TY - JOUR A1 - Ulbricht, Alexander A1 - Altenburg, Simon A1 - Sprengel, Maximilian A1 - Sommer, Konstantin A1 - Mohr, Gunther A1 - Fritsch, Tobias A1 - Mishurova, Tatiana A1 - Serrano-Munoz, Itziar A1 - Evans, Alexander A1 - Hofmann, M. A1 - Bruno, Giovanni T1 - Separation of the Formation Mechanisms of Residual Stresses in LPBF 316L N2 - Rapid cooling rates and steep temperature gradients are characteristic of additively manufactured parts and important factors for the residual stress formation. This study examined the influence of heat accumulation on the distribution of residual stress in two prisms produced by Laser Powder Bed Fusion (LPBF) of austenitic stainless steel 316L. The layers of the prisms were exposed using two different border fill scan strategies: one scanned from the centre to the perimeter and the other from the perimeter to the centre. The goal was to reveal the effect of different heat inputs on samples featuring the same solidification shrinkage. Residual stress was characterised in one plane perpendicular to the building direction at the mid height using Neutron and Lab X-ray diffraction. Thermography data obtained during the build process were analysed in order to correlate the cooling rates and apparent surface temperatures with the residual stress results. Optical microscopy and micro computed tomography were used to correlate defect populations with the residual stress distribution. The two scanning strategies led to residual stress distributions that were typical for additively manufactured components: compressive stresses in the bulk and tensile stresses at the surface. However, due to the different heat accumulation, the maximum residual stress levels differed. We concluded that solidification shrinkage plays a major role in determining the shape of the residual stress distribution, while the temperature gradient mechanism appears to determine the magnitude of peak residual stresses. KW - Additive Manufacturing KW - Laser Powder Bed Fusion KW - LPBF KW - AISI 316L KW - Online Process Monitoring KW - Thermography KW - Residual Stress KW - Neutron Diffraction KW - X-ray Diffraction KW - Computed Tomography PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-512903 DO - https://doi.org/10.3390/met10091234 VL - 10 IS - 9 PB - MDPI CY - Basel AN - OPUS4-51290 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kupsch, Andreas A1 - Trappe, Volker A1 - Müller, Bernd R. A1 - Bruno, Giovanni T1 - Evolution of CFRP stress cracks observed by in situ X-ray refractive imaging N2 - Modern air-liners and wind turbine rotor blades are made up primarily of fiber reinforced plastics. Failure of these materials heavily impairs the serviceability and the operational safety. Consequently, knowledge of the failure behavior under static and cyclic loads is of great interest to estimate the operational strength and to compare the performance of different materials. Ideally, the damage evolution under operational load is determined with in situ non-destructive testing techniques. Here, we report in-situ synchrotron X-ray imaging of tensile stress induced cracks in carbon fiber reinforced plastics due to inter-fiber failure. An inhouse designed compact tensile testing machine with a load range up to 15 kN was integrated into the beamline. Since conventional radiographs do not reveal sufficient contrast to distinguish cracks due to inter-fiber failure and micro cracking from fiber bundles, the Diffraction Enhanced Imaging (DEI) technique is applied in order to separate primary and scattered (refracted) radiation by means of an analyzer crystal. This technique allows fast measurements over large fields-of-view and is ideal for in-situ investigations. Imaging and the tensile test are run at the highest possible frame rate (0.7 s-1 ) and the lowest possible strain rate (5.5∙10-4 s -1 ). For 0°/90° non-crimp fabrics, the first inter-fiber cracks occur at 380 MPa (strain 0.8 %). Prior to failure at about 760 MPa (strain 2.0 %), we observe the evolution of nearly equidistant (1 mm distance) cracks running across the entire sample in the fully damaged state. KW - X-ray refraction KW - Diffraction Enhanced Imaging KW - Carbon Fiber Reinforced Plastics KW - In situ tensile test KW - Crack evolution PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-515060 DO - https://doi.org/10.1088/1757-899X/942/1/012035 SN - 1757-8981 SN - 1757-899X VL - 942 SP - 012035-1 EP - 012035-9 PB - IOP publishing CY - Bristol, UK AN - OPUS4-51506 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bruno, Giovanni T1 - Brittle Materials in Mechanical Extremes N2 - The goal of the Special Issue “Brittle Materials in Mechanical Extremes” was to spark a discussion of the analogies and the differences between different brittle materials, such as, for instance, ceramics and concrete. Indeed, the contributions to the Issue spanned from construction materials (asphalt and concrete) to structural ceramics, reaching as far as ice. The data shown in the issue were obtained by advanced microstructural techniques (microscopy, 3D imaging, etc.) and linked to mechanical properties (and their changes as a function of aging, composition, etc.). The description of the mechanical behavior of brittle materials under operational loads, for instance, concrete and ceramics under very high temperatures, offered an unconventional viewpoint on the behavior of brittle materials. This is not at all exhaustive, but a way to pave the road for intriguing and enriching comparisons. KW - Microcracking KW - Ceramics KW - Concrete KW - Asphalt KW - Mechanicalproperties KW - Microstructure KW - Strength PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-514558 DO - https://doi.org/10.3390/ma13204610 VL - 13 IS - 20 SP - 4610 PB - MDPI CY - Basel AN - OPUS4-51455 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Markötter, Henning A1 - Müller, Bernd R. A1 - Kupsch, Andreas A1 - Evsevleev, Sergei A1 - Arlt, T. A1 - Ulbricht, Alexander A1 - Dayani, Shahabeddin A1 - Bruno, Giovanni T1 - A Review of X-Ray Imaging at the BAMline (BESSY II) N2 - The hard X-ray beamline BAMline at BESSY II (Berlin, Germany) has now been in service for 20 years. Several improvements have been implemented in this time, and this review provides an overview of the imaging methods available at the BAMline. Besides classic full-field synchrotron X-ray computed tomography (SXCT), also absorption edge CT, synchrotron X-ray refraction radiography (SXRR), and synchrotron X-ray refraction tomography (SXRCT) are used for imaging. Moreover, virtually any of those techniques are currently coupled in situ or operando with ancillary equipment such as load rigs, furnaces, or potentiostats. Each of the available techniques is explained and both the current and the potential usage are described with corresponding examples. The potential use is manifold, the examples cover organic materials, composite materials, energy-related materials, biological samples, and materials related to additive manufacturing. The article includes published examples as well as some unpublished applications. KW - Material science KW - Radiography KW - Refraction KW - Tomography KW - X-ray imaging PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-572417 DO - https://doi.org/10.1002/adem.202201034 SN - 1438-1656 SP - 1 EP - 22 PB - Wiley VHC-Verlag AN - OPUS4-57241 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mouiya, M. A1 - Martynyuk, M. A1 - Kupsch, Andreas A1 - Laquai, R. A1 - Müller, Bernd R. A1 - Doyen, N.T. A1 - Tamraoui, Y. A1 - Serrano-Munoz, Itziar A1 - Huger, M. A1 - Kachanov, M. A1 - Bruno, Giovanni T1 - The stress–strain behavior of refractory microcracked aluminum titanate: The effect of zigzag microcracks and its modeling N2 - The stress–strain behavior of ceramics, such as aluminum titanate, has certain features that are unusual for brittle materials—in particular, a substantial nonlinearity under uniaxial tension, and load–unload hysteresis caused by the sharp increase of the incremental stiffness at the beginning of unloading. These features are observed experimentally and are attributed to microcracking. Here we compare different degrees of stress–strain nonlinearity of aluminum titanate materials and quantitatively model them. We use advanced mechanical testing to observe the mechanical response at room and high temperature; electron microscopy, and X-ray refraction radiography to observe the microstructural changes. Experiments show that two types of microcracks can be distinguished: (i) microcracks induced by cooling from the sintering temperature (due to heterogeneity and anisotropy of thermal expansion), with typical sizes of the order of grain size, and (ii) much larger microcracks generated by the mechanical loading. The two microcrack types produce different effects on the stress–strain curves. Such microcracks and the features of the stress–strain behavior depend on the density of the cooling-induced microcracks and on the distribution of grain sizes. They are modeled analytically and numerically. KW - Hystersis KW - Nonlinear stress-strain curve KW - Refractory KW - Stiffness KW - X-ray refraction PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-580517 DO - https://doi.org/10.1111/jace.19325 SN - 1551-2916 VL - 106 SP - 6995 EP - 7008 PB - Wiley-Blackwell CY - Oxford [u.a.] AN - OPUS4-58051 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nadammal, Naresh A1 - Mishurova, Tatiana A1 - Fritsch, Tobias A1 - Serrano-Munoz, Itziar A1 - Kromm, Arne A1 - Haberland, C. A1 - Portella, Pedro Dolabella A1 - Bruno, Giovanni T1 - Critical role of scan strategies on the development of microstructure, texture, and residual stresses during laser powder bed fusion additive manufacturing N2 - Laser based powder bed fusion additive manufacturing offers the flexibility to incorporate standard and userdefined scan strategies in a layer or in between the layers for the customized fabrication of metallic components. In the present study, four different scan strategies and their impact on the development of microstructure, texture, and residual stresses in laser powder bed fusion additive manufacturing of a nickel-based superalloy Inconel 718 was investigated. Light microscopy, scanning electron microscopy combined with electron backscatter diffraction, and neutron diffraction were used as the characterization tools. Strong textures with epitaxially grown columnar grains were observed along the build direction for the two individual scan strategies. Patterns depicting the respective scan strategies were visible in the build plane, which dictated the microstructure development in the other planes. An alternating strategy combining the individual strategies in the successive layers and a 67◦ rotational strategy weakened the texture by forming finer microstructural features. Von Mises equivalent stress plots revealed lower stress values and gradients, which translates as lower distortions for the alternating and rotational strategies. Overall results confirmed the scope for manipulating the microstructure, texture, and residual stresses during laser powder bed fusion additive manufacturing by effectively controlling the scan strategies. KW - Additive manufacturing KW - Laser powder bed fusion KW - Nickel-based superalloys KW - Scan strategies KW - Residual stresses KW - Microstructure and texture PY - 2021 DO - https://doi.org/10.1016/j.addma.2020.101792 VL - 38 SP - 1792 PB - Elsevier B.V. AN - OPUS4-51944 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Isaac, Augusta A1 - Serrano‐Munoz, Itziar A1 - Kostka, Aleksander A1 - Widjaja, Martinus Putra A1 - González‐Doncel, Gaspar A1 - Bruno, Giovanni A1 - Fernández, Ricardo T1 - Subgrain and Cavity Development during Creep of Al‐3.85%Mg N2 - It is classically considered that the creep mechanisms for type M (e.g., pure Al) and type A alloys (e.g., Al–Mg alloys) are different. In previous studies, it is predicated that fractal dislocation structures build up during creep can unify the creep behavior of pure Al and Al–Mg alloys. So far, good agreement between model and experimental data for pure Al is obtained. In this work, an Al‐3.85%Mg material crept at different strain levels (6%, 12%, 24%, and 35%) is analyzed by means of electron channelling contrast imaging. The formation of subgrains is observed at very large deformations (35%). Further examinations at 35% deformation, using electron backscatter diffraction, indicate that the subgrains and cavities tend to localize at regions where high intergranular stress mismatch is expected to occur. Laboratory X‐ray computed tomography is used to analyze the evolution of cavities between 12% and 24% stages, indicating that the fractal dimension of the cavities smaller than 100 μm varies with creep strain, as a reflection of the evolution of dislocation distribution. It is explained how the present data feed the model of the creep behavior of Al‐3.85%Mg. KW - Al–Mg alloys KW - Creep KW - Dislocations KW - Fractal KW - Intergranular residual stress KW - Subgrains PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-645905 DO - https://doi.org/10.1002/adem.202500263 SN - 1438-1656 SP - 1 EP - 10 PB - Wiley VHC-Verlag AN - OPUS4-64590 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pohl, P. A1 - Kümmel, F. A1 - Schunk, C. A1 - Serrano-Munoz, Itziar A1 - Markötter, Henning A1 - Göken, M. A1 - Höppel, H. W. T1 - About the Role of Interfaces on the Fatigue Crack Propagation in Laminated Metallic Composites N2 - The influence of gradients in hardness and elastic properties at interfaces of dissimilar materials in laminated metallic composites (LMCs) on fatigue crack propagation is investigated experimentally for three different LMC systems: Al/Al-LMCs with dissimilar yield stress and Al/Steel-LMCs as well as Al/Ti/Steel-LMCs with dissimilar yield stress and Young’s modulus, respectively. The damage tolerant fatigue behavior in Al/Al-LMCs with an alternating layer structure is enhanced significantly compared to constituent monolithic materials. The prevalent toughening mechanisms at the interfaces are identified by microscopical methods and synchrotron X-ray computed tomography. For the soft/hard transition, crack deflection mechanisms at the vicinity of the interface are observed, whereas crack bifurcation mechanisms can be seen for the hard/soft transition. The crack propagation in Al/Steel-LMCs was studied conducting in-situ scanning electron microscope (SEM) experiments in the respective low cycle fatigue (LCF) and high cycle fatigue (HCF) regimes of the laminate. The enhanced resistance against crack propagation in the LCF regime is attributed to the prevalent stress redistribution, crack deflection, and crack bridging mechanisms. The fatigue properties of different Al/Ti/Steel-LMC systems show the potential of LMCs in terms of an appropriate selection of constituents in combination with an optimized architecture. The results are also discussed under the aspect of tailored lightweight applications subjected to cyclic loading. KW - Laminated metallic composites KW - Toughening mechanisms KW - Interfaces KW - Fatigue crack propagation KW - Fatigue crack growth PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-526531 DO - https://doi.org/10.3390/ma14102564 VL - 14 IS - 10 SP - 2564 PB - MDPI AN - OPUS4-52653 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bruson, Danilo A1 - Serrano-Munoz, Itziar A1 - Fritsch, Tobias A1 - Markötter, Henning A1 - Galati, Manuela T1 - Revealing the (positive) role of porosity within polymeric additively manufactured lattices via X-ray computed tomography N2 - The mechanical properties of lattice geometries are known to be significantly influenced by a variety of manufacturing defects. This study investigates the influence of porosity on the mechanical behaviour of strut-based body-centred cubic (BCC) lattice structures produced with powder bed fusion with laser beam PBF-LB/P using PA2200 nylon powder. The study combines advanced techniques, including in-situ laboratory X-ray computed tomography (XCT), synchrotron XCT to visualise pores and roughness in high resolution at a single-cell level and image-based finite element analysis (FEA). The findings show that failure in thin-walled AM lattices is governed by the combined effects of porosity morphology, location, surface roughness, and cross-section reduction. The presence of internal porosity is found to attenuate both the amplitude of elastic modulus fluctuations and the severity of stress concentrations induced by surface irregularities. KW - Nylon Pa2200 KW - Laser powder bed fusion (PBF-LB) KW - Processing defects KW - Synchrotron X-ray computed tomography (XCT) KW - Digital volume correlation (DVC) KW - Image-based finite element simulations PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-633245 DO - https://doi.org/10.1016/j.ijsolstr.2025.113488 SN - 0020-7683 VL - 320 SP - 1 EP - 16 PB - Elsevier B.V. AN - OPUS4-63324 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Buljak, Vladimir A1 - Serrano-Munoz, Itziar A1 - Kupsch, Andreas A1 - Müller, Bernd R. A1 - Prasek, Marko A1 - Contillo, Adriano A1 - Mouiya, Mossaab A1 - Huger, Marc A1 - Bruno, Giovanni T1 - On the closure of thermally induced micro-cracks in aluminum titanate ceramics N2 - Aluminum Titanate (AT) refractory ceramics (as some other ceramic composites) are prone to microcracking, due to the thermal expansion anisotropy of AT and to the mismatch with the thermal expansion of the constituents. Such microcracks cause the room temperature Young's modulus to be only a fraction of that of the non-microcracked material. As a function of temperature, the Young's modulus increases non-linearly. Such increase suggests that microcracks close or even heal at high temperatures. Upon cooling, thermal stress accumulates again, and microcracks re-open. This cycle is fully reversible. While confirming the hysteretic behavior of the Young's modulus, we observe that the amount of microcracks (as determined by in-situ Synchrotron X-ray refraction radiography) decreases linearly upon heating. The apparent mismatch between the Young's modulus and the microcrack content dependence on temperature is explained by a simple FEM model. Such model employs cohesive elements upon cooling, in order to estimate the amount of initial microcracks. On purpose, the model does not include healing upon heating and only allows crack closure. It predicts that crack closure continuously occurs upon heating, thereby qualitatively reproducing the nearly linear dependence of the X-ray refraction signal. It is therefore concluded that the sudden and non-linear increase of Young's modulus with temperature is mainly caused by crack healing. Such finding agrees with previous work and paves the road to a more systematic separation of crack closure and healing in flexible ceramics. KW - X-ray computed tomography KW - X-ray refraction radiography KW - In-situ imaging KW - BAMline KW - Micromechanics KW - BESSY II PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-645082 DO - https://doi.org/10.1016/j.ceramint.2025.09.237 SN - 0272-8842 VL - 51 IS - 27 SP - 55141 EP - 55152 PB - Elsevier CY - Amsterdam AN - OPUS4-64508 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -