TY - CONF A1 - Suárez Ocano, Patricia T1 - I n situ monitoring of growing oxidation of the chemically complex alloy AlMo 0.5 NbTa 0.5 TiZr in the high temperature regime using synchrotron radiation Preliminary results N2 - The chemically complex alloys (CCAs) that contain mostly refractory elements (rCCAs), may be highly resistant to heat and load, which makes them attractive candidates for use at extremely high temperatures associated with many technological applications, e.g. aeroengine turbines. However, the field of CCAs, especially their resistance in harsh (oxidative) and hot environment is still young and not much experimental evidence for the understanding mechanisms in this regime is available, which the proposed study addresses. For safe use in structural applications, in addition to their mechanical performance, the environmental resistance of this alloy is also critical. Surface degradation can significantly decrease the mechanical resistance during high temperature exposure, leading to premature failure. The AlMo0.5NbTa0.5TiZr rCCA only contains Al as a protection candidate and it is composed of a coherent B2/bcc nanoscopic cube-on-cube interweave and an hexagonal phase. The evaluation of the oxidation process in the AlMo0.5NbTa0.5TiZr rCCA in the heat-treated state has not been assessed yet. The proposed study focusses on a deeper understanding of the formation mechanism and growth kinetics of oxides at high temperature in the AlMo0.5NbTa0.5TiZr rCCA using synchrotron radiation. Due to the envisaged high temperature structural applications, the alloy is evaluated in an oxidation environment specifically between 800°C and 1000°C. T2 - Large scale facility-based techniques SPP meeting CY - Online meeting DA - 02.11.2021 KW - Refractory chemically complex alloys KW - Oxidation behavior KW - Microstructural analysis KW - Synchrotron radiation PY - 2021 AN - OPUS4-54383 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Suárez Ocano, Patricia A1 - Gadelmeier, C. A1 - Gratzel, U. A1 - Agudo Jácome, Leonardo T1 - Creep Properties of the Refractory Chemically Complex AlMo 0.5 NbTa 0.5 TiZr Alloy N2 - The development of refractory CCAs has been explored for potential use in high temperature applications. An example of this is the AlMo0.5NbTa0.5TiZr alloy, which resembles the well-known γ/γ’ microstructure in Ni-Base superalloys with cuboidal particles embedded in a continuous matrix. The aim of this work is to evaluate the alloy’s mechanical behavior under tension in the temperature range 800-1000°C, by applying creep tests under vacuum (excluding oxidation effects). Some little temperature influence on minimum creep rate @ 1000 and 1100 °C was found and at a first glance, and Norton plots shows that deformation is probably both diffusion and dislocation controlled. However, further work is needed to stablish deformation and degradation micro mechanisms in the studied creep regime. T2 - SPP Kick-Off Meeting 2nd Phase CY - Online meeting DA - 14.04.2021 KW - Creep behavior KW - Chemically complex alloy KW - Microstructure PY - 2021 AN - OPUS4-53389 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bayerlein, Bernd A1 - Schilling, Markus A1 - Olbricht, Jürgen A1 - Skrotzki, Birgit A1 - Portella, Pedro Dolabella A1 - Hartrott, P. A1 - Hadzic, N. A1 - Todor, A. A1 - Birkholz, H. A1 - Grundmann, J. T1 - Digitalisierung der Materialien in PMD & Mat-o-Lab - Eine normkonforme Anwendungsontologie des Zugversuchs N2 - Zur Bewältigung der Herausforderung bei der Digitalisierung von Materialien und Prozessen ist eine mit allen Stakeholdern konsistente Kontextualisierung von Materialdaten anzustreben, d.h. alle erforderlichen Informationen über den Zustand des Materials einschließlich produktions- und anwendungsbezogener Änderungen müssen über eine einheitliche, maschinenlesbare Beschreibung verfügbar gemacht werden. Dazu werden Wissensrepräsentationen und Konzeptualisierungen ermöglichende Ontologien verwendet. Erste Bemühungen in den beiden Projekten Plattform Material Digital und Materials-open-Laboratory führten zur Erstellung von Anwendungsontologien, die Prozesse und Testmethoden explizit beschreiben. Dabei wurde u.a. der Zugversuch an Metallen bei Raumtemperatur nach DIN EN ISO 6892-1 ontologisch beschrieben. Diese als Beispiel dienende Ontologieentwicklung wird in dieser Präsentation vorgestellt. T2 - Werkstoffprüfung 2021 CY - Online meeting DA - 02.12.2021 KW - Ontologie KW - Semantisches Web KW - Wissensrepräsentation KW - Digitalisierung KW - Zugversuch PY - 2021 AN - OPUS4-53929 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Agudo Jácome, Leonardo T1 - Navigating the Nanoworld: Understanding Materials Properties with the Transmission Electron Microscope N2 - The field of materials science is defined as “the study of the properties of solid materials and how those properties are determined by a material’s composition and structure.”. Many –if not most– of the materials that are produced nowadays owe their properties to structures engineered down to the nanoscopic level. This need has been partly realized thanks to the understanding of materials’ building blocks via characterization techniques that reach this level of resolution. Transmission electron microscopy, since its first implementation in the early 1930s (in Berlin), has been implemented to achieve imaging –and spectral– analysis at lateral resolutions down to the atomic level. In this contribution, a series of practical examples will be presented, where applied materials are characterized by a range of transmission electron microscopy techniques to understand structural and functional properties of a wide range of materials. Among these materials examples will be presented on structural conventionally and additively manufactured metallic alloys, high entropy alloys, dissimilar aluminum-to-steel welds, magnetic nanoparticles, ceramic coatings, high temperature oxidation products. Addressed will be either the effect of processing route or that of the exposure to experimental conditions similar to those found in the respective intended applications. T2 - UA/UAB/UAH MSE Graduate Seminar CY - Online meeting DA - 19.01.2022 KW - Transmission electron microscopy (TEM) KW - Characterization KW - Microstructure KW - 3D PY - 2022 AN - OPUS4-54238 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmies, Lennart A1 - Bettge, Dirk A1 - Yarysh, Anna A1 - Sonntag, U. A1 - Botsch, B. A1 - Hemmleb, M. T1 - Using Machine Learning and Topographic SEM Imaging for Software Assisted Fractography N2 - The aim of a fractographic investigation is the evaluation of macroscopic and microscopic fracture surface characteristics and, as a result, the determination of the fracture mechanism of a component from a failure case. The basis for such evaluations of fracture characteristics comes from actual comparative mechanical testing and from the literature. A fractographic analysis can be very complex and, in any case, requires considerable experience. In the IGF project "iFrakto", software is being developed that quantitatively determines fracture characteristics and fracture mechanisms utilizing digitized expert knowledge, machine learning, and standard 2D and topographical data from SEM imaging. Topographical data are obtained from 4QBSE detector using shape-from-shading technology. In the medium term, a software tool should provide knowledge-based suggestions for the evaluation of fracture surfaces in real time during SEM work or at subsequent evaluation. As a basis for this, round robins were carried out among fractographers in order to create a knowledge base, to query the practice-relevant requirements for such tools and to carry out first practical tests. Actual results are presented and the relevance of the evaluation strategy is evaluated. T2 - Material Science and Engineering 2022 CY - Darmstadt, Germany DA - 27.9.2022 KW - Fractography KW - Machine Learning KW - Topography PY - 2022 AN - OPUS4-55938 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hemmleb, M. A1 - Bettge, Dirk A1 - Schmies, Lennart A1 - Sonntag, U. A1 - Botsch, B. T1 - Integrated topographic SEM imaging for software assisted fractography N2 - The aim of a fractographic investigation is the evaluation of macroscopic and microscopic fracture surface characteristics and, as a result, the determination of the fracture mechanism of a component from a failure case. The basis for such evaluations of fracture characteristics comes from actual comparative mechanical testing and from the literature. A fractographic analysis can be very complex and, in any case, requires considerable experience. Machine learning methods enables the quantitative determination of fracture characteristics and fracture mechanisms utilizing digitized expert knowledge [1]. Although the application of SE images provides promising results, additional information is required to obtain reliable solutions. As expected, BSE and 3D information helps to improve the classification (Fig. 1). But only a fast, widely integrated, and automated topography measurement can provide the required amount of referenced surface data for the application of machine learning methods. To fulfil these requirements, topographical data are obtained from a BSE detector with four symmetric segments (4Q-BSE) using shape-from-shading technology [2]. Surface height calculation is performed live during image acquisition and provides immediate feedback in three dimensions. All available signals (SE, BSE and more if applicable) are recorded simultaneously together with the surface topography and stored in a multichannel data file. This guaranties the same geometrical reference for all data, which is required for further analysis (Fig. 2). When applying machine learning methods to topographic data together with SEM images, topographic information must be provided as depth image. Consequently, a unique height scale is required for all applied data with different magnifications. This requires a calibrated height measurement, which is ensured with the integrated 3D calibration of the topographic acquisition and a dedicated calibration sample. Thus, a large number of data sets from different fracture samples was generated and used as training data for machine learning. T2 - 16th Multinational Congress on Microscopy CY - Brno, Czech Republic DA - 04.09.2022 KW - Fractography KW - Machine Learning KW - Topography PY - 2022 AN - OPUS4-55937 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Manzoni, Anna Maria A1 - Yesilcicek, Yasemin A1 - Demir, E. A1 - Haas, S. A1 - Glatzel, U. T1 - Combining trace elements for microstructural optimization in the Al10Co25Cr8Fe15Ni36Ti6 compositionally complex alloy N2 - Trace elements W and Hf have different influence on the microstructure and the mechanical properties when added to the Al10Co25Cr8Fe15Ni36Ti6 compositionally complex alloy. The addition of both can thus merge both element’s beneficial influences when combined with the appropriate heat treatment: Hf enhances the cubicity of the γ’ particles in the γ matrix while the W reduces the negative influence of the Heusler phase: this phase can be completely dissolved when W is present in the alloy. T2 - ICHEM 2020 CY - Berlin, Germany DA - 27.09.2020 KW - High entropy alloys KW - Transmission electron microscopy KW - Lattice misfit KW - X-ray diffraction KW - Scanning electron microscopy PY - 2020 AN - OPUS4-51370 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sonnenburg, Elke A1 - Bettge, Dirk A1 - Sommer, Kontantin A1 - Agudo Jácome, Leonardo T1 - Präparation, Kontrastierung und Darstellung des Gefüges von additiv gefertigtem austenitischem Stahl 316L N2 - Der weit verbreitete austenitische Stahl 316L soll auch mittels additiver Fertigung verarbeitet werden (316L-AM). Zur Entwicklung optimaler Aufbauverfahren ist ein detailliertes Verständnis des Gefüges notwendig. Das additiv aufgebaute Gefüge zeigt eine Mikrostruktur, die geprägt ist von sehr hohen Abkühlraten und gerichtetem Kornwachstum. Mittels klassischer Metallographie können die Charakteristika des Gefüges wie Körner, Subkörner und Schmelzlinien sichtbar gemacht werden. Mittels EBSD werden Kristallorientierungen ermittelt und bildhaft aufbereitet. Die Feinstruktur der Körner wird im REM in der Übersicht aufgelöst. Erst im TEM kann bei hoher Vergrößerung die Natur der Zellstruktur quantitativ ermittelt werden. T2 - Metallographie 2020 CY - Online meeting DA - 16.09.2020 KW - Präparation KW - Kontrastierung KW - Additiv gefertigter Stahl PY - 2020 AN - OPUS4-51245 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nolze, Gert A1 - Tokarski, T. T1 - Lattice parameter determination with EBSD. Is that possible? N2 - CALM is software for determining the Bravais lattice type and the resulting lattice parameters from a single Kikuchi pattern. It requires the definition of 4 bands and a single bandwidth from which all other band positions as well as bandwidths are derived. For band detection, it uses the Funk transform, which allows detection of twice as many bands as usual. CALM works for any symmetry and requires low-noise patterns of at least 320x240 pixels. The resulting errors are <2% even for such small patterns, assuming good quality. The relative errors are <0.5%. However, this requires a projection centre position best derived from a sample of a cubic phase in CALM. However, this must have been recorded under identical conditions. Hundreds of Kikuchi patterns of phases with different symmetries were examined. T2 - Institutskolloquium Kassel CY - Online meeting DA - 30.10.2020 KW - Phasenidentifikation KW - EBSD KW - Gitterkonstanten PY - 2020 AN - OPUS4-51813 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koclega, Damian A1 - Radziszewska, Agnieszka A1 - Kranzmann, Axel A1 - Dymek, Stanislaw T1 - The microstructure characterization of the oxide scale created on Inconel 686 clad N2 - The Ni-Cr-Mo-W alloy is characterized by the excellent high-temperature corrosion resistance, good strength and ability to work in aggressive environments. To protect the surface of the substrate 13CrMo4-5 steel against aggressive environments the Inconel 686 as clad layer was used. The corrosion process was performed in oxidizing mixture of gases like O2, COx, SOx. The second part of corrosion Experiment concerned the corrosion test of the coating in reducing atmosphere of the specified gases with ashes, which contained e.g. Na, Cl, Ca, Si, C, Fe, Al. T2 - EUROCORR 2018 CY - Crocow, Poland DA - 09.09.2018 KW - Laser cladding KW - Inconel 686 coating KW - High-temperature corrosion KW - Aggressive gases PY - 2018 AN - OPUS4-47393 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -