TY - JOUR A1 - Sturm, Patrick A1 - Moye, J. A1 - Gluth, Gregor A1 - Vogler, Nico A1 - Taffe, A. A1 - Kühne, Hans-Carsten ED - Rossignol, S. ED - Gluth, Gregor T1 - Properties of alkali-activated mortars with salt aggregate for sealing structures in evaporite rock N2 - Concrete structures for sealing of tunnels in the host rock are an essential part of systems for nuclear waste storage. However, concretes based on blended cements or magnesium oxychloride cements, which are commonly considered for this application, can deteriorate severely due to a significant heat of hydration and associated deformation and cracking. Alkali-activated materials (AAMs) offer a potential solution to this problem because of their low heat release during hardening. To explore their suitability for the construction of sealing structures in evaporite rock, various AAMs with salt aggregate were studied regarding fresh properties, heat release, mechanical properties and microstructure. The heat of reaction of the AAMs was up to 55% lower than that of a blended cement designed for sealing structures, indicating significant benefits for the intended application. Other relevant properties such as mechanical strength and permeability depended strongly on the mix-design of the AAMs and curing conditions. KW - Alkali-activated materials KW - Geopolymers KW - Nuclear waste storage KW - Sealing structures KW - Evaporite rock PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-519422 DO - https://doi.org/10.1016/j.oceram.2020.100041 SN - 2666-5395 VL - 5 IS - Special issue: Alkali-activated materials and geopolymers in ceramics and beyond SP - 1 EP - 8 PB - Elsevier CY - Amsterdam AN - OPUS4-51942 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kästle, Emanuel A1 - Duffner, Eric A1 - Ghaznavi, Ali T1 - DAVID Project meeting 23.09.2025 N2 - Yearly report on the DAVID project, presented in front of the consortial partners. The report shows the progress achieved by the DAVID project team at BAM in terms of testing newly developed carbon-fiber reinforced pressure vessels of type IV. T2 - DAVID project meeting CY - Berlin, Germany DA - 23.09.2025 KW - Acoustic Emission KW - Pressure Vessels KW - DAVID project KW - Damage monitoring KW - Fiber reinforced polymers PY - 2025 AN - OPUS4-65289 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram T1 - On the assessment of dynamic fracture toughness of ferritic ductile cast iron using the master curve concept N2 - An established and validated method to determine and assess dynamic fracture toughness values of ferritic ductile cast iron (DCI) in the ductile-to-brittle transition regime is currently not available. Although the ASME-Code, Sect. III, Div. 3, WC-2330 explicitly requires safety assessment considerations for dynamic loading, sufficiently substantial information on the procedure is not given. Therefore, the applicability of the probabilistic Master Curve (MC) concept according to ASTM E1921 to DCI is being investigated in the joint German research project MCGUSS conducted by BAM Berlin and MPA Stuttgart. Using a tailored manufacturing specification, a DCI material of grade GJS-400 has been casted to provide a test material which is very homogeneous but typical for heavy-sections. The experimental test program covers test specimens of various geometries and sizes (Tensile, Charpy-V, Pellini, SE(B)10, SE(B)25, SE(B)140, DC(T)9, C(T)25 and C(T)50). In total about 500 specimens will be tested to investigate and validate the Master Curve concept and its background for DCI (e.g. size effects, weakest-link, Weibull distribution, microstructure-property correlation). While the whole project has not yet concluded, several work packages have already been completed. This presentation is focused on dynamic large-scale fracture mechanics test series using SE(B)140 specimens and instrumented Charpy impact testing using ISO-V specimens. T2 - European Conference on Fracture 2024 CY - Zagreb, Croatia DA - 26.08.2024 KW - Dynamic fracture toughness KW - Ductile cast iron KW - Master curve concept PY - 2024 AN - OPUS4-61452 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram T1 - Recent Results on the Investigation of the Master Curve Concept for Ferritic Ductile Cast Iron N2 - Within the current framework for safety assessment of ferritic ductile cast iron (DCI) containers for transport as well as interim and final storage of radioactive materials, the IAEA guidelines SSG 26 apply fracture mechanics principles. Crack initiation in either, stable or unstable modes is generally forbidden. Additionally, for DCI, the ASME-Code, Sect. III, Div. 3, WC-2330, explicitly requires a safety proof regarding dynamic loading conditions. Nevertheless, corresponding information given in the ASME Code does not seem to be sufficient to appropriately perform a dynamic fracture mechanics safety assessment for DCI. To address and improve this status of the dynamic brittle fracture safety assessment framework for DCI, the application of the fracture mechanics master curve (MC) concept to DCI is being investigated in an ongoing joint research project (acronym MCGUSS) between BAM Berlin and MPA Stuttgart. For ferritic DCI, the MCGUSS project addresses the currently lacking systematic review of applicability and potential modifications to the assumptions and the procedure according to ASTM E1921. The aim is to establish a methodology to determine and assess dynamic fracture toughness values of DCI in the ductile-to-brittle transition regime using small samples extracted from a component. The research approach and the planned investigations were outlined in more detail earlier. This paper is focused on the discussion of recent experimental results to establish the dynamic fracture mechanics toughness data base and its MC analyses. MCGUSS fracture mechanics test setups and the dynamic fracture toughness data base achieved at the time of abstract submission is discussed (covering 128 specimens). Current application limits of ASTM E1921 MC to DCI are discussed, and planned investigations to further investigate and modify the MC procedure for DCI are outlined. T2 - ASTM 23rd International ASTM/ESIS Symposium on Fatigue and Fracture Mechanics CY - Atlanta, GA, USA DA - 12.11.2025 KW - Dynamic fracture toughness KW - Ductile cast iron KW - Safety assessment KW - Master curve KW - Statistics PY - 2025 AN - OPUS4-64746 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, Marcel A1 - Baer, Wolfram T1 - Investigation of the Master Curve Concept for Ferritic Ductile Cast Iron N2 - The current framework for safety assessment of ferritic ductile cast iron (DCI) containers for transport and storage of radioactive materials applies fracture mechanics principles. As established by the IAEA safety standard SSG 26, prevention of crack initiation is the governing criterion and no reliance in design should be placed on any predicted ductile tearing resistance. Similarly, the ASME-Code, Sect. III, Div. 3 explicitly deals with DCI and requires a safety proof for dynamic loading conditions. However, information given in the guidelines does not seem to be sufficient to appropriately perform such dynamic fracture mechanics safety assessments. The ongoing German research project MCGUSS is tailored to tackle this status. In MCGUSS, the application potential of the probabilistic fracture mechanics master curve (MC) concept according to ASTM E1921 is being systematically investigated and potential modifications specific for dynamic brittle fracture of DCI will be identified. While MCGUSS covers testing of a high number of SE(B)- and C(T)-type specimens, this poster focuses on preliminary C(T) results. The obtained data was statistically analyzed, and current results of MC analyses are discussed. Special emphasis of MCGUSS is on using optical and scanning electron microscopy to link microstructural damage and failure processes to the fracture toughness data gained. A fracture mechanism called "specimen size-dependent arrest of local brittle fractures before global brittle failure by weakest link" is proposed to describe the established dynamic toughness data. Concerning the MC concept, it was shown that the ASTM E1921 procedure cannot simply be adopted to dynamic DCI toughness data on a one-to-one basis. Material specific modifications are being investigated and the DCI dynamic fracture toughness data base is to be expanded. T2 - MPA Conference 2025 CY - Stuttgart, Germany DA - 06.10.2025 KW - Dynamic fracture toughness KW - Ductile cast iron KW - Safety assessment KW - Master curve KW - Statistics PY - 2025 AN - OPUS4-64367 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, Marcel A1 - Baer, Wolfram A1 - Mayer, Uwe A1 - Weihe, Stephan T1 - Investigation of the Master Curve Concept for Ferritic Ductile Cast Iron N2 - Within fracture mechanics safety assessment for steels in nuclear technology, the probabilistic master curve (MC) concept according to ASTM E1921 is currently used for quasi-static loading conditions as a supplement to the established deterministic ASME reference curve concept. However, for ductile cast iron (DCI), a systematic review of potential modifications to the assumptions and the procedure according to ASTM E1921 and an associated validation are still lacking. For this reason, the application of the fracture mechanics MC concept to ferritic ductile cast iron is being investigated in a recently started joint research project between MPA Stuttgart and BAM Berlin. According to the IAEA guidelines SSG 26, the safety assessment of DCI containers for transport as well as storage of radioactive materials is based on the fracture mechanics criterion of general crack initiation exclusion. Within this context, the focus of the current research project is on the further development of brittle fracture safety assessment methods. Therefore, a methodology shall be established to determine and assess dynamic fracture toughness values of DCI in the ductile-to-brittle transition regime, using samples extracted from a component. For the experimental program, a DCI material will be produced as it is generally used for transport and storage containers. A basic mechanical-technological material characterization consisting of tensile, Charpy and Pellini tests is planned and a comprehensive fracture mechanics test program was compiled covering dynamic testing of DC(T)9, C(T)25, C(T)50, SE(B)10, SE(B)25, and SE(B)140 specimens. Numerical analyses of different specimen geometries and test setups are planned to investigate the influences of stress triaxiality and loading rate. Throughout the experimental program, the microstructure-property relationship will be investigated based on quantitative metallographic and fractographic analyses. Finally, different MC assessment strategies will be considered and modifications will be made if necessary. T2 - 21st International Symposium ASTM/ESIS Symposium on Fatigue and Fracture Mechanics CY - Washington, DC, USA DA - 08.11.2023 KW - Ductile Cast Iron KW - Dynamic Fracture Toughness KW - Cleavage Fracture KW - Master Curve Concept PY - 2023 SP - 1 EP - 5 PB - ASTM International CY - West Conshohocken, PA AN - OPUS4-59064 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, Marcel A1 - Baer, Wolfram A1 - Mayer, Uwe A1 - Weihe, Stefan T1 - Master Curve-Auswertungen und Untersuchung des Größeneffekts für c(t)-proben - Aktuelle Erkenntnisse zur Untersuchung des Master Curve Konzepts für ferritisches Gusseisen mit Kugelgraphit bei dynamischer Beanspruchung N2 - Ausgehend vom Stand des Regelwerkes und der Forschung wird in einem BMUV-Verbundprojekt zwischen der MPA Stuttgart und der BAM Berlin die Anwendung des Master Curve (MC)-Konzepts auf ferritisches Gusseisen mit Kugelgraphit (DCI) untersucht. Ziel des Verbundprojekts ist die Anwendbarkeit des MC-Konzepts näher zu untersuchen und ggf. Modifikationen vorzunehmen, um eine Bewertungsmethode für die dynamische Bruchzähigkeit von DCI im Übergangsbereich zu erarbeiten. Auf den Jahrestagungen 2023 und 2024 des DVM-AK Bruchmechanik und Bauteilsicherheit wurden bereits der Forschungsansatz sowie erste Ergebnisse des Projekts MCGUSS präsentiert. Der Beitrag für die diesjährige Tagung soll nun MC-Auswertungen und den Größeneffekt für C(T)-Proben aus DCI diskutieren. T2 - 57. Tagung des DVM-Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Köln, Germany DA - 18.02.2025 KW - Versuche KW - Master Curve KW - Bruchmechanik KW - Dynamische Beanspruchung KW - Gusseisen mit Kugelgraphit PY - 2025 DO - https://doi.org/10.48447/BR-2025-495 SP - 123 EP - 129 PB - DVM-Verlag CY - Berlin AN - OPUS4-62555 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Holzwarth, Marcel A1 - Mayer, Uwe A1 - Baer, Wolfram T1 - Investigating the Applicability of the Master Curve Concept for Ductile Cast Iron – Early Results for 2 Different Test Temperatures N2 - Based on the state-of-the-art research and regulations, the application of the fracture mechanics master curve (MC) concept to ferritic ductile cast iron (DCI) is being investigated in a joint research project between MPA Stuttgart and BAM Berlin. This paper outlines the research approach, the planned investigations and first results of the experimental program. T2 - 8th SEDS Workshop: Safety of Extended Dry Storage CY - Garching, Germany DA - 15.05.2024 KW - Dynamic fracture KW - Brittle fracture KW - Ductile cast iron KW - Master Curve PY - 2024 SP - 1 EP - 4 AN - OPUS4-60013 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Broichert, C. A1 - Klingenhof, M. A1 - Frisch, M. A1 - Dresp, S. A1 - Kubo, N.M. A1 - Artz, J. A1 - Radnik, Jörg A1 - Palkovits, S. A1 - Beine, A.K. A1 - Strasser, P. A1 - Palkovits, R. T1 - Particle size-controlled synthesis of highperformance MnCo-based materials for alkaline OER at fluctuating potentials N2 - For the large-scale generation of hydrogen via water electrolysis the design of long term stable and active catalysts for the oxygen evolution reaction (OER) remains a key challenge. Most catalysts suffer from severe structural corrosion that becomes even more pronounced at fluctuating potentials. Herein, MnCo based cubic particles were prepared via a hydrothermal approach, in which the edge length of the micron-sized particles can be controlled by changing the pH value of the precursor solution. The cubes are composed of varying amounts of MnCo2O4, CoCO3 and a mixed (Mn/Co)CO3 phase. Structure–activity relationships were deduced revealing a volcano-type behavior for the intrinsic OER activity and fraction of spinel oxide phase. A low overpotential of 0.37 V at 10 mA cm−2 and a stability of more than 25 h was achieved in 1.0 M KOH using a rotating disc electrode (RDE) setup. The best performing catalyst material was successfully tested under dynamic process conditions for 9.5 h and shows a superior catalytic activity as anode for the Overall water splitting in an electrolyser setup in 1.0 M KOH at 333 K compared to a reference NiCo-spinel catalyst. KW - Water electrolysis KW - Oxygen evolution reaction KW - Structure activity relationships PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-536050 DO - https://doi.org/10.1039/d1cy00905b SN - 2044-4753 VL - 11 IS - 12 SP - 7278 EP - 7286 PB - Royal Society of Chemistry AN - OPUS4-53605 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram T1 - Statistische Auswertung der SE(B)-Bruchzähigkeitsdatenbasis und Untersuchungen zum Bruchmechanismus - Neue Ergebnisse zur Untersuchung des Master Curve Konzepts für ferritisches Gusseisen mit Kugelgraphit bei dynamischer Beanspruchung (Projekt MCGUSS) N2 - Die Zielstellung des laufenden Kooperationsprojektes MCGUSS zwischen der BAM Berlin und der MPA Stuttgart ist es, das probabilistische Master Curve (MC)-Konzept hinsichtlich seiner Übertragbarkeit auf ferritisches Gusseisen mit Kugelgraphit (DCI) zu untersuchen. Über Teilergebnisse der Arbeiten wurde bereits auf den Jahrestagungen 2023 bis 2025 des DVM-AK Bruchmechanik und Bauteilsicherheit berichtet. Der vorliegende Beitrag hat zwei Schwerpunkte. Zum einen wurde die Datenbasis der dynamischen Bruchzähigkeit für SE(B)-Proben der Dicken 10 mm, 25 mm und 140 mm auf insgesamt 101 Versuche bei Temperaturen von -40 °C bis -140 °C erweitert, statistisch ausgewertet sowie MC-Analysen unterzogen. Die Ergebnisse zeigen, dass die Daten sich zwar mit einer Weibullverteilung gut beschreiben lassen, die MC-Methode nach ASTM E1921 jedoch nicht ohne Weiteres anwendbar ist, sondern Modifikationen erforderlich sind. Des Weiteren werden neue Ergebnisse zum werkstoffspezifischen Bruchmechanismus bei dynamischer Belastung im unteren Übergangsbereich der Zähigkeit diskutiert. Die fraktographische Datenbank wurde durch REM-Analysen weiterer Bruchflächen von SE(B)25-Proben bei -40 °C, -60 °C und -80 °C ergänzt. Die Ergebnisse unterstreichen die prägende Rolle, die Rissarrestereignissen im Verlauf des dynamischen Sprödbruchversagens bei DCI zukommt. Der in MCGUSS zur Erklärung eines gegenüber Stahl inversen Probengrößeneinflusses vorgeschlagene Mechanismus „Specimen size-dependent arrest of local brittle fractures before global brittle failure by weakest link“ wird dadurch weiter unterstützt. T2 - DVM-Jahrestagung 2026 des Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Stuttgart, Germany DA - 24.02.2026 KW - Dynamic fracture toughness KW - Ductile cast iron KW - Safety assessment KW - Master curve KW - Statistics PY - 2026 AN - OPUS4-65593 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -