TY - JOUR A1 - Homann, C. A1 - Krukewitt, Lisa A1 - Frenzel, Florian A1 - Grauel, Bettina A1 - Würth, Christian A1 - Resch-Genger, Ute A1 - Haase, M. T1 - NaYF4:Yb,Er/NaYF4 Core/Shell Nanocrystals with High Upconversion Luminescence Quantum Yield N2 - Upconversion core/shell nanocrystals with different mean sizes ranging from 15 to 45 nm were prepared via a modified synthesis procedure based on anhydrous rare‐earth acetates. All particles consist of a core of NaYF4:Yb,Er, doped with 18 % Yb3+ and 2 % Er3+, and an inert shell of NaYF4, with the shell thickness being equal to the radius of the core particle. Absolute measurements of the photoluminescence quantum yield at a series of different excitation power densities show that the quantum yield of 45 nm core/shell particles is already very close to the quantum yield of microcrystalline upconversion phosphor powder. Smaller core/shell particles prepared by the same method show only a moderate decrease in quantum yield. The quantum yield of 15 nm core/shell particles, for instance, is reduced by a factor of three compared to the bulk upconversion phosphor at high power densities (100 W cm−2) and by approximately a factor of 10 at low power densities (1 W cm−2). KW - Core shell structure KW - Upconversion KW - Non lienear processes KW - Nanoparticle KW - Quantum yield PY - 2018 DO - https://doi.org/10.1002/anie.201803083 VL - 57 IS - 28 SP - 8765 EP - 8769 PB - Wiley-VCH AN - OPUS4-45574 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rifai, Haifa A1 - Staude, Andreas A1 - Meinel, Dietmar A1 - Illerhaus, Bernhard A1 - Bruno, Giovanni T1 - In-situ pore size investigations of loaded porous concrete with non-destructive methods N2 - Subject of this investigation is the in-situ evolution of pore volume and pore size distribution in Ytong (a porous concrete material) under increasing pressure with two different non-destructive analytical methods: Nuclear Magnetic Resonance (NMR) and X-ray Computed Tomography (CT). For both methods special strain devices to apply external pressure were constructed. The results from the two techniques yield complementary information on the pore size distribution and allows covering different pore size regions. KW - Pore size KW - Porous concrete KW - Computed tomography KW - Nuclear magnetic resonance PY - 2018 DO - https://doi.org/10.1016/j.cemconres.2018.06.008 SN - 0008-8846 SN - 1873-3948 VL - 111 SP - 72 EP - 80 PB - Elsevier Ltd. AN - OPUS4-45617 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ermawati, F. U. A1 - Supardi, Z. A. I. A1 - Suasmoro, S. A1 - Hübert, Thomas T1 - Contribution of Relaxation Effect to the Permittivity of Mg1-xZnxTiO3 Ceramics N2 - This work reported the investigation on the effect of relaxation to the permittivity (epsilon' r ) characteristic of Mg1-x Zn x TiO3 ceramics for x = 0 – 0.5 (MZT0 – MZT0.5) measured from 1 Hz to 330 MHz. Within that frequency range, the relaxation effect that consists of the space charge (SC) and the dipolar (D) polarization mechanisms were identified. The contribution of the D relaxation in MZT0 – MZT0.2 systems extents overall from about 100 Hz to 330 MHz, while that in MZT0.3 – MZT0.5 systems is from 50 kHz to 330 MHz. The remaining frequencies, i.e. from 1 to 90 Hz for MZT0 – MZT0.2 and from 1 Hz to 50 kHz for MZT0.3 – MZT0.5, are attributed to the SC relaxation. The D polarization mechanism provides constant epsilon' r values which vary from (15.4 – 17.0) ± 0.3 throughout the samples. Contribution of the SC polarization mechanism to the characteristic is supported by the simultaneous presence of different content and level of resistivity of the secondary phase of (Mg1-αZnα)2TiO4 in MZT0 – MZT0.2 systems and of (Zn1-αMgα)2TiO4 in MZT0.3 – MZT0.5, along with the presence of the main Mg1-x Zn x TiO3 phase, as a result of the variation of zinc content in the systems. T2 - The 5th International Conference on Advanced Materials Sciences and Technology (ICAMST 2017) CY - Makassar, Indonesia DA - 19.09.2017 KW - Dielectric ceramic KW - dipolar polarization KW - Mg1-xZnxTiO3 KW - permittivity KW - space charge polarization PY - 2018 DO - https://doi.org/10.1088/1757-899X/367/1/012003 SN - 1757-8981 VL - 367 SP - 1 EP - 6 PB - IOP Publishing Ltd AN - OPUS4-45618 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lauer, Franziska A1 - Diehn, Sabrina A1 - Seifert, Stephan A1 - Kneipp, Janina A1 - Sauerland, V. A1 - Barahona, C. A1 - Weidner, Steffen T1 - Multivariate analysis of MALDI imaging mass spectrometry data of mixtures of single pollen grains N2 - Mixtures of pollen grains of three different species (Corylus avellana, Alnus cordata, and Pinus sylvestris) were investigated by matrixassisted laser desorption/ionization time-of-flight imaging mass spectrometry (MALDI-TOF imaging MS). The amount of pollen grains was reduced stepwise from > 10 to single pollen grains. For sample pretreatment, we modified a previously applied approach, where any additional extraction steps were omitted. Our results show that characteristic pollen MALDI mass spectra can be obtained from a single pollen grain, which is the prerequisite for a reliable pollen classification in practical applications. MALDI imaging of laterally resolved pollen grains provides additional information by reducing the complexity of the MS spectra of mixtures, where frequently peak discrimination is observed. Combined with multivariate statistical analyses, such as principal component analysis (PCA), our approach offers the chance for a fast and reliable identification of individual pollen grains by mass spectrometry. KW - MALDI Imaging MS KW - Pollen grains KW - Multivariate Statistics KW - Hierarchical cluster analysis KW - Principal component analysis PY - 2018 DO - https://doi.org/10.1007/s13361-018-2036-5 SN - 1044-0305 SN - 1879-1123 VL - 29 IS - 11 SP - 2237 EP - 2247 PB - Springer AN - OPUS4-45607 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Keller, Julia A1 - Borzekowski, Antje A1 - Haase, H. A1 - Menzel, R. A1 - Rueß, L. A1 - Koch, Matthias T1 - Toxicity assay for citrinin, zearalenone and zearalenone-14-sulfate using the nematode Caenorhabditis elegans as model organism N2 - To keep pace with the rising number of detected mycotoxins, there is a growing need for fast and reliable toxicity tests to assess the potential threat to food safety. Toxicity tests with the bacterial-feeding nematode Caenorhabditis elegans as model organism are well established. In this study the C. elegans wildtype strain N2 (var. Bristol) was used to investigate the toxic effects of the food-relevant mycotoxins citrinin (CIT) and zearalenone-14-sulfate (ZEA-14-S) and zearalenone (ZEA) on different life cycle parameters including reproduction, thermal and oxidative stress resistance and lifespan. The metabolization of the mycotoxins by the nematodes in vivo was investigated using HPLC-MS/MS. ZEA was metabolized in vivo to the reduced isomers α-zearalenol (α-ZEL) and β-ZEL. ZEA 14-S was reduced to α-/β-ZEL 14-sulfate and CIT was metabolized to mono-hydroxylated CIT. All mycotoxins tested led to a significant decrease in the number of nematode offspring produced. ZEA and CIT displayed negative effects on stress tolerance levels and for CIT an additional shortening of the mean lifespan was observed. In the case of ZEA-14-S, however, the mean lifespan was prolonged. The presented study shows the applicability of C. elegans for toxicity testing of emerging food mycotoxins for the purpose of assigning potential health threats. KW - Mycotoxins KW - Metabolization KW - Toxicity testing KW - Biotests PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-455772 DO - https://doi.org/10.3390/toxins10070284 VL - 10 IS - 7 SP - 284, 1 EP - 12 PB - MDPI AN - OPUS4-45577 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Al-Terkawi, Abdal-Azim A1 - Scholz, Gudrun A1 - Emmerling, Franziska A1 - Kemnitz, Erhard T1 - Barium coordination polymers based on fluorinated and fluorine-free benzene-dicarboxylates: Mechanochemical synthesis and spectroscopic characterization N2 - A series of new Ba-based coordination polymers (CPs) were mechanochemically synthesized by milling Ba-hydroxide samples with perfluorinated and fluorine-free benzene-dicarboxylic acids, including tetrafluoroisophthalic acid (H2mBDC-F4), tetrafluorophthalic acid (H2oBDC-F4), isophthalic acid (H2mBDC) and phthalic acid (H2oBDC). The new fluorinated CPs: [Ba(mBDC-F4)$0.5H2O] (1) and [Ba(oBDC-F4)·1.5H2O] (2) are compared to their nonfluorinated counterparts: [Ba(mBDC)·2.5H2O] (3), and [Ba(oBDC)·1H2O] (4). These materials are thoroughly characterized using powder X-ray diffraction. The products obtained by milling are all hydrated but vary in their water contents. Compositions and local structures are investigated by elemental analysis, thermal analysis, MAS NMR and attenuated total reflectioninfrared spectroscopy. These materials exhibit high thermal stabilities but small surface areas that remain unchanged even after thermal treatments. KW - Mechanochemical synthesis KW - Barium KW - Fluorine KW - Coordination polymers KW - PXRD KW - MAS NMR spectroscopy PY - 2018 UR - https://www.sciencedirect.com/science/article/pii/S1293255817310798 DO - https://doi.org/10.1016/j.solidstatesciences.2018.03.013 SN - 1293-2558 SN - 1873-3085 VL - 79 SP - 99 EP - 108 PB - Elsevier AN - OPUS4-44880 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wang, Cui A1 - Otto, S. A1 - Dorn, M. A1 - Kreidt, E. A1 - Lebon, J. A1 - Sršan, L. A1 - Di Martino-Fumo, P. A1 - Gerhards, M. A1 - Resch-Genger, Ute A1 - Seitz, M. A1 - Heinze, K. T1 - Deuterated molecular ruby with record luminescence quantum yield N2 - The recently reported luminescent chromium(III) complex 13+ ([Cr(ddpd)2]3+; ddpd=N,N’-dimethyl-N,N’-dipyridine-2-yl-pyridine-2,6-diamine) shows exceptionally strong near-IR emission at 775 nm in water under ambient conditions (F=11%) with a microsecond lifetime as the ligand design in 13+ effectively eliminates non-radiative decay pathways, such as photosubstitution, back-intersystem crossing, and trigonal twists. In the absence of energy acceptors, such as dioxygen, the remaining decay pathways are energy transfer to high energy solvent and ligand oscillators, namely OH and CH stretching vibrations. Selective deuteration of the solvents and the ddpd ligands probes the efficiency of these oscillators in the excited state deactivation. Addressing these energytransfer pathways in the first and second coordination sphere furnishes a record 30% quantum yield and a 2.3 millisecond lifetime for a metal complex with an earth-abundant metal ion in solution at room temperature. The combined fundamental insights will pave the way for selective design strategies in the field of luminescent complexes with earth-abundant metal ions. KW - Record luminescence quantum yield KW - Phorsphorescence KW - Cr-complex KW - Lifetime PY - 2018 DO - https://doi.org/10.1002/ange.201711350 DO - https://doi.org/10.1002/anie.201711350 SN - 1521-3773 VL - 57 IS - 4 SP - 1112 EP - 1116 PB - Wiley-VCH Verlag & Co. KGaA CY - Weinheim AN - OPUS4-45085 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tan, K. H. A1 - Sattari, S. A1 - Donskyi, Ievgen A1 - Cuellar-Camacho, J. L. A1 - Cheng, C. A1 - Schwibbert, Karin A1 - Lippitz, Andreas A1 - Unger, Wolfgang A1 - Gorbushina, Anna A1 - Adeli, M. A1 - Haag, R. T1 - Functionalized 2D nanomaterials with switchable binding to investigate graphene–bacteria interactions N2 - Graphene and its derivatives have recently attracted much attention for sensing and deactivating pathogens. However, the mechanism of multivalent interactions at the graphene–pathogen interface is not fully understood. Since different physicochemical parameters of graphene play a role at this interface, control over graphene’s structure is necessary to study the mechanism of these interactions. In this work, different graphene derivatives and also zwitterionic graphene nanomaterials (ZGNMs) were synthesized with defined exposure, in terms of polymer coverage and functionality, and isoelectric points. Then, the switchable interactions of these nanomaterials with E. coli and Bacillus cereus were investigated to study the validity of the generally proposed “trapping” and “nano-knives” mechanisms for inactivating bacteria by graphene derivatives. It was found that the antibacterial activity of graphene derivatives strongly depends on the accessible area, i.e. edges and basal plane of sheets and tightness of their agglomerations. Our data clearly confirm the authenticity of “trapping” and “nano-knives” mechanisms for the antibacterial activity of graphene sheets. KW - XPS KW - Graphene KW - Graphene–bacteria interaction PY - 2018 DO - https://doi.org/10.1039/c8nr01347k SN - 2040-3364 SN - 2040-3372 VL - 10 IS - 20 SP - 9525 EP - 9537 PB - RSC CY - London AN - OPUS4-45084 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hiebl, B. A1 - Ascher, Lena A1 - Luetzow, K. A1 - Kratz, K. A1 - Gruber, C. A1 - Mrowietz, C. A1 - Nehring, M. E. A1 - Lendlein, A. A1 - Franke, R.- P. A1 - Jung, F. T1 - Albumin solder covalently bound to a polymer membrane: New approach to improve binding strength in laser tissue soldering in-vitro N2 - Laser tissue soldering (LTS) based on indocyanine green (ICG)-mediated heat- denaturation of proteins might be a promising alternative technique for micro-suturing, but up to now the Problem of too weak shear strength of the solder welds in comparison to sutures is not solved. Earlier reports gave promising results showing that solder supported by carrier materials can enhance the cohesive strength of the liquid solder. In these studies, the solder was applied to the carriers by dip coating. Higher reliability of the connection between the solder and the carrier material is expected when the solder is bound covalently to the carrier material. In the present study a poly(ether imide) (PEI) membrane served as carrier material and ICG- supplemented albumin as solder substrate. The latter was covalently coupled to the carrier membrane under physiological conditions to prevent structural protein changes. As laser source a diode continuous-wave laser emitting at 808 nm with intensities between 250mW and 1500mW was utilized. The Albumin functionalized carrier membrane was placed onto the tunica media of explanted pig thoracic aortae forming an overlapping area of approximately 0.5×0.5 cm2. All tests were performed in a dry state to prevent laser light absorption by water. Infrared spectroscopy, spectro-photometrical determination of the secondary and Primary amine groups after acid orange II staining, contact angle measurements, and atomic force microscopy proved the successful functionalization of the PEI membrane with albumin. A laser power of 450mW LTS could generate a membrane-blood vessel connection which was characterized by a shear strength of 0.08±0.002MPa, corresponding to 15% of the tensile strength of the native blood vessel. Theoretically, an overlapping zone of 4.1mmaround the entire circumference of the blood vessel could have provided shear strength of the PEI membrane-blood vessel compound identical to the tensile strength of the native blood vessel. These in-vitro results confirmed the beneficial effects of solder reinforcement by carrier membranes, and suggest LTS with covalently bound solders on PEI substrates for further studies in animal models. KW - Tissue soldering KW - Albumin KW - Polymer membrane KW - Laser PY - 2018 DO - https://doi.org/10.3233/CH-189108 SN - 1386-0291 SN - 1875-8622 VL - 69 IS - 1-2 SP - 317 EP - 326 PB - IOS Press AN - OPUS4-45149 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Breitfeld, Steffen A1 - Scholz, G. A1 - Emmerling, Franziska A1 - Kemnitz, E. T1 - BaF-benzenedicarboxylate: the first mechanochemical N2 - Anewbariumcoordination polymer, BaF-benzenedicarboxylate (BaF(p-BDC)0.5), with fluorine directly coordinated to the metal cation, was prepared by mechanochemical synthesis routes. Phase-pure BaF-benzenedicarboxylate was synthesized by milling starting either from barium hydroxide or from Barium acetate as sources for barium cations. In both cases, the second reactant was 1,4-benzenedicarboxylic acid (H2(p-BDC)). Ammonium fluoride was used as fluorinating agent directly at milling. This is the first mechanochemical synthesis of coordination polymers where fluorine is directly coordinated to the metal cation. Following the second possibility, barium acetate fluoride (Ba(OAc)F) is formed as ntermediate product after milling, and the new coordination polymer is accessible only after washing with water and dimethyl sulfoxide. The new compound BaF(p-BDC)0.5 was characterized by X-ray powder diffraction, FTIR-, and 19F, 1H-13C CP MAS NMR spectroscopies, DTA-TG, and elemental Analysis. KW - Milling KW - MOF PY - 2018 DO - https://doi.org/10.1007/s10853-018-2331-3 SN - 0022-2461 VL - 53 IS - 19 SP - 13682 EP - 13689 PB - Springer AN - OPUS4-45677 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Emmerling, Franziska A1 - Haferkamp, Sebastian A1 - Kraus, Werner T1 - Studies on the mechanochemical Knoevenagel condensation of fluorinated benzaldehyde derivates N2 - The mechanochemical Knoevenagel condensation of three fluorinated benzaldehyde derivates and malononitrile was investigated. The reactions were performed under solvent- and catalyst-free conditions and resulted in highly crystalline products after crystallization from a viscous phase in the milling jar. The quality of the obtained crystals was sufficient for single-crystal X-ray diffraction circumventing a recrystallization step. To gain more information on the reaction, progress was investigated in situ using time-resolved Raman spectroscopy. The results show a direct conversion of the reactants. KW - C-C coupling KW - Knoevenagel condensation KW - In situ KW - Mechanochemistry PY - 2018 DO - https://doi.org/10.1007/s10853-018-2492-0 SN - 0022-2461 VL - 53 IS - 19 SP - 13713 EP - 13718 PB - Springer Link AN - OPUS4-45682 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bosch, S. A1 - Colini, C. A1 - Hahn, Oliver A1 - Janke, A. A1 - Shevchuk, I. ED - Friedrich, M. ED - Quenzer, J. ED - Wandrey, I. T1 - The Atri fragment revisited I: Multispectral imaging and ink identification N2 - This paper reports the outcome of an interdisciplinary team’s application of multispectral imaging techniques and material analysis to a music fragment from the first decades of the fifteenth century: Atri, Archivio Capitolare, Museo della Basilica Cattedrale, Biblioteca del Capitolo della Cattedrale, Frammento 17. This important parchment leaf has rarely been investigated since its discovery 45 years ago. Thanks to the applied techniques and methods (such as the evaluation of the data using the fingerprint model), it is now possible to discuss new evidence supporting conclusions regarding the fragment’s origin and afterlife. KW - Archaeometry KW - Cultural heritage KW - Non-destructiv testing PY - 2018 SN - 1867-9617 VL - 2018 IS - 11 SP - 141 EP - 156 PB - Universität Hamburg CY - Hamburg AN - OPUS4-45741 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schürmann, Robin A1 - Vogel, Stefanie A1 - Ebel, Kenny A1 - Bald, Ilko T1 - The physico-chemical basis of DNA radiosensitization: Implications for cancer radiation therapy N2 - High-energy radiation is used in combination with radiosensitizing therapeutics to treat cancer. The most common radiosensitizers are halogenatednucleo-sides and cisplatin derivatives, and recently also metal nanoparticles have been suggested as potentialradiosensitizing agents. The radiosensitizingaction of these compounds can at least partly be ascribed to an enhancedreactivity towards secondary low-energy electrons generated along the radiation track of the high-energyprimary radiation, or to an additional emission of secondary reactive electrons close to the tumor tissue. This is referred to as physico-chem ical radiosensitization. In this Conceptarticle we presentcurrent experimental methodsused to study fundamentalprocesses of physico-chemical radiosensitization and discuss the most relevant classes of radiosensitizers. Open questions in the current discussions are identified and future directions outlined, which can lead to optimized treatment protocols or even novel therapeuticconcepts. KW - DNA KW - Radiosensitization KW - Radiation damage KW - Low energy electrons PY - 2018 DO - https://doi.org/10.1002/chem.201800804 SN - 1521-3765 SN - 0947-6539 VL - 24 IS - 41 SP - 10271 EP - 10279 PB - WILEY AN - OPUS4-45742 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Heck, Christian A1 - Kanehira, Y. A1 - Kneipp, Janina A1 - Bald, Ilko T1 - Placement of single proteins within the SERS hot spots of self-assembled silver nanolenses N2 - This study demonstrates the bottom-up synthesis of silver nanolenses.Arobust coating protocol enabled the functionalization of differently sized silver nanoparticles with DNAsingle strands of orthogonal sequence.Coated particles 10 nm, 20 nm, and 60 nm in diameter were self-assembled by DNAorigami scaffolds to form silver nanolenses.Single molecules of the protein streptavidin were selectively placed in the gap of highest electric field enhancement. Streptavidin labelled with alkyne groups served as model analyte in surface- enhanced Raman scattering (SERS) experiments.Bycorre- lated Raman mapping and atomic force microscopy, SERS signals of the alkyne labels of asingle streptavidin molecule, from asingle silver nanolens,were detected. The discrete,self- similar aggregates of solid silver nanoparticles are promising for plasmonic applications. KW - DNA origami KW - Surface enhanced Raman scattering KW - Protein KW - Single molecule KW - Nanotechnology PY - 2018 DO - https://doi.org/10.1002/anie.201801748 SN - 1433-7851 VL - 57 IS - 25 SP - 7444 EP - 7447 PB - WILEY AN - OPUS4-45743 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schaepe, Kaija A1 - R. Bhandari, D. A1 - Werner, J. A1 - Henss, A. A1 - Pirkl, A. A1 - Kleine-Boymann, M. A1 - Rohnke, M. A1 - Wenisch, S. A1 - Neumann, E. A1 - Janek, J. A1 - Spengler, B. T1 - Imaging of lipids in native human bone sections using TOF-secondary ion mass spectrometry, atmospheric pressure scanning microprobe matrix-assisted laser desorption/ionization orbitrap mass spectrometry, and orbitrap-secondary ion mass spectrometry N2 - A method is described for high-resolution label-free molecular imaging of human bone tissue. To preserve the lipid content and the heterogeneous structure of osseous tissue, 4 μm thick human bone sections were prepared via cryoembedding and tape-assisted cryosectioning, circumventing the application of organic solvents and a decalcification step. A protocol for comparative mass spectrometry imaging (MSI) on the same section was established for initial analysis with time-of-flight secondary ion mass spectrometry (TOF-SIMS) at a lateral resolution of 10 μm to <500 nm, followed by atmospheric pressure scanning microprobe matrix-assisted laser desorption/ionization (AP-SMALDI) Orbitrap MSI at a lateral resolution of 10 μm. This procedure ultimately enabled MSI of lipids, providing the lateral localization of major lipid classes such as glycero-, glycerophospho-, and sphingolipids. Additionally, the applicability of the recently emerged Orbitrap-TOF-SIMS hybrid system was exemplarily examined and compared to the before-mentioned MSI methods. KW - ToF-SIMS KW - MALDI KW - Mass spectrometry imaging KW - Lipids KW - Osteoporosis KW - Bone KW - Surface analysis PY - 2018 UR - https://pubs.acs.org/doi/10.1021/acs.analchem.8b00892 DO - https://doi.org/10.1021/acs.analchem.8b00892 SN - 0003-2700 SN - 1520-6882 VL - 90 IS - 15 SP - 8856 EP - 8864 PB - ACS Publ. CY - Washington, DC AN - OPUS4-45730 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wiggenhauser, Herbert A1 - Köpp, Christian A1 - Timofeev, Juri A1 - Azari, H. T1 - Controlled creating of cracks in concrete for non-destructive testing N2 - The non-destructive assessment of cracks in concrete is a common task for which non-destructive evaluation solutions have been published. Primarily, these tests have been carried out on artificial cracks that have been created by using notches instead of natural cracks. This study evaluates a procedure designed to create reproducible and controlled cracks in concrete. The procedure is based on using expanding mortar in a series of blind holes. This is done in combination with carefully aligned reinforcement to guide the direction of the crack development. The depth of the crack is also controlled by reinforcement. Crack depth varies statistically in the range of the Maximum aggregate size (16 mm) used for concrete. KW - Non-destructive testing of concrete KW - Cracks KW - Reference specimen PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-457367 UR - https://rdcu.be/4IPN DO - https://doi.org/10.1007/s10921-018-0517-x SN - 0195-9298 SN - 1573-4862 VL - 37 IS - 3 SP - 67, 1 EP - 9 PB - Springer CY - New York AN - OPUS4-45736 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Oesch, Tyler A1 - Weise, Frank A1 - Bruno, Giovanni T1 - Detection and Quantification of Cracking in Concrete Aggregate through Virtual Data Fusion of X-ray Computed Tomography Images N2 - In this work, which is part of a larger research program, a framework called “virtual data fusion“ was developed to provide an automated and consistent crack detection method that allows for the cross-comparison of results from large quantities of X-ray Computed Tomography (CT) data. A partial implementation of this method in a custom program was developed for use in research focused on crack quantification in Alkali-Silica Reaction (ASR)-sensitive concrete aggregates. During the CT image processing, a series of image analyses tailored for detecting specific, individual crack-like characteristics were completed. The results of these analyses were then “fused” in order to identify crack-like objects within the images with much higher accuracy than that yielded by any individual image analysis procedure. The results of this strategy demonstrated the success of the program in effectively identifying crack-like structures and quantifying characteristics, such as surface area and volume. The results demonstrated that the source of aggregate has a very significant impact on the amount of internal cracking, even when the mineralogical characteristics remain very similar. River gravels, for instance, were found to contain significantly higher levels of internal cracking than quarried stone aggregates of the same mineralogical type. KW - X-ray Computed Tomography (CT) KW - Alkali-Silica Reaction (ASR) KW - Crack Detection KW - Damage Quantification KW - ASR-Sensitive Aggregate PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-512170 DO - https://doi.org/10.3390/ma13183921 VL - 13 IS - 18 SP - Paper 3921 PB - MDPI CY - Basel, Switzerland AN - OPUS4-51217 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Song, L. A1 - You, Yi A1 - Perdomo, R. A1 - Evans-Nguyen, T. T1 - Inexpensive Ultrasonic Nebulization Coupled with Direct Current Corona Discharge Ionization Mass Spectrometry for Liquid Samples and Its Fundamental Investigations N2 - The concept of direct mass-spectrometric analysis, especially exploited by ambient desorption/ionization (ADI) methods, provides numerous means for convenient sample analysis. While many simple and versatile ionization sources have been developed, challenges lay in achieving efficient sample introduction. In previous work, a sample introduction method employing direct current corona discharge (CD) coupled to a surface acoustic wave nebulization (SAWN) device enhanced sampling performance for both polar and nonpolar analytes by up to 4 orders of magnitude. In fact, the SAWN-CD method generated a multiply charged peptide ion signal comparable to that of conventional ESI. Unfortunately, the high cost of the SAWN devices themselves limits their accessibility. Herein, we report on an analogous implementation of CD with an inexpensive ultrasonic nebulizer (USN) on the basis of a commercial room humidifier demonstrating equivalent exemplary performance. We subsequently compare the two methods of SAWN-CD and USN-CD in a screening application of milk for the detection of two antibiotic drugs, ciprofloxacin and ampicillin. Finally, we further investigate the relative softness of these CD-coupled acoustic nebulization methods in comparison to that of ESI using a survival yield study of the thermometer ion nitrobenzylpyridinium. KW - Rapid Analysis KW - Ultrasonic Nebulization KW - Corona Discharge PY - 2020 DO - https://doi.org/10.1021/acs.analchem.0c00524 VL - 92 IS - 16 SP - 11072 PB - ACS Publication AN - OPUS4-51225 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mirtsch, Mona A1 - Kinne, J. A1 - Blind, K. T1 - Exploring the Adoption of the International Information Security Management System Standard ISO/IEC 27001: A Web Mining-Based Analysis N2 - In the light of digitalization and recent EU policy initiatives, information is an important asset that organizations of all sizes and from all sectors should secure. However, in order to provide common requirements for the implementation of an information security management system, the internationally well-accepted ISO/IEC 27001 standard has not shown the expected growth rate since its publication more than a decade ago.In this article, we apply web mining to explore the adoption of ISO/IEC 27001 through a series of 2664 out of more than 900 000 German firms from the Mannheim Enterprise Panel dataset that refers to this standard on their websites. As a result, we present a “landscape” of ISO/IEC 27001 in Germany, which shows that firms not only seek certifications themselves but often refer on their websites to partners who are certified instead. Consequently, we estimate a probit model and find that larger and more innovative firms are more likely to be certified to ISO/IEC 27001 and that almost half of all certified firms belong to the information and communications technology (ICT) service sector. Based on our findings, we derive implications for policymakers and management and critically assess the suitability of web mining to explore the adoption of management system standards. KW - Adoption KW - Information security KW - Management system standards KW - Standards KW - Web mining PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-513284 DO - https://doi.org/10.1109/TEM.2020.2977815 VL - 68 IS - 1 SP - 87 EP - 100 AN - OPUS4-51328 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Koch, Claudia A1 - Blind, K. T1 - Towards Agile Standardization: Testbeds in Support of Standardization for the IIoT N2 - The Industrial Internet of Things (IIoT) poses multiple challenges to traditional standardization, due to the complexity, dynamics, and accelerating speed of technological progress. The need for a timely availability of standards calls for new approaches and tools to enhance standardization processes for smart manufacturing. Industry and standards development organizations worldwide are seeking new solutions. Testbeds have been acknowledged in innovation policy as a powerful tool for knowledge transfer and the further development of emerging technologies. Lately, they have also attracted increasing attention from the standardization perspective as a promising tool for a more agile standards development process. Proponents of such testbeds expect them to support standardization by providing validated solutions and accelerating the processes to meet the growing demands for faster standardization without any detriment to quality. In an explorative, qualitative approach this article is the first to investigate the operation and impact of testbeds in standardization processes based on a multiple case study on testbeds implemented worldwide in the context of the IIoT. KW - Testumgebung KW - Reallabor KW - Normung KW - Standards KW - Standardization KW - Industrie 4.0 KW - Smart manufacturing KW - Industrial internet of things KW - Agility KW - Agile PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-513300 DO - https://doi.org/10.1109/TEM.2020.2979697 VL - 68 IS - 1 SP - 59 EP - 74 AN - OPUS4-51330 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -