TY - JOUR A1 - Gluth, Gregor A1 - Mundra, Shishir A1 - Henning, Ricky T1 - Chloride binding by layered double hydroxides (LDH/AFm phases) and alkali-activated slag pastes: an experimental study by RILEM TC 283-CAM N2 - Chloride binding by the hydrate phases of cementitious materials influences the rate of chloride ingress into these materials and, thus, the time at which chloride reaches the steel reinforcement in concrete structures. Chloride binding isotherms of individual hydrate phases would be required to model chloride ingress but are only scarcely available and partly conflicting. The present study by RILEM TC 283-CAM ‘Chloride transport in alkali-activated materials’ significantly extends the available database and resolves some of the apparent contradictions by determining the chloride binding isotherms of layered double hydroxides (LDH), including AFm phases (monosulfate, strätlingite, hydrotalcite, and meixnerite), and of alkali-activated slags (AAS) produced with four different activators (Na2SiO3, Na2O·1.87SiO2, Na2CO3, and Na2SO4), in NaOH/NaCl solutions at various liquid/solid ratios. Selected solids after chloride binding were analysed by X-ray diffraction, and thermodynamic modelling was applied to simulate the phase changes occurring during chloride binding by the AFm phases. The results of the present study show that the chloride binding isotherms of LDH/AFm phases depend strongly on the liquid/solid ratio during the experiments. This is attributed to kinetic restrictions, which are, however, currently poorly understood. Chloride binding by AAS pastes is only moderately influenced by the employed activator. A steep increase of the chloride binding by AAS occurs at free chloride concentrations above approx. 1.0 M, which is possibly related to chloride binding by the C–(N–)A–S–H gel in the AAS. KW - Chloride binding KW - Sorption isotherm KW - Layered double hydroxide KW - AFm phase KW - Alkali-activated materials PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-599370 DO - https://doi.org/10.1617/s11527-024-02311-3 SN - 1359-5997 SN - 1871-6873 VL - 57 IS - 4 SP - 1 EP - 17 PB - Springer Nature AN - OPUS4-59937 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tambara, R. F. A1 - Durlo Tambara, Luís Urbano A1 - Venquiaruto, S. D. A1 - Pereira da Costa, F. B. T1 - Evaluation of the mechanical performance and capillary absorption of concretes with incorporation of crystallizing admixtures and subjected to damage at early ages T1 - Avaliação do desempenho mecânico e absorção capilar de concretos com incorporação de aditivos cristalizante submetidos a danos nas primeiras idades N2 - This study assessed the self-healing phenomenon in the mechanical properties and capillary absorption of structural concretes. Two crystalline powder additives were evaluated, dosed according to the manufacturers’ recommendations. Crystalline additives increase the density of the C-S-H gel and form insoluble crystals, effectively blocking fissures. Three concrete mixes were produced: a reference mix, additive-X with 0.8%, and additive-Y with 2.0%, relative to the mass of cement. 75% of the rupture load was applied at 3- and 14-days to induce microfissures for comparison with the reference mix. Subsequently, self-healing was assessed at 28- and 76-days. The property of axial compressive strength was determined at 28-days, revealing that crystalline additives contributed to an average increase of 12% in this property. While the age of loading did not significantly impact axial compressive strength, there were significant variations among the types of additives studied, as indicated by ANOVA. Water absorption properties through capillarity were evaluated at 28- and 76-days, showing an average reduction of 42% in water absorption due to the use of crystalline additives. In conclusion, the inclusion of crystalline additives positively contributed to the self-healing of the studied concretes, suggesting a partial recovery of microfissures. N2 - Esta pesquisa avaliou o fenômeno de autocicatrização nas propriedades mecânicas e absorção capilar de concretos estruturais. Foram avaliados dois aditivos cristalizantes em pó, dosados de acordo com o teor recomendado pelos fabricantes. Aditivos cristalizantes aumentam a densidade do gel C-S-H e formam cristais insolúveis, bloqueando fissuras. Três traços de concreto foram produzidos: referência, aditivo-X com 0,8% e aditivo-Y com 2,0% em relação a massa do cimento. Aplicou-se 75% da carga de ruptura aos 3- e 14-dias para gerar microfissuras e comparar com a referência. Posteriormente, a autocicatrização foi avaliada aos 28- e 76-dias. A propriedade de resistência à compressão axial foi determinada aos 28-dias, revelando que os aditivos cristalizantes contribuíram para um aumento médio de 12% desta propriedade. A idade do carregamento dos concretos não apresentou um impacto significativo na resistência à compressão axial, mas apontou resultados significativos entre os tipos de aditivos estudados, conforme ANOVA. As propriedades de absorção de água por capilaridade foram avaliadas aos 28- e 76-dias, indicando uma redução de absorção de água média de 42% devido ao uso dos aditivos cristalizantes. Em conclusão, a incorporação dos aditivos cristalizantes contribuiu de maneira positiva para a autocicatrização dos concretos estudados, indicando uma recuperação parcial das microfissuras. KW - Self-healing KW - Crystalline admixture KW - Concrete KW - Cracks PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-599140 DO - https://doi.org/10.1590/1517-7076-RMAT-2023-0355 SN - 1517-7076 VL - 29 IS - 1 SP - 1 EP - 20 CY - Rio de Janeiro AN - OPUS4-59914 LA - por AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Licht, M. A1 - Nikoonasab, Ali A1 - Gluth, Gregor A1 - Raupach, M. ED - Claßen, M. ED - Hegger, J. ED - Matschei, T. ED - Raupach, M. T1 - Alkali-aktivierte Hüttensandbetone – CO2-reduzierte Bindemittel mit hohem Korrosionsschutzpotential N2 - Durch den Ersatz von Portlandzement können alkali-aktivierte Bindemittel einen bedeutenden Beitrag zur Verringerung der durch die Zementklinkerherstellung verursachten CO2-Emissionen leisten. Für die Verwendung von alkali-aktivierten Bindemitteln in Stahlbetonkonstruktionen, die Chloriden oder Carbonatisierung ausgesetzt sind, ist die Fähigkeit des Stahls, den passiven Zustand zu erreichen und aufrechtzuerhalten, von großer Bedeutung. Die Prozesse der Deckschichtbildung von Stahl in alkali-aktivierten Materialien unterscheiden sich jedoch zum Teil grundlegend von denen in Portlandzementen. Alkali-aktivierte Hüttensandbetone weisen gute technische Eigenschaften auf, bisher fehlen jedoch grundlegende Kenntnisse bzgl. ihrer schützenden Wirkung bei korrosiven Angriffen. Dies ist vor allem auf ihre sulfidhaltige Porenlösung zurückzuführen, welche die elektrochemischen Eigenschaften der Stahloberfläche beeinflusst und die Verwendung herkömmlicher Bewertungsmaßstäbe erschwert. Es werden erste Ergebnisse eines DFG-Forschungsprojektes vorgestellt, in dem das Passivierungsverhalten von Stahl in alkali-aktivierten Hüttensandmörteln unterschiedlicher Zusammensetzungen sowie in Mörteln auf Basis hüttensandhaltiger Normzemente untersucht wird. Über einen Zeitraum von mindestens 28 Tagen werden an Zylinderprüfkörpern im 3-Elektroden-Aufbau das Ruhepotential sowie die Polarisationswiderstände der Stahlelektroden ermittelt. T2 - 10. DAfStb-Jahrestagung mit 62. Forschungskolloquium CY - Aachen, Germany DA - 26.09.2023 KW - Bewehrung KW - Stahlkorrosion KW - Hüttensandmehl KW - Sulfid PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-593775 DO - https://doi.org/10.18154/RWTH-2023-06676 SP - 233 EP - 238 PB - RWTH Aachen CY - Aachen AN - OPUS4-59377 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mittermayr, F. A1 - Gluth, Gregor A1 - Grengg, C. A1 - Garbe, U. A1 - Jiang, G. ED - Jiang, G. T1 - Concrete corrosion characterization using advanced microscopic and spectroscopic techniques N2 - The aim of this chapter is to give an overview of basic and advanced state-of-the-art microstructural and spectroscopic analytics to investigate inorganic material corrosion in the context of biochemically aggressive sewers. The chapter covers optical methods, electron beam, X-ray and neutron techniques (SEM, MLA, XRF, XRD, CT, Neutron radiography and tomography), and spectroscopic methods (MAS-NMR, FT-IR, and Raman). For each technique, a short section on the fundamental scientific background of the method precedes and examples of data output from the latter in respect to the corrosion of cementitious materials including reinforced concrete is presented. KW - Cement KW - Concrete KW - Deterioration KW - Spectroscopy KW - Microscopy PY - 2023 SN - 978-3-031-29940-7 SN - 978-3-031-29941-4 DO - https://doi.org/10.1007/978-3-031-29941-4_4 SP - 59 EP - 97 PB - Springer CY - Cham AN - OPUS4-57423 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Winnefeld, F. A1 - Gluth, Gregor A1 - Bernal, S. A. A1 - Bignozzi, M. C. A1 - Carabba, L. A1 - Chithiraputhiran, S. A1 - Dehghan, A. A1 - Dolenec, S. A1 - Dombrowski-Daube, K. A1 - Dubey, A. A1 - Ducman, V. A1 - Yu, J. A1 - Peterson, K. A1 - Stephan, D. A1 - Provis, J. L. T1 - RILEM TC 247-DTA round robin test: sulfate resistance, alkali-silica reaction and freeze–thaw resistance of alkali-activated concretes N2 - The RILEM technical committee TC 247-DTA ‘Durability Testing of Alkali-Activated Materials’ conducted a round robin testing programme to determine the validity of various durability testing methods, originally developed for Portland cement based-concretes, for the assessment of the durability of alkali-activated concretes. The outcomes of the round robin tests evaluating sulfate resistance, alkali-silica reaction (ASR) and freeze–thaw resistance are presented in this contribution. Five different alkali-activated concretes, based on ground granulated blast furnace slag, fly ash, or metakaolin were investigated. The extent of sulfate damage to concretes based on slag or fly ash seems to be limited when exposed to an Na2SO4 solution. The mixture based on metakaolin showed an excessive, very early expansion, followed by a dimensionally stable period, which cannot be explained at present. In the slag-based concretes, MgSO4 caused more expansion and visual damage than Na2SO4; however, the expansion limits defined in the respective standards were not exceeded. Both the ASTM C1293 and RILEM AAR-3.1 test methods for the determination of ASR expansion appear to give essentially reliable identification of expansion caused by highly reactive aggregates. Alkali-activated materials in combination with an unreactive or potentially expansive aggregate were in no case seen to cause larger expansions; only the aggregates of known very high reactivity were seen to be problematic. The results of freeze–thaw testing (with/without deicing salts) of alkali-activated concretes suggest an important influence of the curing conditions and experimental conditions on the test outcomes, which need to be understood before the tests can be reliably applied and interpreted. KW - Alkali-activated materials KW - Sulfate attack KW - Alkali silica reaction KW - Alkali aggregate reaction KW - Freeze-thaw attack PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-515527 DO - https://doi.org/10.1617/s11527-020-01562-0 VL - 53 IS - 6 SP - 140 PB - Springer Nature AN - OPUS4-51552 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mundra, Shishir A1 - Provis, J. L. T1 - Mechanisms of passivation and chloride-induced corrosion of mild steel in sulfide-containing alkaline solutions N2 - The pore fluid within many concretes is highly alkaline and rich in reduced sulfur species, but the influence of such alkaline-sulfide solutions on the surface film formed on steel reinforcement is poorly understood. This study investigates the critical role of HS− in defining mild steel passivation chemistry. The surface film formed on the steel in alkaline-sulfide solutions contains Fe(OH)2 and Fe–S complexes, and the critical chloride concentration to induce corrosion increases at high sulfide concentration. However, this behavior is dependent on the duration of exposure of the steel to the electrolyte, and the nature of the sulfidic surface layer. KW - Alkali-activated materials KW - Steel corrosion KW - Sulfide KW - Chloride PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-528861 DO - https://doi.org/10.1007/s10853-021-06237-x VL - 56 IS - 26 SP - 14783 EP - 14802 PB - Springer Nature AN - OPUS4-52886 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gluth, Gregor A1 - Arbi, K. A1 - Bernal, S. A. A1 - Bondar, D. A1 - Castel, A. A1 - Chithiraputhiran, S. A1 - Dehghan, A. A1 - Dombrowski-Daube, K. A1 - Dubey, A. A1 - Ducman, V. A1 - Peterson, K. A1 - Pipilikaki, P. A1 - Valcke, S. L. A. A1 - Ye, G. A1 - Zuo, Y. A1 - Provis, J. L. T1 - RILEM TC 247-DTA round robin test: carbonation and chloride penetration testing of alkali-activated concretes N2 - Many standardised durability testing methods have been developed for Portland cement-based concretes, but require validation to determine whether they are also applicable to alkali-activated materials. To address this question, RILEM TC 247-DTA ‘Durability Testing of Alkali-Activated Materials’ carried out round robin testing of carbonation and chloride penetration test methods, applied to five different alkali-activated concretes based on fly ash, blast furnace slag or metakaolin. The methods appeared overall to demonstrate an intrinsic precision comparable to their precision when applied to conventional concretes. The ranking of test outcomes for pairs of concretes of similar binder chemistry was satisfactory, but rankings were not always reliable when comparing alkali-activated concretes based on different precursors. Accelerated carbonation testing gave similar results for fly ash-based and blast furnace slag-based alkali-activated concretes, whereas natural carbonation testing did not. Carbonation of concrete specimens was observed to have occurred already during curing, which has implications for extrapolation of carbonation testing results to longer service life periods. Accelerated chloride penetration testing according to NT BUILD 443 ranked the tested concretes consistently, while this was not the case for the rapid chloride migration test. Both of these chloride penetration testing methods exhibited comparatively low precision when applied to blast furnace slag-based concretes which are more resistant to chloride ingress than the other materials tested. KW - Alkali-activated materials KW - Durability KW - Carbonation KW - Chloride penetration KW - Concrete PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-504045 DO - https://doi.org/10.1617/s11527-020-1449-3 SN - 1359-5997 SN - 1871-6873 VL - 53 IS - 1 SP - 21 PB - Springer Nature AN - OPUS4-50404 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Simon, Sebastian A1 - Gluth, Gregor ED - Rossignol, S. ED - Gluth, Gregor T1 - Unraveling the hardening mechanism during laser-induced slip casting of lithium aluminate-microsilica slurry N2 - Additive manufacturing (AM) of alkali-activated materials is a promising method for producing ceramic precursors, construction elements and other parts. A recently introduced AM process is laser-induced slip casting of lithium aluminate/microsilica slurries, which yields parts with excellent mechanical strengths. To clarify the underlying mechanisms, μ-Raman spectroscopy was applied to parts produced by the process, and the dissolution and hydration of lithium aluminate was studied inter alia using conventional and in-situ X-ray diffraction. The results show that significant dissolution of lithium aluminate occurs, particularly at increased temperatures during laser interaction, which leads to an increase of pH and precipitation of an akopovaite-like Li-Al-CO3 layered double hydroxide. The increase of the pH is likely to induce dissolution of the microsilica and possibly formation of a hydrous lithium aluminosilicate gel. These observations explain the strength evolution of the studied parts and can also aid the development and improvement of related AM methods. KW - Alkali-activated materials KW - Additive manufacturing KW - Laser-induced slip casting KW - Lithium KW - Layered double hydroxide PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-520557 DO - https://doi.org/10.1016/j.oceram.2021.100060 SN - 2666-5395 VL - 5 IS - Special issue: Alkali-activated materials and geopolymers in ceramics and beyond SP - 1 EP - 7 PB - Elsevier CY - Amsterdam AN - OPUS4-52055 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sturm, Patrick A1 - Moye, J. A1 - Gluth, Gregor A1 - Vogler, Nico A1 - Taffe, A. A1 - Kühne, Hans-Carsten ED - Rossignol, S. ED - Gluth, Gregor T1 - Properties of alkali-activated mortars with salt aggregate for sealing structures in evaporite rock N2 - Concrete structures for sealing of tunnels in the host rock are an essential part of systems for nuclear waste storage. However, concretes based on blended cements or magnesium oxychloride cements, which are commonly considered for this application, can deteriorate severely due to a significant heat of hydration and associated deformation and cracking. Alkali-activated materials (AAMs) offer a potential solution to this problem because of their low heat release during hardening. To explore their suitability for the construction of sealing structures in evaporite rock, various AAMs with salt aggregate were studied regarding fresh properties, heat release, mechanical properties and microstructure. The heat of reaction of the AAMs was up to 55% lower than that of a blended cement designed for sealing structures, indicating significant benefits for the intended application. Other relevant properties such as mechanical strength and permeability depended strongly on the mix-design of the AAMs and curing conditions. KW - Alkali-activated materials KW - Geopolymers KW - Nuclear waste storage KW - Sealing structures KW - Evaporite rock PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-519422 DO - https://doi.org/10.1016/j.oceram.2020.100041 SN - 2666-5395 VL - 5 IS - Special issue: Alkali-activated materials and geopolymers in ceramics and beyond SP - 1 EP - 8 PB - Elsevier CY - Amsterdam AN - OPUS4-51942 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hüsken, Götz A1 - Wagner, L.-C. A1 - Gluth, Gregor A1 - Pirskawetz, Stephan A1 - Kühne, Hans-Carsten T1 - Application of Steel Fibres in Alkali-Activated Mortars N2 - Alkali-activated materials are ideal for the repair of concrete structures in harsh environmental conditions due to their high durability in chemically aggressive environments. However, slag-based mortars, in particular, are prone to shrinkage and associated cracks. In this respect, the application of steel fibres is one solution to reduce the formation of shrinkage induced cracks and to improve post cracking behaviour of these mortars. This study investigated the influence of two different types of steel fibres on the tensile properties of two alkali-activated mortars. Direct tensile tests and single fibre pull-outs were performed to analyse the determining failure modes both on macro and micro scale. Mechanical testing was accompanied by non-destructive testing methods such as digital image correlation and acoustic emission for a detailed analysis of the fracture process. T2 - Local Mechanical Properties - LMP 2019 CY - Prague, Czech Republic DA - 06.11.2019 KW - Alkali-activated materials KW - Fibre pull-out KW - Steel fibres KW - Tensile strength PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-509291 UR - https://ojs.cvut.cz/ojs/index.php/APP/article/view/6695 DO - https://doi.org/10.14311/APP.2020.27.0090 VL - 27 SP - 90 EP - 95 CY - Prague, Czech Republic AN - OPUS4-50929 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rudić, O. A1 - Mittermayr, F. A1 - Gluth, Gregor A1 - Simon, Sebastian A1 - Ukrainczyk, N. A1 - Seyrek, Y. A1 - Freytag, B. A1 - Juhart, J. A1 - Grengg, C. T1 - On the benefits of vegetable oil addition for the pore structure and acid resistance of alkali-activated systems N2 - The impact of high additions of vegetable oil (12 vol%) on the mechanical and microstructural properties of metakaolin-slag-based alkali-activated materials (AAMs) was studied. The addition of oil resulted in a slight decrease in initial polymerization kinetics but did not affect the final degree of reaction. AAM-oil-composite-mortars exhibited approximately ∼30% lower compressive strength primarily due to the entrainment of air voids. Newly formed soap phases significantly reduced the volume of small capillary and gel pores (pore radii <15 nm), leading to a decrease in specific inner surface area by a factor of up to 15. The porosity modification induced by the oil addition greatly enhanced the resistance of AAMs against sulfuric acid attack, shifting the dominant processes from diffusion and cracks to framework-dissolution controlled by the inherent phase stabilities. Following the immersion in sulfuric acid (pHstat = 2) for 8 weeks, the depth of corroded layer decreased by 70% and no cracks due to expansive phases were observed. These promising findings suggest that the incorporation of vegetable oil in AAMs has the potential to address durability concerns associated with diffusion-based corrosion processes, thereby expanding the range of future applications. KW - Alkali-activated materials KW - Acid resistance KW - Pore structure PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-581719 DO - https://doi.org/10.1016/j.ceramint.2023.08.036 VL - 49 IS - 20 SP - 33275 EP - 33290 PB - Elsevier Ltd. AN - OPUS4-58171 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mundra, S. A1 - Samson, G. A1 - Masi, G. A1 - Achenbach, R. A1 - Bastidas, D. M. A1 - Bernal, S. A. A1 - Bignozzi, M. C. A1 - Criado, M. A1 - Cyr, M. A1 - Gartner, N. A1 - von Greve-Dierfeld, S. A1 - Legat, A. A1 - Nikoonasab, Ali A1 - Provis, J. L. A1 - Raupach, M. A1 - Gluth, Gregor T1 - Application of electrochemical methods for studying steel corrosion in alkali-activated materials N2 - Alkali-activated materials (AAMs) are binders that can complement and partially substitute the current use of conventional cement. However, the present knowledge about how AAMs protect steel reinforcement in concrete elements is incomplete, and uncertainties exist regarding the application of electrochemical methods to investigate this issue. The present review by EFC WP11-Task Force ‘Corrosion of steel in alkali-activated materials’ demonstrates that important differences exist between AAMs and Portland cement, and between different classes of AAMs, which are mainly caused by differing pore solution compositions, and which affect the outcomes of electrochemical measurements. The high sulfide concentrations in blast furnace slag-based AAMs lead to distinct anodic polarisation curves, unusually low open circuit potentials, and low polarisation resistances, which might be incorrectly interpreted as indicating active corrosion of steel reinforcement. No systematic study of the influence of the steel–concrete interface on the susceptibility of steel to corrosion in AAMs is available. Less common electrochemical methods present an opportunity for future progress in the field. KW - Alkali-activated materials KW - Reinforcement corrosion KW - Steel corrrosion KW - Electrochemical methods KW - Concrete PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-572241 DO - https://doi.org/10.1002/maco.202313743 SN - 1521-4176 VL - 74 IS - 7 SP - 988 EP - 1008 PB - Wiley-VCH CY - Weinheim AN - OPUS4-57224 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Vollpracht, A. A1 - Gluth, Gregor A1 - Rogiers, B. A1 - Uwanuakwa, I. D. A1 - Phung, Q. T. A1 - Villagran Zaccardi, Y. A1 - Thiel, C. A1 - Vanoutrive, H. A1 - Etcheverry, J. M. A1 - Gruyaert, E. A1 - Kamali-Bernard, S. A1 - Kanellopoulos, A. A1 - Zhao, Z. A1 - Martins, I. M. A1 - Rathnarajan, S. A1 - De Belie, N. T1 - Report of RILEM TC 281-CCC: insights into factors affecting the carbonation rate of concrete with SCMs revealed from data mining and machine learning approaches N2 - The RILEM TC 281–CCC ‘‘Carbonation of concrete with supplementary cementitious materials’’ conducted a study on the effects of supplementary cementitious materials (SCMs) on the carbonation rate of blended cement concretes and mortars. In this context, a comprehensive database has been established, consisting of 1044 concrete and mortar mixes with their associated carbonation depth data over time. The dataset comprises mix designs with a large variety of binders with up to 94% SCMs, collected from the literature as well as unpublished testing reports. The data includes chemical composition and physical properties of the raw materials, mix-designs, compressive strengths, curing and carbonation testing conditions. Natural carbonation was recorded for several years in many cases with both indoor and outdoor results. The database has been analysed to investigate the effects of binder composition and mix design, curing and preconditioning, and relative humidity on the carbonation rate. Furthermore, the accuracy of accelerated carbonation testing as well as possible correlations between compressive strength and carbonation resistance were evaluated. One approach to summerise the physical and chemical resistance in one parameter is the ratio of water content to content of carbonatable CaO (w/CaOreactive ratio). The analysis revealed that the w/CaOreactive ratio is a decisive factor for carbonation resistance, while curing and exposure conditions also influence carbonation. Under natural exposure conditions, the carbonation data exhibit significant variations. Nevertheless, probabilistic inference suggests that both accelerated and natural carbonation processes follow a square-root-of-time behavior, though accelerated and natural carbonation cannot be converted into each other without corrections. Additionally, a machine learning technique was employed to assess the influence of parameters governing the carbonation progress in concretes. KW - Carbonation KW - Supplementary cementitious materials KW - Concrete PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-614388 DO - https://doi.org/10.1617/s11527-024-02465-0 SN - 1871-6873 SN - 1359-5997 VL - 57 IS - 9 SP - 1 EP - 33 PB - Springer Nature AN - OPUS4-61438 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lima, G. T. S. A1 - Silvestro, L. A1 - Durlo Tambara, Luís Urbano A1 - Cheriaf, M. A1 - Rocha, J. C. T1 - Autonomous Self-Healing Agents in Cementitious Materials: Parameters and Impacts on Mortar Properties N2 - The concept of self-healing materials and the development of encapsulated curing agents represent a cutting-edge approach to enhancing the longevity and reducing the maintenance costs of cementitious structures. This systematic literature review aims to shed light on the parameters involved in the autonomous self-healing of cementitious materials, utilizing various encapsulated healing agents such as pellets, granules, and capsules. This review also identifies and selects studies that offer additional insights into the efficacy of the self-healing process in cementitious materials and the influence of these specific encapsulated healing agents on the physical mechanical properties of mortars. This comprehensive approach provides a deep understanding of the interplay between self-healing and the physical–mechanical properties of mortars containing these encapsulated healing agents. The main findings indicate that the cement-to-sand ratio, characteristics of fine aggregates, and encapsulation methods significantly impact crack control, self-healing efficiency, and properties of mortar in both fresh and hardened states. The content of encapsulated healing agents within the cementitious matrix affects both the initial workability or flow and subsequent mechanical properties. While pellets coated with PVA film typically reduce workability in the fresh state and compressive strength, capsules coated with Portland cement and sodium silicate mitigate these effects and improve crack sealing in fresh and hardened states without compromising the self-healing capacity of cracks. The three-point flexural test has emerged as the preferred method for a pre-crack assessment over 28 days, with variations depending on the type of healing agent used. As noted in the literature, water has been identified as the optimal environment for autonomous healing. These findings underscore the potential of encapsulation techniques to enhance self-healing capabilities through the controlled release of agents within the cementitious matrix, thereby advancing the research on and development of intelligent construction materials and increasing the durability of cement-based structures. KW - Self-healing cementitious composite KW - Encapsulated curing agents KW - Pellets KW - Granules KW - Capsules KW - Physical–mechanical properties KW - Autonomous self-healing PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-611860 DO - https://doi.org/10.3390/buildings14072000 SN - 2075-5309 VL - 14 IS - 7 SP - 1 EP - 23 PB - MDPI CY - Basel AN - OPUS4-61186 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kazlagić, Anera A1 - Russo, Francesco A1 - Vogl, Jochen A1 - Sturm, Patrick A1 - Stephan, D. A1 - Gluth, Gregor ED - Resch-Genger, Ute ED - Koch, Matthias ED - Meermann, Björn ED - Weller, Michael G. T1 - Development of a sample preparation procedure for Sr isotope analysis of Portland cements N2 - The 87Sr/86Sr isotope ratio can, in principle, be used for provenancing of cement. However, while commercial cements consist of multiple components, no detailed investigation into their individual 87Sr/86Sr isotope ratios or their influence on the integral 87Sr/86Sr isotope ratio of the resulting cement was conducted previously. Therefore, the present study aimed at determining and comparing the conventional 87Sr/86Sr isotope ratios of a diverse set of Portland cements and their corresponding Portland clinkers, the major component of these cements. Two approaches to remove the additives from the cements, i.e. to measure the conventional 87Sr/86Sr isotopic fingerprint of the clinker only, were tested, namely, treatment with a potassium hydroxide/sucrose solution and sieving on a 11-µm sieve. Dissolution in concentrated hydrochloric acid/nitric acid and in diluted nitric acid was employed to determine the 87Sr/86Sr isotope ratios of the cements and the individual clinkers. The aim was to find the most appropriate sample preparation procedure for cement provenancing, and the selection was realised by comparing the 87Sr/86Sr isotope ratios of differently treated cements with those of the corresponding clinkers. None of the methods to separate the clinkers from the cements proved to be satisfactory. However, it was found that the 87Sr/86Sr isotope ratios of clinker and cement generally corresponded, meaning that the latter can be used as a proxy for the clinker 87Sr/86Sr isotope ratio. Finally, the concentrated hydrochloric acid/nitric acid dissolution method was found to be the most suitable sample preparation method for the cements; it is thus recommended for 87Sr/86Sr isotope analyses for cement provenancing. KW - Cement KW - Provenancing KW - Sr isotopes KW - Portland clinker KW - Dissolution PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-542239 DO - https://doi.org/10.1007/s00216-021-03821-7 SN - 1618-2642 SN - 1618-2650 VL - 414 IS - 15 (Topical collection: Analytical methods and applications in the materials and life sciences) SP - 4379 EP - 4389 PB - Springer CY - Berlin AN - OPUS4-54223 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nikoonasab, Ali A1 - Müller, Thoralf A1 - Gluth, Gregor T1 - Study of steel behavior in synthetic pore solutions of GGBFS-containing cements using EIS N2 - Steel corrosion in sulfide-containing solutions presents a challenge in a number of environments and appli¬cations, such as the kraft process, the oil and gas industry, and reinforced concrete structures. In concrete, sulfides are introduced by ground granulated blast-furnace slag (GGBFS), which is a widespread component of standard cements and which can also be utilized in the production of alkali-activated materials (AAMs). However, a knowledge gap exists concerning the compositions of pore solutions in GGBFS-containing cements, especially regarding sulfur and its various species and understanding how these sulfur species affect the surface layer and the corrosion behavior of steel in such environments. The present study employed electrochemical impedance spec¬tros-copy to study the behavior of steel in synthetic solutions representing GGBFS-containing cements and AAMs. The electrochemical behavior of steel in sulfide-containing solutions differs from that observed in ordinary Portland cement solutions, generally exhibiting lower open circuit potentials and polarization resistances in the former environments. This suggests that the criteria or standards used to assess the probability of steel corrosion in Portland cement concrete are not applicable to GGBFS-containing concrete due to differences of their pore solution compositions. T2 - International Workshop on Impedance Spectroscopy – IWIS 2024 CY - Chemnitz, Germany DA - 24.09.2024 KW - Cement KW - Ground granulated blast-furnace slag KW - Sulfide KW - Steel corrosion KW - Impedance spectroscopy PY - 2024 DO - https://doi.org/10.1109/IWIS63047.2024.10847235 SP - 44 EP - 48 PB - IEEE AN - OPUS4-61221 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nikoonasab, Ali A1 - Licht, M. A1 - Weiler, L. A1 - Achenbach, R. A1 - Raupach, M. A1 - Gluth, Gregor T1 - Pore solution compositions and redox potentials of ground granulated blast furnace slag-containing cement pastes N2 - The pore solutions of hardened ground granulated blast furnace slag (GGBFS)-containing cements differ from the pore solutions of other cements with effects on reinforcement corrosion, application of electrochemical methods and immobilisation of radioactive waste. In the present study, the pore solutions of seven different GGBFS-containing cements (alkali-activated slag, alkali-activated slag/fly ash blends, hybrid alkaline cement (HAC), CEM III/C and CEM III/B) were extracted and their elemental and sulfate concentration, pH, redox potential and conductivity were determined; a Portland cement (CEM I) pore solution was analysed analogously. The silicon and aluminium concentrations of the alkali-activated cements increased with fly ash fraction, reaching values up to 5 mM and 10 mM, respectively, and thus were considerably higher than those of the standard cements. The redox potentials of the pore solutions of the GGBFS-containing cements were in the range from −100 mV to –500 mV vs Ag/AgCl, that is considerably lower than that of the Portland cement (8–20 mV vs Ag/AgCl), with the value depending on the GGBFS fraction and whether the cements were alkali-activated or not. These results indicate that the effects of reduced sulfur species from GGBFS in cements are more pronounced in alkali-activated materials, including HAC, and increase with GGBFS fraction. KW - Alkali-activated materials KW - Ground granulated blast furnace slag KW - Sulfide KW - Redox potential KW - Pore solution PY - 2026 DO - https://doi.org/10.1680/jadcr.25.00041 SN - 1751-7605 SN - 0951-7197 VL - 38 IS - 4 SP - 238 EP - 249 PB - Emerald CY - Leeds AN - OPUS4-64619 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bernal, S. A. A1 - Angst, U. M. A1 - Provis, J. L. A1 - Thiel, C. A1 - Gluth, Gregor A1 - Villagran-Zaccardi, Y. A1 - De Belie, N. T1 - Recommendation of RILEM TC 281-CCC: RILEM CPC-18R1—guideline for measuring the carbonation depth of hardened concrete using a pH indicator solution N2 - This recommendation provides a procedure for determining the carbonation depth on the surface of concrete by applying a pH indicator. This includes definitions of carbonation, carbonation depth and carbonation front, as well as descriptions of the different pH indicator solutions that can be used. Recommendations for testing laboratory-prepared specimens and those obtained from concrete structures are also given. This involves guidelines for sample preparation and/or extraction, CO2 exposure duration, carbonation depth determination and reporting of results. A section on data interpretation is also provided, as carbonation results are used for determining durability of concrete, as well as a criterion for materials selection or for carbon uptake calculations. The new Recommendation CPC-18R1 is intended to supersede the former RILEM recommendation CPC-18, particularly when prescribed as the preferred method for evaluating and reporting carbonation depths. KW - Carbonation KW - Concrete KW - pH indicator KW - Phenolphthalein KW - Testing PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-656191 DO - https://doi.org/10.1617/s11527-026-02966-0 SN - 1359-5997 SN - 1871-6873 VL - 59 IS - 3 SP - 1 EP - 11 PB - Springer Nature AN - OPUS4-65619 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -