TY - JOUR A1 - Vollert, F. A1 - Thomas, Maximilian A1 - Kromm, Arne A1 - Gibmeier, J. T1 - Solidification Cracking Assessment of LTT Filler Materials by Means of Varestraint Testing and μCT N2 - Investigations of the weldability of metals often deal with hot cracking, as one of the most dreaded imperfections during weld fabrication. The hot cracking investigations presented in this paper were carried out as part of a study on the development of low transformation temperature (LTT) weld filler materials. These alloys allow to mitigate tensile residual stresses that usually arise during welding using conventional weld filler materials. By this means, higher fatigue strength and higher lifetimes of the weld can be achieved. However, LTT weld filler materials are for example, high-alloyed Cr/Ni steels that are susceptible to the formation of hot cracks. To assess hot cracking, we applied the standardized modified varestraint transvarestraint hot cracking test (MVT), which is well appropriate to evaluate different base or filler materials with regard to their hot cracking susceptibility. In order to consider the complete material volume for the assessment of hot cracking, we additionally applied microfocus X-ray computer tomography (μCT). It is shown that by a suitable selection of welding and MVT parameter the analysis of the complete 3D hot crack network can provide additional information with regard to the hot cracking model following Prokhorov. It is now possible to determine easy accessible substitute values (e.g., maximum crack depth) for the extent of the Brittleness Temperature Range (BTR) and the minimum critical strain Pmin. KW - LTT weld filler materials KW - μCT-analysis KW - Hot cracking KW - Varestraint test PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-509126 DO - https://doi.org/10.3390/ma13122726 VL - 13 IS - 12 SP - 2726 PB - MDPI AN - OPUS4-50912 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yu, C.-H. A1 - Peng, R. L. A1 - Luzin, V. A1 - Sprengel, Maximilian A1 - Calmunger, M. A1 - Lundgren, J.-E. A1 - Brodin, H. A1 - Kromm, Arne A1 - Moverare, J. T1 - Thin-wall effects and anisotropic deformation mechanisms of an additively manufactured Ni-based superalloy N2 - Laser powder bed fusion (LPBF) of Ni-based superalloys shows great potential for high temperature applications, for example, as a burner repair application for gas turbines where the thin-walled structure is important. It motivates this work to investigate the evolution of microstructure and the anisotropic mechanical behavior when plate-like specimens are built with a thickness from 4 mm down to 1 mm. By performing texture analysis using neutron diffraction, a clear transition in fiber texture from <011> to <001> is indicated when the specimen becomes thinner. The residual stress shows no thickness dependence, and at the subsurface the residual stress reaches the same level as the yield strength. Due to the rough as-built surface, a roughness compensation method for mechanical properties of thin-walled structures is outlined and demonstrated. Tensile tests from room temperature up to 700 ◦C have been carried out. Anisotropic mechanical behavior is found at all temperatures, which is strongly related to the anisotropic texture evolution. Stronger texture evolution and grain rotations are discovered when the tensile loading is applied along the building direction. The mechanical behavior has been compared to a wrought material, where the high dislocation density and the subgrain structure of the LPBF material result in a higher yield strength. Combining the statistical texture analysis by neutron diffraction with mechanical testing, EBSD grain orientation mapping and the investigation of dislocation structures using transmission electron microscopy, this work illustrates the significance of texture for the thin-wall effect and anisotropic mechanical behavior of LPBF materials. KW - Hastelloy X KW - Hot tensile test KW - Crystallographic texture KW - Roughness KW - Residual stress KW - Dislocation density PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-518759 DO - https://doi.org/10.1016/j.addma.2020.101672 VL - 36 SP - 101672 PB - Elsevier B.V. AN - OPUS4-51875 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hensel, J. A1 - Kromm, Arne A1 - Nitschke-Pagel, T. A1 - Dixneit, Jonny A1 - Dilger, K. T1 - Capability of martensitic low transformation temperature welding consumables for increasing the fatigue strength of high strength steel joints N2 - The use of low transformation temperature (LTT) filler materials represents a smart approach for increasing the fatigue strength of welded high strength steel structures apart from the usual procedures of post weld treatment. The main mechanism is based on the effect of the low start temperature of martensite formation on the stress already present during welding. Thus, compressive residual stress formed due to constrained volume expansion in connection with phase transformation become highly effective. Furthermore, the weld metal has a high hardness that can delay the formation of fatigue cracks but also leads to low toughness. Fundamental investigations on the weldability of an LTT filler material are presented in this work, including the characterization of the weld microstructure, its hardness, phase transformation temperature and mechanical properties. Special attention was applied to avoid imperfections in order to ensure a high weld quality for subsequent fatigue testing. Fatigue tests were conducted on the welded joints of the base materials S355J2 and S960QL using conventional filler materials as a comparison to the LTT filler. Butt joints were used with a variation in the weld type (DY-weld and V-weld). In addition, a component-like specimen (longitudinal stiffener) was investigated where the LTT filler material was applied as an additional layer. The joints were characterized with respect to residual stress, its stability during cyclic loading and microstructure. The results show that the application of LTT consumables leads to a significant increase in fatigue strength when basic design guidelines are followed. This enables a benefit from the lightweight design potential of high-strength steel grades. KW - Low transformation temperature KW - Welding KW - Fatigue strength KW - Residual stress PY - 2020 DO - https://doi.org/10.3139/120.111562 VL - 62 IS - 9 SP - 891 EP - 899 PB - Carl Hanser Verlag AN - OPUS4-51180 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Increasing the Significance of Varestraint Tests through Improved Crack Evaluation N2 - The contribution describes a newly developed software tool for crack identification and selection in Modified Varestraint Transvarestraint (MVT) testing. From the digital crack information, in addition to the classical results, such as Total Crack Length (TCL) and Maximum Crack Length (MCL), advanced evaluations can be applied, taking into account the loading and welding parameters. A numerical parameter study is conducted to demonstrate how the isolated variation of individual welding and loading parameters, affects the crack lengths that can potentially be expected based on the machine specifics. An alternative crack criterion is presented that evaluates the crack formation in relation to the machine behavior. Some examples demonstrate the possibilities and limitations of the approach. The criterion can be used to compare and transfer the results of different varestraint test variants. T2 - IIW Annual Assembly, Comission II-C CY - Singapore DA - 17.07.2023 KW - Solidification cracking KW - Varestraint-Test PY - 2023 AN - OPUS4-57984 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Erxleben, Kjell A1 - Kaiser, Sebastian A1 - Rhode, Michael A1 - Kannengiesser, Thomas A1 - Kromm, Arne T1 - In-service and repair welding of pressurized hydrogen pipelines–a review on current challenges and strategies N2 - Hydrogen is the energy carrier for a sustainable future without fossil fuels. As this requires a reliable transportation infrastructure, the conversion of existing natural gas (NG) grids is an essential part of the worldwide individual national hydrogen strategies, in addition to newly erected pipelines. In view of the known effect of hydrogen embrittlement, the compatibility of the materials already in use (typically low-alloy steels in a wide range of strengths and thicknesses) must be investigated. Initial comprehensive studies on the hydrogen compatibility of pipeline materials indicate that these materials can be used to a certain extent. Nevertheless, the material compatibility for hydrogen service is currently of great importance. However, pipelines require frequent maintenance and repair work. In some cases, it is necessary to carry out welding work on pipelines while they are under pressure, e.g., the well-known tapping of NG grids. This in-service welding brings additional challenges for hydrogen operations in terms of additional hydrogen absorption during welding and material compatibility. The challenge can be roughly divided into two parts: (1) the possible austenitization of the inner piping material exposed to hydrogen, which can lead to additional hydrogen absorption, and (2) the welding itself causes an increased temperature range. Both lead to a significantly increased hydrogen solubility in the respective materials compared to room temperature. In that connection, the knowledge on hot tapping on hydrogen pipelines is rare so far due to the missing service experiences. Fundamental experimental investigations are required to investigate the possible transferability of the state-of-the-art concepts from NG to hydrogen pipeline grids. This is necessary to ensure that no critical material degradation occurs due to the potentially increased hydrogen uptake. For this reason, the paper introduces the state of the art in pipeline hot tapping, encompassing current research projects and their individual solution strategies for the problems that may arise for future hydrogen service. Methods of material testing, their limitations, and possible solutions will be presented and discussed. KW - In-service KW - Welding KW - Hydrogen pipeline KW - Review PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-638847 DO - https://doi.org/10.1007/s40194-025-02127-x SN - 0043-2288 SP - 1 EP - 24 PB - Springer Science and Business Media LLC AN - OPUS4-63884 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scharf-Wildenhain, R. A1 - Hälsig, A. A1 - Hensel, J. A1 - Wandtke, Karsten A1 - Schröpfer, Dirk A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Einfluss von Wärmeführung und Bauteildesign auf die Eigenschaften und fertigungsbedingten Beanspruchungen additiv geschweißter hochfester Feinkornbaustähle N2 - Hochfeste Feinkornbaustähle verfügen über großes Potenzial für gewichtsoptimierte, effiziente Strukturen in vielen modernen Stahlkonstruktion. Weitere Effizienzsteigerungen können durch additives Fertigen sowie bionische Bauweisen erreicht werden. Hochfeste Zusatzwerkstoffe für additives MSG-Schweißen (engl.: Wire Arc Additive Manufacturing, WAAM) sind bereits von den Schweißzusatzherstellern lieferbar. Eine breite industrielle Anwendung insbesondere für KMU ist aufgrund fehlender quantitativer Erkenntnisse und Richtlinien bezüglich schweißbedingter Beanspruchungen und Bauteilsicherheit während der Herstellung und des Betriebs derzeit stark limitiert. In einem gemeinsamen Forschungsprojekt (FOSTA-P1380/IGF21162BG) der BAM und der TU Chemnitz werden daher die mit Eigenspannungsausbildung und der Gefahr einer Kaltrissbildung verbundenen prozess- und werkstoffbedingten sowie konstruktiven Einflüsse beim WAAM hochfester Stähle untersucht. Der vorliegende Beitrag fokussiert die Analyse der Auswirkungen von Schweißwärmeführung und Design der WAAM-Bauteile auf die Abkühlbedingungen, Gefüge, mechanisch-technologischen Eigenschaften und Eigenspannungen. Hierfür werden geometrisch definierte Probenkörper (Hohlquader) vollautomatisiert mit einem speziellen, hochfesten WAAM-Massivdraht (Streckgrenze >790 MPa) geschweißt. Die Wärmeführung und Probenabmessungen werden innerhalb eines statistischen Versuchsplans variiert. Die Schweißwärmeführung wird dabei so eingestellt, dass die t8/5-Abkühlzeiten im empfohlenen Verarbeitungsbereich (ca. 5 s bis 20 s) sichergestellt sind. Hierzu ließen sich über zusätzliche thermo-physikalische Umformsimulationen mittels Dilatometer die komplexen Wärmezyklen abbilden und die resultierende Zugfestigkeit des Schweißgutes bestimmen. Das WAAM-Schweißen komplexer Geometrien mit variierenden Schweißwärmeführungen und geometrischen Verhältnissen bzw. Wanddicken bedingt neben den Auswirkungen auf die Abkühlbedingungen, Abkühlzeiten und Gefüge deutliche Einflüsse auf die konstruktiven Steifigkeitsverhältnisse beim Schweißen. Es zeigen sich anhand der Schweißexperimente signifikante Auswirkungen durch Probenskalierung und Wärmeeinbringung auf die resultierenden lokalen Eigenspannungen. Die Folge können ungünstige Bauteileigenschaften und risskritische Zugeigenspannungen sein. T2 - DVS Congress 2022 CY - Koblenz, Germany DA - 19.09.2022 KW - MAG-Schweißen KW - Additive Fertigung KW - Eigenspannungen KW - Hochfester Stahl KW - Kaltrisssicherheit KW - Wärmeführung KW - Windenergie PY - 2022 SN - 978-3-96144-189-1 VL - 382 SP - 737 EP - 745 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-56719 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Projektkurzvorstellung: Bewertung konstruktiv bedingter Erstarrungsrisse beim Schweißen hochfester Feinkornbaustähle N2 - Die Integrität von Leichtbaustrukturen aus hochfesten Stählen ist zunehmend durch die Bildung von Heißrissen gefährdet. Aktuell treten Erstarrungsrisse an Konstruktionsmerkmalen auf, obwohl heißrisssichere niedriglegierte Grund- und Zusatzwerkstoffe als auch Schweißprozessbedingungen eingesetzt wurden. Werkstoff- und prozessseitig wurden diese Rissursachen bereits eingehend erforscht. Untersuchungen zum Aspekt der konstruktiv bedingten Heißrissvermeidung, aus denen sich Empfehlungen für ein beanspruchungsgerechtes Gestalten für KMU ableiten lassen, liegen bislang lückenhaft vor bzw. sind veraltet und für hochfeste Leichtbauten kaum zielführend. Konstruktive Gegenmaßnahmen zur Vermeidung von Erstarrungsrissen liegen oft nicht vor. Das Design und die konstruktiven Randbedingungen beeinflussen die Erstarrungsrisse entscheidend. Um eine schnelle Umsetzbarkeit der Resultate für KMU zu ermöglichen, soll eine einfache und kostengünstige Methodik zur Heißrissbewertung entwickelt werden. Gerade KMU haben einen hohen Nachholbedarf an heißrisssicheren und wirtschaftlichen Leichtbaulösungen. Konstrukteure und Anwender aus KMU würden durch fundierte Kenntnisse über mögliche erstarrungsrisskritische Beanspruchungszustände kostenintensive Qualitätsmängel vermeiden. Das Ziel ist es, Kenngrößen zu identifizieren, die während des Schweißens unter realitätsnahen Bedingungen erfasst werden können. Diese Parameter werden als Transfergrößen genutzt, um eine Heißrissbewertung eines geschweißten Bauteils zu ermöglichen. Anliegen des Vorhabens wird die Prüfung und Bewertung von typischen Beanspruchungszuständen beim Schweißen von Leichtbaustrukturen hinsichtlich ihrer Erstarrungsrissneigung sein. Durch Ableitung klassifizierter Gestaltungshinweise wird ein signifikanter Beitrag zur Steigerung der Wettbewerbsfähigkeit insbesondere für KMU geliefert. Die Ergebnisse werden in Normen zur sicheren schweißtechnischen Fertigung von Leichtbaustrukturen aus hochfesten Stählen direkt einfließen. T2 - Sitzung des NA 092-00-05 GA "Gemeinschaftsarbeitsausschuss NAS/NMP: Zerstörende Prüfung von Schweißverbindungen (DVS AG Q 4/Q 4.1)" CY - Online meeting DA - 10.03.2022 KW - Schweißen KW - Erstarrungsrisse KW - hochfester Stahl PY - 2022 AN - OPUS4-54579 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Increasing the Significance of Varestraint Tests through Improved Crack Evaluation N2 - It was found that there is a systematic dependence of the crack growth on the welding parameters as well as on the load. Decreasing welding speeds with simultaneously higher heat input promote crack formation with increasing strain rate. Based on the results, a new crack criterion was finally selected which allows an extended assessment of the material behavior during the MVT-test. The threshold introduced can quantify the dependencies of the crack formation on the welding and testing parameters, which could not be comprehensively described with the conventional evaluation. In principle, the evaluation routine can also be transferred to other Varestraint or externally loaded hot cracking tests. T2 - IIW Intermediate Meeting Comission II-c CY - Garching, Germany DA - 06.03.2023 KW - Solidification cracking KW - Varestraint-Test PY - 2023 AN - OPUS4-57131 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rhode, Michael A1 - Kromm, Arne A1 - Mente, Tobias A1 - Brackrock, Daniel A1 - Czeskleba, Denis A1 - Kannengießer, Thomas T1 - Component test for the assessment of delayed hydrogen-assisted cracking in thick-walled SAW joints for offshore applications N2 - Offshore wind turbines continuously increase in size and weight and demand adequate offshore foundations concepts like monopiles, tripods, or jackets. These components are typically constructed using submerged arc welding (SAW) with high-strength thick steel plates like the S420ML. During welding, the occurrence of delayed hydrogen-assisted cracking (HAC) must be anticipated. HAC is a critical combination of the local hydrogen concentration within a susceptible microstructure under certain mechanical load, i.e., the occurring (welding) residual stresses. The welding sequence of the thick-walled plates complicates the residual stress distribution due to the necessary repeated thermal cycling, i.e., welding seam/layer deposition to fill the joint. For that purpose, SAW with two-wire-technique was used to weld a specially designed and prototype-like mock-up of a real component with a thickness of 50 mm, filled with over 20 passes and a seam length of 1000 mm. Additional welded stiffeners simulated the effect of a high restraint, to achieve critical HAC conditions. The necessity of a minimum waiting time (MWT) before the NDT can be conducted (to exclude HAC) was critically verified by the application of ultrasonic testing of the welded joint at different time-steps of the NDT of up to 48 h after the completion welding. The residual stresses were determined by a robot XRD goniometer. Tensile residual stresses up to the yield limit are found both in the weld metal and in the heat-affected zone. Numerical modeling allowed the qualitative estimation of the hydrogen diffusion in the weld. No noticeable HAC occurrence was identified and confirms the high cracking resistance of the investigated material. Finally, the applicability of the MWT concept should be critically discussed. KW - Hydrogen KW - Cold cracking KW - Minimum Waiting Time KW - Offshore steel grade KW - Component test PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-591981 DO - https://doi.org/10.1007/s40194-023-01658-5 SP - 1 EP - 15 PB - Springer Science and Business Media LLC AN - OPUS4-59198 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröpfer, Dirk A1 - Witte, Julien A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Stresses in repair welding of high-strength steels—part 1: restraint and cold cracking risk N2 - AbstractThe sustainable and resource-efficient production of wind energy plants requires the use of modern high-strength fine-grain structural steels. This applies to both foundation and erection structures, like mobile or ship cranes. During the assembly of steel structures, unacceptable defects can occasionally be found in the weld area. In most cases, the economical solution would be local thermal gouging of the affected areas and re-welding. Due to the high shrinkage restraint of the joint groove in the overall structure, the superposition of global and local welding-induced stresses may lead to crack formation and component failure, particularly in interaction with the degradation of the microstructure and mechanical properties of high-strength steels during the repair process. However, manufacturers hardly have any information about these issues and there is a lack of recommendations and guidelines to take these safety-relevant aspects into account in adequate repair concepts. The aim of this research is to derive recommendations for repair concepts appropriate to the stresses and materials involved providing a basis for standards and guidelines to avoid cold cracking, damage and expensive reworking especially for high-strength steels. Part 1 of this study involves systematic investigations of influences of shrinkage restraint during repair welding of two high-strength steels S500MLO for offshore application and S960QL for mobile crane structures. The quantification of the shrinkage restraint of repair weld joints was achieved by means of experimental and numerical restraint intensity analysis. In welding experiments with self-restrained slot specimens, restraint intensity and introduction of hydrogen via the welding arc using anti spatter spray were varied systematically to analyse the effect on welding result, residual stresses and cold cracking. It could be shown that increasing restraint intensities result in significantly higher transverse residual stress levels. In the case of hydrogen introduction S500MLO showed no cold cracking independent of the restraint conditions. However, S960QL was found to be considerably cold cracking sensitive if hydrogen is introduced. With increasing restraint intensity length and number of cold cracks increases significantly. Part 2 [1] of this study is focussed on microstructure and residual stresses due to gouging and stress optimization via adequate heat control parameters in repair welding. KW - Metals and Alloys KW - Mechanical Engineering KW - Mechanics of Materials PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-595212 DO - https://doi.org/10.1007/s40194-024-01691-y SN - 0043-2288 SP - 1 EP - 13 PB - Springer Science and Business Media LLC AN - OPUS4-59521 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröpfer, Dirk A1 - Witte, Julien A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Stresses in repair welding of high-strength steels—part 2: heat control and stress optimization N2 - In welding of high-strength steels, e.g. for foundations and erection structures of wind energy plants, unacceptable defects can occasionally be found in the weld area, which should be removed by thermal gouging and subsequent re-welding. High shrinkage restraint of repair welds may lead to crack formation and component failure, predominantly in interaction with degraded microstructures and mechanical properties due to repair cycles. This study aims for elaboration of recommendations for repair concepts appropriate to the stresses and materials involved to avoid cold cracking, damage and expensive reworking. In part 1 [1] of this study, systematic investigations of influences of shrinkage restraint on residual stresses and cold cracking risk during repair welding of two high-strength steels S500MLO for offshore application and S960QL for mobile crane structures were focussed. In this part 2, the microstructure, particularly hardness, and residual stresses due to gouging and influences of heat control parameters in repair welding are analysed. A clear reduction in residual stress after gouging can be observed, especially for the specimens with restrained transverse shrinkage. Gouging to a depth of approx. 2/3 of the seam height does not lead to a complete relaxation of the observed reaction forces. Particularly for the higher strength steel S960QL, there are pronounced areas influenced by the gouging process in which a degradation of the microstructure and properties should be assumed. Overall, the repair welds show a significant increase in the width of the weld and HAZ compared to the original weld, especially in the case of S960QL/G89. The repair welds show higher welding-induced stresses than the original welds, especially in the areas of the HAZ and the base metal close to the weld seam. This behaviour can be attributed overall to increased restraint conditions due to the remaining root weld or shorter gouge grooves. In good agreement with earlier investigations, the residual stresses transverse to the weld can be significantly reduced by upwardly limited working or interpass temperatures, and the reaction stresses resulting from high restraint conditions can be effectively counteracted. The influence of the heat input on the stress formation is low compared to the interpass temperature for both test materials. KW - Repair-welding KW - Wind Energy KW - High-strength steels KW - Cold cracking KW - Residual stresses KW - Offshore steels PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-600259 DO - https://doi.org/10.1007/s40194-024-01731-7 SN - 0043-2288 SP - 1 EP - 15 PB - Springer Nature AN - OPUS4-60025 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Influence of residual stresses and heat control on stress relief cracking in a CrMoV steel mockup N2 - Preventing failures in the manufacture or operation of petrochemical reactors made from creep-resistant, low-alloy steels such as 13CrMoV9-10 still requires research, despite over 60 years of investigation into the field of stress relief cracking. Welding this steel grade requires care. This is due to its low toughness and high strength in the welded condition if not heat treated after welding, combined with an increased susceptibility to cracking during stress relaxation. Previous research on cracking in creep resistant steels has focused on thermal and metallurgical factors; however, little knowledge has been gained on cracking under real-life restraint conditions. In this work, the influence of welding heat control on cracking was investigated by simulating the manufacturing conditions prevailing in the construction of petrochemical reactors using a special weld mockup. The application of acoustic emission analysis showed that cracks formed during post-weld heat treatment in a temperature range between 300 °C and 500 °C. Compared to small scale samples, the toughness of the restrained welds was significantly lower. SEM and TEM analyses of all samples revealed early ageing due to early precipitation of special carbides during post-weld heat treatment under restraint. Neutron diffraction experiments showed that the residual stresses in the weld seam reach the yield point of the material. The presentation provides an overview of how a comprehensive assessment of the integrity of submerged arc welded CrMoV steels can be achieved in the laboratory. T2 - Cracking Phenomena in Welding and Additive Manufacturing 2025 CY - Trollhättan, Sweden DA - 12.03.2025 KW - CrMoV KW - Stress Relief Cracking KW - Sub-merged arc welding PY - 2025 AN - OPUS4-62783 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Assessing ferrite content in duplex stainless steel weld metals: WRC '92 predictions vs. practical measurements N2 - The weldability of stainless steels is largely controlled by the chemical composition, and alloys with ferritic or ferritic-austenitic solidification show the highest resistance to hot cracking. As the resulting phase balance also affects the final properties, it may be beneficial to both foresee and measure the weld metal ferrite content. The WRC ’92 constitution diagram is currently the most accurate prediction tool available, but it does not take the cooling rate into consideration and the precision may be less accurate for stainless steels with high ferrite numbers (FN). This study aims to validate the reliability of the WRC ’92 diagram for weld metals with FN > 50. The chemical composition was altered through gas tungsten arc welding (GTAW) of UNS S32205 with ER347 filler wire that had been PVD-coated with either niobium (Nb), copper (Cu), nickel (Ni), manganese (Mn), carbon (C), or silicon (Si). The actual ferrite content was assessed using image analysis, FERITSCOPE® and X-ray diffraction (XRD). While the WRC ’92 diagram predictions were deemed accurate to acceptable for Ni, Si, and Mn, notable deviations were observed for Nb, Cu, and C. The FeriteScope exhibited a consistent trend with image analysis, though the values were higher, and scatter was wider, and the conversion factor is open for discussion. The lowest accuracy and largest spread were obtained using non-contact XRD, rendering it unsuitable for ferrite measurements of welds. T2 - IIW Intermediate Meeting Comission IX-H CY - Incheon, Republic of Korea DA - 12.03.2024 KW - Duplex Stainless Steel KW - Ferrite KW - WRC 92 PY - 2024 AN - OPUS4-59750 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Kannengießer, Thomas A1 - Kromm, Arne A1 - Dixneit, Jonny A1 - Dilger, K. A1 - Nitschke-Pagel, T. A1 - Hensel, J. A1 - Eslami, H. T1 - Schwingfestigkeitsverbesserung hochfester Schweißverbindungen mit Hilfe neuartiger LTT-Zusatzwerkstoffe N2 - Die Verwendung von LTT-Zusatzwerkstoffen stellt einen alternativen Ansatz zu den sonst üblichen Verfahren der Schweißnahtnachbehandlung zur Schwingfestigkeitserhöhung geschweißter Stahlkonstruktionen dar. Der wesentliche Wirkmechanismus beruht auf der Beeinflussung des Eigenspannungszustands durch die niedrige Martensitstarttemperatur bereits während des Schweißens. Dadurch werden die Druckeigenspannungen aus der behinderten Volumenausdehnung infolge Phasenumwandlung voll wirksam. Weiter weist die Schweißnaht eine hohe Härte auf, die die Schwingrissbildung verzögern kann, allerdings auch zu einer niedrigen Kerbschlagarbeit führt. Im vorliegenden Forschungsvorhaben wurden grundlegende Untersuchungen zur schweißtechnischen Verarbeitung eines LTT-Zusatzwerkstoffes durchgeführt. Dies beinhaltet die Sicherstellung der Schweißbarkeit sowie die Charakterisierung der Verbindungseigenschaften. Untersuchungen zur Schweißeignung machten deutlich, dass ein sicherer Einsatz in dem für hochfeste Stähle zur Verfügung stehenden Arbeitsfenster möglich ist. Der verwendete LTT-Zusatz auf Cr-Ni-Basis lässt sich mit hoher Nahtgüte fügen. Auch die mechanischen Eigenschaften erlauben den Einsatz im Bereich hochfester Stähle mit einer Streckgrenze von 960 MPa. Entwicklungspotential gibt es hinsichtlich der Zähigkeit. Die in dieser Arbeit erreichten Kerbschlagwerte liegen deutlich unter denen kommerziell verfügbarer konventioneller Schweißgüter. Die Untersuchungen belegen, dass der Effekt der martensitischen Phasenumwandlung im gesamten Schweißgut zum Tragen kommt. Die angestrebten hohen Druckeigenspannungen finden sich vornehmlich im Schweißgutinnern. Im weiteren Vorgehen wurden Schwingfestigkeitsuntersuchungen an den Stählen S355J2 und S960Q unter Verwendung konventioneller Zusatzwerkstoffe im Vergleich zum LTT-Zusatz durchgeführt. Die verwendeten Konstruktionsdetails sind ein Stumpfstoß unter Variation der Schweißnahtausführung (DY-Naht und V-Naht), ein Kreuzstoß mit HV-Naht sowie ein Überlappstoß mit einseitig und beidseitig geschweißter Kehlnaht. Weitergehend wurde eine bauteilähnliche Probe (die Längssteife) untersucht, bei der der LTT-Zusatzwerkstoff als zusätzliche Schweißlage aufgebracht wurde. Neben der Schwingfestigkeit wurden die Schweißnähte hinsichtlich der Eigenspannungen, der Eigenspannungsstabilität im Schwingversuch sowie metallografisch charakterisiert. Eine generell positive Wirkung des LTT-Zusatzwerkstoffes im Hinblick auf die Schwingfestigkeitssteigerung kann nicht bestätigt werden. Teilweise ist eine Steigerung der Schwingfestigkeit bei Substitution konventioneller Zusatzwerkstoffe zu beobachten, teilweise zeigt sich kein Effekt. Ursächlich hierfür ist die bei manchen Stoßformen mangelnde Steifigkeit quer zur Schweißnaht, die zur Ausbildung hoher Druckeigenspannungen infolge Phasenumwandlung notwendig wäre. Die bauteilähnliche Längssteife bestätigt allerdings das grundlegende Potential der LTT-Zusatzwerkstoffe bei Vorliegen hinreichender Steifigkeit. KW - Schweißen KW - Eigenspannungen KW - Schwingfestigkeit KW - Hochfester Stahl KW - LTT PY - 2020 UR - https://matplus.shop/produkt/p-1060-schwingfestigkeitsverbesserung-hochfester-schweissverbindungen-mit-hilfe-neuartiger-ltt-zusatzwerkstoffe SN - 978-3-946885-75-7 VL - P 1060 SP - 1 EP - 123 PB - Verlag und Vertriebsgesellschaft CY - Düsseldorf AN - OPUS4-51216 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Einfluss der Schweiß- und Prüfparameter bei der Heißrissbewertung hochfester Schweißzusatzwerkstoffe N2 - Die Heißrissneigung beim Schweißen kann mittels einer ganzen Reihe von Prüfverfahren ermittelt werden. Eine etablierte Methode ist die sogenannte Varestraint-Prüfung, welche auch an der Bundesanstalt für Materialforschung und -prüfung (BAM) als modifizierter Varestraint/Transvarestraint-Test (MVT) zum Einsatz kommt. Die Ergebnisse von Varestraint-Prüfungen hängen jedoch stets in unterschiedlichem Maße von der individuellen Prüfmaschinenauslegung und den verwendeten Prüfparametern ab. Dies kann zu einer uneinheitlichen Bewertung des Rissverhaltens führen, wenn die Risslänge konventionell als Kriterium für die Rissneigung herangezogen wird. Scheinbare Abhängigkeiten von Prozessparametern erschweren dann die Interpretation der Ergebnisse. Eine neuartige Bewertungsmethodik entkoppelt den Maschineneinfluss vom Materialverhalten und verwendet die Dehnrate als Risskriterium in Analogie zu Prokhorovs Heißrissmodell. Die neue Auswertung wird anhand einer Studie hochfester Schweißzusatzwerkstoffe vorgestellt, deren Rissverhalten in Abhängigkeit der chemischen Zusammensetzung und der Schweißparameter bewertet wird. T2 - 5. Symposium Materialtechnik CY - Clausthal-Zellerfeld, Germany DA - 23.02.2023 KW - Heißrisse KW - Varestraint-Test KW - Materialprüfung PY - 2023 AN - OPUS4-57070 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Phase Transformation and Strain Evolution during Welding of Low Transformation Temperature Alloys N2 - In this work, the phase and strain formation in multipass welding of LTT gas metal arc welds were observed under realistic restraints by means of time resolved angular-dispersive synchrotron X-ray diffraction at the High Energy Materials Science beamline HEMS at PETRA III (DESY), Hamburg Germany. It was shown that the strain evolution during cooling correlates with the amount of martensite formed. Both, the strain of martensite and austenite are affected during phase transformation. Even though dilution processes limit the LTT effect in the root compared to the top layer, the strains are significantly reduced compared to the conventional weld metal. The observed effects are found for both Ni and Mn based LTT filler metals regardless of their respective Ms temperature. T2 - 2nd International Conference on Advanced Joining Processes AJP 2021 CY - Sintra, Portugal DA - 21.10.2021 KW - Welding KW - Residual Stress KW - In-situ diffraction KW - Synchrotron PY - 2021 AN - OPUS4-53609 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Erxleben, Kjell A1 - Kaiser, Sebastian A1 - Rhode, Michael A1 - Kannengiesser, Thomas A1 - Kromm, Arne T1 - In-service and repair welding of pressurized hydrogen pipelines–a review on current challenges and strategies N2 - Hydrogen is the energy carrier for a sustainable future without fossil fuels. As this requires a reliable transportation infrastructure, the conversion of existing natural gas (NG) grids is an essential part of the worldwide individual national hydrogen strategies, in addition to newly erected pipelines. In view of the known effect of hydrogen embrittlement, the compatibility of the materials already in use (typically low-alloy steels in a wide range of strengths and thicknesses) must be investigated. Initial comprehensive studies on the hydrogen compatibility of pipeline materials indicate that these materials can be used to a certain extent. Nevertheless, the material compatibility for hydrogen service is currently of great importance. However, pipelines require frequent maintenance and repair work. In some cases, it is necessary to carry out welding work on pipelines while they are under pressure, e.g., the well-known tapping of NG grids. This in-service welding brings additional challenges for hydrogen operations in terms of additional hydrogen absorption during welding and material compatibility. The challenge can be roughly divided into two parts: (1) the possible austenitization of the inner piping material exposed to hydrogen, which can lead to additional hydrogen absorption, and (2) the welding itself causes an increased temperature range. Both lead to a significantly increased hydrogen solubility in the respective materials compared to room temperature. In that connection, the knowledge on hot tapping on hydrogen pipelines is rare so far due to the missing service experiences. Fundamental experimental investigations are required to investigate the possible transferability of the state-of-the-art concepts from NG to hydrogen pipeline grids. This is necessary to ensure that no critical material degradation occurs due to the potentially increased hydrogen uptake. For this reason, the paper introduces the state of the art in pipeline hot tapping, encompassing current research projects and their individual solution strategies for the problems that may arise for future hydrogen service. Methods of material testing, their limitations, and possible solutions will be presented and discussed. KW - In-service KW - Hydrogen KW - Repair welding KW - Pipeline PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-638944 DO - https://doi.org/10.1007/s40194-025-02127-x SN - 0043-2288 SP - 1 EP - 24 PB - Springer Science and Business Media LLC AN - OPUS4-63894 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Large scale hydrogen assisted cracking test for thick walled SAW joints for offshore applications N2 - Offshore wind turbines continuously increase in size and weight and demand adequate offshore foundations concepts like monopiles, tripods or jackets. These components are typically submerged arc welded (SAW) high-strength thick steel plates like the S420ML. During welding, the occurrence of delayed hydrogen assisted cracking (HAC) must be anticipated. HAC is a critical combination of the local hydrogen concentration within a susceptible microstructure under certain mechanical load, i.e., the occurring (welding) residual stresses. The welding sequence of the thick-walled plates complicate the residual stress distribution due to the necessary repeated thermal cycling, i.e., welding seam / layer deposition to fill the joint. For that purpose, SAW with two-wire-technique was used to weld a specially designed and prototype-like mock-up of a real component with a thickness of 50 mm, filled more than 20 passes and a seam length of 1,000 mm. Additional welded stiffeners simulated the effect of a high restraint, to stimulate critical HAC conditions. The necessity of a minimum waiting time (MWT) before the NDT can be conducted (to exclude HAC) was critically verified by the application of ultrasonic testing of the welded joint at different time-steps of the NDT of 48 h after welding. The residual stresses were determined by a robot XRD goniometer. Tensile residual stresses up to the yield limit are found both in the weld metal and in the heat-affected zone. Numerical modelling allowed the qualitative estimation of the hydrogen diffusion in the weld. A remarkable HAC occurrence was not identified and proves both, a certain resistance of the weld joint to HAC and the (questionable) duration of the MWT. T2 - IIW Intermediate Meeting of Commission II-A CY - Garching, Germany DA - 06.03.2023 KW - Hydrogen assisted cracking KW - Submerged arc welding KW - Offshore wind turbine KW - High-strength steel KW - Component test PY - 2023 AN - OPUS4-57100 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröpfer, Dirk A1 - Kromm, Arne A1 - Lausch, Thomas A1 - Rhode, Michael A1 - Wimpory, R. C. A1 - Kannengießer, Thomas T1 - Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel: Part III - Assessment of residual stresses from small-scale to real component welds N2 - For higher operational temperatures and pressures required in petrochemical plants, the modified 13CrMoV9-10 steel was developed providing high resistance against creep and compressed hydrogen. Extreme care during the welding procedure is necessary for this steel, attributed to low toughness, high strength in as-welded state, and increased susceptibility to stress relief cracking (SRC) during post-weld heat treatment (PWHT). Previous research of SRC in creep-resistant steels discussed mainly thermal and metallurgical factors. Few previous findings addressed the influences of welding procedure on crack formation during PWHT considering real-life manufacturing conditions. These investigations focus on effects of welding heat control on stresses during welding and subsequent PWHT operations close to realistic restraint and heat dissipation conditions using a special 3D testing facility, which was presented in parts I and II of this contribution. Part III addresses investigations on residual stress evolution affecting crack formation and discusses the transferability of results from large-scale testing to laboratory-scale. Experiments with test set-ups at different scales under diverse rigidity conditions and an assessment of the residual stresses of the weld-specimens using X-ray (surface near) and neutron diffraction analysis (bulk) were performed. This study aims to provide a way of investigating the SRC behaviour considering component-specific residual stresses via small-scale testing concepts instead of expensive weld mock-ups. KW - Welding KW - Creep-resistant steel KW - Residual stresses KW - Post-weld heat treatment KW - Stress relief cracking PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-524403 DO - https://doi.org/10.1007/s40194-021-01101-7 SN - 1878-6669 VL - 65 SP - 1671 EP - 1685 PB - Springer CY - Berlin AN - OPUS4-52440 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erxleben, Kjell A1 - Kaiser, Sebastian A1 - Rhode, Michael A1 - Kannengießer, Thomas A1 - Kromm, Arne T1 - Reparaturschweißen zukünftiger, in Betrieb befindlicher Wasserstoffpipelines N2 - Wasserstoff leistet als Energieträger der Zukunft einen entscheidenden Beitrag zur nachhaltigen Energieversorgung, wobei der Transport auf Basis des europäischen Ferngasleitungsnetzes erfolgen wird. Bisherige Untersuchungen zur Werkstoffkompatibilität zeigen, dass die hier verwendeten, niedriglegierten Rohrstähle für Wasserstofftransport unter normalen Betriebsbedingungen (≤ 60 °C, max. 100 bar) grundsätzlich geeignet sind. Die Eignung kann nicht ohne Weiteres übertragen werden, sobald Reparaturschweißungen beispielsweise aufgrund von Wartungsarbeiten an druckführenden, in Betrieb befindlichen, Hochdruckgasleitungen erfolgen. Aus technisch-ökonomischen Gründen werden Schweißarbeiten dabei im Betrieb unter fortwährendem Druck und Gasfluss durchgeführt. Dies soll auch bei Wasserstoffpipelines erfolgen. Dazu im Erdgasnetz angewandte und etablierte Konzepte sind beispielsweise das „Hot-Tapping“ und „Stoppling“. Beim „Hot-Tapping“ wird eine druckführende Pipeline durch Anflanschen eines abgeschlossenen, druckdichten Systems aus Absperrventil und Bohrvorrichtung angebohrt. Dazu müssen sogenannte Überschieber (aus vorgeformten Zylinderhalbschalen) durch Längsnaht verbunden und dann mit Rohrrundnähten am Produktrohr verbunden werden. Für das zum überwiegenden Teil durchgeführte E-Hand-Schweißen sind dabei Vorwärmtemperaturen von ca. 100 °C bzw. 250 °C für die maximale Zwischenlagentemperatur einzuhalten. Besonderer Fokus liegt auf der Betrachtung dünnwandiger Leitungen, da hier beim Schweißen der Rundnähte die Austenitisierungstemperatur an der Innenseite der Pipeline überschritten wird. Dadurch wird eine signifikant höhere Wasserstoffaufnahme in den Leitungsstahl vermutet, mit einer möglichen Degradation der mechanischen Kennwerte bzw. Rissbildung. Durch die langen Schweiß- und Abkühlzeiten wird der Rohrleitungsstahl zudem teilweise stundenlang Temperaturen von bis zu 250 °C ausgesetzt. Neben der klassischen „Versprödung“ muss daher eventuell auch ein sogenannter Hochtemperatur-Wasserstoffangriff betrachtet werden. Diese vorliegende Studie gibt Einblick zur Übertragbarkeit der bekannten Konzepte aus der Erdgastechnik zum Reparaturschweißen. Dazu werden Möglichkeiten und Grenzen momentaner Prüfkonzepte sowie deren Weiterentwicklungen aufgezeigt. Dies umfasst bspw. geeignete Methodiken zur Werkstoffprüfung als auch skalierte Bauteilversuche unter realistischen Druckgas-Betriebsbedingungen einer Pipeline. In diesem Rahmen erfolgt auch die Kurzvorstellung des Kooperationsprojektes von BAM, DVGW und Ferngasnetzbetreibern „H2-SuD“ zum Einfluss der Temperaturführung und Rohrgeometrie auf die Wasserstoffaufnahme. T2 - DVS CONGRESS 2024 CY - Erfurt, Germany DA - 16.09.2024 KW - Reparaturschweißen KW - Pipeline KW - Wasserstoff KW - Im Betrieb PY - 2024 SN - 978-3-96144-269-0 VL - 395 SP - 341 EP - 349 AN - OPUS4-61478 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Becker, Amadeus A1 - Schröpfer, Dirk A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Determination of residual stress evolution during repair welding of high-strength steel components N2 - During the assembly of steel structures, unacceptable weld defects may be found. An economical solution is local thermal gouging of the affected areas and re-welding. Due to high shrinkage restraints of repair weld and sur- rounding structure, high global and local welding stresses superimpose, and may lead to cracking and component failure, especially in connection with the degraded microstructure and mechanical properties of high-strength steels during the repair process. Component-related investigations of high-strength steels (FOSTA P1311/ IGF20162N) focus on welding residual stress evolution during local thermal gouging and rewelding. In this study, repair welding of S500MLO (EN 10225) is carried out using in-situ digital image correlation (DIC) and ex- situ X-ray diffraction (XRD) to analyse strains and stresses. Self-restrained slit specimen geometries were identified representing defined rigidity conditions of repair welds of real components, which were quantified using the restraint intensity concept. The specimens were rewelded with constant welding heat control and parameters. Weld specimens exhibited significantly increased transverse residual stresses with higher transverse restraint intensities, in the weld metal, and in the heat affected zone. Transverse stresses along the weld seam decrease at the weld seam ends leading to different stress state during gouging and welding. XRD analysis of the longitudinal and transverse local residual stresses after cooling to RT showed a good comparability with global DIC analyses. KW - Repair-welding KW - High-strength steels KW - X-ray diffraction KW - Digital image correlation KW - Residual stresses PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-555672 DO - https://doi.org/10.1016/j.finmec.2022.100073 SN - 2666-3597 VL - 6 SP - 1 EP - 6 PB - Elsevier CY - Amsterdam AN - OPUS4-55567 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Nina A1 - Kromm, Arne A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas T1 - Innovatives Instandsetzungsschweißen von Altstahl: Materialverhalten und Herausforderungen N2 - Aus Gründen der Nachhaltigkeit und Wirtschaftlichkeit gibt es in der stahlverarbeiten-den Industrie einen Trend zum Bauen im Bestand, um kostenintensive Sperrungen oder Rückbau zu vermeiden. Schweißen wird dabei als wirtschaftliches Fügeverfahren im Zusammenhang mit Altstählen kaum genutzt, obwohl Nieten- und Schraubenverbindungen oft unwirtschaftlich sind. Für die Instandsetzung ist häufig beschädigtes Bestands-material durch neue Stähle zu ersetzen bzw. Alt-Neu-Stahl-Mischverbindungen herzu-stellen. Aufgrund der verschiedenen Herstellungsprozesse von Altstählen ist nicht jeder Stahl aus dem 20. Jahrhundert schweißgeeignet. Daher ist zunächst eine Schweißeignungsprüfung erforderlich. In den vorliegenden Untersuchungen wurden verschiedene Altstähle hinsichtlich ihres Schweißverhaltens mittels Dilatometrie analysiert. Ziel war es, eine Datenbasis aus Schweiß-Zustands-Zeit-Diagrammen und Simulationen der Wärmeeinflusszone zu erstellen, um praxisrelevante Schweißuntersuchungen ableiten zu können. Diese geben wesentlichen Aufschluss hinsichtlich ihres schweißmetallurgischen Verhaltens und ihrer Schweißeignung. Solche Grundlagen sind zur Entwicklung innovativer schweißtechnischer Konzepte zur beanspruchungsgerechten Instandsetzung bestehender Altstahl-Infrastruktur in Deutschland notwendig. T2 - 6. Symposium Materialtechnik, 20. bis 21. Februar 2025 CY - Clausthal-Zellerfeld, Germany DA - 20.02.2025 KW - Altstahl KW - Schweiß-ZTU Diagramme KW - Instandsetzungsschweißen KW - Schweißeignungsprüfung KW - Dilatometrie PY - 2025 SN - 978-3-8440-9961-4 DO - https://doi.org/10.21268/20250505-1 VL - 15 SP - 370 EP - 380 PB - Shaker Verlag GmbH CY - Düren AN - OPUS4-63377 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kromm, Arne A1 - Lausch, Thomas A1 - Schröpfer, Dirk A1 - Rhode, Michael A1 - Kannengießer, Thomas T1 - Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel: Part II - Mechanisms of stress relief cracking during post weld heat treatment N2 - Welding of 13CrMoV9-10 vanadium steel requires care due to an increased susceptibility to stress relief cracking during post weld heat treatment. Previous research into the crack formation in creep-resistant steels has focused on thermal and metallurgical factors; however, little knowledge has been gathered regarding the crack formation during post weld heat treatment considering real-life restraint conditions. This work is subdivided in two parts. Part I showed that an increasing heat input during submerged arc welding under restraint led to an increasing stress level in the joint prior to the post weld heat treatment. The magnitude of stress relief cracking observed in the heat-affected zone after the post weld heat treatment is affected by the heat input. In Part II of this work, the cracks and the associated microstructure which occurred under restraint were studied. The application of a Special acoustic emission analysis indicated that the cracks formed in a temperature range between 300 and 500 °C during the post weld heat treatment. The toughness in the heat-affected zone of the restrained welds was affected by the welding heat input. Microstructural analyses of all specimens revealed accelerated aging due to precipitation of carbides during post weld heat treatment under restraint. KW - Welding KW - Creep-resistant steel KW - Post weld heat treatment KW - Stress relief cracking PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-506283 DO - https://doi.org/10.1007/s40194-020-00881-8 SN - 1878-6669 VL - 64 SP - 819 EP - 829 PB - Springer CY - Berlin AN - OPUS4-50628 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kromm, Arne A1 - Lausch, Thomas A1 - Schröpfer, Dirk A1 - Rhode, Michael A1 - Kannengießer, Thomas T1 - Influence of welding stresses on relief cracking during heat treatment of a creep-resistant 13CrMoV steel: Part I - Effect of heat control on welding stresses and stress relief cracking N2 - The avoidance of failures during the fabrication or operation of petrochemical reactors made of creep-resistant, low-alloy steels as 13CrMoV9-10 requires still research despite over 60 years of international investigations in the field of stress relief cracking. The quality of modern base materials and filler metals leads to the fact that previously known crack causes, such as impurities of S or P, recede into the background. Rather, the causes are increasingly to be found in the fabrication process. Investigations on the influence of heat control on the stresses in welded components and thus on the stress relief cracking sensitivity under realistic manufacturing conditions are not yet available. This work is subdivided in two parts. Part 1 of this study focused on the effect of heat control during submerged arc welding on the stresses. For this purpose, a testing facility was applied, which allows to observe the forces and moments accumulating during welding or heat treatment in a component-like specimen under shrinkage restraint. The stress acting in the specimen increases with higher preheat/interpass temperatures and higher heat input. During the heat treatment, the stresses are relieved. Nevertheless, cracks are formed already during heating. The total crack length correlates with the heat input. KW - Welding KW - Creep-resistant steel KW - Post weld heat treatment KW - Stress relief cracking PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-506271 DO - https://doi.org/10.1007/s40194-020-00875-6 SN - 1878-6669 VL - 64 IS - 5 SP - 807 EP - 817 PB - Springer CY - Berlin AN - OPUS4-50627 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Kurzvorstellung des Projektes H2SuD / Wasserstoff und Schweißen Einfluss des Schweißens auf die Wasserstoffaufnahme und Degradation im Betrieb befindlicher H2 Gasleitungen N2 - Die Wasserstoffinfrastruktur ist eine zentraler Bestandteil der erfolgreichen Umsetzung der wasserstoffbasierten Energiewende. Dabei bilden Ferngasleitungen quasi das "Rückgrat" der Transportinfrastruktur großer Gasmengen. Dabei müssen unter Umständen Reparaturen an den Pipelines durchgeführt werden. Dabei ist in der Erdgasinfrastruktur das Schweißen an in Betrieb befindlichen (d.h. von Gas durchflossenen) Pipelines Stand der Technik. Es ist jedoch vollkommen offen, inwieweit diese Technik auf die reine Wasserstoffpipelines übertragbar sind. Hierzu leistet das Projekt H2SuD wichtige Beiträge zur Aufklärung des Einfluss eines Reparaturschweißprozesses auf die Wasserstoffaufnahme und Degradation im Betrieb befindlicher H2 Gasleitungen. T2 - Sitzung des DIN-Gemeinschaftsarbeitsausschusses NA 092 00 05 GA, NAS/NMP: Zerstörende Prüfung von Schweißverbindungen CY - Berlin, Germany DA - 15.03.2023 KW - Wasserstoff KW - Pipeline KW - Reparatur KW - Schweißen PY - 2023 AN - OPUS4-57169 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne A1 - Thomas, Maximilian A1 - Liepold, Philipp A1 - Kannengießer, Thomas A1 - Schröpfer, Dirk T1 - Einfluss der Schweiß- und Prüfparameter bei der Heißrissbewertung hochfester Schweißzusatzwerkstoffe N2 - Die Heißrissneigung beim Schweißen kann mittels einer ganzen Reihe von Prüfverfahren ermittelt werden. Eine etablierte Methode ist die sogenannte Varestraint-Prüfung, welche auch an der Bundesanstalt für Materialforschung und -prüfung (BAM) als modifizierter Varestraint/Transvarestraint-Test (MVT) zum Einsatz kommt. Die Ergebnisse von Varestraint-Prüfungen hängen jedoch stets in unter-schiedlichem Maße von der individuellen Prüfmaschinenauslegung und den verwendeten Prüfparametern ab. Dies kann zu einer uneinheitlichen Bewertung des Rissverhaltens führen, wenn die Risslänge konventionell als Kriterium für die Rissneigung herangezogen wird. Scheinbare Abhängigkeiten von Prozessparametern erschweren dann die Interpretation der Ergebnisse. Eine neuartige Bewertungsmethodik entkoppelt den Maschineneinfluss vom Materialverhalten und verwendet die Dehnrate als Risskriterium. T2 - 5. Symposium Materialtechnik CY - Clausthal-Zellerfeld, Germany DA - 23.02.2023 KW - Heißrisse KW - Varestraint-Test PY - 2023 SN - 978-3-8440-9105-2 SN - 2364-0804 VL - 12 SP - 357 EP - 365 PB - Shaker CY - Düren AN - OPUS4-57993 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Kromm, Arne A1 - Mente, Tobias A1 - Czeskleba, Denis A1 - Brackrock, Daniel A1 - Kannengießer, Thomas T1 - Bauteilversuch zur Bewertung der wasserstoffunterstützten Rissanfälligkeit geschweißter, dickwandiger Offshore-Gründungsstrukturen N2 - Offshore-Windenergieanlagen erfordern Gründungskonzepte aus unterpulver-(UP-)geschweißten Dickblechen (bspw. der Güte S420ML). Während der Schweißfertigung kann eine zeitverzögerte wasserstoffunterstützte Kaltrissbildung auftreten, deren Bewertung aufgrund der Bauteilgröße von Offshore-Strukturen sehr komplex ist. Deswegen wurde eine bauteilähnliche Geometrie (Mock-Up) entwickelt, um reale Steifigkeitsverhältnisse auf den Labormaßstab zu übertragen. Zusätzliche Versteifungen simulieren die Wirkung einer Einspannung bzw. Schrumpfbehinderung der Schweißnaht. Über die Verwendung von Schweißpulvern mit definierter Feuchte wurden zudem ein Extremszenario der Wasserstoffaufnahme simuliert. Entsprechend der vorgegebenen Mindestwartezeit für die ZfP von bis zu 48 h wurde die Schweißnaht zerstörungsfrei mit Phased-Array-Ultraschall-Prüfung (PAUT) geprüft und die Eigenspannungen über Röntgendiffraktometrie (XRD) bestimmt. Zusätzlich wurde die Wasserstoffverteilung in der Schweißverbindung numerisch simuliert. Außer zulässigen Defekten (wie Poren), wurde keine verzögerte Kaltrissbildung in den Mock-Ups festgestellt, was auf hohe Rissbeständigkeit hindeutet. T2 - Tagung Werkstoffprüfung 2023 CY - Berlin, Germany DA - 23.11.2023 KW - Kaltrissbildung KW - Wasserstoff KW - Offshore KW - Schweißen KW - Bauteiltest PY - 2023 DO - https://doi.org/10.48447/WP-2023-219 SP - 316 EP - 321 CY - Berlin AN - OPUS4-58908 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Uhlig, Marvin A1 - Schröder, Nina A1 - Höfer, Kevin A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Hensel, Jonas T1 - Schweißverfahrensqualifikation an Stumpfnahtverbindungen aus Altstahl- und Feinkornbaustahl N2 - Der Erhalt und die Ertüchtigung bestehender Stahltragwerke gewinnen im Bauwesen zunehmend an Bedeutung. Besonders betroffen sind Konstruktionen aus sogenannten Flussstählen, die im Zeitraum zwischen etwa 1880 und 1940, noch vor Einführung der ersten Stahlnorm DIN 488-1, in großem Umfang im Brücken-, Wasserbau- und Hochspannungsanlagenbau verwendet wurden. Diese Stähle wurden in historischen erstellungsverfahren wie dem Thomas-, Bessemer- oder Siemens-Martin-Verfahren erzeugt und weisen im Vergleich zu heutigen Baustählen eine deutlich größere Streuung in ihren chemischen und mechanischen Eigenschaften auf. Trotz ihres hohen Alters sind viele dieser Tragwerke nach wie vor im Betrieb und befinden sich am Rande ihrer statischen und funktionalen Anforderungen. Ihr Rückbau und Ersatz durch Neubauten sind jedoch oftmals mit erheblichem wirtschaftlichem, logistischem und ökologischem Aufwand verbunden. Daher rückt die Instandhaltung und Weiterverwendung solcher Altbauwerke verstärkt in den Fokus von Infrastrukturprogrammen, Sanierungsstrategien und besitzt eine große kulturelle Bedeutung. Im Rahmen der vorliegenden Untersuchung soll das Potenzial des MAG-Schweißens mit G 18 8 Mn Zusatzwerkstoff für Stumpfnahtverbindungen aus Flussstahl und Feinkornbaustahl qualifiziert werden. Ziel ist es, durch experimentelle und werkstofftechnische Analysen weitere Erkenntnisse über die Schweißbarkeit historischer Stähle zu gewinnen, Anwendungsempfehlungen für die Praxis abzuleiten und damit einen Beitrag zur sicheren und wirtschaftlichen Sanierung historischer Infrastrukturbauwerke zu leisten. T2 - DVS Congress 2025 CY - Essen, Germany DA - 16.09.2025 KW - Altstahl KW - MAG-Schweißen KW - Seigerungen KW - Instandsetzung KW - Feinkornbaustahl PY - 2025 SN - 978-3-96144-298-0 VL - 401 SP - 1 EP - 17 AN - OPUS4-64278 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - From the field to the lab and back: Evaluating the integrity of welded components using scaled experiments N2 - This contribution addresses the question of how the behaviour of complex parts or components in industrial practice can be simulated using simple welding experiments in the laboratory. It is demonstrated how so-called mock-ups can be utilised for this purpose. In particular, a test rig specially designed for scaled welding experiments is shown. It allows mechanical restraints and stiffnesses to be simulated, as well as typical welding process parameters and post weld heat treatments. Selected examples show how solidification crack growth during welding of high-strength steels can be quantified, under which conditions stress relaxation cracks occur during the heat treatment of heat-resistant steels, and how the integrity of pressurised hydrogen pipelines can be assessed during repair welding. T2 - 4th International Conference on Advanced Joining Processes 2025 CY - Coimbra, Portugal DA - 16.10.2025 KW - High strength steel KW - Stress relief cracking KW - Hydrogen PY - 2025 AN - OPUS4-64505 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Die Hohlzugprobentechnik - Eine neue Methodik zur Untersuchung der Materialverträglichkeit unter Wasserstoffeinfluss N2 - Die schädigende Wirkung von Wasserstoff auf die mechanischen Eigenschaften von Stählen ist zwar bekannt, aber noch immer nicht ausreichend erforscht. Die schnelle und sichere Markteinführung von Wasserstofftechnologien macht es erforderlich, dieses Thema genauer zu untersuchen. Im Allgemeinen wird dies oft als Wasserstoffversprödung bezeichnet. Daher ist es wünschenswert, eine Prüfmethode zu entwickeln, die auf einfache Weise die Materialeigenschaften unter Wasserstoffatmosphäre ermitteln kann. Derzeit werden mechanische Prüfungen unter Wasserstoffatmosphäre in Autoklaven durchgeführt. Für diese Technik ist eine aufwendige Hardware erforderlich, daher sind die Prüfungen teuer und die Prüfkapazitäten nur in geringem Umfang verfügbar. Die hier vorgestellte Prüfmethode verspricht einen zukunftsweisenden Ansatz zur Reduzierung von Kosten und Bearbeitungszeiten durch die Verwendung von Hohlkörpern, d.h. die Probe selbst stellt den Autoklav dar. T2 - Sitzung des DIN-Gemeinschaftsarbeitsausschusses NA 092 00 05 GA, NAS/NMP: Zerstörende Prüfung von Schweißverbindungen CY - Berlin, Germany DA - 15.03.2023 KW - Prüfung KW - Wasserstoff KW - Probengeometrie KW - Hochdruck PY - 2023 AN - OPUS4-57168 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröder, Nina A1 - Uhlig, Marvin A1 - Kromm, Arne A1 - Schröpfer, Dirk A1 - Höfer, Kevin A1 - Hensel, Jonas A1 - Kannengießer, Thomas T1 - Challenges in the evaluation of the weldability of old mild steels for future use N2 - For reasons of sustainability and cost efficiency, there is an increasing trend in the steel-processing industry to retrofit existing structures, avoiding costly shutdowns or dismantling. Although welding is a cost-effective joining method, it is rarely applied to old steels, whereas riveted or bolted connections are often uneconomical. Repair and refurbishment frequently require the replacement of damaged material or the creation of dissimilar old–new steel joints. Due to the varied manufacturing processes of historical steels, not all twentieth-century steels are inherently weldable, making an initial assessment of weldability essential. In this study, a historical non-deoxidized mild steel (produced by Siemens–Martin processing) originating from the construction of the Berlin Radio Tower (erected in 1926) was investigated using dilatometry to analyze its welding behavior. A database of welding CCT diagrams and HAZ simulations was established to support practice-oriented welding experiments, providing key insights into their weld-metallurgical behavior and weldability. Furthermore, initial welding trials were conducted, and the local residual stress states in dissimilar old–new steel joints were determined. These foundational investigations are critical for the development of innovative, load-adapted welding concepts for the repair and refurbishment of existing old-steel infrastructure in Germany. KW - Old mild steels KW - Repair welding KW - Weldability KW - Thermo-physical simulation KW - CCT diagrams PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-654784 DO - https://doi.org/10.1007/s40194-026-02366-6 SN - 1878-6669 SP - 1 EP - 14 PB - Springer nature AN - OPUS4-65478 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sprengel, Maximilian A1 - Mohr, Gunther A1 - Altenburg, Simon A1 - Evans, Alexander A1 - Serrano-Munoz, Itziar A1 - Kromm, Arne A1 - Pirling, T. A1 - Bruno, Giovanni A1 - Kannengießer, Thomas T1 - Triaxial Residual Stress in Laser Powder Bed Fused 316L: Effects of Interlayer Time and Scanning Velocity N2 - The triaxial distribution of the residual stress in laser powder bed fused austenitic steel 316L was determined by X-ray and neutron diffraction. The residual stress analysis results were linked to the thermal history of the specimens, which were manufactured with varying inter-layer-times and scanning velocities. A clear link between the in-process temperature of the specimens and the residual stress was found, based on in-situ monitoring data. KW - Stainless Steel KW - AGIL KW - Residual Stress KW - X-ray and Neutron Diffraction KW - Additive Manufacturing PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-542620 DO - https://doi.org/10.1002/adem.202101330 SP - 1 EP - 13 PB - Wiley-VCH GmbH AN - OPUS4-54262 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bruno, Giovanni A1 - Mishurova, Tatiana A1 - Serrano-Munoz, Itziar A1 - Ulbricht, Alexander A1 - Fritsch, Tobias A1 - Sprengel, Maximilian A1 - Evans, Alexander A1 - Kromm, Arne A1 - Madia, Mauro ED - Bruno, Giovanni T1 - A Critical Discussion on the Diffraction-Based Experimental Determination of Residual Stress in AM Parts N2 - As opposed to reviewing results on experimental determination of residual stress by diffraction, this paper discusses the open issues when dealing with residual stress determination in additive manufactured parts, in particular those manufactured with laser powder bed fusion techniques. Three points are addressed in detail: (a) the proper determination of the strain-free reference d0, (b) the problem of the determination of the principal axes, and (c) the use of the correct diffraction elastic constants. It is shown that all methods to determine the strain-free reference d0 suffer from caveats, and care must be taken in evaluating the most suitable for the problem being tackled. In addition, it is shown that, in some systems, the principal axes do correspond to the geometrical axes of the specimen, but this needs to be systematically checked, especially in the case of uni- or bidirectional hatching strategies. Finally, the need to experimentally determine the proper diffraction elastic constants is underlined, especially in the case of strongly textured specimens, which again depends on the deposition strategy. T2 - ASTM ICAM 2020 – ASTM International Conference on Additive Manufacturing CY - Online meeting DA - 16.11.2020 KW - Additive Manufacturing KW - Diffraction KW - Residual Stress PY - 2020 DO - https://doi.org/10.1520/STP163120190148 VL - STP1631 SP - 122 EP - 138 PB - ASTM International CY - USA AN - OPUS4-51347 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sprengel, Maximilian A1 - Ulbricht, Alexander A1 - Evans, Alexander A1 - Kromm, Arne A1 - Sommer, Konstantin A1 - Werner, Tiago A1 - Kelleher, J. A1 - Bruno, Giovanni A1 - Kannengießer, Thomas T1 - Towards the optimization of post-laser powder bed fusion stress-relieve treatments of stainless steel 316L N2 - This study reports on the stress relaxation potential of stress-relieving heat treatments for laser powder bed fused 316L. The residual stress is monitored non-destructively using neutron diffraction before and after the heat treatment. Moreover, the evolution of the microstructure is analysed using scanning electron microscopy. The results show, that a strong relaxation of the residual stress is obtained when applying a heat treatment temperature at 900°C. However, the loss of the cellular substructure needs to be considered when applying this heat treatment strategy. KW - Residual stress KW - Additive manufacturing KW - Neutron diffraction KW - Projekt AGIL - Alterung additiv gefertigter metallischer Materialien und Komponenten PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-536045 DO - https://doi.org/10.1007/s11661-021-06472-6 SN - 1543-1940 VL - 52 IS - 12 SP - 5342 EP - 5356 PB - Springer CY - Boston AN - OPUS4-53604 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nadammal, Naresh A1 - Mishurova, Tatiana A1 - Fritsch, Tobias A1 - Serrano-Munoz, Itziar A1 - Kromm, Arne A1 - Haberland, C. A1 - Portella, Pedro Dolabella A1 - Bruno, Giovanni T1 - Critical role of scan strategies on the development of microstructure, texture, and residual stresses during laser powder bed fusion additive manufacturing N2 - Laser based powder bed fusion additive manufacturing offers the flexibility to incorporate standard and userdefined scan strategies in a layer or in between the layers for the customized fabrication of metallic components. In the present study, four different scan strategies and their impact on the development of microstructure, texture, and residual stresses in laser powder bed fusion additive manufacturing of a nickel-based superalloy Inconel 718 was investigated. Light microscopy, scanning electron microscopy combined with electron backscatter diffraction, and neutron diffraction were used as the characterization tools. Strong textures with epitaxially grown columnar grains were observed along the build direction for the two individual scan strategies. Patterns depicting the respective scan strategies were visible in the build plane, which dictated the microstructure development in the other planes. An alternating strategy combining the individual strategies in the successive layers and a 67◦ rotational strategy weakened the texture by forming finer microstructural features. Von Mises equivalent stress plots revealed lower stress values and gradients, which translates as lower distortions for the alternating and rotational strategies. Overall results confirmed the scope for manipulating the microstructure, texture, and residual stresses during laser powder bed fusion additive manufacturing by effectively controlling the scan strategies. KW - Additive manufacturing KW - Laser powder bed fusion KW - Nickel-based superalloys KW - Scan strategies KW - Residual stresses KW - Microstructure and texture PY - 2021 DO - https://doi.org/10.1016/j.addma.2020.101792 VL - 38 SP - 1792 PB - Elsevier B.V. AN - OPUS4-51944 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Werkstoffsichere Dickblechschweißung und KI N2 - Der Vortrag zeigt, welche Herausforderungen beim Schweißen sogenannter Dickblechverbindungen bestehen und welche Strategien zur Lösung genutzt werden können. Ansätze zur Fehlerprävention werden vorgestellt. Es wird dargestellt, wie KI-basierte Methoden die Fehlererkennung erleichtern. Letztlich werden Potentiale zur effizienten Fehlerbeseitigung aufgezeigt und der Anwendernutzen herausgestellt. T2 - Mitgliederversammlung der Forschungsvereinigung Stahlanwendung e. V. CY - Essen, Germany DA - 17.12.2025 KW - UP-Schweißen KW - Eigenspannungen KW - Künstliche Intelligenz KW - Reparatur PY - 2025 AN - OPUS4-65210 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Effect of a High-Performance Modified Spray Arc MAG Process on Load-Oriented Repair of Old Steel Structures N2 - Steel structures erected in the late 19th and early 20th centuries still constitute a substantial part of today’s technical infrastructure. A significant proportion of bridge and engineering structures have been in service for more than 80 or even 100 years and are subjected to continuously increasing traffic volumes, axle loads, and dynamic actions. In view of these rising service demands, load-oriented and structurally adequate repair strategies are essential to ensure long-term structural integrity while preserving the existing building stock in a sustainable manner. As historical steel constructions were predominantly designed for riveted or bolted joints, the subsequent implementation of welded repair or strengthening measures represents a particular challenge. In addition to the specific material characteristics of old mild steels, welding-induced residual stresses and microstructural alterations must be carefully considered, as they can significantly affect load-bearing capacity and the overall structure performance. Consequently, repair concepts must not only restore geometry but also be adapted to the actual stress conditions and service requirements of the structure. Against this background, the present study investigates MAG welding trials on mixed joints between old and modern structural steels. The groove opening angle was systematically varied between 50° and 30° in order to analyse the influence of joint geometry on weld metal volume, heat input, and the resulting residual stress state. Furthermore, advanced high-performance arc processes, such as a modified spray arc mode, were applied to enable controlled and reduced heat input. The objective is to minimise welding-induced residual stresses through process and joint design optimisation, thereby providing a technically sound and load-oriented repair strategy for existing old steel structures suitable for long-term service. T2 - IIW Intermediate Meeting, Commission II-E CY - Bangkok, Thailand DA - 16.03.2026 KW - Historic mild steel KW - Weldability KW - High strength steel PY - 2026 AN - OPUS4-65745 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -