TY - CONF A1 - Rhode, Michael T1 - Welding (and joining) technologies for the hydrogen economy - a short overview N2 - This study gives an overview on the important field of joining processes for component fabrication in hydrogen technologies. The current main issues and future perspectives are highlighted for the different technological field of hydrogen generation, storage, transport and use. In addition, the emerging field of additive manufacturing is included. Some remarks are given for standardization and regulations. T2 - Meeting of the European Welding Association (EWA), Executive Committee (EC) 1 CY - Frankfurt am Main, Germany DA - 22.03.2023 KW - Hydrogen KW - Welding KW - Research KW - Study PY - 2023 AN - OPUS4-57222 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael T1 - Bewertung und Vermeidung von schweißverarbeitungsbedingten Rissen in hochfesten Baustählen N2 - Die vorliegende Präsentation fasst die Ergebnisse von drei laufenden bzw. beendeten AiF/IGF-Projekten zusammen, die über die Forschungsvereinigung Stahlanwendung FOSTA e.V. an der BAM bearbeitet wurden zum Thema: Bewertung und Vermeidung von schweißverarbeitungsbedingten Rissen in hochfesten Baustählen. T2 - FOSTA Tagung: Hochfester Stahl im Stahl und Anlagenbau CY - Essen, Germany DA - 16.05.2023 KW - Studie KW - Schweißen KW - Hochfester Stahl KW - Riss KW - Forschung PY - 2023 AN - OPUS4-57517 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Eigenspannungen in mittels DED-Arc gefertigten Bauteilen aus hochfestem Stahl N2 - Der Vortrag gibt einen Überblick über die mittels XRD und Neutronenbeugung ermittelten Eigenspannungen in additiv gefertigten Bauteilen. Zusätzlich wird der Einfluss der Prozessparameter auf die Härte betrachtet. T2 - Frühjahrssitzung des Fachausschusses 13 Eigenspannungen der AWT CY - Berlin, Germany DA - 28.03.2023 KW - Eigenspannungen KW - DED-arc KW - Hochfester Stahl KW - Neutronenbeugung PY - 2023 AN - OPUS4-57289 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Hot Cracking Behavior of LTT Alloys under Variable Conditions in the Varestraint Test N2 - The use of Low Transformation Temperature (LTT) filler materials is an innovative way to reduce welding residual stresses. The generation of compressive residual stresses in the weld and heat-affected zone can lead to an improvement of the fatigue life of high-strength welds. However, high-alloy filler metals can be prone to solidification cracking. Two important LTT alloys were evaluated under variable welding and loading parameters using the Modified Varestraint/Transvarestraint (MVT) test. Initially conflicting results were interpreted using a newly developed image-based crack detection routine [1]. Based on the melt pool dimensions, the shape of the isotherms is reconstructed, and the theoretical crack growth along numerically determined crystallization paths is considered in relation to the cracks observed. Decreasing welding speeds with simultaneously higher heat input promote crack formation with increasing strain rate. T2 - International Joint Conference EMPOrIA 2023 CY - Aachen, Germany DA - 16.05.2023 KW - LTT KW - Solidification cracking KW - Varestraint test PY - 2023 AN - OPUS4-57546 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Kromm, Arne A1 - Mente, Tobias A1 - Czeskleba, Denis A1 - Brackrock, Daniel A1 - Kannengießer, Thomas T1 - Bauteilversuch zur Bewertung der wasserstoffunterstützten Rissanfälligkeit geschweißter, dickwandiger Offshore-Gründungsstrukturen N2 - Offshore-Windenergieanlagen erfordern Gründungskonzepte aus unterpulver-(UP-)geschweißten Dickblechen (bspw. der Güte S420ML). Während der Schweißfertigung kann eine zeitverzögerte wasserstoffunterstützte Kaltrissbildung auftreten, deren Bewertung aufgrund der Bauteilgröße von Offshore-Strukturen sehr komplex ist. Deswegen wurde eine bauteilähnliche Geometrie (Mock-Up) entwickelt, um reale Steifigkeitsverhältnisse auf den Labormaßstab zu übertragen. Zusätzliche Versteifungen simulieren die Wirkung einer Einspannung bzw. Schrumpfbehinderung der Schweißnaht. Über die Verwendung von Schweißpulvern mit definierter Feuchte wurden zudem ein Extremszenario der Wasserstoffaufnahme simuliert. Entsprechend der vorgegebenen Mindestwartezeit für die ZfP von bis zu 48 h wurde die Schweißnaht zerstörungsfrei mit Phased-Array-Ultraschall-Prüfung (PAUT) geprüft und die Eigenspannungen über Röntgendiffraktometrie (XRD) bestimmt. Zusätzlich wurde die Wasserstoffverteilung in der Schweißverbindung numerisch simuliert. Außer zulässigen Defekten (wie Poren), wurde keine verzögerte Kaltrissbildung in den Mock-Ups festgestellt, was auf hohe Rissbeständigkeit hindeutet. T2 - Tagung Werkstoffprüfung 2023 CY - Berlin, Germany DA - 23.11.2023 KW - Kaltrissbildung KW - Wasserstoff KW - Offshore KW - Schweißen KW - Bauteiltest PY - 2023 DO - https://doi.org/10.48447/WP-2023-219 SP - 316 EP - 321 CY - Berlin AN - OPUS4-58908 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gräbner, Maraike T1 - Process optimisation for realisation of crack-free Ni-based wear protection coatings and assessment of machinability by subsequent milling processes to produce defined surfaces N2 - Reducing CO2 emissions to 62 percent up to 2030 and achieving greenhouse neutrality up to 2050 are the key goals of the EU's climate protection legislation. The expansion of technologies for climate-neutral energy generation is not the only important contribution to reducing greenhouse gases, the efficient use of material systems is also a key factor. In the area of plant engineering, steel components are provided with a wear-protection coating for efficient use to protect them against corrosive, tribological, thermal and mechanical stresses. The wear-protection coatings are primarily made of Co alloys, which are to be replaced by alternative materials, such as nickel alloys, because of the poor working conditions regarding the extraction of the cobalt and because of the health risks. In terms of corrosion behavior, many applications require a crack-free wear protection layer and additional machining. Machining by milling is not economical for wear materials, especially for SME because of the high tool wear, but it is essential to produce defined surfaces with high quality. Alloy modifications of the filler metals for nickel-based plasma deposition welded wear protection coatings and the use of innovative ultrasonic-assisted milling processes are examined to determine how more favorable machinability can be achieved without reducing the wear protection potential. The focus is on the NiCrSiFeB alloy, which is intended to replace CoCr alloys in the area of screw machines. The modification of hard facing layers in terms of microstructure and precipitation morphology as well as suitability for machining is investigated and compared with the CoCr alloy. In this aspect, the alloy modifications are generated by a PTA process by systematically adjusting the preheating and interpass temperatures, a crack-free wear-resistant layer can be generated, which is subsequently machined by a milling process. In addition to the crack-free properties, the microstructure, the bonding as well as the mixing between the NiCrFeB alloy and a 1.8550 as well as between the CoCr alloy and a 1.4828 are analyzed and compared in the joining areas. In addition, heating and cooling rates are determined and a chemical analysis of the weld metals is performed. This study provides important knowledge about the differences between NiCrFeB alloy and CoCr alloys in terms of microstructure morphology, bonding and mixing behavior in the joining zones to the basic material. T2 - 3rd International Conference on Advanced Joining Processes CY - Braga, Portugal DA - 19.10.2023 KW - Legierungsmodifikation KW - Auftragschweißen KW - Ultraschallunterstütztes Fräsen KW - Zerspankräfte PY - 2023 AN - OPUS4-59088 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael T1 - Bauteilversuch zur Bewertung der wasserstoffunterstützten Rissanfälligkeit geschweißter, dickwandiger Offshore Gründungsstrukturen N2 - Offshore-Windenergieanlagen erfordern Gründungskonzepte aus unterpulver-(UP-)geschweißten Dickblechen (bspw. der Güte S420ML). Während der Schweißfertigung kann eine zeitverzögerte wasserstoffunterstützte Kaltrissbildung auftreten, deren Bewertung aufgrund der Bauteilgröße von Offshore-Strukturen sehr komplex ist. Deswegen wurde eine bauteilähnliche Geometrie (Mock-Up) entwickelt, um reale Steifigkeitsverhältnisse auf den Labormaßstab zu übertragen. Zusätzliche Versteifungen simulieren die Wirkung einer Einspannung bzw. Schrumpfbehinderung der Schweißnaht. Über die Verwendung von Schweißpulvern mit definierter Feuchte wurden zudem ein Extremszenario der Wasserstoffaufnahme simuliert. Entsprechend der vorgegebenen Mindestwartezeit für die ZfP von bis zu 48 h wurde die Schweißnaht zerstörungsfrei mit Phased-Array-Ultraschall-Prüfung (PAUT) geprüft und die Eigenspannungen über Röntgendiffraktometrie (XRD) bestimmt. Zusätzlich wurde die Wasserstoffverteilung in der Schweißverbindung numerisch simuliert. Außer zulässigen Defekten (wie Poren), wurde keine verzögerte Kaltrissbildung in den Mock-Ups festgestellt, was auf hohe Rissbeständigkeit hindeutet. T2 - Tagung Werkstoffprüfung 2023 CY - Berlin, Germany DA - 23.11.2023 KW - Kaltrissbildung KW - Wasserstoff KW - Offshore KW - Bauteilversuch KW - Imperfektion PY - 2023 AN - OPUS4-58907 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Giese, Marcel T1 - Mashining of wear resistant materials by means of ultrasonic assisted milling N2 - The long-term global goals of achieving almost net zero carbon emissions in the next decades are closely linked to the development of highly efficient components in plant, process and energy engineering, and their sustainable and resource-saving production. Plant components must increasingly withstand tribological loads in addition to high thermal, mechanical, and corrosive stresses. Such combined stresses demand high-performance alloys economically tailored to the application for wear protection and components produced as semi-finished products, via additive manufacturing (AM) or claddings via deposition welding. For instance, the protection of special components made of less cost-intensive materials, e.g., steel in process engineering for screw machines or exhaust gas separation, is feasible applying cost-intensive Ni- or Co-based hard-phase claddings. Today an increasing number of above-mentioned applications demand precise finishing machining of components to ensure defined compact surfaces with a high integrity and complex contours. Contour milling is standard process for finishing machining of metals. Especially, the desired properties of wear resistant materials (e.g., high strength, hard precipitations) imply significant challenges for milling processes and tools, leading frequently to uneconomic milling conditions due to intolerable high tool wear and surface defects. Inhomogeneous, anisotropic weld structures due to cladding or AM of wear resistance alloys lead to further deteriorations of milling processes due to unstable milling conditions and process forces during chip removal. To tackle these challenges, already several approaches exist, (1) to enhance machinability of the claddings by alloy modifications to specifically influence solidification and hard phases morphology (precipitation shape, size, distribution) and (2) to achieve significant improvements of the machining situation (e.g., increase of tool life and surfaces integrity) by means of modern hybrid machining processes such as ultrasonic-assisted milling. This contribution shows a comprehensive overview of recent results with these promising approaches for additively welded Ni- CoCr-alloys. T2 - 24th International Conference on Wear of Materials CY - Banff, Alberta, Canada DA - 16.04.2023 KW - Ultrasonic assisted milling KW - Surface integrity PY - 2023 AN - OPUS4-58944 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Czeskleba, Denis T1 - Experimental determination of hydrogen diffusion in high-strength submerged arc welded joints by electrochemical permeation N2 - High-strength structural steels are increasingly used in modern steel construction for economic and design reasons, e.g., in building, plant or mobile crane construction. By using steels with higher yield strengths (≥690 MPa), significant weight reductions and lower processing costs can be achieved by reducing the wall thickness. For example, substituting S235J2 with S960QL can reduce weight by up to 78%. Current efforts in lightweight design result from the goal of reducing greenhouse gas emissions by up to 65% by 2030 compared to 1990. These demands mean a significant reduction in process emissions in industry by increasing the efficiency of energy and raw materials. Submerged arc welding (SAW) offers high deposition rates and the welding of sheet thicknesses of up to 200 mm. Due to their special microstructure to achieve strength, high strength steels have reduced ductility and are susceptible to hydrogen-assisted cold cracking (HACC), which can also form with delay. In addition, large plate thicknesses lead to high residual welding stresses and long diffusion paths for hydrogen introduced via the welding process, for example. Furthermore, H-diffusion coefficients for submerged arc multi-layer weld metal are very limited as a basis for estimating the time interval of a possible delayed cold cracking (thus HACC) or for post-heating procedures for hydrogen reduction (no HACC). Reliable H-diffusion coefficients are therefore an adequate tool for assessing the risk of delayed HACC. This study characterizes the hydrogen diffusion behavior in submerged arc multi-pass weld metal, heat-affected zone and base metal of a two different S690 steels (TM and QT condition). Samples were extracted from the weld metal, heat-affected zone and base material to investigate the microstructure-specific influence on the diffusion of hydrogen. Using electrochemical permeation at room temperature and carrier gas hot extraction in the temperature range up to 400 °C, the corresponding diffusion coefficients were determined. From the experimental data, hydrogen diffusion coefficients and absorbed hydrogen concentrations had been calculated. In contrast e.g. to GMA welds, the hydrogen diffusion coefficients did not exhibit significant differences in the two base materials (TM and QT) or the heat-affected zone or weld metal, although quite different welding heat inputs were investigated. From the practical viewpoint, thick-walled SAW joints can be assessed for delayed hydrogen diffusion only by the base material coefficients. The calculated diffusion coefficients will be further used for numerical modelling of the hydrogen diffusion in welded joints. T2 - IIW Intermediate Meeting 2025 CY - Trollhätten, Sweden DA - 10.03.2025 KW - Hydrogen Cracking KW - Submerged Arc Welding KW - Hydrogen Diffusion KW - Cold Cracking PY - 2025 AN - OPUS4-63124 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erxleben, Kjell T1 - Assessment of in-service welding conditions for pressurized hydrogen pipelines via component test N2 - Hydrogen is the energy carrier of tomorrow for a fossil-free future. This requires a reliable transport infrastructure capable of transporting large quantities of hydrogen. In addition to the construction of new pipelines, the conversion of existing natural gas (NG) networks is an essential part of global hydrogen strategies. The transport of hydrogen is fundamentally different from that of NG, as hydrogen can be absorbed into the pipeline material. Given the known effects of hydrogen embrittlement, the compatibility of the materials for the proposed pipelines (typically low alloy steels in a wide range of strengths and thicknesses) must be investigated. However, pipelines require frequent maintenance, repair, or the need to install additional outlets. In some cases, it is necessary to perform welding on or to the pipelines while they are in-service, i.e. with active gas flow under high pressure. This in-service welding poses challenges for hydrogen operations in terms of additional hydrogen absorption during welding and material compatibility. The challenge can be roughly divided into the possible austenitization of the inner pipe material exposed to hydrogen, which can lead to sufficient hydrogen absorption, and the welding itself, which causes an increased temperature range. Both lead to a significant increase in hydrogen solubility of the respective materials compared to room temperature. In this context, knowledge about welding on hydrogen pipelines is scarce due to the lack of operational experience. Fundamental experimental investigations are required to investigate the transferability from natural gas to hydrogen pipeline networks. For this reason, the present study presents a specially designed demonstrator concept for the realistic assessment of the welding process conditions. The demonstrator was designed ex-post sample extraction for quantification of the absorbed hydrogen concentration. For safety reasons, the required volume of pressurized hydrogen was limited by inserting a solid cylinder. Welding experiments on the DN50 and DN200 pressurized demonstrators showed an increased hydrogen uptake in the welded area of several ppm. T2 - Materials Week/Steel Innovation CY - Frankfurt am Main, Germany DA - 02.04.2025 KW - In-service KW - Hydrogen KW - Pipeline KW - Repair welding KW - Component test PY - 2025 AN - OPUS4-62941 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Scharf-Wildenhain, R. A1 - Engelking, Lorenz A1 - Hälsig, A. A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas A1 - Hensel, J. T1 - Effect of heat control on mechanical properties and residual stresses at the transition zone of component and substrate in hybrid DED‑arc manufacturing N2 - In hybrid additive manufacturing, components or semi-finished products manufactured by conventional primary forming are enhanced or modified by additive manufactured structures. However, systematic investigations focusing on the critical transition area between the specific properties of the substrate (like high-strength) and the additively manufactured component, made of specific filler material, are still lacking. The focus of the present study was to determine the influence of heat control on the Δt8/5 cooling time, the distortion, the mechanical properties, and the residual stresses in the transition area of hybrid-additive components. This contributed to the knowledge regarding the safe avoidance of cold cracking, excessive distortion, a reduction in yield stress, and the implementation of hybrid DED-arc manufacturing. The heat control was varied by means of heat input and working temperature such that the Δt8/5 cooling times corresponded to the recommended processing range. The heat input has a greater influence on the cooling time in the transition area than the working temperature. Working temperature and the total energy applied per layer have a significant effect on component distortion. The lowest working temperature of 100 °C in combination with the highest total energy per layer leads to significantly greater distortion compared to manufacturing with a high working temperature of 300 °C and low total energy per layer. In addition, the longitudinal residual compressive stresses in the sensitive transition area are reduced from − 500 MPa to approx. − 200 MPa by adjusting the working temperature from 100 to 300 °C. Such complex interactions must be clarified comprehensively to provide users with easily applicable processing recommendations and standard specifications for an economical hybrid additive manufacturing of components made, for example, of high-strength steels in the transition area. T2 - IIW Annual Assembly and International Conference CY - Rhodes Island, Greece DA - 07.07.2024 KW - Hybrid additive manufacturing KW - DED-arc KW - Heat control KW - High-strength metals KW - Residual stress PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-630415 DO - https://doi.org/10.1007/s40194-025-02036-z SN - 1878-6669 SP - 1 EP - 15 PB - Springer AN - OPUS4-63041 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -