TY - JOUR A1 - Pinomaa, T. A1 - Lindroos, M. A1 - Jreidini, P. A1 - Haapalehto, M. A1 - Ammar, K. A1 - Wang, Lei A1 - Forest, S. A1 - Provatas, N. A1 - Laukkanen, A. T1 - Multiscale analysis of crystalline defect formation in rapid solidification of pure aluminium and aluminium-copper alloys N2 - Rapid solidification leads to unique microstructural features, where a less studied topic is the formation of various crystalline defects, including high dislocation densities, as well as gradients and splitting of the crystalline orientation. As these defects critically affect the material’s mechanical properties and performance features, it is important to understand the defect formation mechanisms, and how they depend on the solidification conditions and alloying. To illuminate the formation mechanisms of the rapid solidification induced crystalline defects, we conduct a multiscale modelling analysis consisting of bond-order potential-based molecular dynamics (MD), phase field crystal-based amplitude expansion simulations, and sequentially coupled phase field–crystal plasticity simulations. The resulting dislocation densities are quantified and compared to past experiments. The atomistic approaches (MD, PFC) can be used to calibrate continuum level crystal plasticity models, and the framework adds mechanistic insights arising from the multiscale analysis. This article is part of the theme issue ‘Transport phenomena in complex systems (part 2)’. KW - Rapid solidification KW - Crystalline defects KW - Molecular dynamics KW - Phase field crystal KW - Phase field method KW - Crystal plasticity PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-542156 DO - https://doi.org/10.1098/rsta.2020.0319 SN - 1364-503X VL - 380 IS - 2217 SP - 1 EP - 20 PB - Royal Society CY - London AN - OPUS4-54215 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eisenbart, M. T1 - KupferDigital – Datenökosystem für die digitale Materialentwicklung auf Basis Ontologie-basierter digitaler Repräsentationen von Kupfer und Kupferlegierungen N2 - Kern des Projektes KupferDigital ist es, einen Demonstrator für ein digitales Datenökosystem zu erstellen, der der Digitalisierung der Materialforschung und der metallverarbeitenden Industrie als zukunftsfähige Plattform zur Verfügung stehen soll. Das Projekt KupferDigital entwickelt Methoden und Konzepte, um den Lebenszyklus am Beispiel von Kupfer – von der Erzgewinnung bis zum Recycling – digital zu erfassen. Grundlage ist die Entwicklung sogenannter Ontologien. Diese können als eine Art Wissensnetz verstanden werden. Sie dienen als gemeinsame Standards für die Beschreibung von Werkstoffen und technischen Vorgängen. Sie helfen bei der digitalen Erfassung von Prozessschritten sowie von Materialeigenschaften. Parallel dazu werden Konzepte für Datenstrukturen, die Speicherung und den Austausch von Werkstoffdaten über neu zu definierende Schnittstellen erarbeitet. Über die Bereitstellung digitalisierter Lebenszyklen von Kupfer wird die Industrie bei der Pro-duktentwicklung befähigt, neue Werkstoffentwicklungen frühzeitig zu bewerten, beispielsweise unter dem Gesichtspunkt der Nachhaltigkeit. Kupfer kommt hier eine aktuelle Bedeutung zu, weil es für die digitale Transformation sowie die Energie- und Mobilitätswende von fundamentaler Bedeutung ist und somit von hohem gesellschaftlichem Wert. Die Projektziele sind sowohl auf weitere metallische Struktur- und Funktionswerkstoffe als auch auf andere Industriebereiche übertragbar. Die Projektergebnisse werden im Rahmen der Aktivitäten der Innovationsplattform MaterialDigital allen Interessierten zur Verfügung gestellt. T2 - MatFo2022 „Vom Material zur Innovation: Digital, Neutral, Vital“ CY - Online meeting DA - 14.11.2022 KW - Kupfer KW - Datenökosystem KW - Materialentwicklung KW - Ontologie PY - 2022 AN - OPUS4-56405 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN ED - Hennecke, M. ED - Skrotzki, Birgit T1 - Hütte Band 2: Grundlagen des Maschinenbaus und ergänzende Fächer für Ingenieure N2 - Die HÜTTE ist ein Kompendium und Nachschlagewerk für unterschiedliche Aufgabenstellungen. Durch Kombination der Einzeldisziplinen dieses Wissenskreises kann das multidisziplinäre Grundwissen für die verschiedenen Technikbereiche und Ingenieuraufgaben zusammengestellt werden. Die HÜTTE enthält in drei Bänden - orientiert am Stand von Wissenschaft und Technik und den Lehrplänen der Technischen Universitäten und Hochschulen - die Grundlagen des Ingenieurwissens. Band 2 enthält die Grundlagen des Maschinenbaus und ergänzende Fächer. KW - Grundlagen des Maschinenbaus PY - 2022 SN - 978-3-662-64371-6 DO - https://doi.org/10.1007/978-3-662-64372-3 SN - 2522-8188 SP - 1 EP - 967 PB - Springer Vieweg CY - Berlin ET - 35 AN - OPUS4-55740 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beygi Nasrabadi, Hossein T1 - Domain-level ontology formulation based on the Platform Material Digital (PMD) ontology: case study Brinell hardness N2 - A large amount of publicly available data is reproduced every day in the field of materials science, while these kind of material data can have different formats and types like paper-type publications, standards, datasheets or isolated datasets in repositories. However, gathering a specific library from such extensive and diverse material data is always challenging for the materials scientists and engineers, since the time-related limitations are not allowed to fully access the large publicly available databases; search across these disparate databases, manage the large volumes of heterogeneous datasets, and integrate data from multiple sources. To address these challenges and make data findable, accessible, interoperable, and reusable (FAIR), an efficient data management system is necessary to build comprehensive, documented, and connected data spaces in the future. A formal standardized knowledge representation through an ontology can address such problems and make data more available and interoperable between related domains. Ontology can also rich machine processable semantic descriptions that increases the performance of scientific searches. In this regard, the Platform MaterialDigital (PMD) is currently working on developing a high-level ontology for the materials and material related processes. For example, in one of the PMD projects of “KupferDigital”, we will try to develop a data ecosystem for digital materials research based on ontology-based digital representations of copper and copper alloys. As a case study, this paper describes the methodology for ontology development of Brinell hardness, based on PMD core ontology. The methodology we describe includes the following steps; gathering the required domain terminology from different resources like standards (DIN EN ISO 6506-1) and test reports, representing the performance of a standard-conformant hardness test and the treatment of the recorded values up to a “reportable” hardness value for a material, designing the process chain according to the semantic technologies, and developing a domain-level ontology of Brinell hardness based on PMD ontology semantic formalization. Apart the mentioned methodology, some interesting tools and methods were introduced and ontology design challenges and possible solutions for modelling materials and processes were discussed. Furthermore, a dataset from the Brinell hardness measurement of cast copper samples is prepared for testing the query process. T2 - MSE 2022 CY - Darmstadt, Germany DA - 27.09.2022 KW - Copper KW - Materials Science KW - Ontology KW - Platform MaterialDigital (PMD) KW - Brinell hardness PY - 2022 AN - OPUS4-56092 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Chen, Yue T1 - Ontopanel: a diagrams.net plugin for graphical semantic modelling N2 - Ontologies that represent a map of the concepts and relationships between them, are becoming an effective solution for data standardization and integration of different resources in the field of materials science, as efficient data storage and management is the building block of material digitization. However, building a domain ontology is not a simple task. It requires not only a collaborative effort between ontologists and domain experts, but also the modeling approaches and tools play a key role in the process. Among all approaches, graphical representation of domain ontologies based on standard conceptual modeling languages is widely used because of its intuitiveness and simplicity. Various tools have been developed to realize this approach in an intuitive way, such as Protégé plugins and web visualization tools. The Materials-open-Lab (MatOLab) project, which aims to develop ontologies and workflows in accordance with testing standards for the materials science and engineering domains, adopted a UML (Unified Modeling Language) approach based on the diagrams.net. It is a powerful, popular, open-source graphical editor. In practical case studies, however, many users’ needs could not be met, such as reusing ontology, conversion, and data mapping. Users must switch between different tools to achieve a certain step, and thereby invariably increase learning cost. The lack of validation also leads to incorrect diagrams and results for users who are not familiar with the ontology rules. To address these issues, we designed Ontopanel, a diagrams.net-based plugin that includes a set of pipeline tools for semantic modeling: importing and displaying protégé-like ontologies, converting diagrams to OWL, validating diagrams by OWL rules, and mapping data. It uses diagrams.net as the front-end for method modeling and Django as the back-end for data processing. As a web-based tool, it is very easy to expand its functionality to meet changing practical needs. T2 - MSE 2022 CY - Darmstadt, Germany DA - 27.09.2022 KW - Ontology KW - Tools KW - Material digital KW - Mat-o-lab KW - Graphic design KW - Ontology development KW - Data mapping KW - FAIR KW - Materials testing PY - 2022 AN - OPUS4-55884 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Han, Ying T1 - The influence of aging and mean stress on fatigue of Al-alloy EN AW-2618A N2 - In this study, the influence of aging and mean stress on fatigue of the aluminium-alloy EN AW-2618A is investigated. Therefore axial fatigue tests are carried out on smooth specimens. The experiments show that the fatigue life decreases with increasing mean stress. Furthermore, the tests with the overaged specimens demonstrate that the number of cycles to failure is decreasing with increasing aging time. T2 - LCF9 CY - Berlin, Germany DA - 21.06.2022 KW - Fatigue KW - Aluminium alloy KW - EN AW-2618A KW - Damage Behavior PY - 2022 AN - OPUS4-55125 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eisenbart, M. T1 - Development of an ontology for the lifecycle of copper and copper alloys N2 - Efforts towards digitalization in the material science and technology community have enhanced in the last years. In 2019 the German digitalization initiative platform „MaterialDigital“1 (MD) has been started. Numerous projects concerning digitalization, including the copper related project „KupferDigital“ (copper digital) have been initiated under the umbrella of MD. The initiative strives to address numerous issues concerning data access, exchange, security, provenance and sovereignty. Heterogeneous data origin, storage and evaluation often result in problems concerning comparability and reproducibility of scientific and technological results. In many cases material data are recorded, but the methods of testing are insufficiently described, or such information is not communicated along with the raw data. The material data can also have numerous different formats such as paper printouts, pdfs, excel sheets or csv-files. Hence, gathering and integrating material data from different sources is challenging for potential users like materials scientists and engineers, especially if there are contradictory data where the reasons for contradictions is not clear due their vague description. In order to address these problems, data should comply to the so called „FAIR“ principle which calls for data to be findable, accessible, interoperable, and reusable (FAIR)2 and hence be accessible via so-called decentralized but interconnected data spaces. By using knowledge representation withontologies, data can be enriched with meaning and the methods of the testing procedures can be accurately provided. In this presentation we want to introduce our approach to such knowledge representation based on a high-throughput alloy development process for Cu-based alloys³ along with characterization techniques such as hardness testing and microstructural characterization (e.g. EBSD – Electron Backscattered Diffraction). T2 - Copper Alloys Conference CY - Dusseldorf, Germany DA - 22.11.2022 KW - Copper KW - Life cycle KW - Ontology PY - 2022 AN - OPUS4-56406 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schilling, Markus T1 - Zugversuchsdaten FAIR integriert: Von der normenkonformen Ontologie bis zu interoperablen Daten im Triple Store N2 - Mit der Digitalisierung von Materialien und Prozessen ist ein Paradigmenwechsel in der Materialentwicklung, -gestaltung und -optimierung verbunden, welcher gleichermaßen vielseitige Möglichkeiten eröffnet und eine große Herausforderung darstellt. Insbesondere sind bei den Digitalisierungsbestrebungen die Qualitätssicherung von Prozessen und Ausgabedaten sowie die Interoperabilität zwischen Anwendungen nach FAIR-Prinzipien (Findability, Accessibility, Interoperability, Reusability) sicherzustellen. Dies umfasst die Speicherung, Verarbeitung und Abfrage von Daten in möglichst standardisierter Form, wobei entsprechend auch Normungs- und Standardisierungsgremien beteiligt werden müssen. Um der Herausforderung gerecht zu werden, Materialdaten für alle Beteiligten konsistent zu kontextualisieren, müssen alle notwendigen Informationen zum Zustand des Materials inklusive produktions- und anwendungsbedingter Veränderungen über eine einheitliche, maschinenlesbare Beschreibung verfügbar gemacht werden. Hierfür sollen Ontologien genutzt werden, da sie maschinenverständliche und -interpretierbare Wissensrepräsentationen durch semantische Konzeptualisierungen ermöglichen, die für das Datenmanagement und die Digitalisierung im Bereich der Materialwissenschaften benötigt werden. Dieses hochaktuelle Thema der Integration und Wiederverwendung von Wissen und Daten aus Herstellung, Bearbeitung und Charakterisierung von Materialien wird in den Projekten Innovationsplattform MaterialDigital (PMD, materialdigital.de) und Materials-open-Lab (Mat-o-Lab, matolab.org) adressiert. Diese beiden unter der Beteiligung der Bundeanstalt für Materialforschung und -prüfung (BAM) durchgeführten Projekte wurden auf der 39. Vortrags- und Diskussionstagung „Werkstoffprüfung“ (2021) grundlegend vorgestellt. In dieser Präsentation sollen die Weiterentwicklungen hinsichtlich der Speicherung von Zugversuchsdaten gemäß einer normenkonformen ontologischen Repräsentation vorgestellt werden. Das umfasst den Weg von der Entwicklung einer Ontologie nach Norm, der Konvertierung von Daten aus Standardtests in das interoperable RDF-Format bis hin zur Verknüpfung von Ontologie und Daten. Letztendlich können die entsprechenden Daten in einem Triple Store abgelegt und abgefragt werden. Die übliche Standardisierung von mechanischen Prüfverfahren im Bereich der Materialwissenschaft und Werkstofftechnik dient als solide Grundlage für die Ontologieentwicklung. Daher wurde der Zugversuch von Metallen bei Raumtemperatur nach DIN EN ISO Norm 6892-1:2019-11 als einer der ersten Anwendungsfälle in den genannten Projekten ausgewählt. Die Betrachtung und Beschreibung des Zugversuchs beinhaltet sowohl dessen ontologische Darstellung als auch eine exemplarische Datengenerierung. Die semantische Verbindung von Ontologie und Daten führt zu Interoperabilität und einer verbesserten Abfragefähigkeit. T2 - Tagung Werkstoffprüfung 2022 CY - Dresden, Germany DA - 27.10.2022 KW - Ontologie KW - Semantisches Web KW - Wissensrepräsentation KW - Digitalisierung KW - Zugversuch PY - 2022 AN - OPUS4-56130 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Shakeel, Y. T1 - NFDI-MatWerk - Reference Datasets N2 - Within NFDI-MatWerk (“National Research Data Infrastructure for Material Sciences”/ “Nationale Forschungsdateninfrastruktur für Materialwissenschaften und Werkstofftechnik“), the Task Area Materials Data Infrastructure (TA-MDI) will provide tools and services to easily store, share, search, and analyze data and metadata. Such a digital materials environment will ensure data integrity, provenance, and authorship. The MatWerk consortium aims to develop specific solutions jointly with Participant Projects (PPs), which are scientific groups or institutes covering different domains, from theory and simulations to experiments. The Data Exploitation Methods group of the Karlsruhe Institute of Technology-Steinbuch Centre of Computing, as part of TA-MDI, is developing specific solutions in close collaboration with three PPs. PP07, together with the University of Stuttgart, aims at the image-based prediction of the material properties of stochastic microstructures using large-scale supercomputers. PP13, in cooperation with the University of Saarland, focuses on tomographic methods at various scales in materials research. PP18, together with the Federal Institute for Materials Research and Testing (“Bundesanstalt für Materialforschung und -prüfung”), aspires to define the criteria for materials reference datasets and usage analytics. The requirements and goals are comparable for each PP: their research outputs, which are scientific datasets, should conform to the FAIR (Findable, Accessible, Interoperable, Reusable) principles. We aim to shape them from a data management perspective making use of the FAIR Digital Object concept, including structured metadata and storage solutions. The results will be a blueprint which will act as a reference for future datasets. Even though the collaboration is in an early stage, the initial steps already show the added value of this approach. This research has been supported by the Federal Ministry of Education and Research (BMBF) – funding code M532701 / the Deutsche Forschungsgemeinschaft (DFG, German Research Foundation) - project number NFDI 38/1, project no. 460247524. T2 - HMC Conference 2022 CY - Online meeting DA - 05.10.2022 KW - NFDI KW - NFDI-MatWerk KW - Reference Data KW - FAIR KW - Creep PY - 2022 AN - OPUS4-56611 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Sonntag, Nadja A1 - Jürgens, M. A1 - Uhlemann, Patrick A1 - Skrotzki, Birgit A1 - Olbricht, Jürgen T1 - Datasets for Service-Like Creep-Fatigue Experiments on Grade P92 Steel N2 - The dataset contains experimental mechanical data from complex service-like creep-fatigue experiments performed isothermally at 620 °C and a low strain amplitude of 0.2 % on tempered martensite-ferritic grade P92 steel. The data sets in text file format provide cyclic deformation (min. and max. stresses) and the total (hysteresis) data of all recorded fatigue cycles for three different creep-fatigue experiments: 1) a standard relaxation fatigue (RF) test with symmetrical dwell times of three minutes introduced at minimum and maximum strain, 2) a fully strain-controlled service-like relaxation (SLR) test combining these three-minute peak strain dwells with a 30-minute dwell in between at zero strain, and 3) a partly stress-controlled service-like creep (SLC) test combining the three-minute peak strain dwells with 30-minute dwells at constant stress. Further information on data and data acquisition, analysis, and experimental details are given in “Experimental Data from Service-Like Creep-Fatigue Experiments on Grade P92 Steel”, submitted to Data in Brief. Additional analyses of these datasets, as well as experimental findings and discussions are presented in “Creep-Fatigue of P92 in Service-Like Tests with Combined Stress- and Strain-Controlled Dwell Times”, submitted to International Journal of Fatigue. KW - Creep-fatigue KW - Stress relaxation KW - Dwell-Fatigue KW - Tempered martensite-ferritic steel PY - 2022 DO - https://doi.org/10.5281/zenodo.7198218 PB - Zenodo CY - Geneva AN - OPUS4-55995 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Fedelich, Bernard ED - Cailletaud, G. ED - Cormier, J. ED - Eggeler, G. ED - Maurel, V. ED - Nazé, L. T1 - Crystal plasticity models: dislocation based N2 - The large number of TEM investigations and the regular microstructure of single-crystal nickel-base superalloys has boosted the development of a number of physically motivated constitutive laws. In contrast to the more phenomenological models discussed in the next chapter, these models use dislocation densities as internal variables. Obvious advantages are that the computed densities can be compared to TEM observations and the Deformation mechanisms can be easier translated into mathematical equations. KW - Nickel-base superalloys KW - Creep KW - Plasticity PY - 2022 SN - 978-0-12-819357-0 SP - 401 EP - 427 PB - Elsevier Inc. ET - 1 AN - OPUS4-53436 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fedelich, Bernard T1 - Experimental and analytical investigation of Low Cycle Fatigue Damage at notches in a polycrystalline Nickel base superalloy N2 - Turbine blades often contain cylindric holes used to generate an air film that protects the blade alloy from the hot gases. These cooling holes of diameter around one mm are drilled by laser through the thickness of the blades. Unfortunately, the resulting stress concentration and the drilling-induced damage are known to favor crack initiation from the holes. It is thus necessary to assess the impact of these cooling holes on the structural integrity of the blades. Since cracks initiate very readily, the fatigue life of the components is mainly controlled by the propagation of the cracks in the stress gradient induced by the holes. For this purpose, displacement controlled high-temperature LCF (Low-Cycle-Fatigue) tests were performed with center hole specimens of a coarse-grained Nickel base Superalloy. The tests were stopped after a defined load drop. In addition, crack propagation tests with Double Edge Notch specimens were performed. Moreover, specimens with different hole surface finishes were investigated, which showed a detrimental effect of the hole surface roughness. In parallel, an evaluation of the LCF tests based on a fracture mechanics-based model (Madia et al., Eng. Fract. Mech., 2018) has been applied. Thereby, the specimen life is controlled by the crack propagation time until failure. Crack growth is controlled by a modified NASGRO equation accounting for large-scale yielding and a progressive build-up of crack closure. The initial crack size has been derived from the measurements of defects around the borehole. A reasonable agreement between predicted and measured lifetimes is observed if one keeps in mind the large uncertainty regarding the effective shape of the cracks. T2 - 23rd European Conference on Fracture CY - Funchal, Madeira, Portugal DA - 27.06.2022 KW - Nickel-base superalloys KW - Notches KW - LCF PY - 2022 AN - OPUS4-55338 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Darvishi Kamachali, Reza A1 - Wang, L. T1 - Elastic energy of multi-component solid solutions and strain origins of phase stability in high-entropy alloys N2 - The elastic energy of mixing for multi-component solid solutions is derived by generalizing Eshelby's sphere-in-hole model. By surveying the dependence of the elastic energy on the chemical composition and lattice misfit, we derive a lattice strain coefficient λ*. Studying several high-entropy alloys and superalloys, we propose that most solid solution multi-component alloys are stable when λ*<0.16, generalizing the Hume-Rothery atomic-size rule for binary alloys. We also reveal that the polydispersity index δ, frequently used for describing strain in multi-component alloys, directly represents the elastic energy e with e=qδ², q being an elastic constant. Furthermore, the effects of (i) the number and (ii) the atomic-size distribution of constituting elements on the phase stability of high-entropy alloys were quantified. The present derivations and discussions open for richer considerations of elastic effects in high-entropy alloys, offering immediate support for quantitative assessments of their thermodynamic properties and studying related strengthening mechanisms. KW - Ordering KW - High-entropy alloys KW - Alloy design KW - Strain energy KW - Phase stability PY - 2022 DO - https://doi.org/10.1016/j.scriptamat.2021.114226 SN - 1359-6462 VL - 206 SP - 1 EP - 6 PB - Elsevier CY - Amsterdam AN - OPUS4-53427 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fedelich, Bernard T1 - Experimental and analytical investigation of high temperature fatigue crack growth at notches in a polycrystalline Nickel base superalloy N2 - The scatter of fatigue crack growth data can become significant for coarse grained materials. By using a probabilistic description of crack propagation as the foundation of a lifetime prediction model, lifetime scatter of laboratory specimens can be reproduced. However, the lifetime of real components is subjected to additional scattering factors such as surface condition or uncertainty regarding direction and shape of emerging cracks. These factors need to be addressed in order to exploit the advantages of probabilistic description, i.e. the reduction of unnecessary conservatisms. High temperature LCF (Low-Cycle-Fatigue) tests were performed with center hole specimens of a coarse-grained Nickel base Superalloy. In addition, crack propagation tests with Double Edge Notch specimens were performed. A procedure to detect the shape of the starting crack that combines the potential drop method and induction thermography was developed. The geometry and the number of notches were varied. Moreover, specimen with different hole surface finishes were investigated, which showed a detrimental effect of the roughness of the hole surface. The results have been compared to predictions of a probabilistic tool for the estimation of lcf lifetime that has been calibrated beforehand on laboratory specimens with and without notches. In parallel, a fracture mechanics-based lifetime model was developed, which includes the initial crack size as a critical parameter. Thereby, the influence of the large grain size (>1mm), and the shape of the starting crack at the notch were considered. Acknowledgements The investigations are conducted as part of the joint research program COOREFLEX-Turbo in the frame of AG Turbo. The work is supported by Siemens AG and the Bundesministerium für Wirtschaft und Technologie (BMWi) as per resolution of the German Federal Parliament under grant number 03ET7071E. T2 - Low Cycle Fatigue 9 CY - Berlin, Germany DA - 21.06.2022 KW - Nickel-base superalloys KW - Notches KW - LCF PY - 2022 AN - OPUS4-55335 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ávila Calderón, Luis T1 - Low cycle fatigue behavior of DED-L Ti-6AL-4V N2 - Laser powder-based directed energy deposition (DED-L) is a technology that offers the possibility for 3D material deposition over hundreds of layers and has thus the potential for application in additive manufacturing (AM). However, to achieve broad industrial application as AM technology, more data and knowledge about the fabricated materials regarding the achieved properties and their relationship to the manufacturing process and the resulting microstructure is still needed. In this work, we present data regarding the low-cycle fatigue (LCF) behavior of Ti-6Al-4V. The material was fabricated using an optimized DED-L process. It features a low defect population and excellent tensile properties. To assess its LCF behavior two conventionally manufactured variants of the same alloy featuring different microstructures were additionally tested. The strain-controlled LCF tests were carried out in fully reversed mode with 0.3 % to 1.0 % axial strain amplitude from room temperature up to 400°C. The LCF behavior and failure mechanisms are described. For characterization, optical microscopy (OM), scanning electron microscopy (SEM), and micro-computed tomography (µCT) were used. The low defect population allows for a better understanding of the intrinsic material’s properties and enables a fairer comparison against the conventional variants. The fatigue lifetimes of the DED-L material are nearly independent of the test temperature. At elevated test temperatures, they are similar or higher than the lifetimes of the conventional counterparts. At room temperature, they are only surpassed by the lifetimes of one of them. The principal failure mechanism involves multiple crack initiation sites. T2 - Ninth International Conference on Low Cycle Fatigue (LCF9) CY - Berlin, Germany DA - 21.06.2022 KW - AGIL KW - Additive Manufacturing KW - Ti-6Al-4V KW - Low-Cycle-Fatigue KW - Microstructure PY - 2022 AN - OPUS4-55123 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bhadeliya, Ashok A1 - Rehmer, Birgit A1 - Fedelich, Bernard A1 - Olbricht, Jürgen A1 - Skrotzki, Birgit A1 - Jokisch, T. ED - Zimmermann, M. T1 - Rissfortschrittsuntersuchungen an gefügten Nickelbasiswerkstoffen bei hoher Temperatur N2 - In nickelbasierten Superlegierungen, die für Gasturbinenschaufeln verwendet werden, sind bei hohen Betriebstemperaturen und -belastungen Kriechschäden, Ermüdung, Korrosion und Oxi-dation zu beobachten. Die betroffenen Turbinenschaufeln müssen ersetzt oder repariert werden, um Effizienzverluste und ein eventuelles Bauteilversagen zu vermeiden. In letzter Zeit wurden additive Fertigungs- und Lötverfahren für die Reparatur und das Fügen von Nickelbasiswerk-stoffen entwickelt, um die Einschränkungen der traditionellen Reparaturverfahren zu überwinden. Für eine auslegungsrelevante Bewertung des Risswachstumsverhaltens in den Fügezonen, die durch diese neuen Technologien erzeugt werden, sind Rissfortschrittsuntersuchungen erfor-derlich. Entsprechende Untersuchungen an gefügten Proben werden in diesem Beitrag vorge-stellt. Die Rissfortschrittsversuche werden an gefügten SEN-Proben (Single Edge Notch) bei einem Spannungsverhältnis von 0,1 und einer Temperatur von 950 °C durchgeführt. Das Riss-wachstum wird mit der DCPD-Methode (Direct Current Potential Drop) überwacht, und die ge-messenen Potenzialsignale werden anhand der optisch vermessenen Risslänge und einer Finite-Elemente-Analyse kalibriert. Der Spannungsintensitätsfaktor (SIF) für die gefügte SEN-Geometrie wird mit Hilfe von Finite-Elemente-Analysen berechnet. Auf diese Weise können Rissfortschrittskurven aus den experimentellen Daten abgeleitet werden. T2 - Tagung „Werkstoffprüfung 2022“ CY - Dresden, Germany DA - 27.10.2022 KW - Lötverbindung KW - Rissfortschritt KW - SEN-Probe KW - Gefügte Nickelbasislegierungen PY - 2022 SN - 978-3-88355-430-3 VL - 2022 SP - 67 EP - 72 AN - OPUS4-57090 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bayerlein, Bernd T1 - Towards Interoperability: Digital Representation of a Material Specific Characterization Method N2 - Certain metallic materials gain better mechanical properties through controlled heat treatments. For example, in age-hardenable aluminum alloys, the strengthening mechanism is based on the controlled formation of nanometer sized precipitates, which represent obstacles to dislocation movement. Precise tuning of the material structure is critical for optimal mechanical behavior in the application. Therefore, analysis of the microstructure and especially the precipitates is essential to determine the ideal parameters for the interplay of material and heat treatment. Transmission electron microscopy (TEM) is utilized to identify precipitate types and orientations in a first step. Dark-field imaging (DF-TEM) is often used to image the precipitates and to quantify their relevant dimensions. The present work aims at the digital representation of this material-specific characterization method. Instead of a time-consuming, manual image analysis, an automatable, digital approach is demonstrated. Based on DF-TEM images of different precipitation states of a wrought aluminum alloy, a modularizable digital workflow for quantitative precipitation analysis is presented. The integration of this workflow into a data pipeline concept will also be discussed. Thus, by using ontologies, the raw image data, their respective contextual information, and the resulting output data from the quantitative precipitation analysis can be linked in a triplestore. Publishing the digital workflow and the ontologies will ensure the reproducibility of the data. In addition, the semantic structure enables data sharing and reuse for other applications and purposes, demonstrating interoperability. The presented work is part of two digitization initiatives, the Platform MaterialDigital (PMD, materialdigital.de) and Materials-open-Laboratory (Mat-o-Lab). T2 - MSE 2022 CY - Darmstadt, Germany DA - 27.09.2022 KW - Interoperability KW - Ontology KW - Precipitation Analysis PY - 2022 AN - OPUS4-55892 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Skrotzki, Birgit T1 - Aging processes in precipitation hardened aluminum alloys N2 - The mechanical strength of wrought high-strength aluminum alloys is essentially based on precipitation hardening, possibly in combination with prior forming, e. g. by stretching. Important parameters for achieving an optimum combination of hardness, strength, ductility, toughness, and further properties such as corrosion resistance are age-hardening temperature and time. During thermal (mechanical) treatment, nucleation and growth of precipitates takes place, leading to the desired degree of hardening. In aluminum alloys, precipitation sequences are usually passed through, i. e. a sequence of metastable precipitates is formed before the stable phase can precipitate. The optimum combination of properties is therefore based on a certain (optimum) microstructure, which can, however, change during the use of a component, since the microstructure is not stable. This happens in particular when the operating temperatures are close to the aging temperature and/or the operating times are sufficiently long. An external mechanical load may accelerate the processes. The presentation gives some examples for this. T2 - Materials Science and Engineering Congress MSE 2022 CY - Darmstadt, Germany DA - 27.9.2022 KW - Aluminium alloy KW - Precipitation hardening KW - Aging KW - Degradation PY - 2022 AN - OPUS4-55877 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Skrotzki, Birgit T1 - Interlinking Structured Data about Aging and Fattigue of an Aluminum Alloy N2 - In typical material oriented research projects numerous types and sources of data need to get connected to form the final outcome. The data-structures have to be described in a manner semantically concise enough so that all participants share the meaning and at the same time flexible enough to allow connecting findings and facts that have not been connected before. The present contribution describes the approach that is being taken in a public funded research project with two cooperating research institutes. The aim of the data-management solution is to describe and interlink three main entity types: material entities like a test specimen that is under observation, immaterial entities like a fatigue life model and processes that generate and transform the immaterial and material entities. The shared understanding of what is described by the data is achieved by referring to existing linked data resources. In addition a common thesaurus that is subject to ongoing discussion is used for concepts and terms that need precision beyond publicly available concept descriptions. The data associated with the entities and processes and entities is rather small and well structured. The entities and processes covered by the vocabularies are typical to laboratories performing fatigue testing and microstructure analysis. Through the interlinking of the entities and processes it becomes possible to intuitively understand the knowledge that is accumulating in the database. For example it is easy to trace the history of a creep test specimen starting from the chemical composition that has been analyzed for the heat, continuing with the heat treatment of the material, going into the creep test itself with the associated creep data and finally finding the transmission electron microscopy images that have been taken from the crept sample. The presented approach is prototypical way to tackle the sustainable management of structured open research data. Open questions remain for example with the management of attributions, the acceptance of an increased effort in data creation and the access control to specific regions of the data. On the other hand the approach sketches what added value can be created, if the community adopts and contributes to the linked data principles. T2 - LCF9 CY - Berlin, Germany DA - 21.6.2022 KW - Data management KW - Data linking KW - Thesaurus PY - 2022 AN - OPUS4-55159 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schilling, Markus A1 - Skrotzki, Birgit T1 - Full dataset of several mechanical tests on an S355 steel sheet as reference data for digital representations N2 - The dataset provided in this repository comprises data obtained from a series of characterization tests performed to a sheet of typical S355 (material number: 1.0577) structural steel (designation of steel according to DIN EN 10025-2:2019). The tests include methods for the determination of mechanical properties such as, e.g., tensile test, Charpy test and sonic resonance test. This dataset is intended to be extended by the inclusion of data obtained from further test methods. Therefore, the entire dataset (concept DOI) comprises several parts (versions), each of which is addressed by a unique version DOI. The data were generated in the frame of the digitization project Innovationplatform MaterialDigital (PMD) which, amongst other activities, aims to store data in a semantically and machine understandable way. Therefore, data structuring and data formats are focused in addition to aspects in the field of material science and engineering (MSE). Hence, this data is supposed to provide reference data as basis for experimental data inclusion, conversion and structuring (data management and processing) that leads to semantical expressivity as well as for MSE experts being generally interested in the material properties and knowledge. KW - S355 steel sheet KW - Mechanical testing KW - Tensile test KW - Charpy test KW - Microstructure analysis KW - Digital representation KW - Data management KW - Data format PY - 2022 DO - https://doi.org/10.5281/zenodo.6778336 PB - Zenodo CY - Geneva AN - OPUS4-55141 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -