TY - THES A1 - Magkos, Sotirios T1 - Iterative reconstruction from under-sampled Computed Tomography data N2 - In X-ray computed tomography (XCT), an X-ray beam of intensity I0 is transmitted through an object and its attenuated intensity I is measured when it exits the object. The attenuation of the beam depends on the attenuation coefficients along its path. The attenuation coefficients provide information about the structure and composition of the object and can be determined through mathematical operations that are referred to as reconstruction. The standard reconstruction algorithms are based on the filtered backprojection (FBP) of the measured data. While these algorithms are fast and relatively simple, they do not always succeed in computing a precise reconstruction, especially from under-sampled data. Alternatively, an image or volume can be reconstructed by solving a system of linear equations. Typically, the system of equations is too large to be solved but its solution can be approximated by iterative methods, such as the Simultaneous Iterative Reconstruction Technique (SIRT) and the Conjugate Gradient Least Squares (CGLS). This dissertation focuses on the development of a novel iterative algorithm, the Direct Iterative Reconstruction of Computed Tomography Trajectories (DIRECTT). After its reconstruction principle is explained, its performance is assessed for real parallel- and cone-beam CT (including under-sampled) data and compared to that of other established algorithms. Finally, it is demonstrated how the shape of the measured object can be modelled into DIRECTT to achieve even better reconstruction results. KW - Computed tomography KW - DIRECTT KW - Iterative algorithm KW - X-ray imaging KW - Metrics PY - 2022 SP - 1 EP - 94 PB - Universitätsbibliothek Potsdam CY - Potsdam AN - OPUS4-56465 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Mishurova, Tatiana T1 - Influence of residual stress and microstructure on mechanical performance of LPBF TI-6AL-4V N2 - Additive manufacturing technologies provide unique possibilities in the production of topologically optimized, near-net shape components. The main limiting factors affecting the structural integrity of Laser Powder Bed Fusion (LPBF) parts are manufacturing defects and residual stress (RS) because both of them are virtually inevitable. Taking into account the complex thermal history of LPBF materials, a prediction of the material behavior is not possible without experimental data on the microstructure, defect distribution, and RS fields. Therefore, this thesis aims to understand the factors that influence the LPBF Ti-6Al-4V material performance the most, covering both the production and the post-processing steps of manufacturing. Indeed, a parametric study on the influence of manufacturing process and post-processing on RS, defects and microstructure was performed. It was found that the volumetric energy Density (EV), commonly used for the LPBF process optimization, does neither consider the pore shapes and distribution, nor the influence of individual parameters on the volume fraction of pores. Therefore, it was recommended not to use EV without great care. It was shown that the Position on the base plate has a great impact on the amount of RS in the part. The micromechanical behavior of LPBF Ti-6Al-4V was also studied using in-situ Synchrotron X-ray diffraction during tensile and compression tests. Diffraction elastic constants (DEC), connecting macroscopic stress and (micro) strain, of the LPBF Ti-6Al-4V showed a difference from the DEC of conventionally manufactured alloy. This fact was attributed to the peculiar microstructure and crystallographic texture. It was therefore recommended to determine experimentally DECs whenever possible. Low Cycle Fatigue (LCF) tests at a chosen operating temperature were performed to evaluate the effect of post-treatment on the mechanical performance. Through the information on the microstructure, the mesostructure, and the RS, the LCF behavior was (indirectly) correlated to the process parameters. It was found that the fatigue performance of LPBF samples subjected to hot isostatic pressing is similar to that of hot-formed Ti-6Al-4V. The tensile RS found at the surface of LPBF as-built samples decreased the fatigue life compared to the heat-treated samples. The modification of the microstructure (by heat treatment) did not affect the Fatigue performance in the elastic regime. This shows that in the absence of tensile RS, the manufacturing defects solely control the failure of LPBF components and densification has the strongest effect on the improvement of the mechanical performance. KW - Additive manufacturing KW - Ti-6Al-4V KW - Residual stress KW - Computed tomography PY - 2021 SP - 1 EP - 143 CY - RWTH Aachen AN - OPUS4-54389 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -