TY - CONF A1 - Gluth, Gregor A1 - Sturm, Patrick A1 - Greiser, Sebastian A1 - Jäger, Christian A1 - Kühne, Hans-Carsten ED - Wang, J. ED - Kriven, W. ED - Fey, T. ED - Colombo, P. ED - Weber, W.J. ED - Amoroso, J. ED - Fahrenholtz, W.G. ED - Shimamura, K. ED - Halbig, M. ED - Kirihara, S. ED - Wu, Y. ED - Shurgart, K. T1 - One-part geopolymers and aluminosilicate gel-zeolite composites: factors influencing microstructure and engineering properties N2 - Mixing and curing of geopolymers and related alkali-activated materials without storage and handling of highly alkaline solutions possesses advantages regarding safety and economic viability. One possible approach is to produce these materials from solid silica feedstocks and solid sodium aluminate, and subsequent mixing with water. We present a comparison between geopolymers and aluminosilicate gel-zeolite composites synthesized by this route from different silica feedstocks (by-product silica from chlorosilane production, microsilica, rice husk ash) and with different SiO2/Al2O3 ratios, using results from XRD, NMR, SEM, thermal analysis, mechanical and acid resistance testing. The use of rice husk ash favors formation of a fully amorphous geopolymer with high strength. Utilization of the other silica feedstocks leads to formation of aluminosilicate gel-zeolite composites, the amount and kind of zeolites depending on the feedstock and the SiO2/Al2O3 ratio. These composites show beneficial dehydration behavior, viz. no distinct dehydration step of thermal strain, with the phase assemblage after heating to 1000°C controlled by the starting composition. Mortars produced from both, the geopolymers as well as the composites, exhibit high resistance to sulfuric acid attack, making them promising materials for the construction and the repair of industrial and sewer structures. T2 - 42nd International Conference on Advanced Ceramics and Composites CY - Daytona Beach, FL, USA DA - 21.01.2018 KW - Alkali-activated materials KW - One-part geopolymers KW - Sulfuric acid resistance KW - High-temperature resistance PY - 2019 U6 - https://doi.org/10.1002/9781119543381.ch17 VL - 39 IS - 3 SP - 183 EP - 196 PB - John Wiley & Sons AN - OPUS4-47282 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -