TY - CONF A1 - Brinkmann, A. T1 - A qNMR Method for Quantification of Surface Functional Groups on Silica Nanoparticles: Bilateral Comparisons N2 - Nanomaterials (NM) of different size, shape, morphology, composition, and surface chemistry are used in a wide range of applications, including medical diagnostics, and imaging and consumer products. The importance of an adequate and reliable characterization is crucial for quality control during NM production, for ensuring an optimum function for the desired application, and for risk assessment studies. Currently there is a lack of reliable and validated methods and reference materials for quantifying NM surface functional groups, despite the importance of surface chemistry for the production of colloidally stable materials, further processing steps, and the interaction with the environment and biological species. Following our initial study on the use of qNMR for quantifying the amount of amino groups on surface modified silica (1), we have carried out two bilateral comparisons between NRC and BAM to further develop and optimize a reliable protocol for these measurements (2,3), using aminated silica nanoparticles prepared by multiple methods, both commercial and in-house synthesized, and with varying amine content. Solution qNMR is based on dissolving aminated silica nanoparticles in strong base to release the surface grafted amino silane molecules, followed by the quantification of these molecules by solution qNMR using an internal standard. This method provides the amount of total amino groups present in the sample, which can differ from probe accessible or surface-sensitive measurements performed with X-Ray photoelectron spectroscopy (XPS). Complementary measurements using optical assays, involving a labeling step with a dye reporter, and XPS are employed to assess the probe accessible and surface amine content for representative samples. These measurements, which illustrate the advantages and potential limitations of the different characterization methods, will contribute to establish a basis for testing the protocol in an international inter-laboratory comparison and for standardization at ISO Technical Committee 229 – Nanotechnologies. T2 - BERM CY - Halifax, Canada DA - 01.06.2025 KW - Quality assurance KW - Nano KW - Particle KW - Synthesis KW - Advanced materials KW - Characterization KW - Electron microscopy KW - Silica KW - Surface KW - qNMR KW - Optical assay KW - Interlaboratory comparison KW - Metrology KW - Standardization PY - 2025 AN - OPUS4-63527 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Tavernaro, Isabella A1 - Abram, Sarah-Luise A1 - Homann, Christian A1 - Scholtz, Lena A1 - Radnik, Jörg A1 - Resch-Genger, Ute T1 - Validated and standardized measurements and quantification of surface functionalities on nanoparticles N2 - Surface-functionalized organic and inorganic engineered nanomaterials (NMs) are widely applied in the life and materials sciences. NM performance depends on key factors such as particle size and shape, crystal phase, morphology, chemical composition, and surface chemistry, i.e., surface coatings, functional groups (FGs), and ligands.1 The latter controls their processability and interaction with the environment and largely their possible toxicity. Thus, methods for FG quantification are important tools for quality control of NM production processes and can foster the sustainable development of functional and safe(r) NMs. This underlines the importance of validated and standardized analytical methods for surface analysis and reference materials.2 This encouraged us to explore simple and versatile tools for quantifying common bioanalytically relevant FGs such as optical assays, electrochemical titration methods, quantitative nuclear magnetic resonance spectroscopy (qNMR), and X-Ray photoelectron spectroscopy (XPS) and to perform a first interlaboratory comparison (ILC) on surface FG quantification.3,4 In a follow-up ILC, BAM and NRC explored qNMR sample preparation, measurement, and data evaluation protocols for commercial and custom-made aminated SiO2 NPs with sizes of 20-100 nm, different amounts of surface amino FGs, and different porosity.5,6 First, the number of amino FGs accessible for a dye reporter was determined with a cost-efficient, automated optical fluorescamine assay. Then, qNMR workflows and protocols were stepwise fine-tuned. The qNMR ILC was complemented by joint XPS measurements. BAM also examined the applicability of fast and automatable potentiometric titrations to screen the total amount of (de)protonable FGs on aminated SiO2 NPs. Our results underline the need to evaluate protocols for FG quantification in ILCs and the advantages of multi-method characterization strategies for efficient method cross validation. T2 - Surface and Micro/Nano Analysis Working Group CY - Paris, France DA - 08.04.2025 KW - Quality assurance KW - Reference material KW - Fluorescence KW - Nano KW - Particle KW - Surface analysis KW - XPS KW - Traceability KW - Metrology KW - Calibration KW - Reference data KW - Reference product KW - Digital certificate KW - QNMR KW - Potentiometry PY - 2025 AN - OPUS4-62969 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Portesi, C. T1 - qNMR for standardised measurements of surface functionalities on nanoparticles N2 - Engineered nanoparticles have a large application potential in fields such as medicine, sensing, catalysis, energy storage, and opto-electronics [1]. The applicability and performance of engineered nanoparticles is largely determined by their surface chemistry, i.e. functional groups and ligands on the particle surface. However, documented standards to quantify functional groups and ligands currently do not exist. Such standards are required to support quality control of nanomaterial production and surface modification processes, and safe-by-design concepts and to meet regulatory requirements. Here, this issue is addressed by developing and standardizing quantitative Nuclear Magnetic Resonance (qNMR) methods for the characterization of surface functionalized nanoparticles which specifically address the determination of the amount and chemical composition of surface functionalities and coatings. This work is being developed under the EMP project 23NRM02 SMURFnano - Standardised measurements of surface functionalities on nanoparticles. qNMR competence of 7 qNMR laboratories involved in the project was first tested with a molecular model sample i.e. citrate, to be assessed in terms of purity. Citrate is often used as hydrophilic surface ligand for different nanoparticles. Then, the first nanoparticle samples, here a set of aminated SiO2 NPs [1] with a particle size of 100 nm and two amino group densities, prepared and characterized by BAM regarding size and surface charge as well as stability over 21 months with an optical assay and qNMR, were assessed in an international interlaboratory comparison (ILC) on qNMR. Thereby, the amount of surface amino groups introduced by grafting of the silica cores with different amounts of 3-aminopropyl)triethoxysilane (APTES) was quantified by each participant following a sample preparation protocol previously developed by BAM and NRC.The results of the ILC were then used to refine the protocol for sample preparation and to identify critical points for qNMR measurement and data analysis. This work will contribute to the development of a Preliminary Work Item (PWI) 19257 (ISO/TC 229) on surface functional groups and coatings on nano-objects. Also, it will lay the groundwork to perform ILCs on the quantification and determination of the amount of surface functional groups under the roof of VAMAS TWA2 (Surface Chemical Analysis) for different types of nanomaterials possessing industry-relevant surface functionalities using qNMR. These ILCs will be complemented by other techniques like X-Ray photoelectron spectroscopy (XPS) and time-of-flight secondary ion mass spectrometry (ToF-SIMS). T2 - BERM CY - Halifax, Canada DA - 01.06.2025 KW - Quality assurance KW - Nano KW - Particle KW - Synthesis KW - Advanced materials KW - Characterization KW - Electron microscopy KW - Silica KW - Surface KW - qNMR KW - Optical assay KW - Interlaboratory comparison KW - Metrology KW - Validation KW - Standardization PY - 2025 AN - OPUS4-63443 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Resch-Genger, Ute T1 - Quantifying the total and accessible amount of surface functionalities and ligands on nano-materials: Overview and recommended methods N2 - Engineered nanoparticles (NPs) with various chemical compositions and surface functionalities are routinely fabricated for industrial applications such as medical diagnostics, drug delivery, sensing, catalysis, energy conversion and storage, opto-electronics, and information storage. NP function, interaction with biological species, and environmental fate are largely determined by surface functionalities. This calls for reliable, reproducible, and standardized surface characterization methods, which are vital for quality control of NPs, and mandatory to meet increasing concerns regarding their safety. Validated and standardized workflows for surface analysis are also increasingly requested by industry, international standardization organizations, regulatory agencies, and policymakers. To establish comparable measurements of surface functionalities across different labs and ease instrument performance validation, reference test materials and reference materials of known surface chemistry as well as reference data are needed. In the following, different methods for determining surface functionalities on ligand-stabilized core and core/shell NPs include advanced techniques are presented and discussed regarding method-inherent advantages and limitations. Special emphasis is dedicated to traceable quantitative nuclear magnetic resonance (qNMR), X-ray electron spectroscopy (XPS) and time of flight secondary ion mass spectrometry (ToF-SIMS), and simpler optical and electrochemical methods. T2 - LNE Workshop CY - Paris, France DA - 04.11.2025 KW - Quality assurance KW - Fluorescence KW - Nano KW - Particle KW - Synthesis KW - Characterization KW - Advanced material KW - Surface KW - Standardization KW - Reference material KW - Functional group KW - Quantification KW - Coating KW - Automation KW - Potentiometry KW - Method KW - Validation KW - Optical assay KW - Fluram KW - Fluorescamine KW - qNMR KW - Comparison KW - ILC PY - 2025 AN - OPUS4-64726 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Resch-Genger, Ute T1 - Standardized Measurements of Surface - Functionalities on Nanoparticles N2 - Engineered nanoparticles (NPs) with various chemical compositions and surface functionalities are routinely fabricated for industrial applications such as medical diagnostics, drug delivery, sensing, catalysis, energy conversion and storage, optoelectronics, and information storage. NP function, interaction with biological species, and environmental fate are largely determined by surface functionalities. Reliable, reproducible, and standardized surface characterization methods are therefore vital for quality control of NPs, and mandatory to meet increasing concerns regarding their safety. Also, industry, international standardization organizations, regulatory agencies, and policymakers need validated and standardized measurement methods and reference materials. However, methodologies for determining NP surface properties, including the amount, chemical composition, and homogeneity of surface functionalities and coatings are largely non-standardized. Suitable methods for determining surface functionalities on ligand-stabilized core and core/shell NPs include advanced techniques such as traceable quantitative nuclear magnetic resonance (qNMR) as well as X-ray electron spectroscopy (XPS) and time of flight secondary ion mass spectrometry (ToF-SIMS), and simpler optical and electrochemical methods. The latter less costly methods are often used by SMEs, e.g., for quality control. To validate methods, establish measurement uncertainties, test reference materials, and produce reference data, international interlaboratory comparisons (ILC) on NP surface functionalization measurements are required and well characterized test and reference nanomaterials providing benchmark values.[1] These needs are addressed by the recently started European metrology project SMURFnano involving 12 partners from different National Metrology Institutes, designated institutes, and research institutes, two university groups as well as one large company and one SME producing NPs. This project as well as first results derived from the development of test and reference materials with a well characterized surface chemistry and ongoing interlaboratory comparisons will be presented. T2 - eMRS CY - Strasbourg, France DA - 27.05.2025 KW - Quality assurance KW - Fluorescence KW - Nano KW - Particle KW - Synthesis KW - Silica KW - Upconversion nanoparticles KW - Optical assay KW - qNMR KW - Surface analysis KW - Ligand KW - Quantification KW - Functional group KW - XPS KW - ToF-SIMS KW - Polymer particle KW - Surface modification KW - Potentiometry KW - Metrology KW - Method KW - Validation KW - ILC PY - 2025 AN - OPUS4-63339 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Resch-Genger, Ute T1 - Standardized Measurements of Surface Functionalities on Nanoparticles - F. Synthesis and characterization of functional nanocomposite materials N2 - Engineered nanoparticles (NPs) with various chemical compositions and surface functionalities are routinely and commonly fabricated for industrial applications such as medical diagnostics, drug delivery, sensing, catalysis, energy conversion and storage, opto-electronics, and information storage. NP function, their interaction with biological species, and also their environmental fate are largely determined by the surface functionalities of the particles. Reliable, reproducible, and standardized surface characterization methods are therefore vital for quality control of NPs, determination of their applicability, and mandatory to meet increasing concerns regarding their safety. In addition, industry as well as international standardization organizations, regulatory agencies, and policymakers need validated and standardized measurement methods and reference materials. However, methodologies for determining NP surface properties, including the amount, chemical composition, and homogeneity of surface functionalities and coatings are largely non-standardized up until now. Suitable methods for determining surface functionalities on ligand-stabilized core and core/shell NPs include advanced techniques such as traceable quantitative nuclear magnetic resonance (qNMR), as well as X-ray electron spectroscopy (XPS) and time of flight secondary ion mass spectrometry (ToF-SIMS), and simpler optical and electrochemical methods. The latter, typically less costly methods are often used by SMEs, e.g., for quality control. To validate methods, establish measurement uncertainties, test reference materials, and produce reference data, international interlaboratory comparisons (ILC) on NP surface functionalization measurements are required to provide well characterized test and reference nanomaterials including benchmark values.[1] These needs are addressed by the current European metrology project SMURFnano, involving 12 partners from different National Metrology Institutes, designated and research institutes, two university groups as well as one large company and one SME producing NPs. This project, as well as first results derived from the development of test and reference materials with a well characterized surface chemistry, and ongoing interlaboratory comparisons, will be presented. T2 - Shift 2025 CY - La Laguna, Tenerife DA - 13.10.2025 KW - Nano KW - Particle KW - Silica KW - Iron oxide KW - Lanthanide KW - Metrology KW - Quality assurance KW - Reference material KW - Surface chemistry KW - Size KW - Shape KW - Particle number concentration KW - Method KW - Optical assay KW - qNMR KW - Validation KW - Potentiometry KW - XPS KW - ILC KW - Standardization PY - 2025 AN - OPUS4-64370 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - de O. Primo, J. A1 - Horsth, D.F. A1 - de S. Correa, J. A1 - Das, A. A1 - Bittencourt, C. A1 - Umek, P. A1 - de Oliveira Guilherme Buzanich, Ana A1 - Radtke, Martin A1 - Yusenko, Kirill A1 - Zanetta, C. A1 - Anaissi, F.J. T1 - Synthesis and Characterization of Ag/ZnO Nanoparticles for Bacteria Disinfection in Water N2 - n this study, two green synthesis routes were used for the synthesis of Ag/ZnO nanoparticles, using cassava starch as a simple and low-cost effective fuel and Aloe vera as a reducing and stabilizing agent. The Ag/ZnO nanoparticles were characterized and used for bacterial dis- infection of lake water contaminated with Escherichia coli (E. coli). Characterization indicated the formation of a face-centered cubic structure of metallic silver nanoparticles with no insertion of Ag into the ZnO hexagonal wurtzite structure. Physicochemical and bacteriological analyses described in “Standard Methods for the Examination of Water and Wastewater” were used to evaluate the efficiency of the treatment. In comparison to pure ZnO, the synthesized Ag/ZnO nanoparticles showed high efficiencies against Escherichia coli (E. coli) and general coliforms present in the lake water. These pathogens were absent after treatment using Ag/ZnO nanoparticles. The results indicate that Ag/ZnO nanoparticles synthesized via green chemistry are a promising candidate for the treatment of wastewaters contaminated by bacteria, due to their facile preparation, low-cost synthesis,and disinfection efficiency. KW - Synchrotron KW - BAMline PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-562440 DO - https://doi.org/10.3390/nano12101764 SN - 2079-4991 VL - 12 IS - 10 SP - 1 EP - 18 PB - MDPI CY - Basel AN - OPUS4-56244 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Margreiter, R. A1 - Baumann, J. A1 - Mantouvalou, I. A1 - Radtke, Martin A1 - Reinholz, Uwe A1 - Strub, E. T1 - Investigations on fire-gilding N2 - Fire-gilding is a historic technique for the application of golden layers on a number of different base materials utilizing a gold amalgam. This technique leaves a significant amount of Hg in the golden layer, giving archeometrists a reliable indicator to identify firegildings. Recent findings on presumably fire-gilded objects have shown in several cases significantly lower Hg content than previously studied objects. This prompted a synchrotron-based X-ray fluorescence investigation into the Hg distribution along the material–gilding interface, as well as a series of measurements regarding the Hg content development in fire-gilded samples during artificial aging. This work presents findings on laboratory-prepared fire-gildings, indicating an Hg enrichment at the interface of firegilded silver samples. Notably, such an enrichment is missing in fire-gilded copper samples. Further, it is confirmed that fire-gilded layers typically do not undercut an Hg bulk content of 5%. In this light, it seems improbable that ancient samples that contain <5% Hg are fire-gilded. The results presented in this study might lead to a non-destructive method to identify the Hg enrichment at the interface. This might be obtained by a combination of different non-destructive measurements and might also work unambiguously in samples in which the gold top layer is altered. KW - BAMline KW - X-Ray Fluorescence KW - Gilding KW - Depth profile KW - Archaeometry PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-552885 DO - https://doi.org/10.1111/arcm.12797 SN - 0003-813X SP - 1 EP - 14 PB - Wiley online library AN - OPUS4-55288 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dobosy, Péter A1 - Nguyen, Hoang Thi Phuong A1 - Záray, Gyula A1 - Streli, Christina A1 - Ingerle, Dieter A1 - Ziegler, Philipp A1 - Radtke, Martin A1 - de Oliveira Guilherme Buzanich, Ana A1 - Endrédi, Anett A1 - Fodor, Ferenc T1 - Effect of iodine species on biofortification of iodine in cabbage plants cultivated in hydroponic cultures N2 - Iodine is an essential trace element in the human diet because it is involved in the synthesis of thyroid hormones. Iodine deficiency affects over 2.2 billion people worldwide, making it a significant challenge to find plant-based sources of iodine that meet the recommended daily intake of this trace element. In this study, cabbage plants were cultivated in a hydroponic system containing iodine at concentrations ranging from 0.01 to 1.0 mg/L in the form of potassium iodide or potassium iodate. During the experiments, plant physiological parameters, biomass production, and concentration changes of iodine and selected microelements in different plant parts were investigated. In addition, the oxidation state of the accumulated iodine in root samples was determined. Results showed that iodine addition had no effect on photosynthetic efficiency and chlorophyll content. Iodide treatment did not considerably stimulate biomass production but iodate treatment increased it at concentrations less than 0.5 mg/L. Increasing iodine concentrations in the nutrient solutions increased iodine content in all plant parts; however, the iodide treatment was 2–7 times more efficient than the iodate treatment. It was concluded, that iodide addition was more favourable on the target element accumulation, however, it should be highlighted that application of this chemical form in nutrient solution decreased the concetrations of selected micoelement concentration comparing with the control plants. It was established that iodate was reduced to iodide during its uptake in cabbage roots, which means that independently from the oxidation number of iodine (+ 5, − 1) applied in the nutrient solutions, the reduced form of target element was transported to the aerial and edible tissues. KW - BAMline KW - XANES KW - Synchrotron KW - Lodine PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-608330 DO - https://doi.org/10.1038/s41598-024-66575-z VL - 14 IS - 1 SP - 1 EP - 12 PB - Springer Science and Business Media LLC AN - OPUS4-60833 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Huang, Junhao A1 - Klahn, Marcus A1 - Tian, Xinxin A1 - Bartling, Stephan A1 - Zimina, Anna A1 - Radtke, Martin A1 - Rockstroh, Nils A1 - Naliwajko, Pawel A1 - Steinfeldt, Norbert A1 - Peppel, Tim A1 - Grunwaldt, Jan‐Dierk A1 - Logsdail, Andrew J. A1 - Jiao, Haijun A1 - Strunk, Jennifer T1 - Fundamental Structural and Electronic Understanding of Palladium Catalysts on Nitride and Oxide Supports N2 - The nature of the support can fundamentally affect the function of a heterogeneous catalyst. For the novel type of isolated metal atom catalysts, sometimes referred to as single‐atom catalysts, systematic correlations are still rare. Here, we report a general finding that Pd on nitride supports (non‐metal and metal nitride) features a higher oxidation state compared to that on oxide supports (non‐metal and metal oxide). Through thorough oxidation state investigations by X‐ray absorption spectroscopy (XAS), X‐ray photoelectron spectroscopy (XPS), CO‐DRIFTS, and density functional theory (DFT) coupled with Bader charge analysis, it is found that Pd atoms prefer to interact with surface hydroxyl group to form a Pd(OH)x species on oxide supports, while on nitride supports, Pd atoms incorporate into the surface structure in the form of Pd−N bonds. Moreover, a correlation was built between the formal oxidation state and computational Bader charge, based on the periodic trend in electronegativity. KW - BAmline KW - XANES KW - Catalyst PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-608341 DO - https://doi.org/10.1002/anie.202400174 SN - 1433-7851 VL - 63 IS - 20 SP - 1 EP - 9 PB - Wiley AN - OPUS4-60834 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Förste, F. A1 - Bauer, L. A1 - Streeck, C. A1 - Radtke, Martin A1 - Reinholz, Uwe A1 - Kadow, D. A1 - Keil, C. A1 - Mantouvalou, I. T1 - Quantitative Analysis and 2D/3D Elemental Imaging of Cocoa Beans Using X‑ray Fluorescence Techniques N2 - As an important raw material for the confectionery industry, the cocoa bean (Theobroma cacao L.) has to meet certain legal requirements in terms of food safety and maximum contaminant levels in order to enter the cocoa market. Understanding the enrichment and distribution of essential minerals but also toxic metals is of utmost importance for improving the nutritional quality of this economically important raw food material. We present three X-ray fluorescence (XRF) techniques for elemental bio-imaging of intact cocoa beans and one additional XRF technique for quantitative analysis of cocoa pellets. The interrelation of all the methods presented gives a detailed picture of the content and 3D-resolved distribution of elements in complete cocoa beans for the first time. KW - BAMline KW - Synchrotron KW - XRF KW - CXC KW - Cocoa PY - 2023 DO - https://doi.org/10.1021/acs.analchem.2c05370 VL - 95 SP - 5627 EP - 5635 PB - ACS Publications AN - OPUS4-57832 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - de Oliveira Guilherme Buzanich, Ana T1 - Recent developments of X-ray absorption spectroscopy as analytical tool for biological and biomedical applications N2 - X-ray absorption spectroscopy (XAS), in its various modalities, has gained exponential attention and applicability in the field of biological and biomedical systems. Particularly in this field, challenges like low concentration of analyte or proneness to radiation damage have certainly settle the basis for further analytical developments, when using X-ray based methods. Low concentration calls for higher sensitivity—by increasing the detection limits (DL); while susceptibility for radiation damage requires shorter measurement times and/or cryogenic sample environment possibilities. This manuscript reviews the latest analytical possibilities that make XAS more and more adequate to investigate biological or biomedical systems in the last 5 years. KW - Biological & biomedical applications KW - TXRF-XAS KW - HERFD-XAS KW - RXES KW - Quick-XAS KW - Dispersive-XAS PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-531206 DO - https://doi.org/10.1002/xrs.3254 SN - 0049-8246 VL - 51 IS - 3 SP - 1 EP - 10 PB - John Wiley & Sons Ltd AN - OPUS4-53120 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Radtke, Martin A1 - Reinholz, Uwe A1 - Guerra, M.F. A1 - Martinón-Torres, M. A1 - Lemasson, Q. A1 - Moignard, B. A1 - Pacheco, C. A1 - Pichon, L. A1 - Macdonald, L. A1 - Hess, M. A1 - Tissot, I. ED - Guerra, M. F. ED - Martinón-Torres, M. ED - Quirke, S. T1 - Analytical approaches to Egyptian goldwork N2 - The structure and composition of ancient gold objects retain information about their long history of manufacture, from the exploitation of the ore to the finishing touches, as well as evidence of their use, deposition, and degradation. By developing an efficient analytical strategy, it is possible to retrieve that information. This chapter sets the necessary foundation 131to explore fully the analytical results presented in the following chapters of this volume. The techniques employed in the analyses of the Egyptian jewellery are described and the analytical parameters provided. For more established techniques, only brief introductions are presented, while more recent developments are presented in greater detail. KW - Gold KW - Synchrotron KW - D2XRF KW - Egypt PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-586039 DO - https://doi.org/10.17863/CAM.99681 SP - 131 EP - 191 AN - OPUS4-58603 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Peters, Stefan A1 - Bartling, Stephan A1 - Parlinska-Wojtan, Magdalena A1 - Wotzka, Alexander A1 - de Oliveira Guilherme Buzanich, Ana A1 - Wohlrab, Sebastian A1 - Abdel-Mageed, Ali M. T1 - Stabilization of intermediate Mo oxidation states by Nb doping enhancing methane aromatization on Mo/HZSM-5 catalysts N2 - The dehydroaromatization of methane is a promising process to produce aromatics and ultra-pure hydrogen. Increased yields and stability of Mo/HZSM-5 against irreversible deactivation were achieved via a redox interaction by doping with otherwise inert Nb. KW - General Materials Science KW - Sustainability and the Environment KW - General Chemistry KW - Renewable Energy PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-597670 DO - https://doi.org/10.1039/D3TA07532J SN - 2050-7488 SP - 1 EP - 16 PB - Royal Society of Chemistry (RSC) AN - OPUS4-59767 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Radtke, Martin A1 - Rakotondrajoa, A. T1 - Machine learning based quantification of synchrotron radiation-induced X-ray fluorescence measurements - a case study N2 - In this work, we describe the use of artificial neural networks for the quantification of X-ray fluorescence measurements. The training data were generated using Monte Carlo simulation, which avoided the use of adapted reference materials. The extension of the available data set by means of an ANN to generate additional data was demonstrated. Particular emphasis was put on the comparability of simulated and experimental data and how the influence of deviations can be reduced. The search for the optimal hyperparameter, manual and automatic, is also described. For the presented case, we were able to train a network with a mean absolute error of 0.1 weight percent for the synthetic data and 0.7 weight percent for a set of experimental data obtained with certified reference materials. KW - Machine learning KW - BAMline KW - XRF KW - Synchrotron KW - Neural network PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-519008 DO - https://doi.org/10.1088/2632-2153/abc9fb SP - 1 EP - 16 PB - IOP Publishing AN - OPUS4-51900 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weidner, Steffen A1 - Meyer, A. A1 - Falkenhagen, Jana A1 - Kricheldorf, H. R. T1 - SnOct2-catalyzed and alcohol-initiated ROPs of L-lactide – About the influence of initiators on chemical reactions in the melt and the solid state N2 - SnOct2 (Sn(II) 2-ethylhexanoate) catalyzed ROPs of L-lactide were performed in bulk with eight different alcohols as initiators. The time was varied between 1 h and 24 h for all initiators. For two initiators the temperature was also lowered to 115 ◦C. Even-numbered chains were predominantly formed in all polymerizations at short times, but the rate of transesterification (e.g. even/odd equilibration) and the molecular weight distribution were found to depend significantly on the nature of the initiator. Observed transesterification reactions also continued in solid poly (L-lactide), and with the most active initiator, almost total equilibration was achieved even at 130 ◦C. This means that all chains including those of the crystallites were involved in transesterification reactions proceeding across the flat surfaces of the crystallites. The more or less equilibrated crystalline polylactides were characterized by DSC and SAXS measurements with regard to their melting temperature (Tm), crystallinity and crystal thickness. KW - Polylactide KW - MALDI-TOF MS KW - Crystallization KW - Catalysts KW - SAXS PY - 2021 DO - https://doi.org/10.1016/j.eurpolymj.2021.110508 VL - 153 SP - 110508 PB - Elsevier Ltd. AN - OPUS4-52633 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Falkenhagen, Jana A1 - Beskers, Timo. F. A1 - Myxa, Anett A1 - Pursch, Matthias T1 - Round-robin test for size exclusion chromatography – Data summary N2 - Size exclusion chromatography (SEC or GPC) is one critical component of polymer analysis to meet the increasing requirements in regulatory context – namely, determination of Mn, as well as oligomers of less than 500 g mol-1 and 1000 g mol-1. The underlying test methods (OECD 118/119 and DIN EN ISO 13885 1 to 3) provide a framework for SEC measurements; however, they lack sufficient specificity to obtain accurate results. Previous SEC round robin tests were mostly performed on homopolymers and did not collect data on oligomer contents. A new round robin test was initiated and conceptualized within the Task force “Method Evaluation for Polymer REACh (MeEP)”, an initiative of “Industrieforum Analytik” within the German Chemical Society (GDCh). Samples for this study were selected to represent both easy benchmark polymers as well as real-life, industry-relevant polymer materials. Data collection focused on the regulatory requirements. Distribution of samples, gathering of individual results and evaluation were carried out by BAM. A data summary as initial result is reported here. Further evaluation and interpretation are a part of ongoing research. KW - Size exclusion chromatography KW - Polymers KW - Oligomer content KW - Round-robin test PY - 2026 DO - https://doi.org/10.26272/opus4-65587 SP - 1 EP - 84 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-65587 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Martins, Ines A1 - Al-Sabbagh, Dominik A1 - Bentrup, U. A1 - Marquardt, Julien A1 - Schmid, Thomas A1 - Scoppola, E. A1 - Kraus, Werner A1 - Stawski, Tomasz A1 - de Oliveira Guilherme Buzanich, Ana A1 - Yusenko, Kirill A1 - Weidner, Steffen A1 - Emmerling, Franziska T1 - Formation Mechanism of a Nano-Ring of Bismuth Cations and Mono-Lacunary Keggin-Type Phosphomolybdate N2 - A new hetero-bimetallic polyoxometalate (POM) nano-ring was synthesized in a one-pot procedure. The structure consists of tetrameric units containing four bismuth-substituted monolacunary Keggin anions including distorted [BiO8] cubes. The nano-ring is formed via self-assembly from metal precursors in aqueous acidic medium. The compound (NH4)16[(BiPMo11O39)4] ⋅ 22 H2O; (P4Bi4Mo44) was characterized by single-crystal X-ray diffraction, extended X-ray absorption fine structure spectroscopy (EXAFS), Raman spectroscopy, matrix-assisted laser desorption/ionisation-time of flight mass spectrometry (MALDI-TOF), and thermogravimetry/differential scanning calorimetry mass spectrometry (TG-DSC-MS). The formation of the nano-ring in solution was studied by time-resolved in situ small- and wide-angle X-ray scattering (SAXS/WAXS) and in situ EXAFS measurements at the Mo−K and the Bi−L3 edge indicating a two-step process consisting of condensation of Mo-anions and formation of Bi−Mo-units followed by a rapid self-assembly to yield the final tetrameric ring structure. KW - Bismuth KW - In situ EXAFS KW - In situ SAXS/WAXS KW - Lacunary Keggin ion KW - Polyoxometalates KW - Self-assembly PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-546823 DO - https://doi.org/10.1002/chem.202200079 SN - 0947-6539 VL - 28 IS - 27 SP - 1 EP - 7 PB - Wiley-VCH CY - Weinheim AN - OPUS4-54682 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Altmann, Korinna A1 - Goedecke, Caroline A1 - Bannick, C.-G. A1 - Abusafia, A. A1 - Scheid, C. A1 - Steinmetz, H. A1 - Paul, Andrea A1 - Beleites, C. A1 - Braun, U. T1 - Identification of microplastic pathways within a typical European urban wastewater system N2 - In recent years, thermoextraction/desorption-gas chromatography/mass spectrometry (TED-GC/MS) has been developed as a rapid detection method for the determination of microplastics (MP) mass contents in numerous environmentally relevant matrices and, in particular, for the measurement of polymers in water samples without time-consuming sample preparation. The TED-GC/MS method was applied to investigate a typical European municipal wastewater system for possible MP masses. Such investigations are important in view of the recent revision of the Urban Wastewater Treatment Directive. Four different representative sampling sites were selected: greywater (domestic wastewater without toilet), combined sewer, and influent and effluent of a wastewater treatment plant (WWTP). All samples were collected by fractional filtration. Filtration was carried out over mesh sizes of 500, 100, 50, and in some cases, 5 µm. Polyethylene (PE), polypropylene (PP), and polystyrene (PS) were detected in all samples, with the PE fraction dominating in all cases. Styrene-butadiene rubber which serves as an indication of tire abrasion, was only found in the influent of the WWTP. The highest MP mass contents were found in the combined sewer, so MP can become a source of pollution during heavy rain events when the capacity limits of the effluent are reached, and the polluted effluent is released uncontrolled into the environment. Based on the studies, MP retention from the WWTP could be estimated to be approximately 96%. Few trends in polymer type or mass contents were detected within the different fractions of the samples or when comparing samples to each other. KW - Microplastics KW - Microplastic analysis KW - TED-GC/MS KW - Microplastic pathways KW - Mass contents PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-568289 DO - https://doi.org/doi.org/10.1002/appl.202200078 SP - 1 EP - 10 PB - Wiley-VCH CY - Weinheim AN - OPUS4-56828 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Oksal-Kilinc, Sefine A1 - Altmann, Korinna A1 - Seiwert, Bettina A1 - Reemtsma, Thorsten A1 - Ruess, Liliane T1 - Grinding method and oxidative aging modulate the impact of tire wear microplastics on the reproduction of the nematode C. elegans N2 - Rationale Tire abrasion is one of the largest sources of microplastic in aquatic and terrestrial environments. Despite this fact, research on tire wear microplastic (TWP) and its effects on soil ecosystems is scarce, especially regarding natural weathering processes. This leaves a large knowledge gap on the interactions of TWP with soil biota. Methodology Cryo-milled tire tread (CMTT) and diamond-ground tire tread (DGTT) were artificially weathered through dry ozone treatment and heat exposure. Particles were analyzed via scanning electron microscopy, particle size distribution, and shape characterization. TWP leachate composition was examined using liquid chromatography–mass spectrometry. The impact on the reproduction of the nematode Caenorhabditis elegans, a widely used toxicological model, was tested for leachate concentration, exposure duration and TWP aging status, using offspring per adult as the endpoint. Results The comminution method significantly influenced TWP particle size distribution, with diamond grinding yielding smaller particles and a more structured surface morphology than cryo-milling. Aging with ozone (180 min) and heat (20 min at 100 °C) reduced DGTT particle sizes by 27-58%, but not in CMTT. Additionally, aging increased carboxylic functional groups and led to a brittle structure in both TWP types. Leachate composition varied with comminution method and aging. Benzothiazole, N-Cyclo-N-phenylurea, and aniline were more abundant in pristine and aged CMTT and aged DGTT. Diphenylguanidine had the highest concentration in all leachates. Aged TWP leachates, regardless of comminution, had significant toxic effects on C. elegans. Leachate from pristine CMTT was more toxic than from pristine DGTT. Nematode offspring correlated negatively with ozone exposure duration in aged DGTT. Tests with aged CMTT leachate showed even short-term exposure reduced offspring numbers. Discussion The results underscore the importance of oxidative and mechanical weathering in TWP toxicity and challenge the use of pristine particles in toxicological assays for risk assessment in the natural environment. KW - Microplastics KW - Tire abrasion KW - Environment PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-654672 DO - https://doi.org/10.1071/EN25051 SN - 1448-2517 VL - 23 IS - 2 SP - 1 EP - 16 PB - CSIRO Publishing AN - OPUS4-65467 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Altmann, Korinna A1 - Braun, U. T1 - Monitoring von Mikroplastik N2 - Der Vortrag gibt einen Überblick was bei der Analyse von Mikroplastik zu beachten ist und beschreibt die Vor- und Nachteile der TED-GC/MS. T2 - Abschlusstreffen MikroPlaTas CY - Online meeting DA - 23.06.2021 KW - Mikroplastik KW - TED-GC/MS KW - Mikroplastik-Analytik PY - 2021 AN - OPUS4-52916 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tannenberg, Robert A1 - Paul, Martin A1 - Röder, Bettina A1 - Gande, S. L. A1 - Sreeramulu, S. A1 - Saxena, K. A1 - Richter, C. A1 - Schwalbe, H. A1 - Swart, C. A1 - Weller, Michael G. T1 - Chemiluminescence biosensor for the determination of cardiac troponin I (cTnI) N2 - Cardiac troponin I (cTnI) is a crucial biomarker for diagnosing cardiac vascular diseases, including acute myocardial infarction (AMI). This study presents a proof-of-concept chemiluminescence-based immunosensor for rapid and accurate measurement of cTnI, with the potential for online monitoring. The immunosensor incorporates a flow cell design and a sensitive complementary metal-oxide-semiconductor (CMOS) camera for optical readout. A microfluidic setup was established to enable selective and quasi-online determination of cTnI within ten minutes. The sensor was tested with recombinant cTnI in phosphate buffer, demonstrating measurements in the concentration range of 2–25 µg/L, with a limit of detection (LoD) of 0.6 µg/L (23 pmol/L) achieved using the optimized system. The immunosensor exhibited high selectivity, as no cross-reactivity was observed with other recombinant proteins such as cTnT and cTnC at a concentration of 16 µg/L. Measurements with diluted blood plasma and serum yielded an LoD of 60 µg/L (2.4 nmol/L) and 70 µg/L (2.9 nmol/L), respectively. This biosensor offers a promising approach for the rapid and sensitive detection of cTnI, contributing to the diagnosis and management of acute myocardial infarction and other cardiac vascular diseases. N2 - Das kardiale Troponin I (cTnI) ist ein wichtiger Biomarker für die Diagnose von Herz-Kreislauf-Erkrankungen, einschließlich des akuten Myokardinfarkts (AMI). In dieser Studie wird ein auf Chemilumineszenz basierender Immunsensor für die schnelle und genaue Messung von cTnI vorgestellt, der das Potenzial für eine Online-Überwachung hat. Der Immunsensor besteht aus einer Durchflusszelle und einer empfindlichen CMOS-Kamera (Complementary Metal-Oxide-Semiconductor) zur optischen Detektion. Es wurde ein mikrofluidischer Aufbau entwickelt, der eine selektive und quasi Online-Bestimmung von cTnI innerhalb von zehn Minuten ermöglicht. Der Sensor wurde mit rekombinantem cTnI in Phosphatpuffer getestet und zeigte einen Messbereich von 2-25 µg/L, wobei mit dem optimierten System eine Nachweisgrenze (LoD) von 0,6 µg/L (23 pmol/L) erreicht wurde. Der Immunsensor zeigte eine hohe Selektivität, da keine Kreuzreaktivität mit anderen rekombinanten Proteinen wie cTnT und cTnC bei einer Konzentration von 16 µg/L beobachtet wurde. Messungen mit verdünntem Blutplasma und Serum ergaben einen LoD von 60 µg/L (2,4 nmol/L) bzw. 70 µg/L (2,9 nmol/L). Dieser Biosensor bietet einen vielversprechenden Ansatz für den schnellen und empfindlichen Nachweis von cTnI, der zur Diagnose und Behandlung des akuten Myokardinfarkts und anderer kardialer Gefäßerkrankungen beitragen kann. KW - Acute myocardial infarction KW - Heart attack KW - Emergency KW - Diagnosis KW - Cardiac troponin KW - Biomarker KW - Immunosensor KW - Biosensor KW - Chemiluminescence KW - Luminol KW - Peroxidase KW - Monoclonal antibodies KW - Flow injection immunoassay KW - Immunometric assay KW - Immunometric biosensor KW - Microfluidic system KW - Monolithic column KW - Online biosensor PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-575471 DO - https://doi.org/10.3390/bios13040455 SN - 2079-6374 VL - 13 IS - 4 SP - 1 EP - 20 PB - MDPI CY - Basel AN - OPUS4-57547 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Altmann, Korinna A1 - Portela, Raquel A1 - Barbero, Francesco A1 - Breuninger, Esther A1 - Camassa, Laura Maria Azzurra A1 - Velickovic, Tanja Cirkovic A1 - Charitidis, Costas A1 - Costa, Anna A1 - Fadda, Marta A1 - Fengler, Petra A1 - Fenoglio, Ivana A1 - Giovannozzi, Andrea M. A1 - Haugen, Øyvind Pernell A1 - Kainourgios, Panagiotis A1 - von der Kammer, Frank A1 - Kirchner, Markus J. A1 - Lomax-Vogt, Madeleine A1 - Lujic, Tamara A1 - Milczewski, Frank A1 - Moussawi, Mhamad Aly A1 - Ortelli, Simona A1 - Parac-Vogt, Tatjana N. A1 - Potthoff, Annegret A1 - Reinosa, Julian J. A1 - Röschter, Sophie A1 - Sacco, Alessio A1 - Wimmer, Lukas A1 - Zanoni, Ilaria A1 - Dailey, Lea Ann T1 - Characterizing nanoplastic suspensions of increasing complexity: Inter-laboratory comparison of size measurements using dynamic light scattering N2 - Understanding the potential human health risks associated with micro- and nanoplastic exposure is currently a priority research area. Nanoplastic toxicity studies are complicated by the lack of available, well-characterized test and reference materials. Further, many nanoplastic test materials are inherently more polydisperse and heterogenous in shape compared to polystyrene beads, making accurate and representative size distribution measurements particularly challenging. The aim of this study was to conduct an inter-laboratory comparison of dynamic light scattering measurements, the most commonly used particle sizing method for nanomaterials. Using a published standard operating procedure, size measurements in water and a standardized cell culture medium (CCM) were generated for spherical, carboxy-functionalized polystyrene nanoparticles (PS-COOH; 50 nm; benchmark material), and for increasingly complex in-house produced spherical poly(ethylene terephthalate) (nanoPET) and irregular shaped polypropylene (nanoPP) test materials. The weighted mean of hydrodynamic diameters of PS-COOH dispersed in water (55 ± 5 nm) showed moderate variation between labs (coefficient of variation, CV = 8.2%) and were similar to literature reports. Measurements of nanoPET (82 ± 6 nm) and nanoPP (182 ± 12 nm) in water exhibited similar CV values (nanoPET: 7.3% and nanoPP; 6.8%). Dispersion of PS-COOH and nanoPET in CCM increased the CV to 15.1 and 14.2%, respectively, which is lower than literature reports (CV = 30%). We conclude with a series of practical recommendations for robust size measurements of nanoplastics in both water and complex media highlighting that strict adherence to a standard operating procedure is required to prevent particle agglomeration in CCM KW - Nanoplastics KW - Reference materials KW - Polypropylene PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-644571 DO - https://doi.org/10.1039/d5en00645g SN - 2051-8153 SP - 1 EP - 15 PB - Royal Society of Chemistry (RSC) CY - Cambridge AN - OPUS4-64457 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Alasonati, E A1 - Bartczak, D A1 - Altmann, Korinna A1 - Giovannozzi, A T1 - Towards Standardised Micro and Nanoplastics Analysis via Interlaboratory Comparisons: First Outlook of the VAMAS TWA 45 P3 Project N2 - This talk is part of the stakeholder workshop of the PlasticTrace project held in September 2025 in Oslo. The presentation shows first results of the VAMAS ILC on nanoplastics. PP nanoparticles were given to the participants. These were asked to measure the mass or particle number or size of the PP nanoplastics. Various techniques such as DLS, FFF, Py-GC/MS, TED-GC/MS, PTA were used. T2 - Stakeholder Workshop PlasticsTrace CY - Online meeting DA - 09.09.2025 KW - Nanoplastics KW - ILC KW - DLS KW - Polypropylene PY - 2025 AN - OPUS4-64714 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Altmann, Korinna T1 - Wessen Problem ist Mikroplastik eigentlich? N2 - In den letzten 20 Jahren ist die Aufmerksamkeit vieler Forschender sowie der Politik und der Bürger selbst auf ein wachsendes Kunststoffproblem unserer Zeit stark gestiegen. Mangelnde Wertstoffkonzepte, Sammelstellen und unbedachtes Einbringen von Kunststoffprodukten in die Umwelt führen dort zu einer Anreicherung. Durch äußere Witterungseinflüsse können diese Produkte degradieren und fraktionieren, so dass heute in allen Teilen der Welt Mikroplastik (1-1000 µm, ISO/TR 21960:2020) unterschiedlicher Polymermaterialien nachgewiesen werden kann. Bei Mikroplastik gilt das Vorsorgeprinzip. Die Partikel können weiter zerfallen in Nanoplastik (< 1 µm, ISO/TR 21960:2020). Ob eine toxikologische Gefährdung von Mikro- oder Nanoplastik ausgeht, wird vielfältig untersucht. Bisher stehen valide Ergebnisse aus. Untersuchungen zur Häufigkeit, dem Transport und möglicher Senken und Eintragspfade muss aber Rechenschafft getragen werden, so dass ein Monitoring von Mikroplastik bereits in der Revision der Trinkwasserrahmen-Richtlinie und der Abwasserrahmen-Richtlinie gefordert wird. Bedenklich ist auch die Verordnung über Mindestanforderungen an die Wasserwiederverwendung (2020/741), in welcher nicht verbindlich gesagt wird, Wasser welcher Reinigungsstufe eines Klärwerks auf die Felder zur Wiederverwendung aufgebracht werden darf. Einer Regulierung über die EU-Plastikstrategie hinaus mit z.B. Verboten für Einwegplastik-Produkte und Rezyklingquoten kann nur entgegengewirkt werden, wenn valide Messmethoden, Referenzmaterialien und Standards existieren, die das tatsächliche Ausmaß von Mikroplastik-Konzentrationen in Luft, Wasser, Boden und Biota zuverlässig und genau aufzeigen. T2 - Technomer CY - Chemnitz, Germany DA - 06.11.2025 KW - Mikroplastik KW - Referenzmaterial KW - TED-GC/MS PY - 2025 AN - OPUS4-64618 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Putzu, Mara A1 - Wiesner, Yosri A1 - Weimann, Christiane A1 - Hodoroaba, Vasile-Dan A1 - Muniategui Lorenzo, Soledad A1 - Fernández-Gonzáles, Verónica A1 - Booth, Andy M. A1 - Igartua, Amaia A1 - Benismail, Nizar A1 - Coïc, Laureen A1 - Chivas-Joly, Carine A1 - Fenoglio, Ivana A1 - Rossi, Andrea Mario A1 - Giovannozzi, Andrea Mario A1 - Altmann, Korinna T1 - Optimization of tablet processing as a reference material for microplastic detection methods N2 - Reference materials (RMs) are essential and highly demanded tools for the development and validation of methods for microplastic (MP) quantification in complex matrices, to ensure comparable and harmonized approaches aligned with EU commission criteria for monitoring MPs (e.g., Drinking Water Directive and Urban Wastewater Treatment Directive). This study investigates different approaches for optimizing the production of polypropylene (PP) RMs in the form of water-soluble tablets, which were carefully evaluated for their homogeneity and stability according to ISO Guide 30, ISO 33401, and ISO 33405. PP particles (1–100 μm) were produced by cryomilling and embedded in a lactose/PEG matrix, then pressed into tablets (18 µg theoretical PP mass). The production process was optimized by varying (i) the size distribution of the matrix components and (ii) the mixer instrument. The materials obtained were characterized by thermogravimetric analysis to assess the homogeneity distribution of MPs with respect to PP mass in the individual tablets and their stability over a 4-month period. The most promising approach, with a homogenous mass of 19 μg (standard deviation of 4 μg), relative standard deviation of 19%, was further investigated for homogeneity by comparison with thermo-analytical mass determination methods, such as TED-GC/MS (thermal extraction desorption-gas chromatography/mass spectrometry) and Py-GC/MS (pyrolysis-gas chromatography-mass spectrometry), and for number-based characterization using micro-Raman spectroscopy. Material characterization was also examined using laser diffraction, scanning electron microscopy, and ATR-FTIR. Based on the results, the optimized processing protocol yields a PP RM suitable for quality control and method performance studies supporting standardization. KW - Microplastics KW - TED-GC/MS KW - Reference materials KW - Polypropylene PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-653290 DO - https://doi.org/10.1007/s00216-025-06271-7 SN - 1618-2642 SP - 1 EP - 14 PB - Springer Science and Business Media LLC AN - OPUS4-65329 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Putzu, Mara A1 - Barbaresi, Marta A1 - Fadda, Marta A1 - Sacco, Alessio A1 - Piergiovanni, Maurizio A1 - Masino, Matteo A1 - Bianchi, Federica A1 - Altmann, Korinna A1 - Benismail, Nizar A1 - Coïc, Laureen A1 - Fenoglio, Ivana A1 - Mattarozzi, Monica A1 - Rossi, Andrea Mario A1 - Careri, Maria A1 - Giovannozzi, Andrea Mario T1 - Accuracy assessment of a micro-Raman spectroscopy method for small microplastic particles in infant milk formula N2 - The presence of microplastics (MPs) in the food chain is increasingly documented, raising concerns over potential risks to human health. Despite growing efforts, standardized methods for MPs detection in food matrices remain limited. This study presents an interlaboratory comparison (ILC) aimed at assessing the accuracy and comparability of an analytical approach for the identification and quantification of small MPs (5–100 μm) in infant milk powder using μ-Raman spectroscopy and a representative polyethylene terephthalate (PET) reference material (RM). The RM, formulated as water-soluble tablets, was designed to replicate the morphology, size distribution, and polymer composition of environmentally relevant MPs, and was previously assessed for homogeneity and stability for mass fraction and particle numbers. The approach was assessed using two PET RM batches with different MPs particle numbers (high load batch: 1759 ± 141 MPs; low load batch: 160 ± 22 MPs), subjected to an enzymatic–chemical digestion, followed by μ-Raman analysis performed independently in two laboratories with different instruments and operators. Results are reported as absolute particle counts per analyzed sample and demonstrated excellent recovery across all size classes, including the smallest particles (down to 5 μm), with recovery rates ranging from 82 % to 88 %, in good agreement with the RM reference values. The analytical approach proved to be robust, reproducible, and suitable for low-level MPs quantification in complex food matrices, supporting ongoing efforts toward method harmonization and standardization for reliable MPs monitoring in the food sector. KW - Microplastics KW - Milk KW - Raman microspectroscopy PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-646239 DO - https://doi.org/10.1016/j.talo.2025.100586 SN - 2666-8319 VL - 12 SP - 1 EP - 8 PB - Elsevier B.V. AN - OPUS4-64623 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wiesner, Yosri A1 - Eisentraut, Paul A1 - Altmann, Korinna T1 - One Year Observation of Microplastic Concentrations in the River Rhine N2 - In recent years, the quantification of microplastics (MP) in aquatic environments has gained increasing attention, particularly regarding their environmental distribution and potential exposure levels. Environmentally relevant exposure data are still essential for a realistic risk assessment of the harmful health potential of microplastics in freshwater systems. This study addresses a large data set of MP concentrations analyzed and processed under statistical aspects and provides mass concentrations as well as associated size fractions of the detected MP. Over a 12 month period, samples were collected at three locations and analyzed across three particle size fractions (100−500 μm, 50−100 μm, and 10−50 μm) using thermalextraction desorption-gas chromatography/mass spectrometry (TED-GC/MS). The most prevalent polymers identified were polyethylene (PE), polypropylene (PP), polystyrene (PS), styrene−butadiene rubber (SBR), and natural rubber (NR). Statistical analyses, including principal component and cluster analysis, revealed size-dependent patterns,minor seasonal variation and spatial variations. These findings are particularly significant for ecotoxicological research and regulatory development, especially regarding tire abrasion a rarely quantified but potentially harmful MP source. The study contributes aluable data for future environmental monitoring and supports EU directives on wastewater and drinking water quality KW - TED-GC/MS KW - Microplastics KW - Environment KW - Monitoring KW - Reference data PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-654669 DO - https://doi.org/10.1021/acsestwater.5c00530 SN - 2690-0637 SP - 1 EP - 10 PB - American Chemical Society (ACS) AN - OPUS4-65466 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Altmann, Korinna T1 - Textile Fibers as Reference Materials for Microplastic Release N2 - Fibers of textile origin are named as high contributor for microplastic pollution in the environment next to e.g. plastics from packaging, tire wear and paints. Small fibers and fragments (microplastics: 1-1000 µm) can be released from textiles by mechanical abrasion during application (e.g. wearing) or washing. To date, the occurrence, transport pathways, and impacts of such small fibers on the environment and human health remain unclear. The European Commission revised the Urban Wastewater Treatment Directive (Directive (EU) 2024/3019) and made monitoring of microplastics mandatory in the next years. Additionally, standards for microplastic detection are developed in the ISO standardization body ISO/TC 147/SC 2 with the documents ISO/DIS 16094-2 and ISO/DIS 16094-3. Detection mainly occurs by thermoanalytical methods for mass or vibrational methods with microscopes for numbers. Such standards and regulatory efforts need validated methods, which themselves need reference materials for validation. Reference materials are well characterized materials that are produced for a specific purpose and are homogeneous and stable within one property of interest. The shape and the composition of the reference particles/fibers will affect the detection, hence it is important to validate the instruments with fibers, if this is the task for monitoring campaigns. This work describes the production of realistic fibers as reference material for microplastic analysis. The individual samples contain of a small number (< 1000) and mass (< 20 µm) of fibres. Homogeneity and stability control occurred by thermogravimetric analysis and µ-Raman. Further characteristics were determined for type, shape and size distribution. T2 - TEXTEH CY - Bucharest, Romania DA - 23.10.2025 KW - Microplastics KW - Reference materials KW - Microfibers KW - Microfiber release PY - 2025 AN - OPUS4-64620 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Kittner, Maria A1 - Altmann, Korinna A1 - Hamann, Sven A1 - Weyer, Rüdiger A1 - Kalbe, Ute T1 - Bewertung der Freisetzung von Mikroplastik aus Sportböden auf Kunststoffbasis - Abschlussbericht N2 - Die Europäische Kommission hat 2023 ein Verbot zum bewussten Austrag von Mikroplastik (MP) in die Umwelt beschlossen, das auch für die Verwendung von synthetischen Gummi-Granulaten (v. a. EPDM) in Sportböden gilt. In Deutschland gibt es laut DFB ca. 5100 Kunstrasenplätze. In der EU beläuft sich die Anzahl laut ECHA auf 13,000 Kunstrasen- und 47,000 Bolzplätze, Tendenz steigend. Das Hauptziel des Projektes war es daher, eine Massenbilanz für die Freisetzung von MP zu erstellen, um so eine Schätzung des MP-Austrags pro Kunstrasenplatz und Jahr zu ermöglichen. Dafür werden die MP-Emissionen von drei Kunstrasenszenarien in verschiedenen Zuständen (ungealtert, künstlich gealtert und in Echtzeit gealtert) verglichen: die Vergangenheit (Kunstrasen: fossilbasiert, EPDM-Füllung), die Gegenwart (der in Europa am häufigsten installierte Rasen) und die Zukunft (Rasen mit recycelten Grasfasern, keine synthetische Füllung sondern z.B. Quarzsand oder Korkschrott). Dazu werden fabrikneue Kunststoffrasen und EPDM-Granulat unter Laborbedingungen beschleunigt gealtert, um die Freiland-Beanspruchung eines Kunststoffrasens in circa 15 Jahren abzubilden. Die Verwendung spezieller Mikrofiltertiegel in Lysimeter-Experimenten ermöglicht die Abschätzung der Partikelgrößen des emittierten MP, was eine Grundbedingung für die Bewertung einer potenziellen Gesundheitsgefährdung für Menschen ist. Ergänzend wurden weitere umweltrelevante Schadstoffausträge aus den Kunststoffrasen quantifiziert. KW - Mikroplastik KW - Kunststoffrasen KW - Schadstoffe KW - Bewitterung KW - Lysimeter PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-633114 DO - https://doi.org/10.26272/opus4-63311 N1 - Das Projekt wurde gefördert vom Bundesinstitut für Bau-, Stadt- und Raumforschung (BBSR) im Auftrag des Bundesministeriums für Wohnen, Stadtentwicklung und Bauwesen (BMWSB) aus Mitteln des Innovationsprogramms Zukunft Bau. Aktenzeichen: FKZ 10.08.18.7-22.02. Projektlaufzeit: 09.2022 bis 03.2025. SP - 1 EP - 75 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-63311 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Visileanu, Emilia A1 - Catalin Grosu, Marian A1 - Tiberiu Miclea, Paul A1 - Altmann, Korinna A1 - Brossell, Dirk T1 - Methods for the collection and characterization of airborne particles in the textile industry N2 - Airborne particulate matter is one of the main air pollutants. Their impact on mortality, and the occurrence of pulmonary and cardiovascular complications, have been the subject of numerous studies. Airborne particles are complex mixtures of organic and inorganic substances from different sources of particle emissions. Particulate Matter (PM) particles are classified according to their aerodynamic diameter expressed in µm and can vary from coarse (PM 10) to fine (less than PM 2.5). These diameter considerations are fundamental because they condition the penetration of particles into the bronchopulmonary system and the body. In recent years, there has been an interest in so-called “ultra-fine” particles, with a diameter of 0.1 µm (or 100 nm), or PM 0.1. They are nanoparticles and their impact on human health is not yet clear.With more than 1.5 million employees, textiles and clothing is a diverse sector that plays an important role in the European manufacturing industry, producing a turnover of €162 billion.An important component of the solid particles that generate air pollution in the textile industry is microplastics (MP) and nano plastics (NP), which also include microfibers (<5mm) and nanofibers (<100 nm), respectively. The particles released into the air during fiber and yarn processing range from 1 µg/m3 to 50 µg/m3.The paper presents the results of the determination of indoor and outdoor air concentration levels in textile companies, to identify the areas with the highest concentration level, by using an online recording system such as the Laser Aerosol Spectrometer MINI LAS model 11-E. The total concentration level TSP (µg/m3), the fractions PM 10(µg/m3), PM 2.5(µg/m3), PM1(µg/m3), as well as the total number of particles TC (1/l), were shown. It was noted that TSP is approximately at the same level both indoors and outdoors, but the fractions of PM10, PM2.5, and PM1 have much higher values indoors than outdoors with possible consequences on workers' health.The next step was the collection of fibers, namely micro and nano plastic particles from the vicinity of the workplaces of polyester, polyamide, and polypropylene fibers processing units in the textile industry in Romania, to obtain a sufficient quantity for laboratory analysis to determine the size and shape of the particles as well as their chemical composition. Two types of pumps were used, differentiated by their operating parameters: TECORA SKYPOST with airflow of 38 l/min and GILAIRPLUS with airflow 2l/min. Filters made of different materials with different diameters and pore sizes were used, namely: quartz filters (ø 47 mm, and ø 37 mm) on a TECORA SKYPOST type pump, polycarbonate nucleopore coated with a gold membrane (ø 25 mm) and silica filter (ø 9 mm) on GILAIRPLUS type pump.Using descriptive statistics, the calculation of correlation coefficients highlighted a strong correlation between the variables: "Collected mass/ Air concentration" and "Collected mass/ Air volume" for all diameters of the filters.The highest collected particle volume, determined by weighing the filters before and after collection, was obtained with the quartz filters (ø 47 mm) at an airflow of 38 l/min. The particles collected (polyester, polyamide, polypropylene) in the first stage were analyzed by SEM and thermogravimetric and it was found that the quartz filters absorbed the particles inside, with very few remaining on the surface. Thus no known methods can be used to perform analysis for particles collected on quartz filters. The number of particles on the filters was insufficient for analysis either because of the collection parameters used or because of the loss of particles during transport. As a result, in the next step, the use of 9 mm Si filters using the GILAIRPLUS pump at an airflow rate of 2l/min was chosen.To improve the transport conditions and avoid the loss of the particles and keep them on the surface of the filters, two methods were applied:- after weighing the filters were reintroduced into the collection pump holder;- a filtration system for airborne micro-nano plastics was designed and manufactured to selectively collect and transport PM10 and PM1 particles collected on SI filters.In both cases, SEM, Raman mapping, and GS-MS microscopy were used for analysis.Several times more PM10 than PM1 (74.5µg compared to 12.5 µg) was found. In all cases, both particles and fibers showed the same Raman fingerprint.The GS-MS analyses showed some contamination of the workspaces with particles other than the processed fibers. The presence of non-notifiable substances was also observed.The most viable filters are Si filters with a pore size of 10 microns to 1 micron and the use of the selected collection and transport filter system. In the following a filter system will be applied for collection on Au membrane-coated polycarbonate filters. T2 - 5th International Conference on Human Systems Engineering and Design: Future Trends and Applications (IHSED 2023) KW - Microplastics KW - Textiles PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-624442 DO - https://doi.org/10.54941/ahfe1004132 VL - 112 SP - 212 EP - 223 PB - AHFE International AN - OPUS4-62444 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dittmar, Stefan A1 - Weyrauch, Steffen A1 - Reemtsma, Thorsten A1 - Eisentraut, Paul A1 - Altmann, Korinna A1 - Ruhl, Aki S. A1 - Jekel, Martin T1 - Settling Velocities of Tire and Road Wear Particles: Analyzing Finely Graded Density Fractions of Samples from a Road Simulator and a Highway Tunnel N2 - The terminal settling velocity is considered the most critical parameter determining the transport of tire and road wear particles (TRWP) in aquatic environments. Nonetheless, no respective empirical data has been reported so far. In this study, particle samples from a road simulator and a highway tunnel were investigated with a validated imaging method. Different density and size fractions of both samples were measured separately, acquiring sizes and settling velocities of more than 30,000 individual particles. In addition, tire marker polymers were analyzed for each fraction via thermal extraction desorption-gas chromatography/mass spectrometry. Finally, the acquired particle data was combined according to the fractions’ estimated tire contents in order to deduce detailed probability distributions of particle size and settling velocity for the actual TRWP from both samples. Weighted by TRWP-incorporated tire mass, median diameters of 54 and 44 μm as well as median settling velocities of 0.65 and 0.22 mm/s were found for TRWP from the road simulator and highway tunnel, respectively. This study thus provides the first ever empirical data on TRWP settling velocities in water, which can be highly valuable input for modeling the environmental transport of TRWP and for dimensioning TRWP retention systems. KW - Microplastics KW - TED-GC/MS KW - Sinking velocities KW - Transport PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-635449 DO - https://doi.org/10.1021/acs.est.5c04165 SN - 0013-936X VL - 59 IS - 26 SP - 13434 EP - 13446 PB - American Chemical Society (ACS) AN - OPUS4-63544 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Visileanu, Emilia A1 - Altmann, Korinna A1 - Stepa, Raluca A1 - Haiducu, Maria A1 - Miclea, Paul Tiberiu A1 - Vladu, Alina A1 - Dondea, Felicia A1 - Grosu, Marian Catalin A1 - Scarlat, Razvan T1 - Comparative Analysis of Airborne Particle Concentrations in Textile Industry Environments Throughout the Workday N2 - This paper addresses the growing concern surrounding microplastic pollution, particularly within the textile industry, and the associated potential health risks linked to the inhalation and ingestion of microplastic particles. Microplastics, defined as plastic particles smaller than five millimeters, are increasingly found not only in aquatic environments, but also in soils, air, and food. Although research on the health impacts of microplastics is still emerging, early studies indicate that these particles could contribute to health issues, including oxidative stress, inflammation, and cardiovascular diseases. Notably, individuals with higher concentrations of plastics in arterial plaques are more susceptible to heart attacks and strokes. In the textile industry, synthetic fibers such as polyester, nylon, and acrylic release microplastics into the air during production. The paper discusses a study conducted in a textile company that processes polyester yarns, where airborne microplastic concentrations were measured at various locations throughout the day. Particle sizes ranging from 0.3 nm to 10 nm were analyzed, revealing the presence of polyester polymers in the particulate matter. These findings underscore the widespread nature of microplastic pollution, particularly in industrial settings, and raise concerns about the health risks associated with prolonged exposure to airborne microplastics. While further research is necessary to fully understand the extent of these health impacts, preliminary data suggest a troubling link between microplastic inhalation and cardiovascular conditions. KW - Microplastics KW - Textiles KW - Airborne particles PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-635269 DO - https://doi.org/10.3390/microplastics4020034 SN - 2673-8929 VL - 4 IS - 2 SP - 1 EP - 17 PB - MDPI AG AN - OPUS4-63526 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fink, Friedrich A1 - Stawski, Tomasz M. A1 - Emmerling, Franziska A1 - Falkenhagen, Jana T1 - A novel machine-learning approach to unlock technical lignin classification by NIR spectroscopy - bench to handheld N2 - In this research, the utilization of near-infrared (NIR) spectroscopy in conjunction with advanced machine learning methods is investigated for categorizing technical lignins obtained from different biomass sources and industrial procedures. Technical lignins, such as kraft, organosolv and lignosulfonates, have different chemical compositions, which continue to make uniform characterization and application in sustainable sectors extremely difficult. Fast, universally accessible analytics combined with data analysis is still an open question. For the first time three distinct NIR spectrometers—a high-performance benchtop system, a mid-priced compact device, and an economical handheld unit—were utilized to record NIR spectra of 31 unique lignin samples. The spectra underwent pre-processing through standard normal variate (SNV) transformation and Savitzky-Golay derivatives to amplify spectral features and decrease noise. Principal component analysis (PCA) was employed to reduce data complexity and extract crucial characteristics for classification purposes. Subsequently, four machine learning algorithms—Support Vector Machines (SVM), Gaussian Naive Bayes (GNB), Gaussian Process Classification (GPC), and Decision Tree Classification (DTC)—were implemented for the classification of the lignin samples. The DTC model exhibited the highest accuracy among them across different spectrometers. Although the benchtop spectrometer produced the most precise outcomes, the compact NeoSpectra system also displayed potential as a cost-efficient option. Nonetheless, the restricted spectral coverage of the handheld NIRONE spectrometer resulted in reduced classification accuracy. Our discoveries highlight the capability of NIR spectroscopy, combined with robust data analysis techniques, for the swift and non-destructive classification of technical lignins, facilitating their improved utilization in sustainable fields. KW - Technical lignins KW - NIR spectroscopy KW - Classification KW - Machine-learning KW - PCA PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-634518 DO - https://doi.org/10.1016/j.chemolab.2025.105467 SN - 0169-7439 VL - 264 SP - 1 EP - 10 PB - Elsevier B.V. CY - Amsterdam AN - OPUS4-63451 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wiesner, Yosri A1 - Bednarz, Marius A1 - Braun, Ulrike A1 - Bannick, Claus Gerhard A1 - Ricking, Mathias A1 - Altmann, Korinna T1 - A promising approach to monitor microplastic masses in composts N2 - Inputs of plastic impurities into the environment via the application of fertilizers are regulated in Germany and the EU by means of ordinances. Robust and fast analytical methods are the basis of legal regulations. Currently, only macro- and large microplastic contents (>1 mm) are measured. Microplastics (1–1,000 µm), are not yet monitored. Thermal analytical methods are suitable for this purpose, which can determine the mass content and can also be operated fully automatically in routine mode. Thermal extraction desorption-gas chromatography/mass spectrometry (TED-GC/MS) allows the identification of polymers and the determination of mass contents in solid samples from natural environments. In accordance with the German or European Commission (EC) Fertiliser Ordinance, composting plants should be monitored for microplastic particles with this method in the future. In this context a compost plant was sampled. At the end of the rotting process, the compost was sieved and separated in a coarse (>1 mm) and a fine fraction (<1 mm). The fine fraction was processed using density separation comparing NaCl and NaI as possible salt alternative and screened for microplastic masses by TED-GC/MS with additional validation and quality assurance experiments. With TED-GC/MS total microplastics mass contents of 1.1–3.0 μg/mg in finished compost could be detected with polyethylene mainly. What differs much to the total mass of plastics in the coarse fraction with up to 60 μg/mg, which were visually searched, identified via ATR-FTIR and gravimetrically weighted. KW - Microplastics KW - TED-GC/MS KW - Compost KW - Monitoring KW - Soil PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-586688 DO - https://doi.org/10.3389/fenvc.2023.1281558 SN - 2673-4486 VL - 4 SP - 1 EP - 12 PB - Frontiers Media CY - Lausanne AN - OPUS4-58668 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, Axel A1 - Altmann, Korinna A1 - Kocher, B. A1 - Braun, U. T1 - Determination of tire wear markers in soil samples and their distribution in a roadside soil N2 - Tire wear (TW) constitutes a significant source of microplastic in terrestrial ecosystems. It is known that particles emitted by roads can have an effect up to 100 m into adjacent areas. Here, we apply for the first-time thermal extraction desorption gas chromatography-mass spectrometry (TED-GC/MS) to determine TW in soil samples by detection of thermal decomposition products of styrene-butadiene rubber (SBR), without additional enrichment. Additionally, zinc contents were determined as an elemental marker for TW. Mixed soil samples were taken along three transects along a German motorway in 0.3, 2.0, and 5.0 m distance from the road. Sampling depths were 0–2, 2–5, 5–10, and 10–20 cm. Four fine fractions, 1 000–500, 500–100, 100–50, and <50 μm, were analyzed. TW contents based on SBR ranged from 155 to 15 898 mg kg−1. TW contents based on zinc were between 413 and 44 812 mg kg−1. Comparison of individual values of SBR and zinc reveals SBR as a more specific marker. Results confirm that most TW ends up in the topsoil within a 2 m distance. The sampling strategy resulted in representative data for a larger area. Standard deviations of quadruple TED-GC/MS determination of SBR were <10% for all grain size fractions. TED-GC/MS is a suitable analytical tool for determining TW in soil samples without the use of toxic chemicals, enrichment, or special sample preparation. KW - Microplastic KW - TED-GC/MS KW - Tire wear PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-543344 DO - https://doi.org/10.1016/j.chemosphere.2022.133653 VL - 294 SP - 1 EP - 8 PB - Elsevier Ltd. AN - OPUS4-54334 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Senges, Gene A1 - de Oliveira Guilherme Buzanich, Ana A1 - Lindič, Tilen A1 - Gully, Tyler A. A1 - Winter, Marlon A1 - Radtke, Martin A1 - Röder, Bettina A1 - Steinhauer, Simon A1 - Paulus, Beate A1 - Emmerling, Franziska A1 - Riedel, Sebastian T1 - Unravelling highly oxidized nickel centers in the anodic black film formed during the Simons process by in situ X-ray absorption near edge structure spectroscopy N2 - The electrofluorination after Simons has been used for the last century to produce everyday life materials. An in situ XANES investigation of the controversially debated black film apparent in the Simons process revealed high-valent nickel centers. KW - Synchrotron KW - BAMline KW - XANES PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-608366 DO - https://doi.org/10.1039/d3sc06081k SN - 2041-6520 VL - 15 IS - 12 SP - 4504 EP - 4509 PB - Royal Society of Chemistry (RSC) AN - OPUS4-60836 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Monikh, Fazel A. A1 - Materić, Dušan A1 - Valsami-Jones, Eugenia A1 - Grossart, Hans-Peter A1 - Altmann, Korinna A1 - Holzinger, Rupert A1 - Lynch, Iseult A1 - Stubenrauch, Jessica A1 - Peijnenburg, Willie T1 - Challenges in studying microplastics in human brain N2 - Human exposure to microplastics and nanoplastics (MNPs) is an emerging concern with potential implications for health. As awareness of this issue grows, it has prompted increasing scientific attention toward understanding if, and how, MNPs accumulate in human tissues. In a recent study, Nihart et al.1 used the analytical technique of pyrolysis gas chromatography–mass spectrometry (Py-GC–MS) to detect MNPs in human liver, kidney and brain, reporting the highest concentrations in the brain, with polyethylene as the predominant polymer. The study as reported appears to face methodological challenges, such as limited contamination controls and lack of validation steps, which May affect the reliability of the reported concentrations. In this Matters Arising, we highlight methodological limitations that have General relevance for advancing robust and reproducible MNP detection in human biomonitoring studies. KW - Microplastics KW - Nanoplastics KW - Py-GC-MS PY - 2025 DO - https://doi.org/10.1038/s41591-025-04045-3 SN - 1078-8956 VL - 31 IS - 12 SP - 1 EP - 3 PB - Springer Science and Business Media LLC AN - OPUS4-64698 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Altmann, Korinna T1 - Seasonal microplastic concentrations along the rivers Rhine and Danube N2 - Over the last 20 years, many researchers, politicians and citizens have become increasingly aware of the growing plastic problem of our time. A lack of recycling concepts and plastic collection points as well as careless dumping lead to accumulation of plastic products in the environment. Natural weathering can cause these plastics to degrade and fractionate, meaning that microplastics (1 1,000 µm, ISO/TR 21960:2020) and nanoplastics (< 1 µm, ISO/TR 21960:2020) of various synthetic polymer materials can now be detected in all parts of the world. Whether microplastics or nanoplastics pose a toxicological hazard is being investigated in a variety of ways. Valid results are still pending. However, the EU precautionary principle applies to micro- and nanoplastics. Monitoring of microplastics is already required in the revision of the Drinking Water and Wastewater Framework Directive. Reliable monitoring of rivers can be carried out by sampling with sedimentation boxes and microplastic detection by using thermal extraction desorption gas chromatography/mass spectrometry (TED-GC/MS) in routine operation (Figure 1). The river Rhine was sampled for microplastic masses at three different sampling locations over a period of one year and in addition the Danube at randomized sampling locations The TED-GC/MS results showed that various synthetic polymers frequently produced in industry, such as polyethylene, polypropylene or polystyrene as well as the tire compound styrene-butadiene rubber were found. The work not only shows a possible workflow for monitoring concepts, but also provides information on environmentally relevant concentrations of microplastics and tire components in surface waters. This in turn is necessary for ecotoxicological studies. T2 - ESOPS CY - Berlin, Germany DA - 09.09.2024 KW - Microplastics KW - TED-GC/MS KW - Polymer 3R PY - 2024 AN - OPUS4-61016 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Béalu, Zoé A1 - Walther, Johanna A1 - Abusafia, Attaallah A1 - Altmann, Korinna A1 - Meurer, Maren A1 - Gretzschel, Oliver A1 - Schäfer, Michael A1 - Steinmetz, Heidrun T1 - Removal of Organic Micropollutants and Microplastics via Ozonation Followed by Granular Activated Carbon Filtration N2 - Discharge from Wastewater Treatment Plants (WWTPs) can result in the emission of organic micropollutants (OMPs) and microplastics (MPs) into the aquatic environment. To prevent this harmful release, a pilot plant consisting of an ozonation followed by a granular activated carbon (GAC) filter was operated at a WWTP in Germany, and its side-effects on the concentrations of nitrogen (N) and phosphorous (P) compounds were measured. Over 80% of OMPs and transformation products were removed during the operating time (around 6000 bed volumes) no matter the ozone dose (from around 0.1 to 0.5 mgO3/mgDOC), except for Diatrizoic acid, whose breakthrough appeared at 3500 BV. Formation of the oxidation by-product, NDMA, increased with higher ozone doses, but the concentration remained below 100 ng/L. Bromate was formed at a higher ozone dose (0.4 mgO3/mgDOC) but at a low concentration—below 10 µg/L. The MP particles detected in the inflow (PE, SBR, PP, and PS) were effectively eliminated to a high degree, with a removal rate of at least 92%. Carbon parameters (COD, DOC, and SAC254) were removed further by the pilot plant, but to different extents. As expected, nitrate was formed during ozonation, while nitrite’s concentration decreased. Further, nitrite decreased and nitrate increased within the GAC filter, while ammonium was eliminated by at least 90%. Total P concentration decreased after the pilot, but the concentration of PO4-P increased. KW - Microplastics KW - TED-GC/MS KW - Granular Activated Carbon Filtration KW - Removal of Organic Micropollutants KW - Wastewater treatment plant PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-615209 DO - https://doi.org/10.3390/environments11110241 VL - 11 IS - 11 SP - 1 EP - 38 PB - MDPI AG AN - OPUS4-61520 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fadda, Marta A1 - Sacco, Alessio A1 - Altmann, Korinna A1 - Ciornii, Dmitri A1 - Milczewski, Frank A1 - Bañares, Miguel A. A1 - Portela, Raquel A1 - Giovannozzi, Andrea Mario A1 - Rossi, Andrea Mario T1 - Tracking nanoplastics in drinking water: a new frontier with the combination of dielectrophoresis and Raman spectroscopy N2 - Detection of micro- (MPs) and nanoplastics (NPs) in food and environmental matrices has been gaining relevance due to their potential toxicological effects on human health. While MPs have been detected in a wide range of complex matrices, suitable methods for the characterization and chemical identification of NPs are still lacking, primarily due to significant methodological challenges associated with their nano-specific physiochemical properties, including size distribution (1 nm – 1 µm), dynamic surface chemical changes, and carbon-based composition, which complicate their detection compared to engineered nanomaterials. To overcome the traditional limitations of spectroscopic techniques in terms of spatial resolution and sensitivity at the sub-micrometer level, a novel label-free methodology is presented for specifically identifying the chemical composition of NPs directly in suspension by combining Raman spectroscopy with dielectrophoresis (DEP). Using a custom-built device, small volumes of NPs are injected into a dielectrophoretic cell and locally trapped by DEP forces to fill the Raman confocal volume, facilitating their detection and identification, and providing high signal-to-noise ratio Raman spectra for more reliable analysis. This approach was successfully applied to both Milli-Q water and a commercial brand of drinking water, enabling the rapid identification of various types of NPs with different sizes and polymer compositions at concentrations as low as 20 µg/mL. These included certified reference polystyrene beads ranging from 800 to 60 nm in diameter, as well as polydisperse NPs, more representative of real samples in terms of size distribution and polymer type, such as polyethylene (450 nm), polypropylene (180 nm), and polyethylene terephthalate (100 nm). Moreover, the chemical fingerprint of each NPs was thoroughly investigated and compared with the corresponding bulk polymers, highlighting possible changes in the Raman bands due to surface oxidation or nanometer-scale effect. Therefore, this innovative method can be considered a valuable approach for addressing gaps in the detection and identification of NPs, as well as for monitoring their dynamic phisiochemical changes in real matrices. KW - Nanoplastics KW - Water contaminants KW - Raman microspectroscopy KW - Dielectrophoresis PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-633658 DO - https://doi.org/10.1186/s43591-025-00131-y SN - 2662-4966 VL - 5 IS - 1 SP - 1 EP - 11 PB - Springer Science and Business Media LLC AN - OPUS4-63365 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Cakir, Cafer Tufan T1 - Algorithm-Assisted Multimodal Synchrotron Experiments: XRD–XES Integration and SpecTwin N2 - Multimodal synchrotron-based techniques are emerging as powerful tools for advanced materials characterization, enabling simultaneous insights into both crystal and electronic structure. We present a combined X-ray diffraction (XRD) and high-resolution X-ray emission spectroscopy (XES) approach implemented in a double-dispersive setup. This configuration enables simultaneous acquisition of structural and spectroscopic information with high precision, allowing us to resolve correlations between lattice arrangements and electronic configurations under in situ conditions. To enhance experimental throughput and reproducibility, we employ digital twin concepts and optimization algorithms for experiment design and parameter control. These methods effectively eliminate trial-and-error procedures when optimizing the setup to achieve the desired resolution for XES analysis. In addition, we introduce SpecTwin, a dedicated software environment that integrates XES data analysis, simulation, and optimization routines. This combined methodology underscores the potential of algorithm-assisted multimodal X-ray experiments to advance the quantitative understanding of structure–property relationships in complex materials. T2 - Joint BAM-HZB Symposium on Multimodal Synchrotron Experiments for Next-Generation Materials Research CY - Berlin, Germany DA - 25.02.2026 KW - XAS KW - Digital Twin KW - Optimization KW - Multimodal PY - 2026 AN - OPUS4-65608 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bartczak, Dorota A1 - Sikora, Aneta A1 - Goenaga-Infante, Heidi A1 - Altmann, Korinna A1 - Drexel, Roland A1 - Meier, Florian A1 - Alasonati, Enrica A1 - Lelong, Marc A1 - Cado, Florence A1 - Chivas-Joly, Carine A1 - Fadda, Marta A1 - Sacco, Alessio A1 - Rossi, Andrea Mario A1 - Pröfrock, Daniel A1 - Wippermann, Dominik A1 - Barbero, Francesco A1 - Fenoglio, Ivana A1 - Booth, Andy M. A1 - Sørensen, Lisbet A1 - Igartua, Amaia A1 - Wouters, Charlotte A1 - Mast, Jan A1 - Barbaresi, Marta A1 - Rossi, Francesca A1 - Piergiovanni, Maurizio A1 - Mattarozzi, Monica A1 - Careri, Maria A1 - Caebergs, Thierry A1 - Piette, Anne-Sophie A1 - Parot, Jeremie A1 - Giovannozzi, Andrea Mario T1 - Multiparameter characterisation of a nano-polypropylene representative test material with fractionation, light scattering, high-resolution microscopy, spectroscopy, and spectrometry methods N2 - Reference and quality control materials with comparable physicochemical properties to nanoplastic contaminants present in environmental and food nanoplastics are currently lacking. Here we report a nanoplastic polypropylene material prepared using a top-down approach involving mechanical fragmentation of larger plastics. The material was found to be homogeneous and stable in suspension and has been characterised for average particle size, size distribution range, particle number concentration, polypropylene mass fraction and inorganic impurity Content using a wide range of analytical methods, including AF4, cFFF, PTA, (MA)DLS, MALS, SEM, AFM, TEM, STEM, EDS,Raman, ICP-MS and pyGC-MS. The material was found to have a broad size distribution, ranging from 50 nm to over 200 nm, with the average particle size value dependent on the technique used to determine it. Particle number concentration ranged from 1.7–2.4 × 1010 g−1 , according to PTA. Spectroscopy techniques confirmed that the material was polypropylene, with evidence of aging due to an increased level of oxidation. The measured mass fraction was found to depend on the marker used and ranged between 3 and 5 μg g−1 . Inorganic impurities such as Si, Al, Mg, K, Na, S, Fe, Cl and Ca were also identified at ng g−1 levels. Comparability and complementarity across the measurement methods and techniques is also discussed. KW - Polypropylene KW - Nanoplastics KW - Analytics KW - Reference material KW - Scattering methods PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-654680 DO - https://doi.org/10.1039/D5EN00917K SN - 2051-8153 SP - 1 EP - 15 PB - Royal Society of Chemistry (RSC) AN - OPUS4-65468 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ponader, Marco A1 - Röder, Bettina A1 - Paul, Martin A1 - Weller, Michael G. T1 - Sintered glass monoliths as supports for affinity columns N2 - A novel stationary phase for affinity separations is presented. This material is based on sintered borosilicate glass readily available as semi-finished filter plates with defined porosity and surface area. The material shows fast binding kinetics and excellent long-term stability under real application conditions due to lacking macropores and high mechanical rigidity. The glass surface can be easily modified with standard organosilane chemistry to immobilize selective binders or other molecules used for biointeraction. In this paper, the manufacturing of the columns and their respective column holders by 3D printing is shown in detail. The model system protein A/IgG was chosen as an example to examine the properties of such monolithic columns under realistic application conditions. Several specifications, such as (dynamic) IgG capacity, pressure stability, long-term performance, productivity, non-specific binding, and peak shape, are presented. It could be shown that due to the very high separation speed, 250 mg antibody per hour and column can be collected, which surpasses the productivity of most standard columns of the same size. The total IgG capacity of the shown columns is around 4 mg (5.5 mg/mL), which is sufficient for most tasks in research laboratories. The cycle time of an IgG separation can be less than 1 min. Due to the glass material’s excellent pressure resistance, these columns are compatible with standard HPLC systems. This is usually not the case with standard affinity columns, limited to manual use or application in low-pressure systems. The use of a standard HPLC system also improves the ability for automation, which enables the purification of hundreds of cell supernatants in one day. The sharp peak shape of the elution leads to an enrichment effect, which might increase the concentration of IgG by a factor of 3. The final concentration of IgG can be around 7.5 mg/mL without the need for an additional nano-filtration step. The purity of the IgG was > 95% in one step and nearly 99% with a second polishing run. KW - Affinity Chromatography KW - Affinity Extraction KW - Affinity Separation KW - Protein Purification KW - Down Stream Processing KW - Antibody Purification KW - Diagnostic Antibodies KW - Therapeutic Antibodies KW - Automated Purification KW - HPLC KW - FPLC KW - IgG determination KW - Concentration step KW - Monoclonal Antibodies KW - Polyclonal Antibodies KW - Human Plasma KW - Glass Support KW - Borosilicate Glass KW - Monolith KW - Sintered Material KW - Additive Manufacturing KW - Column holder KW - Construction KW - Open Science KW - Citizen Science KW - Protein A KW - Regeneration KW - High-Speed Separations KW - Robustness PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-527581 DO - https://doi.org/10.3390/separations8050056 SN - 2297-8739 N1 - Geburtsname von Ponader, Marco: Wilke, M. - Birth name of Ponader, Marco: Wilke, M. VL - 8 IS - 5 SP - 1 EP - 16 PB - MDPI CY - Basel AN - OPUS4-52758 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Ponader, Marco A1 - Röder, Bettina A1 - Paul, Martin A1 - Weller, Michael G. T1 - Sintered glass monoliths as new supports for affinity columns N2 - A novel stationary phase for affinity separations is presented. This material is based on sintered borosilicate glass readily available as semi-finished filter plates with defined porosity and surface area. The material shows fast binding kinetics and excellent long-term stability under real application conditions due to lacking macropores and high mechanical rigidity. The glass surface can be easily modified with standard organosilane chemistry to immobilize selective binders or other molecules used for biointeraction. In this paper, the manufacturing of the columns and their respective column holders by 3D printing is shown in detail. The model system protein A/IgG was chosen as an example to examine the properties of such monolithic columns under realistic application conditions. Several specifications, such as (dynamic) IgG capacity, pressure stability, long-term performance, productivity, non-specific binding, and peak shape, are presented. It could be shown that due to the very high separation speed, 250 mg antibody per hour and column can be collected, which surpasses the productivity of most standard columns of the same size. The total IgG capacity of the shown columns is around 4 mg (5.5 mg/mL), which is sufficient for most tasks in research laboratories. The cycle time of an IgG separation can be less than 1 minute. Due to the glass material's excellent pressure resistance, these columns are compatible with standard HPLC systems. This is usually not the case with standard affinity columns, limited to manual use or application in low-pressure systems. The use of a standard HPLC system also improves the ability for automation, which enables the purification of hundreds of cell supernatants in one day. The sharp peak shape of the elution leads to an enrichment effect, which might increase the concentration of IgG by a factor of 3. The final concentration of IgG can be around 7.5 mg/mL without the need for an additional nanofiltration step. The purity of the IgG was > 95% in one step and nearly 99% with a second polishing run. KW - Affinity Chromatography KW - Glass KW - Purification KW - Antibodies KW - Solid support KW - HPLC KW - FPLC KW - Separation PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-529117 DO - https://doi.org/10.20944/preprints202103.0298.v1 SN - 2310-287X N1 - Geburtsname von Ponader, Marco: Wilke, M. - Birth name of Ponader, Marco: Wilke, M. SP - 1 EP - 17 PB - MDPI CY - Basel AN - OPUS4-52911 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Morcillo, Dalia A1 - Oelze, Marcus A1 - Seena Prem, Pranav A1 - de Oliveira Guilherme Buzanich, Ana A1 - Emmerling, Franziska A1 - Recknagel, Sebastian A1 - Panne, Ulrich A1 - Abad Andrade, Carlos Enrique T1 - Lithium isotope fractionation as an early indicator of degradation mechanisms in lithium-ion batteries N2 - Aging in lithium-ion batteries (LIBs) degrades performance and hinders sustainability, demanding advanced diagnostics for early failure prediction. We investigate lithium isotope fractionation (LIF) as an innovative probe of degradation in lithium cobalt oxide (LCO) coin cells aged over 0−700 cycles. High-precision multi-collector inductively coupled plasma mass spectrometry (MC-ICP-MS) quantified δ7Li variations across cell stages: non-cycled (0 cycles), newly formed (5 cycles), semi-aged (250 cycles), and fully aged (700 cycles). During early cycling (≤ 45 cycles), chemical processes drive 7Li enrichment at the anode (δ7Li vs LSVEC = +12 ‰) through solid electrolyte interphase (SEI) formation, while the cathode depletes in 7Li (δ7Li vs LSVEC = −0.7 ‰). Beyond 45 cycles, electric field-induced migration predominates, promoting 6Li intercalation into the anode and increasing the δ7Li of the cathode by 8.1 ‰. Mass balance verifies isotope conservation, attributing shifts to redistribution and trapping. Complementary electrochemical impedance spectroscopy (EIS) and X-ray absorption spectroscopy and diffraction confirm SEI expansion, cobalt oxidation, lattice shrinkage, and changes in electrode structure, corroborating LIF trends. Notably, a δ7Li inflection at approximately 270 cycles anticipates end-of-life by 70 cycles, surpassing traditional methods in sensitivity. LIF emerges as a predictive indicator of aging mechanisms, informing optimized designs for durable LIBs. KW - Lithium isotope fractionation KW - Lithium-ion batteries KW - Degradation mechanisms KW - LiCoO2 cathodes KW - LCO KW - Isotopic tracing KW - Lithium isotopes PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-650945 DO - https://doi.org/10.26434/chemrxiv-2025-16lvq SP - 1 EP - 19 AN - OPUS4-65094 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hoque, Maroof Arshadul A1 - Sommerfeld, Thomas A1 - Lisec, Jan A1 - Das, Prasenjit A1 - Prinz, Carsten A1 - Heinekamp, Christian A1 - Stolar, Tomislav A1 - Etter, Martin A1 - Rosenberger, David A1 - George, Janine A1 - Bhattacharya, Biswajit A1 - Emmerling, Franziska T1 - Mechanochemically Synthesized Covalent Organic Framework Effectively Captures PFAS Contaminants N2 - Per‐ and polyfluoroalkyl substances (PFAS) are persistent environmental contaminants that pose significant health risks, prompting urgent efforts to develop effective removal methods and adsorbers. Covalent organic frameworks (COFs) are metal‐free adsorbers with high stability and tunable porosity. A highly crystalline COF is synthesised mechanochemically using 1,3,5‐tris(4‐aminophenyl)benzene (TAPB) and 1,3,5‐triformylbenzene (TFB). The formation dynamics are monitored in real time with time‐resolved in situ synchrotron X‐ray diffraction. The TAPB‐TFB COF demonstrates good efficiency in eliminating PFAS from water. Perfluorooctanoic acid (PFOA) and perfluorooctanesulfonic acid (PFOS) are effectively extracted, and most of the adsorption occurred within the first 10 min. Additionally, X‐ray photoelectron spectroscopy, Fourier transform infrared spectroscopy, and DFT calculations are employed to elucidate the molecular interactions between PFAS and the COF framework. The rapid and efficient removal of PFAS makes TAPB‐TFB COF a promising material for water treatment applications. KW - COFs KW - Ball-milling KW - PFAS PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-648712 DO - https://doi.org/10.1002/smll.202509275 SN - 1613-6810 VL - 21 IS - 44 SP - 1 EP - 8 PB - Wiley CY - Weinheim AN - OPUS4-64871 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - de Oliveira Guilherme Buzanich, Ana A1 - Radtke, Martin A1 - Yusenko, Kirill A1 - Stawski, Tomasz A1 - Kulow, Anicó A1 - Cakir, Cafer Tufan A1 - Röder, Bettina A1 - Naese, Christoph A1 - Britzke, Ralf A1 - Sintschuk, Michael A1 - Emmerling, Franziska T1 - BAMline - A real-life sample materials research beamline N2 - With increasing demand and environmental concerns, researchers are exploring new materials that can perform as well or better than traditional materials while reducing environmental impact. The BAMline, a real-life sample materials research beamline, provides unique insights into materials’ electronic and chemical structure at different time and length scales. The beamline specializes in x-ray absorption spectroscopy, x-ray fluorescence spectroscopy, and tomography experiments. This enables real-time optimization of material properties and performance for various applications, such as energy transfer, energy storage, catalysis, and corrosion resistance. This paper gives an overview of the analytical methods and sample environments of the BAMline, which cover non-destructive testing experiments in materials science, chemistry, biology, medicine, and cultural heritage. We also present our own synthesis methods, processes, and equipment developed specifically for the BAMline, and we give examples of synthesized materials and their potential applications. Finally, this article discusses the future perspectives of the BAMline and its potential for further advances in sustainable materials research. KW - Extended X-ray absorption fine structure KW - Energy storage KW - Environmental impacts KW - Nondestructive testing techniques KW - X-ray fluorescence spectroscopy KW - Corrosion KW - Near edge X-ray absorption fine structure spectroscopy KW - X-ray absorption spectroscopy PY - 2023 DO - https://doi.org/10.1063/5.0157194 VL - 158 IS - 24 SP - 1 EP - 22 PB - AIP Publishing AN - OPUS4-57824 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Drago, C A1 - Wiesner, Yosri A1 - Braun, U A1 - Giovannozi, A A1 - Fadda, M A1 - Putzu, Mara A1 - Lorenzo, S A1 - Moscoso-Pérez, C A1 - Benismail, N A1 - Palma, C A1 - Almeida, J A1 - Mattarozzi, M A1 - Barbaresi, M A1 - Piergiovanni, M A1 - Masino, M A1 - Bianchi, F A1 - Careri, M A1 - v Bavel, B A1 - Maltseva, A A1 - Sillanpää, M A1 - Pröfrock, D A1 - Wippermann, D A1 - Altmann, Korinna T1 - Harmonisation of sample preparation for microplastic analysis: Recovery rates of tablets containing microplastics as reference material for food and environmental matrix N2 - Microplastic are found ubiquitarians in the environment and food products. Up to now, their impact of risks on health and environment is still controversially discussed, but based on the precautionary principle alone, their presence should be monitored and emission should be reduced (see here also the status of existing EU regulations ). The crucial point is not only the reduction of microplastics pollution but also the introduction of legally binding, standardized procedures for their analysis. The limited availability of certified reference material as well as absence of standard operating procedures to identify, characterize and quantify microplastics according to number and mass have generated lack of comparability between different analytical methods and laboratories; but also, the need of time-consuming development of own protocols for each laboratory. Further on, harmonisation and standardisation of microplastics analysis requires specific reference materials that are used to validate the measurement and to ensure the comparability of results. In the first step, we developed tablets of a water-soluble matrix, containing defined numbers of microplastic particles or mass contents. These can be solved in water and can be handled as reference materials in bottled drinking water without additional sample preparation. These samples can be measured, using mass-based methods as thermo-analytical methods like thermal desorption-gas chromatography-mass spectrometry (TED-GC/MS) or pyrolysis–gas chromatography–mass spectrometry (Py-GC/MS) and using umber-based methods as vibrational spectroscopy like Infrared and Raman directly after filtration. The aim of this work was to delevop standard operating procedure to measure microplastics in more complex matrices and to harmonise and compare different detection and characterization methods. In fact, these matrices require different additional treatments to allow a reliable quantification and identification of microplastics. T2 - SETAC Europe 2025 CY - Vienna, Austria DA - 11.05.2025 KW - Microplastics KW - Nanoplastics PY - 2025 AN - OPUS4-63366 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wiesner, Yosri A1 - Altmann, Korinna A1 - Braun, U. T1 - Determination of Microplastic Mass Content by Thermal Extraction Desorption Gas Chromatography– Mass Spectrometry N2 - The scientific and practical challenge of detecting microplastics (MPs) in the environment in a targeted and rapid manner is solved by innovative coupling of thermogravimetric analysis with mass spectrometric methods. Fast identification and quantitative determination of most thermoplastic polymers and elastomers is possible by using thermal extraction Desorption gas chromatography–mass spectrometry (TED-GC–MS). KW - Microplastics KW - Mikroplastik KW - TED-GC/MS KW - Microplastics analytic KW - Mikroplastik Massegehalt PY - 2021 VL - 17 IS - 3 SP - 2 EP - 7 PB - MultiMedia (UK) LLC CY - Cranbury AN - OPUS4-52570 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -