TY - CONF A1 - Le, Quynh Hoa A1 - Bäßler, Ralph A1 - Peetz, Christoph A1 - Buggisch, Enrico A1 - Bettge, Dirk A1 - Kranzmann, Axel T1 - Electrochemical study on wellbore constellations for CO2 injection N2 - Carbon Capture and Storage (CCS) is identified as an excellent technology to reach the target of CO2 reduction. However, the safety issue and cost effectiveness hinder the future of CCS. For the reliability and safety issues of injection wells the corrosion resistance of the materials used needs to be determined. In this study, representative low cost materials including carbon steel 1.8977 and low alloyed steel 1.7225 were embedded in cement to mimic the realistic casing-cement interface. Electrochemical studies were carried out using these metal-cement specimens in comparison with those made of metal only in CO2 saturated synthetic aquifer fluid, at 333 K, to reveal the effect of cement on the steel performance. The results showed the protective effect of cement on the performance of pipeline metals during polarisation process. However, the corrosion current density was high in all cases, with and without cement, indicating that the corrosion resistance of these materials is low. This conclusion was supported by the surface analysis of the polarized specimens, which revealed both homogenous and pitting corrosions. Furthermore, to reveal the possible protective performance of FeCO3, the pipeline steels were pre-carbonated and then tested in the same condition as freshly polished specimens. T2 - EUROCORR 2018 CY - Krakow, Poland DA - 09.09.2018 KW - CCUS KW - Supercritical/dense phase CO2 KW - Carbon steels KW - Martensitic steel KW - Superaustenite steel KW - Injection KW - Impurities PY - 2018 AN - OPUS4-46279 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sobol, Oded A1 - Röhsler, Andreas A1 - Nolze, Gert A1 - Unger, Wolfgang A1 - Böllinghaus, Thomas T1 - Sputtering derived artefacts in austenitic steel during Time-of-Flight Secondary Ion Mass Spectrometry analyses N2 - Among the very few techniques to localize hydrogen (H) at the microscale in steels, Time-of-flight secondary ion mass spectrometry (ToF-SIMS) was proven to be a reliable tool. The necessity to detect hydrogen stems from its deleterious effects in metals, that are often used as structural components and to obtain better understanding of the underlying metallurgical mechanisms of hydrogen embrittlement (HE) which are still unclear. Austenitic stainless steels are nowadays commonly used in a wide variety of application, from hydrogen transport and storage facilities to petrochemical and offshore applications where they are exposed to aggressive environments and therefore prone to HE. One of the greater risks in the austenitic class is the embrittlement of the material due to the instability of the γ austenite and its transformation into a brittle α martensitic phase. This transformation takes place due to the local stresses that are induced by the uptake of hydrogen during service. Nonetheless, it was shown that this transformation can occur as an artefact during SIMS analysis itself where Cs-sputtering is necessary not only to remove surface contaminations but mainly to enhance H/D secondary ion yield. In the following contribution we show the influence of different sputtering conditions on AISI 304L austenitic stainless steel in order to distinguish the artefact from the hydrogen induced transformation. The material was charged electrochemically in a deuterium based electrolyte. Deuterium (D) must be in these experiments as a replacement for hydrogen which cannot be used because adsorbed hydrogen superimposes hydrogen originating from charging the sample in the SIMS images. ToF-SIMS analyses were conducted by ToF SIMS IV (IONTOF GmbH, Münster, Germany). The experiments were carried out on deuterium charged and non-charged samples. The structural characterization was carried out by SEM and EBSD examinations before and after charging, both with a Leo Gemeni 1530VP field-emission scanning electron microscope and a Zeiss Supra 40 instrument (Carl Zeiss Microscopy GmbH, Oberkochen, Germany). The results showed that the use of 1keV Cs+ beam induces stacking faults while higher sputter beam energies results in γ→α transformation. T2 - SIMS Europe 2018 CY - Münster, Germany DA - 16.09.2018 KW - Austenitic steel KW - Hydrogen KW - ToF-SIMS KW - Artefact PY - 2018 AN - OPUS4-46701 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kratzig, Andreas A1 - Bettge, Dirk A1 - Peetz, Andreas A1 - Kranzmann, Axel T1 - Interaction of Reactive Components in CO2 Streams with Transport Pipeline Steel X70 N2 - In context of CLUSTER project, impacts of impurities (SO2, NO2, O2, CO, H2S, H2, N2, Ar and H2O) in CO2 streams captured from different sources in a regional cluster on transport, injection and storage were investigated. Corrosion studies of oxidizing, reductive or mixed atmospheres towards transport pipeline steel X70 were carried out applying high pressure (10 MPa) at low temperatures (278 K or 313 K). T2 - GHGT-14 Conference CY - Melbourne, Australia DA - 22.10.2018 KW - Carbon capture KW - CCS KW - Carbon dioxide KW - Corrosion PY - 2018 AN - OPUS4-47017 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Falk, Florian A1 - Menneken, Martina A1 - Stephan-Scherb, Christiane T1 - Early oxidation and sulfidation of high temperature model alloys: An EDXRD in situ study N2 - The fundamental impact of sulfur and water on corrosion rates and potential failure of the exposed material is well known. However, the access to the related corrosion mechanism causing material degradation is often a problem to solve. This study investigates the effect of SO2 and water vapor in the initial stages of corrosion of an Fe9Cr0.5Mn model alloy at 650 °C in situ. The analysis was carried out under laboratory conditions using energy-dispersive X-ray diffraction (EDXRD). T2 - Dechema EFC Workshop CY - Frankfurt am Main, Germany DA - 26.09.2018 KW - Sulfidation KW - Model alloy KW - Oxidation PY - 2018 AN - OPUS4-46134 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Menneken, Martina A1 - Falk, Florian A1 - Stephan-Scherb, Christiane T1 - Early stages of corrosion in hot, aggressive environments N2 - We investigated the effect of water vapor in the initial stages of SO2 corrosion of an Fe-9Cr-0.5Mn model alloy at 650 °C. Two separate experiments were run, one with 99.5%-Ar + 0.5%-SO2 and one with 69.5%-Ar + 0.5%-SO2 with 30%-H2O atmosphere. During the experiment the scale growth was observed in-situ, using energy dispersive X-ray diffraction (EDXRD). Our results confirm an increased speed of oxygen transport into the material, with the addition of water, while the transport of sulfur appears to be less affected. T2 - Sektionstreffen der DMG Sektionen "Angewandte Mineralogie in Umwelt & Technik" und "Chemie, Physik und Kristallographie der Minerale" CY - Bad Windsheim, Germany DA - 28.02.2018 KW - Corrosion KW - In-situ KW - EDXRD PY - 2018 AN - OPUS4-45369 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Le, Quynh Hoa A1 - Bäßler, Ralph A1 - Kratzig, Andreas A1 - Bettge, Dirk A1 - Kranzmann, Axel A1 - Knauer, S. T1 - Droplet corrosion of CO2 transport pipeline steels N2 - In this work, the focus was set on the corrosion process of condensate as drops on the surface of carbon steels (X52, X70), martensitic steel UNS S41500, and superaustenite UNS 08031 in CO2 atmosphere with impurities at 278 K (to simulate the transportation condition in a buried pipeline). Exposure tests were performed at both normal pressure and high pressure where CO2 is supercritical or in dense phase. The drop, 1 ‑ 10 µL in volume, was prepared by dropping CO2 saturated ultra-pure water onto the surface of steel coupons in a one-liter-autoclave. The CO2 gas stream, simulating the oxyfuel flue gas with varying concentration of impurities (SO2 and O2), was then pumped into the autoclave to observe the condensation and corrosion impacts of impurities. Comparable exposure tests were carried out with the same gas mixture and the same volume of water as vapor to observe the drop formation and the corrosion process that follows. The wettability and stability of drops on the surface of steel coupons in CO2 supercritical/dense phase environment was evaluated additionally by contact angle measurement. T2 - NACE International Annual Corrosion Conference CY - Phoenix, AZ, USA DA - 15.04.2018 KW - CCUS KW - Supercritical/dense phase CO 2 KW - Carbon steels KW - Martensitic steel KW - Superaustenite steel KW - Droplet corrosion PY - 2018 AN - OPUS4-44922 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Röhsler, Andreas A1 - Sobol, Oded A1 - Nolze, Gert A1 - Unger, Wolfgang A1 - Böllinghaus, Thomas T1 - In-situ observation of the hydrogen behaviour in austenitic stainless steel by time-of-flight secondary ion mass spectrometry during mechanical loading N2 - The reduction of harmful emissions to the environment is one of the most urgent challenges of our time. To achieve this goal, it is inevitable to shift from using fossil fuels to renewable energy sources. Within this transition, hydrogen can play a key role serving as fuel in transportation and as means for energy storage. The storage and transport of hydrogen using austenitic stainless steels as the infrastructure, as well as the use of these grades in hydrogen containing aggressive environments, remains problematic. The degradation of the mechanical properties and the possibility of phase transformation by ingress and accumulation of hydrogen are the main drawbacks. Advanced studies of the behaviour of hydrogen in austenite is necessary to fully understand the occurring damage processes. This knowledge is crucial for the safe use of components in industry and transportation facilities of hydrogen. A powerful tool for depicting the distribution of hydrogen in steels, with high accuracy and resolution, is time-of-flight secondary ion mass spectrometry (ToF-SIMS). We here present a comprehensive research on the hydrogen degradation processes in AISI 304L based on electrochemical charging and subsequent ToF-SIMS experiments. To obtain furthermore information about the structural composition and cracking behaviour, electron-backscattered diffraction (EBSD) and scanning electron microscopy (SEM) were performed afterwards. All the gathered data was treated employing data fusion, thus creating a thorough portrait of hydrogen diffusion and its damaging effects in AISI 304L. Specimens were charged with deuterium instead of hydrogen. This necessity stems from the difficulty to separate between artificially charged hydrogen and traces existing in the material or adsorbed from the rest gas in the analysis chamber. Similar diffusion and permeation behaviour, as well as solubility, allow nonetheless to draw onclusions from the experiments. T2 - International Conference on Metals and Hydrogen; Steely Hydrogen 2018 CY - Ghent, Belgium DA - 29.05.2018 KW - Hydrogen KW - Deuterium KW - ToF-SIMS KW - AISI 304L PY - 2018 AN - OPUS4-45079 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Goedecke, Caroline A1 - Altmann, Korinna A1 - Bannick, C. G. A1 - Kober, E. A1 - Ricking, M. A1 - Schmitt, T. A1 - Braun, Ulrike T1 - Detection of polymers in treated waste water using TED-GC-MS N2 - The presence of large quantities of plastic waste and its fragmentation in various environmental compartments are an important subject of current research. In the environment, (photo ) oxidation processes and mechanical abrasion lead to the formation of microplastics. However, until now, there are no established quality assurance concepts for the analysis of microplastic (<5 mm) in environmental compartments, including sampling, processing and analysis. The aim of the present work is the development of suitable examination methods and protocols (sampling, sample preparation and detection) to qualify and quantify microplastic in urbane water management systems. At first a fractional filtration system for sampling and the analytical tool, the so-called TED-GC-MS (thermal desorption gas chromatography mass spectrometry) were developed. The TED-GC-MS method is a two-step analytical procedure which consists of a thermal extraction where the sample is annealed and characteristic decomposition products of the polymers are collected on a solid phase. Afterwards these products are analysed using GC-MS. The developed fractional filtration for sampling and the TED-GC-MS for detection were used for quantitative analysis to screen the waste water influent and effluent of a Berlin waste water treatment plant for the most relevant polymers, polyethylene (PE), polypropylene (PP), polystyrene (PS), polyethylene terephthalate (PET) and polyamide (PA). The results of the study revealed that the polymeres PE, PS and PP were detected in the effluent, and PE and PS were find in the raw waste water of the sewage treatment plant in Ruhleben, Berlin. Differences in polymer types and amounts were detected at different sampling dates and within different sieve fractions. Much higher amounts of polymers were observed in the raw waste water. The peak areas of the decomposition products, used for quantification of the polymers, were adjusted using so-called response factors since the TED-GC-MS method is more sensitive for PP and PS than for PE. It has been shown that PE is the most dominant polymer in the samples. Comparing the masses of polymers in the effluent and in the raw sewage, a removal of 99 % of the polymers in the water treatment plant can be assumed. These results are consistent with the literature where removal rates between 98-99 % were described. T2 - SETAC Europe CY - Rom, Italy DA - 13.05.2018 KW - Microplastics KW - Thermogravimetry KW - Waste water KW - Chromatography PY - 2018 AN - OPUS4-44968 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Altmann, Korinna A1 - Goedecke, Caroline A1 - Bannick, C.G. A1 - Ricking, M. A1 - Kober, E. A1 - Schmitt, T. A1 - Braun, Ulrike T1 - Detektion von Polymeren im Abwasser eines Klärwerks mittels TED-GC_MS N2 - In den Umweltmedien Wasser, Boden und Luft wird Mikroplastik (MP) gefunden. Mögliche Eintragspfade, besonders Einträge über den Klarlauf kommunaler Klärwerke, sind unklar. Dazu wurde das Klärwerk Ruhleben in Berlin an jeweils vier Tagen im Sommer- und Winterbetrieb beprobt. Es wurde jeweils 1 m3 Klarlauf fraktioniert filtriert (500, 100 und 50 µm Siebe). Weiterhin wurde Rohabwasser exemplarisch untersucht. Als Analyse-methoden wurden die TED-GC-MS und die FTIR Mikroskopie verwendet. Bei der TED-GC-MS wird die Probe zunächst thermisch extrahiert, bevor die charakteristischen Zersetzungsgase mittels einer GC-Säule getrennt und im MS detektiert werden [1,2]. Es ist hier erstmals gelungen, nicht nur das MP zu identi-fizieren, sondern auch eine Massenbilanz zu erstellen und so eine quantitative Auswertung vorzunehmen. Es wurde PE, PS ganzjährig und PP im Sommer gefunden. Das Klärwerk Ruhleben hat einen Rückhalt an MP von 99%. T2 - Wasser 2018 CY - Papenburg, Germany DA - 07.05.2018 KW - Mikroplastik KW - Abwasser KW - TED-GC-MS KW - Bilanzierung PY - 2018 AN - OPUS4-44889 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wander, Lukas A1 - Braun, Ulrike A1 - Becker, Roland A1 - Maiwald, Michael A1 - Paul, Andrea T1 - Mikroplastikanalyse: Nahinfrarotspektroskopie und chemometrische Auswertung N2 - Für die Erfassung der Verbreitung von Mikroplastik (MP) in der Umwelt ist die zeit- und kostenaufwendige Analysestrategie und der damit verbundene geringe Probendurchsatz eine limitierende Größe. Eine große Zahl verschiedener Studien dokumentriet das Auftreten von MP über den gesamten Globus. Meist sind die Studien aufgrund des großen analytischen Aufwands auf exemplarische, stichpunktartige Untersuchungen kleiner Umweltaliquoten und zahlenmäßig kleiner Probenumfänge begrenzt. Um die Verbreitung, die Eintragspfade und den Verbleib von MP in der Umwelt besser zu verstehen und effektive Vermeidungsstrategien abzuleiten, ist es jedoch notwendig, analytisch mehr Proben erfassen zu können. Bildgebende mikro-spektroskopische Methoden wie das Raman- und FTIR-Imaging ermöglichen eine zeitaufwendige, umfassende Charakterisierung kleiner Umweltaliquoten. Neben der Partikelanzahl sind zusätzlich Informationen zu Partikelgröße, Größenverteilung und Oberflächenmorphologie zugänglich. Chemische und thermische Extraktionsverfahren sind bereits deutlich schneller und können diese Informationen durch eine Massenbilanz vervollständigen. Die analysierbare Probenmenge ist jedoch auf Milligramm Mengen beschränkt. Wir schlagen daher vor, die Analyse von Proben auf MP durch ein vorangestelltes Screening mit der Nahinfrarot-Spektroskopie (NIRS) zur komplementieren. In diesem wird bereits eine erste Einschätzung über die Präsenz von MP in einer Probe gefällt und dadurch die wertvolle Messzeit anderer Methoden effizienter genutzt. NIR zur Analyse von Polymeren wird seit langem eingesetzt, jedoch bisher lediglich im Rahmen einer Studie zur Mikroplastikuntersuchung mittels Hyperspektraler Bildgebung beschrieben. Der NIR Spektralbereich findet sich zwischen dem sichtbaren Licht und dem mittleren Infrarot (MIR). MIR Spektren sind durch klar definierte Banden charakterisiert, welche mehrheitlich von den Grundschwingungen der Moleküle stammen. Die höheren Energien im nahen Infrarot regen hingegen Kombinations- und Oberschwingungen der Streck und Biegeschwingungen an. Die resultierenden Absorptionsbanden sind oft breit und relativ unspezifisch. Erst mit Hilfe einer computergestützten Datenauswertung lassen sich aus diesen Spektren nützliche Informationen gewinnen. Dies erklärt die steigende Popularität der NIR-Spektroskopie in der jüngeren Vergangenheit mit einem Schwerpunkt als prozessanalytische Methode. NIR Spektrometer für das industrielle Prozessmonitoring zeichnen sich durch eine kompakte und robuste Konstruktionsweise aus. Die verfügbaren faseroptischen Reflexionssonden eignen sich gut um pulverförmige Proben zu untersuchen. Der räumlich erfassbare Messbereich kann durch die Sondengeometrie variiert werden. Sind die untersuchten Partikel im Verhältnis zur abgetasteten Fläche klein, wird als spektrale Information die Summe der Absorption aller Partikel im Sichtfeld erfasst. Die Methode ist deshalb nicht für Detailuntersuchungen von MP geeignet, erlaubt es jedoch innerhalb weniger Minuten eine Einschätzung über das Vorkommen von Mikroplastik in einer Probe zu treffen. Exemplarisch wurden für diese Untersuchungen vier der am weitesten verbreiteten Kunststoffe Polyethylen (PE), Polyethylenterephthalat (PET), Polypropylen (PP) und Polystyrol (PS) gewählt. Aus den additivfreien Polymeren wurden nach einer Kryo-vermahlung und anschließender Siebung (< 125 µm) Modellproben generiert. Die Polymere wurden dafür zu einem Massenanteil von 1 % mit einem Standardboden (LUFA2.3, gesiebt < 125 µm) vermischt. Die Gesamtmenge von 1 g je Probe wurde in Aluminiumbehältern präpariert und 8 Messungen an unterschiedlichen, zufällig gewählten Positionen vorgenommen. Die erhaltenen Spektren wurden zur Kalibrierung chemometrischer Modelle genutzt. In einem hierarchischen Ansatz wurde anhand der NIR-Spektren eine Klassifizierung vorgenommen: 1. Bestimmung ob eine Probe MP enthält (Ja/Nein). 2. Identifikation der Polymere in der Probe. Eine aussagekräftige Klassifizierung beruht auf einer Vorbehandlung der Spektren. Hierdurch werden die Unterschiede zwischen den einzelnen Polymerbanden hervorgehoben. Die Eignung der so erstellten Modelle wurde anhand eines Referenzmaterials und am Beispiel von Realproben erfolgreich getestet. Dabei zeigte sich, dass nicht nur in den erstellten Polymer-Bodenmischungen, sondern auch in den Rückständen von fermentiertem Bioabfall und in Filterrückständen einer Waschmaschine, MP richtig erkannt wurde. Weiterhin zeigten Tests mit Mikroplastik-freien Bodenproben unterschiedlicher Herkunft, dass keine falsch-positive Resultate erzeugt wurden. Alle vier untersuchten Polymere, d.h. PE, PET, PS und PP mit einem Massenanteil von 1 % in einer Bodenmatrix werden auch bei einer gemischten Polymerzusammensetzung mit der NIR-Spektroskopie erkannt. Der kombinierte Einsatz von NIRS und Chemometrie ermöglicht die Entscheidung über ein potenzielles Vorkommen sowie die Zuordnung des Materials der enthaltenen Polymerpartikel für eine Massefraktion ≥ 1 % in einer (trockenen) Probenmenge von 1 g innerhalb von 10–15 min. Der zeitaufwendige Schritt der Methode liegt hier in der Erstellung geeigneter chemometrischer Modelle sowie deren Validierung. Wesentliche Voraussetzung ist dabei, dass bei der Kalibrierung die Varianz der zu erwartenden Partikel und der Matrix realistisch abgebildet wird. T2 - GDCh Jahrestagung der Wasserchemischen Gesellschaft CY - Papenburg, Ems, Germany DA - 07.05.2018 KW - Mikroplastik KW - Nahinfrarotspektroskopie KW - Chemometrie KW - Boden PY - 2018 AN - OPUS4-44887 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Usmani, Shirin A1 - Stephan, Ina A1 - Huebert, Thomas A1 - Kemnitz, E. T1 - Nano metal fluorides for wood protection against fungi JF - ACS Applied Nano Materials N2 - Wood treated with nano metal fluorides is found to resist fungal decay. Sol−gel synthesis was used to synthesize MgF2 and CaF2 nanoparticles. Electron microscopy images confirmed the localization of MgF2 and CaF2 nanoparticles in wood. Efficacy of nano metal fluoride-treated wood was tested against brown-rot fungi Coniophora puteana and Rhodonia placenta. Untreated wood specimens had higher mass losses (∼30%) compared to treated specimens, which had average mass loss of 2% against C. puteana and 14% against R. placenta, respectively. Nano metal fluorides provide a viable alternative to current wood preservatives. KW - Brown-rot fungi KW - Coniophora puteana KW - Fluoride nanoparticles KW - Fluorolytic sol−gel KW - Rhodonia placenta KW - SEM wood characterization KW - Wood protection PY - 2018 DO - https://doi.org/10.1021/acsanm.8b00144 SN - 2574-0970 VL - 2018 SP - 1 EP - 6 PB - American Chemical Society (ACS) CY - Washington DC, US AN - OPUS4-44730 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Schmidt, Wolfram A1 - Ramirez Caro, Alejandra A1 - Sojref, Regine A1 - Mota Gassó, Berta ED - Greim, M. ED - Kusterle, W. ED - Teubert, O. T1 - Contribution of the coarse aggregates to rheology - effects of flow coefficient, particle size distribution, and volume fraction T2 - Rheologische Messungen an Baustoffen 2018 N2 - In order to observe the effect of the aggregate phases between 2 mm and 16 mm without overlap with rheological effects induced by the cement hy-dration and without interactions with a threshold fine sand particle size that affects both, paste and aggregates, rheological experiments were conducted on a limestone filler based paste mixed with aggregates up to 16 mm. Vari-ous aggregate fractions were blended and mixed with the replacement paste in different volumetric ratios. The dry aggregates’ flow coefficients were determined and compared to yield stress and plastic viscosity values at different aggregate volume fractions. The results indicated that the flow coefficient is not a suitable parameter to predict the performance of the aggregates in the paste. It was shown that the yield stress of pastes is largely determined by the blend of different aggregate fractions, while the plastic viscosity to large extend depends upon the coars-est aggregate fraction. Based on the results, ideal aggregate composition ranges for minimised yield stress are presented. For the plastic viscosity no such grading curves to achieve minimum values could be found, but high viscosity curves are identified. KW - Rheology KW - Flow Coefficient KW - Particle Size Distribution KW - Volume Fraction KW - Cement KW - Concrete KW - Reference Material KW - Limestone Filler PY - 2018 SN - 978-3-7469-1878-5 SP - 96 EP - 108 PB - tredition GmbH CY - Hamburg AN - OPUS4-44434 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Altenburg, Simon A1 - Maierhofer, Christiane A1 - Hilgenberg, Kai A1 - Mohr, Gunther A1 - Gumenyuk, Andrey A1 - Straße, Anne A1 - Pittner, Andreas A1 - Günster, Jens A1 - Gornushkin, Igor B. A1 - Pelkner, Matthias A1 - Ehlers, Henrik A1 - Heckel, Thomas A1 - Zscherpel, Uwe A1 - Seeger, Stefan A1 - Bruno, Giovanni T1 - ProMoAM - Verfahrensentwicklung für das Prozessmonitoring in der additiven Fertigung N2 - Verfahren zum in-situ Monitoring der Prozess- und Bauteilparameter sollen Fehlstellen und Inhomogenitäten bereits während der Fertigung nachweisen und zukünftig auch die Regelung der Prozessparameter ermöglichen. T2 - Challenges in Additive Manufacturing: Innovative Materials and Quality Control, Berlin Partner Workshop CY - Berlin, Germany DA - 12.09.2018 KW - Additive Fertigung KW - Prozessmonitoring KW - ProMoAM PY - 2018 AN - OPUS4-46300 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Panne, Ulrich A1 - Braun, Ulrike A1 - Schartel, Bernhard A1 - Weidner, Steffen A1 - Rurack, Knut A1 - Thünemann, Andreas A1 - Sturm, Heinz T1 - Polymerwissenschaften@BAM - Sicherheit macht Märkte N2 - Die Bundesanstalt für Materialforschung und -prüfung (BAM) ist eine Ressortforschungseinrichtung, die zum Schutz von Mensch, Umwelt und Sachgüter, forscht, prüft und berät. Im Fokus aller Tätigkeiten in der Materialwissenschaft, der Werkstofftechnik und der Chemie steht dabei die technische Sicherheit von Produkten und Prozessen. Dazu werden Substanzen, Werkstoffe, Bauteile, Komponenten und Anlagen sowie natürliche und technische Systeme erforscht und auf sicheren Umgang oder Betrieb geprüft und bewertet. Schwerpunkt des Vortrages sind multimodale Polymeranalytik, nanoskalige Sensormaterialien und die Charakterisierung von technischen Eigenschaften von Polymeren sowie ihre Alterung und Umweltrelevanz. T2 - Institutsvortrag CY - Fraunhofer IAP, Potsdam, Germany DA - 18.05.2018 KW - Polymerwissenschaften PY - 2018 AN - OPUS4-45243 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -