TY - GEN A1 - Babutzka, Martin A1 - et al., T1 - Exposure Site Catalogue - Catalogue of atmospheric corrosion field exposure sites in Europe N2 - Exposure sites and outdoor exposure have always been a part of atmospheric corrosion research providing the “final answer”, although at the cost of long exposure times. Individual exposure programs such as ISOCORRAG, MICAT and ICP Materials have resulted in collaborative networks of exposure sites. So far, however, there has been no collective effort to put together currently active sites in a comprehensive manner and across programs and nations. The information collected in the catalogue is possible thanks to the work of all individual site managers listed as contact persons, efforts of members of Working Party 25 (WP25) Atmospheric Corrosion of the European Federation of Corrosion (EFC) and financial support of the EFC. With this Catalogue you can both get a general overview of what is available and be guided if you are looking for a particular environment with certain characteristics. KW - Atmospheric Corrosion KW - Atmosphärische Korrosion KW - Corrosion KW - Korrosion KW - Exposure KW - Auslagerungsversuche PY - 2022 UR - https://efcweb.org/Scientific+Groups/WP25_+Atmospheric+Corrosion/Current+Activities/_/Exposure%20site%20catalogue%20EFC%20lores.pdf SP - 1 EP - 56 PB - European Federation of Corrosion, EFC AN - OPUS4-55284 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erning, Johann Wilhelm ED - Stojanovic, I. T1 - Hygienic assessment of SLM-printed stainless steel N2 - Electrochemical measurements for the hygienic assessment of additively manufactured products are discussed. The Assessment and details of the material are described, examples for the application are given. N2 - Elektrochemische Messungen zur hygienischen Bewertung additiv gefertigter Bauteile werden diskutiert. Die Bewertung und Details des Werkstoffs werden beschrieben, Anwendungsbeispiele gezeigt. T2 - Kormat 2022 CY - Online meeting DA - 26.04.2022 KW - Korrosion KW - Trinkwasser KW - Hygienische Bewertung KW - Additive Fertigung PY - 2022 SN - 1848-4255 SP - 21 EP - 25 PB - Proceedings of the Croatian Society for Material Protection CY - Zagreb AN - OPUS4-54932 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erning, Johann Wilhelm T1 - Hygienic assessment of SLM-printed stainless steel N2 - Elektrochemische Messungen zur hygienischen Bewertung additiv gefertigter Bauteile werden diskutiert. Die Bewertung und Details des Werkstoffs werden beschrieben, Anwendungsbeispiele gezeigt. T2 - Kormat 2022 CY - Online meeting DA - 26.04.2022 KW - Korrosion KW - Trinkwasser KW - Hygienische Bewertung KW - Additive Fertigung PY - 2022 AN - OPUS4-54709 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erning, Johann Wilhelm T1 - Materials in contact with drinking water and regulatory issues N2 - The state of play in regard to regulations of materials in contact with drinking water in europe is discussed T2 - Kormat 2022 CY - Online meeting DA - 26.04.2022 KW - Korrosion KW - Trinkwasser KW - Hygiene KW - Risikobewertung PY - 2022 AN - OPUS4-54710 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Prestressed Concrete Structures with ConcentratedTendons- Structural Damage due to Hydrogen-Induced Stress Corrosin Cracking N2 - In the course of the deconstruction of the "Bridge of the 20th anniversary of the GDR" at the Altstädter Bahnhof in Brandenburg a. d. Havel, new information on the initiation of hydrogen-induced stress cracks was obtained. BAM was commissioned by the Brandenburg State Road Administration to participate in a corresponding joint project which is financed by the Federal Ministry for Digital and Transport. The added value of the new information gained in this project goes beyond the specific structure. It describes unexpected new damage patterns that can be transferred to other structures with concentrated tendons (tendon block method and Baur-Leonhardt method) and were previously unknown in this form. These should be made known to other developers to enable them to initiate any necessary actions. T2 - Consec 2024 CY - Chennai, India DA - 24.09.2024 KW - Corrosion KW - Spannstahl KW - Hydrogen KW - Korrosion PY - 2024 AN - OPUS4-61305 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Exposure Site 41 Berlin N2 - The United Nations Educational, Social and Cultural Organization (UNESCO) is establishing a project with the objective of investigating the role of air pollution in the acceleration of ongoing corrosion processes and the resulting corrosion intensity. Consequently, since the early 1980s, research has been conducted on 60 different exposure sites. The Bundesumweltamt has mandated the BAM to oversee a designated test sites, a responsibility that the BAM has accepted since 2024. The presentation will provide a visual representation of the newly constructed test site, in addition to the inaugural results of 2024. T2 - UNESCO Materials RISE Meeting CY - Prague, Czech Republic DA - 05.05.2025 KW - Korrosion KW - Corrosion PY - 2025 AN - OPUS4-63080 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Atmospheric Corrosion - Sheltered Ventilated Conditions - An Opportunity for a Standardized Exposure site Rack N2 - To determine the corrosivity of atmospheric conditions, standardized metal sheets are exposed. After pickling, the loss of mass indicates the corrosivity of the atmospheric conditions. Under marine conditions, a sheltered opportunity will mirror the situation where e.g. chlorides could accumulate on the surface because they are protected from rain. Under these conditions, the corrosivity could be even higher than under free weather conditions. These sheltered conditions are necessary for a realistic service life prediction. T2 - Eurocorr 2024 CY - Paris, France DA - 01.09.2024 KW - Corrosion KW - Atmospheric corrosion KW - Korrosion PY - 2024 AN - OPUS4-60967 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schwarz, W. A1 - Wilsch, Gerd A1 - Katsumi, N. A1 - Ebell, Gino A1 - Völker, Tobias T1 - Ion distribution in concrete overlay, mapped by laser induced breakdown spectroscopy (LIBS), modified by an embedded zinc anode N2 - Galvanic corrosion protection by embedded zinc anodes is an accepted technique for the corrosion protection of reinforcing steel in concrete. Galvanic currents flow between the zinc anode and the steel reinforcement due to the potential difference that is in the range of a few hundred mV. The ion distribution was studied on two steel reinforced concrete specimens admixed with 3 wt.% chloride/wt. cement and galvanically protected by a surface applied EZ-anode. On both specimens, a zinc anode was embedded and glued to the concrete surface by a geo-polymer-based chloride-free binder. At one specimen, the EZ-anode was operated for 2,5 years, the EZ-anode at the other specimen was not electrically connected to the reinforcement, this specimen serves as a reference. Both specimens have been stored under identical conditions. The ion distribution between the anode (EZ-anode) and cathode (steel reinforcement) was studied by laser-induced breakdown spectroscopy (LIBS) after 7 months, 12 months, and 2,5 years. Results of the LIBS studies on the specimen with activated EZ-anode after 7 months, 12 months, and 2,5 years and of the reference specimen after 2,5 years are reported. Results show that diffusion of ions contributes to the changes in the ion distribution but migration, especially of chlorides towards the EZ-anode is significant despite the weak electric field – several hundred millivolts - generated by the galvanic current. Results show that chloride ions accumulate near the zinc-anode as in water-insoluble zinc-hydroxy chlorides - Simonkolleit. T2 - ICCRRR 2022 CY - Capetown, South Africa DA - 03.10.2022 KW - Korrosion KW - Corrosion KW - LIBS KW - Zinc PY - 2022 AN - OPUS4-55948 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Prestressed Concrete Structures with Concentrated Tendons - Structural Damage due to Hydrogen-Induced Stress Corrosion Cracking N2 - In the course of the deconstruction of the "Bridge of the 20th anniversary of the GDR" at the Altstädter Bahnhof in Brandenburg a. d. Havel, new information on the initiation of hydrogen-induced stress cracks was obtained. BAM was commissioned by the Brandenburg State Road Administration to participate in a corresponding joint project which is financed by the Federal Ministry for Digital and Transport. The added value of the new information gained in this project goes beyond the specific structure. It describes unexpected new damage patterns that can be transferred to other structures with concentrated tendons (tendon block method and Baur-Leonhardt method) and were previously unknown in this form. These should be made known to other developers to enable them to initiate any necessary actions. T2 - Eurocorr 2022 CY - Berlin, Gemany DA - 29.08.2022 KW - Korrosion KW - Corrosion KW - Hydrogen KW - Stress Cracking PY - 2022 AN - OPUS4-55613 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Potential Mapping - What could we measure and what should we able to detect – guideline B03 of DGZfP N2 - “Electrochemical potential mapping according to guideline B3 of DGZfP (German Society for Non-Destructive Testing) is a recognized technique for the localization of corroding reinforcing steels. Areas of corroding reinforcement steel can be located in a non-destructive manner by means of this procedure. Half‐cell potential measurements are used in order to detect chloride‐induced corrosion. However, it is not recommended in order to assess the risk of carbonation‐induced corrosion. For this purpose, determining the carbonation depth and the concrete cover appears more appropriate. The content of this specification exclusively refers to the application of mobile, local variable reference electrodes, which are only placed on the concrete surface while measuring. The technique distinguishes itself thereby from the range of corrosion monitoring systems with stationary installed reference electrodes and sensor systems, respectively, whereby it is possible to continuously track measurements within the area of the installed electrodes. However, these methods are not dealt with in this specification.” T2 - NDT-CE 2022 CY - Zurich, Switzerland DA - 16.08.2022 KW - Korrosion KW - Potentialfeldmessung KW - Corrosion KW - Half-cell potential KW - Potential mapping PY - 2022 AN - OPUS4-55524 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -