TY - JOUR A1 - Kingsbery, P. A1 - Manzoni, Anna Maria A1 - Suárez Ocano, Patricia A1 - Többens, D. M. A1 - Stephan-Scherb, C. T1 - High‐temperature KCl‐induced corrosion of high Cr and Ni alloys investigated by in‐situ diffraction N2 - High‐temperature KCl‐induced corrosion in laboratory air was observed in situ utilizing X‐ray diffraction. High Cr‐containing model alloys (Fe‐13Cr, Fe‐18Cr‐12Ni, and Fe‐25Cr‐20Ni) were coated with KCl and exposed to dry air at 560°C. KCl‐free alloys were studied in the equivalent atmosphere as a reference. After exposure to KCl‐free environments, all alloys showed the formation of very thin oxide layers, indicating good corrosion resistance. In contrast, KCl‐bearing alloys showed distinct damage after exposure. KW - Corrosion KW - In-situ diffraction KW - High-temperature corrosion PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-600831 DO - https://doi.org/10.1002/maco.202314224 SN - 0947-5117 SP - 1 EP - 10 PB - Wiley VHC-Verlag AN - OPUS4-60083 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schilling, Markus T1 - Data-Driven Materials Science: Reproducibility and Standardization N2 - Advancing development and digitalization in materials science requires to focus on quality assurance, interoperability, and compliance with FAIR principles. Semantic technologies offer effective solutions for these challenges by enabling the storage, processing, and contextualization of data in machine-actionable and human-readable formats – essential for robust data management. This presentation highlights the PMD Core Ontology 3.0 (PMDco 3.0), developed specifically for the field of materials science and engineering, and its implementation within generic knowledge representation frameworks. Demonstrators such as standardized mechanical testing, material processing workflows, and the Orowan Demonstrator exemplify the ontology’s practical applications. The use of graph patterns, able to be compiled into rule-based semantic shapes, supports a unified and automated approach to managing heterogeneous experimental data across domains. T2 - Persson Group Seminar CY - Berkeley, CA, USA DA - 23.06.2025 KW - Semantic Data KW - Data Integration KW - Digitalization KW - Data Interoperability KW - PMD Core Ontology KW - Graph Patterns PY - 2025 AN - OPUS4-63484 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schilling, Markus T1 - On Shared Vocabulary, Ontologies, Semantic Data and Prototype Applications N2 - The advancement of development and digitalization in materials science necessitates rigorous quality assurance, interoperability, and adherence to FAIR principles. Semantic technologies contribute to these objectives by facilitating the structured storage, processing, and contextualization of data, yielding machine-actionable and human-interpretable knowledge representations vital for modern data management. This presentation showcases the prototypical application of generic approaches of knowledge representation in materials science. It includes the design and documentation of graph patterns that may be compiled into rule-based semantic shapes. The development and application of the PMD Core Ontology 3.0 (PMDco 3.0) tailored for materials science is highlighted. Its integration into daily lab life is demonstrated through its functional incorporation into electronic lab notebooks (ELN). In this respect, a possible integration of semantic technologies into openBIS is presented. The openBIS system is usable as a central data storage system that may be complimented by semantic annotation of data to enhance data contextualization and automation. Graph-based knowledge representations and rule-based semantic shapes are shown which were developed alongside the PMD Core Ontology 3.0 (PMDco 3.0) and can enrich openBIS functionalities. Practical examples from material processing and mechanical testing illustrate how semantic extensions of openBIS enable machine-actionable, interoperable, and reusable research data, paving the way for a unified, ontology-driven laboratory data ecosystem. T2 - openBIS User Group Meeting (openBIS UGM) CY - Berlin, Germany DA - 22.09.2025 KW - Semantic Data KW - Data Integration KW - Digitalization KW - OpenBIS KW - Ontologies KW - Graph Patterns PY - 2025 AN - OPUS4-64307 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Agudo Jácome, Leonardo T1 - The Al4-xZr5(Ox-y) Trojan horse in the AlMo0.5NbTiTa0.5Zr refractory high entropy superalloy N2 - Unlike conventional alloys, which typically consist of one main element, high-entropy alloys (HEAs) contain five or more principal elements, which broaden chemical complexity and with it a realm of synergistic mechanisms. The AlMo0.5NbTa0.5TiZr HEA initiated a subclass of Al-containing refractory (r)HEAs that has recently drawn attention [2]. The alloy has a superalloy-resembling B2/bcc nanostructure, which inspired its name refractory high entropy superalloy (RSA). With high-temperature (HT) compressive strengths beyond conventional Ni-based superalloys, this nanostructure could be used for improved HT structural applications. However, in the application-relevant HT regime the Al-Zr-rich B2 phase decomposes to form a hexagonal Al-Zr-based intermetallic (Al4-xZr5; x: 0..1) [3,4]. This work explores the fascinating yet fatal micromechanisms associated to this phase transformation, in the context of creep, annealing and oxidation experiments performed between 800 and 1200 °C. The material was produced by arc-melting and heat treatment in argon, which lead to grain boundaries decorated with up to 7%. Interrupted constant-load creep tests were performed under vacuum (at 10-4 Pa), at 900–1100 °C with external tensile stresses of 30–120 MPa. Oxidation experiments were separately conducted for 24 hours at 800 and 1000 °C in both dry (21% O2 + 79% N2) and humid (8% O2 + 74% N2 + 18% H2O) air. After the experiments, the samples were characterized by X-ray diffraction, scanning electron microscopy and transmission electron microscopy to reveal degradation mechanisms. Crystallographic texture, orientation relationships and stabilization of an oxygen-containing iso structure (Al4-xZr5(Ox-y); y: 0..x) of the Al-Zr-rich intermetallic are found and discussed. T2 - BCC Superalloy Network Opening Workshop CY - Reutte, Austria DA - 08.02.2024 KW - High entropy alloy KW - Superalloy KW - Degradation KW - Electron microscopy KW - Microstructure PY - 2024 AN - OPUS4-59833 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Manzoni, Anna Maria T1 - Tuning high entropy alloys towards superalloy applications N2 - The discovery of the high entropy concept at the beginning of the 3rd millennium lead to a worldwide increase in metallurgical research, as the possible element combinations seemed nearly endless and the range of applications wide. In the early years of research, one of the main goals was the discovery of a single-phase high entropy alloy. As research evolved, it was found that properties could be enhanced by opening the HE-concept towards multiphase alloys, and from the wide area of possibilities our group chose a tuning of the properties towards high temperature application. Compositionally complex Al10Co25Cr8Fe15Ni36Ti6 alloy, which is single-phase at high temperature, around 1200°C, shows a three phase morphology at intermediate temperatures, around 800°C. A high temperature homogenization procedure has to be applied in order to decrease the segregation induced by the dendritic growth. Subsequent annealing promotes the formation of the strengthening γ' precipitates. The alloy shows a positive lattice misfit between the γ and the γ' phase, which can be an indicator for good creep properties. The microstructure can be optimized by adding trace elements such as Mo and Hf, known as γ and γ' strengtheners in Ni-based superalloys, respectively. Atom probe measurements show that Mo segregates into the γ matrix, and Hf prefers the γ' precipitates, where it increases the lattice parameter and thus also the lattice misfit, by about 50%. The alloy family shows interesting mechanical properties, especially the Al9.5Co25Cr8Fe15Ni36Ti6Hf0,5 alloy – its tensile properties are better than those of commercial Alloy 800H and IN617 at temperatures up to 700°C. T2 - BAM Abteilungsseminar CY - Online meeting DA - 21.01.2021 KW - High entropy alloys KW - Compositionally complex alloys KW - Superalloys KW - Hochentropie-Legierung KW - Legierung mit komplexer Zusammensetzung KW - Superlegierung PY - 2021 AN - OPUS4-52442 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hébrard, Louis T1 - Comparison of Room and High Temperature Fatigue Behavior of a New LPBF VDM 780 Alloy N2 - The actual environmental challenges require a huge effort from all industrial sectors to reduce their emissions of greenhouse gasses and pollutants. In this context, aeronautics is deeply concerned as one of the most emissive industrial sectors (cf. EU Green Deal). The answer to this pressing challenge is complex and involves new fuels and engine concepts, new aerostructures with higher weight-savings, as well as new, energy-efficient, and sustainable manufacturing technologies and materials. Two technologies may contribute particularly to achieving the goals: (i) new and more energy-efficient processes such as additive manufacturing (AM) can be used for part production; (ii) the engine efficiency of airplanes can be significantly improved to save fuel and reduce gas emissions. The latter can be achieved by increasing the engine thermal efficiency, i.e., increasing the turbine inlet temperature. Currently, only single-crystalline cast materials are available to be used for the thermally highest-loaded parts in the gas turbine engine, i.e., the turbine blades in the high-pressure turbine just behind the combustion chamber. These materials rely on a special casting technology, although they lose these original material performances when additive manufactured. In addition, current materials suitable for metal additive manufacturing have a limited range of temperature application. Therefore, the focus is on the development of new materials targeting higher in-service operation temperatures and durability. Recently, a new Ni-based superalloy (VDM 780) has been developed to ensure microstructural stability up to 800 °C. The goal of this work is to provide a deeper understanding of the high temperature fatigue properties of this alloy. This will enable the identification of the maximum operating temperature of this alloy and assess its performance in order to establish its potential in view of a new generation of more efficient aero-engines. T2 - 11th Edition of Fatigue Design International Conference CY - Senlis, France DA - 19.11.2025 KW - Fatigue KW - Additive Manufacturing KW - Ni-based superalloy KW - High Temperature PY - 2025 AN - OPUS4-64992 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schilling, Markus T1 - Vom Experiment zur semantischen Wissensrepräsentation: Datenstandards und Interoperabilität in der Materialcharakterisierung N2 - Im Zeitalter der digitalen Transformation rückt die strukturierte Erfassung und semantische Verknüpfung von Materialcharakterisierungsdaten immer stärker in den Fokus, um eine effiziente Nutzung über Disziplin- und Projektgrenzen hinweg zu gewährleisten. Dabei bilden etablierte Datenstandards und semantische Technologien sowie Ontologien die Grundlage für eine nach FAIR-Kriterien aufgebaute Dateninfrastruktur, die sowohl maschinenlesbare als auch nachvollziehbare Wissensrepräsentationen ermöglicht. In dieser Präsentation sollen Prinzipien interoperabler Datenarchitekturen erläutert werden, wobei auf die Bedeutung normkonformer Modelle und semantischer Konzeptualisierungen eingegangen wird. Dabei wird der steigende Bedarf an verlässlichen, reproduzierbaren und wiederverwendbaren Daten im Bereich der Materialwissenschaft und Werkstofftechnik adressiert, der insbesondere die Materialcharakterisierung und Werkstoffprüfung vor neue Herausforderungen stellt. Hinsichtlich der angestrebten Möglichkeiten zum erleichterten Datenaustausch kommen einheitlichen Datenformaten und -beschreibungen eine besondere Bedeutung zu. Anhand ausgewählter Publikationen und Demonstratoren wird aufgezeigt, wie Ontologien als verbindende Zwischenschicht unterschiedliche Material- und Verfahrensdomänen konsistent abbilden und zusammenführen können. Ein praktischer Anwendungsfall verdeutlicht die RDF-basierte Repräsentation von Zugversuchsdaten und deren Einbettung in ein Triple-Store-Datenbank-Umfeld. Hierbei fließen Erfahrungen aus der Entwicklung und Anwendung der PMD Core Ontology (PMDco) sowie normenkonformer Ontologien (z.B. Tensile Test Ontology, TTO) ein, welche im Rahmen des Projektes Plattform MaterialDigital (PMD, materialdigital.de) erstellt und betrachtet wurden. Darüber hinaus werden weitere methodische Ansätze und Entwicklungen aus diesem Projekt illustriert. T2 - Tagung Werkstoffprüfung 2025 CY - Dresden, Germany DA - 27.11.2025 KW - Wissensrepräsentation KW - Ontologie KW - Werkstoffprüfung KW - Digitale Transformation KW - Interoperabilität PY - 2025 AN - OPUS4-64944 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Han, Ying T1 - Segmented primary phases of Al-alloy EN AW-2618A in the T61 state using synchrotron computed tomography N2 - The video file contains data from a synchrotron computed tomography measurement of the primary phases of the Al-alloy EN AW-2618A in the T61 state. The volume fraction of the primary phases was determined. KW - Aluminum alloy KW - EN AW-2618A KW - Computed tomography KW - Primary phases PY - 2024 DO - https://doi.org/10.5281/zenodo.12730717 PB - Zenodo CY - Geneva AN - OPUS4-60657 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ulbricht, Alexander T1 - Evolution of Creep Damage of 316L Produced by Laser Powder Bed Fusion N2 - The damage mechanisms of metallic components produced by process laser powder bed fusion differ significantly from those typically observed in conventionally manufactured variants of the same alloy. This is due to the unique microstructures of additively manufactured materials. Herein, the focus is on the study of the evolution of creep damage in stainless steel 316L specimens produced by laser powder bed fusion. X-ray computed tomography is used to unravel the influence of the process-specific microstructure from the influence of the initial void distribution on creep damage mechanisms. The void distribution of two specimens tested at 600 °C and 650 °C is analyzed before a creep test, after an interruption, and after fracture. The results indicate that the formation of damage is not connected to the initial void distribution. Instead, damage accumulation at grain boundaries resulting from intergranular cracking is observed. T2 - Annual International Solid Freeform Fabrication Symposium CY - Austin, TX, USA DA - 14.08.2023 KW - AISI 316L KW - Additive Manufacturing KW - Computed Tomography KW - Creep KW - Laser Powder Bed Fusion KW - Microstructure KW - PBF-LB/M/316L PY - 2023 AN - OPUS4-58285 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ulbricht, Alexander T1 - Formation of Creep Damage of 316L Produced by Laser Powder Bed Fusion N2 - The damage mechanisms of metallic components produced by process laser powder bed fusion differ significantly from those typically observed in conventionally manufactured variants of the same alloy. This is due to the unique microstructures of additively manufactured materials. Herein, the focus is on the study of the evolution of creep damage in stainless steel 316L specimens produced by laser powder bed fusion. X-ray computed tomography is used to unravel the influence of the process-specific microstructure from the influence of the initial void distribution on creep damage mechanisms. The void distribution of two specimens tested at 600 °C and 650 °C is analyzed before a creep test, after an interruption, and after fracture. The results indicate that the formation of damage is not connected to the initial void distribution. Instead, damage accumulation at grain boundaries resulting from intergranular cracking is observed. T2 - 4th Symposium on Materials and Additive Manufacturing - Additive 2024 CY - Berlin, Germany DA - 12.06.2024 KW - AISI 316L KW - Additive Manufacturing KW - Computed Tomography KW - Creep KW - Laser Powder Bed Fusion KW - Microstructure KW - PBF-LB/M/316L PY - 2024 AN - OPUS4-60295 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Jakob T1 - Diffraction and Single-Crystal Elastic Constants of Laser Powder Bed Fused Inconel 718 N2 - Laser powder bed fusion (PBF-LB/M) of metallic alloys is a layer-wise additive manufacturing process that provides significant scope for more efficient designs of components, benefiting performance and weight, leading to efficiency improvements for various sectors of industry. However, to benefit from these design freedoms, knowledge of the high produced induced residual stress and mechanical property anisotropy associated with the unique microstructures is critical. X-ray and neutron diffraction are considered the benchmark for non-destructive characterization of surface and bulk internal residual stress. The latter, characterized by the high penetration power in most engineering alloys, allows for the use of a diffraction angle close to 90° enabling a near cubic sampling volume to be specified. However, the complex microstructures of columnar growth with inherent crystallographic texture typically produced during PBF-LB/M of metallics present significant challenges to the assumptions typically required for time efficient determination of residual stress. These challenges include the selection of an appropriate set of diffraction elastic constants and a representative lattice plane suitable for residual stress analysis. In this contribution, the selection of a suitable lattice plane family for residual stress analysis is explored. Furthermore, the determination of an appropriate set of diffraction and single-crystal elastic constants depending on the underlying microstructure is addressed. In-situ loading experiments have been performed at the Swiss Spallation Neutron Source with the main scope to study the deformation behaviour of laser powder bed fused Inconel 718. Cylindrical tensile bars have been subjected to an increasing mechanical load. At pre-defined steps, neutron diffraction data has been collected. After reaching the yield limit, unloads have been performed to study the accumulation of intergranular strain among various lattice plane families. T2 - 11th European Conference on Residual Stresses CY - Prag, Czech Republic DA - 03.06.2024 KW - Additive Manufacturing KW - Laser Powder Bed fusion KW - Diffraction Elastic Constants KW - Microstructure KW - Electron Backscatter Diffraction PY - 2024 AN - OPUS4-60289 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Jakob T1 - Diffraction and Single-Crystal Elastic Constants of Laser Powder Bed Fused Inconel 718 N2 - In this presentation, the results of the determination of the diffraction and single-crystal elastic constants of laser powder bed fused Inconel 718 are presented. The analysis is based on high-energy synchrotron diffraction experiments performed at the Deutsches Elektronen-Synchrotron. It is shown that the characteristic microstructure of laser powder bed fused Inconel 718 impacts the elastic anisotropy and therefore the diffraction and single-crystal elastic constants. Finally, the consequences on the diffraction-based residual stress determination of laser powder bed fused Inconel 718 are discussed. T2 - AWT-Fachausschuss 13 "Eigenspannungen" CY - Wolfsburg, Germany DA - 19.03.2024 KW - Additive Manufacturing KW - Laser Powder Bed fusion KW - Diffraction KW - In-Situ Testing KW - Diffraction Elastic Constants PY - 2024 AN - OPUS4-59900 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN ED - Hennecke, M. ED - Skrotzki, Birgit T1 - Hütte Band 2: Grundlagen des Maschinenbaus und ergänzende Fächer für Ingenieure N2 - Die HÜTTE ist ein Kompendium und Nachschlagewerk für unterschiedliche Aufgabenstellungen. Durch Kombination der Einzeldisziplinen dieses Wissenskreises kann das multidisziplinäre Grundwissen für die verschiedenen Technikbereiche und Ingenieuraufgaben zusammengestellt werden. Die HÜTTE enthält in drei Bänden - orientiert am Stand von Wissenschaft und Technik und den Lehrplänen der Technischen Universitäten und Hochschulen - die Grundlagen des Ingenieurwissens. Band 2 enthält die Grundlagen des Maschinenbaus und ergänzende Fächer. KW - Grundlagen des Maschinenbaus PY - 2022 SN - 978-3-662-64371-6 DO - https://doi.org/10.1007/978-3-662-64372-3 SN - 2522-8188 SP - 1 EP - 967 PB - Springer Vieweg CY - Berlin ET - 35 AN - OPUS4-55740 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beygi Nasrabadi, Hossein T1 - Domain-level ontology formulation based on the Platform Material Digital (PMD) ontology: case study Brinell hardness N2 - A large amount of publicly available data is reproduced every day in the field of materials science, while these kind of material data can have different formats and types like paper-type publications, standards, datasheets or isolated datasets in repositories. However, gathering a specific library from such extensive and diverse material data is always challenging for the materials scientists and engineers, since the time-related limitations are not allowed to fully access the large publicly available databases; search across these disparate databases, manage the large volumes of heterogeneous datasets, and integrate data from multiple sources. To address these challenges and make data findable, accessible, interoperable, and reusable (FAIR), an efficient data management system is necessary to build comprehensive, documented, and connected data spaces in the future. A formal standardized knowledge representation through an ontology can address such problems and make data more available and interoperable between related domains. Ontology can also rich machine processable semantic descriptions that increases the performance of scientific searches. In this regard, the Platform MaterialDigital (PMD) is currently working on developing a high-level ontology for the materials and material related processes. For example, in one of the PMD projects of “KupferDigital”, we will try to develop a data ecosystem for digital materials research based on ontology-based digital representations of copper and copper alloys. As a case study, this paper describes the methodology for ontology development of Brinell hardness, based on PMD core ontology. The methodology we describe includes the following steps; gathering the required domain terminology from different resources like standards (DIN EN ISO 6506-1) and test reports, representing the performance of a standard-conformant hardness test and the treatment of the recorded values up to a “reportable” hardness value for a material, designing the process chain according to the semantic technologies, and developing a domain-level ontology of Brinell hardness based on PMD ontology semantic formalization. Apart the mentioned methodology, some interesting tools and methods were introduced and ontology design challenges and possible solutions for modelling materials and processes were discussed. Furthermore, a dataset from the Brinell hardness measurement of cast copper samples is prepared for testing the query process. T2 - MSE 2022 CY - Darmstadt, Germany DA - 27.09.2022 KW - Copper KW - Materials Science KW - Ontology KW - Platform MaterialDigital (PMD) KW - Brinell hardness PY - 2022 AN - OPUS4-56092 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Beygi Nasrabadi, Hossein A1 - Skrotzki, Birgit T1 - Ontology-Oriented Modeling of the Vickers Hardness Knowledge Graph N2 - This research deals with the development of the Vickers hardness knowledge graph, mapping the example dataset in them, and exporting the data-mapped knowledge graph as a machine-readable Resource Description Framework (RDF). Modeling the knowledge graph according to the standardized test procedure and using the appropriate upper-level ontologies were taken into consideration to develop the highly standardized, incorporable, and industrial applicable models. Furthermore, the Ontopanel approach was utilized for mapping the real experimental data in the developed knowledge graphs and the resulting RDF files were successfully evaluated through the SPARQL queries. KW - Data Mapping KW - FAIR Data KW - Ontology KW - Knowledge Graph KW - Vickers Hardness PY - 2024 DO - https://doi.org/10.4028/p-k8Gj2L VL - 149 SP - 33 EP - 38 PB - Trans Tech Publications Ltd CY - Switzerland AN - OPUS4-59981 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bayerlein, Bernd T1 - Adapting FAIR Practices in Materials Science: Digital Representation of Material-Specific Characterization Methods N2 - Age-hardenable aluminum alloys undergo precise heat treatments to yield nanometer-sized precipitates that increase their strength and durability by hindering the dislocation mobility. Tensile tests provide mechanical properties, while microstructure evaluation relies on transmission electron microscopy (TEM), specifically the use of dark-field TEM images for precise dimensional analysis of the precipitates. However, this manual process is time consuming, skill dependent, and prone to errors and reproducibility issues. Our primary goal is to digitally represent these processes while adhering to FAIR principles. Ontologies play a critical role in facilitating semantic annotation of (meta)data and form the basis for advanced data management. Publishing raw data, digital workflows, and ontologies ensures reproducibility. This work introduces innovative solutions to traditional bottlenecks and offers new perspectives on digitalization challenges in materials science. We support advanced data management by leveraging knowledge graphs and foster collaborative and open data ecosystems that potentially revolutionize materials research and discovery. T2 - TMS - Specialty Congress 2024 CY - Cleveland, Ohio, US DA - 16.06.2024 KW - FAIR KW - Research Data Management KW - Semantic Interoperability KW - Ontologies KW - Materials and Processes Data Reusability PY - 2024 AN - OPUS4-60375 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Skrotzki, Birgit T1 - Fatigue Crack Growth of Heat Resistant Austenitic Cast Iron under Isothermal and Anisothermal Conditions N2 - The heat-resistant cast iron EN-GJSA-XNiSiCr35-5-2 (Ni-Resist D-5S) was investigated for its fatigue crack growth behavior at room and high temperatures. Force-controlled tests were carried out at constant temperatures (20 °C, 500 °C, 700 °C) without and with hold time and different load ratios. The crack growth behavior was also characterized under TMF loading (Tmin = 400 °C, Tmax = 700 °C) by applying IP and OP conditions and different load ratios. Three different techniques were combined to monitor crack growth: potential drop, thermography, and compliance method. The effect of the different loading conditions on the fatigue crack growth behavior will be presented and discussed. T2 - TMF Workshop 2024 CY - Berlin, Germany DA - 25.04.2024 KW - Fatigue crack growth KW - Thermomechanical fatigue KW - Austenitic cast iron KW - Ni-Resist PY - 2024 AN - OPUS4-59964 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bhadeliya, Ashok T1 - High temperature fatigue crack growth in nickel-based alloys joined by brazing and additive manufacturing N2 - Gas turbine components, made of nickel-based alloys, undergo material damage due to high temperatures and mechanical stresses. These components need periodic replacement to avoid efficiency loss and failure. Repair of these parts is more cost-effective than replacement. State-of-the-art repair technologies, including different additive manufacturing (AM) and brazing processes, are considered for efficient restoration. Materials properties mismatches and/or internal defects in repaired parts may expedite crack initiation and propagation, reducing fatigue life. To understand the crack growth behavior in joining zones and predict the remaining life of repaired components, fatigue crack growth (FCG) tests were conducted on specimens of nickel-based alloys joined via brazing, pre-sintered preforms and AM. The FCG experimental technique was successfully adapted for joined specimens and results indicate that the investigated braze material provides a lower resistance to crack growth. In AM-sandwich specimens, the crack growth rates are significantly reduced at the interface of AM and cast material. T2 - TMS 2024 Annual Meeting & Exhibition CY - Orlando, Florida, USA DA - 03.03.2024 KW - Fatigue crack growth KW - Joined nickel-based alloys PY - 2024 AN - OPUS4-59854 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bhadeliya, Ashok T1 - High temperature fatigue crack growth in nickel-based alloys joined by brazing and additive manufacturing N2 - Nickel-based alloys have been widely used for gas turbine blades owing to their excellent mechanical properties and corrosion resistance at high temperatures. The operating temperatures of modern gas turbines have been increased in pursuit of increased thermal efficiency. Turbine blades are exposed to these high temperatures combined with mechanical stresses, resulting in material damage through creep, fatigue, and other mechanisms. These turbine blades must be regularly inspected and replaced as needed, to prevent the loss of efficiency, breakdown, and catastrophic failure. Repair of the damaged turbine blades is often a more practical and cost-effective option than replacement, as replacement is associated with high costs and loss of material resources. To this end, state-of-the-art repair technologies including different additive manufacturing and brazing processes are considered to ensure efficient repair and optimum properties of repaired components. In any repaired part, materials property-mismatches and/or inner defects may facilitate the crack initiation and propagation and thus reduce the number of load cycles to failure. Therefore, a fundamental understanding of the fatigue crack growth and fracture mechanisms in joining zones is required to enable the prediction of the remaining life of repaired components and to further improve and adapt the repair technologies. Fatigue crack growth experiments have been conducted on SEN (Single Edge Notch) specimens joined via brazing, and pre-sintered Preform (PSP) and multi-materials (casted/printed) specimens layered via additive manufacturing (AM). The experiments were performed at 950 °C and various stress ratios. The crack growth was measured using DCPD (Direct Current Potential Drop) method. The stress intensity factors for joined SEN specimens were calculated using the finite element method and then used to derive the fatigue crack growth curves. Metallographic and fractographic analyses were conducted to get insight into the fracture mechanism. Results show that the experimental technique for fatigue crack growth was successfully adapted and applied for testing joined specimens. Furthermore, the initial tests indicate that the investigated braze filler material provides a lower resistance to crack growth, and bonding defects cause a crack to deviate to the interface of the base material and joining zone. In AM-sandwich specimens, the crack growth rates are significantly reduced when the crack reaches the interface of printed material and casted material. The obtained crack growth data can be used to calibrate a crack growth model, which will further be utilized to predict the remaining life of repaired components. T2 - Fatigue 2024 Conference CY - Cambridge, UK DA - 19.06.2024 KW - Fatigue crack growth KW - Joined nickel-based alloys PY - 2024 AN - OPUS4-60893 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ávila Calderón, Luis T1 - Creep Behavior of Stainless Steel 316L Manufactured by Laser Powder Bed Fusion N2 - Metal additive manufacturing (Metal AM) continues to gain momentum. Many companies explore the manufacturing of innovative products, including components for safety critical applications. Despite the intensive research of recent years, a fundamental understanding of the process‑structure‑property relationships remains challenging due to, i.a., the inherently complex and highly hierarchical microstructures arising from the wide range of build process parameter variability. This contribution presents the resu lts of an experimental study on the creep behavior of an austenitic 316L stainless steel produced by laser powder bed fusion (PBF LB/M/316L) with an emphasis on understanding the effects of microstructure on creep mechanisms. Hot tensile tests and constant force creep tests at 600 °C and 650 °C, X ray computed tomography, as well as optical and electron microscopy were performed. The produced PBF LB/M/316L exhibits a low void population 0.01 %) resulting from the manufacturing parameters used and which a llowed us to understand the effects of other microstructural aspects on creep behavior, e.g., grain morphology and dislocation substructure. A hot‑rolled variant of 316L hwas also tested as a reference. The produced PBF LB/M/316L possesses shorter primary and secondary creep stages and times to rupture and smaller creep stress exponents than the hot‑rolled variant. Overall, the creep damage is more extensive in the PBF LB/M/316L and is characterized as predominantly intergranular. It is considered that the damage behavior is mainly impacted by the formation of precipitates at the grain boundaries combined with their unfavorable orientation. The dislocation substructure and local elemental segregation appear to have a decisive impact on the overall creep behavior. T2 - 16th International Conference on Creep and Fracture of Engineering Materials and Structures CY - Bangalore, India DA - 28.07.2024 KW - AGIL KW - 316L KW - Additive Manufacturing KW - Creep KW - Microstructure evolution PY - 2024 AN - OPUS4-60839 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schilling, Markus T1 - Towards Structured Data Spaces: Prototypical Application of Semantic Technologies as a Driver for Innovation in Materials Science N2 - In the pursuit of advancing development and digitalization within materials science, ensuring quality assurance, interoperability, and adherence to FAIR principles is significant. To address these aspects, semantic technologies are employed for storage, processing, and contextualization of data, offering machine-actionable and human-readable knowledge representations crucial for data management. This presentation showcases the prototypical application of generic approaches of knowledge representation in materials science. It includes the design and documentation of graph patterns that may be compiled into rule-based semantic shapes. The development and application of the PMD Core Ontology 3.0 (PMDco 3.0) tailored for materials science is highlighted. Its integration into daily lab life is demonstrated through its functional incorporation into electronic lab notebooks (ELN). Examples of material processing and standardized mechanical testing illustrate how knowledge graph operations enhance ELN capabilities, providing a generalizable unified approach for managing diverse experimental data from different sources with automation potentials. T2 - TMS Specialty Congress 2025 CY - Anaheim, CA, USA DA - 15.06.2025 KW - Semantic Data KW - Data Integration KW - Digitalization KW - Data Interoperability KW - Plattform MaterialDigital PY - 2025 AN - OPUS4-63401 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ávila Calderón, Luis Alexander A1 - Matzak, Kathrin A1 - Olbricht, Jürgen A1 - Dolabella Portella, Pedro A1 - Skrotzki, Birgit T1 - BAM Reference Data: High Temperature Tensile Data of Single-Crystal Ni-Based Superalloy CMSX-6 N2 - This publication provides comprehensive metadata and test results of tensile tests at elevated temperature according to DIN EN ISO 6892-2:2018-09 on the single crystal Ni-based superalloy CMSX-6 at T = 980 °C. The tests were performed in an ISO 17025-accredited test laboratory. The calibrations of measuring equipment are documented, meet the requirements of the measurement standard, and are metrologically traceable. The provided data were audited and are BAM reference data. KW - Digitalisierung KW - Referenzdaten KW - CMSX-6 KW - Zugversuch KW - NFDI-MatWerk KW - Ni-Basis-Superlegierung PY - 2025 DO - https://doi.org/10.5281/zenodo.17846616 PB - Zenodo CY - Geneva AN - OPUS4-65338 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Camin, B. T1 - Grenzflächenanalyse diffusionsgeschweißter Werkstoffpaarungen Nickel/ Nickelbasis-Superlegierung CMSX-4 N2 - Der Kirkendall-Effekt tritt bei aneinandergrenzenden Metallpaarungen auf, die höheren Temperaturen ausgesetzt sind. Es findet als Funktion von der Temperatur, der Zeit und der Konzentration die Diffusion von Atomen und Leerstellen über die Phasengrenze hinweg statt. Für die Untersuchung des Kirkendall-Effekts wurde mittels Diffusionsschweißens eine Werkstoffpaarung bestehend aus reinem Nickel (Ni) und der Nickelbasis-Superlegierung CMSX-4 hergestellt. Das Gefüge des reinen Nickels ist polykristallin und von CMSX-4 einkristallin. Da der Kirkendall-Effekt neben den oben genannten Parametern zudem von der Kristallorientierung abhängig ist, wurden zwei verschiedene Kristallorientierungen, die [111]- und [001]-Richtungen, gewählt. Aus 3D µ-tomografischen Untersuchungen ist bekannt, dass heiß-isostatisches Pressen (HIP) eine Verringerung der Porosität in CMSX-4 bewirkt, die durch die Erstarrung des Einkristalls bei der Herstellung entsteht [1]. Daher wurden bei den Diffusionsschweißungen Werkstoffpaarungen von reinem Nickel mit drei CMSX-4-Varianten -mit einer γ/γ‘-Mikrostrukturkombiniert: Ni/ CMSX-4 [111], Ni/ CMSX-4 [001] und Ni/ CMSX-4 [001]-HIPed. Die bei der Diffusionsschweißung entstehenden Grenzschichten wurden mittels Stereo-, Licht- und Rasterelektronenmikroskopie sowie EDX-Analysen untersucht. Bei allen Diffusionsschweißungen entstand eine feste Verbindung zwischen den Werkstoffpaarungen. Wie bereits aus [2] bekannt, bildet sich bei allen Proben auf der Rein-Nickelseite der Grenzfläche ein Porensaum aus, während sich auf der CMSX-4-Seite ein γ‘-freie Zone bildet (Abbildung 1). Sowohl die jeweilige Porosität als auch Porengröße des Porensaums der drei Werkstoffpaarungen ist verschieden. Dieses gilt ebenso für die durchschnittliche Schichtdicke der γ‘-freie Zone. Die geringste durchschnittliche Schichtdicke mit 1,45 µm weist die Paarung Ni/ CMSX-4 [001]-HIPed (Abbildung 1b) auf, wobei die Dicke über den Probenquerschnitt konstant ist. Dagegen schwanken die Schichtdicken der γ‘-freie Zonen bei Ni/ CMSX� 4 [111] (Abbildung 1c) zwischen 1,82 – 4,1 µm und Ni/ CMSX-4 [001] (Abbildung 1a) zwischen 1,36 - 4,55 µm. EDX-Messungen (Linescans) von der CMSX-4-Seite über die γ‘-freie Zone bis in den Nickelwerkstoff zeigen den qualitativen Verlauf der Elementkonzentrationen von Nickel und Aluminium (Abbildung 2). Bei allen Werkstoffpaarungen nimmt die Konzentration des Elements Nickel kontinuierlich zu. Während in der Werkstoffpaarung Ni/CMSX-4 [111] der Konzentrationszunahme symmetrisch über die Grenzfläche verläuft, weist Nickel bei den Werkstoffpaarungen Ni/CMSX-4 mit [001]-Orientierung keinen symmetrischer Konzentrationsverlauf auf. Daraus lässt sich schließen, dass hier die Diffusion von Nickel über die Grenzfläche in die γ‘-freie Zone in Abhängigkeit von der Kristallorientierung unterschiedlich stattfindet. Entgegengesetzt diffundiert das Element Aluminium von der CMSX-4-Seite zur Nickelseite, wie sich aus dem ebenfalls unsymmetrischen Elementverlauf schließen lässt. Bemerkenswert ist hier ein Knick, der sich nach einem Steilabfall einem Plateau anschließt, wie im vergrößerten Ausschnitt in Abbildung 2 mit einem roten Pfeil markiert ist. Dieser Verlauf ist von der Kristallorientierung unabhängig und ist auf die bessere Diffusivität von Al im Vergleich zu Ni zurückzuführen. T2 - Materialographie 2024 CY - Berlin, Germany DA - 18.09.2024 KW - Diffusionsschweißen KW - Grenzfläche KW - Nickelbasis-Superlegierung KW - Kirkendall-Effekt PY - 2024 AN - OPUS4-61095 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schilling, Markus T1 - Ansätze zur digitalen Wissensrepräsentation aus der Plattform MaterialDigital (PMD) N2 - Die Digitalisierung von Materialien und Prozessen stellt eine große Herausforderung dar, die nur durch eine Bündelung der Bemühungen aller Beteiligten in diesem Bereich erreicht werden kann. Bei einer derartigen digitalen Beschreibung spielen Datenanalysemethoden, eine Qualitätssicherung von Prozessen inklusive Input- und Output-Daten sowie die Interoperabilität zwischen Anwendungen nach den FAIR-Prinzipien eine wichtige Rolle. Dies umfasst das Speichern, Verarbeiten und Abfragen von Daten in einer vorzugsweise standardisierten Form (Beteiligung von Normungsgremien). Zur Bewältigung dieser Herausforderung ist eine mit allen Stakeholdern konsistente Kontextualisierung der Materialdaten anzustreben, d.h. alle erforderlichen Informationen über den Zustand des Materials einschließlich produktions- und anwendungsbezogener Änderungen müssen über eine einheitliche, maschinenlesbare Beschreibung verfügbar gemacht werden. Dazu werden Wissensrepräsentationen und Konzeptualisierungen ermöglichende Ontologien verwendet. Eine zentrale Betrachtungsweise in diesem Zusammenhang ist die Realisierung von (automatisierten) Datenpipelines, die eine Beschreibung und Verfolgung von Daten ausgehend von ihrer Erzeugung, bspw. in einem Messgerät, bis zu ihrer globalen Verwendung in möglicherweise verschiedenen Kontexten beinhalten. Erste Bemühungen und Ansätze zu diesen Problemstellungen führten im Projekt Innovations-Plattform Material Digital (PMD, materialdigital.de) zur Erstellung von Anwendungsontologien, die Prozesse und Testmethoden explizit beschreiben. Dabei wurde u.a. der Zugversuch an Metallen bei Raumtemperatur nach ISO 6892-1 ontologisch beschrieben. Diese als Beispiel dienende Ontologieentwicklung wird in dieser Präsentation vorgestellt. Weiterhin wurde, ausgehend von der domänenspezifischen Entwicklung von Anwendungsontologien, eine Kernontologie erstellt, die eine übergeordnete Verbindung von ontologischen Konzepten aufgrund der Verwendung gleichen Vokabulars und semantischer Verknüpfungen erlaubt. Diese sowie die das PMD-Projekt selbst werden ebenfalls in dieser Präsentation vorgestellt. T2 - DVM Workshop: Grundlagen und Beispiele zur Digitalisierung für die Materialforschung und -prüfung CY - Online meeting DA - 19.10.2021 KW - Plattform Material Digital (PMD) KW - Ontologie KW - Zugversuch KW - Wissensrepräsentation KW - Semantic Web PY - 2021 AN - OPUS4-53565 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schilling, Markus T1 - Towards digitalization of materials in PMD: An application ontology of the tensile test N2 - Due to the diversity of materials and the processes associated with their production and use, the complexity of the lifecycles of materials and the multitude of academic and industrial researchers participating in generation of data for material design impose a huge challenge. The topical goal of digitalizing materials and processes can only be adequately addressed by consolidating the efforts of all stakeholders in this field. There are many scattered activities, but there is a demand for an elimination of redundancies as well as an advance in acceptance and a common basis in the digitalization of materials. Furthermore, data analysis methods play an important role in both, the experimental and simulation-based digital description of materials, but they have been poorly structured so far. Therefore, the two joint projects Platform Material Digital (PMD, materialdigital.de) and Materials open Laboratory (Mat-o-Lab, matolab.de) aim to contribute to a standardized description of data processing methods in materials research. Besides stimulating the formation of a collaborative community in this respect, their main technical goals are the quality assurance of the processes and the output data, the acquisition and definition of their accuracy as well as the interoperability between applications. In this regard, data management in accordance with the FAIR (findability, accessibility, interoperability, reuseability) principles is addressed. There is a common agreement in the scientific community following current discussions that data is supposed to be conform to these principles. This includes storage, processing and querying of data in a preferably standardized form. To meet the challenge to contextualize material data in a way that is consistent with all stakeholders, all necessary information on the condition of the material including production and application-related changes have to be made available via a uniform, machine-readable description. For this purpose, ontologies are to be used since they allow for machine-understandable knowledge representations and conceptualizations that are needed for data management and the digitalization in the field of materials science. As first efforts in PMD and Mat-o-Lab, application ontologies are created to explicitly describe processes and test methods. Thereby, the well-known tensile test of metals at room temperature was described ontologically in accordance with the respective ISO standard 6892-1:2019-11. The efforts in creating this tensile test application ontology are shown in this presentation. Especially, the path of ontology development based on standards to be pursued is focused, which is in accordance with the generic recommendations for ontology development and which is supposed to be exemplary for the creation of other application ontologies. T2 - VirtMet: 1st International Workshop on Metrology for Virtual Measuring Instruments and Digital Twins CY - Online meeting DA - 21.09.2021 KW - Platform Material Digital (PMD) KW - Ontology KW - Tensile test KW - Standard KW - Ontology development PY - 2021 AN - OPUS4-53481 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Chen, Yue T1 - Ontopanel: a diagrams.net plugin for graphical semantic modelling N2 - Ontologies that represent a map of the concepts and relationships between them, are becoming an effective solution for data standardization and integration of different resources in the field of materials science, as efficient data storage and management is the building block of material digitization. However, building a domain ontology is not a simple task. It requires not only a collaborative effort between ontologists and domain experts, but also the modeling approaches and tools play a key role in the process. Among all approaches, graphical representation of domain ontologies based on standard conceptual modeling languages is widely used because of its intuitiveness and simplicity. Various tools have been developed to realize this approach in an intuitive way, such as Protégé plugins and web visualization tools. The Materials-open-Lab (MatOLab) project, which aims to develop ontologies and workflows in accordance with testing standards for the materials science and engineering domains, adopted a UML (Unified Modeling Language) approach based on the diagrams.net. It is a powerful, popular, open-source graphical editor. In practical case studies, however, many users’ needs could not be met, such as reusing ontology, conversion, and data mapping. Users must switch between different tools to achieve a certain step, and thereby invariably increase learning cost. The lack of validation also leads to incorrect diagrams and results for users who are not familiar with the ontology rules. To address these issues, we designed Ontopanel, a diagrams.net-based plugin that includes a set of pipeline tools for semantic modeling: importing and displaying protégé-like ontologies, converting diagrams to OWL, validating diagrams by OWL rules, and mapping data. It uses diagrams.net as the front-end for method modeling and Django as the back-end for data processing. As a web-based tool, it is very easy to expand its functionality to meet changing practical needs. T2 - MSE 2022 CY - Darmstadt, Germany DA - 27.09.2022 KW - Ontology KW - Tools KW - Material digital KW - Mat-o-lab KW - Graphic design KW - Ontology development KW - Data mapping KW - FAIR KW - Materials testing PY - 2022 AN - OPUS4-55884 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Han, Ying T1 - The influence of aging and mean stress on fatigue of Al-alloy EN AW-2618A N2 - In this study, the influence of aging and mean stress on fatigue of the aluminium-alloy EN AW-2618A is investigated. Therefore axial fatigue tests are carried out on smooth specimens. The experiments show that the fatigue life decreases with increasing mean stress. Furthermore, the tests with the overaged specimens demonstrate that the number of cycles to failure is decreasing with increasing aging time. T2 - LCF9 CY - Berlin, Germany DA - 21.06.2022 KW - Fatigue KW - Aluminium alloy KW - EN AW-2618A KW - Damage Behavior PY - 2022 AN - OPUS4-55125 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Zapala, P. A1 - Abel, Andreas A1 - Michels, H. A1 - Skrotzki, Birgit T1 - Werkstoffanwendungen für Eisenaluminide (FeAl), (WAFEAL) N2 - Die zunehmende geopolitische Bedeutung der Ressourcenverfügbarkeit sowie die Anforderungen an einen geschlossenen Materialkreislauf treiben die Materialforschung voran, um konventionelle Werkstoffe mit weniger kritischen Zusätzen zu legieren oder sogar vollständig mit nachhaltigeren Alternativen zu substituieren. Eine potenzielle Alternative stellen die intermetallischen Eisenaluminid-Legierungen (FeAl) dar. Im Labormaßstab wurden bereits viele Legierungskonzepte für verbesserte Hochtempera- tureigenschaften oder Duktilität erfolgreich gießtechnisch umgesetzt. Eine erfolgreiche Erprobung von FeAl-Legierungen im industriellen Maßstab stand zu Beginn des Projekts aber weiterhin aus. Ziel des Vorhabens war daher die Entwicklung von simulationsgestützten Gießkonzepten in industrienahe Gießprozesse anhand der Modelllegierung Fe-26Al-4Mo-0,5Ti-1B und die Eingrenzung der prozesstechnischen Verfahrensgrenzen durch Warmrissversuche. Erkenntnisse hieraus wurden in einen praxisorientierten, für zukünftige Anwender in KMUs zugänglichen Handlungskatalog für die gießgerechte Auslegung von Bauteilen aus Eisenaluminiden überführt. Fokus wurde insbesondere auf das Feinguss- und Kokillengussverfahren im Schleuderguss gesetzt. Neben zahlreicher Konstruktions- und Gießprozessparameter wurden auch Wärmebehandlungen und Legierungszusätze (Al, Mo, B) variiert, um den Einfluss von Legierungselementen auf Gießbarkeit, Mikrostruktur und mechanische Kennwerte zu be- stimmen. Eine umfangreiche Basis an Daten aus Mikrostrukturanalysen (Mikroskopische Bildgebung, Bestimmung von Korngrößen sowie Phasenzusammensetzungen und -anteilen, Fraktographie), mechanischen Tests (Härtemessungen, Druckversuch, Zugversuch, Warmzugversuch, Kriechversuch) sowie Messungen thermophysikalischer Eigenschaften konnte für die Modelllegierung erzeugt werden. Korrelationen dieser Informationen mit Prozessvariablen erlaubten Schlussfolgerungen zu Härtungsmechanismen und Duktilität in der Legierung und wie sie prozesstechnisch in Gieß- und Bauteilauslegung gesteuert werden können. Der erfolgreiche Abguss von hochkomplexen Bauteilgeometrien mit dünnen Wandstärken sowie optimierte Legierungszusammensetzungen zeigen Perspektiven auf neue Anwendungsfelder auf. Das Ziel des Forschungsvorhabens ist erreicht worden. KW - Simulationsgestützte Gießkonzepte KW - Intermetallische FeAl-Legierungen PY - 2023 IS - 1322 SP - 1 EP - 168 PB - Forschungsvereinigung Verbrennungskraftmaschinen (FVV) CY - Frankfurt am Main AN - OPUS4-56932 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Abel, Andreas A1 - Zapala, P. A1 - Michels, H. A1 - Skrotzki, Birgit T1 - Materials applications of iron aluminide (FeAl), (WAFEAL) T1 - Werkstoffanwendungen für Eisenaluminide (FeAl), (WAFEAL) N2 - The increasing importance of resource availability and closed-loop material cycles are driving materials research to reduce alloying content in conventional materials or even substitute them with more sustainable alternatives. Intermetallic iron aluminide alloys (FeAl) present a potential alternative. Many alloy concepts for improved high-temperature properties or ductility have already been successfully implemented in casting technologies on a laboratory scale. However, successful testing of FeAl alloys on an industrial scale was still pending at the beginning of the project. Therefore, the aim of the project was to develop simulation based casting concepts for industrial casting processes using the base alloy Fe-26Al-4Mo-0.5Ti-1B and to narrow down process limits by means of hot cracking tests. Findings were transferred into practice-oriented guidelines for casting of iron aluminides, which is accessible to future applicants in SMEs. The focus was placed on centrifugal casting combined with investment casting or die casting. In addition to numerous design and casting process parameters, heat treatments and alloying additions (Al, Mo, B) were varied to determine the influence of alloying elements on castability, microstructure and mechanical properties. Data from microstructure analyses (microscopic imaging, determination of grain sizes as well as phase compositions and volume fractions, fractography), mechanical tests (hardness measurements, compression tests, ambient and high-temperature tensile tests, creep tests) as well as measurements of thermophysical properties could be generated on the base alloy. Correlations of materials data with process variables allowed conclusions to be drawn on strengthening mechanisms and ductility of the alloy and how they can be controlled in terms of processing and component design. Successful casting of highly complex components with thin wall thicknesses and optimised alloy compositions points out prospects for new fields of application. N2 - Die zunehmende geopolitische Bedeutung der Ressourcenverfügbarkeit sowie die Anforderungen an einen geschlossenen Materialkreislauf treiben die Materialforschung voran, um konventionelle Werkstoffe mit weniger kritischen Zusätzen zu legieren oder sogar vollständig mit nachhaltigeren Alternativen zu substituieren. Eine potenzielle Alternative stellen die intermetallischen Eisenaluminid-Legierungen (FeAl) dar. Im Labormaßstab wurden bereits viele Legierungskonzepte für verbesserte Hochtemperatureigenschaften oder Duktilität erfolgreich gießtechnisch umgesetzt. Eine erfolgreiche Erprobung von FeAl-Legierungen im industriellen Maßstab stand zu Beginn des Projekts aber weiterhin aus. Ziel des Vorhabens war daher die Entwicklung von simulationsgestützten Gießkonzepten in industrienahe Gießprozesse anhand der Modelllegierung Fe-26Al-4Mo-0,5Ti-1B und die Eingrenzung der prozesstechnischen Verfahrensgrenzen durch Warmrissversuche. Erkenntnisse hieraus wurden in einen praxisorientierten, für zukünftige Anwender in KMUs zugänglichen Handlungskatalog für die gießgerechte Auslegung von Bauteilen aus Eisenaluminiden überführt. Fokus wurde insbesondere auf das Feinguss- und Kokillengussverfahren im Schleuderguss gesetzt. Neben zahlreicher Konstruktions- und Gießprozessparameter wurden auch Wärmebehandlungen und Legierungszusätze (Al, Mo, B) variiert, um den Einfluss von Legierungselementen auf Gießbarkeit, Mikrostruktur und mechanische Kennwerte zu bestimmen. Eine umfangreiche Basis an Daten aus Mikrostrukturanalysen (Mikroskopische Bildgebung, Bestimmung von Korngrößen sowie Phasenzusammensetzungen und -anteilen, Fraktographie), mechanischen Tests (Härtemessungen, Druckversuch, Zugversuch, Warmzugversuch, Kriechversuch) sowie Messungen thermophysikalischer Eigenschaften konnte für die Modelllegierung erzeugt werden. Korrelationen dieser Informationen mit Prozessvariablen erlaubten Schlussfolgerungen zu Härtungsmechanismen und Duktilität in der Legierung und wie sie prozesstechnisch in Gieß- und Bauteilauslegung gesteuert werden können. Der erfolgreiche Abguss von hochkomplexen Bauteilgeometrien mit dünnen Wandstärken sowie optimierte Legierungszusammensetzungen zeigen Perspektiven auf neue Anwendungsfelder auf. T2 - FVV Transfer + Netzwerktreffen | Informationstagung – Frühjahr 2023 CY - Würzburg, Germany DA - 29.03.2023 KW - Fe-Al alloys KW - Intermetallics KW - Iron aluminides KW - Microstructure-property-correlation KW - High temperature mechanical properties KW - Creep data KW - Tensile data KW - Fractography KW - Casting PY - 2023 VL - R604 SP - 1 EP - 32 PB - FVV e. V. CY - Frankfurt a.M. AN - OPUS4-57247 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eisenbart, M. T1 - Development of an ontology for the lifecycle of copper and copper alloys N2 - Efforts towards digitalization in the material science and technology community have enhanced in the last years. In 2019 the German digitalization initiative platform „MaterialDigital“1 (MD) has been started. Numerous projects concerning digitalization, including the copper related project „KupferDigital“ (copper digital) have been initiated under the umbrella of MD. The initiative strives to address numerous issues concerning data access, exchange, security, provenance and sovereignty. Heterogeneous data origin, storage and evaluation often result in problems concerning comparability and reproducibility of scientific and technological results. In many cases material data are recorded, but the methods of testing are insufficiently described, or such information is not communicated along with the raw data. The material data can also have numerous different formats such as paper printouts, pdfs, excel sheets or csv-files. Hence, gathering and integrating material data from different sources is challenging for potential users like materials scientists and engineers, especially if there are contradictory data where the reasons for contradictions is not clear due their vague description. In order to address these problems, data should comply to the so called „FAIR“ principle which calls for data to be findable, accessible, interoperable, and reusable (FAIR)2 and hence be accessible via so-called decentralized but interconnected data spaces. By using knowledge representation withontologies, data can be enriched with meaning and the methods of the testing procedures can be accurately provided. In this presentation we want to introduce our approach to such knowledge representation based on a high-throughput alloy development process for Cu-based alloys³ along with characterization techniques such as hardness testing and microstructural characterization (e.g. EBSD – Electron Backscattered Diffraction). T2 - Copper Alloys Conference CY - Dusseldorf, Germany DA - 22.11.2022 KW - Copper KW - Life cycle KW - Ontology PY - 2022 AN - OPUS4-56406 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schilling, Markus T1 - Zugversuchsdaten FAIR integriert: Von der normenkonformen Ontologie bis zu interoperablen Daten im Triple Store N2 - Mit der Digitalisierung von Materialien und Prozessen ist ein Paradigmenwechsel in der Materialentwicklung, -gestaltung und -optimierung verbunden, welcher gleichermaßen vielseitige Möglichkeiten eröffnet und eine große Herausforderung darstellt. Insbesondere sind bei den Digitalisierungsbestrebungen die Qualitätssicherung von Prozessen und Ausgabedaten sowie die Interoperabilität zwischen Anwendungen nach FAIR-Prinzipien (Findability, Accessibility, Interoperability, Reusability) sicherzustellen. Dies umfasst die Speicherung, Verarbeitung und Abfrage von Daten in möglichst standardisierter Form, wobei entsprechend auch Normungs- und Standardisierungsgremien beteiligt werden müssen. Um der Herausforderung gerecht zu werden, Materialdaten für alle Beteiligten konsistent zu kontextualisieren, müssen alle notwendigen Informationen zum Zustand des Materials inklusive produktions- und anwendungsbedingter Veränderungen über eine einheitliche, maschinenlesbare Beschreibung verfügbar gemacht werden. Hierfür sollen Ontologien genutzt werden, da sie maschinenverständliche und -interpretierbare Wissensrepräsentationen durch semantische Konzeptualisierungen ermöglichen, die für das Datenmanagement und die Digitalisierung im Bereich der Materialwissenschaften benötigt werden. Dieses hochaktuelle Thema der Integration und Wiederverwendung von Wissen und Daten aus Herstellung, Bearbeitung und Charakterisierung von Materialien wird in den Projekten Innovationsplattform MaterialDigital (PMD, materialdigital.de) und Materials-open-Lab (Mat-o-Lab, matolab.org) adressiert. Diese beiden unter der Beteiligung der Bundeanstalt für Materialforschung und -prüfung (BAM) durchgeführten Projekte wurden auf der 39. Vortrags- und Diskussionstagung „Werkstoffprüfung“ (2021) grundlegend vorgestellt. In dieser Präsentation sollen die Weiterentwicklungen hinsichtlich der Speicherung von Zugversuchsdaten gemäß einer normenkonformen ontologischen Repräsentation vorgestellt werden. Das umfasst den Weg von der Entwicklung einer Ontologie nach Norm, der Konvertierung von Daten aus Standardtests in das interoperable RDF-Format bis hin zur Verknüpfung von Ontologie und Daten. Letztendlich können die entsprechenden Daten in einem Triple Store abgelegt und abgefragt werden. Die übliche Standardisierung von mechanischen Prüfverfahren im Bereich der Materialwissenschaft und Werkstofftechnik dient als solide Grundlage für die Ontologieentwicklung. Daher wurde der Zugversuch von Metallen bei Raumtemperatur nach DIN EN ISO Norm 6892-1:2019-11 als einer der ersten Anwendungsfälle in den genannten Projekten ausgewählt. Die Betrachtung und Beschreibung des Zugversuchs beinhaltet sowohl dessen ontologische Darstellung als auch eine exemplarische Datengenerierung. Die semantische Verbindung von Ontologie und Daten führt zu Interoperabilität und einer verbesserten Abfragefähigkeit. T2 - Tagung Werkstoffprüfung 2022 CY - Dresden, Germany DA - 27.10.2022 KW - Ontologie KW - Semantisches Web KW - Wissensrepräsentation KW - Digitalisierung KW - Zugversuch PY - 2022 AN - OPUS4-56130 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bayerlein, Bernd T1 - Towards interoperability: Digital representation of a material specific characterization method N2 - Certain metallic materials gain better mechanical properties through controlled heat treatments. In age-hardenable aluminum alloys, the strengthening mechanism is based on the controlled formation of nanometer sized precipitates, which hinder dislocation movement. Analysis of the microstructure and especially the precipitates by transmission electron microscopy allows identification of precipitate types and orientations. Dark-field imaging is often used to image the precipitates and quantify their relevant dimensions. The present work aims at the digital representation of this material-specific characterization method. Instead of a time-consuming, manual image analysis, a digital approach is demonstrated. The integration of an exemplary digital workflow for quantitative precipitation analysis into a data pipeline concept is presented. Here ontologies enable linking of contextual information to the resulting output data in a triplestore. Publishing digital workflow and ontologies ensures the reproducibility of the data. The semantic structure enables data sharing and reuse for other applications and purposes, demonstrating interoperability. T2 - TMS - 7th World Congress on Integrated Computational Materials Engineering (ICME) CY - Orlando, Florida, USA DA - 21.05.2023 KW - Ontology KW - Semantic Interoperability KW - Digtial Representation KW - Data Management KW - Reproducibility KW - FAIR PY - 2023 AN - OPUS4-57548 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Shakeel, Y. T1 - NFDI-MatWerk - Reference Datasets N2 - Within NFDI-MatWerk (“National Research Data Infrastructure for Material Sciences”/ “Nationale Forschungsdateninfrastruktur für Materialwissenschaften und Werkstofftechnik“), the Task Area Materials Data Infrastructure (TA-MDI) will provide tools and services to easily store, share, search, and analyze data and metadata. Such a digital materials environment will ensure data integrity, provenance, and authorship. The MatWerk consortium aims to develop specific solutions jointly with Participant Projects (PPs), which are scientific groups or institutes covering different domains, from theory and simulations to experiments. The Data Exploitation Methods group of the Karlsruhe Institute of Technology-Steinbuch Centre of Computing, as part of TA-MDI, is developing specific solutions in close collaboration with three PPs. PP07, together with the University of Stuttgart, aims at the image-based prediction of the material properties of stochastic microstructures using large-scale supercomputers. PP13, in cooperation with the University of Saarland, focuses on tomographic methods at various scales in materials research. PP18, together with the Federal Institute for Materials Research and Testing (“Bundesanstalt für Materialforschung und -prüfung”), aspires to define the criteria for materials reference datasets and usage analytics. The requirements and goals are comparable for each PP: their research outputs, which are scientific datasets, should conform to the FAIR (Findable, Accessible, Interoperable, Reusable) principles. We aim to shape them from a data management perspective making use of the FAIR Digital Object concept, including structured metadata and storage solutions. The results will be a blueprint which will act as a reference for future datasets. Even though the collaboration is in an early stage, the initial steps already show the added value of this approach. This research has been supported by the Federal Ministry of Education and Research (BMBF) – funding code M532701 / the Deutsche Forschungsgemeinschaft (DFG, German Research Foundation) - project number NFDI 38/1, project no. 460247524. T2 - HMC Conference 2022 CY - Online meeting DA - 05.10.2022 KW - NFDI KW - NFDI-MatWerk KW - Reference Data KW - FAIR KW - Creep PY - 2022 AN - OPUS4-56611 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Sonntag, Nadja A1 - Jürgens, M. A1 - Uhlemann, Patrick A1 - Skrotzki, Birgit A1 - Olbricht, Jürgen T1 - Datasets for Service-Like Creep-Fatigue Experiments on Grade P92 Steel N2 - The dataset contains experimental mechanical data from complex service-like creep-fatigue experiments performed isothermally at 620 °C and a low strain amplitude of 0.2 % on tempered martensite-ferritic grade P92 steel. The data sets in text file format provide cyclic deformation (min. and max. stresses) and the total (hysteresis) data of all recorded fatigue cycles for three different creep-fatigue experiments: 1) a standard relaxation fatigue (RF) test with symmetrical dwell times of three minutes introduced at minimum and maximum strain, 2) a fully strain-controlled service-like relaxation (SLR) test combining these three-minute peak strain dwells with a 30-minute dwell in between at zero strain, and 3) a partly stress-controlled service-like creep (SLC) test combining the three-minute peak strain dwells with 30-minute dwells at constant stress. Further information on data and data acquisition, analysis, and experimental details are given in “Experimental Data from Service-Like Creep-Fatigue Experiments on Grade P92 Steel”, submitted to Data in Brief. Additional analyses of these datasets, as well as experimental findings and discussions are presented in “Creep-Fatigue of P92 in Service-Like Tests with Combined Stress- and Strain-Controlled Dwell Times”, submitted to International Journal of Fatigue. KW - Creep-fatigue KW - Stress relaxation KW - Dwell-Fatigue KW - Tempered martensite-ferritic steel PY - 2022 DO - https://doi.org/10.5281/zenodo.7198218 PB - Zenodo CY - Geneva AN - OPUS4-55995 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Radners, Jan T1 - Aluminum High Temperature Fatigue N2 - The high operating temperatures of radial compressor wheels in exhaust gas turbochargers lead to abchange in the original microstructure of the heat-resistant aluminum alloy EN AW-2618A (overaging). This is caused by thermal loads that are close to the age hardening temperature and can even exceed it for a short time. The aging mechanisms have been investigated together with low cycle fatigue (LCF), thermomechanical fatigue (TMF) and creep up to max. 190 °C in previous research projects. The behavior of the alloy under high cycle fatigue (HCF) and the influence of load spectra have hardly been investigated. Since the operating temperatures of centrifugal compressors are expected to increase in the future, this research project investigated the HCF behavior at 230 °C, a test temperature significantly higher than the age hardening temperature. The objectives of the project were to establish a suitable experimental database, to understand the relevant microstructural processes, and to further develop and adapt suitable models and evaluation methods. In addition to a basic characterization of the HCF behavior in the initial condition T61, the experimental investigation program included targeted mechanical tests to isolate the influencing factors of mean stress (𝑅 = −1, 𝑅 = 0.1), material overaging (T61, 10 h/230 °C, 1000 h/230 °C), test temperature (20 °C, 230 °C), test frequency (0.2 Hz, 20 Hz) as well as variable amplitudes. On this basis, the models and evaluation methods developed in the previous projects were adapted and further developed to reflect thermal and mechanical loads in the lifetime assessment. T2 - The FVV Transfer + Networking Event (Herbst 2023) CY - Würzburg, Germany DA - 04.10.2023 KW - Aluminum alloys KW - Fatigue KW - EN AW-2618A PY - 2023 AN - OPUS4-58537 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schilling, Markus T1 - FAIR data in PMD: Development of MSE mid-level and standard-compliant application ontologies N2 - The efforts taken within the project ‘platform MaterialDigital’ (PMD, materialdigital.de) to store FAIR data in accordance with a standard-compliant ontological representation (‘application ontology’) of a tensile test of metals at room temperature (ISO 6892-1:2019-11) will be presented. This includes the path from developing an ontology in accordance with the respective standard, converting ordinary data obtained from standard tests into the interoperable RDF format, up to connecting the ontology and data. The semantic connection of the ontology and data leads to interoperability and an enhanced ability of querying. For further reusability of data and knowledge semantically stored, the PMD core ontology (PMDco) was developed, which is a mid-level ontology in the field of MSE. The semantic connection of the tensile test application ontology to the PMDco is also presented. Moreover, Ontopanel, a tool for domain experts facilitating visual ontology development and mapping for FAIR data sharing in MSE, is introduced briefly. T2 - World Congress on Integrated Computational Materials and Engineering (ICME) CY - Orlando, Florida, USA DA - 21.05.2023 KW - Digitalization KW - Semantic Web Technologies KW - FAIR KW - Data Interoperability KW - PMD Core Ontology KW - Tensile Test Ontology PY - 2023 AN - OPUS4-57549 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schilling, Markus T1 - Seamless Science in Platform MaterialDigital (PMD): Demonstration of Semantic Data Integration as Good Practices N2 - Following the new paradigm of materials development, design, and optimization, digitalization is the main goal in materials sciences and engineering (MSE) which imposes a huge challenge. In this respect, the quality assurance of processes and output data as well as the interoperability between applications following FAIR principles are to be ensured. For storage, processing, and querying of data in contextualized form, Semantic Web technologies (SWT) are used since they allow for machine-actionable and human-readable knowledge representations needed for data management, retrieval, and (re)use. The project ‘platform MaterialDigital’ (PMD) aims to bring together and support interested parties from both industrial and academic sectors in a sustainable manner in solving digitalization tasks and implementing digital solutions. Therefore, the establishment of a virtual material data space and the systematization of the handling of hierarchical, process-dependent material data are focused. Core points to be dealt with are the development of agreements on data structures and interfaces implemented in distinct software tools and to offer users specific support in their projects. Furthermore, the platform contributes to a standardized description of data processing methods in materials research. In this respect, selected MSE methods are semantically represented on a prototypical basis which are supposed to serve as best practice examples with respect to knowledge representation and the creation of knowledge graphs used for material data. Accordingly, this poster presentation illustrates demonstrators developed and deployed within the PMD project. Semantically anchored using the mid-level PMD Core Ontology (PMDco), they address data transformation leading to a novel data management which is based on semantic integrated data. The PMD data acquisition pipeline (DAP), which is fueled by traditional, diverse data formats, and a pipeline applying an electronic laboratory notebook (ELN) as data source are displayed. Additionally, the efficient combination of diverse datasets originating from different sources is demonstrated by the representation of a use case dealing with the well-known Orowan relation. T2 - Materials Science and Engineering Congress 2024 CY - Darmstadt, Germany DA - 24.09.2024 KW - Semantic Data KW - Data Integration KW - Digitalization KW - Demonstrators PY - 2024 AN - OPUS4-61136 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bayerlein, Bernd A1 - Waitelonis, Jörg A1 - Birkholz, Henk A1 - Jung, Matthias A1 - Schilling, Markus A1 - v. Hartrott, Philipp A1 - Bruns, Marian A1 - Schaarschmidt, Jörg A1 - Beilke, Kristian A1 - Mutz, Marcel A1 - Nebel, Vincent A1 - Königer, Veit A1 - Beran, Lisa A1 - Kraus, Tobias A1 - Vyas, Akhilesh A1 - Vogt, Lars A1 - Blum, Moritz A1 - Ell, Basil A1 - Chen, Ya‐Fan A1 - Waurischk, Tina A1 - Thomas, Akhil A1 - Durmaz, Ali Riza A1 - Ben Hassine, Sahar A1 - Fresemann, Carina A1 - Dziwis, Gordian A1 - Beygi Nasrabadi, Hossein A1 - Hanke, Thomas A1 - Telong, Melissa A1 - Pirskawetz, Stephan A1 - Kamal, Mohamed A1 - Bjarsch, Thomas A1 - Pähler, Ursula A1 - Hofmann, Peter A1 - Leemhuis, Mena A1 - Özçep, Özgür L. A1 - Meyer, Lars‐Peter A1 - Skrotzki, Birgit A1 - Neugebauer, Jörg A1 - Wenzel, Wolfgang A1 - Sack, Harald A1 - Eberl, Chris A1 - Portella, Pedro Dolabella A1 - Hickel, Tilmann A1 - Mädler, Lutz A1 - Gumbsch, Peter T1 - Concepts for a Semantically Accessible Materials Data Space: Overview over Specific Implementations in Materials Science N2 - This article describes advancements in the ongoing digital transformation in materials science and engineering. It is driven by domain‐specific successes and the development of specialized digital data spaces. There is an evident and increasing need for standardization across various subdomains to support science data exchange across entities. The MaterialDigital Initiative, funded by the German Federal Ministry of Education and Research, takes on a key role in this context, fostering collaborative efforts to establish a unified materials data space. The implementation of digital workflows and Semantic Web technologies, such as ontologies and knowledge graphs, facilitates the semantic integration of heterogeneous data and tools at multiple scales. Central to this effort is the prototyping of a knowledge graph that employs application ontologies tailored to specific data domains, thereby enhancing semantic interoperability. The collaborative approach of the Initiative's community provides significant support infrastructure for understanding and implementing standardized data structures, enhancing the efficiency of data‐driven processes in materials development and discovery. Insights and methodologies developed via the MaterialDigital Initiative emphasize the transformative potential of ontology‐based approaches in materials science, paving the way toward simplified integration into a unified, consolidated data space of high value. KW - Semantic Interoperability KW - Data Spaces KW - Integration Workflows KW - MaterialDigital PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-622952 DO - https://doi.org/10.1002/adem.202401092 SN - 1527-2648 SP - 1 EP - 25 PB - Wiley-VCH CY - Weinheim AN - OPUS4-62295 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Hickel, Tilmann A1 - Richter, Silke A1 - Bitzek, E. A1 - Ávila Calderón, Luis A1 - Gedsun, A. A1 - Forti, M. A1 - Hammerschmidt, T. A1 - Olbricht, Jürgen A1 - Skrotzki, Birgit T1 - NFDI-MatWerk/IUC02 Definition for Reference Data of Materials N2 - This definition was agreed within the infrastructure use case IUC02 “Framework for curation and distribution of reference datasets” of the consortium NFDI-MatWerk. It is broadly formulated to cover experimental and simulation MSE data and will be developed further in agreement with the MSE community. KW - Referenzdaten KW - Digitalisierung KW - NFDI-MatWerk KW - Research Data Management KW - Reference Data PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-611688 DO - https://doi.org/10.5281/zenodo.11667673 PB - Zenodo CY - Geneva AN - OPUS4-61168 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wang, Lei A1 - Darvishi Kamachali, Reza T1 - Incorporating elasticity into CALPHAD-informed density-based grain boundary phase diagrams reveals segregation transition in Al-Cu and Al-Cu-Mg alloys N2 - The phase-like behavior of grain boundaries (GBs), recently evidenced in several materials, is opening up new possibilities in the design of alloy microstructures. In this context, GB phase diagrams are contributing to a predictive description of GB segregation and (interfacial) phase changes. The influence of chemo-mechanical solute-GB interactions on the GB phase diagram remains elusive so far. This is particularly important for multi-component alloys where the elastic interactions among solute atoms, of various sizes and bonding energies, can prevail, governing a complex co-segregation phenomenon. Recently, we developed a density-based model for GB thermodynamics that intrinsically accounts for GB elasticity in pure elements. In this work, we incorporate the homogeneous and heterogeneous elastic energies associated with the solutes into the density-based framework. We derive the multi-component homogeneous elastic energy by generalizing the continuum misfitting sphere model and extend it for GBs. The density-based free energy functional directly uses bulk CALPHAD thermodynamic data. The model is applied to binary and ternary Al alloys. We reveal that the elastic energy can profoundly affect the GB solubility and segregation behavior, leading to Cu segregation in otherwise Cu-depleted Al GBs. Consequently, GB segregation transition, i.e., a jump in the GB segregation as a function of alloy composition, is revealed in Al-Cu and Al-Cu-Mg alloy systems with implications for subsequent GB precipitation in these alloys. CALPHAD-informed elasticity-incorporated GB phase diagrams enable addressing a broader range of GB phenomena in engineering multi-component alloys. KW - Grain boundary thermodynamics KW - Density-based model KW - Al alloys KW - Grain boundary phase diagram KW - CALPHAD KW - Elastic energy PY - 2021 DO - https://doi.org/10.1016/j.commatsci.2021.110717 VL - 199 SP - 110717 PB - Elsevier B.V. AN - OPUS4-53058 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Darvishi Kamachali, Reza T1 - A model for grain boundary thermodynamics N2 - Systematic microstructure design requires reliable thermodynamic descriptions of each and all microstructure elements. While such descriptions are well established for most bulk phases, thermodynamic assessment of microstructure defects is challenging because of their individualistic nature. In this paper, a model is devised for assessing grain boundary thermodynamics based on available bulk thermodynamic data. We propose a continuous relative atomic density field and its spatial gradients to describe the grain boundary region with reference to the homogeneous bulk and derive the grain boundary Gibbs free energy functional. The grain boundary segregation isotherm and phase diagram are computed for a regular binary solid solution, and qualitatively benchmarked for the Pt–Au system. The relationships between the grain boundary's atomic density, excess free volume, and misorientation angle are discussed. Combining the current density-based model with available bulk thermodynamic databases enables constructing databases, phase diagrams, and segregation isotherms for grain boundaries, opening possibilities for studying and designing heterogeneous microstructures. KW - Phase Diagram KW - Thermodynamics KW - Grain boundary PY - 2020 VL - 10 IS - 45 SP - 26728 EP - 26741 AN - OPUS4-51268 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fedelich, Bernard T1 - Untersuchung des Kriechverhaltens einer Nickelbasis-Superlegierung bei ultrahohen homologen Temperaturen und Anwendung auf das heiß-isostatische Pressen (HIP) N2 - Mit Hilfe des HIP-Verfahrens („Hot Isostatic Pressing“) werden Poren in der einkristallinen Nickel-Basis Superlegierung CMSX-4 kontinuierlich geschrumpft und dadurch die nach der Erstarrung und der Wärmebehandlung vorhandene Porosität stark reduziert. In diesem Beitrag werden experimentelle und numerische Untersuchungen zu den Mechanismen der Porenschrumpfung zusammengefasst. Es zeigt sich, dass das Verformungsverhalten während Kriechversuchen bei der HIP-Temperatur durch Versetzungsgleitung auf oktaedrischen Ebenen dominiert wird. Dagegen zeigen Messungen der Porositätsabnahme und Simulationen des Porenschließens, dass die Kinetik der Porenschrumpfung durch das Phänomen der Leerstellendiffusion zwischen Poren und Kleinwinkelkorngrenzen („Low Angle Boundary“, LAB) bestimmt wird. Im Gegensatz führt die klassische Kristallviskoplastizität zu einer systematischen Überschätzung dieser Kinetik. Der scheinbare Widerspruch lässt sich auflösen, wenn man bedenkt, dass auf der Skala der Poren Versetzungsquellen nicht gleichmäßig verteilt sind, wie in der konventionellen Kristallplastizität implizit angenommen wird. Stattdessen wird in einem weiterführenden Modell davon ausgegangen, das Kleinwinkelkorngrenzen (LABs) als Versetzungsquellen fungieren, während die Scherspannungen sehr stark in der Nähe der Poren lokalisiert sind, was die Emission von Versetzungen deutlich reduziert. T2 - Langzeitverhalten warmfester Stähle und Hochtemperaturwerkstoffe CY - Online meeting DA - 27.11.2020 KW - HIP KW - Superlegierung KW - Kriechen PY - 2020 AN - OPUS4-51795 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ávila Calderón, Luis T1 - Mechanical behaviour of AM metals: Creep of LPBF 316L and low-cycle-fatigue of LMD Ti-6Al-4V N2 - Additively manufactured metallic materials have already started to find application in safety-relevant components. However, this has only happened for certain materials and specific applications and loading conditions, since there is still an extensive lack of knowledge as well as of historical data regarding their mechanical behaviour. This contribution aims to address this lack of understanding and historical data concerning the creep behaviour of the austenitic stainless steel 316L manufactured by Laser-Powder-Bed-Fusion (L-PBF) and the low-cycle-fatigue behaviour of the titanium alloy Ti-6Al-4V manufactured by Laser-Metal-Deposition (LMD). Furthermore, it aims to assess their mechanical behaviour against their conventional counterparts. With that in mind, specimens from conventional and additive materials are tested and their mechanical behaviour analysed based on characteristic curves. To understand the damage behaviours the materials are characterized by destructive and non-destructive techniques before and after failure. T2 - 1st Workshop on In-situ Monitoring and Microstructure Development in Additive Manufacturing CY - Online Meeting DA - 10.12.2020 KW - Ti-6Al-4V KW - 316L KW - Additive manufacturing KW - Creep behaviour KW - Low-cycle-fatigue behaviour PY - 2020 AN - OPUS4-51879 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Fedelich, Bernard ED - Cailletaud, G. ED - Cormier, J. ED - Eggeler, G. ED - Maurel, V. ED - Nazé, L. T1 - Crystal plasticity models: dislocation based N2 - The large number of TEM investigations and the regular microstructure of single-crystal nickel-base superalloys has boosted the development of a number of physically motivated constitutive laws. In contrast to the more phenomenological models discussed in the next chapter, these models use dislocation densities as internal variables. Obvious advantages are that the computed densities can be compared to TEM observations and the Deformation mechanisms can be easier translated into mathematical equations. KW - Nickel-base superalloys KW - Creep KW - Plasticity PY - 2022 SN - 978-0-12-819357-0 SP - 401 EP - 427 PB - Elsevier Inc. ET - 1 AN - OPUS4-53436 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fedelich, Bernard T1 - Experimental and analytical investigation of Low Cycle Fatigue Damage at notches in a polycrystalline Nickel base superalloy N2 - Turbine blades often contain cylindric holes used to generate an air film that protects the blade alloy from the hot gases. These cooling holes of diameter around one mm are drilled by laser through the thickness of the blades. Unfortunately, the resulting stress concentration and the drilling-induced damage are known to favor crack initiation from the holes. It is thus necessary to assess the impact of these cooling holes on the structural integrity of the blades. Since cracks initiate very readily, the fatigue life of the components is mainly controlled by the propagation of the cracks in the stress gradient induced by the holes. For this purpose, displacement controlled high-temperature LCF (Low-Cycle-Fatigue) tests were performed with center hole specimens of a coarse-grained Nickel base Superalloy. The tests were stopped after a defined load drop. In addition, crack propagation tests with Double Edge Notch specimens were performed. Moreover, specimens with different hole surface finishes were investigated, which showed a detrimental effect of the hole surface roughness. In parallel, an evaluation of the LCF tests based on a fracture mechanics-based model (Madia et al., Eng. Fract. Mech., 2018) has been applied. Thereby, the specimen life is controlled by the crack propagation time until failure. Crack growth is controlled by a modified NASGRO equation accounting for large-scale yielding and a progressive build-up of crack closure. The initial crack size has been derived from the measurements of defects around the borehole. A reasonable agreement between predicted and measured lifetimes is observed if one keeps in mind the large uncertainty regarding the effective shape of the cracks. T2 - 23rd European Conference on Fracture CY - Funchal, Madeira, Portugal DA - 27.06.2022 KW - Nickel-base superalloys KW - Notches KW - LCF PY - 2022 AN - OPUS4-55338 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dzugan, J. A1 - Lucon, E. A1 - Koukolikova, M. A1 - Li, Y. A1 - Rzepa, S. A1 - Yasin, M.S. A1 - Shao, S. A1 - Shamsaei, N. A1 - Seifi, M. A1 - Lodeiro, M. A1 - Lefebvre, F. A1 - Mayer, U. A1 - Olbricht, Jürgen A1 - Houska, M. A1 - Mentl, V. A1 - You, Z. T1 - ASTM interlaboratory study on tensile testing of AM deposited and wrought steel using miniature specimens N2 - An interlaboratory study, involving eigth international laboratories and coordinated by COMTES FHT (Czech Republic), was conducted to validate tensile measurements obtained using miniature specimens on additively manufactured (AM) components and artifacts. In addition to AM 316L stainless steel (316L SS), a wrought highstrength steel (34CrNiMo6V, equivalent to AISI 4340) was also used. Based on the results, a precision statement in accordance with ASTM E691 standard practice was developed, intended for inclusion in a proposed annex to the ASTM E8/E8M tension testing method. The primary outcomes of the study highlighted the agreement between yield and tensile strength measured from miniature and standard-sized tensile specimens. Furthermore, most tensile properties exhibited similar standard deviations, offering users insight into the efficacy of miniature specimen applications. KW - 316L stainless steel KW - Additive manufacturing KW - High-strength steel KW - Miniature specimens KW - Tensile tests PY - 2024 DO - https://doi.org/10.1016/j.tafmec.2024.104410 SN - 0167-8442 VL - 131 SP - 1 EP - 13 PB - Elsevier B.V. AN - OPUS4-60180 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Darvishi Kamachali, Reza A1 - Wang, L. T1 - Elastic energy of multi-component solid solutions and strain origins of phase stability in high-entropy alloys N2 - The elastic energy of mixing for multi-component solid solutions is derived by generalizing Eshelby's sphere-in-hole model. By surveying the dependence of the elastic energy on the chemical composition and lattice misfit, we derive a lattice strain coefficient λ*. Studying several high-entropy alloys and superalloys, we propose that most solid solution multi-component alloys are stable when λ*<0.16, generalizing the Hume-Rothery atomic-size rule for binary alloys. We also reveal that the polydispersity index δ, frequently used for describing strain in multi-component alloys, directly represents the elastic energy e with e=qδ², q being an elastic constant. Furthermore, the effects of (i) the number and (ii) the atomic-size distribution of constituting elements on the phase stability of high-entropy alloys were quantified. The present derivations and discussions open for richer considerations of elastic effects in high-entropy alloys, offering immediate support for quantitative assessments of their thermodynamic properties and studying related strengthening mechanisms. KW - Ordering KW - High-entropy alloys KW - Alloy design KW - Strain energy KW - Phase stability PY - 2022 DO - https://doi.org/10.1016/j.scriptamat.2021.114226 SN - 1359-6462 VL - 206 SP - 1 EP - 6 PB - Elsevier CY - Amsterdam AN - OPUS4-53427 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ganesh, Rahul T1 - Numerical calculation of ΔCTOD for thermomechanical fatigue crack growth N2 - The cyclic crack tip opening displacement ΔCTOD is a promising loading Parameter to quantify the crack propagation under thermomechanical fatigue (TMF). In this work, suitable techniques are investigated and compared for an accurate calculation of ΔCTOD under TMF loading using a viscoplastic temperature dependent material model. It turned out that collapsed special crack tip elements give the best results. An efficient FEM-technique is developed to simulate the incremental crack growth by successive remeshing, whereby the deformations and internal state variables are mapped from the old mesh onto the new one. The developed techniques are demonstrated and discussed for two-dimensional examples like TMF-specimens. Recommendations are made regarding important numerical control parameters like optimal size of crack tip elements, length of crack growth increment in relation to plastic zone size and ΔCTOD value. T2 - 53. Tagung des Arbeitskreises "Bruchmechanik und Bauteilsicherheit" CY - Online meeting DA - 18.02.2021 KW - Crack tip opening displacement KW - Thermomechanical fatigue KW - Crack growth PY - 2021 AN - OPUS4-52520 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ávila Calderón, Luis A1 - Schriever, Sina T1 - BAM Reference Data: Creep of Single-Crystal Ni-Based Superalloy CMSX-6 N2 - This publication provides comprehensive metadata and test results of constant force creep tests according to DIN EN ISO 204:2019-4 on the single crystal Ni-based superalloy CMSX-6 at T = 980 °C and initial stresses between 140 MPa and 230 MPa. The tests were carried out in an accredited test laboratory using calibrated measuring equipment. The data were audited and are BAM reference data. KW - NFDI-MatWerk KW - Digitalisierung KW - CMSX-6 KW - Creep KW - Reference Data KW - Referenzdaten KW - Ni-Based Superalloy PY - 2024 DO - https://doi.org/10.5281/zenodo.13937986 PB - Zenodo CY - Geneva AN - OPUS4-61649 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Epishin, A. I. A1 - Fedelich, Bernard A1 - Viguier, B. A1 - Schriever, Sina A1 - Svetlov, I. L. A1 - Petrushin, N. V. A1 - Saillard, R. A1 - Proietti, A. A1 - Poquillon, D. A1 - Chyrkin, A. T1 - Creep of single-crystals of nickel-base γ-alloy at temperatures between 1150 °C and 1288 °C N2 - A γ-analogue of the superalloy CMSX-4 that does not contain the strengthening γ′ -phase and only consists of the γ-solid solution of nickel has been designed, solidified as single-crystals of different orientations, and tested under creep conditions in the temperature range between 1150 and 1288 °C. The tests have revealed a very high creep anisotropy of this alloy, as was previously found for CMSX-4 at supersolvus temperature of 1288 °C. This creep anisotropy could be explained by the dominance of 〈011〉{111} octahedral slip. Furthermore, the analysis of the creep data has yielded a high value of the creep activation energy, Qc≈442 kJ/mol, which correlates with the high activation energy of Re diffusion in Ni. This supports the hypothesis that dislocation motion in the γ-matrix of Re-containing superalloys is controlled by the diffusion of the Re atoms segregating at the dislocation core. The Norton stress exponent n is close to 5, which is a typical value for pure metals and their alloys. The absence of γ′ -reprecipitation after high-temperature creep tests facilitates microstructural investigations. It has been shown by EBSD that creep deformation results in an increasing misorientation of the existing low angle boundaries. In addition, according to TEM, new low angle boundaries appear due to reactions of the a/2 〈011〉 mobile dislocations and knitting of new networks. KW - Nickel alloys KW - Single-crystals KW - Creep KW - Electron microscopy KW - Deformation mechanisms PY - 2021 DO - https://doi.org/10.1016/j.msea.2021.141880 SN - 0921-5093 VL - 825 SP - 1 EP - 13 PB - Elsevier CY - Amsterdam AN - OPUS4-53132 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fedelich, Bernard A1 - Feldmann, Titus A1 - Haftaoglu, Cetin A1 - Nolze, Gert A1 - Schriever, Sina A1 - Epishin, A. A1 - Camin, B. A1 - Lopez-Galilea, I. A1 - Ruttert, B. A1 - Theisen, W. T1 - Untersuchung des Kriechverhaltens einer Nickelbasis-Superlegierung bei ultrahohen homologen Temperaturen und Anwendung auf das heiß-isostatische Pressen (HIP) N2 - Mit Hilfe des HIP-Verfahrens („Hot Isostatic Pressing“) werden Poren in der einkristallinen Nickel-Basis Superlegierung CMSX-4 kontinuierlich geschrumpft und dadurch die nach der Erstarrung und der Wärmebehandlung vorhandene Porosität stark reduziert. In diesem Beitrag werden experimentelle und numerische Untersuchungen zu den Mechanismen der Porenschrumpfung zusammengefasst. Es zeigt sich, dass das Verformungsverhalten während Kriechversuchen bei der HIP-Temperatur durch Versetzungsgleitung auf oktaedrischen Ebenen dominiert wird. Dagegen zeigen Messungen der Porositätsabnahme und Simulationen des Porenschließens, dass die Kinetik der Porenschrumpfung durch das Phänomen der Leerstellendiffusion zwischen Poren und Kleinwinkelkorngrenzen („Low Angle Boundary“, LAB) bestimmt wird. Im Gegensatz führt die klassische Kristallviskoplastizität zu einer systematischen Überschätzung dieser Kinetik. Der scheinbare Widerspruch lässt sich auflösen, wenn man bedenkt, dass auf der Skala der Poren Versetzungsquellen nicht gleichmäßig verteilt sind, wie in der konventionellen Kristallplastizität implizit angenommen wird. Stattdessen wird in einem weiterführenden Modell davon ausgegangen, das Kleinwinkelkorngrenzen (LABs) als Versetzungsquellen fungieren, während die Scherspannungen sehr stark in der Nähe der Poren lokalisiert sind, was die Emission von Versetzungen deutlich reduziert. T2 - Langzeitverhalten warmfester Stähle und Hochtemperaturwerkstoffe CY - Online meeting DA - 27.11.2020 KW - HIP KW - Superlegierung KW - Kriechen PY - 2020 SN - 978-3-946885-95-5 VL - 2020 SP - 28 EP - 39 PB - Forschungsvereinigung Warmfeste Stähle und Hochtemperaturwerkstoffe AN - OPUS4-51796 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fedelich, Bernard T1 - Experimental and analytical investigation of high temperature fatigue crack growth at notches in a polycrystalline Nickel base superalloy N2 - The scatter of fatigue crack growth data can become significant for coarse grained materials. By using a probabilistic description of crack propagation as the foundation of a lifetime prediction model, lifetime scatter of laboratory specimens can be reproduced. However, the lifetime of real components is subjected to additional scattering factors such as surface condition or uncertainty regarding direction and shape of emerging cracks. These factors need to be addressed in order to exploit the advantages of probabilistic description, i.e. the reduction of unnecessary conservatisms. High temperature LCF (Low-Cycle-Fatigue) tests were performed with center hole specimens of a coarse-grained Nickel base Superalloy. In addition, crack propagation tests with Double Edge Notch specimens were performed. A procedure to detect the shape of the starting crack that combines the potential drop method and induction thermography was developed. The geometry and the number of notches were varied. Moreover, specimen with different hole surface finishes were investigated, which showed a detrimental effect of the roughness of the hole surface. The results have been compared to predictions of a probabilistic tool for the estimation of lcf lifetime that has been calibrated beforehand on laboratory specimens with and without notches. In parallel, a fracture mechanics-based lifetime model was developed, which includes the initial crack size as a critical parameter. Thereby, the influence of the large grain size (>1mm), and the shape of the starting crack at the notch were considered. Acknowledgements The investigations are conducted as part of the joint research program COOREFLEX-Turbo in the frame of AG Turbo. The work is supported by Siemens AG and the Bundesministerium für Wirtschaft und Technologie (BMWi) as per resolution of the German Federal Parliament under grant number 03ET7071E. T2 - Low Cycle Fatigue 9 CY - Berlin, Germany DA - 21.06.2022 KW - Nickel-base superalloys KW - Notches KW - LCF PY - 2022 AN - OPUS4-55335 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wang, Lei A1 - Darvishi Kamachali, Reza T1 - Density-based Thermodynamics of Microstructure Defects N2 - Systematic microstructure design requires reliable thermodynamic descriptions and phase diagrams of each and all microstructure elements. While such descriptions are well established for most bulk phases, thermodynamic assessment of crystal defects is greatly challenged by their individualistic aspects. In this talk, we present a density-based thermodynamic concept to describe defects based on available bulk thermodynamic data. Here dealing with grain boundaries (GBs), we apply this concept to compute GB (phase) diagram. Applications to segregation engineering of GBs in bulk and nanocrystalline alloys will be presented. We further develop this model to include the effect of elastic interactions due to atom size mismatch and obtain the corresponding GB (phase) diagram for the ternary Al-Cu-Li system. T2 - TMS 2021 CY - Online meeting DA - 15.03.2021 KW - Microstrucrue Design KW - Density-based Thermodynamics PY - 2021 AN - OPUS4-52337 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kianinejad, Kaveh A1 - Czediwoda, Fabian A1 - Glatzel, U. A1 - Völkl, R. A1 - Stöhr, B. A1 - Ávila Calderón, Luis A1 - Schriever, Sina A1 - Saliwan Neumann, Romeo A1 - Fedelich, Bernard A1 - Darvishi Kamachali, Reza T1 - Microstructure-based modelling of the anisotropic creep behaviour in additively manufactured INCONEL 718 N2 - The existing gap in the adequate prediction of the microstructure-property relationships remains a significant barrier to the safe application of the additively manufactured materials. This challenge is fundamentally tied to the intricate microstructural defects that emerge during the processing. Systematic microstructure-based modelling can offer solutions to address this bottleneck. In this work, we utilize a crystal plasticity model, developed for gamma''-strengthened Ni-base alloys and calibrated with single crystal tensile and creep tests of Inconel 718. By systematically refining the representative volume element complexity---from equiaxed to elongated grain morphologies, and from unimodal to bimodal orientation and grain size distributions---we demonstrate how each layer of structural realism contributes to the model’s predictive capacity. Creep tests of laser-based powder bed fusion (PBF-LB/M) manufactured samples in three orientations (with the tensile axis parallel, perpendicular, and 45° tilted relative to the building direction) were performed at 650° C, accompanied by electron backscatter secondary diffraction measurements. The results of our simulations reveal that the bimodal grain morphology and crystallographical texture significantly influence the observed creep anisotropy. We show that the elongated grain structure combined with grain boundary sliding plays a major role in the creep response, specifically in tilted specimens. KW - Additive manufactured Ni-base superalloys KW - Creep Anisotropy KW - Crystal plasticity PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-646884 DO - https://doi.org/10.1016/j.msea.2025.149029 VL - 945 SP - 1 EP - 15 PB - Elsevier B.V. AN - OPUS4-64688 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Darvishi Kamachali, Reza T1 - Interfacial Spinodals N2 - Despite their finite spatial extent, interfaces can have profound impacts on microstructure properties. This is because of their distinct phase-like properties distinguishing them from the adjacent homogeneous bulk structure. When noticed by solute atoms, interfaces can experience their own chemical phase changes. In this talk, we investigate the constrained states of chemically decomposed phases at interfaces. A density-based theory of interfaces is proposed to describe the confined chemical decomposition at general grain boundaries. Here the grain boundary is viewed as a lesser dense, defected structure with reference to the corresponding bulk structure. Using this picture, the thermodynamic origins of interfacial spinodal phenomena are revealed. We also show that transient interfacial spinodals can be activated over a large alloy composition range, enabling kinetic engineering of interfacial chemistry. T2 - TMS 2021 CY - Online meeting DA - 15.03.2021 KW - Microstrucrue Design KW - Spinodal Decomposition KW - Interfacial Spinodal PY - 2021 AN - OPUS4-52338 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Butz, Adam T1 - Detection and prediction of high temperature fatigue crack growth around notches in polycrystalline nickel base alloy N2 - Im Rahmen eines Vorhabens wurden Methoden zur Reduktion des Versuchsaufwandes bei der Modellerstellung für LCF-Lebensdauervorhersage untersucht. Einige dieser Methoden sind hier kurz vorgestellt. N2 - Methods for reducing the experimental effort necessary for the development of LCF life time prediction models were investigated. Some of these methods are briefly presented here. T2 - 4th International Symposium for Fatigue Design and Material Defects CY - Online meeting DA - 26.05.2020 KW - LCF KW - Mechanistic Modelling KW - Fatigue KW - Data Fusion PY - 2020 AN - OPUS4-50904 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ávila Calderón, Luis T1 - Creep behavior and microstructural evolution of LPBF 316L N2 - This presentation shows some experimental results of the characterization of the creep behavior of LPBF 316L, which has been poorly studied and understood to date. The presentation includes results regarding the mechanical properties, the initial microstructural state and its evolution under loading, and the damage mechanism. This work was done within the BAM focus area materials project AGIL. As a benchmark to assess the material properties of the LPBF 316L, a conventionally manufactured variant was also tested. T2 - 2nd Workshop on In-situ Monitoring and Microstructure Development in Additive Manufactured alloys at BAM CY - Online Meeting DA - 19.04.2021 KW - 316L KW - Additive Manufacturing KW - Creep behavior PY - 2021 AN - OPUS4-52682 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Abel, Andreas T1 - Microstructural and mechanical characterisation of cast Fe-Al-Mo-Ti-B alloys N2 - With the advent of variable renewable energies, long-term energy storage capacities and flexible power generation technologies will be required for reliable grid stability. Hence, power plant technologies and turbomachinery components will continue to be developed and employed for efficient re-conversion of stored energy. With the introduction of new working fluids for higher thermal efficiencies, the working conditions of exposed components and materials will require higher corrosion resistance, but with the same mechanical performance, manufacturability and cost. Intermetallic iron aluminide alloys with their outstanding oxidation and corrosion resistance and good high-temperature properties depict a possible candidate for use in high-temperature structural applications. A quinary Fe-26Al-4Mo-0.5Ti-1B solid-solution alloy with eutectic particle hardening particularly demonstrated competitive mechanical properties compared to high-alloy P92 steels in previous studies. To derive standard material specifications with industrially relevant casting strategies, centrifugal investment-cast Fe-25Al-3.7Mo-0.4Ti-1B was characterised with respect to microstructure, thermophysical properties and mechanical properties under quasi-static tensile and creep loading up to 700 °C. Compared to P92 steel, the alloy demonstrated superior tensile strength above 550 °C and lower creep rates at 650 °C if stresses increase above 170 MPa. At lower temperatures though, the mechanical properties were inferior to P92 steel and related Fe-Al-Mo-Ti-B alloys, which was correlated to large grain sizes, a high tendency to surface and bulk cracking and a pronounced effect of tension-compression asymmetry. In further studies on alloy composition with varying Al, Mo and B concentration, a non-linear relationship of solid-solution hardening with solute Mo concentration was found. In this regard, halving Mo was the most effective measure for reducing brittleness without decreasing strength at room and elevated temperatures. Higher solidification rates and grain refinement down to 30 µm by die casting had a positive effect on ambient tensile strength, but were not achievable by investment casting. Dilatometry and hardness measurements indicated a low thermal vacancy hardening effect which was less sensitive to low-temperature annealing than in B2 FeAl alloys. Although mechanical properties up to 550 °C could be considerably improved by alloy development and processing, ductility at room temperature generally remained below 1%, necessitating substantial design margins for components from Fe-Al-Mo-Ti-B alloys. Despite the inherent limitations of alloy and casting process, the gained insights will help to prioritise future areas of research to mature cost-effective higher-order Fe Al alloys for high-temperature structural applications. KW - Hardness KW - Iron aluminide alloy KW - Micro structure KW - Tensile strength KW - Creep strength PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-632810 DO - https://doi.org/10.5445/IR/1000181739 SP - 1 EP - 179 PB - Karlsruher Institut für Technologie (KIT) CY - Karlsruhe AN - OPUS4-63281 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Avila Calderon, Luis Alexander A1 - Schriever, Sina A1 - Hang, Y. A1 - Olbricht, Jürgen A1 - Portella, P. D. A1 - Skrotzki, Birgit T1 - Creep reference data of single-crystal Ni-based superalloy CMSX-6 N2 - The article presents creep data for the single-crystal, [001]-oriented nickel-based superalloy CMSX-6, tested at a temperature of 980 °C under initial stresses ranging from 140 MPa to 230 MPa. The constant-load creep experiments were performed in accordance with DIN EN ISO 204:2019–4 standard within an ISO 17025 accredited laboratory. A total of 12 datasets are included, each of which includes the percentage creep extension as a function of time. The data series and associated metadata were systematically documented using a data schema specifically developed for creep data of single-crystal Ni-based superalloys. This dataset serves multiple purposes: it can be used to compare with one's own creep test results on similar materials, to verify testing setups (e.g., by replicating tests on the same or comparable materials), to calibrate and validate creep models, and to support alloy development efforts. KW - NFDI MatWerk KW - Referenzdaten KW - Kriechen KW - CMSX-6 KW - Digitalisierung PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-654056 DO - https://doi.org/10.1016/j.dib.2025.112436 VL - 65 SP - 1 EP - 11 PB - Elsevier AN - OPUS4-65405 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ávila Calderón, Luis T1 - Management of Reference Data of Creep of Ni-Based Superalloys Exemplified for CMSX-6 N2 - The identification of process-structure-property relationships of materials inevitably requires the combination of research data from different measurements. Therefore, the concepts related to FAIR (findable, accessible, interoperable, reusable) data handling, increasingly reported in literature, are particularly important in the materials science and engineering domain. However, they have not yet been integrated into a single, overarching methodological framework, particularly for reference data. Here, we introduce such a framework, which covers data generation, documentation, handling, storage, sharing, data search and discovery, retrieval, and usage. Furthermore, we prototypically implement it using a real dataset with creep data of a single-crystal CMSX-6 Ni-based superalloy. The implementation is traceable and permanently accessible through open repositories. The individual elements considered in the framework ensure the functionality and usability of the data and, thus, the adherence to the FAIR principles. In conjunction with this, we present a definition for reference data of materials. Our definition underlines particularly the importance of a comprehensive documentation, e.g., on material provenance, data processing procedures, and the software and hardware used, including software-specific input parameters, as these details enable data users or independent parties to assess the quality of the datasets and to reuse and reproduce the results. Reference data that is managed according to the proposed framework can be used to advance knowledge in the materials science and engineering domain, e.g., by identifying new process-structure-property relations. T2 - The 20th International Conference on Strength of Materials CY - Kyoto, Japan DA - 02.06.2025 KW - NFDI-MatWerk KW - Referenzdaten KW - Data schema KW - Creep PY - 2025 AN - OPUS4-63428 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schilling, Markus T1 - Crafting High-Quality, Reliable, and FAIR Data: From Metadata, Schema and Ontologies to Data Management and Knowledge Transfer N2 - Following the new paradigm of materials development, design and optimization, digitalization is the main goal in materials sciences (MS) which imposes a huge challenge. In this respect, the quality assurance of processes and output data as well as the interoperability between applications following FAIR (findability, accessibility, interoperability, reusability) principles are to be ensured. For storage, processing, and querying of data in contextualized form, Semantic Web Technologies (SWT) are used since they allow for machine-actionable and human-readable knowledge representations needed for data management, retrieval, and (re)use. In this respect, the motivation for digital transformation in materials sciences stemming from the need to handle the ever-increasing volume and complexity of data will be elaborated on. By embracing digital tools and methodologies, researchers can enhance the efficiency, accuracy, and reproducibility of their work. The benefits of digital transformation in materials sciences are manifold, including improved data management, enhanced collaboration, and accelerated innovation. Being a core component of this transformation, ensuring data reliability and reproducibility is critical for the advancement of the field, enabling researchers to build on each other's work with confidence. Implementing FAIR data principles facilitates this by making data more accessible and usable across different platforms and studies. Furthermore, Semantic Web technologies (SWT) and ontologies play a crucial role in achieving these goals. Ontologies, typically consisting of the T-Box (terminological component) and A-Box (assertional component), provide a structured framework for representing knowledge. This presentation will outline the path of ontology creation and the formal transformation procedure, highlighting the various ontology levels that organize data into meaningful hierarchies. Real-world use cases presented, such as the Tensile Test Ontology (TTO) and the Orowan Demonstrator, illustrate the practical applications of these technologies. These examples will demonstrate how ontologies can be leveraged to standardize data and facilitate interoperability between different systems and research groups. Finally, in this presentation, Ontopanel is introduced, a tool designed to aid in the creation and management of ontologies. Ontopanel simplifies the process of developing and maintaining ontologies, making it accessible to researchers and practitioners in the field. By integrating these technologies and principles, the materials science community can move towards a more digital, interconnected, and efficient future making the knowledge and education on these topics very valuable. T2 - MaRDA MaRCN FAIR Train Workshop CY - Washington, DC, USA DA - 29.07.2024 KW - FAIR KW - Metadata KW - Digitalization KW - Data Interoperability KW - Ontology KW - Education KW - Workshop PY - 2024 AN - OPUS4-60720 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ávila Calderón, Luis T1 - Management of Reference Data of Creep of Ni-Based Superalloys Exemplified for CMSX-6 N2 - The identification of process-structure-property relationships of materials inevitably requires the combination of research data from different measurements. Therefore, the concepts related to FAIR (findable, accessible, interoperable, reusable) data handling, increasingly reported in literature, are particularly important in the materials science and engineering domain. However, they have not yet been integrated into a single, overarching methodological framework, particularly for reference data. Here, we introduce such a framework, which covers data generation, documentation, handling, storage, sharing, data search and discovery, retrieval, and usage. Furthermore, we prototypically implement it using a real dataset with creep data of a single-crystal CMSX-6 Ni-based superalloy. The implementation is traceable and permanently accessible through open repositories. The individual elements considered in the framework ensure the functionality and usability of the data and, thus, the adherence to the FAIR principles. In conjunction with this, we present a definition for reference data of materials. Our definition underlines particularly the importance of a comprehensive documentation, e.g., on material provenance, data processing procedures, and the software and hardware used, including software-specific input parameters, as these details enable data users or independent parties to assess the quality of the datasets and to reuse and reproduce the results. Reference data that is managed according to the proposed framework can be used to advance knowledge in the materials science and engineering domain, e.g., by identifying new process-structure-property relations. T2 - TMS 2025 Annual Meeting & Exhibition CY - Las Vegas, NV, USA DA - 22.03.2025 KW - Referenzdaten KW - Creep KW - Data schema KW - NFDI-MatWerk PY - 2025 AN - OPUS4-62849 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schilling, Markus T1 - Semantic Technologies in Action: Integrating Mechanical and Microstructure Data in MSE N2 - Semantic technologies (ST) are a powerful tool for storing, processing, and querying data in a contextualized and interoperable manner. They enable machine-actionable and human-readable knowledge representations essential for advanced data management, retrieval, and reuse. As one of the key factors within the frame of the collaborative project platform MaterialDigital (PMD), the establishment of a virtual material data space and the semantic modeling of hierarchical, process-dependent material data is aimed at to serve as best-practice examples of knowledge representation through ontologies and knowledge graphs. In this presentation, the application of ST to a specific use case from the field of materials sciences and engineering (MSE) is demonstrated: the integration and analysis of data related to a 2000 series age-hardenable aluminum alloy. By semantically representing mechanical and microstructural data obtained from tensile tests and dark-field transmission electron microscopy across various aging times, an expandable knowledge graph was constructed that is aligned with the PMD Core Ontology (PMDco) and enriched through the Tensile Test (TTO) and Precipitate Geometry Ontologies. This semantically integrated dataset enables advanced analytical capabilities via SPARQL queries and reveals microstructure–property relationships consistent with the well-known Orowan mechanism. The approach highlights the potential of semantic data integration to support FAIR data principles and to foster a more data-centric and interoperable research infrastructure in MSE. T2 - MSE Research Data Forum 2025 CY - Siegburg, Germany DA - 08.07.2025 KW - Semantic Data KW - Data Integration KW - Digitalization KW - Data Interoperability PY - 2025 AN - OPUS4-63666 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ávila Calderón, Luis T1 - IUC02: Framework for Curation & Distribution of Reference Datasets (On the example of Creep Data of Ni Based superalloys) N2 - A research data management framework to conceptualize & implement a digital infrastructure for the Generation, Distribution, and Utilization of reference datasets of materials is presented. The documentation of the test data is often incomplete. This concerns, e.g., material’s manufacturing process or chemical composition, or test equipment’s description and its calibration status. Our concept addresses this issue by proposing the implementation of a requirements profile. A crucial part of the concept is to reach a community-agreement on the definition of reference data and on the underlying data schema and vocabulary. In this presentation a general workflow overview and the relevance of selected individual subworkflows is presented. T2 - MSE Research Data Forum 2025 CY - Siegburg, Germany DA - 08.07.2025 KW - NFDI MatWerk KW - Referenzdaten KW - Kriechen PY - 2025 AN - OPUS4-64881 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ávila Calderón, Luis T1 - Management of Reference Data of Creep of Ni Based Superalloys Exemplified for CMSX 6 N2 - Research data management (RDM) framework to conceptualize & implement a digital infrastructure for the Generation, Distribution, and Utilization of reference datasets of materials. Documentation of the test data is often incomplete. This concerns, e.g., material’s manufacturing process or chemical composition, or test equipment’s description and its calibration status. Our concept addresses this issue by proposing the implementation of a requirements profile. A crucial part of the concept is to reach a community-agreement on the definition of reference data and on the underlying data schema and vocabulary. T2 - 2. SupERBO Symposium on Superalloys CY - Bochum, Germany DA - 27.02.2025 KW - NFDI MatWerk KW - Referenzdaten KW - Kriechen PY - 2025 AN - OPUS4-64859 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schilling, Markus T1 - Platform MaterialDigital (PMD) - Knowledge Representation, Interoperability, Reliability N2 - Through collaboration in the materials science and engineering (MSE) community, the PMD is collectively developing common standards and prototype solutions for data acquisition, structuring, storage, and processing. This comprises the development of architectural, standardized and foundational ontologies and workflows. Demonstrators resulting from these developments provide good practice examples. The PMD Core Ontology (PMDco) was created as an anchor that allows implementation of semantic data integration. It provides a common and expanding vocabulary to represent and share knowledge while enabling efficient collaboration and promoting interoperability between diverse domains. T2 - Kupfer-Symposium 2025 CY - Schwäbisch-Gmünd, Germany DA - 12.11.2025 KW - Semantic Data KW - Data Integration KW - Digitalization KW - Data Interoperability KW - PMD Core Ontology PY - 2025 AN - OPUS4-64708 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ávila Calderón, Luis A1 - Hammerschmidt, T. A1 - Stotzka, R. T1 - Demonstration of the Infrastructure Use Case 02: Framework for curation and distribution of reference datasets N2 - In our current view, reference datasets in the MSE domain represent specific material properties, e.g., structural, mechanical, … characteristics. A reference dataset must fulfill high-quality standards, not only in precision of measurement but also in a comprehensive documentation of material, processing, and testing history (metadata). This Infrastructure Use Case (IUC) aims to develop a framework for generating reference material datasets using creep data of a single crystal Ni-based superalloy as a best practice example. In a community-driven process, we aim to encourage the discussion and establish a framework for the creation and distribution of reference material datasets. In this poster presentation, we highlight our current vision and activities and intend to stimulate the discussion about the topic reference datasets and future collaborations and work. T2 - NFDI-MatWerk Conference CY - Siegburg, Germany DA - 27.06.2023 KW - Referenzdaten KW - Reference data KW - Creep KW - Metadata schema KW - Syngle Crystal alloy PY - 2023 AN - OPUS4-57924 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schilling, Markus T1 - Seamless Science with the Platform MaterialDigital (PMD): Demonstration of Semantic Data Integration as Good Practices N2 - Following the new paradigm of materials development, design, and optimization, digitalization is the main goal in materials sciences and engineering (MSE) which imposes a huge challenge. In this respect, the quality assurance of processes and output data as well as the interoperability between applications following FAIR principles are to be ensured. For storage, processing, and querying of data in contextualized form, Semantic Web technologies (SWT) are used since they allow for machine-actionable and human-readable knowledge representations needed for data management, retrieval, and (re)use. The project ‘platform MaterialDigital’ (PMD) aims to bring together and support interested parties from both industrial and academic sectors in a sustainable manner in solving digitalization tasks and implementing digital solutions. Therefore, the establishment of a virtual material data space and the systematization of the handling of hierarchical, process-dependent material data are focused. Core points to be dealt with are the development of agreements on data structures and interfaces implemented in distinct software tools and to offer users specific support in their projects. Furthermore, the platform contributes to a standardized description of data processing methods in materials research. In this respect, selected MSE methods are semantically represented on a prototypical basis which are supposed to serve as best practice examples with respect to knowledge representation and the creation of knowledge graphs used for material data. Accordingly, this poster presentation illustrates demonstrators developed and deployed within the PMD project. Semantically anchored using the mid-level PMD Core Ontology (PMDco), they address data transformation leading to a novel data management which is based on semantic integrated data. The PMD data acquisition pipeline (DAP), which is fueled by traditional, diverse data formats, and a pipeline applying an electronic laboratory notebook (ELN) as data source are displayed. Additionally, the efficient combination of diverse datasets originating from different sources is demonstrated by the representation of a use case dealing with the well-known Orowan relation. T2 - 9. Dresdner Werkstoffsymposium CY - Dresden, Germany DA - 16.05.2024 KW - Semantic Data KW - Data Integration KW - Plattform MaterialDigital KW - Demonstrators KW - Electronic Lab Notebook PY - 2024 AN - OPUS4-60102 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ávila Calderón, Luis T1 - Management of Reference Data in Materials Science and Engineering Exemplified for Creep Data of a Single-Crystalline Ni-Based Superalloy N2 - Here we present our research data management (RDM) framework to conceptualize & implement a digital infrastructure for the Generation, Distribution, and Utilization of reference datasets of materials. The documentation of the test data is often incomplete. This concerns, e.g., material’s manufacturing process or chemical composition, or test equipment’s description and its calibration status. Our concept addresses this issue by proposing the implementation of a requirements profile. A crucial aspect of our concept is to reach a community-agreement on the definition of reference data and on the underlying data schema and vocabulary. T2 - MaRDA2025 Virtual Annual Meeting CY - Online meeting DA - 18.02.2025 KW - NFDI MatWerk KW - Referenzdaten KW - Kriechen KW - Datenschema PY - 2025 AN - OPUS4-64858 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ávila Calderón, Luis A1 - Shakeel, Y. A1 - Gedsun, A. A1 - Forti, M. A1 - Hunke, S. A1 - Han, Ying A1 - Hammerschmidt, T. A1 - Aversa, R. A1 - Olbricht, Jürgen A1 - Chmielowski, M. A1 - Stotzka, R. A1 - Bitzek, E. A1 - Hickel, Tilmann A1 - Skrotzki, Birgit T1 - Management of reference data in materials science and engineering exemplified for creep data of a single-crystalline Ni-based superalloy N2 - The identification of process-structure-property relationships of materials inevitably requires the combination of research data from different measurements. Therefore, the concepts related to FAIR (findable, accessible, interoperable, reusable) data handling, increasingly reported in literature, are particularly important in the materials science and engineering domain. However, they have not yet been integrated into a single, overarching methodological framework, particularly for reference data. Here, we introduce such a framework. Our concept covers data generation, documentation, handling, storage, sharing, data search and discovery, retrieval, and usage. Furthermore, we prototypically implement it using a real dataset with creep data of a single-crystal CMSX-6 Ni-based superalloy. The presented implementation is traceable and permanently accessible through open repositories. The individual elements considered in the framework ensure the functionality and usability of the data and, thus, the adherence to the FAIR principles. In conjunction with this, we present a definition for reference data of materials. Our definition underlines particularly the importance of a comprehensive documentation, e.g., on material provenance, data processing procedures, and the software and hardware used, including software-specific input parameters, as these details enable data users or independent parties to assess the quality of the datasets and to reuse and reproduce the results. Reference data that is managed according to the proposed framework can be used to advance knowledge in the materials science and engineering domain, e.g., by identifying new process-structure-property relations. KW - Referenzdaten KW - NFDI-MatWerk KW - Data schema KW - Research Data Management KW - Reference Data PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-625047 DO - https://doi.org/10.1016/j.actamat.2025.120735 VL - 286 SP - 1 EP - 15 PB - Elsevier Inc. AN - OPUS4-62504 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schilling, Markus T1 - Digital Transformation in Materials Science: PMD Core Ontology (PMDco) 3.0 – Patterns & Applications N2 - The digitalization of Materials Science and Engineering (MSE) demands standardized, interoperable approaches for representing complex experimental and simulation data. To address this challenge, the Platform MaterialDigital Core Ontology (PMDco) provides a mid-level semantic framework that bridges high-level ontologies and domain-specific terminologies. PMDco version 3.0, recently released, introduces significant enhancements based on a full alignment with the Basic Formal Ontology (BFO) as standardized in ISO/IEC 21838-2. This alignment ensures conceptual consistency and facilitates integration across heterogeneous data sources while enabling FAIR-compliant workflows. First addressing the idea behind a mid-level ontology in MSE, this presentation emphasizes its role in harmonizing diverse data models and supporting machine-actionable knowledge representation. New features and design patterns introduced in PMDco 3.0 will be highlighted, which strengthen interoperability and provide reusable modeling structures for common MSE concepts. Practical applications and prototype implementations will be discussed. PMDco has been developed through active community involvement and its future evolution relies on continued collaboration and discussion within the MSE community. Participation is strongly encouraged to ensure that PMDco remains relevant, comprehensive, and widely adopted. More information and opportunities to contribute can be found at materialdigital.de and github.com/materialdigital/core-ontology. T2 - VMAP User Forum 2026 CY - Sankt Augustin, Germany DA - 24.02.2026 KW - Semantic Technology KW - Knowledge Graph KW - PMD Core Ontology KW - Semantic Pattern KW - Machine-actionability PY - 2026 AN - OPUS4-65574 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ávila Calderón, Luis A1 - Shakeel, Y. A1 - Schriever, Sina A1 - Gedsun, A. A1 - Forti, M. A1 - Jordan, Hans A1 - Han, Ying A1 - Baer, O. A1 - Aversa, R. A1 - Olbricht, Jürgen A1 - Hammerschmidt, T. A1 - Hickel, T. A1 - Skrotzki, Birgit T1 - NFDI-MatWerk/IUC02 Data schema for creep data of Ni-based superalloys including a comprehensive documentation of test results and metadata N2 - This data schema was developed within the infrastructure use case IUC02: “Framework for curation and distribution of reference datasets” of the consortium NFDI-MatWerk. It intends to define a structured approach for collecting all required information on a creep experiment using the established terminology of the respective test standard ISO 204:2022 and additional terminology agreed upon by the domain experts. The individual entries are grouped according to their content type and sub-summarized under respective headlines, thereby suggesting a basic categorization and a related hierarchy of concepts. This hierarchy can be similarly applied to other test methods and different metallic (and other) materials. In version 1.1 some editorial and formal changes were made. KW - NFDI-MatWerk KW - Digitalisierung KW - Referenzdaten KW - Kriechen KW - Ni-based Superalloys PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-611629 DO - https://doi.org/10.5281/zenodo.11668375 PB - Zenodo CY - Geneva AN - OPUS4-61162 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Beygi Nasrabadi, Hossein A1 - Bauer, Felix A1 - Uhlemann, Patrick A1 - Thärig, Steffen A1 - Rehmer, Birgit A1 - Skrotzki, Birgit T1 - Mechanical testing dataset of cast copper alloys for the purpose of digitalization N2 - This data article presents a set of primary, analyzed, and digitalized mechanical testing datasets for nine copper alloys. The mechanical testing methods including the Brinell and Vickers hardness, tensile, stress relaxation, and low-cycle fatigue (LCF) testing were performed according to the DIN/ISO standards. The obtained primary testing data (84 files) mainly contain the raw measured data along with the testing metadata of the processes, materials, and testing machines. Five secondary datasets were also provided for each testing method by collecting the main meta- and measurement data from the primary data and the outputs of data analyses. These datasets give materials scientists beneficial data for comparative material selection analyses by clarifying the wide range of mechanical properties of copper alloys, including Brinell and Vickers hardness, yield and tensile strengths, elongation, reduction of area, relaxed and residual stresses, and LCF fatigue life. Furthermore, both the primary and secondary datasets were digitalized by the approach introduced in the research article entitled “Toward a digital materials mechanical testing lab” [1]. The resulting open-linked data are the machine-processable semantic descriptions of data and their generation processes and can be easily queried by semantic searches to enable advanced data-driven materials research. KW - FAIR principles KW - Hardness KW - Low-Cycle Fatigue (LCF) KW - Tensile testing KW - Stress relaxation PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-605005 DO - https://doi.org/10.1016/j.dib.2024.110687 SN - 2352-3409 SP - 1 EP - 15 PB - Elsevier BV AN - OPUS4-60500 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Han, Ying A1 - Kruse, Julius A1 - Rosalie, Julian A1 - Radners, J. A1 - von Hartrott, P. A1 - Skrotzki, Birgit T1 - Influence of mean stress and overaging on fatigue life of aluminum alloy EN AW-2618A N2 - Fatigue tests were performed on the forged aluminum alloy EN AW-2618A in the T61 state. Different stress ratios (R = -1, R = 0.1) were selected to study the influence of mean stress on fatigue life. Two overaged states (10 h/230 ◦C, 1000 h/230 ◦C) were also tested to investigate the influence of overaging on fatigue life. Transmission electron microscopy (TEM) was used to characterize the precipitates (S-phase), which are mainly responsible for the strength of the alloy. A fractographic analysis was also performed to determine the failure mode. Overaging reduces the fatigue life compared to the T61 state. The longer the aging time, the lower the fatigue resistance. The reason is the decrease in (yield) strength, which correlates with the radius of the S-phase: the precipitate radius increases by a factor of approximately two for the overaged states compared to the initial state. The analysis of the fracture surfaces showed crack initiation occurs predominantly on the outer surface and is associated with the primary phases. KW - Aluminum alloys KW - Aging KW - Fatigue KW - Microstructure KW - Electron microscopy KW - S-Phase PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-583708 DO - https://doi.org/10.1016/j.msea.2023.145660 SN - 0921-5093 VL - 886 SP - 1 EP - 10 PB - Elsevier B.V. AN - OPUS4-58370 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rehmer, Birgit A1 - Bayram, Faruk A1 - Ávila Calderón, Luis A1 - Mohr, Gunther A1 - Skrotzki, Birgit T1 - Elastic modulus data for additively and conventionally manufactured variants of Ti-6Al-4V, IN718 and AISI 316 L N2 - This article reports temperature-dependent elastic properties (Young’s modulus, shear modulus) of three alloys measured by the dynamic resonance method. The alloys Ti-6Al-4V, Inconel IN718, and AISI 316 L were each investigated in a variant produced by an additive manufacturing processing route and by a conventional manufacturing processing route. The datasets include information on processing routes and parameters, heat treatments, grain size, specimen dimensions, and weight, as well as Young’s and shear modulus along with their measurement uncertainty. The process routes and methods are described in detail. The datasets were generated in an accredited testing lab, audited as BAM reference data, and are hosted in the open data repository Zenodo. Possible data usages include the verification of the correctness of the test setup via Young’s modulus comparison in low-cycle fatigue (LCF) or thermo-mechanical fatigue (TMF) testing campaigns, the design auf VHCF specimens and the use as input data for simulation purposes. KW - Elastic modulus KW - Young's modulus KW - Shear modulus KW - Additive manufacturing KW - AISI 316L KW - IN 718 KW - Ti-6Al-4V KW - Reference data KW - Temperature dependence PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-579716 DO - https://doi.org/10.1038/s41597-023-02387-6 VL - 10 IS - 1 SP - 1 EP - 9 PB - Springer Nature AN - OPUS4-57971 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sonntag, Nadja A1 - Jürgens, Maria A1 - Uhlemann, Patrick A1 - Skrotzki, Birgit A1 - Olbricht, Jürgen T1 - Experimental data from service-like creep-fatigue experiments on grade P92 steel N2 - This article refers to the research article entitled “Creep-Fatigue of P92 in Service-Like Tests with Combined Stress- and Strain-Controlled Dwell Times” [1]. It presents experimental mechanical data from complex service-like creep-fatigue experiments performed isothermally at 620 °C and a low strain amplitude of 0.2 % on tempered martensite-ferritic grade P92 steel. The data sets in text file format provide cyclic deformation (min. and max. stresses) and the total (hysteresis) data of all recorded fatigue cycles for three different creep-fatigue experiments: 1) a standard relaxation fatigue (RF) test with symmetrical dwell times of three minutes introduced at minimum and maximum strain, 2) a fully strain-controlled service-like relaxation (SLR) test combining these three-minute peak strain dwells with a 30-minute dwell in between at zero strain, and 3) a partly stress-controlled service-like creep (SLC) test combining the three-minute peak strain dwells with 30-minute dwells at constant stress. Such service-like (SL) tests with additional long-term stress- and strain-controlled dwell times are non-standard, rare, and expensive, making these data very valuable. They may be used to approximate cyclic softening in the technically relevant range, for the design of complex SL experiments, or for detailed analyses of stress-strain hystereses (e.g., for stress or strain partitioning methods, for the determination of hysteresis energies (work), inelastic strain components, etc.). In addition, the latter analyses may supply important input for advanced parametric lifetime modeling of components under creep-fatigue loading or model calibration parameters. KW - Tempered martensite-ferritic steel KW - Creep KW - Stress relaxation KW - Creep-fatigue KW - Dwell times PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-578407 DO - https://doi.org/10.1016/j.dib.2023.109333 SN - 2352-3409 VL - 49 SP - 1 EP - 9 PB - Elsevier Inc. AN - OPUS4-57840 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Ávila Calderón, Luis T1 - Mechanisches Verhalten von additiv gefertigtem nichtrostendem Stahl X2CrNiMo17-12-2 (AISI 316L) und Vergleich zur konventionell gefertigten Variante T1 - Mechanical behavior of additively manufactured stainless steel X2CrNiMo17-12-2 (AISI 316L) and comparison with a conventionally manufactured variant N2 - Die additive Fertigung (AM) metallischer Werkstoffe ist eine Technologie, die zunehmend Gegenstand von Forschungsaktivitäten und industrieller Anwendung ist. Dennoch steht sie noch vor Herausforderungen, um eine breite Nutzung in sicherheitsrelevanten Anwendungen zu erreichen. Die Hauptgründe für die Verzögerung des technologischen Durchbruchs zugunsten von AM-Metallen gegenüber konventionell hergestellten Varianten sind das Fehlen eines tieferen Verständnisses der Prozess-Struktur-Eigenschafts-Beziehungen und die begrenzte Verfügbarkeit von Daten zu den Materialeigenschaften. In diesem Kontext stellt diese Arbeit einen Beitrag sowohl zum Verständnis der Prozess-Struktur-Eigenschafts-Beziehungen als auch zur Verbesserung der Datenlage von 316L dar, einem häufig als Konstruktionswerkstoff in verschiedenen Hochtemperaturbauteilen verwendeten Werkstoff. Die Arbeit legt den Fokus auf die mittels Laser-Pulverbettschmelzen hergestellte Werkstoffvariante, PBF-LB/M/316L. Eine konventionell hergestellte Variante, HR/316L, wurde auch untersucht. Bei PBF-LB/M/316L wurde zusätzlich der Effekt ausgewählter Wärmebehandlungen ausgewertet. Die Untersuchung umfasste die Charakterisierung der mechanischen Eigenschaften und der Verformungs- und Schädigungsmechanismen bei erhöhten Prüftemperaturen bei LCF und Kriechen, wo die Daten und Wissenslage am spärlichsten ist. Außerdem hat die untersuchte PBF-LB/M/316L-Wersktoffvariante einen geringen Porositätsgrad. Somit hat diese Arbeit die Mikrostruktur stärker in den Fokus genommen als die meisten bisher in der Literatur verfügbaren Studien. Die mechanische Prüfkampagne umfasste Zugversuche zwischen Raumtemperatur und 650 °C, LCF-Versuche zwischen Raumtemperatur und 600 °C sowie Kriechversuche bei 600 °C und 650 °C. In Ermangelung konkreter Richtlinien und Normen wurde die Charakterisierung zumeist anhand der bestehenden internationalen Prüfnormen und Probengeometrien durchgeführt. Aus jedem dieser Prüfverfahren wurden die entsprechenden Festigkeits- und Verformungskennwerte ermittelt. Darüber hinaus wurde mit Hilfe gezielter mikrostruktureller Untersuchungen ein Beitrag zum Verständnis des Zusammenhangs zwischen der Mikrostruktur und den mechanischen Eigenschaften in Bezug auf die Verformungs- und Schädigungsmechanismen geleistet. Die Dehngrenze von PBF-LB/M/316L ist etwa doppelt so hoch wie die von HR/316L und dieser Trend setzt sich mit ansteigender Prüftemperatur fort. Die Bruchdehnung ist bei allen Prüftemperaturen geringer. PBF-LB/M/316L weist über den größten Teil der Ermüdungslebensdauer vor allem bei Raumtemperatur höhere zyklische Spannungen als HR/316L auf. Ausschließlich bei den kleinsten Dehnungs-schwingbreiten sind die Ermüdungslebensdauer ausgeprägt kürzer. Das Wechselverformungsverhalten von PBF-LB/M/316L ist durch eine Anfangsverfestigung gefolgt von einer kontinuierlichen Entfestigung charakterisiert, welche bis zum Auftreten der zum Versagen führenden Entfestigung stattfindet. Die Kriechbruchzeiten und die Dauer jeder Kriechphase sind bei allen Kombinationen von Prüfparametern bei PBF-LB/M/316 kürzer als bei HR/316L. Die Spannungsabhängigkeit von PBF-LB/M/316L ist im Vergleich zu HR/316L geringer und die Duktilität beim Kriechen kleiner. Die minimale Kriechrate wird bei allen geprüften Parameterkombinationen bei deutlich geringeren Kriechdehnungen erreicht. Eine Wärmebehandlung bei 450 °C / 4 h bewirkt keine wesentliche Änderungen der Mikrostruktur und Zugversuchseigenschaften. Eine zusätzliche Wärmebehandlung bei 900 °C / 1 h verursacht eine Abnahme der Dehngrenze des PBF-LB/M/316L. Diese blieb aber immer noch um den Faktor 1,5x höher als bei HR/316L. Die Verformungsmerkmale wurden kaum davon beeinflusst. Bezüglich des Kriechverhaltens hat die Wärmebehandlung bei 900 °C / 1 h längere sekundäre und tertiäre Kriechstadien bewirkt und die Kriechdehnung hat sich signifikant erhöht. Die Bruchbilder unterscheiden sich generell nicht nur aber vor allem mit ansteigender Prüftemperatur, bei der bei PBF-LB/M/316L oft interkristalline Rissbildung beobachtet wurde. Die Zellstruktur trägt als der Hauptfaktor zu den unterschiedlichen mechanischen Eigenschaften im Vergleich zur HR/316L-Variante bei. Darüber hinaus spielen mutmaßlich die Kornmorphologie, die Stapelfehlerenergie und der Stickstoffgehalt eine Rolle. N2 - Metal additive manufacturing (AM) is a technology that is increasingly the subject of research activities and industrial applications. However, it still faces challenges to achieve widespread use in safety-relevant applications. The main reasons for the delay of this technological breakthrough in favor of AM metals over conventionally manufactured variants are the lack of a deeper understanding of process-structure-property relationships and the limited availability of data on material properties. In this context, this work contributes to both achieving a better understanding of process-structure-property relationships and the improvement of data for 316L, an alloy frequently used as a structural material in various high-temperature components. The work focuses on a material variant produced by laser pow-der bed fusion, PBF-LB/M/316L. A conventionally produced variant, HR/316L, was also investigated. For PBF-LB/M/316L, the effect of selected heat treatments was also evaluated. The investigation included the characterization of the mechanical properties and the related deformation and damage mechanisms at elevated test temperatures in LCF and creep, where data and knowledge are scarce. The PBF-LB/M/316L variant studied has a low degree of porosity. Thus, this work is more focused on the microstructure than most studies available in the literature. The mechanical test campaign included tensile tests between room temperature and 650 °C, LCF tests between room temperature and 600 °C, and creep tests at 600 °C and 650 °C. In the absence of concrete guidelines and standards for testing of AM metals, the characterization mostly took place using existing international test standards and specimen geometries. From each of the test methods, corresponding strength, and deformation characteristic values were determined. In addition, targeted microstructural investigations contributed to understanding the relationship between the microstructure and the mechanical properties in terms of deformation and damage mechanisms. The proof stress of PBF-LB/M/316L is about twice that of HR/316L. This trend remains with increasing test temperature. The elongation after fracture is lower at all test temperatures. Regarding LCF, PBF-LB/M/316L exhibits higher cyclic stresses than HR/316L for most of the fatigue life, especially at room temperature. Exclusively at the smallest strain amplitudes, the fatigue lives of PBF-LB/M/316L are markedly shorter than in HR/316L. The cyclic stress-strain deformation behavior of PBF-LB/M/316L features an initial strain hardening followed by a continuous softening, which occurs until the softening leading to failure takes place. The creep rupture times and the duration of each creep stage are shorter for PBF-LB/M/316 than for HR/316L for all combinations of test parameters. The stress dependence of PBF-LB/M/316L is lower, and the creep ductility is smaller compared to HR/316L. The minimum creep rate is reached at significantly lower creep extensions for all parameter combinations tested. A heat treatment at 450 °C / 4 h did not cause significant changes in the microstructure and tensile behavior. An additional heat treatment at 900 °C / 1 h caused a decrease in the proof stress of PBF-LB/M/316L. However, it still remained higher than the one of HR/316L by a factor of 1.5x. The deformation characteristics were hardly affected. Regarding the creep behavior, this latter heat treatment at 900 °C / 1 h caused longer secondary and tertiary creep stages, and the creep strain increased significantly. The fracture characteristics generally differed, which happened not only but especially with increasing test temperature, where intergranular cracking often took place in PBF-LB/M/316L. The cellular structure is considered the main factor contributing to the different mechanical properties compared to the HR/316L variant. In addition, grain morphology, stacking fault energy, and nitrogen content might play a role. KW - AGIL KW - Additive Fertigung KW - Laser-Pulverbettschmelzen KW - Mikrostrukturentwicklung KW - 316L KW - LCF KW - Kriechen KW - Additive Manufacturing KW - Microstructure KW - Mechanical Properties KW - Mechanische Eigenschaften PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-597143 DO - https://doi.org/10.14279/depositonce-19828 SP - 1 EP - 190 CY - Berlin AN - OPUS4-59714 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ávila Calderón, Luis T1 - Low cycle fatigue behavior of DED-L Ti-6AL-4V N2 - Laser powder-based directed energy deposition (DED-L) is a technology that offers the possibility for 3D material deposition over hundreds of layers and has thus the potential for application in additive manufacturing (AM). However, to achieve broad industrial application as AM technology, more data and knowledge about the fabricated materials regarding the achieved properties and their relationship to the manufacturing process and the resulting microstructure is still needed. In this work, we present data regarding the low-cycle fatigue (LCF) behavior of Ti-6Al-4V. The material was fabricated using an optimized DED-L process. It features a low defect population and excellent tensile properties. To assess its LCF behavior two conventionally manufactured variants of the same alloy featuring different microstructures were additionally tested. The strain-controlled LCF tests were carried out in fully reversed mode with 0.3 % to 1.0 % axial strain amplitude from room temperature up to 400°C. The LCF behavior and failure mechanisms are described. For characterization, optical microscopy (OM), scanning electron microscopy (SEM), and micro-computed tomography (µCT) were used. The low defect population allows for a better understanding of the intrinsic material’s properties and enables a fairer comparison against the conventional variants. The fatigue lifetimes of the DED-L material are nearly independent of the test temperature. At elevated test temperatures, they are similar or higher than the lifetimes of the conventional counterparts. At room temperature, they are only surpassed by the lifetimes of one of them. The principal failure mechanism involves multiple crack initiation sites. T2 - Ninth International Conference on Low Cycle Fatigue (LCF9) CY - Berlin, Germany DA - 21.06.2022 KW - AGIL KW - Additive Manufacturing KW - Ti-6Al-4V KW - Low-Cycle-Fatigue KW - Microstructure PY - 2022 AN - OPUS4-55123 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bhadeliya, Ashok A1 - Rehmer, Birgit A1 - Fedelich, Bernard A1 - Olbricht, Jürgen A1 - Skrotzki, Birgit A1 - Jokisch, T. ED - Zimmermann, M. T1 - Rissfortschrittsuntersuchungen an gefügten Nickelbasiswerkstoffen bei hoher Temperatur N2 - In nickelbasierten Superlegierungen, die für Gasturbinenschaufeln verwendet werden, sind bei hohen Betriebstemperaturen und -belastungen Kriechschäden, Ermüdung, Korrosion und Oxi-dation zu beobachten. Die betroffenen Turbinenschaufeln müssen ersetzt oder repariert werden, um Effizienzverluste und ein eventuelles Bauteilversagen zu vermeiden. In letzter Zeit wurden additive Fertigungs- und Lötverfahren für die Reparatur und das Fügen von Nickelbasiswerk-stoffen entwickelt, um die Einschränkungen der traditionellen Reparaturverfahren zu überwinden. Für eine auslegungsrelevante Bewertung des Risswachstumsverhaltens in den Fügezonen, die durch diese neuen Technologien erzeugt werden, sind Rissfortschrittsuntersuchungen erfor-derlich. Entsprechende Untersuchungen an gefügten Proben werden in diesem Beitrag vorge-stellt. Die Rissfortschrittsversuche werden an gefügten SEN-Proben (Single Edge Notch) bei einem Spannungsverhältnis von 0,1 und einer Temperatur von 950 °C durchgeführt. Das Riss-wachstum wird mit der DCPD-Methode (Direct Current Potential Drop) überwacht, und die ge-messenen Potenzialsignale werden anhand der optisch vermessenen Risslänge und einer Finite-Elemente-Analyse kalibriert. Der Spannungsintensitätsfaktor (SIF) für die gefügte SEN-Geometrie wird mit Hilfe von Finite-Elemente-Analysen berechnet. Auf diese Weise können Rissfortschrittskurven aus den experimentellen Daten abgeleitet werden. T2 - Tagung „Werkstoffprüfung 2022“ CY - Dresden, Germany DA - 27.10.2022 KW - Lötverbindung KW - Rissfortschritt KW - SEN-Probe KW - Gefügte Nickelbasislegierungen PY - 2022 SN - 978-3-88355-430-3 VL - 2022 SP - 67 EP - 72 AN - OPUS4-57090 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bhadeliya, Ashok T1 - High temperature fatigue crack growth in nickel-based alloys joined by brazing and additive manufacturing N2 - Nickel-based alloys have been widely used for gas turbine blades owing to their excellent mechanical properties and corrosion resistance at high temperatures. The operating temperatures of modern gas turbines have been increased in pursuit of increased thermal efficiency. Turbine blades are exposed to these high temperatures combined with mechanical stresses, resulting in material damage through creep, fatigue, and other mechanisms. These turbine blades must be regularly inspected and replaced as needed, to prevent the loss of efficiency, breakdown, and catastrophic failure. Repair of the damaged turbine blades is often a more practical and cost-effective option than replacement, as replacement is associated with high costs and loss of material resources. To this end, state-of-the-art repair technologies including different additive manufacturing and brazing processes are considered to ensure efficient repair and optimum properties of repaired components. In any repaired part, materials property-mismatches and/or inner defects may facilitate the crack initiation and propagation and thus reduce the number of load cycles to failure. Therefore, a fundamental understanding of the fatigue crack growth and fracture mechanisms in joining zones is required to enable the prediction of the remaining life of repaired components and to further improve and adapt the repair technologies. Fatigue crack growth experiments have been conducted on SEN (Single Edge Notch) specimens joined via brazing, and pre-sintered Preform (PSP) and multi-materials (casted/printed) specimens layered via additive manufacturing (AM). The experiments were performed at 950 °C and various stress ratios. The crack growth was measured using DCPD (Direct Current Potential Drop) method. The stress intensity factors for joined SEN specimens were calculated using the finite element method and then used to derive the fatigue crack growth curves. Metallographic and fractographic analyses were conducted to get insight into the fracture mechanism. Results show that the experimental technique for fatigue crack growth was successfully adapted and applied for testing joined specimens. Furthermore, the initial tests indicate that the investigated braze filler material provides a lower resistance to crack growth, and bonding defects cause a crack to deviate to the interface of the base material and joining zone. In AM-sandwich specimens, the crack growth rates are significantly reduced when the crack reaches the interface of printed material and casted material. The obtained crack growth data can be used to calibrate a crack growth model, which will further be utilized to predict the remaining life of repaired components. T2 - DGM Arbeitskreis Mechanisches Werkstoffverhalten bei hoher Temperatur im FachausschussWerkstoffverhalten unter mechanischer Beanspruchung CY - Munich, Germany DA - 10.10.2023 KW - Fatigue crack growth KW - Joined nickel-based alloys PY - 2023 AN - OPUS4-60908 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ávila Calderón, Luis T1 - Creep Behavior of Stainless Steel 316L Manufactured by Laser Powder Bed Fusion N2 - This contribution presents the results of an experimental study on the creep behavior of an austenitic 316L stainless steel produced by laser powder bed fusion (PBF-LB/M/316L) with an emphasis on understanding the effects of microstructure on the creep mechanisms. Hot tensile tests and constant force creep tests at 600 °C and 650 °C, X-ray computed tomography, as well as optical and electron microscopy were performed. The produced PBF-LB/M/316L exhibits a low void population (< 0.01 %) resulting from the manufacturing parameters used and which allowed us to understand the effects of other microstructural aspects on creep behavior, e.g., grain morphology and dislocation substructure. A hot‑rolled variant of 316L was also tested as a reference. T2 - International Materials Science and Engineering Congress - MSE 2024 CY - Darmstadt, Germany DA - 24.09.2024 KW - AGIL KW - Additive Fertigung KW - Mikrostruktur KW - Mikrostrukturentwicklung KW - Kriechen KW - Kriechschädigung PY - 2024 AN - OPUS4-61169 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Gesell, Stephan A1 - Fedelich, Bernard A1 - Rehmer, Birgit A1 - Uhlemann, Patrick A1 - Skrotzki, Birgit A1 - Ganesh, R. A1 - Dude, D. P. A1 - Kuna, M. A1 - Kiefer, B. T1 - TMF-Rissverlaufsberechnung für ATL-Heißteile N2 - Die Steigerung der Leistung und des thermodynamischen Wirkungsgrades von Verbrennungsmotoren führt zu erhöhten Anforderungen an die Festigkeit abgasführender Komponenten wie z. Bsp. Abgasturbolader. Als Folge erhöhter thermomechanischer Wechselbeanspruchungen (TMF) im Betrieb kommt es an den mechanisch und/oder thermisch höchst beanspruchten Stellen der Bauteile zur Bildung von Rissen, wodurch die Lebensdauer der Komponenten begrenzt wird. Derzeit werden bei Turboladern heißgehende Bauteile mit detektierten Rissen zumeist prophylaktisch ersetzt, da die weitere Ausbreitung der Risse während des Betriebs nicht vorhergesagt werden kann. Um diese aufwändige und un- ökonomische Praxis zu vermeiden, wurde im vorliegenden Forschungsvorhaben eine rechnerische Bewertungsmethode auf Basis der experimentellen und numerischen Bruchmechanik erarbeitet, mit deren Hilfe bereits in der Auslegungsphase oder während des Betriebs die (restliche) Lebensdauer der abgasführenden Komponenten vorhergesagt werden kann. Damit wird erstmalig die quantitative Vorhersage der Rissentwicklung bei TMF-Beanspruchungsbedingungen unter Berücksichtigung großer zyklischer viskoplastischer Verformungen ermöglicht. Zentrales Ergebnis des Vorhabens ist eine automatisierte Berechnungsprozedur auf der Basis spezieller Finite-Elemente-Techniken (FEM), womit sowohl der Pfad als auch die Größe eines Risses als Funktion der Anzahl der Lastwechsel in Bauteilen unter TMF-Bedingungen berechnet werden kann. Als geeigneter Beanspruchungsparameter zur Bewertung des Rissfortschritts unter TMF wurde die zyklische Rissöffnungsverschiebung ΔCTOD verwendet. Das Werkstoffverhalten des betrachteten austenitischen Gusseisens Ni-Resist D-5S wurde mit einem validierten viskoplastischen, temperaturabhängigen Materialmodell modelliert, das zur Berücksichtigung große Verzerrungen und Rotationen am Riss erweitert wurde. Für die genaue Berechnung des ΔCTOD bei TMF wurden effiziente FEM-Techniken erarbeitet. Zur Simulation der Rissausbreitung wurde ein automatischer FEM-Algorithmus mit inkrementeller adaptiver Neuvernetzung entwickelt, bei dem die Verformungen und inelastischen Zustandsvariablen jeweils vom alten auf das neue Netz übertragen werden. Dieser Algorithmus wurde im Software-Paket ProCrackPlast implementiert, das in Verbindung mit dem kommerziellen FEM-Code Abaqus zur Lösung dreidimensionaler Rissprobleme zur Verfügung steht. Ziel der umfangreichen experimentellen Arbeiten war es, an isothermen LCF und anisothermen TMF-Versuchen mit gekerbten Flachzugproben (SENT) das Risswachstum im Temperaturbereich von 20 °C bis 700 °C zu ermitteln. Mit Hilfe begleitender 2D FEM Simulationen wurden anhand dieser Datenbasis die Rissfortschrittskurven des Werkstoffs unter Anwendung des ΔCTOD-Konzepts bestimmt und in geeigneter, parametrisierter Form den Nutzern zur Verfügung gestellt. Die Versuche an SENT-Proben wurden mit der entwickelten Software ProCrackPlast als 3D Modell simuliert. Der Vergleich der 2D und 3D Simulationen ergab einen systematischen Unterschied im CTOD und CTOD, der mit Hilfe eines Übertragungsfaktors korrigiert wurde. Der Vergleich der 3D Berechnungen mit den Experimenten zeigte eine zufriedenstellende Übereinstimmung der er- reichten Risslänge mit der Zahl der Lastzyklen im gesamten Temperaturbereich, wobei die numerische Prognose meist auf der konservativen / sicheren Seite lag. Die Übertragbarkeit der Ergebnisse der 2D Parameteridentifikation auf 3D Risskonfigurationen mit Mixed-Mode Beanspruchung ist mit zusätzlichen Versagenshypothesen verbunden, die aufgrund fehlender Versuchsdaten im Vorhaben nicht endgültig geklärt werden konnten. Zur Validierung des Gesamtkonzeptes wurden LCF-Proben mit einem bauteil- typischen Oberflächenriss experimentell und numerisch untersucht. In der Simulation konnte die komplexe Form und Größe der Rissentwicklung zufriedenstellend (richtig) vorhergesagt werden. Die Leis- tungsfähigkeit der erarbeiteten rechnerische Bewertungsmethode wurde an weiteren TMF-Beispielen vorgestellt und diskutiert. Die Software ProCrackPlast und die viskoplastische Materialroutine wurden dem Anwenderkreis des Vorhabens zusammen mit einem Nutzer-Handbuch und Verifikationsbeispielen zur Verfügung gestellt. Das Ziel des Forschungsvorhabens ist erreicht worden. KW - Abgasturbolader Heißteile KW - Numerische Simulation KW - Rissverlauf PY - 2023 VL - 1320 SP - 1 EP - 137 PB - Forschungsvereinigung Verbrennungskraftmaschinen (FVV) CY - Frankfurt am Main AN - OPUS4-56960 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bayerlein, Bernd T1 - Towards Interoperability: Digital Representation of a Material Specific Characterization Method N2 - Certain metallic materials gain better mechanical properties through controlled heat treatments. For example, in age-hardenable aluminum alloys, the strengthening mechanism is based on the controlled formation of nanometer sized precipitates, which represent obstacles to dislocation movement. Precise tuning of the material structure is critical for optimal mechanical behavior in the application. Therefore, analysis of the microstructure and especially the precipitates is essential to determine the ideal parameters for the interplay of material and heat treatment. Transmission electron microscopy (TEM) is utilized to identify precipitate types and orientations in a first step. Dark-field imaging (DF-TEM) is often used to image the precipitates and to quantify their relevant dimensions. The present work aims at the digital representation of this material-specific characterization method. Instead of a time-consuming, manual image analysis, an automatable, digital approach is demonstrated. Based on DF-TEM images of different precipitation states of a wrought aluminum alloy, a modularizable digital workflow for quantitative precipitation analysis is presented. The integration of this workflow into a data pipeline concept will also be discussed. Thus, by using ontologies, the raw image data, their respective contextual information, and the resulting output data from the quantitative precipitation analysis can be linked in a triplestore. Publishing the digital workflow and the ontologies will ensure the reproducibility of the data. In addition, the semantic structure enables data sharing and reuse for other applications and purposes, demonstrating interoperability. The presented work is part of two digitization initiatives, the Platform MaterialDigital (PMD, materialdigital.de) and Materials-open-Laboratory (Mat-o-Lab). T2 - MSE 2022 CY - Darmstadt, Germany DA - 27.09.2022 KW - Interoperability KW - Ontology KW - Precipitation Analysis PY - 2022 AN - OPUS4-55892 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Skrotzki, Birgit T1 - Aging processes in precipitation hardened aluminum alloys N2 - The mechanical strength of wrought high-strength aluminum alloys is essentially based on precipitation hardening, possibly in combination with prior forming, e. g. by stretching. Important parameters for achieving an optimum combination of hardness, strength, ductility, toughness, and further properties such as corrosion resistance are age-hardening temperature and time. During thermal (mechanical) treatment, nucleation and growth of precipitates takes place, leading to the desired degree of hardening. In aluminum alloys, precipitation sequences are usually passed through, i. e. a sequence of metastable precipitates is formed before the stable phase can precipitate. The optimum combination of properties is therefore based on a certain (optimum) microstructure, which can, however, change during the use of a component, since the microstructure is not stable. This happens in particular when the operating temperatures are close to the aging temperature and/or the operating times are sufficiently long. An external mechanical load may accelerate the processes. The presentation gives some examples for this. T2 - Materials Science and Engineering Congress MSE 2022 CY - Darmstadt, Germany DA - 27.9.2022 KW - Aluminium alloy KW - Precipitation hardening KW - Aging KW - Degradation PY - 2022 AN - OPUS4-55877 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Agudo Jácome, Leonrado T1 - Low-Cycle Fatigue Behavior of Laser Powder Bed Fused Inconel 718 at Room and High Temperature N2 - The nickel-base superalloy Inconel 718 (IN718) is one of the most commonly used Ni-based superalloys for high temperature structural applications for its remarkable strength, as well as creep, fatigue, and corrosion resistance up to 650 °C. While IN718 has traditionally been employed as cast or wrought material, it is difficult to machine because of its high strength and toughness. The additive manufacturing of IN718 components made by metal AM has thus gained extensive attention to produce expensive near-net shaped components of high-temperature alloys such as IN718, for it saves material and costs in processing and machining steps. Among all metal additive manufacturing (AM) technologies, laser powder bed fusion (PBF-LB/M) is the most widespread, IN718 being one of the most common alloys produced with it. However, high cooling rates associated to the PBF-LB/M process, hinders the primary strengthening phases γ’’ and γ’ to form, as these cooling rates induce a dislocation cellular substructure, at which walls primary Laves phases bind segregating Nb, Ti and Mo. Many of the therefore needed heat-treatment strategies can then promote Laves-phase transformation into the stable δ phase along the cell and grain boundaries. Laves and δ phases, as well as grain-boundary primary carbides may have adverse effects on mechanical properties. The mostly needle-shaped δ phase was namely found to have a detrimental effect on creep rupture life while no direct effect on LCF fatigue life was evident. In this work room- and high-temperature (650 °C) low-cycle fatigue behavior of PBF-LB/M IN718 is investigated in the four-step heat-treated state and compared to wrought IN718. The microstructure of both materials is characterized across length scales via microscopy methods. The fatigue life at room temperature of the PBF-LB/M IN718 material is slightly lower than that for the wrought material, which is reversed at 650 °C. The cyclic stress response for both materials is marked by cyclic softening that is more pronounced at higher test temperatures. Multiple secondary cracks form at high strain amplitudes, at both room and high temperatures. High testing temperatures enhance specially crack formation at the transitions of regions between elongated grains and columns of stacked grains with ripple patterns in the PBF-LB/M material. Additional to this behavior, pronounced crack branching and deflection indicate that the cracks are controlled by sharp micromechanical gradients. T2 - EUROMAT 2025 CY - Granada, Spain DA - 14.09.2025 KW - Additive manufacturing KW - Low-cycle fatigue KW - Microstructural characterization KW - Ni-base superalloy PY - 2025 AN - OPUS4-64354 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Ávila Calderón, Luis A1 - Han, Ying A1 - Matzak, Kathrin A1 - Olbricht, Jürgen A1 - Skrotzki, Birgit T1 - NFDI-MatWerk/IUC02 data schema for elevated temperature tensile data of Ni-based superalloys N2 - Strength characteristics, such as proof strength and tensile strength, of metallic materials are usually measured at room temperature. However, for high-temperature materials, the values at operational temperatures are equally important for analyzing the mechanical behavior of components or for designing purposes. Elevated temperature tensile tests (often referred to as hot tensile tests) generally enable the measurement of the same material parameters as those obtained at room temperature. Typically, tensile and proof strength, elongation after fracture, and reduction of area are analyzed, with the focus often being on proof strength. The attached data schema for elevated temperature tensile tests was developed within the German NFDI-MatWerk initiative (https://nfdi-matwerk.de/). It builds on a previously published creep data schema and follows a reference data methodology that has also been previously outlined. The presented schema constitutes a structured approach for collecting all relevant information on an elevated temperature tensile test experiment. Overall, this development, as defined in the previously published data schema for creep data, aims to provide a comprehensive hierarchical data description that can be implemented in data management platforms (such as electronic laboratory notebooks), facilitate consistent quality assessment across different users and data providers, and promote the alignment of datasets to the FAIR principles by providing easy interoperability and full reusability. The presented schema was initially developed for datasets of Ni-based high-temperature alloys. However, thanks to its modular structure, it can also be applied to tensile tests of various metallic and other materials. Although the focus is on elevated temperature tensile testing, the data schema also offers a solid foundation for documenting room temperature tensile tests. In such cases, an adjustment of the requirement profile might be necessary, and categories or entries specific to mechanical testing at elevated temperatures, such as “temperature-measuring system”, “specified temperature”, or “soaking time”, become irrelevant. Overall, a detailed approach was followed to ensure the collection of all relevant information, including both metadata and test results. This includes, for example, comprehensive descriptions of the material’s manufacturing history and of the laboratory equipment, and basic strength and deformation characteristic values. The resulting data schema aims to support the description and identification of high-quality datasets, which may qualify as reference data of materials. Our current definition of reference data of materials has been published elsewhere. It should be noted, however, that not all research datasets —depending on their origin and purpose— require this full level of detail. Nevertheless, the presented data schema can support data providers in evaluating the completeness and value of their datasets. This version of the data schema covers elevated temperature tensile tests on both single- and polycrystalline specimen materials. The terminology is aligned with DIN EN ISO 6892-1 and DIN EN ISO 6892-2. It is designed to record the use of temperature measurement using thermocouples and the use of contacting extensometer systems. The requirement profile refers to the highest quality class of reference data, taken from calibrated instruments, and which shall enable the following usages: 1. Checking one's own elevated temperature tensile test results on nominally similar material 2. Verification of own testing set-up (e.g., by testing the same or a similar material) 3. Using the data as input data for simulations in the context of design or alloy development KW - NFDI MatWerk KW - Referenzdaten KW - Zugversuch KW - CMSX-6 KW - Datenschema KW - NFDI MatWerk KW - CMSX-6 KW - Data schema KW - Reference data KW - Tensile test PY - 2025 UR - https://doi.org/10.5281/zenodo.17846436 DO - https://doi.org/10.5281/zenodo.17846435 PB - Zenodo CY - Geneva AN - OPUS4-65190 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Jentzsch, Stefan A1 - Stock, Daniel A1 - Häcker, Ralf A1 - Skrotzki, Birgit A1 - Darvishi Kamachali, Reza A1 - Klingbeil, Dietmar A1 - Kindrachuk, Vitaliy T1 - Shear Band Formation with Split Hopkinson Bar Experiments N2 - The essence of dynamic failure is closely linked to dramatic shear deformations which often lead to the formation of adiabatic shear bands (ASB). Under high loading velocities and the subsequent rapid temperature increase, the localization of shear strain is crucial in view of safety issues of systems in mechanical and aircraft engineering, especially with respect to fast rotating components and diverse crash scenarios. In this research, we perform high speed impact tests at the split Hopkinson pressure bar (SHPB) setup and use particular hat-shaped specimen geometries that resemble the stresses and failure conditions at the component level. In the first step, we specify a notched specimen geometry using finite element (FE) simulations to ensure pure shear. Further, quasi-static compressive tests and a series of impact tests at high strain rates of 10^3-10^4 s^-1 are conducted on specimens manufactured from a fine-grain structural steel with the properties of S355. Optical microscopy and electron backscatter diffraction (EBSD) of the sheared zones unveil significant localization to maximal shear strains of about 0.9 accompanied by grain refinement by factors 5 to 14. The displacements across the surface of the specimens are captured with subset-based local digital image correlation (DIC) during the impact time, and serve as an objective to validate a viscoplastic constitutive relationship. More precisely, the deformation distribution is accurately reproduced by the widely recognized Johnson-Cook (JC) model, which features an enhanced description of damage evolution. Thus, combining experimental and characterization techniques, continuum mechanics and reasonable optimization strategies for the identification of model parameters provides an efficient approach for comprehensive insights into the strain localization behaviour and its impact on the mechanical performance of S355 under extreme strain rates and deformations. KW - Adiabatic shear bands KW - Finite element analysis KW - Viscoplastic material modelling KW - Split Hopkinson pressure bar KW - Hat-shaped specimen KW - Johnson–Cook parameter identification PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-613339 DO - https://doi.org/10.1016/j.ijmecsci.2024.109749 VL - 284 SP - 1 EP - 14 PB - Elsevier BV AN - OPUS4-61333 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Eisenbart, Miriam A1 - Hanke, Thomas A1 - Bauer, Felix A1 - Beygi Nasrabadi, Hossein A1 - Junghanns, Kurt A1 - Dziwis, Gordian A1 - Tikana, Ladji A1 - Parvez, Ashak Mahmud A1 - van den Boogaart, Karl Gerald A1 - Sajjad, Mohsin A1 - Friedmann, Valerie A1 - Preußner, Johannes A1 - Ramakrishnan, Anantha Narayanan A1 - Klengel, Sandy A1 - Meyer, Lars‐Peter A1 - Martin, Michael A1 - Klotz, Ulrich Ernst A1 - Skrotzki, Birgit A1 - Weber, Matthias T1 - KupferDigital: Ontology‐Based Digital Representation for the Copper Life Cycle N2 - The copper life cycle comprises numerous stages from the alloy production to the manufacturing and usage of engineered parts until recycling. At each step, valuable data are generated and stored; some are transferred to the subsequent stations. A thorough understanding of the materials’ behavior during manufacturing processes or throughout their product lifetime is highly dependent on a reliable data transfer. If, for example, a failure occurs during the service life, information about the manufacturing route can be of decisive importance for detecting the root cause of the failure. Additionally, the life cycle assessment hinges on the availability of data. Recording and storing interoperable structured data is, therefore, a thriving research field with huge implications for the economic strength of the manufacturing industry. In the KupferDigital project, it is demonstrated how an ontology‐based data space can be utilized not only as an innovative method for storing and providing interoperable life cycle data but also as a means to enable automated data analysis and evaluation, leading to new insights and the creation of new knowledge using semantic data and technologies. This work illustrates how data recorded at different research facilities can be integrated into one single data space, allowing queries across heterogeneous sources. KW - Copper Alloy KW - Ontology KW - Digitalization KW - Data Space KW - Semantic Representation PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-630213 SN - 1527-2648 DO - https://doi.org/10.1002/adem.202401735 VL - 27 IS - 8 SP - 1 EP - 29 PB - Wiley AN - OPUS4-63021 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Skrotzki, Birgit T1 - Interlinking Structured Data about Aging and Fattigue of an Aluminum Alloy N2 - In typical material oriented research projects numerous types and sources of data need to get connected to form the final outcome. The data-structures have to be described in a manner semantically concise enough so that all participants share the meaning and at the same time flexible enough to allow connecting findings and facts that have not been connected before. The present contribution describes the approach that is being taken in a public funded research project with two cooperating research institutes. The aim of the data-management solution is to describe and interlink three main entity types: material entities like a test specimen that is under observation, immaterial entities like a fatigue life model and processes that generate and transform the immaterial and material entities. The shared understanding of what is described by the data is achieved by referring to existing linked data resources. In addition a common thesaurus that is subject to ongoing discussion is used for concepts and terms that need precision beyond publicly available concept descriptions. The data associated with the entities and processes and entities is rather small and well structured. The entities and processes covered by the vocabularies are typical to laboratories performing fatigue testing and microstructure analysis. Through the interlinking of the entities and processes it becomes possible to intuitively understand the knowledge that is accumulating in the database. For example it is easy to trace the history of a creep test specimen starting from the chemical composition that has been analyzed for the heat, continuing with the heat treatment of the material, going into the creep test itself with the associated creep data and finally finding the transmission electron microscopy images that have been taken from the crept sample. The presented approach is prototypical way to tackle the sustainable management of structured open research data. Open questions remain for example with the management of attributions, the acceptance of an increased effort in data creation and the access control to specific regions of the data. On the other hand the approach sketches what added value can be created, if the community adopts and contributes to the linked data principles. T2 - LCF9 CY - Berlin, Germany DA - 21.6.2022 KW - Data management KW - Data linking KW - Thesaurus PY - 2022 AN - OPUS4-55159 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Suarez Ocano, Patricia T1 - Influence of heat-treatment-induced microstructural evolution on the Low Cycle Fatigue behavior of 316L stainless steel fabricated by Laser Powder Bed Fusion N2 - Additive manufacturing, particularly the laser powder bed fusion (PBF-LB/M) process, has gained significant attention in recent years due to its ability to produce complex geometries with enhanced mechanical properties. Among the various materials used, 316L stainless steel is highly favored for cyclically loaded components due to its exceptional mechanical strength, high-temperature performance, and corrosion resistance, making it widely applicable across various industries. 316L SS fabricated by PBF-LB/M (PBF-LB/M/316L) exhibits a unique hierarchical microstructure, with high density of low-angle grain boundaries (LAGBs), nano-dispersed silicates, chemical micro-segregations, and solidification-induced cellular structures. Particularly, the submicron-sized cellular features enriched with chromium (Cr) and molybdenum (Mo), along with high dislocation densities, contribute to a superior strength-ductility balance compared to conventionally manufactured 316L SS. The dispersed silicate particles act also as a strengthening phase, impeding dislocation movement and enhancing plastic deformation resistance. This study explores the effect of heat treatments on the low-cycle fatigue (LCF) behavior of PBF-LB/M/316L at room temperature (RT) and 600 °C. First, three heat treatment conditions were applied to the as-built material: 450 °C for 4 hours (HT450/4), 800 °C for 3 hours (HT800/3), and 900 °C for 1 hour (HT900/1) to investigate their influence on microstructural evolution. Microstructural analysis revealed that the HT450/4 condition preserved the cellular structure with high dislocation density, while the HT800/3 condition showed partial dissolution of cells together with reduction in segregated elements along the cell walls and a reduced dislocation density. The HT900/1 condition resulted in complete segregation and cellular structure dissolution with comparable dislocation density to HT800/3 while maintaining the crystallographic texture and grain morphology. Intermetallic χ phase was mostly observed at the grain boundaries in HT800/3, but not in HT900/1. Fully reversed LCF tests were conducted under strain-controlled conditions with a strain amplitude of 0.8 %. Tests were interrupted at specific intervals to analyze the interaction between hierarchical microstructural features and deformation mechanisms in the three heat-treated conditions. Due to the pronounced dislocation cell structures and elemental segregation, the microstructure of the HT450/4 condition significantly impact deformation and damage mechanisms during cyclic loading, which in turn, differ from the conventional produced counterparts. The results provide insights into the relationship between microstructural features and fatigue performance, highlighting key deformation and failure mechanisms under cyclic loading. T2 - FEMS 2025 EUROMAT 18th European Congress and Exhibition on Advanced Materials and Processes CY - Granada, Spain DA - 14.09.2025 KW - Additive manufacturing KW - 316L stainless steel KW - Heat treatments KW - Low Cycle Fatigue KW - Microstructure PY - 2025 AN - OPUS4-64238 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schilling, Markus A1 - Skrotzki, Birgit T1 - Full dataset of several mechanical tests on an S355 steel sheet as reference data for digital representations N2 - The dataset provided in this repository comprises data obtained from a series of characterization tests performed to a sheet of typical S355 (material number: 1.0577) structural steel (designation of steel according to DIN EN 10025-2:2019). The tests include methods for the determination of mechanical properties such as, e.g., tensile test, Charpy test and sonic resonance test. This dataset is intended to be extended by the inclusion of data obtained from further test methods. Therefore, the entire dataset (concept DOI) comprises several parts (versions), each of which is addressed by a unique version DOI. The data were generated in the frame of the digitization project Innovationplatform MaterialDigital (PMD) which, amongst other activities, aims to store data in a semantically and machine understandable way. Therefore, data structuring and data formats are focused in addition to aspects in the field of material science and engineering (MSE). Hence, this data is supposed to provide reference data as basis for experimental data inclusion, conversion and structuring (data management and processing) that leads to semantical expressivity as well as for MSE experts being generally interested in the material properties and knowledge. KW - S355 steel sheet KW - Mechanical testing KW - Tensile test KW - Charpy test KW - Microstructure analysis KW - Digital representation KW - Data management KW - Data format PY - 2022 DO - https://doi.org/10.5281/zenodo.6778336 PB - Zenodo CY - Geneva AN - OPUS4-55141 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Jentzsch, Stefan A1 - Stock, Daniel A1 - Häcker, Ralf A1 - Skrotzki, Birgit A1 - Darvishi Kamachali, Reza A1 - Klingbeil, Dietmar A1 - Kindrachuk, Vitaliy T1 - Split Hopkinson Pressure Bar (SHPB) investigations of steel S355 specimens and complementary characterization methods N2 - The workbook SHPB_S355.xlsx contains in the main spreadsheet S355_TestOverview an overview on the S355 specimens, which were tested in Split Hopkinson Pressure Bar (SHPB) and complementary quasi-static (QS) tests. The tests were conducted with notched hat-shaped specimens without a notch offset (S355_TestOverview/column geometry: “no offset”) and a small notch offset of x=0.35 mm (S355_TestOverview/column geometry: “offset”), cf. Fig. 1 [1]. Furthermore, for selected specimens, links are provided to DIC and bar strain measurement files as well as to evaluations from further characterization methods (microhardness, EBSD). For the boundary conditions at the SHPB projectile impact, the pressures of the compressor p, driving the projectile, and the associated projectile impact velocities are provided in SHPB_S355.xlsx. The DIC displacement measurements are provided in FurtherMeasurements/DIC with frame output times in the file labels, which are associated with an imaginary trigger at the left end of the shortened incident bar (length 300 mm), which is considered within the SHPB simulation setup, see [1]. Furthermore, the DIC reference coordinate systems are provided as COS.jpg files in the respective DIC folders. Starting from the strain signals at the bars, captured by strain gauges at the incident (file name BC_Inc) and transmission bar (BC_Trans), displacement boundary conditions (which are provided for the tests in FurtherMeasurements/BarDisplBCs) are calculated by eq. (12) in [1], incorporating the acoustic velocity equal to 4639 m/s at the bars and a correction factor. Fig. 1 shows the shear specimen geometry (lengths in mm) with the offset of the notches x. For the quasi-static tests force(displacements)-values are directly provided in FurtherMeasurements/Fu_curves, which are considered from the relative displacements of the specimens, evaluated by DIC. The Vickers microhardness (HV 0.01) distribution across the shear localization zone was assessed by QNESS 60A+ EVO (DIN EN ISO 6507-1) for quasi-statically and dynamically tested specimens, applying the small notch offset, such that the specimens did not fail in the localization region. Therefore, raw data is provided in FurtherMeasurements/Microhardness. For fitting the microhardness distribution perpendicularly to the shear bands (as i.e. provided for the SHPB specimen in [1]), representative microhardness profiles were considered. Similarly for specimens with the small notch offset, EBSD data on dynamic and quasi-static tests is provided in FurtherMeasurements/EBSD. The grain size distributions for positions at the notch and the undeformed region are included in the subdirectory ./GrainLists_Shortened and EBSD images in the PowerPoint Presentations. Further information as the sizes and misorientations of the single grains, is incorporated in the subfolders ./GrainLists_FurtherInf. KW - Adiabatic shear bands KW - Split Hopkinson pressure bar KW - Digital image correlation PY - 2025 DO - https://doi.org/10.5281/zenodo.17591439 PB - Zenodo CY - Geneva AN - OPUS4-64842 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Jürgens, Maria A1 - Sonntag, Nadja A1 - Olbricht, Jürgen A1 - Fedelich, Bernard A1 - Skrotzki, Birgit T1 - The effect of dwell times on the thermomechanical fatigue life performance of grade P92 steel at intermediate and low strain amplitudes N2 - Results of an extended TMF test program on grade P92 steel in the temperature range of 620 °C - 300 °C, comprising in-phase (IP) and out-of-phase (OP) tests, partly performed with symmetric dwells at Tmax/Tmin, are presented. In contrast to previous studies, the low-strain regime is also illuminated, which approaches flexible operation in a power plant with start/stop cycles. At all strain amplitudes, the material performance is characterized by continuous cyclic softening, which is retarded in tests at lower strains but reaches similar magnitudes in the course of testing. In the investigated temperature range, the phase angle does not affect fatigue life in continuous experiments, whereas the IP condition is more detrimental in tests with dwells. Fractographic analyses indicate creep-dominated and fatigue-dominated damage for IP and OP, respectively. Analyses of the (micro)hardness distribution in the tested specimens suggest an enhanced microstructural softening in tests with dwell times for the low- but not for the high-strain regime. To rationalize the obtained fatigue data, the fracture-mechanics-based D_TMF concept, which was developed for TMF life assessment of ductile alloys, was applied. It is found that the D_TMF parameter correlates well with the measured fatigue lives, suggesting that subcritical growth of cracks (with sizes from a few microns to a few millimeters) governs failure in the investigated range of strain amplitudes. KW - 9-12%Cr steel KW - Thermomechanical fatigue KW - Symmetric dwell periods KW - Low strain KW - Parametric modeling PY - 2021 DO - https://doi.org/10.1016/j.msea.2020.140593 VL - 805 SP - 140593 PB - Elsevier B.V. AN - OPUS4-52374 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bayerlein, Bernd T1 - Digital Transformation in Materials Science:Insights from Platform MaterialDigital N2 - In the digital transformation of materials science and engineering, existing processes are being closely examined to optimize and extend them using technologies such as the Semantic Web, while adhering to the FAIR principles. The challenge is to identify and adapt these technologies to significantly improve daily operations, covering the entire cycle of data generation, collection, storage to its processing and use. This presentation presents different approaches developed within the Platform MaterialDigital (PMD) and related initiatives, each addressing specific challenges of digitalization and demonstrating their benefits. These will be illustrated by a case study on age-hardenable aluminium alloys in different aging states, based on a comprehensive dataset of microstructural and mechanical properties. In this context, ontologies are essential for organizing data into interoperable semantic structures, thereby enabling the representation of concepts and their relationships. The PMD Core Ontology (PMDco) serves as a higher semantic layer that connects domain-specific ontologies [1]. The PMDco provides MSE-specific bridging concepts that enhance data mapping and integration capabilities. This approach facilitates the linking of results from natural language processing of a corpus of microscopy abstracts, which supported the development of a microscopy ontology. In addition, the presentation highlights how modular, digital workflows can improve the reproducibility of transmission electron microscopy image processing and analysis [2]. It also shows how freely available mechanical and microstructural datasets are semantically integrated and made searchable through PMDco, facilitating correlation analysis [3]. Looking ahead, the integration of these components has the potential to advance and sustain MSE practices. T2 - MSE Congress 2024 - Materials Science and Engineering CY - Darmstadt, Germany DA - 24.09.2024 KW - Semantic Interoperability KW - FAIR data management KW - Digtial Representation PY - 2024 AN - OPUS4-61137 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Skrotzki, Birgit T1 - Interconnecting data repositories: The Platform MaterialDigital (BMBF) N2 - Presentation of the Platform MaterialDigital. Presentation of the needs and challenges in materials science and engineering. T2 - 3rd EMMC International Workshop - EMMC CY - Online meeting DA - 02.03.2021 KW - Digitization KW - Standardization KW - Ontology PY - 2021 AN - OPUS4-52247 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Skrotzki, Birgit A1 - Schriever, Sina T1 - BAM reference data - Results of ASTM E139-11 creep tests on a reference material of Nimonic 75 nickel-base alloy N2 - Results of creep tests on a certified reference material at T = 600°C and a tensile creep load of 160 MPa are provided. The evaluated results include the times to reach 2% and 4% creep strain, respectively, and the creep rate after 400 h. The data were audited and are BAM reference data. KW - Reference data KW - Creep KW - Nickel-base alloy KW - Nimonic 75 KW - Reference material BCR-425 PY - 2021 DO - https://doi.org/10.5281/zenodo.5106606 PB - Zenodo CY - Geneva AN - OPUS4-52970 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beygi Nasrabadi, Hossein A1 - Skrotzki, Birgit T1 - Ontology-oriented modeling of the Vickers hardness knowledge graph N2 - This research deals with the development of the Vickers hardness knowledge graph, mapping the example dataset in them, and exporting the data-mapped knowledge graph as a machine-readable Resource Description Framework (RDF). Modeling the knowledge graph according to the standardized test procedure and using the appropriate upper-level ontologies were taken into consideration to develop the highly standardized, incorporable, and industrial applicable models. Furthermore, the Ontopanel approach was utilized for mapping the real experimental data in the developed knowledge graphs and the resulting RDF files were successfully evaluated through the SPARQL queries. T2 - ICMMM 2023: 10th International Conference on Mechanics, Materials and Manufacturing CY - Washington, D.C., USA DA - 18.08.2023 KW - Ontology KW - Knowledge graph KW - Data mapping KW - Vickers hardness KW - FAIR data PY - 2023 AN - OPUS4-58100 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Beygi Nasrabadi, Hossein A1 - Skrotzki, Birgit T1 - Tensile test ontology (TTO) N2 - Tensile Test Ontology (TTO) has developed for representing the Tensile testing process, testing equipment requirements, test pieces charactristics, and related testing parameters and their measurement procedure according to DIN EN ISO 6892-1 standard. Versions info: V2 developed using BFO+CCO top-level ontologies. V3 developed using PROVO+PMDco top-level ontologies. Repositories: GitLab: https://gitlab.com/kupferdigital/process-graphs/tensile-test GitHub: https://github.com/HosseinBeygiNasrabadi/Tensile-Test-Ontology-TTO- MatPortal: https://matportal.org/ontologies/TTO IndustryPortal: https://industryportal.enit.fr/ontologies/TTO KW - Ontology KW - Tensile testing PY - 2024 UR - https://gitlab.com/kupferdigital/process-graphs/tensile-test UR - https://github.com/HosseinBeygiNasrabadi/Tensile-Test-Ontology-TTO- UR - https://matportal.org/ontologies/TTO UR - https://industryportal.enit.fr/ontologies/TTO PB - GitLab CY - San Francisco, CA, USA AN - OPUS4-60545 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ferrari, Bruno A1 - Fantin, Andrea A1 - Said, D. A1 - Fitch, A. N. A1 - Suárez Ocano, Patricia A1 - Mishurova, Tatiana A1 - Roveda, Ilaria A1 - Kromm, Arne A1 - Darvishi Kamachali, Reza A1 - Bruno, Giovanni A1 - Evans, Alexander A1 - Requena, G. A1 - Agudo Jácome, Leonardo A1 - Serrano Munoz, Itziar T1 - The impact of scanning strategy on cell structures in PBF-LB/M/IN718: an in situ synchrotron x-ray diffraction study N2 - In additive manufacturing, any change of the process parameters, such as scanning strategy, directly affects the cooling rates, heat accumulation, and overall thermal history of the build. Consequently, parts built with different process parameters tend to have different levels of crystallographic texture, residual stress, and dislocation density. These features can influence the properties of the material and their development during post-processing operations. In this study, IN718 prisms were built by laser powder bed fusion (PBF-LB/M) using two different scanning strategies (continuous 67° rotations around the build direction, ROT, and alternating 0°/67° scans, ALT) to provide two different as-built conditions. In situ time-resolved synchrotron diffraction was performed during a solution heat treatment at 1027 °C for 1 h. Ex situ scanning electron microscopy was used to support and complement the in situ observations. An approach to quantify the effect of elemental microsegregation at the cell walls is developed based on the deconvolution of asymmetric γ-nickel matrix peaks. Following this approach, the scanning strategies are shown to affect the as-built fraction of cell walls in the material, resulting in a difference of approximately 5 %, in weight fraction, between ROT and ALT (19 % vs. 24 %, respectively). This microsegregation was observed to be rapidly homogenized during the heating ramp, and no significant changes to the peak shape in the γ peaks occurred during the isothermal part of the heat treatment, regardless of the scanning strategy. KW - Additive manufacturing KW - Inconel 718 KW - Synchrotron x-ray diffraction KW - Heat treatment KW - Laser powder bed fusion KW - Cellular microstructure PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-650958 DO - https://doi.org/10.1016/j.jmrt.2025.11.214 SN - 2238-7854 VL - 41 SP - 593 EP - 608 PB - Elsevier B.V. AN - OPUS4-65095 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Evans, Alexander T1 - Ageing behaviour of laser powder bed fused 316L: a powder to failure approach N2 - Laser powder bed fusion (LPBF) is an additive manufacturing process for materials which inherently tends to yield various degrees of metastable hierarchical microstructures, defects and high residual stresses in the as-built condition depending on the process parameters. The understanding of the evolution of these typical features during heat treatment and subsequent thermal and mechanical ageing is crucial for the wider acceptance for safety critical structures. A multi-disciplinary research project at BAM studying the development of the microstructure, defects, residual stresses typical of LPBF 316L and their evolution during thermal and mechanical ageing has led to insights into the stability of these inherent features. This presentation aims to give a broad overview of the project with a few specific cases of investigation. Firstly, the formation of residual stresses, the nature of the initial microstructure, the tensile properties and a modelling approach to understand the anisotropy will be presented. This will be followed by examples of studies of their evolution during heat treatment, long term thermal exposure, and room temperature and high temperature mechanical testing compared to a baseline of conventional wrought variant of the same alloy. T2 - International Conference on Additive Manufacturing 2021 (ICAM 2021) CY - Online meeting DA - 01.11.2021 KW - Ageing KW - Additive manufacturing KW - Laser powder bed fusion KW - AGIL PY - 2021 AN - OPUS4-54106 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -