TY - JOUR A1 - Thiele, Marc A1 - Pirskawetz, Stephan T1 - Analysis of damage evolution in concrete under fatigue loading by acoustic emission and ultrasonic testing N2 - The fatigue process of concrete under compressive cyclic loading is still not completely explored. The corresponding damage processes within the material structure are especially not entirely investigated. The application of acoustic measurement methods enables a better insight into the processes of the fatigue in concrete. Normal strength concrete was investigated under compressive cyclic loading with regard to the fatigue process by using acoustic methods in combination with other nondestructive measurement methods. Acoustic emission and ultrasonic signal measurements were applied together with measurements of strains, elastic modulus, and static strength. It was possible to determine the anisotropic character of the fatigue damage caused by uniaxial loading based on the ultrasonic measurements. Furthermore, it was observed that the fatigue damage seems to consist not exclusively of load parallel oriented crack structures. Rather, crack structures perpendicular to the load as well as local compacting are likely components of the fatigue damage. Additionally, the ultrasonic velocity appears to be a good indicator for fatigue damage beside the elastic modulus. It can be concluded that acoustic methods allow an observation of the fatigue process in concrete and a better understanding, especially in combination with further measurement methods. KW - Concrete KW - Fatigue KW - Damage evolution KW - Ultrasonic testing KW - Acoustic emission PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-541891 DO - https://doi.org/10.3390/ma15010341 SN - 1996-1944 VL - 15 IS - 1 SP - 341 EP - 355 PB - MDPI CY - Basel AN - OPUS4-54189 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Thibaux, Philippe A1 - Thiele, Marc A1 - Van Wittenberghe, Jeroen A1 - Baeßler, Matthias T1 - Comparison of resonance and hydraulic testing on large scale fatigue tests of welded tubular joints for offshore wind turbine foundations N2 - Jackets structures as foundations for offshore wind energy converters are efficient solutions. But these structures require the welding of a large number of joints. The design of the Jacket structures is typically driven by fatigue. Therefore, consequently the fatigue strength of the joints is a primary parameter for an optimized design. The present paper investigates if tubular joints produced by manual welding using the current techniques have an improved performance compared to the relevant standards that are applied for the design of the foundations. To investigate this, 4 full-scale tests in geometry representative of a structure were performed, 2 using a resonance method and 2 using a three-point bending method with hydraulic actuators. The results are similar, with cracks initiated early and extending extensively before failure. The results are very close to the current T-curve from DNV RP-C203 applied for tubular joints. KW - Fatigue KW - Tubular joints KW - Resonance testing KW - Steel welds PY - 2025 DO - https://doi.org/10.1016/j.ijfatigue.2024.108797 SN - 0142-1123 VL - 193 SP - 1 EP - 16 PB - Elsevier Ltd. AN - OPUS4-62373 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hille, Falk A1 - Sowietzki, D. A1 - Makris, R. T1 - Luminescence-based early detection of fatigue cracks N2 - Classic non-destructive fatigue crack detection methods reveal the state of the fatigue damage evolution at the moment of application, generally not under operational conditions. The here introduced crack luminescence method realizes a clear visibility of the occurred and growing crack in loaded components during operation. Different established experiments show that due to the sensitive coating a crack Formation can be detected even in early stage under the premise the crack reached the surface. The coating consists of two layers with different properties and functions. The bottom layer emits light as fluorescence under UV radiation. The top layer covers the fluorescing one and prevents the emitting of light in case of no damage at the surface. In case of surface crack occurrence, the luminescent light is clearly noticeable by visual observations and also by standard camera equipment which makes automated crack detection possible as well. It is expected that crack luminescence can increase structural safety as well as reduce costs and time for inspections and preventive maintenance. KW - Coating KW - Fatigue KW - Crack damage detection KW - Luminescence PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-510517 DO - https://doi.org/10.1016/j.matpr.2020.02.338 SN - 2214-7853 SP - 1 EP - 5 PB - Elsevier CY - Amsterdam AN - OPUS4-51051 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Thibaux, Philippe A1 - Van Wittenberghe, Jeroen A1 - Fricke, Wolfgang A1 - Thiele, Marc A1 - Nielsen, Lars Peter A1 - Conti, Fabien T1 - Results of the JaCo project: fatigue strength of robot‑welded tubular joints for offshore wind energy converters N2 - Jacket foundations requires the welding of a large number of tubular joints. These foundations type is suitable to support wind energy converters in deeper water. In order to increase the production speed and its quality, robot systems were developed to produce tubular joints. Since fatigue is dominating the design of these structures, an assessment of the performance of tubular joints produced by robots was performed and compared with the performance of manually welded joints. 18 large-scale tests were performed on joints with dimensions representative for offshore structures, which were produced in industrial environment. Breakthrough cracks occurred through the chord, with cracks initiated at the weld toe, although in some cases cracks were also initiated between weld beads. The measured fatigue strengths of joints produced by robot were similar or higher than the T-curve of DNV-RP-C203. Some delivered components showed fatigue strength that was more than 20% higher than the standard curve. These results emphasize that mastering the welding process with robots is necessary to achieve superior levels of fatigue strength. KW - Fatigue KW - Tubular joint KW - Robot welding KW - Hot spot method KW - Large-scale testing PY - 2024 DO - https://doi.org/10.1007/s40194-024-01903-5 SN - 1878-6669 SP - 1 EP - 14 PB - Springer CY - Berlin ; Heidelberg AN - OPUS4-62319 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -