TY - JOUR A1 - Thiele, Marc A1 - Pirskawetz, Stephan T1 - Analysis of damage evolution in concrete under fatigue loading by acoustic emission and ultrasonic testing N2 - The fatigue process of concrete under compressive cyclic loading is still not completely explored. The corresponding damage processes within the material structure are especially not entirely investigated. The application of acoustic measurement methods enables a better insight into the processes of the fatigue in concrete. Normal strength concrete was investigated under compressive cyclic loading with regard to the fatigue process by using acoustic methods in combination with other nondestructive measurement methods. Acoustic emission and ultrasonic signal measurements were applied together with measurements of strains, elastic modulus, and static strength. It was possible to determine the anisotropic character of the fatigue damage caused by uniaxial loading based on the ultrasonic measurements. Furthermore, it was observed that the fatigue damage seems to consist not exclusively of load parallel oriented crack structures. Rather, crack structures perpendicular to the load as well as local compacting are likely components of the fatigue damage. Additionally, the ultrasonic velocity appears to be a good indicator for fatigue damage beside the elastic modulus. It can be concluded that acoustic methods allow an observation of the fatigue process in concrete and a better understanding, especially in combination with further measurement methods. KW - Concrete KW - Fatigue KW - Damage evolution KW - Ultrasonic testing KW - Acoustic emission PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-541891 DO - https://doi.org/10.3390/ma15010341 SN - 1996-1944 VL - 15 IS - 1 SP - 341 EP - 355 PB - MDPI CY - Basel AN - OPUS4-54189 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thiele, Marc A1 - Makris, Ralf ED - Aign, J. T1 - Reinforcement bar and reinforcement bar splicing systems under impact loading – Experimental tests and test specification N2 - Reinforced concrete is a widely used material for power generation structures, where load scenarios like impact loadings need to be considered. In this context mechanical splicing systems for the connection of reinforcement bars are of specific interest and impact resistance for the splicing systems has to be verified. High speed tensile tests need to be performed on splicing systems for reinforcement bars to confirm the capability of the coupler to resist impact loading. Furthermore, the ability of the reinforcement steel to dissipate energy by ductile behaviour with pronounced plastic strains should be confirmed by these tests. During the last decades comprehensive experiences were developed at BAM performing high speed tensile tests on reinforcement bars as well as on several splicing systems. For the lack of available standards defining these tests in detail an appropriate test procedure was developed and continuously optimized during this period at BAM. The test procedure is partially based on testing principles adapted from available standards. The main intention behind this test procedure is to perform high-speed tensile tests with a specific constant strain rate generated at the specimen. Furthermore, main objective was to establish a procedure to guarantee the comparability of test results for different diameter of reinforcement as well as for different types of couplers. Besides the pure execution of the high-speed tensile tests, the test specification also declares how to evaluate the measurements and the test results. Finally, some typical results will be presented in this contribution. T2 - SMIRT 26 CY - Potsdam, Germany DA - 10.07.2022 KW - Impact KW - Coupler systems KW - High-speed KW - Reinforcement PY - 2022 SP - 1 EP - 10 AN - OPUS4-55422 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schwedler, Michael A1 - Dörfeldt, Stefan A1 - Lüddecke, Falk A1 - Seidel, Marc A1 - Thiele, Marc ED - Kurrer, Karl-Eugen T1 - Einflussfaktoren auf die Vorspannkraft von Schrauben mit Durchmessern bis M72 in Ringflanschverbindungen T1 - Factors influencing the pretension force in bolts with diameter up to M72 in ring flange connections N2 - Bei Monopfahlgründungen von Offshore-Windenergieanlagen wird die Verbindung zwischen Monopfahl und Übergangsstück als geschraubter Ringflansch ausgeführt. Die zunehmende Leistungsfähigkeit der Windenergieanlagen führt zu immer größeren Schnittgrößen in diesem Anschluss. In der Folge erhöhen sich nicht nur die Querschnittsabmessungen, sondern es kommen auch zunehmend größere Schrauben zum Einsatz. Da die einschlägigen Regelwerke zur Bemessung dieser Verbindungen nicht für Schrauben der Größen M64 oder M72 konzipiert wurden, stellt sich die Frage der Übertragbarkeit auf solche Anwendungsfälle. Im Rahmen des Aufsatzes werden Einflüsse diskutiert, die eine Herabsetzung der Schraubentragfähigkeit verursachen könnten. Diese Einflüsse, vornehmlich geometrische Imperfektionen, werden systematisch untersucht und ergänzend in praxisrelevanten Beispielen bewertet. Die somit gewonnenen Erkenntnisse werden für die abschließende Beurteilung der großen Schrauben in Ringflanschverbindungen herangezogen. KW - Ermüdung KW - Vorspannung KW - Imperfektion KW - Offshore KW - Windenergieanlage KW - Schrauben PY - 2018 DO - https://doi.org/10.1002/stab.201810571 SN - 0038-9145 SN - 1437-1049 VL - 87 IS - 2 SP - 149 EP - 161 PB - Wilhelm Ernst und Sohn CY - Berlin AN - OPUS4-44285 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thiele, Marc T1 - Fatigue in Concrete N2 - The current knowledge about fatigue behavior of concrete is still incomplete. This concerns especially the progress of fatigue which precedes the fatigue failure. An overview on the fatigue behaviour in concrete is given. Therefore, the process of fatigue itself under cyclic compressive loading was investigated in a systematic and comprehensive way. The aim of this investigation was to obtain a deeper insight and to provide a better understanding of the damage process occurring within the material during fatigue loading. T2 - 1st Infrastar Training School CY - IFSTTAR, Nantes, France DA - 08.04.2019 KW - Fatigue KW - Concrete PY - 2019 AN - OPUS4-48945 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Frei, Vivian A1 - Thiele, Marc A1 - Pirskawetz, Stephan A1 - Meng, Birgit A1 - Rogge, Andreas T1 - Characterizing the Fatigue Behavior of High-Performance Concrete for Wind Energy Structures N2 - Severe mechanical fatigue conditions for worldwide proliferating windfarms are a Major challenge for high-performance concrete in towers, connecting joints and foundations of wind turbines. High-performance concrete offers potential for the application in offshore windfarms, not only regarding its good mechanical, but also chemical resistivity due to low diffusivity in the highly densified microstructure. For a more reliable fatigue assessment, monitoring based on nondestructive testing can be a valuable complement to design rules. Both approaches demand reliable experimental data, information about scalability and the development of standardized testing methods. This article presents results of an ongoing research program of BAM (Bundesanstalt für Materialforschung und -prüfung), which is a part of a joint national project (WinConFat) funded by the German Federal Ministry for Economic Affairs and Energy. The subproject implemented by BAM examines the fatigue behavior in dependence of size and slenderness for varying concrete strength at different stress levels. Besides fatigue strength, nondestructive testing is carried out additionally. Methods used are strain measurement and ultrasonic testing. The change of strain, stiffness and ultrasonic pulse velocity in the fatigue process is discussed. Results disclose a deeper insight into the damage process under cyclic loading of high-performance concrete and contribute to improve nondestructive monitoring. T2 - LORCENIS - Long Lasting Reinforced Concrete fpr Energy Infrastructure under Severe Operating Conditions CY - Ghent, Belgium DA - 10.09.2019 KW - Compressive Cyclic loading KW - Fatigue KW - High-strength concrete KW - Non destructive testing KW - Ultrasonic testing PY - 2019 SN - 978-9-463-88638-3 SP - 1 EP - 4 AN - OPUS4-49500 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Frei, Vivian A1 - Pirskawetz, Stephan A1 - Thiele, Marc A1 - Rogge, Andreas T1 - Experimental investigation of size effect on fatigue behavior of high strength concrete - concept and preliminary results N2 - The worldwide spread of windfarms brings new challenges, especially for concrete structures as a part of towers, connecting joints and foundations of wind turbines. High-cyclic loadings in such structures lead to a high relevance of the subject of fatigue. A proper assessment of the fatigue strength of concrete demands therefore a basis of reliable experimental data and the development of standardized testing methods. This article presents first results of an ongoing research program of BAM (Bundesanstalt für Materialforschung und -prüfung) which is a part of a joint project (WinConFat) funded by the German Federal Ministry for Economic Affairs and Energy. The subproject investigates the effects of size and slenderness of the specimens on the fatigue behaviour of high strength concrete at different stress levels. Not only the fatigue strength, but also the fatigue process itself is monitored by means of several measurement methods. Strain measurements are used to calculate the load dependent elastic modulus in the fatigue hysteresis as indicators for fatigue development. Furthermore, the application of non-destructive methods like acoustic emission analysis and ultrasonic measurement in laboratory tests gives a deeper insight into damage processes under cyclic loading. The results shall be used to improve design rules for concrete members under fatigue load and to develop or improve non-destructive techniques for in-service structural health monitoring. T2 - 5th International fib Congress: Better - Smarter - Stronger CY - Melbourne, Australia DA - 08.10.2018 KW - Acoustic emission testing KW - Compressive cyclic loading KW - Fatigue KW - High-strength concrete KW - Non-destructive testing KW - Size effect KW - Slenderness effect KW - Ultrasonic testing PY - 2018 SN - 978-1-877040-14-6 SP - 1 EP - 11 AN - OPUS4-46408 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Glienke, R. A1 - Kalkowsky, F. A1 - Hobbacher, A. F. A1 - Holch, A. A1 - Thiele, Marc A1 - Marten, F. A1 - Kersten, R. A1 - Henkel, K.-M. T1 - Evaluation of the fatigue resistance of butt‑welded joints in towers of wind turbines - A comparison of experimental studies with small scale and component tests as well as numerical based approaches with local concepts N2 - Wind turbines are exposed to a high number of load cycles during their service lifetime. Therefore, the fatigue strength verification plays an important role in their design. In general, the nominal stress method is used for the fatigue verification of the most common used butt-welded joints. The Eurocode 3 part 1–9 is the current design standard for this field of application. This paper presents recent results of fatigue tests on small-scaled specimens and large components with transverse butt welds to discuss the validity of the FAT-class. Furthermore, results from numerical simulations for the verification with the effective notch stress and the crack propagation approach are used for comparison. Based on the consistency between the numerical results and the fatigue tests, the influence of the seam geometry on the fatigue resistance was investigated. Finally, a prediction of the fatigue strength of butt-welded joints with plate thicknesses up to 80 mm was carried out. KW - Transverse butt weld KW - Weld imperfections KW - Wind turbine tower KW - Fatigue strength KW - Local approaches KW - Large components KW - Wind energy PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-596648 DO - https://doi.org/10.1007/s40194-023-01630-3 SN - 1878-6669 SP - 1 EP - 26 PB - Springer CY - Berlin AN - OPUS4-59664 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ratkovac, Mirjana A1 - Gerards-Wünsche, Paul A1 - Thiele, Marc A1 - Brackrock, Daniel A1 - Stamm, Michael T1 - Detection and monitoring of the fatigue crack growth on welds – Application-oriented use of NDT methods N2 - Early detection of fatigue cracks and accurate measurements of the crack growth play an important role in the maintenance and repair strategies of steel structures exposed to cyclic loads during their service life. Observation of welded connections is especially of high relevance due to their higher susceptibility to fatigue damage. The aim of this contribution was to monitor fatigue crack growth in thick welded specimens during fatigue tests as holistically as possible, by implementing multiple NDT methods simultaneously in order to record the crack initiation and propagation until the final fracture. In addition to well-known methods such as strain gauges, thermography, and ultrasound, the crack luminescence method developed at the Bundesanstalt für Materialforschung und -prüfung (BAM), which makes cracks on the surface particularly visible, was also used. For data acquisition, a first data fusion concept was developed and applied in order to synchronize the data of the different methods and to evaluate them to a large extent automatically. The resulting database can ultimately also be used to access, view, and analyze the experimental data for various NDT methods. During the conducted fatigue tests, the simultaneous measurements of the same cracking process enabled a comprehensive comparison of the methods, highlighting their individual strengths and limitations. More importantly, they showed how a synergetic combination of different NDT methods can be beneficial for implementation in large-scale fatigue testing but also in monitoring and inspection programs of in-service structures - such as the support structures of offshore wind turbines. T2 - Fatigue Design 2023 (FatDes 2023) CY - Senlis, France DA - 29.11.2023 KW - Fatigue KW - Welded KW - NDT KW - Crack growth PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-600238 DO - https://doi.org/10.1016/j.prostr.2024.03.062 VL - 57 SP - 560 EP - 568 PB - Elsevier B.V. AN - OPUS4-60023 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Frei, Vivian A1 - Pirskawetz, Stephan A1 - Thiele, Marc A1 - Rogge, Andreas T1 - Ermüdungsverhalten von Beton für unterschiedliche Probekörpergeometrien N2 - Die heute in der Anwendung befindlichen Bemessungskonzepte für Ermüdung von Beton stammen zum Teil noch aus den 1990er Jahren und sind speziell hinsichtlich hochfester Betone konservativ ausgelegt. Um die Vorteile von Türmen für Windkraftanlagen, vor allem auch aus hochfesten Betonen, im Zuge des geplanten Ausbaus der Windenergieversorgung in Deutschland wirtschaftlich nutzbar zu machen, müssen diese Bemessungskonzepte weiterentwickelt werden. Dafür sind umfangreiche Untersuchungen zur Ermittlung von Bruchlastwechselzahlen und zur Charakterisierung der Schädigungsentwicklung unter Ermüdungsbeanspruchung erforderlich. Allgemein anerkannte bzw. verbindliche Regelwerke oder Verfahren zur experimentellen Bestimmung der Ermüdungsfestigkeit (Bruchlastwechselzahlen) an Betonproben gibt es zurzeit aber nicht und die bisher durchgeführten Untersuchungen variieren in Parametern wie Probengeometrie, Probengröße und Prüffrequenz. Eine vergleichende Analyse der Ergebnisse der Studien und insbesondere die Übertragbarkeit auf bauteilrelevante Abmessungen ist auf dieser Grundlage nur sehr eingeschränkt möglich. KW - Ermüdungsverhalten KW - Probekörpergeometrien KW - Druckschwellenversuch KW - Bruchlastwechselzahlen KW - Beton PY - 2023 UR - https://www.betonverein.de/dbv-heft-52-materialermuedung-von-stahl-und-spannbeton-unter-hochzyklischer-beanspruchung-ergebnisse-des-verbundforschungsvorhabens-win-con-fat IS - 52 SP - 19 EP - 22 PB - Deutscher Beton- und Bautechnik-Verein E.V. CY - Berlin AN - OPUS4-58746 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Brinkmann, M. A1 - Wiehle, Philipp A1 - Thiele, Marc A1 - Graubner, C.-A. ED - Schermer, D. ED - Brehm, E. T1 - Grundlagen zur Bemessung druckbeanspruchten Lehmmauerwerks N2 - Lehmmauerwerk bietet sich aufgrund seiner zahlreichen ökologischen Vorteile für die Errichtung klimafreundlicher und ressourcenschonender Gebäude an. Um den Anwendungsbereich tragenden Lehmmauerwerks durch eine zeitgemäße Nachweisführung zu erweitern, werden in diesem Beitrag Grundlagen für die Entwicklung eines eurocodekonformen Bemessungskonzepts erarbeitet. Hierzu werden die Ergebnisse umfangreicher experimenteller Untersuchungen an Lehmmauerwerk sowie Lehmsteinen und -mörteln nach Konditionierung bei unterschiedlichen Klimata vorgestellt. Darauf aufbauend erfolgt eine Traglastanalyse druckbeanspruchter Lehmmauerwerkswände mittels numerischer und analytischer Methoden. Die daraus gewonnenen Erkenntnisse werden abschließend in einen an DIN~EN~1996-3/NA angelehnten Bemessungsvorschlag überführt, welcher die materialspezifischen Besonderheiten von Lehmmauerwerk berücksichtigt und eine fundierte Grundlage für eine wirtschaftliche und zuverlässige Nachweisführung darstellt. KW - Druckfestigkeit KW - Lehm KW - Mauerwerk KW - Bemessung KW - Feuchte PY - 2023 SN - 978-3-433-03373-9 DO - https://doi.org/10.1002/9783433611142.ch4 VL - 48 SP - 79 EP - 110 PB - Ernst & Sohn GmbH CY - Berlin ET - 1 AN - OPUS4-57509 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -