TY - JOUR A1 - Mosquera Feijoo, Maria A1 - Oder, Gabriele A1 - Saliwan Neumann, Romeo A1 - Buchheim, Michaela A1 - Kranzmann, Axel A1 - Olbricht, Jürgen T1 - Impact of Sample Geometry and Surface Finish on VM12‑SHC Ferritic–Martensitic Steel Under Cyclic Steam Atmosphere Operating Conditions N2 - The steam side oxidation of ferritic–martensitic VM12-SHC steel was investigated under thermo-cyclic conditions in water steam at 620/320 °C and 30 bar with a focus on assessing the influence of pre-oxidation time, specimen geometry and surface finish. The specimens were pre-oxidized under isothermal conditions in water steam at 620 °C and 30 bar for 500 h or 1500 h. After pre-oxidation treatment, all specimens were subjected up to 258 thermal cycles. Three different geometries—rectangular coupons, U-shaped ring segments and ring samples—were investigated to evaluate the influence of open/closed shape, and flat/curved surface on corrosion rate. At the same time, two types of surface finish were considered: “as received” and “ground.” The formation of a protective scale by pre-oxidation was investigated. EBSD and ESMA analyses revealed that the Cr-content of the alloy appeared to be insufficient for obtaining a protective oxide scale under studied conditions, at the same time the anayses confirmed that initial oxidation depends on presence of minor alloying elements as Si and Mn, strong oxide formers which can alter the kinetics and morphology of the corrosion reaction. Moreover, rectangular coupons with small wall thickness and flat surface exhibited the highest corrosion rate, while “ground” curved samples showed only local oxidation. This indicates that for same pre-oxidation time, oxidation kinetics is controlled by curvature. KW - Cyclic steam oxidation KW - 12%Cr steel KW - Specimen geometry KW - Surface treatments PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-551808 DO - https://doi.org/10.1007/s11085-022-10114-6 SN - 0030-770X SP - 1 EP - 18 PB - Springer AN - OPUS4-55180 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mrkwitschka, Paul A1 - Rühle, Bastian A1 - Kuchenbecker, Petra A1 - Löhmann, Oliver A1 - Lindemann, Franziska A1 - Hodoroaba, Vasile-Dan T1 - Embedding and cross-sectioning as a sample preparation procedure for accurate and representative size and shape measurement of nanopowders N2 - Reliable measurement of the size of polydisperse, complex-shaped commercial nanopowders is a difficult but necessary task, e.g., for regulatory requirements and toxicity risk assessment. Suitable methods exist for the accurate characterization of the size of non-aggregated, stabilized, spherical and monodisperse nanoparticles. In contrast, industrial nanoscale powders usually require dedicated sample preparation procedures developed for the analysis method of choice. These nano-powders tend to agglomerate and/or aggregate, a behavior which in combination with an innate broad particle size distribution and irregular shape often significantly alters the achievable accuracy of the measured size parameters. The present study systematically tests two commercially available nanoscale powders using different sample preparation methods for correlative analysis by scanning electron microscopy, dynamic light scattering, Brunauer–Emmet–Teller method and differential mobility analysis. One focus was set on the sample preparation by embedding nanoparticles in carbon-based hot-mounting resin. Literature on this topic is scarce and the accuracy of the data extracted from cross sections of these particles is unclearly stated. In this paper systematic simulations on the deviation of the size parameters of well-defined series of nanoparticles with different shapes from the nominal value were carried out and the contributing factors are discussed. KW - Nanopowder KW - Electron microscopy KW - Sample preparation KW - Cross-sectioning KW - Cerium oxide KW - Zinc oxide PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-593289 DO - https://doi.org/10.1038/s41598-023-51094-0 SN - 2045-2322 VL - 14 SP - 1 EP - 10 PB - Springer Nature CY - London AN - OPUS4-59328 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Murugan, Jegatheesan A1 - Darvishi Kamachali, Reza T1 - High‑throughput investigation of grain boundary segregation landscape in the Fe–Ni–Cr system N2 - Understanding phase stability in multicomponent alloy systems, particularly at internal interfaces, remains a major challenge in materials science. Grain boundary (co-)segregation is a critical factor influencing interfacial stability, often leading to microstructural degradation and safety concerns. In this study, we investigate segregation behavior in the face-centered cubic (FCC) Fe–Ni–Cr alloy system, a foundational system for many steels, superalloys, and high-entropy alloys. CALPHAD-integrated density-based phase-field model is extended to compute the segregation of Fe, Ni, and Cr at grain boundaries as a function of the bulk composition, with the relative GB density serving as a key parameter representing grain boundary character. A high-throughput computational screening is performed across the stable compositional space at 723 K, 1023 K, and 1323 K. The results reveal a rich and temperature-sensitive segregation landscape, with element-specific enrichment and depletion patterns that vary with alloy composition. Notably, opposite segregation trends between Ni and Cr, and frequent co-segregation of Fe and Ni, are observed at lower temperatures. The developed framework captures the coupled effects of temperature, chemical interactions, grain boundary structure, and enthalpy-entropy compensation on segregation and GB phase stability. The origin and implications of these phenomena are discussed in terms of the underlying thermodynamic driving forces. KW - Segregation Engineering KW - Grain boundary segregation KW - Thermodynamics KW - CALPHAD KW - Fe--Ni--Cr alloys PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-646404 DO - https://doi.org/10.1007/s10853-025-11717-5 SN - 1573-4803 SP - 1 EP - 21 PB - Springer Science + Business Media CY - Dordrecht [u.a.] AN - OPUS4-64640 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, Ralf A1 - Behrens, Harald A1 - Ageo-Blanco, Boris A1 - Reinsch, Stefan A1 - Wirth, Thomas T1 - Foaming Species and Trapping Mechanisms in Barium Silicate Glass Sealants N2 - Barium silicate glass powders 4 h milled in CO2 and Ar and sintered in air are studied with microscopy, total carbon analysis, differential thermal Analysis (DTA), vacuum hot extraction mass spectroscopy (VHE-MS), Fourier-transformed infrared (FTIR) spectroscopy, X-ray photoelectron spectroscopy (XPS), and time-of-flight secondary-ion mass spectrometry (TOF-SIMS). Intensive foaming of powder compacts is evident, and VHE studies prove that foaming is predominantly caused by carbonaceous species for both milling gases. DTA Shows that the decomposition of BaCO3 particles mix-milled with glass powders occurs at similar temperatures as foaming of compacts. However, no carbonate at the glass surface could be detected by FTIR spectroscopy, XPS, and TOF-SIMS after heating to the temperature of sintering. Instead, CO2 molecules unable to rotate identified by FTIR spectroscopy after milling, probably trapped by mechanical dissolution into the glass bulk. Such a mechanism or microencapsulation in cracks and particle aggregates can explain the contribution of Ar to foaming after intense milling in Ar atmosphere. The amount of CO2 molecules and Ar, however, cannot fully explain the extent of foaming. Carbonates mechanically dissolved beneath the surface or encapsulated in cracks and micropores of particle aggregates are therefore probably the major foaming source. KW - Milling KW - Foaming KW - Glass powder KW - Sintering PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-531227 DO - https://doi.org/10.1002/adem.202100445 SN - 1438-1656 VL - 24 IS - 6 SP - 2100445-1 EP - 2100445-13 AN - OPUS4-53122 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, Ralf A1 - Waurischk, Tina A1 - Behrens, H. A1 - Deubener, J. T1 - Crack growth in borate and silicate glasses: Stress-corrosion susceptibility and hydrolytic resistance N2 - A double cantilever beam technique in air equipped with ultrasound modulation was used to measure the crack velocity v in borate and silicate glasses. In all glasses v and the stress intensity KI followed the empirical correlation v ~ KIn. Indicated by its smallest KI at v = 1 μm s − 1, KI* = 0.27 MPa m0.5, the silicoborate glass containing 70 mol% B2O3 was found most susceptible to stress-corrosion enhanced crack growth. Contrarily, the sodium calcium magnesium silicate glass appeared least susceptible with KI* = 0.57 MPa m0.5. No clear correlation is evident between KI*, reflecting the stress-corrosion susceptibility, and the hydrolytic resistance for all glasses under study, but values of n obtained from the present study and taken from previous literature for 35 glasses tend to decrease with increasing network modifier ion fraction. Energy dissipation during stress-corrosion enhanced crack propagation is assumed to cause this trend. KW - DCB KW - Alkali and alkaline earth silicate and borate glass KW - Crack growth in air KW - Stress-corrosion KW - Stress intensity PY - 2021 DO - https://doi.org/10.1016/j.jnoncrysol.2020.120414 VL - 551 SP - 120414 PB - Elsevier B.V. AN - OPUS4-51393 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller-Elmau, Johanna A1 - Göbel, Artur A1 - Junge, Paul A1 - Müller, Julian A1 - Rousseau, Tom A1 - Görke, Oliver A1 - Nikasch, Christian A1 - Kiliani, Stefan T1 - Thermal cycling of YAG infiltration and plasma sprayed coatings as environmental barrier coating on ceramic heat shields for use in hydrogen operating gas turbines N2 - Environmental barrier coatings (EBC) are intended to protect alumina ceramic tiles in hot water vapor conditions, enabling gas turbines to operate with higher hydrogen content or even pure hydrogen. For these operating conditions, yttrium aluminum garnet (YAG) promises the highest protection against hydrolysis, which can be applied via atmospheric plasmaspraying (APS). To enhance the protection efficiency, the coating is combined with a prior infiltration of the base material. The obtained design acts as in-depth protection even if the coating exhibits cracks. KW - Thermal shock KW - Thermal cycles KW - Environmental barrier coating (EBC) KW - Water vapor corrosion PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-639829 DO - https://doi.org/10.1016/j.oceram.2025.100837 VL - 23 SP - 1 EP - 7 PB - Elsevier Ltd. AN - OPUS4-63982 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nadammal, Naresh A1 - Mishurova, Tatiana A1 - Fritsch, Tobias A1 - Serrano-Munoz, Itziar A1 - Kromm, Arne A1 - Haberland, C. A1 - Portella, Pedro Dolabella A1 - Bruno, Giovanni T1 - Critical role of scan strategies on the development of microstructure, texture, and residual stresses during laser powder bed fusion additive manufacturing N2 - Laser based powder bed fusion additive manufacturing offers the flexibility to incorporate standard and userdefined scan strategies in a layer or in between the layers for the customized fabrication of metallic components. In the present study, four different scan strategies and their impact on the development of microstructure, texture, and residual stresses in laser powder bed fusion additive manufacturing of a nickel-based superalloy Inconel 718 was investigated. Light microscopy, scanning electron microscopy combined with electron backscatter diffraction, and neutron diffraction were used as the characterization tools. Strong textures with epitaxially grown columnar grains were observed along the build direction for the two individual scan strategies. Patterns depicting the respective scan strategies were visible in the build plane, which dictated the microstructure development in the other planes. An alternating strategy combining the individual strategies in the successive layers and a 67◦ rotational strategy weakened the texture by forming finer microstructural features. Von Mises equivalent stress plots revealed lower stress values and gradients, which translates as lower distortions for the alternating and rotational strategies. Overall results confirmed the scope for manipulating the microstructure, texture, and residual stresses during laser powder bed fusion additive manufacturing by effectively controlling the scan strategies. KW - Additive manufacturing KW - Laser powder bed fusion KW - Nickel-based superalloys KW - Scan strategies KW - Residual stresses KW - Microstructure and texture PY - 2021 DO - https://doi.org/10.1016/j.addma.2020.101792 VL - 38 SP - 1792 PB - Elsevier B.V. AN - OPUS4-51944 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nasr Esfahani, M. A1 - Zare Pakzad, S. A1 - Li, T. A1 - Li, X. A1 - Tasdemir, Z. A1 - Wollschläger, Nicole A1 - Leblebici, Y. A1 - Erdem Alaca, B. T1 - Effect of Native Oxide on Stress in Silicon Nanowires: Implications for Nanoelectromechanical Systems N2 - Understanding the origins of intrinsic stress in Si nanowires (NWs) is crucial for their successful utilization as transducer building blocks in next-generation, miniaturized sensors based on anoelectromechanical systems (NEMS). With their small size leading to ultrahigh-resonance frequencies and extreme surface-to-volume ratios, silicon NWs raise new opportunities regarding sensitivity, precision, and speed in both physical and biochemical sensing. With silicon optoelectromechanical properties strongly dependent on the level of NW intrinsic stress, various studies have been devoted to the measurement of such stresses generated, for example, as a result of harsh fabrication processes. However, due to enormous NW surface area, even the native oxide that is conventionally considered as a benign surface condition can cause significant stresses. To address this issue, a combination of nanomechanical characterization and atomistic simulation approaches is developed. Relying only on low-temperature processes, the fabrication approach yields monolithic NWs with optimum boundary conditions, where NWs and support architecture are etched within the same silicon crystal. Resulting NWs are characterized by transmission electron microscopy and micro-Raman spectroscopy. The interpretation of results is carried out through molecular dynamics simulations with ReaxFF potential facilitating the incorporation of humidity and temperature, thereby providing a close replica of the actual oxidation environment - in contrast to previous dry oxidation or self-limiting thermal oxidation studies. As a result, consensus on significant intrinsic tensile stresses on the order of 100 MPa to 1 GPa was achieved as a function of NW critical dimension and aspect ratio. The understanding developed herein regarding the role of native oxide played in the generation of NW intrinsic stresses is important for the design and development of silicon-based NEMS. KW - Nanoelectromechanical systems (NEMS) KW - Silicon nanowires KW - Native oxide KW - Intrinsic stress KW - Raman spectroscopy PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-560471 DO - https://doi.org/10.1021/acsanm.2c02983 SN - 2574-0970 VL - 5 SP - 13276 EP - 13285 PB - ACS Publ. CY - Washington, DC AN - OPUS4-56047 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nawaz, Q. A1 - Blaeß, Carsten A1 - Mueller, Ralf A1 - Boccaccini, A.R. T1 - Processing and cytocompatibility of Cu-doped and undoped fluoride-containing bioactive glasses N2 - Sintered or additive-manufactured bioactive glass (BG) scaffolds are highly interesting for bone replacement applications. However, crystallization often limits the high-temperature processability of bioactive glasses (BGs). Thus, the BG composition must combine high bioactivity and processability. In this study, three BGs with nominal molar (%) compositions 54.6SiO2-1.7P2O3-22.1CaO-6.0Na2O-7.9K2O-7.7MgO (13–93), 44.8SiO2-2.5P2O3-36.5CaO-6.6Na2O-6.6K2O-3.0CaF2 (F3) and 44.8SiO2-2.5P2O3-35.5CaO-6.6Na2O-6.6K2O-3.0CaF2-1.0CuO (F3–Cu) were investigated. The dissolution and ion release kinetics were investigated on milled glass powder and crystallized particles (500–600 μm). All glasses showed the precipitation of hydroxyapatite (HAp) crystals after 7 days of immersion in simulated body fluid. No significant differences in ion release from glass and crystalline samples were detected. The influence of surface roughness on cytocompatibility and growth of preosteoblast cells (MC3T3-E1) was investigated on sintered and polished BG pellets. Results showed that sintered BG pellets were cytocompatible, and cells were seen to be well attached and spread on the surface after 5 days of incubation. The results showed an inverse relation of cell viability with the surface roughness of pellets, and cells were seen to attach and spread along the direction of scratches. KW - Bioactive glass KW - Crystallization KW - Solubility KW - Cytocompatibility KW - Surface roughness PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-598257 DO - https://doi.org/10.1016/j.oceram.2024.100586 SN - 2666-5395 VL - 18 SP - 1 EP - 8 PB - Elsevier Ltd. AN - OPUS4-59825 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Neumann, Christian A1 - Thore, Johannes A1 - Clozel, Mélanie A1 - Günster, Jens A1 - Wilbig, Janka A1 - Meyer, Andreas T1 - Additive manufacturing of metallic glass from powder in space N2 - Additive manufacturing of metals – and in particular building with laser-based powder bed fusion – is highly flexible and allows high-resolution features and feedstock savings. Meanwhile, though space stations in low Earth orbit are established, a set of visits to the Moon have been performed, and humankind can send out rovers to explore Venus and Mars, none of these milestone missions is equipped with technology to manufacture functional metallic parts or tools in space. In order to advance space exploration to long-term missions beyond low Earth orbit, it will be crucial to develop and employ technology for in-space manufacturing (ISM) and in-situ resource utilisation (ISRU). To use the advantages of laser-based powder bed fusion in these endeavours, the challenge of powder handling in microgravity must be met. Here we present a device capable of building parts using metallic powders in microgravity. This was proven on several sounding rocket flights, on which occasions Zr-based metallic glass parts produced by additive manufacturing in space were built. The findings of this work demonstrate that building parts using powder feedstock, which is more compact to transport into space than wire, is possible in microgravity environments. This thus significantly advances ISRU and ISM and paves the way for future tests in prolonged microgravity settings. KW - Metallic Glass KW - Additive Manufacturing KW - Space PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-600667 DO - https://doi.org/10.1038/s41526-023-00327-7 VL - 9 SP - 1 EP - 9 PB - Springer Nature AN - OPUS4-60066 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nolze, Gert A1 - Tokarski, T. A1 - Cios, G. A1 - Winkelmann, A. T1 - Manual measurement of angles in backscattered and transmission Kikuchi diffraction patterns N2 - A historical tool for crystallographic analysis is provided by the Hilton net, which can be used for manually surveying the crystal lattice as it is manifested by the Kikuchi bands in a gnomonic projection. For a quantitative analysis using the Hilton net, the projection centre as the relative position of the signal source with respect to the detector plane needs to be known. Interplanar angles are accessible with a precision and accuracy which is estimated to be ≤0.3o. Angles between any directions, e.g. zone axes, are directly readable. Finally, for the rare case of an unknown projection-centre position, its determination is demonstrated by adapting an old approach developed for photogrammetric applications. It requires the indexing of four zone axes [uvw]i in a backscattered Kikuchi diffraction pattern of a known phase collected under comparable geometric conditions. KW - Electron backscatter diffraction KW - EBSD KW - Angle measurement KW - Gnomonic projections KW - Kikuchi patterns PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-507625 DO - https://doi.org/10.1107/S1600576720000692 VL - 53 SP - 435 EP - 443 AN - OPUS4-50762 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nolze, Gert A1 - Tokarski, T. A1 - Rychlowski, L. T1 - Use of electron backscatter diffraction patterns to determine the crystal lattice. Part 1. Where is the Bragg angle? N2 - The derivation of a crystal structure and its phase-specific parameters from a single wide-angle backscattered Kikuchi diffraction pattern requires reliable extraction of the Bragg angles. By means of the first derivative of the lattice profile, an attempt is made to determine fully automatically and reproducibly the band widths in simulated Kikuchi patterns. Even under such ideal conditions (projection centre, wavelength and lattice plane traces are perfectly known), this leads to a lattice parameter distribution whose mean shows a linear offset that correlates with the mean atomic number Z of the pattern-forming phase. The consideration of as many Kikuchi bands as possible reduces the errors that typically occur if only a single band is analysed. On the other hand, the width of the resulting distribution is such that higher image resolution of diffraction patterns, employing longer wavelengths to produce wider bands or the use of higher interference orders is less advantageous than commonly assumed. KW - Bragg angles KW - Kikuchi bands KW - Kikuchi patterns KW - First derivative KW - Lattice parameters PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-573141 DO - https://doi.org/10.1107/S1600576723000134 SN - 0021-8898 VL - 56 IS - Pt. 2 SP - 349 EP - 360 AN - OPUS4-57314 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nolze, Gert A1 - Tokarski, T. A1 - Rychlowski, L. T1 - Use of electron backscatter diffraction patterns to determine the crystal lattice. Part 2. Offset corrections N2 - A band width determination using the first derivative of the band profile systematically underestimates the true Bragg angle. Corrections are proposed to compensate for the resulting offset Δa/a of the mean lattice parameters derived from as many Kikuchi band widths as possible. For dynamically simulated Kikuchi patterns, Δa/a can reach up to 8% for phases with a high mean atomic number Z, whereas for much more common low-Z materials the offset decreases linearly. A predicted offset Δa/a = f(Z) is therefore proposed, which also includes the unit-cell volume and thus takes into account the packing density of the scatterers in the material. Since Z is not always available for unknown phases, its substitution by Zmax, i.e. the atomic number of the heaviest element in the compound, is still acceptable for an approximate correction. For simulated Kikuchi patterns the offset-corrected lattice parameter deviation is Δa/a < 1.5%. The lattice parameter ratios, and the angles α, β and γ between the basis vectors, are not affected at all.1.5%. The lattice parameter ratios, and the angles � , � and � between the basis vectors, are not affected at all. KW - Mean atomic number KW - Kikuchi patterns KW - Lattice parameters KW - Automated Bragg angle determination KW - Lattice parameter determination PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-573153 DO - https://doi.org/10.1107/s1600576723000146 SN - 0021-8898 VL - 56 IS - Pt. 2 SP - 361 EP - 366 AN - OPUS4-57315 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nolze, Gert A1 - Tokarski, T. A1 - Rychlowski, L. T1 - Use of electron backscatter diffraction patterns to determine the crystal lattice. Part 3. Pseudosymmetry N2 - A pseudosymmetric description of the crystal lattice derived from a single wideangle Kikuchi pattern can have several causes. The small size (<15%) of the sector covered by an electron backscatter diffraction pattern, the limited precision of the projection centre position and the Kikuchi band definition are crucial. Inherent pseudosymmetries of the crystal lattice and/or structure also pose a challenge in the analysis of Kikuchi patterns. To eliminate experimental errors as much as possible, simulated Kikuchi patterns of 350 phases have been analysed using the software CALM [Nolze et al. (2021). J. Appl. Cryst. 54, 1012–1022] in order to estimate the frequency of and reasons for pseudosymmetric crystal lattice descriptions. Misinterpretations occur in particular when the atomic scattering factors of non-equivalent positions are too similar and reciprocal-lattice points are systematically missing. As an example, a pseudosymmetry prediction depending on the elements involved is discussed for binary AB compounds with B1 and B2 structure types. However, since this is impossible for more complicated phases, this approach cannot be directly applied to compounds of arbitrary composition and structure. KW - Bravais lattices KW - Pseudosymmetry KW - Lattice point density KW - Ordered/disordered structures KW - Lattice distortion PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-573169 DO - https://doi.org/10.1107/s1600576723000845 SN - 0021-8898 VL - 56 IS - Pt. 2 SP - 367 EP - 380 AN - OPUS4-57316 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nolze, Gert A1 - Tokarski, T. A1 - Rychlowski, L. A1 - Cios, G. A1 - Winkelmann, A. T1 - Crystallographic analysis of the lattice metric (CALM) from single electron backscatter diffraction or transmission Kikuchi diffraction patterns N2 - A new software is presented for the determination of crystal lattice parameters from the positions and widths of Kikuchi bands in a diffraction pattern. Starting with a single wide-angle Kikuchi pattern of arbitrary resolution and unknown phase, the traces of all visibly diffracting lattice planes are manually derived from four initial Kikuchi band traces via an intuitive graphical user interface. A single Kikuchi bandwidth is then used as reference to scale all reciprocal lattice point distances. Kikuchi band detection, via a filtered Funk transformation, and simultaneous display of the band intensity profile helps users to select band positions and widths. Bandwidths are calculated using the first derivative of the band profiles as excess-deficiency effects have minimal influence. From the reciprocal lattice, the metrics of possible Bravais lattice types are derived for all crystal systems. The measured lattice parameters achieve a precision of <1%, even for good quality Kikuchi diffraction patterns of 400 x 300 pixels. This band-edge detection approach has been validated on several hundred experimental diffraction patterns from phases of different symmetries and random orientations. It produces a systematic lattice parameter offset of up to ±4%, which appears to scale with the mean atomic number or the backscatter coefficient. KW - Electron backscatter diffraction KW - Kikuchi patterns KW - Lattice parameters KW - Radon transform PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-527076 DO - https://doi.org/10.1107/S1600576721004210 SN - 1600-5767 VL - 54 IS - Pt 3 SP - 1012 EP - 1022 AN - OPUS4-52707 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nolze, Gert A1 - Winkelmann, A. T1 - About the reliability of EBSD measurements: Data enhancement N2 - An extensive set of information about the diffracting volume is carried by EBSD patterns: the crystal lattice, the reciprocal lattice, the crystal structure, the crystal symmetry, the mean periodic number of the diffracting phase, the source point from where it has been projected (projection centre), the crystal orientation, the sample topography (local tilt), the (preparation) quality of defect density of the crystal, and possible pattern overlaps. Some of this information is used regularly in conventional EBSD analyses software while others are still waiting for a more widespread application. Despite the wealth of information available, the accuracy and precision of the data that are presently extracted from conventional EBSD patterns are often well below the actual physical limits. Using a selection of example applications, we will demonstrate the gain in angular resolution possible using relatively low-resolution patterns of approximately 20k pixels in combination with pattern matching (PM) approaches. In this way, fine details in a microstructure can be revealed which would otherwise be hidden in the orientation noise. KW - EBSD KW - Orientation precision KW - Disorientation KW - Grain boundary KW - Phase transformation PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-521618 DO - https://doi.org/10.1088/1757-899X/891/1/012018 VL - 891 SP - 012018 PB - IOP Science AN - OPUS4-52161 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nolze, Gert A1 - Winkelmann, A. A1 - Cios, G. A1 - Tokarski, T. T1 - Tetragonality mapping of martensite in high-carbon steel by EBSD N2 - The locally varying tetragonality in martensite grains of a high-carbon steel (1.2 mass percent C) was resolved by electron backscatter diffraction (EBSD) with a spatial resolution in the order of 100 nm. Compared to spatially integrating X-ray diffraction, which yielded an average tetragonality fo c/a=1.05, the EBSD measurements in the scanning electron microscope allowed to image a local variation of the lattice papameter ration c/a in the range of 1.02 ≤ c/a ≤ 1.07. The local variation of tetragonality is confirmed by two different EBSD data analysis approaches based on the fitting of simulated to experimental EBSD patterns. The resulting EBSD-based tetragonality maps are pointing to a complex interaction of carbon concentration and local lattice distortions during the formation process of martensitic structures. KW - EBSD KW - Martensite KW - Tetragonal distortion KW - Pattern matching PY - 2021 DO - https://doi.org/10.1016/j.matchar.2021.111040 VL - 175 SP - 111040 PB - Elsevier Inc. AN - OPUS4-52343 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Orlov, Nikolai A1 - Kiseleva, A. K. A1 - Milkini, P. A. A1 - Evdokimov, P. V. A1 - Putlayev, V. I. A1 - Günster, Jens T1 - Potentialities of Reaction Sintering in the Fabrication of High-Strength Macroporous Ceramics Based on Substituted Calcium Phosphate N2 - Calcium alkali metal (potassium and sodium) double and triple phosphates have been synthesized in different ways. Was for the first time used reaction sintering to produce ceramics based on calcium alkali metal mixed phosphates and investigated the densification behavior of mixed phosphate-based multiphase materials during sintering by this method. Was presented the microstructure of polished surfaces of sintered samples differing in phase composition and determined the density of ceramics prepared using reaction mixtures differing in composition. The effect of reaction sintering on the porosity of the ceramics has been assessed. Using stereolithographic printing and reaction sintering, was produced macroporous mixed Calcium phosphate-based ceramic implants. Their compressive strength has been determined to be 0.78 ± 0.21 MPa for two-phase samples and 1.02 ± 0.13 MPa for three-phase samples. KW - Reaction Sintering KW - Bio Ceramics PY - 2020 DO - https://doi.org/10.1134/s0020168520120146 VL - 56 IS - 12 SP - 1298 EP - 1306 PB - Pleiades Publishing LTD AN - OPUS4-52004 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pan, Z. A1 - Waurischk, Tina A1 - Duval, A. A1 - Müller, Ralf A1 - Deubener, J. A1 - Krishnan, N. M. A. A1 - Wondraczek, K. A1 - Wondraczek, L. T1 - Precise Real‐Time Measurement of Liquid Viscosity Using Digital Video Data N2 - Quantitative knowledge of liquid viscosity is of fundamental importance in many areas of materials synthesis and processing. However, the determination of viscosity often relies on specialized experimental equipment, offline experimentation, or invasive procedures, in particular when required in extreme conditions such as at high temperature, high pressure, and in confined or corrosive environments. Here, this study proposes and validates a fast and simple method that mimics the intuitive perception of liquid flow within a quantitative framework. For this, this study employs digital video observation to derive quantitative values of the shear viscosity of liquids, with high precision and rapid acquisition rates. The technique involves capturing liquid dynamics after minor mechanical stimulation. Processed imaging data are indexed by similarity and referenced to a digital database generated with a finite element model, from which values of viscosity are obtained in line. The approach is tested on water at room temperature and on a high‐temperature glass melt. Covering a viscosity range of four orders of magnitude, both yield convincing agreement with tabulated reference data at low computational cost. KW - Image analyses KW - Liquids KW - Materials discovery KW - Similarity analyses KW - Viscosities PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-634606 DO - https://doi.org/10.1002/aisy.202500297 SN - 2640-4567 SP - 1 EP - 12 PB - Wiley AN - OPUS4-63460 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Paskin, A. A1 - Couasnon, T. A1 - Perez, J. P. H. A1 - Lobanov, S. S. A1 - Blukis, R. A1 - Reinsch, Stefan A1 - Benning, L. G. T1 - Nucleation and Crystallization of Ferrous Phosphate Hydrate via an Amorphous Intermediate N2 - The fundamental processes of nucleation and crystallization are widely observed in systems relevant to material synthesis and biomineralization; yet most often, their mechanism remains unclear. In this study, we unravel the discrete stages of nucleation and crystallization of Fe3(PO4)2·8H2O (vivianite). We experimentally monitored the formation and transformation from ions to solid products by employing correlated, time-resolved in situ and ex situ approaches. We show that vivianite crystallization occurs in distinct stages via a transient amorphous precursor phase. The metastable amorphous ferrous phosphate (AFEP) intermediate could be isolated and stabilized. We resolved the differences in bonding environments, structure, and symmetric changes of the Fe site during the transformation of AFEP to crystalline vivianite through synchrotron X-ray absorption spectroscopy at the Fe K-edge. This intermediate AFEP phase has a lower water content and less distorted local symmetry, compared to the crystalline end product vivianite. Our combined results indicate that a nonclassical, hydration-induced nucleation and transformation driven by the incorporation and rearrangement of water molecules and ions (Fe2+ and PO4 3−) within the AFEP is the dominating mechanism of vivianite formation at moderately high to low vivianite supersaturations (saturation index ≤ 10.19). We offer fundamental insights into the aqueous, amorphous-to-crystalline transformations in the Fe2+−PO4 system and highlight the different attributes of the AFEP, compared to its crystalline counterpart. KW - Nucleation KW - Crystallization KW - Vivianite KW - Ferrous phosphate hydrate PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-580696 DO - https://doi.org/10.1021/jacs.3c01494 SN - 0002-7863 VL - 145 IS - 28 SP - 15137 EP - 15151 PB - ACS Publications AN - OPUS4-58069 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Paskin, Alice A1 - Couasnon, Thaïs A1 - Blukis, Roberts A1 - Perez, Jeffrey Paulo H. A1 - Reinsch, Stefan A1 - Roddatis, Vladimir A1 - Syczewski, Marcin A1 - Benning, Liane G. T1 - Temperature-Induced Phase Transitions of Vivianite: In Situ Analysis of a Redox-Driven Crystallization N2 - We document a solid-state, temperature-dependent (25−700 °C), multistage redox transformation of crystalline ferrous iron phosphate, vivianite (Fe3(PO4)2·8H2O). Under anoxic conditions, vivianite breaks down at T > 250 °C into an anhydrous, amorphous intermediate Fe3(PO4)2 phase, yet the bulk shape and morphology of the starting vivianite crystals were retained. This amorphous intermediate phase remained stable until T > 500 °C, after which a redox-dependent crystallization into two different minerals was observed. Under anoxic conditions, the amorphous ferrous intermediate (Fe3(PO4)2) transformed into the crystalline ferrous phosphate (graftonite, (Fe2+)3(PO4)2), while under oxic conditions it crystallized into a ferric phosphate (rodolicoite, Fe3+PO4). Graftonite formation occurs via an exothermic molar enthalpy (ΔHcryst) of −16.7 ± 0.2 kJ mol−1. Rietveld refinements of the two crystalline endmembers (vivianite and graftonite) revealed a unit cell volume decrease of ∼3.1% during the transformation, which was observed by in situ electron microscopic observations as an overall shrinking of the initial vivianite crystals. Despite volume loss and bubble-like features, the original vivianite shape was preserved, indicating a solid-state pseudomorphic transformation. Ex situ XRD and TEM-EELS analyses confirmed the ferrous-to-ferric oxidation, forming rodolicoite, through changes in the Fe geometry and oxidation state. KW - Vivianite KW - Graftonite KW - Crystallization enthalpy KW - Ferrous phosphates PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-640782 DO - https://doi.org/10.1021/acs.inorgchem.5c02399 SN - 0020-1669 VL - 46 IS - 36 SP - 18227 EP - 18236 PB - American Chemical Society (ACS) AN - OPUS4-64078 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Paulisch-Rinke, M. C. A1 - Manzoni, Anna Maria A1 - Agudo Jácome, Leonardo A1 - Vogel, F. A1 - Reimers, W. T1 - Influence of chemical composition on microstructure and mechanical properties in the extruded aluminum alloys 7021B and 7175 N2 - The aim of this study is to improve the mechanical properties of Al 7xxx series alloys by achieving the strengthening benefits typically provided by Cu while avoiding the formation of low-melting eutectic phases associated with excessive Cu content. This is accomplished through a tailored combination of alloying elements and optimized thermomechanical treatments. Alloys 7021B (high Zn content) and 7175 (high Cu and Mg content) are analyzed and optimized threefold in this study: the heat treatment, the microstructural evolution and the mechanical properties are investigated by several methods and compared with the aim of improving the process parameters for subsequent application. The peak-aging process is optimized via compression tests to overcome the strength-ductility trade-off. Microstructure and phase chemistry analyses by transmission electron microscopy and atom probe tomography enable a better understanding of the underlying morphological features such as the spatial distribution, and the chemical composition of the hardening phases. The mechanical properties of the peak-aged alloys are determined by compression and tensile tests. Both alloys exhibit very high strength – even by 7xxx series standards. It can be traced back to the dislocation movement: it is impeded both by homogeneously distributed cuttable Guinier–Preston zones in both alloys and by non-cuttable η’ precipitates. As a result, we demonstrate that alloy 7021B offers novel possibilities for processing and industrial application: high strength, typically associated with Cu containing alloys, can also be obtained in Cu free alloys, if the Zn content is sufficiently high. We can thus suggest new opportunities for processing and industrial applications by reducing the risk of forming low-melting eutectic phases. KW - Aluminium alloys KW - Transmission electron microscopy KW - Atom probe tomography KW - Extrusion KW - Mechanical properties PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-640338 DO - https://doi.org/10.1016/j.matdes.2025.114649 SN - 0264-1275 VL - 258 SP - 1 EP - 11 PB - Elsevier Ltd. AN - OPUS4-64033 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Paulus, Daniel A1 - Bresch, Sophie A1 - Moos, Ralf A1 - Schönauer-Kamin, Daniela T1 - Powder aerosol deposited calcium cobaltite as textured P-type thermoelectric material with power factors approaching single crystal values N2 - In this work, the thermoelectric material calcium cobaltite Ca3Co4O9 (CCO), a promising p-type conducting thermoelectric oxide with anisotropic properties, was processed by the powder aerosol deposition method (PAD) to form a dense ceramic CCO film with a thickness in the µm range. The prepared films were characterized regarding their microstructure and thermoelectric properties between room temperature and 900 °C. After heat treatment at 900 °C, the CCO PAD film in-plane shows excellent properties in terms of electrical conductivity (280 S/cm at 900 °C) and Seebeck coefficient (220 µV/K at 900 °C). The calculated power factor in-plane (ab) reaches with 1125 µW/(m K2) 40 % of the single crystal value, surpassing the known-properties of CCO bulk ceramics. Examination of the microstructure shows a strong fiber texture of the film as well as a strong coarsening of the grains during the first heat treatment up to 900 °C. KW - thermoelectrics KW - calcium cobaltite KW - thermoelectric oxide KW - aerosol deposition method (ADM) PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-606246 DO - https://doi.org/10.1016/j.jeurceramsoc.2024.116717 SN - 0955-2219 VL - 44 IS - 15 SP - 1 EP - 8 PB - Elsevier BV AN - OPUS4-60624 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pauw, Brian Richard A1 - Smales, Glen Jacob A1 - Anker, A. S. A1 - Annadurai, V. A1 - Balazs, D. M. A1 - Bienert, Ralf A1 - Bouwman, W. G. A1 - Breßler, Ingo A1 - Breternitz, J. A1 - Brok, E. S. A1 - Bryant, G. A1 - Clulow, A. J. A1 - Crater, E. R. A1 - De Geuser, F. A1 - Del Giudice, A. A1 - Deumer, J. A1 - Disch, S. A1 - Dutt, S. A1 - Frank, K. A1 - Fratini, E. A1 - Garcia, P. R. A. F. A1 - Gilbert, E. P. A1 - Hahn, Marc Benjamin A1 - Hallett, J. A1 - Hohenschutz, M. A1 - Hollamby, M. A1 - Huband, S. A1 - Ilavsky, J. A1 - Jochum, J. K. A1 - Juelsholt, M. A1 - Mansel, B. W. A1 - Penttilä, P. A1 - Pittkowski, R. K. A1 - Portale, G. A1 - Pozzo, L. D. A1 - Rochels, L. A1 - Rosalie, Julian A1 - Saloga, Patrick E. J. A1 - Seibt, S. A1 - Smith, A. J. A1 - Smith, G. N. A1 - Spiering, G. A. A1 - Stawski, Tomasz M. A1 - Taché, O. A1 - Thünemann, Andreas A1 - Toth, K. A1 - Whitten, A. E. A1 - Wuttke, J. T1 - The human factor - Results of a small-angle scattering data analysis round robin N2 - A round-robin study has been carried out to estimate the impact of the human element in small-angle scattering data analysis. Four corrected datasets were provided to participants ready for analysis. All datasets were measured on samples containing spherical scatterers, with two datasets in dilute dispersions and two from powders. Most of the 46 participants correctly identified the number of populations in the dilute dispersions, with half of the population mean entries within 1.5% and half of the population width entries within 40%. Due to the added complexity of the structure factor, far fewer people submitted answers on the powder datasets. For those that did, half of the entries for the means and widths were within 44 and 86%, respectively. This round-robin experiment highlights several causes for the discrepancies, for which solutions are proposed. KW - Round Robin KW - Data analysis KW - Small-angle scattering KW - Nanomaterials KW - Interlaboratory comparability KW - Nanostructure quantification KW - Methodology KW - MOUSE PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-587091 DO - https://doi.org/10.1107/S1600576723008324 SN - 1600-5767 VL - 56 IS - 6 SP - 1618 EP - 1629 PB - Wiley-Blackwell CY - Oxford AN - OPUS4-58709 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pavasarytė, Lina A1 - Azevedo do Nascimento, Allana A1 - Cysne Barbosa, Ana Paula A1 - Trappe, Volker A1 - Melo, Daniel T1 - Effects of particle size and particle concentration of poly (ethylene-co-methacrylic acid) on properties of epoxy resin N2 - Self-healing polymers have been developed to improve durability and reduce costs associated with maintenance during service. The addition of thermoplastics to thermosets to produce mendable polymers appears as a promising selfhealing technique. In this study, poly (ethylene-co-methacrylic acid) (EMAA) was added to epoxy resin and the effects of EMAA addition on epoxy properties were evaluated. Specimens with two different contents of thermoplastic and particles sizes were manufactured. A two-level full factorial experimental design was used to evaluate the effect of particle size and particle content on properties of epoxy modified with addition of EMAA. Tensile tests and dynamic mechanical analysis (DMA) were used and the evaluated responses were tensile strength, modulus of elasticity, and glass transition temperature (Tg). X-ray computed tomography (XCT) was used to investigate particle size and concentration after manufacturing. It was found that the particle concentration has greater effects on stress–strain behavior of epoxy while Tg was not significantly affected by neither of the analyzed entrance variables. KW - Fracture KW - Self-healing KW - Epoxy KW - Thermoplastic PY - 2024 DO - https://doi.org/10.1002/app.55677 SN - 0021-8995 SP - 1 EP - 14 PB - Wiley online library AN - OPUS4-60205 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pereira, Raíssa Monteiro A1 - Lohbauer, Ulrich A1 - Schulbert, Christian A1 - Göken, Mathias A1 - Wurmshuber, Michael A1 - Campos, Tiago Bastos Moreira A1 - Thim, Gilmar Patrocínio A1 - Mieller, Björn A1 - Belli, Renan T1 - Instantiations of Multiscale Kinship in Pressing‐Defect Distributions in Yttria‐Stabilized Zirconias by Powder Partitioning N2 - Modern dry pressing of ceramic powders using spray‐dried granulates cannot avoid the occurrence of defects related to persisting inter‐ and intra‐granulate interstitial voids. These constitute the parent defect size population limiting the application of polycrystalline ceramics in high‐stress conditions. The mitigation of such defects could widen the range of application in technical and biomedical engineering, reduce the safety range for design, and extend the lifetime of components. Herein, the Weibull size‐effect on strength in size‐partitioned Yttria‐stabilized zirconias (YSZ) feedstocks is used to explore the viability of changing the density distribution of granulate sizes as an effective strategy to obtain a denser particle packing that could reduce the size distribution of strength‐limiting pressing defects. In a direct assessment of critical defect size using multiscale strength testing with a dataset of ≈1300 values, the success of such an approach in increasing the strength reliability for small volume components is demonstrated, along with its ultimate failure in altering the defect size distribution in sintered YSZ ceramics across several length scales. Finally, it is shown that granule morphology (spherical or dimpled) fails to affect the defect density and size distribution in YSZ ceramics. KW - Zirconia KW - Strength KW - Toughness KW - Weibull distribution KW - Defect population PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-602697 DO - https://doi.org/10.1002/adem.202400139 SN - 1438-1656 SP - 1 EP - 17 PB - Wiley VHC-Verlag AN - OPUS4-60269 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Petrushin, N. V. A1 - Epishin, A. I. A1 - Svetlov, I. L. A1 - Nolze, Gert A1 - Elyutin, E. S. A1 - Solov'ev, A. E. T1 - Influence of the Sign of the γ/γ' Misfit on the Structure and Creep Strength of Single Crystals of Nickel-Based Superalloys N2 - Using the method of directional solidification, single crystals of experimental nickel-based superalloys with negative, zero, and positive γ/γ' misfits are obtained. The γ' solvus, solidus, and liquidus temperatures of the alloys are determined, and the microstructures of the alloys after directional solidification, heat treatment, and creep tests are investigated. Creep tests are performed at temperatures of 800 and 1000°C. It is found that single crystals of the alloy with a negative γ/γ' misfit have the highest creep resistance and lifetime (the crystal lattice period of the γ' phase is smaller than that of the γ matrix). KW - Nickel-based superalloys KW - Single crystal KW - Creep KW - Creep strength KW - Microstructure, γ/γ' misfit PY - 2023 DO - https://doi.org/10.1134/s207511332301029x SN - 2075-1133 VL - 14 IS - 1 SP - 13 EP - 22 AN - OPUS4-59505 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pfennig, A. A1 - Simkin, Roman T1 - Identifying the initial corrosion fatigue failure based on dropping electrochemical potential N2 - The corrosion fatigue of duplex stainless-steel X2CrNiMoN22-5-3 can be determined by purely alternating axial cyclic load to failure using hour-glass shaped specimens. The experimental setup comprises a corrosion chamber allowing for the circulation of an aquifer electrolyte heated to 369 K simulating a carbon capture and storage as well as geothermal power plant environment. During engineering of a carbon storage site or geothermal power plant, it may be crucial to determine the failure onset of a component beforehand. Therefore, an algorithm with 93.3% reliability was established based on splitting the measured potential values into ten time series with a capacity of ten values. The failure of corrosion fatigue specimens in a geothermal environment correlates to the drop of the curves of the electrochemical potential which is measured simultaneously within the corrosion chamber. Crack initiation was, therefore, successfully derived from the electrochemical potential. KW - Corrosion fatigue KW - Surface corrosion KW - CO2 KW - Crack initiation KW - Geothermal energy production PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-629310 DO - https://doi.org/10.3390/app15010403 SN - 2076-3417 VL - 15 IS - 1 SP - 1 EP - 15 PB - MDPI CY - Basel AN - OPUS4-62931 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pfennig, Anja A1 - Mohring, Wencke A1 - Wolf, Marcus T1 - The insignificant improvement of corrosion and corrosion fatigue behavior in geothermal environment applying Boehmit coatings on high alloyed steels N2 - The efficacy of alumina-sol based coatings in a water-free atmosphere at high temperatures suggests a potential solution for enhancing the corrosion resistance of high-alloyed steels in Carbon Capture and Storage (CCS) environments. In this study, coupons of X20Cr13, designed for use as injection pipes with 13% Chromium and 0.20% Carbon (1.4021, AISI 420), were sol-gel coated with water and ethanol-based alumina. These coated coupons were then exposed to CO2-saturated saline aquifer water, simulating conditions in the Northern German Basin, for 1000 h at ambient pressure and 60 °C. Corrosion fatigue experiments were also conducted using specimens of X5CrNiMoCuNb16-4 (1.4542, AISI 630), a suitable candidate for geothermal applications, to assess the impact of the ethanol-based coating on the number of cycles to failure at different stress amplitudes. Unfortunately, the coating exhibited early spallation, resulting in corrosion kinetics and corrosion fatigue data identical to those of uncoated specimens. Consequently, the initially promising Boehmit coating is deemed unsuitable for CCS applications and further research therefore not advisable. KW - Alumina coating KW - High alloyed steel KW - Pitting KW - Surface corrosion KW - CO2 KW - Pipeline KW - Corrosion KW - CCS KW - CO2-storage PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-623786 DO - https://doi.org/10.3390/app14041575 SN - 2076-3417 VL - 14 IS - 4 SP - 1 EP - 12 PB - MDPI CY - Basel AN - OPUS4-62378 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pfennig, Anja A1 - Wolf, M. A1 - Kranzmann, Axel T1 - Corrosion and Corrosion Fatigue of Steels in Downhole CCS Environment—A Summary N2 - Static immersion tests of potential injection pipe steels 42CrMo4, X20Cr13, X46Cr13, X35CrMo4, and X5CrNiCuNb16-4 at T = 60°C and ambient pressure, as well as p = 100 bar were performed for 700–8000 h in a CO2-saturated synthetic aquifer environment similar to CCS sites in the Northern German Basin (NGB). Corrosion rates at 100 bar are generally lower than at ambient pressure. The main corrosion products are FeCO3 and FeOOH with surface and local corrosion phenomena directly related to the alloy composition and microstructure. The appropriate heat treatment enhances corrosion resistance. The lifetime reduction of X46Cr13, X5CrNiCuNb16-4, and duplex stainless steel X2CrNiMoN22-5-3 in a CCS environment is demonstrated in the in situ corrosion fatigue CF experiments (axial push-pull and rotation bending load, 60°C , brine: Stuttgart Aquifer and NGB, flowing CO2: 30 L/h, +/- applied potential). Insulating the test setup is necessary to gain reliable data. S-N plots, micrographic-, phase-, fractographic-, and surface analysis prove that the life expectancy of X2CrNiMoN22-5-3 in the axial cyclic load to failure is clearly related to the surface finish, applied stress amplitude, and stress mode. The horizontal grain attack within corrosion pit cavities, multiple fatigue cracks, and preferable deterioration of austenitic phase mainly cause fatigue failure. The CF life range increases significantly when a protective potential is applied. KW - Carbon capture and storage KW - Steel KW - High alloyed steel KW - Corrosion KW - Corrosion fatigue KW - CCS PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-523948 DO - https://doi.org/10.3390/pr9040594 VL - 9 IS - 4 SP - 594 PB - MDPI CY - Basel, Switzerland AN - OPUS4-52394 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pinomaa, T. A1 - Lindroos, M. A1 - Jreidini, P. A1 - Haapalehto, M. A1 - Ammar, K. A1 - Wang, Lei A1 - Forest, S. A1 - Provatas, N. A1 - Laukkanen, A. T1 - Multiscale analysis of crystalline defect formation in rapid solidification of pure aluminium and aluminium-copper alloys N2 - Rapid solidification leads to unique microstructural features, where a less studied topic is the formation of various crystalline defects, including high dislocation densities, as well as gradients and splitting of the crystalline orientation. As these defects critically affect the material’s mechanical properties and performance features, it is important to understand the defect formation mechanisms, and how they depend on the solidification conditions and alloying. To illuminate the formation mechanisms of the rapid solidification induced crystalline defects, we conduct a multiscale modelling analysis consisting of bond-order potential-based molecular dynamics (MD), phase field crystal-based amplitude expansion simulations, and sequentially coupled phase field–crystal plasticity simulations. The resulting dislocation densities are quantified and compared to past experiments. The atomistic approaches (MD, PFC) can be used to calibrate continuum level crystal plasticity models, and the framework adds mechanistic insights arising from the multiscale analysis. This article is part of the theme issue ‘Transport phenomena in complex systems (part 2)’. KW - Rapid solidification KW - Crystalline defects KW - Molecular dynamics KW - Phase field crystal KW - Phase field method KW - Crystal plasticity PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-542156 DO - https://doi.org/10.1098/rsta.2020.0319 SN - 1364-503X VL - 380 IS - 2217 SP - 1 EP - 20 PB - Royal Society CY - London AN - OPUS4-54215 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Plarre, Rüdiger A1 - Zocca, Andrea A1 - Spitzer, Andrea A1 - Benemann, Sigrid A1 - Gorbushina, Anna A1 - Li, Y. A1 - Waske, Anja A1 - Funk, Alexander A1 - Wilgig, Janka A1 - Günster, Jens T1 - Searching for biological feedstock material: 3D printing of wood particles from house borer and drywood termite frass N2 - Frass (fine powdery refuse or fragile perforated wood produced by the activity of boring insects) of larvae of the European house borer (EHB) and of drywood termites was tested as a natural and novel feedstock for 3D-printing of wood-based materials. Small particles produced by the drywood termite Incisitermes marginipennis and the EHB Hylotrupes bajulus during feeding in construction timber, were used. Frass is a powdery material of particularly consistent quality that is essentially biologically processed wood mixed with debris of wood and faeces. The filigree-like particles flow easily permitting the build-up of woodbased structures in a layer wise fashion using the Binder Jetting printing process. The Quality of powders produced by different insect species was compared along with the processing steps and properties of the printed parts. Drywood termite frass with a Hausner Ratio HR = 1.1 with ρBulk = 0.67 g/cm3 and ρTap = 0.74 g/cm3 was perfectly suited to deposition of uniformly packed layers in 3D printing. We suggest that a variety of naturally available feedstocks could be used in environmentally responsible approaches to scientific material sciences/additive manufacturing. KW - 3D printing KW - X-ray tomographic KW - SEM micrography KW - Drywood termite PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-521517 DO - https://doi.org/10.1371/journal.pone.0246511 VL - 16 IS - 2 SP - e0246511 AN - OPUS4-52151 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Plichta, T. A1 - Sirjovona, V. A1 - Zvonek, M. A1 - Kalinka, Gerhard A1 - Cech, V. T1 - The Adhesion of Plasma Nanocoatings Controls the Shear Properties of GF/Polyester Composite N2 - High-performance fibre-reinforced polymer composites are important construction materials based not only on the specific properties of the reinforcing fibres and the flexible polymer Matrix but also on the compatible properties of the composite interphase. First, oxygen-free (a-CSi:H) and oxygen-binding (a-CSiO:H) plasma nanocoatings of different mechanical and tribological properties were deposited on planar silicon dioxide substrates that closely mimic E-glass. The nanoscratch test was used to characterize the nanocoating adhesion expressed in terms of critical normal load and work of adhesion. Next, the same nanocoatings were deposited on E-glass fibres, which were used as reinforcements in the polyester composite to affect its interphase properties. The shear properties of the polymer composite were characterized by macro- and micromechanical tests, namely a short beam shear test to determine the short-beam strength and a single fibre push-out test to determine the interfacial shear strength. The results of the polymer composites showed a strong correlation between the short-beam strength and the interfacial shear strength, proving that both tests are sensitive to changes in fibre-matrix adhesion due to different surface modifications of glass fibres (GF). Finally, a strong correlation between the shear properties of the GF/polyester composite and the adhesion of the plasma nanocoating expressed through the work of adhesion was demonstrated. Thus, increasing the work of adhesion of plasma nanocoatings from 0.8 to 1.5 mJ·m−2 increased the short-beam strength from 23.1 to 45.2 MPa. The results confirmed that the work of adhesion is a more suitable parameter in characterising the level of nanocoating adhesion in comparison with the critical normal load. KW - Mechanical properties KW - Plasma nanocoatings KW - Glass fibre KW - Polymer composite KW - Short-beam strength KW - Interfacial shear strength KW - Work of adhesion PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-521844 DO - https://doi.org/10.3390/polym13040593 VL - 13 IS - 4 SP - 593 PB - MDPI CY - Basel,Schweiz AN - OPUS4-52184 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pu, Y. A1 - Lawrence, M. J. A1 - Celorrio, V. A1 - Wang, Q. A1 - Gu, M. A1 - Sun, Z. A1 - Agudo Jácome, Leonardo A1 - Russell, A. E. A1 - Huang, L. A1 - Rodriguez, P. T1 - Nickel confined in 2D earth-abundant oxide layers for highly efficient and durable oxygen evolution catalysts N2 - Low cost, high-efficiency catalysts towards water splitting are urgently required to fulfil the increasing demand for energy. In this work, low-loading (<20 wt%) Ni-confined in layered metal oxide anode catalysts (birnessite and lepidocrocite titanate) have been synthesized by facile ion exchange methodology and subjected to systematic electrochemical studies. It was found that Ni-intercalated on K-rich birnessite (Ni-KMO) presents an onset overpotential (ηonset) as low as 100 mV and overpotential at 10 mA cm−2 (η10) of 206 mV in pH = 14 electrolyte. By combining electrochemical methods and X-ray absorption and emission spectroscopies (XAS and XES), we demonstrate Ni sites are the active sites for OER catalysis and that the Mn3+ sites facilitate Ni intercalation during the ion-exchange process, but display no observable contribution towards OER activity. The effect of the pH and the nature of the supporting electrolyte on the electrochemical performance was also evaluated. KW - Confined catalyst KW - Low-loading KW - Layered manganese oxide KW - Oxygen evolution reaction KW - Transmission electron microscopy (TEM) PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-515027 DO - https://doi.org/10.1039/D0TA04031B SN - 2050-7496 SN - 2050-7488 VL - 8 IS - 26 SP - 13340 EP - 13350 PB - Royal Society of Chemistry CY - London AN - OPUS4-51502 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Qu, R. A1 - Maaß, Robert A1 - Liu, Z. A1 - Tönnies, D. A1 - Tian, L. A1 - Ritchie, R. A1 - Zhang, Z. A1 - Volkert, A. T1 - Flaw-insentive fracture of a micrometer-sized brittle metallic glass N2 - Brittle materials, such as oxide glasses, are usually very sensitive to flaws, giving rise to a macroscopic fracture strength that is much lower than that predicted by theory. The same applies to metallic glasses (MGs), with the important difference that these glasses can exhibit certain plastic strain prior to catas- trophic failure. Here we consider the strongest metallic alloy known, a ternary Co 55 Ta 10 B 35 MG. We show that this macroscopically brittle glass is flaw-insensitive at the micrometer scale. This discovery emerges when testing pre-cracked specimens with self-similar geometries, where the fracture stress does not de- crease with increasing pre-crack size. The fracture toughness of this ultra-strong glassy alloy is further shown to increase with increasing sample size. Both these findings deviate from our classical under- standing of fracture mechanics, and are attributed to a transition from toughness-controlled to strength- controlled fracture below a critical sample size. KW - Metallic glass KW - Fracture toughness KW - Size effect KW - Small-scale PY - 2021 DO - https://doi.org/10.1016/j.actamat.2021.117219 VL - 218 PB - Elsevier Ltd. AN - OPUS4-53097 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rabe, T. A1 - Kalinka, Gerhard A1 - Mieller, Björn T1 - Manufacturing and deformation behavior of alumina and zirconia helical springs at room temperature N2 - Ceramic helical springs with identical dimensions were produced by hard machining from alumina, alumina toughened zirconia (ATZ), and tetragonal zirconia polycrystals (TZP) stabilized with different oxides. According to the results of the spring constant determination under deformation rates of 3 mm/min, the deformation behavior of all ceramic springs obeys to Hook’s law. However, variation of the deformation rate, tests under constant load, and spring recovery behavior revealed differences in the deformation behavior of alumina, TZP, and ATZ springs. Alumina springs exhibited time-independent deformation in all tests. In contrast, anelastic deformation at room temperature was demonstrated in all springs containing TZP. This deformation is completely reversible over a period of several days. Anelastic behavior is particularly pronounced in Y-TZP springs, whereas Ce-TZP springs exhibit comparatively very low but still reliably detectable anelasticity. Oxygen vacancies in the TZP ceramic are considered the most likely explanation for the anelastic behavior of TZP springs at room temperature. KW - Alumina KW - Creep KW - Elastic properties KW - Zirconia PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-571858 DO - https://doi.org/10.1111/jace.19085 SN - 0002-7820 SP - 1 EP - 14 PB - Wiley-Blackwell CY - Oxford [u.a.] AN - OPUS4-57185 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rashidi, Reza A1 - Riechers, Birte A1 - Rosalie, Julian A1 - Maaß, Robert T1 - Annealing-dependent elastic microstructure in a Zr-based metallic glass N2 - In this letter, we demonstrate the robust presence of an elastic microstructure in a Zr-based metallic glass (MG) with a characteristic length-scale of the order of 100 nm. This length scale increases systematically towards the MG surface in differently sized casts, whereas thermal relaxation homogenizes both the internal length-scale gradient and the magnitude of the elastic fluctuations. Strongest changes during relaxation arise in the stiffest parts of the elastic microstructure. These findings indicate that the elastic microstructure emerges due to cooling constraints and may therefore be a microstructural manifestation of the internal residual stresses that arise during MG-solidification. KW - Metallic glass KW - Heterogeneity KW - Elastic microstructure KW - Nanoindentation PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-610962 DO - https://doi.org/10.1016/j.scriptamat.2024.116380 VL - 255 SP - 1 EP - 5 PB - Elsevier B.V. CY - Amsterdam, Niederlande AN - OPUS4-61096 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rehmer, Birgit A1 - Bayram, Faruk A1 - Ávila Calderón, Luis A1 - Mohr, Gunther A1 - Skrotzki, Birgit T1 - Elastic modulus data for additively and conventionally manufactured variants of Ti-6Al-4V, IN718 and AISI 316 L N2 - This article reports temperature-dependent elastic properties (Young’s modulus, shear modulus) of three alloys measured by the dynamic resonance method. The alloys Ti-6Al-4V, Inconel IN718, and AISI 316 L were each investigated in a variant produced by an additive manufacturing processing route and by a conventional manufacturing processing route. The datasets include information on processing routes and parameters, heat treatments, grain size, specimen dimensions, and weight, as well as Young’s and shear modulus along with their measurement uncertainty. The process routes and methods are described in detail. The datasets were generated in an accredited testing lab, audited as BAM reference data, and are hosted in the open data repository Zenodo. Possible data usages include the verification of the correctness of the test setup via Young’s modulus comparison in low-cycle fatigue (LCF) or thermo-mechanical fatigue (TMF) testing campaigns, the design auf VHCF specimens and the use as input data for simulation purposes. KW - Elastic modulus KW - Young's modulus KW - Shear modulus KW - Additive manufacturing KW - AISI 316L KW - IN 718 KW - Ti-6Al-4V KW - Reference data KW - Temperature dependence PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-579716 DO - https://doi.org/10.1038/s41597-023-02387-6 VL - 10 IS - 1 SP - 1 EP - 9 PB - Springer Nature AN - OPUS4-57971 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rhode, Michael A1 - Richter, Tim A1 - Schröpfer, Dirk A1 - Manzoni, Anna Maria A1 - Schneider, M. A1 - Laplanche, G. T1 - Welding of high-entropy alloys and compositionally complex alloys - an overview N2 - High-entropy alloys (HEAs) and compositionally complex alloys (CCAs) represent new classes of materials containing five or more alloying elements (concentration of each element ranging from 5 to 35 at. %). In the present study, HEAs are defined as single-phase solid solutions; CCAs contain at least two phases. The alloy concept of HEAs/CCAs is fundamentally different from most conventional alloys and promises interesting properties for industrial applications (e.g., to overcome the strength-ductility trade-off). To date, little attention has been paid to the weldability of HEAs/CCAs encompassing effects on the welding metallurgy. It remains open whether welding of HEAs/CCAs may lead to the formation of brittle intermetallics and promote elemental segregation at crystalline defects. The effect on the weld joint properties (strength, corrosion resistance) must be investigated. The weld metal and heat-affected zone in conventional alloys are characterized by non-equilibrium microstructural evolutions that most probably occur in HEAs/CCAs. The corresponding weldability has not yet been studied in detail in the literature, and the existing information is not documented in a comprehensive way. Therefore, this study summarizes the most important results on the welding of HEAs/CCAs and their weld joint properties, classified by HEA/CCA type (focused on CoCrFeMnNi and AlxCoCrCuyFeNi system) and welding process. KW - High-entropy alloy KW - Compositionally complex alloy KW - Welding KW - Properties KW - Review PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-527068 DO - https://doi.org/10.1007/s40194-021-01110-6 SP - 1 EP - 15 PB - Springer Nature AN - OPUS4-52706 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Richter, Tim A1 - Schröpfer, Dirk A1 - Rhode, Michael A1 - Boerner, Andreas A1 - Saliwan Neumann, Romeo A1 - Schneider, M. A1 - Laplanche, G. T1 - Influence of machining on the surface integrity of high- and medium-entropy alloys N2 - High- and medium-entropy alloys (HEAs) are a quite new class of materials. They have a high potential for applications from low to high temperatures due to the excellent combination of their structural properties. Concerning their application as components; processing properties, such as machinability, have hardly been investigated so far. Hence, machinability analyses with a focus on the influence of the milling process and its basic parameters (cutting speed, feed per cutting edge) on the resulting surface integrity of specimens from an equiatomic high- (CoCrFeMnNi) and a medium- (CoCrNi) entropy alloy have been carried out. A highly innovative milling process with ultrasonic assistance (USAM) was compared to conventional milling processes. Recent studies have shown that USAM has a high potential to significantly reduce the mechanical load on the tool and workpiece surface during milling. In this study, the basic machining and ultrasonic parameters were systematically varied. After machining, the surface integrity of the alloys was analyzed in terms of topography, defects, subsurface damage, and residual stresses. It was observed that USAM reduces the cutting forces and increases the surface integrity in terms of lower tensile residual stresses and defect density near the surfaces for the CoCrFeMnNi alloy. It was shown that the cutting forces and the metallurgical influence in the sub surface region are reduced by increasing the cutting speed and reducing the feed rate per cutting edge. With the CoCrNi alloy, the tool revealed severe wear. As a result, for this alloy no influence of the parameters on the machinability could be determined. KW - High Entropy Alloy KW - Medium Entropy Alloys KW - Ultrasonic assited machining PY - 2022 DO - https://doi.org/10.1016/j.matchemphys.2021.125271 SN - 0254-0584 VL - 275 SP - 125271 PB - Elsevier B.V. AN - OPUS4-53606 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Riechers, Birte A1 - Das, Amlan A1 - Dufresne, Eric A1 - Derlet, Peter M. A1 - Maaß, Robert T1 - Intermittent cluster dynamics and temporal fractional diffusion in a bulk metallic glass N2 - Glassy solids evolve towards lower-energy structural states by physical aging. This can be characterized by structural relaxation times, the assessment of which is essential for understanding the glass’ time-dependent property changes. Conducted over short times, a continuous increase of relaxation times with time is seen, suggesting a time-dependent dissipative transport mechanism. By focusing on micro-structural rearrangements at the atomic-scale, we demonstrate the emergence of sub-diffusive anomalous transport and therefore temporal fractional diffusion in a metallic glass, which we track via coherent x-ray scattering conducted over more than 300,000 s. At the longest probed decorrelation times, a transition from classical stretched exponential to a power-law behavior occurs, which in concert with atomistic simulations reveals collective and intermittent atomic motion. Our observations give a physical basis for classical stretched exponential relaxation behavior, uncover a new power-law governed collective transport regime for metallic glasses at long and practically relevant time-scales, and demonstrate a rich and highly non-monotonous aging response in a glassy solid, thereby challenging the common framework of homogeneous aging and atomic scale diffusion. KW - Glassy solids KW - Fractional diffusion KW - Coherent x-ray scattering PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-608015 DO - https://doi.org/10.1038/s41467-024-50758-3 VL - 15 IS - 1 SP - 1 EP - 9 PB - Springer Science and Business Media LLC AN - OPUS4-60801 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Riechers, Birte A1 - Das, Amlan A1 - Rashidi, Reza A1 - Dufresne, Eric A1 - Maaß, Robert T1 - Metallic glasses: Elastically stiff yet flowing at any stress N2 - Crystalline solids have a minimum stress needed to displace atoms or to move defects. This stress defines the true elastic limit and is generally a sizeable share of the macroscopic yield stress. Here we demonstrate that a metallic glass, an amorphous solid with a yield stress in the giga-pascal regime, lacks such a true microscopic elastic limit. Leveraging in-situ coherent x-ray scattering, we uncover a strongly accelerated atomic-scale transport upon the application of a stress as small as 0.005 times the yield stress. With increasing stress levels, the distribution of structural relaxation times changes from compressed exponential to simple exponential form, revealing a stress–temperature equivalence in the time-scale domain. These findings strongly promote a microstructurally heterogeneous picture of metallic glasses, in which a part of the amorphous microstructure controls macroscopic yielding whereas another part admits microplastic flow at any stress. KW - Metallic glasses KW - Microstructure PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-624530 DO - https://doi.org/10.1016/j.mattod.2024.11.015 VL - 82 SP - 92 EP - 98 PB - Elsevier B.V. AN - OPUS4-62453 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Riechers, Birte A1 - Ott, C. A1 - Das, S. M. A1 - Liebscher, C. A1 - Samwer, K. A1 - Derlet, P. M. A1 - Maaß, Robert T1 - On the elastic microstructure of bulk metallic glasses N2 - Metallic glasses (MGs) are known to be structurally heterogeneous at the nanometer (nm) scale. In addition, elastic property mapping has indicated the presence of at least an order-of-magnitude larger length scales, of which the origin continues to remain unknown. Here we demonstrate the existence of an elastic decorrelation length of the order of 100 nm in a Zr-based bulk MG using spatially resolved elastic property mapping via nanoindentation. Since compositional modulations sufficiently large to account for this elastic microstructure were not resolved by analytical scanning-transmission electron microscopy, chemical phase separation such as spinodal decomposition cannot explain their occurrence as previously suggested. Instead, we argue that the revealed long-range elastic modulations stem from structural variations affecting the local density. These emerge during solidification and are strongly influenced by the cooling constraints imposed on bulk MGs during the casting process. KW - Metallic glasses KW - Nanoindentation KW - Elastic microstructure PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-573504 DO - https://doi.org/10.1016/j.matdes.2023.111929 SN - 0264-1275 VL - 229 SP - 1 EP - 8 PB - Elsevier Ltd. CY - Amsterdam, Niederlande AN - OPUS4-57350 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Riechers, Birte A1 - Roed, L. A1 - Mehri, S. A1 - Ingebrigtsen, T. A1 - Hecksher, T. A1 - Dyre, J. A1 - Niss, K. T1 - Predicting nonlinear physical aging of glasses from equilibrium relaxation via the material time N2 - The noncrystalline glassy state of matter plays a role in virtually all fields of materials science and offers complementary properties to those of the crystalline counterpart. The caveat of the glassy state is that it is out of equilibrium and therefore exhibits physical aging, i.e., material properties change over time. For half a century, the physical aging of glasses has been known to be described well by the material-time concept, although the existence of a material time has never been directly validated. We do this here by successfully predicting the aging of the molecular glass 4-vinyl-1,3-dioxolan-2-one from its linear relaxation behavior. This establishes the defining property of the material time. Via the fluctuation-dissipation theorem, our results imply that physical aging can be predicted from thermal-equilibrium fluctuation data, which is confirmed by computer simulations of a binary liquid mixture. KW - Physical aging KW - Equilibrium relaxation KW - Glass PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-546015 DO - https://doi.org/10.1126/sciadv.abl9809 SN - 2375-2548 VL - 8 IS - 11 SP - 1 EP - 8 PB - American Association for the Advancement of Science CY - Washington, DC AN - OPUS4-54601 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rizzardi, Q. A1 - Derlet, P. M. A1 - Maaß, Robert T1 - Intermittent microplasticity in the presence of a complex microstructure N2 - We demonstrate the gradual shift from scale-free intermittent microplasticity to a scale-dependent behavior via the introduction of a variety of microstructural features within the Al-Cu binary alloy system. As long as the obstacles to dislocation motion remain shearable, the statistics of intermittent microplasticity has fat-tailed contributions. The introduction of incoherent precipitates leads to a complete transition from scale-free powerlaw scaling to an exponential and scale-dependent distribution. These results demonstrate how non-Gaussian interactions survive across different microstructures and further suggest that characteristic microstructural length scales and obstacle pinning-strengths are of secondary importance for the intermittency statistics, as long as dislocations can shear their local environment. KW - Scale-dependent behavior KW - Al-Cu binary alloy system PY - 2022 DO - https://doi.org/10.1103/PhysRevMaterials.6.073602 SN - 2475-9953 VL - 6 IS - 7 SP - 1 EP - 9 PB - American Physical Society AN - OPUS4-55387 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rizzardi, Q. A1 - Derlet, P. M. A1 - Maaß, Robert T1 - Microstructural signatures of dislocation avalanches in a high-entropy alloy N2 - Here, we trace in situ the slip-line formation and morphological signature of dislocation avalanches in a highentropy alloy with the aim of revealing their microstructural degree of localization. Correlating the intermittent microplastic events with their corresponding slip-line patterns allows defining two main event types, one of which is linked to the formation of new slip lines, whereas the other one involves reactivation of already existing slip lines. The formation of new slip lines reveals statistically larger and faster avalanches. The opposite tendency is seen for avalanches involving reactivation of already existing slip lines. The combination of both these types of events represents the highest degree of spatial avalanche delocalization that spans the entire sample, forming a group of events that determine the truncation length scale of the truncated power-law scaling. These observations link the statistics of dislocation avalanches to a microstructural observable. KW - High-entropy alloy KW - Dislocation avalanches PY - 2021 DO - https://doi.org/10.1103/PhysRevMaterials.5.043604 SN - 2475-9953 VL - 5 IS - 4 SP - 3604 PB - American Physical Society CY - College Park, MD AN - OPUS4-52458 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rizzardi, Q. A1 - McElfresh, C. A1 - Sparks, G. A1 - Stauffer, D. A1 - Marian, J. A1 - Maaß, Robert T1 - Mild-to-wild plastic transition is governed by athermal screw dislocation slip in bcc Nb N2 - Plastic deformation in crystals is mediated by the motion of line defects known as dislocations. For decades, dislocation activity has been treated as a homogeneous, smooth continuous process. However, it is now recognized that plasticity can be determined by longrange correlated and intermittent collective dislocation processes, known as avalanches. Here we demonstrate in body-centered cubic Nb how the long-range and scale-free dynamics at room temperature are progressively quenched out with decreasing temperature, eventually revealing intermittency with a characteristic length scale that approaches the Burgers Vector itself. Plasticity is shown to be bimodal across the studied temperature regime, with conventional thermally-activated smooth plastic flow (‘mild’) coexisting with sporadic Bursts (‘wild’) controlled by athermal screw dislocation activity, thereby violating the classical Notion of temperature-dependent screw dislocation motion at low temperatures. An abrupt increase of the athermal avalanche component is identified at the critical temperature of the material. Our results indicate that plasticity at any scale can be understood in terms of the coexistence of these mild and wild modes of deformation, which could help design better alloys by suppressing one of the two modes in desired temperature Windows. KW - Plastic deformation KW - Microplastic stress KW - Intermittent microplasticity PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-543927 DO - https://doi.org/10.1038/s41467-022-28477-4 VL - 13 IS - 1 SP - 1 EP - 9 PB - Nature AN - OPUS4-54392 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rockenhäuser, Christian A1 - Rowolt, C. A1 - Milkereit, B. A1 - Darvishi Kamachali, Reza A1 - Kessler, O. A1 - Skrotzki, Birgit T1 - On the long-term aging of S-phase in aluminum alloy 2618A N2 - The aluminum alloy 2618A is applied for engine components such as radial compressor wheels which operate for long time at elevated temperatures. This results in coarsening of the hardening precipitates and degradation in mechanical properties during the long-term operation, which is not taken into account in the current lifetime prediction models due to the lack of quantitative microstructural and mechanical data. To address this issue, a quantitative investigation on the evolution of precipitates during long-term aging at 190 °C for up to 25,000 h was conducted. Detailed transmission electron microscopy (TEM) was combined with Brinell hardness measurements and thorough differential scanning calorimetry (DSC) experiments. The results showthat GPB zones and S-phase Al2CuMg grow up to < 1,000 h during which the GPB zones dissolve and S-phase precipitates form. For longer aging times, only S-phase precipitates coarsen, which can be well described using the Lifshitz–Slyozov Wagner theory of ripening. A thorough understanding of the underlying microstructural processes is a prerequisite to enable the integration of aging behavior into the established lifetime models for components manufactured from alloy 2618A. KW - Long-term aging KW - Transmission electron microscopy (TEM) KW - Differential scanning calorimetry (DSC) KW - Microstructure KW - S-phase KW - Ostwald ripening PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-519899 DO - https://doi.org/10.1007/s10853-020-05740-x SN - 0022-2461 VL - 56 IS - 14 SP - 8704 EP - 8716 PB - Springer Nature AN - OPUS4-51989 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rockenhäuser, Christian A1 - von Hartrott, P. A1 - Skrotzki, Birgit T1 - Brinell-Hardness data (HBW 2.5/62.5) of aluminum alloy EN AW-2618A after different aging times and temperatures N2 - The article covers data on the Brinell hardness of the forged precipitation-hardened aluminum alloy EN AW-2618A in the initial T61 condition (i. e. slightly underaged) and after isothermal aging for up to 25,0 0 0 h at aging temperatures between 160 °C and 350 °C. In addition, the hardness was determined on specimens after creep testing at 190 °C and various stresses. The hardness decreases with increasing ag- ing time due to the microstructural evolution of the harden- ing precipitates. The drop occurs faster the higher the aging temperature. Aging under creep load additionally accelerates the hardness decrease. KW - Aluminum alloy KW - EN AW-2618A KW - Brinell hardness KW - Aging KW - Creep KW - Ostwald ripening KW - Reheating PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-567611 DO - https://doi.org/10.1016/j.dib.2022.108830 SN - 2352-3409 VL - 46 PB - Elsevier Inc. AN - OPUS4-56761 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rodricks, Carol Winnifred A1 - Prockat, Annabell A1 - Kalinka, Gerhard A1 - Trappe, Volker T1 - Novel Recyclable Hierarchical Carbon Fiber/Epoxy Composites: Preserving Fiber Length and Orientation Using Elium N2 - Current recycling methods for polymer matrix composites produce short, unoriented carbon fibers, limiting their use to intermediate‐strength applications. A method is therefore needed to recycle fibers while preserving their original length and orientation, enabling a circular economy for carbon fiber composites. This study proposes a novel hierarchical composite designed to retain fiber length and orientation during recycling. Virgin carbon fibers are encased in an insoluble epoxy matrix to form tapes that act as the primary units of the structure. The primary tape matrix shields the fibers from chemical degradation while preserving their alignment throughout recycling. The tapes are then embedded in a secondary recyclable matrix, Elium, a thermoplastic polymer soluble in acetone with mechanical properties comparable to epoxy. The composite is recycled by dissolving the secondary Elium matrix in acetone and recovering the primary tape units with intact fiber length and orientation. The primary units can then be used to assemble new composites. In this study, hierarchical composite laminates underwent recycling up to three times. Their mechanical properties were assessed after each cycle. Laminates with an Elium secondary matrix retained 60%–90% of the mechanical performance of epoxy‐based laminates. Minimal degradation was observed between cycles, and fiber length, orientation, and volume fraction were fully preserved. Pushout tests confirmed that fibers in the primary tapes were sufficiently shielded during the recycling process. These results validate the feasibility of a hierarchical recyclable composite that combines recyclability with high mechanical performance, serving as a proof of concept and providing opportunities for future development. KW - Review KW - Interface KW - Micromechanics KW - Polymer matrix composites KW - Glass fibre reinforced composites PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-655276 DO - https://doi.org/10.1002/pc.70869 SN - 0272-8397 SP - 1 EP - 16 PB - Wiley Periodicals LLC. AN - OPUS4-65527 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rodrigues, A. C. P. A1 - Feller, A. A1 - Agudo Jácome, Leonardo A1 - Azevedo, C. R. F. T1 - Use of synthetic Fe3O4-rich tribofilms to investigate the effect of microconstituents, temperature and atmosphere on the friction coefficient during pin-on-disc tribotest N2 - This work investigates the effect of the tribotesting parameters (temperature, atmosphere, and third body chemical composition) on the coefficient of friction (CoF) during pin-on-disc dry (PoD) sliding tribotests using artificial third bodies. The third body comprised nanometric Fe3O4-based binary to quaternary chemical compositions containing copper, graphite, and zirconia. These mixtures were manually or ball-milled prepared, and pin-on-disc tribotests were conducted at 23 °C and 400 °C under air or nitrogen atmospheres. Combining PoD and artificial third body to create synthetic tribofilms might be useful for testing new formulations of Cu-free friction materials. Microstructural characterisation of the tribofilms was used to study the stability of the Fe3O4, copper, and graphite nanoparticles under different testing conditions to understand their effects on the CoF. For the Fe3O4-C-ZrO2-X systems, the ball milling mixing promoted the formation of turbostratic graphite in the tribofilm, impairing the lubricating effect of the graphite under air atmosphere at 23 °C. The formation of monoclinic CuO in the tribofilms during tribotests at 400 °C under air and N2 atmospheres promoted a lubricating effect. KW - Tribology KW - Microstructure KW - Oxide KW - Transmission electron microscopy PY - 2022 DO - https://doi.org/10.1088/2051-672X/ac9d51 SN - 2051-672X VL - 10 IS - 4 SP - 044009-1 EP - 044009-18 PB - IOP Pobilishing AN - OPUS4-56467 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rosalie, Julian A1 - Hohenwarter, A. T1 - Dynamic Precipitation during High-Pressure Torsion of a Magnesium–Manganese Alloy N2 - An ultrafine-grained magnesium alloy has been produced through room temperature high-pressure torsion (HPT) of solutionized Mg–1.35 wt% Mn. Dynamic precipitation of nanometer-scale Mn particles occurs during deformation. These particles populate the grain boundaries, acting as pinning sites which allow the alloy to develop a grain size of 140 nm after 0.5 rotations. Further, HPT deformation results in a gradual increase in grain size with no increase in precipitate size. Despite the extensive deformation applied, the alloy does not develop a bimodal grain structure and retains a grain size of 230 nm after 10 complete rotations, demonstrating the stability and effectiveness of these pinning particles. KW - Grain-boundary pinning KW - Magnesium alloys KW - High-pressure torsion KW - Severe plastic deformation KW - Ultrafine-grained materials PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-656471 DO - https://doi.org/10.1002/adem.202500424 SN - 1527-2648 VL - 28 IS - 4 SP - 1 EP - 9 PB - Wiley AN - OPUS4-65647 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rosenbusch, Ivo A1 - Arai, Marylyn Setsuko A1 - Rizzo, Fabio A1 - de Camargo, Andrea S. S. A1 - Ravoo, Bart Jan T1 - A host–guest approach to ratiometric pH sensing using upconversion nanoparticles N2 - A new pH nanosensor based on β-NaYF4:Yb3+/Tm3+ upconversion nanoparticles functionalized with cyclodextrin and a pH-sensitive adamantane-modified nitrobenzoxadiazole dye (NBD-Ad). KW - Host-guest materials KW - Upconversion nanoparticles KW - Ratiometric optical sensors KW - pH sensing PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-637722 DO - https://doi.org/10.1039/d5na00145e SN - 2516-0230 VL - 7 IS - 13 SP - 4142 EP - 4151 PB - Royal Society of Chemistry (RSC) AN - OPUS4-63772 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rosenbusch, Sjard Mathis A1 - Diercks, Philipp A1 - Kindrachuk, Vitaliy A1 - Unger, Jörg F. T1 - Integrating custom constitutive models into FEniCSx: A versatile approach and case studies N2 - The development and integration of user-defined constitutive relationships into finite element (FE) tools using standardized interfaces play a pivotal role in advancing the capabilities of FE solvers for structural mechanics applications. While commercial FE solvers like Abaqus and Ansys have designed their interfaces to provide custom stresses, tangents, and updated history variables, the open-source solver FEniCSx remains efficient only when the constitutive update has an analytical representation. This restricts the application of FEniCSx for non-linear structural mechanics. Since FEniCSx has become a powerful and popular open-source tool for solving partial differential equations, particularly due to its automatic computation of Hessians, we aim to develop a generalized interface to enhance its capability for constitutive modeling. This approach will address complex constitutive equations that require iterative solutions at the quadrature point level. Specific implementation challenges, such as using return-mapping procedures, can then be managed commonly. The provided interface for custom constitutive models offers a versatile way to implement them in various languages, including C++, Python, Rust, and Fortran. Finally, with UMATs for viscoplastic models as an example, we demonstrate how existing user subroutines can be incorporated into the interface and utilized within the FEniCSx framework. KW - Finite element method KW - Constitutive models KW - FEniCSx KW - UMAT KW - Rust KW - Python KW - C++ PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-630439 DO - https://doi.org/10.1016/j.advengsoft.2025.103922 SN - 0965-9978 VL - 206 SP - 1 EP - 11 PB - Elsevier CY - Amsterdam AN - OPUS4-63043 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ruffini, A. A1 - Le Bouar, Y. A1 - Finel, A. A1 - Epishin, A. I. A1 - Fedelich, Bernard A1 - Feldmann, Titus A1 - Viguier, B. A1 - Poquillon, D. T1 - Dislocations interacting with a pore in an elastically anisotropic single crystal nickel-base superalloy during hot isostatic pressing N2 - The formation of pores in CMSX-4 nickel based superalloys is detrimental to the service life of the material. A way to avoid the problem is to treat the superalloys under Hot Isostatic Pressing (HIP), which enables a large volume fraction of pores to be annihilated. This paper aims to understand the contribution of plastic activity related to the gliding of dislocations on the pore annihilation. Simulations based on a phase-field model of dislocation are performed and make it possible to consider the strong anisotropy of the CMSX-4 under HIP conditions in conjunction to the strong elastic heterogeneity introduced by the pore. For pores with a radius of few micrometers, it is shown that edge parts of dislocation lines that present an extra half atomic plane oriented towards the pore are stacked above and under it in the direction which is perpendicular to their slip-planes, causing an increase of the number of dislocation along the four octahedral directions of the FCC single crystal which intersect the pore center. Results are streamlined within the isotropic elastic theory of dislocations. Effects of elastic anisotropy and dislocation reactions are also investigated in order to specify what would be the dislocation configuration around a pore in CMSX-4 under HIP conditions. Notably, the elastic anisotropy is shown to significantly modify the arrangement of dislocations close to the pore equator. Simulations also allow for the characterization of pore/dislocation interactions when dislocations are involved in Low Angle Boundaries as experimentally observed. KW - HIP KW - Superalloys KW - Dislocation KW - Pore KW - Phase-field PY - 2022 DO - https://doi.org/10.1016/j.commatsci.2021.111118 SN - 0927-0256 VL - 204 SP - 1 EP - 14 PB - Elsevier CY - Amsterdam AN - OPUS4-54220 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Röhsler, Andreas A1 - Sobol, Oded A1 - Hänninen, H. A1 - Böllinghaus, Thomas T1 - In-situ ToF-SIMS analyses of deuterium re-distribution in austenitic steel AISI 304L under mechanical load N2 - Hydrocarbons fuel our economy. Furthermore, intermediate goods and consumer products are often hydrocarbon-based. Beside all the progress they made possible, hydrogen-containing substances can have severe detrimental effects on materials exposed to them. Hydrogen-assisted failure of iron alloys has been recognised more than a century ago. The present study aims to providing further insight into the degradation of the austenitic stainless steel AISI 304L (EN 1.4307) exposed to hydrogen. To this end, samples were electrochemically charged with the hydrogen isotope deuterium (2H, D) and analysed by scanning electron microscopy (SEM), electron back-scatter diffraction (EBSD) and time-of-flight secondary ion mass spectrometry (ToF-SIMS). It was found that deuterium caused a phase transformation from the original γ austenite into ε- and α’-martensite. Despite their low solubility for hydrogen, viz. deuterium, the newly formed phases showed high deuterium concentration which was attributed to the increased density of traps. Information about the behaviour of deuterium in the material subjected to external mechanical load was gathered. A four-point-bending device was developed for this purpose. This allowed to analyse in-situ pre-charged samples in the ToF-SIMS during the application of external mechanical load. The results indicate a movement of deuterium towards the regions of highest stress. KW - ToF-SIMS KW - Hydrogen KW - Deuterium KW - AISI 304L KW - EBSD PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-505142 DO - https://doi.org/10.1038/s41598-020-60370-2 VL - 10 IS - 1 SP - 3611 PB - Nature AN - OPUS4-50514 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rütters, H. A1 - Fischer, S. A1 - Le, Quynh Hoa A1 - Bettge, Dirk A1 - Bäßler, Ralph A1 - Maßmann, J. A1 - Ostertag-Henning, C. A1 - Wolf, J. L. A1 - Pumpa, M. A1 - Lubenau, U. A1 - Knauer, S. A1 - Jaeger, P. A1 - Neumann, A. A1 - Svensson, K. A1 - Pöllmann, H. A1 - Lempp, C. A1 - Menezes, F. F. A1 - Hagemann, B. T1 - Towards defining reasonable minimum composition thresholds – Impacts of variable CO2 stream compositions on transport, injection and storage N2 - To set up recommendations on how to define “reasonable minimum composition thresholds” for CO2 streams to access CO2 pipeline networks, we investigated potential impacts of CO2 streams with different and temporally variable compositions and mass flow rates along the CCS chain. All investigations were based on a generic “CCS cluster scenario” in which CO2 streams captured from a spatial cluster of eleven emitters (seven fossil-fired power plants, two cement plants, one refinery and one steel mill) are collected in a regional pipeline network. The resulting CO2 stream (19.78 Mio t impure CO2 per year) is transported in a trunk line (onshore and offshore) and injected into five generic replicate storage structures (Buntsandstein saline aquifers) offshore. Experimental investigations and modeling of selected impacts revealed beneficial as well as adverse impacts of different impurities and their combinations. Overall, no fundamental technical obstacles for transporting, injecting and storing CO2 streams of the considered variable compositions and mass flow rates were observed. We recommend to define minimum composition thresholds for each specific CCS project through limiting i) the overall CO2 content, ii) maximum contents of relevant impurities or elements, iii) acceptable variability of concentrations of critical impurities, and defining impurity combinations to be avoided. KW - Impurities KW - CO2 quality KW - Pipeline network KW - Whole-chain CCS scenario KW - Recommendations PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-543004 DO - https://doi.org/10.1016/j.ijggc.2022.103589 SN - 1750-5836 VL - 114 SP - 1 EP - 14 PB - Elsevier CY - New York, NY AN - OPUS4-54300 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Salari, Farid A1 - Zocca, Andrea A1 - Bosetti, Paolo A1 - Hlaváček, Petr A1 - Italiano, Antonino A1 - Gobbin, Filippo A1 - Colombo, Paolo A1 - Kühne, Hans-Carsten A1 - Sglavo, Vincenzo M. T1 - Powder-bed 3D printing by selective activation of magnesium phosphate cement: Determining significant processing parameters and their effect on mechanical strength N2 - The present work addresses powder bed binder jetting additive manufacturing by selective magnesium phosphate cement activation. Despite the potential of this technology to aid the digitalization of the construction industry, the effect of processing parameters on the mechanical performance of printed materials has not yet been studied to generate a guideline for the further development of the technology. Statistical methodologies were used to screen the effect of four printing process parameters (printing speed, layer thickness, raster angle, and build direction on flexural and compressive strength). As the exploited technology works with constant fluid pressure, the physical interpretation of the effect of each factor can be considered taking into account the interactions between the binder materials in the powder bed. Analysis of variance (ANOVA) indicated that printing speed and layer thickness significantly affect mechanical performances. Furthermore, the layout of samples for the printing process is preferable to be parallel the printhead movement. An anisotropic behavior was observed, and the samples subjected to compressive forces parallel to the layer plane possessed lower strength values. This effect can be interpreted as a result of a weak area of low density in between layers, leading to a pronounced delamination under compression. Even though the strength of the printed material is not suitable for a structural concrete, it can be marginally improved by design of experiment and optimized for non-structural applications, such as for porous artificial stone. Design of experiment coupled with ANOVA methods can be used in the future to support the development of novel material mixtures, thus expanding the fields of application of this novel additive manufacturing technology. KW - Concrete 3D-printing KW - Particle-bed binder jetting KW - Design of experiment PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-601654 DO - https://doi.org/10.1016/j.oceram.2024.100609 VL - 18 SP - 1 EP - 11 PB - Elsevier B.V. AN - OPUS4-60165 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Scheffler, Franziska A1 - Fleck, Mirjam A1 - Busch, Richard A1 - Casado, Santiago A1 - Gnecco, Enrico A1 - Tielemann, Christopher A1 - Brauer, Delia S. A1 - Müller, Ralf T1 - Surface Crystallization of Barium Fresnoite Glass: Annealing Atmosphere, Crystal Morphology and Orientation N2 - Controlled oriented crystallization of glass surfaces is desired for high precision applications, since the uppermost crystal layer significantly influences the properties of the material. In contrast to previous studies, the data presented here deal with separated crystals growing at defect-free surfaces in four atmospheres with different degrees of humidity (ambient/dry air, argon and vacuum). A glass with the composition 2 BaO–TiO2–2.75 SiO2 was heat-treated at 825 °C until fresnoite (Ba2TiSi2O8) grew to a significant size. The crystal growth rate is found to increase with increasing humidity. The morphology of the crystals changes from highly distorted dendrites in the driest atmosphere (vacuum) to circular/spear-head-shaped crystals in the wettest atmosphere (ambient air), which we attribute to a decrease in viscosity of the glass surface due to water uptake. The least distorted crystals appear in the form of depressions of up to 6 µm. This has an influence on the observed crystal orientation, as measured by electron backscatter diffraction (EBSD). The pulled-in crystals change the orientation during growth relative to the flat glass surface due to an enrichment in SiO2 at the crystal fronts. This confirms that the orientation of crystals is not fixed following nucleation. KW - Fresnoite KW - Surface crystallization KW - Crystal growth KW - Crystal morphology KW - Crystal orientation KW - EBSD PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-587230 DO - https://doi.org/10.3390/cryst13030475 VL - 13 IS - 3 SP - 1 EP - 17 PB - MDPI AG CY - Basel AN - OPUS4-58723 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Scherb, T. A1 - Fantin, Andrea A1 - Checcia, S. A1 - Stephan-Scherb, Christiane A1 - Escolástico, S. A1 - Franz, A. A1 - Seeger, J. A1 - Meulenberg, W. A. A1 - d'Acapito, F. A1 - Serra, J. M. T1 - Unravelling the crystal structure of Nd5.8WO12-d and Nd5.7W0.75Mo0.25O12-d mixed ionic electronic conductors N2 - Mixed ionic electronic conducting ceramics Nd6-yWO12-d (d is the Oxygen deficiency) provide excellent stability in harsh environments containing strongly reactive gases such as CO2, CO, H2, H2O or H2S. Due to this chemical stability, they are promising and cost-efficient candidate materials for gas separation, catalytic membrane reactors and protonic ceramic fuel cell technologies. As in La6-yWO12-d, the ionic/electronic transport mechanism in Nd6-yWO12-d is expected to be largely controlled by the crystal structure, the conclusive determination of which is still lacking. This work presents a crystallographic study of Nd5.8WO12-d and molybdenum-substituted Nd5.7W0.75Mo0.25O12-d prepared by the citrate complexation route. High-resolution synchrotron and neutron powder diffraction data were used in combined Rietveld refinements to unravel the crystal structure of Nd5.8WO12-d and Nd5.7W0.75Mo0.25O12-d. Both investigated samples crystallize in a defect fluorite crystal structure with space group Fm3m and doubled unit-cell parameter due to cation ordering. Mo replacesWat bothWyckoff sites 4a and 48h and is evenly distributed, in contrast with La6-yWO12-d. X-ray absorption spectroscopy as a function of partial pressure pO2 in the near-edge regions excludes oxidation state changes of Nd (Nd3+) and W(W6+) in reducing conditions: the enhanced hydrogen permeation, i.e. ambipolar conduction, observed in Mo-substituted Nd6-yWO12-d is therefore explained by the higher Mo reducibility and the creation of additional – disordered – oxygen vacancies. KW - Powder diffraction KW - Mixed conductors KW - X-ray absorption spectroscopy PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-514607 DO - https://doi.org/10.1107/S1600576720012698 VL - 53 SP - 1471 EP - 1483 AN - OPUS4-51460 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Scheuerlein, C. A1 - Andrieux, J. A1 - Michels, M. A1 - Lackner, F. A1 - Chiriac, R. A1 - Hagner, M. A1 - Di Michiel, M. A1 - Meyer, Christian A1 - Toche, F. ED - Foley, C. P. T1 - Effect of the fabrication route on the phase and volume changes during the reaction heat treatment of Nb3Sn superconducting wires N2 - Accelerator magnets that can reach magnetic fields well beyond the Nb-Ti performance limits are presently being built and developed, using Nb3Sn superconductors. This technology requires reaction heat treatment (RHT) of the magnet coils, during which Nb3Sn is formed from its ductile precursor materials (a “wind and react” approach). The Nb3Sn microstructure and microchemistry are strongly influenced by the conductor fabrication route, and by the Phase changes during RHT. By combining in situ differential scanning calorimetry, high Energy synchrotron x-ray diffraction, and micro-tomography experiments, we have acquired a unique data set that describes in great detail the phase and microstructure changes that take place during the processing of restacked rod process (RRP), powder-in-tube (PIT), and internal tin (IT) Nb3Sn wires. At temperatures below 450 ° the phase evolutions in the three wire types are similar, with respectively solid state interdiffusion of Cu and Sn, Cu6Sn5 formation, and Cu6Sn5 peritectic transformation. Distinct differences in phase evolutions in the wires are found when temperatures exceed 450 °C. The volume changes of the conductor during RHT are a difficulty in the production of Nb3Sn accelerator magnets. We compare the wire diameter changes measured in situ by dilatometry with the phase and void volume evolution of the three types of Nb3Sn wire. Unlike the Nb3Sn wire length changes, the wire diameter evolution is characteristic for each Nb3Sn wire type. The strongest volume increase, of about 5%, is observed in the RRP wire, where the main diameter increase occurs above 600 °C upon Nb3Sn formation. KW - Nb3Sn KW - Microstructure KW - Phase transformations KW - Volume changes KW - X-ray diffraction KW - Differential scanning calorimetry KW - Synchrotron micro-tomography PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-505128 DO - https://doi.org/10.1088/1361-6668/ab627c VL - 33 IS - 3 SP - 034004 PB - IOP Publishing CY - Bristol (UK) AN - OPUS4-50512 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schilling, Markus A1 - Bayerlein, Bernd A1 - von Hartrott, Philipp A1 - Waitelonis, Jörg A1 - Birkholz, Henk A1 - Portella, Pedro Dolabella A1 - Skrotzki, Birgit T1 - FAIR and Structured Data: A Domain Ontology Aligned with Standard‐Compliant Tensile Testing N2 - The digitalization of materials science and engineering (MSE) is currently leading to remarkable advancements in materials research, design, and optimization, fueled by computer‐driven simulations, artificial intelligence, and machine learning. While these developments promise to accelerate materials innovation, challenges in quality assurance, data interoperability, and data management have to be addressed. In response, the adoption of semantic web technologies has emerged as a powerful solution in MSE. Ontologies provide structured and machine‐actionable knowledge representations that enable data integration, harmonization, and improved research collaboration. This study focuses on the tensile test ontology (TTO), which semantically represents the mechanical tensile test method and is developed within the project Plattform MaterialDigital (PMD) in connection with the PMD Core Ontology. Based on ISO 6892‐1, the test standard‐compliant TTO offers a structured vocabulary for tensile test data, ensuring data interoperability, transparency, and reproducibility. By categorizing measurement data and metadata, it facilitates comprehensive data analysis, interpretation, and systematic search in databases. The path from developing an ontology in accordance with an associated test standard, converting selected tensile test data into the interoperable resource description framework format, up to connecting the ontology and data is presented. Such a semantic connection using a data mapping procedure leads to an enhanced ability of querying. The TTO provides a valuable resource for materials researchers and engineers, promoting data and metadata standardization and sharing. Its usage ensures the generation of finable, accessible, interoperable, and reusable data while maintaining both human and machine actionability. KW - Data Interoperability KW - Domain Ontology Development KW - FAIR Data Management KW - Knowledge Representation KW - Tensile Test Ontology KW - Semantic Web Technologies PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-598142 DO - https://doi.org/10.1002/adem.202400138 SN - 1438-1656 SP - 1 EP - 19 PB - Wiley VHC-Verlag AN - OPUS4-59814 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schilling, Markus A1 - Bruns, Sebastian A1 - Bayerlein, Bernd A1 - Kryeziu, Jehona A1 - Schaarschmidt, Jörg A1 - Waitelonis, Jörg A1 - Dolabella Portella, Pedro A1 - Durst, Karsten T1 - Seamless Science: Lifting Experimental Mechanical Testing Lab Data to an Interoperable Semantic Representation N2 - The scientific landscape is undergoing rapid transformations with the advent of the digital age which revolutionizes research methodologies. In materials science and engineering, an adoption of modern data management techniques is desirable to maximize the efficiency and accessibility of research efforts. Traditional practices in testing laboratories are usually inadequate for efficient data acquisition and utilization as they lead to local storage and difficulty in publication and correlation with other results. Electronic laboratory notebooks (ELNs) are promising prospects in this respect. Semantic concepts and ontologies enhance interoperability by standardizing experimental data representation. An in‐laboratory pipeline seamlessly integrating an ELN with transformation scripts to convert experimental into interoperable data in a machine‐actionable format is created in this study as a proof of concept. Tensile test results and the corresponding tensile test ontology are used exemplary. Linking ELN data to semantic concepts enriches the stored information while improving interpretability and reusability. Involving undergraduate students builds a bridge between theory and practice during their training and promotes their digital skills. This study underscores the potential of ELNs and knowledge representations as beneficial means toward improved data management practices that enhance collaborative research and education while ensuring compatibility with evolving standards and technologies. KW - Semantic Data KW - Data Integration KW - Tensile Test Ontology KW - Electronic Lab Notebook KW - Wissensrepräsentation KW - Education PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-618251 DO - https://doi.org/10.1002/adem.202401527 SP - 1 EP - 13 PB - Wiley VHC-Verlag AN - OPUS4-61825 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schilling, Markus A1 - Marschall, Niklas A1 - Niebergall, Ute A1 - Böhning, Martin T1 - Modernizing FNCT data handling in polymer labs: Towards efficient management N2 - A streamlined Python-based workflow for transforming Full-Notch Creep Test (FNCT) data into organized, machine-actionable formats is presented. The workflow automates the conversion of raw FNCT data from classic CSV and Excel files into structured outputs that facilitate future semantic integration. Emphasizing practical data handling, the approach includes automation scripts for efficient data extraction, transformation, and storage, which culminate in well-ordered files. This transformation paves the way for potential semantic data integration and facilitates access for users with varying levels of digital experience to enhanced data management in polymer research and testing. KW - PE-HD KW - Full-Notch Creep Test (FNCT) KW - Environmental Stress Cracking (ESC) KW - Data Interoperability KW - FAIR Data KW - Semantic Data PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-637826 DO - https://doi.org/10.1016/j.commatsci.2025.114085 SN - 0927-0256 VL - 259 SP - 1 EP - 5 PB - Elsevier B.V. AN - OPUS4-63782 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schilling, Markus A1 - Marschall, Niklas A1 - Niebergall, Ute A1 - Wachtendorf, Volker A1 - Böhning, Martin T1 - Characteristics of environmental stress cracking of PE-HD induced by biodiesel and diesel fuels N2 - In the context of the increasing effect of carbon dioxide emissions on the global climate biodiesel produced from renewable sources has emerged as a promising contender replacing fossil fuels, especially in long-range transport vehicles, using existing engines and infrastructure. High-density polyethylene is one of the prevailing materials for pipe and container applications for storage and transport of such fuels, both, from fossil and renewable resources. The contact with the respective fuels raises questions concerning material compatibility as biodiesel exhibits significant differences compared to conventional diesel fuel affecting its sorption and plasticization behavior in polyethylene. In this study, its behavior with respect to environmental stress cracking, considered one of the most frequent damage mechanisms leading to failure of polymer parts and packaging, was evaluated using the well-established Full Notch Creep Test. This approach allows for a detailed fracture surface analysis using imaging techniques, such as optical and laser scanning microscopy, as well as infrared spectroscopy. Comparing the environmental stress cracking behavior in standard surfactant solutions with that in biodiesel and diesel, respective crack propagation rates, showing different levels of acceleration, were determined and details of the underlying mechanisms could be revealed. Furthermore, the specific infrared absorption of the biodiesel’s ester functionality allows its semi-quantitative determination on the fracture surface of the tested specimens after failure. Thus, a preferred uptake of sorptive fluids in the fracture zone due to local morphological changes of the polyethylene could be directly evidenced by infrared spectroscopy. KW - Environmental stress cracking (ESC) KW - Full notch creep test (FNCT) KW - Confocal laser scanning microscopy (LSM) KW - Biodiesel KW - Diesel PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-608591 DO - https://doi.org/10.1016/j.polymertesting.2024.108547 SN - 0142-9418 VL - 138 SP - 1 EP - 16 PB - Elsevier Ltd. AN - OPUS4-60859 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schilling, Markus A1 - Marschall, Niklas A1 - Niebergall, Ute A1 - Wachtendorf, Volker A1 - Böhning, Martin T1 - Unveiling Effects of Biodiesel and Diesel on Environmental Stress Cracking of PE-HD N2 - The behavior of high‐density polyethylene with respect to resistance against environmental stress cracking (ESC) is usually regarded as an inherent material property being specific for respective types of PE‐HD and tested using standardized methods, conditions, and also standard testing liquids (usually aqueous surfactant solutions). On the other hand, for practical applications the ESC behavior of those polymeric materials, commonly used for pipes or containers, in contact with other liquids (e.g., fuels) is often of relevant interest, but for a reasonable assessment, where consistent benchmark data for a direct comparison are often missing, it is essential to determine the actually prevailing failure mode and classify it related to crack propagation or other mechanisms. Using the well‐established Full Notch Creep Test, which favorably allows for a detailed microscopic fracture surface analysis after failure, the behavior of two typical PE‐HD types for container applications is investigated in biodiesel and diesel and compared to a standard surfactant solution. This enables a clear identification of characteristic features of the interaction of biodiesel and diesel as sorptive fuels in contact with the polymer, revealing the complex interplay of sorption and plasticization as well as ESC inducing effects on PE‐HD, which could be clearly shown for both fuels. KW - Biodiesel KW - Confocal laser scanning microscopy (LSM) KW - Diesel KW - Full notch creep test (FNCT) KW - Plasticization PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-650525 DO - https://doi.org/10.1002/pen.70239 SN - 0032-3888 SP - 1 EP - 16 PB - Wiley CY - Hoboken (NJ) AN - OPUS4-65052 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schilling, Markus A1 - Niebergall, Ute A1 - Marschall, Niklas A1 - Alig, I. A1 - Böhning, Martin T1 - A phenomenological criterion for an optical assessment of PE-HD fracture surfaces obtained from FNCT N2 - The full-notch creep test (FNCT) is a common test method to evaluate the environmental stress cracking (ESC) behavior of high-density polyethylene (PE-HD), e.g. for container materials. The test procedure as specified in ISO 16770 provides a comparative measure of the resistance against ESC using the time to failure of PE-HD specimens under constant mechanical load in a well-defined liquid test environment. Since the craze-crack damage mechanism underlying the ESC phenomenon is associated with brittle failure, the occurrence of a predominantly brittle fracture surface is a prerequisite to consider an FNCT measurement as representative for ESC, i.e. a time to failure dominated by craze-crack propagation. The craze-crack propagation continuously reduces the effective residual cross-sectional area of the specimen during the test, which results in a corresponding increase of the effective mechanical stress. Thus, a transition to ductile shear deformation is inevitable at later stages of the test, leading usually to a pronounced central ligament. Therefore, an optical evaluation of FNCT fracture surfaces concerning their brittleness is essential. An enhanced imaging analysis of FNCT fracture surfaces enables a detailed assessment of craze-crack Propagation during ESC. In this study, laser scanning microscopy (LSM) was employed to evaluate whether FNCT fracture surfaces are representative with respect to craze-crack propagation and ESC. Based on LSM height data, a phenomenological criterion is proposed to assess the validity of distinct FNCT measurements. This criterion is supposed to facilitate a quick evaluation of FNCT results in practical routine testing. Its applicability is verified on a sample basis for seven different commercial PE-HD container materials. KW - Environmental stress cracking (ESC) KW - Full notch creep test (FNCT) KW - Laser scanning microscopy (LSM) KW - Fracture surfaces KW - Optical criterion of brittleness PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-521012 DO - https://doi.org/10.1016/j.polymertesting.2020.107002 VL - 94 SP - 107002 PB - Elsevier Ltd. CY - Amsterdam AN - OPUS4-52101 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schilling, Markus A1 - Niebergall, Ute A1 - Marschall, Niklas A1 - Meinel, Dietmar A1 - Böhning, Martin T1 - Relation of craze to crack length during slow crack growth phenomena in high‐density polyethylene N2 - The craze‐crack mechanism occurring in high‐density polyethylene (HDPE) causing slow crack growth and environmental stress cracking is investigated in detail with respect to the relation of crack length and the related craze zone. This is essential for the understanding of the resulting features of the formed fracture surface and their interpretation in the context of the transition from crack propagation to ductile shear deformation. It turns out that an already formed craze zone does not inevitably result in formation of a propagating crack, but could also undergo ductile failure. For the examination, the full notch creep test (FNCT) was employed with a subsequent advanced fracture surface analysis that was performed using various imaging techniques: light microscopy, laser scanning microscopy, scanning electron microscopy, and X‐ray micro computed tomography scan. FNCT specimens were progressively damaged for increasing durations under standard test conditions applying Arkopal, the standard surfactant solution, and biodiesel as test media were used to analyze the stepwise growth of cracks and crazes. From considerations based on well‐established fracture mechanics approaches, a theoretical correlation between the length of the actual crack and the length of the preceding craze zone was established that could be evidenced and affirmed by FNCT fracture surface analysis. Moreover, the yield strength of a HDPE material exposed to a certain medium as detected by a classic tensile test was found to be the crucial value of true stress to induce the transition from crack propagation due to the craze‐crack mechanism to shear deformation during FNCT measurements. Highlights - Progress of crack formation in high‐density polyethylene is analyzed by different imaging techniques - Determined growth rates depend on distinction between craze zone and crack - The ratio of the present crack to the anteceding craze zone is validated theoretically - The transition from crack propagation to ductile shear deformation is identified - An already formed craze zone may still fail by ductile mechanisms KW - Craze-crack mechanism KW - Environmental stress cracking (ESC) KW - Full notch creep test (FNCT) KW - Laser scanning microscopy (LSM) KW - Slow crack growth (SCG) KW - X-ray computed tomography (CT) PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-601831 DO - https://doi.org/10.1002/pen.26698 SN - 1548-2634 VL - 64 IS - 6 SP - 2387 EP - 2403 PB - Wiley AN - OPUS4-60183 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmies, Lennart A1 - Botsch, B. A1 - Le, Q.-H. A1 - Yarysh, A. A1 - Sonntag, U. A1 - Hemmleb, M. A1 - Bettge, Dirk T1 - Classification of fracture characteristics and fracture mechanisms using deep learning and topography data T1 - Klassifikation von Bruchmerkmalen und Bruchmechanismen mittels Deep Learning und unter Verwendung von Topographiedaten N2 - In failure analysis, micro-fractographic analysis of fracture surfaces is usually performed based on practical knowledge which is gained from available studies, own comparative tests, from the literature, as well as online databases. Based on comparisons with already existing images, fracture mechanisms are determined qualitatively. These images are mostly two-dimensional and obtained by light optical and scanning electron imaging techniques. So far, quantitative assessments have been limited to macrocopically determined percentages of fracture types or to the manual measurement of fatigue striations, for example. Recently, more and more approaches relying on computer algorithms have been taken, with algorithms capable of finding and classifying differently structured fracture characteristics. For the Industrial Collective Research (Industrielle Gemeinschaftsforschung, IGF) project “iFrakto” presented in this paper, electron-optical images are obtained, from which topographic information is calculated. This topographic information is analyzed together with the conventional 2D images. Analytical algorithms and deep learning are used to analyze and evaluate fracture characteristics and are linked to information from a fractography database. The most important aim is to provide software aiding in the application of fractography for failure analysis. This paper will present some first results of the project. N2 - Die mikrofraktographische Analyse von Bruchflächen wird in der Schadensanalyse meist auf der Basis von Erfahrungswissen vorgenommen, welches aus vorliegenden Untersuchungen, eigenen Vergleichsversuchen und aus der Literatur und online Datenbanken stammt. Durch Vergleiche mit bereits vorliegenden Bildern werden qualitativ Bruchmechanismen ermittelt. Grundlage dafür sind zumeist zweidimensionale Aufnahmen aus licht- und elektronenoptischen Verfahren. Quantitative Aussagen beschränken sich bislang beispielsweise auf makroskopische Anteile von Bruchmechanismen oder die manuelle Ausmessung von Schwingstreifen. In jüngerer Zeit gibt es vermehrt Ansätze, Computer-Algorithmen einzusetzen, die in der Lage sind, unterschiedlich strukturierte Bruchmerkmale zu finden und zu klassifizieren. Im hier vorgestellten IGF-Vorhaben „iFrakto“ werden elektronenoptische Aufnahmen erzeugt und daraus Topographie-Informationen berechnet. Diese gewonnenen Topographie-Informationen werden zusammen mit den klassischen 2D-Bildern ausgewertet. Analytische Algorithmen und Deep Learning werden eingesetzt, um Bruchmerkmale zu analysieren, zu bewerten und mit Informationen aus einer fraktographischen Datenbank zu verknüpfen. Wichtigstes Ziel ist die Bereitstellung von Software zur Unterstützung der Fraktographie in der Schadensanalyse. In diesem Beitrag werden erste Ergebnisse des Vorhabens vorgestellt. KW - Fractography KW - Deep Learning KW - Classification PY - 2023 DO - https://doi.org/10.1515/pm-2022-1008 SN - 0032-678X VL - 60 IS - 2 SP - 76 EP - 92 PB - De Gruyter AN - OPUS4-56962 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmies, Lennart A1 - Hemmleb, Matthias A1 - Bettge, Dirk T1 - Relevant input data for crack feature segmentation with deep learning on SEM imagery and topography data N2 - Fractography plays a critical role in failure analysis of engineering components and has a considerable importance for safety investigations. Usually, the interpretation of fracture surfaces is done by experts with the help of literature and experimental data, that requires a lot of experience. The use of deep learning (DL) with neural networks in failure analysis becomes more and more relevant with the rapidly developing possibilities. Especially, the modern network architectures can assist fractographers in determining various fracture features on SEM images of the fracture surfaces. The basis for the best possible evaluation is the understanding of the influence of the input data used for training deep neural networks (DNN). Therefore, this study discusses the influence of the selection of the input data used for the prediction quality of these networks in order to take this into account for future data acquisition. Specimens of various metallic materials were subjected to fatigue cracking experiment under laboratory conditions. The fractured surfaces were then imaged using various modes or detectors (such as SE, BSE and topography) in SEM, and those captured images were used to create a training data set. The relevance of the individual data for the quality of the prediction is determined by a specific combination of the different detector data. For the training, the well-established architecture of a UNet-ResNet34 with a fixed set of hyperparameters is used. It has been found in this present study that the combination of all input data significantly increases the prediction accuracy, whereby even the combination of SE and BSE data provides considerable advantages over the exclusive use of SE images. KW - Fractography KW - Machine Learning KW - Deep Learning KW - KI PY - 2023 DO - https://doi.org/10.1016/j.engfailanal.2023.107814 VL - 156 SP - 1 EP - 8 PB - Elsevier AN - OPUS4-58918 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schneider, J. A1 - Farris, L. A1 - Nolze, Gert A1 - Reinsch, Stefan A1 - Cios, G. A1 - Tokarski, T. A1 - Thompson, S. T1 - Microstructure evolution in Inconel 718 produced by powder bed fusion additive manufacturing N2 - Inconel 718 is a precipitation strengthened, nickel-based super alloy of interest for the Additive Manufacturing (AM) of low volume, complex parts to reduce production time and cost compared to conventional subtractive processes. The AM process involves repeated rapid melting, solidification and reheating, which exposes the material to non-equilibrium conditions that affect elemental segregation and the subsequent formation of solidification phases, either beneficial or detrimental. These variations are difficult to characterize due to the small length scale within the micron sized melt pool. To understand how the non-equilibrium conditions affect the initial solidification phases and their critical temperatures, a multi-length scale, multi modal approach has been taken to evaluate various methods for identifying the initial phases formed in the as-built Inconel 718 produced by laser-powder bed fusion (L-PBF) additive manufacturing (AM). Using a range of characterization tools from the bulk differential thermal analysis (DTA) and x-ray diffraction (XRD) to spatially resolved images using a variety of electron microscopy tools, a better understanding is obtained of how these minor phases can be properly identified regarding the amount and size, morphology and distribution. Using the most promising characterization techniques for investigation of the as-built specimens, those techniques were used to evaluate the specimens after various heat treatments. During the sequence of heat treatments, the initial as-built dendritic structures recrystallized into well-defined grains whose size was dependent on the temperature. Although the resulting strength was similar in all heat treated specimens, the elongation increased as the grain size was refined due to differences in the precipitated phase distribution and morphology. KW - Metal additive manufacturing KW - Inconel 718 KW - Heat treatment KW - Grain boundary precipitates KW - Laves phase PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-542758 DO - https://doi.org/10.3390/jmmp6010020 SN - 2504-4494 VL - 6 IS - 1 SP - 1 EP - 20 PB - MDPI CY - Basel AN - OPUS4-54275 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schneider, M. A1 - Bettge, Dirk A1 - Hilgenberg, Kai A1 - Binder, M. A1 - Dollmeier, K. A1 - Dreyer, M. A1 - Klöden, B. A1 - Schlingmann, T. A1 - Schmidt, J. T1 - Reproducibility and Scattering in Additive Manufacturing: Results from a Round Robin on PBF-LB/M AlSi10Mg Alloy T1 - Reproduzierbarkeit und Streuung bei der additiven Fertigung: Ergebnisse eines Ringversuchs mit einer PBF-LB/M AlSi10Mg-Legierung N2 - The round robin test investigated the reliability users can expect for AlSi10Mg additive manufactured specimens by laser powder bed fusion through examining powder quality, process parameter, microstructure defects, strength and fatigue. Besides for one outlier, expected static material properties could be found. Optical microstructure inspection was beneficial to determine true porosity and porosity types to explain the occurring scatter in properties. Fractographic analyses reveal that the fatigue crack propagation starts at the rough as-built surface for all specimens. Statistical analysis of the scatter in fatigue using statistical derived safety factors concludes that at a stress of 36.87 MPa the fatigue limit of 107 cycles could be reached for all specimen with a survival probability of 99.999 %. N2 - Im Rahmen eines Ringversuchs wurde durch die Untersuchung der Pulverqualität, der Prozessparameter, der Gefügefehler, der Festigkeit und der Ermüdung die Zuverlässigkeit bestimmt, die Nutzer von AlSi10Mg-Proben erwarten können, die mit pulverbettbasiertes Schmelzen mittels Laser (engl. Laser Powder Bed Fusion) gefertigt worden sind. Abgesehen von einem Ausreißer wurden die erwarteten statischen Materialeigenschaften erreicht. Eine optische Gefügeprüfung diente dazu, die tatsächliche Porosität und Arten von Porosität zu ermitteln, um die bei den Eigenschaften auftretende Streuung zu erklären. Fraktographische Unterschungen zeigen eine bei allen Proben von der rauen Oberfläche im As-built-Zustand ausgehende Ermüdungsrissausbreitung. Aus der statistischen Analyse der Streuung bezüglich der Ermüdung unter Anwendung von statistischen abgeleiteten Sicherheitsfaktoren geht hervor, dass alle Proben die Dauerfestigkeit von 107 Zyklen bei einer Spannung von 36,87 MPa mit einer Überlebenswahrscheinlichkeit von 99,999 % erreichten. KW - Additive manufacturing KW - Reproducibility KW - Reliability PY - 2022 DO - https://doi.org/10.1515/pm-2022-1018 SN - 2195-8599 VL - 59 IS - 10 SP - 580 EP - 614 PB - De Gruyter AN - OPUS4-55935 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schraa, Lucas A1 - Rodricks, Carol A1 - Kalinka, Gerhard A1 - Roetsch, Karl A1 - Scheffler, Christina A1 - Sambale, Anna A1 - Uhlig, Kai A1 - Stommel, Markus A1 - Trappe, Volker T1 - Characterisation and Modelling of the Fibre-Matrix Interface of Short Fibre Reinforced Thermoplastics using the Push-Out Technique N2 - This study investigates the suitability of the single fibre push-out (SFPO) test for the determination of the interfacial shear strength (IFSS) of injection moulded short fibre reinforced thermoplastics. It includes a detailed description of the required sample preparation steps and the boundary conditions of the SFPO setup. Experimental SFPO tests were carried out on PA66 GF, PPA GF35 and PA6 GF50 materials. Furthermore, a finite element model was set up to simulate the behaviour of these materials during this test. The numerical results showed that the inhomogeneous stress distribution in the fibre-matrix interphase during the test causes the measured apparent IFSS to underestimate the true strength of the interphase. The simulations put the experimental results into perspective and provide valuable information for the further development of the test setup. This study therefore not only provides new insights into the interphase strength of injection moulded short fibre reinforced thermoplastics, but also an insight into local load conditions during testing and thus an indication of the true IFSS. KW - GFRP KW - Interface KW - fibre matrix bond KW - single fibre push-out PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-626087 DO - https://doi.org/10.1016/j.compositesb.2025.112317 SN - 1879-1069 VL - 297 SP - 1 EP - 8 PB - Elsevier Ltd. CY - Niederlande AN - OPUS4-62608 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröder, Jakob A1 - Evans, Alexander A1 - Luzin, V. A1 - Abreu Faria, G. A1 - Degener, Sebastian A1 - Polatidis, E. A1 - Čapek, J. A1 - Kromm, Arne A1 - Dovzhenko, G. A1 - Bruno, Giovanni T1 - Texture-based residual stress analysis of laser powder bed fused Inconel 718 parts N2 - Although layer-based additive manufacturing methods such as laser powder bed fusion (PBF-LB) offer an immense geometrical freedom in design, they are typically subject to a build-up of internal stress (i.e. thermal stress) during manufacturing. As a consequence, significant residual stress (RS) is retained in the final part as a footprint of these internal stresses. Furthermore, localized melting and solidification inherently induce columnar-type grain growth accompanied by crystallographic texture. Although diffraction-based methods are commonly used to determine the RS distribution in PBF-LB parts, such features pose metrological challenges in their application. In theory, preferred grain orientation invalidates the hypothesis of isotropic material behavior underlying the common methods to determine RS. In this work, more refined methods are employed to determine RS in PBF-LB/M/IN718 prisms, based on crystallographic texture data. In fact, the employment of direction-dependent elastic constants (i.e. stress factors) for the calculation of RS results in insignificant differences from conventional approaches based on the hypothesis of isotropic mechanical properties. It can be concluded that this result is directly linked to the fact that the {311} lattice planes typically used for RS analysis in nickel-based alloys have high multiplicity and less strong texture intensities compared with other lattice planes. It is also found that the length of the laser scan vectors determines the surface RS distribution in prisms prior to their removal from the baseplate. On removal from the baseplate the surface RS considerably relaxes and/or redistributes; a combination of the geometry and the scanning strategy dictates the sub-surface RS distribution. KW - Additive manufacturing KW - Electron backscattered diffraction KW - Principal stress KW - Residual stress PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-578331 DO - https://doi.org/10.1107/S1600576723004855 SN - 1600-5767 VL - 56 IS - Pt 4 SP - 1076 EP - 1090 AN - OPUS4-57833 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröder, Jakob A1 - Evans, Alexander A1 - Polatidis, E. A1 - Čapek, J. A1 - Mohr, Gunther A1 - Serrano-Munoz, Itziar A1 - Bruno, Giovanni T1 - Understanding the impact of texture on the micromechanical anisotropy of laser powder bed fused Inconel 718 N2 - The manufacturability of metallic alloys using laser-based additive manufacturing methods such as laser powder bed fusion has substantially improved within the last decade. However, local melting and solidification cause hierarchically structured and crystallographically textured microstructures possessing large residual stress. Such microstructures are not only the origin of mechanical anisotropy but also pose metrological challenges for the diffraction-based residual stress determination. Here we demonstrate the influence of the build orientation and the texture on the microstructure and consequently the mechanical anisotropy of as-built Inconel 718. For this purpose, we manufactured specimens with [001]/[011]-, [001]- and [011]/[111]-type textures along their loading direction. In addition to changes in the Young’s moduli, the differences in the crystallographic textures result in variations of the yield and ultimate tensile strengths. With this in mind, we studied the anisotropy on the micromechanical scale by subjecting the specimens to tensile loads along the different texture directions during in situ neutron diffraction experiments. In this context, the response of multiple lattice planes up to a tensile strain of 10% displayed differences in the load partitioning and the residual strain accumulation for the specimen with [011]/[111]-type texture. However, the relative behavior of the specimens possessing an [001]/[011]- and [001]-type texture remained qualitatively similar. The consequences on the metrology of residual stress determination methods are discussed. KW - Laser powder bed fusion KW - Additive manufacturing KW - Electron backscatter diffraction KW - Tensile testing KW - Diffraction PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-555840 DO - https://doi.org/10.1007/s10853-022-07499-9 SN - 1573-4803 VL - 2022 IS - 57 SP - 15036 EP - 15058 PB - Springer Science + Business Media B.V. CY - Dordrecht AN - OPUS4-55584 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröder, Jakob A1 - Fritsch, Tobias A1 - Ferrari, Bruno A1 - Altmann, Mika León A1 - Bruno, Giovanni A1 - Toenjes, Anastasiya T1 - Laser powder bed fusion: Defect type influences critical porosity re-growth during reheating after hot isostatic pressing N2 - Despite the remarkable product design flexibility offered by additive manufacturing (AM) techniques, such as laser powder bed fusion, AM processes are susceptible to the formation of defects. In this context, the control of process parameters and the application of post-processing treatments, such as hot isostatic pressing (HIP), are of paramount importance to achieve the desired mechanical properties. The present study investigates the effectiveness of HIP as a function of process parameters in laser powder bed fused Ti-6V-4Al (PBF-LB/Ti64) using X-ray computed tomography. The process parameters are modified to obtain reference samples with low porosity, lack of fusion defects, or keyhole porosity. In all instances, subsurface keyhole porosity was observed in the as-built parts. Moreover, it was found that the efficacy of pore closure is dependent on the specific defect type. In the case of low porosity and keyhole pores, HIP resulted in effective closure. Conversely, larger lack of fusion defects were not closed due to their interconnectivity and the entrapment of argon gas. Subsequent heat treatments above the β-transus temperature allowed the investigation of the impact of defect type on porosity re-growth. For the first time, we reveal that lack of fusion defects are affected by considerable pore re-growth during post-HIP heat treatments of PBF-LB/Ti64. Such phenomenon is driven by the increasing internal pore pressure and local creep deformation at high temperatures. In contrast, re-growth is limited in samples with low porosity or keyhole pores. KW - Additive Manufacturing KW - Hot Isostatic Pressing KW - Titanium KW - Laser Powder Bed Fusion KW - X-ray Computed Tomography KW - Heat Treatment KW - Porosity PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-629289 DO - https://doi.org/10.1016/j.jmatprotec.2025.118839 VL - 340 SP - 1 EP - 9 PB - Elsevier B.V. AN - OPUS4-62928 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröder, Jakob A1 - Fritsch, Tobias A1 - Luzin, Vladimir A1 - Ferrari, Bruno A1 - Simón-Muzás, Juan A1 - Evans, Alexander A1 - Bruno, Giovanni T1 - Impact of scan strategy on principal stresses in laser powder bed fusion N2 - Additive manufacturing techniques, such as laser powder bed fusion (PBF-LB), are well known for their exceptional freedom in part design. However, these techniques are also characterized by the development of large thermal gradients during production and thus residual stress (RS) formation in produced parts. In this context, neutron diffraction enables the non-destructive characterization of the bulk RS distribution. By control of the thermal gradients in the powder-bed plane by scan strategy variation we study the impact of in-process scan strategy variations on the microstructure and the three-dimensional distribution of RS. Microstructural analysis by means of electron backscatter diffraction reveals sharp microstructure transitions at the interfaces ranging from 100-200 µm. The components of the RS tensor are determined by means of neutron diffraction and the principal stress directions and magnitudes are determined by eigenvalue decomposition. We find that the distribution of RS in the powder-bed plane corresponds to the underlying scan strategy. When the alternating scan vectors align with the x- and y sample coordinate axes, the principal stress directions co-align. In the present geometry, nearly transverse isotropic stress states develop when the scan vectors are either aligned 45° between x and y or continuously rotated by 67° between each layer. KW - Additive Manufacturing KW - Laser Powder Bed Fusion KW - Electron Backscatter Diffraction KW - Neutron Diffraction KW - Residual Stress KW - Principal Stress PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-607910 DO - https://doi.org/10.1016/j.matdes.2024.113171 SN - 0264-1275 VL - 244 SP - 1 EP - 10 PB - Elsevier Ltd. AN - OPUS4-60791 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröder, Jakob A1 - Han, Ying A1 - Fritsch, Tobias A1 - Hejazi, Bardia A1 - Ulbricht, Alexander A1 - Skrotzki, Birgit A1 - Bruno, Giovanni T1 - X-ray computed tomography quantifies primary phases and reveals crack morphology in high-cycle fatigue of aluminum alloy EN AW-2618A N2 - Since the introduction of high-strength aluminum alloys understanding their fatigue behavior is of high interest for the structural integrity of engineering components, in this context, the alloy EN AW-2618A gains its high strength from both nanometer size precipitates and micrometer size primary phases. The latter phases are often identified as crack initiation sites. In this study, it uses a combination of synchrotron and laboratory-based X-ray computed tomography to image and quantify such primary phases and the fatigue cracks appearing in interrupted tests. Based on the gray-level differences in the synchrotron X-ray computed tomography scans, this study is able to distinguish low- and high-absorbing particles. The dominant (volume fraction >99%) high absorbing primary phase can be quantified in good agreement with results of Thermo-Calc calculations. To image the fatigue crack, laboratory X-ray computed tomography scans are performed at different tensile loads to open the crack. The results show that with an appropriate crack opening tensile load, the fatigue crack morphology can be reliably revealed. Based on these results, the influence of the primary phases on the fatigue crack initiation and propagation are discussed. KW - X-ray computed tomography KW - Fatigue KW - Aluminum KW - Primary phases PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-632724 DO - https://doi.org/10.1002/adem.202500235 SN - 1527-2648 SP - 1 EP - 9 PB - Wiley-VCH CY - Weinheim AN - OPUS4-63272 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröder, Jakob A1 - Heldmann, A. A1 - Hofmann, M. A1 - Evans, Alexander A1 - Petry, W. A1 - Bruno, Giovanni T1 - Determination of diffraction and single-crystal elastic constants of laser powder bed fused Inconel 718 N2 - High energy X-ray synchrotron diffraction is used to investigate the elastic anisotropy of the nickel-based superalloy IN718 produced by laser powder bed fusion (PBF-LB). This material is characterized by a columnar grain morphology with some crystallographic texture. The material is subjected to elastic loading to determine the diffraction elastic constants (DECs). Furthermore, the single-crystal elastic constants (SCEC) are refined from these experiments using different micromechanical models. The results show that each micromechanical model predicts a specific set of SCEC that well describes the elastic anisotropy of PBF-LB/IN718. KW - Mechanical Engineering KW - Mechanics of Materials KW - Condensed Matter Physics KW - General Materials Science PY - 2023 DO - https://doi.org/10.1016/j.matlet.2023.135305 SN - 0167-577X VL - 353 SP - 1 EP - 5 PB - Elsevier B.V. AN - OPUS4-58477 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Serrano-Munoz, Itziar A1 - Agudo Jácome, Leonardo A1 - Thompsom, Sean A1 - Schneider, Judy T1 - On the transferability of post-processing heat treatments designed for PBF-LB IN718 alloys to directed energy deposition specimens N2 - Many processes are being developed for metal additive manufacturing (AM) which vary by their heat source and feedstock. The use of directed energy deposition (DED) is growing due to its ability to build larger structures outside of a contained powder bed chamber. However, the only standard exclusively for post-build heat treatment of AM IN718 is ASTM standard F3055-14a, developed for powder bed fusion (PBF). This study evaluates the applicability of this current heat treatment standard to AM IN718 specimens produced using two methods of DED: laser-blown powder (LP)-DED and arc-wire (AW)-DED. Electron microscopy and X-ray diffraction techniques were used to characterize the specimens in the as-built condition and after the full heat treatment (FHT) specified in F3055. No evidence of remaining Laves phase was observed in the two DED specimens after the FHT. Yield strengths for the DED specimens were 1049 MPa for FHT AW-DED and 1096 MPa for LP-DED, higher than the minimum stated for PBF-LB IN718 of 920 MPa. The size, morphology, inter-spacing, and diffraction patterns of the γ´ and γ´´ strengthening precipitates are found to be similar for both DED processes. Differences were observed in the microstructure evolution where the F3055 heat treatments resulted in partial recrystallization of the grain structure, with a higher content of annealing twins observed in the AW-DED. These microstructural differences correlate with differences in the resulting elongation to failure. Thus, it is proposed that variations in heat treatments are needed for optimizing IN718 produced by different AM processes. KW - Additive manufacturing variants KW - Directed energy deposition (DED) KW - Post-process heat treatments KW - SEM-EBSD and TEM microscopy KW - XRD phase analysis PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-628165 DO - https://doi.org/10.1007/s00170-025-15386-1 SN - 1433-3015 VL - 137 IS - 7-8 SP - 3949 EP - 3965 PB - Springer Science and Business Media LLC AN - OPUS4-62816 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Serrano-Munoz, Itziar A1 - Mishurova, Tatiana A1 - Thiede, Tobias A1 - Sprengel, Maximilian A1 - Kromm, Arne A1 - Nadammal, Naresh A1 - Nolze, Gert A1 - Saliwan Neumann, Romeo A1 - Evans, Alexander A1 - Bruno, Giovanni T1 - The residual stress in as‑built Laser Powder Bed Fusion IN718 alloy as a consequence of the scanning strategy induced microstructure N2 - The effect of two types of scanning strategies on the grain structure and build-up of Residual Stress (RS) has been investigated in an as-built IN718 alloy produced by Laser Powder Bed Fusion (LPBF). The RS state has been investigated by X-ray diffraction techniques. The microstructural characterization was performed principally by Electron Backscatter Diffraction (EBSD), where the application of a post-measurement refinement technique enables small misorientations (< 2°) to be resolved. Kernel average misorientation (KAM) distributions indicate that preferably oriented columnar grains contain higher levels of misorientation, when compared to elongated grains with lower texture. The KAM distributions combined with X-ray diffraction stress maps infer that the increased misorientation is induced via plastic deformation driven by the thermal stresses, acting to self-relieve stress. The possibility of obtaining lower RS states in the build direction as a consequence of the influence of the microstructure should be considered when envisaging scanning strategies aimed at the mitigation of RS. KW - Additive manufacturing KW - LPBF KW - Residual stress KW - Inconel 718 KW - Kernel average misorientation KW - Texture PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-511769 DO - https://doi.org/10.1038/s41598-020-71112-9 VL - 10 IS - 1 SP - 14645 AN - OPUS4-51176 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Shimada, Y. A1 - Ikeda, Yuki A1 - Yoshida, K. A1 - Sato, M. A1 - Chen, J. A1 - Du, Y. A1 - Inoue, K. A1 - Maaß, Robert A1 - Nagai, Y. A1 - Konno, T. T1 - In situ thermal annealing transmission electron microscopy of irradiation induced Fe nanoparticle precipitation in Fe–Si alloy N2 - The typical experimental conditions inside a transmission electron microscope (TEM), such as ultra-high vacuum, high-energy electron irradiation, and surface effects of ultrathin TEM specimens, can be the origin of unexpected microstructural changes compared with that of bulk material during in situ thermal-annealing experiments. In this paper, we report on the microstructural changes of a Fe–15%Si alloy during in situ TEM annealing, where, in its bulk form, it exhibits an ordering transformation from D03 to B2 at 650 °C. Using a heating-pot type double tilt holder with a proportional–integral–differential control system, we observed the precipitation of α-Fe both at the sample surface and inside the sample. Surface precipitates formed via surface diffusion are markedly large, several tens of nm, whereas precipitates inside the specimen, which are surrounded by Fe-poor regions, reach a maximum size of 20 nm. This unexpected microstructural evolution could be attributed to vacancies on Si sites, which are induced due to high-energy electron irradiation before heating, as well as enhanced thermal diffusion of Fe atoms. KW - In situ thermal-annealing experiment KW - Microstructural changes of a Fe Si alloy KW - Microstructural evolution PY - 2022 DO - https://doi.org/10.1063/5.0070471 SN - 0021-8979 VL - 131 IS - 16 SP - 1 EP - 8 PB - AIP Publishing AN - OPUS4-54728 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Singh, Shobhit Pratap A1 - Löwe, Peter A1 - Schriever, Sina A1 - Olbricht, Jürgen A1 - Rehmer, Birgit A1 - Nolze, Gert A1 - Skrotzki, Birgit T1 - High-throughput creep evaluation of IN738LC in bending using digital image correlation at 850 °C N2 - High-temperature alloys, when used in structural applications, undergo slow time-dependent deformation known as creep. Assessing creep behavior is critical for estimating the in-service life of these alloys. Conventionally, uniaxial creep tests are widely conducted at elevated temperatures to determine creep rates. In recent years, bending creep of cantilevers, when combined with digital image correlation (DIC), has emerged as a promising high-throughput technique for rapidly estimating creep life. However, the applicability of bending creep above 700 ◦C for high-temperature alloys using DIC has not been fully established. In this work, we compare uniaxial creep rates of the nickel-based superalloy IN738LC with bending creep rates measured at 850 ◦C using high-temperature DIC. The bending creep data show excellent agreement with uniaxial creep results in the stress range of 240–360 MPa. The measured creep xponent, a critical rate-determining parameter, is found to be ~8 for both uniaxial and bending creep, with the rate data scattered within a factor of two. An in-house experimental setup was developed to perform bending creep tests at high temperatures, with strain monitored through DIC. Our results demonstrate that bending creep, combined with DIC, provides a reliable and efficient method for creep testing of high-temperature alloys. Compared to conventional uniaxial creep experiments, this approach requires significantly less time and material, thereby reducing effort, energy, and cost. We anticipate that this technique will serve as a foundation for testing precious high-temperature materials. For instance, in ongoing rapid discoveries of advanced alloys, in-service creep life can be evaluated much faster with reduced material requirements. Moreover, this method holds strong potential for application to high-entropy alloys and additively manufactured alloys designed for demanding high-temperature environments. KW - Digital image correlation KW - Bending creep KW - Nickel-based superalloys KW - High throughput testing KW - High-temperature materials PY - 2025 UR - https://www.sciencedirect.com/science/article/pii/S0921509325017034?via%3Dihub DO - https://doi.org/10.1016/j.msea.2025.149479 VL - 950 SP - 1 EP - 12 PB - Elsevier B.V. AN - OPUS4-64814 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sommer, Konstantin A1 - Agudo Jácome, Leonardo A1 - Hesse, René A1 - Bettge, Dirk T1 - Revealing the nature of melt pool boundaries in additively manufactured stainless steel by nano-sized modulation N2 - In the current study, the 3D nature of the melt pool boundaries (MPBs) in a 316 L austenitic steel additively manufactured by laser-based powder bed fusion (L-PBF) is investigated. The change of the cell growth direction and its relationship to the MPBs is investigated by transmission electron microscopy. A hitherto unreported modulated substructure with a periodicity of 21 nm is further discovered within the cell cores of the cellular substructure, which results from a partial transformation of the austenite, which is induced by a Ga+ focused ion beam. While the cell cores show the modulated substructure, cell boundaries do not. The diffraction pattern of the modulated substructure is exploited to show a thickness ≥200 nm for the MPB. At MPBs, the cell walls are suppressed, leading to continuously connecting cell cores across the MPB. This continuous MPB is described either as overlapping regions of cells of different growing directions when a new melt pool solidifies or as a narrow planar growth preceding the new melt pool. KW - Additive manufacturing KW - Austenitic steel 316L KW - Melt pool boundary KW - Microstructural characterization KW - Transmission electron microscopy PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-547295 DO - https://doi.org/10.1002/adem.202101699 SN - 1527-2648 VL - 24 IS - 6 SP - 1 EP - 11 PB - Wiley-VCH CY - Weinheim AN - OPUS4-54729 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sonntag, Nadja A1 - Jürgens, Maria A1 - Skrotzki, Birgit A1 - Olbricht, Jürgen T1 - Creep-fatigue of P92 in service-like tests with combined stress- and strain-controlled dwell times N2 - Complex service-like relaxation- and creep-fatigue tests with strain- and stress-controlled dwells and fatigue cycle durations of approx. 2200 s were performed exemplarily on a grade P92 steel at 620 ◦C in this study. The results indicate deviations in the prevailing creep mechanisms of long-term relaxation and creep dwells, affecting subsequent dwells, load shifts, and the macroscopic softening behavior quite differently. In addition, fracture surfaces and longitudinal metallographic sections reveal intergranular crack growth for complex loading with stress-controlled dwells, whereas complex strain-controlled tests enhance oxidation and transgranular crack propagation. These findings substantiate the limited transferability of relaxation-fatigue to creep-fatigue conditions. KW - Tempered martensite-ferritic steel KW - P92 KW - Dwell periods KW - Creep-fatigue interaction KW - Stress relaxation PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-564239 DO - https://doi.org/10.1016/j.ijfatigue.2022.107381 SN - 0142-1123 VL - 168 SP - 1 EP - 12 PB - Elsevier Ltd. AN - OPUS4-56423 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sonntag, Nadja A1 - Jürgens, Maria A1 - Uhlemann, Patrick A1 - Skrotzki, Birgit A1 - Olbricht, Jürgen T1 - Experimental data from service-like creep-fatigue experiments on grade P92 steel N2 - This article refers to the research article entitled “Creep-Fatigue of P92 in Service-Like Tests with Combined Stress- and Strain-Controlled Dwell Times” [1]. It presents experimental mechanical data from complex service-like creep-fatigue experiments performed isothermally at 620 °C and a low strain amplitude of 0.2 % on tempered martensite-ferritic grade P92 steel. The data sets in text file format provide cyclic deformation (min. and max. stresses) and the total (hysteresis) data of all recorded fatigue cycles for three different creep-fatigue experiments: 1) a standard relaxation fatigue (RF) test with symmetrical dwell times of three minutes introduced at minimum and maximum strain, 2) a fully strain-controlled service-like relaxation (SLR) test combining these three-minute peak strain dwells with a 30-minute dwell in between at zero strain, and 3) a partly stress-controlled service-like creep (SLC) test combining the three-minute peak strain dwells with 30-minute dwells at constant stress. Such service-like (SL) tests with additional long-term stress- and strain-controlled dwell times are non-standard, rare, and expensive, making these data very valuable. They may be used to approximate cyclic softening in the technically relevant range, for the design of complex SL experiments, or for detailed analyses of stress-strain hystereses (e.g., for stress or strain partitioning methods, for the determination of hysteresis energies (work), inelastic strain components, etc.). In addition, the latter analyses may supply important input for advanced parametric lifetime modeling of components under creep-fatigue loading or model calibration parameters. KW - Tempered martensite-ferritic steel KW - Creep KW - Stress relaxation KW - Creep-fatigue KW - Dwell times PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-578407 DO - https://doi.org/10.1016/j.dib.2023.109333 SN - 2352-3409 VL - 49 SP - 1 EP - 9 PB - Elsevier Inc. AN - OPUS4-57840 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sonntag, Nadja A1 - Piesker, Benjamin A1 - Ávila Calderón, Luis A1 - Mohr, Gunther A1 - Rehmer, Birgit A1 - Agudo Jácome, Leonardo A1 - Hilgenberg, Kai A1 - Evans, Alexander A1 - Skrotzki, Birgit T1 - Tensile and Low‐Cycle Fatigue Behavior of Laser Powder Bed Fused Inconel 718 at Room and High Temperature N2 - This study investigates the room‐ and high‐temperature (650 °C) tensile and low‐cycle‐fatigue behavior of Inconel 718 produced by laser powder bed fusion (PBF‐LB/M) with a four‐step heat treatment and compares the results to the conventional wrought material. The microstructure after heat treatment is characterized on different length scales. Compared to the wrought variant, the elastic and yield properties are comparable at both test temperatures while tensile strength, ductility, and strain hardening capacity are lower. The fatigue life of the PBF‐LB/M variant at room temperature is slightly lower than that of the wrought material, while at 650 °C, it is vice versa. The cyclic stress response for both material variants is characterized by cyclic softening, which is more pronounced at the higher test temperature. High strain amplitudes (≥0.7%) at room temperature and especially a high testing temperature result in the formation of multiple secondary cracks at the transitions of regions comprising predominantly elongated grain morphology and columns of stacked grains with ripple patterns in the PBF‐LB/M material. This observation and pronounced crack branching and deflection indicate that the cracks are controlled by sharp micromechanical gradients and local crystallite clusters. KW - Additive manufacturing KW - Fatigue damage KW - Heat treatment KW - Inconel 718 KW - Laser powder bed fusion KW - Low-cycle fatigue KW - Tensile strength PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-599316 DO - https://doi.org/10.1002/adem.202302122 SN - 1527-2648 SP - 1 EP - 17 PB - Wiley AN - OPUS4-59931 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sprengel, Maximilian A1 - Ulbricht, Alexander A1 - Evans, Alexander A1 - Kromm, Arne A1 - Sommer, Konstantin A1 - Werner, Tiago A1 - Kelleher, J. A1 - Bruno, Giovanni A1 - Kannengießer, Thomas T1 - Towards the optimization of post-laser powder bed fusion stress-relieve treatments of stainless steel 316L N2 - This study reports on the stress relaxation potential of stress-relieving heat treatments for laser powder bed fused 316L. The residual stress is monitored non-destructively using neutron diffraction before and after the heat treatment. Moreover, the evolution of the microstructure is analysed using scanning electron microscopy. The results show, that a strong relaxation of the residual stress is obtained when applying a heat treatment temperature at 900°C. However, the loss of the cellular substructure needs to be considered when applying this heat treatment strategy. KW - Residual stress KW - Additive manufacturing KW - Neutron diffraction KW - Projekt AGIL - Alterung additiv gefertigter metallischer Materialien und Komponenten PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-536045 DO - https://doi.org/10.1007/s11661-021-06472-6 SN - 1543-1940 VL - 52 IS - 12 SP - 5342 EP - 5356 PB - Springer CY - Boston AN - OPUS4-53604 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stargardt, Patrick A1 - Bresch, Sophie A1 - Falkenberg, Rainer A1 - Mieller, Björn T1 - Effect of Reaction Layers on Internal Stresses in Co‐Fired Multilayers of Calcium Manganate and Calcium Cobaltite N2 - A widespread recovery of waste heat requires a cost‐effective production of thermoelectric generators. Thermoelectric oxides are predestined for use at high temperatures. For manufacturing reasons, a multilayer generator design will be easily scalable and cost‐effective. To evaluate the potential of ceramic multilayer technology for that purpose, a multilayer of the promising thermoelectric oxides calcium cobaltite (Ca3Co4O9), calcium manganate (CMO, CaMnO3), and glass–ceramic insulation layers is fabricated. Cracks and reaction layers at the interfaces are observed in the microstructure. The compositions of these reaction layers are identified by energy‐dispersive X‐ray spectroscopy and X‐ray diffraction. Mechanical and thermal properties of all layers are compiled from literature or determined by purposeful sample preparation and testing. Based on this data set, the internal stresses in the multilayer after co‐firing are calculated numerically. It is shown that tensile stresses in the range of 50 MPa occur in the CMO layers. The reaction layers have only a minor influence on the level of these residual stresses. Herein, it is proven that the material system is basically suitable for multilayer generator production, but that the co‐firing process and the layer structure must be adapted to improve densification and reduce the tensile stresses in the CMO. KW - Ceramic multilayers KW - Co-firings KW - Internal stresses PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-601626 DO - https://doi.org/10.1002/pssa.202300956 SP - 1 EP - 9 PB - Wiley VHC-Verlag AN - OPUS4-60162 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stephan-Scherb, Christiane A1 - Lehmusto, Juho A1 - Falk, Florian A1 - Sobol, Oded A1 - Pint, Bruce T1 - Comprehensive insights into competitive oxidation/sulfidation reactions on binary ferritic alloys at high temperatures N2 - Interpreting high-temperature corrosion induced by mixed-gas atmospheres is challenging due to the different contributions of oxidizing gases. Here, a comprehensive study on the combined oxidation/sulfidation using label molecules is presented. Fe-Cr model alloys with 2 wt% and 9 wt% Cr were isothermally exposed using a volumetric mixture of 0.5%S16O2/27%H218O and 0.5%S16O2/7%H218O at 650 ◦C for 5 h and then characterized by secondary ion mass spectroscopy (SIMS). Additionally, the reactions were followed in-situ utilizing energy dispersive X-ray diffraction. The study showed that both S16O2 and H218O contribute to the oxidation of the alloys but to different extents depending on the Cr-content. KW - SEM KW - Steel KW - Iron KW - SIMS PY - 2022 DO - https://doi.org/10.1016/j.corsci.2022.110236 SN - 0010-938X VL - 203 SP - 1 EP - 13 PB - Elsevier Ltd. AN - OPUS4-58992 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stephan-Scherb, Christiane A1 - Menneken, Martina A1 - Weber, Kathrin A1 - Agudo Jácome, Leonardo A1 - Nolze, Gert T1 - Elucidation of orientation relations between Fe-Cr alloys and corrosionproducts after high temperature SO2 corrosion N2 - The early stages of corrosion of Fe-Cr-model alloys (2 and 9 % Cr) were investigated after exposure at 650 °C in0.5 % SO2containing gas by electron backscattered diffraction (EBSD) and transmission electron microscopy(TEM). The impact of the grain orientation of the base alloy on the orientation relations of the corrosion productsis presented. After 2 min–5 min exposure the formation of a multi-layered corrosion zone was discovered. Aclear orientation relationship between ferrite and the (Fe,Cr)3O4 spinel could be demonstrated. The obtainedresults show the importance of the grain orientation on oxidation resistance. KW - Iron KW - TEM KW - SEM KW - High temperature corrosion PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-508911 DO - https://doi.org/10.1016/j.corsci.2020.108809 VL - 174 SP - 1 EP - 11 PB - Elsevier AN - OPUS4-50891 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stephan-Scherb, Christiane A1 - Schulz, Wencke A1 - Schneider, M. A1 - Karafiludis, Stephanos A1 - Laplanche, G. T1 - High-Temperature Oxidation in Dry and Humid Atmospheres of the Equiatomic CrMnFeCoNi and CrCoNi High- and Medium-Entropy Alloys N2 - Surface degradation phenomena of two model equiatomic alloys from the CrMnFeCoNi alloy system were investigated in 2% O2 and 10% H2O (pO2 = 0.02 and 10−7 atm, respectively) at 800 °C for times up to 96 h. The crystallographic structures, morphologies, and chemical compositions of the corrosion layers developing on CrMnFeCoNi and CrCoNi were comparatively analyzed by mass gain analysis, X-ray diffraction, and scanning electron microscopy combined with energy-dispersive X-ray spectroscopy and electron backscatter diffraction. The oxidation resistance of CrMnFeCoNi is relatively poor due to the fast growth of porous Mnoxide(s). CrCoNi forms an external chromia layer that is dense and continuous in a dry 2% O2 atmosphere. This layer buckles and spalls off after exposure to 10% H2O atmosphere. Beneath the chromia layer, a Cr-depleted zone forms in the CrCoNi alloy in both environments. As the oxide scale spalls off in the H2O-containing atmosphere, a secondary chromia layer was observed and correspondingly enlarges the Cr-depleted zone. In contrast, as the chromia layer remains without significant spallation when CrCoNi is exposed to a dry oxidizing atmosphere, the region depleted in Cr is narrower. KW - High temperature oxidation KW - High entropy alloys KW - Medium entropy alloys KW - CrMnFeCoNi KW - CrCoNi KW - Mn-oxides PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-517859 DO - https://doi.org/10.1007/s11085-020-10014-7 SN - 0030-770X VL - 95 IS - 1-2 SP - 105 EP - 133 PB - Springer AN - OPUS4-51785 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stinville, J.C. A1 - Charpagne, M.A. A1 - Maaß, Robert A1 - Proudhon, H. A1 - Ludwig, W. A1 - Callahan, P.G. A1 - Wang, F. A1 - Beyerlein, I.J. A1 - Echlin, M.P. A1 - Pollock, T.M. T1 - Insights into Plastic Localization by Crystallographic Slip from Emerging Experimental and Numerical Approaches N2 - Advanced experimental and numerical approaches are being developed to capture the localization of plasticity at the nanometer scale as a function of the multiscale and heterogeneous microstructure present in metallic materials. These innovative approaches promise new avenues to understand microstructural effects on mechanical properties, accelerate alloy design, and enable more accurate mechanical property prediction. This article provides an overview of emerging approaches with a focus on the localization of plasticity by crystallographic slip. New insights into the mechanisms and mechanics of strain localization are addressed. The consequences of the localization of plasticity by deformation slip for mechanical properties of metallic materials are also detailed. KW - Slip localization KW - Metallic materials KW - Experimental and numerical techniques KW - Mechanical properties KW - Plasticity PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-578398 DO - https://doi.org/10.1146/annurev-matsci-080921-102621 SN - 1531-7331 VL - 53 SP - 275 EP - 317 AN - OPUS4-57839 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Suárez Ocano, Patricia A1 - Agudo Jácome, Leonardo A1 - Lopez-Galilea, I. A1 - Darvishi Kamachali, Reza A1 - Fries, S. G. T1 - Data regarding the experimental findings compared with CALPHAD calculations of the AlMo0.5NbTa0.5TiZr refractory high entropy superalloy N2 - This contribution contains the raw data used to compare experimental results with thermodynamic calculations using the CALPHAD method, which is related to the research article “The AlMo0.5NbTa0.5TiZr refractory high entropy superalloy: experimental findings and comparison with calculations using the CALPHAD method” [1] , and therefore this article can be used as a basis for interpreting the data contained therein. The AlMo0.5NbTa0.5TiZr refractory superalloy was characterized in the cast and annealed condition (1400 °C for 24 h) in order to measure grain size and to identify and measure the size and area fraction of the phases present. The raw data of this article include X-ray diffraction (XRD) measurements, microstructural characterization by scanning and transmission electron microscopy (SEM and TEM), and elemental analysis by energy dispersive X-ray spectroscopy (EDX). XRD includes the determination of phases and the lattice parameters (A2, B2, and hexagonal structure). Microstructural analysis by scanning and transmission electron microscopy includes (1) identification of composition, size, and volume fraction of the present phases and (2) determination of grain size. Based on these experimental data, it is possible to identify similarities and discrepancies with the data calculated using the CALPHAD method for the alloy under study in Ref. [1] , which provides the basis for better and more efficient development of reliable databases. KW - Transmission electron microscopy KW - Scanning electron microscopy KW - Microstructural characterization KW - Refractory high entropy alloys PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-568009 DO - https://doi.org/10.1016/j.dib.2022.108858 SN - 2352-3409 VL - 46 SP - 1 EP - 19 PB - Elsevier CY - Amsterdam AN - OPUS4-56800 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Suárez Ocano, Patricia A1 - Fries, S. G. A1 - Lopez-Galilea, I. A1 - Darvishi Kamachali, Reza A1 - Roik, J. A1 - Agudo Jácome, Leonardo T1 - The AlMo0.5NbTa0.5TiZr refractory high entropy superalloy: Experimental findings and comparison with calculations using the CALPHAD method N2 - Detailed microstructural characterization of the AlMo0.5NbTa0.5TiZr refractory high entropy superalloy in the as-cast state is reported for first time and compared with the state annealed at 1400 oC for 24 h. The former shows a dendritic structure, with a mixture of A2/B2 phases < 20 nm in both the dendritic and interdendritic regions. A mostly amorphous phase, rich in Al and Zr, is found within the interdendritic region. The annealed state reproduced the combination of A2/B2/Al-Zr-rich phases reported previously. Calculations from two relevant ThermoCalc databases were compared with the experimental results. Equilibrium calculations were compared with results for the annealed alloy, whereas solidification paths calculated using Scheil-Gulliver model were used for comparison with the as-cast alloy. A previously hypothesized spinodal decomposition during cooling as the mechanism responsible for the patterned A2/B2 microstructure is confirmed via the CALPHAD calculations, pointing to its use as an efficient design tool for such alloys. Finally, the comparison between the experimental and computational findings allowed better understanding the solidification path and equilibrium stability of this alloy, giving a base to make better decisions on the field of new refractory superalloy design. KW - CALPHAD database analysis KW - Refractory superalloys KW - Chemically complex alloy KW - Characterization KW - Microstructure PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-545906 DO - https://doi.org/10.1016/j.matdes.2022.110593 SN - 1873-4197 VL - 217 SP - 1 EP - 13 PB - Elsevier CY - Amsterdam AN - OPUS4-54590 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Suárez Ocano, Patricia A1 - Manzoni, Anna Maria A1 - Lopez-Galilea, I. A1 - Ruttert, B. A1 - Laplanche, G. A1 - Agudo Jácome, Leonardo T1 - Influence of cooling rate on the microstructure and room temperature mechanical properties in the refractory AlMo0.5NbTa0.5TiZr superalloy N2 - Refractory chemically complex alloys with bcc-based microstructures show great potential for high-temperature applications but most of them exhibit limited room-temperature ductility, which remains a challenge. One such example is the AlMo0.5NbTa0.5TiZr alloy, mainly consisting of a nano-scaled structure with an ordered B2 matrix and a high-volume fraction of aligned cuboidal and coherently embedded A2 precipitates. This work aims to investigate how the cooling rate after hot isostatic pressing of the AlMo0.5NbTa0.5TiZr alloy affects its microstructure and its resulting hardness and fracture toughness at room temperature. A slow cooling rate of 5 °C/min leads to a coarse microstructure consisting of aligned slabs (mean A2 precipitate ≈ 25 nm) with a nanohardness of about 8 GPa. In contrast, after the fastest cooling rate (30 °C/min), the A2 precipitates become more cubic with an edge length of ≈ 16 nm, resulting in an increase in nanohardness by 10 %. The fracture toughness is roughly independent of the cooling rate and its mean value (≈ 4.2 MPa∙m1/2) resembles that of some B2 intermetallics and other A2/B2 alloys. As the lattice misfit between the A2 and B2 phases is known to play a key role in microstructure formation and evolution, its temperature dependence between 20 and 900 °C was investigated. These findings offer insights into the evolution of the microstructure and room-temperature mechanical properties of the AlMo0.5NbTa0.5TiZr alloy, which could help the development of advanced chemically complex alloys. KW - High entropy alloy KW - Lattice misfit KW - Scanning electron microscopy KW - Transmission electron microscopy KW - X-ray diffraction KW - Refractory alloy PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-572809 DO - https://doi.org/10.1016/j.jallcom.2023.169871 SN - 0925-8388 VL - 949 SP - 169871 PB - Elsevier B.V. AN - OPUS4-57280 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Suárez Ocaño, Patricia A1 - Ávila Calderón, Luis A1 - Agudo Jácome, Leonardo A1 - Rehmer, Birgit A1 - Mohr, Gunther A1 - Evans, Alexander A1 - Skrotzki, Birgit T1 - Effect of 700–900 °C heat treatments and room and high temperature tensile deformation on the microstructure of laser powder bed fused 316L stainless steel N2 - The effect of post-processing heat treatments on the hierarchical microstructure evolution and mechanical strength of the austenitic stainless steel 316L produced by laser powder bed fusion has been investigated. Heat treatments between 700 and 900 ◦C and 0.5 to 3 h, were applied to samples treated at 450 ◦C for 4 h. The results showed a stable microstructure at all studied temperatures and times in terms of grain size, morphology, aspect ratio, density of low-angle grain boundaries, and texture. However, temperature and time promoted the diffusion of segregated elements together with a reduction in dislocation density and disappearance of the cellular structure. This was associated with a reduction in hardness and tensile proof strength at both room and high temperature. In addition, microstructural characterization coupled with thermodynamic CALPHAD-based equilibrium calculations showed that the formation of carbides and intermetallic phases was already visible after annealing at 800 ◦C for 3 hours, although these intermetallics did not affect the tensile properties at this level. Analysis of the microstructure evolution after tensile deformation showed differences in the deformation mechanisms at room and high temperature, with twinning and martensitic transformation occurring at room temperature, the latter not widely reported for additively manufactured 316L. Finally, comparisons with similar materials produced under comparable conditions showed differences in the tensile properties, attributed to differences in chemical composition and the associated presence of stacking faults in the undeformed state. KW - Additive manufacturing KW - 316L stainless steel KW - Heat treatments KW - Tensile properties KW - Microstructure PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-632471 DO - https://doi.org/10.1016/j.msea.2025.148469 SN - 0921-5093 VL - 939 SP - 1 EP - 24 PB - Elsevier CY - Amsterdam AN - OPUS4-63247 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Svetlov, I. L. A1 - Epishin, A. I. A1 - Petrushin, N. V. A1 - Gerstein, G. A1 - Nolze, Gert A1 - Maier, H. J. T1 - Creep of Directionally Solidified Eutectics Ni/Ni3 Al–NbC under Thermal Cycling N2 - A nickel-based eutectic alloy with a γ/γ'-NbC structure was directionally solidified with a planar front. The specimens were tested for creep under sawtooth thermal cycling in the temperature range from 600 to 1100°C. It has been established that the lifetime under the conditions of thermal cycling is about five times shorter than it is predicted by the linear damage accumulation rule on the basis of results of isothermal creep tests. Faster creep under thermal cycling is caused by the rapid coarsening of the γ/γ' microstructure due to the periodic partial dissolution and reprecipitation of the γ' phase in heating and cooling half-cycles. KW - High temperature nickel-based eutectic alloys KW - γ/γ' matrix KW - Carbide phase NbC KW - In-situ composites KW - Creep under thermal cycling PY - 2022 DO - https://doi.org/10.1134/S2075113322040347 SN - 2075-1133 VL - 13 IS - 4 SP - 1099 EP - 1108 PB - Springer Science + Business Media CY - Dordrecht AN - OPUS4-55163 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Swaminathan, Srinivasan A1 - Sun, K. A1 - Was, G. S. T1 - Decoupling the roles of grain boundary oxidation and stress in IASCC of neutron-irradiated 304L stainless steel N2 - Irradiation assisted stress corrosion cracking (IASCC) is known to be a combination of applied stress, and a corrosive environment in irradiated materials, but an appropriate understanding of how each of these components affects cracking is not yet clear. In this work, we isolate the role of grain boundary (GB) oxidation in IASCC. For this purpose, solution-annealed 304L stainless steel irradiated in reactor to 5.4 or 69 dpa was studied using a miniaturized four-point bend technique. Two modes of bend tests were conducted; straining in simulated pressurized water reactor primary water (PW) at 320 ◦C in an incremental manner, and pre-oxidation in PW at 320 ◦C without application of stress followed by dynamic straining in purified Ar at the same temperature until crack initiation. Exposure of the 5.4 dpa sample for 210 h in high temperature water initiated cracks in Ar at 60% of the yield stress (0.6YS), whereas the companion sample of the same dose exposed for 1010 h cracked in Ar at 0.5YS. The long-term exposure in water led to GB oxidation that ultimately lowered the crack initiation stress. Dynamic straining in water resulted in larger crack lengths and greater crack depths indicating stress accelerated oxidation and cracking. Dislocation pile-ups at dislocation channel-grain boundary sites provide an amplification of the applied stress to a level consistent with the fracture stress of the grain boundary oxide, providing an explanation for IASCC that occurs at applied stresses well below the irradiated yield stress of the alloy. There was no evidence of cracking upon straining of an unoxidized 69 dpa sample in Ar to well above yield, confirming that the irradiated state is not inherently susceptible to intergranular (IG) cracking and that oxidized GBs are responsible for initiation of IG cracking. KW - Stress corrosion cracking KW - Grain boundary oxidation KW - Stainless steel KW - Crack initiation KW - IASCC PY - 2023 DO - https://doi.org/10.1016/j.jnucmat.2023.154604 SN - 0022-3115 VL - 585 SP - 1 EP - 15 PB - Elsevier B.V. AN - OPUS4-58233 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sänger, Johanna C. A1 - Riechers, Birte A1 - Pauw, Brian Richard A1 - Maaß, Robert A1 - Günster, Jens T1 - Microplastic response of 2PP‐printed ceramics N2 - AbstractTwo‐photon polymerization (2PP) additive manufacturing (AM) utilizes feedstocks of ceramic nanoparticles of a few nanometers in diameter, enabling the fabrication of highly accurate technical ceramic design with structural details as small as 500 nm. The performance of these materials is expected to differ from conventional AM ceramics, as nanoparticles and three‐dimensional printing at high resolution introduce new microstructural aspects. This study applies 2PP‐AM of yttria‐stabilized zirconia to investigate the mechanical response behavior under compressive load, probing the influence of smallest structural units induced by the line packing during the printing process, design of sintered microblocks, and sintering temperature and thereby microstructure. We find a dissipative mechanical response enhanced by sintering at lower temperatures than conventional. The pursued 2PP‐AM approach yields a microstructured material with an increased number of grain boundaries that proposedly play a major role in facilitating energy dissipation within the here printed ceramic material. This microplastic response is further triggered by the filigree structures induced by hollow line packing at the order of the critical defect size of ceramics. Together, these unique aspects made accessible by the 2PP‐AM approach contribute to a heterogeneous nano‐ and microstructure, and hint toward opportunities for tailoring the mechanical response in future ceramic applications. KW - Manufacturing KW - Mechanical properties KW - Microstructure KW - Plasticity KW - Zirconia: yttria stabilized PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-605176 DO - https://doi.org/10.1111/jace.19849 SN - 1551-2916 VL - 107 IS - 10 SP - 6636 EP - 6645 PB - Wiley CY - Oxford AN - OPUS4-60517 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -