TY - CONF A1 - Schönherr, J. A. T1 - Robust Determination of Fatigue Crack Propagation Thresholds from Crack Growth Data N2 - To assess the ability of cracks to grow, a robust determination of the threshold against fatigue crack propagation ∆Kth is of paramount importance. The standards ASTM E647 and ISO 12108 introduce operational definitions of ∆Kth based on the crack propagation rate da/dN. For evaluating ∆Kth, both suggest fitting a linear function to a defined subset of the logarithmic ∆K – da/dN test data, where ∆Kth follows by evaluating the linear function at da/dN = 10-7 mm/cycle and da/dN = 10-8 mm/cycle, respectively. In general, this kind of fit suffers from a bad representation of the actual curvature of the crack propagation curve. Therefore, we propose a robust method for evaluating ∆Kth using a non-linear function that reduces the artificial conservativeness induced by the evaluation method as well as the susceptibility to scatter in test data and the influence of test data density. The method is calibrated against a large set of S690QL crack growth data obtained from a total of 48 specimens, and validated against a set of S355NL and S960QL data (3 specimens each), obtained as a part the IBESS (integral fracture mechanics determination of the fatigue strength of welds) project. T2 - ECF23 (European Conference on Fracture 2022) CY - Madeira, Portugal DA - 27.06.2022 KW - Fatigue crack propagation threshold KW - ISO 12108 KW - ASTM E647 KW - Data evaluation methods KW - Experimental determination PY - 2022 AN - OPUS4-55252 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zhu, Jiangchao T1 - Bruchmechanische Bewertung der Integrität einer Turbinenscheibe bei Überdrehzahl N2 - Turbinenscheiben sind thermisch und mechanisch hochbeanspruchte, sicherheitsrelevante Komponenten in Gasturbinen. Ihre Integrität wird in Bauteiltests unter Überdrehzahlbedingungen nachgewiesen. Kontext des Aufsatzes ist die Erarbeitung einer zusätzlichen Bewertungsebene auf der Grundlage von Versuchen unter monotoner Beanspruchung, die die Beanspruchung im Bauteil realistisch wiedergeben soll. Betrachtet wird ein halbelliptischer Riss, der bei der weiteren Ausbreitung als Umfangsriss wächst (rim peeling). Die Simulation dieser Stelle im Bauteil schließt die mechanische und thermische Beanspruchung sowie sie Dehnungsbehinderung ein. Letztere wird anhand zweier Parameter, der Spannungsmehrachsigkeit ℎ und des (allerdings modifizierten) Constraint-Parameters nach Newman, der die Spannungen über den plastisch verformten Bereich mittelt, bestimmt. Erwartungsgemäß zeigt sich, dass die höchste Dehnungsbehinderung weder an den Oberflächenpunkten, noch an den tiefsten Punkten, sondern an einer Stelle zwischen beiden auf der Rissfront auftritt. Als Versuchsgeometrie für die monotonen Tests soll eine Kreuzprobe mit wanddurchdringenden Rissen ausgehend von einer Innenbohrung dienen. Durch geeignete Wahl der Risstiefe sowie der in beiden Richtungen angreifenden Kräfte gelingt es, bauteiladäquate Zustände zu erzeugen. T2 - 54. Tagung des Arbeitskreis Bruchmechanik und Bauteilsicherheit CY - Online meeting DA - 22.02.2022 KW - Struktur Integrität KW - Turbinenscheibe KW - Constraint KW - Bruchmechanik PY - 2022 AN - OPUS4-54402 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pfretzschner, Beate A1 - Schaupp, Thomas A1 - Hannemann, Andreas A1 - Schultz, Michael A1 - Griesche, Axel T1 - On the Genesis of Artifacts in Neutron Transmission Imaging of Hydrogenous Steel Specimens N2 - Hydrogen-charged supermartensitic steel samples were used to systematically investigate imaging artifacts in neutron radiography. Cadmium stencils were placed around the samples to shield the scintillator from excessive neutron radiation and to investigate the influence of the backlight effect. The contribution of scattered neutrons to the total detected intensity was investigated by additionally varying the sample-detector distance and applying a functional correlation between distance and intensity. Furthermore, the influence of the surface roughness on the edge effect due to refraction was investigated. KW - Refraction KW - Neutron imaging KW - Hydrogen KW - Supermartensitic steel KW - Backlight KW - Scattering PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-506587 DO - https://doi.org/10.3390/jimaging6040022 VL - 6 IS - 22 SP - 1 EP - 10 PB - MDPI CY - Basel, Switzerland AN - OPUS4-50658 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Vecchiato, Luca T1 - Fatigue limit estimation of welded joints under constant amplitude uniaxial loading adopting the cyclic R-curve analysis N2 - Most of the in-service failures of welded structures are due to fatigue damage occurring in the joints. Damage tolerant approaches based on the principles of Fracture Mechanics have been shown to play a key role in this framework, as the fatigue limit is defined by the non-propagating condition of multiple defects at the weld toe. The fatigue limit assessment can be performed using the cyclic R-curve analysis which consists in comparing the driving force of a crack propagating into a component, which depends on the geometry, material and external loads, with its resistance curve, i.e. the cyclic R-curve. The crack propagation occurs whenever the crack driving force is higher than the resistance to fatigue crack propagation, while the crack is arrested in the opposite case. Consequently, this suggests that the fatigue limit of a component is defined as that stress level at which the crack driving force curve is tangent to the crack resistance curve. In the present work, the cyclic R-curve analysis has been adopted for determining the fatigue limit of stress-relieved transverse non-load-carrying joints made of S355 structural steel and subjected to fatigue axial loadings. Experimental tests have been performed to evaluate the fatigue limit of the joints. The driving force, identified by the applied Stress Intensity Factor (SIF), has been evaluated by means of linear elastic finite element analysis taking advantage of the Peak Stress Method for its rapid estimation. Based on the experimental observations that the crack initiation and early crack growth phases in welded joints occur within the Heat Affected Zone (HAZ) the cyclic R-curve has been experimentally derived for both the base metal and HAZ material. T2 - European Conference on Fracture 2022 (ECF23) CY - Funchal, Portugal DA - 27.06.2022 KW - Welded Joints KW - Fatigue Limit KW - Cyclic R-curve PY - 2022 AN - OPUS4-55254 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Madia, Mauro T1 - Fraucture mechanics-based probablistic structural integrity assessment for aero-engine turbine disk N2 - Aero-engine turbine disks are safety-relevant components which are operated under high thermal and mechanical stress conditions. The aim of this work is to present part of a fracture mechanics-based probabilistic assessment procedure under development which aims at calculating the critical rotational speed of the turbine disk based on the numerical-analytical solutions and regulations for the failure probability. In particular, the rim-peeling failure mode is considered as case study. A semi-circular surface crack is modelled at the most stressed region at the diaphragm of a turbine disk. In order to design a lab representative specimen, beside the crack driving force, expressed in terms of J-integral, also the constraint to plastic deformation e.g., stress triaxiality, at the crack-tip must be similar for the same crack in the specimen and in the disk. The analytical solutions to calculate the crack driving force for the lab representative specimen are used for the Monte Carlo simulations, the result of which has been assessed in the form of a Failure Assessment Diagram (FAD). The results of the probabilistic structural integrity assessment show good agreement between Monte Carlo simulations and certification values for the disk in terms of expected failure mode and value of the critical speed. T2 - ICF15 - International Conference on Fracture CY - Atlanta, GA, USA DA - 12.06.2023 KW - Fracture Mechanics KW - Failure Assessment Diagram KW - Finite Element Analysis KW - Component Assessment PY - 2023 AN - OPUS4-57727 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Madia, Mauro T1 - Probabilistic structural integrity assessment of welded joints N2 - The fatigue assessment of welded joints requires several input data, which can be subdivided into three categories: geometry, material and loading. The number of input data depends essentially on the complexity of the models employed and on the level of accuracy of the analysis. It is common practice to use safety factors in design to account for the scatter of the input parameters. Nevertheless, overly-conservative factors lead often to unrealistic estimations of fatigue life. This work presents a fracture mechanics-based model for the structural integrity assessment of welded joints under constant amplitude fatigue loading, in which the local geometry at the weld toe and the fatigue crack growth properties are considered statistically distributed. The approach is validated against a large number of experimental data. T2 - ICF15 - International Conference on Fracture CY - Atlanta, GA, USA DA - 12.06.2023 KW - Fatigue KW - Fracture Mechanics KW - Weldments KW - Short crack KW - Probabilistic Assessment PY - 2023 AN - OPUS4-57726 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Madia, Mauro T1 - Progress in the determination of the fatigue propagation resistance in metals and its application to fatigue assessment N2 - This plenary lecture aims at showing the progress in the experimental determination of the fatigue propagation resistance in metals and its application to fatigue assessment. In particular, different new experimental techniques are introduced, which allow a better description of the crack propagation resistance from short to long crack regime. These data can be then applied in the fatigue assessment to predict the fatigue limit and the total life of metallic components. T2 - 5th Iberian Conference on Structural Integrity CY - Coimbra, Portugal DA - 30.03.2022 KW - Crack propagation resistance KW - Cyclic R-Curve KW - Fatigue assessment KW - Kitagawa-Takahashi diagram KW - S-N diagram PY - 2022 AN - OPUS4-54603 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Teske, Tanita T1 - Untersuchung des Potentials des Kaltgasspritzens für die Reparatur zyklisch belasteter Bauteile N2 - Das Kaltgasspritzen als Reparaturverfahren bietet die Möglichkeit den teuren Austausch beschädigter Bauteile in der Luft- und Raumfahrt zu vermeiden. In dieser Arbeit wurden das Potential an der Aluminiumlegierung AL6061-T6, unter Verwendung von Stickstoff als Prozessgas, untersucht. Mit Fokus auf das In-situ Kugelstrahlen, zur Verbesserung der mechanischen Eigenschaften, wurden quasi-statische Zugversuche und einachsige Zeitfestigkeitsversuche durchgeführt. Im Ergebnis zeigte sich die Verbesserung der Adhäsion zwischen Grundwerkstoff und aufgebrachten Material als entscheidendes Kriterium für eine erfolgreiche Anwendung. Zur Verbesserung der Adhäsion wurden die Substratoberflächen laserstrukturiert und der Einfluss mit Adhäsionsversuchen überprüft. T2 - 9. Tagung des DVM-Arbeitskreises Additiv gefertigte Bauteile und Strukturen CY - Stuttgart, Germany DA - 06.11.2024 KW - Kaltgasspritzen KW - Reparatur KW - Ermüdungsfestigkeit KW - Laserstrukturierung KW - Luft- und Raumfahrt PY - 2024 AN - OPUS4-63179 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kruse, Julius T1 - Anwendung der IBESS-Prozedur zur Berechnung der Schwingfestigkeit geschweißter bauteilähnlicher Proben mit künstlichen Defekten N2 - Im Rahmen eines Kooperationsprojekts mit der Schottel GmbH wurde eine bauteilnahe Probengeometrie entwickelt, mit der sich unter Verwendung einer einachsigen Prüfmaschine das Spannungstiefenprofil in dem unter überlagerter Biege- und Zugspannung beanspruchtem Querschnitt im Schweißnahtübergang des Bauteils reproduzieren ließ. Proben dieser Geometrie wurden vom Kooperationspartner im geschweißten bzw. geschweißten und spannungsarmgeglühten Zustand bereitgestellt. An der BAM wurden je Wärmebehandlungszustand mittels Senkerodieren zwei verschiedene künstliche Defektgeometrien im Schweißnahtübergang eingebracht. Anhand der Proben wurden experimentell für alle vier Probenzustände Wöhlerlinien für ein Spannungsverhältnis von R = 0,1 ermittelt. Zusätzlich wurde das u.a. an der BAM entwickelte IBESS-Verfahren angewandt, um die Wöhlerlinien analytisch zu bestimmen. Hierbei wurde eine sehr gute Übereinstimmung von Berechnung und Experiment erreicht, wobei die Berechnung zu einer leicht konservativen Lebensdauervorhersage führte. T2 - 56. DVM Tagung "Bruchmechanik und Bauteilsicherheit" CY - Kassel, Germany DA - 20.02.2024 KW - Bruchmechanik KW - Ermüdung KW - Schwingfestigkeit KW - Schweißverbindungen PY - 2024 AN - OPUS4-59781 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Scacco, F. A1 - Zerbst, Uwe A1 - Meneghetti, G. A1 - Madia, Mauro T1 - Comparison between PSM and IBESS approaches for the fatigue life estimation of weldments N2 - In the framework of the fatigue assessment of welded components, several methods are available in design standards such as the nominal stress, hot-spot stress, notch stress and linear elastic fracture mechanics approaches. The present paper aims at comparing two advanced local approaches for the fatigue strength assessment of different welded joints made of steel. The first one is IBESS which is based on short crack fracture mechanics. The second one is the PSM which instead involves the strain energy density approach. Both methods will be briefly presented, and the fatigue life prediction results discussed. The results obtained for the joint geometries considered in this work show advantages and drawbacks of the approaches, which are thoroughly analysed as well. KW - Fatigue KW - Welded joints KW - FAT class KW - IBESS KW - Peak stress method (PSM) KW - Finite element (FE) PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-545139 DO - https://doi.org/10.1007/s40194-022-01284-7 SP - 1 EP - 23 PB - Springer AN - OPUS4-54513 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Madia, Mauro A1 - Zerbst, Uwe A1 - Werner, Tiago T1 - Estimation of the Kitagawa-Takahashi diagram by cyclic R curve analysis N2 - The Kitagawa-Takahashi (KT) diagram is a proven concept for describing the fatigue limit in presence of a defect or crack. It can be determined empirically with great experimental effort. It can also be estimated by means of the El Haddad relationship if the endurance limit and the long fatigue crack propagation threshold are available in reasonable accuracy. A third option is the determination using the cyclic R-curve, which describes the dependency of the fatigue crack propagation threshold on the crack growth at the short crack propagation stage. This can be experimentally determined using a closure-free initial pre-crack. It can then be applied to the determination of crack arrest for a given applied load and a given defect or crack size. Compared to the other two methods mentioned above, this option has considerable advantages: It can be applied to any component and any stress ratio. It allows the treatment of multiple cracks and provides estimations of the S-N curve in the finite life regime as well as at the endurance limit. Compared to the empirical determination of the KT diagram, the experimental effort is significantly lower and compared to the El Haddad approach it avoids problems such as the use of non-conservative long fatigue crack propagation thresholds (when the conventional load reduction method is applied to materials prone to corrosion) and the mathematical predetermination of the curve shape. The work introduces the method and provides a critical discussion as well as quantitative comparison between the different methods. T2 - FATIGUE DESIGN 2021 CY - Online meeting DA - 17.11.2021 KW - Fatigue life KW - Endurance limit KW - Kitagawa-Takahashi diagram KW - Cyclic R-curve PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-544931 DO - https://doi.org/10.1016/j.prostr.2022.03.032 SN - 2452-3216 VL - 38 SP - 309 EP - 316 PB - Elsevier B.V. AN - OPUS4-54493 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schönherr, J. A. A1 - Duarte, Larissa A1 - Madia, Mauro A1 - Zerbst, Uwe A1 - Geilen, M. B. A1 - Klein, M. A1 - Oechsner, M. T1 - Robust determination of fatigue crack propagation thresholds from crack growth data N2 - The robust determination of the threshold against fatigue crack propagation DKth is of paramount importance in fracture mechanics based fatigue assessment procedures. The standards ASTM E647 and ISO 12108 introduce operational definitions of DKth based on the crack propagation rate da/dN and suggest linear fits of logarithmic DK– da/dN test data to calculate DKth. Since these fits typically suffer from a poor representation of the actual curvature of the crack propagation curve, a method for evaluating DKth using a nonlinear function is proposed. It is shown that the proposed method reduces the artificial conservativeness induced by the evaluation method as well as the susceptibility to scatter in test data and the influence of test data density. KW - Fatigue crack propagation threshold KW - ISO 12108 KW - ASTM E647 KW - Data evaluation methods KW - Experimental determination PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-552153 DO - https://doi.org/10.3390/ma15144737 SN - 1996-1944 VL - 15 IS - 14 SP - 1 EP - 21 PB - MDPI CY - Basel AN - OPUS4-55215 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Duarte, Larissa T1 - Analytische Prozedur zur Berechnung der Ermüdungslebensdauer basierend auf effektiven Rissfortschrittsdaten und zyklischer R-Kurve N2 - Bruchmechanik-basierende Methoden können für die Ermüdungsbewertung von mechanischen Bauteilen angewendet werden, die Defekte oder Risse enthalten und zyklischen Belastungen ausgesetzt sind. Die Kenntnis des Risswachstumsverhaltens für kurze und lange Risse ermöglicht die Bestimmung sowohl endlicher als auch unendlicher Lebensdauer. Ein erstes Problem ergibt sich jedoch aus der empirischen Bestimmung von Ermüdungswerkstoffkennwerten, die je nach Prüfbedingungen, z. B. Prüfmethode, Frequenz und Spannungsverhältnis R, variieren. Dies ist auf die Rissschließeffekte und weitere Umgebungsphänomene zurückzuführen, die das Rissfortschrittsverhalten beeinflussen. Ein zweites Problem ist das Fehlen von Standardversuchsverfahren zur Bestimmung des Schwellenwerts gegen Ermüdungsrissausbreitung ΔKth in Abhängigkeit von der Rissausbreitung. Dies ist problematisch, da ΔKth mit der Zunahme der Rissschließeffekte im Kurzrissbereich zunimmt und seine ungenaue experimentelle Bestimmung zu großen Abweichungen bei der Bewertung und, was noch kritischer ist, zu nicht konservativen Vorhersagen führt. Mit dem Ziel, zuverlässigere und sicherere Bewertungsverfahren bereitzustellen, wird in dieser Arbeit eine Methode vorgeschlagen, die auf effektiven Risswachstumsdaten basiert, die bei hohen Spannungsverhältnissen (R ≈ 0,8) ermittelt wurden. Zur Beschreibung der Entwicklung der Rissschließeffekte wird ein Kurzrissmodell auf der Grundlage von zyklischen R-Kurven und CPLR-Daten verwendet. Die analytischen Vorhersagen werden mit experimentellen Daten verglichen, die zur Validierung des Verfahrens durchgeführt wurden, und die daraus entstandenen Unterschiede werden diskutiert. Übersetzt mit DeepL.com (kostenlose Version) T2 - BMDK-Seminar SS24 CY - Magdeburg, Germany DA - 10.04.2024 KW - Schwellenwert gegen Ermüdungsrissausbreitung KW - Rissschließeffekte KW - Ermüdungslebensdauer KW - Zyklische R-Kurve PY - 2024 AN - OPUS4-59876 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Duarte, Larissa A1 - Madia, Mauro A1 - Zerbst, Uwe T1 - The effect of the environmental conditions on the threshold against fatigue crack propagation N2 - The threshold against fatigue crack propagation (ΔKth) is a crucial parameter for the damage tolerance assessment of engineering components subjected to cyclic loading and it is composed by two distinct components, one intrinsic, dependent on the elastic material properties and the lattice type, and one extrinsic, related to the occurrence of crack closure effects. An important issue is that several factors can influence ΔKth and, in general, the fatigue crack propagation behavior. In this work, the influence of the experimental procedure, air humidity, stress ratio and test frequency on da/dN-ΔK data has been investigated. Results are discussed with their potential causes and consequences on the calculations of the residual lifetime. KW - Fatigue crack propagation threshold KW - Crack closure effect KW - Experimental procedure KW - Environmental conditions PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-544905 DO - https://doi.org/10.1016/j.prostr.2022.03.030 VL - 38 SP - 292 EP - 299 PB - Elsevier B.V. AN - OPUS4-54490 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Madia, Mauro T1 - Determination of the Kitagawa-Takahashi diagram for the EA4T railway axle steel by means of the cyclic R-curve method N2 - The Kitagawa-Takahashi (KT) diagram is a well-established tool in the fatigue community for the prediction of the fatigue limit of metallic materials in presence of defects. Nevertheless, its determination is associated with a large number of fatigue tests carried out on specimens with artificial defects (notches) to describe the fatigue limit-defect size relationship in the short crack regime. The preparation of the specimens and the execution of the tests is time expensive. Therefore, few phenomenological models have been introduced in the past to provide a first approximation of the KT diagram based solely on the fatigue limit for smooth specimen and the fatigue crack propagation threshold for long cracks. Despite the use of such models is widely spread, these suffer from problems related to the uncertainties of the material parameters. Furthermore, the mechanics of short cracks, which is the physical mechanism behind the concept of the fatigue limit, is not considered. This work discusses the advantages and drawbacks of using short fatigue crack propagation models for predicting the fatigue limit of flawed metallic materials. The KT diagrams for a EA4T railway axle steel in as-received and full-hardened condition are approximated by means of the cyclic R-curve method. T2 - 13th International Fatigue Congress CY - Hiroshima, Japan DA - 06.11.2023 KW - Fatigue limit KW - Crack propagation KW - Short crack KW - Cyclic R-curve KW - EA4T railway axle steel PY - 2023 AN - OPUS4-58867 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Duarte, Larissa T1 - Fatigue assessment procedure based on effective crack propagation data and cyclic R-curve N2 - Fracture mechanics-based methods can be applied to the fatigue assessment of mechanical components containing defects or cracks subjected to cyclic loading. The knowledge of the crack growth behavior for short and long cracks enables the determination of both finite and infinite life regimes. Nevertheless, a first problem arises from the empirical determination of the fatigue data, which vary according to the test conditions, e.g., the test method, frequency and the stress ratio R. This is due to crack closure and further environmental phenomena affecting crack propagation behavior. A second issue regards the lack of standard experimental procedures for the determination of the fatigue crack propagation threshold ΔKth dependency on the crack size. This is problematic, since ΔKth increases with the build-up of the closure effects in the short crack regime and its inaccurate experimental determination leads to large deviations in the assessment and, even more critical, to non-conservative predictions. Aiming at providing more reliable and safer assessment procedures, the present work proposes a method based on effective crack growth data obtained at high stress ratios (R ≈ 0.8). A short-crack model based on the cyclic R-curve and CPLR data is employed for describing the development of the closure effects. The predictions are compared to established methods and validated by experimental tests. T2 - Fatigue 2022+1 CY - Hiroshima, Japan DA - 06.11.2023 KW - Component assessment KW - Fatigue crack propagation KW - Fatigue threshold KW - Crack closure KW - Cyclic R-curve PY - 2023 AN - OPUS4-58842 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Duarte, Larissa A1 - Zerbst, Uwe A1 - Madia, Mauro T1 - Vergleichende Untersuchungen zum intrinsischen Schwellenwert der da/dN-ΔK-Kurve N2 - Für die Bestimmung der Restlebensdauer zyklisch beanspruchter Bauteile kommt dem Schwellenwert für Ermüdungsrissausbreitung, Δ𝐾𝑡ℎ, und dem sich anschließenden Schwellenwertbereich der 𝑑𝑎𝑑𝑁⁄−Δ𝐾-Kurve große Bedeutung zu. Dem stehen Unsicherheiten bei der Bestimmung und Analyse gegenüber. Der Aufsatz befasst sich mit der Ermittlung des sogenannten intrinsischen Schwellenwerts, der als robuster Eingangsparameter für eine „rissschließfreie“ Analyse der Restlebensdauer von entscheidender Bedeutung ist. T2 - 53. Tagung des DVM-Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Online meeting DA - 18.02.2021 KW - Schadenstolerante Bauteilauslegung, Restlebensdauer, intrinsischer Schwellenwert gegen Ermüdungsrissausbreitung PY - 2021 SN - 2366-4797 SP - 211 EP - 220 PB - Deutscher Verband für Materialforschung und -prüfung e.V. (DVM) CY - Berlin AN - OPUS4-52704 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Duarte, Larissa A1 - Zerbst, Uwe A1 - Madia, Mauro T1 - Der Schwellenwert der da/dN-∆K-Kurve als Auslegungskriterium für die Bauteilbewertung N2 - Für die Bestimmung der Restlebensdauer zyklisch beanspruchter Bauteile kommt dem Schwellenwert für Ermüdungsrissausbreitung ∆Kth und dem sich anschließenden Schwellenwertbereich der da/dN-∆K-Kurve große Bedeutung zu. Dem stehen Unsicherheiten bei der Bestimmung und Analyse gegenüber. Der Aufsatz befasst sich mit der Ermittlung des sogenannten intrinsischen Schwellenwerts, der als robuster Eingangsparameter für eine „rissschließfreie“ Analyse der Restlebensdauer von entscheidender Bedeutung ist. T2 - Tagung Werkstoffprüfung 2020 CY - Online meeting DA - 03.12.2020 KW - Schadenstolerante Bauteilauslegung, KW - Intrinsischer Schwellenwert gegen Ermüdungsrissausbreitung KW - Restlebensdauer PY - 2020 DO - https://doi.org/10.48447/WP-2020-025 SP - 1 EP - 8 AN - OPUS4-52788 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Vecchiato, L. A1 - Madia, Mauro A1 - Meneghetti, G. T1 - Extension of the peak stress method to estimate the fatigue limit of welded joints by means of the cyclic R-curve method N2 - A new simplified and effective method has been formalised to estimate the Constant Amplitude Fatigue Limit (CAFL) of stress-relieved steel welded joints subjected to uniaxial push–pull loading and failing from the weld toe. Starting from the sharp V-notch assumption of the NSIF approach and the cyclic R-curve of the material in the heat affected zone, the proposed method identifies the CAFL as threshold level of the local stress field at the V-notched weld toe in the uncracked configuration. Such threshold stress field assures the crack arrest at the V-notched weld toe, according to the cyclic R-curve analysis. The method has been validated against experimental results and proved effective for a straightforward assessment of the CAFL of welded joints, as the stable crack propagation analysis of classical fracture mechanics approaches can be avoided. KW - Cyclic R-curve KW - Welded joint KW - Fatigue limit KW - Peak stress method KW - Finite element analysis PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-581059 DO - https://doi.org/10.1016/j.tafmec.2023.104039 SN - 0167-8442 VL - 127 SP - 1 EP - 19 PB - Elsevier AN - OPUS4-58105 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zhu, Jiangchao A1 - Madia, Mauro A1 - Schurig, Michael A1 - Kruse, Julius A1 - Conrad, Fabian A1 - Schlums, Hartmut A1 - Kontermann, Christian A1 - Zerbst, Uwe T1 - On the use of representative specimens for the structural integrity assessment of safety-relevant rotating components N2 - Safety-relevant components, for which a failure in service could have catastrophic consequences, are usually designed for extremely low probability of failure and they are subjected to stringent part qualification procedures according to guidelines set by regulatory agencies. Manufacturers are often forced to perform tests on full scale or scaled components to ensure the structural integrity under defined loading conditions, which usually implies a huge experimental and financial effort. Therefore, companies try to develop new strategies such as digital twins, which allow to massively reduce costs, without compromising safety. This work presents a new quasi-static testing and assessment concept, the main idea of which is to replace, or at least reduce, the experimental testing on components by testing specimens representative of the component. Fracture mechanics specimens have been designed iteratively by numerical simulations to match the stress state at the crack-tip of the maximum permissible defect defined by regulatory agencies for the component. Potentially, the major benefit of the proposed approach is that the tests can be performed on conventional laboratory testing machines. The effectiveness of the methodology is demonstrated in case of the structural integrity assessment of a Ni-base superalloy aero-engine turbine disk at overspeed conditions. KW - Structural integrity KW - Turbine disk KW - Burst KW - Fracture mechanics KW - Representative specimens KW - Quasi-static testing PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-624208 DO - https://doi.org/10.1016/j.engfracmech.2024.110710 SN - 0013-7944 VL - 314 SP - 1 EP - 23 PB - Elsevier Ltd. AN - OPUS4-62420 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Werner, Tiago T1 - Damage tolerant design of metallic AM parts N2 - Additive Manufacturing (AM) opens new possibilities in the design of metallic components, including very complex geometries (e.g. structures optimized for certain loads), optimization of materials (e.g. gradient materials) and cost-effective manufacturing of spare parts. In the recent years, it has been used for the first safety-relevant parts, but the consideration of cyclic mechanical behavior in AM is still at the very beginning. The reason for this is the complexity of mechanical material properties, i.e. inhomogeneity, anisotropy and a large number of defects frequently textured and characterized by large scattering in size. Additionally, high surface roughness and residual stresses with complex distributions are typical of AM. Due to these reasons, the transferability of experimentally determined properties from specimens to components is a challenge. This presentation provides an overview of the questions concerning the application of AM to safety-relevant components. Possible strategies for the fatigue design of such components are presented. Besides the Kitagawa-Takahashi-diagram method and the cyclic R-curve analysis as approaches for damage-tolerant design, the identification of critical locations, the problem of representative material properties and the handling of residual stresses are addressed. T2 - 4th international symposium on Fatigue Design and Material Defects CY - Online meeting DA - 26.05.2020 KW - Additive Manufacturing KW - Cyclic R-Curve KW - Component assessment PY - 2020 AN - OPUS4-50938 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -