TY - CONF A1 - Rolle, Annette A1 - Komann, Steffen A1 - Wille, Frank ED - Baraldi, P. ED - Di Maio, F. ED - Zio, E. T1 - Ageing aspect in the safety evaluation of special form radioactive material N2 - In accordance with the IAEA transport regulations Special Form Radioactive Material (SFRM) is either an indispersible solid radioactive material or a sealed capsule containing radioactive material. The design of special form radioactive material has to resist a severe transport accident without undue loss or dispersal of radioactive material. The safety assessment for design approval shall include besides the required test program (impact, percussion, bending and heat test) also the evaluation of the management system for design, manufacture, testing, documentation, use, maintenance and inspection. The specified quality assurance measures have to assure, that every specimen of the approved design is produced in the same verified quality and every specimen must be able to survive the severe mechanical and thermal tests at any time of its working life. Due to the long-term use of SFRM the consideration of ageing is an important aspect in the approval procedure by BAM, the competent authority for SFRM approval in Germany. Different fields of application imply a wide range of environmental conditions, from clean room atmosphere to highly aggressive industrial conditions. So, besides of radioactive content, corrosion is a main factor for possible design degradation. This paper will describe major influencing factors to be taken into account to assess the ageing behavior of a SFRM design and will emphasize that there is a need for a regulatory specification of a SFRM-working life as basis for the aging evaluations. T2 - 30th European Safety and Reliability Conference and 15th Probabilistic Safety Assessment and Management Conference (ESREL2020 PSAM15) CY - Online meeting DA - 01.11.2020 KW - Special form radioactive material KW - Transport KW - Ageing KW - Material KW - Safety assessment KW - Management system PY - 2020 UR - https://www.rpsonline.com.sg/proceedings/esrel2020/html/3659.xml SN - 987-981-14-8593-0 SP - Paper 3659,1 EP - 5 PB - Research Publishing CY - Singapore AN - OPUS4-50969 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - von Werder, Julia A1 - Gardei, André A1 - Hoppe, Johannes A1 - Meng, Birgit ED - Littmann, K. T1 - Funktionalisierung von Fasern für zementgebundene Materialien - ausgewählte Prüfmethoden N2 - Die geringe Zugfestigkeit von zementgebundenen Materialien kann durch die Zugabe von Fasern maßgeblich verbessert werden. Ziel eines gemeinsamen Verbundprojekts mit einem Industriepartner war die Erhöhung der Leistungsfähigkeit von kurzen Polymer- und Carbonfasern durch eine Verbesserung des Verbundes zwischen Faseroberfläche und Zementsteinmatrix. Von der IONYS AG wurde dazu eine spezielle Funktionalisierung entwickelt, die über eine Hydrophilisierung der Faseroberfläche eine chemische Anbindung an die Zementsteinmatrix gewährleistet. Aufgabe der BAM war es, die Effizienz der neuen Beschichtung bezüglich der Erhöhung der Nachrissbiegezugfestigkeit und der Reduzierung der Schwindrissbildung während der Erhärtungsphase zu quantifizieren. Die Ergebnisse zeigen, dass die Funktionalisierung die Neigung zur Schwindrissbildung für die Carbonfasern und in noch stärkerem Maße für die Polymerfasern reduziert. Eine Erhöhung der Nachrissbiegezugfestigkeit konnte dagegen nur für die deutlich steiferen Carbonfasern nachgewiesen werden. T2 - 10. Kolloquium Industrieböden CY - Esslingen, Germany DA - 03.03.2020 KW - Fibres KW - Cementitious materials KW - Shrinkage KW - Strain hardening PY - 2020 SN - 978-3-8169-3505-6 SP - 173 EP - 178 PB - expert Verlag GmbH CY - Tübingen AN - OPUS4-51915 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - von Werder, Julia A1 - Fontana, P. A1 - Hoppe, Johannes A1 - Bilgin, S. A1 - Meng, Birgit ED - Serrat, C. ED - Casas, J. R. ED - Gibert, V. T1 - Composite Facade Elements with Self-Cleaning Surface made of Ultra-High-Performance Concrete (UHPC) N2 - In the framework of the European project H-House various concrete façade elements were developed with the aim to ensure a long service life by combining a very durable material with self-cleaning properties. The façade elements presented are made of a shell of UHPC filled with blocks of aerated autoclaved concrete as insulating material. Self-cleaning properties were realized amongst others by imprinting a microstructure into the surface during casting. The paper focuses on selected technological aspects of the manufacturing process of prototypes which had to be performed in two concreting sections. Furthermore the challenges faced when upscaling the self-cleaning properties are addressed and the strategy to assess the self-cleaning properties by measuring the contact and the roll-off angel is presented. The results show that a successfull upscalaing process requires detailed planning and that the best results can often be achieved with a moderate work effort or material use. T2 - XV International Conference on Durability of Building Materials and Components (DBMC 2020) CY - Online meeting DA - 20.10.2020 KW - Ultra-High-Performance Concrete KW - Facade Elements KW - Self-Cleaning Properties KW - Adhesive Pull-Strength KW - Microstructure KW - Architectural Concrete PY - 2020 SN - 978-84-121101-8-0 SP - 1289 EP - 1297 PB - International Center for Numerical Methods in Engineering (CIMNE) CY - Spain AN - OPUS4-51967 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wachtendorf, Volker A1 - Schartel, Bernhard A1 - Lin, Xuebao A1 - Tan, Yi A1 - Schoch, R. A1 - Lang, M. A1 - Tröppner, O. A1 - Bosse, M. ED - Ziegahn, K.-F. T1 - Untersuchung der Witterungsbeständigkeit komplexer Funktionalitäten von Polymerwerkstoffen durch künstliche Bewitterung: Flammschutz N2 - In den letzten Jahrzehnten wurde die Degradation der polymeren Matrix von flammgeschützten Polymeren eingehend untersucht. Erst in den letzten Jahren jedoch hat sich die Frage der Lebensdauer der Funktionalität des Flammschutzes selbst als wichtige Fragestellung herauskristallisiert, z.B. bei Kabeln. Deshalb sollte diese Fragestellung durch systematisch-variierte künstliche Klima- und Bewitterungstests an flammgeschützten Polymerwerkstoffen untersucht werden. T2 - 50. Jahrestagung der Gesellschaft für Umweltsimulation (GUS) CY - Online meeting DA - 23.03.2022 KW - Flammschutz, Witterungsbeständigkeit, Langzeitbeständigkeit, UV, E&E PY - 2022 SN - 978-3-9818507-7-2 VL - 50 SP - 143 EP - 148 CY - Pfinztal (Berghausen) AN - OPUS4-54543 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zhu, Jiangchao A1 - Schurig, M. A1 - Schlums, H. A1 - Madia, Mauro A1 - Zerbst, Uwe T1 - Bruchmechanische Bewertung der Integrität einer Turbinenscheibe bei Überdrehzahl N2 - Turbinenscheiben sind thermisch und mechanisch hochbeanspruchte, sicherheitsrelevante Komponenten in Gasturbinen. Ihre Integrität wird in Bauteiltests unter Überdrehzahlbedingungen nachgewiesen. Kontext des Aufsatzes ist die Erarbeitung einer zusätzlichen Bewertungsebene auf der Grundlage von Versuchen unter monotoner Beanspruchung, die die Beanspruchung im Bauteil realistisch wiedergeben soll. Betrachtet wird ein halbelliptischer Riss, der bei der weiteren Ausbreitung als Umfangsriss wächst (rim peeling). Die Simulation dieser Stelle im Bauteil schließt die mechanische und thermische Beanspruchung sowie sie Dehnungsbehinderung ein. Letztere wird anhand zweier Parameter, der Spannungsmehrachsigkeit ℎ und des (allerdings modifizierten) Constraint-Parameters nach Newman, der die Spannungen über den plastisch verformten Bereich mittelt, bestimmt. Erwartungsgemäß zeigt sich, dass die höchste Dehnungsbehinderung weder an den Oberflächenpunkten, noch an den tiefsten Punkten, sondern an einer Stelle zwischen beiden auf der Rissfront auftritt. Als Versuchsgeometrie für die monotonen Tests soll eine Kreuzprobe mit wanddurchdringenden Rissen ausgehend von einer Innenbohrung dienen. Durch geeignete Wahl der Risstiefe sowie der in beiden Richtungen angreifenden Kräfte gelingt es, bauteiladäquate Zustände zu erzeugen. T2 - 54. Tagung des DVM-Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Online meeting DA - 22.02.2022 KW - Bruchmechanik KW - Struktur Integrität KW - Turbinenscheibe KW - Constraint PY - 2022 SP - 13 EP - 22 AN - OPUS4-54403 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erning, Johann Wilhelm T1 - “Grabenkorrosion": How scientific debate leads to an solution. and modern failures due to neglection of well described facts N2 - In the late 1980s, a new type of corrosion appeared in drinking water installations where galvanized steel pipes failed forming a deep groove with no corrosion at the other surfaces. The reason was discussed quite fiercely between failure analysts and material suppliers. In the end the discussion lead to the solution: inductive welded pipes of a certain sulphur content were prone to selective corrosion. The history of the arguments is discussed using old communications between Wilhelm Schwenk and Wolfgang Stichel, who later published the results in a paper unfortunately only I german. Thus the knowledge got lost and new cases based on the same material problems are observed in application of so-called C-Steel piping systems. Failure cases are shown. T2 - MTech 2023 CY - Cavtat, Croatia DA - 02.10.2023 KW - Corrosion KW - Grabenkorrosion PY - 2023 SN - 2806-8769 SP - 1 EP - 6 PB - Croatian Society for Heat Treatment and Sufrace Engineering CY - Zagreb AN - OPUS4-58521 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schultheiß, Annika L. A1 - Kruschwitz, Sabine A1 - Wilsch, Gerd A1 - Bogner, Andreas A1 - Patel, Ravi T1 - Lessons learnt on quantiative spatial chloride analysis using libs and µXRF N2 - Understanding chloride ingress is crucial in the context of the durability of concrete structures against corrosion. Techniques such as Laser-Induced Breakdown Spectroscopy (LIBS) and Micro X‑ray Fluorescence (µXRF) can provide a 2D representation of chloride ingress. However, obtaining quantitative data from such techniques is not a trivial task. In this study, we focus on factors such as sample preparation, measurement settings, calibration strategy, and post-processing of results which directly affect the outcome of the experiments but are rarely discussed in the literature. T2 - Rilem Annual Week 2024 CY - Toulouse, Frankreich DA - 25.08.2024 KW - Durability KW - Chloride ingress KW - LIBS KW - µXRF KW - Nondestructive testing KW - Imaging PY - 2024 SP - 1 EP - 9 AN - OPUS4-61664 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Duarte, Larissa A1 - Madia, Mauro A1 - Kanna, Naveen A1 - Bär, Jürgen ED - Ricoeur, Andreas T1 - Anwendung der zyklischen R-Kurven-Analyse zur Abschätzung des Kitagawa-Takahashi-Diagramms N2 - Die ausgeprägte Langzeitfestigkeit eines Werkstoffes entspricht der maximalen Spannung, unterhalb derer alle ursprünglich wachstumsfähigen Mikrorisse arretieren. Für fehlerbehaftete Werkstoffe stellt das Kitagawa-Takahashi (KT)-Diagramm die Abhängigkeit der ausgeprägten Langzeitfestigkeit von der Defektgröße dar. Das KT-Diagramm kann mit großem Aufwand experimentell bestimmt oder durch verschiedene Modelle abgeschätzt werden. Solche Ansätze ergeben oft nichtkonservative Prognosen und berücksichtigen weder den Aufbau der Rissschließeffekte noch lokale Spannungen. In dieser Arbeit wird ein Kurzrissmodell auf Grundlage der zyklischen R-Kurve und des Rissarrestphänomens zur Abschätzung des KT-Diagramms vorgestellt. Die Abschätzungen werden mit experimentellen Daten validiert, die mit gekerbten Proben nach dem Treppenstufenverfahren ermittelt wurden. T2 - 57. Tagung des DVM-Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Köln, Germany DA - 18.02.2025 KW - Langzeitfestigkeit KW - KT-Diagramm KW - zyklische R-Kurven-Analyse PY - 2025 DO - https://doi.org/10.48447/BR-2025-512 VL - 257 SP - 93 EP - 104 PB - Deutscher Verband für Materialforschung und -prüfung e.V. CY - Berlin, Deutschland AN - OPUS4-62603 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Genga, R. M. A1 - Glaser, D. A1 - Rokebrand, P. A1 - Cornish, L. A. A1 - Woydt, M. A1 - Gradt, Thomas A1 - Janse van Vuuren, A. A1 - Polese, C. ED - von Leipzig, K. ED - Sacks, N. ED - McClelland, M. T1 - Laser shock peening: A NbC based cermet enhancement alternative for improved GCI interrupted face-milling N2 - Attempts were made to improve the properties and machining performance of NbC based cermet cutting inserts for face milling of grey cast iron (GCI) (BS 1452/GG35) by spark plasma sintering (SPS), use of sub-stoichiometric NbC (NbC₀ˏ₈₈), Cr₃C₂ and Mo₂C additives and laser shock peening (LSP). The microstructure, hardness, fracture toughness and Young’s modulus of WC–Co, NbC₀ˏ₈₈-Co and NbC₀ˏ₈₈-Ni cermet-based inserts were investigated for machining performance. Additions of Mo₂C and manufacture by SPS significantly refined the NbC₀ˏ₈₈-Ni/Co cermet’s carbide grain size from ~5.0 μm to <0.9 μm, which increased the hardness (by ~4GPa) and wear resistance. Laser shock peening (LSP) improved the fracture toughness of all the inserts, from 10% (in the SPS WC based in cermets) to ~100% (in the LPS NbC based cermets). Uncoated cutting inserts were manufactured from the sintered cermets in an SNMA (double sided square insert without a chipformer on the cutting edge) shape (12.7 × 12.7 × 4.3 mm³, 1.6 mm nose radius). The inserts were used for interrupted face-milling of GCI at cutting speeds (ν˛) ranging from 100 m/minute (400 rpm)–500 m/minute (2000 rpm) and depths of cut (ɑₚ) of 0.2–1.0 mm. The insert wear was measured after every pass and analyzed by annular dark field scanning transmission electron microscopy (ADF-STEM). Cutting temperatures were measured with a high-speed thermal camera and forces were measured using a Kistler dynamometer. During machining at ν˛ = 200 m/minute and ɑₚ = 1.0 mm, WC–Co inserts had the lowest flank wear rate (FWR), although LSP significantly improved the tool life of the NbC₀ˏ₈₈-Ni inserts, significantly reducing the FWR from 148.63 μm/minute to 99.79 μm/minute (by ~33%) and the average resultant force from 1257 ± 15 N to 535 ± 15 N. During machining at ν˛ = 500 m/minute and ɑₚ = 0.2 mm, LSP significantly lowered the FWRs of the NbC₀ˏ₈₈ inserts, giving better tool life than all the WC based inserts. Generally, LSP improved the NbC₀ˏ₈₈ inserts’ tool life, reducing the flank wear rate by up to 33% during roughing and 63% during finishing. T2 - 8th International Conference on Competitive Manufacturing (COMA ’22) CY - Stellenbosch, South Africa DA - 09.03.2022 KW - Niobium carbide KW - Laser shock peening KW - Face milling KW - Tool wear PY - 2023 SN - 978-3-031-15602-1 SN - 978-3-031-15601-4 SN - 978-3-031-15604-5 DO - https://doi.org/10.1007/978-3-031-15602-1_62 SN - 2194-0525 SN - 2194-0533 N1 - Serientitel: Lecture notes in production engineering – Series title: Lecture notes in production engineering SP - 871 EP - 889 PB - Springer CY - Cham AN - OPUS4-62689 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geburtig, Anja A1 - Wachtendorf, Volker A1 - Trubiroha, P. T1 - Simulationsdaten zur photooxidativen Beanspruchung an verschiedenen geografischen Freibewitterungs-Standorten N2 - Freibewitterungen weisen grundsätzlich eine hohe Variabilität der jeweiligen Intensität der Beanspruchungsparameter auf; sie sind nicht einfach wiederholbar. Um dennoch die Ergebnisse einer Beanspruchung vergleichen zu können, ist eine aussagekräftige Charakterisierung der Freibewitterung wichtig. Traditionell werden Daten bekannter Einflussgrößen wie Globalstrahlung, Temperatur oder Feuchtewerte herangezogen. Obwohl man weiß, dass diese Größen an den exponierten Oberflächen wechselwirken und kombiniert als Mikroklima Einfluss auf Degradationsprozesse nehmen, werden schon aus Praktikabilitätsgründen diese separat als klimatische Messgrößen angegeben. Die Aussagekraft dieser Daten ist mäßig. Ziel dieses Beitrags ist es, die Aussagekraft und damit Vergleichbarkeit zu erhöhen, indem diese Messdaten als Stundendaten zu Wirkintegralen vorverarbeitet und jahresweise akkumuliert werden. Betrachtet wird dafür der Prozess der Photooxidation, da dieser Alterungs-mechanismus bei allen Kunststoffen auftritt. Für eine einfache Modellierung wird die wirksame UV-Bestrahlung, gewichtet mit einer Arrhenius-abhängigen Ober¬flächen-temperatur (TOF), über den Beanspruchungszeitraum von hier je einem Jahr akkumuliert. Die Idee einer solchen Messgröße für photooxidative Ober¬flächen¬alterung wurde bereits vorgestellt [1]. Dort wurde ein Gerät vor¬geschlagen, mit dem dieser Wert für verschieden absorbierende Oberflächen für die Dauer einer Exposition akkumuliert wird, und ergänzend eine Abschätzung der Betauungs¬zeiten dieser Referenz-Oberflächen erfolgen könnte. Hier soll es um eine rechnerisch generierte Zusammenstellung dieser photo¬oxidativen 1-Jahres-Alterungswerte für verschiedene Standorte gehen. Ein Temperaturfaktor erfasst dabei den Einfluss der Strahlungserwärmung auf eine weiße, graue bzw. schwarze Referenzoberflächen, spiegelt also die Kopplung von solarer Strahlung und Temperatur wider [1]. Ermittelt wird er aus Stunden¬daten der Globalstrahlung und der Lufttemperatur. Die spektrale Wirkung wird aus Sonnenhöhenständen entsprechend der geografischen Breite mit Hilfe der FastRT-Oberfläche [2] als PiT·h-Wert abgeschätzt [3]. Anhand der errechneten Jahreswerte können die Schweregrade der photo¬oxidativen Beanspruchung an den verschiedenen Standorten unmittelbar verglichen werden. Die gezeigten Simulationsdaten für ein solches „elektronisches Referenzmaterial“ für photooxidative Degradation zeigen die prinzipielle Möglichkeit einer Kartografierung solcher Daten auf. T2 - 53. Jahrestagung der GUS CY - Stutensee-Blankenloch, Germany DA - 26.03.2025 KW - Polymer 3R, UV, Bestrahlung, Bewitterung PY - 2025 SN - 978-3-9826129-2-8 VL - 53 SP - 19 EP - 28 PB - Gesellschaft für Umweltsimulation e.V. CY - 76327 Pfinztal (Berghausen) AN - OPUS4-62902 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erning, Johann Wilhelm T1 - Sprechen wir über Korrosion - aber richtig! N2 - Die Korrosion in ihren zahlreichen Erscheinungsformen beschäftigt Fachleute und Laien. Um-so wichtiger ist es, die einzelnen Phänomene korrekt und eindeutig zu benennen. Nur so kann man eine saubere Beschreibung der Korrosionsvorgänge erreichen und damit in der wörtlichen und schriftlichen Kommunikation richtig verstanden werden. An zahlreichen Beispielen wird der richtige und normgemäße Sprachgebrauch beschrieben. T2 - Korrosionsschutz in der maritimen Technik CY - Hamburg, Germany DA - 29.01.2020 KW - Korrosion KW - Nomenklatur PY - 2020 SN - 978-3-935406-72-7 SP - 7 EP - 11 AN - OPUS4-50327 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kempf, A. A1 - Hilgenberg, Kai T1 - Einfluss der Porosität auf die Duktilitätseigenschaften von additiv gefertigtem AlSi10Mg N2 - Die Werkstoffeigenschaften im selektiven Laserstrahlschmelz-Verfahren hergestellter Bauteile werden von einer Vielzahl technologischer Parameter beeinflusst, sodass sich die Fertigungsgüte verschiedener Anlagen voneinander unterscheiden kann. Vor diesem Hintergrund wurde in der vorliegenden Arbeit untersucht, inwiefern sich durch verschiedene nachgelagerte Wärmebehandlungen die Mikrostruktur und die quasistatischen Festigkeitseigenschaften von Proben aus der Aluminiumlegierung AlSi10Mg, die mit verschiedenen Anlagen, Pulvern, Belichtungsstrategien und Prozessparametern gefertigt wurden, harmonisieren lassen. Die Versuche zeigten u.a., dass die erheblichen Festigkeitsunterschiede im Ausgangszustand unabhängig von der angewendeten Wärmebehandlungsroute aufgehoben wurden. Dennoch wurden signifikante Unterschiede in der Duktilität ermittelt. Anhand umfangreicher Bruchflächenanalysen konnte nachgewiesen werden, dass die in der Bruchfläche ermittelte Porosität eine lineare Korrelation zu der Bruchdehnung aufwies. T2 - 5. Tagung des Arbeitskreises Additiv gefertigte Bauteile und Strukturen CY - Online Meeting DA - 04.11.2020 KW - Wärmebehandlung KW - Additive Fertigung KW - Laser powder bed fusion KW - AlSi10Mg KW - Ringversuch PY - 2020 SN - 2509-8772 VL - 405 SP - 93 EP - 104 AN - OPUS4-51657 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hofmann, Detlef A1 - Basedau, Frank A1 - Heidenreich, F. A1 - Herten, M. T1 - Verwendung faseroptischer Messtechnik im Zuge wiederholter Eignungsprüfungen an Verpressankern N2 - Im Rahmen des Ausbaus des Dortmund-Ems-Kanals wurden an der Schleuse Gleesen Forschungsanker installiert, die Rückschlüsse auf das Tragverhalten in Folge des chemischen Angriffs kalklösender Kohlensäure geben sollen. Die Forschungsanker werden seit der Erstellung im Jahr 2017 mit verteilter faseroptischer Sensorik während der jährlichen Eignungsprüfungen untersucht. Die Ergebnisse der Jahre 2017 bis 2019 werden im Folgenden dargestellt. T2 - Messen in der Geotechnik 2020 CY - Braunschweig, Germany DA - 20.02.2020 KW - Faseroptische Sensorik KW - Rayleigh Rückstreuung KW - Verpressanker KW - Chemischer Angriff KW - Rissbildung PY - 2020 SN - 978-3-948141-02-8 DO - https://doi.org/10.24355/dbbs.084-201912181435-0 IS - 110 SP - 297 EP - 323 AN - OPUS4-51687 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Duarte, Larissa A1 - Zerbst, Uwe A1 - Madia, Mauro T1 - Vergleichende Untersuchungen zum intrinsischen Schwellenwert der da/dN-ΔK-Kurve N2 - Für die Bestimmung der Restlebensdauer zyklisch beanspruchter Bauteile kommt dem Schwellenwert für Ermüdungsrissausbreitung, Δ𝐾𝑡ℎ, und dem sich anschließenden Schwellenwertbereich der 𝑑𝑎𝑑𝑁⁄−Δ𝐾-Kurve große Bedeutung zu. Dem stehen Unsicherheiten bei der Bestimmung und Analyse gegenüber. Der Aufsatz befasst sich mit der Ermittlung des sogenannten intrinsischen Schwellenwerts, der als robuster Eingangsparameter für eine „rissschließfreie“ Analyse der Restlebensdauer von entscheidender Bedeutung ist. T2 - 53. Tagung des DVM-Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Online meeting DA - 18.02.2021 KW - Schadenstolerante Bauteilauslegung, Restlebensdauer, intrinsischer Schwellenwert gegen Ermüdungsrissausbreitung PY - 2021 SN - 2366-4797 SP - 211 EP - 220 PB - Deutscher Verband für Materialforschung und -prüfung e.V. (DVM) CY - Berlin AN - OPUS4-52704 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Duarte, Larissa A1 - Zerbst, Uwe A1 - Madia, Mauro T1 - Der Schwellenwert der da/dN-∆K-Kurve als Auslegungskriterium für die Bauteilbewertung N2 - Für die Bestimmung der Restlebensdauer zyklisch beanspruchter Bauteile kommt dem Schwellenwert für Ermüdungsrissausbreitung ∆Kth und dem sich anschließenden Schwellenwertbereich der da/dN-∆K-Kurve große Bedeutung zu. Dem stehen Unsicherheiten bei der Bestimmung und Analyse gegenüber. Der Aufsatz befasst sich mit der Ermittlung des sogenannten intrinsischen Schwellenwerts, der als robuster Eingangsparameter für eine „rissschließfreie“ Analyse der Restlebensdauer von entscheidender Bedeutung ist. T2 - Tagung Werkstoffprüfung 2020 CY - Online meeting DA - 03.12.2020 KW - Schadenstolerante Bauteilauslegung, KW - Intrinsischer Schwellenwert gegen Ermüdungsrissausbreitung KW - Restlebensdauer PY - 2020 DO - https://doi.org/10.48447/WP-2020-025 SP - 1 EP - 8 AN - OPUS4-52788 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Tian, H. A1 - Voigt, Marieke A1 - Lehmann, C. A1 - Meng, Birgit A1 - Stephan, D. ED - Middendorf, B. ED - Fehling, E. T1 - Composition and microstructure stability of cement compound under cyclic hydrothermal condition N2 - There have been many researches focused on the performance improvement of ultra-high performance concrete (UHPC) by autoclaving treatment. The goal of autoclaving is to increase the pozzolanic reaction, and to densify the cement stone and the transition zone which originates from the incorporation of supplementary cementitious materials (SCMs), such as silica fume, fly ash and blast furnace slag. Due to the superior properties, UHPC can also be utilized under high mechanical load and aggressive condition, for example, the fabrication of water tanks for thermal storage which is of great significance for saving energy and reducing CO2 emission. It is known that mineral stability of the hydration products of an inorganic binder is highly related to the temperature and pressure of the environment. A certain stable composition at room temperature, however, may undergo a phase transformation at high temperature and the performance decrease under this severe condition will generally be more severe. In this way, the rationale behind this deterioration under long-term hydrothermal condition involving many cycles and long duration has to be clarified, and then appropriate optimizing methods will be performed in order to obtain a kind of construction with high durability under aggressive environment. For this purpose, different types and amounts of SCMs are introduced into the standard mixture of UHPC and the phase compositions after autoclaving at 200 °C and 15.5 bar are determined by combined X-ray diffraction and scanning electron microscope. Mercury intrusion porosimeter is used to characterise the microstructure of the samples. In order to establish the relationship between microstructure and macroscopic properties, compressive and flexural strength are also investigated. T2 - HiPerMat 2020 CY - Kassel, Germany DA - 11.03.2020 KW - Hydrothermal treatment KW - UHPC KW - Composition PY - 2020 SN - 978-3-7376-0828-2 VL - 23 SP - 87 EP - 88 PB - Kassel University Press CY - Kassel AN - OPUS4-52375 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wachtendorf, Volker A1 - Geburtig, Anja T1 - Digitale Umweltsimulation am Beispiel der Photooxidation von Polymeren N2 - Die Umweltwirkungen auf ein Material werden als Überlapp der Funktionskurven von Materialempfindlichkeit und einwirkenden Umweltparametern betrachtet. Wenn entweder die Empfindlichkeit oder die Beanspruchungen Null sind, ergibt sich auch keine Umweltwirkung und bei beidseitig Werten größer Null das jeweilige Produkt der beiden. Die Akkumulation der nicht-reversiblen Effekte über die Zeit und allen Eigenschaftsänderungen entspricht der Alterung des Materials für den jeweiligen Expositionszeitraum. Die digitale Umweltsimulation gliedert sich hier in drei Teilaspekte. Ein erster, rein materialwissenschaftlicher Teil hat die Aufgabe, alle relevanten Materialempfindlichkeiten experimentell zu quantifizieren. Ein zweiter – unter Umständen numerischer Teil – hat die Aufgabe, das Bauteil und seine Einbaulage zu digitalisieren und aus den makroskopischen Umgebungsbedingungen die relevanten mikroklimatischen Umweltparameter für alle Oberflächen- oder Volumenelemente zu bestimmen. In einem dritten Teil werden die Einwirkungen über den betrachteten Zeitraum berechnet und kumuliert. Dieses Konzept, das auf den so genannten Expositions-Reaktions-Funktionen (ERF) basiert, wird an Beispielen der Photoxidation erläutert. Dieses Vorgehen wurde schon beim ViPQuali-Projekt als Numerische Umweltsimulation umgesetzt. Überprüft werden muss das Modell unbedingt an einer realitätsnahen Validierungsbeanspruchung. Hier werden die ermittelten ERFs mit über den kompletten Beanspruchungszeitraum geloggten Umweltparametern gekoppelt, um die berechnete mit der experimentell erfahrenen Alterungswirkung zu vergleichen. Nur so kann sichergestellt sein, dass alle für die Anwendungsumgebung relevanten Materialempfindlichkeiten einbezogen wurden. T2 - 52. Jahrestagung der GUS CY - Stutensee-Blankenloch, Germany DA - 26.03.2024 KW - UV KW - Polymer 3R KW - Bewitterung KW - Bestrahlung PY - 2024 SN - 978-3-9826129-0-4 SP - 31 EP - 40 PB - Gesellschaft für Umweltsimulation e.V. CY - Pfinztal (Berghausen) AN - OPUS4-59830 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Yang, Fan A1 - Meng, Xiangmeng A1 - Bachmann, Marcel A1 - Artinov, Antoni A1 - Putra, Stephen Nugraha A1 - Rethmeier, Michael T1 - Numerical analysis of the influence of an auxiliary oscillating magnetic field on suppressing the porosity formation in deep penetration laser beam alloys of aluminum alloys N2 - The contactless magnetohydrodynamic technology has been considered as a potential and promising method to improve the weld qualities of deep penetration laser beam welding. In this paper, numerical investigations are conducted to study the influence of the auxiliary oscillating magnetic field on the porosity suppression in laser beam welding of 5754 aluminum alloy. To obtain a deeper insight into the suppression mechanism, a three-dimensional transient multi-physical model is developed to calculate the heat transfer, fluid flow, keyhole dynamic, and magnetohydrodynamics. A ray tracing algorithm is employed to calculate the laser energy distribution on the keyhole wall. A time-averaged downward Lorentz force is produced by an oscillating magnetic field. This force acts in the molten pool, leading to a dominant downward flow motion in the longitudinal section, which blocks the bubble migration from the keyhole tip to the rear part of the molten pool. Therefore, the possibility for the bubbles to be captured by the solidification front is reduced. The electromagnetic expulsive force provides an additional upward escaping speed for the bubbles of 1 m/s ~ 5 m/s in the lower and middle region of the molten pool. The simulation results are in a good agreement with experimental measurements. Based on the results obtained in this study, a better understanding of the underlying physics in laser beam welding enhanced by an auxiliary oscillating magnetic field can be provided and thus the welding process can be further optimized reducing the porosity formation. T2 - 13th International Seminar Numerical Analysis of Weldability CY - Seggau, Austria DA - 04.09.2022 KW - Deep penetration laser beam welding KW - Oscillating magnetic field KW - Numerical simulation KW - Porosity KW - Molten pool behaviour PY - 2023 SN - 2410-0544 VL - 13 SP - 237 EP - 254 PB - Verlag der Technischen Universität Graz AN - OPUS4-58804 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ratkovac, Mirjana A1 - Gerards-Wünsche, Paul A1 - Thiele, Marc A1 - Brackrock, Daniel A1 - Stamm, Michael T1 - Detection and monitoring of the fatigue crack growth on welds – Application-oriented use of NDT methods N2 - Early detection of fatigue cracks and accurate measurements of the crack growth play an important role in the maintenance and repair strategies of steel structures exposed to cyclic loads during their service life. Observation of welded connections is especially of high relevance due to their higher susceptibility to fatigue damage. The aim of this contribution was to monitor fatigue crack growth in thick welded specimens during fatigue tests as holistically as possible, by implementing multiple NDT methods simultaneously in order to record the crack initiation and propagation until the final fracture. In addition to well-known methods such as strain gauges, thermography, and ultrasound, the crack luminescence method developed at the Bundesanstalt für Materialforschung und -prüfung (BAM), which makes cracks on the surface particularly visible, was also used. For data acquisition, a first data fusion concept was developed and applied in order to synchronize the data of the different methods and to evaluate them to a large extent automatically. The resulting database can ultimately also be used to access, view, and analyze the experimental data for various NDT methods. During the conducted fatigue tests, the simultaneous measurements of the same cracking process enabled a comprehensive comparison of the methods, highlighting their individual strengths and limitations. More importantly, they showed how a synergetic combination of different NDT methods can be beneficial for implementation in large-scale fatigue testing but also in monitoring and inspection programs of in-service structures - such as the support structures of offshore wind turbines. T2 - Fatigue Design 2023 (FatDes 2023) CY - Senlis, France DA - 29.11.2023 KW - Fatigue KW - Welded KW - NDT KW - Crack growth PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-600238 DO - https://doi.org/10.1016/j.prostr.2024.03.062 VL - 57 SP - 560 EP - 568 PB - Elsevier B.V. AN - OPUS4-60023 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Duarte, Larissa A1 - Madia, Mauro A1 - Zerbst, Uwe T1 - The use of effective fatigue crack propagation data obtained at closure-free conditions for component assessment N2 - The knowledge of fatigue crack propagation data in terms of their effective values is important for a conservative and safe life assessment of components subjected to cyclic loading. To overcome issues related to the precise consideration of the crack-closure effects on experimental data obtained at small R ratios, closure-free data have been obtained at R ≈ 0.8 by different experimental procedures. The statistical analysis of the intrinsic fatigue crack propagation threshold obtained experimentally has shown a small data scatter and good agreement between procedures. When compared with effective values obtained from analytical corrections of closure-affected data, the data obtained at R ≈ 0.8 should lead to a conservative life estimation. T2 - 43rd International Conference on Materials Mechanics CY - Sani, Greece DA - 05.06.2022 KW - Component assessment KW - Effective crack propagation data KW - Experimental procedure KW - Crack-closure PY - 2022 SP - 104 EP - 108 AN - OPUS4-56851 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geburtig, Anja A1 - Wachtendorf, Volker A1 - Trubiroha, P. A1 - Giehl, A. A1 - Schönlein, A. A1 - Feil, F. T1 - Normenvorschlag zur Bewitterung transparenter oder transluzenter Kunststoffe N2 - Aufgrund des tieferen Eindringens der solaren Strahlung treten bei transparenten und bei transluzenten (durchscheinenden) Kunststoffen veränderte Bedingungen gegenüber opaken Proben auf. Dies kann zu speziellen Effekten und damit zu einem abweichenden Bewitterungsverhalten führen. Auch aus Mangel an geeigneten Normen werden diese Effekte häufig vernachlässigt. Deshalb initiiert der DIN-FNK auf ISO-Ebene ein entsprechendes Dokument. Die Norm ist in der Form eines Technical Reports geplant. In einem ersten Teil sollen die Besonderheiten transparenter oder transluzenter Kunststoffe erläutert werden, um den Nutzer für mögliche Probleme zu sensibilisieren. Im zweiten Teil werden Empfehlungen für Bestrahlung oder Bewitterung herausgearbeitet. In einem dritten Teil geht es dann um Besonderheiten bei der Messung von Eigenschaftsänderungen transparenter bzw. transluzenter Kunststoffe. In informativen Anhängen sollen verschiedene Beispiele die Thematik illustrieren. T2 - 51. Jahrestagung der GUS CY - Stutensee-Blankenloch, Germany DA - 29.03.2023 KW - Bewitterung KW - Polymer 3R KW - Bestrahlung KW - UV PY - 2023 SN - 978-3-9818507-8-9 SP - 39 EP - 46 PB - Gesellschaft für Umweltsimulation e.V. CY - Pfinztal (Berghausen) AN - OPUS4-57271 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geburtig, Anja A1 - Wachtendorf, Volker A1 - Falkenhagen, Jana T1 - Combined impact of UV radiation and nitric acid (HNO3) on HDPE jerrycans – comparison of outdoor and lab test N2 - A damaging action of HNO3-55% only occurs in combination with its decomposition into nitrous gases, which can be caused by UV radiation. In a laboratory test, transparent HDPE jerrycans have been exposed to both UV radiation and 55 wt-% nitric acid solution at (41 ± 2)°C, for up to 20 days. For comparison, UV radiant exposure (21 days) and nitric acid exposure (up to 6 weeks) were performed separately, at nearly equal temperatures. The respective damages are compared with FTIR spectroscopy in ATR and HT-gel permeation chromatography (GPC) on a molecular level and with hydraulic internal pressure testing as a component test. For the used jerrycans, relevant oxidation can only be found after the combined exposure. The gradual increase in oxidative damage shows the good reproducibility of the lab exposure. The decomposition of nitric acid into nitrous gases by UV radiation – as well as the jerrycan oxidation – is also observed at lower HNO3 concentration (28 wt- %). Similar results are obtained after outdoor tests. Again, the damage occurs only after combined exposure, in contrast to the exposures to UV only and to HNO3 only, which were conducted in parallel. Outdoor exposures are most readily accepted as they represent possible end-use conditions. However, the reproducibility of these exposures is poor due to the large temporal variations in weather. There are also several safety risks, which is why the number of replicates remains limited. Since the outdoor and lab exposure tests show the same qualitative results, it is appropriate to conduct systematic studies in the laboratory. After 6 days of lab exposure, the oxidation damage is rated as critical, which corresponds to about 1/10 year in Central Europe, according to the UV radiant exposure. It should be noted that this amount can also occur in two sunny weeks. T2 - 24th iapri World Packaging Conference CY - Valencia, Spain DA - 17.06.2024 KW - Ppolyethylene KW - UV exposure KW - Nitric acid KW - Oxidation PY - 2024 VL - 2 SP - 30 EP - 37 PB - ITENE AN - OPUS4-60414 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bulling, Jannis A1 - Jurgelucks, B. A1 - Prager, Jens A1 - Walther, A. T1 - Modellierung und Validierung eines inversen Verfahrens zur Schadensrekonstruktion mittels Lamb-Wellen im Ultraschallbereich N2 - Das Ausbreitungsverhalten geführter Ultraschallwellen ermöglicht die großflächige Prüfung von Platten und schalenförmigen Bauteilen wie Rohren und Laminaten auf Fehlstellen von wenigen Prüfpunkten aus. Während die beschränkte Divergenz der geführten Wellen die Ultraschallprüfung begünstigt, erschwert das dispersive und multimodale Verhalten der Lamb-Wellen die Auswertung der Ultraschallsignale. Die dispersive und multimodale Wellenausbreitung verkompliziert die Bestimmung der Fehlerposition bei der Auswertung der Geschwindigkeiten einzelner Wellenpakete. Zudem ist es herausfordernd, einen einfachen Zusammenhang zwischen den Reflexionen der Fehlstelle und deren Größe und Form herzustellen. Eine Möglichkeit zur genauen Bestimmung der Fehlerposition und -geometrie bietet der direkte Vergleich der Messsignale mit den Signalen aus einem Simulationsmodell. Die Nachbildung des Schadens im Simulationsmodell stellt ein inverses Problem dar, das iterativ gelöst werden kann, indem ein Vorwärtsmodell immer weiter optimiert wird. Klassische Ansätze wie die Finite Elemente Methode (FEM) sind für die Simulation von Ultraschallwellen aufgrund der kleinen Wellenlängen im Vergleich zur Bauteilgröße meist ineffizient. Aus diesem Grund basiert das vorgestellte Vorwärtsmodell auf der semi-analytischen Scaled Boundary Finite Element Method (SBFEM), die große Teile der Wellenausbreitung analytisch berechnet. In diesem Beitrag wird die Validierung des zweidimensionalen Modells an Platten mit einer rechteckigen Nut als Ersatzfehler präsentiert und es werden erste Schritte zur Validierung von 3D-Modellen vorgestellt. T2 - DAGA 2024 CY - Hannover, Germany DA - 18.03.2024 KW - Geführter Ultraschall KW - Inverse Verfahren KW - SBFEM PY - 2024 UR - https://www.dega-akustik.de/publikationen/online-proceedings SP - 644 EP - 647 AN - OPUS4-60212 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geburtig, Anja A1 - Trubiroha, Peter A1 - Wachtendorf, Volker T1 - Significance of new data pairs for irradiance and (surface) temperature N2 - There is consent that UV irradiance and temperature at the place of photodegradation are the most important environmental parameters in weathering, along with humidity. This contribution shows how an improvement in the measurement data situation can improve the significance and comparability of outdoor exposures. Photooxidative ageing is calculated using sample polymers for which the corresponding modelling data (Exposure Response Functions, ERF) is available. The mean square deviations are estimated, which result from using different spectral irradiances and different spectral sensitivities, both of the sensors and the polymers. It will be shown here how the significance of the irradiance values increases with increasing approximation of the spectral sensitivities of the sensor and polymer. Also, the mean square deviations are estimated, which result from using different activation energies and surface temperatures. A selection of different variables to describe the weathering exposure is created. The potential of either individual values or data pairs is evaluated in terms of significance or correlation to the calculated photooxidative ageing. Recording hourly data also enables subsequent evaluations of individual test specimens, adapted to the respective colour or to determine activation energies. An accumulated value, calculated from PIT-radiometer irradiance and a suited surface temperature, can provide a comparison of different outdoor exposures over different locations or years. Thus, a characterisation of the weathering exposure would be related to a reference spectral sensitivity (much closer to a polymer than that of a common UV radiometer), one reference activation energy, and different surface temperature scenarios with, on the one hand, graded solar absorptions (white / grey / black) and, on the other hand, different thermal couplings (coated metal / thick plastic). This results in three values each for plastic samples and coated metals (light / grey / dark). It will never be possible to accurately predict the weathering tests for individual samples (with their specific sensitivities), but the proposed approaches can go a long way towards the comparability of outdoor weathering exposures. T2 - 10th European Weathering Symposium EWS CY - Graz, Austria DA - 11.09.2024 KW - Polymer 3R KW - Outdoor weathering PY - 2024 SN - 978-3-9826129-1-1 SP - 121 EP - 133 PB - Stober Medien GmbH CY - Eggenstein AN - OPUS4-61291 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zhu, J. A1 - Madia, Mauro A1 - Schurig, M. A1 - Kruse, Julius A1 - Conrad, F. A1 - Schlums, H. A1 - Kontermann, C. A1 - Zerbst, Uwe T1 - Anwendung von repräsentativen Proben zur Bewertung der Strukturintegrität von sicherheitsrelevanten Komponenten N2 - Sicherheitsrelevante Bauteile, bei denen ein Versagen im Betrieb katastrophale Folgen haben könnte, sind in der Regel für eine sehr geringe Ausfallwahrscheinlichkeit ausgelegt und unterliegen strengen Qualifizierungsverfahren gemäß den von den Aufsichtsbehörden festgelegten Richtlinien. Die Hersteller sind oft gezwungen, Tests an realen oder skalierten Komponenten durchzuführen, um die Strukturintegrität unter definierten Belastungsbedingungen sicherzustellen, die in der Regel strenger sind als die im Betrieb zu erwartenden. Dies ist in der Regel mit einem enormen experimentellen und finanziellen Aufwand verbunden. Daher versuchen die Unternehmen, neue Strategien wie digitale Zwillinge zu entwickeln, mit denen die Kosten massiv gesenkt werden können, ohne die Sicherheit zu beeinträchtigen. In dieser Arbeit wird ein neues quasistatisches Prüf- und Bewertungskonzept vorgestellt, dessen Hauptidee darin besteht, die experimentelle Prüfung von Bauteilen durch die Prüfung von für das Bauteil repräsentativen Proben zu ersetzen oder zumindest zu reduzieren. Der größte Vorteil des vorgeschlagenen Konzepts besteht darin, dass die Versuche auf Laborprüfmaschinen durchgeführt werden können. Die Wirksamkeit der Methodik wird anhand der Bewertung der Strukturintegrität einer Turbinenscheibe aus einer Ni-Basis-Superlegierung für Flugzeugtriebwerke bei Überdrehzahl demonstriert. T2 - 57. Tagung des DVM-Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Köln, Germany DA - 18.02.2025 KW - Strukturintegrität KW - Bruchmechanik KW - Turbinenscheibe KW - Repräsentative Proben PY - 2025 DO - https://doi.org/10.48447/BR-2025-536 SP - 231 EP - 240 PB - DVM CY - Berlin AN - OPUS4-62602 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kanna, Naveen A1 - Bär, Jürgen A1 - Duarte, Larissa A1 - Madia, Mauro ED - Ricoeur, Andreas T1 - Ermittlung von Kitagawa-Takahashi-Diagrammen mittels Gleichstrompotentialsondenmessungen N2 - Das Kitagawa-Takahashi Diagramm ist ein wichtiges Werkzeug zur Beschreibung der ausgeprägten Langzeitfestigkeit fehlerbehafteter Bauteile. Insbesondere im technisch relevanten Übergangsbereich unterscheiden sich jedoch die verwendeten Modelle. Daher ist für eine sichere Aussage eine experimentelle Absicherung in diesem Bereich zwingend notwendig. In dieser Arbeit wird eine Methode vorgestellt, die eine einfache und schnelle Absicherung des Verlaufs im Übergangsbereich erlaubt. Hierzu werden in Flachproben mittels eines Gravierlasers scharfe Kerben mit einer definierten Breite und Tiefe eingebracht. Die so präparierten Proben werden mit blockweise steigender Last bis zum Bruch ermüdet. Die Erkennung von Anrissen erfolgt mittels einer Gleichstrom-Potentialsonde mit der auch die Länge des Lastblocks gesteuert wird. T2 - 57. Tagung des DVM-Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Cologne, Germany DA - 18.02.2025 KW - Ausgeprägte Langzeitfestigkeit KW - Materialdefekte KW - KT-Diagramm KW - Gleichstrom-Potentialsonde PY - 2025 DO - https://doi.org/10.48447/BR-2025-513 VL - 257 SP - 105 EP - 112 PB - Deutscher Verband für Materialforschung und -prüfung e.V. CY - Berlin, Deutschland AN - OPUS4-62604 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Voigt, Marieke A1 - von Werder, Julia A1 - Meng, Birgit ED - Middendorf, B. ED - Fehling, E. T1 - Microstructure analysis of thermally treated ultra high performance concrete in the context of the durability performance N2 - Ultra high performance concrete (UHPC) is known for its high compressive strength of more than 150 MPa and its high durability. Thermal treatment at 90°C can accelerate the strength development so that the 28-days-strength can be achieved immediately after the treatment and an additional increase up to 30 % in some cases. The reason for the strength development is an accelerated hydration of the clinker minerals and an intensified pozzolanic reaction leading to a denser microstructure. In previous research inhomogeneities in form of a zonation after unprotected thermal treatment were observed and analysed in respect to changes in the microstructure. This zonation is defined by a different microstructure in the core compared to the outer zone in the matter of porosity, mineral phase composition and a significant change in the potassium and sulphur concentration of the zones is measurable. To isolate different transport mechanisms responsible for these element distributions UHPC samples were thermally treated at 90 °C and the microstructure was investigated under dry conditions and after immersion in water to investigate the influence of dehydration during and rehydration after the thermal treatment on the microstructure. Through durability testing via water absorption, water vapour diffusion, permeability testing and sulfuric acid resistance transport mechanisms like diffusion, migration, capillary suction are under investigation in correlation with the microstructure analysis. For the microstructure analysis measurements with µXRF, mercury intrusion porosity, XRD and SEM were conducted. T2 - HiPerMat 2020 CY - Kassel, Germany DA - 11.03.2020 KW - UHPC KW - Thermal treatment KW - Zonation KW - Transport mechanism KW - Durability PY - 2020 SN - 978-3-7376-0828-2 DO - https://doi.org/10.17170/kobra-202002271026 VL - 23 SP - 151 EP - 152 PB - Kassel University Press CY - Kassel AN - OPUS4-52373 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wachtendorf, Volker A1 - Wägner, Yannick A1 - Geburtig, Anja T1 - Gedanken, Tipps & Tricks zu künstlichen Bewitterungsprüfungen N2 - Die Fragestellung kann nur exemplarisch dargestellt werden, aber ist hoffentlich auch für langjährige Praktiker in den ausgewählten Punkten interessant. Es sollen für folgende Bereiche Beispiele gegeben werden: Probenvorbereitung, Testvorbereitung, Testdurchführung und Auswertung. T2 - 53. Jahrestagung der GUS 2025 CY - Stutensee-Blankenloch bei Karlsruhe, Germany DA - 26.03.2025 KW - Wechseltemperaturen KW - Künstliche Bewitterung KW - Prüfung KW - UV KW - Feuchte KW - Beregnung PY - 2025 SN - 978-3-9826129-2-8 VL - 53 SP - 253 EP - 257 PB - Gesellschaft für Umweltsimulation e.V. CY - 76327 Pfinztal (Berghausen) AN - OPUS4-62861 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nicolai, Marcel A1 - Bulling, Jannis A1 - Lugovtsova, Yevgeniya A1 - Zeipert, Henning A1 - Prager, Jens A1 - Henning, Bernd ED - van Keulen, Wim ED - Kok, Jim T1 - On the repulsion effect of coupled Lamb wave modes N2 - Lamb waves, recognized for their significance in material characterisation, structural health monitor-ing, and non-destructive testing, exhibit complex behaviours that are crucial for industrial applica-tions. This paper delves into the mathematical and physical principals of the repulsion effect that can be observed in the dispersion curves of coupled Lamb wave modes. This effect is the result from the mechanical coupling of thin-walled solid plates and prevents the crossing of the dispersion curves. The study employs the Scaled Boundary Finite Element Method to calculate the dispersion curves of coupled plates and to simulate their interaction for a weak and ideal coupling. Through a mathemati-cal framework and a physical analogy with simple harmonic oscillators, the paper elucidates the un-derlying principals of this effect. Furthermore, the paper highlights the practical significance of the repulsion effect in Lamb waves, suggesting its application for testing and monitoring the integrity of multi-layer structures like adhesive bonds, which are important for various industrial applications. A deepened understanding of this effect could contribute to the enhancement of non-destructive evalua-tion techniques. T2 - ICSV 2024 CY - Amsterdam, The Netherlands DA - 08.07.2024 KW - Scaled Boundary Finite Element Method (SBFEM) KW - Lamb waves KW - Mode repulsion KW - Mechanical coupling KW - Dispersion curves PY - 2024 SN - 978-90-90-39058-1 SN - 2329-3675 SP - 410 EP - 418 PB - The International Institute of Acoustics and Vibration (IIAV) CY - Amsterdam AN - OPUS4-62855 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nicolai, Marcel A1 - Bulling, Jannis A1 - Lugovtsova, Yevgeniya A1 - Zeipert, Henning A1 - Prager, Jens A1 - Henning, Bernd T1 - On the repulsion effect of coupled Lamb wave modes N2 - This work investigates the phenomenon of mode repulsion in coupled Lamb wave systems. By mechanically coupling two dissimilar plates using spring elements, it is shown that previously intersecting Lamb wave modes are repelled, avoiding any crossing in the dispersion curves. The effect, rooted in eigenvalue theory and first observed in quantum systems, is explained through both mathematical models and classical analogies with coupled harmonic oscillators. Numerical simulations using the Scaled Boundary Finite Element Method validate the theoretical predictions, revealing a correlation between strain distribution and frequency splitting. The observed mode repulsion provides new insights into interface properties and offers potential for applications such as monitoring adhesive degradation in layered structures. T2 - DAGA 2024 CY - Hannover, Germany DA - 18.03.2024 KW - Scaled Boundary Finite Element Method (SBFEM) KW - Lamb waves KW - Mode repulsion KW - Mechanical coupling KW - Dispersion curves PY - 2024 SP - 632 EP - 635 AN - OPUS4-62854 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kühnel, Alena A1 - Stelzner, Ludwig A1 - Weise, Frank T1 - Measurement and analysis of concrete pavement surface textures using hand-held 3D laser scanning technology N2 - Concrete pavement surface textures are divided by means of their dimension into four categories: microtexture, macrotexture, megatexture and roughness. They influence the most important performance characteristics of road surfaces, such as friction (also referred to as “skid resistance”), tire/pavement noise, evenness and surface drainage. These properties are relevant for driving safety, comfort and environmental aspects. Up to now, research in Germany has focused on monitoring these characteristics by tire/pavement noise and skid resistance measurements. However, the topography of surface textures has not been sufficiently investigated and evaluated until now. The development and availability of high-performance, hand-held 3D scanning systems during the last years enable measurements of the microtexture and macrotexture of concrete pavement surfaces at short measuring times and high resolution. This paper shows the ability of modern laser-based technology to record three-dimensional data of different concrete pavement surface textures in situ. For this purpose, a special measuring frame has been developed. The presented results were primarily obtained within the framework of a research project commissioned by the German Federal Highway Research Institute (BASt) and processed by the Federal Institute for Materials Research and Testing. Various concrete pavement surface textures by means of diamond grinding and hybrid of diamond grinding and grooving were investigated in situ. In addition, exposed aggregate concretes (EAC), which were introduced as a standard type of concrete for motorway pavements in Germany in 2006, have been analyzed. Based on the gathered 3D data, evaluation routines for qualitative and quantitative analysis have been developed and applied. The aim was to derive the statistical parameters such as the relative and cumulative frequency distribution of the profile depth as well as the roughness coefficient for diamond ground pavements and EAC. Also, the “mean profile depth” (MPD) as a common texture-related parameter was determined. T2 - 14th International Symposium on Concrete Roads CY - Krakow, Poland DA - 25.06.2023 KW - Concrete pavement surface textures KW - 3D Laser Scanning KW - Diamond Grinding KW - Exposed aggregate concrete KW - Data analysis KW - Surface characteristics PY - 2023 SP - 1 EP - 14 AN - OPUS4-57893 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - von Werder, Julia A1 - Simon, Sebastian A1 - Meng, Birgit T1 - Internal sulfate resistance of concrete N2 - If the amount of sulfate within the mix design for concrete is not balanced, ettringite formation which first controls solidification continues while the concrete is hardening. Ettringite forms by reaction of sulfate contained in the cement or in some admixture with calcium aluminate (C3A) as cement component. The “late primary ettringite formation” promotes an increase in volume within the hardened concrete leading to cracks. To analyze the effect of substituting part of ordinary Portland cement (OPC) by a treated brown coal fly ash mortar bars were tested according to ASTM C452. This test method was originally developed to extrapolate from the internal to external sulfate attack and is based on the idea that by testing a concrete mixture containing sulfate the process of deterioration is accelerated because it does not have to diffuse into the concrete before reaction first. In addition to the samples prescribed in ASTM C452 further samples in the size of the German SVA procedure were tested also designed for accessing the external sulfate resistance. The results show that while the replacement of 25 % of cement by brown coal fly ash leads to length changes around the limit defined by ASTM, the substitution of 50 % cement exceeded the limit by a multiple. The progress of expansion is the very similar for the two geometries tested. In-situ XRD measurements confirmed that while for pastes made of OPC the formation of ettringite is completed after 20 hours, this is not true for the mixtures containing the brown coal fly ash. In a different study the effect of hydrothermal treatment on the phase composition of ultra-high-performance concrete was analyzed. The results show that the sulfate and aluminate resulting from the decomposition of ettringite are bound into new phases. If this binding is permanent this might allow the larger use of sulfate bearing raw materials. T2 - EuroCoalAsh 2021 Conference CY - Online meeting DA - 02.11.2021 KW - Brown coal fly ash KW - Ettringite KW - Internal sulfate resistance KW - Test methods KW - In-situ XRD KW - Hydrothermal treatment PY - 2021 SP - 131 EP - 137 CY - Thessaloniki AN - OPUS4-54133 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reuter, T. A1 - Wohlgemuth, F. A1 - Bellon, Carsten A1 - Hausotte, T. T1 - Measurement-based Detector Characteristics for Digital Twins in aRTist 2 N2 - Various software products for the simulation of industrial X-ray radiography have been developed in recent years (e.g., aRTist 2, CIVA CT, Scorpius XLab, SimCT, Wilcore) and their application potential has been shown in numerous works. However, full systematic approaches to characterise a specific CT system for these simulation software products to obtain a truthful digital twin are still missing. In this contribution, we want to present two approaches to obtain realistic grey values in X-ray projections in aRTist 2 simulations based on measured projections. In aRTist 2, the displayed grey value of a pixel is based on the energy density incident on that pixel. The energy density is calculated based on the X-ray tube spectrum, the attenuation between source and detector as well as an energy-dependent sensitivity curve of the detector. The first approach presented in this contribution uses the sensitivity curve as a free modelling parameter. We measured the signal response at different thicknesses of Al EN-AW6082 at different tube voltages (i.e., different tube spectra). We then regarded the grey values displayed by these projections as a data regression respectively an optimisation problem and obtained the sensitivity curve that is best able to reproduce the measured behaviour in aRTist 2. The resulting sensitivity curve does not necessarily hold physical meaning but is able to simulate the real system behaviour in the simulation software. The second approach presented in this contribution is to estimate the sensitivity curve based on assumptions about the characteristics of the scintillation detector (e.g., scintillator material, scintillator thickness and signal processing characteristics). For this approach, a linear response function (linear relationship between the deposited energy per pixel and the resulting grey value) is assumed. If the detector characteristics, which affect the simulated deposited energy, are properly modelled, the slope and offset of the response function to match the measured grey values should be the same for different tube spectra. As the offset is constant and given by the grey values measured at no incident radiation, the slope is the remaining parameter to evaluate the success of the detector modelling. We therefore adapted the detector characteristics by changing the detector setup until the slope was nearly the same for all measured tube spectra. We are aware that the resulting parameters of the scintillator material and thickness might not be the real ones, but with those modelling parameters we are able to simulate realistic grey values in aRTist 2. Both of those approaches could potentially be a step forward to a full systematic approach for a digital twin of a real CT system in aRTist 2. T2 - 20th World Conference on Non-Destructive Testing (WCNDT 2024) CY - Incheon, South Korea DA - 27.05.2024 KW - Digital Twin KW - Computed Tomography KW - Simulation PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-602046 DO - https://doi.org/10.58286/29910 SP - 1 EP - 10 PB - NDT.net CY - Mayen, Germany AN - OPUS4-60204 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nietzke, Jonathan A1 - Rhode, Michael A1 - Mente, Tobias A1 - Kannengießer, Thomas T1 - Experimental and numerical characterization of hydrogen diffusion in thick-walled submerged arc welded joint of S420G2+M offshore steel grade N2 - Offshore wind turbines are an important goal in national energy strategies worldwide. Foundation structures are manufactured from submerged arc welded (SAW) plates with thicknesses up to 200 mm. In that connection, high-strength steels like the S420G2+M are more and more applied offering the possibility for increased stability and load-bearing capacity of the foundations. These offshore steel grades can show a susceptibility for delayed hydrogen assisted cold cracking of the weld joints. For that purpose, a minimum waiting time (MWT) of up to 48 h (dependent on applied standards) is recommended before non-destructive testing is allowed and conducted. But this concept is based on older steel grades that have been used for three or more decades. Nowadays, the metallurgical improvements (clean steels, proper rolling, and heat treatment) of base materials and well as welding consumables must be anticipated. Hence, the MWT concept should be critically discussed as it is assumed to be very conservative. For that reason, the focus of this study was to investigate the diffusion behavior in S420G2+M steel and its multi-layer SAW joint. Electrochemical permeation experiments were carried at room temperature. Boundary conditions were anticipated in terms of using different sample thicknesses. From the experimental data, hydrogen diffusion coefficients and absorbed diffusible hydrogen concentrations had been calculated. It was shown that hydrogen diffusion in the base material is increased compared to the weld metal. In addition, the sample thickness had a significant on the calculated diffusion coefficients. The minimum and maximum diffusion coefficients had been used for numerical modelling of the hydrogen diffusion in the welding joint. It became clear that a MWT must be always regarded together with a critical initial diffusible hydrogen concentration for the evaluation of a possible delayed cracking as diffusion times were mostly > 48 h due to the thick plates. T2 - 4th International Conference on Metals and Hydrogen - Steely & Hydrogen 2022 CY - Ghent, Belgium DA - 11.10.2022 KW - Hydrogen KW - Submerged arc welding KW - Diffusion KW - Minimum waiting time KW - Electrochemical permeation PY - 2022 SP - 1 EP - 11 CY - Ghent, Belgium AN - OPUS4-56075 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Nietzke, Jonathan A1 - Czeskleba, Denis A1 - Kannengießer, Thomas T1 - Untersuchung von Spannungsrelaxationsrissmechanismen mittels Simulation einachsiger Spannungszustände in der Grobkornzone von UP-geschweißtem CrMoV-Stahl N2 - Druckbehälter mit großen Wandstärken (250+ mm) aus hochwarmfesten, niedriglegierten Stählen werden hauptsächlich Mehrdraht-Unterpulver-(UP) geschweißt. Der damit verbundene hohe Energieeintrag führt unter anderem zu hohen lokalen Schweißeigenspannungen, welche bei unsachgemäßer Prozessführung der notwendigen Wärmenachbehandlung (PWHT) zu Spannungsrelaxationsrissen (SRR) führen. In den Bewertungskriterien zur Spannungsrelaxationsrissanfälligkeit finden weder die, mit klassischen, freischrumpfenden Schweißversuchen nicht abbildbaren, erhöhten Eigenspannungen aus der Schrumpfbehinderung der Bauteilsteifigkeit Beachtung, noch die damit einhergehenden metallurgischen Effekte wie bspw. das Ausscheidungswachstum während der PWHT und damit einhergehende Härteunterschiede an den Korngrenzen bzw. die vorzeitige Alterung durch Bildung differenter Sonderkarbide. Die Aufheizrate des PWHT als Einflussfaktor für die SRR-Bildung bleibt derzeit ebenfalls unbeachtet. Daher wurde eine Versuchsmethodik entwickelt, die eine mögliche SRR-Anfälligkeit durch die Kopplung von thermischer und mechanischer Beanspruchung untersucht. Dazu wurden Proben mit unterschiedlichen Gefügen thermisch simuliert und während des PHWT repräsentativ mit sehr hohen Lasten/Eigenspannungen mechanisch beansprucht. Dazu wurde an Kleinzugproben für das as-welded UP-Schweißgut und die thermisch simulierte GKZ eines 13CrMoV9-10 die Dehnung des Prüfbereichs bei variablen Querspannungen und Aufheizraten gemessen. Diese aufheizraten- und gefügeabhängige Längenänderung der Probe wurde durch mathematische Prozeduren analysiert. Damit war es möglich, singuläre werkstoffliche Effekte auf μm-Ebene (Ausscheidungswachstum) als summarische Längen- bzw. Volumenänderung per klassischer Kurvendiskussion zu beschreiben. Die erste und zweite Ableitung zeigten eine ausscheidungsabhängige Härtezunahme, welche von der Spannung und Aufheizrate im geringen Maß linear abhängig war. Gleichzeitig sind Volumenänderungen bei Bildung und Wachstum differenter Sonderkarbide bekannt, welche zusammen mit gefügespezifischen Untersuchungen und der neuen Versuchsmethodik zu einer verbesserten Beurteilung der SRR-Anfälligkeit von geschweißten CrMoV-Stählen beitragen sollen. Prinzipiell ist die vorgestellte Methodik jedoch werkstoff- und zustandsoffen, d.h. sowohl für Grundwerkstoff e als auch definierte Wärmebehandlungsbedingungen geeignet. Dies ermöglicht erstmals die Schaffung einer Transfergröße zwischen Labor und realen Schweißungen, unter Beibehaltung der Bauteilsteifigkeit, d.h. vereinfachte, aber realistische Eigenspannungsabbildung als Grundlage für weitergehende gefügespezifische metallurgische Effekte während des PWHT. T2 - DVS Congress 2022 CY - Koblenz, Germany DA - 19.09.2022 KW - UP-Schweißen KW - Spannungsrelaxationsriss KW - Wärmenachbehandlung KW - Ersatzgeometrie KW - Prüfverfahren PY - 2022 SN - 978-3-96144-190-7 VL - 382 SP - 69 EP - 75 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-55946 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Kannengießer, Thomas T1 - Fügetechnik in Wasserstofftechnologien - Forschungsbedarf für die Branche (Kurzversion) N2 - Die Studie gibt einen kurzen Überblick über die jetzige Bedeutung der Fügetechnik in Wasserstofftechnologien und über zukünftige Forschungsbedarfe für die Branche in den einzelnen Technologiefeldern Wasserstofferzeugung, -speicherung, -transport und -nutzung. Fügetechnologien haben dabei wesentliche Bedeutung für die erfolgreiche Umsetzung von technischen Komponenten der Wasserstofftechnologien. Die Schwerpunkte bzw. Forschungsbedarfe ergeben sich bspw. durch die Erstellung neuer Infrastruktur für Wasserstoffspeicherung und -transport sowie durch Umnutzung der bestehenden Erdgasinfrastruktur. Bei der Wasserstofferzeugung und -anwendung wird z.B. die Entwicklung effiziente Massenproduktionsmethoden von Elektrolyseuren und Brennstoffzellen einen wichtigen Meilenstein bilden und laserbasierte Fügetechnologien sind hier zum Teil schon etabliert. Die additive Fertigung nimmt dabei eine Querschnittsposition ein und besitzt hohes Anwendungspotential für die Zukunft z.B. für die Fertigung von Komponenten in Gasturbinen. Aus den technischen Fragestellungen und Forschungsbedarfen ergeben sich zudem Herausforderungen für die notwendige Neu- und Weiterentwicklung von technischen Regelwerken und Normen und den Eingang in die Aus- und Weiterbildung von fügetechnischem Fachpersonal. T2 - DVS Congress 2021 CY - Online meeting DA - 14.09.2021 KW - Wasserstoff KW - Fügetechnik KW - Forschung KW - Werkstoff KW - Bedarf PY - 2021 SN - 978-3-96144-146-4 VL - 371 SP - 612 EP - 624 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-53370 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Czeskleba, Denis A1 - Kannengießer, Thomas T1 - Kurzbericht zum Projekt „Entwicklung von Wärmenachbehandlungskonzepten zur Vermeidung von Spannungsrelaxationsrissen an Bauteilen aus hochwarmfesten Stählen“ (DVS-Nr. 01.2261 / IGF-Nr. 20171 N) N2 - Komponenten aus dickwandigen, hochwarmfesten CrMoV-Stählen erfordern eine anspruchsvolle UP-Schweißverarbeitung. Dabei muss die notwendige Wärmenachbehandlung der Schweißnaht (PWHT) sicher beherrscht werden. Hier kann u.U. Bauteilversagen infolge von Spannungsrelaxationsrissbildung (SRR) auftreten. Bislang erfolgt die Beurteilung der SRR-Neigung primär über Ersatzgrößen, wie temperaturbedingte Änderung der Härte und Duktilität. Die Wirkung der konstruktiven Schrumpfbehinderung einer Schweißnaht auf die SRR ist bislang völlig unbekannt. Hier setzt das Forschungsprojekt an, hinsichtlich der Gewinnung und Optimierung der Parameter für die PWHT unter realitätsnahen Bauteilsteif igkeiten (def inierte Einspannbedingung) mit dem Ziel der SRR-Vermeidung. Am Beispiel des niedriglegierten, hochwarmfesten Stahls 13CrMoV9-10 wurden UP- Schweißungen unter industriepraktischen Bedingungen freischrumpfend bzw. unter definierter Schrumpfbehinderung durchgeführt. Diese wurden mit unterschiedlichen PWHT-Szenarien (Variation der Auf heizrate und Endtemperatur) beaufschlagt. Die Ergebnisse des Projektes DVS 01.2261 / IGF 20171 N werden in diesem Beitrag vorgestellt, wie Aussagen zur SRR-Suszeptibilität in Abhängigkeit von Mikrostruktur und vorliegender mehrachsiger mechanischer Beanspruchung der Schweißnaht vor/während des PWHT. Für einen kritischen Zustand sind hohe Kräfte / Spannungen notwendig, die in freischrumpfenden Schweißversuchen u.U. nicht abbildbar sind. Die Berücksichtigung des mikrostrukturspezifischen Ausscheidungsverhaltens (in Schweißgut und Wärmeeinflusszone) unter realitätsnahen Einspannbedingungen ist für die Bewertung einer SRR-Suszeptibilität notwendig. Instrumentierte Schweißversuche unter definierter Schrumpfbehinderung ermöglichen hier das Monitoring der entstehenden Reaktionskräfte, -momente bzw. -spannungen. Ausgehend von diesem Referenzzustand erfolgte die Applikation der PWHT-Szenarien bzw. deren praktische Überprüfung. Zusätzlich wurde eine Ersatzprüfmethodik entwickelt, die die Betrachtung der mikrostrukturspezifischen SRR-Suszeptibilität unter Beibehaltung der äußeren Schrumpfbehinderung der Schweißnaht während des PWHT ermöglicht. Hierdurch wird die Bauteilübertragbarkeit ermöglicht und eine Transfergröße geschaffen, welche die Bauteilbewertung hinsichtlich der SRR-Neigung umfasst. T2 - DVS Congress 2022 CY - Koblenz, Germany DA - 19.09.2022 KW - UP-Schweißen KW - Spannungsrelaxationsriss KW - Forschungsprojekt KW - Dickblech KW - Wärmebehandlung PY - 2022 SN - 978-3-96144-190-7 SP - 76 EP - 82 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-55944 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quackatz, Lukas A1 - Griesche, Axel A1 - Kannengießer, Thomas A1 - Treutler, K. A1 - Gehling, T. A1 - Eissel, A. A1 - Wesling, V. T1 - In situ Messung der chemischen Konzentration in der Schmelze während des WIG-Schweißens von Duplexstählen N2 - Duplexstähle besitzen ein zweiphasiges Gefüge und werden aufgrund ihrer verbesserten Schweißeignung gegenüber den Vollausteniten häufig im Anlagen- bzw. Apparatebau eingesetzt. Aufgrund der hohen Abkühlgeschwindigkeit und dem Abbrand von Legierungselementen kommt es zu einer Ferritisierung des Schweißguts und damit zu einer Degradation der mechanischen Eigenschaften. Zur Vorhersage des Phasenverhältnisses im Schweißgut wird das WRC1992-Diagramm genutzt. Dieses Diagramm zeigt einige Ungenauigkeiten und benötigt zur genaueren Vorhersage der Phasenverhältnisse eine Überarbeitung. Um den Einfluss einzelner Elemente auf das Schweißnahtmikrogefüge besser zu verstehen, wurden drahtförmige Schweißzusatzwerkstoffe mit dem Ferrit-Bildner Nb und dem Austenit-Bildner Cu beschichtet und für Schweißungen verwendet. Die Messmethode der Laser-induzierten Plasmaspektroskopie (LIBS) bietet hier eine gute Möglichkeit der in situ Überwachung der chemischen Konzentrationen, während des WIG-Schweißens von Duplexstählen. Die LIBS-Messergebnisse, konnten mit der Ferritnummer und der Schweißnahtmikrostruktur korreliert werden. T2 - Symposium Materialtechnik der TU Clausthal CY - Clausthal-Zellerfeld, Germany DA - 23.02.2023 KW - LIBS KW - In situ measurement KW - WRC 1992 diagram KW - Dduplex stainless steel KW - TIG welding PY - 2023 VL - 12 SP - 612 EP - 627 PB - Shaker CY - Aachen AN - OPUS4-57991 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Seifert, Lando A1 - Müller, Thoralf A1 - Ebell, Gino ED - Pillai, Radhakrishna G. T1 - Development of a new test method for assessing the susceptibility of prestressing steels to hydrogen-induced stress corrosion cracking N2 - For prestressing steel’s factory production control, approvals, and continuous surveillance in Germany, a susceptibility test against hydrogen-induced stress corrosion cracking is performed. The measured time to fracture results (in hours) must be reproducible and reliable in the test. ISO 15630-3 gives currently unpersuasive and diverging results using a free corrosion approach for hydrogen charging. A newly developed test method uses cathodic polarization for defined hydrogen charging instead of an uncontrolled and variable electron supply by metal dissolution during free corrosion. With this new test method, a reliable differentiation is possible between highly susceptible-known “old-type” quenched and tempered prestressing steel, i.e., Neptun, Hennigsdorfer, Sigma, and currently approved cold-drawn wires St 1470/1670 (CDS-1670) and St 1570/1770 (CDS-1770). The reproducibility of the new test method was evaluated in a round-robin test with eight attended testing institutes on a St 1470/1670 (CDS-1670) batch. T2 - Conference CONSEC24 CY - Chennai, India DA - 25.09.2024 KW - Hydrogen charging KW - ISO 15630-3 KW - Prestressing steels KW - Round-robin KW - Stress corrosion cracking PY - 2024 UR - https://consec24.com/# SP - 1 EP - 8 PB - Indian Institute of Technology (IIT) Madras, Centre of Excellence on Technologies for Low Carbon & Lean Construction CY - Chennai, India AN - OPUS4-61163 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Yang, Fan A1 - Meng, Xiangmeng A1 - Putra, Stephen Nugraha A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Assessment of keyhole stability in laser beam welding with external magnetic field using numerical simulation N2 - The challenge of understanding the physical mechanisms behind porosity reduction by a magnetic field during laser beam welding (LBW) is partly due to the difficulty in quantitatively evaluating keyhole stability. The commonly used index, such as keyhole depth, is typically one-dimensional, which is insufficient to capture the dynamic and three-dimensional fluctuations of the keyhole. In this paper, by utilizing a 3D multiphysical model of LBW with magnetic field, a novel keyhole geometry reconstruction algorithm has been developed to describe the keyhole profile and its fluctuation in a statistical manner to evaluate keyhole stability quantitatively. An equivalent diameter is proposed in this algorithm to reduce the irregularity of the keyhole geometry. The calculation results indicate that the time-averaged keyhole shape over 300 ms in the LBW of steel is conical, regardless of the application of an external magnetic field, which provides a more representative shape. Meanwhile, it is observed from the statistical aspect that the keyhole diameter becomes smaller, except the top part, under the influence of the magnetic field. The standard deviation of the equivalent diameter can be used as a physical variable to assess the keyhole stability quantitatively. The application of an external magnetic field can produce a noticeable reduction of the standard deviation of the equivalent diameter, namely, stabilizing the keyhole during LBW of steel. However, the different contribution from the keyhole stability affected by a magnetic field in suppressing porosity is different with materials. T2 - International Congress of Applications of Lasers & Electro-Optics 2024 CY - Hollywood, Los Angeles, USA DA - 04.11.2024 KW - Deep penetration laser beam welding KW - Numerical simulation KW - Keyhole shape KW - Keyhole stability KW - Magnetic field PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-616024 DO - https://doi.org/10.2351/7.0001528 VL - 36 IS - 4 SP - 1 EP - 7 PB - AIP Publishing AN - OPUS4-61602 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Straße, Anne A1 - Üstündag, Ömer A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael ED - Schmidt, M. ED - Vollertsen, F. ED - Govekar, E. T1 - LMD coatings as filler material for laser beam welded 30 mm thick plates N2 - The development of high energy laser sources enables single-pass welds of thick plates up to 30 mm, but often additional materials are needed to influence the properties of the weld seams. However, the homogenous distribution of filler materials in form of e.g. electrodes is only possible up to 7 mm while the elements are only traceable up to a depth of 14 mm. To overcome this problem a two-step process is used where first the edges of the weld partners are coated with the filler material by laser metal deposition (LMD) and afterwards are welded by laser beam. Single-pass welds with electromagnetic weld pool support of 30 mm thick S355 J2+N-plates with austenitic AISI 316L-coatings were investigated as well as the influence of the coatings to the penetration depth of the laser beam without electromagnetic weld pool support in double-sided joints. The weld seams were tested by X-ray inspection and cross sections. T2 - 11th CIRP Conference on Photonic Technologies [LANE 2020] CY - Online meeting DA - 07.09.2020 KW - Penetration depth KW - Laser metal deposition (LMD) KW - Laser beam welding KW - Filler material distribution PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-512790 DO - https://doi.org/10.1016/j.procir.2020.09.055 SN - 2212-8271 VL - 94 SP - 293 EP - 297 PB - Elsevier B.V. CY - Amsterdam AN - OPUS4-51279 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Yang, Fan A1 - Meng, Xiangmeng A1 - Putra, Stephen Nugraha A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Experimental and numerical investigations of suppression mechanisms by an oscillating magnetic field on process porosity during laser beam welding N2 - The magnetohydrodynamic (MHD) technology is recognized as a promising approach for improving the quality of deep penetration laser beam welding. This study employs experimental and numerical methods to investigate the effects of an auxiliary oscillating magnetic field on reducing porosity in the laser beam welding of 5754 aluminum alloy. The experimental results clearly demonstrate a significant reduction of 97% in the porosity ratio of the welded joints applied with an oscillating magnetic field compared to those without magnetic field, thereby validating the efficiency of applying MHD technology in mitigating porosity during the laser beam welding process. In addition, a transient 3D multi-physical model has been developed, integrating the MHD model and metal vapor plume, to gain a more comprehensive understanding of the porosity suppression mechanism. The weld pool shape is significantly widened and enlarged because of the Lorentz force, which facilitates the escape of gas bubbles. Meanwhile, the introduction of an oscillating magnetic field generates a time-averaged downward Lorentz force. This averaged downward Lorentz force, in turn, enhances and stables the downward fluid flow, which hinders the bubble backward movement. Meanwhile, this averaged downward Lorentz force induces an upward electromagnetic expulsive force on the bubble, which effectively increases the upward escape velocity of bubbles in the weld pool. The simulation results agree well with the experimental results. T2 - 44. Assistentenseminar Füge- und Schweißtechnik CY - Päwesin, Germany DA - 20.09.2023 KW - Laser beam welding KW - Numerical simulation KW - Magnetohydrodynamic technology KW - Porosity defect KW - Keyhole PY - 2024 UR - https://www.dvs-media.eu/de/neuerscheinungen/4671/44.-assistentenseminar-fuegetechnik SN - 978-3-96144-267-6 VL - 394 SP - 77 EP - 86 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-60784 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Blasón Gonzalez, Sergio A1 - Werner, Tiago A1 - Kruse, Julius A1 - Gilli, Daniel A1 - Madia, Mauro T1 - Experimental procedure for the determination of intrinsic fatigue crack propagation threshold ΔKth,eff and characterization of FCGR curves on miniature steel specimens N2 - The largest percentage of component life under fatigue loading conditions is spent in the short crack regime and in the initial phase of long cracks. The use of Fracture Mechanics in the characterization of fatigue crack growth rate curves has proven to be a useful and adequate tool in the prediction of fatigue lifetimes as long as certain conditions are satisfied. All the above implies the need for a methodical and accurate procedure of assessment of the material response in order to achieve a reliable prediction of lifetime in components under safe conditions, based on the damage tolerance approach. It also highlights the need to analyse the response of increasingly reduced thicknesses, which, as time goes by, show greater differences with respect to those commonly studied and defined in standards and design guidelines, as well as to the experimental studies that can be found in the literature at present. Some examples of thin-walled components are turbine blades or certain additively manufactured parts where, additionally, variations in material properties can occur locally and should also be examined. T2 - 2nd International Symposium on Notch Mechanics (2nd ISNM) CY - Madrid, Spain DA - 03.09.2020 KW - miniature specimens; FCGR curves; intrinsic threshold PY - 2021 SP - 1 EP - 2 AN - OPUS4-55242 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scharf-Wildenhain, R. A1 - Hälsig, A. A1 - Hensel, J. A1 - Wandtke, Karsten A1 - Schröpfer, Dirk A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Einfluss von Wärmeführung und Bauteildesign auf die Eigenschaften und fertigungsbedingten Beanspruchungen additiv geschweißter hochfester Feinkornbaustähle N2 - Hochfeste Feinkornbaustähle verfügen über großes Potenzial für gewichtsoptimierte, effiziente Strukturen in vielen modernen Stahlkonstruktion. Weitere Effizienzsteigerungen können durch additives Fertigen sowie bionische Bauweisen erreicht werden. Hochfeste Zusatzwerkstoffe für additives MSG-Schweißen (engl.: Wire Arc Additive Manufacturing, WAAM) sind bereits von den Schweißzusatzherstellern lieferbar. Eine breite industrielle Anwendung insbesondere für KMU ist aufgrund fehlender quantitativer Erkenntnisse und Richtlinien bezüglich schweißbedingter Beanspruchungen und Bauteilsicherheit während der Herstellung und des Betriebs derzeit stark limitiert. In einem gemeinsamen Forschungsprojekt (FOSTA-P1380/IGF21162BG) der BAM und der TU Chemnitz werden daher die mit Eigenspannungsausbildung und der Gefahr einer Kaltrissbildung verbundenen prozess- und werkstoffbedingten sowie konstruktiven Einflüsse beim WAAM hochfester Stähle untersucht. Der vorliegende Beitrag fokussiert die Analyse der Auswirkungen von Schweißwärmeführung und Design der WAAM-Bauteile auf die Abkühlbedingungen, Gefüge, mechanisch-technologischen Eigenschaften und Eigenspannungen. Hierfür werden geometrisch definierte Probenkörper (Hohlquader) vollautomatisiert mit einem speziellen, hochfesten WAAM-Massivdraht (Streckgrenze >790 MPa) geschweißt. Die Wärmeführung und Probenabmessungen werden innerhalb eines statistischen Versuchsplans variiert. Die Schweißwärmeführung wird dabei so eingestellt, dass die t8/5-Abkühlzeiten im empfohlenen Verarbeitungsbereich (ca. 5 s bis 20 s) sichergestellt sind. Hierzu ließen sich über zusätzliche thermo-physikalische Umformsimulationen mittels Dilatometer die komplexen Wärmezyklen abbilden und die resultierende Zugfestigkeit des Schweißgutes bestimmen. Das WAAM-Schweißen komplexer Geometrien mit variierenden Schweißwärmeführungen und geometrischen Verhältnissen bzw. Wanddicken bedingt neben den Auswirkungen auf die Abkühlbedingungen, Abkühlzeiten und Gefüge deutliche Einflüsse auf die konstruktiven Steifigkeitsverhältnisse beim Schweißen. Es zeigen sich anhand der Schweißexperimente signifikante Auswirkungen durch Probenskalierung und Wärmeeinbringung auf die resultierenden lokalen Eigenspannungen. Die Folge können ungünstige Bauteileigenschaften und risskritische Zugeigenspannungen sein. T2 - DVS Congress 2022 CY - Koblenz, Germany DA - 19.09.2022 KW - MAG-Schweißen KW - Additive Fertigung KW - Eigenspannungen KW - Hochfester Stahl KW - Kaltrisssicherheit KW - Wärmeführung KW - Windenergie PY - 2022 SN - 978-3-96144-189-1 VL - 382 SP - 737 EP - 745 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-56719 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Becker, Amadeus A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas A1 - Michael, Thomas T1 - Konstruktive Einflüsse bei der beanspruchungsgerechten Reparatur geschweißter Bauteile aus hochfesten Feinkornbaustählen N2 - Für eine nachhaltige und ressourceneffiziente Fertigung von Windkraftanlagen ist der Einsatz moderner hochfester Feinkornbaustähle vielfach notwendig. Bei der Montage hochfester Stahlkonstruktionen kommt es trotz anforderungsgerechter schweißtechnischer Fertigung vereinzelt zur Detektion von unzulässigen Unregelmäßigkeiten im Schweißbereich. Derzeitige Normen und Verarbeitungsrichtlinien geben hierbei kaum Informationen zu adäquaten Reparaturkonzepten, insbesondere für hochfeste Stähle. Vor diesem Hintergrund werden an der Bundesanstalt für Materialforschung und -prüfung (BAM) bauteilrelevante Untersuchungen zu den schweißbedingten Beanspruchungen und Gefügeveränderungen bei der schweißtechnischen Reparatur durch lokales thermisches Ausfugen und erneutes Schweißen durchgeführt. Hierzu werden einige wesentliche Ergebnisse an Beispielen des Ingenieurbaus, mit Blick auf die mechanisch-technologischen Eigenschaften und Eigenspannungen erörtert. In einem aktuellen Vorhaben (FOSTA P1311, IGF 20162N) sind darauf aufbauend die Einflüsse durch die Schrumpfbehinderung und Wärmeführung beim Reparaturschweißen hochfester Feinkornbaustähle (S500MLO, S960QL) sowie die Reparaturzyklenanzahl Fokus systematischer Untersuchungen. Mittels strukturmechanischer Berechnungen ließen sich hierzu selbstbeanspruchende Probenformen identifizieren, die unterschiedliche definierte Steifigkeitsverhältnisse von Reparaturschweißnähten realer Bauteile abbilden. Schweißnähte an diesen bauteilähnlichen Proben weisen signifikant erhöhte schweißbedingte Beanspruchungen mit zunehmenden (Biege-)Einspanngraden auf. Im Vergleich mit bisherigen Erkenntnissen wird gezeigt, dass eine sichere Reparatur solcher Schweißnähte nur mittels optimaler Reparaturkonzepte und Wärmeführung gelingt, um diesen hohen Beanspruchungen und auch den speziellen Gefügen hochfester Stähle Rechnung zu tragen. Ziel der Untersuchungen ist es letztlich, Empfehlungen für beanspruchungs- und werkstoffgerechte Reparaturkonzepte gerade für KMU abzuleiten, um Schäden und zumeist teure Nacharbeiten zu vermeiden. T2 - 4. Niedersächsisches Symposium Materialtechnik CY - Online meeting DA - 25.02.2021 KW - Eigenspannungen KW - Gefügedegradation KW - Hochfester Feinkornbaustahl KW - Reparatur KW - Schweißen PY - 2021 SN - 978-3-8440-8021-6 SN - 2364-0804 VL - 10 SP - 488 EP - 501 PB - Shaker Verlag CY - Düren AN - OPUS4-53315 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eissel, A. A1 - Treutler, K. A1 - Wesling, V. A1 - Engelking, Lorenz A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas T1 - Modifikation von CoCr-Legierungen für die additive lichtbogenbasierte Fertigung N2 - Für Komponenten im Turbinen- oder Anlagenbau werden aufgrund ihrer Eigenschaften häufig Kobalt-Chrom-Legierungen verwendet. Diese weisen eine hohe Korrosionsbeständigkeit und hohen Verschleißwiederstand auf. Aufgrund der komplexen Strukturen und dem Bestreben nach Ressourceneffizienz wird zur Herstellung der Komponenten die additive Fertigung verwendet. Hierbei sind hinsichtlich der Inhomogenität und Anisotropie der Gefüge und deren Eigenschaften weitere Kenntnisse notwendig. Bei den vorliegenden Belastungen liegt ein erhöhter Anspruch an die Oberflächenintegrität vor, welcher durch komplementären Einsatz von additiven und abtragenden Fertigungsschritten sichergestellt wird. Dabei sind gerade Co-Cr-Legierungen wegen der niedrigen Wärmeleitfähigkeit verbunden mit hoher Festigkeit und Zähigkeit äußerst herausfordernd mit Blick auf eine wirtschaftliche Zerspanung mit geometrisch bestimmter Schneide. Ausgehend von dieser Problemstellung erfolgt im Zuge eines Gemeinschaftsvorhabens des ISAF in Kooperation mit der BAM eine gezielte Beeinflussung des Gefüges. Ziel des Projektes ist die Zusammenhänge zwischen verschiedenen Legierungsmodifikationen, der entstehenden Gefügemorphologie und den Zerspanungseigenschaften von Co- Cr-Legierungen für die additive Fertigung mittels PTA darzustellen. Der Fokus liegt auf dem Beheben der bestehenden Nachteile bei gleichzeitigem Aufrechthalten der besonderen Eigenschaften der Legierung. Durch das Hinzulegieren von variierenden Gehalten von Zirkonium und Hafnium wird die Gefügeveränderung eingestellt. Es hat sich gezeigt, dass Hafnium als zusätzliches Legierungselement einen deutlichen Einfluss auf die Gefügemorphologie hat. Darüber hinaus wird die Auswirkung der Legierungsmodifikation auf die Härte und die Zerspanbarkeit dargestellt. T2 - 42. Assistentenseminar der Wissenschaftlichen Gesellschaft Fügetechnik e.V. CY - Blankenau, Germany DA - 06.10.2021 KW - Legierungsmodifikation KW - ultraschallunterstütztes Fräsen KW - Additive Fertigung PY - 2022 SN - 978-3-96144-210-2 VL - 385 SP - 103 EP - 113 PB - DVS Media GmbH AN - OPUS4-56658 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Engelking, Lorenz A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas A1 - Eissel, A. A1 - Treutler, K. A1 - Wesling, V. T1 - Herstellung beanspruchungsgerechter Oberflächen durch Kombination innovativer additiver und abtragender Fertigungsschritte an hochbelasteten Komponenten N2 - Die additive Fertigung (AM) durch schweißtechnische Verfahren eröffnet vielfach ökonomische Vorteile für eine ressour-ceneffiziente Bauteilherstellung. Gerade hinsichtlich der Homogenität und Anisotropie der resultierenden Schweißgefüge und den damit verbundenen Eigenschaften gibt es noch offene Fragestellungen. Die Einstellung der finalen Bauteilgeo-metrie und Oberflächengüte erfordert den komplementären Einsatz abtragender Fertigungsschritte. Hochleistungslegie-rungen auf der Basis von Nickel oder Kobalt sind aufgrund ihrer niedrigen Wärmeleitfähigkeit verbunden mit hoher Festigkeit und Zähigkeit schwer spanbar. Eine gezielte Gefügebeeinflussung mittels Modifikation der AM-Schweißzusatz-werkstoffe und der Einsatz des ultraschallunterstützten Fräsens (US) bietet das Potential insgesamt die Zerspanungssi-tuation zu verbessern. Dieser Lösungsansatz unter Gewährleistung des Erhalts der geforderten Werkstoff- bzw. Bauteileigenschaften ist Untersuchungsgegenstand eines Gemeinschaftsvorhabens (IGF-Nr. 20.979 N/DVS-Nr. 1.3211) der BAM und TU Clausthal/ISAF. Der vorliegende Beitrag stellt Ergebnisse für die beiden untersuchten FeNi- und CoCr-Legierungen sowie wesentliche Zusammenhänge zwischen Legierungsmodifikation, entstehender Gefügemorphologie und Zerspanungseigenschaften der mittels MAG additiv gefertigter Proben vor. Das größte Potential für die Modifikation zeigten Zr und Hf. Die Zulegierung in das Schweißgut erfolgte durch Beschichtung von Massivdrähten sowie durch Her-stellung von Fülldrähten. T2 - DVS Congress - GST CY - Essen, Germany DA - 11.09.2023 KW - Legierungsmodifikation KW - Ultraschallunterstütztes Fräsen KW - Additive Fertigung KW - Oberflächenintegrität PY - 2023 SN - 978-3-96144-230-0 VL - 389 SP - 697 EP - 703 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-58380 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Kannengießer, Thomas A1 - Mente, Tobias T1 - Zuverlässige Wasserstoff Bestimmung in Metallen und ihren Schweißverbindungen: Parameter, Einflüsse, Grenzen N2 - Im Zuge der wasserstoffbasierten Energiewirtschaft von morgen, kommt der Errichtung der dementsprechenden Infrastruktur die zentrale Rolle zu. Der überwiegende Teil bisher eingesetzter und meist geschweißter Werkstoffe, wie Stähle, kann unter bestimmten Bedingungen zur Wasserstoffversprödung neigen. Dies umfasst die klassische verzögerte Kaltrissbildung während der Schweißverarbeitung als auch Versprödungsphänomene während des Betriebs. Für die Bewertung eines jeden Wasserstoffeffektes auf bspw. die mechanischen Eigenschaften eines geschweißten metallischen Werkstoffes, muss der Wasserstoffgehalt präzise bestimmt werden, Im Fall von Schweißnähten ist die beispielsweise nach der ISO 3690, die klassische isotherme Trägergas-Heißextraktion (TGHE). Die TGHE basiert dabei auf der beschleunigten Wasserstoffentgasung aufgrund der thermischen Aktivierung des Wasserstoffs bei erhöhten Temperaturen. Neben der reinen Quantifizierung des Wasserstoffs, kann über die thermische Desorptionsanalyse (TDA) mit variierten Heizraten, der Bindungszustand an mikrostrukturellen Defekten im Material festgestellt und bewertet werden. Für beide Techniken sind experimentelle und messtechnische Einflüsse zu beachten, die großen Effekt auf das Ergebnis haben. Für die TGHE schlägt die ISO 3690 schlägt beispielswiese verschiedene Probengeometrien sowie Mindestextraktionszeiten vor. Die vorliegende Studie fasst Ergebnisse und Erfahrungen zahlreicher Untersuchungen an der Bundesanstalt für Materialforschung und -prüfung (BAM) mit unterschiedlichen Probentemperaturen und Geometrien (ISO 3690 Typ B und zylindrische TDA-Proben) zusammen hinsichtlich: Einfluss der Probenoberfläche (poliert/geschweißt), Messgenauigkeiten in Abhängigkeit des Probenvolumens sowie die unzureichende Überwachung des Effektes des PI-Reglers auf die Extraktionstemperatur. Insbesondere eine abweichende Extraktionstemperatur zur eingestellten Temperatur, kann die Messergebnisse wesentlich verfälschen. Basierend auf den Ergebnissen werden Methoden aufgezeigt, um schnell die gewünschte Extraktionstemperatur zu erreichen, ohne physisch in das Messequipment eingreifen zu müssen. Dies dient der wesentlichen Verbesserung der Zuverlässigkeit der Wasserstoffmessung durch erhöhte Signalstabilität und beschleunigte Wasserstoffdesorption. Im Allgemeinen ist eine unabhängige Temperaturmessung mit Dummy-Proben für die gewählte Heizprozedur angeraten, um mögliche unerwünschte Temperatureinflüsse bereits vor der Messung auszuschließen. Die beschriebenen Methoden können ohne großen Aufwand direkt in die industrielle Anwendung überführt werden. T2 - DVS Congress 2023 CY - Essen, Germany DA - 11.09.2023 KW - Wasserstoff KW - Schweißen KW - Forschung KW - ISO 3690 PY - 2023 SN - 978-3-96144-230-0 VL - 389 SP - 435 EP - 442 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-58309 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Kannengießer, Thomas A1 - Schaupp, Thomas ED - Brockmann, S. ED - Krupp, U. T1 - Wasserstoffunterstützte Kaltrissbildung in Schweißnähten hochfester Stahlgüten - Anforderungen an die Prüfung N2 - Wasserstoff kann eine Rissbildung u.U. auch noch nach Tagen in der Schweißnaht bewirken. Dabei stellen höherfeste Stähle etablierte Kaltrissprüftests vor Herausforderungen. Generell nimmt die zur Rissvermeidung tolerierbare Wasserstoffkonzentration mit zunehmender Festigkeit der Werkstoffe ab. Zudem verändern weiterentwickelte Schweißverfahren die Nahtgeometrie und Wärmeeinbringung und die Ausbildung risskritischer Mikrostrukturen (z.B. Wärmeeinflusszone). Am Beispiel des Implant- und Tekken-Tests werden die Einsatz- u. Anwendungsgrenzen bewertet. Zu berücksichtigen ist, dass beim Schweißen eine äußere mechan. Beanspruchung durch bauteilspezifische Steifigkeitsverhältnisse wirksam ist. Zusätzlich werden weiterführende Prüfverfahren zur Bestimmung der Wasserstoffkonzentration und -diffusion in Schweißnähten vorgestellt, wie die Trägergasheißextraktion (TGHE) für die Ermittlung der Wasserstoffkonzentration (ISO 3690) oder Hochtemperaturdiffusionskoeffizienten. Diese Werte sind für die schweißtechnische Praxis von großer Bedeutung, um Haltezeiten z.B. für das Wasserstoffarmglühen abzuleiten. T2 - Tagung Werkstoffprüfung 2021 CY - Online meeting DA - 02.12.2021 KW - Wasserstoff KW - Kaltrissprüfung KW - Schweißen KW - Stahl KW - Hochfest PY - 2021 SN - 978-3-941269-98-9 SP - 15 EP - 20 PB - Stahlinstitut VDEh CY - Düsseldorf AN - OPUS4-53900 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kaiser, Sebastian A1 - Erxleben, Kjell A1 - Rhode, Michael A1 - Kannengießer, Thomas T1 - Repair Welding of In-Service Hydrogen Pipelines - Concepts and Challenges N2 - Hydrogen is set as the energy carrier of tomorrow for a more sustainable fossil fuel free future. As this necessitates a reliable transport infrastructure, repurposing of the existing natural gas grid is planned. With regards to the well-known effect of hydrogen embrittlement, the compatibility of utilized materials must be investigated. First comprehensive studies on pipeline material hydrogen compatibility indicate that these materials can be applied to a certain extent. Nonetheless, the material compatibility is currently of high interest and focus of numerous research projects worldwide. However, pipelines require frequent maintenance and repair work. As part of these, in some cases it is necessary to do weldments onto pipelines while they are pressurized. This in-service welding introduces additional challenges for the material compatibility. Due to the resulting high temperatures, the metallurgical changes in the material and of course the presence of high-pressure hydrogen in the pipeline, additional investigations need to be conducted to ensure that no critical material degradation because of increased hydrogen absorption occurs and an overall material compatibility is given. For this reason, the present paper introduces in-service welding on pipelines. An overview of current research projects that deal with the application of in-service welding specifically on hydrogen pipelines and the emerging problems when applying these techniques on hydrogen pipelines is given. Methods of material testing, their limits and possible solutions are presented and discussed. T2 - 2024 15th International Pipeline Conference CY - Calgary, Alberta, Canada DA - 23.09.2024 KW - Hydrogen KW - Pipeline KW - Welding KW - In-Service PY - 2024 SN - 978-0-7918-8856-8 DO - https://doi.org/10.1115/IPC2024-133052 SP - 1 EP - 6 PB - The American Society of Mechanical Engineers (ASME) CY - New York AN - OPUS4-62262 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Straße, Anne A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Nahteigenschaftsverbesserung von dickwandigen laserstrahlgeschweißten Duplexblechen mittels pulveraufgetragenen Pufferschichten N2 - Duplexstähle finden aufgrund ihrer Eigenschaften, wie der guten Korrosionsbeständigkeit, einer hohen Festigkeit bei gleichzeitig guter Duktilität häufig industrielle Anwendung. Durch die hohen Abkühlraten beim Laserstrahlschweißen weisen Schweißnähte jedoch anstelle eines ausgeglichenen Duplexgefüges einen deutlich erhöhten Ferritanteil, im Vergleich zum Basiswerkstoff, auf. Dies führt zu einer verringerten Duktilität sowie Korrosionsbeständigkeit. Um dieses Problem zu lösen, wurde ein Prozess entwickelt, der auf einer Kantenbeschichtung mit nickelhaltigem Zusatzmaterial der zu fügenden Bleche mittels Laser-Pulver-Auftragschweißen (LPA) basiert. Die resultierenden Schweißnähte wurden zerstörend anhand von Schliffbildern, EDX-Aufnahmen, Härtemessungen und Kerbschlagbiegeversuchen geprüft. T2 - 40. Assistentenseminar der Füge- und Schweißtechnik CY - Braunlage, Germany DA - 25.09.2019 KW - Laser-Pulver-Auftragschweißen; Laserstrahlschweißen, Duplex, Pufferschichten PY - 2020 VL - 357 SP - 131 EP - 140 PB - DVS Media CY - Düsseldorf AN - OPUS4-50144 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Straße, Anne A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Quality improvement of laser welds on thick duplex plates by laser cladded buttering N2 - Because of its excellent corrosion resistance, high tensile strength and high ductility, duplex stainless steel 2205 offers many areas of application. Though laser beam welding accompanied by high cooling rates, duplex steels tend to perform higher ferrite contents in weld metal as the base metal, which leads to a reduction of ductility and corrosion resistance of the weld joint. To overcome this problem, a solution, based on buttering the plate edges by laser metal deposition (LMD) with material containing higher Ni concentrations prior to laser welding was suggested. In this context different process parameters for LMD process were investigated. In a second step the possibility of welding those edges defect free while achieving balanced austenite-ferrite ratio was verified with metallographic analysis, Electron Backscatter Diffraction (EBSD) and impact testing according to Charpy. T2 - Lasers in Manufacturing (LiM) 2019 CY - Munich, Germany DA - 24.06.2019 KW - Laser Metal Deposition; Laser Beam Welding; Duplex; Stainless Steel PY - 2020 SP - We_A31_4_4-1 EP - We_A31_4_4-6 PB - WLT (Wissenschaftliche Gesellschaft für Lasertechnik) AN - OPUS4-50143 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Putra, Stephen Nugraha A1 - Meng, Xiangmeng A1 - Yang, Fan A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Einfluss der temperaturabhängigen Modellierung der Laserstrahlabsorption auf die Schmelzbadgeometrie beim Hochleistungslaserstrahlschweißen N2 - Der Absorptionsgrad metallischer Werkstoffe spielt bei Fügeprozessen mit einer Strahlungsquelle wie dem Hochleistungslaserstrahltiefschweißen eine bedeutende Rolle. Dieser beeinflusst die Menge der absorbierten Laserenergie, welche zum Aufschmelzen sowie zur lokalen Verdampfung des zu verbindenden Materials führt. Die Laserstrahlabsorption wird von vielen physikalischen Faktoren, z.B. Laserprofil, Laserwellenlänge, Materialeigenschaft sowie Temperatur, entschieden. Dennoch wird die Temperaturabhängigkeit in vielen Simulationsarbeiten häufig ignoriert und stattdessen ein empirisch angepasster Parameter zur Kalibrierung der Ergebnisse implementiert. Diese Vorgehensweise wirkt sich negativ auf die Zuverlässigkeit des numerischen Modells sowie auf die Vorhersagbarkeit der Simulationsergebnisse aus. In der vorliegenden Arbeit wird die Temperaturabhängigkeit des Laserabsorptionsgrades in ein selbstkonsistentes zweiphasiges Modell unter Berücksichtigung der gekoppelten 3D-Fluidströmung und Wärmeübertragung einbezogen. Die berechnete Laserstrahlabsorption wird durch die temperaturabhängigen Materialeigenschaften, die Lasercharakteristik und den Einfallswinkel des Laserstrahls bestimmt. Die freie Oberfläche jeder Phase wird mithilfe der Volume-of-Fluid Methode (VOF), berechnet und die Laser-Material-Wechselwirkung wird durch ein implementiertes Ray-Tracing-Verfahren modelliert, welches auf einem lokalisierten Level-Set-Algorithmus basiert. Anschließend wird die transiente Wärmeeinbringung und die Geometrie der Schweißnaht analysiert und mit dem temperaturunabhängigen Absorptionsmodell verglichen. Es wurde festgestellt, dass die Temperaturabhängigkeit der Laserabsorption entscheidend für die genaue Bestimmung der Wärmeeinbringung und der Schmelzbadgeometrie ist. Das entwickelte Modell wurde anhand der experimentellen Untersuchungen validiert und die Bedeutung der Temperaturabhängigkeit bei der Laserstrahlabsorption wurde für die Simulation des Laserstrahltiefschweißens quantifiziert. T2 - 44. Assistentenseminar Füge- und Schweißtechnik CY - Päwesin, Germany DA - 20.09.2023 KW - Laser beam welding KW - Numerical modeling KW - Ray tracing method KW - Weld pool dynamics PY - 2024 UR - https://www.dvs-media.eu/de/neuerscheinungen/4671/44.-assistentenseminar-fuegetechnik SN - 978-3-96144-267-6 VL - 394 SP - 57 EP - 68 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-60779 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - John, Sebastian A1 - Duffner, Eric A1 - Mair, Georg W. T1 - Degradation and damage analysis of composite pressure vessels via experimental modal analysis N2 - For mobile gas storage systems, the application of type IV pressure vessels is state of the art. Type IV tanks consist of an inner polymer liner fully wrapped with fibre-reinforced plastic (FRP). Because of the complex fabric of the FRP as well as a difficulty estimable interaction behaviour between the single components under load, there are still no satisfying non-destructive testing methods to assess the current state of failure nor to estimate the level of degradation accurately and economically. At BAM division 3.5, analysing the ageing process of mobile composite pressure vessels is a major task to ensure safe usage over the whole lifetime. In this context, key aspects of our ongoing research activities are the invention of new test procedures and the development of accurate lifetime prediction models. In order to determine the level of degradation or damage, one meaningful non-destructive approach is to analyse the structural dynamic behaviour via an experimental modal analysis (EMA). Over the last few years, different types and sizes of composite pressure vessels have been tested in several research projects. The presented paper gives an insight into how to extract and interpret modal parameters and how to fit them to the results of residual strength tests. T2 - NOVEM Conference 2023 CY - Auckland, New Zealand DA - 09.01.2023 KW - Composite material KW - Pressure vessel KW - Degradation KW - Modal analysis PY - 2023 SP - 57-1 EP - 57-6 AN - OPUS4-58062 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Yang, Fan A1 - Meng, Xiangmeng A1 - Putra, Stephen Nugraha A1 - Artinov, Antoni A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Numerical analysis of the effect of the metal vapor plume on the keyhole and the molten pool behavior during deep penetration laser beam welding N2 - The effect of the oscillating metal vapor plume on the keyhole and molten pool behavior during the laser beam welding of AlMg3 aluminum alloys is investigated by the experimental and numerical method. The real-time height of the metal vapor plume is measured by high-speed camera observation. The obtained experimental results are used to evaluate the additional heating source and laser beam attenuation caused by the scattering and absorption based on the Beer-Lambert theory. Furthermore, the dynamic behavior of the metal vapor plume is incorporated into a 3D transient heat transfer and fluid flow model, coupled with the ray tracing method, for the laser beam welding of the AlMg3 alloy. It is found that the additional heating resulting from the scattered and absorbed laser beam energy by the metal vapor plume significantly expands the shape of the molten pool on the top region. Moreover, the oscillating metal vapor plume caused the fluctuation of the molten pool shape. The probability of keyhole collapse at the bottom increases significantly to 72% due to the oscillating laser power induced by the laser beam attenuation. The internal interplay between the metal vapor plume, molten pool shape, and the keyhole collapse are obtained. The developed model has been validated by the experiments, which shows a good agreement. T2 - International Congress of Applications of Lasers & Electro-Optics 2023 CY - Chicago, Illinois, USA DA - 16.10.2023 KW - Deep penetration laser beam welding KW - Numerical simulation KW - Oscillating vapor plume KW - Keyhole collapse PY - 2023 SP - 1 EP - 10 AN - OPUS4-58841 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Chaudhuri, Somsubhro A1 - Purayil, Sruthi Krishna Kunji A1 - Kruse, Julius A1 - Madia, Mauro A1 - Nielsen, Sören T1 - Thermography-Assisted Mechanical Testing of Cold-Spray (AM) Repair N2 - Cold Spray Additive Manufacturing (CSAM) is a solid-state process that is being increasingly used for structural repairs in aerospace and energy sectors. It enables the deposition of dense material at low temperatures by accelerating metal particles to supersonic velocities, thereby reducing thermal distortion. However, the structural integrity of CSAM repairs—particularly at the interface between the deposited layer and the substrate—remains a critical concern. Various post-treatments and characterization methods have been explored to optimize performance. While X-ray Computed Tomography (XCT) is effective for sub-surface inspection, it cannot be applied in situ during mechanical testing. Digital Image Correlation (DIC), a surface-based method, also lacks sub-surface sensitivity. To address this, Infrared Thermography (IRT) was employed alongside DIC during the tensile and fatigue testing of aluminum CSAM-repaired specimens. A cooled IRT camera operating at 200 FPS captured thermal data, with lock-in processing subsequently applied in post-processing. IRT successfully detected early interfacial damage and enabled the tracking of crack propagation, which was later confirmed through fracture surface analysis. This extended abstract presents findings from fatigue tests using IRT. T2 - 18th International Workshop on Advanced Infrared Technology and Applications (AITA 2025) CY - Kobe, Japan DA - 15.09.2025 KW - Thermography KW - Thermografie KW - Thermal stress analysis KW - Cold spray KW - Damage detection PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-642299 DO - https://doi.org/10.3390/proceedings2025129018 VL - 129 IS - 1 SP - 1 EP - 5 PB - MDPI CY - Basel AN - OPUS4-64229 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bauer, J. A1 - Miclea, P.-T. A1 - Braun, U. A1 - Altmann, Korinna A1 - Turek, M. A1 - Hagendorf, C. T1 - Microplastic detection and analysis in water samples N2 - Microplastic detection in water samples becomes important for tracing microplastic sources. Microplastic may harm desalination facilities by blocking filters and disturbing the marine food chain. Thermo analytical methods such as pyrolysis gas chromatography mass spectroscopy, and spectroscopic methods like (micro) Raman spectroscopy or (micro) Fouriertransform infrared spectroscopy in combination with appropriate filters and sample preparation are suitable for analyzing microplastics on a scale from 1 µm to 1000 µm fast and unambiguous. While the thermo analytical methods are suitable for larger sample volumes, Raman spectroscopy and Fouriertransform infrared spectroscopy are able to detect and analyze single microplastic particles for instance in bottled water. Machine learning algorithms ensure a reliable classification of different plastic materials. T2 - International Conference on Sustainable Energy-Water-Environment Nexus in Desert Climate 2019 CY - Ar-Rayyan, Qatar DA - 02.12.2019 KW - Microplastics KW - Water samples PY - 2022 SP - 111 EP - 113 PB - Springer AN - OPUS4-56240 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Visileanu, Emilia A1 - Catalin Grosu, Marian A1 - Tiberiu Miclea, Paul A1 - Altmann, Korinna A1 - Brossell, Dirk T1 - Methods for the collection and characterization of airborne particles in the textile industry N2 - Airborne particulate matter is one of the main air pollutants. Their impact on mortality, and the occurrence of pulmonary and cardiovascular complications, have been the subject of numerous studies. Airborne particles are complex mixtures of organic and inorganic substances from different sources of particle emissions. Particulate Matter (PM) particles are classified according to their aerodynamic diameter expressed in µm and can vary from coarse (PM 10) to fine (less than PM 2.5). These diameter considerations are fundamental because they condition the penetration of particles into the bronchopulmonary system and the body. In recent years, there has been an interest in so-called “ultra-fine” particles, with a diameter of 0.1 µm (or 100 nm), or PM 0.1. They are nanoparticles and their impact on human health is not yet clear.With more than 1.5 million employees, textiles and clothing is a diverse sector that plays an important role in the European manufacturing industry, producing a turnover of €162 billion.An important component of the solid particles that generate air pollution in the textile industry is microplastics (MP) and nano plastics (NP), which also include microfibers (<5mm) and nanofibers (<100 nm), respectively. The particles released into the air during fiber and yarn processing range from 1 µg/m3 to 50 µg/m3.The paper presents the results of the determination of indoor and outdoor air concentration levels in textile companies, to identify the areas with the highest concentration level, by using an online recording system such as the Laser Aerosol Spectrometer MINI LAS model 11-E. The total concentration level TSP (µg/m3), the fractions PM 10(µg/m3), PM 2.5(µg/m3), PM1(µg/m3), as well as the total number of particles TC (1/l), were shown. It was noted that TSP is approximately at the same level both indoors and outdoors, but the fractions of PM10, PM2.5, and PM1 have much higher values indoors than outdoors with possible consequences on workers' health.The next step was the collection of fibers, namely micro and nano plastic particles from the vicinity of the workplaces of polyester, polyamide, and polypropylene fibers processing units in the textile industry in Romania, to obtain a sufficient quantity for laboratory analysis to determine the size and shape of the particles as well as their chemical composition. Two types of pumps were used, differentiated by their operating parameters: TECORA SKYPOST with airflow of 38 l/min and GILAIRPLUS with airflow 2l/min. Filters made of different materials with different diameters and pore sizes were used, namely: quartz filters (ø 47 mm, and ø 37 mm) on a TECORA SKYPOST type pump, polycarbonate nucleopore coated with a gold membrane (ø 25 mm) and silica filter (ø 9 mm) on GILAIRPLUS type pump.Using descriptive statistics, the calculation of correlation coefficients highlighted a strong correlation between the variables: "Collected mass/ Air concentration" and "Collected mass/ Air volume" for all diameters of the filters.The highest collected particle volume, determined by weighing the filters before and after collection, was obtained with the quartz filters (ø 47 mm) at an airflow of 38 l/min. The particles collected (polyester, polyamide, polypropylene) in the first stage were analyzed by SEM and thermogravimetric and it was found that the quartz filters absorbed the particles inside, with very few remaining on the surface. Thus no known methods can be used to perform analysis for particles collected on quartz filters. The number of particles on the filters was insufficient for analysis either because of the collection parameters used or because of the loss of particles during transport. As a result, in the next step, the use of 9 mm Si filters using the GILAIRPLUS pump at an airflow rate of 2l/min was chosen.To improve the transport conditions and avoid the loss of the particles and keep them on the surface of the filters, two methods were applied:- after weighing the filters were reintroduced into the collection pump holder;- a filtration system for airborne micro-nano plastics was designed and manufactured to selectively collect and transport PM10 and PM1 particles collected on SI filters.In both cases, SEM, Raman mapping, and GS-MS microscopy were used for analysis.Several times more PM10 than PM1 (74.5µg compared to 12.5 µg) was found. In all cases, both particles and fibers showed the same Raman fingerprint.The GS-MS analyses showed some contamination of the workspaces with particles other than the processed fibers. The presence of non-notifiable substances was also observed.The most viable filters are Si filters with a pore size of 10 microns to 1 micron and the use of the selected collection and transport filter system. In the following a filter system will be applied for collection on Au membrane-coated polycarbonate filters. T2 - 5th International Conference on Human Systems Engineering and Design: Future Trends and Applications (IHSED 2023) KW - Microplastics KW - Textiles PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-624442 DO - https://doi.org/10.54941/ahfe1004132 VL - 112 SP - 212 EP - 223 PB - AHFE International AN - OPUS4-62444 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Erxleben, Kjell A1 - Richter, Tim A1 - Schröpfer, Dirk T1 - Charakterisierung der WIG und FSW-Mischverbindungen neuartiger Multielement-Legierungen mit einem austenitischen Stahl N2 - Multielement-Legierungen (MPEA - Multiple Principal Element Alloys), gemeinhin und partiell fälschlicherweise auch als Hochentropielegierungen bezeichnet) stellen eine neue Klasse von Werkstoffen dar, die aus mindestens drei Legierungselementen mit jeweils 5 bis 35 Atom-% bestehen. Somit unterscheidet sich dieses Legierungskonzept fundamental von konventionellen Werkstoffen wie Stahl oder Nickellegierungen. Hierzu werden die Legierungselemente gezielt ausgewählt und die Mikrostrukturen ein- und zum Teil auch mehrphasig eingestellt. Das Ziel ist dabei, hochinnovative MPEA mit individuell einstellbaren Eigenschaften für die industrielle Anwendung zu identifizieren. Dabei werden insbesondere Zielkonflikte, wie bspw. der Trade-off zwischen Festigkeit und Duktilität bei konventionellen Stählen, überwunden. Insbesondere die hohe mechanische Festigkeit bei höchster Korrosionsbeständigkeit sind bei bestimmten Legierungssystemen von hohem Interesse. Hier kann u.a. die Substitution klassischer hochlegierter Stähle oder Ni-Basislegierungen perspektivisch erfolgen. In den letzten 20 Jahren lag der Fokus jedoch auf der reinen Materialsynthese. Mit der Zunahme verfügbarer Werkstoffquantitäten, stehen Verarbeitungsfragen, wie werkstoff- und beanspruchungsgerechte Füge- bzw. Schweißverfahren jetzt im Mittelpunkt. Der Schweißeignung von MPEA wurde bisher nur äußert wenig Aufmerksamkeit zuteil. Erfahrungen zu Mischverbindungen (DMWs - Dissimilar Metal Welds) fehlen dabei vollständig, sind jedoch essenziell für die Anwendung dieser Werkstoffe in Verbindung mit konventionellen Werkstoffen. Die vorliegende Studie präsentiert erstmals im deutschen Sprachraum, die umfassenden experimentellen Ergebnisse zur Schweißeignung von MPEA-Mischverbindungen und der resultierenden Mikrostruktur. Dazu wurden zwei äquiatomare MPEAs in Form einer Co20Cr20Fe20Mn20Ni20 (Hochentropie-) und Co33.3Cr33.3Ni33.3 (Mediumentropielegierung) mittels WIG und Rührreibschweißen mit einem konventionellen, korrosionsbeständigem Cr-Ni-Stahl AISI 304 (1.4301 bzw. X5CrNi18-10) gefügt. Die erstmals untersuchten DMWs resultierten dabei in sehr interessanten Mikrostrukturen, mechanisch-technologische Eigenschaften wurden durch instrumentierte Zugversuche gewonnen, die gleichzeitig der Ermittlung der lokalen Verformung im Schweißnahtbereich dienten (durch Verwendung der berührungslosen DIC-Digital Image Correlation-Technik). Dabei zeigt sich für beide Schweißverfahren eine Erweichung in der Wärmeeinflusszone (WEZ) der MPEAs sowie eine geringfügig verminderte Zugfestigkeit, bei einer deutlichen Abnahme der Bruchdehnung. Durch die Experimente konnte der prinzipielle Nachweis der Schweißeignung der MPEAs für DMWs mit konventionellen Werkstoffen erbracht werden, die auch eine dementsprechende mechanische Beanspruchbarkeit ermöglichen. Dies ermöglicht weitere Betrachtungen zur Anwendung dieser innovativen Werkstoffe. T2 - DVS Congress 2023 CY - Essen, Germany DA - 11.09.2023 KW - Schweißeignung KW - Mischverbindung KW - Hochentropielegierung KW - Multielement-Legierung KW - FSW KW - WIG PY - 2023 SN - 978-3-96144-230-0 VL - 389 SP - 615 EP - 623 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-58352 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Engelking, Lorenz A1 - Eissel, A. A1 - Schröpfer, Dirk A1 - Treutler, K. A1 - Kannengießer, Thomas A1 - Wesling, V. T1 - Effect of alloy modification for additive manufactured Ni alloy components on microstructure and subsequent machining properties N2 - Ni alloys are generally classified as difficult-to-cut materials and cost intensive. Additive manufacturing (AM) offers economic advantages. However, machining of these AM components is mandatory to create the final contour or surface. The inhomogeneous and anisotropic microstructure and properties of AM components causes an unstable cutting process. Moreover, undesirable tensile residual stresses are generated due to subsequent machining. In this investigation, the initial alloy 36 is modified with Ti and Nb up to 1.6 wt.-% and build-up welded via gas metal arc welding (GMAW) and plasma-transferred-arc (PTA). Then, finish-milling tests are carried out to investigate the influence of the modification as well as the cutting parameters on the resulting cutting force and the surface integrity. In addition, the conventional milling process (CM) is compared with the ultrasonic-assisted milling process (US), which has a significant influence on the machinability as well as on the surface integrity. T2 - Additive Fertigung – Werkstoffe – Prozesse – Wärmebehandlung 2022 CY - Bremen, Germany DA - 29.06.2022 KW - Additive manufacturing KW - Alloy 36 KW - Alloy modification KW - Ultrasonic-assisted milling KW - Surface integrity PY - 2022 SP - 57 EP - 67 AN - OPUS4-55430 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erxleben, Kjell A1 - Kaiser, Sebastian A1 - Rhode, Michael A1 - Kannengießer, Thomas A1 - Hadick, C. A1 - Schu, K. T1 - Quantification of hydrogen uptake during in-service hydrogen pipeline welding N2 - Hydrogen must be transported on a large scale from producers to consumers to ensure the energy transition. The necessary pipeline grid is achieved by conversion of the natural gas (NG) grid and building new pipelines. Welding during service as part e.g. of “hot-tapping” is unavoidable for maintenance/repair/expansion. Based on existing studies, the basic material compatibility of (low-alloyed) pipeline steels with hydrogen is postulated. However, this cannot be assumed for the case of in-service welding on pipelines in pressurized condition. The reason is the increased temperature e.g. by preheating and (in particular) during welding of the single passes. As a result, the inner pipeline surface undergoes multiple short-term heating but to high temperatures. In particular, the first passes can result in a temperature close to the austenitic transformation of the material for small wall thicknesses. Both increase the hydrogen uptake into the welded joint. If hydrogen embrittlement is likely to occur, depends on the hydrogen uptake, which must be quantified. For this purpose, welding experiments on pressurized demonstrators were conducted. The hydrogen uptake at 100 bar was compared to reference experiments with nitrogen. A new sample extraction routine for the quantification of the weld-zone specific hydrogen uptake was established. Comprehensive experiments with different steels (P235, L360, L485), wall thicknesses (4.1 mm to 7.8 mm) and diameters (DN50 and DN200) were conducted. In addition, the influence of the welding layer sequence on the hydrogen uptake between single- and multi-layer welds was investigated. Analytical approaches were used to approximate the hydrogen uptake in the respective weld zones. The main findings were that the layer sequence and especially the wall thickness have a large influence on the hydrogen uptake. T2 - 20th Pipeline Technology Conference ptc2025 CY - Berlin, Germany DA - 06.05.2025 KW - In-service KW - Hydrogen KW - Pipeline KW - Repair welding KW - component test PY - 2025 SP - 1 EP - 12 AN - OPUS4-63166 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erxleben, Kjell A1 - Kaiser, Sebastian A1 - Rhode, Michael A1 - Kannengießer, Thomas A1 - Kromm, Arne T1 - Reparaturschweißen zukünftiger, in Betrieb befindlicher Wasserstoffpipelines N2 - Wasserstoff leistet als Energieträger der Zukunft einen entscheidenden Beitrag zur nachhaltigen Energieversorgung, wobei der Transport auf Basis des europäischen Ferngasleitungsnetzes erfolgen wird. Bisherige Untersuchungen zur Werkstoffkompatibilität zeigen, dass die hier verwendeten, niedriglegierten Rohrstähle für Wasserstofftransport unter normalen Betriebsbedingungen (≤ 60 °C, max. 100 bar) grundsätzlich geeignet sind. Die Eignung kann nicht ohne Weiteres übertragen werden, sobald Reparaturschweißungen beispielsweise aufgrund von Wartungsarbeiten an druckführenden, in Betrieb befindlichen, Hochdruckgasleitungen erfolgen. Aus technisch-ökonomischen Gründen werden Schweißarbeiten dabei im Betrieb unter fortwährendem Druck und Gasfluss durchgeführt. Dies soll auch bei Wasserstoffpipelines erfolgen. Dazu im Erdgasnetz angewandte und etablierte Konzepte sind beispielsweise das „Hot-Tapping“ und „Stoppling“. Beim „Hot-Tapping“ wird eine druckführende Pipeline durch Anflanschen eines abgeschlossenen, druckdichten Systems aus Absperrventil und Bohrvorrichtung angebohrt. Dazu müssen sogenannte Überschieber (aus vorgeformten Zylinderhalbschalen) durch Längsnaht verbunden und dann mit Rohrrundnähten am Produktrohr verbunden werden. Für das zum überwiegenden Teil durchgeführte E-Hand-Schweißen sind dabei Vorwärmtemperaturen von ca. 100 °C bzw. 250 °C für die maximale Zwischenlagentemperatur einzuhalten. Besonderer Fokus liegt auf der Betrachtung dünnwandiger Leitungen, da hier beim Schweißen der Rundnähte die Austenitisierungstemperatur an der Innenseite der Pipeline überschritten wird. Dadurch wird eine signifikant höhere Wasserstoffaufnahme in den Leitungsstahl vermutet, mit einer möglichen Degradation der mechanischen Kennwerte bzw. Rissbildung. Durch die langen Schweiß- und Abkühlzeiten wird der Rohrleitungsstahl zudem teilweise stundenlang Temperaturen von bis zu 250 °C ausgesetzt. Neben der klassischen „Versprödung“ muss daher eventuell auch ein sogenannter Hochtemperatur-Wasserstoffangriff betrachtet werden. Diese vorliegende Studie gibt Einblick zur Übertragbarkeit der bekannten Konzepte aus der Erdgastechnik zum Reparaturschweißen. Dazu werden Möglichkeiten und Grenzen momentaner Prüfkonzepte sowie deren Weiterentwicklungen aufgezeigt. Dies umfasst bspw. geeignete Methodiken zur Werkstoffprüfung als auch skalierte Bauteilversuche unter realistischen Druckgas-Betriebsbedingungen einer Pipeline. In diesem Rahmen erfolgt auch die Kurzvorstellung des Kooperationsprojektes von BAM, DVGW und Ferngasnetzbetreibern „H2-SuD“ zum Einfluss der Temperaturführung und Rohrgeometrie auf die Wasserstoffaufnahme. T2 - DVS CONGRESS 2024 CY - Erfurt, Germany DA - 16.09.2024 KW - Reparaturschweißen KW - Pipeline KW - Wasserstoff KW - Im Betrieb PY - 2024 SN - 978-3-96144-269-0 VL - 395 SP - 341 EP - 349 AN - OPUS4-61478 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kaiser, Sebastian A1 - Erxleben, Kjell A1 - Rhode, Michael A1 - Kannengießer, Thomas T1 - Herausforderungen beim Schweißen im Betrieb an Wasserstoff-Ferngasleitungen N2 - Als Energieträger der Zukunft kommt grünem Wasserstoff große Bedeutung bei der Energiewende und der zukünftigen, nachhaltigen Energieversorgung zu Teil. Zum effizienten und sicheren Transport des Wasserstoffs ist die Bereitstellung einer Pipeline-Infrastruktur geplant. Die meisten Länder verfolgen hierbei die Strategie der Umwidmung bestehender Erdgastransportleitungen, ergänzt durch Errichtung neuer Pipelines. Die bestehenden Erdgasnetze sind dabei aus unterschiedlichsten Rohrgeometrien und Materialien zusammengesetzt. Bei der Umwidmung von Erdgaspipelines zum Transport von Wasserstoff müssen daher Fragen der Materialverträglichkeit hinsichtlich des als Wasserstoffversprödung bekannten Phänomens der Beeinträchtigung der mechanischen Eigenschaften metallischer Werkstoffe durch Wasserstoff betrachtet werden. Bisherige Forschungsergebnisse und Feldversuche deuten darauf hin, dass die niedriglegierten, ferritischen Stähle, aus denen die Ferngasleitungen des Erdgasnetzes überwiegend bestehen, für den Transport von Wasserstoff unter normalen Betriebsbedingungen geeignet sind. Eine Frage, die bislang weniger Aufmerksamkeit erhielt, ist die, wie sich das Schweißen im Betrieb an Wasserstoffpipelines auf die Materialkompatibilität auswirkt. Im Erdgasnetz sind etablierte Verfahren wie beispielsweise das „Hot-Tapping“ unumgänglich für die Instandhaltung und Erweiterung des Netzes. Hierbei werden an eine im Betrieb befindliche Pipeline geteilte T-Stücke aufgeschweißt, über die die Pipeline dann mit geeigneten Bohrvorrichtungen während eines ununterbrochenen Betriebs angebohrt werden kann. Um zu beurteilen, ob diese Verfahren gefahrlos auf Wasserstoffpipelines übertragen werden können, müssen Problemstellungen betrachtet werden, die sich durch den Wärmeeintrag ins Material beim Schweißen ergeben. Wasserstofflöslichkeit und Diffusionsgeschwindigkeit sind temperaturabhängig. Erhöhte Temperaturen könnten eine Wasserstoffaufnahme ins Material bewirken, die zu einer kritischen Degradation der mechanischen Eigenschaften des Materials führen könnte. Die Temperaturen, die beim Schweißen erreicht werden, führen lokal zur Überschreitung der Austenitisierungstemperatur. Austenit weist eine deutlich höhere Löslichkeit von Wasserstoff auf, während die Diffusionsgeschwindigkeit des Wasserstoffs in dieser Phase deutlich herabgesetzt ist. Es wird vermutet, dass dies zu einer lokal erhöhten Wasserstoffkonzentration führt. Damit geht ein erhöhtes Risiko einer kritischen Materialdegradation einher. Durch die lange Zeitdauer beim Schweißen von mehrlagigen Rundkehlnähten an großen Pipelines, einschließlich einer möglichen Vorwärmprozedur, ist weiterhin zu klären, ob der aus Anwendungsfällen in der Petrochemie bekannte Hochtemperaturwasserstoffangriff auftritt. Der vorliegende Beitrag liefert einen Überblick über das Schweißen im Betrieb an Gaspipelines, hierbei auftretenden Herausforderungen bei der möglichen Anwendung auf Wasserstoffleitungen. Dabei werden auch aktuelle Forschungsprojekte zum Thema Schweißen an Wasserstoffpipelines im Betrieb eingehend diskutiert. In diesem Zusammenhang werden erste Ergebnisse des gemeinschaftlichen Forschungsprojektes „H2-SuD: Einfluss des Schweißens auf die Wasserstoffaufnahme und Degradation im Betrieb befindlicher H2-Ferngasleitungen“ des Deutschen Vereins des Gas- und Wasserfaches (DVGW), der Bundesanstalt für Materialforschung und -prüfung (BAM) und deutscher Gasnetzbetreiber (Open Grid Europe, ONTRAS Gastransport, u.v.m.) präsentiert. T2 - 53. Sondertagung - Schweißen im Anlagen-und Behälterbau 2025 CY - Munich, Germany DA - 18.03.2025 KW - Materialdegradation KW - Pipeline KW - Schweißen KW - Wasserstoff PY - 2025 SN - 978-3-96144-290-4 (Print) SN - 978-3-96144-291-1 (E-Book) VL - 2025 SP - 106 EP - 115 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-62911 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Kannengießer, Thomas T1 - Schweißen im Wasserstoffanlagen- und Behälterbau - Eine Kurzübersicht N2 - Wasserstoff erfüllt die zentrale Rolle für die Umwandlung der bisherigen fossil-basierten Energieerzeugung und -nutzung auf eine dekarbonisierte, nachhaltige Form. Dazu muss der Wasserstoff erzeugt, gespeichert, transportiert werden, bevor er wieder der Nutzung zugeführt wird. Hierzu sind entlang der gesamtem Prozesskette Wasserstofftechnologien notwendig, die einen sicheren Betrieb erfordern. Hierbei kommt dem schweißtechnischen Anlagen- und Behälterbau wesentliche Bedeutung zu, insbesondere (aber nicht ausschließlich) für Speicherung und Transport des Wasserstoffes. Der vorliegende Beitrag gibt einen kurzen Überblick, wo und wie die konventionelle Schweißtechnik hierzu wichtige Beiträge leistet. Die additive Fertigung, also das „Drucken“ von Bauteilen wird dabei zunehmend wichtiger, entlang der gesamtem Prozesskette der Wasserstofftechnologien. Gleichwohl darf nicht unterschätzt werden, dass auch wesentlicher Bedarf an der Erweiterung und teilweiser Neufassung von bestehenden Regel- und Normenwerken besteht. T2 - 51. Sondertagung "Schweißen im Behälter- und Anlagenbau" CY - Munich, Germany DA - 01.03.2023 KW - Wasserstoff KW - Anlagenbau KW - Schweißen KW - Studie KW - Pipeline PY - 2023 SN - 978-3-96144-219-5 VL - 387 SP - 83 EP - 88 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-57075 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Nina A1 - Kromm, Arne A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas T1 - Innovatives Instandsetzungsschweißen von Altstahl: Materialverhalten und Herausforderungen N2 - Aus Gründen der Nachhaltigkeit und Wirtschaftlichkeit gibt es in der stahlverarbeiten-den Industrie einen Trend zum Bauen im Bestand, um kostenintensive Sperrungen oder Rückbau zu vermeiden. Schweißen wird dabei als wirtschaftliches Fügeverfahren im Zusammenhang mit Altstählen kaum genutzt, obwohl Nieten- und Schraubenverbindungen oft unwirtschaftlich sind. Für die Instandsetzung ist häufig beschädigtes Bestands-material durch neue Stähle zu ersetzen bzw. Alt-Neu-Stahl-Mischverbindungen herzu-stellen. Aufgrund der verschiedenen Herstellungsprozesse von Altstählen ist nicht jeder Stahl aus dem 20. Jahrhundert schweißgeeignet. Daher ist zunächst eine Schweißeignungsprüfung erforderlich. In den vorliegenden Untersuchungen wurden verschiedene Altstähle hinsichtlich ihres Schweißverhaltens mittels Dilatometrie analysiert. Ziel war es, eine Datenbasis aus Schweiß-Zustands-Zeit-Diagrammen und Simulationen der Wärmeeinflusszone zu erstellen, um praxisrelevante Schweißuntersuchungen ableiten zu können. Diese geben wesentlichen Aufschluss hinsichtlich ihres schweißmetallurgischen Verhaltens und ihrer Schweißeignung. Solche Grundlagen sind zur Entwicklung innovativer schweißtechnischer Konzepte zur beanspruchungsgerechten Instandsetzung bestehender Altstahl-Infrastruktur in Deutschland notwendig. T2 - 6. Symposium Materialtechnik, 20. bis 21. Februar 2025 CY - Clausthal-Zellerfeld, Germany DA - 20.02.2025 KW - Altstahl KW - Schweiß-ZTU Diagramme KW - Instandsetzungsschweißen KW - Schweißeignungsprüfung KW - Dilatometrie PY - 2025 SN - 978-3-8440-9961-4 DO - https://doi.org/10.21268/20250505-1 VL - 15 SP - 370 EP - 380 PB - Shaker Verlag GmbH CY - Düren AN - OPUS4-63377 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erxleben, Kjell A1 - Kaiser, Sebastian A1 - Rhode, Michael A1 - Kannengießer, Thomas A1 - Hadick, C. A1 - Schu, K. T1 - Component test concept for evaluation of in-service welding on pressurized hydrogen pipelines N2 - Hydrogen is set as the energy carrier of tomorrow and most countries will achieve large-scale hydrogen transport through the conversion of the natural gas (NG) grid and the construction of new pipelines. The interaction between hydrogen and the pipeline materials differs fundamentally from that of NG, as hydrogen is readily absorbed into the material. Considering the possible hydrogen embrittlement (HE), the compatibility of the pipeline materials (low-alloyed steels with a wide strength/thickness range) must be investigated. However, pipelines require intervention for maintenance, repair, or grid expansion with welding on/onto the pipelines while in service, i.e. the well-known "hot tapping" and "plugging" or “stoppling”. The challenges compared to NG can be broadly divided into the possible austenitization of the inner pipe material exposed to hydrogen and the welding itself. Both result in a significant increase in hydrogen solubility and could potentially pose challenges in terms of HE. Emphasis is placed on the word "could" because knowledge of "hot tapping" on hydrogen pipelines is scarce due a lack of service experience. To this end, this study proposes a concept for a component-like demonstrator with the objectives: (1) safe feasibility of "hot tapping" on pressurized model hydrogen pipeline sections, (2) facilitate ex-post sample extraction for the purpose of quantifying the absorbed hydrogen concentrations, and (3) ensure in-situ temperature measurement during welding to monitor the pipeline surface temperature. For safety reasons in the event of an unintentional "burn-through", a solid cylinder was inserted in the demonstrator to restrict the hydrogen gas volume to a small, pressurized layer. Reference pipeline surface temperature measurements were ensured on comparable, unpressurized geometries. The investigated range of welding conditions was investigated for representative material/thickness combinations (DN50 to DN200), suggesting the feasibility of the demonstrator for the determination of reliable in-service welding conditions for both installed and new pipelines for hydrogen service. T2 - 20th Pipeline Technology Conference ptc2025 CY - Berlin, Germany DA - 06.05.2025 KW - In-service KW - Hydrogen KW - Pipeline KW - Repair welding KW - component test PY - 2025 SP - 1 EP - 11 AN - OPUS4-63168 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Richter, Tim A1 - Schröpfer, Dirk A1 - Rhode, Michael A1 - Börner, Andreas T1 - Rührreibschweißen von Hoch- und Mittelentropie-Legierungen N2 - Hoch- und Mittelentropie-Legierungen (engl. High/Medium Entropy Alloys–HEA/MEA) sind relativ neue Werkstoffklassen. Im Gegensatz zu herkömmlichen Le-gierungen bestehen HEA aus fünf bzw. MEA aus drei oder vier Legierungselementen im äquiatomaren Gleichgewicht. Viele HEA weisen aufgrund hervorragender struktu-reller Eigenschaftskombinationen von sehr tiefen bis zu hohen Temperaturen enor-mes Anwendungspotential auf. Die Anwendung für reale Bauteile stellt jedoch die zentrale Frage der Eignung für die fügetechnische Verarbeitung. Dieser Aspekt findet in der weltweiten Materialforschung bisher kaum Beachtung. Anforderungen an die zuverlässige und sichere fügetechnische Verarbeitung dieser Werkstoffe sind von wesentlicher Bedeutung hinsichtlich wirtschaftlicher Bauteilfertigung für spätere po-tenzielle Anwendungsbereiche, bspw. in der Energietechnik. Das Rührreibschweißen (engl. Friction Stir Welding–FSW) stellt hierbei einen vielversprechenden Fügepro-zess dar, dessen Hauptvorteil in der Schweißprozesstemperatur unterhalb der Schmelztemperatur der zu fügenden Werkstoffe liegt. Dies bedingt die Vermeidung der Ausbildung von harten, versprödenden intermetallischen Phasen, wie sie z. B. beim konventionellen Schmelzschweißen von Eisen-Aluminium-Verbindungen auf-treten. Die vorliegende Arbeit stellt grundlegende Untersuchungen zur Schweißbar-keit einer CoCrFeMnNi-Legierung (HEA) und einer CoCrNi-Legierung (MEA) mit dem FSW-Prozess vor. Die Versuchsschweißungen werden mittels mikroskopischer Analysen hinsichtlich des Schweißnahtaufbaus sowie Schweißnahtfehlern charakte-risiert. FSW zeigt sich als grundlegend geeignet zur Verbindungsschweißung der HEA bzw. MEA. Anhand dieser Ergebnisse kann eine weitere Bewertung der Schweißbar-keit erfolgen. T2 - 4 Niedersächsisches Symposium Materialtechnik Clausthal CY - Online meeting DA - 25.02.2021 KW - Hochentropie Legierung KW - Rührreibschweißen KW - Mediumentropie Legierung PY - 2021 SP - 502 EP - 511 AN - OPUS4-52255 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Engelking, Lorenz A1 - Eissel, A. A1 - Schröpfer, Dirk A1 - Treutler, K. A1 - Kannengießer, Thomas A1 - Wesling, V. ED - Brockmann, S. ED - Krupp, U. T1 - Untersuchungsmethoden beim Fräsen additiv gefertigter schwer spanbarer Kobalt-Chrom-Legierungen N2 - Für den Anlagenbau werden hochbelastete Komponenten aus Co-Cr-Legierungen hergestellt. Dabei ist die Zerspanung so herausfordernd, dass additive Fertigungsschritte oft wirtschaftlicher sind. Diese bedingen aber vorwiegende heterogene, anisotrope Gefüge und Eigenschaften und bei nachfolgender Fräsbearbeitung unstetige Zerspankräfte und instabile Spanvorgänge. Hierbei können hybride Zerspanprozesse helfen, hohe Belastungen für Werkzeug und Werkstückoberfläche zu minimieren. Diesbezügliche Charakterisierungen erfordern speziell adaptierte Zerspanungsanalysen. Anhand eines Anwendungsbeispiels, bei dem eine Modifikation der Ausgangslegierung mit 1 % Hf erfolgte, wird die Wechselwirkung zwischen Gefügemorphologie und Fräsprozess dargestellt, der konventionelle mit einem hybriden ultraschallunterstützten Fräsprozess verglichen und die Charakterisierung des Werkzeugverschleißes anhand zweier verschiedener Fräser betrachtet. Analysen auftretender Prozesskräfte mittels Piezo-Mehrkomponenten-Dynamometer, der Werkzeugoszillation mittels Laser-Vibrometer und zusätzliche In-situ-Temperaturmessungen der Werkzeugschneiden mittels Highspeed-Pyrometer bilden den Kern der neuen Zerspanungsprüftechnik. Die vorgestellten Untersuchungsmethoden bilden die Vorgänge bei der Zerspanung additiv gefertigter Werkstoffe detailliert und reproduzierbar ab. Sowohl Legierungsmodifikation als auch hybride Prozessbedingungen lassen gezielte Einflüsse zur deutlichen Verbesserung der Zerspanungssituation zu. T2 - Tagung Werkstoffprüfung 2021 CY - Online meeting DA - 02.12.2021 KW - Ultraschallunterstütztes Fräsen KW - Legierungsmodifikation KW - Additive Fertigung KW - Plasma-Pulver-Auftragschweißen KW - Werkzeugverschleiß PY - 2021 SN - 978-3-941269-98-9 SP - 93 EP - 98 PB - Stahlinstitut VDEh CY - Düsseldorf AN - OPUS4-54921 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Richter, Tim A1 - Rhode, Michael A1 - Schröpfer, Dirk T1 - Innovative Multielement-Legierungen: Aktuelle Ergebnisse zur Schweißbarkeit und Anwendungseigenschaften N2 - Multielement-Legierungen (MPEA – multiple pricipal element alloys) stellen eine neue Klasse von Werkstoffen dar, die aus mindestens drei äquiatomaren Legierungselementen mit jeweils einem Gehalt von 5–35 Atom-% bestehen. Somit unterscheidet sich das Legierungskonzept fundamental von konventionellen bspw. Stahl- oder Al-basierten Legierungen. In jüngster Zeit lag der Schwerpunkt auf dem Legierungs-Design der MPEA und der Überprüfung bzw. Erreichung der gewünschten Eigenschaften bzw. -kombinationen. Hierzu werden die egierungselemente gezielt ausgewählt und die Mikrostrukturen ein- und zum Teil auch mehrphasig eingestellt. Ziel sind hochinnovative MPEA mit angepassten Eigenschaften für die industrielle Anwendung. Dabei sollen insbesondere die bei konventionellen Legierungen wesentlichen Zielkonflikte, wie bspw. der Trade-off zwischen Festigkeit und Duktilität, überwunden werden. Darüber hinaus sind mechanische Eigenschaften bei sehr hohen sowie kryogenen Temperaturen bei gleichzeitig höchster Korrosionsbeständigkeit von hohem Interesse. Die Herstellung von Bauteilen erfordert dazu werkstoff- und beanspruchungsgerechte Füge- bzw. Schweißverfahren. Der Schweißeignung von MPEA wurde bis Ende 2021 nur äußert wenig Aufmerksamkeit zuteil. Die Auswirkungen durch Schweißprozesse auf die Metallurgie und die gewünschten Eigenschaften sind bisher kaum bekannt und limitieren die potenzielle Anwendbarkeit als Funktions- oder Konstruktionswerkstoffe. In einem interdisziplinären BAM-Forschungsprojekt werden aktuell grundlegende Untersuchungen zur Schweißverarbeitung und resultierender Mikrostruktur-Anwendungseigenschafts-Beziehung verschiedener MPEA durchgeführt. Insbesondere Wärmeeinflusszone und Schweißgut sind geprägt durch eine Mikrostruktur, die aus Ungleichgewichtszuständen resultiert. Im Falle von MPEA wurde dies bisher nicht systematisch untersucht. Dazu erfolgte im Rahmen des Projektes eine umfassende Literaturauswertung zum Schweißen von MPEA und Zusammenfassung in einer umfassenden, systematischen Datenbasis. Aus diesem Grund sollen in der vorliegenden Studie die bisher bedeutsamsten Erkenntnisse zur Schweißbarkeit von MPEA systematisch nach MPEA-Typ und Schweißverfahren geordnet und mit eigenen aktuellen Forschungsergebnissen verglichen werden. Durch WIG- und Rührreibschweißversuche an den MPEA-Systemen CoCrNiFeMn bzw. CoCrNi konnten im Projektverlauf bereits wesentliche Fragestellungen beantwortet werden. Dazu zählen Auftreten bzw. Verhinderung intermetallischer Phasen/Seigerungen oder deren Auswirkung auf die Eigenschaften der Schweißverbindung (bspw. Festigkeit oder Korrosionsbeständigkeit). T2 - DVS Congress 2022 CY - Koblenz, Germany DA - 19.09.2022 KW - High Entropy Alloy KW - Schweißen KW - Multielementlegierungen PY - 2022 SP - 62 EP - 67 AN - OPUS4-56706 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Richter, Tim A1 - Schröpfer, Dirk A1 - Rhode, Michael A1 - Börner, Andreas T1 - Influence of modern machining processes on the surface integrity of high-entropy alloys N2 - High Entropy Alloys (HEAs) are a recent class of materials. In contrast to conventional alloys, HEAs consist of five alloying elements in equiatomic equilibrium. The high entropy effect is due, among other things, to the increased configuration entropy, which promotes solid solution formation. Many HEAs have enormous application potential due to excellent structural property combinations from very low to high temperatures. For the introduction of HEAs in real components, however, the question of the applicability of machining production technologies for component manufacture is of central importance. This has so far received Little attention in global materials research. Reliable and safe processing is essential for the demand of economical component production for potential areas of application, e.g. in power plant technology. For metals, milling is the standard machining process. This article presents the results of machining analyses. It focuses on the surface integrity resulting from the milling process on a Co20Cr20Fe20Mn20Ni20-HEA. For this purpose, investigations were carried out using ball nose end milling tools for conventional milling process in comparison to an innovative hybrid process available at BAM Berlin, Ultrasonic-Assisted Milling (USAM). USAM promises a lower Degradation of the surface properties due to lower loads on the workpiece surface during machining. For this purpose, basic milling parameters (cutting speed and tooth feed) were systematically varied and cutting forces were measured during the milling experiments. The subsequent Analysis of these forces allows an understanding of the mechanical loads acting on the tool and component surface. These loads cause topographical, mechanical and microstructural influences on the surface and consequently on the surface integrity. For their characterization, light and scanning electron microscopy were used, and the roughness and residual stresses via X-ray diffraction were measured. The results indicate significant advantages using USAM, especially due to reduced cutting forces compared to the conventional milling process. This causes lower mechanical loads on the tool and surface, combined with lower tensile residual stresses on and below the surface, and ultimately results in a significantly enhanced surface integrity. T2 - Symposium on Materials and Joining Magdeburg 2020 CY - Online meeting DA - 07.09.2020 KW - High entropy alloy KW - Machining KW - Ultrasonic machining PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-512958 DO - https://doi.org/10.1088/1757-899X/882/1/012016 VL - 882 IS - 012016 SP - 1 EP - 11 PB - Institute of Physics CY - London AN - OPUS4-51295 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Nietzke, Jonathan A1 - Richter, Tim T1 - Hydrogen diffusion and desorption characteristics of a CoCrFeMnNi high entropy and a CoCrNi medium entropy alloy N2 - High-entropy alloys (HEAs) are innovative high-performance materials that have attracted more and more research attention. HEAs are characterized by a solid solution of typically five equiatomic metallic elements. In addition, medium-entropy alloys (MEA, with three elements) are of interest and become more and more important. Depending on the alloy concept, HEAs and MEAs show exceptional mechanical properties, especially high-strength and ductility combinations at both cryogenic and elevated temperatures combined with excellent corrosion resistance. Future structural HEA/MEA components can be exposed to potential applications with hydrogen containing environments like high-temperature water in pressurized nuclear reactors or aerospace structures. Other potential applications could be in materials for vessel walls in the field of cryogenic and high-pressure hydrogen storage. So far, the susceptibility of HEAs/MEAs to hydrogen assisted cracking (if any) and the hydrogen diffusion is not investigated in detail yet and can limit or extend possible applications of HEA/MEA as structural materials. In our work, we focused on the hydrogen absorption, diffusion, and distribution in a HEA (CoCrFeMnNi the original Cantor-alloy) and a MEA (CoCrNi). Cathodic hydrogen charging was carried out for the hydrogen ingress, and thermal desorption analysis (TDA) revealed complex hydrogen trapping in both alloy types up to 300 °C. The absorbed total hydrogen concentrations were > 100 ppm for the HEA and > 40 ppm for MEA. In addition, the assessment of the peak deconvolution is not trivial and must consider both experimental and microstructure influences. T2 - 4th International Conference on Metals and Hydrogen - Steely & Hydrogen 2022 CY - Ghent, Belgium DA - 11.10.2022 KW - Hydrogen KW - High-entropy alloy KW - Multiple principal element alloy KW - Thermal desorption analysis KW - Diffusion PY - 2022 SP - 1 EP - 11 CY - Ghent, Belgium AN - OPUS4-56076 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kanzler, Daniel A1 - Bertovic, Marija T1 - Expertise oder KI – Was hilft uns in der ZfP'? N2 - Die zunehmende Integration von Automatisierung und KI in die zerstörungsfreie Prüfung (ZfP) verändert nicht nur die Prüfprozesse selbst, sondern auch die Art und Weise, wie Entscheidungen getroffen werden. Während technische Systeme die Fehleranfälligkeit verringern und die Datenverarbeitung unterstützen können, bleibt die letztendliche Verantwortung beim Menschen. Dieser Beitrag untersucht die Rolle der Intuition in der Entscheidungsfindung und analysiert typische Fehleinschätzungen mithilfe der Prospekttheorie und Erkenntnissen aus der kognitiven Psychologie. Zudem wird aufgezeigt, wie fundierte Entscheidungen in KI-gestützten ZfP Prozessen unterstützt werden können – durch Schulung, erklärbare Systeme, nutzerzentrierte Gestaltung, geeignete Metriken und eine gezielte Aufgabenverteilung zwischen Mensch und Technik. T2 - DGZfP-Jahrestagung 2025 CY - Berlin, Germany DA - 26.05.2025 KW - Zerstörungsfreie Prüfung KW - Künstliche Intelligenz KW - Entscheidungsfindung KW - Mensch-Maschine-Interaktion KW - Human Factors PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-634070 DO - https://doi.org/10.58286/31237 SP - 1 EP - 10 PB - NDT.net AN - OPUS4-63407 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas A1 - Schröpfer, Dirk A1 - Schröder, Nina A1 - Kannengießer, Thomas T1 - Einfluss von Konstruktion und Wasserstoff auf die Kaltrissbildung hochfester Feinkornbaustähle N2 - Der konstruktive Leichtbau erfordert den zunehmenden Einsatz hochfester Feinkornbaustähle mit Streckgrenzen ≥ 690 MPa. Neben den durch die Wandstärkenreduzierung erreichbaren Einsparungen an Ressourcen und Fertigungszeit lässt sich eine weitere Minimierung der Schweißzeit und -kosten mittels abgesenkter Schweißnahtvolumina erreichen. Hierzu wurden moderne Lichtbogenprozesse, wie bspw. der modifizierte Sprühlichtbogen (Mod.SLB), mit erhöhter Abschmelzleistung entwickelt, mit denen auch enge Nahtspalte bzw. Nahtöffnungswinkel geschweißt werden können. Hochfeste Verbindungen unterliegen zunehmend erhöhten Anforderungen in Bezug auf die schweißtechnische Verarbeitung und der resultierenden Bauteilperformance und sicherheit. Dies gilt insbesondere beim Bauteilschweißen mittels solcher Hochleistungsverfahren in Verbindung mit engen Nahtspalten. In der vorliegenden Arbeit soll dieser Herausforderung durch Klärung der Einflüsse auf die Kaltrissbildung bei einem hochfesten Feinkornbau-stahl S960QL Rechnung getragen werden. Für die Kaltrissprüfung werden entsprechende adaptierte Proben analog dem selbstbeanspruchenden TEKKEN-Test verwendet und hinsichtlich Rissbildung, Gefüge, Gehalt an diffusiblem Wasserstoff und Eigenspannungen analysiert. Die Variation der Nahtöffnungswinkel der Prüfnähte erfolgt zwischen 30° und 60°. Zur Vermeidung wasserstoffunterstützter Kaltrissbildung wird die Wirksamkeit einer Nachwärmprozedur aus der Schweißwärme heraus untersucht. Als Ergebnis zeigen die Schweißgüter, die an reduziertem Nahtöffnungswinkel erzeugt wurden, im Mittel etwas höhere Wasserstoffkonzentrationen. Zudem ist an diesen Schweißgütern eine vermehrte Mikro- als auch Makrorissbildung festzustellen. An allen Proben, die nicht nachgewärmt wurden, treten Kerbrisse aufgrund von Kaltrissbildung auf, deren Vermeidung sich durch ein Nachwärmen unmittelbar nach dem Schweißen als besonders effektiv darstellte. T2 - DVS Congress 2020 - Große Schweißtechnische Tagung CY - Online meeting DA - 14.09.2020 KW - Hochfester Feinkornbaustahl KW - MAG-Schweißen KW - Kaltriss KW - Wasserstoff KW - TEKKEN PY - 2020 SN - 978-3-96144-098-6 VL - 365 SP - 564 EP - 570 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-51259 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eissel, A. A1 - Engelking, Lorenz A1 - Treutler, K. A1 - Schröpfer, Dirk A1 - Wesling, V. A1 - Kannengießer, Thomas T1 - Herstellung beanspruchungsgerechter Oberflächen durch Kombination innovativer additiver und abtragender Fertigungsschritte an hochbelasteten Komponenten N2 - In vielen Anwendungen werden aufgrund zunehmender Anforderungen an den Widerstand gegenüber hohen, kombinierten mechanischen, tribologischen, thermischen und korrosiven Beanspruchungen Hochleistungslegierungen eingesetzt. Den vielfach komplexen Bauteilstrukturen, herausfordernden Fertigungseigenschaften und der Erhöhung der Ressourceneffizienz lässt sich heute mit der additiven Fertigung (AM) begegnen, dem oftmals noch unzureichende Kenntnisse über die resultierende Homogenität und Anisotropie der speziellen Gefüge und den damit verbundenen Eigenschaften entgegensteht. Viele Anwendungen benötigen zudem definierte Oberflächen mit hohen Anforderungen an die Oberflächenintegrität, dem durch komplementären Einsatz von additiven und abtragenden Fertigungsschritten Rechnung getragen wird. Hochleistungslegierungen auf der Basis von Nickel oder Kobalt sind infolge der niedrigen Wärmeleitfähigkeit verbunden mit hoher Festigkeit und Zähigkeit äußerst herausfordernd mit Blick auf eine wirtschaftliche Zerspanung mit geometrisch bestimmter Schneide. Ein Vorhaben (IGF-Nr. 20.979 N/DVS-Nr. 1.3211) der BAM und TU Clausthal/ISAF befasst sich mit der Lösung dieser Problemstellung durch gezielte Beeinflussung des Gefüges mittels Modifikation der Schweißzusatzwerkstoffe und den Einsatz des ultraschallunterstützten Fräsens (US), bei gleichzeitiger Sicherstellung der geforderten Eigenschaften der untersuchten Werkstoffe. Im vorliegenden Beitrag werden für die beiden untersuchten FeNi- und CoCr-Legierungen wesentliche Zusammenhänge zwischen verschiedenen Legierungsmodifikationen, der entstehenden Gefügemorphologie und den Zerspanungseigenschaften von mittels PTA additiv gefertigter Proben dargestellt. Hierbei ließen sich Ti, Zr und Hf pulvermetallurgisch zu den jeweiligen Ausgangsschweißzusätzen hinzulegieren. T2 - #additivefertigung: Metall in bestForm CY - Essen, Germany DA - 26.10.2022 KW - Legierungsmodifikation KW - Ultraschallunterstütztes Fräsen KW - Additive Fertigung PY - 2022 SN - 978-3-96144-202-7 VL - 383 SP - 93 EP - 99 PB - DVS-Media GmbH AN - OPUS4-56615 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Becker, Amadeus A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas T1 - Beanspruchungsgerechte Reparatur beim Bauteilschweißen hochfester Feinkornbaustähle N2 - Eine nachhaltige und ressourceneffiziente Fertigung und Errichtung von Windenergieanlagen, sowohl auf See als auch an Land, erfordert zunehmend den Einsatz moderner hochfester Feinkornbaustähle. Werden nach dem Schweißen dieser hochfesten Konstruktionen unzulässige Defekte detektiert, sind nach geltenden Verarbeitungsrichtlinien die defekten Bereiche durch lokales Ausfugen und anschließendes Schweißen zu reparieren. Fehlende Informationen zu adäquaten Reparaturkonzepten in den Regelwerken bedingen oftmals eine unzureichende Berücksichtigung dabei auftretender zusätzlicher Beanspruchungen durch die erhöhte Schrumpfbehinderung der Ausfugenuten. Zusätzlich haben die ausführenden Betriebe vielfach kaum Kenntnis über die Degradation angrenzender Gefüge durch thermische Ausfugeprozesse und erneutes Schweißen, die in diesem Zusammenhang besonders bei den hochfesten Stählen als kritisch anzusehen sind. Das aktuelle Forschungsvorhaben der BAM (FOSTA P1311/IGF-Nr.20162N) fokussiert hierfür systematisch bauteilrelevante Untersuchungen zu den schweißbedingten Beanspruchungen und Gefügeveränderungen bei der Reparatur von hochfesten Schweißverbindungen. Wesentlich sind hierbei der Einfluss der Schrumpfbehinderung, der Wärmeführung beim Schweißen und Ausfugen sowie der Reparaturzyklenanzahl und die metallurgischen Aspekte bei den hochfesten Güten S500MLO für zukünftige Offshore-Anwendungen und S960QL für aktuelle Mobilkrananwendungen. Aufbauend auf einigen Studien zur schweißbedingten Beanspruchung hochfester Stähle zeigt der vorliegende Beitrag die Identifikation geeigneter Probengeometrien und Schweißdetails mittels numerischer und experimenteller Analysen. Dadurch wird die Übertragbarkeit der vorgestellten Schweißexperimente und Ergebnisse hinsichtlich der resultierenden Schweißeigenspannungen auf reale Reparaturfälle im Bereich des hochfesten Stahlbaus sichergestellt. Es zeigt sich in Übereinstimmung mit früheren Ergebnissen eine signifikante Erhöhung der Beanspruchungen an den variierten schlitzförmigen Prüfnähten. Das Eigenspannungsniveau sowohl im Schweißgut als auch in der WEZ korreliert mit dem Einspanngrad. Mit dem Ziel beanspruchungs- und werkstoffgerechte Reparaturkonzepte zu erarbeiten, sind zum einen geringere Wärmeinbringungen, besonders durch niedrige Zwischenlagentemperaturen und Einspannbedingungen anzustreben, um hohe Beanspruchungen und kritische Gefügedegradationen im Reparaturbereich zu vermeiden. Dies wird durch systematische Untersuchungen zum Ausfugen und Schweißen sowie letztlich dem Transfer von Verarbeitungsempfehlungen für die Anwender und Richtlinien erreicht. T2 - DVS Congress 2021 CY - Online meeting DA - 14.09.2021 KW - MAG-Schweißen KW - Reparatur KW - Eigenspannungen KW - Hochfester Stahl KW - Thermisches Ausfugen KW - Windenergie KW - Gefügedegradation PY - 2021 SN - 978-3-96144-146-4 VL - 371 SP - 285 EP - 292 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-56666 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Nietzke, Jonathan A1 - Mente, Tobias A1 - Kannengießer, Thomas T1 - Diffusionsmessungen in UP-Mehrlagenschweißgut als effektives Tool gegen verzögerte Kaltrissbildung in Dickblechschweißungen N2 - Offshore-Windenergieanlagen bilden einen zentralen Bestandteil der zukünftigen Energieerzeugung. Hierzu notwendige Gründungs- und Turmstrukturen werden vorrangig aus UP-geschweißten Blechen aus hochfesten niedriglegierten Stählen mit Dicken bis zu 200 mm hergestellt. Die großen Blechdicken begünstigen hohe Schweißeigenspannungen und lange Diffusionswege für z. B. über den Schweißprozess eingebrachten Wasserstoff. Damit steigt das Risiko für eine wasserstoffunterstützte Kaltrissbildung (WKB) an. Zum sichereren Ausschluss von WKB in den geschweißten Komponenten wird in Abhängigkeit der Nahtgröße, Wärmeeinbringung und Stahlsorte eine Mindestwartezeit (MWZ) von bis zu 48 h empfohlen, bevor die zerstörungsfreie Prüfung durchgeführt wird. Es ist allerdings offen, ob die empfohlene MWZ zu konservativ ist. Einflüsse sind hier bspw. die schwierige Bewertung des Wasserstoffdiffusionsverhaltens im heterogenen UP-Mehrlagen-Schweißgut (SG) im Vergleich zum Grundwerkstoff (GW). Zudem sind nur sehr begrenzt H-Diffusionskoeffizienten für UP-Mehrlagen-SG als Grundlage zur Abschätzung des Zeitintervalls einer möglichen verzögerten Kaltrissbildung (somit MWZ) oder auch für Nachwärmprozeduren zur Wasserstoffreduktion (keine MWZ) verfügbar. Verlässliche H-Diffusionskoeffizienten sind daher ein adäquates Tool zur Bewertung des Risikos einer verzögerten WKB. Dieser Beitrag beschreibt Untersuchungen zur Charakterisierung der Wasserstoffdiffusionsverhalten in UP-Mehrlagen-SG eines 60 mm dicken Bleches einer Offshore-Stahlgüte. Dazu wurden Proben unterschiedlicher Dicke aus dem reinen Schweißgut extrahiert und über elektrochemische Permeation und Trägergasheißextraktion im Temperaturbereich bis 400 °C sehr interessante Ergebnisse zu den korrespondierenden Diffusionskoeffizienten erarbeitet. T2 - DVS Congress 2021 CY - Online meeting DA - 14.09.2021 KW - UP-Schweißen KW - Wasserstoff KW - Kaltriss KW - Permeation KW - Diffusion PY - 2021 SN - 978-3-96144-146-4 VL - 371 SP - 448 EP - 459 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-53369 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Giese, Marcel A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas A1 - Gräbner, Maraike A1 - Treutler, Kai A1 - Wesling, Volker T1 - Legierungsmodifikation und Einsatz hybrider Fräsprozesse zur Optimierung der Zerspanungssituation Ni-basierter Verschleißschutzauftragschweißungen mit definierten Oberflächen N2 - Die Verringerung der CO2-Emissionen ist eng mit der Entwicklung hocheffizienter und wirtschaftlicher Komponenten aus Stahl in der Anlagen- und Verfahrenstechnik verknüpft. Um den hohen kombinier-ten korrosiven, tribologischen, thermischen und mechanischen Beanspruchungen stand zu halten, werden auf Anwendungsfall und Stahlwerkstoff abgestimmte Verschleißschutzschichten eingesetzt. Neben der zunehmenden Forderung konventionelle Kobalt- durch Nickellegierungen zu ersetzen, wächst auch der Bedarf nach definierten Ober- bzw. Funktionsflächen hoher Güte. Aufgrund hohen Werkzeugverschleißes ist die erforderliche Fräsbearbeitung zu Herstellung der komplexen Geomet-rien der Bauteile für KMU oftmals wirtschaftlich nicht möglich. Mittels Legierungsmodifikation der Schweißzusätze für nickelbasierte plasmaauftraggeschweißte Verschleißschutzschichten und durch den Einsatz innovativer ultraschallunterstützter Fräsprozesse soll eine günstigere Zerspanbarkeit er-reicht werden, ohne das Verschleißschutzpotential zu mindern. Im vorliegenden Beitrag wird der Ein-fluss der mittels Legierungsmodifikation eingestellten Gefüge- und Ausscheidungsmorphologie auf die Zerspanbarkeit untersucht. Dies erfolgt anhand einer typischerweise für Schneckenmaschinen einge-setzten Verschleißschutzlegierung NiCrMoSiFeB-Legierung („Colmonoy 56 PTA“), die konventionelle CoCr-Legierungen (Stellite) substituiert. Metallurgische Untersuchungen und In-situ-Messungen auf-tretender Prozesskräfte an der Werkzeugschneide beim Fräsen sowie anschließende Untersuchungen von Werkzeugverschleiß und Oberflächenintegrität ermöglichen eine detaillierte Analyse und Korrela-tion zwischen mikrostrukturellen Eigenschaften und Zerspanbarkeit. T2 - DVS Congress 2023 CY - Essen, Germany DA - 11.09.2023 KW - Werkzeugverschleiß KW - Oberflächenintegrität KW - Ultraschallunterstütztes Fräsen KW - Zerspankräfte PY - 2023 SP - 742 EP - 747 AN - OPUS4-59210 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Giese, Marcel A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas A1 - Müller, Thomas A1 - Treutler, Kai A1 - Wesling, Volker T1 - Legierungsmodifikation und Einsatz hybrider Fräsprozesse zur Optimierung der Zerspanungssituation Ni-basierter Verschleißschutzauftragschweißungen mit definierten Oberflächen N2 - Die Bestrebungen zur Verringerung der CO2-Emissionen erfordern hochbelastbare und effiziente Komponenten aus Stahl in der Anlagen-, Verfahrens- und Kraftwerkstechnik. Hierfür sind in zunehmendem Maße auf den Anwendungsfall und Stahlwerkstoff abgestimmte Verschleißschutzschich-ten und definierte, zerspante Oberflächen notwendig. Die hohen Härten dieser Schichten und der Einsatz konventioneller Co-basierter Verschleißwerkstoffe führen oftmals zu unwirtschaftlichen Bauteilen, gerade aufgrund hohen Werkzeugverschleißes bei der Zerspanung mit geometrisch bestimmter Schneide. Er-kenntnisse über den Einsatz Ni-basierter Verschleißwerkstoffe und die Optimierung der Zerspanbarkeit mittels Legierungsmodifikationen und moderner hybrider Fräsprozesse ohne Verschlechterung der Ver-schleißschutzeigenschaften sind deshalb für die Anwender und Verarbeiter zur wirtschaftlichen Fertigung hochbelasteter Stahlbauteile wesentlich. Der vorliegende Beitrag stellt die Untersuchungsmethodik eines aktuell laufenden Vorhabens der TU Clausthal und BAM, Berlin, vor. Fokus liegt hierbei auf den hochin-strumentierten Fräsexperimenten, die eine reproduzierbare Analyse und Korrelation zwischen den mik-rostrukturellen Eigenschaften der auftraggeschweißten Legierungen, dem Zerspanprozess und der Zer-spanbarkeit, insbesondere der resultierenden Oberflächenintegrität, ermöglichen sollen. T2 - Tagung Werkstoffprüfung 2022 CY - Dresden, Germany DA - 27.10.2022 KW - Werkzeugverschleiß KW - Oberflächenintegrität KW - Ultraschallunterstütztes Fräsen KW - Zerspankräfte PY - 2022 SP - 368 EP - 374 AN - OPUS4-59211 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne A1 - Thomas, Maximilian A1 - Liepold, Philipp A1 - Kannengießer, Thomas A1 - Schröpfer, Dirk T1 - Einfluss der Schweiß- und Prüfparameter bei der Heißrissbewertung hochfester Schweißzusatzwerkstoffe N2 - Die Heißrissneigung beim Schweißen kann mittels einer ganzen Reihe von Prüfverfahren ermittelt werden. Eine etablierte Methode ist die sogenannte Varestraint-Prüfung, welche auch an der Bundesanstalt für Materialforschung und -prüfung (BAM) als modifizierter Varestraint/Transvarestraint-Test (MVT) zum Einsatz kommt. Die Ergebnisse von Varestraint-Prüfungen hängen jedoch stets in unter-schiedlichem Maße von der individuellen Prüfmaschinenauslegung und den verwendeten Prüfparametern ab. Dies kann zu einer uneinheitlichen Bewertung des Rissverhaltens führen, wenn die Risslänge konventionell als Kriterium für die Rissneigung herangezogen wird. Scheinbare Abhängigkeiten von Prozessparametern erschweren dann die Interpretation der Ergebnisse. Eine neuartige Bewertungsmethodik entkoppelt den Maschineneinfluss vom Materialverhalten und verwendet die Dehnrate als Risskriterium. T2 - 5. Symposium Materialtechnik CY - Clausthal-Zellerfeld, Germany DA - 23.02.2023 KW - Heißrisse KW - Varestraint-Test PY - 2023 SN - 978-3-8440-9105-2 SN - 2364-0804 VL - 12 SP - 357 EP - 365 PB - Shaker CY - Düren AN - OPUS4-57993 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Kromm, Arne A1 - Mente, Tobias A1 - Czeskleba, Denis A1 - Brackrock, Daniel A1 - Kannengießer, Thomas T1 - Bauteilversuch zur Bewertung der wasserstoffunterstützten Rissanfälligkeit geschweißter, dickwandiger Offshore-Gründungsstrukturen N2 - Offshore-Windenergieanlagen erfordern Gründungskonzepte aus unterpulver-(UP-)geschweißten Dickblechen (bspw. der Güte S420ML). Während der Schweißfertigung kann eine zeitverzögerte wasserstoffunterstützte Kaltrissbildung auftreten, deren Bewertung aufgrund der Bauteilgröße von Offshore-Strukturen sehr komplex ist. Deswegen wurde eine bauteilähnliche Geometrie (Mock-Up) entwickelt, um reale Steifigkeitsverhältnisse auf den Labormaßstab zu übertragen. Zusätzliche Versteifungen simulieren die Wirkung einer Einspannung bzw. Schrumpfbehinderung der Schweißnaht. Über die Verwendung von Schweißpulvern mit definierter Feuchte wurden zudem ein Extremszenario der Wasserstoffaufnahme simuliert. Entsprechend der vorgegebenen Mindestwartezeit für die ZfP von bis zu 48 h wurde die Schweißnaht zerstörungsfrei mit Phased-Array-Ultraschall-Prüfung (PAUT) geprüft und die Eigenspannungen über Röntgendiffraktometrie (XRD) bestimmt. Zusätzlich wurde die Wasserstoffverteilung in der Schweißverbindung numerisch simuliert. Außer zulässigen Defekten (wie Poren), wurde keine verzögerte Kaltrissbildung in den Mock-Ups festgestellt, was auf hohe Rissbeständigkeit hindeutet. T2 - Tagung Werkstoffprüfung 2023 CY - Berlin, Germany DA - 23.11.2023 KW - Kaltrissbildung KW - Wasserstoff KW - Offshore KW - Schweißen KW - Bauteiltest PY - 2023 DO - https://doi.org/10.48447/WP-2023-219 SP - 316 EP - 321 CY - Berlin AN - OPUS4-58908 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Artinov, Antoni A1 - Meng, Xiangmeng A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Numerical study on the formation of a bulging region in partial penetration laser beam welding N2 - A transient three-dimensional thermo-fluid dynamics numerical model was developed to study the formation of a bulging region in partial penetration laser beam welding. The model accounts for the coupling between the fluid flow, the heat transfer, and the keyhole dynamics by considering the effects of multiple reflections and Fresnel absorption of the laser beam in the keyhole, the phase transitions during melting and evaporating, the thermo-capillary convection, the natural convection, and the phase-specific and temperature-dependent material properties up to the evaporation temperature. The validity of the model was backed up by experimentally obtained data, including the drilling time, the weld pool length, the local temperature history outside the weld pool, the process efficiency, and a range of metallographic crosssections. The model was applied for the cases of partial penetration laser beam welding of 8 mm and 12 mm thick unalloyed steel sheets. The obtained experimental and numerical results reveal that the bulging region forms transiently depending on the penetration depth of the weld, showing a tendency to transition from a slight bulging to a fully developed bulging region between penetration depths of 6 mm and 9 mm, respectively. T2 - 13th International Seminar "Numerical Analysis of Weldability" CY - Seggau, Austria DA - 04.09.2022 KW - Laser beam welding KW - Deep penetration KW - Bulge formation KW - Numerical modeling PY - 2023 SN - 978-3-85125-968-1 SN - 978-3-85125-969-8 SN - 2410-0544 VL - 13 SP - 101 EP - 126 PB - Verlag der Technischen Universität Graz AN - OPUS4-58802 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Artinov, Antoni A1 - Kising, Pascal A1 - Bachmann, Marcel A1 - Meng, Xiangmeng A1 - Rethmeier, Michael T1 - Numerical analysis of the dependency of the weld pool shape on turbulence and thermodynamic activity of solutes in laser beam welding of unalloyed steels N2 - A three-dimensional numerical model was developed to accurately predict the steady-state weld pool shape in full penetration laser beam welding. The model accounts for the coupling between the heat transfer and the fluid dynamics by considering the effects of solid/liquid phase transition, thermo-capillary convection, natural convection, and phase-specific and temperature-dependent material properties up to the evaporation temperature. A fixed right circular cone was utilized as a keyhole geometry to consider the heat absorbed from the laser beam. The model was used to analyze the influence of the thermodynamic activity of solutes and turbulence on the weld pool shape. A mesh sensitivity analysis was performed on a hybrid mesh combining hexahedral and tetrahedral elements. For the case of full penetration laser beam welding of 8 mm thick unalloyed steel sheets, the dependence of the weld pool shape on the surface-active element sulfur was found to be negligible. The analysis of the results showed that a laminar formulation is sufficient for accurately predicting the weld pool shape since the turbulence has a minor impact on the flow dynamics in the weld pool. The validity of the numerical results was backed up by experimental measurements and observations, including weld pool length, local temperature history, and a range of metallographic crosssections. T2 - 13th International Seminar Numerical Analysis of Weldability CY - Seggau, Austria DA - 04.09.2022 KW - Weld pool shape KW - Numerical modeling KW - Laser beam welding KW - Thermo-capillary convection KW - Turbulence PY - 2023 SN - 978-3-85125-968-1 SN - 978-3-85125-969-8 SN - 2410-0544 VL - 13 SP - 161 EP - 188 PB - Verlag der Technischen Universität Graz AN - OPUS4-58803 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Yang, Chunliang A1 - Wu, Chuansong A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Numerical analysis of ultrasonic vibration enhanced friction stir welding of dissimilar Al/Mg alloys N2 - The ultrasonic vibration enhanced friction stir welding (UVeFSW) process has unique advantages in joining dissimilar Al/Mg alloys. While there are complex coupling mechanisms of multi-fields in the process, it is of great significance to model this process, to reveal the influence mechanism of ultrasonic vibration on the formation of Al/Mg joints. In this study, the acoustic-plastic constitutive equation was established by considering the influence of both ultrasonic softening and residual hardening on the flow stress at different temperatures and strain rates. And the ultrasonic induced friction reduction (UiFR) effect on friction coefficient in different relative directions at the FSW tool-workpiece interface was quantitatively calculated and analyzed. The Al/Mg UVeFSW process model was developed through introducing the above acoustic effects into the model of Al/Mg friction stir welding (FSW). The ultrasonic energy is stronger on the aluminum alloy side. In the stirred zone, there is the pattern distribution of ultrasonic sound pressure and energy. The heat generation at the tool-workpiece contact interface and viscous dissipation were reduced after applying ultrasonic vibra-tion. Due to the UiFR effect, the projection of friction coefficient and heat flux distributions at the tool-workpiece interface present a "deformed" butterfly shape. The calculated results show that ultrasonic vibra-tion enhanced the material flow and promoted the mixing of dissimilar materials. T2 - 13th International Seminar Numerical Analysis of Weldability CY - Seggau, Austria DA - 04.09.2022 KW - Friction stir welding KW - Ultrasonic vibration KW - Al/Mg alloys KW - Numerical simulation PY - 2023 SN - 2410-0544 VL - 13 SP - 517 EP - 538 PB - Verlag der Technischen Universität Graz AN - OPUS4-58805 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meng, Xiangmeng A1 - Artinov, Antoni A1 - Bachmann, Marcel A1 - Üstündag, Ömer A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - A numerical study on the suppression of a detrimental weld pool profile in wire feed laser beam welding by magnetohydrodynamic technique N2 - The weld quality and the possible defect formation are directly determined by the weld pool shape and the thermo-fluid dynamics therein. In this paper, an untypical weld pool profile, i.e., elongated at its top and bottom but narrowed at the middle, is found experimentally and numerically in the wire feed laser beam welding. The detrimental influence of the weld pool narrowing on the element transport is analyzed and discussed. A magnetohydrodynamic technique is utilized to suppress the narrowing, aiming at a more homogenous element distribution. It is found that a low-temperature region is formed in the middle of the weld pool due to the interaction of the two dominant circulations from the top and bottom regions. The weld pool is significantly narrowed due to the untypical growth of the mushy zone in the low-temperature region, which results in a direct blocking effect on the downward flow and the premature solidification in the middle region. The Lorentz force produced by a transverse oscillating magnetic field shows the potential to change the flow pattern into a single-circulation type and the low-temperature-gradient region is mitigated. Therefore, the downward transfer channel is widened, and its premature solidification is prevented. The numerical results are well validated by experimental measurements of metal/glass observation and X-ray fluorescence element mapping. T2 - 13th International Seminar Numerical Analysis of Weldability CY - Seggau, Austria DA - 04.09.2022 KW - Thermo-fluid flow KW - Element transport KW - Laser beam welding KW - Magnetohydrodynamics KW - Multi - physical modeling PY - 2023 SN - 2410-0544 VL - 13 SP - 143 EP - 160 PB - Verlag der Technischen Universität Graz AN - OPUS4-58806 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Yang, Chunliang A1 - Yang, Fan A1 - Meng, Xiangmeng A1 - Putra, Stephen Nugraha A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Experimental and numerical study on grain refinement in electromagnetic assisted laser beam welding of 5754 al alloy N2 - Through experimental observation and auxiliary numerical simulation, this investigation studies the different types of grain refinement of 5754 aluminum alloy laser beam welding by applying a transverse oscillating magnetic field. Scanning electron microscope results have proved that the application of a magnetic field can reduce the average crystal branch width and increase its number. The interaction between the induced eddy current generated by the Seebeck effect and the applied external magnetic field produces a Lorentz force, which is important for the increase of the number of crystal branches. Based on the theory of dendrite fragmentation and the magnetic field-induced branches increment, the grain size reduction caused by the magnetic field is studied. Furthermore, the effects of the magnetic field are analyzed by combining a phase field method model and simulations of nucleation and grain growth. The grain distribution and average grain size after welding verifies the reliability of the model. In addition, the introduction of a magnetic field can increase the number of periodic three-dimensional solidification patterns. In the intersection of two periods of solidification patterns, the metal can be re-melted and then re-solidified, which prevents the grains that have been solidified and formed previously from further growth and generates some small cellular grains in the new fusion line. The magnetic field increases the building frequency of these solidification structures and thus promotes this kind of grain refinement. T2 - International Congress of Applications of Lasers & Electro-Optics 2023 CY - Chicago, USA DA - 16.10.2023 KW - Laser beam welding KW - Magnetic field KW - Crystal branch development KW - Grain refinement KW - Periodic solidification pattern PY - 2023 SP - 1 EP - 10 AN - OPUS4-58809 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Putra, Stephen Nugraha A1 - Meng, Xiangmeng A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Der Einfluss verschiedener räumlicher Diskretisierungsansätze des Ray-Tracing-Verfahrens bei der Simulation des Laserstrahltiefschweißen N2 - Die Wärmeverteilung des Lasers beim Laserstrahltiefschweißen ist für die Formgebung der Dampfkapillare und für die Schweißbaddynamik entscheidend. In dieser Arbeit werden die Laserwärmeverteilung und deren Einflüsse auf die Schweißbadtiefe sowie -breite numerisch anhand des Ray-Tracing-Verfahrens analysiert. Hierbei wird der La-serstrahl in mehreren Strahlenbündeln bzw. Subrays unterteilt. Diesbezüglich soll der Pfad der Subrays präzis be-rechnet werden, um die Dynamik der Dampfkapillare und des Schweißbades eines realen Schweißprozesses rich-tig abzubilden. Zu diesem Zweck beschäftigt sich die vorliegende Arbeit mit der Genauigkeitsverbesserung der Kontaktposition und der Reflexionsrichtung der Subrays auf der freien Oberfläche anhand der Level-Set-Methode. Um die Güte dieses Simulationsansatzes zu gewährleisten, wurde eine Gegenüberstellung mit den zwei klassischen Ray-Tracing-Verfahren mittels drei verschiedenen Benchmark-Testreihen durchgeführt. Anschließend wurden die Versuchsergebnisse zur Validierung der implementierten numerischen Ansätze verwendet. Im Rahmen dieser Arbeit kann es gezeigt werden, dass unterschiedliche Wärmeverteilung aufgrund der verschiedenen Ray-Tracing-Verfahren deutlich zu erkennen ist, welche wiederum die Schweißbaddynamik sowie die lokalisierte Dampfkapil-lardynamik stark beeinflussen. Ferner wurde es bestätigt, dass die implementierte Level-Set-Methode zu einer ge-naueren Ermittlung der Kontaktposition und der Reflexionsrichtung der Subrays und somit zu einer Verbesserung der simulierten Schmelzkontur führt. T2 - 43. Assistentenseminar Füge- und Schweißtechnik CY - Schwarzenberg/Erzgebirge, Germany DA - 27.09.2022 KW - Laser beam welding KW - Ray tracing method KW - Weld pool dynamics KW - Numerical modeling PY - 2023 UR - https://www.dvs-media.eu/de/neuerscheinungen/4584/43.-assistentenseminar-fuegetechnik SN - 978-3-96144-212-6 VL - 386 SP - 91 EP - 102 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-59119 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bachmann, Marcel A1 - Putra, Stephen Nugraha A1 - Yang, Fan A1 - Meng, Xiangmeng A1 - Pusbatzkies, Pablo A1 - Rethmeier, Michael T1 - Elucidation of the Laser Beam Energy Attenuation by the Vapor Plume Formation during High Power Laser Beam Welding N2 - In high-power laser beam welding, a common phenomenon is the formation of a keyhole caused by the rapid evaporation of the material. Under atmospheric pressure, this evaporation generates a vapor plume that interacts with the laser beam, leading to energy attenuation and scattering of the laser radiation along its path. These interactions affect the stability of the process and the overall weld quality. This study investigates the influence of the vapor plume on the weld pool and keyhole dynamics during high-power laser beam welding of AlMg3 aluminum alloy through experimental and numerical approaches. The primary goal is to identify key vapor plume characteristics, particularly its length fluctuations, and to improve the accuracy of the numerical models. To achieve this, an algorithm was developed for the automated measurement of the vapor plume length using high-speed imaging and advanced data processing techniques. The measured plume length is then used to estimate the additional vapor heating and laser energy attenuation using the Beer–Lambert law. A refined numerical CFD model, incorporating 3D transient heat transfer, fluid flow, and ray tracing, was developed to evaluate the vapor plume’s impact. Results show that already the time-averaged plume length effectively captures its transient influence and aligns well with experimental weld seam geometries. Additionally, energy scattering and absorption caused by the vapor plume led to a wider weld pool at the top surface. The study also shows an increased percentage of keyhole collapses due to the reduced laser power absorption at the keyhole bottom, further highlighting the importance of accurately modeling vapor plume effects. T2 - International Congress of Applications of Lasers & Electro-Optics 2025 CY - Orlando, USA DA - 12.10.2025 KW - Laser beam welding KW - Vapor plume formation KW - Weld pool KW - Keyhole dynamics KW - Numerical modeling PY - 2025 SP - 1 EP - 10 AN - OPUS4-64817 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hälsig, André A1 - Eßbach, Tim-Bernd A1 - Scharf-Wildenhain, Ronny A1 - Altobelli, Martin Gabriel A1 - Phadnis, Prathamesh Jayant A1 - Hensel, Jonas A1 - Fabry, Çağtay A1 - Pittner, Andreas A1 - Armansyah, T1 - Qualitätssicherung beim Lichtbogenschweißen N2 - Der fortschreitende Trend der Automatisierung und Dokumentation sowie die wirtschaftliche und technische Optimierung von Fügeaufgaben machen es notwendig, Sensoren zielführend in bestehende und vorhandene Anlagentechnik zu integrieren. Jedoch bietet die reine Datenerfassung alleine nur einen geringen Mehrwert. Erst durch eine optimierte Datenspeicherung, eine intelligente sowie automatische Datenauswertung und -bewertung entsteht ein echter Nutzen für den industriellen Anwender. Zur Qualifizierung einer standardisierbaren Herangehensweise der Qualitätssicherung beim Lichtbogenschweißen wurden mit einer nationalen Arbeitsgruppe bestehende Unstetigkeiten der Qualitätsbeeinflussung geschweißter Bauteile aufgeschlüsselt und definiert. Parallel dazu wurde ein automatisiertes Schweißsystem mit hochgenauer Messtechnik (u. a. Stromstärke, Spannung, Drahtvorschub, Thermokamera, Geometriescanner usw.) ausgerüstet und validiert. Hierfür wurde die Open-Source-Technologie WelDX der BAM genutzt. Anschließend wurden bewusst fehlerhaft geschweißte Nähte im Vergleich zu fehlerfreien Referenzschweißungen hergestellt, Messdaten erfasst und analysiert. Im Rahmen dieses Beitrags werden erste Ergebnisse und Erkenntnisse in Bezug auf die Detektion und Bewertung von Unstetigkeiten beim Lichtbogenschweißen dargestellt. Dabei wurde deutlich, dass alternative Darstellungs- und Analysemethoden wie die Anwendung der Mahalanobis-Distanz im Stromstärke-Spannungs-Diagramm eine eindeutigere Korrelation zwischen Unstetigkeiten und Prozesssignalen ermöglichen. T2 - DVS CONGRESS 2025 CY - Essen, Germany DA - 16.09.2025 KW - Lichtbogenschweißen KW - Qualitätssicherung KW - Forschungsdatenmanagement KW - WelDX PY - 2025 SN - 978-3-96144-298-0 VL - 401 SP - 76 EP - 85 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-64565 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Uhlig, Marvin A1 - Schröder, Nina A1 - Höfer, Kevin A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Hensel, Jonas T1 - Schweißverfahrensqualifikation an Stumpfnahtverbindungen aus Altstahl- und Feinkornbaustahl N2 - Der Erhalt und die Ertüchtigung bestehender Stahltragwerke gewinnen im Bauwesen zunehmend an Bedeutung. Besonders betroffen sind Konstruktionen aus sogenannten Flussstählen, die im Zeitraum zwischen etwa 1880 und 1940, noch vor Einführung der ersten Stahlnorm DIN 488-1, in großem Umfang im Brücken-, Wasserbau- und Hochspannungsanlagenbau verwendet wurden. Diese Stähle wurden in historischen erstellungsverfahren wie dem Thomas-, Bessemer- oder Siemens-Martin-Verfahren erzeugt und weisen im Vergleich zu heutigen Baustählen eine deutlich größere Streuung in ihren chemischen und mechanischen Eigenschaften auf. Trotz ihres hohen Alters sind viele dieser Tragwerke nach wie vor im Betrieb und befinden sich am Rande ihrer statischen und funktionalen Anforderungen. Ihr Rückbau und Ersatz durch Neubauten sind jedoch oftmals mit erheblichem wirtschaftlichem, logistischem und ökologischem Aufwand verbunden. Daher rückt die Instandhaltung und Weiterverwendung solcher Altbauwerke verstärkt in den Fokus von Infrastrukturprogrammen, Sanierungsstrategien und besitzt eine große kulturelle Bedeutung. Im Rahmen der vorliegenden Untersuchung soll das Potenzial des MAG-Schweißens mit G 18 8 Mn Zusatzwerkstoff für Stumpfnahtverbindungen aus Flussstahl und Feinkornbaustahl qualifiziert werden. Ziel ist es, durch experimentelle und werkstofftechnische Analysen weitere Erkenntnisse über die Schweißbarkeit historischer Stähle zu gewinnen, Anwendungsempfehlungen für die Praxis abzuleiten und damit einen Beitrag zur sicheren und wirtschaftlichen Sanierung historischer Infrastrukturbauwerke zu leisten. T2 - DVS Congress 2025 CY - Essen, Germany DA - 16.09.2025 KW - Altstahl KW - MAG-Schweißen KW - Seigerungen KW - Instandsetzung KW - Feinkornbaustahl PY - 2025 SN - 978-3-96144-298-0 VL - 401 SP - 1 EP - 17 AN - OPUS4-64278 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meng, Xiangmeng A1 - Putra, Stephen Nugraha A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Parametric study of the laser energy absorption in high-power laser beam welding N2 - Laser energy absorption on the keyhole wall is decisive for the thermodynamic behavior and the resultant weld properties in the high-power laser beam welding process. However, its highly transient nature on a microsecond scale makes the quantitative analysis challenging. In this paper, the influence of the relevant welding parameters on laser energy absorption is studied statistically by utilizing multiphysical modeling, in which the three-dimensional transient keyhole dynamics and thermo-fluid flow are calculated. A dynamic mesh adaption technique and a localized level-set-based ray-tracing method are employed to improve the model accuracy further. The results show that the focus position has a remarkable effect on the time-averaged laser absorption, and in contrast, the laser energy distribution regime is only slightly influenced by the welding speed in the studied parameter range (1.5–3.0 m/min). The absorption ratio of the laser energy on the keyhole front wall decreases with increasing welding speed and increases with upward-moving focus positions. The comparison between the calculated results and the experimental measurements ensures the validity of the proposed model. T2 - International Congress of Applications of Lasers & Electro-Optics 2024 CY - Los Angeles, CA, USA DA - 03.11.2024 KW - Laser beam welding KW - Laser energy absorption KW - Multiphysics modeling KW - Parametric study KW - Weld pool PY - 2024 SP - 1 EP - 8 AN - OPUS4-61629 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Bernd R. A1 - Soares, A.P. A1 - Kupsch, Andreas A1 - Baum, D. A1 - Hesse, B. A1 - Zaslansky, P. T1 - Untersuchung der Integrität von glasfaserverstärkten Zahnstiften mittels Synchrotron-Röntgenrefraktion N2 - Die Integrität der Verstärkungsfasern in Komposit-Zahnstiften ist entscheidend für die Biegefestigkeit und die langfristige Haftung am Zement in den Wurzelkanälen. Es wurde vermutet, dass die Integrität von glasfaserverstärkten Zahnstiften durch das Beschleifen während der zahnmedizinischen Behandlung beeinträchtigt wird. Eine Beschädigung der Fasern führt zu einer erheblichen strukturellen Schwächung über den gesamten Stiftdurchmesser. Glasfragmente, die durch den Kontakt mit dem Zahnbohrer entstehen, können sich vom Stift lösen und die Haftfähigkeit erheblich verringern. Mit Hilfe hochauflösender Synchrotron-Röntgen-Refraktions-Radiographie (SXRR) konnte das Ausmaß der Schäden zuverlässig identifiziert und charakterisiert werden. Dazu wurden die Glasfaserstifte sowohl im Herstellungszustand als auch nach der Bearbeitung mit einem Diamantbohrer untersucht. Die Datensätze wurden zur Visualisierung und Quantifizierung der morphologischen Charakteristika intakter und durch das Beschleifen beschädigter Regionen analysiert. Sie zeigen Schäden im bearbeiteten Bereich (z. B. Brüche, Splitter und Risse) sowie herstellungsbedingte Inhomogenitäten der Fasern mit einer signifikanten Zunahme der inneren Oberflächen in Probenregionen, die durch das Beschleifen beschädigt wurden. T2 - DGZfP Jahrestagung 2022 CY - Kassel, Germany DA - 23.05.2022 KW - Röntgen-Refraktion KW - Verbundwerkstoffe KW - Zahnstifte PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-549231 SP - 1 EP - 7 AN - OPUS4-54923 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Thoralf A1 - Lehmann Schlag, Jens A1 - Burkert, Andreas T1 - KorroPad®-Ein Kurzzeitprüfverfahren zur Qualitätssicherung der Oberflächen- und Schweißnahtnachbearbeitung nichtrostender Stähle N2 - Die Ausbildung einer stabilen Passivschicht ist entscheidend für den Korrosionsschutz nichtrostender Stähle. KorroPad® bietet eine schnelle, zerstörungsfreie Bewertung der Passivschichtstabilität und ist seit 2025 als DIN 50024 genormt. Die Methode ermöglicht eine 15‑minütige Vor‑Ort‑Prüfung ohne Spezialwissen und schließt die Lücke zwischen teuren Laborverfahren und fehlender prozessbegleitender Qualitätssicherung. Der Beitrag beschreibt Funktionsprinzip, Anwendung sowie Beispiele aus der Oberflächen- und Schweißnahtbearbeitung. T2 - 43. Vortrags- und Diskussionstagung Werkstoffprüfung 2025 CY - Dresden, Germany DA - 26.11.2025 KW - KorroPad KW - Nichtrostender Stahl KW - Korrosion KW - Passivität PY - 2025 SN - 978-3-88355-454-9 VL - 43 SP - 1 EP - 7 PB - DGM Deutsche Gesellschaft für Materialkunde e.V. CY - Sankt Augustin AN - OPUS4-64933 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stuff, Maria A1 - Rübner, Katrin A1 - Prinz, Carsten A1 - Rische, N. A1 - Chronz, M. A1 - Kühne, Hans-Carsten ED - Siegesmund, S. ED - Middendorf, B. T1 - Towards a better understanding of tuff stone deterioration N2 - Stone deterioration is the result of a complex interaction of external physical, chemical and biological forces with the mineralogical-petrophysical properties of the stone. With a better understanding of how these properties are linked to material behavior and durability, more effective measures for stone conservation can be developed. Studying these interactions in tuff is particularly complex due to the naturally high heterogeneity of tuff rocks. The first aim of a current research project is to combine the results of recent and older studies on tuff deterioration. Furthermore, the literature overview is complemented by our own investigation of Weibern and Ettringen tuff, with a focus on pore structure characteristics. T2 - STONE - 14th international congress on the deterioration and conservation of stone CY - Meeting was canceled DA - 07.09.2020 KW - Pore structure KW - Weathering KW - Weibern tuff KW - Ettringen tuff PY - 2020 SN - 978-3-96311-172-3 SP - 805 EP - 810 PB - Mitteldeutscher Verlag CY - Halle (Saale) AN - OPUS4-51549 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fedelich, Bernard A1 - Feldmann, Titus A1 - Haftaoglu, Cetin A1 - Nolze, Gert A1 - Schriever, Sina A1 - Epishin, A. A1 - Camin, B. A1 - Lopez-Galilea, I. A1 - Ruttert, B. A1 - Theisen, W. T1 - Untersuchung des Kriechverhaltens einer Nickelbasis-Superlegierung bei ultrahohen homologen Temperaturen und Anwendung auf das heiß-isostatische Pressen (HIP) N2 - Mit Hilfe des HIP-Verfahrens („Hot Isostatic Pressing“) werden Poren in der einkristallinen Nickel-Basis Superlegierung CMSX-4 kontinuierlich geschrumpft und dadurch die nach der Erstarrung und der Wärmebehandlung vorhandene Porosität stark reduziert. In diesem Beitrag werden experimentelle und numerische Untersuchungen zu den Mechanismen der Porenschrumpfung zusammengefasst. Es zeigt sich, dass das Verformungsverhalten während Kriechversuchen bei der HIP-Temperatur durch Versetzungsgleitung auf oktaedrischen Ebenen dominiert wird. Dagegen zeigen Messungen der Porositätsabnahme und Simulationen des Porenschließens, dass die Kinetik der Porenschrumpfung durch das Phänomen der Leerstellendiffusion zwischen Poren und Kleinwinkelkorngrenzen („Low Angle Boundary“, LAB) bestimmt wird. Im Gegensatz führt die klassische Kristallviskoplastizität zu einer systematischen Überschätzung dieser Kinetik. Der scheinbare Widerspruch lässt sich auflösen, wenn man bedenkt, dass auf der Skala der Poren Versetzungsquellen nicht gleichmäßig verteilt sind, wie in der konventionellen Kristallplastizität implizit angenommen wird. Stattdessen wird in einem weiterführenden Modell davon ausgegangen, das Kleinwinkelkorngrenzen (LABs) als Versetzungsquellen fungieren, während die Scherspannungen sehr stark in der Nähe der Poren lokalisiert sind, was die Emission von Versetzungen deutlich reduziert. T2 - Langzeitverhalten warmfester Stähle und Hochtemperaturwerkstoffe CY - Online meeting DA - 27.11.2020 KW - HIP KW - Superlegierung KW - Kriechen PY - 2020 SN - 978-3-946885-95-5 VL - 2020 SP - 28 EP - 39 PB - Forschungsvereinigung Warmfeste Stähle und Hochtemperaturwerkstoffe AN - OPUS4-51796 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meng, Xiangmeng A1 - Bachmann, Marcel A1 - Kising, Pascal A1 - Yang, Fan A1 - Rethmeier, Michael T1 - Prediction of weld pool and keyhole geometries in high-power laser beam welding through a physics-informed generative artificial intelligence approach N2 - The weld pool and keyhole geometries are critical characteristics in evaluating the stability of the high-power laser beam welding (LBW) process and determining the resultant weld quality. However, obtaining these data through experimental or numerical methods remains challenging due to the difficulties in experimental measurements and the high computational demands of numerical modelling. This paper presents a physics-informed generative approach for predicting weld pool and keyhole geometries in the LBW process. With the help of a well experimentally validated numerical model considering the underlying physics in the LBW, the geometries of the weld pool and keyhole under various welding conditions are calculated, serving as the dataset of the generative model. A Conditional Variational Autoencoder (CVAE) model is employed to generate realistic 2D weld pool and keyhole geometries from the welding parameters. We utilize a β-VAE model with the Evidence Lower Bound (ELBO) loss function and include Kullback-Leibler divergence annealing to better optimize model performance and stability during training. The generated results show a good agreement with the ground truth from the numerical simulation. The proposed approach exhibits the potential of physics-informed generative models for a rapid and accurate prediction of the weld pool geometries across a diverse range of process parameters, offering a computationally efficient alternative to full numerical simulations for process optimization and control in laser beam welding processes. T2 - International Congress of Applications of Lasers & Electro-Optics 2025 CY - Orlando, USA DA - 12.10.2025 KW - Laser beam welding KW - Generative artificial intelligence KW - Machine learning KW - numerical simulation PY - 2025 SP - 1 EP - 10 AN - OPUS4-65075 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Huo, Wenjie A1 - Schmies, Lennart A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael A1 - Wolter, Katinka T1 - An illumination based backdoor attack against crack detection systems in laser beam welding N2 - Deep neural networks (DNNs) have been wildly used in engineering and have achieved state-of-the-art performance in prediction and measurement tasks. A solidification crack is a serious fault during laser beam welding and it has been proven to be successfully detected using DNNs. Recently, research on the security of DNNs is receiving increasing attention because it is necessary to explore the reliability of DNNs to avoid potential security risks. The backdoor attack is a serious threat, where attackers aim to inject an inconspicuous pattern referred to as trigger into a small portion of training data, resulting in incorrect predictions in the reference phase whenever the input contains the trigger. In this work, we first generate experimental data containing actual cracks in the welding laboratory for training a crack detection model. Then, targeting this scenario, we design a new type of backdoor attack to induce the model to predict the crack as a normal state. Considering the stealthiness of the attack, a common phenomenon during the welding process, illumination, is used as the backdoor trigger. Experimental results demonstrate that the proposed method can successfully attack the crack detection system and achieve over 90% attack success rate on the test set. T2 - 8th ML4CPS 2025 – Machine Learning for Cyber-Physical Systems CY - Berlin, Germany DA - 06.03,2025 KW - System security KW - Welding crack detection KW - Backdoor attack KW - Deep neural networks PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-651357 DO - https://doi.org/10.24405/20021 VL - 2025 SP - 12 EP - 21 PB - Universitätsbibliothek der HSU/UniBw H CY - Hamburg AN - OPUS4-65135 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ganesh, Rahul A1 - Gesell, Stephan A1 - Kuna, M. A1 - Fedelich, Bernard A1 - Kiefer, B. T1 - Numerical calculation of ΔCTOD for thermomechanical fatigue crack growth N2 - The cyclic crack tip opening displacement ΔCTOD is a promising loading Parameter to quantify the crack propagation under thermomechanical fatigue (TMF). In this work, suitable techniques are investigated and compared for an accurate calculation of ΔCTOD under TMF loading using a viscoplastic temperature dependent material model. It turned out that collapsed special crack tip elements give the best results. An efficient FEM-technique is developed to simulate the incremental crack growth by successive remeshing, whereby the deformations and internal state variables are mapped from the old mesh onto the new one. The developed techniques are demonstrated and discussed for two-dimensional examples like TMF-specimens. Recommendations are made regarding important numerical control parameters like optimal size of crack tip elements, length of crack growth increment in relation to plastic zone size and ΔCTOD value. N2 - Zur Bewertung des Rissfortschritts unter thermomechanischer Ermüdung (TMF) ist die zyklische Rissöffnungsverschiebung ΔCTOD ein aussichtsreicher bruchmechanischer Beanspruchungsparameter. In dieser Arbeit werden unter Anwendung eines viskoplastischen, temperaturabhängigen Materialmodells geeignete FEM-Techniken für die akkurate Berechnung des ΔCTOD bei TMF erprobt und verglichen. Als beste Technik hat sich die Verwendung kollabierter Rissspitzenelemente erwiesen. Es wurde ein effizienter FEM-Algorithmus zur Simulation der Rissausbreitung mit inkrementeller Neuvernetzung entwickelt, bei dem die Verformungen und inelastischen Zustandsvariablen jeweils vom alten auf das neue Netz übertragen werden. Die erarbeiteten Techniken werden am Beispiel von zweidimensionalen Strukturen und TMF-Proben vorgestellt und diskutiert. Dabei werden wesentliche Kontrollparameter der Simulation wie optimale Grösse der Rissspitzenelemente, Länge des Rissinkrementes in Relation zur plastischen Zone und dem ΔCTOD-Wert empfohlen. T2 - 53. Tagung des Arbeitskreises "Bruchmechanik und Bauteilsicherheit" CY - Online meeting DA - 18.02.2021 KW - Crack tip opening displacement KW - Thermomechanical fatigue KW - Crack growth PY - 2021 SP - 1 EP - 10 PB - DVM (Deutscher Verband für Materialforschung und -prüfung) CY - Berlin AN - OPUS4-52519 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ganesh, R. A1 - Gesell, Stephan A1 - Fedelich, Bernard A1 - Kuna, Meinhard A1 - Kiefer, B. T1 - Procrackplast: Eine Software zur Simulation des 3D-Risswachstums unter großen plastischen Deformationen T1 - Procrackplast: A software for simulating 3D crack growth under large plastic deformation N2 - The finite element software ProCrackPlast is developed for the automated simulation of fatigue crack growth in arbitrarily loaded three-dimensional components with large scale plastic deformations, in particular under cyclic thermomechanical (TMF) loading. ProCrackPlast is developed by extending the software Procrack, created at TU Freiberg for linear-elastic crack growth simulations. The pre-processing, FEM analysis, and the post-processing in ProCrackPlast are done by the commercial software ABAQUS. ProCrackPlast resorts to a crack growth procedure which adaptively updates the crack in finite increments based on the fracture-mechanical parameter, cyclic crack tip opening displacement ΔCTOD . Features of this software along with two application examples of fatigue crack growth in a typical cast steel, Ni-Resist, are presented in this paper to show its capability and performance. N2 - Es wird die Finite-Element-Software ProCrackPlast vorgestellt, die eine automatische Simulation der Ermüdungsrissausbreitung in beliebig belasteten dreidimensionalen Bauteilen mit größeren plastisch verformten Bereichen ermöglicht, insbesondere bei thermomechanischer Wechselbelastung (TMF). ProCrackPlast entstand durch Erweiterung des Programs ProCrack, das an der TU Freiberg für linear-elastische inkrementelle Rissfortschrittsanalysen entwickelt wurde. Das Pre-Processing, die FEM Analyse und das Post-Processing werden mit Hilfe der kommerziellen FE-Software ABAQUS durchgeführt. ProCrackPlast beruht auf einem Algorithmus, mit dem der Rissfortschritt adaptiv in endlichen Inkrementen unter Verwendung des bruchmechanischen Parameters der zyklischen Rissöffnungsverschiebung ΔCTOD gesteuert wird. Die Funktionseigenschaften dieser Software werden anhand von zwei Anwendungsbeispielen zum Ermüdungsrisswachstum für einen typischen Stahlguss, Ni-Resist, exemplarisch dargestellt, um die Möglichkeiten und Leistungsfähigkeit von ProCrackPlast zu demonstrieren. T2 - 54. Tagung des Arbeitskreises "Bruchmechanik und Bauteilsicherheit" CY - Online meeting DA - 22.02.2021 KW - Automated finite element analysis KW - Automatische Finite Element Simulation KW - Thermomechanical fatigue KW - Crack growth KW - Thermomechanische Ermüdung KW - Rissausbreitung PY - 2022 SP - 205 EP - 214 PB - Deutscher Verband für Materialforschung und -prüfung e.V. AN - OPUS4-54435 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, M. A1 - Baer, Wolfram A1 - Mayer, U. A1 - Weihe, S. T1 - Untersuchung des Master Curve-Konzepts für ferritisches Gusseisen mit Kugelgraphit N2 - Das Master Curve (MC) Konzept nach ASTM E1921 wird momentan u.a. in der Kerntechnik für die bruchmechanische Sicherheitsbewertung ferritischer Stähle eingesetzt. Für ferritisches Gusseisen mit Kugelgraphit (GJS) fehlt jedoch eine Validierung dieser Methode und ggf. eine systematische Überprüfung möglicher Modifikationen grundlegender Ansätze des MC-Konzepts. Aus diesem Grund soll in einem kürzlich gestarteten BMUV-Verbundprojekt zwischen der MPA Stuttgart und der BAM Berlin die Anwendbarkeit des MC-Konzepts auf GJS bei dynamischer Beanspruchung untersucht werden. Ziel ist es, eine effektive und effiziente Methodik bereitzustellen, mit der mittels einer vergleichsweise kleinen Stichprobe bruchmechanischer Kleinproben eine Referenztemperatur T0 zur werkstoffspezifischen Temperaturjustierung der MC ermittelt werden kann. T2 - 55. Jahrestagung des DVM-Arbeitskreises "Bruchmechanik und Bauteilsicherheit" CY - Darmstadt, Germany DA - 14.02.2023 KW - Dynamische Beanspruchung KW - Bruchmechanik KW - Master Curve-Konzept KW - Gusseisen mit Kugelgraphit PY - 2023 DO - https://doi.org/10.48447/Br-2023-BB SP - 101 EP - 108 PB - DVM Berlin CY - Berlin AN - OPUS4-57024 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram A1 - Breidung, Marc A1 - Kiyak, Yusuf A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Küppers, M. T1 - Aspekte der analytischen bruchmechanischen Bauteilbewertung N2 - Am Beispiel eines abgesetzten zylindrischen Bauteils (Achsschenkel) werden Probleme der analytischen bruchmechanischen Bauteilbewertung diskutiert. Als Basis-philosophie wird ein Fail Safe-Kriterium (kontrolliertes Versagen) angesetzt. Die Forderung ist, dass sich der Achsschenkel, bevor er bricht, in einem Ausmaß plastisch verformen kann, bei dem der Fahrer bemerkt, dass mit seinem Fahrzeug etwas nicht in Ordnung ist. Um das zu gewährleisten, muss der Werkstoff einen bestimmten Riss-widerstand aufweisen. Dazu werden im hier vorgestellten ersten Teil des Projektes mittels FEM Rissspitzenbeanspruchungen in Abhängigkeit von der Auslenkung des Zylinders und angenommener Rissgrößen ermittelt. Diese finden als Zielgrößen in der weiteren Analyse Anwendung. Da eine einfach umzusetzende Lösung angestrebt wird, werden zusätzlich analytische Rechnungen an Ersatzgeometrien (halbunendliche Platte und Vollzylinder), aber mit den realen Spannungen am Bauteil durchgeführt. Es zeigt sich, dass die Ergebnisse wegen des Steifigkeitsunterschieds zwischen Bauteil und Ersatzgeometrie unvertretbar konservativ sind. Alternativ wird ein hybrides Konzept vorgestellt, für das die Modellparameter mittels FEM bestimmt werden. Es liefert sehr genaue Ergebnisse. Im Rahmen der analytischen Rechenvorschrift können die Lösungen auf andere Werkstoffe übertragen werden, ohne dass zusätzliche FEM-Analysen notwendig sind. T2 - 54. Tagung des DVM-Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Online meeting DA - 22.02.2022 KW - FEM KW - Bauteilbewertung KW - Fail-safe KW - Analytisches Modell PY - 2022 DO - https://doi.org/10.48447/Br-2022-BB VL - 254 SP - 1 EP - 11 PB - DVM CY - Berlin AN - OPUS4-54406 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -