TY - CONF A1 - Ebell, Gino T1 - Entwicklung der Potentialfeldmessung –forschung, Regelwerk, Fortbildung N2 - Ein Übersichtsvortrag zur Entwicklung der Prüfmethode zu einem etablierten und geregelten Messverfahren für die Korrosionszustandsermittlung von Stahlbetonbauwerken. T2 - GfKORR Jahrestagung - Aktuelles aus der Korrosionsforschung - Nutzen und praktische Anwendungen CY - Frankfurt a. M., Germany DA - 08.11.2022 KW - Potentialfeldmessung KW - Korrosion KW - Stahlbeton KW - Korrosionsprüfung PY - 2022 AN - OPUS4-56206 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schwarz, W. A1 - Wilsch, Gerd A1 - Katsumi, N. A1 - Ebell, Gino A1 - Völker, Tobias T1 - Ion distribution in concrete overlay, mapped by laser induced breakdown spectroscopy (LIBS), modified by an embedded zinc anode N2 - Galvanic corrosion protection by embedded zinc anodes is an accepted technique for the corrosion protection of reinforcing steel in concrete. Galvanic currents flow between the zinc anode and the steel reinforcement due to the potential difference that is in the range of a few hundred mV. The ion distribution was studied on two steel reinforced concrete specimens admixed with 3 wt.% chloride/wt. cement and galvanically protected by a surface applied EZ-anode. On both specimens, a zinc anode was embedded and glued to the concrete surface by a geo-polymer-based chloride-free binder. At one specimen, the EZ-anode was operated for 2,5 years, the EZ-anode at the other specimen was not electrically connected to the reinforcement, this specimen serves as a reference. Both specimens have been stored under identical conditions. The ion distribution between the anode (EZ-ANODE) and cathode (steel reinforcement) was studied by laser-induced breakdown spectroscopy (LIBS) after 7 months, 12 months, and 2,5 years. Results of the LIBS studies on the specimen with activated EZ-anode after 7 months, 12 months, and 2,5 years and of the reference specimen after 2,5 years are reported. Results show that diffusion of ions contributes to the changes in the ion distribution but migration, especially of chlorides towards the EZ-anode is significant despite the weak electric field – several hundred millivolts - generated by the galvanic current. Results show that chloride ions accumulate near the zinc-anode as in water-insoluble zinc-hydroxy chlorides - Simonkollite. T2 - ICCRRR 2022 CY - Capetown, South Africa KW - Corrosion KW - LIBS KW - Zinc KW - Anode PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-560576 DO - https://doi.org/10.1051/matecconf/202236404023 SN - 2261-236X VL - 364 SP - 1 EP - 7 PB - EDP Sciences CY - Les Ulis AN - OPUS4-56057 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kaplan, F. A1 - Steinbock, O. A1 - Saloga, K. A1 - Ebell, Gino A1 - Schmidt, S. T1 - Überwachung der Brücke am Altstädter Bahnhof T1 - Monitoring of the bridge at the Altstadter Bahnhof in Brandenburg a. d. Havel N2 - Die B 1-Brücke am Altstädter Bahnhof war der wichtigste Verkehrsknotenpunkt in Brandenburg an der Havel. Im Dezember 2019 wurden die überführte Bundesstraße und die Straßenbahnlinie für den Verkehr gesperrt. Grund für die Sperrung war eine einsetzende Rissbildung in den Längsträgerstegen in Verbindung mit Hohlstellen, die letztlich auf gerissene Spanndrähte zurückgeführt werden. Um eine Sperrung der hoch frequentierten unterführten Verkehrswege zu verhindern, wurde ein umfangreiches Überwachungskonzept erforderlich. Wesentlicher Bestandteil dieses Konzepts war ein auf der Schallemissionsanalyse basierendes Monitoringsystem, mit dessen Hilfe Spanndrahtbrüche aufgezeichnet und lokalisiert werden konnten. Auf Grundlage der so gewonnenen Ergebnisse konnten Schwerpunkte für die Bauwerksprüfung abgeleitet werden. In diesem Bericht werden die gewonnenen Erkenntnisse zum messtechnisch erfassten Schadensfortschritt und den damit verbundenen visuell festgestellten Schäden beschrieben. Dabei werden die Besonderheit des verbauten konzentrierten Spannglieds (Spannblockverfahren nach TGL 173-33) und des Spannstahls in Bezug auf die Schadensbilder dargestellt. Die gewonnenen Erkenntnisse sollten bei der Beurteilung anderer Bauwerke mit vergleichbarer Bauart berücksichtigt werden. KW - Korrosion KW - Spannstahl KW - Spannungsrisskorrosion PY - 2022 DO - https://doi.org/10.1002/bate.202200008 SN - 0932-8351 VL - 99 IS - 3 SP - 222 EP - 230 PB - Ernst & Sohn AN - OPUS4-54485 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Corrosion of Steel in Concrete and Corrosion Behavior of Stainless Steel N2 - In order to obtain a statement on the corrosion resistance of stainless steel against pitting corrosion, a well-tested measuring arrangement is required. For this purpose, the so-called ECISS test can be used to determine the critical chloride content. This makes it possible to assess the corrosion resistance of various stainless steels that have different chromium contents. T2 - ISO-TC17-SC16-WG13 Expertensitzung CY - Online meeting DA - 11.01.2022 KW - Corrosion KW - Lochkorrosion KW - Chloride induced corrosion KW - Concrete KW - Stainless steel PY - 2022 AN - OPUS4-54239 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Boschmann Käthler, C. A1 - Ebell, Gino A1 - Keßler, S. A1 - Schiegg, Y, A1 - Dauberschmidt, C. A1 - Angst, U. M. T1 - A comparison of methods to assess the resistance of reinforcing steel against chloride‐induced corrosion in concrete - Particular consideration of 12% chromium steel N2 - The critical chloride content C(crit) is an indicator for the corrosion resistance of reinforcing steels in concrete. In this article, several experimental methods for determining the critical chloride content C(crit) of mild and an alloyed (12% Cr) steel in cementitious materials are compared. The methods used include accelerated polarization tests and tests using more natural (unpolarized) conditions in which chloride ingress occurs by diffusion and capillary uptake. The advantages and disadvantages of the methods are discussed, in particular, with the objective of reaching a compromise between applicability to practice and feasibility in laboratory testing. KW - Chloride‐induced corrosion KW - Critical chloride content KW - Reinforced concrete KW - Testing methods PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-529751 DO - https://doi.org/10.1002/maco.202112826 SN - 0947-5117 N1 - This article has been published in 2021 as an "Early View" version with the DOI 10.1002/maco.202112609. VL - 73 IS - 3 SP - 306 EP - 325 PB - Wiley-VCH CY - Weinheim AN - OPUS4-52975 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Prestressed Concrete Structures with Concentrated Tendons - Structural Damage due to Hydrogen-Induced Stress Corrosion Cracking N2 - In the course of the deconstruction of the "Bridge of the 20th anniversary of the GDR" at the Altstädter Bahnhof in Brandenburg a. d. Havel, new information on the initiation of hydrogen-induced stress cracks was obtained. BAM was commissioned by the Brandenburg State Road Administration to participate in a corresponding joint project which is financed by the Federal Ministry for Digital and Transport. The added value of the new information gained in this project goes beyond the specific structure. It describes unexpected new damage patterns that can be transferred to other structures with concentrated tendons (tendon block method and Baur-Leonhardt method) and were previously unknown in this form. These should be made known to other developers to enable them to initiate any necessary actions. T2 - Eurocorr 2022 CY - Berlin, Gemany DA - 29.08.2022 KW - Korrosion KW - Corrosion KW - Hydrogen KW - Stress Cracking PY - 2022 AN - OPUS4-55613 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Potential Mapping - What could we measure and what should we able to detect – guideline B03 of DGZfP N2 - “Electrochemical potential mapping according to guideline B3 of DGZfP (German Society for Non-Destructive Testing) is a recognized technique for the localization of corroding reinforcing steels. Areas of corroding reinforcement steel can be located in a non-destructive manner by means of this procedure. Half‐cell potential measurements are used in order to detect chloride‐induced corrosion. However, it is not recommended in order to assess the risk of carbonation‐induced corrosion. For this purpose, determining the carbonation depth and the concrete cover appears more appropriate. The content of this specification exclusively refers to the application of mobile, local variable reference electrodes, which are only placed on the concrete surface while measuring. The technique distinguishes itself thereby from the range of corrosion monitoring systems with stationary installed reference electrodes and sensor systems, respectively, whereby it is possible to continuously track measurements within the area of the installed electrodes. However, these methods are not dealt with in this specification.” T2 - NDT-CE 2022 CY - Zurich, Switzerland DA - 16.08.2022 KW - Korrosion KW - Potentialfeldmessung KW - Corrosion KW - Half-cell potential KW - Potential mapping PY - 2022 AN - OPUS4-55524 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Feistkorn, S. A1 - Algernon, D. A1 - Arndt, R. A1 - Ebell, Gino A1 - Friese, M. A1 - Grosse, C. U. A1 - Holstein, R. A1 - Niederleithiger, Ernst A1 - Schickert, M. A1 - Schulze, S. A1 - Taffe, A. A1 - Walther, A. A1 - Wolf, J. A1 - Zoega, A. A1 - Zwanzig, M. T1 - Introduction to DIN 4871: Qualification of NDT Personnel in Civil Engineering (NDT‐CE) N2 - Recently, non-destructive testing in civil engineering (NDT-CE), in particular of concrete components, has successfully mastered the leap from research to practice. Several methods have been established for field inspections to determine the concrete cover of reinforcement or to estimate the compressive strength as well as other parameters related to the concrete material. In addition, the application of non-destructive testing is indispensable, if information about the inner structure - such as the location of rebars and tendon ducts or the damage-related condition assessment to detect grouting defects, honeycombs, delamination, or corrosion - is required. Besides the selection of a suitable NDT method and an appropriate inspection system, the reliability of the results depends largely on the person who applies the non-destructive inspection technique and evaluates the inspection results. To ensure a high quality of non-destructive concrete evaluation as well as to keep the uncertainty caused by the inspection personnel to a minimum, structured, consistent, and regulated theoretical as well as practical training of inspection personnel is essential. To close this gap, the subcommittee of education and training (UA-A) within the committee for NDT-CE of the German Society for Non-Destructive Testing (DGZfP) has been reactivated in 2018 to establish uniform training standards for non-destructive concrete inspections in the long term. The subcommittee consists of scientists, practitioners, authorities, and clients. So far, the national standard DIN 4871 “Non-destructive testing - Qualification of NDT personnel in Civil Engineering (NDT-CE)” was developed. This standard considers the civil-industry-specifics, for example, that standards for NDT of concrete, as well as related product standards with a few exceptions, still do not exist at the moment. Within this presentation, the concept, the connection to ISO 9712 and other standards as well as an overview of the recently developed German standard DIN 4871 will be presented. T2 - NDT-CE 2022 CY - Zurich, Switzerland DA - 16.08.2022 KW - Non-destrucive testing KW - Civil engineering PY - 2022 AN - OPUS4-55526 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schwarz, W. A1 - Wilsch, Gerd A1 - Katsumi, N. A1 - Ebell, Gino A1 - Völker, Tobias T1 - Ion distribution in concrete overlay, mapped by laser induced breakdown spectroscopy (LIBS), modified by an embedded zinc anode N2 - Galvanic corrosion protection by embedded zinc anodes is an accepted technique for the corrosion protection of reinforcing steel in concrete. Galvanic currents flow between the zinc anode and the steel reinforcement due to the potential difference that is in the range of a few hundred mV. The ion distribution was studied on two steel reinforced concrete specimens admixed with 3 wt.% chloride/wt. cement and galvanically protected by a surface applied EZ-anode. On both specimens, a zinc anode was embedded and glued to the concrete surface by a geo-polymer-based chloride-free binder. At one specimen, the EZ-anode was operated for 2,5 years, the EZ-anode at the other specimen was not electrically connected to the reinforcement, this specimen serves as a reference. Both specimens have been stored under identical conditions. The ion distribution between the anode (EZ-anode) and cathode (steel reinforcement) was studied by laser-induced breakdown spectroscopy (LIBS) after 7 months, 12 months, and 2,5 years. Results of the LIBS studies on the specimen with activated EZ-anode after 7 months, 12 months, and 2,5 years and of the reference specimen after 2,5 years are reported. Results show that diffusion of ions contributes to the changes in the ion distribution but migration, especially of chlorides towards the EZ-anode is significant despite the weak electric field – several hundred millivolts - generated by the galvanic current. Results show that chloride ions accumulate near the zinc-anode as in water-insoluble zinc-hydroxy chlorides - Simonkolleit. T2 - ICCRRR 2022 CY - Capetown, South Africa DA - 03.10.2022 KW - Korrosion KW - Corrosion KW - LIBS KW - Zinc PY - 2022 AN - OPUS4-55948 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino A1 - Burkert, Andreas T1 - Neue Erkenntnisse zu wasserstoffinduzierten Spannungsrissen infolge korrosiver Belastung hochempfindlicher Spannstähle in Spannblockverfahren nach TGL 173-33 N2 - Brückenbauwerke, die im Spannblockverfahren hergestellt wurden, können bauartbedingt wasserstoffinduzierte Spannungsrisse über den gesamten Querschnitt eines Spannkanals aufweisen. Das Risswachstum kann infolge dynamischer Beanspruchung über die Nutzungsdauer fortschreiten und zu Spanndrahtbrüchen führen. T2 - 5. Brückenkolloquium CY - Ostfildern, Germany DA - 06.09.2022 KW - Korrosion KW - Spannungsrisskorrosion KW - Spannstahl PY - 2022 SP - 567 EP - 572 PB - Expert -TAE CY - Esslingen AN - OPUS4-55662 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -