TY - JOUR A1 - Gottlieb, Cassian A1 - Günther, Tobias A1 - Wilsch, Gerd T1 - Impact of grain sizes on the quantitative concrete analysis using laser-induced breakdown spectroscopy JF - Spectrochimica Acta Part B: Atomic Spectroscopy N2 - In civil engineering concrete is the most used building material for making infrastructures like bridges and parking decks worldwide. It is as a porous and multiphase material made of aggregates with a defined grain size distribution, cement and water as well as different additives and admixtures depending on the application. Different grain sizes are important to ensure the needed density and compressive strength. The resulting porous cement matrix contains a mixture of flour grains (aggregates with a grain size below 125 lm) and cement particles (particle size≈50lm). Harmful species like chlorides may penetrate together with water through the capillary pore space and may trigger different damage processes. The damage assessment of concrete structures in Germany is estimated due to the quantification of harmful elements regarding to the cement content only. In the evaluation of concrete using LIBS a two-dimensional scanning is necessary to consider the heterogeneity caused by the aggregates. Therefore, a LIBS system operating with a low energy NdCr:YAG laser, a pulse energy of 3 mJ, a wavelength of 1064 nm, a pulse width of 1.5 ns and a Repetition rate of 100 Hz has been used. Different Czerny-Turner spectrometers with CCD detectors in the UV and NIR range have been used for the detection. Large aggregates (macro-heterogeneity) can be excluded from the evaluation, whereas small aggregates in the range of the laser spot size (flour grains) cannot be spatially resolved. In this work the micro heterogeneity caused by flour grains and their impact on the quantification with LIBS will be discussed. To analyze the effect of changing grain sizes and ratios, the ablation behavior has been determined and compared. Samples with defined grain sizes were made and analyzed using LIBS. The grain size distributions were analyzed with laser diffraction (LDA). KW - LIBS KW - Concrete KW - Micro heterogeneity KW - Grain sizes PY - 2018 DO - https://doi.org/10.1016/j.sab.2018.02.004 SN - 0584-8547 SN - 0038-6987 VL - 142 SP - 74 EP - 84 PB - Elsevier AN - OPUS4-44595 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gottlieb, Cassian A1 - Günther, Tobias A1 - Wilsch, Gerd A1 - Gornushkin, Igor B. A1 - Gojani, Ardian T1 - Temporal evaluation and imaging of laser-induced plasmas on cement-based materials N2 - In civil engineering, the laser-induced breakdown spectroscopy has been applied as a fast and reliable method for a quantitative evaluation of concrete cores. Due to a two-dimensional scanning, the heterogeneity of concrete can be evaluated and elements like Cl, Na, and S are related to the cement matrix only. This study deals with the temporal evaluation and imaging of laser-induced plasmas on cement-based materials, in order to investigate the impact of aggregates with diffrent grain size on the spectral response in LIBS. T2 - Xth international conference on Laser-Induced Breakdown Spectroscopy CY - Atlanta, GA, USA DA - 21.10.2018 KW - LIBS KW - Concrete KW - Grain size PY - 2018 AN - OPUS4-46794 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilsch, Gerd A1 - Gottlieb, Cassian A1 - Günther, Tobias A1 - Millar, Steven ED - Forde, Mike T1 - Application of laser induced breakdown spectroscopy T2 - Structural Faults + Repair-2018 N2 - A big part of the infrastructure is made of concrete, which is a multiphase system made of cement, aggregates, water and pores. Concrete is often used in combination with steel as reinforced concrete. Environmental influences, especially the ingress of harmful ions in combination with the ingress of water, trigger different damage processes which reduce the designed lifetime of a structure. The ingress of chlorides from de-icing salt or sea water leads to corrosion of the reinforcement. In addition, the carbonation of the concrete may trigger the corrosion of the reinforcement. The ingress of alkalis from deicing salts may cause the expansion of the amorphous silica aggregates (alkali-silica reaction) through formation of a swelling gel of calcium silicate hydrate if water is present. The ingress of sulphates may cause spalling of the concrete surface due to ettringite formation. For the standard procedure in civil engineering cores are taken, cut in slices, grinded and the obtained homogenized powder is solved in acid and investigated by standard procedures. BAM has developed the LIBS technique for the 2D evaluation of the chemical composition of concrete. The technique is established for automated laboratory use with high numbers of samples to investigate transport processes of harmful species (Cl-, CO2 , SO4 2-and alkalis) in concrete. Information about ingress depth and the quantitative values are important to estimate the remaining lifetime of the infrastructure. LIBS is a surface technique. To get information about the ingress depth, a drill core has to be taken and cut in the middle. The measurements are carried out at the cross section. The main advantages of LIBS are the direct measurement on the surface of the concrete, fast analysis (sample rate 100 Hz) with a spatial resolution of up to 100 µm, the consideration of the heterogeneity of the concrete and the possibility of automated measurements which save a lot of manpower and time. As an example the investigation of ingress profiles for standard diffusion and migration tests in civil engineering takes hours in comparison to just a few minutes using LIBS. At the same time a 2D-evaluation provides information about hot spots of elemental concentration which may not be found by standard methods. The state of the art of LIBS technique for applications in civil engineering will be presented, including typical results of 2D investigation of concrete in laboratory. The performance is also demonstrated by examples for onsite applications using a mobile LIBS system. The road map to standardization is presented as well. T2 - Structural Faults + Repair-2018 CY - Edinburgh, UK DA - 15.05.2018 KW - Sulphate KW - Chloride KW - Concrete KW - LIBS PY - 2018 SN - 0-947644-86-5 DO - https://doi.org/10.25084/sfr.2018.0030 SP - 1 EP - 7 PB - University of Edinburgh CY - Edinburgh AN - OPUS4-46947 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -