TY - CONF A1 - Reichel, Levin A1 - Kromm, Arne A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas T1 - Moderne Schweißverfahren zur Optimierung von Reparaturschweißungen an hochfesten Offshore-Stählen N2 - The successful energy transition in Germany will require offshore wind turbines with outputs >10 MW in the future, for which high-strength steels with a yield strength of up to 500 MPa and wall thicknesses up to 150 mm are increasingly being used. The repair of weld seams when detecting defects during NDT requires local-ized gouging and rewelding. This involves high demands on welding manufacturing, especially for high-strength steels. Due to a lack of investigations, there are no re-pair concepts and information in standards and guidelines, particularly for high-strength thick plate joints made of high-strength offshore steels. However, these are urgently needed to enable processors, especially SMEs, to carry out safe and eco-nomical repairs. Therefore, BAM started the FOSTA project P1629 (IGF 01IF22746N) to investigate the stress-optimized repair (local gouging and welding) of high-strength thick plate joints made of offshore grades in the yield strength range off 355 to 460 MPa and similar weld metal with controlled high-performance GMAW processes and optimized narrower gouging grooves. The experimental analyses consider the complex interaction of material, process, and design-related influences on the formation of weld-related stresses and the special microstructure of high-strength fine-grain structural steels. Welding-related material degradation and crack-critical residual tensile stresses need to be avoided to ensure high component safety and performance. With component-related welding experiments on special testing equipment, adapted process and heat control concepts along with variable groove configurations will be developed and recommendations for guidelines elabo-rated. This is the prerequisite for fully utilizing the strength potential of high-strength steels and making a valuable contribution to the energy transition in Germany, espe-cially for steel-processing SMEs. T2 - Symposium Materialtechnik TU Clausthal CY - Clausthal-Zellerfeld, Germany DA - 19.02.2025 KW - Reparaturschweißen KW - Thermisches Ausfugen KW - Offshore KW - Sprühlichtbogen KW - Eigenspannungen PY - 2025 AN - OPUS4-62630 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Engelking, Lorenz A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas A1 - Eissel, A. A1 - Treutler, K. A1 - Wesling, V. T1 - Herstellung beanspruchungsgerechter Oberflächen durch Kombination innovativer additiver und abtragender Fertigungsschritte an hochbelasteten Komponenten N2 - Die additive Fertigung (AM) durch schweißtechnische Verfahren eröffnet vielfach ökonomische Vorteile für eine ressour-ceneffiziente Bauteilherstellung. Gerade hinsichtlich der Homogenität und Anisotropie der resultierenden Schweißgefüge und den damit verbundenen Eigenschaften gibt es noch offene Fragestellungen. Die Einstellung der finalen Bauteilgeo-metrie und Oberflächengüte erfordert den komplementären Einsatz abtragender Fertigungsschritte. Hochleistungslegie-rungen auf der Basis von Nickel oder Kobalt sind aufgrund ihrer niedrigen Wärmeleitfähigkeit verbunden mit hoher Festigkeit und Zähigkeit schwer spanbar. Eine gezielte Gefügebeeinflussung mittels Modifikation der AM-Schweißzusatz-werkstoffe und der Einsatz des ultraschallunterstützten Fräsens (US) bietet das Potential insgesamt die Zerspanungssi-tuation zu verbessern. Dieser Lösungsansatz unter Gewährleistung des Erhalts der geforderten Werkstoff- bzw. Bauteileigenschaften ist Untersuchungsgegenstand eines Gemeinschaftsvorhabens (IGF-Nr. 20.979 N/DVS-Nr. 1.3211) der BAM und TU Clausthal/ISAF. Der vorliegende Beitrag stellt Ergebnisse für die beiden untersuchten FeNi- und CoCr-Legierungen sowie wesentliche Zusammenhänge zwischen Legierungsmodifikation, entstehender Gefügemorphologie und Zerspanungseigenschaften der mittels MAG additiv gefertigter Proben vor. Das größte Potential für die Modifikation zeigten Zr und Hf. Die Zulegierung in das Schweißgut erfolgte durch Beschichtung von Massivdrähten sowie durch Her-stellung von Fülldrähten. T2 - DVS Congress - GST CY - Essen, Germany DA - 11.09.2023 KW - Legierungsmodifikation KW - Ultraschallunterstütztes Fräsen KW - Additive Fertigung KW - Oberflächenintegrität PY - 2023 SN - 978-3-96144-230-0 VL - 389 SP - 697 EP - 703 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-58380 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Kannengießer, Thomas A1 - Mente, Tobias T1 - Zuverlässige Wasserstoff Bestimmung in Metallen und ihren Schweißverbindungen: Parameter, Einflüsse, Grenzen N2 - Im Zuge der wasserstoffbasierten Energiewirtschaft von morgen, kommt der Errichtung der dementsprechenden Infrastruktur die zentrale Rolle zu. Der überwiegende Teil bisher eingesetzter und meist geschweißter Werkstoffe, wie Stähle, kann unter bestimmten Bedingungen zur Wasserstoffversprödung neigen. Dies umfasst die klassische verzögerte Kaltrissbildung während der Schweißverarbeitung als auch Versprödungsphänomene während des Betriebs. Für die Bewertung eines jeden Wasserstoffeffektes auf bspw. die mechanischen Eigenschaften eines geschweißten metallischen Werkstoffes, muss der Wasserstoffgehalt präzise bestimmt werden, Im Fall von Schweißnähten ist die beispielsweise nach der ISO 3690, die klassische isotherme Trägergas-Heißextraktion (TGHE). Die TGHE basiert dabei auf der beschleunigten Wasserstoffentgasung aufgrund der thermischen Aktivierung des Wasserstoffs bei erhöhten Temperaturen. Neben der reinen Quantifizierung des Wasserstoffs, kann über die thermische Desorptionsanalyse (TDA) mit variierten Heizraten, der Bindungszustand an mikrostrukturellen Defekten im Material festgestellt und bewertet werden. Für beide Techniken sind experimentelle und messtechnische Einflüsse zu beachten, die großen Effekt auf das Ergebnis haben. Für die TGHE schlägt die ISO 3690 schlägt beispielswiese verschiedene Probengeometrien sowie Mindestextraktionszeiten vor. Die vorliegende Studie fasst Ergebnisse und Erfahrungen zahlreicher Untersuchungen an der Bundesanstalt für Materialforschung und -prüfung (BAM) mit unterschiedlichen Probentemperaturen und Geometrien (ISO 3690 Typ B und zylindrische TDA-Proben) zusammen hinsichtlich: Einfluss der Probenoberfläche (poliert/geschweißt), Messgenauigkeiten in Abhängigkeit des Probenvolumens sowie die unzureichende Überwachung des Effektes des PI-Reglers auf die Extraktionstemperatur. Insbesondere eine abweichende Extraktionstemperatur zur eingestellten Temperatur, kann die Messergebnisse wesentlich verfälschen. Basierend auf den Ergebnissen werden Methoden aufgezeigt, um schnell die gewünschte Extraktionstemperatur zu erreichen, ohne physisch in das Messequipment eingreifen zu müssen. Dies dient der wesentlichen Verbesserung der Zuverlässigkeit der Wasserstoffmessung durch erhöhte Signalstabilität und beschleunigte Wasserstoffdesorption. Im Allgemeinen ist eine unabhängige Temperaturmessung mit Dummy-Proben für die gewählte Heizprozedur angeraten, um mögliche unerwünschte Temperatureinflüsse bereits vor der Messung auszuschließen. Die beschriebenen Methoden können ohne großen Aufwand direkt in die industrielle Anwendung überführt werden. T2 - DVS Congress 2023 CY - Essen, Germany DA - 11.09.2023 KW - Wasserstoff KW - Schweißen KW - Forschung KW - ISO 3690 PY - 2023 SN - 978-3-96144-230-0 VL - 389 SP - 435 EP - 442 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-58309 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas A1 - Kannengießer, Thomas T1 - Heißriss-Forschung an der BAM - Ein kleiner Überblick N2 - Die Vermeidung von Heißrissen beim Schweißen ist für die Sicherheit geschweißter Komponenten unerlässlich. Die Entstehung von Heißrissen wird durch die komplexe Interaktion von Schweißprozess, Metallurgie und der konstruktiven Umgebung beschrieben. Bislang wurden mehr als 140 Heißrisstests entwickelt, um die Neigung gegenüber einer Rissbildung festzulegen. Grundsätzlich werden diese in selbstbeanspruchende und fremdbeanspruchte Heißrisstests eingeteilt. Der Vortrag gibt einen Überblick über Forschungsthemen der BAM, welche sich in den letzten Jahren hauptsächlich mit den metallurgischen als auch mit den konstruktiven Einflüssen auf die Rissbildung beschäftigt haben. Von austenitischen und ferritischen Werkstoffen, über neuentwickelte LTT-Legierungen bis hin zur in-situ Radiographie zur Überwachung des Risswachstums während des Schweißens wird ein breites Forschungsspektrum aufgezeigt. Zum Abschluss ist ein Ausblick für zukünftige Forschungsfelder gegeben. Diese Arbeiten konzentrieren sich auf die zwei- und dreidimensionale bildliche Charakterisierung von (Mikro-)Heißrissen in innovativen Werkstoffen zur Erweiterung bestehender Modellvorstellungen zum Rissphänomen. T2 - Forschungsseminar CY - Technische Universität Clausthal, Clausthal, Germany DA - 31.01.2018 KW - Heißriss KW - Austenit KW - Ferrit KW - LTT-Legierung KW - Prüfverfahren PY - 2018 AN - OPUS4-44019 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas T1 - Kaltrissbildung in Mehrlagenschweißungen - Einflussanalyse von Nahtgeometrie und Wärmeführung beim Einsatz modifizierter Sprühlichtbögen N2 - Ausgehend vom derzeit vorrangigen Einsatz in Mobilkranen, kommen höherfeste Feinkornbaustähle mit Streckgrenzen ab 960 MPa zunehmend auch in anderen modernen Stahlkonstruktionen zur Anwendung. Dies ist aufgrund aktueller Forderungen nach Energie- und Ressourceneffizienz im Sinne des konstruktiven Leichtbaus vielfach notwendig. Die Verwendung höherfester Stähle sowie deren schweißtechnische Verarbeitung, insbesondere in sicherheitsrelevanten Tragstrukturen, erfordert ein tiefgreifendes Verständnis der Zusammenhänge zwischen Schweißverfahren, Wärmeeinbringung, Abkühlbedingungen sowie den daraus resultierenden metallurgischen Vorgängen in der Schweißnaht und den nahtnahen Bereichen. Vorwiegend werden höherfeste Güten mittels MAG-Prozess geschweißt. Bedeutende Fortschritte in der Regelungstechnik führten unter den Herstellern von Schweißstromquellen in den letzten Jahren zur Entwicklung zahlreicher modifizierter Sprühlichtbogenprozesse (mod. SLB). Diese Prozesse ähneln sich in ihren Eigenschaften und ermöglichen die bekannten positiven Aspekte, wie Einsparung an Schweißzusatz sowie Schweiß- und Rüstzeit aufgrund der Möglichkeit reduzierter Nahtöffnungswinkel. Der mod. SLB bedingt zusammen mit einer anderen Nahtgeometrie veränderte Naht- und Schweißraupenquerschnitte sowie einen abweichenden Lagenaufbau. Diese wirtschaftlich-technisch attraktive Möglichkeit reduzierter Nahtöffnungswinkel findet in den Regelwerken zur schweißtechnischen Verarbeitung höherfester Feinkornbaustähle unter Vermeidung von Kaltrissbildung bisher keine Berücksichtigung. Dabei gilt es, gerade die Interaktion der Haupteinflussgrößen auf die Kaltrissbildung unter reduziertem Nahtöffnungswinkel zu betrachten. Im Rahmen zweier AiF-Forschungsvorhaben (IGF-Nr. 17.978 N, 18.596 BR) wurde daher der Einfluss der Wärmeführung anhand vergleichender Mehrlagenschweißungen mittels konventionellem Übergangslichtbogen und mod. SLB mit angepasster Nahtkonfiguration auf schweißbedingte Beanspruchungen sowie auf die Wasserstoffkonzentration im Schweißgut untersucht. T2 - DVS Congress 2018 - Große Schweißtechnische Tagung CY - Friedrichshafen, Germany DA - 17.09.2018 KW - Kaltriss KW - Hochfester Feinkornbaustahl KW - MAG-Schweißen PY - 2018 SN - 978-3-96144-036-8 VL - 344 SP - 73 EP - 78 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-45977 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Kannengießer, Thomas A1 - Schaupp, Thomas ED - Brockmann, S. ED - Krupp, U. T1 - Wasserstoffunterstützte Kaltrissbildung in Schweißnähten hochfester Stahlgüten - Anforderungen an die Prüfung N2 - Wasserstoff kann eine Rissbildung u.U. auch noch nach Tagen in der Schweißnaht bewirken. Dabei stellen höherfeste Stähle etablierte Kaltrissprüftests vor Herausforderungen. Generell nimmt die zur Rissvermeidung tolerierbare Wasserstoffkonzentration mit zunehmender Festigkeit der Werkstoffe ab. Zudem verändern weiterentwickelte Schweißverfahren die Nahtgeometrie und Wärmeeinbringung und die Ausbildung risskritischer Mikrostrukturen (z.B. Wärmeeinflusszone). Am Beispiel des Implant- und Tekken-Tests werden die Einsatz- u. Anwendungsgrenzen bewertet. Zu berücksichtigen ist, dass beim Schweißen eine äußere mechan. Beanspruchung durch bauteilspezifische Steifigkeitsverhältnisse wirksam ist. Zusätzlich werden weiterführende Prüfverfahren zur Bestimmung der Wasserstoffkonzentration und -diffusion in Schweißnähten vorgestellt, wie die Trägergasheißextraktion (TGHE) für die Ermittlung der Wasserstoffkonzentration (ISO 3690) oder Hochtemperaturdiffusionskoeffizienten. Diese Werte sind für die schweißtechnische Praxis von großer Bedeutung, um Haltezeiten z.B. für das Wasserstoffarmglühen abzuleiten. T2 - Tagung Werkstoffprüfung 2021 CY - Online meeting DA - 02.12.2021 KW - Wasserstoff KW - Kaltrissprüfung KW - Schweißen KW - Stahl KW - Hochfest PY - 2021 SN - 978-3-941269-98-9 SP - 15 EP - 20 PB - Stahlinstitut VDEh CY - Düsseldorf AN - OPUS4-53900 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Kannengießer, Thomas A1 - Kromm, Arne A1 - Dixneit, Jonny A1 - Dilger, K. A1 - Nitschke-Pagel, T. A1 - Hensel, J. A1 - Eslami, H. T1 - Schwingfestigkeitsverbesserung hochfester Schweißverbindungen mit Hilfe neuartiger LTT-Zusatzwerkstoffe N2 - Die Verwendung von LTT-Zusatzwerkstoffen stellt einen alternativen Ansatz zu den sonst üblichen Verfahren der Schweißnahtnachbehandlung zur Schwingfestigkeitserhöhung geschweißter Stahlkonstruktionen dar. Der wesentliche Wirkmechanismus beruht auf der Beeinflussung des Eigenspannungszustands durch die niedrige Martensitstarttemperatur bereits während des Schweißens. Dadurch werden die Druckeigenspannungen aus der behinderten Volumenausdehnung infolge Phasenumwandlung voll wirksam. Weiter weist die Schweißnaht eine hohe Härte auf, die die Schwingrissbildung verzögern kann, allerdings auch zu einer niedrigen Kerbschlagarbeit führt. Im vorliegenden Forschungsvorhaben wurden grundlegende Untersuchungen zur schweißtechnischen Verarbeitung eines LTT-Zusatzwerkstoffes durchgeführt. Dies beinhaltet die Sicherstellung der Schweißbarkeit sowie die Charakterisierung der Verbindungseigenschaften. Untersuchungen zur Schweißeignung machten deutlich, dass ein sicherer Einsatz in dem für hochfeste Stähle zur Verfügung stehenden Arbeitsfenster möglich ist. Der verwendete LTT-Zusatz auf Cr-Ni-Basis lässt sich mit hoher Nahtgüte fügen. Auch die mechanischen Eigenschaften erlauben den Einsatz im Bereich hochfester Stähle mit einer Streckgrenze von 960 MPa. Entwicklungspotential gibt es hinsichtlich der Zähigkeit. Die in dieser Arbeit erreichten Kerbschlagwerte liegen deutlich unter denen kommerziell verfügbarer konventioneller Schweißgüter. Die Untersuchungen belegen, dass der Effekt der martensitischen Phasenumwandlung im gesamten Schweißgut zum Tragen kommt. Die angestrebten hohen Druckeigenspannungen finden sich vornehmlich im Schweißgutinnern. Im weiteren Vorgehen wurden Schwingfestigkeitsuntersuchungen an den Stählen S355J2 und S960Q unter Verwendung konventioneller Zusatzwerkstoffe im Vergleich zum LTT-Zusatz durchgeführt. Die verwendeten Konstruktionsdetails sind ein Stumpfstoß unter Variation der Schweißnahtausführung (DY-Naht und V-Naht), ein Kreuzstoß mit HV-Naht sowie ein Überlappstoß mit einseitig und beidseitig geschweißter Kehlnaht. Weitergehend wurde eine bauteilähnliche Probe (die Längssteife) untersucht, bei der der LTT-Zusatzwerkstoff als zusätzliche Schweißlage aufgebracht wurde. Neben der Schwingfestigkeit wurden die Schweißnähte hinsichtlich der Eigenspannungen, der Eigenspannungsstabilität im Schwingversuch sowie metallografisch charakterisiert. Eine generell positive Wirkung des LTT-Zusatzwerkstoffes im Hinblick auf die Schwingfestigkeitssteigerung kann nicht bestätigt werden. Teilweise ist eine Steigerung der Schwingfestigkeit bei Substitution konventioneller Zusatzwerkstoffe zu beobachten, teilweise zeigt sich kein Effekt. Ursächlich hierfür ist die bei manchen Stoßformen mangelnde Steifigkeit quer zur Schweißnaht, die zur Ausbildung hoher Druckeigenspannungen infolge Phasenumwandlung notwendig wäre. Die bauteilähnliche Längssteife bestätigt allerdings das grundlegende Potential der LTT-Zusatzwerkstoffe bei Vorliegen hinreichender Steifigkeit. KW - Schweißen KW - Eigenspannungen KW - Schwingfestigkeit KW - Hochfester Stahl KW - LTT PY - 2020 UR - https://matplus.shop/produkt/p-1060-schwingfestigkeitsverbesserung-hochfester-schweissverbindungen-mit-hilfe-neuartiger-ltt-zusatzwerkstoffe SN - 978-3-946885-75-7 VL - P 1060 SP - 1 EP - 123 PB - Verlag und Vertriebsgesellschaft CY - Düsseldorf AN - OPUS4-51216 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Launert, B. A1 - Rhode, Michael A1 - Pasternak, H. A1 - Kannengießer, Thomas ED - Dubina, D. ED - Ungureanu, V. T1 - Welding Residual Stresses in High-strength Steel. Experimental Results N2 - This article presents the latest results of an ongoing national research project on improved models for the prediction of welding residual stresses of thick-plated welded I-girders. The experimental program is presented and the importance of different influencing factors on the residual stresses is discussed in detail. All results are compared for mild (S355J2+N) and high strength (S690QL) steel. Finally, conclusions for further works are drawn. T2 - SDSS 2016 - The International Colloquium on Stability and Ductility of Steel Structures - SDSS 2016 CY - Timisoara, Romania DA - 30.05.2016 KW - Residual Stresses KW - Welding KW - High-Strength Steel KW - I-Girder KW - Component Test PY - 2016 SN - 978-92-9147-133-1 VL - 2016 SP - 517 EP - 524 PB - Ernst & Sohn AN - OPUS4-37890 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dixneit, Jonny A1 - Kromm, Arne A1 - Hannemann, Andreas A1 - Friedersdorf, Peter A1 - Kannengießer, Thomas A1 - Gibmeier, J. T1 - In-situ load analysis in multi-run welding using LTT filler materials N2 - Modifying the level of mostly detrimental welding residual stresses already during the welding process would be highly attractive as time- and cost-consuming post processing may be prevented. The nature of stress buildup during welding-associated cooling is highly affected by phase transformations. Up to now, it is not clear in which way this is applicable to real component welding exhibiting high shrinkage restraint and complex heat input. In this study, two different low transformation temperature (LTT) alloys have been investigated concerning the stress development in restrained multi-run butt welding in order to evaluate the potential of stress reduction. Pulsed gas metal arc welding (P-GMAW) welding was executed on a testing facility designed to simulate real lifelike restraint conditions of component weldments. The effect of reducedMS-temperatures and the heat control on the globally acting stresses was monitored by in-situ measurement of the reaction forces during welding fabrication. Additional local residual stress measurements allowed analyzing global as well as local loading of the welded construction. Although phase transformation has a significant influence on unloading the joint during each weld pass, the reaction stress upon cooling to room temperature seems to be determined mainly by the heat input. On the surface, low longitudinal residual stresses were observed in case of LTT whereas transverse residual stresses are less affected. T2 - 69th IIW Annual Assembly and International Conference CY - Melbourne, Australia DA - 10.07.2016 KW - Phase transformation temperature KW - Residual stress KW - Welding KW - Dilution KW - Restraint PY - 2016 DO - https://doi.org/10.1007/s40194-016-0373-1 SN - 0043-2288 VL - 60 IS - 6 SP - 1159 EP - 1168 PB - Springer CY - Heidelberg AN - OPUS4-37892 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pasternak, H. A1 - Launert, B. A1 - Rhode, Michael A1 - Kannengießer, Thomas ED - Zingoni, A. T1 - Residual Stresses and Imperfections in Welded High-strength I-shape Sections N2 - This article addresses the imperfections caused by the weld assembly in I-shape sections made of two structural steel grades. Load influencing imperfections are assumed as deviations from the ideal shape (e.g. bending distortion) and longitudinal residual stresses. The quality of a numerically aided design of components exposed to either compression and/or bending is significantly affected, depending on these parameters. The Eurocode (EC3) provides robust simplified models. As a result, the Ultimate Limit State (ULS) is approached on a conservative basis. The following investigations are aimed at providing further guidance on these values in component-like specimens. The long term goal is an improved understanding of the load-bearing capacity of such sections. As a first step in this process, the experimental and corresponding numerical studies are presented. T2 - 6th International Conference on Structural Engineering, Mechanics and Computation (SEMC 2016) CY - Cape Town, South Africa DA - 05.09.2016 KW - Residual Stresses KW - Welding KW - High-strength Steel KW - Numerical Modeling KW - Component PY - 2016 SN - 978-1-138-02927-9 VL - 2016 SP - 1139 EP - 1146 PB - CRC Press, Taylor & Francis Group CY - Boca Raton, FL, USA AN - OPUS4-37888 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas T1 - Einsatz modifizierter Sprühlichtbogenprozesse zur Optimierung schweißbedingter Beanspruchungen an Bauteilen aus hochfesten Feinkornbaustählen N2 - In dem IGF-Vorhaben IGF-Nr. 17978 N (P 1011) wurden unter gezielter definierter Schrumpfbehinderung Schweißexperimente an hochfesten Feinkornbaustählen durchgeführt, um den Einfluss der Wärmeführung sowie den Einsatz modifizierter Sprühlichtbogenprozesse verbunden mit schmaleren Nahtfugen auf die lokalen Eigenspannungen und die Gesamteigenbeanspruchungen an geschweißten Bauteilen zu analysieren. Diese Kurzdarstellung fasst die wesentlichen Zusammenhänge zu schweißbedingten Beanspruchungen an hochfesten Schweißverbindungen sowie einige der erarbeiteten Erkenntnisse und erreichten Ziele des Forschungsprojektes zusammen. KW - Schweißverbindung KW - Eigenspannungen KW - Hochfester Feinkornbaustahl KW - Schweißprozess PY - 2016 SP - 1 EP - 2 AN - OPUS4-38653 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kannengießer, Thomas A1 - Florian, Wolfgang A1 - Wilken, Klaus T1 - Moderne Möglichkeiten der Prüfung und Simulation von Bauteilschweißungen N2 - Die hier vorgestellte Großanlage zur Prüfung und Simulation von Bauteil­ schweißungen (GAPSI 16) mit einer Maximalprüfkraft von ±16 MN erlaubt wirklichkeitsnahe Analysen des Bau­ teilverhaltens während des Schwei­ ßens. Ein fundamentaler Vorteil ge­ genüber konventionellen Universal­ prüfmaschinen ist, Momente während des Schweißens mittels acht unabhän­ giger Hydraulikzylinder in zwei Prüf­ tischen aufbringen bzw. registrieren zu können. Derzeitige Forschungsvorhaben sind zum einen Spannungs- und Verformungsvorgängen während des Schweißens von Blechen und zum anderen Modellen gewidmet, womit Kenngrößen für Flammrichtarbeiten ermittelt werden können. Simulations­ versuche an Großproben tragen we­ sentlich zu höherer Aussagesicherheit bei, zumal konventionelle Prüfmetho­ den mit einfachen Kleinproben und auch Berechnungen nach der Finite­ Elemente-Methode (FEM) stets Rand­ bedingungen und zumeist größere Idealisierungen enthalten. Dagegen weist die Großprüfanlage GAPSI 16 mit angepaßten Probengeometrien und Spannkräften einen neuen Weg. KW - GAPSI 16 KW - Prüfung und Simulation KW - Bauteilschweißungen PY - 1997 SN - 0943-4569 VL - 70 IS - 5 SP - 192 EP - 194 PB - Allianz Versicherungen AG CY - München AN - OPUS4-38257 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kannengießer, Thomas T1 - Crack resistance of supermartensitic steel pipeline welds in offshore industry N2 - The increasing application of supermartensitic steels for welded pipelines is an economical alternative to the hitherto used higher-alloyed materials in the North Sea oil and gas indus-try. Failure in such constructions must at any rate be excluded for economical and ecologi-cal reasons. The application of these steels for the transport of corrosive mixtures may, however, involve hydrogen pickup with subsequent hydrogen-assisted stress corrosion cracking. It is therefore necessary not only to assure the weldability, but particularly to have best possible knowledge of the service behaviour and of the failure risk. In order to ensure the transferability of test results to real joined components, innovative test methods are in-creasingly required to be incorporated into a closed test sequence. It will be demonstrated how it is possible to gain significant advantages from the direct comparison between ex-perimentally determined results from component weld tests on the one hand and material-specific data from small-scale tests on the other hand and numerical simulations. These data that have now been made available are of major importance for industrial applications and are considered to provide a sound basis for realistic lifetime assessments. T2 - Conference Welding and Related Inspection Technologies, IIW CY - Stellenbosch, South Africa DA - 08.03.2006 KW - Supermartensitics KW - Hydrogen pickup KW - Hydrogen diffusion KW - Permeation experiments KW - Component tests KW - Numerical simulation KW - Closed test sequence PY - 2006 SP - 1 EP - 14 PB - Beta Products cc CY - Lyttelton, South Africa AN - OPUS4-38925 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kannengießer, Thomas A1 - Kromm, Arne T1 - Characterising phase transformations of different LTT alloys and their effect on residual stresses and cold cracking N2 - Novel martensitic filler materials with specially adjusted martensite start temperatures (Ms) can counteract the cooling specific shrinkage due to expansion effects of the weld metal associated with phase transformations. That can be exploited to create compressive residual stresses in the weld and adjacent areas, i.e. beneficial for increasing fatigue strength. The Ms temperature is shifted via the chemical composition, mainly by the alloying elements nickel and chromium, resulting as well in different retained austenite contents. Investigations were made using different Low Transformation Temperature (LTT) alloys with varying nickel content. The resulting phase transformation temperatures were – for the first time – detected using high energy synchrotron diffraction and Single Sensor Differential Thermal Analysis (SS-DTA). Compared to angle dispersive diffraction, energy dispersive diffraction offers the possibility to measure residual stresses of the martensite and austenite phase parallel fast in one experiment up to depths of 100 µm. The residual stresses show significant distributions dependent on Ms temperature. The effect on the cold cracking behaviour of these alloys was investigated using the Tekken test. Results show that cold cracking can be avoided when appropriate contents of retained austenite are existent. KW - Austenite KW - Cold cracking KW - Martensite KW - Low themperature KW - Transformation PY - 2011 DO - https://doi.org/10.1007/BF03321286 SN - 0043-2288 VL - 55 IS - 3 SP - 48 EP - 56 PB - International Institute of Welding CY - France AN - OPUS4-38978 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröpfer, Dirk A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Engineering approach to assess residual stresses in welded components N2 - Present trends to lightweight design lead to an expanding relevance of high-strength fine-grained structural steels especially in mobile crane constructions. With growing material strength, the challenge for welding fabrication increases, since high loading capacities and safety requirements have to be accomplished. The utilisation of the high strength potential often requires complex constructions associated with high restraint conditions while welding. Increased residual stresses may occur due to superimposing reaction and restraint stresses, which have to be quantified and evaluated to ensure the safety and integrity of high-strength steel constructions. Particularly, the scope of residual stresses has to be taken into account for different effects in the HAZ, notches, weld and base metal. Commonly, conservative assumptions of residual stresses lead to distinct underestimations of the load bearing capacity particularly for welded high-strength steel constructions. This study concludes results of recent works of the researchers regarding the complex interaction among heat control, material and restraint intensity on the residual stress state in welded components. These analyses are extended by further experiments. Based on the obtained major effects, an approach for a welding residual stress assessment regarding component design according to prevailing standards for crane construction, an important application for high-strength steels, is presented. KW - Process parameters KW - Residual stresses KW - MAG welding KW - Restraint KW - High-strength steels PY - 2017 DO - https://doi.org/10.1007/s40194-016-0394-9 SN - 0043-2288 SN - 1878-6669 VL - 91 IS - 1 SP - 91 EP - 106 PB - Springer CY - Berlin, Heidelberg AN - OPUS4-39044 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Kannengießer, Thomas T1 - List of questions relating to the revision of ISO 3690 regarding the acceptance of the carrier gas hot extraction method N2 - Is it reasonable to restrict ISO 3690 any longer to the determination of the weld metal hydrogen content of ferritic steel? In what respect is the determination of the content of the diffusible and of the total hydrogen content, respectively, (still) merely a research task (supermartensite, duplex materials, austenite, magnesium, aluminium), or is there actually a demand in industry and is there already a first cause for monitoring in view of damage prevention, respectively? Is there a need, arising from the development of materials and filler materials and from their intended applications, for more extensive standards dealing with hydrogen analyses for these materials? Which parts of ISO 3690 could also be applied to any other metallic material/filler material, if necessary, and where would a complete alteration be required, respectively? KW - ISO 3690 KW - List of questions KW - Carrier gas KW - Extraction method PY - 2004 SP - 1 EP - 11 PB - IIW CY - USA AN - OPUS4-39260 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Kannengießer, Thomas A1 - Schröpfer, Dirk T1 - Einsatz modifizierter Sprühlichtbogenprozesse zur Optimierung schweißbedingter Beanspruchungen an Bauteilen aus hochfesten Feinkornbaustählen N2 - Aufgrund aktueller Leichtbaubestrebungen sowie Forderungen nach Energie- und Ressourceneffizienz werden zunehmend hochfeste Feinkornbaustähle mit Streckgrenzen ≥ 690 MPa in modernen Stahlkonstruktionen eingesetzt. Vorrangig werden diese mit Streckgrenzen bis 960 MPa verarbeitet und mittels MAG-Schweißprozessen gefügt. Moderne Invertertechnik ermöglichte jüngst zahlreiche Firmenentwicklungen (bspw. „DeepARC“, „forceArc“), die zu modifizierten Sprühlichtbögen (mod. SLB) mit ähnlichen Eigenschaften führten. Neben den bekannten wirtschaftlichen Vorteilen dieser mod. SLB, lassen gerade die reduzierten möglichen Nahtöffnungswinkel und die geringere Wärmeeinbringung eine positive Wirkung auf schweißbedingte Beanspruchungen erwarten. Erste Eigenspannungsanalysen bei vorangegangenen Schweißeignungsuntersuchen mit mod. SLB zeigten bereits bei freischrumpfenden Laborproben geringere Zugeigenspannungen in der Schweißnaht im Vergleich zu konventionell geschweißten Proben. Die betriebsfeste Auslegung von hochfesten Schweißkonstruktionen und die Ausnutzung hoher Streckgrenzen erfordern jedoch eine ausreichende Quantifizierung schweißbedingter Beanspruchungen der mod. SLB unter definierter, bauteilrelevanter Schrumpfbehinderung. Dies betrifft sowohl die Kräfte und Spannungen im lokalen Schweißnahtbereich als auch die Gesamtbeanspruchung sowie den Einfluss von Wärmeführung, Bauteilgeometrie, Einspanngrad und Nahtöffnungswinkel. Hierzu lagen in der Industrie, besonders bei den KMU, kaum Kenntnisse vor und sollten deshalb als Ziel dieses Forschungsprojektes erarbeitet werden. Die vergleichenden Untersuchungen mit konventionellen Lichtbogen und mod. SLB mit angepasster Nahtkonfiguration erfolgten mithilfe von speziellen Prüfanlagen, mit der reale Bauteilsteifigkeiten abgebildet werden können. Bei beiden Prozessvarianten waren mit den gewählten Parametern Schweißnähte unter Erfüllung der Anforderungen an die mechanisch-technologischen Eigenschaften realisierbar. Bei den Analysen konnte eine signifikante Reduzierung der Eigenbeanspruchungen durch eine verminderte Wärmeeinbringung bei dem Einsatz einer Nahtkonfiguration mit abgesenktem Nahtöffnungswinkel beobachtet werden. Insbesondere erwiesen sich zur Absenkung mehrachsiger Beanspruchungszustände aufgrund von Biegemomenten in den bauteilnahen Schweißungen die engeren Nahtspalte als zielführend. Eine Vorstellung der erarbeiteten Kenntnisse und Empfehlungen in entsprechenden Gremien zur Normung erfolgten, um mittelfristig vor allem den KMU eine einfachere Konstruktionsauslegung und sichere Verarbeitung hochfester Feinkornbaustähle zu ermöglichen. Mit einer normativen Absicherung kann Qualifizierungs- und Zulassungsaufwand eingespart werden, der aktuell beim Einsatz hochfester Stähle vielfach notwendig ist. Ferner werden die Betriebe durch die Ergebnisse in die Lage versetzt, die technischen und wirtschaftlichen Vorteile der mod. SLB-Prozesse auszunutzen und signifikante Einsparungen bei Schweißzusatz, Schweiß- und Rüstzeit sowie unter Berücksichtigung der Eigenbeanspruchung optimierte Ergebnisse hinsichtlich der Tragfähigkeit von Bauteilen zu erreichen und die Produktivität zu erhöhen. KW - MAG-Schweißen KW - Hochfester Stahl KW - Eigenspannungen KW - Kaltrisssicherheit PY - 2017 UR - https://matplus.shop/produkt/p-1011-einsatz-modifizierter-spruehlichtbogenprozesse-zur-optimierung-schweissbedingter-beanspruchungen-an-bauteilen-aus-hochfesten-feinkornbaustaehlen-2 SN - 978-3-946885-12-2 N1 - Das IGF-Vorhaben 17978 N wurde über die Arbeitsgemeinschaft industrieller Forschungsvereinigungen "Otto von Guericke" (AiF) im Rahmen des Programms zur Förderung der Industriellen Gemeinschaftsforschung (IGF) vom Bundesministerium für Wirtschaft und Energie (BMWi) aufgrund eines Beschlusses des Deutschen Bundestages gefördert VL - P 1011 SP - 1 EP - 136 PB - Verlag und Vertriebsgesellschaft CY - Düsseldorf AN - OPUS4-59257 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Influence of the weld geometry on the residual stress reduction using low transformation temperature welding consumables N2 - Low transformation temperature (LTT) welding consumables offer an innovative approach to increase the fatigue strength of welded high-strength steel structures. LTT welding consumables are characterized by a martensitic phase transformation near ambient temperature, which generates compressive residual stresses in the weld and heat affected zone (HAZ). The aim is to achieve a weld geometry, which generate high compressive residual stresses at the fatigue crack critical weld toe. Longitudinal stiffeners were gas metal arc welded using a conventional welding consumable; the base material was a high strength steel S700M. A chromium-nickel alloyed LTT consumable was deposit subsequently just on front sides of the stiffeners. Different welding parameters led to varying cross sections of the weld. The residual stresses were determined using X-ray diffraction (XRD) in the crack critical HAZ. When using only the conventional, the HAZ is characterized by high tensile residual stresses. The additional application of the LTT alloy leads to a significant reduction of the tensile residual stresses. Depending on the weld geometry, even compressive residual stresses can be observed at the weld toe T2 - ECRS 2024 CY - Prague, Czech Republic DA - 03.06.2024 KW - LTT (Low Transformation Temperature) KW - Residual stress reduction KW - Fatigue PY - 2024 AN - OPUS4-60305 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Dittmann, Florian A1 - Varfolomeev, Igor T1 - Effect of weld design on fatigue strength of welded components using LTT filler materials N2 - Low transformation temperature (LTT) filler metals are an innovative approach to reduce tensile residual stress in weld seams and the surrounding heat affected zone (HAZ). The reduced tensile stress leads to an improvement in the fatigue strength of welded components. LTT filler metals are characterized by a reduced martensite start temperature (Ms), which is close to room temperature because of their chemical composition. This paper focuses on the hybrid use of LTT filler metals, where the LTT filler is applied as an additional layer to conventional welds on fatigue-critical spots. Conventional gas metal arc welded longitudinal stiffeners are used as specimens and at the face ends of the stiffeners, a second LTT layer was added with various weld modifications. These modifications were achieved by changing the welding parameters such as welding speed and offset to the first layer. These samples were used to analyze shape, dilution and resulting Ms, residual stress and fatigue strength. The dilution and dilatometer verified Ms did not change significant, although the surface of the 2nd LTT weld seam was varying clear with each modification. However, the weld modification had a significant effect on the residual stress state and the fatigue strength. The X-ray determined residual stress in the HAZ became lower when the weld toe of the LTT layer was further away from the stiffener. The Fatigue strength is clearly dependent on the residual stress state. The lower the residual stress at weld toe, the higher the fatigue strength. All samples with LTT weld exhibit significantly higher fatigue strength values than conventionally single and double-layer welded samples. The results show that on the one hand LTT filler metals increase the fatigue strength, and on the other hand the impact of LTT fillers materials is not restricted to the dilution and Ms, the shape of the weld seam must also be considered. T2 - IIW Intermediate Meeting CII CY - Trollhättan, Sweden DA - 10.03.2025 KW - LTT (Low Transformation Temperature) KW - Residual stress reduction KW - Fatigue strength KW - High-strength steels KW - Welding PY - 2025 AN - OPUS4-62708 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Nina A1 - Rhode, Michael A1 - Kannengießer, Thomas T1 - Einfluss unterschiedlicher Mikrolegierungsrouten eines S690QL auf das Ausscheidungsverhalten in der Wärmeeinflusszone N2 - Mikrolegierungselementen, wie Nb und Ti sind für eine signifikante Festigkeitssteigerung von vergüteten, hochfesten Feinkornbaustählen mit einer Nominalstreckgrenze ≥ 690 MPa unerlässlich. Normvorgaben zur chemischen Zusammensetzung dieser Stähle geben zur Erzielung der vorgeschriebenen Eigenschaften dabei oft nur Grenzgehalte für die Hersteller vor. Die Wirkung der Mikrolegierungselemente bzw. ihrer Karbide und/oder Nitride ist teilweise komplett konträr, insbesondere bei Auflösung und Wiederausscheidung in der WEZ bei identischem Schweißzusatz. Somit wird eine adäquate Vorhersage der Chargenabhängigkeit hinsichtlich der Schweißeignung und des Tragverhaltens der Schweißverbindung erschwert. Eine unerwünschte Eigenschaft ist dabei die Erweichung der WEZ, wie auch u.U. der gegenteilige Effekt der Aufhärtung. Vor diesem Hintergrund werden im Rahmen eines DFG-Vorhabens systematisch Mikrolegierungs-routen mit variierenden Ti- und Nb-Gehalten des hochfesten und vergüteten Feinkornbaustahls S690QL untersucht. Dazu wird das MAG-Schweißen mit modifizierten Sprühlichtbogen verwendet, welches durch hohe Abschmelzleistung gekennzeichnet ist und schmalere Nahtöffnungswinkel (α = 30°) ermöglicht. An Dreilagen-Schweißungen wird der Effekt der metallurgischen Zusammensetzung in Kombination mit hoher Wärmeeinwirkung auf die Ausbildung einer kritischen WEZ-Gefügezone mit Erweichung und/oder exzessiver Aufhärtung untersucht. Ein besonderes Augenmerk wird auf die Phasenumwandlungen und das Ausscheidungsverhalten im Gefüge der Wärmeeinflusszone gelegt. Neben umfangreichen metallographischen Untersuchungen einzelner WEZ-Bereiche wurden, unter Variation der chemischen Zusammensetzung, thermodynamische Phasenberechnungen mittels Thermo-Calc durchgeführt. Hierdurch wird ein Verständnis zur Phasentransformation und Ausscheidungswachstum und -auflösung während des Schweißens in Abhängigkeit von Temperatur und Abkühlbedingungen geschaffen. Das Ziel ist es, den Einfluss der Wärmeeinwirkung auf die Gefügeausbildung in der WEZ und dessen mechanischer Eigenschaften zu analysieren. Insbesondere wird hier auf die Auswirkung der unterschiedlichen Mikrolegierungskonzepte (Ti oder Nb) geachtet. T2 - 5. Symposium Materialtechnik CY - Clausthal-Zellerfeld, Germany DA - 23.02.2023 KW - WEZ Erweichung KW - Thermodynamische Simulation KW - Mikrolegierungseinfluss KW - Schweißen von hochfesten FKB PY - 2023 SN - 978-3-8440-9105-2 VL - 12 SP - 332 EP - 343 PB - Shaker Verlag AN - OPUS4-58006 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kannengießer, Thomas T1 - Metallurgische Einflüsse auf die Wasserstoffversprödung und Kaltrissneigung höherfester geschweißter Offshore-Konstruktionen für die Windenergie N2 - Bei der Fertigung dickwandiger Bauteile durch Schweißverfahren mit großen Abschmelzleistungen kommt es zu einer Wasserstoffversprödung. Diese ist abhängig von den Grundwerkstoff-Zusatzwerkstoff-Kombinationen, welche zu unterschiedlichen Ausscheidungen führen und das Diffusions- und Trappingverhalten des Wasserstoffes im Gefüge beeinflussen. Die metallurgischen Einflüsse sind bisher unbekannt. Es werden Empfehlungen zur Wärmeführung beim Schweißen abgeleitet. Hierzu ist es notwendig, die metallurgie- und mikrostrukturspezifische Wasserstoffdiffusion und -freisetzungstemperatur zu bestimmen. Die Konzepte zur Vermeidung der Kaltrissanfälligkeit werden an UP/MSG-Bauteilschweißungen entwickelt. Ziel ist die Identifikation von metallurgisch günstigen GW-Zusatz-Kombinationen zur a-priori Vermeidung zeitverzögerter wasserstoffunterstützter Kaltrissbildung geschweißter Komponenten aus modernen Stählen. T2 - Sitzung des Arbeitskreises "Fügetechnik für die Windenergie" des DVS e. V. CY - Duisburg, Germany DA - 14.02.2018 KW - Höherfester Stahl KW - Metallurgie KW - Kaltriss KW - Diffusion PY - 2018 AN - OPUS4-44258 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gibmeier, J. A1 - Weidemann, Jens A1 - Dixneit, Jonny A1 - Kannengießer, Thomas A1 - Kromm, Arne T1 - Influence of structural stiffness on the residual stresses during welding of low transformation temperature alloys N2 - Low Transformation Temperature (LTT) alloys are high alloyed filler materials, which exhibit a martensitic phase transformation at comparatively low temperatures in order to prevent high tensile residual stresses. A number of publications have already shown that even compressive residual stresses can be observed when using LTT filler materials. Up to know it is not clear in which way this it applicable to multi-run welding exhibiting high shrinkage restraint and complex heat input. In this study the potential for stress reduction during welding of LTT alloys was studied by numerical simulation. This allows for evaluation of the stress development in every single weid run. Additionally, the impact of the structural stiffness was incorporated by modelling a special sample geometry exhibiting a high intensity of restraint. The results show that the stress formation in weid longitudinal direction is determined by the phase transformation as high compressive residual stresses were found here independent from the weid run. On the other hand the transformation induced stresses in weid transverse direction are superimposed by tensile stresses originated from shrinkage restraint. With increasing number of runs the tensile residual stress level is raised. The results were confirmed by residual stress measurements using diffraction methods. T2 - 11th International Seminar - Numerical Analysis of Weldability CY - Graz, Austria DA - 27.09.2015 KW - Influence KW - Structural stiffness KW - Residual stresses KW - Low transformation KW - Temperature alloys KW - Welding PY - 2016 SN - 978-3-85125-490-7 SN - 2410-0544 SP - 259 EP - 276 PB - Verlag der Technischen Universität Graz CY - Graz AN - OPUS4-38998 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rhode, Michael A1 - Mente, Tobias A1 - Kannengießer, Thomas A1 - Schaupp, Thomas A1 - Zavdoveev, Anatoly T1 - Challenges for testing hydrogen-assisted cold cracking in weld seams of high-strength steel grades N2 - Hydrogen can cause weld cold cracking even days after fabrication. In this respect, higher strength steels present a challenge to established cold crack testing. In general, the tolerable hydrogen concentration for crack prevention decreases with increasing material strength. In addition, advanced welding processes require changes in weld geometry and heat input. This directly influences the formation of crack-critical microstructures, e.g. in hardened areas of the heat-affected zone. The limits of use and application of modern cold cracking tests are evaluated by (1) the externally loaded Implant-test and (2) the self-restraint Tekken-test. In particular, external mechanical stresses, which cause additional mechanical loads on the components during welding, must be considered due to the component-specific stiffness of high-strength steels. Accompanying test methods for determining hydrogen concentration and diffusion in welds are presented, such as carrier gas hot extraction for determining hydrogen concentration (ISO 3690) or temperature-dependent diffusion coefficients. These values are of great importance for a holistic approach to the evaluation of the cold cracking sensitivity of high strength steels. KW - Hydrogen KW - Welding KW - Cold cracking test KW - High-strength steel PY - 2024 DO - https://doi.org/10.37434/tpwj2024.08.01 SN - 0957-798X VL - 2024 IS - 8 SP - 3 EP - 9 PB - International Association "Welding" CY - Kyiv, Ukraine AN - OPUS4-60946 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kaiser, Sebastian A1 - Erxleben, Kjell A1 - Rhode, Michael A1 - Kannengießer, Thomas T1 - Repair Welding of In-Service Hydrogen Pipelines - Concepts and Challenges N2 - Hydrogen is set as the energy carrier of tomorrow for a more sustainable fossil fuel free future. As this necessitates a reliable transport infrastructure, repurposing of the existing natural gas grid is planned. With regards to the well-known effect of hydrogen embrittlement, the compatibility of utilized materials must be investigated. First comprehensive studies on pipeline material hydrogen compatibility indicate that these materials can be applied to a certain extent. Nonetheless, the material compatibility is currently of high interest and focus of numerous research projects worldwide. However, pipelines require frequent maintenance and repair work. As part of these, in some cases it is necessary to do weldments onto pipelines while they are pressurized. This in-service welding introduces additional challenges for the material compatibility. Due to the resulting high temperatures, the metallurgical changes in the material and of course the presence of high-pressure hydrogen in the pipeline, additional investigations need to be conducted to ensure that no critical material degradation because of increased hydrogen absorption occurs and an overall material compatibility is given. For this reason, the present paper introduces in-service welding on pipelines. An overview of current research projects that deal with the application of in-service welding specifically on hydrogen pipelines and the emerging problems when applying these techniques on hydrogen pipelines is given. Methods of material testing, their limits and possible solutions are presented and discussed. T2 - 2024 15th International Pipeline Conference CY - Calgary, Alberta, Canada DA - 23.09.2024 KW - Hydrogen KW - Pipeline KW - Welding KW - In-Service PY - 2024 SN - 978-0-7918-8856-8 DO - https://doi.org/10.1115/IPC2024-133052 SP - 1 EP - 6 PB - The American Society of Mechanical Engineers (ASME) CY - New York AN - OPUS4-62262 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -