TY - JOUR A1 - Morys, Michael A1 - Häßler, Dustin A1 - Krüger, Simone A1 - Schartel, Bernhard A1 - Hothan, Sascha T1 - Beyond the standard time-temperature curve: Assessment of intumescent coatings under standard and deviant temperature curves N2 - Nowadays there are intumescent coatings available for diverse applications. There is no established assessment of their protection performance besides the standard time-temperature curve, but natural fire scenarios often play an important role. A reliable straightforward performance-based assessment is presented. The effective thermal conductivity per thickness is calculated based on intermediate-scale fire tests. The optimum thermal insulation, the time to reach it, and the time until contingent failure of the coating are used for an assessment independent of the heating curve. The procedure was conducted on four different commercially intumescent coatings for steel construction, one solvent-based, one waterborne, one epoxy-based, and a bandage impregnated with a waterborne coating. The performance was studied under four different but similar shaped heating curves with different maximum temperatures (standard time-temperature curve, hydrocarbon curve and two self-designed curves with reduced temperature). The thermal protection performance is crucially affected by the residue morphology. Therefore, a comprehensive morphology analysis, including micro-computed tomography and scanning electron microscopy, was conducted on small-scale residues (7.5 x 7.5 cm2). Two different types of inner structures and the residue surface after different heat exposures were discussed in terms of their influence on thermal protection performance. KW - Intumescence KW - Coating KW - Computed tomography KW - Small scale KW - Heating curves KW - Residue morphology PY - 2020 DO - https://doi.org/10.1016/j.firesaf.2020.102951 SN - 0379-7112 VL - 112 SP - 102951 PB - Elsevier Ltd. AN - OPUS4-50334 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmidt, Martin A1 - Wu, Dejian A1 - Zhao, P. A1 - Tan, X. A1 - Huang, W. A1 - Qianc, X. T1 - Minimum explosion concentrations of coal dusts with CH4/H2/CO below the gas lower explosion limit N2 - A 20-L spherical explosion chamber was used to investigate the explosion characteristics of dust clouds in air with the presence of flammable gas which is lower than its lower explosion limit (LEL). including minimum explosion concentration (MEC) of dust. Explosion pressure (Pex) and explosion pressure rise (dp/dt)ex). Two dust samples (anthracite coal, bituminous coal) and were three flammable gases (CH4, H2 and CO) were tested. Experimental results showed that the explosion of hybrid mixtures occurs when both dust and gas concentrations are lower than the LEL/MEC of the single substances. Meanwhile. all flammable gases with different volume fractions have distinct effects on the MEC. Pex and (dp/dt)ex of the dust samples. With the increase of the flammable gas concentration. either the Pex and (dp/dt)ex increase or the MEC decreases for all the hybrid mixtures of both two dust samples. At the same concentration of coal dusts. the addition of CH4 promotes higher explosion risks than the other two flammable gases. The distribution of (dp/dt)ex is quite different with the restricted area defined by empirical formulas. These results improve our understanding of the explosion behaviour and the explosion risk of hybrid dust-gas mixtures in air. KW - Dust explosions KW - Gas explosions KW - Minimum explosible concentration KW - Lower explosion limit KW - Hybrid mixtures PY - 2020 DO - https://doi.org/10.1016/j.fuel.2019.116401 SN - 0032-5910 VL - 260 SP - UNSP 116401 PB - Elsevier Sci. Ltd. AN - OPUS4-49956 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wu, Dejian A1 - Schmidt, Martin A1 - Tan, X. A1 - Zhao, P. A1 - Huang, W. A1 - Qian, X. T1 - Minimum ignition temperature of carbonaceous dust clouds in air with CH4/H-2/CO below the gas lower explosion limit N2 - Godbert-Greenwald furnace was used to investigate the minimum ignition temperature of dust clouds (MITC) in air with the presence of flammable gas which is lower than its lower explosion limit (LEL). Three flammable gases (CH4, H2 and CO) and three carbonaceous dusts (anthracite coal, bituminous coal and sweet potato starch) were tested. Results showed that all flammable gases have distinct effects on the MITC of the dust samples and volatile matter content of dust plays an important role during the ignition process. Specifically, the MITC of anthracite coal dust decreased from 610 °C to 560 °C, 580 °C and 570 °C with 3% CH4, 3% CO and 2.5% H2, respectively. Moreover, a heterogeneous ignition mechanism model was proposed to verify the equally global ignition characteristic between hybrid anthracite coal-CxHy mixture and bituminous coal. All three gases had an ignorable effect on the MITC of starch dust considering the experimental error. The presence of CO and H2 slightly promoted the ignition of bituminous coal dust, but the addition of CH4 showed a distinct concentration effect on the MITC of bituminous coal: the MITC decreased with 1% CH4 while increased with 2% and 3% CH4. This negative-effect of flammable gases at such low concentrations on ignition temperature of bituminous coal dusts was found for the first time. Furthermore, the presence of the 2nd flammable gas had a smaller effect on the MITC of dust samples with a higher volatile content, resulted from the competition of heterogeneous and homogeneous ignition mechanisms. KW - Dust explosions KW - Gas explosions KW - Minimum ignition temperature KW - Hybrid mixtures PY - 2020 DO - https://doi.org/10.1016/j.fuel.2019.116811 SN - 0016-2361 VL - 264 SP - 116811 PB - Elsevier Ltd. AN - OPUS4-50856 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schartel, Bernhard T1 - Flammschutz für technische Kunststoffte für elektronische Anwendungen N2 - Das Brandverhalten stellt wie das ausgezeichnete elektrische Isolationsverhalten, die geringen elektrischen Verluste, die Verarbeitbarkeit und Formbarkeit eine der wesentlichen Schlüsseleigenschaften im Eigenschaftsprofil von Polymerwerkstoffen in der Elektronik und der Elektrotechnik dar. Dabei bedarf es einer Ausrüstung der Polymerwerkstoffe mit Flammschutzmittel. Die Entwicklung von immer effizienteren, synergistischen und multifunktionalen Multikomponentensystemen ist dabei eine herausragende Quelle für Innovation. Die Entwicklung und Verbesserung der werkstoff- und anwendungsspezifischen Flammschutzlösungen bestimmen die aktuellen und zukünftigen Polymermaterialien in der Elektronik und Elektrotechnik mit. Der Vortrag stellt anhand von Beispielen einige der erfolgreichen Konzepte dar. Es wird versucht, über das wissenschaftlich-systematische Verständnis Grundprinzipien und vielversprechende Lösungsstrategien zu verdeutlichen. T2 - Kunststoff trifft Elektronik, KUZ Kunststoffzentrum in Leipzig CY - Leipzig, Germany DA - 29.01.2020 KW - Flame retardant KW - Ssynergy KW - Flame retardant mode of action KW - UL 94 KW - Cone calorimeter PY - 2020 AN - OPUS4-50495 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Schartel, Bernhard A1 - Kebelmann, Katharina ED - Hu, Y. ED - Wang, X. T1 - Fire testing for the development of flame retardant polymeric materials N2 - Flame retarded polymeric materials are used in various applications in which a certain fire behavior is demanded. Protection goals are defined, such as limited flammability in terms of hindered sustained ignition or limited contribution to a fire, and these protection levels are tested with defined specimens or components in defined fire scenarios, that is to say, different fire tests. Passing a specific fire test by meeting whatever its demands is often the most important development goal, so the parameters of the different fire tests vary widely to emphasize different fire properties. Some fire tests are used to screen or provide a general assessment of flame retardant polymers during development, while other fire tests and tailored experiments are performed to address special phenomena or understand the flame retardancy modes of action. For all fire testing, the devil is in the details – demanding know-how and crucial efforts to manage the quality of investigations and advanced interpretation. This chapter aims to offer a structured overview of all these aspects. KW - Fire testing KW - Flame retardant KW - Fire retardant KW - Flammability KW - Ignition KW - Oxygen index KW - Cone calorimeter KW - UL 94 KW - Developing fire KW - Uncertainty KW - Fire resistance PY - 2020 SN - 978-1-138-29578-7 SP - 35 EP - 55 PB - CRC Press AN - OPUS4-50236 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Battig, Alexander A1 - Markwart, J. C. A1 - Wurm, F. R. A1 - Schartel, Bernhard T1 - Sulfur's role in the flame retardancy of thio-ether–linked hyperbranched polyphosphoesters in epoxy resins N2 - Hyperbranched polyphosphoesters are promising multifunctional flame retardants for epoxy resins. These polymers were prepared via thiol-ene polyaddition reactions. While key chemical transformations and modes of actions were elucidated, the role of sulfur in the chemical composition remains an open question. In this study, the FR-performance of a series of phosphorus-based flame retardant additives with and without sulfur (thioethers or sulfones) in their structure are compared. The successful synthesis of thio-ether or sulfone-containing variants is described and verified by 1H and 31P NMR, also FTIR and MALDI-TOF. A decomposition process is proposed from pyrolytic evolved gas analysis (TG-FTIR, Py-GC/MS), and flame retardancy effect on epoxy resins is investigated under pyrolytic conditions and via fire testing in the cone calorimeter. The presence of sulfur increased thermal stability of the flame retardants and introduced added condensed phase action. Likely, Sulfur radical generation plays a key role in the flame-retardant mode of action, and sulfones released incombustible SO2. The results highlight the multifunctionality of the hyperbranched polymer, which displays better fire performance than its low molar mass thio-ether analogue due to the presence of vinyl groups and higher stability than its monomer due to the presence of thio-ether groups. KW - Phosphoester KW - Hyperbranched KW - Sulfur KW - Thio-ether KW - Flame retardant KW - Epoxy resin PY - 2020 DO - https://doi.org/10.1016/j.eurpolymj.2019.109390 SN - 0014-3057 VL - 122 SP - 109390 PB - Elsevier Ltd. AN - OPUS4-50238 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Turski Silva Diniz, Analice A1 - Huth, Christian A1 - Schartel, Bernhard T1 - Dripping and decomposition under fire: Melamine cyanurate vs. glass fibres in polyamide 6 N2 - Manipulating the melt dripping of thermoplastics makes a fire scenario more or less dangerous. Yet, a detailed understanding of this phenomenon has remained a question mark in studies of the flammability of plastics. In this work, the individual and collective impacts of additives on the dripping behaviour of polyamide 6 (PA6) were studied. A set of materials compounded with melamine cyanurate (MCA) and glass fibre (GF) was investigated. Under UL 94 vertical test conditions, the dripping during first and second ignition was quantified and investigated in detail. The number, size and temperature of the drops were addressed, and the materials and their drops evaluated with respect to such aspects as their averaged molecular weight, thermal decomposition and rheological properties. PA6 with V-2 classification improved to V-0 with the addition of MCA, and achieved HB in the presence of GF. PA6/GF/MCA achieved V-2. Non-flaming drops of PA6/MCA consisted of oligomeric fragments. Flaming drops of PA6/GF showed a more pronounced decomposition of PA6 and an increased GF content. The dripping behaviour of PA6/GF/MCA can be understood as a combination of the influence of both additives. The results showed nicely that dripping under fire is neither a straightforward material property nor a simple additive influence, but the complex response of the material influenced by the interaction and competition of different phenomena. KW - Dripping KW - UL 94 KW - Polyamide 6 KW - Melamine cyanurate KW - Glass fibre KW - Flame retardant PY - 2020 DO - https://doi.org/10.1016/j.polymdegradstab.2019.109048 SN - 0141-3910 VL - 171 SP - 109048 PB - Elsevier Ltd. AN - OPUS4-50239 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zirnstein, Benjamin A1 - Schulze, Dietmar A1 - Schartel, Bernhard T1 - Combination of phosphorous flame retardants and aluminum trihydrate in multicomponent EPDM composites N2 - Ethylene propylene diene monomer (EPDM) Rubbers with the flame retardants tris(2-ethylhexyl)phosphate, ammonium polyphosphate, polyaniline, and aluminum trihydroxide were prepared and analyzed in this study. The homogenous dispersion of the fillers in the rubber matrix was confirmed by scanning electron microscope. To investigate the interplay of the different flame retardants, the flame retardants were varied systematically. The comprehensive study sought combinations of flame retardants that allow high loadings of flame retardants without deterioration of the physical and mechanical properties of the EPDM rubber. The eight EPDM rubbers were investigated via thermogravimetric analysis and pyrolysis gas chromatography coupled with a mass spectrometer (Py GC/MS) to investigate the potential synergistic effects. In the Py-GC/MS experiments, 27 pyrolysis products were identified. Furthermore, UL 94, limiting oxygen index, FMVSS 302, glow wire tests, and cone calorimeter tests were carried out. In the cone calorimeter test the EPDM rubbers R-1AP and R-1/2P achieved an increase in residue at flameout of 76% and a reduction in total heat evolved of about 35%. Furthermore, the compounds R-1AP and R-1/2P achieved a reduction in MARHE to about 150 kW m−1, a reduction of over 50% compared to the unprotected rubber R. KW - EPDM KW - Rubber KW - Aluminum hydroxide (ATH) KW - Phosphorous flame retardant PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-502859 DO - https://doi.org/10.1002/pen.25280 SN - 1548-2634 VL - 60 IS - 2 SP - 267 EP - 280 PB - Wiley AN - OPUS4-50285 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Hauswaldt, Sebastian T1 - Kontinuumsmechanische Werkstoffmodelle zur numerischen Simulation von Stahlbauteilen im Brandfall N2 - Das nichtlineare und geschwindigkeitsabhängige Materialverhalten von Stahl wird besonders bei hohen Temperaturen sichtbar. Für Finite-Elemente-Simulationen von Stahlkonstruktionen im Brandfall sollte aus diesem Grund plastisches und geschwindigkeitsabhängiges Materialverhalten beschrieben werden. Die vorliegende Arbeit betrachtet unter diesem Aspekt bisherige Materialuntersuchungen und macht Vorschläge für dreidimensionale Materialmodelle mit entsprechenden Eigenschaften. Es werden zunächst die phänomenologischen Eigenschaften von Baustahl anhand einer Literaturrecherche analysiert, wobei verstärkt auf Untersuchungen des Materialverhaltens bei Belastungen und Aufheizprozessen, wie sie im Brandfall zu erwarten sind, geachtet wird. Die für die Bemessung von Stahlkonstruktionen gebräuchliche Spannungsbeschreibung des EC 3-1-2 wird untersucht. Es werden ihre Stärken, aber auch die zur Entwicklung einer kontinuumsmechanischen Materialformulierung fehlenden Eigenschaften, aufgezeigt. Ein nichtlinear-elastisches kontinuumsmechanisches Materialmodell der Deformationstheorie der Plastizität wird so angepasst, dass es die Spannungs-Dehnungslinien gemäß EC 3-1-2 im einachsigen Spannungszustand beschreibt. Es wird des Weiteren ein thermoelastisch-viskoplastisches Modell vorgestellt, das in der Lage ist, Kriechen und Relaxation bei Aufheiz- und Abkühlprozessen zu beschreiben. Die Struktur dieses Materialmodells wird so gewählt, dass die Parameter an hierfür geeigneten Messergebnissen leicht identifiziert werden können. Der deviatorische Anteil des Modells besteht aus einem geschwindigkeitsunabhängigen, plastischen Anteil und einem geschwindigkeitsabhängigen, viskoelastischen Anteil. Der geschwindigkeitsunabhängige, plastische Anteil wurde als Differentialgleichung auf Grundlage der so genannten endochronen Plastizitätstheorie formuliert. Die Parameter der Materialmodelle werden auf Grundlage der Messergebnisse stationärer Warmzugversuche an Baustahlproben identifiziert. Sowohl das nichtlinear-elastische EC 3-1-2-Materialmodell als auch das thermoelastisch-viskoplastische Materialmodell mit den an Baustahl angepassten Materialparametern wird numerisch für die Verwendung mit Finite-Elemente-Programmen aufbereitet und als UMAT-Subroutine für ABAQUS in der Programmiersprache FORTRAN implementiert. Hierbei wird insbesondere auf die Bereitstellung der konsistenten Tangentenoperatoren Wert gelegt, um eine effiziente numerische Berechnung bei Verwendung der Materialmodelle zu ermöglichen. Abschließend werden erste Simulationsrechnungen vorgestellt, um beispielhaft die Möglichkeiten der Anwendung der entwickelten und implementierten Materialmodelle für Simulationen von Stahlkonstruktionen im Brandfall aufzuzeigen. N2 - The non-linear and rate-dependent material behaviour of steel becomes particularly visible at high temperatures. For finite-element-simulations of steel structures in the event of fire, plastic and rate- dependent material behaviour should therefore be described. With this in mind, this thesis looks at previous material investigations and makes suggestions for three-dimensional material models with the corresponding properties. The phenomenological properties of structural steel are analysed on the basis of a literature study, whereby increased attention is paid to the material behaviour under loads and heating processes, as can be expected in the event of fire. The stress-strain-relation of the EC 3-1-2 used for the design of steel structures is examined. The advantages of this description, but also the missing properties for the development of a continuum-mechanical material formulation, are shown. A non-linear-elastic continuum mechanical material model of the deformation theory of plasticity is adapted in such a way that it describes the stress-strain curves according to EC 3-1-2 in the state of uniaxial stress. Furthermore, a thermoelastic-viscoplastic model is presented which is able to describe creep and relaxation during heating and cooling processes. The structure of this material model is chosen in such a way that the parameters can be easily identified using certain measurement results. The deviatoric part of the model consists of a rate-independent, plastic part and a rate-dependent, vis- coelastic part. The rate-independent, plastic part was formulated as a differential equation based on the endochronic theory of plasticity. The parameters of this material model are identified on the basis of the measurement results of stationary hot tensile tests on structural steel specimens. Both the non-linear-elastic EC 3-1-2 material model and the thermoelastic-viscoplastic material model with the material parameters adapted to mild steel are prepared numerically for use with finite- element-programs and implemented as UMAT-subroutines for ABAQUS in the FORTRAN code. Particular emphasis is placed on the provision of consistent tangent operators to enable efficient numerical calculation when using the material models. Finally, first finite-element-simulations are presented in order to show the possibilities of the developed and implemented material models for simulations of steel constructions in case of fire. T3 - BAM Dissertationsreihe - 167 KW - Brandschutz KW - Stahl KW - Brandverhalten KW - Finite-Elemente-Methode KW - Materialmodell KW - Eurocode 3-1-2 KW - UMAT KW - Fire prevention KW - Steel KW - Fire behaviour KW - Finite element method KW - Material model KW - Eurocode 3-1-2 KW - UMAT PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-507662 SN - 1613-4249 VL - 167 SP - i EP - 206 PB - Bundesanstalt für Materailforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-50766 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schartel, Bernhard A1 - Günther, Martin T1 - Flame retardancy of polyurethanes N2 - Polyurethanes (PU) represent one of the most versatile classes of plastics. They are processed and used as thermoplastic, elastomer, and thermoset. The requirements regarding flammability are correspondingly versatile. Depending on the material and the field of application, specific fire tests have to be fulfilled. This paper describes the different concepts used to fulfil these requirements by choosing the right raw materials and flame retardants. KW - Polyurethane KW - Flame retardant KW - Foam KW - Flammability KW - Pyrolysis KW - Cone calorimeter PY - 2020 VL - 17 IS - 1 SP - 44 EP - 48 PB - Dr. Gupta AN - OPUS4-50737 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -