TY - JOUR A1 - Pfennig, Anja A1 - Wolf, M. A1 - Kranzmann, Axel T1 - Corrosion and Corrosion Fatigue of Steels in Downhole CCS Environment—A Summary N2 - Static immersion tests of potential injection pipe steels 42CrMo4, X20Cr13, X46Cr13, X35CrMo4, and X5CrNiCuNb16-4 at T = 60°C and ambient pressure, as well as p = 100 bar were performed for 700–8000 h in a CO2-saturated synthetic aquifer environment similar to CCS sites in the Northern German Basin (NGB). Corrosion rates at 100 bar are generally lower than at ambient pressure. The main corrosion products are FeCO3 and FeOOH with surface and local corrosion phenomena directly related to the alloy composition and microstructure. The appropriate heat treatment enhances corrosion resistance. The lifetime reduction of X46Cr13, X5CrNiCuNb16-4, and duplex stainless steel X2CrNiMoN22-5-3 in a CCS environment is demonstrated in the in situ corrosion fatigue CF experiments (axial push-pull and rotation bending load, 60°C , brine: Stuttgart Aquifer and NGB, flowing CO2: 30 L/h, +/- applied potential). Insulating the test setup is necessary to gain reliable data. S-N plots, micrographic-, phase-, fractographic-, and surface analysis prove that the life expectancy of X2CrNiMoN22-5-3 in the axial cyclic load to failure is clearly related to the surface finish, applied stress amplitude, and stress mode. The horizontal grain attack within corrosion pit cavities, multiple fatigue cracks, and preferable deterioration of austenitic phase mainly cause fatigue failure. The CF life range increases significantly when a protective potential is applied. KW - Carbon capture and storage KW - Steel KW - High alloyed steel KW - Corrosion KW - Corrosion fatigue KW - CCS PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-523948 DO - https://doi.org/10.3390/pr9040594 VL - 9 IS - 4 SP - 594 PB - MDPI CY - Basel, Switzerland AN - OPUS4-52394 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pfennig, A. A1 - Simkin, Roman T1 - Identifying the initial corrosion fatigue failure based on dropping electrochemical potential N2 - The corrosion fatigue of duplex stainless-steel X2CrNiMoN22-5-3 can be determined by purely alternating axial cyclic load to failure using hour-glass shaped specimens. The experimental setup comprises a corrosion chamber allowing for the circulation of an aquifer electrolyte heated to 369 K simulating a carbon capture and storage as well as geothermal power plant environment. During engineering of a carbon storage site or geothermal power plant, it may be crucial to determine the failure onset of a component beforehand. Therefore, an algorithm with 93.3% reliability was established based on splitting the measured potential values into ten time series with a capacity of ten values. The failure of corrosion fatigue specimens in a geothermal environment correlates to the drop of the curves of the electrochemical potential which is measured simultaneously within the corrosion chamber. Crack initiation was, therefore, successfully derived from the electrochemical potential. KW - Corrosion fatigue KW - Surface corrosion KW - CO2 KW - Crack initiation KW - Geothermal energy production PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-629310 DO - https://doi.org/10.3390/app15010403 SN - 2076-3417 VL - 15 IS - 1 SP - 1 EP - 15 PB - MDPI CY - Basel AN - OPUS4-62931 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -