TY - CONF A1 - Aristia, Gabriela A1 - Nofz, Marianne A1 - Bäßler, Ralph A1 - Sojref, Regine A1 - Le, Quynh Hoa T1 - Preliminary Study on Al2O3 Sol-Gel Coating for Corrosion Protection of Martensitic Stainless Steel in Artificial Geothermal Water N2 - Al2O3 coatings are often used as protective layers on steels against electrochemical and high-temperature corrosion because they are chemically inert and stable at elevated temperatures. This study presents preliminary work on the possibilities of using Al2O3 sol-gel coatings for corrosion protection of martensitic stainless steels in geothermal environments. Al2O3 sol-gel coatings were applied on UNS S42000, which is known to be susceptible to uniform and localized corrosion. The coated steel specimens were then tested in two types of artificial geothermal water, which simulate the geothermal fluids found in Sibayak (SBY), Indonesia, and North German Basin (NGB), Germany, respectively. SBY has pH 4 and 1.5 g/L of chloride ions, whereas NGB has a pH of 6 and 166 g/L of chloride ions. All experiments were carried out in autoclaves at 150 °C and 1 MPa under the deaerated condition. Evaluations were performed by investigating the surface profiles of both uncoated and coated steels before and after the corrosion test using a Laser Scanning Microscope (LSM) and Scanning Electron Microscope (SEM). Finally, Electrochemical Impedance Spectroscopy (EIS) was performed to compare the corrosion resistance of Al2O3 coated steels in SBY and NGB solutions. It was observed from the corrosion test that Al2O3 coatings are more suitable for use in the geothermal water with a higher pH. T2 - AMPP Annual International Corrosion Conference 2021 CY - Online Meeting DA - 19.04.2021 KW - Protective coating KW - Sol-gel coating KW - Geothermal KW - Martensitic steel KW - Corrosion PY - 2021 SP - 16777-01 EP - 16777-12 CY - Houston AN - OPUS4-52501 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heuser, Lina T1 - Silver diffusion in low-melting alkali zinc borate model glasses studied by means of SNMS, TEM and XAS N2 - In many late-breaking research fields as in photovoltaics, microelectronics, nuclear waste glasses or at least mirror glasses silver diffusion in glasses is relevant to the issues of high-level functionality and recycling. The present study is focused on silver diffusion in innovative, low-melting alkali zinc borate glasses (X2O-ZnO-B2O3, X = Li, Na, K, Rb) potentially usable for silver metallization-pastes in solar cells. The glasses were coated with a thin metallic silver layer and heat treatments in air and nitrogen close to Tg at 470 °C for 2 h were performed. After heat treatment under air and nitrogen atmospheres the coating thickness, measured by a white light interferometer, was about 1.8 µm thick. Silver depth profiles determined by means of secondary neutral mass spectrometry (SNMS) indicate the fastest silver diffusion to a depth of 3.5 µm for Li2O-ZnO-B2O3 (LZB) glass. Nevertheless, the influence of the different alkali ions on the silver diffusion is small. The oxygen availability determines the silver diffusion into the glasses. The oxygen promotes the oxidation of the silver layer enabling Ag+ to diffuse into the glass and to precipitate as Ag0. Both species were detected by x-ray absorption spectroscopy (XAS). The precipitated metallic silver particles in Na2O-ZnO-B2O3 (NZB) glass have a mean size of 5.9 nm ± 1.2 nm diameter, which was determined using transmission electron microscopy (TEM). Phase separation in zinc-rich and zinc-poor phases with a mean diameter of 75 nm ± 20 nm occurred in NZB glass after heat treatment. Ion diffusion of the glasses into the silver layer was suggested by EDX-line scans. T2 - 94. Glastechnische Tagung CY - Online meeting DA - 10.05.2021 KW - Silver diffusion KW - Alkali zinc borate glass KW - Metallic silver precipitates KW - Phase separation PY - 2021 AN - OPUS4-52861 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Chahal, Shweta T1 - Sustainable Synthesis of Na+ and Bi3+ - doped Cs₂AgInCl₆ Double Perovskites for Efficient White-Light Emission N2 - Double halide perovskites have emerged as promising, less-toxic alternatives to lead-based perovskites for diverse photochemical applications. Among them, Cs₂AgInCl₆ has attracted significant attention, particularly when doped with various elements, which induce self-trapped exciton (STE) states within the bandgap, resulting in efficient white-light emission and a remarkable enhancement of photoluminescence quantum yield (PL QY). While several solid-state and solution-based methods have been employed for the synthesis of double halide perovskites, many rely on toxic solvents and complex procedures, hindering scalability. In this study, we present two environmentally friendly synthesis approaches for the preparation of Cs₂AgInCl₆ doped with monovalent (Na⁺) and trivalent (Bi³⁺) cations: 1. Green solution-based method: Utilizes mild reagents and entirely replaces harsh chemicals, enabling synthesis at ambient conditions. 2. Mechanochemical approach: Employs high-energy ball milling for 62 minutes at room temperature to obtain the desired crystalline phase. These green methodologies provide sustainable and scalable alternatives to conventional routes, minimizing the environmental footprint. We systematically compare the structural and optical properties of the doped perovskites synthesized via both approaches. The resulting materials exhibit strong UV absorption, broadband white-light emission, high PL QY (up to 85%, Fig. 1), long PL lifetimes, and good thermal and environmental stability (up to 300 °C in air). These results highlight the potential of doped Cs₂AgInCl₆ double perovskites as an eco-friendly material with possible photonic applications as in white-light devices. T2 - eMRS Fall Meeting 2025 CY - Warsaw, Poland DA - 15.09.2025 KW - Fluorescence KW - Advanced material KW - Perovskite KW - Synthesis KW - Characterization KW - Fluorescence quantum yield KW - Absolute KW - Integrating sphere spectroscopy KW - Sustainable synthesis KW - Lifetime KW - Photophysics PY - 2025 AN - OPUS4-64185 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Abel, Andreas A1 - Rosalie, Julian A1 - Reinsch, Stefan A1 - Zapala, Pawel A1 - Michels, Heiner A1 - Skrotzki, Birgit T1 - Influence of Mo and B additions in intermetallic near-Fe3Al alloys on microstructure and mechanical properties N2 - Iron aluminides, already reported in the late 19th century, did not cease to attract the interest of scientists and engineers ever since. Besides good oxidation resistance, low density and resource availability, potentials for hightemperature strengths that compete with high-alloy steels were unlocked by low alloy contents. Still, research on alloy design continues, as alloying usually comes at the price of brittleness in low-temperature regimes. A potential candidate is the quinary Fe–Al–Mo–Ti–B system which is strengthened by solid solution and eutectic borides. It was shown to have good strength and outstanding creep resistance under compressive loading up to elevated temperatures. Although the individual effect of alloy additions is well understood in iron aluminides, little is known about the combined effects of alloying concentrations on microstructure, phase stability and mechanical properties. Therefore a systematic study of two Ti-doped near-Fe3Al alloys with varying contents of Mo (2–4 at.%) and B (0.5–1 at.%) was conducted. In total eight different alloys were fabricated by investment casting into ceramic shell molds. Alloys were characterized and compared by grain size, phase transitions, microstructure evolution as well as elemental compositions and volume fractions of phases. For mechanical characterization, macrohardness and microhardness tests as well as tensile tests at ambient and high tempera tures were conducted. Independent of alloy additions, alloys with 24–25 at.% Al exhibit superior proof strength due to a higher matrix hardness. Decreasing B content generally decreases strength by lower secondary phase fractions which contribute via particle hardening. Reducing Mo content decreases both the solute concentration in the matrix and secondary phase fractions. Surprisingly, strength is similar or even superior to alloys with higher Mo content. Strength relations are discussed with a focus on solid-solution hardening theory and other competing strengthening mechanisms. KW - Materials Chemistry KW - Metals and Alloys KW - Mechanical Engineering KW - Mechanics of Materials KW - General Chemistry PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-585284 DO - https://doi.org/10.1016/j.intermet.2023.108074 VL - 163 SP - 1 EP - 11 PB - Elsevier Ltd. AN - OPUS4-58528 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Chahal, Shweta A1 - Xiao, Boyu A1 - Grant, Jessica A1 - Furniss, David A1 - Farries, Mark A1 - Phang, Sendy A1 - Neate, Nigel A1 - Robertson, Lorelei A1 - Roe, Martin A1 - Barney, Emma A1 - Seddon, Angela B. T1 - Ce3+-doped chalcogenide glass fibre for laser beyond 4 microns wavelength: Glass material-integrity N2 - The 4-μm wavelength barrier encountered for mid-infrared fibre lasing based on heavy metal fluoride glasses has been overcome. We reported, in 2021, the first continuous wave, mid-infrared fibre laser operating beyond 4 μm at room temperature in a fibre with a Ce3+-doped selenide-chalcogenide core. Defects, such as crystallites in the core glass, could cause unwanted light-scattering, diminishing fibre laser efficiency. It is important to identify such optical loss mechanisms and eradicate them. Here, we report on investigating the material nano-structure of a chalcogenide-glass lasing fibre which exhibits 7 mW laser power output; the fibre has a Ce3+-doped core (8.5 μm diameter), concentrically surrounded by an inner- and outer-cladding, where both cladding-glasses are nominally the same composition. High resolution transmission electron microscopy and electron diffraction show that the core, inner-cladding and outer-cladding of the lasing fibre are internally nano-crystallite-free and amorphous. However, the external outer surface of the last 10 m of fibre drawn, of the total 100 m, contains monoclinic GeSe2 crystallites adjacent to discrete, small (<0.5 mm) wrinkled defects. The final length of fibre is drawn from the final part of the glass fibreoptic preform. The glass preform has as its outermost component an extruded chalcogenide glass tube. It is the last part of the tube which spends the longest time at high temperature inside the extruder during tube manufacture, encouraging heterogeneous nucleation at the tube outer-surface in contact with the extruder. These heterogeneous nuclei subsequently nucleate crystal growth during fibre-drawing in the outermost fibre surface. KW - Optical glass KW - Photonics PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-653371 DO - https://doi.org/10.1016/j.optmat.2025.117219 SN - 0925-3467 VL - 166 SP - 1 EP - 14 PB - Elsevier CY - Amsterdam AN - OPUS4-65337 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Waurischk, Tina A1 - Deubener, J. A1 - Müller, Ralf T1 - Internal friction and energy dissipation during fracture in silicate glasses N2 - To obtain a deeper insight into the nature of energy dissipation during fracture, the internal friction of 13 borosilicate, aluminosilicate, soda-lime, and lead-containing glasses, for which inert crack growth data are known, was measured using dynamic mechanical thermal analysis. For asymmetrically bent glass beams, the loss tangent, tan δ, was determined between 0.2 and 50 Hz at temperatures between 273 K and the glass transition temperature, Tg. It was found that the area under the tan δ vs T·Tg−1 curve correlates with the crack growth exponent, n, in the empirical v = v0·KIn relation between crack growth velocity, v, and stress intensity, KI, which indicates that n correlates with the degree of energy dissipation of sub-Tg relaxation phenomena. KW - Glass KW - Internal friction KW - Crack growth PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-651371 DO - https://doi.org/10.1063/5.0255432 SN - 0021-9606 VL - 162 IS - 19 SP - 1 EP - 9 PB - AIP Publishing AN - OPUS4-65137 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pan, Z. A1 - Waurischk, Tina A1 - Duval, A. A1 - Müller, Ralf A1 - Deubener, J. A1 - Krishnan, N. M. A. A1 - Wondraczek, K. A1 - Wondraczek, L. T1 - Precise Real‐Time Measurement of Liquid Viscosity Using Digital Video Data N2 - Quantitative knowledge of liquid viscosity is of fundamental importance in many areas of materials synthesis and processing. However, the determination of viscosity often relies on specialized experimental equipment, offline experimentation, or invasive procedures, in particular when required in extreme conditions such as at high temperature, high pressure, and in confined or corrosive environments. Here, this study proposes and validates a fast and simple method that mimics the intuitive perception of liquid flow within a quantitative framework. For this, this study employs digital video observation to derive quantitative values of the shear viscosity of liquids, with high precision and rapid acquisition rates. The technique involves capturing liquid dynamics after minor mechanical stimulation. Processed imaging data are indexed by similarity and referenced to a digital database generated with a finite element model, from which values of viscosity are obtained in line. The approach is tested on water at room temperature and on a high‐temperature glass melt. Covering a viscosity range of four orders of magnitude, both yield convincing agreement with tabulated reference data at low computational cost. KW - Glass KW - Liquid Viscosity KW - Digital Video Data KW - Finite Element Method PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-651363 DO - https://doi.org/10.1002/aisy.202500297 SN - 2640-4567 VL - 7 IS - 12 SP - 1 EP - 12 PB - Wiley VHC-Verlag AN - OPUS4-65136 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Santos Baltieri, Ricardo T1 - Luminescence Thermometry in Pure TeO₂ Glasses Doped with Er3+/Yb3+ and Eu3+: Remote Sensing Capability Across the Biological Temperature Range N2 - The development of non-contact and remote temperature sensors based on rare-earth (RE3+)-doped glasses is crucial for emerging applications in biomedical diagnostics and microscale thermal monitoring. In this study, we explore the fundamental thermometric properties of pure tellurite (TeO2) glasses doped with either Er3+/Yb3+ or Eu3+ ions in a wide range of temperature. The Er3+/Yb3+-co-doped system was analyzed through upconversion emission thermometry, particularly involving thermally coupled levels 2H11/2 and 4S3/2. The intensity ratio between these levels exhibits a clear temperature dependence from 100 K to 530 K, with an inversion near 160 K and optimal sensitivity above 250 K. At 300 K, the relative sensitivity (SR) reached 1.1% K−1, and the absolute sensitivity peaked at 6.5 × 10−3 K−1 at 460 K. Figure on the left is the Er3+ upconversion luminescence dependency on temperature, in the center is the excitation spectra of Eu3+ with temperature, and on the right is the comparison between calculated and measured temperature for Eu3+ samples. In parallel, the excitation spectra of Eu3+-doped TeO2 glasses were acquired from 100 K to 520 K, revealing three thermally responsive spectral regions. These transitions exhibited temperature-dependent intensity inversions, enabling the use of excitation-based thermometry. Notably, one of the regions provided the most accurate temperature predictions, with a relative sensitivity of 0.5% K−1 at 300 K. Both systems benefit from the high optical transparency, chemical stability, and low phonon energy of pure TeO2 glass, making them ideal candidates for remote sensing platforms, such as fiber-optic tips or implantable probes. While the Er3+/Yb3+ system provides robust upconversion emission for conventional thermometry, the Eu3+ system introduces an innovative excitation-based strategy, broadening the applicability of RE3+-doped tellurite glasses for optical thermometry. Acknowledgements This work was supported by the São Paulo Research Foundation (FAPESP – N. 2020/11038-2, 2023/05994-6, 2024/04675-7) and National Council for Scientific and Technological Development (CNPq - 304718/2023-8). T2 - Shift 2025 Conference CY - Tenerife, Spain DA - 13.10.2025 KW - Lanthanide KW - Optical thermometry KW - Energy conversion PY - 2025 AN - OPUS4-65195 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Meira, Maria Fernanda Cavalcante A1 - Fernandes, Gabriela Leal Peres A1 - de Camargo, Andréa Simone Stucchi A1 - Ravaro, Leandro Piaggi A1 - Arai, Marylyn Setsuko A1 - Navarro, Maria Fidela de Lima A1 - Brighenti, Fernanda Lourenção A1 - Oliveira, Analú Barros de A1 - Danelon, Marcelle ED - Stucchi de Camargo, Andrea T1 - Modification of restorative glass ionomer cement with zinc oxide nanoparticles and calcium glycerophosphate microparticles: in vitro assessment of mechanical properties and antimicrobial activity N2 - Abstract The incorporation of bioactive agents into resin-modified glass ionomer cement (RMGIC) is a promising strategy to improve its mechanical strength and biofilm control, especially for patients with active dental caries. Objective This study aimed to evaluate the effects of incorporating ZnONPs and CaGP into RMGIC on its mechanical and microbiological properties. Design Six groups were tested: 1) RMGIC (without CaGP/ZnONPs); 2) RMGIC-1.0%ZnONPs; 3) RMGIC-2.0%ZnONPs; 4) RMGIC-3.0%CaGP; 5) RMGIC-3.0%CaGP-1.0%ZnONPs; and 6) RMGIC-3.0%CaGP-2.0%ZnONPs. The compressive strength (CS), diametral tensile strength (DTS), and surface hardness (SH) were evaluated after 24 hours and 7 days. Antimicrobial and antibiofilm activity were evaluated using agar diffusion and biofilm metabolic activity (XTT) assays. Results After 24 hours, all the groups showed similar DTS values (p0.05), except for RMGIC-3.0%CaGP-1.0%ZnONPs, which showed the highest DTS value (p<0.05). Comparing 24 hours and 7 days, the DTS values of RMGIC-3.0%CaGP-2.0%ZnONPs, RMGIC-3.0%CaGP, and RMGIC-3.0%CaGP-2.0%ZnONPs were similar (p=0.360). After 24 hours, the RMGIC group showed the CS highest value, followed by RMGIC-2.0%ZnONPs (p < 0.05). After 7 days, the RMGIC-3.0%CaGP-1.0%ZnONPs group exhibited the highest CS value, approximately 15% higher than RMGIC (p<0.05). The RMGIC-1.0%ZnONPs group exhibited significantly higher SH at 24 hours (p=0.621). At 7 days, the highest SH value was observed for the RMGIC-3.0%CaGP-1.0%ZnONPs group (p<0.05). Regarding antimicrobial and antibiofilm activity, including results from biofilm metabolism assays, the RMGIC-3.0%CaGP-1.0%ZnONPs group demonstrated the most effective antimicrobial and inhibitory effects (p<0.05). Conclusion This study demonstrated that adding ZnONPs and CaGP to RMGIC enhanced its mechanical and antimicrobial and antibiofilm properties, suggesting enhanced mechanical performance and improved protection against cariogenic biofilms—critical factors for successful restorative treatments. Therefore, the addition of ZnONPs and CaGP is a promising strategy to develop advanced restorative materials that improve clinical outcomes, especially for patients with active dental caries. KW - Resin-modified glass ionomer cement KW - Phosphate KW - Zinc oxide nanoparticles KW - Biofilm KW - Mechanical properties PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-652799 DO - https://doi.org/10.1590/1678-7757-2025-0356 SN - 1678-7765 VL - 33 SP - 1 EP - 14 PB - FapUNIFESP (SciELO) AN - OPUS4-65279 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Arai, Marylyn S. A1 - Brambilla, Gabriel V. A1 - Corrêa, Bruna Carolina A1 - Merízio, Leonnam G. A1 - Inada, Natalia M. A1 - de Camargo, Andrea S. S. T1 - A Dual-Mode “Turn-On” Ratiometric Luminescent Sensor Based on Upconverting Nanoparticles for Detection and Differentiation of Gram-Positive and Gram-Negative Bacteria N2 - Infectious bacterial diseases, intensified by antibiotic resistance, cause millions of deaths annually and pose risks beyond human health, including water and food contamination. Current diagnostics are often slow, require complex equipment, and lack specificity, highlighting the need for rapid and reliable detection methods. To address this, we developed a luminescent sensor based on NaYF4 upconverting nanoparticles (UCNPs) doped with Er3+ or Tm3+, coated with COOH-PEG4-COOH, and functionalized with vancomycin (Van) or polymyxin-B (Poly) to selectively target Gram-positive and Gram-negative bacteria, respectively. Gold nanoparticles (AuNPs) served as quenchers, enabling a ratiometric “turn-on” mechanism: upon bacterial binding, the UCNP emission, initially quenched by AuNPs, was partially restored. This allowed Differentiation through changes in the green/red (G/R) ratio for Er-UCNP@PEG4-Van and the blue/red (B/R) ratio for Tm-UCNP@PEG4-Poly. The sensor distinguished between Gram-positive and Gram-negative bacteria over a wide concentration range (0.05 to 5 × 105 CFU/mL) and showed high correlation with actual bacterial counts (r = 0.99 for S. aureus, r = 0.91 for E. coli). This platform is a potential fast, selective, and reliable tool for bacterial detection in clinical and environmental settings. KW - Lminescent sensor KW - Upconverting nanoparticles KW - Gram-positive and Gram-negative bacteria KW - Ratiometric luminescent sensors PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-652785 DO - https://doi.org/10.1021/acsomega.5c07006 SN - 2470-1343 VL - 10 IS - 39 SP - 46040 EP - 46050 PB - American Chemical Society (ACS) AN - OPUS4-65278 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -