TY - CONF A1 - Buchheim, Janine A1 - Recknagel, Christoph A1 - Wolter, Patrick A1 - Kittler-Packmor, Kai T1 - A new approach towards scientific evaluation and performance-related design of bituminous joint sealing materials and constructions N2 - While there is a permanent improvement of concrete pavement mixtures and pavement construction types over the last decades, the state-of-the-art joint sealing materials and joint constructions seem to stagnate on an antiquated empirical level. This status has been reaffirmed in the latest European standard. The consequences in the motorway network due to unsatisfying capability and durabilty of joint sealing systems are unacceptable. In addition, inadequate traffic performance (noise emissions, roll-over comfort) and traffic safety losses in the joint area of concrete pavements are existing challenges. These deficits and weaknesses reflect a demand for joint sealing materials and constructions whose approval requirements take functional aspects into account. Furthermore a sufficient analysis of decisive loads and a practice-oriented method to evaluate the requirements towards performance and durability is still missed. In this contribution decisive loads to German highways are analyzed. The design of test specimen for representative functional testing of joint sealing systems is discussed. The focus is on the geometry of the test specimens and the used concrete mixture. Finally, a new approach for a function-orientated test concept that considers representative load functions is presented. The potential of this approach to validate the durability and capability of various joint sealing systems is also presented using an example. T2 - RILEM International Symposium on Bituminous Materials CY - Online meeting DA - 08.06.2020 KW - Joint sealing KW - Expansion joint KW - Performance testing KW - Capability KW - Durability PY - 2020 SN - 978-3-030-46454-7 VL - 27 SP - 1 EP - 6 PB - Springer Nature AN - OPUS4-53488 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Nietzke, Jonathan A1 - Mente, Tobias A1 - Kannengießer, Thomas T1 - Diffusionsmessungen in UP-Mehrlagenschweißgut als effektives Tool gegen verzögerte Kaltrissbildung in Dickblechschweißungen N2 - Offshore-Windenergieanlagen bilden einen zentralen Bestandteil der zukünftigen Energieerzeugung. Hierzu notwendige Gründungs- und Turmstrukturen werden vorrangig aus UP-geschweißten Blechen aus hochfesten niedriglegierten Stählen mit Dicken bis zu 200 mm hergestellt. Die großen Blechdicken begünstigen hohe Schweißeigenspannungen und lange Diffusionswege für z. B. über den Schweißprozess eingebrachten Wasserstoff. Damit steigt das Risiko für eine wasserstoffunterstützte Kaltrissbildung (WKB) an. Zum sichereren Ausschluss von WKB in den geschweißten Komponenten wird in Abhängigkeit der Nahtgröße, Wärmeeinbringung und Stahlsorte eine Mindestwartezeit (MWZ) von bis zu 48 h empfohlen, bevor die zerstörungsfreie Prüfung durchgeführt wird. Es ist allerdings offen, ob die empfohlene MWZ zu konservativ ist. Einflüsse sind hier bspw. die schwierige Bewertung des Wasserstoffdiffusionsverhaltens im heterogenen UP-Mehrlagen-Schweißgut (SG) im Vergleich zum Grundwerkstoff (GW). Zudem sind nur sehr begrenzt H-Diffusionskoeffizienten für UP-Mehrlagen-SG als Grundlage zur Abschätzung des Zeitintervalls einer möglichen verzögerten Kaltrissbildung (somit MWZ) oder auch für Nachwärmprozeduren zur Wasserstoffreduktion (keine MWZ) verfügbar. Verlässliche H-Diffusionskoeffizienten sind daher ein adäquates Tool zur Bewertung des Risikos einer verzögerten WKB. Dieser Beitrag beschreibt Untersuchungen zur Charakterisierung der Wasserstoffdiffusionsverhalten in UP-Mehrlagen-SG eines 60 mm dicken Bleches einer Offshore-Stahlgüte. Dazu wurden Proben unterschiedlicher Dicke aus dem reinen Schweißgut extrahiert und über elektrochemische Permeation und Trägergasheißextraktion im Temperaturbereich bis 400 °C sehr interessante Ergebnisse zu den korrespondierenden Diffusionskoeffizienten erarbeitet. T2 - DVS Congress 2021 CY - Online meeting DA - 14.09.2021 KW - UP-Schweißen KW - Wasserstoff KW - Kaltriss KW - Permeation KW - Diffusion PY - 2021 SN - 978-3-96144-146-4 VL - 371 SP - 448 EP - 459 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-53369 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Kannengießer, Thomas T1 - Fügetechnik in Wasserstofftechnologien - Forschungsbedarf für die Branche (Kurzversion) N2 - Die Studie gibt einen kurzen Überblick über die jetzige Bedeutung der Fügetechnik in Wasserstofftechnologien und über zukünftige Forschungsbedarfe für die Branche in den einzelnen Technologiefeldern Wasserstofferzeugung, -speicherung, -transport und -nutzung. Fügetechnologien haben dabei wesentliche Bedeutung für die erfolgreiche Umsetzung von technischen Komponenten der Wasserstofftechnologien. Die Schwerpunkte bzw. Forschungsbedarfe ergeben sich bspw. durch die Erstellung neuer Infrastruktur für Wasserstoffspeicherung und -transport sowie durch Umnutzung der bestehenden Erdgasinfrastruktur. Bei der Wasserstofferzeugung und -anwendung wird z.B. die Entwicklung effiziente Massenproduktionsmethoden von Elektrolyseuren und Brennstoffzellen einen wichtigen Meilenstein bilden und laserbasierte Fügetechnologien sind hier zum Teil schon etabliert. Die additive Fertigung nimmt dabei eine Querschnittsposition ein und besitzt hohes Anwendungspotential für die Zukunft z.B. für die Fertigung von Komponenten in Gasturbinen. Aus den technischen Fragestellungen und Forschungsbedarfen ergeben sich zudem Herausforderungen für die notwendige Neu- und Weiterentwicklung von technischen Regelwerken und Normen und den Eingang in die Aus- und Weiterbildung von fügetechnischem Fachpersonal. T2 - DVS Congress 2021 CY - Online meeting DA - 14.09.2021 KW - Wasserstoff KW - Fügetechnik KW - Forschung KW - Werkstoff KW - Bedarf PY - 2021 SN - 978-3-96144-146-4 VL - 371 SP - 612 EP - 624 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-53370 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kröll, Mirco A1 - Grundtner, R. A1 - Pagano, F. A1 - Nyberg, E. A1 - Heino, V. A1 - Spaltmann, Dirk A1 - Gradt, Thomas T1 - Auswirkungen von vereinheitlichten Prozeduren auf tribologische Versuche N2 - Anerkannte Institutionen stellen ihre Kompetenzen auf dem Gebiet tribologischer Charakterisierungen Industrie und Forschung zur Verfügung (https://www.i-tribomat.eu/). Ein Aspekt hierbei ist eine tribologische Datenbank. Um die nötige Qualität der Daten sicherzustellen, sind vereinheitlichte Prozeduren erforderlich, in deren Auswirkungen dieser Vortrag einen Einblick gibt. T2 - 62. Tribologie-Fachtagung der Gesellschaft für Tribologie e. V. CY - Online meeting DA - 27.09.2021 KW - Datenbank KW - Tribologische Daten KW - Europäisches Tribologie-Zentrum PY - 2021 SN - 978-3-9817451-6-0 VL - 15 SP - 15/1 EP - 15/4 AN - OPUS4-53430 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Becker, Amadeus A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas A1 - Michael, Thomas T1 - Konstruktive Einflüsse bei der beanspruchungsgerechten Reparatur geschweißter Bauteile aus hochfesten Feinkornbaustählen N2 - Für eine nachhaltige und ressourceneffiziente Fertigung von Windkraftanlagen ist der Einsatz moderner hochfester Feinkornbaustähle vielfach notwendig. Bei der Montage hochfester Stahlkonstruktionen kommt es trotz anforderungsgerechter schweißtechnischer Fertigung vereinzelt zur Detektion von unzulässigen Unregelmäßigkeiten im Schweißbereich. Derzeitige Normen und Verarbeitungsrichtlinien geben hierbei kaum Informationen zu adäquaten Reparaturkonzepten, insbesondere für hochfeste Stähle. Vor diesem Hintergrund werden an der Bundesanstalt für Materialforschung und -prüfung (BAM) bauteilrelevante Untersuchungen zu den schweißbedingten Beanspruchungen und Gefügeveränderungen bei der schweißtechnischen Reparatur durch lokales thermisches Ausfugen und erneutes Schweißen durchgeführt. Hierzu werden einige wesentliche Ergebnisse an Beispielen des Ingenieurbaus, mit Blick auf die mechanisch-technologischen Eigenschaften und Eigenspannungen erörtert. In einem aktuellen Vorhaben (FOSTA P1311, IGF 20162N) sind darauf aufbauend die Einflüsse durch die Schrumpfbehinderung und Wärmeführung beim Reparaturschweißen hochfester Feinkornbaustähle (S500MLO, S960QL) sowie die Reparaturzyklenanzahl Fokus systematischer Untersuchungen. Mittels strukturmechanischer Berechnungen ließen sich hierzu selbstbeanspruchende Probenformen identifizieren, die unterschiedliche definierte Steifigkeitsverhältnisse von Reparaturschweißnähten realer Bauteile abbilden. Schweißnähte an diesen bauteilähnlichen Proben weisen signifikant erhöhte schweißbedingte Beanspruchungen mit zunehmenden (Biege-)Einspanngraden auf. Im Vergleich mit bisherigen Erkenntnissen wird gezeigt, dass eine sichere Reparatur solcher Schweißnähte nur mittels optimaler Reparaturkonzepte und Wärmeführung gelingt, um diesen hohen Beanspruchungen und auch den speziellen Gefügen hochfester Stähle Rechnung zu tragen. Ziel der Untersuchungen ist es letztlich, Empfehlungen für beanspruchungs- und werkstoffgerechte Reparaturkonzepte gerade für KMU abzuleiten, um Schäden und zumeist teure Nacharbeiten zu vermeiden. T2 - 4. Niedersächsisches Symposium Materialtechnik CY - Online meeting DA - 25.02.2021 KW - Eigenspannungen KW - Gefügedegradation KW - Hochfester Feinkornbaustahl KW - Reparatur KW - Schweißen PY - 2021 SN - 978-3-8440-8021-6 SN - 2364-0804 VL - 10 SP - 488 EP - 501 PB - Shaker Verlag CY - Düren AN - OPUS4-53315 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gook, Sergej A1 - El-Sari, Bassel A1 - Üstündag, Ömer A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael A1 - Biegler, Max T1 - Kombination des Laserhybridschweißens und UP-Engspaltschweißens für dickwandige Bauteile zur Erhöhung der Wirtschaftlichkeit N2 - Dieser Beitrag befasst sich mit der Entwicklung eines wirtschaftlichen und robusten Verfahrens zum Schweißen dicker Stahlbleche. Es werden Ergebnisse für das Fügen von Blechen im Dickenbereich von 25 mm bis 80 mm vorgestellt. Die 30 mm dicken Schweißnähte konnten im Stumpfstoß in zwei Durchgängen unter Verwendung des Laserhybridschweißens und des Unterpulverschweißens (UP) geschweißt werden. Das Laserhybridschweißen wird als Einschweißung mit einer Tiefe von ca. 25 mm ausgeführt. Die UP-Lagen werden auf der gegenüberliegenden Seite des Blechs aufgebracht. Bei richtiger Wahl der Schweißparameter wird der Nahtquerschnitt durch eine sichere Überlappung beider Lagen geschlossen. Bei Blechdicken über 30 mm ist eine Kantenvorbereitung erforderlich, die eine Ausführung der UP-Fülllagen in Engspalttechnik ermöglicht. Die Vorteile der vorgeschlagenen Prozesskombination liegen darin, dass die Nahtwurzel der Laserhybridnaht nicht geformt werden muss. Defekte in der Wurzel der Laserhybrideinschweißung können durch die UP-Lagen effektiv beseitigt werden. Das Verfahren bietet eine hohe Stabilität des Schweißprozesses in Bezug auf die Qualität der Blechkanten. Plasmageschnittene Kanten konnten ohne Bindefehler geschweißt werden. Die erreichte Nahtqualität wurde durch zerstörende und zerstörungsfreie Prüfungen bestätigt. T2 - Innovationstag 2024 CY - Düsseldorf, Germany DA - 10.04.2024 KW - Laserhybridschweißen KW - Windturm KW - Dickblech KW - Unterpulverschweißen PY - 2024 SN - 978-3-96144-253-9 VL - 391 SP - 186 EP - 194 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-60031 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, Marcel A1 - Mayer, Uwe A1 - Baer, Wolfram T1 - Investigating the Applicability of the Master Curve Concept for Ductile Cast Iron – Early Results for 2 Different Test Temperatures N2 - Based on the state-of-the-art research and regulations, the application of the fracture mechanics master curve (MC) concept to ferritic ductile cast iron (DCI) is being investigated in a joint research project between MPA Stuttgart and BAM Berlin. This paper outlines the research approach, the planned investigations and first results of the experimental program. T2 - 8th SEDS Workshop: Safety of Extended Dry Storage CY - Garching, Germany DA - 15.05.2024 KW - Dynamic fracture KW - Brittle fracture KW - Ductile cast iron KW - Master Curve PY - 2024 SP - 1 EP - 4 AN - OPUS4-60013 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, M. A1 - Baer, Wolfram A1 - Mayer, U. A1 - Weihe, S. T1 - Untersuchung des Master Curve-Konzepts für ferritisches Gusseisen mit Kugelgraphit N2 - Das Master Curve (MC) Konzept nach ASTM E1921 wird momentan u.a. in der Kerntechnik für die bruchmechanische Sicherheitsbewertung ferritischer Stähle eingesetzt. Für ferritisches Gusseisen mit Kugelgraphit (GJS) fehlt jedoch eine Validierung dieser Methode und ggf. eine systematische Überprüfung möglicher Modifikationen grundlegender Ansätze des MC-Konzepts. Aus diesem Grund soll in einem kürzlich gestarteten BMUV-Verbundprojekt zwischen der MPA Stuttgart und der BAM Berlin die Anwendbarkeit des MC-Konzepts auf GJS bei dynamischer Beanspruchung untersucht werden. Ziel ist es, eine effektive und effiziente Methodik bereitzustellen, mit der mittels einer vergleichsweise kleinen Stichprobe bruchmechanischer Kleinproben eine Referenztemperatur T0 zur werkstoffspezifischen Temperaturjustierung der MC ermittelt werden kann. T2 - 55. Jahrestagung des DVM-Arbeitskreises "Bruchmechanik und Bauteilsicherheit" CY - Darmstadt, Germany DA - 14.02.2023 KW - Dynamische Beanspruchung KW - Bruchmechanik KW - Master Curve-Konzept KW - Gusseisen mit Kugelgraphit PY - 2023 DO - https://doi.org/10.48447/Br-2023-BB SP - 101 EP - 108 PB - DVM Berlin CY - Berlin AN - OPUS4-57024 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Erxleben, Kjell A1 - Richter, Tim A1 - Schröpfer, Dirk T1 - Charakterisierung der WIG und FSW-Mischverbindungen neuartiger Multielement-Legierungen mit einem austenitischen Stahl N2 - Multielement-Legierungen (MPEA - Multiple Principal Element Alloys), gemeinhin und partiell fälschlicherweise auch als Hochentropielegierungen bezeichnet) stellen eine neue Klasse von Werkstoffen dar, die aus mindestens drei Legierungselementen mit jeweils 5 bis 35 Atom-% bestehen. Somit unterscheidet sich dieses Legierungskonzept fundamental von konventionellen Werkstoffen wie Stahl oder Nickellegierungen. Hierzu werden die Legierungselemente gezielt ausgewählt und die Mikrostrukturen ein- und zum Teil auch mehrphasig eingestellt. Das Ziel ist dabei, hochinnovative MPEA mit individuell einstellbaren Eigenschaften für die industrielle Anwendung zu identifizieren. Dabei werden insbesondere Zielkonflikte, wie bspw. der Trade-off zwischen Festigkeit und Duktilität bei konventionellen Stählen, überwunden. Insbesondere die hohe mechanische Festigkeit bei höchster Korrosionsbeständigkeit sind bei bestimmten Legierungssystemen von hohem Interesse. Hier kann u.a. die Substitution klassischer hochlegierter Stähle oder Ni-Basislegierungen perspektivisch erfolgen. In den letzten 20 Jahren lag der Fokus jedoch auf der reinen Materialsynthese. Mit der Zunahme verfügbarer Werkstoffquantitäten, stehen Verarbeitungsfragen, wie werkstoff- und beanspruchungsgerechte Füge- bzw. Schweißverfahren jetzt im Mittelpunkt. Der Schweißeignung von MPEA wurde bisher nur äußert wenig Aufmerksamkeit zuteil. Erfahrungen zu Mischverbindungen (DMWs - Dissimilar Metal Welds) fehlen dabei vollständig, sind jedoch essenziell für die Anwendung dieser Werkstoffe in Verbindung mit konventionellen Werkstoffen. Die vorliegende Studie präsentiert erstmals im deutschen Sprachraum, die umfassenden experimentellen Ergebnisse zur Schweißeignung von MPEA-Mischverbindungen und der resultierenden Mikrostruktur. Dazu wurden zwei äquiatomare MPEAs in Form einer Co20Cr20Fe20Mn20Ni20 (Hochentropie-) und Co33.3Cr33.3Ni33.3 (Mediumentropielegierung) mittels WIG und Rührreibschweißen mit einem konventionellen, korrosionsbeständigem Cr-Ni-Stahl AISI 304 (1.4301 bzw. X5CrNi18-10) gefügt. Die erstmals untersuchten DMWs resultierten dabei in sehr interessanten Mikrostrukturen, mechanisch-technologische Eigenschaften wurden durch instrumentierte Zugversuche gewonnen, die gleichzeitig der Ermittlung der lokalen Verformung im Schweißnahtbereich dienten (durch Verwendung der berührungslosen DIC-Digital Image Correlation-Technik). Dabei zeigt sich für beide Schweißverfahren eine Erweichung in der Wärmeeinflusszone (WEZ) der MPEAs sowie eine geringfügig verminderte Zugfestigkeit, bei einer deutlichen Abnahme der Bruchdehnung. Durch die Experimente konnte der prinzipielle Nachweis der Schweißeignung der MPEAs für DMWs mit konventionellen Werkstoffen erbracht werden, die auch eine dementsprechende mechanische Beanspruchbarkeit ermöglichen. Dies ermöglicht weitere Betrachtungen zur Anwendung dieser innovativen Werkstoffe. T2 - DVS Congress 2023 CY - Essen, Germany DA - 11.09.2023 KW - Schweißeignung KW - Mischverbindung KW - Hochentropielegierung KW - Multielement-Legierung KW - FSW KW - WIG PY - 2023 SN - 978-3-96144-230-0 VL - 389 SP - 615 EP - 623 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-58352 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Kannengießer, Thomas A1 - Mente, Tobias T1 - Zuverlässige Wasserstoff Bestimmung in Metallen und ihren Schweißverbindungen: Parameter, Einflüsse, Grenzen N2 - Im Zuge der wasserstoffbasierten Energiewirtschaft von morgen, kommt der Errichtung der dementsprechenden Infrastruktur die zentrale Rolle zu. Der überwiegende Teil bisher eingesetzter und meist geschweißter Werkstoffe, wie Stähle, kann unter bestimmten Bedingungen zur Wasserstoffversprödung neigen. Dies umfasst die klassische verzögerte Kaltrissbildung während der Schweißverarbeitung als auch Versprödungsphänomene während des Betriebs. Für die Bewertung eines jeden Wasserstoffeffektes auf bspw. die mechanischen Eigenschaften eines geschweißten metallischen Werkstoffes, muss der Wasserstoffgehalt präzise bestimmt werden, Im Fall von Schweißnähten ist die beispielsweise nach der ISO 3690, die klassische isotherme Trägergas-Heißextraktion (TGHE). Die TGHE basiert dabei auf der beschleunigten Wasserstoffentgasung aufgrund der thermischen Aktivierung des Wasserstoffs bei erhöhten Temperaturen. Neben der reinen Quantifizierung des Wasserstoffs, kann über die thermische Desorptionsanalyse (TDA) mit variierten Heizraten, der Bindungszustand an mikrostrukturellen Defekten im Material festgestellt und bewertet werden. Für beide Techniken sind experimentelle und messtechnische Einflüsse zu beachten, die großen Effekt auf das Ergebnis haben. Für die TGHE schlägt die ISO 3690 schlägt beispielswiese verschiedene Probengeometrien sowie Mindestextraktionszeiten vor. Die vorliegende Studie fasst Ergebnisse und Erfahrungen zahlreicher Untersuchungen an der Bundesanstalt für Materialforschung und -prüfung (BAM) mit unterschiedlichen Probentemperaturen und Geometrien (ISO 3690 Typ B und zylindrische TDA-Proben) zusammen hinsichtlich: Einfluss der Probenoberfläche (poliert/geschweißt), Messgenauigkeiten in Abhängigkeit des Probenvolumens sowie die unzureichende Überwachung des Effektes des PI-Reglers auf die Extraktionstemperatur. Insbesondere eine abweichende Extraktionstemperatur zur eingestellten Temperatur, kann die Messergebnisse wesentlich verfälschen. Basierend auf den Ergebnissen werden Methoden aufgezeigt, um schnell die gewünschte Extraktionstemperatur zu erreichen, ohne physisch in das Messequipment eingreifen zu müssen. Dies dient der wesentlichen Verbesserung der Zuverlässigkeit der Wasserstoffmessung durch erhöhte Signalstabilität und beschleunigte Wasserstoffdesorption. Im Allgemeinen ist eine unabhängige Temperaturmessung mit Dummy-Proben für die gewählte Heizprozedur angeraten, um mögliche unerwünschte Temperatureinflüsse bereits vor der Messung auszuschließen. Die beschriebenen Methoden können ohne großen Aufwand direkt in die industrielle Anwendung überführt werden. T2 - DVS Congress 2023 CY - Essen, Germany DA - 11.09.2023 KW - Wasserstoff KW - Schweißen KW - Forschung KW - ISO 3690 PY - 2023 SN - 978-3-96144-230-0 VL - 389 SP - 435 EP - 442 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-58309 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, Marcel A1 - Baer, Wolfram A1 - Mayer, Uwe A1 - Weihe, Stephan T1 - Investigation of the Master Curve Concept for Ferritic Ductile Cast Iron N2 - Within fracture mechanics safety assessment for steels in nuclear technology, the probabilistic master curve (MC) concept according to ASTM E1921 is currently used for quasi-static loading conditions as a supplement to the established deterministic ASME reference curve concept. However, for ductile cast iron (DCI), a systematic review of potential modifications to the assumptions and the procedure according to ASTM E1921 and an associated validation are still lacking. For this reason, the application of the fracture mechanics MC concept to ferritic ductile cast iron is being investigated in a recently started joint research project between MPA Stuttgart and BAM Berlin. According to the IAEA guidelines SSG 26, the safety assessment of DCI containers for transport as well as storage of radioactive materials is based on the fracture mechanics criterion of general crack initiation exclusion. Within this context, the focus of the current research project is on the further development of brittle fracture safety assessment methods. Therefore, a methodology shall be established to determine and assess dynamic fracture toughness values of DCI in the ductile-to-brittle transition regime, using samples extracted from a component. For the experimental program, a DCI material will be produced as it is generally used for transport and storage containers. A basic mechanical-technological material characterization consisting of tensile, Charpy and Pellini tests is planned and a comprehensive fracture mechanics test program was compiled covering dynamic testing of DC(T)9, C(T)25, C(T)50, SE(B)10, SE(B)25, and SE(B)140 specimens. Numerical analyses of different specimen geometries and test setups are planned to investigate the influences of stress triaxiality and loading rate. Throughout the experimental program, the microstructure-property relationship will be investigated based on quantitative metallographic and fractographic analyses. Finally, different MC assessment strategies will be considered and modifications will be made if necessary. T2 - 21st International Symposium ASTM/ESIS Symposium on Fatigue and Fracture Mechanics CY - Washington, DC, USA DA - 08.11.2023 KW - Ductile Cast Iron KW - Dynamic Fracture Toughness KW - Cleavage Fracture KW - Master Curve Concept PY - 2023 SP - 1 EP - 5 PB - ASTM International CY - West Conshohocken, PA AN - OPUS4-59064 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Putra, Stephen Nugraha A1 - Meng, Xiangmeng A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Der Einfluss verschiedener räumlicher Diskretisierungsansätze des Ray-Tracing-Verfahrens bei der Simulation des Laserstrahltiefschweißen N2 - Die Wärmeverteilung des Lasers beim Laserstrahltiefschweißen ist für die Formgebung der Dampfkapillare und für die Schweißbaddynamik entscheidend. In dieser Arbeit werden die Laserwärmeverteilung und deren Einflüsse auf die Schweißbadtiefe sowie -breite numerisch anhand des Ray-Tracing-Verfahrens analysiert. Hierbei wird der La-serstrahl in mehreren Strahlenbündeln bzw. Subrays unterteilt. Diesbezüglich soll der Pfad der Subrays präzis be-rechnet werden, um die Dynamik der Dampfkapillare und des Schweißbades eines realen Schweißprozesses rich-tig abzubilden. Zu diesem Zweck beschäftigt sich die vorliegende Arbeit mit der Genauigkeitsverbesserung der Kontaktposition und der Reflexionsrichtung der Subrays auf der freien Oberfläche anhand der Level-Set-Methode. Um die Güte dieses Simulationsansatzes zu gewährleisten, wurde eine Gegenüberstellung mit den zwei klassischen Ray-Tracing-Verfahren mittels drei verschiedenen Benchmark-Testreihen durchgeführt. Anschließend wurden die Versuchsergebnisse zur Validierung der implementierten numerischen Ansätze verwendet. Im Rahmen dieser Arbeit kann es gezeigt werden, dass unterschiedliche Wärmeverteilung aufgrund der verschiedenen Ray-Tracing-Verfahren deutlich zu erkennen ist, welche wiederum die Schweißbaddynamik sowie die lokalisierte Dampfkapil-lardynamik stark beeinflussen. Ferner wurde es bestätigt, dass die implementierte Level-Set-Methode zu einer ge-naueren Ermittlung der Kontaktposition und der Reflexionsrichtung der Subrays und somit zu einer Verbesserung der simulierten Schmelzkontur führt. T2 - 43. Assistentenseminar Füge- und Schweißtechnik CY - Schwarzenberg/Erzgebirge, Germany DA - 27.09.2022 KW - Laser beam welding KW - Ray tracing method KW - Weld pool dynamics KW - Numerical modeling PY - 2023 UR - https://www.dvs-media.eu/de/neuerscheinungen/4584/43.-assistentenseminar-fuegetechnik SN - 978-3-96144-212-6 VL - 386 SP - 91 EP - 102 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-59119 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram A1 - Holzwarth, Marcel A1 - Mayer, Uwe ED - Vormwald, Michael T1 - Untersuchung des Master Curve-Konzepts für ferritisches Gusseisen mit Kugelgraphit: Versuchswerkstoff und erste Ergebnisse an SE(B)140-Großproben N2 - In einem laufenden Kooperationsprojekt zwischen der BAM Berlin und der MPA Stuttgart wird das probabilistische Master Curve (MC) Konzept nach ASTM E1921 hinsichtlich seiner Übertragbarkeit auf ferritisches Gusseisen mit Kugelgraphit (DCI) untersucht. Zielsetzung ist die Bereitstellung einer Vorgehensweise zur Bestimmung und Bewertung der dynamischen Bruchzähigkeit von DCI im Übergangsbereich. In diesem Beitrag wird der Versuchswerkstoff der Festigkeitsklasse GJS-400 näher vorgestellt. Ferner werden erste Ergebnisse von zwei bruchmechanischen Versuchsserien an SE(B)140-Großproben bei Belastungsraten von ca. 6∙104 MPa√ms-1 bei -40 °C und -60 °C präsentiert. T2 - 56. Tagung des DVM-Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Kassel, Germany DA - 20.02.2024 KW - Dynamische Beanspruchung KW - Bruchmechanik KW - Master Curve-Konzept KW - Gusseisen mit Kugelgraphit PY - 2024 DO - https://doi.org/10.48447/BR-2024-BB SP - 49 EP - 58 PB - DVM-Verlag CY - Berlin AN - OPUS4-59518 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, Marcel A1 - Baer, Wolfram A1 - Mayer, Uwe A1 - Weihe, Stefan ED - Vormwald, Michael T1 - Untersuchung des Master Curve-Konzepts für ferritisches Gusseisen mit Kugelgraphit: Kritische Belastungsrate und erste Ergebnisse an C(T)-Proben N2 - Im laufenden Verbundprojekt MCGUSS untersuchen dieProjektpartner MPA Stuttgart und BAM Berlin das probabilistische Master Curve (MC) Konzept nach ASTM E1921 hinsichtlich seiner Übertragbarkeit auf ferritisches Gusseisen mit Kugelgraphit (DCI). Ziel des Projektes ist die Entwicklung einer Methode zur Bestimmung und Bewertung der dynamischen Bruchzähigkeit von DCI im Übergangsbereich. In diesem Beitrag werden die Eigenschaften des verwendeten Werkstoffs der Festigkeitsklasse GJS-400 vorgestellt und die sich daraus ergebenden Probenentnahmestellen näher erläutert. Weiterhin werden erste Ergebnisse der C(T)25-Versuchsserien vorgestellt, die bei Belastungsraten von ca. 5∙103 MPa√ms-1, 5∙104 MPa√ms-1 und 5∙105 MPa√ms-1 und einer Temperatur von -40 °C durchgeführt wurden. T2 - 56. Tagung des DVM-Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Kassel, Germany DA - 20.02.2024 KW - Dynamische Belastung KW - Master Curve KW - Gusseisen KW - C(T)-Proben PY - 2024 SP - 37 EP - 47 PB - DVM Verlag CY - Berlin AN - OPUS4-59519 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Nina A1 - Rhode, Michael A1 - Kannengießer, Thomas T1 - Mikrolegierungseinfluss auf das Ausscheidungsverhalten und die mechanischen Eigenschaften geschweißter hochfester Baustähle N2 - Mikrolegierungselemente, wie Nb und Ti, sind für die signifikante Festigkeitssteigerung von vergüteten, hochfesten Feinkornbaustählen mit einer Nominalstreckgrenze ≥ 690 MPa unerlässlich. Normvorgaben zur chemischen Zusammensetzung geben dabei nur obere Grenzwerte für die Hersteller vor. Weiterhin wirken sich bereits kleine Abweichungen in der Legierungsroute teilweise drastisch auf die mechanischen Eigenschaften aus. Somit wird eine adäquate Vorhersage der Schweißeignung und der Integrität der Schweißverbindung aufgrund der variierenden Mikrogefüge erschwert bis unmöglich. Unerwünschte Nebeneffekte sind die mögliche Erweichung der Wärmeeinflusszone (WEZ) als auch der gegenteilige Effekt der Aufhärtung. Vor diesem Hintergrund werden erstmals systematisch die unterschiedlichen Mikrolegierungsrouten mit variierenden Ti und Nb-Gehalten an Versuchsschmelzen untersucht. Die Stahlgüte S690QL bildet dabei die Grundlage der chemischen Zusammensetzung sowie der entsprechenden Wärmebehandlung. Zur Untersuchung der jeweiligen Schweißeignung wurden Dreilagen-Schweißungen mittels moderner MAG-Hochleistungsschweißprozesse durchgeführt und kritische Gefügebereiche mit hoher Erweichung/Aufhärtung identifiziert. Der Fokus der analytischen Betrachtungen lag hier auf der Identifikation der Phasenumwandlungen beim Abkühlen und auf dem metallurgischen Ausscheidungsverhalten. Zusätzlich wurden isotherme und nicht-isotherme Phasenberechnungen mit der Software Thermo-Calc durchgeführt. Mechanisch-technologische Untersuchungen zur Kerbschlagzähigkeit mittels Kerbschlagbiegeversuchen durchgeführt wurden, bestätigen dabei die Ergebnisse der thermodynamischen Simulation bezüglich des Ausscheidungsverhaltens während der Temperatur-Zeit Schweißzyklen. Daraus lässt sich der Einfluss der Wärmeeinwirkung beim Schweißen auf die Gefügeausbildung in der WEZ und der korrespondierenden mechanischen Eigenschaften qualitativ beschreiben. T2 - DVS Congress 2023 Große Schweißtechnische Tagung CY - Essen, Germany DA - 11.09.2023 KW - WEZ-Erweichung KW - Mikrolegierungseinflüsse KW - Hochfester Feinkornbaustahl KW - Kerbschlagzähigkeit PY - 2023 SN - 978-3-96144-230-0 VL - 389 SP - 218 EP - 225 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-59419 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, Marcel A1 - Mayer, Uwe A1 - Baer, Wolfram A1 - Weihe, Stefan T1 - Investigation of the Master Curve Concept for Ferritic Ductile Cast Iron N2 - Within fracture mechanics safety assessment for steels in nuclear technology, the probabilistic master curve (MC) concept according to ASTM E1921 is currently used for quasi-static loading conditions as a supplement to the established deterministic ASME reference curve concept. However, for ductile cast iron (DCI), a systematic review of potential modifications to the assumptions and the procedure according to ASTM E1921 and an associated validation are still lacking. For this reason, the application of the fracture mechanics MC concept to ferritic ductile cast iron is being investigated in a joint research project between MPA Stuttgart and BAM Berlin. According to Hojo et al. (2008) the MC concept is already in use for the brittle fracture safety assessment of ferritic forged steel containers, which would suggest an extension to ductile cast iron containers. In compliance with IAEA SSG-26, the safety assessment of DCI containers for transport as well as storage of radioactive materials is based on the fracture mechanics criterion of general exclusion of crack initiation. Within this context, the focus of the current research project is on the further development of brittle fracture safety assessment methods. Therefore, a methodology shall be established to determine and assess dynamic fracture toughness values of DCI in the ductile-to-brittle transition regime, using only a low number of small fracture mechanics test specimens extracted from a component. For the experimental program, a DCI material of grade GJS-400 (GGG-40) has been produced as it is generally used for transport and storage containers for nuclear material. A basic mechanical-technological material characterization consisting of tensile, Charpy, and Pellini tests has been planned and a comprehensive fracture mechanics test program was compiled covering dynamic testing of DC(T)9, C(T)25, C(T)50, SE(B)10, SE(B)25, and SE(B)140 specimens at various loading rates and temperatures. The specimen testing is divided between the project partners based on specimen geometry. MPA Stuttgart has been tasked with the testing of the C(T), DC(T) and Pellini specimens, while BAM Berlin was assigned the SE(B), Charpy and tensile tests. These tests allow for the determination of the loading rate relevant for brittle fracture via C(T)25 specimens and an assessment of size effects by transferring the relevant loading rate to other specimen geometries and sizes. Numerical analyses of different specimen geometries and test setups are planned to investigate the influence of stress triaxiality and loading rate. Furthermore, the time-dependent course of the Weibull stress is assessed via these numerical analyses. Throughout the experimental program, the microstructure-property relationship will also be investigated based on quantitative metallographic and fractographic analyses like scanning electron microscope images and metallographic sections. With the acquired experimental database fundamental assumptions of the MC concept, like the weakest link model and the Weibull distribution, will be assessed for the application to DCI. In the end, the applicability of the MC concept will be evaluated and if necessary, modifications to the MC concept for DCI will be proposed. This paper will present the preliminary results of the GJS400 material characterization and the related selection of test specimen extraction points. First results of the C(T)25 and SE(B)140 specimen testing will also be discussed supported by first metallographic analyses. T2 - SMiRT27 Conference CY - Yokohama, Japan DA - 03.03.2024 KW - Ductile Cast iron KW - Dynamic Fracture Toughness KW - Safety Assessment KW - Master Curve Concept PY - 2024 SP - 1 EP - 10 AN - OPUS4-59302 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Liepold, Philipp ED - Kromm, Arne ED - Kannengießer, Thomas T1 - Anwendung von Convolutional Neural Networks (CNNs) bei der Erkennung von Rissen im Modifizierten Varestraint-Transvarestraint-Heißrisstest (MVT-Test) N2 - Der Modifizierte Varestraint-Transvarestraint-Test wird an der Bundesanstalt für Materialforschung und -prüfung als Variante des Varestraint-Tests verwendet. Die Auswertung dieser Tests findet klassisch durch Abmessungen der entstandenen Risse unter dem Lichtmikroskop statt. Eine solche Auswertung ist aufwendig und fehleranfällig. Convolutional Neural Networks können trainiert werden, um die Risse auf digitalen Bildern zu segmentieren, wodurch der menschliche Fehler in der Auswertung eliminiert werden kann. Die Ergebnisse können durch Overlay mit den Originalbildern verglichen werden. T2 - DVS-Congress, Große Schweißtechnische Tagung CY - Essen, Germany DA - 11.09.2023 KW - CNN KW - MVT KW - KI PY - 2023 SN - 978-3-96144-231-7 SN - 978-3-96144-230-0 VL - 2023 SP - 153 PB - Print Media Group GmbH & Co. KG CY - Hamm AN - OPUS4-59336 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Marquardt, R. A1 - Biegler, M. A1 - Rethmeier, Michael T1 - Laser-Pulver-Auftragschweißen von funktional gradierten Materialien auf Cobalt-Chrom Basis N2 - Um Bauteile vor Verschleiß und Korrosion zu schützen werden Beschichtungen aus resistenteren Materialien aufgetragen. Hierzu zählen unter anderen die Legierungen auf Cobalt-Chrom Basis. Der diskrete Materialsprung ist jedoch unter thermischen und mechanischen Belastungen häufig Ursache für das Versagen der Beschichtung. In dieser Arbeit werden daher Materialgradierungen von verschiedenen Stahllegierungen zu einer Cobalt-Chrom Basislegierung untersucht. Die Ergebnissen werden dafür auch mit Resultaten zu vorangegangenen Untersuchungen verglichen. Kern der Arbeit bilden geätzte Schliffbilder der Materialpaarungen und Auswertungen mittels Farbeindringprüfung sowie die metallografische Bestimmung der Porosität. Ziel der Arbeit ist ein defektfreier Aufbau der funktional gradierten Materialpaarungen. T2 - 43. Assistentenseminar Fügetechnik CY - Päwesin, Germany DA - 20.09.2023 KW - Directed Enery Deposition KW - Funktionally Graded Material KW - Additive Manufacturing KW - DED KW - FGM KW - AM PY - 2023 SN - 978-3-96144-212-6 SP - 1 EP - 6 PB - DVS Media GmbH AN - OPUS4-59116 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Raute, J. A1 - Seitz, G. A1 - Biegler, M. A1 - Rethmeier, Michael T1 - Wire Electron Beam Additive Manufacturing von niedriglegierten Zinnbronzen – Erreichbare Bauteileigenschaften und Prozessmerkmale N2 - Die Additive Fertigung gewinnt zunehmend an Bedeutung für die Verarbeitung von Kupferwerkstoffen im industriellen Umfeld. Hierbei wird verstärkt auf drahtförmige Ausgangswerkstoffe gesetzt, da diese Vorteile im Handling bieten, bereits aus der Schweißtechnik bekannt sind und sich zumeist durch geringere Beschaffungskosten auszeichnen. In den letzten Jahren entwickelte sich unter den drahtbasierten Verfahren der Directed-Energy-Deposition (DED) eine Prozessvariante unter Nutzung des Elektronenstrahls zur industriellen Marktreife. Dabei zeigt die Technologie Wire Electron Beam Additive Manufacturing (DED-EB) besondere Vorteile gegenüber anderen DED-Prozessen für die Anwendung an Kupfer. Um das Verfahren einem breiten Anwenderkreis in der Industrie zugänglich zu machen, fehlen jedoch Daten zu Leistungsfähigkeit, Prozessgrenzen und Anwendungsmöglichkeit- en. Die vorliegende Untersuchung beschäftigt sich mit dieser Problemstellung am Beispiel der Legierung CuSn1MnSi. Über mehrstufige Testschweißungen werden die physikalisch möglichen Prozessgrenzen ermittelt und Rückschlüsse über die Eignung der Parameter zum additiven Aufbau gezogen. An verschiedenen additiv gefertigten Probekörpern werden anschließend Kennwerte für Aufbaurate, Härte, Mikrostruktur, Oberflächenqualität sowie mechanische Festigkeitswerte ermittelt. Es zeigt sich, dass das die durch DED-EB hergestellten Proben, trotz des groben Gefüges sowie der thermischen Belastung im Aufbauprozess, in ihren Eigenschaften gut mit den Spezifikationen des Ausgangsmaterials übereinstimmen. T2 - Kupfersymposium 2023 CY - Jena, Germany DA - 29.11.2023 KW - Wire Electron Beam Additive Manufacturing KW - DED-EB KW - CuSn1 KW - Additive Fertigung PY - 2023 SN - 978-3-910411-03-6 SP - 28 EP - 33 PB - Kupferverband e. V. AN - OPUS4-59118 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Kromm, Arne A1 - Mente, Tobias A1 - Czeskleba, Denis A1 - Brackrock, Daniel A1 - Kannengießer, Thomas T1 - Bauteilversuch zur Bewertung der wasserstoffunterstützten Rissanfälligkeit geschweißter, dickwandiger Offshore-Gründungsstrukturen N2 - Offshore-Windenergieanlagen erfordern Gründungskonzepte aus unterpulver-(UP-)geschweißten Dickblechen (bspw. der Güte S420ML). Während der Schweißfertigung kann eine zeitverzögerte wasserstoffunterstützte Kaltrissbildung auftreten, deren Bewertung aufgrund der Bauteilgröße von Offshore-Strukturen sehr komplex ist. Deswegen wurde eine bauteilähnliche Geometrie (Mock-Up) entwickelt, um reale Steifigkeitsverhältnisse auf den Labormaßstab zu übertragen. Zusätzliche Versteifungen simulieren die Wirkung einer Einspannung bzw. Schrumpfbehinderung der Schweißnaht. Über die Verwendung von Schweißpulvern mit definierter Feuchte wurden zudem ein Extremszenario der Wasserstoffaufnahme simuliert. Entsprechend der vorgegebenen Mindestwartezeit für die ZfP von bis zu 48 h wurde die Schweißnaht zerstörungsfrei mit Phased-Array-Ultraschall-Prüfung (PAUT) geprüft und die Eigenspannungen über Röntgendiffraktometrie (XRD) bestimmt. Zusätzlich wurde die Wasserstoffverteilung in der Schweißverbindung numerisch simuliert. Außer zulässigen Defekten (wie Poren), wurde keine verzögerte Kaltrissbildung in den Mock-Ups festgestellt, was auf hohe Rissbeständigkeit hindeutet. T2 - Tagung Werkstoffprüfung 2023 CY - Berlin, Germany DA - 23.11.2023 KW - Kaltrissbildung KW - Wasserstoff KW - Offshore KW - Schweißen KW - Bauteiltest PY - 2023 DO - https://doi.org/10.48447/WP-2023-219 SP - 316 EP - 321 CY - Berlin AN - OPUS4-58908 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -