TY - CONF A1 - Deresse, N. E. A1 - Thiele, Marc A1 - Pirskawetz, Stephan A1 - Sarem, M. A1 - Francois, St. A1 - Verstrynge, E. T1 - Evaluation of Concrete Fatigue Damage with Elastic Wave-based Measurement Techniques N2 - The fatigue damage evolution and the fatigue life of quasi-brittle materials such as concrete are not yet completely understood. Accordingly to get better insights, researchers have recently been incorporating advanced measuring techniques in their fatigue experiments. In this research, acoustic emission techniques (AET), active ultrasonic, and deformation measurements are used to track the damage evolution of concrete samples subjected to fatigue loading. The samples are subjected to constant amplitude and stepwise fatigue loading in Brazilian splitting test set-ups. Initially, a good agreement is observed between the deformation and the ultrasonic measurements in capturing the crack propagation during Brazilian splitting tests. The three fatigue damage phases could be identified with all of the three techniques. The Phase II damage rates quantified by deformation measurements and AET in stepwise fatigue tests were used to predict the number of cycles to failure at various stress levels. The predictions were validated using the number of cycles to failure of the constant amplitude fatigue tests. T2 - 36th Conference of the European Working Group on Acoustic Emission CY - Potsdam, Germany DA - 18.09.2024 KW - Concrete KW - Acoustic emission KW - Ultrasonic testing KW - Fatigue PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-615677 DO - https://doi.org/10.58286/30228 SN - 1435-4934 VL - 29 IS - 10 SP - 1 EP - 10 PB - NDT.net AN - OPUS4-61567 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eichner, Lukas A1 - Thiele, Marc A1 - Hille, Falk A1 - Baeßler, Matthias T1 - Digitale Modellierungsprozesse in der wiederkehrenden Prüfung von Windenergieanlagen - DiMoWind-Inspect - Abschlusstreffen N2 - Dieses Dokument enthält die Präsentationsfolien des BAM-Teams beim Abschlusstreffen des Forschungsprojekts DiMoWind-Inspect. Es wurden die Arbeitspakete Datenmanagement, Referenzkennzeichnungssystem, Grundlagen der Schadensbewertung, Risikobasierte Inspektions- und Instandhaltungsplanung und Schadensdetektion mittels Risslumineszenz sowie eine abschließende Bewertung des Projekts vorgestellt. T2 - DiMoWind-Inspect - Abschlusstreffen CY - Berlin, Germany DA - 12.09.2024 KW - Building Information Modeling (BIM) KW - Referenzkennzeichnungssystem KW - Risslumineszenz (Riluminati) KW - Risikobasierte Inspektionsplanung (RBI) PY - 2024 AN - OPUS4-61054 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pirskawetz, Stephan A1 - Thiele, Marc A1 - Löhr, Manuel A1 - Loewe, Anna A1 - Degener, Sebastian A1 - Herrmann, Ralf T1 - Acoustic emission for monitoring of fatigue damage in concrete elements of wind turbine towers N2 - Wind energy has become an important player in the energy transition in Germany. Towers of onshore wind turbines are often designed as hybrid structures: the lower part is made of prestressed concrete whereas the upper part is made of steel tubes. The tall structures are permanently subjected to cyclic loads. A research project of BAM as part of the joint project WinConFat - Structure focusses on the evelopment of techniques to monitor fatigue damage evolution in the concrete part. Results of a previous project show that a combination of ultrasonic and acoustic emission testing can give an indication for critical conditions near the end of the fatigue life of the concrete. In the ongoing project acoustic emission sensors have been installed at the base and at the transition piece between concrete and steel of a hybrid wind turbine tower. Beside of acoustic emission measurement the sensor spacing allows for measuring the concrete ultrasonic velocity along the circumference in both levels. Additional measurements like strain, temperature, inclination, or acceleration allow for comparison of environmental loads and change of acoustic properties of the concrete. The paper focusses on first acoustic measurements recorded since December 2023 in comparison to operating data of the wind turbine. T2 - EWGAE2024: 36th Conference of the European Working Group on Acoustic Emission CY - Potsdam, Germany DA - 18.09.2024 KW - Concrete fatigue monitoring KW - Acoustic emission KW - Ultrasound KW - Hybrid wind turbine tower PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-612197 DO - https://doi.org/10.58286/30234 SN - 1435-4934 VL - 29 IS - 10 SP - 1 EP - 9 AN - OPUS4-61219 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ratkovac, Mirjana A1 - Gerards-Wünsche, Paul A1 - Thiele, Marc A1 - Brackrock, Daniel A1 - Stamm, Michael T1 - Detection and monitoring of the fatigue crack growth on welds – Application-oriented use of NDT methods N2 - Early detection of fatigue cracks and accurate measurements of the crack growth play an important role in the maintenance and repair strategies of steel structures exposed to cyclic loads during their service life. Observation of welded connections is especially of high relevance due to their higher susceptibility to fatigue damage. The aim of this contribution was to monitor fatigue crack growth in thick welded specimens during fatigue tests as holistically as possible, by implementing multiple NDT methods simultaneously in order to record the crack initiation and propagation until the final fracture. In addition to well-known methods such as strain gauges, thermography, and ultrasound, the crack luminescence method developed at the Bundesanstalt für Materialforschung und -prüfung (BAM), which makes cracks on the surface particularly visible, was also used. For data acquisition, a first data fusion concept was developed and applied in order to synchronize the data of the different methods and to evaluate them to a large extent automatically. The resulting database can ultimately also be used to access, view, and analyze the experimental data for various NDT methods. During the conducted fatigue tests, the simultaneous measurements of the same cracking process enabled a comprehensive comparison of the methods, highlighting their individual strengths and limitations. More importantly, they showed how a synergetic combination of different NDT methods can be beneficial for implementation in large-scale fatigue testing but also in monitoring and inspection programs of in-service structures - such as the support structures of offshore wind turbines. T2 - Fatigue Design 2023 (FatDes 2023) CY - Senlis, France DA - 29.11.2023 KW - Fatigue KW - Welded KW - NDT KW - Crack growth PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-600238 DO - https://doi.org/10.1016/j.prostr.2024.03.062 VL - 57 SP - 560 EP - 568 PB - Elsevier B.V. AN - OPUS4-60023 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thiele, Marc T1 - Monitoring an Türmen von Onshore Windenergieanlagen in Betonbauweise im Hinblick auf Ermüdung N2 - Der Beitrag stellt das Messkonzept sowie dessen Umsetzung für ein umfassendes Monitoringsystem an einer onshore Windenergieanlage mit einem Hybridturm vor. Dieses ist Bestandteil des Forschungsvorhabens Win-ConFat–Structure, welches neben der Validierung geeigneter Sensorik auch die Bewertung des Zustands und der möglichen Restlebensdauer der ermüdungsbeanspruchten Betonstruktur zum Ziel hat. Neben dem Monitoringsystem werden erste Messergebnisse aus den Betriebsdaten sowie vom Verhalten der Turmstruktur vorgestellt. T2 - 11. Jahrestagung des DAfStb mit 63. Forschungskolloquium der BAM Green Intelligent Building CY - Berlin, Germany DA - 16.10.2024 KW - Onshore Windenergieanlagen KW - Ermüdung KW - Lebensdauerbewertung KW - Monitoring KW - WinConFat PY - 2024 AN - OPUS4-61773 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thiele, Marc A1 - Herrmann, Ralf A1 - Degener, Sebastian A1 - Pirskawetz, Stephan A1 - Loewe, Anna ED - Rogge, Andreas ED - Meng, Birgit T1 - Monitoring an Türmen von Onshore Windenergieanlagen in Betonbauweise im Hinblick auf Ermüdung N2 - Der Beitrag stellt das Messkonzept sowie dessen Umsetzung für ein umfassendes Monitoringsystem an einer onshore Windenergieanlage mit einem Hybridturm vor. Dieses ist Bestandteil des Forschungsvorhabens Win-ConFat – Structure, welches neben der Validierung geeigneter Sensorik auch die Bewertung des Zustands und der möglichen Restlebensdauer der ermüdungsbeanspruchten Betonstruktur zum Ziel hat. Neben dem Monitoringsystem werden erste Messergebnisse aus den Betriebsdaten sowie vom Verhalten der Turmstruktur vorgestellt. T2 - 11. Jahrestagung des DAfStb mit 63. Forschungskolloquium der BAM Green Intelligent Building CY - Berlin, Germany DA - 16.10.2024 KW - Monitoring KW - Windenergieanlage und Hybridturm KW - Ermüdung KW - WinConFat – Structure PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-613276 SN - 978-3-9818564-7-7 SP - 286 EP - 293 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-61327 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -