TY - CONF A1 - Olbricht, Jürgen A1 - Bismarck, Marc A1 - Skrotzki, Birgit T1 - Size effects in miniature specimen creep testing of heat resistant ferritic-martensitic steels N2 - The use of miniaturized specimen geometries in mechanical testing allows extracting the sample material directly from the sidewall of critical components of power plants, like e.g. headers and steam pipes. In this way, both the impacts of the processing of the component (including all shaping and tempering influences) and of the exposure to the complex aging/loading/oxidation conditions in the plant (in case of post-Service tests) can be analyzed and representative mechanical properties are obtained. T2 - CREEP 2015 - 13th International conference on creep and fracture of engineering materials and structures CY - Toulouse, France DA - 31.05.2015 PY - 2015 SP - 163 EP - 164 AN - OPUS4-33528 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias A1 - Wolff, Dietmar ED - Van Breugel, K. ED - Koenders, E.A.B. T1 - Approach for the investigation of long-term behaviour of elastomeric seals for transport and storage packages N2 - Elastomers are widely used as main sealing materials for Containers for low and intermediate Ievel radioactive waste and as additional component to metal seals in spent fuel and high active waste Containers. According to appropriate guidelines and regulations safe enclosure of the radioactive Container contents has to be guaranteed for long storage periods as well as down to temperatures of -40 °C for transportation. Therefore the understanding of seal behaviour in general is of high importance and ageing of elastomeric seals has to be considered with regard to possible dynamic events taking possibly place during transport after storage. T2 - 1st Ageing of materials & structures 2014 conference CY - Delft, The Netherlands DA - 26.05.2014 KW - O-Ring KW - Seal KW - Ageing KW - Elastomer KW - Compression set PY - 2014 SN - 978-94-6186-313-3 SP - 87 EP - 93 AN - OPUS4-30820 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias A1 - Wolff, Dietmar A1 - Stark, Wolfgang A1 - Völzke, Holger T1 - Investigation of elastomer seal behavior for transport and storage packages N2 - Rubbers are widely used as main sealing materials for containers for low and intermediate level radioactive waste and as additional component to metal seals in spent fuel and high active waste containers. According to appropriate guidelines and regulations safe enclosure of the radioactive container contents has to be guaranteed for long storage periods as well as down to temperatures of -40 °C for transportation. Therefore the understanding of seal behavior is of high importance. In this paper we focus on the behavior of elastomer seals at low temperatures with regard to poten-tial decrease of leak-tightness. In addition, changes in material properties due to aging effects over long periods of time and their influence on the seal performance is investigated. It is known that material properties of rubbers are strongly temperature dependent. At low tempera-tures this is caused by the rubber-glass transition (abbr. glass transition). During continuous cool-ing, the material changes from rubber-like entropy-elastic to stiff energy-elastic behavior, that al-lows nearly no strain or retraction due to the glass transition. Hence rubbers are normally used above their glass transition but the minimum working temperature limit is not defined precisely. Aging of elastomer seals is important, as possible dynamic loads may have to be considered during the whole interim storage period (so far approved in Germany for up to 40 years) and for transporta-tion after storage. For the investigations, fluorocarbon (FKM) and ethylene-propylene-diene (EPDM) rubbers were selected as they are often used in radioactive waste containers. Some materials were purchased from a commercial seal producer and some materials were compounded and cured at BAM. The elastom-ers where studied by several thermo-analytical methods and compression set to characterize the material behavior at low temperatures. Additionally component tests were performed to determine the breakdown temperature of the sealing function of complete elastomer O-rings. T2 - PATRAM 2013 - 17th International symposium on the packaging and transportation of radioactive materials CY - San Francisco, CA, USA DA - 18.08.2013 PY - 2013 SP - Paper 227, 1 EP - 8 PB - Omnipress AN - OPUS4-30377 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias A1 - Wolff, Dietmar A1 - Stark, Wolfgang T1 - Investigating low temperature properties of rubber seals N2 - To achieve the required tightness levels of Containers for low and intermediate level radioactive wastes rubbers are widely applied as main sealing materials. The save encapsulation of the radioactive Container contents has to be guaranteed according to legislation and appropriate guidelines for long storage periods as well as down to temperatures of-40 °C during transportation. Therefore the understanding of failure mechanisms that lead to leakage at low temperatures is of high importance. It is known that the material properties of rubbers are strongly influenced by temperature. At low temperatures this is caused by the rubber-glass transition (abbr. glass transition). During continuous cooling the material changes from rubber-like entropy-elastic to stiff energy-elastic behaviour, that allows nearly no strain or retraction. Therefore, rubbers are normally used above their glass transition but the minimum working temperature limit is not defrned precisely, what can cause problems during application. The temperature ränge where full functionality is possible is strongly dependent on the application conditions and the material. For this investigation mainly ethylene propylene diene (EPDM) and fluorocarbon rubbers (FKM) were selected as they are often used for radioactive waste Containers. Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA) are typically used for the determination of the temperature ränge of the glass transition process. The standardized compression set measurement according to ISO 815 is common for investigation of rubber sealing materials as the test simulates the seal behaviour after release. To reduce the test time of the Standard tests a faster technique giving the same information was developed. Additionally, the breakdown temperature of the sealing function of complete O-ring seals is measured in a component test Setup to compare it with the results of the other tests. The experimental Setup is capable of measuring the leakage rate at low temperatures by the pressure rise method. A model was developed that allows calculating the minimum working temperature limit of a seal by combining the results of the applied methods. T2 - WM2013 Conference CY - Phoenix, Arizona, USA DA - 24.02.2013 PY - 2013 SN - 978-0-9836186-2-1 SP - 1 EP - 12 CY - Phoenix, Arizona, USA AN - OPUS4-28853 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grelle, Tobias A1 - Wolff, Dietmar A1 - Probst, Ulrich A1 - Jaunich, Matthias A1 - Völzke, Holger T1 - Component and material investigations on metal seals for high level radioactive waste containers N2 - In Germany casks for interim storage of spent nuclear fuel and high level radioactive waste are equipped with Helicoflex® metal seals as main sealing barrier of the double lid system. The long-term behaviour of those seals is investigated at Bundesanstalt für Materialforschung und –prüfung (BAM) in order to evaluate the safety function of the containment at different temperatures over storage periods of 40 years or more in case extended interim storage becomes necessary. Long-term investigations have been done for ageing times of up to 8.5 years at temperatures ranging from room temperature to 150 °C. It was found that the seal force and useable resilience decrease over time, which is mainly caused by creep deformation of the aluminium (or silver) outer jacket of the seals. This effect becomes stronger with increasing temperature. The ageing processes of the seal material and the overall seal behaviour is under investigation in order to derive analytical descriptions for the long-term seal performance. Thus, standardized tests on the basic seal materials, with focus on aluminium, and additional investigations on the seals as a component are conducted. The current investigations include compression and tension creep measurements as well as tensile testing. Furthermore, ageing of seal segments provides information on the development of the contact area width, jacket thickness and microstructural changes in dependence of time and temperature. The obtained data are used for the development of material models and an analytical approach to describe and predict the time and temperature dependent sealing behaviour in the long-term. T2 - 11th International Conference on the Transport, Storage and Disposal of Radioactive Materials CY - London, UK DA - 15.05.2018 KW - Metal seal KW - Creep KW - Long-term behavior PY - 2018 SP - 18535, 1 EP - 6 AN - OPUS4-45452 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wolff, Dietmar A1 - von der Ehe, Kerstin A1 - Jaunich, Matthias A1 - Böhning, Martin T1 - Performance of neutron radiation shielding material (U)HMW-PE influenced by gamma radiation N2 - Due to their extreme high hydrogen contents high molecular weight (HMW-) and ultra-high molecular weight (UHMW-) polyethylene (PE) are a comprehensible choice as neutron radiation shielding material in thick walled metallic casks for storage and transport of radioactive materials. For this application it has to be taken into consideration that gamma radiation – that is a direct consequence of inserting radioactive material in such casks – has a high influence on the molecular structure of polyethylene. In order to be applicable for long-term neutron radiation shielding purposes during the whole storage period (in Germany for instance up to 40 years) PE has to withstand any type of degradation affecting safety relevant aspects. The scope of our work comprises an estimation of the influence of gamma radiation and temperature on the molecular and supra molecular structure of (U)HMW-PE used as cask components for neutron radiation shielding. Therefore it was investigated to what extent these changes are detectable by a combination of conventional polymer characterization techniques such as Differential Scanning Calorimetry (DSC), Thermo Mechanical Analysis (TMA), Dynamic Mechanical Analysis (DMA), and Thermo Gravimetric Analysis (TGA). Additionally optical (FTIR) and weighing methods were applied. For UHMWPE the results are compared with those published for similar UHMW-PE material that is used in medical technology. For this application, gamma irradiation is applied deliberately for purposes such as sterilization and crosslinking, the latter leading to partial improvement of mechanical properties and better chemical stability. As a result the so far observed structural changes of the irradiated material are not safety relevant for the application of polyethylene as neutron shielding material; moreover, some properties actually improve via irradiation. T2 - PSAM 11 ESREL 2012 - 11th International probabilistic safety assessment and management conference & The annual european safety and reliability conference CY - Helsinki, Finland DA - 25.06.2012 KW - (U)HMW-PE KW - Gamma irradiation KW - Shielding material KW - Cask for storage and transport of radioactive materials PY - 2012 SP - 1 EP - 8 AN - OPUS4-26176 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Shirai, K. A1 - Namba, K. A1 - Wataru, M. A1 - Völzke, Holger A1 - Wolff, Dietmar A1 - Probst, Ulrich A1 - Jaunich, Matthias A1 - Schulz, Sebastian T1 - Numerical evaluation of the long-term sealing performance of the silver gasket for dual purpose metal cask under high temperature N2 - It is important to evaluate the effect of thermal ageing on the sealing performance of metal gaskets under high temperature for long-term usage. Therefore, in order to gain representative data for this kind of metal-sealed lid System, BAM is currently performing laboratory tests of different gasket types with aluminum and silver jackets at three different temperatures under static conditions up to four years so far, using test flanges for gaskets with full scale cross section diameter but much smaller outer diameter. On the other hand, in order to investigate the applicability of the numerical methodology to evaluate the long-term behavior of the metal gaskets, such as a correlation between seal pressure force and holding time, CRIEPI is developing a modeling method including material tests (tensile and creep tests) at high temperature. In this paper, the applicability of the finite element method (ABAQUS) to predict the recovery displacement and residual seal pressure force of the gasket complex was verified by comparing the calculated values with BAM’s laboratory test results under the joint research agreement between BAM and CRIEPI. T2 - PATRAM 2013 - 17th International symposium on the packaging and transportation of radioactive materials CY - San Francisco, CA, USA DA - 18.08.2013 KW - Metal seals KW - Extended storage KW - Long-term storage KW - Dual purpose cask PY - 2013 SP - 1 EP - 8 PB - Omnipress AN - OPUS4-31947 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias A1 - Grelle, Tobias A1 - Wolff, Dietmar T1 - Influence of partial release on sealing performance of elastomer O-rings at low temperatures N2 - For many sealing applications rubbers are applied due to their special material properties and easy use. In many applications as e.g. in aviation, traffic or process technology the material can be exposed to low temperatures during operation. Therefore it is important to know the material behaviour at those low temperatures to determine the temperature range that allows a safe operation of the seal. As rubbers are used as main sealing materials for containers for low and intermediate level radioactive waste and as additional component to metal seals in spent fuel and high acitve waste containers, a comprehensive elastomer investigation program is run at BAM. This program comprises investigations of elastomer overall performance, durability, influence of gamma irradiation and low temperature behaviour. In this paper we focus on the behaviour of elastomer seals below ambient temperatures after a fast partial release. Despite the primarily static application conditions of many seals their behaviour after partial compression release is of interest with regard to potential decrease of leak-tightness. For this investigation a special setup was designed which allows the partial release of compressed seal systems at different temperatures accompanied by leakage rate measurements. The results for FKM seals are presented and discussed. T2 - Technomer 2015 - 24. Fachtagung über Verarbeitung und Anwendung von Polymeren CY - Chemnitz, Germany DA - 12.11.2015 KW - O-ring KW - Glass-rubber transition KW - Compression set KW - Partial release PY - 2015 SN - 978-3-939382-12-6 SP - P 3.7, 1 EP - 6 CY - Chemnitz AN - OPUS4-35130 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rockenhäuser, Christian A1 - von Hartrott, P. A1 - Metzger, M. A1 - Skrotzki, Birgit T1 - Comparison of S-phase coarsening in alloy 2618A during ageing, creep, and fatigue N2 - The coarsening of S-phase precipitates in alloy 2618A was compared for different ageing conditions (heat treatment, creep, and fatigue). T2 - LightMAT 2017 CY - Bremen, Germany DA - 08.11.2017 KW - Alloy 2618A KW - Degradation KW - Coarsening KW - S-phase KW - Dark-field transmission electron microscopy (DFTEM) PY - 2017 SP - 1 EP - 3 AN - OPUS4-42837 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rockenhäuser, Christian A1 - Skrotzki, Birgit T1 - Microstructure evolution in a 2618A aluminium alloy during ageing N2 - The aluminium alloy 2618A is an Al-Cu-Mg alloy which is part of the 2xxx series of age-hardenable alloys. These materials are designed for long-term Operation in transportation and aerospace industries. The desired properties, e.g. creep behavior, hardness, and damage tolerance, are controlled by the distribution of fine precipitates formed within the matrix. However, the strength of the material declines du ring exposition to elevated temperatures due to the overageing of the S-phase precipitates (AI2CuMg) and the conversion of the S-phase into the stable equilibrium S-phase. A quantitative model of the overageing process at application relevant temperatures would be desirable for accurate predictions of component lifetime made from the 2618A alloy. T2 - MC 2015 - Microscopy conference CY - Göttingen, Germany DA - 06.09.2015 KW - Aluminium alloys KW - Transmission electron microscopy KW - Microstructure KW - Coarsening PY - 2015 SP - MS4.P078, 150 EP - 151 AN - OPUS4-34304 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rehmer, Birgit A1 - Finn, Monika A1 - Uhlemann, Patrick A1 - Skrotzki, Birgit A1 - Scheuerlein, C. ED - Frenz, H. ED - Langer, B. T1 - Vergleichende Bewertung verschiedener Verfahren der E-Modulbestimmung für metallische Werkstoffe N2 - Für numerische Beanspruchungs- und Lebensdaueranalysen ist die Kenntnis des E-Moduls der eingesetzten Werkstoffe von zentraler Bedeutung. Für seine experimentelle Bestimmung wurden eine Vielzahl von Verfahren entwickelt, die zum Teil werkstoffspezifisch Eingang in die Normung gefunden haben. Prinzipiell können diese Verfahren in zwei Gruppen eingeteilt werden - die statischen und die dynamischen Prüfverfahren. Während die statischen Verfahren auf der direkten Messung des Spannungs-Dehnungs-Zusammenhangs während einer Belastung im elastischen Verformungsbereich beruhen (Zug-, Biege- bzw. Druckversuch) nutzen die dynamischen Verfahren die Analyse der resultierenden Schwingungen nach einer entsprechenden Anregung eines Prüfkörpers (Resonanz- bzw. Impulsanregungsmethode). Für verschiedene Werkstoffe wurden statische und dynamische Verfahren zur E-Modulbestimmung eingesetzt. Die Unterschiede und Vorteile der verschiedenen Verfahren werden vergleichend diskutiert. T2 - Tagung Werkstoffprüfung 2017 CY - Berlin, Germany DA - 30.11.2017 KW - E-Modul KW - Zugversuch KW - Druckversuch KW - Resonanzmethode KW - Impuls-Anregungsmethode PY - 2017 SN - 978-3-9814516-7-2 SN - 1861-8154 SP - 217 EP - 224 PB - Deutscher Verband für Materialforschung und -prüfung CY - Berlin AN - OPUS4-43255 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jürgens, Maria ED - Skrotzki, Birgit ED - Olbricht, Jürgen T1 - Creep fatigue behavior of P91/P92 N2 - 9-12% Cr ferritic-martensitic stainless steels are widely used as high temperature construction materials in power plants due to their excellent creep resistance and good oxidation resistance. Creep resistance is considered as the primary parameter in material selection for base-load power plants, but the growing share of renewable energy sources in power generation forces many installations into more "flexible" operation with frequent load reductions and shutdowns. Under cyclic operation of power plants, temperature gradients occur especially in thick-walled components. Locally, these gradients lead to complex time- and temperature-dependent loading scenarios which may result in superimposed creep deformation/damage, creep-fatigue and thermo-mechanical fatigue. The combination of different damage processes may seriously reduce the lifetimes of respective components. A fundamental understanding of the damage evolution in ferritic-martensitic steels under combined static and cyclic loading is therefore required. In the present contribution, the creep-fatigue behavior of two different 9% Cr steel grades (P91 and P92) was investigated. Standard creep-tests as well as LCF/TMF tests with hold time have been carried out to study the material behavior of the new loading scenarios. Microstructural investigations help to identify the observed deformation characteristics and the dominating damage mechanisms under different loads. The test programme is complemented by cyclic creep-tests (temperature change) and creep-tests under atmospheres. In a next step, the experimental results will be used for parameter identification of a deformation and lifetime model to predict the material behavior. T2 - ECCC 2017 CY - Düsseldorf, Germany DA - 10.09.2017 KW - Near-service testing KW - Power plant KW - Ferritic-martensitic steels KW - P91 KW - P92 KW - Creep-Fatigue PY - 2017 SN - 978-3-514-00832-8 SP - 1 EP - 5 AN - OPUS4-42270 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zaghdoudi, Maha A1 - Kömmling, Anja A1 - Jaunich, Matthias A1 - Wolff, Dietmar A1 - Albouy, P.-A. A1 - Häcker, Ralf A1 - Stock, Daniel T1 - Overview of ongoing research and future prospects on polyethylene neutron shielding materials at bam N2 - The extension of the interim storage period of radioactive waste before disposal will cause additional challenges for the nuclear waste management in Germany, so that an extensive knowledge of the long-term performance of casks, including their components and inventories, will be required for future extended storage licenses. Ultra-high and high molecular weight polyethylenes ((U)HMW-PE) are used for neutron shielding purposes in casks for storage and transport of spent fuel and high-level waste due to their extremely high hydrogen content. During their service life of several decades as cask components, the PE materials are exposed to neutron and gamma radiation from the radioactive inventory of the casks, mechanical assembling stresses and temperature. All these combined effects affect the material properties of such components which in turn may be crucial for some possible accident scenarios. At the Bundesanstalt für Materialforschung und -prüfung (BAM), the effects of high temperature exposure in combination with subsequent or previous irradiation were investigated with a comprehensive aging program including thermal aging at 125 °C for different aging periods up to 5 years and irradiation with doses ranging from 50 to 600 kGy. This contribution provides an overview of the ongoing research related to the structural changes of (U)HMW-PE induced by gamma irradiation and high temperature exposure and focuses on current research perspectives at BAM with regard to the prediction of the dynamic behavior of the material during extended interim storage in case of an accident scenario. First results of the coupled effect of temperature, radiation and mechanical loading will be presented. The effect of microstructural changes induced by gamma irradiation and high temperature on the mechanical behavior of (U)HMW-PE will be assessed. T2 - PATRAM22 CY - Juan-Les-Pins, Antibes, France DA - 11.06.2023 KW - (U)HMWPE KW - Ageing KW - Irradiation KW - WAXD KW - SHPB PY - 2023 SP - 1 EP - 10 AN - OPUS4-57707 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Olbricht, Jürgen A1 - Agudo Jácome, Leonardo A1 - Jürgens, Maria A1 - Roohbakhshan, Farshad A1 - Fedelich, Bernard A1 - Skrotzki, Birgit T1 - Cyclic loading performance and related microstructure evolution of ferritic-martensitic 9-12% Cr steels N2 - The current competitive situation on electricity markets forces power plants into cyclic operation regimes with frequent load shifts and starts/shutdowns. In the present work, the cyclic mechanical behavior of ferritic-martensitic 9-12 % Cr steels under isothermal and thermomechanical loading was investigated for the example of grade P92 material. A continuous softening was observed under all loading conditions. The introduction of hold periods to the applied cycles reduced material lifetime, with most prominent effects at technologically relevant small strain levels. The microstructural characterization reveals a coarsening of the original “martensitic” lath-type microstructure to a structure with polygonal subgrains and reduced dislocation density. The microstructural data forms the input for a physically-based modelling approach. T2 - 44th MPA-Seminar CY - Leinfelden/Stuttgart, Germany DA - 17.10.2018 KW - Ferritic-martensitic steels KW - Cyclic loading KW - Microstructure evolution PY - 2018 SP - 259 EP - 265 AN - OPUS4-47118 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hodoroaba, Vasile-Dan A1 - Yamamoto, K. A1 - Grulke, E. A. A1 - Maurino, V. ED - Bosse, H. ED - Buhr, E. ED - Dziomba, T. ED - Hodoroaba, Vasile-Dan ED - Klein, T. ED - Krumrey, M. T1 - Shape controlled TiO2 nanoparticles as candidates for nano-CRM’s – an ISO case study N2 - Extraction of true, 3D shape (and size) of non-spherical nanoparticles (NPs) is associated with Errors by conventional 2D electron microscopy using projection images. Significant efforts within the ISO technical committee TC 229 ‘Nanotechnologies’ are aimed at establishing accurate TEM and SEM measurement of NP size and shape as robust, standard procedures. Study groups have been organizing inter-laboratory comparisons on well-selected NP systems according to the market needs, such as aggregated titania nano-powder for which size and shape distribution of primary crystallites of irregular shape must be measured accurately. To be noticed is e. g. the fact that the measurement procedure allows only manual selection of the particles clearly distinguishable for analysis as well as manual definition of the contour of the imaged NPs. An inter-laboratory exercise on titania NPs (pure anatase, grown by hydrothermal synthesis) of well-defined non-spherical shape, i.e. bipyramidal, has been recently started within ISO/TC 229 under similar conditions as for the irregular shaped titania. In the TEM micrograph the particles tracked manually according to the measurement protocol. Overlapped particles were allowed to be considered, as long as they are clearly distinguishable. One decisive NP selection criterion was to analyze only those NPs with a roundness value below 0.7, i.e. the NPs laying on the support foil and, hence, with projection areas clearly deviating from perfect circles (R=1). The overall evaluation (for 15 labs) of the size descriptors (area, Feret, minFeret, perimeter) and shape descriptors (aspect ratio, roundness, compactness, extent) by analysis of variance is just to be finished and included in ISO/WD 21363 Nanotechnologies -- Protocol for particle size distribution by transmission electron microscopy. T2 - NanoWorkshop 2018: Workshop on Reference Nanomaterials CY - Berlin, Germany DA - 14.05.2018 KW - Titanium dioxide KW - Nanoparticles KW - Shape-controlled KW - Electron microscopy PY - 2019 SN - 978-3-95606-440-1 DO - https://doi.org/https://doi.org/10.7795/110.20190412 SN - 0179-0609 VL - F-61 SP - 245 EP - 255 PB - Physikalisch-Technische Bundesanstalt CY - Braunschweig und Berlin AN - OPUS4-49990 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Olbricht, Jürgen A1 - Bismarck, Marc A1 - Skrotzki, Birgit T1 - Charakterisierung des Kriechverhaltens hochwarmfester Stähle durch Versuche an Miniaturproben N2 - Die Einsatzbedingungen der Bauteile von fossil befeuerten Kraftwerken unterliegen derzeit durch aktuelle Entwicklungen des Energiesektors (Stichwort „Energiewende“) erheblichen Veränderungen. Während das Interesse an einer weiteren Steigerung der Wirkungsgrade und den damit verbundenen Erhöhung der Prozessdrücke und -temperaturen prinzipiell anhält, werden parallel neue Verbrennungsprozesse wie z. B. die Oxyfuelverbrennung diskutiert und die Einsatzmöglichkeiten von Ersatzbrennstoffen wie Biomasse und hochkalorischen Müllfraktionen werden untersucht. Während diese Maßnahmen über veränderte Rauchgaszusammensetzungen ggf. zu einem generell verstärkten Hochtemperaturkorrosions-Angriff der Bauteile führen, zwingt der Ausbau der Stromerzeugung auf Basis von Wind- und Sonnenenergie die Anlagenbetreiber gleichzeitig zu einer lastflexiblen Anlagenfahrweise mit häufigen Warm- und Kaltstarts bei möglichst hohen Lastgradienten. Diese veränderten Betriebsbedingungen stellen eine Herausforderung für die Überwachung und Instandhaltung bestehender Kraftwerke sowie für die Konstruktion neuer Anlagen und Komponenten dar. N2 - Miniaturized specimen geometries in mechanicai testing allow extracting the sample material directly from critical components of power plants. In this way, both the Impacts of manufacturing and of the complex aging/loading/oxidation conditions during Service on life consumption are captured and representative mechanicai properties are obtained. In the present contribution, example results of a comparative creep/creep rupture study on P91 tempered martensite ferritic Steel, involving cylindrical Standard and miniature specimens (diameter 3 mm), are presented. The test results of miniature specimens exhibit all characteristic creep features of tempered martensite ferritic steels, and realistic stress and temperature dependences are obtained which correspond well to literature data. However, direct comparison with large scale specimen data reveals small but systematic variations in minimum creep rates, elongations at fracture and times to rupture. These differences are discussed in the light of literature findings on specimen size influences in other heat resistant alloys. Size effects need to be considered for a correct interpretation of results from miniature specimen creep tests. T2 - Langzeitverhalten warmfester Stähle und Hochtemperaturwerkstoffe - Beiträge zur 37. Vortragsveranstaltung der Arbeitsgemeinschaft für warmfeste Stähle und Hochtemperaturwerkstoffe CY - Düsseldorf, Germany DA - 28.11.2014 PY - 2014 SP - 106 EP - 116 AN - OPUS4-32402 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias A1 - Goral, Milan A1 - Sagradov, Ilja A1 - Wolff, Dietmar A1 - Völzke, Holger T1 - Aging investigations of metal seals used in containers for interim storage of spent fuel N2 - For bolted casks for used fuel and high level waste the sealing system has an important impact of ensuring safe enclosure of the inventory The used metal seals show some changes over time which have been addressed for nearly 15 years in running experiments at BAM The observed changes are temperature de pendent and therefore it is expected that test s at higher temperature allow for an acceleration of the effects and ideally the proposal of an ageing model covering the expected time of use . Nevertheless, questions concerning the influence of the experimental approach on the results and effects taking place at the initial days of ageing remain. To address these a new project was launched to give a better understanding of the seal behavior. T2 - PVP2024, Pressure Vessels & Piping Conference CY - Bellevue, WA, USA DA - 29.07.2024 KW - Metal seal KW - Aging KW - Interim storage PY - 2024 SN - 978-0-7918-8851-3 SP - 1 EP - 4 PB - ASME AN - OPUS4-61357 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hartelt, Manfred A1 - Wäsche, Rolf A1 - Hodoroaba, Vasile-Dan T1 - Verschleißpartikel-Analyse mit Rasterelektronenmikroskopie und energiedispersiver Röntgenspektrometrie im Transmissionsmodus (TSEM/EDX) N2 - Untersucht wurden Verschleißpartikel als elektronen-transparente Proben auf dünnen Trägerfolien mit einem hochauflösendem Rasterelektronenmikroskop und energiedispersiver Röntgenspektrometrie im Transmissionsmodus. Die hohe laterale Auflösung dieser modernen Methoden ermöglicht eine morphologische Charakterisierung der Verschleißpartikel bis in den nm-Bereich. Die hochauflösende Elementanalyse erlaubt eine Interpretation der Zusammensetzung und damit Rückschlüsse auf die Verschleißpartikelbildung. Die tribologischen Untersuchungen sind an einem Modell-Verschleißtribometer nach DIN 51834-2 geschmiert, aber ohne Ölkreislauf, durchgeführt worden. Die Präparation der Verschleißpartikel über eine Entnahme und Übertragung einer geringen Schmierstoffmenge mit einer Mikropipette auf eine TEM-Trägerfolie ist mit einem geringen Aufwand möglich. Der präparative Aufwand ist relativ gering. Das benötigte Schmierstoffvolumen beträgt wenige Mikroliter (0,001ml). Die Untersuchung zeigt die geringe geometrische Größe der Verschleißpartikel und bestätigt indirekt die These der Reaktionsschichtbildung mit einer geringen Schichtdicke, die ständig verschleißt und sich stetig neu bildet. Die beschriebenen Verschleißprozesse sind in der Modell-Verschleiß-Prüfung mit sehr hohen Pressungen am Versuchsbeginn nachweisbar. T2 - 55. Tribologie-Fachtagung - Reibung, Schmierung und Verschleiß - Forschung und praktische Anwendungen CY - Göttingen, Germany DA - 22.09.2014 PY - 2014 SN - 978-3-00-046545-1 VL - I SP - 05/1 EP - 05/10 AN - OPUS4-31528 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bertovic, Marija T1 - Human-Related Risks in the Non-Destructive Testing (NDT) of Hollow Railway Axles: Implications for the Education and Training of the NDT Personnel N2 - Non-destructive testing (NDT) is a major contributor to the safe railway operation. Even though NDT reliability in railway maintenance is affected by human factors, there are only just a few studies published in this field so far. Education and training of the NDT personnel are some of the most important drivers of safe and reliable NDT. Continuously improving current practices and tools used for educational purposes can be achieved not only through technical con¬tent, but also through the attention to human factors. The aim of this study was to deepen the understanding of possible human-related risks in the manual ultrasonic inspection of the hollow railway axles and to suggest measures to improve the education and training of the NDT person¬nel. This was achieved by means of Failure Modes and Effects Analysis (FMEA) carried out with eight NDT experts and by a survey of 27 experienced inspectors. The results show that failures can happen throughout the entire NDT process. Prevention of those failures could be improved through the optimization of the organization, technology, documentation and regulations, working conditions and the general process, and through the optimization of the formal education and training. Specialized training of the executives, extended training of the supervisors and the inspectors and improvement of the inspection documentation have been suggested. The study also showed potential for the improvements of the inspection in the field. T2 - 29th European Safety and Reliability Conference CY - Hannover, Germany DA - 22.09.2019 KW - Human Factors KW - Non-Destructive Testing KW - NDT KW - Education KW - Training KW - Failure Modes and Effects Analysis KW - Railway KW - Axle Inspection KW - Ultrasonic Testing KW - Reliability PY - 2019 SN - 978-981-11-2724-3 DO - https://doi.org/10.3850/978-981-11-2724-3_1058-cd SP - 294 EP - 300 PB - Research Publishing CY - Singapore AN - OPUS4-49733 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias A1 - Hagenow, Peter A1 - Kasparek, Eva Maria A1 - Kömmling, Anja A1 - Noack, Volker A1 - Völzke, Holger A1 - Wolff, Dietmar T1 - Requirements for the use of elastomer seals in casks for final disposal of low and intermediate level waste N2 - Elastomer seals are widely used as barrier seals in containers for low and intermediate level radioactive waste and in some countries for spent fuel transportation casks. Depending on the area of use, the rubber materials have to demonstrate proper sealing performance with regard to mechanical, thermal and environmental conditions as well as irradiation during the entire operation period. In Germany the low and intermediate level radioactive waste is planned to be disposed in the Konrad repository in standardized containers. Many of these containers use an elastomer seal between lid and container body. Depending on the radiactive inventory and a possible containment of the waste in inner barrels and/or concrete structures, such containers may require a specific leak tightness. In such cases, specified leakage rates are shall not be exceeded by the the seals to keep potential activity releases from the inventories well below defined limits. Generally, all waste containers have to fulfill the waste acceptance criteria for the Konrad repository as defined by the reports BfS SE-IB-29/08 and SE-IB-30/08. From these criteria several requirements for seal performance are derived. The seals have to: - ensure full functionality until final container disposal, - maintain its function in case of a thermal or mechanical accident, - ensure encapsulation also at -20 °C. This combination of requirements is challenging especially as a seal exchange, which is typical for many other applications, is hardly possible and thus a sound understanding of how to perform safety evaluation of containers is required. Therefore BAM has initiated investigations on elastomer seal behaviour. This work focuses on low temperature behaviour and sealing performance concerning static conditions as well as partial loss of compression and ageing of elastomer seals. Concerning ageing, property changes caused by long-term thermooxidative conditions as well as gamma irradiation are investigated. This contribution presents an overview and explanation of the aims of the ongoing research and gives an update of the most relevant results. T2 - 13th Internationales Symposium "Konditionierung radioaktiver Betriebs- und Stillegungsabfälle CY - Dresden, Germany DA - 22.03.2017 KW - Disposal KW - Konrad repository KW - Seal PY - 2017 SP - 595 EP - 601 AN - OPUS4-39870 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -