TY - CONF A1 - Schartel, Bernhard T1 - Small but Great – Multifunctional Graphene in Rubber Nanocomposites N2 - A few layer/multilayer graphene (MLG) with a specific surface area of BET ≥ 250 m2/g is proposed as an efficient multifunctional nanofiller for rubbers. The preparation method, i.e., ultrasonically-assisted solution or latex premixing of master batches followed by conventional two-roll milling, strongly influences the dispersion in the elastomeric matrix and is fundamental for the final properties. When homogenously dispersed, single stacks of only approximately 10 graphene sheets, with an aspect ratio of ca. 35, work at low loadings, enabling the replacement of large amounts of carbon black (CB), an increase in efficiency, and a reduction in filler load. The appropriate preparation yielded nanocomposites in which just 3 phr are sufficient to significantly improve the rheological, curing, gas barrier properties, electrical and thermal conductivity, as well as mechanical properties of different rubbers, as shown for chlorine-Isobutylene-Isoprene rubber (CIIR), nitrile-butadiene rubber (NBR), natural rubber (NR), and styrene-butadiene rubber (SBR).[1-5] 3 phr of MLG tripled the Young’s modulus of CIIR, an effect equivalent to 20 phr of CB. The stronger interactions between MLG and NR or SBR also resulted in a reduction in the elongation at break by 20% and 50%, respectively, while the same parameter was hardly changed for CIIR/MLG and NBR/MLG. CIIR/MLG and NBR/MLG were stiffer but just as defomable than CIIR and NBR. The strong reinforcing effect of 3 phr MLG was confirmed by the increase of greater than 10 Shore A in hardness. MLG reduces gas permeability, increases thermal and electrical conductivities, and retards flammability. We investigated MLG also as a synergist for reducing the aluminium trihydrate loading in flame retardant hydrogenated acrylonitrile-butadiene (HNBR), polybutadiene chloroprene (BR/CR), and chlorosulfonated polyethylene rubber(CSM).[6-8] The higher the nanofiller concentration is, the greater the improvement in the properties. For instance, the permeability decreased by 30% at 3 phr of MLG, 50% at 5 phr and 60% at 10 phr, respectively. Moreover, the MLG nanocomposites improve stability of mechanical properties against the effects of weathering. In key experiments an increase in UV-absorption and a pronounced radical scavenging were proved as stabilizing mechanisms. In a nutshell, MLG is an efficient multifunctional nanofiller ready to be used for innovative rubber development. T2 - 34th PDDG Conference CY - Dubrovnik, Croatia DA - 11.06.2023 KW - Graphene KW - Nanocomposites KW - Reinforcement KW - Antioxydant KW - Flame retardant KW - Durability PY - 2023 AN - OPUS4-57693 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schartel, Bernhard T1 - Multifunctional Elastomer/Graphene Nanocomposites N2 - A few layer/multilayer graphene (MLG) with a specific surface area of BET=250 m2/g is proposed as an efficient multifunctional nanofiller for rubbers. The preparation method, i.e., ultrasonically-assisted solution mixing of master batches followed by two-roll milling, strongly influences the dispersion in the elastomeric matrix and is fundamental for the final properties. When homogenously dispersed, single stacks of only approximately 10 graphene sheets, with an aspect ratio of 34, work at low loadings, enabling the replacement of large amounts of carbon black (CB), an increase in efficiency, and a reduction in filler load. The appropriate preparation yielded nanocomposites in which just 3 phr are sufficient to significantly improve the rheological, curing, gas barrier properties, electrical and thermal conductivity, as well as mechanical properties of different rubbers, as shown for chlorine-Isobutylene-Isoprene rubber (CIIR), nitrile-butadiene rubber (NBR), natural rubber (NR), and styrene-butadiene rubber (SBR). 3 phr of MLG tripled the Young’s modulus of CIIR, an effect equivalent to 20 phr of CB. The stronger interactions between MLG and NR or SBR also resulted in a reduction in the elongation at break by 20% and 50%, respectively, while the same parameter was hardly changed for CIIR/MLG and NBR/MLG. CIIR/MLG and NBR/MLG were stiffer but just as defomable than CIIR and NBR. The strong reinforcing effect of 3 phr MLG was confirmed by the increase of greater than 10 Shore A in hardness. MLG reduces gas permeability, increases thermal and electrical conductivities, and retards flammability, the latter shown by the reduction in heat release rate in the cone calorimeter. We investigated MLG also as a synergist for reducing the aluminium trihydrate loading in flame retardant hydrogenated acrylonitrile-butadiene (HNBR), polybutadiene chloroprene (BR/CR), and chlorosulfonated polyethylene rubber(CSM). The higher the nanofiller concentration is, the greater the improvement in the properties. For instance, the permeability decreased by 30% at 3 phr of MLG, 50% at 5 phr and 60% at 10 phr, respectively. Moreover, the MLG nanocomposites improve stability of mechanical properties against the effects of weathering. In key experiments an increase in UV-absorption and a pronounced radical scavenging were proved as stabilizing mechanisms. In a nutshell, MLG is an efficient multifunctional nanofiller ready to be used for innovative rubber development. T2 - 19th European Polymer Congress, EPF 2022 CY - Prague, Czech Republic DA - 26.06.2022 KW - Graphene KW - Nanocomposite KW - Rubber KW - Elastomer PY - 2022 AN - OPUS4-55196 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tabaka, Weronika A1 - Schartel, Bernhard T1 - Less is More: Optimised Fire Performance in Glass Fibre-reinforced Polybutylene Terephthalate Laminates with Concentrated Flame Retardant Top Layer N2 - To achieve optimum fire performance while maintaining mechanical integrity, flame retardants (FR) were strategically concentrated in the surface layer of a two-layer glass fibre-reinforced polybutylene terephthalate (PBT) laminate structure. Three potentially synergistic FR systems were selected to improve the fire performance of glass fibre-reinforced PBT: boehmite (AlOOH) with melamine polyzinc phosphate (MPZnP), aluminium diethyl phosphinates (AlPi) with melamine cyanurate (MC), and expandable graphite (EG) with melamine polyphosphate (MPP). Limited Oxygen Index (LOI) and UL-94 testing highlighted the influence of laminate architecture on flammability. The cone calorimeter results showed that increasing the FR concentration in the top layer significantly reduced both the peak heat release rate (PHRR) and the maximum average rate of heat emission (MARHE), with improvements depending on the specific FR system used. The laminate L-PBT/GF/AlOOH/MPZnP with a 2:2 thickness ratio showed outstanding performance, achieving a 45 % reduction in MARHE compared to composites with uniform FR distribution. This result showcases the superior thermal barrier properties and synergistic behaviour of AlOOH and MPZnP. The fire performance of laminates containing AlPi and MC was strongly influenced by the distribution and concentration of AlPi/MC. The EG/MPP system was found to be highly effective, forming a protective intumescent layer that significantly reduced both HRR and MARHE, demonstrating the effectiveness of strategically concentrating FR in the top layer. KW - Glass fibres KW - PBT KW - Flame retardants KW - Composites KW - Laminates KW - Fire behaviour KW - Flammability PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-626381 DO - https://doi.org/10.1016/j.jcomc.2025.100577 SN - 2666-6820 VL - 16 SP - 1 EP - 15 PB - Elsevier CY - Amsterdam AN - OPUS4-62638 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rappsilber, Tim A1 - Yusfi, Nawar A1 - Krüger, Simone A1 - Hahn, S.-K. A1 - Fellinger, Tim-Patrick A1 - Krug von Nidda, Jonas A1 - Tschirschwitz, Rico T1 - Meta-analysis of heat release and smoke gas emission during thermal runaway of lithium-ion batteries N2 - Herein a meta-analysis of 76 experimental research papers from 2000 to 2021 is given about possible effects on the thermal runaway of lithium-ion battery cells. Data on the hazards of gas emissions and released heat are related to each other and differentiated by cell properties such as, cell geometry, cathode type or state of charge. Quantitative information on the total heat release in the range of 2.0–112.0 kJ Wh−1, the peak heat release rate in the range of 0.006–2.8 kW Wh−1and the smoke gas emission were extracted, normalized in terms of cell energy (Wh), combined in a data library and compared graphically. The total amount of gas emitted (3–48 mmol Wh−1) as well as the released amount of carbon monoxide (1–161 mg Wh−1) and hydrogen fluoride (2–197 mg Wh−1) were investigated as a function of the state of charge and cell geometry. The analysis reveals that the measured values are significantly influenced by the types of calorimeters and smoke gas analyzers used as well as by the type of thermal runaway trigger. This meta-analysis can serve as an important basis for any risk assessment of lithium-ion batteries. KW - Lithium-ion battery KW - Thermal runaway KW - Cathode active material KW - Heat release KW - Smoke gas emission PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-568071 DO - https://doi.org/10.1016/j.est.2022.106579 SN - 2352-152X VL - 60 SP - 1 EP - 15 PB - Elsevier CY - Amsterdam AN - OPUS4-56807 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Tabaka, Weronika T1 - Bench-scale fire stability testing of carbon fibre reinforced polymer laminates with protective layers N2 - Fire resistance testing of components made of carbon fibre reinforced polymers (CFRP) composites usually demands intermediate-scale or full-scale testing. In this study, a bench-scale test is presented as a practicable and efficient method to assess the improvement in structural integrity of CFRP with different protective interlayers during fire. Fire stability is one of the biggest issues of carbon fibre reinforced polymer (CFRP) composites, particularly when they are using in load bearing applications. As soon as the glass transition temperature of polymer matrix (100-200°C) is achieved, the composite loses its structural integrity, what leads to the distortion and failure. The principal fire stability test is based on simultaneous application of fire and mechanical load. Since the carbon fibres can transfer the tensile loads quite well, the compression load is chosen as a required mechanical load for a test. The fire tests were preceded by a static load test at room temperature to determine ultimate failure load. The specimen was loaded with a compression force until the failure load was reached, which was observed as a buckling. For the fire tests, 10% of compression failure load and direct flame of a fully developed fire (heat flux ≈ 180 kW m-2) were applied simultaneously to the specimen, while the time to failure was measured. The possibilities of bench-scale fire stability testing were presented by investigating new types of laminate structures, which exhibit promising flame retardancy and fireproof properties. The new approach of CFRP laminate differs with a protective concept. Every system consists of two different interlayers (titanium foil, thermoplastic foil PEI, ceramic layer WHIPOX, rubber tape Pyrostat, basalt fibres and kenaf fibres), where the one layer constitutes the fireproof protection, that delays the rise of temperature in the rest of laminate, and the second layer provides very good structural connection with carbon fibre layers, thus improves the mechanical integrity of CFRP composite in fire. The time to failure of CFRP composite was 17s. Protective systems significantly enhance the fire stability and increased time to failure by 3 to 10 times. Thicker specimens showed longer resistance time, however CFRP laminate with ceramic layer and titanium foil presented outstanding results and the best performance. The protection with Kenaf and basalt fibres offered a natural fibre solution with also good fire resistance performance Although bench-scale tests are limited with respect to assessing the performance of components and structures, they are valuable in the assessment of different materials concepts. Furthermore, the reduced effort of conducting bench-scale test (lower costs, time, personnel resources) makes it more practical and effective. T2 - 19th European meeting on Fire Retardant Polymeric Materials (FRPM23) CY - Dübendorf, Switzerland DA - 26.06.2023 KW - Fire resistance KW - Carbon fibre reinforced polymer KW - Bench-scale testing PY - 2023 AN - OPUS4-57880 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias A1 - Kömmling, Anja A1 - Böhning, Martin A1 - Silbernagl, Dorothee T1 - Comparison of ageing behavior of O-ring seals under hydrogen and air N2 - Elastomeric seals are essential components in the infrastructure which prevent leakage of gas and ensure proper function of technical devices and are therefore highly safety relevant. For proper function a remaining resilience and tolerance to pressure changes is required. The ageing of elastomers is an undesirable but inevitable process leading to a limited lifetime of rubber products such as seals. Independent of the application, as e.g. automotive, piping or container applications, a long lifetime or at least a timely exchange of a seal before occurrence of critical failure is desired. Hydrogen is a key element for the energy turnaround and therefore the compatibility of seals with hydrogen is essential. In addition to the effect of hydrogen uptake and release, which might also cause destructive effects such as rapid gas decompression, ageing at high temperature under hydrogen atmosphere is of interest too. Most of the existing work is addressing the performance of new materials and comprises only very limited investigations concerning long-term use and the behaviour of aged materials in contact with hydrogen. As ageing can lead to substantial changes of material properties, it must be evaluated whether these changes are beneficial or deteriorating for the component function. In this work we present and compare results of the characterization of three sealing materials (EPDM, HNBR, FKM) after ageing at high temperature under hydrogen and air. Despite the common assumption that ageing under hydrogen atmosphere should be less severe for the material in comparison to air ageing, this is not the case for every material. T2 - ASME PVP2025, Pressure Vessels & Piping Conference CY - Montreal, Quebec, Canada DA - 20.07.2025 KW - Aging KW - Seal KW - Compression set KW - Atomic force microscopy PY - 2025 SP - 1 EP - 7 AN - OPUS4-63889 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zaghdoudi, M. A1 - Kömmling, Anja A1 - Böhning, Martin A1 - Jaunich, Matthias T1 - Ageing of elastomers in air and in hydrogen environment - A comparative study N2 - EPDM, HNBR and FKM materials were exposed at 150 ◦C to air under atmospheric pressure and to hydrogen at 50 bar for different ageing times. All measurements after hydrogen exposure were conducted on samples in degassed condition to assess irreversible effects resulting from that exposure and to compare them to those after ageing in air. Density, hardness, tensile properties, compression set, and hydrogen permeability of all samples were analysed. In both ageing environments, HNBR exhibited the most significant changes of material properties. However, for both EPDM and HNBR, considerably less severe ageing effects were observed under hydrogen in comparison to ageing in air. On the other hand, FKM showed about the same low level of deterioration in both ageing environments but exhibited poor resistance against damage due to rapid gas decompression in hydrogen environment that can lead to seal failure. The obtained results may serve as a guidance toward a better understanding for design and utilisation of elastomeric materials in future hydrogen infrastructure components. KW - Rapid gas decompression KW - Condensed matter physics KW - Hydrogen KW - Sustainability and the environment KW - Rubber sealing KW - Renewable energy PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-597417 DO - https://doi.org/10.1016/j.ijhydene.2024.03.053 SN - 0360-3199 SN - 1879-3487 VL - 63 SP - 207 EP - 216 PB - Elsevier CY - Oxford AN - OPUS4-59741 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Klippel, Andrea A1 - Hofmann‐Böllinghaus, Anja A1 - Piechnik, Kira A1 - Heydick, Lukas A1 - Wu, Hongyi A1 - Köhler, Florian A1 - Klaffke, Benjamin T1 - Experimental Analysis of Fire Behavior in Pine Forests and Agricultural Fields: Large‐Scale Tests Conducted Within the European TREEADS Project N2 - Two large‐scale experiments investigated fire spread mechanisms in vegetation ground fires in a pine forest and an agricultural field within the European TREEADS project. The tests, conducted in Saxony‐Anhalt and Brandenburg, targeted regions with dry, sandy soils and extensive pine stands and aim to improve suppression strategies and wildfire research. The forest experiment was conducted on a 16 × 22 m plot with line ignition using a gasoline‐diesel mix. Fire spread was documented with drone‐based video and infrared imaging. Ninety‐six thermocouples and two gas sensors were mounted on trees, and a mobile FTIR spectrometer enabled real‐time smoke analysis. A tilled and foam‐treated strip prevented uncontrolled spread. Under stable weather conditions (23°C, light wind, low soil moisture), a consistent temperature rise and distinct combustion phases were observed. Smoldering dominated in areas with mosses, grasses, and deadwood, with intermittent flaming, limited flame heights (< 0.5 m), and substantial smoke production. Peak temperatures exceeded 500°C, and CO concentrations reached 238 ppm, though wind turbulence complicated gas sampling. The second experiment on a cut agricultural field near Nauen involved burning approximately 700 m2 using a 20 m ignition line aligned with wind direction. Drone‐based infrared monitoring captured rapid spread on the stubble surface. The results underscore the variability and measurement challenges of outdoor fires and highlight the necessity of continued large‐scale experiments to support physical and numerical wildfire modeling. These findings provide essential empirical data for evaluating vegetation‐specific burning behavior, improving sensor deployment strategies, and refining validation approaches for next‐generation wildfire spread models under central European fuel and weather conditions, and supporting decision‐making in wildfire management. KW - Wildfire KW - Pine KW - Crop PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-654199 DO - https://doi.org/10.1002/fam.70045 SN - 0308-0501 SP - 1 EP - 11 PB - Wiley AN - OPUS4-65419 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hahn, Sarah‐K. A1 - Gnutzmann, Tanja A1 - Meinert, Marion A1 - Hofmann-Böllinghaus, Anja A1 - Oberhagemann, Dirk A1 - Krause, Ulrich T1 - Incipient Fires—Definition, Detection and Extinguishment by Laypersons N2 - The earlier a fire is noticed, the less developed it is and the easier it can be prevented respectively stopped, even by laypersons. Within the research project ‘TEBRAS’ the incipient phase of fires was investigated in detail. In the course of the project, it became apparent that the definition of what exactly the incipient phase of a fire encompasses is not definite and depends on the disciplines dealing with the subject ‘fire’. Based on the results of a literature review, an inquiry under experts and laypersons as well as practical fire tests a definition for the phenomenon of the incipient fire was developed which divides it into four phases. Driving key factors for each phase are identified considering the main parameters to detect and extinguish the fire. KW - Developing fires KW - Development of fires PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-649310 DO - https://doi.org/10.1002/fam.70025 SN - 0308-0501 VL - 50 IS - 1 SP - 3 EP - 10 PB - Wiley AN - OPUS4-64931 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wagner, Jan A1 - Häfner, P. A1 - Reimann, H.-A. A1 - Schartel, Bernhard T1 - Valorization of Natural Fibers in Flame Retarded Poly(lactic acid) N2 - Extensive research has explored natural fiber reinforced composites, typically focusing on a single fiber within a polymer matrix. Comprehensive comparisons across different natural fibers in the same polymer, which are critical for industrial material selection, remain limited. This work presents a systematic comparison of untreated hemp, flax, and sisal fibers incorporated at varying fiber lengths and loadings into flame retarded poly(lactic acid) (PLA). Fire behavior, thermal, and mechanical responses were investigated through thermogravimetry, UL 94, and cone calorimetry, alongside crystallinity, molecular weight (MW), and microstructural analysis. Fiber incorporation reduced the peak heat release rate (pHRR) by up to 30 % in 30 wt% hemp, attributed to protective layer formation, but increased flammability in UL 94. A phytic acid melamine salt combined with expandable graphite and 20 wt% hemp produced incomplete combustion at 50 kW/m², raising char residue from 4 to 24 wt% and halving pHRR. Petrella plots revealed that fiber addition alone lowered fire load and flashover propensity as effectively as phytic acid melamine; with hemp, phytic acid and expendable graphite, the flashover hazard and fire load were halved. MW was preserved while crystallinity and modulus increased with fiber content. Hemp delivered the most consistent reinforcement, while optimized processing enabled flax and sisal to improve stiffness. Performance gains were strongest when individual fibers were dispersed via optimized processing, preventing bundle fracture under load. Plasma modification of the fibers improved the maximum tensile strength in the composites. A practical guide is provided for valorizing natural fibers in PLA composites, demonstrating routes to bio-based, compostable materials with improved fire safety and mechanical performance suitable for industrial processing. KW - Poly(lactic acid) KW - Hemp KW - Sisal KW - Flax KW - Flame retardant KW - Phytic acid PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-653038 DO - https://doi.org/10.1016/j.mtcomm.2025.114575 SN - 2352-4928 VL - 50 SP - 1 EP - 41 PB - Elsevier Ltd. AN - OPUS4-65303 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Vega Puga, E. A1 - Wachtendorf, Volker A1 - Kömmling, Anja A1 - Brendelberger, S. A1 - Jaunich, Matthias A1 - Sattler, C. T1 - Lifetime prediction and degradation assessment of FKM and FFKM O-rings under high temperature thermo-oxidative ageing N2 - To support the development of solar reactor technologies for hydrogen production, this study investigates the thermo-oxidative degradation mechanisms of fluorinated elastomers and predicts their lifetimes at high temperatures (200–300 ◦C) consistent with the application requirements. An accelerated ageing programme is conducted with FKM and FFKM O-rings and flat samples for up to 21 days. Optical microscopy is used to analyse the exposed seals’ morphological changes, while IR microscopy is utilised to investigate the underlying chemical degradation mechanisms of both elastomers. Findings suggest that FKM’s degradation arises from dehydrofluorination of the polymer, followed by chain scission and backbone cleavage as a result of the oxidation of newly formed C=C double bonds. FFKM’s degradation is primarily associated with chain scission, but there is also indication that post-curing processes may occur during material ageing. Furthermore, hardness, equilibrium compression set (CS), continuous compression stress relaxation (CSR) and leakage rate tests are used to evaluate changes in the mechanical properties and sealing performance of the elastomers. Equilibrium CS data is extrapolated using time-temperature shifts (TTS) and used to derive an end-of-life criterion of 75 % equilibrium CS, which correlates to leakage rates higher than a predetermined threshold. Service lifetime predictions of FKM and FFKM O-rings at several temperatures are performed and a seal operating temperature of 200 ◦C is suggested, which ensures reasonable O-ring replacement intervals of more than half a year in the solar reactor for both considered materials. KW - Fluoroelastomer KW - Perfluoroelastomer KW - Thermo-oxidative ageing KW - Lifetime prediction KW - Compression set PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-630112 DO - https://doi.org/10.1016/j.polymertesting.2025.108820 SN - 1873-2348 VL - 147 SP - 1 EP - 17 PB - Elsevier BV CY - Amsterdam AN - OPUS4-63011 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias T1 - Comparison of Ageing Behavior of O-Ring Seals Under Hydrogen and Air N2 - Elastomeric seals are essential components in the infrastructure which prevent leakage of gas and ensure proper function of technical devices and are therefore highly safety relevant. For proper function a remaining resilience and tolerance to pressure changes is required. The ageing of elastomers is an undesirable but inevitable process leading to a limited lifetime of rubber products such as seals. Independent of the application, as e.g. automotive, piping or container applications, a long lifetime or at least a timely exchange of a seal before occurrence of critical failure is desired. Hydrogen is a key element for the energy turnaround and therefore the compatibility of seals with hydrogen is essential. In addition to the effect of hydrogen uptake and release, which might also cause destructive effects such as rapid gas decompression, ageing at high temperature under hydrogen atmosphere is of interest too. Most of the existing work is addressing the performance of new materials and comprises only very limited investigations concerning long-term use and the behaviour of aged materials in contact with hydrogen. As ageing can lead to substantial changes of material properties, it must be evaluated whether these changes are beneficial or deteriorating for the component function. In this work we present and compare results of the characterization of three sealing materials (EPDM, HNBR, FKM) after ageing at high temperature under hydrogen and air. Despite the common assumption that ageing under hydrogen atmosphere should be less severe for the material in comparison to air ageing, this is not the case for every material. T2 - ASME PVP2025, Pressure Vessels & Piping Conference CY - Montreal, Canada DA - 20.07.2025 KW - Aging KW - Seal KW - Compression set KW - Atomic force microscopy PY - 2025 AN - OPUS4-63888 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias T1 - Elastomerdichtungen für Wasserstoffanwendungen - Vergleich des Alterungsverhaltens in Luft und Wasserstoff N2 - In diesem Beitrag soll ein Fokus auf das Alterungsverhalten von Elastomerdichtungen unter Wasserstoff gelegt werden. Hierfür wurden Untersuchungen bei einem mittleren Wasserstoffdruck über Alterungszeiten von bis zu 100 Tagen durchgeführt. Das Alterungsverhalten wird im Vergleich der Alterungseffekte unter thermooxidativen Bedingungen betrachtet und bewertet. Die Annahme, dass der Alterungseffekt unter Wasserstoff stets weniger ausgeprägt ist als an Luft bestätigt sich nicht durch die Ergebnisse. T2 - 4. O-Ring-Forum der Firma ISGATEC CY - Bad Schönborn, Germany DA - 15.05.2025 KW - Wasserstoff KW - Dichtung KW - Thermische Alterung KW - Elastomer PY - 2025 AN - OPUS4-63135 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schilling, Markus A1 - Marschall, Niklas A1 - Niebergall, Ute A1 - Wachtendorf, Volker A1 - Böhning, Martin T1 - Unveiling Effects of Biodiesel and Diesel on Environmental Stress Cracking of PE-HD N2 - The behavior of high‐density polyethylene with respect to resistance against environmental stress cracking (ESC) is usually regarded as an inherent material property being specific for respective types of PE‐HD and tested using standardized methods, conditions, and also standard testing liquids (usually aqueous surfactant solutions). On the other hand, for practical applications the ESC behavior of those polymeric materials, commonly used for pipes or containers, in contact with other liquids (e.g., fuels) is often of relevant interest, but for a reasonable assessment, where consistent benchmark data for a direct comparison are often missing, it is essential to determine the actually prevailing failure mode and classify it related to crack propagation or other mechanisms. Using the well‐established Full Notch Creep Test, which favorably allows for a detailed microscopic fracture surface analysis after failure, the behavior of two typical PE‐HD types for container applications is investigated in biodiesel and diesel and compared to a standard surfactant solution. This enables a clear identification of characteristic features of the interaction of biodiesel and diesel as sorptive fuels in contact with the polymer, revealing the complex interplay of sorption and plasticization as well as ESC inducing effects on PE‐HD, which could be clearly shown for both fuels. KW - Biodiesel KW - Confocal laser scanning microscopy (LSM) KW - Diesel KW - Full notch creep test (FNCT) KW - Plasticization PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-650525 DO - https://doi.org/10.1002/pen.70239 SN - 0032-3888 SP - 1 EP - 16 PB - Wiley CY - Hoboken (NJ) AN - OPUS4-65052 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dudziak, Mateusz A1 - Dural, Esra A1 - Dey, R. A1 - Ullrich, M. S. A1 - Huth, Christian A1 - Thomson, C. A1 - Schartel, Bernhard T1 - Together We Can: Synergistic Flame Retardancy by Melamine Polyphosphate and Phosphorylated Microalgae in Polylactide Biocomposites N2 - A strategy for enhancing the sustainable flame retardancy of polylactide (PLA) composites by partially replacing melamine polyphosphate (MPP), a commercial flame retardant proposed for PLA, with wastewater polyphosphate-enriched microalgae (P-Algae) has been explored. The incorporation of P-Algae at a 1:1 ratio with MPP leads to a notable synergistic effect, surpassing the expected additive behavior of the individual components. Comprehensive characterization encompassing thermogravimetric analysis coupled with FTIR, pyrolysis combustion flow calorimeter (PCFC), cone calorimeter, oxygen index (LOI), UL-94 tests, and rheological measurements—demonstrates that the presence of this biomaterial can significantly enhance flame retardant performance. Replacing 50% of MPP with P-Algae in PLA resulted in a 17% reduction in peak heat release rate (pHRR) and maintained a V-0 rating in UL-94 testing. The use of P-Algae does not compromise the flame retardancy of PLA but rather contributes positively, offering a promising path toward more sustainable flame-retardant systems. By leveraging naturally derived biomass, this approach aligns with the growing demand for novel eco-friendly technologies in polymer engineering. Insights into an innovative renewable additive as a functional and effective component in flame-retardant biocomposites have been achieved. KW - Flame retardancy KW - Melamine polyphosphate KW - Phosphorus- enriched microalgae KW - Polylactide PLA KW - Synergism PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-640539 DO - https://doi.org/10.1002/pat.70350 SN - 1099-1581 SN - 1042-7147 VL - 36 IS - 9 SP - e70350 PB - John Wiley & Sons Ltd. AN - OPUS4-64053 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klippel, A. A1 - Hofmann-Böllinghaus, Anja A1 - Piechnik, K. A1 - Gnutzmann, Tanja T1 - Development of toxicity assessment method for bus interior materials N2 - In recent years, fire safety requirements for bus interior materials have been increased and introduced into international regulations. Fire safety requirements for the burning rate, melting and dripping behaviour of interior materials already exist for many years. However, it remains unclear to what extent the release of smoke, combustion products and their toxicity should be limited. Therefore, a research and development project 82.0723 funded by BASt (Federal Highway Research Institute) was initiated to develop a simplified procedure for testing the toxicity and smoke development in case of fire of interior materials used in buses. The scope of the research included calculations to assess the toxicity of fire gases and the derivation of specifications for the formation of practicable limit values for smoke toxicity. Further investigations are needed to derive these limit values for smoke toxicity in order to be applicable for real fire scenarios in buses. T2 - Conference Fire in Vehicles FIVE CY - Stavanger, Norway DA - 24.04.2023 KW - Bus materials PY - 2023 SP - 80 EP - 90 AN - OPUS4-57627 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Manes, M. A1 - El Houssami, M. A1 - Campbell, R. A1 - Sauca, A. A1 - Rush, D. A1 - Hofmann-Böllinghaus, Anja A1 - Andersson, P. A1 - Wagner, P. A1 - Veeneklaas, J. A1 - van Hees, P. A1 - Guillaume, E. T1 - Closing Data Gaps and Paving the Way for Pan-European Fire Safety Efforts: Part I—Overview of Current Practices for Fire Statistics N2 - The analysis of the current state of fire statistics and data collection in Europe and other countries is needed to increase awareness of how fire incidents affect buildings and to support pan-European fire prevention and fire mitigation measures. The terminology and data collected regarding fire incidents in buildings in the EU Member States were mapped to obtain meaningful datasets to determine common terminology, collection methodology, and data interpretation system. An extensive literature review showed that fire data collection systems have been instrumental in informing firefighting strategies, evidence-based planning, prevention, and educational programmes. Differences and similarities between fire data collection systems were also investigated. The amount and quality of the information in fire statistical recording systems appear to be influenced by the complexity and structure with which the data are collected. The analysis also examined the existing fire statistics in the EU Member States and a few other countries. Finally, a detailed investigation of the number of fires, fire deaths, and injuries from 2009 to 2018 in several countries was examined based on data from a report by CTIF. The trends showed differences attributable to the existing fire statistical practices in terms of terminology and data collection, and interpretation. Part II proposes a common terminology for selected fire statistical variables. The results provide relevant information regarding fire safety at the European level and should be used to guide the development of more uniform fire statistics across Europe. KW - Fire statistics KW - European project PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-575711 DO - https://doi.org/10.1007/s10694-023-01415-6 SN - 1572-8099 SP - 1 EP - 44 PB - Springer CY - Heidelberg AN - OPUS4-57571 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - El Houssami, M. A1 - Försth, M. A1 - Fredriksson, H. A1 - Drean, V. A1 - Guillaume, E. A1 - Hofmann-Böllinghaus, Anja A1 - Sandinge, A. T1 - Fire safety of interior materials of buses N2 - This study provides an analysis on the fire safety of passengers and the fire protection of coaches and buses. A brief review of major bus fire incidents, an overview of current regulations in Europe, and their limitations are presented. The study finds that the current small-scale fire test methods described in UN ECE Reg No. 118 need to be replaced by test methods that can assess the reaction to fire of materials when exposed to ignition sources of varying sizes. To address these shortcomings, the study proposed an expert recommendation to update the material fire safety requirements and testing for buses. Additional measures are proposed, derived from objectives and strategies applied in other transport sectors, and can be tested through existing European and international standards, which are widely used by several industries. These measures aim to extend the time with tenable conditions for a safe evacuation in case of fire, reduce the degree of damage to buses, reduce the risk for fast and excessive thermal exposure on modern energy carriers needed for a more sustainable transport sector. KW - Fire KW - Bus interior materials KW - Rregulations PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-575700 DO - https://doi.org/10.1002/fam.3134 SN - 1099-1018 SP - 1 EP - 15 PB - Wiley CY - London AN - OPUS4-57570 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Piechnik, Kira A1 - Heydick, Lukas A1 - Hofmann-Böllinghaus, Anja A1 - Klippel, Andrea T1 - Comprehensive laboratory study on smoke gases during the thermal oxidative decomposition of forest and vegetation fuels N2 - AbstractThis study investigates the composition of smoke gases in forest and vegetation samples to draw conclusions about the actual smoke gas composition during wildfires. The focus is particularly on regions with extensive pine forests, like in Eastern Germany. The relevance of smoke gases is well illustrated by the example of wildfires in Québec, influencing air quality in New York, in 2023. By employing a modified DIN tube furnace, a bench‐scale test set‐up, the research emphasizes the examination of smoke composition from tree species and ground cover, prioritizing gases while disregarding particles. Key smoke gases are identified as CO, CO2, SO2, HCN, C3H4O (acrolein) and CH2O (formaldehyde) and their concentrations are compared with Acute Exposure Guideline Levels (AEGL) limits. Acknowledging the limitations of AEGL usage and the problem with direct quantitative comparison of toxicant concentrations (cf. ISO 29903‐1:2020), the study highlights variations in smoke composition across different samples. The results of the studies reveal a significant disparity in CO concentration between dry and fresh pine needles. Frequently, the AEGLs of key gases are exceeded significantly. The elemental analysis of the barks indicates distinct differences in composition, reflecting in the concentrations of smoke gases. The ratio of 1 mole of substance turnover to the identified key components will be used to determine input parameters for the subsequent numerical simulation. KW - Forest KW - Wildfire KW - Ignition PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-617744 DO - https://doi.org/10.1002/fam.3253 SP - 1 EP - 12 PB - Wiley online library AN - OPUS4-61774 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wu, Hongyi A1 - Buhk, Frederik A1 - Christiani, Ricardo A1 - Hofmann-Böllinghaus, Anja T1 - Influence of local vegetation on ignition and fire spread of vegetation fires-Experimental and numerical approach N2 - Within the framework of the European TREEADS project, Brandenburg and Saxony-Anhalt were designated as model regions. This designation facilitated the investigation of vegetation types, soil structure, and soil dryness. Brandenburg and Saxony-Anhalt are identified as the driest regions in Germany according to the annual mean soil moisture data. In these regions, 48% to 73% of the forests are composed of pine species. The soil profile is characterized by a relatively thin organic layer, measuring between 0.2 and 0.3 meters, underlain by sandy substrates. Consequently, surface and ground fires are more prevalent in these areas compared to other types of fires, such as crown fires. To investigate the influence of local vegetation, it goes through two aspects. One is laboratory study, the local vegetation samples were collected and tested for the thermal properties, such as activation energy, heat content and reaction kinetic of pyrolysis and dehydration. At the same time, small and medium scale combustion experiments were conducted to investigate the burning behavior. The other aspect is using the thermal properties as the input parameters for the development of numerical simulation in the computational fluid dynamics (CFD) tool. These models were then be validated with the combustion experiments, as a baseline for the further scaling up of the models, in order to investigate how the parameters influencing the fire spread in a large-scale case numerically. T2 - Interflam 2025, 16th International Fire Science and Engineering Conference CY - London, United Kingdom DA - 30.06.2025 KW - Wildfire PY - 2025 SP - 2221 EP - 2225 PB - Interscience CY - London AN - OPUS4-63932 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -