TY - CONF A1 - Waurischk, Tina T1 - Internal friction and energy dissipation during crack propagation in silicate glasses N2 - To obtain a deeper insight into the nature of energy dissipation during crack propagation, the internal friction of 13 borosilicate, aluminosilicate, soda-lime, and lead-containing glasses, for which inert crack growth data are available in the literature, was measured using dynamic mechanical thermal analysis. For asymmetrically bent glass beams, the loss tangent tanδ was determined between 0.2 and 50 Hz at temperatures between 273 K and the glass transition temperature Tg. It was found that the area under the tanδ vs. T/Tg curve correlates with the crack growth exponent, n, in the empirical v ~ KIn relation between crack growth velocity, v, and stress intensity, KI. This correlation was most distinct for T/Tg < 0.3, still clear for T/Tg < 0.5, but not found for T/Tg > 0.8. The observed results indicate that n correlates with the degree of energy dissipation of relaxation phenomena below Tg. T2 - 27th International Congress on Glass 2025 CY - Kolkata, India DA - 20.01.2025 KW - Internal friction KW - Energy dissipation KW - Crack propagation KW - Silicate glasses PY - 2025 AN - OPUS4-63819 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Waurischk, Tina A1 - Deubener, J. A1 - Müller, Ralf T1 - Internal friction and energy dissipation during fracture in silicate glasses N2 - To obtain a deeper insight into the nature of energy dissipation during fracture, the internal friction of 13 borosilicate, aluminosilicate, soda-lime, and lead-containing glasses, for which inert crack growth data are known, was measured using dynamic mechanical thermal analysis. For asymmetrically bent glass beams, the loss tangent, tan δ, was determined between 0.2 and 50 Hz at temperatures between 273 K and the glass transition temperature, Tg. It was found that the area under the tan δ vs T·Tg−1 curve correlates with the crack growth exponent, n, in the empirical v = v0·KIn relation between crack growth velocity, v, and stress intensity, KI, which indicates that n correlates with the degree of energy dissipation of sub-Tg relaxation phenomena. KW - Glass KW - Internal friction KW - Crack growth PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-651371 DO - https://doi.org/10.1063/5.0255432 SN - 0021-9606 VL - 162 IS - 19 SP - 1 EP - 9 PB - AIP Publishing AN - OPUS4-65137 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -