TY - CONF A1 - Mieller, Björn T1 - Synthesis and testing of beta aluminate sodium electrolyte (BASE) for sodium ion battery development N2 - Sodium beta aluminate, or beta aluminate solid electrolyte (BASE), is an established material for tubular electrolytes in NaNiCl2 and NaS batteries, and a promising candidate for planar electrolytes in safe all solid-state batteries. The synthesis of BASE with high ionic conductivity is still challenging due to process dependent formation of different phases in the sintered material. However, to drive forward the development of active materials for all solid-state sodium ion batteries, the fabrication of solid electrolyte specimens with reproducible performance is required. With respect to the various testing scenarios in the field, for example cell assembly for cycling, electrolyte parts are needed in various shapes, sizes, and thicknesses in the lab. Different ceramic shaping technologies can be applied to produce such geometries, including pressing combined with green or hard machining, or tape casting combined with punching. Typically, different shaping technologies require adapted pre-treatment of the powder which might affect the resulting properties and thus need to be investigated. In this contribution, starting from the raw materials mixture, aspects of milling, drying, aqueous slurry preparation for tape casting, and firing are discussed with respect to particle size distribution, stability, energy consumption and resulting material properties. Finally, the fabrication and cyclic testing of Na/electrolyte/Na coin cells is presented. T2 - XIXth Conference of the European Ceramic Society / SBS6 International Sodium Battery Symposium CY - Dresden, Germany DA - 01.09.2025 KW - Ceramics KW - Beta aluminate solid electrolyte KW - Sodium ion battery PY - 2025 AN - OPUS4-64054 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Busch, Richard T1 - Surface Initiated Structure Formation in Glass Ceramics N2 - A summery of previous research regarding surface crystallization is given as well as results regarding thecurrent DFG project are presented. T2 - XRM Workshop CY - Halle, Germany DA - 03.03.2020 KW - Glass KW - Surface KW - XRM PY - 2020 AN - OPUS4-51337 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph T1 - Suitability of Metallic Materials in CC(U)S Applications N2 - Commercially available carbon steels are suitable for compression and pipelines as long as moisture content and impurities are limited. (water 50 to 100 ppmv, SO2 and NO2 ca. 100 ppmv). Corrosion rates increase with increasing water content. (0.2 – 20 mm/a). Condensation of acids and therefore droplet formation is always possible, even at low water contents. A low SO2 content within the CO2-stream might be more important than a low water content. Cr13-steels showed a general susceptibility to shallow pitting and pitting. So, they seem to be not suitable for CCUS applications. Low alloyed steels showed better corrosion behavior. � (predictable uniform corrosion) For direct contact with saline aquifer fluids only high alloyed steels shall be used. T2 - EUROCORR 2021 CY - Budapest, Hungary DA - 20.09.2021 KW - Carbon capture storage KW - Corrosion KW - Steel KW - CCS KW - CCU KW - CO2 PY - 2021 AN - OPUS4-53461 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph T1 - Study of Polyaniline/Silicon Dioxide based Coating on Carbon Steel in Artificial Geothermal Brine N2 - By using the available resources in Indonesia, such as silicon dioxide and marine coating base, the PANI/SiO2 modified alkyd coating was able to protect carbon steel in a deaerated artificial geothermal water. The screening of coatings shows that the modification by adding individual pigment was not sufficient to protect carbon steel even during a short-term exposure, indicated by the discoloration after only seven days of exposure. Electrochemical tests indicated that there was no significant change in the Ecorr between the coated and uncoated carbon steel at room temperature. At 150 °C, the coated carbon steel has a lower potential than that of carbon steel, indicating that the coating is protecting carbon steel cathodically or slowing down the corrosion reaction. Finally, a long-term exposure test confirmed that the PANI/SiO2 modified coating successfully protects the carbon steel in the Sibayak artificial geothermal water up to 150 °C for 6 months. T2 - World Geothermal Congress CY - Online meeting DA - 15.06.2021 KW - Coatings KW - Corrosion KW - Polyaniline KW - Sibayak KW - SiO2 KW - Geothermal PY - 2021 AN - OPUS4-52831 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Miliūtė, Aistė T1 - Structural evolution of ZrV2O7: supercell persistence revealing local and global structure duality N2 - In the AM2O7 family of negative thermal expansion materials (NTE), evidence of supercell at room temperature was reported following the Völlenke et al. discovery of missed superlattice due to the apparent linearity of the M-O-M bond in GeP2O7. Korthuis et al. and Khosrovani et al. demonstrated it to be true for cubic ZrV2O7 as well. It was concluded that at room temperature, the structure consists of 27 'subcells' with bent M2O7 groups that appear to form a linear configuration due to refinement of averaged position. However, around 100 °C, the transition to the “parent” cell was reported, where the cell volume increases, and the M-O-M angles are constrained by the Pa-3 space group symmetry to be 180°. We followed structural changes in the ZrV2O7 at high temperatures to demonstrate partial disorder within the crystal, local and global structural duality and supercell persistence at high temperatures. Total scattering measurements and Pair Distribution Function (PDF) analysis revealed that the experimental pattern cannot be fitted with the “parent structure” model, and only the 3×3×3 supercell model can correspond to local and global structures throughout the full 25-700 °C temperature range. We also show how short and long-range order within the crystal changes when approaching the phase transition, which might indicate the existence of coherent structural domains that evolve between order and disorder with increasing temperature. We further hypothesize how this can be related to the negative thermal expansion mechanism and the interpretation of structure solutions presenting data from high-temperature X-ray absorption fine structure (XAFS) and Transmission Electron Microscopy (TEM) measurements. T2 - 5th International Symposium on Negative Thermal Expansion and Related Materials (ISNTE-5) CY - Porto, Portugal DA - 29.07.2025 KW - NTE KW - Ab initio KW - PDF KW - CSM PY - 2025 AN - OPUS4-63874 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gadelmeier, C. T1 - Strengthening mechanisms of single crystalline CrCoNi and CrMnFeCoNi at creep temperatures above 700 °C N2 - The main deference between high entropy alloys and conventional alloys is the solid solution strengthening effect, which moves from a single element to a multi-element matrix. Little is known about the effectiveness of this effect at high temperatures. Investigation of temperature dependent solid solution strengthening in single phase multicomponent alloys with medium and high entropy using creep testing was performed. Creep tests carried out on single phase SX CrCoNi , CrMnFeCoNi and pure Ni from 700 to 1200 °C excluding oxidation, grain boundaries and multiphase effects. It was found that the influence of solid solution strengthening of CrCoNi and CrMnFeCoNi increases by decreasing temperature (1200 to 700 °C), and dislocation forests occur in CrCoNi and CrMnFeCoNi in comparison to pure Ni. T2 - SPP Kick-Off Meeting 2nd Phase CY - Online meeting DA - 14.04.2021 KW - High entropy alloys KW - Mechanical properties KW - Transmission electron microscopy KW - Solid solution strengthening PY - 2021 AN - OPUS4-54381 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Marschall, Niklas T1 - Spinodal Decomposition in FeMnNiCoCu: Alloying effects N2 - Spinodal decomposition in multi-component alloys remains insufficiently understood, particularly when multiple driving forces govern phase evolution. Chemical thermodynamics provides reliable predictions of spinodal instabilities, but elastic energy contributions can significantly alter the boundaries of phase stability. In this work, we establish a framework to analyze phase stability in high-entropy alloys by combining Hessian-based spinodal analysis with convex hull constructions that capture miscibility gaps. This approach allows us to disentangle the roles of chemical, elastic, and kinetic factors in early-stage decomposition. Our results highlight how elastic contributions can extend the effective spinodal region beyond chemically predicted boundaries, thereby influencing microstructural pathways. This combined stability analysis offers new insights into the mechanisms governing decomposition and advancing the theoretical understanding of phase evolution in high-entropy alloys. T2 - FEMS EUROMAT 2025 CY - Granada, Spain DA - 14.09.2025 KW - High-entropy alloy KW - Elasticity KW - Phase stability KW - Hessian KW - Convex hull PY - 2025 AN - OPUS4-64263 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sonntag, U. T1 - Softwaregestützte Bestimmung von Bruchmechanismen und Bruchflächenmerkmalen mittels Machine Learning und Topographie-Informationen N2 - Ziel von fraktographischen Untersuchungen ist die Auswertung von makroskopischen und mikroskopischen Bruchflächenmerkmalen und daraus resultierend die Bestimmung des Bruchmechanismus eines Bauteils aus einem Schadensfall. Die Grundlage für die Bewertung von Bruchmerkmalen stammt dabei aus zuvor durchgeführten eigenen Vergleichsversuchen und aus der Literatur. Eine fraktographische Analyse kann sehr aufwändig sein und setzt in jedem Fall erhebliches Erfahrungswissen voraus. Im IGF-Vorhaben „iFrakto“ wird Software entwickelt, die auf Basis von digitalisiertem Expertenwissen, Machine Learning und unter Zuhilfenahme von Topographie-Daten anhand von REM-Aufnahmen Bruchmerkmale und Bruchmechanismen quantitativ bestimmt, s. Abbildung. Solche Software soll mittelfristig direkt am REM oder bei der nachfolgenden Auswertung wissensbasierte Vorschläge für die Bewertung von Bruchflächen liefern. Als Grundlage hierfür wurden Ringversuche unter Fraktograph/inn/en durchgeführt, um die Wissensbasis zu schaffen, die praxisrelevanten Anforderungen an solche Software abzufragen und erste Praxistests durchzuführen. Die bisherigen Ergebnisse werden vorgestellt und die Relevanz der Auswertestrategie und unterschiedlicher Sensordaten bewertet. T2 - 56. Metallographie-Tagung CY - Saarbrücken, Germany DA - 21.9.2022 KW - Fraktographie KW - Machine Learning KW - Topographie PY - 2022 AN - OPUS4-55939 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heuser, Lina T1 - Sintering of silver‑alkali zinc borate glass‑composites N2 - Since decades electric contacts based on silver metallization pastes are key components of photovoltaics and advanced microelectronics. For the metallization of commercial Si solar cells, high conductive silver glass pastes are cost effectively applicated by screen printing. Nevertheless, silver pastes are still one of the most crucial and expensive none Si materials in solar cells. Ever shorter time to market as well as increasing demands on reduced Ag consumption and line width require the targeted development of silver-glass-pastes with increased sinter ability and electrical conductivity. As a main difficulty, however, the liquid phase sintering of silver glass pastes is poorly understood so far. In the present study, the influence of different network modifier in alkali-zinc-borate paste glasses on liquid phase sintering of silver-glass-pastes was investigated. Low melting X2O-ZnO-B2O3 glasses with X = Na, Li and Rb (abbr. LZB, NZB, and RZB) were utilized to prepare silver-glass-composites containing 30 %Vol glass. Shrinkage behavior of the silver-glass-composites compared with that of pure silver and pure glass powder compacts was studied with heating microscopy. The powder compacts were uniaxially pressed and heated at 5 K/min to the glass softening temperature. Glass transformation temperature and viscosity of the glasses were respectively measured with dilatometry and rotational viscometry. The thermal behavior of the pure glasses was analyzed with thermal analysis. Additionally, the contact angle of glass on pure silver foil was determined by means of heating microscopy between room temperature and 830 °C. Thermal analysis of the alkali-zinc-borate-glasses under study has shown transformation temperatures between 450 °C (RZB), 460 °C (LZB) and 465 °C (NZB). For all glasses crystallization was found to start approximately at about 550 °C. However, different peak areas hint on a different degree of crystallization. Conformingly, the sintering behavior, measured in terms of area shrinkage, significantly differed for the silver-pastes under study. For silver-pastes with NZB or LZB-glass, sintering starts at 464 °C for NZB Ag pastes and at 451 °C for LZB Ag pastes and ends at 597 °C for NZB Ag paste and at 594 °C for LZB Ag paste. The sintering of the RZB Ag paste proceeds between 426 °C and 703 °C. The final densification was retarded possibly due to crystallization or swelling. The low sinter onset at 426 °C seems to correlate with the good wetting behavior of the RZB glass. Thus, the lowest apparent contact angle between the just densified powder compact sintered at a silver substrate was found for this glass. Moreover, microstructure analyses of the various composites indicate differences in silver dissolution and reprecipitation. T2 - Technology Crossover Extravaganza, HiTEC/CICMT/APEPS CY - Online meeting DA - 26.04.2021 KW - Silver-glass-metallization-paste KW - Sintering KW - Crystallization KW - Alkali ions KW - Sintering atmosphere PY - 2021 AN - OPUS4-52872 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heuser, Lina A1 - Sobek, P. T1 - Sintering of silver-alkali zinc borate glass composites N2 - High conductive silver-glass-metallization-pastes are key components in photovoltaics and advanced microelectronics. However, the underlying mechanisms of liquid phase sintering as silver dissolution, diffusion and reprecipitation are poorly understood so far. In the current work, the influence of different network modifier in alkali-zinc-borate paste-glasses on liquid phase sintering of silver-glass-composites was studied. Therefore, silver-glass-composites containing 30 vol% glass were prepared, using low melting X2O-ZnO-B2O3 glasses with X = Na, Li, and Rb (NZB, LZB, and RZB). Glass transition temperature, viscosity, glass-silver wetting, crystallization and sintering behavior was studied by means of thermal analysis, dilatometry, heating microscopy and microscopy. Similar glass transition temperatures of 450 °C (RZB), 460 °C (LZB) and 465 °C (NZB) were found by means of thermal analysis for glasses under study. Also, all glasses have a similar crystallization onset at about 550 °C, even though exhibiting with a different degree of crystallization. Despite these similarities, however, the sintering behavior, measured in terms of area shrinkage, significantly differs for the composites. This finding indicates a different degree of silver dissolution. Assuming that dissolved silver reduces the viscosity, this effect could explain why glass crystallization starts at lower temperature in the composites. For example, the crystallization peak of LZB at 629 °C measured for pure glass powder compacts was decreased to 586 °C for the composite. Confirmatively, microstructure analyses indicate different degrees of silver dissolution, as e.g. revealed by different amount of silver precipitates within the residual glass phase, and reprecipitation. Best silver dissolution appeared for the RZB glass. Nevertheless, the final densification of RZB was retarded probably due to swelling and crystallization. T2 - XRM Workshop CY - Halle, Germany DA - 03.03.2020 KW - Silver-glass-metallization-paste KW - Sintering KW - Alkali ions PY - 2020 AN - OPUS4-51243 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Ralf T1 - Sintering and Foaming of Silicate Glass Powders N2 - The lecture focuses on the mechanisms of non-desired gas bubble formation and foaming during the sintering of glass powder compacts. It is shown that foaming is driven by carbon gases and that carbonates, encapsulated in micropores or mechaniacally dissolved beneath the glass surface, provide the major foaming source. T2 - Sandanski Workshop Sinter crystallization 27th-29th September 2021 PROJECT “THEORY AND APPLICATIONS OF SINTER-CYSTALLIZATION” DN 19/7 CY - Online meeting DA - 27.10. 2021 KW - Sintering KW - Non-desired foaming PY - 2021 AN - OPUS4-53772 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heuser, Lina T1 - Silver in low-melting alkali zinc borate glasses N2 - Ein aktuelles Forschungsziel ist die Substitution von Bleioxid in niedrig schmelzenden Gläsern z.B. zur Anwendung in Silber-Metallisationspasten. Im Fokus steht hier die Untersuchung der Silberdiffusion in Alkali-Zink-Boratgläsern (X2O-ZnO-B2O3, X = Li, Na, K, Rb). Zudem wird der Redoxzustand des Silbers (Ag) und somit die Art der diffundierenden Silberspezies bestimmt. Hierzu wurde eine metallische Silberschicht mittels Sputterns auf Glaswürfel aufgebracht. Die Wärmebehandlung erfolgte nahe der Glasübergangstemperatur bei 470 °C über 2 h unter Luft und Stickstoffatmosphäre. Die Schichtdicke der Silberbeschichtung betrug 1.8 µm nach der Wärmebehandlung, gemessen mittels Weißlicht-Interferometer. Die Silberdiffusionsprofile wurden mittels Sekundär-Neutral-Teilchen-Massenspektrometrie gemessen. Die Diffusionskoeffizienten des Silbers liegen in der Größenordnung von ~10-14 cm2/s und unterscheiden sich nur gering in Abhängigkeit des Alkali-Ions im Glas. Mittels Fluoreszenz-Spektroskopie ließen sich gelöste Ag+-Ionen und [Agm]n+-Cluster nach der Wärmebehandlung unterscheiden. Zusätzlich konnten ausgeschiedene metallische Silber-Partikel im Natrium-enthaltenden Glas mittels Transmissionselektronenmikroskopie beobachtet werden. Diese haben einen mittleren Durchmesser von ~6 nm. N2 - Substitution of lead oxide in low-melting glasses, e.g., for application in silver metallization pastes, is a current research goal. This work is focused on the investigation of silver diffusion in alkali zinc borate glasses (X2O-ZnO-B2O3, X = Li, Na, K, Rb). In addition, the redox state of silver (Ag) and thus the type of diffusing silver species were studied. For this purpose, a metallic silver coating was applied on glass cubes by means of sputtering. Heat treatment of the samples was performed close to the glass transition temperatures at 470 °C for 2 h under air and nitrogen atmosphere. Coating thickness was 1.8 µm after heat treatment, measured by a white light interferometer. Silver diffusion profiles were measured by means of secondary neutral mass spectrometry. The silver diffusion coefficients are in the range of ~10-14 cm2/s and indicate no significant differences depending on the type of alkali ions in the glass. Dissolved Ag+-ions and [Agm]n+-clusters in the glasses were differentiated using fluorescence spectroscopy. Precipitated metallic silver particles in the sodium containing glass were observed by means of transmission electron microcopy. Their mean particle diameter was ~6 nm. T2 - Living Glass Surfaces XI - Year of Glass CY - Ilmenau, Germany DA - 14.09.2022 KW - Alkali zinc borate glasses KW - Silver diffusion KW - Transmission electron microscopy KW - Fluorescence spectroscopy KW - Silver cluster PY - 2022 AN - OPUS4-55736 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heuser, Lina T1 - Silver diffusion in low-melting alkali zinc borate model glasses studied by means of SNMS, TEM and XAS N2 - In many late-breaking research fields as in photovoltaics, microelectronics, nuclear waste glasses or at least mirror glasses silver diffusion in glasses is relevant to the issues of high-level functionality and recycling. The present study is focused on silver diffusion in innovative, low-melting alkali zinc borate glasses (X2O-ZnO-B2O3, X = Li, Na, K, Rb) potentially usable for silver metallization-pastes in solar cells. The glasses were coated with a thin metallic silver layer and heat treatments in air and nitrogen close to Tg at 470 °C for 2 h were performed. After heat treatment under air and nitrogen atmospheres the coating thickness, measured by a white light interferometer, was about 1.8 µm thick. Silver depth profiles determined by means of secondary neutral mass spectrometry (SNMS) indicate the fastest silver diffusion to a depth of 3.5 µm for Li2O-ZnO-B2O3 (LZB) glass. Nevertheless, the influence of the different alkali ions on the silver diffusion is small. The oxygen availability determines the silver diffusion into the glasses. The oxygen promotes the oxidation of the silver layer enabling Ag+ to diffuse into the glass and to precipitate as Ag0. Both species were detected by x-ray absorption spectroscopy (XAS). The precipitated metallic silver particles in Na2O-ZnO-B2O3 (NZB) glass have a mean size of 5.9 nm ± 1.2 nm diameter, which was determined using transmission electron microscopy (TEM). Phase separation in zinc-rich and zinc-poor phases with a mean diameter of 75 nm ± 20 nm occurred in NZB glass after heat treatment. Ion diffusion of the glasses into the silver layer was suggested by EDX-line scans. T2 - 94. Glastechnische Tagung CY - Online meeting DA - 10.05.2021 KW - Silver diffusion KW - Alkali zinc borate glass KW - Metallic silver precipitates KW - Phase separation PY - 2021 AN - OPUS4-52861 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heuser, Lina T1 - Silver - alkali borate glass pastes N2 - Network modifier ions can decisively influence properties and structure of low melting alkali-zinc-borate glasses and thus cause complex effects on the liquid phase sintering of silver-glass metallization pastes. This effect was studied for X2O-ZnO-B2O3 (X = Li, Na, Rb) glasses for silver-glass metallization pastes. Viscosity and the glass transition temperature, Tg, were measured with rotational viscometry and dilatometry. Dried model pastes with 30 vol% LZB, NZB or RZB glass were prepared for sintering studies by means of heating microscopy measuring the silhouette area shrinkage of uniaxially pressed powder compacts during heating at 5 K/min. For comparison, the silhouette area shrinkage of pure glass and silver powder compacts were determined. Glass-silver wetting was investigated during heating of bulk glass cylinders placed on silver substrates. Glass RZB turned out to have the lowest viscosity among the glasses under study. Its glass transformation temperature, Tg, was found at 444 °C and it caused the lowest sintering onset for its glass and paste powder compacts. Slightly increased values of Tg were found for NZB and LZB (468 °C and 466 °C, respectively) and a slightly retarded sintering was found for both paste powder compacts. These results indicate that liquid phase sintering of silver-glass pastes under air atmosphere is mainly influenced by glass viscosity. T2 - GLASS MEETING 2020 CY - Online meeting DA - 07.12.2020 KW - Silver-glass metallization paste KW - Sintering KW - Alkali ions KW - Viscosity KW - Silver precipitates PY - 2020 AN - OPUS4-52871 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Werner, Tiago T1 - Short fatigue crack propagation in L-PBF 316L stainless steel N2 - Fracture mechanics is a key to fatigue assessment in AM metal components. Short fatigue cracks are initiated at defects and pronounced surface roughness intrinsic to AM. The subsequent crack-propagation is strongly influenced by microstructural interactions and the build-up of crack-closure. The aim of the present study is to give an insight into short-crack propagation in AM-metals. Fatigue crack propagation resistance curves were determined experimentally for AISI 316L manufactured by Laser Powder Bed Fusion (L-PBF) which was heat treated at three different temperatures. Differences in the build-up of the fatigue-crack propagation threshold in between the L-PBF specimens and compared to wrought material are due to the residual stress states, a pronounced roughness of the crack-faces in the L-PBF specimens and phase transformation in the vicinity of the crack-tip, resulting in increased crack-closure. This, together with crack-branching found along the crack path, enhances the resistance to the propagation of fatigue cracks. T2 - ASTM International Conference on Additive Manufacturing 2020 CY - Online meeting DA - 16.11.2020 KW - Additive Manufacturing KW - Cyclic R-Curve KW - Component assessment KW - L-PBF KW - 316L KW - Residual Stress KW - Fatigue Crack Growth PY - 2020 AN - OPUS4-51585 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mishurova, Tatiana T1 - Separation of the impact of residual stress and microstructure on the fatigue performance of LPBF Ti-6Al-4V at elevated temperature (Keynote) N2 - Ti-6Al-4V alloy is intensively used in the aerospace industry because of its high specific strength. However, the application of Laser Powder Bed Fusion (LPBF) Ti-6Al-4V alloy for structurally critical load-bearing components is limited. One of the main limiting factors affecting the structural integrity, are manufacturing defects. Additionally, the high cooling rates associated with LPBF process result in the formation of large residual stress (RS) with complex fields. Such RS can cause cracking and geometrical distortions of the part even right after production. Also, the microstructure of LPBF Ti-6Al-4V in the as-built condition is significantly different from that of the conventionally produced alloy. All these factors affect the mechanical behavior of the material. Therefore, to improve the material performance it is important to evaluate the individual effect of RS, defects, and microstructure on fatigue life. To this aim Ti-6Al-4V LPBF material in as-built condition and subjected to different post-processing, including two heat treatments (for stress relief and microstructural modification) and Hot Isostatic Pressing (HIP, for densification), were investigated. Prior to fatigue tests at elevated temperature, the microstructure, the mesostructure, and subsurface RS on the fatigue samples were investigated. It was found that the fatigue performance of HIPped samples is similar to that of conventionally produced Ti-6Al-4V. The tensile RS found at the surface of as-built samples decreased the fatigue life compared to heat-treated samples. Additionally, the modification of the microstructure (by heat treatment) did not affect the fatigue performance in the regime of mostly elastic strain. This shows that in the absence of tensile RS the manufacturing defects solely control the failure of LPBF components and densification has the strongest effect on the improvement of the mechanical performance. T2 - EUROMAT 2021 CY - Online meeting DA - 12.09.2021 KW - Additive manufacturing KW - Ti-6Al-4V KW - Residual stress KW - Fatigue performance PY - 2021 AN - OPUS4-53278 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schilling, Markus T1 - Semantic Technologies in Action: Integrating Mechanical and Microstructure Data in MSE N2 - Semantic technologies (ST) are a powerful tool for storing, processing, and querying data in a contextualized and interoperable manner. They enable machine-actionable and human-readable knowledge representations essential for advanced data management, retrieval, and reuse. As one of the key factors within the frame of the collaborative project platform MaterialDigital (PMD), the establishment of a virtual material data space and the semantic modeling of hierarchical, process-dependent material data is aimed at to serve as best-practice examples of knowledge representation through ontologies and knowledge graphs. In this presentation, the application of ST to a specific use case from the field of materials sciences and engineering (MSE) is demonstrated: the integration and analysis of data related to a 2000 series age-hardenable aluminum alloy. By semantically representing mechanical and microstructural data obtained from tensile tests and dark-field transmission electron microscopy across various aging times, an expandable knowledge graph was constructed that is aligned with the PMD Core Ontology (PMDco) and enriched through the Tensile Test (TTO) and Precipitate Geometry Ontologies. This semantically integrated dataset enables advanced analytical capabilities via SPARQL queries and reveals microstructure–property relationships consistent with the well-known Orowan mechanism. The approach highlights the potential of semantic data integration to support FAIR data principles and to foster a more data-centric and interoperable research infrastructure in MSE. T2 - MSE Research Data Forum 2025 CY - Siegburg, Germany DA - 08.07.2025 KW - Semantic Data KW - Data Integration KW - Digitalization KW - Data Interoperability PY - 2025 AN - OPUS4-63666 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schilling, Markus T1 - Semantic Technologies for Digital Transformation in Materials Science: From PMDco to Prototypical Applications N2 - The digital transformation of Materials Science and Engineering (MSE) is accelerating the adoption of structured, interoperable, and FAIR data practices, in particular with respect to an advanced research data management. Semantic technologies play a pivotal role in this transformation, as the enable the integration, contextualization, and automation of diverse data sources across experimental, computational, and simulation domains. Central to these efforts is the Platform MaterialDigital Core Ontology (PMDco), now in version 3.0, which provides a robust mid-level semantic framework tailored for MSE. PMDco bridges abstract high-level ontologies, such as the Basic Formal Ontology (BFO) standardized in ISO/IEC 21838-2, with domain-specific terminologies to ensure consistency and interoperability across applications. This presentation explores the application of PMDco and its integration into workflows within the Platform MaterialDigital (PMD) initiative. Through its deployment in electronic laboratory notebooks (ELNs), PMDco enables semantic representation of experimental data, such as tensile test results compliant with ISO 6892-1:2019-11, transforming them into machine-actionable knowledge graphs. Prototypical implementations demonstrate how semantic technologies enhance laboratory processes, improve data reuse, and streamline documentation which offers opportunities for automation and education. Further extending its versatility, PMDco serves as a linking point for semantically representing simulation data, enabling comprehensive integration of experimental and computational datasets. This creates structured data spaces that support advanced digital workflows. Beyond PMDco, the presentation highlights the design of graph patterns and semantic shapes, showcasing generalizable methods for managing diverse data in MSE being based on data structuring and formatting. By presenting best practices in ontology development, data acquisition, and knowledge graph generation, this talk underscores the transformative potential of semantic technologies in MSE. It offers a forward-looking perspective on the role of structured data spaces as a driver for innovation, ensuring that materials science continues to advance through rigorous, interoperable, and automated digital methodologies. T2 - FEMS Euromat 2025 CY - Granada, Spanien DA - 14.09.2025 KW - Semantic Data KW - Data Integration KW - Digitalization KW - Data Interoperability KW - PMD Core Ontology KW - Graph Patterns PY - 2025 AN - OPUS4-64165 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schilling, Markus T1 - Seamless Science: Navigating Daily Lab Life through Semantic Data Integration, Electronic Lab Notebooks, and Knowledge Graphs in the Era of MSE Digitalization N2 - The field of materials science and engineering (MSE) is currently experiencing a significant paradigm shift towards enhanced digitalization which imposes a huge challenge on researchers, scientists, engineers, and technicians. In this respect, the quality assurance of processes and output data as well as the interoperability between applications following FAIR principles are to be ensured. For storage, processing, and querying of data in contextualized form, Semantic Web technologies (SWT) are used as they allow for machine-actionable and human-readable knowledge representations needed for data management, retrieval, and (re)use. The collaborative project ‘platform MaterialDigital’ (PMD) aims to solve digitalization tasks and implement digital solutions in the field of MSE in a prototypical manner. Therefore, the establishment of a virtual material data space and the systematization of the handling of hierarchical, process-dependent material data are focused. In this respect, selected MSE methods are semantically represented which are supposed to serve as best practice examples with respect to knowledge representation and the creation of knowledge graphs used for material data. Accordingly, this presentation shows the efforts taken within PMD to store data in accordance with a testing standard compliant semantic representation of a tensile test of metals at room temperature (ISO 6892-1:2019-11). A semantic link of the corresponding tensile test ontology (TTO) and data leads to enhanced data useability and interoperability. The PMD core ontology (PMDco), developed in PMD and used as mid-level ontology in TTO, is also presented briefly. Moreover, as a best practice example, the acquisition of tensile test data with subsequent generation of knowledge graph data by semantic interconnection using TTO was realized by applying an electronic laboratory notebook (ELN). Corresponding tensile tests were performed by undergraduate MSE students at the Technical University of Darmstadt. The resulting data pipeline, also illustrated in the presentation, enabled a fully-fledged digitally integrated experimental procedure, the approach of which may be transferred to other test series and experiments. In addition to facilitating the acquisition, analysis, processing, and (re)usability of data, this also raises the awareness of students with respect to data structuring and semantic technologies in terms of education and training. T2 - Materials Science and Engineering Congress 2024 CY - Darmstadt, Germany DA - 24.09.2024 KW - FAIR KW - Plattform Material Digital KW - Digitalization KW - Data Interoperability KW - Electronic Lab Notebook KW - Education PY - 2024 AN - OPUS4-61138 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bettge, Dirk A1 - Klinger, Christian T1 - Schadensanalyse an Fahrradkomponenten - Fraktographie, Ursachen, Prävention N2 - Komponenten von Fahrrädern werden im Betrieb vorwiegend schwingend beansprucht. Typische Werkstoffe sind Stahl, Aluminiumlegierungen, Messing, CFK und thermoplastische Kunststoffe. Da es sich, unabhängig von der Preiskategorie, um konstruktiven Leichtbau handelt, werden einige Bauteile betriebsfest mehr oder weniger weit oberhalb der Dauerfestigkeit ausgelegt. Die im normalen Betrieb auftretenden Schäden sind daher weit überwiegend Schwingbrüche. Andere Schadensmechanismen wie z.B. Korrosion spielen quantitativ eine untergeordnete Rolle. Schwingbrüche treten nach einer Periode unbemerkten Risswachstums oft ohne Vorwarnung und ohne makroskopische Verformung auf. Im Falle von sicherheitsrelevanten Komponenten wie Rahmen, Gabeln, Lenkern, Sattelstützen, Kurbelarmen oder Pedalen kann dies zu erheblichen Personenschäden führen, die den Wert des ursächlichen Bauteilschadens weit überschreiten. Über einen langjährigen Zeitraum wurden gebrochene Komponenten aus dem Alltag und aus Gerichtsverfahren analysiert. Das Hauptaugenmerk lag hierbei auf der fraktographischen Analyse, teilweise wurden die zu Grunde liegenden Schadensursachen ermittelt. Einflussfaktoren sind beispielsweise konstruktive Kerben an ungünstigen Stellen, aber auch Werkstoffwahl und Fertigungsqualität spielen eine Rolle. In den meisten Fällen wurde jedoch die konstruktive Lebensdauer überschritten. Diese wird praktisch nie mitgeteilt, und eine wiederkehrende Prüfung sicherheitsrelevanter Bauteile findet nicht statt. Im Sinne der Vermeidung von Schäden und Unfällen könnte darauf hingewirkt werden, für sicherheitsrelevante Komponenten Lebensdauern besser abzuschätzen und von der Laufleistung abhängige Sichtprüfungen zu empfehlen. T2 - DGM Tagung Werkstoffprüfung CY - Dresden, Germany DA - 26.10.2022 KW - Fraktographie KW - Fahrrad KW - Lebensdauer KW - Öffentliche Sicherheit KW - Schadensanalyse KW - Schadensprävention PY - 2022 AN - OPUS4-56122 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -