TY - CONF A1 - Sänger, Johanna A1 - Riechers, Birte A1 - Pauw, Brian Richard A1 - Günster, Jens T1 - Transparent feedstocks for photon-based additve manufacturing technologies for powder processing of ceramics N2 - Photon-based additive manufacturing technologies such as SLA, DLP, LCM, moreover volumetric two-photon-polymerization, Xolography and holographic technologies promise the highest accuracy and dimensional freedom. But to transfer the light through the feedstock it needs sufficient transparency at the used light wavelength. Ceramic particles used for powder processing routes act as scattering sites and therefore hinder the light transmission, unless… The particle size and particle size distribution are chosen small and narrow enough. Particles which are smaller than roughly 1/10th of the light wavelength, mostly nanoparticles around 5nm size, decrease scattering vastly. This turns resins even with homogeneously distributed ceramic weight fraction of up to 80% transparent again. Feedstocks could be prepared for the highly accurate two-photon-polymerization gaining the smallest yttria stabilized zirconia structures with a resolution of 500nm and unique mechanical properties. The same feedstocks could be applied to DLP and LCM as layer-by-layer AM-technologies for bigger parts. Hybridizing both technologies lead to ceramic parts with microscopic accuracy at macroscopic dimensions. The feedstock was even applied to the volumetric Xolography with the highest transparency requirement so far and to versatile and flexible holographic AM. Highly filled nano-particle containing transparent ceramic feedstocks open the way for technical ceramics in high precision manufacturing where the performance and durability and accessibility are increased and created by the unique ceramic properties such as mechanical strength, chemical and thermal resistance and biocompatibility T2 - 14th International Conference on Ceramic Materials and Components for Energy and Environmental Systems CY - Budapest, Hungary DA - 18.08.2024 KW - Transparent KW - Ceramic KW - Additive manufacturing PY - 2024 AN - OPUS4-60891 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Günster, Jens A1 - Zocca, Andrea T1 - Dense Powder Beds for the Additive Manufacturing of Ceramics N2 - Regarding feedstocks for the additive manufacturing (AM) of ceramics, two features are most critical in classical powder based AM processes: a high particle packing density (typically >50% TD) must be achieved with very fine particles (typically submicron) in order to ensure sufficient sintering activity. Three innovative approaches will be introduced to overcome this problem: 1. Layer wise slurry deposition: The use of water based ceramic slurries as feedstock for the additive manufacture of ceramics has many advantages which are not fully exploit yet. In the layerwise slurry deposition (LSD) process a slurry with no or low organic content is repetitively spread as thin layers on each other by means of a doctor blade. During the deposition, the ceramic particles settle on the previously deposited and dried material to form thin layers with a high packing density (55-60%). The LSD therefore shares aspects both of tape casting and slip casting. The LSD differentiates from the classical powder-based AM layer deposition, which typically achieves with a flowable coarse grained powder a low packing density (35-50%) only, consequently hindering the ability of sintering ceramic parts to full density. The LSD is coupled with the principles of selective laser sintering (SLS) or binder jetting, to generate novel processes which take advantage of the possibility of achieving a highly dense powder-bed. 2. Laser induced slip casting: Contrary to the LSD process, which requires drying of each individual layer, the direct interaction of ceramic slurries with intense laser radiation, for the laser induced slip casting (LIS), is a promising approach for the additive manufacture of voluminous parts. 3. Gas flow assisted powder deposition: By the application of a vacuum pump a gas flow is realized throughout the powder bed. This gas flow stabilizes the powder bed and results into an enhanced flowability and packing density of the powder during layer deposition. The presentation will provide a detailed discussion of potentialities and issues connected to the mentioned technologies and will describe the most recent developments in their application to technical ceramics. T2 - SmatMade 2022 CY - Osaka, Japan DA - 25.10.2022 KW - Additive Manufacturing KW - Advanced ceramics PY - 2022 AN - OPUS4-59886 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Günster, Jens A1 - Sänger, Johanna A1 - Zocca, Andrea T1 - Continuous layer deposition for the Additive Manufacturing of ceramics by Layerwise Slurry Deposition N2 - Powder bed technologies are amongst the most successful Additive Manufacturing (AM) techniques. The application of these techniques to most ceramics has been difficult so far, because of the challenges related to the deposition of homogeneous powder layers when using fine powders. In this context, the "layerwise slurry deposition" (LSD) has been developed as a layer deposition method enabling the use of powder bed AM technologies also for advanced ceramic materials. The layerwise slurry deposition consists of the layer-by-layer deposition of a ceramic slurry by means of a doctor blade, in which the slurry is deposited and dried to achieve a highly packed powder. Not only very fine, submicron powders can be processed with low organics, but also the dense powder bed provides excellent support to the parts built. The latest development of this technology shows that it is possible to print ceramic parts in a continuous process by depositing a layer onto a rotating platform, growing a powder bed following a spiral motion. The unique mechanical stability of the layers in LSD-print allows to grow a powder bed several centimeters thick without any lateral support. The continuous layer deposition allows to achieve a productivity more than 10X higher compared to the linear deposition, approaching a build volume of 1 liter/hour. T2 - DKG Jahrestagung 2024 CY - Höhr-Grenzhausen, Germany DA - 09.09.2024 KW - Ceramic KW - Additive manufacturing PY - 2024 AN - OPUS4-61051 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Günster, Jens A1 - Sänger, Johanna A1 - Pauw, Brian Richard T1 - Two-Photon-Polymerization for Ceramics Powder Processing N2 - Manipulating ceramic powder compacts and ceramic suspensions (slurries) within their volume with light requires a minimum transparency of the materials. Compared to polymers and metals, ceramic materials are unique as they offer a wide electronic band gap and thus a wide optical window of transparency. The optical window typically ranges from below 0.3 µm up to 5µm wavelength. Hence, to penetrate with laser light into the volume of a ceramic powder compound its light scattering properties need to be investigated and tailored. In the present study we introduce the physical background and material development strategies to apply two-photon-polymerization (2PP) for the additive manufacture of filigree structures within the volume of ceramic slurries. T2 - DKG Jahrestagung 2023 CY - Jena, Germany DA - 27.03.2023 KW - Additive Manufacturing KW - Transparent ceramics PY - 2023 AN - OPUS4-59880 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Günster, Jens A1 - Sänger, Johanna A1 - Pauw, Brian Richard T1 - Tailoring powder properties for the light based volumetric additive manufacture of Ceramics N2 - Manipulating ceramic powder compacts and ceramic suspensions (slurries) within their volume with light requires a minimum transparency of the materials. Compared to polymers and metals, ceramic materials are unique as they offer a wide electronic band gap and thus a wide optical window of transparency. The optical window typically ranges from below 0.3 µm up to 5µm wavelength. Hence, to penetrate with light into the volume of a ceramic powder compound, its light scattering properties need to be investigated and tailored. In the present study we introduce the physical background and material development strategies to apply two-photon-polymerization (2PP), and other volumetric methods for the additive manufacture of filigree structures within the volume of ceramic slurries. T2 - ICACC 2024 CY - Daytona Beach, Florida, USA DA - 28.01.2024 KW - Additive Manufacturing KW - Two Photon Polymerization KW - Advanced ceramics PY - 2024 AN - OPUS4-59889 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Günster, Jens A1 - Sänger, Johanna A1 - Pauw, Brian Richard T1 - Two-Photon-Polymerization for Ceramics Powder Processing N2 - Manipulating ceramic powder compacts and ceramic suspensions (slurries) within their volume with light requires a minimum transparency of the materials. Compared to polymers and metals, ceramic materials are unique as they offer a wide electronic band gap and thus a wide optical window of transparency. The optical window typically ranges from below 0.3 µm up to 5µm wavelength. Hence, to penetrate with laser light into the volume of a ceramic powder compound its light scattering properties need to be investigated and tailored. In the present study we introduce the physical background and material development strategies to apply two-photon-polymerization (2PP) for the additive manufacture of filigree structures within the volume of ceramic slurries. T2 - ECerSXVIII Conference Exhebition of the European Ceramic Society CY - Lyon, France DA - 02.07.2023 KW - Additive Manufacturing KW - Transparent ceramics PY - 2023 AN - OPUS4-59883 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Günster, Jens T1 - Binder Jetting of Advanced Ceramics N2 - The Binder Jetting BJ process is one of the most versatile additive manufacturing technologies in use. In this process a binder is locally jetted into a powder bed for the consolidation of a 3D structure, layer by layer. Basically, all materials which can be provided as a flowable powder and, thus, spreadable to a thin layer, can be processed. Metals, ceramics and polymers are processable, but also materials from nature, such as sand, wood sawdust and insect frass. Moreover, the BJ technology is adapted to large building volumes of some cubic meters easily. Besides these striking advantages, the manufacture of ceramic parts by BJ is still challenging, as the packing density of the powder bed is generally too low and the particle size of a flowable powder too large for a successful densification of printed parts in a subsequent sintering step to an advanced ceramic product. After an introduction of binder jetting in general and highlighting some examples, strategies for obtaining dense ceramic parts by BJ will be introduced. T2 - yCAM 2022 CY - Barcelona, Spain DA - 08.11.2022 KW - Additive Manufacturing KW - Ceramics PY - 2022 AN - OPUS4-59887 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Günster, Jens T1 - Ceramic Processing with Light N2 - In order to be able to manipulate ceramic powder compacts and ceramic suspensions (slurries) in their volume with light, a minimum transparency of the materials is required. Compared to polymers and metals, ceramic materials are characterized by the fact that they have a wide electronic band gap and therefore a wide optical window of transparency. The optical window generally ranges from less than 0.3 µm to 5 µm wavelength. Therefore, to focus light into the volume of a ceramic powder compact, its light scattering properties need to be tailored. In this study, we present the physical background and material development strategies for the application of two-photon polymerization (2PP), Xolography and selective volumetric sintering for the additive manufacturing of structures in the volume of ceramic slips and green compacts. T2 - CMCEE 14 CY - Budapest, Hungary DA - 18.08.2024 KW - Ceramic KW - Additive manufacturing KW - Light PY - 2024 AN - OPUS4-60892 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Günster, Jens T1 - Continuous layer deposition for the Additive Manufacturing of ceramics by Layerwise Slurry Deposition N2 - Powder bed technologies are among the most successful additive manufacturing (AM) techniques. The application of these techniques to most ceramics has been difficult due to the challenges associated with the deposition of homogeneous powder layers when using fine powders. In this context, layerwise slurry deposition (LSD) has been developed as a deposition method that enables the use of powder bed AM technologies for advanced ceramic materials. In layerwise slurry deposition, a ceramic slurry is deposited in layers using a doctor blade and dried to produce a highly compacted powder. Not only can very fine submicron powders with low organic content be processed, but the dense powder bed also provides excellent support for the manufactured parts. The latest development of this technology shows that it is possible to print ceramic parts in a continuous process by depositing a layer on a rotating platform on which a powder bed grows in a spiral motion. The unique mechanical stability of the layers in LSD printing makes it possible to build up a powder bed several centimeters thick without lateral support. Continuous layer deposition achieves more than 10 times the productivity of linear deposition, approaching a build volume of 1 liter per hour. T2 - International Conference on Additive Manufacturing Technology Frontiers CY - Xi’an, China DA - 11.04.2025 KW - Ceramic KW - advanced ceramics PY - 2025 AN - OPUS4-63963 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Günster, Jens T1 - Pulverbasierte additive Fertigung unter reduzierten Schwerkraftbedingungen N2 - 2014 wurden die ersten additiv gefertigten Bauteile in der Internationalen Raumstation (ISS) hergestellt. Die Ära des 3D Drucks im Weltraum startete bereits 2010 mit einem NASA Projekt. Made in Space Inc. entwickelte im Auftrag der NASA einen 3D Drucker auf Basis der Fused Deposition Modeling (FDM) Technologie. Seit 2016 gibt es in der ISS eine Additive Manufacturing Facility und seitdem wurden mittels FDM mehr als hundert Teile aus Kunststoff 3D gedruckt. Die ESA arbeitet gleichfalls an der Entwicklung eines FDM-3D Druckers für die Schwerelosigkeit, z.B. im ESA Projekt „IMPERIAL“, „MELT 3D printer“. Metallische Bauteile mit guten mechanischen Eigenschaften und guter Genauigkeit können kommerziell mittels des Laserstrahlschmelzens (Laser Powder Bed Fusion LPBF) dargestellt werden. Diese Technologie kann allerdings im Weltraum nur unter der Voraussetzung angewendet werden, dass das Pulvermaterial in der Schwerelosigkeit manipuliert und in Form einer dünnen Schicht stabilisiert werden kann. Standard LBM-Anlagen sind deshalb für einen Betrieb in Schwerelosigkeit nicht geeignet, was z.B. auch von Made in Space Inc. in der Vergangenheit beleuchtet wurde. Die pulverbasierte additive Fertigung unter Schwerelosigkeit erfordert die Entwicklung völlig neuartiger Technologien zum Schichtauftrag. Methoden: Mit Hilfe der „Gasflussunterstützten Pulverdeposition“ wurden im Rahmen des Projekts unter reduzierter Schwerkraft systematische Parameterstudien zum LPBF-Prozess durchgeführt. Das Projekt knüpfte an erfolgreiche Vorarbeiten zur Gasflussunterstützten Pulverdeposition unter µg Bedingungen aus vier DLR Parabelflugkampagnen (30., 31., 33. und 34.) an. Ergebnisse: In den Parabelflugkampagnen 76 der ESA und 38 des DLR wurde eine neue Einheit in Wabenform für den Schichtauftrag von Pulver getestet. Es konnte gezeigt werden, dass diese Einheit, die auch als Pulverreservoir funktionierte und mittels eines Aktuators in Schwingungen versetzt wurde, einen reproduzierbaren Schichtauftrag mit geringem Pulververlust unter Schwerelosigkeit ermöglicht. Um die Qualität der aufgetragenen Schicht überwachen zu können, wurde ein Linienscanner beschafft und in die Anlage integriert. Mit diesem kann ein 3D Profil der Schichten im laufenden Prozess erstellt werden, was eine Qualitätskontrolle jeder einzelnen Schicht im Prozess erlaubt. Neben Edelstahl (316L) wurde das Schmelzverhalten von Regolith direkt im Pulverbett unter Bedingungen reduzierter Schwerkraft ebenfalls untersucht. Ein Modell zum Verständnis der Einflussgrößen Gravitation, Schmelzbadgröße, Partikelgröße und Zusammensetzung des Regolith wurde entwickelt. Schlussfolgerungen: Die Entwicklung einer leistungsfähigen Rakeleinheit für den Schichtauftrag unter Schwerelosigkeit ist Voraussetzung für die Generierung defektfreier Bauteile in der pulverbasierten additiven Fertigung in Schwerelosigkeit. Der Übergang zum Werkstoff Regolith hat die Thematik der Verwendung von lokalen Rohstoffen (ISRU), z.B. Mondstaub auf dem Mond, in Kombination mit dem Ziel einer hohen Produktivität beim Aufbau großer Strukturen hervorgebracht. Hierbei ist das Thema einer handhabbaren Schmelzpoolgröße im Laserschmelzprozess unter variierender Schwerkraft in den Fokus gerückt und wird derzeit noch beforscht. T2 - DLR Statussymposium CY - Bonn, Germany DA - 12.03.2025 KW - Regolith KW - Mond KW - ISRU KW - micro-g PY - 2025 AN - OPUS4-63964 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Günster, Jens T1 - Laser beam melting additive manufacturing at μ-gravity N2 - At the Workshop "Neutron and Synchrotron Monitoring in Aerospace Advanced Manufacturing" at the Institute of Materials Physics in Space, German Aerospace Center (DLR) in Cologne, we presented on the opportunities and our experiences of using a powder based additive manufacturing process for in-space manufacturing applications in microgravity. T2 - Workshop 'Neutron and Synchrotron Monitoring in Aerospace Advanced Manufacturing' CY - Cologne, Germany DA - 11.08.2022 KW - Additive manufacturing KW - In-space manufacturing KW - Microgravity KW - μ-gravity KW - Laser beam melting KW - Advanced manufacturing KW - Aerospace KW - Process monitoring PY - 2022 AN - OPUS4-56521 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Günster, Jens T1 - Tailoring powder properties for the light based volumetric additive manufacture of Ceramics N2 - In order to be able to manipulate ceramic powder compacts and ceramic suspensions (slurries) within their volume with light, a minimum transparency of the materials is required. Compared to polymers and metals, ceramic materials are characterized by the fact that they have a wide electronic band gap and therefore a wide optical window of transparency. The optical window generally ranges from less than 0.3 µm to 5 µm wavelength. In order to focus light into the volume of a ceramic powder compact, its light scattering properties must therefore be tailored. In this study, we present the physical background and material development strategies for the application of two-photon polymerization (2PP) and selective volumetric sintering for the additive manufacturing of structures in the volume of ceramic slips and green compacts. T2 - SmartMade 2024 CY - Osaka, Japan DA - 10.04.2024 KW - Additive Manufacturing KW - Two Photon Polymerization KW - Advanced ceramics PY - 2024 AN - OPUS4-59888 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -