TY - CONF A1 - Beck, Uwe A1 - Baier, Jennifa A1 - Hidde, Gundula A1 - Sahre, Marion A1 - Weise, Matthias T1 - Particles in PVD-coatings: Imperfection or functional add-on feature? N2 - The application of PVD-coatings ranges from mechanical engineering, i.e. thicker tribological coatings, to precision optics, i.e. thinner optical coatings. For physical vapor deposition (PVD) technologies such as evaporation, sputtering, ion beam assisted/driven deposition, vacuum is a prerequisite for two reasons: at first process-related ones (evaporation source, plasma discharge, and mean free path) and at second coating-related ones (pure, perfect, and dense films). Usually, the goal is a homogenous coating of defined stoichiometry and micro-structure without any imperfection. However, the implementation of micro- or nano-particles may occur accidentally or delibe-rately. Independent of the particle origin, there are two fundamental rules regarding coating functionality: at first, the larger the particle diameter to coating thickness ratio the more affected the functionality of the coating, and at second, the larger the material contrast in terms of the functional feature of interest the more affected the coating performance. Hence, embedded particles have to be avoided for the majority of thin films by all means. The unintended implementation of particles usually results in a malfunction of the coating from the beginning or is at least considered as a weak point of the coating creating a time-dependent defect under service conditions. The intended implementation of particles on surfaces and in coatings may create add-on features, topographic ones and functional ones, however, the facts mentioned hold true. Examples of particle-initiated coating defects are demonstrated in dependence on the origin and the field of application. Strategies for deliberate attachment/embedding of particles on surfaces/in coatings are discussed regarding process compatibility and coating integrity. For industrial applications, both the validation of process compatibility of particle injection and the plasma resistance of particles under vacuum and plasma conditions have to be confirmed. Further points of interest are the homogeneity of particle distribution and the avoidance of particle agglomeration which is still a crucial point for dry dispersed particles. So far, technical applications are limited to PVD hybrid coatings, plasma dispersion coatings are still a challenge except for applications where homogeneity is not required as in case of product authentication. T2 - ICMCTF 2018, International Conference on Metallurgical Coatings and Thin Films CY - San Diego, CA, USA DA - 23.04.2018 KW - PVD-coatings KW - PVD-processes KW - Unintended particle generation KW - Particles as imperfections KW - Deliberate particle implementation KW - Particles as add-on features PY - 2018 AN - OPUS4-44973 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Griepentrog, Michael T1 - Towards the standardization of dynamic instrumented indentation testing N2 - Nowadays the Instrumented Indentation Testing (IIT) is one of the most commonly used methods to determine the mechanical properties of materials in the nano range. This method is already extensive standardized in EN ISO 14577 part 1-4. Because of the great interest of researchers and industries in investigations of time depending material behavior mostly all suppliers of IIT equipment are offering the possibility of dynamic testing. Realizing this development ISO/TC 164/SC3 Hardness Testing has proposed to start the new standardization project “Linear elastic dynamic instrumented indentation testing DIIT”. The development of this standard is accompanied by the first international intercomparing exercise comparing results of dynamic instrumented indentation testing from testing machines using different hardware solutions and different models for data evaluation. The draft of part 5 of ISO 14577 “Linear elastic dynamic instrumented indentation testing DIIT” specifies verification and calibration of testing machines for carrying out the measurement of the dynamic material response when an oscillatory force or displacement, with amplitudes small in comparison to the prescribed target values, is imparted to the indenter while the indenter is continuously loaded to a prescribed target load or target depth or while the load or displacement is held constant at a prescribed target value. In case of a material showing plastic-elastic behavior, the measured dynamic response is used for continuous evaluation of the dynamic stiffness of the contact as a function of depth and frequency. Using the dynamic stiffness of the contact a reduced dynamic modulus will be calculated. In case of a material showing visco-elastic behavior from the measured dynamic response also the dynamic contact damping coefficient as function of depth and frequency is evaluated continuously. Using dynamic contact stiffness and dynamic contact damping coefficient reduced lost and storage modulus for visco-elastic materials will be calculated. The main normative requirements of the draft will be presented and discussed in the light of the first results of the intercomparing excise. T2 - IIW6, International Indentation Workshop 6 CY - Sapporo, Japan DA - 02.07.2018 KW - ISO 14577 KW - Instrumented indentation testing KW - Nanoindentation KW - IIT KW - Mechanical properties KW - Dynamic testing KW - Visco-elastic KW - Loss module KW - Storage module PY - 2018 AN - OPUS4-45850 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rietz, U. A1 - Lerche, D. A1 - Hielscher, Stefan A1 - Grunwald, Daniel A1 - Beck, Uwe T1 - Determination of coating properties by using analytical centrifugation N2 - The majority of all products have coated surfaces designed to fulfil different requirements. Building constructions are exposed to external influences like a wide temperature and humidity range, rain and UV radiation to name a few. The extension of machine life for metal cutting tools, like drills or milling cutters is another field of application for coated surfaces. The surfaces have to be modified in a way to maintain their specific functionality. Although adhesion testing of coatings is of great interest, it is still a challenge to obtain reliable quantitative results and to meet economic requirements. In this talk we deal with the curing behaviour of different 2-component epoxy paint systems for corrosion protection of metal constructions. After preparation of specimens the strength was determined in specified time intervals during curing. It could be shown that epoxy paints differ significantly on curing time as well as final strength. The second experimental study deals with coating systems on glass fibre reinforced plastics which are used for wind power turbines to reduce abrasive wear and ice adhesion for aerodynamic and safety reasons. All measurements have been carried out by CAT-TechnologyTM (Centrifugal Adhesion Testing), which uses the radially directed centrifugal force as test-load. The multi-sample test instrument analyses up to eight test specimen under identical testing conditions. By varying the rotational speed (100 rpm up to 13,000 rpm), forces from 0.1 N to 6.5 kN are applied. Upon reaching the critical rupture force, the stamp separates from the substrate and a sample related IR-signal is sent from the spinning rotor. For each test specimen breaking force is calculated and displayed in real-time. The innovative measurement principle meets the requirements of DIN EN 15870 and ISO 4624. T2 - EURADH 2018 CY - Lisbon, Portugal DA - 05.07.2018 KW - Adhesive strength determination KW - CAT-technology KW - Centrifugal adhesion testing KW - Metal coatings KW - Decorative coatings on polymer substrates PY - 2018 AN - OPUS4-46001 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beck, Uwe A1 - Hidde, Gundula A1 - Lange, Thorid A1 - Gargouri, H. A1 - Kärkkänen, I. A1 - Naumann, F. T1 - Plasma Activation and Plasma-assisted ALD Surface Modification of Polymers for Improved Bonding and Adhesive Strength N2 - Bonding strength is crucial on polymers of low surface energy, for clean surfaces limited to 0.5, 1, and 2 MPa for PTFE, PP, and PE. Plasma treatment may improve bonding strength by a factor of 2 (PTFE) or 5 (PP and PE). The efficiency of treatment is usually 10% as both low pressure and atmospheric pressure processes show low topographic conformity. Besides, lifetime of activation/modification is rather short. Hence, bonding has to be carried out immediately after plasma treatment. The concept of plasma-assisted ALD (atomic layer deposition) interlayers was introduced in the project HARFE of SENTECH (modification/deposition/in-situ monitoring) and BAM (bonding, characterization, testing). ALD deposition has a high surface conformity and for dielectric films of Al2O3 also a good long-term stability given that the films are dense enough. Based on TMA and O2/O3 precursors, ALD layer stacks from 60 to 375 monolayers were prepared under different conditions. For a transfer time of 24 hours from deposition to measurement, bonding strength could be increased up to 5 MPa (PTFE) respectively 10 MPa (PP, PE). The huge potential of ALD layers as adhesive interlayers was demonstrated for Al2O3 on stainless steel with bonding strength beyond 15 MPa, i.e. interface strength within the ALD stack is also in this range. This is a prerequisite for subsequent PVD/CVD-deposition in hybrid systems. By means of the SI ALD LL system of SENTECH thermal and plasma-supported ALD processes can be alternatively realized. Ellipsometric in-situ monitoring provides monolayer sensitivity and reveals that the efficient bonding of the lower ALD layers on the polymer has to be further improved. Testing of bonding strength was realized by CAT (centrifugal adhesion testing) technology. It was shown that ALD modification correlates with the increase of surface energy and bonding strength. T2 - PSE 2018 - 16th Conference on Plasma Surface Engineering CY - Garmisch-Partenkirchen, Germany DA - 17.09.2018 KW - Plasma activation KW - Plasma-assisted ALD modification KW - Adhesive ALD interlayer KW - Bonding strength KW - Adhesive strength PY - 2018 AN - OPUS4-46015 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beck, Uwe A1 - Hielscher, Stefan A1 - Lange, Thorid A1 - Rietz, U. A1 - Lerche, D. T1 - State-of-the-Art in Multiple-Sample Evaluation of Adhesive and Bonding Strength N2 - The paper addresses the “State-of-the-Art in Multiple-Sample Evaluation of Adhesive and Bonding Strength” and the following points are discussed in more detail: 1. Motivation (coatings, varnishes, tapes, laminates, CFRP, adhesive-bonded joints) 2. Conventional single-sample testing (evaluation of adhesive and bonding strength; failure pattern) 3. Multiple-sample handling (MSH), bonding (MSB), and testing: centrifugal adhesion testing (CAT) (multiple-sample approach, tensile test within a centrifuge) 4. Application examples of CAT-Technology™ (laminates, optical coatings, CFRP joints) Finally, a summary is given regarding status quo and benefits of CAT-technology under tensile stress conditions whereas examples of testing in a centrifuge under compressive stress conditions are mentioned in the outlook. T2 - The 5th International Conference Competitive Materials and Technology Processes CY - Miskolc-Lillafüred, Hungary DA - 08.10.2018 KW - Centrifugal Adhesion Testing KW - CAT KW - Multiple-sample handling (MSH) KW - Multiple-sample bonding (MSB) KW - Tensile strength of laminates KW - Tensile strength of coatings KW - Adhesive strength KW - Bonding strength PY - 2018 AN - OPUS4-46336 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Donėlienė, J. A1 - Rudzikas, M. A1 - Rades, Steffi A1 - Dörfel, Ilona A1 - Peplinski, Burkhard A1 - Sahre, Mario A1 - Pellegrino, F. A1 - Maurino, V. A1 - Ulbikas, J. A1 - Galdikas, A. A1 - Hodoroaba, Vasile-Dan T1 - Morphology and structure of TixOy nanoparticles generated by femtosecond laser ablation in water N2 - In this work femto-second pulsed laser ablation in liquid (PLAL) procedure for the generation of titanium oxide nanoparticles (NP) is reported with the purpose of understanding morphology and structure of the newly generated NPs. Ablation duration was varied for optimization of NP generation processes between 10 and 90 min. Surface morphology of NPs as well as their size and shape (distribution) were analysed by various complementary electron microscopy techniques, i.e. SEM, TSEM and TEM. The crystalline structure of titanium oxide particles was investigated byXRD(two instruments operated in different geometries) and HR-TEM. Concentration of generated titanium oxide NPs in liquid was analysed by ICP-MS. A mix of crystalline (mainly anatase), partly crystalline and amorphous spherical titanium oxide NPs can be reported having a mean size between 10 and 20 nm, which is rather independent of the laser ablation (LA) duration. A second component consisting of irregularly shaped, but crystalline titanium oxide nanostructures is co-generated in the LA water, with more pronounced occurrence at longer LA times. The provenance of this component is assigned to those spherical particles generated in suspension and passing through the converging laser beam, being hence subject to secondary irradiation effects, e. g. fragmentation. KW - Titanium oxide KW - Nanoparticles KW - Laser ablation in liquid KW - Particle morphology KW - Nanoparticle structure PY - 2018 DO - https://doi.org/10.1088/2053-1591/aaba56 SN - 2053-1591 VL - 5 IS - 4 SP - 045015-1 EP - 045015-12 PB - IOP Publishing CY - London, UK AN - OPUS4-44678 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Donėlienė, J. A1 - Rudzikas, M. A1 - Rades, Steffi A1 - Dörfel, Ilona A1 - Peplinski, Burkhard A1 - Sahre, Mario A1 - Pellegrino, F. A1 - Maurino, V. A1 - Ulbikas, J. A1 - Galdikas, A. A1 - Hodoroaba, Vasile-Dan T1 - Electron Microscopy and X-Ray Diffraction Analysis of Titanium Oxide Nanoparticles Synthesized by Pulsed Laser Ablation in Liquid N2 - A femto-second pulsed laser ablation in liquid (PLAL) procedure for the generation of titanium oxide nanoparticles (NP) is reported with the purpose of understanding morphology and structure of the newly generated NPs. Ablation duration was varied for optimization of NP generation processes between 10 and 90 min. Surface morphology of NPs as well as their size and shape (distribution) were analysed by various complementary electron microscopy techniques, i.e. SEM, TSEM and TEM. The crystalline structure of titanium oxide particles was investigated by XRD(two instruments operated in different geometries) and HR-TEM. Concentration of generated titanium oxide NPs in liquid was analysed by ICP-MS. A mix of crystalline (mainly anatase), partly crystalline and amorphous spherical titanium oxide NPs can be reported having a mean size between 10 and 20 nm, which is rather independent of the laser ablation (LA) duration. A second component consisting of irregularly shaped, but crystalline titanium oxide nanostructures is co-generated in the LA water, with more pronounced occurrence at longer LA times. The provenance of this component is assigned to those spherical particles generated in suspension and passing through the converging laser beam, being hence subject to secondary irradiation effects, e. g. fragmentation. KW - Laser ablation in liquid KW - Nanoparticles KW - Titanium oxide KW - Particle morphology PY - 2018 UR - https://www.cambridge.org/core/journals/microscopy-and-microanalysis/article/electron-microscopy-and-xray-diffraction-analysis-of-titanium-oxide-nanoparticles-synthesized-by-pulsed-laser-ablation-in-liquid/AE368446FAC70E08C514F9AEABFD131B DO - https://doi.org/10.1017/S1431927618009030 VL - 24 IS - S1 (August) SP - 1710 EP - 1711 PB - Cambridge University Press CY - New York, NY, U.S.A. AN - OPUS4-45949 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hodoroaba, Vasile-Dan A1 - Donėlienė1, J. A1 - Rudzikas, M. A1 - Rades, Steffi A1 - Dörfel, Ilona A1 - Peplinski, Burkhard A1 - Sahre, Mario A1 - Pellegrino, F. A1 - Maurino, V. A1 - Ulbikas, J. A1 - Galdikas, A. T1 - Electron Microscopy and X-Ray Diffraction Analysis of Titanium Oxide Nanoparticles Synthesized by Pulsed Laser Ablation in Liquid N2 - A femto-second pulsed laser ablation in liquid (PLAL) procedure for the generation of titanium oxide nanoparticles (NP) is reported with the purpose of understanding morphology and structure of the newly generated NPs. Ablation duration was varied for optimization of NP generation processes between 10 and 90 min. Surface morphology of NPs as well as their size and shape (distribution) were analysed by various complementary electron microscopy techniques, i.e. SEM, TSEM and TEM. The crystalline structure of titanium oxide particles was investigated by XRD and HR-TEM. Concentration of generated titanium oxide NPs in liquid was analysed by ICP-MS. A mix of crystalline (mainly anatase), partly crystalline and amorphous spherical titanium oxide NPs can be reported having a mean size between 10 and 20 nm, which is rather independent of the laser ablation (LA) duration. A second component consisting of irregularly shaped, but crystalline titanium oxide nanostructures is co-generated in the LA water, with more pronounced occurrence at longer LA times. The provenance of this component is assigned to those spherical particles generated in suspension and passing through the converging laser beam, being hence subject to secondary irradiation effects, e. g. fragmentation. T2 - Microscopy & Microanalysis 2018 CY - Baltimore, MD, USA DA - 05.08.2018 KW - Nanoparticles KW - Titanium oxide KW - Laser ablation in liquid KW - Electron microscopy KW - XRD PY - 2018 AN - OPUS4-46502 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kirner, Sabrina V. A1 - Slachciak, Nadine A1 - Elert, Anna Maria A1 - Griepentrog, Michael A1 - Fischer, Daniel A1 - Hertwig, Andreas A1 - Sahre, Mario A1 - Dörfel, Ilona A1 - Sturm, Heinz A1 - Pentzien, Simone A1 - Koter, Robert A1 - Spaltmann, Dirk A1 - Krüger, Jörg A1 - Bonse, Jörn T1 - Tribological performance of titanium samples oxidized by fs-laser radiation, thermal heating, or electrochemical anodization N2 - Commercial grade-1 titanium samples (Ti, 99.6%) were treated using three alternative methods, (i) femtosecond laser processing, (ii) thermal heat treatment, and (iii) electrochemical anodization, respectively, resulting in the formation of differently conditioned superficial titanium oxide layers. The laser processing (i) was carried out by a Ti:sapphire laser (pulse duration 30 fs, central wavelength 790 nm, pulse repetition rate 1 kHz) in a regime of generating laser-induced periodic surface structures (LIPSS). The experimental conditions (laser fluence, spatial spot overlap) were optimized in a sample-scanning setup for the processing of several square-millimeters large surface areas covered homogeneously by these nanostructures. The differently oxidized titanium surfaces were characterized by optical microscopy, micro Raman spectroscopy, variable angle spectroscopic ellipsometry, and instrumented indentation testing. The tribological performance was characterized in the regime of mixed friction by reciprocating sliding tests against a sphere of hardened steel in fully formulated engine oil as lubricant. The specific tribological performance of the differently treated surfaces is discussed with respect to possible physical and chemical mechanisms. KW - Femtosecond laser KW - Titanium KW - Oxidation KW - Friction PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-445609 DO - https://doi.org/10.1007/s00339-018-1745-8 SN - 0947-8396 SN - 1432-0630 VL - 124 IS - 4 SP - 326, 1 EP - 10 PB - Springer-Verlag AN - OPUS4-44560 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beck, Uwe A1 - Griepentrog, Michael A1 - Hertwig, Andreas A1 - Weise, Matthias T1 - White light interference microscopy, ellipsometry, and instrumented indentation testing as reference procedures N2 - The paper addresses “WHITE LIGHT INTERFERENCE MICROSCOPY, ELLIPSOMETRY, AND INSTRUMENTED INDENTATION TESTING AS REFERENCE PROCEDURES“ and is subdivided in the following sections: 1. Measurement vs. testing vs. reference procedures, 2. White light interference microscopy (WLIM) for determination of step height h, 3. Spectroscopic ellipsometry (SE) for determination of layer thickness d and 4. Instrumented indentation testing (IIT) for determination of indentation hardness HIT. The following points are discussed in more detail: methodology of measurement and testing, uncertainty budgets for direct (WLIM), model-based (SE) and formula-based (IIT) reference procedures by means of specific examples. It is shown that standardization efforts are connected to reference procedures. T2 - Referenzverfahren CY - BAM, Berlin, Germany DA - 21.02.2018 KW - Reference procedures KW - Uncertainty budgets KW - White light interference microscopy KW - Spectroscopic ellipsometry KW - Instrumented indentation testing PY - 2018 AN - OPUS4-44256 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -