TY - CONF A1 - Gesell, Stephan A1 - Fedelich, Bernard A1 - Ganesh, Rahul A1 - Kuna, Meinhard A1 - Skrotzki, Birgit A1 - Kiefer, Björn T1 - A CTOD-based crack growth law for thermomechanical fatigue N2 - Due to combined cyclic mechanical and thermal loading during operation, the material of exhaust gas conducting components of combustion engines is exposed to thermomechanical fatigue (TMF). This leads to formation and growth of cracks, especially at the most highly stressed points of these components. In order to better predict the service life of cracked components before failure, it is necessary to identify a crack propagation law for the material used. Isothermal crack propagation tests have been carried out at several temperatures with a typical cast iron to identify such a law. The crack length is measured by the potential drop method. The compliance method, fractography and thermographic camera measurements have been used to validate and calibrate the potential drop measurements. Each of the isothermal tests has been simulated using a specially developed FEM-algorithm based on remeshing and remapping. This algorithm has been implemented in python and ABAQUS. Thereby, the crack tip region is modeled by collapsed Quad8 elements. From the individual simulations, the cyclic crack tip opening displacement (ΔCTOD) is extracted and regarded as a potential fracture mechanics parameter which controls the crack growth rate. By combining the data from the experiments and the simulations, the crack propagation law has been identified. Finally, anisothermal crack propagation tests have been performed for validation of the crack growth law. T2 - European Conference on Fracture 2022 CY - Funchal, Portugal DA - 27.06.2022 KW - Fatigue crack growth KW - Finite elmenet simulation KW - TMF experiments PY - 2022 AN - OPUS4-56934 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kuchenbecker, Petra T1 - Herausforderungen bei der Granulometrie von (technischen) Nano-Pulvern N2 - Einführungsvortrag im Rahmen der Veranstaltung der BAM-Akademie zur Anwendung der OECD TG 124 "Volume Specific Surface Area of Manufactured Nanomaterials" zu Herausforderungen bei der Granulometrie von Nanopulvern. Es werden die Einflüsse von Partikelform, Breite der Partikelgrößenverteilung und Agglomeration/ Aggregation auf das Messergebnis sowie die Vergleichbarkeit der Ergebnisse verschiedener Messverfahren dargelegt. T2 - BAM Akademie II: Info-Tage "Nano or not Nano" CY - Online meeting DA - 25.01.2024 KW - Nanopulver KW - Granulometrie KW - Partikelgröße KW - VSSA KW - OECD TG 124 PY - 2024 AN - OPUS4-59558 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maaß, Robert T1 - Tracing structural dynamics in metallic glasses during cryogenic cycling N2 - Highly unrelaxed structural states of metallic glasses have often advantageous mechanical properties. Since metallic glasses continuously relax with time (age) or inherently are well relaxed after processing, methods to uniformly rejuvenate the material are needed. One approach that has received attention is the so-called cryogenic-cycling method, during which a metallic glass is repeatedly immersed into liquid nitrogen. In some cases, cryogenic cycling is truly efficient in increasing the stored excess enthalpy of metallic glasses, but it does not seem to be universally applicable to all alloys and structural states. The origins for these differences remain unclear due to our limited understanding of the underlying structural evolution. In order to shed more light onto the fundamental structural processes of cryogenic cycling, we pursue in-situ x-ray photon correlation spectroscopy (XPCS) to trace the atomic-scale structural dynamics of a Zr-based metallic glass in two different structural states (ribbon and bulk metallic glass). This method allows calculating the relaxation times as a function of time throughout the thermal cycling. It is found that the investigated glasses exhibit heterogeneous structural dynamics at 300 K, which changes to monotonic aging at 78 K. Cryogenic cycling homogenizes the relaxation time distribution for both structural states. This effect is much more pronounced in the ribbon, which is the only structural state that rejuvenates upon cycling. We furthermore reveal how fast atomic-scale dynamics is correlated with long-time average structural relaxation times irrespective of the state, and that the ribbon exhibits unexpected additional fast atomic-scale relaxation in comparison to the plate material. Overall, a picture emerges that points towards heterogeneities in fictive temperature as a requirement for cryogenic energy storage. T2 - MRS Fall 2020 - Invited Talk CY - Boston, MA, USA DA - 27.11.2020 KW - Relaxation metallic glasses PY - 2020 AN - OPUS4-59542 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kuchenbecker, Petra T1 - Einführung: Volume Specific Surface Area (VSSA) N2 - Im Rahmen der 2. BAM-Akademie-Veranstaltung "Nano or not Nano" wurde die OECD TG 124 "Volume Specific Surface Area of Manufactured Nanomaterials" vorgestellt. Der Vortrag enthält ein Einführung zur VSSA mit Definitionen, Vorteilen und Einschränkungen. T2 - BAM Akademie II: Info-Tage "Nano or not Nano" CY - Online meeting DA - 25.01.2024 KW - Nano powder KW - VSSA KW - Specific surface KW - OECD TG PY - 2024 AN - OPUS4-59560 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kuchenbecker, Petra T1 - Bestimmung der Skelettdichte mittels Gaspyknometrie N2 - Im Rahmen des 2. BAM-Akademie Info-Tages "Nano or not Nano" wurde die OECD TG 124 "Volume Specific Surface Area of Manufactured Nanomaterials" vorgestellt. Der Vortrag beschreibt detailliert das Messverfahren der He-Gaspyknometrie zur Bestimmung der Skelettdichte von Pulvern und geht auf Anwendbarkeit, Besonderheiten bei Nanopulvern und wichtige Einstellparameter für die Messung ein. T2 - BAM Akademie II: Info-Tage "Nano or not Nano" CY - Online meeting DA - 25.01.2024 KW - Pycnometry KW - Density KW - Nano powder PY - 2024 AN - OPUS4-59561 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalinka, Gerhard T1 - Testing the fibre matrix interface of short glass fibre reinforced PMCs with using the push out technique N2 - With this presentation, the push-out technique is explained. The focus of the experimental work is on the characterization of the fiber-matrix interface of short fiber reinforced composites. The reinforcing component was glass fibers and the matrix polymer was PA6.6 and PPA. It is demonstrated for the first time that the push-out technique ca be applied on injection molded short fiber PMC and is sensitive to the mechanical interface properties. Further studies are planned on the influence of multiple processing, the temperature and humidity. T2 - Composirtes United Workshop „Fiber Matrix Interphases“ CY - Online meeting DA - 09.11.2023 KW - Polymer Matrix Composite KW - Glass Fibres KW - PA6.6 KW - PPA KW - Push-out Test KW - Interface Strength PY - 2023 AN - OPUS4-59053 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Birkholz, H. A1 - Bayerlein, Bernd A1 - Schilling, Markus A1 - Grundmann, J. A1 - Hanke, T. A1 - Waitelonis, J. A1 - Sack, H. A1 - Mädler, L. T1 - PMD Core Ontology: A Community Driven Mid-Level Ontology in the MSE Domain N2 - Knowledge representation in the materials science and engineering (MSE) domain is a vast and multi-faceted challenge: Overlap, ambiguity, and inconsistency in terminology are common. Invariant and variant knowledge are difficult to align cross-domain. Generic top-level semantic terminology often is too abstract, while MSE domain terminology often is too specific. In this presentation, an approach how to maintain a comprehensive and intuitive MSE-centric terminology composing a mid-level ontology–the PMD core ontology (PMDco)–via MSE community-based curation procedures is shown. The PMDco is designed in direct support of the FAIR principles to address immediate needs of the global experts community and their requirements. The illustrated findings show how the PMDco bridges semantic gaps between high-level, MSE-specific, and other science domain semantics, how the PMDco lowers development and integration thresholds, and how to fuel it from real-world data sources ranging from manually conducted experiments and simulations as well as continuously automated industrial applications. T2 - FEMS EUROMAT 2023 CY - Frankfurt a. M., Germany DA - 03.09.2023 KW - Knowledge Representation KW - Semantic Interioerability KW - Mid-Level Ontology for MSE KW - FAIR Data Management PY - 2023 AN - OPUS4-58201 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beygi Nasrabadi, Hossein A1 - Hanke, T. A1 - Eisenbart, M. A1 - Skrotzki, Birgit T1 - Materials Mechanical Testing Ontology (MTO) N2 - The materials mechanical testing ontology (MTO) was developed by collecting the mechanical testing vocabulary from ISO 23718 standard, as well as the standardized testing processes described for various mechanical testing of materials like tensile testing, Brinell hardness test, Vickers hardness test, stress relaxation test, and fatigue testing. Confirming the ISO/IEC 21838-2 standard, MTO utilizes the Basic Formal Ontology (BFO), Common Core Ontology (CCO), Industrial Ontologies Foundry (IOF), Quantities, Units, Dimensions, and data Types ontologies (QUDT), and Material Science and Engineering Ontology (MSEO) as the upper-level ontologies. Reusing these upper-level ontologies and materials testing standards not only makes MTO highly interoperable with other ontologies but also ensures its acceptance and applicability in the industry. MTO represents the mechanical testing entities in the 230 classes and four main parts: i) Mechanical testing experiments entities like tensile, hardness, creep, and fatigue tests as the subclasses of mseo:Experiment, ii) Mechanical testing quantity concepts such as toughness, elongation, and fatigue strength in the appropriate hierarchies of bfo:Disposition and bfo:Quality classes, iii) Mechanical testing artifacts like indenter as the subclasses of cco:Artifact, and iv) mechanical testing data like the stress-strain, S-N, or creep curves as the subclasses of cco:InformationContentEntity. MTO is publicly available via the KupferDigital GitLab repository. T2 - FEMS EUROMAT 2023 CY - Frankfurt a. M., Germany DA - 03.09.2023 KW - Mechanical testing KW - Ontology KW - Standard PY - 2023 AN - OPUS4-58270 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bayerlein, Bernd A1 - Schilling, Markus A1 - Z.-Jan, G.-A. A1 - Hanke, T. A1 - v. Hartrott, P. A1 - Fliegener, S. A1 - Kryeziu, J. A1 - Waitelonis, J. A1 - Sack, H. A1 - Skrotzki, Birgit T1 - Adopting FAIR data practices in materials science: Semantic representation of a quantitative precipitation analysis N2 - Many metallic materials gain better mechanical properties through controlled heat treatments. For example, in age-hardenable aluminium alloys, the strengthening mechanism is based on the controlled formation of nanometre-sized precipitates, which represent obstacles to dislocation movement and consequently increase the strength. Precise tuning of the material microstructure is thus crucial for optimal mechanical behaviour under service condition of a component. Therefore, analysis of the microstructure, especially the precipitates, is essential to determine the optimum parameters for the interplay of material and heat treatment. Transmission electron microscopy (TEM) is utilized to identify precipitate types and orientations in the first step. Dark-field imaging (DF-TEM) is often used to image the precipitates and thereafter quantify their relevant dimensions. Often, these evaluations are still performed by manual image analysis, which is very time-consuming and to some extent also poses reproducibility problems. Our work aims at a semantic representation of an automatable digital approach for this material specific characterization method under adaption of FAIR data practices. Based on DF-TEM images of different precipitation states of a wrought aluminium alloy, the modularizable, digital workflow of quantitative analysis of precipitate dimensions is described. The integration of this workflow into a data pipeline concept will also be discussed. Using ontologies, the raw image data, their respective contextual information, and the resulting output data of the quantitative image analysis can be linked in a triplestore. Publishing the digital workflow and the ontologies will ensure data reproducibility. In addition, the semantic structure enables data sharing and reuse for other applications and purposes, demonstrating interoperability. T2 - FEMS EUROMAT 2023 CY - Frankfurt a. M., Germany DA - 03.09.2023 KW - Semantic Representation KW - FAIR data management KW - Quantitative Precipitation Analysis KW - Knowledge graph and ontologies PY - 2023 AN - OPUS4-58199 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz, Wencke A1 - Manzoni, Anna Maria A1 - Stephan-Scherb, Christiane T1 - Corrosion induced alloy sulfidation in a high-entropy alloy (HEA) N2 - To apply high-entropy alloys (HEA) of the CrMnFeCoNi family in challenging atmospheres, their degradation behavior under harsh environments needs to be investigated. Oxidation studies to HEAs have not been extensively investigated and most of them are concentrated on environments like synthetic air, laboratory air, CO/CO2, O2 and H2O atmospheres. Main corrosion products which were identified after aging times of up to 100 h are Mn2O3 (≤800°C) and Mn3O4 (≥800°C). Another corrosive medium in high temperature applications is SO2, which preferentially forms sulfides on commercial steels for example. These can be occurred both in the oxide layer and at the oxide/metal interface. For instance, on Fe-Cr based alloys sulfides (Cr5S6) were detected along grain boundaries and their number increases with exposure time and Cr-content in the alloy. These sulfides show an increased hardness, compared to the bulk alloy, and cause an embrittlement of the grain boundaries. This is a serious material degradation phenomenon, now addressed for the case of HEAs. In the present study metal sulfides were identified after corrosion of the HEA CrMnFeCoNi alloy in an Ar-0.5vol.%SO2 atmosphere at 800°C for 24 h, 48 h, 96 h and 192 h exposure time. After all three duration times, a thin non-protective Cr2O3 layer has formed at the oxide/alloy interface. At the gas side a thick Mn3O4 layer with local voids containing sulfur could be detected by SEM-EDS analysis. Furthermore, S precipitates could be detected in the bulk material near the surface. These sulfides were characterized in detail by scanning and transmission electron microscopy. Based on these results, a model for grain boundary sulfidation of high-entropy alloy CrMnFeCoNi is discussed. T2 - EUROMAT 2021 EUROPEAN CONGRESS AND EXHIBITION ON ADVANCED MATERIALS AND PROCESSES CY - Online meeting DA - 13.09.2021 KW - High-entropy alloys KW - High-temperature corrosion KW - Sulfidation KW - Chromium oxide KW - Manganese oxide PY - 2021 AN - OPUS4-53455 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Botsch, B A1 - Sonntag, U A1 - Bettge, Dirk A1 - Le, Quynh Hoa A1 - Schmies, Lennart A1 - Yarysh, Anna T1 - Classification of fracture surface types based on SEM images N2 - The following work deals with the quantitative fracture surface evaluation in damage analysis. So far, fracture surfaces have almost exclusively been evaluated qualitatively, i.e. the presence of fracture features is documented and their surface proportions are estimated, if necessary. Many years of experience are required, as well as an intensive comparison with defined comparative images from the literature. The aim of this work is the development of classifiers which can recognize fracture mechanisms or fracture features in scanning electron microscope images (SEM). The basis is 46 SEM images, which have been evaluated by fractography experts with regard to fracture features. The existing data set of images is expanded using augmentation methods in order to increase the variability of the data and counteract overfitting. Only convolutional neural networks (CNN) are used to create the classifiers. Various network configurations are tested, with the SegNet achieving the best results. T2 - Materialsweek 2021 CY - Online meeting DA - 07.09.2021 KW - Fractography KW - Fracture surface KW - Deep learning KW - SEM PY - 2021 AN - OPUS4-53418 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nolze, Gert A1 - Tokarski, T. T1 - Lattice parameter determination with EBSD. Is that possible? N2 - CALM is software for determining the Bravais lattice type and the resulting lattice parameters from a single Kikuchi pattern. It requires the definition of 4 bands and a single bandwidth from which all other band positions as well as bandwidths are derived. For band detection, it uses the Funk transform, which allows detection of twice as many bands as usual. CALM works for any symmetry and requires low-noise patterns of at least 320x240 pixels. The resulting errors are <2% even for such small patterns, assuming good quality. The relative errors are <0.5%. However, this requires a projection centre position best derived from a sample of a cubic phase in CALM. However, this must have been recorded under identical conditions. Hundreds of Kikuchi patterns of phases with different symmetries were examined. T2 - Institutskolloquium Kassel CY - Online meeting DA - 30.10.2020 KW - Phasenidentifikation KW - EBSD KW - Gitterkonstanten PY - 2020 AN - OPUS4-51813 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weinel, Kristina T1 - Electron-beam-induced production of gold nanoparticles N2 - Several studies have shown that the electron beam (e-beam) can be used to create nanomaterials from microparticles in situ in a TEM. However, attempts to produce gold nanoparticles (NPs) on silicon oxide substrate remained to be accomplished. Here, we show that the production of gold NPs is possible by using the e-beam in a SEM, under a set of parameters. The NPs produced present a size gradient along the radial direction. A parameter study shows that the microparticles may: 1) flicker away without producing NPs, 2) fragment to form NPs and/or 3) react with the silicon oxide substrate, depending on the applied current. A hypothesis regarding the driving physical phenomena that lead the microparticles to fragment into NPs is discussed. Fabrication of gold NPs in the SEM provides a more cost-effective option as compared to the established method in the TEM. T2 - PhD Seminar CY - Berlin, Germany DA - 26.11.2023 KW - Electron-beam-induced modification KW - Gold nanoparticles KW - Fabrication method KW - Scanning electron microscope KW - Nano-assemblies PY - 2023 AN - OPUS4-59080 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bettge, Dirk A1 - Le, Quynh-Hoa A1 - Roth, J. T1 - Entwicklung einer fraktographischen Symbolik N2 - Bei der Untersuchung von Bruchflächen werden zunächst Beobachtungen gemacht, d.h. makroskopische und mikroskopische Merkmale analysiert und in Bildern dokumentiert. Im zweiten Schritt werden anhand der gefundenen Merkmale Rissverlauf und Bruchmechanismen ermittelt. Abschließend sollen diese Ergebnisse in einem Bericht oder Gutachten zusammengefasst werden. Hierbei ist eine skizzenhafte Darstellung der fraktographischen Befunde hilfreich für das Verständnis des Lesers. Ein vorgefertigter fraktographischer Symbolsatz würde dies erheblich vereinfachen. Skizzen von fraktographischen Befunden sind in der Literatur recht häufig zu finden, z.B. in der VDI 3822 oder dem ASM Handbook Fractography, allerdings gibt es hierzu keine umfassende Systematik, wie sie z.B. aus der Meteorologie (Wetterkarten), Geographie (Landkarten, Seekarten) oder Geologie (Bodenkarten) seit langer Zeit bekannt sind. Deshalb wird hier der Versuch unternommen, einen Symbolsatz zu entwickeln und zur Verfügung zu stellen, mit dessen Hilfe fraktographische Befunde in eindeutiger und übersichtlicher Weise veranschaulicht werden können. Der fraktographische Symbolsatz ("Fracto Graphics") befindet sich in Entwicklung, ist offen zur Diskussion sowie für Verbesserungen. T2 - 55. Metallographie-Tagung CY - Online meeting DA - 29.9.2021 KW - Fraktographie KW - Symbolik KW - Schadensanalyse PY - 2021 AN - OPUS4-53433 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weinel, Kristina T1 - Electron-beam induced particle synthesis: Phenomenological study of the physical mechanisms N2 - Several studies have shown that the electron beam (e-beam) can be used to create nanomaterials from microparticles in situ in a TEM. However, attempts to produce gold nanoparticles (NPs) on silicon oxide substrate remained to be accomplished. Here, we show that the production of gold NPs is possible by using the e-beam in a SEM, under a set of parameters. To understand the physical mechanisms leading to the gold NPs, the mechanisms of e-beam induced charging as well as e-beam induced heating of the MPs were discussed. Several hints point to heating as the driving mechanism. T2 - IFW Dresden, Seminar CY - Dresden, Germany DA - 06.12.2023 KW - Electron-beam-induced modification KW - Nanoparticle synthesis KW - Scanning electron microscopy KW - Driving physical mechanism KW - Negative charged microparticle KW - Temperature driven process PY - 2023 AN - OPUS4-59081 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Manzoni, Anna Maria T1 - A decade of cube optimization in the Al- Co-Cr-Fe-Ni-Ti high entropy family N2 - The multi-phase approach has proven to widen the application properties of high entropy alloys. After a decade of testing different alloys in the Al-Co-Cr-Cu-Fe-Ni-Ti family the Al10Co25Cr8Fe15Ni36Ti6 was found to be a solid base for more fine-tuned microstructural optimization. Following the example of superalloys, the Al10Co25Cr8Fe15Ni36Ti6 alloy aims for a γ/γ' microstructures in order to guarantee a good microstructural stability at high temperatures. The shape and volume fraction of the γ' particles is known to influence the mechanical properties of superalloys, and they do so in the high entropy family as well [1]. Shape, misfit and creep properties of several modified versions of the Al10Co25Cr8Fe15Ni36Ti6 alloy are compared and discussed in this talk. T2 - Department seminar National Chung Hsing University CY - Taichung, Taiwan DA - 15.11.2023 KW - High entropy alloys KW - Transmission electron microscopy KW - X-ray diffraction KW - Creep KW - Phase analysis PY - 2023 AN - OPUS4-58979 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lemiasheuski, Anton A1 - Bajer, Evgenia A1 - Oder, Gabriele A1 - Göbel, Artur A1 - Hesse, Rene A1 - Bettge, Dirk T1 - Development of an Automated 3D Metallography System (RASI) and its Application in Microstructure Analysis N2 - Many microstructural features exhibit non-trivial geometries, which can only be derived to a limited extent from two-dimensional images. E.g., graphite arrangements in lamellar gray cast iron have complex geometries, and the same is true for additively manufactured materials and three-dimensional conductive path structures. Some can be visualized using tomographic methods, but some cannot be due to weak contrast and/or lack of resolution when analyzing macroscopic objects. Classic metallography can help but must be expanded to the third dimension. The method of reconstructing three-dimensional structures from serial metallographic sections surely is not new. However, the effort required to manually assemble many individual sections into image stacks is very high and stands in the way of frequent application. For this reason, an automated, robot-supported 3D metallography system is being developed at BAM, which carries out the steps of repeated preparation and image acquisition on polished specimen. Preparation includes grinding, polishing and optionally etching of the polished surface. Image acquisition comprises autofocused light microscopic imaging at several magnification levels. The image stacks obtained are then pre-processed, segmented, and converted into 3D models, which in the result appear like microtomographic models, but with high resolution at large volume. Contrasting by classical chemical etching reveals structures that cannot be resolved using tomographic methods. The integration of further imaging and measuring methods into this system is underway. Some examples will be discussed in the presentation. T2 - Euromat 2023 CY - Frankfurt a. M., Germany DA - 04.07.2023 KW - Metallography KW - 3D Reconstruction KW - Roboter KW - Automation KW - Microstructure PY - 2023 AN - OPUS4-58202 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bayerlein, Bernd T1 - Probenpräparation für AFM-basierte Untersuchungsverfahren N2 - Adapted and advanced sample preparation of semiconductor layer systems with the focused ion beam for AFM-based test methods N2 - Der vorliegende Vortrag gibt einen Überblick über Probenpräparationen mit der Focused Ion Beam (FIB) für AFM-basierte Untersuchungsverfahren. Anhand zweier Beispiele wird gezeigt, wie ionenstrahlpolierte Lamellen aus Halbleiter-Schichtsystemen elektrisch leitfähig auf Substrate platziert werden, so dass in-situ und in-operando Messungen mit Scanning Microwave Microscope (SMM) bzw. Spectroscopic infrared scanning near-field optical microscope (IR-SNOM) durchgeführt werden können. T2 - 15. Berlin-Brandenburger Präparatorentreffen CY - Potsdam/Golm, Germany DA - 11.04.2019 KW - Focused Ion Beam KW - AFM based test methods KW - Sample preparation KW - Semiconductor materials KW - Layer system PY - 2019 AN - OPUS4-47784 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Manzoni, Anna Maria A1 - Mohring, W. A1 - Laplanche, G. A1 - Schneider, M. A1 - Hagen, S. A1 - Stephan-Scherb, C. T1 - High temperature oxidation of CrFeNi in synthetic air N2 - The surface corrosion behaviour is a key issue which determines whether the material is applicable at a given atmosphere. Medium-entropy alloy FeCrNi alloy was exposed to synthetic air at 1000°C, 1050°C, and 1100 °C for up to 1000 h using a thermobalance. The oxidation rate was parabolic at 1000 and 1050°C, but breakaway occurred at 1100°C after 5 h of aging time. The whole oxide scales formed under the isothermal oxidation tests spalled off and additional oxidation tests were carried out at 1000 °C and 1050°C for 24 h and up to 100 h at 1000°C in a tubular furnace. The corrosion behaviour of the MEA was analysed by scanning electron microscope, energy-dispersive X-ray spectroscopy, and X-ray diffraction and compared to the behaviour of 316 L. The experimental results showed that under all conditions chromium is the main diffusion element resulting in the formation of a Cr2O3 layer at the MEA surface. Spallation of the layer induces the formation of additional oxidation products under the surface of the (spalled off) chromia layer. T2 - Euromat 2023 CY - Frankfurt a. M., Germany DA - 03.09.2023 KW - Medium entopy alloy KW - Oxidation KW - Scanning electron microscopy KW - Thermogravimetric analysis PY - 2023 AN - OPUS4-58198 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz, Wencke A1 - Stephan-Scherb, Christiane A1 - Laplanche, Guillaume T1 - High temperature corrosion phenomena of HEAs and MEAs N2 - High- and medium-entropy alloys (HEAs and MEAs) constitute a new class of materials. Those with a face-centered cubic (fcc) structure from the Cr-Mn-Fe-Co-Ni system have excellent mechanical properties and are considered for high-temperature applications since diffusion in these alloys was reported to be sluggish. However, their corrosion resistance at high temperatures must still be evaluated to further qualify them for such kinds of applications. Various groups studied the oxidation behavior of HEAs and MEAs under (dry) laboratory and artificial air as well as CO2/CO mixtures in different temperature ranges. CrCoNi exhibits the best corrosion resistance at 800 °C due to the formation of a protective Cr2O3 layer. The matrix below the oxide scale was reported to be correspondingly depleted in Cr. It was further shown that the addition of Mn and Fe to CrCoNi changes the phase composition of the oxide scale at 800 °C. A Mn2O3 layer was grown during oxidation on CrMnCoNi and CrMnFeCoNi and a Cr2O3 scale was formed at the matrix/oxide scale interface. Beneath these oxide layers, Mn- and Cr-depleted zones were detected. These phase morphologies demonstrate the inward diffusion of oxygen and outward diffusion of Cr and Mn resulting in the formation of Cr2O3 and Mn2O3. In the present study, the corrosion resistance of CrMnFeCoNi and CrCoNi were confirmed and additionally characterized under further oxidizing atmospheres at 800 °C including Ar-2 Vol.% O2, Ar-2 Vol.% H20, and Ar-2 Vol.% SO2 mixtures. T2 - Symposium on Advanced Mechanical and Microstructural Characterization of High-Entropy Alloys CY - Ruhr-Universität Bochum, Germany DA - 03.02.2020 KW - Mn3O4 KW - High-entropy alloy KW - Medium-entropy alloy KW - High-temperature corrosion KW - Chromia PY - 2020 AN - OPUS4-50984 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -