TY - GEN A1 - Pauw, Brian Richard A1 - Röder, Bettina A1 - Smales, Glen Jacob T1 - High temperature in-vacuum flow-through sample holder (sandwich design version 1.1) N2 - Technical drawings and documents for building a compact, heated, vacuum compatible flow-through sample holder. This holder is in use at the BAM MOUSE instrument as well as at the I22 beamline at the Diamond Light Source (see references for instrument details). This holder has several features: - The holder can be used in vacuum environments as well as in atmosphere - It has two G 1/4" UNF fittings to attach HPLC tubing for (optionally) flowing a medium through the sample cell - There are two additional (unflowed) sample positions for backgrounds and calibrants, held at the same temperature - The low-mass design coupled with a 250W heating element can achieve heating rates of 1 degree C per second, when coupled (for example) with an Omron E5CC PID controller. - The sample holder insert can be made from various materials depending on the application. Sealing the sample from the vacuum can be achieved using kapton, teflon or Magic tape, depending on the temperature requirements. The inlet and outlet holes will need to be punctured with a needle to enable flow. - Large exit cones ensure a clear exit angle of at least 45 degrees two theta. - It has been tested with temperatures up to 400 degrees C. - Compression area has been raised and polished to ensure a good vacuum seal. KW - SAXS KW - X-ray scattering KW - Sample cell KW - Sample holder KW - Heated KW - Flow-through KW - Vacuum compatible KW - XRD KW - WAXS PY - 2023 DO - https://doi.org/10.5281/zenodo.7501030 PB - Zenodo CY - Geneva AN - OPUS4-56777 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Stawski, Tomasz A1 - Miliute, Aiste T1 - Structural Refinement of ZrV₂O₇ with Negative Thermal Expansion Using Pair Distribution Function Analysis N2 - This repository contains Python scripts specifically developed for structural refinement of Zirconium Vanadate (ZrV₂O₇), a material known for its negative thermal expansion (NTE). The scripts implement Pair Distribution Function (PDF) analysis to refine crystal structures directly from experimental X-ray diffraction (XRD) data. The refinement workflow is built around the DiffPy-CMI library, enhanced with custom functionalities tailored for ZrV₂O₇ and similar oxide materials. KW - Zirconium vandate KW - Total scattering KW - Pair distribution function KW - Structure refinement PY - 2025 DO - https://doi.org/10.5281/zenodo.15395752 PB - Zenodo CY - Geneva AN - OPUS4-64750 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Habibimarkani, Heydar A1 - Prinz, Carsten A1 - Sahre, Mario A1 - Hodoroaba, Vasile-Dan A1 - Radnik, Jörg T1 - CV, TEM, XRD and XPS/HAXPES datasets of FeNi-based nanoparticles for the oxygen evolution reaction N2 - The datasets from Cyclic Voltammetry, Transmision Electron Microscopy, X-ray Diffraction, and (Hard Energy) X-ray Photoelectron Spectroscopy are related to the publication H. Habibimarkani, S.-L. Abram, A. Guilherme Buzanich, C. Prinz, M. Sahre, V.-D. Hodoroaba and J. Radnik "In-depth analysis of FeNi-based nanoparticles for the oxygen evolution reaction" Scientific Reports (2025), https://doi.org/10.1038/s41598-025-92720-3 Details of the materials and the experimental procedures are described in this publications. KW - Oxygen evolution reaction KW - Fe-Ni nanopartices KW - Comprehensive analysis PY - 2025 DO - https://doi.org/10.5281/zenodo.14975964 PB - Zenodo CY - Geneva AN - OPUS4-63335 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Radnik, Jörg A1 - Chemello, Giovanni A1 - Knigge, Xenia A1 - Al-Sabbgh, Dominik A1 - Hodoroaba, Vasile-Dan T1 - XPS, HAXPES, XRD and SEM datasets of functionalized graphene nanoplateletes N2 - The datasets from (Hard Energy) X-ray photoelectron spectroscopy, X-ray diffraction and Scanning Electron Microsopy are related to the publication G. Chemello, X. Knigge, D. Ciornii, B.P. Reed, A.J. Pollard, C.A. Clifford, T. Howe, N. Vyas, V.-D. Hodoroaba, J. Radnik "Influence of the morphology on the functionalization of graphene nanoplatelets analyzed by comparative photoelectron spectroscopy with soft and hard X-rays" Advanced Materials Interfaces (2023), DOI: 10.1002/admi.202300116. KW - Graphene related 2D materials KW - X-ray photoelectron spectroscopy KW - Hard-energy X-ray photoelectron spectroscopy KW - Scanning electron microscopy KW - Powder X-ray diffraction PY - 2023 DO - https://doi.org/10.5281/zenodo.7956497 PB - Zenodo CY - Geneva AN - OPUS4-57898 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Prinz, Carsten A1 - Zimathies, Annett A1 - Emmerling, Franziska T1 - Experimental raw data sets associated with certified reference material BAM-P114 (titanium dioxide) for comparison of nitrogen and argon sorption, available in the universal adsorption information format (AIF) N2 - These data sets serve as models for calculating the specific surface area (BET method) using gas sorption in accordance with ISO 9277. The present measurements were carried out with nitrogen at 77 Kelvin and argon at 87 Kelvin. It is recommended to use the following requirements for the molecular cross-sectional area: Nitrogen: 0.1620 nm² Argon: 0.1420 nm² Expected specific surface area for nitrogen (BET): 24 to 25 m²/g Expected specific surface area for argon (BET): 20 m²/g Titanium dioxides certified with nitrogen sorption and additionally measured with argon for research purposes were used as sample material. The resulting data sets are intended to serve as comparative data for own measurements and show the differences in sorption behaviour and evaluations between nitrogen and argon. These data are stored in the universal AIF format (adsorption information format), which allows flexible use of the data. KW - Physisorption KW - Specific surface area KW - AIF KW - Argon KW - Nitrogen PY - 2024 DO - https://doi.org/10.5281/zenodo.13283291 PB - Zenodo CY - Geneva AN - OPUS4-60782 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Prinz, Carsten A1 - Zimathies, Annett A1 - Emmerling, Franziska T1 - Experimental raw data sets associated with certified reference material BAM-P115 (titanium dioxide) for comparison of nitrogen and argon sorption, available in the universal adsorption information format (AIF) N2 - These data sets serve as models for calculating the specific surface area (BET method) using gas sorption in accordance with ISO 9277. The present measurements were carried out with nitrogen at 77 Kelvin and argon at 87 Kelvin. It is recommended to use the following requirements for the molecular cross-sectional area: Nitrogen: 0.1620 nm² Argon: 0.1420 nm² Expected specific surface area for nitrogen (BET): 140 to 154 m²/g Expected specific surface area for argon (BET): 129 to 135 m²/g Titanium dioxides certified with nitrogen sorption and additionally measured with argon for research purposes were used as sample material. The resulting data sets are intended to serve as comparative data for own measurements and show the differences in sorption behaviour and evaluations between nitrogen and argon. These data are stored in the universal AIF format (adsorption information format), which allows flexible use of the data. KW - Physisorption KW - Specific surface area KW - AIF KW - Argon KW - Nitrogen PY - 2024 DO - https://doi.org/10.5281/zenodo.13269756 PB - Zenodo CY - Geneva AN - OPUS4-60783 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Wolf, Jako A1 - Stawski, Tomasz A1 - Smales, Glen Jacob A1 - Thünemann, Andreas A1 - Emmerling, Franziska T1 - SI Files for "Towards automation of the polyol process for the synthesis of silver nanoparticles" N2 - The graphml file: reaction_graph_AgNP.graphml is included. It contains topological information (Fig. 1 in the main text) about the reaction setup and metadata with reaction condtions. It used by the Python API used to control the Chemputer. SAXS reports. The complete report sheets generated by McSAS are included. They contain extended information characterising the size distributions and the fitting parameters. NP3_I: saxs_report_NP3_I.pdf NP3_II: saxs_report_NP3_II.pdf NP3_III: saxs_report_NP3_III.pdf NP3_IV: saxs_report_NP3_IV.pdf NP5_I: saxs_report_NP5_I.pdf NP5_II: saxs_report_NP5_II.pdf NP5_III: saxs_report_NP5_III.pdf KW - Automated synthesis KW - Silver KW - Nanoparticles PY - 2022 DO - https://doi.org/10.5281/zenodo.5910614 PB - Zenodo CY - Geneva AN - OPUS4-55197 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Prinz, Carsten A1 - Zimathies, Annett A1 - Emmerling, Franziska T1 - Experimantal raw data sets associated with certified reference material BAM-P116 (titanium dioxide) for comparison of nitrogen and argon sorption, available in the universal adsorption information format (AIF) N2 - These data sets serve as models for calculating the specific surface area (BET method) using gas sorption in accordance with ISO 9277. The present measurements were carried out with nitrogen at 77 Kelvin and argon at 87 Kelvin. It is recommended to use the following requirements for the molecular cross-sectional area: Nitrogen: 0.1620 nm² Argon: 0.1420 nm² Titanium dioxides certified with nitrogen sorption and additionally measured with argon for research purposes were used as sample material. The resulting data sets are intended to serve as comparative data for own measurements and show the differences in sorption behaviour and evaluations between nitrogen and argon. These data are stored in the universal AIF format (adsorption information file), which allows flexible use of the data. KW - Physisorption KW - Surface area KW - AIF KW - Argon KW - Nitrogen PY - 2023 DO - https://doi.org/10.5281/zenodo.10199628 PB - Zenodo CY - Geneva AN - OPUS4-59102 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Stawski, Tomasz A1 - Smales, Glen Jacob A1 - Scoppola, E. A1 - Jha, D. A1 - Morales, L. F. G. A1 - Moya, A. A1 - Wirth, R. A1 - Pauw, Brian Richard A1 - Emmerling, Franziska A1 - Van Driessche, A. E. S. T1 - Supplementary data set for "Seeds of imperfection rule the mesocrystalline disorder in natural anhydrite single crystals" N2 - In recent years, we have come to appreciate the astounding intricacy of the formation process of minerals from ions in aqueous solutions. In this context, a number of studies have revealed that nucleation in the calcium sulfate system is non-classical, involving the aggregation and reorganization of nanosized prenucleation particles. In a recent work we have shown that this particle-mediated nucleation pathway is actually imprinted in the resultant single micron-sized CaSO4 crystals. This property of CaSO4 minerals provides us with an unique opportunity to search for evidence of non-classical nucleation pathways in geological environments. In particular, we focused on the quintessential single crystals of anhydrite extracted from the Naica mine in Mexico. We elucidated the growth history from this mineral sample by mapping growth defects at different length scales. Based on these data we argue that the nano-scale misalignment of the structural sub-units observed in the initial calcium sulfate crystal seed propagate through different length-scales both in morphological, as well as strictly crystallographic aspects, eventually causing the formation of large mesostructured single crystals of anhydrite. Hence, the nanoparticle mediated nucleation mechanism introduces a 'seed of imperfection', which leads to a macroscopic single crystal, in which its fragments do not fit together at different length-scales in a self-similar manner. Consequently, anisotropic voids of various sizes are formed with very well-defined walls/edges. But, at the same time the material retains its essential single crystal nature. These findings shed new light on the longstanding concept of crystal structure. KW - Calcium sulfate KW - Mesocrystal KW - Anhydrite PY - 2021 DO - https://doi.org/10.5281/zenodo.4943234 PB - Zenodo CY - Geneva AN - OPUS4-53765 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Miliūtė, Aistė T1 - Synthesis and phase purity of the negative thermal expansion material ZrV2O7 N2 - This repository contains computational and experimental data for the manuscript titled “Synthesis and phase purity of the negative thermal expansion material ZrV2O7”. KW - NTE KW - Sol-gel KW - Solid-state KW - Ab-initio KW - XRD KW - Raman PY - 2024 DO - https://doi.org/10.5281/zenodo.12688634 PB - Zenodo CY - Geneva AN - OPUS4-61360 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -