TY - GEN A1 - Ávila Calderón, Luis A1 - Schriever, Sina T1 - BAM Reference Data: Creep of Single-Crystal Ni-Based Superalloy CMSX-6 N2 - This publication provides comprehensive metadata and test results of constant force creep tests according to DIN EN ISO 204:2019-4 on the single crystal Ni-based superalloy CMSX-6 at T = 980 °C and initial stresses between 140 MPa and 230 MPa. The tests were carried out in an accredited test laboratory using calibrated measuring equipment. The data were audited and are BAM reference data. KW - NFDI-MatWerk KW - Digitalisierung KW - CMSX-6 KW - Creep KW - Reference Data KW - Referenzdaten KW - Ni-Based Superalloy PY - 2024 DO - https://doi.org/10.5281/zenodo.13937986 PB - Zenodo CY - Geneva AN - OPUS4-61649 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Epishin, A. I. A1 - Fedelich, Bernard A1 - Viguier, B. A1 - Schriever, Sina A1 - Svetlov, I. L. A1 - Petrushin, N. V. A1 - Saillard, R. A1 - Proietti, A. A1 - Poquillon, D. A1 - Chyrkin, A. T1 - Creep of single-crystals of nickel-base γ-alloy at temperatures between 1150 °C and 1288 °C N2 - A γ-analogue of the superalloy CMSX-4 that does not contain the strengthening γ′ -phase and only consists of the γ-solid solution of nickel has been designed, solidified as single-crystals of different orientations, and tested under creep conditions in the temperature range between 1150 and 1288 °C. The tests have revealed a very high creep anisotropy of this alloy, as was previously found for CMSX-4 at supersolvus temperature of 1288 °C. This creep anisotropy could be explained by the dominance of 〈011〉{111} octahedral slip. Furthermore, the analysis of the creep data has yielded a high value of the creep activation energy, Qc≈442 kJ/mol, which correlates with the high activation energy of Re diffusion in Ni. This supports the hypothesis that dislocation motion in the γ-matrix of Re-containing superalloys is controlled by the diffusion of the Re atoms segregating at the dislocation core. The Norton stress exponent n is close to 5, which is a typical value for pure metals and their alloys. The absence of γ′ -reprecipitation after high-temperature creep tests facilitates microstructural investigations. It has been shown by EBSD that creep deformation results in an increasing misorientation of the existing low angle boundaries. In addition, according to TEM, new low angle boundaries appear due to reactions of the a/2 〈011〉 mobile dislocations and knitting of new networks. KW - Nickel alloys KW - Single-crystals KW - Creep KW - Electron microscopy KW - Deformation mechanisms PY - 2021 DO - https://doi.org/10.1016/j.msea.2021.141880 SN - 0921-5093 VL - 825 SP - 1 EP - 13 PB - Elsevier CY - Amsterdam AN - OPUS4-53132 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kianinejad, Kaveh A1 - Czediwoda, Fabian A1 - Glatzel, U. A1 - Völkl, R. A1 - Stöhr, B. A1 - Ávila Calderón, Luis A1 - Schriever, Sina A1 - Saliwan Neumann, Romeo A1 - Fedelich, Bernard A1 - Darvishi Kamachali, Reza T1 - Microstructure-based modelling of the anisotropic creep behaviour in additively manufactured INCONEL 718 N2 - The existing gap in the adequate prediction of the microstructure-property relationships remains a significant barrier to the safe application of the additively manufactured materials. This challenge is fundamentally tied to the intricate microstructural defects that emerge during the processing. Systematic microstructure-based modelling can offer solutions to address this bottleneck. In this work, we utilize a crystal plasticity model, developed for gamma''-strengthened Ni-base alloys and calibrated with single crystal tensile and creep tests of Inconel 718. By systematically refining the representative volume element complexity---from equiaxed to elongated grain morphologies, and from unimodal to bimodal orientation and grain size distributions---we demonstrate how each layer of structural realism contributes to the model’s predictive capacity. Creep tests of laser-based powder bed fusion (PBF-LB/M) manufactured samples in three orientations (with the tensile axis parallel, perpendicular, and 45° tilted relative to the building direction) were performed at 650° C, accompanied by electron backscatter secondary diffraction measurements. The results of our simulations reveal that the bimodal grain morphology and crystallographical texture significantly influence the observed creep anisotropy. We show that the elongated grain structure combined with grain boundary sliding plays a major role in the creep response, specifically in tilted specimens. KW - Additive manufactured Ni-base superalloys KW - Creep Anisotropy KW - Crystal plasticity PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-646884 DO - https://doi.org/10.1016/j.msea.2025.149029 VL - 945 SP - 1 EP - 15 PB - Elsevier B.V. AN - OPUS4-64688 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Avila Calderon, Luis Alexander A1 - Schriever, Sina A1 - Hang, Y. A1 - Olbricht, Jürgen A1 - Portella, P. D. A1 - Skrotzki, Birgit T1 - Creep reference data of single-crystal Ni-based superalloy CMSX-6 N2 - The article presents creep data for the single-crystal, [001]-oriented nickel-based superalloy CMSX-6, tested at a temperature of 980 °C under initial stresses ranging from 140 MPa to 230 MPa. The constant-load creep experiments were performed in accordance with DIN EN ISO 204:2019–4 standard within an ISO 17025 accredited laboratory. A total of 12 datasets are included, each of which includes the percentage creep extension as a function of time. The data series and associated metadata were systematically documented using a data schema specifically developed for creep data of single-crystal Ni-based superalloys. This dataset serves multiple purposes: it can be used to compare with one's own creep test results on similar materials, to verify testing setups (e.g., by replicating tests on the same or comparable materials), to calibrate and validate creep models, and to support alloy development efforts. KW - NFDI MatWerk KW - Referenzdaten KW - Kriechen KW - CMSX-6 KW - Digitalisierung PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-654056 DO - https://doi.org/10.1016/j.dib.2025.112436 VL - 65 SP - 1 EP - 11 PB - Elsevier AN - OPUS4-65405 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ávila Calderón, Luis A1 - Shakeel, Y. A1 - Schriever, Sina A1 - Gedsun, A. A1 - Forti, M. A1 - Jordan, Hans A1 - Han, Ying A1 - Baer, O. A1 - Aversa, R. A1 - Olbricht, Jürgen A1 - Hammerschmidt, T. A1 - Hickel, T. A1 - Skrotzki, Birgit T1 - NFDI-MatWerk/IUC02 Data schema for creep data of Ni-based superalloys including a comprehensive documentation of test results and metadata N2 - This data schema was developed within the infrastructure use case IUC02: “Framework for curation and distribution of reference datasets” of the consortium NFDI-MatWerk. It intends to define a structured approach for collecting all required information on a creep experiment using the established terminology of the respective test standard ISO 204:2022 and additional terminology agreed upon by the domain experts. The individual entries are grouped according to their content type and sub-summarized under respective headlines, thereby suggesting a basic categorization and a related hierarchy of concepts. This hierarchy can be similarly applied to other test methods and different metallic (and other) materials. In version 1.1 some editorial and formal changes were made. KW - NFDI-MatWerk KW - Digitalisierung KW - Referenzdaten KW - Kriechen KW - Ni-based Superalloys PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-611629 DO - https://doi.org/10.5281/zenodo.11668375 PB - Zenodo CY - Geneva AN - OPUS4-61162 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Skrotzki, Birgit A1 - Schriever, Sina T1 - BAM reference data - Results of ASTM E139-11 creep tests on a reference material of Nimonic 75 nickel-base alloy N2 - Results of creep tests on a certified reference material at T = 600°C and a tensile creep load of 160 MPa are provided. The evaluated results include the times to reach 2% and 4% creep strain, respectively, and the creep rate after 400 h. The data were audited and are BAM reference data. KW - Reference data KW - Creep KW - Nickel-base alloy KW - Nimonic 75 KW - Reference material BCR-425 PY - 2021 DO - https://doi.org/10.5281/zenodo.5106606 PB - Zenodo CY - Geneva AN - OPUS4-52970 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Singh, Shobhit Pratap A1 - Löwe, Peter A1 - Schriever, Sina A1 - Olbricht, Jürgen A1 - Rehmer, Birgit A1 - Nolze, Gert A1 - Skrotzki, Birgit T1 - High-throughput creep evaluation of IN738LC in bending using digital image correlation at 850 °C N2 - High-temperature alloys, when used in structural applications, undergo slow time-dependent deformation known as creep. Assessing creep behavior is critical for estimating the in-service life of these alloys. Conventionally, uniaxial creep tests are widely conducted at elevated temperatures to determine creep rates. In recent years, bending creep of cantilevers, when combined with digital image correlation (DIC), has emerged as a promising high-throughput technique for rapidly estimating creep life. However, the applicability of bending creep above 700 ◦C for high-temperature alloys using DIC has not been fully established. In this work, we compare uniaxial creep rates of the nickel-based superalloy IN738LC with bending creep rates measured at 850 ◦C using high-temperature DIC. The bending creep data show excellent agreement with uniaxial creep results in the stress range of 240–360 MPa. The measured creep xponent, a critical rate-determining parameter, is found to be ~8 for both uniaxial and bending creep, with the rate data scattered within a factor of two. An in-house experimental setup was developed to perform bending creep tests at high temperatures, with strain monitored through DIC. Our results demonstrate that bending creep, combined with DIC, provides a reliable and efficient method for creep testing of high-temperature alloys. Compared to conventional uniaxial creep experiments, this approach requires significantly less time and material, thereby reducing effort, energy, and cost. We anticipate that this technique will serve as a foundation for testing precious high-temperature materials. For instance, in ongoing rapid discoveries of advanced alloys, in-service creep life can be evaluated much faster with reduced material requirements. Moreover, this method holds strong potential for application to high-entropy alloys and additively manufactured alloys designed for demanding high-temperature environments. KW - Digital image correlation KW - Bending creep KW - Nickel-based superalloys KW - High throughput testing KW - High-temperature materials PY - 2025 UR - https://www.sciencedirect.com/science/article/pii/S0921509325017034?via%3Dihub DO - https://doi.org/10.1016/j.msea.2025.149479 VL - 950 SP - 1 EP - 12 PB - Elsevier B.V. AN - OPUS4-64814 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ávila Calderón, Luis A1 - Rehmer, Birgit A1 - Schriever, Sina A1 - Ulbricht, Alexander A1 - Agudo Jácome, Leonardo A1 - Sommer, Konstantin A1 - Mohr, Gunther A1 - Skrotzki, Birgit A1 - Evans, Alexander T1 - Creep and creep damage behavior of stainless steel 316L manufactured by laser powder bed fusion N2 - This study presents a thorough characterization of the creep properties of austenitic stainless steel 316L produced by laser powder bed fusion (LPBF 316L) contributing to the sparse available data to date. Experimental results (mechanical tests, microscopy, X-ray computed tomography) concerning the creep deformation and damage mechanisms are presented and discussed. The tested LPBF material exhibits a low defect population, which allows for the isolation and improved understanding of the effect of other typical aspects of an LPBF microstructure on the creep behavior. As a benchmark to assess the material properties of the LPBF 316L, a conventionally manufactured variant of 316L was also tested. To characterize the creep properties, hot tensile tests and constant force creep tests at 600 °C and 650 °C are performed. The creep stress exponents of the LPBF material are smaller than that of the conventional variant. The primary and secondary creep stages and the times to rupture of the LPBF material are shorter than the hot rolled 316L. Overall the creep damage is more extensive in the LPBF material. The creep damage of the LPBF material is overall mainly intergranular. It is presumably caused and accelerated by both the appearance of precipitates at the grain boundaries and the unfavorable orientation of the grain boundaries. Neither the melt pool boundaries nor entrapped gas pores show a significant influence on the creep damage mechanism. KW - 316L KW - Laser Powder Bed Fusion (LPBF) KW - Creep behavior KW - Additive Manufacturing KW - AGIL PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-539373 DO - https://doi.org/10.1016/j.msea.2021.142223 SN - 0921-5093 VL - 830 SP - 142223 PB - Elsevier B.V. AN - OPUS4-53937 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Han, Ying A1 - Schriever, Sina A1 - von Hartrott, Philipp A1 - Rockenhäuser, Christian A1 - Skrotzki, Birgit T1 - Creep dataset for aluminum alloy EN AW-2618A in the T61 and overaged condition 1000 h/190 °C N2 - The article presents creep data for the precipitation-hardened aluminum alloy EN AW-2618A, which was tested in its initial slightly underaged T61 condition and after being aged at 190 °C for 1000 h. The creep test temperatures ranged between 160 °C and 230 °C, and the applied initial stresses between 40 MPa and 290 MPa. The testing times reached up to 4700 h. 19 data sets are provided as creep strain vs. time series. A data schema originally developed to manage creep reference data of a single-crystalline nickel-based superalloy was adapted for the research data set of the polycrystalline aluminum alloy and used to enrich the test data with extensive metadata. The dataset can be used to calibrate and validate creep models. The creep data supplement the hardness and microstructure data that have been previously published. KW - Aluminum alloy EN AW-2618A KW - Aging KW - Overaging KW - High temperature KW - Creep PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-641517 DO - https://doi.org/10.1016/j.dib.2025.112054 SN - 2352-3409 VL - 62 SP - 1 EP - 10 PB - Elsevier CY - Amsterdam [u.a.] AN - OPUS4-64151 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Han, Ying A1 - Schriever, Sina A1 - von Hartrott, Philipp A1 - Rockenhäuser, Christian A1 - Skrotzki, Birgit T1 - Dataset on the Creep Properties of EN AW-2618A Aluminum Alloy in the T61 and an overaged condition N2 - This publication contains comprehensive metadata and test results of constant force creep tests according to DIN EN ISO 204 on the aluminum alloy EN AW-2618A in the T61 condition (8 h/530 °C/quenching in boiling water followed by 28 h/195 °C/air cooling) and in an overaged condition (T61 + 1.000 h/190 °C). The test temperatures cover 160 °C, 180 °C, 190 °C, and 230 °C, and the initial stresses range between 40 MPa and 290 MPa. KW - Creep KW - Aging KW - Overaging KW - Aluminum alloy KW - EN AW-2618A KW - High temperature PY - 2025 DO - https://doi.org/10.5281/zenodo.15744297 PB - Zenodo CY - Geneva AN - OPUS4-63572 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -