TY - CONF A1 - Liepold, Philipp T1 - Crack Segmentation via Convolutional Neural Networks (CNNs) for Varestraint Type Tests N2 - The Modified Varestraint-Transvarestraint (MVT) hot cracking test is the local variant of the world wide used Varestraint type tests. In this work, a Convolutional Neural Network (CNN) was trained to segment cracks in light microscope images of welded MVT samples. The network was trained on a dataset created by the presenter of considerable size. With the help of CNNs, the evaluation of MVT test samples can be automated, reducing the influence of human error on the evaluation. T2 - MPA Stuttgart CY - Stuttgart, Germany DA - 8.10.2024 KW - CNN KW - MVT PY - 2024 AN - OPUS4-61332 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröpfer, Dirk A1 - Reichel, Levin A1 - Kannengießer, Thomas T1 - Beanspruchungsgerechte Reparatur von Schweißverbindungen bei der Fertigung von Bauteilen aus hochfesten Feinkornbaustählen N2 - Zunehmende Anlagengrößen im Bereich Windenergie erfordern hochfeste Stähle, um vorhandene Leichtbaupotenziale auszuschöpfen. An die schweißtechnische Verarbeitung dieser Stahlgüten werden hohe Anforderungen gestellt. Bei mittels zerstörungsfreier Prüfung festgestellten Fehlstellen empfehlen geltende Verarbeitungsrichtlinien lokales Ausfugen und Reparaturschweißen. Degradationen der speziellen hochfesten Gefüge und Werkstoffeigenschaften sowie hohe Schrumpfbehinderungen der umliegenden Struktur ausgefugter Bereiche erhöhen das Risiko erneuter Schweißdefekte, insbesondere durch Überlagerung von globalen und lokalen schweißbedingten Eigenspannungen nach dem Reparaturschweißen. Fehlende Informationen über geeignete Reparaturkonzepte in den Regelwerken können dazu führen, dass reparaturbedingte Beanspruchungen unzureichend berücksichtigt werden. Das FOSTA-Vorhaben P1311 (IGF20162N) fokussiert das Reparaturschweißen zweier hochfester Stähle: S500MLO für Offshore-Anwendungen und S960QL für Errichterstrukturen, z. B. Mobilkräne. Simulationen von Einspannbedingungen und Bauteilanalysen sowie Versuche mit anwendungs- bzw. realitätsnahen Bauteilstrukturen ließen sich auftretende schweißbedingte Beanspruchungen mittels Röntgendiffraktometrie (XRD), Härtemessungen und metallografischer Untersuchungen ermitteln. In diesem Beitrag steht die Interaktion aus Wärmeführung und konstruktiver Steifigkeit als Einfluss auf die entstehenden Beanspruchungen bei einfacher und mehrfacher Reparatur im Vordergrund. Die Ergebnisse zeigen, dass sich risskritische Eigenspannungen durch adaptierte Wärmeführungskonzepte vermeiden lassen, und dass dies eine Grundlage für Verarbeitungsempfehlungen und für normative Vorgaben ist. Dies kann insbesondere kleine und mittelständischen Unternehmen bei einer wirtschaftlichen, beanspruchungsgerechten Reparatur hochfester geschweißter Bauteilen unterstützen. T2 - DVS Innovationstage 2024 CY - Düsseldorf, Germany DA - 10.04.2024 KW - Mod. Sprühlichtbogen KW - Reparaturschweißen KW - Thermisches Ausfugen KW - Offshore KW - P1311 PY - 2024 SP - 120 EP - 126 AN - OPUS4-61931 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wandtke, Karsten A1 - Engelking, Lorenz A1 - Schröpfer, Dirk A1 - Scharf-Wildenhain, Ronny A1 - Hälsig, Andre A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Fertigungsbedingte Beanspruchungen und Kaltrisssicherheit in generativ gefertigten Bauteilen aus hochfesten Feinkornbaustählen N2 - Additive Fertigungsverfahren wie das Direct Energy Deposition-Arc (DED-Arc) oder Wire Arc Additive Manufacturing (WAAM) ermöglichen die effiziente Herstellung gewichtsoptimierter, endkonturnaher Bauteile im modernen Stahlbau. Steigerungen der Effizienz können durch den Einsatz hochfester Stähle erreicht werden, insbesondere durch Verringerung von Wandstärken und Bauteilgewicht sowie signifikante Einsparung von Kosten, Zeit und Ressourcen. DED-Arc Schweißzusatzwerkstoffe sind bereits auf dem Markt verfügbar, allerdings fehlen Richtlinien und quantitative Kenntnisse über die schweißbedingte Beanspruchung während der Fertigung und im Betrieb, welche den industriellen Einsatz stark limitieren. In einem gemeinsamen Projekt der BAM und der Technischen Universität Chemnitz wurden die wesentlichen Einflüsse und komplexen Wechselwirkungen von Werkstoff, Fertigungsverfahren, Konstruktion und Bearbeitungsschritten auf die Eigenspannungen untersucht. Ziel war es, den stahlverarbeitenden Anwendern, insbesondere KMU, eine risssichere und beanspruchungsgerechte Herstellung und Modifizierung von Bauteilen und Halbzeugen aus hochfesten Feinkornbaustahl unter Verwendung MSG-basierter generativer Verfahren zu ermöglichen. T2 - DVS Innovationstage 2024 CY - Düsseldorf, Germany DA - 10.04.2024 KW - Wire Arc Additive Manufacturing (WAAM) KW - Feinkornbaustähle KW - Additive Fertigung KW - Kaltrisssicherheit KW - Direct Energy Deposition-Arc (DED-Arc) PY - 2024 SP - 96 EP - 104 AN - OPUS4-61932 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröpfer, Dirk A1 - Reichel, Levin A1 - Kannengießer, Thomas T1 - Beanspruchungsgerechte Reparatur von Schweiß-Verbindungen bei der Fertigung von Bauteilen aus hochfesten Feinkornbaustählen (FOSTA P1311, IGF 20162 N) N2 - Zunehmende Anlagengrößen im Bereich Windenergie erfordern hochfeste Stähle, um vorhandene Leichtbaupotenziale auszuschöpfen. An die schweißtechnische Verarbeitung dieser Stahlgüten werden hohe Anforderungen gestellt. Bei mittels zerstörungsfreier Prüfung festgestellten Fehlstellen empfehlen geltende Verarbeitungsrichtlinien lokales Ausfugen und Reparaturschweißen. Degradationen der speziellen hochfesten Gefüge und Werkstoffeigenschaften sowie hohe Schrumpfbehinderungen der umliegenden Struktur ausgefugter Bereiche erhöhen das Risiko erneuter Schweißdefekte, insbesondere durch Überlagerung von globalen und lokalen schweißbedingten Eigenspannungen nach dem Reparaturschweißen. Fehlende Informationen über geeignete Reparaturkonzepte in den Regelwerken können dazu führen, dass reparaturbedingte Beanspruchungen unzureichend berücksichtigt werden. Das FOSTA-Vorhaben P1311 (IGF20162N) fokussiert das Reparaturschweißen zweier hochfester Stähle: S500MLO für Offshore- Anwendungen und S960QL für Errichterstrukturen, z. B. Mobilkräne. Simulationen von Einspannbedingungen und Bauteilanalysen sowie Versuche mit anwendungs- bzw. realitätsnahen Bauteilstrukturen ließen sich auftretende schweißbedingte Beanspruchungen mittels Röntgendiffraktometrie (XRD), Härtemessungen und metallografischer Untersuchungen ermitteln. In diesem Beitrag steht die Interaktion aus Wärmeführung und konstruktiver Steifigkeit als Einfluss auf die entstehenden Beanspruchungen bei einfacher und mehrfacher Reparatur im Vordergrund. Die Ergebnisse zeigen, dass sich risskritische Eigenspannungen durch adaptierte Wärmeführungskonzepte vermeiden lassen, und dass dies eine Grundlage für Verarbeitungsempfehlungen und für normative Vorgaben ist. Dies kann insbesondere kleine und mittelständischen Unternehmen bei einer wirtschaftlichen, beanspruchungsgerechten Reparatur hochfester geschweißter Bauteilen unterstützen. T2 - DVS Innovationstage 2024 CY - Düsseldorf, Germany DA - 10.04.2024 KW - Reparaturschweißen KW - Thermisches Ausfugen KW - Sprühlichtbogen KW - Offshore PY - 2024 AN - OPUS4-61933 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Giese, Marcel T1 - Defined surfaces via ultrasonic assisted machining of modified wear protection coating alloys N2 - The development of technologies for climate-neutral energy generation is an important contribution to reducing CO2 emissions, whereby the efficient use of material systems is a key factor. Wear-resistant coatings are required for highly efficient and economical steel components in energy, process and power plant engineering in order to withstand the high corrosive, tribological, thermal and mechanical loads. Considering price and supply risks as well as the increasing demands on corrosive resistance at high temperatures, conventional cobalt alloys are to be replaced by nickel alloys. In addition, there is a growing demand for defined surfaces of high quality or functional surfaces of these protective coatings. The milling required for this is often not economically feasible, especially for SMEs, due to high tool wear. A joint project of BAM and ISAF of TU Clausthal (Fosta P1550/IGF 21959 N) investigates the optimization of these challenging machining conditions by means of alloy modifications of the welding powder for plasma transferred arc cladding, without reducing the wear protection potential and using innovative ultrasonic assisted milling process for better machinability without reducing wear resistance. This article presents the results of investigations into the relationships between different alloy modifications (Ti, Al, Nb Mo and Hf with wX ≤ 0.01), the resulting microstructure and precipitation morphology, the machinability and the wear protection properties using a NiCrMoSiFeB alloy (trade name: Colmonoy 56 PTA). Tests using cast samples have already shown that the addition of Nb leads to a finer distribution of the hard phases and that this results in a reduction in cutting forces and tool wear during ultrasonic-assisted milling. The change in the microstructure morphology through the addition of Al, on the other hand, causes a significant increase in the cutting forces that occur. T2 - IIW Annual Assembly CY - Rhodos, Griechenland DA - 07.07.2024 KW - Ultrasonic assisted milling KW - Surface integrity PY - 2024 AN - OPUS4-61926 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael T1 - Evaluation of the wear protection of modified NiMoCrSi alloy and machinability using ultrasonic-assisted milling N2 - The development of technologies for climate-neutral energy generation is an important contribution to reducing CO2 emissions, whereby the efficient use of material systems is a key factor. Wear-resistant coatings are required for highly efficient and economical steel components in energy, process and power plant engineering in order to withstand the high corrosive, tribological, thermal and mechanical loads. Considering price and supply risks as well as the increasing demands on corrosive resistance at high temperatures, conventional cobalt alloys are to be replaced by nickel alloys. In addition, there is a growing demand for defined surfaces of high quality or functional surfaces of these protective coatings. The milling required for this is often not economically feasible, especially for SMEs, due to high tool wear. A joint project of BAM and ISAF of TU Clausthal (Fosta P1550/IGF 21959 N) investigates the optimization of these challenging machining conditions by means of alloy modifications of the welding powder for plasma transferred arc cladding, without reducing the wear protection potential and using innovative ultrasonic assisted milling process for better machinability without reducing wear resistance. This article presents the results of investigations into the relationships between different alloy modifications (Ti, Al, Nb Mo and Hf with wX ≤ 0.01), the resulting microstructure and precipitation morphology, the machinability and the wear protection properties using a NiCrMoSiFeB alloy (trade name: Colmonoy 56 PTA). Tests using cast samples have already shown that the addition of Nb leads to a finer distribution of the hard phases and that this results in a reduction in cutting forces and tool wear during ultrasonic-assisted milling. The change in the microstructure morphology through the addition of Al, on the other hand, causes a significant increase in the cutting forces that occur. T2 - IIW Intermediate meeting of Commission II-A CY - Online meeting DA - 12.03.2024 KW - Ultrasonic assisted milling KW - Surface integrity PY - 2024 AN - OPUS4-61924 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin T1 - Effects of weld seam design on the fatigue strength of welded components with LTT welding filler N2 - Low Transformation Temperature (LTT) welding fillers offer an innovative approach to increase the compressive residual stresses in weld seams which have a positive impact on the fatigue strength of welded structures. LTT welding fillers exhibit a martensitic phase transformation close to ambient temperature which generates compressive residual stresses through a volume expansion in the weld seam and the heat affected zone (HAZ). This article focuses on the punctually placement of additional LTT layers to generate compressive residual stresses in fatigue-critical areas of conventional weld joints. This enables an economical solution without effecting the integrity of welded joints. For this, longitudinal stiffeners made of high-strength steel were gas metal arc welded using conventional welding consumable in the first layer. Afterwards, a chromium-nickel alloyed LTT welding consumable was applied on front sides of the stiffeners. By varying the welding parameters, three different weld geometries of the LTT weld bead could be realized. The effects of additional LTT layers were investigated with regards to dilution, residual stresses, and fatigue strength. The dilution does not exhibit much difference regards to the chemical composition. Therefore, it can be assumed that all three variants have a similar martensite start temperature. X-ray residual stresses measurements show that the residual stresses at the critical weld toe are significantly reduced by using LTT welding filler. While the conventional weld is characterized by tensile residual stresses, compressive residual stresses can be detected at the LTT weld. The level of residual stresses is influenced by the geometry of the LTT layer. LTT layers with a high offset to the conventional weld generate more compressive residual stresses in the HAZ than with a low offset. Therefore, the weld geometry has a considerable impact on the residual stress profile. The fatigue testing results shows that the LTT layers in all three variants has a positive impact to the fatigue strength. T2 - MPA Seminar Stuttgart 2024 CY - Stuttgart, Germany DA - 08.10.2024 KW - LTT (Low Transformation Temperature) KW - Fatigue strength KW - Weld geometry KW - Residual stress PY - 2024 AN - OPUS4-61615 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröpfer, Dirk T1 - Evaluation of the wear protection of modified Nimocrsi alloy and machinability using ultrasonic-assisted milling N2 - The targets for reducing CO2 emissions are closely linked to the development of highly efficient and economical steel components in plant, process and power plant technology, which require wear protection coatings tailored to the application and steel material for high combined corrosive, tribological, thermal and mechanical stresses. There is a growing demand in industry for defined functional surfaces of high quality for these coatings. Milling is a standard process for finish machining. The desired properties of wear resistant alloys imply significant challenges for the milling process due to high tool wear and surface defects. Besides the hardness of the coating materials, especially due to the precipitations, inhomogeneous, anisotropic weld structures of the claddings lead to further deteriorations of milling processes due to unstable milling conditions and process forces. A joint project of BAM and ISAF of TU Clausthal (Fosta P1550/IGF 21959 N) investigates the optimization of these challenging machining conditions by means of alloy modifications of the welding powder for plasma transferred arc cladding, without reducing the wear protection potential and using ultrasonic assisted milling process. T2 - 6th European Symposium on Friction, Wear and Wear Protection CY - Oberhof, Germany DA - 26.02.2024 KW - Ultrasonic assisted milling KW - Surface integrity PY - 2024 AN - OPUS4-61927 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wandtke, Karsten T1 - Einfluss Spanender Bearbeitungsschritte auf die Eigenspannungen in additiv gefertigten Bauteilen aus hochfestem Stahl N2 - Der Vortrag gibt einen Überblick über den Einfluss der Prozessparameter auf die Eigenspannungen sowie die Härte in additiv gefertigten Bauteilen aus hochfestem stahl. Des Weiteren wird dargestellt, wie sich das Bauteildesign und trennende Fertigungsschritte auf die Eigenspannungen der Bauteile auswirken. T2 - Fachausschuss für Eigenspannungen AWT CY - Wolfsburg, Germany DA - 20.03.2024 KW - Hochfester Stahl KW - Additive Fertigung KW - Eigenspannungen PY - 2024 AN - OPUS4-61624 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Engelking, Lorenz T1 - Bericht zum Fortschritt des laufenden Projekts: „Herstellung beanspruchungsgerechter Oberflächen durch Kombination innovativer additiver und abtragender Fertigungsschritte an hochbelasteten Komponenten“ N2 - Das DVS-Vorhaben 01.3211 „Herstellung beanspruchungsgerechter Oberflächen durch Kombination innovativer additiver und abtragender Fertigungsschritte an hochbelasteten Komponenten“ ist ein Kooperationsprojekt der Bundesanstalt für Materialforschung und -prüfung (BAM) und dem Institut für Schweißtechnik und Trennende Fertigungsverfahren (ISAF) der Technischen Universität Clausthal. Das Übergeordnete Projektziel ist das Erlangen von Erkenntnissen für eine sichere und wirtschaftliche, kombinierte additive und abtragende Fertigung aus kostenintensiven Werkstoffen hochbelasteter Komponenten insbesondere für KMU. Dabei stehe die beiden Werkstoffe CoCr26Ni9Mo5W (2.4681) und FeNi36 (1.3912) im Fokus. Mittels Modifikation der Schweißzusätze sind homogen und isotrop ausgeprägte Werkstoffeigenschaften und eine Erhöhung der Prozessstabilität und Fertigungsfreiheitsgrade bei der additiven Fertigung erzielbar. Darüber hinaus wird der Einfluss nachfolgender abtragender Bearbeitungsschritte des ultraschallunterstützen und des konventionellen Fräsprozesses untersucht. Die mit dem Forschungsvorhaben verbundenen Nutzen für KMU sind die Stärkung der Innovationsfähigkeit und der Wirtschaftlichkeit sowie die Erhöhung der Wettbewerbsfähigkeit. In AP-1 wurden Zerspanversuche am FeNi- und CoCr-Ausgangswerkstoff durchgeführt. Ziel der Versuche war in erster Linie die Identifikation geeigneter Fräswerkzeuge und -parameter. In AP-2 wurden die Legierungsmodifikationen des CoCr-Ausgangswerkstoffes durchgeführt und die Mikrostruktur sowie die Härte analysiert. In AP-4 wurden erste Zerspanversuche in Abhängigkeit der Legierungsmodifikation der CoCr-Legierung durchgeführt. T2 - Sitzung des Fachausschusses 01 „Schweißmetallurgie und Werkstoffverhalten“ des DVS CY - Online meeting DA - 26.10.2021 KW - Fortschrittsbericht KW - DVS KW - Ultraschallunterstütztes Fräsen KW - Additive Fertigung PY - 2021 AN - OPUS4-53636 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -