TY - JOUR A1 - Liepold, Philipp A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - A Force Based Determination of Hot Cracking Susceptibility N2 - Two high-strength, low-alloy Gas Metal Arc Welding (GMAW) wires were evaluated for their susceptibility to Solidification Cracking (SC) using a modified version of the Transverse Motion Weldability (TMW) test. In theoriginal TMW test, the Transverse Displacement Speed (TDS) is varied iteratively, and crack lengths are measured in each iteration. The modified version eliminates the need for multiple runs by continuously reducing the TDS over a single run. Rather than emphasizing crack lengths, this method assesses the reaction force to the TDS, thereby determining a Critical TDS (CTDS). This critical point directly correlates with the cessation of SC growth. CTDS values were measured under a range of welding parameters, thereby demonstrating the influence of Welding speed and arc energy (U × I/welding speed) on SC susceptibility for the tested filler metals. The CTDS data obtained from this testing method have the potential to provide valuable insights for practical applications in the field. KW - Force based KW - Neural Network KW - TRS PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-640140 DO - https://doi.org/10.5781/JWJ.2025.43.4.10 SN - 2466-2100 VL - 43 IS - 4 SP - 447 EP - 457 AN - OPUS4-64014 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Czeskleba, Denis A1 - Irfan, Muhammad Dary A1 - Wandtke, Karsten A1 - Kaiser, Sebastian A1 - Kannengießer, Thomas T1 - Wasserstoffdiffusion in hochfesten UP-Schweißverbindungen – einfacher als gedacht N2 - Hochfeste Baustähle werden im modernen Stahlbau aus wirtschaftlichen und konstruktiven Gründen zunehmend eingesetzt, z. B. im Gebäude-, Anlagen- oder Mobilkranbau. Durch den Einsatz von Stählen mit höheren 690 MPa) können durch die Reduzierung der Wanddicke erhebliche Gewichtsreduzierungen und geringere Verarbeitungskosten erreicht werden, insbesondere bei der Verwendung des Unterpulverschweißen (UP) durch seine hohe Abschmelzleistung. Aufgrund ihrer speziellen Mikrostruktur haben hochfeste Stähle eine begrenzte Duktilität und sind anfälliger für wasserstoffunterstützte Kaltrisse (HACC). Darüber hinaus führen große mittels UP geschweißter Blechdicken zu hohen Schweißeigenspannungen und langen Diffusionswegen für z.B. durch den Schweißprozess eingebrachten Wasserstoff. Abgesicherte Diffusionskoeffizienten für UP-Schweißungen dieser Festigkeitsklasse sind als Grundlage für die Abschätzung des Zeitintervalls einer möglichen verzögerten Kaltrissbildung oder für Nachwärmung zur Wasserstoffreduktion nur sehr begrenzt verfügbar. Aus diesem Grund wurden experimentelle Versuche zur mikrostruktur-spezifischen Diffusion in S690-Schweißungen durchgeführt. Dazu wurde ein thermomechanisch (TM) gewalzter bzw. vergüteter (QL) Zustand dieses Werkstoffs betrachtet, sowie das jeweilige charakteristische Schweißgut und WEZ. Dazu wurden den Schweißmikrostrukturen lokal Proben entnommen und über Permeations- bzw. Warmauslagerungsversuche die gefügespezifische Diffusion von Raumtemperatur bis 400°C charakterisiert. Im Gegensatz zu bekannten Effekten des Wärmebehandlungszustandes der Grundwerkstoffe auf die Diffusion in MSGSchweißverbindungen, zeigten die Wasserstoffdiffusionskoeffizienten über alle untersuchten Gefügezustände keine signifikanten Unterschiede, insbesondere nicht für die lokale WEZ diverser, untersuchter Streckenergiebereiche. Aus praktischer Anwendersicht können daher dickwandige UP-Verbindungen hinsichtlich einer verzögerten Wasserstoffdiffusion nur anhand der einfach ermittelbaren Diffusionskoeffizienten für den Grundwerkstoffkoeffizient beurteilt werden. Zudem zeigte sich, dass der unterschiedliche Walz- und Wärmebehandlungszustand (TM vs. QL) in UP-Schweißnähten eine untergeordnete Rolle für die Wasserstoffdiffusion und damit für die mögliche Zeitverzögerung der Kaltrissbildung hat. Ergänzende numerische Simulationen der Wasserstoffverteilung bestätigten das Verhalten. T2 - DVS Congress 2025 CY - Essen, Germany DA - 16.09.2025 KW - Unterpulverschweißen KW - Wasserstoffdiffusion KW - Wasserstoffunterstützte Kaltrissbildung KW - Wasserstoffrisse PY - 2025 SN - 978-3-96144-299-7 DO - https://doi.org/10.53192/DVSC20250330 VL - 401 SP - 330 EP - 340 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-64132 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erxleben, Kjell T1 - Component test for the assessment of in-service welding on/onto pressurized hydrogen pipelines N2 - Hydrogen is seen as the energy carrier of the future. Therefore a reliable infrastructure to transport hydrogen in a large scale is needed. A so called European hydrogen backbone out of long distance transmission pipelines is planned by European countries to create a hydrogen transport infrastructure. Due to economic reasons this will be achieved by new build pipelines such as repurposed natural Gas (NG) pipelines, converted to hydrogen useage. A general suitability for hydrogen service of low alloyed pipeline steel, as it is used for NG service today, is given. But in case of necessary in-service welding procedures in terms of e.g. hot-tapping and stoppling, the risk of a critical hydrogen uptake into the pipe materials due to much higher temeperatures while welding and the possibility of hydrogen embrittlement (HE) needs to be closely investigated. The presentation gives an overview of the current H2-SuD project, investigating the feasability of in-service welding on future hydrogen pipelines. Therefore, component-like demonstrators were developed to test (I) the additional hydrogen uptake due to in-service welding under hydrogen pressure and (II) to measure the temperature field due to different welding parameters and demonstrator geometries, especially on the inner pipe wall surface. Collected data will be used to validate a numerical simulation of the thermal field and additionally the hydrogen diffusion in the pipeline material. T2 - Presentation at The University of Manchester CY - Manchester, United Kingdom DA - 12.09.2025 KW - In-service KW - Hydrogen KW - Pipeline KW - Welding PY - 2025 AN - OPUS4-64129 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kaiser, Sebastian T1 - Wasserstoffdiffusion in hochfesten UP-Schweißverbindungen - einfacher als gedacht N2 - Hochfeste Baustähle werden im modernen Stahlbau aus wirtschaftlichen und konstruktiven Gründen zunehmend eingesetzt, z. B. im Gebäude-, Anlagen- oder Mobilkranbau. Durch den Einsatz von Stählen mit höheren 690 MPa) können durch die Reduzierung der Wanddicke erhebliche Gewichtsreduzierungen und geringere Verarbeitungskosten erreicht werden, insbesondere bei der Verwendung des Unterpulverschweißen (UP) durch seine hohe Abschmelzleistung. Aufgrund ihrer speziellen Mikrostruktur haben hochfeste Stähle eine begrenzte Duktilität und sind anfälliger für wasserstoffunterstützte Kaltrisse (HACC). Darüber hinaus führen große mittels UP geschweißter Blechdicken zu hohen Schweißeigenspannungen und langen Diffusionswegen für z.B. durch den Schweißprozess eingebrachten Wasserstoff. Abgesicherte Diffusionskoeffizienten für UP-Schweißungen dieser Festigkeitsklasse sind als Grundlage für die Abschätzung des Zeitintervalls einer möglichen verzögerten Kaltrissbildung oder für Nachwärmung zur Wasserstoffreduktion nur sehr begrenzt verfügbar. Aus diesem Grund wurden experimentelle Versuche zur mikrostruktur-spezifischen Diffusion in S690-Schweißungen durchgeführt. Dazu wurde ein thermomechanisch (TM) gewalzter bzw. vergüteter (QL) Zustand dieses Werkstoffs betrachtet, sowie das jeweilige charakteristische Schweißgut und WEZ. Dazu wurden den Schweißmikrostrukturen lokal Proben entnommen und über Permeations- bzw. Warmauslagerungsversuche die gefügespezifische Diffusion von Raumtemperatur bis 400°C charakterisiert. Im Gegensatz zu bekannten Effekten des Wärmebehandlungszustandes der Grundwerkstoffe auf die Diffusion in MSGSchweißverbindungen, zeigten die Wasserstoffdiffusionskoeffizienten über alle untersuchten Gefügezustände keine signifikanten Unterschiede, insbesondere nicht für die lokale WEZ diverser, untersuchter Streckenergiebereiche. Aus praktischer Anwendersicht können daher dickwandige UP-Verbindungen hinsichtlich einer verzögerten Wasserstoffdiffusion nur anhand der einfach ermittelbaren Diffusionskoeffizienten für den Grundwerkstoffkoeffizient beurteilt werden. Zudem zeigte sich, dass der unterschiedliche Walz- und Wärmebehandlungszustand (TM vs. QL) in UP-Schweißnähten eine untergeordnete Rolle für die Wasserstoffdiffusion und damit für die mögliche Zeitverzögerung der Kaltrissbildung hat. Ergänzende numerische Simulationen der Wasserstoffverteilung bestätigten das Verhalten. T2 - DVS Congress 2025 CY - Essen, Germany DA - 16.09.2025 KW - Unterpulverschweißen KW - Wasserstoffdiffusion KW - Wasserstoffunterstützte Kaltrissbildung KW - Wasserstoffrisse PY - 2025 AN - OPUS4-64130 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael T1 - Numerical simulation of weld heat input effect on microstructure and hydrogen diffusion in thick-walled S690 submerged arc welded joints N2 - High-strength, low-alloy (HLSA) steels such as S690 are an attractive option for heavy industries such as offshore wind turbines and peripheral equipment due to their combination of excellent mechanical properties and weldability. The construction of these thick-walled structures requires highly efficient welding processes such as submerged arc welding (SAW). However, SAW presents challenges related to delayed hydrogen assisted cold cracking (HACC). Despite its importance, the effect of different diffusion coefficients on the cold cracking susceptibility of different microstructures within SAW-welded S690 steels is not fully understood. For this reason, the present study focuses on comparing the cold cracking susceptibility of thermomechanically rolled (TM) or quenched and tempered (QL) variants of S690 steel. SAW was performed on specimens of both steel grades to produce weldments consisting of weld metal, heat-affected zone (HAZ), and base metal. Electrochemical hydrogen permeation tests (ISO 17081) were performed to determine the microstructure specific coefficients. Using the obtained coefficients, a numerical model was developed to identify the time- and microstructure-dependent local hydrogen diffusion and its influence on the distribution within the welds. The results showed that the TM grade exhibited slightly accelerated hydrogen diffusion compared to the QL grade, which is beneficial for hydrogen reduction and increases the HACC resistance. However, the further simulations with different ply sequences showed that the welding heat input (i.e. welding ply sequence) had a significantly higher effect on hydrogen accumulation. Specifically, increased welding heat input and increased thicknesses decrease hydrogen diffusivity. For this reason, microstructure-specific hydrogen diffusion played a minor role in thick-layer SAW joints compared to the need to control the welding parameters (layer sequence, individual layer thickness, welding heat input). T2 - FEMS Euromat 2025 - 18th European Congress and Exhibition on Advanced Materials and Processes CY - Granada, Spain DA - 15.09.2025 KW - Hydrogen assisted cracking KW - Welding KW - High strength steels KW - Numerical simulation KW - Electrochemical permeation PY - 2025 AN - OPUS4-64158 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael T1 - Hydrogen trap characterization in 200 and 1,000 bar charged CoCrNi medium entropy alloy compared to steel AISI 316L N2 - Multiple principal element alloys (MPEAs) represent a new class of metallic materials. MPEAs, such as the CoCrNi medium entropy alloy (MEA), have attracted considerable research attention as potential materials to replace, for example, austenitic steels in high-pressure hydrogen environments. Due to the relatively new alloy concept, studies on the specific hydrogen diffusion and trapping behavior of high-pressure hydrogen-charged CoCrNi MEAs are rare so far. For this reason, a CoCrNi-MEA was investigated and compared to an austenitic stainless steel, AISI 316L. Both materials were subjected to high pressure hydrogen loading for two different pressures: 200 bar and 1,000 bar. After charging, thermal desorption analysis (TDA) was used with three heating rates from 0.125 K/s to 0.500 K/s to clarify the specific hydrogen desorption and trapping behavior. To the best of our knowledge, this study is the first to characterize hydrogen diffusion and trapping in 1,000 bar high-pressure charged CoCrNi. For this purpose, the underlying TDA spectra were analyzed in terms of peak deconvolution into a metallurgically justifiable number of defined peaks. The individual peak temperatures and activation energies “EA” were calculated. The following conclusions can be drawn from the results obtained: (1) Exposure to 200 bar or 1,000 bar leads to an increase in hydrogen absorption, regardless of the material investigated, expressed by a significantly increased desorption rate at 1,000 bar. However, the effusion peaks typically occur only at high temperatures. The (2) TDA showed that a four-peak deconvolution scenario was sufficient to describe the trapping behavior and the "EA" indicated the dominance of irreversible traps. In addition, the average trapping energy is higher than in the 316L. The (3) charge pressure related hydrogen solubility was in the order of: CoCrNi-MEA < 316L for both pressures and (4) charging at 1000 bar results in an average concentration of 49 wt.ppm (CoCrNi-MEA) and > 75 wt.ppm (316L). In summary, the CoCrNi-MEA was characterized by a reduced solubility, but very deep entrapment compared to the 316L. For this reason, further application potentials of the MEA may arise. T2 - FEMS Euromat 2025 - 18th European Congress and Exhibition on Advanced Materials and Processes CY - Granada, Spain DA - 15.09.2025 KW - Medium entropy alloy KW - Hydrogen KW - Trapping KW - Diffusion KW - High-pressure charging PY - 2025 AN - OPUS4-64160 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael T1 - Effect of Ti and Nb on hydrogen trapping in welded S690 HSLA steel and effect on delayed cold cracking N2 - Fine-grain, high-strength, low-alloy (HSLA) structural steels with yield strengths > 600 MPa are now the state of the art in construction applications such as mobile cranes and civil engineering. HSLA grades derive their strength from a combination of specific heat treatment and the underlying chemical composition. In this context, Ti or Nb are essential to obtain a fine-grained microstructure as well as the necessary carbides or nitrides for precipitation strengthening. In this context, the specific effect of Ti or Nb-rich compounds on hydrogen trapping and diffusion is well known for special laboratory cast alloys, but unknown for realistic steel compositions. For this reason, a series of S690Q-based alloys were synthesized, close to a real steel composition, but with well controlled Ti or Nb additions in different amounts. Specimens were obtained from these alloys by electrochemical discharge machining (EDM). The specimens were tested using the well-established electrochemical permeation technique. From the experimental results, the hydrogen diffusion coefficients and the analytical subsurface hydrogen concentration were calculated. In addition, the hydrogen trapping behavior at elevated temperatures was interpreted by thermal desorption analysis (TDA) using different heating rates of hydrogen charged samples. The results showed that in contrast to metallurgically "pure" laboratory cast alloys, realistic chemical compositions were similar in their hydrogen trapping behavior, despite some small differences. All investigated steel grades exhibited shallow and reversible hydrogen trapping, regardless of their chemical composition. Of course, the experiments only allowed the calculation of effective diffusion coefficients and trapping energies, which represent an average of the entire microstructure. Nevertheless, HSLA steels are typically joined by arc welding, which includes the risk of delayed hydrogen assisted cracking. From the point of view of welding practice, however, a more or less identical hydrogen diffusion behavior means that no special "metallurgically specific", justifiable measures need to be considered, despite the well-established processes such as "soaking" or dehydrogenation heat treatment. Of course, a closer look at the heat-affected zone (HAZ) or the weld metal of the specific welds is necessary. However, especially in the case of thick-walled welds, it is assumed that the weld metal and HAZ are similar to the base material due to the multi-layer welding, which results in multiple annealing cycles of the weld metal and HAZ. T2 - FEMS Euromat 2025 - 18th European Congress and Exhibition on Advanced Materials and Processes CY - Granada, Spain DA - 15.09.2025 KW - Hydrogen assisted cracking KW - HSLA KW - Diffusion KW - Electrochemical permeation PY - 2025 AN - OPUS4-64156 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael T1 - Component test for the assessment of in-service welding on/onto pressurized hydrogen pipelines N2 - Hydrogen is the energy carrier of tomorrow and requires a reliable large-scale transport infrastructure. In addition to new pipelines, the conversion of existing natural gas (NG) pipeline grids is an essential part. The transport of hydrogen is fundamentally different from that of NG, as hydrogen can be absorbed into the pipeline material. Given the effects of hydrogen embrittlement, the material compatibility (low alloy steels in a wide range of strengths and thicknesses) must be investigated. However, pipelines e.g. require maintenance or the need for installation of additional outlets with the necessity of welding on/onto the pipelines while they are still in service, i.e. with gas flow under high pressure, such as the well-known "hot tapping". This in-service welding poses challenges for hydrogen operations. The challenge can be roughly divided into the possible austenitization of the inner pipe material exposed to hydrogen, the welding itself, which causes an increased temperature range. Both lead to a significant increase in hydrogen solubility and diffusivity compared to room temperature. In addition, possible surface reactions of the present iron oxides (e.g. magnetite or hematite) with the hot hydrogen should be considered. In this context, the knowledge of hydrogen pipelines is scarce due to the lack of operational experience. Fundamental experimental investigations are required to investigate the transferability from NG to hydrogen pipeline grids. For this reason, the present study presents a specially designed mock-up / demonstrator concept for the realistic assessment of the welding process conditions. The mock-up was designed to allow in-situ temperature measurement during the welding process as well as ex-post sample extraction for quantification of the absorbed hydrogen concentration. For safety reasons, the required volume of pressurized hydrogen was limited by inserting a solid cylinder to ensure a 1 cm thick layer of hydrogen gas. Welding experiments on the DN60 and DN200 pressurized mock-ups showed the possibility of safe welding on or onto pressurized hydrogen pipelines. Indeed, the austenitizing temperature was reached on the inner surface of the pipeline, especially on thinner-walled pipelines, using current welding parameter recommendations. This corresponded to an increased hydrogen uptake in the welded area of several ppm. From this point of view, the suggested component concept is a viable strategy for the screening of several materials and welding parameter combinations under realistic operational conditions. T2 - FEMS Euromat 2025 - 18th European Congress and Exhibition on Advanced Materials and Processes CY - Granada, Spain DA - 15.09.2025 KW - In-service welding KW - Pipeline KW - Hydrogen KW - Component test PY - 2025 AN - OPUS4-64159 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael T1 - Component-test for determination of welding residual stresses and their effect on stress relief cracking in thick-walled welds N2 - Controlling the residual stress level during welding of creep-resistant Cr-Mo-V steels is crucial to avoid so called stress relief cracking (SRC) during post weld heat treatment (PWHT) of large-scale components. In the present study, a laboratory scale test specimen (slotted sample with 400 mm width, 400 mm length and 25 mm thickness) was used to simulate thick-walled component welds made of 13CrMoV9-10. The aim was to identify the level and distribution of residual stresses to evaluate the suitability of the specimen for laboratory based SRC testing. High restraint was ensured by the specimen geometry with a narrow welding gap in the center. This gap was filled by multi-layer submerged arc welding. Two specimens were welded with identical parameters and compared in the as-welded state and after PWHT (705 °C for 10 h). Neutron diffraction was used to determine the residual stresses in the weld metal, the heat-affected zone (HAZ) and the base material at different depths longitudinal, transverse, and normal to the welding direction. The experiments were performed on the former instrument E3 of the research reactor BER II of Helmholtz-Zentrum Berlin (HZB), Germany. Complementarily, laboratory X-ray diffraction was applied to characterize the surface residual stresses. In the welded condition, especially in the weld metal and the adjacent HAZ, the longitudinal residual stresses reached values of up to 1,000 MPa to 1,200 MPa due to the increasing strength and hardness of the CrMoV-material during welding. The conducted welding experiments revealed that way higher residual stresses in the welded joint have to anticipated before the PWHT is performed than it was expected in advance. This demonstrated the necessity of suitable component-like welding tests as they must ensure realistic mechanical stiffness (hindered shrinkage of welding joint by slotted self-restraint sample) and heat dissipation conditions (definition of minimum welding joint thickness vs. welding process-specific heat input). T2 - FEMS Euromat 2025 - 18th European Congress and Exhibition on Advanced Materials and Processes CY - Granada, Spain DA - 15.09.2025 KW - Component test KW - Submerged arc welding KW - Post weld heat treatment KW - Residual stresses KW - Neutron diffraction PY - 2025 AN - OPUS4-64161 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Blasón Gonzalez, Sergio A1 - Chaudry, Mohsin Ali A1 - Elorriaga, A. A1 - Madia, Mauro A1 - Zerbst, Uwe A1 - Llavori, I. A1 - Hilgenberg, Kai T1 - Design methodology of vessel produced by L PBF stainless steel using representative specimens N2 - This work presents the preliminary results of an ongoing project with a double objective: on the one hand, the characterisation of the mechanical properties against fatigue damage of an additively manufactured 316 stainless steel produced by laser powder bed-based (L-PBF) technology; on the other hand, the implementation of numerical simulation techniques able to predict the mechanical behaviour of the material in order to optimise and reduce the design costs of vessels used in the chemical sector. The current state of the work developed in this research framework allows showing the first batch of experimental results of crack propagation rate (FCGR) and high cycle fatigue (HCF) tests. The geometry of the vessels studied presents three clearly differentiated regions, either in terms of thickness (11-15 mm) or concerning the inclination of the walls to the direction of manufacturing (0º - 45º). The experimental campaign carried out so far allows identifying the differences in behaviour when comparing different extraction locations around the vessel. This is due to the variations in thermal cycles that the deposited material undergoes during the manufacturing process. Therefore, this causes variations in the microstructure which lead to changes in the response of the material. In this work, these differences are analysed qualitatively and quantitatively from the results of FCGR and HCF, thus allowing to locate the regions with the highest risk in terms of structural integrity against fatigue. This preliminary phase together with the numerical simulation of the additive manufacturing process are key to achieving a reliable description and modelling of the material. The latter will make it possible to address the priority aim of this project, involving the manufacture of independent samples whose properties are representative of the original material extracted from the reference vessels. It is, therefore, a comprehensive methodology for the design of additively manufactured components based on the localised fatigue mechanical properties of representative specimens. T2 - ECF23, European Conference on Fracture 2022 CY - Funchal, Portugal DA - 27.06.2022 KW - Additive manufacturing KW - Steel 316L KW - Fracture Mechanics PY - 2022 AN - OPUS4-55240 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -