TY - GEN A1 - Ávila Calderón, Luis Alexander A1 - Matzak, Kathrin A1 - Olbricht, Jürgen A1 - Dolabella Portella, Pedro A1 - Skrotzki, Birgit T1 - BAM Reference Data: High Temperature Tensile Data of Single-Crystal Ni-Based Superalloy CMSX-6 N2 - This publication provides comprehensive metadata and test results of tensile tests at elevated temperature according to DIN EN ISO 6892-2:2018-09 on the single crystal Ni-based superalloy CMSX-6 at T = 980 °C. The tests were performed in an ISO 17025-accredited test laboratory. The calibrations of measuring equipment are documented, meet the requirements of the measurement standard, and are metrologically traceable. The provided data were audited and are BAM reference data. KW - Digitalisierung KW - Referenzdaten KW - CMSX-6 KW - Zugversuch KW - NFDI-MatWerk KW - Ni-Basis-Superlegierung PY - 2025 DO - https://doi.org/10.5281/zenodo.17846616 PB - Zenodo CY - Geneva AN - OPUS4-65338 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kianinejad, Kaveh A1 - Czediwoda, Fabian A1 - Glatzel, U. A1 - Völkl, R. A1 - Stöhr, B. A1 - Ávila Calderón, Luis A1 - Schriever, Sina A1 - Saliwan Neumann, Romeo A1 - Fedelich, Bernard A1 - Darvishi Kamachali, Reza T1 - Microstructure-based modelling of the anisotropic creep behaviour in additively manufactured INCONEL 718 N2 - The existing gap in the adequate prediction of the microstructure-property relationships remains a significant barrier to the safe application of the additively manufactured materials. This challenge is fundamentally tied to the intricate microstructural defects that emerge during the processing. Systematic microstructure-based modelling can offer solutions to address this bottleneck. In this work, we utilize a crystal plasticity model, developed for gamma''-strengthened Ni-base alloys and calibrated with single crystal tensile and creep tests of Inconel 718. By systematically refining the representative volume element complexity---from equiaxed to elongated grain morphologies, and from unimodal to bimodal orientation and grain size distributions---we demonstrate how each layer of structural realism contributes to the model’s predictive capacity. Creep tests of laser-based powder bed fusion (PBF-LB/M) manufactured samples in three orientations (with the tensile axis parallel, perpendicular, and 45° tilted relative to the building direction) were performed at 650° C, accompanied by electron backscatter secondary diffraction measurements. The results of our simulations reveal that the bimodal grain morphology and crystallographical texture significantly influence the observed creep anisotropy. We show that the elongated grain structure combined with grain boundary sliding plays a major role in the creep response, specifically in tilted specimens. KW - Additive manufactured Ni-base superalloys KW - Creep Anisotropy KW - Crystal plasticity PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-646884 DO - https://doi.org/10.1016/j.msea.2025.149029 VL - 945 SP - 1 EP - 15 PB - Elsevier B.V. AN - OPUS4-64688 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Abel, Andreas T1 - Microstructural and mechanical characterisation of cast Fe-Al-Mo-Ti-B alloys N2 - With the advent of variable renewable energies, long-term energy storage capacities and flexible power generation technologies will be required for reliable grid stability. Hence, power plant technologies and turbomachinery components will continue to be developed and employed for efficient re-conversion of stored energy. With the introduction of new working fluids for higher thermal efficiencies, the working conditions of exposed components and materials will require higher corrosion resistance, but with the same mechanical performance, manufacturability and cost. Intermetallic iron aluminide alloys with their outstanding oxidation and corrosion resistance and good high-temperature properties depict a possible candidate for use in high-temperature structural applications. A quinary Fe-26Al-4Mo-0.5Ti-1B solid-solution alloy with eutectic particle hardening particularly demonstrated competitive mechanical properties compared to high-alloy P92 steels in previous studies. To derive standard material specifications with industrially relevant casting strategies, centrifugal investment-cast Fe-25Al-3.7Mo-0.4Ti-1B was characterised with respect to microstructure, thermophysical properties and mechanical properties under quasi-static tensile and creep loading up to 700 °C. Compared to P92 steel, the alloy demonstrated superior tensile strength above 550 °C and lower creep rates at 650 °C if stresses increase above 170 MPa. At lower temperatures though, the mechanical properties were inferior to P92 steel and related Fe-Al-Mo-Ti-B alloys, which was correlated to large grain sizes, a high tendency to surface and bulk cracking and a pronounced effect of tension-compression asymmetry. In further studies on alloy composition with varying Al, Mo and B concentration, a non-linear relationship of solid-solution hardening with solute Mo concentration was found. In this regard, halving Mo was the most effective measure for reducing brittleness without decreasing strength at room and elevated temperatures. Higher solidification rates and grain refinement down to 30 µm by die casting had a positive effect on ambient tensile strength, but were not achievable by investment casting. Dilatometry and hardness measurements indicated a low thermal vacancy hardening effect which was less sensitive to low-temperature annealing than in B2 FeAl alloys. Although mechanical properties up to 550 °C could be considerably improved by alloy development and processing, ductility at room temperature generally remained below 1%, necessitating substantial design margins for components from Fe-Al-Mo-Ti-B alloys. Despite the inherent limitations of alloy and casting process, the gained insights will help to prioritise future areas of research to mature cost-effective higher-order Fe Al alloys for high-temperature structural applications. KW - Hardness KW - Iron aluminide alloy KW - Micro structure KW - Tensile strength KW - Creep strength PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-632810 DO - https://doi.org/10.5445/IR/1000181739 SP - 1 EP - 179 PB - Karlsruher Institut für Technologie (KIT) CY - Karlsruhe AN - OPUS4-63281 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ávila Calderón, Luis T1 - Management of Reference Data of Creep of Ni-Based Superalloys Exemplified for CMSX-6 N2 - The identification of process-structure-property relationships of materials inevitably requires the combination of research data from different measurements. Therefore, the concepts related to FAIR (findable, accessible, interoperable, reusable) data handling, increasingly reported in literature, are particularly important in the materials science and engineering domain. However, they have not yet been integrated into a single, overarching methodological framework, particularly for reference data. Here, we introduce such a framework, which covers data generation, documentation, handling, storage, sharing, data search and discovery, retrieval, and usage. Furthermore, we prototypically implement it using a real dataset with creep data of a single-crystal CMSX-6 Ni-based superalloy. The implementation is traceable and permanently accessible through open repositories. The individual elements considered in the framework ensure the functionality and usability of the data and, thus, the adherence to the FAIR principles. In conjunction with this, we present a definition for reference data of materials. Our definition underlines particularly the importance of a comprehensive documentation, e.g., on material provenance, data processing procedures, and the software and hardware used, including software-specific input parameters, as these details enable data users or independent parties to assess the quality of the datasets and to reuse and reproduce the results. Reference data that is managed according to the proposed framework can be used to advance knowledge in the materials science and engineering domain, e.g., by identifying new process-structure-property relations. T2 - The 20th International Conference on Strength of Materials CY - Kyoto, Japan DA - 02.06.2025 KW - NFDI-MatWerk KW - Referenzdaten KW - Data schema KW - Creep PY - 2025 AN - OPUS4-63428 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ávila Calderón, Luis T1 - Management of Reference Data of Creep of Ni-Based Superalloys Exemplified for CMSX-6 N2 - The identification of process-structure-property relationships of materials inevitably requires the combination of research data from different measurements. Therefore, the concepts related to FAIR (findable, accessible, interoperable, reusable) data handling, increasingly reported in literature, are particularly important in the materials science and engineering domain. However, they have not yet been integrated into a single, overarching methodological framework, particularly for reference data. Here, we introduce such a framework, which covers data generation, documentation, handling, storage, sharing, data search and discovery, retrieval, and usage. Furthermore, we prototypically implement it using a real dataset with creep data of a single-crystal CMSX-6 Ni-based superalloy. The implementation is traceable and permanently accessible through open repositories. The individual elements considered in the framework ensure the functionality and usability of the data and, thus, the adherence to the FAIR principles. In conjunction with this, we present a definition for reference data of materials. Our definition underlines particularly the importance of a comprehensive documentation, e.g., on material provenance, data processing procedures, and the software and hardware used, including software-specific input parameters, as these details enable data users or independent parties to assess the quality of the datasets and to reuse and reproduce the results. Reference data that is managed according to the proposed framework can be used to advance knowledge in the materials science and engineering domain, e.g., by identifying new process-structure-property relations. T2 - TMS 2025 Annual Meeting & Exhibition CY - Las Vegas, NV, USA DA - 22.03.2025 KW - Referenzdaten KW - Creep KW - Data schema KW - NFDI-MatWerk PY - 2025 AN - OPUS4-62849 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schilling, Markus T1 - Semantic Technologies in Action: Integrating Mechanical and Microstructure Data in MSE N2 - Semantic technologies (ST) are a powerful tool for storing, processing, and querying data in a contextualized and interoperable manner. They enable machine-actionable and human-readable knowledge representations essential for advanced data management, retrieval, and reuse. As one of the key factors within the frame of the collaborative project platform MaterialDigital (PMD), the establishment of a virtual material data space and the semantic modeling of hierarchical, process-dependent material data is aimed at to serve as best-practice examples of knowledge representation through ontologies and knowledge graphs. In this presentation, the application of ST to a specific use case from the field of materials sciences and engineering (MSE) is demonstrated: the integration and analysis of data related to a 2000 series age-hardenable aluminum alloy. By semantically representing mechanical and microstructural data obtained from tensile tests and dark-field transmission electron microscopy across various aging times, an expandable knowledge graph was constructed that is aligned with the PMD Core Ontology (PMDco) and enriched through the Tensile Test (TTO) and Precipitate Geometry Ontologies. This semantically integrated dataset enables advanced analytical capabilities via SPARQL queries and reveals microstructure–property relationships consistent with the well-known Orowan mechanism. The approach highlights the potential of semantic data integration to support FAIR data principles and to foster a more data-centric and interoperable research infrastructure in MSE. T2 - MSE Research Data Forum 2025 CY - Siegburg, Germany DA - 08.07.2025 KW - Semantic Data KW - Data Integration KW - Digitalization KW - Data Interoperability PY - 2025 AN - OPUS4-63666 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ávila Calderón, Luis T1 - IUC02: Framework for Curation & Distribution of Reference Datasets (On the example of Creep Data of Ni Based superalloys) N2 - A research data management framework to conceptualize & implement a digital infrastructure for the Generation, Distribution, and Utilization of reference datasets of materials is presented. The documentation of the test data is often incomplete. This concerns, e.g., material’s manufacturing process or chemical composition, or test equipment’s description and its calibration status. Our concept addresses this issue by proposing the implementation of a requirements profile. A crucial part of the concept is to reach a community-agreement on the definition of reference data and on the underlying data schema and vocabulary. In this presentation a general workflow overview and the relevance of selected individual subworkflows is presented. T2 - MSE Research Data Forum 2025 CY - Siegburg, Germany DA - 08.07.2025 KW - NFDI MatWerk KW - Referenzdaten KW - Kriechen PY - 2025 AN - OPUS4-64881 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ávila Calderón, Luis T1 - Management of Reference Data of Creep of Ni Based Superalloys Exemplified for CMSX 6 N2 - Research data management (RDM) framework to conceptualize & implement a digital infrastructure for the Generation, Distribution, and Utilization of reference datasets of materials. Documentation of the test data is often incomplete. This concerns, e.g., material’s manufacturing process or chemical composition, or test equipment’s description and its calibration status. Our concept addresses this issue by proposing the implementation of a requirements profile. A crucial part of the concept is to reach a community-agreement on the definition of reference data and on the underlying data schema and vocabulary. T2 - 2. SupERBO Symposium on Superalloys CY - Bochum, Germany DA - 27.02.2025 KW - NFDI MatWerk KW - Referenzdaten KW - Kriechen PY - 2025 AN - OPUS4-64859 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schilling, Markus T1 - Platform MaterialDigital (PMD) - Knowledge Representation, Interoperability, Reliability N2 - Through collaboration in the materials science and engineering (MSE) community, the PMD is collectively developing common standards and prototype solutions for data acquisition, structuring, storage, and processing. This comprises the development of architectural, standardized and foundational ontologies and workflows. Demonstrators resulting from these developments provide good practice examples. The PMD Core Ontology (PMDco) was created as an anchor that allows implementation of semantic data integration. It provides a common and expanding vocabulary to represent and share knowledge while enabling efficient collaboration and promoting interoperability between diverse domains. T2 - Kupfer-Symposium 2025 CY - Schwäbisch-Gmünd, Germany DA - 12.11.2025 KW - Semantic Data KW - Data Integration KW - Digitalization KW - Data Interoperability KW - PMD Core Ontology PY - 2025 AN - OPUS4-64708 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ávila Calderón, Luis T1 - Management of Reference Data in Materials Science and Engineering Exemplified for Creep Data of a Single-Crystalline Ni-Based Superalloy N2 - Here we present our research data management (RDM) framework to conceptualize & implement a digital infrastructure for the Generation, Distribution, and Utilization of reference datasets of materials. The documentation of the test data is often incomplete. This concerns, e.g., material’s manufacturing process or chemical composition, or test equipment’s description and its calibration status. Our concept addresses this issue by proposing the implementation of a requirements profile. A crucial aspect of our concept is to reach a community-agreement on the definition of reference data and on the underlying data schema and vocabulary. T2 - MaRDA2025 Virtual Annual Meeting CY - Online meeting DA - 18.02.2025 KW - NFDI MatWerk KW - Referenzdaten KW - Kriechen KW - Datenschema PY - 2025 AN - OPUS4-64858 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ávila Calderón, Luis A1 - Shakeel, Y. A1 - Gedsun, A. A1 - Forti, M. A1 - Hunke, S. A1 - Han, Ying A1 - Hammerschmidt, T. A1 - Aversa, R. A1 - Olbricht, Jürgen A1 - Chmielowski, M. A1 - Stotzka, R. A1 - Bitzek, E. A1 - Hickel, Tilmann A1 - Skrotzki, Birgit T1 - Management of reference data in materials science and engineering exemplified for creep data of a single-crystalline Ni-based superalloy N2 - The identification of process-structure-property relationships of materials inevitably requires the combination of research data from different measurements. Therefore, the concepts related to FAIR (findable, accessible, interoperable, reusable) data handling, increasingly reported in literature, are particularly important in the materials science and engineering domain. However, they have not yet been integrated into a single, overarching methodological framework, particularly for reference data. Here, we introduce such a framework. Our concept covers data generation, documentation, handling, storage, sharing, data search and discovery, retrieval, and usage. Furthermore, we prototypically implement it using a real dataset with creep data of a single-crystal CMSX-6 Ni-based superalloy. The presented implementation is traceable and permanently accessible through open repositories. The individual elements considered in the framework ensure the functionality and usability of the data and, thus, the adherence to the FAIR principles. In conjunction with this, we present a definition for reference data of materials. Our definition underlines particularly the importance of a comprehensive documentation, e.g., on material provenance, data processing procedures, and the software and hardware used, including software-specific input parameters, as these details enable data users or independent parties to assess the quality of the datasets and to reuse and reproduce the results. Reference data that is managed according to the proposed framework can be used to advance knowledge in the materials science and engineering domain, e.g., by identifying new process-structure-property relations. KW - Referenzdaten KW - NFDI-MatWerk KW - Data schema KW - Research Data Management KW - Reference Data PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-625047 DO - https://doi.org/10.1016/j.actamat.2025.120735 VL - 286 SP - 1 EP - 15 PB - Elsevier Inc. AN - OPUS4-62504 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Agudo Jácome, Leonrado T1 - Low-Cycle Fatigue Behavior of Laser Powder Bed Fused Inconel 718 at Room and High Temperature N2 - The nickel-base superalloy Inconel 718 (IN718) is one of the most commonly used Ni-based superalloys for high temperature structural applications for its remarkable strength, as well as creep, fatigue, and corrosion resistance up to 650 °C. While IN718 has traditionally been employed as cast or wrought material, it is difficult to machine because of its high strength and toughness. The additive manufacturing of IN718 components made by metal AM has thus gained extensive attention to produce expensive near-net shaped components of high-temperature alloys such as IN718, for it saves material and costs in processing and machining steps. Among all metal additive manufacturing (AM) technologies, laser powder bed fusion (PBF-LB/M) is the most widespread, IN718 being one of the most common alloys produced with it. However, high cooling rates associated to the PBF-LB/M process, hinders the primary strengthening phases γ’’ and γ’ to form, as these cooling rates induce a dislocation cellular substructure, at which walls primary Laves phases bind segregating Nb, Ti and Mo. Many of the therefore needed heat-treatment strategies can then promote Laves-phase transformation into the stable δ phase along the cell and grain boundaries. Laves and δ phases, as well as grain-boundary primary carbides may have adverse effects on mechanical properties. The mostly needle-shaped δ phase was namely found to have a detrimental effect on creep rupture life while no direct effect on LCF fatigue life was evident. In this work room- and high-temperature (650 °C) low-cycle fatigue behavior of PBF-LB/M IN718 is investigated in the four-step heat-treated state and compared to wrought IN718. The microstructure of both materials is characterized across length scales via microscopy methods. The fatigue life at room temperature of the PBF-LB/M IN718 material is slightly lower than that for the wrought material, which is reversed at 650 °C. The cyclic stress response for both materials is marked by cyclic softening that is more pronounced at higher test temperatures. Multiple secondary cracks form at high strain amplitudes, at both room and high temperatures. High testing temperatures enhance specially crack formation at the transitions of regions between elongated grains and columns of stacked grains with ripple patterns in the PBF-LB/M material. Additional to this behavior, pronounced crack branching and deflection indicate that the cracks are controlled by sharp micromechanical gradients. T2 - EUROMAT 2025 CY - Granada, Spain DA - 14.09.2025 KW - Additive manufacturing KW - Low-cycle fatigue KW - Microstructural characterization KW - Ni-base superalloy PY - 2025 AN - OPUS4-64354 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ávila Calderón, Luis A1 - Han, Ying A1 - Matzak, Kathrin A1 - Olbricht, Jürgen A1 - Skrotzki, Birgit T1 - NFDI-MatWerk/IUC02 data schema for elevated temperature tensile data of Ni-based superalloys N2 - Strength characteristics, such as proof strength and tensile strength, of metallic materials are usually measured at room temperature. However, for high-temperature materials, the values at operational temperatures are equally important for analyzing the mechanical behavior of components or for designing purposes. Elevated temperature tensile tests (often referred to as hot tensile tests) generally enable the measurement of the same material parameters as those obtained at room temperature. Typically, tensile and proof strength, elongation after fracture, and reduction of area are analyzed, with the focus often being on proof strength. The attached data schema for elevated temperature tensile tests was developed within the German NFDI-MatWerk initiative (https://nfdi-matwerk.de/). It builds on a previously published creep data schema and follows a reference data methodology that has also been previously outlined. The presented schema constitutes a structured approach for collecting all relevant information on an elevated temperature tensile test experiment. Overall, this development, as defined in the previously published data schema for creep data, aims to provide a comprehensive hierarchical data description that can be implemented in data management platforms (such as electronic laboratory notebooks), facilitate consistent quality assessment across different users and data providers, and promote the alignment of datasets to the FAIR principles by providing easy interoperability and full reusability. The presented schema was initially developed for datasets of Ni-based high-temperature alloys. However, thanks to its modular structure, it can also be applied to tensile tests of various metallic and other materials. Although the focus is on elevated temperature tensile testing, the data schema also offers a solid foundation for documenting room temperature tensile tests. In such cases, an adjustment of the requirement profile might be necessary, and categories or entries specific to mechanical testing at elevated temperatures, such as “temperature-measuring system”, “specified temperature”, or “soaking time”, become irrelevant. Overall, a detailed approach was followed to ensure the collection of all relevant information, including both metadata and test results. This includes, for example, comprehensive descriptions of the material’s manufacturing history and of the laboratory equipment, and basic strength and deformation characteristic values. The resulting data schema aims to support the description and identification of high-quality datasets, which may qualify as reference data of materials. Our current definition of reference data of materials has been published elsewhere. It should be noted, however, that not all research datasets —depending on their origin and purpose— require this full level of detail. Nevertheless, the presented data schema can support data providers in evaluating the completeness and value of their datasets. This version of the data schema covers elevated temperature tensile tests on both single- and polycrystalline specimen materials. The terminology is aligned with DIN EN ISO 6892-1 and DIN EN ISO 6892-2. It is designed to record the use of temperature measurement using thermocouples and the use of contacting extensometer systems. The requirement profile refers to the highest quality class of reference data, taken from calibrated instruments, and which shall enable the following usages: 1. Checking one's own elevated temperature tensile test results on nominally similar material 2. Verification of own testing set-up (e.g., by testing the same or a similar material) 3. Using the data as input data for simulations in the context of design or alloy development KW - NFDI MatWerk KW - Referenzdaten KW - Zugversuch KW - CMSX-6 KW - Datenschema KW - NFDI MatWerk KW - CMSX-6 KW - Data schema KW - Reference data KW - Tensile test PY - 2025 UR - https://doi.org/10.5281/zenodo.17846436 DO - https://doi.org/10.5281/zenodo.17846435 PB - Zenodo CY - Geneva AN - OPUS4-65190 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Eisenbart, Miriam A1 - Hanke, Thomas A1 - Bauer, Felix A1 - Beygi Nasrabadi, Hossein A1 - Junghanns, Kurt A1 - Dziwis, Gordian A1 - Tikana, Ladji A1 - Parvez, Ashak Mahmud A1 - van den Boogaart, Karl Gerald A1 - Sajjad, Mohsin A1 - Friedmann, Valerie A1 - Preußner, Johannes A1 - Ramakrishnan, Anantha Narayanan A1 - Klengel, Sandy A1 - Meyer, Lars‐Peter A1 - Martin, Michael A1 - Klotz, Ulrich Ernst A1 - Skrotzki, Birgit A1 - Weber, Matthias T1 - KupferDigital: Ontology‐Based Digital Representation for the Copper Life Cycle N2 - The copper life cycle comprises numerous stages from the alloy production to the manufacturing and usage of engineered parts until recycling. At each step, valuable data are generated and stored; some are transferred to the subsequent stations. A thorough understanding of the materials’ behavior during manufacturing processes or throughout their product lifetime is highly dependent on a reliable data transfer. If, for example, a failure occurs during the service life, information about the manufacturing route can be of decisive importance for detecting the root cause of the failure. Additionally, the life cycle assessment hinges on the availability of data. Recording and storing interoperable structured data is, therefore, a thriving research field with huge implications for the economic strength of the manufacturing industry. In the KupferDigital project, it is demonstrated how an ontology‐based data space can be utilized not only as an innovative method for storing and providing interoperable life cycle data but also as a means to enable automated data analysis and evaluation, leading to new insights and the creation of new knowledge using semantic data and technologies. This work illustrates how data recorded at different research facilities can be integrated into one single data space, allowing queries across heterogeneous sources. KW - Copper Alloy KW - Ontology KW - Digitalization KW - Data Space KW - Semantic Representation PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-630213 SN - 1527-2648 DO - https://doi.org/10.1002/adem.202401735 VL - 27 IS - 8 SP - 1 EP - 29 PB - Wiley AN - OPUS4-63021 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Suarez Ocano, Patricia T1 - Influence of heat-treatment-induced microstructural evolution on the Low Cycle Fatigue behavior of 316L stainless steel fabricated by Laser Powder Bed Fusion N2 - Additive manufacturing, particularly the laser powder bed fusion (PBF-LB/M) process, has gained significant attention in recent years due to its ability to produce complex geometries with enhanced mechanical properties. Among the various materials used, 316L stainless steel is highly favored for cyclically loaded components due to its exceptional mechanical strength, high-temperature performance, and corrosion resistance, making it widely applicable across various industries. 316L SS fabricated by PBF-LB/M (PBF-LB/M/316L) exhibits a unique hierarchical microstructure, with high density of low-angle grain boundaries (LAGBs), nano-dispersed silicates, chemical micro-segregations, and solidification-induced cellular structures. Particularly, the submicron-sized cellular features enriched with chromium (Cr) and molybdenum (Mo), along with high dislocation densities, contribute to a superior strength-ductility balance compared to conventionally manufactured 316L SS. The dispersed silicate particles act also as a strengthening phase, impeding dislocation movement and enhancing plastic deformation resistance. This study explores the effect of heat treatments on the low-cycle fatigue (LCF) behavior of PBF-LB/M/316L at room temperature (RT) and 600 °C. First, three heat treatment conditions were applied to the as-built material: 450 °C for 4 hours (HT450/4), 800 °C for 3 hours (HT800/3), and 900 °C for 1 hour (HT900/1) to investigate their influence on microstructural evolution. Microstructural analysis revealed that the HT450/4 condition preserved the cellular structure with high dislocation density, while the HT800/3 condition showed partial dissolution of cells together with reduction in segregated elements along the cell walls and a reduced dislocation density. The HT900/1 condition resulted in complete segregation and cellular structure dissolution with comparable dislocation density to HT800/3 while maintaining the crystallographic texture and grain morphology. Intermetallic χ phase was mostly observed at the grain boundaries in HT800/3, but not in HT900/1. Fully reversed LCF tests were conducted under strain-controlled conditions with a strain amplitude of 0.8 %. Tests were interrupted at specific intervals to analyze the interaction between hierarchical microstructural features and deformation mechanisms in the three heat-treated conditions. Due to the pronounced dislocation cell structures and elemental segregation, the microstructure of the HT450/4 condition significantly impact deformation and damage mechanisms during cyclic loading, which in turn, differ from the conventional produced counterparts. The results provide insights into the relationship between microstructural features and fatigue performance, highlighting key deformation and failure mechanisms under cyclic loading. T2 - FEMS 2025 EUROMAT 18th European Congress and Exhibition on Advanced Materials and Processes CY - Granada, Spain DA - 14.09.2025 KW - Additive manufacturing KW - 316L stainless steel KW - Heat treatments KW - Low Cycle Fatigue KW - Microstructure PY - 2025 AN - OPUS4-64238 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Jentzsch, Stefan A1 - Stock, Daniel A1 - Häcker, Ralf A1 - Skrotzki, Birgit A1 - Darvishi Kamachali, Reza A1 - Klingbeil, Dietmar A1 - Kindrachuk, Vitaliy T1 - Split Hopkinson Pressure Bar (SHPB) investigations of steel S355 specimens and complementary characterization methods N2 - The workbook SHPB_S355.xlsx contains in the main spreadsheet S355_TestOverview an overview on the S355 specimens, which were tested in Split Hopkinson Pressure Bar (SHPB) and complementary quasi-static (QS) tests. The tests were conducted with notched hat-shaped specimens without a notch offset (S355_TestOverview/column geometry: “no offset”) and a small notch offset of x=0.35 mm (S355_TestOverview/column geometry: “offset”), cf. Fig. 1 [1]. Furthermore, for selected specimens, links are provided to DIC and bar strain measurement files as well as to evaluations from further characterization methods (microhardness, EBSD). For the boundary conditions at the SHPB projectile impact, the pressures of the compressor p, driving the projectile, and the associated projectile impact velocities are provided in SHPB_S355.xlsx. The DIC displacement measurements are provided in FurtherMeasurements/DIC with frame output times in the file labels, which are associated with an imaginary trigger at the left end of the shortened incident bar (length 300 mm), which is considered within the SHPB simulation setup, see [1]. Furthermore, the DIC reference coordinate systems are provided as COS.jpg files in the respective DIC folders. Starting from the strain signals at the bars, captured by strain gauges at the incident (file name BC_Inc) and transmission bar (BC_Trans), displacement boundary conditions (which are provided for the tests in FurtherMeasurements/BarDisplBCs) are calculated by eq. (12) in [1], incorporating the acoustic velocity equal to 4639 m/s at the bars and a correction factor. Fig. 1 shows the shear specimen geometry (lengths in mm) with the offset of the notches x. For the quasi-static tests force(displacements)-values are directly provided in FurtherMeasurements/Fu_curves, which are considered from the relative displacements of the specimens, evaluated by DIC. The Vickers microhardness (HV 0.01) distribution across the shear localization zone was assessed by QNESS 60A+ EVO (DIN EN ISO 6507-1) for quasi-statically and dynamically tested specimens, applying the small notch offset, such that the specimens did not fail in the localization region. Therefore, raw data is provided in FurtherMeasurements/Microhardness. For fitting the microhardness distribution perpendicularly to the shear bands (as i.e. provided for the SHPB specimen in [1]), representative microhardness profiles were considered. Similarly for specimens with the small notch offset, EBSD data on dynamic and quasi-static tests is provided in FurtherMeasurements/EBSD. The grain size distributions for positions at the notch and the undeformed region are included in the subdirectory ./GrainLists_Shortened and EBSD images in the PowerPoint Presentations. Further information as the sizes and misorientations of the single grains, is incorporated in the subfolders ./GrainLists_FurtherInf. KW - Adiabatic shear bands KW - Split Hopkinson pressure bar KW - Digital image correlation PY - 2025 DO - https://doi.org/10.5281/zenodo.17591439 PB - Zenodo CY - Geneva AN - OPUS4-64842 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Evans, Alexander A1 - Schröder, Jakob A1 - Pirling, T. A1 - Ulbricht, Alexander A1 - Suárez Ocaño, Patricia A1 - Bruno, Giovanni T1 - Resolving the Subsurface Residual Stress Maximum in Laser Powder Bed-Fused 316L Stainless Steel by Diffraction-Based Analysis N2 - Laser powder bed fusion (PBF-LB/M) is a metal additive manufacturing process. Due to the complex nature of the layer-wise, repeated heating and cooling cycles, it tends to generate high-magnitude residual stresses. If not correctly understood and mitigated through in- or post-process approaches, these residual stresses can be detrimental as they are often tensile at the surface. However, determining the magnitude and location of peak tensile residual stresses is not trivial as they are often located subsurface. This work focuses on determining the magnitude and location of these deleterious tensile residual stresses in a PBF-LB/316L specimen. Two diffraction-based Methods are used to reveal the relationship between the residual stresses and the underlying microstructure. On the one hand, high spatial resolution Neutron diffraction is used to determine triaxial stresses from the bulk to a depth of 0.15 mm. On the other hand, laboratory X-ray diffraction coupled with electrolytical layer removal allows the biaxial residual stress depth profile to be probed from the surface to a depth of about 0.6 mm. The results show a good agreement between the two methods. The peak residual stress is shown to be 500 MPa, which appears as a plateau between 0.08 and 0.35 mm in depth. KW - Residual stress KW - Diffraction KW - Laser Powder Bed Fusion KW - 316L KW - Additive manufacturing KW - Microstructure KW - AGIL PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-652138 DO - https://doi.org/10.1007/s11837-025-07719-y SN - 1543-1851 VL - 77 IS - 12 SP - 9726 EP - 9737 PB - Springer Nature AN - OPUS4-65213 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Skrotzki, Birgit T1 - Ermüdungsrisswachstum von warmfestem austenitischem Gusseisen unter isothermen und anisothermen Belastungen N2 - Das Ermüdungsrisswachstumsverhalten des warmfesten Gusseisens EN-GJSA-XNiSiCr35-5-2 (auch unter der Bezeichnung Ni-Resist D-5S bekannt) wurde bei Raum- und hoher Temperatur untersucht. Es wurden kraftgeregelte Versuche bei konstanten Temperaturen (20 °C, 500 °C, 700 °C) ohne und mit Haltezeit und unterschiedlichen Lastverhältnissen durchgeführt. Zusätzlich wurde das Risswachstumsverhalten auch unter TMF-Belastung (Tmin = 400 °C, Tmax = 700 °C) unter IP- und OP-Bedingungen charakterisiert. Die Überwachung des Rissfortschritts erfolgte durch die Kombination von drei verschiedenen Techniken: Potenzialabfall, Thermografie und Compliance-Methode. Die Auswirkungen der verschiedenen Belastungsbedingungen auf das Ermüdungsrisswachstum werden vorgestellt und diskutiert. T2 - Bauteilverhalten bei thermomechanischer Ermüdung CY - Berlin, Germany DA - 25.03.2025 KW - Gusseisen KW - Thermomechanische Ermüdung KW - Rissfortschritt KW - Risswachstum KW - Ermüdungsriss KW - Thermographie PY - 2025 AN - OPUS4-63185 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Singh, Shobhit Pratap A1 - Löwe, Peter A1 - Schriever, Sina A1 - Olbricht, Jürgen A1 - Rehmer, Birgit A1 - Nolze, Gert A1 - Skrotzki, Birgit T1 - High-throughput creep evaluation of IN738LC in bending using digital image correlation at 850 °C N2 - High-temperature alloys, when used in structural applications, undergo slow time-dependent deformation known as creep. Assessing creep behavior is critical for estimating the in-service life of these alloys. Conventionally, uniaxial creep tests are widely conducted at elevated temperatures to determine creep rates. In recent years, bending creep of cantilevers, when combined with digital image correlation (DIC), has emerged as a promising high-throughput technique for rapidly estimating creep life. However, the applicability of bending creep above 700 ◦C for high-temperature alloys using DIC has not been fully established. In this work, we compare uniaxial creep rates of the nickel-based superalloy IN738LC with bending creep rates measured at 850 ◦C using high-temperature DIC. The bending creep data show excellent agreement with uniaxial creep results in the stress range of 240–360 MPa. The measured creep xponent, a critical rate-determining parameter, is found to be ~8 for both uniaxial and bending creep, with the rate data scattered within a factor of two. An in-house experimental setup was developed to perform bending creep tests at high temperatures, with strain monitored through DIC. Our results demonstrate that bending creep, combined with DIC, provides a reliable and efficient method for creep testing of high-temperature alloys. Compared to conventional uniaxial creep experiments, this approach requires significantly less time and material, thereby reducing effort, energy, and cost. We anticipate that this technique will serve as a foundation for testing precious high-temperature materials. For instance, in ongoing rapid discoveries of advanced alloys, in-service creep life can be evaluated much faster with reduced material requirements. Moreover, this method holds strong potential for application to high-entropy alloys and additively manufactured alloys designed for demanding high-temperature environments. KW - Digital image correlation KW - Bending creep KW - Nickel-based superalloys KW - High throughput testing KW - High-temperature materials PY - 2025 UR - https://www.sciencedirect.com/science/article/pii/S0921509325017034?via%3Dihub DO - https://doi.org/10.1016/j.msea.2025.149479 VL - 950 SP - 1 EP - 12 PB - Elsevier B.V. AN - OPUS4-64814 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ávila Calderón, Luis T1 - Creep Behavior of Stainless Steel 316L Manufactured by Laser Powder Bed Fusion N2 - The broader industrial adoption of metal AM in safety-critical applications is limited, among others, by the still in-sufficient understanding of process–structure–property relationships and a lack of reliable mate-rial data. The content presented here approaches this limitation regarding the creep behavior of one of the most studied AM alloys: PBF-LB/M/316L stainless steel. A nearly as-built and a condition heat treated at 900 °C for 1 h, along with a conventionally manufactured variant are investigated. The creep behavior until reaching the minimum creep rate is mainly determined by the solidification cell structure. The damage is overall mainly intergranular, independent of the heat treated condition. The heat treatment at 900 °C for 1 h partially influenced the microstructure (mainly in terms of cell structure). The creep behavior until reaching the minimum creep rate remained nearly unchanged. The creep lifetime and ductility were enhanced. The crystallographic texture evolved after creep deformation. T2 - TMS 2025 Annual Meeting & Exhibition CY - Las Vegas, NV, USA DA - 23.03.2025 KW - AGIL KW - Creep KW - 316L KW - Microstructure PY - 2025 AN - OPUS4-63456 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -