TY - CONF A1 - Marquardt, Raphael A1 - Biegler, Max A1 - Rethmeier, Michael T1 - Influence of laser power on the melt pool shape of handheld laser beam welding of 1.5 mm thick micro alloyed steel N2 - Manual welding of structures requires highly skilled welders due to the large heat-affected zone of arc-based processes, that can negatively impact microstructure and cause distortion. Handheld laser beam welding is a promising alternative with high welding velocity and a concentrated heat input. However, its current use in industry is limited to parts with aesthetic requirements, often made of high-alloyed steel. To extend the use of handheld laser beam welding to low-cost steels with good mechanical properties, this study investigates the influence of laser power on the melt pool shape for micro-alloyed steel with a thickness of 1.5 mm. Tested joint geometries are T-joints welded with filler wire as well as butt joints and overlap joints without filler wire, which are typically found in assemblies under mechanical load. Weld quality is assessed by weld porosity analysis. The results show that the handheld laser beam welding with filler wire produces T-joints with a very good external appearance, but with porosity between level C and D in the cross sections according to DIN EN ISO 13919-1. By increasing the laser power, a deep penetration of the T-joint zone can be achieved without increasing the actual throat thickness. For handheld laser beam welding of butt joints a full penetration weld of the highest quality class can be reached. Overlap joints can be welded with full or partial penetration depending on the laser power selected, with quality classes between B and C in terms of porosity. T2 - 20th Nordic Laser Materials Processing Conference CY - Kongens Lyngby, Denmark DA - 26.08.2025 KW - Hand held laser welding KW - Laser beam welding KW - Low alloyed steel KW - Process parameter PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-641671 DO - https://doi.org/10.1088/1757-899X/1332/1/012015 SN - 1757-899X VL - 1332 SP - 1 EP - 6 PB - Institute of Physics CY - London [u.a.] AN - OPUS4-64167 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Marquardt, Raphael T1 - Influence of laser power on the melt pool shape of handheld laser beam welding of 1.5 mm thick micro alloyed steel N2 - Manual welding of structures requires highly skilled welders due to the large heat-affected zone of arc-based processes, that can negatively impact microstructure and cause distortion. Handheld laser beam welding is a promising alternative with high welding velocity and a concentrated heat input. However, its current use in industry is limited to parts with aesthetic requirements, often made of high-alloyed steel. To extend the use of handheld laser beam welding to low-cost steels with good mechanical properties, this study investigates the influence of laser power on the melt pool shape for micro-alloyed steel with a thickness of 1.5 mm. Tested joint geometries are T-joints welded with filler wire as well as butt joints and overlap joints without filler wire, which are typically found in assemblies under mechanical load. Weld quality is assessed by weld porosity analysis. The results show that the handheld laser beam welding with filler wire produces T-joints with a very good external appearance, but with porosity between level C and D in the cross sections according to DIN EN ISO 13919-1. By increasing the laser power, a deep penetration of the T-joint zone can be achieved without increasing the actual throat thickness. For handheld laser beam welding of butt joints a full penetration weld of the highest quality class can be reached. Overlap joints can be welded with full or partial penetration depending on the laser power selected, with quality classes between B and C in terms of porosity. T2 - 20th Nordic Laser Materials Processing Conference CY - Kongens Lyngby, Denmark DA - 26.08.2025 KW - Hand held laser welding KW - Laser beam welding KW - Low alloyed steel KW - Process parameter PY - 2025 AN - OPUS4-64169 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Putra, Stephen Nugraha A1 - Meng, Xiangmeng A1 - Yang, Fan A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Einfluss der temperaturabhängigen Modellierung der Laserstrahlabsorption auf die Schmelzbadgeometrie beim Hochleistungslaserstrahlschweißen N2 - Der Absorptionsgrad metallischer Werkstoffe spielt bei Fügeprozessen mit einer Strahlungsquelle wie dem Hochleistungslaserstrahltiefschweißen eine bedeutende Rolle. Dieser beeinflusst die Menge der absorbierten Laserenergie, welche zum Aufschmelzen sowie zur lokalen Verdampfung des zu verbindenden Materials führt. Die Laserstrahlabsorption wird von vielen physikalischen Faktoren, z.B. Laserprofil, Laserwellenlänge, Materialeigenschaft sowie Temperatur, entschieden. Dennoch wird die Temperaturabhängigkeit in vielen Simulationsarbeiten häufig ignoriert und stattdessen ein empirisch angepasster Parameter zur Kalibrierung der Ergebnisse implementiert. Diese Vorgehensweise wirkt sich negativ auf die Zuverlässigkeit des numerischen Modells sowie auf die Vorhersagbarkeit der Simulationsergebnisse aus. In der vorliegenden Arbeit wird die Temperaturabhängigkeit des Laserabsorptionsgrades in ein selbstkonsistentes zweiphasiges Modell unter Berücksichtigung der gekoppelten 3D-Fluidströmung und Wärmeübertragung einbezogen. Die berechnete Laserstrahlabsorption wird durch die temperaturabhängigen Materialeigenschaften, die Lasercharakteristik und den Einfallswinkel des Laserstrahls bestimmt. Die freie Oberfläche jeder Phase wird mithilfe der Volume-of-Fluid Methode (VOF), berechnet und die Laser-Material-Wechselwirkung wird durch ein implementiertes Ray-Tracing-Verfahren modelliert, welches auf einem lokalisierten Level-Set-Algorithmus basiert. Anschließend wird die transiente Wärmeeinbringung und die Geometrie der Schweißnaht analysiert und mit dem temperaturunabhängigen Absorptionsmodell verglichen. Es wurde festgestellt, dass die Temperaturabhängigkeit der Laserabsorption entscheidend für die genaue Bestimmung der Wärmeeinbringung und der Schmelzbadgeometrie ist. Das entwickelte Modell wurde anhand der experimentellen Untersuchungen validiert und die Bedeutung der Temperaturabhängigkeit bei der Laserstrahlabsorption wurde für die Simulation des Laserstrahltiefschweißens quantifiziert. T2 - 44. Assistentenseminar Füge- und Schweißtechnik CY - Päwesin, Germany DA - 20.09.2023 KW - Laser beam welding KW - Numerical modeling KW - Ray tracing method KW - Weld pool dynamics PY - 2024 UR - https://www.dvs-media.eu/de/neuerscheinungen/4671/44.-assistentenseminar-fuegetechnik SN - 978-3-96144-267-6 VL - 394 SP - 57 EP - 68 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-60779 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fritzsche, André A1 - Hilgenberg, Kai A1 - Rethmeier, Michael T1 - Influence of welding parameters on electromagnetic supported degassing of die-casted and wrought aluminum N2 - Laser beam welding of aluminum die casting is challenging. A large quantity of gases (in particular, hydrogen) is absorbed by aluminum during the die-cast manufacturing process and is contained in the base material in solved or bound form. After remelting by the laser, the gases are released and are present in the melt as pores. Many of these metallurgic pores remain in the weld seam as a result of the high solidification velocities. The natural (Archimedean) buoyancy is not sufficient to remove the pores from the weld pool, leading to process instabilities and poor mechanical properties of the weld. Therefore, an electromagnetic (EM) system is used to apply an additional buoyancy component to the pores. The physical mechanism is based on the generation of Lorentz forces, whereby an electromagnetic pressure is introduced into the weld pool. The EM system exploits the difference in electrical conductivity between poorly conducting pores (inclusions) and the comparatively better conducting aluminum melt to increase the resulting buoyancy velocity of the pores. Within the present study, the electromagnetic supported degassing is investigated in dependence on the laser beam power, welding velocity, and electromagnetic flux density. By means of a design of experiments, a systematic variation of these parameters is carried out for partial penetration laser beam welding of 6mm thick sheets of wrought aluminum alloy AlMg3 and die-cast aluminum alloy AlSi12(Fe), where the wrought alloy serves as a reference. The proportion of pores in the weld seams is determined using x-ray images, computed tomography images, and cross-sectional images. The results prove a significant reduction of the porosity up to 70% for both materials as a function of the magnetic flux density. T2 - ICALEO 2019 CY - Orlando, FL, USA DA - 07.10.2019 KW - Laser beam welding KW - Electromagnetic supported degassing KW - Die-casted aluminum PY - 2020 DO - https://doi.org/10.2351/7.0000064 VL - 32 IS - 2 SP - 022031-1 EP - 022031-8 PB - AIP Publishing AN - OPUS4-50728 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Meng, Xiangmeng A1 - Artinov, Antoni A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Theoretical study of influence of electromagnetic stirring on transport phenomena in wire feed laser beam welding N2 - The additional element from the filler wire in the laser beam welding is usually distributed inhomogeneously in the final weld due to the high solidification rate of weld pool. It has been found that the electromagnetic stirring produced by an external oscillating magnetic field can enhance the material mixing in the weld pool to achieve a more uniform element distribution. However, the magnetic field has a highly nonlinear and multicoupled interaction with the weld pool behavior, which makes the quantitative explanation of the physical mechanism difficult. In this study, the effect of electromagnetic stirring on the transport phenomena in the wire feed laser beam welding is investigated by a numerical modeling. A 3D transient multiphysical model considering the magnetohydrodynamics, heat transfer, fluid flow, keyhole dynamics, and element transport is developed. The multiple reflections and the Fresnel absorption of the laser on the keyhole wall are calculated using the ray tracing method. The numerical results show that a Lorentz force produced by the oscillating magnetic field and its induced eddy current gives significant influence on the transport phenomena in the molten pool. The forward and downward flow is enhanced by the electromagnetic stirring, which homogenizes the distribution of the additional elements from a nickel-based filler wire in a steel weld pool. The numerical results show a good agreement with the high-speed images of the molten pool, the fusion line from the optical micrograph, and the element distribution from the energy dispersive x-ray spectroscopy. This work provides a physical base for the electromagnetic-controlled laser beam welding and some guidance for the selection of electromagnetic parameters. KW - Magnetohydrodynamics KW - Molten pool dynamics KW - Element transport KW - Laser beam welding PY - 2020 DO - https://doi.org/10.2351/7.0000069 VL - 32 IS - 2 SP - 022026-1 EP - 022026-9 AN - OPUS4-50874 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Artinov, Antoni T1 - On the relationship between the bulge effect and the hot cracking formation during deep penetration laser beam welding N2 - Recent studies have confirmed the widening of the weld pool interface, known as a bulge effect, during deep penetration high power laser beam welding. The link between such geometric particularities of the weld pool shape and the hot cracking phenomena is significant. The present work seeks to extend the level of understanding by investigating their relationship. A coupled multiphysics, multiscale numerical framework is developed, comprising a series of subsequent analyses. The study examines the influences of the bulge on the three most dominant effects causing hot cracking, namely the thermal cycles, the mechanical loading, and the local microstructure. The bulge in the weld pool shape forms approximately in the middle of the plate, thus correlating with the location of hot cracking. It increases the hot cracking susceptibility by enhancing the three dominant effects. The numerical results are backed up by experimental data. T2 - 11th CIRP Conference on Photonic Technologies [LANE 2020] CY - Online meeting DA - 07.09.2020 KW - Hot cracking KW - Bulge effect KW - Numerical modelling KW - Laser beam welding KW - Deep penetration PY - 2020 AN - OPUS4-51277 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Straße, Anne T1 - LMD coatings as filler material for laser beam welded 30 mm thick plates N2 - The development of high energy laser sources enables single-pass welds of thick plates up to 30 mm, but often additional materials are needed to influence the properties of the weld seams. However, the homogenous distribution of filler materials in form of e.g. electrodes is only possible up to 7 mm while the elements are only traceable up to a depth of 14 mm. To overcome this problem a two-step process is used where first the edges of the weld partners are coated with the filler material by laser metal deposition (LMD) and afterwards are welded by laser beam. Single-pass welds with electromagnetic weld pool support of 30 mm thick S355 J2+N-plates with austenitic AISI 316L-coatings were investigated as well as the influence of the coatings to the penetration depth of the laser beam without electromagnetic weld pool support in double-sided joints. The weld seams were tested by X-ray inspection and cross sections. T2 - 11th CIRP Conference on Photonic Technologies [LANE 2020] CY - Online meeting DA - 07.09.2020 KW - Penetration depth KW - Laser metal deposition (LMD) KW - Laser beam welding KW - Filler material distribution PY - 2020 AN - OPUS4-51276 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gumenyuk, Andrey T1 - New developments in high power laser and hybrid welding of thick plates for application in modern ship building N2 - High power laser beam welding has been already introduced in ship building industry since last two decades and is characterized by higher performance as conventional arc welding technologies through its higher welding speed, penetration depth and therefore higher productivity. Moreover, high quality weld joints are achievable thanks to a stronger automatization degree and better repeatability of the process. A further advantage of the laser beam welding is a manufacturing of parts with very low distortion according to much lower heat input, so that rework amount can be reduced significantly. Nevertheless, there are still some unresolved problems limiting the range of application of the technology in part manufacturing within ship building industry, restricted by development and application of new materials or new design of ship vessels. The present contribution deals with some novel aspects of laser beam welding technology allowing to widen this range significantly. One of the possibilities is to increase the weld seam thickness for single pass laser or laser-hybrid welding is to apply contactless EM-support system based on generation of the Lorentz force counteracting the liquid metal drop out. Also, application of laser-hybrid welding technology for welding novel materials like cold resistant steel X8Ni9 used for construction of LNG tanks brings technological and design advantages comparing to conventional welding technologies by using of a similar alloyed filler wire instead of expensive Ni-based filler material. Finally, it is shown how the application of computational techniques can be used to helps to improve the quality of laser welded joints and avoid the critical weld failure by optimization of the welding process parameters. T2 - SHY Virtual Laserforum 2020 CY - Online meeting DA - 01.09.2020 KW - Ship building KW - Laser beam welding KW - Hybrid laser arc welding PY - 2020 UR - https://laserforum.mobieforum.fi/ AN - OPUS4-51221 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakir, Nasim T1 - In situ determination of the critical staining condition for solidification cracking during laser beam welding N2 - Using a novel optical measurement technique together with the OF algorithm, a two-dimensional deformation analysis during welding was conducted. The OF technique was the first of its kind to provide a measurement of the full strain field locally in the immediate vicinity of the solidification front. The local critical strain and strain rate in vicinity of the solidification front has observed 1.57%, 28 %/s, respectively. T2 - Lane 2020 CY - Online meeting DA - 07.09.2020 KW - Optical measurement technique KW - Laser beam welding KW - Solidification cracking PY - 2020 AN - OPUS4-51741 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meng, Xiangmeng T1 - Numerical study of additional element transport in wire feed laser beam welding N2 - The distribution of the alloying elements from the filler wire in laser beam welding plays an important role on the property of the final weld. In this study, the transport phenomena in the wire feed laser beam welding are investigated numerically. A three-dimensional transient heat transfer and fluid flow model coupled with free surface tracing and element transport is developed. A ray-tracing method with local grid refinement algorithm is used to calculate the multiple reflections and Fresnel absorption on the keyhole wall. The filler material flows backward along the lateral side of the weld pool, and subsequently flows forward along the longitudinal plane to bring the additional alloying elements to the forepart of the weld pool. The occurrence of the bulging phenomenon may further prevent the downward transfer of the additional elements to the root of the weld pool. The numerical results show a good agreement with the experimental fusion line and element distribution. T2 - 11th CIRP Conference on Photonic Technologies [LANE 2020] CY - Online meeting DA - 07.09.2020 KW - Laser beam welding KW - Element transport KW - Filler material PY - 2020 AN - OPUS4-51568 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Üstündag, Ömer A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Influence of oscillating magnetic field on the keyhole stability in deep penetration laser beam welding N2 - The stability of the keyhole decreases for deep penetrated high-power laser beam welding. The keyhole tends to collapse with increasing laser power and e.g. keyhole induced porosity can occur. This study deals with the observation of the keyhole during high-power laser beam welding in partial penetration mode by means of a high-speed camera. A butt configuration of 25 mm thick structural steel and transparent quartz glass was used for the experiments. An oscillating magnetic field was applied perpendicular to the welding direction on the root side of the steel plate. The keyhole was highlighted with a coaxial diode laser. It was ascertained that the stability of the keyhole and the weld penetration depth were increased by applying an oscillating magnetic field with an oscillating frequency of 1.2 kHz and a magnetic flux density of 50 mT. KW - Magnetic field KW - Laser beam welding KW - Keyhole stability PY - 2021 DO - https://doi.org/10.1016/j.optlastec.2020.106715 SN - 0030-3992 VL - 135 SP - 106715 PB - Elsevier Ltd. AN - OPUS4-52007 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Savitsky, Viktor A1 - Schmies, Lennart A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Comparative performance of DIC and optical flow algorithms for displacement and strain analysis in laser beam welding N2 - The measurement of strain and displacement in the context of the welding process represents a significant challenge. Optical methods, such as digital image correlation (DIC) or optical flow algorithms, have demonstrated their efficacy in robust and reliable data acquisition in harsh environments, including those encountered in welding processes. Concurrently, a trade-off between the accuracy of the measurement and the computational resources required for the associated calculations must be evaluated on a case-by-case basis. The application of filters to initial images represents a technique that serves to enhance the quality and accuracy of the strain and displacement prediction. In the present study, the estimated error of two algorithms, namely the Lucas-Kanade (LK) and the inverse compositional Gauss-Newton (IC-GN), is compared on the basis of both synthetic and real welding images. The displacement field is evaluated for different zones in the laser weld seam with varying contrast performance. Based on the aforementioned results, a strain calculation was conducted for both methods, which yielded comparable results for the LK and IC-GN algorithms. KW - Laser speckle KW - DIC KW - Optical flow KW - Error estimation KW - Strain measurement KW - Laser beam welding PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-625919 DO - https://doi.org/10.1016/j.optlaseng.2025.108870 SN - 1873-0302 VL - 187 SP - 1 EP - 15 PB - Elsevier Ltd. AN - OPUS4-62591 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Meng, Xiangmeng A1 - Artinov, Antoni A1 - Bachmann, Marcel A1 - Üstündag, Ömer A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - The detrimental molten pool narrowing phenomenon in wire feed laser beam welding and its suppression by magnetohydrodynamic technique N2 - Element transport in the wire feed laser beam welding (WFLBW) is directly determined by the molten pool shape and thermo-fluid flow therein. In this paper, an untypical molten pool profile, i.e., elongated at its top and bottom but narrowed at the middle, is found experimentally by real-time metal/glass observa- tion and numerically by multi-physical modeling. Ex-situ X-ray fluorescence element mapping is used to characterize the element dilution status in the fusion zone. For the first time, the detrimental influence of the molten pool narrowing on the element transport is identified and discussed, combining the exper- imental and numerical results. A magnetohydrodynamic technique is utilized to suppress the narrowing, aiming at a more homogenous element distribution. It is found that due to the interaction of the two dominant circulations from the top and bottom regions of the molten pool, a low-temperature region is formed. It leads to an untypical growth of the mushy zone, narrowing the molten pool in the middle re- gion. Its detrimental effect on material mixing is non-negligible considering the direct blocking effect on the downward flow and the premature solidification at the middle region. The Lorentz force from a trans- verse oscillating magnetic field can change the flow pattern into a single-circulation type. The downward transfer channel is widened, and its premature solidification is prevented because the low-temperature- gradient region is mitigated. This paper provides a supplementary reason regarding the common issue of insufficient material mixing during LBW, and a promising technique to optimize the process. KW - Thermo-fluid flow KW - Element transport KW - Laser beam welding KW - Magnetohydrodynamics KW - Multi-physical modeling PY - 2022 DO - https://doi.org/10.1016/j.ijheatmasstransfer.2022.122913 VL - 193 SP - 122913 PB - Elsevier B.V. AN - OPUS4-55006 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bachmann, Marcel T1 - Numerical studies of keyhole dynamic behavior during the laser beam welding with an oscillating magnetic field N2 - The formation of keyhole induced porosity (Process porosity) during laser beam welding (LBW) is mainly associated with the dynamic keyhole behavior. Experimental studies have confirmed that the application of a magnetic field can effectively suppress process porosity. However, there is still no quantitative evidence supporting that this suppression mechanism involves a direct influence of the magnetic field on the keyhole dynamics. In this paper, a novel keyhole reconstruction algorithm is developed and incorporated into a three-dimensional transient multi-physics coupled numerical model to study the dynamic keyhole behavior under the influence of an oscillating magnetic field. This keyhole reconstruction algorithm accurately reproduces the 2D time-averaged keyhole shape, effectively capturing the keyhole tailing and the backward shift of its centroid on the keyhole top. The application of an oscillating magnetic field reduces the keyhole diameter and enhances its stability. The frequency of keyhole collapse is reduced under the influence of a magnetic field. Additionally, the occurrence of keyhole collapses with long duration is significantly reduced in the presence of a magnetic field. T2 - 78th IIW Annual Assembly and International Conference CY - Genua, Italy DA - 22.06.2025 KW - Laser beam welding KW - Magnetohydrodynamics KW - Porosity KW - Numerical simulation PY - 2025 AN - OPUS4-63645 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rethmeier, Michael A1 - Gook, Sergej T1 - Notch impact toughness of laser beam welded thick sheets of cryogenic nickel alloyed steel X8Ni9 N2 - This research work deals with the investigations of the impact toughness of laser beam welded 14.5 mm thick sheets made of cryogenic steel X8Ni9 as a function of preheating. This 9% nickel alloyed steel is widely used in the liquefied natural gas (LNG) industry. An application of highly efficient welding processes such as high-power laser beam welding (LBW) in LNG sector requires an understanding of the interactions between the LBW process parameters and weld properties, in particular the impact toughness. The results show that the original fine-grained martensitic microstructure of the base metal (BM) is significantly changed by melting and crystallization during the LBW, what can lead to a decrease in the impact toughness of the weld metal (WM) below the required level. An optimal preheating temperature range leads to the favorable thermal welding cycle and is of remarkable importance for maintaining the notch impact toughness of laser beam welded joints of these thick steel sheets. A parameter window was identified in which V-notch impact toughness comparable to that of the BM at -196 °C was achieved. T2 - 11th CIRP Conference on Photonic Technologies LANE 2020 CY - Online meeting DA - 06.09.2020 KW - Cryogenic steel KW - Laser beam welding KW - Welding thermal cycle PY - 2020 AN - OPUS4-51750 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Karkhin, Victor A1 - Artinov, Antoni A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Simulation of solidification during laser welding of thin plates T1 - Моделирование процесса кристаллизации при лазерной сварке пластин малой толщины N2 - It is proposed to model the experimentally observed weld pool boundary with superellipses (Lamé curves) and to find the unknown parameters of the curves using optimization methods. It has been shown experimentally that during laser welding of austenitic stainless steel with a thickness of 2 mm at a speed of 20 mm/s, the rear weld pool part has a shape close to triangular which can be accurately approximated by a superellipse. Analytical dependences of the trajectory and growth rate of the crystal and its cross-sectional area on the geometry of the rear weld pool part are obtained. KW - Laser beam welding KW - Plane crystalization KW - Mathematical modeling KW - Superellipse KW - Thin steel plates PY - 2023 DO - https://doi.org/10.34641/SP.2023.1061.4.033 VL - 4 SP - 28 EP - 33 AN - OPUS4-59649 LA - rus AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gook, S. A1 - Üstündag, Ömer A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Verfahren zum fehlerfreien Laserstrahl-MSG-Hybridschweißen geschlossener Rundnähte N2 - In diesem Beitrag werden Ergebnisse der Untersuchungen eines Verfahrens zum fehlerfreien Laserstrahl-MSG-Hybridschweißen von geschlossenen Rundnähten vorgestellt. Das Verfahren zielt auf die Vermeidung von Schweißnahtunregelmäßigkeiten im Überlappbereich einer hybridgeschweißten Rundnaht. Eine Strategie der Prozessführung beim Schließen der Rundnaht wurde entwickelt, mit der ein fehlerfreier Überlappbereich durch die Kontrolle der Erstarrungsbedingungen am Schweißnahtende erreicht wird. Die kontrollierte Wärmeführung wird durch eine Anpassung der Parameter von beiden beteiligten Schweißprozessen, dem Laserstrahl sowie dem Metallschutzgas (MSG)-Schweißprozess, realisiert. Experimentelle Untersuchungen wurden an 12 bis 15 mm dicken Rohrabschnitten durchgeführt. Der Einfluss von Prozessparametern wie der Veränderung des Abbildungsmaßstabs und der Defokussierung des Laserstrahls auf die Erstarrungsbedingungen am Ende der Rundnaht wurde untersucht, um eine optimale Strategie zum Herausführen der Prozessenergie zu finden. Im Rahmen der experimentellen Untersuchungen konnte gezeigt werden, dass eine Defokussierung des Laserstrahls im Bereich zwischen 60 mm und 100 mm über einen kurzen Auslaufbereich der Naht von etwa 15 mm zu einer deutlich besseren Nahtausbildung im Überlappbereich führt. Es konnte eine günstige kelchförmige Schweißnaht ohne eine Tendenz zur Rissbildung erzielt werden. Die Laseroptik mit motorisch angesteuertem Linsensystem ermöglichte dabei eine Vergrößerung des Laserstrahldurchmessers ohne eine Veränderung der Position des MSG-Lichtbogens relativ zur Bauteiloberfläche. KW - Hybrid welding KW - Laser beam welding KW - Pipe manufacturing KW - As-shielded arc welding KW - Weld defects PY - 2021 VL - 73 IS - 3 SP - 116 EP - 121 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-52365 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rethmeier, Michael A1 - Gumenyuk, Andrey A1 - Bachmann, Marcel T1 - High-power laser beam welding for thick section steels – new perspectives using electromagnetic systems N2 - In recent years, it was shown that the introduction of additional oscillating and permanent magnetic fields to laser beam and laser-arc hybrid welding can bring several beneficial effects. Examples are a contactless weld pool support for metals of high thickness suffering from severe drop-out when being welded conventionally or an enhanced stirring to improve the mixing of added filler material in the depth of the weld pool to guarantee homogeneous resulting mechanical properties of the weld. The latest research results show the applicability to various metal types over a wide range of thicknesses and welding conditions. The observations made were demonstrated in numerous experimental studies and a deep understanding of the interaction of the underlying physical mechanisms was extracted from numerical calculations. KW - Laser beam welding KW - Numerical simulations KW - Electromagnetic support PY - 2021 DO - https://doi.org/10.1080/13621718.2021.1999763 VL - 27 IS - 1 SP - 43 EP - 51 PB - Taylor & Francis Group AN - OPUS4-53970 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rethmeier, Michael T1 - The bulging effect and its relevance in high power laser beam welding N2 - The present work deals with the recently confirmed widening of the weld pool interface, known as a bulging effect, and its relevance in high power laser beam welding. A combined experimental and numerical approach is utilized to study the influence of the bulge on the hot cracking formation and the transport of alloying elements in the molten pool. A technique using a quartz glass, a direct-diode laser illumination, a high speed camera, and two thermal imaging cameras is applied to visualize the weld pool geometry in the longitudinal section. The study examines the relevance of the bulging effect on both, partial and complete penetration, as well as for different sheet thicknesses ranging from 8 mm to 25 mm. The numerical analysis shows that the formation of a bulge region is highly dependent on the penetration depth and occurs above 10 mm penetration depth. The location of the bulge correlates strongly with the cracking location. The obtained experimental and numerical results reveal that the bulging effect increases the hot cracking susceptibility and limits the transfer of alloying elements from the top of the weld pool to the weld root T2 - The 18th Nordic Laser Materials Processing Conference CY - Lulea, Sweden DA - 18.01.2022 KW - Laser beam welding KW - Melt pool dinamics PY - 2022 AN - OPUS4-54333 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gumenyuk, Andrey T1 - Influence of an external applied AC magnetic field on the melt pool dynamics at high-power laser beam welding N2 - The study deals with the determination of the influence of an externally applied oscillating magnetic field on the melt pool dynamics in high power laser beam and hybrid laser arc welding processes. An AC magnet was positioned under the workpiece which is generating an upward directed electromagnetic force to counteract the formation of the droplets. To visualise the melt flow characteristics, several experiments were carried out using a special technique with mild steel from S355J2 with a wall thickness of up to 20 mm and a quartz glass in butt configuration. The profile of the keyhole and the melt flow were recorded with a high-speed camera from the glass side. Additionally, the influence of the magnetic field orientation to the welding direction on the filler material dilution on laser hybrid welding was studied with variating oscillation frequency. The element distribution over the whole seam thickness was measured with X-ray fluorescence (XRF). The oscillation frequency demonstrated a greater influence on the melt pool dynamics and the mixing of the elements of the filler wire. The high-speed recordings showed, under the influence of the magnetic field, that the melt is affected under strong vortex at the weld root, which also avoids the formation of droplets T2 - The 18th Nordic Laser Materials Processing Conference CY - Lulea, Sweden DA - 18.01.2022 KW - Laser beam welding KW - Melt pool dinamics PY - 2022 AN - OPUS4-54331 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -