TY - CONF A1 - Kromm, Arne T1 - LTT-Zusatzwerkstoffe zur Optimierung von Schweißeigenspannungen N2 - Der Vortrag gibt eine Einführung zum Thema LTT-Zusatzwerkstoffe. Anhand experimenteller Befunde werden die Mechanismen erläutert und die Auswirkungen auf die Schweißeigenspannungen verdeutlicht. T2 - 1. LTT-Workshop des ISF RWTH Aachen CY - Aachen, Germany DA - 11.05.2022 KW - LTT-Zusatzwerkstoff KW - Hochfester Stahl KW - Eigenspannungen KW - Martensit KW - Phasenumwandlung PY - 2022 AN - OPUS4-56267 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Griesche, Axel T1 - The debye waller factor for temperature distribution determination in NBEI experiments: a case study for GTAW N2 - We could show in GTAW experiments with steel samples that the attenuation of neutron transmission underneath the welding torch due to the Debye-Waller-effect correlates well with sample temperatures obtained by FE numerical simulations. This would allow principally to determine sample temperatures by measuring the neutron beam attenuation. T2 - ITMNR-9 CY - Buenos Aires, Argentina DA - 17.10.2022 KW - Debye waller factor KW - GTAW KW - Temperature distribution determination PY - 2022 AN - OPUS4-56150 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael T1 - Repair welding of pressurized in-service hydrogen pipelines - A review on current challenges and strategies N2 - As energy carrier of the future, green hydrogen can make a decisive contribution to a sustainable energy supply. Particularly important is the decarbonization of heavy industry. Therefore, a reliable supply of hydrogen must be guaranteed. A hydrogen pipeline grid can achieve this purpose. In Europe concrete plans for a hydrogen pipeline grid already exist, as the so called “European Hydrogen backbone”. As building a completely new pipeline grid is economically not justifiable, a dual-way strategy of repurposing natural gas (NG) pipelines and newly built pipelines is intended. Long distance pipeline grids require regular maintenance and repairs. For natural gas (NG) pipelines in-service welding is state of the art. Concepts such as hot-tapping (drilling into pressurized pipelines) and “stoppling” (sealing off pipeline sections after installing bypasses or pressure relieves) allow the repair of damaged pipeline sections or the installation of new branches without shutting the pipeline down, which in most cases isn’t possible from an economic standpoint. The EIGA 121/14 guideline already pointed out in 2014 that “a hydrogen hot-tap shall not be considered a routine procedure”. This shows that the determination of the transferability of these repair concepts to hydrogen pipelines is of utmost importance. Due to the degrading effects of hydrogen on mechanical proper-ties, commonly referred to as “hydrogen embrittlement” it is necessary to understand and investigate the occurring effects. In the special case of repair welding on in-service hydrogen pipelines an increased hydro-gen uptake due to a large heat input and microstructural changes in the material needs to be considered. Therefore, material degradation must be investigated to determine whether modifications of repair procedures are necessary to ensure a reliable and safe hydrogen transportation via pipelines. For this reason, this paper gives an overview on existing weld repair concepts and its risks and limitations in terms of hydrogen absorption and possible embrittlement effects when transferred to hydrogen pipelines. The complexity lies in a large variety of materials (low alloyed steels), pipeline diameters and corresponding welded joints. The material compatibility of materials in used (repurposed NG-pipelines) and new condition must be investigated. Particularly for repurposed/used pipelines the effect of a pre-matured/corroded inner surface and sometimes insufficient documentation of the material “history” needs to be considered. An overview on ongoing and completed R&D-projects with respect to repair concepts for hydrogen pipelines and hydrogen effects on pipeline materials is given. The focus hereby lies on possible methods of material testing and modeling. Its current difficulties, limits and possible solution will be discussed. T2 - IIW Intermediate Meeting, Com. II-A CY - Incheon, Republic of Korea DA - 12.03.2024 KW - Hydrogen KW - Repair welding KW - Pipelines KW - In-service PY - 2024 AN - OPUS4-59674 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael T1 - Combined effect of heating rate and restraint condition on stress relief cracking susceptibility during PWHT of thick-walled Cr-Mo-V steel submerged arc welded joints N2 - Contemporary steels creep-resistant steels like the 13CrMoV9-10 are used as thick plates e.g., for applications in hydrocrackers. The large plate thickness requires high efficiency welding processes like submerged arc welding (SAW) and a mandatory post weld heat treatment (PWHT). The PWHT-parameters stem from a combination of empirical knowledge and traditional experiments on free shrinking (FS) welds. In that connection, the formation of so-called stress-relief cracking (SRC) must be anticipated. The SRC susceptibility of a welded component is a complex combination and interaction of com-ponent specific, thermal, and metallurgical factors. Many of which have to date not been conclusively researched. For example, it is well known that SRCs develop during PWHT due to formation and growth of carbides on prior austenite grain boundaries, resulting in a significant hardness increase (secondary hardening) and toughness decrease. This leads to a high SRC susceptibility of the coarse grain heat-affected zone (CGHAZ) of the last weld bead during PWHT. This is intensified in case of high residual stresses from the component-specific, structurally induced stiffness. In combination with multi-layer welding this leads to a multiaxial stress distribution. Nonetheless, the combined effect of PWHT and high-residual stresses on the SRC formation is merely unknown. For that reason, this study presents the effect of different heating rates in conjunction with a certain component stiffness. For that reason, SAW joints of 13CrMoV9-10 steel were investigated under FS and defined external restraint condition. T2 - IIW Intermediate Meeting, Com. II-A CY - Incheon, Republic of Korea DA - 12.03.2024 KW - Stress relief cracking KW - Welding KW - Post weld heat treatment KW - Submerged arc welding KW - Cr-Mo-V steel KW - Creep-resisting steel PY - 2024 AN - OPUS4-59673 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Kannengießer, Thomas T1 - Call for interested people to contribute to series of comprehensive papers on welding and joining of components for sustainable energy systems N2 - Joining and welding technologies are of high importance for the manufacturing of components and parts used in sustainable energy generation, conversion, and transport. In that connection, offshore and on-shore installed wind turbines are of high interest for the generation of electrical energy as well as photo-voltaic systems (solar cells). The electricity can be either directly transported or conversed via power-to-gas e.g., to hydrogen. In that scope, electrolyzer up to MW-range are of interest as well as the conver-sion back to electricity via fuel cells. In addition, hydrogen is a key element of the decarburization of in-dustries as well as the mobility sector encompassing sea, air and land transportation driven by hydrogen or its derivates. Well-known examples cover the direct reduction of iron ore to replace the conventional blast furnace process up to gas turbines or fuel cells for home-end use. All mentioned technologies re-quire reliable components, which are to a high extend dependent on joining and especially welding pro-cessing of materials. Especially, the (petro-) chemical industry has many years of experience with both materials used in hydrogen applications. The challenge is e.g., the transition to mass production of sys-tem components of electrolyzers/fuel cells and for distribution grids. At this point, the scalability of cur-rently applied joining processes often limits the economic efficiency, whereas especially laser welding or additive manufacturing will be of high interest. In that connection, it is very important to provide answers by joint research of universities, institutes, and industrial companies. Very often, solutions are already available and “just” have to be investigated and adapted for the new application, like repair welding of NG pipelines. For that reason, we want to set up a series of comprehensive papers with the aforementioned title. The idea is to get an in-depth but manageable overview of the importance of joining technologies in sustaina-ble energy generation, conversion, and transport encompassing current processes, limitations, and fur-ther perspectives. In that connection, the additive manufacturing is gaining more and more attention. If applicable, current challenges in the adaption or creation of new standards/regulations shall be addressed. T2 - IIW Intermediate Meeting, Com. II-A CY - Incheon, Republic of Korea DA - 12.03.2024 KW - Hydrogen KW - Welding KW - Comprehensive study KW - Component manufatcturing KW - Additive manufacturing PY - 2024 AN - OPUS4-59676 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Liepold, Philipp T1 - CTS Testing of High-Strength Filler Materials N2 - Controlled Thermal Severity (CTS) tests are known for applicatying high restraint intensity to fillet welds. Due to two different variations of the test it was possible to apply different amounts of restraint intensity to high-strength GMAW fillet welds at a high level of restraint. The results show the effect of heat input, filler material and restraint intensity on solidification cracking susceptibility. T2 - DIN Sitzung NA 092-00-05 GA „Zerstörende Prüfung von Schweißverbindungen“ (DVS AG Q 4/Q 4.1) CY - Berlin, Germany DA - 20.03.2024 KW - CTS PY - 2024 AN - OPUS4-59773 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Eigenspannungsabbau mittels LTT - Schweißzusätzen unter Berücksichtigung der Nahtgeometrie N2 - Der Vortrag befasst sich mit der gezielten Einbringung zusätzlicher LTT-Lagen zur Erzeugung von Druckeigenspannungen in ermüdungskritischen Bereichen von konventionellen Schweißverbindungen. Dies ermöglicht eine wirtschaftliche Lösung, ohne die Integrität der Schweißverbindungen zu beeinträchtigen. Dazu wurden Längssteifen aus hochfestem Stahl in der ersten Lage mit konventionellem Schweißzusatzwerkstoff mittels Metall-Lichtbogenschweißen geschweißt. Anschließend wurde ein Chrom-Nickel-legierter LTT-Schweißzusatz auf die Stirnseiten der Steifen aufgebracht. Durch Variation der Schweißparameter konnten verschiedene Schweißnahtgeometrien des LTT-Zusatzwerkstoffs analysiert werden. T2 - NA 092-00-05 GA "Gemeinschaftsarbeitsausschuss NAS/NMP: Zerstörende Prüfung von Schweißverbindungen (DVS AG Q 4/Q 4.1) CY - Berlin, Germany DA - 20.03.2024 KW - LTT KW - Eigenspannungen KW - hochfester Stahl PY - 2024 AN - OPUS4-59752 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Investigation of hot cracking susceptibility via Modified Varestraint Transvarestraint testing of high-strength filler material N2 - MVT testing was conducted in Transvarestraint mode in multiple welding conditions and under a range of bending speeds. The materials observed were high strength filler metals used in GTAW namely DIN EN ISO 16834-A G 69 4 M21 Mn3Ni1CrMo (G69), 16834-A G 89 6 M21 Mn4Ni2CrMo (G89 6), 16834-A G 89 5 M21 Mn4Ni2,5CrMo (G89 5) and a filler wire 18276-A T 89 4 ZMn2NiCrMo M M21 1 H5 (T89). For evaluation light optical microscope pictures were used. Pixels containing cracks were manually segmented using a self-written program. Out of the segmented images data including crack length, position and area can be calculated for every crack. The results show dependencies of solidification cracking on the test parameters. T2 - IIW Intermediate Meeting Comission II-C CY - Incheon, Republic of Korea DA - 12.03.2024 KW - Solidification cracking KW - High strength steel KW - Varestraint test PY - 2024 AN - OPUS4-59749 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Nina T1 - Ti and Nb influence on the HAZ microstructures of weld-simulated high strength structural steel S690QL N2 - High-strength low-alloyed (HSLA) steels with yield strength / proof stress ≥ 600 MP are the basis of modern light-weight steel constructions. Indeed, the economic and ecological benefits strongly depend on their processability in terms of welding. In this context, he use of highly productive welding processes, suitable welding consumables is of vital interest and requires a fundamental understanding of the microstructural changes in the HSLA steel and especially the heat-affected zone (HAZ) of the welded joint. Microalloying elements, such as Ti or Nb, are essential to achieve the desired mechanical properties. In this context, the underlying standards such as EN 10025-6 only specify maximum values, resulting in different manufacturer customized microalloy concepts. Furthermore, even small deviations can have a drastic effect expressed by an excessive hardening or softening despite identical welding conditions and filler metal. The reason is the different thermal stability of the Ti and Nb-related precipitates (typically carbides or carbon nitrides). As a result, it is difficult (or even impossible) to adequately predict the weldability. Against this background, different microalloying routes with varying Ti and Nb contents for a S690QL reference grade were systematically investigated in terms of lab-cast alloys close to realistic chemical compositions. To investigate the influence of the welding heat input on the HAZ microstructure formation, physical simulations were carried with specified peak temperatures and cooling times (by a dilatometer, see Fig. 1a). The focus was the identification of the occurring phase transformations during cooling and the final HAZ microstructure, see Fig. 1b. In this context, a double welding cycle was simulated to further identify the behavior of the so-called intercritical HAZ (where softening is likely to occur) in case of the common multi-layer welding for thick plates, see Fig. 1c. The results showed: (1) microalloying has significant influence on the formation of the individual HAZ dependent on (2) the thermal stability of the Ti or Nb-precipitates and (3) synergistic effects of further elements such as Mo and their effect on phase transformations in the HAZ. The results represent a microstructure-based validation of welding processing of such HSLA-steels e.g. in terms of preferred microalloy and weld heat input combinations. T2 - MaterialsWeek/SteelInnovation 2025 CY - Frankfurt am Main, Germany DA - 02.04.2025 KW - HSLA KW - Dilatometry KW - Microalloying elements KW - HAZ-Softening KW - Digital Image Correlation (DIC) PY - 2025 AN - OPUS4-62938 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael T1 - Simulation der Wasserstoffverteilung in UP-geschweißten Grobblechen als Bewertungstool für die Kaltrissanfälligkeit von Offshorestrukturen N2 - Gründungsstrukturen für Offshore-Windkraftanlagen bestehen in der Regel aus hochfesten Stahlgrobblechen, die im UP-Verfahren geschweißt werden, durch den u.U. größere Mengen an Wasserstoff eingebracht werden können. Die große Blechdicke führt zudem zu langen Diffusionswegen und einer verlängerten Diffusionszeit für den Wasserstoff. Infolgedessen kann sich der Wasserstoff in Bereichen mit hoher mechanischer Spannung und Dehnung ansammeln und daher zu einer verzögerten Kaltrissbildung führen. Aufgrund der verzögerten Diffusion muss daher eine Mindestwartezeit von bis zu 48 h eingehalten werden, bevor eine zerstörungsfreie Prüfung durchgeführt wird. Darüber hinaus ist die Beurteilung möglicher Kaltrissstellen sehr komplex. Es wurde daher ein numerisches Modell zur Abbildung einer bauteilähnlichen Schweißnahtprüfung entwickelt. Dazu wurde das Temperaturfeld während des Schweißens und der anschließenden Abkühlung experimentell bestimmt und numerisch simuliert. Auf dieser Grundlage wurde Diffusionsmodell zur numerischen Simulation der zeitlich-örtlichen Wasserstoffkonzentration erstellt. Mit diesem Modell wurden zwei Anwendungsfälle simuliert: (1) Veränderung der Wasserstoffverteilung als Funktion des Temperaturzyklus während des Mehrlagenschweißens und (2) für das Wartezeitintervall ≤ 48 h. Ein Vorteil des Diffusionsmodells ist die Simulation einer normierten Konzentration, d.h. zwischen „0“ (kein Wasserstoff) und „1“ (max. Konzentration), die auf experimentell ermittelte Wasserstoffkonzentrationen skaliert werden kann. T2 - 6. Symposium Materialtechnik CY - Clausthal-Zellerfeld, Germany DA - 20.02.2025 KW - Gründungsstrukturen KW - Offshore KW - Kaltrissbildung KW - Wasserstoff KW - Numerische Simulation PY - 2025 AN - OPUS4-62616 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -