TY - CONF A1 - Lemiasheuski, Anton A1 - Bajer, Evgenia A1 - Oder, Gabriele A1 - Göbel, Artur A1 - Hesse, Rene A1 - Bettge, Dirk T1 - Development of an Automated 3D Metallography System (RASI) and its Application in Microstructure Analysis N2 - Many microstructural features exhibit non-trivial geometries, which can only be derived to a limited extent from two-dimensional images. E.g., graphite arrangements in lamellar gray cast iron have complex geometries, and the same is true for additively manufactured materials and three-dimensional conductive path structures. Some can be visualized using tomographic methods, but some cannot be due to weak contrast and/or lack of resolution when analyzing macroscopic objects. Classic metallography can help but must be expanded to the third dimension. The method of reconstructing three-dimensional structures from serial metallographic sections surely is not new. However, the effort required to manually assemble many individual sections into image stacks is very high and stands in the way of frequent application. For this reason, an automated, robot-supported 3D metallography system is being developed at BAM, which carries out the steps of repeated preparation and image acquisition on polished specimen. Preparation includes grinding, polishing and optionally etching of the polished surface. Image acquisition comprises autofocused light microscopic imaging at several magnification levels. The image stacks obtained are then pre-processed, segmented, and converted into 3D models, which in the result appear like microtomographic models, but with high resolution at large volume. Contrasting by classical chemical etching reveals structures that cannot be resolved using tomographic methods. The integration of further imaging and measuring methods into this system is underway. Some examples will be discussed in the presentation. T2 - Euromat 2023 CY - Frankfurt a. M., Germany DA - 04.07.2023 KW - Metallography KW - 3D Reconstruction KW - Roboter KW - Automation KW - Microstructure PY - 2023 AN - OPUS4-58202 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Swaminathan, Srinivasan A1 - Kumar, S. A1 - Kranzmann, Axel A1 - Hesse, Rene A1 - Goldbeck, Hennig A1 - Fantin, Andrea T1 - Corrosion characteristics of 316L stainless steel in oxide-rich molten solar salt at 600◦C N2 - An attempt has been made in this work, to observe the influence on alloy aging by the sodium oxide (Na2O) in solar salt (60 wt% NaNO3 + 40 wt% KNO3). The accelerated aging was established by adding Na2O (0.005, 0.07, 0.135 and 0.2 wt%) to the solar salt and their effect on corrosion of 316L stainless steel (SS) at 600 ◦C in that oxide-rich solar salts for 168 h in synthetic air was investigated. Corrosion is significantly more in oxide-rich solar salt compared to pure solar salt. Strikingly, the oxide scale-base metal interface is wavy in solar salt containing 0.005 % Na2O clearly shows the oxide addition to salt melt influences Cr-rich inner oxide layer formation and its selective dissolution at early stage that leads to non-uniform corrosion. Interestingly, with increase of Na2O to 0.07 %, steel corrosion proceeded uniformly by accelerated disintegration of Cr-rich inner layer and subsequent dissolution. Severe scale spallation and weight loss in nitrate melt containing 0.2 % Na2O fostering more rapid corrosion, alarming that substantial tolerance of oxide content in solar salt is ≥ 0.135 % for an acceptable corrosion of 316L SS. Despite preferential dissolution of Cr and scale degradation/spallation with increased oxide content in solar salt, the corrosion layer in all cases comprised of sodium ferrite, and Cr-rich Cr-Fe mixed oxides with the Ni enrichment at the scale-metal interface. Competing processes between oxide scale growth, degradation and dissolution or even spallation has been discussed with an emphasis of Na2O addition to solar salt. KW - Molten salt corrosion KW - Solar salt KW - Thermal energy storage KW - Stainless steel KW - Concentrating solar power PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-610819 DO - https://doi.org/10.1016/j.solmat.2024.113176 VL - 278 SP - 1 EP - 13 PB - Elsevier B.V. AN - OPUS4-61081 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -