TY - JOUR A1 - Amouroux, B. A1 - Eftekhari, A. A1 - Roux, C. A1 - Micheau, J. A1 - Roblin, P. A1 - Pasturel, M. A1 - Gauffre, F. A1 - Würth, Christian A1 - Resch-Genger, Ute A1 - Sliwa, M. A1 - Bouchet, A. A1 - Coudret, C. T1 - Synthesis and Emission Dynamics of Sub-3 nm Upconversion Nanoparticles N2 - Reducing the size of upconversion nanoparticles (UCNPs) down to a few nm yields luminescent materials containing a very small number of emitters. Considering the bottom limit of one activator per particle ultrasmall UCNPs offer an unprecedented platform to study the contributions of the energy transfers at play in upconversion luminescence. Maintaining detectable emission despite the limited number of emitting ions and the high surface-to-volume ratio requires suitable particle architectures. Na(Gd-Yb)F4:Tm3+ emissive sub-3 nm diameter 𝜷-phase UCNPs are prepared using a gadolinium-rich composition in situ mixing of the precursors and a microwave high-temperature cycling sequence allowing precise control of the particle size and dispersity. These cores are coated with a NaGdF4 inert shell to minimize the deleterious influence of surface quenching (SQ). Time-resolved luminescence measurements combining standard NIR excitation of the Yb3+ sensitizer and direct UV excitation of the Tm3+ activator are performed to quantify cross relaxation and surface quenching processes. The fine tuning of the number of activators per particle via an optimized synthesis pathway along with the use of an appropriate excitation scheme enabled to provide an accurate analysis of the different mechanisms at play in these model nanoparticles and to characterize the structure of the core-shell architecture. KW - Lanthanide KW - Nanoparticle KW - Luminescence KW - Quantitative spectroscopy KW - Quantum yield KW - Energy transfer KW - Quality assurance KW - Synthesis KW - Surface modification KW - Photophysics PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-606877 DO - https://doi.org/10.1002/adom.202303283 SN - 2195-1071 SP - 1 EP - 13 AN - OPUS4-60687 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zou, Q. A1 - Marcelot, C. A1 - Ratel-Ramond, N. A1 - Yi, X. A1 - Roblin, P. A1 - Frenzel, Florian A1 - Resch-Genger, Ute A1 - Eftekhari, A. A1 - Bouchet, A. A1 - Coudret, C. A1 - Verelst, M. A1 - Chen, X. A1 - Mauricot, R. A1 - Roux, C. T1 - Heterogeneous Oxysulfide@Fluoride Core/ Shell Nanocrystals for Upconversion-Based Nanothermometry N2 - Lanthanide (Ln3+)-doped upconversion nanoparticles (UCNPs) often suffer from weak luminescence, especially when their sizes are ultrasmall (less than 10 nm). Enhancing the upconversion luminescence (UCL) efficiency of ultrasmall UCNPs has remained a challenge that must be undertaken if any practical applications are to be envisaged. Herein, we present a Ln3+-doped oxysulfide@fluoride core/shell heterostructure which shows efficient UCL properties under 980nm excitation and good stability in solution. Through epitaxial heterogeneous growth, a ∼4 nm optically inert β-NaYF4 shell was coated onto ∼5 nm ultrasmall Gd2O2S:20%Yb,1%Tm. These Gd2O2S:20%Yb,1%Tm@NaYF4 core/shell UCNPs exhibit a more than 800-fold increase in UCL intensity compared to the unprotected core, a 180-fold increase in luminescence decay time of the 3H4 → 3H6 Tm3+ transition from 5 to 900 μs, and an upconversion quantum yield (UCQY) of 0.76% at an excitation power density of 155 W/cm2. Likewise, Gd2O2S:20%Yb,2%Er@NaYF4 core/shell UCNPs show a nearly 5000-fold increase of their UCL intensity compared to the Gd2O2S:20%Yb,2%Er core and a maximum UCQY of 0.61%. In the Yb/Er core−shell UCNP system, the observed variation of luminescence intensity ratio seems to originate from a change in lattice strain as the temperature is elevated. For nanothermometry applications, the thermal sensitivities based on thermally coupled levels are estimated for both Yb/Tm and Yb/Er doped Gd2O2S@NaYF4 core/shell UCNPs. KW - Upconversion nanoparticle KW - Nanosensor KW - Lanthanide KW - Surface coating KW - Quantum yield KW - Photophysic PY - 2022 DO - https://doi.org/10.1021/acsnano.2c02423 SN - 1936-0851 SP - 1 EP - 11 PB - ACS Publications AN - OPUS4-55440 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -