A. A1 - Bisson, M A1 - Neofytou, P. T1 - EC4Safenano - Catalogue of Services N2 - The publicly available document encapsulates the first version of the Catalogue of Services of the future EC4Safenano Centre (CoS 2019). The CoS 2019 is structured in 12 Service Categories and 27 Service Topics, for each of the 12 categories considered. This architecture configures a 12 x 27 matrix that allows ordering the potential EC4Safenano offer in 324 types of services/groups of services. Each type of service/group of services is described, in a simple and friendly way, by means of a specific service sheet: the EC4Safenano - Service Data Sheet (EC4-SDS). These EC4-SDSs allow structuring and summarizing the information of each service, providing the customer with a concise view of characteristics of the service and also the contact details with the service provider. The CoS 2019 deploys a map of services consisting of a set of 100 EC4-SDSs, covering 7 of the 12 Service Categories and 17 of the 27 Service Topics. The harmonization of services is visualized as a future necessary step in EC4Safenano, in order to strengthen the offer and provide added value to customers with a growing offer of harmonized services in future versions of the CoS. The information contained in this document is structured in 3 main sections, as follows: • Catalogue structure. This section describes in short the main characteristics of the CoS 2019. • Catalogue content. This section represents the core part of the document and encapsulates the set of 100 SDSs displaying the offer proposed by the CoS 2019. • Online Catalogue. This section describes the resources implemented by EC4Safenano to facilitate the on-line consultation of the CoS 2019 by customers and other interested parties. KW - Nano-safety KW - Analytical services KW - Nanomaterials KW - Catalogue of services KW - EC4SafeNano KW - European Centre PY - 2021 UR - https://ec4safenano.eu-vri.eu/Public/Guidance SP - 1 EP - 72 PB - EU-VRi – European Virtual Institute for Integrated Risk Management CY - Stuttgart, Germany AN - OPUS4-52943 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zaghdoudi, Maha A1 - Weber, Mike A1 - Kömmling, Anja A1 - Jaunich, Matthias A1 - Wolff, Dietmar T1 - Numerical Modelling of Compression Stress Relaxation and Compression Set of Elastomer O-Ring During Aging N2 - Elastomer seals are used in many industrial applications due to their excellent mechanical properties at a wide range of temperatures. Their high versatility and recovery potential under several load conditions make them well suitable for the application in containers designed for transport, storage and/or disposal of radioactive materials. In containers for low and intermediate level radioactive waste, elastomer seals are used as barrier seals, and as auxiliary seals in storage and transportation casks (dual purpose casks) for heat generating radioactive waste, such as spent fuel and high-level waste. While a seal exchange at defined intervals is typical in many conventional applications, it is impossible or at least hard to perform when principles of minimization of radiation exposure have to be considered and prohibit an unnecessary cask handling. An extensive knowledge of the change of the elastomer’s properties during aging and the availability of reliable end-of-lifetime criteria to guarantee the permanent safe enclosure of the radioactive material is mandatory. As BAM is involved in most of the national cask licensing procedures and in the evaluation of cask-related long-term safety issues, great efforts have been already made and are still planned to scientifically support this task. Compression stress relaxation and compression set were identified as key indicators of elastomer long-term performance and quantitatively investigated in comprehensive test programs. Among other representative types of elastomers, specimens made from ethylene propylene diene rubber (EPDM) were tested before, during and after aging to capture the most important of their complex mechanical properties. In the presented study, exemplary results were used to simulate the compression stress relaxation and the compression set of elastomer O-rings during aging. Regarding the influence of temperature, the time-temperature superposition principle is applied in the relaxation analysis of elastomer O-rings. The proposed model is implemented in the commercial finite element software ABAQUS/Standard® [1] with a sequential temperature displacement coupling. Numerical results match the experimental compression stress relaxation measurements well. The prediction of compression set values after long-term aging shows a relatively good agreement with the experimental results. Nevertheless, all input parameters derived from the specimen tests, additional assumptions concerning boundary conditions and modeling strategy are discussed with regard to the identified slight discrepancies. The possibility to extend the finite element model to represent the O-ring seal’s ability to recover after a (fast) partial release is taken into account. T2 - ASME 2020 Pressure Vessels & Piping Conference (PVP2020) CY - Online meeting DA - 03.08.2020 KW - Compression Set KW - O-ring KW - Simulation KW - Sequential analysis KW - Ageing KW - stress relaxation PY - 2020 SN - 978-0-7918-8388-4 DO - https://doi.org/10.1115/PVP2020-21270 SP - PVP2020-21270 PB - ASME AN - OPUS4-51490 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Subramani Bhagavatheswaran, E. A1 - Wießner, S. A1 - Jaunich, Matthias A1 - Wolff, Dietmar T1 - Einfluss der Alterung auf dichtungsrelevante Eigenschaften von FKM-, VMQ- und EPDM-Elastomeren N2 - Da Elastomere in vielfältigen Dichtungsanwendungen eingesetzt werden und dabei teilweise großen Einfluss auf die Funktionsfähigkeit und Sicherheit haben, ist der Einfluss der Alterung auf dichtungsrelevante Eigenschaften relevant. Eine strukturierte Untersuchung des Einflusses von verschiedenen Mischungsrezepturen auf die Bauteileigenschaften, das Alterungsverhalten und die Funktion wird vorgestellt. T2 - Technomer 2017 CY - Chemnitz, Germany DA - 09.11.2017 KW - Dichtung KW - Alterung KW - Struktur-Eigenschaftsbeziehung KW - Elastomer PY - 2017 SN - 978-3-939382-13-3 VL - 2017 SP - 41 EP - 41 AN - OPUS4-42844 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias A1 - Wolff, Dietmar T1 - Untersuchungen an Elastomerdichtungen - Tieftemperatur und Alterung N2 - Ziel unserer Arbeit ist es, den sicheren Einschluss von gefährlichen Gütern in entsprechenden Verpackungen (z.B. Behälter für radioaktive Stoffe) unter verschiedenen Umgebungsbedingungen und über lange Zeiten sicher zu stellen bzw. die Materialauswahl entsprechend zu steuern. Aufgrund ihrer einfachen und zuverlässigen Anwendung werden Elastomere für viele Dichtungsaufgaben eingesetzt. In vielen Anwendungsbereichen wie z.B. Verkehr, Luftfahrt und Verfahrenstechnik können während des Einsatzes tiefe Temperaturen auftreten, bei denen die Funktionsfähigkeit der Dichtung erhalten bleiben muss. Daher ist die Untersuchung des Verhaltens von Elastomerdichtungen bei tiefen Temperaturen wichtig, um ihren Temperatureinsatzbereich nach unten abzugrenzen und dadurch einen verlässlichen Betrieb zu sichern. Dazu wurden umfangreiche Untersuchungen durchgeführt, auf deren Ergebnisse hier kurz eingegangen werden soll. Bei allen Anwendungen ist die Frage nach der Lebenszeit einer Dichtung entscheidend für z.B. Austauschintervalle oder Wartung. Besondere Bedeutung hat die Lebensdauer allerdings bei Anwendungen, in denen ein Austausch der Dichtung nicht möglich ist. Hier kann die Dichtung über die Lebensdauer des Gesamtsystems entscheiden. Daher ist eine verlässliche Abschätzung der Lebensdauer für diese Anwendungen relevant. Dazu ist eine umfangreiche Datenbasis erforderlich. Entsprechende Arbeiten, die gerade begonnenen worden sind, sollen ergänzend vorgestellt werden. Erste konkrete Ergebnisse werden im Vortrag vorgestellt. T2 - PolyMerTec 14 CY - Merseburg, Germany DA - 25.06.2014 PY - 2014 SP - 313 EP - 318 AN - OPUS4-32151 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Rauscher, H. A1 - Mech, A. A1 - Gaillard, C. A1 - Stintz, M. A1 - Wohlleben, W. A1 - Weigel, St. A1 - Ghanem, A. A1 - Hodoroaba, Vasile-Dan A1 - Babick, F. A1 - Mielke, Johannes T1 - Recommendations on a Revision of the EC Definition of Nanomaterial Based on Analytical Possibilities N2 - In October 2011 the European Commission (EC) published a "Recommendation on the definition of nanomaterial" (2011/696/EU), to promote consistency in the interpretation of the term "nanomaterial" for legislative and policy purposes in the EU. The EC NM Definition includes a commitment to its review in the light of experience and of scientific and technological developments. This review is ongoing in 2015 and as a contribution to the review the Joint Research Centre of the European Commission (JRC) has already developed a series of three scientific-technical reports with the title: “Towards a review of the EC Recommendation for a definition of the term nanomaterial” which provides to the EC policy services science-based options on how the definition could be revised or supported with additional guidance. The overarching nature and wide scope of the EC NM Definition, as it does not exclude a priori any particulate material regardless the state, form and size, creates many analytical challenges in its imple-mentation for all stakeholders, including enterprises and regulators. The NanoDefine project has as core objective to support the implementation of the EC NM Definition. In this report key aspects of the EC NM Definition are addressed, with the goal to improve the implement-ability of the EC NM Definition. These aspects are presented and discussed based on the results of two years of research performed within the framework of the project. As a result this report assesses how well the requirements of the EC NM Definition can be fulfilled with currently available analytical possi-bilities. It presents recommendations and options on a revision of the EC NM Definition to improve the implementability of the definition based on currently available analytical possibilities, according to the state of the art of mid-2015. Of the technical issues considered in this report, the following seem to deserve the most attention in terms of clarification of the definition and/or provision of additional implementation guidance:  The term ‘external dimension’. A clear definition of 'External dimension' should be included in the text of the EC NM definition and more precise guidance on what is considered as an external dimension and how to properly character-ise it should be provided.  The ‘number based particle size distribution‘. The EC NM Definition uses a threshold related to the number based size distribution of particles. Yet most of the easily available techniques provide a mass-, volume- or scattered light intensity-based size distribution which needs to be converted into a number based distribution to be used for regulatory pur-poses. A specific guidance on the conditions under which these methods can be used to identify a na-nomaterial by employing appropriate quantity or metrics conversion should be provided.  The ‘polydispersity‘ and ‘upper size limit‘ Polydispersity is a challenge for the measurement of particle size distribution for the EC NM definition, specifically for materials with high polydispersity index and broad size distribution especially when the volume or mass of the fraction containing particles below 100 nm is very small. Therefore a dedicated guidance should be provided that allows applying an upper size limit in measurements and particle statistics. KW - Nanomaterial KW - EU Definition of nanomaterial KW - Nanoparticles PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-432339 UR - http://www.nanodefine.eu/publications/reports/NanoDefine_TechnicalReport_D7.10.pdf SP - 1 EP - 68 PB - The NanoDefine Consortium CY - Wageningen, The Netherlands AN - OPUS4-43233 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias A1 - Weber, Mike A1 - Kömmling, Anja A1 - Zencker, Uwe A1 - Wolff, Dietmar A1 - Völzke, Holger T1 - Performance of elastomer seals in transport and storage casks N2 - Elastomer seals are widely used as barrier seals in containers for low and intermediate level radioactive waste and for spent fuel transportation casks. In addition, they are also used for spent fuel storage and transportation casks (dual purpose casks (DPC)) as auxiliary seals to allow leakage rate measurements of metal barrier seals for demonstration of their proper assembling conditions. Depending on the area of use, the rubber materials have to demonstrate proper sealing performance with regard to mechanical, thermal, and environmental conditions as well as irradiation during the entire operation period. Concerning DPC, degradation effects should be limited in a way that, for example, effects from potentially released decomposition elements may not harm e.g. metal barrier seals. Leakage rate measurements should be possible also after long interim storage periods prior to subsequent transportation. Because of the complex requirements resulting from the various applications of containers for radioactive waste and spent nuclear fuel, BAM has initiated several test programmes for investigating the behaviour of elastomer seals. In this contribution the current status is described and first results are discussed. T2 - International conference on management of spent fuel from nuclear power reactors: An integrated approach to the back end of the fuel cycle CY - Vienna, Austria DA - 15.06.2015 KW - Ageing KW - Elastomer KW - Glass-rubber transition KW - Irradiation KW - Material model PY - 2015 SP - 1 EP - 8 AN - OPUS4-33553 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kömmling, Anja A1 - Jaunich, Matthias A1 - Wolff, Dietmar T1 - Ageing and lifetime prediction of O-ring seals made of HNBR, EPDM and FKM N2 - BAM is the federal institute for materials research and testing in Germany. One of our tasks is to evaluate the safety of casks designed for transport and/or storage of radioactive waste. As elastomeric seals are used in the containers as safety-relevant parts, it is our goal to be able to evaluate the service lifetime of the seals with regard to the requirements for long-term safety (40 years and more) of the containers. For this reason, an accelerated ageing programme with selected rubbers often used for seals (HNBR, EPDM and FKM) was started. Ageing was performed at four different temperatures (75 °C, 100 °C, 125 °C and 150 °C) for up to 2 years. For assessing properties related to the sealability, O-rings were aged in compression by 25 % (corresponding to the compression during service) between plates. For comparison, uncompressed O-rings were aged as well. The aged materials were characterized with conventional polymer analysis methods such as hardness and tensile tests, but also with more seal-specific methods such as compression stress relaxation (CSR, reflecting the loss of sealing force of a compressed seal over time), and compression set (CS, representing the recovery behaviour of a seal after release from compression). CS is chosen as the property for lifetime prediction as it is both sensitive to degradation and related to the seal performance. CS data is extrapolated to 60 °C, which yields lifetimes of approximately 5 years for HNBR and 64 years for EPDM for a criterion of 85 % CS respectively, and approx. 40 years for FKM for a criterion of 65 % CS (the highest value measured so far). T2 - 12. Kautschuk Herbst Kolloquium CY - Hanover, Germany DA - 22.11.2016 KW - Rubber KW - Compression set KW - Extrapolation KW - Degradation PY - 2016 SN - 9783981407648 VL - 2016 AN - OPUS4-38483 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias A1 - Grelle, Tobias A1 - Wolff, Dietmar T1 - Investigation of elastomer seal behaviour for transport and storage packages N2 - According to the relevant guidelines and regulations, the safe enclosure of radioactive Container contents has to be guaranteed for long storage periods as well as down to temperatures of -40 °C during transportation. As rubbers are widely used as the main sealing materials for Containers for low- and intermediate-level radioactive waste and as additional component to metal seals in spent fuel and high active waste Containers, a comprehensive eiastomer investigation Programme is in place at BAM. This Programme comprises investigations of overall eiastomer performance, durability, influence of gamma irradiation and low temperature behaviour. In this paper we focus on the behaviour of eiastomer seals at low temperatures with regard to the potential increase in leakage as material properties of rubbers are strongly temperature-dependent. During continuous cooling, the material behaviour of elastomers changes in the rubber-glass transition temperature ränge from rubberlike entropy-elasticity to stiff energy-elasticity, allowing for almost no strain or retraction. Hence rubbers are normally used above their rubber-glass transition but the minimum limit at which they work has not been defined precisely. For the investigations, fluorocarbon (FKM) and ethylene-propylene-diene (EPDM) rubbers were selected, as they are often used in radioactive waste Containers. The elastomers were studied using several thermoanalytical methods and compression set. The results were compared with component tests to determine the temperature at which the sealing function of O-rings made of eiastomer breaks down. In addition to these results, under static conditions we designed a new measurement set-up which allows for a small deflection of the flange and simultaneous leakage rate measurement at low temperatures. T2 - RAMTRANS 2015 - 10th International conference on radioactive materials transport and storage CY - Oxford, UK DA - 19.05.2015 KW - O-ring KW - Glass-rubber transition KW - Irradiation KW - Compression set PY - 2015 SP - 1 EP - 10 AN - OPUS4-33489 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hoster, B. A1 - Jaunich, Matthias A1 - Stark, Wolfgang T1 - Monitoring of the vulcanisation process by ultrasound during injection moulding N2 - Today rubber is due to its unique property profile one of the most important materials for the production of bearings, dampers or also tires and tubes. In the production of rubber goods a chemical cross-linking reaction (vulcanisation) generates the final material properties. This process takes place during the shape giving of the rubber compound in the mould and can proceed for several minutes. The cross-linking process is influenced by the mixture of the basic polymer, the cross-linking agent, the influence of catalysts and inhibitors and especially the processing conditions. The quality of every ingredient, the reproducibility of the mixing ratio, the homogeneity of the mixture and the accurateness in temperature control can have a direct influence on the cross linking reaction. To control the quality of a rubber compound and verify the processing conditions in industry moving die rheometers, named curemeter, are involved in the production process. Starting from our experience in cure monitoring of thermosetting materials by measuring ultrasound velocity in the mould we extended the measuring principle to rubber vulcanisation monitoring. After first investigations using a compression mould we dealt here with on-line monitoring of vulcanisation in an injection moulding process which is one of the most used techniques in rubber industry. KW - Ultrasonic KW - Sound velocity KW - Vulcanisation KW - On-line monitoring KW - Injection moulding PY - 2009 UR - https://www.ndt.net/search/docs.php3?id=8042 SN - 1435-4934 VL - 14 IS - 9 SP - 1 EP - 9 PB - NDT.net CY - Kirchwald AN - OPUS4-19858 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grelle, Tobias A1 - Probst, Ulrich A1 - Jaunich, Matthias A1 - Skrotzki, Birgit A1 - Wolff, Dietmar T1 - Creep investigations on aluminum seals for application in radioactive waste containers N2 - In Germany spent nuclear fuel and high level radioactive waste is stored in interim storage containers with double lid systems. Those lids are equipped with metal seals (e.g. Helicoflex®) that ensure the safe enclosure of the inventory. The used metal seals consist of three components as can be seen in the cross-sectional view in Figure 1. The innermost part is a helical spring that is surrounded by an inner jacket made of stainless steel. The outer jacket that is made of a softer material which in case of assembly in the aforementioned storage containers is silver or aluminum (i.e. Al 99.5). During application the seal is compressed and due to the restoring force of the helical spring, the outer jacket is plastically deformed and adapts to the sealing surface. Hence, leakage paths are closed and the sealing function is generated. In Germany the above-mentioned containers are licensed for up to 40 years of interim storage, which in case extended storage becomes necessary before a final repository is available will have to be extended to even longer periods. Therefore, the evaluation of the long-term behavior of the seals is necessary, taking into account storage conditions, decay heat and possible mechanical loads as well. At Bundesanstalt für Materialforschung und –prüfung (BAM) long-term investigations are being conducted in which seals are assembled in test flanges and aged at temperatures ranging from room temperature to 150°C for accelerated aging. The aged seals are tested semi-annually (after the first 6 months in which the seals are tested more frequently) regarding the sealing performance, the remaining seal force, and the useable resilience upon decompression. Results of these investigations have been published over the past years (e.g. Grelle, Wolff, Probst, Jaunich, & Völzke, 2017; Völzke, Wolff, Probst, Nagelschmidt, & Schulz, 2014). It was found that the seal force and the useable resilience decrease with time and temperature, which is in agreement with the result of other studies (Sassoulas et al., 2006; Wataru et al., 2016) as well. Geometry change of the outer jacket has been identified as the main reason for this seal behavior. At the prevailing operating temperatures and stresses the aluminum is subjected to creep deformation leading to a thinning of the outer jacket. Since the seal groove depth remains unchanged the helical spring expands, which in turn leads to a decrease of the generated spring and seal force. Although the main reason for the change of seal parameters over time and temperature is known, a detailed characterization of the seal behavior and a reliable prediction of the parameter development for aging times that exceed the experimental time frame have not been possible, yet. For deeper understanding of the aging processes, an Investigation program, which is covered in this contribution, is conducted at Bundesanstalt für Materialforschung und –prüfung (BAM) that focusses on the behavior of the aluminum jacket and its influence on the long-term sealing performance. The program investigates properties of material samples as well as the behavior of the seal as a component. Original sheet material of the same aluminum that is used for manufacturing of the seals is investigated in compression creep tests. For this, a DMA (dynamic mechanical analysis) machine is employed (here used for static tests) that allows for a measurement of the specimens deformation under forces of up to 500 N. The advantage of this method is that the original material can be tested in the same shape as used for the seals which is 0.5 mm thick sheet material. For investigation of tensile creep standard specimens are used, that were machined from surrogate material of the same composition and annealing condition. Furthermore, aluminum seals that are cut into smaller segments are assembled in flanges and placed in heating chambers at temperatures ranging from 23°C to 150°C. After different periods of time from 3 days to 300 days the segments are taken out of the flanges and are investigated, thus giving information on different states of aging. Measurements of the development of the seal contact width and the aluminum jacket thickness are done with an optical microscope. Further investigations on the segments will include metallography and hardness measurements. From the detailed material and component behavior including the results of the long-term seal force and useable resilience investigations a better understanding of the overall seal behavior can be gained. The aim is to contribute to the development of material models and analytical approaches for the prediction of the sealing behavior in dependence of time and temperature. T2 - International Conference on Aluminum Alloys CY - Montreal, Canada DA - 17.06.2018 KW - Metal seal KW - Creep KW - Long-term behavior PY - 2018 SN - 978-1-926872-41-4 SP - 1 EP - 2 AN - OPUS4-45844 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Agudo Jácome, Leonardo A1 - Nolze, Gert A1 - Roohbakhshan, Farshad A1 - Fedelich, Bernard A1 - Olbricht, Jürgen A1 - Skrotzki, Birgit T1 - Cyclic operation performance of 9-12% Cr ferritic-martensitic steels part 2: Microstructural evolution during cyclic loading and its representation in a physically-based micromechanical model N2 - The current competitive situation on electricity markets forces conventional power plants into cyclic operation regimes with frequent load shifts and starts/shutdowns. In the present work, the cyclic mechanical behavior of ferritic-martensitic 9-12 % Cr steels under isothermal and thermomechanical loading was investigated for the example of grade P92 material. A continuous softening was observed under all loading conditions. The introduction of hold periods to the applied cycles reduced material lifetime, with most prominent effects at technologically relevant small strain levels. The microstructural characterization reveals a coarsening of the original “martensitic” lath-type microstructure to a structure with polygonal subgrains and reduced dislocation density. The microstructural data forms the input for a physically-based modelling approach. T2 - 45. MPA-Seminar CY - Leinfelden-Echterdingen, Germany DA - 01.10.2019 KW - Tempered Martensite Ferritic Steels KW - P92 KW - TEM KW - EBSD KW - Micromechanical model PY - 2019 SP - 80 EP - 85 PB - MPA (Materialprüfungsanstalt Universität Stuttgart) CY - Stuttgart AN - OPUS4-50052 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Bartczak, D. A1 - Hodoroaba, Vasile-Dan T1 - Report on the development and validation of the reference material candidates with non-spherical shape, non-monodisperse size distributions and accurate nanoparticle concentrations N2 - One aim of the EMPIR nPSize project 17NRM04 was to develop and validate three classes of candidate reference (test) materials (RTMs), with i) well-defined non-spherical shape, ii) relatively high polydispersity index, and iii) accurate particle concentrations. To fulfil the requirements of the project, 11 different types of materials were prepared. Following the initial assessment of the materials suitability, nPSize5_PT_UNITO, nPSize6_AC_UNITO and nPSize7_GN_CEA materials were found unsuitable for the project, due to various reasons. PT material was deemed unsuitable due to its predominantly agglomerated nature. AC material contained relatively high amount of impurities (other particle forms). GN material was found too heterogeneous in both the length and width for the purpose of the project. The remaining 8 candidate RTMs were assessed for their homogeneity and stability and used for successful delivery of the associated activities within the nPSize project. KW - Nanoparticles KW - Particle size distribution KW - Reference materials KW - Non-spherical shape KW - EMPIR nPSize KW - Electron microscopy KW - AFM KW - SAXS PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-556015 DO - https://doi.org/10.5281/zenodo.7016466 SP - 1 EP - 22 PB - Zenodo CY - Geneva AN - OPUS4-55601 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Babick, F. A1 - Mielke, Johannes A1 - Hodoroaba, Vasile-Dan A1 - Weigel, St. A1 - Wohlleben, W. T1 - Critical review manuscript with real-world performance data for counting, ensemble and separating methods including in-build mathematical conversion to number distributions submitted for publication N2 - The content of the paper is the assessment of the performance of (conventional) measurement techniques (MTs)with respect to the classification of disperse materials according to the EC recommendation for a definition of nanomaterial. This performance essentially refers to the accurate assessment of the number weighted median of (the constituent) particles. All data and conclusions are based on the analytical study conducted as real-world performance testing. It comprised different types of MTs (imaging, counting, fractionating, spectroscopic and integral) as well as different types of materials. Beside reference materials with well-defined size distribution the study also included several commercial powders (variation of particle composition, morphology, coating, size range and polydispersity). In order to ensure comparability of measurement results, the participants were guided to use uniform protocols in sample preparation, conducting measurements, data analysis and in reporting results. Corresponding documents have been made public, in order to support the reviewing process of the paper, respectively to ensure the reproducibility of data by other users under the same conditions. The scientific paper relies on a comprehensive set of revised measurement data reported in uniform templates, completely describes the experimental procedures and discusses the MTs’ performance for selected materials in detail. Even more, the study is summarised and evaluated, which leads to recommendations for the use of MTs within a tiered approach of NM characterisation. In addition, the paper critically examines the factors that may affect the outcome of such a comparison among different MTs. KW - Nanomaterial KW - Measurement techniques KW - EC definition of nanomaterial KW - Nanoparticles PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-389646 UR - http://www.nanodefine.eu/index.php/downloads/nanodefine-technical-reports UR - http://www.nanodefine.eu/publications/reports/NanoDefine_TechnicalReport_D3.3.pdf SP - D3.3, 1 EP - 72 PB - The NanoDefine Consortium CY - Wageningen, The Netherlands AN - OPUS4-38964 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Hodoroaba, Vasile-Dan A1 - Mielke, Johannes T1 - Templates for nanomaterial characterisation of tier 1 and tier 2 measurement methods N2 - The EU FP7 NanoDefine project was launched in November 2013 and will run until October 2017. The Project is dedicated to support the implementation of the EU Recommendation on the Definition of Nanomaterial by the provision of the required analytical tools and respective guidance. Main goal is to develop a novel tiered approach consisting of (i) rapid and cost-efficient screening methods and (ii) confirmatory measurement methods. The "NanoDefiner" eTool will guide potential end-users, such as concerned industries and regulatory bodies as well as enforcement and contract laboratories, to reliably classify if a material is nano or not. To achieve this objective, a comprehensive inter-laboratory evaluation of the performance of current characterisation techniques, instruments and software is performed. Instruments, software and methods are further developed. Their capacity to reliably measure the size of particulates in the size range 1-100 nm and above (according to the EU definition) is validated. Technical reports on project results are published to reach out to relevant stakeholders, such as policy makers, regulators, industries and the wider scientific community, to present and discuss our goals and results, to ensure a continuous exchange of views, needs and experiences obtained from different fields of expertise and application, and to finally integrate the resulting feedback into our ongoing work on the size-related classification of nanomaterials. KW - Nanomaterial KW - Measurement method KW - Screening methods KW - Confirmatory methods PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-389827 UR - http://www.nanodefine.eu/index.php/downloads/nanodefine-technical-reports SP - 1 EP - 74 PB - The NanoDefine Consortium CY - Wageningen, The Netherlands AN - OPUS4-38982 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beckmann, Jörg A1 - von der Ehe, Kerstin A1 - Jaunich, Matthias A1 - Schade, U. A1 - Aziz, E. F. A1 - Wolff, Dietmar T1 - Fourier-spektroskopische Untersuchungen im mittleren- und fernen Infrarotbereich an Co-60 bestrahlten und thermisch belasteten ultrahochmolekularen Polyethylen-Proben N2 - Fourier-Spektroskopische Untersuchungen von hochmolekularem Polyethylen (HMW-PE) und ultrahochmolekularem Polyethylen (UHMW-PE) im Mittleren - und Fernen Infrarotbereich können Veränderungen der molekularen Strukturen nachweisen, die durch Co60 γ-Strahlung und Rekristallisationsprozesse initiiert werden. UHMW-PE und HMW-PE sind im gewählten IR-Bereich unterscheidbar. Die integrale Absorption der B1u – Gitterschwingungen im Fernen Infrarotbereich (THz-Bereich) ermöglichen die quantitative Beschreibung des Kristallinitätsgrades und dessen Abbau. Die Bildung ungesättigter Vinylengruppen und der Abbau ungesättigter Methylengruppen können im Mittleren Infrarotbereich nachgewiesen werden. T2 - DGZfP-Jahrestagung 2014 CY - Potsdam, Germany DA - 26.05.2014 KW - Infrared and far-infrared spectroscopy KW - Polyethylene KW - Co-60 irradiation PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-313317 SN - 978-3-940283-61-0 VL - 148 SP - 1 EP - 7 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-31331 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Subramani Bhagavatheswaran, E. A1 - Wießner, S. A1 - Jaunich, Matthias A1 - Wolff, Dietmar T1 - Aging study and electrical resistance based stress-monitoring of rubber seals N2 - Elastomer seals are widely used as barrier seals in containers for low and intermediate level radioactive waste. In addition, they are also used in waste fuel storage and transportation casks as auxiliary seals. Depending on the area of use, the rubber materials have to demonstrate proper sealing performance with respect to mechanical, thermal and environmental conditions as well as irradiation during the entire operation period. A fundamental understanding of the structure property relationship and their changes during aging can help to evaluate the long-term sealing performance. In the present study, specific materials are investigated to study the structure-property and seal performance-correlation. Fluoro-elastomer (FKM), silicone rubber (VMQ) and ethylene propylene diene rubber (EPDM) were chosen as base rubbers. Comparable mechanical properties for these seals, especially in terms of a comparable compression behavior were achieved by careful control of base rubber formulation, i.e., by opting for the right filler and its concentration, amount of crosslinking chemicals, and with the assistance of process oils. Moreover, with the same rubber, similar mechanical properties were achieved by varying the filler concentration and crosslinking degree, which shall enable to correlate the particular influence on the structure property dependency of the seals in detail. The materials are investigated under pristine and aged conditions to evaluate the influence of aging, e.g. on the stress relaxation or recovery behavior. These values appear to be suitable parameters to judge the expected sealing performance. Due to the electrically conducting nature of some fillers used to reinforce rubbers (such as carbon blacks, carbon nanotubes (CNTs), Graphene, etc.) it is possible to obtain current information about mechanical and visco-elastic properties by monitoring the electrical conductivity or resistivity. A simple relation that relates electrical resistance with mechanical stress was derived and the stress values were theoretically predicted from the electrical resistance values, which showed good correlation with experimental results. T2 - 192nd Technical meeting of the ACS Rubber Division CY - Cleveland, OH, USA DA - 09.10.2017 KW - Seal KW - Rubber KW - Degradation KW - Structure-property relationship KW - Ageing PY - 2017 VL - 2017 SP - 1 EP - 25 AN - OPUS4-42849 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Sonntag, Nadja T1 - Untersuchung magnetischer Streufelder in einem inhomogen verformten Baustahl mittels passiv-magnetischer Prüfverfahren N2 - Die Metal Magnetic Memory (MMM) Methode ist ein standardisiertes, zerstörungsfreies Prüfverfahren, das für die Detektion von lokal geschädigten Materialbereichen in ferromagnetischen Bauteilen oder Proben verwendet wird. Es basiert auf der Annahme lokaler magnetoelastischer Wechselwirkungen an Spannungskonzentrationsstellen, die schwache magnetische Streufelder an den geschädigten Prüfkörperoberflächen hervorrufen. Die MMM-Methode überträgt dabei die für einachsige und elastische Verformungen entwickelten magnetoelastischen Modellvorstellungen ohne weitere Anpassungen in den Schädigungskontext, der jedoch mehrachsige Beanspruchungen und elastisch-plastische Deformationsprozesse erwarten lässt. Das Ziel der Arbeit ist es daher, die gängigen MMM-Hypothesen zur Signalentstehung fach- und skalenübergreifend und unter stärkerer Berücksichtigung mechanischer und mikrostruktureller Aspekte zu überprüfen. Zu diesem Zweck wurden zum einen gekerbte Flachzugproben aus einem unlegierten Baustahl inhomogen elastisch-plastisch verformt und die entstehenden magnetischen Streufelder an deren Oberflächen mit einem Drei-Achsen-GMR-Magnetometer detektiert. Die so ermittelten Magnetfeld-verteilungen wurden für unterschiedliche Verformungszustände ortsaufgelöst und richtungsabhängig mit gemessenen Dehnungsverteilungen (digitale Bildkorrelation) und mit simulierten Lastspannungs-verteilungen korreliert. Die eingeschnürten Probenbereiche wurden zusätzlich topographisch mittels Streifenlichtprojektion und Weißlichtinterferenzmikroskopie vermessen, um den Magnetisierungs-prozess ebenfalls vor dem Hintergrund geometrischer Effekte diskutieren zu können. Um systematische, verformungsinduzierte Veränderungen der magnetischen Mikrostruktur (magnetischer Domänen) im polykristallinen, quasi-isotropen Material nachzuweisen, wurde zum anderen ein in dieser Arbeit entwickelter statistischer Ansatz der Domänenanalyse angewandt. Hierfür wurde das Material zunächst durch Härteeindrücke mehrachsig elastisch-plastisch verformt, und die verformten Probenbereiche wurden anschließend mit Hilfe der Bitterstreifentechnik hauptsächlich bei niedriger Vergrößerung lichtmikroskopisch untersucht. Die beobachteten makroskopischen Domänen-kontraste wurden über ein analytisches, kontaktmechanisches (ECM-) Modell und über Makro-Eigen-spannungsmessungen (energiedispersive Synchrotron-Beugungsuntersuchungen) charakteristischen Verformungszonen unter den Härteeindrücken zugeordnet. Die Ergebnisse dieser Untersuchungen belegen, dass die Entstehung der Streufelder – entgegen bisheriger Annahmen – nicht allein auf mechanische Spannungs- und Verformungsgradienten im Material zurückzuführen, sondern auch topographisch bedingt ist. Die Vernachlässigung überlagerter geometrischer Effekte kann zu sicherheitsrelevanten Fehlinterpretationen der magnetischen Signale führen. Einachsige magnetoelastische Modellvorstellungen sollten zudem nicht ohne Anpassungen auf komplexe Beanspruchungen übertragen werden, da u. a. sowohl mechanische Größen (wie Spannungen oder Dehnungen) als auch mikrostrukturelle Parameter (wie z. B. Versetzungsdichten) bei komplexen Belastungen als ortsabhängige Variablen behandelt werden müssen. Die in dieser Arbeit beobachteten Domänenkontraste lassen sich zweifelsfrei charakteristischen Verformungszonen zuordnen, mikro-strukturell jedoch nicht allein mit anzunehmenden Gradienten der Versetzungsdichte erklären. Statt-dessen entstehen beispielsweise lokale Verformungstexturen, die zusätzliche magnetische Anisotropien bewirken könnten. Da bisher weder die makroskopischen noch die mikrostrukturellen Ursachen der Streufeldentstehung hinreichend verstanden sind, scheint die MMM-Methode für die quantitative Bewertung des Schädigungszustands derzeit ungeeignet. N2 - The Metal Magnetic Memory (MMM) method is a standardized, nondestructive testing method used for the detection of locally damaged material areas in ferromagnetic components or samples. It assumes local magnetoelastic interactions in stress concentration zones, causing weak magnetic stray fields on the damaged specimen surfaces. The MMM method transfers magnetoelastic model conceptions developed for uniaxial and elastic deformations without further adjustments into the damage context, which is, however, associated with multiaxial stresses and elastic-plastic deformations. The objective of this thesis is therefore to verify prevalent MMM hypotheses concerning the signal generation, putting emphasis on complex mechanical and microstructural aspects of damage while using interdisciplinary and multi-scale approaches. To this end, on the one hand, notched tensile specimens made of an unalloyed structural steel were inhomogeneously (elastically and plastically) deformed and deformation-induced magnetic stray fields were then detected by a three-axis GMR magnetometer. The obtained surface magnetic field distributions were correlated with measured strain distributions (digital image correlation) and with numerically simulated mechanical stress distributions (finite element analysis). To enable discussions on the magnetization process against the background of geometrical effects, the necked specimen regions were additionally investigated using optical profilometry methods (fringe projection and white light interference microscopy). On the other hand, a newly developed meso-scale approach to magnetic domain analysis was applied to prove systematic, deformation-induced changes of the magnetic microstructure within the polycrystalline, quasi-isotropic material: After multiaxial elastic-plastic deformation of coupon specimens by hardness indentation, the deformed sample regions were studied by Bitter technique in optical microscopy, preferably at low magnification. The observed macroscopic domain contrasts were related to characteristic deformation zones below the indents by using an analytical model from the field of contact mechanics (ECM) and macro-residual stress measurements (obtained from energy-dispersive synchrotron diffraction experiments). It is demonstrated that the formation of magnetic stray fields, quite contrary to previous assumptions, results not only from mechanical (e.g. stress) gradients within the material, but is also topographically induced. The neglect of such superimposed geometric effects may also lead to safety-relevant misinterpretations of the magnetic signals. Furthermore, uniaxial magnetoelastic model concepts should not be applied to complex stress/strain conditions without adaptation since both mechanical quantities (such as stresses or strains) and microstructural parameters (such as dislocation densities) must be treated as location-dependent variables. The observed magnetic domain contrasts could clearly be assigned to characteristic deformation zones but cannot be explained solely by hypothesized gradients of the dislocation density. Instead, for example, local deformation textures emerge, which may cause additional magnetic anisotropies. The MMM method currently seems unsuitable for quantitative damage assessments of components or specimens since neither the macroscopic nor the microstructural origins of the stray field formation have yet been sufficiently understood. KW - Magnetoelastischer Effekt KW - Magnetische Domänen KW - Mehrachsige Verformung KW - Schädigung KW - Unlegierter Baustahl KW - Magnetoelastic effect KW - Magnetic domains KW - Multiaxial deformation KW - Damage KW - Structural steel PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-484302 DO - https://doi.org/10.14279/depositonce-8524 SP - 1 EP - 117 CY - Berlin AN - OPUS4-48430 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Kömmling, Anja T1 - Alterung und Lebensdauervorhersage von O-Ring-Dichtungen T1 - Aging and lifetime prediction of O-ring seals N2 - Für Anwendungen, bei denen Elastomerdichtungen ihre Dichtheit über sehr lange Zeiträume (z. B. Jahrzehnte) behalten müssen, ohne dass ein Austausch praktikabel wäre, ist es nötig, die Lebensdauer solcher Dichtungen zuverlässig bestimmen zu können. Aus diesem Grund wurden Alterungsversuche an O-Ring-Dichtungen sowie Flachproben auf Basis von hydriertem Acrylnitril-Butadien-Kautschuk (HNBR), Ethylen-Propylen-Dien-Kautschuk (EPDM) und Fluorkautschuk (FKM) über bis zu zwei Jahre bei mehreren Temperaturen durchgeführt. Zur Untersuchung der auftretenden Eigenschaftsveränderungen wurden u. a. Härtemessungen, Zugversuche, dynamisch-mechanische und thermogravimetrische Analysen durchgeführt. Zur Beurteilung des Relaxations- und Rückstellverhaltens der alternden Dichtungen wurden außerdem Druckspannungsrelaxations- und Druckverformungsrestmessungen durchgeführt. Darüber hinaus wurde die Leckagerate gemessen, um ein Versagen der Dichtung zu detektieren. Durch die Untersuchung der gealterten Proben wurden sowohl die auftretenden Eigenschaftsveränderungen charakterisiert wie auch die damit zusammenhängenden Alterungsmechanismen diskutiert. Anhand der großen Datenmenge aus Ergebnissen von verschiedenen Untersuchungsmethoden, die für mehrere Alterungszeiten und -temperaturen durchgeführt wurden, sollte zusätzlich die günstigste Vorgehensweise für Lebensdauervorhersagen ermittelt werden. Dies beinhaltete auch die Bestimmung eines Lebensdauerkriteriums, das mit dem Auftreten von Leckage und damit dem Versagen der Dichtung zusammenhängt. Hinsichtlich der Eigenschaftsänderungen und Alterungsmechanismen wurde beim HNBR eine starke Versprödung aufgrund dominanter Vernetzungsreaktionen während der Alterung festgestellt. Diese resultierten auch darin, dass die Sauerstoffpermeabilität abnahm, so dass der Sauerstofftransport ins Innere der Probe (hauptsächlich bei den dickeren O-Ringen) behindert wurde. Dies führte dazu, dass diffusionsbegrenzte Oxidationseffekte (DLO-Effekte) auftraten, d. h. dass das Probeninnere weniger stark alterte als oberflächennahe Bereiche. Während der Alterung von EPDM traten sowohl Kettenspaltungen wie auch Vernetzungsreaktionen auf, was sich vor allem in einer Verschlechterung der Zugeigenschaften und einer Abnahme der Druckkraft sowie in einem steigenden Druckverformungsrest äußerte. Bei sehr stark gealterten Proben dominierten ebenfalls Vernetzungsreaktionen, was sich auch in deutlichen DLO-Effekten äußerte. Aufgrund seiner ausgeprägten Oxidations- und Hochtemperaturbeständigkeit wies FKM vergleichsweise geringe Degradationserscheinungen auf. Nur mit Druckspannungsrelaxation und Druckverformungsrest waren nennenswerte Änderungen ersichtlich. Messungen der statischen Leckagerate ergaben, dass die O-Ringe erst bei sehr weit fortgeschrittener Degradation undicht wurden und bis zu diesem Zeitpunkt kein allmählicher Anstieg der Leckagerate beobachtet werden konnte. Aus diesem Grund wurden Leckagemessungen mit einem modifizierten Versuchsaufbau durchgeführt, bei dem die Dichtung während der Messung leicht entlastet wird. Da dieser Test eine dynamische Rückstellung der Dichtung erfordert und damit höhere Ansprüche an die Dichtung stellt, wurde am geprüften EPDM-O-Ring ein früheres Versagen beobachtet. Der entsprechende Alterungszeitpunkt wurde als Versagenszeitpunkt definiert. Dieser wurde anhand der Daten verschiedener Messmethoden mit dem Degradationszustand korreliert und entspricht beispielsweise einem Druckverformungsrest von 80 %. Auf der Grundlage dieses Kriteriums konnten Lebensdauern mittels Zeit-Temperatur-Verschiebung bestimmt werden. Im Rahmen dieser Arbeit wurden zahlreiche Erkenntnisse darüber gewonnen, worauf bei beschleunigten Alterungsversuchen und Lebensdauerprognosen von O-Ringen zu achten ist und welche Fehlerquellen vermieden werden sollten. Dies wird zusammen mit Empfehlungen für eine bestmögliche Versuchsdurchführung ausführlich diskutiert. N2 - In some applications, elastomer seals have to remain leak tight over extended time periods (up to several decades) as an exchange of the seals is not practical. Therefore, it is necessary to be able to predict the lifetime of such seals reliably. For this reason, ageing experiments with O-rings and sheets based on hydrogenated acrylonitrile butadiene rubber (HNBR), ethylene propylene diene rubber (EPDM) and fluorocarbon rubber (FKM) were performed over up to two years at different temperatures. For investigating the changes of material properties during ageing, measurements of i.a. hardness and tensile behaviour as well as dynamic-mechanical and thermogravimetric analyses were conducted. For assessing the relaxation and recovery behaviour of the ageing seals, compression stress relaxation and compression set experiments were performed. Furthermore, leakage rate was measured to detect seal failure. By examining the aged samples, both the property changes and the responsible degradation mechanisms were characterised. Additionally, the most suitable approach for lifetime predictions should be determined using the large database of results from different test methods performed at several ageing times and temperatures. This included identifying an end-of-lifetime criterion that correlates with leakage and thus seal failure. Regarding the property changes and degradation mechanisms of HNBR, a pronounced embrittlement was observed due to dominant crosslinking reactions during ageing. These also resulted in a decrease of oxygen permeability, leading to a reduction of the oxygen transport into the interior sample (mainly of the thicker O-rings). This resulted in diffusion-limited oxidation effects (DLO effects), meaning that the interior of the sample aged less strongly than regions close to the surface. During ageing of EPDM, both chain scission and crosslinking occurred, which became noticeable in deteriorated tensile properties and decreased compression force as well as an increase of compression set. For strongly aged samples, crosslinking dominated as well and also led to pronounced DLO effects. Due to its excellent heat and oxidative stability, FKM exhibited comparatively minor degradation effects. Only compression stress relaxation and compression set showed notable changes. Measurements of static leakage rate revealed that O-rings became untight only after advanced degradation and that no gradual increase of leakage rate could be observed before failure. For this reason, additional leakage measurements were performed using a modified experiment that enabled a small decompression of the seal during the measurement. As this test requires a dynamic recovery of the seal and is thus more demanding, the tested EPDM O-ring failed earlier compared to the purely static test. The corresponding ageing state was defined as the point of failure and correlated to data from other test methods, corresponding e.g. to a compression set of 80 %. Based on this criterion, the lifetimes could be determined using the time-temperature superposition approach. During this work, a number of findings regarding the best way to conduct accelerated ageing experiments and lifetime predictions of O-rings, and how to avoid possible error sources, were collected and are discussed in detail. KW - Elastomer KW - Gummi KW - Degradation KW - Leckage KW - Verpressung KW - Rubber KW - Aging KW - Lifetime prediction KW - Leakage PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-397374 DO - https://doi.org/10.14279/depositonce-5827 SP - 1 EP - 121 PB - Technische Universität CY - Berlin AN - OPUS4-39737 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rockenhäuser, Christian A1 - Skrotzki, Birgit ED - Laue, Michael T1 - S-phase growth and coarsening in alloy 2618A during ageing N2 - The S-phase growth and coarsening in alloy 2618A during ageing is shown in a quantitative manner. T2 - Microscopy Conference 2017 (MC 2017) CY - Lausanne, Switzerland DA - 20.08.2017 KW - S-phase KW - Coarsening KW - TEM KW - Aluminium alloy 2618A PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:bvb:355-epub-360998 SP - MS4.014, 224 EP - 225 AN - OPUS4-41669 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hillger, W. T1 - Charakterisierung von Luftultraschallprüfköpfen mit thermoakustischen Wandlern N2 - Nicht nur die Qualitätssicherung von Bauteilen wird immer wichtiger und muss immer höheren Anforderungen entsprechen, sondern auch die dafür verwendete Prüfeinrichtung und die Sensorik. Für die Qualitätssicherung von Ultraschall-Prüfköpfen mit Luftankopplung bestand die bisherige Lösung darin, baugleiche Wandler als Aktuatoren (Referenzsender) einzusetzen. Für eine Weiterentwicklung der Wandler ist eine akustische Quelle wünschenswert, die eine weit größere Bandbreite mit flachem Frequenzgang aufweist, als die zu untersuchenden Prüfköpfe. Hier bieten sich thermoakustische Wandler an, die keine ausgeprägten Resonanzen haben und über eine hohe Bandbreite verfügen (min. 10 kHz bis 1 MHz). Diese wurden von der BAM in Berlin entwickelt und decken den Frequenzbereich von typischen Luftultraschall-Prüfköpfen vollständig ab. Der Vortag beschreibt die Besonderheiten der Ansteuerung dieser Wandler, die einen Innenwiderstand von ca. 7 Ohm besitzen und eine Pulsleistung von etwa 10 kW benötigen. Ferner werden erste Ergebnisse der Charakterisierung von unterschiedlichen piezokeramischen Prüfköpfen im Frequenzbereich von 50 kHz bis 500 kHz präsentiert. Beispielhaft zeigte ein Prüfkopf mit mehreren Anpassschichten lokale Frequenzunterschiede im Schallfeld. T2 - DACH-Jahrestagung 2019 CY - Friedrichshafen, Germany DA - 27.05.2019 KW - Ultrasound KW - Air coupled ultrasound KW - Thermoacoustics PY - 2019 UR - https://jahrestagung.dgzfp.de/Portals/jt2019/Dokumente/Kufa_GESAMT_klein_.pdf AN - OPUS4-48255 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zscherpel, Uwe A1 - Ewert, Uwe T1 - Digitale industrielle Radiographie im Anlagenbau N2 - Der Ersatz von Röntgenfilmen durch digitale Detektoren in der Zerstörungsfreien Prüfung im Anlagenbau wird seit 2013 durch neue ISO-Normen unterstützt. Nach der Erfolgsgeschichte der digitalen Photographie und der fast vollständigen Ablösung der Filmtechnik in der optischen Bilderfassung wird erwartet, dass sich der Übergang von der Filmradiographie zur digitalen Radiographie schnell vollzieht. Dieser Trend ist derzeit so noch nicht zu beobachten. Zur mobilen Prüfung wird in Europa immer noch vorrangig die Filmradiographie und nur teilweise die Computerradiographie mit Speicherfolien eingesetzt. Im Bereich der stationären Prüftechnik haben sich die Matrixdetektoren (DDA) weitgehend durchgesetzt, wobei es auch hier noch alternative Detektoren wie Bildverstärker und Fluoroskope gibt. Mit Einführung der DIN EN ISO 17636-2 zur Schweißnahtprüfung wird seit 2013 erstmalig geregelt, wie man einen digitalen Detektor für die technische Radiographie auswählen soll, um im Vergleich zur Filmradiographie eine äquivalente Bildqualität zu erhalten. Essentielle Parameter bestimmen, ob die geforderte Bildgüte (Fehlernachweißempfindlichkeit) erreicht wird. Ein Überblick zeigt, welche Parameter für den praktischen Einsatz wichtig sind und wie sie ermittelt werden. Praktische Einsatzbeispiele im Anlagenbau werden diskutiert. T2 - 47. Sondertagung: Schweißen im Anlagen- und Behälterbau CY - Munich, Germany DA - 19.02.2019 KW - Industrielle Radiographie KW - Digitaler Filmersatz KW - Stand der Normung KW - Bildqualitätsnachweis PY - 2019 SN - 978-3-96144-055-9 VL - 350 SP - 19 EP - 22 PB - DVS Media CY - Düsseldorf AN - OPUS4-50526 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Genath, A. A1 - Hofmann, Michael A1 - Tiebe, Carlo A1 - Einspanier, R. T1 - Proof-of-concept trial of the portable electronic nose PEN3 for detection of formic acid concentration in the beehive N2 - Formic acid (FA) treatment as measure against the ectoparasitic mite, Varroa destructor, which infests the western honey bee, Apis mellifera, is usually performed twice a year. Although the therapeutic index is very narrow and the success of FA-treatment is highly dependent on various external factors, little is known about the local FA concentrations occuring in the hive. In this study we examined whether a commercially available odour measuring device (“electronic nose”) is suitable for measurements of high FA concentrations, as present during treatment. As measuring systems, two different setups were prepared for detection of FA concentrations in gas mixtures: A polymethyl methacrylate (PMMA) box was used to investigate whether the electronic nose is able to distinguish between different FA concentrations and a two-storied Segeberger hive to test under realistic conditions during bee-keeping. In both experimental systems, the signals from the same sensor components (sensor type no. 1, 6, 7, 8 and 9) showed an increased sensitivity towards the presence of FA in the gas mixture. Principle component analysis (PCA) and linear discriminant analysis (LDA) allowed for identification of specific patterns in the measurement signals and showed clear correlations between the signals and the present FA concentration. These results indicate that the introduced commercial multi gas sensor system is suitable for detection of high FA concentrations, and therefore could be a starting point developing a detection method of FA. The future aim is to successfully monitor the efficiency and effectiveness of this anti-varroa-treatment. T2 - 20. GMA/ITG-Fachtagung Sensoren und Messsysteme 2019 CY - Nuremberg, Germany DA - 25.06.2019 KW - Apis mellifera KW - Varroa destructor KW - Formic Acid KW - Metal-Oxide Gas Sensor Array PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-483812 UR - https://www.ama-science.org/proceedings/details/3430 DO - https://doi.org/10.5162/sensoren2019/P3.10 VL - 2019 SP - 794 EP - 799 AN - OPUS4-48381 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schlegel, Moritz-Caspar A1 - Akkerman, Floris T1 - One step back, two steps forward – Resource efficiency requirements within ecodesign N2 - Resource efficiency is a much discussed topic in terms of improving the sustainability of energy related and energy non-related products. Resource efficiency aspects such as the availability of spare parts, the ability to dismantle, etc. have been included in draft working documents in the revision of several already existing Ecodesign regulations as a first step. However, often these aspects are not consistent with the current technology and design of these products. A possible reason could be a lack of sufficient consultation or of a methodology which is sufficiently tailored for this topic. The established strategies and tools, used by policymakers, such as the Methodology for the Ecodesign of Energy-related Products (MEErP), do not seem to deal with these aspects appropriately. Draft requirements need to be very well developed before being discussed with member states and other related stakeholders, because including resource efficiency parameters could lead to additional, very wide-ranging effects on society. This topic cannot be covered well with legislative tools developed primarily for energy aspects. In this paper, a method is presented which can be used to combine products’ properties with crucial resource efficiency indicators. The method can be used to develop a set of draft legislative requirements and to pre-evaluate these requirements by target groups which would be affected by additional legal requirements. These include: market surveillance authorities, standardization organizations, manufacturers and their associations, environmental organizations and research facilities. The method incorporates stakeholders’ feedback to identify potential resource efficiency measures for materials and/or products, their impact on the European ecology, economy and society. Based on this it would help to develop legislative requirements which are feasible and desirable. The results can then be fed into the formal legislative process, probably speeding it up. T2 - ECEEE 2019 Summer Study on Energy Efficiency CY - Belambra Presqu'île de Giens, France DA - 03.06.2019 KW - Resources KW - Circular economy KW - Ecodesign KW - Energy policy PY - 2019 UR - https://www.eceee.org/library/conference_proceedings/eceee_Summer_Studies/2019/ SN - 978-91-983878-5-8 SN - 2001-7960 VL - 2019 SP - 1553 EP - 1562 AN - OPUS4-48341 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simon, Franz-Georg T1 - Abfallverbrennung in der Zukunft, Wertstoffrückgewinnung N2 - Aktuell werden in Deutschland in rund 100 thermischen Abfallbehandlungsanlagen (davon 66 Hausmüllverbrennungsanlagen) rund 20 Millionen Tonnen brennbare Abfälle verbrannt. Mit rund 5 Millionen Tonnen pro Jahr bildet die Rostasche die mengenmäßig größte Rückstandsfraktion. Nach einer Lagerung von einigen Wochen erfüllt die Rostasche im Regelfall die Anforderungen für die Deponieklasse 1. Allerdings wird der Großteil der Rostasche nicht deponiert, sondern aufbereitet und verwertet. Zur Aufbereitung kommen verschieden Verfahren zum Einsatz. Für die Abtrennung der Eisen- und NE-Metalle werden magnetische Verfahren und die Wirbelstromtechnik eingesetzt. Für die mineralischen Fraktion gibt es eine Vielzahl von Sortier- und Klassierungsverfahren, Waschverfahren und weitergehende thermische Verfahren. T2 - Jahrestreffen der Fachgruppen Abfallbehandlung und Wertstoffrückgewinnung sowie Rohstoffe CY - Frankfurt/M., Germany DA - 18.03.2019 KW - Abfallverbrennung KW - Rostasche PY - 2019 SP - 16 EP - 16 AN - OPUS4-48539 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Cassube, Florian A1 - Simon, Franz-Georg T1 - Metallrückgewinnung aus Hausmüllverbrennungsaschen N2 - Angesichts stetig steigender Rohstoffnachfrage und sich verknappenden Ressourcen rücken Sekundärrohstoffe zur Deckung des Bedarfes immer stärker in den Fokus. Besonders Hausmüllverbrennungsaschen (HMVA) verfügen über hohe Anteile an Metallen wie Aluminium, Kupfer, oder Eisen, aber auch Spuren von Silber und Gold. Aus diesem Grund wurde bereits in einer Vielzahl von Arbeiten und Projekte die Behandlung von Rostaschen diskutiert. Hauptaugenmerk der Betrachtungen ist die Rückgewinnung von Wertstoffen, insbesondere der Metallfraktion, sowie die Aufbereitung der Rostasche als Ersatzbaustoff. Die bisherigen Betrachtungen konzentrierten sich auf die Fraktionen der Partikel größer 2 mm. Die Feinfraktion kleiner 2 mm wurde bislang meist deponiert. Da die Feinfraktion etwa 25 M% der HMVA ausmacht, wurde für weitere Untersuchungen zum Zweck einer besseren Verwertung das Projekt „BASH-TREAT“ im Programm ERA-MIN 2 initiiert. T2 - Jahrestreffen der Fachgruppen Abfallbehandlung und Wertstoffrückgewinnung sowie Rohstoffe CY - Frankfurt/M., Germany DA - 18.03.2019 KW - Nassaufbereitung KW - Rostasche PY - 2019 SP - 23 EP - 23 AN - OPUS4-48540 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Horn, Wolfgang A1 - Jann, Oliver A1 - Brosig, L. A1 - Müller, B. A1 - Mertes, A. A1 - de Lima Vasconcelos, S. T1 - Emissions- und geruchsarme Bauprodukte für energieeffiziente Gebäude – Entwicklung von Anforderungen und Konzepten für den Blauen Engel aus Klimaschutzsicht N2 - Menschen, die in der gemäßigten Klimazone leben, verbringen bis zu 90% ihres Lebens in Innenräumen. Deshalb hat das Innenraumklima eine sehr große Bedeutung für deren Wohlergehen, Gesundheit und Leistungsfähigkeit. In Deutschland wird ca. 40% der eingesetzten Primärenergie für das Heizen, Kühlen und Klimatisieren der Innenräume verwendet. Das Forschungsvorhaben hat eine Laufzeit vom Oktober 2013 bis März 2017. Es wird in Kooperation mit der Bundesanstalt für Materialforschung und –prüfung (BAM) und der Hochschule für Technik und Wirtschaft Berlin (HTW Berlin) durchgeführt. Die HTW Berlin koordiniert das Projekt. Die Rheinisch-Westfälische Technische Hochschule Aachen (RWTH) wird teilweise über einen Auftrag in das Projekt integriert. Ziel des Projektes ist es Baustoffe auf ihre Geruchsemissionen zu untersuchen, um Bauprodukte mit niedrigen Emissionen und Gerüchen identifizieren zu können. Den Verbraucherinnen und Verbrauchern wird somit die Möglichkeit gegeben emissions- und geruchsarme Baustoffe zu wählen. Die Aufgabenstellung des Projektes ist nachfolgend aufgeführt: Arbeitspaket 1: Geruchsmessung bei Produkten mit dem Blauen Engel (siehe Kapitel 4 und 5); Arbeitspaket 2: Untersuchung von Vergleichsmaßstäben (siehe Kapitel 6); Arbeitspaket 3: Untersuchung der Linearität der Acetonskala (siehe Kapitel 7); Arbeitspaket 4: Erstellung einer Produktdatenbank (siehe Kapitel 8). Die Geruchsuntersuchung ist in den Vergabekriterien für den „Blauen Engel“ für textile Bodenbeläge (RAL UZ-128) eingebunden worden. Aus den weiteren Untersuchungen sind für die Normung wichtige Erkenntnisse erarbeitet worden. KW - VOC Emissionen KW - Geruch KW - Bewertung KW - Innenraumluftqualtität KW - Bodenbeläge PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-487223 UR - https://www.umweltbundesamt.de/publikationen/emissions-geruchsarme-bauprodukte-fuer UR - https://www.umweltbundesamt.de/sites/default/files/medien/1410/publikationen/2019-08-20-texte_92-2019_emissionsarme-bauprodukte.pdf SN - 1862-4804 VL - 92 SP - 1 EP - 106 PB - Umweltbundesamt CY - Dessau-Roßlau AN - OPUS4-48722 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - de Lima Vasconcelos, S. A1 - Sattler, M. A1 - Müller, B. A1 - Plehn, W. A1 - Horn, Wolfgang T1 - The Influence of textile floor coverings on the indoor air quality N2 - Textile floor coverings are often used in offices and residential buildings. Large areas like meeting rooms, cinemas, theaters and hotels are often equipped with such coverings. They contribute to the comfort of the users as they provide high pedaling comfort and sound absorption. The weakness of these building materials is due to the odor emission that is released from the floor covering, which affects the comfort of the users. A bad air quality and the resulting dissatisfaction can lead to lower employee productivity. The research project of the Hochschule für Technik und Wirtschaft Berlin (HTW-Berlin) is promoted by the German Environment Agency (UBA). The project has the following title: Low-emission and low-odor building products for energy-efficient buildings - Development of requirements and concepts for the Blue Angel from a climate protection perspective; investigates the emission and odor behavior of textile floor coverings (Emissions- und geruchsarme Bauprodukte für energieeffiziente Gebäude - Entwicklung von Anforderungen und Konzepten für den Blauen Engel aus Klimaschutzsicht; untersucht das Emissions- und Geruchsverhalten textiler Bodenbeläge). T2 - Clima 2019 Congress CY - Bucharest, Romania DA - 26.05.2019 KW - VOC Emissionen KW - Geruch KW - Bodenbelag KW - AgBB Bewertung PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-487341 DO - https://doi.org/10.1051/e3sconf/201911102051 SN - 2267-1242 VL - 111 SP - 02051-1 EP - 02051-6 PB - EDP Sciences AN - OPUS4-48734 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Maiwald, Michael A1 - Klaer, R.-H. A1 - Wagner, A. ED - Kockmann, N. T1 - 100 % Digital in der Prozessindustrie Tutzing-Symposion Teil 3: Intelligente Nutzung von Daten und Bausteinen der Digitalisierung N2 - Digitalisierung und Industrie 4.0 verändern komplette Geschäftsmodelle, heben neue Effizienzpotenziale und stärken die Wettbewerbsfähigkeit. Auf dem 57. Tutzing-Symposion vom 15.–18.04.2018 wurde mit Vorträgen und Kreativworkshops erkundet, welche speziellen Anforderungen die Prozessindustrie hat, welche digitalen Innovationen bereits umgesetzt wurden und wo noch Handlungsbedarf besteht. Ein Workshop befasste sich mit den Themenfeldern Datenkonzepte, Datenanalyse, Big Data und künstliche Intelligenz. KW - Prozessindustrie KW - Digitalisierung KW - Industrie 4.0 KW - Datenanalyse KW - Künstliche Intelligenz PY - 2019 SN - 1436-2597 VL - 22 SP - 14 EP - 19 PB - Wiley-VCH CY - Weinheim AN - OPUS4-48838 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wasmer, Paul A1 - Bulling, Jannis A1 - Prager, Jens T1 - Ultrasonic sensor based on phononic crystals N2 - An essential task in many industries, e.g. food, petrol or chemical industry, is the precise and accurate characterization of liquids. Therefore, the development of innovative in-line sensors is of great interest. New concepts based on periodic structures, so-called phononic crystals (PnCs), are an interesting idea for the design of innovative sensors. A PnC-based sensor can be designed by introducing a resonance inside a bandgap, a frequency region where no wave propagation is allowed. High-Q measurement systems using PnCs are already reported in the literature. However, existing designs cannot be implemented into a piping system directly, but need special fittings, openings or by-passes to be in contact with the liquid. To circumvent this issue, we develop a new sensor based on PnCs, which can be directly implemented as part of the piping system. For this purpose, we use a PnC consisting of hollow cylinders with a periodic change of the outer diameter. A bandgap could be found for the described geometry without fluid in simulation and measurement. However, simulations show, that a bandgap for fluid-filled cylinders can only be obtained for quasi-longitudinal modes. Hence, we propose a mode selective excitation for the sensor. T2 - ICA 2019 CY - Aachen, Germany DA - 09.09.2019 KW - Phononic crystal KW - Ultrasound PY - 2019 SN - 978-3-939296-15-7 SN - 2226-7808 SN - 2415-1599 SP - 969 EP - 976 AN - OPUS4-48860 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Abraham, O. A1 - Niederleithinger, Ernst A1 - Chapeleau, X. A1 - Klikowicz, P. A1 - Brühwiler, E. A1 - Bassil, A. A1 - Wang, Xin A1 - Chakraborty, J. A1 - Bayane, I. A1 - Leduc, D. A1 - Salamak, M. A1 - Katunin, A. A1 - Sørensen, J.D. T1 - Addressing the need to monitor concrete fatigue with nondestructive testing: Results of infrastar European project N2 - Fatigue is one of the most prevalent issues, which directly influences the service life expectancy of concrete structures. Fatigue has been investigated for years for steel structures. However, recent findings suggest that concrete structures may also be significantly subjected to fatigue phenomena that could lead to premature failure of certain structural elements. To date, fatigue of reinforced concrete has been given little focus. Knowledge on the influence factors and durability/capacity effects on this material should be improved. Current technological means to measure fatigue in civil structures like bridges and wind turbines (both onshore and offshore) are outdated, imprecise and inappropriate. Meanwhile, this topic has got much more attention as time-variant loading on concrete structures plays an increasing role, e.g. in bridges with increasing traffic and heavier trucks, and for wind turbines for renewable energy production, e.g. for offshore wind turbine support structures affected by wind and waves. The European Innovative Training Networks (ITN) Marie Skłodowska-Curie Actions project INFRASTAR (Innovation and Networking for Fatigue and Reliability Analysis of Structures - Training for Assessment of Risk) provides research training for 12 PhD students. The project aims to improve knowledge for optimizing the design of new structures as well as for more realistic verification of structural safety and more accurate prediction of the remaining fatigue lifetime of existing concrete structures. First, the INFRASTAR research framework is detailed. Then it will be exemplified through the presentation of the major results of the four PhD students involved in the work package dealing with auscultation and monitoring. This includes the development and improvement of Fiber Optics (FO) and Coda Wave Interferometry (CWI) for crack sizing and imagery, new sensor technologies and integration, information management, monitoring strategy for fatigue damage investigation and lifetime prediction. T2 - SMT and NDT-CE 2018 CY - New Brunswick, NJ, USA DA - 27.08.2018 KW - Concrete KW - Fatigue KW - Crack KW - Monitoring KW - Non-destructive testing PY - 2019 UR - https://asnt.org/smt18papers SN - 978-1-57117-456-7 VL - 11/19 SP - 2 EP - 13 PB - The American Society for Nondestructive Testing, Inc. CY - Columbus, OH, USA AN - OPUS4-47237 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hofmann, Michael A1 - Moufid, M. A1 - El Bari, N. A1 - Tiebe, Carlo A1 - Bouchikhi, B. T1 - Testing of a developed multigas sensor system for outdoor odour nuisance monitoring N2 - This work presents the testing of a developed elec¬tronic nose for outdoor odour nuisance monitoring. The sensor system consists of a sampling system, a measuring cell equipped with commercially available low-cost gas sensor elements and a data acquisition system. The sensor testing showed that the developed prototype is able to distinguish, identify and partially quantify individual odorous substances like ethanol, ammonia and hydrogen sulphide. Ethanol and ammonia could even be detected below or near their odour threshold. T2 - ALLSENSORS 2019, The Fourth International Conference on Advances in Sensors, Actuators, Metering and Sensing CY - Athens, Greece DA - 24.02.2019 KW - Electronic nose KW - Outdoor odour KW - Machined olfaction KW - Sensor testing PY - 2019 UR - https://www.thinkmind.org/index.php?view=article&articleid=allsensors_2019_2_40_70065 SN - 978-1-61208-691-0 SN - 2519-836X SP - 27 EP - 28 PB - The ThinkMind Digital Library AN - OPUS4-47505 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wasmer, Paul A1 - Bulling, Jannis A1 - Prager, Jens T1 - Entwicklung eines Ultraschallrohrsensors auf Basis phononischer Kristalle N2 - Die Messung von Flüssigkeitskonzentrationen in Rohrsystemen ist von großem Interesse für viele unterschiedliche Anwendungen. Die meisten Messsysteme sind jedoch nicht in der Lage, die Flüssigkeit direkt im Rohr zu untersuchen und es muss eine zusätzliche Vorrichtung, wie z.B. einem Bypass, angebracht werden, welche den Kontakt zwischen Flüssigkeit und Sensor ermöglicht. Um den Einbauaufwand gering zu halten und die Strömungseigenschaften des Rohres nicht zu beeinflussen, wird ein neuartiges Messsystem entwickelt, welches als Teil der Rohrwand ausgeführt werden kann. Dieses neuartige System ist angelehnt an die Idee der phononischen Kristallen (PnK). PnK’s bestehen im Allgemeinen aus einem Matrixmaterial, in welchem Streuzentren periodisch angeordnet sind. Dies führt beim Eintreffen einer akustischen Welle in definierten Frequenz-bereichen, sogenannter Bandlücken, zu zunehmender destruktiven Interferenz. Wird innerhalb einer solchen Bandlücke durch Einbringen einer flüssigkeitsgefüllten Kavität ein Resonanzverhalten erzeugt, kann dies genutzt werden, um die Flüssigkeit zu analysieren. Im Rahmen von Voruntersuchung wird zunächst das akustische Verhalten des PnK’s, welcher für die Sensorentwicklung genutzt werden soll, unter Vernachlässigung der Flüssigkeit ausführlich untersucht. Hierbei werden zunächst die Bandlücken ermittelt und das Übertragungsverhalten betrachtet. Dieses wird im Anschluss experimentell überprüft. T2 - DAGA 2019 - 45. Jahrestagung für Akustik CY - Rostock, Germany DA - 18.03.2019 KW - Phononischer Kristall KW - Ultraschall KW - Flüssigkeitssensor KW - Scaled Boundary Finite Element Method PY - 2019 SP - 1030 EP - 1033 AN - OPUS4-47780 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dittmann, Daniel A1 - Ruhl, A. S. A1 - Jekel, M. A1 - Braun, Ulrike T1 - Spurenstoffadsorption an Aktivkohle – Untersuchungen mit Analysen oberhalb des Siedepunktes N2 - In diesem Beitrag wird gezeigt wie mit Thermogravimetrischen Analysen (TGA) Aktivkohleoberflächen charakterisiert werden können. Außerdem wie TGA mit Zersetzungsgasanalyse zur Untersuchung von Adsorbat-Systemen (Carbamazepin an drei verschiedenen Aktivkohlen) zur Aufklärung von Adsorptionszuständen genutzt werden kann. T2 - Wasser 2019 CY - Erfurt, Germany DA - 27.05.2019 KW - Aktivkohle KW - Adsorption KW - Carbamazepin KW - Thermogravimetrie PY - 2019 SN - 978-3-947197-11-8 SP - 98 EP - 102 AN - OPUS4-48258 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Raysyan, Anna T1 - Ideen nah am Leben N2 - Ein Schnelltest zum Nachweis von Schadstoffen in der Muttermilch und eine Schnittmustersoftware - Wissenschaftstalente mit anwendungsnahen Ideen und auf dem Weg ins Unternehmertum. KW - Diclofenac KW - Schnelltest KW - Lateral Flow Immunoassay KW - Schwangerschaftstest PY - 2019 IS - 01-02 SP - 12 EP - 13 PB - WISTA Management GmbH CY - Berlin AN - OPUS4-48315 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Hlavacek, Petr A1 - Ebell, Gino A1 - Gluth, Gregor A1 - Reinemann, Stefi A1 - Mietz, Jürgen A1 - Kühne, Hans-Carsten T1 - Betonstahlkorrosion in Geopolymerbetonen bei Angriff von Kohlenstoffdioxid und Chlorid N2 - Der kritische, Korrosion auslösende Chloridgehalt für die Beurteilung der Korrosions-beständigkeit von Betonstahl in Geopolymerbetonen ist von großer Bedeutung für die Dauerhaftigkeitsprognose für bewehrte Elemente aus solchen Materialien. Es sind kaum experimentelle Daten in der Fachliteratur vorhanden und die vorliegenden Werte unterscheiden sich zwischen den Studien erheblich. In diesem Projekt wurde der kritische, Korrosion auslösende Chloridgehalt für Betonstahl (BSt 500) in flugaschebasierten (Ca-armen) Geopolymermörtel für verschiedene Beaufschlagungskombinationen bestimmt: Chloridbeaufschlagung mit 1 M NaCl-Lösung; Auslaugen in entionisiertem Wasser und anschließende Chloridbeaufschlagung im 1 M NaCl-Lösung; Auslaugen in entionisiertem Wasser, Carbonatisierung in Luft bei 20 °C und natürlicher CO2 Konzentration und anschließende Chloridbeaufschlagung mit 1 M NaCl-Lösung. Für Referenz-Zwecke wurde zusätzlich der Korrosion auslösende Chloridgehalt für eine Portland-Zement Mischung bei Auslagerung in 1 M NaCl-Lösung bestimmt. KW - Korrosion KW - Geopolymer PY - 2019 SP - 1 EP - 83 AN - OPUS4-49752 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Webb, A. A1 - Hofmann-Böllinghaus, Anja T1 - Changes in façade regulations N2 - Recent facade fires worldwide have driven change in regulations for façade fire safety in different parts of the world. The Grenfell Tower fire 2017 in London triggered a thorough investigation of many aspects of the fire. One investigation was about the UK building regulations from Dame Judith Hackett. This investigation compares the UK with the situation other parts of the world. Key findings of the review of building regulations by Judith Hackett are: T2 - Interflam 2019 CY - London, UK DA - 01.07.2019 KW - Facades PY - 2019 VL - 2019 SP - 213 EP - 228 PB - Interscience CY - London, UK AN - OPUS4-49893 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wosniok, Aleksander A1 - Schreier, Andy A1 - Krebber, Katerina T1 - Distributed BOFDA measurement on an 86 m long perfluorinated polymer optical fiber N2 - We present our research on the development of a Brillouin optical frequency-domain analysis (BOFDA) using a perfluorinated graded-index polymer optical fiber (PFGI-POF) as a sensing fiber. The described works include investigations both on the selection of the setup components with respect to mode coupling effects and on the impact of the humidity cross-sensitivity. The suitability of the developed POF-based BOFDA is proved by a distributed measurement on an 86 m long PFGI-POF recorded with the spatial resolution of 6 m. T2 - 28th International Conference on Plastic Optical Fibers CY - Yokohama, Japan DA - 20.11.2019 KW - Brillouin sensing KW - BOFDA KW - Perfluorinated graded-index polymer optical fiber KW - PFGI-POF PY - 2019 SP - 27 EP - 28 AN - OPUS4-49865 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Robens-Radermacher, Annika A1 - Unger, Jörg F. T1 - Efficient reliability analysis coupling importance sampling using adaptive subset simulation and PGD model reduction N2 - One of the most important goals in civil engineering is to guaranty the safety of constructions. National standards prescribe a required failure probability in the order of 10−6 (e.g. DIN EN 199:2010-12). The estimation of these failure probabilities is the key point of structural reliability analysis. Generally, it is not possible to compute the failure probability analytically. Therefore, simulation-based methods as well as methods based on surrogate modeling or response surface methods have been developed. Nevertheless, these methods still require a few thousand evaluations of the structure, usually with finite element (FE) simulations, making reliability analysis computationally expensive for relevant applications. The aim of this contribution is to increase the efficiency of structural reliability analysis by using the advantages of model reduction techniques. Model reduction is a popular concept to decrease the computational effort of complex numerical simulations while maintaining a reasonable accuracy. Coupling a reduced model with an efficient variance reducing sampling algorithm significantly reduces the computational cost of the reliability analysis without a relevant loss of accuracy. T2 - GAMM - Gesellschaft für Angewandte Mathematik und Mechanik e.V. CY - Wien, Austria DA - 18.02.2019 KW - PGD model reduction KW - Numerical models KW - FE modelling PY - 2019 DO - https://doi.org/10.1002/pamm.201900169 VL - 19 IS - 1 SP - 1 EP - 2 PB - Wiley- VCH Verlag GmbH CY - Weinheim AN - OPUS4-49786 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heckel, Thomas A1 - Wack, Y. A1 - Mook, G. T1 - Simulation of an instrumented ultrasonic test run with a rail inspection train N2 - Rail inspection performed by ultrasonic rail inspection trains is a complex and challenging process. A large number of variables and parameters given by the environment, the track and the testing-system have an influence on the overall performance of the inspection and the inspection result. Typically the parameter vary in a combination depending on the track condition. To evaluate the individual influence of each relevant variable, simulation tools can be used. Therefore the entire inspection process has to be transferred into a model using combined modelling techniques. The goal of this work is to model an instrumented ultrasonic test run with a rail inspection train with the parameters varied by a script over a virtually driven distance. T2 - 46th Annual Review of Progress in Quantitative Nondestructive Evaluation- QNDE 2019 CY - Portland, OR, USA DA - 14.07.2019 KW - Ultrasound KW - Rail inspection KW - Modelling KW - Simulation PY - 2019 VL - 2019 SP - 1 EP - 3 AN - OPUS4-49839 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Romero-Navarrete, José A. A1 - Otremba, Frank T1 - Lateral load transfer due to sloshing cargo in partially filled containers N2 - A testing methodology has been proposed in this paper, to compare the load transfer derived from solid and liquid cargoes when the carrying vehicle is subjected to a lateral acceleration in a tilt table. Besides the type of cargo, the other factors (a) One-quarter fill level (b) One-half fill level (c) Three-quarter fill level (d) Fast input considered are the fill level and the rate at which the considered are the fill level and the rate at which the acceleration input is acceleration input is exerted on the vehicleexerted on the vehicle. The acceleration The acceleration input can represent the entering of the carrying vehicle into a input can represent the entering of the carrying vehicle into a curved portion curved portion of of aa road. The testing device integrates the needed components to measure the fourmeasure the four--wheel loads of the wheel loads of the carrying vehicle, while carrying vehicle, while providing different times to attain providing different times to attain aa 10°10° angle angle for the tilt table. for the tilt table. The performance measure selected is significant to assess the rollover trend of a vehicle, on the basis of the wheel loads at both sides of the vehicle. both sides of the vehicle. The outputs from the experiments suggest that the sloshing suggest that the sloshing cargo transfercargo transferss the greater loads, the greater loads, regardless of the fill level and regardless of the fill level and acceleration rate inputacceleration rate input, as a result , as a result of the shifting of the center of of the shifting of the center of gravitygravity of the liquidof the liquid, and of of the the dynamic vibration at the end of dynamic vibration at the end of the perturbation input. In this respect, while the solid cargo the perturbation input. In this respect, while the solid cargo exhibits an initial peak and decay, the exhibits an initial peak and decay, the sloshing cargo exhibits sloshing cargo exhibits several oscillations of the saseveral oscillations of the same magnitude, which is attributed me magnitude, which is attributed to the to the liquid inertia and liquid inertia and to the to the reflection of the surface waves. reflection of the surface waves. A further analysis could supplement this research, to assess supplement this research, to assess the effect of some other factors on the dynamic the effect of some other factors on the dynamic behavior of the behavior of the liquid cargoliquid cargo-vehicle system. Fvehicle system. For example, to analyze the effect or example, to analyze the effect of longitudinal baffles, and to validate theoretical models.of longitudinal baffles, and to validate theoretical models. T2 - IMECE – International Mechanical Engineering Congress and Exposition CY - Salt Lake City, UT, USA DA - 11.11.2019 KW - Transfer KW - Sloshing KW - Cargo KW - Container PY - 2019 SP - 2019-10030 PB - ASME AN - OPUS4-49980 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Antons, U. A1 - Eisenkrein-Kreksch, H. A1 - Krankenhagen, Rainer A1 - Altenburg, Simon A1 - Jonietz, Florian T1 - Thermografische Schichtdickenbestimmung von Oberflächenschutzsystemen N2 - Die Anwendung von Polymerbeschichtungen im Bauwesen hat über die letzten Dekaden stetig zugenommen. Neben ästhetischen Aspekten sind vor allem die Verbesserung der Dauerhaftigkeit des Bauwerks und damit einhergehend die Verlängerung der Nutzungsdauer ausschlaggebende Gründe für die Wahl einer Beschichtung. Um die jeweiligen Bauteile vor Alterung, Verschleiß und Schädigung effektiv und zielsicher schützen zu können ist die Einhaltung der von den Herstellern vorgegebenen Mindestschichtdicken von essenzieller Bedeutung. Aus diesem Grund ist es notwendig die Schichtdicke der Beschichtung nach erfolgter Applikation zu überprüfen. Für den in diesem Zusammenhang anspruchs-vollen mineralischen Untergrund Beton stehen für die Baustelle bislang allerdings nur zerstörende Prüfverfahren zur Verfügung. Aufbauend auf den Ergebnissen zur photothermischen Schichtdickenbestimmung von Polymerbeschichtungen im Rah-men des Forschungsprojektes IRKUTSK werden derzeit im WIPANO Projekt PHOBOSS weitreichende Untersuchungen durchgeführt, um diese zerstörungsfreie Untersuchungsmethode auf den Baubereich anzuwenden. Ziel des WIPANO Projektes PHOBOSS ist neben der Verfeinerung und Validierung der Mess-und Auswertungsmethodik die Erstellung eines Normenentwurfes welcher Rahmenbedingungen und Anforderungen für Messung und Messgerät enthalten soll. Im Rahmen dieser Veröffentlichung werden Einblicke in das zur Schichtdickenbestimmung entwickelte Thermografie-verfahren gegeben. Die Funktionsweise des Verfahrens für die Messung von Oberflächenschutzsystemen wird anhand von Labor- und In Situ-Messungen illustriert und der für die Messungen verwendete Prototyp vorgestellt. T2 - 6. Kolloquium "Erhaltung von Bauwerken" CY - Esslingen, Germany DA - 22.01.2019 KW - Beton KW - Oberflächenschutzsystem (OSS) KW - Zerstörungsfreie Prüfung KW - photothermisch KW - Normung PY - 2019 UR - https://www.irb.fraunhofer.de/literaturbeschaffung.jsp SN - 978-3-943563-05-4 SP - 151 EP - 157 PB - TAE Selbstverlag CY - Ostfildern AN - OPUS4-50044 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Otremba, Frank A1 - Romero-Navarrete, José A. A1 - Lozano Guzmán, A. A. T1 - A real-time GPS scheme to assess safe driving skills N2 - GPS-data based calculation scheme for assessing, in real-time, the level of safety exerted during driving, has been described and used. The several variables involved considered the main factors that lead to road mishaps, including the speed, the acceleration and the effects that these variables have on the vehicle when it is negotiating a turn. The performance measure combines three individual performance outputs: speed, acceleration and a hybrid performance measure considering the speed, the acceleration and the change in latitude/longitude. The measures are designed in such a way that weighting factors can be calibrated in order to establish certain critical parameters. On the other hand, the terms in the equations preclude any division by zero of the involved ratios. On the other hand, the simplicity of the equations makes it possible to carry out the assessment in real time. The use of the resultant performance measure to a relatively long path, together with its current average value, indicates that the safe performance of the driving changes with time, and that, for the selected values of the calibration constants, the traveling speed dominates the overall safety performance of the driving. Furthermore, the different calibration constants provide the possibility of considering different types of hazmat carrying vehicles. While many other formulation components could be integrated into the performance measure, this three-component performance measure could be used to assess the driving of a hazmat-carrying vehicle, in order to detect and to prevent dangerous conditions, such as driver fatigue. Finally, the implementation of the different performance measure formulations in a system such as the one described in the introduction of this paper, could be straightforward. T2 - ICASAT – 2019 – IEEE international Conference on Applied Science and Advanced Technology CY - Queretaro, México DA - 27.11.2019 KW - GPS KW - Scheme KW - Safe KW - Driving PY - 2019 SP - 1 EP - 6 AN - OPUS4-49984 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Frei, Vivian A1 - Thiele, Marc A1 - Pirskawetz, Stephan A1 - Meng, Birgit A1 - Rogge, Andreas T1 - Characterizing the Fatigue Behavior of High-Performance Concrete for Wind Energy Structures N2 - Severe mechanical fatigue conditions for worldwide proliferating windfarms are a Major challenge for high-performance concrete in towers, connecting joints and foundations of wind turbines. High-performance concrete offers potential for the application in offshore windfarms, not only regarding its good mechanical, but also chemical resistivity due to low diffusivity in the highly densified microstructure. For a more reliable fatigue assessment, monitoring based on nondestructive testing can be a valuable complement to design rules. Both approaches demand reliable experimental data, information about scalability and the development of standardized testing methods. This article presents results of an ongoing research program of BAM (Bundesanstalt für Materialforschung und -prüfung), which is a part of a joint national project (WinConFat) funded by the German Federal Ministry for Economic Affairs and Energy. The subproject implemented by BAM examines the fatigue behavior in dependence of size and slenderness for varying concrete strength at different stress levels. Besides fatigue strength, nondestructive testing is carried out additionally. Methods used are strain measurement and ultrasonic testing. The change of strain, stiffness and ultrasonic pulse velocity in the fatigue process is discussed. Results disclose a deeper insight into the damage process under cyclic loading of high-performance concrete and contribute to improve nondestructive monitoring. T2 - LORCENIS - Long Lasting Reinforced Concrete fpr Energy Infrastructure under Severe Operating Conditions CY - Ghent, Belgium DA - 10.09.2019 KW - Compressive Cyclic loading KW - Fatigue KW - High-strength concrete KW - Non destructive testing KW - Ultrasonic testing PY - 2019 SN - 978-9-463-88638-3 SP - 1 EP - 4 AN - OPUS4-49500 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Linnemann, Konrad A1 - Ballheimer, Viktor A1 - Sterthaus, Jens A1 - Rolle, Annette A1 - Wille, Frank A1 - Vlassopoulos, Efstathios A1 - Papaioannou, Dimitrios T1 - Numerical Simulation of Spent Fuel Segments under Transport Loads N2 - Packages for the transport of spent nuclear fuel shall meet the International Atomic Energy Agency regulations to ensure safety under different transport conditions. The physical state of spent fuel and the fuel rod cladding as well as the geometric configuration of fuel assemblies are important inputs for the evaluation of package capabilities under these conditions. Generally, the mechanical behavior of high burn-up spent fuel assemblies under transport conditions shall be analyzed with regard to the assumptions which are used in the containment and criticality safety analysis. Considering the complexity of the interactions between the fuel rods as well as between the fuel assemblies, basket, and cask containment, the exact mechanical analysis of such phenomena is nearly impossible. The gaps in Information concerning the material properties of cladding and pellet behavior, especially for the high burn-up fuel, make the analysis more complicated additionally. As a result, enveloping analytical approaches are usually used by BAM within the safety assessment of packages approved for transport of spent nuclear fuel. To justify the safety margins of such approaches additional analyses are necessary. In this paper, numerical simulations of a spent fuel assembly Segment are presented. The segment modeled represents the part of a generalized BWR fuel assembly between two spacers. Dynamic and quasi-static finite element calculations are performed to simulate the spent fuel behavior under regulatory defined accident conditions of transport. Beam elements are used for the modeling of the fuel rods representing the compound consisting of claddings and fuel pellets. The dynamic load applied is gathered from an experimental drop test with a spent fuel cask performed at BAM. A hot cell bending test performed at JRC Karlsruhe is the basis for obtaining the material behavior of the fuel rods. The material properties are determined by simulating the test setup of JRC and optimizing the results to fit the experimental load deflection curve. The simulations of the fuel assembly segment are used to get a better understanding about the loads on fuel rods under accident conditions of transport. T2 - 17th International High-Level Radioactive Waste Management Conference (IHLRWM 2019) CY - Knoxville, Tennessee, USA DA - 14.04.2019 KW - Spent Nuclear Fuel KW - Finite Element Simulation KW - Transport packages PY - 2019 SN - 978-1-51088-669-8 SP - 1 EP - 7 AN - OPUS4-52046 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pirskawetz, Stephan A1 - Hüsken, Götz A1 - Gründer, Klaus-Peter A1 - Kadoke, Daniel ED - Caspeele, R. ED - Taerwe, L. ED - Frangopol, D. M. T1 - Damage mechanisms analysis of reinforced concrete beams in bending using non-destructive testing N2 - Beams that are loaded in transverse direction are one of the main structural elements used in reinforced concrete structures. Bending beams are used, for example, in bridge girders or joists. The strength related failure modes at maximum loading can be divided into bending and shear failure that could occur with or without indication. Conventional design concepts used in practice for designing structural elements subjected to bending aim at failure modes with sufficient indication (e.g. large deflections or cracks), as it occurs in the case of secondary flexure-compression-failure. These indicators can also be used to identify structural changes of civil infrastructure systems (e.g. bridges) using non-destructive testing methods for Structural Health Monitoring (SHM). However, profound knowledge on the determining failure modes of bending beams is required for the reliable application of structural health monitoring. Therefore, resulting effects of different thermal and mechanical loads on the response of a structure are investigated by means of a bridge demonstrator. The results of this investigation are used for developing a monitoring system. Different non-destructive testing (NDT) methods have been used for analyzing the deformation behavior of a reinforced concrete beam in bending. The suitability of the different measuring techniques will be discussed by means of the obtained experimental results. For this purpose, the deformation behavior of a reinforced concrete beam having a span of 2.75 m was investigated in a four-point bending flexural test at laboratory scale. The focus is on the characterization of determining failure modes by the NDT methods and the comparison with classical measuring techniques (e.g. deformation measurements by displacement transducers). The bending tests have been accompanied by Acoustic Emission analysis (AE), optical deformation measurements using Stereophotogrammetry (SP) and Digital Image Correlation (DIC). The conducted tests have shown that the three-dimensional detection of deformations and resulting strains with optical techniques is beneficial for analyzing the damage mechanism of loaded structures and related crack formation and propagation. Optical techniques can be supplemented by acoustic emission testing which gives detailed information on crack formation and progressing damage. The combination of both techniques offers the application as efficient monitoring system for larger structures. T2 - Sixth International Symposium on Life-Cycle Civil Engineering (IALCCE 2018) CY - Ghent, Belgium DA - 28.10.2018 KW - Concrete Beam KW - Bending KW - Digital Image Correlation KW - Stereophotogrammetry KW - Acoustic Emission Analysis KW - Non-Destructive Testing PY - 2019 SN - 978-1-138-62633-1 SN - 978-1-315-22891-4 SP - 2411 EP - 2417 PB - CRC Press AN - OPUS4-46439 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gröke, Carsten A1 - Neumann, Martin A1 - Komann, Steffen A1 - Wille, Frank T1 - Anforderungen an die Bauartprüfung und Maßnahmen zur Qualitätssicherung für nicht zulassungspflichtige Versandstücke N2 - Überblick über die Regelwerksanforderungen an die Bauarten von nicht zulassungspflichtigen Versandstücken, sowie die zu erfüllenden Maßnahmen zur Qualitätssicherung für die Auslegung, die Herstellung und den Betrieb. T2 - KONTEC 2019 CY - Dresden, Germany DA - 27.03.2019 KW - Radioaktiv KW - Beförderung KW - IP-2 KW - IP-3 KW - Typ A KW - Anerkennung KW - Bauartprüfung PY - 2019 SP - 136 EP - 142 AN - OPUS4-56343 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rappsilber, Tim A1 - Krüger, Simone A1 - Below, Philipp T1 - Wood crib fire tests to evaluate the influence of extinguishing media and jet type on extinguishing performance at close range N2 - This paper is intended to be the first study to discuss the fire suppressing performance of the four most common extinguishing media under the same reproducible conditions. The tests were performed in bench-scale and used standardized 5A wood cribs as well as a miniature extinguishing system with a liquid flow rate of 1.4 lmin−1. The tests results present a consistent overview of the fire suppression efficacies of water, water with a foaming agent, nozzle-aspirated foam and compressed air foam. Depending on their jet types, the cooling capabilities of the extinguishing media water and water with a foaming agent were compared to the cooling capability of a full Jet of wet, general and dry foams. The results show that compressed air foam suppressed fire most effectively under the test conditions. Because of the convoluted crib structure, water and water with foaming agents used from a distance are more effective in the form of a full jet rather than a spraying jet. At close range, spraying jets multiply their effectiveness. A slight difference can be observed in the cooling performance of extinguishing foams that use foaming agents from different manufacturers. The paper establishes a link between the foaming agent's cooling capability and its wetting power by relating the results of wood crib fire tests according to DIN EN 3–7 and findings from laboratory immersion tests compliant with DIN EN 1772. KW - CAF KW - Druckluftschaum KW - Löschen KW - Krippe PY - 2019 DO - https://doi.org/10.1016/j.firesaf.2019.04.014 SN - 0379-7112 SN - 1873-7226 VL - 106 SP - 136 EP - 145 PB - Elsevier Ltd. AN - OPUS4-47996 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Winkler, Nicolas P. A1 - Neumann, Patrick P. A1 - Hüllmann, Dino A1 - Kohlhoff, Harald A1 - Bartholmai, Matthias A1 - Bennetts, V. H. A1 - Lilienthal, A. J. T1 - Remote Gas Sensing with Multicopter-Platforms N2 - This presentation gives an introduction to the gas-sensitive aerial robots developed at BAM, including various application examples in the field of mobile robot olfaction: gas source localization and gas distribution mapping. T2 - Zweites Innovationsforum "Autonome, mobile Dienste; Services für Mobilität" CY - Berlin, Germany DA - 04.06.2019 KW - Tunable Diode Laser Absorption Spectroscopy (TDLAS); UAV-REGAS KW - Localization of gas sources KW - Mobile Robot Olfaction KW - Nano UAV Swarm KW - Tomographic reconstruction of gas plumes PY - 2019 UR - http://modisem.de/files/Ereignisse/2019-06/Innovationsforum_Downloads/IF2_2019_Tagungsband_WEB.pdf SN - 978-3-942709-22-4 N1 - Tagungsband auf Deutsch, Beitrag auf Englisch. VL - 2019 SP - 24 EP - 34 AN - OPUS4-48699 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Wu, Cheng-Chieh T1 - The measurement- and model-based structural analysis for damage detection T1 - Schadensfrüherkennung mittels messungs- und modellbasierter Strukturanalyse N2 - The present work is intended to make a contribution to the monitoring of civil engineering structures. The detection of damage to structures is based on the evaluation of spatially and temporally distributed hybrid measurements. The acquired data can be evaluated purely geometrically or physically. It is preferable to do the latter, since the cause of damage can be determined by means of geometrical-physical laws in order to be able to intervene in time and ensure the further use of the structures. For this reason, the continuum mechanical field equations in conjunction with the finite element method and hybrid measurements are combined into a single evaluation method by the adjustment calculation. This results in two challenges. The first task deals with the relationship between the finite element method and the method of least squares. The finite element method solves certain problem classes, which are described by a system of elliptical partial differential equations. Whereas the method of least squares solves another class of problems, which is formulated as an overdetermined system of equations. The striking similarity between both methods is known since many decades. However, it remains unresolved why this resemblance exists. The contribution is to clarify this by examining the variational calculus, especially with regard to its methodological procedure. Although the well-known Gauss-Markov model within the method of least squares and the finite element method solve inherently different problem classes, it is shown that both methods can be derived by following the same methodological steps of the variational calculus. From a methodical viewpoint, this implies that both methods are not only similar, but actually the same. In addition, it is pointed out where a possible cross-connection to other methods exists. The second task introduces a Measurement- and Model-based Structural Analysis (MeMoS) by integrating the finite element method into the adjustment calculation. It is shown in numerical examinations how this integrated analysis can be used for parameter identification of simple as well as arbitrarily shaped structural components. Based on this, it is examined with which observation types, with which precision and at which location of the structure these measurements must be carried out in order to determine the material parameters as precisely as possible. This serves to determine an optimal and economic measurement set-up. With this integrated analysis, a substitute model of a geometrically complex structure can also be determined. The issue of the detection and localisation of damage within a structure is studied by means of this structural analysis. The Measurement and Model-based Structural Analysis is validated using two different test setups, an aluminum model bridge and a bending beam. N2 - Die vorliegende Arbeit soll einen Beitrag zur Überwachung von Ingenieurbauwerken leisten. Die Detektion von Schäden an Bauwerken basiert auf der Auswertung von räumlich und zeitlich verteilten Hybridmessungen. Die erfassten Daten können rein geometrisch oder physikalisch ausgewertet werden. Letzteres ist vorzuziehen, da die Schadensursache mittels geometrisch-physikalischer Gesetze ermittelt werden kann, um rechtzeitig eingreifen und die weitere Nutzung der Bauwerke sicherstellen zu können. Aus diesem Grund werden die kontinuumsmechanischen Feldgleichungen in Verbindung mit der Finite-Elemente-Methode und Hybridmessungen durch die Ausgleichungsrechnung zu einer einzigen Auswertemethode kombiniert. Dabei ergeben sich zwei Aufgabenstellungen. Die erste Aufgabe beschäftigt sich mit der Beziehung zwischen der Finite-Elemente-Methode und der Ausgleichungsrechnung. Die Finite-Elemente-Methode löst bestimmte Problemklassen, die durch ein System elliptischer partieller Differentialgleichungen beschrieben werden. Während die Methode der kleinsten Quadrate eine weitere Klasse von Problemen löst, die als ein überdeterminiertes Gleichungssystem formuliert ist. Die auffallende Ähnlichkeit zwischen den beiden Methoden ist seit vielen Jahrzehnten bekannt. Es bleibt jedoch ungeklärt, warum diese Ähnlichkeit besteht. Der Beitrag soll dies klären, indem die Variationsrechnung im Hinblick auf ihr methodisches Vorgehen untersucht wird. Obwohl das bekannte Gauß-Markov-Modell innerhalb der Methode der kleinsten Quadrate und die Finite-Elemente-Methode inhärent unterschiedliche Problemklassen lösen, wird gezeigt, dass beide Methoden durch die gleichen methodischen Schritte der Variationsrechnung abgeleitet werden können. Aus methodischer Sicht bedeutet dies, dass beide Methoden nicht nur ähnlich, sondern sogar gleich sind. Außerdem wird darauf hingewiesen, wo eine mögliche Querverbindung zu anderen Methoden besteht. Die zweite Aufgabenstellung stellt eine Messungs- und Modellbasierte Strukturanalyse (MeMoS) durch die Integration der Finite-Elemente-Methode in die Ausgleichungsrechnung vor. In numerischen Untersuchungen wird gezeigt, wie diese integrierte Analyse zur Parameteridentifikation sowohl einfacher als auch beliebig geformter Strukturbauteile eingesetzt werden kann. Darauf aufbauend wird untersucht, mit welchen Beobachtungstypen, mit welcher Genauigkeit und an welcher Stelle der Struktur diese Messungen durchgeführt werden müssen, um die Materialparameter möglichst genau zu bestimmen. Dies dient der Ermittlung eines optimalen und wirtschaftlichen Messaufbaus. Mit dieser integrierten Analyse kann auch ein Ersatzmodell einer geometrisch komplexen Struktur ermittelt werden. Die Frage der Erkennung und Lokalisierung von Schäden innerhalb einer Struktur wird mit Hilfe dieser Strukturanalyse behandelt. Die Messungs- und Modellbasierte Strukturanalyse wird mit zwei verschiedenen Testaufbauten, einer Aluminium-Modellbrücke und einem Biegebalken, validiert. KW - Damage detection KW - Continuum mechanics KW - Adjustment calculation KW - Finite element method KW - Variational calculus KW - Integrated analysis KW - Schadenserkennung KW - Kontinuumsmechanik KW - Ausgleichungsrechnung KW - Finite-Elemente-Methode KW - Variationsrechnung KW - Integrierte Analyse PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:101:1-2019100201583156925935 DO - https://doi.org/10.14279/depositonce-8845 SP - 1 EP - 169 PB - Technische Universität Berlin CY - Berlin AN - OPUS4-49288 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klimek, André A1 - Hothan, Sascha A1 - Rogge, Andreas T1 - Investigation of Size Effects in Concrete Spalling T1 - Untersuchung des Maßstabseffekts auf das Abplatzverhalten von Beton N2 - Spalling of concrete due to fire exposure can lead to severe damage of building components. It is a much discussed subject in structural engineering and not yet completely understood. Generally, it is assumed that thermohydraulic and thermomechanical processes induce tensile stresses in the concrete. Furthermore, the tensile strength of concrete is reduced due to increasing temperatures. The combination of an increasing tensile stress and a decreasing tensile strength result in the occurrence of explosive spalling. The spalling behaviour of concrete is influenced by many parameters, for instance the water cement ratio, porosity, permeability of concrete as well, the presence of steel reinforcement and polypropylene fibres, also the size and geometry of the fire exposed area. Within the current research project at Bundesanstalt für Materialforschung und prüfung (BAM), the susceptibility to spalling of six different concrete mixtures is analysed to quantify the size effect using small scale, intermediate scale and full scale tests. A special fire test setup was built to test specimens simultaneously to enable a better comparability. All specimens are tested without additional mechanical load and unrestraint to prevent external induced cracking at the fire exposed site. Thermocouples are used to measure in situ the temperature distribution as an indication on the thermal degradation of the concrete during the fire tests. Afterwards the maximum spalling depth and the damaged area of the specimen are illustrated by a photogrammetric measurement system. The contribution to the spalling workshop presents the results of four concrete mixtures tested in intermediate-scale and full-scale fire tests. The comparisons are based on the concrete temperature as well as the obtained photogrammetric data. The results show that the spalling depth and the spalling area are significantly affected by the size of the fire exposed area. T2 - 6th International Workshop on Concrete Spalling due to Fire Exposure CY - Sheffield, UK DA - 19.09.2019 KW - Concrete KW - Spalling KW - Fire Test KW - Photogrammetry KW - Size Effect PY - 2019 UR - https://firespallingworkshop2019.group.shef.ac.uk/wp-content/uploads/2019/09/Fire-Spalling-Workshop_Proceedings.pdf SN - 978-1-5272-4135-0 SP - 61 EP - 70 PB - The University of Sheffield CY - Sheffield AN - OPUS4-49254 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wu, Cheng-Chieh A1 - Weisbrich, S. A1 - Burger, M. A1 - Neitzel, F. T1 - A Four-Point Bending Test Apparatus for Measurement- and Model-based Structural Analysis N2 - By means of a small-scale truss bridge, the ability of the Measurement- and Model-based Structural Analysis to detect and localize damage was examined. Although there was no noteworthy difficulty in detecting damage, it turned out that damage localization responds sensitively to systematic influences, i.e. non-modelled properties of the mechanical model. Therefore, another experiment is being conducted to re-examine the Measurement- and Model-based Structural Analysis. For this purpose, the bending test is carried out as it has been already theoretically respectively numerically discussed. In this attempt, the systematic influences such as residual stress are kept as low as possible. T2 - 36th Danubia Adria Symposium on Advances in Experimental Mechanics CY - Pilsen, Czech Republic DA - 24.09.2019 KW - Damage detection KW - Adjustment calculation KW - Finite element method PY - 2019 SN - 978-80-261-0876-4 SP - 63 EP - 64 CY - Pilsen, Czech Republic AN - OPUS4-49290 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz ED - Lombaert, G. ED - Degrande, G. T1 - Predicted and measured amplitude-speed relations of railway ground vibrations at four German sites with different test trains N2 - The present contribution evaluates four measuring series made by the Federal Institute of Material Research and Testing for the relations between train speed and ground vibration amplitudes. This experimental evaluation is supported by the simulation of the train passages at the different sites by using appropriate excitation mechanisms and forces as well as layered soil models which have been derived from impact measurements at each site. T2 - 13th International Workshop on Railway Noise and Vibration CY - Leuven, Belgium DA - 16.09.2019 KW - Train speed KW - Ground vibration KW - Excitation forces KW - Layered soils PY - 2019 SP - 1 EP - 8 PB - KU Leuven CY - Leuven AN - OPUS4-49440 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz ED - Adam, C. T1 - Bahnerschütterungen bei verschiedenen Böden und Zuggeschwindigkeiten – Messungen in Deutschland, Österreich und der Schweiz N2 - Die Bundesanstalt für Materialforschung und -prüfung hat in den letzten 30 Jahren an vielen Orten Bahnerschütterungen gemessen. Dabei wurden immer auch Versuche zur Bestimmung der Bodeneigen-schaften durchgeführt, meist mit Hammeranregung, gelegentlich auch mit Schwingeranregung. Es werden verschiedene Auswertemethoden wie Seismogramm-Montage, Spektrale Analyse (SASW), Multistation Analysis of Surface Waves (MASW), f,v-Analyse (Dispersion aus zweifacher Fourier-Analyse), Spatial AutoCorrelation (SPAC, hier auch für deterministische Quellen) vorgestellt. Durch Approximation der frequenzabhängigen Wellengeschwindigkeiten (Dispersion) oder der gemessenen Übertragungsfunktionen erhält man ein passendes Bodenmodell. Zu diesem Bodenmodell kann man dann die Übertragungsfunktionen für Hammer- und Zuganregung berechnen. Mit allgemeinen oder spezifischen Achslastspektren werden dann die Bahnerschütterungen prognostiziert und mit den Messergebnissen verglichen. Bei etlichen Messorten, insbesondere in der Schweiz, wurden deutliche Merkmale einer Bodenschichtung beobachtet. Es ergibt sich eine deutliche Reduktion der tiefen Frequenzanteile durch den steifen unterliegenden Halbraum. Die weiche Deckschicht bestimmt das hochfrequente Verhalten. Hier bewirkt die Materialdämpfung des Bodens oft einen starken Amplitudenabfall, sowohl mit der Entfernung als auch mit der Frequenz. Für den verbleibenden mittelfrequenten Anteil wurde an mehreren Messorten die Amplituden-Fahrgeschwindigkeits-Gesetzmäßigkeiten untersucht. Es gibt konstante bis stark ansteigende Amplituden, und es zeigt sich auch hier, dass der geschichtete Boden von entscheidender Bedeutung ist. T2 - 16. D-A-CH Tagung Erdbebeningenieurwesen & Baudynamik (D-A-CH 2019) CY - Innsbruck, Austria DA - 26.09.2019 KW - Wellengeschwindigkeit KW - Dispersionsmessung KW - Bodenübertragungsfunktion KW - Bahnerschütterungen KW - Zuggeschwindigkeit PY - 2019 SP - 1 EP - 8 PB - Universität Innsbruck CY - Innsbruck AN - OPUS4-49441 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Otremba, Frank A1 - Romero-Navarrete, José A. ED - Otremba, Frank ED - Romero-Navarrete, José A. T1 - Sloshing in Vertical Circular Tanks and Earthquakes Perturbations N2 - A simplified formulation is proposed in this paper to assess the proximity of the earthquake-related Perturbation frequencies to the natural sloshing frequencies of the liquid contained in vertical cylindrical tanks. The methodology is based upon an existing gravity-waves approach, which was developed for rectangular cross-section reservoirs, and is extended in this paper to analyze circular cross-section tanks. The experimental outputs of this paper show that the existing methodology correlates at 100% with experimental data in the case of rectangular containers; while the corresponding average error in the case of a conical container and a cylindrical container is 7% and 9.1 %, respectively. The full diameter of the cross section was considered. The use of sovalidated methodology to full scale tanks, suggests that cylindrical vertical tanks with a capacity lower than 700 m3, could be exposed to a resonance excitation when subjected to earthquake motions, regardless of the fill level. T2 - WCECS 2019 CY - San Francisco, CA, USA DA - 22.10.2019 KW - Sloshing KW - Tanks KW - Earthquake KW - Perturbation PY - 2019 SP - 1 EP - 6 PB - IA ENG CY - San Francisco AN - OPUS4-49407 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Küttenbaum, Stefan A1 - Braml, T. A1 - Maack, Stefan T1 - Refining stochastic models for the reassessment of bridges using advanced NDT-methods N2 - Increasing requirements on the infrastructure caused by more and heavier traffic coincide with both the aging and the progressive degradation of bridge constructions. These exemplary issues lead to a non-negligible need for reassessments of existing bridges. Compared to the new building design, safety reserves can be used in the evaluation of such existing structures, since uncertainties that may arise during the design, construction and previous Service time are better known or no longer present. Uncertainties can be evaiuated more precisely by measurements. In the meantime, the application of advanced NDT-methods on concrete structures have become so capable, that crucial structure Parameters like certain material properties or geometrical dimensions can be quantified without significant destructive interventions. The measured data can be explicitly incorporated into the probabilistic computation models used for the bridge reassessment in form of random variables. Therewith, a previously insufficient model can be refined to achieve a higher level of approximation. This contribution emphasises two fundamental steps of the measured data based probabilistic reassessment: The sensitivity analyses to identify the cruciai Parameters and the needed accuracy of the related information as well as the comparison with expected uncertainties of non-destructively measured Parameters. T2 - 17th International Probabilistic Workshop CY - Edinburgh, UK DA - 11.09.2019 KW - Measurement KW - Reassessment KW - NDT KW - Concrete bridges PY - 2019 SP - 99 EP - 105 AN - OPUS4-48998 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Johann, Sergej A1 - Strangfeld, Christoph A1 - Zimmek, David A1 - Bartholmai, Matthias ED - Helmerich, Rosemarie ED - Ilki, A. ED - Motavalli, M. T1 - Smart electronic helper for long-term monitoring of bridges and building structures N2 - Increasing traffic volume on the one hand and ageing infrastructure on the other hand have created many new challenges for maintenance and structural health monitoring of roads and bridges. In the past, many bridges and road structures have been neglected, often resulting in traffic congestion, road closure, and increased repair costs. This research is concerned with the development of a system to improve the challenge of maintenance and early detection of damage, particularly moisture penetration and corrosion of steel reinforced concrete components. The objective is to develop a method that will also work after 30 years and longer. Many new IoT solutions are equipped with internal energy storage elements (accumulators or batteries) which are inappropriate here, since most relevant signs of concrete degradation occur after decades, where the functioning of such elements are more than questionable. The presented technology approach uses radio-frequency identification (RFID) and enables connectivity to sensors. It offers the advantage of an passive, completely independent energy supply without any energy storage components. Since the system should be permanently embedded in concrete, it is crucial to develop a long-term stable device which is adapted to the environmental influences of the structure, e.g., long-term resistance in very alkaline environment of pH 13. In numerous experiments, the robustness of the system was tested and evaluated. Various tests with encapsulations to protect the electronics were performed, and for long-term validation different concrete specimens were instrumented with RFID-sensor-systems. Their operating time is now around two years and investigations for signs of fatigue and damage to the encapsulation and the electronics are ongoing. T2 - 5th International Conference on Smart Monitoring, Assessment and Rehabilitation of Civil Structures (SMAR 2019) CY - Potsdam, Germany DA - 27.08.2019 KW - Long term monitoring KW - Passive RFID KW - SHM KW - Sensors KW - Smart structures PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-489890 SP - 1 EP - 6 PB - German Society for Non-Destructive Testing (DGZfP e.V.) AN - OPUS4-48989 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Romero Navaratte, José A. A1 - Otremba, Frank T1 - Scientific Society of Mechanical Engineers N2 - The efficiency and safety of railway transportation depends on many factors and operating conditions, associated to the vehicle, the infrastructure, the operator and the environment. From the vehicle-infrastracture perspective, some influential factors include the dynamics of the vehicle and infrastructure interaction when the vehicle operates on curved tracks. Düring such changes of direction, the vehicle dynamically responds to the lateral perturbation, producing a lateral load transfer that represents an increase of the wheel forces on one side of the track, as a function of the train operating conditions and track design, including track's geometry and over-elevation, and vehicle's operating speed as well as its inertial properties and dimensions. In this context, the lateral load transfer superimposes to tangential steering forces, which are developed when the vehicle enters the curved track, and stabilize once a steady state is attained if the vehicle travels along a constant radius track at constant speed. The magnitude of such tangential forces depends on a variety of factors, including the yaw stiffness of the bogie, and the friction at the centre plate. While the friction at the centre plate generates higher tangential forces on the track and a consequential greater rail wearing and lose of locomotive energy, such friction is also crucial to avoid the hunting phenomenon when the vehicle travels along tangents. In this paper, a mechanically active centre plate is proposed, which increases the friction torque at the centre plate when the vehicle travels along tangents, and reduces such a friction torque when the vehicle negotiates curved portions of the track. Such conceptual design includes the principles of Operation and a needed preliminary experimental model to assess the potential benefits as well as the feasibility of such equipment. T2 - 11th international conference on railway bogies and running gears CY - Budapest, Hungary DA - 09.09.2019 KW - Centre plate KW - Railway KW - Fiction PY - 2019 SP - 28 EP - 30 AN - OPUS4-49004 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jonietz, Florian A1 - Krankenhagen, Rainer A1 - Altenburg, Simon A1 - Eisenkrein-Kreksch, H. T1 - Standardisierung eines thermografischen Verfahrens zur Schichtdickenbestimmung von Beton-Oberflächenschutzsystemen N2 - Polymerbeschichtungen auf Beton bieten einerseits mechanischen Schutz vor Beschädigungen und verhindern das Eindringen von Wasser, gelösten Salzen und CO2 und können andererseits der Oberfläche ein gewünschtes Aussehen geben. Daher werden sie in der Bauindustrie insbesondere bei Brücken und Parkhäusern häufig verwendet. Für die beabsichtigte Wirkung der Beschichtung ist deren Schichtdicke ein entscheidender Faktor und muss daher nach Aufbringung der Schicht und im Betrieb regelmäßig überprüft werden. Üblich sind hier zerstörende Verfahren mit nachträglich erforderlicher Ausbesserung. Im Rahmen eines Vorgängerprojektes wurde an der BAM in Kooperation mit der IBOS GmbH ein zerstörungsfreies Verfahren entwickelt, welches auf aktiver Thermografie basiert. Ein Prototyp mit Halogenlampe und Infrarot-Kamera wurde erprobt. Das hier beschriebene Folgeprojekt hat das Ziel, dieses Verfahren zu standardisieren, damit es sich in der Industrie als zerstörungsfreies Alternativverfahren zur Schichtdickenbestimmung durchsetzt. Im ersten Schritt wird gezeigt, bei welchen Oberflächenschutzsystemen das Verfahren bereits zuverlässige Schichtdickenmessungen ermöglicht und praxistauglich ist. Anschließend werden weitere Forschungsthemen definiert und bearbeitet, die eine Anwendung für alle Oberflächenschutzsysteme ermöglichen sollen. Besondere Herausforderungen stellen etwa Sandeinstreuungen in der Polymerschicht dar. Auch muss der Frage nach der Anwendbarkeit auf Mehrschichtsysteme nachgegangen werden. Des Weiteren stellt sich die Frage nach dem Einfluss der Beschaffenheit des Betonuntergrunds auf die Anwendbarkeit des Verfahrens. Im zu erarbeitenden Normentwurf sollen diese Untersuchungen die Möglichkeiten, aber auch die Grenzen der aktiven Thermografie zur Schichtdickenmessung von Oberflächenschutzsystemen aufzeigen. Im Beitrag werden die systematischen Untersuchungen bezüglich dieser Fragestellungen dargelegt. T2 - DACH-Jahrestagung 2019 CY - Friedrichshafen, Germany DA - 27.05.2019 KW - thermografisches Verfahren KW - Standardisierung KW - Schichtdickenbestimmung KW - Beton-Oberflächenschutzsysteme KW - Polymerbeschichtungen auf Beton PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-490093 UR - http://www.ndt.net/?id=24548 SN - 978-3-947971-02-2 VL - 171 SP - Mi.1.C.4-1 EP - Mi.1.C.4-9 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-49009 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sklorz, Christian A1 - Balke, Christian A1 - Otremba, Frank T1 - Fire protection systems for above-ground storage tanks N2 - Liquefied propane gas (LPG) tanks in a fully engulfing accidental fire experience a fast increase in internal pressure. The result is often a Boiling Liquid Expanding Vapor Explosion (BLEVE) that can result in a large fireball and flying debris over a radius of more than 100 meters. In the last 30 years BAM has carried out more than 30 real scale fire tests on propane storage vessels across three test sites. The primary research goal was to identify systems that can delay or prevent a BLEVE. Early studies started with water deluge systems, and have since moved on to consider alternative protection systems. It has been shown that an unprotected vessel fails within 10 minutes or less. Tests with different oil and propane fueled fires have given an overview on possible real accidents involving full-engulfing scenarios. LPG tanks of various sizes (2.7 m³, 3.6 m³, 4.8 m³, 6.7 m³) were used with different filling levels. Numerous protection systems, ranging from active systems like water systems to passive thick- and thin-film layers. Also, the degree of thickness of these layers was variated. Pressure relief valves (PRV) have also been investigated, both alone and in combination with protection systems. This paper gives an overview of the work performed by BAM in the field of BLEVE prevention of protecting system since the last 30 years. It has been shown that e.g. with a full applied coating degree on the tank with and without PRV can be reached an exposition in a test fire scenario a duration of more than 60min. For partly coated tanks with and without PRV the duration time is like an unprotected vessel. Furthermore, it could be shown that the active water system also protects with technically correct design. T2 - Loss Prevention 2019 CY - Delft, Niederlande DA - 16.06.2019 KW - Fire KW - Protection systems KW - Propane storage tanks PY - 2019 SN - 978-88-95608-72-3 VL - 75 SP - 1 EP - 6 AN - OPUS4-49021 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stelzner, Ludwig A1 - Weise, Frank A1 - Oesch, Tyler A1 - Dlugosch, R. A1 - Powierza, Bartosz T1 - Transport and reconfiguration of moisture in HPC due to unilateral heating N2 - Explosive spalling is caused by, among others, the thermohydraulic spalling mechanism. During this process, vaporization, dehydration, moisture-transport and condensation processes interact. As a result, a drying and dehydration zone as well as a saturated zone, known as a moisture clog, are observed inside the unilaterally-heated concrete. The presented research is focused on the experimental investigation of the underlying thermohydraulic processes. To investigate these, a test methodology based on X-ray computed tomography (CT) and nuclear magnetic resonance (NMR) was developed. Thereby, the X-ray CT scans are carried out simultaneously during the application of a defined unilateral-heating regime on a specially-constructed specimen. This miniaturized specimen, equipped with a double-layer casing, reproduces the condition within a planar, unilaterally-heated building component. A preliminary test methodology and the first experimental results were presented at the 5th International Workshop on Concrete Spalling in Borås, Sweden (2017). The contribution for the upcoming workshop presents an improved version of this test methodology and new results for a high-performance concrete (HPC) mixture exposed to temperatures up to 500 °C. Regarding the CT measurements, a higher time-resolution of 15 min was achieved and a quantification of the moisture changes was implemented. Due to an increase in signal quality of the NMR measurements, a pore-size specific moisture distribution can now be resolved. This allows to conclude about the moisture reconfiguration between small gel pores and larger interhydrate pores. Additionally, the NMR measurement are no longer limited to first 2.5 cm below the heated surface but a one-dimensional moisture distribution can now be estimated over the whole 10 cm long specimen. The presented results demonstrate that the combination of X-ray CT and NMR measurements enables to image and quantify the thermally-induced moisture transport and reconfiguration from small gel pores up to macro pores. This provides important insights into the thermohydraulic damage mechanism and leads to a better understanding of spalling avoidance strategies, like the addition of polypropylene fibres. T2 - 6th International Workshop on Concrete Spalling due to fire exposure CY - Sheffield, UK DA - 19.09.2019 KW - Moisture clog KW - X-ray CT KW - NMR KW - Moisture transport KW - HPC PY - 2019 UR - https://firespallingworkshop2019.group.shef.ac.uk/wp-content/uploads/2019/09/Fire-Spalling-Workshop_Proceedings.pdf SN - 978-1-5272-4135-0 SP - 181 EP - 190 CY - Sheffield AN - OPUS4-49161 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baensch, Franziska A1 - Brunner, A. J. ED - Rosemarie, Helmerich ED - Ilki, A. ED - Motavalli, M. T1 - Towards predictor development for assessing structural integrity of components made from wood materials using Acoustic Emission monitoring and signal analysis N2 - Against the background of sustainable resource management and efficiency, wood-based materials are currently experiencing a revival and, among others, plywood, Laminated Veneer Lumber and glued laminated timber are becoming increasingly more important in the building sector. Even though these materials are so-called engineered products, the element wood is naturally grown with intrinsic variability in mechanical properties and requires professional handling on-site. Otherwise, load-bearing structures made of wood materials may entail certain risks. Critical situations can, in principle, be avoided by implementing a structural health monitoring system into components or structures made from wood material. The aim is to indicate accumulation of mechanical damage and to eliminate or at least significantly reduce the risk of unexpected failure. Toward this purpose, the failure behavior of several layered wood materials under quasi-static tension was investigated in laboratory-scale experiments by means of acoustic emission (AE) measurement. Based on spectral analysis and pattern recognition, two classes of AE signals are identified for each investigated lay-up that are characterized by either low or high frequency contents in the respective power spectra. AE activity and intensity of both signal classes are analyzed, striving for predictors appropriate for AE monitoring concepts. T2 - 5th International Conference on Smart Monitoring, Assessment and Rehabilitation of Civil Structures (SMAR 2019) CY - Potsdam, Germany DA - 27.08.2019 KW - Acoustic Emission Monitoring KW - Signal Analysis KW - Structural Integrity KW - Wood Materials PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-491198 SN - 978-3-947971-07-7 SP - Paper Tu.2.D.4, 1 EP - 8 PB - German Society for Non-Destructive Testing (DGZfP e.V.) AN - OPUS4-49119 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wosniok, Aleksander A1 - Jansen, R. A1 - Chen, L. A1 - Toet, P. A1 - Doppenberg, E. A1 - De Jong, W. A1 - Chruscicki, Sebastian T1 - Static load monitoring of a concrete bridge using a high-precision distributed fiber optic sensor system N2 - In the present study, the impact of static traffic loading on the slight deflection effects in the concrete structure of an existing bridge has been investigated using distributed fiber optic sensors. In the face of increasing traffic density and severe traffic loading, the results of the load tests on the Amsterdam bridge 705 make an important contribution to the understanding of its structural behavior. The concept of the static loading was based on the use of two 36-ton trucks stopped on the bridge at multiple pre-determined locations. The load applied in this way led to location-dependent small deflection effects recorded as longitudinal strain of the sensing fiber embedded at the underside of the bridge. The measurements were performed with a commercially-available solution based on Tunable Wavelength Coherent Optical Time Domain Reflectometry with the measurement accuracy in the range of 0.5 µm/m. T2 - 5th International Conference on Smart Monitoring, Assessment and Rehabilitation of Civil Structures CY - Potsdam, Germany DA - 27.08.2019 KW - Bridge monitoring KW - Distributed fiber optic sensing KW - Static load monitoring KW - TW-COTDR PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-490408 SP - 1 EP - 8 AN - OPUS4-49040 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baeßler, Matthias A1 - Bhuyan, Delwar A1 - Hille, Falk A1 - Viefhues, Eva A1 - Döhler, M. A1 - Mevel, L. ED - Zingoni, Alphose T1 - Impact of environmental based effects on SHM strategies N2 - Environmental based perturbations influence significantly the ability to identify structural dam-age in Structural Health Monitoring. Strategies are needed to classify such effects and consider them appropri-ately in SHM. It has to be considered if seasonal effects just mask the structural response or if temperature itself correlates to a weakening of the structure. Various methods have been developed and analyzed to separate environmental based effects from damage induced changes in the measures. Generally, two main approaches have emerged from research activity in this fields: (a) statistics-based tools analyzing patterns in the data or in computed parameters and (b) methods, utilizing the structural model of the bridge considering environmental as well as damage-based changes of stiffness values. With the background of increasing affordability of sensing and computing technology, effort should be made to increase sensitivity, reliability and robustness of proce-dures, separating environmental from damage caused changes in SHM measures. The contribution describes an attempt to evaluate both general strategies, their advantages and drawbacks. In addition, two vibration moni-toring procedures are introduced, allowing for temperature-based perturbations of the monitoring data. T2 - SEMC 2019 CY - Cape Town, South Africa DA - 02.09.2019 KW - SHM environmental bridges PY - 2019 SN - 978-1-138-38696-9 SN - 978-0-429-42650-6 DO - https://doi.org/10.1201/9780429426506 SP - Paper 324, 1 EP - Paper 324, 6 PB - CRC Press CY - Boca Raton AN - OPUS4-49167 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Vössing, Konrad A1 - Gaal, Mate A1 - Niederleithinger, Ernst ED - Ross, R. ED - Sauter, U. T1 - Contactless testing of wood-based materials with novel air-coupled ultrasonic transducers N2 - The detection of delamination, rot and cracks causing a decrease of strength in wooden construction elements is a key task for nondestructive testing (NDT). Air-coupled ultrasound (ACU) is used to detect flaws without having to provide contact to the surface or otherwise affect the object. Novel ferroelectric transducers with a high signal-to-noise ratio enable an accurate flaw detection. Transducers made of cellular polypropylene (PP) are suitable for characterizing wood-based materials (WBM) because their extremely low Young’s modulus and low density mean a favorable acoustic impedance for the transmission of ultrasonic waves between the transducer and air. The transducers can be applied during the production of WBM and during its service life. The device enables a fast in-situ recognition of defects with frequencies between 90 kHz and 250 kHz. Measurements can be performed in through transmission for a high resolution or in pulse-echo technique in case of one-sided access at the expense of reduced signal strength. Ultrasonic quality assurance for wood is an important attempt to increase the acceptance of wooden structures and towards sustainability in civil engineering in general. T2 - 21. International Nondestructive Testing and evaluation of Wood Symposium CY - Freiburg, Germany DA - 24.09.2019 KW - Air-coupled ultrasound KW - Defect detection KW - Nondestructive Testing KW - Timber PY - 2019 SP - 100 PB - FVA CY - Freiburg AN - OPUS4-49169 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mair, Georg W. A1 - Saul, Herbert A1 - Wang, Bin T1 - Safety criteria for the transport of hydrogen in permanently mounted composite pressure vessels N2 - The recent growing of the net of hydrogen fuelling stations increases the demands to transport compressed hydrogen on road by batterie vehicles or tube-trailers, both in composite pressure vessels. As transport regulation the ADR is applicable in Europe and adjoined regions and used for national transport in EU. This regulation provides requirements based on the burst pressure of each individual pressure vessel, regardless the capabilities of the transported hydrogen and relevant consequences resulting from worst case scenarios. In 2012, BAM (German Federal Institute for Materials Research and Testing) introduced consequence-dependent requirements and established them in national requirements concerning the “UN service life checks” etc. to consider the transported volume and pressure of gases. However, this results in a stringent requirement in case of using large pressure vessels (so called “tubes”) on vehicles. In the studies presented here, the safety measures for hydrogen road transport are identified and reviewed through some safety measures from some countries like Japan, USA and China. Subsequently, the failure consequences of using trailers, the related risks and chances are evaluated. Finally, a chance-related risk criterion is suggested to add into regulations and consequently to be defined as safety goal in standards for hydrogen transport vehicles and consequently for mounted pressure vessels. T2 - ICHS International Conference on Hydrogen Safety) 2019 CY - Adelaide, Australia DA - 24.09.2019 KW - pressure-volume product KW - probabilistic approach KW - hydrogen transport KW - risk limit KW - F-N-diagram KW - maximum acceptable consequence KW - chance-risk analysis KW - specific risk value PY - 2019 SP - 104-01 EP - 104-15 PB - International Association for Hydrogen Safety (HySafe) CY - Adelaide AN - OPUS4-50124 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wang, Bin A1 - Mair, Georg W. A1 - Gesell, Stephan T1 - Determination of Distribution Function used in MCS on Safety Analysis of Hydrogen Pressure Vessel N2 - The test data of static burst strength and load cycle strength of composite pressure vessels are often described by GAUSSian normal or WEIBULL distribution function to perform safety analyses. The goodness of assumed distribution function plays a significant role in the inferential statistics to predict the population properties by using limited test data. Often, GAUSSian and WEIBULL probability nets are empirical methods used to validate the distribution function; Anderson-Darling and Kolmogorov-Smirnov tests are the mostly favorable approaches for Goodness of Fit. However, the different approaches used to determine the parameters of distribution function lead mostly to different conclusions for safety assessments. In this study, six different methods are investigated to show the variations on the rates for accepting the composite pressure vessels according to GTR No. 13 life test procedure. The six methods are: a) Norm-Log based method, b) Least squares regression, c) Weighted least squares regression, d) A linear approach based on good linear unbiased estimators, e) Maximum likelihood estimation and f) The method of moments estimation. In addition, various approaches of ranking function are considered. In the study, Monte Carlo simulations are conducted to generate basic populations based on the distribution functions which are determined using different methods. Then the samples are extracted randomly from a population and evaluated to obtain acceptance rate. Here, the “populations” and “samples” are corresponding to the burst strength or load cycle strength of the pressure vessels made from composite material and a plastic liner (type 4) for the storage of hydrogen. To the end, the results are discussed, and the best reliable methods are proposed. T2 - ICHS International Conference on Hydrogen Safety) 2019 CY - Adelaide, Australia DA - 24.09.2019 KW - Monte-Carlo Simulation KW - Distribution function KW - Weibull Distribution PY - 2019 SP - 103-1 EP - 103-16 AN - OPUS4-50383 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mair, Georg W. A1 - Gesell, Stephan T1 - Betriebsfestigkeit von Composite-Wasserstoffspeichern Erster Ansatz zur Simulation der Auswirkung der erstmaligen Prüfung N2 - Druckbehälter werden vor ihrer Inbetriebnahme obligatorisch einer hydraulischen Prüfung bis zum sog. Prüfdruck belastet. Damit sollen fehlerhaft gefertigte Individuen erkannt und ausgesondert werden. Mit dieser Prüfung werden aber auch diejenigen Einzelbehälter ausgesondert, die ohne einem nachvollziehbaren Fertigungsfehler, nur auf Basis der statistischen Streuung ggf. eine Festigkeit unterhalb des Prüfdrucks aufweisen. Da der Prüfdruck im Fall der Wasserstoffspeicher mindestens 20% über dem maximal zulässigem Betriebsdruck liegt, wäre damit ein Versagen im Betrieb ausgenommen, gäbe es die verschiedenen Alterungs- bzw. Ermüdungseffekt nicht. Um den Einfluss der erstmaligen Prüfung auf eine angenommene ausfallfreie Zeit bewerten zu können, wird hier die Alterung und die erstmalige Prüfung in Kombination analysiert. Hierzu wird auf Basis der Restfestigkeitsdaten aus einer umfangreichen Prüfkampagne ein Ansatz für die Beschreibung der Alterung ermittelt und auf andere Lastzustände übertragen. So kann für das Baumuster, das der o.g. Prüfkampagne zugrunde lag, mithilfe einer Monte-Carlo-Simulation gezeigt werden, dass mindestens 10.000 LW vor einem ersten Alterungsversagen mit 1 aus 1 Mio. In Abhängigkeit der Anzahl der Individuen, die bei der erstmaligen Prüfung versagen, und der Streuung der gesamten Population, kann diese Mindestfestigkeit auf realistisch 50.000 Lastwechsel steigen. Damit ist gezeigt, dass aufgrund der erstmaligen Prüfung eine Mindestfestigkeit erzeugt wird, die stark vom Alterungsverhalten abhängt. Im Ergebnis heißt dies, dass in den Vorschriften aktuell die Bedeutung des Mindestberstdrucks in der Baumusterprüfung überschätzt und die möglichst betriebsbegleitende Erfassung der Alterung unterschätzt sind. T2 - 29. Fachtagung Technische Zuverlässigkeit 2019 CY - Nürtingen, Germany DA - 07.05.2019 KW - Alterung KW - Berstdruck KW - Streuung KW - Degradation KW - statistische Auswertung KW - ausfgallfreie Lastwechsel PY - 2019 SN - 978-3-18-092345-1 SN - 0083-5560 SP - 223 EP - 234 PB - VDI-Verlag GmbH CY - Düsseldorf AN - OPUS4-50181 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quercetti, Thomas A1 - Scheidemann, Robert A1 - Komann, Steffen A1 - Ballheimer, Viktor A1 - Wille, Frank T1 - Package testing of a dual purpose cask for SNF from German research reactors N2 - A new dual purpose cask design was developed for the safe transport and interim storage of spent fuel elements of German research reactors. In the framework of the safety assessment within the licensing procedure the Bundesanstalt für Materialforschung und –prüfung (BAM) as competent authority performed a series of drop tests according to the IAEA-Regulations [1]. The package consists of a cylindrical thick-walled ductile cast iron cask body closed by a double lid system with metallic seals. A lid and bottom sided impact limiter consisting of a wood/steel construction limit the mechanical impact loading. The full-scale test specimen was equipped with a basket and assembled with dummy-fuel elements. The package and test specimen, respectively have a total mass of approximately 24 metric tons. The mechanical test program included three 9m free drop tests, in horizontal, vertical and oblique cask orientation onto the lid system. Additionally, a 1m-puncture drop test followed the horizontal drop test to consider an IAEA-test sequence. The horizontal and vertical drop tests were performed at a temperature of minus 40°C. During the oblique drop test the upper impact limiter was heated to +80°C. The tests were conducted onto an unyielding target, fulfilling the requirements of the IAEA regulations [1]. The test specimen was considerably instrumented with strain gauges and accelerometers. Transient strains at selected locations of the inner and outer container walls, of the primary and secondary lid, as well as of the corresponding lid bolts were measured during the drop tests. Furthermore, decelerations in different locations at the cask body and the lids were measured. The complex geometrical deformation of the impact limiters due to the impact were determined by optical 3d- measurements using the projected fringe method in combination with multi-image photogrammetry. Before and after the drop tests the leakage rate of the lid system was determined by helium leakage testing. The experimental results contribute to the evaluation of the package response to mechanical tests, demonstrating safety under normal and accident conditions of transport. Especially to the verification of the dynamic finiteelement model of the package used in the package design safety report [2]. The paper describes the performance of the drop tests, selected test results focusing on the lid screws and the cask body and the deformation of the impact limiters as well as impact kinematics, respectively. T2 - IHLRWM2019 CY - Knoxville, TN, USA DA - 14.04.2019 KW - Drop test KW - Package testing KW - Dual purpose cask PY - 2019 SN - 978-0-89448-761-3 VL - 2019 SP - paper 27283, 1 EP - 7 PB - ANS AN - OPUS4-50619 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schlick-Hasper, Eva A1 - Goedecke, Thomas A1 - Ackermann, M. A1 - Senkel, U. T1 - Staubdichtheit von Säcken und FIBC für feste Gefahrgüter - Eine kritische Betrachtung der derzeitigen Regelsetzung und Transportpraxis N2 - In den internationalen Gefahrgutvorschriften ist vorgeschrieben, dass Säcke und flexible Großpackmittel (Flexible Intermediate Bulk Container – FIBC) staubdicht sein müssen. Eine quantitative Definition des Terminus Staubdichtheit, wie in anderen Technikgebieten üblich, ist jedoch nicht gegeben. Auch geeignete Prüfverfahren zum Nachweis der Staubdichtheit sind in den Vorschriften nicht genannt. In der Praxis der stichpunkartigen Kontrollen von Gefahrguttransporten durch die Schwerlastgruppe der Autobahnpolizei Münster werden immer wieder Austritte von pulverförmigen oder körnigen Gefahrgütern aus eigentlich intakten Säcken und FIBC detektiert. Es wird ein Überblick über die im Jahr 2018 festgestellten Gefahrgutaustritte aus diesen Gefahrgutverpackungen sowie eine systematische Einordnung hinsichtlich betroffener Bauarten und möglicher Ursachen gegeben. Bei der Stofffreisetzung aus intakten Gefahrgutverpackungen liegt ein mechanischer Transport von Partikeln durch Leckkanäle, z. B. im Verschluss-, Naht- oder Wandungsbereich, vor. Generell kommen zwei Freisetzungswege in Frage: Einerseits eine Langzeit-Freisetzung während des Transports, hervorgerufen durch eine kombinierte Wirkung von Stapellast des Füllguts und Transportvibrationen; andererseits eine stoßartige Freisetzung. Auf Grundlage von durchgeführten Untersuchungen hinsichtlich der stoßartigen Freisetzung pulverförmiger Stoffe aus Gefahrgutsäcken werden erste Lösungsansätze hin zu einer Verbesserung der Staubdichtheit von Gefahrgutsäcken und -FIBC vorgestellt. Es wird ein Ausblick auf nachfolgende Arbeiten gegeben. T2 - 48. Jahrestagung der GUS 2019 CY - Stutensee, Ortsteil Blankenloch, Germany DA - 27.03.2019 KW - Gefahrgutverpackungen KW - Staubdichtheit KW - Säcke KW - FIBC PY - 2019 SN - 978-3-9818507-3-4 SP - 157 EP - 170 AN - OPUS4-47691 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Herrmann, Ralf A1 - Moortgat-Pick, A. A1 - Marx, S. ED - Helmerich, Rosemarie ED - Ilki, A. ED - Motavalli, M. T1 - Vibration Analysis of Structures using a Drone (UAV) based Mobile Sensing Platform N2 - The identification of the dynamic behavior of structures, like bridges and towers, is relevant to address multiple issues. In many cases the dynamic parameters should be acquired only once or at a frequency that doesn’t justify the installation of distinct vibration sensors for a long-term monitoring. To identify modal frequencies of a structure, a drone based mobile sensing platform has been implemented. This sensing platform measures the relative displacement be-tween the structure and the drone, which also shows a strong dynamic behavior under wind tur-bulences. By regarding the dynamic model of the drone and additional measurements at the dis-tance sensor the absolute movement of the structure can be estimated based on the measured relative distance. This time domain data is a suitable input for various operational modal analysis algorithms. The system has been used to identify the dynamic properties of test and real structure, like a 1.5 MW wind turbine tower. T2 - 5th International Conference on Smart Monitoring, Assessment and Rehabilitation of Civil Structures (SMAR 2019) CY - Potsdam, Germany DA - 27.08.2019 KW - Modal Analysis KW - Drone KW - Vibration KW - Wind Turbines KW - Bridges PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-492045 UR - http://data.smar-conferences.org/downloads/SMAR_2019_Proceedings.zip SN - 978-3-947971-07-7 SP - We.4.C.3 EP - 8 PB - German Society for Non-Destructive Testing (DGZfP e.V.) AN - OPUS4-49204 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kotschate, Daniel A1 - Gaal, Mate T1 - Plasma-akustische Wechselwirkungen von Mikrohohlkathodenentladungen N2 - Während des Entladungsprozesses interagieren Mikrohohlkathodenentladungen (engl. micro hollow cathode discharges) durch verschiedenste physikalische Phänomene mit ihrer Umgebung. Analog zu Funken- und Koronaentladung treten neben den optischen Erscheinungen auch akustische Wechselwirkungen bis in den Ultraschallbereich auf. Diese Wechselwirkungen sind bisher jedoch nur selten Gegenstand der Forschung gewesen. Durch elektro-chemischen Prozesse und die Stromdichteverteilung während des Zündvorgangs erfährt das angrenzende Fluid eine, durch den thermoakustischen Effekt hervorgerufene, rapide Dichteänderung und erzeugt somit eine akustische Emission. Dieser Beitrag gibt einen Überblick über den letzten Stand der akustischen Beschreibung der Mikrohohlkathode. Weiterhin wird anhand von Anwendungsbeispielen, wie der Charakterisierung von akustischen Sensoren, sowie der Nutzung innerhalb der zerstörungsfreien Werkstoffprüfung, die Nutzung dieser Entladungsart präsentiert. Darüber hinaus erlaubt die Kenntnis hinsichtlich der akustischen Eigenschaften der Entladung wichtige Rückschlüsse im Rahmen der Plasmadiagnostik. T2 - 45. Jahrestagung für Akustik (DAGA 2019) CY - Rostock, Germany DA - 18.03.2019 KW - Micro hollow cathode discharge KW - Atmospheric pressure plasma PY - 2019 SP - 1049 EP - 1051 AN - OPUS4-47790 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rica, S. A1 - Van Baars, S. A1 - Kullolli, Borana ED - Ülgen, D. ED - Saygili, A. ED - Kahyaoglu, M. R. ED - Durmaz, S. ED - Toygar, O. ED - Göcügenci, A. T1 - The importance of the horizontal stresses on the bearing capacity of a foundation pile N2 - In case one wants to predict or design the bearing capacity of a foundation pile and there are no possibilities to perform an in-situ test, such as a Cone Penetration Test, the pile bearing capacity is in most cases estimated with analytical formulas. The most known and used method is the Meyerhof method published some decades ago. There are also other design methods such as derived from a certain failure mechanism around the pile tip, which is, in most cases, wedge failure mechanism. This failure mechanism was originally developed for a shallow (infinite) strip foundation, though. Therefore, it represents a plane failure mechanism. Numerical simulations on loaded foundation piles performed with the Plaxis software Show however, that the failure mechanism of a foundation pile represents a far more complex threedimensional failure mechanism around the pile tip. In addition, the existing analytical methods for foundation piles are based on the vertical stresses in the soil, as if the failure mechanism is the same as of a shallow foundation. Numerical simulations, performed in Plaxis show that, not the vertical, but the horizontal stresses, play an important role on the pile bearing capacity. Plaxis represents the stresses in the soil by using the procedure. So, different horizontal soil stresses are obtained for different values of the lateral earth pressure coefficient. The results show that the pile tip bearing capacity depends strongly on the horizontal stresses in the soil, but only for. The same results were observed by using a Material Point Method (MPM). Consequently, the analytical methods should estimate the pile bearing. T2 - 1st Mediterranean Young Geotechnical Engineers Conference CY - Bodrum, Turkey DA - 23.09.2019 KW - Analytical Design Methods KW - Foundation Pile KW - Horizontal stress PY - 2019 UR - http://mygec2019.org/ VL - 2019 SP - 151 EP - 158 PB - 1st Mediterranean Young Geotechnical Engineers Conference CY - Bodrum, Turkey AN - OPUS4-49639 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Tschirschwitz, Rico A1 - Kluge, Martin A1 - Krentel, Daniel ED - Tschirschwitz, Rico T1 - Druckgasbehälter im Feuer - Auswirkungen im Versagensfall N2 - Es wurden insgesamt 57 Einzelversuche zum Versagen von Druckgasbehältern durchgeführt. Untersucht wurden dabei 11-kg-Propangasflaschen, PKW-Radmuldentanks für LPG- sowie CNG-Tanks vom Typ III (Compositetanks mit Aluminiumliner) und Typ IV (Compositetanks mit Polymerliner). Mit 18 hydraulischen Berstversuchen wurde das Versagensverhalten unter kalten Bedingungen charakterisiert. In 39 Unterfeuerungsversuchen mit den gefüllten LPG- und CNG-Tanks, davon 36 mit Tanks ohne Sicherheitseinrichtung, wurde das Behälter¬ver¬sagen durch Brandbeaufschlagung untersucht. Neben verschiedenen Behältermantel¬temperaturen und dem Behälterinnendruck wurde auch die Temperatur des gespeicherten Mediums dokumentiert. Dadurch war es möglich, genau zu dokumentieren, unter welchen Bedingungen und bei welchem Zustand der Behälter versagt hat. In einem Großteil der Unterfeuerungsversuche mit Behältern ohne Sicherheitseinrichtungen kam es zur Bildung eines Feuerballs, einer massiven Druck- und Temperaturwirkung auf den Nahbereich sowie einer Vielzahl von Fragmenten im Nah- und Fernbereich. In einer Entfernung von l = 7 m wurden Überdrücke von bis zu p = 0,41 bar gemessen. In 30 Unterfeuerungsversuchen kam es zur Fragmentierung des Behälters. Dabei konnten 159 Fragmente mit Wurfweite und Masse dokumentiert werden. Die dabei maximal festgestellte Wurfweite eines Fragments lag bei l = 311 m. T2 - 15. BAM/PTB-Kolloquium zur chemischen und physikalischen Sicherheitstechnik CY - Brunswick, Germany DA - 21.05.2019 KW - Behälterversagen KW - Druckgasbehälter KW - LPG KW - Feuer KW - Propan PY - 2019 DO - https://doi.org/10.7795/210.20190521L VL - 15. SP - 1 EP - 20 PB - PTB CY - Braunschweig AN - OPUS4-48086 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Romero-Navarrete, José A. ED - Otremba, Frank ED - Sklorz, Christian ED - Madrid, M. M. T1 - A convex bottom tank for atmospheric road tankers N2 - The potential benefits to the roll stability of a road tanker, derived from using a convex-bottom tank, instead of a concave-bottom one, are assessed. The convex-bottom tank consists of a modified elliptical figure to which the concave bottom is substituted by a convex one. The concave-bottom consists of an elliptical shape. Static and dynamic analyses are performed, for which the proposed shape revels enhancements on the order of 10%. The static rollover stability factor, and the lateral load transfer ratio, are used as performance measures for the static and the dynamic analysis, respectively. The dynamic analysis derives from a simplified model, for which the sloshing mass is substituted by a calibrated simple pendulum. Other potential benefits of the proposed tank shape are discussed, including a reduction in the aerodynamic drag, and a longer life for the vehicle components. T2 - CONiiN XV International Engineering Congress CY - Santiago de Querétaro, Mexcio DA - 13.05.2019 KW - Conveux KW - Tank KW - Atmospheric PY - 2019 SP - 1 EP - 7 AN - OPUS4-48115 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Romero-Navarrete, José A. ED - Otremba, Frank T1 - Impact of sloshing and non-sloshing cargo N2 - The interaction between the sloshing cargo and the carrying vehicle has been predominantly studied from the perspective of road safety, aiming at characterizing the effects of cargo motion on both, the lateral stability of the vehicles and the respective braking performance. In this regard, one main issue is to objectively clarify the potential effects of the sloshing cargoes, when compared with solid or non-sloshing cargoes. While there are abundant theoretical studies about the comparative effects of one substance and the other on the vehicle performance, only few experimental studies have been reported with that approach. In this paper, the outputs from an experimental study involving the longitudinal load transfer of sloshing and non-sloshing cargoes, is presented. The longitudinal load transfer is characterized in this paper on the basis of the moment of the reaction forces at the wheel-support interface, with respect to the impact spot. Results suggest that for one-quarter fill level, the sloshing cargo produces an amplification of the performance measure (12% maximum) while at half fill level the sloshing cargo damps the outputs (6.31 % reduction), while at high fill levels, the sloshing effect is mixed, as a function of the impact input, from -1.1% at low impact distance, to +6.6 for large impact distance. T2 - CONiiN XV International Engineering Congress CY - Santiago de Querétaro, Mexico DA - 13.05.2019 KW - Sloshing KW - Non-sloshing KW - Cargo PY - 2019 SP - 1 EP - 6 AN - OPUS4-48117 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Dirk A1 - T., Heidermann T1 - Ergebnisse der experimentellen Untersuchungen zur Visualisierung der Wirksamkeit von Deflagrationsrohrsicherungen in einer PVC-U Rohrleitung N2 - Deflagrationsrohrsicherungen sind Sicherheitseinrichtungen, die den Durchfluss von brennbaren Gasen und Dämpfen brennbarer Flüssigkeiten ermöglichen, den Flammendurchschlag und eine weitere Explosionsausbreitung nach der Zündung von explosionsfähigen Gas-/Dampf-Luftgemischen jedoch verhindern sollen. Die Einbaubedingungen sind dabei von besonderer Bedeutung für die Wirksamkeit der Deflagrationsrohrsicherungen. Oft lassen sich aus betrieblichen bzw. verfahrenstechnischen Gründen entsprechende Einbaubedingungen nur schwer oder nicht realisieren. So können beispielsweise Rohrleitungsverzweigungen zusätzliche Turbulenzen induzieren und dadurch zu erhöhten Flammenausbreitungsgeschwindigkeiten und Explosionsdrücken und ggf. zum Versagen der Deflagrationsrohrsicherung führen. Neben den „klassischen“ Untersuchungsmethoden dieser Belastungssituationen von Deflagrationsrohrsicherungen, wie die Erfassung des Explosionsdruckes und der Flammenausbreitungsgeschwindigkeiten, werden in diesem Beitrag die Ergebnisse der visuellen Beobachtungen des Reaktionsverlaufes sowie die Belastungen der Flammendurchschlagsicherung bei unterschiedlichen Einbaubedingungen in den Vordergrund gestellt. Gegenübergestellt wird die Belastungssituation der Flammensperre in einer geraden und einer verzweigten Rohrleitung. Verwendet wurde dafür eine speziell gefertigte Deflagrationsrohrsicherung, die eine Beobachtung des Reaktionsverlaufs im Bereich der spiralförmig gewickelten Metallbändern erlaubt. Zusätzlich wurde im geschützten Bereich in der Rohrleitung eine Kamera installiert, die die Belastungssituation bei den einzelnen Versuchen dokumentierte. Die Ergebnisse bestätigen sehr eindrucksvoll, dass die Belastungssituation der Deflagrationsrohrsicherung sich in Abhängigkeit von der Konfiguration der Rohrleitung entscheidend ändert T2 - 15. BAM/PTB-Kolloquium zur chemischen und physikalischen Sicherheitstechnik CY - Brunswick, Germany DA - 21.05.2019 KW - Flammendurchschlagsicherungen KW - Rohrleitungen KW - Deflagrationen PY - 2019 DO - https://doi.org/10.7795/210.20190521A VL - 15. SP - 1 EP - 10 PB - PTB CY - Braunschweig AN - OPUS4-48084 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Krause, Martin A1 - Mielentz, Frank A1 - Milman, B. T1 - Machbarkeitsstudie zur zerstörungsfreien Rißcharakterisierung in festen Fahrbahnen N2 - Die Forschungsvereinbarung zwischen der Deutschen Bahn AG (DB) und der BAM zur Erstellung der vorliegenden Studie basiert auf einem Angebot der BAM an die DB vom November 1998. Es sollten die in der Literatur beschriebenen Ansätze, Risse in Betonbauteilen mit akustischen Verfahren, insbesondere Ultraschallverfahren, zu charakterisieren, aufgegriffen werden. Dabei stand die Umsetzung speziell für die Fragestellungen an Festen Fahrbahnen im Vordergrund. Die für die Lösung der Prüfaufgaben erfolgversprechenden Ansätze sollten zunächst im Laboratorium unter idealen und dann unter praxisnahen Bedingungen untersucht und unter Verwendung von modernen Ansätzen der Ultraschalltechnik, soweit möglich, verbessert werden. KW - Spannbetonschwelle KW - Feste Fahrbahn KW - Zerstörungsfreie Prüfung PY - 2000 SP - 1 EP - 16 AN - OPUS4-64247 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quercetti, Thomas A1 - Scheidemann, Robert A1 - Komann, Steffen A1 - Ballheimer, Viktor A1 - Wille, Frank T1 - Drop Testing of a New Package Design for the Transport of SNF from German Research Reactors N2 - A new dual purpose cask design was developed for the safe transport and interim storage of spent fuel elements of German research reactors. In the framework of the safety assessment within the package approval procedure the Bundesanstalt für Materialforschung und –prüfung (BAM) as competent authority performed a series of drop tests according with the IAEA Transport Regulations. The package consists of a cylindrical thick-walled ductile cast iron cask body closed by a bolted lid system with metallic seals. A lid and bottom sided impact limiter consisting of a wood/steel construction limit the mechanical impact loading. The full-scale test specimen was equipped with a basket and assembled with dummy-fuel elements. The package and test specimen, respectively have a total mass of approximately 24 metric tons. The mechanical drop test program included three 9m free drop tests, in horizontal, vertical and oblique cask orientation onto the lid system. Additionally, a 1m-puncture bar drop test followed the horizontal drop test to consider an IAEA-drop test sequence. The horizontal and vertical drop tests were performed at a temperature of minus 40°C. During the oblique drop test the upper impact limiter was heated up to +80°C. The tests were conducted onto an unyielding target, fulfilling the IAEA requirements. The test specimen was considerably instrumented with strain gauges and accelerometers. Transient strains at selected locations of the inner and outer container walls, of the primary and secondary lid, as well as of the corresponding lid bolts were measured during the drop tests. Furthermore, decelerations in different locations at the cask body and the lids were measured. The complex geometrical deformation of the impact limiters due to the impact were determined by optical 3D- measurements. Before and after the drop tests the leakage rate of the lid system was determined by helium leakage testing. The experimental results contribute to the evaluation of the package response to mechanical tests, demonstrating safety under normal and accident conditions of transport and especially to the verification of the dynamic finite-element model of the package used in the package design safety report. T2 - PATRAM 2019 CY - New Orleans, LA, USA DA - 04.08.2019 KW - SNF KW - Drop testing KW - New package design PY - 2019 SP - Paper 19-A-1142,1 EP - 10 AN - OPUS4-50622 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geoerg, Paul A1 - Schumann, J. A1 - Boltes, M. A1 - Holl, S. A1 - Hofmann-Böllinghaus, Anja T1 - The influence of individual impairments on crowd dynamics N2 - Emergency exits as bottlenecks in escape routes are important for designing traffic facilities. Especially the fundamental diagram is a crucial performance criterion for assessment of pedestrians' safety in facilities and an important basis for calculation methods. For this reason, several studies were performed during the last decades which focus on the quantification of movement through bottlenecks. These studies were usually conducted with populations of homogeneous characteristics to reduce influencing variables and for reasons of practicability. Studies which consider heterogeneous characteristics in performance parameters are rarely available. In response and to reduce this lack of data a series of well-controlled large-scale movement studies considering pedestrians with different disabilities was carried out. T2 - Interflam 2019 CY - London, UK DA - 01.07.2019 KW - Evacuation PY - 2019 VL - 2019 SP - 775 EP - 791 PB - Interscience CY - London, UK AN - OPUS4-48647 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klippel, Andrea A1 - Hofmann-Böllinghaus, Anja T1 - Quantitative risk analysis and numerical investigation to determine critical fire scenarios in the environment of handicapped people N2 - Crisis management, particularly the evacuation of handicapped People during a fire scenario presents a highly demanding challenge for nursing staff and rescue forces on site. The German research Project SiME is an interdisciplinary cooperation of university and non-university research institutions as well as medium-sized companies, which work together to develop strategies to manage such critical scenarios. In the SiME project, which is funded by the German Federal Ministry of Education and Research, evacuation characteristics of pedestrians with physical, mental or age-related disabilities are investigated to fit consisting numerical evacuation models with data. One of the major tasks of the OvGU was to set up a database of scenarios related to fire, explosion or substance releases in the working and living environment of handicapped people. Therefore, more than 463 fire Events occurring over the last decade in Germany were documented in this database and categorized by a suitable assignment of characteristics e.g. location of fire, ignition source, number of fatalities and injured. The evaluated data were the basis for carrying out a quantitative risk analysis. Thus event trees were set up for different integrative infrastructures with which occurrence probabilities for different scenarios could be calculated for each path. The extent of damage, as a quantity describing the impact, was assumed to be personal injury or death or serious injury. By a risk assessment critical Scenarios could be derived from the risk analysis. T2 - Interflam 2019 CY - London, UK DA - 1.07.2019 KW - Evacuation PY - 2019 VL - 2019 SP - 795 EP - 806 PB - Interscience CY - London, UK AN - OPUS4-48649 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Martin A1 - Erdt, René A1 - Gödde, M. A1 - Salg, S. A1 - Ittemann, L. T1 - Selbstentzündungsverhalten von Feststoffen: Validierung der Extrapolation von Labortests mit Hilfe halbtechnischer Versuche bis 1 m³ N2 - Vorgestellt wird ein 2018 gestartetes Projekt zur Überprüfung der Extrapolation von im Labormaßstab ermittelten Selbstentzündungstemperaturen auf technisch relevante Volumina. Für die Ermittlung reaktionskinetischer Daten von Feststoffschüttungen stehen eine Reihe von Untersuchungsmethoden zur Verfügung. Dies sind thermische Analysen wie z.B. die differential scanning calorimetry DSC sowie Mikrokalorimetrie zur hochgenauen Messung von Wärmeströmen, bei denen sehr geringe Probenmengen zum Einsatz kommen. In der Regel wird das Selbstentzündungsverhalten jedoch mit Hilfe von isoperibolen oder adiabaten Warmlagerungsversuchen beurteilt, hier liegen die Probenvolumina üblicherweise im Bereich von ca. 100 cm³ bis zu einigen Litern. Die Extrapolation über mehrere Größenordnungen auf technische Volumina birgt Unsicherheiten, da mit Zunahme des Lagervolumens veränderte Start- und Randbedingungen vorliegen können. Zudem besteht die Möglichkeit, dass bei in technischen Lagern vorherrschenden niedrigen Temperaturen Reaktionen ablaufen, die in Standard- Laborversuchen nicht erfasst werden aber einen wesentlichen Einfluss auf das Selbstentzündungsverhalten aufweisen können. Hauptziel des Projektes ist es daher, die im Labormaßstab vorhandenen Prüfeinrichtungen durch einen Versuchsstand zur Untersuchung von Probengrößen von bis zu 1000 dm³ zu erweitern, die Eignung (oder Nichteignung) der etablierten Methoden nachzuweisen und im Labormaßstab nicht erfassbare Einflussgrößen zu ermitteln. Zudem sollen anhand der kleinskaligen Tests Entscheidungskriterien abgeleitet werden, ob eine Extrapolation nach den derzeit üblichen Methoden zulässig ist. T2 - 15. BAM-PTB-Kolloquium zur chemischen und physikalischen Sicherheitstechnik CY - Brunswick, Germany DA - 21.05.2019 KW - Spontanious ignition KW - Self-ignition KW - Minimum ignition temperature KW - Dust layers KW - Große Volumina KW - Explosionsschutz KW - Selbstentzündung KW - DSC PY - 2019 DO - https://doi.org/10.7795/210.20190521B SP - 1 EP - 15 PB - Physikalisch-Technische Bundesanstalt (PTB) AN - OPUS4-48939 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schalau, Sebastian A1 - Habib, Abdel Karim A1 - Krause, U. T1 - CFD-Simulation von Schwergasausbreitungen N2 - Um die Ausbreitung von Schwergaswolken infolge störfallbedingter Freisetzungen in bebautem Gelände besser vorhersagen zu können, wird eine praxisorientierte Methode zur numerischen Simulation von Schwergasausbreitungen vorgestellt. T2 - 15. BAM-PTB-Kolloquium zur chemischen und physikalischen Sicherheitstechnik CY - Brunswick, Germany DA - 21.05.2019 KW - Explosionsschutz KW - CFD KW - Schwergas KW - Gasausbreitung PY - 2019 DO - https://doi.org/10.7795/210.20190521G SP - 1 EP - 10 PB - Physikalisch-Technische Bundesanstalt (PTB) AN - OPUS4-48940 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Patrick P. A1 - Hirschberger, Paul A1 - Baurzhan, Zhandos A1 - Tiebe, Carlo A1 - Hofmann, Michael A1 - Hüllmann, Dino A1 - Bartholmai, Matthias T1 - Indoor air quality monitoring using flying nanobots: Design and experimental study N2 - In this paper, we introduce a nano aerial robot swarm for Indoor Air Quality (IAQ) monitoring applications such as occupational health and safety of (industrial) workplaces. The robotic swarm is composed of nano Unmanned Aerial Vehicles (UAVs), based on the Crazyflie 2.0 quadrocopter, and small lightweight Metal Oxide (MOX) gas sensors for measuring the Total Volatile Organic Compound (TVOC), which is a measure for IAQ. An indoor localization and positioning system is used to estimate the absolute 3D position of the swarm similar to GPS. A test scenario was built up to validate and optimize the swarm for the intended applications. Besides calibration of the IAQ sensors, we performed experiments to investigate the influence of the rotor downwash on the gas measurements at different altitudes and compared them with stationary measurements. Moreover, we did a first evaluation of the gas distribution mapping performance. Based on this novel IAQ monitoring concept, new algorithms in the field of Mobile Robot Olfaction (MRO) are planned to be developed exploiting the abilities of an aerial robotic swarm. T2 - 2019 IEEE International Symposium on Olfaction and Electronic Nose (ISOEN) CY - Fukuoka, Japan DA - 26.05.2019 KW - Indoor air quality KW - Nano aerial robot KW - Aerial robot olfaction KW - Swarm KW - Gas detector PY - 2019 SN - 978-1-5386-8327-9 SN - 978-1-5386-8328-6 DO - https://doi.org/10.1109/ISOEN.2019.8823496 SP - 1 EP - 3 PB - IEEE AN - OPUS4-48920 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neumann, Patrick P. A1 - Hirschberger, Paul A1 - Bartholmai, Matthias ED - Zemčík, Robert ED - Krystek, Jan T1 - Influence of rotor downwash on vertically displaced nanobots in flight N2 - Using a swarm of copter-based gas-sensitive aerial nano robots for monitoring indoor air quality is challenging due to, e.g., limited air space in buildings. To avoid an over-regulation of the available indoor air space (e.g., prohibit copters to fly above each other), a safety region around each copter must be defined to guarantee a safe operation of the swarm. The key contributions of this paper are the realization of experiments that investigate the influence of the rotor downwash on flying vertically displaced nano robots and the development of a model describing the above-mentioned safety region. T2 - 36th Danubia-Adria Symposium on Advances in Experimental Mechanics CY - Pilsen, Czech Republic DA - 24.09.2019 KW - Gas sensing KW - Mobile Robot Olfaction KW - Nano aerial robot KW - Swarm PY - 2019 SP - 23 EP - 24 CY - Plzeň AN - OPUS4-49173 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Horn, Wolfgang A1 - Hahn, Oliver A1 - Jann, Oliver T1 - Kunstgüter in Vitrinen: was helfen Materialuntersuchungen gemäß BEMMA-Schema? N2 - Moderne Vitrinen sollen gleichzeitig eine hohe Dichtigkeit und die Abwesenheit jeglicher Fremdstoffe in den Vitrinen gewährleisten. Diese Anforderungen sind zeitgleich kaum erfüllbar, da es emissionsfreie Materialien (vor allem Kleb- und Beschichtungsstoffe) nicht gibt. Um die potentiellen Emissionen zu minimieren wurde ein Messverfahren entwickelt, welches inzwischen als BEMMA-Schema (Bewertung von Emissionen aus Materialien für Museumsausstattungen) in die Museumswelt Einzug genommen hat. Die erfolgreiche Bewertung der für den Bau verwendeten Materialien gemäß BEMMA-Schema resultiert nicht in einer emissionsfreien Vitrine, sondern soll bei der Auswahl geeigneter Materialien zur Herstellung möglichst emissionsarmer Vitrinen helfen. Konkrete handwerkliche Durchführungen beim Bau, Dichtheits¬anforderungen, wie auch die Aufstellbedingungen (Umgebung der Vitrine) beeinflussen die Emissionscharakteristik der fertigen Vitrine in der Praxis. Eine saubere Vitrine hilft nichts in einer belasteten Umgebung oder auch bei emittierenden Exponaten. Inzwischen liegen Erfahrungen mit dem Schema seit 2012 vor. Der Messablauf sieht vor, dass von den Materialien kleine Muster mit der Mikrokammer (Markes) innerhalb von 2 Tagen untersucht werden. Dabei wird mit Silikagelkartuschen auf Ameisen- und Essigsäure, mit DNPH auf Aldehyde und Ketone und mit Tenax® sowohl auf VOC als auch für die spezifische Oxim-Analytik die Abluft der Mikrokammern untersucht. Die Bewertungskriterien basieren auf den Ergebnissen einer Vorstudie mit ca. 150 verschiedenen Produkten im Zeitraum 2010 bis 2012. T2 - 12. Fachkongress der Arbeitsgemeinschaft ökologischer Forschungsinstiute (AGÖF) CY - Hallstadt (Bamberg), Germany DA - 17.10.2019 KW - Museum KW - Emission KW - Bauprodukte KW - BEMMA KW - Vitrinen PY - 2019 SN - 978-3-930576-11-1 VL - 12. Fachkongress SP - 245 EP - 249 PB - Arbeitsgemeinschaft ökologischer Forschungsinstiute (AGÖF) e. V. CY - Springe-Eldagsen AN - OPUS4-49326 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hüllmann, Dino A1 - Neumann, Patrick P. A1 - Lilienthal, A. J. T1 - Gas Dispersion Fluid Mechanics Simulation for Large Outdoor Environments N2 - The development of algorithms for mapping gas distributions and localising gas sources is a challenging task, because gas dispersion is a highly dynamic process and it is impossible to capture ground truth data. Fluid-mechanical simulations are a suitable way to support the development of these algorithms. Several tools for gas dispersion simulation have been developed, but they are not suitable for simulations of large outdoor environments. In this paper, we present a concept of how an existing simulator can be extended to handle both indoor and large outdoor scenarios. T2 - 36th Danubia Adria Symposium on Advances in Experimental Mechanics CY - Pilsen, Czech Republic DA - 24.09.2019 KW - Gas dispersion simulation KW - CFD KW - Gas tomography PY - 2019 SN - 978-80-261-0876-4 SP - 49 EP - 50 CY - Pilsen, Czech Republic AN - OPUS4-49224 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas A1 - Kannengießer, Thomas T1 - Legierungskonzept höherfester Schweißverbindungen und deren Kaltrissverhalten N2 - Höherfeste Feinkornbaustähle mit Streckgrenzen ≥ 690 MPa neigen bei der schweißtechnischen Fertigung zur Bildung von wasserstoffunterstützten Kaltrissen. Diese Mikrorisse entstehen aus der kritischen Interaktion von lokalem risskritischem Gefüge, lokal erhöhter Wasserstoffkonzentration und lokal erhöhter Beanspruchung bzw. Dehnung. Aktuell gültigen Regelwerken zur schweißtechnischen Verarbeitung höherfester Feinkornbaustähle sind Anweisungen zu entnehmen, um das Risiko einer Kaltrissbildung zu minimieren. Die Weiterentwicklung der Werkstoffe (Legierungskonzepte) und neuer Lichtbogenprozesse zur Verringerung der Nahtöffnungswinkel bei gleichzeitiger Erhöhung der Abschmelzleistung (modifizierter Sprühlichtbogen) brachten jedoch auch neue Fragen hinsichtlich der Wasserstoffmenge in der Schweißverbindung nach dem Schweißen und der Kaltrissempfindlichkeit mit sich. Mikrolegierungselemente (V, Nb und Ti) bedingen bspw. eine verlangsamte Wasserstoffdiffusion. Schweißverbindungen unter reduziertem Nahtöffnungswinkel beinhalten höhere Wasserstoffkonzentrationen. Dieser Beitrag zeigt den Einfluss von Einbrandprofil (höhere Abschmelzleistung) auf die Kaltrissempfindlichkeit an einem höherfesten Feinkornbaustahl mit artähnlichem mikrolegierten Schweißzusatzwerkstoff anhand des fremdbeanspruchten Implant-Tests. T2 - DVS Congress 2019 - Große Schweißtechnische Tagung CY - Rostock, Germany DA - 16.09.2019 KW - Höherfester Feinkornbaustahl KW - Kaltrisse KW - Wasserstoff KW - Implant-Test PY - 2019 SN - 978-3-96144-066-5 VL - 355 SP - 327 EP - 332 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-49007 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Askar, Enis T1 - The influence of strong ignition sources on the explosion and decomposition limits of gases N2 - Explosion and decomposition limits of flammable and chemically unstable gases were determined experimentally in a dosed autoclave with varying ignition energy up to 1000 J. The ignition source was a lightning arc caused by an exploding wire igniter as described in EN 1839 B .. In case of methane only the upper explosion limit was influenced significantly by the ignition energy, whereas the lower explosion limit was constant. In case of R32 however. it was the lower explosion limit that was influenced significantly by the ignition energy and not the upper explosion limit. A particularly strong dependency from the ignition energy was found for the decomposition limits of the chemically unstable gases in nitrogen. T2 - 16th International Symposium on Loss Prevention and Safety Promotion in the Process Industries CY - Delft, The Netherlands DA - 16.06.2019 KW - Explosionsgrenzen KW - Zündenergie KW - Chemisch instabile Gase KW - Kältemittel KW - Zündquellen PY - 2019 AN - OPUS4-48993 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beckmann, Jörg ED - Spranger, Holger T1 - Synthetische Aperturfokussierung für die Terahertzspektroskopie N2 - Die zeitaufgelöste THz-Spektroskopie (THz-TDS) operiert mit elektromagnetischen Impulsen, die ein Amplitudenspektrum im unteren THz-Bereich aufweisen. Die THz-TDS ist in der Lage, dielektrische Volumina zerstörungs- und kontaktfreie zu durchstrahlen. Um eine 3D-THz Bildung zu ermöglichen, wurde für die THz-TDS ein rechnergestütztes Mess- und Rekonstruktionsverfahren (THz-TDSAFT) entwickelt, mit dem es gelingt, unter Verwendung der im Zeitbereich registrierten THz-TDS-Daten das Volumeninnere in Form eines dreidimensionalen Tomogramms zu rekonstruieren. Die THz-TD-SAFT basiert auf die für die Ultraschalltechnik entwickelte Synthetische Apertur Fokussierung (SAFT) bzw. des heuristisch begründeten Algorithmus des Synthetischen Apertur Radars (SAR). Anhand von Beispielen wird die Möglichkeiten der THz-TD-SAFT demonstriert und nachgewiesen, dass mit dem Rekonstruktionsansatz die künstlich eingebauten Fehlstellen bezüglich der Position und Größe geometrisch richtig im Tomogramm abgebildet werden können. T2 - 4. Fachseminar des FA MTHz, Mikrowellen- und Terahertz-Prüftechnik in der Praxis CY - Fürth, Germany DA - 02.04.2019 KW - THz-TDS KW - Tomographie, KW - Zerstörungsfreie Prüfung PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-490481 UR - https://www.ndt.net/search/docs.php3?MainSource=262 SP - 1 EP - 8 PB - DGZfP CY - Berlin AN - OPUS4-49048 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scheuschner, Nils A1 - Altenburg, Simon A1 - Straße, Anne A1 - Gumenyuk, Andrey A1 - Maierhofer, Christiane T1 - In-situ thermographic monitoring of the laser metal deposition process N2 - In this paper shortwave infrared (SWIR) thermographic measurements of the manufacturing of thin single-line walls via laser metal deposition (LMD) are presented. As the thermographic camera is mounted fixed to the welding arm, an acceleration sensor was used to assist in reconstructing the spatial position from the predefined welding path. Hereby we could obtain data sets containing the size of the molten pool and the oxide covered areas as functions of the position in the workpiece. Furthermore, the influence of the acquisition wavelength onto the thermograms was investigated in a spectral range from 1250 nm to 1550 nm. All wavelengths turned out to be usable for the in-situ process monitoring of the LMD process. The longer wavelengths are shown to be beneficial for the lower temperature range, while shorter wavelengths show more details within the molten pool. T2 - Sim-AM 2019 - 2. International Conference on Simulation for Additive Manufacturing CY - Pavia, Italy DA - 11.09.2019 KW - Additive manufacturing KW - 3D printing KW - Thermography KW - Direct energy deposition KW - Laser Metal Deposition KW - 3D Druck KW - Laser Pulver Auftragsschweißen KW - Additive Fertigung KW - Thermografie PY - 2019 UR - http://congress.cimne.com/SIM-AM2019/frontal/Doc/proceedings.pdf SN - 978-84-949194-8-0 SP - 246 EP - 255 AN - OPUS4-49086 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - von Oertzen, Alexander T1 - New Standardisation Tasks under the European Explosives Directive: Electronic Detonators, On-site Mixed Explosives N2 - Since the early drafting of the European standards for civil explosives, harmonised under directive 93/15/EEC and 2014/28/EU, blasting technology has developed notably. This is particularly evident for electronic detonators and electronic firing systems, and the EU commission agreed to initiate a standardisation initiative, also noting that the currently existing document on electronic detonators is “only” a Technical Specification (CEN/TS). This paper addresses the current activities in the area of standardisation. The EU is about to launch a formal standardisation request to cover the most recent technological developments not addressed by the current standards. The request would also include various adjustments of references to the new Directive for civil explosives, and in addition the task of developing a Technical Specification for on-site mixed explosives and corresponding manufacturing units. The latter has been included to address the nowadays frequently found mobile production on the basis of ammonium nitrate prills or emulsions. T2 - EFEE 10th anniversary World Conference on Explosives and Blasting CY - Helsiniki, Finland DA - 15.09.2019 KW - On-site mixed Explosives KW - Technical Specification KW - Harmonised Standards KW - Standardisation KW - Electronic Detonators PY - 2019 SN - 978-0-955029-6-6 SP - 215 EP - 219 PB - EFEE European Federation of Explosives Engineers AN - OPUS4-49107 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakenecker, A. A1 - Topolniak, Ievgeniia A1 - Lüdtke-Buzug, K. A1 - Pauw, Brian Richard A1 - Buzug, T. T1 - Additive manufacturing of superparamagnetic micro-devices for magnetic actuation N2 - 3D microstructures with sub-micron resolution can be manufactured in additive manner applying multi-photon laser structuring technique. This paper is focused on the incorporation of superparamagnetic iron oxide nanoparticles into the photoresist in order to manufacture micrometer-sized devices featuring a magnetic moment. The aim of the project is to achieve untethered actuation of the presented objects through externally applied magnetic fields. Future medical application scenarios such as drug delivery and tissue engineering are targeted by this research. T2 - Additive Manufacturing Meets Medicine 2019 CY - Lübeck, Germany DA - 12.09.2019 KW - MPI KW - Two-Photon Polymerization KW - Magnetic swimmers KW - MPLS PY - 2019 UR - www.journals.infinite-science.de/ammm DO - https://doi.org/10.18416/AMMM.2019.1909S09T06 SP - 153 EP - 154 PB - Infinite Science Publishing AN - OPUS4-49114 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Spaltmann, Dirk A1 - Kogia, M. A1 - Liedtke, S. A1 - Dykeman, D. A1 - Gradt, Thomas T1 - Challenges for the design of a universal tribological database for materials N2 - Renowned institutions in the field of tribology combine their testing and analytical capabilities with experts in materials/process information management technology to provide the respective Services in Europe (i-TRIBOMAT). This requires a centralized materials information management system or the standardised capture, consolidation and harmonization of tribological information. T2 - 60. Tribologe-Fachtagung CY - Goettingen, Germany DA - 23.09.2019 KW - Database KW - Tribology KW - Digital KW - LIMS PY - 2019 SN - 978-3-9817451-4-6 SP - 37/1 EP - 37/5 PB - GfT (Gesellschaft für Tribologie) CY - Jülich AN - OPUS4-49147 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Metz, Christian A1 - Franz, Philipp A1 - Fischer, C. A1 - Wachtendorf, Volker A1 - Maierhofer, Christiane T1 - Zerstörungsfreie Charakterisierung der Alterung additiv gefertigter Kunststoffbauteile N2 - Das vorgestellte Projekt beschäftigt sich mit den optischen, thermophysikalischen und mechanischen Materialeigenschaften von additiv gefertigten Kunststoffteilen und deren Alterung. Dazu wurden mittels Fused Layer Modeling (FLM) Probekörper aus ABS hergestellt, die anschließend für drei Monate einer künstlichen Bewitterung unterzogen wurden. Die dabei erzeugte definierte Alterung wurde nach drei Zeitabschnitten jeweils mit zerstörungsfreien Methoden charakterisiert. Dabei wurde neben den spektroskopischen Standardmethoden auch die aktive Thermografie eingesetzt. Die Ergebnisse zeigen, dass sich mittels der Thermografie sowohl chemische Veränderungen als auch mechanische Schädigungen (Fehlstellen) darstellen lassen. Die Bewitterung beeinflusst die Teiltransparenz der Proben zumindest im sichtbaren Spektralbereich, was bei der Charakterisierung der Fehlstellen, die mittels optisch angeregter aktiver Thermografie detektiert wurden, berücksichtigt werden muss. T2 - DGZfP-Jahrestagung 2019 CY - Friedrichshafen, Germany DA - 27.05.2019 KW - 3D Druck KW - Additive Fertigung KW - Thermografie KW - Polymere KW - Künstliche Bewitterung PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-491561 UR - https://jt2019.dgzfp.de/Portals/jt2019/bb/Di.3.B.1.pdf SN - 978-3-947971-02-2 VL - 171 SP - 1 EP - 8 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-49156 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gumenyuk, Andrey A1 - Üstündag, Ö. A1 - Gook, S. A1 - Rethmeier, Michael T1 - Laserhybridschweißen von dickwandigen Stählen mit elektromagnetischer Schmelzbadunterstützung N2 - Die steigenden Anforderungen in Hinsicht auf Sicherheitsfaktoren von gefügten Bauteilen führen zu einer Zunahme der zu schweißenden Bauteildicken. Das Laserstrahl-Lichtbogen-Hybridschweißverfahren – verbreitet im industriellen Einsatz vor allem im Schiffs- und Windkraftanlagenbau – ermöglicht das einlagige Fügen von dickwandigen Strukturen. Eine Herausforderung stellt das Schweißen von dickwandigen Bauteilen mit reduzierter Geschwindigkeit in Wannenlage (PA-Position) da. Sie ist aufgrund des erhöhten hydrostatischen Druckes und die daraus resultierenden Tropfenbildung an der Wurzelseite bedingt realisierbar. Die im Rahmen dieser Studie eingesetzte elektromagnetische Schmelzbadunterstützung wirkt dem gravitationsbedingten Austropfen der Schmelze entgegen und kompensiert den hydrostatischen Druck. Dabei werden unterhalb der Schweißzone mit Hilfe eines extern angelegten oszillierenden Magnetfeldes Wirbelströme im Werkstück induziert, die eine nach oben gerichtete Lorentzkraft erzeugt. Die Lorentzkraft wirkt dem hydrostatischen Druck entgegen und stellt einen sicheren Schweißprozess ohne Tropfenbildung dar. Mit dem Hybridschweißverfahren mithilfe der elektromagnetischen Schmelzbadunterstützung gelingt es mit einem 20-kW Faserlaser bis zu 30 mm dicke Bleche in einer Lage zu schweißen. Bei 25 mm dicken einlagig geschweißten Platten aus S355 konnte ein Spalt bis 1 mm und ein Kantenversatz bis zu 2 mm sicher überbrückt werden. Die Reduzierung der Schweißgeschwindigkeit hat eine Verringerung der notwendigen Laserleistung zur Folge und begünstigt außerdem die mechanisch-technologischen Eigenschaften, infolge der reduzierten Abkühlgeschwindigkeit. Durch die geringe Martensitbildung führt dies zu einer Verbesserung der Kerbschlagzähigkeit. T2 - 19. Tagung in Hamburg - DVS CY - Hamburg, Germany DA - 24.04.2019 KW - Laser-Hybridschweißen KW - Elektromagnetische Schmelzbadunterstützung KW - Schweißen von kaltzähen Stählen PY - 2019 SP - 34 EP - 46 PB - DVS AN - OPUS4-47918 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Vandrich, Jasmina T1 - Metabolic engineering in Halomonas elongata N2 - Halomonas elongata is a halophilic γ-proteobacterium that synthesizes and accumulates the compatible solute ectoine to cope with osmotic stress in saline environments. Ectoine possesses protecting properties and stabilizes proteins as well as whole cells against stresses like ionizing radiation and cytotoxins. These properties make ectoine a highly demanded ingredient in cosmetics and pharmaceuticals. To date H. elongata is the industrial Producer strain of ectoine, but several metabolic factors for optimum ectoine production remain to be explored. In this work, we used up to date Metabolic engineering approaches following the ‘Push, Pull, Block – strategy’ to examine targets that contribute to ectoine synthesis. Firstly, the basics of glucose catabolism were inspected to PUSH and enhance carbon flow towards ectoine synthesis. Secondly, lysine biosynthesis was targeted to BLOCK a pathway that is competing for precursors with ectoine synthesis. Thirdly, the mechanosensitive (MS) channels of H. elongata have been examined as possible excretion routes for ectoine. An overexpression of the ectoine excretion channels potentially could PULL out product at the end of ectoine synthesis and increase overall ectoine flux. For the interrogation of central metabolic pathways, we established the new molecular tool CRISPR-mediated interference (CRISPRi) for targeted modulation of gene expression. PUSH Glucose catabolism through the Entner-Doudoroff (ED) and Emden-Meyerhof-Parnas (EMP) pathway was targeted with CRISPRi and examined on gene expression level for ist response to changing salinity and different carbon sources. Changing salinity did not influence gene expression levels of glucose catabolism but the carbon source glucose triggered glycolysis through the (ED) pathway. When gene expression of the ED pathway was downregulated with CRISPRi, the growth rates remained constant. The observations indicate a metabolic overflow mechanism for glycolysis, in which fluxes are constantly high - even at lower salinity when no resources are demanded for ectoine synthesis. The further analysis of glucose to product conversion rates will advise optimum conditions for future industrial cultivation processes. BLOCK Lysine biosynthesis was downregulated with CRISPRi, which led to a significant increase in ectoine production. Hence, the blockage of lysine biosynthesis would be a valuable strategy for the optimization of the industrial producer strain in future studies. PULL MS channels and ectoine regulation are inevitably connected in osmoadaptation. Therefore, ectoine excretion, growth performance and gene expression levels of the MS channels were monitored in steady state conditions and in response to osmotic shock in the wildtype strain and in a MS channel deletion mutant. We observed that the MS channels were essential for the survival of osmotic shock but surprisingly their presence reduced cell growth under high salinity. The MS channels were only partially responsible for ectoine excretion. Thus, alternative ectoine excretion channels must exist and remain to be explored. KW - Halomonas elongata KW - Ectoine KW - CRISPR dCas9 PY - 2019 SP - 1 EP - 94 CY - Potsdam AN - OPUS4-51094 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Genath, A. A1 - Hofmann, Michael A1 - Tiebe, Carlo A1 - Einspanier, R. T1 - Auf dem Weg zum Monitoring der Ameisensäurekonzentration in der Bienenstock-Luft mit einem Multigassensorsystem N2 - Die Varroose gilt weltweit als eine der bedeutendsten Erkrankungen der westlichen Honigbiene, Apis mellifera. Verursacht wird sie durch den Ektoparasiten Varroa destructor, der durch Saugen der Hämolymphe und Virenübertragung sowohl die Bienenbrut als auch die adulten Individuen schädigt. Ohne imkerliche Unterstützung gehen betroffene Bienenvölker in der Regel innerhalb von drei Jahren ein. Als bewährte, häufige Behandlung wird flächendeckend 60%ige Ameisensäure (AS) - im Bienenstock appliziert über verschiedene Verdampfungssysteme - eingesetzt. Sie wirkt als einziger zugelassener Stoff gegen die Varroamilbe auch in die verdeckelte Brut hinein und birgt kein Risiko der Resistenzentwicklung. Allerdings ist das therapeutische Fenster, der Bereich zwischen Milbenabtötung und Bienenschädigung, relativ schmal und die tatsächliche AS-Konzentration im Bienenstock stark abhängig von äußeren Einflussfaktoren, wie Temperatur, Luftfeuchte oder Applikationsart. Eine Bestimmung der exakten AS-Konzentration im Bienenstock ist also notwendig, um einerseits das Wirkungsoptimum zu bestimmen und andererseits bei Übersteigen der Maximalkonzentrationen mit Folge-Schädigung der Bienen, ein rechtzeitiges Eingreifen der Imker zu ermöglichen. T2 - 6. HSN-Fachsymposium „Innovative Sensorik, verteilte Sensorsysteme, neue Technologien und Anwendungsfelder“ CY - Karlsruhe, Germany DA - 06.11.2019 KW - Biene KW - Apis mellifera KW - Varroa destructor KW - Ameisensäure KW - Multigassensorik PY - 2019 SP - 22 EP - 25 AN - OPUS4-49605 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stankevich, S. A1 - Gumenyuk, Andrey A1 - Straße, Anne A1 - Rethmeier, Michael ED - Reisgen, U. ED - Schmidt, M. ED - Zaeh, M. ED - Rethmeier, Michael T1 - Measurement of thermal cycle at multi-pass layer build-up with different travel path strategies during DLMD process N2 - The shape of the parts, created by the technology of direct laser metal deposition (DLMD), is influenced by various parameters, for example, the power and diameter of the laser source spot. The contribution of energy from the laser affects the temperature distribution in the formed layers. The changing temperature in the working area entails a Change in the geometry of the layers and affects the stability of the process. In this paper, experiments on the measurement of temperature cycles in the DLMD process with different directions of the filling track are carried out. An infrared camera was used to measure thermal cycles. The calibration of the acquired data (i.e. correspondence table between the intensity of thermal radiation of the material and the absolute temperature) was done with help of two-color pyrometer ex situ and in situ measurements. The experiments are carried out on two materials 316L and Inconel 718. The effect of the maximum temperature on the layer height is shown, and thermal cycles in the formation of layers for different filling strategies are presented. T2 - Laser in Manufacturing Conference 2019 CY - Munich, Germany DA - 24.06.2019 KW - Thermography KW - Direct Laser Metal Deposition PY - 2019 SP - 1 EP - 9 AN - OPUS4-48716 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröpfer, Dirk A1 - Schaupp, Thomas A1 - Kannengießer, Thomas T1 - Kaltrissvermeidung in Schweißverbindungen aus hochfesten Feinkornbaustählen bei engen Nahtspalten und fokussiertem Lichtbogen N2 - Heute werden in Stahlkonstruktionen zunehmend hochfeste Baustähle (Streckgrenze ≥ 960 MPa) eingesetzt. Daher sind auch in Schweißnähten solche hohen Festigkeiten gefordert. Jedoch können hohe Eigenspannungen aufgrund geringerer plastischer Dehnungsreserven in diesen Schweißnähten die Sicherheit der Bauteile vermindern. Diese sind insbesondere im Zusammenhang mit Wasserstoff und Härtegefügen risskritisch. Niedrige Bauteilbeanspruchungen und Kosteneinsparungen lassen sich heutzutage mit modernen fokussierten Lichtbogenvarianten und engeren Nahtspalten erreichen. Die vorliegende Studie zeigt allerdings, dass diese modernen Schweißprozesse und die angepasste Nahtgeometrie höhere Wasserstoffkonzentrationen und signifikant gesteigerte oberflächennahe Zugeigenspannungsniveaus bedingen. Anhand mehrlagiger Schweißversuche an S960QL unter Variation von Wärmeführung, Lichtbogenvariante und Nahtöffnungswinkel wurden die Effekte und Wechselwirkungen unter Zuhilfenahme von Eigenspannungsanalytik mittels Röntgendiffraktometrie und Wasserstoffanalytik mittels Trägergasheißextraktion systematisch untersucht. Das Schweißgefüge führte unter kritischer mechanischer Beanspruchung und erhöhtem Gehalt an diffusiblem Wasserstoff insbesondere bei geringem Nahtöffnungswinkel und fokussiertem Lichtbogen zu einer deutlichen Ausbildung von Mikrorissen. Die Mikrorisse führten teils zu einer makroskopischen Ausprägung. Durch Analysen zur Nachwärmung aus der Schweißwärme heraus konnten suffiziente Wärmeführungsparameter für eine effektive Prävention solcher Risse erarbeitet werden. Die vorliegende Arbeit zeigt anhand des Interaktionssystems bei der wasserstoffunterstützten Kaltrissbildung Gefüge-Beanspruchung-Wasserstoff, welche Wärmeführungs- und Schweißparameter sich für die hochfesten Feinkornbaustähle zur Kaltrissvermeidung eignen. T2 - 3. Niedersächsisches Symposium Materialtechnik CY - Clausthal-Zellerfeld, Germany DA - 14.02.2019 KW - Hochfeste Feinkornbaustähle KW - Kaltrisse KW - MAG-Schweißen KW - Eigenspannungen KW - Wasserstoff KW - Wärmeführung PY - 2019 SN - 978-3-8440-6471-1 SN - 2364-0804 VL - 7 SP - 377 EP - 389 PB - Shaker Verlag CY - Aachen AN - OPUS4-47497 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Reinemann, Steffi A1 - Lehmann, Jens A1 - Rosemann, Paul A1 - Babutzka, Martin A1 - Bohlmann, Tatjana A1 - Burkert, Andreas T1 - Optimierung industrieller Korundschleifprozesse zur Sicherstellung der Korrosionsbeständigkeit nichtrostender Stähle N2 - Durch eine breite Beteiligung von Schleifmittelherstellern, -anwendern und wissenschaftlichen Einrichtungen im projektbegleitenden Ausschuss (PA) konnte der vielschichtige Themenkomplex „Schleifen“ im Kontext zu den Projektzielen umfassend untersucht werden. Es wurden praxisrelevante Parameterfelder definiert, die eine erfolgreiche Aufklärung der Projektfragestellung ermöglichten. Im Zuge der Untersuchungen wurde ein signifikanter Einfluss beim Einsatz von Granulatschleifbändern auf das Korrosionsverhalten geschliffener Oberflächen festgestellt. Damit zeigten geschliffene Oberflächen regelmäßig eine schlechtere Korrosionsbeständigkeit als Oberflächen, die mit sonst gleichen Parametern mit einlagig gestreuten Bändern bearbeitet wurden. Die durch einige Untersuchungsergebnisse aus vorangegangenen AiF-Vorhaben ursprünglich verfolgte These, dass Unterschiede in der Korrosionsbeständigkeit auf die Kornart der Schleifmittel Korund bzw. SiC zurückzuführen ist, konnte nur bedingt bestätigt werden. Bei den systematischen Untersuchungen innerhalb dieses Projektes erwies sich der Einfluss der Kornart im Vergleich zum Einfluss des Schleifbandtyps (Granulat bzw. einlagig gestreutes Korn) als weniger relevant. Durch weiterführende Untersuchungen konnten auf Oberflächen, die mit Granulatschleifbändern bearbeitet wurden, große Materialaufplattungen aus Eigenmaterial festgestellt werden. Das Eigenmaterial wird dabei im Schleifprozess zunächst abgetragen und aufgrund der Topografie des Schleifbandes zeitweise auf den Bändern festgehalten. Später lösen sich diese Materialanhäufungen vom Band ab und können prozessbedingt durch Wärme- und Krafteinwirkung auf den bearbeiteten Oberflächen aufgeplattet werden. Durch REM und KorroPad Untersuchungen ließen sich Bereiche mit solchen Eigenmaterialaufplattungen eindeutig als wesentliche Ausgangspunkte für Korrosionsprozesse identifizieren. Das aufgeplattete Material ist stark verformt, thermisch beeinflusst und bildet eine Spaltgeometrie zur Bauteiloberfläche aus. Diese Veränderungen führen zur Störung der Passivschichtausbildung in diesen Bereichen und verursachen damit eine erhöhte Korrosionsanfälligkeit der Oberflächen. Durch gezielte Nachbearbeitungsprozesse ist es möglich, die Eigenmaterialaufplattungen von den Oberflächen zu entfernen. Im Rahmen des Vorhabens wurde dazu eine Nachbearbeitung mittels Schleifvlies geprüft, die zu einer Entfernung der Eigenmaterialaufplattungen und damit zu einer Wiederherstellung der erwarteten Korrosionsbeständigkeit führte. Wird der Endschliff von Oberflächen mit einlagig gestreutem Korn ausgeführt, sind ebenfalls keine korrosionsrelevanten Materialaufplattungen zu erwarten. Die in einem vorhergehenden AiF Vorhaben IGF 17136 N/1 entwickelte Methode der KorroPad-Prüfung konnte auch hier erfolgreich für die Untersuchung der Auswirkung unterschiedlicher Prozessparameter auf die Korrosionsbeständigkeit der Oberflächen eingesetzt werden. Zudem erwies sich das EPR-SL-Verfahren als ein weiterer Ansatz, um die Passivschichtstabilität verschieden geschliffener Oberflächen vergleichend untersuchen zu können. Mit den nun vorliegenden Erkenntnissen können kmU künftig durch Anpassungen und Optimierung von Schleifprozessen eine gute Korrosionsbeständigkeit der bearbeiteten Oberflächen sicherstellen. Die Optimierung der Prozessparameter und -schritte kann durch den Einsatz der KorroPad-Prüfung Inhouse erfolgen und somit die laufende Fertigung im Rahmen der Qualitätsprüfung überwacht und dokumentiert werden. KW - KorroPad KW - Korrosion KW - Korrosionsbeständigkeit KW - Korrosionsschutz KW - Verfleckungen KW - Nichtrostender Stahl KW - Schleifen KW - Oberfläche PY - 2019 SP - 1 EP - 74 AN - OPUS4-47729 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brunner-Schwer, C. A1 - Graf, B. A1 - Rethmeier, Michael T1 - Laser-Plasma-Hybrid-Cladding: Possibilities in the combination 2 of arc and laser for deposition welding N2 - Plasma-Transferred-Arc (PTA) welding is a process that enables high deposition rates, but also causes increased thermal load on the component. Laser based Direct Energy Deposition (DED) welding, on the other hand, achieves a high level of precision and thus comparatively low deposition rates, which can lead to high processing costs. Combining laser and arc energy aims to exploit the respective advantages of both technologies. In this study, different possibilities of this process combination are presented using a PTA system and a 2 kW disk laser. This includes the combination in a common process zone as a highspeed plasma laser cladding technology (HPLC), which achieves process speeds of 10 m/min. Besides that it is being examined whether a pre-running plasma arc can be used to coat difficult-to-weld rail steel with a carbon content of 0.8 % due to a preheating effect. Furthermore, a smoothing of the coating by a plasma arc following the laser is investigated. T2 - Lasers in Manufacturing 2019 CY - Munich, Germany DA - 24.06.2019 KW - Plasma-Transferred-Arc KW - Direct Energy Deposition KW - highspeed plasma laser cladding KW - deposition welding PY - 2019 SP - 1 EP - 9 AN - OPUS4-48724 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakir, Nasim A1 - Biltgen, J. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Influence of Partial Penetration Laser Hybrid Welding Parameters on the Solidification Cracking for Thick-Walled Structures N2 - In this study, the influence of the welding speed and the arc power on the solidification crack formation for partial penetration laser hybrid welded Thick-Walled plates were investigated. Experimentally, a linear correlation between the welding velocity and the crack number was observed. That is by reducing the welding velocity the crack number was reduced. The reduced welding velocity showed a strong impact on stress, as the model demonstrated a very lower stress amount in comparison to the reference case. The reduction of the welding speed could be a helpful technique to reduce the hot cracking. The wire feed speed showed a very slight influence on the crack formation. That can be returned to the large distance between the critical region for cracking and the arc region. T2 - Lasers in Manufacturing Conference 2019 CY - Munich, Germany DA - 24.06.2019 KW - Hybrid laser-arc welding KW - Solidification cracking KW - Thick-walled steel KW - Numerical simulation PY - 2019 SP - 1 EP - 7 PB - WLT Wissenschaftliche Gesellschaft Lasertechnik e.V AN - OPUS4-48733 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Rades, Steffi A1 - Natte, Kishore A1 - Unger, Wolfgang T1 - NanoValid D.5.47 Annex 1, Inter-laboratory comparison on measurand particle size/particle size distribution - Report of the results N2 - An inter-laboratory comparison on the particle size, expressed as mean diameter d, of nanoscaled SiO2 (#14 BAM Silica (see NanoValid DoW, D.5.41/5.42)) has been performed. The majority of participants used Dynamic Light Scattering (DLS). A few used Electron Microscopy as method. Following methods had been applied by only one partner, respectively: Small Angle X-ray Scattering, Analytical Ultracentrifugation, Atomic Force Microscopy and Atomizer with electric mobility spectrometer. KW - Nanoparticle size measurement KW - Silica nanoparticles KW - Inter-laboratory comparison KW - EU FP7 project NanoValid PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-488117 DO - https://doi.org/10.5281/zenodo.3380570 SP - 1 EP - 23 PB - Zenodo CY - Geneva AN - OPUS4-48811 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Rades, Steffi A1 - Unger, Wolfgang T1 - NanoValid D.5.47 Annex 3 Inter-laboratory comparison on measurand specific surface area (BET) of nanoparticular Titania (#15 BAM Titania): Report of the results N2 - This Report describes an inter-laboratory comparison aiming on the establishment of the used method (BET) as a reference method. Another purpose was the certification of the porous reference material #15 BAM Titania as CRM BAM-P110 (cf. D 5.41/42). The certified values determined by nitrogen ad-sorption at 77.3 K according to the international standards ISO 15901-2 and ISO 9277 are summarized in the Table below. KW - Inter-laboratory comparison KW - Specific Surface Area (BET) KW - Nanoparticular TiO2 (Anatase) KW - EU FP7 project NanoValid PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-488491 DO - https://doi.org/10.5281/zenodo.3379612 SP - 1 EP - 22 PB - Zenodo CY - Geneva AN - OPUS4-48849 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Rades, Steffi A1 - Natte, Kishore A1 - Unger, Wolfgang T1 - NanoValid D.5.47 Annex 2 Inter-laboratory comparison on measurand surface charge (Zeta Potential) of silica particles: Report of the results N2 - An inter-laboratory comparison on the surface charge, expressed as zeta potential ζ, of nanoscaled SiO2 has been performed using #14 BAM Silica (see D.5.41/5.42) nanoparticles. The comparability of results delivered by participants has been tested. The Task 5.4 of NanoValid is designed to test, compare and validate current methods to measure and characterize physicochemical properties of selected engineered nanoparticles. The measurand is Surface charge expressed as zeta-Potential. The measurements are to be accompanied by estimates of the uncertainties at a confidence level of 95%, deduced from the standard uncertainties. Therefore an uncertainty budget comprising statistical (Type A) and systematic (Type B) errors has to be established and delivered for the measurand. The protocol comprises two Annexes addressing the establishment of uncertainty budgets following GUM. The final goal of the comparison is to identify those methods of measurement which have potential as reference methods in pc characterization of nanoparticles for the determination of a given measurand. KW - Inter-laborator comparison KW - Surface charge KW - Zeta potential KW - Uncertainty budget KW - Silica nanoparticles KW - NanoValid PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-488483 DO - https://doi.org/10.5281/zenodo.3379815 SP - 1 EP - 10 PB - Zenodo CY - Geneva AN - OPUS4-48848 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Brandes, E. A1 - Stolz, T. A1 - Adebahr-Lindner, Yvonne A1 - Krischok, Frank T1 - Sicherheitstechnische Kenngrößen für die Tankschifffahrt auf Binnenwasserstraßen T1 - Safety characteristic data for the tanker shipping on inland waterways N2 - Im Europäisches Übereinkommen über die Internationale Beförderung gefährlicher Güter auf Binnenwasserstraßen ist festgelegt, welche gefährlichen Güter unter welchen Bedingungen auf europäischen Binnenwasserstraßen befördert werden dürfen. Tabelle C ‚Verzeichnis der zur Beförderung in Tankschiffen zugelassenen gefährlichen Stoffe in numerischer Reihenfolge’ (ADN 3.2.2) listet für die Stoffe, Gemische und Lösungen, deren Beförderung in Tankschiffen zugelassen ist, die anzuwendenden besonderen Vorschriften entweder in vollständiger Information oder in kodierter Form auf. In dieser Tabelle C werden für die einzelnen Stoffe vor allem die zu verwendenden Tankschifftypen, deren Ausrüstung sowie Anforderungen hinsichtlich des Explosionsschutzes, des Schutzes der aquatischen Umwelt und des Schutzes der Menschen vor längerfristigen gesundheitlichen Schäden festgelegt. Bei dem Datenmaterial handelt es sich um durch PTB und BAM bewertete, experimentell oder rechnerisch ermittelte sicherheitstechnische Kenngrößen sowie um Angaben zu den aquatoxischen Eigenschaften und zu den längerfristigen gesundheitlichen Wirkungen auf den Menschen. Die Angaben zum Wasserverunreinigungspotential und die Zuordnungen zu den aquatoxischen Gefahren N1, N2, N3 wurden im Rahmen der Arbeiten der Zentralkommission für die Rheinschifffahrt (ZKR) zu Tabelle C vom Umweltbundesamt (UBA, J. Seelisch) zusammengestellt und bewertet. Die Angaben zu den längerfristigen gesundheitlichen Wirkungen auf den Menschen entsprechen den harmonisierten Einstufungen der EU. KW - Sicherheitstechnische Kenngrößen KW - Ladetankausrüstung KW - Tankschifftyp KW - ADN Tabelle C KW - Binnenwasserstraßen KW - Beförderung gefährlicher Güter KW - Europäisches Übereinkommen PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-495985 DO - https://doi.org/10.7795/530.20190422 SP - 1 EP - 261 AN - OPUS4-49598 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - von Werder, Julia A1 - Simon, Sebastian A1 - Meng, Birgit ED - Gemrich, J. T1 - Hydrothermal Treatment of Ultra-High-Performance Concrete: Mechanical Properties and Phase Composition N2 - The advantages of treating prefabricated components made of Ultra-High-Performance Concrete (UCPC) at 90 °C are largely recognized, while hydrothermal treatment at 185 °C and the corresponding saturation pressure of 1.1 MPa, in contrast, is not applied in building practice so far and was studied only by a few researchers. In the research presented, the parameters pre-storage-time before treatment and dwell time in the autoclave were systematically varied. The results illustrate in which way compressive strength increases with the duration of treatment. Already samples which were only heated up and immediately cooled down show an increase in strength compared to the 28-day reference of about 10 %. After 20 h the maximum increase of about 25 % is reached. Interestingly the compressive strength of samples treated very long hardly decreases. It can be therefore concluded that for the composition investigated the achievable mechanical strength is not severely sensitive regarding the duration of the treatment. Also, pre-storage times before autoclaving longer than 0.5 days showed no significant impact on strength development. The phase composition measured by XRD exhibits significant changes compared to the reference. The amount of ettringite and portlandite have vanished, the cement clinker phases are substantially decreased and hydroxylellestadite and hydrogarnet are formed as new phases. The increase in strength can be assigned to an improved pozzolanic and hydraulic reaction. Contradictory to literature, there was found no tobermorite, a mineral which is known to be susceptible for disintegration at Long autoclaving duration. This explains why no significant strength loss appeared. T2 - 15th International Congress on the Chemistry of Cement CY - Prague, Czech Republik DA - 16.09.2019 KW - Hydrothermal treatment KW - UHPC KW - Phase composition KW - Mechanical strength PY - 2019 SN - 2523-935X SP - 1 EP - 11 AN - OPUS4-49481 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - von Werder, Julia A1 - Gardei, André A1 - Meng, Birgit ED - Caprai, V. ED - Brouwers, H. J. H. T1 - Functionalization of fibres for cement-based materials - selected test methods N2 - The low tensile strength of cement-based materials can be improved by the addition of fibres. In a joint research project, an industrial partner designed special coatings for polymer and carbon fibres by integrating surfactants and hydrophilic compounds. Aim of the developed functionalization was to ensure an even coverage of the fibre surfaces and to anchor them chemically in the cement-based matrix. Task of the BAM was to quantify the effect of the improved bond. In a first step a workable mortar adjusted to the strength of the tested fibres was developed and the fibre distribution assessed by light microscopy and computed tomography. To test the new coating for its efficiency to prevent cracking during hardening and to improve the loadbearing behaviour new test setups were developed or existing methods were adjusted. The experiments showed that the functionalization leads to a reduction of the crack area measured after the exposure of the wet mortar to strong drying conditions in the wind channel. Regarding the Efficiency to mitigate shrinkage cracks the functionalisation turned out to be more efficient for fibres made from polyacrylonitrile (PAN) than for carbon fibres. An improvement of the tensile strength after cracking of the cementitious matrix could only be documented for the coated carbon fibres. It could be quantified, however, only in the three-point bending tests because the fibres turned out to be too brittle for the applied single fibre pull-through test. T2 - 2nd International Conference on Sustainable Building Materials CY - Eindhoven, Netherlands DA - 12.08.2019 KW - Fibres KW - Functionalization KW - Mortar KW - Computed tomography KW - Shrinkage PY - 2019 VL - 5 SP - 16 EP - 25 AN - OPUS4-49480 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ernst, A. A1 - Klein, S. A1 - Hall, T. A1 - Ávila Calderón, Luis A1 - Bähre, D. T1 - Electrochemical dressing of hard tools for abrasive precision machining N2 - In this study an approach for dressing metallic bonded honing stones with hard cutting grains on the basis of electrolysis is investigated. By a combination of concepts from electrochemical machining (ECM) and electropolishing a test rig was designed and put into operation. In general, it can be stated that the Approach investigated in this paper has proved to be a suitable dressing method for honing stones. However, the dressing result is highly dependent on bond components, cutting grain size and concentration which lead to local differences in the material removal and irregular topographies. This could be overcome, for example, by setting the dressing parameters more precisely based on the best results presented in this paper. T2 - International Symposium on ElectroChemical Machining Technology CY - Saarbrücken, Germany DA - 14.11.2019 KW - Irregular topography KW - Honing KW - Electrochemical dressing KW - Honing Stone KW - Laser Scanning Microscopy KW - Electropolishing PY - 2019 SN - 978-3-00-064086-5 SP - 96 EP - 108 PB - Fertigungstechnik Saarbrücken CY - Saarbrücken AN - OPUS4-49490 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lüth, Peter A1 - Frost, K. A1 - Kurth, Lutz A1 - Malow, Marcus A1 - Schmidt, Martin A1 - Michael-Schulz, Heike A1 - Uhlig, S. A1 - Zakel, S. T1 - CEQAT-DGHS Ringversuchsprogramm für die Chemikaliensicherheit - Schlussfolgerungen N2 - Die Ursachen für Chemikalienunfälle können vielfältig sein. Prävention beginnt bereits im Prüflabor, wenn Chemikalien auf ihre gefährlichen Eigenschaften getestet werden. Dazu sind Prüfmethoden entwickelt und veröffentlicht worden, die heute weltweit Anwendung finden. Auf die Validität der Prüfmethode und richtige Durchführung der Prüfung im Laboratorium müssen sich Sicherheitsfachkräfte, Transporteure oder Händler verlassen können. Anhand der in den letzten 10 Jahren im Rahmen des CEQAT-DGHS von BAM und PTB durchgeführten Ringversuche (RV) wird gezeigt, dass bei allen bisher untersuchten Prüfmethoden ein Verbesserungsbedarf besteht. Die RV müssen daher zunächst auf die Methodenverbesserung und -validierung abzielen und nicht auf Leistungstests. Das Labormanagement und die praktische Durchführung der Prüfung sind in vielen Laboratorien verbesserungsbedürftig. Der Begriff „Erfahrung der Prüfer“ ist kritisch zu sehen: Eine „lange Erfahrung mit vielen Prüfungen“ ist nicht unbedingt ein Garant für richtige Ergebnisse. T2 - 15. BAM-PTB-Kolloquium zur chemischen und physikalischen Sicherheitstechnik CY - Braunschweig, Germany DA - 21.05.2019 KW - Gefahrgut KW - Gefahrstoff KW - Ringversuch KW - Prüfmethode KW - Validierung KW - Qualitätssicherung PY - 2019 UR - https://www.ptb.de/cms/index.php?id=18763 DO - https://doi.org/10.7795/210.20190521M SP - 1 EP - 8 PB - Physikalisch-Technische Bundesanstalt (PTB) CY - Braunschweig AN - OPUS4-49489 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Gekoppelte numerische Untersuchung der Bildung von Mittelrippendefekten beim Hochleistungslaserstrahlschweißen N2 - Die Entstehung von Erstarrungsrissen stellt ein in der Schweißtechnik lange bekanntes Problem dar. Diese prozessseitige Herausforderung ist selbst nach dem heutigen Wissenstand schwer zu beherrschen und gefährdet die Sicherheit der gefügten Bauteile. Dieses Problem erweist sich als besonders schwierig beim einlagigen Hochleistungslaserstrahlschweißen von Metallteilen hoher Blechstärke, welche eine essentielle Rolle in vielerlei industriellen Anwendungen spielen. Gegenstand des hier bearbeiteten Forschungsprojekts war die numerische Untersuchung der Entstehungsmechanismen des Mittelrippendefekts beim Laserstrahlschweißen niedriglegierter Stähle. Mittels mehrerer gekoppelter Simulationen, für welche sowohl kommerziellen Softwares, wie COMSOL Multiphysics und ANSYS, als auch in-house entwickelte Programme eingesetzt worden sind, wurden die am stärksten ausgeprägten Mechanismen der Erstarrungsrissbildung und deren Zusammenspiel aufgeklärt. Begleitend zur Simulation wurden mehrere experimentelle Untersuchungen für den niedriglegierten Baustahl S355 an den Blechdicken 12 mm und 15 mm zu deren Validierung durchgeführt. Die Ergebnisse der Simulation des Kristallwachstums, der Diffusion und der Makroseigerung von Schwefel zeigen, dass die Risse für bestimmte Werkstoffe mit einer hohen Konzentration an Verunreinigungen hauptsächlich metallurgisch bedingt entstehen können. Allerdings zeigte die Untersuchung des Einflusses der Ausbauchung (Bulging) im Mittenbereich der Schweißnaht auf das transiente Temperaturfeld und die transienten Transversalspannungen im risskritischen Bereich auch, dass die Rissbildung nicht nur metallurgisch bedingt und insbesondere auch für aus metallurgischer Sicht eigentlich rissunkritische Materialien auftreten kann. Der Bulging-Bereich hat sich in der Untersuchung als besonders kritisch in allen Teilen der Simulationskette gezeigt. Die Einflüsse dieser geometrischen Besonderheit konnten bei allen physikalischen Teilaspekten der Problematik als heißrissinduzierend identifiziert werden. Von besonderer Bedeutung wird an dieser Stelle das erkannte Zusammenspiel dieser Einflüsse hervorgehoben. Bisher wurde die Bildung der Erstarrungsrisse hauptsächlich durch einen einzelnen physikalischen Aspekt, wie z.B. rein metallurgisch oder rein thermomechanisch bedingt, isoliert betrachtet. Die gewonnen Erkenntnisse über die Einflüsse des Bulgings auf die unterschiedlichen Teilaspekte zeigen deutlich, dass alle Entstehungsmechanismen auch die Schmelzbadgeometrie als Ursprung haben. Von dieser hängen die transienten Temperatur- und Spannungsfelder, die Kristallwachsrichtung, die Erstarrungsgeschwindigkeit und die Konzentration von Verunreinigungen, welche zur Entstehung von niedrigschmelzenden Phasen führt, ab. Die Ergebnisse des Forschungsvorhabens sind vielfach in referierten Zeitschriften und auf Fachtagungen veröffentlicht worden. Hervorzuheben dabei ist der „Best Presentation Award“ auf der LANE Conference 2018 in Fürth, wodurch die Thematik einem breiten Publikum bekannt gemacht werden konnte. KW - Laserstrahlschweißen KW - Mittelrippendefekt KW - Simulation PY - 2019 SP - 1 EP - 14 AN - OPUS4-49516 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lüth, Peter A1 - Frost, K. A1 - Kurth, Lutz A1 - Malow, Marcus A1 - Schmidt, Martin A1 - Michael-Schulz, Heike A1 - Uhlig, S. A1 - Zakel, S. T1 - CEQAT-DGHS Ringversuchsprogramm für die Chemikaliensicherheit – Entwicklung von Verfahren zur Verifizierung der Prüfapparatur am Beispiel der Prüfmethode UN Test N.5 N2 - Prävention beginnt im Prüflabor, wenn Chemikalien auf ihre gefährlichen Eigenschaften getestet werden. Dazu sind Prüfmethoden entwickelt und veröffentlicht worden, die heute weltweit Anwendung finden. Auf die Validität der Prüfmethode und richtige Durchführung der Prüfung im Laboratorium müssen sich Sicherheitsfachkräfte, Transporteure oder Händler verlassen können. Anhand der in den letzten 10 Jahren im Rahmen des CEQAT-DGHS von BAM und PTB durchgeführten Ringversuche (RV) wird gezeigt, dass bei allen bisher untersuchten Prüfmethoden ein Verbesserungsbedarf besteht. Die RV müssen daher zunächst auf die Methodenverbesserung und -validierung abzielen und nicht auf Leistungstests. Das Labormanagement und die praktische Durchführung der Prüfung sind in vielen Laboratorien verbesserungsbedürftig. Der Begriff „Erfahrung der Prüfer“ ist kritisch zu sehen: Eine „lange Erfahrung mit vielen Prüfungen“ ist nicht unbedingt ein Garant für richtige Ergebnisse. Bei der Prüfung der gefährlichen Eigenschaften von Chemikalien sind Referenzmaterialen auf Grund der Instabilität in der Regel nicht verfügbar. Für Prüflaboratorien sind RV daher eine Alternative bei der Qualitätssicherung. RV sind jedoch aufwendig und können nur in relativ großen Zeitabständen durchgeführt werden. Es sind deshalb Verfahren zur Verifizierung z. B. der in den Laboratorien verwendeten Prüfapparaturen zu entwickeln. Die Entwicklung von Verifizierungsverfahren wird am Bespiel der Prüfmethode UN Test N.5 demonstriert. T2 - 15. BAM-PTB-Kolloquium zur chemischen und physikalischen Sicherheitstechnik CY - Braunschweig, Germany DA - 21.05.2019 KW - Gefahrgut KW - Gefahrstoff KW - Ringversuch KW - Prüfmethode KW - Validierung KW - Qualitätssicherung KW - Verifizierung PY - 2019 UR - https://www.ptb.de/cms/index.php?id=18763 DO - https://doi.org/10.7795/210.20190521E SP - 1 EP - 10 CY - Braunschweig AN - OPUS4-49495 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niemz, P. A1 - Baensch, Franziska A1 - Brunner, A. J. A1 - Gaff, M. T1 - Acoustic Emission Analysis and Synchrotron- Based Microtomography on Glued Shear Strength Samples from Spruce Solid Wood N2 - For a better understanding of the damage of glued wood tensile tests on miniature specimens made of glued spruce wood with acoustic emission and in-situ synchrotron-based X-ray computer microtomography has been monitored. As adhesive, urea-formaldehyde resin was used. For comparison purposes, tensile tests were carried out on solid wood and bonded miniature tensile shear samples with acoustic emission. The acoustic emission signals of all experiments were with classified pattern recognition. This resulted in two classes of signals for each two frequency peaks. In one class was the low-frequency, in the other the higher frequency peak of higher intensity, but this essentially independent from the structure (solid wood or plywood) and the size scale of the test specimens. The influence of the adhesive layers was determined on plywood test specimens in laboratory scale and on miniature test specimens with an adhesive layer and selected fiber orientations examined. This gave evidence that the sound emission signals from the failure of the adhesive layer presumably of the class with low frequency signals peak in the range of services can be assigned. T2 - 21st International Nondestructive Testing and Evaluation of Wood Symposium CY - Freiburg, Germany DA - 24.09.2019 KW - Bondline KW - Insitu test KW - Acoustic emission KW - Sychrotron tomography PY - 2019 SP - 168 EP - 175 AN - OPUS4-49558 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Uhlmann, E. A1 - Düchting, J. A1 - Petrat, T. A1 - Graf, B. A1 - Rethmeier, Michael T1 - Heat treatment of SLM-LMD hybrid components N2 - Additive manufacturing is no longer just used for the production of prototypes but already found its way into the industrial production. However, the fabrication of massive metallic parts with high geometrical complexity is still too time-consuming to be economically viable. The combination of the powder bed-based selective laser melting process (SLM), known for its geometrical freedom and accuracy, and the nozzle-based laser metal deposition process (LMD), known for its high build-up rates, has great potential to reduce the process duration. For the industrial application of the SLM-LMD hybrid process chain it is necessary to investigate the interaction of the processes and its effect on the material properties to guarantee part quality and prevent component failure. Therefore, hybrid components are manufactured and examined before and after the heat treatment regarding the microstructure and the hardness in the SLM-LMD transition zone. The experiments are conducted using the nickel-based alloy Inconel 718. T2 - LiM 2019 CY - München, Germany DA - 23.06.2019 KW - Additive Manufacturing KW - Selective Laser Melting KW - Hybrid components KW - Inconel 718 KW - Laser Metal Deposition PY - 2019 SP - 1 EP - 9 AN - OPUS4-48410 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Metz, Christian A1 - Franz, Philipp A1 - Maierhofer, Christiane A1 - Wachtendorf, Volker A1 - Fischer, C. ED - Ziegahn, K.-F. T1 - Untersuchung der Beständigkeit additiv gefertigter Bauteile durch Thermografie nach künstlicher Bewitterung N2 - Additiv gefertigte Prüfkörper aus Polyamid 12 (Laser Sinter Verfahren) und Acrylnitril-Butadien-Styrol (Fused Layer Modeling Verfahren) wurden über 2000 Stunden künstlich bewittert und ihr Alterungsverhalten untersucht. Die Ergebnisse wurden anschließend mit denen von Prüfkörpern verglichen, welche auf dieselbe Weise künstlich bewittert, aber mittels konventionellem KunststoffSpritzguss hergestellt wurden. T2 - 48. Jahrestagung der GUS 2019 CY - Stutensee, Germany DA - 27.03.2019 KW - Polymere KW - Additive Fertigung KW - 3D Druck KW - Künstliche Bewitterung KW - Thermografie PY - 2019 SN - 978-3-9818507-3-4 VL - 48 SP - 207 EP - 216 CY - Pfinztal (Berghausen) AN - OPUS4-48502 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nolze, Gert A1 - Saliwan Neumann, Romeo A1 - Reith, F. A1 - Etschmann, B. A1 - Kilburn, M. R. A1 - Brugger, J. T1 - Unravelling the formation histories of placer gold and platinum-group mineral particles from Corrego Bom Successo, Brazil: A window into noble metal cycling N2 - Gold and platinum-group-metals (PGM) are cycled through Earth's environments by interwoven geological, physical, chemical and biological processes leading to the trans/neoformation of metallic particles in placers. The placer deposit at Corrego Bom Successo (CBS, Brazil) is one of the few localities worldwide containing secondary gold- and PGM-particles. Placer gold consists of detrital particles from nearby hydrothermal deposits that were transformed in the surface environment. Processes that have affected these particles include shortdistance transport, chemical de-alloying of the primary Gold silver, and (bio)geochemical dissolution/reprecipitation of Gold leading to the formation of pure, secondary gold and the Dispersion of gold nanoparticles. The latter processes are likely mediated by non-living organic matter (OM) and bacterial biofilms residing on the particles. The biofilms are largely composed of metallophillic β- and γ-Proteobacteria. Abundant mobile gold and platinum nanoparticles were detected in surface waters, suggesting similar mobilities of these metals. Earlier hydrothermal processes have led to the formation of coarsely-crystalline, arborescent dendritic potarite (PdHg). On potarite surfaces, biogeochemical processes have then led to the formation of platinum- and palladium-rich micro-crystalline layers, which make up the botryoidal platinum palladium aggregates. Subsequently potarite was dissolved from the core of many aggregates leaving voids now often filled by secondary anatase (TiO2) containing biophilic elements. The presence of fungal structures associated with the anatase suggests that fungi may have contributed to ist formation. For the first time a primary magmatic PGM-particle comprising a mono-crystalline platinum palladium-alloy with platinum iridium osmium inclusions was described from this locality, finally defining a possible primary source for the PGM mineralisation. In conclusion, the formation of modern-day placer gold- and PGM-particles at CBS began 100s ofmillions of years ago bymagmatic and hydrothermal processes. These provided the metal sources for more recent biogeochemical cycling of PGEs and gold that led to the trans/neoformation of gold- and PGM-particles. KW - Gold KW - Platinum-group-metals KW - Biogeochemical cycling KW - Magmatic and hydrothermal processes KW - Biomineralisation PY - 2019 DO - https://doi.org/10.1016/j.gr.2019.07.003 SN - 1342-937X VL - 76 SP - 246 EP - 259 PB - Elsevier AN - OPUS4-48657 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Askar, Enis A1 - Aksam, A. A1 - Brandes, E. A1 - Markus, D. A1 - Stolz, T. T1 - Berechnung der Explosionsbereiche von Alkoholen, Ketonen und halogenierten Kohlenwasserstoffen im Gemisch mit Inertgasen N2 - Die Explosionsbereiche für Dreistoffsysteme aus Brennstoff, Inertgas und Luft wurden nach dem Modell der konstanten adiabatischen Flammentemperaturprofile berechnet. Für die Parametrisierung des halbempirischen Modells muss der Explosionsbereich für ein bestimmtes Dreistoffsystem aus Brennstoff, Inertgas und Luft bekannt sein. Dann lassen sich Explosionsbereiche desselben Brennstoffs mit einem beliebigen Inertgas und bei einer beliebigen Temperatur berechnen. Ergänzend zu früheren Arbeiten, in denen die Explosionsbereiche für Brenngase aus der homologen Reihe der Alkane und Alkene berechnet worden sind, wurden nun die Berechnungen für 1-Propanol, Aceton und Difluormethan durchgeführt. Als Inertgase wurden neben Stickstoff und Kohlendioxid auch die Edelgase Argon und Helium berücksichtigt. Für die Berechnung der Explosionsbereiche in Systemen mit Helium, ist das Modell erweitert worden, so dass auch die Transporteigenschaften (d.h. Wärmeleitfähigkeit, Diffusionskoeffizient) der Komponenten berücksichtigt werden. Weiterhin ist eine Möglichkeit zur praxisnahen Berechnung der Spitze des Explosionsbereichs implementiert worden. Die Ergebnisse zeigen insgesamt, dass die Berechnung der Explosionsbereiche für Alkohole, Ketone und halogenierte Kohlenwasserstoffe mit ähnlicher Genauigkeit wie für Alkane und Alkene möglich ist. Die vorgenommenen Modifikationen sind geeignet, um auch eine Berechnung für Gasgemische mit Helium durchzuführen, dessen starke inertisierende Wirkung im Vergleich zu den Inertgasen Argon oder Stickstoff vor allem auf den stark unterschiedlichen Transporteigenschaften beruht. Für die Analyse der physikalischen Vorgänge, die zur Zündung führen, ist eine spezielle Kontaktvorrichtung entwickelt worden. Damit können die Entladungen > 200 µm Länge und mit einer Dauer von > 500 µs an einer bestimmbaren Position erzeugt und untersucht werden. Für die Entladungen an der Zündgrenze bei niedrigen Spannungs- und Stromwerten (max. 30 V, 30 bis 100 mA Konstantstrombegrenzung) sind die Bedingung für die Erzeugung ermittelt worden. Das sind die Rauheit auf der Kontaktoberfläche, die langsame Kontaktöffnungsbewegung und eine geeignet regelnde Spannungsquelle mit Konstantstrombegrenzung. Damit sind für diese Entladungen an der Zündgrenze die Strom-Spannungs-Kennlinie, das Spektrum mit dominierenden Linien von Cadmium-Metalldampf sowie die Temperaturverläufe ermittelt worden. T2 - 15. BAM-PTB-Kolloquium zur chemischen und physikalischen Sicherheitstechnik CY - Brunswick, Germany DA - 21.05.2019 KW - Explosionsgrenzen KW - Inertisierung KW - Modell der konstanten Flammentemperaturen KW - Explosionsschutz PY - 2019 DO - https://doi.org/10.7795/210.20190521J SP - 1 EP - 9 AN - OPUS4-48947 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lugovtsova, Yevgeniya A1 - Johannesmann, S. A1 - Henning, B. A1 - Prager, Jens T1 - Analysis of Lamb wave mode repulsion and its implications to the characterisation of adhesive bonding strength N2 - Lamb waves are widely used for non-destructive evaluation of material parameters as well as for detection of defects. Another application of Lamb waves is quality control of adhesive joints. Researchers are currently investigating shear horizontal and zero-group velocity modes for characterisation of the adhesive bonding strength. In a new approach, Lamb wave mode repulsion is used to obtain the coupling strength between different layers to characterise the adhesive bonding strength. The modes of the individual layers become coupled in the multilayered systems forming particular regions, the so-called mode repulsion regions. This study investigates these modes and their interaction in two-layered plate-like structures with varying coupling strength both numerically, with the Scaled Boundary FEM, and experimentally T2 - International Congress on Ultrasonics CY - Bruges, Belgium DA - 03.09.2019 KW - Lamb waves KW - Multi-layered system KW - Adhesive joint KW - Mechanical strength KW - Scaled Boundary FEM PY - 2019 SP - 1 EP - 4 AN - OPUS4-48911 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Üstündag, Ö. A1 - Gook, S. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Investigation of the mechanical properties of single-pass hybrid laser-arc welded thick X120 pipeline steel plates N2 - With global increases in clean energy demand, the natural gas is gaining in importance. Pipelines are the safest and most cost-effective way of transporting natural gas. Due to high transport volume and resulting high operation pressure, the demand for ultra-high strength steel grades such as X120 is very strong. As a result of the fact that these steels are produced by thermo-mechanical controlled processing, the welding process must be selected accordingly. Based on investigations, a high heat input such as by submerged arc welding process leads to softening in the weld metal and loss of strength whereas pure laser beam welding results in high cooling rates and deteriorate toughness of the weld metal. The objective of this research is to investigate the influence of heat input to mechanical properties of hybrid laser-arc welded pipeline steels of grade X120. Test specimens with a thickness of 20 mm could be welded without preheating in a single-pass with different welding velocities to observe the largest possible parameter window of the heat input. The achieved V-notch impact energy for hybrid laser-arc welded samples was 144±37 J at a testing temperature of -40 °C. With a tensile strength of 930±4 MPa the requirements of API 5L was achieved. To prevent gravity drop-outs at the slow welding speeds, an electromagnetic weld pool support system was used, which works contactless and is based on generating Lorentz forces. It was therefore possible to control the cooling rate in order to meet the requirements of the mechanical properties. By adapting the electromagnetic weld pool support to the laser and laser hybrid welding process, the application potential of these technologies for industrial implementation can be drastically increased. T2 - 14th Pipeline Technology Conference CY - Berlin, Germany DA - 18.03.2019 KW - Mechanical properties KW - Hybrid laser arc welding KW - Pipeline steel X120 PY - 2019 UR - https://www.pipeline-conference.com/conferences/14th-pipeline-technology-conference-2019 SN - 2510-6716 SP - 1 EP - 10 AN - OPUS4-48970 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gook, S. A1 - El-Batahgy, A. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Hybrid laser arc welding of thick plates X8Ni9 for LNG tank construction N2 - Results of experimental investigations of the relationship between laser-hybrid welding process parameters, type of the filler metal and the mechanical properties of the welds made from 9% nickel cryogenic steel X8Ni9 are discussed. The results contribute to the development and conversion in the industrial practice a new laser beam-based welding technology for the automated manufacturing of LNG tanks. The remarkable heterogeneity in the chemical composition of the weld metal as well as an insufficient impact toughness could be indicated by using austenitic filler wire. The most promising results were achieved by applying 11%Ni filler wire, which is similar to the base material. A correlation between impact toughness and wire feeding speed could be shown. The highest impact toughness was 134 J at -196°C. The laser-hybrid welds passed the tensile test. The failure stress of 720 MPa with a fracture location in the base metal was achieved for all samples tested. T2 - Lasers in Manufacturing Conference 2019 CY - Munich, Germany DA - 24.06.2019 KW - X8Ni9 KW - Hybrid Laser Arc Welding KW - Cryogenic Steel KW - Low Temperature Toughness PY - 2019 SP - 1 EP - 11 PB - WLT Wissenschaftliche Gesellschaft Lasertechnik e.V. AN - OPUS4-48972 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Shapovalov, Oleg A1 - Gaal, Mate A1 - Hönig, Gerald A1 - Gradt, Thomas A1 - Weiss, S. T1 - Temperature dependence of the propagation speed of a longitudinal wave in different solids for use as a wedge material in an extreme-temperature-resistant ultrasonic transducer N2 - In special cases of angle beam ultrasonic measurement – e.g. defect detection in hot solids as well as flow measurement of liquid gases or energy storage mediums – the applied transducer has to withstand extreme temperatures. Since the irradiation angle into the specific material is determined not only by wedge design, but also by the speed of sound in both the wedge material and the tested object, the developer must take into account the speed of the wave propagation in a wedge material over the whole temperature range of transducers application. In this study we investigate the temperature dependence of the speed of longitudinal wave propagation in 10 different materials in the range from -200 °C to 400 °C. The investigated materials belong to different material classes (ceramics, glass, as well as ferrous and non-ferrous metals) and are all temperature-resistant up to at least 600 °C, and therefore applicable as wedge materials in an ultrasonic transducer for use at extreme temperatures. T2 - 23rd International Congress on Acoustics CY - Aachen, Germany DA - 09.09.2019 KW - Ultrasonic Transducer KW - Speed of sound KW - Longitudinal Wave KW - Temperature PY - 2019 SP - 4776 EP - 4782 AN - OPUS4-48980 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Üstündag, Ö. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Single-pass Hybrid Laser Arc Welding of Thick Materials Using Electromagnetic Weld Pool Support N2 - Hybrid laser-arc welding process allows single-pass welding of thick materials, provides good quality formation of joints with minimal thermal deformations and a high productivity in comparison with arc-based welding processes. Nevertheless, thick-walled steels with a thickness of 20 mm or more are still multi-pass welded using arc welding processes, due to increased process instability by increasing laser power. One limitation factor is the inadmissible formation of gravity drop-outs at the root. To prevent this, an innovative concept of electromagnetic weld pool support is used in this study. With help of such system a stable welding process can be established for 25 mm thick steel plates and beyond. Sound welds could be obtained which are tolerant to gaps and misalignment of the welded parts. The adaptation of this system to laser and hybrid laser-arc welding process can dramatically increase the potential field of application of these technologies for real industrial implementation. T2 - Lasers in Manufacturing Conference 2019 CY - Munich, Germany DA - 24.06.2019 KW - Full Penetration KW - Hybrid Laser Arc Welding KW - Electromagnetic Weld Pool Support KW - Thick Materials PY - 2019 SP - 1 EP - 8 PB - WLT Wissenschaftliche Gesellschaft Lasertechnik e.V. AN - OPUS4-48971 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schirdewahn, S. A1 - Spranger, Felix A1 - Hilgenberg, Kai A1 - Merklein, M. ED - Merklein, M. T1 - Untersuchung des tribologischen Einsatzverhaltens von lokal dispergierten Presshärtewerkzeugoberflächen N2 - Das Presshärteverfahren hat sich zur ressourceneffizienten Verarbeitung von höchstfesten Stahlwerkstoffen im Karosserieleichtbau weltweit etabliert. Die fehlerfreie Bauteilproduktion wird jedoch durch Reibungs- und Verschleißerscheinungen aufgrund hoher thermo-mechanischer Werkzeugbelastungen und fehlender Schmierstoffsysteme limitiert. Als Lösungsansatz wird eine Modifikation der Werkzeugoberfläche mittels Laserimplantation angestrebt, um folglich deren Verschleißbeständigkeit nachhaltig zu erhöhen. Das Verfahren basiert auf einem lokalen Dispergieren keramischer Hartstoffpartikel in die Werkzeugoberfläche, infolgedessen hochfeste und erhabene Strukturen im Mikrometerbereich entstehen. Aufgrund der signifikanten Reduzierung der Kontaktfläche sowie der hohen Verschleißbeständigkeit der eingesetzten TiB2-Hartstoffe wird ein verbessertes tribologisches Einsatzverhalten unter presshärtetypischen Prozessbedingungen erwartet. Zur Verifizierung dieser Annahmen wurden im Rahmen dieser Arbeit modifizierte Pin-on-Disk Tests durchgeführt, um das Reib- und Verschleißverhalten der laserimplantierten Werkzeugoberflächen unter Presshärtebedingungen zu untersuchen. Zur weiteren Vertiefung des Prozess-verständnisses wurden die verschlissenen Platinen via Tastschnittmessungen und Querschliffaufnahmen analysiert. Durch den Ergebnisvergleich mit konventionellen Werkzeugoberflächen erfolgte eine abschließende Bewertung des tribologischen Einsatzverhaltens der laserimplantierten Strukturen. T2 - 14. Erlanger Workshop Warmblechumformung 2019 CY - Fürth, Germany DA - 19.11.2019 KW - Laserimplantation KW - TiB2 KW - X38CrMoV5-3 KW - Presshärten KW - Tribologie PY - 2019 SP - 169 EP - 178 PB - Meisenbach Verlag Bamberg CY - Bamberg AN - OPUS4-49703 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Berthold, J. A1 - Vrana, J. A1 - Heckel, Thomas A1 - Kanzler, D. A1 - Jatzlau, P. A1 - Große, C. T1 - Modellgestützte Bestimmung der Auffindwahrscheinlichkeit (POD) von Reflektoren bei der Ultraschallprüfung großer Schmiedeteile N2 - Bruchmechanische Untersuchungen werden zur Vorhersage der Lebensdauer und der Wartungszyklen benutzt. Dabei wird davon ausgegangen, dass auch Objekte ohne detektierte Anzeigen Materialfehler mit einer Reflektivität kleiner der Nachweisgrenze aufweisen können. Keine detektierte Anzeige bedeutet daher für Bauteilauslegung, dass sie eine konservative Annahme machen müssen: es wird angenommen, dass das Bauteil Materialfehler in Größe der Nachweisgrenze enthält. Dies macht die Nachweisgrenze zu dem die Lebensdauer limitierenden Faktor. Bei probabilistischen Methoden wird zusätzliches Wissen, wie Zuverlässigkeit und Fehlerauffindwahrscheinlichkeiten bei der zerstörungsfreien Prüfung mit in die Berechnung einbezogen, um zu konservative Annahmen zu vermeiden. Ziel ist es eine Model-Assisted-POD aufzubauen mit der die reale volumetrische Ultraschallprüfung großer Schmiedeteile nachgebildet werden kann. Die resultierende POD soll im Weiteren in bruchmechanischen Betrachtungen Verwendung finden. In vorangegangenen Arbeiten [Preißel2015] wurde dazu der Einfluss des Prüfrasters nach der DGZfP-Richtlinie US 07:2014 auf die Fehlerauffindwahrscheinlichkeit (parametrisch) simulativ betrachtet und die Simulationstechnik experimentell validiert. In diesem Paper werden die Ergebnisse von Preißel überprüft und um eine Prüfraster-Summen-POD, die das Szenario der realen Bauteilprüfung beschreibt, erweitert. Zudem wird eine experimentell validierte, simulative, nicht-parametrische POD für schrägliegende Defekte aufgebaut. Schließlich werden erste Untersuchungen zur Defektmorphologie vorgestellt. Diese Arbeit ist im Rahmen eines Studenten-Stipendiums der DGZfP entstanden. T2 - DGZfP DACH Tagung 2019 CY - Friedrichshafen, Germany DA - 27.05.2019 KW - Schmiedeteile KW - POD KW - Ultraschall KW - Zerstörungsfreie Prüfung PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-496796 UR - http://www.ndt.net/?id=24529 VL - 24 IS - 8 SP - 1 EP - 12 PB - NDT.net CY - Kirchwald AN - OPUS4-49679 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heckel, Thomas A1 - Bertovic, Marija A1 - Rosenthal, Martina A1 - Pavlovic, M. A1 - Bartsch, L. A1 - Muhs, V. A1 - Holstein, R. T1 - Zuverlässigkeitsbetrachtungen bei der Ultraschallprüfung von Radsatzwellen im Ausbildungsbetrieb N2 - Im Rahmen der UT1-M1 Ausbildung im Ausbildungszentrum Wittenberge der DGZfP wurden statistische Untersuchungen am Beispiel der Radsatzwellenprüfung mit Testradsatzwellen durchgeführt. Diese Untersuchungen hatten zum Ziel, die wesentlichen Einflussparameter bei der Prüfung auf das Prüfergebnis zu evaluieren. Dabei wurde unter anderem die intrinsische Fähigkeit des Prüfverfahrens zum Auffinden verschiedener Reflektorgeometrien ermittelt. Die Ergebnisse der Handprüfung wurden mit Ergebnissen mechanisierter Prüfungen verglichen. Im Rahmen der Zuverlässigkeitsbetrachtung wurden die Probability of Detection (POD) und die Nachweisgrenzen ermittelt. Ziel dieser Arbeit war es auch, menschliche und organisatorische Einflussfaktoren auf die Ultraschall-Handprüfung von Radsatzwellen zu identifizieren, um Empfehlungen zur Optimierung der Ausbildung auszuarbeiten. Dazu wurden prüfungsbezogene Risiken in der Praxis mittels Fehlzustandsart- und –auswirkungsanalyse (FMEA) analysiert sowie von den Prüfern empfundene Probleme während der Ausbildung und in der Praxis mittels Fragebogen identifiziert. Die Ergebnisse der FMEA haben gezeigt, dass während des gesamten Prozesses Fehler auftreten können, für die Gegenmaßnahmen getroffen und implementiert werden sollten. Aus den Hinweisen und Erkenntnissen wurden einige Empfehlungen zur Optimierung der Ausbildung erarbeitet. T2 - DGZfP DACH Tagung 2019 CY - Friedrichshafen, Germany DA - 27.05.2019 KW - Zuverlässigkeit KW - Wellenprüfung KW - Ultraschall PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-496783 VL - 2019 SP - 1 EP - 11 AN - OPUS4-49678 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Online-Observation of Martensite Formation by combined use of Synchrotron Diffraction and Dilatometry N2 - Welding residual stress engineering by means of an adjusted martensite phase transformation would be highly attractive as detrimental tensile residual stresses may be prevented already during welding without time and cost intensive post processing. The present study shows a synchrotron diffraction analysis of a martensitic steel subjected to thermo-mechanical load cycles. Experiments were conducted regarding the microstructural strain response during the austenite to martensite transformation. The strains are a function of the temperature and the specific loads applied during cooling. The relation between the transformation plasticity of the material, the amount of martensite formed and the arising strains can thus be assessed. The lattice plane specific strains were compared to experimental findings from (macro) dilatation tests. It is shown that the microscopic material behavior differs remarkably from the one observed on the macroscopic scale, what leads to characteristic residual stresses in the material. T2 - Visual-JW 2019 & WSE 2019 The 5th International Symposium on Visualization in Joining & Welding Science through Advanced Measurements and Simulation & The 8th International Conference of Welding Science and Engineering CY - Osaka, Japan DA - 21.11.2019 KW - Martensite KW - Synchrotron KW - Dilatometry KW - Residual stress KW - Phase transformation PY - 2019 SP - 83 EP - 84 PB - SEIEI Printing Co., Ltd CY - Osaka, Japan AN - OPUS4-49770 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kannengießer, Thomas A1 - Kromm, Arne A1 - Lausch, Thomas A1 - Schröpfer, Dirk A1 - Hannemann, Andreas T1 - In-situ Observation of Stress Evolution and Cracking during High Strength Steel Welding N2 - Residual stresses are crucial when assessing the performance of welded components. The present work deals with the possibilities of transferring the real-life boundary conditions of welding, which influence the residual stress, into the laboratory. The possibilities of a test system with a load capacity of 2 MN specifically developed for online monitoring of stress formation and cracking are shown. Due to the structural design, global process, geometry and material-dependent stresses are induced, which can be quantified in-situ during welding and post weld heat treatment. Examples are presented how the conditions to be found during production are simulated in the laboratory. It is shown how welding residual stresses in high-strength steels are affected by the heat control. Elevated working temperatures significantly increase the tensile residual stresses in the heat affected zone (HAZ). The effect of mechanical stresses resulting from welding on stress relief cracking is demonstrated by the example of a creep resistant steel. Reheat cracks were monitored online during post weld heat treatment. T2 - Visual-JW 2019 & WSE 2019 The 5th International Symposium on Visualization in Joining & Welding Science through Advanced Measurements and Simulation & The 8th International Conference of Welding Science and Engineering CY - Osaka, Japan DA - 21.11.2019 KW - Residual stress KW - Restraint KW - Welding KW - Large-scale test KW - Reheat cracking PY - 2019 SP - 83 EP - 84 PB - SEIEI Printing Co., Ltd CY - Osaka, Japan AN - OPUS4-49773 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas A1 - Yahyaoui, Hamza A1 - Schröder, Nina A1 - Kannengießer, Thomas ED - Christ, H.-J. T1 - Kaltrissprüfung hochfester Feinkornbaustähle beim Schweißen mit modifiziertem Sprühlichtbogen N2 - Der konstruktive Leichtbau erfordert den zunehmenden Einsatz hochfester Feinkornbaustähle mit Streckgrenzen bis zu 1300 MPa. Um darüber hinaus Schweißzeit, Schweißnahtvolumina und Schweißkosten zu minimieren, kam es zur Entwicklung moderner Lichtbogenprozesse mit erhöhter Abschmelzleistung, wie bspw. dem modifizierten Sprühlichtbogen (mod. SLB). Dieser Beitrag zeigt Kaltrissuntersuchungen beim Einsatz des mod. SLB unter reduziertem Nahtöffnungswinkel eines Hochfesten S960QL. Mit Hilfe des fremdbeanspruchten Implant-Tests konnte dargelegt werden, dass durch die erhöhte Abschmelzleistung ein tieferes Einbrandprofil entsteht und es dadurch zu einer zeitverzögerten Rissbildung kommt. Ergebnisse des selbstbeanspruchenden TEKKEN-Tests zeigen eine deutliche Rissbildung im Schweißgut unter reduziertem Nahtöffnungswinkel. Durch eine Nachwärmung unmittelbar nach dem Schweißen kann diese Rissbildung minimiert werden. T2 - Tagung Werkstoffprüfung CY - Neu-Ulm, Germany DA - 03.12.2019 KW - Hochfester Feinkornbaustahl KW - Kaltrissprüfung KW - TEKKEN-Test KW - Implant-Test KW - Eigenspannungen PY - 2019 SN - 978-3-88355-418-1 SP - 231 EP - 236 PB - INVENTUM GmbH CY - Sankt Augustin AN - OPUS4-49923 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klingelhöffer, Hellmuth T1 - Temperaturschwankungen an Extensometern - ein vielfach vernachlässigtes Thema N2 - Extensometer werden seit langer Zeit erfolgreich für die Ermittlung von werkstoffmecha-nischen Kennwerten eingesetzt. Allerdings wurden in den letzten Jahren immer wieder durch Temperaturschwankungen bedingte Drift an Extensometern festgestellt, die be-sonders in Langzeitversuchen zu Problemen führen können. Es wurden Ursachen für die thermische Drift von Extensometern aufgezeigt. Anhand von einem Beispiel wurde gezeigt, wie sich Temperaturschwankungen an einem Extensometer auf die Ergebnisse von werkstoffmechanischen Ermüdungsversuchen auswirken können. An einem weiteren Beispiel wurde beschrieben, dass der durch Temperaturschwankungen verursachte Dehnungsfehler eines Extensometers stark von der Höhe der Temperaturschwankung und von der Dehnungsschwingbreite abhängt und, je nach Anwendungsfall größer als 1% werden kann. Es wurde verdeutlicht, dass bisherige nach Norm vorgeschriebene Maß-nahmen oft nicht ausreichen, um Einflüsse von Temperaturschwankungen am Extenso-meter zuverlässig zu unterbinden. Vorschläge wurden aufgezeigt, um die Temperatursta-bilität von Extensometern zu verbessern. Das gesamte Temperaturmanagement von Raumtemperatur, Kühlwassertemperatur, Temperaturmessung am Extensometer etc. sollte von Grund auf neu betrachtet werden, um Verbesserungen bei der Temperatur-konstanz von Extensometern zu erlangen. Ferner wurde vorgeschlagen, Extensometer in temperaturkompensierter Ausführung zu entwickeln und zu verkaufen. Dieses sollte Ret-rofits für existierende Extensometer miteinschließen. Konkrete Maßnahmen zur Imple-mentierung in Materialprüfungsnormen müssen weiter diskutiert werden. T2 - Tagung Werkstoffprüfung 2019 CY - Neu-Ulm, Germany DA - 03.12.2019 KW - Extensometer KW - Temperaturschwankungen KW - Dehnungsfehler PY - 2019 SN - 978-3-88355-418-1 SP - 361 EP - 366 PB - Inventum GmbH CY - Sankt Augustin AN - OPUS4-49965 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zakel, S. A1 - Schröder, Volkmar A1 - Askar, Enis A1 - Gabel, D. A1 - Hirsch, W. A1 - Kleinert, J. A1 - Krause, U. A1 - Krietsch, Arne A1 - Meistes, J. A1 - Sachtleben, A. A1 - Schmidt, Martin T1 - Sicherheitstechnische Kenngrößen des Explosionsschutzes von hybriden Stoffgemischen - Normungsfähige Bestimmungsverfahren N2 - In diesem Verbundvorhaben werden standardisierte Messverfahren für hybride Gemische erarbeitet, die der Bestimmung sicherheitstechnischer Kenngrößen des Explosionsschutzes dienen. Unter einem hybriden Gemisch wird dabei ein mehrphasiges System aus Brenngas oder brennbarem Dampf, sowie Luft und brennbarem Staub verstanden. Die Veröffentlichung der Ergebnisse erfolgt in einem Abschlussbericht und als DIN-Spezifikation (DIN SPEC). Diese DIN SPEC versetzt Prüfinstitute und Industrie in die Lage, Explosionsgefahren beim Betrieb technischer Anlagen mit hybriden Gemischen einzuschätzen und damit Prozesse sowohl sicherer als auch effizienter zu steuern. Dieses Projekt wird im Rahmen des WIPANOProgramms (Wissens- und Technologietransfer durch Patente und Normen) vom BMWi gefördert. T2 - 14. Fachtagung Anlagen-, Arbeits- und Umweltsicherheit CY - Köthen, Germany DA - 07.11.2019 KW - Explosionsschutz KW - Sicherheitstechnische Kenngrößen KW - Hybride Gemische KW - Normung PY - 2019 SN - 978-3-89746-220-5 SP - 73 CY - Frankfurt am Main AN - OPUS4-49954 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fritzsche, André A1 - Hilgenberg, Kai A1 - Rethmeier, Michael T1 - Influence of welding parameters on electromagnetic supported degassing of die-casted and wrought aluminum N2 - The paper describes a systematic investigation of the EM influenced laser beam welding of the aluminum die casting alloy AlSi12(Fe) in comparison to a reference material, a wrought aluminum alloy AlMg3. By using of a face centred CCD test plan, the influencing variables laser power, welding velocity and magnetic flux density are varied with regard to their influence on the remaining porosity. The global pore fraction of the weld seams was analyzed by X-ray images with ImageJ. This enabled a qualitatively very good regression model to be derived for the respective material, which identifies the dominant influencing variables. The results prove, statistically verified, for the investigated parameter range, that - the magnetic flux density is the main cause for the porosity reduction, - the porosity rises with increasing laser power the porosity in the weld seams rises, - the influence of the welding velocity is negligible, - the pore quantity in wrought alloy is more strongly minimized by the magnetic flux density than in die casting, - the porosity decreases due to the EM influence by approx. 70 % compared to the unaffected welds. This effect is emphasized by the contour line charts, which illustrate the relationship between laser power and magnetic flux density. With the exception of the quadratic influence of B at the wrought alloy, the statistical correlation shows a linear development of the respective influence variables for both aluminum alloys. In order to investigate these deviations, further simulations with a focus on weld pool geometry and weld pool flow are to be performed. In addition, the welding results can be classified in accordance with DIN EN ISO 13919-2 in the highest evaluation group B for AlMg3 and in evaluation group C for AlSi12(Fe) by applying a magnetic flux density of 350 mT. The analysis of the CT images at constant laser power and welding velocity allows a direct comparison both between the two alloys and also as a function of the magnetic flux density with regard to the number and size of pores. An increase in the magnetic flux density leads to a significant decrease in the number and volume of pores, which can be seen more clearly in wrought alloy than in die casting. Very acceptable results can be achieved for both materials and different welding parameters. This successfully demonstrates the desired process robustness and functionality of the EM system for practical applications. For subsequent investigations of overlap joints, the lowest possible laser power and a high magnetic flux density are recommended. T2 - 38th International Congress on Applications of Lasers & Electro-Optics CY - Orlando, FL, USA DA - 07.10.2019 KW - AISI D2 KW - Laser implantation KW - Surface texturing KW - TiB2 PY - 2019 SN - 978-1-940168-1-42 SP - Paper Macro 1202 AN - OPUS4-50009 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Magkos, Sotirios T1 - Iterative reconstruction from under-sampled Computed Tomography data N2 - In X-ray computed tomography (XCT), an X-ray beam of intensity I0 is transmitted through an object and its attenuated intensity I is measured when it exits the object. The attenuation of the beam depends on the attenuation coefficients along its path. The attenuation coefficients provide information about the structure and composition of the object and can be determined through mathematical operations that are referred to as reconstruction. The standard reconstruction algorithms are based on the filtered backprojection (FBP) of the measured data. While these algorithms are fast and relatively simple, they do not always succeed in computing a precise reconstruction, especially from under-sampled data. Alternatively, an image or volume can be reconstructed by solving a system of linear equations. Typically, the system of equations is too large to be solved but its solution can be approximated by iterative methods, such as the Simultaneous Iterative Reconstruction Technique (SIRT) and the Conjugate Gradient Least Squares (CGLS). This dissertation focuses on the development of a novel iterative algorithm, the Direct Iterative Reconstruction of Computed Tomography Trajectories (DIRECTT). After its reconstruction principle is explained, its performance is assessed for real parallel- and cone-beam CT (including under-sampled) data and compared to that of other established algorithms. Finally, it is demonstrated how the shape of the measured object can be modelled into DIRECTT to achieve even better reconstruction results. KW - Computed tomography KW - DIRECTT KW - Iterative algorithm KW - X-ray imaging KW - Metrics PY - 2022 SP - 1 EP - 94 PB - Universitätsbibliothek Potsdam CY - Potsdam AN - OPUS4-56465 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kupsch, Andreas A1 - Schob, D. A1 - Léonard, Fabien A1 - Müller, Bernd R. A1 - Sagradov, I. A1 - Roszak, R. A1 - Sparr, H. A1 - Franke, R. A1 - Ziegenhorn, M. A1 - Bruno, Giovanni T1 - Bestimmung der Mikrostruktur und Simulation des Schädigungsverhaltens von lasergesintertem Polyamid 12 unter quasistatischer Zugbelastung N2 - Um das Material- und Schädigungsverhalten von additiv gefertigtem Polyamid 12 (PA12) unter quasistatischer Belastung zu charakterisieren, wurden mechanische Tests und Röntgenverfahren zur Bestimmung der Mikrostruktur eingesetzt. Die Proben wurden nach dem Prinzip des Selektiven Lasersinterns (SLS) hergestellt. Unter quasistatischer Belastung mit Haltezeiten ergab sich ein viskoplastisches Materialverhalten. Im Zugversuch wurde eine maximale Zugfestigkeit von 40.6 MPa und eine Bruchdehnung von 7.4% beobachtet. Mittels Röntgenrefraktion wurde eine Erhöhung von inneren Oberflächen beobachtet, die senkrecht zur Zugrichtung orientiert sind. Die Analyse der Gesamtporosität aus Computertomographie-Messungen ergab keine Änderung infolge der Zugbelastung. Jedoch wurde eine bimodale Porengrößenverteilung und eine steigende Sphärizität festgestellt. Das Materialverhalten wurde mit dem Chaboche-Modell simuliert und ergab eine sehr gute Übereinstimmung mit den experimentellen Ergebnissen. Allerdings gestattet dieses Modell nicht, das Schädigungsverhalten abzubilden. Daher wurde zur Simulation des Schädigungsverhaltens das Modell gemäß dem Ansatz von Gurson, Tvergaard und Needleman unter Berücksichtigung der mikrostrukturellen Parameter erweitert. Der Schwerpunkt des Beitrags liegt auf den Röntgenverfahren zur experimentellen Bestimmung der Mikrostruktur. T2 - DGZfP-Jahrestagung 2021 CY - Online meeting DA - 10.05.2021 KW - Additive Fertigung (AM) KW - Polyamid 12 KW - Röntgenrefraktion KW - Computertomographie KW - Numerische Simulation PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-526833 UR - https://jahrestagung.dgzfp.de/Portals/jt2021/bb/P16.pdf SP - 1 EP - 8 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-52683 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Bernd R. A1 - Kupsch, Andreas A1 - Serrano-Munoz, Itziar A1 - Laquai, René A1 - Bruno, Giovanni T1 - Anwendungen der Röntgenrefraktionstechnik zur zerstörungsfreien Charakterisierung von Keramiken und Verbundwerkstoffen N2 - Die Brechung von Röntgenstrahlen (Röntgenrefraktion) an Grenzflächen zwischen Materialien unterschiedlicher Dichte ist analog zur Ablenk-ung von sichtbarem Licht an z.B. Glasoberflächen. Es gibt jedoch zwei wesentliche Unterschiede: a) konvexe Grenzflächen verursachen Divergenz (d.h. der Brechungsindex n ist kleiner als 1), und b) die Ablenkungswinkel sind sehr klein, und reichen von einigen Bogensekunden bis zu einigen Bogenminuten (d.h. n ist nahe bei 1); Wie auch bei sichtbarem Licht ist die Ablenkungsrichtung der Röntgenstrahlen abhängig von der Orientierung der durchstrahlten Grenzfläche. Aufgrund dieser Eigenschaften eignen sich Röntgenrefraktionsmethoden hervorragend für: a) die Erkennung und Quantifizierung von Defekten wie Poren und Mikrorissen und b) die Bewertung von Porosität und Partikeleigenschaften wie Orientierung, Größe und räumliche Verteilung. Wir zeigen die Anwendung der Röntgenrefraktionsradiographie (2,5D Technik) und der -tomographie (3D Technik) für die Untersuchung verschiedener Probleme in der Werkstoffwissenschaft und -technologie: a) Sintern von SiC-Grünkörpern b) Porositätsanalyse in Dieselpartikelfiltersilikaten c) Faser-Matrix-Haftung in Metall- und Polymermatrixverbundwerkstoffen d) Mikrorissbildung in Glaskeramik. Wir zeigen, dass der Einsatz von Röntgenrefraktionsmethoden quantitative Ergebnisse liefert, die direkt als Parameter in Werkstoffmodellen verwendet werden können. T2 - DACH-Jahrestagung 2023 CY - Friedrichshafen, Germany DA - 15.05.2023 KW - Röntgen-Refraktion KW - Verbundwerkstoffe KW - Keramik PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-576171 UR - https://jahrestagung.dgzfp.de/Portals/jt2023/BB180/Inhalt/p9.pdf UR - https://jahrestagung.dgzfp.de/Portals/jt2023/BB180/Inhalt/default.htm SN - 978-3-947971-29-9 SP - 1 EP - 16 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-57617 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kupsch, Andreas A1 - Trappe, Volker A1 - Müller, Bernd R. A1 - Bruno, Giovanni T1 - Rissentwicklung in CFK-Laminaten nachgewiesen durch in situ Röntgen-Refraktion N2 - In Leichtbauanwendungen sind Materialien mit geringen Dichten und hohen Festigkeiten gefragt. Insbesondere Faser-Kunststoff-Verbunde (FKV) erfüllen diese Anforderungen und werden zunehmend für Strukturbauteile eingesetzt. Die Oberflächen moderner Rotorblätter von Windkraftanlagen werden aus FKV gefertigt. Das Versagen dieser Materialien hat massiven Einfluss auf die Einsatzfähigkeit der gesamten Windkraftanlage. Daher ist die Kenntnis des Versagensverhaltens dieser Komponenten unter statischer und zyklischer Belastung von großem Interesse, um die Betriebsbeanspruchung abzuschätzen. Im Idealfall wird die Schadensentwicklung unter Betriebslast mit zerstörungsfreien in-situ-Prüfverfahren ermittelt. Hier berichten wir über die Beobachtung der Rissentwicklung in Carbon-Faserverstärkten Kunststoffen (CFK) unter kontinuierlicher Zugbelastung durch in-situ Synchrotron-Röntgenrefraktionsradiographie. Eine selbst entwickelte elektromechanische Zugprüfmaschine mit einem Kraftbereich bis zu 15 kN wurde in den Strahlengang an der BAMline (BESSY II) integriert. Da in herkömmlichen (Absorptions-) Radiographien Defekte wie Zwischenfaserbrüche oder Faser-Matrix-Enthaftung keinen ausreichenden Kontrast verursachen, wird zur Kontrastanhebung die Röntgenrefraktion benutzt. Hier wird das sogenannte Diffraction Enhanced Imaging (DEI) angewandt, um Primär- und gebrochene Strahlung mit Hilfe eines Analysatorkristalls zu trennen. Diese Technik ermöglicht schnelle Messungen mit einem Gesichtsfeld von einigen Quadratmillimetern (hier: 14 mm × 7.2 mm) und ist ideal für in-situ Untersuchungen. Die Bildgebung und der Zugversuch erfolgen mit einer Bildfrequenz von 0.7 / s und einer Dehnrate von 0.00055 / s . Bei 0°/90° Fasergelegen treten die ersten Zwischenfaserrisse bei 380 MPa (Dehnung 0.8 %) auf. Vor dem Versagen bei ca. 760 MPa (Dehnung 2.0 %) beobachten wir die Ausbildung eines nahezu äquidistanten Rissmusters (Risse in ca. 1 mm Abstand), das sich im geschädigten Zustand über die gesamte Probe erstreckt. T2 - DACH-Jahrestagung 2023 CY - Friedrichshafen, Germany DA - 15.05.2023 KW - Röntgen-Refraktion KW - Synchrotronstrahlung KW - CFK KW - Rissentwicklung PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-576230 SN - 978-3-947971-29-9 VL - BB 180 SP - 1 EP - 8 AN - OPUS4-57623 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Fritsch, Tobias T1 - A Multiscale Analysis of Additively Manufactured Lattice Structures N2 - Additive Manufacturing (AM) in terms of laser powder-bed fusion (L-PBF) offers new prospects regarding the design of parts and enables therefore the production of lattice structures. These lattice structures shall be implemented in various industrial applications (e.g. gas turbines) for reasons of material savings or cooling channels. However, internal defects, residual stress, and structural deviations from the nominal geometry are unavoidable. In this work, the structural integrity of lattice structures manufactured by means of L-PBF was non-destructively investigated on a multiscale approach. A workflow for quantitative 3D powder analysis in terms of particle size, particle shape, particle porosity, inter-particle distance and packing density was established. Synchrotron computed tomography (CT) was used to correlate the packing density with the particle size and particle shape. It was also observed that at least about 50% of the powder porosity was released during production of the struts. Struts are the component of lattice structures and were investigated by means of laboratory CT. The focus was on the influence of the build angle on part porosity and surface quality. The surface topography analysis was advanced by the quantitative characterisation of re-entrant surface features. This characterisation was compared with conventional surface parameters showing their complementary information, but also the need for AM specific surface parameters. The mechanical behaviour of the lattice structure was investigated with in-situ CT under compression and successive digital volume correlation (DVC). The Deformation was found to be knot-dominated, and therefore the lattice folds unit cell layer wise. The residual stress was determined experimentally for the first time in such lattice structures. Neutron diffraction was used for the non-destructive 3D stress investigation. The principal stress directions and values were determined in dependence of the number of measured directions. While a significant uni-axial stress state was found in the strut, a more hydrostatic stress state was found in the knot. In both cases, strut and knot, seven directions were at least needed to find reliable principal stress directions. KW - Additive manufacturing KW - Laser powder bed fusion KW - Residual stress KW - Surface roughness analysis KW - Computed tomography PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:517-opus4-470418 DO - https://doi.org/10.25932/publishup-47041 SP - 1 EP - 97 PB - Universitätsbibliothek Potsdam CY - Potsdam AN - OPUS4-53476 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gunnerek, R. A1 - Soundarapandiyan, G. A1 - Mishurova, T. A1 - Schröder, J. A1 - Bruno, Giovanni A1 - Boykin, J. A1 - Diaz, A. A1 - Klement, U. A1 - Hryha, E.ON T1 - Chemical mechanical polishing of powder bed fusion – laser beam processed 316 L stainless steel N2 - Additive manufacturing via powder bed fusion – laser beam (PBF-LB) enables the fabrication of complex geometries but suffers from inherently rough surfaces and surface tensile residual stresses, both of which can compromise structural integrity, particularly under fatigue loading. To address these limitations, this study investigates chemical mechanical polishing (CMP) as a surface finishing method for improving surface quality and modifying the residual stress state in PBF-LB 316 L stainless steel. The work uniquely examines how scan rotation (0◦ vs. 67◦ rotation) and contour parameters influence CMP effectiveness in material removal, surface smoothing, and subsurface stress redistribution. With a targeted material removal of 110 μm, CMP reduced surface roughness (Sa) by up to 94 %, achieving values as low as 0.7 μm. Microstructural analysis revealed no grain refinement but identified a thin, plastically deformed surface layer. This plastic deformation resulted in the transformation of tensile surface stresses (340 MPa) into beneficial compressive stresses (􀀀 400 MPa), as confirmed by synchrotron X-ray diffraction, which also showed a shift toward isotropic strain distribution. Further, these findings demonstrate that the initial scan strategy influences CMP performance and that CMP can enhance both surface integrity and mechanical reliability without altering the underlying microstructure. This study advances the understanding of how process induced microstructure and surface features affect CMP outcomes, enabling more informed design of post-processing strategies for improved surface integrity and mechanical performance in additively manufactured metals. KW - Residual stress KW - Additive manufacturing KW - Chemical mechanical polishing KW - As-built microstructure KW - Surface roughness KW - Surface finishing KW - Material removal PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-640522 DO - https://doi.org/10.1016/j.jmatprotec.2025.119055 SN - 0924-0136/ VL - 345 SP - 1 EP - 12 PB - Elsevier B.V. AN - OPUS4-64052 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bernardy, Christopher A1 - Habib, Abdel Karim A1 - zur Nedden, Philipp Maximilian A1 - von Saldern, Jakob Georg Raimund A1 - Beuth, Jan Paul A1 - Orchini, Alessandro ED - Carcassi, Marco T1 - Thermal radiation of inclined large scale hydrogen jet flames N2 - In order to assess the thermal radiation emanating from hydrogen jet flames, experiments under real scale conditions were carried out at the Test Site Technical Safety of BAM. Herein, the behavior of inclined hydrogen jet flames was investigated. The aim of the work is to determine the Surface Emissive Power and radiant heat fraction of these flames and to provide a reliable dataset for model evaluation purposes. Since the aforementioned values are not directly measurable, the incident heat radiation was measured at defined distances from the flame, as well as the flame's shape and size. The required values were then derived from these measurements. The hydrogen releases ranged from 0.005 kg/s to 0.175 kg/s with a 30 mm orifice. The mass flows were held constant during the releases, nevertheless a transient behavior of the flame could be observed since the experiments were carried out under open field conditions, with unsteady wind fields. In the literature, the flame lengths are often determined using visible light imaging, either by injecting coloring substances in the low light emitting hydrogen jet flame or by carrying out the measurements in darkness. In this work the jet flames were visualized using infrared (IR) and OH* imaging. The recorded flame shapes and resulting flame lengths are compared. Results from this showed that the flame lengths determined with OH* and IR recordings differ greatly. A flame length ratio l_(f OH*)/l_(f IR) in the range of 0.47-0.62 can be found. In addition, the SEP differ also in the range of 10 kW/m²-16 kW/m² (IR) and 40 kW/m²-80 kW/m² (OH*) for hydrogen jet flames due to differences in the determined flame surface. Conclusions regarding the determined x_(RAD )values for IR and OH* result in approximately the same range of 0.031-0.043. T2 - 11th International conference on hydrogen safety 2025 CY - Seoul, Republic of Korea DA - 22.09.2025 KW - IR and OH* measurement KW - Hydrogen release KW - Inclined jet flame KW - Thermal radiation KW - Radiant heat fraction PY - 2025 SN - 979-12-243-0274-2 SP - 837 EP - 849 AN - OPUS4-65362 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Mishurova, Tatiana T1 - Influence of residual stress and microstructure on mechanical performance of LPBF TI-6AL-4V N2 - Additive manufacturing technologies provide unique possibilities in the production of topologically optimized, near-net shape components. The main limiting factors affecting the structural integrity of Laser Powder Bed Fusion (LPBF) parts are manufacturing defects and residual stress (RS) because both of them are virtually inevitable. Taking into account the complex thermal history of LPBF materials, a prediction of the material behavior is not possible without experimental data on the microstructure, defect distribution, and RS fields. Therefore, this thesis aims to understand the factors that influence the LPBF Ti-6Al-4V material performance the most, covering both the production and the post-processing steps of manufacturing. Indeed, a parametric study on the influence of manufacturing process and post-processing on RS, defects and microstructure was performed. It was found that the volumetric energy Density (EV), commonly used for the LPBF process optimization, does neither consider the pore shapes and distribution, nor the influence of individual parameters on the volume fraction of pores. Therefore, it was recommended not to use EV without great care. It was shown that the Position on the base plate has a great impact on the amount of RS in the part. The micromechanical behavior of LPBF Ti-6Al-4V was also studied using in-situ Synchrotron X-ray diffraction during tensile and compression tests. Diffraction elastic constants (DEC), connecting macroscopic stress and (micro) strain, of the LPBF Ti-6Al-4V showed a difference from the DEC of conventionally manufactured alloy. This fact was attributed to the peculiar microstructure and crystallographic texture. It was therefore recommended to determine experimentally DECs whenever possible. Low Cycle Fatigue (LCF) tests at a chosen operating temperature were performed to evaluate the effect of post-treatment on the mechanical performance. Through the information on the microstructure, the mesostructure, and the RS, the LCF behavior was (indirectly) correlated to the process parameters. It was found that the fatigue performance of LPBF samples subjected to hot isostatic pressing is similar to that of hot-formed Ti-6Al-4V. The tensile RS found at the surface of LPBF as-built samples decreased the fatigue life compared to the heat-treated samples. The modification of the microstructure (by heat treatment) did not affect the Fatigue performance in the elastic regime. This shows that in the absence of tensile RS, the manufacturing defects solely control the failure of LPBF components and densification has the strongest effect on the improvement of the mechanical performance. KW - Additive manufacturing KW - Ti-6Al-4V KW - Residual stress KW - Computed tomography PY - 2021 SP - 1 EP - 143 CY - RWTH Aachen AN - OPUS4-54389 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bruno, Giovanni A1 - Laquai, René A1 - Wieder, Frank A1 - Kupsch, Andreas A1 - Müller, Bernd R. T1 - The combined use of X-ray refraction and transmission radiography and computed tomography N2 - Alternative to conventional transmission-based radiography and computed tomography, X-ray refraction techniques are being increasingly used to detect damage in light materials. In fact, their range of application has been recently extended even to metals. The big advantage of X-ray refraction techniques is that they are able to detect nanometric defects, whose size would lie below the resolution of even state-of-the-art synchrotron-based X-ray computed tomography (SXCT). The superiority of synchrotron X-ray refraction radiography and tomography (SXRR and SXRCT) has been shown in the case of light materials, in particular composites. X-ray refraction techniques also yield a quantitifaction of the amount of damage (the so-called relative internal specific surface) and can well be compared with damage models. At the same time, it is impossible for SXRR and SXRCT to image single defects. We show that the combination of refraction- and transmission-based imaging techniques yields an impressive amount of additional information about the type and amount of defects in microstructured materials such as additively manufactured metals or metal matrix composites. We also show that the use of data fusion techniques allows the classification of defects in statistically significant representative volume elements. T2 - 11th Conference on Industrial Computed Tomography CY - Online meeting DA - 08.02.2022 KW - X-ray refraction radiography KW - Computed Tomography KW - Synchrotron radiation KW - Additive manufacturing KW - Damage evolution PY - 2022 UR - https://www.ndt.net/article/ctc2022/papers/ICT2022_paper_id268.pdf SP - 1 EP - 7 AN - OPUS4-54324 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thiede, Tobias A1 - Cabeza, Sandra A1 - Mishurova, Tatiana A1 - Nadammal, Naresh A1 - Kromm, Arne A1 - Bode, Johannes A1 - Haberland, C. A1 - Bruno, Giovanni T1 - An assessment of bulk residual stress in selective laser melted Inconel 718 N2 - Additive Manufacturing (AM) of metals has become industrially viable for a large variety of applications, including aerospace, automotive and medicine. Powder bed techniques such as Selective Laser Melting (SLM) based on layer-by-layer deposition and laser melt enable numerous degrees of freedom for the geometrical design. Developing during the manufacturing process, residual stresses may limit the application of SLM parts by reducing the load bearing capacity as well as induce unwanted distortion depending on the boundary conditions specified in manufacturing. The residual stress distribution in the bulk of IN718 elongated prisms produced by SLM was studied non-destructively by means of neutron diffraction. The samples with different scanning strategies, i.e. hatching length, were measured in as-build condition (on a build plate) and after removal from the build plate. The absolute values of all stress components decreased after removal from the build plate. Together with surface scan utilizing a coordinate-measuring machine (CMM), it is possible to link the stress release to the sample distortion. Obtained results indicated different residual stress states for each of the transversal, longitudinal and normal component depending on the thermal gradient in the respective direction. T2 - ECNDT 2018 CY - Göteborg, Sweden DA - 11.06.2018 KW - Residual stress KW - Selective laser melting KW - Neutron diffraction KW - IN718 PY - 2018 UR - http://cdn.ecndt2018.com/wp-content/uploads/2018/05/ecndt-0315-2018-File001.pdf SP - 1 AN - OPUS4-45325 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Laquai, René T1 - Extending synchrotron X-ray refraction imaging techniques to the quantitative analysis of metallic materials N2 - In this work, two X-ray refraction based imaging methods, namely, synchrotron X-ray refraction radiography (SXRR) and synchrotron X-ray refraction computed tomography (SXRCT), are applied to analyze quantitatively cracks and porosity in metallic materials. SXRR and SXRCT make use of the refraction of X-rays at inner surfaces of the material, e.g., the surfaces of cracks and pores, for image contrast. Both methods are, therefore, sensitive to smaller defects than their absorption based counterparts X-ray radiography and computed tomography. They can detect defects of nanometric size. So far the methods have been applied to the analysis of ceramic materials and fiber reinforced plastics. The analysis of metallic materials requires higher photon energies to achieve sufficient X-ray transmission due to their higher density. This causes smaller refraction angles and, thus, lower image contrast because the refraction index depends on the photon energy. Here, for the first time, a conclusive study is presented exploring the possibility to apply SXRR and SXRCT to metallic materials. It is shown that both methods can be optimized to overcome the reduced contrast due to smaller refraction angles. Hence, the only remaining limitation is the achievable X-ray Transmission which is common to all X-ray imaging methods. Further, a model for the quantitative analysis of the inner surfaces is presented and verified. For this purpose four case studies are conducted each posing a specific challenge to the imaging task. Case study A investigates cracks in a coupon taken from an aluminum weld seam. This case study primarily serves to verify the model for quantitative analysis and prove the sensitivity to sub-resolution features. In case study B, the damage evolution in an aluminum-based particle reinforced metal-matrix composite is analyzed. Here, the accuracy and repeatability of subsequent SXRR measurements is investigated showing that measurement errors of less than 3% can be achieved. Further, case study B marks the fist application of SXRR in combination with in-situ tensile loading. Case study C is out of the highly topical field of additive manufacturing. Here, porosity in additively manufactured Ti-Al6-V4 is analyzed with a special interest in the pore morphology. A classification scheme based on SXRR measurements is devised which allows to distinguish binding defects from keyhole pores even if the defects cannot be spatially resolved. In case study D, SXRCT is applied to the analysis of hydrogen assisted cracking in steel. Due to the high X-ray attenuation of steel a comparatively high photonenergy of 50 keV is required here. This causes increased noise and lower contrast in the data compared to the other case studies. However, despite the lower data quality a quantitative analysis of the occurance of cracks in dependence of hydrogen content and applied mechanical load is possible. N2 - In der vorliegenden Arbeit werden die zwei, auf Refraktion basierende, Röntgenbildgebungsverfahren Synchrotron Röntgen-Refraktions Radiographie (engl.: SXRR) und Synchrotron Röntgen-Refraktions Computertomographie (engl.: SXRCT) für die quantitative Analyse von Rissen und Porosität in metallischenWerkstoffen angewandt. SXRR und SXRCT nutzen die Refraktion von Röntgenstrahlen an inneren Oberflächen des Materials, z.B. die Oberflächen von Rissen und Poren, zur Bildgebung. Beide Methoden sind daher empfindlich gegenüber kleineren Defekten als ihre auf Röntgenabsorption basierenden Gegenstücke, Röntgenradiographie und Röntgen-Computertomographie. Sie sind in der Lage Defekte von nanometrischer Größe zu detektieren. Bislang wurden die Methoden für die Analyse von keramischen Werkstoffen und faserverstärkten Kunststoffen eingesetzt. Die Analyse von metallischenWerkstoffen benötigt höhere Photonenenergien benötigt werden um eine ausreichende Transmission zu erreichen. Dies hat kleinere Refraktionswinkel, und damit geringeren Bildkontrast, zur Folge, da der Brechungsindex von der Photonenenergie abhängt. Hier wird erstmals eine umfassende Studie vorgelegt, welche die Möglichkeiten zur Untersuchung metallischer Werkstoffe mittels SXRR und SXRCT untersucht. Es wird gezeigt, dass der geringere Kontrast, verursacht durch die kleineren Refraktionswinkel, überwunden werden kann. Somit ist die einzig verbleibende Beschränkung die erreichbare Transmission, die alle Röntgenbildgebungsverfahren gemeinsam haben. Darüber hinaus wird ein Modell für die quantitative Auswertung der inneren Oberflächen präsentiert und verifiziert. Zu diesem Zweck werden vier Fallstudien durchgeführt, wobei jede eine spezifische Herausforderung darstellt. In Fallstudie A werden Risse in einer Probe aus einer Aluminiumschweißnaht untersucht. Diese Fallstudie dient hauptsächlich dazu das Modell für die quantitative Analyse zu verifizieren und die Empfindlichkeit gegenüber Strukturen unterhalb des Auflösungsvermögens zu beweisen. In Fallstudie B wird die Entwicklung der Schädigung in einem aluminiumbasierten partikelverstärktem Metall-Matrix Komposit untersucht. Dabei wird die Genauigkeit und Wiederholbarkeit der SXRR Messungen analysiert und es wird gezeigt das Messfehler kleiner 3% erreicht werden können. Darüber hinaus wird in Fallstudie B erstmals SXRR in Kombination mit in-situ Zugbelastung eingesetzt. Fallstudie C ist aus dem hochaktuellen Bereich der additive Fertigung. Hier wird Porosität in additiv gefertigtem Ti-Al6-V4 analysiert mit besonderem Augenmerk auf der Morphologie der Poren. Es wurde ein Verfahren zur Klassifizierung, basierend auf SXRR Messungen, erfunden, welches Bindefehler und Poren voneinander unterscheiden kann auch wenn die Defekte nicht räumlich aufgelöst werden können. In Fallstudie D wird SXRCT zur Analyse von wasserstoffunterstützter Rissbildung in Stahl angewandt. Wegen der hohen Röntgenschwächung des Stahls muss hier mit 50 keV eine vergleichsweise hohe Photonenenergie genutzt werden. Dadurch zeigen die Daten ein erhöhtes Rauschen und geringeren Kontrast verglichen mit den anderen Fallstudien. Allerdings ist es, trotz der geringeren Datenqualität, möglich das Auftreten von Rissen in Abhängigkeit der Wasserstoffkonzentration und mechanischen Belastung zu untersuchen. KW - Synchrotron X-ray refraction computed tomography KW - Lean duplex steel X2CrMnNiN21-5-1 KW - hydrogen embrittlement KW - Metal-matrix composite KW - Al6061 KW - Ti-Al6-V4 KW - In-situ tensile test PY - 2022 SP - 1 EP - 71 AN - OPUS4-54385 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Winkelmann, A. A1 - Britton, T. B. A1 - Nolze, Gert T1 - EBSD Kikuchi Pattern Analysis, Silicon 15kV N2 - Supplementary data and images for Si EBSD pattern analysis as presented in: A. Winkelmann, T.B. Britton, G. Nolze "Constraints on the effective electron energy spectrum in backscatter Kikuchi diffraction", Physical Review B (2019). KW - EBSD KW - Electron energy KW - Energy distribution KW - Kikuchi pattern KW - Simulation PY - 2019 DO - https://doi.org/10.5281/zenodo.2565061 PB - Zenodo CY - Geneva AN - OPUS4-51907 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Illemann, J. A1 - Meinel, Dietmar A1 - Bellon, Carsten T1 - Effektive Bestimmung der Fokusparameter von Mikrofokus-Röntgenquellen N2 - Mikrofokus-Röntgenquellen werden in der industriellen CT flexibelverwendet, um mit kleiner Leistung hohe Auflösung zu erzielen oder mit verminderter Auflösung bei höherer Leistung kürzere Messzeiten zu erreichen. Insbesondere Quellen in offener Bauweise benötigen Wartung wie Filamentwechsel und Nachstellen der Fokusparameter. Ziel ist es, einen optimal kleinen Quellfleck bei bekannter Spannung einzustellen und dessen Größe zu bestimmen. Zur Überprüfung der Quellfleckgröße sind bereits Verfahren unter Verwendung lithographisch hergestellter Masken mit Strichmustern oder Siemenssternen aus Mikrometer dünnen Schichten aus stark absorbierendem Material wie z.B. Gold bekannt. Diese erfordern wegen der geringen Absorption eine lange Messzeit und sind nur kostenintensiv herzustellen. Ihre Verwendung zur regelmäßigen Qualitätsüberprüfung von CT-Anlagen ist daher nicht verbreitet. Ziel dieser Arbeit ist es, die richtungsabhängige Quellfleckgröße absolut zu bestimmen, wobei nur einfach zu beschaffende Wolframspitzen verwendet werden. Dazu werden radiographische Bilder in hoher Vergrößerung aufgenommen und die Grauwertverteilung parametrisiert. Unter Verwendung der Kenntnis von Targetmaterial und Spannung wird eine eineindeutige Zuordnung zur Quellfleckgröße vorgenommen. Dieses erfordert eine extensive Simulation für verschiedene Spannungen, Fokusgrößen und andere Einflussgrößen, sowie die experimentelle Verifikation an verschiedenen CT-Anlagen im Vergleich zu einer bekannten Methode. Erste Ergebnisse werden vorgestellt und die praktische Implementierung unter Angabe der Einschränkungen der Verwendbarkeit diskutiert. Die Autoren hoffen, damit einen wesentlichen Beitrag zur Verbesserung der Qualitätssicherung und zur Arbeitseffizienz in der Mikrocomputertomographie leisten zu können. T2 - DGZfP DACH-Jahrestagung 2019 CY - Friedrichshafen, Germany DA - 27.05.2019 KW - Mikro-Computertomographie KW - Röntgenröhre KW - Quellfleckgröße KW - Brennfleck PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-485960 UR - https://www.ndt.net/search/docs.php3?id=24551 UR - https://www.ndt.net/article/dgzfp2019/papers/Mi.2.A.3.pdf IS - NDT.net Issue: 2019-08 SP - 1 EP - 13 AN - OPUS4-48596 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Z., Zhang A1 - Ewert, Uwe A1 - Barrett, T. D. A1 - Bond, L. J. T1 - Paper Watermark Imaging using Electron and Low Energy X-ray Radiography N2 - Historians and librarians are interested in watermarks and mould surface patterns in historic papers, because they represent the “fingerprints” of antique papers. However, these features are usually covered or hidden by printing, writing or other media. Different techniques have been developed to extract the watermarks in the paper while avoiding interference from media on the paper. Beta radiography provides good results, but this method cannot be widely used because of radiation safety regulations and the long exposure times required due to weak isotope sources employed. In this work, two promising methods are compared which can be used to extract digital high-resolution images for paper watermarks and these are electron radiography and low energy X-ray radiography. For electron radiography a “sandwich” of a lead sheet, the paper object, and a film in a dark cassette, is formed and it is exposed at higher X-ray potentials (> 300 kV). The photoelectrons escaping from the lead sheet penetrate the paper and expose the film. After development, the film captures the watermark and mould surface pattern Images for the paper being investigated. These images are then digitized using an X-ray film digitizer. The film employed could potentially be replaced by a special type of imaging plate with a very thin protection layer to directly generate digital Images using computed radiography (CR). For the second method, a low energy X-ray source is used with the specimen paper placed on a digital detector array (DDA). This method directly generates a low energy digital radiography (DR) image. Both methods provide high quality images without interference from the printing media, and provide the potential to generate a “fingerprint” database for historical papers. There were nevertheless found to be differences in the images obtained using the two methods. The second method, using a low energy X-ray source, has the potential to be integrated in a portable device with a small footprint incorporating user safety requirements. Differences obtained using the two methods are shown and discussed. T2 - 45th Annual Conference on Review of Progress in Quantitative Nondestructive Evaluation (QNDE) CY - Burlington, VT, USA DA - 15.07.2018 KW - X-ray Radiography KW - Paper watermark PY - 2019 SN - 978-0-7354-1832-5 DO - https://doi.org/10.1063/1.5099750 SN - 0094-243X VL - 2102 IS - 1 SP - 030004-1 EP - 030004-9 PB - American Institute of Physics AN - OPUS4-49922 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beck, Uwe A1 - Griepentrog, Michael A1 - Hertwig, Andreas A1 - Hielscher, Stefan A1 - Weise, Matthias T1 - Auf dem Weg zu Industrie 4.0: Bestimmung von Messunsicherheitsbudgets in der Oberflächentechnik N2 - Vorgestellt wurde die Bestimmung von Messunsicherheitsbudgets für sehr unterschiedliche physikalische Größen, die in der Oberflächentechnik von hoher Relevanz sind: Stufenhöhe h, Schichtdicke d, Eindringhärte HIT und Haftfestigkeit. Die Unterschiede betreffen die Art der Prüfmethodik (optisch zerstörungsfrei vs. mechanisch invasiv/zerstörend), die laterale Größe des Integrationsgebietes der Messung (lokal: nano bis sub-mikro vs. global: mikro bis makro) und die Art der Bestimmung von Messunsicherheitsbudgets (physikalische Größen: direkt rückführbar; Werkstoffkenngröße: genormt; Systemkenngröße: genormt). Im Rahmen von Industrie 4.0 werden ausgehend der geforderten Spezifikation des beschichteten Produkts (Mittelwert mit Vertrauensbereich oder Mindestwert) durchgehende Toleranzbänder zur Oberflächenmodifizierung/Beschichtung des Substrats, einhergehend mit Prozessfenstern, die diese Toleranzbänder garantieren, erforderlich, die zuverlässig erfasst werden müssen. Die Frage der anzuwendenden Mess- und Prüftechnik und die damit notwendige Betrachtung von Messunsicherheitsbudgets ist für die Digitalisierung von Konditionierungs-, Zustands-, Regel- und Steuergrößen unverzichtbar. Mit Blick auf die Einhaltung von Prozessfenstern und die dafür notwendige Prozessführung wird technologisches Kern-Know-how digitalisiert, das es unbedingt zu schützen gilt. Nur lokale Netze können diese Sicherheit garantieren, in globalen Netzen ist die Datensicherheit bestenfalls maximierbar T2 - 14. ThGOT Thementage Grenz- und Oberflächentechnik und 6. Kolloquium Dünne Schichten in der Optik CY - Zeulenroda, Germany DA - 12.03.2019 KW - Oberflächentechnik KW - Messunsicherheit KW - Messtechnik KW - Prüftechnik KW - Haftfestigkeit PY - 2019 SN - 978-3-00-058187-8 VL - 2019 SP - 1 EP - 10 AN - OPUS4-47670 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Vössing, Konrad A1 - Gaal, Mate A1 - Niederleithinger, Ernst T1 - Air-coupled ferroelectret ultrasonic transducers for nondestructive testing of wood in through transmission and reflection mode N2 - The necessity and demand for nondestructive testing of wood-based materials which can automatically scan huge areas of wood is increasing. Air-coupled ultrasound (ACU) is used to detect defects and damage without altering the structure permanently. Using through transmission it is possible to detect even small holes and missing adhesive. If only one side of an object is accessible the reflection mode is preferred at the expense of a reduced resolution and penetration depth. Novel ferroelectret transducers with a high signal-to-noise ratio (SNR) enable a high-precision structure recognition. The transducers made of cellular polypropylene (PP) are quite suitable for ACU testing due to their extremely low Young’s modulus and low density which result in a favorable acoustic impedance for the transmission of ultrasonic waves between the transducer and air. Thus, defects such as delamination, rot, and cracks can be detected. Promising results were obtained under laboratory conditions with frequencies from 90 kHz to 200 kHz. The advantage of these ACU transducers is that they do not require contact to the sample, are accurate, and cost effective. Ultrasonic quality assurance for Wood is an important attempt to increase the acceptance of wooden structures and towards sustainability in civil engineering in general. T2 - International Conference on Sustainable Materials, Systems and Structures CY - Rovinj, Croatia DA - 20.03.2019 KW - Air-coupled ultrasound KW - Cellular polypropylene KW - Wood KW - Nondestructive Testing KW - Defect detection PY - 2019 SP - 28 EP - 33 AN - OPUS4-47682 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bente, Klaas A1 - Oeff, Julius A1 - Gaal, Mate T1 - Quantitative, zeiteffiziente, winkel- und frequenzaufgelöste Analyse von Elektretwandlern im Hör- und Ultraschallbereich N2 - Die Bildgebung oder Analyse von Materialien mittels luftgekoppelten Ultraschalls profitiert von einer hohen Geschwindigkeit, Flexibilität und Materialschonung des assoziierten Verfahrens. Die Luftankopplung hat jedoch den wesentlichen Nachteil, dass die auftretenden Impedanzsprünge an Grenzflächen zu enormen Verlusten in den Signalamplituden führen. Ultraschallwandler, die laut genug senden und sensitiv genug empfangen, um die geringen Signalamplituden noch auswerten zu können, sind somit zentraler Gegenstand der aktuellen Forschung und Entwicklung. Vielversprechende Wandlertypen sind piezokeramische Wandler, Elektretwandler, aber auch passive, breitbandige Ultraschallempfänger, wie optische Mikrophone. Die quantitative Charakterisierung der Sensitivitäten solcher Wandler wird oft vernachlässigt, da kein simples, universelles Verfahren zur Verfügung steht. In diesem Beitrag geht es um die Methodik der Charakterisierung von Luftultraschallwandlern mittels thermoakustischer Ultraschallsender. Thermoakustische Wandler erzeugen Ultraschall durch das schnelle heizen eines finiten Volumens an Luft vor dem Wandler. Die erhöhte interne Energie führt zu einer Druckänderung, welche sich als akustische Welle fortpflanzen kann. Da keine mechanische Volumenarbeit vom Wandler erbracht wird, funktioniert das Verfahren resonanzfrei. Die Charakterisierung wird am Beispiel von Elektretwandlern durchgeführt. Elektretwandler sind sensitive und immer verschleißresistentere Schallwandler, wodurch sie verbreitet Einsatz im Hör- und Ultraschallbereich finden. Geladene, zelluläre Polypropylen-Folien eignen sich besonders gut als Wandlermaterial aufgrund ihrer, verglichen mit Piezokompositen, hundertfach niedrigeren akustischen Impedanz bei gleichem piezoelektrischem Koeffizienten. Doch das winkel- und frequenzabhängige Verhalten der Wandler ist kaum untersucht und wenig quantifiziert. Es wird gezeigt, dass diese Folien eine schichtdickenabhängige Sensitivität in Größenordnungen zwischen 0.1 mV/Pa und 10 mV/Pa aufwiesen. Ein Maximum in der Sensitivität fand sich nahe ihrer mechanischen Resonanzfrequenz im Ultraschallbereich, aber auch im niederfrequenten Hörschallbereich. Darüber hinaus konnte die Winkelabhängigkeit der Sensitivität charakterisiert werden. Die Analyse konnte dabei zeiteffizient gestaltet werden, da pro Winkel eine Messung für die Berechnung der Übertragungsfunktion des Wandlers genügte. Quantifiziert wurden die Ergebnisse durch das einmalige Vermessen des Emitters mittels Laser-Doppler-Vibrometrie (LDV). Mit den erzielten Ergebnissen wurde zum einen das komplexe Sensitivitätsverhalten der Wandler untersucht, aber auch eine grundlegende Methodik aufgezeigt, wie Wandler quantitativ, multivariat charakterisiert werden können. Winkel- und frequenzaufgelöste Sensitivitäten erlauben zum einen die Analyse der Anwendbarkeit der Wandler für sämtliche Einsatzgebiete, zum anderen stehen so Rückschlüsse über die mechanische Dynamik von Elektretfolien in Aussicht, da deren Sensitivität direkt mit ihrem Elastizitätsmodul skaliert. T2 - DAGA 2019 CY - Rostock, Germany DA - 18.03.2019 KW - Luftultraschall KW - Ultraschall KW - Elektretwandler KW - Thermoakustik KW - Wandlercharakterisierung PY - 2019 SP - 748 AN - OPUS4-47712 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Osterloh, Kurt A1 - Röhrs, S. A1 - Schwabe, A. A1 - Radujcovic, S. A1 - Bücherl, T. A1 - Dangendorf, V. A1 - Zscherpel, Uwe A1 - Reiche, I. A1 - Nüsser, A. ED - Zscherpel, Uwe ED - Kasperl, S. T1 - Elucidating the distribution of organic consolidants in wood by Neutron Tomography N2 - While the absorption of X-rays and gamma radiation is determined by the Z-number of the elements a specimen is composed of, it is the hydrogen making an effective contrast with neutron imaging. As a consequence, interrogating with neutrons presents a suitable tool to study the distribution of organic consolidants in materials such as wood as encountered in impregnated wooden artworks. Four different examples of objects are presented here to demonstrate the potential of neutron CT: 1) small wooden pieces of ship wrecks (< 2 cm thickness) interrogated with cold neutrons (0.5 meV at the ANTARES facility of the FRM II in Garching) to demonstrate the potential and the limitation of using low energy neutrons, 2) a wooden statue soaked with carbolineum (fission neutrons 1.8 MeV at the NECTAR facility of the FRM II), 3) a smaller wooden figure of a skull heavily soaked with carbolineum so it was too tight for the fission neutrons used before with accelerator neutrons (broad range about 5.5 MeV at the PTB in Braunschweig) and 4) pieces of charred wood to study the impregnation with a consolidant (NECTAR, FRM II). With the exception of the last example, all results have been combined with X-ray tomography (BAM 8.3 in Berlin). In the case of the charred wood specimens (example 4) the density histograms of the neutron tomography results were compared with those obtained from untreated references. The observed gain in specific density of the soaked specimens corresponded with an increase of specific weight. All results obtained so far showed distinct distribution patterns attributable to structural peculiarities or organic consolidants providing valuable support for subsequent restoration works. T2 - International symposium on digital industrial radiography and computed tomography DIR2019 CY - Fürth, Germany DA - 02.07.2019 KW - Neutron Imaging KW - Cold to fast neutron testing KW - Tomography of wood samples KW - Art restauration PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-505326 UR - https://www.ndt.net/search/docs.php3?id=24740 SN - 1435-4934 VL - 24 IS - 11 SP - 1 EP - 8 PB - NDT.net CY - Kirchwald AN - OPUS4-50532 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zscherpel, Uwe A1 - Ewert, Uwe T1 - Aktuelle Entwicklungen in der Standardisierung N2 - In den letzten zwei Jahren wurden 11 neue Standards/Standardrevisionen zur RT veröffentlicht (ohne Strahlenschutz) und 5 werden dafür gestrichen. Es wird über die neuen Anforderungen ausgewählter Normen bzw. Normrevisionen informiert und insbesondere auch über die veränderten Parameter, die bei Prüfpraxis und bei der Klassifizierung zu berücksichtigen sind. Das wichtigste Projekt ist die Revision der DIN EN ISO 17636-1, -2, RT von Schweißverbindungen, in ISO TC 44 SC 5 WG 1. Die Standards zur Schweißnahtprüfung in der Kerntechnik, DIN 25435, wurden ins Englische übertragen und bei ISO TC 85 SC 6 bearbeitet. Hauptaktivität bei ASTM ist gegenwärtig die Überarbeitung der CT-Standards und die Berücksichtigung der Anforderungen an das dimensionelle Messen. Der Guide ASTM E 1441 zur Bestimmung von MTF, Kontrast-Detail-Funktion (CDF) und Kontrast-Diskrimination-Diagramm (CDD) wird revidiert. E 2445 zur CR Long Term Stability wird ebenfalls revidiert. Die Revision soll auch in die ISO 16371-1 eingehen. Dazu ist ein Round Robin-Test geplant. Auch die Standards zur Durchstrahlungsprüfung auf Korrosion und Ablagerungen in Rohren mit Röntgen- und Gammastrahlen (EN 16407-1, -2, 2014) wurden revidiert. Diese Revision wurde als DIN EN ISO 20769-1, -2 2018 veröffentlicht und EN 16407 wird zurückgezogen. Die Revision der Standards EN 12543 und EN 12679 zur Messung der Brennfleckgröße und der Strahlergröße ist mit Verzögerung in Überarbeitung, um die digitalen Detektoren und Messmöglichkeiten mit Bildverarbeitungsprogrammen zu berücksichtigen. Ein Entwurf zur Messung der Brennfleckgröße von nano-Fokusröhren wird derzeit vom Europäischen Metrologie-Programm EMPIR gefördert. Zur radiographischen Gussteilprüfung wurde der Standard EN 12681 revidiert und 2018 veröffentlicht. Er wurde um Zulässigkeitsgrenzen erweitert und die digitale Radiographie wurde in Teil 2 berücksichtigt. T2 - 17. Seminar der DGZfP "Aktuelle Fragen der Durchstrahlungsprüfung und des Strahlenschutzes" CY - Kassel, Germany DA - 28.03.2019 KW - Digitale Radiographie KW - Standards KW - Bildqualität KW - Klassifizierung PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-505371 UR - https://www.ndt.net/search/docs.php3?id=24807 VL - 24 IS - 12 SP - 1 EP - 5 PB - NDT.net CY - Kirchwald AN - OPUS4-50537 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Luco Colilles, Arnau T1 - Evaluation of two compact near-infrared spectrometers for the detection of microplastics in soil samples N2 - In the last years, the Process Analytical Technology (PAT) research field has become of great importance due to its connection with the industrial world. This industry related research, along with the evolutionary progress that technology has seen lately, has allowed that key analytical techniques in an industrial environment have undergone a radical development. One of these techniques has been the near-infrared spectroscopy (NIRS). This technique, currently common in "online" industrial analysis, has seen a remarkable revolution, especially since the introduction of the microelectromechanical systems technology (MEMS) in the spectroscopy field. Nowadays it is possible to find compact spectrometers no bigger than a wristwatch in the market. Although there is an unavoidable question: can these compact spectrometers actually compete against the traditional spectrometers? In this project different calibration parameters of two compact NIR spectrometers ("Spectral Engines Oy NIR-One Sensor NM2.0", with 1550 to 1950 nm range; and "NeoSpectra Si-ware", with 1300 to 2550 nm range) were evaluated, and the obtained results were compared with a reference spectrometer ("Bruker Optik GmbH Matrix-F", with 15000 to 4000 cm–1 range). In order to obtain the different calibration parameters, a sequence of quality performance tests were conducted. The results obtained after the different experiments carried out with both compact spectrometers prove that their performance is more than acceptable for routine analysis. Afterward, model samples of different microplastics in soil at different known concentration were analyzed with all three spectrometers. Chemometric models capable to identify and classify microplastics in soil were established. For this analysis five of the most used plastics worldwide were used: polyethylene (PE), polyethylene terephthalate (PET), polypropylene (PP), polystyrene (PS), and polyvinyl chloride (PVC). After the Principal component analysis (PCA), it can be seen that only the NIR-One NM2.0 is capable to differentiate all types of microplastics in soil at concentrations of 1–2 %, while the NeoSpectra Si-ware is unable to identify the PET sample. KW - Near-infrared KW - Microplastics KW - Compact spectrometers PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-511626 UR - http://hdl.handle.net/2445/138198 SP - 1 EP - 29 PB - Universitat de Barcelona CY - Barcelona AN - OPUS4-51162 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ahmadi, Samim A1 - Thiel, Erik A1 - Karagianni, Christina A1 - Hirsch, Philipp Daniel A1 - Burgholzer, P. A1 - Mayr, G. A1 - Jung, P. A1 - Caire, G. A1 - Ziegler, Mathias T1 - Photothermal super resolution image reconstruction using structured 1D laser illumination N2 - The separation of two closely spaced defects in fields of Thermographic NDE is very challenging. The diffusive nature of thermal waves leads to a fundamental limitation in spatial resolution. Therefore, super resolution image reconstruction can be used. A new concerted ansatz based on spatially structured heating and joint sparsity of the signal ensemble allows for an improved reconstruction of closely spaced defects. This new technique has been studied using a 1D laser array with randomly chosen illumination pattern. This paper presents the results after applying super resolution algorithms, such as the iterative joint sparsity (IJOSP) algorithm, to our processed measurement data. Different data processing techniques before applying the IJOSP algorithm as well as the influence of regularization parameters in the data processing techniques are discussed. Moreover, the degradation of super resolution reconstruction goodness by the choice of experimental parameters such as laser line width or number of measurements is shown. The application of the super resolution results in a spatial resolution enhancement of approximately a factor of four which leads to a better separation of two closely spaced defects. T2 - Quantitative Nondestructive Evaluation Conference 2019 CY - Portland, OR, USA DA - 14.07.2019 KW - Super resolution KW - Photothermal KW - Thermography KW - Laser PY - 2019 SP - Paper 8593, 1 PB - ASME AN - OPUS4-50924 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Kowarik, Stefan A1 - Pithan, L. T1 - kowarik-labs/AI-reflectivity: v0.1 N2 - AI-reflectivity is a code based on artificial neural networks trained with simulated reflectivity data that quickly predicts film parameters from experimental X-ray reflectivity curves. This project has a common root with (ML-reflectivity)[https://github.com/schreiber-lab/ML-reflectivity] and evolved in parallel. Both are linked to the following publication: Fast Fitting of Reflectivity Data of Growing Thin Films Using Neural Networks A. Greco, V. Starostin, C. Karapanagiotis, A. Hinderhofer, A. Gerlach, L. Pithan, S. Liehr, F. Schreiber, S. Kowarik (2019). J. Appl. Cryst. For an online live demonstration using a pre-trained network have a look at github. KW - Artificial neural networks KW - X-ray reflectivity PY - 2019 DO - https://doi.org/10.5281/zenodo.3477583 PB - Zenodo CY - Geneva AN - OPUS4-51888 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Lisec, Jan T1 - CorrectOverloadedPeaks (R package to correct APCI-HR-MS peak data) N2 - Metabolomics, the analysis of potentially all small molecules within a biological system, has become a valuable tool for biomarker identification and the elucidation of biological processes. While metabolites are often present in complex mixtures at extremely different concentrations, the dynamic range of available analytical methods to capture this variance is generally limited. Here, we show that gas chromatography coupled to atmospheric pressure chemical ionization mass spectrometry (GC-APCI-MS), a state of the art analytical technology applied in metabolomics analyses, shows an average linear range (LR) of 2.39 orders of magnitude for a set of 62 metabolites from a representative compound mixture. We further developed a computational tool to extend this dynamic range on average by more than 1 order of magnitude, demonstrated with a dilution series of the compound mixture, using robust and automatic reconstruction of intensity values exceeding the detection limit. The tool is freely available as an R package (CorrectOverloadedPeaks) from CRAN (https://cran.r-project.org/) and can be incorporated in a metabolomics data processing pipeline facilitating large screening assays. KW - Software KW - Metabolomics KW - R package KW - Data processing PY - 2019 UR - https://github.com/cran/CorrectOverloadedPeaks/ PB - GitHub CY - San Francisco, CA, USA AN - OPUS4-57853 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hertwig, Andreas T1 - A multi-method study of femtosecond laser modification and ablation of amorphous hydrogenated carbon coatings N2 - We report here the optical constants of ECR (MW) and RF generated a-C:H layers before and after laser irradiation. The work is described in the following publication: https://doi.org/10.1007/s00339-024-07980-z The data uploaded are the optical constants (n and k) of the a-C:H layers before (base) and after (ROIx) laser irradiation. Please see the article for the nomenclature of the data and for the methods applied ot produce the layers, laser shots, and OK data. KW - Spectroscopic ellipsometry KW - Amorphous hydrogenated carbon layers KW - Laser materials processing KW - Correlative imaging spectroscopy PY - 2024 DO - https://doi.org/10.5281/zenodo.13928596 PB - Zenodo CY - Geneva AN - OPUS4-61855 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kömmling, Anja A1 - Jaunich, Matthias A1 - Wolff, Dietmar T1 - Influence of Ageing on Sealability of HNBR, EPDM and FKM O-rings N2 - At BAM, which is the federal institute for materials research and testing in Germany, it is one of our tasks to evaluate the safety of casks designed for transport and/or storage of radioactive material. This includes assessment of elastomeric seals applied in the containers. Besides examining the low-temperature behaviour and irradiation effects of elastomeric seals, it is our goal to evaluate the service lifetime of the seals with regard to the requirements for long-term safety (40 years and more) of the containers. Therefore, we started an accelerated ageing programme with selected rubbers often used for seals (HNBR, EPDM and FKM) which are aged at four different temperatures (75 °C, 100 °C, 125 °C and 150 °C) up to 1 year. In order to assess sealability, O-rings are aged in compression by 25 % (corresponding to the compression during service) between plates as well as in flanges that allow leakage rate measurements. For comparison, uncompressed O-rings are aged as well. Further methods characterising seal performance are compression stress relaxation (CSR) reflecting the loss of sealing force of a compressed seal over time, and compression set (CS) which represents the recovery behaviour of a seal after release from compression. Additionally, hardness is measured for information about the change of mechanical properties. The experimental results indicate that while hardness, CSR and CS show considerable degradation effects, the leakage rate stays constant or even decreases until shrinkage and the loss of resilience of the aged seal leads to the formation of a leakage path. This indicates that static leakage rate, which is the only available direct seal performance criterion, has only limited sensitivity for the degradation of the seal material. T2 - International Sealing Conference CY - Stuttgart, Germany DA - 12.10.2016 KW - Rubber KW - Seal KW - Degradation PY - 2016 SN - 978-3-8163-0674-9 VL - 2016 SP - 551 EP - 563 PB - VDMA AN - OPUS4-38014 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nadejde, C. A1 - Neamtu, Mariana A1 - Hodoroaba, Vasile-Dan A1 - Schneider, Rudolf A1 - Ababei, G. A1 - Panne, Ulrich T1 - Characterization and application of Green Fenton-like catalysts for the removal of water pollutants N2 - Three types of magnetite-chitosan/iron oxalate/iron citrate nanoparticles (NP) were evaluated as magnetic heterogeneous catalysts for water treatment. T2 - PTIM 2015, 1st International Caparica Conference on Pollutant Toxic Ions and Molecules CY - Caparica, Portugal DA - 02.112015 KW - Bisphenol A degradation KW - Nanocatalysts KW - Characterization KW - Fenton oxidation KW - Wastewater PY - 2015 SN - 978-989-99361-6-4 SP - 186 EP - 187 PB - Proteomass AN - OPUS4-40082 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rockenhäuser, Christian A1 - von Hartrott, P. A1 - Metzger, M. A1 - Skrotzki, Birgit T1 - Digital material representation of precipitation coarsening in alloy 2618A for the lifetime assessment of radial compressor wheels N2 - The concept of digital material representation is introduced and the aluminium alloy 2618A is discussed as an example of this concept regarding the simulation of material ageing based on nanoscaled precipitates. T2 - Microscopy Conference 2019 (MC2019) CY - Berlin, Germany DA - 01.09.2019 KW - Alloy 2618A KW - Aluminium KW - Digital material representation KW - Transmission electron microscopy KW - Material degradation PY - 2019 SP - 183 EP - 184 AN - OPUS4-48885 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Hodoroaba, Vasile-Dan A1 - Fontanges, R. A1 - Delvallée, A. A1 - Deumer, J. A1 - Salzmann, C. A1 - Crouzier, L. A1 - Gollwitzer, C. A1 - Klein, T. A1 - Koops, R. A1 - Sebaihi, N. A1 - Pauw, Brian Richard A1 - Smales, Glen Jacob A1 - Artous, S. A1 - Taché, O. A1 - Feltin, N. T1 - Report on full algorithm sequences for nanoparticle detection and size measurement as developed on both a physical basis and by machine learning N2 - he main objective of the nPSize project is to improve the measurement capabilities for nanoparticle size based on both measurement methods traceable to SI units and new reference materials. Two basic approaches have been used in order to develop measurement procedures resulting in traceable results of the nanoparticle size distribution: physical modelling for the methods used in the project (TSEM, SEM, AFM and SAXS) and machine learning. Physical modelling: In this part, the physical models associated with different shape measurements for the techniques TSEM, SEM, AFM and SAXS have been collected and further developed with the aim to simulate the resulting signal as measured by the individual methods. Uncertainties and traceability associated with each model were investigated and evaluated. In the following, the progress on these physical models is reported for each individual method. Machine Learning modelling: The aim of this part is to use machine learning to enable automatic measurement of nanoparticle shape from expert a-priori information only. No physical model will be used as a-priori information in this task. The accuracy and traceability of the size results obtained by each technique will be analyzed and compared with the physical modelling. A machine learning database will then be used to create automatic detection algorithms. KW - Nanoparticles KW - Particle size distribution KW - SEM KW - TSEM KW - TEM KW - SAXS KW - AFM PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-546531 DO - https://doi.org/10.5281/zenodo.5807864 SP - 1 EP - 20 PB - Zenodo CY - Geneva AN - OPUS4-54653 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rockenhäuser, Christian A1 - Schriever, Sina A1 - Skrotzki, Birgit ED - Panfilov, Peter ED - Kodzhaspirov, Georgii T1 - Microstructural evolution during creep of Al-alloy 2618A N2 - The aluminum alloy 2618A is an Al-Cu-Mg alloy with additions of Fe and Ni, which was designed for long-term operation at elevated temperature in transportation and aerospace industries. Typical applications include aircraft parts and structures (sheet material) or engine components such as turbo charger centrifugal compressor wheels (forged material). Such components are subjected to prolonged aging during service, (e.g. 50 000 h) at temperatures which are close to their age hardening temperature (ca. 190 °C). The microstructural evolution during creep exposure is studied. T2 - Creep 2017 CY - St. Petersburg, Russia DA - 19.07.2017 KW - Creep KW - Microstructure KW - Coarsening KW - TEM PY - 2017 SN - 978-5-7422-5799-8 SP - 80 EP - 81 PB - SpbPU Publisher CY - St. Petersburg, Russia AN - OPUS4-40750 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Mike A1 - Zaghdoudi, Maha A1 - Kömmling, Anja A1 - Jaunich, Matthias A1 - Wolff, Dietmar T1 - A numerical approach to correlate compression stress relaxation and compression set of elastomer O-rings with tightness N2 - The excellent mechanical properties of elastomer seals at a wide range of temperatures as well as their high versatility and recovery potential under several load conditions make these materials well suitable for the application in containers designed for transport and disposal of negligible heat generating radioactive waste. While a seal exchange at defined intervals is typical in many conventional applications, it is impossible or at least hard to perform when principles of minimization of radiation exposure have to be considered which prohibit an avoidable cask handling. An extensive knowledge of the change of the elastomer properties during aging and the availability of reliable end-of-lifetime criteria to guarantee the safe enclosure of the radioactive material for the required time are mandatory. As BAM is involved in most of the national cask licensing procedures and in the evaluation of cask-related long-term safety issues, great efforts have already been made and are still ongoing to scientifically support this task. Among other representative types of elastomers, specimen made from ethylene propylene diene rubber (EPDM) were tested before, during and after aging to capture the with respect to application most important of their complex mechanical properties. Exemplary results of these investigations were used to calibrate material models implemented in the commercial finite element software ABAQUS/Standard®. The finite element model already presented in previous works uses a sequential temperature displacement coupling. The calculated compression stress relaxation (CSR) and compression set (CS) values do satisfactorily match the experimental results. In many investigations performed at BAM both values (CSR and CS) were identified as key indicators of elastomer’s long-term performance. However, the possibility to correlate these equivalent indicators with performance values such as tightness and leakage rate, measurable in the mounted state, is an important goal of our future work. In the presented study the ABAQUS® feature of “pressure penetration” is introduced in the suggested finite element model for this purpose. It provides the possibility to simulate the penetration of a gas into a possible gap between flange and O-ring causing an opening of a leakage path. Three dimensional and axis-symmetric finite element models were generated to represent flat and grooved flanges of different dimensions. The sensitivity of the feature to several input parameters is investigated and the observed behavior of the O-ring is correlated with the results of performed leakage tests. T2 - ASME 2021 Pressure Vessels & Piping Conference (PVP2021) CY - Online meeting DA - 13.07.2021 KW - Elastomer KW - Tightness KW - Leakage KW - Compression set KW - Compression stress relaxation PY - 2021 SN - 978-0-7918-8535-2 DO - https://doi.org/10.1115/PVP2021-61976 SP - 1 EP - 8 PB - American Society of Mechanical Engineers (ASME) CY - New York, NY, USA AN - OPUS4-54422 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias A1 - Grelle, Tobias A1 - Wolff, Dietmar T1 - Low temperature properties of elastomer seals - Comparison between purely static and partially released seals - N2 - Rubber is widely used as sealing material in various applications. In many fields the function of seal materials at low temperatures is necessary. Therefore the understanding of failure mechanisms that lead to leakage at low temperatures is of high importance. It is known that the material properties of rubbers are strongly temperature dependent. At low temperatures this is caused by the rubber-glass transition (abbr. glass transition). During continuous cooling the material changes from rubber-like entropy-elastic behaviour to stiff energy-elastic behaviour, that allows nearly no strain or retraction, due to the glass transition. Hence rubbers are normally used above their glass transition but the minimum working temperature limit is not defined precisely, what can cause problems during application. Therefore the lower operation temperature limit of rubber seals should be determined in dependence of the material properties. In the past we investigated the material properties and sealing behaviour of elastomeric seals at low temperatures. Additionally we started to study the effect of a small partial release of elastomer seals at low temperatures. To study the influence of dynamic events on seal performance and to enhance the understanding of occurring seal failure, a setup for a fast partial seal release was designed. In this contribution we focus on the correlation of material properties and component behaviour under different application conditions. It is desired to widen the understanding of the process of seal failure at low temperature. T2 - 12. Kautschuk-Herbst-Kolloquium CY - Hannover, Germany DA - 22.11.2016 KW - Seal properties KW - Low temperature KW - Partial release KW - Leakage rate PY - 2016 SN - 9783981407648 SP - 34 AN - OPUS4-38501 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grun, Benthe Birger A1 - Skrotzki, Birgit A1 - Olbricht, Jürgen ED - Christ, Hans-Jürgen T1 - Charakterisierung von Hochtemperaturwerkstoffen durch Zug- und Ermüdungsversuche an Kleinproben T1 - Characterization of high-temperature materials by tensile and fatigue tests on small specimens N2 - Die Verwendung von miniaturisierten Probengeometrien in der mechanischen Prüfung ermöglicht die Entnahme des Probenmaterials direkt aus kritischen Bereichen wie Fügeverbindungen und ermöglicht die Prüfung von kleinen Bauteilen wie additiv gefertigten Strukturen. In der vorliegenden Arbeit werden exemplarisch die Ergebnisse von vergleichenden Zug- und niederzyklischen Schwing-versuchen (LCF) an dem austenitischen Stahl AISI 316L und der Nickelbasislegierung IN718 vorgestellt. Die Prüfergebnisse der Kleinproben aus AISI 316L weisen die charakteristischen Eigenschaften des Werkstoffs auf, und die Analyse der Zug- und Ermüdungsdaten führt zu Werten, die den Literaturdaten weitgehend entsprechen. Der direkte Vergleich mit Standardprobendaten zeigt jedoch systematische Abweichungen bei Zugfestigkeit, Dehngrenze und Gleichmaßdehnung, die in diesem Beitrag diskutiert werden. N2 - The use of miniaturized specimen geometries in mechanical testing allows to extract speci-men material directly from critical areas such as weldments and to test small structures such as additively manufactured components. In the present paper, example results of comparative tensile and low-cyclic fatigue tests (LCF) on the austenitic steel AISI 316L and the nickel-based alloy IN718 are presented. The test results of the small specimens on AISI 316L show the characteristic properties of the material, and the analysis of the tensile and fatigue tests leads to values which largely correspond to literature data. However, the direct comparison with standard sample data shows systematic deviations in tensile strength, yield strength and uniform elongation, which are discussed in this paper. T2 - Werkstoffprüfung 2019 CY - Neu-Ulm, Germany DA - 03.12.2019 KW - Kleinprobenprüfung KW - Probengrößeneffekt KW - Low Cycle Fatigue KW - Zugversuch KW - AISI 316L KW - IN 718 PY - 2019 SP - 329 EP - 334 AN - OPUS4-50220 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias A1 - Stark, Wolfgang A1 - Hoster, B. T1 - In-situ vulcanization monitoring by ultrasonic wave propagation T2 - 8. Kautschuk-Herbst-Kolloquium CY - Hannover, Deutschland DA - 2008-11-26 KW - Vulcanization KW - Cure monitoring KW - Ultrasound PY - 2008 SP - 133 AN - OPUS4-18574 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Agroui, K. A1 - Jaunich, Matthias A1 - Hadj Arab, A. T1 - Analysis techniques of polymeric encapsulant materials for photovoltaic modules: Situation and perspectives N2 - The properties of the encapsulant are critical to the long-term performance of photovoltaic (PV) modules under the influence of sunlight including UV, elevated temperature, humidity and diffusion of oxygen. Encapsulation process represents about 40% of the whole PV module cost. The introduction of new non-EVA encapsulant material type “Low-Cost, High-Performance” should provide a solution to outdoor yellowing degradation problems. The emerging encapsulant materials exhibit a good compatibility with emerging PV solar cells for long term durability. This new generation of encapsulant materials has the advantage to improve the PV module performances and long term durability for specific climate like desert regions. This scientific contribution presents an overview of the different encapsulant materials currently on the market, the general requirements of the emerging encapsulant materials and characterizations techniques for degradation, diagnostic and reliability lifetime estimation in the framework of Algerian renewable energy strategy. T2 - Africa-EU Symposium on Renewable Energy Research and Innovation CY - Tlemcen, Algeria DA - 08.03.2016 KW - solar cells KW - PV modules KW - polymer encapsulant KW - encapsulation KW - analysis techniques PY - 2016 SP - 27 EP - 27 PB - European Union Energy Initiative – Partnership Dialogue Facility (EUEI PDF) CY - Eschborn, Germany AN - OPUS4-35917 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Charmi, Amir T1 - A multiscale numerical framework for the simulation of anistropic material response of additively manufactured stainless steel 316L undergoing large plastic deformation N2 - Additive manufacturing (AM) offers significantly greater freedom of design compared to conventional manufacturing processes since the final parts are built layer by layer. This enables metal AM, also known as metal 3D printing, to be utilized for improving efficiency and functionality, for the production of parts with very complex geometries, and rapid prototyping. However, despite many technological advancements made in recent years, several challenges hinder the mass adoption of metal AM. One of these challenges is mechanical anisotropy which describes the dependency of material properties on the material orientation. Therefore, in this work, stainless steel 316L parts produced by laser-based powder bed fusion are used to isolate and understand the root cause of anisotropy in AM parts. Furthermore, an efficient and accurate multiscale numerical framework is presented for predicting the deformation behavior of actual AM parts on the macroscale undergoing large plastic deformations. Finally, a novel constitutive model for the plastic spin is formulated to capture the influence of the microstructure evolution on the material behavior on the macroscale. KW - Additive Fertigung KW - Austenitischer Stahl KW - Finite-Elemente-Methode KW - Mehrskalenmodell KW - Simulation PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:gbv:wim2-20240207-173356-002 DO - https://doi.org/10.25643/dbt.59550 SP - 1 EP - 163 PB - Bauhaus-Universität Weimar CY - Weimar AN - OPUS4-59511 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Boller, Ch. A1 - Mueller, Bernd R. A1 - Heckel, Thomas A1 - Starke, P. A1 - Gohlke, Daniel A1 - Venkat, R. S. A1 - Bruno, Giovanni T1 - Nonlinearities based inverse approach for the characterisation of the damage evaluation process in very high cycle fatigued CFRP specimens N2 - This paper focuses on the aspect on how damage evolution processes in composite materials and structures including matrix fracture, delamination, fibre-matrix debonding, and fibre fracture can be detected by taking advantage of the material’s inherit mechanical properties. These properties can be described on the basis of non-linear mechanical phenomena measurable as an inert frequency response signal. The approach is proposed as a means for residual life structural assessment specifically in the context of VHCF. T2 - The Seventh International Conference on Very High Cycle Fatigue - VHCF7 CY - Dresden, Germany DA - 03.07.2017 KW - Composite materials KW - Damage KW - Non-destructive testing KW - Fatigue KW - Structural simulation KW - Non-linear vibration PY - 2017 VL - 2017 SP - 1 EP - 8 PB - DVM AN - OPUS4-41102 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lange, Axel A1 - Hentschel, Manfred P. A1 - Kupsch, Andreas A1 - Jaenisch, Gerd-Rüdiger A1 - Kardjilov, N. A1 - Tötzke, C. A1 - Markötter, Henning A1 - Hilger, A. A1 - Manke, I. T1 - X-ray compton tomography N2 - The potentials of incoherent X-ray Scattering (Compton) tomography are investigated. Imaging materials of very different density or atomic number at once is a perpetual challenge for X-ray tomography or radiography, in general. In a basic laboratory set-up for simultaneous perpendicular Compton Scattering and direct beam attenuation tomographic scans are conducted by single channel photon counting. This results in asymmetric distortions of the projection profiles of the scattering CT-data set. ln a first approach corrections of Compton scattering data by taking advantage of rotational symmetry yield tomograms without major geometric artefacts. A cylindrical sample composed of PE, PA, PVC, glass and wood demonstrates similar Compton contrast for all the substances, while the conventional absorption tomogram only reveals the two high order materials. Compärison to neutron tomography reveals astonishing similarities except for the glass component (without hydrogen). Therefore, Compton CT bears the potential to replace neutron tomography, which requires much more efforts. T2 - ECNDT 2014 - 11th European Conference on Non-Destructive Testing CY - Prague, Czech Republic DA - 06.10.2014 KW - X-ray compton scattering KW - Computed tomography KW - Neutron tomography PY - 2014 SN - 978-80-214-5018-9 SP - 1 EP - 9 PB - Brno University of Technology CY - Brno AN - OPUS4-31972 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Naghib Zadeh, Hamid A1 - Rabe, Torsten T1 - Pressure-assisted sintering of multilayer transformer using LTCC-compatible NiCuZn-ferrite and silver conductor N2 - A low-fired NiCuZn-ferrite and a new LTCC dielectric material with matched sintering shrinkages and coefficients of thermal expansion were used for integration of magnetic function into LTCC. Silver was used as inner conductor material. Silver diffusion during sintering into the surrounding glassy phase modifies the sintering behaviour of LTCC near the silver conductor and generates warping and delamination of the multilayer. Silver diffusion can be prevented by sintering in nitrogen atmosphere. However, sintering in nitrogen atmosphere causes partial decomposition of NiCuZn-ferrite by reduction of divalent copper oxide (CuO) to cuprite (Cu2O). It was found that diffusion of silver and associated deformation can be highly reduced if a higher heating rate during sintering in air is used. A Defect-free multilayer transformer with several silver conductive layers could be manufactured by pressure-assisted sintering only. T2 - CICMT 2012 - 8th International conference on ceramic interconnect & ceramic microsystems technologies CY - Erfurt, Germany DA - 16.04.2012 KW - LTCC KW - Ferrite KW - Silver conductor PY - 2012 IS - Session WP 1 / WP 15 SP - 000476 EP - 000483 AN - OPUS4-27775 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nehrig, Marko A1 - Bletzer, Claus Wilhelm A1 - Wille, Frank T1 - Safety assessment aspects of type B(U) packages containing wet intermediate level waste N2 - In Germany, the mechanical and thermal safety assessment of approved packages for the transport of RAM is carried out by BAM as the competent authority according to the International Atomic Energy Agency regulations. BAM was involved in several approval procedures with ductile cast iron containers containing wet intermediate level waste. These contents, which are not dried, only drained, consist of saturated ion exchange resin and a small amount of free water. Compared to the safety assessment of packages with dry content, attention must be paid to some more specific points. The physical and chemical compatibility of the content itself and of the content with materials of the package must be shown. From the mechanical resistance point of view, the package has to withstand the forces resulting from the freezing liquid. The most interesting point, however, is the pressure build-up inside the package due to vapourisation. This could be caused by radiolysis of the liquid and must be taken into account for the storage period. The paper deals primarily with the pressure build-up inside the package caused by the regulatory thermal test (30 min at 800°C) as part of the cumulative test scenario under accident conditions of transport. To determine the pressure, the temperature distribution in the content must be calculated for the whole period from the beginning of the thermal test until cooling down. In this case, calculating the temperature distribution requires, besides the consideration of conduction and heat radiation, consideration of evaporation and condensation including the associated processes of transport. T2 - RAMTRANSPORT 2012 - 9th International Conference on the Radioactive Materials Transport and Storage CY - London, UK DA - 22.05.2012 KW - Radioactive materials KW - Safety assessment KW - Pressure build-up KW - Wet intermediate level waste PY - 2012 SP - 1 EP - 7 AN - OPUS4-26314 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Averin, Anton T1 - Automated thermographic inspection of radioactive waste drums N2 - In Germany, more than 130,000 cubic meters of low- and medium-level radioactive waste, comprising approximately 90% of the nation’s total radioactive waste, are stored in 200-liter drums. These waste drums, housed in interim storage facilities, are subject to human visual inspections for outer corrosion, while the final disposal site, the Konrad mine, is scheduled for completion in 2030. Manual inspections introduce the risk of human error, making the process less reliable and less safe. The proposed study aims to automate these inspections by implementing remote and non-destructive testing (NDT) methods. The part of project specifically focuses on the application of infrared thermography to detect inner defects in the metallic drums, which could not have been detected so far using visual inspection alone. However, several challenges affect the accuracy of thermographic inspections, such as the presence of surface contaminants (scratches, dirt, stickers), multiple paint layers with low thermal conductivity, and barrel curvature, which disrupt heat distribution and obscure defect signals. This study explores the effectiveness of various thermographic heat sources—flash lamps and laser—as well as techniques including conventional pulse thermography (PT), lock-in thermography. It explores various thermal data processing methods as principal component thermography (PCT), pulse-phase thermography (PPT) and thermal signal reconstruction (TSR). Additionally, machine learning models were estimated to process thermographic images, effectively filtering artifacts (e.g. surface contaminants). The findings suggest that combining advanced thermography techniques with machine learning improves defect detection, ensuring more reliable and automated inspection processes for radioactive waste storage. T2 - SPIE Defense + Commercial Sensing - Thermosense: Thermal Infrared Applications XLVII CY - Orlando, FL, USA DA - 13.04.2025 KW - Automated inspection KW - Defect detection KW - Infrared thermography KW - Laser thermography KW - Machine Learning KW - Principal component thermography KW - Pulse-phase thermography KW - Thermal Data Processing PY - 2025 UR - https://www.spiedigitallibrary.org/conference-proceedings-of-spie/13470/3052732/Automated-thermographic-inspection-of-radioactive-waste-drums/10.1117/12.3052732.short DO - https://doi.org/10.1117/12.3052732 SP - 1 EP - 19 PB - SPIE AN - OPUS4-63285 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Zhu, Pengfei A1 - Maldague, Xavier T1 - Principal Component Analysis-Based Terahertz Self-Supervised Denoising and Deblurring Deep Neural Networks N2 - Terahertz (THz) systems inherently introduce frequency-dependent degradation effects, resulting in low-frequency blurring and high-frequency noise in amplitude images. Conventional image processing techniques cannot simultaneously address both issues, and manual intervention is often required due to the unknown boundary between denoising and deblurring. To tackle this challenge, we propose a principal component analysis (PCA)-based THz self-supervised denoising and deblurring network (THz-SSDD). The network employs a Recorrupted-to-Recorrupted self-supervised learning strategy to capture the intrinsic features of noise by exploiting invariance under repeated corruption. PCA decomposition and reconstruction are then applied to restore images across both low and high frequencies. The performance of the THz-SSDD network was evaluated on four types of samples. Training requires only a small set of unlabeled noisy images, and testing across samples with different material properties and measurement modes demonstrates effective denoising and deblurring. Quantitative analysis further validates the network’s feasibility, showing improvements in image quality while preserving the physical characteristics of the original signals. KW - Non-destructive testing (NDT) KW - Terahertz KW - Denoising KW - Self-supervised learning KW - Deblurring PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-654043 DO - https://doi.org/10.48550/arXiv.2601.12149 SN - 2331-8422 SP - 1 EP - 9 PB - Cornell University CY - Ithaca, NY AN - OPUS4-65404 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hassenstein, Christian A1 - Hirsch, Philipp Daniel A1 - Wassermann, Jonas A1 - Heckel, Thomas T1 - Automated self-adjustment of array probe with a robotic ultrasonic test system N2 - Ultrasonic testing of objects with complex geometries often requires the use of a robotic arm to position the probe perpendicular to the local surface. Using immersion makes it possible to test these objects with standard ultrasonic linear array probes. Here, the probe positions and orientations provided by the robot are used for merging the locally acquired image data into a 3D-reconstruction. The quality of this reconstruction is highly dependent on the alignment of the position of the physical probe with the position used in the digital model. For common industrial tools, the tool center point (TCP) is usually acquired using geometric features of the tools. However, for ultrasonic arrays in immersion, there is a water standoff between the probe and the test object, therefore the TCP is in free space in front of the array and cannot be acquired with the common method. To overcome this challenge, we propose a method that allows the robotic ultrasonic system to automatically self-adjust the position and orientation of the ultrasonic probe using a test block made of steel with defined geometric features as a target for referencing. For each of the six degrees of freedom, a scan and adjustment routine are established using the data based on the actual ultrasound characteristics of the probe. Given a coarse pre-definition of the tool position and the known target test block, minimal human interaction is required to supervise the adjustment method, leading to higher quality reconstructions than with manual adjustment. T2 - 20th World Conference On Non-Destructive Testing (WCNDT 2024) CY - Incheon, South Korea DA - 27.05.2024 KW - Testing KW - Automation KW - NDT 4.0 KW - Robotics KW - Ultrasonic PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-616387 UR - https://www.ndt.net/search/docs.php3?id=30309 SN - 1435-4934 SP - 1 EP - 9 PB - NDT.net AN - OPUS4-61638 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Genga, R. M. A1 - Conze, S. A1 - Berger, L.M. A1 - Pötschke, J. A1 - Witte, Julien A1 - Schröpfer, D. A1 - Cermak, A. A1 - Zeman, P. A1 - Ngongo, S. A1 - Janse van Vuuren, A. T1 - Enhanced Fe and Ni bonded NbC Laser Surface Engineered based Hardmetals: Alternative Cutter Materials for Electric Vehicle Applications N2 - The efforts to substitute both tungsten carbide (WC) and cobalt (Co) has gained prominence in recent years due to the classification of Co as a carcinogen and the classification of Co and W as critical raw materials in the EU as well as within regulations of the U.S. National Toxicology Program. In this study, substitution of both WC and Co with advanced hardmetals consisting of NbC with Ni and Fe-based metal binders are investigated for their use of machining of metals used electric vehicle manufacturing. The developed NbC-Ni/Fe based hardmetals employ a Machining Property Led Tailored Design (MPLTD) approach. This reverse engineering strategy uses data from machining performance to guide the development of microstructural, mechanical, and behavioral properties. Four advanced NbC-based hardmetals were produced, two with Ni-based binders and two with Fe-based binders, along with two reference materials for comparison (WC-Co and straight NbC-12Ni). Hardmetals were characterized using field emission scanning electron microscopy (FE-SEM), annular dark-field scanning transmission electron microscopy (ADF-STEM), Vickers hardness, fracture toughness, and elastic moduli. Cutting tool inserts were manufactured from the developed hardmetals and enhanced using femto-second laser surface engineering. The inserts’ performance was evaluated through face milling tests on AZ31 automotive magnesium alloy, providing insights into their suitability for high-demand industrial applications. T2 - 21. Plansee Seminar CY - Reutte, Österreich DA - 01.06.2025 KW - Niobium carbide KW - Alternative binders KW - Alternative hard phases KW - Face milling KW - AZ31 magnesium alloy PY - 2025 VL - 2025 SP - 1 EP - 10 AN - OPUS4-65382 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Spitzer, Stefan T1 - Influence of the ignition source on the Safety Characteristics of hybrid dust-gas mixtures N2 - Safety characteristics like the lower explosion limit, the highest concentration for a given substance mixed with air that does not result in a self-propagating flame, or the maximum explosion pressure, the highest pressure that can be reached after ignition for a given combustible substance mixed with air at any concentration, are widely used in the industry to either prevent an explosion or to mitigate the effects of it. Safety characteristics are not physical constants, are determined experimentally and depend on the chosen experimental parameters such as the ignition energy or turbulence. For the determination of the safety characteristics lower explosion limit (LEL), limiting oxygen concentration (LOC), maximum explosion pressure (pmax) and maximum rate of pressure rise ((dp/dt)max) of gases and vapors the gas is filled via partial pressures into a test vessel and then ignited under quiescent conditions with a weak (2 J - 20 J) ignition source. For dusts, the same safety characteristics are determined under turbulent conditions to elevate the dust homogeneously and it is ignited with two chemical igniters with an ignition energy of 1000 J each (LEL and LOC) or 5000 J each (pmax and (dp/dt)max). For the determination of safety characteristics of hybrid mixtures (a mixture containing a combustible dust and a flammable gas) there is no existing standard. In the last 40 years most of the research on their safety characteristics was performed with dust testing equipment that was modified for the addition of flammable gas. Because of the different mixing procedures of gases and dusts with air and because of different ignition energies and sources that are normally used for the standard tests of gases or dusts, the results were hardly reproducible. Statements about the different safety characteristics were contradictory and left the reader or the person responsible for designing safety measures for a process plant or a facility behind with no clear suggestion about the behavior of hybrid mixtures. This thesis is aimed on determining the influence of the different ignition sources and energies on the safety characteristics pmax, (dp/dt)max, lower explosion limit, and limiting oxygen concentration of hybrid mixtures. Several test series were conducted to characterize different standardized ignition sources, that are already in use for the determination of safety characteristics of single-phase substances (gases, liquids, dusts). The burning duration, the igniting volume and the net energy were investigated. It was shown, that the chemical igniters and the exploding wire are suitable ignition sources for the determination of safety characteristics of hybrid mixtures in general. Their burning duration was long enough to ignite dusts and quick enough, that the decay of the turbulence or sedimentation of the dusts did not occur. Both ignition sources produced comparable results for the determination of pmax, LEL and (dp/dt)max of dusts when they had the same ignition energy. A reduced ignition energy of the exploding wire and the chemical igniters did not affect the pmax and (dp/dt)max. The LEL changed with lower energies. However, for the determination of the LOC of hybrid mixtures the exploding wires with an overall energy of 2 kJ produced the best results. The influence of the different mixing procedures that have already been used for hybrid mixtures and the requirements for them were also investigated experimentally for the gas concentration and the determined safety characteristics and compared to each other. It was shown, that the partial pressure method works for mixing hybrid mixtures but the pressures should be measured very accurately and the gas concentration should be validated. Furthermore, the influence of the turbulence that is inevitable when testing dusts, on the safety characteristics of gases was determined. It was found that the chemical igniters and exploding wires produced comparable results for the determination of pmax, LEL and (dp/dt)max under turbulence. For the LOC only exploding wires with two times 1 kJ worked. Finally, the safety characteristics of hybrid mixtures were determined with different ignition energies and sources and the data were compared. It was discovered, that the pmax of hybrid mixtures was the same value than the higher determined one of the single substances while (dp/dt)max of hybrid mixtures was about 10 % to 25 % higher than the value of the stoichiometric gas mixture under turbulence. The point was found at the stoichiometric gas concentration with very little amounts of dust. To prove the key findings of this work and for the establishment of a standardized procedure for the determination of safety characteristics of hybrid mixtures, an international round robin test was conducted with eleven participating facilities in seven countries. The results were comparable within a reasonable range and are presented in this dissertation in an extra chapter. Based upon the observations in this work a reliable solution for a new standardizable ignition source to determine the safety characteristics of hybrid dust-gas-mixtures is proposed. KW - Ignition Sources KW - Hybrid Mixtures KW - Explosions PY - 2023 SP - 1 EP - 132 AN - OPUS4-58905 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Recknagel, Christoph A1 - Spitzer, Stefan A1 - Hoppe, Johannes A1 - Wenzel, Norman A1 - Pirskawetz, Stephan T1 - Innovative Sensorik für Fugensysteme N2 - Die zielgerichtete Weiterentwicklung von Bauteilen und Konstruktionselementen im Straßenbau hochbeanspruchter Verkehrswege unserer Infrastruktur (Bundesfernstraßen) erfordert spezielle, bauteiladaptierte technische Möglichkeiten/Sensorik zur Quantifizierung des Gebrauchsverhaltens. Bei Fugen in Verkehrsflächen stellen insbesondere langsam und schnell ablaufende Plattendeformationen infolge jahreszeitlicher und verkehrlicher Beanspruchungen maßgebende Beanspruchungszustände dar. Eine Quantifizierung dieser Einwirkungen hilft bei der Weiterentwicklung sowie auch bei der Bewertung optimierter technischer Lösungen. In Forschung kompakt 17/21 „Innovative Sensorik für Fugensysteme“ wird eine neuartige, robuste Lösung der BAM zur Datenerfassung und Bauwerksmonitoring von hochbeanspruchten Verkehrsflächen aus Beton vorgestellt. KW - Betonfahrbahndecke KW - Fugen KW - Quantifizierung realer Verformungen PY - 2021 VL - 17 SP - 1 EP - 2 PB - Eigenverlag der BASt CY - BASt, Bergisch Gladbach AN - OPUS4-54115 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mishurova, Tatiana A1 - Cabeza, S. A1 - Artzt, Katia A1 - Haubrich, J. A1 - Requena, G. A1 - Bruno, Giovanni T1 - Analyse von oberflächennahen Eigenspannungen in SLM TI-6AL-4V Proben N2 - Bei der additiven Fertigung können sich während des Prozesses aufgrund von hohen Aufheiz- und Abkühlraten Eigenspannungen ausbilden, die potentiell zu einem Verzug von Bauteilen führen und sich negativ auf das mechanische Verhalten auswirken. In dieser Studie wurden Ti-6Al-4V Proben durch Selektives Laserschmelzen mit verschiedenen Lasergeschwindigkeiten additiv gefertigt, um die Auswirkung der Laserenergiedichte auf den Eigenspannungszustand zu untersuchen. Die oberflächennahe Eigenspannungsanalysen wurden mittels energiedispersiver Synchrotronbeugung durchgeführt. Insgesamt wurden hohe Zugspannungen an den Seitenflächen der Proben gefunden. Es wurde festgestellt, dass je höher die Laserenergiedichte während der Fertigung ist, desto geringer fallen die Eigenspannungen aus. Eine nachträglich durchgeführte Wärmebehandlung führt zu einem vollständigen Abbau von Eigenspannungen. T2 - 2. Tagung des DVM-Arbeitskreises Additiv gefertigte Bauteile und Strukturen CY - Berlin, Germany DA - 09.11.2017 KW - Selektive Laserschmelzen KW - Wärmebehandlung KW - Synchrotronbeugung KW - Eigenspannungen PY - 2017 SP - 89 EP - 98 AN - OPUS4-42871 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Serrano-Munoz, Itziar A1 - Mouiya, Mossaab A1 - Prasek, Marco A1 - Kupsch, Andreas A1 - Bruno, Giovanni T1 - High temperature in-situ heat treatment of a refractory material by means of synchrotron refraction radiography N2 - The stress–strain behavior of certain ceramics, such as aluminum titanate (AT, Al2TiO5), has features that are unusual for brittle material. In particular, a substantial nonlinearity under uniaxial tension, and load–unload hysteresis caused by the increase of the incremental stiffness at the beginning of unloading. These features are observed experimentally and attributed to microcracking. In this study, we investigate the mechanical response of an AT material at room and high temperature. Microstructure and microcracking are analyzed by means of electron microscopy, and both synchrotron micro computed tomography (µCT) and refraction radiography (SXRR). Synchrotron refraction radiography is combined with in-situ heating at high-temperatures (up to 1400°C) to be able to monitor the relative closure of microcracks as a function of increasing/decreasing temperatures. T2 - ECCM21 CY - Nantes, France DA - 02.07.2024 KW - Refractory materials KW - Microcracking KW - Synchrotron µCT and refraction radiography KW - In-situ heating up to 1400°C PY - 2024 UR - https://gem.ec-nantes.fr/en/eccm21-proceedings/ SN - 978-2-912985-01-9 DO - https://doi.org/10.60691/yj56-np80 SP - 47 EP - 53 PB - The European Society for Composite Materials (ESCM) and the Ecole Centrale de Nantes. CY - Nantes AN - OPUS4-60581 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mishurova, Tatiana A1 - Artzt, Katia A1 - Bruno, Giovanni A1 - Requena, Guillermo A1 - Haubrich, Jan T1 - Subsurface residual stress analysis in Ti-6Al-4V additive manufactured parts by synchrotron x-ray diffraction N2 - Synchrotron X-ray diffraction is a powerful non-destructive technique for the analysis of the material stress-state. High cooling rates and heterogeneous temperature distributions during additive manufacturing lead to high residual stresses. These high residual stresses play a crucial role in the ability to achieve complex geometries with accuracy since they can promote distortion of parts during manufacturing. Furthermore, residual stresses are critical for the mechanical performance of parts in terms of durability and safety. In the present study, Ti-6Al-4V bridge-like specimens were manufactured additively by selective laser melting (SLM) under different laser scanning speed conditions in order to compare the effect of process energy density on the residual stress state. Subsurface residual stress analysis was conducted by means of synchrotron X-ray diffraction in energy dispersive mode for three conditions: as-built on base plate, released from base plate, and after heat treatment on the base plate. The quantitative residual stress characterization shows a correlation with the qualitative bridge curvature method. Computed tomography (CT) was carried out to ensure that no stress relief took place owing to the presence of porosity. CT allows obtaining spatial and size pores distribution which helps in optimization of the SLM process. High tensile residual stresses were found at the lateral surface for samples in the as-built conditions. We observed that higher laser energy density during fabrication leads to lower residual stresses. Samples in released condition showed redistribution of the stresses due to distortion. T2 - 12th ECNDT 2018 CY - Göteborg, Sweden DA - 11.06.2018 KW - Additive manufacturing KW - Selective laser melting KW - Residual stress KW - Synchrotron X-ray diffraction KW - Ti-6Al-4V PY - 2018 UR - http://cdn.ecndt2018.com/wp-content/uploads/2018/05/ecndt-0213-2018-File001.pdf SP - 1 EP - 8 AN - OPUS4-45217 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mishurova, Tatiana A1 - Léonard, Fabien A1 - Oesch, Tyler A1 - Meinel, Dietmar A1 - Bruno, Giovanni A1 - Rachmatulin, Natalia A1 - Fontana, Patrick A1 - Sevostianov, I. T1 - Evaluation of fiber orientation in a composite and its effect on material behavior N2 - The reinforcement of concrete with polymer fibers provides resistance to crack formation. The orientation distribution of these fibers has a significant influence on the mechanical behavior of the material. To optimize material performance, micromechanical models that are capable of making accurate predictions of the mechanical behavior of composite materials are needed. These models must be calibrated using experimental results from microstructural characterization. For the fiber orientation distribution analysis in the present study, computed tomography (CT) data were used to evaluate the properties of a fiber-reinforced cement mortar. The results have indicated that the fibers in this material have highly anisotropic orientation characteristics and that there is a clear tendency for the polymer fibers to agglomerate during mixing and casting. The incorporation of this experimental data into micromechanical models will increase the accuracy of those models for material simulation and optimization. T2 - 7th Conference on Industrial Computed Tomography (iCT 2017) CY - Leuven, Belgium DA - 07.02.2017 KW - Orientation distribution KW - Fiber-reinforced concrete KW - Computed tomography PY - 2017 UR - http://www.ndt.net/?id=20818 SN - 1435-4934 VL - 22 IS - 3 SP - 1 EP - 7 PB - NDT.net CY - Kirchwald AN - OPUS4-39338 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thiede, Tobias T1 - Influence of deposition hatch length on residual stress in selective laser melted Inconel 718 N2 - Additive Manufacturing (AM) by Selective Laser Melting (SLM) offers ample scope for producing geometrically complex parts in comparison to the traditional subtractive manufacturing strategies. Developing during the manufacturing process, residual stresses may limit the application of SLM parts by reducing the load bearing capacity as well as induce unwanted distortion depending on the boundary conditions specified in manufacturing. The present study aims to evaluate the bulk residual stresses in SLM parts by using neutron diffraction measurements performed at E3 line -BER II neutron reactor- of Helmholtz-Zentrum für Materialien und Energie (HZB) Berlin. Together with microstructure characterization and distortion measurements, it is possible to describe the stress state throughout the whole sample. The sample was measured in as-build condition (on a build plate) and after releasing from the build plate. The used material is the nickel based superalloy 718. This alloy is widely used in aerospace and chemical industries due to its superior corrosion and heat resistant properties. Obtained results indicated different residual stress states for each of the transversal, longitudinal and normal component. The normal and transversal component exhibits a rather compressive behavior while the longitudinal was tensile in the center part of the sample and became compressive towards the tip. As expected, the absolute values of all stress components decreased after releasing the sample from the building plate. A surface scan utilizing a coordinate-measuring machine (CMM) allowed us to present top surface distortion before and after releasing. The top surface showed a distortion around ±80µm after releasing. Microstructure evolution in the scanning-building cross-section is largely dominated by columnar grains. In addition, many small random orientated grains are prominent in the regions of a laser overlap during SLM. In summary, for the sample of superalloy 718 manufactured by SLM, a small distortion occurred when removing the sample from the build plate whereby the residual stress state decreases. Moreover, the observed columnar grains in the building direction could give a reason for the lowest stress values in that normal direction. However, the most important parameter controlling the residual stresses is the temperature gradient. Hence, future investigations are planned for a different scan strategy to distribute the laser impact in a more homogenous manner. T2 - HZB User Meeting 2017 CY - Berlin, Germany DA - 15.12.2017 KW - AM KW - SLM KW - IN 718 KW - Neutron diffraction KW - Residual stress KW - Hatch length KW - Microstructure PY - 2017 AN - OPUS4-43475 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Vogl, Jochen T1 - Calibration of Mg isotope amount ratios and delta values N2 - In the past, δ26/24Mg measurements were referenced to NIST SRM 980, the initial zero of the δ26/24Mg scale. With the development of MC-ICPMS, the detection of small but measurable isotopic differences in different chips of SRM 980 became apparent. To solve this problem a suite of magnesium isotope reference materials, ERM-AE143, -AE144 and -AE145, has been certified in a first study by applying an ab initio calibration for absolute Mg isotope ratios without any a priori assumptions, a procedure which fulfils all requirements of a primary method of measurement. We could achieve for the first time measurement uncertainties for isotope amount ratios close to the typical precision of magnesium delta values, δ26/24Mg, which are at the 0.1 ‰ level (2SD). In addition, it was demonstrated that commonly used fractionation laws are invalid for correcting Mg isotope ratios in multi-collector ICPMS as they result in a bias which is not covered by its associated uncertainty. Depending on their type, fractionation laws create a bias up to several per mil, with the exponential law showing the smallest bias between 0.1 ‰ to 0.7 ‰. With these isotope reference materials, it is possible to establish SI-traceability for magnesium delta measurements. To realize this, we organized a second study within which five expert laboratories participated to cross-calibrate all available magnesium isotope standards, which are NIST SRM 980, IRMM-009, ERM-AE143, ERM-AE144, ERM-AE145 and the standards DSM3 and Cambridge-1. The mean δ26/24Mg values for the individual iRMs, calculated from the laboratory means show 2 SD reproducibilities varying between 0.025 and 0.093 ‰. Propagated measurement uncertainties suggest a standard uncertainty of about 0.1‰ for δ26/24Mg determinations (2SD). Thus, SI traceability for magnesium isotope amount ratios and delta values is demonstrated to be established. T2 - European Winter Conference on Plasma Spectrochemistry CY - Pau, France DA - 03.02.2019 KW - Delta value KW - SI-traceability KW - Absolute isotope ratio PY - 2019 N1 - Geburtsname von Mieller, Björn: Brandt, B. - Birth name of Mieller, Björn: Brandt, B. AN - OPUS4-47710 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Spitzer, Stefan A1 - Askar, Enis A1 - Krietsch, Arne A1 - Schröder, Volkmar T1 - Comparative study on standardized ignition sources used for explosion testing N2 - For the determination of safety characteristics of gases, vapors and dusts different types of ignition sources are used in international standards and guidelines. Table 1 compares technical relevant ignition sources with their main features. The paper presents test results of a comparative calorimetric and visual study between four different types of ignition sources. The ignition procedures were analyzed visually with a high-speed camera and electric recordings. In addition to that, the influence of the electrode-orientation, -distance as well as ignition energy on the reproducibility of the exploding wire igniter was tested. The exploding wire is already in use for standardized determination of safety characteristics of gases, first tests on the suitability of the exploding wire igniter for dust testing have been carried out by Scheid et al. Using the exploding wire, the ignition energy can be varied from 2 to 10 000 J (2 x 5 000 J) and thus it could be used for gases, vapors, dusts and hybrid mixtures. Moreover it can be used at high initial pressures and it is the only ignition source with an easily measurable ignition energy release. Furthermore, it does not introduce another chemical reaction into the system. Finally, a proposal for a standard ignition source for explosion tests on hybrid mixtures is derived from the test results. T2 - 13th International Symposium on Hazards, Prevention and Mitigation of Industrial Explosions CY - Online meeting DA - 27.07.2020 KW - Ignition source KW - Exploding Wire KW - Hybrid mixtures KW - Safety characteristics determination PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-517908 UR - https://oar.ptb.de/files/download/5f3e662f4c93901010006dbf DO - https://doi.org/10.7795/810.20200724 VL - 13 SP - 864 EP - 875 PB - PTB Physikalisch-Technische Bundesanstalt Braunschweig AN - OPUS4-51790 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Spitzer, Stefan A1 - Askar, Enis A1 - Krietsch, Arne A1 - Schröder, Volkmar T1 - Entwicklungen zu Bestimmungsverfahren für sicherheitstechnische Kenngrössen hybrider Gemische N2 - Zur Bestimmung sicherheitstechnischer Kenngrößen (STK) von hybriden Gemischen (Gemisch aus mindestens zwei brennbaren Phasen, wie z.B. Staub/Gas- oder Gas/Dampf-Gemisch) existieren bislang keine einheitlichen, genormten Prüfmethoden. Die Normen und Regelwerke zur Bestimmung der STK von einphasigen brennbaren Systemen (Staub, Gas, Dampf) unterscheiden sich teilweise erheblich. Beispielsweise sind in den jeweiligen Normen für Stäube, Gase und Dämpfe unterschiedliche Zündquellen und Zündenergien definiert. Des Weiteren unterscheiden sich die in den Normen definierten Prüfabläufe bei der Gemischherstellung. Bei der Entwicklung einer einheitlichen Norm für hybride Gemische muss der Einfluss dieser beiden Parameter ermittelt werden, um die Vergleichbarkeit mit den STK der einzelnen Komponenten Gas, Staub und Dampf gewährleisten zu können und bisherige Erkenntnisse zu hybriden Gemischen interpretieren und bewerten zu können. T2 - VDI-Fachtagung "Sichere Handhabung brennbarer Stäube" CY - Online meeting DA - 04.11.2020 KW - Explodierender Draht KW - Sicherheitstechnische Kenngrößen KW - Hybride Gemische PY - 2020 SN - 978-3-18-092376-5 SN - 0083-5560 VL - 2376 SP - 3 EP - 15 PB - VDI Verlag GmbH CY - Düsseldorf AN - OPUS4-51789 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN ED - Bosse, H. ED - Buhr, E. ED - Dziomba, T. ED - Hodoroaba, Vasile-Dan ED - Klein, T. ED - Krumrey, M. T1 - NanoWorkshop 2018: Workshop on Reference Nanomaterials N2 - The Scope of the Workshop was to provide a forum for discussion on progress in development, characterisation and application of reference nanomaterials. Results of recently finished national and international research projects have been presented. Moreover, the need for future developments have been addressed. Attendees of the Workshop were expected to be experts from academia, research institutes, regulatory bodies and industry working or interested in the area of reference nanomaterials. The following structure of Workshop was planned: the main focus of the first day was on reference material needs and development, while the second day was focussed on reference materials characterisation and standardisation. Over 111 participants from 13 countries and the European Joint Research Centre have registered for the Workshop with 16 platform presentations and 42 poster contributions grouped in 2 sessions and 10 topical areas. A summary of the observations, analysis and conclusions of the Workshop is made including an overview table of links to information on existing reference nanomaterials. KW - Reference Nanomaterials KW - Nanometrology KW - Standardization KW - Nanoparticle Characterization KW - Comparability of Measurement Results KW - Nanomaterial Properties PY - 2019 SN - 978-3-95606-440-1 DO - https://doi.org/10.7795/110.20190412 SN - 0179-0609 VL - 2018 SP - 1 EP - 315 PB - Physikalisch-Technische Bundesanstalt CY - Braunschweig AN - OPUS4-47861 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Bettge, Dirk T1 - Mikrostrukturelle Untersuchungen zum Verformungs- und Bruchverhalten der Nickelbasislegierungen SC16 und IN738LC N2 - Ziele dieser Arbeit waren die vergleichende Beschreibung des Verformungs- und Bruchverhaltens der polykristallinen Legierung IN738LC und von [001]-nah orientierten SC16-Einkristallen über einen großen Temperaturbereich sowie die Herstellung von Zusammenhängen zwischen Versetzungs- und Bruchmechanismen. Besonderes Augenmerk galt dem Tieftemperaturbereich bis 450 °C, dabei insbesondere der Stapelfehlerbildung in der Gamma'-Phase, dem Fließspannungsminimum im Zugversuch und der zusätzlichen zyklischen Verfestigung in diesem Temperaturbereich. Spezifische Unterschiede zwischen beiden Werkstoffen sollten herausgearbeitet werden. Dazu wurden hauptsächlich mikroskopische Methoden, insbesondere die Transmissions-Elektronenmikroskopie eingesetzt. Die Ausgangsgefüge wurden untersucht. Beide Werkstoffe hatten die übliche Standardwärmebehandlung erfahren und wiesen daher eine bimodale gamma'-Verteilung auf. An SC16 wurden Auslagerungsversuche bei 950 °C vorgenommen und die Veränderung der gamma'-Morphologie beschrieben. Die Temperaturabhängigkeiten der Verformungsmechanismen von SC16 und IN738LC sind vergleichbar mit den in der Literatur bezüglich einkristalliner Superlegierungen mit höheren gamma'-Volumenanteilen beschriebenen. Beginnend bei Raumtemperatur treten mit steigender Temperatur folgende Mechanismen auf: Tieftemperatur-(LT-)Stapelfehler, Antiphasengrenzen-gekoppelte Versetzungspaare, Hochtemperatur-(HT-)Stapelfehler und Orowan-Ringe um die gaama'-Teilchen. Das Fließspannungsminimum des IN738LC bei 450 °C kann einem Wechsel im Verformungsmechanismus zugeordnet werden. Die Mechanismenwechsel finden bei SC16 bei höheren Temperaturen statt als bei IN738LC. Von Raumtemperatur bis 750 °C wird bei IN738LC im LCF-Bereich bei out-of-phase-Versuchen eine zusätzliche zyklische Verfestigung beobachtet, die ihr Maximum bei 450 °C hat. Bei dieser Temperatur wird die plastische Verformung durch a/2<110>-Versetzungspaare erzeugt, die die gaama'-Phase parallel zu {111} schneiden. Während der out-of-phase-Versuche werden zusätzliche Gleitsysteme auf verschiedenen {111}-Ebenen aktiviert, was zu einer erhöhten Dichte von unbeweglichen Versetzungen führt. Bei höheren Temperaturen können Versetzungen gaama'-Teilchen und andere Hindernisse durch Quergleiten und Klettern umgehen. Beim SC16 lassen sich LT- (bis 750 °C) und HT-Bruchverhalten (ab 750 °C) klar unterscheiden. Ersteres zeigt sich in großflächigem Abscheren und Bruchinitiierung an der Probenoberfläche. Der HT-Bruch wird an Poren im Innern initiiert und führt zu einem "Teller-Tasse"-Bruch mit einer ringförmigen Scherlippe im äußeren Bereich. Beim IN738LC hingegen treten die beim SC16 gefundenen Elemente in den Bruchflächen nur in untergeordneter Weise hervor. Der Rissverlauf ist fast immer interdendritisch und nur zum Teil transkristallin. Primärkarbide werden im LT-Bereich gespalten, im HT-Bereich abgelöst. Minima der Temperaturabhängigkeit der Bruchdehnung des IN738LC gehen jeweils mit lokalisierter Gleitung in einzelnen Gleitbändern einher. Immer wenn bei einer bestimmten Temperatur ein neuer Verformungsmechanismus einzusetzen beginnt, werden inhomogene Gleitverteilungen beobachtet, die zu einer geringen Verformbarkeit führen. KW - Nickelbasis KW - Versetzung KW - TEM PY - 1997 SN - 978-3-89574-242-2 SN - 3-89574-242-2 SP - 1 EP - 142 PB - Verlag Dr. Köster CY - Berlin AN - OPUS4-38194 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias A1 - Wolff, Dietmar A1 - Stark, Wolfgang T1 - Tieftemperaturverhalten von Elastomerdichtungen - Eigenschaftsbestimmung für den Einsatz in Transport- und Lagerbehältern für radioaktive Stoffe N2 - Die Messung des dynamischen Speichermoduls mit der Dynamisch-Mechanischen-Analyse ermöglicht einen schnellen Überblick über das temperaturabhängige Verhalten von elastomeren Dichtungsmaterialien. Ein direkter Rückschluss von der so ermittelten Glasübergangstemperatur Tg auf die Versagenstemperatur einer Dichtung ist aber ohne zusätzliche Messungen bisher nicht möglich. Mit den Ergebnissen des Druckverformungsrestes DVR und des DVRDMA ist eine ge-nauere Beschreibung der Tieftemperatureigenschaften und dadurch der Funktion von elastomeren Dichtungsmaterialien möglich. Messungen ergeben beispielsweise, dass sich das EPDM bei einer Temperatur von -40 °C laut der Dynamisch Mechanischen Analyse noch im gummielastischen Bereich befindet. Die DVRDMA-Werte zeigen eine Rückstellung um mehr als 40 % der Ausgangsdeformation in wenigen Minuten. Mit derart detailliert bestimmten Eigenschaften lassen sich Rückschlüsse auf einsatzspezifische Anforderungen wie z. B. die Dichtwirkung in Abhängigkeit von Betriebstemperatur und mechanischer Belastungsgeschwindigkeit ziehen, so dass je nach Einsatzbedingungen für die Dichtungen eine geeignete Materialauswahl getrof-fen werden kann. T2 - Jahrestagung Kerntechnik 2010 CY - Berlin, Deutschland DA - 2010-05-04 KW - Dichtungen KW - Elastomere KW - Tieftemperaturverhalten PY - 2010 IS - Sektion 5 / 503 SP - 1 EP - 4 CY - Berlin AN - OPUS4-21272 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Beygi Nasrabadi, Hossein A1 - Bauer, Felix A1 - Uhlemann, Patrick A1 - Rehmer, Birgit A1 - Skrotzki, Birgit T1 - KupferDigital mechanical testing datasets: Stress relaxation and low-cycle fatigue (LCF) tests N2 - The KupferDigital project deals with the development of a data ecosystem for digital materials research on the basis of ontology-based digital representations of copper and copper alloys. This document provides exemplary mechanical testing datasets for training the developed KupferDigital infrastructures. Different types of cast copper alloys were provided for this research and their mechanical testing (stress relaxation and low-cycle fatigue) was performed in the accredited materials testing laboratory, while the test results were reported according to the DIN/ISO standards and attached with the maximum possible metadata about the sample history, equipment, and calibration. The attached content file consisted of the obtained primary raw testing data as well as the secondary datasets of these tests containing the detailed metadata of mechanical testing methods. Such test data files are processed by the KupferDigital digital tools to be converted to standardized machine-readable data files. KW - Copper alloys KW - Dataset KW - Stress relaxation KW - Mechanical testing KW - Low-cycle fatigue. PY - 2024 DO - https://doi.org/10.5281/zenodo.10820437 PB - Zenodo CY - Geneva AN - OPUS4-59665 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias A1 - Grelle, T. A1 - Wolff, Dietmar T1 - Influences on the low temperature sealability of elastomer O-rings N2 - For many sealing applications rubbers are applied due to their special material properties and easy use. In many applications, e.g. in aviation, traffic or process technology the material can be exposed to low temperatures during Operation. Therefore it is important to know the material behaviour at those low temperatures to determine the temperature range that allows a safe Operation of the seal. As rubbers are used as main sealing materials for Containers for low and intermediate level radioactive waste and as additional component to metal seals in spent fuel and high active waste Containers, a comprehensive elastomer investigation program is run at BAM. This program comprises investigations of elastomer overall performance, durability, influence of gamma irradiation and low temperature behaviour. In this paper we focus on the behaviour of elastomer seals at low temperatures with regard to potential decrease of leak-tightness as material properties of rubbers are strongly temperature dependent. But additionally to the investigation presented in the past which considered the material properties of new materials and the seal behaviour under purely static conditions [1, 2] we now focus on irradiated materials and on the sealing performance after a fast partial release of the compressed seal. For the investigations different materials were used, e.g. fluorocarbon (FKM) and ethylenepropylene-diene (EPDM) rubber. To determine the effect of gamma irradiation some samples were irradiated and studied by several thermo-analytical methods and compression set. For the investigation of the seal performance under non static conditions we decided to design a new measurement setup which allows for a small flange deflection and simultaneous leakage rate measurement at low temperatures. T2 - IRC 2015 - International rubber conference CY - Nuremberg, Germany DA - 29.06.2015 KW - O-ring KW - Glass-rubber transition KW - Irradiation KW - Compression set PY - 2015 SP - 1 EP - 7 AN - OPUS4-33784 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bismarck, Marck A1 - Skrotzki, Birgit A1 - Olbricht, Jürgen T1 - Size effects in miniature specimen creep testing of P91 N2 - The use of miniaturized specimen geometries in mechanical testing allows extracting the sample material directly from critical components of power plants like e.g. headers and pipes. In this way, both the impacts of the manufacture of the component (including all shaping and tempering influences) and of the complex aging/loading/oxidation conditions during Service can be analyzed and representative mechanical properties are obtained. In the present study, example results of a comparative creep and creep rupture study on P91 tempered martensite ferritic Steel, involving Standard and miniature specimens that were all taken from one batch of material, are presented. Cylindrical creep specimens with a minimum gauge length diameter of 3 mm were used, representing the smallest recommended test geometry of ISO 204. The test results of miniature specimens exhibit all characteristic creep features of tempered martensite ferritic steels, and analysis of the stress and temperature dependence of creep results in values that correspond well to literature data for P91. However, direct comparison with large scale specimen data reveals small but systematic variations in minimum creep rates, elongations at fracture and times to rupture. In our contribution, these differences are discussed in the light of literature findings on specimen size influences in other heat resistant alloys. Size effects need to be considered for a correct interpretation of results from miniature specimen creep tests. T2 - 3rd International ECCC Conference CY - Rom, Italy DA - 05.05.2014 KW - Material PY - 2017 SN - 978-88-7484-510-1 SP - 430 EP - 435 PB - Tipography Inail CY - Milan AN - OPUS4-41239 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Beygi Nasrabadi, Hossein A1 - Skrotzki, Birgit A1 - Hanke, Thomas A1 - Chen, Yue T1 - Brinell test ontology (BTO) N2 - Brinell Test Ontology (BTO) has developed for representing the Brinell testing process, testing equipment requirements, test pieces charactristics, and related testing parameters and their measurement procedure according to DIN EN ISO 6506-1 standard. Versions info: V2 developed using BFO+CCO top-level ontologies. V3 developed using EMMO+CHAMEO top-level ontologies. V4 developed using PROVO+PMDco top-level ontologies. V5 developed using BFO+IOF top-level ontologies. Repositories: GitLab: https://gitlab.com/kupferdigital/process-graphs/brinell-hardness-test GitHub: https://github.com/HosseinBeygiNasrabadi/Brinell-Test-Ontology-BTO- MatPortal: https://matportal.org/ontologies/BTO IndustryPortal: https://industryportal.enit.fr/ontologies/BTO KW - Ontology KW - Knowledge graph KW - Data mapping KW - Brinell hardness KW - FAIR data PY - 2024 UR - https://gitlab.com/kupferdigital/process-graphs/brinell-hardness-test UR - https://github.com/HosseinBeygiNasrabadi/Brinell-Test-Ontology-BTO- UR - https://matportal.org/ontologies/BTO UR - https://industryportal.enit.fr/ontologies/BTO PB - GitLab CY - San Francisco, CA, USA AN - OPUS4-60543 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Butz, Adam A1 - Fedelich, Bernard A1 - Rehmer, Birgit A1 - Skrotzki, Birgit A1 - Schmitz, Sebastian ED - Moninger, G. T1 - Risserkennung an Bohrlochproben: Numerische Voruntersuchung für eine neuartige Methode zur Rissformerkennung T1 - Crack Detection on Borehole Specimens: Numerical pre-examination for a novel crack shape detection method N2 - Es konnte anhand einer numerischen Voruntersuchung gezeigt werden, dass anhand der kombinierten Auswertung der im Versuch verwendeten Sensorik eine Einteilung der unter Ermüdung in Bohrlochproben auftretenden Rissformen in verschiedene Hauptkategorien (Eckriss, Oberflächenriss, Durchgangsriss) möglich ist. N2 - When fatigued specimens with a hole are to be investigated regarding crack growth, it may be the case that the shape of the crack can’t be identified with sufficient certainty. If marking the fracture surface e.g. using beach marks is not possible, a method is required that nevertheless allows for the determination of the crack shape in order to calculate the corresponding fracture mechanics parameters. This paper describes a numerical pre-study for a method that allows for the classification of cracks in a sample featuring a drill hole into one of three crack shape classes based on the combined evaluation of various types of test data. T2 - Tagung Werkstoffprüfung 2018 CY - Bad Neuenahr, Germany DA - 06.12.2018 KW - Crack KW - LCF KW - Data Fusion KW - Risse KW - Rissform KW - Datenfusion PY - 2018 VL - 2018 SP - 249 EP - 254 AN - OPUS4-46976 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zaghdoudi, Maha A1 - Weber, Mike A1 - Kömmling, Anja A1 - Jaunich, Matthias A1 - Wolff, Dietmar T1 - Simulation of compression set of epdm o-rings during aging N2 - It is common practice in the application of finite element analysis to model compression set (CS) of elastomers during aging with two different material models according to the two-network theory of Tobolsky. The theory relies on the existence of two networks. The first one represents the original network after vulcanization and is sensitive to chain scission. The second network accounts for the formation of additional crosslinking during aging. Besides the use of user subroutines to describe the two-network model, an element overlay technique is also needed as the full set of both material behaviors did not exist for assignment to a single element. This element overlay technique is valuable for research and developmental purposes but makes extension to industrial usage quite challenging. Our goal is to simulate the CS of elastomers after long-term aging in a commercial finite element software with no need for extra subroutine codes or mesh superposition. Ethylene propylene diene (EPDM) O-rings were aged in a compressed state at 75 °C, 100 °C, 125 °C and 150 °C for up to 183 days. Investigations of the experimental test results were used to identify material models and their parameters to develop a finite element model to simulate CS. The model was implemented in the finite element software ABAQUS/Standard® with a sequential temperature-displacement coupling. Regarding the influence of temperature, the Arrhenius equation is adopted for the time-temperature relationship. The activation energy value that is required for the simulation is firstly determined from shifting the experimental CS results with the time-temperature superposition technique and plotting the shift factors in an Arrhenius diagram. The experiments were compared with the simulation results. Afterwards different activation energies were used in the simulation and discussed. A suitable choice of the activation energy value with regard to the reference temperature and the test temperature is presented. With the chosen activation energies, the match between numerical CS values after long-term aging and the experimental results was improved. T2 - ASME 2022 Pressure Vessels & Piping Conference CY - Las Vegas, USA DA - 17.07.2022 KW - Simulation KW - Compression set KW - EPDM KW - Aging PY - 2022 SP - 1 EP - 9 AN - OPUS4-57370 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hodoroaba, Vasile-Dan A1 - Hörenz, Christoph T1 - Improving nanoparticle size measurement accuracy for safety assessment N2 - Nanomaterials and nanoparticles are finding applications across a wide range of technology sectors, from medicine and food to transportation and construction. In order to assess these new materials for potential risks to health and the environment, they need to be well-characterised. The measurement of constituent nanoparticle size, shape, and size distribution are important factors for the risk evaluation process. EMPIR project Improved traceability chain of nanoparticle size measurements (17NRM04, nPSize) is working to assess a range of traceable nanoparticle measurement approaches, including Scanning Electron Microscopy (also in Transmission Mode), Atomic Force Microscopy and Small Angle X-ray Scattering, and deliver improved calibration methods to users. For the techniques under investigation, physical models of their response to a range of nanoparticle types are developed. Validated reference materials will also be used for an inter-comparison of measurement systems, with an evaluation of the associated measurement uncertainty. With project contributions to standards development work, manufacturers will be better placed to assess the human and environmental risks posed by nanomaterials across a whole range of products. KW - Nanoparticles KW - Particle size distribution KW - Traceability KW - Electron microscopy KW - AFM KW - SAXS PY - 2021 UR - https://www.euramet.org/?L=0&news=40%3A1159 SP - 1 PB - EURAMET e.V. CY - Braunschweig AN - OPUS4-52129 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Han, Ying A1 - Schriever, Sina A1 - von Hartrott, Philipp A1 - Rockenhäuser, Christian A1 - Skrotzki, Birgit T1 - Dataset on the Creep Properties of EN AW-2618A Aluminum Alloy in the T61 and an overaged condition N2 - This publication contains comprehensive metadata and test results of constant force creep tests according to DIN EN ISO 204 on the aluminum alloy EN AW-2618A in the T61 condition (8 h/530 °C/quenching in boiling water followed by 28 h/195 °C/air cooling) and in an overaged condition (T61 + 1.000 h/190 °C). The test temperatures cover 160 °C, 180 °C, 190 °C, and 230 °C, and the initial stresses range between 40 MPa and 290 MPa. KW - Creep KW - Aging KW - Overaging KW - Aluminum alloy KW - EN AW-2618A KW - High temperature PY - 2025 DO - https://doi.org/10.5281/zenodo.15744297 PB - Zenodo CY - Geneva AN - OPUS4-63572 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rockenhäuser, Christian A1 - Skrotzki, Birgit A1 - Karlin, J. A1 - Von Hartrott, P. T1 - Lebensdauerberechnung von Aluminium-Radialverdichterrädern unter Berücksichtigung der Werkstoffalterung [Zwischenbericht über das Vorhaben Nr. 1172 (IGF-Nr. 17734)] N2 - Aluminiumlegierungen mit besonders hoher Festigkeit werden vor allem in der Luft- und Raumfahrt sowie der Automobilindustrie eingesetzt. Ein Anwendungsbeispiel im Fahrzeugbereich sind Radialverdichterräder von Abgasturboladern. Der hierfür untersuchte Werkstoff ist die Legierung 2618A. Die hohe Festigkeit wird durch Ausscheidungshärtung erreicht. Es scheiden sich hierbei durch eine entsprechende Wärmebehandlung Al-Cu-Mg-Teilchen in die Aluminium-Matrix aus. Diese Teilchen stellen Hindernisse für die Bewegung von Versetzungen dar und haben im Fall der Legierung 2618A stabförmige Geometrie. Durch Einsatz bei Betriebstemperatur von etwa 160 °C bis 190 °C vergröbern die Teilchen im Verlauf der Einsatzzeit (Ostwaldreifung) und die Festigkeit nimmt ab. Der Zwischenbericht soll einen Überblick über die bisherigen experimentellen und theoretischen Ergebnisse geben. Es konnten Brinell-Härteverläufe nach Auslagerung bei 160 °C, 180 °C und 190 °C bis 8.760 h Auslagerungszeit gemessen werden. Erste TEM (Transmissionselektronenmikroskopie )-Untersuchungen der Mikrostruktur liegen vor. Anhand dieser Untersuchungen wurden erste Simulationen und Berechnungen der AI-Cu-Mg-Teilchengrößenentwicklung (Vergröberung) durchgeführt. Auswirkungen dieser Vergröberung der AlCu-Mg-Teilchen auf die Fließgrenze bei Raumtemperatur wurden berechnet. Weitere Ergebnisse sind Kriechversuche an Proben im Ausgangszustand T61 der Legierung 2618A bei den Temperaturen 160 °C, 180 °C und 190 °C. Um das zyklische visko-plastische Verhalten des Werkstoffes und den Einfluss der Alterung zu untersuchen, wurden LCF-Ermüdungsversuche an verschiedenen Auslagerungszuständen durchgeführt. T2 - Herbsttagung 2015 Turbomaschinen CY - Würzburg, Germany DA - 29.09.2015 KW - Aluminium alloys KW - Transmission electron microscopy KW - Microstructure KW - Coarsening PY - 2015 IS - R573 SP - 37 EP - 69 AN - OPUS4-34480 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schicker, Johannes A1 - Sievert, Rainer A1 - Fedelich, Bernard A1 - Noack, Hans-Dieter A1 - Matzak, Kathrin A1 - Kazak, Fedor A1 - Kühn, Hans-Joachim A1 - Klingelhöffer, Hellmuth A1 - Skrotzki, Birgit T1 - Entwicklung von Rechenmodellen zur Lebensdauervorhersage von Werkstoffen für Abgasturbolader-Heißteile unter thermo-mechanischer Ermüdungsbeanspruchung und Übertragung für Anwendung auf Bauteile PY - 2008 IS - R 542 SP - 5 EP - 29 CY - Frankfurt am Main AN - OPUS4-18954 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grelle, Tobias A1 - Wolff, Dietmar A1 - Probst, Ulrich A1 - Jaunich, Matthias A1 - Völzke, Holger T1 - Investigation of the time and temperature dependent behavior of metal seals in radioactive waste containers N2 - The Bundesanstalt für Materialforschung und –Prüfung (BAM) runs an investigation program on the long-term behavior of multi-component metal seals. Such seals are used in a wide area of applications including transport and storage casks for spent nuclear fuel and high level radioactive waste. The seal function is mainly based on the compression of the inner helical spring, which generates the necessary seal force to keep the sealing surfaces in close contact. This in turn leads to a plastic deformation of the outer jacket of the seal, comprised of highly ductile aluminum or silver that adapts to the sealing surfaces of cask body and bolted lid, thus providing high Level leak tightness. In Germany, those casks are licensed for Interim storage periods of up to 40 years or more if extended Interim storage would become necessary before a final repository is available. Thus, the sealing performance has to be evaluated, including factors like elevated temperature due to decay heat or mechanical loads due to transport under normal as well as accident conditions. Long-term investigations at BAM have been running over the last nine years to identify and evaluate the seal performance by measuring the remaining seal force, the useable resilience and the leakage rate after various time intervals at temperatures ranging from room temperature up to 150 °C. It was found that the seal force and useable resilience decrease with time and temperature, caused by creep deformation of the outer jacket. In order to obtain an analytical description for the seal behavior and to achieve more information on the material behavior under application conditions a comprehensive investigation program with Focus on aluminum as outer jacket material was launched. The program includes material investigations such as compression and tension creep tests with representative basic materials. An additional test setup allows for the continuous measurement of the remaining seal force at temperatures of up to 150 °C. Furthermore, seal segments are compressed and stored in heating chambers, thus producing segments at different stages of the aging process. The segments are investigated regarding the development of the contact area width, jacket thickness and microstructural changes. This data will be used to develop material models and an analytical description of the time and temperature dependent long-term sealing behavior. This paper explains the current status of gained test results and modelling approaches and closes with an outlook to the future Project plans. T2 - ASME 2018 Pressure Vessels and Piping Conference CY - Prague, Czech Republic DA - 15.07.2018 KW - Metal seal KW - Creep KW - Long-term behavior PY - 2018 SP - PVP2018-84584, 1 EP - 6 AN - OPUS4-46110 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Beygi Nasrabadi, Hossein A1 - Bauer, Felix A1 - Tikana, Ladji A1 - Uhlemann, Patrick A1 - Thärig, Steffen A1 - Rehmer, Birgit A1 - Skrotzki, Birgit T1 - KupferDigital mechanical testing datasets N2 - The KupferDigital project aims to develop digital methods, tools, and data space infrastructures for digitalizing the entire life cycle of copper materials. The mechanical testing process is one of the main chains of such life cycles which generates lots of important testing data about the mechanical properties of the materials and their related materials and testing metadata. To train the digitalization of the mechanical testing process, different kinds of copper alloys were provided for this project, and their mechanical properties were measured by typical methods like Brinell and Vickers hardness and tensile testing. The primary raw testing data as well as the secondary datasets of these tests are provided. The detailed materials specifications, the utilized mechanical testing methods, and provided datasets are described in the content file. The test data files of heterogeneous structures are processed by the KupferDigital digital tools to be converted to standardized machine-readable data files. KW - Copper alloys KW - Dataset KW - Tensile testing KW - Mechanical testing KW - Hardness test PY - 2023 DO - https://doi.org/10.5281/zenodo.7670582 PB - Zenodo CY - Geneva AN - OPUS4-57038 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hodoroaba, Vasile-Dan T1 - Report on the Round Robin Exercise - Coated Materials T2 - Final General Meeting of the EU-GDS Network CY - Wiener Neustadt, Austria DA - 2002-03-02 PY - 2002 AN - OPUS4-1468 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jürgens, Maria A1 - Fedelich, Bernard A1 - Olbricht, Jürgen A1 - Skrotzki, Birgit T1 - Thermo-mechanical fatigue behavior of P91/P92 N2 - 9-12% Cr ferritic-martensitic stainless steels are widely used as high temperature construction materials in power plants due to their excellent creep resistance and good oxidation resistance. Creep resistance is considered as the primary parameter in material selection for base-load power plants, but the growing share of renewable energy sources in power generation forces many installations into more "flexible" operation with frequent load reductions and shutdowns. Under cyclic operation of power plants, temperature gradients occur especially in thick-walled components. Locally, these gradients lead to complex time- and temperature-dependent loading scenarios which may result in superimposed creep deformation/damage, creep-fatigue and thermo-mechanical fatigue. The combination of different damage processes may seriously reduce the lifetimes of respective components. A fundamental understanding of the damage evolution in ferritic-martensitic steels under combined static and cyclic loading is therefore required. In the present contribution, the thermo-mechanical fatigue and creep-fatigue behavior of two different 9% Cr steel grades (P91 and P92) was investigated. Standard LCF/TMF-tests as well as near-service loading tests with different hold times have been carried out to study the material behavior of the new loading scenarios. Microstructural investigations help to identify the observed deformation characteristics (like e.g. pronounced softening) and the dominating damage mechanisms under different loads. The test programme is complemented by selected tests on service-aged material which demonstrate possible reactions of older components in existing plants to changes in operation profiles. In a next step, the experimental results will be used for parameter identification of a deformation and lifetime model to predict the material behavior. T2 - LCF08 CY - Dresden, Germany DA - 27.06.2017 KW - Near-service testing KW - Power plant KW - Ferritic-martensitic steels KW - P91 KW - P92 KW - Thermo-Mechanical Fatigue PY - 2017 SN - 978-3-9814516-5-8 VL - 2017 SP - 101 EP - 105 PB - DVM CY - Berlin AN - OPUS4-42268 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sagradov, Ilja T1 - Long-term tests on metal seals using continuous force measurement in compressed state N2 - In Germany, spent fuel and heat generating radioactive waste is stored in casks for transport and storage (DPCs). The storage licenses were granted for up to 40 years. Due to the delay in identifying a final repository site for such radioactive waste, the storage periods are to be extended significantly. The objective of our research work is to collect additional material data for metal seals in order to be able to better assess the long-term safety of the sealing system of the casks for a period of up to 100 years. A principal safety consideration for the DPCs is the long-term performance of bolted lid sealing systems utilizing metal seals to ensure the safe enclosure of the radioactive inventory during interim storage. To assess the sealing behavior, it is necessary to examine the aging-dependent residual restoring force for the metal seals and the usable resilience. By investigating the change in these values as a function of time and temperature, further insight can be gained into the assessment of long-term safety for extended interim storage. In the present study, the restoring force of metal seals with an outer aluminum jacket and a torus diameter of 9.9 mm was measured continuously. For this purpose, a specially designed device equipped with a load cell was used under isothermal conditions. As part of the investigation, the level and rate of decrease of the restoring seal force were recorded over test periods of one and two months. The seal temperature was set to 35 °C, 75 °C, 100 °C, 125 °C, and 150 °C, respectively. A direct correlation was observed between the temperature of the seal, the level of the restoring force after compressing and heating the seal, and the drop-off characteristics of the restoring force. It was found that in our test device the force level immediately after reaching the respective temperature is lower for higher seal temperatures, while the drop rate of the restoring force is higher. This paper describes the experimental setting and discusses first results in comparison with our long-term discontinuous measurements. T2 - 21st International Symposium on the Packaging and Transportation of Radioactive Materials - PATRAM 2025 CY - San Antonio, TX, USA DA - 27.07.2025 KW - Long-Term Safety Assessment KW - Extended Interim Storage KW - Metal Seal Aging KW - Restoring Force Degradation KW - Temperature-Dependent Performance PY - 2025 VL - 2025 SP - 1 EP - 10 CY - Indianapolis, IN, USA AN - OPUS4-63881 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Radners, J. A1 - Han, Ying A1 - von Hartrott, P. A1 - Skrotzki, Birgit T1 - Aluminium Hochtemperaturermüdung N2 - Die hohen Betriebstemperaturen während des Einsatzes von Radialverdichterrädern in Abgasturboladern führen zu einer Änderung der ursprünglich eingestellten Mikrostruktur in der warmfesten Aluminiumlegierung EN AW-2618A (Überalterung). Grund dafür sind thermische Belastungen, die nahe der Aushärtetemperatur liegen und diese kurzzeitig sogar überschreiten können. Die Alterungsmechanismen wurden zusammen mit den Themen niederzyklische (LCF) und thermomechanische Ermüdung (TMF) sowie Kriechen bis max. 190 °C in vorangegangenen Forschungsvorhaben untersucht. Kaum untersucht war bisher das Verhalten der Legierung unter hochzyklischer Beanspruchung (HCF) sowie der Einfluss von Kerben und Lastkollektiven. Da zukünftig mit weiter steigenden Betriebstemperaturen für Radialverdichter zu rechnen ist, wurde in diesem Forschungsvorhaben das HCF-Verhalten bei 230 °C untersucht und somit bei einer Prüftemperatur, die deutlich oberhalb der Aushärtetemperatur liegt. Das Ziel des Projektes war der Aufbau einer geeigneten experimentellen Datenbasis, das Verständnis der relevanten mikrostrukturellen Prozesse sowie die Weiterentwicklung und Anpassung geeigneter Modelle und Bewertungsmethoden. Das experimentelle Untersuchungsprogramm umfasste neben einer Basischarakterisierung des HCF-Verhaltens am Ausgangszustand T61 gezielte mechanische Versuche zur Isolierung der Einflussfakto-ren Mittelspannung (𝑅 = −1, 𝑅 = 0,1), Werkstoffüberalterung (T61, 10 h/230 °C, 1000 h/230 °C), Prüftemperatur (20 °C, 230 °C), Prüffrequenz (0,2 Hz, 20 Hz) sowie Kerbwirkung und variable Amplituden. Darauf aufbauend wurden die in den vorangegangenen Projekten entwickelten Modelle und Bewertungsmethoden angepasst und weiterentwickelt, um die genannten thermischen und mechanischen Belastungen in der Lebensdauerbewertung abzubilden. KW - HCF KW - Aluminium KW - EN AW-2618A KW - Ermüdung PY - 2023 SP - 1 EP - 111 CY - Frankfurt am Main AN - OPUS4-57850 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wolff, Dietmar A1 - Jaunich, Matthias A1 - Probst, Ulrich A1 - Nagelschmidt, Sven T1 - Understanding the long-term behavior of sealing systems and neutron shielding material for extended dry cask storage N2 - In Germany, the concept of dry interim storage in dual purpose metal casks before disposal is being pursued for spent nuclear fuel (SF) and high active waste (HAW) management. However, since there is no repository available today, the initially planned and established dry interim storage license duration of up to 40 years will be too short and its extension will become necessary. For such a storage license extension it is required to assess the long-term performance of SF and all safety related storage system components in order to confirm the viability of extended storage. The main safety relevant components are the thick-walled dual purpose metal casks. These casks consist of a monolithic cask body with integrated neutron shielding components (polymers, e.g. polyethylene) and a monitored double lid barrier system with metal and elastomeric seals. The metal seals of this bolted closure system guarantee the required leak-tightness whereas the elastomeric seals allow for leakage rate measurement of the metal seals. This paper presents an update on running long-term tests on metal seals at different temperatures under static conditions over longer periods of time. In addition, first results of our approach to understand the aging behavior of different elastomeric seals and neutron radiation shielding material polyethylene are discussed. T2 - PSAM 12 - Probabilistic safety assessment and management CY - Honolulu, Hawaii, USA DA - 22.06.2014 KW - Extended storage KW - Dual purpose casks KW - Metal seals KW - Elastomeric seals KW - Neutron shielding material PY - 2014 SP - 1 EP - 9 AN - OPUS4-32072 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Schicker, Johannes A1 - Sievert, Rainer A1 - Fedelich, Bernard A1 - Noack, Hans-Dieter A1 - Kazak, Fedor A1 - Matzak, Kathrin A1 - Kühn, Hans-Joachim A1 - Klingelhöffer, Hellmuth A1 - Skrotzki, Birgit T1 - TMF Lebensdauerberechnung ATL-Heißteile - Entwicklung von Rechenmodellen zur Lebensdauervorhersage von Werkstoffen für Abgasturbolader-Heißteile unter thermomechanischer Ermüdungsbeanspruchung und Übertragung für Anwendung auf Bauteile PY - 2010 IS - 902 SP - 1 EP - 156 CY - Frankfurt am Main AN - OPUS4-20931 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Liu, Yung A1 - Völzke, Holger A1 - Zencker, Uwe A1 - Jaunich, Matthias T1 - Cooperation in Advanced Technologies Associated with the Back End of Nuclear Fuel Cycle N2 - A Memorandum of Understanding (MOU) between Argonne National Laboratory (Argonne) and the German Bundesanstalt für Materialforschung und -prüfung (BAM) was signed in October 2014. Its objectives are to promote cooperation among scientists and specialists at Argonne and BAM and establish a framework for collaboration in advanced technologies associated with the back end of the nuclear fuel cycle. Collaborative activities involving Argonne and BAM may be implemented through the promotion of joint research activities and scientific workshops and conferences; exchange of technical information; and visits by scientists, specialists, and graduate, postgraduate, and Ph.D. students. The MOU was renewed in January 2020 for another five years. Highlights of the progress and achievements are provided in identified topical areas for collaboration on ageing management guidance, storage, transportation and disposal R&D, joint conference activities, and conclude with the benefits of the MOU in fostering Argonne and BAM collaboration. T2 - 26th International Conference on Structural Mechanics in Reactor Technology - SMiRT 26 CY - Potsdam, Germany DA - 10.07.2022 KW - Nuclear fuel cycle KW - Back end KW - Spent fuel performance KW - Storage KW - Transportation PY - 2022 SP - 1 EP - 10 AN - OPUS4-55861 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - von der Ehe, Kerstin A1 - Jaunich, Matthias A1 - Wolff, Dietmar T1 - UHMW-PE - a shielding material with special properties influenced by radiation N2 - Ultra high molecular weight polyethylene (UHMW-PE) - due to its high hydrogen content - is used as neutron shielding material in casks for storage and transport of radioactive materials. Besides this, UHMW-PE - as a high-performance polymer - has been used for several years in medical technology due to its excellent slip and wear properties. Due to the special properties of UHMW-PE which result basically from its extreme chain lengths and its high degree of crystallinity, it is predestinated for the aforementioned applications. In both cases, irradiation and its impact on the molecular structure of polyethylene play an important role. In the first case, irradiation exists as a by-product of inserting the radioactive material in the cask. Hence PE has to withstand any type of degradation affecting safety relevant aspects to be applicable for long term radiation shielding purposes for instance over a period of 40 years. In the second case irradiation is applied deliberately for purposes such as sterilization and crosslinking, leading to partial improvement of the mechanical properties (e.g. fracture toughness, crack propagation resistance, wear resistance) and better Chemical stability. Specifically concerning their use in the field of medical technology, different types of UHMW-PE have been objects of numerous publications. It is generally accepted that two parallel and competitive processes, based on chain scission and reactions of Ccentered radicals and molecular fragments, occur in PE as a consequence of radiation: radical recombination accounts for crosslinking, together with some disproportionation, formation of low molecular weight fragments, and recrystallization. Furthermore, formation of oxygenated structures in the presence of traces of oxygen is an antagonist of the C-centered radicals. Radiation induced scission preferentially takes place in the amorphous phase and noncrystalline surface of the crystals. It is followed by folding of molecular fragments, crystallinity growth and increased perfection in the crystal lamellae [4, 5]. Chain scission results in shorter polymer molecules, fewer entanglements, and consequently, increased molecular mobility. The scope of our investigation comprises an estimation of the radiation and thermal impact on the molecular and supra molecular structure of the two types of PE used for neutron shielding cask components. A further point which is worth to explore is to what extent these changes are detectable by thermo-analytical (TA) methods, such as Differential Scanning Calorimetry (DSC), Thermo Mechanical Analysis (TMA), Dynamic Mechanical Analysis (DMA) and Thermogravimetry (TG). Additionally FT-IR and solubility measurements have been performed. In our studies we focused on the UHMW-PE material GUR 4120 which was y irradiated at RT and compared to the untreated material. T2 - Jahrestagung Kerntechnik 2011 CY - Berlin, Germany DA - 17.05.2011 PY - 2011 SP - 1 EP - 5 AN - OPUS4-24620 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Beygi Nasrabadi, Hossein A1 - Skrotzki, Birgit A1 - Hanke, Thomas A1 - Eisenbart, Miriam T1 - Mechanical testing ontology (MTO) N2 - The materials mechanical testing ontology (MTO) was developed by collecting the mechanical testing vocabulary from ISO 23718 standard, as well as the standardized testing processes described for various mechanical testing of materials like tensile testing, Brinell hardness test, Vickers hardness test, stress relaxation test, and fatigue testing. Versions info: V2 developed using BFO+CCO top-level ontologies. V3 developed using PROVO+PMDco top-level ontologies. V4 developed using BFO+IOF top-level ontologies. Repositories: GitLab: https://gitlab.com/kupferdigital/ontologies/mechanical-testing-ontology GitHub: https://github.com/HosseinBeygiNasrabadi/Mechanical-Testing-Ontology MatPortal: https://matportal.org/ontologies/MTO IndustryPortal: https://industryportal.enit.fr/ontologies/MTO KW - Ontology KW - Mechanical testing KW - FAIR data PY - 2023 UR - https://gitlab.com/kupferdigital/ontologies/mechanical-testing-ontology/ PB - GitLab CY - San Francisco, CA, USA AN - OPUS4-58271 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Radners, Jan A1 - Han, Ying A1 - von Hartrott, Philipp A1 - Skrotzki, Birgit T1 - Aluminum High Temperature Fatigue N2 - The high operating temperatures of radial compressor wheels in exhaust gas turbochargers lead to a change in the original microstructure of the heat-resistant aluminum alloy EN AW-2618A (overaging). This is caused by thermal loads that are close to the age hardening temperature and can even exceed it for a short time. The aging mechanisms have been investigated together with low cycle fatigue (LCF), thermomechanical fatigue (TMF) and creep up to max. 190 °C in previous research projects. The be-havior of the alloy under high cycle fatigue (HCF) and the influence of load spectra have hardly been investigated. Since the operating temperatures of centrifugal compressors are expected to increase in the future, this research project investigated the HCF behavior at 230 °C, a test temperature significantly higher than the age hardening temperature. The objectives of the project were to establish a suitable experimental database, to understand the relevant microstructural processes, and to further develop and adapt suitable models and evaluation methods. In addition to a basic characterization of the HCF behavior in the initial condition T61, the experimental investigation program included targeted mechanical tests to isolate the influencing factors of mean stress (𝑅=−1, 𝑅=0.1), material overaging (T61, 10 h/230 °C, 1000 h/230 °C), test temperature (20 °C, 230 °C), test frequency (0.2 Hz, 20 Hz) as well as variable amplitudes. On this basis, the models and evaluation methods developed in the previous projects were adapted and further developed to reflect thermal and mechanical loads in the lifetime assessment. T2 - The FVV Transfer + Networking Event (Herbst 2023) CY - Würzburg, Germany DA - 04.10.2023 KW - Aluminum alloys KW - Fatigue KW - EN AW-2618A PY - 2023 SP - 1 EP - 30 AN - OPUS4-58562 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rehmer, Birgit A1 - Bayram, Faruk A1 - Ávila Calderón, Luis A1 - Mohr, Gunther A1 - Skrotzki, Birgit T1 - BAM reference data: Temperature-dependent Young's and shear modulus data for additively and conventionally manufactured variants of austenitic stainless steel AISI 316L N2 - The elastic properties (Young's modulus, shear modulus) of austenitic stainless steel AISI 316L were investigated between room temperature and 900 °C in an additively manufactured variant (laser powder bed fusion, PBF‑LB/M) and from a conventional process route (hot rolled sheet). The moduli were determined using the dynamic resonance method. The data set includes information on processing parameters, heat treatments, grain size, specimen dimensions and weight, Young’s and shear modulus as well as their measurement uncertainty. The dataset was generated in an accredited testing lab using calibrated measuring equipment. The calibrations meet the requirements of the test procedure and are metrologically traceable. The dataset was audited as BAM reference data. KW - Elastic modulus KW - Young's modulus KW - Shear modulus KW - Additive manufacturing KW - AISI 316L PY - 2023 DO - https://doi.org/10.5281/zenodo.7813835 PB - Zenodo CY - Geneva AN - OPUS4-57288 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - von Hartrott, P. A1 - Rockenhäuser, Christian A1 - Schriever, Sina A1 - Skrotzki, Birgit T1 - Correlation of the precipitate size evolution and the creep rate of the aluminium alloy EN AW 2618A at 190 °C N2 - A short description of the work done on the topic "Correlation of the precipitate size evolution and the creep rate of the aluminium alloy EN AW 2618A at 190 °C" is given. T2 - International Conference on Aluminium Alloys 16 CY - Montreal, Canada DA - 17.06.2018 KW - Alloy 2618A KW - Degradation KW - Aluminium KW - Creep KW - Coarsening PY - 2018 SN - 978-1-926872-41-4 SP - 99 AN - OPUS4-45284 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - von Hartrott, Philipp A1 - Skrotzki, Birgit T1 - Room temperature and elevated temperature tensile test and elastic properties data of Al-alloy EN AW-2618A after different aging times and temperatures N2 - The dataset contains two types of data: elastic properties (Young's and shear modulus, Poisson's ratio) between room temperature and 250 °C and a set of tensile tests at different aging times, aging temperatures, and test temperatures. KW - Aluminium alloy KW - Young's modulus KW - Shear modulus KW - Aging KW - Tensile test KW - Strength PY - 2023 UR - https://doi.org/10.5281/zenodo.10377164 DO - https://doi.org/10.5281/zenodo.10377163 PB - Zenodo CY - Geneva AN - OPUS4-59161 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Jürgens, Maria T1 - Verhalten des hochwarmfesten Stahles P92 unter zyklischen thermo-mechanischen Bedingungen in lastflexiblen Dampfkraftwerken N2 - Die Erzeugung von Erneuerbaren Energien unterliegt starken Schwankungen, die von konventionellen Kraftwerken ausgeglichen werden müssen, um das Stromnetz stabil zu halten. Für die konventionellen Kraftwerke bedeutet dies eine zunehmend zyklische Fahrweise, die zu häufigeren Last- und Temperaturwechseln führt. Von den eingesetzten Werkstoffen fehlen Daten zum Verhalten unter zyklischer Fahrweise. Ziel dieser Arbeit ist es daher, für P92, einen als Rohrleitungswerkstoff eingesetzten hochwarmfesten Stahl, zu untersuchen, welche Auswirkungen zyklische Fahrweisen auf die Schädigungsprozesse und Lebensdauern haben. Da durch den zyklischen Betrieb eine verstärkte Schädigung durch Ermüdungsprozesse zu erwarten ist, wurden dehnungskontrollierte isotherme (LCF) und nicht-isotherme (TMF) Ermüdungsversuche mit und ohne Haltezeit bei verschiedenen Temperaturen bzw. Temperaturintervallen durchgeführt. Mit den Haltezeitversuchen soll dabei das Kriech-Ermüdungs-Verhalten untersucht werden. Bei den TMF-Versuchen wurde zusätzlich die Temperaturrate variiert, um näher an den realen Lastwechselgeschwindigkeiten zu prüfen. Schließlich wurden auf Basis der durchgeführten LCF- und TMF-Versuche betriebsnahe Versuchsprozeduren entwickelt, um unterschiedliche Betriebsmodi in einem Versuch abzubilden. Die durchgeführten mechanischen Versuche stellen eine umfangreiche Basis zu Ermüdungsdaten an P92 dar. Neben der Abhängigkeit der Lebensdauer von Temperatur, Temperaturintervall und –rate, sowie Dehnung und Haltezeit, konnte auch das Entfestigungsverhalten genauer charakterisiert werden. Sowohl Haltezeiten als auch das Reduzieren der Temperaturrate können die Lebensdauer erheblich verringern. Dabei kommt es gerade bei vermeintlich kleinen Dehnungen, bei denen die Streckgrenze nur leicht überschritten wird, zu einer Lebensdauerreduzierung. Haltezeiten verstärken zudem die zyklische Entfestigung. Die fraktographische Analyse der Proben hat ergeben, dass es keinen direkten Zusammenhang zwischen der Entfestigung und der Bildung von Nebenrissen gibt. Stattdessen zeigen EBSD- und TEM-Untersuchungen, dass es zur Bildung einer Subkornstruktur kommt und die Entfestigung auf dem Verschwinden von Kleinwinkelkorngrenzen beruht. Während bei den LCF-Proben eine reine Ermüdungsschädigung vorliegt, konnte bei einigen TMF-Proben eine kriechdominierende Schädigung nachgewiesen werden. Die betriebsnahen Zyklen zeigen, dass sich mit den durchgeführten Versuchen das reale Betriebsverhalten gut abschätzen lässt. Da es jedoch auch Parameterkombinationen gibt, bei denen keine Änderung des Entfestigungs- und Lebensdauerverhaltens auftritt, sollte genau bekannt sein, welche Belastungen in einem Bauteil auftreten. KW - P92 KW - LCF KW - TMF KW - Energiewende KW - Kriechermüdung KW - Energy transition KW - Creep-fatigue PY - 2020 DO - https://doi.org/10.14279/depositonce-10538 SP - 1 EP - 144 CY - Berlin AN - OPUS4-51571 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hodoroaba, Vasile-Dan ED - Hodoroaba, Vasile-Dan T1 - Liaison Report from ISO/TC 202 'Microbeam Analysis' to ISO/TC 229 'Nanotechnologies' N2 - Liaison activities within ISO/TC 202 'Microbeam Analysis' which are relevant to ISO/TC 229 'Nanotechnologies' are reported acoording to the structure defined by ISO/TC229 Nanotechnologies Liaisons Coordination Group (NLCG): new standards/documents, coordination issues, and further detailed specific information, e.g. publications, events, comments. KW - ISO/TC 229 Nanotechnologies KW - ISO/TC 202 Microbeam Analysis KW - Standardisation PY - 2023 SP - 1 EP - 3 CY - ISO, Geneva, CH AN - OPUS4-58986 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rockenhäuser, Christian A1 - Skrotzki, Birgit T1 - Quantitative dark-field transmission electron microscopy of the microstructure evolution in a 2618A aluminum alloy during ageing N2 - Quantitative Dark-Field Transmission Electron Microscopy of the Microstructure Evolution in a 2618A Aluminum Alloy During Ageing was presented and discussed. T2 - Microscopy & Microanalysis 2016 CY - Columbus, OH, USA DA - 24.07.2016 KW - Aluminium alloys KW - Coarsening KW - Transmission electron microscopy KW - Dark-field transmission electron miscoscopy KW - Material degradation PY - 2016 DO - https://doi.org/10.1017/S1431927616007145 VL - 2016 SP - Paper 1260 AN - OPUS4-38279 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Beygi Nasrabadi, Hossein A1 - Skrotzki, Birgit T1 - Fatigue test ontology (FTO) N2 - Fatigue Test Ontology (FTO) has developed for representing the fatigue testing process, testing equipment requirements, test pieces charactristics, and related testing parameters and their measurement procedure according to DIN EN ISO 12106 standard. Versions info: V2 developed using PROVO+PMDco top-level ontologies. V3 developed using BFO+IOF top-level ontologies. Repositories: GitLab: https://gitlab.com/kupferdigital/process-graphs/lcf-test GitHub: https://github.com/HosseinBeygiNasrabadi/Fatigue-Test-Ontology-FTO- MatPortal: https://matportal.org/ontologies/FTO IndustryPortal: https://industryportal.enit.fr/ontologies/FTO KW - Ontology KW - Fatigue testing KW - FAIR data PY - 2024 UR - https://gitlab.com/kupferdigital/process-graphs/lcf-test UR - https://github.com/HosseinBeygiNasrabadi/Fatigue-Test-Ontology-FTO- UR - https://matportal.org/ontologies/FTO UR - https://industryportal.enit.fr/ontologies/FTO PB - GitLab CY - San Francisco, CA, USA AN - OPUS4-60547 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Uckert, Danilo A1 - Matzak, Kathrin A1 - Kühn, Hans-Joachim A1 - Rehmer, Birgit A1 - Peter, Frauke A1 - Fedelich, Bernard A1 - Skrotzki, Birgit T1 - Erweiterung bestehender Werkstoff- und Rechenmodelle zur Lebensdauervorhersage für Abgasturbolader-Heißteile unter thermomechanischer Ermüdungsbeanspruchung T2 - Informationstagung Turbomaschinen - Frühjahrstagung 2014 CY - Magdeburg, Germany DA - 2014-03-27 KW - TMF-Lebensdauerberechnung KW - ATL-Heißteile PY - 2014 IS - R567 SP - 147 EP - 175 AN - OPUS4-30489 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rockenhäuser, Christian A1 - Piesker, Benjamin A1 - Heidl, Daniel A1 - Skrotzki, Birgit T1 - Influence of prestraining on the aging response of an Al-Cu-Li alloy N2 - The influence of prestraining on the aging response of an Al-Cu-Li alloy is investigated by preparation of different strain states (3 %, 4 %, 6 %) of the initial aging state. The Brinell hardness of the subsequently aged samples (up to 60 h aging time) was measured and it was found that the increasing dislocation concentration in the 3 different initial states leads to faster hardness increases and slightly higher maximum hardness. T2 - Microscopy Conference 2019 (MC2019) CY - Berlin, Germany DA - 01.09.2019 KW - Al-Cu-Li alloys KW - hardness KW - coarsening PY - 2019 SP - 186 EP - 187 PB - Deutsche Gesellschaft für Elektronenmikroskopie (DGE) CY - Dresden AN - OPUS4-48918 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Skrotzki, Birgit T1 - Brinell-Hardness (HBW 2.5/62.5) of Al-alloy EN AW-2618A after different aging times and temperatures N2 - The dataset contains data from Brinell hardness measurements of Al-alloy EN AW-2618A after aging for different times and temperatures. Aging was either load free or with applied tensile load (creep). KW - Aluminium alloy KW - EN AW-2618A KW - Brinell hardness KW - Aging KW - Creep PY - 2022 UR - https://doi.org/10.5281/zenodo.6787085 UR - https://doi.org/10.5281/zenodo.10396823 DO - https://doi.org/10.5281/zenodo.6787084 PB - Zenodo CY - Geneva AN - OPUS4-55158 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Han, Ying A1 - Radners, J. A1 - von Hartrott, P. A1 - Skrotzki, Birgit T1 - Aluminium high temperature fatigue N2 - The studied aluminium alloy is EN AW-2618A (2618A). It is very widely used for exhaust gas turbo-charger compressor wheels. Due to long operating times, high cycle fatigue (HCF) and material aging under the influence of temperatures up to 230 °C is particularly relevant for the wheels. The wheels are typically milled from round wrought blanks. From such round blanks, different testpieces are extracted and a comprehensive series of HCF tests is conducted at room temperature. The tests investigate the materials fatigue performance in the T61 state for two load-ratios, namely R = -1 and R = 0.1. Additionally, two overaged material states are tested, accounting for the aging process the material undergoes during long operating times at high temperatures. The experimental results are evaluated and compared to each other. Furthermore, the design process of notched specimens is presented. With the notched specimens, it is aimed to quantify the notch sensitivity of the material. Relating thereto, two potential model parameters for the fatigue lifetime model are introduced. Finally, the extended research data management in this project is highlighted and its advantages for sustainable use in material science and engineering applications are shown. N2 - In diesem Projekt wird die Aluminiumlegierung EN AW-2618A (2618A) untersucht, welche sehr verbreitet in Verdichterrädern von Abgasturboladern zum Einsatz kommt. Hochzyklische Ermüdung und Werkstoffalterung bei Temperaturen von bis zu 230 °C ist bei Abgasturboladern aufgrund der langen Einsatzzeiten besonders relevant. Die Verdichterräder werden typischerweise aus geschmiedeten Rohlingen gefräst. Aus entsprechenden Rohlingen werden im Rahmen des Projekts eine Vielzahl von Proben mit unterschiedlichen Geometrien entnommen. Die Proben werden unter verschiedenen Prüfbedingungen in hochzyklischen Ermüdungsversuchen bei Raumtemperatur getestet. Zum einen wird das Ermüdungsverhalten des Werkstoffs im T61-Zustand für die zwei Belastungsverhältnisse R = -1 und R = 0,1 untersucht. Zum anderen werden zwei überalterte Materialzustände getestet. Damit soll dem Alterungsprozess Rechnung getragen werden, den das Material während langer Betriebszeiten bei hohen Temperaturen durchläuft. Die experimentellen Ergebnisse werden evaluiert und miteinander verglichen. Darüber hinaus wird der Entwurfsprozess von gekerbten Probengeometrien dokumentiert. Die gekerbten Proben sollen Aufschluss über die Kerbempfindlichkeit des Werkstoffs geben. In diesem Zusammenhang werden zwei mögliche Modellparameter für das zu entwickelnde Lebensdauermodell vorgestellt. Abschließend wird das erweiterte Forschungsdatenmanagement des Projekts beleuchtet und seine Vorteile für die nachhaltige Nutzung in materialwissenschaftlichen und ingenieurtechnischen Anwendungen aufgezeigt. T2 - FVV Frühjahrstagung 2022 CY - Würzburg, Germany DA - 31.03.2022 KW - EN AW-2618A KW - High cycle fatigue KW - Aluminium alloy PY - 2022 IS - FVV Publikationen Heft R602 SP - 617 EP - 634 PB - Forschungsvereinigung Verbrennungskraftmaschinen (FVV) CY - Frankfurt am Main AN - OPUS4-54622 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Paatsch, Wolfgang A1 - Hodoroaba, Vasile-Dan T1 - Quantitative and localized Hydrogen Analysis of electroplated Material T2 - AESF SUR/FIN® 2004 & INTERFINISH 2004 World Congress CY - Chicago, IL, USA DA - 2004-06-28 PY - 2004 SP - 556 EP - 564 PB - American Electroplaters and Surface Finishers Society (AESF) CY - Orlando AN - OPUS4-4695 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hodoroaba, Vasile-Dan T1 - Depth profiling of layered samples by Glow Discharge Optical Emission Spectroscopy (GD-OES) T2 - AIST-BAM Symposium on Materials Surface Technology in Twin Institute Programme CY - Tsukuba, Japan DA - 2003-02-18 PY - 2003 SP - 71 EP - 73 AN - OPUS4-6926 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klingelhöffer, Hellmuth A1 - Matzak, Kathrin A1 - Kühn, Hans-Joachim A1 - Skrotzki, Birgit T1 - Einfluss des Auswerteverfahrens auf die Bestimmung von zyklischen Werkstoffdaten im Hochtemperatur-LCF-Bereich T2 - 28. VDEh Vortragsveranstaltung der Arbeitsgemeinschaft für warmfeste Stähle und der Arbeitsgemeinschaft für Hochtemperaturwerkstoffe "Langzeitverhalten warmfester Stähle und Hochtemperaturwerkstoffe" CY - Düsseldorf, Deutschland DA - 2005-11-25 KW - Normung KW - Low Cycle Fatigue PY - 2005 SP - 137 EP - 146 PB - Stahlinstitut VDEh CY - Düsseldorf AN - OPUS4-11560 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Paatsch, Wolfgang A1 - Hodoroaba, Vasile-Dan T1 - Quantitative and localized Hydrogen Analysis of electroplated Material KW - Hydrogen KW - GD-OES depth profiling KW - Electroplating KW - Certified reference materials (CRM) KW - Certified reference coatings (CRC) KW - Quantification KW - Embrittlement PY - 2004 SP - 63 EP - 70 PB - American Electroplaters and Surface Finishers Society (AESF) CY - Orlando AN - OPUS4-6977 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Beygi Nasrabadi, Hossein A1 - Skrotzki, Birgit T1 - Vickers test ontology (VTO) N2 - Vickers Test Ontology (VTO) has developed for representing the Vickers testing process, testing equipment requirements, test pieces charactristics, and related testing parameters and their measurement procedure according to DIN EN ISO 6507-1 standard. Versions info: V2 developed using BFO+CCO top-level ontologies. Repositories: GitLab: https://gitlab.com/kupferdigital/process-graphs/vickers-hardness-test GitHub: https://github.com/HosseinBeygiNasrabadi/Vickers-Test-Ontology-VTO- MatPortal: https://matportal.org/ontologies/VTO IndustryPortal: https://industryportal.enit.fr/ontologies/VTO KW - Ontology KW - Knowledge graph KW - Data mapping KW - Vickers hardness KW - FAIR data. PY - 2024 UR - https://gitlab.com/kupferdigital/process-graphs/vickers-hardness-test UR - https://github.com/HosseinBeygiNasrabadi/Vickers-Test-Ontology-VTO- UR - https://matportal.org/ontologies/VTO UR - https://industryportal.enit.fr/ontologies/VTO PB - GitLab CY - San Francisco, CA, USA AN - OPUS4-60544 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Bachmann, Marcel A1 - Rethmeier, Michael A1 - Meng, Xiangmeng T1 - Project title: Multi-physical simulation of the influence of an auxiliary magnetic field on the process porosity formation during high-power laser beam welding N2 - In this project, a multiphysically coupled numerical model will be developed to quantitatively describe porosity reduction in high-power laser beam welding of up to 10 mm thick AlMg3 using an oscillating magnetic field. The aim is to gain fundamental insights into the physical dependencies of the introduced electromagnetic forces on the melt pool behavior and the reduction of porosity. With the help of the numerical model, the transient, multi-coupled, three-dimensional problem of heat transfer, liquid flow, free surface deformation, and magnetic induction is to be solved, taking into account temperature-dependent material properties. The numerical modelling of the heat source will integrate all relevant physical mechanisms, for instance, multiple reflections of the laser radiation by an advanced ray tracing model, as well as local Fresnel absorption at the keyhole wall. This allows an analysis of the keyhole fluctuations, which have a dominant influence on the formation of process spores during deep penetration welding, based on physical principles. In addition, further physical factors such as the ablation pressure of the evaporating metal, the Laplace pressure, and Marangoni shear stresses are also to be integrated into the model. To evaluate the pore formation and reduction by means of the electromagnetic forces introduced in the molten pool, suitable models for describing the movement of the pores in the melt are to be developed. For the process pores, their movement can be implemented by tracking their surface under consideration of their internal pressure and temperature. With the help of the simulation model, all key factors for the formation of process pores during laser beam welding of the used aluminum alloy, as well as their avoidance, can be decoupled and analyzed. Accompanying welding tests are planned at BAM on a 20 kW fiber laser and a 16 kW disk laser. The magnetic flux density will be up to 500 mT at a maximum frequency of 5 kHz. The experimental results, in particular temperature measurements, weld cross sections, computer tomography, and X-ray examinations, will be used to verify the multiphysical model and its calibration. Moreover, the models will be validated and quantified by in situ high-speed imaging of the keyhole dynamics in a metal/quartz glass configuration with keyhole illumination by a diode laser coaxial to the processing laser. On the basis of the numerical and experimental results, the dependencies between applied magnetic field, melt pool behavior, and porosity formation will be revealed in this project. KW - Laser beam welding KW - Electromagnetic weld pool control KW - Numerical simulation KW - Process porosity PY - 2026 DO - https://doi.org/10.34657/27669 SP - 1 EP - 14 AN - OPUS4-65335 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Rosalie, Julian M. A1 - Pauw, Brian R. A1 - Hohenwarter, Anton T1 - Precipitate size evolution in an ultrafine-grained magnesium-manganese alloy N2 - Precipitate size evolution during room temperature high-pressure torsion (HPT) of a Mg-1.35wt.%Mn alloy was studied using scanning transmission electron microscopy (STEM) and Small-/Wide-angle X-ray scattering (SAXS/WAXS). The volume fraction of the nm-scale α-Mn particles increased with applied strain, however small angle X-ray scattering (SAXS) indicated that the majority of manganese remained in solution even after 10 HPT rotations, indicating that the reaction progress is still limited by the diffusivity of Mn. Analysis of the precipitate size distribution determined that the mean particle size did not increase over the course of HPT. This, in combination with the precipitate size distribution suggested that precipitate growth was subject to interfacial rather than diffusional control. KW - Severe plastic deformation KW - High-pressure torsion KW - Ultrafine-grained alloys KW - Magnesium KW - Grain-boundary pinning KW - Precipitate growth KW - Interface control KW - Diffusional control PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-653422 DO - https://doi.org/10.48550/arXiv.2601.05619 SP - 1 EP - 15 AN - OPUS4-65342 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maierhofer, Christiane A1 - Röllig, Mathias A1 - Steinfurth, Henrik A1 - Augustin, Sven A1 - Mecke, R. A1 - Schiller, M. A1 - Kernchen, A. A1 - Kalisch, U. A1 - Meinhardt, J. A1 - Hennen, C. A1 - Groll, E. T. A1 - Arnold, T. T1 - Characterisation of historic façades using active thermography with solar heating and optical methods N2 - Active thermography is well suited for the detection of delaminations and cracks in façade elements like plaster and tiles. Not only artificial heating but also solar heating can be used if the adjustment of the façade and the weather conditions are suitable. Optical methods like laser scanners, photogrammetric methods and crack tracking sensors are providing geometrical 3D data which can be used for a 3D mapping of thermograms and for providing data with higher geometrical resolution. Thus, by the combination and fusion of these data, a comprehensive mapping and monitoring of damages of façade systems is possible. T2 - 19th World Conference on Non-destructive Testing (WCNDT) CY - München, Germany DA - 13.06.2016 KW - Non-destructive testing KW - Active thermography KW - Solar heating KW - Historic facades KW - Optical methods PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-366833 SN - 978-3-940283-78-8 VL - BB 158 SP - Mo.2.C.2., 1 EP - 8 PB - DGZfP CY - Berlin AN - OPUS4-36683 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schlick-Hasper, Eva A1 - Seidler, Oliver A1 - Goedecke, Thomas A1 - Kraume, M. T1 - Helium leak testing of dangerous goods packagings N2 - The International Dangerous Goods Regulations prescribe the immersion under water method (“bubble test”) as standard method for the leakproofness test of dangerous goods packagings. But this test procedure acts as a test method for leak localisation, not for quantitative leakage rates measurement. Additionally, the sensitivity in detecting leaks of small diameters is restricted, depending on the test liquid and the test pressure. The bubble test is not suitable for a comparison with quantitative limit leakage rates based on realistic transport conditions. This is especially important when estimating the risk of the formation of an explosive atmosphere during the intercontinental carriage of dangerous goods packagings in freight containers. To compare measured leakage rates with limit leakage rates, a quantitative leak testing procedure is required. Therefore a new approach for dangerous goods packagings is implemented: The pressure technique by accumulation using Helium as a tracer gas. This work presents the test equipment necessary for the quantitative measurement of Helium leakage rates through closures of different kinds of dangerous goods packagings. The essential steps to achieve good repeatable results are: A controlled Helium filling process to reach a defined test pressure in the test sample, a sufficient homogenisation of the Helium-air-mixture inside the test sample and the ensuring of a constant pressure level of the test sample during the test. The Helium loss rate of the accumulation chamber has to be measured separately to receive a correction factor for the measured leakage rates. Different constructional measures are introduced to prevent a disturbing influence of the Helium leakage rate of the filling valves on the measurement results. Methods to estimate the disturbing effect of Helium permeation through permeable parts of the test sample are also presented. As a supporting method for the experimental investigations the Helium sniffer test can be applied. This practical application-oriented advice can enable other users to establish a pressure technique by accumulation for their own technical field. T2 - 19th World Conference on Non-Destructive Testing CY - Munich, Germany DA - 13.06.2016 KW - Gefahrgutverpackungen KW - Dichtheit KW - Helium KW - Überdruckverfahren PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-366358 SN - 978-3-940283-78-8 VL - 158 SP - p175, 1 EP - 10 AN - OPUS4-36635 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pohl, Rainer A1 - Casperson, Ralf A1 - Maierhofer, Christiane A1 - Müller, Jan A1 - Pelkner, Matthias T1 - Gegenüberstellung von Wirbelstromprüfung und aktiver Thermografie an CFK-Versuchskörpern N2 - In vielen Bereichen der Technik haben Konstruktionen unter Einsatz von CFK-Bauteilen und Komponenten die klassischen Metalle abgelöst. Die zerstörungsfreie Prüfung solcher CFK-Bauteile gewinnt somit zunehmend an Bedeutung. Ein mögliches Prüfverfahren ist dabei die Wirbelstromprüfung. Aufgrund der relativ geringen elektrischen Leitfähigkeit von CFK-Komponenten kommt hierbei häufig die sogenannte HF-Wirbelstromprüfung zum Einsatz. In verschiedenen Untersuchungen der BAM konnten jedoch auch mit Wirbelstromprüfsystemen in niedrigen Frequenzbereichen gute Ergebnisse erzielt werden. Um die Möglichkeiten und Grenzen dieser konventionellen Wirbelstromprüfung auszuloten, wurden Messungen an Versuchskörpern durchgeführt, welche bereits bei der Validierung der Blitz- und Lock-in-Thermografie für neue Verfahrensnormen erfolgreich eingesetzt wurden. Ein Typ dieser Versuchskörper sind Flachproben aus CFK von 6 mm Dicke. In diesen wurden Flachbodenbohrungen mit Durchmessern zwischen 4 mm und 24 mm eingebracht. Die Restwandstärken liegen zwischen 0,06 mm und 3,66 mm. Ein weiterer CFK-Versuchskörper hat die Geometrie eines Stufenkeiles. Bei verschiedenen Stufenkeilen sind Wanddicken zwischen 1,4 mm und 5,4 mm realisiert worden. In diesen wurden künstliche quadratische Delaminationen mit Kantenlängen zwischen 2 mm und 20 mm eingebracht. Die Ergebnisse der Wirbelstromprüfung werden denen der aktiven Thermografie gegenübergestellt. Zur Nachbildung von Kompositwerkstoffen wurden die flachen Versuchskörper mit geeigneten Versuchskörpern aus Aluminium und Stahl kombiniert. Die Wirbelstromprüfungen wurden mit einem handelsüblichen Prüfgerät im Frequenzbereich zwischen 500 Hz und 3 MHz und entsprechend angepassten Sensoren durchgeführt. T2 - DGZfP Jahrestagung 2017 CY - Koblenz, Germany DA - 22.05.2017 KW - Wirbelstromprüfung KW - Aktive Thermografie KW - CFK PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-403607 SN - 978-3-940283-85-6 VL - 162 SP - 1 EP - 10 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-40360 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bertovic, Marija A1 - Kanzler, D. A1 - Pavlovic, Mato A1 - Holstein, R. T1 - Aktueller Stand der Diskussion zur Zuverlässigkeit der ZfP und den menschlichen Faktoren N2 - Dass die Zuverlässigkeit der ZfP eine sehr wichtige Rolle bei der Bewertung sicherheitsrelevanter Systeme spielt, ist bekannt. Laut dem modularen Zuverlässigkeitsmodell für zerstörungsfreie Prüfprozesse hängt die Zuverlässigkeit von der innewohnenden (physikalisch-technischen) Fähigkeit der Prüfsystems, den Anwendungsparametern, den menschlichen Faktoren und dem organisatorischen Kontext ab. Seit Einführung des Modells während des ersten Workshops zur Zuverlässigkeit der ZfP (European-American Workshop on Reliability of NDE) wurde das Modell in weiteren fünf Workshops stetig weiterentwickelt, diskutiert und an den Stand der Wissenschaft angepasst. Das Ziel dieser Publikation ist es, den aktuellen Stand der Diskussion und die neusten Fragestellungen der internationalen Zuverlässigkeitsgemeinschaft vorzustellen. Im Einzelnen werden die Entwicklung fortgeschrittener Modelle zur Bewertung der Probability of Detection (POD), Bewertungsansätze im Bereich Structural Health Monitoring und Fragestellungen zu den menschlichen Faktoren dargestellt. Besonderer Wert wurde sowohl auf die Entwicklung, als auch auf die Anwendung der Ansätze in der industriellen Praxis gelegt. T2 - DGZfP-Jahrestagung 2017 CY - Koblenz, Germany DA - 22.05.2017 KW - Zuverlässigkeit KW - Zerstörungsfreie Prüfung KW - Probability of detection KW - Human factors KW - Reliability PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-404861 SN - 978-3-940283-85-6 VL - DGZfP-Berichtsband BB 162 SP - 1 EP - 7 AN - OPUS4-40486 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mitzscherling, Steffen A1 - Barth, Enrico A1 - Götschel, S. A1 - Homann, Tobias A1 - Prager, Jens A1 - Weiser, M. T1 - Verbesserung und Qualifizierung der Ultraschallprüfung von Mischnähten im Primärkreis von KKW N2 - Die im Primärkreislauf von Kernkraftwerken anzutreffenden austenitischen Schweiß- und Mischnähte sind nicht nur extrem sicherheitsrelevant, sondern stellen auch sehr hohe Anforderungen an die Materialprüfung. Neben der eingeschränkten Zugänglichkeit ist das makroskopische Gefüge der Schweißnaht für die Prüfung mit Ultraschall von höchster Bedeutung. Um Materialfehler zuverlässig in Position und Größe bestimmen zu können, müssen die Kornorientierungen und die elastischen Konstanten des anisotropen Schweißnahtgefüges bekannt sein. Für die bildgebende Darstellung möglicher Materialfehler kommen folgende Arbeitsschritte zum Einsatz: Zunächst wird die Schweißnaht durchschallt, um mit einem inversen Verfahren wichtige Schweißnahtparameter wie beispielsweise die Kornorientierung bestimmen zu können. Auf der Basis dieser Parameter werden im nächsten Schritt die Schallwege mittels Raytracing (RT) simuliert. Zuletzt werden dieser RT-Simulation die Messdaten (A-Scans) von verschiedenen Sender- und Empfängerpositionen zugeordnet und nach der SAFT-Methode (Synthetic Aperature Focusing Technique) zeitaufgelöst überlagert. Die Kombination aus inversem Verfahren, RT und SAFT gewährleistet auch in anisotropen Werkstoffen eine ortsrichtige Visualisierung der Fehler. Wir erläutern diese drei Verfahren und stellen die Prüfanordnung von Prüfkörpern mit künstlichen Testfehlern vor. Messdaten sowie deren Auswertung werden mit den Ergebnissen einer CIVA-Simulation verglichen. T2 - DGZfP-Jahrestagung 2017 CY - Koblenz, Germany DA - 22.05.2017 KW - Zerstörungsfreie Prüfung KW - Ultraschall KW - SAFT KW - Schweißnaht KW - Austenit PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-404329 SN - 978-3-940283-85-6 VL - DGZfP BB 162 SP - P16, 1 EP - 8 AN - OPUS4-40432 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Lange, Nele T1 - Selektive chemische Modifikation von Siliziumnitrid-Oberflächen für neuartige biosensorische Applikationen N2 - Biosensoren gewinnen in den letzten Jahren zunehmend an Bedeutung. So erfolgt die Identifizierung des Analyten mit Biosensoren deutlich schneller und unkomplizierter als mit herkömmlichen analytischen Methoden. Aufgrund des Schlüssel-Schloss-Prinzips ist zudem die Detektion von Biosensoren äußerst selektiv. Die Herstellung dieser Sensoren erfolgt häufig trotz der Unzuverlässigkeit der Silanchemie über die Silanisierung der Si-H- bzw. Si-OH-Bindungen an der Silizium-Oberfläche. Die Abhängigkeit von Temperatur- und pH-Wert, sowie die Veränderung der Filmdicke bei nur kleinen Schwankungen des Wassergehalts während der Umsetzung werden oft vernachlässigt. Seltener wird die Si-NHx-Bindung genutzt, um dünne organische Filme zu erzeugen. Im Rahmen dieser Arbeit wurde eine neue Funktionalisierungsstrategie entwickelt, die die Silanchemie vermeidet. Die Idee basiert auf der Herstellung einer Azid-terminierten Oberfläche erzeugt aus Oberflächenaminen des materialintrinsischen Stickstoffs von Siliziumnitrid (Si3N4). Diese Azidgruppen bildeten die Grundlage für die Click-Chemie mit geeigneten Alkin-terminierten (Bio)molekülen und die anschließende Immobilisierung von ausgewählten Analyten. Die Funktionalisierungsstrategie umfasst die Erzeugung von NHx-terminierten Si3N4-Oberflächen durch Flusssäureätzung gefolgt von deren Umwandlung in Azidgruppen durch verschiedene Methoden. Im Anschluss wurden Alkine durch die Kupfer-katalysierte Azid-Alkin-Cycloaddition (CuAAC, Click-Chemie) an die Azid-terminierte Oberfläche immobilisiert. Der Erfolg der einzelnen Reaktionsschritte wurde durch oberflächenanalytische Methoden, durch XPS, NEXAFS und ToF-SIMS, überprüft. Die Charakterisierung der gebildeten Triazolringe erfolgte anhand des N 1s-XP-Spektrums sowie der NEXAFS C K-Kante. Die CF3-Gruppe wurde anhand der C 1s und F 1s-XP-Spektren, sowie der NEXAFS F K-Kante identifiziert. ToF-SIMS Untersuchungen bestätigten ebenfalls die Bindung des Alkins an die Si3N4-Oberfläche. Im weiteren Verlauf der Arbeit wurde die direkte Anbindung eines Biomoleküls an die Si3N4 Oberfläche getestet. Hierfür wurde das Biotin/Streptavidin-System durch eine Click-Reaktion an der Oberfläche verankert. Die erfolgreiche Biotin/Streptavidin-Interaktion wurde ebenfalls mit XPS, NEXAFS und ToF-SIMS nachgewiesen. Der Erfolg der Click-Reaktionen war sowohl bei der Methodenentwicklung als auch bei der Immobilisierung des Modellfilms vom genutzten Lösungsmittel abhängig. Neben der direkten Immobilisierung von (Bio)molekülen an die Si3N4-Oberfläche durch die Click-Chemie gelang es auch einen Kupfer(II)trifluormethoxyphenanthrolin-Komplex als künstliche Nuklease über Amid-Kopplung an die Si-NHx-Oberfläche zu binden. Hierbei diente ein OCF3-Substituent des Kupfer(II)trifluormethoxyphenanthrolin-Komplexes als XPS-Sonde. Die Identifizierung des Komplexes erfolgte anhand der OCF3-Komponente im C 1s- und F 1s-XP-Spektrum und der NEXAFS F K-Kante, sowie des Cu 2p-XP-Spektrums. Die ToF-SIMS-Massenspektren bestätigten ebenfalls die Bindung des Komplexes. Die Kupfermenge wurde mit der Massenspektrometrie mit induktiv gekoppeltem Plasma (ICP-MS) zu 0.08 µg/cm2 bestimmt, was 87 x 1012 Kupferatome pro cm2 entspricht. Nach der Verifizierung des immobilisierten Komplexes erfolgte die Untersuchung der Spaltaktivität der auf der Si3N4-Oberfläche gebundenen künstlichen Nuklease gegenüber Plasmid-DNA. Hierbei wurde eine Zunahme der Spaltaktivität mit zunehmender DNA-Inkubationszeit festgestellt. Weiterhin ist bemerkenswert, dass der verwendete Kupfer(II)trifluormethoxyphenanthrolin-Komplex erst auf der Oberfläche seine Spaltaktivität entfaltet. Kontrollproben in Lösung zeigten im Gegensatz zu dem immobilisierten Komplex keine Spaltaktivität. KW - Surface Chemistry KW - Silicon Nitride KW - Click Chemistry KW - DNA Cleavage KW - XPS KW - NEXAFS KW - ToF-SIMS PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:188-fudissthesis000000105216-6 SP - 1 EP - 240 PB - Freie Universität CY - Berlin AN - OPUS4-42790 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Köppe, Enrico T1 - Lokalisierung sich bewegender Objekte innerhalb und außerhalb von Gebäuden N2 - In der vorliegenden Dissertation „Lokalisierung sich bewegender Objekte innerhalb und außerhalb von Gebäuden“ wird die Herausforderung thematisiert ohne Nutzung lokaler Infrastruktur eine genaue Lokalisierung sich bewegender Objekte innerhalb von Gebäuden durchzuführen. Eine der wichtigsten Fragestellungen, die Grundlage dieser Arbeit ist, beschäftigt sich mit der Möglichkeit, eine Indoor-Lokalisierung mit Low-Cost-Sensoren zu realisieren. Im Rahmen der vorliegenden Arbeit ist diese Aufgabenstellung entsprechend den nachfolgend beschriebenen Schritten abgearbeitet worden. Zuerst wurde die mathematische Abbildung der verschiedenen Koordinatensysteme (Sensorsystem, Weltkoordinaten) näher betrachtet und die Überführungsmöglichkeiten (Quaternion) analysiert. Um der Herausforderung gerecht zu werden, ohne die Nutzung lokaler Infrastruktur ein sich bewegendes Objekt zu lokalisieren, musste eine eigene Testplattform realisiert werden. Für die Testplattform ist eine eigene Hardware mit ausgewählten handelsüblichen Low-Cost-Sensoren entworfen worden. Diese BodyGuard-System genannte Testplattform dient zur Überführung und Überprüfung der entwickelten mathematischen Algorithmen. Bei anschließenden ersten Tests stellte sich heraus, dass die Qualität der Ortsbestimmung (Genauigkeit) nur durch eine Kalibrierung der Sensoren sichergestellt werden kann. Aufgrund dieser Tatsache ist ein automatisches Kalibrierverfahren entwickelt worden. Weiterführend werden die unterschiedlichen Sensoren mittels Plausibilitätsprüfung miteinander fusioniert, um zum Beispiel das Driftverhalten zu eliminieren. Aufbauend auf diesen kalibrierten, plausibilisierten und fusionierten Bewegungsdaten ist der Betrachtungszeitraum für unterschiedliche Bewegungsmerkmale eingeführt worden, um so die Akkumulation von Lokalisierungsunsicherheiten als Funktion der Zeit zu vermeiden. Im letzten Schritt ist eine Validierung der Algorithmen in Experimenten durchgeführt worden. Das Ergebnis der Arbeit lässt sich wie folgt zusammenfassen. Unter Anwendung der Kalibriermethode zur Charakterisierung der Sensoren, deren Eigenschaften und Verhalten bei Bewegungen, lässt sich eine Position auch über einen längeren Zeitraum ausreichend genau bestimmen und eine Indoor-Lokalisierung auch mit Low-Cost-Sensoren realisieren. Die über diese Methode erzielte Genauigkeit liegt bezogen auf den zurückgelegten Weg bei ±1 % Abweichung über einen Zeitraum von 15 Minuten. PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:188-fudissthesis000000097278-3 SP - 1 EP - 157 PB - Freie Universität CY - Berlin AN - OPUS4-32427 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zscherpel, Uwe A1 - Schumacher, David A1 - Redmer, Bernhard A1 - Ewert, Uwe A1 - Ullberg, C. A1 - Weber, N. A1 - Pantsar, T. T1 - Digital radiology with photon counting detectors N2 - The progress in X-ray detector electronics (sensitivity and speed) allows meanwhile fast single photon detection by a matrix detector. Combined photon counting and energy discrimination is implemented in the electronic circuit of each detector pixel. The company XCounter developed detectors based on CdTe single crystals, which can be tiled to larger areas and have a pixel size of 100ìm. The largest area available in beginning of 2014 is 50x75 mm². These detectors have very promising properties, which make them very suitable for NDT applications: 1. A CdTe attenuation layer of 750 µm thickness allows efficient X-ray detection up to ca. 300 keV. In counting mode only photon noise is important; no other detector noise sources need to be considered. There is no Offset signal without radiation. 2. Each of the detector pixels has two energy thresholds. These can be used for dual energy imaging for materials separation. Also the suppression of scattered radiation by energy thresholding will improve the image contrast sensitivity. First experiments will be presented which demonstrate the advantages of this new detector technology over the conventional charge integrating detectors. A challenge is the development of a modified detector calibration procedure, which becomes critical at longer exposure times. T2 - ECNDT 2014 - 11th European conference on non-destructive testing CY - Prague, Czech Republic DA - 06.10.2014 KW - Materials characterization KW - Radiographic testing (RT) KW - Digital detector array KW - Photo counting KW - Image quality KW - Calibration KW - Dual-energy KW - Energy discrimination KW - Digital radiology KW - Detectors PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-323063 UR - https://www.ndt.net/?id=16709 SN - 1435-4934 N1 - Geburtsname von Schumacher, David: Walter, D. - Birth name of Schumacher, David: Walter, D. VL - 19 IS - 12 SP - 1 EP - 8 PB - NDT.net CY - Kirchwald AN - OPUS4-32306 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Laquai, René A1 - Müller, Bernd R. A1 - Nellesen, J. A1 - Hentschel, M.P. A1 - Kupsch, Andreas A1 - Tillmann, W. T1 - Synchrotron-Refraktion mit in-situ Zugbelastung zur Charakterisierung der Schadensentwicklung in Metall-Matrix- Kompositen N2 - Die Synchrotron-Refraktions-Topographie basiert auf der Brechung von Röntgenstrahlung an den Grenzflächen zwischen Materialien mit unterschiedlichem Brechungsindex. Refraktionseffekte verändern die Ausbreitungsrichtung der Röntgenstrahlung, welche mit Hilfe der Methode des Analyser-Based Imaging analysiert wird. Dabei wird ein Silizium-Einkristall im Strahlengang zwischen Probe und Detektor platziert. Dieser Analysator-Kristall filtert, innerhalb seiner Streuebene, die Röntgenstrahlung gemäß ihrer Ausbreitungsrichtung. Durch das Rastern verschiedener Winkelpositionen des Analysator-Kristalls erhält man das Winkelspektrum der von der Probe gebrochenen Strahlung. Aus dieser Rocking Curve lässt sich die spezifische innere Oberfläche der Probe bestimmen. Diese Information wird über einen 2D-Detektor mit einer nominellen Pixelgröße von 3,6 μm gewonnen. Die Installation einer Zugprüfmaschine ermöglicht es die Proben in verschiedenen Lastzuständen insitu zu untersuchen. Damit ist es möglich die spezifische innere Oberfläche in Abhängigkeit der Last darzustellen und so Schädigungsmechanismen abzuleiten. Der Vorteil bei der Ausnutzung des Refraktionseffekts gegenüber der einfachen Durchstrahlung ist die höhere Sensitivität gegenüber Defekten mit geringem Volumen aber großer Oberfläche. Somit werden auch Mikrorisse und, speziell bei Kompositen, die Enthaftung zwischen Matrix und Verstärkung (Partikel, Fasern) erfasst. In dieser Studie wurden Metall-Matrix-Komposite bestehend aus einer Aluminium-Matrix verstärkt mit Aluminiumoxid-Partikeln untersucht. Hierzu wurden knochenförmige Zugproben präpariert, deren Messlänge einen rechteckigen Querschnitt von 1,7 mm × 1,3 mm aufwies. Die Proben wurden einem Zugversuch unterzogen, welcher in Intervallen unterbrochen wurde. Bei jeder Unterbrechung wurde unter quasi-statischer Last die Rocking Curve gemessen und ein Radiogramm der spezifischen inneren Oberflächen berechnet. Dabei konnte ab dem Erreichen einer Last von ca. 600 N ein Anstieg der spezifischen inneren Oberfläche beobachtet werden. Demgegenüber zeigen die zum Vergleich durchgeführten Durchstrahlungsaufnahmen keinerlei Defekte. Daher belegt diese Untersuchung das Potential der Refraktion-Topographie zur frühzeitigen Erkennung von Schädigungen mit hoher Empfindlichkeit. T2 - DGZfP Jahrestagung 2017 CY - Koblenz, Germany DA - 22.05.2017 KW - Metall-Matrix-Komposite KW - Schadensentwicklung KW - Röntgen-Refraktions-Radiographie KW - In-situ Zugbelastung PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-405794 SN - 978-3-940283-85-6 SP - 1 EP - 7 PB - DGZfP AN - OPUS4-40579 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Höhne, Christian A1 - Boehm, Rainer A1 - Prager, Jens T1 - Detektion der Einhüllenden in SAFT-Daten durch Anwendung multidimensionaler analytischer Signale mit single-orthant-Spektren N2 - Die Synthetic Aperture Focusing Technique (SAFT) ist ein Verfahren zur Verarbeitung von HF-Bildern, die an unterschiedlichen Prüfkopfpositionen aufgenommen wurden. Es wird in der zerstörungsfreien Werkstoffprüfung genutzt, um eine Abbildung von Materialfehlern innerhalb des Gebietes zu erstellen, auf das die Rekonstruktion angewandt wird. Die nach Abschluss der SAFT-Rekonstruktion zusammengestellten Informationen über Reflektoren liegen zunächst nach wie vor in Form von HF-Daten vor. Die Interpretierbarkeit der SAFT-Bilder ist im Allgemeinen davon abhängig, wie diese Daten vor der endgültigen Darstellung aufbereitet werden. Die Bildung der Amplitudeneinhüllenden aus dem zugehörigen analytischen Signal stellt eine Möglichkeit einer solchen Aufbereitung nach Anwendung des SAFT-Algorithmus dar. Sie ist jedoch nur im eindimensionalen Fall eindeutig definiert. In diesem Beitrag wird das Konzept der analytischen Signale mit single-orthant-Spektren aufgegriffen, um eine Detektion der Einhüllenden an mehrdimensionalen HF-Daten durchzuführen. Dabei wird über die Betragsquadrate aller möglichen nach dieser Definition zu bildenden analytischen Signale gemittelt. Es wird gezeigt, dass die Anwendung des beschriebenen Verfahrens einem Separationsansatz entspricht. Außerdem wird eine Möglichkeit aufgezeigt die Gültigkeit dieses Ansatzes anhand der totalen und partiellen Hilberttransformationen des Signals im konkreten Fall zu überprüfen. Die Ergebnisse dieser Methode zur Verbesserung von SAFT Bildern werden unter Verwendung synthetischer und experimenteller Daten an rekonstruierten Abbildungen verschiedener Reflektorarten beispielhaft dargestellt. T2 - DACH-Jahrestagung 2012 CY - Graz, Austria DA - 17.09.2012 KW - Ultrasonic testing (UT) KW - Synthetic aperture focusing technique (SAFT) KW - Analytic signal PY - 2013 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-327039 UR - https://www.ndt.net/search/docs.php3?id=14341 SN - 1435-4934 VL - 18 IS - 5 SP - 1 EP - 8 PB - NDT.net CY - Kirchwald AN - OPUS4-32703 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Kranzmann, Axel T1 - Impact of saline aquifer water on surface and shallow pit corrosion of martensitic stainless steels during exposure to CO2 environment (CCS) N2 - Pipe steels suitable for carbon capture and storage technology (CCS) require resistance against the corrosive environment of a potential CCS-site, e.g. heat, pressure, salinity of the aquifer, CO2-partial pressure. Samples of different mild and high alloyed stainless injection-pipe steels partially heat treated: 42CrMo4, X20Cr13, X46Cr13, X35CrMo4 as well as X5CrNiCuNb16-4 were kept at T=60 °C and ambient pressure as well as p=100 bar for 700 h - 8000 h in a CO2-saturated synthetic aquifer environment similar to possible geological on-shore CCS-sites in the northern German Basin. Main corrosion products are FeCO3 and FeOOH. Corrosion rates obtained at 100 bar are generally much lower than those measured at ambient pressure. Highest surface corrosion rates are 0.8 mm/year for 42CrMo4 and lowest 0.01 mm/year for X5CrNiCuNb16-4 in the vapour phase at ambient pressure. At 100 bar the highest corrosion rates are 0.01 mm/year for 42CrMo4, X20Cr13 (liquid phase), X46Cr13 and less than 0.01 mm/year for X35CrMo4 and X5CrNiCuNb16-4 after 8000 h of exposure with no regard to atmosphere. Martensitic microstructure offers good corrosion resistance. T2 - 8th International Conference on Future Environment and Energy (ICFEE 2018) CY - Phuket, Thailand DA - 10.01.2018 KW - CCS KW - CO2 corrosion KW - Pipeline PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-465896 DO - https://doi.org/10.1088/1755-1315/150/1/012012 VL - 150 SP - 81 EP - 90 PB - IOP Publ. AN - OPUS4-46589 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schumm, A. A1 - Martin, E. A1 - Beaumont, M. A1 - Ewert, Uwe A1 - Kolkoori, Sanjeevareddy A1 - Zscherpel, Uwe A1 - Wrobel, Norma A1 - Redmer, Bernhard T1 - A comparative study on the performance of digital detector systems for high energy applications N2 - For cast components reaching or exceeding total material thicknesses of 150mm, high energy sources such as linear accelerators or Betatrons are required in order to obtain reasonable exposure times. In this study, the performance of digital detector systems, involving imaging plates (IP) and digital detector arrays (DDA), was evaluated with respect to the testing class B requirements as formulated in the standard EN ISO 17636-2. As a reference, traditional radiographic film and a Cobalt-60 source was used. With film exposures, testing class B was achieved with Co-60 and Betatron (7.5 MV) at longer exposure times. The preliminary results show that the testing class B was not obtained with the examined digital detector arrays (DDA) and the high resolution imaging plates (IP) , even at 40, 60 and 80 minutes exposure time with a 7.5 MV Betatron. Class A was achieved using high resolution imaging plates with optimized metal filters between object and IPs and a high resolution DDA with intermediate Cu filters. Class A was also achieved applying a DDA with lower basic spatial resolution than required by Table B.13 of EN ISO 17636-2, but using the compensation principle as described in this standard. The next generation of digital detector arrays might potentially be able to obtain class B performance with the expected spatial resolution and sensitivity improvements. T2 - ECNDT 2014 - 11th European conference on non-destructive testing CY - Prague, Czech Republic DA - 06.10.2014 KW - Radiography KW - Image quality KW - Betatron KW - Digital detector array (DDA) KW - Casting KW - Standards KW - High energy radiography KW - Comparison of detectors KW - Steel weldment PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-323075 UR - https://www.ndt.net/?id=16394 SN - 1435-4934 VL - 19 IS - 12 SP - 1 EP - 6 PB - NDT.net CY - Kirchwald AN - OPUS4-32307 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - VIDEO A1 - Pauw, Brian Richard T1 - "Ultima Ratio": Multi-scale, high-resolution 3D-FFT scattering pattern simulations N2 - This talk highlights a proof-of-concept that demonstrates the ability to calculate high-resolution Fourier transforms. These can be combined with multi-scale modeling to simulate scattering over a wide range, from small-angle scattering to XRD and PDF. The preprint documenting this is available on the ArXiv here: https://doi.org/10.48550/arXiv.2303.13435 The Jupyter notebook, VASP calculation details and MOUSE measured scattering patterns are available from this Zenodo repository: https://dx.doi.org/10.5281/zenodo.7764045 T2 - Shapespyer/MuSSIC Launch Workshop CY - Didcot, UK DA - 20.02.2023 KW - Video KW - Simulation KW - High-resolution KW - Fourier Transform KW - 3D FFT KW - Nanomaterial KW - Metal organic framework KW - MOF KW - SAXS KW - XRD KW - PDF KW - X-ray diffraction KW - Pair distribution function KW - Small-angle X-ray scattering PY - 2023 UR - https://www.youtube.com/watch?v=lEApkOqR5e8 DO - https://doi.org/10.26272/opus4-57212 PB - YouTube, LLC CY - San Bruno, CA, USA AN - OPUS4-57212 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hosseini, Seyed M. H. A1 - Heckel, Thomas A1 - Boehm, Rainer A1 - Brackrock, Daniel A1 - Gohlke, Dirk A1 - Riemer, Stefanie A1 - Gaal, Mate T1 - Gegenüberstellung der Performance verschiedener Ultraschallsensorsysteme bei der Untersuchung von CFK-Platten T1 - Comparison of performance of different ultrasonic systems for inspection of CFRP plates N2 - Die Zahl der industriellen Anwendungen mit Einsatz von Faserverbundwerkstoffen wächst kontinuierlich vor allem wegen der exzellenten Materialeigenschaften und des geringen Gewichtes dieses Werkstoffes. Entsprechend steigen die Anforderungen an zerstörungsfreie Prüfsysteme zur Gewährleistung des sicheren Betriebes von Komponenten und Strukturen bestehend aus Verbundwerkstoffen. Im Rahmen des EU-Projekes VITCEA (Validated Inspection Techniques for Composites in Energy Applications) wird das Ziel verfolgt, neue Prüfverfahren für moderne Verbundwerkstoffe zu entwickeln und zu validieren. Im Vordergrund steht hierbei als Applikation im Industriesektor Energieversorgung die Prüfung von sicherheitsrelevanten Komponenten von onshore und offshore Windkraftanlagen, wie z.B. deren Rotorblätter und tragende Strukturen. Eine Teilaufgabe innerhalb des Projektes stellen der Vergleich und die Validierung verschiedener Ultraschallprüfmethoden bezüglich ihrer Fähigkeit zum Nachweis der typischen Herstellungs- und betriebsbedingten Materialschädigungen von CFK und GFK dar. Neben verschiedenen konventionellen Ultraschall-Prüftechniken, werden die Phased-Array-Prüfung, insbesondere die Prüfung mit Matrixarrays, sowie die Untersuchung mit berührüngsloser Luftultraschalltechnik bezüglich ihrer Nachweisgrenzen und der Möglichkeiten zur Fehlercharakterisierung an Faserverbundwerkstoffen untersucht. Die Ergebnisse werden mit Untersuchungen mit thermographischen Methoden und Mikrowellentechnik verglichen. N2 - Applications of fiber-reinforced plastic (FRP) composites in modern industries are increasing due to their considerable advantages such as light weight and excellent mechanical properties. Accordingly, importance of operational safety of modern structures made of advanced composites by ensuring the material quality has led to increasing demands for development of non-destructive evaluation (NDE) systems. In the context of a European-project entitled 'Validated Inspection Techniques for Composites in Energy Applications' (VITCEA), the aim is to develop and validate traceable procedures for novel NDE techniques with contrasting damage detection capabilities in energy related applications such as wind and marine turbine blades, nacelles, oil and gas flexible risers. As a part of VITCEA, the present study focuses on application of ultrasonic tests (UTs) including conventional, matrix array, immersion and air-coupled, for quantitative defect detection and quality characterization of FRP structures. Results of UTs are subjected to be compared with other NDE approaches which are applicable for inspection of FRPs such as thermography and microwave techniques. Within the present report, the initial results obtained from conventional and immersion UTs are presented and their capabilities as well as limitations are discussed. In order to validate theoretical predictions and simulation results, further experimental tests will be performed in the framework of the project using reference defect artefacts in which the defect sizes and locations are well defined and controlled. T2 - DGZfP Seminar des Fachausschusses Ultraschallprüfung CY - Saarbrücken, Germany DA - 03.11.2015 KW - Ultraschallsensorsysteme KW - Faserverbundwerkstoffe KW - Kontakttechnik Technik KW - Tauchtechnik KW - Phased-Array-Prüfung KW - Luftultraschall PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-349264 UR - https://www.dgzfp.de/Portals/ultraschall2015/BB/3.pdf SP - Vortrag 3, 1 EP - 10 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) AN - OPUS4-34926 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krankenhagen, Rainer A1 - Maierhofer, Christiane T1 - Einzelblitz vs. Multiblitz - Blitzthermografie mit mehreren Blitzen N2 - Die Blitzthermografie weist eine Reihe von Vorteilen gegenüber anderen Verfahren der aktiven Thermografie auf und hat daher eine relativ große Verbreitung in Forschung und Industrie gefunden. Ein wesentlicher Nachteil ist jedoch die begrenzte Energie, die pro Blitz genutzt werden kann. Es stellt sich die Frage, ob sich durch mehrere kurz hintereinander ausgeführte Blitze eine Verbesserung des Energieeintrags erreichen lässt. Zur experimentellen Untersuchung dieser Frage wurde ein Versuchsstand mit vier Blitzlampen so umgerüstet, dass die Blitzlampen zeitgleich oder nacheinander mit einer regelbaren Verzögerung ausgelöst werden können („Multiblitz“). Als Probekörper dienten Platten aus CFK, an deren Rückseite Flachbodenbohrungen (FBB) eingebracht worden waren. Betrachtet wurde jedoch nur der absolute Temperaturhub am ungestörten Material. Die Experimente zeigen relativ geringe Effekte im Prozentbereich, wie sie auch gemäß einer quantitativen Abschätzung zu erwarten sind. Interessanterweise vergrößerte sich der Einfluss der Multiblitzanregung auf die Energieeinkopplung deutlich bei einem etwas vergrößerten Abstand zwischen Blitzlampen und untersuchter Oberfläche. Die Ursache für diesen Effekt ist derzeit unklar, vermutet werden eine Temperaturabhängigkeit und/oder eine Abstandsabhängigkeit des Wärmübergangskoeffizienten im Konvektionsterm. T2 - Thermographie-Kolloquium 2015 CY - Leinfelden-Echterdingen, Germany DA - 01.10.2015 KW - Thermografie KW - Blitzthermografie KW - Konvektion KW - Wärmeverluste KW - Einkoppeleffizienz KW - Energiekopplung PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-345487 SN - 978-3-940283-74-0 VL - 154 SP - 1 EP - 8 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-34548 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gaal, Mate A1 - Dohse, Elmar A1 - Bartusch, Jürgen A1 - Kreutzbruck, Marc T1 - Luftultraschallprüfung von CFK mit planaren und fokussierenden Wandlern N2 - Für die Prüfung von Leichtbaustrukturen ist in den letzten Jahren ein vermehrter Einsatz der Luftultraschallprüfung zu verzeichnen. Insbesondere eignet sich Luftultraschall für die Prüfung von Faserkunststoffverbunden und hybrider Werkstoffverbunde, die ihre Anwendung in der Automobilindustrie und Luftfahrt finden. Für den Bau von marktüblichen Luftultraschall-Wandlern werden Piezokomposite mit Anpassschichten versehen. Ihre Herstellung ist allerdings sehr anspruchsvoll und die erreichbaren Signal-Rausch-Abstände sind für viele Prüfprobleme als noch nicht ausreichend einzustufen. Zwecks gesteigerter Effizienz beim Schallübertrag in die Luft wurden Luftultraschall-Sender und -Empfänger aus zellulärem Polypropylen entwickelt. Dieses piezoelektrische Material ist aufgrund seiner geringer Dichte und seiner sehr geringen Schallgeschwindigkeit an die niedrige akustische Impedanz der Luft deutlich besser angepasst, als die üblicherweise verwendeten Anpassschichten. Letztere können bei Polypropylen-Wandlern daher gänzlich vermieden werden. In diesem Beitrag wird Luftultraschall-Prüfung an zwei verschiedenen CFK-Testkörpern vorgestellt: an einer Platte mit T-Stringern aus dem Seitenleitwerk eines Flugzeugs und an einer Platte mit künstlich eingebrachten Fehlern. Es wurde mit unterschiedlichen planaren und fokussierenden Wandlern geprüft. Marktübliche Wandler mit Anpassschichten wurden mit den selbstentwickelten Wandlern aus zellulärem Polypropylen verglichen. Der Signal-Rausch-Abstand und die laterale Auflösung wurden sowohl im Prüfaufbau mit senkrechter Einschallung als auch mit Schrägeinschallung gemessen. Die Ergebnisse zeigen, dass die Schrägeinschallung zwar den Signal-Rauschabstand erhöht, aber die laterale Auflösung verschlechtern kann. T2 - DACH Jahrestagung 2015 CY - Salzburg, Austria DA - 11.05.2015 PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-349751 UR - http://jt2015.dgzfp.de/Portals/jt2015/BB/mi1a3.pdf SP - Mi.1.A.3-1 EP - Mi.1.A.3-9 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-34975 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - VIDEO A1 - Pauw, Brian Richard T1 - How to run a (lab) SAXS instrument efficiently N2 - Here I talk about our holistic approach to X-ray scattering, and what improvements we made to our methodology to make measuring with us a very streamlined process. KW - Laboratory management KW - MOUSE KW - X-ray scattering KW - Instrument utilization KW - Research efficiency KW - Automation KW - Metadata collection KW - Laboratory automation PY - 2022 UR - https://www.youtube.com/watch?v=ncadUQ43Uwc DO - https://doi.org/10.26272/opus4-55761 PB - YouTube, LLC CY - San Bruno, CA, USA AN - OPUS4-55761 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kolkoori, Sanjeevareddy A1 - Wrobel, Norma A1 - Osterloh, Kurt A1 - Redmer, Bernhard A1 - Deresch, Andreas A1 - Ewert, Uwe T1 - Hochenergieradiographie - Erkennung von Einzelheiten in großen, komplexen Schichttiefen N2 - Zur Durchstrahlung großer, dichter Objekte reichen die Energien, die mit normalen Röntgenröhren erzielt werden können, ab gewissen Schichtdicken nicht mehr aus. Als hochenergetische Strahlenquellen stehen Kobalt-60 und Elektronenbeschleuniger zur Verfügung. Als Einschränkung der Hochenergieradiographie ist der geringere Kontrast besonders beim Vorhandensein leichterer Objekte umgeben von Körpern bestehend aus schweren Elementen anzusehen. Es ist daher zu erwarten, dass Objekte aus organischen Substanzen hinter dicken Schwermetallwänden oder in Bohrungen von Metallblöcken schwer zu erkennen sind. Im Gegensatz zu einem Gammastrahler wie Kobalt-60 mit den beiden Spektrallinien um 1,3 MeV besitzt die Bremsstrahlung aus einem Beschleuniger einen wesentlichen Anteil an niederenergetischer Strahlung, der fließend zu höheren Energien übergeht. Es wird hier untersucht, welche Signaturen von leichten Materialien in einer Umgebung aus Schwermetall bis zu welcher Dicke und bis zu welchem Komplexizitätsgrad erkennbar sind. Mit einem Betatron (JME X-ray Betatron 7,5 MeV) und einem Matrixdetektor (Perkin Elmer XRD 1621) wurden Aufnahmen von unterschiedlichen leichten Objekten angefertigt, die zunehmend in eine Umgebung aus Schwermetallen gestellt wurden. Mit unterschiedlichen Energieeinstellungen wurde untersucht, inwieweit eine Materialerkennung hinter welcher Abschirmung möglich ist. Die experimentellen Ergebnisse werden mit Simulationen verglichen, die mit einer Software zur Modellierung von Durchstrahlungsverfahren (aRTist) erzeugt wurden. Dabei wird dem Problem der Aufhärtung bei Anwendung von Bremsstrahlung Rechnung getragen. Die Ergebnisse können sowohl zur Erkennung von Fremdkörpern in Maschinen oder Pumpen als auch zur Überprüfung von Frachtladungen im Bereich der öffentlichen Sicherheit und bei Zollkontrollen dienen. T2 - DGZfP-Jahrestagung 2013 CY - Dresden, Germany DA - 06.05.2013 KW - Hochenergieradiographie KW - Containerprüfung KW - Materialerkennung PY - 2013 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-288589 SN - 978-3-940283-49-8 IS - DGZfP-BB 141 (Mo.2.A.4) SP - 1 EP - 9 PB - Deutsche Gesellschaft für zerstörungsfreie Prüfung e.V. (DGZfP) AN - OPUS4-28858 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kruschwitz, Sabine T1 - NDT for microstructure and moisture investigation of porous building material N2 - Non-destructive testing methods are mostly applied and established for the detection of embedded mounting parts or structural defects in building elements. The assessment of the concrete microstructure or microstructural changes like chemical alterations or the formation of microcracks, e.g. due to material aging, freeze-thaw cycles, alkali-silica reaction and ettringite, is not in the focus of ndt research though. Concrete moisture and enhanced salt contents, which usually trigger all chemical microstructural changes, are other material properties, lacking reliable ways of measuring. But, the assessment of such material properties, on the long term also in a depth resolved manner, is definitely important, when the sustainability of our concrete infrastructure buildings shall be evaluated. New consideration like the potential use of ndt, in particular the combination of different methods and alternate ways of data analysis are subject of research currently undertaken at BAM. These approaches involve for example working towards (i) a deeper understanding of how to measure moisture distributions reliably and follow transport phenomena, (ii) the use of stray phenomena in radar and ultrasound to locate material inhomogeneities or (iii) the application of LIBS for the delineation of diffusion and migration processes but also (iv) the use of new tools for data analysis like data fusion. First results are presented and new ideas discussed. T2 - NDT-CE 2015 - International symposium non-destructive testing in civil engineering CY - Berlin, Germany DA - 15.09.2015 KW - Screed KW - Moisture KW - Non-destructive testing KW - Radar KW - Microstructure KW - Monitoring KW - Concrete deterioration KW - Cracking PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-347593 UR - http://www.ndt.net/?id=18354 SN - 1435-4934 VL - 20 IS - 11 SP - 1 EP - 5 PB - NDT.net CY - Kirchwald AN - OPUS4-34759 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Osterloh, Kurt A1 - Fratzscher, Daniel A1 - Jechow, Mirko A1 - Bücherl, T. A1 - Schillinger, B. A1 - Hasenstab, A. A1 - Zscherpel, Uwe A1 - Ewert, Uwe T1 - Limited view tomography of wood with fast and thermal neutrons N2 - Neutrons are absorbed particularly by hydrogen containing materials so they can be used as a tool for visualising heterogeneous density distributions of organic materials. Penetration limits are set by the layer thicknesses and the neutron energies applied. In case of specimens with a flat shape the situation may be encountered that the object only could be penetrated in selected directions. In addition, the overall size may exceed the beam diameter and thus the viewing window if a certain region of interest should be studied by tomography without destroying the integrity of the specimen. This study shows the capabilities and limits of thermal and fast neutrons to investigate flat wooden specimens such as boards and girders by neutron tomography under such circumstances. Taking projections was impaired either by the limits of penetrability or by the total size of the object. As a consequence, projections were included for reconstruction only from a limited angular range of 90°. It could be shown that an approach based on the slice theorem was capable to visualise structural features along the beam directions while simply omitting the perpendicular ones without causing additional artefacts. Small samples with a thickness of up to 2 cm but several times broader could be studied with the ANTARES facility of the FRM II neutron source in Garching providing thermal neutrons while larger objects required a beam of higher energy as available in the NECTAR facility of the same institution. The fast (fission) neutrons (1.5 – 2 MeV) of this site allowed investigating an area of interest inside a girder with a cross section of 23.5 x 49 cm². Internal features such as inclusions could be detected as well as a heterogeneous density distribution in glue layers. T2 - International symposium on digital industrial radiology and computed tomography CY - Berlin, Germany DA - 20.06.2011 KW - Computed tomography KW - Slice theoreme KW - Limited angle tomography PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-250663 SN - 978-3-940283-34-4 VL - 128 SP - 1 EP - 5 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-25066 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Berchtold, Florian A1 - Knaust, Christian A1 - Rogge, Andreas A1 - Arnold, L. A1 - Thöns, Sebastian ED - Lönnermark, Anders ED - Ingason, Haukur T1 - Risk Analysis for Road Tunnels – A Metamodel to Efficiently Integrate Complex Fire Scenarios N2 - Fires in road tunnels constitute complex scenarios with interactions between the fire, tunnel users and safety measures. More and more methodologies for risk analysis quantify the consequences of these scenarios with complex models. Examples for complex models are the computational fluid dynamics model Fire Dynamics Simulator (FDS) and the microscopic evacuation model FDS+Evac. However, the high computational effort of complex models often limits the number of scenarios in practice. To balance this drawback, the scenarios are often simplified. Accordingly, there is a challenge to consider complex scenarios in risk analysis. To face this challenge, we improved the metamodel used in the methodology for risk analysis presented on ISTSS 2016. In general, a metamodel quickly interpolates the consequences of few scenarios simulated with the complex models to a large number of arbitrary scenarios used in risk analysis. Now, our metamodel consists of the projection array-based design, the moving least squares method, and the prediction interval to quantify the metamodel uncertainty. Additionally, we adapted the projection array-based design in two ways: the focus of the sequential refinement on regions with high metamodel uncertainties; and the combination of two experimental designs for FDS and FDS+Evac. To scrutinise the metamodel, we analysed the effects of three sequential refinement steps on the metamodel itself and on the results of risk analysis. We observed convergence in both after the second step (ten scenarios in FDS, 192 scenarios in FDS+Evac). In comparison to ISTSS 2016, we then ran 20 scenarios in FDS and 800 scenarios in FDS+Evac. Thus, we reduced the number of scenarios remarkably with the improved metamodel. In conclusion, we can now efficiently integrate complex scenarios in risk analysis. We further emphasise that the metamodel is broadly applicable on various experimental or modelling issues in fire safety engineering. T2 - International Symposium on Tunnel Safety and Security CY - Boras, Sweden DA - 14.03.2018 KW - Risk KW - Metamodel KW - CFD KW - Evacuation KW - Uncertainty PY - 2018 SN - 978-91-88695-48-2 VL - 8 SP - 349 EP - 360 AN - OPUS4-44535 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Long, Lijia A1 - Thöns, Sebastian A1 - Döhler, M. T1 - Damage Detection and Deteriorating Structural Systems N2 - This paper addresses the quantification of the value of damage detection system and algorithm information on the basis of Value of Information (VoI) analysis to enhance the benefit of damage detection information by providing the basis for its optimization before it is performed and implemented. The approach of the quantification the value of damage detection information builds upon the Bayesian decision theory facilitating the utilization of damage detection performance models, which describe the information and its precision on structural system level, facilitating actions to ensure the structural integrity and facilitating to describe the structural system performance and its functionality throughout the service life. The structural system performance is described with its functionality, its deterioration and its behavior under extreme loading. The structural system reliability given the damage detection information is determined utilizing Bayesian updating. The damage detection performance is described with the probability of indication for different component and system damage states taking into account type 1 and type 2 errors. The value of damage detection information is then calculated as the difference between the expected benefits and risks utilizing the damage detection information or not. With an application example of the developed approach based on a deteriorating Pratt truss system, the value of damage detection information is determined,demonstrating the potential of risk reduction and expected cost reduction. T2 - International Workshop on Structural Health Monitoring CY - Stanford, CA, USA DA - 12.09.2017 KW - Reliability updating KW - Structural reliability and risks KW - Damage detection KW - Value of information PY - 2017 SN - 978-1-60595-330-4 SP - 1276 EP - 1284 AN - OPUS4-43624 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Götschel, S. A1 - Maierhofer, Christiane A1 - Müller, Jan P. A1 - Rothbart, Nick A1 - Weiser, M. T1 - Quantitative defect reconstruction in active thermography for fiber-reinforced composites N2 - Carbon-fiber reinforced composites are becoming more and more important in the production of light-weight structures, e.g., in the automotive and aerospace industry. Thermography is often used for non-destructive testing of These products, especially to detect delaminations between different layers of the composite. In this presentation, we aim at methods for defect reconstruction from thermographic measurements of such carbon-fiber reinforced composites. The reconstruction results shall not only allow to locate defects, but also give a quantitative characterization of the defect properties. We discuss the simulation of the measurement process using finite element methods, as well as the experimental validation on flat bottom holes. Especially in pulse thermography, thin boundary layers with steep temperature gradients occurring at the heated surface need to be resolved. Here we use the combination of a 1D analytical solution combined with numerical solution of the remaining defect equation. We use the simulations to identify material Parameters from the measurements. Finally, fast heuristics for reconstructing defect geometries are applied to the acquired data, and compared for their accuracy and utility in detecting different defects like back surface defects or delaminations. T2 - 19th World Conference on Non-Destructive Testing 2016 CY - München, Germany DA - 13.06.2016 KW - Active thermography KW - Numerical simulation KW - Time-resolved thermogram KW - Thermal wave PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-366644 UR - https://www.wcndt2016.com/Programme/show/Th-4-C-4 VL - 2016 SP - Th.4.C.4-1 EP - Th.4.C.4-10 AN - OPUS4-36664 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Spranger, Holger A1 - Beckmann, Jörg A1 - Boehm, Rainer T1 - THz-ToF techniques for the detection of inherent discontinuities in dielectric materials based on a SAFT – and an optical layer reconstruction algorithm N2 - Electromagnetic waves with frequencies between 0.1 and 10 THz are described as THz-radiation (T-ray). The ability to penetrate dielectric materials makes T-rays attractive to reveal discontinuities in polymer and ceramic materials. THz-Time Domain Spectroscopy Systems (THz-TDS) are available on the market today which operates with THz-pulses transmitted and received by optically pumped semiconductor antennas. In THz-TDS the travelling time (ToF) and shape of the pulse is changed if it interacts with the dielectric material and its inherent discontinuities. A tomogram of the object under the test can be reconstructed from time of flight diffraction (ToFD) scans if a synthetic focusing aperture (SAFT) algorithm is applied. Otherwise, planar discontinuities like cracks in plastics or delaminated layers in composites can be abstracted as layers located at any angle in relation to the outer sample surface direction. A tomogram from the scanned sample can then be reconstructed in case the interactions of electromagnetic pulses with the existing inherent interfaces are detectable and a model is assumed which describes the device under the test as multilayer structure composed of thin layers with different dielectric properties. A short description of both the SAFT – and Optical Layer algorithm for the reconstruction of the inherent structure is initially given. Measurements on representative samples with a variety of artificially produced small and large scale. Reconstructed tomograms are presented to discuss and evaluate the benefits and limits of the two different reconstruction approaches. T2 - 19th World Conference on Non-Destructive Testing 2016 CY - Munich, Germany DA - 13.06.2016 KW - THz SAFT Optical layer reconstruction PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-365866 SN - 978-3-940283-78-8 VL - 158 SP - 1 EP - 10 AN - OPUS4-36586 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Marotzke, Christian A1 - Feldmann, Titus T1 - Nonlinear time dependent behaviour of epoxy resins N2 - The nonlinear behaviour of epoxy resins is studied on standard tensile tests. A strain field measurement system is applied (Aramis) in order to monitor local strains. The residual strain is measured by recovering the specimens for up to 68 hours after unloading. The time span the specimen is exposed to load has a large influence on the creeping process and the residual strain after recovering. This is studied by comparison of instantaneous unloading with keeping the specimen under permanent load for thirty minutes. It is shown that moderate differences in the initial strain can lead to large differences in the creep behaviour as well as in the residual strain. T2 - 37th Risø International Symposium on Materials Science CY - Risø, DK DA - 05.09.2016 KW - composites KW - epoxy resin KW - viscoelasticity KW - plasticity PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-378552 DO - https://doi.org/10.1088/1757-899X/139/1/012035 SN - 1757-8981 VL - 139 SP - Article 012035, 1 EP - 8 PB - IOP Publishing CY - London AN - OPUS4-37855 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gaal, Mate A1 - Daschewski, Maxim A1 - Bartusch, Jürgen A1 - Schadow, Florian A1 - Dohse, Elmar A1 - Kreutzbruck, Marc A1 - Weise, Matthias A1 - Beck, Uwe T1 - Novel air-coupled ultrasonic transducer combining the thermoacoustic with the piezoelectric effect N2 - In recent years, there has been an increasing industrial demand for one-sided inspection of various structures by means of air-coupled ultrasonic technique. Lightweight structures based on carbon-fibre-reinforced polymers may have very complex shapes, making air-coupled transmission difficult or even impossible. The inspection of concrete structures is another example where one-sided inspection is required. To address these challenges a new type of transducer for air-coupled pulse-echo inspection was developed, which unites two principles: thermoacoustic emission and piezoelectric reception. The thermoacoustic emitter is a titanium electrode with a thickness of several tens of nanometer. This electrode was deposited onto charged cellular polypropylene, which serves as a piezoelectric receiver. The thermoacoustic transmission is based on a transformation of the thermal energy of an electrically heated electrode into the acoustic energy of an ultrasonic wave. Thermoacoustic emitters provide resonance-free behaviour and thus extremely broadband pulses. Charged cellular polypropylene is piezoelectric due to the polarization of its cells and it is well matched to air, with a Young modulus in the order of magnitude of MPa. In this contribution we present some pulse-echo measurements with the first prototypes of the combined thermoacoustic-piezoelectric transducer. T2 - World Conference of Non-Destructive Testing CY - Munich, Germany DA - 13.6.2016 KW - Thermoacoustic KW - Piezoelectric KW - Ultrasonic transducer KW - Ferroelectret PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-367151 VL - 158 SP - Mo.1.F.4, 1 EP - 6 AN - OPUS4-36715 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kreutzbruck, Marc A1 - Bauer, P. A1 - Caspers, F. A1 - Heck, S. A1 - Müller, F. A1 - Pohl, Rainer A1 - Scheuerlein, C. A1 - Sickert, Roland A1 - Maierhofer, Christiane A1 - Brackrock, Daniel T1 - Sensoren für Verbunddrähte aus Niob-Titan und Kupfer N2 - Der Large Hadron Collider (LHC) des europäischen Kernforschungszentrums CERN ist einer der weltweit größten und leistungsfähigsten Teilchenbeschleuniger. Um den Teilchenstrahl auf seiner Kreisbahn zu halten, werden mit Hilfe supraleitender Spulen sehr starke Magnetfelder erzeugt. Die hierzu benötigten hohen Ströme werden über Verbunddrähte aus Niob-Titan und Kupfer geleitet. Die Drähte werden u.a. durch Ultraschallschweißungen miteinander verbunden. Eine mangelhafte Verbindung kann zur Erwärmung der Kontaktstelle und in Folge davon zum Zusammenbruch der Supraleitung führen. Auf Anfrage des CERN wurden an der BAM Untersuchungen zur Prüfbarkeit solcher Verbindungen bei Umgebungstemperatur durchgeführt. Es gelang, für einen Verbindungstypen einen Wirbelstromsensor für eine manuelle Prüfung zu entwickeln. Ein Prototyp des Sensors befindet sich beim CERN in der praktischen Erprobung. Das Sensorprinzip sowie Prüfergebnisse aus Labor und Praxis werden vorgestellt. T2 - DGZfP-Jahrestagung 2014 CY - Potsdam, Germany DA - 26.05.2014 KW - Ultraschallprüfung mit Matrix-Sensoren KW - Aktive Thermografie KW - Gabelsensor PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-319785 SN - 978-3-940283-61-0 VL - 148 SP - 1 EP - 12 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-31978 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bertovic, Marija A1 - Gaal, Mate A1 - Müller, Christina A1 - Fahlbruch, B. A1 - Schombach, D. T1 - Einfluss des Zeitdrucks auf die manuelle Ultraschallprüfung. Untersuchung zu menschlichen Faktoren auf die Ergebnisse zerstörungsfreier Prüfungen N2 - Die übergeordnete Zielsetzung unserer Untersuchung bestand darin, am Beispiel von Prüfungen mit Ultraschall eine belastbare Aussage zum Einfluss der Arbeitsbedingungen des Prüfers auf die Qualität der Ergebnisse von zerstörungsfreien Prüfungen zu ermitteln und Möglichkeiten zur Minimierung ungünstiger Einflussfaktoren aufzuzeigen. Der Schwerpunkt der Untersuchung wurde auf die manuelle Ultraschallprüfung gelegt und der Faktor 'Zeitdruck' (in drei Stufen variiert) als die zu variierende physische Einflussgröße gewählt. Die Variation des Faktors Zeitdruck wurde gemäß dem Prozessmodell von der Erhebung psychologischer Faktoren, die das Individuum und die Organisation beschreiben, begleitet. Die Ultraschallprüfungen erfolgten mit zehn Prüfern am Großbehälter und an Vergleichskörpern mit eingebrachten Testfehlern (Nuten, Risse). Die ausgewählten Fehler waren typisch für Prüfaufgaben, die bei wiederkehrenden Ultraschallprüfungen in Kernkraftwerken von den Prüfern zu lösen sind. Die Prüfaufgabe bestand darin, die in den vorgegebenen Prüfabschnitten vorhandenen Reflektoren aufzufinden und deren Amplituden, Ortskoordinaten und Längenerstreckungen zu ermitteln. Als Bewertungsmaßstab für die Qualität der Prüfaussage und für den Einfluss des menschlichen Faktors diente die Präzision der gemessenen Werte. Die Ergebnisse zeigen einen hohen Einfluss des menschlichen Faktors auf das Prüfergebnis und eine Einwirkung des Zeitdrucks besonders auf die Präzision der Messwerte. Hierbei war die Wirkung des individuell wahrgenommenen Zeitdrucks zusammen mit der psychischen Arbeitsbeanspruchung signifikant. Es wurde unter anderem herausgearbeitet, dass durch eine gute Vorbereitung auf die Prüfung, z.B. durch die sorgfältige Einweisung und ein vorgeschaltetes Fertigkeitstraining an Vergleichskörpern, die Zuverlässigkeit der Prüfergebnisse verbessert werden kann. Insgesamt hatte der Faktor 'Organisation' neben der 'Erfahrung' einen hohen Einfluss auf das Leistungsvermögen der Prüfer. Die Projektergebnisse wurden im Abschlussbericht des Forschungsvorhabens SR2514 dargestellt, es wurden drei Empfehlungen zur Vorbereitung und Einweisung der Prüfer, zur Stärkung der Verantwortung der Prüfaufsicht und zum 4-Augen-Prinzip formuliert. Die Empfehlungen wurden in der KTA- Regel 3201.4 'Komponenten des Primärkreises von Leichtwasserreaktoren; Teil 4: Wiederkehrende Prüfungen und Betriebsüberwachung (RÄE Fassung 2010-11)', umgesetzt. T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Germany DA - 30.05.2011 KW - Human factors KW - ZfP KW - Ultraschallprüfung KW - UT KW - Zeitdruck PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-251610 UR - http://jt2011.dgzfp.de/Portals/jt2011/BB/mi2c3.pdf SN - 978-3-940283-33-7 IS - DGZfP-BB 127 (Mi.2.C.3) SP - 1 EP - 9 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-25161 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Maack, Stefan A1 - Schäfer, S. A1 - Braml, T. A1 - Wimmer, J. A1 - Jedlitschka, A. A1 - Kuhn, T. A1 - Fertig, T. A1 - Schütz, A. T1 - CASPAR Construction Administration Shell - Plattform für die beweissichere und rückführbare Datennutzung im Bauwesen N2 - Das zentrale Ziel des Forschungsvorhabens CASPAR ist die Entwicklung einer technischen Lösung zur beweissicheren und rückführbaren Datenbasis von digitalen Informationen zur Bewertung von Bauwerken. Ein konsistentes, semantisches und maschinenlesbares Datenmodell wurde entwickelt, um Daten aus verschiedenen Quellen zu aggregieren und Schnittstellen für die Echtzeit-Kommunikation mit Sensoren zu schaffen. Ein besonderer Schwerpunkt lag auf der Einführung der Verwaltungsschale (Asset Administration Shell, AAS), einer Kerntechnologie der Industrie 4.0, als standardisierten digitalen Zwilling für Brückenbauwerke. Die Verwaltungsschale ermöglicht die strukturierte, interoperable und semantisch eindeutige Darstellung von Bauwerksdaten. Eine Blockchain-basierte Lösung wurde entwickelt, um die sichere und manipulationsresistente Datenübertragung und -ablage zu gewährleisten. Ein Demonstrator, basierend auf der Open Source Plattform Eclipse BaSyx, wurde entwickelt, um die Technologien zu veranschaulichen. Der Demonstrator wurde im November 2024 auf der Messe SPS in Nürnberg vorgestellt. Ein wesentlicher Bestandteil des Forschungsvorhabens war die Entwicklung eines konsistenten, semantischen und maschinenlesbaren Datenmodells für Brückenbauwerke. Dieses Modell ermöglicht die Aggregation von Informationen aus verschiedenen Quellen und die Entwicklung von Schnittstellen für die Echtzeit-Kommunikation mit Sensoren. Ein besonderer Schwerpunkt lag auf der Einführung der Verwaltungsschale (Asset Administration Shell, AAS), einer Kerntechnologie der Industrie 4.0, als standardisierten digitalen Zwilling für Brückenbauwerke. Die Verwaltungsschale ermöglicht die strukturierte, interoperable und semantisch eindeutige Darstellung von Bauwerksdaten. Eine Blockchain-basierte Lösung wurde entwickelt, um die sichere und manipulationsresistente Datenübertragung und -ablage zu gewährleisten. Ein Demonstrator, basierend auf der Open Source Plattform Eclipse BaSyx, wurde entwickelt, um die Technologien zu veranschaulichen. KW - Lebenszyklus KW - Brücken KW - Datenablage KW - Digitalisierung KW - Industrie 4.0 KW - Bauwesen PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-640571 DO - https://doi.org/10.34657/21445 SP - 1 EP - 37 PB - TIB Technische Informationsbibliothek AN - OPUS4-64057 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Pittner, Andreas A1 - Fabry, Çağtay T1 - Abschlussbericht IGF 17.923 N: "Sensorgestütztes MSG-Engspaltschweißen von Feinkornstählen mit modifizierter Prozessführung im Dickblechbereich" N2 - Die im Forschungsvorhaben erzielten Ergebnisse zeigen konkrete technische Lösungen für die automatisierte Anwendung des MSG Engspaltschweißen, sowohl mittels optischer als auch prozessorientierter Sensorik, und sprechen damit ein breites Spektrum möglicher Anwender, insbesondere KMU, an. Die Seitenführung des Brenners auf Basis der optischen Messgrößen stellt eine robuste und einfach zu implementierende Möglichkeit zur Nahtverfolgung dar. Für die Höhenführung über der Schweißnaht wurde neben der Lösung mittels optischer Messverfahren zusätzlich eine direkt darauf aufbauende Möglichkeit zur Implementierung eines Lichtbogensensors abgeleitet. Das Vorgehen konnte sowohl für Sprühlichtbogenprozesse als auch bei Verwendung von Impulslichtbogenprozessen erfolgreich angewendet werden. Die zur Sicherstellung eines gleichmäßigen Flankeneinbrandes entwickelte Pendelregelung ist ebenfalls für unterschiedliche Lichtbogenarten einsetzbar und muss vom Anwender auch beim Einsatz einer großen Bandbreite unterschiedlicher Prozessparameter nahezu nicht konfiguriert werden. Neben der im Rahmen der Verfahrensprüfung untersuchten Pendelraupentechnik konnte die Übertragbarkeit des Vorgehens auch auf die Strichraupentechnik anhand von gezielten Schweißversuchen aufgezeigt werden. Die zunächst auf Basis der optischen Messwerte ausgelegte Füllgradregelung konnte die vorgesehenen Spaltvariationen von 18 bis 24 mm im Rahmen der durchgeführten Verfahrensprüfung ausgleichen. Die Ableitung eines äquivalenten Lichtbogensensors durch Kopplung beider Messprinzipien wurde am Laufzeitende des Vorhabens aufgezeigt, konnte jedoch durch zeitliche Beschränkung nicht für die Verfahrensprüfung berücksichtigt werden. In Absprache mit dem projektbegleitenden Ausschuss wurde die Entwicklung der Prozessregelung für das Vorhaben auf Schweißungen in Wannenlage und Grundwerkstoffe der Güte S355J2 beschränkt. Die Qualifizierung des Verfahrens unter Einsatz der beschriebenen Regelalgorithmen nach DIN EN ISO 15614-1 konnte für alle betrachteten Spaltbreiten zwischen 18 und 24 mm anhand einer 50 mm dicken Demonstratorprobe nachgewiesen werden. KW - Schutzgasschweißen KW - MSG-Engspaltschweißen KW - Prozesssteuerung KW - Lichtbogensensorik KW - Prozessregelung KW - GMAW KW - Narrow gap GMAW KW - GMAW control KW - Arc-sensing PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-390934 SP - 1 EP - 38 AN - OPUS4-39093 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brackrock, Daniel A1 - Recknagel, Christoph A1 - Brekow, Gerhard A1 - Kreutzbruck, Marc T1 - Untersuchungen von Glas-Metall Klebverbindungen mit Hilfe von Ultraschall N2 - Klebverbindungen im modernen Hochbau können helfen, innovative ästhetische Bedürfnisse im Fassadenbau umzusetzen, technologische Verbesserungen zu erreichen, aber auch die Wechselwirkung von Gebäuden mit der Umwelt unter energetischen Aspekten zu optimieren. Aufgrund der hohen sicherheitstechnischen Bedeutung gibt es hohe Anforderungen an die Leistungsfähigkeit, Dauerhaftigkeit und die Gütesicherheit. Mit einer zerstörungsfreien praxistauglichen Prüftechnik, die eine sichere Überprüfung der Integrität von Glas-Metall Klebverbindungen im Ingenieurhochbau gewährleistet, kann sowohl ein wichtiger Beitrag zur Qualitätssicherung bei der Herstellung von Fassadenelementen aber auch bei der späteren Bauwerksüberwachung im Verlauf der Nutzungsdauer geleistet werden. Für eine Beurteilung der Qualität der Verbundfuge (z.B. bezgl. Standsicherheit) sind dabei Aussagen zur Homogenität der Verbundfuge, zum adhäsiven und kohäsiven Verbundverhalten gefordert. Hierzu besteht aktuell insbesondere Bedarf an zerstörungsfreien praxisgerechten, hoch ortsauflösenden und möglichst bildgebenden Untersuchungsverfahren. Es wird mit einem Matrixarray und mit konventionellen Winkelprüfköpfen eine Prüftechnik vorgestellt, mit der die Wechselwirkung zwischen Ultraschallwelle und Fehlstelle in der Klebefuge untersucht wird. Hierbei ist das erste Untersuchungsziel, mit einer angepassten Ultraschall-Prüftechnik mögliche Inhomogenitäten oder Schädigungsstellen in der geklebten Glas-Metall Verbindung zu detektieren. Über diese qualitativen Aussagen hinaus werden weiterführende Informationen über die flächenhafte Ausdehnung und den Ort einer mangelnden Klebung ermittelt. Dazu werden die Messwerte zusammen mit den Positionen des Ultraschallprüfkopfs aufgezeichnet. Mit Hilfe einer bildhaften Auswertung der gemessenen Ultraschallechos in Abhängigkeit vom Prüfkopfort werden die Möglichkeiten einer detaillierten Integritätsanalyse der Glas-Metall Klebschicht dargestellt. In diesem Beitrag werden experimentelle Prüfergebnisse vorgestellt, die im Sinne einer Verfahrensvalidierung an einem speziellen Beispielprobekörper zur Nachstellung einer SSG-Verglasung (ermittelt wurden und die Detektion fehlerhafter Klebestellen in einer Glas-Metall-Klebverbindung zum Ziel haben. T2 - DGZfP-Jahrestagung 2014 CY - Potsdam, Germany DA - 26.05.2014 PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-331181 UR - https://www.ndt.net/?id=17428 SN - 978-3-940283-61-0 VL - 148 SP - 1 EP - 8 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-33118 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schlick-Hasper, Eva A1 - Seidler, Oliver A1 - Goedecke, Thomas A1 - Kraume, M. T1 - Helium leak testing of dangerous goods packagings N2 - The International Dangerous Goods Regulations prescribe the immersion under water method (“bubble test”) as standard method for the leakproofness test of dangerous goods packagings. But this test procedure acts as a test method for leak localisation, not for quantitative leakage rates measurement. Additionally, the sensitivity in detecting leaks of small diameters is restricted, depending on the test liquid and the test pressure. The bubble test is not suitable for a comparison with quantitative limit leakage rates based on realistic transport conditions. This is especially important when estimating the risk of the formation of an explosive atmosphere during the intercontinental carriage of dangerous goods packagings in freight containers. To compare measured leakage rates with limit leakage rates, a quantitative leak testing procedure is required. Therefore a new approach for dangerous goods packagings is implemented: The pressure technique by accumulation using Helium as a tracer gas. This work presents the test equipment necessary for the quantitative measurement of Helium leakage rates through closures of different kinds of dangerous goods packagings. The essential steps to achieve good repeatable results are: A controlled Helium filling process to reach a defined test pressure in the test sample, a sufficient homogenisation of the Helium-air-mixture inside the test sample and the ensuring of a constant pressure level of the test sample during the test. The Helium loss rate of the accumulation chamber has to be measured separately to receive a correction factor for the measured leakage rates. Different constructional measures are introduced to prevent a disturbing influence of the Helium leakage rate of the filling valves on the measurement results. Methods to estimate the disturbing effect of Helium permeation through permeable parts of the test sample are also presented. As a supporting method for the experimental investigations the Helium sniffer test can be applied. This practical application-oriented advice can enable other users to establish a pressure technique by accumulation for their own technical field. T2 - 19th World Conference on Non-Destructive Testing CY - Munich, Germany DA - 13.06.2016 KW - Überdruckverfahren KW - Gefahrgutverpackungen KW - Dichtheit KW - Helium KW - Dangerous goods packagings KW - Leakproofness KW - Helium KW - Pressure technique PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-371376 UR - http://ndt.net/?id=19785 SN - 1435-4934 VL - 21 IS - 7 SP - 1 EP - 10 PB - NDT.net CY - Kirchwald AN - OPUS4-37137 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schlick-Hasper, Eva A1 - Schneider, Uwe A1 - Goedecke, Thomas A1 - Kraume, M. T1 - Durchströmung von Glaskapillaren mit Lachgas und Helium N2 - Distickstoffmonoxid (N2O, Lachgas) und Helium (He) sind gängige Prüfgase für Dichtheitsprüfungen. Die einfachste Leckgeometrie stellt ein ideal zylindrisches Rohr dar. Es wurden Glaskapillaren verschiedener Abmessungen mit Lachgas und Helium durchströmt. Der Überdruck am Kapillareingang lag zwischen 100 mbar und 400 mbar. Es handelte sich um vier annähernd zylindrische Glaskapillaren mit den mittleren Durchmessern: Kapillare 1: ca. 102 μm; Kapillare 2: ca. 71 μm; Kapillare 3B: ca. 49 μm; Kapillare 4: ca. 53 μm. Zudem wurde eine nichtzylindrische Kapillare geprüft (Kapillare 3A). Die Kapillaren 1, 2 und 3B wurden mit beiden Prüfgasen getestet. Kapillare 3A wurde nur mit Lachgas durchströmt, Kapillare 4 nur mit Helium. Für die Messung der Leckageraten kam das Überdruckverfahren mit Ansammlung (Verfahren B3 nach DIN EN 1779: 1999-10) zum Einsatz. Als Detektor für Lachgas diente der Lachgasdetektor Maihak Unor 6 N, für Helium der Leckdetektor T-Guard der Firma Inficon. Es wurden verschiedene Theorieansätze verglichen. Beim Theorieansatz Ib erfolgte die Umrechnung der Lachgas-Messwerte auf die Helium-Messwerte und umgekehrt anhand der Druck-, Temperatur- und Gasartabhängigkeit der Leckagerate für laminar-viskose Gasströmung (DIN EN 1779: 1999-10; DGZfP-Richtlinie DP2: 2009-12). Beim Theorieansatz II wurde die Berechnung der Leckagerate für die laminar-viskose Rohrströmung unter der Annahme einer ideal zylindrischen Kapillare durchgeführt. Zusätzlich wurde mit „ANSYS Fluent“ eine CFD-Simulation vorgenommen. Bei Kapillare 3A wurde eine Serienschaltung der Strömungsleitwerte von Rohr und Düse angesetzt. Bei Anwendung des Ansatzes Ib werden bei Umrechnung der Helium-Messwerte auf Lachgas die Lachgas-Messwerte überschätzt. Umgekehrt werden bei der Umrechnung der Lachgas-Messwerte auf Helium die Helium-Messwerte unterschätzt. Bei Analyse der Einlauflängen der Rohrdurchströmung ist festzustellen, dass diese für Lachgas stets größer als für Helium sind. Bei Lachgas liegt daher für einige Messwerte noch keine ausgebildete laminare Rohrströmung vor. Einlaufeffekte können somit nicht vernachlässigt werden. Als Fazit ergibt sich, dass bei Verwendung von Helium als Prüfgas und Umrechnung der Helium-Messwerte auf Lachgas die Lachgas-Leckageraten sicherheitstechnisch konservativ abgeschätzt werden. T2 - 7. DGZfP-Fachseminar Dichtheitsprüfung und Lecksuche CY - Dortmund, Germany DA - 20.09.2016 KW - Glaskapillaren KW - Lachgas KW - Helium KW - Laminare Strömung PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-396659 UR - http://www.ndt.net/search/docs.php3?MainSource=215 SN - 1435-4934 VL - 22 IS - 4 SP - Vortrag 5, 1 EP - 15 AN - OPUS4-39665 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Lehmann, Jens A1 - Burkert, Andreas T1 - KorroPad - Beurteilung der Korrosionsbeständigkeit von Oberflächen nichtrostender Stähle N2 - Mit dem KorroPad Verfahren ist es dem Anwender möglich den Zustand der Passivschicht nichtrostender Stähle auf sehr einfache und schnelle Weise einschätzen zu können. Das Verfahren eignet sich dazu, den Grad der Passivität in Abhängigkeit der Umgebungsbedingungen und der Zeit nachzuvollziehen. Dies ermöglicht dem Anwender und Verarbeiter von nichtrostenden Stählen, die Lagerungsbedingungen und -zeiten einer frisch bearbeiteten Stahloberfläche zu ermitteln, welche für die Ausbildung einer stabilen Passivschicht notwendig sind, bevor diese risikoarm eingesetzt werden kann. Wie die hier dargestellten Beispiele und auch weitere zahlreiche praktische Anwendungen gezeigt haben, eignet sich das KorroPad ebenfalls für die Identifikation kritischer Prozessparameter bei der Verarbeitung nichtrostender Stähle. Mit dem Verfahren lassen sich viele rozessbedingte Einflussfaktoren auf die Oberflächengüte wie auch auf den Werkstoff charakterisieren. Aufgrund der schnellen und einfachen Auswertung der Prüfergebnisse können positive wie auch negative Veränderungen hinsichtlich der Passivschichtstabilität zügig erkannt werden. Dies ermöglicht es dem Anwender schnell zu reagieren, um kritische Einflüsse zu korrigieren und um eine Optimierung von Inhouse-Prozessen durchzuführen. Weitere Einsatzgebiete sind im Bereich der Wareneingangs- und/oder Warenausgangskontrolle denkbar, überall wo es um die Frage der Passivschichtstabilität einer nichtrostenden Stahloberfläche geht. KW - Korrosionstest KW - nichtrostender Stahl KW - Edelstahl Rostfrei PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-397049 UR - http://www.ndt.net/article/dgzfp-bau-2016/papers/16.pdf SN - 1435-4934 VL - 22 IS - 4 SP - Artikel 16 PB - NDT.net CY - Bad Breising AN - OPUS4-39704 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Maack, Stefan A1 - Bertovic, Marija A1 - Radtke, Martin A1 - et al., ED - Wahlster, W. ED - Winterhalter, C. T1 - Deutsche Normungsroadmap künstliche Intelligenz N2 - Rund ein Jahr haben DIN und DKE in einem gemeinsamen Projekt mit dem Bundesministerium für Wirtschaft und Energie und zusammen mit ca. 300 Fachleuten aus Wirtschaft, Wissenschaft, öffentlicher Hand und Zivilgesellschaft an der Normungsroadmap Künstliche Intelligenz gearbeitet. Eine hochrangige Steuerungsgruppe unter dem Vorsitz von Prof. Wolfgang Wahlster hat die Erarbeitung koordiniert und begleitet. Ziel der Roadmap ist die frühzeitige Entwicklung eines Handlungsrahmens für die Normung und Standardisierung, der die internationale Wettbewerbsfähigkeit der deutschen Wirtschaft unterstützt und europäische Wertmaßstäbe auf die internationale Ebene hebt. KW - Künstliche Intelligenz KW - Normung KW - Roadmap PY - 2020 UR - https://www.din.de/resource/blob/772438/ecb20518d982843c3f8b0cd106f13881/normungsroadmap-ki-data.pdf VL - 2020 SP - 1 EP - 232 PB - Deutsches Institut für Normung (DIN) CY - Berlin ET - 1. AN - OPUS4-51733 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gluth, Gregor ED - Wittke, W. T1 - Alkalisch aktivierter Beton (Geopolymer-Beton) N2 - Alkalisch aktivierte Bindemittel (AAB) sind Zemente, deren Erhärtung auf der alkalischen Anregung von reaktiven Aluminiumsilicaten beruht. AAB sind nach gegenwärtigem Stand die vielversprechendste Option, die mit der Herstellung und dem Einsatz von Zementen verbundenen CO2-Emissionen mittel- bis langfristig signifikant zu senken. Die Erhärtungsreaktionen und die Einflüsse auf die Mikrostruktur von AAB sind durch jahrzehntelange Forschung gut verstanden, und zahlreiche Beispiele belegen, dass AAB grundsätzlich als Betonbindemittel geeignet sind. Offene Fragen bestehen aber immer noch hinsichtlich der Dauerhaftigkeit von mit AAB hergestellten Betonen. Der vorliegende Beitrag gibt eine kurze Einführung in die Nomenklatur und die Geschichte von AAB. Die wichtigsten Reaktionen und Reaktionsprodukte, die zur Bildung der Mikrostruktur von AAB führen, werden beschrieben. Der Hauptteil des Beitrags diskutiert aktuelle Forschungsergebnisse und offene Fragen zur Dauerhaftigkeit von Betonen auf Basis von AAB. Wichtige Fortschritte auf diesem Gebiet konnten in den letzten Jahren insbesondere zum Einfluss von Sulfiden auf die Bewehrungskorrosion, zum Carbonatisierungswiderstand und zum Säurewiderstand erzielt werden. T2 - 10. Felsmechanik- und Tunnelbautag CY - Weinheim, Germany DA - 22.05.2025 KW - Alkali-activated materials KW - Carbonation KW - Reinforcement corrosion KW - MIC KW - Microbially induced corrosion PY - 2025 SN - 978-3-00-083562-9 SP - 73 EP - 84 PB - WBI GmbH CY - Weinheim AN - OPUS4-64266 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine A1 - Gradt, Thomas T1 - Friction and wear behaviour of graphite filled polymer composites in hydrogen environment N2 - Ensuring a sustainable energy supply is currently one of the most important areas for industry and research institutions. Hydrogen technology is a promising candidate, but its broad extension requires extremely high reliability and safety in all areas for common applications as automobiles and stationary fuel cells. Particularly components containing tribosystems are critical parts. T2 - WTC 2013 - 5th World tribology congress CY - Torino, Italy DA - 08.09.2013 PY - 2013 SP - Paper 868, 1 EP - 2 AN - OPUS4-30942 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Vollpracht, A. A1 - Thiel, C. A1 - Zhao, Z. A1 - Villagrán Zaccardi, Y. A. A1 - Cordoba, G. P. A1 - Gluth, Gregor A1 - Vanoutrive, H. A1 - Gruyaert, E. A1 - Kanellopoulos, A. A1 - Mi, R. A1 - De Belie, N. T1 - Carbonation of concrete with SCMs: a data analysis by RILEM TC 281-CCC N2 - The RILEM TC 281–CCC "Carbonation of concrete with supplementary cementitious materials" is studying the effect of supplementary cementitious materials (SCMs) on natural and accelerated carbonation of blended cements. In this context a large database with carbonation depths over time has been set-up with currently 910 concrete and mortar mixes, which have been tested at different curing conditions. The collected data includes information on chemical composition and physical properties of the raw materials, on mix-design, compressive strength, curing and carbonation testing conditions. Data for a large variety of binders (with up to 94 % SCMs) and mix designs (with w/b ratios ranging from 0.26 to 0.75) were collected from the literature and unpublished material testing projects. Natural carbonation was recorded for several years in many cases, and indoor as well as outdoor results are included. However, in this contribution only lab conditions are considered. Carbonation kinetics are investigated considering the binder composition and mix design. Furthermore, the accuracy of accelerated carbonation testing is evaluated. As described in literature, the w/CaOreactive-ratio is a decisive factor for carbonation resistance but curing and exposure conditions influence the results as well. Even with identical test conditions, the scatter is very large. T2 - 16th International Congress on the Chemistry of Cement 2023 (ICCC2023) CY - Bangkok, Thailand DA - 18.09.2023 KW - Carbonation KW - Supplemetary cementitious materials KW - Blended cement KW - Concrete PY - 2023 UR - https://www.iccc-online.org/fileadmin/gruppen/iccc/proceedings/ICCC16_2023_Vol_III.pdf VL - III SP - 360 EP - 363 PB - Thailand Concrete Association AN - OPUS4-58736 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sturm, Patrick A1 - Gluth, Gregor A1 - Lindemann, Mathias A1 - Greiser, Sebastian A1 - Jäger, Christian A1 - Brouwers, H.J.H. ED - Bernal, S.A. ED - Provis, J.L. T1 - Structural investigations on one-part geopolymers after different drying regimes T2 - 34th Cement and concrete science conference CY - Sheffield, UK DA - 2015-09-14 KW - Geopolymers KW - One-part mix PY - 2015 SP - 37 EP - 40 AN - OPUS4-34554 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reiche, I. A1 - Berger, Achim A1 - Görner, Wolf A1 - Merchel, Silke A1 - Radtke, Martin A1 - Riederer, J. A1 - Riesemeier, Heinrich T1 - Dürer's chemischer Fingerprint - Untersuchungen mittels Synchrotron-induzierter Röntgenfluoreszenzanalyse T2 - 5. Erfurter Fachtage für Konservierung und Restaurierung CY - Erfurt, Germany DA - 2002-11-28 PY - 2002 AN - OPUS4-2123 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Henning, Ricky A1 - Sturm, Patrick A1 - Kühne, Hans-Carsten A1 - Keßler, S. A1 - Gluth, Gregor T1 - Untersuchungen zur Wärmeentwicklung von hybriden Zementen N2 - Die Hauptfunktion von Verschlussbauwerken für End- und Zwischenlager von radioaktiven Abfällen besteht in der Erhaltung der geologischen Barriere. Vor allem soll ein potenzieller Stofftransport durch eine möglichst geringe Permeabilität des Bauwerks verhindert bzw. auf vernachlässigbare Werte herabgesetzt werden. Die in-situ-Permeabilität des Verschlussbauwerks steht dabei in direktem Zusammenhang mit dessen Poren- und Makrostruktur, welche bei Bauwerken auf Basis von Beton insbesondere durch Schwind-verformungen und durch thermisch induzierte Rissbildung infolge der Reaktionswärmeentwicklung des Bindemittels gestört werden kann. Die Betone müssen daher neben einer hohen chemischen Langzeitstabilität auch eine geringe bzw. langsame Wärmeentwicklung während der Erhärtungsreaktionen aufweisen. Als hybride Zemente werden Mischungen aus Portlandzement, Betonzusatzstoffen und einem alkalischen Aktivator bezeichnet. Dabei können u. a. Alkalisulfate, Alkalicarbonate, Alkalisilicate und Alkalihydroxide als Aktivatoren zum Einsatz kommen. Aufgrund ihrer hohen chemischen Stabilität im salinaren Milieu sind Betone aus solchen Zementen potenziell besonders gut als Verfüllmaterial für End- und Zwischenlager im Steinsalz geeignet. In der vorliegenden Studie wurden daher hybride Zemente hinsichtlich ihrer Wärmeentwicklung in einem isothermen Kalorimeter sowie hinsichtlich Phasenbestand und Festigkeiten untersucht. Hybride Zementleime wurden auf Basis von Portlandklinker, Hüttensandmehl, Flugasche und Natriumsulfat hergestellt und die Zusammensetzungen systematisch variiert, um den Einfluss der Komponenten auf Wärmeentwicklung, Phasenbestand und mechanische Eigenschaften der Leime zu untersuchen; zusätzlich wurden zu Vergleichszwecken ein Zementleim auf Basis der Betonrezeptur M2 sowie eine alkalisch aktivierte Flugasche untersucht. T2 - 2. Tage der Standortauswahl CY - Online meeting DA - 11.02.2021 KW - Hybride Zemente KW - Hydratationswärme KW - Kalorimetrie PY - 2021 SP - 137 EP - 139 AN - OPUS4-52216 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hlavacek, Petr A1 - Gluth, Gregor A1 - Reinemann, Steffi A1 - Ebell, Gino A1 - Kühne, Hans-Carsten A1 - Mietz, Jürgen T1 - Corrosion of steel reinforcement in geopolymer mortars - carbonation resistance, chloride migration, and preliminary corrosion potential data N2 - Alkali-activated materials such as geopolymers are currently receiving a lot of attention because of their potential to be used as binders for concrete with advantageous engineering properties and reduced manufacturing CO2 emissions. Knowledge of the durability of steel in these concretes and related properties of alkali-activated materials is a prerequisite for their application as building materials, if they are to be used for steel reinforced elements. However, to date only limited data exists on this topic. The present contribution focuses on durability-related transport properties of geopolymer-based mortars (as model systems for concrete). We report results of accelerated carbonation, rapid chloride migration (RCM) and air permeability measurements as well as porosity data for fly ash-based geopolymer mortars, including mixes containing ground granulated blast furnace slag (GGBFS). In addition, we report polarization resistance data and corrosion potential vs. time curves for carbon steel bars embedded in two of the fly ash-based geopolymer mortars and a CEM I-based mortar (as reference). Despite comparable total porosities, the carbonation depths, the chloride migration coefficients and the air permeabilities of the mortars differed significantly. In general, the addition of GGBFS to the binders improved the performance (decreased transport coefficients); however, this was not found to be true for the air permeability in all cases. This latter effect can be explained by drying damage of the C-(A-)S-H gel in GGBFS-containing binders. On the other hand, low transport coefficients can also be achieved by optimization of the binder formulation without the addition of GGBFS, which is also reflected in the material’s air permeability. Thus, there exists no simple correlation between air permeability (of harshly dried mortars) and durability-related transport coefficients for the studied alkali-activated materials. The corrosion potential vs. time curves in combination with polarization resistance values reveal that the steel reinforcement in geopolymer mortars assumed a passive state. However, this happened considerably later than for steel in CEM I-based mortars. The free corrosion potential of carbon steel reinforcement in the geopolymer mortars had different values than the free corrosion potential values for the CEM I-based mortar for both the active and the passive state; possible reasons for this behavior are discussed. T2 - EUROCORR 2017 CY - Prague, Czech Republic DA - 03.09.2017 KW - Geopolymers KW - Alkali-activated materials KW - Corrosion KW - Steel reinforcement KW - Concrete PY - 2017 SP - Paper 87351, 1 EP - 7 AN - OPUS4-41870 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mundra, S. A1 - Furcas, F. E. A1 - Huthwelker, T. A1 - Simon, Sebastian A1 - Borca, C. N. A1 - Provis, J. L. A1 - Gluth, Gregor T1 - Kinetics of Sulfide Oxidation in alkaline solutions studied by X-ray absorption near-edge structure spectroscopy N2 - The oxidation of sulfur in aqueous solutions is an important process in several geochemical and industrial contexts. In concrete technology, it is particularly relevant for the protection of steel reinforcement in slag cement-based concretes, as the presence of sulfides affects the passivation of the steel and corrosion initiation in the presence of chlorides. However, the knowledge about the kinetics of sulfide oxidation in alkaline solutions, such as concrete pore solutions, is incomplete. To address this issue, we prepared solutions with 0.80 M NaOH, and nominally 10, 100 and 350 mM HS−, respectively, and followed the evolution of the sulfur species during bubbling with oxygen-containing gas (concentration 100% or 22%) using X-ray absorption near-edge structure (XANES) spectroscopy at the sulfur K-edge. Polysulfide, thiosulfate, sulfite and sulfate were identified and quantified via linear combination fitting of the spectra, using previously measured standards. A preliminary analysis of the results shows that the initial rate constant of sulfide oxidation depends strongly on the HS− concentration, while it less strongly depending on the oxygen concentration, in line with previous results for lower pH values. Approaches to fit the data to obtain the rate constants of all relevant reactions will be discussed. T2 - 41st Cement & Concrete Science Conference CY - Leeds, Great Britain DA - 12.09.2022 KW - XANES KW - Sulfide oxidation KW - Kinetics PY - 2022 SP - 1 EP - 3 PB - Institute of Materials, Minerals & Mining (IOM3) AN - OPUS4-55650 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gluth, Gregor A1 - Oppat, Klaus A1 - Vogler, Nico A1 - Kühne, Hans-Carsten ED - Littmann, K. T1 - Vergleich unterschiedlicher Verfahren zur Messung der Oberflächenrauheit N2 - Die Oberflächenrauheit eines Bauteils ist eine wichtige Kenngröße für zahlreiche seiner Eigenschaften. Der im Bauwesen übliche Rauheitsparameter ist die Rautiefe Rt bzw. MTD, die durch volumetrische Verfahren (Sandflächenverfahren) ermittelt wird und in zahlreichen Normen Verwendung findet. Laserbasierte Verfahren müssen deshalb eine Umrechnung der aus Oberflächenprofilen gewonnenen Informationen in Rt bzw. MTD ermöglichen. Hierzu wird i.A. ein empirischer Zusammenhang zwischen Parametern zur Beschreibung des Profils und der Rautiefe der entsprechenden Oberfläche verwendet. Der Aufsatz stellt verschiedene Rauheitsdefinitionen vor und vergleicht sie miteinander. Es wird ferner gezeigt, dass die nach verschiedenen Prüfvorschriften ermittelten Rautiefen voneinander abweichen. Das Vorgehen bei der Ermittlung des Zusammenhangs zwischen Profilparametern und Rautiefen nach einem volumetrischen Verfahren wird demonstriert und der Stand der laufenden Entwicklung eines Prüfgeräts auf Basis eines Linienlasers vorgestellt. T2 - 7. Internationales Kolloquium Industrieböden 2010 CY - Ostfildern, Germany DA - 14.12.2010 KW - Rauheit KW - Rautiefe KW - Volumetrische Methode KW - Sandflächenverfahren KW - Laserverfahren KW - Linienlaser PY - 2010 SN - 3-924813-85-X SP - 135 EP - 141 PB - Technische Akademie Esslingen (TAE) CY - Ostfildern AN - OPUS4-22855 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Cuéllar, Pablo A1 - Benseghier, Z. A1 - Luu, L.-H. A1 - Bonelli, S. A1 - Delenne, J.-Y. A1 - Radjai, F. A1 - Philippe, P. T1 - Numerical insight into the micromechanics of jet erosion of a cohesive granular material N2 - Here we investigate the physical mechanisms behind the surface erosion of a cohesive granular soil induced by an impinging jet by means of numerical simulations coupling fluid and grains at the microscale. The 2D numerical model combines the Discrete Element and Lattice Boltzmann methods (DEM-LBM) and accounts for the granular cohesion with a contact model featuring a paraboloidal yield surface. Here we review first the hydrodynamical conditions imposed by the fluid jet on a solid granular packing, turning then the attention to the impact of cohesion on the erosion kinetics. Finally, the use of an additional subcritical debonding damage model based on the work of Silvani and co-workers provides a novel insight into the internal solicitation of the cohesive granular sample by the impinging jet. T2 - 8th International Conference on Micromechanics on Granular Media CY - Montpellier, France DA - 03.07.2017 KW - Micromechanical modelling KW - LBM-DEM KW - Jet erosion KW - Granular cohesion KW - Subcritical debonding PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-411186 DO - https://doi.org/10.1051/epjconf/201714015017 VL - 140 SP - Paper 15017, 1 EP - Paper 15017, 4 PB - The European Physical Journal (EPJ) - Web of Conferences AN - OPUS4-41118 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brunier-Coulin, F. A1 - Sarrat, J.-L. A1 - Cuéllar, Pablo A1 - Philippe, P. T1 - Experimental investigation of impinging jet erosion on model cohesive granular materials N2 - Erosion of soils affects both natural landscapes and engineering constructions as embankment dams or levees. Improving the safety of such earthen structures requires in particular finding out more about the elementary mechanisms involved in soil erosion. Towards this end, an experimental work was undertaken in three steps. First, several model materials were developed, made of grains (mostly glass beads) with solid bridges at particle contacts whose mechanical yield strength can be continuously varied. Furthermore, for most of them, we succeeded in obtaining a translucent system for the purpose of direct visualization. Second, these materials were tested against surface erosion by an impinging jet to determine a critical shear stress and a kinetic coefficient. Note that an adapted device based on optical techniques (combination of Refractive Index Matching and Planar Laser Induced Fluorescence) was used specifically for the transparent media. Third, some specifically developed mechanical tests, and particularly traction tests, were implemented to estimate the mechanical strength of the solid bridges both at micro-scale (single contact) and at macro-scale (sample) and to investigate a supposed relationship with soil resistance to erosion. T2 - 8th International Conference on Micromechanics on Granular Media CY - Montpellier, France DA - 03.07.2017 KW - Erosion onset KW - Experimental testing KW - Cohesive granular media KW - RIM-PLIF techniques PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-411215 DO - https://doi.org/10.1051/epjconf/201714008002 VL - 140 SP - Paper 08002, 1 EP - Paper 08002, 4 PB - The European Physical Journal (EPJ) - Web of Conferences AN - OPUS4-41121 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Niederleithinger, Ernst A1 - Abraham, O. A1 - Mooney, M. T1 - Geophysical methods in civil engineering: Overview and new concepts N2 - Geophysical methods have been used in civil engineering for decades. The main field of application is - to no surprise – in geotechnical projects from site characterization to foundation quality assurance. For more than 25 years, ground penetrating radar (GPR) and seismic methods have found applications in structural engineering. Recently introduced geophysical methods have been adopted to ultrasonic investigations in various fields. They help to improve the quality of structural imaging and to detect small changes in concrete. An overview of the history and current use of geophysics in civil engineering is given. Selected examples of new concepts include advances in wave based imaging, quality assurance for foundations, detecting small changes in concrete as well as moisture and corrosion detection are discussed. T2 - NDT-CE 2015 - International symposium non-destructive testing in civil engineering CY - Berlin, Germany DA - 15.09.2015 KW - Nondestructive testing KW - Civil engineering KW - Geophysics PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-344666 UR - https://www.ndt.net/?id=18260 SN - 1435-4934 VL - 20 IS - 11 SP - 1 EP - 6 PB - NDT.net CY - Kirchwald AN - OPUS4-34466 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Philippe, P. A1 - Cuéllar, Pablo A1 - Brunier-Coulin, F. A1 - Luu, L.-H. A1 - Benahmed, N. A1 - Bonelli, S. A1 - Delenne, J.-Y. T1 - Physics of soil erosion at the microscale N2 - We focus here on the major and still relevant issue of soil erosion by fluid flows, and more specifically on the determination of both a critical threshold for erosion occurrence and a kinetics that specifies the rate of eroded matter entrainment. A state-of-the-art is first proposed with a critical view on the most commonly used methods and erosion models. It is then discussed an alternative strategy, promoting the use of model materials that allow systematic parametric investigations with the purpose of identifying more precisely the local mechanisms responsible for soil particle erosion and ultimately quantifying both critical onsets and kinetics, possibly through existing or novel empirical erosion laws. Finally, we present and discuss several examples following this methodology, implemented either by means of experiments or numerical simulations, and coupling erosion tests in several particular hydrodynamical configurations with wisely selected mechanical tests. T2 - 8th International Conference on Micromechanics on Granular Media CY - Montpellier, France DA - 03.07.2017 KW - Erosion phenomena KW - Onset of jet erosion KW - LBM-DEM numerical simulation KW - Experimental testing KW - PLIF-RIM optical techniques PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-411198 DO - https://doi.org/10.1051/epjconf/201714008014 VL - 140 SP - Paper 08014, 1 EP - Paper 08014, 4 PB - The European Physical Journal (EPJ) - Web of Conferences AN - OPUS4-41119 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erhard, Anton A1 - Goedecke, Thomas A1 - Menrad, Andreas A1 - Bethke, John T1 - Application of nondestructive testing - Methods for packaging examination N2 - Nondestructive testing (NDT) methods are applicable in many ways for defect detection as well as optimization of packaging production processes. The visual inspection method is the technique which is mostly used, although neither the customer nor a skilled inspector may be aware of this. Techniques like ultrasound for wall thickness measurement, the application of x-ray techniques or the use of dye penetrant techniques for crack detection are rather well known to the NDT family. However, acoustic emission techniques can also be helpful for the characterization of packaging materials. In this paper the employment of x-ray computer tomography (CT) for measurement of wall thickness in plastic jerrycans, especially on the edges, and its possible optimization of production processes will be discussed. A comparison of the CT and ultrasonic examinations of wall thickness and the reliability of this measured data are also important points for the discussion, especially if some safety factors can be derived from the results. The leakage test is also good for jerrycans, IBCs or other kinds of drums for the transportation and storage of dangerous goods. The disadvantage of this kind of test is that a lack of quality, e.g. wall thickness deterioration, cannot be detected if the wall thickness withstands the internal pressure. Therefore, especially for Quality assurance, the other, previously mentioned techniques are better for a statistical assessment of a batch. This paper is focused on the comparison of different NDT results with special emphasis on the large range of material mechanical properties. T2 - 25th IAPRI Symposium on Packaging CY - Berlin, Germany DA - 16.05.2011 KW - Materialeigenschaft KW - Zerstörungsfreie Prüfung KW - Computertomographie KW - Kunststoffbehälter PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-239191 SN - 978-3-940283-31-3 VL - 126 SP - 1 EP - 7 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-23919 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Niederleithinger, Ernst A1 - Wolf, Julia A1 - Mielentz, Frank A1 - Wiggenhauser, Herbert T1 - Using embedded ultrasonic sensors for active and passive concrete monitoring N2 - Challenging new constructions and ageing infrastructure are increasing the demand for permanent monitoring of loads and condition. Various methods and sensors are used for this purpose. But the technologies available today have difficulties in detecting slowly progressing locally confined damages. Extensive investigations or instrumentations are required so far for this purpose. In this study we present new sensors and data processing methods for ultrasonic transmission, which can be used for non-destructive long term monitoring of concrete. They can be mounted during construction or thereafter. Larger volumes can be monitored by a limited number of sensors for changes of material properties. The principles of ultrasonic transmission and influencing factors are presented. This latter include load, damages as well as environmental parameters as temperature or moisture. Various methods for data processing, e. g. coda wave interferometry are introduced. They allow the detection of very small changes in the medium. The embedded sensors are shown including mounting and operation. Application examples so far include small scale laboratory freeze-thaw experiments, localizing loads in larger concrete models, monitoring load effects on real structures as well as detecting acoustic events. Some sensors are operating already for several years. The sensors can be used as transmitter or receivers or switched between both roles. While most of the previous experiments have been active (at least one sensor serving as transmitter), new studies show that the sensors are useful as well for passive measurements, e. g. in acoustic emission or time reversal experiments. Besides application in civil engineering our setups can also be used for model studies in geosciences. T2 - NDT-CE 2015 - International symposium non-destructive testing in civil engineering CY - Berlin, Germany DA - 15.09.2015 KW - SHM KW - Monitoring KW - Ultrasound concrete KW - Embedded sensors PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-344652 UR - http://www.ndt.net/?id=18408 SN - 1435-4934 VL - 20 IS - 11 SP - 1 EP - 4 PB - NDT.net CY - Kirchwald AN - OPUS4-34465 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Schork, Benjamin T1 - Fracture mechanics based determination of the fatigue strength of weldments N2 - A fracture mechanics model which shall be applied to the fatigue strength determination of weldments has to focus on various aspects such as: (a) the description of mechanical and physical short fatigue crack extension which is characterised by yielding conditions which do not permit the application of the common ΔK concept and by the gradual build-up of the crack closure effect, (b) a consistent methodology for determining the initial crack size, (c) based on this, the determination of a fatigue limit, (d) the treatment of multiple crack propagation at load levels above this limit, (e) the variation of the local geometry along the weld toe, and (f) statistical effects.The paper gives alimited overview of the work the authors did in this field during the last years within the German project cluster IBESS. A model is presented and briefly discussed which covers the questions above. T2 - XV Portugese Conference on Fracture CY - Lissabon, Portugal DA - 10.02.2016 KW - Weldments KW - fatigue strength KW - fracture mechanics KW - fatigue crack propagation PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-361571 UR - http://www.sciencedirect.com/science/article/pii/S2452321616000044 DO - https://doi.org/doi:10.1016/j.prostr.2016.02.003 VL - 2016/1 SP - 10 EP - 17 PB - Elsevier B.V. CY - Amsterdam, Netherlands AN - OPUS4-36157 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fiedler Bremer, C. A1 - Scholz, R. A1 - Myslicki, S. A1 - Starke, P. A1 - Boller, C. A1 - Walther, F. A1 - Krause, Martin T1 - NDT-based characteriazation of timber and vulcanized fiber for civil infrastructure N2 - The paper addresses beech wood as well as vulcanized fiber and discusses the results obtained when using acoustic emission and thermography as non-destructive testing techniques along tensile and load increase fatigue tests to characterize the wooden material’s behavior under increasing fatigue loads to get enhanced information regarding the fatigue behavior of both materials. Reference is mainly made to the materials’ anisotropic and microstructural behavior and what implications this has with respect to the materials’ strength. The influence of moisture is discussed, as well as parameters that may deserve monitoring in the sense of structural health monitoring to be applied in timber structures in general. T2 - NDT-CE 2015 - International symposium non-destructive testing in civil engineering CY - Berlin, Germany DA - 15.09.2015 KW - Ermüdung KW - Belastungsversuch KW - Thermographie KW - ZfP KW - Timber PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-346377 UR - https://www.ndt.net/?id=18419 SN - 1435-4934 VL - 20 IS - 11 SP - 1 EP - 11 PB - NDT.net CY - Kirchwald AN - OPUS4-34637 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Helmerich, Rosemarie A1 - Mielentz, Frank A1 - Milmann, Boris A1 - Adam, Louisa A1 - Villalobos, S. A1 - Guimaraes, M. A1 - Wiggenhauser, Herbert T1 - Detection of cracks perpendicular to the surface using acoustic methods N2 - Cracks perpendicular to the surface may be initial indicators for a deterioration process of concrete structures. Moisture penetrates inside the structure and transports adverse chemicals. The paper presents an investigation about the reliability of available commercial non-destructive evaluation techniques to reliably estimate the depth of surface-breaking cracks in reinforced concrete structures. Aim of the study was the investigation of surface-braking cracks under laboratory conditions. Commercial acoustic devices as impact echo equipment, single ultrasonic transducers and arrays were applied even if they have not been developed for this purpose. The commercial software and descriptions for application was followed strictly to compare the function, precision and repeatability of the measurements. Both, perpendicular notches and cracks have been considered. The study was completed with a discussion about reference specimens. The study was the basis for formulation of gaps in research. The Electric Power Research Institute (EPRI) has initiated and funded a Project. T2 - NDT-CE 2015 - International symposium non-destructive testing in civil engineering CY - Berlin, Germany DA - 15.09.2015 KW - Acoustic test KW - Commercial acoustic devices KW - Ultrasonic test KW - Crack depth KW - Concrete specimens PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-345729 UR - https://www.ndt.net/?id=18412 SN - 1435-4934 VL - 20 IS - 11 SP - 1 EP - 9 PB - NDT.net CY - Kirchwald AN - OPUS4-34572 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Feldmann, Rüdiger A1 - Zoёga, Andreas A1 - Milmann, Boris A1 - Krause, Martin T1 - Ortung tiefliegender Bewehrung durch Ultraschall mit bildgebender Phasenauswertung N2 - Die Ortung von schlaffer Bewehrung in Beton erfolgt routinemäßig mit bildgebenden Radar- oder Wirbelstromverfahren. Die Anwendung dieser Verfahren ist aber begrenzt, wenn es sich um die Ortung tiefliegender Bewehrung (ab ca. 30 cm) oder um jungen Beton handelt. Grund ist die Schwächung der Radarpulse durch oberflächennahe Bewehrung oder durch die Betonfeuchte. Das bildgebende Ultraschallechoverfahren bietet den Vorteil, dass die Ultraschallpulse in diesen Fällen eine wesentlich höhere Eindringtiefe erreichen. Im vorliegenden Beitrag wird eine Fallstudie vorgestellt, bei der mehrlagig eingebrachte Bewehrungseisen in einer nur einseitig zugänglichen 60 cm dicken Betonplatte geortet werden sollten, um eine Kernbohrung ohne Verkanten der Bohrkrone durchzuführen. Zur Ortung der Bewehrung wurde das Ultraschallechoverfahren mitScherwellen der Mittenfrequenz 50 kHz mit einem automatisch arbeitenden Bauwerksscanner eingesetzt. Aus den flächig aufgenommenen Messdaten wurde mit der Rekonstruktionsrechnung nach dem Prinzip der synthetischen Apertur (SAFT, Synthetic Aperture Focusing Technique) die Position der Bewehrungseisen bildhaft ortsgenau dargestellt. Dies gelingt mit einer Auswertungsoption, bei der die Phase der reflektierten Ultraschallpulse ermittelt und farbcodiert dargestellt wird (Phasenauswertung). Damit lassen sich Reflexionen der Bewehrung eindeutig von eventuellen Fehlstellen oder Rückwandechos unterscheiden. T2 - Fachtagung Bauwerksdiagnose 2014 CY - Berlin, Germany DA - 13.02.2014 KW - Ultraschallecho-Verfahren KW - SAFT KW - Bewehrung KW - Beton KW - Abbildungsverfahren PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-351056 UR - https://www.ndt.net/?id=15885 SN - 1435-4934 VL - 19 IS - 8 SP - 1 EP - 11 PB - NDT.net CY - Kirchwald AN - OPUS4-35105 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Völker, Christoph A1 - Shokouhi, P. T1 - Data aggregation for improved honeycomb detection in concrete using machine learning-based algorithms N2 - We present the results of several machine learning (ML)- inspired data fusion algorithms applied to multi-sensory nondestructive testing (NDT) data. Our dataset consists of Impact-Echo (IE), Ultrasonic Pulse Echo (US) and Ground Penetrating Radar (GPR) data collected on large-scale concrete specimens with built–in simulated honeycombing defects. The main objective is to improve the detectability of honeycombs by fusing the information from the three different sensors. We describe normalization, feature detection and optimal feature selection. We have used unsupervised and supervised ML, i.e., classification and clustering, for data fusion. We demonstrate the advantage of data fusion in reducing the false positives up to 10% compared to the best single sensor, thus, improving the detectability of the defects. The methods were evaluated on a concrete specimen. The effectiveness of the proposed approach was demonstrated on a separate full-scale concrete specimen. The results indicate the transportability of the conclusions from one specimen to the other. T2 - NDT-CE 2015 - International symposium non-destructive testing in civil engineering CY - Berlin, Germany DA - 15.09.2015 KW - Data fusion KW - Concrete evaluation KW - Honeycombing KW - Machine learning KW - Clustering PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-350968 UR - https://www.ndt.net/?id=18364 SN - 1435-4934 VL - 20 IS - 11 SP - 1 EP - 8 PB - NDT.net CY - Kirchwald AN - OPUS4-35096 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rothbart, Nick A1 - Maierhofer, Christiane A1 - Goldammer, M. A1 - Hohlstein, F. A1 - Koch, J. A1 - Kryukov, I. A1 - Mahler, G. A1 - Stotter, B. A1 - Oswald-Tranta, B. A1 - Sengebusch, M. T1 - A round robin test of flash thermography of CFRP and metal structures N2 - Within the scope of a DIN INS project, a flash thermography round robin test that evaluates reliability, comparability and efficiency of different testing situations is organized. The results give information about the detectability of defects e.g. by their size and depth, the evaluation method and by the materials used. Besides, the influence of equipment and parameters used by the participants on the results were analysed. All of the quantitative results as well as the feedback given by the participants will be presented in a DIN committee in order to contribute to a flash thermography standard. T2 - 7th International Symposium on NDT in Aerospace CY - Bremen, Germany DA - 16.11.2015 KW - Flash thermography KW - Round robin test KW - Metal KW - Flat bottom holes KW - SNR PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-351070 UR - https://www.ndt.net/?id=18921 SN - 1435-4934 VL - 21 IS - 4 SP - 1 EP - 8 PB - NDT.net CY - Kirchwald AN - OPUS4-35107 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lehmann, Jens A1 - Burkert, Andreas T1 - KorroPad - Beurteilung der Korrosionsbeständigkeit von Oberflächen nichtrostender Stähle N2 - Mit dem KorroPad Verfahren ist es dem Anwender möglich den Zustand der Passivschicht nichtrostender Stähle auf sehr einfache und schnelle Weise einschätzen zu können. Das Verfahren eignet sich dazu, den Grad der Passivität in Abhängigkeit der Umgebungsbedingungen und der Zeit nachzuvollziehen. Dies ermöglicht dem Anwender und Verarbeiter von nichtrostenden Stählen, die Lagerungsbedingungen und –zeiten einer frisch bearbeiteten Stahloberfläche zu ermitteln, welche für die Ausbildung einer stabilen Passivschicht notwendig sind, bevor diese risikoarm eingesetzt werden kann. Wie die hier dargestellten Beispiele und auch weitere zahlreiche praktische Anwendungen gezeigt haben, eignet sich das KorroPad ebenfalls für die Identifikation kritischer Prozessparameter bei der Verarbeitung nichtrostender Stähle. Mit dem Verfahren lassen sich viele prozessbedingte Einflussfaktoren auf die Oberflächengüte wie auch auf den Werkstoff charakterisieren. Aufgrund der schnellen und einfachen Auswertung der Prüfergebnisse können positive wie auch negative Veränderungen hinsichtlich der Passivschichtstabilität zügig erkannt werden. Dies ermöglicht es dem Anwender schnell zu reagieren, um kritische Einflüsse zu korrigieren und um eine Optimierung von Inhouse-Prozessen durchzuführen. Weitere Einsatzgebiete sind im Bereich der Wareneingangs- und/oder Warenausgangskontrolle denkbar, überall wo es um die Frage der Passivschichtstabilität einer nichtrostenden Stahloberfläche geht. T2 - Fachtagung Bauwerksdiagnose - Praktische Anwendungen Zerstörungsfreier Prüfungen und Zukunftsaufgaben CY - Berlin, Germany DA - 25.02.2016 KW - Korrosionsschnelltest, Nichtrostender Stahl, Passivschicht, KorroPad PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-355146 SN - 978-3-940283-77-1 VL - 157 SP - 1 EP - 7 PB - Deutsche Gesellschaft für zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-35514 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schlick-Hasper, Eva A1 - Schneider, Uwe A1 - Goedecke, Thomas A1 - Kraume, M. T1 - Durchströmung von Glaskapillaren mit Lachgas und Helium N2 - Distickstoffmonoxid (N2O, Lachgas) und Helium (He) sind gängige Prüfgase für Dichtheitsprüfungen. Die einfachste Leckgeometrie stellt ein ideal zylindrisches Rohr dar. Es wurden Glaskapillaren verschiedener Abmessungen mit Lachgas und Helium durchströmt. Der Überdruck am Kapillareingang lag zwischen 100 mbar und 400 mbar. Es handelte sich um vier annähernd zylindrische Glaskapillaren mit den mittleren Durchmessern: Kapillare 1: ca. 102 μm; Kapillare 2: ca. 71 μm; Kapillare 3B: ca. 49 μm; Kapillare 4: ca. 53 μm. Zudem wurde eine nichtzylindrische Kapillare geprüft (Kapillare 3A). Die Kapillaren 1, 2 und 3B wurden mit beiden Prüfgasen getestet. Kapillare 3A wurde nur mit Lachgas durchströmt, Kapillare 4 nur mit Helium. Für die Messung der Leckageraten kam das Überdruckverfahren mit Ansammlung (Verfahren B3 nach DIN EN 1779: 1999-10) zum Einsatz. Als Detektor für Lachgas diente der Lachgasdetektor Maihak Unor 6 N, für Helium der Leckdetektor T-Guard der Firma Inficon. Es wurden verschiedene Theorieansätze verglichen. Beim Theorieansatz Ib erfolgte die Umrechnung der Lachgas-Messwerte auf die Helium-Messwerte und umgekehrt anhand der Druck-, Temperatur- und Gasartabhängigkeit der Leckagerate für laminar-viskose Gasströmung (DIN EN 1779: 1999-10; DGZfP-Richtlinie DP2: 2009-12). Beim Theorieansatz II wurde die Berechnung der Leckagerate für die laminar-viskose Rohrströmung unter der Annahme einer ideal zylindrischen Kapillare durchgeführt. Zusätzlich wurde mit „ANSYS Fluent“ eine CFD-Simulation vorgenommen. Bei Kapillare 3A wurde eine Serienschaltung der Strömungsleitwerte von Rohr und Düse angesetzt. Bei Anwendung des Ansatzes Ib werden bei Umrechnung der Helium-Messwerte auf Lachgas die Lachgas-Messwerte überschätzt. Umgekehrt werden bei der Umrechnung der Lachgas-Messwerte auf Helium die Helium-Messwerte unterschätzt. Bei Analyse der Einlauflängen der Rohrdurchströmung ist festzustellen, dass diese für Lachgas stets größer als für Helium sind. Bei Lachgas liegt daher für einige Messwerte noch keine ausgebildete laminare Rohrströmung vor. Einlaufeffekte können somit nicht vernachlässigt werden. Als Fazit ergibt sich, dass bei Verwendung von Helium als Prüfgas und Umrechnung der Helium-Messwerte auf Lachgas die Lachgas-Leckageraten sicherheitstechnisch konservativ abgeschätzt werden. T2 - 7. DGZfP-Fachseminar Dichtheitsprüfung und Lecksuche CY - Dortmund, Germany DA - 20.09.2016 KW - Laminare Strömung KW - Glaskapillaren KW - Lachgas KW - Helium PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-380965 UR - http://www.dgzfp.de/seminar/lecksuche/Pr%C3%A4sentationen SP - 1 EP - 15 AN - OPUS4-38096 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Millar, Steven A1 - Gottlieb, Cassian A1 - Wilsch, Gerd A1 - Eichler, Thorsten A1 - Bohling, C. A1 - Molkenthin, A. T1 - Laser induced breakdown spectroscopy (LIBS) - On-site investigatioons on a bridge with a mobile LIBS-system N2 - LIBS is on the step from a laboratory application to on-site analysis. A validated mobile LIBS-system for on-site application on building materials is under development at BAM in cooperation with industrial partners (system developers and companies), who will use this technique for investigation on building structures like bridges and parking decks. The system is designed to measure the content of harmful species like chlorine, sulfur or alkalis, to give the engineer a tool for the estimation of the condition of concrete structures and for quality assurance during concrete repair work on-site. In these work results of on-site measurements on a chloride contaminated bridge are shown. Further work will focus on providing guidelines to establish LIBS as a standard procedure for chemical investigations of building materials. T2 - NDT-CE 2015 - International symposium non-destructive testing in civil engineering CY - Berlin, Germany DA - 15.09.2015 KW - LIBS KW - Chlorides KW - Sulfur KW - Alkalis KW - Corrosion KW - ASR KW - Chemical analysis KW - Chloride KW - Elementanalyse KW - Natrium KW - Baustoffuntersuchungen KW - Baustoffe KW - Dauerhaftigkeit KW - Messsysteme KW - Mobiles LIBS PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-345795 UR - http://www.ndt.net/?id=18296 SN - 1435-4934 VL - 20 IS - 11 SP - 1 EP - 5 PB - NDT.net CY - Kirchwald AN - OPUS4-34579 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Grothe, Sven T1 - Ultrasonic signal evaluation used to detect weather-related temperature changes in a concrete specimen N2 - Ultrasonic measurement evaluation methods have been proven to be effective for detection of subtle changes, caused by temperature, load or moisture. However, for its application outdoors it is necessary to analyse unavoidable influences, such as weather. Therefore an ultrasonic monitoring system with 40 ultrasonic sensors (20 transmitters, 20 receivers; 25 kHz central frequenzy) has been implemented on a concrete specimen (4×5×0.8m3), that is exposed to weather conditions. Data from 400 sensor combinations was collected over a period of six months with an interval of two hours. The data was evaluated by both qualitative (correlation techniques) and quantitative (ultrasonic velocity changes via Coda Wave Interferometry and time of flight method) evaluation methods and compared to the temperature changes caused by weather. T2 - NDT-CE 2015 - International symposium non-destructive testing in civil engineering CY - Berlin, Germany DA - 15.09.2015 PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-346398 UR - https://www.ndt.net/?id=18336 SN - 1435-4934 VL - 20 IS - 11 SP - 1 EP - 4 PB - NDT.net CY - Kirchwald AN - OPUS4-34639 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Altenburg, Simon A1 - Chien, M. A1 - Bavendiek, F. A1 - Krankenhagen, Rainer T1 - Thermografische Schichtdickenbestimmung von Oberflächenschutzsystemen für Beton N2 - Im Bauwesen werden Polymerbeschichtungen auf Beton häufig eingesetzt um zum einen ein bestimmtes Aussehen zu schaffen und zum anderen das Bauteil vor Alterung, Verschleiß und Schädigung zu schützen. Für praktisch alle Ziele ist die Wirkung von der eigens dafür definierten Schichtdicke der Polymerbeschichtung abhängig. Daher wird die Dicke der Beschichtung nach erfolgtem Schichtauftrag überprüft. Für den in diesem Zusammenhang anspruchsvollen mineralischen Untergrund Beton stehen bislang allerdings nur zerstörende Prüfverfahren zur Verfügung. Aus diesem Grund wurden im Rahmen des Projektes IRKUTSK ein auf aktiver Thermografie basierendes Verfahren sowie ein Gerät für den vor-Ort-Einsatz entwickelt, mit dessen Hilfe eine zerstörungsfreie Schichtdickenbestimmung möglich ist. Hier wird ein kurzer Einblick in das zur Schichtdickenbestimmung entwickelte Thermografieverfahren gegeben. Die Besonderheiten bei der quantitativen Auswertung, die durch die Teiltransparenz der Polymerbeschichtungen auftreten, werden erläutert. Die Funktion des Verfahrens für einlagige Systeme wird anhand von La-bormessungen illustriert. T2 - Thermographie-Kolloquium 2017 CY - Berlin, Germany DA - 28.09.2017 KW - Schichtdickenbestimmung KW - Beton KW - Oberflächenschutzsystem KW - Thermografie PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-423577 SN - 978-3-940283-88-7 VL - 163 SP - 1 EP - 8 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-42357 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Galindo Guerreros, Julio Cesar A1 - Niederleithinger, Ernst A1 - Mackens, S. A1 - Fechner, T. T1 - Quality assurance of jet grout columns with borehole seismic measurements N2 - Sealing and strengthening of the subsoil by injection is a major issue in the field of geotechnical engineering. One commonly applied method is jet grouting, which allows creating columns of grouted soil by eroding and mixing the in-situ soil with a thin cement suspension. A general difficulty linked with this method is to predict the resulting column diameter and its material strength. In this paper we illustrate the application of a newly developed non-destructive quality assurance testing tool used to determine the diameter of jet grout columns. This approach incorporates standard crosshole and downhole seismic measurements. To demonstrate its effectiveness, we tested the new approach within two-dimensional finite-difference numerical simulations. Additional field tests showed that this tool is also applicable in real site conditions. For this purpose, three jet grout columns were produced with different process parameters in a depth between 3.0 and 10 m. The evaluated diameters were within 1.0 and 1.5 m, slightly deviating from the previously predicted range by the jet grouting contractor. Moreover, we were able to detect the base of the columns at 10 m depth with no significant difficulties. On the other hand, unsaturated, partly unconsolidated sands between ground water level and surface considerably affected the seismic data, hence complicating the detection of the top of the columns. T2 - NDT-CE 2015 - International symposium non-destructive testing in civil engineering CY - Berlin, Germany DA - 15.09.2015 KW - Jet grout KW - Seismics KW - Crosshole KW - Downhole PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-346753 UR - https://www.ndt.net/?id=18277 SN - 1435-4934 VL - 20 IS - 11 SP - 1 EP - 7 PB - NDT.net CY - Kirchwald AN - OPUS4-34675 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Osterloh, Kurt A1 - Fratzscher, Daniel A1 - Zscherpel, Uwe A1 - Ewert, Uwe A1 - Hasenstab, A. A1 - Bücherl, T. A1 - Schillinger, B. T1 - Partielle Tomographie mit Neutronen zur Beurteilung von Leimschichten in Holz N2 - Verleimte Holzproben wurden je nach Größe mit thermischen (ANTARES) bzw. schnellen Neutronen (NECTAR) an der Forschungs-Neutronenquelle Heinz Maier-Leibnitz (FRM II) der Technischen Universität München in Garching untersucht. Entweder ließen die durchstrahlbare Schichtdicke oder die eingeschränkte Strahlgeometrie es nicht zu, das Probenteil allseitig zu durchstrahlen. Um dennoch innere Strukturen wie Leimschichten zumindest mit einem eingeschränkten Winkelbereich tomographisch darzustellen, wurde mit Hilfe des Slice-Theorems erfolgreich rekonstruiert. Ein Brett von 2 cm Dicke wurde mit thermischen Neutronen erfolgreich untersucht, ein größeres mit schnellen. T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Germany DA - 30.05.2011 KW - Neutronentomographie KW - Eingeschränkter Winkelbereich KW - Holz PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-250649 SN - 978-3-940283-33-7 VL - 127 SP - 1 EP - 6 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-25064 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Osterloh, Kurt A1 - Ewert, Uwe A1 - Zvizdic, D. A1 - Krstelj, V. T1 - Die EFNDT Arbeitsgruppe 5 'Öffentliche Sicherheit mit ZfP-Techniken' neu formiert N2 - Für die öffentliche Sicherheit wird gesorgt, indem Gefahren rechtzeitig entdeckt werden. Deren Ursprung kann im technischen oder menschlichen Versagen liegen, womit im englischen Sprachraum zwischen 'Safety' und 'Security' unterschieden wird. Hinsichtlich der Folgen verschwimmt aber dieser Unterschied, obwohl für deren Verhinderung unterschiedliche Zuständigkeiten existieren. Bezüglich des gemeinsamen Interesses und auch überlappender Methoden und Vorgehensweisen würden beide Seiten gewinnen können, wenn es eine Brücke zwischen ihnen gäbe. Eine solche zu schaffen hat sich die EFNDT Arbeitsgruppe (Working Group) 5 zur Aufgabe gestellt. Gestaltet werden soll sie durch gemeinsame Veranstaltungen und Seminaren, die zur Bildung von Konsortien und der Durchführung gemeinsamer Projekte führen sollen. T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Germany DA - 03.05.2011 KW - EFNDT Working Group 5 KW - Technische und öffentliche Sicherheit KW - Gemeinsamkeiten in ZfP und öffentlicher Sicherheit KW - Brückenbildung zwischen Zuständigkeitsbereichen PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-250631 SN - 978-3-940283-33-7 VL - 127 SP - 1 EP - 5 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-25063 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holtappels, Kai A1 - Brinkmann, C. A1 - Schönbucher, A. T1 - Experimentelle Bestimmung und Simulation der Stabilitätsgrenzdrücke von Gasgemischen mit zerfallsfähigen Komponenten T2 - DECHEMA/GVC-Arbeitsausschuss "Sicherheitstechnische Kenngrößen" CY - Frankfurt am Main, Deutschland DA - 2000-10-05 PY - 2000 SP - 1 EP - 21 AN - OPUS4-1721 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nattuveettil, Keerthana A1 - Brunner, Nanine A1 - Tiebe, Carlo A1 - Thomas, Marcus A1 - Melzer, Michael A1 - Bartholmai, Matthias A1 - Johann, Sergej A1 - Neumann, Patrick P. T1 - Digital approach of certification in Quality Infrastructure N2 - QI-Digital is a joined project aiming at digitalising Quality Infrastructure (QI) processes involving standardization, conformity assessment, accreditation, metrology, and market surveillance [1]. Federal institute of material research and testing (BAM) is working on the creation of a digital calibration certifi-cate (DCC) to achieve digital metrological traceability and conformity assessment. The utilisation of machine readable and executable DCCs in the XML format is demonstrated on an example of a tem-perature measurement at a hydrogen refueling station. The certificates will be retrieved and analysed automatically at a Process Control System or at a Digital Twin. T2 - SMSI 2023 Conference CY - Nürnberg, Germany DA - 08.05.2023 KW - Quality Infrastructure KW - Digital Certificates KW - Temperature calibration KW - Digitalisation KW - Hydrogen technology PY - 2023 DO - https://doi.org/10.5162/SMSI2023/A3.4 SP - 51 EP - 52 PB - AMA Service GmbH CY - Wunstorf AN - OPUS4-57964 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Melzer, Michael A1 - Thomas, Marcus A1 - Tiebe, Carlo T1 - Digitaler Kalibrierschein 8.1I1451B mit digitaler Signatur und digitalem Akkreditierungssymbol (eAttestation) N2 - Es handelt sich hierbei um die erste Veröffentlichung einer verifizierbaren eAttestation (DCC mit DAkkS-Siegel). Sie wurde vom akkreditierten Kalibrierlabor D-K-11075-08, im Rahmen des QI-Digital Vorhabens, für den Fachbereich 8.1 erstellt und dient im Zusammenhang mit dem Vortrag "Digitale Kalibrierzertifikate – die Umsetzung in akkreditierten Laboratorien" auf dem 324. PTB-Seminar "Berechnung der Messunsicherheit – Empfehlungen für die Praxis" als Anschauungsmaterial für die Digitalisierung in der Metrologie. T2 - 324. PTB-Seminar: Berechnung der Messunsicherheit – Empfehlungen für die Praxis CY - Berlin, Germany DA - 22.05.2023 KW - Akkreditierung KW - DCC KW - Digitalisierung KW - QI-Digital KW - eAttestation PY - 2023 UR - https://www.ptb.de/cms/fileadmin/internet/fachabteilungen/abteilung_8/8.4_mathematische_modellierung/324_PTB_Seminar/Vortraege/8.1I1451B_DAkkS_TEMP_Fluke2638A_SignDFN_eAttest.pdf SP - 1 EP - 3 CY - Berlin, Deutschland AN - OPUS4-58010 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mair, Georg W. A1 - Bock, Robert A1 - Günzel, Stephan A1 - Gesell, Stephan T1 - Monte-Carlo-Analysis of Minimum Burst Requirements for Composite Cylinders for Hydrogen Service N2 - For achieving Net Zero-aims hydrogen is an indispensable component, probably the main component. For the usage of hydrogen, a wide acceptance is necessary, which requires trust in hydrogen based on absence of major incidents resulting from a high safety level. Burst tests stand for a type of testing that is used in every test standard and regulation as one of the key issues for ensuring safety in use. The central role of burst and proof test is grown to historical reasons for steam engines and steel vessels but - with respect for composite pressure vessels (CPVs) - not due an extraordinary depth of outcomes. Its importance results from the relatively simple test process with relatively low costs and gets its importance by running of the different test variations in parallel. In relevant test und production standards (as e. g. ECE R134) the burst test is used in at least 4 different meanings. There is the burst test on a) new CPVs and some others b) for determining the residual strength subsequent to various simulations of ageing effects. Both are performed during the approval process on a pre-series. Then there is c) the batch testing during the CPVs production and finally d) the 100% proof testing, which means to stop the burst test at a certain pressure level. These different aspects of burst tests are analysed and compared with respect to its importance for the resulting safety of the populations of CPVs in service based on experienced test results and Monte-Carlo simulations. As main criterial for this the expected failure rate in a probabilistic meaning is used. This finally ends up with recommendations for relevant RC&S especially with respect to GTR 13. T2 - 9th International Conference on Hydrogen Safety CY - Online meeting DA - 21.09.2021 KW - Hydrogen KW - Burst test KW - Composite pressure vessels KW - Net zero KW - Monte-Carlo-Analysis PY - 2021 SP - 133 EP - 146 PB - IGEM AN - OPUS4-55668 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gawlitza, Kornelia A1 - Johann, Sergej A1 - Mansurova, Maria A1 - Kohlhoff, Harald A1 - Tiebe, Carlo A1 - Bell, Jérémy A1 - Bartholmai, Matthias A1 - Rurack, Knut T1 - Semi-automatic Measurement Device for Long-Term Monitoring of Ammonia in Gas Phase N2 - In the present paper the development of a semi-automated device for long-term monitoring of gaseous ammonia is described. A sensor material was produced that changes its optical properties in the pres-ence of low concentrations of ammonia in air. The implementation into an electronic device enables precise, simple, economic and fast monitoring of low concentrations of harmful gases, like ammonia, and hence can help to improve the climate monitoring in livestock housing, barns or stables. T2 - SMSI 2021 CY - Online meeting DA - 03.05.2021 KW - Spectroscopy KW - Embedded sensor KW - Environment KW - Air quality PY - 2021 SP - 133 EP - 134 AN - OPUS4-52576 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holtappels, Kai A1 - Brinkmann, C. A1 - Stickling, J. A1 - Dietlen, Siegmund A1 - Schönbucher, A. T1 - Determination and prediction of decomposition limits for acetylene/inert gas and acetylene/fuel gas-mixtures T2 - International Meeting on Chemical Engineering, Environmental Protection and Biotechnology 2000 ; ACHEMA 2000 CY - Frankfurt am Main, Germany DA - 2000-05-22 PY - 2000 PB - DECHEMA CY - Frankfurt, Main AN - OPUS4-1716 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ferrero, Fabio A1 - Kluge, Martin A1 - Kreißig, Michael A1 - Schmidtchen, Ulrich A1 - Holtappels, Kai T1 - Prevention of the explosion of acetylene cylinders involved in fire: experiments and simulations N2 - In order to assess the effectiveness of water cooling of acetylene cylinders involved in fire, a total of 13 bonfire tests with 8.9-, 10 and 50-l-cylinders were performed. During the experiments the pressure in the cylinder and the temperature at different locations within the porous material and on the Shell surface as well as the flame temperature were measured. Overall 8 burst tests were performed, in order to determine the times to explosion for the cylinders. Cylinders failed not later than 15 minutes from the ignition of the bonfire, often with generation of a fireball. During the other 5 tests, the fire was extinguished before the expected burst and the cylinder was cooled with water. In 2 of the 5 extinction experiments, the explosion of the cylinder could be prevented. Noticeably, in one case the on-set of the decomposition of acetylene had already been observed, before the cooling was started. In spite of that, the cooling was still effective. The interpretation of the current results and of the data from previous tests with 40-l-cylinder suggests that single acetylene cylinders involved in fire might be saved by cooling, if their pressure does not exceed a value of about 45 bara. The recorded values of pressure and temperature were used to develop and validate a mathematical model for the prediction of the heat transfer in acetylene cylinders during the exposure to fire and the afterward cooling. The predictions agreed well with the experimental results. T2 - 23rd ICDERS 2011 CY - Irvine, CA, USA DA - 24.07.2011 KW - Acetylene KW - Gas cylinders KW - Fire exposure KW - Decomposition PY - 2011 N1 - Geburtsname von Kluge, Martin: Beckmann-Kluge, M. - Birth name of Kluge, Martin: Beckmann-Kluge, M. IS - Paper 132 SP - 1 EP - 6 AN - OPUS4-24153 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Johann, Sergej A1 - Tiebe, Carlo A1 - Kohlhoff, Harald A1 - Bartholmai, Matthias T1 - Feasibility Study for Safe Workplaces through automation and digitalization technology with redesigned Smart Sensors and LoRaWAN Monitoring System N2 - This project addresses the application of safe and healthy workplaces in offices, chemical laboratories and other workplaces where indoor air quality plays an important role. The LoRaWAN (Long Range Wide Area Network) is used as a communication interface to make sensor data globally accessible. The objectives of the project are to create a sensor node and an online and offline system that collects the data from the sensor nodes and stores it on a local server, in a cloud, and also locally on the node to prevent communication failures. An important point in this project is the development of the sensor nodes and the placement of these in the premises, thus no development work is involved in Building the infrastructure. T2 - SMSI 2021 CY - Online meeting DA - 03.05.2021 KW - Smart sensors KW - Air quality monitoring KW - LoRaWAN KW - VOC KW - Multisensor system PY - 2021 SP - 230 EP - 231 AN - OPUS4-52649 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Moufid, M. A1 - Tiebe, Carlo A1 - El Bari, N. A1 - Bartholmai, Matthias A1 - Bouchikhi, B. T1 - Characterization of Unpleasant Odors in Poultry Houses Using Metal Oxide Semiconductor-Based Gas Sensor Arrays and Pattern Recognition Methods N2 - In this study, the ability of an electronic nose developed to analyze and monitor odor emissions from three poultry farms located in Meknes (Morocco) and Berlin (Germany) was evaluated. Indeed, the potentiality of the electronic nose (e-nose) to differentiate the concentration fractions of hydrogen sulfide, ammonia, and ethanol was investigated. Furthermore, the impact change of relative humidity values (from 15% to 67%) on the responses of the gas sensors was reported and revealed that the effect remained less than 0.6%. Furthermore, the relevant results confirmed that the developed e-nose system was able to perfectly classify and monitor the odorous air of poultry farms. T2 - 1st International Electronic Conference on Chemical Sensors and Analytical Chemistry CY - Online meeting DA - 01.07.2021 KW - Pattern recognition methods KW - Gas sensors KW - Electronic nose KW - poultry odorous air monitoring PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-544005 UR - https://csac2021.sciforum.net/ DO - https://doi.org/10.3390/CSAC2021-10481 VL - 5 IS - 52 SP - 1 EP - 7 PB - MDPI AN - OPUS4-54400 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Holtappels, Kai A1 - Liebner, Christian A1 - Schröder, Volkmar A1 - Pasman, H. A1 - Pekalski, A. A1 - Carson, D. A1 - Proust, C. T1 - Report on the experimental factors influencing explosion indices determination KW - SAFEKINEX KW - Explosionskenngrößen KW - Experimentelle Einflüsse KW - Nicht-atmosphärische Bedingungen PY - 2004 UR - http://www.morechemistry.com/SAFEKINEX/deliverables/02.Del.%20No.%202%20Exp.%20Factors%20Expl.%20Indices%20Det.pdf SP - 1 EP - 52 AN - OPUS4-5976 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schumacher, David A1 - Zscherpel, Uwe A1 - Ewert, Uwe T1 - Photon counting and energy discriminating x-ray detectors - benefits and applications N2 - Since a few years the direct detection of X-ray photons into electrical signals is possible by usage of highly absorbing photo conducting materials (e.g. CdTe) as detection layer of an underlying CMOS semiconductor X-ray detector. Even NDT energies up to 400 keV are possible today, as well. The image sharpness and absorption efficiency is improved by the replacement of the unsharp scintillation layer (as used at indirect detecting detectors) by a photo conducting layer of much higher thickness. If the read-out speed is high enough (ca. 50 – 100 ns dead time) single X-ray photons can be counted and their energy measured. Read-out noise and dark image correction can be avoided. By setting energy thresholds selected energy ranges of the X-ray spectrum can be detected or suppressed. This allows material discrimination by dual-energy techniques or the reduction of image contributions of scattered radiation, which results in an enhanced contrast sensitivity. To use these advantages in an effective way, a special calibration procedure has to be developed, which considers also time dependent processes in the detection layer. This contribution presents some of these new properties of direct detecting digital detector arrays (DDAs) and shows first results on testing fiber reinforced composites as well as first approaches to dual energy imaging. T2 - 19th World Conference on Non-Destructive Testing, 2016 CY - Munich, Germany DA - 13.06.2016 KW - CFRP KW - Photon counting detectors KW - dual-energy KW - laminography PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-365744 SN - 978-3-940283-78-8 N1 - Geburtsname von Schumacher, David: Walter, D. - Birth name of Schumacher, David: Walter, D. VL - 2016 / 158 SP - Tu.2.B.5 AN - OPUS4-36574 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hosseini, Seyed M.H. A1 - Ségur, D. A1 - Boehm, Rainer A1 - Gohlke, Dirk A1 - Heckel, Thomas A1 - Riemer, S. A1 - Brackrock, Daniel A1 - Gaal, Mate T1 - Characterization and optimization of ultrasonic tests for inspection of fiber-reinforced plastic composites in energy related applications N2 - Applications of fibre reinforced plastic (FRP) composites in modern industries are increasing due to their considerable advantages such as light weight and excellent mechanical properties. Accordingly, importance of operational safety of modern structures made of advanced composites by ensuring the material quality has led to increasing demands for development of non-destructive evaluation (NDE) systems. In the context of a European project entitled “Validated Inspection Techniques for Composites in Energy Applications” (VITCEA), the aim is to develop and validate traceable procedures for novel NDE techniques with contrasting damage detection capabilities in energy related applications such as wind and marine turbine blades, nacelles, oil and gas flexible risers. Accordingly, VITCEA focuses on optimization of ultrasonic tests (UTs) for quantitative defect detection and quality characterization of FRP structures. In this context, the present study describes the ultrasound field in heterogeneous composite materials. The theoretical predictions are compared with simulation results obtained from CIVA a software package dedicated to NDT simulations based on the asymptotic ray theory. T2 - WCNDT 2016 - - 19th World Conference on Non-Destructive Testing CY - München DA - 13.06.2016 KW - Ultrasonic tests KW - Composite KW - Wave propagation KW - Analytical approach PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-356398 SP - We.4.D.5, 1 EP - 8 AN - OPUS4-35639 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rothbart, Nick A1 - Maierhofer, Christiane A1 - Goldammer, M. A1 - Hohlstein, F. A1 - Koch, J. A1 - Kryukov, I. A1 - Mahler, G. A1 - Stotter, B. A1 - Walle, G. A1 - Oswald-Tranta, B. A1 - Sengebusch, M. T1 - A round robin test on flash thermography N2 - A round robin test on flash thermography was organized within the scope of a standardization research project. This test gives information on reliability, comparability and efficiency of different testing situations. Data recorded on metal and CFRP test specimens with flat bottom holes (FBH) were analysed by evaluating the detectability and by calculating the signal-to-noise ratio (SNR) of the defect signatures as a function of defect parameters. For the investigation of the influence of material properties on the spatial resolution as well as on penetration depth, test specimens made of steel and copper with crossed notches and a notch ramp were constructed and investigated. Here, the minimum resolvable notch distance and the maximum detectable depth of the ramp were analysed. T2 - 19th World Conference on Non-destructive Testing (WCNDT) CY - Munich, Germany DA - 13.06.2016 KW - Active thermography KW - Flash excitation KW - Round robin test KW - Standardisation PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-366853 SN - 978-3-940283-78-8 VL - BB 158 SP - We.3.D.4., 1 EP - 8 PB - DGZfP CY - Berlin AN - OPUS4-36685 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krankenhagen, Rainer A1 - Röllig, Mathias A1 - Worzewski, Tamara A1 - Doroshtnasir, Manoucher T1 - Thermographic rotor blade inspection from larger distances – a promising tool for the maintenance of wind turbines N2 - The permanently increasing number of wind turbines requires suited inspection and monitoring methods to ensure liability and security. Concerning the inspection of ro-tor blades, only manual inspections are state of the art. Thermographic Testing (TT) has the potential to detect typical failures and damages on rotor blades. The paper presents some results of onsite measurements carried out as “passive thermogra-phy”, i.e. without a defined heating procedure. Due the totally contactless meas-urement principle, TT can be applied to rotating blades as well as to resting blades. Both methods will be compared with respect to their possible realization. T2 - WCNDT 2016 CY - Munich, Germany DA - 13.06.2016 KW - Wind turbine rotor blade KW - Thermographic inspection KW - Passive thermography KW - Nondestructive testing PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-366331 SN - 978-3-940283-78-8 SP - We.4.D.4., 1 EP - 8 AN - OPUS4-36633 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thiel, Erik A1 - Kreutzbruck, M. A1 - Ziegler, Mathias T1 - Laser projected photothermal thermography for characterizing hidden defects N2 - For the last 20 years active thermography has developed into a standard method in non-destructive material testing. It has become possible to detect defects such as cracks, voids, or even material inhomogeneities. Until now, it is still difficult to quantify subsurface or hidden defects in size due to the diffusive nature of heat flow within a solid. Facing this issue, lockin thermography and other photothermal techniques have been established. They are based on exciting a sample periodically (e.g. with a halogen lamp), causing a controlled periodical heat flow and thereby representing strongly damped thermal waves. These techniques make use of interference and reflection of thermal waves which allow enhancing depth resolution. So far, only the temporal component of the light source was modified to achieve a defined vertical heat flow – In contrast, we propose a novel technique in which we are able to control both: time and space. This technique enables us to exploit the possibilities of coherent thermal wave shaping. We achieve that by combining a spatial light modulator (SLM) with a high power laser. This approach allows us to launch a set of individually controlled and fully coherent high energy thermal waves into the sample volume. That means, we intentionally use wave propagation throughout the sample’s material in both - vertical and lateral direction. As one possible application, we use a thermal waves’ interference effect of two phase shifted wave patterns to detect the position of hidden defects. The wave patterns are positioned with a certain distance and a 180° phase shift to each other creating an amplitude depletion zone right in the middle of the two patterns. When a defect is brought unsymmetrically into the depletion zone, the lateral heat flow is disturbed. If the sample is now moved through the depletion zone, a defect can be easily characterized. Exciting periodically while controlling simultaneously phase and amplitude enables us to have a defined thermal wave propagation throughout the sample which means thermal waves can be controlled almost like acoustical or optical waves. This offers the opportunity to transfer known technologies from wave shaping techniques to thermography methods. T2 - 19th World Conference of Non-Destructive Testing 2016 CY - München, Germany DA - 13.06.2016 KW - Thermal waves KW - DMD KW - Active thermography KW - SLM PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-365702 SP - Th.4.I.2 - 1 EP - Th.4.I.2 - 6 AN - OPUS4-36570 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schukar, Vivien A1 - Köppe, Enrico A1 - Hofmann, Detlef A1 - Westphal, Anja A1 - Sahre, Mario A1 - Gong, Xin A1 - Bartholmai, Matthias A1 - Beck, Uwe T1 - Magnetic field detection with an advanced FBG-based sensor device N2 - A high-performance fiber Bragg grating-based (FBG) sensor device has been developed for the detection of small magnetic fields. Based on a smart multilayer jacket around the fibre over the physical length of the FBG, magnetic fields generated by rotating machine parts, power generators or power cable can be easily detected, analysed and evaluated. Consequently, this innovative, on-line and non-contact inspection method results in an increase in quality and reliability of high-performing machine parts, devices and cables. The basic physical principle is based on a magnetostrictive multilayer system that strains the high-resolution FBG element in presence of magnetic fields. Subsequently, a fixed relationship between induced magnetic field and wavelength change of the FBG element describes the characteristic sensitivity curve. Intensive tests regarding characterisation of this magnetic field FBG sensor have been carried out and its performance has been evaluated. T2 - 30th Eurosensors Conference, EUROSENSORS 2016 CY - Budapest, Hungary DA - 04.09.2016 KW - Fiber Bragg grating KW - Magnetostriction KW - Strain KW - Magnetic field PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-376703 DO - https://doi.org/10.1016/j.proeng.2016.11.445 SN - 1877-7058 VL - 168 SP - 1270 EP - 1274 PB - Elsevier Ltd. AN - OPUS4-37670 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kotschate, Daniel A1 - Gohlke, Dirk A1 - Heckel, Thomas T1 - Three dimensional examination of directivity pattern in immersion tank testing N2 - High resolution examination of safety-relevant parts in immersion tank testing with focussing probes is forming a main topic of modern non-destructive testing. For the usage of complex reconstruction methods and algorithms, an individual and detailed knowledge about the transmission behaviour of the used probes is essential, as this has a significant influence on the results of data reconstruction. Especially the knowledge about position and diameter of the focal point is needed to achieve the highest possible sensitivity. Through the individual position of the beam axis within the examined volume, a four dimensional metro logical determination of the acoustical pressure (x, y, z, t) is necessary. With the measured data it is possible to draw interferences about the sound field and acoustical pressure distribution. The presented work realized a method of automatic determination of the beam axis, the position of focal point and the focal diameter to support individual testing setups and transducer characterization. T2 - 7th International Symposium on NDT in Aerospace CY - Bremen, Germany DA - 16.11.2015 PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-339995 AN - OPUS4-33999 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Ballach, F. A1 - Bartscher, M. A1 - Bellon, Carsten A1 - Borges de Oliveira, F. A1 - Braun, M. A1 - Dennerlein, F. A1 - Flessner, M. A1 - Fuchs, P. A1 - Günnewig, O. A1 - Hausotte, T. A1 - Hess, J. A1 - Kasperl, S. A1 - Kirschbaum, K. A1 - Li, K. A1 - Maass, N. A1 - Mayer, T. A1 - Orth, Anthony A1 - Reuter, T. A1 - Suppes, A. A1 - von Schmid, M. A1 - Weiß, D. T1 - Realistische Simulation realer Röntgencomputertomografie-Systeme mit basisqualifizierter Simulationssoftware – CTSimU2 BT - Abschlussbericht N2 - Das Förderprojekt CTSimU2 baute auf den Ergebnissen des Projektes CTSimU auf. Dieses Vorprojekt erarbeitete ein (Basis-)Qualifizierungsframework für Simulationssoftwares zur Anwendung bei der Röntgen-CT für dimensionelle Messungen. Dabei stand die ausreichende physikalische Korrektheit der Durchstrahlungssimulation im Vordergrund. Für die realitätsnahe Simulation einer CT-Anlage in einer Simulationssoftware (Digitales Modell) ist jedoch nicht nur die Korrektheit der Simulationssoftware selbst, sondern auch die Güte der Parametrisierung des realen CT-Systems in der Simulationssoftware entscheidend – dies stellte den Ausgangspunkt dar. Die Parametrisierung eines CT-Systems in einer Simulationssoftware lässt sich in vier Schritte unterteilen: nach der Datenaufnahme am realen CT-System folgt die Auswertung der aufgenommenen Daten für die Generierung allgemeiner Parameterangaben. Als letztes folgte die Übertragung der Parameter in die spezifischen Simulationssoftwares und die Validierung der resultierenden Simulationsparameter. Die Methodik der Datenaufnahme am CT und die Auswertung der Daten wurde in einem Werkzeugkasten allgemein beschrieben. Der dritte Schritt, die Umsetzung der Parameter, war softwarespezifisch und wurde beispielhaft mit den vorhandenen Simulationssoftwares durchgeführt. Die Validierung der Parameter war standardisierbar und konnte durch den entwickelten Test geleistet werden, auf dessen Basis die ausreichend korrekte Simulation einer realen Anlage beurteilt werden konnte. Endresultat des Projektes war ein Richtlinienentwurf (z. B. VDI/VDE 2630) zu diesem Test, der einen informativen Annex zum Stand der Technik bezüglich der Möglichkeiten zur Parameterbestimmung enthält. Mit einer Simulationssoftware, die die Basisqualifizierung aus CTSimU bestanden hat und einen Parameterdatensatz für ein reales CT-System enthält, der den Test aus CTSimU2 bestanden hat, können realistische Simulationen dieses CT-Systems möglich sein. KW - Computertomografie KW - Simulation KW - Dimensionelles Messen PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-641719 DO - https://doi.org/10.34657/21602 N1 - Dieses Projekt wurde durch die Förderrichtlinie WIPANO gefördert und durch das Bundesministerium für Wirtschaft und Klimaschutz (2022 -2025) finanziert. Der Projektträger Jülich verwaltet die Projekte der Förderrichtlinie WIPANO. SP - 1 EP - 22 PB - TIB Technische Informationsbibliothek CY - Hannover AN - OPUS4-64171 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ziegler, Mathias A1 - Thiel, Erik A1 - Studemund, Taarna T1 - Laser-Thermografie – Von der flächigen zur strukturierten Anregung N2 - Im Bereich der optisch angeregten Thermografie haben sich Blitzlampen (impulsförmig-flächige Erwärmung) und Halogenlampen (moduliert-flächige Erwärmung) für die spezifischen Regime Impuls- und Lockin-Thermografie etabliert. Mittels eines rasternden fokussierten Lasers wird die Flying-spot Laserthermografie z.B. zur Risserkennung (Dauerstrichbetrieb) und die photothermische Materialcharakterisierung (hochfrequent moduliert)implementiert. Durch die Verfügbarkeit neuer Technologien (schnelle und hochauflösende IR-Kameras, brillante innovativer Lichtquellen und performante Datenakquisitions- und Verarbeitungstechnik) wird ein Paradigmenwechsel von den getrennt voneinander stehenden photothermischen und thermografischen Techniken hin zu einer einheitlichen quantitativen Mess-und Prüftechnik ermöglicht, die schneller und präziser ist. Ähnlich wie ein LED-Array, jedoch mit einer um zwei Größenordnungen höheren Bestrahlungsstärke, steht jetzt eine neuartige brillante Laserquelle, das VCSEL-Array (vertical-cavity surface-emitting laser) zur Verfügung, welches die starke Beschränkung der zeitlichen Dynamik der etablierten Lichtquellen aufhebt und gleichzeitig spektral sauber von der Detektionswellenlänge getrennt ist. Es vereint somit das schnelle zeitliche Verhalten eines Diodenlasers mit der hohen optischen Bestrahlungsstärke und dem großen Beleuchtungsbereich von Blitzlampen. Darüber hinaus kann die Erwärmung auch strukturiert vorgenommen werden, da einzelne Bereiche des VCSEL-Arrays unabhängig voneinander angesteuert werden können. Dieser neue Freiheitsgrad ermöglicht die Entwicklung ganz neuer thermografischer ZfP-Verfahren. T2 - Thermographie-Kolloquium 2017 CY - Berlin, Germany DA - 28.09.2017 KW - Thermografie KW - Laser KW - Zerstörungsfreie Prüfung KW - Lock-in KW - VCSEL KW - Photothermisch PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-431170 UR - https://www.dgzfp.de/Portals/thermo2017/BB/6.pdf SN - 978-3-940283-88-7 VL - 163 SP - 1 EP - 15 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-43117 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schadow, Florian A1 - Brackrock, Daniel A1 - Gaal, Mate A1 - Heckel, Thomas T1 - Ultrasonic inspection and data analysis of glass- and carbon-fibre-reinforced plastics N2 - Non-destructive testing (NDT) helps to find material defects without having an influence on the material itself. It is applied as a method of quality control, for online structural health monitoring, and for inspection of safety related components. Due to the ability of automation and a simple test setup ultrasonic testing is one major NDT technique next to several existing options. Whereas contact technique allows the use of higher frequencies of some MHz and phased array focusing, air-coupled ultrasonic testing (ACUT) shows different advantages. Most significant for ACUT is the absence of any coupling fluid and an economical test procedure respective time and costs. Both contact technique and ACUT have been improved and enhanced during the past years. One important enhancement is the development of airborne transducers based on ferroelectrets, like charged cellular polypropylene (cpp), which makes the application of any matching layers being mandatory in conventional piezoelectric transducers unnecessary. In this contribution we show ultrasonic inspection results of specimens made of carbon- and glass-fibre-reinforced plastic. These specimens include defects represented by drill holes and artificial delaminations of various size and depth. We compare inspection results achieved by using contact technique to those achieved by ACUT. For ACUT, conventional piezoelectric transducers and transducers based on cpp were used, both focused as well as non-focused types. Contact inspections were performed with a multi-channel matrix array probe. Once the inspection data is recorded it can be analysed in order to detect and evaluate defects in the specimen. We present different analysing strategies and compare these regarding detection rate and sizing of defects. T2 - 3rd International Symposium on Fatigue Design and Material Defects, FDMD 2017 CY - Lecco, Italy DA - 19.09.2017 KW - Ultrasonic testing KW - Air-coupled KW - Carbon-fibre-reinforced plastic KW - Glass-fibre-reinforced KW - Material inspection KW - Defect sizing PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-434802 DO - https://doi.org/10.1016/j.prostr.2017.11.092 SN - 2452-3216 VL - 7 SP - 299 EP - 306 PB - Elsevier B.V. AN - OPUS4-43480 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schumacher, David A1 - Ewert, Uwe A1 - Zscherpel, Uwe T1 - Influencing parameters on image quality using photon counting detectors for laminography N2 - Classical film radiography is a well-established NDT technique and it is most commonly used for testing weld seams and corroded pipes e.g. in oil and gas industry or in nuclear power plants. In the course of digitization, digital detector arrays (DDA) are finding their way into industrial applications and are replacing film radiography step by step. This study deals with the latest generation of DDAs, the photon counting and energy resolving detectors (PCD), and their characteristics compared to charge integrating detectors (CID). No matter which technology to use, radiography still lacks a general issue: A three-dimensional object is projected onto a two dimensional image. Of course, advanced computed tomography (CT) algorithms exist since many years, but if the object to investigate is too large to fit into the manipulation system or its shape is not appropriate, CT is not feasible or sensible to be applied. To overcome this limitation, numerous laminographic algorithms have been developed in the past. In this study, photon counting detectors are used in combination with co-planar translational laminography to gain reconstructed three-dimensional volumes. Both laminographic testing and PCDs require a serious knowledge of many parameters that can influence the image quality in the resulting datasets. These are e.g. the detector efficiency and calibration procedure, setting of energy thresholds, exposure data, number of projections, beam length correction and spatial resolution. The use of PCDs yields more variables to be considered compared to CIDs. The most important parameters in laminographic testing and in the use of PCDs are described in this study and limits are discussed. T2 - 7th European-American Workshop on Reliability of NDE CY - Potsdam, Germany DA - 05.09.2017 KW - X-ray imaging KW - Digital radiography KW - Co-planar translational laminography KW - Reliability KW - Photon counting detectors PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-428912 UR - http://www.nde-reliability.de/portals/nde17/BB/31.pdf SP - Paper 31, 1 EP - 11 AN - OPUS4-42891 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Guhl, Svetlana A1 - Meyer, Klas A1 - Kern, Simon A1 - Gräßer, Patrick A1 - Maiwald, Michael ED - Maiwald, Michael T1 - Process monitoring of an intensified continuous production unit with compact NMR spectroscopy N2 - Monitoring chemical reactions is the key to chemical process control. Today, mainly optical online methods are applied. NMR spectroscopy has a high potential for direct loop process control. Compact NMR instruments based on permanent magnets are robust and relatively inexpensive analyzers, which feature advantages like low cost, low maintenance, ease of use, and cryogen-free operation. Instruments for online NMR measurements equipped with a flow-through cell, possessing a good signal-to-noise-ratio, sufficient robustness, and meeting the requirements for integration into industrial plants (i.e., explosion safety and fully automated data analysis) are cur-rently not available off the rack. Recently, promising benchtop NMR instruments with acceptable performance came to market and process integrated sensors developed on basis of such laboratory instruments are on their way. T2 - 12. Kolloquium des Arbeitskreises Prozessanalytik CY - Berlin, Germany DA - 28.11.2016 KW - Online NMR spectroscopy KW - Modular production units KW - Low field NMR spectroscopy PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-383646 SP - P17, 75 EP - 77 AN - OPUS4-38364 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Simon, Franz-Georg A1 - Pienkoß, Fabian T1 - INTEGRAL - Integriertes Konzept für mineralische Abfälle und Landmanagement zur nachhaltigen Entwicklung von Stadt-Land-Nutzungsbeziehungen, Teilvorhaben 4: BAM, Ermittlung stofflicher Parameter N2 - Zusammenfassend wurde in dieser Arbeit gezeigt, dass die Setzmaschinentechnik eine geeignete Methode ist, um Brechsande aus gemischten Bauabfällen aufzubereiten. Die Trennung des Materials in zwei Stoffströme unterschiedlicher Dichte hat sich mit einer Absenkung um 56% besonders effizient in der Reduzierung von PAK Belastungen im Feststoff erwiesen. Auch die Sulfatlast im Produktstrom wurde durch den Prozess im Vergleich zum Aufgabegut um 29% gesenkt. Neben der Erhöhung des Median Partikeldurchmessers durch Klassierungseffekte, ist die Herabsetzung verschiedener Eluatparameter ebenfalls positiv zu bewerten. Dies bezieht sich zum einen auf die elektrische Leitfähigkeit, die nach EBV von RC-3 auf RC-1 aufgewertet wurde und zum anderen auf die Chromkonzentration, die von RC-2 auf die Stufe RC-1 angehoben wurde. Die vorliegenden Aufbereitungsergebnisse erlaubten jedoch nicht eine Gesamteinordnung des Materials als Ersatzbaustoff oberhalb der Klasse RC-3. Hierzu ist eine weitere Absenkung der Eluatwerte für Sulfat um 25% von RC-3 (1325 mg L-1) auf RC-2 (< 1000 mg L-1) und des PAK-15 Wertes um 4% von RC-3 (8.3 µg L-1) auf RC-2 (< 8.0 µg L-1) erforderlich. Eine detaillierte Optimierung der Prozessparameter der Setzmaschinentechnik könnten diesen Spielraum ermöglichen. KW - Setzmaschine KW - Nassaufbereitung KW - Ersatzbaustoff PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-600263 DO - https://doi.org/10.2314/KXP:1887868135 N1 - Das diesem Bericht zugrunde liegende Vorhaben wurde mit Mitteln des Bundesministeriums für Bildung und Forschung unter dem Förderkennzeichen 033L223D gefördert SP - 1 EP - 18 PB - Technische Informationsbibliothek (TIB) CY - Hannover AN - OPUS4-60026 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Trappe, Volker A1 - Hickmann, Stefan A1 - Kupsch, Andreas A1 - Müller, Bernd R. A1 - Laquai, René A1 - De Monte, M. T1 - Risse an gekerbten kurzglasfaserverstärkten Thermoplasten zerstörungsfrei charakterisiert mit Röntgenverfahren N2 - Proben mit einer Mittelkerbe aus Polyamid 66 mit 35% Gewichtsan-teil an Kurzglasfaser (PA-GF35) wurden im Spritzgießverfahren hergestellt und in einem ungeschädigten und durch Schwingbeanspruch geschädigten Zustand mittels Röntgenverfahren charakterisiert. Sowohl die Faserorientierungsverteilung als auch die Riss-/Mikrorissbildung wurden mit der Röntgenrefraktionstopographie in einem SAXS-Aufbau und dem Diffraction-Enhanced-Imaging am Synchrotron (BESSY II) analysiert. Beide Verfahren spiegeln in guter Übereinstimmung die Charakteristiken dieser Werkstoffklasse in Bezug auf die Fertigungsqualität und die Schädigungsme-chanismen wider. T2 - DGZfP-Jahrestagung 2017 CY - Koblenz, Germany DA - 22.05.2017 KW - Kurzfaserverstärktes Polyamid KW - Röntgenverfahren KW - Rissfortschritt PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-435659 UR - https://www.dgzfp.de/Dienste/Publikationen?kategorie=Berichtsb%C3%A4nde SN - 978-3-940283-85-6 VL - 2017 SP - 1 EP - 11 PB - DGZfP CY - Berlin AN - OPUS4-43565 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nicolicea, Alberto A1 - Pelkner, Matthias A1 - Melzer, Michael A1 - Oliveros-Mata, E. S. A1 - Zabila, Y. A1 - Makarov, D. T1 - Flexible AMR sensors for novel non-destructive testing capabilities N2 - Reshapeable magnetic field sensors fabricated on flexible substrates by thin-film deposi-tion or printing have recently emerged with promising applications in different field. In this study, flexible anisotropic magneto-resistive (AMR) sensors were used for the scanning of a curved and flat sample with reference defects, to prove the capability of this method for curved surface scanning, and to benchmark the performance when compared to a more standard method using rigid giant magneto-resistive (GMR) sensors. Defects with depths ranging from 110 μm up to 2240 μm were detected with a signal-to-noise ratio (SNR) of 2.7 up to 27.9 employing flexible AMR sensors. T2 - XMR-Symposium CY - Wetzlar, Germany DA - 12.03.2025 KW - non-destructive testing KW - Flexible sensor KW - Magnetoresistance PY - 2025 SP - 1 EP - 6 AN - OPUS4-65045 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meng, Xiangmeng A1 - Bachmann, Marcel A1 - Kising, Pascal A1 - Yang, Fan A1 - Rethmeier, Michael T1 - Prediction of weld pool and keyhole geometries in high-power laser beam welding through a physics-informed generative artificial intelligence approach N2 - The weld pool and keyhole geometries are critical characteristics in evaluating the stability of the high-power laser beam welding (LBW) process and determining the resultant weld quality. However, obtaining these data through experimental or numerical methods remains challenging due to the difficulties in experimental measurements and the high computational demands of numerical modelling. This paper presents a physics-informed generative approach for predicting weld pool and keyhole geometries in the LBW process. With the help of a well experimentally validated numerical model considering the underlying physics in the LBW, the geometries of the weld pool and keyhole under various welding conditions are calculated, serving as the dataset of the generative model. A Conditional Variational Autoencoder (CVAE) model is employed to generate realistic 2D weld pool and keyhole geometries from the welding parameters. We utilize a β-VAE model with the Evidence Lower Bound (ELBO) loss function and include Kullback-Leibler divergence annealing to better optimize model performance and stability during training. The generated results show a good agreement with the ground truth from the numerical simulation. The proposed approach exhibits the potential of physics-informed generative models for a rapid and accurate prediction of the weld pool geometries across a diverse range of process parameters, offering a computationally efficient alternative to full numerical simulations for process optimization and control in laser beam welding processes. T2 - International Congress of Applications of Lasers & Electro-Optics 2025 CY - Orlando, USA DA - 12.10.2025 KW - Laser beam welding KW - Generative artificial intelligence KW - Machine learning KW - numerical simulation PY - 2025 SP - 1 EP - 10 AN - OPUS4-65075 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rosenbusch, Sjard Mathis A1 - Balzani, Daniel A1 - Unger, Jörg F. T1 - Regularization of softening plasticity models for explicit dynamics using a gradient-enhanced modified Johnson-Holmquist model N2 - The behavior of concrete under high strain rates is often described by plasticity models with softening, which is modeled by a reduction of the yield surface as a function of the local equivalent plastic strain. Among these are the RHT model, the K\&C model and the Johnson-Holmquist concrete model. These models are however local and therefore produce mesh-dependent results. In this contribution, the gradient-enhancement of such models is investigated. First, the mesh-dependency of these local formulations based on the analysis with a modified JH2 model as a representative for these constitutive formulations is demonstrated using a one-dimensional benchmark example. The central difference method is used as solver with a diagonal mass matrix obtained from a Gauß-Lobatto integration. In the benchmark, the width of the damaged zone decreases upon mesh-refinement and the dissipated plastic energy tends to zero. It is further shown that a significantly small safety factor for the critical time step is needed in order to achieve accurate results for the benchmark example. Next, two gradient-enhancement approaches are investigated. The enhancement is based on the inclusion of inertia and damping to the additional Helmholtz equation which enables the use of the central difference method as an explicit solver. In the first formulation, the yield surface and therefore the softening is formulated in terms of a nonlocal equivalent plastic strain. In the second approach, a hardening term which depends on the local equivalent plastic strain is introduced to the modified JH2 model in addition to the nonlocal softening. This approach is inspired by results from gradient plasticity in quasi-static loading scenarios. It is shown that the approach without hardening can still lead to mesh-dependent results while the model that includes hardening successfully inhibits strain localization and leads to a converging dissipated plastic energy. This is further confirmed in a two-dimensional wedge-splitting experiment where the damage pattern produced by the local model is mesh-dependent as well and the dissipated plastic energy tends to zero with mesh-refinement. The proposed nonlocal model with hardening results in a consistent damage pattern and the dissipated plastic energy converges. Furthermore, the nonlocal model with hardening is less sensitive to time step refinement, such that computational efficiency can be improved compared to the local model. The numerical experiments are implemented using the free and open-source tool FEniCSx. KW - Concrete modeling KW - Explicit Dynamics KW - FEniCS KW - Gradient plasticity KW - JH2 model KW - Mesh convergence PY - 2024 DO - https://doi.org/10.5281/zenodo.13983859 PB - Zenodo CY - Geneva AN - OPUS4-65083 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Schmidt, Anita A1 - Bohlmann, Janine A1 - Jacobasch, Stefan A1 - Kallies, Nicole A1 - Neitsch, Marcel T1 - Überprüfung der Wirksamkeit der Prüf- und Zulassungsprozeduren für Gefahrgutverpackungen und IBC in Deutschland KW - Gefahrgut-Verpackung KW - Bauart-Zulassung KW - IBC KW - Prüfung von Gefahrgutverpackungen PY - 2014 SP - 1 EP - 78 CY - Berlin AN - OPUS4-32647 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine T1 - Effects of UV radiation on the friction behavior of thermoplastic polyurethanes N2 - The effects of UV radiation and humidity condition on the frictional properties of TPU materials are presented in this paper. Photooxidative degradation of polymer leads to deterioration of physical and mechanical properties, which affect its tribological behavior significantly. Unfilled TPUs lose their anti-slip properties. T2 - The 6th World Tribology Congress CY - Beijing, China DA - 17.09.2017 KW - TPU KW - UV radiation KW - Friction PY - 2017 SP - 1 EP - 4 AN - OPUS4-42443 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Merchel, Silke A1 - Berger, Achim A1 - Görner, Wolf A1 - Radtke, Martin A1 - Riesemeier, Heinrich A1 - Reiche, I. A1 - Riederer, J. A1 - Duval, A. A1 - Guicharnaud, H. T1 - Non-Destructive Investigations of Dürer's Silver Point Drawings by Pixe and SY-XRF T2 - 7th International Conference on Non-destructive testing and Microanalysis for the Diagnostics and Conservation of the Cultural and Environmental Heritage ; art 2002 CY - Antwerp, Belgium DA - 2002-06-02 PY - 2002 UR - http://srs.dl.ac.uk/arch/publications/reiche/reiche_fullcorr.pdf SP - 82 AN - OPUS4-1400 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Radtke, Martin A1 - Berger, Achim A1 - Görner, Wolf A1 - Merchel, Silke A1 - Reiche, I. A1 - Riederer, J. A1 - Riesemeier, H. T1 - Spatial Resolved Trace Analysis of Dürer's Silver Point Drawings by Means of SR-XRF T2 - European Conference on Energy Dispersive X-Ray Spectrometry (EDXRS) CY - Berlin, Germany DA - 2002-06-16 PY - 2002 SP - 158 AN - OPUS4-1397 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Radtke, Martin A1 - Reiche, I. A1 - Berger, Achim A1 - Merchel, Silke A1 - Riesemeier, Heinrich A1 - Görner, Wolf A1 - Riederer, J. A1 - Roth, M. ED - Simionovici, A. T1 - BAMline meets Dürer and Van Eyck - Spatially resolved SR-XRF analyses of silver point drawings and their mysterious inscriptions T2 - 17th International Conference on X-Ray Optics and Microanalysis ; 17th ICXOM CY - Chamonix, France DA - 2003-09-22 PY - 2003 N1 - Serientitel: Spectrochimica acta : Part B, Atomic spectroscopy – Series title: Spectrochimica acta : Part B, Atomic spectroscopy IS - 59.2004,10/11 SP - 48 PB - Elsevier CY - Amsterdam AN - OPUS4-2690 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Berger, Achim A1 - Ecker, Klaus A1 - Görner, Wolf A1 - Radtke, Martin A1 - Reinholz, Uwe A1 - Riesemeier, Heinrich A1 - Segebade, Christian T1 - Strahlenverfahren in Kombination - ein Werkzeug für Analyse und Zertifizierung von Feststoffen T2 - 12. Jahrescolloquium "Analyse von Feststoffen unterschiedlicher Materialien aus Industrie und Umwelt" CY - Berlin, Deutschland DA - 2002-11-19 PY - 2002 SP - 1(?) AN - OPUS4-2025 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mair, Georg W. A1 - Hajhariri, Aliasghar A1 - Sklorz, Christian A1 - Kriegsmann, Andreas A1 - Müller, Karsten T1 - A modular concept for protection against debris flight - Design, properties and usage N2 - With advances in technological development, stationary and mobile storage units for compressed hydrogen are becoming larger and larger. Their number is also increasing. At the same time, their design has evolved from steel and aluminium to pressure vessels made of composite materials. For safety reasons the design approval of those composite cylinders requires fire engulfment tests, which are mainly organised as open-air tests always needs dedicated protection measures. Under some conditions those protections measures even reduce the effort for organisational safety measures if e.g. the emission of splinters can get totally prevented. Another aspect is the improved reproducibility of fire tests by reducing the influence of wind. Between 2017 and 2019, BAM developed a stackable protective frame made of steel to safely capture splinters for the safe execution of high-energy impact tests. However, this frame was not flexible enough for the follow-up project, which led to a completely new protection concept for (potentially) destructive tests on gas-filled pressure vessels. This concept is based on very robust building blocks made from welded steel. Despite their considerable weight of around 500 kg p.p., they can be combined and stacked very easily like ‘Lego bricks’. The presentation will show the flexibility of the concept, some results of tests on the robustness against pressure waves and the effectiveness in wind attenuation. Finally, the interaction with a new, also modular burner concept for localised fires and full engulfment fires will be presented. T2 - 11th International conference on hydrogen safety (ICHS 2025) CY - Seoul, Republic of Korea DA - 22.09.2025 KW - Splinter protection KW - Pressure vessel testing KW - Fire engulfment KW - Destructive tests KW - Rupture KW - Gaseous tests KW - Pressure wave KW - Test equipment KW - Precaution measures PY - 2025 SN - 979-1-2243-0274-2 VL - 2025 SP - 1428 EP - 1439 AN - OPUS4-65100 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Channammagari, Harichandana A1 - Sahr, Rabea A1 - Trappe, Volker T1 - Experimentelle, Analytisch-Numerische Untersuchung des thermischen Ausdehnungsverhaltens von Faser-Kunststoff-Verbunden N2 - Im Rahmen des Forschungsvorhabens PROVING wurde eine Methode zur rechnerischen Bestimmung thermomechanischer Eigenspannungen in CFK entwickelt. Ziel ist die Berücksichtigung des thermischen Ausdehnungsverhaltens bei der Bestimmung des dreidimensionalen in-situ-Spannungszustands der Matrix für den strukturellen Nachweis. Die Eigenspannungen werden über mikromechanische Modellierung und FEM berechnet; die zugrunde liegenden Ausdehnungsfunktionen wurden experimentell validiert. N2 - As part of the PROVING research project, a method for calculating thermomechanical residual stresses in CFRP was developed. The aim is to take thermal expansion behavior into account when determining the three-dimensional in-situ stress state of the matrix for structural verification. The residual stresses are calculated using micromechanical modeling and FEM; the underlying expansion functions have been experimentally validated. T2 - 43. Vortrags- und Diskussionstagung Werkstoffprüfung 2025 CY - Dresden, Germany DA - 27.11.2025 KW - Thermische Eigenspannungen KW - Mikromechanik KW - Faser-Kunststoff-Verbunde KW - FEM PY - 2025 SN - 978-3-88355-454-9 VL - 2025 SP - 154 EP - 159 PB - DGM CY - Sankt Augustin AN - OPUS4-65112 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Huo, Wenjie A1 - Schmies, Lennart A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael A1 - Wolter, Katinka T1 - An illumination based backdoor attack against crack detection systems in laser beam welding N2 - Deep neural networks (DNNs) have been wildly used in engineering and have achieved state-of-the-art performance in prediction and measurement tasks. A solidification crack is a serious fault during laser beam welding and it has been proven to be successfully detected using DNNs. Recently, research on the security of DNNs is receiving increasing attention because it is necessary to explore the reliability of DNNs to avoid potential security risks. The backdoor attack is a serious threat, where attackers aim to inject an inconspicuous pattern referred to as trigger into a small portion of training data, resulting in incorrect predictions in the reference phase whenever the input contains the trigger. In this work, we first generate experimental data containing actual cracks in the welding laboratory for training a crack detection model. Then, targeting this scenario, we design a new type of backdoor attack to induce the model to predict the crack as a normal state. Considering the stealthiness of the attack, a common phenomenon during the welding process, illumination, is used as the backdoor trigger. Experimental results demonstrate that the proposed method can successfully attack the crack detection system and achieve over 90% attack success rate on the test set. T2 - 8th ML4CPS 2025 – Machine Learning for Cyber-Physical Systems CY - Berlin, Germany DA - 06.03,2025 KW - System security KW - Welding crack detection KW - Backdoor attack KW - Deep neural networks PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-651357 DO - https://doi.org/10.24405/20021 VL - 2025 SP - 12 EP - 21 PB - Universitätsbibliothek der HSU/UniBw H CY - Hamburg AN - OPUS4-65135 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Cakir, Cafer Tufan T1 - Optimization of depth resolved X-ray absorption spectroscopy in grazing emission mode for characterizing compositionally complex alloys N2 - Layered materials are fundamental to technological advancements, offering distinct properties that differentiate them from bulk materials. In electronics, for instance, thin-film transistors (TFTs) are used to enhance charge transport and flexibility, thereby improving device performance. In the same way, thin-film photovoltaic devices used in renewable energy use strategic layering to absorb light more efficiently and separate electron-hole pairs more effectively, which leads to higher energy conversion efficiency. In recent decades, the development of new alloys has highlighted the importance of layered materials in another context. Compositionally complex alloys, for example, form multiple oxide layers on their surfaces when they oxidize. Studying these corrosion layers is crucial for understanding material-environment interactions. Typical surface analysis techniques, including X-ray photoelectron spectroscopy (XPS), secondary ion mass spectrometry (SIMS), and Meitner-Auger electron spectroscopy (MAES), provide valuable insights but are constrained by their requirements for high Vacuum conditions and their limited depth analysis. In contrast, X-ray absorption near-edge structure (XANES) spectroscopy presents a versatile and advantageous alternative. It operates effectively under ambient conditions and allows time-resolved measurements, enhancing the analysis of materials in real-time as they undergo structural and compositional changes. This adaptability broadens the scope for material analysis, allowing for a more comprehensive understanding of dynamic processes. Grazing Emission X-ray Fluorescence (GEXRF) spectroscopy stands out as a nondestructive, depth-resolved, element-specific characterization technique important for collecting depth-resolved information at the nanometer scale. Its ability to collect in-Depth resolved information based on the grazing emission angle of the fluorescence Radiation makes it ideal for investigating thin films, corrosion layers, and interfaces within layered materials. The integration of XANES in emission mode with GEXRF enables detailed exploration of the chemical states of the analyzed atom and provides depth-resolved information. This study discusses grazing emission X-ray absorption near-edge structure spectroscopy (GEXANES), a novel layer analysis technique that is created by integrating these two methods. This study also innovatively combines machine learning with GEXANES spectroscopy to reduce experimental times. By using active learning, a subset of machine learning, it refines the data acquisition process, enabling more efficient and streamlined methods. The application of active learning in this context illustrates the potential of data-driven approaches to transform experimental methodologies, particularly in resource-limited environments such as synchrotron facilities, thereby accelerating scientific research and discovery. KW - Angle resolved XRF KW - GEXRF KW - BO KW - Active Learning KW - XRF PY - 2025 DO - https://doi.org/10.34726/hss.2025.101302 SP - 1 EP - 129 CY - Technische Univeristät Wien AN - OPUS4-63793 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reiche, I. A1 - Berger, Achim A1 - Duval, A. A1 - Görner, Wolf A1 - Guicharnaud, H. A1 - Merchel, Silke A1 - Radtke, Martin A1 - Riederer, J. A1 - Riesemeier, Heinrich A1 - Roth, M. ED - Marabelli, M. ED - Tabaso, M. T1 - Spatially resolved SR-XRF analyses of complex drawings of the Holbein family T2 - 8th International Conference on "Non-Destructive Investigations and Microanalysis for the Diagnostics and Conservation of the Cultural and Environmental Heritage" CY - Lecce, Italy DA - 2005-05-15 KW - X-ray spectrometry KW - XRF KW - Röntgenfluoreszenzanalyse KW - RFA KW - Silverpoint drawing KW - Silberstiftzeichnung PY - 2005 SP - 7 pages PB - Italian Society of Non Destructive Testing CY - Lecce AN - OPUS4-7677 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weimann, Karin T1 - Optimierung des Rückbaus / Abbruchs von Gebäuden zur Rückgewinnung und Aufbereitung von hochwertigen RC-Baustoffen N2 - Die Nutzung des Wertstoffpotentials von Abfällen und Reststoffen ist ein Grundpfeiler im Schutz von natürlichen Ressourcen. Dabei ist der Aufbau und Erhalt von Stoffkreisläufen im Baubereich - aufgrund der großen Menge an Baurestmassen - von besonderer Ressourcenrelevanz. Während in Zukunft im Sinne der Nachhaltigkeit schon bei der Errichtung von Gebäuden auch auf Möglichkeiten zur Stoffstromtrennung beim Rückbau geachtet werden sollte, sind die heute rückzubauenden Bauwerke nicht unter diesem Gesichtspunkt errichtet worden. T2 - Baustoff Recycling Forum CY - Nürnberg, Deutschland DA - 10.02.2011 KW - RC-Baustoff Recycling KW - Beton KW - Gips KW - Abbruch PY - 2011 SP - 1 EP - 6 AN - OPUS4-23302 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Schreiber, Frank A1 - Nordholt, Niclas A1 - Lewerenz, Dominique T1 - Time-kill kinetics reveal heterogeneous tolerance to disinfectants N2 - Disinfection is an important strategy to limit the spread of infections. Failure of disinfection may facilitate evolution of resistance against disinfectants and antibiotics through the processes of cross-resistance and co-resistance. The best possible outcome of disinfection minimizes the number of surviving bacteria and the chance for resistance evolution. Resistance describes the ability to grow in previously inhibitory concentrations of an antimicrobial, whereas tolerance is associated with enhanced survival of lethal doses. Individual bacteria from the same population can display considerable heterogeneity in their ability to survive treatment (i.e. tolerance) with antimicrobials, which can result in unexpected treatment failure. Here, we investigated how phenotypic heterogeneity affects the ability of E. coli to survive treatment with six different substances commonly used as active substances in disinfectants, preservatives and antiseptics. A mathematical model which assumes that phenotypic heterogeneity underlies the observed disinfection kinetics was used to infer whether time-kill kinetics were caused by a tolerant subpopulation. The analysis identified bimodal kill kinetics for benzalkonium chloride (BAC), didecyldimethylammonium chloride (DDAC), and isopropanol (Iso). In contrast, kill kinetics by chlorhexidine (CHX), glutaraldehyde (GTA), and hydrogen peroxide (H2O2) were best explained by unimodal kill kinetics underpinned by a broad distribution of tolerance times for CHX as opposed to a narrow distribution of tolerance times for GTA and H2O2. These findings have implications for the risk of disinfection failure, with potential consequences for the evolution of antimicrobial resistance and tolerance. KW - Antimicrobial resistance KW - Bacteria KW - Standardization KW - Biocides PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-615572 DO - https://doi.org/https://doi.org/10.1101/2022.06.22.497202 SN - 2692-8205 SP - 1 EP - 20 PB - Cold Spring Harbor Laboratory CY - Cold Spring Harbor, NY AN - OPUS4-61557 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Schmidt, Selina T1 - Effects of biocides on processes underlying resistance evolution N2 - Antimicrobial resistance (AMR) is a global health problem. It is well known that antibiotics can drive evolutionary processes that underlie antimicrobial resistance (AMR) evolution and spread in clinical and environmental settings. In contrast, less is known about the effects of antimicrobial substances that are used as biocides (i.e. disinfectants and preservatives) on AMR evolution and spread. Biocides are present in various settings, interacting with diverse microbial communities. Therefore, it is crucial to evaluate their role in the evolution and dissemination of antimicrobial resistance. Biocides occur in a wide range of concentrations in various environmental settings. By examining how the various concentrations affect selection mechanisms, we gain insights into potential developments related to antimicrobial resistance. The aim of this PhD thesis is to investigate the effects of biocides on processes underlying resistance evolution. Specifically, the work focused on key mechanisms for resistance spread, resistance evolution, and the effect of selection pressures on evolved resistance mechanisms. The thesis is structured around three major objectives: (i) to determine the effect of biocides on the evolution of resistance by affecting the rate of occurrence of de novo mutations, (ii) to determine the effect of biocides on the spread of resistance genes by modifying the rate of horizontal gene transfer (HGT) processes, and (iii) to investigate the selective drivers of the emergence of antimicrobial resistance in adaptive laboratory evolution (ALE) experiments. De-novo mutations are spontaneous mutations that occur at a certain rate in microorganisms. The effect of biocides at subinhibitory environmentally relevant concentrations on the mutation rate in Acinetobacer baylyi, Bacillus subtilis and Escherichia coli was assessed with the fluctuation assay. The results showed that biocides affected mutation rates in a species and substance dependent matter. The bisbiguanide chlorhexidine digluconate, the quaternary ammonium compound didecyldimethylammonium chloride, the metal copper, the pyrethroid-insecticide permethrin, and the azole-fungicide propiconazole increase mutation rates in E. coli, whereas no increases were identified for B. subtilis and A. baylyi. Horizontal gene transfer refers to diverse mechanisms that mediate the transfer of mobile genetic elements between microorganisms. This work focused on conjugation and transformation. Conjugation is a process whereby a conjugative plasmid is transferred from a donor cell to a recipient cell. Transformation is a process whereby exogenous donor DNA is taken up into a recipient cell and integrated into the recipient’s’ genome. The effects of subinhibitory environmentally relevant biocide concentrations on the conjugation rate of E. coli and the transformation rate of the naturally competent organisms A. baylyi in were assessed. The results showed that benzalkonium chloride (BAC), chlorhexidine and permethrin increased conjugation in E. coli, while none of the biocides increased transformation rates in A. baylyi. To further understand the molecular mechanisms underlying the effects on mutation and conjugation rates, I investigated the induction of the RpoS-mediated general stress and the RecA-linked SOS response upon biocide exposure. The results show a link between the general stress and the SOS response with increased rates of mutation and conjugation, but not for all biocides. One major approach to study the evolutionary response of bacteria to antimicrobials are ALE experiments with growth at subinhibitory concentrations linked to serial subculturing over many generations. Such experiments have been used to study resistance evolution to antibiotics and biocides. However, previous work showed that adaptation to biocide stress may be mediated by different evolutionary drivers. Here, I investigated the contributions of evolution for increased survival as opposed to improved growth in ALE experiments with E. coli exposed to subinhibitory BAC concentrations. Two distinct evolutionary treatments selecting for survival only or survival and growth led to specific evolutionary adaptations apparent in the phenotypes and genotypes of the evolved populations. Populations growing in the presence of BAC evolved increased fitness in the presence of BAC associated with higher resistance to BAC and cross-resistance to antibiotics, while this was not the case for populations evolving for increased survival only. Genotypic characterization by whole genome sequencing of the evolved populations revealed parallelism in mutated genes among replicate populations and distinct differences across treatments. Treatments selecting for survival and growth showed mutations in stress response related genes (hslO and tufA), while selection for survival led to mutations in genes for metabolic regulation (cyaA) and cellular structure (flagella fliJ). In summary, this thesis shows that biocides affect AMR evolution and emphasizes the importance of understanding of how biocides impact the molecular and evolutionary process that underlie AMR evolution. KW - Biocides KW - Antimicrobial resistances KW - Microbial survival mechanisms PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:188-refubium-43383-9 SP - 1 EP - 101 PB - Freie Universität CY - Berlin AN - OPUS4-60678 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Epishin, A.I. A1 - Link, T. A1 - Nolze, Gert A1 - Fedelich, Bernard A1 - Schriever, Sina T1 - Creep behaviour of the single-crystal nickel-base superalloy CMSX-4 at ultra-high homologous temperature N2 - Data about the creep behaviour of metals and their alloys at temperatures close to the melting point are very limited. The reason is that most engineering alloys are used at temperatures below 0.6-0.8 of their melting point, so, Investigation of creep at higher temperatures has no practical relevance. For some special applications however it is important, in our case hot isostatic pressing (HIP) of single-crystal turbine blades cast from nickel-base superalloys. In order to remove porosity the blades are HlPed at temperatures between y'-solvus and solidus where superalloy has no strengthening y'-phase and therefore is very soft. For example, the Company Howmet Castings HIPs the superalloy CMSX-4 at the temperature 1288aC, which corresponds to a homologous temperature of about 0.97=1561 K/1612 K (solidus temperature). Therefore knowledge about the creep behaviour of CMSX-4 at this temperature and understanding of the creep mechanisms are necessary to model the kinetics of pore closure during HIP as well as to plan the Parameters of the HIP process. T2 - CREEP 2015 - 13th International conference on creep and fracture of engineering materials and structures CY - Toulouse, France DA - 31.5.2015 PY - 2015 VL - 825 SP - 19 EP - 20 AN - OPUS4-33527 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klippel, A. A1 - Hofmann-Böllinghaus, Anja A1 - Piechnik, K. A1 - Gnutzmann, Tanja T1 - Development of toxicity assessment method for bus interior materials N2 - In recent years, fire safety requirements for bus interior materials have been increased and introduced into international regulations. Fire safety requirements for the burning rate, melting and dripping behaviour of interior materials already exist for many years. However, it remains unclear to what extent the release of smoke, combustion products and their toxicity should be limited. Therefore, a research and development project 82.0723 funded by BASt (Federal Highway Research Institute) was initiated to develop a simplified procedure for testing the toxicity and smoke development in case of fire of interior materials used in buses. The scope of the research included calculations to assess the toxicity of fire gases and the derivation of specifications for the formation of practicable limit values for smoke toxicity. Further investigations are needed to derive these limit values for smoke toxicity in order to be applicable for real fire scenarios in buses. T2 - Conference Fire in Vehicles FIVE CY - Stavanger, Norway DA - 24.04.2023 KW - Bus materials PY - 2023 SP - 80 EP - 90 AN - OPUS4-57627 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Scheibe, Maximilian A1 - Binkowski, Sigrid A1 - Benemann, Sigrid A1 - Saliwan Neumann, Romeo T1 - Comparing different preparation techniques for the characterisation of niobium carbides N2 - Of the up to 85.000 tons of niobium that are produced at the present, 90% are used as a property defining micro alloying element [1,2] in: a. High- and highest strength alloys for car bodies, b. Structural steels in the construction industry and, c. Steels for pipelines and the petrochemical industry, whereby it is mostly added for alloying in the ränge of 80-250 ppm. PY - 2014 IS - 19 SP - 1 EP - 12 AN - OPUS4-32432 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wolf, Marcus A1 - Afanasiev, Roman A1 - Böllinghaus, Thomas A1 - Pfennig, A. T1 - Investigation of Corrosion Fatigue of Duplex Steel X2CrNiMoN22-5 3 Exposed to a Geothermal Environment under Different Electrochemical Conditions and Load Types N2 - Corrosion fatigue (CF) of duplex stainless steel (DSS) X2CrNiMoN22-5-3 was investigated in in-situ geothermal conditions of the Northern German Basin (NGB). The influence of the load type on CF behavior of the alloy was examined by applying push/pull and rotating bending cyclic load to failure. The hour-glass shaped specimens with both polished and precisely turned surface finish were tested in corrosion chambers allowing for the permanent circulation of Northern German Basin electrolyte heated to 369 K. Additionally, the influence of a protective cathodic potential on the CF life expectancy was investigated by employing a potentiostat. The rotating bending cyclic load led to a higher CF life expectancy, which decreased with increasing duration of the experiment due to a higher deterioration rate of the material. The application of a cathodic potential caused a significant increase of the CF lifespan from 4.7 x 105 (open-circuit potential (OCP)) to 107 cycles (preset threshold cycle number) for the potential range from USHE = – 450 to – 900 mV. Microstructural analysis of the CF damage revealed horizontal grain attack within corrosion pit cavities, multiple fatigue cracks and preferable deterioration of the austenitic phase. T2 - 13th International Conference on Greenhouse Gas Control Technologies, GHGT-13 CY - Lausanne, Switzerland DA - 14.11.2016 KW - Different load cases KW - Corrosion fatigue KW - DSS KW - Geothermal environment KW - Different electrochemical conditions PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-439231 DO - https://doi.org/10.1016/j.egypro.2017.03.1657 SN - 1876-6102 VL - 114 SP - 5337 EP - 5345 PB - Elsevier Science AN - OPUS4-43923 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Knaust, Christian A1 - Krause, Ulrich A1 - Hofmann-Böllinghaus, Anja A1 - Schneider, U. T1 - Modeling fire scenarios in buildings with CFD N2 - In the frame of the European harmonization, new European technical standards (Eurocodes) have been developed in recent years. Classical methods, like tables and simplified analytical procedures, as well as general engineering techniques are allowed by the Eurocodes for the fire protection design. The modeling and calculation of fire scenarios with CFD (Computational Fluid Dynamics) numerical methods is one of the general engineering methods. It is nowadays still difficult to check and evaluate the CFD results for their use as technical documents for fire safety design. Analytical engineering techniques, zone models and CFD-models have been used and compared in the present work for the prediction of the fire development in a building. To solve the conservation equation for the CFD-model, the CFD-program FDS, with the mixture fraction model, and the CFD-program FLUENT, with the one step reaction model as well as with the volumetric source term model, have been used. The combustion of polyurethane is modeled in FDS by specifying the heat release rate and the stoichiometry. For the combustion in volumetric source term model, the heat release rate and the smoke release were specified with respect to the stoichiometry. The input parameter for the one step reaction model is the pyrolysis mass flow. In the one step reaction model, the transport equations for polyurethane, H₂O, N₂, O₂, CO₂, CO and C (soot) are solved and the heat of combustion is determined from the standard formation enthalpy of all the components. In volumetric source term model, the transport equation is solved for air and smoke. FDS solves the transport equation for the mixture fraction. To model the fire development, and where no literature data was available, the required material characteristics like specific heat capacity, absorption coefficient and heat of combustion were measured. In all the investigated CFD-models the heat- and species transport equation has been solved and the absorption coefficient of soot has been considered. Furthermore, the fire development has also been investigated using zone models with the programs CFAST and MRFC. Results from analytical engineering techniques (plume calculations), which were design criteria in the past, have been used as plausibility checks for the present work. The calculation results from the investigations were compared to measurements in the same building performed by the National Institute for Standards and Technology (NIST). T2 - 11th International Symposium on Fire Protection CY - Leipzig, Germany DA - 08.06.2010 KW - CFD KW - Computational fluid dynamics KW - Zone model KW - Analytical technique KW - Combustion KW - Soot model KW - FLUENT KW - FDS KW - CFAST KW - MRFC KW - Measurements PY - 2010 SN - 978-3-00-03966-2 N1 - Geburtsname von Hofmann-Böllinghaus, Anja: Hofmann, A. - Birth name of Hofmann-Böllinghaus, Anja: Hofmann, A. SP - 1 EP - 14 PB - Vereinigung zur Förderung des Deutschen Brandschutzes (vfdb) CY - Münster AN - OPUS4-23159 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geoerg, Paul A1 - Hofmann-Böllinghaus, Anja A1 - Pulm, A. T1 - Evacuation dynamics under consideration of vulnerable pedestrian groups N2 - The understanding of human behavior during evacuation processes is an important matter to improve the safety of infrastructures. In many countries, the implementation of performance based codes enables fire safety engineers to use computer based calculation tools to predict and evaluate pedestrian movement and human behavior in buildings. The models are based on experimentally obtained parameters and theoretical models. Pedestrian behavior can be influenced by the characteristics of the buildings (e.g. type of the building) as well as the characteristics of individuals and the pedestrian group. This paper shows that the approach of Required Safe Egress Time (RSET) / Available Safe Egress Time (ASET) is imprecise with regard on heterogeneous pedestrian groups, because this concept completely neglected the variability’s in individual pre-movement and movement abilities. T2 - Interflam CY - Royal Holloway College, London, UK DA - 04.07.2016 KW - Evacuation KW - Vulnerable groups KW - Simulation KW - Egress PY - 2016 SN - 978-0-9933933-1-0 SN - 978-0-9933933-3-4 VL - 1 SP - 769 EP - 774 CY - London, UK AN - OPUS4-36821 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hofmann-Böllinghaus, Anja A1 - Kaudelka, Sven T1 - Fire safety of facades with polystyrol foam insulation N2 - Several fires involving ETIC (external thermal insulation composite) systems with polystyrene foam insulation in Germany led to an extensive discussion about fire safety of such systems. A collection initiated by the Frankfurt fire service of façade fires which include polystyrene insulation foam shows that especially fires which started in front of the buildings led to more severe fires of the façade than fires that started inside the buildings. In several fires the ignition source were burning waste containers. Three large scale tests which were initiated by German building ministries showed weaknesses of the existing systems when challenged by a bigger fire source in front of the façade. Since then measures have been introduced to enhance these systems and an additional test with a 200 kg wood crib in front of a large test rig has been used for approval of ETICS. However, the recently introduced German draft standard DIN E 4102-20 does not take these changes into account although real cases and the large scale tests showed that fire scenarios with a bigger ignition source as a waste container are not covered by the DIN E 4102-20. Numerical investigations show that regarding the heat flux to the area above the opening (e.g. a window) also only a fraction of real fires is covered. Additionally damaged systems have been investigated using the Single Burning Item (SBI) test with higher heat release rates of the burner. The damage significantly influenced the fire development of the specimen. Collapse of a damaged coating of an ETIC system occurred during the test and had a sudden fire growth as a result as the whole specimen was suddenly on fire. Several effects which could be seen in the intermediate scale tests correspond to observations which were made in the real cases. In Germany insulation of existing buildings is often enhanced with application of ETICS. In most cases the buildings are in use at the time when the construction takes place. At several stages of the construction process large amounts of unprotected polystyrene are stored in immediate proximity of the building and unprotected polystyrene can be in place on the façade for several weeks. As a consequence of the investigations challenges and possible measures to enhance fire safety of ETIC systems are discussed. T2 - Interflam 2016 CY - London, UK DA - 04.07.2016 KW - Fire scenarios KW - Fire safety KW - EPS PY - 2016 SN - 978-0-9933933-2-7 VL - 2016 SP - 1151 EP - 1162 PB - Interscience Communications CY - Bromley, UK AN - OPUS4-36895 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böllinghaus, Thomas A1 - Hoffmeister, H. T1 - Hydrogen permeation in supermartensitic stainless steels dependent on heat treatment and chemical composition N2 - Hydrogen might cause severe degradation of supermartensitic stainless steels, if they are activated during exposure to sour environments. Consistent and comprehensive data for hydrogen transport in these materials are thus required to support, in particular, modelling of hydrogen assisted cracking as a part of life time assessment of welded steel components. In addition to previously published diffusion coefficients and subsurface concentrations of a supermartensitic stainless steel further data dependent on heat treatment are provided by this contribution. Furthermore, a higher alloyed material has been investigated in the state as received and also in the quenched condition, in order to approach the influences of chemical composition on hydrogen transport in supermartensitic stainless steels. With respect to welding it turned out that the diffusion coefficient and the subsurface concentration are markedly dependent on heat treatment of the materials. T2 - Corrosion 2000 CY - Orlando, FL, USA DA - 2000-03-26 PY - 2000 SP - Paper 00141, 1 EP - 19 PB - NACE International CY - Houston, Tex. AN - OPUS4-11844 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wu, Hongyi A1 - Buhk, Frederik A1 - Christiani, Ricardo A1 - Hofmann-Böllinghaus, Anja T1 - Influence of local vegetation on ignition and fire spread of vegetation fires-Experimental and numerical approach N2 - Within the framework of the European TREEADS project, Brandenburg and Saxony-Anhalt were designated as model regions. This designation facilitated the investigation of vegetation types, soil structure, and soil dryness. Brandenburg and Saxony-Anhalt are identified as the driest regions in Germany according to the annual mean soil moisture data. In these regions, 48% to 73% of the forests are composed of pine species. The soil profile is characterized by a relatively thin organic layer, measuring between 0.2 and 0.3 meters, underlain by sandy substrates. Consequently, surface and ground fires are more prevalent in these areas compared to other types of fires, such as crown fires. To investigate the influence of local vegetation, it goes through two aspects. One is laboratory study, the local vegetation samples were collected and tested for the thermal properties, such as activation energy, heat content and reaction kinetic of pyrolysis and dehydration. At the same time, small and medium scale combustion experiments were conducted to investigate the burning behavior. The other aspect is using the thermal properties as the input parameters for the development of numerical simulation in the computational fluid dynamics (CFD) tool. These models were then be validated with the combustion experiments, as a baseline for the further scaling up of the models, in order to investigate how the parameters influencing the fire spread in a large-scale case numerically. T2 - Interflam 2025, 16th International Fire Science and Engineering Conference CY - London, United Kingdom DA - 30.06.2025 KW - Wildfire PY - 2025 SP - 2221 EP - 2225 PB - Interscience CY - London AN - OPUS4-63932 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böllinghaus, Thomas A1 - Kannengießer, Thomas T1 - Steps to more conclusive testing of welded supermartensitic stainless steel pipes T2 - 2nd International Conference Supermartensitic Stainless Steels 2002 CY - Brussels, Belgium DA - 2002-10-03 KW - Component testing KW - Conclusive test sequences KW - Hydrogen assisted cracking KW - Supermartensitic stainless steels KW - Martensite transformation KW - Welded pipelines PY - 2002 SP - 71 EP - 76 PB - KCI Publ. CY - Zutphen AN - OPUS4-2301 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ganesh, Rahul A1 - Gesell, Stephan A1 - Kuna, M. A1 - Fedelich, Bernard A1 - Kiefer, B. T1 - Numerical calculation of ΔCTOD for thermomechanical fatigue crack growth N2 - The cyclic crack tip opening displacement ΔCTOD is a promising loading Parameter to quantify the crack propagation under thermomechanical fatigue (TMF). In this work, suitable techniques are investigated and compared for an accurate calculation of ΔCTOD under TMF loading using a viscoplastic temperature dependent material model. It turned out that collapsed special crack tip elements give the best results. An efficient FEM-technique is developed to simulate the incremental crack growth by successive remeshing, whereby the deformations and internal state variables are mapped from the old mesh onto the new one. The developed techniques are demonstrated and discussed for two-dimensional examples like TMF-specimens. Recommendations are made regarding important numerical control parameters like optimal size of crack tip elements, length of crack growth increment in relation to plastic zone size and ΔCTOD value. N2 - Zur Bewertung des Rissfortschritts unter thermomechanischer Ermüdung (TMF) ist die zyklische Rissöffnungsverschiebung ΔCTOD ein aussichtsreicher bruchmechanischer Beanspruchungsparameter. In dieser Arbeit werden unter Anwendung eines viskoplastischen, temperaturabhängigen Materialmodells geeignete FEM-Techniken für die akkurate Berechnung des ΔCTOD bei TMF erprobt und verglichen. Als beste Technik hat sich die Verwendung kollabierter Rissspitzenelemente erwiesen. Es wurde ein effizienter FEM-Algorithmus zur Simulation der Rissausbreitung mit inkrementeller Neuvernetzung entwickelt, bei dem die Verformungen und inelastischen Zustandsvariablen jeweils vom alten auf das neue Netz übertragen werden. Die erarbeiteten Techniken werden am Beispiel von zweidimensionalen Strukturen und TMF-Proben vorgestellt und diskutiert. Dabei werden wesentliche Kontrollparameter der Simulation wie optimale Grösse der Rissspitzenelemente, Länge des Rissinkrementes in Relation zur plastischen Zone und dem ΔCTOD-Wert empfohlen. T2 - 53. Tagung des Arbeitskreises "Bruchmechanik und Bauteilsicherheit" CY - Online meeting DA - 18.02.2021 KW - Crack tip opening displacement KW - Thermomechanical fatigue KW - Crack growth PY - 2021 SP - 1 EP - 10 PB - DVM (Deutscher Verband für Materialforschung und -prüfung) CY - Berlin AN - OPUS4-52519 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Müller, Simon T1 - FireSpread_MedEU N2 - Wildfires are becoming more frequent and severe under the influence of climate change, posing increasing risks to ecosystems, human health, and infrastructure. Accurate spatiotemporal data on wildfire propagation is essential for advancing fire behavior modeling, improving management strategies, and mitigating future impacts. However, existing datasets with both high spatial and temporal resolution are rare, costly, and time-consuming to produce. To address this gap, we present FireSpread_MedEU, a dataset comprising 313 consecutive burned area maps from 102 wildfire events across the Mediterranean and Europe between 2017 and 2023. Burned areas were derived from high-resolution Planet optical satellite imagery (~3 m spatial, mostly daily temporal resolution) using a semi-automated workflow, followed by manual refinement to ensure highest accuracy. Each dataset entry is enriched with detailed metadata and a subjective quality assessment. With its high level of spatiotemporal precision, FireSpread_MedEU provides essential data for the development and validation of machine learning models or wildfire simulation models. It opens new research opportunities in wildfire behavior analysis, risk assessment, and predictive modeling. KW - Wildfire KW - Spread KW - Machine Learning PY - 2025 DO - https://doi.org/10.5281/zenodo.16813435 PB - Zenodo CY - Geneva AN - OPUS4-64768 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ganesh, R. A1 - Gesell, Stephan A1 - Fedelich, Bernard A1 - Kuna, Meinhard A1 - Kiefer, B. T1 - Procrackplast: Eine Software zur Simulation des 3D-Risswachstums unter großen plastischen Deformationen T1 - Procrackplast: A software for simulating 3D crack growth under large plastic deformation N2 - The finite element software ProCrackPlast is developed for the automated simulation of fatigue crack growth in arbitrarily loaded three-dimensional components with large scale plastic deformations, in particular under cyclic thermomechanical (TMF) loading. ProCrackPlast is developed by extending the software Procrack, created at TU Freiberg for linear-elastic crack growth simulations. The pre-processing, FEM analysis, and the post-processing in ProCrackPlast are done by the commercial software ABAQUS. ProCrackPlast resorts to a crack growth procedure which adaptively updates the crack in finite increments based on the fracture-mechanical parameter, cyclic crack tip opening displacement ΔCTOD . Features of this software along with two application examples of fatigue crack growth in a typical cast steel, Ni-Resist, are presented in this paper to show its capability and performance. N2 - Es wird die Finite-Element-Software ProCrackPlast vorgestellt, die eine automatische Simulation der Ermüdungsrissausbreitung in beliebig belasteten dreidimensionalen Bauteilen mit größeren plastisch verformten Bereichen ermöglicht, insbesondere bei thermomechanischer Wechselbelastung (TMF). ProCrackPlast entstand durch Erweiterung des Programs ProCrack, das an der TU Freiberg für linear-elastische inkrementelle Rissfortschrittsanalysen entwickelt wurde. Das Pre-Processing, die FEM Analyse und das Post-Processing werden mit Hilfe der kommerziellen FE-Software ABAQUS durchgeführt. ProCrackPlast beruht auf einem Algorithmus, mit dem der Rissfortschritt adaptiv in endlichen Inkrementen unter Verwendung des bruchmechanischen Parameters der zyklischen Rissöffnungsverschiebung ΔCTOD gesteuert wird. Die Funktionseigenschaften dieser Software werden anhand von zwei Anwendungsbeispielen zum Ermüdungsrisswachstum für einen typischen Stahlguss, Ni-Resist, exemplarisch dargestellt, um die Möglichkeiten und Leistungsfähigkeit von ProCrackPlast zu demonstrieren. T2 - 54. Tagung des Arbeitskreises "Bruchmechanik und Bauteilsicherheit" CY - Online meeting DA - 22.02.2021 KW - Automated finite element analysis KW - Automatische Finite Element Simulation KW - Thermomechanical fatigue KW - Crack growth KW - Thermomechanische Ermüdung KW - Rissausbreitung PY - 2022 SP - 205 EP - 214 PB - Deutscher Verband für Materialforschung und -prüfung e.V. AN - OPUS4-54435 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gollnow, C. A1 - Kannengießer, Thomas ED - Böllinghaus, Thomas ED - Lippold, J. E. ED - Cross, C. E. T1 - Consideration of welding-specific component design on solidification crack initiation N2 - A commonly used way of minimizing the occurrence of hot cracks, especially solidification cracks during component welding, is mainly to analyse and vary process parameters such as welding speed and consequently the heat input. Metallurgy and component design are however hardly ever considered due to special production requirements and therefore, restricted flexibility in material selection and design. Such conditions, especially crack-critical welding positions are given by slot-welds or welds near pre-deformed areas, for instance bending edges. Hence, it follows that increased local and global residual component stress caused cracking on reaching a solidification crack critical level, which is characterised by solidification crack initiation. T2 - 4th International Workshop Cracking Phenomena in Welds CY - BAM, Berlin, Germany DA - 02.04.2014 KW - solidification cracks PY - 2016 SN - 978-3-319-28432-3 DO - https://doi.org/10.1007/978-3-319-28434-7_6 SP - 101 EP - 117 PB - Springer International Publishing CY - Cham, Switzerland AN - OPUS4-36567 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rosen, Andrew S. A1 - Gallant, Max A1 - George, Janine A1 - Riebesell, Janosh A1 - Sahasrabuddhe, Hrushikesh A1 - Shen, Jimmy-Xuan A1 - Wen, Mingjian A1 - Evans, Matthew L. A1 - Petretto, Guido A1 - Waroquiers, David A1 - Rignanese, Gian-Marco A1 - Persson, Kristin A. A1 - Jain, Anubhav A1 - Ganose, Alex M. T1 - Jobflow: Computational Workflows Made Simple N2 - Jobflow is a free, open-source library for writing and executing workflows. Complex workflows can be defined using simple python functions and executed locally or on arbitrary computing resources using the FireWorks workflow manager. Some features that distinguish jobflow are dynamic workflows, easy compositing and connecting of workflows, and the ability to store workflow outputs across multiple databases. KW - Automation KW - Workflows KW - Computational Materials Science PY - 2024 DO - https://doi.org/10.5281/zenodo.10466868 PB - Zenodo CY - Geneva AN - OPUS4-59313 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ueltzen, Katharina A1 - Naik, Aakash A1 - Ertural, Christina A1 - Benner, Philipp A1 - George, Janine T1 - Software and data repository: Can simple exchange heuristics guide us in predicting magnetic properties of solids? N2 - Software and data for the publication "Can simple exchange heuristics guide us in predicting magnetic properties of solids?" Release that corresponds to the first preprint version of the article. Full Changelog: https://github.com/DigiMatChem/paper-exchange-heuristics-in-magnetic-materials/commits/v1.0.0 KW - Magnetism KW - Machine Learning KW - Materials Design KW - Chemically Complex Materials KW - Sustainable Materials Design PY - 2025 DO - https://doi.org/10.5281/zenodo.16811104 PB - Zenodo CY - Geneva AN - OPUS4-64672 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Smales, Glen Jacob A1 - Pauw, Brian Richard T1 - Technical Drawings for The MOUSE Modular Sample Holder N2 - OpenSCAD, STL and technical drawings for the Modular sample holder designed primarily for use with The MOUSE instruments. This modular sample holder can be used in conjunction with the following: - Capillary flow-cell for liquid samples (10.5281/zenodo.7499421) - Solid sample rack/plate (10.5281/zenodo.7499424) - Laser-cut sample holder (10.5281/zenodo.7499437) KW - X-ray scattering KW - SAXS KW - Sample holder KW - MOUSE PY - 2023 DO - https://doi.org/10.5281/zenodo.7499416 PB - Zenodo CY - Geneva AN - OPUS4-56775 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kannengießer, Thomas A1 - Böllinghaus, Thomas A1 - Zimmer, Peter T1 - Investigations of cold cracking by the CTS-Test at various cooling conditions N2 - Numerous national and international activities of regulation and standardization of cold cracking tests are currently being undertaken. Most of these test procedures operate as crack-no-crack tests and are focussed on the determination of technological parameters, as for instance the welding conditions and the heat input as well as pre- and postheating temperature and times. Such parameters predominantly influence the cooling conditions of the weld, which significantly affect the three well known local parameters on hydrogen cracking microstructure, hydrogen concentration and mechanical load. As one of the test procedures, the CTS-Test is currently standardized in the draft standard prEN ISO17642 which has been prepared on the European level by CEN/TC 121/WG 13 (destructive tests on welds). As compared to other cold cracking tests, quite extensive specimen cooling procedures are prescribed for the CTS-Test. As a contribution to the ongoing discussion the present document highlights the effect of different cooling procedures after welding propagated for the modified CTS-Test. The major part of the work includes a comparison of experimentally determined cooling curves at specific weld locations with respective thermal finite element analyses. As a result, it turned out that the prescribed water cooling after welding does not alter the microstructure relevant cooling time Δt(8/5) and the cold cracking relevant cooling time Δt(3/1) as compared to simple air cooling. With increasing preheating temperature the effect of water cooling becomes more pronounced on the cooling time Δt(3/1), but still does not affect the cooling time Δt(8/5). The effects of rapid cooling of the CTS specimens after welding have thus to be reconsidered, in particular, with respect to its transferability to component welds and to additional non-realistic quenching effects. T2 - 56th IIW Annual Assembly - International Conference on Welded Construction for Urban Infrastructure CY - Bucharest, Romania DA - 10.07.2003 KW - Kaltrisstests KW - Schweißsicherheit PY - 2003 SP - 1 EP - 12 PB - International Institute of Welding CY - Roissy AN - OPUS4-2630 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nolze, Gert A1 - Saliwan Neumann, Romeo A1 - Buchheim, Michaela T1 - Microstructure investigations of iron meteorites by EBSD and EDS analyses N2 - Meteorites are a unique and inspiring material for microstructural studies because if their very specific genesis. Iron meteorites have been formed under unimaginable cooling rates of a few ten Kelvins per million years so that the observable transformation of the formerly huge Fe-Ni single crystals of taenite occurred under nearly-equilibrium conditions. Octahedrites (meteorites having a Ni content between 6...15%) are characterized by ribbons of the low-temperature Fe-Ni phase kamacite separated by rims of residual taenite. This very specific feature is known as Widmanstaetten structure and has been investigated by synchrotron radiation in order to cover a higher volume fraction for a statistically relevant description of orientation relationships. However, plessite – a microstructure mainly consisting of the same phases – reflects the orientation relationship between kamacite and taenite as well. For their characterization, a scanning electron microscope is very suitable in order to investigate crystal orientations or identify phases. Despite the apparently ideal formation circumstances of iron meteorites, Ni concentration profiles prove non-equilibrium conditions. Combined EDS (energy dispersive spectroscopy) and EBSD (electron backscatter diffraction) measurements at a selected plessitic region of the Cape York iron shows that a correlation exists between Ni-concentration and the locally detected orientation relationship. T2 - 15th European Microscopy Congress CY - Manchester, UK DA - 16.09.2012 KW - Phase identification KW - Corrosion KW - Chloride KW - Dermbach PY - 2012 SP - 90 AN - OPUS4-37775 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hofmann-Böllinghaus, Anja T1 - Fire Safety of Facades N2 - Fire safety of façades is a complex topic regarding the different façades systems which differ in build and as well in possible fire safety measures. A great variation of materials is used in façade systems which also have a wide spread variation of reaction-to-fire behaviour. As building regulations are national legislations the implementation of fire safety of façade systems in building regulations differs significantly in different countries. Therefore the testing and classification of façade systems differs as well hugely. Approaches to regulate the material only are as well in use as to concentrate mainly on large scale testing and several approaches in between. It was not possible yet to find a harmonized test for façades in Europe. However, in many countries severe fires with combustible façade systems brought the challenges of fire safety of façades to a greater awareness. An overview over different large scale test and implementation in building regulations shows the differences. Challenges in fire safety of façades regarding the testing, the weathering, aging and damage of the systems and the impact on fire safety are discussed. T2 - Interflam 2016 CY - London, UK DA - 04.07.2016 KW - Facades KW - Fire safety KW - Combustible PY - 2016 SN - 978-0-9933933-2-7 VL - 2016 SP - 1095 EP - 1102 PB - Interscience Communications CY - Bromley, UK AN - OPUS4-36896 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Junias, Josua Kondja A1 - Holtappels, Kai A1 - Liebner, Christian A1 - Thewis, Max A1 - Askar, Enis A1 - Shaanika, Erasmus T1 - Hydrogen Mixtures Flammability Limits Prediction using Machine Learning Models N2 - Flammability characteristics of hydrogen mixtures have been extensively investigated at different initial conditions(temperature and pressure). Based on the available experimental datasets, empirical and semi-empirical models are commonly used to calculate flammability limits in dependance to initial conditions and mixture composition to reduce the experimental effort. However, unevenly distributed empirical data and the complex non-linear relationship characteristics of these data present significant challenges to empirical flammability limits prediction methods under various mixture initial conditions. Moreover, the empirical models and semi-empirical models only cover some influencing parameters, respectively. To address these issues, the present study adapts a machine learning (ML) approach for improving the hydrogen-air/oxygen-inert gas mixture flammability limits prediction at different conditions with a holistic approach. A Multi-Layer Perceptron (MLP) model was trained, validated, and tested using key input features such as flammability state, initial mixture temperature, equivalence ratio, inert gas concentration, adiabatic flame temperature, and Lewis numbers. Data augmentation techniques were conducted on experimental datasets to improve the predictive capability of the model. The models’ performance was compared with empirical flammability limit prediction methods. The goal is to deliver fast, reliable, and more accurate predictions across different scenarios with a single prediction model. Most importantly, the machine learning approach offers a cost-effective and robust alternative to existing empirical flammability limit prediction methods, thus also reducing the experimental effort for explosion limits determination. T2 - 11th International Conference on Hydrogen Safety (ICHS) 2025 CY - Seoul, South Korea DA - 22.09.2025 KW - Machine Learning KW - Flammability Limits PY - 2025 SN - 979 -12 -243 -0274 - 2 SP - 1389 EP - 1401 AN - OPUS4-64624 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Popiela, Bartosz A1 - Günzel, Stephan A1 - Mair, Georg W. T1 - Discussion of creep phenomena during initial loading of type 4 composite pressure vessels N2 - To maintain the highest safety standards for compressed gas storage in composite pressure vessels, a deeper understanding of their ageing mechanism is required. In this study, two designs of type 4 cylinders were manufactured the only difference being the internal pressure function used during the filament winding process. Hence, their residual stress state and the quality of the composite layers varied. Ten pressure vessels were initially loaded under sustained pressure and increased temperature and later subjected to slow burst tests. Comparing the results with cylinders tested in a pristine state underlines a significant improvement in the performance of initially loaded cylinders of one of the designs. This phenomenon was caused by a significant decrease of the scattering of burst pressures within a sample. At the same time, a slight decrease of the burst pressures could be observed. An explanation of this behavior could be supported by strain measurements with fiber optic sensors, which were embedded in the composite material. The strains measured during the initial loading indicate a stress redistribution, which has an impact on the strength of the pressure vessel. Moreover, an increased stiffness during the slow burst tests after initial loading was observed that indicates a better exploitation of the individual layers of the composite structure. The study supports previous observations on the increased performance after initial loading and provides new insights into the strain development in creep effects in type 4 pressure vessels. T2 - Pressure Vessels & Piping Conference PVP2025 CY - Montreal, Quebec, Canada DA - 20.07.2025 KW - Type 4 pressure vessel KW - Creep KW - Fiber optic sensors KW - Slow burst test KW - Mechanics of composites PY - 2025 SN - 978-0-7918-8907-7 VL - 2025 SP - 1 EP - 7 PB - ASME AN - OPUS4-63897 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schreiber, Frank T1 - Differential selection for survival and for growth in adaptive laboratory evolution experiments with benzalkonium chloride N2 - Biocides are used to control microorganisms across different applications, but emerging resistance may pose risks for those applications. Resistance to biocides has commonly been studied using adaptive laboratory evolution (ALE) experiments with growth at subinhibitory concentrations linked to serial subculturing. It has been shown recently that E. coli adapts to repeated lethal stress imposed by the biocide benzalkonium chloride (BAC) by increased survival (i.e. tolerance) and not by evolving the ability to grow at increased concentrations (i.e. resistance). Here, we investigate the contributions of evolution for tolerance as opposed to resistance for the outcome of ALE experiments with E. coli exposed to BAC. We find that BAC concentrations close to the half maximal effective concentration (EC50, 4.36 µg mL-1) show initial killing (~40%) before the population resumes growth. This indicates that cells face a two-fold selection pressure: for increased survival and for increased growth. To disentangle the effects of both selection pressures, we conducted two ALE experiments: (i) one with initial killing and continued stress close to the EC50 during growth and (ii) another with initial killing and no stress during growth. Phenotypic characterization of adapted populations showed that growth at higher BAC concentrations was only selected for when BAC was present during growth. Whole genome sequencing revealed distinct differences in mutated genes across treatments. Treatments selecting solely for survival led to mutations in genes for metabolic regulation (cyaA) and cellular structure (flagella fliJ), while treatments selecting for growth and survival led to mutations in genes related to stress response (hslO and tufA). Our results demonstrate that serial subculture ALE experiments with an antimicrobial at sub-inhibitory concentrations can select for increased growth and survival. This finding has implications for the design of ALE experiments to assess resistance risks of antimicrobials in different scenarios such as disinfection, preservation, and environmental pollution. KW - Antimicrobial resistance KW - Bacteria KW - Standardization KW - Biocides PY - 2024 UR - https://www.ncbi.nlm.nih.gov/bioproject/PRJNA1074740 PB - National Library of Biotechnology Information CY - Bethesda AN - OPUS4-61559 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schreiber, Frank A1 - Kanaris, Orestis A1 - Nordholt, Niclas T1 - Consequences of benzalkonium chloride tolerance for selection dynamics and de novode novo resistance evolution driven by antibiotics N2 - Biocides are used in large amounts in industrial, medical, and domestic settings. Benzalkonium chloride (BAC) is a commonly used biocide, for which previous research revealed that Escherichia coli can rapidly adapt to tolerate BAC-disinfection, with consequences for antibiotic susceptibility. However, the consequences of BAC- tolerance for selection dynamics and resistance evolution to antibiotics remain unknown. Here, we investigated the effect of BAC -tolerance in E. coli on its response upon challenge with different antibiotics. Competition assays showed that subinhibitory concentrations of ciprofloxacin—but not ampicillin, colistin and gentamicin—select for the BAC-tolerant strain over the BAC-sensitive ancestor at a minimal selective concentration of 0.0013–0.0022 µg∙mL−1. In contrast, the BAC-sensitive ancestor was more likely to evolve resistance to ciprofloxacin, colistin and gentamicin than the BAC-tolerant strain when adapted to higher concentrations of antibiotics in a serial transfer laboratory evolution experiment. The observed difference in the evolvability of resistance to ciprofloxacin was partly explained by an epistatic interaction between the mutations conferring BAC -tolerance and a knockout mutation in ompF encoding for the outer membrane porin F. Taken together, these findings suggest that BAC -tolerance can be stabilized in environments containing low concentrations of ciprofloxacin, while it also constrains evolutionary pathways towards antibiotic resistance. KW - Antimicrobial surfaces KW - Biocides KW - Antimicrobial resistance KW - Antibiotics PY - 2025 UR - https://www.ncbi.nlm.nih.gov/bioproject/?term=PRJNA1282584 PB - National Library of Medicine CY - Bethesda AN - OPUS4-65221 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Chaurasia, Prashant Kumar A1 - Fabry, Çağtay A1 - Pittner, Andreas A1 - Rethmeier, Michael T1 - Tandem-GMAW: advanced pulsed and short cicuiting process mode experimental data N2 - This dataset consists of raw recordings for 5 Tandem gas metal arc welding experiments (Tandem-GMAW / T-GMAW). KW - T-GMAW KW - High power welding KW - Deposition efficiency KW - Life Cycle Assessment PY - 2025 DO - https://doi.org/10.5281/zenodo.17951724 PB - Zenodo CY - Geneva AN - OPUS4-65206 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - European Food Safety Authority (EFSA), A1 - European Centre for Disease Prevention and Control (ECDC), A1 - European Chemicals Agency (ECHA), A1 - European Environment Agency (EEA), A1 - European Medicines Agency (EMA), A1 - European Commission's Joint Research Centre (JRC), T1 - Annex to: Scientific report 'Impact of the use of azole fungicides, other than as human medicines, on the development of azole-resistant Aspergillus spp.' doi:10.2903/j.efsa.2025.9200 - Annex E - Detailed answer to Term of Reference 5 'Environmental hotspots' and Term of Reference 6 'Prevention and control options' N2 - The widespread use of azole compounds in various sectors has led to the emergence of azole-resistant Aspergillus fumigatus (ARAf), which poses a significant challenge for treating fungal infections, especially in immunocompromised patients. Certain environmental conditions and practices, particularly in agricultural settings and the use of azoles as biocides, have been identified as hotspots for the selection and dispersal of azole-resistant strains of Aspergillus spp. Factors contributing to the selection of resistance include the use of azoles in crop protection, wood preservation and, to a much lesser extent, veterinary medicine. For plant protection products (PPPs), a number of scenarios (green waste of indoor-grown vegetables, uses with the production of wet pomace used as fertiliser, maize or sugar beet silage, and field heaps including flower bulbs) are deemed high risk for hotspot development. Based on EU authorised use patterns, these scenarios are characterised by the hazard characteristics of the azole fungicides in terms of activity against the wild-type Aspergillus spp. compared to resistant strains, substrate characteristics and residue levels, and environmental conditions that promote the growth of the fungus. For biocidal azole applications, products (biocidal product [BP]) for temporary preservation of freshly cut wood have been identified to have the potential for hotspot formation because freshly cut wood allows the growth of Aspergillus spp., and azole concentrations in treated wood are above the predicted no effect concentration (PNEC) for resistance selection (PNECres) and below the minimum inhibitory concentration (MIC) of ARAf for most analysed products on the EU market. Following identification of environmental hotspots, the report recommends measures to prevent the selection of azole-resistant strains in the environment, including controlled storage of organic waste, proper waste management, and responsible use and disposal of azole-treated products. Azole use in veterinary medicinal products (VMPs) represents a very small percentage of total azole use and is unlikely to be a significant source of selection of resistance in the environment. As such, the focus for mitigating resistance should be on other uses of azoles. The report stresses the importance of ongoing surveillance to monitor the presence of ARAf in the environment and to inform risk assessments and management strategies. As industrial chemicals, the azole substances are mostly used as intermediates (precursors) to manufacture yet a different substance, are formulated into a mixture or are reported to be manufactured as active substances in PPP, BP or VMP (therefore already covered above). There are only a few industrial azole substances with widespread use, and as for the moment, there is no evidence from the literature that industrial azoles would be a source of a possible hotspot; thus, the industrial chemicals were not further investigated. There are several areas where further research is needed, including understanding the environmental conditions that support the growth of Aspergillus spp. in different agricultural matrices or on wood, assessing human exposure to resistant strains, regional waste practices and the impact of active substance combinations for azole resistance selection. There is also a need for more comprehensive data on the use and quantities of azole-containing products. Furthermore, industrial substances with widespread use and having antifungal effects, e.g. an antidandruff substance in cosmetics, could be further investigated. Measures were identified that could be implemented with respect to the use of azole fungicides in PPPs as well as in BPs and with respect to the storage, processing and disposal of crop (waste) materials containing azole residues to prevent or minimise the selection of environmental resistance or to minimise the spread of resistant Aspergillus spp. to patients. Any measures that slow down or prevent growth in the presence of azoles, sporulation and dispersal of Aspergillus spp. should be encouraged. A coordinated effort among various stakeholders, including farmers, manufacturers, industrial users, waste managers, regulatory bodies and scientists, is essential to effectively address the challenge of azole resistance in A. fumigatus. KW - Antimicrobial surfaces KW - Biocides KW - Antimicrobial resistance KW - Azoles KW - Fungi KW - Wood preservatives PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-652187 UR - https://doi.org/10.5281/zenodo.14223436 DO - https://doi.org/10.5281/zenodo.14223435 SP - 1 EP - 76 PB - Zenodo CY - Geneva AN - OPUS4-65218 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Winkler, Juliette A1 - Beck, M. A1 - Gluth, Gregor ED - Schneider, F. ED - Hehl, K. ED - Heyde, S. T1 - Kurz- und mittelfristige Verbundfestigkeit von alkaliaktivierten Mörteln auf Beton N2 - Ein zentrales Fundament moderner Gesellschaften ist eine intakte Abwasserinfrastruktur. Schäden infolge biogener Schwefelsäurekorrosion von konventionellen Betonen haben jedoch zu einem erheblichen Sanierungsbedarf geführt. Alkaliaktivierte Mörtel besitzen aufgrund eines hohen Säurewiderstands das Potential, einen Beitrag zur langfristigen Lösung dieses Problems zu leisten. Dazu müssen jedoch zunächst die Faktoren, die den Haftverbund zwischen diesen Mörteln und dem Betonsubstrat bestimmen, besser verstanden werden, um die Eigenschaften der Beschichtungssysteme gezielt anpassen und verbessern zu können. Die vorliegende Arbeit liefert hierzu einen Beitrag und zeigt dadurch Wege zu einer technisch machbaren und nachhaltigen Sanierung von Abwasserbauwerken auf. KW - Alkalisch aktivierte Bindemittel KW - Abwassersysteme KW - Reparatursysteme KW - Verbund KW - Dauerhaftigkeit PY - 2022 SN - 978-3-8440-8818-2 SP - 89 EP - 100 CY - Berlin AN - OPUS4-57701 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine A1 - Gradt, Thomas T1 - MoS2-filled PEEK composite as a self-lubricating material for aerospace applications T2 - 40th Aerospace mechanisms symposium CY - Cocoa Beach, FL, USA DA - 2010-05-12 KW - PEEK composite KW - MoS2 KW - Friction KW - Ultra high vacuum KW - Aerospace PY - 2010 IS - NASA/CP-2010-216272 SP - 347 EP - 351 CY - Hanover, MD, USA AN - OPUS4-22047 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weimann, Karin A1 - Matyschik, Jan T1 - Sulfate in Bauschutt - Herkunft und Auswirkungen T2 - Fachtagung Recycling R´10 CY - Weimar, Deutschland DA - 2010-09-22 KW - Recycling KW - Bauschutt KW - RC-Baustoffe PY - 2010 SP - 1 EP - 2 AN - OPUS4-22840 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gluth, Gregor A1 - Lehmann, Christian A1 - Rübner, Katrin A1 - Kühne, Hans-Carsten T1 - Hydration and strength development of calcite-rich wastepaper sludge ash N2 - In paper recycling large amounts of waste sludge, containing organics as well as inorganic fillers of the recycled paper, are produced. A large fraction of these sludges is incinerated; the ashes generated in this process, often referred to as wastepaper sludge ash (WSA), have the potential to be used as binder material, either alone or as supplementary cementitious material. However, ashes from different paper mills differ in their Chemical and mineralogical composition, thus, the reaction products and the properties of the hardened binders may vary s i gn i fi cantley. In the present study, a calcite-rich WSA was analyzed for reaction products and strength development. The WSA contained, besides calcite, hydraulic phases such as tricalcium aluminate (C3A) and belite (C2S), lime as well as inert phases. When activated with water, the WSA yielded a compressive strength of up to 12.3 MPa and the major hydration product was monocarboaluminate (C4A CO2 IIH2O or C4ACH11). Activation with 2M NaOH or 2M KOH solution caused a more rapid strength gain until one day of curing, but afterwards the strength development slowed down and the strength afiter 28 days was significantly lower than for the water-activated pastes. From TG analyses it is apparent that the higher strength of the alkaliactivated pastes after one day of curing was caused by a more rapid consumption of calcite and associated formation of C4ACH11. At later curing times the amount of calcite did not change substantially and consequently strength development almost ceased. The results demonstrate the complex influence of alkaline conditions on the hydration of WSA and show that the reaction products, which determine the durability properties of the hardened pastes (and materials made from it), of the calcite-rich WSA differ from the products of other WS As, as discussed in the article. T2 - CIC 2014 - Concrete Innovation Conference 2014 CY - Oslo, Norway DA - 11.06.2014 KW - Wastepaper sludge ash (WSA) KW - Alkali-activation KW - Strength KW - Tetracalcium monocarboaluminate PY - 2014 SP - 1 EP - 8 AN - OPUS4-31038 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Niemeyer, B. A1 - Schwarzmaier, A. A1 - Radtke, Martin A1 - Hahn, Oliver T1 - Archaische Goldarbeiten aus Kleinasien in der Berliner Antikensammlung – Herstellungstechnik, Materialanalytik und der Fundkomplex »aus Ephesos« N2 - Ein Konvolut einzelner Schmuckstücke und die Goldbeigaben eines angeblichen Grabfundes wurden technologisch und analytisch untersucht. Die meisten Objekte sind Blecharbeiten, die aus einer Vielzahl von Einzelteilen mit metallischem Goldlot zusammengefügt und mit Granulation oder granulations-imitierendem Perl- oder Kerbdraht verziert wurden. Nur vier kleine Ohrringe sind massiv gegossen. Zwei Zierbleche dürften über Patrizen (Positivmodeln), die Deckel der Astragale in Matrizen (Negativmodeln) geformt worden sein. Alle Objekte wurden mit Synchrotron- und atmosphärischer Röntgenfluoreszenz analysiert. Die Daten zeigen das breite Spektrum an Goldlegierungen, die im 7./6. Jahrhundert v. Chr. in Kleinasien verarbeitet wurden: vom natürlichen Seifengold (Elektrum) bis zu geläutertem, fast reinem Gold. Eine Korrelation zwischen Goldqualität und Verarbeitungsmethode konnte nicht festgestellt werden. Sowohl hochreines als auch mit viel Silber und Kupfer legiertes Gold wurde zum Schmieden von Blecharbeiten, aber auch zum Massivguss verwendet. Aus der Goldfarbe kann wegen des Phänomens der oberflächlichen Goldanreicherung nicht auf eine Legierungszusammensetzung geschlossen werden. Der 1963 angekaufte Fundkomplex aus lydischen Metallarbeiten und ostionischen Salbgefäßen aus Ton dürfte einen Grabfund des frühen 6. Jahrhunderts v. Chr. darstellen, dessen Herkunft aus Ephesos jedoch nicht zu sichern ist. KW - Gold KW - Synchrotron KW - XRF PY - 2017 SN - 1866-7007 VL - 9 SP - 57 EP - 83 PB - RGZM. Archäologische Staatssammmlung München CY - München AN - OPUS4-42986 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine A1 - Brice, H. A1 - Gradt, Thomas T1 - Stick-slip behaviour of polymer films in LHe N2 - Superconducting magnets are susceptible to quenching, even with the smallest amounts of energy disturbances due to the extremely low thermal capacity of materials at 4.2 K. Hence, small mechanical disturbances resulting in frictional heating can be sufficient to exceed the wire’s critical temperature, causing it to quench. Unfortunately, relative motion between surfaces in the magnet System is inevitable due to various forces present in the System, including winding pretension, differences in material thermal contraction and the large electromagnetic forces. Typically insulating polymers are present at this interface to achieve the required electrical insulation requirements. T2 - WTC 2013 - 5th World tribology congress CY - Torino, Italy DA - 08.09.2013 PY - 2013 SP - Paper 366, 1 EP - 4 AN - OPUS4-30940 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hofmann, Michael A1 - Tiebe, Carlo T1 - VDI/VDE 3518 - Technische Richtlinie für Multigassensoren N2 - Der Beitrag präsentiert die erarbeiteten technischen Richtlinien zur Anwendung und Prüfung von Multigassensoren innerhalb der Richtlinienreihe VDI/VDE 3518 sowie in diesem Zusammenhang die Möglichkeiten der Sensorprüfung im akkreditierten Prüflabor des Fachbereichs 8.1 der BAM. Im Speziellen wird das in Kürze veröffentlichte Blatt 3 der Richtlinienreihe vorgestellt, das Bezug auf Multigassensoren für geruchsbezogene Messungen mit elektronischen Nasen nimmt. T2 - 5. Fachsymposium "Intelligente Sensorik/Analytik und sichere Sensornetze: Innovative Technologien und neue Anwendungsfelder" CY - Eggenstein -Leopoldshafen, Germany DA - 14.11.2018 KW - Multigassensoren KW - Richtlinie KW - Prüfung KW - Elektronische Nase PY - 2018 UR - http://hybridsensornet.org/symposien.html SP - 61 EP - 62 AN - OPUS4-46839 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine A1 - Gradt, Thomas T1 - Gleitverhalten von PEEK-Kompositwerkstoffen in Wasserstoffumgebung N2 - Die Reibeigenschaften von PEEK-Materialien gegen Stahlscheiben wurden in Luft, Vakuum und Wasserstoffumgebung untersucht. Die Ergebnisse zeigen, dass reines PEEK umgebungsabhängig ist und die Desorption von Gasen im Vakuum zu hohen Verschleißraten führt. Die niedrigsten Verschleißraten sowohl in Vakuum als auch in einer Wasserstoffumgebung erzielen TiO2-Partikel. Ferner treten chemische Prozesse in den Materialien und im Tribokontakt auf und interagieren miteinander. T2 - 57. Tribologie-Fachtagung CY - Göttingen, Germany DA - 26.09.2016 KW - PEEK KW - Reibung KW - Wasserstoffumgebung PY - 2016 SN - 978-3-9817451-1-5 SP - 60/1 EP - 60/10 AN - OPUS4-37839 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fedelich, Bernard A1 - Epishin, A. A1 - Link, T. A1 - Klingelhöffer, Hellmuth A1 - Künecke, Georgia A1 - Portella, Pedro Dolabella ED - Huron, E.S. ED - Reed, R.C. ED - Hardy, M.C. ED - Mills, M.J. ED - Montero, R.E. ED - Portella, Pedro Dolabella ED - Telesman, J. T1 - Rafting during high temperature deformation in a single crystal superalloy: experiments and modeling T2 - Superalloys 2012 - 12th International symposium on superalloys CY - Seven, Springs, PA, USA DA - 2012-09-09 KW - Creep KW - Single crystal KW - Rafting KW - Modeling KW - CMSX-4 KW - Low-cycle-fatigue PY - 2012 SP - 491 EP - 500 PB - Wiley AN - OPUS4-26842 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Anderson, Johan A1 - Chiva, Roman A1 - Dumont, Fabien A1 - Lalu, Octavian A1 - Hofmann-Böllinghaus, Anja T1 - Assessment of fire performance of facades in a round robin using the European approach N2 - In recent years, an experimental round robin of full-scale façade tests was conducted using the proposed new European approach for assessing the fire performance of façades. The initial results were used to develop a calibration scheme and to propose assessment criteria aligned with appropriate safety levels. During the project, a need emerged to evaluate the stability of the fire source and the Consistency of heat exposure. This paper addresses these concerns by comparing the mass loss rates across a series of tests and analysing averaged temperature readings at various locations on the façade. The findings indicate that the method demonstrates high stability in terms of mass loss rates and provides consistent and appropriate heat exposure. T2 - Interflam 2025, 16th International Fire Science and Engineering Conference CY - London, UK DA - 30.06.2025 KW - Facade systems KW - Testing PY - 2025 VL - 2025 SP - 562 EP - 572 PB - Interscience CY - London AN - OPUS4-63998 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eliezer, Dan A1 - Tal-Gutelmacher, E. A1 - Cross, Carl Edward A1 - Böllinghaus, Thomas ED - Gdoutos, E. T1 - Irreversible Hydrogen Trapping in Welded Beta-21S Titanium Alloy T2 - 16th European Conference of Fracture CY - Alexandroupoli, Greece DA - 2006-07-03 KW - Titanium alloys KW - Beta-21S KW - Hydrogen desorption KW - Thermal Desorption Spectroscopy (TDS) PY - 2006 VL - 16 IS - 803 SP - 1 EP - 8 CY - Alexandroupolis AN - OPUS4-14453 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schreiber, Frank T1 - Differential selection for survival and for growth in adaptive laboratory evolution experiments with benzalkonium chloride N2 - Biocides are used to control microorganisms across different applications, but emerging resistance may pose risks for those applications. Resistance to biocides has commonly been studied using adaptive laboratory evolution (ALE) experiments with growth at subinhibitory concentrations linked to serial subculturing. It has been shown recently that E. coli adapts to repeated lethal stress imposed by the biocide benzalkonium chloride (BAC) by increased survival (i.e. tolerance) and not by evolving the ability to grow at increased concentrations (i.e. resistance). Here, we investigate the contributions of evolution for tolerance as opposed to resistance for the outcome of ALE experiments with E. coli exposed to BAC. We find that BAC concentrations close to the half maximal effective concentration (EC50, 4.36 µg mL-1) show initial killing (~40%) before the population resumes growth. This indicates that cells face a two-fold selection pressure: for increased survival and for increased growth. To disentangle the effects of both selection pressures, we conducted two ALE experiments: (i) one with initial killing and continued stress close to the EC50 during growth and (ii) another with initial killing and no stress during growth. Phenotypic characterization of adapted populations showed that growth at higher BAC concentrations was only selected for when BAC was present during growth. Whole genome sequencing revealed distinct differences in mutated genes across treatments. Treatments selecting solely for survival led to mutations in genes for metabolic regulation (cyaA) and cellular structure (flagella fliJ), while treatments selecting for growth and survival led to mutations in genes related to stress response (hslO and tufA). Our results demonstrate that serial subculture ALE experiments with an antimicrobial at sub-inhibitory concentrations can select for increased growth and survival. This finding has implications for the design of ALE experiments to assess resistance risks of antimicrobials in different scenarios such as disinfection, preservation, and environmental pollution. KW - Antimicrobial resistance KW - Bacteria KW - Standardization KW - Biocides PY - 2024 DO - https://doi.org/10.5061/dryad.2jm63xszx PB - Dryad AN - OPUS4-61558 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Block, S. A1 - Boß, K.-H. A1 - Frobese, D.-H. A1 - Pape, H. A1 - Gösslinghoff, L. A1 - Grossepieper, T. A1 - Kasper, R. A1 - Kirchner, W. A1 - Kollmann, P. A1 - Kröger, P. A1 - Ringlstetter, P. A1 - Kuska, T. A1 - Mattejat, K. A1 - Niehüser, H. A1 - Pfeiffer, F. A1 - Pötzsch, Klaus-Michael A1 - Jochems, Frank A1 - Schäfer, H. A1 - Vogt, W. A1 - Zankl, C. A1 - Ludzay, J. T1 - Empfehlungen zur Vermeidung von Überdrücken an Tankfahrzeugen bei Untenbefüllung N2 - Das Risiko von Überdrücken bei der Untenbefüllung von Tankfahrzeugen hat zu Vorfällen mit zum Teil erheblichen Sach- und Personenschäden geführt und ist ein nicht auszuschließendes Gefährdungspotential für Menschen, Umwelt, Anlagen und Transportmittel. Zur weiteren Verbesserung des Managements dieses Risikos und seiner potentiellen Auswirkungen hat der MWV die DGMK gebeten, das Thema in einem Projekt zu bearbeiten, um mögliche Sicherungsdefizite aufzudecken und Lösungsmöglichkeiten aufzuzeigen. Als Forschungsstelle wurde die Physikalisch-Technische Bundesanstalt (PTB) ausgewählt, die das DGMK-Projekt 727 „Überdrucksicherung an Tankfahrzeugen“ gemeinsam mit Vertretern von Tankfahrzeug- und Armaturenherstellern, Mineralölindustrie sowie der Bundesanstalt für Materialforschung und -prüfung (BAM) bearbeitet hat. In Messungen an zwei Füllstellen wurden reale Druck-, Temperatur- und Volumenstromverhältnisse für die Beladung eines Tankfahrzeugs aufgenommen. Es wurde festgestellt, dass es in einem Tankfahrzeug, in dem keine zusätzlichen Druckverluste wie z. B. durch Vereisungen im Inneren der Kippventil-Flammendurchschlagsicherungs-Armatur auftreten, zu keinem unzulässig hohen Druckaufbau in einer Tankwagenkammer kommen kann. Zusätzlich erfolgten Versuche in einer Kältekammer, um die Möglichkeit und die Randbedingungen einer Vereisung des Kippventils und der Flammendurchschlagsicherung zu ermitteln. Mit diesen Ergebnissen sind Szenarien erarbeitet worden, die bekannte Überdruckschadensereignisse erklären können. Aus einer Gefährdungsbeurteilung heraus wurden Maßnahmen beschrieben, wie zukünftig solche Überdruckschäden an Tankfahrzeugen vermieden werden können. Aufbauend auf den Ergebnissen des Projektes hat die Projektbegleitung diese und weitere Maßnahmen hinsichtlich ihrer Umsetzbarkeit diskutiert und die vorliegende Empfehlung zur Vermeidung von Überdrücken an Tankfahrzeugen bei Untenbefüllung erarbeitet. KW - Untenbefüllung KW - Tankfahrzeuge KW - Überdruck KW - Mineralöl KW - Sicherheitsventile PY - 2012 VL - 727 IS - 3 SP - 1-4 EP - Anl. 1-3 AN - OPUS4-27921 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rahman, Mehbub-Ur A1 - Prager, Jens T1 - Simulation of lamb wave propagation with elastodynamic finite integration technique (EFIT) N2 - This paper presents the numerical modeling of the Lamb wave propagation in plate like structures with the Elastodynamic Finite Integration Technique (EFIT) and ist validation with the measured results. In general, Lamb waves offer an attractive method to detect the defects inside long plate like structures efficiently. However, such a nondestructive testing (NDT) requires profound understanding of the Lamb wave propagation in the plates, generation of the symmetric and anti-symmetric modes of different orders and their interaction with the defects of the materials. Modern simulation tools based on numerical methods can be used to model this complex NDT situation. EFIT is an effective tool to model such problems in an efficient way. With the help of the simulation results obtained from the EFIT tool the propagation of different symmetric and antisymmetric Lamb wave modes is analyzed and thus a proper technique is developed to excite different modes and to separate them from each other precisely. A validation of the numerical results with the measured results is also presented. T2 - DAGA 2012 - 38. Jahrestagung für Akustik - Fortschritte der Akustik CY - Darmstadt, Germany DA - 19.03.2012 PY - 2012 SP - 953 EP - 954 PB - Deutsche Gesellschaft für Akustik e.V. AN - OPUS4-25999 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Vöse, Markus A1 - Fedelich, Bernard T1 - Simulation of creep damage in a Cu polycrystal under multiaxial loading N2 - The stress States of components under Service conditions differ in general from the loading conditions that are routinely applied during material testing. When data that results, e.g., from uniaxial testing should be used for lifetime assessment, a good understanding of the failure behaviour in dependence of the stress state is necessary. For polycrystalline materials under high temperature loading, the development of creep damage is one important factor that limits a component’s lifetime. For cases where creep damage is related to the nucleation and growth of grain boundary cavities, the local normal stress acting on a grain boundary has been found to have a strong influence on the damage development. Hence, creep damage is usually localized along planes that lie perpendicular to the maximum principal tensile stress. T2 - CREEP 2015 - 13th International conference on creep and fracture of engineering materials and structures CY - Toulouse, France DA - 31.05.2015 PY - 2015 SP - 175 EP - 176 AN - OPUS4-33455 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Wolf, Marcus A1 - Gröber, Andre A1 - Böllinghaus, Thomas A1 - Kranzmann, Axel T1 - Corrosion fatigue of 1.4542 exposed to a laboratory saline aquifer water CCS-environment N2 - X5CrNiCuNb16-4 has been proven to be sufficient resistant in corrosive environments, but shows rather unusual corrosion behaviour in CCS environment. Therefore a series of 30 specimens was tested at stress amplitudes between 150 MPa and 500 MPa (sinusoidal dynamic test loads, R=-1; resonant frequency ∼ 30 Hz). Due to the rather heterogeneous fine machined surfaces (Rz=4) the specimens are comparable with prefabricated parts. X5CrNiCuNb16-4 reached the maximum number of cycles (10 x 106) at a stress amplitude of 150 MPa and lies 60% below the stress amplitude measured in air. The scatter range TN = 1:34 is disproportionately large. Although the fracture surface exhibited the typical striations and corroded surface areas no significant differences were found. The hardness was found to be homogeneous in all specimens tested at 335 HV10. Non-metallic inclusions were found within the microstructure, but no correlation could be found between the inclusions and early rupture. Still specimens that showed inclusions at the fracture surface and its cross section endured lower number of cycles. Additionally Aluminium was analysed in specimens with low number of cycles and may be cause for early rupture during corrosion fatigue tests. These findings reveal a very high sensitivity on a homogeneous microstructure upon the corrosion and corrosion fatigue behaviour of X5CrNiCuNb16-4 and needs to be taken into account when regarding this steel as pipe steel during injection of CO2 into saline aquifers. T2 - 13th International Conference on Greenhouse Gas Control Technologies CY - Lausanne, Switzerland DA - 14.11.2016 KW - Steel KW - Corrosion fatigue KW - Electrochemistry KW - Reliability KW - CCS KW - CO2-storage PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-418525 DO - https://doi.org/10.1016/j.egypro.2017.03.1678 SN - 1876-6102 VL - 114 SP - 5219 EP - 5228 AN - OPUS4-41852 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Epishin, A.I. A1 - Link, T. A1 - Fedelich, Bernard A1 - Svetlov, I.L. A1 - Golubovskiy, E.R. T1 - Hot isostatic pressing of single-crystal nickel-base superalloys: mechanism of pore closure and effect on mechanical properties N2 - Pore annihilation was investigated in the single-crystal nickel-base superalloy CMSX-4. HIP tests at 1288 °C/103 MPa were interrupted at different times, then the specimens were investigated by TEM, metallography and density measurements. The kinetics of pore annihilation was determined. The pore closure mechanism was identified as plastic deformation on the octahedral slip systems. A model describing the kinetics of pore closure has been developed on the base of crystal plasticity and large strain theory. Mechanical tests with the superalloy CMSX-4 and the Ru-containing superalloy VGM4 showed, that HIP significantly increases the fatigue life at low temperatures but has no effect on creep strength. T2 - Eurosuperalloys 2014 - 2nd European symposium on superalloys and their applications CY - Giens, France DA - 12.05.2014 PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-316410 DO - https://doi.org/10.1051/matecconf/20141408003 N1 - Serientitel: MATEC Web of conferences – Series title: MATEC Web of conferences VL - 14 SP - 08003-1 EP - 08003-6 PB - EDP Sciences AN - OPUS4-31641 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Strangfeld, Christoph A1 - Schönsee, Eric A1 - Jeyifous, Olubunmi Anthony A1 - Mezhov, Alexander A1 - Hüsken, Götz T1 - Introduction of a monitoring system for Bingham fluids in additive manufacturing with concrete N2 - Freeform additive manufacturing of concrete structures is a rising technology in civil engineering with several fascinating advantages. Nonetheless, to ensure reliability and structural integrity, standards and quality control are required in the future to bring this technology into the market. As the concrete is manufactured continuously, continuous quality control of the printing process is also required, i.e. comprehensive process monitoring. At BAM, a test rig will be installed, enabling the printing of concrete structures with a maximum size of 2 m x 1 m x 1 m (l x w x h). Here, process monitoring is the focus of the test rig. In this study, we show the results of the first pump tests, including the measurement of several parameters such as temperature and pressure along the supply system, i.e. from the concrete pump to the printer head. T2 - NDT-CE 2022 CY - Zurich, Switzerland DA - 16.08.2022 KW - Additive manufacturing of concrete KW - Process monitoring KW - Non-destructive testing KW - Bingham fluid PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-556367 SP - 1 EP - 12 AN - OPUS4-55636 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Jafari, Abbas T1 - A python library for finite element (FE) modelling of static/quasi-static structural mechanics problems with legacy FEniCS N2 - This is a python library for finite element (FE) modelling of static/quasi-static structural mechanics problems with legacy FEniCS, which contains the following main modules. Module structure: for defining a structural mechanics experiment, including geometry, mesh, boundary conditions (BCs), and time-varying loadings. The time is quasi-static, i.e. no dynamic (inertia) effects will be accounted for in the problem module as follows. Module material: for handling constitutive laws such as elasticity, gradient damage, plasticity, etc. Module problem: for establishing structural mechanics problems for desired structures and material laws coming from the two above modules, and solving the problems built up. These can be performed for two main cases: static (no time-evolution) that also includes homogenization, and quasi-static (QS). KW - Finite element (FE) KW - Static/quasi-static structural mechanics KW - FEniCS PY - 2025 DO - https://doi.org/10.5281/zenodo.17805724 PB - Zenodo CY - Geneva AN - OPUS4-65269 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Jafari, Abbas A1 - Titscher, Thomas A1 - Robens-Radermacher, Annika T1 - Bayem: Implementation and derivation of “variational Bayesian inference for a nonlinear forward model [Chappell et al 2008]“ for arbitrary, user-defined model errors N2 - A python implementation of an analytical variational Bayes algorithm of "Variational Bayesian inference for a nonlinear forward model", Chappell, Michael A., Adrian R. Groves, Brandon Whitcher, and Mark W. Woolrich, IEEE Transactions on Signal Processing 57, no. 1 (2008): 223-236, with an updated free energy equation to correctly capture the log evidence. The algorithm requires a user-defined model error allowing an arbitrary combination of custom forward models and measured data. KW - Implementation KW - Variational Bayesian inference KW - Nonlinear forward model PY - 2025 DO - https://doi.org/10.5281/zenodo.17804665 PB - Zenodo CY - Geneva AN - OPUS4-65268 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, M. A1 - Baer, Wolfram A1 - Mayer, U. A1 - Weihe, S. T1 - Untersuchung des Master Curve-Konzepts für ferritisches Gusseisen mit Kugelgraphit N2 - Das Master Curve (MC) Konzept nach ASTM E1921 wird momentan u.a. in der Kerntechnik für die bruchmechanische Sicherheitsbewertung ferritischer Stähle eingesetzt. Für ferritisches Gusseisen mit Kugelgraphit (GJS) fehlt jedoch eine Validierung dieser Methode und ggf. eine systematische Überprüfung möglicher Modifikationen grundlegender Ansätze des MC-Konzepts. Aus diesem Grund soll in einem kürzlich gestarteten BMUV-Verbundprojekt zwischen der MPA Stuttgart und der BAM Berlin die Anwendbarkeit des MC-Konzepts auf GJS bei dynamischer Beanspruchung untersucht werden. Ziel ist es, eine effektive und effiziente Methodik bereitzustellen, mit der mittels einer vergleichsweise kleinen Stichprobe bruchmechanischer Kleinproben eine Referenztemperatur T0 zur werkstoffspezifischen Temperaturjustierung der MC ermittelt werden kann. T2 - 55. Jahrestagung des DVM-Arbeitskreises "Bruchmechanik und Bauteilsicherheit" CY - Darmstadt, Germany DA - 14.02.2023 KW - Dynamische Beanspruchung KW - Bruchmechanik KW - Master Curve-Konzept KW - Gusseisen mit Kugelgraphit PY - 2023 DO - https://doi.org/10.48447/Br-2023-BB SP - 101 EP - 108 PB - DVM Berlin CY - Berlin AN - OPUS4-57024 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram A1 - Holzwarth, Marcel A1 - Mayer, Uwe ED - Vormwald, Michael T1 - Untersuchung des Master Curve-Konzepts für ferritisches Gusseisen mit Kugelgraphit: Versuchswerkstoff und erste Ergebnisse an SE(B)140-Großproben N2 - In einem laufenden Kooperationsprojekt zwischen der BAM Berlin und der MPA Stuttgart wird das probabilistische Master Curve (MC) Konzept nach ASTM E1921 hinsichtlich seiner Übertragbarkeit auf ferritisches Gusseisen mit Kugelgraphit (DCI) untersucht. Zielsetzung ist die Bereitstellung einer Vorgehensweise zur Bestimmung und Bewertung der dynamischen Bruchzähigkeit von DCI im Übergangsbereich. In diesem Beitrag wird der Versuchswerkstoff der Festigkeitsklasse GJS-400 näher vorgestellt. Ferner werden erste Ergebnisse von zwei bruchmechanischen Versuchsserien an SE(B)140-Großproben bei Belastungsraten von ca. 6∙104 MPa√ms-1 bei -40 °C und -60 °C präsentiert. T2 - 56. Tagung des DVM-Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Kassel, Germany DA - 20.02.2024 KW - Dynamische Beanspruchung KW - Bruchmechanik KW - Master Curve-Konzept KW - Gusseisen mit Kugelgraphit PY - 2024 DO - https://doi.org/10.48447/BR-2024-BB SP - 49 EP - 58 PB - DVM-Verlag CY - Berlin AN - OPUS4-59518 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, Marcel A1 - Baer, Wolfram A1 - Mayer, Uwe A1 - Weihe, Stefan ED - Vormwald, Michael T1 - Untersuchung des Master Curve-Konzepts für ferritisches Gusseisen mit Kugelgraphit: Kritische Belastungsrate und erste Ergebnisse an C(T)-Proben N2 - Im laufenden Verbundprojekt MCGUSS untersuchen dieProjektpartner MPA Stuttgart und BAM Berlin das probabilistische Master Curve (MC) Konzept nach ASTM E1921 hinsichtlich seiner Übertragbarkeit auf ferritisches Gusseisen mit Kugelgraphit (DCI). Ziel des Projektes ist die Entwicklung einer Methode zur Bestimmung und Bewertung der dynamischen Bruchzähigkeit von DCI im Übergangsbereich. In diesem Beitrag werden die Eigenschaften des verwendeten Werkstoffs der Festigkeitsklasse GJS-400 vorgestellt und die sich daraus ergebenden Probenentnahmestellen näher erläutert. Weiterhin werden erste Ergebnisse der C(T)25-Versuchsserien vorgestellt, die bei Belastungsraten von ca. 5∙103 MPa√ms-1, 5∙104 MPa√ms-1 und 5∙105 MPa√ms-1 und einer Temperatur von -40 °C durchgeführt wurden. T2 - 56. Tagung des DVM-Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Kassel, Germany DA - 20.02.2024 KW - Dynamische Belastung KW - Master Curve KW - Gusseisen KW - C(T)-Proben PY - 2024 SP - 37 EP - 47 PB - DVM Verlag CY - Berlin AN - OPUS4-59519 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram A1 - Müller, Karsten A1 - Wossidlo, Peter T1 - Investigations on the Dynamic Fracture Toughness of Heavy-Section Ductile Cast Iron for Transport and Storage Casks T2 - PATRAM 2001 ; Annual International Symposium on Packaging and Transportation of Radioactive Materials CY - Chicago, IL, USA DA - 2001-09-03 PY - 2001 IS - CD-ROM PB - PATRAM CY - Chicago, Ill. AN - OPUS4-1930 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram A1 - Häcker, Ralf A1 - Börnert, Johannes T1 - Dynamic mechanical properties of ductile cast iron materials for thickwalled components T2 - 15th European Conference of Fracture (ECF15) - Advanced Fracture Mechanics for Life and Safety Assessments CY - Stockholm, Schweden DA - 2004-08-11 PY - 2004 SP - 8 pages CY - Stockholm AN - OPUS4-7026 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram T1 - Statistical analysis of dynamic fracture toughness data of two DCI large scale specimen test series T2 - PATRAM 2007, 15th International Symposium on the Packaging and Transportation of Radioactive Materials CY - Miami, Florida, USA DA - 2007-10-21 KW - Dynamische Bruchzähigkeit KW - Duktiles Gusseisen KW - Statistik KW - Großproben KW - Werkstoffkennwert PY - 2007 SP - 1 EP - 7 PB - Institute of Nuclear Materials Management AN - OPUS4-19066 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram A1 - Wossidlo, Peter ED - Zimmermann, M. T1 - Zur Frage der Verwendung von Untermaßprobenergebnissen des Kerbschlagbiegeversuchs - Eine ernüchternde Bilanz N2 - Der Kerbschlagbiegeversuch ist seit der ersten Hälfte des letzten Jahrhunderts standardisiert und seit langem als Prüfverfahren international genormt. Weltweit sind zu garantierende Werte der Kerbschlagenergie (KV) und Übergangstemperaturen (TÜ) in Produktnormen und Regelwerken festgelegt. Unter bestimmten Bedingungen besteht dabei die Option, statt Normalproben Untermaßproben zu prüfen. Im Rahmen einer Untersuchung der BAM wurde der aktuelle Status von Prüf- und Produktnormen sowie Regelwerken zur Bewertung der Bauteilintegrität hinsichtlich ihres Umgangs mit Untermaßprobenergebnissen erfasst. Zur Schaffung einer geeigneten aktuellen Datenbasis wurden an ISO-V-Proben der Dicken 2,5, 5,0, 7,5 und 10,0 mm aus vier aktuellen Baustählen KV2-T-Kurven ermittelt. Es wurden unterschiedliche Vorgehensweisen zur Kurvenanpassung und Festlegung von Übergangstemperaturen praktiziert. Ferner kamen verfügbare Ansätze zur Skalierung von Untermaßprobenergebnissen auf die Werte von Normalproben zur Anwendung. Das Ausmaß des Probendickeneffektes ist werkstoff- und temperaturabhängig. Im Bereich der Werkstoffprüfung ist akzeptiert, dass die Ergebnisse von Normal- und Untermaß-proben nicht ohne Weiteres ineinander überführt werden können. Der Stand der Produktnormung und der Regelwerke ist jedoch im besten Falle als unzureichend, vielfach jedoch schlicht als falsch zu bezeichnen. In einem weiten anwendungsrelevanten Temperaturbereich werden hier sogar deutlich nicht-konservative Skalierungsergebnisse geliefert. Die betroffenen Produkt-normenreihen und Regelwerke müssen überarbeitet werden. T2 - 40. Vortrags- und Diskussionstagung Werkstoffprüfung 2022: Werkstoffe und Bauteile auf dem Prüfstand, Prüftechnik – Kennwertermittlung – Schadensvermeidung CY - Dresden, Germany DA - 27.10.2022 KW - Kerbschlagbiegeversuch, Untermaßproben, Normalproben, Skalierung von Ergebnissen PY - 2022 SP - 1 EP - 6 PB - Deutsche Gesellschaft für Materialkunde (DGM) CY - Sankt Augustin AN - OPUS4-56155 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Leinitz, Sarah A1 - Schmidt, Wolfram A1 - Mota, Berta A1 - Crasselt, Claudia ED - Ludwig, H.-M. T1 - Einfluss der wässrigen Phase von Zementleim und Polycarboxylatethern auf die Rheologie und die frühe Hydratation von Zement N2 - Die Rheologie von fließfähigen zementären Systemen mit Fließmitteln wird durch eine Vielzahl parallel stattfindender Effekte beeinflusst. Zu diesen Effekten zählen Wechselwirkungen zwischen den Polymeren und Ionen in der Porenlösung, frühe Phasenbildung, zeitabhängige und kompetitive Adsorption zwischen anionischen Polymeren und Sulfationen, Bildung von Phasen in der Porenlösung sowie Morphologieänderungen an Partikeloberflächen. Die frühe Hydratation von Zement, die durch Lösungs- und Fällungsprozesse angetrieben wird, beeinflusst diese Effekte erheblich. Das permanente Ungleichgewicht der Porenlösung führt zu Veränderungen der Partikeloberflächen, welches widerum zur Folge hat, dass rheometrische Messungen dieser Zementleime anfällig für Streuungen sind. Um die Einflüsse aus der Zementhydratation zu minimieren, wurden die rheometrischen Untersuchungen mit Zement in Porenlösung durchgeführt. Die Experimente wurden mit verschiedenen Feststoffvolumenfraktionen durchgeführt und mit den Ergebnissen identischer Systeme mit Wasser anstelle von Porenlösung verglichen. Zusätzlich wurden die gleichen Systeme mit Zugabe von Polycarboxylatethern untersucht. Die Ergebnisse zeigen, dass die Leime mit Wasser niedrigere Werte für Fließgrenze und plastische Viskosität aufweisen, als die Systeme mit Porenlösung. Während die Polymere eine Verminderung der Fließgrenze zur Folge hatte, war die Wirkung von Polymeren auf die plastische Viskosität vernachlässigbar. Zusätzlich wurde die frühe Hydratation unter Verwendung von Wärmeflusskalorimetrie, Rasterelektronenmikroskopie und Nadeleindringtiefe beobachtet. T2 - 20. Internationale Baustofftagung CY - Weimar, Germany DA - 12.09.2018 KW - Rheologie KW - Polycarboxylatether KW - Zementleim KW - Fließmittel PY - 2018 SN - 978-3-00-059950-7 VL - 20 SP - 744 EP - 751 PB - F.A. Finger-Institut für Baustoffkunde CY - Weimar AN - OPUS4-45973 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram A1 - Holzwarth, M. A1 - Mayer, U. T1 - Investigation of the Master Curve Concept for ferritic Ductile Cast Iron N2 - Based on state-of-the-art research and regulations, the application of the fracture mechanics master curve (MC) concept to ferritic ductile cast iron (DCI) is being investigated in a recently started German joint research project between BAM Berlin and MPA Stuttgart. This paper outlines the research approach and the planned investigations and provides first results. According to the IAEA guidelines SSG 26, the safety assessment of DCI containers for transport as well as interim and final storage of radioactive materials is based on the fracture mechanics criterion of general crack initiation exclusion. Within this context, the focus of the current research project is on the further development of brittle fracture safety assessment methods under dynamic loading conditions. Within fracture mechanics safety assessments for steels in nuclear technology, the probabilistic MC concept according to ASTM E1921 is currently used for quasi-static loading conditions as a supplement to the established deterministic ASME reference curve concept. The MC concept allows for an effective statistical consideration of the scatter of the material toughness in the transition regime. Furthermore, the MC can also be used for elevated loading rates as they occur in accident or crash scenarios. However, for DCI, a systematic review of potential modifications to the MC assumptions and procedure according to ASTM E1921 and an associated validation are still lacking. Therefore, a corresponding methodology shall be established to determine and assess dynamic fracture toughness values of DCI in the ductile-to-brittle transition regime, using samples extracted from a component. For the experimental program, a DCI material was produced as it is generally used for transport and storage containers. A basic mechanical-technological material characterization consisting of tensile, Charpy, and Pellini tests is planned. A comprehensive fracture mechanics test program was compiled covering dynamic testing of DC(T)9, C(T)25, C(T)50, SE(B)10, SE(B)25, and SE(B)140 specimens. Moreover, numerical analyses of different specimen geometries and test setups are planned to investigate the influences of stress triaxiality and loading rate. Throughout the experimental program, the microstructure-property relationship will be investigated based on quantitative metallographic and fractographic analyses. Finally, different MC assessment strategies will be considered, and modifications will be made if necessary. T2 - PATRAM22 Conference CY - Juans-les-Pins, France DA - 11.06.2023 KW - Master Curve KW - Ductile cast iron KW - Dynamic fracture toughness PY - 2023 SP - 1 EP - 9 PB - World Nuclear Transport Institute AN - OPUS4-57765 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram A1 - Ohm, Katrin A1 - Holzwarth, Marcel A1 - Mayer, Uwe T1 - Master Curve-Auswertungen und fraktographische Analysen zum Bruchmechanismus – neue Ergebnisse zur Untersuchung des Master Curve Konzepts für ferritisches Gusseisen mit Kugelgraphit bei dynamischer Beanspruchung (Projekt MCGUSS) N2 - In diesem Beitrag werden erste Master Curve (MC)-Auswertungen und fraktographische Analysen zum Bruchmechanismus aus dem laufenden Kooperationsprojekt MCGUSS zwischen der BAM Berlin und der MPA Stuttgart diskutiert. Für zwei SE(B)140-Großprobenversuchsserien mit je 6-8 Versuchen bei -40 °C bzw. -60 °C und Belastungsraten von 5-8x10^4 MPa√m/s wurden Referenztemperaturen T0 bestimmt. Ergänzt wird dies für erste Versuchsreihen an SE(B)25-Kleinproben, die bei -60 °C und Belastungsraten von ca. 2x10^5 MPa√m/s geprüft wurden. An ausgewählten Bruchflächen dieser Versuche wurden detaillierte fraktographische REM-Analysen vorgenommen. Im Vordergrund stand die Charakterisierung des Bruchmechanismus in Abhängigkeit von den Einflussfaktoren Temperatur und Probengröße. In Richtung der Zähigkeitstieflage werden die Analysen komplettiert durch die Ergebnisse von zwei SE(B)140-Großprobenversuchen bei -100 °C bzw. -140 °C und Belastungsraten von ca. 5-8x10^4 MPa√m/s. T2 - 57. Tagung des DVM-Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Köln, Germany DA - 18.02.2025 KW - Dynamische Beanspruchung KW - Bruchmechanik KW - Master Curve-Konzept KW - Gusseisen mit Kugelgraphit PY - 2025 DO - https://doi.org/10.48447/BR-2025-467 SP - 113 EP - 122 PB - DVM-Verlag CY - Berlin AN - OPUS4-62554 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, Marcel A1 - Mayer, Uwe A1 - Baer, Wolfram A1 - Weihe, Stefan T1 - Investigation of the Master Curve Concept for Ferritic Ductile Cast Iron N2 - Within fracture mechanics safety assessment for steels in nuclear technology, the probabilistic master curve (MC) concept according to ASTM E1921 is currently used for quasi-static loading conditions as a supplement to the established deterministic ASME reference curve concept. However, for ductile cast iron (DCI), a systematic review of potential modifications to the assumptions and the procedure according to ASTM E1921 and an associated validation are still lacking. For this reason, the application of the fracture mechanics MC concept to ferritic ductile cast iron is being investigated in a joint research project between MPA Stuttgart and BAM Berlin. According to Hojo et al. (2008) the MC concept is already in use for the brittle fracture safety assessment of ferritic forged steel containers, which would suggest an extension to ductile cast iron containers. In compliance with IAEA SSG-26, the safety assessment of DCI containers for transport as well as storage of radioactive materials is based on the fracture mechanics criterion of general exclusion of crack initiation. Within this context, the focus of the current research project is on the further development of brittle fracture safety assessment methods. Therefore, a methodology shall be established to determine and assess dynamic fracture toughness values of DCI in the ductile-to-brittle transition regime, using only a low number of small fracture mechanics test specimens extracted from a component. For the experimental program, a DCI material of grade GJS-400 (GGG-40) has been produced as it is generally used for transport and storage containers for nuclear material. A basic mechanical-technological material characterization consisting of tensile, Charpy, and Pellini tests has been planned and a comprehensive fracture mechanics test program was compiled covering dynamic testing of DC(T)9, C(T)25, C(T)50, SE(B)10, SE(B)25, and SE(B)140 specimens at various loading rates and temperatures. The specimen testing is divided between the project partners based on specimen geometry. MPA Stuttgart has been tasked with the testing of the C(T), DC(T) and Pellini specimens, while BAM Berlin was assigned the SE(B), Charpy and tensile tests. These tests allow for the determination of the loading rate relevant for brittle fracture via C(T)25 specimens and an assessment of size effects by transferring the relevant loading rate to other specimen geometries and sizes. Numerical analyses of different specimen geometries and test setups are planned to investigate the influence of stress triaxiality and loading rate. Furthermore, the time-dependent course of the Weibull stress is assessed via these numerical analyses. Throughout the experimental program, the microstructure-property relationship will also be investigated based on quantitative metallographic and fractographic analyses like scanning electron microscope images and metallographic sections. With the acquired experimental database fundamental assumptions of the MC concept, like the weakest link model and the Weibull distribution, will be assessed for the application to DCI. In the end, the applicability of the MC concept will be evaluated and if necessary, modifications to the MC concept for DCI will be proposed. This paper will present the preliminary results of the GJS400 material characterization and the related selection of test specimen extraction points. First results of the C(T)25 and SE(B)140 specimen testing will also be discussed supported by first metallographic analyses. T2 - SMiRT27 Conference CY - Yokohama, Japan DA - 03.03.2024 KW - Ductile Cast iron KW - Dynamic Fracture Toughness KW - Safety Assessment KW - Master Curve Concept PY - 2024 SP - 1 EP - 10 AN - OPUS4-59302 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, Marcel A1 - Baer, Wolfram A1 - Mayer, Uwe A1 - Weihe, Stefan T1 - On the Applicability of the Master Curve Concept for Ductile Cast Iron based on experimental and microstructural results N2 - Based on the state-of-the-art research and regulations, the application of the fracture mechanics master curve (MC) concept to ferritic ductile cast iron (DCI) is being investigated in a joint research project (MCGUSS) between BAM Berlin and MPA Stuttgart. The experimental program included a basic mechanical-technological material characterization consisting of tensile, Charpy and Pellini tests. To determine the relevant loading rate for brittle fracture, instrumented C(T)25 fracture tests were performed at different loading rates at a temperature of -40°C. The relevant loading rates are 5x10^3 MPa√ms-1 and 5x10^4 MPa√ms-1. A series of dynamic fracture tests consisting of DC(T)9, C(T)25 and C(T)50 specimens were performed at MPA. BAM performed corresponding test series with SE(B)10 (pre-cracked Charpy), SE(B)25 and SE(B)140 specimens to cover the influence of specimen geometry. In total about 400 tests were performed during this project. The experimental program is complemented by extensive fractographic and metallographic studies using scanning electron microscopy and cross sectioning, as well as characterizations of the chemical composition of the material and of the morphology and distribution of the graphite particles. KJcd values were evaluated for all C(T)25 specimens and some C(T)50 and DC(T)9 specimens. First Master Curve analyses suggest that modifications on the Master Curve setup will be neccessary for instance changing the coefficient from 0.019 to 0.045. This modification requires further validation and is only one of many possible modifications. The SE(B) specimen results clearly show an inverse size effect. This does not correlate with the weakest link effect attributed to steels which dictates lower fracture toughness values for larger specimens. Due to the presence of graphite particles in the DCI material, it is currently assumed that these particles play a significant role in the failure behavior of DCI materials and the following fracture mechanism is proposed: “Specimen size-dependent arrest of local brittle fracures before global brittle failure by weakest link”. T2 - 9th SEDS Workshop: Safety of Extended Dry Storage, 20.-22. Mai 2025 CY - Garching, Germany DA - 20.05.2025 KW - Statistics KW - Dynamic fracture toughness KW - Ductile cast iron KW - Master curve KW - Safety assessment PY - 2025 SP - 1 EP - 3 AN - OPUS4-63566 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram A1 - Klingbeil, Dietmar T1 - Entwicklung einer Key Curve-Methode für Gusseisen mit Kugelgraphit bei dynamischer Beanspruchung T2 - 37. MPA-Seminar - Werkstoff- & Bauteilverhalten in der Energie- & Anlagentechnik CY - Stuttgart, Deutschland DA - 2011-10-06 KW - Dynamic fracture mechanics KW - Crack resistance curve KW - Single specimen technique KW - Key curve PY - 2011 SP - 35.1 EP - 35.19 AN - OPUS4-24618 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Andrés Arcones, Daniel A1 - Weiser, M. A1 - Koutsourelakis, P-S. A1 - Unger, Jörg F. T1 - Embedded Model Bias Quantification with Measurement Noise for Bayesian Model Calibration N2 - A key factor in ensuring the accuracy of computer simulations that model physical systems is the proper calibration of their parameters based on real-world observations or experimental data. Inevitably, uncertainties arise, and Bayesian methods provide a robust framework for quantifying and propagating these uncertainties to model predictions. Nevertheless, Bayesian methods paired with inexact models usually produce predictions unable to represent the observed datapoints. Additionally, the quantified uncertainties of these overconfident models cannot be propagated to other Quantities of Interest (QoIs) reliably. A promising solution involves embedding a model inadequacy term in the inference parameters, allowing the quantified model form uncertainty to influence non-observed QoIs. This paper introduces a more interpretable framework for embedding the model inadequacy compared to existing methods. To overcome the limitations of current approaches, we adapt the existing likelihood models to properly account for noise in the measurements and propose two new formulations designed to address their shortcomings. Moreover, we evaluate the performance of this inadequacy-embedding approach in the presence of discrepancies between measurements and model predictions, including noise and outliers. Particular attention is given to how the uncertainty associated with the model inadequacy term propagates to the QoIs, enabling a more comprehensive statistical analysis of prediction’s reliability. Finally, the proposed approach is applied to estimate the uncertainty in the predicted heat flux from a transient thermal simulation using temperature observations. KW - Model bias KW - Bayesian inference KW - Noise KW - Model updating KW - Quantity of Interest PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-652720 DO - https://doi.org/10.48550/arXiv.2410.12037 SP - 1 EP - 37 PB - arXiv.org AN - OPUS4-65272 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Villani, P. A1 - Andés-Arcones, Daniel A1 - Unger, Jörg F. A1 - Weiser, M. T1 - Posterior sampling with Adaptive Gaussian Processes in Bayesian parameter identification N2 - Posterior sampling by Monte Carlo methods provides a more comprehensive solution approach to inverse problems than computing point estimates such as the maximum posterior using optimization methods, at the expense of usually requiring many more evaluations of the forward model. Replacing computationally expensive forward models by fast surrogate models is an attractive option. However, computing the simulated training data for building a sufficiently accurate surrogate model can be computationally expensive in itself, leading to the design of computer experiments problem of finding evaluation points and accuracies such that the highest accuracy is obtained given a fixed computational budget. Here, we consider a fully adaptive greedy approach to this problem. Using Gaussian process regression as surrogate, samples are drawn from the available posterior approximation while designs are incrementally defined by solving a sequence of optimization problems for evaluation accuracy and positions. The selection of training designs is tailored towards representing the posterior to be sampled as good as possible, while the interleaved sampling steps discard old inaccurate samples in favor of new, more accurate ones. Numerical results show a significant reduction of the computational effort compared to just position-adaptive and static designs. KW - Adaptive Gaussian Processes KW - Bayesian parameter identification KW - AGP PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-652731 DO - https://doi.org/10.48550/arXiv.2411.17858 SP - 1 EP - 23 PB - arXiv.org AN - OPUS4-65273 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Unger, Jörg F. T1 - Methodological Prerequisites for Reliable Simulation Results in the Virtual Lab and Digital Twins N2 - Simulationen übernehmen zunehmend eine zentrale Rolle in sicherheitskritischen Entscheidungsprozessen, etwa im Bauwesen, bei digitalen Zwillingen oder in der prädiktiven Instandhaltung. Damit diese Entscheidungen auf zuverlässigen numerischen Modellen basieren können, müssen die zugrunde liegenden Teilmodelle eindeutig beschrieben, reproduzierbar und in der Community validiert sein. Dieses Manuskript skizziert die notwendigen Voraussetzungen für vertrauenswürdige, FAIR-konforme und entscheidungsfähige Simulationsprozesse. Zunächst wird die Notwendigkeit einer formalen, softwareunabhängigen Beschreibung mathematischer Modelle und numerischer Implementierungen diskutiert. Standards wie VMAP, Ontologien wie MathModDB sowie BIM- und STEP-Formate bieten erste Ansätze zur semantischen Modellbeschreibung und zur automatisierten Generierung simulationsfähiger Eingabedaten. Im zweiten Teil wird die Rolle experimenteller Daten für die Validierung von Modellen beleuchtet. Es wird gezeigt, dass hochwertige, strukturierte und maschinenlesbare Validierungsdatensätze essenziell sind, insbesondere für die Bewertung konstitutiver Modelle. Ein weiteres Kapitel widmet sich der Unsicherheitsquantifizierung. Neben klassischen Fehlermaßen werden aleatorische und epistemische Unsicherheiten sowie deren Einfluss auf die Modellbewertung behandelt. Besondere Aufmerksamkeit gilt der Bayes’schen Kalibrierung, der Trennung von Trainings und Testdaten und der Notwendigkeit, auch Begleitversuche aus Materialtests zu dokumentieren. Abschließend wird die Idee einer Benchmarking-Plattform vorgestellt, die auf reproduzierbaren Workflows, automatisierter Provenienzverfolgung und der Nutzung von Research Object (RO) Crates basiert. Diese Plattform erlaubt die dezentrale Veröffentlichung und zentrale Abfrage von Benchmark-Ergebnissen und fördert eine gemeinschaftliche Verifikation und Validierung. Ziel ist es, die Vergleichbarkeit von (Open-Source-)Simulationstools zu verbessern um dadurch komplexe experimentelle Setups zunehmend durch zuverlässige Simulationen ersetzen zu können. T2 - NAFEMS - Symbiose von Simulation und Test CY - Wiesbaden, Germany DA - 12.11.2025 KW - Verification and Validation, KW - Digital twins KW - Virtual lab KW - Uncertainty quantification PY - 2025 SN - 978-1-83979-242-7 SP - 23 EP - 28 PB - NAFEMS CY - Wiesbaden, Germany AN - OPUS4-65271 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Wolf, Marcus A1 - Bork, Claus-Peter T1 - Corrosion fatigue of X46Cr13 at 60 °C exposed to CO2-saturated geothermal brine N2 - In geothermal power plants the materials used in pumps are loaded cyclically and exposed constantly to the highly corrosive hot thermal water. The lifetime reduction of AISI 420C (X46Cr13, 1.4034) is demonstrated in in-situ-laboratory experiments (T=60 °C, geothermal brine: Stuttgart Aquifer flow rate: 9 l/h, CO2). S-N plots, micrographic-, phase-, fractographic- and surface analysis were applied to obtain sustainable information on the corrosion fatigue behavior. Maximum number of cycles (here 12.5 x 106 cycles to failure) is reached at σa =173 MPa. No typical fatigue strength exists and passive corrosion fatigue may be identified as failure cause. T2 - EUROCORR 2012 - The European corrosion congress CY - Istanbul, Turkey DA - 09.09.2012 KW - Steel KW - Corrosion fatigue KW - Corrosion chamber KW - CCS KW - CO2-storage PY - 2012 SP - 1 EP - 11 AN - OPUS4-28586 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Protz, Christian A1 - Völzke, Holger A1 - Ellouz, Manel A1 - Kasparek, Eva Maria A1 - Zencker, Uwe A1 - Grünewald, Heike A1 - Gründer, Klaus-Peter T1 - ConDrop - Development of numerical simulation approaches for drop test analyses of steel sheet containers N2 - According to disposal requirements, containers for radioactive waste have to withstand drop tests at defined conditions corresponding to the considered package category. Alternatively to prototype drop tests, numerical methods can be applied, if they are suitable and sufficiently verified. In this context BAM (Federal Institute for Materials Research and Testing) started the research project ConDrop to develop a reliable Finite Element (FE) model describing the mechanical behavior of a box shaped steel container during a drop test and to determine unfavorable scenarios within future safety assessment procedures of comparable steel sheet containers. In a first step, a FE model of a representative steel sheet container was developed. Flat bottom-side drop tests with the unloaded container from different heights onto an IAEA target were simulated. In order to verify the numerical calculations, two drop tests with an unloaded KONRAD Type V steel sheet container were carried out at the BAM drop test facility. Both drop tests (flat drop from heights 0.4 m and 5 m onto the unyielding IAEA target) had been documented by various extensive measurements: strain and deceleration measurement by means of strain gauges and accelerometers, high-speed video as well as optical 3D-measurements using the method of projected fringes in combination with close range photogrammetry. The measured strain and deceleration values are presented and compared with the calculated results. T2 - 53rd INMM Annual meeting CY - Orlando, FL, USA DA - 15.07.2012 KW - INMM 53rd annual meeeting PY - 2012 SP - 1 EP - 7 AN - OPUS4-26417 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Glauber, J.-P. A1 - Lorenz, J. A1 - Liu, J. A1 - Seifert, M. A1 - Hoffmann, V. A1 - Abad Andrade, Carlos Enrique A1 - Rogalla, D. A1 - Harms, C. A1 - Wark, M. A1 - Nolan, M. A1 - Devi, A. T1 - High Quality Crystalline VN Thin Films via MOCVD from a New Vanadium Precursor: Linking Growth Chemistry to Functional Catalytic Surfaces N2 - Vanadium nitride (VN) has been identified as a promising material for numerous applications including electrochemical nitrogen reduction reaction (eNRR). For such applications, catalyst nanoengineering will help to experimentally test its theoretically predicted eNRR activity, but the majority of investigated VN catalysts are prepared by fabrication methods that do not allow for nanoengineering to the required degree. Herein, we report on a new metalorganic chemical vapor deposition (MOCVD) process for the growth of high quality, facetted and crystalline VN thin films relevant for eNRR applications. N,N’-diisopropylformamidinato [V(dpfamd)3] was identified as a promising precursor as it possesses favorable thermal properties relevant for MOCVD. The application of [V(dpfamd)3] in a MOCVD process with NH3 as co-reactant yielded crystalline VN thin films on Si substrates with high compositional purity. With the potential of using the catalytic activity of VN towards eNRR, the structure-property correlation is of relevance and in this context, the thin films were subjected to complementary analysis including X-ray diffraction (XRD), Rutherford backscattering spectrometry in combination with nuclear reaction analysis (RBS/NRA), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Based on the observation of the significant influence NH3 has on the growth characteristics, we conducted first principles density functional theory (DFT) simulations of the precursor reactivity in the absence and presence of NH3 towards VN, supporting experimental findings of energetically more favorable decomposition of [V(dpfamd)3] to VN in the presence of NH3. Process transfer from Si to conductive Ti substrates, relevant for prospective electrochemical testing, revealed comparable VN thin film properties rendering these films promising for further investigation of eNRR applications in follow up studies. KW - Metal nitrades KW - MOCVD KW - Nitrogen reduction reaction KW - Precursors KW - DFT PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-648600 DO - https://doi.org/10.26434/chemrxiv-2025-1t4gq SP - 1 EP - 25 AN - OPUS4-64860 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Grimault de Freitas, Tomás A1 - de Araujo Abilio, André A1 - Konert, Florian A1 - Nietzke, Jonathan A1 - Krzysch, Zephanja A1 - Böllinghaus, Thomas A1 - Sobol, Oded T1 - Challenges with metallic materials for the transport and storage of hydrogen N2 - The hydrogen economy is one of the most important solutions to achieve climate neutrality in Europe. It involves the production, storage, transport and use of large quantities of hydrogen in existing and new infrastructures. Components along this supply chain, such as pipelines and storage tanks, are made of various metallic materials, with steel being the most common construction material. The rapid introduction of hydrogen therefore brings with it major challenges, in particular the need for comprehensive qualification of components and materials to ensure the sustainable and safe use of hydrogen technologies. This article provides an overview of the state of the art in the testing of materials and components as well as corresponding future trends and developments for a successful transition to a hydrogen economy. T2 - VGBE - Materials and Quality Assurance 2023 CY - Bergheim, Germany DA - 10.05.2023 KW - Hydrogen Embrittlement KW - Materials Testing KW - Component Testing KW - High-Pressure Gaseous Hydrogen KW - Hollow Specimen Technique PY - 2024 VL - 4 SP - 60 EP - 64 PB - VGBE Energy AN - OPUS4-60686 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Georg, Paul A1 - Block, R. A1 - Heister, W. A1 - Holl, S. A1 - Pulm, A. A1 - Hofmann-Böllinghaus, Anja T1 - A score regarding the need for assistance - considering pedestrians with impairments in evacuation planning N2 - The capabilities of pedestrians for evacuation have a significant impact on the time required to reach a safe place. Usually, the evacuation is split into two main stages: pre-movement-phase and movement-phase. For both a large number of studies investigate different representations of behaviour and impacts. But the influence of impairments is usually not taken into account. In addition, most of the scientific researches focus the investigation of the movement phase. This publication presents a novel approach to score the need for assistance and to estimate the effect on evacuation performance. The proposed score considers characteristic impairments in three dimensions of behaviour: reception, perception and realisation. In an unannounced evacuation training in a sheltered workshop, the evacuation behaviour and pre-movement phase were analysed. The analysis indicates that the pre-movement time depends on the kind of impairment as well as on organisational boundaries. Despite the special needs for assistance, the evacuation process in a sheltered workshop is quite similar to other sub-populations. T2 - 5. Magdeburger Brand- und Explosionsschutztage 2017 CY - Magdeburg, Germany DA - 23.03.2017 KW - Human behaviour KW - Human factors KW - Egress KW - Evacuation KW - Persons with impairments PY - 2017 SN - 978-3-00-056201-3 DO - https://doi.org/10.978.300/0562013 SP - 1 EP - 13 CY - Magdeburg AN - OPUS4-40051 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krentel, Daniel A1 - Tschirschwitz, Rico A1 - Kluge, Martin A1 - Askar, Enis A1 - Habib, Abdel Karim A1 - Kohlhoff, Harald A1 - Neumann, Patrick P. A1 - Rudolph, Michael A1 - Schoppa, André A1 - Storm, Sven-Uwe A1 - Szczepaniak, Mariusz T1 - Experimental investigation of failure of LPG gas tanks in passenger cars during full fire development N2 - In continuation of a preceding test series involving sole LPG vehicle tanks, three passenger cars equipped with identical toroidal steel LPG tanks were set on fire. The tanks were installed in the space normally reserved for the spare tyre, in the car boot. No safety device was installed on the tank, in order to force critical failure of the cylinder. Two of the cars were equipped with a tank filled with liquefied propane to a level of 20 % (5.3 kg), the third one was filled completely (25.5 kg). The partially filled tanks failed critically within a time period of more than 20 min after the initiation of the fire. The fully-filled tank did not rupture; the propane was released continuously through a small leak that appeared during the fire. Comprehensive equipment was used to procure measurement data, enabling an analysis of potential consequences and hazards to humans and infrastructure within the vehicle surroundings. The inner status of the tank (pressure, temperature of the liquid phase and the steel casing), the development of the fire (temperature inside and around the vehicle) and the pressure induced in the near-field in case of tank rupture were recorded. The results were analysed in detail and compared against the data gained in tests involving sole, but identical LPG tanks. T2 - FIVE 2018 CY - Boras, Sweden DA - 03.10.2018 KW - Behälterversagen KW - LPG KW - Alternative Antriebe KW - Fahrzeugbrand KW - Auswirkungsbetrachtung PY - 2018 SN - 978-91-88695-95-6 VL - 51 SP - 123 EP - 131 PB - RISE Safety CY - Boras AN - OPUS4-46310 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rabe, Frederik A1 - Kaudelka, Sven A1 - Hofmann-Böllinghaus, Anja A1 - Monreal, Nils A1 - Dülsen, Steffen A1 - Kempel, Florian A1 - Mühlnikel, Rüdiger A1 - Klaffke, Benjamin ED - Abildgaard, L.-L. ED - Sörensen, J.G. ED - Dederichs, A. T1 - Experimental and numerical investigation of enclosure fires - Application to room fires and intermediate scale tests N2 - One of our research topics focus on fire in residential buildings because approximately 80% of all fire fatalities in Europe occur in residential building fires. The aim is to identify critical fire scenarios and to model these fire scenarios with experimental and numerical methods. We perform a wide ränge of reaction-to-fire tests and use different Software tools to simulate fires. Another field of research is fire-safety of escape and rescue routes, because in case of fire, smoke in staircases can be a serious problem. In 2005, 8 people died in Berlin during a staircase fire which was caused by arson. A stroller had been ignited and the resulting smoke filled the staircase quickly. The wooden staircase also was involved in the fire. Several inhabitants tried to leave their flats via the staircase and were trapped. T2 - FSD 2014 - Fire Safety Day CY - Lyngby/Kopenhagen, Denmark DA - 12.06.2014 KW - Äquivalente Branddauer KW - Numerische Simulation KW - Brandszenarien PY - 2014 SP - 49 EP - 50 AN - OPUS4-30901 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krentel, Daniel A1 - Rudolph, Michael A1 - Tschirschwitz, Rico A1 - Kluge, Martin A1 - Askar, Enis A1 - Habib, Abdel Karim A1 - Kohlhoff, Harald A1 - Neumann, Patrick P. A1 - Schalau, Bernd A1 - Schoppa, André A1 - Storm, Sven-Uwe A1 - Szczepaniak, Mariusz A1 - Mair, Georg W. T1 - Infrared radiation measurement at failure of mobile gas vessels N2 - 15 identical off-the-shelf propane cylinders (m = 11 kg liquid propane) were underfired. The infrared Radiation of the Explosion, that occurred in the aftermath of the vessel failure, was recorded using four bolometers. These measurements are compared with an estimation of the Maximum intensity gained by an Analysis of the Video data, an Extended Version of the Stefan-Boltzmann law and a BLEVE model. T2 - 26th International Colloquium on the Dynamics of Explosions and Reactive Systems CY - Boston, USA DA - 30.07.2017 KW - Failure of gas vessels KW - Propane cylinder KW - Gas explosion KW - Consequences KW - Infrared radiation PY - 2017 SP - 1 EP - 6 PB - FM Global CY - Seattle, USA AN - OPUS4-41993 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hofmann-Böllinghaus, Anja A1 - Knaust, Christian A1 - Krüger, Simone T1 - Brandverhalten von Bauprodukten: Brauchen wir Regelungen für die Menge und Giftigkeit der Rauchgase? T2 - 57. Jahresfachtagung der Vereinigung zur Förderung des Deutschen Brandschutzes e.V. (vfdb 2008) CY - Bochum, Deutschland DA - 2008-04-27 PY - 2008 N1 - Geburtsname von Hofmann-Böllinghaus, Anja: Hofmann, A. - Birth name of Hofmann-Böllinghaus, Anja: Hofmann, A. SP - 169 EP - 178 AN - OPUS4-17755 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hofmann-Böllinghaus, Anja A1 - Kaudelka, Sven T1 - Einfluss von Beschädigungen auf das Brandverhalten von WDVS N2 - Nach dem großen Baustellenbrand in Frankfurt 2012 hatte die Bauministerkonferenz (BMK) beschlossen, das Brandverhalten von Wärmedämmverbundsystemen [WDVS] hinsichtlich von Brandquellen vor der Fassade zu untersuchen. Die Feuerwehr Frankfurt hat eine Sammlung von Bränden, bei denen WDVS beteiligt waren, initiiert. Wertet man diese Sammlung hinsichtlich der Brandentstehung aus, fällt auf, dass von den insgesamt 57 Bränden 79 % (45 Brände) vor der Fassade begannen. 25 dieser 45 Brände wurden durch brennenden Müll oder Müllcontainer ausgelöst. Die meisten der gesammelten Brände (50) waren in den letzten fünf Jahren (2010 - 2014). Auf Grund dieser Erkenntnisse wurden an der BAM Müilcontainer (aus Plastik) hinsichtlich ihrer Entflammbarkeit und Wärmefreisetzung untersucht. Außerdem wurden im Auftrag der BMK Müllcontainer hinsichtlich ihrer Wärmefreisetzung und Brandentwicklung im Großversuch an der MFPA Leipzig untersucht. Mit Hilfe dieser Voruntersuchungen wurde eine Brandquelle identifiziert, die Zündquellen wie einen brennenden, Müllcontainer oder kleinere Ansammlungen von Sperrmüll repräsentiert: Es wurde eine 200 kg Holzkrippe gewählt, da die Holzkrippe bessere Ergebnisse hinsichtlich der Reproduzierbarkeit der Ergebnisse darstellt als z.B. ein Müllcontainer. Mit dieser Zündquelle wurden Großversuche an der MFPA Leipzig mit einem zugelassenen WDVS durchgeführt. Das WDVS zeigte unter diesen Prüfbedingungen ein nicht akzeptables Brandverhalten. Die folgenden zwei Versuche wurden mit Ertüchtigungsmaßnahmen durchgeführt, die eine signifikante Verbesserung des Brandverhaltens brachten. Zusätzlich wurde an der BAM eine Serie von Brandversuchen im Kieinmaßstab in der Single Burning Item (SBI) Prüfeinrichtung durchgeführt. Dabei wurde die auf das WDVS wirkende Wärmefreisetzungsrate variiert und der Einfluss von Grad und Größe von Beschädigungen der Putzschicht hinsichtlich des Brandverhaltens untersucht. Deutliche Unterschiede im Brandverhalten konnten sowohl quantitativ als auch qualitativ nachgewiesen werden. Neben der den Versuchsbedingungen zugrunde liegenden Wärmefreisetzungsrate konnten Art und Lage der Beschädigung in der Putzschicht als auch brandbeeinflussende Größen charakterisiert und beschrieben werden. T2 - FeuerTRUTZ Brandschutzkongress 2015 CY - Nuremberg, Germany DA - 18.02.2015 KW - Fassaden KW - Brandschutz KW - WDVS KW - Polystyrol PY - 2015 SP - Kap. 2.2, 269 EP - 279 AN - OPUS4-33341 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hofmann-Böllinghaus, Anja A1 - Kaudelka, Sven A1 - Ruhs, A. T1 - Challenges for fire safety in etic systems with polystyrene insulation N2 - Several fires involving external thermal insulating (ETIC) systems with polystyrene in Germany started an extensive discussion about fire safety of such systems. The Frankfurt fire service started to collect reports about real fire cases which involved ETICS with polystyrene two years ago. This collection shows that especially fires, which started in front of the buildings led to more severe fires of the facades than fires inside the buildings. In several fires the ignition sources were burning waste containers. Three of the real cases are discussed in more detail: a serious fire in Frankfurt on a building site and two fires of apartment buildings, which developed quite differently. Additionally the plastic waste containers, which started several fires are investigated regarding ignitability and heat release rates. The investigation shows that plastic waste containers are very effective as ignition source and that the usual placement directly in front of combustible facades can be a problem for fire safety. Moving these containers and unintentional contact with the facade can lead to damage of the facade coating. These damages were investigated qualitatively and quantitative on a wide collection of buildings. After classifying the damage intermediate scale tests were performed in a modified Single Burning Item (SBI) Test. The damage of the coating was varied as well as the power of the sand bed burner of the SBI apparatus. The damage significantly influenced the fire development on the specimen. In some tests the damaged rendering of the ETIC system collapsed and resulted in a sudden fire growth: after the collapse of the rendering the whole specimen was suddenly on fire. Several effects, which could be seen in the intermediate scale tests correspond to observations which were made in the real cases. As a consequence of the investigations challenges and possible measures to enhance fire safety of ETIC systems are discussed. T2 - Fire and materials 2015 - 14th International conference and exhibition CY - San Francisco, CA, USA DA - 02.02.2015 KW - ETICS KW - Large and intermediate scale tests KW - Facade fires PY - 2015 SP - 543 EP - 553 PB - Interscience Communications AN - OPUS4-32693 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Vöse, Markus A1 - Fedelich, Bernard ED - Maruyama, K. ED - Abe, F. ED - Igarashi, M. ED - Kishida, K. ED - Suzuki, M. ED - Yoshimi, K. T1 - Grain boundary cavitation under time-varying normal stresses N2 - In a polycrystal, the development of creep damage, especially for low extemal loads, is related to nucleation and difiüsive growth of cavities on the grain boundaries. For low stresses, the contribution to cavity growth by dislocation creep of the suirounding material can be neglected. However, grain boundaiy diffitsion is mainly driven by the local normal stiess acting on the grain boundaiy. Under creep conditions, even under a constant extemal load, an individual grain boundaiy generally experiences a time-varying normal stress, due to stress redistributions within the polycrystalline stiuctuie. Indeed, a constrained cavitating grain boundaiy is relieved, since matter is transported to and deposited in the grain boundaiy plane, which causes the adjoining giains to drill apart. A Simulation proceduie based on the use of complex holomoiphic fiinctions for solving the diffiision problem has been used to investigate multiple cavity growth on a grain boundaiy subjected to a constant normal stress. A simplified model has been developed to describe the cavitation behaviour observed in the simulations. Finally, the analysis of cavitation simulations with time-vaiying nomial stresses, including the cases with veiy low or negative stresses, has been used to extend the simplified cavitation model to more general normal stiess time profiles. T2 - 12th International Conference on Creep and Fracture of Engineering Materials and Structures CY - Kyoto, Japan DA - 27.05.2012 KW - Creep damage KW - Grain boundary diffusion KW - Cavitation KW - Simulation KW - Evolution equations PY - 2012 SP - 1 EP - 4 AN - OPUS4-27544 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böllinghaus, Thomas A1 - Schobbert, Helmut A1 - Lammers, Marco A1 - Michael, Thomas A1 - Skopp, André T1 - Laser-Plasma-Pulver-Schweißen hochlegierter austenitischer Stähle T2 - 5. Konferenz "Strahltechnik" CY - Halle (Saale), Deutschland DA - 2001-11-27 PY - 2001 SP - 67 EP - 76 CY - Halle (Saale) AN - OPUS4-2428 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gaal, Mate A1 - Wernicke, Pascal A1 - Hufschläger, Daniel T1 - Pulse compression for air-coupled ferroelectret and thermoacoustic transducers N2 - The main advantage of air-coupled ultrasonic testing is the absence of a liquid couplant, which can damage some materials. However, most air-coupled testing scenarios have the challenge of low signals and a signal-to-noise ratio (SNR) several orders of magnitude lower than with couplant-assisted tech-niques. Since this challenge of small SNR also exists in radar technology, the pulse compression used there was adapted and applied to the physical conditions of air-coupled ultrasonic testing. This paper presents ultrasonic transmission measurements on a carbon-fibre-reinforced polymer plate using two experimental setups: 1) a thermoacoustic transmitter and an optical microphone and 2) a pair of ferroe-lectret transducers as transmitter and receiver. Thermoacoustic transmitters convert electrical energy to heat, which causes the air to expand thus producing acoustic waves. The optical microphone is based on a Fabry-Perot interferometer. Ferroelectrets are charged cellular polymers, having piezoelectric proper-ties and excellent acoustic matching to air. Both thermoacoustic transmitters and ferroelectrets are non-linear regarding the relationship between the excited sound pressure and the excitation voltage. Due to these physical boundary conditions, unipolar coding was used to modulate the excitation signals. Vari-ous codes were tested, and parameters of the excitation pulses were varied to find the optimal combina-tion for each experimental setup. The application of pulse compression to the combination of thermo-acoustic transmitter and optical microphone increased the signal-to-noise ratio by up to 16 dB and for the ferroelectret transducers by up to 23 dB. T2 - 30th International Congress on Sound and Vibration CY - Amsterdam, The Netherlands DA - 08.07.2024 KW - Pulse compression KW - Air-coupled ultrasonic transducers KW - Ferroelectret KW - Thermoacoustics PY - 2024 SN - 978-90-90-39058-1 SP - 1 EP - 7 AN - OPUS4-60725 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Auersch, Lutz T1 - Reduction of ground-induced building vibrations by kinematic and inertial soil-structure interac-tion and by base isolation N2 - Many buildings on the soil have been measured and the transfer function freefield-to-building is ana-lysed. In general, an amplification at low frequencies, an amplification for the floor resonances, and a reduction for higher frequencies can be observed. Most of the measurement examples show a flexible behaviour along the height of the buildings. The prediction of building vibration consists typically of three steps. At first, the dynamic stiffness of the foundation and secondly the kinematic soil-structure interaction has to be calculated for example by the combined finite-element boundary-element meth-od. The stiffness of the foundation reduces the incoming waves (the kinematic interaction). Finally, the inertial interaction of the building with the foundation soil is calculated by the conventional finite ele-ment method where the dynamic foundation stiffness from the first step is added at the bottom of the building. The building on the compliant soil has a fundamental vertical resonance usually below 10 Hz. A parametrical variation clearly shows the influence of the elasticity of the building on this reso-nance frequency and amplitude. Moreover for column-type office buildings, the low-frequency floor resonances can further reduce this fundamental frequency. A 1-dimensional model has been estab-lished which can well approximate the behaviour of the 3-dimensional building models. It is used to demonstrate the effect of a base isolation with soft elements at the foundation. A rigid building model clearly over-estimates the isolation effect, which is smaller for a model with flexible walls, columns and floors. An even simpler model of an infinitely high building is suggested for the mitigation effect, and the resonance frequency of the rigid building should be replaced by a better performance indica-tor, which is based on the impedance ratio of the isolation and the wall and which can be also ex-pressed as a characteristic frequency. T2 - 30th International Congress on Sound and Vibration CY - Amsterdam, Netherlands DA - 08.07.2024 KW - Building vibrations KW - Base isolation KW - Foundation stiffness KW - Kinematic soil-structure interaction KW - Transfer functions of flexible buildings PY - 2024 SN - 978-90-90-39058-1 SN - 2329-3675 SP - 1 EP - 8 AN - OPUS4-61245 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Baer, Wolfram T1 - Key Curve-Einprobenverfahren zur Ermittlung dynamischer Bruchmechanikkennwerte duktiler Gusseisenwerkstoffe? - Review und Analyse T2 - 38. Tagung des DVM-Arbeitskreises Bruchvorgänge "Technische Sicherheit, Zuverlässigkeit und Lebensdauer" CY - Aachen, Deutschland DA - 2006-02-14 KW - Key Curve KW - Dynamische Bruchmechanik KW - Duktiles Gusseisen KW - Einprobenverfahren KW - Dynamische Risswiderstandskurve KW - Review PY - 2006 VL - 38 SP - 91 EP - 98 CY - München AN - OPUS4-12669 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram ED - Bell, R. ED - Merati, A. ED - M. Nganbe, ED - Tyson, B. ED - Wang, X. T1 - Analyses of dynamic fracture toughness data of ductile cast iron based on ASME code case N-670 and ASTM E 1921 T2 - ICF12 - 12th International Conference on Fracture CY - Ottawa, Canada DA - 2009-07-12 KW - Dynamic fracture toughness KW - Ductile cast iron KW - Statistics PY - 2009 SP - 1 EP - 10(?) AN - OPUS4-19709 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wosniok, Aleksander A1 - Schukar, Marcus A1 - Breithaupt, Mathias A1 - Kriegsmann, Andreas T1 - Distributed Fibre Optic Monitoring of Hydrogen Storage Composite Pressure Vessels for Automotive Use N2 - We present our research work on the condition monitoring of hydrogen storage composite pressure vessels using distributed fibre optic sensors. The sensing fibres are integrated into the composite structure by wrapping them over the polymer liner in the helical and circumferential direction during the manufacturing process of the carbon fibre reinforced polymer. The following use of optical backscatter reflectometry allows for continuous condition monitoring and precise detection and localization of structural damages during the entire service life. To account for the time-dependent strength degradation of the composite pressure vessels, both slow burst and ambient hydraulic cycling tests, respectively, were conducted on five 70 MPa pressure vessels with integrated fibre optic sensors. The results achieved via distributed fibre optic strain sensing demonstrate a near linear strain response to pressure suitable for sensitive condition monitoring and confirm the required robustness of the selected sensor solution. T2 - DGZfP-Jahrestagung 2025 CY - Berlin, Germany DA - 26.05.2025 KW - Distributed fibre optic sensor (DFOS) KW - Composite pressure vessel KW - Optical backscatter reflectometry KW - Slow burst test KW - Ambient hydraulic cycling test PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-653067 DO - https://doi.org/10.58286/32344 SP - 1 EP - 8 PB - NDT.net AN - OPUS4-65306 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kocherla, Amarteja A1 - Strangfeld, Christoph A1 - Hüsken, Götz T1 - Embedded Sensors for Quality Control and Structural Integrity Monitoring of Large-scale 3DCP Structures N2 - In extrusion-based 3D concrete printing (3DCP), addressing challenges related to safety, reliability, and quality control is crucial for widespread adoption. Yet current limitations in monitoring material properties during and after printing hinder the development of effective 3DCP guidelines. Therefore, the development of an inline sensing system capable of real-time monitoring and adjustment of process parameters is necessary to overcome these challenges. Building upon an existing inline sensing system developed by BAM, which currently monitors material properties during printing and the geometry of the print post-extrusion, this study extends its capabilities to post-extrusion monitoring using embedded piezoelectric (PZT) sensors. These PZT sensors provide localized measurements of material changes through electrical impedance (EI) measurements without disrupting the printing process. By embedding these sensors in 3D printed structures, continuous monitoring is achieved from layer deposition through 1-day of hydration. To achieve this, initially, PZT sensors were developed with multiple layers of protective coatings. Two different 3D printed mixtures, each with different hydration behaviors, were utilized, and PZT sensors were strategically placed between printed layers to maintain their integrity. EI measurements were collected continuously from printing through 1 day of hydration. Analysis of amplitude and frequency changes in the EI response spectrum provided insights into material behavior post-printing. The study highlights how continuous monitoring of frequency and conductance can track structural builtup and property development of the material. Rapid changes in conductance measurements, immediately post-printing indicate swift structural built-up, while key hydration phases are reflected in frequency measurements. T2 - 34th Annual Conference and Exhibition on Non Destructive Evaluation & Enabling Technologies CY - Chennai, India DA - 12.12.2024 KW - Embedded Sensors KW - 3D Concrete Printing KW - Quality Control KW - Inline Sensing KW - Structural Integrity PY - 2025 SP - 1 EP - 8 PB - Springer Nature CY - Heidelberg AN - OPUS4-65305 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Knigge, Xenia A1 - Radnik, Jörg T1 - Physico-chemical characterization of sterilized TiO2 D540 nanoparticles by XPS / HAXPES / SEM N2 - Here a dataset of XPS, HAXPES and SEM measurements for the physico-chemical characterization of sterilized TiO2 D540 nanoparticles is presented. The measurements are part of the H2020 project “NanoSolveIT”. KW - XPS KW - HAXPES KW - SEM KW - NanoSolveIT KW - TiO2 D540 nanoparticles PY - 2023 DO - https://doi.org/10.5281/zenodo.7961317 PB - Zenodo CY - Geneva AN - OPUS4-57669 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Knigge, Xenia A1 - Radnik, Jörg T1 - Physico-chemical characterization of sterilized ZnO nanoparticles by XPS / HAXPES / SEM N2 - Here a dataset of XPS, HAXPES and SEM measurements for the physico-chemical characterization of sterilized ZnO nanoparticles is presented. The measurements are part of the H2020 project “NanoSolveIT”. KW - XPS KW - HAXPES KW - SEM KW - ZnO nanoparticles KW - NanoSolveIT PY - 2023 DO - https://doi.org/10.5281/zenodo.7990301 PB - Zenodo CY - Geneva AN - OPUS4-57661 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hahn, Marc Benjamin T1 - Behind the paper: Radiation, DNA and water: New techniques for deeper insights N2 - To gain deeper insights into the old questions about the influence of water on radiation interaction with DNA, new spectroscopic techniques had to be applied. KW - DNA KW - DNA radiation damage KW - XPS KW - Geant4 KW - Low energy electrons KW - OH radical KW - Hydrated DNA KW - Hydration shell KW - Double-strand break (DSB) KW - Dissociative electron attachment (DEA) KW - Single-strand break (SSB) KW - LEE KW - PES KW - Ionization KW - Reactive oxygen species KW - ROS KW - Base damage KW - Base loss KW - Cancer therapy KW - TOPAS KW - TOPAS-nbio PY - 2021 UR - https://go.nature.com/3gjZVWG SP - 1 EP - 3 PB - Springer Nature CY - London AN - OPUS4-52461 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Knigge, Xenia A1 - Radnik, Jörg T1 - Physico-chemical characterization of sterilized CeO2 nanoparticles by XPS / HAXPES / SEM N2 - Here a dataset of XPS, HAXPES and SEM measurements for the physico-chemical characterization of sterilized CeO2 nanoparticles is presented. The measurements are part of the H2020 project “NanoSolveIT”. KW - XPS KW - HAXPES KW - SEM KW - NanoSolveIT KW - CeO2 nanoparticles PY - 2023 DO - https://doi.org/10.5281/zenodo.7941461 PB - Zenodo CY - Geneva AN - OPUS4-57667 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Knigge, Xenia A1 - Radnik, Jörg T1 - Physico-chemical characterization of sterilized Co2.25Fe0.75O4 nanoparticles by XPS / HAXPES / SEM N2 - Here a dataset of XPS, HAXPES and SEM measurements for the physico-chemical characterization of sterilized Co2.25Fe0.75O4 nanoparticles is presented. The measurements are part of the H2020 project “NanoSolveIT”. KW - XPS KW - HAXPES KW - SEM KW - NanoSolveIT KW - Co2.25Fe0.75O4 nanoparticles PY - 2023 DO - https://doi.org/10.5281/zenodo.7940538 PB - Zenodo CY - Geneva AN - OPUS4-57663 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Knigge, Xenia A1 - Radnik, Jörg T1 - Physico-chemical characterization of sterilized Fe2O3 nanoparticles by XPS / HAXPES / SEM N2 - Here a dataset of XPS, HAXPES and SEM measurements for the physico-chemical characterization of sterilized Fe2O3 nanoparticles is presented. The measurements are part of the H2020 project “NanoSolveIT”. KW - XPS KW - HAXPES KW - SEM KW - NanoSolveIT KW - Fe2O3 nanoparticles PY - 2023 DO - https://doi.org/10.5281/zenodo.7941001 PB - Zenodo CY - Geneva AN - OPUS4-57665 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jonietz, Florian A1 - Krankenhagen, Rainer A1 - Noack, M. A1 - Gensecke, K. A1 - Wiedenmann, E. T1 - 3D-Formbestimmung mit integrierter thermografischer Qualitätsprüfung N2 - Sowohl die 3D-Formbestimmung als auch die Thermografie sind Verfahren der Qualitätssicherung. Im vorgestellten Projekt wird versucht, die beiden Methoden zusammenzuführen. Das Prinzip des für die Formbestimmung verwendeten 3D-Scanners beruht auf dem bereits bekannten Verfahren der Streifenlichtprojektion. Die Neuartigkeit des hier verwendeten 3D-Scanners besteht darin, dass nicht im sichtbaren, sondern im infraroten Spektralbereich gearbeitet wird. Dadurch wird es möglich, nicht die Reflexion, sondern die Wärmestrahlung des Prüfobjektes nach Absorption der eingebrachten Strahlung auszuwerten. Dies ermöglicht, auch optisch „nicht-kooperative“ Oberflächen zu erfassen. Die Anregung mit Wärmestrahlung stellt das Bindeglied zum Verfahren der aktiven Thermografie für die Detektion verdeckter Schäden dar. Bei letzterem Verfahren wird der Wärmestau über Defekten beim Eindringen der Wärme in die Tiefe des Materials gemessen. Dabei stellen Defekte eine Störung des 3D-Scan-Verfahrens dar, während umgekehrt unregelmäßig geformte Oberflächen das thermografische Verfahren erschweren, d.h. der Messeffekt eines der Verfahren ist ein Störeffekt für das jeweils andere Verfahren. Es wird zum einen der Frage nachgegangen, inwieweit das 3D-Scan-Verfahren durch verdeckte thermische Defekte beeinträchtigt wird, und zum anderen die Möglichkeit untersucht, den vorhandenen 3D-Scanner auch für die aktive Thermografie einzusetzen. Es werden CFK-Proben mit künstlich eingebrachten thermischen Defekten untersucht und die Möglichkeiten und Grenzen der vorhandenen Messapparatur für die Defekterkennung aufgezeigt. T2 - DGZfP-Jahrestagung 2017 CY - Koblenz, Germany DA - 22.05.2017 KW - 3D-Formbestimmung KW - Thermografische Qualitätsprüfung KW - Streifenlichtprojektion KW - 3D-Scanner KW - Aktive Thermografie PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-407856 UR - https://jahrestagung.dgzfp.de/Portals/151//doc/Mi.1.A.3.pdf SN - 978-3-940283-85-6 VL - 162 SP - 1 EP - 9 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-40785 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mooshofer, H. A1 - Boehm, Rainer A1 - Heinrich, W. A1 - Fendt, K. A1 - Goldammer, M. A1 - Kolk, K. A1 - Vrana, J. T1 - Amplitudenbasierte Fehlergrößenbewertung mit SAFT: Auf dem Weg von der bildlichen Darstellung zum Messverfahren N2 - Die Größenbewertung von Anzeigen und die Bestimmung der Nachweisgrenze spielen bei der Ultraschallprüfung eine zentrale Rolle: Sie stellen sicher, dass kritische Ungänzen erfasst und bruchmechanisch behandelt werden können. Bei SAFT wurde bisher die Größe von Ungänzen dadurch bestimmt, dass die räumliche Anzeigenausdehnung im Rekonstruktionsergebnis ausgewertet wird, d.h. die Anzahl von Voxel über die sich eine Anzeige erstreckt. Auf diese Weise lassen sich jedoch nur Defektanzeigen bewerten, die größer oder gleich der Wellenlänge sind. Bei kleinen Defekten versagt diese Methode, d.h. es ist keine Größenbewertung möglich. Außerdem bietet diese Methode keine Aussage über die Nachweisgrenze des Verfahrens. Ein Hauptvorteil von SAFT gegenüber der konventionellen Ultraschallprüfung ist aber gerade die Verbesserung der Nachweisgrenze, denn SAFT steigert das Signal-Rausch-Verhältnis (SNR) gegenüber dem Gefügerauschen und reduziert statistisches Rauschen. Um diesen Hauptvorteil nutzen (und quantifizieren) zu können, wird für SAFT eine Methode zur Nachweisgrenzenbestimmung und zur Größenbewertung der Anzeigen kleiner Ungänzen benötigt. Neben ihrer räumlichen Ausdehnung lassen sich Anzeigen im SAFT-Ergebnis auch durch ihre Amplitude charakterisieren, wenn die Prüfkopfeigenschaften und die geometrischen Verhältnisse beim Scan berücksichtigt werden. Genauer gesagt durch die Amplitudensumme, in die - neben der Echoamplitude - auch die winkelabhängige Streucharakteristik eingeht. Im Folgenden wird dargelegt, dass sich die Amplitudensumme zur Nachweisgrenzenbestimmung und zur Größenbewertung kleiner Ungänzen eignet. Es wird der Zusammenhang zwischen der Amplitudensumme und der Größe von Ungänzen dargestellt, und es wird gezeigt, dass auch die Anzeigenposition und die Form des Prüfobjektes eine Rolle spielen können. Auf dieser Basis wird eine Methode zur Größenbestimmung kleiner Anzeigen im SAFT-Ergebnis entwickelt. Damit lässt sich das SAFT-Ergebnis als Ersatzfehlergröße darstellen, so wie das bei konventioneller Ultraschallprüfung z.B. mit Hilfe von AVG-Diagrammen erfolgt. Durch die Vervollständigung um die Größenbewertung ist SAFT nicht mehr nur ein bildgebendes Verfahren, sondern es kann vielmehr als vollwertiges Messverfahren dienen. T2 - DGZfP-Jahrestagung 2017 CY - Koblenz, Germany DA - 22.05.2017 KW - Synthetic aperture focussing technique (SAFT) KW - Defektgrößenbewertung KW - Gewichtete Amplitudensumme KW - Kleine Reflektoren PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-411571 SN - 978-3-940283-85-6 VL - 162 SP - 1 EP - 9 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-41157 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maierhofer, Christiane A1 - Krankenhagen, Rainer A1 - Röllig, Mathias A1 - Hosseini, Seyed A1 - Heckel, Thomas A1 - Gaal, Mate A1 - Schadow, Florian A1 - Brackrock, Daniel A1 - Gower, M. A1 - Lodeiro, M. A1 - Baker, G. T1 - Quantitative Bewertung künstlicher und natürlicher Fehler in Faserverbundwerkstoffen mit aktiver Thermografie und Ultraschall N2 - Im EMRP-Projekt VITCEA werden komplementäre ZFP-Verfahren zur Prüfung von Faserverbundwerkstoffen weiterentwickelt und validiert. In diesem Beitrag werden Ergebnisse verschiedener Techniken der aktiven Thermografie und des Ultraschalls vorgestellt. Die Nachweisempfindlichkeiten bezüglich künstlicher und natürlicher Fehler mit unterschiedlichen lateralen Ausdehnungen und in verschiedenen Tiefen werden miteinander verglichen. T2 - DGZfP Jahrestagung 2017 CY - Koblenz, Germany DA - 22.05.2017 KW - CFK KW - GFK KW - Aktive Thermografie KW - Phased Array Ultraschall KW - Luftultraschall PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-410902 SN - 978-3-940283-85-6 VL - BB 162 SP - Di1B1, 1 EP - Di1B1, 8 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung e. V. AN - OPUS4-41090 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - VIDEO A1 - Pauw, Brian Richard T1 - Just a minute: X-ray scattering N2 - An extremely brief summary of what X-ray scattering can do for you (X-ray scattering encompasses small-angle X-ray scattering (SAXS), and wide-angle X-ray scattering (WAXS/XRD), amongst others). See my other videos for more detailed explanations on sample selection, data correction, data analysis, etc. KW - X-ray scattering KW - Introduction KW - Materials science KW - Nanostructure investigation KW - MOUSE PY - 2022 UR - https://www.youtube.com/watch?v=jWWNQyaCTHA DO - https://doi.org/10.26272/opus4-55768 PB - YouTube, LLC CY - San Bruno, CA, USA AN - OPUS4-55768 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Lugovtsova, Yevgeniya T1 - Damage detection in multi-layered plates using ultrasonic guided waves N2 - This thesis investigates ultrasonic guided waves (GW) in multi-layered plates with the focus on higher order modes. The aim is to develop techniques for hybrid structures such as of adhesive bonds and composite pressure vessels (COPV) which are widely used in automotive and aerospace industries and are still challenging to inspect non-destructively. To be able to analyse GW, numerical methods and precise material properties are required. For this purpose, an efficient semi-analytical approach, the Scaled Boundary Finite Element Method, is used. The material properties are inferred by a GW-based optimisation procedure and a sensitivity study is performed to demonstrate the influence of properties on GW. Then, an interesting feature, called mode repulsion, is investigated with respect to weak and strong adhesive bonds. The results show that the coupling between two layers influences the distance between coupled modes in a mode repulsion region, thus allowing for the characterisation of adhesive bonds. At next, wave-damage interaction is studied in the hybrid structure as of the COPV. Results show that the wave energy can be concentrated in a certain layer enabling damage localisation within different layers. Further investigations are carried out on the hybrid plate with an impact-induced damage. Two well-known wavenumber mapping techniques, which allow to quantify the damage in three dimensions, are implemented and their comparison is done for the first time. KW - Lamb waves KW - Composites KW - Structural Health Monitoring KW - Inverse procedure KW - Scaled Boundary Finite Element Method PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:bsz:291--ds-382863 DO - https://doi.org/10.22028/D291-38286 SP - 1 EP - 131 PB - SciDok - Der Wissenschaftsserver der Universität des Saarlandes CY - Saarbrücken, Germany AN - OPUS4-57058 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mair, Georg W. A1 - Becker, Ben A1 - Duffner, Eric A1 - John, Sebastian T1 - Storage systems for CGH2- systematic improvement of RC&s composite storage systems for compressed hydrogen - systematic improvement of regulations for more attractive storage units N2 - Hydrogen is an attractive energy carrier that requires high effort for safe storage. For ensuring safety they have to undergo a challenging approval process. Relevant standards and regulations for composite cylinders used for the transport of for on-board storage of hydrogen are currently based on deterministic (e.g. ISO 11119-3) or semi-probabilistic (UN GTR No. 13) criteria. This paper analysis the properties of such methods in regards to the evaluation of load cycle strength. Their characteristics are compared with the probabilistic approach of the BAM. Based on Monte-Carlo simulations, the available design range (mean value and scatter of strength criteria) of current concepts were exemplarily estimated. The aspect of small sample sizes is analysed and discussed with respect to the evaluation procedures. T2 - 10th International Conference on Sustainable Energy and Environmental Protection CY - Bled, Slovenia DA - 27.06.2017 KW - Probabilistic KW - Hydrogen KW - Composite KW - Cylinder KW - Regulations KW - Load cycles KW - GTR 13 KW - ISO 11119 PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-416820 SN - 978-961-286-054-7 DO - https://doi.org/10.18690/978-961-286-054-7 SP - 1 EP - 10 PB - University of Maribor Press CY - Maribor, Slovenia AN - OPUS4-41682 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kruschwitz, Sabine T1 - Feuchtemessung im Bauwesen - Ein Überblick N2 - Ein Großteil der Schäden im Baubereich ist auf feuchteinduzierte Prozesse zurückzuführen. Der Erhaltungsaufwand allein im Hochbau wurde bereits vor einiger Zeit auf jährlich ca. 35 Mrd. Euro geschätzt. Aus diesem Grund hat die Feuchtemessung in der Bauwerksdiagnose eine sehr hohe Bedeutung - und im Idealfall sollte sie natürlich alles können: schnell sein, wiederholbar und zerstörungsfrei anwendbar. Zwar gibt es eine Vielzahl an verfügbaren Feuchtemesstechniken, oft fällt es Anwendern aber schwer, einzuschätzen welches die richtige Prüfmethode für ihr Problem ist. Genormt sind nur direkte und zerstörende Verfahren, die zwar teils hochgenau, aber doch nur stichprobenartig Aussagen liefern können. Die anderen, zerstörungsfreien Methoden basieren auf der Änderung feuchteabhängiger physikalischer Materialeigenschaften. Ihre Grundlagen, sowie Vor- und Nachteile werden hier näher dargestellt. T2 - Fachtagung Bauwerksdiagnose 2014 CY - Berlin, Germany DA - 13.02.2014 KW - Feuchtemessung KW - Zerstörungsfreie Prüfung KW - Baustoffe PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-311672 UR - http://www.bauwerksdiagnose2014.de/portals/bwd2014/BB/vortrag%205.pdf UR - http://www.bauwerksdiagnose2014.de/Berichtsband SN - 978-3-940283-56-6 SP - 1 EP - 8 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-31167 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lexow, Jürgen T1 - Industrial safety - Public demand and an answer of BAM the federal German institute for materials research and testing N2 - Safe industrial operation is expected by the public. It contributes to a clean environment, innovation and prosperity. BAM the Federal German Institute for Materials Research and Testing has its responsibility in further developing safety in technology and chemistry by research, testing and expert advice. The basic reasoning for this activity and examples of current work are provided. Particular attention is given to the unique BAM Test site Technical Safety. Acceptance of fi ndings and transfer of results are based on collaboration and exchange of personal. Modes of cooperation are described. KW - Industrial safety KW - Large test fecility KW - Structural integrity KW - Dangerous substance PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-322519 DO - https://doi.org/10.2478/tvsbses-2014-0010 SN - 1805-3238 VL - 9 IS - 2 SP - 40 EP - 45 PB - VSB - Sborník vedeckých prací Vysoké Skoly Bánské - Technické Univerzity Ostrava CY - Ostrava AN - OPUS4-32251 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kolkoori, Sanjeevareddy A1 - Wrobel, Norma A1 - Deresch, Andreas A1 - Redmer, Bernhard A1 - Ewert, Uwe T1 - Dual high-energy X-ray digital radiography for material discrimination in cargo containers N2 - In this contribution, we present a dual high-energy X-ray imaging technique for cargo container inspection using the 'spectral high-energy X-ray attenuation method'. This method is based on attenuation of continuous highenergy spectra. The developed experimental technique consists of a betatron as high-energy (up to 7.5 MeV) X-ray source and a matrix detector with high spatial resolution (400 ìm) for digital X-ray imaging. In order to evaluate the material discrimination capability using dual high-energy X-ray imaging, a test specimen is proposed, comprising step wedges of different low and high atomic number (Z) materials. The selected X-ray spectra for the dual-energy experiments correspond to 3 MV and 7.5 MV acceleration potential of the betatron. We evaluated the ratio between low- and high-energy X-ray attenuation coefficients quantitatively based on simulated poly-energetic high-energy X-ray source spectra and the detector sensitivity using the 'analytical Radiographic Testing inspection simulation tool' (aRTist) developed at BAM. The simulated effective attenuation coefficients are compared with corresponding experimental results in order to establish a method for identification of low- and high-Z materials in the container. Finally, important applications of the proposed technique in the context of aviation security are discussed. T2 - ECNDT 2014 - 11th European conference on non-destructive testing CY - Prague, Czech Republic DA - 06.10.2014 KW - Digital radiography KW - NDT KW - High-energy X-ray imaging KW - Betatron KW - Digital detector array (DDA) KW - Container inspection KW - Material discrimination KW - Effective attenuation coefficient PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-322394 UR - https://www.ndt.net/?id=16430 SN - 1435-4934 VL - 19 IS - 12 SP - 1 EP - 10 PB - NDT.net CY - Kirchwald AN - OPUS4-32239 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wrobel, Norma A1 - Kolkoori, Sanjeevareddy A1 - Zscherpel, Uwe A1 - Ewert, Uwe T1 - Innovative X-ray backscatter technique for security applications: Detection of dangerous materials N2 - Radiological inspections, in general, are NDT&E methods to detect the bulk of explosives without invasion into the object of analysis. In contrast to personal luggage, cargo or structural components constitute a complexity that may significantly hamper the detection of a threat by conventional transmission radiography. A novel approach of interrogating a large object to a certain depth only with a single sided access will be presented. It consists of an X-ray backscatter camera with a special twisted slit collimator for imaging backscattered objects. The new X-ray backscatter camera is not only imaging the objects due to their densities but also by taking into account the influences of surrounding objects. Additionally, it does not only image illuminated features but also depicts shadows from absorbing materials. This is a unique characteristic of the developed X-ray backscatter camera. Experimental mock-ups are conducted imitating container with threats among a complex packing as they may be encountered in reality. At the end, the significant advantages of the presented X-ray backscatter camera in the context of aviation and port security will be discussed. T2 - ECNDT 2014 - 11th European conference on non-destructive testing CY - Prague, Czech Republic DA - 06.10.2014 KW - Radiography KW - X-ray backscatter imaging KW - Irradiation geometry KW - Detection of dangerous materials KW - Security applications PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-322429 UR - https://www.ndt.net/?id=16432 SN - 1435-4934 VL - 19 IS - 12 SP - 1 EP - 8 PB - NDT.net CY - Kirchwald AN - OPUS4-32242 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kolkoori, Sanjeevareddy A1 - Wrobel, Norma A1 - Zscherpel, Uwe A1 - Ewert, Uwe T1 - New X-ray backscatter imaging technique for nondestructive testing of aerospace components N2 - Critical parts in aircraft manufacturing such as stringers are very commonly used in modern aircraft structures to resist the compressive loads caused by the aerodynamic effects. They are generally made-up of thin aluminium (Al) metal sheets and are one of the key components in the aircraft wings. Any defects in the stringer leads to weakening of the stiffness of the whole wing structure and consequently, failures may occur. Hence, the structural integrity of the stringers should be evaluated using reliable non-destructive testing (NDT) methods. Due to the complex shaped structure of the stringer, the one-sided access NDT method such as X-ray backscatter technique is more preferable for the non-destructive imaging. In this paper, we present a new X-ray backscatter technique to image the internal sections of the stringer with only a single-sided access. The whole object was inspected by changing the viewing direction of the X-ray backscatter camera. For the first time, the X-ray backscatter measurements were conducted using high-energy (> 0.5MeV) X-rays and proved the applicability of the present technique to inspect thick carbon-fiber laminated components. In order to improve the inspection time and image quality of the backscatter image, we used high-resolution (180ìm) digital detector arrays (DDAs). At the end, important applications of the presented X-ray backscatter technique to the aerospace industry are discussed. T2 - ECNDT 2014 - 11th European conference on non-destructive testing CY - Prague, Czech Republic DA - 06.10.2014 KW - X-ray backscatter imaging KW - Twisted-slit collimator KW - NDT KW - Digital detector array (DDA) KW - Stringer KW - Aerospace applications PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-322376 UR - https://www.ndt.net/?id=16431 SN - 1435-4934 VL - 19 IS - 12 SP - 1 EP - 8 PB - NDT.net CY - Kirchwald AN - OPUS4-32237 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kind, Thomas T1 - Ortung von Spanngliedern zum schadensfreien Bohren im Rahmen von Ertüchtigungsmaßnahmen N2 - Am Beispiel der Ertüchtigung einer Brücke in Bremen wird gezeigt, wie mit den zerstörungsfreien Prüfverfahren (ZfP) Radar- und Ultraschall die genau Lage vorgespannte Bewehrung gefunden bzw. bestätigt werden kann. Im Rahmen von Ertüchtigungsmaßnahmen an Spannbetonbrücken werden häufig Kernbohrungen durchgeführt, die die vorhandenen Spannbewehrungen nicht beschädigen dürfen. Es wird die Vorgehensweise beschrieben, wie mit ZfP ein wesentlicher Beitrag geleistet wird, das Risiko einer Beschädigung zu minimieren und somit eine bessere Planungssicherheit für die Ertüchtigungsmaßnahmen zu schaffen. Dabei werden auch die Grenzen der beiden Verfahren aufgezeigt. T2 - Fachtagung Bauwerksdiagnose 2012 - Praktische Anwendungen zerstörungsfreier Prüfungen und Zukunftsaufgaben CY - Berlin, Germany DA - 23.02.2012 KW - Radar KW - Zerstörungsfreie Prüfung KW - Stahlbeton KW - Ultraschall PY - 2012 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-398225 SN - 978-3-940283-40-5 VL - 134 (Vortrag 11) SP - 1 EP - 7 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin, Germany AN - OPUS4-39822 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maierhofer, Christiane A1 - Ziegler, Mathias A1 - Kunert, M. A1 - Goldammer, M. T1 - Entwicklung von Referenzprobekörpern für die Standardisierung der Blitzthermografie N2 - Die aktive Thermografie wird in der Industrie zunehmend in verschiedenen Bereichen zur Qualitätssicherung, Zustandsdiagnose und Zustandsüberwachung eingesetzt. Bestehende Normen zur Thermografie beschreiben die Grundlagen, Geräte und Begriffe. In diesem Beitrag wird über ein Projekt berichtet, dessen Ziel die Erarbeitung einer Prüfnorm zur Blitzthermografie ist. Diese sollte neben der Auswahl geeigneter Gerätekomponenten, der Auswertungsverfahren und der Vorgehensweise bei der Prüfung auch die Beschreibung geeigneter Referenzprobekörper enthalten, die eine Bewertung der Messapparatur und eine Qualitätssicherung der Prüfung ermöglichen. T2 - Thermographie-Kolloquium 2011 CY - Stuttgart, Germany DA - 29.09.2011 KW - Aktive Thermografie KW - Blitzanregung KW - Prüfnorm KW - Referenzprobekörper PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-246230 SN - 978-3-940283-36-8 VL - 130 SP - 1 EP - 7 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-24623 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Illerhaus, Bernhard A1 - Badde, Aurelia A1 - Michaelis, Matthias A1 - Berger, U. A1 - Onel, Yener A1 - Meinel, Dietmar A1 - Goebbels, Jürgen T1 - Einsatz von mobilen Röntgenuntersuchungsmethoden im Museum - Zwei Fallbeispiele N2 - Zwei Bildhauermodelle aus dem Georg-Kolbe-Museum Berlin standen zur Restaurierung an. Das kleinere, 'Lucino' (1920), 41cm, wurde hochauflösend mit CT gemessen, da mittels CT sowohl der Herstellungsprozeß einer Gipsstatue als auch der innere Zustand, wie Ergänzungen, Klebungen und Armierungen, festgestellt werden können. Aus den CT Bildern ergab sich eine für die vorher vermutete Gipszusammensetzung ungewöhnliche innere Struktur. Mit einer Freihand bedienten Röntgenpistole zur Messung der Röntgenfluoreszenz wurde daraufhin die Zusammensetzung des Materials der Statuette als Terracotta bestimmt. Durch den Einsatz von Helium als Spülmittel konnten auch leichte Materialien nachgewiesen und so eine Unterscheidung zwischen Gips und gebranntem Ton durchgeführt werden. Aus den CT Daten wurde eine virtuelle Darstellung der äußeren Geometrie gewonnen. Ein damit versuchsweise erstelltes Replik (Rapid Prototyping, 3D-Drucker, TU-Berlin) entsprach nicht den Anforderungen des Museums zur Erstellung einer Gußform für eine Bronzekleinserie der Statuette. Die zweite Statue, die 'Große Nacht' (1930) ist mit ihrer Größe von 2,12m und aufgrund des durch korrodierende Metallarmierung verursachten Schadensbildes nicht mehr transportfähig. Eine in-situ Untersuchung mit dem mobilen Tomographen, der in den 1980ern zur Untersuchung von Bäumen gebaut und jetzt mit einem modernen Flachdetektor und einer Röntgenröhre ausgestattet ist, wird vorgestellt. Die Möglichkeiten acder in-situ CT für große Skulpturen werden anhand der Ergebnisse diskutiert. T2 - DGZfP-Jahrestagung 2010 CY - Erfurt, Deutschland DA - 10.05.2010 KW - Mobile CT KW - Mobile RFA PY - 2010 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-246956 UR - https://www.ndt.net/?id=10149 SN - 978-3-940283-26-9 VL - 122 SP - 1 EP - 8 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-24695 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dey, Anika A1 - Casperson, Ralf A1 - Pohl, Rainer A1 - Thomas, Hans-Martin T1 - Die Wirbelstromprüfung als Hilfsmittel für die Schieneninstandhaltung N2 - Die zerstörungsfreie Oberflächenprüfung an verlegten Eisenbahnschienen mit Wirbelstrom hat in den letzten Jahren durch ständige Weiterentwicklung und Verifizierung enorm an Bedeutung gewonnen. Es wurde u.a. angestrebt zuverlässige Planungsgrößen für den Einsatz von Instandhaltungsmaßnahmen zu erhalten, durch deren gezielten Einsatz Risswachstum unterbunden werden kann. Die Ursache für das Wachstum von Rissen in der Schiene liegt in der Materialermüdung des Werkstoffes infolge der Betriebsbelastungen im RadSchiene-Kontakt. Nach einer gewissen Beanspruchungsdauer kommt es an den Kontaktflächen der Fahrkante zu einer Kaltverfestigung des Schienenstahls. Durch fortschreitende Verfestigung des kontaktbeanspruchten Oberflächenbereichs der gehärteten Schicht wird der Werkstoff spröde und es bilden sich feine Risse aus. Die Risse wachsen anfangs unter einem flachen Winkel in das Schieneninnere hinein, neigen dann aber ab einem gewissen Stadium dazu in das Innere des Schienenkopfes abzukippen, was im Extremfall zu einem Schienenbruch führen kann. Diese Rollkontaktermüdungsrisse, auch genannt Head Checks, entstehen bevorzugt in der Fahrkante von bogenäußeren Schienen. Die Anwendung der Wirbelstromprüfung an der Schiene wurde bisher zur Ermittlung der Schädigungstiefe dieser Rollkontaktermüdungsrisse eingesetzt. Das Wirbelstromverfahren besitzt die Eigenschaft, sehr empfindlich auf alle Veränderungen der Materialeigenschaften an der Oberfläche zu reagieren. Daher wurde festgestellt, dass sich neben der Detektion von Rissen auch Fehler wie Eindrückungen oder Schlupfwellen, bis hin zu Materialveränderungen durch Schweißen oder Aufhärtungen in der Schienenoberfläche bestimmen lassen. Die Wirbelstromprüfung besitzt daher das Potenzial, mögliche Orte der Entstehung von Ermüdungsrissen in einem extrem frühzeitigen Stadium nachzuweisen. Ziel ist es, die rissgefährdeten Zonen schon im Zustand der Kaltverfestigung zu identifizieren. Dadurch können sich neue Aspekte für die präventive Schieneninstandhaltung ergeben. T2 - DGZfP-Jahrestagung 2010 - Zerstörungsfreie Materialprüfung ZfP in Forschung, Entwicklung und Anwendung CY - Erfurt, Germany DA - 10.05.2010 PY - 2010 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-214813 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-21481 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gaal, Mate A1 - Caldeira, Rui A1 - Bartusch, Jürgen A1 - Kupnik, M. T1 - Air-coupled ultrasonic ferroelectret receiver with additional DC voltage N2 - Highly sensitive air-coupled ultrasonic sensors are essential for various applications such as testing of composite materials. One of the major challenges for the development of air-coupled ultrasonic sensors is the impedance matching to air. With a lower acoustic impedance than the usual piezoelectric materials, charged cellular polypropylene film (cPP) offers better matching to air with a similar piezoelectric coefficient. The piezoelectric behaviour demonstrated by cPP comes from polarized air cells that create a permanent internal voltage. The sensitivity of the sensor varies with the application of an additional DC bias voltage. Thus, this work presents a cPP ultrasonic sensor with an improvement of up to 15 ± 1 dB on the signal-to-noise ratio. T2 - Eurosensors 2017 CY - Paris, France DA - 3.9.2017 KW - Ultrasonic KW - Air-coupled KW - Cellular polypropylene KW - Transducer KW - Ferroelectret PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-419009 DO - https://doi.org/10.3390/proceedings1040362 VL - 1 IS - 4 SP - Article 362, 1 EP - 4 AN - OPUS4-41900 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kruschwitz, Sabine A1 - Bischof, Eik A1 - Taffe, A. T1 - Multi-sensor investigation of concrete moisture using ultrasound, radar and microwave N2 - Moisture and salt loads of concrete can significantly change its microstructure and consequently lead to chemical and mechanical degradation. However, the non-destructive investigation of moisture and salt present in concrete is still difficult. In order to address and compare the sensitivity of different methods concrete samples with different pore systems realized by varying the w/z ratios have been fabricated. The focus of this study was put on the analysis of ultrasonic long and trans waves measured on the surface and in transmission mode. The results show clear dependencies of all applied methods. With the radar and microwave methods predominantly changes in the concrete moisture could be detected, whereas the different pore systems were not observed to alter the signals. In contrast for the ultrasound method also the ongoing hydration as well as the nature of the pore system strongly influenced the signals. As a consequence in a subsequent drying experiment it was also tried to delineate the effects of moisture and hydration. All specimens have been re-saturated under pressure and the drying experiment was repeated using the same multi-sensor approach. T2 - NDT-CE 2015 - International symposium non-destructive testing in civil engineering CY - Berlin, Germany DA - 15.09.2015 KW - Concrete KW - Moisture KW - Non-destructive testing KW - Ultrasound KW - Radar KW - Velocities KW - Microwave KW - Multi-sensor approach PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-347612 UR - http://www.ndt.net/?id=18322 SN - 1435-4934 VL - 20 IS - 11 SP - 1 EP - 4 PB - NDT.net CY - Kirchwald AN - OPUS4-34761 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kruschwitz, Sabine A1 - Feldmann, Rüdiger T1 - Comparison of non-destructive moisture measurement methods on cement and calcium sulphate based screed samples N2 - Measuring the moisture content of floor screeds is usually done with minor destructive testing methods like Darr drying or the Calcium Carbid (CM) method. These require small samples, deliver only punctual information and still have proven not to be very reliable. Hence, a study has been made using the standard destructive tests as well as a suite of non-destructive testing methods working out their use for moisture determination. In this study five partners from research institutes and industry worked together and intensively researched different technologies. The main focus was put on the varying sensitivity of the measuring techniques in different moisture ranges. Especially for low moisture contents ( or ‘critical’ moisture contents when the screed is dry enough to be covered with the final floor finish), several commercial devices including the most commonly used CM-method failed to determine the correct moisture content for cementitious samples. Hence the need for more accurate, if possible non-destructive methods is high, taking also into account that the chemistry (and physical properties) of screeds may vary strongly depending on their origin and purpose. T2 - NDT-CE 2015 - International symposium non-destructive testing in civil engineering CY - Berlin, Germany DA - 15.09.2015 KW - Screed KW - Moisture KW - Non-destructive testing KW - Radar KW - Capacitive methods KW - Resistivity KW - Multi-sensor KW - Electrics KW - Monitoring PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-347602 UR - http://www.ndt.net/?id=18368 SN - 1435-4934 VL - 20 IS - 11 SP - 1 EP - 4 PB - NDT.net CY - Kirchwald AN - OPUS4-34760 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Prager, Jens A1 - Boehm, Rainer A1 - Höhne, Christian T1 - SAFT-Rekonstruktion für die Querfehlerprüfung in austenitischen Schweißnähten und Mischnähten N2 - Die Untersuchung austenitischer Schweißnähte ist eine Herausforde-rung für die zerstörungsfreie Prüfung mit Ultraschall, bei der die Anwendung her-kömmlicher Prüftechniken häufig keine zufriedenstellenden Ergebnisse liefert. Die Ursache dafür ist das inhomogen-anisotrope Gefüge im Schweißnahtbereich, das zu einer Verzerrung des Schallfeldes und damit zu Schwierigkeiten bei der Auffindbarkeit und bei der Größenbestimmung von Fehlern führt. Eine neue Her-ausforderung ist die Detektion von Querfehlern in Rohrleitungen des Primärkreises von Kernkraftwerken, aber auch in längsnahtgeschweißten, plattierten Rohrleitun-gen, die zunehmend an Bedeutung gewinnt. Dabei können die Prüfköpfe auf Grund einer unbeschliffenen Decklage meist nicht direkt auf die Naht aufgesetzt werden. Vielmehr muss eine SE-Anordnung der Köpfe verwendet werden, bei der durch die längeren Schallwege der negative Einfluss des austenitischen Gefüges noch ver-stärkt wird. Im vorliegenden Beitrag wird eine RT-SAFT-Prüftechnik vorgeschlagen, mit der die Fehlerdetektion deutlich verbessert werden konnte. Dabei wurde die SAFT-Rekonstruktion mit einem Ray-Tracing-Ansatz zur Bestimmung der Schalllaufwege und -laufzeiten und mit einem Schweißnahtmodell kombiniert. Das Schweißnaht-modell repräsentiert die Kornorientierung und die elastischen Konstanten in einer diskretisierten Form und macht so die komplexe Nahtstruktur für die Berechnung zugänglich. Die Aufnahme der Messdaten erfolgt mit zwei Gruppenstrahlerprüfköpfen in V-Anordnung, die beidseitig der Schweißnaht geführt werden sind. Im Beitrag werden die Prüfanordnung und das Rekonstruktionsverfahren vor-gestellt und die Ergebnisse von experimentellen Untersuchungen an austenitischen Schweißnähten und Mischnähten mit künstlich eingebrachten Testfehlern präsen-tiert. Die Ergebnisse der direkten Fehlergrößen- und -lagebestimmung werden mit den Resultaten konventioneller Prüftechniken verglichen. T2 - Seminar des Fachausschusses Ultraschallprüfung CY - Berlin, Germany DA - 11.11.2013 KW - Ultraschallprüfung KW - SAFT KW - Austenitische Schweißnähte PY - 2013 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-295838 IS - Vortrag 15 SP - 1 EP - 9 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) AN - OPUS4-29583 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niederleithinger, Ernst T1 - Neue Ideen für die zerstörungsfreie Prüfung von Beton: Seismische Interferometrie und mehr N2 - Ultraschallverfahren haben sich im Bauwesen in den letzten Jahren immer mehr in der Praxis etabliert. Echomessungen zur Geometriebestimmung sind Stand der Technik. In der Wissenschaft gibt es zahlreiche Ideen, die Messmethodik und die Auswertung weiter zu verbessern sowie den Einsatzbereich zu erweitern. Erste eingebettete Ultraschallsysteme zum Langzeitmonitoring sind installiert, Mehrkanalgeräte ermöglichen immer größere Aperturen und Eindringtiefen, verbesserte Abbildungsverfahren zeigen immer mehr Details. Zusätzlich lassen sich Verfahren aus der Geophysik adaptieren, die weiteren Fortschritt versprechen. Die Seismische Interferometrie dient klassisch dazu, Materialeigenschaften des Erduntergrundes mittels seismischer Wellen zu bestimmen. Derzeitige Anwendungsbereiche sind die Verbesserung seismischer Abbildungsverfahren, Interpolation seismischer Spuren (A-Scans), Bestimmung von Quellparametern oder die Eliminierung unerwünschter Signale in passiven und aktiven Experimenten, hauptsächlich durch Kreuzkorrelation und Bestimmung Greenscher Funktionen. Diese Techniken können auch auf Ultraschalldaten, die an Betonkonstruktionen erfasst wurden, angewendet werden. Moderne Abbildungsverfahren benötigen eine möglichst hohe A-Scan-Dichte und eine genaue Kenntnis des Quellsignals. Beides ist nicht unbedingt gegeben, z. B. wegen der physischen Größe der Sensoren und wechselnder Ankopplungsbedingungen. In simulierten und realen Experimenten wurden interferometrische Methoden zur Lösung dieser Aufgabenstellungen evaluiert. Es zeigt sich, dass fehlende A-Scans kinematisch korrekt interpoliert werden können, wenn ausreichend viele Sender- und Empfängerpositionen genutzt wurden. Amplituden und Signalform sind verändert, können aber durch adaptive Filterung angepasst werden. Die Quellsignalform kann mit hoher Genauigkeit rekonstruiert werden. Die Ergebnisse können potentiell zu einer Verbesserung der Abbildung des Inneren der untersuchten Objekte genutzt werden. T2 - DGZfP-Jahrestagung 2014 CY - Potsdam, Germany DA - 26.05.2014 KW - Zerstörungsfreie Prüfung KW - Geophysik PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-337967 UR - http://www.ndt.net/article/dgzfp2014/papers/di1c1.pdf SN - 978-3-940283-61-0 IS - DGZfP-BB 148 SP - Di.1.C.1, 1 EP - 8 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-33796 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krause, Martin A1 - Mauke, R. A1 - Effner, Ute A1 - Milmann, Boris A1 - Völker, Christoph A1 - Wiggenhauser, Herbert T1 - Ultrasonic testing of a sealing construction made of salt concrete in an underground disposal facility for radioactive waste N2 - For the closure of radioactive waste disposal facilities engineered barriers- so called “drift seals” are used. The purpose of these barriers is to constrain the possible infiltration of brine and to prevent the migration of radionuclides into the biosphere. In a rock salt mine a large scale in-situ experiment of a sealing construction made of salt concrete was set up to prove the technical feasibility and operability of such barriers. In order to investigate the integrity of this structure, non-destructive ultrasonic measurements were carried out. Therefore two different methods were applied at the front side of the test-barrier: 1 Reflection measurements from boreholes 2 Ultrasonic imaging by means of scanning ultrasonic echo methods This extended abstract is a short version of an article to be published in a special edition of ASCE Journal that will briefly describe the sealing construction, the application of the non-destructive ultrasonic measurement methods and their adaptation to the onsite conditions -as well as parts of the obtained results. From this a concept for the systematic investigation of possible contribution of ultrasonic methods for quality assurance of sealing structures may be deduced. T2 - NDT-CE 2015 - International symposium non-destructive testing in civil engineering CY - Berlin, Germany DA - 2015-09-15 KW - Ultrasonic reflection measurement KW - Dry contact transducers in boreholes KW - Interface salt-concrete / rock salt KW - Ultrasonic imaging of internal reflectors PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-346203 UR - http://www.ndt.net/?id=18304 SN - 1435-4934 VL - 20 IS - 11 SP - 1 EP - 4 PB - NDT.net CY - Kirchwald AN - OPUS4-34620 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Grothe, Sven T1 - Ultrasonic signal evaluation used to detect temperature changes in a concrete specimen caused by a heating system N2 - Ultrasonic measurement evaluation methods have been proven to be effective for detection of subtle changes, caused by temperature, load or moisture. To detect and localize temperature changes, a concrete block of 4 × 5 × 0.8 m3, including a heating cartridge and multiple temperature sensors, has been set up to change the temperature and monitor the temperature distribution in a certain area inside the specimen. An ultrasonic monitoring system with 40 ultrasonic sensors (20 transmitters, 20 receivers, 25 kHz central frequency) has been implemented on the specimen. Data from 400 sensor combinations was collected over the whole period of the experiment in an interval of 30 minutes. Quantitative methods (CodaWave Interferometry and Time of Flight method) were used to evaluate the changes in ultrasonic travel-time caused by the heating period, when the cartridge was active, and the cooling period after turning off the cartridge. Furthermore the travel-time changes from all 400 sensor combinations were used to locate the heating cartridge. T2 - NDT-CE 2015 - International symposium non-destructive testing in civil engineering CY - Berlin, Germany DA - 15.09.2015 PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-346387 UR - http://www.ndt.net/?id=18336 SN - 1435-4934 VL - 20 IS - 11 SP - 1 EP - 4 PB - NDT.net CY - Kirchwald AN - OPUS4-34638 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Schaupp, Thomas A1 - Kannengießer, Thomas A1 - Burger, S. A1 - Zinke, M. A1 - Jüttner, S. T1 - Ermittlung geeigneter Wärmeführungen zur Vermeidung wasserstoffunterstützter Kaltrisse beim Schweißen höherfester Feinkornbaustähle mit modifiziertem Sprühlichtbogen N2 - Um den wachsenden Anforderungen an den stofflichen und konstruktiven Leichtbau sowie den Forderungen nach Ressourceneffizienz Rechnung zu tragen, werden in vielen Industriebranchen zunehmend höherfeste Feinkornbaustähle mit Streckgrenzen ≥ 690 MPa eingesetzt. Allerdings werden mit zunehmender Festigkeit deutlich höhere Anforderungen an deren schweißtechnische Verarbeitung gestellt. Weil gerade die Sensibilität gegenüber einer Degradation der mechanischen Eigenschaften der höherfesten Feinkornbaustähle durch den beim Schweißen aufgenommenen Wasserstoff mit steigender Festigkeit zunimmt, ist auf eine geeignete Wärmeführung zu achten. Für konventionelle MAG-Schweißprozesse liegen bereits Erfahrungen und Regelwerke zur Wärmeführung und entsprechende Wasserstoffgrenzwerte vor. Moderne Invertertechnik ermöglichte die Entwicklung modifizierter Sprühlichtbögen (mod. SLB). Im Vergleich zu konventionellen Lichtbogenprozessen wird ein äußerst kurzer und richtungsstabiler Lichtbogen, eine höhere Abschmelzleistung, ein größerer Kontaktrohrabstand und ein tieferer Einbrand realisiert. Neben den bekannten Vorteilen lassen außerdem reduzierte mögliche Nahtöffnungswinkel einen anderen Lagenaufbau und unterschiedliche Geometrien der einzelnen Schweißraupen erwarten. Jedoch fehlen hierzu Aussagen über den schweißverfahrensspezifisch eingetragenen Wasserstoff und die damit einhergehende Kaltrissgefahr. Hierzu lagen in der Industrie, besonders bei den KMU, kaum Kenntnisse vor und sollten deshalb als Ziel dieses Forschungsprojektes erarbeitet werden. Die vergleichenden Untersuchungen mit konventionellem Übergangslichtbogen und mod. SLB mit angepasster Nahtkonfiguration erfolgten an freischrumpfenden Stumpfstoßverbindungen sowohl mit Massivdraht als auch Metallpulverfülldraht. Zur Durchführung der Untersuchungen wurde eine Methodik entwickelt, die es ermöglicht, im Schweißgut realer Verbindungsschweißungen die Wasserstoffkonzentration reproduzierbar zu bestimmen. Anhand der Analysen konnte gezeigt werden, dass die Schweißprozessparameter die in das Schweißgut eingebrachte Wasserstoffkonzentration in Einlagenschweißungen beeinflussen. Auch beim Mehrlagenschweißen gestaltet sich der Wasserstoffeintrag abhängig von den Schweißprozessparametern und ist auf den unterschiedlichen Lagenaufbau zurückzuführen. Grundsätzlich ist den erarbeiteten Ergebnissen zu entnehmen, dass im Schweißgut von Stumpfstoßverbindungen mit abgesenktem Nahtöffnungswinkel erhöhte mittlere Wasserstoffkonzentrationen existieren. Außerdem beinhalten Schweißgüter aus Metallpulverfülldraht höhere Wasserstoffmengen als Massivdrahtschweißungen. Geeignete Wärmeführungen führten zu einer signifikanten Reduzierung der Wasserstoffkonzentration bei dem Einsatz der Nahtkonfiguration mit abgesenktem Nahtöffnungswinkel. Dabei erwies sich eine Nachwärmprozedur aus der Schweißwärme heraus als zielführend. Die Vorstellung von Zwischenergebnissen in Normungsgremien erfolgten, um mittelfristig vor allem den KMU eine sichere Verarbeitung höherfester Feinkornbaustähle zu ermöglichen. Die dargestellten Ergebnisse stellen einen wichtigen Beitrag zur sicheren Auslegung von Schweißkonstruktionen aus höherfestem Feinkornbaustahl dar und ermöglichen den KMU die technischen und wirtschaftlichen Vorteile der mod. SLB-Prozesse auszunutzen sowie unter Berücksichtigung der wasserstoffunterstützten Kaltrissbildung kostenintensive Nacharbeiten zu reduzieren. KW - Wasserstoff KW - MAG-Schweißen KW - Höherfester Feinkornbaustahl KW - Schweißprozessparameter KW - Wärmeführung KW - Kaltrissprüfung PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-425946 SP - 1 EP - 94 AN - OPUS4-42594 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mähner, D. A1 - Sodeikat, Ch. A1 - Maack, Stefan T1 - ZfPBau-Verfahren an Elementwänden – Fallbeispiele und vergleichende Untersuchungen N2 - Die zerstörungsfreien Prüfverfahren konnten ihre Fähigkeit bei der Untersuchung von Elementwänden in einzelnen Fallstudien erbringen. Aufbauend auf den Kenntnissen aus der Praxis und auf Testreihen im Rahmen von Laboruntersuchungen wurde ein erster Ringversuch geplant und durchgeführt. Im Rahmen dieses Ringversuchs wurden verschiedene Strukturdefekte und Einbauteile in Elementwände eingebaut. Die Messung der Wände erfolgte anschließend durch mehrere Messteams mit unterschiedlichen zerstörungsfreien Prüfverfahren. Zum Einsatz kamen hierbei das Ultraschall-Echo- und das Impact-Echo-Verfahren sowie das Impuls-Radar-Verfahren. Zur Verbesserung der Vergleichbarkeit zwischen den unterschiedlichen Prüfverfahren wurde auf die Elementwände ein einheitliches Messraster aufgebracht. Für eine möglichst objektive Messung der Wände erhielten die Messteams vor den Messungen keine Details zu den Strukturdefekten oder Einbauteilen. Die Prüfaufgabe bestand darin, die Wände mit dem jeweiligen Prüfverfahren zu untersuchen. Anschließend wurden die Ergebnisse der Messteams zentral gesammelt und ausgewertet. Anhand der zentralen Auswertung sollten Aussagen zu den eingebauten Inhomogenitäten ableitet werden. Hierdurch kann zum einen die Leistungsfähigkeit der Prüfverfahren an unterschiedlichsten Inhomogenitäten getestet werden, zum anderen können die Ergebnisse und somit die Prüfverfahren untereinander verglichen werden. Zu diesen in der Praxis immer häufiger vorkommenden Fragestellungen können grundsätzliche Aussagen zum Einsatz von zerstörungsfreien Prüfungen bei Elementwänden gewonnen werden. Über die Ergebnisse dieses Ringversuches wird nachfolgend berichtet. T2 - Fachtagung Bauwerksdiagnose - Praktische Anwendungen Zerstörungsfreier Prüfungen und Zukunftsaufgaben CY - Berlin, Germany DA - 25.02.2016 KW - Beton KW - Zerstörungsfreie Prüfung im Bauwesen KW - Elementwände KW - WU-Bauwerke PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-388331 UR - http://www.bauwerksdiagnose2016.de/Portals/bwd2016/BB/vortrag%2010.pdf SP - 1 EP - 22 PB - Deutsche Gesellschaft für zerstörungsfreie Prüfung e.V. CY - Berlin AN - OPUS4-38833 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maack, Stefan A1 - Holst, R. T1 - Rekonstruktion des Bestandsplans im Zuge der Nachrechnung der Brücke über die Leine bei Schwarmstedt N2 - Der aktuell im Rahmen der Nachrechnungsrichtlinie geforderte Nachweis von Tragfähigkeit, Gebrauchstauglichkeit und Ermüdung der Brückenbauwerke im Bestand der Länder und des Bundes stellt eine enorme Herausforderung dar. Insbesondere bei unvollständigen oder fehlenden Bestandsplänen der Bauwerke sind Maßnahmen erforderlich, um die erforderlichen Informationen zu beschaffen. Ein wirkungsvolles Instrument können hierfür die zerstörungsfreien Prüfverfahren des Bauwesens sein. In dem präsentierten Forschungsprojekt erfolgte die Rekonstruktion eines Bestandsplanes direkt auf die Anforderungen des mit der Nachrechnung beauftragten Ingenieurbüros. Darüber hinaus wurde der Entwurf eines Leitfadens erstellt, der im Falle von unvollständigen oder fehlenden Bestandsplänen die Grundlagen für die Beauftragung und Durchführung der Nachrechnung schafft. T2 - Fachtagung Bauwerksdiagnose 2016 - Praktische Anwendungen Zerstörungsfreier Prüfungen und Zukunftsaufgaben CY - Berlin, Germany DA - 25.02.2016 KW - Zerstörungsfreie Prüfung KW - Nachrechnungsrichtlinie KW - Brücken PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-388355 UR - http://www.bauwerksdiagnose2016.de/Portals/bwd2016/BB/vortrag%206.pdf SP - 1 EP - 14 PB - Deutsche Gesellschaft für zerstörungsfreie Prüfung e.V. CY - Berlin AN - OPUS4-38835 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pirskawetz, Stephan A1 - Hüsken, Götz A1 - Gründer, Klaus-Peter A1 - Kadoke, Daniel ED - Bohse, Jürgen ED - Purschke, Matthias T1 - Analyse der Schadensmechanismen biegebeanspruchter Stahlbetonbalken mittels zerstörungsfreier Prüftechniken N2 - Der durch Kräfte senkrecht zur Stabachse belastete Balken ist eines der Haupttragelemente des Stahlbetonbaus. Biegebalken finden unter anderem Anwendung in Form von Brückenträgern oder Unterzügen. Die bei maximaler Beanspruchung auftretenden Versagensformen unterteilen sich dabei in Biege- und Querkraftversagen (Schubversagen). Ein Versagen des Balkens kann je nach Versagensmechanismus mit oder ohne Vorankündigung erfolgen. Gebräuchliche Bemessungskonzepte der Baupraxis zur Dimensionierung entsprechender Tragelemente zielen auf ein Versagen mit ausreichender Vorankündigung (große Verformungen oder breite Risse) ab, wie es z.B. beim sekundären Biegedruckversagen entsteht. Für die Zustandsüberwachung von Bauwerken (z.B. Brücken) mittels zerstörungsfreier Prüftechniken sind fundierte Kenntnisse zu den bei Biegebeanspruchung auftretenden Schadensmechanismen erforderlich. Im Rahmen eines BAM-internen Projektes sollen durch praxisnahe Untersuchungen an einer brückenähnlichen Referenzstruktur unterschiedliche auf das Tragwerk einwirkende thermische und mechanische Belastungen untersucht werden und in die Entwicklung eines Monitoringsystems einfließen. Anhand der aus Biegeversuchen vorliegenden Ergebnisse wird der Einsatz unterschiedlicher Methoden der zerstörungsfreien Materialprüfung gezeigt und deren Anwendbarkeit für die Analyse des Verformungsverhaltens von Stahlbetonbalken diskutiert. Hierzu wurde das Verformungsverhalten eines Stahlbetonbalkens (L = 2,75 m) in einem Vierpunkt-Biegeversuch im Labormaßstab untersucht. Das Hauptaugenmerk liegt dabei auf der Charakterisierung der ausschlaggebenden Versagensmodi durch die einzelnen zerstörungsfreien Prüfverfahren und der Vergleich zu klassischen Messmethoden (z.B. Verformungsmessung mittels induktiver Wegaufnehmer (IWA)). Die Biegeversuche wurden dazu durch Schallemissionsanalyse (SEA) und optische Verformungsanalyse mittels Stereo-Fotogrammetrie (SF) und Bildkorrelationsverfahren (BKV) begleitet. T2 - 21. Kolloquium Schallemission CY - Fulda, Germany DA - 09.03.2017 KW - Optische Verformungsanalyse KW - Rissbildung KW - Schallemission KW - Stahlbeton KW - Tragverhalten bei Biegebeanspruchung PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-393617 SN - 978-3-940283-82-5 VL - 59 SP - 1 EP - 10 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-39361 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Maack, Stefan A1 - Kneib, G. T1 - Elastic wave propagation of ultrasound in bituminous road surfaces - simulations and measurements N2 - Maintenance costs of road infrastructure are increasing steadily. The main cause of this is the nearly exponential increase of traffic during the last decades. Adverse environmental impacts on infrastructure get more and more important as well. Therefore, it is important to determine how limited financial resources can be directed with an optimum pay-out. Often a decision has to be made whether existing structures have to be rebuilt or repaired based on the condition of the structures. The present study takes first steps towards the usage of low-frequency ultrasound as a tool to evaluate the road condition. The overall aim is to derive a prediction model for future road conditions. In order to better understand and interpret recorded wave fields simulations of elastic wave propagation in layered and scattering road models have been performed. The study combined investigations in the laboratory with field measurements. In a series of extensive laboratory tests with different asphalt mixtures characteristic wave properties have been derived. Travel time (resp. velocity) as important material parameter has been investigated for different wave types, different centre frequencies and at various temperatures. An investigation of the directivity of wave radiation in the heterogeneous asphalt bodies led to an estimate of the related disturbing influences. Based on the laboratory results field measurements were performed on a real road and the records were processed to identify layers, propagation speeds and attenuation. The results were verified by a series of simulations. T2 - NDT-CE 2015 - International symposium non-destructive testing in civil engineering CY - Berlin, Germany DA - 15.09.2015 KW - Bituminous material KW - Road inspection KW - Elastic waves KW - Ultrasound KW - Non-destructive testing PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-345364 UR - https://www.ndt.net/?id=18421 SN - 1435-4934 VL - 20 IS - 11 SP - 1 EP - 9 PB - NDT.net CY - Kirchwald AN - OPUS4-34536 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Maack, Stefan A1 - Thunell, B. A1 - Wiggenhauser, Herbert T1 - Study of special challenges for NDT-methods on nuclear structures N2 - The special design of buildings, constructed for nuclear power plants is a particular challenge for the nondestructive testing in the building industry. In particular the major component thicknesses, the degree of reinforcement and surface coating systems make the application of NDT methods difficult. The studies first steps were undertaken to determine to which extent established applications of these techniques are useable in the field of infrastructure buildings. Methods have been evaluated that are already state of the art. So for example the ground penetrating radar was used for locating metallic mounting parts. Furthermore, the low-lying internal structure of the containment was investigated with the ultrasonic method. T2 - NDT-CE 2015 - International symposium non-destructive testing in civil engineering CY - Berlin, Germany DA - 15.09.2015 KW - Non-destructive testing KW - Ground penetrating radar KW - Ultrasonic KW - Nuclear structures KW - Pulse echo technique PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-345330 UR - http://www.ndt.net/?id=18422 SN - 1435-4934 VL - 20 IS - 11 SP - 1 EP - 4 PB - NDT.net CY - Kirchwald AN - OPUS4-34533 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zoёga, Andreas A1 - Kurz, J. H. A1 - Oelschlägel, T. A1 - Rohrschneider, A. A1 - Müller, Christina A1 - Pavlovic, Mato A1 - Hintze, H. A1 - Kanzler, D. T1 - Investigations to introduce the probability of detection method for ultrasonic inspection of hollow axles at Deutsche Bahn N2 - Currently at Deutsche Bahn (DB) ultrasonic inspections in maintenance procedures for wheelset axles with a bore hole are, to the greatest possible extent, carried out using automated ultrasonic inspection system. Although the acceptance levels are in accordance with DIN 27201 part 7, the testing results have shown in recent years that in the case of true indications, the effective defect sizes were far below the level of acceptance. Due to this experience it can be assumed that the automated ultrasonic inspection systems are testing substantially more sensitively than required. This increased sensitivity leads to an increase in false indications, generally resulting in the unnecessary demounting of wheelsets. In Research cooperation between Federal Institute for Materials Research and Testing (BAM) and DB the effective flaw detection sensitivity of existing automated ultrasonic inspection system will be determined and the true/false indication ratio optimised. Through systematic investigations with the Probability of Detection method on the existing automated ultrasonic inspection system the results could be directly applied to the optimisation of existing ultrasonic inspections of wheelset axles with a bore hole in maintenance procedures and the level of reliability can be considerably increased. T2 - 19th World Conference on Non-Destructive Testing CY - München, Germany DA - 13.06.2016 KW - NDT KW - Reliability KW - POD KW - Railway KW - Axles KW - UT PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-375813 UR - http://www.ndt.net/article/wcndt2016/papers/we2g4.pdf SP - id 19515, 1 EP - 8 AN - OPUS4-37581 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Trappe, Volker A1 - Müller, Alexander A1 - Hickmann, Stefan T1 - Infinite life of CFRP evaluated non-destructively with X-ray-refraction topography in-situ mechanical loading N2 - Carbon Fibre Reinforced Plastics (CFRP) are more and more used in modern civil aircrafts. These days the whole fuselage is made of this material (B787; A350). Due to strict certification standards the normal in-service loading gives a low stress level compared to the static and even the fatigue strength of the material. Hence CFRP are assumed to have an infinite life. To evaluate this assumption, fatigue tests on CFRP-specimens were performed up to 108 load cycles and the first inter-fibre failure was evaluated non-destructively by accompanying Xray-refraction topography. A tensile testing machine was integrated in a small angle X-ray scattering (SAXS) setup. X-ray refraction topography was performed while the CFRP samples were tensile loaded. This non-destructive technique enables the detection of micro-cracking and inter-fibre failure especially for CFRP. For Glass Fibre Reinforced Plastic (GFRP) X-ray refraction and in-situ loading has already been successfully used. The increase of inner surfaces due to inter fibre failure was measured as a function of the stress state. Fatigue tests were performed at and below the limit of inter-fibre failure strength. State of the art is to assume the failure of the samples under cyclic loading as the fatigue life. Accompanying non-destructive X-ray refraction measurements reflects the damage state and enables to trace its evolution even if the total failure of the specimens does not occur. This investigation technique is of high interest to give the engineer a design value of infinite life which is practically often reached due to knock down factors of certification standards. Finally the infinite life was found for cyclic fatigue loaded CFRP-samples even under high inter fibre transverse and shear loading investigated up to 108 load cycles. T2 - 19th World Conference on Non-Destructive Testing CY - Munich, Germany DA - 13.06.2016 KW - CFRP KW - NDT KW - Fatigue KW - Damage evolution PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-375015 UR - https://www.ndt.net/?id=19360 SN - 978-3-940283-78-8 VL - 2016 SP - 1 EP - 9 PB - DGZFP CY - Berlin AN - OPUS4-37501 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Spranger, Holger A1 - Beckmann, Jörg T1 - THz-SAFT Rekonstruktion von HDPE-Bauteilen N2 - Obwohl THz-TDS-Systeme vielfältige Qualitätsparameter von Dielektrika ermitteln können, ist deren industrielle Nutzung im Bereich der zerstörungsfreien Bauteilprüfung noch nicht anerkannter Stand der Technik. Ein pragmatischer Weg, TDS-Systeme neben traditionellen Prüfverfahren zu etablieren, sind systematische Untersuchungen an Modellbauteilen, mit dem Ziel einer Methodenentwicklung zur zuverlässigen berührungslosen Prüfung von Dielektrika. Anhand von THz-TDS-Messungen an Polyethylen-Testkörpern mit künstlich eingebauten Fehlstellen werden anfänglich die Möglichkeiten der Laufzeitmessung zur Ermittlung von Tiefenlagen von Ungänzen in Testkörpern präsentiert. Im weitern Teil wird gezeigt, wie durch eine veränderte Versuchsdurchführung und Verwendung eines modifizierten SAFT-Rekonstruktions-Algorithmus Tomogramme berechnet werden können, in denen die künstlich eingebrachten Fehlstellen hinsichtlich ihrer Größe und Lage geometrisch richtig dargestellt werden. T2 - 3. Fachseminar des FA MTHz Mikrowellen- und Terahertz-Prüftechnik in der Praxis CY - Würzburg, Germany DA - 05.04.2017 KW - THz KW - THz-SAFT KW - THz-TDS KW - SAFT KW - HDPE PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-396883 SN - 978-3-940283-84-9 VL - 161 SP - 1 EP - 9 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-39688 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ronneteg, U. A1 - Grybäck, T. A1 - Bertovic, Marija A1 - Müller, Christina A1 - Pavlovic, Mato T1 - Safe for 1 million years – NDT matters! N2 - The General Guidance in the Swedish regulations state that the safety assessment for a final repository for spent nuclear fuel should be 1 million years after closure. SKB developed the KBS-3 method, according to which the spent nuclear fuel is protected by three barriers. It is encapsulated in canisters with a diameter of 1 metre and a length of 5 metres. The canister consists of a cast iron insert surrounded by a 5 centimetre thick shell of copper. The canisters are disposed in the bedrock at a depth of about 500 meters surrounded by bentonite clay. In order to assess the safety over this extremely long period, an extensive quality control programme is applied to the canisters before deposit. In this programme, the use of non-destructive testing (NDT) is vital. The safety assessment of the canister in turn places high demands on the coverage, detectability, and reliability of the applied NDT inspections of the canister parts, i.e. cast iron insert, copper base, tube and lid, and the copper friction stir welds (FSW). This paper presents the extensive full-scale inspection development programme that runs at the Canister Laboratory in Oskarshamn (Sweden). In order to fulfil the high demands, phased array ultrasonic inspection techniques are developed using practical trials aided by ultrasonic modelling. The techniques apply, for example, different frequencies, inspection angles, focus depths, and both longitudinal and shear waves. Increased inspection reliability of the FSW is achieved by applying digital X-ray technique using a 9 MeV linear accelerator and a line detector. To complete the coverage, complementary surface inspections methods, i.e. eddy current array, magnetic flux sensor techniques and magnetic particle inspection, are applied. The canister safety assessment was the driving force to include reliability studies during the NDT development. Initially, the technical reliability was considered, resulting in development of advanced POD models (probability of detection). In combination with human factors studies, these models were implemented as tools in the development of the NDT techniques. Human factors studies were also applied to improve the inspection procedures to be more user-friendly enabling reliable inspections. T2 - 19th World Conference on Non-Destructive Testing CY - München, Germany DA - 13.06.2016 KW - NDT KW - Reliability KW - Spent nuclear fuel PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-375785 UR - http://www.ndt.net/article/wcndt2016/papers/we4e4.pdf SP - id 19464, 1 EP - 9 AN - OPUS4-37578 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kanzler, D. A1 - Pavlovic, Mato A1 - Bertovic, Marija T1 - Zukünftige Möglichkeiten und Pflichten der zerstörungsfreien Prüfung N2 - In unserer heutigen Zeit werden die Zwischenräume innerhalb der einzelnen Abteilungen eines Betriebs und zwischen einzelnen nationalen oder globalen Akteuren immer wichtiger: Produzierbarkeit vs. Wirtschaftlichkeit, Fortschritt vs. Nachhaltigkeit. Auch die zerstörungsfreie Prüfung (ZfP) – bisher hauptsächlich als Endkontrolle oder Wartungselement wahrgenommen – kann und sollte im Wandel der Digitalisierung und Industrie 4.0 einen neuen Stellenwert erhalten. Die ZfP kann schon während der Konstruktion helfen, sichere und zuverlässige Produkte zu erstellen. Jedoch müssen dafür eine adäquate Informationskultur und die notwendigen Kennzahlen vorhanden sein. Objektive, probabilistische Kennzahlen (wie die POD - Auffindwahrscheinlichkeit) sind hierbei der Schlüssel. Diese müssen jedoch unbedingt an Prüfverfahren, Prüfgegenstand und Prüfbedingung angepasst werden, da sonst die gesamte Aussage in Frage zu stellen ist. Im Vortrag werden Beispiele aus der Anwendung gezeigt, die die Aussagekraft der Kennzahl aber auch die Sorgfalt, mit denen die einzelnen Aussagen genutzt werden, unterstrichen werden soll. Bewertung von Daten von realen Fehler, Anpassung an die Bruchfestigkeit und die Betrachtung von mehreren Prüfparametern am Beispiel der Bewertung von radiographischen, Ultraschall- und Wirbelstromprüfung werden in dem Vortrag gezeigt. T2 - DGZfP-Jahrestagung 2017 CY - Koblenz, Germany DA - 22.05.2017 KW - Zuverlässigkeit KW - Zerstörungsfreie Prüfung PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-404877 SN - 978-3-940283-85-6 VL - DGZfP-Berichtsband BB 162 SP - 1 EP - 6 AN - OPUS4-40487 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hüllmann, Dino A1 - Kohlhoff, Harald A1 - Neumann, Patrick P. ED - Bársony, I. ED - Zolnai, Z. ED - Battistig, G. T1 - Embedded control of a PMSM servo drive without current measurements N2 - A permanent-magnet synchronous motor (PMSM) servo drive for lightweight robotic platforms that have a high torque demand at low rotational speeds has been developed. First, a current-independent torque controller is derived and cascaded with a speed and position controller, while merely an encoder is used as a sensor device in combination with a speed estimator. Finally, the speed estimator output is compared to gyroscope measurements and the overall functioning is verified on a real system. T2 - 30th Eurosensors Conference - Eurosensors 2016 CY - Budapest, Hungary DA - 04.09.2016 KW - BLDC KW - PMSM KW - Motor control KW - Servo drive KW - Optical incremental encoder PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-388973 DO - https://doi.org/10.1016/j.proeng.2016.11.487 SN - 1877-7058 VL - 168 SP - 1671 EP - 1675 PB - Elsevier B.V. CY - Amsterdam, Netherlands AN - OPUS4-38897 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - McGrath, B. A1 - Holstein, R. A1 - Bertovic, Marija T1 - How NDT companies can benefit from human factors knowledge N2 - Ultrasonic phased array is, currently, the technology which is being applied as the solution to a lot of inspection problems. The perceived benefits are seen to be worth the outlay on equipment and specialised personnel. Yet, there is a source of knowledge, freely available, which can also deliver immediate benefits, through more reliable inspection results, and consequently increased client confidence, but which is largely ignored by the greater part of the NDT community. This talk will review the latest Human Factors knowledge and provide practical illustrations of how companies can use it to improve their competitive edge. T2 - 19th World Conference on Non-Destructive Testing CY - München, Germany DA - 13.06.2016 KW - NDT KW - Reliability KW - Human factors PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-375742 UR - http://www.ndt.net/article/wcndt2016/papers/tu4d3.pdf SP - id 19532, 1 EP - 8 AN - OPUS4-37574 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Douma, J. A1 - Niederleithinger, Ernst A1 - Snieder, R. T1 - Improved focusing using deconvolution within a concrete block N2 - Time reversal techniques are used in ocean acoustics, medical imaging and non-destructive evaluation to backpropagate recorded signals to the source of origin. We demonstrate experimentally a technique which improves the temporal focus achieved at the source location. The experiment consists of propagating a signal from a transducer within a concrete block to a single receiver on the surface, and then applying time reversal or deconvolution to focus the energy back at the source location. The results show that we are able to generate a focus in time at the correct location. The proposed method is simple and proven to be robust. Additionally, its costs are negligible due to deconvolution being a preprocessing step to the recorded data. The technique can be applied for detailed investigation of the source mechanisms (e. g. cracks) but also for monitoring purposes. T2 - DGZfP-Jahrestagung 2014 CY - Potsdam, Germany DA - 26.05.2014 KW - Ultrasonics KW - Acoustic emission KW - Time reversal KW - Deconvolution PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-337953 UR - http://www.ndt.net/article/dgzfp2014/papers/di2c2.pdf SN - 978-3-940283-61-0 IS - DGZfP-BB 148 SP - Di.2.C.2, 1 EP - 8 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-33795 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Unnikrishnakurup, Sreedhar A1 - Myrach, Philipp A1 - Polomski, Benjamin A1 - Le Claire, Elisabeth A1 - Vengara, N. A1 - Balasubramaniam, Krishnan A1 - Ziegler, Mathias T1 - Thermographic crack detection in hot steel surfaces N2 - The detection and characterization of surface cracks in steel specimens prior to damage is a technologically and economically highly significant task and is of utmost importance when it comes to safety-relevant structures. In steel production where steel billets at high temperatures have to be inspected while moving a number of well-established NDT methods cannot be applied. Laser thermography however is a promising candidate to serve as a fast, non-contact and remote tool in this case. We present a study that shows that the crack detection capabilities of laser thermography can be extended also to specimens at high temperature. A combination of inductive and laser heating allows to systematically study the contrast formation as well as the optimization of the important measurement parameters. The experiments are accompanied by FEM simulations that provide a better insight of the physical correlations and support the experimental developments. The aim of these studies is to develop a system with high inspection speed and detection performance to be in-line operated under the hostile environment of steel production lines. T2 - 19th World Conference on Non-Destructive Testing (WCNDT 2016) CY - Munich, Germany DA - 13.06.2016 KW - In-line Monitoring KW - Laser Infrared thermography KW - Cracks KW - Induction heating KW - Steel billets KW - FEM simulation PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-389161 UR - http://ndt.net/?id=19573 SN - 1435-4934 VL - 21 IS - 7 SP - 1 EP - 8 PB - NDT.net CY - Kirchwald AN - OPUS4-38916 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Jonietz, Florian A1 - Ziegler, Mathias A1 - Myrach, Philipp A1 - Suwala, H. A1 - Rethmeier, Michael T1 - Untersuchung von Punktschweißverbindungen mit aktiver Thermografie N2 - Widerstandspunktschweißen ist insbesondere im Automobilbau eine der wichtigsten Fügetechniken. Bislang erfolgt die Qualitätssicherung überwiegend durch stichprobenartige zerstörende Prüfung. Eine zerstörungsfreie Prüftechnik würde neben der Reduzierung der Prüfkosten auch eine Optimierung des Punktschweißverfahrens bedeuten, da prinzipiell jeder Schweißpunkt geprüft werden könnte und somit auch eine Reduzierung der Anzahl der Schweißpunkte möglich ist. Es wird ein Verfahren vorgestellt, bei dem die Punktschweißverbindung zwischen zwei Stahlblechen optisch auf einer Blechseite mittels Laser oder Blitzlicht erwärmt wird. Die aufgeschmolzene Zone, die sogenannte Schweißlinse, stellt dabei neben der mechanischen Verbindung auch eine Wärmebrücke zwischen den beiden verschweißten Blechen dar, die bei diesem Verfahren ausgenutzt wird. Durch den verbesserten thermischen Kontakt zwischen den verschweißten Blechen an der Schweißlinse kontrastiert diese deutlich mit dem umgebenden Blechmaterial, bei dem der Wärmeübertrag zwischen den Blechen vergleichsweise gering ist. Dieser Kontrast im thermischen Verhalten kann mittels zeitabhängiger Thermografie gemessen werden. Durch das hier vorgestellte Verfahren kann mittels aktiver Thermografie sowohl in Transmissions- als auch in Reflexionsanordnung die Größe des thermischen Kontaktes zwischen den beiden Blechen ermittelt werden, welche ein Maß für die Größe der Schweißlinse und damit für die qualitative Güte der Schweißung darstellt. Ein Vorteil des entwickelten Verfahrens ist seine Anwendbarkeit auf Bleche ohne Oberflächenbehandlung. T2 - DACH-Jahrestagung 2015 CY - Salzburg, Austria DA - 11.05.2015 PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-343476 UR - http://www.ndt.net/?id=19068 SN - 1435-4934 VL - 21 IS - 4 SP - 1 EP - 7 PB - NDT.net CY - Kirchwald AN - OPUS4-34347 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Taffe, Alexander A1 - Spies, M. A1 - Recknagel, J. T1 - Schulung zur zuverlässigen Ortung von Bewehrung in Stahlbetonbauteilen von Kraftwerken N2 - In kerntechnischen Anlagen werden Revisionszeiträume genutzt, um unter anderem Anlagenteile nach dem Stand der Technik zu ertüchtigen und um Nachrüstungsmaßnahmen zur Erhöhung der Betriebssicherheit durchzuführen. Solche Anlagenteile werden häufig mittels Dübelplatten befestigt. Die Dübel sind in Stahlbetonbauteile einzubringen, die kraftwerkstypisch mit dichter Bewehrung versehen sind. Zerstörungsfreie Untersuchungen zur genauen Ortung bewehrungsfreier Orte sind hierzu erforderlich. Bei dieser vermeintlich einfachen Prüfaufgabe wurde deutlich, dass in der Praxis Bedarf an verbesserter Anwendungssicherheit der zur Verfügung stehenden ZFP-Verfahren besteht, die eng mit der Ausbildung von Prüfern verbunden ist. Dieser Beitrag berichtet über die bislang im Bereich ZfPBau erstmalig umgesetzte Strategie aus Verfahrensanweisung und Schulung zur zuverlässigen Ortung von Bewehrung an Stahlbetonbauteilen. Sie kann als Muster für weitere ZfPBau-Schulungen zur zuverlässigen Anwendung der Verfahren dienen. T2 - Fachtagung Bauwerksdiagnose 2012 - Praktische Anwendungen zerstörungsfreier Prüfungen und Zukunftsaufgaben CY - Berlin, Germany DA - 23.02.2012 KW - Zerstörungsfreie Prüfung im Bauwesen KW - ZfPBau KW - Ausbildung KW - Bewehrungsortung KW - Bauwerksdiagnose KW - Kernkraftwerk KW - Bauwerksprüfung PY - 2012 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-285909 UR - https://bauwerksdiagnose2012.dgzfp.de/Portals/bwd2012/Dokumente/bb/v04.pdf SN - 978-3-940283-40-5 IS - DGZfP BB 134 SP - 1 EP - 7 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-28590 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Taffe, Alexander A1 - Spies, M. A1 - Recknagel, J. A1 - Rieß, H. T1 - Schulung zur zuverlässigen Ortung von Bewehrung in Stahlbetonbauteilen von Kraftwerken N2 - In kerntechnischen Anlagen werden Revisionszeiträume genutzt, um unter anderem Anlagenteile nach dem Stand der Technik zu ertüchtigen und um Nachrüstungsmaßnahmen zur Erhöhung der Betriebssicherheit durchzuführen. Solche Anlagenteile werden häufig mittels Dübelplatten befestigt. Die Dübel sind in Stahl-betonbauteile einzubringen, die kraftwerkstypisch mit dichter Bewehrung versehen sind. Zerstörungsfreie Untersuchungen zur genauen Ortung bewehrungsfreier Orte sind hierzu erforderlich. Bei dieser vermeintlich einfachen Prüfaufgabe wurde deutlich, dass in der Praxis Bedarf an verbesserter Anwendungssicherheit der zur Verfügung stehenden ZFP-Verfahren besteht, die eng mit der Ausbildung von Prüfern verbunden ist. Dieser Beitrag berichtet über die bislang im Bereich ZfPBau erstmalig umgesetzte Strategie aus Verfahrensanweisung und Schulung zur zuverlässigen Ortung von Bewehrung an Stahlbetonbauteilen. Sie kann als Muster für weitere ZfPBau-Schulungen zur zuverlässigen Anwendung der Verfahren dienen. T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Germany DA - 30.05.2011 KW - Zerstörungsfreie Prüfung im Bauwesen KW - Ausbildung KW - Bewehrungsortung KW - Performance demonstration KW - Blindtest KW - Wirbelstrom KW - Radar PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-253752 UR - https://jt2011.dgzfp.de/Portals/jt2011/BB/di2b1.pdf SN - 978-3-940283-33-7 IS - DGZfP BB 127 SP - 1 EP - 8 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-25375 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kinne, Marko A1 - Farhan, Muhammad A1 - Schneider, Ronald A1 - Thöns, Sebastian T1 - Influence of the structural integrity management on the levelized cost of energy of offshore wind: a parametric sensitivity analysis N2 - The levelized cost of energy (LCoE) is an important measure to quantify the macro-economic efficiency of an offshore wind farm and to enable a quantitative comparison with other types of energy production. The costs of the structural integrity management - which is required to ensure an adequate lifetime reliability of the turbine support structures - are part of the operational expenditures of an offshore wind farm. An optimization of the structural integrity management may reduce the operational expenditures and consequently the LCoE. However, the effect of the structural integrity management on the LCoE is hardly known. To investigate this effect, this paper presents a sensitivity analysis of the LCoE of a generic offshore wind farm. The probabilistic models of the parameters influencing the LCoE are based on a literature study including an explicit model for the structural integrity management. The analysis reveals that LCoE may potentially be reduced if an optimization of the structural integrity management enables a service life extension. T2 - International Probabilistic Workshop 2022 CY - Stellenbosch, South Africa DA - 08.09.2022 KW - Structural integrity management KW - Levelized cost of energy KW - Sensitivity analysis PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-572724 DO - https://doi.org/10.14311/APP.2022.36.0090 VL - 36 SP - 90 EP - 98 PB - Acta Polytechnica CTU Proceedings AN - OPUS4-57272 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Detjens, Marc A1 - Hübert, Thomas A1 - Tiebe, Carlo A1 - Banach, Ulrich T1 - Temperature influence on coulometric trace humidity measurement N2 - Planar coulometric sensors were tested in humidified synthetic air at various gas temperatures. Generated frost point temperature in the gas ranged from -30 °C to -60 °C and were measured by coulometric sensors and in addition by a calibrated dew point hygrometer. The gas temperatures, which were measured by a calibrated Pt100 sensor, were set to -20 °C, 0 °C, 23 °C, 40 °C, 50 °C, and 60 °C during the experiments. Empiric nonlinear functions were calculated between the generated humidity and the sensor signals. In comparison to the measured signals at 23 °C, the sensor signals were lower at the other gas temperatures. The measurements at 60 °C showed indistinct results due to a great signal noise. The response behavior of the sensors was similar at 23 °C, 40 °C and 50 °C. In contrast to that, the sensors reacted slowly at a gas temperature of -20 °C and 0 °C. In summary, with coulometric sensors it was possible to measure continuously trace humidity with an expanded uncertainty below 2 K. T2 - IEEE Sensors 2017 CY - Glasgow, Scotland, UK DA - 30.10.2017 KW - Response behavior KW - Coulometric sensors KW - Trace humidity measurement KW - Temperature influence KW - Chemical reaction PY - 2017 SN - 978-1-5386-4056-2 SP - 1308 EP - 1310 PB - IEEE CY - Piscataway, NJ, USA AN - OPUS4-43241 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holtappels, Kai A1 - Brinkmann, C. A1 - Dietlen, Siegmund A1 - Stickling, J. A1 - Schönbucher, A. T1 - Simulation und experimentelle Bestimmung des Fremdgaseinflusses auf die Stabilitätsgrenzen instabiler Gase am Beispiel von C2H2/Inertgas- und C2H2/Brenngas-Systemen T2 - 5. Fachtagung Anlagen-, Arbeits- und Umweltsicherheit CY - Köthen, Deutschland DA - 2000-11-09 PY - 2000 SP - 369 EP - 376 PB - VDI-Gesellschaft Verfahrenstechnik und Chemieingenieurwesen CY - Düsseldorf AN - OPUS4-1717 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Holtappels, Kai A1 - Schröder, Volkmar A1 - Pasman, H. T1 - Report on the experimentally determined explosion limits, explosion pressures and rates of explosion pressure rise - Part 2: ethane, ethylene, propane, n-butane, ammonia and carbon monoxide; Contract No. EVG1-CT-2002-00072 KW - Explosion limits KW - Explosion pressures KW - Rate of pressure rise KW - Ethane KW - Ethylene KW - Propane KW - N-butane KW - Ammonia KW - Carbon monoxide PY - 2007 UR - http://www.morechemistry.com/SAFEKINEX/deliverables/46.Del.%20No.%209.pdf IS - 9 SP - 1 EP - 55 PB - Bundesanstalt für Materialforschung und -prüfung CY - Berlin AN - OPUS4-15760 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Holtappels, Kai T1 - Impulse zum Hochlauf einer Wasserstoffwirtschaft in Deutschland N2 - Wasserstoff als sauberer, vielseitig einsetzbarer Energieträger spielt bei der dringend benötigten Energiewende eine entscheidende Rolle. Die Etablierung einer Wasserstoffwirtschaft wird tiefgreifende Auswirkungen auf verschiedene Sektoren der deutschen Wirtschaft haben und diese grundlegend transformieren. Die vorliegende Publikation fokussiert Herausforderungen und Maßnahmen für den Hochlauf einer Wasserstoffwirtschaft in Deutschland und ist in einem knapp einjährigen Multi-Stakeholder-Dialog gemeinsam mit führenden Expertinnen und Experten aus Industrie, Wissenschaft, Gesellschaft (NGOs) sowie Vertretern aus der Politik-entstanden. KW - Wasserstoff KW - Markthochlauf KW - Zukunftsdialog KW - Herausforderungen PY - 2025 SN - 978-3-911670-07-4 SP - 1 EP - 62 PB - VDI Verein Deutscher Ingenieure e.V. CY - Düsseldorf AN - OPUS4-63941 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Tiebe, Carlo A1 - Bayat, Mehmet E. A1 - Bartholmai, Matthias T1 - Unsicherheit bei der Probenahme von Sprengstoffspuren und Detektion durch Ionenmobilitätsspektrometrie N2 - IMS trägt zur Luftfrachtsicherheit bei Geltende Luftsicherheitsgesetze verpflichten Luftsicherheitsbehörden, Flughafenbetreiber und Fluggesellschaften umfassende Sicherheitsmaßnahmen auf den Flughäfen zu ergreifen, um die Gefahr möglicher terroristischer Bedrohungen zu erkennen und zu verhindern. Wenn ein verdächtiges Objekt durch Röntgenstrahlen identifiziert wurde, kann die IMS als schnelles Analyseverfahren vor Ort orthogonal zur Radiologie eingesetzt werden, um chemische Informationen über Gefahrstoffe wie Sprengstoffe oder Drogen vor dem Abflug zu erhalten. Vor der Detektion von Sprengstoffen beginnt die Untersuchung eines verdächtigen Objekts mit der Probenahme mittels Wischprobensammlern. Eine Luftsicherheitskontrollkraft wischt dabei Oberflächen des Objekts mit einem Probensammler ab, um Partikel von Gefahrstoffen zu sammeln. Der beladene Probensammler wird anschließend in einen Probeneinlass eingeführt. Nach thermischer Desorption der gesammelten Stoffe erhält der Bediener (z. B. Luftsicherheitskontrollkraft) ein boolesches Ergebnis - "Alarm" oder "Kein Alarm". Verfahren und Ergebnisse In dieser Studie wurden drei Verfahren mit vier ECAC-zertifizierten ETD-Geräten zur Entwicklung eines Unsicherheitskonzeptes bezüglich der Probenahme (PN) angewandt: I) direkte Probenaufnahme durch lösemittelbasierten Auftrag einer bekannten Sprengstoffmenge auf einem Probensammler, II) Auftragung einer bekannten Menge eines gelösten Sprengstoffs auf einem 10 cm × 10 cm Substrat (Aluminium, Papier, Eisen und Polyvinylchlorid) und manuelle PN nach Lösemittelverdampfung, III) lösemittelbasierter Sprengstoffauftrag auf eine PTFE- oder PTFE-beschichtete Glasfaseroberfläche, nach Lösemittelverdunstung trockene Übertragung auf das zu beprobende Substrat zur PN. Nach dem binären Regressionsverfahren wurde die funktionale Abhängigkeit der Detektionswahrscheinlichkeit von einer bekannten Sprengstoffmasse mit einer Logit-Funktion beschrieben: POD=1/(1+e^(-A·(m-B))). Dabei ist POD die Wahrscheinlichkeit der Detektion für eine bekannte Sprengstoff-Masse, die Parameter A (logistische Wachstumsrate der Kurve) und B (m-Wert des Mittelpunktes des Sigmoids) sind geschätzte Parameter nach der Methode der kleinsten Quadrate, und m ist die Sprengstoffmasse. Das entwickelte Messunsicherheitsmodell kombiniert quantitative Ergebnisse aus Wägen, Lösen und Pipettieren sowie qualitative Ergebnisse - "Alarm" oder "Kein Alarm" und die Unsicherheit der PN. Identifizierte Unsicherheitsursachen sind die Durchführung der Wischprobenahme, Staub, Lösemitteleffekte und die Unsicherheit bei der Herstellung von Testlösungen. T2 - 8. IMS-Anwendertreffen CY - Potsdam, Germany DA - Veranstaltung wurde abgesagt - Meeting was cancelled KW - IMS KW - Ionenmobilitätsspektrometrie KW - Wischprobenahme KW - binäres Regressionsverfahren KW - ETD KW - Sprengstoffspurendetektion PY - 2020 VL - 2020 SP - 9 EP - 9 PB - Universität Potsdam CY - Potsdam AN - OPUS4-51136 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine A1 - Gradt, Thomas T1 - Friction and wear characteristics of polymers in gaseous and liquid hydrogen N2 - The tribological characteristics of pure and graphite filled polymers were investigated in gaseous hydrogen at ambient temperatures and in LH2 at -253°C. It could be shown that the tribological properties of PI and PEEK materials is related to the formation of a transfer film. The influence of both hydrogen and cryogenic temperatures will be discussed in the presentation. T2 - 21th International Colloquium Tribology CY - Stuttgart/Ostfildern, Germany DA - 09.11.2018 KW - Friction KW - Wear KW - Hydrogen KW - PEEK PY - 2018 SP - 1 EP - 2 AN - OPUS4-43903 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klein, P. A1 - Friedrich, K. A1 - Theiler, Geraldine A1 - Hübner, Wolfgang T1 - Mechanische und tribologische Eigenschaften von PTFE/PEEK/CF-Verbundwerkstoffen T2 - BAM-Sonderheft 2003 "Polymere Verbundwerkstoffe zwischen Raumtemperatur und 4,2 K" ; 2. Symposium im DFG-Projekt: Eigenschaften von PTFE- und PEEK-Matrix-Werkstoffen bei tribologischer Beanspruchung CY - Berlin, Deutschland DA - 2003-02-27 PY - 2003 SP - 11 EP - 17 AN - OPUS4-2669 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Eberwein, Robert T1 - Untersuchung der Gefährdung von Personen und Bauwerken in Folge des Versagens von LNG-Kraftstoffspeichern für Fahrzeuge in Tunneln N2 - Liquefied Natural Gas (LNG) aus regenerativen Quellen, stellt einen potenziellen Kraftstoff für den Schwer- und Fernverkehr des Straßenverkehrs dar. Gegenüber seinen positiven Eigenschaften zu dem in diesem Verkehrssektor häufig verwendeten Kraftstoff Diesel birgt der Kraftstoff aber auch Gefahren für Personen und Bauwerke durch seine sehr niedrige Temperatur bei der Speicherung von ca. -160 °C und seine Explosionsfähigkeit in der Gas-Phase. In der Arbeit wurde sich mit der Gefährdung von Personen und Bauwerken hinsichtlich der von LNG ausgehenden Gefahren in Tunneln auseinandergesetzt. Tunnel stellen besonders schützenswerte Bauwerke dar, da aus vorhergehenden Störfällen in Tunneln bekannt ist, dass diese mit hohen Personen-, Bauwerks-, und Volkswirtschaftlichen-Schäden einhergehen können. Untersuchungsschwerpunkt bei der Bewertung von Gefährdungen durch LNG stellte eine Ereigniskaskade bestehend aus Freisetzung, Verdampfung, Stoffausbreitung und Zündung des sich gebildeten explosionsfähigen LNG-Gas/Luft-Gemisches dar. Mit dem Ziel eine solche Ereigniskaskade realitätsnah vorhersagen und zukünftig hierzu Risikoanalysen durchführen zu können wurden innerhalb der Arbeit Parameterstudien sowie Kalibrierungen und Validierungen gegenüber experimentellen Untersuchungen durchgeführt. Mit den Modellen wurden in der Arbeit exemplarische Fallbeispiele zu Störfällen untersucht. Ergebnisse dieser waren, dass Gefährdungen insbesondere von flüssigem LNG nach dessen Freisetzung und der Verbrennung von LNG-Gas/Luft-Gemischen ausgingen. N2 - Liquefied Natural Gas (LNG) from regenerative sources is a potential fuel for heavy and long-distance road traffic. In contrast to its positive properties compared to diesel, which is often used in this transport sector, the fuel also contains hazards from its very low storage temperature of approx. -160 °C and its explosiveness in the gas phase for personal and structural safety. The dissertation dealt with the dangers to persons and infrastructures according to the hazards by LNG in tunnels. Tunnels are especiallyworth protecting structures since it is known from previous incidents in tunnels that they can go hand in hand with high damage to the people, the structure, and the economy. The main focus of the investigation into the assessment of hazards from LNG was an event cascade consisting of release, evaporation, dispersion, and ignition of the explosive LNG-vapor/air-mixture formed. To realistically predict such an event cascade and being able to carry out risk analyzes for this purpose in the future, parameter studies such as calibrations and validations were carried out concerning experimental investigations. Exemplary case studies on incidents were examined in the thesis with the validated models. The results of this were that there were especially hazards in particular from liquid LNG after its release and the combustion of LNG-vapor/air-mixtures. KW - Verflüssigtes Erdgas KW - Erneuerbare Energien KW - Numerische Strömungsmechanik KW - Sicherheitstechnik KW - Liquefied Natural Gas KW - LNG KW - Renewable fuels KW - CFD KW - Safety engineering PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-521145 DO - https://doi.org/10.14279/depositonce-11346 SP - 1 EP - 240 PB - TU Berlin CY - Berlin AN - OPUS4-52114 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zeps, Robert A1 - Rosenow, B. A1 - Kluge, Martin A1 - Blanchard, R. A1 - Holtappels, Kai T1 - Druckentlastungsvorgänge in großvolumigen Behältern N2 - Es wurden Druckentlastungsvorgänge in einem 5 m³ Autoklav mit einem L/D-Verhältnis von 1,14 nach der Zündung von Methan-Luft-Gemischen untersucht. Schwerpunkt der Arbeit war die Bestimmung der Explosionsdrücke, der zeitlichen Druckanstiege bzw. der KG-Werte und der reduzierten Explosionsdrücke in Abhängigkeit der Methankonzentration. Im geschlossenen Behälter wurden die Explosionsdrücke und zeitlichen Druckanstiege für Methan-Luft-Gemische mit Methankonzentrationen von 5,9 Vol-% bis 13,5 Vol-% ermittelt. Die Ergebnisse zeigen gute Übereinstimmung mit den Literaturwerten. Weiter wurden Druckentlastungsversuche mit einer kreisrunden Entlastungsfläche von 0,011 m² und einer Druckentlastungsfolie mit einem statischen Ansprechdruck von 1,94 bar durchgeführt. Hierbei wurden Gemische mit Methankonzentrationen von 5,9 Vol-% bis 14,3 Vol-% untersucht. Dabei zeigte sich, dass die vergleichsweise kleine Entlastungsfläche nur dann zu reduzierten Explosionsdrücken gleich dem statischen Ansprechdruck der Berstfolie führte, wenn die Methankonzentration ≤ 5,9 Vol-% oder ≥ 14,0 Vol-% betrug. Bei allen anderen untersuchten Methankonzentrationen führten die durch die Druckentlastung induzierten Turbulenzen zu einer Beschleunigung der Verbrennungsreaktion und zu Explosionsdrücken vergleichbar denen im geschlossenen Behälter. T2 - 14. Kolloquium zur chemischen und physikalischen Sicherheitstechnik (BAM-PTB-Kolloquium) CY - Berlin, Germany DA - 14.06.2016 KW - Druckentlastung KW - Up-Scale KW - Deflagration KW - Sicherheitstechnik PY - 2016 SN - 978-3-9817853-5-7 SN - 0938-5533 VL - 2016 SP - 21 EP - 28 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-37176 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hausberger, A. A1 - Major, Z. A1 - Theiler, Geraldine A1 - Gradt, Thomas A1 - Schwarz, T. T1 - Investigation on the friction and wear behaviour of thermoplastic polyurethanes by controlling the adhesion and deformation part of friction N2 - In this work, unfilled and graphite filled TPU materials were used to investigate the contribution of the adhesion and deformation component of friction. Pin-on-Disc tests were conducted in the air and under vacuum condition by using different surface roughness. T2 - 6. European Conference on Tribology CY - Ljubljana, Slovenia DA - 07.06.2017 KW - TPU KW - Friction KW - Wear KW - Adhesion KW - Deformation KW - Vacuum PY - 2017 SP - 4.02 - 1 EP - 4.02 - 2 AN - OPUS4-40763 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baensch, Franziska A1 - Hofmann, Detlef A1 - Johann, Sergej A1 - Tiebe, Carlo A1 - Basedau, Frank A1 - Sturm, Patrick A1 - Lay, Vera A1 - Niederleithinger, Ernst T1 - Multi-sensor conception for safe sealing structures in underground repositories N2 - The project "SealWasteSafe" of the Bundesanstalt für Materialforschung und -prüfung (BAM, Berlin) deals with sealing structures applied for underground disposal of nuclear waste from two perspectives: (1) material improvement for application in sealing constructions and (2) feasibility study regarding multi-sensor approaches to ensure quality assurance and long-term monitoring. One specimen of 150 l made of alkali-activated material, which was found innovative and suitable for sealing constructions based on preliminary laboratory studies, and, for comparison purpose, another one made of salt concrete, are manufactured with an integrated multi-sensory setup for quality assurance and long-term-monitoring. The specimens were left in their cast form and additionally thermally insulated to simulate the situation in the repository. The multi-sensory concept comprises RFID technology embedded in the specimens suppling material temperature and moisture measurements, integrated fibre optic sensing allowing strain measurement and acoustic emission testing for monitoring possible crack formation. Overall, the suitability and the functionality of the sensors embedded into and attached to strongly alkaline (pH > 13 for the AAM) and salt corrosive (NaCl) environment was proven for the first 672 h. First temperature measurement based on RFID succeeded after 626 h for the alkali-activated material and after 192 h for the conventional salt concrete. Strain measurement based on distributed fibre optic sensing turned out the alkali-activated material with > 1 mm m-1 undergoing approximately twice the compression strain as the salt concrete with strains < 0.5 mm m-1. In contrast, the acoustic emission first and single hits representing crack formation in numbers, was found for alkali-activated material half of that detected at the salt concrete. T2 - SMIRT 26 CY - Berlin/Potsdam, Germany DA - 10.07.2022 KW - SealWasteSafe KW - Monitoring KW - Acoustic emission KW - Fibre optic sensing KW - RFID technology KW - alkali-activated material PY - 2022 SP - 1 EP - 10 AN - OPUS4-55371 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eberwein, Robert A1 - Hajhariri, Aliasghar A1 - Camplese, Davide A1 - Scarponi, Giordano Emrys A1 - Cozzani, Valerio A1 - Otremba, Frank ED - Di Benedetto, Almerinda T1 - Experimental Research Of A Tank For A Cryogenic Fluid With A Wall Rupture In A Fire Scenario N2 - In the course of decarbonizing the energy industry, cryogenic energy carriers as liquefied hydrogen (LH2) and liquefied natural gas (LNG) are seen as having great potential. In technical applications, the challenge is to keep these energy carriers cold for a long time. This is achieved in the road transport sector and also stationary applications by thermal super insulations (TSI) which based on double-walled tanks with vacuum and multilayer insulation (MLI) in the interspace. This study focuses on the behaviour of widely used combustible MLI in a fire scenario, at vacuum and atmospheric pressure conditions. The former corresponds to the typical design condition and the latter to the condition after an outer hull rapture of a tank. Furthermore, two fire scenarios were taken into account: a standard-oriented approach and a hydrocarbon fire-oriented approach. For the study, a test rig was applied that allows testing of TSI at industrial conditions and subsequent analysis of TSI samples. The test rig allows thermal loading and performance analysis of TSI samples at the same time. Comparing the tests, the samples degraded differently. However, no sudden failure of the entire MLI was observed in any test. These results are relevant for the evaluation of incidents with tanks for the storage of cryogenic fluids and can thus contribute to the improvement of TSI and the development of emergency measures for the protection of persons and infrastructures. T2 - 15th International Symposium on Hazards, Prevention and Mitigation of Industrial Explosions (ISHPMIE) CY - Neapel, Italy DA - 10.06.2024 KW - Liquefied hydrogen KW - Liquefied natural gas KW - Cryogenic storage tank KW - Fire KW - Thermal insulation KW - Multi-Layer Insulation PY - 2024 SP - 707 EP - 717 AN - OPUS4-60460 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eberwein, Robert A1 - Hajhariri, Aliasghar A1 - Camplese, Davide A1 - Scarponi, Giordano Emrys A1 - Cozzani, Valerio A1 - Otremba, Frank T1 - A comparative study on insulation materials in tanks for the storage of cryogenic fluids in fire incidents N2 - Liquefied Hydrogen (LH2) or Liquefied Natural Gas (LNG) establish themselves as important energy carriers in the transport sector. Its storage requires tanks with Thermal Super Insulations (TSI) to keep the transported fluid cold. TSI has proven itself in various applications over a long time, but not in the land transport sector, where accidents involving collisions, fires, and their combination are to be expected. The focus of this study is to investigate the behavior of different types of TSI when exposed to a heat source that represents a fire. Therefore, a High-Temperature Thermal Vacuum Chamber (HTTVC) was used that allows the thermal loading of thermal insulation material in a vacuum and measuring the heat flow through the TSI in parallel. Within this study, 5 samples were tested regarding 3 different types of MLI, rock wool, and perlites. The thermal exposure caused different effects on the samples. In practice, this can be connected to the rapid release of flammable gases as well as a Boiling Liquid Expanding Vapour Explosion (BLEVE). These results are relevant for the evaluation of accident scenarios, the improvement of TSI, and the development of emergency measures. T2 - IMECE 2023 CY - New Orleans, Louisiana, USA DA - 29.10.2023 KW - LH2 KW - LNG KW - Fire PY - 2023 SP - 1 EP - 7 AN - OPUS4-58768 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Wolfgang A1 - Gradt, Thomas A1 - Theiler, Geraldine A1 - Aßmus, Kristin A1 - Ostrovskaya, Y. T1 - Werkstoff-Untersuchungen für technische Anwendungen in flüssigem Wasserstoff T2 - 1. Deutscher Wasserstoff-Energie-Tag 2002 CY - Essen, Deutschland DA - 2002-10-12 PY - 2002 IS - CD-ROM SP - 1 EP - 8 AN - OPUS4-1973 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Rübner, Katrin T1 - Aufbaukörnungen - Steigerung der Ressourceneffizienz im Bauwesen durch die Entwicklung innovativer Technologien für die Herstellung hochwertiger Aufbaukörnungen aus sekundären Rohstoffen auf der Basis von heterogenen Bau- und Abbruchabfällen, TP: Materialcharakterisierung KW - Bauabfall KW - Mineralischer Baustoff KW - Recycling KW - Granulieren PY - 2012 SP - 1 EP - 36 CY - Berlin AN - OPUS4-30066 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine A1 - Gradt, Thomas T1 - Comparison of the sliding behaviour of several polymers in hydrogen N2 - The work presented here deals with the friction and wear behaviour of polymer materials in hydrogen. Commercially available grades of PEEK, PA, PPA, PAI, PI and PBI were investigated at room temperature in air and hydrogen gas (H2) as well as in liquid hydrogen at -253°C (LH2). T2 - 7th World Tribology Congress, WTC 2022 CY - Lyon, France DA - 10.07.2022 KW - Friction KW - Wear KW - Polymers KW - Hydrogen KW - Cryogenic PY - 2021 SP - 1 AN - OPUS4-62089 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holtappels, Kai A1 - Theil, Benjamin A1 - Erdelen-Peppler, M. A1 - Meiwes, K.C. T1 - Explosive cutting of pipelines for the determination of materials properties N2 - Incidents in the past already showed that pipelines transporting compressible fluids are in risk of suffering propagating ductile fractures in case of damages to the pipes. Therefore, the knowledge of the fracture properties of pipeline steels is of high importance. Commonly the properties are determined in laboratory scale, but these do not fully correspond with full-scale fracture behaviour especially at dynamic conditions when highly pressurized gases are released during the crack propagation. This paper describes so-called West Jefferson Tests and Midscale-Tests in which pipelines under pressure were cut with an explosive charge to initiate the crack propagation. T2 - 9th World conference on Explosives and Blasting CY - Stockholm, Sweden DA - 10.09.2017 KW - Pipelines KW - Explosive cutting KW - Determination of materials PY - 2017 SN - 978-0-9550290-5-9 SP - 385 EP - 390 PB - European Federation of Explosives Engineers CY - UK AN - OPUS4-41994 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sauer, Hannah A1 - Okpeke, Bright Ebikemefa A1 - Dzielendziak, Agnieszka Sylwia A1 - Batcke, Lars A1 - Eberwein, Robert A1 - Ehlers, Sören T1 - Comparative life cycle assessment of different vacuum insulation panel core materials for cryogenic storage tanks – with a focus on glass bubbles as a novel core material N2 - Developing a sustainable hydrogen supply chain is important in facilitating the energy transition towards climate neutrality. Hydrogen in its free form can be stored and transported either as a gas or a liquid. Due to gaseous hydrogen's comparatively low energy density, liquefied hydrogen (LH 2) is often preferred, especially with regard to long-distance transportation and storage in bulk. A notable challenge associated with LH2 is the inherent requirement to preserve it at a low temperature of -253°C. Consequently, the utilisation of thermally insulated tanks is necessary to minimise LH 2 evaporation. There is a lack of literature on the environmental impacts of insulation materials and concepts for cryogenic storage tank applications in the hydrogen supply chain. Hence, this study investigates a novel concept, namely vacuum insulation panels (VIPs), focusing on their core materials, with a view to assessing their environmental sustainability and circularity. A cradle-to-grave life cycle assessment (LCA) model is employed to investigate six distinct VIP core materials, namely, silica aerogel, rigid polyurethane foam, expanded perlite, glass fibre, fumed silica, and glass bubbles (hollow glass microspheres), with a special focus on the latter. The LCA results show that polyurethane foam and silica aerogel rank low in environmental performance, making them less suitable as primary choice. Expanded perlite is the most environmentally friendly material option, followed by glass fibre, glass bubbles, and fumed silica. Improvements to the environmental impact of glass bubbles can be achieved via the implementation of closed-loop recycling in their life cycle. T2 - The World Hydrogen Technologies Convention 2025 CY - Dublin, Ireland DA - 21.10.2025 KW - LH2 KW - Insulation KW - Life cycle assessment PY - 2025 UR - https://www.whtc2025.com/conference-proceedings SP - 65 EP - 67 AN - OPUS4-64668 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Volkov, E.N. A1 - Konnov, A.A. A1 - Gula, Michal A1 - Holtappels, Kai A1 - Burluka, A.A. T1 - Laminar flames of N2O: experiments vs modeling KW - Lachgas KW - Laminare Flammen KW - Flammengeschwindigkeiten PY - 2008 SP - 57 EP - 58 AN - OPUS4-18783 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Volkmar A1 - Holtappels, Kai T1 - Explosion characteristics of hydrogen-air and hydrogen-oxygen mixtures at elevated pressures T2 - International Conference on Hydrogen Safety CY - Pisa, Italy DA - 2005-09-08 KW - Sicherheitstechnik KW - Wasserstoff KW - Explosionsgrenzen KW - Explosionsdrücke KW - Knallgas PY - 2005 SP - 35 PB - University of Pisa CY - Pisa AN - OPUS4-11085 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rolle, Annette A1 - Probst, Ulrich A1 - Ballheimer, Viktor A1 - Müller, Karsten A1 - Winkler, H. P. T1 - Transport condition effects on the sealing system and activity release within spent fuel transport casks N2 - Transport casks for spent fuel have to meet the International Atomic Energy Agency requirements for routine, normal and accident conditions of transport (RCT, NCT, and ACT). In regard to Containment capability a transport cask has to be designed to restrict the release of radioactive content to the required limits of 10'6 A2 per hour under NCT and A2 per week for ACT. Two barriers, which should avoid the release of fuel particles and fission products to the environment, are discussed in this paper: fuel rod claddings and the cask sealing System composed of cask body as well as of bolted lids and metallic seals. Both barriers can be affected by transport conditions. Vibrations and impact forces can increase the fraction of rods undergoing cladding breaches and can also lead to deformations or displacements of cask components involving an unloading or a movement of the lids or the seals. The above mentioned effects have to be properly considered in the safety analysis carried out by the applicant. The assumptions and results of the activity release calculations are verified by BAM Federal Institute for Materials Research and Testing. BAM is the German competent authority responsible, in particular, for Containment safety assessment within the licensing procedure of casks for spent fuel. T2 - RAMTRANSPORT 2012 - 9th International Conference on the Radioactive Materials Transport and Storage CY - London, UK DA - 22.05.2012 KW - Radioactive material KW - Safety assessment KW - Spent fuel KW - Leak tightness PY - 2012 SP - 1 EP - 9 AN - OPUS4-26498 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weimann, Karin A1 - Hoffmann, C. T1 - Ressourceneffizienz im Betonrecycling - Rahmen und Möglichkeiten in Deutschland und der Schweiz N2 - Aufgrund der großen anfallenden Massenströme ist die Wiederverwertung von Baurestmassen in Industrienationen von besonderer Bedeutung. Auch vor dem Hintergrund der Ressourceneffizienz wird beispielsweise die Nutzung des in Bauschutt vorhandenen Wertstoffpotentials zunehmend wichtiger. Eine besondere Rolle spielt dabei die Wiederverwertung von Altbeton. Ein Grund hierfür ist der deutliche Anstieg des seit Mitte des letzten Jahrhunderts im Bauwesen verbrauchten Betons und die damit verbundene – zeitlich versetzte – Zunahme des Altbetonanteils im Bauschutt. Darüber hinaus ist das Wertstoffpotential von Altbeton im Vergleich zu anderen Abbruchmaterialien besonders groß, denn Altbeton kann unter bestimmten Bedingungen sehr hochwertig auch als rezyklierte Gesteinskörnung wieder in der Betonherstellung eingesetzt werden. Damit kann ein Kreislauf im Sinne eines Closed-loop-Recycling verwirklicht und Altbeton damit hochwertig wiederverwertet werden. T2 - R’13 - Fachtagung Recycling CY - Weimar, Germany DA - 19.09.2013 KW - Ressourceneffizienz KW - Beton KW - Recycling KW - Ökobilanzielle Betrachtung PY - 2013 IS - Paper 14 SP - 1 EP - 11 PB - Bauhaus-Univ. CY - Weimar AN - OPUS4-30061 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Liebner, Christian A1 - Holtappels, Kai A1 - Schröder, Volkmar T1 - Selbstentzündungsprozesse bei nichtatmosphärischen Bedingungen - Die Identifizierung unerwarteter Risiken T2 - 7. Fachtagung Anlagen-, Arbeits- und Umweltsicherheit CY - Köthen, Deutschland DA - 2004-11-04 PY - 2004 PB - VDI-Verl. CY - Halle AN - OPUS4-5218 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weimann, Karin A1 - Giese, Lutz T1 - EU-LIFE Demonstrationsvorhaben zur Bauschuttaufbereitung - Die BAM arbeitet an neuen Wegen zum Betonbrechsandrecycling PY - 2002 VL - 2002-03 SP - 26 EP - 27 PB - VSR Verl. CY - Leipzig AN - OPUS4-1613 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weimann, Karin A1 - Giese, Lutz T1 - Nassaufbereitung von Betonbrechsand für die Betonherstellung PY - 2004 VL - 6-1 SP - 60 EP - 66 PB - Stein-Verl. CY - Baden-Baden AN - OPUS4-2831 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Giese, Lutz A1 - Segebade, Christian A1 - Weimann, Karin T1 - Aufbereitung und Recycling von Photovoltaik CdTe-Dünnschichtmodulen - EU-Life-Environment Demonstrationsvorhaben RESOLVED T2 - Tagung "Aufbereitung und Recycling 2004" - 50. Jahrestag der Gründung des Forschungsinstituts für Aufbereitung, CY - Freiberg, Deutschland DA - 2004-01-01 PY - 2004 SP - 1 EP - 2(?) PB - Forschungsinstitut für Aufbereitung CY - Freiberg AN - OPUS4-5311 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Giese, Lutz A1 - Weimann, Karin A1 - Loge, Kristina ED - Waldau, A. T1 - Wet Processing and Recycling of Compound Semiconductor Cells T2 - Workshop on Life Cycle Analysis and Recycling of Solar Modules CY - Brussels, Belgium DA - 2004-01-01 PY - 2004 VL - EUR 2110 SP - 175 EP - 184 CY - Brüssel AN - OPUS4-5315 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Giese, Lutz A1 - Segebade, Christian A1 - Weimann, Karin A1 - Loge, Kristina T1 - Abtrennung von Verbindungshalbleitern aus Gemengen T2 - Freiberger Solartage CY - Freiberg, Deutschland DA - 2004-09-02 PY - 2004 SP - 1 EP - 16(?) AN - OPUS4-5313 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weimann, Karin T1 - Verwertung der Sandfraktion aus dem Bauschuttrecycling T2 - Baustoff-Recycling-Tag 2004 CY - München, Deutschland DA - 2004-05-14 PY - 2004 AN - OPUS4-5316 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Ecker, K. H. A1 - Wätjen, U. A1 - Berger, Achim A1 - Grötzschel, R. A1 - Persson, L. A1 - Pritzkow, W. A1 - Radtke, Martin A1 - Riebe, Gundel A1 - Riesemeier, Heinrich A1 - Vogl, Jochen T1 - Certification of antimony implanted in silicon wafer with a silicon dioxide diffusion barrier - IRMM-302 and BAM-L001 N2 - This Report describes the certification of the reference material antimony implanted in Si/SiO2 intended to be used for calibration of surface and near surface analytical methods. It describes the preparation, homogeneity measurements and the analytical work performed for the certification of both Areal density of antimony Atoms (retained dose) and the isotope amount Ratio as well as giving considerations on the stability of the material. KW - Isotope ratio KW - Areal density KW - Surface analysis PY - 2002 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-355752 SP - 1 EP - 40 PB - Institute for Reference Materials and Measurements CY - Geel, Belgium AN - OPUS4-35575 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Liebner, Christian A1 - Holtappels, Kai A1 - Schröder, Volkmar A1 - Pasman, H. A1 - Pekalski, A. T1 - Report on experimentally determined self-ignition temperature and the ignition delay time KW - Autoignition KW - Pressure Dependency KW - Ignition Temperature KW - Cool Flame KW - Slow Combustion KW - Gases KW - n-Butane KW - Ethylene KW - Methane PY - 2005 UR - http://www.morechemistry.com/SAFEKINEX/deliverables/26.Del.%20No.%205%20SIT+IDT%20steel+quartz.pdf SP - 74 pages AN - OPUS4-5975 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eberwein, Robert A1 - Hajhariri, Aliasghar A1 - Camplese, D. A1 - Scarponi, G. E. A1 - Cozzani, V. A1 - Otremba, Frank T1 - Insulation Materials Used in Tanks for the Storage of Cryogenic Fluids in Fire Scenarios N2 - The importance of tanks for storing cryogenic fluids in the energy industry is increasing because of ongoing political conflicts and the implementation of more environmentally friendly energy sources. Key representatives for the application of cryogenic tanks are natural gas in the form of Liquefied Natural Gas (LNG) and hydrogen, e. g. in the form of Liquefied Hydrogen (LH2), for which significantly higher transport capacities can be achieved with the same transport volume using cryogenic storages than with storages based solely on overpressure. What applies to all cryogenic transported fluids in common is their condition that must be maintained. Hence heat flows into the preserved fluid must be minimized. Thermal super Insulations (TSI) based on e. g. multilayer insulations (MLI), perlites, and vacuum are utilized for this purpose and have already proven themselves in similar applications. However, for the use of tanks for cryogenic fluids in the transport sector, there is insufficient knowledge regarding the course and consequences of incidents, which is due to the still short period of use and the few documented incidents, hence few investigations carried out in this field. Typical scenarios in the transport sector represent car accidents with collisions, fires, and their combination, which are associated with extraordinary loads on the tank. The focus of this study is to investigate the behavior of TSI as a result of their thermal exposure to a heat source representing a fire. It is worth mentioning that this could lead to an increase of the heat flux into a tank by several orders of magnitude, and to permanent damage of the TSI, ultimately rapid release of flammable gas as well as a Boiling Liquide Expanding Vapour Explosion (BLEVE). For this purpose, a high temperature thermal vacuum chamber (HTTVC) has been developed that allows thermal loading of MLI or perlites in a vacuum and simultaneous measurement of heat flow through this TSI. The HTTVC is designed to represent realistic insulation conditions and to withstand thermal loads from typical design fires. The HTTVC was applied to investigate TSI based on MLI and vacuum. It is shown that the thermal stress caused permanent damage to the TSI, with shrinkage, phase change, pyrolysis, and condensation being significant damage mechanisms. The results are relevant for the evaluation of accident scenarios and can thus contribute to the improvement of TSI and the development of emergency measures for the protection of persons and infrastructures. T2 - ASME 2023 Pressure Vessels & Piping Conference (PVP2023) CY - Atlanta, Georgia, USA DA - 16.07.2023 KW - LH2 KW - LNG KW - MLI KW - Fire PY - 2023 SP - 1 EP - 8 PB - ASME AN - OPUS4-57973 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hajhariri, Aliasghar ED - Eberwein, Robert ED - Perrone, Luca pakj ED - Cozzani, Valerio ED - Otremba, Frank ED - Seidlitz, Holger T1 - Study the Impact of Spacer at Thermal Degradation Process of MLI-based Insulation in Fire Condition N2 - To reduce carbon dioxide emissions, energy carries such as hydrogen consider to be a solution. Consumption of hydrogen as a fuel meets several restrictions such as its low volumetric energy density in gas phase. To tackle this problem, storage as well as transportation in liquid phase is recommended. To be able to handle this component in liquid phase, an efficient thermal insulation e.g., MLI insulation is required. Some studies have been revealed vulnerability of this type of insulation against high heat flux, for instance a fire accident. Some investigations have been depicted the importance of consideration of the MLI thermal degradation in terms of its reflective layer. However, limited number of studies have been focused on the thermal degradation of spacer material and its effect on the overall heat flux. In this study, through systematic experimental measurements, the effect of thermal loads on glass fleece, glass paper as well as polyester spacers are investigated. The results are reported in various temperature and heat flux profiles. Interpreting the temperature profiles revealed as the number of spacers in the medium increases, the peak temperature detectable by the temperature sensor on the measurement plate decreases. Moreover, the contribution of each individual spacer in all cases regarding the experimental temperature range is assessed to be around 8%. This value may increase to around 50% for glass paper and polyester spacers, and to around 25% for glass fleece spacers as the number of spacer layers increases up to six layers. To utilize the outcomes of the experiment later and integrate the results into numerical and CFD simulations, a model is proposed for the mentioned experimental temperature range up to 300°C to predict a heat flux attenuation factor. The model proposes a fitting factor that can reproduce the least square fitted line to the experimental data. T2 - 15th International Symposium on Hazards, Prevention, and Mitigation of Industrial Explosions Naples (ISHPMIE) CY - Naples, Italy DA - 10.06.2024 KW - Multi-Layer Insulation KW - Cryogenics KW - Liquid Hydrogen KW - Heat Transfer KW - Hydrogen Storage PY - 2024 SP - 744 EP - 755 AN - OPUS4-60461 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eberwein, Robert A1 - Scarponi, Giordano Emrys A1 - Cozzani, Valerio A1 - Otremba, Frank T1 - Lh2 Tanks In Fire Incidents - The Cryogenic High Temperature Thermal Vacuum Chamber Enables In-Depth Insights N2 - Liquefied Hydrogen (LH2) and Liquefied Natural Gas (LNG) establish themselves as important energy carriers in the transport sector. Their storage requires tanks with thermal super-insulations to keep them at cryogenic conditions for a long time. These insulation systems have proven itself in various applications over a long time. However, these insulations are still new in land transportation, where accidents involving collisions, fires, and their combination are to be expected. This study summarizes the results of the ongoing research program in which insulations commonly used in industry were analysed through experimental and numerical studies under fire-like conditions. It was found that there are strong differences among the various insulation systems. Several safety concerns and research gaps exists for layered insulations, which are typically used in land transport. To further analyse these insulation systems, a new test concept called Cryogenic High Temperature Thermal Vacuum Chamber (CHTTVC) was developed and manufactured. This concept enables the testing of large insulation samples under industrial conditions and the consideration of cryogenic conditions relevant for the investigation of various phenomena. The results are important for the evaluation of accident scenarios, the improvement of thermal super-insulations, and the development of emergency measures. T2 - IMECE 2024 CY - Oregon, Portland, USA DA - 17.11.2024 KW - LH2 KW - LNG KW - Fire KW - Insulation KW - Safety PY - 2024 SN - 978-0-7918-8869-8 SP - 1 EP - 7 PB - ASME AN - OPUS4-61751 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Molnarne, Maria A1 - Wilrich, Cordula A1 - Holtappels, Kai T1 - Chemically unstable gases and gas mixtures - new categories in the GHS N2 - In connection with the use of chemically unstable gases (especially acetylene and ethylene oxide) accidents keep on happening - amongst them also quite serious ones. These gases are known to be chemically unstable. A chemically unstable sas is a flammable gas that is able to react exolosivelv even in the absence of air or oxveen. The investigation of accidents showed that the Chemical instability of flammable gases played an important role in the severity of accidents. Therefore, this hazardous property was included in the global harmonizatiön of the Classification of Chemicals. The Classification of chemically unstable flammable gases and mixtures is an amendment to Chapter 2.2 “Flammable gases” of the UN Globally Harmonized System of Classification and Labelling of Chemicals (GHS), because most chemically unstable gases are flammable as well. The proposal to add them to the GHS originated from the experts of an informal working group of the UN Sub-Committee of Expert on the GHS (UNSCEGHS) headed by BAM, Germany. The UNSCEGHS has decided to include it in the Fourth Revised Edition of the GHS. The respective method for determining whether a gas is chemically unstable or not, is included in the UN Manual of Tests and Criteria. This paper presents some experimental investigations of these gases, the test methods, examples of new classifications and results from CHEMSAFE T2 - 14th Annual symposium, Mary Kay O´Connor process safety center - Beyond regulatory compliance: making safety second nature CY - College Station, TX, USA DA - 25.10.2011 KW - Chemically unstable gases KW - GHS KW - Chemisch instabile Gase PY - 2011 SP - 871 EP - 882 AN - OPUS4-24913 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sarif, Raduan A1 - Tiebe, Carlo A1 - Herglotz, Christian T1 - Early Response Prediction for H2 Sensors N2 - Green hydrogen (H2) is essential for the global transition to clean energy; it will significantly reduce emissions from heavy industry and the long-distance transport system. H2 can be used as fuel in fuel cells, storing surplus renewable energy, and as a feedstock in industrial processes. However, H2 faces significant safety challenges during storage and transportation. Accidents due to H2 leakage and explosions raise serious concerns due to its high flammability, rapid diffusion in air, and extremely low ignition energy. To mitigate risks associated with H2 leakages, reliable and automated H2 safety systems are essential for emergency repairs or shutdown. An early response from H2 sensors is crucial for early warning in accidents. The earlier response time of H2 sensors is often constrained by their sensor principle, which is heavily influenced by the sensor material’s properties. This study explores methods for earlier sensor response through predictive algorithms. Specifically, we investigate transient response predictions using a First-Order (FO) model and propose improvements through the First-Order with early response and the First-Order with adapted early response model. Both models can predict the stable value of the H2 sensor response from a small time window, which is 70.89% and 83.72% earlier, respectively, than the time required for the sensor hardware to reach it physically. The model’s performance is evaluated by calculating the fitting error with a 2 % threshold. Our current research lays the groundwork for future advancements in real-time sensor response predictions for hydrogen leakage. T2 - IARIA Congress 2025 : The 2025 IARIA Annual Congress on Frontiers in Science, Technology, Services, and Applications CY - Venice, Italy DA - 06.07.2025 KW - H2 Safety KW - H2 leakage detection KW - First-Order (FO) model KW - H2 Sensor data analysis KW - H2 sensor response predictions PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-640676 UR - https://www.thinkmind.org/articles/iaria_congress_2025_1_250_50159.pdf SN - 978-1-68558-284-5 SP - 1 EP - 8 PB - IARIA Press CY - Wilmington AN - OPUS4-64067 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sarif, Raduan A1 - Tiebe, Carlo A1 - Herglotz, Christian T1 - Analysis of Methods for Predicting H2 Sensor Responses N2 - Hydrogen (H2) is crucial for replacing fossil fuels and achieving net-zero emissions, but its flammability and explosiveness pose safety challenges. Rapid H2 leak detection is essential for triggering emergency accidents. However, H2 sensor response is constrained by material properties and gas flow dynamics, causing response and detection delays. Our current study explores various available algorithms for H2 sensor response prediction from early responses with a small time window, accelerating leakage detection. Our findings identify the most efficient algorithms for real-time implementation, enhancing H2 safety systems. T2 - SMSI 2025 2025-05-06 - 2025-05-08 Nürnberg CY - Nuremberg, Germany DA - 06.05.2025 KW - H2 safety KW - Early H2 leakage detection KW - Prediction algorithms KW - Stable H2 value prediction PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-640617 SN - 978-3-910600-06-5 DO - https://doi.org/10.5162/SMSI2025/C6.3 SP - 169 EP - 170 PB - AMA Verband für Sensorik und Messtechnik e.V. CY - Berlin AN - OPUS4-64061 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine A1 - Cano Murillo, Natalia A1 - Sawae, Y. A1 - Shinmori, H. A1 - Hashimoto, H. A1 - Aoyagi, A. A1 - Dobbelaar, E. T1 - Towards sustainable and hydrogen compatible sealing materials N2 - Materialien auf PTFE-Basis werden in der Regel als Kolbenringe in Hochdruck- und/oder kryogenem Wasserstoff verwendet. In diesem Projekt werden neu formulierte und nachhaltigere Polymerwerkstoffe mit herkömmlichen Materialien verglichen. Auf Grundlage der tribologischen Ergebnisse werden vielversprechende Kandidaten zusammen mit Reibungsmechanismen sowohl bei Hochdruck- als auch bei Niedrigtemperatur-Wasserstoff vorgeschlagen. T2 - 66. GfT Tribologie-Fachtagung 2025 CY - Wernigerode, Germany DA - 29.09.2025 KW - Wasserstoff KW - Reibung KW - Verschleiß KW - Kolbenring KW - Dynamische Dichtung PY - 2025 VL - 09 SP - 1 EP - 4 AN - OPUS4-64314 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaad, C. A1 - Tiebe, Carlo A1 - Groth, Katrina M. T1 - A Framework for Transforming Process Control System Data from a Hydrogen Fueling Station into HyCReD Data N2 - Reliability data for hydrogen infrastructure components is essential for developing Quantitative Risk Assessment (QRA) for these technologies, which in turn is necessary for a safer deployment and expansion of the hydrogen market. However, there is currently a lack of hydrogen component reliability data available for these systems, thus limiting the usefulness of insights obtained from these QRA. The Hydrogen Component Reliability Database (HyCReD) has been proposed as a tool for reliability data collection and as a source for future QRAs. In this paper, we develop a digital tool that automatically processes data coming from Process Control System (PCS) in a hydrogen fueling station, detects the relevant failure events for hydrogen systems during its operation, and then logs the event information into HyCReD. To build this tool, we first categorized the station components in hydrogen service, their specific failure modes, and the specific failure mechanisms that are relevant to a QRA. Then, we identified the data available in the station PCS and the methods available for diagnosing the relevant failure events. The resulting tool is divided into three steps: (1) PCS data collection through an API, (2) data analysis for the detection and diagnosis of new failure events, and (3) logging that event into HyCReD. Finally, we discuss the potential for expanding the detection and diagnosis to more complex failure modes present in a hydrogen fueling station. This digital tool is set for implementation and validation on an experimental hydrogen fueling site. The goal for this digital tool is to be applicable to every kind of hydrogen fueling station and to be extendable to similar hydrogen technologies. T2 - 35th European Safety and Reliability Conference (ESREL2025) and the 33rd Society for Risk Analysis Europe Conference (SRA-E 2025) CY - Stavanger, Norway DA - 15.06.2025 KW - Reliability data KW - Hydrogen safety KW - HyCReD KW - Hydrogen Component Reliability Database KW - Hydrogen fueling station KW - Hydrogen refuelling station KW - HRS PY - 2025 UR - https://rpsonline.com.sg/proceedings/esrel-sra-e2025/html/ESREL-SRA-E2025-P6264.html SN - 978-981-94-3281-3 DO - https://doi.org/10.3850/978-981-94-3281-3-procd SP - 2663 EP - 2670 PB - Research Publishing CY - Singapore AN - OPUS4-63532 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eberwein, Robert A1 - Hajhariri, Aliasghar A1 - Otremba, Frank A1 - Camplese, Davide A1 - Scarponi, Giordano E. A1 - Cozzani, Valerio A1 - Seidlitz, Holger T1 - Repeatable testing of a cryogenic storage tank with variable insulation material in fire like conditions N2 - For decarbonizing the energy industry and transport, cryogenic energy carriers have great potential. The storage takes place in tanks with thermal super-insulations, which are in application for decades, but there is only limited knowledge about its behaviour in a fire scenario. This represents a major incident that may generate extraordinary loads on the tank and its insulation system, and that eventually lead to a sudden tank failure. This paper presents a test rig called the Cryogenic High Temperature Thermal Vacuum Chamber (CHTTVC), which can be used to test typical thermal superinsulation’s under cryogenic and fire-like conditions in parallel. The test method makes it possible to measure the heat flow through the thermal superinsulation over time and to investigate the degradation behaviour of the insulation within a test. In the paper results from the first tests are presented. T2 - 18th Cryogenics 2025, IIR Conference CY - Prague, Czech Republic DA - 07.04.2025 KW - LH2 KW - LNG KW - Fire KW - Insulation KW - Safety PY - 2025 DO - https://doi.org/10.18462/iir.cryo.2025.0007 SP - 205 EP - 210 CY - Prag AN - OPUS4-63740 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tiebe, Carlo A1 - Johann, Sergej A1 - Dessel, S. T1 - Prüfanweisung für Gassensoren N2 - Viele Sensoren sind auf dem Markt, die flüchtige organische Substanzen im Innenraum nicht nur messen, sondern gleichzeitig auch die Luftgüte bewerten. Damit diese Sensoren gute und vergleichbare Daten liefern, erarbeitet ein Fachausschuss der VDI/VDE-Gesellschaft Mess- und Automatisierungstechnik (GMA) eine neue VDI-Richtlinie. KW - VOC KW - Gassensor KW - Innenraumluft KW - IAQ KW - Richtlinie KW - Gasmesssystem PY - 2021 VL - 51 IS - 03-04 SP - 41 EP - 42 AN - OPUS4-52445 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Detjens, Marc A1 - Tiebe, Carlo A1 - Banach, Ulrich A1 - Ritter, U. T1 - Ionische Flüssigkeiten als neuartige Sensorbeschichtung für coulometrische Spurenfeuchtesensoren N2 - Die Arbeit präsentiert erste Messungen mit coulometrischen Sensoren, die mit einer ionischen Flüssigkeit beschichtet sind. Diese Sensoren werden in der Industrie verwendet, um die Spurenfeuchte in unterschiedlichen Gasen zu messen. Normalerweise erfolgt eine Beschichtung der Sensoren mit Phosphorpentoxid und dessen Hydrolyseprodukte. In dieser Arbeit wurde stattdessen eine hygroskopische ionische Flüssigkeit benutzt. Die generierte Gasfeuchte für die Untersuchungen betrug bezogen auf die Frostpunkttemperatur -80 °C bis -30 °C, was gleichbedeutend mit einem Wasserdampf-Stoffmengenanteil von 0,5 μmol·mol-1 bis 376 μmol·mol-1 ist. Zusätzlich zu der Messung mit coulometrischen Sensoren erfolgte eine Referenzmessung der Gasfeuchte mittels eines Taupunkthygrometers. Erste Ergebnisse haben gezeigt, dass es möglich ist mit dieser Art der Beschichtung unterschiedliche Gasfeuchten zu messen. Aber es ergaben sich trotz gleicher Feuchte unterschiedliche Signalintensitäten bei den benutzen Sensoren und es zeigte sich eine Drift des Sensorsignales. T2 - Sensoren und Messsysteme CY - Nuremberg, Germany DA - 26.06.2018 KW - Spurenfeuchtemessung KW - Sensorbeschichtung KW - Elektrolyseverfahren KW - Ionische Flüssigkeiten PY - 2018 SN - 978-3-8007-4683-5 SN - 0932-6022 SP - 520 EP - 523 PB - VDE VERLAG GMBH CY - Berlin, Offenbach AN - OPUS4-45319 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Moufid, M. A1 - Tiebe, Carlo A1 - El Bari, N. A1 - Bartholmai, Matthias A1 - Bouchikhi, B. T1 - Combining of TD-GC-MS and home developed electronic nose for road traffic air monitoring N2 - In this work, we demonstrate the ability of an electronic nose system based on an array of six-semiconductor gas sensors for outdoor air quality monitoring over a day at a traffic road in downtown of Meknes city (Morocco). The response of the sensor array reaches its maximum in the evening of the investigated day which may due to high vehicular traffic or/and human habits resulting in elevated concentrations of pollutants. Dataset treatment by Principal Component Analysis and Discriminant Function Analysis shows a good discrimination between samples collected at different times of the day. Moreover, Support Vector Machines were used and reached a classification success rate of 97.5 %. Thermal Desorption-Gas Chromatography-Mass Spectrometry (TD-GC-MS) technique was used to validate the developed e-nose system by identifying the composition of the analyzed air samples. The discrimination obtained by e-nose system was in good agreement with the TD-GC-MS results. This study demonstrates the usefulness of TD-GC-MS and e-nose, providing high accuracy in discriminating outdoor air samples collected at different times. This demonstrates the potential of using the e-nose as a rapid, easy to use and inexpensive environmental monitoring system. T2 - 2021 IEEE International Conference on Design & Test of Integrated Micro & Nano-Systems (DTS) CY - Sfax, Tunisia DA - 07.06.2021 KW - GC-MS KW - Electronic nose KW - Gas sensors KW - Urban air monitoring PY - 2021 DO - https://doi.org/10.1109/DTS52014.2021.9498110 SP - 1 EP - 6 AN - OPUS4-54401 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holtappels, Kai A1 - Brinkmann, C. A1 - Stickling, J. A1 - Schönbucher, A. T1 - Simulation des Fremdgaseinflusses auf sicherheitstechnische Kenngrößen von Ethin mit dem Modell EPSIM T2 - Bunsentagung 2002 ; Industrie-Symposium Industrielle Anwendungen der NMR: Struktur und Dynamik ; 101. Hauptversammlung der Deutschen Bunsen-Gesellschaft für Physikalische Chemie CY - Potsdam, Germany DA - 2002-05-09 PY - 2002 IS - 101 SP - P125 EP - P126 CY - Potsdam AN - OPUS4-1533 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holtappels, Kai A1 - Dietlen, Siegmund A1 - Brinkmann, C. A1 - Stickling, J. A1 - Schönbucher, A. T1 - Prediction and measurement of the inert gas influence on explosion limits for industrial used gas/air-mixtures especially at elevated pressures T2 - 3rd ECCE ; 3rd European Congress of Chemical Engineering ; 618th [Event of the European Federation of Chemical Engineering] CY - Nuremberg, Germany DA - 2001-06-26 PY - 2001 SP - 1 EP - 28 PB - DECHEMA] CY - [Frankfurt am Main AN - OPUS4-1125 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holtappels, Kai A1 - Schröder, Volkmar T1 - Explosion characteristics of hydrogen-oxygen and hydrogen-air mixtures at elevated temperatures and pressures T2 - 2nd European Hydrogen Energy Conference CY - Zaragoza, Spain DA - 2005-11-22 KW - Wasserstoff KW - Sicherheitstechnische Kenngrößen KW - Nicht-atmosphärische Bedingungen PY - 2005 SP - 664 EP - 666 PB - IDAE Instituto para la Diversificación y Ahorro de la Energía CY - Madrid AN - OPUS4-11535 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thöns, Sebastian A1 - Rücker, Werner A1 - Faber, M.H. T1 - Support structure reliability of offshore wind turbines utilizing an adaptive response surface method T2 - OMAE 2010 - 29th International conference on ocean, offshore and arctic engineering CY - Shanghai, China DA - 2010-06-06 PY - 2010 IS - OMAE2010-20546 SP - 1 EP - 10 AN - OPUS4-21666 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine A1 - Halder, Karabi A1 - Balasooriya, Winoj T1 - Effect of high-pressure hydrogen environment on the physical and mechanical properties of elastomers N2 - This paper deals with the exposure of HBNR rubbers to high pressure hydrogen (100 MPa) at 120 °C for 7 and 21 days under static conditions followed by characterization of their physical and mechanical properties. T2 - EHEC European Hydrogen Energy Conference 2022 CY - Madrid, Spain DA - 18.05.2022 KW - Rubbers KW - Hydrogen KW - Characterization PY - 2022 SP - 1 EP - 2 AN - OPUS4-62085 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Detjens, Marc A1 - Tiebe, Carlo A1 - Banach, Ulrich T1 - Influence of Gas Pressure on Coulometric Trace Humidity Measurement N2 - Planar coulometric sensors were investigated in humidified synthetic air at various absolute gas pressures, i. e. 2 bar, 5, bar, 10 bar, and 15 bar. Humidified gas flow at adjusted gas pressure was split into two flows, one passed a coulometric sensor and the other one passed a reference hygrometer after decompression. Both signals were recorded and then compared after calculation of resulting frost point temperature. Calculation is based on a calibration function obtained at ambient pressure. Comparison showed that an increasing pressure resulted in a higher derivation between sensor signal (calculated frost point temperature) and reference frost point temperature. At an absolute pressure of 2 bar the differences were minor in consideration of the uncertainty, however at 15 bar the differences were 6.77 K. Nevertheless, it was possible to measure the gas humidity at higher pressure with coulometric trace humidity sensors. T2 - 17th International Meeting of Chemical Sensors, IMCS 2018 CY - Vienna, Austria DA - 15.07.2018 KW - Gas pressure influence KW - Coulometric sensors KW - Trace humidity measurement PY - 2018 SN - 978-3-9816876-9-9 DO - https://doi.org/10.5162/IMCS2018/P2EC.7 SP - 715 EP - 716 PB - AMA Service GmbH CY - Wunstorf / Germany AN - OPUS4-45539 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Theiler, Geraldine A1 - Gradt, Thomas T1 - Friction and wear characteristics of polymers in gaseous and liquid N2 - In the present work it was shown that the the aim of the presented tests is to investigate polymer composites for their suitability for friction systems in gaseous and liquid hydrogen. T2 - 59. Tribologie-Fachtagung CY - Göttingen, Germany DA - 24.09.2018 KW - Friction KW - Wear KW - Polymer composites KW - Hydrogen KW - Cryogenic temperature PY - 2018 SN - 978-3-9817451-3-9 SP - 60/1 EP - 60/4 AN - OPUS4-46178 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Harwege, Finn A1 - Schmidt, Heiko A1 - Eberwein, Robert T1 - Testing of vacuum insulation panels for liquid hydrogen storage tanks N2 - Vacuum insulation panel (VIP) based insulation could present an alternative to the common double walled vacuum insulation for large liquefied Hydrogen (LH2) storage tanks. In this paper a brief introduction on VIPs and the envisioned design of VIP-based LH2-tank insulation is given. The design of a flat plate boil-off calorimeter for the testing of the insulation concept is shown, with regard to thermal design, mechanical design and instrumentation. Finally, an overview over the particular challenges for modelling VIP-based insulation and the proposed testing to be performed on the test rig is presented. T2 - 18th Cryogenics IIR International Conference CY - Prague, Czech Republic DA - 07.04.2025 KW - Liquefied Hydrogen KW - Insulation KW - Calorimeter KW - Vacuum Insulation Panel KW - LH2 PY - 2025 SN - 0151-1637 DO - https://doi.org/10.18462/iir.cryo.2025.0010 SN - 978-2-36215-053-1 VL - 2025 SP - 168 EP - 174 PB - ICCEX CY - Prag AN - OPUS4-62959 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Giese, Lutz A1 - Weimann, Karin A1 - Loge, Kristina ED - Stadermann, G. T1 - Wiederverwertung von PV-Dünnschichtmodulen T2 - Workshop. ForschungsVerbund Sonnenenergie CY - Berlin, Deutschland DA - 2003-12-11 PY - 2003 SP - 1(?) EP - 3(?) PB - Oktoberdruck CY - Berlin AN - OPUS4-2828 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weimann, Karin T1 - Nassaufbereitung von Betonbrechsand mit dem Ziel der vollständigen Verwertung T2 - Tagung Recycling 2003 CY - Weimar, Deutschland DA - 2003-03-27 PY - 2003 SP - 1(?) EP - 14(?) AN - OPUS4-2830 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weimann, Karin A1 - Farago, Patrick A1 - Mayer, Felix ED - Angulo, Sergio ED - Landmann, Mirko T1 - New sources for secondary gypsum N2 - In order to protect natural gypsum deposits and to compensate for the decreasing amount of Flue Gas Desulfurization (FGD) gypsum it is necessary to develop and explore new sources of gypsum. For this purpose, the potentials of different gypsum wastes are investigated in the study “GipsRec 2.0”, funded by the Federal Ministry of Education and Research (Germany). On the one hand, the project worked on a new processing technology for gypsum fiberboards (GFB). While the recycling of gypsum plasterboards has already been carried out on an industrial scale for several years, the recycling of gypsum fiberboards (GFB) has proven to be challenging. Gypsum fiberboards from demolition sites and offcuts from GFB production were used for these investigations. The tests were conducted on a technical scale. Furthermore, various synthetic gypsums are being investigated with regard to their suitability for gypsum production. The analyses are carried out on production residues. In this project, a promising process for gypsum fiberboard recycling could be developed, as well as other waste gypsums are investigated and evaluated with regard to their potential as secondary raw material. In addition, selected process routes are assessed for their environmental impact using a life cycle assessment (LCA) approach. T2 - RILEM - V International Conference Progress of Recycling in the Built Environment CY - Weimar, Germany DA - 10.10.2023 KW - Gypsum recycling KW - Gypsum fiberboards and synthetic gypsum KW - Environmental evaluation PY - 2023 VL - V SP - 1 EP - 10 PB - RILEM Publications Sarl CY - Bagneux, France AN - OPUS4-60315 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Nowak, S. H. A1 - Petric, M. A1 - Buchriegler, J. A1 - Bjeoumikhov, A. A1 - Bjeoumikhova, Z. A1 - von Borany, J. A1 - Munnik, F. A1 - Radtke, Martin A1 - Renno, A. D. A1 - Reinholz, Uwe A1 - Scharf, O. A1 - Tilgner, J. A1 - Wedell, R. T1 - Road to micron resolution with a color X-ray camera - Polycapillary optics characterization N2 - In a color X-ray camera spatial resolution is achieved by means of a polycapillary optic conducting X-ray photons from small regions on a sample to distinct energy dispersive pixels on a CCD matrix. At present, the resolution limit of color X-ray camera systems can go down to several microns and is mainly restricted by Pixel dimensions. The recent development of an efficient subpixel resolution algorithm allows a release from pixel size, limiting the resolution only to the quality of theoptics. In this work polycapillary properties that influence the spatial resolution are systematized and assessed both theoretically and experimentally. It is demonstrated that with the current technological Level reaching one micron resolution is challenging, but possible. KW - Color X-ray camera KW - Polycapillary optics PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-404404 DO - https://doi.org/10.48550/arXiv.1705.08939 SN - 2331-8422 SP - 1 EP - 11 PB - Cornell University CY - Ithaca, NY AN - OPUS4-40440 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Priebe, Nsesheye Susan T1 - Influence of calcination conditions and varying compositions on the reactivity and performance of brick clays as supplementary cementitious materials T1 - Der Einfluss von Kalzinierungsbedingungen und verschiedenen Zusammensetzungen auf die Reaktivität und Eigenschaften von Ziegeltonen verwendet als Zusatzstoffe in Beton N2 - Calcined clays as supplementary cementitious materials (SCMs) have been identified and credited to be a viable solution in mitigating the CO2 emissions related to cement production and consumption. Calcined clays range from a variety of different clay types based on an assortment of varying minerals and compositions. While extensive data is available on kaolinitic clays (based on the 1:1 clay type), other clays such as brick clays (based on the 2:1 clay type) are currently understudied, although such clays are largely more available than the kaolinitic clays. The aim of this thesis is to draw attention to the varying compositions present in two selected brick clays in Germany and elaborate on how such compositions affect their suitability to be used as SCMs in blended cement systems. The novelty of this thesis explains the relationship between the reactivity of the bricks to their varying compositions and their suitability for their employment as SCMs. This was based on their chemical and physical transformations in the calcination temperature range 650–900 or 950 °C, and the performance of the calcined brick clays in blended cement systems measured by their heat evolution, strength development and durability-related properties. The results of their performance were compared to two kaolinitic clays with varying compositions. While the kaolinitic clays generally exhibited the best performance as SCMs, the brick clay with a lower Fe2O3 content showed promising results similar to the kaolinitic clays when an optimum calcination temperature is applied and when substituted at a moderate cement substitution rate. Thus, this finding promoted further efforts made to improve the reactivity of the brick clay by producing a mixed clay composed of 50 % brick clay (with lower Fe2O3 content) and 50 % kaolinitic clay. The mixed clay was compared to the two individual brick clays and one kaolinitic clay, whereby optimum calcination conditions were performed in large-scale simulating an industrial-scale production of SCMs. All calcined clays exhibited pozzolanic reactivity, with the performance of the brick clays inferior to the kaolinitic clay, however, the mixed clay performed very similar to the kaolinitic clay. At a similar degree of hydration compared to plain Portland cement, the good performance of the mixed clays was especially evident in the strength development and improved chloride penetration resistance, which was caused by a refinement in the pore structure in the cementitious systems. Moreover, it was deduced that not only the high surface area, but also, the solubility of Si and Al ions in the resulting calcinate of the mixed clays plays a significant role when calcined at ~600–700 °C, which points to viable options for optimal employment of brick clays in cementitious systems. N2 - Die bei der Zementproduktion freigesetzte CO2-Menge und die daraus resultierenden Folgen für das Klima machen die Entwicklung von Zementersatzstoffen mit geringerem CO2-Fußabdruck erforderlich. Als besonders vielversprechend haben sich dabei die kalzinierten Tone erwiesen. Bei diesen handelt es sich um komplexe Systeme, bestehend aus einer Vielzahl verschiedener Tonminerale in variierender Konzentration und Zusammensetzung. Während für kaolinitische Tone (basierend auf 1:1 Tonmineralarten) bereits umfangreiche Daten gesammelt werden konnten, ist der Kenntnisstand zu anderen Tonarten z.B. Ziegeltonen (basierend auf 2:1 Tonmineralarten) derzeit noch unzureichend. Besonders vor dem Hintergrund der erheblich größeren Verfügbarkeit dieser Tonarten stellt dies einen erheblichen Nachteil dar. Ziel dieser Arbeit ist es, anhand zweier Ziegeltone aus Deutschland, aufzuzeigen welche Auswirkung die unterschiedliche Zusammensetzung der Tone sowohl auf die Reaktivität als auch auf den Einsatz als Zementersatzstoffen in Mischzementsystemen hat. Entsprechende Änderungen in der Zusammensetzung der kalzinierten Tone wurden durch die Variation der Kalzinierungstemperatur im Temperaturbereich zwischen 650 °C und 900 °C bzw. 950 °C und den folglich unterschiedlich ablaufenden chemischen und physikalischen Umwandlungsprozessen der Tonminerale erreicht. Die Leistungsfähigkeit dieser Systeme wurde anhand der Wärme- und Festigkeitsentwicklung sowie den Dauerhaftigkeitseigenschaften bewertet. Als Referenzsysteme dienten zwei 1:1 Tone mit unterschiedlicher Zusammensetzung. Die bei den 1:1 Tonen erzielten Reaktivitäten waren im Vergleich zu den Ziegeltonen zwar höher, aber bei entsprechender Kalzinierungstemperatur und moderater Zementersatzrate konnten auch bei den Ziegeltonen vielversprechende Ergebnisse erzielt werden. Basierend auf diesen Ergebnissen wurden in einem weiteren Schritt Mischtone, bestehend aus kaolinitischem Ton und Ziegelton mit geringerem Fe2O3 Gehalt (50:50), untersucht. Zur Bewertung wurden die zuvor untersuchten Ziegeltone und ein 1:1 Ton herangezogen. Bei allen kalzinierten Tonen konnte die pozzolanische Reaktion nachgewiesen werden, wobei der Ziegelton die geringsten und die 1:1 Tone die höchsten Werte lieferte. Das Mischtonsysteme sind leistungstechnisch bei den 1:1 Tonen einzuordnen. Die strukturverfeinernde Wirkung des Mischtons beim Einsatz als Zementersatz in Portlandzementsystemen führte sowohl bei der Festigkeitsentwicklung als auch beim Chlorideindringwiderstand zu einer Leistungssteigerung. Zudem konnte gezeigt werden, dass nicht nur die große spezifische Oberfläche, sondern auch die hohe Löslichkeit der Si- und Al-Ionen in den Kalzinaten der bei ~600-700 °C kalzinierten Mischtone einen großen Einfluss hat und den Einsatz der Ziegeltone in zementären Systemen begünstigt. Die Möglichkeit zur Herstellung von Zementersatzstoffen im industriellen Maßstab konnte durch Versuche im Großmaßstab ebenfalls nachgewiesen werden. KW - Blended cement KW - Brick clay KW - Calcined clay KW - Hydration KW - Illite KW - Kalzinierte Tone KW - Ziegelton PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:co1-opus4-58816 DO - https://doi.org/10.26127/BTUOpen-5881 SP - i EP - 153 PB - Brandenburgische Technische Universität Cottbus-Senftenberg CY - Cottbus AN - OPUS4-55048 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Licht, M. A1 - Nikoonasab, Ali A1 - Gluth, Gregor A1 - Raupach, M. ED - Claßen, M. ED - Hegger, J. ED - Matschei, T. ED - Raupach, M. T1 - Alkali-aktivierte Hüttensandbetone – CO2-reduzierte Bindemittel mit hohem Korrosionsschutzpotential N2 - Durch den Ersatz von Portlandzement können alkali-aktivierte Bindemittel einen bedeutenden Beitrag zur Verringerung der durch die Zementklinkerherstellung verursachten CO2-Emissionen leisten. Für die Verwendung von alkali-aktivierten Bindemitteln in Stahlbetonkonstruktionen, die Chloriden oder Carbonatisierung ausgesetzt sind, ist die Fähigkeit des Stahls, den passiven Zustand zu erreichen und aufrechtzuerhalten, von großer Bedeutung. Die Prozesse der Deckschichtbildung von Stahl in alkali-aktivierten Materialien unterscheiden sich jedoch zum Teil grundlegend von denen in Portlandzementen. Alkali-aktivierte Hüttensandbetone weisen gute technische Eigenschaften auf, bisher fehlen jedoch grundlegende Kenntnisse bzgl. ihrer schützenden Wirkung bei korrosiven Angriffen. Dies ist vor allem auf ihre sulfidhaltige Porenlösung zurückzuführen, welche die elektrochemischen Eigenschaften der Stahloberfläche beeinflusst und die Verwendung herkömmlicher Bewertungsmaßstäbe erschwert. Es werden erste Ergebnisse eines DFG-Forschungsprojektes vorgestellt, in dem das Passivierungsverhalten von Stahl in alkali-aktivierten Hüttensandmörteln unterschiedlicher Zusammensetzungen sowie in Mörteln auf Basis hüttensandhaltiger Normzemente untersucht wird. Über einen Zeitraum von mindestens 28 Tagen werden an Zylinderprüfkörpern im 3-Elektroden-Aufbau das Ruhepotential sowie die Polarisationswiderstände der Stahlelektroden ermittelt. T2 - 10. DAfStb-Jahrestagung mit 62. Forschungskolloquium CY - Aachen, Germany DA - 26.09.2023 KW - Bewehrung KW - Stahlkorrosion KW - Hüttensandmehl KW - Sulfid PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-593775 DO - https://doi.org/10.18154/RWTH-2023-06676 SP - 233 EP - 238 PB - RWTH Aachen CY - Aachen AN - OPUS4-59377 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hüsken, Götz A1 - Wagner, L.-C. A1 - Gluth, Gregor A1 - Pirskawetz, Stephan A1 - Kühne, Hans-Carsten T1 - Application of Steel Fibres in Alkali-Activated Mortars N2 - Alkali-activated materials are ideal for the repair of concrete structures in harsh environmental conditions due to their high durability in chemically aggressive environments. However, slag-based mortars, in particular, are prone to shrinkage and associated cracks. In this respect, the application of steel fibres is one solution to reduce the formation of shrinkage induced cracks and to improve post cracking behaviour of these mortars. This study investigated the influence of two different types of steel fibres on the tensile properties of two alkali-activated mortars. Direct tensile tests and single fibre pull-outs were performed to analyse the determining failure modes both on macro and micro scale. Mechanical testing was accompanied by non-destructive testing methods such as digital image correlation and acoustic emission for a detailed analysis of the fracture process. T2 - Local Mechanical Properties - LMP 2019 CY - Prague, Czech Republic DA - 06.11.2019 KW - Alkali-activated materials KW - Fibre pull-out KW - Steel fibres KW - Tensile strength PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-509291 UR - https://ojs.cvut.cz/ojs/index.php/APP/article/view/6695 DO - https://doi.org/10.14311/APP.2020.27.0090 VL - 27 SP - 90 EP - 95 CY - Prague, Czech Republic AN - OPUS4-50929 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sterthaus, Jens A1 - Ballheimer, Viktor A1 - Kuschke, Christian A1 - Wille, Frank T1 - Numerical analysis of bolted trunnion systems of packages for radioactive materials N2 - Packages for the transport of radioactive material are generally equipped with particular components for crane operations and supporting the package during transport. As an example of such components the bolted trunnion system of heavy packages are analysed in this paper. According to the German guideline BAM-GGR 012 created by the BAM Federal Institute for Materials Research and Testing for analysis and assessment of bolted lid and trunnion Systems, the finite element (FE) method is to be used preferably in the analysis of such kind of structures to obtain more accurate and detailed Information about their stressing. The FE model of a trunnion System should include the trunnion itself, the bolts and an appropriate part of the packaging wall with necessary contact conditions on all interfaces between these components. The use of solid finite elements, which is generally recommended in the BAM-GGR 012 guideline, leads to local stress and strain fields as a result of the calculation. The modelling strategy, e.g. the way of modelling interaction between the components of the trunnion System, has an essential impact on these local values. The effect of different assumptions in a FE model is demonstrated in this paper using the calculation results for a reference trunnion System. The approaches for preparation and Interpretation of results in connection with local or nominal assessment criteria are discussed as well. T2 - ASME 2012 Pressure Vessels and Piping Division Conference - PVP 2012 CY - Toronto, Ontario, Canada DA - 15.07.2012 KW - Bolted trunnion KW - German guideline BAM-GGR 012 KW - Local stress and strain fields KW - Local and nominal assessment criteria PY - 2012 SP - 1 EP - 6 PB - American Society of Mechanical Engineers (ASME) CY - New York, NY AN - OPUS4-26835 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Steppan, Enrico A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - High-energy synchrotron study of the stress-strain behavior of hydrogen-charged high strength steel N2 - The ambition for light weight construction while simultaneously increasing the loading capacity is a main aim of many industries such as crane, vehicle, bridge construction, shipbuilding and plant construction. This aim is achieved by application of high strength structural steels with yield strengths of up to 1300 MPa. The plate thickness can be reduced and consequently the service load is increased. High strength structural steels are quenched and tempered and/or even thermo-mechanically processed. Their superior properties are due to precipitations formed by micro alloying elements finely dispersed in a martensitic matrix. The aim of this study was to observe the influence of hydrogen in the microstructure of high strength structural steel with the yield strength of 1300 MPa by using diffraction methods. Energy dispersive X-ray diffraction (EDXRD) available at the EDDI beam line of the HZB in Berlin Germany was utilized to compare the stress-strain behavior of samples exhibiting varying amounts of hydrogen during tensile loading. T2 - Visual-JW2012 - International Symposium on Visualization in Joining and Welding Science through Advanced Measurements and Simulation CY - Osaka, Japan DA - 28.11.2012 KW - High strength structural steel KW - Hydrogen diffusion KW - Hydrogen assisted cold cracking KW - Energy dispersive X-ray diffraction PY - 2012 IS - IWIS-17 SP - 228 EP - 229 PB - Joining and Welding Research Institute (JWRI) CY - Osaka AN - OPUS4-27396 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Viehrig, H.-W. A1 - Baer, Wolfram A1 - Gerwien, Peter A1 - Grundmann, N. A1 - Houska, M. A1 - Lucon, E. A1 - Mottitschka, T. A1 - Trubitz, P. T1 - Bestimmung der J-Risswiderstandskurve an einem zähen Reaktordruckbehälterstahl - Ergebnisse eines Round Robin Tests N2 - Die Bruchzähigkeit von Stählen kann im elastisch-plastischen Beanspruchungsbereich anhand von Risswiderstandskurven z.B. nach den Prüfnormen ISO 12135 und ASTM E1820 ermittelt werden, wobei die duktile Rissausbreitung mittels Mehr- oder Einprobenverfahren gemessen wird. Das Teilentlastungsverfahren ist das am weitesten verbreitete Einprobenverfahren zur Ermittlung von Risswiderstandskurven. Die Risswiderstandskurven wurden mit 1TC(T)-Proben aus einem Reaktordruckbehälterstahl mit dem Teilentlastungsverfahren von vier Prüflaboratorien gemessen und nach beiden Prüfnormen ausgewertet. Im Beitrag werden die möglichen Fehlerquellen bei der Anwendung des Teilentlastungsverfahrens und die Unterschiede bei der Auswertung nach beiden T2 - 45. Tagung des DVM-Arbeitskreises Bruchvorgänge CY - Berlin, Germany DA - 19.02.2013 KW - Duktiles Risswachstum KW - J-Integral KW - Teilentlastungsverfahren KW - Bruchzähigkeit KW - Ductile tearing KW - J integral KW - Unloading compliance KW - Fracture toughness KW - Bruchmechanik KW - Round Robin KW - Risswiderstandskurve PY - 2013 N1 - Serientitel: DVM-Bericht – Series title: DVM-Bericht VL - 245 SP - 91 EP - 100 AN - OPUS4-27912 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baensch, Franziska A1 - Baer, Wolfram A1 - Chruscicki, Sebastian A1 - Habib, Abdel Karim A1 - Homann, Tobias A1 - Hussels, Maria-Teresa A1 - Prager, Jens A1 - Schmidt, Dirk A1 - Stajanca, Pavol A1 - Weltschev, Margit A1 - Wossidlo, Peter T1 - Feasibility study - Continuous monitoring of pipes using distributed acoustic and fibre optic sensors N2 - The feasibility study „AGIFAMOR. Ageing infrastructures – distributed acoustic monitoring of pipes” is an interdisciplinary research project at BAM internally financed from 2015 to 2018. Therefore, the quite young fibre optic sensing technology of distributed acoustic sensing (DAS) was investigated to possibly be extended towards a global condition monitoring system for pipelines operating in real time. DAS is a highly dynamic fibre optic sensing technology based on the method of coherent optical time domain reflectometry (C-OTDR). DAS allows capturing strain changes in the range of kHz. For the experimental work, the most suitable application yielding an optimum sensitivity was proven by wrapping a standard single-mode silica fibre around the pipe. The DAS sensitivity was investigated regarding the detection of 1) incidents that initiate propagation of acoustic waves in the pipe wall, 2) changes inside the pipeline causing altered flow and 3) damage development in the pipe wall. Therefore, several testing setups in laboratory as well as in real scale were realized. For comparison purposes, experiments were accompanied by acoustic emission analyses and by measurements with accelerometers. DAS was found to be very sensitive to gas ignition and its propagation across the pipe. Furthermore, the ability of DAS to detect and localize acoustic signals associated with pipeline leakage was demonstrated. The detection of crack formation and propagation within the pipe wall by means of DAS was studied during bending tests on several pipe segments, but was not proven so far with certainty. As expected, these studies turned out as the most difficult challenge due to the random occurrence and transient nature of microscopic damage phenomena. T2 - Proceedings of the International Symposium on Structural Health Monitoring and Nondestructive Testing CY - Saarbrücken, Germany DA - 04.10.2018 KW - Accelerometers KW - Acoustic emission KW - Fibre optic acoustic sensing KW - Continous monitoring KW - Bending tests on pipe segments KW - Leak detection PY - 2018 SP - Paper 21 AN - OPUS4-46375 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram A1 - Müller, Karsten A1 - Wossidlo, Peter A1 - Klingbeil, Dietmar T1 - Dynamic fracture toughness behaviour of ductile cast iron with respect to structural integrity assessment N2 - Modern structural integrity assessment procedures in the field of nuclear related technology incorporate fracture mechanical concepts. Therefore, they inevitably require the availability of both, loading parameters as well as material characteristics in terms of fracture mechanical quantities. Especially in case of dynamic loading conditions, the methods for the determination of the loading parameters need further improvement and there is a lack of material characteristics as well. In Germany, ductile cast iron (DCI) is used for heavy-sectioned casks for radioactive materials. New developments in cask design and efforts to extend the application limits require further investigations. The present study is part of an ongoing fracture mechanics research programme of BAM which is focused on the systematic mechanical and fracture mechanical material characterisation of DCI materials under dynamic loading conditions. In this study, results of fracture mechanics investigations on ductile cast iron from an original DCI container with a wide variety of microstructure under dynamic loading conditions in the temperature range from -50 °C to +22 °C are presented. Large scale as well as small scale single edge crack bend specimens SE(B) with thicknesses of 140 mm and 15 mm, respectively were tested. Furthermore, it is reported on the results of a finite element simulation of the dynamic large scale fracture mechanics tests. Strength and deformation characteristics were determined in dynamic tensile tests. They are discussed with respect to the influence of pearlite content and test temperature. The material specific experimental difficulties in the determination of reliable dynamic crack initiation toughness values of DCI are outlined. T2 - 17th International Conference on Structural Mechanics in Reactor Technology ; SMiRT 17 CY - Prague, Czech Republic DA - 2003-08-17 KW - Dynamic fracture toughness KW - Ductile cast iron KW - Structural integrity KW - Component KW - Specimen geometry KW - Testing KW - Loading rate KW - Test temperature KW - Microstructure KW - Graphite morphology KW - Crack initiation toughness KW - Analysis procedure KW - Finite element simulation KW - Fracture mechanics PY - 2003 IS - G04-4 SP - 1 EP - 8 CY - Prague AN - OPUS4-2856 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stajanca, Pavol A1 - Baensch, Franziska A1 - Baer, Wolfram A1 - Chruscicki, Sebastian A1 - Homann, Tobias A1 - Seifert, Stefan A1 - Schmidt, Dirk A1 - Weltschev, Margit A1 - Wossidlo, Peter A1 - Habib, Abdel Karim T1 - Monitoring of pipes by distributed acoustic fibre optic sensors – A large-scale test on a pipeline under realistic operation condition N2 - The monitoring of oil and gas pipelines by means of distributed fibre optic sensors is becoming common. The most recent development in the field of fibre optic sensing is the distributed acoustic sensing (DAS), which allows to detect and to localize third party threats to pipelines. For this purpose, fibre optic telecommunication cables located close to the pipelines are usually used. However, DAS carries a far greater potential for continuous condition monitoring of pipelines. The interdisciplinary research project AGIFAMOR (Ageing Infrastructures – Fibre Optic Monitoring of Pipes) at BAM investigates a new technical approach to extend the application field of DAS towards the detection and localization of acoustic signals that indicate critical alterations and certain damage scenarios originated from within the pipeline or the pipe wall. Therefore, the optical fibre sensors are applied onto the pipe itself and the application procedure towards an optimal acoustic signal transduction is optimized. A number of laboratory scale experiments were performed focusing on the signal transmission of acoustic signals as well as the detection of damages in the pipe wall by means of DAS. Furthermore, real-scale tests on a pipeline DN100 of 38m length have been carried out at the BAM test site for technical safety (BAM-TTS) to study the detection and localization of leaks and of changing flow profiles due to corrosion or sedimentation processes. T2 - 13th Pipeline Technology Conference CY - Berlin, Germany DA - 12.03.2018 KW - Pipeline monitoring KW - Distributed acoustic sensing KW - Fiber optic sensing PY - 2018 SN - 2198-428X SP - Poster session, paper 9, 1 EP - 8 PB - EITEP (Euro Institute for Information and Technology Transfer in Environmental Protection) CY - Hannover AN - OPUS4-44519 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram A1 - Häcker, Ralf T1 - Untersuchungen zum Verformungs- und Bruchverhalten von Gusseisenwerkstoffen mit Kugelgraphit bei dynamischer Beanspruchung / Investigations on the deformation and failure behaviour of ductile cast iron materials at high strain rate loading T2 - 31. Tagung des DVM-Arbeitskreises Bruchvorgänge CY - Darmstadt, Germany DA - 1999-02-24 KW - Verformungs- und Bruchverhalten KW - Gusseisenwerkstoffe KW - Dynamische Belastung KW - Dehnrate KW - Prüftemperatur KW - Gefüge KW - Thermisch aktiviertes Fließen KW - Deformation and failure behaviour KW - Ductile cast iron KW - High strain rate loading KW - Strain rate KW - Test temperature KW - Microstructure KW - Thermally activated flow PY - 1999 N1 - Serientitel: DVM-Bericht – Series title: DVM-Bericht SP - 125 EP - 134 PB - Deutscher Verband für Materialforschung und -prüfung CY - Hamburg AN - OPUS4-11901 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baensch, Franziska A1 - Hussels, Maria-Teresa A1 - Chruscicki, Sebastian A1 - Baer, Wolfram A1 - Wossidlo, Peter A1 - Homann, Tobias A1 - Prager, Jens A1 - Schmidt, Dirk A1 - Weltschev, Margit A1 - Habib, Abdel Karim T1 - BAM-Projekt AGIFAMOR – Zustandsüberwachung von Rohrleitungen N2 - Rohrleitungssysteme sind aufgrund ihrer Funktion und Ausdehnung für den Betrieb, die Verfügbarkeit und die Sicherheit von Industrieanlagen von besonderer Bedeutung. Die bisher in definierten Intervallen durchgeführten, wiederkehrenden Prüfungen zur Sicherstellung leckagefreier Rohrleitungen sind kostenintensiv und mit einem erhöhten Aufwand verbunden. Mit dem interdisziplinären Forschungsprojekt AGIFAMOR (Ageing Infrastructures – Akustisches Monitoring von Rohrleitungen) arbeitet die BAM an der Entwicklung und Erprobung einer örtlich und zeitlich kontinuierlichen Zustandsüberwachung von Rohrleitungen basierend auf einem faseroptischen akustischen Messsystem, welches einen vergleichsweise geringen Installationsaufwand der Sensoren erfordert. Mit diesem Verfahren sollen vor allem betriebsbedingte Schädigungen infolge von Korrosion sowie daraus entstehende Pittings oder Risse erkannt und damit Leckagen verhindert werden. Im Rahmen einer Machbarkeitsstudie zum Teilaspekt „Detektion von Risswachstum“ wurde ein 2,5 m langes, definiert vorgekerbtes Stahlrohr mit der faseroptischen Sensorik (FOS) ausgestattet und quasistatisch unter 4-Punkt-Biegung belastet. Mit fortschreitender Belastung wächst, ausgehend vom vorhandenen Außenumfangskerb, ein Riss im Stahlrohr bis zum Erreichen der Leckage – in der Praxis ein gefährliches Schadensszenario. Parallel zur FOS erfolgten Messungen mit Schallemissionssensoren, Beschleunigungssensoren und Potentialsonden, deren Ergebnisse die Interpretation der FOS-Messergebnisse unterstützen sollen. T2 - 21. Kolloquium Schallemission CY - Fulda, Germany DA - 09.03.2017 KW - Beschleunigungssensoren KW - Faseroptische Sensorik KW - Schallemission KW - Monitoring KW - Rohrleitung PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-401811 SN - 978-3-940283-82-5 VL - DGZfP-BB 159 SP - Vortrag 17, 1 EP - 8 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-40181 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, Marcel A1 - Baer, Wolfram A1 - Mayer, Uwe A1 - Weihe, Stephan T1 - Investigation of the Master Curve Concept for Ferritic Ductile Cast Iron N2 - Within fracture mechanics safety assessment for steels in nuclear technology, the probabilistic master curve (MC) concept according to ASTM E1921 is currently used for quasi-static loading conditions as a supplement to the established deterministic ASME reference curve concept. However, for ductile cast iron (DCI), a systematic review of potential modifications to the assumptions and the procedure according to ASTM E1921 and an associated validation are still lacking. For this reason, the application of the fracture mechanics MC concept to ferritic ductile cast iron is being investigated in a recently started joint research project between MPA Stuttgart and BAM Berlin. According to the IAEA guidelines SSG 26, the safety assessment of DCI containers for transport as well as storage of radioactive materials is based on the fracture mechanics criterion of general crack initiation exclusion. Within this context, the focus of the current research project is on the further development of brittle fracture safety assessment methods. Therefore, a methodology shall be established to determine and assess dynamic fracture toughness values of DCI in the ductile-to-brittle transition regime, using samples extracted from a component. For the experimental program, a DCI material will be produced as it is generally used for transport and storage containers. A basic mechanical-technological material characterization consisting of tensile, Charpy and Pellini tests is planned and a comprehensive fracture mechanics test program was compiled covering dynamic testing of DC(T)9, C(T)25, C(T)50, SE(B)10, SE(B)25, and SE(B)140 specimens. Numerical analyses of different specimen geometries and test setups are planned to investigate the influences of stress triaxiality and loading rate. Throughout the experimental program, the microstructure-property relationship will be investigated based on quantitative metallographic and fractographic analyses. Finally, different MC assessment strategies will be considered and modifications will be made if necessary. T2 - 21st International Symposium ASTM/ESIS Symposium on Fatigue and Fracture Mechanics CY - Washington, DC, USA DA - 08.11.2023 KW - Ductile Cast Iron KW - Dynamic Fracture Toughness KW - Cleavage Fracture KW - Master Curve Concept PY - 2023 SP - 1 EP - 5 PB - ASTM International CY - West Conshohocken, PA AN - OPUS4-59064 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, Marcel A1 - Baer, Wolfram A1 - Mayer, Uwe A1 - Weihe, Stefan T1 - Master Curve-Auswertungen und Untersuchung des Größeneffekts für c(t)-proben - Aktuelle Erkenntnisse zur Untersuchung des Master Curve Konzepts für ferritisches Gusseisen mit Kugelgraphit bei dynamischer Beanspruchung N2 - Ausgehend vom Stand des Regelwerkes und der Forschung wird in einem BMUV-Verbundprojekt zwischen der MPA Stuttgart und der BAM Berlin die Anwendung des Master Curve (MC)-Konzepts auf ferritisches Gusseisen mit Kugelgraphit (DCI) untersucht. Ziel des Verbundprojekts ist die Anwendbarkeit des MC-Konzepts näher zu untersuchen und ggf. Modifikationen vorzunehmen, um eine Bewertungsmethode für die dynamische Bruchzähigkeit von DCI im Übergangsbereich zu erarbeiten. Auf den Jahrestagungen 2023 und 2024 des DVM-AK Bruchmechanik und Bauteilsicherheit wurden bereits der Forschungsansatz sowie erste Ergebnisse des Projekts MCGUSS präsentiert. Der Beitrag für die diesjährige Tagung soll nun MC-Auswertungen und den Größeneffekt für C(T)-Proben aus DCI diskutieren. T2 - 57. Tagung des DVM-Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Köln, Germany DA - 18.02.2025 KW - Versuche KW - Master Curve KW - Bruchmechanik KW - Dynamische Beanspruchung KW - Gusseisen mit Kugelgraphit PY - 2025 DO - https://doi.org/10.48447/BR-2025-495 SP - 123 EP - 129 PB - DVM-Verlag CY - Berlin AN - OPUS4-62555 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, Marcel A1 - Mayer, Uwe A1 - Baer, Wolfram T1 - Investigating the Applicability of the Master Curve Concept for Ductile Cast Iron – Early Results for 2 Different Test Temperatures N2 - Based on the state-of-the-art research and regulations, the application of the fracture mechanics master curve (MC) concept to ferritic ductile cast iron (DCI) is being investigated in a joint research project between MPA Stuttgart and BAM Berlin. This paper outlines the research approach, the planned investigations and first results of the experimental program. T2 - 8th SEDS Workshop: Safety of Extended Dry Storage CY - Garching, Germany DA - 15.05.2024 KW - Dynamic fracture KW - Brittle fracture KW - Ductile cast iron KW - Master Curve PY - 2024 SP - 1 EP - 4 AN - OPUS4-60013 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nerger, Tino A1 - Neumann, Patrick P. A1 - Weller, Michael G. T1 - A New Approach: Passive Smart Dust for Detection of Hazardous Substances N2 - Remote sensing of hazardous substances is a key task that can be achieved with the help of remotely operated platforms equipped with specific sensors. A huge variety of methods and used vehicles have been developed for different purposes in recent years. The term smart dust refers to a science fiction novel and develop shortly after into a research proposal at UC Berkley funded by DARPA. Subsequently, the topic gained attraction but was overall considered as to complex for the technologies available at that time. In the launched passive smart dust project, we shift to a simple “chemical intelligent” passive sensor particle on the ground combined a read-out active sensor attached to an Unmanned Aerial Vehicle (UAV). The reactive particle surface can be preadjusted in the lab for exact desired properties regarding certain reactions to hazardous substances. Moreover, the aimed interaction with the active sensor can be modified. Planed applications allow for different materials e.g., for short time measurement, being ecologically degradable, or weather stable for long time monitoring. T2 - 38th Danubia-Adria Symposium on Advances in Experimental Mechanics CY - Poros, Greece DA - 20.09.2022 KW - Smart Dust KW - Drone KW - Remote Detection KW - Hazardous substances PY - 2022 SP - 1 EP - 2 CY - Athens, Greece AN - OPUS4-55925 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Döring, Sarah A1 - Weller, Michael G. A1 - Reinders, Yvonne A1 - Konthur, Zoltán A1 - Jaeger, Carsten T1 - Challenges and Insights in Absolute Quantification of Recombinant Therapeutic Antibodies by Mass Spectrometry: An Introductory Review N2 - This review describes mass spectrometry (MS)-based approaches for the absolute quantification of therapeutic monoclonal antibodies (mAbs), focusing on technical challenges in sample treatment and calibration. Therapeutic mAbs are crucial for treating cancer, inflammatory, infectious, and autoimmune diseases. We trace their development from hybridoma technology and the first murine mAbs in 1975 to today’s chimeric and fully human mAbs. With increasing commercial relevance, absolute quantification of mAbs, traceable to SI units, has attracted attention from science, industry, and national metrology institutes (NMIs). Quantification of proteotypic peptides after enzymatic digestion using liquid chromatography-tandem mass spectrometry (LC-MS/MS) has emerged as the most viable strategy, though methods targeting intact mAbs are still being explored. We review peptide-based quantification, focusing on critical experimental steps like denaturation, reduction, alkylation, choice of digestion enzyme, and selection of signature peptides. Challenges in amino acid analysis (AAA) for quantifying pure mAbs and peptide calibrators, along with software tools for targeted MS data analysis, are also discussed. Short explanations within each chapter provide newcomers an overview of the field’s challenges. Finally, we discuss prospects and limitations of developing standardized protocols and certified reference materials (CRMs) and suggest future applications of newer technologies for the absolute quantification of therapeutic antibodies. KW - Antibody KW - Mass spectrometry KW - Absolute quantification KW - Metrology KW - Reference products PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-621841 DO - https://doi.org/10.20944/preprints202412.1081.v1 SP - 1 EP - 22 PB - MDPI AN - OPUS4-62184 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Döring, Sarah A1 - Wulfes, Birte S. A1 - Atanasova, Aleksandra A1 - Jaeger, Carsten A1 - Walzel, Leopold A1 - Tscheuschner, Georg A1 - Flemig, Sabine A1 - Gawlitza, Kornelia A1 - Feldmann, Ines A1 - Konthur, Zoltán A1 - Weller, Michael G. T1 - Corundum Particles as Trypsin Carrier for Efficient Protein Digestion N2 - Reusable enzyme carriers are valuable for proteomic workflows, yet many supports are expensive or lack robustness. This study describes the covalent immobilization of recombinant trypsin on micrometer-sized corundum particles and assesses their performance in protein digestion and antibody analysis. The corundum surface was cleaned with potassium hydroxide, silanized with 3-aminopropyltriethoxysilane and activated with glutaraldehyde. Recombinant trypsin was then attached, and the resulting imines were reduced with sodium cyanoborohydride. Aromatic amino acid analysis (AAAA) estimated an enzyme loading of approximately 1 µg/mg. Non-specific adsorption of human plasma proteins was suppressed by blocking residual aldehydes with a Tris-glycine-lysine buffer. Compared with free trypsin, immobilization shifted the temperature optimum from 50 to 60 °C and greatly improved stability in 1 M guanidinium hydrochloride. Activity remained above 80 % across several reuse cycles, and storage at 4 °C preserved functionality for weeks. When applied to digesting the NISTmAb, immobilized trypsin provided peptide yields and sequence coverage comparable to soluble enzyme and outperformed it at elevated temperatures. MALDI-TOF MS analysis of Herceptin digests yielded fingerprint spectra that correctly identified the antibody and achieved >60 % sequence coverage. The combination of low cost, robustness and analytical performance makes corundum-immobilized trypsin an attractive option for research and routine proteomic workflows. KW - Aluminum oxide KW - Mass spectrometry KW - Enzyme immobilization KW - Antibodies KW - Protein quantification PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-647944 DO - https://doi.org/10.20944/preprints202510.2002.v1 SP - 1 EP - 22 PB - Preprints.org AN - OPUS4-64794 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Nerger, Tino A1 - Neumann, Patrick P. A1 - Weller, Michael G. T1 - Drone-Based Localization of Hazardous Chemicals by Passive Smart Dust N2 - The distribution of tiny sensors over a specific area was first proposed in the late 1990s as a concept known as Smart Dust. Several efforts focused primarily on computing and networking capabilities but quickly ran into problems related to power supply, cost, data transmission, and environmental pollution. To overcome these limitations, we propose using paper-based (confetti-like) chemosensors that exploit the inherent selectivity of chemical reagents, such as colorimetric indicators. In this work, cheap and biodegradable passive sensors made from cellulose could successfully indicate the presence of hazardous chemicals, e.g., strong acids, by a significant color change. A conventional color digital camera attached to a drone could easily detect this from a safe distance. The collected data was processed to define the hazardous area. Our work presents a combination of the smart dust concept, chemosensing, paper-based sensor technology, and low-cost drones for flexible, sensitive, economical, and rapid detection of hazardous chemicals in high-risk scenarios. N2 - Die Verteilung winziger Sensoren über ein bestimmtes Gebiet wurde erstmals Ende der 1990er Jahre als Konzept namens „Smart Dust“ vorgeschlagen. Mehrere Bemühungen konzentrierten sich hauptsächlich auf Rechen- und Netzwerkfähigkeiten, stießen jedoch schnell auf Probleme im Zusammenhang mit der Stromversorgung, den Kosten, der Datenübertragung und der Umweltverschmutzung. Um diese Einschränkungen zu überwinden, schlagen wir die Verwendung von papierbasierten (konfettiartigen) Chemosensoren vor, die die inhärente Selektivität chemischer Reagenzien, wie z. B. kolorimetrischer Indikatoren, nutzen. In dieser Arbeit konnten günstige und biologisch abbaubare passive Sensoren aus Zellulose erfolgreich das Vorhandensein gefährlicher Chemikalien, z.B. starker Säuren, durch eine deutliche Farbänderung anzeigen. Eine herkömmliche Farb-Digitalkamera, die an einer Drohne befestigt ist, konnte dies aus sicherer Entfernung leicht erkennen. Die gesammelten Daten wurden verarbeitet, um den Gefahrenbereich zu abzugrenzen. Unsere Arbeit stellt eine Kombination aus dem Smart-Dust-Konzept, Chemosensorik, papierbasierter Sensortechnologie und kostengünstigen Drohnen für eine flexible, empfindliche, wirtschaftliche und schnelle Erkennung gefährlicher Chemikalien in Hochrisikoszenarien dar. KW - Confetti KW - Remote sensing KW - Drones KW - UAV KW - Optical detection KW - Chemosensor KW - pH indicator KW - Paper-based sensors KW - Harmful chemicals KW - Chemical desaster PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-621284 DO - https://doi.org/10.20944/preprints202408.0030.v1 SP - 1 EP - 17 PB - MDPI CY - Basle, Switzerland AN - OPUS4-62128 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Tannenberg, Robert A1 - Tscheuschner, Georg A1 - Raab, Christopher A1 - Flemig, Sabine A1 - Döring, Sarah A1 - Ponader, Marco A1 - Thurmann, Melinda A1 - Paul, Martin A1 - Weller, Michael G. T1 - Simplified Sample Preparation and Lateral Flow Immunoassay for the Detection of Plant Viruses N2 - Lateral flow immunoassays (LFA) are widely used for decentralized testing, but their application for in-field plant virus diagnostics is often limited by tedious sample preparation. Here, we present a simplified dipstick LFA for the detection and monitoring of cowpea chlorotic mottle virus (CCMV) as a model plant pathogen. The assay employes a monoclonal mouse antibody for capture and a polyclonal rabbit antibody conjugated to 80-nm gold nanoparticles for detection. Conventional sample and conjugate pads are omitted, allowing the test strips to be dipped directly into wells containing plant extract and antibody-gold conjugate. In addition, no plastic casing was necessary, which significantly reduces waste. It was shown that CCMV concentrations as low as 4 μg/L or 400 pg per sample could be reliably detected in 15 minutes. Specificity tests confirmed that other plant viruses, cowpea mosaic virus (CPMV) and tobacco mosaic virus (TMV), did not produce false positive results. Furthermore, we describe a field-compatible sampling procedure using a manual punch and a disposable syringe. This step combines sample grinding, extraction, and conjugate reconstitution within the syringe frit, enabling the analysis of punched leaf discs without laboratory equipment. When applied to CCMV-infected cowpea plants, the assay revealed systemic infection before visual symptoms became apparent. This work demonstrates that simplified LFAs combined with innovative sampling techniques can provide sensitive, specific, and rapid diagnostics for crop monitoring and support early intervention strategies in agriculture. N2 - Lateral Flow Immunoassays (LFA) werden häufig für dezentrale Tests verwendet, aber ihre Anwendung für die Diagnose von Pflanzenviren im Feld wird oft durch die mühsame Probenvorbereitung eingeschränkt. Hier stellen wir einen vereinfachten Dipstick-LFA zum Nachweis und zur Überwachung des Cowpea Chlorotic Mottle Virus (CCMV) als Modellpflanzenpathogen vor. Der Assay verwendet einen monoklonalen Maus-Antikörper zum Einfangen des Virus und einen polyklonalen Kaninchen-Antikörper, der an 80-nm-Goldnanopartikel konjugiert ist, zum Nachweis. Herkömmliche Proben- und Konjugatpads entfallen, sodass die Teststreifen direkt in Vertiefungen getaucht werden können, die Pflanzenextrakt und Antikörper-Gold-Konjugat enthalten. Darüber hinaus war keine Kunststoffhülle erforderlich, was den Abfall erheblich reduziert. Es zeigte sich, dass CCMV-Konzentrationen von nur 4 μg/L oder 400 pg pro Probe innerhalb von 15 Minuten zuverlässig nachgewiesen werden konnten. Spezifitätstests bestätigten, dass andere Pflanzenviren, das Cowpea Mosaic Virus (CPMV) und das Tobacco Mosaic Virus (TMV), keine falsch positiven Ergebnisse lieferten. Darüber hinaus beschreiben wir ein feldtaugliches Probenahmeverfahren unter Verwendung eines manuellen Stanzers und einer Einwegspritze. Dieser Schritt kombiniert das Zerkleinern der Probe, die Extraktion und die Rekonstitution des Konjugats innerhalb der Spritzenfritte und ermöglicht so die Analyse von ausgestanzten Blattscheiben ohne Laborausrüstung. Bei der Anwendung auf CCMV-infizierte Augenbohnenpflanzen zeigte der Test eine systemische Infektion, bevor visuelle Symptome sichtbar wurden. Diese Arbeit zeigt, dass vereinfachte LFAs in Kombination mit innovativen Probenahmetechniken eine sensitive, spezifische und schnelle Diagnostik für die Überwachung von Nutzpflanzen ermöglichen und frühzeitige Interventionsstrategien in der Landwirtschaft unterstützen können. KW - Vigna unguiculata KW - Cowpea KW - Sample preparation KW - Plant pathogen KW - Mobile detection KW - Crop monitoring KW - Plastic waste KW - Lateral flow immunoassay KW - Plant virus KW - Sample pad KW - Conjugate pad PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-651731 DO - https://doi.org/10.20944/preprints202512.1492.v1 SP - 1 EP - 14 PB - MDPI CY - Basle, Switzerland AN - OPUS4-65173 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Bosc-Bierne, Gaby A1 - Weller, Michael G. T1 - Investigation of Impurities in Peptide Pools N2 - Peptide pools are important research tools in different biomedical fields. They consist of a complex mixture of defined peptides, which places high demands on the production and quality control of these products. Previously it was shown that the combination of UHPLC with high-resolution mass-spectrometry (HRMS) is a fast and powerful method to confirm the relative concentration and the structural identity of all peptides expected to be in the pool. In this work, the additional information contained in the UV chromatograms and mass spectra is used to search for impurities due to synthesis by-products, degradation during storage and transportation and to identify possible analytical artifacts. It was shown that most impurities are only present in trace amounts and can be considered uncritical for most applications. The most frequent and perhaps unexpected impurities were homo- and heterodimers caused by the free cysteines contained in these peptide pools. Furthermore, pyroglutamate and aspartimide formation, deamidation, methionine oxidation, and amino acid deletions could be found. This list is not intended to be comprehensive, but rather a brief guide to quickly identify impurities and, in the long term, to suggest possible changes in the composition of the peptide pools to avoid such impurities by design or by special precautions. N2 - Peptidpools sind wichtige Forschungswerkzeuge in verschiedenen biomedizinischen Bereichen. Sie bestehen aus einer komplexen Mischung definierter Peptide, was hohe Anforderungen an die Produktion und Qualitätskontrolle dieser Produkte stellt. Zuvor wurde gezeigt, dass die Kombination von UHPLC mit hochauflösender Massenspektrometrie (HRMS) eine schnelle und leistungsstarke Methode ist, um die relative Konzentration und die strukturelle Identität aller Peptide zu bestätigen, die im Pool erwartet werden. In dieser Arbeit werden die zusätzlichen Informationen in den UV-Chromatogrammen und Massenspektren genutzt, um nach Verunreinigungen durch Synthesenebenprodukte, Abbau während der Lagerung und des Transports zu suchen und mögliche analytische Artefakte zu identifizieren. Es wurde gezeigt, dass die meisten Verunreinigungen nur in Spuren vorhanden sind und für die meisten Anwendungen als unkritisch angesehen werden können. Die häufigsten und vielleicht unerwartetsten Verunreinigungen waren Homo- und Heterodimere, die durch die in diesen Peptidpools enthaltenen freien Cysteine verursacht wurden. Außerdem konnten Pyroglutamat- und Aspartimidbildung, Deamidierung, Methioninoxidation und Aminosäurendeletion festgestellt werden. Diese Liste erhebt keinen Anspruch auf Vollständigkeit, sondern soll vielmehr eine kurze Anleitung zur schnellen Identifizierung von Verunreinigungen und langfristig zur Anregung möglicher Änderungen in der Zusammensetzung der Peptidpools sein, um solche Verunreinigungen durch Design oder besondere Vorsichtsmaßnahmen zu vermeiden. KW - Peptides KW - Mixtures KW - Degradation KW - Rearrangement KW - Cystein-Dimers KW - Immunology KW - MHC PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-621270 DO - https://doi.org/10.20944/preprints202412.0832.v1 SP - 1 EP - 16 PB - MDPI CY - Basle, Switzerland AN - OPUS4-62127 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Fischer, Janina T1 - Suspensionsarray-Fluoreszenzimmunoassay zur Multiplexbestimmung von SARS-CoV-2-Antikörpern N2 - Übergeordnetes Ziel der Arbeit war die Entwicklung und Optimierung eines Suspensionsarray-Fluoreszenzimmunoassays (SAFIA) für die simultane Bestimmung verschiedener gegen SARS-CoV-2-Proteine gerichtete Antikörper mittels Multiplexdetektion in komplexen Matrices wie humanen Blutserumproben. KW - SARS-CoV-2 KW - Corona KW - COVID-19 KW - Coronavirus KW - Virus KW - Spike-Protein KW - Nucleocapsid-Protein KW - RBD KW - SAFIA KW - LFIA KW - ELISA KW - Partikel KW - Mutationen KW - Neutralisierende Antikörper KW - Durchflusszytometrie KW - ACE2 PY - 2022 SP - 1 EP - 99 PB - Humboldt-Universität zu Berlin CY - Berlin AN - OPUS4-54722 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bienwald, Frank T1 - Optimierung der Aminosäureanalytik aromatischer Aminosäuren mittels HPLC N2 - Ausgehend von dem in der Literatur beschriebenen Verfahren zur Bestimmung aromatischer Aminosäuren konnte eine Analysemethode zur Proteinbestimmung über die optische Detektion von Tyrosin und Phenylalanin nach chromatographischer Trennung der Protein-Hydrolysate entwickelt werden, die gegenüber dem Verfahren aus der Literatur erhebliche Vorteile besitzt. Der Einsatz von Rundbodenvials stellt eine Neuerung und kostengünstige Alternative zu der konventionellen Hydrolyse in Vakuumhydrolyseröhrchen wie auch zu den Mikrowellenvials der Mikrowellenhydrolyse dar, die das Potential für Miniaturisierungen der Proben hat und sich zudem für große Probendurchsätze eignet. Anstelle der Mikrowellenheizungen wurde ein konventionelles Ölbad als Heizquelle verwendet. Somit ergibt sich eine Verbesserung auch darin, dass diese Methode geringere Geräteinvestitionen erfordert. Wie die Ergebnisse nahelegen, sind sowohl Salzsäure als auch Bromwasserstoffsäure geeignete Reagenzien, die bei der sauren Hydrolyse von Proteinen verwendet werden können. Mit Hilfe antioxidativer Zusätze können Nebenreaktionen erfolgreich vermieden werden. Hier haben sich L-Cystein und Oxalsäure als wirkungsvolle Additive herausgestellt. Wichtige Verbesserungen betreffen vor allem die Zeitersparnis bei der Hydrolyse, die Aufarbeitung der Hydrolysate und die chromatographischen Separationen. Erstere konnte gegenüber der konventionellen Methode von 22 Stunden auf 45 Minuten reduziert werden. Die chromatographische Trennung wurde so weit optimiert, dass die Laufzeit von 64 auf 35 Minuten verkürzt werden konnte. Zudem konnte auf das zeitraubende und kontaminationsanfällige Eindampfen der Hydrolysate verzichtet werden. Während der Aufarbeitung der Hydrolysate konnten die Menge eingesetzter Chemikalien reduziert und damit mögliche Störungen während der optischen Detektion verringert werden. Letztere wurde zum einen durch das Einbeziehen der UV-Absorption bei 260 nm erweitert, sodass eine Alternative zur Absorption bei 215 nm vorliegt, die ebenere Basislinien im Chromatogramm ermöglicht. Zum anderen wurde gezeigt, dass mit Hilfe der Fluoreszenz die Empfindlichkeit der Methode gegenüber der UV-Absorption erheblich verbessert werden kann. Anhand der Probe eines Birkenpollenextraktes ließ sich die Anwendbarkeit der optimierten Methode auf Realproben demonstrieren. KW - Aromatische Aminosäuren KW - Aromatic amino acid analysis KW - AAAA KW - Phenylalanine KW - Tyrosine KW - Hydrochloric acid KW - Hydrobromic acid KW - HCl KW - HBr KW - Chromatographie KW - Reversed-phase KW - Hydrolysis KW - AdvanceBio Peptide Map KW - PRP-C18 PY - 2017 SP - 1 EP - 71 PB - Humboldt-Universität zu Berlin CY - Berlin AN - OPUS4-54650 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bahri, Marwa T1 - Ortsspezifische Biokonjugation von humanen Antikörpern mit IgG-bindenden Peptiden N2 - Es wurde im Rahmen dieser Arbeit eine neue Methode der Biokonjugation entwickelt, die es ermöglicht humane Antikörper ortspezifisch mit IgG-bindenden Peptiden zu konjugieren. Als Basis fungierte ein Peptid, welches für den Einsatz gezielt modifiziert wurde. So sollte am C-Terminus ein Biotin eingefügt werden, dass für die spätere Detektion der Biokonjugation genutzt werden kann, während am N-Terminus ein Cross-Linker für die kovalente Bindung zum Antikörper eingefügt wurde. Das Biotin wurde mittels Biotin-Lysin eingebaut. Dies hat den Vorteil, dass die modifizierte Aminosäure direkt in der SPPS genutzt werden kann. Auch der Cross-Linker soll schon während der SPPS in das Peptid integriert werden. Als Cross Linker wurden die zwei heterobifunktionellen Succinimidyl(3-bromoacetamid)propionate und Succinimidyl(4-iodacetyl)aminobenzoat untersucht. Die Aktivierung des Peptides mit dem SBAP-Cross-Linker erfolgte am besten im pH-Bereich zwischen 7,0 und 9,0. Die Modifizierung des Peptides mit dem Iodid-Cross-Linker SIAB unter den gleichen Bedingungen zeigte allerdings keine zufriedenstellenden Ergebnisse. Da das erste Peptid allerdings in den Folgeexperimenten sehr gute Ergebnisse zeigte, musste kein weiterer Linker getestet werden. Zusätzlich zu der Cross-Linker-Wahl sollte der Abstand zwischen dem Cross-Linker und dem Grundgerüst des Peptides auf den Einfluss der Bindung untersucht werden. Dazu wurden drei Kontrollpeptide synthetisiert, die entweder um zwei Aminosäuren zwischen dem ursprünglichen N-Terminus des Peptides und dem SBAP-Linker verlängert wurden, keinen SBAP-Linker beinhalten oder die Verlängerung ohne SBAP-Linker besaßen. Die erfolgreiche Synthese aller vier Peptide wurde mittels MALDI-TOF-MS bestätigt. KW - Peptide KW - Bioconjugation KW - Crosslinker PY - 2020 SP - 1 EP - 82 PB - Humboldt-Universität zu Berlin CY - Berlin AN - OPUS4-54659 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Linke, Michael T1 - Entwicklung einer magnetischen Anreicherungsmethode für Peptidbibliotheken zur Identifizierung von Proteinbindern N2 - Das Ziel der Arbeit war die Entwicklung einer magnetischen Anreicherungsmethode für eine Bead-basierte Substanzbibliothek zur Identifizierung von Proteinbindern. Im Ramen des Forschungsbelegs wurde bereits eine Anreicherungsmethode für ein Modellsystem einer Peptidbibliothek entwickelt. Das Modellsystem bestand dabei aus zwei verschiedenen Peptiden. Als Positivkontrolle wurde das FLAG-Peptid gewählt, welches selektiv gegen den Anti-FLAG-Antikörper bindet, und ein weiteres Peptid wurde als Negativkontrolle gewählt. Anhand dieses Modellsystems konnte die zuvor entwickelte Anreicherungsmethode von 20.000 auf 1.000.000 Beads vergrößert werden. Hierbei wurde ein Anreicherungsfaktor von 818 und eine gute Wiederfindungsrate von 82% erreicht. KW - Peptide library KW - OBOC library KW - Enrichment KW - Magnetic beads KW - Protein interaction PY - 2018 SP - 1 EP - 86 PB - Humboldt-Universität zu Berlin CY - Berlin AN - OPUS4-54651 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Ciornii, Dmitri A1 - Hodoroaba, Vasile-Dan A1 - Benismail, Nizar A1 - Altmann, Korinna T1 - Project 2: Interlaboratory Comparison on detection and quantitative assessment of microplastics by use of spectroscopic and thermo-analytical methods N2 - Validated and standardized methods in microplastic analysis are indispensable for robust monitoring and regulation. Alongside also reference materials are urgently needed. An interlaboratory comparison (ILC) offers a powerful tool to address both these challenges. The present study aimed to compare the precision and accuracy of various methods for the detection and quantification of microplastic in a water-soluble matrix. Additionally, it evaluated the suitability of the test materials (containing environmentally relevant plastic polymers) to serve as reference materials for the microplastic analysis. In this ILC several most used thermo-analytical and spectroscopic methods have been addressed: Pyrolysis-Gas Chromatography Mass Spectrometry (Py-GC/MS), Thermal Extraction-Desorption Gas Chromatography Mass Spectrometry (TED-GC/MS), micro-Fourier Transform Infrared Spectroscopy (µ-FTIR), and micro-Raman Spectroscopy and Laser Direct Infrared Spectroscopy (LDIR). Microplastic powders of polyethylene (PE) and polyethylene terephthalate (PET) were used to assess suitability of the test materials (microplastic tablets) for method validation and use in the ILCs. The participants were guided with a SOP how to dissolve the test samples and, depending on their selected method, either quantify the number of particles (by the spectroscopic methods) or determine the mass fraction of microplastic particles per sample (by the thermo-analytical methods). KW - ILC KW - Microplastic KW - FTIR KW - Raman KW - TED-GC/MS KW - Py-GC/MS PY - 2024 SP - 1 EP - 16 AN - OPUS4-60612 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Tscheuschner, Georg A1 - Kaiser, Melanie N. A1 - Lisec, Jan A1 - Beslic, D. A1 - Muth, Thilo A1 - Krüger, M. A1 - Mages, H.-W. A1 - Dorner, B. G. A1 - Knospe, J. A1 - Schenk, J. A. A1 - Sellrie, F. A1 - Weller, Michael G. T1 - MALDI-TOF-MS-based identification of monoclonal murine anti-SARS-CoV-2 antibodies within one hour N2 - During the SARS-CoV-2 pandemic, many virus-binding monoclonal antibodies have been developed for clinical and diagnostic purposes. This underlines the importance of antibodies as universal bioanalytical reagents. However, little attention is given to the reproducibility crisis that scientific studies are still facing to date. In a recent study, not even half of all research antibodies mentioned in publications could be identified at all. This should spark more efforts in the search for practical solutions for the traceability of antibodies. For this purpose, we used thirty-five monoclonal antibodies against SARS-CoV-2 to demonstrate how sequence-independent antibody identification can be achieved by simple means applied onto the protein. First, we examined the intact and light chain masses of the antibodies relative to the reference material NIST-mAb 8671. Already half of the antibodies could be identified based solely on these two parameters. In addition, we developed two complementary peptide mass fingerprinting methods with MALDI-TOF-MS that can be performed in 45 minutes and had a combined sequence coverage of over 80%. One method is based on the partial acidic hydrolysis of the protein by 5 mM of sulfuric acid at 99 °C. Furthermore, we established a fast way for a tryptic digest without an alkylation step. We were able to show that the distinction of clones is possible simply by a brief visual comparison of the mass spectra. In this work, two clones originating from the same immunization gave the same fingerprints. Later, a hybridoma sequencing confirmed the sequence identity of these sister clones. In order to automate the spectral comparison for larger libraries of antibodies, we developed the online software ABID 2.0 (https://gets.shinyapps.io/ABID/). This open-source software determines the number of matching peptides in the fingerprint spectra. We propose that publications and other documents critically relying on monoclonal antibodies with unknown amino acid sequences should include at least one antibody fingerprint. By fingerprinting an antibody in question, its identity can be confirmed by comparison with a library spectrum at any time and context. KW - SARS-CoV-2 antibody KW - Reproducibility crisis KW - Peptide mass fingerprinting KW - Monoclonal antibody KW - Traceability KW - Antibody identification KW - Identity KW - Antibody light chain KW - MALDI-TOF-MS KW - Trypsin KW - Acidic cleavage KW - Antibody subclass KW - Database KW - Peak overlap KW - ABID KW - Sulfuric acid KW - Online software KW - Sequencing KW - Peptide coverage PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-545182 DO - https://doi.org/10.20944/preprints202203.0229.v1 SN - 2310-287X SP - 1 EP - 24 PB - MDPI CY - Basel AN - OPUS4-54518 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Tchipilov, Teodor A1 - Raysyan, Anna A1 - Weller, Michael G. T1 - Methods for the quantification of particle-bound protein – Application to reagents for lateral-flow immunoassays (LFIA) N2 - Protein immobilization for the functionalization of particles is used in various applications, including biosensors, lateral-flow immunoassays (LFIA), bead-based assays, and others. Common methods for the quantification of bound protein are measuring protein in the supernatant before and after coating and calculating the difference. This popular approach has the potential for a significant overestimation of the amount of immobilized protein since layers not directly bound to the surface (soft protein corona) are usually lost during washing and handling. Only the layer directly bound to the surface (hard corona) can be used in subsequent assays. A simplified amino acid analysis method based on acidic hydrolysis and RP-HPLC-FLD of tyrosine and phenylalanine (aromatic amino acid analysis, AAAA) is proposed to directly quantify protein bound to the surface of gold nano- and latex microparticles. The results are compared with indirect methods such as colorimetric protein assays, such as Bradford, bicinchoninic acid (BCA), as well as AAAA of the supernatant. For both particle types, these indirect quantification techniques show a protein overestimation of up to 1700% compared to the direct AAAA measurements. In addition, protein coating on latex particles was performed both passively through adsorption and covalently through EDC/sulfo-NHS chemistry. Our results showed no difference between the immobilization methodologies. This finding suggests that usual protein determination methods are no unambiguous proof of a covalent conjugation on particles or beads. KW - Soft protein corona KW - Hard protein corona KW - Gold particles KW - Nanoparticles KW - Mikroparticles KW - Antibody KW - Bioconjugation KW - Protein quantification KW - Supernatant KW - Sodium chloride method KW - Covalent conjugation KW - Latex particles KW - Lateral flow immunoassays PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-545365 DO - https://doi.org/10.20944/preprints202203.0332.v1 SP - 1 EP - 8 PB - MDPI CY - Basel AN - OPUS4-54536 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Schroeder, Barbara A1 - Le Xuan, Hoa A1 - Völzke, Jule L. A1 - Weller, Michael G. T1 - Preactivation crosslinking – An efficient method for the oriented immobilization of antibodies N2 - Crosslinking of proteins for their irreversible immobilization on surfaces is a proven and popular method. However, many protocols lead to random orientation and the formation of undefined or even inactive by-products. Most concepts to obtain a more targeted conjugation or immobilization requires the recombinant modification of at least one binding partner, which is often impractical or prohibitively expensive. Here a novel method is presented, which is based on the chemical preactivation of Protein A or G with selected conventional crosslinkers. In a second step, the antibody is added, which is subsequently crosslinked in the Fc part. This leads to an oriented and covalent immobilization of the immunoglobulin with a very high yield. Protocols for Protein A and Protein G with murine and human IgG are presented. This method may be useful for the preparation of columns for affinity chromatography, immunoprecipitation, antibodies conjugated to magnetic particles, permanent and oriented immobilization of antibodies in biosensor systems, microarrays, microtitration plates or any other system, where the loss of antibodies needs to be avoided, and maximum binding capacity is desired. This method is directly applicable even to antibodies in crude cell culture supernatants, raw sera or protein-stabilized antibody preparations without any purification nor enrichment of the IgG. This new method delivered much higher signals as a traditional method and, hence, seems to be preferable in many applications. KW - Antibody coating KW - Proximity-enhanced reaction KW - Immunoglobulins KW - IgG KW - Protein G KW - Protein A KW - Immunoprecipitation KW - Immunocapture KW - Stabilization KW - Biosensor KW - Biochip KW - Microarray KW - ELISA KW - Immunoassay KW - Immunosensor KW - Crosslinker KW - Nanoparticles KW - Click chemistry KW - Herceptin KW - Trastuzumab PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-478797 DO - https://doi.org/10.20944/preprints201904.0205.v1 SN - 2310-287X SP - 1 EP - 17 PB - MDPI CY - Basel AN - OPUS4-47879 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Tscheuschner, Georg A1 - Schwaar, Timm A1 - Weller, Michael G. T1 - Fast Confirmation of Antibody Identity by MALDI-TOF-MS Fingerprints N2 - Thousands of antibodies for diagnostic and other analytical purposes are on the market. However, it is often difficult to identify duplicates, reagent changes, and to assign the correct original publications to an antibody. This slows down scientific progress and might even be a cause of irreproducible research and a waste of resources. Recently, activities were started to suggest the sole use of recombinant antibodies in combination with the open communication of their sequence. In this case, such uncertainties should be eliminated. Unfortunately, this approach seems to be rather a long-term vision since the development and manufacturing of recombinant antibodies remain quite expensive in the foreseeable future. Also, nearly all commercial antibody suppliers may be reluctant to publish the sequence of their antibodies, since they fear counterfeiting. De-novo sequencing of antibodies is also not feasible today for a reagent user without access to the hybridoma clone. Nevertheless, it seems to be crucial for any scientist to have the opportunity to identify an antibody undoubtedly to guarantee the traceability of any research activity using antibodies from a third party as a tool. For this purpose, we developed a method for the identification of antibodies based on a MALDI-TOF-MS fingerprint. To circumvent lengthy denaturation, reduction, alkylation, and enzymatic digestion steps, the fragmentation was performed with a simple formic acid hydrolysis step. Eighty-nine unknown monoclonal antibodies were used for this study to examine the feasibility of this approach. Although the molecular assignment of peaks was rarely possible, antibodies could be easily recognized in a blinded test, simply from their mass-spectral fingerprint. A general protocol is given, which could be used without any optimization to generate fingerprints for a database. We want to propose that in most scientific projects relying critically on antibody reagents, such a fingerprint should be established to prove and document the identity of the used antibodies and to assign a specific reagent to a datasheet of a commercial supplier, a public database record or an antibody ID. KW - Reproducibility KW - Quality Control KW - Traceability KW - Diagnostics KW - ELISA KW - Immunoassay PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-506590 DO - https://doi.org/10.20944/preprints202002.0207.v1 SN - 2310-287X SP - 1 EP - 17 PB - MDPI CY - Basel AN - OPUS4-50659 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ponader, Marco A1 - Weller, Michael G. T1 - Affinitätschromatografie - Neues Trägermaterial aus Borosilikatglas N2 - Therapeutische Antikörper sind innerhalb weniger Jahre zur wichtigsten pharmazeutischen Produktklasse aufgestiegen. Für 2023 werden weltweite Umsätze von über 200 Milliarden USD erwartet. Auch diagnostische Antikörper sind mittlerweile unverzichtbare Produkte, auf deren Basis zahllose Immunoassays und andere Schnelltests entwickelt wurden. Neben der bereits sehr aufwendigen Herstellung von Antikörpern ist deren Aufreinigung aus komplexen Zellkulturmedien oder Blutseren und -plasmen zu einem Engpass in der Produktion und Nutzung dieser komplexen Proteine geworden. Schnelle und einfache Reinigungsmethoden für Antikörper sind daher sehr gefragt. KW - Affinitätschromatographie KW - Affinitätsextraktion KW - Antikörper KW - Glasmonolith KW - Additive Fertigung KW - IgG KW - Immunglobulin KW - HPLC KW - FPLC KW - biokompatibel KW - Borosilikatglas KW - gesintert KW - Titan-Halterung KW - Druckstabilität PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-477490 UR - https://www.chemiextra.com/ N1 - Geburtsname von Ponader, Marco: Wilke, M. - Birth name of Ponader, Marco: Wilke, M. IS - 4 SP - 16 EP - 17 PB - Sigwerb CY - Zug AN - OPUS4-47749 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Herrmann, Stefan T1 - Charakterisierung zweier monoklonaler Antikörper zur Detektion von Sprengstoffen N2 - In 2019 over 30 000 people were killed or injured by explosions caused by explosives like TNT, PETN, HMX and RDX. Therefore, highly sensitive assays for the detection of TNT are needed. In this study we compared two commercially available TNT antibodies: A1.1.1 and EW75C with a highly optimized indirect competitive ELISA based on a BSA-TNA conjugate. As a result, a precision profile for both antibodies was determined with a LOD of 170 pmol L-1 for the clone A1.1.1 and a LOD of 3,2 nmol L-1 for the clone EW75C. The measurements showed that the clone A1.1.1 is a highly sensitive antibody for the detection of TNT while the clone EW75C does show medium performance at most. In the cross-reactivity characterization of both antibodies many substances, closely related to the structure of TNT were tested. Both antibodies showed strong cross reactivity with trinitroaniline and trinitrobenzene. For the clone A1.1.1, which is known to originate from immunization of mice with an TNP-glycine-KLH conjugate, this has to be expected. Interestingly the clone EW75C, which was not characterized yet, showed similar behavior. This suggests a TNA-conjugate as immunogen for the EW75C antibody as well. None of both antibodies showed cross-reactions to the high explosives PETN, HMX and RDX. Also, the cross-reactions of nitro musks with the antibodies were investigated. Despite their prohibition, nitro musks are still used in Asia especially and are particularly popular in India. The overall superior clone A1.1.1 showed a significant cross-reactivity to musk ambrette. For practical reasons the influence of musk ambrette on this assay when used in natural environment should be investigated. In further experiments, the highly sensitive TNT antibody A1.1.1 was digested with papain to obtain monovalent Fab-fragments. Due to its high stability against the digestion, a custom protocol for the IgG1 subclass of mice, to which the clone A1.1.1 belongs, was developed, resulting in a quantitative digestion of the intact antibody to Fab fragments. The success of the digestion was determined with MALDI-TOF-MS and SDS-PAGE. It was shown that this protocol worked for many different antibodies of IgG1 subclass as well. KW - TNT KW - Trinitrotoluol KW - Nitroaromaten KW - Nitromoschus KW - Duftstoffe KW - ELISA KW - Immunoassay KW - Antibody KW - Explosives KW - Klon A1.1.1 KW - Klon EW75C KW - Fab Fragment KW - Kreuzreaktion KW - Crossreactivity KW - Precision Profile KW - Präzisionsprofil KW - Affinity KW - Affinitätskonstante KW - IC50 PY - 2020 SP - 1 EP - 113 PB - Hochschule für Technik und Wirtschaft Berlin - htw CY - Berlin AN - OPUS4-54556 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hiller, Lukas T1 - Herstellung und Charakterisierung eines rekombinanten Anti-Tetanus-Antikörpers aus verschiedenen Säugerzelllinien N2 - Antikörper sind in der medizinischen Welt nicht mehr wegzudenken. Ihr Einsatz-Repertoire als Therapeutika für die Behandlung diverser Krankheiten und Infektionen weitet sich von Jahr zu Jahr mehr aus. Dabei basiert ein Großteil der verwendeten Antikörper zu diesem Zeitpunkt auf monoklonalen Antikörpern auf Basis von Hybridomazellen. Doch hier könnten rekombinante Antikörper aufgrund ihrer Vektor-basierten Expression eine vielversprechende und womöglich sogar revolutionierende Alternative bieten. So ergeben sich neue Optimierungsoptionen für Merkmale wie Affinität, Stabilität und Kompatibilität über Anpassungen auf genetischer oder posttranslationaler Ebene. Allerdings ergibt sich kein Anwendungszweck ohne die vorhergehende detaillierte Charakterisierung der Antikörper. Denn nur mit spezifischem Wissen über die diversen Eigenschaften und Wechselwirkungen kann eine effektive und präzise Verwendung in der Diagnostik und Therapeutik gewährleistet werden und auf diese Weise Leben retten. Aus diesem Grund beschäftigt sich diese Masterarbeit mit der Vertiefung der rekombinanten Antikörper-Thematik. Dazu soll ein Anti-Tetanus-Antikörper erstmals rekombinant in verschiedenen Zelllinien hergestellt und anschließend über umfangreiche analytische Verfahren mit einem Fokus auf die Einflussanalyse der unterschiedlichen posttranslationalen Glykosylierungen charakterisiert werden. Zu diesem Zweck wurden als Grundlage einerseits zwei P1316-Dual-Expressions-Vektoren mit variierenden Insert-Positionen der schweren und leichten Kette durch Gibson-Assembly sowie individuellen pRK5-Plasmide für eine separiert Expression der Antikkörperketten mithilfe Restriktionsfragment-Ligation generiert. In einer Gegenüberstellung der der Expressionsausbeuten stellte sich die Überlegenheit der P1316-Plasmid-Konfiguration heraus, in der das Leichtketten-Insert an der ersten Expressionsstelle positioniert ist. Deshalb wurde dieser Vektor als Ausgangspunkt für die anschließende hochskalierten Herstellung des Anti-Tetanus-Antikörpers in Expi293F-GnTI- und ExpiCHO-S-Zellen verwendet. Ein ELISA bestätigte die Bindungsaktivität der rekombinanten Antikörper am Tetanus-Toxoid unabhängig vom Expressionssystem. Nach einer folgenden Optimierung der für die Aufreinigung verwendeten Protein-A-Affinitätschromatographie, wurde über weitere Charakterisierungsmethoden wie Größenausschlusschromatographie und dynamische Lichtstreuung eine vergleichbare Aggregation aufgrund der sauren Elution aufgezeigt. In diesem Kontext wurde die Notwendigkeit einer Zweistufen-Präparation mit Affinitäts- und Größenausschlusschromatografie für den Erhalt monodisperser Proben verdeutlicht. Zudem wurden die verschiedenen intakten Massen mitsamt ihrer spezifischen Glykan-abhängigen Streumaßen in Relation zum monoklonalen NISTmAB-Referenzantikörper bestimmt. Dabei konnte den Erwartungen nach sowohl die geringere Masse als auch die uniformere Glykosylierung der in Expi293 GnTI- exprimierten Immunoglobuline in Relation zum ExpiCHO-S-Antikörper nachgewiesen werden. Anschließend wurde das Stabilitätsverhalten mittels thermischer Entfaltung und dynamischer Lichtstreuung über einen ausgeweiteten Zeitraum sowie verschiedenen Temperaturen dokumentiert. Grundlegend wurde eine höhere thermische Stabilität der zweiten konstanten Schwerketten-Domäne des aus ExpiCHO-S-Zellen stammenden Antikörpers nachgewiesen. Außerdem konnte eine problemlose Lagerungsfähigkeit beider unterschiedlich glykosylierter Antikörper bei Raumtemperatur für mindestens 4 Wochen festgestellt werden. Des Weiteren wurde die Langzeitlagerung im Rahmen der Auswirkung von Gefrier-Auftau-Zyklen mit gleichbleibenden Methoden sowie zusätzlicher Größenausschlusschromatographie erprobt. Hierbei stellte sich der Erhalt der strukturellen Integrität nach bis zu 15 Zyklen heraus. Allerdings geht die Monodispersität bereits nach wenigen Zyklen verloren, wobei die geringfügiger glykosylierten Expi293F-GnTI-Anti-Tetanus-Antikörper eine stärkere Beeinträchtigung durch multiple Gefrier-Auftau-Zyklen aufwiesen. KW - Rekombinante Antikörper KW - Affinitätschromatographie KW - Größenausschlusschromatographie KW - MALDI-TOF-MS KW - Dynamische Lichtstreuung PY - 2024 SP - 1 EP - 120 CY - Berlin AN - OPUS4-59865 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nerger, Tino A1 - Neumann, Patrick P. A1 - Weller, Michael G. T1 - Drone-based Localization of Hazardous Chemicals by Passive Smart Dust N2 - We introduce a passive smart dust concept as a novel solution for environmental monitoring. Utilizing chemical reagents like colorimetric indicators and other chemosensors, these particles detect varying environmental conditions. We developed paper-based sensors that are both cost-effective and eco-friendly. In practical tests, these sensors, dispersed over a designated area, successfully identified hazardous substances by changing their color when exposed to acids or bases. This color change was remotely detectable using a drone-mounted color camera. The data thus obtained was processed through specialized software, accurately pinpointing areas of contamination. This method proves the efficacy and scalability of passive smart dust technology for real-time, environmentally sustainable remote sensing of hazardous materials T2 - 2024 IEEE International Symposium on Olfaction and Electronic Nose (ISOEN) CY - Grapevine, Texas, USA DA - 12.05.2024 KW - Indicator KW - Passive Smart Dust KW - Colorimetric Sensor KW - Drone KW - Cellulose KW - Environmental Monitoring KW - Confetti KW - Hazard Detection PY - 2024 SN - 979-8-3503-7053-9 VL - 1 SP - 1 EP - 3 PB - IEEE CY - Piscataway, NJ 08855-1331 USA AN - OPUS4-60176 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nerger, Tino A1 - Neumann, Patrick P. A1 - Weller, Michael G. T1 - Passive Smart Dust a versatile low-cost sensor platform N2 - Coated cellulose particles as colourimetric passive sensors that are detected by the optical camera system of a drone. In this way, hazardous substances, e.g. acids, can be detected from a safe distance in a cost-effective and environmentally friendly way. N2 - Beschichtete Zellulose Partikel als kolorimetrische passive Sensoren, die mittels optische Kamerasystem einer Drohne erfasst werden. Somit können Gefahrenstoffe, in ersten Versuchen zB Säuren aus sicherer Entfernung, kostengünstig und umweltverträglich detektiert werden. T2 - SMSI 2023 Sensor and Measurement Science International CY - Nuremberg, Germany DA - 08.05.2023 KW - Passive Smart Dust KW - Drone KW - Colorimetric sensor particles KW - Remote detection PY - 2023 DO - https://doi.org/10.5162/SMSI2023/C5.3 SP - 1 EP - 2 AN - OPUS4-57527 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Le Xuan, Hoa T1 - Gezieltes Crosslinking von Immunglobulinen mit ortspezifischen Bindern N2 - Die neue Crosslinking-Methode ist hilfreich, um Immunglobuline des Isotyps G ortspezifisch an ihrer Bindungsstelle mit Protein A oder G zu konjugieren. Die Kopplungen von Protein A und G konnten erfolgreich an Maus- und Human-IgG durchgeführt, sowie die Bedingungen untersucht und optimiert werden. Die Aktivierung von Protein G mit Glutaraldehyd erfolgt am besten bei pH 8 und die anschließende Kopplung mit Maus-IgG1 bei einem pH-Wert von 6. Jedoch wurden mit SIAB und Sulfo-SIAB als Crosslinker im Vergleich zu Glutaraldehyd noch höhere Signale erhalten. Für die Kopplung von SIAB sind 40% DMSO im Reaktionspuffer günstig, währenddessen Sulfo-SIAB gut wasserlöslich ist daher keine Lösungsvermittler benötigt. Es ergab sich ein optimaler pH-Wert von 7,4 um Protein A mit SIAB zu aktivieren und den gleichen pH-Wert um die Kopplung mit Maus-IgG1 durchzuführen. Für die Kopplung von Protein G mit Maus-IgG1 hingegen zeigten die Experimente, dass ein leicht saurer pH-Wert bei pH 6 für den IgG-Kopplungsschritt am günstigsten ist. Während die Inkubationszeit von Maus-IgG1 mit Protein G bei 16 h liegt, muss mit Protein A bis zu 40 h inkubiert werden, um das Kopplungsmaximum zu erreichen. Des Weiteren wurde das Crosslinking von Human-IgG (Herceptin) mit SIAB untersucht. Dabei zeigte sich, wie in der Abbildung 47 zu sehen ist, dass Protein A und G vergleichbar gut an Human-IgG zu koppeln sind. Für das Crosslinking von Protein G mit Maus-IgG1 ist dagegen ein deutlich besserer Umsatz im Vergleich zu Protein A zu erkennen (Abbildung 48). Heterobifunktionale Linker können mit der reaktiveren Gruppe die erste Bindung eingehen, um erst nach Zugabe eines weiteren Reagenzes die zweite Bindung auszubilden und zudem intramolekulare Reaktionen möglichst zu vermeiden. KW - Antikörper KW - Antibodies KW - Vernetzung KW - Immobilisierung KW - Immobilization KW - Herceptin KW - Human antibodies KW - Therapeutic antibodies KW - Diagnostic antibodies KW - Oriented immobilization PY - 2019 SP - 1 EP - 100 PB - Humboldt-Universität zu Berlin CY - Berlin AN - OPUS4-54658 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schwaar, Timm T1 - Entwicklung von multidimensionalen Hochdurchsatzmethoden zur Analyse von partikelbasierten Peptidbibliotheken N2 - Ziel dieser Arbeit war die Entwicklung einer Methode zur Hochdurchsatzanalyse von partikelgebundenen Split-and-Mix-Peptidbibliotheken. Dabei wurde ein System entwickelt, das Partikelbibliotheken in kurzer Zeit auf ihre Bindung zu einem Zielmolekül hin untersucht und im nächsten Schritt eine direkte „Ein-Partikel“-Sequenzierung der Peptide von der festen Phase ermöglicht. Die Analyse der Bindung eines Zielmoleküls an ein selektiv bindendes Peptid wurde dabei in einem Modellsystem simuliert. Dazu wurde FITC-markiertes Neutravidin 3 mit festphasengebundenen biotinylierten und nicht-biotinylierten Peptiden inkubiert. Die Bindung von Neutravidin-FITC an die biotinylierten Peptide konnte erfolgreich mittels eines Fluoreszenzmikroskops nachgewiesen werden, wobei diese Methode für eine Hochdurchsatzanalyse ungeeignet war. So wurde die Analyse des Fluoreszenzassays auf einen Microarrayscanner übertragen (siehe Abbildung 33). Dies gelang erfolgreich wobei die hohe Eigenfluoreszenz des Tentagel-Harzes zu falsch positiven Ergebnissen führte. Mit einem Wechsel zum längerwelligen Fluoreszenzfarbstoff ATTO-633 konnten falsch positive Ergebnisse vermieden werden. Somit wurde die zeitintensive Fluoreszenzanalyse von einem Fluoreszenzmikroskop erfolgreich auf einen Microarrayscanner übertragen, welcher in kurzer Zeit (ca. 5 min pro Objektträger) eine Vielzahl an peptidbeladenen Partikeln gleichzeitig analysieren kann. KW - Peptide KW - OBOC library KW - MALDI-TOF-MS KW - Sequencing KW - Ladder sequencing KW - Solid-phase peptide synthesis KW - SPPS KW - Microarray KW - Fluorescence label KW - Polymer beads KW - Tentagel KW - Merrifield KW - Split and mix technology PY - 2015 SP - 1 EP - 80 PB - Humboldt-Universität zu Berlin CY - Berlin AN - OPUS4-54644 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hartfiel, Reni T1 - Zweistufiges Screening von One-Bead-One-Peptide-Bibliotheken linearer & cyclischer Peptide gegen Pflanzenviren N2 - In der Masterarbeit wurde ein Screening gegen den CCMV mit einer linearen Peptidbibliothek entwickelt, wobei zwei lineare Binder identifiziert wurden. Das resynthetisierte Peptid wurde auf seine Bindungseigenschaften mittels ELISA und MST untersucht. Aufgrund eines Aminosäurefehlers in der selbst durchgeführten Resynthese des Peptids sind die Ergebnisse nicht vollständig übertragbar. Um eine umsetzbare Cyclusgröße für die Peptidbibliothek zu finden, wurden Ringgrößen mit sechs bis acht Aminosäuren untersucht. Da keiner der gewählten Ringgrößen bevorzugt war, wurde die Ringgröße aus acht Aminosäuren für die Peptidbibliothek gewählt. Der Ringschluss wurde durch die Bildung einer Disulfidbrücke erreicht. Dadurch war die Alkylierung der vorhandenen Thiolgruppe in den Abbruchsequenzen notwendig. Neben den etablierten Alkylierungsreagenzien Iodessigsäure, Iodacetamid und Acrylamid wurden zwei Epoxide mituntersucht. Hierbei konnte nur bei Acrylamid und Propylenoxid eine vollständige Alkylierung beobachtet werden. Eine synthetische Peptidbibliothek aus zehn Aminosäuren pro Kopplungsschritt und einer Peptidlänge von acht Aminosäuren wurde erfolgreich nach der Split-and-Mix-Synthese hergestellt. Neben den kanonischen Aminosäuren wurde die synthetische Aminosäure 3-(3-Pyridyl)-alanin in die Peptidbibliothek mit eingebaut. Peptidsequenzen aus der cyclische Peptidbibliothek konnte mittels MALDI-TOF-MS identifiziert werden. Es konnte außerdem gezeigt werden, dass synthetische Aminosäuren mit proteinogenen Aminosäuren erfolgreich übersetzt werden. Anschließend wurde das entwickelte Screening auf eine cyclische Peptidbibliothek übertragen. Dabei konnte kein Binder identifiziert werden, da zu viele Nebenreaktionen auftraten. Ein alternativer Ringschluss über die Seitenketten von Lysin und Cystein wurden mit ortho-Phthaldialdehyd und 2,4,6-Trichloro-1,3,5-triazin (Cyanurchlorid) untersucht. Beide Bedingungen wiesen keinen erfolgreichen Ringschluss auf. Obwohl der Ringschluss über die Seitenketten von Lysin und Cystein nicht erfolgreich war, sollte ein Austausch von Cystein angestrebt werden, so dass kein freies Cystein in den Abbruchsequenzen vorhanden ist und die Alkylierung überflüssig wäre. Der Ringschluss durch Verwendung anderer Seitenketten bietet einen vielseitigen Ansatz. KW - CCMV KW - Pflanzenvirus KW - Peptidbibliothek KW - Peptid-Aptamer KW - Alkylierung KW - Cyclisierung KW - MALDI-TOF-MS KW - Fluoreszenz KW - Chip KW - Sequenzierung KW - Peptid-Synthese PY - 2022 SP - 1 EP - 81 PB - Humboldt-Universität zu Berlin CY - Berlin AN - OPUS4-54501 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Tchipilov, Teodor A1 - Meyer, Klas A1 - Weller, Michael G. T1 - Quantitative 1H nuclear magnetic resonance (qNMR) of aromatic amino acids for protein quantification N2 - qNMR is a valuable technique for metrological studies due to the uniformity of its signal response for all chemical species of an isotope of interest, which enables compound-independent calibration. However, protein quantification remained challenging as large molecules produce wide, low-intensity signals that reduce the already low sensitivity. Combining qNMR with the hydrolysis of protein samples into amino acids circumvents many of these issues and facilitates the use of NMR spectroscopy for absolute protein and peptide quantification.In this work, different conditions have been tested for quantifying aromatic amino acids and proteins. First, we examined the pH-based signal shifts in the aromatic region. The preferable pH depends on the selection of the amino acids for quantification and which internal standard substance should be used to avoid peak overlap. Several aromatic compounds, such as terephthalic acid, sulfoisophthalic acid, and benzene tricarboxylic acid, have been applied as internal standards. The quantification of amino acids from an amino acid standard, as well as from a certified reference material (bovine serum albumin), was performed. Using the first two suggested internal standards, recovery was ~ 97 % for histidine, phenylalanine, and tyrosine at a concentration of approximately 1 mM in solution. Acidic hydrolysis of a certified reference material (CRM) of bovine serum albumin (BSA) and subsequent quantification of Phe and Tyr yielded recoveries of 98 ± 2 and 88 ± 4 %, respectively, at a protein concentration of 16 g/L or 250 µM. KW - Amino acid analysis KW - AAA KW - Protein hydrolysis KW - Metrology KW - Traceability KW - Reference materials KW - Internal standards KW - Calibration PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-564520 DO - https://doi.org/10.20944/preprints202211.0569.v1 SP - 1 EP - 13 PB - MDPI CY - Basel AN - OPUS4-56452 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Giesen, Charlotte A1 - Jakubowski, Norbert A1 - Panne, Ulrich A1 - Weller, Michael G. T1 - Ochratoxin-A-Bestimmung in Wein mittels eines ICP-MS-basierten Immunoassays PY - 2010 UR - http://www.analytik-news.de/Fachartikel/Volltext/BAM2.pdf SP - 1 EP - 6 PB - Dr. Beyer Internet-Beratung CY - Ober-Ramstadt AN - OPUS4-22702 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Steglich, P. A1 - Mai, C. A1 - Bondarenko, S. A1 - Paul, Martin A1 - Weller, Michael G. A1 - Schrader, S. A1 - Mai, A. T1 - BioPIC - Integration of Biosensors based on Photonic Integrated Circuits by Local-Backside Etching N2 - Silicon photonic sensors are promising candidates for lab-on-a-chip solutions with versatile applications and scalable production prospects using complementary metal-oxide semiconductor (CMOS) fabrication methods. However, the widespread use has been hindered because the sensing area adjoins optical and electrical components making packaging and sensor handling challenging. In this work, a local back-side release of the photonic sensor is employed, enabling a separation of the sensing area from the rest of the chip. This approach allows preserving the compatibility of photonic integrated circuits in the front-end of line and metal interconnects in the back-end of line. T2 - ATTRACT online Conference CY - Online meeting DA - 22.09.2020 KW - Silicon Photonics KW - Photonic Sensor KW - Photonic Integrated Circuits KW - Point-Of-Care-Diagnostics KW - CMOS KW - Microfluidics KW - Lab-on-a-chip KW - Ring resonator PY - 2020 UR - https://attract-eu.com/showroom/project/integration-of-biosensors-based-on-photonic-integrated-circuits-by-local-backside-etching-biopic/ SP - 1 EP - 5 AN - OPUS4-51735 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Döring, Sarah T1 - Corundum Particles as Trypsin Carrier for Efficient Protein Digestion N2 - This dataset contains raw LC–MS/MS files of trypsin-digested NISTmAb acquired on a SCIEX TripleTOF 6600 mass spectrometer in DIA (SWATH) mode for antibody quantification. In addition, it includes MALDI-TOF MS peptide mass fingerprints of trypsin-digested Herceptin as well as reference spectra that can be used for antibody identification using the open-source software ABID 2.0 (https://bam.de/ABID). The data were generated within a study demonstrating the applicability of corundum-immobilized trypsin for antibody digestion and its suitability for peptide-based LC–MS/MS quantification and MALDI-TOF MS fingerprinting–based antibody identification. KW - NISTmAb KW - Herceptin KW - MALDI-TOF MS peptide mass fingerprint KW - ABID 2.0 PY - 2025 DO - https://doi.org/10.5281/zenodo.17416536 PB - Zenodo CY - Geneva AN - OPUS4-65365 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Döring, Sarah T1 - Vergleichende Darstellung SARS-CoV-2-spezifischer Nanobodys aus unterschiedlichen Wirtsorganismen N2 - Aufgrund der anhaltenden COVID-19-Pandemie werden neutralisierende Therapeutika benötigt. Eine Möglichkeit zur Behandlung stellt die Verwendung monoklonaler Anti-SARS-CoV-2-Immun-globuline dar. Ihre Produktion in Säugetierzellen ist jedoch schwer skalierbar, um den weltweiten Bedarf zu decken. VHH-Antikörper, auch Nanobodys genannt, bieten hierfür eine Alternative, da sie eine hohe Temperaturstabilität aufweisen und eine kostengünstige Produktion in prokaryotischen Wirtsorganismen ermöglichen. KW - E. coli KW - Corona KW - Virus KW - Spike-Protein KW - Nanobody KW - Antikörper KW - Expression KW - Fingerprint KW - Vhh KW - RBD KW - COVID-19 KW - SARS-CoV-2 KW - ELISA KW - MST KW - Halomonas elongata KW - Periplasma KW - SDS-PAGE KW - ACE2-Rezeptor PY - 2021 SP - 1 EP - 111 PB - Technische Universität Berlin CY - Berlin AN - OPUS4-54624 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Krop, U. A1 - Scherz, Franziska A1 - Weller, Michael G. A1 - Monks, K. T1 - Fast and robust purification of antibodies from human serum with a new monolithic protein A column N2 - The use of antibodies is becoming more and more important. Therewith the need for fast and robust methods for their purification and columns with a long lifetime is growing. In this application, we describe a fast and robust protein A affinity chromatography method with a new monolithic column. Antibodies were successfully purified in less than 1.5 minutes with a flowrate of 5 mL/min highlighting the advantages of this column and method. KW - Antibodies KW - Protein A KW - MNPQ KW - Technology transfer KW - Human serum KW - Purification KW - IgG KW - SDS PAGE KW - Regeneration PY - 2017 UR - http://www.knauer.net/en/application/fast_and_robust_purification_of_antibodies_from_human_serum_with_a_new_monolithic_protein_a_column.html SP - 1 EP - 2 PB - Knauer CY - Berlin AN - OPUS4-43163 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Bosc-Bierne, Gaby A1 - Ewald, Shireen A1 - Kreuzer, Oliver J. A1 - Weller, Michael G. T1 - Efficient Quality Control of Peptide Pools N2 - Peptide pools composed of short amino acid sequences have proven to be versatile tools in various research areas and clinical applications. They are powerful tools for epitope mapping, immunotherapy, and vaccine development. Their importance lies in their ability to map complex protein structures, enabling a comprehensive understanding of immune responses and facilitating the identification of potential therapeutic agents. The application of peptide pools also extends to the field of personalized medicine, offering tailored solutions for diseases such as cancer and infectious diseases. Peptide pools are complex mixtures of immunostimulatory antigens primarily intended for T-cell stimulation. They are commercially available in many different compositions and variants. However, unlike other reagents that consist of only one or a few compounds, peptide pools are highly complex products with limited stability. This makes their quality control a major challenge. Quantitative peptide analysis usually requires sophisticated methods, in most cases isotope-labeled standards and reference materials. None of these are routinely available for these products. Synthesis and purification of all labeled peptides might be required. Usually, this approach would be prohibitively laborious and expensive. Therefore, an approach is needed to provide a practical and feasible method for quality control of peptide pools. With insufficient quality control, the use of such products could lead to incorrect experimental results, which would worsen the well-known reproducibility crisis in the biomedical sciences. Here we propose the use of ultra-high performance liquid chromatography (UHPLC) with two detectors, a standard UV detector (at 214 nm) for quantitative analysis and a high-resolution mass spectrometer (HRMS) for identity confirmation. To be cost-efficient and fast, quantification and identification are performed in one chromatographic run. An optimized protocol is shown, and different peak integration methods are compared and discussed. This work was performed using a peptide pool known as CEF, which consists of 32 peptides derived from cytomegalovirus (CMV), Epstein-Barr virus (EBV) and influenza virus, ranging from 8 to 12 amino acids in length. N2 - Peptidpools, die aus kurzen Aminosäuresequenzen bestehen, haben sich in verschiedenen Forschungsbereichen und klinischen Anwendungen als vielseitige Werkzeuge erwiesen. Sie sind leistungsstarke Werkzeuge für die Epitopkartierung, die Immuntherapie und die Impfstoffentwicklung. Ihre Bedeutung liegt in ihrer Fähigkeit, komplexe Proteinstrukturen zu kartieren, was ein umfassendes Verständnis der Immunantworten ermöglicht und die Identifizierung potenzieller Therapeutika erleichtert. Die Anwendung von Peptidpools erstreckt sich auch auf den Bereich der personalisierten Medizin und bietet maßgeschneiderte Lösungen für Krankheiten wie Krebs und Infektionskrankheiten. Peptidpools sind komplexe Mischungen immunstimulierender Antigene, die hauptsächlich zur T-Zell-Stimulation bestimmt sind. Sie sind in vielen verschiedenen Zusammensetzungen und Varianten im Handel erhältlich. Im Gegensatz zu anderen Reagenzien, die nur aus einer oder wenigen Verbindungen bestehen, sind Peptidpools jedoch hochkomplexe Produkte mit begrenzter Stabilität. Dies macht ihre Qualitätskontrolle zu einer großen Herausforderung. Die quantitative Peptidanalyse erfordert in der Regel ausgefeilte Methoden, in den meisten Fällen isotopenmarkierte Standards und Referenzmaterialien. Keines dieser Verfahren ist für diese Produkte routinemäßig verfügbar. Möglicherweise ist die Synthese und Reinigung aller markierten Peptide erforderlich. In der Regel wäre dieser Ansatz unerschwinglich aufwendig und teuer. Daher ist ein Ansatz erforderlich, der eine praktische und praktikable Methode für die Qualitätskontrolle von Peptidpools bietet. Bei unzureichender Qualitätskontrolle könnte die Verwendung solcher Produkte zu falschen Versuchsergebnissen führen, was die bekannte Reproduzierbarkeitskrise in den biomedizinischen Wissenschaften verschlimmern würde. Hier schlagen wir die Verwendung der Ultrahochleistungsflüssigkeitschromatographie (UHPLC) mit zwei Detektoren vor, einem Standard-UV-Detektor (bei 214 nm) für die quantitative Analyse und einem hochauflösenden Massenspektrometer (HRMS) für die Identitätsbestätigung. Um kosteneffizient und schnell zu sein, werden Quantifizierung und Identifizierung in einem chromatographischen Durchlauf durchgeführt. Es wird ein optimiertes Protokoll vorgestellt und verschiedene Peak-Integrationsmethoden werden verglichen und diskutiert. Diese Arbeit wurde mit einem Peptidpool namens CEF durchgeführt, der aus 32 Peptiden besteht, die vom Cytomegalovirus (CMV), Epstein-Barr-Virus (EBV) und Influenzavirus stammen und zwischen 8 und 12 Aminosäuren lang sind. KW - Quality control KW - UHPLC-UV-HRMS KW - Relative peptide quantification KW - Compound confirmation KW - Structure confirmation KW - Cost efficiency KW - Infectious diseases KW - Orbitrap PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-621307 DO - https://doi.org/10.20944/preprints202404.0992.v1 SN - 2310-287X SP - 1 EP - 18 PB - MDPI CY - Basel AN - OPUS4-62130 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Völzke, Jule L. A1 - Hodjat Shamami, Parya A1 - Gawlitza, Kornelia A1 - Feldmann, Ines A1 - Zimathies, Annett A1 - Weller, Michael G. T1 - High-purity corundum as support for affinity extractions from complex samples N2 - Nonporous corundum powder, known as an abrasive material in the industry, was functionalized covalently with protein binders to isolate and enrich specific proteins from complex matrices. The materials based on corundum were characterized by TEM, ESEM, BET, DLS, and zeta potential measurements. The strong Al-O-P bonds between the corundum surface and amino phosphonic acids are used to introduce functional groups for further conjugations. The common cross-linker glutaraldehyde was compared with a hyperbranched polyglycerol (PG) of around 10 kDa. The latter is oxidized with periodate to generate aldehyde groups that can covalently react with the amines of the surface and the amino groups from the protein via a reductive amination process. The amount of bound protein was quantified via aromatic amino acid analysis (AAAA). This work shows that oxidized polyglycerol can be used as an alternative to glutaraldehyde. With polyglycerol, more of the model protein bovine serum albumin (BSA) could be attached to the surface under the same conditions, and lower nonspecific binding (NSB) was observed. As a proof of concept, IgG was extracted with protein A from crude human plasma. The purity of the product was examined by SDS-PAGE. A binding capacity of 1.8 mg IgG per g of corundum powder was achieved. The advantages of corundum are the very low price, extremely high physical and chemical stability, pressure resistance, favorable binding kinetics, and flexible application. KW - Protein KW - Bioseparation KW - Purification KW - Immunoprecipitation KW - Affinity chromatography KW - Polyglycerol KW - Glutaraldehyde KW - Linker KW - Bioconjugation KW - Self-assembled monolayer (SAM) KW - Periodate oxidation KW - Reductive amination KW - Antibodies KW - Igg KW - Immunoglobulins KW - Carrier KW - Solid phase KW - Hyperbranched polymer KW - Aromatic amino acid analysis aaaa PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-555142 DO - https://doi.org/10.20944/preprints202208.0004.v1 SN - 2310-287X SP - 1 EP - 13 PB - MDPI CY - Basel AN - OPUS4-55514 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Paul, Martin A1 - Weller, Michael G. T1 - Antibody screening by microarray technology – Direct identification of selective high-affinity clones N2 - The primary screening of hybridoma cells is a time-critical and laborious step during the development of monoclonal antibodies. Often critical errors occur in this phase, which supports the notion that the generation of monoclonal antibodies with hybridoma technology is difficult to control and hence a risky venture. We think that it is crucial to improve the screening process to eliminate most of the immanent deficits of the conventional approach. With this new microarray-based procedure, several advances could be achieved: Selectivity for excellent binders, high throughput, reproducible signals, avoidance of misleading avidity (multivalency) effects, and simultaneous performance of competition experiments. The latter can directly be used to select clones of desired cross-reactivity properties. In this paper, a model system with two excellent clones against carbamazepine, two weak clones and blank supernatant has been designed to examine the effectiveness of the new system. The excellent clones could be detected largely independent of the IgG concentration, which is unknown during the clone screening since the determination and subsequent adjustment of the antibody concentration is not possible in most cases. Furthermore, in this approach, the enrichment, isolation, and purification of IgG for characterization is not necessary. Raw cell culture supernatant can be used directly, even when fetal calf serum (FCS) or other complex media had been used. In addition, an improved method for the oriented antibody-immobilization on epoxy-silanized slides is presented. Based on the results of this model system, we conclude that this approach should be preferable to most other protocols leading to many of false positives, causing expensive and lengthy confirmation steps to weed out the poor clones. KW - Hybridoma KW - Monoclonal Antibodies KW - Clones KW - Competitive Immunoassay KW - Hapten Immunoassay KW - False Positives PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-506621 DO - https://doi.org/10.20944/preprints201911.0023.v1 SN - 2310-287X SP - 1 EP - 17 PB - MDPI CY - Basel AN - OPUS4-50662 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Tscheuschner, Georg T1 - Entwicklung einer Methode zur schnellen Identifikation von Antikörpern mittels MALDI-TOF-MS N2 - Im Vergleich zu anderen Proteinen ist die Identifizierung von Antikörpern anhand ihrer Sequenz zum Beispiel mittels "peptide mass fingerprinting" schwierig. Da die Sequenzinformation eines Antikörpers aufgrund der hypersomatischen Mutation während der Affinitätsreifung nicht im Genom eines Organismus gespeichert ist, kann die Aminosäuresequenz nicht auf einfachem Weg der DNA-Sequenzierung gewonnen werden. Das ist nur in seltenen Fällen möglich, wenn dem Endanwender der Zellklon der Antikörper-produzierenden Zelle zugänglich ist. Eine Sequenzierung auf Protein-Ebene ist sehr aufwändig und teuer und wird daher fast nie für die Charakterisierung von analytischen Antikörpern verwendet. Der Mangel an Validierung dieser analytischen Antikörper, die bei Experimenten verwendeten werden, löst aber eine Reihe Probleme aus, die die Wiederholbarkeit dieser Experimente schwierig und in einigen Fällen unmöglich macht. Das sorgt jährlich für verschwendete Forschungsgelder in Milliardenhöhe und hindert den wissenschaftlichen Fortschritt. Ziel der vorliegenden Arbeit war die Entwicklung einer einfachen und schnellen Methode, die es trotzdem ermöglicht, die Identifikation von Antikörpern sicherzustellen. Dazu wurde eine Methode basierend auf dem "peptide mass fingerprinting" gewählt. Das Problem der unbekannten Aminosäuresequenz der Antikörper wurde gelöst, indem lediglich die Peptidmuster der entstehenden Fingerprint-Spektren zur Identifikation herangezogen wurden. MALDI wurde dabei als Ionisationsmethode für die Massenspektrometrie gewählt, da die resultierenden Spektren im Gegensatz zu ESI-MS einfach auszuwerten sind. Auch kann auf eine vorige Trennung der Peptide mittels LC verzichtet werden, was zusätzlich Analysenzeit spart. Für die Proteinspaltung wurde eine simple saure Hydrolyse mittels Ameisensäure gewählt. Im Vergleich zum herkömmlichen Trypsin-Verdau konnten auf zeitraubende Arbeitsschritte wie Denaturierung, Reduktion und Alkylierung der Antikörper verzichtet werden. Die Hydrolyse mittels Ameisensäure wurde bisher nur auf kleine und mittelgroße Proteine angewendet, sodass im ersten Teil dieser Arbeit mehrere Schritte optimiert wurden bevor zufriedenstellende Fingerprint-Spektren von Antikörpern erhalten wurden. KW - Peptide KW - Fingerprint KW - Peptide mass fingerprinting KW - Massenspektrometrie KW - Saure Hydrolyse KW - Festphasenextraktion KW - Protein G KW - Ameisensäure KW - ABID KW - Korrelationsmatrix PY - 2019 SP - 1 EP - 116 PB - Humboldt-Universität zu Berlin CY - Berlin AN - OPUS4-54626 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram A1 - Ohm, Katrin A1 - Holzwarth, Marcel T1 - Statistische Auswertung der SE(B)-Bruchzähigkeitsdatenbasis und Untersuchungen zum Bruchmechanismus – neue Ergebnisse zur Untersuchung des Master Curve Konzepts für ferritisches Gusseisen mit Kugelgraphit bei dynamischer Beanspruchung (Projekt MCGUSS) N2 - Die Zielstellung des laufenden Kooperationsprojektes MCGUSS zwischen der BAM Berlin und der MPA Stuttgart ist es, das probabilistische Master Curve (MC)-Konzept hinsichtlich seiner Übertragbarkeit auf ferritisches Gusseisen mit Kugelgraphit (DCI) zu untersuchen. Über Teilergebnisse der Arbeiten wurde bereits auf den Jahrestagungen 2023 bis 2025 des DVM-AK Bruchmechanik und Bauteilsicherheit berichtet. Der vorliegende Beitrag hat zwei Schwerpunkte. Zum einen wurde die Datenbasis der dynamischen Bruchzähigkeit für SE(B)-Proben der Dicken 10 mm, 25 mm und 140 mm auf insgesamt 101 Versuche bei Temperaturen von -40 °C bis -140 °C erweitert, statistisch ausgewertet sowie MC-Analysen unterzogen. Die Ergebnisse zeigen, dass die Daten sich zwar mit einer Weibullverteilung gut beschreiben lassen, die MC-Methode nach ASTM E1921 jedoch nicht ohne Weiteres anwendbar ist, sondern Modifikationen erforderlich sind. Des Weiteren werden neue Ergebnisse zum werkstoffspezifischen Bruchmechanismus bei dynamischer Belastung im unteren Übergangsbereich der Zähigkeit diskutiert. Die fraktographische Datenbank wurde durch REM-Analysen weiterer Bruchflächen von SE(B)25-Proben bei -40 °C, -60 °C und -80 °C ergänzt. Die Ergebnisse unterstreichen die prägende Rolle, die Rissarrestereignissen im Verlauf des dynamischen Sprödbruchversagens bei DCI zukommt. Der in MCGUSS zur Erklärung eines gegenüber Stahl inversen Probengrößeneinflusses vorgeschlagene Mechanismus „Specimen size-dependent arrest of local brittle fractures before global brittle failure by weakest link“ wird dadurch weiter unterstützt. T2 - DVM-Jahrestagung 2026 des Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Stuttgart, Germany DA - 24.02.2026 KW - Statistics KW - Dynamic fracture toughness KW - Ductile cast iron KW - Master curve KW - Safety assessment PY - 2026 SP - 1 EP - 12 PB - DVM-Verlag CY - Berlin AN - OPUS4-65591 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Weller, Michael G. T1 - Interview with Dr Michael G. Weller N2 - This author interview is by Dr Michael G. Weller, Head of Division 1.5 Protein Analysis at Federal Institute for Materials Research and Testing (BAM). BAM (www.bam.de/en) is a senior scientific and technical institute with responsibility to the German Federal Ministry for Economic Affairs and Energy. Dr Weller's review paper, Quality issues of research antibodies is available for download in Analytical Chemistry Insights. KW - Antibodies KW - Quality KW - Reproducibility PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-392326 UR - http://insights.sagepub.com/la_press_news.php?pa=view&news_item_id=4025 SP - 1 PB - SAGE CY - London AN - OPUS4-39232 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Thünemann, Andreas A1 - Emmerling, Franziska A1 - Hodoroaba, Vasile-Dan T1 - Review of existing calibration or reference N2 - We report on calibration standards of nanoparticles meeting the definition of a nanomaterial given by the European Commission (EU 2011) which are relevant for the characterisation methods applied in the NanoDefine project. We found that the Impact of nanoparticles is outstanding in the scientific literature. A number of 270.000 paper titles on nanoparticles are listed in the Web of Science data base. But surprisingly, the availability of suitable certified standard reference materials is scarce. Only a few sources were found. For example, BAM provides the database Nanoscaled Reference Materials at http://www.nano-refmat.bam.de/en/ in cooperation with the ISO/TC 229 Nanotechnologies. In addition, two publications from 2013 on nanoscale reference materials are available. Candidates of nano-(certified) reference materials from other ongoing or just finished FP6 and FP7 nano-metrology projects have been extracted from the Compendium of Projects in the European NanoSafety Cluster (Compendium NSC, 2013). Recommendations for selection of representative test materials and calibration standards for NanoDefine internal tasks, respectively, are also given. KW - Nanomaterial KW - Reference materials KW - Certified reference materials PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-389836 UR - http://www.nanodefine.eu/index.php/downloads/nanodefine-technical-reports SP - 1 EP - 18 CY - Wageningen, The Netherlands AN - OPUS4-38983 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Miliūtė, Aistė ED - Bustamante, Joana ED - Karafiludis, Stephanos ED - Zöllner, Moritz ED - Eddah, Mustapha ED - Emmerling, Franziska ED - Mieller, Björn ED - George, Janine ED - Stawski, Tomasz T1 - Synthesis and phase purity of the negative thermal expansion material ZrV2O7 N2 - Synthesis of pure, homogeneous, and reproducible materials is key for the comprehensive understanding, design, and tailoring of material properties. In this study, we focus on the synthesis of ZrV2O7, a material known for its negative thermal expansion properties. We investigate the influence of solid-state and wet chemistry synthesis methods on the purity and homogeneity of ZrV2O7 samples. Our findings indicate that different synthesis methods significantly impact the material's characteristics. The solid-state reaction provided high-purity material through extended milling time and repeated calcination cycles, while the sol-gel reaction enabled a “near-atomic” level of mixing and, therefore, homogenous phase-pure ZrV2O7. We confirmed purity via X-ray diffraction and Raman spectroscopy, highlighting differences between phase-pure and multiphase ceramics. These analytical techniques allowed us to distinguish subtle differences in the structure of the material. Based on ab initio simulated phonon data, we were able to interpret the Raman spectra and visualise Raman active atom vibrations. We show that phase purity enables the unbiased characterisation of material properties such as negative thermal expansion. KW - NTE KW - Sol-gel KW - Solid-state KW - Ab-initio KW - XRD KW - Raman PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-613643 DO - https://doi.org/10.26434/chemrxiv-2024-d4sj9 SN - 2573-2293 VL - 2024 SP - 1 EP - 60 PB - American Chemical Society CY - Washington, D.C. AN - OPUS4-61364 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Visileanu, Emilia A1 - Catalin Grosu, Marian A1 - Tiberiu Miclea, Paul A1 - Altmann, Korinna A1 - Brossell, Dirk T1 - Methods for the collection and characterization of airborne particles in the textile industry N2 - Airborne particulate matter is one of the main air pollutants. Their impact on mortality, and the occurrence of pulmonary and cardiovascular complications, have been the subject of numerous studies. Airborne particles are complex mixtures of organic and inorganic substances from different sources of particle emissions. Particulate Matter (PM) particles are classified according to their aerodynamic diameter expressed in µm and can vary from coarse (PM 10) to fine (less than PM 2.5). These diameter considerations are fundamental because they condition the penetration of particles into the bronchopulmonary system and the body. In recent years, there has been an interest in so-called “ultra-fine” particles, with a diameter of 0.1 µm (or 100 nm), or PM 0.1. They are nanoparticles and their impact on human health is not yet clear.With more than 1.5 million employees, textiles and clothing is a diverse sector that plays an important role in the European manufacturing industry, producing a turnover of €162 billion.An important component of the solid particles that generate air pollution in the textile industry is microplastics (MP) and nano plastics (NP), which also include microfibers (<5mm) and nanofibers (<100 nm), respectively. The particles released into the air during fiber and yarn processing range from 1 µg/m3 to 50 µg/m3.The paper presents the results of the determination of indoor and outdoor air concentration levels in textile companies, to identify the areas with the highest concentration level, by using an online recording system such as the Laser Aerosol Spectrometer MINI LAS model 11-E. The total concentration level TSP (µg/m3), the fractions PM 10(µg/m3), PM 2.5(µg/m3), PM1(µg/m3), as well as the total number of particles TC (1/l), were shown. It was noted that TSP is approximately at the same level both indoors and outdoors, but the fractions of PM10, PM2.5, and PM1 have much higher values indoors than outdoors with possible consequences on workers' health.The next step was the collection of fibers, namely micro and nano plastic particles from the vicinity of the workplaces of polyester, polyamide, and polypropylene fibers processing units in the textile industry in Romania, to obtain a sufficient quantity for laboratory analysis to determine the size and shape of the particles as well as their chemical composition. Two types of pumps were used, differentiated by their operating parameters: TECORA SKYPOST with airflow of 38 l/min and GILAIRPLUS with airflow 2l/min. Filters made of different materials with different diameters and pore sizes were used, namely: quartz filters (ø 47 mm, and ø 37 mm) on a TECORA SKYPOST type pump, polycarbonate nucleopore coated with a gold membrane (ø 25 mm) and silica filter (ø 9 mm) on GILAIRPLUS type pump.Using descriptive statistics, the calculation of correlation coefficients highlighted a strong correlation between the variables: "Collected mass/ Air concentration" and "Collected mass/ Air volume" for all diameters of the filters.The highest collected particle volume, determined by weighing the filters before and after collection, was obtained with the quartz filters (ø 47 mm) at an airflow of 38 l/min. The particles collected (polyester, polyamide, polypropylene) in the first stage were analyzed by SEM and thermogravimetric and it was found that the quartz filters absorbed the particles inside, with very few remaining on the surface. Thus no known methods can be used to perform analysis for particles collected on quartz filters. The number of particles on the filters was insufficient for analysis either because of the collection parameters used or because of the loss of particles during transport. As a result, in the next step, the use of 9 mm Si filters using the GILAIRPLUS pump at an airflow rate of 2l/min was chosen.To improve the transport conditions and avoid the loss of the particles and keep them on the surface of the filters, two methods were applied:- after weighing the filters were reintroduced into the collection pump holder;- a filtration system for airborne micro-nano plastics was designed and manufactured to selectively collect and transport PM10 and PM1 particles collected on SI filters.In both cases, SEM, Raman mapping, and GS-MS microscopy were used for analysis.Several times more PM10 than PM1 (74.5µg compared to 12.5 µg) was found. In all cases, both particles and fibers showed the same Raman fingerprint.The GS-MS analyses showed some contamination of the workspaces with particles other than the processed fibers. The presence of non-notifiable substances was also observed.The most viable filters are Si filters with a pore size of 10 microns to 1 micron and the use of the selected collection and transport filter system. In the following a filter system will be applied for collection on Au membrane-coated polycarbonate filters. T2 - 5th International Conference on Human Systems Engineering and Design: Future Trends and Applications (IHSED 2023) KW - Microplastics KW - Textiles PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-624442 DO - https://doi.org/10.54941/ahfe1004132 VL - 112 SP - 212 EP - 223 PB - AHFE International AN - OPUS4-62444 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Ecke, Alexander T1 - Integrated Diagnostics of Pharmaceutical Contaminants in Water Supply and Management Systems N2 - The contamination of drinking water with pharmaceuticals represents a severe health risk. In order to monitor the drinking water quality continuously and enable quick countermeasures in case of contamination, novel sensors are required. Here, immunoanalytical methods based on the binding of the analyte to highly selective antibodies can be helpful. In this work, magnetic bead-based immunoassays (MBBAs) have been developed for the detection of two relevant contaminants of drinking water: diclofenac (DCF) and amoxicillin (AMX). In case of the latter, not only the parent drug is of interest in the risk assessment but also its hydrolysis products (HPs). In a comprehensive study, the influence of external factors and intrinsic properties of the water on the rate of hydrolysis was investigated. As the hydrolysis of AMX further impacts the recognition by the antibody, a strategy to analyze samples with unknown hydrolysis degree of AMX was established employing the enzyme β-lactamase in sample preparation. For both analytes, the MBBAs enable the fast quantification with results obtained in less than one hour which represents a major improvement over conventional immunoassays like the enzyme-linked immunosorbent assay (ELISA). Compared to the respective ELISAs with the same antibodies, the MBBAs further exhibit improved analytical parameters such as a broader measurement range and lower limits of detection. Due to the magnetic properties of the beads that serve as a platform for the assays, they are suitable for the mobile and automated detection at the point-of-care. An integrated diagnostic system was designed in which electrochemical detection with chronoamperometry on a microfluidic chip allows for further miniaturization of the system to enable monitoring of the drinking water quality online in water supply pipes at waterworks. N2 - Die Kontamination von Trinkwasser mit Arzneimitteln stellt eine ernste Gesundheitsgefahr dar. Um die Trinkwasserqualität kontinuierlich überwachen und im Falle einer Verunreinigung zeitnah reagieren zu können, sind neuartige Sensoren erforderlich. Hier können immunanalytische Methoden, die auf der Bindung des Analyten an hochselektive Antikörper beruhen, hilfreich sein. In dieser Arbeit wurden magnetpartikelbasierte Immunoassays (MBBAs) für zwei relevante Kontaminanten des Trinkwassers entwickelt: Diclofenac (DCF) und Amoxicillin (AMX). Bei letzterem erwiesen sich neben der Ausgangsverbindung auch dessen Hydrolyseprodukte (HPs) als relevant für die Gefährdungsbeurteilung. In einer umfassenden Studie wurde der Einfluss von externen Faktoren und intrinsischen Eigenschaften des Wassers auf die Hydrolysegeschwindigkeit untersucht. Da die Hydrolyse von AMX auch die Erkennung durch den Antikörper beeinflusst, wurde eine Strategie zur Analyse von Proben mit unbekanntem Hydrolysegrad von AMX unter Verwendung des Enzyms β-Lactamase in der Probenvorbereitung entwickelt. Für beide Analyten ermöglichen die MBBAs eine schnelle Quantifizierung mit Ergebnissen in weniger als einer Stunde, was eine wesentliche Verbesserung gegenüber herkömmlichen Immunoassays wie dem Enzyme-linked Immunosorbent Assay (ELISA) darstellt. Im Vergleich zu den entsprechenden ELISAs mit denselben Antikörpern weisen die MBBAs zudem verbesserte analytische Parameter auf, wie einen breiteren Messbereich und niedrigere Nachweisgrenzen. Aufgrund der magnetischen Eigenschaften der Partikel, die als Plattform für die Assays dienen, eignen sie sich für den mobilen und automatisierten Einsatz vor Ort. Ein integriertes Diagnosesystem, bei dem die elektrochemische Detektion mittels Chronoamperometrie auf einem mikrofluidischen Chip eine weitere Miniaturisierung des Systems ermöglicht, wurde entworfen, um die Überwachung der Trinkwasserqualität online in Wasserwerken zu ermöglichen. KW - Antibiotics KW - Immunoassay KW - Amoxicillin KW - Diclofenac KW - Biosensor KW - Antibodies PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-591901 DO - https://doi.org/10.18452/25853 SP - 1 EP - 129 CY - Berlin AN - OPUS4-59190 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Weller, Michael G. T1 - The mystery of homochirality on earth N2 - Homochirality is an obvious feature of life on Earth. On the other hand, extraterrestrial samples contain largely racemic compounds. The same is true for any common organic synthesis. Therefore, it has been a perplexing puzzle for decades how these racemates could have formed enantiomerically enriched fractions as a basis for the origin of homochiral life forms. Numerous hypotheses have been put forward as to how preferentially homochiral molecules could have formed and accumulated on Earth. In this article, it is shown that homochirality of the abiotic organic pool at the time of formation of the first self-replicating molecules is not necessary and not even probable. It is proposed to abandon the notion of a molecular ensemble and to focus on the level of individual molecules. Although the formation of the first self-replicating, most likely homochiral molecule is a seemingly improbable event, on a closer look, it is almost inevitable that homochiral molecules have formed simply on a statistical basis. In this case, the non-selective leap to homochirality would be one of the first steps in chemical evolution directly out of a racemic “ocean”. Moreover, most studies focus on the chirality of the primordial monomers with respect to an asymmetric carbon atom. However, any polymer with a minimal size that allows folding to a secondary structure, would spontaneously lead to asymmetric higher structures (conformations). Most of the functions of these polymers would be influenced by this inherently asymmetric folding. To summarize, simple and universal mechanisms may have led to homochiral self-replicating systems in the context of chemical evolution. A homochiral monomer pool is deemed unnecessary and probably never existed on primordial Earth. N2 - Homochiralität ist ein offenkundiges Merkmal des Lebens auf der Erde. Andererseits enthalten extraterrestrische Proben überwiegend racemische Verbindungen. Das Gleiche gilt für jede gängige organische Synthese. Daher war es seit Jahrzehnten ein Rätsel, wie diese Racemate enantiomerenangereicherte Fraktionen als Grundlage für den Ursprung homochiraler Lebensformen bilden konnten. Es wurden zahlreiche Hypothesen darüber formuliert, wie sich bevorzugt homochirale Moleküle auf der Erde gebildet und angereichert haben könnten. In diesem Artikel wird gezeigt, dass die Homochiralität des abiotischen organischen Pools zum Zeitpunkt der Bildung der ersten selbstreplizierenden Moleküle nicht notwendig und nicht einmal wahrscheinlich ist. Es wird vorgeschlagen, die Vorstellung eines molekularen Ensembles aufzugeben und sich auf die Ebene der einzelnen Moleküle zu konzentrieren. Obwohl die Bildung des ersten selbstreplizierenden, vermutlich homochiralen Moleküls ein scheinbar unwahrscheinliches Ereignis ist, ist es bei näherer Betrachtung fast unvermeidlich, dass sich homochirale Moleküle einfach auf statistischer Basis gebildet haben. In diesem Fall wäre der nicht-selektive Sprung zur Homochiralität einer der ersten Schritte der chemischen Evolution direkt aus einem racemischen "Ozean" heraus. Außerdem konzentrieren sich die meisten Studien auf die Chiralität der ursprünglichen Monomere in Bezug auf ein asymmetrisches Kohlenstoffatom. Jedes Polymer mit einer Mindestgröße, die eine Faltung zu einer Sekundärstruktur ermöglicht, würde jedoch spontan zu asymmetrischen höheren Strukturen (Konformationen) führen. Die meisten Funktionen dieser Polymere würden durch diese inhärent asymmetrische Faltung beeinflusst. Zusammenfassend lässt sich sagen, dass einfache und universelle Mechanismen zu homochiralen selbstreplizierenden Systemen im Rahmen der chemischen Evolution geführt haben könnten. Ein homochiraler Monomerpool wird als unnötig erachtet und hat daher wahrscheinlich auf der Urerde auch nie existiert. KW - Chemical evolution KW - Abiogenesis KW - Chirality KW - Amino acids KW - Peptides KW - Folding chirality PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-598462 DO - https://doi.org/10.20944/preprints202401.1939.v1 SN - 2310-287X SP - 1 EP - 12 PB - MDPI CY - Basel AN - OPUS4-59846 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schroeder, Barbara T1 - Selektive und irreversible Immobilisierung von Antikörpern N2 - Das Ziel dieser Arbeit war es, die Vernetzung (Crosslinking) zwischen Protein G und einem Antikörper so durchzuführen, dass es zu keiner Modifikation der Antigen-Bindungsstelle des Antikörpers kommt. Zudem wurde im Rahmen dieser Arbeit ein Immunoassay entwickelt, mithilfe dessen zwanzig verschiedene Crosslinker in Hinblick auf ihre Fähigkeit Protein G zu funktionalisieren, untersucht werden konnten. Es konnten fünf Reagenzien identifiziert werden, die eine Derivatisierung von Protein G sowie eine anschließende Immobilisierung des Antikörpers auf dem Protein ermöglichen. Des Weiteren wurde gezeigt, dass mithilfe dieses Verfahrens sowohl die Immunpräzipitation als auch die massenspektrometrische Identifizierung und Charakterisierung von Proteinkomplexen erleichtert und verbessert werden kann. KW - Antikörper KW - Orientierte Immobilisierung KW - Protein A KW - Protein G KW - Linker KW - Crosslinker KW - IgG KW - Immunglobulin KW - Glutaraldehyd KW - 1,3-Butadiendiepoxid KW - NHS-Iodacetamid-Crosslinker SIAB KW - Succinimidyl(4-iodacetyl)aminobenzoat (SIAB) KW - Sulfo-SIAB KW - SIAB KW - SIA KW - SBAP PY - 2017 SP - 1 EP - 172 PB - Humboldt-Universität zu Berlin CY - Berlin AN - OPUS4-54537 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Canning, S. A1 - Voskuil, J. A1 - Weller, Michael G. T1 - An author and reviewer in conversation – reproducibility and antibody validation N2 - A recent Opinion Article by Jan Voskuil (JV), Aeonian Biotech, discussed the challenges in validation of research antibodies. It was openly peer reviewed by Michael Weller (MW), Federal Institute for Materials Research and Testing (BAM), Germany. In this blog, both discuss these challenges, the reproducibility crisis and open data. DA - 19 May, 2017 KW - Antibodies KW - Monoclonal KW - Antibody ID KW - Quality control KW - Open data KW - Reproducibility KW - Peer review PY - 2017 UR - https://blog.f1000.com/2017/05/19/an-author-and-reviewer-in-conversation-reproducibility-and-antibody-validation SN - 2051-9796 SP - 1 EP - 5 PB - F1000 Research Ltd. CY - London AN - OPUS4-40310 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Paul, Martin T1 - Microarrays for the screening of monoclonal antibodies from supernatants N2 - In this thesis a protocol based on a direct competitive and non-competitive immunoassay using the microarray format was developed to screen emulated hybridoma supernatants against the drug carbamazepine (CBZ). As support, epoxy slides were manufactured by coating microscope glass slides with epoxy silanes. The manufactured epoxy slides showed similar capacity for protein immobilization as commercially available NEXTERION slides, but showed a higher autofluorescence background. On the epoxy slides, protein A, Cys-A, G and Cys-G were immobilized as antibody capturing coating. It could be shown that the Cys-tag considerably increased the immobilization of all compared proteins, especially of protein G. Protein Cys-G immobilized at pH 8-9 was considered the most suitable protein for antibody immobilization due to good spot uniformity and a high binding capacity for IgG. Additionally, in immobilization experiments it could be shown, that 10-500 fold excess of bovine IgG, introduced by two different fetal bovine serum (FBS) products, showed no significant competition on the immobilization of mice or goat IgG on protein Cys-G. To examine the captured antibodies for affinity to CBZ, the CBZ-TOTA-DY654 tracer was custom synthesized. It could be demonstrated, that the tracer antibody interaction was competitive with the tracer precursor, CBZ-TOTA-NH2 and CBZ. Furthermore, the synthesized tracer was also successfully used by externals to evaluate CBZ affine hybriodoma cells in flow cytometry. In the simulated screening, five antibodies with known affinity to CBZ were diluted in a cell culture medium. The screening method allowed to differentiate between affine antibodies (IC50 < 20 µg/ml) and unaffine antibodies (IC50 > 20 µg/ml), when concentrations of 0.1 µg/ml IgG or greater have been used. Of five applied antibodies, all highly affine clones (CE2 and B3212M) were reported as positives while no false-positive samples were observed. The screening included competitive, with around 89500 fold excess of CBZ, and non-competitive tracer incubation on different segments of the same chip, which resulted in total signal suppression on the competitive segment. The screening was performed in 20 hours, only a few nanoliters, of each simulated supernatant, were consumed in the screening process, furthermore in the method standard 96 well MTPs were used and no cleanroom facilities were required. KW - Carbamazepine KW - Microscopic slides KW - Protein A cys KW - Competition KW - Epoxy silanes KW - Supernatant KW - Antibody immobilization PY - 2017 SP - 1 EP - 96 PB - Humboldt-Universität zu Berlin CY - Berlin AN - OPUS4-54645 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Völzke, Jule Lexa T1 - Herstellung und Charakterisierung Antigen-beschichteter Nanopartikel als Analoga von Virus-like Particles (VLP) N2 - In dieser Arbeit wurden drei verschiedene Nanomaterialien auf ihre Bindungsfähigkeit zu Proteinen untersucht. Zu Beginn standen dabei die Herstellung stabiler Dispersionen der einzelnen Nanopartikel und die Stabilität der gebildeten Konjugate im Vordergrund. Der Nachweis einer erfolgreichen Konjugatbildung, sprich der Beschichtung von Nanopartikel mit Proteinen, wurde sowohl qualitativ mittels DLS-Messungen als auch über quantitative Protein-Bestimmungen erbracht. Für die Quantifizierung konnten verschiedene Methoden eingesetzt werden. Neben der klassischen Vorgehensweise, welche indirekt über die Quantifizierung von ungebundenem Protein im Überstand erfolgt, konnten ihm Rahmen dieser Arbeit verschiedene direkte Bestimmungsmethoden entwickelt werden. So wurden mittels kolorimetrischer Tests, wie dem BCA-Assay und dem Bradford-Assay, Nanodiamantdispersionen mit Hilfe einer Korrekturwellenlänge vermessen und quantifiziert. Ebenso zum Einsatz kam die Methode der Aminosäureanalytik, welche aufgrund ihrer guten Rückführbarkeit auf Aminosäurestandards Ergebnisse mit hoher Richtigkeit generieren kann und ebenso die Detektion kleiner Proteinmengen möglich macht. Nach den erfolgten quantitativen Betrachtungen wurden die Protein-beschichteten Nanopartikel auf ihre Anwendbarkeit als Analoga von Virus-like Particles (VLP) bei einer Immunisierung zur Gewinnung von polyklonalen Antikörpern gegen humanes Ceruloplasmin in Kaninchen überprüft. Es konnte mittels ELISA gezeigt werden, dass die Konjugate erfolgreich für die Herstellung von Antikörpern eingesetzt werden können und im zeitlichen Verlauf einer Immunisierung eine Steigerung des Antikörper-Titers zu erreichen ist. KW - DLS KW - Dynamische Lichtstreuung KW - Aluminiumoxid KW - Nanodiamant KW - Gold-Nanopartikel KW - BSA KW - Albumin KW - Protein G KW - Ceruloplasmin KW - Immunpräzipitation KW - Ultraschall KW - BCA KW - Bradford-Assay KW - AAAA KW - Aromatische Aminosäureanalytik KW - ICP-MS KW - NaCl-Methode PY - 2018 SP - 1 EP - 107 PB - Humboldt-Universität zu Berlin CY - Berlin AN - OPUS4-54625 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Taube, Peter T1 - Development of columns based on glass monoliths for affinity chromatography N2 - The aim of this work was the preparation of a novel stationary monolithic phase for affinity chromatography and HPLC-applications. Therefore, we have chosen porous glass filters that are available with different pore sizes as raw materials to prepare monolithic columns. We purchased VitraPOR 4 (10-16 μm pore size) and VitraPOR 5 (1.0-1.6 μm pore size) monolithic glass filters. The physical properties of these glass filters were characterized. The surface area, pore size distribution and the porosity were determined using mercury intrusion porosimetry and BET. These glass filters only exhibit flow through pores and therefore show no bimodal pore size distribution in the mercury intrusion curves. Due to their low permeability, the applied filters that exhibit an inner diameter of 8.0 mm and a length of 15.0±0.1 mm could be operated at flow rates more than 10 ml/min. High flow rates are favorable for fast separation experiments. KW - Monolith KW - Affinity chromatography KW - Affinity extraction KW - Borosilicate glass KW - Sintered KW - Surface area KW - Flow rate KW - VitraPOR KW - Pressure KW - Protein A KW - Dynamic binding capacity KW - Protein A cys KW - Column regeneration KW - Performance comparison PY - 2017 SP - 1 EP - 102 PB - Humboldt-Universität zu Berlin CY - Berlin AN - OPUS4-54564 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Gabler, Mariella T1 - Development of an affinity-based method for the site-selective synthesis of antibody-drug-conjugates N2 - For the site-selective synthesis of ADCs, a variety of obstacles must be overcome. Those include designing bifunctional affinity peptides with reasonably low 𝐾𝑑-values that couple to the mAb in a site-selective manner. These peptides should also include a functional group that links the payload to the mAb under mild conditions without adversely affecting it. The bioconjugation between peptide and antibody and the linker between peptide and payload must be stable and durable to provide safety when used for medical purposes. The usage of metals and organic solvents should be minimized. Within the project, new types of functionalized affinity peptides were designed, and their affinity towards the Fc-fragment was determined. KW - Antibody drug conjugate KW - ADC KW - Human antibody KW - Peptide KW - Linker KW - Toxin KW - Payload KW - Monomethyl Auristatin E KW - MMAE KW - DM1 KW - Click chemistry KW - Copper-catalyzed KW - SDS-PAGE KW - HPLC KW - Trastuzumab KW - Herceptin KW - SPR KW - MALDI-TOF-MS KW - Mertansine KW - Site-selective bioconjugation KW - Affinity PY - 2021 SP - 1 EP - 100 PB - Humboldt-Universität zu Berlin CY - Berlin AN - OPUS4-54519 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Schwaar, Timm T1 - Entwicklung von multidimensionalen Hochdurchsatzmethoden zur Analyse von Partikel-basierten Peptidbibliotheken N2 - Gegenwärtig ist das Interesse und der Bedarf von Proteinbindern insbesondere in der Biotechnik und Pharmaforschung sehr groß. Kombinatorische, Partikel-basierte (One-Bead-One-Compound) Peptidbibliotheken sind eine Technik, um selektiv bindende Proteine zu identifizieren. Allerdings beinhaltet das Screening dieser Peptidbibliotheken aufwendige Schritte, wie die Separation, Sequenzierung und Charakterisierung von identifizierten Bindern. In dieser Arbeit wurde ein Chip-System entwickelt, auf dem alle Schritte eines Screenings durchgeführt werden können. Dafür wurde ein Glasobjektträger mit einem magnetisch leitenden, doppelseitigen Klebeband versehen. Die Partikel der Bibliothek wurden durch ein Sieb aufgetragen. Dies führte zu einer geordneten Immobilisierung der Partikel auf dem Chip. Über 30.000 Partikel konnten so auf einem Chip immobilisiert werden. Für die Identifizierung von selektiven Protein-bindenden Peptiden wird die immobilisierte Peptidbibliothek mit einem Fluorophor-markierten Protein inkubiert, bindende Partikel mittels Fluoreszenzscan identifiziert und die Peptidsequenz direkt auf dem Chip mittels Matrix-Assisted-Laser-Desorption/Ionization-(MALDI)-Flugzeit-(TOF)-Massenspektroskopie (MS) bestimmt. Die Durchführung einer Abbruchsequenz-Methode erlaubt die eindeutige Bestimmung der Peptidsequenzen mit einer nahezu 100 % Genauigkeit. Die entwickelte Technologie wurde in einem FLAG-Peptid-Modell validiert. Bei dem Screening wurden neue anti-FLAG-Antikörper-bindende Peptide identifiziert. Anschließend wurden in einem Screening von ca. 30.000 Partikeln IgG-bindende Peptide mit mittleren mikromolaren Dissoziationskonstanten identifiziert. Für die Identifizierung stärkerer Binder wurde eine magnetische Anreicherung entwickelt, die dem Chip-Screening vorgeschaltet werden kann. Hiermit wurden aus ca. 1 Million gescreenter Partikel, Peptide mit Dissoziationskonstanten im niedrigen mikromolaren Bereich identifiziert. N2 - The screening of one-bead-one-compound (OBOC) libraries is a well-established technique for the identification of protein-binding ligands. The demand for binders with high affinity and specificity towards various targets has surged in the biomedical and pharmaceutical field in recent years. The combinatoric peptide screening traditionally involves tedious steps such as affinity selection, bead picking, sequencing and characterization. In this thesis, a high-throughput “all-on-one chip” system is presented to avoid slow and technically complex bead picking steps. Beads of a combinatorial peptide library are immobilized on a conventional glass slide equipped with an electrically conductive tape. The beads are applied by using a precision sieve, which allows the spatially ordered immobilization of more than 30,000 beads on one slide. For the target screening, the immobilized library is subsequently incubated with a fluorophore-labeled target protein. In a fluorescence scan followed by matrix-assisted laser desorption/ionization (MALDI)-time of flight (TOF) mass spectrometry (MS), high-affinity binders are directly and unambiguously sequenced directly from the bead. The use of an optimized ladder sequencing approach improved the accuracy of the de-novo sequencing step to 100 %. This new technique was validated by employing a FLAG-based model system. In a first step, new peptide binders for the M2 anti-FLAG monoclonal antibody were identified. Finally, this system was utilized to screen for IgG-binding peptides. The screening of about 30.000 peptides on one chip led to the identification of peptide binders in the mid micromolar range. A magnetic enrichment technique was developed to increase the number of screened beads. By combining the magnetic enrichment strategy with the chip system, 1 million beads were screened and IgG-binders in the low micromolar range were identified. KW - Peptidbibliotheken KW - Hochdurchsatzscreening KW - Peptidsequenzierung KW - Chip-Screening PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-511649 DO - https://doi.org/10.18452/21793 SP - 1 EP - 153 PB - Humboldt-Universität CY - Berlin AN - OPUS4-51164 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Atanasova, Aleksandra T1 - Herstellung und Einsatz neuartiger Trypsin-Partikel für den enzymatischen Antikörper-Verdau N2 - In dieser Arbeit wurden zwei Trypsinvarianten, der Wildtyp (wtT) und eine thermostabile Variante (tsT), rekombinant hergestellt. Die Herstellung von Proteinen in Bakterien kann zu Fehlfaltungen und Einschlusskörperchen führen, weshalb eine geeignete Faltungsstrategie notwendig ist. In dieser Arbeit konnte eine schrittweise Vorgehensweise erfolgreich angewendet werden. Nach der Ni-NTA-Aufreinigung wurde zusätzlich eine substratspezifische Benzamidin-Aufreinigung eingesetzt, um die Aktivität zu verbessern. Außerdem wurden die rekombinanten Trypsine auf Korund immobilisiert. Korund ist ein kostengünstiges Material, das nach Silanisierung und Glutaraldehyd-Kopplung für die Bindung von Proteinen geeignet gemacht wurde. Dabei konnte gezeigt werden, dass mehr wtT als tsT gebunden wurde, was sich auch in den Kopplungsdichte widerspiegelte. Die immobilisierten Enzyme wurden in Bezug auf Aktivität, Wiederverwendbarkeit, Lagerfähigkeit und Temperaturstabilität untersucht. Beide Varianten zeigten vergleichbare Leistungen, wobei tsT bei höheren Temperaturen eine etwas bessere Stabilität aufwies. Für den Antikörperverdau wurden sowohl thermische als auch chemische Denaturierungen bei verschiedenen Temperaturen ( 37 °C und 60 °C) getestet. Die Analyse mit MALDI-TOF-MS zeigte, dass gute Werte für die Sequenzabdeckung erzielt werden konnten. Besonders die chemische Denaturierung führte zu besseren Ergebnissen mit weniger Selbstverdau. Beim Vergleich mit kommerziell immobilisiertem Crude-Trypsin zeigten die rekombinanten Varianten eine höhere Spezifität und bessere Sequenzabdeckung bei gleichzeitig geringerem Selbstverdau. Die Wiederverwendbarkeit wurde durch fünf Verdauzyklen bei 37 °C überprüft. Dabei blieb die Aktivität weitgehend stabil, auch wenn die Peakintensität in den MALDI-Spektren mit jedem Zyklus abnahm. Eine eindeutige Zuordnung der Fingerprints des Antikörpers aus einer Bibliothek von über 90 Antikörpern war trotz dessen gegeben. KW - Korund KW - Immobilisierung KW - Proteomik KW - Rekombinante Proteine KW - Thermostabile Enzyme PY - 2025 SP - 1 EP - 86 CY - Berlin AN - OPUS4-64433 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Döring, Sarah T1 - Sequence of Mus Musculus monoclonal IgG2c anti-CCMV Immunoglobulin N2 - We report the full-length nucleotide and amino acid sequences of the light (κ) and heavy chain of the IgG2c anti-CCMV monoclonal antibody (hybridoma clone BAM-CCMV-29-81), generated against Cowpea Chlorotic Mottle Virus (CCMV). Sequencing of hybridoma clone was performed using a cost-effective Sanger-based workflow that includes DNA-level subclass determination and peptide mass fingerprint confirmation. The κ-chain sequence was assigned to IGKV4-6101 / IGKJ101, while the heavy chain was assigned to IGHV2-601 / IGHD1-101 / IGHJ3*01 with IgG2c constant regions from the NOD strain. Both chains were validated against RNA Illumina sequencing, confirming 100% identity. The sequences are available in GenBank under accession numbers PX123807 (κ-chain) and PX123808 (heavy chain). KW - Antibody Sequencing KW - BAM-CCMV-29-81 KW - anti-CCMV-antibody PY - 2025 UR - https://www.ncbi.nlm.nih.gov/nuccore/PX123807 UR - https://www.ncbi.nlm.nih.gov/nuccore/PX123808 PB - National Library of Medicine CY - Bethesda AN - OPUS4-63968 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Fischer, Janina A1 - Kaufmann, Jan Ole A1 - Weller, Michael G. T1 - Simple Determination of Affinity Constants of Antibodies by Competitive Immunoassays N2 - The affinity constant, also known as the equilibrium constant, binding constant, equilibrium association constant, or the reciprocal value, the equilibrium dissociation constant (Kd), can be considered as one of the most important characteristics for any antibody-antigen pair. Many methods based on different technologies have been proposed and used to determine this value. However, since a very large number of publications and commercial datasheets do not include this nformation, significant obstacles in performing such measurements seem to exist. In other cases where such data are reported, the results have often proved to be unreliable. This situation may indicate that most of the technologies available today require a high level of expertise that does not seem to be available in many laboratories. In this paper, we present a simple approach based on standard immunoassay technology that is easy and quick to perform. It relies on the effect that the molar IC50 approaches the Kd value in the case of infinitely small concentrations of the reagent concentrations. A two-dimensional dilution of the reagents leads to an asymptotic convergence to Kd. The approach has some similarity to the well-known checkerboard titration used for the optimization of immunoassays. A well-known antibody against the FLAG peptide, clone M2, was used as a model system and the results were compared with other methods. This approach could be used in any case where a competitive assay is available or can be developed. The determination of an affinity constant should belong to the crucial parameters in any quality control of antibody-related products and assays and should be mandatory in papers using immunochemical protocols. N2 - Die Affinitätskonstante, auch bekannt als Gleichgewichtskonstante, Bindungskonstante, Gleichgewichtsassoziationskonstante oder der Kehrwert, die Gleichgewichtsdissoziationskonstante (Kd), kann als eine der wichtigsten Eigenschaften für jedes Antikörper-Antigen-Paar angesehen werden. Es wurden viele Methoden auf der Grundlage verschiedener Technologien vorgeschlagen und verwendet, um diesen Wert zu bestimmen. Da jedoch eine sehr große Anzahl von Veröffentlichungen und kommerziellen Datenblättern diese Informationen nicht enthalten, scheint es erhebliche Hindernisse bei der Durchführung solcher Messungen zu geben. In anderen Fällen, in denen solche Daten angegeben werden, haben sich die Ergebnisse oft als unzuverlässig erwiesen. Diese Situation könnte darauf hindeuten, dass die meisten der heute verfügbaren Technologien ein hohes Maß an Fachwissen erfordern, das in vielen Laboren nicht vorhanden zu sein scheint. In diesem Artikel stellen wir einen einfachen Ansatz vor, der auf der Standard-Immunoassay-Technologie basiert und einfach und schnell durchzuführen ist. Er beruht auf dem Effekt, dass sich der molare IC50-Wert dem Kd-Wert im Fall unendlich kleiner Konzentrationen der Reagenzienkonzentrationen nähert. Eine zweidimensionale Verdünnung der Reagenzien führt zu einer asymptotischen Konvergenz zu Kd. Der Ansatz weist eine gewisse Ähnlichkeit mit der bekannten Schachbrett-Titration auf, die zur Optimierung von Immunoassays verwendet wird. Ein bekannter Antikörper gegen das FLAG-Peptid, Klon M2, wurde als Modellsystem verwendet und die Ergebnisse wurden mit anderen Methoden verglichen. Dieser Ansatz kann in allen Fällen verwendet werden, in denen ein kompetitiver Test verfügbar ist oder entwickelt werden kann. Die Bestimmung einer Affinitätskonstante sollte zu den entscheidenden Parametern in jeder Qualitätskontrolle von Antikörper-bezogenen Produkten und Tests gehören und in Veröffentlichungen, die immunchemische Protokolle verwenden, obligatorisch sein. KW - ELISA KW - Microplate KW - Microtiter plate KW - IC50 KW - Test midpoint KW - Competitive immunoassay KW - Law of mass action KW - Thermodynamics KW - Equilibrium constant KW - SPR KW - Surface plasmon resonance KW - Clones KW - Interaction KW - kd value KW - ITC KW - MST PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-621298 DO - https://doi.org/10.20944/preprints202404.0996.v1 SN - 2310-287X SP - 1 EP - 11 PB - MDPI CY - Basel AN - OPUS4-62129 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lohrke, Heiko A1 - Kohlhoff, Harald A1 - Erdmann, Jessica A1 - Winkler, Nicolas P. A1 - Neumann, Patrick P. T1 - Combined GNSS/Visual Inter-Robot Tracking Method for Open-Path Gas Tomography N2 - Methane emissions are a significant environmental and safety concern, yet many gas tomography systems intended to measure them require manual alignment, reliable high-bandwidth links, or fiducials. We present a lightweight, fully autonomous framework enabling line-of-sight inter-robot Tunable Diode Laser Absorption Spectroscopy (TDLAS) measurements without such constraints. A sensor robot equipped with a gimbal-mounted TDLAS unit tracks a reflector robot bearing an illuminated, color-controllable target. Coarse localization is achieved via RTK-GNSS, with vision-based fine tracking and passive time synchronization handled onboard. The system, based on off-the-shelf Pixhawk controllers and ArduPilot firmware, was validated in a 15m × 7m outdoor trial. Despite GNSS inaccuracies and deliberate occlusion by a methane-filled bag, the system retained lock, recovered from visual loss in under one second, and captured a 2800 ppm·m plume signature. These results demonstrate robust, scalable methane sensing for mobile gas tomography or standalone leak detection. Core components are released open-source to support future deployment. T2 - IEEE SENSORS 2025 CY - Vancouver, BC, Kanada DA - 19.10.2025 KW - Gas tomography KW - Tracking KW - Robot KW - Methane KW - TDLAS PY - 2025 SN - 979-8-3315-4467-6 DO - https://doi.org/10.1109/SENSORS59705.2025.11330519 SP - 1 EP - 4 PB - IEEE CY - Piscataway, NJ, USA AN - OPUS4-65615 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Abbas, Ioana M. T1 - Development of LC-MS/MS methods for the quantitative determination of hepcidin-25, a key regulator of iron metabolism N2 - Isotope-dilution liquid chromatography-tandem mass spectrometry (ID-LC-MS/MS) is emerging in the field of clinical chemistry and laboratory medicine as an alternative to immunoassays and is acknowledged as the MS “gold standard” for small biomolecule quantification. Hepcidin-25, a key iron-regulatory peptide hormone discovered in 2000, has revolutionized the understanding of iron disorders and its quantitative determination in biological samples should advance the management of iron-related pathology (diagnosis, prognosis and treatment). This study applied LC-MS/MS, using the triple quadrupole (QqQ) mass spectrometer, in a rapid and robust analytical strategy for the quantification of hepcidin-25 in human serum, to be implemented in routine laboratories. For this purpose, two sample preparation strategies and two complementary chromatographic separation conditions were investigated, where the use of acidic mobile phases (0.1% trifluoroacetic acid) was compared with a novel approach involving solvents at high pH (containing 0.1% ammonia). The application of these LC-MS/MS methods to human samples in an intra-laboratory comparison, using the same hepcidin-25 calibrators, yielded a very good correlation of the results. The LC-MS/MS employing trifluoroacetic acid-based mobile phases was selected as a highly sensitive (limit of quantification LOQ of 0.5 μg/L) and precise (coefficient of variation CV<15%) method and was recommended as a reference method candidate for hepcidin-25 quantification in real samples (in the dynamic range of 0.5-40 μg/L). One of the novel aspects of the methodology was the use of amino- and fluoro-silanized autosampler vials to reduce the interaction of the 25-residue peptide to laboratory glassware surfaces. Moreover, this LC-MS/MS method was used for an international round robin study, applying a secondary reference material as a calibrator. By determining the degree of equivalence between the results of the ten participating methodologies, the performance of the method developed in this study was found to be in the optimal range as defined by the International Consortium for Harmonization of Clinical Laboratory Results (ICHCLR). In this work, the formation of hepcidin-25 complexes with copper(II) was investigated. The first reversed-phase chromatographic separation of hepcidin-25/Cu2+ and hepcidin-25 (copper “free”) was achieved by applying mobile phases containing 0.1% of ammonia (pH 11). LC-MS/MS and high-resolution mass spectrometry (Fourier-transform ion cyclotron resonance (FTICR) MS) were applied for the mass spectrometric characterization of the formed hepcidin-25-Cu(II) species at pH values of 11 and 7.4 respectively. A new species corresponding to hepcidin-25 complexed with two copper ions was identified at high pH. KW - Copper KW - LC-MS/MS KW - Chromatography KW - Mass spectrometry KW - Metal complex KW - Metalloprotein KW - Peptide KW - Metrology KW - Reference material PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:11-110-18452/20119-6 UR - https://edoc.hu-berlin.de/handle/18452/20119?show=full DO - https://doi.org/10.18452/19358 SP - 1 EP - 156 CY - Berlin AN - OPUS4-45780 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Steglich, P. A1 - Rabus, D. G. A1 - Sada, C. A1 - Paul, Martin A1 - Weller, Michael G. A1 - Mai, C. A1 - Mai, A. T1 - Silicon Photonic Micro-Ring Resonators for Chemical and Biological Sensing: A Tutorial N2 - Silicon photonic micro-ring resonators (MRR) developed on the silicon-on-insulator (SOI) platform, owing to their high sensitivity and small footprint, show great potential for many chemical and biological sensing applications such as label-free detection in environmental monitoring, biomedical engineering, and food analysis. In this tutorial, we provide the theoretical background and give design guidelines for SOI-based MRR as well as examples of surface functionalization procedures for label-free detection of molecules. After introducing the advantages and perspectives of MRR, fundamentals of MRR are described in detail, followed by an introduction to the fabrication methods, which are based on a complementary metal-oxide semiconductor (CMOS) technology. Optimization of MRR for chemical and biological sensing is provided, with special emphasis on the optimization of waveguide geometry. At this point, the difference between chemical bulk sensing and label-free surface sensing is explained, and definitions like waveguide sensitivity, ring sensitivity, overall sensitivity as well as the limit of detection (LoD) of MRR are introduced. Further, we show and explain chemical bulk sensing of sodium chloride (NaCl) in water and provide a recipe for label-free surface sensing. KW - Lab on a chip KW - Biosensor KW - Cmos KW - Silanization KW - Surface derivatization KW - Evanescent wave PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-529360 DO - https://doi.org/10.36227/techrxiv.14909901.v1 SP - 1 EP - 18 PB - IEEE CY - Piscataway Township AN - OPUS4-52936 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Paul, Martin A1 - Tannenberg, Robert A1 - Tscheuschner, Georg A1 - Ponader, Marco A1 - Weller, Michael G. T1 - Cocaine detection by a laser-induced immunofluorometric biosensor N2 - The trafficking of illegal drugs by criminal networks at borders, harbors, or airports is an increasing issue in public health as these routes ensure the main supply of illegal drugs. The prevention of drug smuggling, including the installation of scanners and other analytical devices to detect ultra-small traces of drugs within a reasonable time frame, remains a challenge. The presented immunosensor is based on a monolithic affinity column with a large excess of immobilized hapten, which traps fluorescently labeled antibodies as long as the analyte cocaine is absent. In the presence of the drug, some binding sites of the antibody will be blocked, which leads to an immediate breakthrough of the labeled protein, detectable by highly sensitive laser-induced fluorescence with the help of a Peltier-cooled complementary metal-oxide-semiconductor (CMOS) camera. Liquid handling is performed with high-precision syringe pumps and microfluidic chip-based mixing devices and flow cells. The biosensor achieved limits of detection of 23 pM (7 ppt) of cocaine with a response time of 90 seconds and a total assay time below 3 minutes. With surface wipe sampling, the biosensor was able to detect 300 pg of cocaine. This immunosensor belongs to the most sensitive and fastest detectors for cocaine and offers near-continuous analyte measurement. KW - Drug search KW - Customs KW - Confiscation KW - Border surveillance KW - Narcotics KW - International drug trade KW - Drug trafficking KW - Illicit drug KW - Immunosensor KW - Antibodies KW - Detection PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-529951 DO - https://doi.org/10.20944/preprints202107.0521.v1 SN - 2310-287X N1 - Geburtsname von Ponader, Marco: Wilke, M. - Birth name of Ponader, Marco: Wilke, M. SP - 1 PB - MDPI CY - Basel AN - OPUS4-52995 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Ponader, Marco A1 - Röder, Bettina A1 - Paul, Martin A1 - Weller, Michael G. T1 - Sintered glass monoliths as new supports for affinity columns N2 - A novel stationary phase for affinity separations is presented. This material is based on sintered borosilicate glass readily available as semi-finished filter plates with defined porosity and surface area. The material shows fast binding kinetics and excellent long-term stability under real application conditions due to lacking macropores and high mechanical rigidity. The glass surface can be easily modified with standard organosilane chemistry to immobilize selective binders or other molecules used for biointeraction. In this paper, the manufacturing of the columns and their respective column holders by 3D printing is shown in detail. The model system protein A/IgG was chosen as an example to examine the properties of such monolithic columns under realistic application conditions. Several specifications, such as (dynamic) IgG capacity, pressure stability, long-term performance, productivity, non-specific binding, and peak shape, are presented. It could be shown that due to the very high separation speed, 250 mg antibody per hour and column can be collected, which surpasses the productivity of most standard columns of the same size. The total IgG capacity of the shown columns is around 4 mg (5.5 mg/mL), which is sufficient for most tasks in research laboratories. The cycle time of an IgG separation can be less than 1 minute. Due to the glass material's excellent pressure resistance, these columns are compatible with standard HPLC systems. This is usually not the case with standard affinity columns, limited to manual use or application in low-pressure systems. The use of a standard HPLC system also improves the ability for automation, which enables the purification of hundreds of cell supernatants in one day. The sharp peak shape of the elution leads to an enrichment effect, which might increase the concentration of IgG by a factor of 3. The final concentration of IgG can be around 7.5 mg/mL without the need for an additional nanofiltration step. The purity of the IgG was > 95% in one step and nearly 99% with a second polishing run. KW - Affinity Chromatography KW - Glass KW - Purification KW - Antibodies KW - Solid support KW - HPLC KW - FPLC KW - Separation PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-529117 DO - https://doi.org/10.20944/preprints202103.0298.v1 SN - 2310-287X N1 - Geburtsname von Ponader, Marco: Wilke, M. - Birth name of Ponader, Marco: Wilke, M. SP - 1 EP - 17 PB - MDPI CY - Basel AN - OPUS4-52911 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Morcillo, Dalia A1 - Oelze, Marcus A1 - Seena Prem, Pranav A1 - de Oliveira Guilherme Buzanich, Ana A1 - Emmerling, Franziska A1 - Recknagel, Sebastian A1 - Panne, Ulrich A1 - Abad Andrade, Carlos Enrique T1 - Lithium isotope fractionation as an early indicator of degradation mechanisms in lithium-ion batteries N2 - Aging in lithium-ion batteries (LIBs) degrades performance and hinders sustainability, demanding advanced diagnostics for early failure prediction. We investigate lithium isotope fractionation (LIF) as an innovative probe of degradation in lithium cobalt oxide (LCO) coin cells aged over 0−700 cycles. High-precision multi-collector inductively coupled plasma mass spectrometry (MC-ICP-MS) quantified δ7Li variations across cell stages: non-cycled (0 cycles), newly formed (5 cycles), semi-aged (250 cycles), and fully aged (700 cycles). During early cycling (≤ 45 cycles), chemical processes drive 7Li enrichment at the anode (δ7Li vs LSVEC = +12 ‰) through solid electrolyte interphase (SEI) formation, while the cathode depletes in 7Li (δ7Li vs LSVEC = −0.7 ‰). Beyond 45 cycles, electric field-induced migration predominates, promoting 6Li intercalation into the anode and increasing the δ7Li of the cathode by 8.1 ‰. Mass balance verifies isotope conservation, attributing shifts to redistribution and trapping. Complementary electrochemical impedance spectroscopy (EIS) and X-ray absorption spectroscopy and diffraction confirm SEI expansion, cobalt oxidation, lattice shrinkage, and changes in electrode structure, corroborating LIF trends. Notably, a δ7Li inflection at approximately 270 cycles anticipates end-of-life by 70 cycles, surpassing traditional methods in sensitivity. LIF emerges as a predictive indicator of aging mechanisms, informing optimized designs for durable LIBs. KW - Lithium isotope fractionation KW - Lithium-ion batteries KW - Degradation mechanisms KW - LiCoO2 cathodes KW - LCO KW - Isotopic tracing KW - Lithium isotopes PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-650945 DO - https://doi.org/10.26434/chemrxiv-2025-16lvq SP - 1 EP - 19 AN - OPUS4-65094 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Abad Andrade, Carlos Enrique T1 - Advances and Applications of Molecular Absorption Spectrometry: from Non-Metals to Isotope Analysis N2 - The present work covers two main aspects of high-resolution continuum source graphite furnace molecular absorption spectrometry (HR-CS-GFMAS), an analytical technique for elemental trace analysis. First, a comprehensive mechanistic study of molecule formation in graphite furnaces is presented, which is a key step into the recovery of analytical signals. For this, the molecule formation of CaF was studied, which is used for the indirect analytical determination of fluorine in HR-CS-GFMAS. A zirconium coating catalyzes the CaF formation, and its structure was investigated. The kinetics of this reaction was established by monitoring its molecular spectrum at different atomisation temperatures. An Arrhenius plot showed a pseudo-first order reaction with respect to fluorine (n = 1). An intermediate state was isolated, and its structure was elucidated by spectroscopic methods: scanning electron microscopy with energy dispersive X-ray spectroscopy (SEM-EDX), X-ray photoelectron spectroscopy (XPS), X-ray absorption spectroscopy (XANES and EXAFS), and Raman microspectroscopy. Here a mechanism is proposed, where ZrO2 works as a heterogeneous catalyst: after a pyrolytic step, an intermediate state of ZrO(OCaF) is activated, and at higher temperatures, CaF(g) is released from the zirconium-coated graphite surface. Second, analytical methods were developed by using HR-CS-MAS as detector for non-metals and isotope analysis. Therefore, the determination of organic absorbable chlorine in water, the quantification of fluorine in consume care products with declared perfluorinated ingredients, and the determination of sulfur content in crude oils were investigated. Finally, the high resolution of the instrumentation allows to measure isotopic shifts with high precision in some observed molecular spectra. Consequently, the molecular spectra of enriched isotopes of boron and magnesium were investigated, establishing so the potential of HR-CS-MAS for the accurate and precise determination of isotopic amount ratios. Zusammenfassung Die vorliegende Arbeit befasst sich mit zwei zentralen Aspekten der High-Resolution-Continuum-Source-Molekülabsorptionsspektrometrie mit Graphitrohrtechnik (HR-CS-GFMAS), einer Analysetechnik für elementare Spurenanalyse. Der erste Teil der Arbeit umfasst eine mechanistische Studie zur Molekülbildung auf Graphitoberflächen. Dies ist ein wichtiger Schritt, um analytische Signale zu entdecken. Dazu wurde die Molekülbildung von CaF analysiert, welches für die indirekte, analytische Bestimmung von Fluor in HR-CS-GFMAS genutzt wird. Die CaF Bildung wurde mittels einer Beschichtung aus Zirconium katalysiert und deren Struktur analysiert. Die Kinetik dieser Reaktion wurde durch Beobachtung des jeweiligen Molekülspektrums bei verschiedenen Atomisierungstemperaturen beobachtet. Ein Arrheniusplot zeigte für Fluor (n = 1) eine Reaktion Pseudo-erster Ordnung. Ein Übergangszustand wurde über die mit Zirconium überzogene Grafitoberfläche isoliert und seine Struktur mittels spektroskopischer Methoden Energiedispersive Rasterelektronenmikroskopie / Röntgenspektroskopie (REM-EDX), Röntgenphoto¬elektronenspektroskopie (XPS), Röntgenabsorptionsspektroskopie (XAS) und Raman Spektroskopie untersucht. Auf Grundlage dieser Ergebnisse wird ein Mechanismus vorgeschlagen, bei dem ZrO2 als heterogener Katalysator fungiert; in Folge einer Pyrolysestufe wird ein Übergangszustand des ZrO(OCaF) aktiviert, welcher bei höheren Temperaturen CaF(g) an der Zirconium-Graphitoberfläche freisetzt. Im zweiten Teil der Arbeit werden Analysemethoden entwickelt, in dem HR-CS-MAS als Detektor für Nichtmetalle und Isotopanalyse angewandt wird. Hierfür wurde organisch gebundenes Chlor im Wasser bestimmt, der Fluorgehalt in Pflegeprodukten mit perfluorierten Inhaltsstoffen quantifiziert und der Schwefelgehalt in Erdöl untersucht. Weiterhin ermöglicht die hohe Auflösung der Messgeräte eine präzise Bestimmung der Isotopenverschiebung einiger untersuchter Molekülspektren. Daher wurden die Molekülspektren angereicherter Bor- und Magnesiumisotope untersucht. Auf diese Weise wurde das Potential von HR-CS-MAS für die akkurate und präzise Bestimmung von Isotop-Mengenverhältnissen nachgewiesen. KW - Isotope analysis KW - Non-metals analysis KW - Molecular absorption spectrometry KW - Boron KW - Fluorine KW - Graphite furnace KW - HR-CS-MAS KW - Applied optical spectroscopy PY - 2019 UR - https://hu-berlin.hosted.exlibrisgroup.com/permalink/f/jl2ii5/HUB_UB_ALMA_DS21669801300002882 SP - X EP - 118 CY - Berlin, Germany AN - OPUS4-49891 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Prinz, Carsten A1 - Zimathies, Annett A1 - Emmerling, Franziska T1 - Experimental raw data sets associated with certified reference material BAM-P114 (titanium dioxide) for comparison of nitrogen and argon sorption, available in the universal adsorption information format (AIF) N2 - These data sets serve as models for calculating the specific surface area (BET method) using gas sorption in accordance with ISO 9277. The present measurements were carried out with nitrogen at 77 Kelvin and argon at 87 Kelvin. It is recommended to use the following requirements for the molecular cross-sectional area: Nitrogen: 0.1620 nm² Argon: 0.1420 nm² Expected specific surface area for nitrogen (BET): 24 to 25 m²/g Expected specific surface area for argon (BET): 20 m²/g Titanium dioxides certified with nitrogen sorption and additionally measured with argon for research purposes were used as sample material. The resulting data sets are intended to serve as comparative data for own measurements and show the differences in sorption behaviour and evaluations between nitrogen and argon. These data are stored in the universal AIF format (adsorption information format), which allows flexible use of the data. KW - Physisorption KW - Specific surface area KW - AIF KW - Argon KW - Nitrogen PY - 2024 DO - https://doi.org/10.5281/zenodo.13283291 PB - Zenodo CY - Geneva AN - OPUS4-60782 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Smales, Glen Jacob A1 - Pauw, Brian Richard T1 - DACHS/MOFs/AutoMOFs_3/Synthesis N2 - The DACHS (Database for Automation, Characterization and Holistic Synthesis) project aims to create completely traceable experimental data, covering syntheses, measurements, analyses, and interpretations. DACHS_MOFs focuses on the synthesis and characterisation of metal-organic frameworks, across multiple, automation-assisted experimental series (AutoMOFs), with the overall goal of producing reproducible MOF samples through tracking of the synthesis parameters. DACHS_MOFs is simultaneously used to test the DACHS principles. This upload contain synthesis data from AutoMOFs_3 in HDF5 format (.h5). Each .h5 file contains detailed information on the chemical, experimenal, and synthesis parameters used during the synthesis of a single AutoMOF sample. KW - Synthesis KW - Automation KW - Traceability KW - Procedure PY - 2024 DO - https://doi.org/10.5281/zenodo.11237815 PB - Zenodo CY - Geneva AN - OPUS4-60633 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Herzel, Hannes T1 - Phase reaction during thermochemical treatment of sewage sludge and biomass ashes with alkali compounds to increase nutrient plant availability N2 - Das Element Phosphor ist für Pflanzen, Tiere und Menschen essenziell. Um die Phosphorversorgung für Pflanzen in der Landwirtschaft zu gewährleisten, werden Phosphordünger eingesetzt. Die Nährstoffe werden hauptsächlich durch Wirtschaftsdünger (Gülle, Jauche, Stallmist) zurückgeführt. Zusätzlich werden in der konventionellen Landwirtschaft mineralische Phosphordünger eingesetzt, die vorwiegend aus dem fossilen Rohstoff Phosphorit gewonnen werden. Um die Abhängigkeit von fossilen Rohstoffen zu reduzieren, sollen nährstoffhaltige Rest- und Abfallstoffe zur Phosphordünger aufbereitet werden. In Abwasserkläranlagen fällt phosphorreicher Klärschlamm als Abfallstoff an. Der größte Anteil des Klärschlammes wird in Steinkohlekraftwerken, Zementwerken oder in Monoklärschlammverbrennungsanlagen verbrannt. Die Klärschlammaschen aus den Monoverbrennungsanlagen enthalten bis zu 12 Gew.-% Phosphor und sind daher für die Düngerherstellung geeignet. Ein geeignetes Verfahren zur Aufbereitung der Klärschlammaschen ist die thermochemische Behandlung im Drehrohrofen. Mit dem sogenannten AshDec®-Prozess, kann ein Phosphordünger hergestellt werden. Aktuell wird eine großtechnische Anlage in Altenstadt (Bayern) geplant, die im Jahr 2023 den Betrieb aufnehmen soll. Der zentrale Bestandteil ist die Phasenumwandlung von schlecht pflanzenverfügbaren Phosphaten in der Klärschlammasche (vorwiegend das Calciumphosphat Whitlockit und Aluminiumphosphat) zu gut pflanzenverfügbaren Calciumalkaliphosphaten im Produkt. Um dies zu erzielen, werden die Aschen mit Natrium- und/oder Kalium-Verbindungen gemischt und einer thermochemischen Behandlung bei 800-1000 °C zugeführt. Um die Pflanzenverfügbarkeit und Düngewirkung von Phosphaten abschätzen zu können, ist die chemische Extraktionsmethode mit neutraler Ammoniumcitratlösung geeignet. In der Dissertation werden die (Phosphor-)Phasenreaktionen und die Prozessbedingungen des thermochemischen Verfahrens untersucht, um das Verfahren gezielt zu modifizieren und die Wirtschaftlichkeit zu steigern. Die Zielphasen der thermochemischen Behandlung sind die Calciumalkaliphosphate CaNaPO4 und CaKPO4, und deren Mischphasen Ca(Na,K)PO4, welche in der Publikation 3.1 synthetisiert wurden. Für diese Calciumalkaliphosphate wurden die thermodynamischen Daten der Standardbildungsenthalpie, Standardentropie, Wärmekapazität und die Wärmemenge der Phasenumwandlung bestimmt (Publikation 3.1). Bei der thermochemischen Behandlung von Klärschlammaschen wurden als Additive Natrium- und Kaliumsulfat bei verschiedenen Temperaturen getestet. Der Einsatz von Kaliumadditiven ist erwünscht, um den Marktwert des Produktes durch die Produktion eines Phosphor-Kalium-Düngers zu erhöhen. Zusätzlich wird eine möglichst geringe Prozesstemperatur angestrebt, bei der die erwünschten Calciumalkaliphosphate gebildet werden. In den Publikationen 3.2 und 3.3 wird gezeigt, dass für Klärschlammaschen eine komplette Phasenumwandlung zu Calciumnatriumphosphaten ab 875 °C in Laborversuchen (Korundtiegel) mit dem Additiv Natriumsulfat erzielt werden kann. Der Einsatz von Kaliumsulfat erforderte notwendige Reaktionstemperaturen von über 1100 °C. Diese unterschiedlichen Reaktionstemperaturen hängen mit den Schmelzpunkten von Natriumsulfat (890 °C) und Kaliumsulfat (1070 °C) zusammen. Um Kaliumsulfat in den Prozess bei niedrigen Temperaturen zu integrieren, wurden Natriumsulfat und Kaliumsulfat vor der Behandlung gemischt. Dies führte zu einer Schmelzpunkterniedrigung und resultierte in Reaktionstemperaturen zwischen 900 °C bis 1000 °C für die untersuchten Mischungen von Natrium- und Kaliumsulfat (Publikation 3.3). Die Zusammensetzung der Calciumalkaliphosphate Ca(Na,K)PO4 war anders als erwartet. Bei der Phasenanalytik stellte sich heraus, dass bei geringem und mittlerem Anteil von Kaliumsulfat im Alkali-Additiv nur Calciumnatriumphosphate mit sehr geringen Kaliumgehalten gebildet wurden. Erst bei einem hohen Anteil von Kaliumsulfat in der Mischung der Alkalisulfate konnten kaliumhaltige Calciumalkaliphosphate nachgewiesen werden (u.a. (Ca0.9Mg0.1)(Na0.6K0.4)PO4). Dieser geringere Einbau von Kalium in die Calciumalkaliphosphate hängt mit den zusätzlich stattfindenden Reaktionen zwischen den Alkalien und den Silikaten zusammen. Es ist bekannt, dass die zugegebenen Alkalisulfate zuerst mit Silikaten und anschließend mit den Phosphaten reagieren. Silikate bauen bevorzugt Kalium ein, deswegen konnten erst kaliumhaltige Phosphate gebildet werden, wenn die Reaktion mit den Silikaten abgeschlossen war. Dies führte zu einem geringeren Kaliumanteil in den gebildeten Phosphaten im Vergleich zum Kaliumanteil der verwendeten Alkaliadditive. Das in Silikaten gebundene Kalium ist wahrscheinlich schlecht für die Pflanzen verfügbar. Dies könnte den Einsatz der produzierten Phosphor-Kalium-Dünger einschränken. Der bevorzugte Kaliumeinbau in Silikaten konnte auch in Kalkulationen mit den thermodynamischen Daten aus der Publikation 3.1 gezeigt werden. Mittels Phasenanalytik vor und nach der chemischen Extraktion, konnte die Zugehörigkeit zu verschiedenen Modifikationen der Calciumalkaliphosphaten sicher bestimmt werden und eine ungefähre Zusammensetzung dieser Calciumalkaliphosphate abgeschätzt werden. So konnte nachgewiesen werden, dass die Modifikation vom CaNaPO4 ungefähr 10 % Magnesium einbauen kann. Wenn mehr Magnesium eingebaut wird, bildet sich die Phase (Ca,Mg)NaPO4, die eine vergleichbare Struktur wie die bekannte Phase (Ca0.72Mg0.28)NaPO4 aufweist. Dieses magnesiumreiche Calciumnatriumphosphat entstand vermutlich, wenn entweder erhöhte Anteile an Kalium eingebaut wurden (Ca0.8Mg0.2)(Na0.85K0.15)PO4 (Publikation 3.3) oder die Phasenumwandlung vom Calciumphosphat Whitlockit zum Calciumalkaliphosphat CaNaPO4 noch nicht abgeschlossen war (Publikation 3.2). Wenn mehr Kalium eingebaut wird, dann entsteht eine Phase (u.a. (Ca0.9Mg0.1)(Na0.6K0.4)PO4) ähnlich zu den Mischphasen aus der Publikation 3.1. In den Publikationen 3.4 und 3.5 wurden keine Klärschlammaschen untersucht, sondern Biokohlen aus Modellklärschlämmen (Publikation 3.5) und Biomasseaschen (Publikation 3.4) aus der Vergasung oder Verbrennung einer Mischung aus Zuckerrohrbagasse und Hühnertrockenkot. Die thermochemischen Produkte der Biokohlen bzw. Biomasseaschen enthielten das gewünschte CaNaPO4 und hatten eine hohe Düngewirkung in Pflanzenwachstumsversuchen mit Sojapflanzen bzw. Gräsern. KW - AshDec KW - Recycling fertilizer KW - Calcium alkali phosphate PY - 2020 SP - 1 EP - 186 CY - Jena AN - OPUS4-54724 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Pauw, Brian Richard A1 - Laskina, Sofya A1 - Naik, Aakash A1 - Smales, Glen Jacob A1 - George, Janine A1 - Breßler, Ingo A1 - Benner, Philipp T1 - "Ultima Ratio": Simulating wide-range X-ray scattering and diffraction N2 - We demonstrate a strategy for simulating wide-range X-ray scattering patterns, which spans the small- and wide scattering angles as well as the scattering angles typically used for Pair Distribution Function (PDF) analysis. Such simulated patterns can be used to test holistic analysis models, and, since the diffraction intensity is on the same scale as the scattering intensity, may offer a novel pathway for determining the degree of crystallinity. The "Ultima Ratio" strategy is demonstrated on a 64-nm Metal Organic Framework (MOF) particle, calculated from Q < 0.01 1/nm up to Q < 150 1/nm, with a resolution of 0.16 Angstrom. The computations exploit a modified 3D Fast Fourier Transform (3D-FFT), whose modifications enable the transformations of matrices at least up to 8000^3 voxels in size. Multiple of these modified 3D-FFTs are combined to improve the low-Q behaviour. The resulting curve is compared to a wide-range scattering pattern measured on a polydisperse MOF powder. While computationally intensive, the approach is expected to be useful for simulating scattering from a wide range of realistic, complex structures, from (poly-)crystalline particles to hierarchical, multicomponent structures such as viruses and catalysts. KW - X-ray KW - Simulation KW - 3D Fourier Transform KW - High resolution KW - XRD KW - SAXS KW - PDF KW - Total scattering KW - X-ray scattering KW - Metal organic framework KW - Electron density map KW - FFT PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-572067 DO - https://doi.org/10.48550/arXiv.2303.13435 VL - Cornell University SP - 1 EP - 12 PB - Ithaca, NY AN - OPUS4-57206 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stroh, Julia A1 - Emmerling, Franziska ED - Plank, J. ED - Lei, L. T1 - Direct insight into the admixture activity during cement hydration using levitated droplets N2 - Chemical admixtures are widely used to adjust properties of the cementitious mixtures. Different superplasticizers (SP) are typically added to improve the flowability of the fresh cement paste. Their working period is the initial stage of the cement hydration from its beginning until stiffening. Currently, polycarboxylate-based SP (PCE-SP) are the most effective ones. They can act beyond their aimed function causing changes in the hydration course, e. g. retardation effects. The exact mechanisms and influencing factors are still under investigation. However, the occurrence of the retardation effect indicates the involvement of PCE in the hydration reactions. Some observations indicate, that the retardation depends on the type, molecular structure and concentration of PCE, and the presence of other admixtures (stabiliser, ST). These factors influence further the working time of admixture and its amount related efficacy in the flow improvement. We investigate the cement hydration process in situ in levitated droplets. High resolution synchrotron X-ray diffraction allows gathering temporal course of the hydration reactions. The measurement setup is based on an ultrasonic levitator allowing in situ investigation of the temporal changes of the phase composition in the hydrating cementitious system. Further, the hydration can be followed ab initio avoiding the time loss for the sample preparation and filling in the sample holder. The collected data allows to conclude about the mechanisms of the admixture action and their involvement into the ongoing hydration process. T2 - 2nd International Conference on Polycarboxylate Superplasticizers (PCE 2017) CY - München, Germany DA - 28.09.2017 KW - Portland cement KW - Initial hydration KW - Acoustic levitator KW - Admixtures KW - Time resolution PY - 2017 SN - 978-3-9816240-6-9 SP - 185 EP - 193 AN - OPUS4-43167 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Kazlagić, Anera T1 - Provenancing of cement by the means of isotope techniques N2 - Concrete is the most important human-made material because it serves as the basis of our built environment. Since the properties of concretes are dominated by their key compound, cement, devising a way to determine the cement’s origin, known as provenancing, is of great importance for answering different provenance-related questions. These questions range from liability issues when damage occurs to concrete-made structures, to forensic investigations where cement particles are found at crime scenes. This thesis showcases the use of isotope techniques to answer these provenance-related questions. Conventional 87Sr/86Sr and 143Nd/144Nd isotope and elemental ratios consisting of Ca, Sr, K, Mn, Mg, and Ti are used as fingerprints for ordinary Portland cement (OPC) provenancing. The first part of this thesis describes research previously conducted in fingerprinting cementitious materials, providing an overview of provenance studies of cement and the main approaches commonly used. In several studies, the origin of clinker for certain locations was determined via different approaches. However, clinker is an intermediate product, which is available only at the production site and therefore, the practical relevance is rather limited. Furthermore, the use of Sr and Nd isotope systems, together with elemental fingerprints are presented as state of the art in the field. Therein, the principal approach for the overall study is sketched. For the second part of the study, a sample preparation technique for Sr isotopes in Portland cement was developed. The aim was to find the most appropriate sample preparation procedure for cement provenancing and selection was realised by comparing the 87Sr/86Sr isotope ratios of differently treated OPCs with those of the corresponding clinkers. Based on these findings, the third part of the study focused on the measurements of Sr and Nd isotope ratios, together with elemental ratios, to establish a reliable technique for OPC provenancing. The outcomes of this final stage are then used to establish a procedure for fingerprinting cements. This becomes possible with the use of Sr and Nd isotope ratios and geochemical profiles. To perform isotope ratio measurements and obtain reliable data, it was necessary to establish a quality control procedure. Thus, an interlaboratory comparison (ILC) was organised to characterise 87Sr/86Sr isotope ratios in geological and industrial reference materials by applying the conventional method for 87Sr/86Sr isotope ratios. As reference material, four cements (VDZ 100a, VDZ 200a, VDZ 300a, IAG OPC-1), one limestone (IAG/CGL ML-3) and one slate (IAG OU-6) were selected, thus covering a wide range of Sr isotope signatures. KW - Isotope ratio KW - Strontium KW - Neodymium KW - Ordinary Portland cement PY - 2023 SP - 1 EP - 148 CY - Berlin AN - OPUS4-59172 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geburtig, Anja A1 - Schulz, Ulrich A1 - Mechtel, M. A1 - Klimmasch, T. T1 - Reflow ability of automotive coatings T2 - 27th FATIPEC Congress CY - Aix-en-Provence, France DA - 2004-04-19 PY - 2004 VL - 1 SP - 279 EP - 289 PB - Association Francaise des Techniciens des Peintures, Vernis,Encres CY - Aix en Provence AN - OPUS4-21349 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geburtig, Anja A1 - Wachtendorf, Volker A1 - Trubiroha, P. T1 - Simulationsdaten zur photooxidativen Beanspruchung an verschiedenen geografischen Freibewitterungs-Standorten N2 - Freibewitterungen weisen grundsätzlich eine hohe Variabilität der jeweiligen Intensität der Beanspruchungsparameter auf; sie sind nicht einfach wiederholbar. Um dennoch die Ergebnisse einer Beanspruchung vergleichen zu können, ist eine aussagekräftige Charakterisierung der Freibewitterung wichtig. Traditionell werden Daten bekannter Einflussgrößen wie Globalstrahlung, Temperatur oder Feuchtewerte herangezogen. Obwohl man weiß, dass diese Größen an den exponierten Oberflächen wechselwirken und kombiniert als Mikroklima Einfluss auf Degradationsprozesse nehmen, werden schon aus Praktikabilitätsgründen diese separat als klimatische Messgrößen angegeben. Die Aussagekraft dieser Daten ist mäßig. Ziel dieses Beitrags ist es, die Aussagekraft und damit Vergleichbarkeit zu erhöhen, indem diese Messdaten als Stundendaten zu Wirkintegralen vorverarbeitet und jahresweise akkumuliert werden. Betrachtet wird dafür der Prozess der Photooxidation, da dieser Alterungs-mechanismus bei allen Kunststoffen auftritt. Für eine einfache Modellierung wird die wirksame UV-Bestrahlung, gewichtet mit einer Arrhenius-abhängigen Ober¬flächen-temperatur (TOF), über den Beanspruchungszeitraum von hier je einem Jahr akkumuliert. Die Idee einer solchen Messgröße für photooxidative Ober¬flächen¬alterung wurde bereits vorgestellt [1]. Dort wurde ein Gerät vor¬geschlagen, mit dem dieser Wert für verschieden absorbierende Oberflächen für die Dauer einer Exposition akkumuliert wird, und ergänzend eine Abschätzung der Betauungs¬zeiten dieser Referenz-Oberflächen erfolgen könnte. Hier soll es um eine rechnerisch generierte Zusammenstellung dieser photo¬oxidativen 1-Jahres-Alterungswerte für verschiedene Standorte gehen. Ein Temperaturfaktor erfasst dabei den Einfluss der Strahlungserwärmung auf eine weiße, graue bzw. schwarze Referenzoberflächen, spiegelt also die Kopplung von solarer Strahlung und Temperatur wider [1]. Ermittelt wird er aus Stunden¬daten der Globalstrahlung und der Lufttemperatur. Die spektrale Wirkung wird aus Sonnenhöhenständen entsprechend der geografischen Breite mit Hilfe der FastRT-Oberfläche [2] als PiT·h-Wert abgeschätzt [3]. Anhand der errechneten Jahreswerte können die Schweregrade der photo¬oxidativen Beanspruchung an den verschiedenen Standorten unmittelbar verglichen werden. Die gezeigten Simulationsdaten für ein solches „elektronisches Referenzmaterial“ für photooxidative Degradation zeigen die prinzipielle Möglichkeit einer Kartografierung solcher Daten auf. T2 - 53. Jahrestagung der GUS CY - Stutensee-Blankenloch, Germany DA - 26.03.2025 KW - Polymer 3R, UV, Bestrahlung, Bewitterung PY - 2025 SN - 978-3-9826129-2-8 VL - 53 SP - 19 EP - 28 PB - Gesellschaft für Umweltsimulation e.V. CY - 76327 Pfinztal (Berghausen) AN - OPUS4-62902 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geburtig, Anja A1 - Trubiroha, Peter A1 - Wachtendorf, Volker T1 - Significance of new data pairs for irradiance and (surface) temperature N2 - There is consent that UV irradiance and temperature at the place of photodegradation are the most important environmental parameters in weathering, along with humidity. This contribution shows how an improvement in the measurement data situation can improve the significance and comparability of outdoor exposures. Photooxidative ageing is calculated using sample polymers for which the corresponding modelling data (Exposure Response Functions, ERF) is available. The mean square deviations are estimated, which result from using different spectral irradiances and different spectral sensitivities, both of the sensors and the polymers. It will be shown here how the significance of the irradiance values increases with increasing approximation of the spectral sensitivities of the sensor and polymer. Also, the mean square deviations are estimated, which result from using different activation energies and surface temperatures. A selection of different variables to describe the weathering exposure is created. The potential of either individual values or data pairs is evaluated in terms of significance or correlation to the calculated photooxidative ageing. Recording hourly data also enables subsequent evaluations of individual test specimens, adapted to the respective colour or to determine activation energies. An accumulated value, calculated from PIT-radiometer irradiance and a suited surface temperature, can provide a comparison of different outdoor exposures over different locations or years. Thus, a characterisation of the weathering exposure would be related to a reference spectral sensitivity (much closer to a polymer than that of a common UV radiometer), one reference activation energy, and different surface temperature scenarios with, on the one hand, graded solar absorptions (white / grey / black) and, on the other hand, different thermal couplings (coated metal / thick plastic). This results in three values each for plastic samples and coated metals (light / grey / dark). It will never be possible to accurately predict the weathering tests for individual samples (with their specific sensitivities), but the proposed approaches can go a long way towards the comparability of outdoor weathering exposures. T2 - 10th European Weathering Symposium EWS CY - Graz, Austria DA - 11.09.2024 KW - Polymer 3R KW - Outdoor weathering PY - 2024 SN - 978-3-9826129-1-1 SP - 121 EP - 133 PB - Stober Medien GmbH CY - Eggenstein AN - OPUS4-61291 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völzke, Holger A1 - Nieslony, Gregor A1 - Noack, Volker A1 - Hagenow, Peter A1 - Kovacs, Oliver T1 - Current developments in container design testing for the Konrad repository N2 - The Konrad repository for not heat generating radioactive wastes was licensed first in 2002. But due to legal actions this license has not been finally confirmed before 2007. Subsequently, the Federal Office for Radiation Protection (BfS) began scheduling backfitting of the former iron ore mine into a repository. The licensed repository volume is 303,000 m3 based on estimations of expected waste volumes to be disposed off although the mine itself would offer a much larger volume. Once the repository is ready for Operation, waste packages can be disposed, but this is not expected before the end of this decade. Nevertheless, there is already today a great interest in qualified and certified waste conditioning and packaging for disposal requiring Containers, tested, evaluated and certified by BAM and BfS. Key points of the Konrad license concern comprehensive requirements for waste products and Containers. Details are described in BfS reports, which constitute the basic documents for the license. Following the final license confirmation a revision of these documents has been requested in order to include considerations of water poisoning substances. This work is currently done by BfS in Cooperation with the NLWKN of Lower Saxony and the Institute for Safety Technology (ISTec). Concerning the specification for Containers themselves no or only minor changes are expected. T2 - KONTEC 2011 - 10. Internationales Symposium "Konditionierung radioaktiver Betriebs- und Stilllegungsabfälle" CY - Dresden, Germany DA - 06.04.2011 KW - Cask KW - Safety KW - Repository KW - Design testing KW - Radioactive waste PY - 2011 SP - 683 EP - 695 AN - OPUS4-23672 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geburtig, Anja A1 - Wachtendorf, Volker A1 - Trubiroha, P. T1 - Discussion on Weathering Reference Materials N2 - Weathering reference materials (WRMs) are used to characterize the harshness of an exposure, aiming on either reproducibility of a specific exposure or on the comparability between various kinds of natural or artificial weathering exposure. The materials that are used as weathering reference materials differ in their sensitivities (as well as in interactions and interferences of the latter), conditioned by the different processes which lead to the respective property change. It is also essential to take into account the necessary measurement equipment for the respective property change, in order to allow timely intervention. What are the key issues on choosing a weathering reference material? What can be learned from the weathering reference materials, investigated so far? Possibilities and limitations are discussed on the basis of existing weathering reference materials. Conclusions are drawn, for establishing new weathering reference materials. T2 - 9th European Weathering Symposium CY - Basel, Switzerland DA - 18.09.2019 KW - Temperature dependency KW - Weathering KW - Irradiation KW - Spectral sensitivity PY - 2019 SN - 978-3-9818507-5-8 SP - 283 EP - 292 PB - Thomas Würtz Grafik-Design CY - Karlsruhe, Germany AN - OPUS4-49150 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Kohlbrecher, J. A1 - Breßler, Ingo T1 - SASfit 0.94.12 N2 - Small-angle scattering is an increasingly common method for characterizing particle ensembles in a wide variety of sample types and for diverse areas of application. SASfit has been one of the most comprehensive and flexible curve-fitting programs for decades, with many specialized tools for various fields. KW - Small-angle scattering KW - SAXS KW - SANS KW - Scattering pattern analysis PY - 2023 UR - https://doi.org/10.5281/zenodo.7530357 DO - https://doi.org/10.5281/zenodo.7530356 PB - Zenodo CY - Geneva AN - OPUS4-57913 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geburtig, Anja A1 - Wachtendorf, Volker A1 - Trubiroha, P. A1 - Giehl, A. A1 - Schönlein, A. A1 - Feil, F. T1 - Normenvorschlag zur Bewitterung transparenter oder transluzenter Kunststoffe N2 - Aufgrund des tieferen Eindringens der solaren Strahlung treten bei transparenten und bei transluzenten (durchscheinenden) Kunststoffen veränderte Bedingungen gegenüber opaken Proben auf. Dies kann zu speziellen Effekten und damit zu einem abweichenden Bewitterungsverhalten führen. Auch aus Mangel an geeigneten Normen werden diese Effekte häufig vernachlässigt. Deshalb initiiert der DIN-FNK auf ISO-Ebene ein entsprechendes Dokument. Die Norm ist in der Form eines Technical Reports geplant. In einem ersten Teil sollen die Besonderheiten transparenter oder transluzenter Kunststoffe erläutert werden, um den Nutzer für mögliche Probleme zu sensibilisieren. Im zweiten Teil werden Empfehlungen für Bestrahlung oder Bewitterung herausgearbeitet. In einem dritten Teil geht es dann um Besonderheiten bei der Messung von Eigenschaftsänderungen transparenter bzw. transluzenter Kunststoffe. In informativen Anhängen sollen verschiedene Beispiele die Thematik illustrieren. T2 - 51. Jahrestagung der GUS CY - Stutensee-Blankenloch, Germany DA - 29.03.2023 KW - Bewitterung KW - Polymer 3R KW - Bestrahlung KW - UV PY - 2023 SN - 978-3-9818507-8-9 SP - 39 EP - 46 PB - Gesellschaft für Umweltsimulation e.V. CY - Pfinztal (Berghausen) AN - OPUS4-57271 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Komann, Steffen A1 - Kiyak, Yusuf A1 - Wille, Frank A1 - Zerbst, Uwe A1 - Weber, Mike A1 - Klingbeil, Dietmar T1 - Assessment of ductile cast iron fracture mechanics analysis within licensing of German transport packages N2 - In recent years BAM was involved in several licensing procedures of new package designs for the transport of radioactive material, where the cask body was made of Ductile Cast Iron (DCI). According to IAEA regulations type B(U) packages must withstand the defined accident conditions of transport. For the cask material DCI, it is necessary to determine the brittle fracture behaviour. Due to the complex structure of the cask body and the dynamic loading a fracture mechanical assessment in an analytical way is not always possible. Numerical calculations are necessary to determine the fracture mechanical load in the component. At the first step a numerical analysis has to be done to identify the loading state at the cask body. Secondly an analysis of a detail of the cask body is made considering the boundary conditions of the global model. An artificial flaw is considered in this detailed model to calculate the fracture mechanical loading state. The size of the artificial flaw is characterized by the ultrasonic inspection used for the quality assurance of the package. The applicant developed additional analysis tools for calculation of stress intensity factor and/or J-Integral. The paper describes the authority assessment approach for the DCI fracture mechanics analysis. T2 - ASME 2012 Pressure vessels & piping division conference CY - Toronto, Ontario, Canada DA - 15.07.2012 PY - 2012 SP - PVP2012-78213, 1-7 PB - American Society of Mechanical Engineers CY - New York AN - OPUS4-26363 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geburtig, Anja A1 - Gorbushina, Anna A1 - Plarre, Rüdiger A1 - Stephan, Ina T1 - Umweltsimulation an der BAM – Grundlegende Ansätze mit Beispielen aus der natürlichen Umwelt N2 - Drei grundlegend verschiedene Ansätze für Umweltsimulation werden an Beispielen illustriert: (i) Ganzheitlicher Ansatz - Nachstellen von Umweltmilieus im Labor Ziel ist hier das Nachstellen von (kombinierten) Umweltbedingungen im Labor; die Umweltparameter werden mit all ihren Wechselwirkungen aufgebracht. Hauptnutzen ist eine gegenüber der natürlichen Beanspruchung erhöhte Reproduzierbarkeit der Umweltbedingungen. Hat man sein Laborsetup entwickelt, ist es auf verschiedene Materialien anwendbar. Unter solchen Laborbedingungen ermittelte Lebensdauern sind dabei nicht auf die typischerweise sehr variablen Real-Umweltbedingungen übertragbar. (ii) Parametrisierter Ansatz - Ermittlung einzelner Materialempfindlichkeiten Hierbei werden im Labor die Wirkungen separater Umweltparameter auf Materialien nachgestellt. Für eine solche Separation der Einflussfaktoren ist insbesondere die Aufschlüsselung möglicher Wechselwirkungen der Umwelt-parameter (z.B. Mikroklima an bestrahlten Oberflächen) erforderlich. Einzelne (meist Alterungs-) Empfindlichkeiten können qualitativ nachgewiesen werden oder sogar – als Beanspruchungs-Wirkungs-Funktionen – quantifiziert werden, was einen wesentlichen Schritt in Richtung der Digitalisierung der Material¬prüfung darstellt. Insbesondere ist dann auch eine Lebensdauer-vorhersage für vorgegebene Zeitreihen der Beanspruchungs¬parameter umsetzbar. (iii) Rückwirkungen auf die Umwelt Umweltbeanspruchungen können zur Freisetzung von Schadstoffen in die Umwelt führen. Durch die Nachstellung kritischer, aber realitätsnaher Einsatzszenarien kann die Menge an freigesetzten Substanzen abgeschätzt werden. Egal, welcher Ansatz verfolgt wird – ein Vergleich mit der oder einer Real-beanspruchung ist unerlässlich, ebenso wie die Messdatenaufzeichnung (data logging) aller potenziell relevanten Beanspruchungsparameter während dieser Realbeanspruchung. Obwohl die naturnahe Umwelt – sowohl in der BAM als auch bei der GUS – gegenüber der technischen Umwelt eher untergeordnet auftritt, werden zur Illustration Beispiele aus der naturnahen Umwelt verwendet. T2 - 50. Jahrestagung der GUS CY - Online meeting DA - 23.03.2022 KW - Umweltsimulation PY - 2022 SN - 978-3-9818507-7-2 SP - 79 EP - 89 AN - OPUS4-55015 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krankenhagen, Rainer A1 - Maierhofer, Christiane ED - Cardone, G. T1 - Determination of the spatial energy distribution generated by means of a flash lamp N2 - In order to carry out a quantitative analysis of thermographic data the heating energy and its spatial distribution have to be known. Especially in the case of flash lamp excitation the correct determination of these parameters is complicated due to very short excitation times combined with high power densities. The paper describes a procedure for the characterization of such lamps using a simple calorimetric sensor and a plane reference area. The presented results illustrate the performance and the suitability of the method in the field of thermography. T2 - QIRT 11 - 11th International conference on Quantitative InfraRed Thermography CY - Naples, Italy DA - 11.06.2012 KW - Thermography KW - Flash lamp KW - Heat pulse KW - Calorimetric sensor KW - Energy meter KW - Energy distribution PY - 2012 SP - 1 EP - 10(?) AN - OPUS4-26378 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kolkoori, Sanjeevareddy A1 - Rahman, Mehbub-Ur A1 - Prager, Jens T1 - 3D ray tracing model for ultrasound field evaluation in inhomogeneous anisotropic materials: model and experimental validation N2 - In this contribution a 3D ray tracing model for ultrasonic field evaluation in inhomogeneous anisotropic materials such as austenitic welds is presented. The inhomogenity of austenitic weld material is represented as several homogeneous layers. The general problem of energy reflection and transmission at the boundaries of the layers are solved resulting 3D amplitude and energy reflection and transmission coefficients. The directivity factor for the ray in general arbitrary oriented austenitic weld material (including lay back orientation) is determined based on Lamb's reciprocity theorem. The transducer excited ultrasonic fields are accurately evaluated by employing ray directivity factor, transmission coefficients, divergence of the ray bundle and density of rays. Finally, the comparison between theoretical and experimental results will be described. T2 - DAGA 2012 - 38. Jahrestagung für Akustik - Fortschritte der Akustik CY - Darmstadt, Germany DA - 19.03.2012 KW - Ultrasonic field KW - 3D ray tracing KW - Inhomogeneous KW - Austenitic weld PY - 2012 SP - 959 EP - 960 PB - Deutsche Gesellschaft für Akustik e.V. AN - OPUS4-26204 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hjelmar, O. A1 - Wahlström, M. A1 - Comans, R. A1 - Kalbe, Ute A1 - Grathwohl, P. A1 - Mehu, J. A1 - Schiopu, N. A1 - Hyks, J. A1 - Laine-Ylijoki, J. A1 - Van Zomeren, A. A1 - Krüger, Oliver A1 - Schoknecht, Ute A1 - Wendel, T. A1 - Abdelghafour, M. A1 - Borho, N. ED - Arm, M. ED - Vandecasteele, C. ED - Heynen, J. ED - Suer, P. ED - Lind, B. T1 - Robustness validation of two harmonized European leaching tests for assessment ot the leaching of construction products, including waste-based construction materials N2 - Two leaching tests, a tank leaching test (TS-2) and a percolation test (TS-3), developed by CEN/TC 351 for use in assessing environmental properties in relation to CE marking of construction products, are undergoing robustness validation as part of the standardisation procedure. This paper provides an overview of the activities included in the robustness validation programme. T2 - WASCON 2012 CY - Gothenburg, Sweden DA - 30.05.2012 KW - Tank leaching test KW - Percolation test KW - Robustness validation KW - Construction products PY - 2012 SP - 1 EP - 5 PB - ISCOWA and SGI AN - OPUS4-26966 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Trubiroha, P. A1 - Geburtig, Anja A1 - Wachtendorf, Volker T1 - 40 Years of Global-UV-Test weathering device: with fluorescent UV lamps and a precise microclimatical control into the future N2 - On the basis of a lot of investigation on the spectral sensitivity of photo degradation of plastics and on the underestimated influence of temperature and relative humidity on degradation processes a new type of weathering device was presented at the end of the seventies: It was a combination of a radiation source with fluorescent UV lamps and a precise climatic cabinet. The radiation emission from a combination of four different types of fluorescent UV lamps was superimposed on the specimen surfaces in the climatic cabinet to match the UV part of solar radiation as closely as possible. Air temperature was controlled to within ± 1 °C, and relative humidity to within ± 5 %RH. As the lamps’ emission is focussed on the UV range almost no radiation heating of the sample occurs. Therefore, the temperature of the sample, which is the quantity of consideration for the degradation, is nearly identical with the chamber’s air temperature, which is the quantity to be controlled. Also, therefore, high humidity can be obtained on the sample surface. The limitation of the emission to the UV range is sufficient for the study of the polymer matrix. This type of weathering device offers an exactness of microclimatic control of the sample’s surface, which should be a standard for weathering devices. Even now it is the only weathering device which generates pure relative humidity (without aerosol). T2 - 9th European Weathering Symposium CY - Basel, Switzerland DA - 18.09.2019 KW - Weathering KW - Irradiation PY - 2019 SN - 978-3-9818507-5-8 SP - 37 EP - 47 PB - Thomas Würtz Grafik-Design CY - Karlsruhe, Germany AN - OPUS4-49151 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geburtig, Anja A1 - Wachtendorf, Volker A1 - Trubiroha, P. T1 - Evaluation of outdoor exposures by means of exposure response functions N2 - Outdoor exposure tests are a common tool to evaluate the weathering resistance of a polymeric material or component. However, they have only a limited validity, mainly due to the limited reproducibility of the weather as well as of the bad adaptability to other exposure sites. Typically, an outdoor exposure is characterized by the measured radiant exposure; sometimes averaged temperature data are added. These can be – separately – related to long-term annual means, to get an idea on the severity of the exposure. However, as for polymeric ageing, irradiance and temperature act simultaneously, such severity of an outdoor exposure could be better described by a computed property change of a similar material, which is calculated from the hourly irradiance and temperature values on the base of established exposure response functions. In this way, various outdoor exposures are evaluated. For several exposure sites, annual deviations of the ageing amount are related to annual mean values, to evaluate the weathering reproducibility at the exposure site. Additionally, correlations to relevant weather parameters are illuminated. Also some specific exposure conditions, such as tilt angle, are tested. Compared to the use of weathering reference materials, this procedure unfavourably depends on the availability of a suited control as well as on the quality of the established exposure response function. In contrast, it enables a later exposure evaluation, on the base of documented weather data, if for instance no reference material was exposed. T2 - 8th European Weathering Symposium CY - Vienna, Austria DA - 20.09.2017 KW - Weathering KW - Service life prediction KW - Photodegradation PY - 2017 SN - 978-3-9818507-1-0 VL - 18 SP - 127 EP - 135 PB - Thomas Würtz Grafik Design CY - Karlsruhe AN - OPUS4-42126 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wachtendorf, Volker A1 - Geburtig, Anja T1 - Digitale Umweltsimulation am Beispiel der Photooxidation von Polymeren N2 - Die Umweltwirkungen auf ein Material werden als Überlapp der Funktionskurven von Materialempfindlichkeit und einwirkenden Umweltparametern betrachtet. Wenn entweder die Empfindlichkeit oder die Beanspruchungen Null sind, ergibt sich auch keine Umweltwirkung und bei beidseitig Werten größer Null das jeweilige Produkt der beiden. Die Akkumulation der nicht-reversiblen Effekte über die Zeit und allen Eigenschaftsänderungen entspricht der Alterung des Materials für den jeweiligen Expositionszeitraum. Die digitale Umweltsimulation gliedert sich hier in drei Teilaspekte. Ein erster, rein materialwissenschaftlicher Teil hat die Aufgabe, alle relevanten Materialempfindlichkeiten experimentell zu quantifizieren. Ein zweiter – unter Umständen numerischer Teil – hat die Aufgabe, das Bauteil und seine Einbaulage zu digitalisieren und aus den makroskopischen Umgebungsbedingungen die relevanten mikroklimatischen Umweltparameter für alle Oberflächen- oder Volumenelemente zu bestimmen. In einem dritten Teil werden die Einwirkungen über den betrachteten Zeitraum berechnet und kumuliert. Dieses Konzept, das auf den so genannten Expositions-Reaktions-Funktionen (ERF) basiert, wird an Beispielen der Photoxidation erläutert. Dieses Vorgehen wurde schon beim ViPQuali-Projekt als Numerische Umweltsimulation umgesetzt. Überprüft werden muss das Modell unbedingt an einer realitätsnahen Validierungsbeanspruchung. Hier werden die ermittelten ERFs mit über den kompletten Beanspruchungszeitraum geloggten Umweltparametern gekoppelt, um die berechnete mit der experimentell erfahrenen Alterungswirkung zu vergleichen. Nur so kann sichergestellt sein, dass alle für die Anwendungsumgebung relevanten Materialempfindlichkeiten einbezogen wurden. T2 - 52. Jahrestagung der GUS CY - Stutensee-Blankenloch, Germany DA - 26.03.2024 KW - UV KW - Polymer 3R KW - Bewitterung KW - Bestrahlung PY - 2024 SN - 978-3-9826129-0-4 SP - 31 EP - 40 PB - Gesellschaft für Umweltsimulation e.V. CY - Pfinztal (Berghausen) AN - OPUS4-59830 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wachtendorf, Volker A1 - Geburtig, Anja A1 - Schulz, Ulrich A1 - Trubiroha, Peter T1 - „Test Tailoring“ eines künstlichen Bewitterungstests am Beispiel der Entwicklung des „Acid Dew and Fog“ Testes N2 - Häufig ist es wünschenswert, für neue Materialien oder Anwendungen künstliche Bewitterungsverfahren zu benutzen, die auf die spezifischen Anforderungen besser zugeschnitten sind, als es bei bestehenden standardisierten Verfahren der Fall ist. Nachdem man die spezifischen Parameter der Beanspruchung unter Anwendungsbedingungen und die spezifische Empfindlichkeit des Materials erfasst hat, beginnt ein Prozess, der als „Test Tailoring“ häufig abstrakt verwendet, auf den aber nur selten näher eingegangen wird. Genau dieser Prozess soll hier am Beispiel der Entwicklung eines künstlichen Bewitterungstests unter saurer Beaufschlagung, dem in der BAM entwickelten Acid Dew and Fog Test, beispielhaft erläutert werden. T2 - 47. Jahrestagung der GUS 2018, Umwelteinflüsse erfassen, simulieren, bewerten CY - Pfinztal (Berghausen), Germany DA - 21.03.2018 KW - Test Tailoring KW - Bewitterung KW - Acid Dew and Fog KW - Umweltsimulation PY - 2018 VL - 47 SP - Vortrag V4, 45 EP - 54 PB - Gesellschaft für Umweltsimulation e.V. CY - Pfinztal AN - OPUS4-45412 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz, Ulrich A1 - Stephan, Ina A1 - Wachtendorf, Volker A1 - Geburtig, Anja A1 - Slomko, R. A1 - Petzold, I. T1 - Mildew-caused Damage on Automotive Coatings T2 - European Coatings Conference "Novel Biocide Technology II" CY - Berlin, Germany DA - 2005-02-24 KW - Mildew KW - Fungi KW - Mould KW - Weathering KW - Coating KW - Pinholes KW - Damage PY - 2005 SP - 17 pages PB - Vincentz CY - Hannover AN - OPUS4-11223 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geburtig, Anja A1 - Wachtendorf, Volker A1 - Trubiroha, P. ED - Ziegahn, K.-F. T1 - Quantitative Auswertemöglichkeiten bei der spektralen Bestrahlung – Berechnung des Wirkungsspektrums N2 - Für die Bewertung des Wellenlängeneinflusses auf die Alterungsvorgänge bei der Bestrahlung UV- oder lichtempfindlicher Materialien kann die Methode der spektralen Bestrahlung angewendet werden. Im Prinzip wird dabei das linear dispergierte Spektrum einer Strahlenquelle mit kontinuierlichem Spektrum (z.B. Xe-Lampe) auf eine Probenoberfläche abgebildet, so dass Ort einer Materialänderung und Wellenlänge der Bestrahlung einander zugeordnet werden können. Nachfolgende lokal-auflösende Analysemethoden ermitteln eine Eigenschaftsänderung an einem spezifischen Ort der Probe, aus dem sich dann die Bestrahlungswellenlänge ergibt. Der verwendete Aufbau wird beschrieben. Es wird an einem ausgewählten Beispiel gezeigt, wie durch geeignete Anbindung eines Messsystems zur Bestimmung der spektralen Bestrahlungsstärke und ortsaufgelöste Messungen der Eigenschaftsänderungen eine quantitative Auswertung realisiert werden kann. Der Einfluss nichtlinearer Alterungsverläufe wird diskutiert. Grenzen der Methode werden aufgezeigt und Erweiterungsmöglichkeiten dargestellt. T2 - 46. Jahrestagung der GUS CY - Stutensee-Blankenloch, Germany DA - 22.03.2017 KW - UV-Bestrahlung PY - 2017 SN - 978-3-9816286-9-2 SP - V 8, 91 EP - 99 AN - OPUS4-42578 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Völzke, Holger A1 - Wolff, Dietmar A1 - Barnabas, I. A1 - Ordogh, M. A1 - Shirai, K. A1 - Saegusa, T. A1 - Cho, C.-H. A1 - Kook, D. A1 - Lopez, J. F. A1 - Conde, J. M. A1 - Alejano, C. A1 - Lloret, M. A1 - Quecedo, M. A1 - Shea, J. A1 - Ross, P. J. A1 - White, N. A1 - Rossiter, G. A1 - Hodgson, Z. A1 - Sorenson, K. A1 - McConnell, P. A1 - Hanson, B. ED - Sorenson, K. ED - Shirai, K. ED - Völzke, Holger T1 - Extended storage collaboration program - International subcommittee report - International perspectives on technical data gaps associated with extended storage and transportation of used nuclear fuel N2 - The US Electric Power Research Institute (EPRI) chartered a volunteer committee in November 2009 to share information and data related to extended storage and subsequent transportation of used nuclear fuel. This committee is named the Extended Storage Collaboration Program (ESCP) and was initially comprised of representatives from industry (fuel and cask vendors, utilities, the Nuclear Energy Institute, and EPRI), as well as government (e.g., US Department of Energy) and the US Nuclear Regulatory Commission. The primary motivation for establishing this committee was the recognition that used fuel will need to be stored past the regulatory licensing timeframe. In the US, this is mainly a result of the cessation of licensing activities for the planned Yucca Mountain repository. Recognizing that there is a global interest in extended storage and transportation, the International Subcommittee was established in December 2010 to extend the reach of ESCP internationally in order to fully address extended storage and transportation issues, as they apply to different systems, national policies, and regulations around the world. This Subcommittee serves to deepen the overall understanding of degradation mechanisms associated with storage and transportation systems, expand the access to data and programs related to extended storage and transportation, and strengthen the overall technical basis for programmatic decisions. The International Subcommittee established three basic objectives: 1. Conduct a technical data gap survey 2. Assess opportunities to leverage specific research to benefit the larger international group 3. Integrate our work with relevant International Atomic Energy Agency (IAEA) committee work This report constitutes completion of Objective #1. The International Subcommittee worked to identify and prioritize technical gaps that need to be addressed to support licensing activities within their own countries. Because there are varying types of storage and transportation system designs, national policies and regulations, there are identified commonalities as well as differences that stress the importance of this work on an international scale. Section 5 of this report identifies and prioritizes all of the identified data gaps for each participating organization. However, important data gaps were identified that had a consensus of opinion of being a high priority. These technical gaps, as a function of storage system component are: 1. Fuel – hydride effects on fuel cladding and retrievability of fuel after storage 2. Canister – general canister corrosion and stress corrosion cracking of canister closure welds, particularly in marine environments 3. Closure – degradation of bolts and seals (metallic and organic) 4. Overpack – concrete degradation Dry storage systems were originally designed for limited periods. With extended dry storage, it is generally believed that used fuel can be stored safely and securely past the regulatory time period. However, the technical arguments need to be made to justify extended licensing periods. Addressing the data gaps will provide the necessary arguments to justify license extensions. In the development of this report, the International Subcommittee met five times over a period of 18 months to work through the issues of identifying and prioritizing the data gaps, and discussing of technical issues as they pertain to the safety of used fuel storage and transportation. The meeting locations and dates were: 1. Vienna June 2010 2. London October 2010 3. Charlotte December 2010 4. Berlin June 2011 5. Charlotte December 2011 This report is not meant to be a technical document. Rather, it is an overview of country regulatory policy, a review of in-country operational status and used fuel inventory, followed by a role-up of identification and prioritization of technical data gaps. Technical documents that were used in the data gap assessments are referenced. It is important to note that this document represents only the opinions of the contributors. This document in no way represents any official country position. The organizations providing support to the writing of this report are: Germany: - Bundesanstalt für Materialforschung und -prüfung Hungary: - Radioaktiv Julladekokat Kezelo Kozhasznu - Som System Kft. Japan: - Central Research Institute of Electric Power Industry South Korea: - Korea Atomic Energy Research Institute - Korea Radioactive Waste Management Corporation Spain: - Consejo de Seguridad Nuclear - ENRESA Empresa Nacional de Residuos Radiactivos - ENUSA Industrias Avanzadas United Kingdom: - EDF Energy - National Nuclear Laboratory Ltd. United States: - Pacific Northwest National Laboratory - Sandia National Laboratories KW - Used/spent fuel dry storage KW - Used/spent fuel transportation KW - Extended used/spent nuclear fuel storage KW - High burnup spent fuel storage and transportation KW - Spent fuel storage and transportation KW - Extended Storage Collaboration Program (ESCP) KW - ESCP International Subcommittee PY - 2012 UR - https://www.epri.com/research/products/1026481 N1 - This final report was prepared as part of the volunteer Extended Storage Collaboration Program (ESCP). VL - 1026481 SP - 1 EP - 132 PB - Electric Power Research Institute (EPRI) CY - Palo Alto, CA, USA AN - OPUS4-27405 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Trubiroha, P. A1 - Geburtig, Anja A1 - Wachtendorf, Volker T1 - Natural versus artificial weathering of polymers – main differences in climatic conditions N2 - Different climatic conditions and weather variables during natural and artificial exposure of polymers may be reasons for an unsatisfying correlation between the ageing results. Here the main differences are discussed for: - Global solar radiation In weathering devices there is a constant spectral irradiance which is 5 times higher than the averaged spectral irradiance outdoors, which is strongly varying in its diurnal course. Intensified weathering using Fresnel reflectors concentrates only the direct solar radiation with a relatively low UV proportion. Problems of reciprocity may arise from the different mean of irradiance levels. - Temperatures at specimen surfaces. Because of the high irradiance levels mentioned above, artificial exposures may lead to high surface temperatures and large temperature differences between differently coloured specimen surfaces, if the artificial radiation source emits much VIS- and IR-radiation. Outdoors the surface temperature and temperature differences of exposed specimens are influenced by considerably lower irradiance levels and additionally by an effective radiation loss in the night. - Relative humidity at specimen surfaces In weathering devices the relative humidity at specimen surfaces is very low if it is uncontrolled. If controlled by ultrasonic humidifiers or spray nozzles, the additional exposure to water droplets is quite likely. - Wetness on specimen surfaces All usual spray programs prescribed in weathering standards recommend frequently changing of short spray/dry periods and result in total times of wetness (TOW) of the exposed specimen surfaces which is only about 30 % of the outdoor TOW. - Acidic precipitation and bio films Acidic precipitation and bio films are usual outdoor conditions which are only considered in special weathering tests. T2 - 8th European Weathering Symposium CY - Vienna, Austria DA - 20.09.2017 KW - Artificial weathering KW - Natural weathering KW - Weathering parameters PY - 2017 SN - 978-3-9818507-1-0 VL - 18 SP - 63 EP - 75 CY - Karlsruhe AN - OPUS4-42127 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Köppen, Robert A1 - Becker, Roland A1 - Emmerling, Franziska A1 - Jung, Christian A1 - Nehls, Irene T1 - HBCD enantiomers: absolute configurations and thermal rearrangement T2 - Organohalogen Compounds PY - 2006 UR - http://www.dioxin20xx.org/pdfs/2006/06-466.pdf VL - 68 SP - 1991 EP - 1994 PB - Norwegian Institute of Public Health AN - OPUS4-14540 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Küttenbaum, S. A1 - Braml, T. A1 - Kainz, C. A1 - Maack, Stefan A1 - Taffe, A. T1 - Guidance on inspection-supported reliability assessment of existing bridges in Germany N2 - This contribution is intended to disseminate the contents of a national recommendation for Action draft for the inspection-based reliability analysis of existing bridges. The focus is on the utilization of non-destructive testing methods for verifications in both the ultimate and the serviceability Limit states. First, the contents of the developed recommendation for action are outlined. The Guideline covers the process from the purposeful definition of inspection strategies via the quality assessment of measured information to the partial factor-based assessment under consideration of qualityevaluated on-site inspection results. Secondly, the concept of the drafted recommendation for action is demonstrated using a prestressed concrete bridge as a case study. T2 - IABSE Symposium Tokyo 2025 CY - Tokyo, Nippon DA - 18.05.2025 KW - Life management KW - Brücken KW - Non-destructive testing KW - Civil engineering KW - State-of-the-art PY - 2025 DO - https://doi.org/10.1080/10168664.2024.2363597 VL - 34 IS - 3 SP - 1 EP - 8 AN - OPUS4-65630 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Prinz, Carsten A1 - Zimathies, Annett A1 - Emmerling, Franziska T1 - Experimental raw data sets associated with certified reference material BAM-P115 (titanium dioxide) for comparison of nitrogen and argon sorption, available in the universal adsorption information format (AIF) N2 - These data sets serve as models for calculating the specific surface area (BET method) using gas sorption in accordance with ISO 9277. The present measurements were carried out with nitrogen at 77 Kelvin and argon at 87 Kelvin. It is recommended to use the following requirements for the molecular cross-sectional area: Nitrogen: 0.1620 nm² Argon: 0.1420 nm² Expected specific surface area for nitrogen (BET): 140 to 154 m²/g Expected specific surface area for argon (BET): 129 to 135 m²/g Titanium dioxides certified with nitrogen sorption and additionally measured with argon for research purposes were used as sample material. The resulting data sets are intended to serve as comparative data for own measurements and show the differences in sorption behaviour and evaluations between nitrogen and argon. These data are stored in the universal AIF format (adsorption information format), which allows flexible use of the data. KW - Physisorption KW - Specific surface area KW - AIF KW - Argon KW - Nitrogen PY - 2024 DO - https://doi.org/10.5281/zenodo.13269756 PB - Zenodo CY - Geneva AN - OPUS4-60783 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mrkwitschka, Paul A1 - Hodoroaba, Vasile-Dan A1 - Radnik, Jörg T1 - XPS/HAXPES and EDS spectra with ROI N2 - XPS/HAXPES spectra as well as EDS spectra and SEM micrographs with regions of interest. Measurement scheme included as a powerpoint presentation. Investigated materials: Ionic liquid and commercial and lab-synthesized graphene oxide. KW - EDX KW - XPS KW - Graphene Oxide KW - Ionic Liquid PY - 2026 DO - https://doi.org/10.5281/zenodo.18231732 PB - Zenodo CY - Geneva AN - OPUS4-65624 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Pauw, Brian Richard A1 - Smales, Glen Jacob A1 - Anker, A. S. A1 - Balazs, D. M. A1 - Beyer, F. L. A1 - Bienert, Ralf A1 - Bouwman, W. G. A1 - Breßler, Ingo A1 - Breternitz, J. A1 - Brok, E. S. A1 - Bryant, G. A1 - Clulow, A. J. A1 - Crater, E. R. A1 - De Geuser, F. A1 - Giudice, A. D. A1 - Deumer, J. A1 - Disch, S. A1 - Dutt, S. A1 - Frank, K. A1 - Fratini, E. A1 - Gilbert, E. P. A1 - Hahn, Marc Benjamin A1 - Hallett, J. A1 - Hohenschutz, Max A1 - Hollamby, M. J. A1 - Huband, S. A1 - Ilavsky, J. A1 - Jochum, J. K. A1 - Juelsholt, M. A1 - Mansel, B. W. A1 - Penttilä, P. A1 - Pittkowski, R. K. A1 - Portale, G. A1 - Pozzo, L. D. A1 - Ricardo de Abreu Furtado Garcia, P. A1 - Rochels, L. A1 - Rosalie, Julian A1 - Saloga, P. E. J. A1 - Seibt, S. A1 - Smith, A. J. A1 - Smith, G. N. A1 - Annadurai, V. A1 - Spiering, G. A. A1 - Stawski, Tomasz A1 - Taché, O. A1 - Thünemann, Andreas A1 - Toth, K. A1 - Whitten, A. E. A1 - Wuttke, J. T1 - The human factor - Results of a small-angle scattering data analysis round robin N2 - A Round Robin study has been carried out to estimate the impact of the human element in small-angle scattering data analysis. Four corrected datasets were provided to participants ready for analysis. All datasets were measured on samples containing spherical scatterers, with two datasets in dilute dispersions, and two from powders. Most of the 46 participants correctly identified the number of populations in the dilute dispersions, with half of the population mean entries within 1.5 % and half of the population width entries within 40 %, respectively. Due to the added complexity of the structure factor, much fewer people submitted answers on the powder datasets. For those that did, half of the entries for the means and widths were within 44 % and 86 % respectively. This Round Robin experiment highlights several causes for the discrepancies, for which solutions are proposed. KW - Round robin KW - Sall-angle scattering KW - Nanostructure quantification KW - Nanostructure KW - SAXS KW - MOUSE KW - X-ray scattering KW - Size distribution KW - Nanoparticles PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-571342 DO - https://doi.org/10.48550/arXiv.2303.03772 SP - 1 EP - 23 PB - Cornell University CY - Ithaca, NY AN - OPUS4-57134 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Wolf, Jako A1 - Stawski, Tomasz A1 - Smales, Glen Jacob A1 - Thünemann, Andreas A1 - Emmerling, Franziska T1 - SI Files for "Towards automation of the polyol process for the synthesis of silver nanoparticles" N2 - The graphml file: reaction_graph_AgNP.graphml is included. It contains topological information (Fig. 1 in the main text) about the reaction setup and metadata with reaction condtions. It used by the Python API used to control the Chemputer. SAXS reports. The complete report sheets generated by McSAS are included. They contain extended information characterising the size distributions and the fitting parameters. NP3_I: saxs_report_NP3_I.pdf NP3_II: saxs_report_NP3_II.pdf NP3_III: saxs_report_NP3_III.pdf NP3_IV: saxs_report_NP3_IV.pdf NP5_I: saxs_report_NP5_I.pdf NP5_II: saxs_report_NP5_II.pdf NP5_III: saxs_report_NP5_III.pdf KW - Automated synthesis KW - Silver KW - Nanoparticles PY - 2022 DO - https://doi.org/10.5281/zenodo.5910614 PB - Zenodo CY - Geneva AN - OPUS4-55197 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Smales, Glen Jacob A1 - Pauw, Brian Richard T1 - DACHS/MOFs/AutoMOFs_5/Synthesis N2 - The DACHS (Database for Automation, Characterization and Holistic Synthesis) project aims to create completely traceable experimental data, covering syntheses, measurements, analyses, and interpretations. DACHS_MOFs focuses on the synthesis and characterisation of metal-organic frameworks, across multiple, automation-assisted experimental series (AutoMOFs), with the overall goal of producing reproducible MOF samples through tracking of the synthesis parameters. DACHS_MOFs is simultaneously used to test the DACHS principles. This upload contain synthesis data from AutoMOFs_5 in HDF5 format (.h5). Each .h5 file contains detailed information on the chemical, experimenal, and synthesis parameters used during the synthesis of a single AutoMOF sample. KW - Automation KW - Procedure KW - Synthesis KW - Traceability PY - 2024 DO - https://doi.org/10.5281/zenodo.11237987 PB - Zenodo CY - Geneva AN - OPUS4-61344 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pauw, Brian Richard A1 - Smales, Glen Jacob A1 - Moeez, A. A1 - Hörmann, Anja A1 - Breßler, Ingo T1 - Example configurations and test cases for the Python HDF5Translator framework. N2 - This is a set of use examples for the HDF5Translator framework. This framework lets you translate measurement files into a different (e.g. NeXus-compatible) structure, with some optional checks and conversions on the way. For an in-depth look at what it does, there is a blog post here. The use examples provided herein are each accompanied by the measurement data necessary to test and replicate the conversion. The README.md files in each example show the steps necessary to do the conversion for each. We encourage those who have used or adapted one or more of these exampes to create their own conversion, to get in touch with us so we may add your example to the set. KW - Measurement data conversion KW - Data conversion KW - HDF5 KW - NeXus KW - NXsas KW - Framework KW - Python PY - 2024 DO - https://doi.org/10.5281/zenodo.10925971 PB - Zenodo CY - Geneva AN - OPUS4-59796 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Prinz, Carsten A1 - Zimathies, Annett A1 - Emmerling, Franziska T1 - Experimantal raw data sets associated with certified reference material BAM-P116 (titanium dioxide) for comparison of nitrogen and argon sorption, available in the universal adsorption information format (AIF) N2 - These data sets serve as models for calculating the specific surface area (BET method) using gas sorption in accordance with ISO 9277. The present measurements were carried out with nitrogen at 77 Kelvin and argon at 87 Kelvin. It is recommended to use the following requirements for the molecular cross-sectional area: Nitrogen: 0.1620 nm² Argon: 0.1420 nm² Titanium dioxides certified with nitrogen sorption and additionally measured with argon for research purposes were used as sample material. The resulting data sets are intended to serve as comparative data for own measurements and show the differences in sorption behaviour and evaluations between nitrogen and argon. These data are stored in the universal AIF format (adsorption information file), which allows flexible use of the data. KW - Physisorption KW - Surface area KW - AIF KW - Argon KW - Nitrogen PY - 2023 DO - https://doi.org/10.5281/zenodo.10199628 PB - Zenodo CY - Geneva AN - OPUS4-59102 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bauer, J. A1 - Miclea, P.-T. A1 - Braun, U. A1 - Altmann, Korinna A1 - Turek, M. A1 - Hagendorf, C. T1 - Microplastic detection and analysis in water samples N2 - Microplastic detection in water samples becomes important for tracing microplastic sources. Microplastic may harm desalination facilities by blocking filters and disturbing the marine food chain. Thermo analytical methods such as pyrolysis gas chromatography mass spectroscopy, and spectroscopic methods like (micro) Raman spectroscopy or (micro) Fouriertransform infrared spectroscopy in combination with appropriate filters and sample preparation are suitable for analyzing microplastics on a scale from 1 µm to 1000 µm fast and unambiguous. While the thermo analytical methods are suitable for larger sample volumes, Raman spectroscopy and Fouriertransform infrared spectroscopy are able to detect and analyze single microplastic particles for instance in bottled water. Machine learning algorithms ensure a reliable classification of different plastic materials. T2 - International Conference on Sustainable Energy-Water-Environment Nexus in Desert Climate 2019 CY - Ar-Rayyan, Qatar DA - 02.12.2019 KW - Microplastics KW - Water samples PY - 2022 SP - 111 EP - 113 PB - Springer AN - OPUS4-56240 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dittmann, Daniel A1 - Saal, L. A1 - Zietzschmann, F. A1 - Mai, M. A1 - Altmann, Korinna A1 - Al-Sabbagh, Dominik A1 - Ruhl, A. S. A1 - Jekel, M. A1 - Braun, U. T1 - Aktivkohlecharakterisierung als weiterer Schlüssel für Adsorptionsprognosen organischer Spurenstoffe in der vierten Reinigungsstufe N2 - In diesem Beitrag wird der Einfluss des Aktivkohleprodukts auf die Adsorption von Spurenstoffen aus Kläranlagenablauf gezeigt und diskutiert. Im zweiten Teil wird das Material Aktivkohle analytisch charakterisiert und die Eigenschaften systematisiert. Die gewonnenen Erkenntnisse werden mit Bezug zu Praxislösungen zusammengefasst. T2 - Wasser 2021 CY - Online meeting DA - 10.05.2021 KW - Aktivkohle KW - Thermogravimetrie KW - Zersetzungsgasanalyse KW - Proximatanalyse PY - 2021 SP - 373 EP - 378 AN - OPUS4-52740 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Stawski, Tomasz A1 - Smales, Glen Jacob A1 - Scoppola, E. A1 - Jha, D. A1 - Morales, L. F. G. A1 - Moya, A. A1 - Wirth, R. A1 - Pauw, Brian Richard A1 - Emmerling, Franziska A1 - Van Driessche, A. E. S. T1 - Supplementary data set for "Seeds of imperfection rule the mesocrystalline disorder in natural anhydrite single crystals" N2 - In recent years, we have come to appreciate the astounding intricacy of the formation process of minerals from ions in aqueous solutions. In this context, a number of studies have revealed that nucleation in the calcium sulfate system is non-classical, involving the aggregation and reorganization of nanosized prenucleation particles. In a recent work we have shown that this particle-mediated nucleation pathway is actually imprinted in the resultant single micron-sized CaSO4 crystals. This property of CaSO4 minerals provides us with an unique opportunity to search for evidence of non-classical nucleation pathways in geological environments. In particular, we focused on the quintessential single crystals of anhydrite extracted from the Naica mine in Mexico. We elucidated the growth history from this mineral sample by mapping growth defects at different length scales. Based on these data we argue that the nano-scale misalignment of the structural sub-units observed in the initial calcium sulfate crystal seed propagate through different length-scales both in morphological, as well as strictly crystallographic aspects, eventually causing the formation of large mesostructured single crystals of anhydrite. Hence, the nanoparticle mediated nucleation mechanism introduces a 'seed of imperfection', which leads to a macroscopic single crystal, in which its fragments do not fit together at different length-scales in a self-similar manner. Consequently, anisotropic voids of various sizes are formed with very well-defined walls/edges. But, at the same time the material retains its essential single crystal nature. These findings shed new light on the longstanding concept of crystal structure. KW - Calcium sulfate KW - Mesocrystal KW - Anhydrite PY - 2021 DO - https://doi.org/10.5281/zenodo.4943234 PB - Zenodo CY - Geneva AN - OPUS4-53765 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geburtig, Anja A1 - Wachtendorf, Volker A1 - Trubiroha, Peter T1 - Accelerated weathering test for plastics and coatings that are exposed to acidic precipitation T2 - 7th International Symposium on Weatherability (Proceedings ) CY - Yokohama, Japan DA - 2008-10-23 KW - Acid rain KW - ADF KW - Acid dew and fog test KW - Artificial weathering test PY - 2008 SP - 49 EP - 54 CY - Yokohama AN - OPUS4-21116 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geburtig, Anja T1 - UV radiation and light as impact factors N2 - Radiation in the spectral ranges of UV and VIS are environmental impact factors that can cause ageing of many materials or products. The reason for this is that especially organic materials, such as food or many pharmaceutical, are subject to photochemical degradation. Of course, suited transparent packaging material may give protection against such impact for radiation sensitive fillings. But for this, it is necessary to know about the spectral range of the fillings sensitivity as well as about the radiation impact of the radiation sources that are relevant during the life time of the product. The spectral irradiance for characterizing the emission of various radiation sources is easily measured by means of a spectroradiometer. The spectral sensitivity of a filling's property can be determined by spectrally dispersed irradiation, where the positions on a sample are related to the different wavelengths. Thus, the damaging effect of the different wavelengths can be directly evaluated. A lateral measurement of the relevant property change shows the activation spectrum, which is the product of the spectral radiant exposure and the spectral sensitivity. By measuring the spectral irradiance for each sample position, the spectral sensitivity of the ageing property can be calculated. Comparing the fillings spectral sensitivity and the spectral irradiance of a potential radiation source during later transport and storage, conclusions can be drawn about necessary spectral absorption of a (partly) transparent packaging to give sufficient protection. The setup for such investigation will be shown and several illustrating samples from daily food experience will be given. T2 - 20th IAPRI World Conference on Packaging CY - Campinas, Brazil DA - 12.06.2016 KW - UV radiation KW - Light KW - Spectral sensitivity KW - Spectral irradiance KW - Spectral absorption PY - 2016 SN - 978-85-7029-136-3 SP - 136 EP - 139 AN - OPUS4-36913 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Trubiroha, Peter A1 - Geburtig, Anja A1 - Wachtendorf, Volker T1 - Grundsätzliches zur witterungsbedingten Alterung von Polymerwerkstoffen T2 - SKZ-Fachtagung "Bewitterung von Kunststoffen und Lacken in der Automobilindustrie" CY - Würzburg, Deutschland DA - 2005-02-16 KW - Witterung KW - Alterung KW - Klima KW - Vorgeschichte KW - Prüfverfahren KW - Prüfgeräte PY - 2005 SP - 36 Seiten PB - SKZ CY - Würzburg AN - OPUS4-7099 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wachtendorf, Volker A1 - Geburtig, Anja A1 - Trubiroha, P. ED - Ziegahn, K.-F. T1 - Messung der effektiven UV-Bestrahlung bei der Bewitterung von Polymeren N2 - Bei der Bestrahlung und Bewitterung von polymeren Werkstoffen wird die Degradation durch eine Absorption von Strahlung initiiert und meistens durch weitere Klimagrößen, wie z.B. Wärme, Feuchte und atmosphärische Gase beeinflusst. Die Messung einer effektiven Bestrahlungsstärke und ihre zeitliche Integration sind deshalb von großer Bedeutung und zwar sowohl für die Kontrolle der Funktion des Bewitterungs- oder Bestrahlungsgerätes als auch als zusätzliche Angabe der wirkenden Beanspruchung. Photochemische Prozesse werden beim Sehen oder allgemeiner bei Farbstoffen schon durch sichtbare (VIS) Strahlung, dagegen bei der Erythembildung der Haut und der Photodegradation von Polymeren erst durch die energiereicheren Photonen der ultravioletten (UV) Strahlung initiiert. Die spektrale Empfindlichkeit des Auges und die Erythembildung sind im VIS- bzw. UV-Bereich sehr stark wellenlängenabhängig, was durch die Angabe der mit der spektralen Hellempfindlichkeit V(λ) des Auges bewerteten VIS-Strahlung in Lux (lx) bzw. die mit der Erythem-Wirkfunktion Serythem bewertete UV Strahlung als dimensionsloser UV-Index berücksichtigt wird. Spektrale Empfindlichkeiten. Die Photodegradation von Polymeren ist im UV-Bereich ebenfalls stark wellenlängenabhängig, was bisher bei der radiometrischen UV-Messung nicht berücksichtigt wurde. Seit Mitte der 70er Jahre, als die lx- bzw lxh- Messung bei der Strahlungsbeanspruchung langsam durch die Ermittlung der radiometrischen UV-Bestrahlungsstärke bzw. der UV-Bestrahlung im gesamten UV-Bereich abgelöst wurde, gab es hier bei der Bewitterungsprüfung keine weiteren Fortschritte auf dem Gebiet der Charakterisierung der Strahlungsbeanspruchung im UV-Bereich. Seit Jahren liegen zahlreiche Ergebnisse über die spektrale Empfindlichkeit von Photo-degradationsprozessen vor, die zeigen, dass die spektrale Empfindlichkeit im Bereich der Globalstrahlung an der kurzwelligen Grenze bei ca. 300 nm, am größten ist und im langwelligen UV-Bereich bei ca. 400 nm gegen Null geht. Die Messungen der radiometrischen Größen UV-Gesamtbestrahlungsstärke und UV-Gesamtbestrahlung erfasst deshalb über weite Wellenlängenbereiche Strahlungsanteile, die für die Photodegradation bedeutungslos sind und mittelt über potenziell bedeutsame Änderungen im kurzwelligen UV-Bereich hinweg. Es wird das Konzept eines neuen UV-Radiometers vorgestellt, dessen spektrale Empfindlichkeit einer mittleren spektralen Empfindlichkeit der Photodegradation von Polymeren entspricht. Die effektive UV-Bestrahlungsstärke und UV-Bestrahlung kann dadurch wesentlich genauer erfasst werden. T2 - 48. Jahrestagung der GUS 2019 CY - Stutensee, Germany DA - 27.03.2019 KW - UV-Bestrahlungsstärke PY - 2019 SN - 978-3-9818507-3-4 SP - 89 EP - 100 AN - OPUS4-47896 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geburtig, Anja T1 - Possibilities on prediction of plastic’s fragmentation time - Digital twins for decomposing-time predictions N2 - Depending on the specific plastic’s ageing sensitivities, the durations which plastic components remain in the environment can be very long. As, in the past, the advantages in ageing resistance and durability were highly evaluated, we now face the problem of quite stable plastic waste within the environment. However, there is only little knowledge on the real timescales until macroscopic fragmentation for the different kinds of plastic under various environmental conditions. Here, weathering methods are presented, which have been used for the failure prediction in specific outdoor conditions. Issues of uncertainty, reproducibility, or validation are discussed. For the prediction of the plastic’s fragmentation, much longer time scales have to be considered. To do this within a limited project life span, various processes as well as their acceleration potential have to be evaluated separately, such as temperature increase or spectral shift. The possibilities and limitations of such controlled acceleration will be discussed. T2 - 29th IAPRI Symposium on Packaging CY - Twente, Enschede, The Netherland DA - 11.06.2019 KW - Digital twin KW - Plastic KW - Ageing KW - Environment KW - Fragmentation PY - 2019 SN - 978-90365-4731-4 SP - 630 EP - 631 PB - University of Twente CY - Twente, Enschede, The Netherlands AN - OPUS4-48238 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wöhlecke, Andreas T1 - Aktuelles aus dem BAM-Fachbeirat N2 - Die Anforderungen an Geokunststoffprodukte und deren Qualitätssicherung unterliegen einem stetigen Wandel, der sowohl durch technische Veränderungen als auch durch normative und organisatorische Entwicklungen geprägt ist. Insbesondere der Fachbeirat der BAM gemäß Deponieverordnung (DepV) spielt hier im Bereich der Deponietechnik eine wichtige Rolle. An dieser Stelle sollen aktuelle Themen aus dem Fachbeirat der BAM vorgestellt werden, die wesentliche Änderungen in der Zulassungs- und Anwendungspraxis betreffen. Der Beitrag beleuchtet unter anderem Veränderungen innerhalb der BAM, die Modernisierung der Publikationsformate sowie die fachliche Weiterentwicklung der Zulassungsrichtlinien. T2 - 22. Leipziger Deponiefachtagung CY - Leipzig, Germany DA - 10.03.2026 KW - Deponie KW - Geotextil KW - Abdichtungssystem PY - 2026 SN - 978-3-00-085899-4 VL - 22 SP - 15 EP - 22 PB - HWTK Leipzig CY - Leipzig AN - OPUS4-65664 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Averin, Anton A1 - Hirsch, Philipp Daniel A1 - Lecompagnon, Julien T1 - Thermographic Reference Dataset: Defect Detection in Nuclear Waste Barrel Cutouts Using Long Pulse Thermography N2 - We introduce a thermographic dataset for subsurface defect detection in radioactive waste storage drums, comprising thermal sequences from 7 barrel specimens with artificially manufactured internal defects. The dataset was acquired using cost-effective halogen-lamp excitation (2kW per lamp) as an alternative to laser-based systems, with dual-camera thermal imaging (CMOS and bolometric) to enable performance comparison across imaging modalities. The specimens include both new and aged barrel types with controlled defects — FBHs, lines, crosses, triangles, and rectangles — simulating internal corrosion at varying scales (4mm to 60mm). Three heating regimes (both lamps, left only, right only) were systematically applied across multiple measurement regions per sample, yielding normalized thermal sequences. To lower the barrier for machine learning practitioners without thermography expertise, the dataset provides pre-computed features derived from principal component analysis, pulse phase thermography, and independent component analysis extracted using experimentally optimized time windows. Ground-truth binary masks mapping defect locations are included to enable supervised learning. This resource is designed to support the development and benchmarking of automated defect detection algorithms for non-destructive testing of curved, thin-walled metallic structures under realistic surface conditions (paint inhomogeneity, dirt, geometric artifacts), while validating low-cost thermographic inspection alternatives for industrial deployment. KW - Nondestructive Testing KW - Corrosion detection KW - Waste storage KW - Thermography KW - Safety PY - 2026 DO - https://doi.org/10.5281/zenodo.18916290 PB - Zenodo CY - Geneva AN - OPUS4-65666 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stelzner, Ludwig A1 - Kobe, André A1 - Pittrich, Tim T1 - Konstruktiver Brandschutz: Abplatzverhalten von Beton, Innovativer Versuchsaufbau und klinkereffiziente Zemente N2 - Bauteile aus Beton besitzen in der Regel ohne zusätzliche Schutzmaßnahmen aufgrund ihrer großen Masse, der Nichtbrennbarkeit des Baustoffs sowie der geringen Wärmeleitfähigkeit einen hohen Feuerwiderstand. Jedoch kann der Querschnitt durch Abplatzungen im Brandfall reduziert und die Bewehrung freigelegt werden. Dies kann zum frühzeitigen Verlust der Standsicherheit und in der Folge insbesondere bei Infrastrukturbauwerken zu massiven ökonomischen Folgeschäden führen. Der Beitrag präsentiert aktuelle Forschungsarbeiten der BAM zur Analyse des Abplatzverhaltens von Beton. Auf Basis experimenteller Untersuchungen zum Einfluss der Prüfkörpergröße auf das Abplatzverhalten wird eine weiterentwickelte Prüfmethodik vorgestellt. Diese ermöglicht es, die Abplatzneigung von Betonrezepturen mittels kleinformatiger Prüfkörper zu analysieren. Abschließend wird unter Anwendung dieser Methode der Einfluss verschiedener Zementarten auf das Abplatzverhalten eines normalfesten Betons untersucht. T2 - STUVA-Tagung 2025 – Internationales Forum für Tunnel und Infrastruktur CY - Hamburg, Germany DA - 25.11.2025 KW - Explosionsartiges Abplatzen KW - Brandfall KW - Klinkereffiziente Zemente PY - 2025 SN - 978-3-96892-327-7 SP - 437 EP - 444 AN - OPUS4-65685 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wachtendorf, Volker A1 - Geburtig, Anja A1 - Trubiroha, P. T1 - Application of a newly proposed sensor for effective UV-irradiance for the monitoring of both natural and artificial weathering conditions N2 - To improve on the classic radiometric sensor with radiometric measurement [ ] here a new UV-sensor characteristic for effective UV is proposed that no longer applies equal weighting of spectral irradiation into the UV irradiance value but rather aims at approaching a weighting according to a typical spectral sensitivity curve of polymers. This curve resembles the erythema curve of the skin which is the basis of the UV-index. For the use of the sensor it would be desirable to keep it in the artificial weathering device for the complete weathering test (including rain phases) while the same sensor should also be applicable for the monitoring of outdoor weathering exposures. A first application of this kind of weighted measurement and a comparison with radiometric measurements accompanied with polymer ageing results will be presented together with conclusions for a future effective UV irradiance sensor. T2 - 9th European Weathering Symposium CY - Basel, Switzerland DA - 18.09.2019 KW - UV-irradiance PY - 2019 SN - 978-3-9818507-5-8 VL - 19 SP - 293 EP - 306 AN - OPUS4-49154 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wachtendorf, Volker A1 - Barthel, Anne-Kathrin A1 - Geburtig, Anja A1 - Trubiroha, P. ED - Reichert, T. T1 - Low-Temperature Irradiation Experiments for PE, PA, and PC Matrices N2 - In this paper, we demonstrate the effects of radiation exposures of polymeric materials with UV-A 340 nm lamps (ISO 4892-3, Type 1A) at -10 °C in comparison to an irradiation at +50 °C using a Global UV Test 200 fluorescent lamp device from Weiss Umwelttechnik GmbH, which incorporates an active cooling appliance. While the effects at -10 °C actually are lower than at + 50°C their extent was clearly beyond expectations. T2 - 8th European Weathering Symposium CY - Vienna, Austria DA - 20.09.2017 KW - Artificial weathering KW - Irradiation KW - Low-temperature KW - Photo-oxidation KW - Polyamide KW - Polycarbonate KW - Polyethylene PY - 2017 SN - 978-3-9818507-1-0 VL - 18 SP - Paper 22, 319 EP - 329 PB - Thomas Würtz Grafik Design CY - Karlsruhe AN - OPUS4-42130 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Trubiroha, P. A1 - Geburtig, Anja A1 - Wachtendorf, Volker T1 - Messung der Temperatur von bestrahlten Oberflächen-Blechdicke beim BST N2 - Die Grenzen der Oberflächentemperaturen von Proben, die der natürlichen oder einer künstlichen Globalstrahlung ausgesetzt sind, können grob mit sog. Schwarzstandard Thermometern BST oder Weißstandard Thermometern WST ermittelt werden [ 1a) ]. Um einige Mängel der aktuellen Konstruktion zu beseitigen, wird ein neues Konzept dieser Thermometer vorgeschlagen, das sie weniger träge und ihre physikalischen Eigenschaften ähnlicher denen einer 5 mm dicken Polymerplatte macht. Es wird auch gezeigt, dass eine Anforderung an die Reaktionszeit von weniger als 1 min in EN 513 unrealistisch ist. T2 - 45. Jahrestagung der GUS CY - Stutensee DA - 16.03.2016 KW - Oberflächentemperatur KW - Strahlungserwärmung KW - IR-Thermometer PY - 2016 SN - 978-3-9816286-7-8 SP - 125 EP - 134 AN - OPUS4-36916 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sitte, M. A1 - Geburtig, Anja T1 - Einfluss der Trocknungszeit nach Feuchtelagerung beim Wellpappen-Berstversuch N2 - Es ist bekannt, dass Wellpappe als meistgenutztes Material für Gefahrgutverpackungen wesentliche Schwächen unter feuchten bzw. nassen Bedingungen zeigt. Verlässliche quantifizierbare Daten hierzu sind leider Mangelware. Obwohl das Material für den weltweiten Versand verwendet wird, werden die Zulassungsprüfungen, v.a. aus Gründen der Reproduzierbarkeit, bei Normklima durchgeführt. Der Berstdruck als wesentliche Größe zur Materialspezifikation wird in Abhängigkeit seiner Vorgeschichte untersucht. Es werden Zeitverlauf und Reversibilität des Berstdruckes nach feuchter Konditionierung für verschiedene Wellpappen-Typen gezeigt. Vorgestellt wird ein Aufbau zur Kopplung des Box-Compression-Tests als Bauteiltest an verschieden feuchte Klimata. T2 - 45. Jahrestagung der GUS CY - Stutensee, Germany DA - 16.03.2016 KW - Feuchtdiffusion KW - Konditionierungsdauer KW - Berstversuch PY - 2016 SN - 978-3-9816286-7-8 SP - 239 EP - 244 AN - OPUS4-36917 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geburtig, Anja A1 - Wachtendorf, Volker A1 - Trubiroha, P. T1 - Quantitative Auswertemöglichkeiten bei der spektralen Bestrahlung – Berechnung des Wirkungsspektrums N2 - Für die Bewertung des Wellenlängeneinflusses auf die Alterungsvorgänge bei der Bestrahlung UV- oder lichtempfindlicher Materialien kann die Methode der spektralen Bestrahlung angewendet werden. Im Prinzip wird dabei das linear dispergierte Spektrum einer Strahlenquelle mit kontinuierlichem Spektrum (z.B. Xe-Lampe) auf eine Probenoberfläche abgebildet, so dass Ort einer Materialänderung und Wellenlänge der Bestrahlung einander zugeordnet werden können. Nachfolgende lokal-auflösende Analysemethoden ermitteln eine Eigenschaftsänderung an einem spezifischen Ort der Probe, aus dem sich dann die Bestrahlungswellenlänge ergibt. Der verwendete Aufbau wird beschrieben. Es wird an einem ausgewählten Beispiel gezeigt, wie durch geeignete Anbindung eines Messsystems zur Bestimmung der spektralen Bestrahlungsstärke und ortsaufgelöste Messungen der Eigenschaftsänderungen eine quantitative Auswertung realisiert werden kann. Der Einfluss nichtlinearer Alterungsverläufe wird diskutiert. Grenzen der Methode werden aufgezeigt und Erweiterungsmöglichkeiten dargestellt. T2 - 46. Jahrestagung der GUS CY - Stutensee-Blankenloch, Germany DA - 22.03.2017 KW - Bewitterung KW - Spektrale Bestrahlung KW - Kunststoffe PY - 2017 SN - 978-3-9816286-9-2 SP - 91 EP - 99 AN - OPUS4-39595 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Homberg, U. A1 - Baum, D. A1 - Prohaska, S. A1 - Kalbe, Ute A1 - Witt, K. J. T1 - Automatic extraction and analysis of realistic pore structures from muCT data for pore space characterization of graded soil N2 - We present image-based methods to extract and analyze the pore structure of graded soil from CT scans. To assess and characterize realistic pore structures of graded soil, we process data of hetero disperse granulär material acquired via high-resolut ion CT. Real soil material configures a pore space with irregulär formations and complex arrangements. In Order to derive parameters of the pore space, a compact representation of the complex pore structure and efficient analysis methods are required. For this purpose, we propose mathematical definitions of the pore structure elements like pore centers, pore paths, pore constrictions, and pore bodies. These definitions are based on the distance map given on the Segmentation of the soil material into particles andpore space. For the extraction of the deftned structure elements, we present two image-basedprocessing pipelines that use the correspondence between our distance-based definition of pore structure elements and a Voronoi decomposition of the pore space. From the extractedpore centers andpore paths, we construct a graph and encode the distance Information on it. This graph, which we call the pore graph, is a compact 3d-representation of the topology of the pore space and provides a good basis to apply efficient graph-based methods for quantification as well as visualization and exploration of the spatial relationships and Connectivity of the pore space. T2 - ICSE6 - 6th International conference on scour and erosion CY - Paris, France DA - 27.08.2012 KW - Microtomography KW - Image analysis KW - Pore structure KW - Pore constriction KW - Suffosion KW - Graded soil PY - 2012 IS - ICSE6-181 SP - 345 EP - 352 AN - OPUS4-26965 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalbe, Ute A1 - Krüger, Oliver A1 - Berger, Wolfgang A1 - Wachtendorf, Volker A1 - Hally, S. ED - Arm, M. ED - Vandecasteele, C. ED - Heynen, J. ED - Suer, P. ED - Lind, B. T1 - Development of leaching procedures for synthetic turf systems N2 - Scrap tyres are widely reused in the form of granules as infill materials or component of sub-base layers in construction of sporting grounds such as synthetic turf areas and athletic track surfaces. The recycled rubber may contain organic and inorganic pollutants due to the presence of vulcanisation catalysts, stabilisers and other additives which can be released into soil and groundwater in the case of outdoor sports facilities. In order to evaluate the amount of potentially mobile pollutants, leaching tests can be employed. This study aimed particularly at the investigation of the feasibility of column tests using complete synthetic surface flooring or turf system assemblies. The release of zinc and polycyclic aromatic hydrocarbons (PAH) leached from components of sports surfaces containing recycled rubber granules was considered. Additionally, batch tests on coated and uncoated styrene butadiene rubber (SBR) granules aged by artificial weathering were performed to indicate its possible influence on the leaching behaviour of zinc and PAH. The chosen approach of column tests simulating typical complete synthetic sports surface installations has been proven to be feasible and robust. The time-dependent leaching behaviour and interactions between single components can be evaluated by column tests. Zinc was the most relevant contaminant in the eluates and its leachability was enhanced after accelerated ageing by artificial weathering. Leachable PAH were found in relatively low but well detectable amounts which increase by ageing as well. T2 - WASCON 2012 CY - Gothenburg, Sweden DA - 30.05.2012 KW - Waste rubber KW - Artificial turf KW - Leaching behaviour KW - Batch test KW - Column test PY - 2012 SP - 1 EP - 5 PB - ISCOWA and SGI AN - OPUS4-26968 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Köppe, Enrico A1 - Bartholmai, Matthias A1 - Liers, A. A1 - Schiller, J. T1 - Radio-based multi-sensor system for person tracking and indoor positioning N2 - Sensor based person tracking is a challenging topic. The main objective is positioning in areas without GPS connection, i.e. indoors. A research project is carried out at BAM, Federal Institute for Materials Research and Testing, to develop and to validate a multi-sensor system for 3D localization. It combines body motion sensing and a guard system for the tracking and recording of the status of persons. The so named BodyGuard system was designed for sensor-based monitoring and radio-based transmission of the movement of a person. Algorithms were developed to transform the sensor data into a spatial coordinate. Thispaper describes how the BodyGuard system operates, which main components were used in the system, how the individual sensor data are converted into 3D motion data, with which algorithms the individual sensors are processed, how individual errors are compensated and how the sensor data are merged into a 3D Model. Final objective of the BodyGuard system is to determine the exact location of a person in a building, e.g. during fire-fighting operations. T2 - WPNC '12 - 9th Workshop on positioning, navigation and communication 2012 CY - Dresden, Germany DA - 15.03.2012 KW - Wireless sensor network (WSN) KW - Embedded systems KW - Sensor calibration and validation KW - Person tracking KW - Inertial navigation system KW - Inertial measurement unit PY - 2012 IS - PS 11 SP - 1 EP - 7 CY - Dresden AN - OPUS4-26028 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias A1 - Stark, Wolfgang A1 - Wolff, Dietmar T1 - Low temperature - For a seal this depends on the applied material T1 - Tieftemperatur - Bei Dichtungen entscheidet dies der eingesetzte Werkstoff N2 - For many sealing applications rubbers are applied due to their special material properties and easy use. In many applications as e.g. in aviation, traffic or process technology the material can be exposed to low temperatures during Operation. Therefore it is important to know the material behavior at those low temperatures to determine the temperature ränge that allows a safe Operation of the seal. One of our main Interests is to ensure the safe enclosureof dangerous goods under various conditions such as different temperatures and over long periods of time. For low temperatures the seal function of an elastomer is limited by the rubber-glass transition during which the material properties change from rubber-like to stiff and glass-like. For a given application this correlation is not trivial, as the glass-rubber transition covers a broad temperatureregion and is strongly influenced by the applied loading frequency. Therefore the applicability of a seal material has to be assessed by its properties in relation to the application conditions and the necessary level of tightness. To characterize the material and the seal function thermal analysis (Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA)), a modlfied method for the accelerated determination of compression set and component tests were applied to different rubber classes, The results show that the temperature ränge where the compression set values come close to 100 % correlates well with the onset temperature of the storage modulus measured by DMA ata measurement frequency of 1 Hz. An in depth analysis of the compression set data allows an estimation of the expected time- and temperature-dependent recovery behavior. T2 - DKT 2012 - German Rubber Conference CY - Nuremberg, Germany DA - 02.07.2012 PY - 2012 IS - 10-2330_5-L-1530 SP - 1 EP - 4 PB - Deutsche Kautschuk-Gesellschaft CY - Frankfurt am Main AN - OPUS4-26190 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Battistella, Beatrice A1 - Revill, Adam A1 - Venzago, Cornel A1 - Hoffmann, Volker A1 - Agudo Jácome, Leonardo A1 - Al-Sabbagh, Dominik A1 - Recknagel, Sebastian A1 - Abad Andrade, Carlos Enrique T1 - Depth-Resolved Lithium Isotope Fractionation as a Diagnostic of Interphase Evolution and Degradation in Lithium Ion Batteries N2 - Lithium isotopic fractionation is well-established in dynamic geochemical systems; however, its role in lithium-ion batteries (LIBs) remains uninvestigated. Herein, we report the first depth-resolved demonstration that isotopic separation occurs during Li-ion cell operation whose magnitude depends on the cycling history. Using depth-resolved glow discharge mass spectrometry, we monitored the 7Li/6Li ratio in LiNi0.333Mn0.333Co0.333O2 (NMC111)||graphite coin cell electrodes at defined life-cycle stages. Different charging rates were examined to get mechanistic insight into kinetic and thermodynamic control in the fractionation process. Although pristine electrodes exhibit a uniform isotopic ratio, cycled electrodes show a distinct 7Li enrichment in the positive electrode and a corresponding accumulation of 6Li at the surface of the negative electrode. The degree of isotopic separation varies with the charging rate. Isotopic signatures correlate with capacity fading, indicating lithium isotope mapping as a sensitive diagnostic tool for tracking electrode degradation and the evolution of the electrode–electrolyte interphases in LIBs. KW - Li-ion batteries KW - Lithium isotopes KW - Post-mortem analysis KW - GD-MS KW - Depth profile KW - Mass spectrometry PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-651287 DO - https://doi.org/10.26434/chemrxiv-2025-5rvlk SP - 1 EP - 19 AN - OPUS4-65128 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Häcker, Ralf T1 - Ermittlung der Unsicherheiten in der Werkstoffprüfung N2 - Einschränkung der Werkstoffprüfung. Stand und Entwicklungen hinsichtlich der Messunsicherheit Ein konkretes, einfaches Beispiel zum Zugversuch • Modellunsicherheit • Verfahrensunsicherheit T2 - 266. PTB-Seminar CY - Berlin, Deutschland DA - 20.03.2012 KW - Messunsicherheit KW - Werkstoffprüfung KW - Zugversuch PY - 2012 SP - 1 EP - 27 CY - Berlin AN - OPUS4-25736 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gravenkamp, Hauke A1 - Song, C. A1 - Prager, Jens T1 - Numerische Berechnung der Dispersionseigenschaften von Lambwellen in Platten mit beliebiger Materialzusammensetzung N2 - Für alle Anwendungen geführter Wellen, beispielsweise in der zerstörungsfreien Materialprüfung, ist die exakte und effiziente Berechnung von Dispersionseigenschaften erforderlich. Dabei müssen für eine gegebene Frequenz die Anzahl der ausbreitungsfähigen Moden und deren Wellenzahlen sowie Phasen- und Gruppengeschwindigkeiten berechnet werden. Für den Fall von Lambwellen in homogenen isotropen Platten existieren analytische Gleichungen für die Wellenzahlen, die sich mit numerischen Nullstellensuchverfahren lösen lassen. Für komplexere Strukturen oder dreidimensionale, nicht rotationssymmetrische Wellenleiter ist die Entwicklung numerischer Methoden erforderlich. In der vorliegenden Arbeit wird ein numerisches Verfahren, basierend auf der Scaled Boundary Finite Element Method (SBFEM) [1] vorgestellt. Mit diesem lassen sich Dispersionseigenschaften von beliebigen Wellenleitern sehr effizient berechnen. Ergebnisse werden für den Fall von Wellen in Platten mit komplexer Materialzusammensetzung präsentiert. T2 - DAGA 2012 - 38. Jahrestagung für Akustik - Fortschritte der Akustik CY - Darmstadt, Deutschland DA - 19.03.2012 KW - Ultraschall KW - Lambwellen KW - Dispersion KW - Scaled boundary finite element method PY - 2012 SP - 1 EP - 2 PB - Deutsche Gesellschaft für Akustik e.V. AN - OPUS4-25978 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Altmann, Korinna A1 - Abusafia, A A1 - Bannick, C-G A1 - Braun, U A1 - Crasselt, Claudia A1 - Dittmar, S A1 - Fuchs, M A1 - Gehde, M A1 - Hagendorf, C A1 - Heller, C A1 - Herper, D A1 - Heymann, S A1 - Kerndorff, A A1 - Knefel, M A1 - Jekel, M A1 - Lelonek, M A1 - Lunkenbein, T A1 - Obermaier, N A1 - Manhart, M A1 - Meurer, Maren A1 - Miclea, P-T A1 - Paul, A A1 - Richter, S A1 - Ricking, M A1 - Rohner, C A1 - Ruhl, A A1 - Sakai, Y A1 - Saravia Arzabe, C A1 - Scheid, C A1 - Schmitt, M A1 - Schnarr, M A1 - Schwertfirm, F A1 - Steinmetz, H A1 - Wander, Lukas A1 - Wiesner, Yosri A1 - Zechmeister, L T1 - RUSEKU - Repräsentative Untersuchungsstrategien für ein integratives Systemverständnis von spezifischen Einträgen von Kunststoffen in die Umwelt : Abschlussbericht N2 - Im Verbundprojekt RUSEKU wurde die Probenahme von Wasserproben entscheidend weiterentwickelt. Wichtig ist hierbei zu gewährleisten, dass genügend Merkmalsträger in jeder Probe untersucht werden. Es muss daher eine für den Probenahmeort repräsentative Beprobung hinsichtlich des Wasservolumens in Abhängigkeit der Partikelanzahl gewährleistet sein. Das Hauptaugenmerk lag im vorliegenden Projekt auf einer praxisnahen Beprobungsstrategie. Es wurden verschiedene Konzepte ausprobiert. • Grundsätzlich hat sich gezeigt, dass eine Stichprobe eine Momentaufnahme des MP-Massengehaltes zeigt. Es wird eine hohe Statistik, also eine Vielzahl an Messungen am gleichen Probenahmeort, benötigt, um eine valide Aussage über den MP-Gehalt zu machen. • Es zeigt sich, dass eine integrale Probenahme über mehrere Wochen mit dem SK routinemäßig möglich ist. Die erfassten MP-Massen sind reproduzierbar und robust. • Die DFZ ist für Stichproben geeignet. Partikel < 50 µm werden eventuell unterschätzt • Die fraktionierte Filtration kann für Stich- und Mischproben direkt im Feld genutzt werden. Fraktionen von 10 und 5 µm werden später im Labor Vakuum filtriert. Es erfolgt eine Fraktionierung der Probe mit Siebmaschenweiten von 1000, 500, 100, 50, 10 und 5 µm. • Die fraktionierte Filtration kann auch anschließend an die Beprobung mit dem SK zur Anwendung kommen. Wird die mit dem SK gewonnene Wasserprobe fraktioniert filtriert, kann neben einem MP-Gesamtgehalt auch eine Einschätzung über die Partikelgrößen gewonnen werden. • Für Wässer mit geringen Partikelzahlen wurde ein Messfiltertiegel entwickelt. Dieser hat eine Maschenweite von 6 µm. Seine Anwendung kann mögliche Verluste beim Transferieren vom Probenahmetool zum Messgefäß und mögliche Kontaminationen reduzieren. Die Optimierung der Probenahmestrategie wurde durch Modellversuche und Simulationen unterstützt. Modellversuche zum Sinkverhalten und Simulationen von MP in realen Gewässern verdeutlichten das komplexe Verhalten der Partikel. Es konnte gezeigt werden, dass Partikel ab einer bestimmten Größe (und kleiner) bei genügend starker Turbulenz sich in der Wassersäule unabhängig von ihrer Dichte verhalten und so auch MP mit kleiner Dichte (z.B. PE) in der gesamten Wassersäule zu finden sind. Es konnte mit dem TEM die Existenz von NP gezeigt werden. Ein wesentlicher Aspekt des RUSEKU Projektes war die Beprobung realer Kompartimente. Beprobt wurde neben Oberflächengewässern, das urbane Abwassersystem der Stadt Kaiserslautern, Waschmaschinenabwasser und Flaschenwasser. • In Oberflächengewässern wurde hauptsächlich PE gefunden. Je nach Probe und Gewässer konnten auch PP, PS, PET, PA, SBR und Acrylate nachgewiesen werden. • Im urbanen Abwassersystem der Stadt Kaiserslautern konnte an allen Probenahmestandorten MP nachgewiesen werden. Es wurde hauptsächlich PE, neben geringeren Mengen an PP, PS und SBR gefunden. Nach einem Regenereignis war der SBR Anteil deutlich erhöht. • Die Beprobung eines realen Wäschepostens, bestehend aus T-Shirts und Hemden mit PA/CO oder PES/CO Mischgewebe, zeigte einen PA- und PES-Austrag im Waschwasser. Der überwiegende Teil der detektierten Fasern ist aber auf Baumwolle zurückzuführen. Reine gravimetrische Messungen zur Detektion von MP führen zu einer starken Überschätzung. • In Flaschenwasser (PET-Flaschen) konnte MP detektiert werden. PET wurde nur im stillen Mineralwasser, nicht in Mineralwasser mit Kohlensäure gefunden werden. Teilweise wurde auch das MP-Material des Verschlusses im Wasser detektiert. • Für Luftproben konnte ein Aufbau zur größenselektiven Beprobung getestet werden. Neben der Probenahme hat das Projekt auch gezeigt, dass die TED-GC/MS geeignet für die MP-Detektion im Routinebetrieb ist. Die TED-GC/MS konnte weiter optimiert werden. Es wurden MP-Massen bestimmt. Im Projekt wurden erste realitätsnahe Referenzmaterialien für die MP Detektion hergestellt. Die Herstellung von realitätsnahen Polymeren in ausreichender Homogenität und Menge hat sich als große Herausforderung herausgestellt. KW - Mikroplastik KW - Probennahme KW - TED-GC/MS KW - Fraktionierte Filtration KW - Mikroplastikreferenzmaterial PY - 2022 SP - 1 EP - 201 AN - OPUS4-57800 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Smales, Glen Jacob A1 - Pauw, Brian Richard T1 - DACHS/MOFs/AutoMOFs_4/Synthesis N2 - The DACHS (Database for Automation, Characterization and Holistic Synthesis) project aims to create completely traceable experimental data, covering syntheses, measurements, analyses, and interpretations. DACHS_MOFs focuses on the synthesis and characterisation of metal-organic frameworks, across multiple, automation-assisted experimental series (AutoMOFs), with the overall goal of producing reproducible MOF samples through tracking of the synthesis parameters. DACHS_MOFs is simultaneously used to test the DACHS principles. This upload contain synthesis data from AutoMOFs_4 in HDF5 format (.h5). Each .h5 file contains detailed information on the chemical, experimenal, and synthesis parameters used during the synthesis of a single AutoMOF sample. KW - Automation KW - Procedure KW - Synthesis KW - Traceability PY - 2024 DO - https://doi.org/10.5281/zenodo.11237899 PB - Zenodo CY - Geneva AN - OPUS4-61343 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Smales, Glen Jacob A1 - Pauw, Brian Richard T1 - DACHS/MOFs/AutoMOFs_1/Synthesis N2 - The DACHS (Database for Automation, Characterization and Holistic Synthesis) project aims to create completely traceable experimental data, covering syntheses, measurements, analyses, and interpretations. DACHS_MOFs focuses on the synthesis and characterisation of metal-organic frameworks, across multiple, automation-assisted experimental series (AutoMOFs), with the overall goal of producing reproducible MOF samples through tracking of the synthesis parameters. DACHS_MOFs is simultaneously used to test the DACHS principles. This upload contain synthesis data from AutoMOFs_1 in HDF5 format (.h5). Each .h5 file contains detailed information on the chemical, experimenal, and synthesis parameters used during the synthesis of a single AutoMOF sample. KW - Synthesis KW - Automation KW - Traceability KW - Procedure PY - 2024 DO - https://doi.org/10.5281/zenodo.11236031 PB - Zenodo CY - Geneva AN - OPUS4-60243 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pauw, Brian Richard A1 - Smales, Glen Jacob A1 - Hörmann, Anja A1 - Moeez, Abdul A1 - Breßler, Ingo T1 - BAMresearch/HDF5Translator: A Framework for translating and transforming data between HDF5 files N2 - HDF5Translator is a Python framework for translating and transforming data between HDF5 files. It supports operations like unit conversion, dimensionality adjustments, and subtree copying, making it suitable for managing and manipulating a wide range of scientific datasets. KW - Measurement data conversion KW - Data conversion KW - HDF5 KW - NeXus KW - NXsas KW - Framework KW - Python KW - Methodology PY - 2024 DO - https://doi.org/10.5281/zenodo.10927639 PB - Zenodo CY - Geneva AN - OPUS4-59797 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pauw, Brian Richard A1 - Laskina, Sofya A1 - Naik, Aakash A1 - Smales, Glen Jacob A1 - George, Janine A1 - Breßler, Ingo A1 - Benner, Philipp T1 - Jupyter notebook and VASP calculation details accompanying the manuscript: "Ultima Ratio: Simulating wide-range X-ray scattering and diffraction" N2 - Summary: This notebook and associated datasets (including VASP details) accompany a manuscript available on the ArXiv (https://doi.org/10.48550/arXiv.2303.13435) and hopefully soon in a journal as short communication as well. Most of the details needed to understand this notebook are explained in that paper with the same title as above. For convenience, the abstract is repeated here: Paper abstract: We demonstrate a strategy for simulating wide-range X-ray scattering patterns, which spans the small- and wide scattering angles as well as the scattering angles typically used for Pair Distribution Function (PDF) analysis. Such simulated patterns can be used to test holistic analysis models, and, since the diffraction intensity is presented coupled to the scattering intensity, may offer a novel pathway for determining the degree of crystallinity. The "Ultima Ratio" strategy is demonstrated on a 64-nm Metal Organic Framework (MOF) particle, calculated from $Q<0.01$\,$\mathrm{nm}^{-1}$ up to $Q\approx150$\,$\mathrm{nm}^{-1}$, with a resolution of 0.16\,\AA. The computations exploit a modified 3D Fast Fourier Transform (3D-FFT), whose modifications enable the transformations of matrices at least up to $8000^3$ voxels in size. Multiple of these modified 3D-FFTs are combined to improve the low-$Q$ behaviour. The resulting curve is compared to a wide-range scattering pattern measured on a polydisperse MOF powder. While computationally intensive, the approach is expected to be useful for simulating scattering from a wide range of realistic, complex structures, from (poly-)crystalline particles to hierarchical, multicomponent structures such as viruses and catalysts. KW - X-ray KW - Simulation KW - Scattering KW - MOUSE KW - Nanomaterials KW - XRD KW - SAXS KW - PDF KW - Total scattering KW - 3D Fourier transform KW - High resolution KW - FFT PY - 2023 DO - https://doi.org/10.5281/zenodo.7764044 PB - Zenodo CY - Geneva AN - OPUS4-57207 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Graf, Benjamin A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Laser metal deposition as repair technology for stainless steel and titanium alloys N2 - In a repair process chain, damaged areas or cracks can be removed by milling and subsequently be reconditioned with new material deposition. The use of laser metal deposition has been investigated for this purpose. The material has been deposited into different groove shapes, using both stainless steel and Ti-6Al-4 V. The influence of welding parameters on the microstructure and the heat affected zone has been studied. The parameters have been modified in order to achieve low heat input and consequently low distortion as well as low metallurgical impact. Finally, an evaluation of the opportunities for an automatized repair process is made. T2 - LANE 2012 - Laser Assisted net shape engineering 7 CY - Fürth, Germany DA - 12.11.2012 KW - Laser metal deposition KW - Laser powder cladding KW - Repair welding KW - Ti-6Al-4 V KW - Stainless steel PY - 2012 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-273066 DO - https://doi.org/10.1016/j.phpro.2012.10.051 N1 - Serientitel: Physics Procedia – Series title: Physics Procedia VL - 39 SP - 376 EP - 381 PB - Elsevier B.V. AN - OPUS4-27306 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Friedrich, Jörg Florian A1 - Unger, Wolfgang A1 - Lippitz, Andreas A1 - Koprinarov, Ivaylo A1 - Weidner, Steffen A1 - Kühn, Gerhard ED - Nowack, H. T1 - Wechselwirkungen zwischen plasmamodifizierten Polymeroberflächen und Metallen T2 - 5. Internationale Fachtagung - ND-Plasma-Technologie CY - Duisburg, Deutschland DA - 1997-09-22 PY - 1997 VL - 5 SP - 1(?) EP - 17(?) PB - Print-Service CY - Mülheim AN - OPUS4-6995 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Friedrich, Jörg Florian A1 - Gerstung, Vanessa A1 - Mix, Renate A1 - Kühn, Gerhard A1 - Weidner, Steffen ED - d'Agostino, R. T1 - Pulsed plasma initiated homo- and copolymerisation - molar masses T2 - 16th International Symposium on Plasma Chemistry (ISPC-16) CY - Taormina, Italy DA - 2003-06-22 PY - 2003 IS - CD-ROM PB - Dep. of Chemistry, Univ. CY - Bari AN - OPUS4-2710 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Ralph-Peter A1 - Falkenhagen, Jana A1 - Much, Helmut A1 - Schulz, Günter A1 - Friedrich, Jörg Florian T1 - Beiträge zur Charakterisierung von synthetischen Si-Polymeren durch Kopplung von HPLC-Trennmethoden mit der MALDI-TOF-MS T2 - DFG-Symposium zum Schwerpunktprogramm "Silicium-Chemie" CY - Werfenweng, Österreich DA - 2000-09-27 PY - 2000 AN - OPUS4-2251 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Falkenhagen, Jana A1 - Krüger, Ralph-Peter A1 - Maier, Bärbel A1 - Much, Helmut A1 - Schulz, Günter T1 - Orthogonal two-dimensional chromatography of poly(ethylene oxid) adducts T2 - HPLC '96 CY - San Francisco, CA, USA DA - 1996-06-16 PY - 1996 CY - San Francisco AN - OPUS4-2221 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geburtig, Anja A1 - Wachtendorf, Volker A1 - Falkenhagen, Jana T1 - Combined impact of UV radiation and nitric acid (HNO3) on HDPE jerrycans – comparison of outdoor and lab test N2 - A damaging action of HNO3-55% only occurs in combination with its decomposition into nitrous gases, which can be caused by UV radiation. In a laboratory test, transparent HDPE jerrycans have been exposed to both UV radiation and 55 wt-% nitric acid solution at (41 ± 2)°C, for up to 20 days. For comparison, UV radiant exposure (21 days) and nitric acid exposure (up to 6 weeks) were performed separately, at nearly equal temperatures. The respective damages are compared with FTIR spectroscopy in ATR and HT-gel permeation chromatography (GPC) on a molecular level and with hydraulic internal pressure testing as a component test. For the used jerrycans, relevant oxidation can only be found after the combined exposure. The gradual increase in oxidative damage shows the good reproducibility of the lab exposure. The decomposition of nitric acid into nitrous gases by UV radiation – as well as the jerrycan oxidation – is also observed at lower HNO3 concentration (28 wt- %). Similar results are obtained after outdoor tests. Again, the damage occurs only after combined exposure, in contrast to the exposures to UV only and to HNO3 only, which were conducted in parallel. Outdoor exposures are most readily accepted as they represent possible end-use conditions. However, the reproducibility of these exposures is poor due to the large temporal variations in weather. There are also several safety risks, which is why the number of replicates remains limited. Since the outdoor and lab exposure tests show the same qualitative results, it is appropriate to conduct systematic studies in the laboratory. After 6 days of lab exposure, the oxidation damage is rated as critical, which corresponds to about 1/10 year in Central Europe, according to the UV radiant exposure. It should be noted that this amount can also occur in two sunny weeks. T2 - 24th iapri World Packaging Conference CY - Valencia, Spain DA - 17.06.2024 KW - Ppolyethylene KW - UV exposure KW - Nitric acid KW - Oxidation PY - 2024 VL - 2 SP - 30 EP - 37 PB - ITENE AN - OPUS4-60414 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weidner, Steffen A1 - Falkenhagen, Jana A1 - Friedrich, Jörg Florian A1 - Krüger, Ralph-Peter A1 - Schulz, Günter A1 - Much, Helmut T1 - Liquid Adsorption Chromatography near Critical Conditions of Adsorption coupled with Matrix-assisted Laser/Ionization Mass Spectrometry T2 - 47th ASMS Conference on Mass Spectrometry and Allied Topics CY - Dallas, TX, USA DA - 1999-06-13 PY - 1999 CY - Dallas, Tex AN - OPUS4-2165 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Ralph-Peter A1 - Friedrich, Jörg Florian A1 - Much, Helmut A1 - Schulz, Günter A1 - Falkenhagen, Jana T1 - Zur Charakterisierung von Si-Polymeren durch Kopplung flüssigchromatographischer Arbeitsweisen mit der MALDI-TOF-MS T2 - DFG-Symposium zum Schwerpunktprogramm "Silicium-Chemie" CY - Bielefeld, Deutschland DA - 1999-05-09 PY - 1999 AN - OPUS4-2239 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Friedrich, Jörg Florian A1 - Schulz, Eckhard A1 - Weidner, Steffen A1 - Kühn, Gerhard T1 - Verbesserungen der mechanischen Festigkeiten von Faser-Polymer-Verbundwerkstoffen durch Vorbehandlung der Fasern im Niederdruckplasma T2 - Vortragsbände des 8. Internationalen Techtextil-Symposiums 1997 CY - Frankfurt am Main, Deutschland DA - 1997-05-12 PY - 1997 VL - 8 SP - 1(?) EP - 16(?) PB - Messe Frankfurt CY - Frankfurt am Main AN - OPUS4-7287 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Ralph-Peter A1 - Falkenhagen, Jana A1 - Much, Helmut A1 - Schulz, Günter A1 - Friedrich, Jörg Florian T1 - Beiträge zur Charakterisierung von synthetischen Si-Polymeren durch Kopplung von HPLC-Trennmethoden mit der MALDI-TOF-MS T2 - Incom 2001 - International Symposium on Instrumentalized Analytical Chemistry and Computer Technology CY - Düsseldorf, Deutschland DA - 2001-03-27 PY - 2001 AN - OPUS4-2254 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Ralph-Peter A1 - Falkenhagen, Jana A1 - Much, Helmut A1 - Schulz, Günter A1 - Weidner, Steffen T1 - Charakterisierung von synthetischen Polymeren durch Kopplung flüssigchromato-graphischer Trennmethoden mit der MALDI-TOF-Massenspektrometrie T2 - 1. Berliner Werkstofftag CY - Berlin, Deutschland DA - 1999-09-16 PY - 1999 AN - OPUS4-2242 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Friedrich, Jörg Florian A1 - Wigant, L. A1 - Unger, Wolfgang A1 - Lippitz, Andreas A1 - Weidner, Steffen A1 - Kühn, Gerhard A1 - Geng, Sh. A1 - Erdmann, J. A1 - Gorsler, H.-V. T1 - Plasmavorbehandlungen von Polymeroberflächen T2 - 2. Freiberger Polymertag CY - Freiberg DA - 1995-05-30 PY - 1995 SP - 17 Seiten CY - Freiberg AN - OPUS4-7014 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Friedrich, Jörg Florian A1 - Ghode, Archana A1 - Kühn, Gerhard A1 - Weidner, Steffen A1 - Geng, Shiming A1 - Retzko, Iris A1 - Unger, Wolfgang A1 - Lippitz, Andreas ED - Schindel-Bidinelli, E. T1 - Polymeroberflächenfunktionalisierungen im gepulsten Plasma mit nachfolgender chemischer Behandlung T2 - 14. Internationales Symposium Swissbonding ; 14. Internationaler Kongreß Swiss Bonding ; 14th Swiss Bonding 00 CY - Rapperswil, Schweiz DA - 2000-05-16 PY - 2000 SP - 31 EP - 44 PB - SWIBOTECH GmbH CY - Bülach AN - OPUS4-6980 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Altmann, Korinna T1 - Deliverable 2: Summary report on: The development of pristine SI traceable reference materials for SMPs (0.1 μm - 10 μm) and NPs (< 0.1 μm), representative of partially degraded/naturally aged samples in complex food and environmental matrices, and for realistic polydisperse size distributions and irregular shapes N2 - PlasticTrace aims to address the urgent need for development and harmonisation of methods for the chemical identification, physical characterisation and quantification of released small micro/nanoplastics (SMPs/NPs) in drinking water, food and environmental matrices, as required by the EU’s Circular Economy Action Plan (CEAP). This report describs the characterisation of nanoPP analysed in the PlasticTrace project aiming to develop a reference material. The nanoPP was analysed mainly by light scattering methods. Homogeneity control was done by DLS. KW - Nanoplastics KW - Reference materials PY - 2024 N1 - Project Number 21GRD07: PlasticTrace (Tracing Micro and NanoPlastics in Food and Environment), funded by the European Union SP - 1 EP - 29 PB - European Association of National Metrology Institutes (EURAMET) CY - Braunschweig AN - OPUS4-62299 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Miliūtė, Aistė T1 - Synthesis and phase purity of the negative thermal expansion material ZrV2O7 N2 - This repository contains computational and experimental data for the manuscript titled “Synthesis and phase purity of the negative thermal expansion material ZrV2O7”. KW - NTE KW - Sol-gel KW - Solid-state KW - Ab-initio KW - XRD KW - Raman PY - 2024 DO - https://doi.org/10.5281/zenodo.12688634 PB - Zenodo CY - Geneva AN - OPUS4-61360 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Götschel, S. A1 - Weiser, M. A1 - Maierhofer, Christiane A1 - Richter, Regina ED - Cardone, G. T1 - Data enhancement for active thermography N2 - Pulse thermography is a non-destructive testing method based on infrared imaging of transient thermal patterns. Heating the surface of the structure under test for a short period of time generates a non-stationary temperature distribution and thus a thermal contrast between the defect and the sound material. Due to measurement noise, preprocessing of the experimental data is necessary, before reconstruction algorithms can be applied. We propose a decomposition of the measured temperature into Green's function solutions to eliminate noise. T2 - QIRT 11 - 11th International conference on Quantitative InfraRed Thermography CY - Naples, Italy DA - 11.06.2012 KW - Datenglättung KW - Rekonstruktion PY - 2012 SP - 1 EP - 9 AN - OPUS4-26447 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Linnemann, Konrad A1 - Ballheimer, Viktor A1 - Sterthaus, Jens A1 - Wille, Frank T1 - Methodological aspects for finite element modeling of lid systems for type B(U) transport packages N2 - The regulatory compliance of the containment system is of essential importance for the assessment process of Type B(U) transport packages. The requirements of the IAEA safety standards for transport conditions implies high loading on the containment system. The integrity of the containment system has to be ensured in mechanical and thermal tests. The containment system of German SNF and HLW transport packages usually includes bolted lids with metal gaskets. The finite element (FE) method is recommended for the analysis of lid systems according to the guideline BAM-GGR 012 for assessment of bolted lid and trunnion systems. FE analyses provide more accurate and detailed information about loading and deformation of such kind of structures. The results allow the strength assessment of the lid and bolts as well as the evaluation of relative displacements between the lid and the cask body in the area of the gasket groove. This paper discusses aspects concerning FE simulation of lid systems for Type B(U) packages for the transport of SNF and HLW. The work is based on the experiences of BAM Federal Institute for Materials Research and Testing as the German competent authority for the mechanical design assessment of such kind of packages. The issues considered include modeling strategies, analysis techniques and the interpretation of results. A particular focus of this paper is on the evaluation of the results with regard to FE accuracy, influence of the FE contact formulation and FE modeling techniques to take the metallic gasket into account. T2 - RAMTRANSPORT 2012 - 9th International Conference on the Radioactive Materials Transport and Storage CY - London, UK DA - 22.05.2012 PY - 2012 IS - Paper 2.2 RAM 27 SP - 1 EP - 8 AN - OPUS4-26353 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mizuno, Y. A1 - Lenke, Peter A1 - Krebber, Katerina A1 - Nakamura, K. T1 - Brillouin gain spectrum characterization in POF fabricated by different manufacturers at 1.32 and 1.55 um N2 - The Brillouin gain spectra (BGS) in perfluorinated graded-index polymer optical fibers (PFGl-POFs) are characterized at 1.32 and 1.55 pm. Three kinds of PFGl-POFs with the same core diameter but fabricated by different manufacturers are tested. For all the PFGl-POFs, the Stokes power measured at 1.32 pm is higher than that at 1.55 pm eine to the lower propagation loss, but significant difference in Stokes power is observed among the three. Based on the measurement by optical time-domain reflectometry, we show that the actual Propagation loss of the PFGl-POFs plays a crucial role in observing BGS. T2 - POF 2012 - 21st International conference on plastic optical fibers CY - Atlanta, Georgia, USA DA - 10.09.2012 KW - Brillouin scattering KW - Perfluorinated graded-index polymer optical fiber KW - Optical time-domain reflectometry KW - Nonlinear optics PY - 2012 SP - 96 EP - 99 AN - OPUS4-26742 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Gert A1 - Rethmeier, Michael ED - Kožuh, Z. T1 - Spot welding and weldbonding of high strength steels for lightweight auto body manufacturing N2 - The resistance spot welding procedure is one of the most important joining technique in lightweight car body shell mass production. Especially for newly developed ultra high strength steels (UHSS) and advanced high strength steels (AHSS), this joining technique has more advantages than other thermal and mechanical joining procedures for thin Steel sheets. Additionally, the technique of adhesive bonding and its combination with the technique of resistance spot welding called weldbonding becomes more and more important. The weldbonding affords many advantages, e.g. improved crash performance, fatigue behaviour and corrosion resistance. The main target of the contribution is to show the influence of different joined ultra and advanced high strength steels on the process reliability for both the resistance spot welding process and the weldbonding process. In this connection the influence of surface conditions of the steel sheets, the applied adhesive and the choice of the welding parameters on the process reliability will be studied. The results for the weldbonding procedure are based on different adhesives. Based on the representation of welding current ranges by weldability lobes, Statements concerning the weldbonding process reliability for some special AHSS and UHSS will be given. The mechanical behaviour of spot welded and weldbonded joints for different AHSS and UHSS will be studied. T2 - EUROJOIN 8 - 8th European Conference CY - Pula, Croatia DA - 24.05.2012 KW - Spot welding KW - Weldbonding KW - High strength steels KW - Process reliability KW - Mechanical properties of joints PY - 2012 SN - 978-953-7518-02-8 SP - 633 EP - 643 PB - Croatian Welding Society (CWS) CY - Zagreb AN - OPUS4-26383 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Smales, Glen Jacob A1 - Pauw, Brian Richard T1 - DACHS/MOFs/AutoMOFs_2/Synthesis N2 - The DACHS (Database for Automation, Characterization and Holistic Synthesis) project aims to create completely traceable experimental data, covering syntheses, measurements, analyses, and interpretations. DACHS_MOFs focuses on the synthesis and characterisation of metal-organic frameworks, across multiple, automation-assisted experimental series (AutoMOFs), with the overall goal of producing reproducible MOF samples through tracking of the synthesis parameters. DACHS_MOFs is simultaneously used to test the DACHS principles. This upload contain synthesis data from AutoMOFs_2 in HDF5 format (.h5). Each .h5 file contains detailed information on the chemical, experimenal, and synthesis parameters used during the synthesis of a single AutoMOF sample. KW - Automation KW - Procedure KW - Synthesis KW - Traceability PY - 2024 DO - https://doi.org/10.5281/zenodo.11236074 PB - Zenodo CY - Geneva AN - OPUS4-60611 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Friedrich, Jörg Florian A1 - Unger, Wolfgang A1 - Lippitz, Andreas A1 - Weidner, Steffen A1 - Geng, Sh. A1 - Wigant, L. A1 - Wöll, Ch. A1 - Erdmann, J. A1 - Gorsler, H.-V. T1 - Characterization of plasma-modified organic surfaces by electron spectroscopy, SEIRA, and MALDI-TOF-MS T2 - 6th European Conference on Applications of Surface and Interface Analysis CY - Montreux, Switzerland DA - 1995-10-09 PY - 1995 SP - TC 11 PB - Wiley CY - Chichester AN - OPUS4-7001 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Rita A1 - Kelm, Jürgen A1 - Kretzschmar, Hans-Jürgen A1 - Schulze, Dietmar A1 - Trubiroha, Peter A1 - Weidner, Steffen T1 - Eine neue Klasse von Ozonschutzmitteln - verbesserter Ozonschutz durch teilweisen Einbau in die Polymermatrix T2 - IRC '03 ; International Rubber Conference 2003 ; Internationale Kautschuk-Tagung 2003 CY - Nürnberg, Deutschland DA - 2003-06-30 PY - 2003 SP - 139 EP - 142 PB - DKG, Dt. Kautschuk-Ges. CY - Frankfurt, Main AN - OPUS4-2608 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weidner, Steffen A1 - Kühn, Gerhard A1 - Just, Ulrich A1 - Werthmann, Barbara A1 - Decker, Renate A1 - Schwarz, Bärbel A1 - Borowski, Renate T1 - MALDI/MS - A New Technique in Characterizing Chemical Heterogeneity of Degradation Products of Poly(Ethylene Terephthalate)s T2 - International GPC Symposium '96 CY - San Diego, CA, USA DA - 1996-09-08 PY - 1996 SP - 632 EP - 651 CY - Milford, Mass. AN - OPUS4-11905 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Just, Ulrich A1 - Weidner, Steffen A1 - Wittke, Wolfgang A1 - Friedrich, Jörg Florian A1 - Rittig, F. A1 - Gruber, F. T1 - 2D-Characterization of Polyamides using Chromatography and MALDI-TOF-MS T2 - Waters International GPC 2003 and ISPAC-16-Symposium CY - Baltimore, MD, USA DA - 2003-06-09 PY - 2003 AN - OPUS4-2631 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz, Günter A1 - Falkenhagen, Jana A1 - Krüger, Ralph-Peter T1 - Kopplung von HPLC-Trennmethoden mit der MALDI-TOF-Massenspektrometrie zur Charakterisierung von Si-haltigen Verbindungen T2 - DFG-Symposium zum Schwerpunktprogramm "Silicium-Chemie" CY - Werfenweng, Österreich DA - 2002-05-02 PY - 2002 AN - OPUS4-1797 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Ralph-Peter A1 - Falkenhagen, Jana A1 - Gerstung, Vanessa A1 - Much, Helmut A1 - Schulz, Günter A1 - Friedrich, Jörg Florian T1 - Beiträge zur Charakterisierung von synthetischen Si-Polymeren durch Kopplung von HPLC-Trennmethoden mit der MALDI-TOF-Massenspektrometrie T2 - Berliner Polymeren-Tage 2000 CY - Berlin, Deutschland DA - 2000-10-09 PY - 2000 CY - Berlin AN - OPUS4-2252 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Ralph-Peter A1 - Falkenhagen, Jana A1 - Much, Helmut A1 - Schulz, Günter A1 - Rikowski, E. T1 - Characterization of silicon polymers (silsesquioxanes, dendrimers and copolymers) by means of different modes of Liquid Chromatography and MALDI-TOF-MS PY - 1998 PB - Messe München GmbH CY - München AN - OPUS4-2236 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heunisch, Andreas A1 - Schulz, Bärbel A1 - Rabe, Torsten T1 - LTCC antenna array with integrated liquid crystal phase shifter for satellite communication N2 - Low Temperature Cofired Ceramic (LTCC) is used as a substrate material for microelectronic devices in satellite communication. Its dielectric properties and excellent variability allows a good compactness and a high level of integration. An LTCC antenna array for microwave signals operating at 30 GHz is presented. All components such as radio frequency distribution network, four waveguide phase shifters and horn antennas are integrated in one ceramic module. The phase shifters are implemented as high volume cavities in the LTCC. A tailored mixture of liquid crystal can be stored inside the cavities. By applying an electric field, the anisotropic LC-molecules are aligned. The field is provided through a biasing network with four electrodes and screen printed resistive layers with resistance values in the MΩ/□ range. The alignment and with it the phase shifting is nearly seamless. The antenna module is manufactured in multilayer technology and consists of more than 40 layers. Lamination is carried out by thermocompression in two steps. A water based adhesive is used in the second. The cofiring is done in a sintering press. Temperature and pressure profile are chosen carefully, considering the high volume of the laminate and the buried cavities inside the module. After sintering, the horn antennas are milled into the front side of the ceramic body, which is about 5 mm in height. T2 - CICMT 2012 - 8th International conference on ceramic interconnect & ceramic microsystems technologies CY - Erfurt, Germany DA - 16.04.2012 KW - LTCC multilayer KW - Liquid crystals KW - Cavities KW - Pressure assisted sintering PY - 2012 SP - 000097 EP - 000102 (Session TP 1 / TP 15) AN - OPUS4-27404 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Höhne, Christian A1 - Boehm, Rainer A1 - Prager, Jens T1 - Anwendung multidimensionaler analytischer Signale mit Single-Orthant-Spektren zur Aufbereitung von SAFT-Daten in der Ultraschallprüfung N2 - Die Rekonstruktion von Materialfehlern aus gemessenen HF-Bildern mit Hilfe der Synthetic Aperture Focussing Technique (SAFT) ist ein bildgebendes Verfahren der zerstörungsfreien Werkstoffprüfung. Die Auswertbarkeit der gewonnenen Ergebnisse wird dabei maßgeblich durch die Darstellung der mittels SAFT-Rekonstruktion zusammengestellten Daten bestimmt, welche zunächst nur in Form positiver und negativer Amplitudenwerte vorliegen. Die Aufbereitung dieser Daten erfolgt durch Bildung der Einhüllenden der Amplituden aus dem zugehörigen analytischen Signal. Die Erweiterung dieses, nur im eindimensionalen Fall eindeutig definierten, Konzepts auf zweidimensionale Signalverläufe erfolgt dabei in Form einer Mittelung über die Betragsquadrate aller möglichen mit Single-Orthant-Spektren (SO-Spektren) zu bildenden analytischen Signale. Es wird gezeigt dass dies der Verwendung einer Approximation als separables Signal entspricht und für den zweidimensionalen Fall eine Möglichkeit vorgeschlagen Signale anhand ihrer partiellen und totalen Hilberttransformationen auf Separabilität und damit Anwendbarkeit dieser Näherung zu testen. Die Ergebnisse der so durchgeführten Bildverbesserung werden am Beispiel einer zweidimensionalen SAFT-Rekonstruktion an verschiedenen Reflektorarten dargestellt. T2 - DAGA 2012 - 38. Jahrestagung für Akustik - Fortschritte der Akustik CY - Darmstadt, Deutschland DA - 19.03.2012 PY - 2012 VL - II SP - 957 EP - 958 PB - Deutsche Gesellschaft für Akustik e.V. AN - OPUS4-25977 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Ralph-Peter A1 - Falkenhagen, Jana A1 - Much, Helmut A1 - Schulz, Günter A1 - Rikowski, E. T1 - Zur Charakterisierung von Si-Polymeren durch MALDI-TOF-MS in Kopplung mit flüssigchromatographischen Arbeitsweisen T2 - InCom '99 CY - Düsseldorf, Deutschland DA - 1999-03-22 PY - 1999 AN - OPUS4-2238 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Friedrich, Jörg Florian A1 - Schulz, Eckhard A1 - Weidner, Steffen A1 - Kühn, Gerhard T1 - Improvement in Mechanical Strength of Fibre Polymer Composites by Fibre Pretreatment in Low-Pressure Plasmas T2 - Vortragsbände des 8. Internationalen Techtextil-Symposiums 1997 CY - Frankfurt am Main, Deutschland DA - 1997-05-12 PY - 1997 SP - 1(?) EP - 16(?) PB - Messe Frankfurt CY - Frankfurt am Main AN - OPUS4-7286 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Falkenhagen, Jana A1 - Krüger, Ralph-Peter A1 - Schulz, Günter T1 - Characterization of polylactides by coupling of chromatographic methods with MALDI-TOF-MS T2 - Polydays 2002 ; ISPAC 2002 CY - Berlin, Germany DA - 2002-09-30 PY - 2002 AN - OPUS4-1807 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Falkenhagen, Jana A1 - Krüger, Ralph-Peter A1 - Schulz, Günter A1 - Weidner, Steffen T1 - Polymer Characterization by LC / MALDI-MS Coupling T2 - Vortragstagung "Funktionspolymere für Systemlösungen" CY - Darmstadt, Germany DA - 2002-03-18 PY - 2002 AN - OPUS4-1805 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Falkenhagen, Jana A1 - Krüger, Ralph-Peter A1 - Schulz, Günter T1 - Polymercharakterisierung durch Kombination chromatographischer Verfahren sowie HPLC - MALDI-TOF-MS - Kopplung T2 - Tagung der BASF AG 2002 CY - Ludwigshafen, Deutschland DA - 2002-12-03 PY - 2002 AN - OPUS4-1804 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Falkenhagen, Jana A1 - Krüger, Ralph-Peter A1 - Much, Helmut A1 - Schulz, Günter T1 - Investigations of Polymer Heterogeneity by Two-Dimensional HPLC, MALDI-TOF-MS and FTIR Coupling T2 - ISPAC 8, HPLC ´95 CY - Sanibel Island, FL, USA DA - 1995-05-20 PY - 1995 PB - Gordon and Breach CY - Sant Helier AN - OPUS4-2203 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Ralph-Peter A1 - Falkenhagen, Jana A1 - Schulz, Günter T1 - Calixarene in Photoresisten (Kopplung von flüssigchromatographischen Methoden mit der MALDI-TOF-MS) T2 - Fachgruppenvollversammlung BAM CY - Berlin, Deutschland DA - 2002-01-29 PY - 2002 AN - OPUS4-2191 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Falkenhagen, Jana A1 - Krüger, Ralph-Peter A1 - Much, Helmut A1 - Schulz, Günter T1 - Coupling of different modes of liquid chromatography of polymers with spectroscopic methods and MALDI-TOF-MS-key for determination of polymer heterogeneity T2 - 6th SPSJ International Polymer Conference (IPC 97) CY - Kusatsu, Japan DA - 1997-10-20 PY - 1997 VL - 6 AN - OPUS4-2233 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Ralph-Peter A1 - Falkenhagen, Jana A1 - Much, Helmut A1 - Schulz, Günter T1 - Charakterisierung von Si-Polymerarchitekturen durch Kopplung von flüssigchromatographischen Methoden mit der MALDI-TOF-Massenspektrometrie im DFG-Schwerpunktprogramm T2 - DFG-Kolloquium zum Schwerpunktprogramm "Silicium-Chemie" CY - Bielefeld, Deutschland DA - 1997-05-12 PY - 1997 AN - OPUS4-2231 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Falkenhagen, Jana A1 - Krüger, Ralph-Peter A1 - Schulz, Günter A1 - Weidner, Steffen T1 - Polymer characterization by LC / MALDI-MS coupling T2 - Bayreuther Polymer Symposium 2001 CY - Bayreuth, Germany DA - 2001-09-16 PY - 2001 CY - Bayreuth AN - OPUS4-2256 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Friedrich, Jörg Florian A1 - Unger, Wolfgang A1 - Lippitz, Andreas A1 - Koprinarov, Ivaylo A1 - Weidner, Steffen A1 - Kühn, Gerhard ED - Schindel-Bidinelli, E. T1 - Umweltfreundliches Metallisieren von Kunststoffen durch Plasmavorbehandlung in einem geschlossenen Reaktor T2 - Swissbonding 97 ; 11. Internationales Symposium Klebtechnik und Umwelt ; 11th International Symposium Bonding and Sealing Technology CY - Rapperswil, Schweiz DA - 1997-05-26 PY - 1997 SP - 1(?) EP - 3(?) PB - SWIBOTECH CY - Rorbas AN - OPUS4-6994 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Ralph-Peter A1 - Falkenhagen, Jana A1 - Much, Helmut A1 - Schulz, Günter T1 - Neue Ergebnisse der HPLC/MALDI-TOF-MS - Kopplung zur Charakterisierung von synthetischen Polymeren T2 - Analytica Conference 98 CY - München, Deutschland DA - 1998-04-21 PY - 1998 CY - München AN - OPUS4-2235 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gebhardt, Moritz Oliver A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael ED - Turichin, G. T1 - Laser-MSG-hybrid welding of thick walled precision pipes N2 - Thick-walled pipes made of steel are the basis of a large number of components in mechanical and installation engineering, e.g. for hydraulic components, in power station technology or in the petroleum industry. Particularly when strict positional and shape tolerances are demanded, the classical manufacturing process is chip-producing machining from the solid material. However, this is time-intensive and material-intensive. The laser/GMA hybrid processes with modern high-power lasers are a suitable alternative. With these processes, it is currently possible to weld components with a wall thickness up to approx. 15 mm with little distortion in one pass. However, in initial experiments, solidification cracks with longitudinal and vertical orientations in relation to the welding direction, so-called central line cracks, were established in welds on pipes. Within the framework of a research project, it was possible to determine the cause of the cracking and to find measures in order to avoid it. The technical boundary conditions could be complied with in this respect. The article gives an overview of the research project and the essential results. T2 - VII. International scientific and technical conference 'Beam technologies & laser application' CY - Saint-Petersburg, Russia DA - 18.09.2012 PY - 2013 SP - 235 EP - 247 PB - Publishing house SPbSPU AN - OPUS4-28041 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Ralph-Peter A1 - Falkenhagen, Jana A1 - Schulz, Günter A1 - Weinmann, S. T1 - Beiträge zur Charakterisierung von Polyactiden durch Kopplung von HPLC-Trennmethoden mit der MALDI-TOF-MS T2 - Analytica Conference 2002 CY - München, Deutschland DA - 2002-04-23 PY - 2002 AN - OPUS4-2188 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Falkenhagen, Jana A1 - Krüger, Ralph-Peter A1 - Much, Helmut A1 - Schulz, Günter A1 - Spranger, K. T1 - Neue Möglichkeiten der Polymercharakterisierung durch 2D-HPLC, Kopplung mit spektroskopischen Methoden und MALDI-TOF-MS T2 - Gesellschaft Deutscher Chemiker, "Klassische Polymere im Aufwind, Polymerchemie aktuell" CY - Dresden, Deutschland DA - 1996-03-25 PY - 1996 CY - Dresden AN - OPUS4-2212 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Ralph-Peter A1 - Falkenhagen, Jana A1 - Much, Helmut A1 - Schulz, Günter A1 - Spranger, K. ED - Günther, W. T1 - MALDI-TOF-MS zur Charakterisierung von synthetischen Polymeren in Kopplung mit der HPLC T2 - InCom '96 - International Symposium on Instrumentalized Analytical Chemistry and Computer Technology CY - Düsseldorf, Deutschland DA - 1996-03-25 PY - 1996 PB - IAS CY - Moers AN - OPUS4-2213 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Ralph-Peter A1 - Falkenhagen, Jana A1 - Schulz, Günter T1 - Einführung in die MALDI-TOF-Massenspektrometrie an synthetischen Polymeren T2 - Innovent Technologieentwicklung CY - Jena, Deutschland DA - 2002-08-14 PY - 2002 AN - OPUS4-1800 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Falkenhagen, Jana A1 - Krüger, Ralph-Peter A1 - Schulz, Günter T1 - Mehrdimensionale Analysenverfahren für komplexe Polymere - Arbeitskreis Polymeranalytik T2 - Tagung des Arbeitskreises Polymeranalytik CY - Darmstadt, Deutschland DA - 2002-09-25 PY - 2002 AN - OPUS4-1802 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Falkenhagen, Jana A1 - Krüger, Ralph-Peter A1 - Schulz, Günter T1 - Polymercharakterisierung mittels flüssigchromatographischer und spektroskopischer Methoden T2 - Innovent Technologieentwicklung CY - Jena, Deutschland DA - 2002-08-14 PY - 2002 AN - OPUS4-1801 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Falkenhagen, Jana T1 - Charakterisierung von Polymeren durch Kopplung von flüssigchromatographischen und spektroskopischen Methoden T2 - HPLC-Tage CY - Mannheim, Deutschland DA - 2002-11-12 PY - 2002 AN - OPUS4-1803 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Much, Helmut A1 - Falkenhagen, Jana A1 - Krüger, Ralph-Peter A1 - Schulz, Günter T1 - Charakterisierung von synthetischen Polymeren durch Kopplung flüssigchromato-graphischer Trennmethoden mit der MALDI-TOF-Massenspektrometrie T2 - Workshop "Hierarchic Structure Formation and Function of Organic-Inorganic Hybrid Systems" CY - Ulm, Deutschland DA - 1999-11-26 PY - 1999 AN - OPUS4-2243 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Ralph-Peter A1 - Falkenhagen, Jana A1 - Much, Helmut A1 - Schulz, Günter ED - Günther, W. T1 - Neue Ergebnisse der MALDI-TOF-Massenspektrometrie von synthetischen Polymeren T2 - InCom '97 - International Symposium on Instrumentalized Analytical Chemistry and Computer Technology CY - Düsseldorf, Deutschland DA - 1997-03-17 PY - 1997 VL - 97 PB - IAS CY - Moers AN - OPUS4-2230 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Falkenhagen, Jana A1 - Krüger, Ralph-Peter A1 - Much, Helmut A1 - Schulz, Günter T1 - Characterization and identification of new polymer structures by optimization and coupling of HPLC and MALDI-TOF-MS T2 - Dechema-Diskussionstagung "Neue Methoden der Polymeranalytik" CY - Mainz, Germany DA - 2001-04-02 PY - 2001 CY - Mainz AN - OPUS4-2255 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Ralph-Peter A1 - Falkenhagen, Jana A1 - Much, Helmut A1 - Schulz, Günter T1 - Beiträge zur Charakterisierung von synthetischen Si-Polymeren durch Kopplung von HPLC-Trennmethoden mit der MALDI-TOF-MS T2 - Analytica Conference 2000 CY - München, Deutschland DA - 2000-04-11 PY - 2000 CY - München AN - OPUS4-2245 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Ralph-Peter A1 - Falkenhagen, Jana A1 - Much, Helmut A1 - Schulz, Günter A1 - Spranger, K. T1 - Zur Charakterisierung von synthetischen Polymeren durch MALDI-TOF in Kopplung mit der LACCC T2 - Analytica Conference 96 CY - München, Deutschland DA - 1996-04-23 PY - 1996 PB - Messe München GmbH CY - München AN - OPUS4-2219 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Falkenhagen, Jana A1 - Krüger, Ralph-Peter A1 - Rikowski, Eckhard A1 - Schulz, Günter A1 - Friedrich, Jörg Florian ED - Grellmann, W. T1 - Synthesis and Characterisation of Polyhedral Silsesquioxanes with Nanotubular Structures T2 - 23. DVM-Vortrags- und Diskussionstagung "Werkstoffprüfung 2005", DA - 2005-12-01 PY - 2005 SP - 25 EP - 30 PB - DVM AN - OPUS4-11947 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Ralph-Peter A1 - Falkenhagen, Jana A1 - Much, Helmut A1 - Schulz, Günter T1 - Characterization of silicon polymers (silsesquioxanes, dendrimers and copolymers) by means of different modes of Liquid Chromatography and MALDI-TOF-MS T2 - 11th International Symposium on Polymer Analysis and Characterization CY - Santa Margherita Ligure, Italien DA - 1998-05-25 PY - 1999 N1 - Serientitel: International journal of polymer analysis and characterization – Series title: International journal of polymer analysis and characterization IS - 5.1999,3 PB - Gordon and Breach CY - St. Helier AN - OPUS4-19053 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hauswaldt, Sebastian A1 - Korzen, Manfred A1 - Hartmann, S. ED - Fontana, M. ED - Frangi, A. ED - Knobloch, M. T1 - A continuum-mechanical model for FE-simulations of steel constructions in fire N2 - This paper presents a thermoviscoplastic constitutive model within the framework of continuum mechanics for the description of the behavior of structural steel subjected to fire loading. The model is represented through a set of ordinary differential equations and belongs to the class of so-called unified theories which do not separate plastic and creep strains. The material parameters are identified for the structural steel S 235 on the basis of tension and compression tests at constant temperature with varying strain rates and verified against transient creep test with varying temperature. For effective numerical simulations with the finite element program ABAQUS the model is prepared with a stress algorithm and consistent tangent operator. The simulations are compared with experimental data of fire resistance tests on columns. T2 - SIF 2012 - 7th International conference on structures in fire CY - Zurich, Switzerland DA - 06.06.2012 KW - Constitutive equation KW - Viscoplasticity KW - Endochronic plasticity KW - UMAT KW - Finite element method KW - Fire resistance PY - 2012 DO - https://doi.org/10.3929/ethz-a-007050197 SP - 439 EP - 448 CY - Zurich, Switzerland AN - OPUS4-26108 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Tschiche, Harald T1 - Determination of degradation products of thermoplastic polyurethane using fluorescent sensors in a model system N2 - Polyurethanes (PU) are formed by polyaddition reaction between diols and diisocyantes. They can be formed utilizing three building blocks, namely a polyol or long-chain diol, a chain extender or short-chain diol, and a diisocyanate. The derived multi-phase block copolymer has thermoplastic properties and is called thermoplastic PU (TPU). This modular approach allows for a variety of alternations yielding a broad range of structural properties and applications. TPUs are based on three main classes of polyols, i.e. polyethers, polyesters, and polycaprolactones. With these different polyols and the ability of changing the ratio of building blocks a variety of material properties can be obtained thus TPUs find numerous applications in e.g. lightweight construction1, insulation, flame retardants, lacquer and glue, as well as medicine. Linear, isocyanate terminated, polyurethane prepolymers prepared from non-equivalent amounts of diisocyanate such as methylene diphenyl diisocyanate (MDI) attached to a polyol are widely used as precursors of the correspondent polymers. Chain-extending reactions with low molecular weight compounds bearing different amounts of active hydrogens enable both linear and crosslinked polyurethane to be formed. Due to TPUs being used in a broad range of applications facing a variety of stress (e.g. mechanical, hydrolytic, thermal, radiative/UV, as well as its combinations) the complexity of possible degradation mechanism is high. A functional group derived from degradation of the bulk matrix can be detected utilizing a suited fluorogenic sensor molecule. There are several fluorogenic dyes known for the application as sensor for amine groups e.g. fluorescamine, pyrylium dyes, deriving a fluorescent signal upon reaction. T2 - ANAKON 2017 CY - Tübingen, Germany DA - 03.04.2017 KW - Bewitterung KW - Polyurethan KW - Functional group detection KW - Polyurethanes PY - 2017 AN - OPUS4-40262 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bayat, Mehmet Emin A1 - Nandayapa, Edgar R. A1 - Tiebe, Carlo A1 - Unger, Eva L. A1 - List-Kratochvil, Emil J. W. T1 - Raw data from: "An operando spectroscopic examination of the influence of trace humidity on interdigital back contact metal halide perovskite solar cells" N2 - Controlling trace humidity is vital for both the fabrication and long-term stability of metal halide perovskite (MHP) solar cells. Relevant humidity levels are typically below 10 ppmV, especially in glovebox-based processing and in well-encapsulated devices. Even minute amounts during fabrication can influence crystallization, introducing defects and lowering efficiency. Over time, humidity accelerates degradation of the perovskite layer and internal interfaces, ultimately reducing operational lifetime. Probing these effects at low concentrations under operando conditions is therefore essential for advancing device performance and durability. In this work, we employed a high-precision transfer standard dew point hygrometer to investigate humidity levels between 5 and 35 ppmV in non-encapsulated MHP solar cells. To permit unobstructed water migration during operation, we fabricated interdigital back contact devices. Operando measurements revealed water transport through the perovskite layer and enabled quantification of outgassing. Under trace-humidified conditions, devices exhibited initial charge-carrier quenching, followed by gradual recovery. Notably, the photocurrent response to humidified nitrogen demonstrated that the MHP layer behaves fully reversibly within the explored timescale and across the investigated humidity levels and conditions. These findings establish a systematic operando framework for examining extrinsic stressors in perovskites and highlight opportunities for assessing passivation strategies. KW - Metal halide perovskite PY - 2026 DO - https://doi.org/10.5281/zenodo.18600851 PB - Zenodo CY - Geneva AN - OPUS4-65757 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Hothan, Sascha A1 - Häßler, Dustin A1 - Stelzner, Ludwig A1 - Kremberg, Jan A1 - u. a., T1 - CO2 Einsparung durch Ressourceneffizienz als Folge von Materialsubstitution bei hochbeanspruchten Zuggliedern im Brückenbau - Netzwerkbogenbrücken mit Zuggliedern aus Carbon N2 - Für die hoch beanspruchten Zugglieder von Netzwerkbogenbrücken stellt der Einsatz von Carbonzuggliedern eine technisch innovative und vorteilhafte Lösung dar. Im Rahmen von ersten Pilotanwendungen konnte ein ausreichender Ermüdungswiderstand für den jeweiligen Einsatz nachgewiesen werden – der tatsächlich vorhandene Ermüdungswiderstand wurde bislang jedoch nicht erforscht. Die Aufgabenstellung des Verbundforschungsvorhabens umfasst die Gewinnung einer Datengrundlage für statistisch abgesicherte Bauteilkennlinien und Traglasten auf Grundlage von statischen Versuchen. Der Schwerpunkt liegt auf der Gewinnung einer Datengrundlage an realmaßstäblichen Bauteilversuchen unter Ermüdungsbelastung zur Bestimmung einer Ermüdungsversagensfunktion (S-N-Kurve), welche durch Kleinversuchsserien und faseroptische Messungen zur isolierten Betrachtung einzelner Einflussgrößen begleitet wurde. Direkt übertragbare Erkenntnisse zum Tragverhalten bei Brandbeanspruchung lagen ebenfalls nicht vor und sollten im Zuge von Bauteilversuchen unter Last und gleichzeitiger Brandbeanspruchung gewonnen werden zur Vergleichbarkeit des Verhaltens mit herkömmlichen Zuggliedern aus Stahl. Die Aufgabenstellung wurde in 9 Arbeitspaketen und insgesamt 29 Teilarbeitspaketen aufgegliedert. Diese beinhalten die Schaffung einer gemeinsamen Wissens- und Arbeitsbasis, die Erarbeitung von Versuchsparametern, die Planung und Herstellung der Versuchskörper und der Versuchsstände, statische Versuche, Ermüdungsversuche bis zum Bruch, Ermüdungsversuche mit Bestimmung der Resttragfähigkeit, Versuche zur Untersuchung des Tragverhaltens bei erhöhter Temperatur und Brandbeanspruchung bei simultaner mechanischer Zugbelastung, faseroptische Messungen und Kleinprobenversuche sowie die Zusammenführung und Auswertung der Ergebnisse. KW - Brandschutz KW - Carbon KW - Zugglied PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-657994 DO - https://doi.org/10.34657/32958 SP - 1 EP - 179 AN - OPUS4-65799 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Eggert, Lara A1 - Burkert, Andreas T1 - H2Mare-Projekt PtX-Wind - Untersuchung zu bauseitigen Fragestellungen der Korrosion und des Korrosionsschutzes mit Fokus auf die Außenkorrosion von Bau- und Anlagenteilen N2 - Im Teilvorhaben „Untersuchung zu bauseitigen Fragestellungen der Korrosion und des Korrosionsschutzes mit Fokus auf die Außenkorrosion von Bau- und Anlagenteilen“ standen korrosionstechnische Untersuchungen zum Einfluss maritimer Exposition für großtechnische Offshore-Power-to-X-(PtX-) Anlagen im Mittelpunkt. Die Planung und der Betrieb solcher OffshoreProzessanlagen stellen aufgrund der vorherrschenden Umweltbedingungen hohe Anforderungen an die Korrosionsbeständigkeit der eingesetzten Materialien, wobei dem wirksamen Korrosionsschutz eine zentrale Rolle für einen wartungsarmen, langlebigen und umweltverträglichen Anlagenbetrieb zukommt. Vor diesem Hintergrund wurde das Korrosionsverhalten metallischer Werkstoffe und Korrosionsschutzsysteme unter realen maritimen und Offshore-Bedingungen systematisch untersucht. Durch die Verknüpfung normativer und wissenschaftlicher Literaturrecherchen mit kontrollierten Laboruntersuchungen sowie mehrjährigen Expositionsversuchen an ausgewählten maritimen Standorten wurden grundlegende Zusammenhänge zwischen Umweltparametern, Werkstoffeigenschaften, konstruktiven Randbedingungen und Korrosionsmechanismen analysiert. Die gewonnenen Ergebnisse stellen eine repräsentative Datengrundlage zur Charakterisierung der Korrosivitätsbedingungen im maritimen Umfeld dar und bilden eine wissenschaftlich fundierte Basis für die Bewertung, Auslegung und Optimierung von Werkstoffen, Beschichtungen und Korrosionsschutzkonzepten für maritime und Offshore-Anwendungen. KW - Offshore-Power-to-X-Anlagen KW - Maritime Korrosion KW - Korrosionsschutz PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-657965 DO - https://doi.org/10.34657/32992 SP - 1 EP - 32 AN - OPUS4-65796 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kaminski, Katja A1 - Kluge, Stephanie A1 - Frenzel, Olivia A1 - Bücker, Michael A1 - Westphalen, Tanja ED - Ziegahn, Karl-Friedrich T1 - Entwicklung, Validierung und Anwendung eines beschleunigten Bewitterungsprotokolls zur Bewertung der Freisetzung von Bisphenol A (BPA) aus Polycarbonat (PC)-Materialien in die Umwelt N2 - BPA unterliegt einer kontinuierlichen behördlichen Kontrolle und ist als besonders besorgniserregender Stoff (SVHC) gelistet. Besondere Besorgnis besteht hinsichtlich seines häufigen Nachweises in Oberflächengewässern, obwohl es leicht biologisch abbaubar ist. In mehreren Studien wurden die Quellen und Wege von BPA in die Umwelt untersucht, wobei festgestellt wurde, dass seine Hauptverwendung als Monomer in PC nur marginal zu den BPA-Freisetzungen in die Umwelt über seinen Lebenszyklus beiträgt. Um die tatsächlichen Freisetzungen von BPA aus PC unter umweltrelevanten Bedingungen besser zu verstehen, wurde eine neu entwickelte Methodik (Bundesanstalt für Materialforschung und -prüfung, BAM) angewendet, die ein neuartiges beschleunigtes Bewitterungsprotokoll für Polycarbonat-Materialien in Kombination mit einem sensitiven Analysenverfahren umfasst, welches eine Bestimmung von BPA im Ultraspurenbereich ermöglicht. Das Bewitterungsprotokoll erreicht eine 13,6-fache Beschleunigung im Vergleich zu mitteleuropäischen Wetterbedingungen und simuliert Umweltstressoren (globale Strahlung, Regen, Temperaturschwankungen) in einer Bewitterungskammer, wobei gleichzeitig die BPA-Freisetzung mit einem validierten LC-MS/MS-Verfahren unter Verwendung einer organischen Isotopenverdünnungskalibrierung bestimmt wird. In parallelen Freilandversuchen wurden die Trübung und die Vergilbung („Yellowness-Index“) der zu untersuchenden Proben als Referenzparameter untersucht. T2 - 54. Jahrestagung der GUS 2026 CY - Blankenloch-Stutensee, Germany DA - 25.03.2026 KW - Polycarbonat KW - Bisphenol A KW - Bewitterung PY - 2026 SN - 978-3-9826129-3-5 VL - 54 SP - 139 EP - 153 AN - OPUS4-65793 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Burkert, Andreas A1 - Eggert, Lara T1 - H2Mare-Projekt TransferWind - Übertragung von wissenschaftlichen Erkenntnissen zur bauseitigen maritimen und offshore-Korrosion in die Normung und Erarbeitung einer Handlungsempfehlung zu Korrosionsschutz und -prüfung N2 - Die Werkstoffauswahl und der Korrosionsschutz zur Sicherstellung der Dauerhaftigkeit stellen für den Offshore Bereich noch immer eine Herausforderung dar. Erfahrungen und Regelwerke liegen insbesondere aus dem Bereich von Offshore Windenergieanlagen vor. Diese Regelwerke befinden sich in einem stetigen Prozess der Anpassung an aktuelle Erkenntnisse und Erfahrungen, da es sich noch um relativ neue Anwendungen handelt. Für Offshore-Prozessanlagen, wie diese im H2Mare-Projekt betrachtet werden, sind die Anforderungen wesentlich komplexer, da Anlagenkomponenten den Beanspruchungen aus den Prozessen im Inneren der Anlagen ebenso genügen müssen, wie den Beanspruchungen aus der maritimen Umgebung. Hier kommen im Vergleich zu Windkraftanlagen eine größere Palette von Werkstoffen insbesondere aus dem Bereich der rost- und säurebeständigen Stähle sowie höhere Prozesstemperaturen zum Tragen, die für Windkraftanlagen keine Relevanz haben. KW - Offshore-Power-to-X-Anlagen KW - Maritime Korrosion KW - Korrosionsschutz PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-658008 DO - https://doi.org/10.34657/32991 SP - 1 EP - 25 AN - OPUS4-65800 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -