TY - JOUR A1 - Feldmann, Titus A1 - Fedelich, Bernard A1 - Epishin, A. T1 - Simulation of Hot Isostatic Pressing in a Single-Crystal Ni Base Superalloy with the Theory of Continuously Distributed Dislocations Combined with Vacancy Diffusion N2 - Single-crystal components made of nickel base superalloys contain pores after casting and homogenization heat treatment. Hot isostatic pressing (HIP), which is carried above the γ' -solvus temperature of the alloy, is industrially applied to reduce porosity. A modeling of HIP based on continuously distributed dislocations is developed in a 2D setting. Glide and climb of straight-edge dislocations, as well as vacancy diffusion, are the deformation mechanisms taken into account. Thereby, dislocation glide is controlled by dragging a cloud of large atoms, and climb is controlled by vacancy diffusion. Relying on previous investigations of the creep behavior at HIP temperatures, it is assumed that new dislocations are nucleated at low-angle boundaries (LAB) and move through subgrains until they either reach the opposite LABs or react with other dislocations and annihilate. Vacancies are created at the pore surface and diffuse through the alloy until they are either consumed by climbing dislocations or disappear at the LABs. The field equations are solved by finite elements. It is shown that pore shrinking is mostly controlled by vacancy diffusion as the shear stresses at the LABs are too low to nucleate a sufficient amount of dislocations. KW - Nickel-base superalloys KW - HIP KW - Dislocation KW - Creep KW - Model PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-542309 DO - https://doi.org/10.1002/adem.202101341 VL - 2022 PB - Wiley AN - OPUS4-54230 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Fedelich, Bernard ED - Cailletaud, G. ED - Cormier, J. ED - Eggeler, G. ED - Maurel, V. ED - Nazé, L. T1 - Crystal orientation and elastic properties N2 - The elastic constants are the most basic mechanical properties of a material and are needed for any structural analysis of a component. For example, they have a major influence on the eigenfrequencies of vibrating parts. Single crystals of Ni-base superalloys are strongly anisotropic, which means that the observed properties are orientation dependent. Tensor algebra is then required to mathematically formulate the elastic properties and their relations to the crystal orientation. Hence, this chapter first summarizes some basic definitions and calculation rules for Rotation matrices, including the definition of the Euler angles, which are most commonly used to define the relative orientations of the crystal and the component. Parts of this chapter closely follow the lines of the excellent exposition of the topic by Olschewski. KW - Nickel-base superalloys KW - Elasticity PY - 2022 SN - 978-0-12-819357-0 SP - 41 EP - 67 PB - Elsevier Inc. AN - OPUS4-53435 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Fedelich, Bernard ED - Cailletaud, G. ED - Cormier, J. ED - Eggeler, G. ED - Maurel, V. ED - Nazé, L. T1 - Crystal plasticity models: dislocation based N2 - The large number of TEM investigations and the regular microstructure of single-crystal nickel-base superalloys has boosted the development of a number of physically motivated constitutive laws. In contrast to the more phenomenological models discussed in the next chapter, these models use dislocation densities as internal variables. Obvious advantages are that the computed densities can be compared to TEM observations and the Deformation mechanisms can be easier translated into mathematical equations. KW - Nickel-base superalloys KW - Creep KW - Plasticity PY - 2022 SN - 978-0-12-819357-0 SP - 401 EP - 427 PB - Elsevier Inc. ET - 1 AN - OPUS4-53436 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fedelich, Bernard A1 - Butz, Adam A1 - Rehmer, Birgit A1 - Mäde, Lucas A1 - Vöse, Markus T1 - Experimental and analytical investigation of Low Cycle Fatigue Damage at notches in a polycrystalline Nickel base superalloy N2 - Turbine blades often contain cylindric holes used to generate an air film that protects the blade alloy from the hot gases. These cooling holes of diameter around one mm are drilled by laser through the thickness of the blades. Unfortunately, the resulting stress concentration and the drilling-induced damage are known to favor crack initiation from the holes. It is thus necessary to assess the impact of these cooling holes on the structural integrity of the blades. Since cracks initiate very readily, the fatigue life of the components is mainly controlled by the propagation of the cracks in the stress gradient induced by the holes. For this purpose, displacement controlled high-temperature LCF (Low-Cycle-Fatigue) tests were performed with center hole specimens of a coarse-grained Nickel base Superalloy. The tests were stopped after a defined load drop. In addition, crack propagation tests with Double Edge Notch specimens were performed. Moreover, specimens with different hole surface finishes were investigated, which showed a detrimental effect of the hole surface roughness. In parallel, an evaluation of the LCF tests based on a fracture mechanics-based model (Madia et al., Eng. Fract. Mech., 2018) has been applied. Thereby, the specimen life is controlled by the crack propagation time until failure. Crack growth is controlled by a modified NASGRO equation accounting for large-scale yielding and a progressive build-up of crack closure. The initial crack size has been derived from the measurements of defects around the borehole. A reasonable agreement between predicted and measured lifetimes is observed if one keeps in mind the large uncertainty regarding the effective shape of the cracks. T2 - 23rd European Conference on Fracture CY - Funchal, Madeira, Portugal DA - 27.06.2022 KW - Nickel-base superalloys KW - Notches KW - LCF PY - 2022 AN - OPUS4-55338 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fedelich, Bernard A1 - Butz, Adam A1 - Rehmer, Birgit A1 - Mäde, L. A1 - Schmitz, S. A1 - Vöse, M. T1 - Experimental and analytical investigation of high temperature fatigue crack growth at notches in a polycrystalline Nickel base superalloy N2 - The scatter of fatigue crack growth data can become significant for coarse grained materials. By using a probabilistic description of crack propagation as the foundation of a lifetime prediction model, lifetime scatter of laboratory specimens can be reproduced. However, the lifetime of real components is subjected to additional scattering factors such as surface condition or uncertainty regarding direction and shape of emerging cracks. These factors need to be addressed in order to exploit the advantages of probabilistic description, i.e. the reduction of unnecessary conservatisms. High temperature LCF (Low-Cycle-Fatigue) tests were performed with center hole specimens of a coarse-grained Nickel base Superalloy. In addition, crack propagation tests with Double Edge Notch specimens were performed. A procedure to detect the shape of the starting crack that combines the potential drop method and induction thermography was developed. The geometry and the number of notches were varied. Moreover, specimen with different hole surface finishes were investigated, which showed a detrimental effect of the roughness of the hole surface. The results have been compared to predictions of a probabilistic tool for the estimation of lcf lifetime that has been calibrated beforehand on laboratory specimens with and without notches. In parallel, a fracture mechanics-based lifetime model was developed, which includes the initial crack size as a critical parameter. Thereby, the influence of the large grain size (>1mm), and the shape of the starting crack at the notch were considered. Acknowledgements The investigations are conducted as part of the joint research program COOREFLEX-Turbo in the frame of AG Turbo. The work is supported by Siemens AG and the Bundesministerium für Wirtschaft und Technologie (BMWi) as per resolution of the German Federal Parliament under grant number 03ET7071E. T2 - Low Cycle Fatigue 9 CY - Berlin, Germany DA - 21.06.2022 KW - Nickel-base superalloys KW - Notches KW - LCF PY - 2022 AN - OPUS4-55335 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -