TY - JOUR A1 - Mair, Georg A1 - Becker, B. A1 - Gesell, Stephan A1 - Wang, Bin T1 - Monte-Carlo-analysis of minimum load cycle requirements for composite cylinders for hydrogen N2 - Hydrogen is an attractive energy carrier that requires high effort for safe storage. For ensuring safety, storage cylinders must undergo a challenging approval process. Relevant standards and regulations for composite cylinders used for the transport of hydrogen and for its onboard storage are currently based on deterministic (e.g. ISO 11119-3) or to some respect semi-probabilistic criteria (UN GTR No. 13; with respect to burst strength). This paper provides a systematic analysis of the load cycle properties resulting from these regulations and standards. Their characteristics are compared with the probabilistic approach of the Federal Institute for Materials Research and Testing BAM. The most important aspect of comparing different concepts is the rate for accepting designs with potentially unsafe or critical safety properties. This acceptance rate is analysed by operating Monte-Carlo simulations over the available range of production properties. T2 - ICHS 2017 CY - Hamburg, Germany DA - 11.09.2017 KW - Safety assessment KW - Failure rate KW - Ageing KW - Degradation KW - End of life KW - Production scatter PY - 2018 DO - https://doi.org/10.1016/j.ijhydene.2018.09.185 SN - 0360-3199 VL - 44 IS - 17 SP - 8833 EP - 8841 PB - Elsevier Ltd AN - OPUS4-46341 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - You, Zengchao A1 - Hoffmann, V. A1 - Morcillo, Dalia A1 - Agudo Jácome, Leonardo A1 - Leonhardt, Robert A1 - Winckelmann, Alexander A1 - Richter, Silke A1 - Recknagel, Sebastian A1 - Abad Andrade, Carlos Enrique T1 - Investigation of aluminum current collector degradation in lithium-ion batteries using glow discharge optical emission spectrometry N2 - In this work, we employed glow discharge optical emission spectrometry (GD-OES) depth profiling as a fast and semi-quantitative method to investigate the aluminum (Al) current collector degradation in commercial lithium cobalt oxide (LCO) pouch cells with no Al2O3 pretreatment. After battery aging, a heterogeneous deposit was found on the surface of the cathode. Gray hotspot areas within an extensive pale white region were formed. Consistent with energy dispersive X-ray (EDX) analysis of micro-cross sections milled via targeted focused ion beam (FIB), an Al-containing layer of approximately 3 µm can be observed using GD-OES. We attribute one main cause of this layer is the degradation of the Al current collector. The nonuniform growth of this layer was investigated by performing GD-OES depth profiling at different in-plane positions. We found that the gray area has a higher mass concentration of Al, probably in metallic form, whereas the white area was probably covered more homogeneously with Al2O3, resulting from the inhomogeneous distribution of the pitting positions on the current collector. Compared to FIB-EDX, GD-OES enables a faster and more convenient depth profile analysis, which allows the more productive characterization of lithium-ion batteries (LIBs), and consequently benefits the development of preferable battery materials. KW - GD-OES KW - depth profiles KW - Li-ion battery KW - battery aging mechanism KW - current collector corrosion PY - 2023 DO - https://doi.org/10.1016/j.sab.2023.106681 SN - 0584-8547 VL - 205 SP - 106681 PB - Elsevier B.V. CY - Amsterdam, Netherlands AN - OPUS4-57383 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -